ETHERIFIED ALKYL OR ARYLCARBAMYLMETHYLATED AMINOTRIAZINES AND CURABLE COMPOSITIONS CONTAINING THE SAME

Abstract: Novel carbamyl-methylated aminotriazines and curable compositions comprising these aminotriazines are disclosed. The carbamyl-methylated aminotriazines are substituted with derivatives of monoalkyl ethers and/or monoaryl ethers of alkylene glycols. The curable compositions are particularly useful as film formers in coatings.

Description: ETHERIFIED ALKYL OR ARYLCARBAMYLMETHYLATED AMINOTRIAZINES AND CURABLE COMPOSITIONS CONTAINING THE SAME Field of the Invention The present invention relates to novel triazines and to curable compositions containing such materials. More particularly, the present invention relates to novel carbamyl-methylated aminotriazines and to curable compositions comprising these novel aminotriazines. Background of the Invention The incorporation and use of carbamyl-substituted aminotriazines in curable compositions is known in prior art. For example, see U.S. Patent Number 4,708,984, and U.S. Patent Number 4, 710,542. The above compositions, for the most part, have limited compatibility with organic solvents and often require formulations with high solvent contents. Additionally, the coatings deposited with such compositions often give cured films which are deficient in coating properties such as gloss, flow, flexibility and impact resistance. Also, such coatings require a high curing temperature of 232°C or higher. The present invention overcomes certain of the above shortcomings by providing novel carbamylmethylated aminotriazines which, when formulated into curable compositions, provide coatings with good gloss and flow characteristics, are hard yet flexible and have good impact resistance. Coatings made with such compositions can be prepared with relatively low curing temperatures of 176°C or lower. Additionally, the novel compositions offer a broad range of compatibility with organic solvents, and coatings formulations with low solvent contents can be formulated. The novel compositions can also be formulated as aqueous dispersions which can be used in electrodeposition applications . Summary of the Invention According to the present invention, there are provided triazines selected from the group consisting of (i) a triaminotriazine compound of the formula C3N6 (CH20R) 6 -χ(CH 2 NHCOOR' ) x ; (ii) a benzoguanamine compound of the formula C3N5(C6H5) 'CH2OR) -y(CH2NHCOOR' ) y ; (iii) an oligomer of (i) or of (ii); (iv) mixtures among various members of (i) , (ii) and (iii) wherein the R and R' are independently radicals derived from monoalkyl ethers of alkylene glycols having at least 4 carbon atoms and monoaryl ethers of alkylene glycols having at least 8 carbon atoms; alone or combined with alkyl groups having 1 to 20 carbon atoms where x is in the range of from about 2 to about 6, and y is in the range of from about 2 to about 4. Also contemplated by the present invention are curable compositions comprising the triazines described above and an active hydrogen-containing material. Coatings deposited from these compositions upon curing possess good gloss and flow characteristics as well as good flexibility and impact resistance while providing hard films. Such coatings will have the added benefit of low curing temperatures and offer a broad range of compatibility with organic solvents. In addition, coatings formulations with low solvent contents can be obtained. The compositions can be dispersed in aqueous mediurr. to form aqueous-based coating compositions. Such properties make these compositions well suited for use in coil coatings, extrusion coatings, can coatings and electrodeposition coatings. Detailed Description of the Invention The preferred embodiments of invention are triaminotriazines of the formula C3 6 (CH2OR) g_ x (CH2NHCOOR' ) x and of the benzoguanamine formula C3N5(C6H 5 ) (CH OR) 4-y(CH2NHCOOR • ) y : R and R 1 are independently radicals derived from monoalkyl ethers of alkylene (including polyalkylene) glycols having at least 4, more preferably 4-12 carbon atoms and monoaryl ethers of alkylene (including polyalkylene) glycols having at least 8, preferably from 8-12 carbon atoms. For example, in the case of the monomethyl ether of propylene glycol, R and R 1 are CH 3 I CH3O - CH 2 - CH - . In the case of the monophenyl ether of diethylene glycol, R b i l alkylene oxy groups) and aryloxy substituted alkylene (including alkylene oxy) groups. Preferably, the alkoxy group contains 1 to 10 carbon atoms, the aryloxy group contains 6 to 10 carbon atoms and the alkylene (including the alkylene oxy group) contains 2 to 6 carbon atoms. Preferably, X is in the range of about 3 to 6 carbon atoms, and y is in the range of about 3 to 4 carbon atoms. Preferred alkylene glycols are ethylene glycol, propylene glycol, diethylene glycol and dipropylene glycol. Preferred monoaryl and monoalkyl substituents are phenyl, methyl, propyl, butyl and hexyl groups. R and R' can be mixed groups and can also include alkyl groups of about 1 to 20 carbon atoms. Preferred alkyl substituents are of 1-4 carbon atoms, such as methyl and butyl groups. As starting materials to produce the alkyl or aryl carbamylmethylated triazines of this invention, there can be used hydroxymethyl or alkoxymethyl melamines and/or benzoguanamines and oligomers thereof known in the art. Many of these starting materials are commercially available or can be made by well known procedures. The melamine or benzoguanamine compounds are reacted with glycol ether carbamates, such as methoxypropyl carbamate and butoxyethyl carbamate, alone or in combination with alcohols and alkylcarbamates . The glycol ether carbamates are prepared by reacting glycol ethers, such as the monoalkyl and monoaryl ethers of alkylene glycols such as those mentioned above, with urea in the presence of a transesterification catalyst such as tin, nickel or lead by methods well known in the art. An idealized reaction equation for the preparation of the new compounds from an alkoxymethylmelamine or a hydroxymethylmelamine and glycol ether carbamates is as follows : C3N6(CH2θR)6 + XH2NCOOR' H+ > C3N6 (CH 2 OR) 6-x (CH2NHCOOR' ) x + xROH wherein R, R' and x are defined above. The mole ratio of melamine compound to glycol ether carbamate is selected to provide the desired degree of substitution. Preferably, from 3 to 6 moles of glycol ether carbamate can be used per 1 mole of melamine compound. If less than 3 moles of carbamate are used, per mole of melamine compound, premature gelation can be a problem. This chemical reaction is typically carried out by heating in the melt or in solution. With the benzoguanamine starting material, the preferred mole ratio of glycol ether carbamate to benzoguanamine starting material is 3 to 4/1 (i.e. y = 3-4 for the benzoguanamine compound shown in the structural formula) . The reaction temperature can range from 70 to 125°C. The preferred temperature range is 95 to 115°C. The quantity of alcohol (ROH) evolved gives an indication of reaction completion. An acid catalyst such as methane sulfuric acid is usually present during the reaction. With 6 moles of glycol ether carbamate, the reaction is usually not 100% complete unless forced. However, a high degree of substitution, x = 5-6; (y = 3-4 with the benzoguanamine compound) is obtained. Preferably reaction is conducted in the presence of a high boiling alcohol such as methoxy propanol and butoxyethanol which bring about an etherification or transetherification reaction with the starting melamine or benzoguanamine compound. It is noted that the resulting carbamylmethyl aminotriazine products tend to be oligomeric. Gel permeation chromatography typically indicates the majority of the product is comprised of a distribution of oligomers. The triazines of the present invention can be used in combination with active hydrogen-containing materials, which are well known in the art, to form curable compositions. The active hydrogen-containing materials can have as the active hydrogen group a group selected from carboxylic acid hydroxy, amino (i.e. primary amine, secondary amine (including imine) ) , amido, and thiol including mixtures of such groups. The active hydrogen-containing materials useful herein are typically film-forming compositions. Examples of suitable active hydrogen-containing polymers are hydroxy functional acrylic polymer, hydroxy functional polyesters, hydroxy functional polyurethanes, hydroxy functional epoxy polymers and hydroxy functional epoxy-amine reaction product polymers including mixtures thereof . Useful hydroxyl-containing acrylic polymers are described in U.S. 4,913,972, col. 16, line 63 to col. 4, line 47; hydroxy functional polyesters are described in U.S. 4,913,972, col. 16, lines 9-62; hydroxy functional polyurethanes are described in U.S. 4,913,972, col. 17, line 62 to col. 18, line 7 and col. 15, line 35 to col. 16, line 8; hydroxy functional epoxies are described in U.S. 4,913,972, col. 17, lines 38-61 and hydroxy functional epoxy amine reaction products are described in U.S. 4,031,050, col. 3, line 23 to col. 5, line 8. These hydroxyl functional polymers typically have hydroxyl values of 50 to 400 on a resin solids basis. Generally, the curable compositions described above will contain at least 5 and preferably 20 to 100, percent by weight of aminotriazine and active hydrogen-containing polymer based on total weight of the curable composition. Preferably, the weight ratio of aminotriazine to active hydrogen-containing material will range from about 5 to about 40 parts to correspondingly from 60 to 95 parts of the active hydrogen-containing material. The curable compositions of the present invention can be solubilized or dispersed in organic solvents such as alcohols, esterε, or water or mixtures thereof. For solubilization or dispersion in water or mixtures of water and organic solvent, the polyester, polyurethane or acrylic polymers preferably contain carboxylic acid groups and are at least partially neutralized with amine to form anionic polymers. Epoxy-amine reaction product polymers can be neutralized with acid to form cationic polymers. The curable composition typically includes a cure catalyεt. The cure catalyst can be a metal salt and/or complex of a metal such as lead, zinc, iron, manganese, and preferably tin. Suitable salts of these metals are, for example, acetates, octoateε, laurateε and naphthenates . Specific examples include tetrabutyldiacetoxy distannoxane, dibutyltin dilaurate, dibutyltin oxide and tin acetyl acetonate complex. The cure catalyst is used in amounts effective to accelerate cure at the temperatures employed, e.g., 120 to 400°C, preferably 150 to 360°C for 30 seconds to 30 minutes. Typically, the catalyst is used in amounts from about 0.1 to about 2.0, preferably 0.2 to 1.7%, metal by solids weight based on the weight of the curable compositions. Acid catalysts can also be used when the aminotriazine compounds of the present invention contain ether functional groups. Example of εuch catalysts include nitric acid, εulfuric acid, p-toluenesulfonic acid and the like. Where used, the acid catalyεt is present in amounts of 0.1 to 2.0 percent by weight based on weight of the curable composition. Preferably, the combination of a tin catalyst and an acid catalyst iε uεed. Beεideε the above-mentioned ingredientε, the compoεitions can optionally contain pigments and various conventional additives εuch aε antioxidants, surface active agentε, flow control agents and the like. The following exampleε illustrate the triazines and curable compositions of the present invention and are not to be construed as limiting the claims unless otherwise indicated. All parts are by weight unless otherwise indicated. EXAMPLE 1 Reaction Product of 6 Moles of Methoxypropyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (180. Og, 0.46 mole, American Cyanamid Co. CYMEL 303), methoxypropyl carbamate (370. Og, 2.78 mole) , and methanesulfonic acid (1.10g) are stirred at 100°C in a flask equipped with a Dean Stark distillation trap and a nitrogen sparge inlet. Over 3 to 4 hours 64g of methanol (72% of theoretical) are collected in the receiver. Methoxypropyl acetate (150g, Dow Chemical Co, PM Acetate) is