IMPROVED PROCESS FOR RESIN TRANSFER MOLDING

Abstract: An improved process to make composites contains the steps of: (1) partially curing a tackifier resin in contact with a substrate to form a shapeable preform; (2) adding a matrix resin and co-curing the tackifier and matrix resin to form a composite. The resulting composites are useful in structural applications.

Description: IMPROVED PROCESS FOR RESIN TRANSFER MOLDING The present invention relates to resin transfer molding processes and preforms useful in those processes Resin transfer molding processes are used to make fiber reinforced composite materials Layers of reinforcing material are loaded into a mold, and a thermosetting resin is injected into the mold and cured by ordinary and accepted procedures to provide a finished composite piece It is difficult and time consuming to load different layers of fiber into the mold It was previously necessary to stitch the fibers together in order to provide net-shaped preforms More recently, a thermoplastic-like resin is sometimes used as a "tackifier" to stiffen the reinforcing material and hold it in place before the molding process begins See Heck et al , U S Patent 4,992,228 (February 12, 1991) and Flonc et al , U S Patent 5,080,851 (January 14, 1992) ("Thermoplastic-like" means that the resin is a solid, thermosetting resin that exhibits thermoplastic properties, such as a glass-transition temperature and/or a melting point, below the temperature that cures the resin, so that the resin is thermoformable ) In such a process, the individual fiber plies are sprinkled with a solid powder of the tackifier The powder is heated to fuse it onto the surface of the substrate and then cooled to solidify The different plies can be stacked together, heated to fuse the plies together, and then cooled leaving a preform The preform can be placed into the mold and used in an ordinary resin transfer molding process thereafter The known processes have an unrecognized drawback The tackifier is not completely soluble in the matrix resin used in the resin transfer molding process The tackifier requires more time to dissolve in the matrix resin than the time required to complete the curing process As curable resin is pumped into the mold, it transports the undissolved tackifier to one end of the molded product The resulting composite product contains a matrix resin whose chemical composition is different at one section, from the chemical composition at the other section The section containing high concentrations of tackifier frequently has poorer physical properties (such as glass-transition temperature) or mechanical properties (such as compression or short beam shear strength) than the section that contains lower proportions of tackifier What is needed is an improved process which does not effect the initial dispersion of tackifier throughout the composite product More preferably, the process gives an even dispersion of tackifier throughout the composite product One aspect of the present invention is a process to make a matrix composite by the steps of (1) contacting a reinforcing substrate with a tackifier whereby a preform is made, (2) contacting one or more preforms with a matrix resin, which is a second curable resin or resin composition that is capable of reacting with the tackifier, under conditions such that the tackifier and matrix resin are cured, whereby a composite is formed, characterized in that the tackifier is a first curable resin or resin composition which is partially cured while in contact with the substrate so that it adheres to the substrate but remains thermoplastic-like and capable of further reaction A second aspect of the present invention is a preform that contains (1) a reinforcing substrate suitable for use in a matrix composite, and (2) a tackifier adhered to the substrate characterized in that the tackifier is a thermoplastic-like, partially-cured, curable resin or resin composition that is either (1) a single resin that is capable of curing with itself, or (2) a partially-cured mixture containing a resin and hardener for the resin A third aspect of the present invention is an improved method to make composites having the steps of (1) contacting a fiber-containing reinforcing substrate with a tackifier, which is a first curable resin or resin composition, at a temperature selected such that the tackifier binds fibers within the substrate together but remains capable of further reaction, whereby a preform is made, and (2) impregnati ng one or more preforms with a matrix resin, which is a second curable resin or resin composition that is capable of reacting with the tackifier, and (3) curing the tackifier and matrix resin, whereby a composite is formed, characterized in that (a) the tackifier contains a labeling moiety that can be quantitatively analyzed