Microfiltration and/or ultrafiltration membrane, method of the preparation of such a membrane, and a method of the filtration of a liquid by means of such a membrane

Abstract: The invention relates to a microfiltration and/or ultrafiltration membrane consisting of a polymer having nominal pores of 0.001 - 10 µm. The special feature of the membranes according to the invention is that the matrix of the membrane incorporates an active adsorbent which is preferably polyvinyl polypyrrolidon. Usually the polyvinyl polypyrrolidon is present in the membrane in an amount of 5 - 90 % by weight and preferably in an amount of 30 - 70 % by weight. Preferably the membrane is hydrophillic and is usually asymmetric or is constructed of different layers. The nominal pore size of the membrane is 0.05 - 5 µm and preferably 0.2 - 1.0 µm, while the membrane is tubular, flat or capillary. Furthermore, the invention relates to a method of the preparation of the membrane and to a method of the filtration of undissolved components from a liquid and/or the simultaneous adsorption of dissolved components from the liquid by means of the membrane according to the invention. The method according to the invention is especially suitable for the removal of components causing turbidity from a liquid, especially beer, by means of the membrane according to the invention.

Description: The invention relates to a microfiltration and/or ultrafiltration membrane, to a method of its preparation and to methods of removing dissolved and/or undissolved components from a liquid by means of such a membrane. Membranes are known from the prior art which can, for instance, be used for the filtration of all kinds of liquids containing solid components. These membranes can, for instance be used for the removal of yeast cells causing turbidity from unfiltered beer or for the treatment of unfiltered fruit juices. However, the disadvantage of such a filter is that when, for example, it is used for the filtration of beer, dissolved components, such as polyphenols, are allowed to pass through, which by reacting with proteins can after a time cause turbidity. Naturally this is not desirable as such turbidity takes away the very essential characteristic of beer, namely clearness. It is also known that the polyphenols causing such turbidity can be removed from the beer, which is first filtered in order to remove the insoluble components such as yeast etc., by adding polyvinyl polypyrrolidon in powder form. The undesirable polyfenols are adsorbed by polyvinyl polypyrrolidon (PVPP) and the solid PVPP particles are then removed from the beer by filtration. Traditionally one used kieselguhr filters for the clarification of beer, however, a disadvantage is that they produce much waste. These kieselguhr or diatomaceous earth filters have lately been replaced by cross-flow microfiltration. Such a membrane is, for instance, described in applicant's US-A-No. 4,798,847. FR- A- 2 295 771 discloses a process for removing turbidity causing dissolved impurities (such as polyphenols) and undissolved impurities from liquids such as beer, wherein the liquid to be purified is passed through a wet laid sheet (ie a "dynamic" membrane") comprising specific polyamide adsorbent particles. PVPP particles are only used for comparative purposes. A similar technique is used according to EP- A- 0 351 363: A "dynamic" membrane of adsorbent particles (eg a mixture of PVPP particles and other fibres or particles) is formed on a filter membrane before and during the filtration. WO- A- 86/06589 discloses the use solvent- cast microporous films/membranes made from specific polyamides for removing polyphenols from liquids (eg beer). It is suggested to incorporate, by co- precipitation, "inert" powders such as diatomite earth "for improving the polyphenol uptake". US- A- 4 943 374 discloses the separation of germs and turbidity causing substances from beer by filtration through a PES- membrane comprising PVP as hydrophilisation agent. The incorporation of adsorbent particles is not addressed. It goes without saying that the known method of the removal of polyfenols by addition of powdered PVPP is time-consuming, making the process expensive. It is the object of the invention to provide a membrane whereby the disadvantages of the known membranes are effectively removed. To this end the present method provides a microfiltration and/or ultrafiltration membrane as defined in claim 1. Surprisingly it has been shown that the incorporation of an active adsorbent into the membrane matrix, being polyvinyl polypyrrolidon (PVPP), provides a membrane capable of selectively adsorbing dissolved components from the liquid. This makes polyvinyl polypyrrolidon a particularly suitable adsorbent for the removal of polyfenols from beer or other liquids. Good results have been obtained when the active adsorbent, ie the polyvinyl polypyrrolidon, is present in the membrane in an amount of 5 - 90 % by weight, and preferably in an amount of 30 - 70 % by weight. The membrane comprising PVPP particles as active adsorbent incorporated in the membrane matrix can be subjected to regeneration. The membrane structure must be resistant to the regeneration fluid, in other words, the membrane structure must stay intact under the influence of the regeneration solution applied. When