Process for preparing photovoltaic modules based on crystalline silicon

Abstract: A process for preparing low-cost photovoltaic modules based on crystalline silicon, characterised in that the semiconductor is treated while supported on a substrate having properties compatible with the process.

Description: This invention relates to a process for preparing photovoltaic modules based on thin crystalline silicon. Photovoltaic modules based on crystalline silicon have been produced for some time and are used to generate electrical energy. In currently used production methods, as described for example by Martin A. Green in "Solar Cells, Operating Principles, Technology and System Applications" Prentice-Hall Inc. N.J., the modules consist of individual solar cells bonded together to form an assembly of cells electrically connected together in series or parallel. This assembly is then encapsulated between a high transmittance glass sheet and a further sheet of glass or suitable plastics material as rear protection. The entire unit is then sealed with a polymer resin. These processes use silicon sheets having a thickness exceeding 350-500 µm. Process evaluation indicates that a considerable decrease in the cost per watt can be achieved by reducing the thickness and hence the quantity of silicon. The problem is that the fragility of the material increases as the thickness decreases and the area increases, and in addition the photovoltaic module process production yield falls drastically when the wafer thickness falls below 300 µm. We have now solved these problems by a low-cost production process for photovoltaic modules in which thin large-area wafers of silicon are involved. In accordance therewith the present invention provides a process for preparing photovoltaic modules based on mono and polycrystalline silicon, as claimed in claim 1. Preferred features of the process are claimed in the dependent claims 2-7. US-A-4,184,903 discloses a method for fabricating a photovoltaic module wherein a plurality of electrically interconnected solar cells are bonded to a rigid transparent support panel, comprising the steps of depositing on one face of each solar cell a film of substantially transparent adhesive, positioning said one face of each cell in contiguous relation with a common surface of a transparent support panel and simultaneously vacuum-bonding said plurality of cells to the panel. FR-A-2,481,522 discloses a method for fabricating a photovoltaic module comprising the steps of depositing on a face of a silicon disk, doped with electrically active impurities, a dopant containing compound via silk screen process, of diffusing the dopant agent by heating at high temperature to produce on the silicon disk a superficial layer of the other conductivity type of forming contacts on the front part and rear part of the active units and interconnecting the active elements. The process is described hereinafter with reference to the accompanying figures, in which equivalent elements correspond to identical reference numerals. In stage a), shown in Figure 1, mono or polycrystalline silicon wafers are used, obtained by cutting p or n doped hyperpure silicon ingots. The wafer thickness is between 100 and 500 µm, 100 µm being preferred. Their area can be varied as desired. After cleaning using ultrasound or one of the various known detergent solutions used in such cases, the wafers 1 are deposited on a support substrate 2 consisting of sintered amorphous quartz or another workable material resistant to the high temperature of process stage c). The substrate comprises seats for receiving the silicon wafers and provided with through holes 3, the seat thickness being less than the wafer thickness. The substrate is deposited (to adhere via a gasket) on an evacuable metal support 4 through which vacuum can be applied to the seats. In this manner the wafers are kept adhering to the support by a pneumatic vacuum system. Stage b). The metal support plus the substrate containing the silicon wafers are placed, while maintaining the whole assembly under vacuum, in a commercial apparatus able to deposit on the silicon wafers a silk screen paste containing a doping agent of opposite type to that of the silicon wafer. Stage c). The doping agent is diffused in a tunnel kiln with a high temperature thermal cycle enabling the doping agent to diffuse into the silicon with a suitable concentration profile. The temperature exceeds 900°C, 950°C being preferred. Stage d) The substrate with the silicon wafers, located on the metal support and maintained under vacuum, is placed on a traverser table with micrometric x-y movements. Using preferably a power laser, or alternatively a diamond-set grinding wheel or other suitable implement, the diffused layer (short-circuiting the device) is removed from the edge of the silicon wafer. It is also possible, particularly in the case of large-area wafers, to use this method for dividing the overall surface of the silicon wafer into different independent active elements. These elements, prepared from a single silicon wafer, are then electrically connected together in the subsequent stages of the process to form a photovoltaic module. At the end of this stage, as the procedure for diffusing the doping agent in the kiln will have formed an insulating silicon oxide layer on the surface of the wafers, it is opportune to remove it with hydrofluoric acid. For this purpose, as can be seen from Figure 2, the substrate with the wafers is inserted into a masking cover 5 consisting of a "pocket" of