Manufacture of electrodes

Abstract: An electrode suitable for use in fuel cells, for example in solid polymer fuel cells, comprises a non-uniform electrode layer and has improved electrochemical performance

Description: This invention concerns improved electrodes and method of manufacture of electrodes, and in particular a gas diffusion electrode with an improved performance and a method of manufacture of such electrodes for use in fuel cells. It is useful to recall that in a fuel cell, a fuel, which may be hydrogen, a hydrocarbon or an oxygen-containing fuel such as methanol, is oxidised at a fuel electrode (anode) and oxygen is reduced at the cathode. An electrolyte contacts the electrodes and may be alkaline or acidic, liquid or solid. The liquid electrolyte phosphoric acid fuel cell (PAFC) operating at a temperature of 190°C-210°C, is the type of fuel cell closest to commercialisation and will find applications in the multi-megawatt utility power generation market and also as combined heat and power, ie co-generation systems, in the 50 to several hundred kilowatt range. Fuel cells in which the electrolyte is a solid polymer are known as solid polymer fuel cells, (SPFCs), or proton exchange membrane fuel cells, (PEMFCs). The solid proton-conducting polymer membrane electrolytes, commonly based on perfluorosulphonic acid materials, have to be maintained in a hydrated form during operation in order to prevent loss of ionic conduction through the electrolyte. This limits the operating temperature of the SPFC typically to between 80°C and 120°C dependent on the operating pressure. The SPFC does, however, provide much higher power density output than the PAFC, and can operate efficiently at much lower temperatures. Because of this it is envisaged that the SPFC will find use in applications such as small scale residential power generation and in vehicular power generation. In particular, zero emissions regulations have been passed in areas of the United States which are likely to restrict the use of combustion engines in the future. Prototype SPFC-powered vehicles are now being demonstrated for these applications. In these fuel cells, both the anode reaction, at which the fuel is oxidised, and the cathode reaction, at which oxygen is reduced, require electrocatalysts in order to proceed at useful rates. Precious metals, and in particular platinum, have been found to be the most efficient and stable electrocatalysts for all low temperature fuel cells, operating at below 300°C, in which the electrolyte may be acidic or alkaline in nature, but are particularly useful in acid electrolyte fuel cells such as the SPFC. The platinum electrocatalyst is provided as very small particles (20-50 Å ), of high surface area, which are often, but not always, distributed on, and supported by, larger microscopic conducting carbon particles to provide a desired catalytic loading. Electrodes are formed from the electrocatalyst material and, for the fuel cell reactions to proceed efficiently, these electrodes are designed to optimise contact between the reactant gas, the electrolyte, and the precious metal electrocatalyst. The electrode has to be porous, and is often known as a gas diffusion (or gas porous) electrode, in order to allow the reactant gas to enter the electrode from the back, the electrolyte to penetrate through the front, and products, particularly water, to diffuse out of the electrode. Efficient porous gas diffusion electrodes, using platinum loadings of 0.2-0.5mg/cm 2 of electrode area, have been developed for fuel cells using liquid acid electrolytes such as the PAFC. The electrolyte can penetrate the portion of the porous structure of the catalysed carbon support which contains most of the platinum electrocatalyst, and in practice above 90% of the electrocatalyst is effectively utilised to carry out the fuel reactions. In practice gas diffusion electrodes comprise the electrocatalyst material and other non-catalytic components, such as polymeric binders, formed as one or more layers, and supported on a porous conducting substrate material, for example, conducting carbon materials (papers, cloths, foams) or, particularly in the case of non-acid fuel cells, metal meshes of nickel or steel grids. In the SPFC the electrodes are bonded to the solid polymer electrolyte, which is in the form of a thin membrane, to form a single integral unit, known as the membrane electrode assembly (MEA). It has been found that the supported catalysed porous gas diffusion electrodes, developed for the PAFC, are in general, unsuitable for use with SPFCs, as only very low current densities are usually attainable. This is because very little of the platinum electrocatalyst surface is present at the three-phase