MULTI-FIBER TYPE OPTICAL CABLE COUPLER AND PROCESS FOR PRODUCTION THEREOF

Abstract: When a multi-fiber type optical cable coupler obtained from a tape core wire (1) is fixed to a reinforcement case (3), a glass portion (2b) as a non-extension portion outside a fusing extension portion (2c) of the coupler and a protective cladding layer (2a) at the back of the glass portion (2b) are fixed by an adhesive layer (4). A collective coating resin layer (1a) of the tape core wire (1) is not fixed to the reinforcement case (3). When it is fixed, it is fixed to the reinforcement case (3) by a soft adhesive layer (5) different from the adhesive layer (4) described above. A resin having a viscosity of 50 to 200 P or a UV-curing and thermosetting resin is suitable as the resin of the adhesive layer (4).

Description: Field of the Invention The present invention relates to a method of manufacturing a multiple-optical- fiber coupler in which 2n optical core fibers are melted, coupled and elongated. Background of the Invention Generally, a conventional optical fiber coupler has a drawback that it easily changes in characteristics and is damaged due to external force or temperature change, because it has a small outer diameter portion of a few tens of µm. Therefore, the conventional optical fiber coupler is designed such that the coupler for the melted, coupled and elongated optical fibers is fixed to a reinforcement substrate having a linear expansion coefficient as much as quartz, so that the characteristics are stable. As the reinforcement substrate, a plate member is used as described in Japanese Utility Model Application Laying-open No. 23408/1989 and a pipe member is used as described in Japanese Patent Application Laying-open No. 63907/1989, for example. On the other hand, thermosetting adhesive or ultraviolet cure adhesive of epoxy, urethane acrylate, and cyanoacrylate is used as the adhesive for adhering the conventional coupler. Recently, a high density optical communication line has developed so that the number of optical couplers increases. Therefore, since the conventional optical fiber coupler is designed to couple a pair of optical fibers to each other, there are caused problems that an occupied area by the optical fiber coupler increases and accommodation of excess portions at the ends of the optical fibers is complex. On the contrary, as disclosed in Japanese Patent Application Laying-open No. 295211/1990, for instance, the reinforcing method of the optical fiber coupler is proposed in which after an optical fiber coupler for coupling two optical fibers is fixed to a reinforcement member so that a plurality of reinforcement members are accommodated in a package, the optical fibers are coupled outside of the package by a tape to construct an arrayed optical fiber coupler. Another method of reinforcing an optical fiber coupler is proposed in which optical fiber couplers for each coupling two optical fibers to each other are arranged on a fixing member having a plurality of grooves in a comb manner, as disclosed in Japanese Patent Application Laying-open No. 254406/1988. The methods disclosed in the above Japanese Patent Application Laying-open No. 295211/1990 and Japanese Patent Application Laying-open No. 254406/1988 are complicated and have a problem that it takes a long time to form an arrayed optical fiber coupler because the optical fiber couplers for each coupling two optical fibers are mounted in a high density manner. For this reason, as disclosed in Japanese Patent Application Laying-open No. 120510/1990, the method is tried in which an arrayed optical fiber coupler is directly constituted from arrayed optical fiber ribbons. In a case that the arrayed optical fiber coupler is fixed to a reinforcement substrate, however, there is a problem that the transmission characteristics are remarkably degraded due to temperature change or humidity change. Figs. 10A, 10B and 10C show a reinforcement structure in a conventional arrayed optical fiber coupler. Fig. 10A is a plan view of the reinforcement structure, Fig. 10B is a perspective view of a reinforcement case used in the reinforcement structure shown in Fig. 10A, and Fig. 10C is a cross sectional view of an arrayed optical fiber ribbon used in the reinforcement structure shown in Fig. 10A. A reference numeral 1 denotes an arrayed optical fiber ribbon in Fig. 10C. This arrayed optical fiber ribbon 1 is constituted by collectively coating four optical fibers 2 each having a protection coating layer 2a with a coating layer 1a. A reference numeral 3 denotes a reinforcement case in Figs. 10A and 10B. On the upper surface 3a of the reinforcement case 3, a pair of fixed walls 3b extending along a longitudinal direction of the case in parallel to each other at both side edges are provided to prevent the displacement of the optical fiber ribbon 1 by the reinforcement structure. In this arrayed optical fiber ribbon 1, after part of the coating layer 1a and protection coating layer 2a of each optical fiber is removed to expose a glass portion of the optical fiber 2, the ribbons 1 are overlain in a vertical direction and corresponding