PROCESS FOR PRODUCING 1,1,1,3,3-PENTAFLUOROPROPANE

Abstract: A process for producing 1,1,1,3,3-pentafluoropropane in a high yield, which comprises conducting vapor-phase reduction of 2,2-dichloro-1,1,1,3,3-pentafluoropropane with hydrogen in the presence of a catalyst comprising at least one metal selected from the group consisting of palladium, platinum and rhodium.

Description: This invention relates to a method of producing a useful compound of 1,1,1,3,3-pentafluoropropane that can be substituted for the CFC and HCFC having been used as refrigerants, blowing agents, and cleaning agents. Prior Art As the production method of 1,1,1,3,3-pentafluoropropane, it is known that 2,2,3-trichloro-1,1,1,3,3-pentafluoropropane as a raw material is reduced with hydrogen by using a palladium catalyst (U.S. Patent 2942036). The method, however, is unsuitable as an industrial method for producing 1,1,1,3,3-pentafluoropropane because the yield of the product is low and a large amount of a by-product, 1,1,1,3,3-pentafluoropropene is formed. Objectives of the invention This invention is designed to produce 1,1,1,3,3-pentafluoropropane with high yield. The constitution of the invention As a result of closely studying the processes for producing 1,1,1,3,3-pentafluoropropane, the inventors found a process by which the targeted material can be obtained with a high yield when 2,2-dichloro-1,1,1,3,3-pentafluoropropane as a raw material is reduced with hydrogen in a vapor phase in the presence of a catalyst composed of at least one chosen from the group of palladium, platinum, and rhodium. The invention has thus been produced. The point of this invention is thus a method of producing 1,1,1,3,3-pentafluoropropane with high yield, in which 2,2-dichloro-1,1,1,3,3-pentafluoropropane as a raw material is reduced with hydrogen, usually at a temperature from 30° to 450°C , in a vapor phase in the presence of a catalyst composed of at least one chosen from the group of palladium, platinum, and rhodium. As a vapor-phase reaction, a fixed-bed reactor or a fluidized-bed reactor can be used. A catalyst composed of at least one chosen from the group of palladium, platinum, and rhodium is preferable to be carried on a carrier composed of at least one carrier chosen from the group of active carbon, alumina, silica gel, titanium oxide, and zirconia. Although having little influence on the reaction, the particle size of carriers is preferably from 0.1 to 100 mm. As for catalyst concentration on the carriers, although a wide range from 0.05% to 10% can be used, a concentration of from 0.5% to 5% is usually recommended. The reaction temperature is usually from 30° to 450°C , preferably from 70° to 400°C . In the reduction reaction of 2,2-dichloro-1,1,1,3,3-pentafluoropropane with hydrogen, the ratio of hydrogen to the raw material can be changed widely. But hydrogenation is usually performed by using at least a stoichiometrical amount of hydrogen. To the total mole of starting material, for example, five or more moles of hydrogen can be used, which considerably exceed its stoichiometrical amount. Reaction pressure is not particularly restricted. The reaction can be conducted under pressure, at a reduced pressure, or at normal pressure. It is preferable to conduct the reaction under pressure or at normal pressure because a more complicated apparatus is needed for reaction at reduced pressure. The contact time is usually from 0.1 to 300 seconds, preferably from one to 30 seconds. The raw material 2,2-dichloro-1,1,1,3,3-pentafluoropropane to be used in the reaction of this invention can be synthesized by a reaction of fluorodichloromethane (CHFCl 2 ) and tetrafluoroethylene (CF 2 CF 2 ) at a temperature of between 0 ° and 150°C in the presence of a catalyst of aluminum chloride (AlCl 3 ) activated with trichlorofluoromethane (CCl 3 F) (see U.S. Patent 5157171). In this reaction, 3,3-dichloro-1,1,1,2,2-pentafluoropropane and 1,3-dichloro-1,1,2,2,3-pentafluoropropane are simultaneously produced as by-products. In addition, the raw material to be used in the reaction of this invention can also be obtained by a rearrangement reaction of 3,3-dichloro-1,1,1,2,2-pentafluoropropane and/or of 1,3-dichloro-1,1,2,2,3-pentafluoropropane as raw materials produced as by-products in the process by using an AlCl 3 catalyst that is activated with CCl 3 F similarly as mentioned above, at a temperature of between 50° and 100°C . The amount of AlCl 3 used as a catalyst in the reactions, including the rearrangement reaction, is from 0.1 to two equivalent, preferably from 0.3 to one equivalent. Inasmuch as the reaction pressure is not particularly restricted, the reaction can be conducted under pressure, at a reduced pressure, or at normal pressure. It is preferable, however, to conduct the reaction under pressure or at normal pressure because a more complicated apparatus will be needed for reaction at reduced pressure. The possibility of utilizing the invention in industry According to this invention, the targeted material can be obtained with high yield when 2,2-dichloro-1,1,1,3,3-pentafluoropropane as a raw material is reduced with hydrogen in a vapor phase in the presence of a catalyst composed of at least one chosen from the group of palladium, platinum, and rhodium. Examples This invention will be explained more concretely in the following examples. Example 1 Nineteen cc of platinum catalyst carried on active carbon (particle size 3 mm) at 0.5% concentration were infused into a reactor made of SUS-316 (2 cm inside diameter and 40 cm in length). The reactor was heated to 180°C using an electric furnace during exposure to nitrogen gas. After the desired temperature was attained, gaseous 2,2-dichloro-1,1,1,3,3-pentafluoropropane that had been gasified in advance was introduced into the reactor at 16.4 cc/min., together with hydrogen at 65.6 cc/min. The reaction temperature was kept at 180°C . The reaction pressure was 1.013 × 10 5 Pa, while the contact time was 8.4 sec. The produced gas was washed with water and dried with calcium chloride. It was then analyzed by gas chromatography. The result is shown in Table 1. Example 2 In the same reactor as used in Example 1, 18 cc of palladium catalyst carried on active carbon (particle size 3 mm) at 0.5% concentration were packed. The reactor was heated to 180°C in an electric furnace during exposure to nitrogen gas. After the desired temperature was attained, gaseous 2,2-dichloro-1,1,1,3,3-pentafluoropropane that had been gasified in advance was introduced into the reactor at 24 cc/min., together with hydrogen at 96 cc/min. The reaction temperature was kept at 180°C . The reaction pressure was 1.013 × 10 5 Pa and the contact time was 5.4 sec. The produced gas was analyzed by gas chromatography after washing with water and drying with calcium chloride. The result is shown in Table 1. Example 3 Infused into the same reactor as used in Example 1 were 18 cc of rhodium catalyst carried on active carbon (particle size 1 mm) at 0.5% concentration. The reactor was heated to 200 °C in an electric furnace during exposure to nitrogen gas. After the desired temperature was reached, gaseous 2,2-dichloro-1,1,1,3,3-pentafluoropropane that had been gasified in advance was introduced into the reactor at 24 cc/min., together with hydrogen at 96 cc/min. The reaction temperature was kept at 200°C . The reaction pressure was 1.013 × 10 5 Pa and the contact time was 5.2 sec. The produced gas was analyzed by gas chromatography after washing with water and drying with calcium chloride. The result is shown in Table 1. Example 4 Ten cc of palladium catalyst carried on alumina (particle size 3 mm) at 0.5% concentration were packed into a reactor made of SUS 316 (2 cm inside diameter and 40 cm length). The reactor was heated to 190°C in an electric furnace during exposure to nitrogen gas. After the target temperature was reached, gaseous 2,2-dichloro-1,1,1,3,3-pentafluoropropane that had been gasified in advance was introduced into the reactor at 16.4 cc/min., together with hydrogen at 65.6 cc/min. The reaction temperature was kept at 190°C . The reaction pressure was 3.04 × 10 5 Pa and the contact time was 12 sec. The produced gas was analyzed by gas chromatography after washing with water and drying with calcium chloride. The result is shown in Table 1. Example Conversion (%) Selectivity (%) 1 99.7 98.5 2 99.8 99.0 3 99.5 97.8 4 99.7 98.2

