Curable organopolysiloxane composition containing adhesion promoter

Abstract: There is disclosed a curable organopolysiloxane composition suitable for forming an adherent coating on metals which is durable under acidic conditions, said composition comprising: (A) an organopolysiloxane that contains at least 2 alkenyl groups in each molecule; (B) an organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule; (C) an adhesion promoter; and (D) a hydrosilylation catalyst, said composition is characterized in that the adhesion promoter is prepared by reacting (a) an amine compound with the general formula R n NH (3 - n) in which R denotes a monovalent hydrocarbon group and n is 1 or 2, and (b) an aliphatically unsaturated epoxy compound, and, optionally, condensing the above reaction product with (c) a silicon compound that contains at least two silicon-bonded alkoxy groups in each molecule.

Description: The invention relates to a curable organopolysiloxane composition containing a novel adhesion promoter which imparts an adhesive character to the composition which is durable under acidic conditions. Addition reaction-curing organopolysiloxane compositions cure relatively rapidly at room temperature or when heated. For this reason, they have been broadly examined as protectants for metal surfaces. These compositions are typically composed of an organopolysiloxane that contains at least 2 alkenyl groups in each molecule, an organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule, and a hydrosilylation catalyst. However, these compositions generally exhibit poor adhesion, and this deficiency has necessitated the addition of an adhesion promoter to equip these compositions with self-bondability. A variety of adhesion promoters are known for this purpose. The following have already been disclosed as curable organopolysiloxane compositions with improved self-bonding properties: JP-A 51-28309, JP-A 52-48146, JP-A 1-85224, JP-A 54-80358, JP-A 48-75633, JP-A 61-72077. When cured at around 150°C, the curable organopolysiloxane compositions disclosed in JP-A(s) 51-28309, 52-48146, 1-85224, exhibit an excellent adhesiveness for substrates such as iron and aluminum, but have an inadequate adhesiveness for substrates such as nickel-plated substrates and copper. As a result, delamination occurs rather easily when the adherent composition bonded to these latter metals is treated with an acidic aqueous solution. For the adhesion promoters taught in JP-A(s) 48-75633 and 61-72077, foaming occurs when the addition reaction-curing organopolysiloxane compositions are subjected to heat curing because their adhesion promoters are extremely unstable due to hydroxyl and/or silicon-bonded alkoxy groups being in the molecule. US-A-4 357 440 discloses a new compound, 2-hydroxy-3-t-butylamino-1-propyl methacrylate, and latex coating compositions containing said compound as a wet-adhesion aid. JP-A-60231723 discloses a hydroxy alkylamine additive for polyepoxy resins represented by the following formula: wherein R1, R2, R3 and R4 may be identical or different groups and represent H, a 1 - 17C (un)saturated aliphatic group, alicyclic group, aromatic group, heterocyclic group or heterocycle residue except nitrogen bound by R1-R4, wherein these groups may be substituted by halogen, nitro, alkoxy, allyloxy or acetyl. The present invention introduces a highly adhesive curable organopolysiloxane composition whose adhesiveness is very durable under acidic conditions as well as an adhesion promoter which imparts this superior adhesiveness. The invention provides a curable organopolysiloxane composition that is composed of (A) 100 weight parts of an organopolysiloxane that contains at least 2 alkenyl groups in each molecule; (B) an organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule, in a quantity sufficient to give 0.3 to 5.0 moles of silicon-bonded hydrogen in component (B) per 1 mole of total alkenyl in the composition; (C) 0.3 to 10 weight parts of an adhesion promoter whose effective ingredient is the reaction product of a) an amine compound with the general formula wherein R denotes monovalent hydrocarbon groups and n is 1 or 2 and (b) an aliphatically unsaturated epoxy compound; wherein said reaction product is condensed with a silicon compound that contains at least two silicon-bonded alkoxy groups in each molecule; and (D) a catalytic quantity of a hydrosilylation catalyst. The present invention also relates to an adhesion promoter comprising the reaction product of (a) an amine compound with the general formula R n NH (3 - n) wherein R denotes monovalent hydrocarbon groups and n is 1 or 2 and (b) an aliphatically unsaturated epoxy compound, wherein said reaction product is condensed with (c) a silicon compound that contains at least two silicon bonded alkoxy groups in each molecule. The organopolysiloxane comprising component (A), consists of an organopolysiloxane that contains at least 2 alkenyl groups in each molecule. The alkenyl in component (A) is vinyl, allyl, butenyl, pentenyl, hexenyl, and decenyl, with vinyl being preferred. The bonding position for