glass portions 2b are heated and elongated to be melted and coupled. The glass portion 2b is fixed to the upper surface 3a and the fixed wall 3b of the reinforcement case 3 by an adhesive layer 4, as well as the coating resin layer 1a of the optical fiber ribbon 1. However, because distortion remained in the collectively coating resin layer 1a from when the arrayed optical fiber ribbon 1 has been manufactured is released in a form of contraction of the collectively coating resin layer 1a due to temperature change or humidity change, a relative shift is caused between the collectively coating resin layer 1a and the glass portion 2b including a melted, bonded and elongated portion. Thus, in the conventional arrayed optical fiber coupler, because the collectively coating resin layer 1a is strongly fixed to the reinforcement case 3, a stress is generated at a melted, bonded and elongated portion having a small diameter so that the transmission characteristics of the optical fiber coupler is changed. In a case where four or more optical fibers are collectively adhered and fixed to the reinforcement member, the optical fiber coupler does often not have sufficient circumstance resistance characteristics. For instance, an allowable change value is generally 0.2 dB or less in a heat cycle test in which temperature load of -20 to +60 °C is applied to the optical fiber coupler to examine characteristics change. However, in the above structure, the change value of about 0.5 dB is often observed, as shown in Fig. 11. The change value needs to be 0.2 dB or less after 100 hours in a characteristics change test under 60 °C and 95 %. In the above structure, the more than 0.3 dB change values are frequently observed, as shown in Fig. 12. It should be noted that in Fig. 11 the abscissa represents time length of the heat cycle test, the ordinate represents temperature in the heat cycle test and change value of coupling loss due to the heat cycle test and that in Fig. 12 the abscissa represents time length during which a sample is exposed under humidity and heat condition and the ordinate represents change value of coupling loss under the humidity and heat condition. Another prior art that is of interest is EP-A-0 525 743 that discloses a method of reinforcing a multiple optical fiber coupling unit comprising the steps of: removing a portion of longitudinal coatings of optical fibers of the multiple optical fiber coupling unit to expose glass portions of said optical fibers; fusing a portion of said exposed glass portions so as to optically couple said optical fibers; extending the fused portion to a predetermined state; fixing non-extended portions of said exposed glass portions on a first reinforcing substrate with a first adhesive; and fixing said first reinforcing substrate on a second reinforcing substrate with a second adhesive. The second adhesive can be a soft adhesive with the Young's modulus thereof being no larger than 0.1 kg/mm 2 at -40°C. The first adhesive is one of a thermosetting and ultraviolet-setting adhesive. This prior art also discloses a multiple fiber coupler unit comprising a plurality of optical fibers optically coupled by fusing ends thereof; a first substrate being affixed to said optical fibers near said fused ends by a first adhesive so as to reinforce the coupled optical fibers; and a second substrate being affixed to said first substrate by a second adhesive. The first substrate may be made from one of quartz and liquid crystal polymers having a coefficient of linear expansion substantially equal to a coefficient of linear expansion of said optical fibers. The second substrate is made from one of liquid crystal polymers and invar. The second substrate may be of a box-like configuration. The first adhesive is one of a thermosetting and ultraviolet-setting adhesive and the second adhesive may be a flexible silicon rubber adhesive. The second adhesive can have a Young's modulus at -40°C that is not larger than 0.1 kg/mm 2 . An object of the present invention is to provide an arrayed optical fiber coupler and a method of manufacturing the same in which the arrayed optical fiber coupler has a reinforcement structure with sufficient circumstance resistance characteristics and, even if a relative shift is caused between a collectively coating resin layer and a glass portion of optical fiber ribbon because of distortion arising in the collectively coating resin layer from when the optical fiber ribbon is manufactured, a melted, coupled and elongated portion is not influenced due to said relative shift. Disclosure of the Invention In order to achieve the object of the present invention, the invention defined in Claim 1 is a method of manufacturing a multiple-optical-fiber coupler which comprises a first ribbon of optical fibers in which all of the optical fibers are arranged in parallel with each other and entirely coated with a collective coating resin layer and a second ribbon of optical fibers in which all of the optical fibers are arranged in parallel with each other and entirely coated with a collective coating resin layer. The coupler includes a reinforcement