Organopolysiloxane compositions, their preparation and use, articles coated with them

Abstract: An organopolysiloxane composition contains (A) a both end hydroxyl - blocked diorganopoly - siloxane, (B) an inert diorganopolysiloxane, (C) a silane or siloxane having at least three hydrolyzable functional groups, (D) an organosilane having at least two alkoxy groups each attached to a silicon atom and one mercapto group separated from a silicon atom by an alkylene group or a partial hydrolyzate thereof, (E) an organosilane having at least two alkoxy groups each attached to a silicon atom and one amino group separated from a silicon atom by an alkylene group or a partial hydrolyzate thereof, (F) a condensation catalyst, and (G) a fine powder, typically of polycarbonate, having a mean particle size of 0.1 - 50 µm. The composition is useful as a surface treating agent for cured rubber moldings for imparting non - tackiness, water repellency and lubricity to the rubber surface and forming a long-lasting abrasion resistant coating.

Description: This invention relates to organopolysiloxane compositions which may be useful as surface treating agents e.g. for imparting non-tacky, water repellent, and lubricating properties to a cured rubber surface and forming an abrasion resistant coating. It also relates to rubber articles having such a coating. Other aspects concern the preparation and use of the compositions. Prior Art Inert silicone oil and various curable organopolysiloxane compositions have been used for imparting non-tackiness and water repellency to rubber surfaces. Inert silicone oil has high initial wear properties, but does not last long since it is readily shed from the substrate surface by physical actions as weak as water washing. The curable organopolysiloxane compositions used heretofore are typically those containing a both end hydroxyl-blocked diorganopolysiloxane, a Si-H group-containing organopolysiloxane and/or an organoalkoxysilane, and an organic tin compound. These compositions form on the substrate surface coatings which are acceptably tack-free and water repellent, but poor in lubricity and wear resistance. It is possible to improve adhesiveness to a substrate and lubricity, giving wear resistance, by adding a mixture or reaction product of an organopolysiloxane having an epoxy group such as glycidoxy group and epoxycyclohexyl group and alkoxysilane or siloxane having an amino group (Japan Kokoku Nos. 54-43023, 56-19813 and 56-47864), but the improvement is not yet fully attained. It is also possible to improve lubricity and wear resistance by adding inert silicone oil to such organopolysiloxane compositions containing a both end hydroxylblocked diorganopolysiloxane, a Si-H group-containing organopolysiloxane and/or an organoalkoxysilane, and an organic tin compound (JP-A-62/215667), but the coatings are not satisfactorily durably wear resistant where frictional forces are repeatedly applied. Our general aim is to provide new organopolysiloxane compositions, in particular useful for surface coating, also methods of preparing and using them and the resulting articles. In a first aspect the invention provides an organopolysiloxane composition comprising (A) 100 parts by weight of diorganopolysiloxane of the following general formula (1): wherein R 1 are substituted or unsubstituted monovalent hydrocarbon groups and m is in the range 150 to 10,000; (B) 5 to 80 parts by weight of diorganopolysiloxane of the following general formula (2): wherein R 1 are substituted or unsubstituted monovalent hydrocarbon groups and n is equal to or larger then m; (C) 0.2 to 30 parts by weight of silane and/or siloxane having per molecule at least three hydrolysable groups bonded to Si selected from alkoxy, alkenyloxy, ketoxime, acyloxy, amide, aminoxy, isocyanate, silylester and halogen groups, any other groups bonded to Si being selected from hydrocarbon groups which may be substituted with halogen atom or nitrile group and said siloxane f present being an oligomer having from 2 to 10 silicon atoms; (D) 1 to 20 parts by weight of organosilane having per molecule at least two alkoxy groups bonded to Si and a mercapto group bonded to Si through an alkylene group, any other group bonded to Si being C 1-8 hydrocarbon which may be substituted with halogen atom or nitrile group; and/or a partial hydrolysate of such organosilane; (E) 5 to 150 parts by weight of organosilane having per molecule at least two alkoxy groups bonded to Si and a substituted or unsubstituted amino group bonded to Si through an alkylene group, any other group bonded to Si being C 1-8 hydrocarbon which may be substituted with halogen atom or nitrile group; and/or a partial hydrolysate of such organosilane; (F) condensation catalyst in an amount of 0.1 to 30 parts by weight per 100 parts by weight of components (A) to (C) combined, and (G) microparticulate powder having a mean particle size of up to 50 µm in an amount of 2 to 40 parts by weight per 100 parts by weight of components (A) to (C) combined. A second aspect is a rubber article having a cured surface coating of such of composition. A third aspect is the use of such a composition to form a surface coating on a substrate. The organopolysiloxane composition contains a both end hydroxyl - blocked diorganopolysiloxane (A) as a main component for forming a cured coating; a silane or siloxane (C) as a crosslinking agent; component (F) as a catalyst for promoting condensation reaction between components (A) and (C); an inert diorganopolysiloxane (B) having a degree of polymerization equal to or higher than that of component (A) as a lubricant; a microparticulate powder (G) for flattening the cured product and imparting abrasion resistance; and organosilanes (D) and (E) as an adhesion enhancer for improving the binding of microparticulates to the matrix resin and enhancing the adhesion of the matrix resin to a rubber substrate. Since these components act in a synergistic manner, the composition, when applied and cured to a rubber substrate surface, forms a cured coating which is tack-free, water repellent, lubricating and abrasion resistant and maintains abrasion resistance over a long term. FURTHER EXPLANATIONS; OPTIONAL AND PREFERRED FEATURES Component (A) is a diorganopolysiloxane of the following general formula (1) which is a main component to form a coating by curing through reaction of its hydroxyl group at each end with a hydrolysable functional group of component (C) and alkoxy groups of components (D) and (E). In formula (1), R 1 are substituted or unsubstituted monovalent hydrocarbon groups, preferably selected from hydrocarbon groups having 1 to 8 carbon atoms, more preferably 1 to 6, preferably free from aliphatic unsaturated bonds. Examples are alkyl groups such as methyl, ethyl, propyl, iso-propyl, butyl, iso-butyl, tert-butyl, pentyl, neo-pentyl, hexyl and cyclohexyl, alkenyl groups such as vinyl, allyl, propenyl, iso-propenyl, butenyl, iso-butenyl and cyclohexenyl, aryl groups such as phenyl, tolyl, xylyl and naphthyl, aralkyl groups such as styrenyl, benzyl, phenylethyl and phenylpropyl and substituted hydrocarbon groups in which some hydrogen atoms of these hydrocarbon groups are replaced e.g. by halogen atoms including fluorine atoms and chlorine atoms, nitrile groups or the like such as chloromethyl, chloropropyl, bromoethyl, trifluoropropyl and cyanoethyl. The skilled person in this art is well aware of a range of well-known possible substituents and their associated effects or lack of effect. Part (usually 1 mol% or less) of R 1 may be a hydroxyl group if particularly desired for imparting certain properties. A substituted or unsubstituted alkyl group, particularly a methyl group is preferred among these groups because of ease of synthesis, ease of handling, and an ability to impart adequate curability to the composition. Letter m which represents a degree of polymerisation is an integer of at least 150, preferably from 150 to 10,000, more preferably from 200 to 10,000. If m is less than 150, the cured coating becomes brittle and would not follow deformation of the substrate. If m is too large, the composition before curing would have an increased viscosity to render handling less efficient. Two or more diorganopolysiloxanes may be used in combination if m is within the above-defined range and if desired. Component (B) is an inert diorganopolysiloxane of the following general formula (2) which is free of a hydroxyl group attached to a silicon atom in a molecule and serves to impart lubricity and abrasion resistance to a cured coating. In formula (2), R 2 are substituted or unsubstituted monovalent hydrocarbon groups preferably having 1 to 8, more preferably 1 to 6 carbon atoms free from aliphatic unsaturated bond. The options are the same as described for R 1 . Again, a substituted or unsubstituted alkyl group, particularly a methyl group is a preferred R 2 group because of ease of synthesis. Integer n is equal to or greater than m, and preferably in the range of 150 to 12,000, more preferably 200 to 10,000. Some of the above-mentioned advantages may be lost if n is smaller than m. Component (B) is blended in amounts of 5 to 80 parts, preferably 5 to 60 parts by weight per 100 parts by weight of component (A). Less than 5 parts by weight of component (B) on this basis may give a cured coating which is less lubricating and less abrasion resistant whereas more than 80 parts by weight of component (B) may give a cured coating which is rather low in mechanical strength and less abrasion resistant. Component (C) is either one or both of a silane and a siloxane oligomer, particularly an organosilane and/or an organosiloxane each having at least three hydrolysable functional groups in a molecule. It serves as a crosslinking agent to form a coating of a three-dimensional network structure by reacting with a hydroxyl group attached to a silicon atom in component (A) in the presence of the condensation catalyst (F). Examples of the hydrolysable functional group include alkoxy