Claims: A method of producing 1,1,1,3,3-pentafluoropropane characterised by reducing 2,2-dichloro-1,1,1,3,3-pentafluoropropane by making it react with hydrogen in a vapor phase in the presence of a catalyst composed of at least one chosen from the group of palladium, platinum, and rhodium. A production method as defined in Claim 1, in which the catalyst is carried on a carrier composed of at least one chosen from the group of active carbon, alumina, silica gel, titanium oxide, and zirconia. A production method as defined in Claim 2, in which the catalyst's concentration on each carrier is from 0.05% to 10%. A production method as defined in any of Claims 1 through 3, in which carrier particle size ranges from 0.1 to 100 mm. A production method as defined in any of Claims 1 through 4, in which hydrogenation is conducted by using at least a stoichiometrical amount of hydrogen to 2,2-dichloro-1,1,1,3,3-pentafluoropropane. A production method as defined in any of Claims 1 through 5, in which the reaction is conducted at a temperature of between 30° and 450°C . A production method as defined in any of Claims 1 through 6, in which the reaction is a vapor-phase reaction in a fixed-bed reactor or in a fluidized-bed reactor. A production method as defined in any of Claims 1 through 7, in which the reaction is performed under pressure or at normal pressure. A production method as defined in any of Claims 1 through 8, in which the reaction has a contact time with a catalyst of between 0.1 and 300 sec. A production method as defined in any of Claims 1 through 9, in which 2,2-dichloro-1,1,1,3,3-pentafluoropropane is synthesized from fluorodichloromethane and tetrafluoroethylene in the presence of a catalyst. A production method as defined in Claim 10, in which 2,2-dichloro-1,1,1,3,3-pentafluoropropane is synthesized from fluorodichloromethane and tetrafluoroethylene at a temperature of between 0° and 150°C in the presence of an aluminum chloride catalyst activated with trichlorofluoromethane. A production method as defined in any of Claims 1 through 9, in which 2,2-dichloro-1,1,1,3,3-pentafluoropropane is synthesized by a rearrangement reaction of 3,3-dichloro-1,1,1,2,2-pentafluoropropane and/or 1,3-dichloro-1,1,2,2,3-pentafluoropropane, which are produced as by-products in the processes as defined in Claims 10 or 11, in the presence of a catalyst. A production method as defined in Claim 12, in which the rearrangement reaction is performed at a temperature of between 50° and 100°C by using a catalyst of aluminum chloride activated with trichlorofluoromethane. A production method as defined in any of Claims 10 through 13, in which a catalyst is used in an amount of from 0.1 to 2 equivalent. A production method as defined in any of Claims 10 through 14, in which the synthetic reaction is performed under pressure or at normal pressure.

Inventors: AOYAMA HIROKAZU, SEKI EIJI, AOYAMA, HIROKAZU, SEKI, EIJI, AOYAMA, HIROKAZU YODOGAWA WORKS OF, SEKI, EIJI YODOGAWA WORKS OF DAIKIN INDUSTRIES LTD
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LTD.
Application year: 1994
Main classification: C07C19
IPC codes: C07C17