GROUTING MATERIALS AND THEIR USE

Abstract: A grouting material which is self-dispersing when brought into contact with a volume of water containing liquor or slurry and is settable to a solid mass after such dispersion, the material comprising a composition, composition X, which comprises a blend of: Component (A): a cementive constituent forming from 10 per cent to 95 per cent by weight of the composition; component (B): a disintegrating mechanism promoting constituent forming from 2 per cent to 75 per cent by weight of the composition; component (C): an optimal swelling constituent which forms from 0 per cent to 50 per cent by weight of the composition; component (D): a binder constituent which forms from 0.1 per cent to 10 per cent by weight of the composition; the percentages of components A, B, C and D adding to 100 per cent.

Description: GROUTING MATERIALS AND THEIR USE The present invention relates to grouting materials and methods for their use. Grouting or cementing materials are commonly employed to form solid rigid masses by addition of powders of the material to water. Such materials may be employed not only for the production of concrete for widely used building structures but also in specialised applications such as the encapsulation in containers of hazardous substances such as radioactive wastes. It is usual for the grouting material to be mixed as soon as it is added to water. Such mixing can be time consuming and costly and in specialised applications requires significant quality control and care. For example, where mixing for encapsulation of radioactive waste liquors and slurries is carried out it has in some cases been necessary to mix the cementing material with the waste liquor or slurry. Decontamination of the mixing equipment is required in such cases and this is hazardous as well as time consuming and costly. The present invention provides a novel grouting material, and a method of using the same, which allows addition of the material to a water-containing liquor or slurry to form a solid mass therein, eg to encapsulate the same, without the need for the conventional mixing step. According to the present invention in a first aspect there is provided a grouting material which is self- dispersing when brought into contact with a volume of water containing liquor or slurry and is settable to a solid mass after such dispersion, the material comprising a composition, Composition X, which comprises a blend of: Component A: a cementive constituent forming from 10 per cent to 95 per cent by weight of the composition; Component B: a disintegrating mechanism promoting constituent forming from 2 per cent to 75 per cent by weight of the composition; Component C: an optional swelling constituent which forms from 0 per cent to 50 per cent by weight of the composition; Component D: a binder constituent which forms from 0.1 per cent to 10 per cent by weight of the composition. The percentages of components A, B, C and D add to 100 per cent. Desirably, Components A, B and C each comprise powders which preferably have mean particle diameters less than 25 micrometers, especially less than 10 micrometers. The material comprising Composition X may incorporate, as well as composition X, other optional additives such as hardeners, inert fillers, strength-inducing fibres or whiskers and bio-active materials. Desirably, the material is in the form of granules or pellets having a mean diameter or length greater than 0.5mm, eg in the range 1mm to 25mm. Such pellets may be in the form of spheres, spheroids, cubes, cuboids, cylinders or other suitable shapes. The purpose of using the material in pellet form is to provide large voids between pellets to increase volume loadings in use when added to water- containing liquor or slurry. According to the present invention in a second aspect there is provided a method of forming a mass of solid in a volume of water-containing liquor or slurry which comprises the steps of adding pellets of the aforementioned material of Composition X to the liquor or slurry in such quantity that the material may disperse throughout the volume or a substantial layer thereof, allowing the material to become dispersed in the said volume and allowing the material to set to form a mass of solid. The liquor or slurry may contain hazardous substances, eg radioactive waste material, and may be contained in a suitable container, eg a stainless steel drum. The solid mass formed by the said method may comprise an encapsulating layer or body which suitably seals the contents of the container. The present invention unexpectedly and beneficially provides a material and a method of using the material which may be used to encapsulate liquors and slurries, especially containing hazardous substances, in containers without the need for expensive and costly mixing of the encapsulant into the slurry or to form a separate encapsulant slurry as is conventionally practised. Compositions containing Components B, C and D as defined above for use with cements are known in the prior art from US 3579366. However, the materials comprising such compositions are to be used as additives with conventional cement powders to reduce shrinkage when the cement sets. Such compositions are added to the cement powder and mixing of the cement with water in the conventional way is still required. Such prior art compositions would be unsuitable to add to cement powder to be used to encapsulate waste liquors without mixing as described herein. This is because the disintegration reaction would already have occurred by the time the waste liquor is added to the cement matrix. In Composition X, Component A may comprise a suitable known inorganic cementitious material. Such materials generally comprise basic compounds such as oxides, aluminates and silicates of metals such as calcium, magnesium, lead and vanadium. Portland cement, gypsum, high alumina cement or a mixture of these may for example be suitable. Component A is preferably uniformly distributed throughout pellets of Composition X in sufficient quantity to give suitable cementing action when the constituent comes into contact with water. Component B is an agent which will produce an effect to aid dispersion of solids throughout a liquid medium to facilitate the required reaction between the two. It may comprise one or more salts highly soluble in water eg calcium nitrate and/or sodium carbonate. Component B may alternatively comprise as a dispersing agent one of the gas liberating materials known in the prior art, the material thereby promoting dispersion of the material of Composition X by gas liberation during use. For example, as in USP 3579366 the dispersing agent may comprise at least one compound decomposable into at least one gaseous decomposition product at the elevated temperature produced by the heat of reaction when Composition X is in use. Examples of suitable compounds of this type include ammonium carbonate, ammonium bicarbonate and urea. These compounds have the advantage of decomposing entirely into gaseous products, so that no residue is left within the granule composition. These materials may be added to the admixture at any time prior to granulation or pelletization. In accordance with another mechanism the dispersing agent comprising Component B may take the form of a mixture of compounds, one selected from the group consisting of the carbonate or bicarbonate salts, and the other from the group consisting of mild acids such as citric and tartaric acids. Since mixtures of these compounds begin to react almost immediately, they should be added just prior to granulation or pelletization, so that most of the decomposition into gases will take place during the heating step caused by the heat of reaction obtained during use. Another possible mixture for use as Component B is a finely divided metal, eg aluminium particles plus a mild acid such as citric or tartaric acid. Such a mixture will release hydrogen during use. Component C which may comprise from 5 per cent to 50 per cent by weight may comprise one or more clays or chemicals such as gum arabic. The purpose of optional Component C is to provide a swelling agent which can absorb water and reduce shrinkage in a controlled manner to produce an acceptable product without cracks thereby allowing greater volumes of liquor or slurry to be satisfactorily encapsulated. Component D may comprise water and/or one or more water soluble organic liquids, for example one or more of the binders known in the prior art such as compounds which are readily soluble in water and do not react with the other ingredients. Examples of such compounds include stearic acid, cellulose ethers, such as methyl cellulose, ethyl cellulose and carboxy methyl cellulose, polymers and co-polymers of ethylene oxide, carboxy vinyl polymers, polyethylene glycols and polyvinyl alcohols. In the formation of pellets of materials comprising Composition X, the various component materials, Components A to D plus other optional ingredients, are intermixed or blended together in a blender or mill. Standard granulators or pelletising equipment or plant can be used to manufacture the pellet or granule. After pelleting or granulating, the pellets or granules are treated in such a manner such as by heating to produce the desired properties. Correct proportioning, particle size range of constituents and binding energy will produce a pellet or granule with:- (a) sufficient strength to hold material components together during storage prior to use; (b) a disintegrating mechanism capable of dispersing the components when in contact with liquor when in use; (c) a setting and hardening characteristic after dispersion or disintegration in the liquor. In use, granules or pellets of the material of Composition X may be added by a suitable dispenser to a waste liquor or slurry containing hazardous material held in a suitable container, eg a stainless steel drum. Alternatively, liquor or slurry may be added to the granules or pellets held in a container. After the addition in either case the container is left for a suitable period of time, eg 24 to 48 hours, but possibly longer, eg up to 7 days, to allow the constituents of the material of Composition X to be dispersed through the liquor or slurry and, by reacting with the water thereof, to set to form a rigidly encapsulated mass. On setting, the encapsulating solid will retain the hazardous material in the container in a manner that will prevent migration or leaching of such material during subsequent transport, disposal or storage of the encapsulated container. Embodiments of the present invention will now be described by way of example. Example 1 Pellets are made by blending together the following ingredients in the stated percentages followed by pelletising in the manner described above. 20% by weight Portland cement 70% by weight sodium carbonate 10% by weight water (added intermittently) The pellets produced are heat treated in an oven (at a temperature of up to 250C depending on the precise formulation and desired properties) immediately after manufacture and subsequently stored in a manner to avoid deterioration by moisture or carbon dioxide from the air, eg under dry conditions in a silo or in bags. Example 2 Pellets are made in the manner described above by blending together the following ingredients in the following stated percentages followed by pelletising in the manner described above: 90% by weight Portland cement 2.5% by weight citric acid 2.5% by weight sodium carbonate 0.5% by weight binder 4.5% by weight expansion additive (swelling agent) The pellets after manufacture are heat treated immediately in an oven and stored in a manner to avoid deterioration by moisture or carbon dioxide from the air. 30897