after the composite is formed without destroying the composite, and (b) the quantity of labeling moiety is analyzed by non-destructive methods in at least two different points of the composite during or after Step (2) The process and the preform of the present invention can be used to make reinforced matrix composites The third aspect of the present invention has the additional advantage that finished composites can be tested for migration of the tackifier without destroying the composite The composites are useful as structural materials The present invention uses a reinforcing substrate Suitable reinforcements are well-known and familiar to persons of ordinary skill in the art See, E G Kirk-Othmer, Encyclopedia of Chemical Technology-Supplement, Composites, High Performance, at 260-281 (J Wiley & Sons, 1984) The substrate usually contains fibers, such as quartz, aramid, boron, glass, carbon, or gel-spun polyethylene fibers The fibers can be unidirectional or multidirectional They may be in the form of woven or non-woven mats or in the form of random short fibers Preferably, the substrate is in the form of a woven or non-woven fibrous material The substrate is contacted with tackifier under conditions such that the tackifier partially cures and adheres to the fibers The tackifier preferably contains either (1 ) a single resin that is capable of at least partially curing with itself, or (2) a mixture containing resin and hardener that is capable of at least partially curing Examples of suitable resins which can cure with themselves include polyimide and particularly bismaleimide resins, polycyanate ester resins, vinyl ester resins (with suitable initiators and promoters) and benzocyclobutene resins The most preferred example is 1 , 1 '- MDA bismaleimide resin Examples of suitable polyimide and bismaleimide resins are described in Stenzenberger, "Recent Advances in Thermosetting Polyimides", 20 British Polymer Journal 383-396 (1988) Examples of suitable resins that can cure with themselves include 5250-4RTM BMI resin, and are commercially available Examples of suitable resin and hardener mixtures include (a) a mix of epoxy resin (such as TACTIX ® 123 epoxy resin or PR 500™ from 3M) and a known curing agent (such as MILLAMINE™ 5260 curing agent), (b) a mix of polyisocyanate and polyol suitable to make polyurethanes (such as SPECTRIM ® MM310), and (c) epoxy-cyanate ester resin systems (such as E-905L resin from BP Chemicals) The mixture of resin and hardener preferably contains an epoxy resin and suitable curing agent and optionally a catalyst The epoxy resin is preferably the glycidyl ether of a polyhydπc phenol, such as bi phenol, bisphenol A, tetrabromobisphenol A, a novolac resin or bιs-(hydroxyphenyl)fluorene resin It may be either a liquid or a solid epoxy resin It preferably has an epoxy equivalent weight (EEW) of between 150 and 700 The curing agent is preferably an amine, amide, sulfimide, sulfamide, polymercaptan, polyphenol, substituted imidazole, polyacid, polyanhydπde, urea, thiourea or sulfonamide It is more preferably an amine or amide compound, such as dicyanamide In order to assist in partial curing it may be desirable to use multistage curing agent, such as sulfanilamide or cyanoguanidine The multistage curing agent may be a single compound or a mixture of compounds that contain two or more reactive moieties that react with the epoxy resin to cure at different temperatures The equivalent ratio of curing agent to resin is preferably between 0 5 1 and 1 5 1 , and more preferably between 0 8 1 and 1 2 1 , unless a non-stoichiometπc reaction or resin and tackifier is desired Examples of suitable catalysts include primary aliphatic polyamines, tertiary amines, and substituted imidazoles Suitable catalysts, resins and hardeners are commercially available The concentration of catalyst is preferably between 0 and 2 parts catalyst per 100 parts resin, by weight (phr), more preferably between 0 05 and 0 5 phr, and most preferably between 0 08 and 0 2 phr The tackifier should be applied to the substrate in a quantity great enough to hold the fibers in the desired shape and position but small enough to leave the resulting preform porous, so that later the matrix resin can infuse throughout the substrate The quantity of tackifier is preferably at least about 0 25 weight percent of the substrate, more preferably at least about 1 weight percent, and most preferably at least about 3 weight percent The quantity of tackifier is preferably no more than about 1 5 weight percent of the substrate, more preferably no more than about 8 weight percent, and most preferably no more 5 that about 5 weight percent The tackifier may be applied by known methods, such as sprayi ng or di ppi ng for liquids or sprinkling or electrostatic appl ication for powders It is preferably