groups such as methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, tert-butoxy, methoxymethoxy, methoxyethoxy, ethoxymethoxy and ethoxyethoxy; alkenyloxy groups such as vinyloxy, allyloxy, propenoxy, isopropenoxy, butenoxy and isobutenoxy; ketoxime residues, i.e. iminoxy groups, such as dimethyl ketoxime, diethyl ketoxime, methylethyl ketoxime, butanoxime, pentanoxime and isopentanoxime; acyloxy groups such as acetoxy, propyonoxy, butyloyloxy and benzoyloxy; amide groups such as N-methylacetamide and N-ethylacetamide; aminoxy groups such as dimethylaminoxy and diethylaminoxy; isocyanate groups; and α-silylester groups. Beside the foregoing groups, chlorine and other halogen atoms can be used, but are undesirable because hydrogen halides resulting from hydrolysis are seriously corrosive and toxic. Other than the above-mentioned hydrolysable functional groups, substituted or unsubstituted monovalent hydrocarbon groups, preferably having 1 to 10 carbon atoms, may be attached to a silicon atom, Options for which are the same as described for R 1 , and preferably an alkyl group having 1 to 8 carbon atoms, an alkenyl group having 2 to 10 carbon atoms or a phenyl group for ease of synthesis. Examples of the silane having at least three hydrolysable functional groups in a molecule include alkoxy silanes such as methyltrimethoxysilane, vinyltrimethoxysilane, phenyltrimethoxysilane, methyltriethoxysilane, tetramethoxysilane, tetraethoxysilane, tetrapropoxysilane, and 3-chloropropyltrimethoxysilane; alkenyloxysilanes such as methyltriisopropenoxysilane, vinyltriisopropenoxysilane and phenyltriisopropenoxysilane; ketoximesilanes such as methyltris(methylethylketoxime)silane, vinyltris(methylethylketoxime)silane, phenyltris(methylethylketoxime)silane, methyltris(dimethylketoxime)silane, and tetrakis(methylethylketoxime)silane; acetoxysilanes such as methyltriacetoxysilane, vinyltriacetoxysilane, phenyltriacetoxysilane, and tetraacetoxysilane; amidosilanes such as methyltris(N-methylacetamido)silane and vinyltris(N-ethylacetamido)silane; aminoxysilanes such as methyltris(N,N-diethylaminoxy)silane and vinyltris(N,N-diethylaminoxy)silane; and partial hydrolyzates thereof. The organosiloxane having at least three hydrolysable functional groups in a molecule is siloxane oligomer having 2 to 10, preferably 3 to 6 silicon atoms, and has as the substituents directly bonded to the silicon atoms the hydrolysable functional groups and, optionally, unsubstituted or substituted monovalent hydrocarbon groups as given above. Preferably, the organosiloxane (siloxane oligomer) is one (so-called ester siloxane) in which the substituents directly bonded to the silicon atoms are all hydrolysable groups, particularly alkoxy groups. Examples of the siloxane having at least three hydrolysable functional groups in a molecule are shown below. Component (C) is blended in amounts of 0.2 to 30 parts, preferably 0.5 to 25 parts by weight per 100 parts by weight of component (A). Less than 0.2 parts by weight of component (C) on this basis may give insufficient curing of the composition whereas more than 30 parts by weight of component (C) may give a cured coating which is too hard and brittle to follow deformation of the underlying substrate. Component (D) is an organosilane containing at least two alkoxy groups, preferably 2 to 3 alkoxy groups, each attached to a silicon atom and a mercapto group attached to a silicon atom through an alkylene group in a molecule, a partial hydrolysate thereof, or a mixture of such an organosilane and a partial hydrolysate thereof. It is effective for providing good adherence to the rubber substrate when used in combination with component (E). It should be noted that the "partial hydrolysate" in component (D) and component (E) explained later means a condensate obtained by partially hydrolysing the silane so that at least two and preferably at least three alkoxy groups survive therein. The alkoxy group preferably has 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms. Examples of the alkoxy group include methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutoxy, tert-butoxy, methoxyethoxy, and ethoxyethoxy groups, with the methoxy and ethoxy groups being preferred for ease of synthesis. The alkylene group preferably has 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms. Examples of the alkylene group include methylene, ethylene, propylene, tetramethylene, hexamethylene, and methylethylene groups, with the propylene group being preferred for storage stability and ease of synthesis. The organosilane may have one or more organic groups on silicon atom, in addition to the alkoxy groups and the mercapto-alkylene group. These are selected from substituted and unsubstituted monovalent hydrocarbon groups having 1 to 8 carbon atoms as exemplified for R 1 , preferably an alkyl group such as a methyl group. Examples of the organosilane (D) include γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, γ-mercaptopropyltriethoxysilane, and partial