Claims: CLAIMS 1. A grouting material which is self-dispersing when brought into contact with a volume of water-containing liquor or slurry and is settable to a solid mass after such dispersion, the material comprising a composition, Composition X, which comprises a blend of: Component A: a cementive constituent forming from 10 per cent to 95 per cent by weight of the composition; Component B: a disintegrating mechanism promoting constituent forming from 2 per cent to 75 per cent by weight of the composition; Component C: an optional swelling constituent which forms from 0 per cent to 50 per cent by weight of the composition; Component D: a binder constituent which forms from 0.1 per cent to 10 per cent by weight of the composition; the percentages of components A, B, C and D adding to 100 per cent. 2. A material as in Claim 1 and wherein Components A, B and C each comprise powders which have mean particle diameters less than 25 micrometers. 3. A material as in Claim 1 or Claim 2 and which incorporates as well as composition X, one or more other optional additives. 4. A material as in Claim 1, Claim 2 or Claim 3 and wherein the material is in the form of granules or pellets having a mean diameter or length greater than 0.5mm. 5. A method of forming a mass of solid in a volume of water-containing liquor or slurry which comprises the steps of adding pellets of the material as claimed in Claim 4 to the liquor or slurry in such quantity that the material may disperse throughout the volume or a substantial layer thereof, allowing the material to become dispersed in the said volume and allowing the material to set to form a mass of solid. 6. A method as in Claim 5 and wherein the liquor or slurry contains hazardous substances and is contained in a container. 7. A method as in Claim 6 and wherein the solid mass formed comprises an encapsulating layer or body which suitably seals the contents of the container. 8. A material as in Claim 1 and substantially the same as any of the examples of such materials described herein. 9. A method as in Claim 7 and wherein the said material employed in the method is material as claimed in Claim 8. 30897

Inventors: BROWN DAVID JOHN, HIGSON STEPHEN GEOFFREY, BROWN, DAVID, JOHN, HIGSON, STEPHEN, GEOFFREY
Applicants: BRITISH NUCLEAR FUELS PLC, BROWN DAVID JOHN, HIGSON STEPHEN GEOFFREY, BROWN, DAVID, JOHN, HIGSON, STEPHEN, GEOFFREY
Application year: 1994
Main classification: C04B40
IPC codes: C04B7, C04B18, C04B28, C04B40, G21F9