applied substantially evenly across the substrate Individual plies of preform may optionally be shaped or lami nated together (a 10 thermoforming step) after the tackifier is applied (Step 1 ) and before the composite is made (Step 2) For instance, multiple pl ies may be pressed together at a temperature above the glass- transition temperature of the tackifier Likewise, individual preforms or lami nates may be molded or shaped at a temperature that is above the glass-transition temperature of the tackifier and that does not ful ly cure the tackifier The temperature is preferably at least about 1 5 40°C and at most about 100°C when the tackifier is an epoxy resin The temperature is preferably at least about 50°C and at most about 1 10°C when the resi n is a bismaleimide resi n Examples of shapi ng and laminating different preforms are described in Heck et al , U S Patent 4,992,228 (February 12, 1991 ) and Flonc et al , U S Patent 5,080,851 (January 14, 1992) At some time after the tackifier is applied and before it is molded with the matri x 20 resin, the tackifier is partially cured in contact with the substrate It should be cured enough so that it adheres to the fi ber and so that it solidifies enough to hold the fi bers i n the desi red shape and position On the other hand, the curing should not be complete The partial ly cured tackifier should still be thermoformable and should sti ll be capable of reacting with the matrix resi n The tackifier may be partially cured as a separate step, but it is preferably partial ly cured 25 during application to the substrate (Step 1 ) or during the thermoforming step or both Curing can be halted at the desired level of curi ng by at least three different methods Fi rst, a resi n composition that contains both resi n and a curing agent may contai n less than a stoichiometπc quantity of curing agent, so that only an incomplete cure is possible The precise quantities of resi n and curing agent vary depending upon the resin and curi ng 30 agent selected, but can readily be determi ned by persons of ordi nary ski ll i n the art For instance, when the resi n is a difunctioπal epoxy resi n and the curing agent is a diami ne, then the ratio of epoxy equivalents to ami ne equivalents is preferably between 0 5 1 and 0 85 1 or between 1 25 1 and 2 1 Second, when resi n composition contai ns both resin and a curing agent, the 35 curi ng agent may be a multistage curing agent The resi n and curi ng agent are cured at a temperature that wil l only cause curi ng on some of the curi ng agent's active sites In the second step, the composition may be cured at a higher temperature to cause curing at al l of the active sites and completely cure the composition Third, even when the tackifier is self-curing or contains stoichiometπc rat-.os of resin and hardener, the time and temperature of the partial cure may be selected to provide the desired level of curing Again, the optimal time and temperature will vary depending upon the tackifier and the presence or absence of any catalyst within the tackifier Persons of ordinary skill in the art can readily determine the optimum time and temperature without undue experimentation For instance, when the tackifier contains bismaleimide resin, it is preferably reacted for between 5 and 120 minutes at a temperature between 120°C and 1 50 C C Preferably, the glass-transition temperature of the partially cured tackifier is low enough that the preform can be laminated and/or shaped without over-curing the tackifier A partially cured, thermoplastic-like epoxy tackifier preferably has a glass-transition temperature of no more than about 130°C, and more preferably no more than about 80°C A partially cured, thermoplastic-like bismaleimide tackifier preferably has a glass transition temperature of no more than about 180°C, and more preferably no more than about 120°C On the other hand, the glass-transition temperature is preferably high enough so that the preform can be handled and stored at room temperature The glass-transition temperature is preferably at least about 40°C, and more preferably at least about 60°C (Glass-transition temperature can be conveniently measured by differential scanning caloπmetry ) Some partially cured tackifiers may continue to cure slowly at room temperature Therefore, the preform is preferably used in the next step of the reaction before the tackifier cures significantly more The tackifier is preferably shelf-stable for at least about two weeks, more preferably for at least about a month, and most preferably for at least about three months (A tackifier is considered shelf-stable when it can still be used as a tackifier to give adequate adhesion and to react with the matrix after a period of time ) The preform is contacted with a matrix resin that contains a second curable resin or resin