member , each optical fiber has a glass portion and a protection coating layer around said glass portion, each glass portion of the first ribbon of optical fibers has an extent opposing on and in parallel with a corresponding extent of a respective glass portion of the second ribbon of optical fibers to form a pair of optical fibers, and each pair of said optical fibers being fused together to form a thin integral portion in the longitudinally middle portion of said extent. The method comprises the steps of: removing said protection coating layers from the longitudinally middle portions of said optical fibers to expose glass portions thereof; opposing the exposed glass portions of each said pair of said optical fibers in parallel; fusing and elongating each said pair of exposed glass portions by heat to form a thin integral portion; and collectively fixing a part of the exposed glass portions and the protective coating layers to said reinforcement member with an adhesive layer having the viscosity of 50 to 200 P before the cure of the adhesive. In the invention defined in dependent Claim 2 comprises the further steps of: initially removing from each of the first and second ribbons a length of said collective coating layer that is longer than the length of the protection coating layer that is to be removed from each optical fiber and such that a length of said exposed protection coating layer of each optical fiber remains exposed adjacent each end of its respective exposed glass portion. In the invention defined in Claim 3, the method is as defined in Claim 1 or Claim 2 including the further steps of adhesively fixing the collective coating layer of each ribbon to said reinforcement member by means of an adhesive layer that is softer than the adhesive layer that is used to secure the protective coating layer and glass portion of each optical fiber to the reinforcement member. In the invention defined in Claim 4, the adhesive layer defined by Claim 1 additionally has thermosetting property and ultraviolet cure property. In the invention defined in Claim 5, the softer adhesive layer defined by Claim 3 is an adhesive having thermosetting property and ultraviolet cure property. In the present invention, an influence on the melted, coupled and elongated portion can be prevented by not fixing the collectively coating resin layer to the reinforcement member or by fixing the collectively coating resin layer to the reinforcement member with a soft adhesive, to permit the collectively coating resin layer to move relatively to the glass portions. In the present invention, by fixing the optical fibers with the resin having the viscosity of 50 to 200 P before the cure, any space in the resin surrounding the optical fibers can be prevented from being generated so that the coupler can be obtained with less characteristic change for a heat cycle. Also, by using both thermosetting type and ultraviolet cure type resin as an adhesive, the resin hardness can be increased even in the lower portion of the optical fibers, so that the coupler can be obtained with the superior heat and humid resistance characteristics. Brief Description of the Drawings Figs. 1A, 1B and 1C show an arrayed optical fiber coupler according to the first embodiment of the present invention, Fig. 1A is a plan view, Fig. 1B is a cross sectional view taken along the II-II line, and Fig. 1C is a cross sectional view taken along the III-III line; Fig. 2 is a perspective view of a reinforcement case applicable to the first embodiment shown in Figs. 1A, 1B and 1C; Figs. 3A, 3B and 3C show an arrayed optical fiber coupler according to the second embodiment of the present invention, Fig. 3A is a plan view, Fig. 3B is a cross sectional view taken along the II-II line, and Fig. 3C is a cross sectional view taken along the III-III line; Fig. 4 is a perspective view of a reinforcement case applicable to the second embodiment shown in Figs. 3A, 3B and 3C; Figs. 5A, 5B and 5C show an arrayed optical fiber coupler according to the third embodiment of the present invention, Fig. 5A is a plan view, Fig. 5B is a cross sectional view taken along the II-II line, and Fig. 5C is a cross sectional view taken along the III-III line; Fig. 6 is a perspective view of a reinforcement case applicable to the third embodiment shown in Figs. 5A, 5B and 5C; Figs. 7A, 7B and 7C show an arrayed optical fiber coupler according to the fourth embodiment of the present invention, Fig. 7A is a plan view, Fig. 7B is a cross sectional view taken along the II-II line, and Fig. 7C is a cross sectional view taken along the III-III line; Figs. 8A and 8B are cross sectional views showing an example of a tape ribbon applicable to a reinforcement structure in the arrayed optical fiber coupler of the present invention, Fig. 8a shows a 2-arrayed tape ribbon, and Fig. 8B shows a 8-core type of tape ribbon; Fig. 9 is a diagram showing a group of units which are used to achieve the reinforcement structure in the arrayed optical fiber coupler of the present invention; Figs. 10A, 10B and 10C show the reinforcement structure in a conventional arrayed optical fiber coupler, Fig. 10A