the alkenyl in component (A) is not critical, and the alkenyl may be bonded at the molecular chain terminals, or in nonterminal positions on the molecular chain, or at both positions. The non-alkenyl silicon-bonded organic groups in component (A) are exemplified by alkyl groups such as methyl, ethyl, propyl, butyl, pentyl, and hexyl; cycloalkyl groups such as cyclohexyl, and cycloheptyl; aryl groups such as phenyl, tolyl, and xylyl; aralkyl groups such as benzyl, and phenethyl; and halogenated alkyl groups such as 3,3,3-trifluoropropyl, and chloromethyl. Methyl preferably makes up at least half of the non-alkenyl silicon-bonded organic groups in component (A) because this affords good economics and an excellent adhesiveness. The molecular structure of component (A) is not critical and is exemplified by straight-chain, partially branched straight-chain, branched, cyclic, and network structures. Straight-chain structures are preferred. No particular restrictions apply to the viscosity of component (A), but its viscosity at 25°C preferably falls in the range of 100 to 1,000,000 mPa.s (centipoise) since this affords excellent handling characteristics on the part of the resulting curable organopolysiloxane composition. Subject organopolysiloxane (A) is as follows: trimethylsiloxy-endblocked methylvinylpolysiloxanes; trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers; trimethylsiloxy-endblocked methylphenylsiloxane-methylvinylsiloxane copolymers; dimethylvinylsiloxy-endblocked dimethylpolysiloxanes; dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers; dimethylvinylsiloxy-endblocked methylphenylpolysiloxanes; dimethylvinylsiloxy-endblocked methylphenylsiloxane-methylvinylsiloxane copolymers; silicone resins composed of the (CH 3 ) 3 SiO 1/2 , (CH 3 ) 2 (CH 2 =CH)SiO 1/2 , and SiO 4/2 units; and silicone resins composed of the (CH 3 ) 3 SiO 1/2 , (CH 3 ) 2 (CH 2 =CH)SiO 1/2 , CH 3 SiO 3/2 , and SiO 4/2 units. Component (A) may also consist of combinations of two or more of the above organopolysiloxanes. The organopolysiloxane (B), which is a crosslinker for the present composition, consists of an organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule. The bonding position for the silicon-bonded hydrogen in component (B) is not critical, and the silicon-bonded hydrogen may be bonded at the molecular chain terminals, or in nonterminal position on the molecular chain, or at both positions. The silicon-bonded organic groups in component (B) are examplified by alkyl groups such as methyl, ethyl, propyl, butyl, pentyl, and hexyl; cycloalkyl groups such as cyclohexyl, and cycloheptyl; aryl groups such as phenyl, tolyl, and xylyl; aralkyl groups such as benzyl, and phenethyl; and halogenated alkyl groups such as 3,3,3-trifluoropropyl, and chloromethyl. Methyl preferably makes up at least half of the silicon-bonded organic groups in component (B) because this affords good economics and an excellent adhesiveness. The molecular structure of component (B) is also not critical and is exemplified by straight-chain, partially branched straight-chain, branched, cyclic, and network structures. Straight-chain structures are preferred. No particular restrictions apply to the viscosity of component (B), but its viscosity at 25°C preferably falls in the range of 5 to 1,000,000 mPa.s (centipoise) since this affords excellent handling characteristics on the part of the resulting curable organopolysiloxane composition. Subject organopolysiloxane (B) is as follows: trimethylsiloxy-endblocked methylhydrogenpolysiloxanes; trimethylsiloxy-endblocked dimethylsiloxanemethylhydrogensiloxane copolymers; dimethylhydrogensiloxy-endblocked dimethylpolysiloxanes; dimethylhydrogensiloxy-endblocked methylhydrogenpolysiloxanes; dimethylhydrogensiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers; cyclic methylhydrogenpolysiloxanes; cyclic dimethylsiloxane-methylhydrogensiloxane copolymers; tetrakis(dimethylhydrogensiloxy)silane; silicone resins composed of the (CH 3 ) 2 HSiO 1/2 , (CH 3 ) 3 SiO 1/2 , and SiO 4/2 units; and silicone resins composed of the (CH 3 ) 2 HSiO 1/2 , (CH 3 ) 3 SiO 1/2 , CH 3 Si O 3/2 , and SiO 4/2 units. Component (B) may also consist of combinations of two or more of the above organopolysiloxanes. Component (B) must be added to the present composition in a quantity that yields 0.3 to 5.0 moles of silicon-bonded hydrogen in component (B) per 1 mole of total alkenyl in the present composition. The curability of the curable organopolysiloxane composition is sharply reduced when the addition of component (B) provides less than 0.3 moles of silicon-bonded hydrogen from component (B) per 1 mole of total alkenyl in the present composition. At the other extreme, the cured organopolysiloxane will exhibit sharply reduced physical properties when the addition of component (B) provides more than 5.0 moles of silicon-bonded hydrogen from component (B) per 1 mole of total alkenyl in the present composition. The adhesion promoter comprising component (C) is the characterizing component that imparts self-bondability to the present composition. Adhesion