composition The matrix resin should be capable of reacting with the partially cured tackifier in the preform The matrix resin is not required to be chemically related to the tackifier, as long as it can react with the tackifier For instance, an epoxy resin tackifier can be used with a cyanate ester matrix resin or vice-versa However, the matrix resin is preferably chemically related to the tackifier, such as epoxy tackifiers with epoxy matrix resins or bismaleimide tackifiers with bismaleimide matrix resins Most preferably, the matrix resin and the tackifier are essentially the same or differ primarily in the ratio of resin to curing agent The matrix resins have the same description and preferred embodiments previously given for tackifiers, except that at least a stoichiometπc quantity of curing agent should be used The quantity of matrix resin should be sufficient to hold the fibers together, to maintain fiber alignment and, preferably, to transfer loads around broken fibers It is usually preferable to minimize the quantity of matrix resin in the composite After curing, the matrix resin and tackifier usually make up at least about 25 volume percent of the composite and most often make up at least about 35 volume percent The matrix resin and tackifier are preferably no more than about 75 volume percent of the composite, more preferably no more than about 45 volume percent and most preferably no more than about 40 volume percent The matrix resin is preferably applied under sufficient pressure to force it throughout the preform, so that the preform is impregnated with resi n and voids withi n the cured composite are mi nimized The matrix resin is preferably applied at pressures from a vacuum (0 kPa) to 600 psig (3300 kPa) There is frequently a pressure drop across the mold, so that pressure at the inlet may be as high as about 400 psig (2700 kPa) while pressure at the outlet is 50 psig (450 kPa) or lower The cured composite preferably contai ns no more than about 5 volume percent voids, more preferably no more than about 2 volume percent, and most preferably no more than about 1 vol ume percent voids The matrix resin and tackifier are then subjected to temperature and other conditions suitable to ful ly cure them Again, the opti mum time and temperature vanes widely dependi ng upon the matrix resin and tackifier used, and will be familiar to persons ski lled i n the art When the matrix resi n and tackifier are common epoxy resi ns, then the fi nal curing step is preferably at least 30 to 120 mi nutes at a temperature of at least 90°C to 180°C However, for some epoxy resi ns the best curi ng temperature may be as high as 250°C or more When the matrix resin and tackifier are bismalei mide resi ns, then the final curi ng step is preferably at least 60 to 240 minutes at a temperature of at least 1 50°C to 21 0°C, followed by a post-curing step of 60 to 240 mi nutes at 175°C to 230°C The final curi ng step is preferably completed in a mold that can provide a composite of the desi red shape The resulting cured composite can be cooled, finished and used in the ordinary manner for matrix composites It is theorized, without i ntending to be bound, that the dispersion of the tackifier is not significantly disturbed when the matrix resin is i njected because the tackifier is bonded to the substrate during the partial curing reaction i n Step (1 ) Preferably, the tackifier is evenly dispersed in Step (1 ), so that it remains evenly dispersed throughout the moldi ng process The effectiveness of this procedure can readily be verified by labeling the tackifier with a chemical label that can quantitatively be detected usi ng nondestructive methods For instance, a small amount of brommated epoxy resin can be made a part of the tackifier The bromine in the epoxy resin is a label i ng moiety that can be measured quantitatively without destroying the resulting composite part by x-ray fluorescence The average concentration of tackifier preferably varies across the face of the substrate by no more than about 10 percent, more preferably by no more than about 5 percent and most preferably by no more than about 1 percent This procedure is equal ly effective to measure the dispersion of tackifiers i n composites that are made by other processes, such as the process described i n Heck et ai , U S Patent 4,992,228 (February 12, 1991 ) and Flonc et al , U S Patent 5,080,851 (January 14, 1992) The process has additional benefits as well Tackified prepregs are often made by heating the substrate and tackifier under pressure in a mold that compresses the tackified prepreg into the desired shape and thickness In prior art processes, the tackifier often-does not adhere to the substrate strongly enough to hold the prepreg in the desired thickness Rather, the tackified prepreg springs back and