Method for manufacturing a color filter and a liquid crystal panel

Abstract: Provided is a color filter which comprises a substrate and a resin layer on the substrate, the resin layer containing a plurality of colored portions of different colors and non-colored portions.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method of manufacture of a color filter suitable for a liquid crystal display, which can be used in a color television, a personal computer or the like, and a method of manufacture of a liquid crystal panel equipped with the color filter. More specifically, it relates to such methods under using an ink jet recording technique. Related Background Art In recent years, there has been a tendency that the demand of liquid crystal displays, particularly color liquid crystal displays increases with the development of personal computers, particularly portable personal computers. However, for the further spread of the liquid crystal displays, it is necessary to lower their costs, and particularly with regard to the color filter which largely occupies the cost of each display, request for its cost reduction increases. In order to meet the required characteristics of the color filter and to satisfy the above-mentioned demand, various attempts have been heretofore made, but any method which can meet all of the required characteristics has not been established so far. Some methods for manufacturing the color filter will be described below. A first method which has most often been used is a dyeing method. This dyeing method comprises coating a glass substrate with an aqueous polymer material which is a material to be dyed, patterning the material into a desired shape by a photolithography process, and then immersing the thus obtained pattern in a dyeing bath to obtain a colored pattern. This operation is repeated three times to form the colored layers of Red (R), Green (G) and Blue (B). Japanese Patent Application Laid-Open No. 5-288913 has described another example of this dyeing method which comprises forming a photosensitive layer, exposing it to light through a pattern, dyeing unexposed portions, and then repeating this process to manufacture a color filter having three colors of R, G and B. A second method is a pigment dispersion method, which is now being replaced with the above-mentioned dyeing method. This pigment dispersion method comprises first forming, on a substrate, a photosensitive resin layer in which a pigment is dispersed, and then patterning the resin layer to obtain a single-colored pattern. Next, this process is repeated three times to form colored layers having three colors of R, G and B. A third method is an electrodeposition method. This method comprises first patterning transparent electrodes on a substrate, and then immersing it in an electrodeposition coating solution containing a pigment, a resin, an electrolyte and the like to electrodeposit a first color. This process is repeated three times to form colored layers of R, G and B, and in the last step, these layers are calcined. A fourth method is a printing method. This method comprises dispersing a pigment in a thermosetting resin, repeating a printing operation three times to coat with the colors of R, G and B, and then thermosetting the colored resin layers to form colored layers. In each of these methods, a protective layer is usually formed on the colored layers. A point which is common to these methods is that a similar process is required to be repeated three times to give the three colors of R, G and B, which increases the cost. In addition, these methods having many steps lead to deterioration of a yield. Moreover, in the electrodeposition method, the formable patterns are limited, and so it is difficult to apply this method to TFT by an existent technique. The printing method has a drawback that resolution properties and smoothing properties are poor, and so it is not suitable for the formation of a pattern having a fine pitch. In order to overcome these drawbacks, techniques for manufacturing a color filter by the use of an ink jet system have been developed, and these techniques have been described in Japanese Patent Application Laid-Open Nos. 59-75205, 63-235901 and 1-217320. However, a sufficiently satisfactory method has not been obtained yet. JP-A-63294503 discloses a method for manufacturing a color filter by forming a dyeable layer to be colored on a filter forming base material and sticking dyes selectively by an ink-jet method to the desired positions on the surface on the surface of this layer to be colored. The dyes then diffuse into the layers to be dyed. SUMMARY OF THE INVENTION Under such circumstances, an object of the present invention is to provide a method for manufacturing a color filter at a low cost in which necessary characteristics such'as heat resistance, solvent resistance and resolution properties given by a conventional method are kept up, an ink jet suitability is satisfied, and a process for its manufacture is shortened; and a method for manufacturing a liquid crystal panel equipped with the above-mentioned color filter. In particular, an object of the present invention is to provide a method for manufacturing a highly precise and reliable color filter for liquid crystals which can prevent color mixing and color skip when ink droplets are ejected by the use of an ink jet system to carry out the arrangement of colorants. The aforesaid objects of the present invention are achieved by the methods according to claims 1 and 7. The other, dependent claims relate to preferred embodiments. The step of curing the resin layer by light irradiation or heating mentioned in claim 1 may also be realized by a combination of light irradiation and heating. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1A to 1E show a flow sheet of a manufacturing process of a color filter of the present invention. Figs. 2A to 2E show a flow sheet of a manufacturing process of a color filter of the present invention. Fig. 3 shows a sectional view of a liquid crystal panel of the present invention. Fig. 4 shows a sectional view of another liquid crystal panel of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Figs. 3 and 4 show sectional views of TFT color liquid crystal panels incorporated with the color filter of the present invention. These embodiments are not restrictive. The color liquid crystal panel can usually be formed by combining a color filter substrate 1 with a glass substrate 14, and then enclosing a liquid crystal compound 12 therebetween. On the inside of the one substrate 14 of the liquid crystal panel, TFT (not shown) and transparent pixel electrodes 13 are formed in the state of matrices. On the inside of the glass substrate 1, a color filter 9 is arranged so that the color materials of R, G and B are placed at a position opposite to the pixel electrodes, and all over the color filter 9, a transparent common electrode 10 is formed. Black matrices are formed on the side of the color filter substrate (Fig. 3), but in the case of a BM on-array type liquid crystal panel, they are formed on the faced TFT substrate side (Fig. 4). Moreover, on the surfaces of both the substrates, orientation films 11 are formed and then subjected to a rubbing treatment to arrange liquid crystal molecules in a certain direction. Furthermore, polarizing plates 15 adhere to the outsides of the respective glass substrates 1 and 14, and the liquid crystal compound 12 is filled into the space (about 2 to 5 µm) between these glass substrates. As a back light 16, a combination of fluorescent lamps (not shown) and a scattering plate (not shown) is usually used, and display is carried out by utilizing the liquid crystal compound as a light shutter for changing the transmittance of the back light. Reference numeral 2 is a black matrix, 3 is an ink receiving layer, 6 is a protective layer, 7 is a colored portions, and 8 is non-colored portions. Examples of the halogenated triazine compounds include compounds represented by the formula (II) wherein Z is a halogen atom; Y is CZ 3 (Z is a halogen atom), phenyl, a halogenated phenyl, wherein R 7 is an alkyl group having 1 to 5 carbon atoms, and when one group has two R 7 s, they may be different from each other. The preferable examples of the halogenated triazine compounds function as a photoinitiator, and they are preferably compounds in which a trichloromethyl group is introduced into a triazine ring, as in the compounds represented by the above-mentioned formula (II). Typical examples of the halogenated triazine compounds include 2-(p-methoxyphenyl)-4,6-bis(trichloromethyl)-s-triazine, 2-styryl-4,6-bis(trichloromethyl)-s-triazine, 2-(p-methylstyryl)-4,6-bis(trichloromethyl)-s-triazine and 2-phenyl-4,6-bis(trichloromethyl)-s-triazine. The diphenyliodonium salt derivatives include compounds represented by the formula (III) wherein R 4 and R 5 are each hydrogen, an alkoxy group having 1 to 5 carbon atoms or t-butyl group; and X - is BF 4 - , PF 6 - , SbF 6 - or CF 3 SO 3 - . The preferable examples of the diphenyliodonium salt derivatives function as a photoinitiator, and typical examples thereof include diphenyliodonium hexafluoroantimonate, diphenyliodonium tetrafluoroborate, diphenyliodonium hexafluorophosphate, diphenyliodonium triflate and their derivatives. Needless to say, they are not restrictive. The triphenylsulfonium salt derivatives include compounds represented by the formula (IV) wherein R 6 is hydrogen, an alkyl group or an alkoxy group each having 1 to 5 carbon atoms, or fluorine; and X - is as defined above. The preferable examples of the triphenylsulfonium salt derivatives function as a photoinitiator, and typical examples thereof include triphenylsulfonium hexafluoroantimonate, triphenylsulfonium tetrafluoroborate, triphenylsulfonium hexafluorophosate, triphenylsulfonium triflate and their derivatives. Needless to say, they are not restrictive. Fig. 1A shows a glass substrate having black matrices thereon which are shade portions 2. In the first