Method of producing alloys suitable for hydrogen storage

Abstract: Disclosed are a hydrogen storage alloy which contains carbon in a proportion of from 30 to 500 ppm and is represented by the stoichiometric formula A x B 5.0 , wherein A is La or a mixture of La with at least one rare earth metal other than La, B is at least one metal selected from a group consisting of Al, Co, Cr, Cu, Fe, Mn, Ni, Ti, V, Zn and Zr, and x is a rational number in the range 0.95≦ x ≦ 1.00; and has a texture in which only the intermetallic compound phase named AB₅ phase is present and every other intermetallic compound phase is absent: and a method of producing said alloy and an electrode using the same.

Description: FIELD OF THE INVENTION The present invention relates to a method of producing alloys suitable for storage of hydrogen and electrodes using these alloys. BACKGROUND OF THE INVENTION Since alloys capable of storing and releasing hydrogen (which are abbreviated as "hydrogen storage alloys" hereinafter) were discovered and known to be applicable to the storage of hydrogen, it has been attempted to extend their application to a heat pump and a cell without limiting their use to the means of storing hydrogen. In particular, the alkaline rechargeable batteries using such alloys as negative electrode have reached nearly practical levels, and the alloys used therein have undergone successive improvements. More specifically, the LaNi 5 alloy which was first examined (Japanese Tokkai Sho 51-13934, wherein the term "Tokkai" means an "unexamined patent application") has an advantage in that it can store a large quantity of hydrogen. However, it has also disadvantages in that not only La metal is expensive but also the alloy tends to pulverize through the alternation of storage and release of hydrogen and to be corroded by an alkaline or acidic solution. When the above-cited alloy was used as the electrode of an alkaline rechargeable battery, therefore, it had high electric capacity in the early stage of use, but the electric capacity thereof was reduced to one half or less by about 50 times' repetition of a charge-discharge cycle. That is, such a battery cannot withstand the use of long duration. The drawbacks as described above were mitigated by partly replacing the lanthanum (La) with another rare earth element such as Ce, Pr, and Nd, and/or the nickel (Ni) with another metal such as Co, Al and Mn, (as disclosed in Japanese Tokkai Sho 53-4918, Japanese Tokkai Sho 54-64014, Japanese Tokkai Sho 60-250558, Japanese Tokkai Sho 61-91862 and Japanese Tokkai Sho 61-233969). Those alloys, although they were somewhat inferior to the LaNi 5 alloy in quantity of hydrogen stored therein, underwent improvements in liability to corrosion by alkaline and acid solutions and in charge-discharge cycle life of an alkaline rechargeable battery. However, they were still short in charge-discharge cycle life from an industrial point of view, and so it was hard to say that they had sufficient practical utility. The hydrogen storage alloys having the crystal structure of CaCu 5 type (which are hereinafter called the AB 5 type alloys) have a multiphase texture composed of various intermetallic compounds, metals and so on. This is a main reason why such alloys are, as described above, liable to be corroded by alkaline and acidic solutions. Further, it is considered that microcracks formed in the corroded intermetallic compound part push the alloys to be finely pulverized. Of the intermetallic compounds which constitute the AB 5 type alloy, it is supposed that the greater the proportion of the metal on the side A in an intermetallic compound, the more serious the corrosion by alkaline and acidic solutions. In order to solve the above-described problems, we have made intensive studies. As a result thereof, it has been found that the corrosion resistivity and the charge-discharge cycle life of a hydrogen storage alloy can be improved when an alloy contains only the intermetallic compound named AB 5 phase while every other intermetallic compound phase is absent in the alloy, thereby achieving the present invention. JP-A-51 56395 describes a molten Ni-based alloy having a modified carbon content which was cast in a copper mold to form an ingot of AB 5 type crystalline structure with (in weight %) 32-34% rare earth elements, 2.8-13.8% Co, 1.2-4.0% Al, ≤0.008% C and balance Ni. The ingot was annealed for 5 hours at a predetermined temperature within the range of 900 to 1000°C in an Ar atmosphere. It was then crushed in a jaw crusher to give coarse particles of diameter 2 mm or less, and further crushed in a ball mill to give particles of 350 mesh or less. US-A-4 409 180 describes a process for manufacturing intermetallic compounds whereby it is described that in the method comprising a casting step first a mixture of rare