is a plan view, Fig. 10B is a perspective view of the reinforcement case used in the reinforcement structure shown in Fig. 10A, and Fig. 10C is a cross sectional view of a 4-core type tape ribbon which can be used in both the conventional device and in the present invention. Fig. 11 is a graph showing the change of coupling loss in a heat cycle test; Fig. 12 is a graph showing the change of coupling loss under high humid and hot circumstance; Figs. 13A and 13B are cross sectional views of a left (or right) half of Fig. 1C. showing an expanded cross section structure of a fixed portion in the arrayed optical fiber coupler, Fig. 13A shows the structure in which the space surrounded by the 4-core type optical fiber ribbon is filled with fixing resin, and Fig. 13B shows the structure in which the space is not filled with the fixing resin; and Fig. 14 is a cross sectional view showing points P1 to P5 of the fixed portion shown in Fig. 13A where hardness is measured. The Best Mode of Preferred Embodiments The embodiments of the present invention will be described below with reference to the accompanying drawings. Figs. 1A, 1B and 1C show an arrayed optical fiber coupler according to the first embodiment of the present invention. More specifically, Fig. 1A is the plan view of the coupler, Fig. 1B is the cross sectional view of the coupler taken along the line II - II, and Fig. 1C is the cross sectional view of the coupler taken along the line III - III. Fig. 2 is a perspective view of a reinforcement case as a reinforcement member used in the first embodiment. The embodiment of the present invention will be described below with reference to the accompanying drawings. Of constituent elements in the present embodiment shown in Figs. 1A, 1B, 1C, and 2, the same ones as those of the reinforcement structure in the conventional arrayed optical fiber coupler shown in Figs. 10A, 10B and 10C are assigned with the same reference numerals and the description will be omitted. The present embodiment will be described with reference to a 4-core type optical fiber ribbon 1 shown in Fig. 10C. A collectively coating resin layer 1a in the central portion of the 4-core type optical fiber ribbon 1 is removed to expose the optical fibers 2 and these are separated into pairs. Next, a protection coating layer 2a of each of the optical fibers 2 is removed such that a glass portion thereof is exposed. Preferably the protection coating layer 2a is not removed over the whole of the exposed optical fiber portion but is removed in a minimum, in consideration of strength stability. Another 4-core type optical fiber ribbon 1 which is prepared in the same manner as described above to expose the glass portions 2b is overlain on the above-mentioned ribbon 1. The glass portions 2b of the corresponding optical fibers 2 of the optical fiber ribbons 1 are heated and melted and coupled to each other. Then, the glass portions are elongated to form a melted, coupled and elongated section 2c having a small diameter as shown in Fig. 1A. Since the optical fibers 2 are separated into pairs, a group is constituted of 4 optical fibers 2 of the upper and lower ribbons 1 by the melting, coupling and elongating process. Thus, the arrayed optical fiber coupler composed of two groups of four optical fibers 2 can be obtained from the two overlain 4-core type optical fiber ribbons 1. In one embodiment of the present invention the structure is such that an arrayed optical fiber coupler is fixed to a reinforcement case 3 shown in Fig. 2. That is, the reinforcement case 3 shown in Fig. 2 has a partitioning wall 3c between the fixed walls 3b in the central portion on the upper surface 3a of the reinforcement case 3 shown in Fig. 10B so that a groove portion is divided into two grooves by the partitioning wall 3c. Each of the groups of four optical fibers 2 is arranged such that the elongated portions 2c thereof are positioned in the central portion of one groove and the glass portions 2b and the protection coating layers 2a of these optical fibers are fixed to the groove via an adhesive layer 4. Fig. 1B shows the arrangement and fixing of the four optical fibers 2 within the reinforcement case 3 and fig. 1C shows the arrangement and fixing of the glass portions 2b within the reinforcement case 3. In this particular embodiment, the collective coating resin layer 1a of the optical fiber ribbon 1 is not fixed to the reinforcement case 3, see Fig.1A. Therefore, any influence due to distortion remaining in the collective coating resin layer 1a from when the optical fiber ribbon 1 is manufactured can be eliminated so that the degradation of transmission characteristics can be avoided. Figs. 3A, 3B and 3C show the arrayed optical fiber coupler according to the second embodiment of the present invention. Fig. 3A is a plan view, Fig. 3B is a cross sectional view of the coupler taken along the line II-II, and Fig. 3C is a cross sectional view of the coupler taken along the line III- III. Fig. 4 is a perspective view of a reinforcement case as a reinforcement member used in the second embodiment. The difference of the second embodiment from the