promoter (C) is the reaction product of (a) an amine compound with the general formula R n NH (3 - n) wherein R denotes monovalent hydrocarbon groups and n is 1 or 2 and (b) an aliphatically unsaturated epoxy compound, wherein said reaction product is condensed with a silicon compound that contains at least two silicon-bonded alkoxy groups in each molecule. The amine compound (a) is described by general formula R n NH (3 - n) wherein R denotes a monovalent hydrocarbon group, and is exemplified by alkyl groups such as methyl, ethyl, propyl, butyl, pentyl, and hexyl; alkenyl groups such as vinyl, allyl, butenyl, pentenyl, and hexenyl; aryl groups such as phenyl, tolyl, xylyl, and naphthyl; and aralkyl groups such as benzyl, and phenethyl. Allyl and phenyl are preferred. The subscript n in the preceding formula is 1 or 2. When n is 1, the amine compound is a primary amine; and when n is 2, the amine compound is a secondary amine. Subject amine compounds (a) are methylamine, ethylamine, n-propylamine, n-butylamine, tert-butylamine, dimethylamine, diethylamine, dipropylamine, di(n-butyl)amine, di(tert-butyl)amine, allylamine, butenylamine, diallylamine, methylaniline, allylaniline, and aniline. Allylamine and aniline are preferred. The epoxy compound (b) is an aliphatically unsaturated epoxy compound, and is exemplified by allyl glycidyl ether, butenyl glycidyl ether, pentenyl glycidyl ether, 4-vinyl-1,2-epoxycyclohexane, 4-allyl-1,2-epoxycyclohexane, 4-butenyl-1,2-epoxycyclohexane, 4-pentenyl-1,2-epoxycyclohexane, glycidyl methacrylate, and glycidyl acrylate. Allyl glycidyl ether is preferred. The adhesion promoter (C) is prepared by reacting the nitrogen-bonded hydrogen in component (a) with the epoxy group in component (b). This reaction proceeds at room temperature, but is accompanied by a substantial evolution of heat which creates the risk of a violent reaction. The reaction is therefore preferably run by the gradual, dropwise addition of component (b) into component (a), or of component (a) into component (b). Component (b) is preferably added to give a slight molar excess of epoxy groups of component (b) over nitrogen-bonded hydrogen of component (a). Even more desirably, component (b) is added in quantities that give 1.01 to 2 moles epoxy group of component (b) per mole nitrogen-bonded hydrogen of component (a). The basis for this preferred addition of component (b) is that complete consumption of the nitrogen-bonded hydrogen in component (C) yields a substantial improvement in the curability of our present composition. There are no particular restrictions on the temperature in the subject reaction, but the recommended method consists of the gradual dropwise addition of component (a) while component (b) is heated to at least 70°C. Following completion of the reaction, the reaction product can be purified by distilling off unreacted component (b) under reduced pressure. Thereafter the aforementioned reaction product from the amine compound (a) and the aliphatically unsaturated epoxy compound (b) is condensed with a silicon compound (c) that contains at least 2 silicon-bonded alkoxy groups in each molecule. Alkoxysilanes that contain at least two silicon-bonded alkoxy groups in each molecule and alkoxysilylalkylalkoxysilanes that contain at least two silicon-bonded alkoxy groups in each molecule are examples of the silicon compound (c). The alkoxysilanes encompassed by component (c) are specifically exemplified by tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, ethyltrimethoxysilane, vinyltrimethoxysilane, allyltrimethoxysilane, phenyltrimethoxysilane, dimethyldimethoxysilane, methylvinyldimethoxysilane, methylphenyldimethoxysilane, diphenyldimethoxysilane, 3-glycidoxypropyltrimethoxysilane, and 3-methacryloxypropyltrimethoxysilane. Tetramethoxysilane is preferable. Specific examples of alkoxysilylalkylalkoxysilanes encompassed by component (c) include bis(trimethoxysilyl)ethane, bis(trimethoxysilyl)propane, bis(trimethoxysilyl)butane, bis(trimethoxysilyl)pentane, bis(trimethoxysilyl)hexane, bis(triethoxysilyl)ethane, bis(triethoxysilyl)propane, bis(methyldimethoxysilyl)ethane, and bis(methyldimethoxysilyl)propane, Bis(trimethoxysilyl)hexane is preferable. Combinations of two or more of the preceding alkoxysilanes and/or alkoxysilylalkyl- alkoxysilanes may also be used as component (c). When allyl glycidyl ether is used as component (b) for adhesion promoter (C), the resulting adhesion promoter has the following general formula wherein R and n have their previously defined meanings and X denotes an alkoxysilyl group or alkoxysilylalkylsilyl group. The alkoxysilyl groups represented by X can be expressed by the following general formula -SiR 2 a (OR 1 ) (3-a) in which R 1 = alkyl, R 2 = monovalent hydrocarbon group, and a is an integer from 0 to 2. R 1 denotes alkyl, such as methyl, ethyl, propyl, butyl, pentyl, and hexyl, with methyl being preferred. R 2 denotes monovalent hydrocarbon groups, which are the same monovalent hydrocarbon groups as listed above for the R radical of the amine compound (a). The subscript a is an integer from 0 to 