added and the temperature is increased to 115°C at which time more methanol is collected. After cooling the reaction to 80°C, the acid is neutralized with dimethyl ethanolamine (1.10g) . Sufficient PM Acetate (75g) is added to achieve a Gardner-Holdt viscosity of Z to Zl. The resulting clear, colorlesε resin (695g) is measured at 73.9% total nonvolatiles (110°C, 60 minutes) . Gas chromatographic analysis shows about 9% residual carbamate by peak area, corresponding to a slight excess of five (on average) methoxy groups being replaced by the methoxypropyl carbamate groups . The approximate formula is: C 3 N 6 (CH2OCH3) o- l (CH2NHCOOCH(CH3) CH2OCH3) 5- 6 Gel permeation chromatography shows a fairly uniform distribution of oligomeric material (about 78%, M w 5476) and a single peak corresponding to monomeric material . EXAMPLE 2 Reaction Product of 3 Moles of Methoxypropyl Carbamate and 2 Moles of Methoxypropanol with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (200. Og, 0.51 mole) , methoxypropyl carbamate (205. Og, 1.54 mole) , methoxypropanol (137.0g, 1.52 mole, Dow Chemical Co. DOWANOL PM) , and methanesulfonic acid (l.OOg) are stirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 3 hours 55g of methanol (67% of theoretical base upon the number of moles of carbamate and hydroxyl present) is collected in the receiver. Dimethyl ethanolamine (l.OOg) is added to neutralize the acid catalyst. The resulting clear, colorless reεin iε meaεured at a Z Gardner-Holdt viεcoεity and 71.6% total nonvolatiles (110°C, 60 minutes) . Gaε chromatographic analyεis showε <1% reεidual carbamate and about 25% reεidual DOWANOL PM meaning only a minimal amount of the secondary alcohol reacts. The approximate formula is: C3N6 (CH2OCH3) 2-3 (CH2NHCOOCH(CH3) CH2OCH3) 3 (CH2OCH(CH3) CH2OCH3) 0-1 Gel permeation chromatography shows a fairly uniform distribution of oligomeric material (about 70%, M 3200) and a single peak corresponding to monomeric material. EXAMPLE 3 Reaction Product of 3 Moles of Methoxypropyl Carbamate with 1 Mole of Hexamethoxymethylmelamine in Excess 2-Butoxyethanol Oligomeric hexamethoxymethylmelamine (200. Og, 0.51 mole) , methoxypropyl carbamate (205g, 1.54 mole), 2-butoxyethanol (250. Og, 2.12 mole, Union Carbide Co. Butyl CELLOSOLVE), and dodecylbenzenesulfonic acid (2.60g, 70%) are stirred at 110°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 3.5 hours 70g of methanol (87% based upon εix reactive εiteε) iε collected in the receiver, and the acid catalyεt is neutralized with dimethyl ethanolamine (2.60g) . The flask is then fitted with a vacuum distillation receiver, and the presεure is slowly reduced to 100mm Hg to diεtill a portion of the butyl CELLOSOLVE. About 50g of distillate is collected, and the resulting clear, slightly yellow resin is measured at a Zl Gardner-Holdt viεcosity and 75.8% total nonvolatiles (110°C, 60 minutes) . Gas chromatographic analysiε shows <1% reεidual carbamate. The approximate formula iε: C 3 N6(CH2θCH3) 0-3 (CH2NHCOOCH (CH3) CH2OCH3) 3 (CH2OCH2CH2OCH3) 0 -3 Gel permeation chromatography shows a fairly uniform distribution of oligomeric material (about 75%, M 2230) and a single peak correεponding to monomeric material. EXAMPLE 4 Reaction Product of 5 Moles of Butoxypropyl Carbamate wi h 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (445. Og, 1.14 mole), butoxypropyl carbamate (1000. Og, 5.7 mole) , and methanesulfonic acid (1.50g) are stirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 2 hours 120g of methanol (66% of theoretical) is collected in the receiver. PM Acetate (250g) is added and the temperature is increased to 115°C at which time 20g more methanol is collected (77% total) . Sufficient PM Acetate (50g) is added to achieve a Gardner-Holdt viscosity of Zl. The resulting clear, pale yellow resin (1545g) is measured at 68.0% total nonvolatiles (110°C, 60 minutes) . Gas chromatographic analysiε shows <1% residual carbamate. The approximate formula iε : C3N6 (CH2OCH3) (CH2NHCOOCH(CH3)CH2θC4H9) 5 Gel permeation chromatography shows a uniform distribution of oligomeric material (about 75%, M 6027) and a single peak correεponding to monomeric material. EXAMPLE 5 Reaction Product of 5 Moles of Propoxypropyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (295. Og, 0.76 mole), propoxypropyl carbamate (620. Og, 3.8 mole), and methanesulfonic acid (1.80g) are stirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 4 hours 75g of methanol (63% of theoretical) are collected in the receiver. PM Acetate (lOOg) iε added and the temperature is increased to 115°C at which time 25g more methanol iε collected (83% total) . Sufficient PM Acetate (lOOg) is added to achieve a Gardner-Holdt viscosity of Y. The resulting clear, pale yellow resin is measured at 67.0% total nonvolatiles. Gas chromatographic analysis shows <1% residual carbamate. The approximate formula is: C3N6 (CH2OCH3) 1 (CH2NHCOOCH(CH3) CH2OC3H7) 5 EXAMPLE 6 Reaction Product of 6 Moles of 2-Butoxyethyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (121. Og, 0.31 mole), 2-butoxyethyl carbamate (300. Og, 1.36 mole) , and methanesulfonic acid (0.34g) are stirred at 100°C in a flask equipped with a Dean Stark distillation trap and a nitrogen sparge inlet. Over 4 hours 35g of methanol (62% of theoretical) are collected in the receiver. Butyl CELLOSOLVE (75g) iε added and lOg more methanol (79% total) iε collected over 2 hours. The resulting clear, amber resin is measured at 77.1% total nonvolatiles (110°C, 60 minutes) with a Gardner-Holdt viscosity of Z. Gas chromatographic analysiε shows about 9% residual carbamate correεponding to a slight excesε of five (on average) methoxy groups being replaced by carbamate groups. The approximate formula is: C3N6 (CH2OCH3) o-l (CH2NHCOOCH2CH2OC 4 H9) 5-6 EXAMPLE 7 Reaction Product of 3 Moleε of 2-Butoxyethyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (160. Og, 0.41 mole), 2-butoxyethyl carbamate (200. Og, 1.24 mole) , and para-tolueneεulfonic acid (0.72g) are εtirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 5 hours 35g of methanol (90% of theoretical) are collected in