earth metals in the metallic form and nickel are melted, solidified and, if desired, thermally homogenized. After melting and casting and, if desired, homogenization at 900°C for 24 hours to precipitate nickel in excess of 5 atoms, the intermetallic compounds were crushed and then activated by exposure to dry, pure hydrogen gas. Therefore, it is an object of the present invention to provide a method of producing a hydrogen storage alloy wherein only the intermetallic compound named AB 5 -phase can be selectively casted. This object of the present invention is attained with a method of producing a hydrogen storage alloy which comprises weighing out and mixing metallic elements A and B in such amounts that the resulting mixture can have a composition A x B 5.0 , adding carbon to the metal mixture in an amount ranging from 30 to 500 ppm, fusing the admixture homogeneously, and then cooling the homogeneously fused metallic mixture at a speed of from 4 °C/sec to less than 100 °C /sec to deposit only the intermetallic compound named AB 5 phase and represented by the stoichiometric formula A x B 5.0 ; wherein A is La or a mixture of La with at least one rare earth metal other than La, B is at least one metal selected from a group consisting of Al, Co, Cu, Cr, Fe, Mn, Ni, Ti, V, Zn and Zr, and x is a rational number in the range 0.95 ≦ x ≦ 1.00. BRIEF DESCRIPTION OF DRAWING In Fig. 1, there are shown X-ray diffraction charts of the alloy textures obtained in Example 1 and Comparative Example 1 respectively. DETAILED DESCRIPTION OF THE INVENTION The hydrogen storage alloys prepared by the method of the present invention are represented by the stoichiometric formula A 0.95-1.0 B 5.0 , and their texture has only one intermetallic compound phase named the AB 5 phase. More specifically, any other intermetallic compound phases, that is, those named A 2 B 7 phase, AB 2 phase, AB 3 phase, AB phase and A 3 B phase, and any metal phases, that is, those named A phase and B phase, are absent in the alloy texture of the present invention. An alloy having the foregoing composition of mixed metals can be produced properly adopting a conventional method so far as some of the metallic elements described above are weighed out and mixed in respective amounts corresponding to the intended composition. In the production thereof, it is desirable in particular that the metals be fused using a high-frequency wave fusion method, an arc fusion method, a plasma jet flame fusion method, electron-beam fusion method or so on. In mixing metals, it is required to add carbon in such an amount that the hydrogen storage alloy to be produced may have a carbon content of from 30 to 500 ppm. The addition of a slight amount of carbon can inhibit other intermetallic compounds, such as those named the A 2 B 7 phase, the AB 2 phase and so on, from separating out, and enables the solidification of the AB 5 phase alone, thereby depositing the intermetallic compound named the AB 5 phase on the grain boundary. When the carbon content is less than 30 ppm, the deposition of intermetallic compounds other than the AB 5 phase cannot be inhibited. When the carbon content is increased beyond 500 ppm, on the other hand, the carbon deposited on the grain boundary is increased in quantity. The thus deposited carbon becomes an obstacle to the storage-and-release of hydrogen and, what is worse, accelerates the corrosion through the reaction of the excess carbon with hydrogen. In solidifying an alloy by cooling it after fusion, the intermetallic compounds constituting the alloy generally solidify in the order of decreasing melting point. In the production of a hydrogen storage in accordance with the method of the present invention, the alloy is solidified in the order, the AB 5 phase, the A 2 B 7 phase, the AB 2 phase, the AB 3 phase, the AB phase and the A 3 B phase. As for the alloy texture, therefore, grains are first formed in the AB 5 phase, and on this grain boundary comes to be present another intermetallic compound, mainly the intermetallic compound named the A 2 B 7 -phase. Hereupon, the addition of a slight amount of carbon causes the deposition of carbon on the grain boundary at the time of solidification of the AB 5 phase, and so it can inhibit the deposition of other intermetallic compounds named the A 2 B 7 phase, the AB 2 phase and so on respectively. Thus, the alloy cooled down is ground to give the hydrogen storage alloy powder constituted of only the intermetallic compound named the AB 5 phase. More specifically, a homogeneously fused mixture of the prescribed metals to which carbon is added in advance in an amount of from 30 to 500 ppm is cooled down at a cooling speed of from 4 to less than 100°C /sec, thereby obtaining grains of the AB 5 -phase. Cooling the fused mixture can be effected, e.g., by casting it in a mold