first embodiment is mainly in the groove structure of the reinforcement case 3. That is, three partitioning walls 3c, see Fig.4, are formed on the upper surface 3a of the reinforcement case 3 such that 4 grooves can be formed between the fixed walls 3b all with the same size. The elongated portion of a pair of optical fibers 2 is arranged in each of the groove. The protection coating layers 2a and glass portions 2b of the optical fibers 2 are fixed by an adhesive layer 4 for every groove. The collective coating resin layer 1a of the arrayed optical fiber ribbon 1 is not fixed to the reinforcement case in the second embodiment, as in the first embodiment and hence the degradation of transmission characteristics can be avoided. Figs. 5A, 5B and 5C show the arrayed optical fiber coupler according to the third embodiment of the present invention. Fig. 5A is a plan view, Fig. 5B is a cross sectional view of the coupler taken along the line II-II, and Fig. 5C is a cross sectional view of the coupler taken along the line III-III. Fig. 6 is a perspective view of a reinforcement case as a reinforcement member used in the third embodiment. The difference of the third embodiment from the first embodiment is mainly in the structure of the reinforcement case 3 and in that two types of adhesive having different Young's moduli are used in the fixing of the coupler to the reinforcement case. The same 4-core type optical fiber ribbon as in the first embodiment is used as the arrayed optical fiber ribbon and the collective coating resin layer of the ribbon 1 is fixed to the reinforcement case 3 by an adhesive layer 5 in this third embodiment. The adhesive layer 5 is softer than the adhesive layer 4 by which the protection coating layer 2a and glass portion 2b of the optical fiber 2 are fixed to the reinforcement case 3. For this reason, even if the collective coating resin layer 1a of the optical fiber ribbon 1 is directly fixed to the reinforcement case 3, the transmission characteristics are not degraded because the influence of distortion remained in the collectively coating resin layer 1a upon the manufacturing can be cancelled or eliminated by the difference between the adhesive layers 4 and 5 in their Young's modulus. Figs. 7A, 7B and 7C show the arrayed optical fiber coupler according to the fourth embodiment of the present invention. Fig. 7A is a plan view, Fig. 7B is a cross sectional view of the coupler taken along the line II-II, and Fig. 7C is a cross sectional view of the coupler taken along the line III- III. The fourth embodiment indicates an example of the reinforcement structure in the coupler in which the reinforcement case shown in Fig. 10B is used. Also in the fourth embodiment, the protection coating layer 2a and glass portion 2b of the optical fiber 2 of the 4-core type optical fiber ribbon 1 are fixed to the reinforcement case 3 by the adhesive layer 4. This fixing does not involve any fixing of the collective coating resin layer 1a of the optical fiber ribbon 1 to the reinforcement case 3. Therefore, the coupler in the fourth embodiment is not influenced by any distortion remaining in the collective coating resin layer 1a. In the above embodiments, the 4-core type optical fiber ribbon is used as the arrayed optical fiber ribbon. However, a 2-core type optical fiber ribbon shown in Fig. 8A or a 8-core type optical fiber ribbon shown in Fig. 8B may be used. Although ultraviolet cure resin or thermosetting resin is used as a material for the collectively coating resin layer used in the above embodiments, the material is not limited to them. Further, the material of the reinforcement case needs to have the line expansion coefficient as large as the quartz optical fiber and the material such as quartz, liquid crystal plastics (LCP), fiber reinforced plastics (FRP), and invar alloys may be used. The adhesive such as ultraviolet cure adhesive, thermosetting adhesive, and ultraviolet ray and thermosetting adhesive may be used as the adhesive for forming the adhesive layer. Fig. 9 shows a group of units which are used to achieve the arrayed optical fiber coupler according to the present invention. In the figure, a reference numeral 11 denotes an elongating stage, 12 an optical fiber clamper, 13 a microtorch, 14 a light source, 15 a power meter, and 16 a reinforcement case supporting stage. Next, the outline of processes in which the arrayed optical fiber coupler used in this invention is fixed to the reinforcement case using the units will be described below. For instance, the collectively coating resin layer 1a is removed from the central portion of the arrayed optical fiber ribbon 1 shown in Fig. 1A and the optical fibers 2 are separated into pairs. Then, the protection coating layer 2a of each of the optical fibers 2 is removed to expose the glass portion 2b. The exposed glass portions 2b are fixed by the optical fiber clamper 12 and heated by the microtorch 13 such that the glass portions 2b are melted and coupled to each other. Thereafter, the coupled optical fibers 2 is released from the optical fiber clamper 12 and the coupled glass portions are heated and elongated while