using the membrane according to the invention for the filtration of aqueous solutions, a hydrophillic membrane matrix is preferred. The membrane according to the invention is preferably asymmetric, but may also be composed of different layers. By means of a spinning head having, for instance four concentric circular openings, a membrane can be obtained of a so-called sandwich structure. The layers in direct contact with the liquids may determine the pore size and prevent at the same time loss of adsorbent. The central layer may contain a large amount of adsorbent. Preferably as a rule the nominal pore size of the membrane is 0.05 - 5 µm and more preferably 0.2 - 1.0 µm. The membrane according to the invention may be tubular, flat or capillary. The invention relates further to a method of manufacturing the membrane according to the invention as described above, characterized in that a polymer solution/suspension is prepared, starting with the polymers polysulphone or polyether sulphone and polyvinyl pyrrolidon and a suitable solvent mixture in which the active adsorbent polyvinyl polypyrrolidon particles are suspended, after which the mixture is processed into a membrane. When manufacturing the membrane according to the invention one generally uses 5 - 20 parts by weight of polyether sulphone, 1 - 10 parts by weight of polyvinyl pyrrolidon, 5 - 30 parts by weight of polyvinyl polypyrrolidon and 0 - 15 parts by weight of glycerine in N-methyl pyrrolidon. Furthermore, the invention relates to methods of separating undissolved components from a liquid and/or simultaneously adsorbing dissolved components from the liquid by means of the membrane according to the invention, as defined in claims 12, 13 and 15. The liquids to be filtered are preferably subjected to so-called longitudinal flow filtration, whereby the liquid to be filtered is led along the membrane. When removing undissolved components according to the methods of claim 13 or 15, particularly good results are obtained due to the use of asymmetrical membranes according to the invention, whereby the liquid is led along an asymmetric membrane having a pore structure such that the pores at the membrane's feed side are larger than the nominal pore size and the pores of nominal pore size occur in the section toward the permeation side, the separated, undissolved components are then flushed back from the membrane and are subsequently carried away with the feed liquid. Liquids which are especially well suited for filtration by means of the present method are beer, wine, fruit juice, bacterial suspensions, blood, milk, enzyme suspensions, etc. The present method gives particularly good results when applied in the treatment of crude beer. The membrane of the invention is especially effective when the flushing back of the membrane takes place intermittently with a frequency of 1 sec. - 10 min. for 0.1 - 1 sec. at a back pressure of 0.5 - 5 bar. When subjecting a liquid to longitudinal flow filtration, a longitudinal flow velocity of less than 2 m/sec. is preferred. Normally a pressure difference over the membrane of less than 0.5 bar suffices. The membranes of the invention should be regenerated from time to time. This is done by means of a suitable regeneration solution such as, for instance a 0.5 - 2% NaOH solution at 50 - 90°C. The methods according to the invention are preeminently suited for the filtration and selective separation of components from the filtered liquid which later either cause problems with the preparation of beer, or which are of great economic importance in, for example the preparation of pharmacologically active substances which are adsorbed by adsorbents and are released again during regeneration of the membrane. The invention will now be elucidated by means of the following non-limitative examples. Example I Preparation of a membrane having more than 50% active adsorbent per dry material content. A polymer solution/suspension was prepared from 13.4% polyether sulphone (Ultrason E 3000 from BASF) and 13.4% PVPP (XL10 from ISP) and 6% PVP (ISP) in 60.3% NMP and 6.9% glycerol was spun into a hollow fibre and treated as described in US-A-4,798,847. In this way a hydrophillic hollow fibre was obtained of a pore size of 1 micrometer, whereby the particles of the active adsorbent are incorporated and immobilized in the matrix. Example II Membranes from Example I were brought into a filtration module having a surface area of 172 cm 2 . Unfiltered Pilsner beer, non-stabilized and containing yeast (Bavaria, Lieshout) was filtered at an average pressure of 0.6 bar. The flux was on average 100 l/m 2 /h. Filtration took place up to a thickening of 2.9 (5.2 litre on a total of 8 litre). The temperature was 0°C. The following results were obtained: Plato EBC Tannoide Ortho cyanogen Poly phenol Starting beer 12.14 32 0.490 209 Start of filtration 12.01 0.48 0 0.184 90 End of filtration 12.11 0.48 0 0.282 134 This experiment shows that it is possible to filter and stabilize beer in one step. In view of the fact that the fibres contained about 1.72 g PVPP and that this means that normally 3.44 litre can be filtered, these are excellent results (figures recommendation ISP Polyclar R). The fact that the EBC is good shows also that the adsorbent is excellently immobilized and that there is no loss.