acid resistant material such as teflon, with apertures corresponding with the part to undergo chemical attack. During chemical attack, it may be advantageous to enhance the action with ultrasound. The wafers are then washed with deionized water and dried. This removal procedure can be avoided if during the next stage a firing cycle is used such that the metal can penetrate the oxide layer so that the metal is able to alloy with the silicon. Stage e). The substrate with the wafers is again placed on the evacuable metal support and the front contacts are deposited on the various active elements by a silk screen process, preferably using silver-based conducting paste. To form the rear contacts an inverting system is required as shown schematically in Figure 3. The substrate placed on the metal support and kept under vacuum is positioned inverted (transferring system) 6 on a perfectly identical system (receiving system) 7. On removing the vacuum from the transferring system the active elements fall by gravity into the seats of the receiving system, to which vacuum is now applied. The inverted active elements expose their rear surface for silk screen deposition of the contacts. After drying the contacts they are fired at high temperature, of between 700 and 900°C, preferably 800°C, so that they alloy with the silicon to form ohmic contact. Stage f). Conducting tracks are deposited on a glass sheet of about 3 mm thickness and of dimensions equal to or greater than those of the silicon wafer (if this is divided into several sensitive elements) or of a number of wafers (if each of these represents one sensitive element), in positions exactly corresponding to the rear contacts already deposited in the preceding stage on the rear of the silicon wafer, in order to connect the sensitive elements together. The glass sheet is superposed on the silicon such that the two series of contacts are juxtaposed. At this point the vacuum is released and the "sandwich" is heated to about 200°C. Stage g). Interconnections are formed such that the front of one sensitive element is connected to the rear of the next to provide the required current and voltage at the module output. Figure 4 represents an interconnection scheme. A layer of insulating polymer is firstly deposited on one edge of the cell, then by means of a conductive deposit 8 the front contact 9 of a cell is connected to the next cell rear contact 10 which is extended along the glass to pass beyond the cell at the point protected by the insulating layer. This prevents short-circuiting of the cell. Figure 4 also shows the p/n junction 11 and the rear glass 12. Stage h). An anti-reflecting layer is formed on the front of the module. For this purpose a layer of a few ten µm (hundred angstroms) of titanium oxide can be deposited, for example. Stage i). The module is now encapsulated using one of the many known methods. For example a high transmittance toughened glass plate can be used as front protection and ethylene vinyl acetate as the sealing resin. In another embodiment of the invention a single contact firing step can be used for both the rear contacts on the silica and the contacts on the rear protection glass. In this respect, although the silicon firing temperature is very high and basically incompatible with the glass, optimum conditions for this procedure can be achieved by making the firing times very short (of the order of a few seconds) and by effecting the heating by irradiating the silicon surface. Moreover the glass does not absorb radiation in that region of the spectrum. In this case the process is modified in the following manner. In stage e) after depositing the rear contact there is no high temperature firing but instead there is heating to a temperature of between 200 and 300°C. Then in stage f) high temperature firing is effected at around 700-900°C for a time of between 5 and 20 seconds. In a further embodiment of the present invention, in stage f) the contacts are not formed on the glass but instead are formed on the support substrate, which hence becomes a constituent element of the photovoltaic module. Summarizing, the process for producing modules in accordance with this invention does not start from small-area wafers but instead from supported large-area silicon sheets. The module is considered to be a series of silicon sheets having different thickness, stratified and interconnected by silk screen processes. The modules produced by this process have a solar conversion efficiency of not less than that obtained from modules produced by traditional processes. In addition, because of the reduction in the silicon sheet thickness and the effect of the increased production rate achieved by handling large areas up to 0.5 m 2 , resulting in a reduction in production time by a factor of about 10, it is estimated that the industrial production costs per shift are halved for volumes exceeding 10 Mw per year. The following examples are given for a better understanding of the invention and must not be conceived as limitative thereof. EXAMPLE 1 Eight wafers of ultrapure p-doped silicon, of 200 µm thickness and dimensions 20 x 20 cm, are placed on a support substrate consisting of a sintered quartz plate comprising eight seats for containing the wafers. The seats have a depth of 150 µm and comprise one or more through holes in their base. The plate is placed on an evacuable rectangular metal tray provided with a rubber seal gasket. When vacuum is applied to the assembly the wafers are maintained secured to the quartz plate. A doping paste