tension to them is maintained. At this time, the coupled glass portions are heated and elongated while the light branch state of the coupler is monitored using the light source 14 and the power meter 15 and when a predetermined light branch state is achieved, the elongating operation is stopped. Next, the reinforcement case supporting stage 16 is moved to position the reinforcement case on the stage at a predetermined position and the coupler is fixed to the reinforcement case by the adhesive. At this time, it is important to fix the exposed glass portions on the both sides of the elongated portion 2c as peripheral glass portions and the protection coating layers outside of the peripheral glass portions to the reinforcement case. Next, the embodiments of the present invention will be described below, taking a particular example. Two 4-core type tape ribbons are prepared in each of which four optical fibers are collectively coated, two layers protection coating being performed for each of the 3 m band single mode optical fibers which has the difference between the core and the clad in refractive index of 0.3 %, the core diameter of 8µm, the clad diameter of 1.25µm. Using the 4-core type tape ribbon, a coupler is fabricated by the above group of units to have the branch ratio of 50 % in the light of wavelength of 1.3µm. The reinforcement case made from crystalline glass (linear expansion coefficient: 1.5 × 10 -7 /°C) is used. In one embodiment two of the optical fibers of each ribbon are accommodated in one of the grooves of the reinforcement case having the structure shown in Fig. 2 and the glass portion 2b of each optical fiber, other than the elongated portion 2c, and the protection coating layer 2a are fixed to the reinforcement case 3 to obtain the structure shown in Figs. 1A to 1C. Ultraviolet cure type adhesive is used in the fixing (embodiment 1). In another embodiment each of the optical fibers of each ribbon is accommodated in one of the grooves of the reinforcement case having the structure shown in Fig. 4 and the glass portion of each optical fiber other than the elongated portion and the protection coating layer are fixed to the reinforcement case by ultraviolet cure type adhesive to obtain the structure shown in Fig. 3A (embodiment 2). In another embodiment every two of the optical fibers are accommodated in one of the grooves of the reinforcement case having the structure shown in Fig. 6 and the glass portion of each optical fiber other than the elongated portion is fixed to the groove by ultraviolet cure type adhesive as well as the collective coating resin layer 1a of the tape ribbon which is fixed to a non-groove surface of the reinforcement case by soft thermosetting type adhesive (Young's modulus: about 0.07 kg/mm 2 ) to obtain the structure shown in Fig. 5A (embodiment 3). In another embodiment and using the reinforcement case having the structure shown in Fig. 10B, the optical fibers are fixed as in the first and second embodiments to obtain the structure shown in Fig. 7A (embodiment 4). That is, the collective coating resin layer 1a of the tape ribbon 1 is not fixed to the reinforcement case but remains outside of the reinforcement case. As a comparison example, the same arrayed optical fiber coupler as described above is fixed to a reinforcement case 3 having the structure shown in Fig. 10B by ultraviolet cure type adhesive. In this case, the collectively coating resin layer 1a is first removed from the central portion of the arrayed optical fiber ribbon 1 and then the central portion of the arrayed optical fiber ribbon 1 is separated into a plurality of optical fibers 2 and the collective coating resin layer 1a is also fixed to said reinforcement case by the same adhesive to obtain the structure shown in Fig. 10a. A heat cycle test between -20 to 60 °C is performed for the couplers of the first to fourth embodiments and the comparison example under the same condition. The transmission losses of the couplers are measured during the test using a laser emission diode (LED) having the wavelength of 1.3 µm. The measuring result is shown in a table 1. In the table 1, "core 1", "core 2", "core 3", and "core 4" indicate the coupler numbers from one end of the 4-core type tape ribbon. The value of greater change of the insertion losses at a straight port and a cross port is shown as the value of the loss change in the table 1. As seen from the table 1, the comparison example has remarkable characteristic changes depending upon temperature and the influence of the distortion remaining in the collective coating resin layer from when the optical fiber ribbon is manufactured. On the other hand, in the embodiments 1 to 4, because the influence of such distortion does not appear, the transmission characteristics of the couplers are stable. There is studied the characteristic change of the arrayed optical fiber couplers having the reinforcement structures by the adhesive as described above under the particular circumstance tests (heat cycle test and high humid and hot test). That is, as a result of the study of the characteristic change in the above circumstance