the receiver. Butyl CELLOSOLVE (lOOg) is added to achieve a Gardner-Holdt viscosity of Zl. The resulting clear, yellow resin is measured at 81.4% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C3N6 (CH2θCH3)3 (CH2NHCOOCH2CH20C4H9)3 EXAMPLE 8 Reaction Product of 6 Moleε of Diethylene Glycol Butyl Ether Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (200. Og, 0.51 mole), diethylene glycol butyl ether carbamate (630. Og, 3.06 mole) , and methanesulfonic acid (2.0g) are stirred at 110°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 6 hours 85g of methanol are collected (89% of theoretical) in the receiver. The resulting yellow resin is measured at 92.0% total nonvolatiles (110°C, 60 minutes) with a Gardner-Holdt viεcoεity of Z4. The approximate formula iε: C3N6 (CH2OCH3) 0-1 (CH2NHCOOCH2CH2θCH2CH2θC4H9)5-6 EXAMPLE 9 Reaction Product of 3 Moleε of Diethylene Glycol Butyl Ether Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (185.0g, 0.47 mole) , diethylene glycol butyl ether carbamate (300. Og, 1.46 mole), and methanesulfonic acid (0.50g) are εtirred at 95°C in a flask equipped with a Dean Stark diεtillation receiver and a nitrogen εparge inlet. Over 4 hours 40g of methanol (89% of theoretical) are collected in the receiver. The resulting yellow resin is measured at 98% total nonvolatiles (110°C, 60 minutes) with a Gardner-Holdt viscoεity of Z2. Gaε chromatographic analyεiε shows no residual carbamate. The approximate formula is: C 3 N6 (CH2OCH 3 ) 3 (CH2NHCOOCH2CH 2 θCH2CH2θC 4 H9)3 EXAMPLE 10 Reaction Product of 5 Moles of Diethylene Glycol Butyl Ether Carbamate with 1 Mole of Hexamethoxymethylmelamine in Diethylene Glycol Monobutyl Ether Oligomeric hexamethoxymethylmelamine (120.0g, 0.31 mole), diethylene glycol butyl ether carbamate (320. Og, 1.55 mole), diethylene glycol monobutyl ether (130. Og, 0.80 mole, Union Carbide Co., Butyl CARBITOL) , and methanesulfonic acid (1.40g) are stirred at 115°C in a flask equipped with a Dean Stark diεtillation receiver and a nitrogen sparge inlet. Over 3.5 hours 42g of methanol (86% of theoretical) are collected in the receiver, at which time dimethyl ethanolamine (1.40g) is added to neutralize the acid catalyst. The resulting pale yellow resin is filtered and is measured at 81.4% total nonvolatiles with a Gardner-Holdt viscoεity of V. Gas chromatographic analysis shows <1% residual carbamate. The approximate formula is : C3N6 (CH2OCH3) 0-1 (CH2NHCOOCH2CH2OC4H9) 5 (CH2OCH2CH 2 OC 4 H9) o- l Gel permeation chromatography shows a uniform distribution of oligomeric material (about 85%, M w 8459) and a single peak corresponding to monomeric material. EXAMPLE 11 Reaction Product of 5 Moles of Dipropylene Glycol Methyl Ether Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (164.0g, 0.42 mole), dipropylene glycol methyl ether carbamate (400. Og, 2.09 mole), and methanesulfonic acid (1.20g) are εtirred at 95°C in a flask equipped with a Dean Stark diεtillation receiver and a nitrogen sparge inlet. Over 4 hours 44g of methanol (65% of theoretical) are collected in the receiver. PM Acetate (60.0g, Dow Chemical Co.) is added and the temperature is increased to 115°C to collect 8g more methanol (77% total) . Dimethyl ethanolamine (1.20g) is added to neutralize the acid catalyst, and sufficient PM Acetate (150g) is added to achieve a Zl Gardner-Holdt viscosity. The resulting pale yellow resin is measured at 78.4% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C3N6(CH2θCH3) (CH 2 NHCOOCH(CH3) CH2OCH (CH 3 ) CH2OCH3) 5 Gel permeation chromatography shows a uniform distribution of oligomeric material (about 80%, M 4270) and a single peak corresponding to monomeric material. EXAMPLE 12 Reaction Product of 5 Moles of 3-Methoxy-3-methylbutyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (60.0g, 0.15 mole), 3-methoxy-3-methylbutyl carbamate (125. Og, 0.77 mole) , and methanesulfonic acid (0.37g) are stirred at 100°C in a flask equipped with a Dean Stark diεtillation receiver and a nitrogen εparge inlet. Over 1 hour 19g of methanol (79% of theoretical) are collected in the receiver. Dimethyl ethanolamine (0.37g) iε added to neutralize the acid catalyεt followed by εufficient 3-methoxy-3-methyl-1-butanol (40g, Ken Seika Corp.) to achieve a Z2 Gardner-Holdt viscosity. The resulting clear, colorless resin is measured at 76.6% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C 3 N6 (CH2OCH3) 1 (CH2NHCOOCH2CH2C(CH3)20CH 3 ) 5 EXAMPLE 13 Reaction Product of 3.5 Moleε of Methoxypropyl Carbamate with 1 Mole of Dimethoxymethyldiethoxymethylbenzoguanamine Oligomeric dimethoxymethyldiethoxymethylbenzo- guanamine (250. Og, 0.65 mole, American Cyanamid Co., CYMEL 1123), methoxymethyl carbamate (260. Og, 1.95 mole) , and methanesulfonic acid (l.OOg) are stirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 2.5 hours 59g of a methanol/ethanol mixture (78% of theoretical) are collected in the receiver. PM Acetate (100. Og) iε added and the temperature iε increaεed to 115°C to collect 5g more distillate. Dimethyl ethanolamine (l.OOg) is added to neutralize the acid catalyεt. Sufficient PM Acetate (75. Og) is added to achieve a Gardner-Holdt viscosity of Zl. The resulting clear, yellow resin (575g) is measured at 66.5% total nonvolatiles (110°C, 60 minutes) . Gaε chromatographic analyεis shows <2% residual carbamate. The approximate formula is : C 3 N 5 ( C6H5 ) ( CH2θCH3 ) 0-0.5 ( CH2θCH 2 CH3 ) 0 -0.5 (CH2NHCOOCH(CH3)CH2θCH3) 3.5 Gel permeation chromatography showε a uniform distribution of oligomeric material (about 70%, M w 2357) and a single peak corresponding to monomeric material . EXAMPLE 14 Reaction Product of 3 Moles of Phenoxypropyl Carbamate with 1 Mole of Hexamethoxymethylmelamine in Excess Butanol Oligomeric hexamethoxymethylmelamine (180. Og, 0.46 mole), phenoxypropyl carbamate (250. Og, 1.38 mole) , n-butanol (300. Og, 4.0 mole) , and dodecylbenzenesulfonic acid (0.86g, 70%) are stirred at 100°C in a flaεk equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 5 hours 124g of a methanol/butanol mixture are collected in the receiver. Dimethylethanolamine (l.Og) is added to the neutralize