place, the substrate provided with the black matrices is coated with a composition, in which the ink absorbency of light irradiated portions can be improved by light irradiation or the combination of the light irradiation and a heat treatment, and if necessary, prebaking is then carried out to form a resin layer 3 (Fig. 1B). In forming this composition layer, a coating method such as spin coating, roll coating, bar coating, spray coating or dip coating can be used, and this coating means is not particularly restrictive. In this case, a compound such as perylene, anthracene or phenothiazine may be added as a sensitizing agent to the composition layer. Next, light irradiation is carried out from the underside of the substrate, and at this time, the composition layer is pattern-exposed through the black matrices as a mask to improve the ink absorbency of the irradiated portions of the composition layer (Fig. 1C). Thereafter, openings which are the irradiated portions are colored with colors of R, G and B by the use of an ink jet head 5 (Fig. 1D), and if necessary, the inks are then dried. In order to prevent the color skip of the color filter, the portions of the composition layer having a larger area than the openings of the black matrices are preferably colored, and for this coloring, it is necessary that the portions of the composition layer having a larger area than the black matrices as the mask take part in reaction. For the purpose of causing the reaction, some means are effective, and for example, diffused light can be used as irradiation light at the time of exposure, a large excess of energy can be irradiated, or a heat treatment is carried out for a long period of time after the exposure to diffuse the reaction. In this embodiment, there has been described the example where the pattern exposure is carried out by the use of the black matrices as the mask, but the pattern exposure may be done from the upside of the resin composition layer by the use of another photomask. Figs. 2A to 2E show a method for preparing a color filter for use in a liquid crystal panel in which the black matrices are formed on an opposite substrate. The method in which the black matrices are provided on the faced substrates instead of the side of the color filter is effective as a technique of improving an opening ratio. A glass substrate 1 shown in Fig. 2A is coated with a composition in which the ink absorbency of light irradiation portions can be improved by the light irradiation or the combination of the light irradiation and the heat treatment, and if necessary, prebaking is then done to form a composition layer 3 (Fig. 2B). Next, the pattern exposure is carried out through a photomask 4 to improve the ink absorbency of the exposed portions of the composition layer 3 (Fig. 2C), and these exposed portions of the layer are colored in the colors of R, G and B by the use of an ink jet head 5 (Fig. 2D), followed by drying, if necessary. In order to prevent the color skip, it is important that the width of non-colored portions 8 is smaller than that of the black matrices (not shown) provided on the opposite substrate. The resin composition for use in the present invention which can be rendered ink-acceptable is poor in ink-acceptable properties in itself, but it can be rendered ink-acceptable by at least one of the light irradiation or the combination of the light irradiation and the heat treatment under certain conditions. Any resin can be used, so long as it can cure under certain conditions, and examples of the resin include a novolak resin such as cresol-novolak, polyparahydroxystyrene and its derivatives in which a hydroxy group is blocked with a trimethylsilyl group, cellulose derivatives such as hydroxypropyl cellulose, hydroxyethyl cellulose, methyl cellulose and carboxymethyl cellulose in which a hydroxyl group is esterified or blocked with an acetyl group. Suitably usable examples of the photoinitiator which can accelerate a reaction with the aid of light or the combination of light and heat include an onium salt such as triphenylsulfonium hexafluoroantimonate, a halogenated organic compound such as trichloromethyltriazine, naphthoquinonediazide and their derivatives. The particularly preferable resin composition which can be used in the present invention comprises at least (a) an acrylic resin having a structure unit represented by the following formula (V) and (b) a compound as the photoinitiator selected from the group consisting of halogenated triazine compounds, diphenyliodonium salt derivatives and triphenylsulfonium salt derivatives: wherein R 1 is hydrogen or an alkyl group having 1 to 5 carbon atoms; R 2 is an alkylene group having 1 to 5 carbon atoms or a phenylene group; R 3 is an alkyl group having 1 to 5 carbon atoms, an alkyl-substituted silyl group, a phenyl group or a substituted aromatic group. The acrylic resin (a) having a structure unit represented by the above-mentioned formula (V) preferably gives rise to the hydrolysis of an ether