interface, ie where the membrane electrolyte is in direct contact with the electrocatalyst surface and an adjacent gas pore. This occurs most readily at the front surface of the electrode where bonding to the membrane occurs. Very little of the depth of the electrode is used as the electrolyte does not penetrate into the depth of the electrode. State of the art solid polymer fuel cells therefore utilise electrodes containing unsupported platinum black with relatively high noble metal loadings, typically 4mg/cm 2 per electrode, in order to maximise the level of platinum contact at the front face of the electrode. Despite the low platinum utilisation, the performance of the state of the art SPFCs is high compared to the PAFC. Current densities of 500mA/cm 2 at 0.72V, with H 2 /air as reactants, at a temperature of 80°C and a pressure of Satm, have been reported. However, the platinum requirement of these state of the art electrodes is close to 20g/kW. For reasons of cost it is widely accepted that the platinum requirement needs to be reduced to levels of around 0.5g/kW and below for the SPFC to become a viable system for widespread transportation applications. Furthermore, the operating current density needs to be increased to over 1A/cm 2 , whilst maintaining cell voltage at around 0.7V, in order to increase the power density output of the stacks ( ie reduce the volume taken up by the stack for a given power output). Significant increases in the effective surface area of the electrocatalyst utilised in these electrodes is required to reduce costs and improve performance. There have, therefore, recently been disclosed a number of methods in which the proton-conducting electrolyte is incorporated into the electrode structure in order to increase the extent of the three-phase interface. For example, USP 4,876,115 (United States Department of Energy) discloses an SPFC having electrodes which are modified carbon supported catalysed porous gas diffusion electrodes, formed by applying a solution of a soluble form of a proton-conducting material over the front face of a porous gas diffusion electrode. The preferred electrolyte material is a perfluorocarbon copolymer marketed by E I du Pont, under the trade mark Nafion . WO 92/15121 (United States Department of Energy) also discloses an SPFC electrode in which very thin electrode layers are formed from inks comprising the carbon-supported platinum electrocatalyst and solubilised Nafion. The effective platinum surface at the interface is increased, and it is possible to achieve similar performances to the unsupported state of the art platinum black electrodes, at platinum loadings less than 0.5mg/cm 2 . Even though the platinum utilisation is increased, it is still necessary to develop higher performance, lower cost electrode structures in which the electrocatalyst material is used as efficiently as possible, and in which the rates of reactant gas supply and product removal are sufficiently high to enable practically useful densities, and hence cell power densities, to be attained. Gas diffusion electrodes are also used in a wide variety of other electrochemical cells in addition to hydrogen-oxygen (air) fuel cells. Other applications include metal-air batteries, metal oxide-hydrogen batteries, chlor-alkali cathodes, ozone generation cathodes and selective gas sensor devices. The materials used in the formation of such electrodes generally comprise the active electrocatalytic metal (or a combination of more than one metal), in the form of either finely divided metal (or oxide) or dispersed and supported on a suitable electrically conducting support, such as particulate carbon, often in combination with various other electrically conducting carbons and polymers, particularly fluoropolymers such as polytetrafluoroethylene. The active electrocatalytic layer is usually applied, and securely bonded, to a rigid electrically conducting substrate such as carbon fibre paper, carbon cloth or metal mesh. In order to fabricate gas diffusion electrode layers a wide range of processes have been utilised. There are many examples in the prior art of processes which have been employed to produce gas diffusion electrodes, including filtration, powder vacuum deposition, spray deposition, electrodeposition, casting, extrusion, rolling and printing. It is important to note that the technology of these electrode manufacturing processes has primarily been concerned with the formation of one or more uniform layers of the active electrocatalyst component, in terms of either the homogeneity of the formulation of the active layer components and/or the layer thickness. For example, in US 4,313,972 (United Technologies Corporation), a process for making a gas