the acid catalyst, and 44g of butanol are stripped under reduced pressure (100-200 mm Hg) . The resulting clear, pale yellow resin is measured at an X Gardner-Holdt viscosity and 84.5% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C 3 N 6 (CH2OCH3) 0-3 (CH 2 NHCOOCH(CH3)CH 2 OC6H5)3 (CH2OC 4 H 9 ) 0 -3 EXAMPLE 15 Reaction Product of 3 Moleε of Butyl Carbamate and 3 Moles of Methoxypropyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (109. Og, 0.43 mole), butyl carbamate (153. Og, 1.3 mole) , methoxypropyl carbamate (175. Og, 1.3 mole) , and methaneεulfonic acid (l.Og) are εtirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 4 hours 68g of methanol (82% of theoretical based upon the number of moles of carbamate present) are collected in the receiver. Dimethylethanolamine (l.Og) is added to neutralize the acid catalyst and sufficient PM Acetate (llOg) iε added to achieve a Gardner-Holdt viεcoεity of Z- . The resulting clear colorless resin is measured at 82.6% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C3N6 (CH2OCH3) o-l (CH2NHCOO(CH2)3CH3)2-3 (NHCOOCH (CH3) CH2OCH3) 2-3 EXAMPLE 16 Reaction Product of 5 Moles of Methoxypropyl Carbamate with 1 Mole of Monomeric Hexamethoxymethylmelamine at Reduced Pressure Monomeric hexamethoxymethylmelamine (195. Og, 0.5 mole, American Cyanamid Co. CYMEL 300) , methoxypropyl carbamate (333.3g, 2.5 mole) , and methaneεulfonic acid (1.2g) are εtirred in a flask equipped with a vacuum distillation head and purged with dry nitrogen. The temperature iε maintained at 85°C for 1 hour at which time the pressure is reduced to 200mm Hg. Over 4 hourε the pressure is gradually decreased to 50mm Hg. At this time gas chromatographic analysis showed <2% residual carbamate, and sufficient PM Acetate (150g) was added to achieve a Z- Gardner-Holdt viscosity. The resulting clear reεin was measured at 68.8% total nonvolatiles (110°C, 60 minutes) . EXAMPLE 17 Reaction Product of 5 Moleε of 2-Hexyloxyethyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (125. Og, 0.32 mole) , hexyloxyethyl carbamate (300.0g, 1.59 mole), and p-toluenesulfonic acid (0.9g) are εtirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 6 hours 50g of methanol are collected in the receiver at which time PM Acetate (90g) are added. The temperature is increased to 115°C for 2 hours and more methanol is collected. Dimethylethanolamme (0.5g) is added to neutralize the acid catalyst. The resulting clear, yellow reεin is measured at 66.8% total nonvolatiles (110°C, 60 minutes) with a Gardner-Holdt viscosity of X. The approximate formula is : C3N6 (CH2OCH3) 1 -2 (CH2θNHCOOCH2CH2θ(CH2)5CH 3 ) 4 -5 EXAMPLE 18 Reaction Product of 3 Moles of Methoxypropyl Carbamate and 3 Moles of Diethylene Glycol Butyl Ether Carbamate with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (129. Og, 0.33 mole) , methoxypropyl carbamate (133. Og, 1.0 mole), diethylene glycol butyl ether carbamate (290. Og, 70% in butyl CARBITOL, 1.0 mole) , and methaneεulfonic acid (l.lg) are εtirred at 110°C in a flaεk equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. Over 3 hours 58g of methanol (90% of theoretical based upon the number of moles of carbamate present) are collected in the receiver. Dimethylethanolamme (l.lg) is added to neutralize the acid catalyst. The resulting clear, pale yellow reεin is measured at 73.1% total nonvolatiles (110°C, 60 minutes) with a Gardner-Holdt viscosity of U+ . The approximate formula is: - I S C3N6(CH2OCH3 ) 0-l ( CH2NHCOOCH ( CH 3 ) CH 2 OCH3 ) 2-3 (CH2NHCOOCH2CH2OCH2CH2OC4H9) 2-3 EXAMPLE 19 Reaction Product of Ethylene Glycol 2-Ethylhexyl Ether Carbamate, Diethylene Glycol 2-Ethylhexyl Ether Carbamate and 2-Rutoxyethanol with 1 Mole of Hexamethoxymethylmelamine Oligomeric hexamethoxymethylmelamine (123.0g, 0.32 mole) , a mixture of ethylene and diethylene glycol 2-ethylhexyl ether carbamates (300. Og, 1.26 equivalents, carbamate of EKTASOLVE EEH, Eastman Chemical Co.) , 2-butoxyethanol (75. Og, 0.63 mole), and methanesulfonic acid (l.Og) are εtirred at 100°C in a flaεk equipped with a Dean Stark diεtillation receiver and a nitrogen sparge inlet. Over 4 hours 48g of methanol (80% of theoretical) are collected in the receiver at which time dimethylethanolamme (l.Og) is added to neutralize the acid catalyst. Sufficient 2-butoxyethanol (70g) is added to achieve a Gardner-Holdt viscoεity of Z. The resulting clear, pale yellow resin iε meaεured at 77.7% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C 3 N 6 (CH2OCH3) o- l (CH2OCH2CH2OC4H9) 1-2 (CH2NHCOO (CH2CH2O) 11 CH2CH(CH2CH 3 ) C 4 H 9 ) 4 n=l or 2. EXAMPLE 20 Reaction Product of 3.5 Moleε of Diethylene Glycol Butyl Ether Carbamate with 1 Mole of Dimethoxymethyldiethoxymethylbenzoguanamine Oligomeric dimethoxymethyldiethoxymethylbenzo- guanamine (150. Og, 0.39 mole, American Cyanamid Co., CYMEL 1123), diethylene glycol butyl ether carbamate (280. Og, 1.37 mole), diethylene glycol monobutyl ether (120. Og) , and methanesulfonic acid (1.5g) are stirred at 100°C in a flaεk equipped with a Dean Stark diεtillation receiver and a nitrogen sparge inlet. Over 6 hours 40g of methanol are collected in the receiver at which time dimethylethanolamine (1.5g) is added to neutralize the acid catalyεt. The resulting yellow resin iε measured at 65.9% total nonvolatiles with a Gardner-Holdt viscosity of H. The approximate formula is: C3N5 (C6H5) (CH2OCH3) 0-0.5 (CH2OCH2CH3) o-O .5 (CH2NHCOOCH2CH2OCH2CH2OC4H9) 3.5 COMPARATIVE EXAMPLE 1 Reaction Product of 5 Moles of Methyl Carbamate with 1 Mole of Hexamethoxymethylmelamine (see U.S. 4,710,542) Oligomeric hexamethoxymethylmelamine (260. Og, 0.66 mole), methyl carbamate (250. Og, 3.33 mole) , and methanesulfonic acid (l.Og) are εtirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen sparge inlet. After about 20 minutes the contents became extremely viscous and difficult to dissolve. Methoxypropanol (200g) was added and methanol (lOOg, 95% of theoretical) waε removed. Dimethylethanolamine (l.Og) was added to neutralize the acid catalyst, and sufficient methoxypropanol was removed at reduced presεure to achieve a Gardner-Holdt viscosity