Claims: A non dynamic microfiltration and/or ultrafiltration membrane consisting of a polymer forming a matrix and having nominal pores of 0.001-10 µm, wherein the matrix of the membrane incorporates polyvinyl polypyrrolidone particles as an active adsorbent. The membrane according to claim 1, wherein the polyvinyl polypyrrolidone is present in the membrane in an amount of 5-90% by weight. The membrane according to claim 2, wherein the polyvinyl polypyrrolidone is present in the membrane in an amount of 30-70% by weight. The membrane according to claim 1, wherein the membrane matrix is hydrophilic. The membrane according to claim 1, wherein the membrane is asymmetric. The membrane according to claim 1, wherein the membrane is constructed of different layers. The membrane according to claim 1, wherein the nominal pore size of the membrane is 0.05-5 µm. The membrane according to claim 7, wherein the nominal pore size of the membrane is 0.2-1.0 µm. The membrane according to claim 1, wherein the membrane is tubular, flat or capillary. A method of preparing a membrane according to claims 1 - 9, comprising preparing a polymer solution/suspension by mixing together polysulphone or polyether sulphone, Polyvinyl Pyrrolidone, and a suitable solvent mixture in which as active adsorbent polyvinyl polypyrrolidone particles is suspended; and processing the polymer solution/suspension into a membrane. The method according to claim 10, wherein 5-20 parts by weight of polyether sulphone, 1-10 parts by weight of polyvinyl pyrrolidone, 5-30 parts by weight of polyvinyl polypyrrolidone particles, and 0-15 parts by weight of glycerine in N-methyl-pyrrolidone are used. A method of removing dissolved components from a liquid comprising contacting the liquid with a membrane according to claim 1, wherein the adsorbed components are periodically removed by regeneration of the membrane. A method of removing undissolved components and dissolved components from a liquid comprising leading the liquid along an asymmetric membrane according to claim 1, which has a pore structure such that the pores at the membranes feed side are larger than the nominal pore size, and the pores of the nominal pore size occur in the section toward the permeation side, wherein the undissolved components are removed from the asymmetric membrane by back-flushing and the dissolved/adsorbed components by regeneration of the membrane. The method according to claims 12, wherein longitudinal flow filtration is applied. A method of removal of components causing turbidity from a liquid by means of a membrane according to the claim 1, wherein said membrane is an asymmetric membrane having a pore structure such that the pores at the membrane's feed side are larger than the nominal pore size, and the pores of nominal pore size occur in the section toward the permeation side, comprising leading the liquid along said membrane, separating undissolved components by said membrane, and flushing back the membrane to carry away undissolved components. The method according to claims 12-15, wherein the liquid is beer, wine, fruit juice, bacterial suspension, blood, milk, or an enzyme suspension. The method according to claims 12-15, wherein the liquid is crude beer. The method according to claim 12 or 13, wherein the regeneration fluid is a 0.5 to 2% NAOH solution at 50°-90° C. The method according to claims 13 or 15, wherein back-flushing of the membrane takes place intermittently with a frequency of 1 sec.-10 min. for 0.01-1 sec. at a back pressure of 0.5-5 bar. The method according to claims 19, wherein the longitudinal flow velocity is less than 2 m/sec. The method according to claims 12-20, wherein the pressure difference over the membrane is less than 0.5 bar.

Inventors: KOENHEN DIRK MARINUS, KOENHEN, DIRK MARINUS
Applicants: X FLOW BV, X-FLOW B.V.
Application year: 1994
Main classification: B01D61
IPC codes: B01D69, B01J20, B01D61, B01D65, C12H1