cooled with water. As for the quick cooling method of fused metals, there are known the methods disclosed in Japanese Tokkai Sho 58-217609, Japanese Tokkai Sho 63-291363 and Japanese Tokkai Hei 3-216959. These methods utilize a rotating disc system, a rotating roll system and a gas atomizing system respectively, and have an advantage in that they make it unnecessary to grind the alloys produced thereby. Even if these methods are adopted in the present invention, however, they cannot provide the present hydrogen storage alloy which is represented by the stoichiometric formula A 0.95-1.0 B 5.0 and has the AB 5 phase alone. In case the alloys obtained using such methods are used as electrodes, the resulting batteries are low in retention rate of battery capacity. As a reason for the low capacity-retaining rate of such batteries, it can be thought that the alloys produced by those methods are amorphous powders because of high cooling speeds adopted therein which are over 100°C/sec, that is, higher than the suitable range for the present invention. In the alloy texture obtained by the present method, on the other hand, the intermetallic compound forms into remarkably fine grains. In other words, the gap between every pair of grains is narrowed due to fineness of the grains formed, and thereby can be lessened the grain boundary. Thus, it becomes possible to inhibit the deposition of other intermetallic compounds. Moreover, a negative electrode for an alkaline rechargeable battery can be easily prepared using the present hydrogen storage alloys in a conventional manner. For instance, the powder of an alloy according to the present invention is mixed with a small amount of binder, loaded in or on a conductive support, and then formed into an electrode. The hydrogen storage alloys prepared by the method of the present invention, as described hereinabove, can fully achieve their effects when they are used as negative electrode of an alkaline rechargeable battery. In addition, it is a matter of course that they can be used for their original purpose, that is, as a means of storing hydrogen, or for a heat pump and the like. In accordance with the present invention, there are produced the hydrogen storage alloys having greatly improved corrosion resistance to alkaline and acidic solutions since they have the stoichiometric formula of A 0.95-1.0 B 5.0 and their alloy texture has the AB 5 phase alone. Therefore, it can be emphatically said that when the present alloys are applied to the negative electrode of an alkaline rechargeable battery, higher performance than ever and a sufficiently long charge-discharge cycle life can be conferred on the battery. Now, the present invention will be illustrated in more detail by reference to the following examples. However, the invention should not be construed as being limited to these examples. EXAMPLES 1 TO 8 Metallic elements, La (purity: above 99%), Ce (purity: above 99% ), Pr (purity: above 99%), Nd (purity: above 99 %), Ni (purity: above 99%), Co (purity: above 99%), Al (purity: above 99%) and M (Mn, Fe, Cu), were weighed out and mixed in their respective amounts such that the resulting mixture might have a composition as set forth in Table 1. Thereto, carbon was added in an amount ranging from 50 to 400 ppm. Then, the carbon-added mixture was fused using a high-frequency wave fusion method, and cast in a mold cooled with water. Thus, the hydrogen storage alloy having the composition as shown in Table 1 was produced. In casting the fused mixture in the water-cooled mold, the cooling speed of the fused mixture was controlled by properly choosing the cast thickness from the range of 5 to 20 mm. The thus obtained alloys were each ground into fine grains having a size smaller than 75 µm to give a powder. A 10 g portion of this powder was admixed with 2.5 g of a 3 wt% aqueous solution of polyvinyl alcohol to make paste. The paste obtained was filled into a porous foam of Ni metal, dried and then formed with a press to make an electrode having a thickness of 0.5 to 1.0 mm. Further, the electrode was fitted with a lead wire to form in a negative electrode. As for the positive electrode, on the other hand, a porous sintered nickel was impregnated with Ni(OH) 2 , and then subjected to a formation treatment to make a NiOOH electrode. In producing an alkaline rechargeable battery, the thus made negative and positive electrodes were pasted together through a separator made of nonwoven polyolefin fabric, and 6 mole/l of KOH was used as electrolytic solution. The thus produced rechargeable battery was charged with electricity for 2 hours by sending thereto an electric current of 40mA, and then made to discharge an electric current of 20 mA until the battery voltage was dropped to 0.6 V. By repetition of this charge-discharge operation, the rechargeable