of Z. The resulting white, opaque resin is measured at 82.3% total nonvolatiles and is incompatible with a variety of organic εolventε and water. Gas chromatographic analysiε shows <2% reεidual carbamate. COMPARATIVE EXAMPLE 2 Reaction Product of 5 Moleε of Hydroxypropyl Carbamate with 1 Mole of Hexamethoxymethylmelamine Due to the fact that when thiε reaction is run neat or in the presence of a nonreactive solvent (i.e. toluene) , aε generally described in U.S. 4,708,984, gelation occurs within 2 hours at 85°C, the procedure has been amended. Oligomeric hexamethoxymethylmelamine (200. Og, 0.51 mole) , β-hydroxy-ethyl carbamate (305. Og, 2.56 mole), methanol (lOOg) , and p-toluenesulfonic acid (1.5g) are heated to reflux (72°C) in a flask fitted with a vacuum distillation receiver. The disappearance of hydroxypropyl carbamate iε monitored by gas chromatography. After 10 hours at reflux, the pressure is reduced in stages to 100 mm Hg to remove the methanol. Dimethylethanolamine (1.5g) is added to neutralize the acid catalyst, and sufficient methoxypropanol (150g) is added to achieve a Gardner-Holdt viscosity of Z2. The resulting clear, pale yellow resin iε measured at 77.3% total nonvolatiles (110°C, 60 minutes) . The approximate formula is: C 3 N 6 (CH2OCH 3 ) (CH2NHCOOCH2CH(CH3)OH) 5 Gel permeation chromatography shows a fairly uniform distribution of oligomeric material (about 70%, M w 2523) and a single peak corresponding to monomeric material . COMPARATIVE EXAMPLE 3 Reaction Product of 6 Moles of 2-Methoxyethyl Carbamate with 1 Mole of Hexamethoxymethylmelamine (see Organic Coatingε Science and Technology, XV, 379 (1989) Oligomeric hexamethoxymethylmelamine (132.3g, 0.34 mole), 2-methoxyethyl carbamate (200. Og, 1.68) , and methanesulfonic acid (0.63g) are stirred at 100°C in a flask equipped with a Dean Stark diεtillation receiver and a nitrogen sparge inlet. After 30 minuteε the contentε became very viscous and began to foam, so PM Acetate (50g) was added. Over 3 hours 68g of methanol (80% of theoretical) are collected in the receiver at which time dimethylethanolamine (0.63g) is added to neutralize the acid catalyst. Sufficient PM Acetate (25g) is added to achieve a Gardner-Holdt viscoεity of Z. The reεulting clear, yellow reεin iε meaεured at 66.6% total nonvolatiles (110°C, 60 minuteε) . The approximate formula is: C3N6 (CH2OCH3) (CH2NHCOOCH2CH2OCH3) 5 COMPARATIVE EXAMPLE 4 Reaction Product of 5 Moles of Octyl Carbamate with 1 Mole of Hexamethoxymethylmelamine (see U.S. 4.710,542) Oligomeric hexamethoxymethylmelamine (113.Og, 0.29 mole) , n-octyl carbamate (250. Og, 1.49 mole), and methanesulfonic acid (l.Og) are stirred at 100°C in a flask equipped with a Dean Stark distillation receiver and a nitrogen εparge inlet. Over 6 hourε 30g of methanol (65% of theoretical) are collected in the receiver at which time dimethylethanolamine (l.Og) iε added to neutralize the acid catalyεt. The resulting white opaque reεin is meaεured at 78.1% total nonvolatiles (110°C, 60 minuteε) with a Gardner-Holdt viεcoεity of X. The resin became extremely viscous with time. In the following examples, alkoxyalkylcarbamyl- methylated triazines of this invention are formulated into curable compositions and evaluated as coatings. EXAMPLE 21 A black paint was formulated from a methoxypropyl carbamate functional melamine crosslinker such as described in Example 1 (152g) , a cyclohexyl methacrylate functional acrylic polyol such as ACRYSET® UW-2818HS1 (235g, Nippon Shokubai, hydroxyl value = 70) , dibutyltin dilaurate (3.0g) , an ester/alcohol solvent blend (119g, PM Acetate, isopropanol) , and a carbon black millbase with a P/B ratio of 0.05. The resulting paint had an applied viscosity of 30" (#2 Zahn Cup, 77°F) , a density of 8.6 lb/gal, and 54.4% total theoretical nonvolatiles. It was applied via conventional air spray over steel panels with a cured elastomeric primer and baked at 390-400°F for 10 minutes. The properties of the cured coating are reported in Table 1 below. EXAMPLE 22 An indian red paint was formulated from a diethylene glycol butyl ether carbamate functional melamine crosslinker such as described in Example 10 (140g), a hydroxyl functional acrylic εuch aε ACRYSET® UW-2818HS1 (173g) , dibutyltin dilaurate (2.4g) , an eεter/alcohol solvent blend as in Example 21 (lOlg) , and an iron oxide millbase with a P/B ratio of 0.40. The resulting paint had an applied viscoεity of 30" (#2 Zahn Cup, 77°F) , a density of 8.6 lb/gal, and 61.4% total theoretical nonvolatiles. It was applied via conventional air spray over steel panels with a cured elastomeric primer and baked at 390-400°F for 10 minutes. The properties of the cured coating are reported in Table 1 below. EXAMPLE 23 (COMPARATIVE) As a comparative example, a clear coating composition waε formulated from a methyl carbamate functional melamine crosslinker such aε described in Comparative Example 1 (105g) , a hydroxyl functional acrylic such aε ACRYSET® UW2818HS1 (175g) , dibutyltin dilaurate (2.0g) , and an eεter/alcohol blend (lOOg) . The resulting formulation was hazy and appeared to have compatibility problemε . It had a measured viscosity of 30" (#2 Zahn Cup, 77°F) and 58% total theoretical nonvolatiles. It was drawn down over primed steel panels and baked at 400°F for 10 to 20 minutes. The clear coating did not give a well cured film, so many of the physical properties of the cured coating could not be meaεured. What properties could be measured are reported in Table 1 below. TABLE I PROPERTIES 21 22 22 DFT (Dry Film Thickness, mil) 1.2 1.2 1.2 60° Gloss 1 90 64 - Pencil Hardness 2 H H <6B MEK Double Rubs 3 100+ 100+ 10 Impact :Direct 4 60+ 60+ - Impact :Reverse 4 (Rl) 60+ 60+ - Adhesion 5 : 30' Boiling Water (BWT) 5 5 - Adhesion: 30' BWT+30in/lb Rl 4+ 4+ - Adhesion: 24hr H 2 0 Soak 5 5 - Detergent Resiεtance 6 Excellent Excellent - 10% Hydrochloric Acid Resistance 7 Excellent Excellent - 5% Salt Spray:3000hr. 8 Excellent Excellent - QUV:3000hr (% gloss retention) 9 >90% >90% _ 1 Specular Glosε measured in accordance with ASTM D523-89. 