2. The alkoxysilyl groups encompassed by X are exemplified by trimethoxysilyl, triethoxysilyl, methyldimethoxysilyl, vinyldimethoxysilyl, phenyldimethoxysilyl, dimethylmethoxysilyl, methylvinylmethoxysilyl, methylphenylmethoxysilyl, diphenylmethoxysilyl, 3-glycidoxypropyldimethoxysilyl, and 3-methacryloxypropyldimethoxysilyl. The alkoxysilylalkylsilyl groups represented by X can be expressed by the following general formula -SiR 2 b (OR 1 ) (2-b) -R 3 -SiR 2 a (OR 1 ) (3-a) wherein R 1 , R 2 and a have their previously defined meanings. R 2 is an alkylene group, which is methylene, ethylene, methylmethylene, methylethylene, propylene, butylene, pentylene, hexylene, heptylene, and octylene, with hexylene being preferred. The subscript b is also an integer from 0 to 2. Specific alkoxysilylalkylsilyl groups encompassed by X include trimethoxysilylethyldimethoxysilyl, trimethoxysilylpropyldimethoxysilyl, trimethoxysilylbutyldimethoxysilyl, trimethoxysilylpentyldimethoxysilyl, trimethoxysilylhexyldimethoxysilyl, triethoxysilylethyldiethoxysilyl, triethoxysilylpropyldiethoxysilyl, methyldimethoxysilylethyldimethoxysilyl, methyldimethoxysilylpropyldimethoxysilyl, methyldimethoxysilylbutyldimethoxysilyl, methyldimethoxysilylpentyldimethoxysilyl, methyldimethoxysilylhexyldimethoxysilyl, dimethylmethoxysilylethyldimethoxysilyl, dimethylmethoxysilylpropyldimethoxysilyl, dimethylmethoxysilylbutyldimethoxysilyl, dimethylmethoxysilylpentyldimethoxysilyl, and dimethylmethoxysilylhexyldimethoxysilyl. This reaction consists of an alcohol-liberating condensation reaction between the silicon-bonded alkoxy in component (c) and the hydroxyl in the reaction product that is the main component of component (C). This condensation reaction can be accelerated by an alcohol-exchange catalyst. The desired reaction product can be obtained by removing the alcohol by-product by heating and/or the application of reduced pressure. This reaction can be expressed, for example, by the following equation. wherein R, R 1 , X and n have their previously defined meanings. There are no particular restrictions on the aforementioned alcohol-exchange catalyst as long as said catalyst is a compound that accelerates alcohol exchange. Specific examples of such catalysts include basic catalysts such as sodium hydroxide, potassium hydroxide, cesium hydroxide, and potassium methylate; or titanium catalysts such as tetrabutoxytitanium. When the nitrogen in the adhesion promoter is strongly basic, the adhesion promoter will itself function as an alcohol-exchange catalyst, thus eliminating the need for a separate addition of alcohol-exchange catalyst. This reaction will proceed even at room temperature, but only very slowly. Accordingly, it is desirable to run this reaction by heating the system to a temperature of 50°C to 200°C. It will also be desirable to remove the alcohol by-product at ambient pressure or under reduced pressure. Component (C) is added to the present composition at 0.3 to 10 weight parts per 100 weight parts component (A). The self-bondability of the curable organopolysiloxane composition drops off sharply at component (C) additions of less than 0.3 weight parts per 100 weight parts component (A). On the other hand, the physical properties of the cured organopolysiloxane will be substantially impaired when component (C) is added in excess of 10 weight parts per 100 weight parts component (A). The hydrosilylation catalyst comprising component (D) is a catalyst that accelerates the cure of the present composition. This hydrosilylation catalyst is exemplified by platinum catalysts such as platinum black, platinum supported on silica micropowder, platinum supported on carbon powder, chloroplatinic acid, alcohol solutions of chloroplatinic acid, platinum/olefin complexes, platinum/alkenylsiloxane complexes, platinum/beta-diketone complexes, and platinum/phosphine complexes; rhodium catalysts such as rhodium chloride, or rhodium chloride/di(n-butyl)sulfide complex; and palladium catalysts. In the present invention, component (D) is preferably a platinum catalyst when the monovalent hydrocarbon group bonded to the nitrogen in component (C) is alkyl or aryl. Or component (D) is preferably a rhodium catalyst when the monovalent hydrocarbon group bonded to the nitrogen in component (C) is alkenyl. Component (D) should be added to the present composition in a catalytic quantity. In specific terms, the preferred addition gives 0.1 to 500 ppm catalyst metal in the composition. The curable organopolysiloxane composition of the invention is prepared by mixing the aforementioned components (A) through (D) to homogeneity. Components which may be added to our composition on an optional basis are exemplified by inorganic fillers such as dry-process silica, wet-process silica, crystalline silica, diatomaceous earth, silica balloons, calcium carbonate, carbon black, titanium dioxide, aluminum oxide, zinc oxide, colorants, heat stabilizers, antioxidants, and flame retardants. An acetylenic compound, amine compound, mercaptan compound, or phosphorus compound, may be added in order to control the cure