linkage by cations formed from the photoinitiator by light irradiation to produce a hydroxyl group. Typical examples of the acrylic resin are as follows: / and The molecular weight of these resins is preferably in the range of from 10 2 to 10 7 . The employment of this kind of resin causes a definite difference of ink absorbency between an irradiated portion and a nonirradiated portion to permit the prevention of the color mixing of inks. Usable examples of the halogenated triazine compounds, the diphenyliodonium salt derivatives and the triphenylsulfonium salt derivatives with respect to compound (b) are as defined above. With regard to a ratio between the compounds (a) and (b), the amount of the compound (b) is in the range of from 0.01 to 10 parts by weight, preferably from 0.01 to 5 parts by weight with respect to 100 parts by weight of the acrylic resin which is the compound (a). In the exposed portions of the resin layer comprising these components, the amount of a hydroxyl group increases with the progress of the reaction, so that these portions become easy to absorb inks. Thus, when the resin layer is colored, the color mixing of the inks can be prevented. In order to improve the ink absorbency of the resin, the conversion of the resin into the hydrophilic group is preferably 30% or more. As the technique of a quantitative analysis of this hydrophilic group, a spectral analysis utilizing IR, NMR or the like is effective. The resin layer comprising these components is very excellent in fastnesses to heat, water and the like, and it can sufficiently withstand a high temperature and washing in subsequent steps. Next, if necessary, a protective layer 6 is formed (Figs. 1E and 2E) to obtain a color filter. As the protective layer, there can be used a resin material of a photosetting type, a thermosetting type or a photo-thermosetting type, or an inorganic film formed by vapor deposition or sputtering. Thus, as the protective layer, any material can be used, so long as it does not impede the transparency of the obtained color filter, and can sufficiently withstand subsequent steps such as an ITO formation step and an oriented film formation step. Next, the present invention will be described in more detail with reference to examples. The designation of "%" means "% by weight" unless otherwise noted. Example 1 5 g of polyparahydroxystyrene having a hydroxyl group protected with a trimethylsilyl group and 0.5 g of a cationic photoinitiator (SP-170, made by Adeca Co., Ltd.) were dissolved in 250 g of ethyl cellosolve acetate to prepare a resin composition which could be used in the present invention. A glass substrate 1 was spin-coated with the above-mentioned resin composition so as to make the thickness of a film of 1 µm, and prebaking was then carried out at 100°C for 15 minutes. Next, overall exposure was done in an exposure of 1.5 J/cm 2 , and an infrared absorption spectrum was then measured in a reflective mode by the use of FT-IR (Micro FTIR-100, made by Nippon Bunko Kogyo Co., Ltd.). The thus measured infrared absorption spectrum was compared with a spectrum before the exposure to inspect the residue of a hydroxyl group. As a result, it was confirmed that the residue of the hydroxyl group was increased to 700% of that of the hydroxyl group before the exposure. Next, a glass substrate 1 on which black matrices 2 were formed was spin-coated with the above-mentioned resin composition so as to make the thickness of a film of 2 µm, and prebaking was then carried out at 100°C for 15 minutes. Afterward, portions of the resulting resin layer on light-transmittable portions (which partially contained the resin on the black matrices) were subjected to pattern exposure in an exposure of 1.5 J/cm 2 through a photomask provided with openings having a diameter larger than the width of the light-transmittable portions to render the resin layer ink-acceptable. Furthermore, the ink-acceptable portions of the resin layer were colored with dye inks having a pH 9 by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by drying the inks at 90°C for 5 minutes. In succession, a heat treatment was carried out at 200°C for 60 minutes to cure the resin layer 3. Next, the resin layer 3 was spin-coated with a two-pack thermosetting resin SS-7625 (made by JSR) as a protective layer 6 so as to make the thickness of the layer of 1 µm, and a heat treatment was carried out at 230°C for 1 hour to cure a protective layer 6. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 2 A silicon substrate was spin-coated with a resin composition prepared in Example 1 so as to make the thickness of a layer of 1 µm, and prebaking was then carried out at 100°C for 15 minutes. Next, overall exposure was done in an exposure of 1.5 J/cm 2 , and followed by a heat treatment for 1 minute on a hot plate at 150°C. Afterward, the residue of a hydroxyl group was compared between before and after the exposure in the same manner as in Example 1, and as a result, it was confirmed that the residue of the hydroxyl group was increased to 500% of that of the hydroxyl group before the exposure. Next, a glass substrate 1 on which black matrices 2 were formed was spin-coated with the above-mentioned resin composition so as to make the thickness of a layer of 2 µm, and prebaking was then carried out at 100°C for 15 minutes to form a resin layer 3. Afterward, the portions of the resulting resin layer on light-transmittable portions (partially containing the resin on the black matrices) were subjected to pattern exposure in an exposure of 1.5 J/cm 2 through a photomask provided with openings having a diameter larger than the width of the light-transmittable portions, followed by a heat treatment for 1 minute on a hot plate at 150°C, thereby rendering the resin layer ink-acceptable. Furthermore, the ink-acceptable portions of the resin layer were colored with dye inks having a pH 9.5 by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by drying the inks at 90°C for 5 minutes. In succession, a heat treatment was carried out at 200°C for 1 hour to cure the resin layer 3, and a protective layer 6 was further formed on the resin layer 3 in the same manner as in Example 1. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, contrast is high and a highly fine color display was possible. Example 3 The same procedure as in Example 2 was effected except that exposure was done from the side of a substrate 1 by the utilization of black matrices as a photomask, as shown in Figs. 1A to 1E, thereby preparing a color filter. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 4 5 g of cellulose triacetate and 0.7 g of 1-naphthyl-bis-trichloromethyl-s-triazine were dissolved in 250 g of chloroform to prepare a resin composition which could be used in the present invention. Afterward, the residue of a hydroxyl group was compared between before and after the exposure in the same manner as in Example 1, and as a result, it was confirmed that the residue of the hydroxyl group after the exposure was increased to 500% of that of the hydroxyl group before the exposure. Next, a glass substrate 1 on which black matrices 2 were formed was roll-coated with the above-mentioned resin composition so as to make the thickness of a layer of 2 µm, and prebaking was then carried out at 90°C for 20 minutes to form a resin layer 3. Afterward, the portions of the resulting resin layer on light-transmittable portions (partially containing the resin on the black matrices) were subjected to pattern exposure in an exposure of 1 J/cm 2 through a photomask provided with openings having a diameter larger than the width of the light-transmittable portions, followed by rendering the resin layer ink-acceptable. Furthermore, the ink-acceptable portions of the resin layer were colored with dye inks having a pH 8.5 by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by drying the inks at 90°C for 5 minutes. In succession, a heat treatment was carried out at 200°C for 60 minutes to cure the resin layer 3. A protective layer 6 was further formed on the resin layer 3 in the same manner as in Example 1. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 5 For a resin composition prepared in Example 4, the amount of a hydroxyl group was compared between before and after the exposure in the same manner as in Example 2, and as a result, it was confirmed that the amount of the hydroxyl group after the exposure was increased to 600% of that of the hydroxyl group before the exposure. Next, a glass substrate 1 on which black matrices 2 were formed was roll-coated with the above-mentioned resin composition so as to make the thickness of a layer of 2 µm, and prebaking was then carried out at 90°C for 20 minutes to form a resin layer 3. Afterward, the portions of the resulting resin layer on light-transmittable portions (partially containing the resin on the black matrices) were subjected to pattern exposure in an exposure of 1 J/cm 2 through a photomask provided with openings having a diameter larger than the width of the light-transmittable portions, followed by prebaking at 150°C for 1 minute on a hot plate, thereby rendering the resin layer ink-acceptable. Furthermore, the ink-acceptable portions of the resin layer were colored with dye inks having a pH 9.3 by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by drying the inks at 90°C for 5 minutes. In succession, overall exposure was done, and a heat treatment was then carried out at 200°C for 60 minutes to cure the resin layer 3. A protective layer 6 was further formed on the resin layer 3 in the same manner as in Example 2. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 6 The same procedure as in Example 5 was effected except that exposure was done from the side of a substrate 1 by the utilization of black matrices as a photomask, as shown in Figs. 1A to 1E, thereby preparing a color filter. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. Example 7 The same procedure as in Example 5 was effected except that a pigment ink having a pH 9.1 was used as an ink, thereby preparing a color filter. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 8 A glass substrate 1 on which black matrices 2 were formed was spin-coated with a resin composition comprising (a) 10 parts by weight of polyphenoxyethyl methacrylate (molecular weight = 12000) and (b) 0.5 part by weight of a halogenated triazine compound (trade name TAZ-110, made by Midori Chemical Co., Ltd.) having the structure so as to make the thickness of a layer of 2 µm, as shown in Fig. 1, and prebaking was then carried out at 90°C for 20 minutes to form a resin layer 3. In succession, overall pattern exposure was done from the side of the substrate 1 so that the portions of the resin composition on the black matrices 2 might also be irradiated with light, and a heat treatment was then carried out at 110°C for 60 seconds. Afterward, openings of the resin composition layer 3 were colored with dye inks by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by a heat treatment at 90°C for 5 minutes and at 200°C for 30 minutes. Next, the resin layer 3 was spin-coated with a two-pack thermosetting resin (trade name Optomer SS-6688, made by Japan Synthetic Rubber Co., Ltd.) as a protective layer 6 so as to make the thickness of the layer of 1 µm, and prebaking was then carried out at 90'C for 30 minutes to form a second resin layer 6, followed by a heat treatment at 230°C for 30 minutes to cure the second resin layer, thereby preparing a color filter for liquid crystal display. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Examples 9 to 11 The same procedure as in Example 8 was carried out except that each composition shown in Table 1 was employed, to prepare a color filter. As a result, the same effect as in Example 8 could be confirmed. Example 12 A glass substrate 1 on which black matrices 2 were formed was spin-coated with a resin composition comprising (a) 10 parts by weight of polyphenoxyethyl methacrylate (molecular weight = 12000) and (b) 0.2 part by weight of a diphenyliodonium salt (trade name DPI-105, made by Midori Chemical Co., Ltd.) having the formula so as to make the thickness of a layer of 2 µm, as shown in Fig. 1, and prebaking was then carried out at 90°C for 20 minutes to form a resin layer 3. Next, overall pattern exposure was done from the side of the substrate 1 so that the portions of the resin composition on the black matrices 2 might also be irradiated with light, and a heat treatment was then carried out at 110°C for 60 seconds. Afterward, openings of the resin composition layer were colored with dye inks by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by a heat treatment at 90°C for 5 minutes and at 200°C for 30 minutes. Moreover, a protective layer 6 was formed in the same manner as in Example 8, thereby preparing a color filter for liquid crystal display. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Examples 13 to 15 The same procedure as in Example 12 was carried out except that each composition shown in Table 2 was employed, to prepare a color filter. As a result, the same effect as in Example 12 could be confirmed. Example 16 A glass substrate 1 on which black matrices 2 were formed was spin-coated with a resin composition comprising (a) 10 parts by weight of polyphenoxyethyl methacrylate (molecular weight = 12000) and (b) 0.2 part by weight of a triphenylsulfonium salt (trade name TPS-105, made by Midori Chemical Co., Ltd.) having the formula so as to make the thickness of a layer of 2 µm, as shown in Fig. 2, and prebaking was then carried out at 90°C for 20 minutes to form a resin layer 3. Next, overall pattern exposure was done from the side of the substrate 1 so that the portions of the resin composition on the black matrices 2 might also be irradiated with light, and a heat treatment was then carried out at 110°C for 60 seconds. Afterward, openings of the resin composition layer were colored with dye inks by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by a heat treatment at 90°C for 5 minutes and at 200°C for 30 minutes. Moreover, a protective layer 6 was formed in the same manner as in Example 8 to prepare a color filter for liquid crystal display. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 3 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Examples 17 to 19 The same procedure as in Example 16 was carried out except that each composition shown in Table 3 was employed, to prepare a color filter. As a result, the same effect as in Example 16 could be confirmed. Example 20 A glass substrate 1 was coated with a composition like in Example 8, as shown in Fig. 2, thereby forming a resin composition layer 3. Next, pattern exposure was carried out from the side of the resin layer 3 through a photomask 4 to improve the ink absorbency of the exposed portions of the resin. Afterward, the exposed portions were colored with dye inks by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by a heat treatment at 90°C for 5 minutes and at 200°C for 30 minutes. Moreover, a