diffusion electrode is described in which a dry powder comprising carbon and a hydrophobic polymer is applied as a uniform layer on the surface of the substrate by dispersing the powder as a cloud of particles in a chamber over the substrate and pulling the powder onto the substrate by applying a vacuum. In EP 0 026 979 (Asahi Glass Company Ltd) it has been proposed to use a printing process (screen printing) to form the electrode layer by screen printing a paste comprising an electrode powder on the surface of a cation exchange membrane using a screen of mesh number 10 to 2400 and a thickness of 4µm to 2mm. The electrode layer is then calendered (bonded) onto the membrane. The electrode layer being of uniform thickness is formed on one or both of the surfaces of the cation exchange membrane. The paste comprises the electrode powder for example platinum and a hydrophobic polymer for example polytetrafluoroethylene (PTFE). It is prepared according to US 4,585,711 by dispersing the platinum on carbon catalyst and embedding it in PTFE strands by a blending process. In US 3,423,247 (Union Carbide Corporation) is disclosed an electrode comprising a porous conductive body having at least two zones. The first zone extends inwardly from the electrolyte side of the electrode, which is highly permeable to the liquid electrolyte and extremely active electrochemically; and a second zone, adjacent the first zone, which is gas-permeable and highly repellant to the liquid electrolyte. Each zone is made up from a plurality of layers each of which is itself uniform in composition and thickness across the whole of the electrode face so as to provide gradients of electrolyte repellency and electrochemical activity between the two surfaces. A preferred method for manufacture of the electrodes is thermoplastic bonding. The disclosure in US 4,091,176 (Stamicarbon, BV) describes a porous multilayer electrode with the layers being formed by bonding together the required number of layers. In US 4,185,131 (United Technology Corporation) is disclosed an electrochemical cell electrode which is manufactured by screen printing an electroconducting material onto a porous substrate and finally catalysing the electroconducting layer. A series of layers of electroconducting material can be built up with the final step being catalysing the outermost layer. It is stated in this disclosure that one drawback of this method is that it is not suitable for use with pre-catalysed carbon. European patent application EP 0 100 548 (Asahi Glass Company Ltd) discloses a method of manufacture of a gas diffusion electrode in which a modified carbon black powder (partially graphitised) is uniformly incorporated into a three-dimensional net-work structure of PTFE. In US 4,585,711 (Communications Satellite) is disclosed a method of manufacturing a gas diffusion electrode in which the catalytic electrode layer is bonded to one side of a conductive grid and to the other side of the grid is bonded a semi-permeable layer of PTFE. The electrocatalytic layer is dispersed in a matrix of filamentary PTFE. In WO 92/15121 (United States Department of Energy) very thin active catalyst layers comprising a composite film are formed by dispersing supported platinum electrocatalyst, at platinum loadings of less than 0.35mg/cm 2 , in a film of proton conducting material. The film is applied to a solid polymer electrolyte membrane by transfer from a teflon release blank under temperature and pressure. The active layer is uniformly thin, and contains a uniform dispersion of the supported electrocatalyst layer in the proton conducting binder layer. Ideally the electrolyte should penetrate into the electrode sufficiently to reach the interior surfaces of the electrode and thereby contact the reactant gases in the presence of the electrocatalyst in as many places as possible. On the other hand, the electrode must be sufficiently hydrophobic in chatacter to prevent the electrolyte or water from totally filling the pores of the electrodes, which can cause flooding of the electrode. When flooding occurs, it becomes more difficult for the reactant gases to diffuse through to the catalyst sites and also more difficult for the product of the fuel cell reaction to diffuse out of the electrode structure and the cell performance drops. The disclosure in EP 0110491 (Westinghouse Electric Corporation) seeks to overcome this problem of flooding by preparing an electrode in which catalyst is dispersed equally through the plane of the electrode which is parallel with the substrate. This is achieved by depositing layers onto a substrate in which each layer contains different proportions of catalyst and hydrophobic and hydrophilic agglomerates. This layered structure