expands in thickness or "lofts" when the pressure of the mold is released This lofting is sometimes 50 percent or more Later, when the tackified prepreg is loaded into the mold for resin-transfer molding, it is too thick for the mold Closing the mold causes the prepreg to twist or wrinkle, resulting in a flawed composite On the other hand, tackifiers used in the present invention adhere more strongly to the substrate because they are partially cured in contact with the substrate The substrate is less likely to loft and more likely to deliver a useful part Preferably, the tackified prepreg lofts by 0 to 25 percent over its thickness in the mold, more preferably O to 10 percent and most preferably 0 to 5 percent The degree of lofting can be measured by comparing the thickness of the tackified prepreg to the internal thickness of the mold used to make it EXAMPLES The following examples are for illustrative purposes only and they should not be taken as limiting the scope of either the specification or the claims Unless otherwise stated all parts and percentages are by weight The following materials are used in the Examples. Epoxy Resin A - is a diglycidyl ether of bisphenol A having a viscosity of 4400 cps at 25°C and an epoxy equivalent weight (EEW) of 176 to 183, that is commercially available from The Dow Chemical Company as TACTIX ® 123 epoxy resin Epoxy Resin E - is a brominated diglycidyl ether of bisphenol A having an EEW of 305 to 355, that is commercially available from The Dow Chemical Company as DER ® 542 Epoxy Resin M - is a fluorene-containing epoxy resin that contains both epoxy and amine functionality, so that it cures without a separate curing agent It has a viscosity of 1 10 cps at 155°C and is commercially available from 3M Company as PR-500 resin Bis-A - is epoxy resin grade bisphenol A with an equivalent weight of 1 14 1 and is commercially available from The Dow Chemical Company TBBA - is tetrabromobisphenol A (2,2-bιs-(3,5-dιbromo-4-hydroxyphenyl)propane) with an equivalent weight of 271 9 that is available from Schenectady Chemical Company BMI Resin J is a bismaleimide resin blend having a viscosity of 50 cps at 130°C, that is commercially available from BASF NARMCO as 5250-4RTM Catalyst A is a 70 weight percent solution of ethyltπphenyl phosphonium acetate-acetic acid complex Catalyst B is the amide of sulf am II ic acid (sulfanilamide) with a melting point of 165 c C to 167°C and is commercially available from Aldπch Chemical Catalyst C is 2-ethyl-4-methylιmιdazole available from Aldπch Chemical Hardener A is a cyclohexyldiamine with an amine equivalent weight of 28 5, that is commercially available from Mil ken Chemical Company as MILLAMINE™ 5260 Example 1 - Process with Advanced Brominated Epoxy Resin Tackifier An advanced bromine-containing epoxy resin is made Epoxy Resin E (500 grams), Bis-A (132 grams), and TBBA (67 grams) are heated under nitrogen atmosphere from ambient temperature to 60°C without stirring At 60°C, the viscosity of the reaction mixture is low enough to allow heating from 60°C to 80°C with stirring Catalyst A (0 62 grams, 1 100 ppm) is added dropwise to the stirred reaction mixture Over 45 minutes, the reaction temperature is increased from 80°C to 150°C An exotherm occurs around 150°C, and heating is reduced so that the reaction temperature does not exceed 200°C Stirring is continued at about 190°C for an additional 45 minutes The hot reaction product is poured onto a cool, non-stick surface as a o layer approximately 1/4 inch thick (6 4 mm) After the advanced resin cools and sol idifies, it is broken into flake form The flaked advanced resin is ground into a fine powder using a Bantam Mill (Mikro-Pul Corporation) fitted with a 0 013 inch (0 33 mm) herringbone slit screen The grinding chamber is cooled to ambient temperature with liquid nitrogen to prevent melting of the resinous 5 compound during the grinding process The advanced resin contains 2 84 percent bromine by weight and has an epoxide equivalent weight of about 746, as measured by titration Its melting point (endotherm minimum) is 58 4°C by differential scanning caloπmetry (DSC) The advanced resin is used as a tackifier to make laminated preforms Eight 0 pieces (plies) of AW370-8H AS4-W carbon fiber reinforcing fabric (Hercules Aerospace) are cut from a bulk roll into squares measuring 8 inch (203 2 mm) on a side A mixture containing about 9 3 grams of the advanced epoxy resin, 0 6 grams of Catalyst B and 0 1 grams of Catalyst C is spri nkled on each ply in an even coat at a concentration of about 2 percent by weight The plies are placed in a hot-air circulation oven for 1 minute at 200°F (93°C) in order to melt the 5 mixture, and adhere it to each ply The plies are then removed from the oven and allowed to cool to ambient temperature The plies are stacked treated