protective layer 6 was formed in the same manner as in Example 8 to prepare a color filter for liquid crystal display, The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 4 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 21 A glass substrate 1 was coated with a composition like in Example 12, as shown in Fig. 2, thereby forming a resin composition layer 3. Next, pattern exposure was carried out from the side of the resin layer 3 through a photomask 4 to improve the ink absorbency of the exposed portions of the resin. Afterward, the exposed portions were colored with dye inks by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by a heat treatment at 90°C for 5 minutes and at 200°C for 30 minutes. Moreover, a protective layer 6 was formed in the same manner as in Example 8 to prepare a color filter for liquid crystal display. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 4 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. Example 22 A glass substrate 1 was coated with a composition like in Example 16, as shown in Fig. 2, thereby forming a resin composition layer 3. Next, pattern exposure was carried out from the side of the resin layer 3 through a photomask 4 to improve the ink absorbency of the exposed portions of the resin. Afterwards the exposed portions were colored with dye inks by the use of an ink jet head 5 to obtain a matrix pattern of R, G and B, followed by a heat treatment at 90°C for 5 minutes and at 200°C for 30 minutes. Moreover, a protective layer 6 was formed in the same manner as in Example 8 to prepare a color filter for liquid crystal display. The thus prepared color filter for liquid crystal display was observed by an optical microscope, and as a result, defects such as color mixing, color unevenness and color skip were not confirmed. A liquid crystal panel shown in Fig. 4 was manufactured by the use of this color filter, and when a device using the panel was driven, a highly fine color display was possible. According to the present invention, there can be provided a highly reliable color filter for liquid crystal display which is free from defects such as color mixing, color unevenness and color skip, and a liquid crystal panel which permits a highly fine color display.

Claims: A method of manufacture of a color filter, wherein in a first step a resin layer (3) to be colored by ink-jet-printing is formed on a substrate (1), said method being characterized by the additional steps of: improving the ink accepting property of portions (7) of the resin layer (3) between adjacent areas (8) of said resin layer (3) by exposing said portions (7) to light irradiation or the combination of light irradiation and heat treatment; providing a plurality of colorants having different colors to said portions (7) exposed in said exposure step, using an ink-jet printing system to form a pattern of the plurality of colors; and curing the resin layer (3) by light irradiation or heating. The method according to claim 1, wherein a protective layer (6) is formed on the resin layer (3). The method according to anyone of claims 1 or 2, wherein the substrate (1) is provided with shade portions (2) thereon, and the areas (8) of the resin layer (3) are on the shade portions (2). The method according to claim 3, wherein the width of the areas (8) of the resin layer (3) on the shade portions (2) is smaller than that of the shade portions (2). The method according to anyone of claims 1 to 4, wherein said resin layer (3) of the first step comprises at least (a) an acrylic resin having a structure unit represented by the following formula (V); and (b) a compound selected from the group consisting of halogenated triazine compounds, diphenyliodonium salt derivatives and triphenylsulfonium salt derivatives: wherein R 1 is hydrogen or an alkyl group having 1 to 5 carbon atoms; R 2 is an alkylene group having 1 to 5 carbon atoms or a phenylene group; and R 3 is an alkyl group having 1 to 5 carbon atoms, an alkyl-substituted silyl group, a phenyl group or a substituted aromatic group. The method according to claim 5, wherein the compound (b) is present in an amount of from 0.01 to 10 parts by weight per 100 parts by weight of the copolymer (a). A method of manufacture of a liquid crystal panel, comprising the steps of: providing a color filter produced by the method according to anyone of the preceeding claims; providing a second substrate at a position opposite to the color filter; and enclosing a liquid crystal composition between the color filter and the second substrate. The method according to claim 7, wherein the second substrate is provided with shade portions thereon.

Inventors: KASHIWAZAKI AKIO, MIYAZAKI TAKESHI, MURAI KEIICHI, SATO HIROSHI, SHIBA SHOJI, SHIROTA KATSUHIRO, YOKOI HIDETO, KASHIWAZAKI, AKIO, MIYAZAKI, TAKESHI, MURAI, KEIICHI, SATO, HIROSHI, SHIBA, SHOJI, SHIROTA, KATSUHIRO, YOKOI, HIDETO
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1994
Main classification: G03F7
IPC codes: G03F7, B41J2, B41M5, G02B5, B41M7, B41M3