rate of our curable organopolysiloxane composition. The following may be added in order to obtain additional improvements in the self-bondability of the curable organopolysiloxane composition of the invention: 3-glycidoxypropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, vinyltrimethoxysilane, allyltrimethoxysilane, tetramethoxysilane, 1,5-bis(trimethoxysilyl)hexane, 1,2-dimethyl-1,1,2,2-tetramethoxydisilane, or the reaction mixture from 3-glycidoxypropyltrimethoxysilane and methylvinylcyclosiloxane. Unreactive silicone oils may be added in order to improve the physical properties of the cured organopolysiloxane. The curable organopolysiloxane composition of this invention can be prepared by mixing the various components described hereinbefore to homogeneity. No specific restrictions apply to the equipment to be used for preparation of our curable organopolysiloxane composition, and, a planetary mixer, kneader mixer, screw mixer, impeller mixer, static mixer, 2-roll mill, 3-roll mill, or twin-screw extruder can be used. The curable organopolysiloxane composition of this invention can be cured at room or elevated temperature. However, in order to obtain an excellent self-bondability, the preferred curing procedure consists of heating the curable organopolysiloxane composition on the substrate to 50°C to 200°C. The curable organopolysiloxane composition of the invention exhibits an excellent self-bondability to metal surfaces. In particular, it is strongly adhesive to the surface of copper, which is widely used in the electrical and electronic sectors. The curable organopolysiloxane composition of our invention can therefore be used as a mask or solder resist during the partial plating of copper conductors. Our curable organopolysiloxane composition exhibits a superior adhesiveness that appears immediately upon curing, and its adhesiveness is also very durable to challenge by acidic conditions. As a result of these attributes, our composition can be used for various types of masks, sealants, potting materials, and coatings. Examples The curable organopolysiloxane composition of the present invention is described below in greater detail through working examples. The adhesiveness was evaluated as follows: either immediately after the curable organopolysiloxane composition had been cured into silicone rubber by heating on the substrate, or after acid challenge of the adhesiveness, the silicone rubber was peeled back using a spatula and the performance at this point was rated. Good adhesion was scored as "+ +"; partial delamination was scored as "+"; and complete delamination was scored as "x". Reference Example 1 285 g of allyl glycidyl ether was placed in a 500-ml four-necked flask equipped with a stirrer, thermometer, reflux condenser, and addition funnel. 57 g of allylamine was then added dropwise from the addition funnel while regulating the system so the temperature did not exceed 150°C. The system was reacted for 2 hours at 150°C after addition of the allylamine. This was followed by removal of the unreacted allyl glycidyl ether by stripping to give a moderately brown liquid product. Analysis of this liquid product by 1 H-nuclear magnetic resonance spectroscopic analysis (NMR), infrared spectroscopic analysis (IR), and gas chromatographic/mass spectrometric analysis (GC/MASS) confirmed it to be an adhesion promoter (designated as adhesion promoter (A)) whose main component was the following compound. Reference Example 2 201 g of allyl glycidyl ether was placed in a 500-Ml four-necked flask equipped with a stirrer, thermometer, reflux condenser, and addition funnel. After the system had been heated to 140°C, 65.9 g of aniline was added dropwise from the addition funnel while regulating the system so the temperature did not exceed 160°C. The system was reacted for 2 hours at 150°C after addition of the aniline. This was followed by removal of the unreacted allyl glycidyl ether by stripping to give a moderately brown liquid product. This liquid product was distilled at 150°C and a pressure of 13.3 Pa (0.2 torr) using a thin-film distillation apparatus to give a moderately yellow liquid product. Analysis of this liquid product by NMR, IR, and GC/MASS confirmed it to be an adhesion promoter (designated as adhesion promoter (B)) whose main component was the following compound. Reference Example 3 100 g of the compound synthesized in Reference Example 1 and 213.3 g of tetramethoxysilane were placed in a 500-ml four-necked flask equipped with a stirrer, thermometer, and distillation setup. 