assists in maintaining a correct balance between electrode pores which are electrolyte-repellant and allow gas flow, and those which are wettable to the electrolyte and fill with electrolyte material. The technology of electrode manufacture has primarily been concerned with the composition of the electrocatalyst layer and the processes used to produce a uniform layer of the catalytically active material which in turn could be securely and conductively bonded onto a chosen substrate. There are many examples of patents which have been directed to producing improved electrodes to achieve particular structural and operational requirements. In GB 1,392,353 (Zlehit) it is disclosed that an electrode with an improved efficiency results from a process whereby a metal grid supports both a catalytic-layer and a gas-permeable layer such that the layers interpenetrate with each other at the interface. This provides a gradient of electrocatalyst which decreases in concentration in a direction away from the substrate. The disclosure in GB 1,361,985 describes a method for preparing an electrode in which a first fibrous layer containing catalyst is deposited on a substrate and a second layer of material (a coating) is deposited on top of the first layer. The advantage of this electrode structure is that the catalyst powder is retained on the substrate. Catalyst from the first layer intermixes to a limited extent with the second layer such that there is a decrease in concentration of catalyst in a direction away from and perpendicular to the substrate. The teaching in US 4,185,131 is directed to producing electrodes of uniform quality and of a single layer by using the technique of screen printing. The electrocatalyst is present in a concentration which is equal in all directions with respect to the substrate. In US 3,979,227 (Katz et al ) an electrode structure is disclosed in which a post-catalysation stage achieves deposition of almost all of the catalyst onto a single hydrophilic region with minimal deposition in a single hydrophobic material. The concentration of the electrocatalyst decreases moving in a direction perpendicular to the substrate. The advantage of this deposition is stated to be that there is an improved utilisation of electrocatalyst because deposition occurs at points where electrolyte will contact the hydrophilic region. In each unit cell of a practical fuel cell stack the reactant gases are introduced into the back of the electrode through a manifold and then pass down the back face of the electrode via a single or a multiplicity of channels which are formed either in the back of the electrode-supporting substrate or in a separate gas flow channel plate in close contact with the back of the electrode. As gas passes along the channels its composition will change as the reactant is consumed and the products formed. For example, in the cathode of acid electrolyte fuel cell, where oxygen is reduced, the oxygen concentration will decrease, the relative humidity increase, and the temperature increase as the reactant gas passes along the gas flow channel from the entrance of the cell to the exit from the cell. Similarly, in the anode gas flow channel, changes in gas composition and temperature will occur as the hydrogen fuel in the presence of water vapour is consumed. The situation may also be further complicated in the anode if the hydrogen fuel, rather than being supplied as pure hydrogen, is provided from a hydrocarbon fossil fuel (such as methanol or methane) which has been separately converted into hydrogen using well established chemical processes, such as steam reforming or partial oxidation. In this case the hydrogen fuel will contain substantial levels of carbon dioxide (up to 25% by volume if the methanol has been steam reformed with water to produce the hydrogen) and trace levels of carbon monoxide (from 1ppm up to 2%). Changes in the concentration of these gases will occur both as the hydrogen is consumed, and also due to the presence of non-electrochemical gas phase reactions which are known to occur on the catalyst surfaces of the electrode material, at fuel cell operating temperatures. Of particular concern is the presence and further formation of carbon monoxide which acts as a platinum catalyst poison by strongly bonding to the catalyst surface and inhibiting the desired hydrogen oxidation reaction. As is exemplified in the prior art reviewed above, it is important to appreciate that with all current electrode fabrication processes, uniform layers of the electrode component materials, in terms of active electrocatalyst loading and composition of the electrode constituents, are formed in the direction corresponding to the plane of the electrode substrate. At