hydrolysates thereof. Preferred among these is γ - mercaptopropyltrimethoxysilane, a partial hydrolysate thereof or a mixture thereof. Component (D) is blended in amounts of 1 to 20 parts, preferably 2 to 15 parts by weight per 100 parts by weight of component (A). Adhesion is usually poor with below 1 part by weight of component (D) whereas more than 20 parts by weight of component (D) usually gives no further advantage and may adversely affect the mechanical properties of a cured coating. Component (E) is an organosilane containing at least two alkoxy groups, preferably 2 to 3 alkoxy groups, each attached to a silicon atom and a substituted or unsubstituted amino group attached to a silicon atom through an alkylene group in a molecule, a partial hydrolysate thereof, or a mixture of such an organosilane and a partial hydrolysate thereof. It can be effective not only for providing good adherence to the rubber substrate when used in combination with component (D), but also for imparting lubricity to the cured coating. Examples of the alkoxy group include the same alkoxy groups described in component (D) such as methoxy, ethoxy, propoxy and butoxy groups, with the methoxy and ethoxy groups being preferred for ease of synthesis. Options for the alkylene group include the same alkylene groups as described for component (D), preferably a propylene group. Examples of the substituted or unsubstituted amino group include amino group, an alkyl-substituted amino group such as methylamino and ethylamino groups, an aminosubstituted amino group such as β-aminoethylamino group, and an aralkyl-substituted amino group such as benzylamino group. Examples of the substituted or unsubstituted amino group attached to a silicon atom through an alkylene group include aminomethyl, β-aminoethyl, γ-aminopropyl, δ-aminobutyl, γ-(methylamino)propyl, γ-(ethylamino)propyl, γ-(β-aminoethylamino)propyl, and γ-(benzylamino)propyl groups. The alkylene group is preferably a propylene group as in the γ-aminopropyl group when stability during storage is taken into account. The organosilane may have one or more organic groups on silicon atom, in addition to the alkoxy groups and the substituted or unsubstituted aminoalkylene group. These are selected from substituted and unsubstituted monovalent hydrocarbon groups having 1 to 8 carbon atoms as exemplified for R 1 , preferably an alkyl group such as a methyl group. Exemplary organosilanes as component (E) are γ-aminopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, N-β-(aminoethyl)-γ-aminopropyltrimethoxysilane, N-benzyl-γ-aminopropyltrimethoxysilane and partially hydrolysed products thereof. Among these, γ-aminopropyltriethoxysilane and a partial hydrolysate thereof are preferred. Component (E) is blended in amounts of 5 to 150 parts, preferably 10 to 100 parts by weight per 100 parts by weight of component (A). Less than 5 parts by weight of component (E) may give poor adhesion and lubricity whereas more than 150 parts by weight of component (E) may interfere with curing and adversely affect the mechanical properties of a cured coating. Component (F) is a condensation catalyst for promoting curing of the composition. It may be selected from conventional condensation catalysts commonly used in known condensation type RTV silicone compositions, for example, metal (Sn, Zn, Fe, etc.) salts of fatty acids such as dibutyltin diacetate, dibutyltin dioctoate, dibutyltin dilaurate, dibutyltin dioleate, dibutyltin distearate, dibutyltin benzylmaleate, tributyltin acetate, tributyltin octoate, tributyltin laurate, dioctyltin diacetate, dioctyltin dilaurate, diethyltin dioleate, monomethyltin dioleate, zinc octanoate, iron octanoate, tin octanoate, and iron stearate; titanates such as tetraisopropyl titanate and tetrabutyl titanate; and titanium chelates such as dimethoxytitanium diacetylacetonate. These condensation catalysts may be used alone or in admixture of two or more. Component (F) is blended in amounts of 0.1 to 30 parts, preferably 0.2 to 25 parts by weight per 100 parts by weight of components (A), (B) and (C) combined. Less than 0.1 part by weight of component (F) on this basis may fail to provide sufficient catalysis to accomplish curing whereas more than 30 parts by weight of component (F) may accelerate reaction too fast so that no appropriate pot life is available, and can adversely affect the heat resistance of a cured coating. Component (G) is a microparticulate powder having a mean particle size of up to 50 µm. It is effective for improving the abrasion resistance of a cured coating, eliminating gloss from the cured coating, and reducing a tacky feel on the coating surface. The powder is generally made of synthetic resin such as polycarbonate, nylon, polyethylene, Teflon®, (PTFE), polyacetal, polymethylsilsesquioxane and inorganic materials such as silica, zirconia and alumina, alone or in admixture of two or more. Preferred among these is polycarbonate resin. The microparticulate powder should have a mean particle size of up to 50 