0.04 g of potassium hydroxide was added to this system, and the system was heated while stirring. During this period, the methanol by-product was removed through a 20-cm Vigreux distillation column. The system was cooled to room temperature after methanol evolution had ceased. The potassium hydroxide was then neutralized by the addition of 1.1 g of propionic acid. The unreacted propionic acid and tetramethoxysilane were removed by stripping to give a liquid product. Analysis of this liquid product by IR confirmed the disappearance of the peaks attributable to hydroxyl. Analysis of this liquid product by NMR and GC/MASS confirmed it to be an adhesion promoter (designated as adhesion promoter (C)) whose main component was the following compound. Reference Example 4 51.1 g of the compound prepared in Reference Example 2, 100 g of bis(trimethoxysilyl)hexane, and 1.5 g of tetrabutoxy-titanium were placed in a 500-ml four-necked flask equipped with a stirrer, thermometer, and distillation setup, and the system was heated to 150°C under reduced pressure produced by an aspirator. The methanol by-product was recovered in a dry ice-acetone trap, and 11 g of methanol by-product was obtained. After methanol production had ceased, the system was cooled to give a liquid product. Analysis of this liquid product by IR confirmed the disappearance of the peaks attributable to hydroxyl. Analysis of this liquid product by NMR and GC/MASS confirmed it to be an adhesion promoter (designated as adhesion promoter (D)) whose main component was the following compound. Reference Example 5 495.6 g of 3-glycidoxypropyltrimethoxysilane and 221 g of 3-aminopropyltriethoxysilane were placed in a 1-liter four-necked flask equipped with stirrer and thermometer. Stirring this system for 3 hours at 100°C produced a viscous adhesion promoter (E). Analysis of this adhesion promoter by IR confirmed the disappearance of the peaks attributable to the N-H bond. Comparative Example 1 A curable organopolysiloxane composition was prepared by mixing the following to homogeneity: 100 weight parts of dimethylvinylsiloxy-endblocked dimethylpolysiloxane with an average degree of polymerization of 300 and a vinyl group content of 0.24 weight%; a trimethylsiloxy-endblocked methylhydrogenpolysiloxane with an average degree of polymerization of 40 and a silicon-bonded hydrogen content of 1.5 weight% (this component was added in sufficient quantity to give 1.5 moles silicon-bonded hydrogen per mole total alkenyl in the composition); 11 weight parts of fumed silica (specific surface = 200 m 2 /g) whose surface had been treated with hexamethyldi-silazane; 2.2 weight parts of adhesion promoter (A); rhodium chloride/di(n-butyl)sulfide complex in an amount sufficient to give a rhodium metal content in the composition of 10 ppm; and 0.02 weight parts of phenylbutynol. This curable organopolysiloxane composition was coated on each of the substrates shown in Table 1 and cured to give the silicone rubber by heating for 1 hour at 150°C. The silicone rubber was in each case peeled from the substrate using a spatula in order to evaluate the adhesion. The results are reported in Table 1. Comparative Example 2 A curable organopolysiloxane composition was prepared by mixing the following to homogeneity: 100 weight parts of dimethylvinylsiloxy-endblocked dimethylpolysiloxane with an average degree of polymerization of 300 and a vinyl group content of 0.24 weight%; a trimethylsiloxy-endblocked methylhydrogenpolysiloxane with an average degree of polymerization of 40 and a silicon-bonded hydrogen content of 1.5 weight% (this component was added in sufficient quantity to give 1.5 moles silicon-bonded hydrogen per mole total alkenyl in the composition); 11 weight parts of fumed silica (specific surface = 200 m 2 /g) whose surface had been treated with hexamethyldi-silazane; 2.2 weight parts of adhesion promoter (B); a chloro-platinic acid/vinylsiloxane complex in an amount sufficient to give a platinum metal content in the composition of 10 ppm; and 0.02 weight parts of phenylbutynol. This curable organopolysiloxane composition was coated on each of the substrates shown in Table 1 and cured to give the silicone rubber by heating for 1 hour at 150°C. The silicone rubber was in each case peeled from the substrate using a spatula in order to evaluate the adhesion. The results are reported in Table 1. Example 1 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 1, but in this case using adhesion promoter (C) in place of the adhesion promoter (A) used in Comparative Example 1. The adhesiveness was evaluated as in Comparative Example 1, and these results are reported in Table 1. Example 2 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 2, but in this case using adhesion promoter (D) in place of the adhesion promoter (B) used in Comparative Example 2. The adhesiveness was evaluated as in Comparative Example 2, and these results are reported in Table 1. Comparative Example 3 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 2, but in this case using adhesion promoter (E) in place of the adhesion promoter (B) used in Comparative Example 2. The adhesiveness was evaluated as in Comparative Example 2, and these results are reported in Table 1. Comparative Example 4 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 2, but in this case omitting the adhesion promoter (B) used in Comparative Example 2. The adhesiveness was evaluated as in Comparative Example 2, and these results are reported in Table 1. present invention comparative examples Comp. Ex. 1 Comp. Ex. 2 Ex. 1 Ex. 2 Comp. Ex. 3 Comp. Ex. 4 adhesion promoter A B C D E none appearance of the silicone rubber + + + + + + + + x foaming + + adhesion aluminum + + + + + + + + + + + + copper + + + + + + + + + + x stainless steel SUS304 + + + + + + + + + + + + nickel + + + + + + + + + + + + glass + + + + + + + + + + + + glass-epoxy resin + + + + + + + + + + x polybutylene terephthalate + + + + + + + + + + x nylon 6 + + x + + + + x x polyphenylene sulfide x x + x x x Comparative Example 5 A curable organopolysiloxane composition was prepared by mixing the following to homogeneity: 80 weight parts of dimethylvinylsiloxy-endblocked dimethylpolysiloxane with an average degree of polymerization of 300 and a vinyl group content of 0.24 weight%; 20 weight parts of silicone resin composed of siloxane units with the formulae (CH 3 )SiO 1/2 , (CH 2 =CH)(CH 3 ) 2 SiO 1/2 , and SiO 4/2 (vinyl group content = approximately 2 weight%); a trimethylsiloxy-endblocked methylhydrogenpolysiloxane with an average degree of polymerization of 40 and a silicon-bonded hydrogen content of 1.5 weight% (this component was added in sufficient quantity to give 1.5 moles silicon-bonded hydrogen per mole total alkenyl in the composition); 14.3 weight parts of fumed silica (specific surface = 200 m 2 /g) whose surface had been treated with hexamethyldisilazane; 2.3 weight parts of adhesion promoter (A); a rhodium chloride/di(n-butyl)sulfide complex in an amount sufficient to give a rhodium metal content in the composition of 10 ppm; and 0.02 weight parts of phenylbutynol. This curable organopolysiloxane composition was applied to copper plate at a coating thickness of 50 micrometers, and cured to give the silicone rubber by heating the coated plate for 1 hour at 150°C. The adhesion was then evaluated by peeling the silicone rubber from the copper plate using a spatula. In addition, the silicone rubber bonded on the copper plate was immersed for 10 minutes in a 10% aqueous solution of hydrochloric acid at 50°C, and the adhesion was evaluated following this immersion. The results are reported in Table 2. Comparative Example 6 A curable organopolysiloxane composition was prepared by mixing the following to homogeneity: 80 weight parts of dimethylvinylsiloxy-endblocked dimethylpolysiloxane with an average degree of polymerization of 300 and a vinyl group content of 0.24 weight%; 20 weight parts of silicone resin composed of siloxane units with the formulas (CH 3 ) 3 SiO 1/2 , (CH 2 =CH)(CH 3 ) 2 SiO 1/2 , and SiO 4/2 (vinyl group content = approximately 2 weight%); a trimethylsiloxy-endblocked methylhydrogenpolysiloxane with an average degree of polymerization of 40 and a silicon-bonded hydrogen content of 1.5 weight% (this component was added in sufficient quantity to give 1.5 moles silicon-bonded hydrogen per mole total alkenyl in the composition); 14.3 weight parts of fumed silica (specific surface = 200 m 2 /g) whose surface had been treated with hexamethyldi-silazane; 2.3 weight parts of adhesion promoter (B); a chloroplatinic acid/vinylsiloxane complex in an amount sufficient to give a platinum metal content in the composition of 10 ppm; and 0.02 weight parts of phenylbutynol. This curable organopolysiloxane composition was applied to copper plate at a coating thickness of 50 micrometers, and cured to give the silicone rubber by heating the coated plate for 1 hour at 150°C. The adhesion was then evaluated by peeling the silicone rubber from the copper plate using a spatula. In addition, the silicone rubber bonded on the copper plate was immersed for 10 minutes in a 10% aqueous solution of hydrochloric acid at 50°C, and the adhesion was evaluated following this immersion. The results are reported in Table 2. Example 3 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 5, but in this case using adhesion promoter (C) in place of the adhesion promoter (A) used in Comparative Example 5. The adhesiveness was evaluated as in Comparative Example 5, and these results are reported in Table 2. Example 4 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 6, but in this case using adhesion promoter (D) in place of the adhesion promoter (B) used in Comparative Example 6. The adhesiveness was evaluated as in Comparative Example 6, and these results are reported in Table 2. Comparative Example 7 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 6, but in this case omitting the adhesion promoter (B) used in Comparative Example 6. The adhesiveness was evaluated as in Comparative Example 6, and these results are reported in Table 2. Comparative Example 8 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 6, but in this case using tetramethoxysilane (TMS) in place of the adhesion promoter (B) used in Comparative Example 6. The adhesiveness was evaluated as in Comparative Example 6, and these results are reported in Table 2. Comparative Example 9 A curable organopolysiloxane composition was prepared using the procedure of Comparative Example 6, but in this case using bis(trimethoxysilyl)hexane (BTMSH) in place of the adhesion promoter (B) used in Comparative Example 6. The adhesiveness was evaluated as in Comparative Example 6, and these results are reported in Table 2. present invention comparative examples Comp. Ex. 5 Comp. Ex. 6 Ex. 3 Ex. 4 Comp. Ex. 7 Comp. Ex. 8 Comp. Ex. 9 adhesion promoter A B C D none TMS BTMSH adhesion initial + + + + + + + + x + + + + after treatment with hydrochloric acid + + + + + + + + x x x