any point along the gas flow channel the composition of the electrode which is exposed to the reactant gases is essentially constant. It is thus apparent that due to the presence of reactant gas composition and temperature gradients, each cell provides an averaged performance which is substantially lower than could be achieved. One reason for this is that in some areas across the face of the electrode, the active electrocatalyst can be operating at less than full utilisation, ie low efficiency, and in other areas there is insufficient active material for the catalytic functions to be performed to their maximum capability. It is therefore not advantageous to form gas diffusion electrodes with uniform layers in the plane of the face of the electrode when reactant gas composition or temperature gradients exist. US patent number 4,851,377 (International Fuel Cells Corporation) has attempted to address this problem by forming an electrode with a non-uniform electrocatalyst loading. The non-uniformity is taught as increasing the concentration of the electrocatalyst layer along one axis of the electrode, the axis being parallel to the electrode substrate. The stated advantage of this non-uniformity is that a progressive increase in electrocatalyst loading is required corresponding with the direction along the gas flow channel from the inlet to the outlet so that a uniform current distribution is achieved across the surface of the electrode. The aim of this invention is to address these problems at the manufacturing stage of the electrode. This will allow matching of the electrode active layer formulation and structure, to the gas flow/water transport/utilisation requirements of the specific cell design. In particular, the use of screen printing allows the pre-determined and controlled application of one or more electrode layers which can be tailored to match gas flow patterns and gradients. Further refinements can be achieved by varying the print pattern across the cell and by using multiple layers to control both the depth and structure of the layers within the pattern. Thus this invention provides a method of varying the electrochemical activity characteristics across the plane of the electrode surface to accommodate variations in gas concentration and flow, water flux and temperature variation. The advantages of the present invention are to provide a higher performance, lower cost gas diffusion electrode material, for application in fuel cells, in which the composition and structure of the electrode material, is specifically tailored to match the operational requirements of the cell and thereby both maximise the electrochemical performance attainable from the cell, and maximise the efficient use of the precious metal-based electrocatalyst and other components. The present invention provides a gas-liquid permeable porous electrode comprising a first electrocatalyst layer and a second non-uniform electrode layer supported on at least one side of a substrate, wherein said second non-uniform electrode layer consists essentially of a gas-phase catalyst adapted to reduce the concentration of carbon monoxide, and PTFE, characterised in that the concentration of said gas-phase catalyst varies across the plane of the electrode. The substrate can be either an electron conducting material or a proton conducting solid polymer membrane film. The non-uniform layer may be applied to at least one face of the substrate and this substrate can be an electron conducting material or a proton conducting solid polymer membrane film. Similarly the layer can be applied to one face of the substrate or applied to more than one face of the substrate, for example a gas face and electrolyte face. The electrode may form either an anode or a cathode in a fuel cell. The invention also provides a membrane electrode assembly wherein at least one of said electrodes is according to the invention. Suitably the electrode assembly forms a fuel cell comprising at least one electrode manufactured in accordance with the invention. The invention also provides a process for the production of an electrode comprising the steps: i) preparation of a paste of a gas-phase catalyst adapted to reduce the concentration of carbon monoxide and PTFE, ii) transferring the paste onto one or more sides of a substrate to form a non-uniform electrode layer, such that the concentration of said paste varies across the plane of the electrode, and (iii) applying an electrocatalyst layer. Preferably the non-uniform electrode layer is in the form of a pattern and suitably the non-uniform layer is formed by using a screen printing technique. The advantage of this technique is that it is particularly simple to fabricate the non-uniform electrode