containing phosphorus is now deposited by silk screen process on the wafers. The quartz plate is extracted from the evacuable tray and inserted in a tunnel kiln where diffusion takes place over a time of 20 minutes, a maximum temperature of 950°C being reached. At the end of the diffusion procedure, on the wafer surface there is a layer n-doped with phosphorus to a depth of 0.2-0.4 µm. The plate is now relocated on the evacuable tray and maintained under vacuum. Using an x-y table and a power laser the wafers are cut so that four active elements are obtained from each wafer. The diffused layer is also removed from the edges. In this manner a total of 32 active units each of about 100 cm 2 are obtained. The silicon oxide which forms on the surface as a result of the diffusion is removed by HF using the device described in the general part. The plate is repositioned on the evacuable tray and the front contacts are deposited on the silicon by a silk screen process. The contacts, formed from Ag, have a thickness of 10 µm and a width of 120 µm. The contacts formed from Ag and Al on the rear are deposited in a like manner after inverting the plate as described in the general part. Both the front and rear contacts are dried at 200°C and both are then alloyed with the silicon by firing at 750°C. Conducting tracks are now silk-screen deposited on a toughened glass sheet of 3 mm thickness and of dimensions equal to those of the quartz plate, to exactly correspond with the rear contacts already deposited on the rear of the wafers. After firing at a temperature compatible with the glass (400°C in our case) the glass plate is superposed so that the contacts on the glass become juxtaposed with those already silk-screen deposited on the silicon. After making the interconnections between the front of one active element and the rear of the next, an 80 nm (800 Å) layer of titanium oxide is vapour-phase deposited on the front part. The module is now encapsulated in the usual manner. EXAMPLE 2 The procedure of Example 1 is followed on 20 x 10 cm silicon sheets as far as the deposition of the rear contacts. At this point instead of firing at high temperature the contacts are dried at 200°C in an oven for a few minutes. The contacts are now formed on the rear glass as described in Example 1 but with the difference that instead of firing at 400°C, firing is effected at 750°C for 15 seconds. The final part of the module forming process is as described in Example 1.

Claims: A process for preparing photovoltaic modules based on mono and polycrystalline silicon solar cells, wherein the silicon is in the form of a supported large-area thin layer, said process comprising the following stages: a) depositing at least one silicon wafers (1) having a surface area up to 0.5 m 2 and thickness between 100 and 500 µm doped with electrically active impurities, on a support substrate (2) consisting of a heat-resistant material and comprising at least one recessed seat provided at its centre with at least one hole which pass through the substrate; adhering said support substrate (2) to an evacuable support (4) via a gasket and adhering said at least one silicon wafer (1) to said support substrate (2) by applying vacuum to said at least one recess through said evacuable support (4); b) depositing a dopant containing paste on the silicon wafers (1) via a silk screen process; c) diffusing the doping agent by heating said support substrate (2) and said silicon wafer (1) to a temperature of between 900 and 1000°C to create a diffused layer; d) defining the surface area of a plurality of the unit photo active elements by cutting the diffused layer; e) forming contacts on the front part and rear part of each unit photo active element by silk screen process; f) forming contacts on a rear protection (12) and applying the rear protection (12) to the rear of said elements, on said rear protection (12) being deposited conducting tracks in position exactly corresponding to the rear contacts already deposited in the preceding stage on the rear of the silicon wafer (1) to connect the sensitive elements together; g) electrically interconnecting together the photo active elements to form a photovoltaic module; h) depositing the anti-reflexing layer on the front of the photo voltaic module; and i) encapsulating the photovoltaic module. Process as claimed in claim 1, characterised in that in stage a) the silicon wafers (1) have a thickness of between 100 and 250 µm. Process as claimed in claim 1, characterised in that in stage a) the silicon wafers (1) have a thickness of 100 µm. Process as claimed in claim 1, characterised in that in stage a) the support substrate (2) is quartz. Process as claimed in claim 1, characterised in that in stage f) the rear protection (12) is a sheet of glass of about 3 mm thickness and of dimension equal to or greater than those of the silicon wafer (1) or of a number of wafers. Process as claimed in claim 1, characterised in that in stage f) the rear protection (12) is the support substrate itself. Process as claimed in claim 5, characterised in that in stage e), after rear contact deposition, heating of said active elements is effected to a temperature of between 200 and 300°C, then in stage f) firing is effected at a temperature between 700 and 800°C for a time of less than 20 seconds.

Inventors: MARGADONNA DANIELE, PASQUA VALTER, ZARCONE MARIANO, MARGADONNA, DANIELE, PASQUA, VALTER, ZARCONE, MARIANO
Applicants: EUROSOLARE SPA, EUROSOLARE S.P.A.
Application year: 1994
Main classification: H01L31
IPC codes: H01L31