battery was examined for charge-discharge cycle life at 20 °C. COMPARATIVE EXAMPLES 1 TO 7 Other hydrogen storage alloys having compositions as shown in Table 1 were produced in the same manner as in Examples described above, except that: in Comparative Examples 1 and 2 each, the metals were mixed in such amounts that the resulting mixture might have a composition beyond the scope of the present invention, namely the value x which is out of the range 0.95 ≦ x ≦ 1.00 in the stoichiometric formula A x B 5.0 ; in Comparative Examples 3, 6 and 7, the amounts of the carbon added was changed to 3,000 ppm, 1,000 ppm and 0 ppm, respectively; in Comparative Example 4, the mold used for casting was not cooled with water and the cooling speed was controlled to 3°C /sec by choosing the cast thickness of 20 mm; and in Comparative Example 5, the fused mixture was quickly cooled using a rotating roll system, and so the cooling speed was 110°C /sec. Alkaline rechargeable batteries were produced in the same way as in Examples described above, except that the alloys produced in Comparative Examples 1 to 7 were used for making negative electrodes, respectively; and then they each were charged and discharged alternately under the same conditions as in the foregoing Examples in order to examine for charge-discharge cycle life. The results obtained are shown in Table 2. Initial Battery Capacity C 0 (mAh/g) Battery Capacity After 300 cycles C 300 (mAh/g) Retention Rate of Capacity C 300 /C 0 (%) Example 1 286 255 89 Example 2 285 257 90 Example 3 282 262 93 Example 4 278 250 90 Example 5 278 236 85 Example 6 273 235 86 Example 7 271 233 88 Example 8 272 237 87 Comparativ Example 1 284 122 43 Comparative Example 2 283 133 40 Comparative Example 3 285 137 48 Comparative Example 4 283 139 49 Comparative Example 5 230 179 78 Comparative Example 6 318 97 31 Comparative Example 7 332 114 34 As can be seen from Table 2, all the rechargeable batteries produced in Examples 1 to 8 were markedly high in retention rate of battery capacity, compared with those produced in Comparative Examples 1 to 7. These experimental results demonstrate that the corrosion resistance of an alkaline rechargeable battery can be improved by the use of the negative electrode produced with the hydrogen storage alloy prepared with the method of the present invention. Then, the X-ray diffraction charts of the alloy textures obtained in Example 1 and Comparative Example 1 respectively are shown in Fig. 1. While the chart of the alloy produced in Comparative Example 1, as noticed by Fig. 1, has the peaks ascribable to the intermetallic compound named the A 2 B 7 phase (which are marked with ○), all the peaks present in the chart of the alloy produced in Example 1 are attributable to the intermetallic compound named the AB 5 phase. This fact proves that the texture of the present by prepared hydrogen storage alloy has the AB 5 phase alone, thereby effecting the improvement in corrosion resistance. Similarly to the above, it has been ascertained that each of the alloy textures obtained in Examples 2 to 8 had the AB 5 phase alone, while each obtained in Comparative Examples 2 to 7 had the A 2 B 7 phase in addition to the AB 5 phase. Additionally, the hydrogen storage alloy produced in Comparative Example 5 was an amorphous powder since it had undergone the quick cooling with the rotating roll system. Although the resulting battery was rather high in retention rate of capacity, the amorphous state of the alloy is supposed to be responsible for the drop in initial battery capacity.

Claims: A method of producing a hydrogen storage alloy: which comprises weighing out and mixing metallic elements A and B in such amounts that the resulting mixture can have a composition A x B 5.0 , adding carbon to the metal mixture in an amount ranging from 30 to 500 ppm, fusing the admixture homogeneously, and then cooling the homogeneously fused metallic mixture at a speed of from 4 °C/sec to less than 100 °C/sec to deposit only the intermetallic compound named AB 5 phase and represented by the stoichiometric formula A x B 5.0 ; wherein A is La or a mixture of La with at least one rare earth metal other than La, B is at least one metal selected from a group consisting of Al, Co, Cu, Cr, Fe, Mn, Ni, Ti, V, Zn and Zr, and x is a rational number in the range 0.95 ≦ x ≦ 1.00. A method of producing a hydrogen storage alloy according to claim 1, wherein B is at least one metal selected from a group consisting of Al, Co, Cu, Fe, Mn and Ni.

Inventors: TAJIMA SHIGENOBU, TAKAI YASUSHI, TOIDE TAKASHI, YAMADA KAZUHIRO, TAJIMA, SHIGENOBU, TAKAI, YASUSHI, TOIDE, TAKASHI, YAMADA, KAZUHIRO, YAMADA, KAZUHIRO EAST 702, AKORU SHIN-TOKOROZAWA
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1994
Main classification: H01M4
IPC codes: C01B3, H01M4, C22C19, C22C14, C22C1