layer and possibly is the most appropriate technique to prepare the layer coincident with a gas field flow or some other desirable geometry. Where required multiple electrode layers can be built up using this technique. The invention will be described by way of the following Example which is to be regarded as illustrative and not limiting. The following Figure is illustrative of the embodiment described herein: Figure 1: illustrates the improved electrode performance when a gas-phase catalyst is present at the gas inlet. The term "performance" is a measure of the cell voltage obtained at a particular current density in a complete single cell operating under defined conditions. A single cell unit comprises an anode, a cathode and an electrolyte, together commonly referred to as a membrane electrode assembly (MEA), in the case of the PEM fuel cell; there are also conducting current collector plates into which gas flow channels are formed into one surface to provide access for reactant hydrogen and oxygen gases to reach the anode and cathode respectively. It is usual for the face of the electrode comprising the electrocatalyst containing electrode layer to be in contact with the surface of the membrane electrolyte. The reactant gases are then fed through the porous conducting substrate material to reach the electrocatalyst surface. The geometric surface area of the face of each electrode comprising the electrode layer was 232cm 2 , and the single cell was representative of the cells used in currently available PEMFC stacks. The cell was operated under practical conditions employed for PEMFC stack operation. The reactant gases which were humidified to prevent the solid electrolyte membrane film from drying out during the performance measurements were fed to the cell as hydrogen at 30 psig pressure, and air also at 30psig pressure. The temperature of the cell was maintained at 80°C. The current density taken from the cell was adjusted by applying a variable electrical load in controlled increments and the resulting cell voltage was measured when steady. The electrodes of the invention were evaluated as either cathodes with a standard anode or as anodes with a standard cathode, as described in the following Example. Although the Example refers to the benefits of the electrode being demonstrated in a solid polymer fuel cell application, to those skilled in the art, it can be seen clearly that the electrodes of the invention would have benefit in all other fuel cell types ( eg phosphoric acid, alkaline, direct methanol oxidation), and indeed other applications of gas diffusion electrodes, as detailed in the previous discussion. In this example the non-uniform electrode layer takes the form of a gas-phase catalyst containing layer which is applied to the substrate only in the region corresponding to the gas inlet and not in the region corresponding to the gas outlet. In this particular example the electrocatalyst containing layer is itself a conventional uniform layer and is applied on top of the non-uniform gas-phase catalyst containing electrode layer. The benefit of this non-uniform electrode is improved performance as a hydrogen oxidation anode operating on hydrogen fuel which contains low levels of carbon monoxide impurities as usually found in a hydrogen fuel source derived from the reformation of fossil fuels such as methane or methanol. Example 1 A hydrogen oxidation anode was formed by coating a porous electronically conducting carbon fibre paper substrate on one surface with a mixture comprising carbon supported platinum gas phase catalyst and an aqueous suspension of polytetrafluoroethylene (PTFE), to form an electrode layer. The catalyst comprised 20wt%Pt supported on Cabot Vulcan XC72R carbon, fabricated via the method disclosed in US 5,068,161. The proportion of PTFE in the electrode layer was 30wt%. The layer loading was varied across the surface of the electrode substrate such that only the region corresponding to the inlet one third of the gas flow path was coated with the electrode layer. The platinum loading in the coated region was 0.35mg/cm 2 . The total average platinum loading across the whole active area of the anode was thus 0.12 mg/cm 2 . The electrode can be fabricated by, for example, filter transfer, or rolling or spreading over the substrate surface. The electrode was dried and fired for 15 minutes at 350°C in nitrogen. A second electrocatalyst containing layer was then applied over the top of the gas phase catalyst layer. The electrocatalyst layer was a uniform layer coated evenly over the whole 232cm 2 geometric active area of the electrode. A carbon supported Pt/Ru catalyst, comprising 20wt%Pt/10wt%Ru supported on Cabot Vulcan XC72R was mixed with a soluble