2 Pencil Hardnesε was determined by taking sharpened pencils of increasing hardness (6B to 5H) and attempting to etch a scribe mark in the coating. The next softest pencil which will etch the coating is reported as the pencil hardness (ASTM D-3363) . 3 Number of rubs back and forth (l double rub) with a cloth saturated with methyl ethyl ketone using normal hand presεure required to remove the coating from the εubεtrate. Limit of the teεt iε 100 double rubε . 4 Impact Reεiεtance was measured with a Gardner Impact Teεter (4 lb, 5/8" ball) . The reεults are reported in inch-pounds, 0.10 inch deformation, no tape-off. 5 Adhesion: Panel was croεεhatched at 1/16" and evaluated with Scotch 610 tape. Reported on a scale of 0 to 5 (best) . 6 Detergent Resiεtance: 72 hour immerεion in 3% εolution of detergent in distilled water at 100°F. 7 10% Hydrochloric Acid Resistance: 15 minute covered spot test. 8 Salt Spray: 3000 hour (scribed) at 95°F and 5% salt solution (ASTM D-117) . 9 QUV Exposure is determined by exposing the coated panels to alternating cycles of U.V. light and condensing humidity in a Q-U-V Accelerated Weathering Tester manufactured by the Q-Panel Co. The U.V. light iε generated with a UVB313 lamp (320-280nm) . The temperature of the light cycle iε 70°C. The temperature of the condensing humidity is 50°C. EXAMPLE 24 A musket brown waterborne dispersion waε prepared uεing a croεεlinker prepared from 5 moleε of butoxypropyl carbamate and 1 mole of hexamethoxymethylmelamine such as that of Example 4. A pigment grind was prepared from a εolventborne acrylic grind vehicle containing εtyrene, butyl acrylate, methyl methacrylate, and acrylic acid (7.9g, 40% solids, acid value = 30), butyl CARBITOL ® (1.5g) , ethylene glycol (5.3g) , triethylamine (0.5g) , and 16.6g of a pigment mixture of carbon black, iron oxide, light sienna, and titanium dioxide (Weight Ratio 1:1.6:2.5:2.3) . To thiε, the carbamate/melamine crosslinker (15.9g) was added at high shear to form the grind paste. The paste waε then added with agitation to an acrylic emulsion containing methyl methacrylate, butyl acrylate, acrylic acid, and hydroxyethyl acrylate (170.0g, 50% solids, hydroxyl value = 10) and appropriate surfactantε. The resulting paint had a P/B ratio of 0.17 at 48.0% total nonvolatiles. It waε applied over elastomerically primed aluminum panels and baked for a 35 second dwell at 520°F (to 420°F peak metal temperature) . The propertieε of the cured coating are reported in Table 2 below. EXAMPLE 25 A musket brown waterborne dispersion was prepared using a crosslinker prepared from 6 moles of diethylene glycol butyl ether carbamate and 1 mole of hexamethoxymethylmelamine such aε that of Example 10. The carbamate/melamine crosslinker (12.8g) was used to prepare the pigment grind in a manner similar to that of Example 24. The resulting paste was added with agitation to 170. Og of the acrylic emulsion deεcribed in Example 24. The reεulting paint had a P/B ratio of 0.17 at 47.5% total nonvolatileε . It waε applied over elaεtomerically primed aluminum panels and baked for a 35 second dwell at 520°F (to 420°F peak metal temperature) . The properties of the cured coating are reported in Table 2 below. TABLE 2 PROPERTIES 2A 22 Pencil Hardnesε HB HB MEK Double Rubs 100 100 T-Bend Adhesion 1 No Pick 2T 2T No Crack 3T 2T 1 The film waε evaluated for cracking and adheεion loss after the coated panel was bent over itself to varying degrees. The film is observed at the edges for cracking and for removal of the film when a piece of adhesive tape is pressed down onto the edge and then quickly ripped from the film. The value iε aεεigned at the loweεt point where cracking or adhesion losε iε not obεerved. A 3T rating meanε that the diameter of the bend is 3 times the thickness of the panel. A 2T bend means that the diameter of the bend is 2 times the thicknesε and εo on. A 0T bend meanε that the panel is bent back over itself and compreεεed flat. EXAMPLE 26 A high solids clear coating composition waε formulated from a crosslinker prepared from 3 moleε of methoxypropyl carbamate, 3 moles of butyl carbamate, and 1 mole of hexamethoxymethylmelamine as described in Example 15 (46.Og), a low molecular weight polyester prepared from sebacic acid and propylene oxide (23.2g, hydroxyl value = 228, 99.8% solidε) , dibutyltin dilaurate (0.9g), and PM Acetate (5.0g) . The reεulting clear had an applied viεcoεity of 20 εecondε (#4 Zahn Cup) and waε drawn down over unprimed εteel panels. The films were baked at 350°F for 20 minutes. The properties of the cured coating are reported in Table 3 below. EXAMPLE 27 A high solidε clear coating composition was formulated from a crosslinker prepared from 3 moles of butoxyethyl carbamate and 1 mole of hexamethoxymethylmelamine as described in Example 7 (38.2g) , the polyester used in Example 26 (23.2g), dibutyltin dilaurate (0.92g), and PM Acetate (7.6g) . The resulting clear had an applied viscosity of 20 secondε (#4 Zahn Cup) and waε drawn down over unprimed steel panels. The films were baked at 350°F for 20 minutes. The properties of the cured coating are reported in Table 3 below. EXAMPLE 28 A high εolids clear coating composition was formulated from a crosεlinker prepared from 3.5 mole of methoxypropyl carbamate and 1 mole of dimethoxymethyl- diethoxymethylbenzoguanamine aε deεcribed in Example 13 (39. Og) , the polyester uεed in Example 26 (23.2g) , dibutyltin dilaurate (0.90g), and PM Acetate (5.2g) . The resulting clear had an applied viscosity of 20 seconds (#4 Zahn Cup) and was drawn down over unprimed steel panelε. The filmε were baked at 350°F for 20 minutes. The properties of the cured coating are reported in Table 3 below. EXAMPLE 29 (COMPARATIVE) As a comparative example, a clear coating composition was formulated from the methoxyethyl carbamate functional crosεlinker described in Comparative Example 3 (49.5g), the polyester used in Example 26 (23.2g) , dibutyltin dilaurate (0.95g), and PM Acetate. The resulting clear had an applied viscoεity of 20 seconds (#4 Zahn Cup) and was drawn down over unprimed εteel panelε. The filmε were baked at 350°F for 20 minuteε. The propertieε of the cured