tests by the inventors, the following facts are found. Fig. 13A shows a cross sectional view of the fixed portion of the coupler which has the characteristic change (coupling loss change) of 0.06 dB is a good result in the heat cycle test shown in Fig. 11 and is superior in the circumstance resistance characteristics and Fig. 13B shows a cross sectional view of the fixed portion of the coupler which has the characteristic change of 0.5 dB is a worse result in the same heat cycle test and is inferior in the circumstance resistance characteristics. As seen from Fig. 13A, in the fixed portion of the superior coupler the space formed between 4 optical fibers 2b is completely filled with the adhesive layer 4 and on the contrary, as seen form Fig. 13B, in the fixed portion of the inferior coupler the space formed between 4 optical fibers 2b is not completely filled with the adhesive layer to form a cavity 6. In the heat cycle test, when the coupler is located in low temperature, a small bending stress would act on each optical fiber (125 µm) 2b because of nonuniform expansion or contraction of the resin so that the transmission characteristics are changed. The inventors fabricated samples in various viscosities of resin (adhesive) of the fixed portion in order to eliminate the generation of the cavity 6 and thereby the characteristic change in the heat cycle test. The following table 2 indicates the result. It can be seen from table 2 that the resin (adhesive) viscosity for fixing the optical fiber is preferably in a range of 50 P to 200 P. That is, the types of resin c to e are suitable for the resin (adhesive) for fixing the optical fibers of the arrayed optical fiber coupler according to the present invention. Next, the optical fiber fixed portion was cut to expose a cross-section and the resin hardnesses in the cross section were measured by a micro FTIR (Fourier transformation type infrared spectrometer). In Fig. 14 the hardness in the measuring point P1 was 95 %, P2 96 %, P3 93 %, P4 88 %, and P5 70 %. As seen from Fig. 14, it was found that the hardness was lacking in the lower portion of the optical fiber (P4 or P5). Because the optical fibers are collectively fixed, the light intensity would be weak in the lower portion of the optical fibers so that the cure of the resin is insufficient. If the cure of the resin is insufficient, it is expected that a portion where polymerization is not caused reacts with water so that deterioration of the resin is caused under a high humid and hot circumstance. The inventors fabricated samples using ultraviolet cure and themosetting resin such that the hardness of the resin in the lower portion of the optical fibers was the same as that of other portions. The following table 3 indicates the result. The symbol "*" in the table 3 indicates the high humid and hot test in the ambient of humidity of 90 % at 60 °C for 100 hours. It is found from the table 3 that ultraviolet ray and thermosetting type resin is good in characteristic and preferable in productivity. Next, the high humid and hot test in the ambient of humidity of 90 % at 60 °C for 100 hours was performed for the couplers of the embodiments 1 and 2 in which the ultraviolet cure adhesive was not used. A monitor wavelength was 1.31 µm and the change of transmission loss was measured for each "optical fiber" of each coupler. The measuring result is shown in a table 4. In the table 4, "fiber 1", "fiber 2", "fiber 3" and "fiber 4" are the same as in the table 1. Result of high humid and hot test embodiment 1 embodiment 2 fiber 1 0.05 dB 0.03 dB fiber 2 0.04 0.05 fiber 3 0.06 0.03 fiber 4 0.08 0.02 As seen from the table 4, it is found that the couplers of the embodiments 1 and 2 have extremely small characteristic change. Possibility of Industrial Application As described above, according to the present invention, the protection of the coupler structure can be reinforced and the stabilization of transmission characteristics can be achieved because the influence of distortion remained in the collectively coating resin layer of the arrayed optical fiber ribbon can be eliminated. The optical fiber coupler added with such a reinforced structure can sufficiently cope with the recent high density optical communication line by the stability of the transmission characteristics. In addition, according to the present invention, by fixing the optical fibers with resin having a viscosity of 50 P to 200 P before cure, the arrayed optical fiber coupler can be obtained in which a cavity can be prevented from being generated in a portion surrounded by the optical fibers with less characteristic change in heat cycle test and with sufficient circumstance resistance characteristics. Further, according to the present invention, by using for the above mentioned resin ultraviolet ray and thermosetting type resin as an adhesive for fixing the optical fibers, the arrayed optical fiber coupler can be obtained with superior high humid and hot characteristic and with sufficient circumstance resistance characteristics because the hardness of the resin can be increased even in the lower portion of the optical fibers.