µm, usually 0.1 to 50 µm, preferably 0.3 to 30 µm. A mean particle size of more than 50 µm may adversely affect the mechanical strength and abrasion resistance of a cured coating. Powder particles with a mean particle size of less than 0.1 µm may be difficult to produce and less effective for abrasion resistance improvement. Preferably the powder particles are of spherical or flake shape although polygonal, irregular and fragmental shapes are acceptable. The particle color is not critical and may be determined for a particular application. For example, the particles may be colored black so as to obscure any discoloration of a coating when the underlying substrate is deformed. Component (G) or fine powder is blended in an amount of 2 to 40 parts, preferably 5 to 30 parts by weight per 100 parts by weight of components (A), (B) and (C) combined. Less than 2 parts by weight of the powder may be insufficient to render a coating abrasion resistant whereas more than 40 parts by weight of the powder may adversely affect the mechanical strength and hence, abrasion resistance of a cured coating. The microparticulate powder may be fed in powder form or dispersion or emulsion form in organic solvents or water. It is understood that microparticulate powder like component (G) is generally added to conventional curable resin compositions, for example, urethane resins and silicone resins for matting and improving abrasion resistance. When microparticulate powder is added to a coating composition, however, there sometimes arises a problem that in case particles themselves are non-bindable with the matrix resin, the particles can sometimes be separated from the matrix resin upon receipt of repetitive frictional forces. We can address this difficulty by using components (D) and (E) in combination to significantly improve the binding of particles to the matrix resin for thereby providing a cured coating with long-lasting abrasion resistance. Various additives and fillers may be blended in the compositions. Exemplary fillers are reinforcing fillers such as fumed silica and precipitated silica, which may have been treated to be hydrophobic, and non-reinforcing fillers such as silica aerogel, ground quartz, and diatomaceous earth. Various silicone resins and organic resins are also useful as reinforcing fillers. The fillers may be used alone or in admixture of two or more. The silicone resins used herein include silicone resins comprising a R 3 SiO 1/2 unit and a SiO 2 unit and/or RSiO 3/2 unit and optionally comprising R 2 SiO 2/2 unit, and silicone resins comprising a RSiO 3/2 unit, and optionally comprising R 3 SiO 1/2 unit and/or R 2 SiO 2/2 unit, with resins having a ≡SiOH or ≡SiOR group in a molecule being preferred. R represents a substituted or unsubstituted monovalent hydrocarbon group preferably having 1 to 8 carbon atoms, options being as for R 1 , particularly methyl, vinyl, phenyl and trifluoropropyl groups. Also the composition may contain inorganic pigments such as carbon black and iron oxide and UV absorbers such as carbon black and benzotriazoles. In addition to components (D) and (E) mentioned above, there can be added a silane coupling agent for improving adhesion to a substrate. Exemplary silane coupling agents include γ-glycidoxypropyltrimethoxysilane, γ-methacryloxypropyltrimethoxysilane, β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, and γ-acryloxytrimethoxysilane and partial hydrolysates thereof. The composition may be prepared simply by mixing the above-mentioned components uniformly. It is recommended to store the components in three separate packages, a mixture of components (A), (B) and (G), a mixture of components (C), (D) and (E), and component (F) and combine them together on use. When the composition is used as a surface treating agent for various rubber substrates, the composition may be used as such or after diluting with an organic solvent. Useful organic solvents include n-hexane, n-heptane, cyclohexane, industrial gasoline, petroleum naphtha, isoparaffin, benzene, toluene, xylene, isopropyl alcohol, butyl alcohol, cyclohexanone, methyl ethyl ketone, alone or in admixture of two or more. Preferred among these are industrial gasoline, petroleum naphtha, isoparaffin, or a mixture of one or more of them with isopropyl alcohol. The amount of the organic solvent used may be suitably determined in accordance with the viscosity desired for the composition on application. A rubber substrate can be surface treated with the compositions described herein by any desired technique, e.g. by conventional application techniques such as dipping, spraying, brush coating, knife coating, and roll coating. The coating, after drying to evaporate off the solvent where the solvent is used, is then cured by allowing to stand at room temperature or heating to an appropriate temperature. A cured coating is formed on the substrate surface in this way. Implementing these proposals, we have found that the surface of a substrate on which a cured coating of the