side up and heated for about 30 minutes at 250°F (121 °C) under vacuum of 737 mmHg in a vacuum bagging apparatus, then cooled to room temperature The resulting preform measures about 0 15 inches in thickness and is quite stiff 0 to the touch The individual plies are strongly adhered to one another due to the partial reaction of the binder mixture Experimental peel strength measurements show that the partially cured preform has three times the peel strength of uncured preforms The laminated preform is used to make a composite The laminated preform is placed in a metal cavity mold having dimensions 15 inches wide by 20 inches long by 1/8 inches 5 tall (381 mm by 508 mm by 3 2 mm) when closed Openings in the mold can be used to pump resin into the mold and allow matter to flow out of the mold The closed mold is heated to 140°F (60°C) A mixture of Epoxy Resin A (1 100 grams) and Curing Agent A ( 192 5 grams, 17 5 phr) at 120 C F (49°C) is introduced into the mold cavity under 10 psi ( 160 kPa) nitrogen atmosphere A 70 mL portion of resin is collected from exit valves in the mold The exit valves are closed and then the pressure on the resin is increased to 60 psi (520 kPa) The mold temperature is increased to 350°F (177°C) at 2°C per minute and held at 350°F for 30 minutes in order to cure the injected resin mixture The mold is cooled to 140°F (60°C) at 3°C per minute and then the cured composite is removed Example 2- Synthesis of Composite Using Advanced BMI Tackifier Compound An advanced BMI tackifier is made BMI Resin J (1000 grams, lot 27821 ) is weighed into a 2-lιter resin kettle The resin kettle is placed in a hot-air circulation oven at 1 10°C (230°F) for approximately one hour in order to lower the viscosity of the resin The kettle is heated using infrared lamps with stirring, according to the time and temperature set out in Table 1 Table 1 in at 0 78 - 10 99 - 20 125 - 30 140 - 40 140 < 10 50 140 30 60 140 50 70 140 78 100 140 242 120 141 546 140 139 1021 147 141 1621 151 140 2173 The preferred viscosity of the final cooled tackifier product is around 200G cps when tested at 150°C Eight pieces (plies) of AW370-8H AS4-W carbon fiber reinforcing fabric (Hercules Aerospace) are cut from a bulk roll into squares measuring 8 inches (203 2 mm) on a side An even coat of the BMI tackifier is sprinkled by hand onto the surface of each of the eight plies at a concentration of 5 percent by weight The plies are placed in a hot-air circulation oven for 1 minute at 200°F (93°C) in order to melt the BMI compound mixture, and adhere it to each ply The plies are then removed from the oven and allowed to cool to ambient temperature The plies are stacked treated side up and heated for 30 minutes at 280°F (140°C) in o a vacuum bag apparatus under 737 mmHg vacuum The oven is turned off and the vacuum bagging apparatus is allowed to cool to ambient temperature while remaining under reduced pressure The laminated preform measures about 0 15 inch in thickness and is stiff to the touch The individual plies are strongly adhered to one another to the partial reaction of the binder mixture 5 The laminated preform is placed in a metal cavity mold having dimensions 15 inches wide by 20 inches long by 1/8 inches tall (381 mm by 508 mm by 3 2 mm) when closed and having inlet and outlet valves The closed mold is heated to 280°F (138°C) BMI Resin J is injected into the mold at 280°F (138°C) and 10 psig (160 kPa) pressure Valve E is now opened to introduce the liquid resin into the mold cavity After a 70 mL portion of resin is collected from 0 the outlets, the outlet valves are closed and the resin pressure is increased to 350 psig (2500 kPa) The mold temperature is increased to 375°F (191 °C) at 2°C per minute and held at 375°F for 240 minutes in order to cure the injected resin mixture The mold is cooled to 140°F (60 C C) at 3°C per minute, and the cured composite article is removed Example 3 - Fabrication of Composite Using a Fluorene- 5 -Containing Epoxy Resin Tackifier Eight pieces (plies) of AW370-8H AS4-W carbon fiber reinforcing fabric (Hercules Aerospace) are cut from a bulk roll into sguares measuring 8 inches 0 5 (203 2 mm) on a side A tackifier is made by advancing Epoxy Resin M until its melting p ' oint is about 60°C The tackifier is sprinkled evenly over each ply at a concentration of about 5 weight percent The plies are placed in a hot-air circulation oven for 1 minute at 200°F (93°C) in order to melt the tackifier, and adhere it to each ply The plies are then removed from the oven and allowed to cool to ambient temperature The plies are stacked treated side up and heated for about 30 minutes at 280°F to 300°F (121°C to 150°C) in a vacuum bagging apparatus under a vacuum of about 737 mmHg, then cooled to room temperature The resulting laminated preform measures about 0 15 