form of Nafion solid polymer electrolyte membrane, produced by Solution Technology of Mendenhall, Pennsylvania, USA, and referred to as a 5% solution of Nafion EW1100, to form a paste which was applied to the electrode by any of the techniques commonly practised by those skilled in the art; for example, screen printing, rolling or spreading. The loading of platinum in this layer was 0.25mg/cm 2 across the whole of the electrode surface. The electrode was dried under vacuum at 70°C to complete the fabrication. An MEA was formed with a standard cathode which comprised a uniform layer of 4.0mg/cm 2 unsupported platinum black loading and an experimental membrane produced by the Dow Chemical Company, Freeport, Texas, USA & referred to as XUS-13204.10. The membrane was cleaned prior to forming the MEA. Comparative Example 1 A conventional low platinum loading uniform layer anode was fabricated by coating a similar porous electronically conducting carbon fibre paper substrate on one surface with a paste mixture comprising the carbon supported Pt/Ru catalyst as described in Example 1, and the soluble form of Nafion solid polymer electrolyte membrane. The paste was applied in a similar manner to that described in Example 1, to form a uniform layer with a platinum loading of 0.25mg/cm 2 across the whole of the electrode surface. The electrode was dried under vacuum at 70°C to complete the fabrication. An MEA was fabricated as described in Example 1. The results are shown in Figure 1. Example 1 of the invention is referred to in the Figure legend as the "patch" electrode, and the conventional Comparative Example 1 as the "single layer". The cell voltage performance at a current density of 700A/ft 2 is measured as a function of air bleed concentration in the hydrogen fuel. This technique as described in US 4,910,099 involves the introduction of a small quantity of air into the hydrogen fuel stream to cause oxidation of low levels of carbon monoxide impurities, which would otherwise cause a performance decrease due to electrocatalyst poisoning. Figure 1 shows that at zero air bleed the performance of the Comparative Example 1, with a single uniform electrode layer, is reduced when the hydrogen fuel was replaced with a fuel containing 40ppm carbon monoxide (CO). As an air bleed is introduced and the level increased, the performance increases and eventually reaches that of the hydrogen fuel with no carbon monoxide poison. With the non-uniform electrode of Example 1, some performance reduction is again observed at zero air bleed, but due to the presence of the gas phase catalyst layer, the performance increases much more rapidly as the air bleed is introduced. This is due to the presence of the gas-phase catalyst containing layer promoting the more efficient oxidation of the carbon monoxide poison before it reaches the electrocatalyst containing layer.

Claims: A gas-liquid permeable porous electrode comprising a first electrocatalyst layer and a second non-uniform electrode layer supported on at least one side of a substrate, wherein said second non-uniform electrode layer consists essentially of a gas-phase catalyst adapted to reduce the concentration of carbon monoxide, and PTFE, characterised in that the concentration of said gas-phase catalyst varies across the plane of the electrode. An electrode according to claim 1, wherein the concentration of said gas-phase catalyst is such that the gas-phase catalyst-containing layer is applied to the substrate only in the region corresponding to the gas inlet and not in the region corresponding to the gas outlet. An electrode according to any preceding claim, wherein said electrode is for use as an anode in a fuel cell. A membrane electrode assembly, wherein at least one of the electrodes is according to any one of claims 1 to 3. A fuel cell comprising an electrode according to any one of claims 1 to 3. A process for the production of an electrode according to any one of claims 1 to 3 said process comprising the steps of (i) preparing a paste of a gas-phase catalyst adapted to reduce the concentration of carbon monoxide and PTFE, (ii) applying said paste to one or more sides of a substrate to form a non-uniform electrode layer such that the concentration of said paste varies across the plane of the electrode, and (iii) applying an electrocatalyst layer. A process according to claim 8, wherein said non-uniform layer is formed using a screen printing technique.

Inventors: FROST JONATHAN CHARLES, GASCOYNE JOHN MALCOLM, HARDS GRAHAM ALAN, FROST, JONATHAN CHARLES, GASCOYNE, JOHN MALCOLM, HARDS, GRAHAM ALAN
Applicants: JOHNSON MATTHEY PLC, JOHNSON MATTHEY PUBLIC LIMITED COMPANY
Application year: 1994
Main classification: H01M4
IPC codes: H01M8, H01M4