Claims: A method of manufacturing a multiple-optical-fiber coupler which comprises a first ribbon (1) of optical fibers (2) in which all of the optical fibers are arranged in parallel with each other and entirely coated with a collective coating resin layer (1a) and a second ribbon (1) of optical fibers (2) in which all of the optical fibers are arranged in parallel with each other and entirely coated with a collective coating resin layer (1a); the coupler including a reinforcement member (3); each optical fiber (2) having a glass portion (2b) and a protection coating layer (2a) around said glass portion (2b); each glass portion (2b) of the first ribbon (1) of optical fibers (2) having an extent opposing on and in parallel with a corresponding extent of a respective glass portion (2b) of the second ribbon (1) of optical fibers to form a pair of optical fibers; each pair of said optical fibers being fused together to form a thin integral portion (2c) in the longitudinally middle portion of said extent; the method comprising the steps of: removing said collective coating resin layers (1a) and said protection coating layers (2a) from the longitudinally middle portions of said optical fibers to expose glass portions (2b) thereof; opposing the exposed glass portions (2b) of each said pair of said optical fibers in parallel; fusing and elongating each said pair of exposed glass portions (2b) by heat to form a thin integral portion (2c); and collectively fixing a part of the exposed glass portions (2b) and the protection coating layers (2a) to said reinforcement member (3) with an adhesive layer (4) having the viscosity of 50 to 200 P before the cure of the adhesive. A method of manufacturing a multiple-optical-fiber coupler as claimed in Claim 1 characterized by the further steps of: initially removing from each of the first and second ribbons a length of said collective coating layer (1a) that is longer than the length of the protection coating layer (2a) that is to be removed from each optical fiber (2) and such that a length of said exposed protection coating layer (2a) of each optical fiber (2) remains exposed adjacent each end of its respective exposed glass portion (2b). A method of manufacturing a multiple-optical-fiber coupler as claimed in Claim 1 or Claim 2 and including the step of adhesively fixing the collective coating layer (1a) of each ribbon (1) to said reinforcement member (3) by means of an adhesive layer (5) that is softer than the adhesive layer (4) that is used to secure the protection coating layer (2a) and glass portion (2b) of each optical fiber (2) to the reinforcement member (3). A method as claimed in Claim 1, characterized in that said adhesive layer (4) additionally has thermosetting property and ultraviolet cure property. A method as claimed in Claim 3, characterized in that said softer adhesive layer (5) is an adhesive having thermosetting property and ultraviolet cure property.

Inventors: HATTORI TOMOYUKI, ISHIGURO YOICHI, KOBAYASHI YUJI, SASAOKA EISUKE, SEMURA SHIGERU, SUGANUMA HIROSHI, TAKIMOTO HIROAKI, WAKINOSONO TOSHIYUKI, HATTORI, TOMOYUKI, ISHIGURO, YOICHI, KOBAYASHI, YUJI, SASAOKA, EISUKE, SEMURA, SHIGERU, SUGANUMA, HIROSHI, TAKIMOTO, HIROAKI, WAKINOSONO, TOSHIYUKI, HATTORI, TOMOYUKI, YOKOHAMA WORKS OF SUMITOMO, ISHIGURO, YOICHI, YOKOHAMA WORKS OF SUMITOMO, KOBAYASHI, YUJI, YOKOHAMA WORKS OF SUMITOMO, SASAOKA, EISUKE, YOKOHAMA WORKS OF SUMITOMO, SEMURA, SHIGERU, YOKOHAMA WORKS OF SUMITOMO, SUGANUMA, HIROSHI, YOKOHAMA WORKS OF SUMITOMO, TAKIMOTO, HIROAKI, YOKOHAMA WORKS OF SUMITOMO, WAKINOSONO, TOSHIYUKI, YOKOHAMA WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1994
Main classification: G02B6
IPC codes: G02B6