Claims: An adhesion promoter comprising the reaction product of (a) an amine compound having the general formula R n NH (3 - n) wherein R denotes a monovalent hydrocarbon group and n is 1 or 2, and (b) an aliphatically unsaturated epoxy compound, wherein said reaction product is condensed with (c) an alkoxysilane which contains at least two silicon-bonded alkoxy groups in each molecule. The adhesion promoter according to claim 1, wherein said alkoxysilane (c) is selected from the group consisting of tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, ethyltrimethoxysilane, vinyltrimethoxysilane, allyltrimethoxysilane, phenyltrimethoxysilane, dimethyldimethoxysilane, methylvinyldimethoxysilane, methylphenyldimethoxysilane, diphenyldimethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, bis(trimethoxysilyl)ethane, bis(trimethoxysilyl)propane, bis(trimethoxysilyl)butane, bis(trimethoxysilyl)pentane, bis(trimethoxysilyl)hexane, bis(triethoxysilyl)ethane, bis(triethoxysilyl)propane, bis(methyldimethoxysilyl)ethane, and bis(methyldimethoxysilyl)propane. The adhesion promoter according to claims 1 or 2, wherein said amine compound (a) is selected from the group consisting of methylamine, ethylamine, n-propylamine, n-butylamine, tert-butylamine, dimethylamine, diethylamine, dipropylamine, di(n-butyl)amine, di(tert-butyl)amine, allylamine, butenylamine, diallylamine, methylaniline, allylaniline and aniline and said epoxy compound (b) is selected from the group consisting of allyl glycidyl ether, butenyl glycidyl ether, pentenyl glycidyl ether, 4-vinyl-1,2-epoxycyclohexane, 4-allyl-1,2-epoxycyclohexane, 4-butenyl-1,2-epoxycyclohexane, 4-pentenyl-1,2-epoxycyclohexane, glycidyl methacrylate, and glycidyl acrylate. The adhesion promoter according to claim 3, wherein said amine compound (a) is selected from the group consisting of allylamine and aniline and said epoxy compound (b) is allyl glycidyl ether. The adhesion promoter according to claim 4, wherein said alkoxysilane (c) is selected from tetramethoxysilane and bis(trimethoxysilyl)hexane. A curable organopolysiloxane composition comprising: (A) 100 parts by weight of an organopolysiloxane that contains at least 2 alkenyl groups in each molecule; (B) an organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule, in a quantity sufficient to provide 0.3 to 5.0 moles of silicon-bonded hydrogen in said component (B) per 1 mole of total alkenyl groups in the composition; (C) 0.3 to 10 parts by weight of the adhesion promoter of claim 1; and (D) 0.1 to 500 ppm of catalyst metal, per million parts of composition of a hydrosilylation catalyst. The composition according to claim 6, wherein said organopolysiloxane (A) is selected from the group consisting of trimethylsiloxy-endblocked methylvinylpolysiloxanes, trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, trimethylsiloxy-endblocked methylphenylsiloxane-methylvinylsiloxane copolymers, dimethylvinylsiloxy-endblocked dimethylpolysiloxanes, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, dimethylvinylsiloxy-endblocked methylphenylpolysiloxanes, dimethylvinylsiloxy-endblocked methylphenylsiloxane-methylvinylsiloxane copolymers, silicone resins composed of the (CH 3 ) 3 SiO 1/2 , (CH 3 ) 2 (CH 2 =CH)SiO 1/2 , and SiO 4/2 units, and silicone resins composed of the (CH 3 ) 3 SiO 1/2 , (CH 3 ) 2 (CH 2 =CH)SiO 1/2 , CH 3 SiO 3/2 , and SiO 4/2 units and said organopolysiloxane (B) is selected from the group consisting of trimethylsiloxy-endblocked methylhydrogenpolysiloxanes, trimethylsiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, dimethylhydrogensiloxy-endblocked dimethylpolysiloxanes, dimethylhydrogensiloxy-endblocked methylhydrogenpolysiloxanes, dimethylhydrogensiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, cyclic methylhydrogenpolysiloxanes, cyclic dimethylsiloxane-methylhydrogensiloxane copolymers, tetrakis(dimethylhydrogensiloxy)silane, silicone resins composed of the (CH 3 ) 2 HSiO 1/2 , (CH 3 ) 3 SiO 1/2 , and SiO 4/2 units, and silicone resins composed of the (CH 3 ) 2 HSiO 1/2 , (CH 3 ) 3 SiO 1/2 , CH 3 SiO 3/2 , and SiO 4/2 units. A copper metal substrate coated with the composition of claim 6. The composition according to claim 6, wherein said hydrosilation catalyst (D) is selected from the group consisting of platinum black, platinum supported on silica micropowder, platinum supported on carbon powder, chloroplatinic acid, alcohol solutions of chloroplatinic acid, platinum/olefin complexes, platinum alkenylsiloxane complexes, platnium/beta-diketone complexes, and platnium/phosphine complexes; rhodium catalyst such as rhodium chloride or rhodium chloride/di(n-butyl)sulfide complex; and palladium catalyst.

Inventors: KASUYA AKIRA, KASUYA, AKIRA, KASUYA, AKIRA, DOW CORNING TORAY SILICONE CO.,LTD.
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: C09J11
IPC codes: C09J183, C08L83, C09J11, C08K5