present composition has been formed is non-tacky to a material which comes in contact therewith, water repellent and lubricating. The cured coating has good abrasion resistance and maintains it over a long time as compared with cured coatings of other, conventional organopolysiloxane compositions. Therefore, the compositions proposed here find best use in applications where frictional forces are repeatedly applied, for example, as a surface treating agent for rubber parts such as automotive weather strips and vibration damping rubber. EXAMPLE Examples of the present invention are given below by way of illustration and not by way of limitation. All parts are by weight. Example 1 To 1,000 parts of industrial gasoline No. 2 were added 100 parts of a both end hydroxyl-blocked dimethylpolysiloxane of the following average formula (1-1) and 15 parts of a dimethylpolysiloxane of the following average formula (2 - 1). 20 parts of spherical particles of polycarbonate resin having a mean particle size of 20 µm was added to the solution, which was agitated and mixed to form a powder dispersion. Then 10 parts of ethylpolysilicate (SiO 2 value 40%), 5 parts of γ-mercaptopropyltrimethoxysilane, and 35 parts of γ-aminopropyltriéthoxysilane were added to the dispersion, which was agitated and mixed. Finally 15 parts of a 50 wt% toluene solution of dibutyltin dilaurate was added to the dispersion, which was fully mixed to form a surface treating composition in industrial gasoline solution form. Example 2 A surface treating composition industrial gasoline solution form was prepared by the same procedure as Example 1 except that 100 parts of the both end hydroxyl-blocked dimethylpolysiloxane of formula (1-1) was replaced by a mixture of 70 parts of the both end hydroxyl-blocked dimethylpolysiloxane of formula (1-1) and 30 parts of a both end hydroxyl-blocked dimethylpolysiloxane of the following average formula (1-2). Comparative Example 1 A surface treating composition in industrial gasoline solution form was prepared by the same procedure as Example 1 except that the polycarbonate resin powder was omitted. Comparative Example 2 A surface treating composition in industrial gasoline solution form was prepared by the same procedure as Comparative Example 1 except that 15 parts of the dimethylpolysiloxane of formula (2-1) was replaced by 15 parts of a dimethylpolysiloxane of the following average formula (2-2). Comparative Example 3 A surface treating composition in industrial gasoline solution form was prepared by the same procedure as Example 2 except that the polycarbonate resin powder was omitted. Comparative Example 4 A surface treating composition in industrial gasoline solution form was prepared by the same procedure as Comparative Example 3 except that 15 parts of the dimethylpolysiloxane of formula (2-1) was replaced by 15 parts of a dimethylpolysiloxane of formula (2-2) as used in Comparative Example 2. Each of the surface treating liquids was spray coated onto a surface of EPDM sponge. The coating was dried in air for 5 minutes and heated at 100°C for 10 minutes to form a cured film 5 µm thick. The cured films resulting from the surface treating compositions within the scope of the invention (Examples 1 and 2) were tough, non-tacky, and lubricating. The cured films were examined by an abrasion test under the following conditions. Sliding abrasion test Tester reciprocal abrasion tester Frictional element glass plate 5 mm thick Load 200 grams Stroke 100 mm Frictional cycle 30 cycles/min. Repetitive friction was applied to the coated EPDM by reciprocally moving the frictional glass element over the coated EPDM under a load of 200 grams. During the test, the abrasion debris was sampled at intervals of 5,000 cycles. The reciprocal cycles were continued until debris of the underlying rubber was detected in the abrasion debris. The test results are shown in Table 1. For example, a test result of 55,000 cycles OK means that abrasion of the underlying rubber occurred between 55,000 and 60,000 cycles; and a test result of 30,000 cycles NG means that abrasion of the underlying rubber occurred between 25,000 and 30,000 cycles. Abrasion test cycles Example 1 55,000 cylces OK Comparative Example 1 30,000 cycles NG Comparative Example 2 20,000 cycles NG Example 2 60,000 cylces OK Comparative Example 3 35,000 cycles NG Comparative Example 4 20,000 cycles NG There have been described organopoly - siloxane compositions which are useful as a surface treating agent e.g. for cured moldings of various rubbers for imparting non-tackiness, water repellency and lubricity to the rubber surface and forming a coating which is durably abrasion resistant. Reference is made to JP-A-5/340045. Although some preferred embodiments have been described, many modifications and variations may be made thereto in the light of the above teachings. It is therefore to be understood that within the scope of the general teachings herein, the invention may be practised otherwise than as described in the Examples.