coating are reported in Table 3 below. TABLE 3 PROPERTIES 26 27 28 23 % Solids 80.9 78.6 76.3 71.0 DFT (mils) 1.3 1.2 1.2 1.15 Pencil Hardneεε H F-H 2B F MEK Double Rubε 100 100 100 100 Impact :Direct >160 100 100 160 Impact :Reverεe >160 90 90 140 EXAMPLE 30 An aqueous dispersion of a cationic reεin and the croεεlinker of Example 8 was prepared from the following ingredients: Ingredientε Parts by Weight EPON 828 3850.2 Bisphenol A/Ethylene Oxide 1370.7 Adduct (1/6 molar ratio) Bisphenol A 1116.2 Methyl Isobutyl Ketone 333.5 Benzyldimethylamine 5.6 Benzyldimethylamine 15.2 Diketamine 1 399.0 N-Methylethanolamine 345.3 Methyl Isobutyl Ketone 564.3 1 Diketamine derived from diethylenetriamine and methyl isobutyl ketone (73% solidε in methyl isobutyl ketone) . The EPON 828 (diglycidyl ether of bisphenol A available from Shell Chemical Co.), bisphenol A/ethylene oxide adduct, bisphenol A and methyl isobutyl ketone (first portion) were charged to a reaction vessel and heated under a nitrogen atmosphere to 140°C. The first portion of the benzyldimethylamine was added, and the reaction mixture waε allowed to exotherm while any water preεent waε removed azeotropically. The reaction mixture waε cooled to 160°C, held for hour, cooled to 145°C, and the εecond portion of benzyldimethylamine added. The reaction was held until a reduced Gardner-Holdt viscoεity (50% resin εolidε in 2-methoxypropanol) of R to S was obtained. At this point the diketamine and N-methylethanolamine were added in succeεεion. The mixture waε allowed to exotherm and then a temperature of 125°C waε established. After 1 hour at 125°C, the second portion of methyl isobutyl ketone was added to the reaction mixture. To 685.5g of the resin aε deεcribed above waε added 400g of the crosslinker of Example 8. This mixture waε held at 110°C for 15 minutes at which time sulfamic acid (29.3g) and deionized water (29.3g) were added. The temperature was maintained at 60-65°C, and the mixture waε reduced in stages with deionized water to 33.0%. The resin possesεed the following measured propertie : MEq Acid = 0.109, MEq Base = 0.215, Particle Size = 1770A, Mw = 21936. A cationic electrodeposition bath was formulated with the aqueous dispersion prepared above and other ingredients as follows : Ingredient Parts by Weight Aqueous Dispersion 1851.2 Flow Control Agent 1 119.1 Plasticizer 2 41.7 Pigment Paste 3 221.5 Deionized Water 1566.5 *** The flow control agent iε a polyepoxide- polyalkylenediamine adduct prepared as generally described in Example A of U.S. 4,933,056. 2 Plasticizer available from Rohm and Haas Company as PARAPLEX WP-1. 3 Pigment paste available from PPG Industries, Inc. aε E-6064, containing 27.2% titanium dioxide, 1.4% carbon black, 15.9% aluminum εilicate, 5.7% basic lead silicate, and 3.8% dibutyltin oxide. The aqueous dispersion, flow control agent, and plasticizer were mixed together for 30 minutes. The pigment paste was then added with agitation, followed by the deionized water. The electrodeposition bath had a solids content of 22% and a pH of 6.97. Phosphated εteel panels were electrodeposited in the bath at 200 volts to a thicknesε of 1.2 milε. The coatingε were cured at 360°F (182°C) for 30 minutes and were resistant to 100 acetone double rubs. The cured films had good humidity and chip resiεtance.

Claims: WHAT IS CLAIMED IS: A triazine selected from the group consisting Of; (a) a triaminotriazine compound of the formula C3N6(CH 2 OR)6-χ(CH2NHCOOR' ) x (b) a benzoguanamine compound of the formula C3N5(C6H 5 ) (CH2-OR)4-y(CH 2 NHCOOR' ) y ; (c) an oligomer of (a) or (b) including mixtures thereof wherein the R and R* are independently radicals derived from monoalkyl ethers of alkylene glycolε having at least 4 carbon atomε and monoaryl ethers of alkylene glycols having at least 8 carbon atoms; alone or combined with hydrogen or alkyl groups having 1 to 20 carbon atoms; x iε in the range of from about 2 to about 6 and y iε in the range of from about 2 to about 4. 2. The triazine compound of claim 1 in which R and R' are derived from monoalkyl etherε of alkylene glycolε having from 4 to 12 carbon atomε alone or combined with alkyl groups having 1 to 4 carbon atomε . 3. The triazine compound of claim 2 in which R and R 1 are derived from monoalkyl ethers of propylene glycol, diethylene glycol and dipropylene glycol . 4. The triazine compound of claim l wherein x is in the range of about 3 to 6 an y iε in the range of about 3 to 4. 5. A curable composition comprising: (a) the triazine compound of claim 1 ; (b) an active hydrogen-containing material. 6. The curable composition of claim 5 in which the active hydrogen-containing material iε a polymeric material in which the active hydrogenε are εelected from the group consiεting of carboxylic acid, hydroxy, amino, amido, thiol or mixtures of such groups . 7. The curable composition of claim 5 in which the active hydrogen-containing polymeric material is selected from the group consisting of hydroxy functional acrylic polymers, hydroxy functional polyeεters, hydroxy functional polyurethanes, hydroxy functional epoxy polymers and hydroxy functional epoxy-amine reaction product polymers including mixtures thereof . 8. The curable compoεition of claim 5 which includeε a cure catalyst. 9. The curable composition of claim 8 in which the cure catalyst is selected from the class consisting of a tin catalyst alone or in combination with an acid catalyεt. 10. The curable compoεition of claim 5 in which components (a) and (b) are dispersed or εolubilized in water or mixtureε of water and organic εolvent. 11. The curable compoεition of claim 5 in which (a) and (b) are present in amounts of at least 5% by weight based on total weight of the compoεition. 12. The curable composition of claim 5 in which the weight ratio of (a) to (b) is from 5-40 to 95-60.

Inventors: MCCOLLUM GREGORY JAMES, RARDON DANIEL EDWARD, MCCOLLUM, GREGORY, JAMES, RARDON, DANIEL, EDWARD
Applicants: PPG INDUSTRIES INC, PPG INDUSTRIES, INC.
Application year: 1994
Main classification: C07D251
IPC codes: C07D251, C08G12, C08G18, C08G59, C08K5, C08L33, C08L67, C08L101, C09D201