inch in thickness and is quite stiff to the touch The individual plies are strongly adhered to one another due to the partial reaction of the binder mixture Experimental peel strength measurements show that the partially cured preform has three times the peel strength of uncured preforms The laminated preform is used to make a composite The laminated preform is placed in a metal cavity mold having dimensions 15 inches wide by 20 inches long by 1/8 inches T (381 mm by 508 mm by 3 2 mm) when closed Openings in the mold can be used to pump resin into the mold and allow matter to flow out of the mold The closed mold is heated to 280°F to 300°F (121 °C to 150°C) Epoxy Resin M at 310°F to 300°F (145°C to 150°C) is introduced into the mold cavity under 10 psi nitrogen atmosphere A 70 mL portion of resin is collected from exit valves in the mold The exit valves are closed and then the pressure on the resin is increased to 350 psig (2500 kPa) The mold temperature is increased to 375°F (19TC) at 2°C per minute and held at 375°F for 120 minutes in order to cure the injected resin mixture The mold is cooled to 140°F (60°C) at 3°C per minute and then the cured composite is removed

Claims: CLAIMS 1 A process to make a matrix composite comprising the steps of (1 ) contacting a reinforcing substrate with a tackifier, which is a first curable resin or resin composition, at a temperature and for a time sufficient to partially cure the tackifier so that it adheres to the substrate but remains thermoplastic-like and capable of further reaction, whereby a preform is made, and (2) contacting one or more preforms with a matrix resin, which is a second curable resin or resin composition that is capable of reacting with the tackifier, under conditions such that the tackifier and matrix resin are cured, whereby a composite is formed, characterized i n that the tackifier is a first curable resin or resin composition, which is partially cured while in contact with the substrate so that it adheres to the substrate but remains thermoplastic-like and capable of further reaction 2 A preform that comprises (1 ) a reinforcing substrate suitable for use in a matrix composite, and (2) a tackifier that adheres to the substrate characterized in that the tackifier is a thermoplastic-like, partially-cured, curable resin or resin composition that is either (1 ) a single resin that is capable of curing with itself, or (2) a partially-cured mixture containing a resin and hardener for the resin 3 A process or preform as described in any of the preceding claims wherein the tackifier is a resin that cures without the need for a separate curing agent 4 A process or preform as described in any of Claims 1-2 wherein the tackifier contains a curable resin and a hardener for that resin 5 A process or preform as described in Claim 4 wherein the resin is an epoxy resin and the hardener is a suitable curing agent for epoxy resins 6 A process or preform as described in Claim 4 wherein the tackifier contains a stoichiometπc excess of curable resin or hardener 7 A process or preform as described in any of the preceding claims wherein the partially cured tackifier in the preform has a glass-transition temperature between 30°C and 180°C 8 A process or preform as described in any of the preceding claims wherein the ratio of tackifier to substrate in the preform is between 1 and 15 weight percent 9 A process as described in any of Claims 1 or 3-8 which further comprises the following step (1 a) pressing a plurality of preforms together at a temperature above the glass- transition temperature of the tackifier at a pressure and for a time sufficient to laminate the preforms together 10 A process as described in any of Claims 1 or 3-9 wherein the matrix resin has a backbone structure and reactive groups similar to the tackifier 1 1 A process as described in any of Claims 1 or 3-10 wherein the the tackifier is partially cured in contact with the substrate under pressure, and the degree of cure is selected so that the tackified prepreg lofts by 0 to 25 percent when the pressure is released 12 A process as described in any of Claims 1 or 3-1 1 , wherein. (a) the tackifier contains a labeling moiety that can be quantitatively analyzed after the composite is formed without destroying the composite; and (b) the quantity of labeling moiety is analyzed by non-destructive methods in at least two different points of the composite during or after Step (2)

Inventors: COOK PHIL H, DAVIS WILLIAM, WAI MARTIN, WHITE WARREN D, COOK, PHIL, H., DAVIS, WILLIAM, WAI, MARTIN, WHITE, WARREN, D.
Applicants: COOK PHIL H, DAVIS WILLIAM, DOW CHEMICAL CO, WAI MARTIN, WHITE WARREN D, COOK, PHIL, H., DAVIS, WILLIAM, THE DOW CHEMICAL COMPANY, WAI, MARTIN, WHITE, WARREN, D.
Application year: 1994
Main classification: B29B15
IPC codes: B29B15, B29C70, C08J5