Claims: An organopolysiloxane composition comprising (A) 100 parts by weight of diorganopolysiloxane of the following general formula (1): wherein R 1 are substituted or unsubstituted monovalent hydrocarbon groups and m is in the range 150 to 10,000; (B) 5 to 80 parts by weight of diorganopolysiloxane of the following general formula (2): wherein R 2 are substituted or unsubstituted monovalent hydrocarbon groups and n is equal to or larger than m; (C) 0.2 to 30 parts by weight of silane and/or siloxane having per molecule at least three hydrolysable groups bonded to Si selected from alkoxy, alkenyloxy, ketoxime, acyloxy, amide, aminoxy, isocyanate, silylester and halogen groups, any other groups bonded to Si being selected from hydrocarbon groups which may be substituted with halogen atom or nitrile group and said siloxane if present being an oligomer having from 2 to 10 silicon atoms; (D) 1 to 20 parts by weight of organosilane having per molecule at least two alkoxy groups bonded to Si and a mercapto group bonded to Si through an alkylene group, any other group bonded to Si being C 1-8 hydrocarbon which may be substituted with halogen atom or nitrile group; and/or a partial hydrolysate of such organosilane; (E) 5 to 150 parts by weight of organosilane having per molecule at least two alkoxy groups bonded to Si and a substituted or unsubstituted amino group bonded to Si through an alkylene group, any other group bonded to Si being C 1-8 hydrocarbon which may be substituted with halogen atom or nitrile group, and/or a partial hydrolysate of such organosilane; (F) condensation catalyst in an amount of 0.1 to 30 parts by weight per 100 parts by weight of components (A) to (C) combined, and (G) microparticulate powder having a mean particle size of up to 50 µm in an amount of 2 to 40 parts by weight per 100 parts by weight of components (A) to (C) combined. A composition according to claim 1 in which, for component (A), m is in the range 200 to 10000. A composition according to claim 1 or claim 2 in which R 1 are methyl groups. A composition according to any one of the preceding claims in which, for component (B), n is in the range 200 to 10000. A composition according to any one of the preceding claims in which component (C) is alkoxysilane. A composition according to any one of the preceding claims in which component (C) is said siloxane oligomer and all the Si-bonded substituents thereon are alkoxy groups. A composition according to any one of the preceding claims in which component (D) is selected from γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, γ-mercaptopropyltriethoxysilane, and partial hydrolysates thereof. A composition according to any one of the preceding claims in which component (E) is selected from γ-aminopropyltriethoxysilane, γ-aminopropyltrimethoxysilane, N-β-(aminoethyl)-γ-aminopropyltrimethoxysilane, N-benzyl-γ-aminopropyltrimethoxysilane and partially hydrolysed products thereof. A composition according to any one of the preceding claims in which component (G) is of polycarbonate resin. A composition according to any one of the preceding claims, further comprising a silane coupling agent for improving substrate adhesion. A composition according to any one of the preceding claims in three-pack storage form, with a mixture of components (A), (B) and (C) separate from a mixture of (C), (D) and (E). A rubber article having a surface coating of a composition according to any one of claims 1 to 11 which has been cured. A rubber article according to claim 12 which is an automotive weather strip or rubber vibration damper. Use of a composition according to any one of claims 1 to 11 to form a surface coating on a substrate. Use according to claim 13 in which the substrate is of rubber.

Inventors: OKADA KAZUMI, SHIONO MIKIO, OKADA, KAZUMI, SHIONO, MIKIO, OKADA, KAZUMI, C/O SILICONE-ELECTR. MATERIALS LAB., SHIONO, MIKIO, C/O SILICONE-ELECTR. MATERIALS LAB.
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1994
Main classification: C09D183
IPC codes: C08L83, C09D183