HIGH Tc SUPERCONDUCTORS MADE BY METAL HETEROSTRUCTURES AT THE ATOMIC LIMIT

Abstract: We describe superconductors with a high critical temperature formed by heterostructures at the atomic limit that can be realized artificially by molecular beam epitaxy, sputtering, lithography, chemical synthesis, electrochemical deposition or other similar technologies, made by a plurality of first portions of a superconducting metallic material forming a lattice of substantially equal elements with constant period lambda p, at least in a first direction (y), and a plurality of second portions formed by a material with different electronic structure from that of the first portions, intercalated to the first portions to realize the separation between said first portions; the heterostructure is characterized by the fact that the plurality of first portions have a size (L) and a period ( lambda p) as to satisfy the condition for the shape resonance condition for the electrons at the Fermi level and the plurality of second portions have a size (W) smaller or of the order of the superconducting Pippard coherence length xi 0 of the superconducting material forming the first portions. Fig. 2.

Description: Description High Tr superconductors made by metal heterostructures at the atomic limit Technical Field The present invention relates to superconductors with a high critical temperature characterized by being formed by a heterostructure made by first portions of a superconducting material of a size L pushed toward the atomic limit. Moreover the invention relates to a method to realize these superconductors. It is well known that a wide industrial application of superconductivity is limited by the fact that the superconducting metals available on the market exhibit very low critical temperatures (the critical temperature indicates the temperature for the onset of the superconductivity, i.e., for the zero resistivity and diamagnetism). These very low temperatures, of the order of few degree's Kelvin, can be reached by using low temperature technologies, which implies high cost and difficulties in the operation. Therefoϊ i the research in this field is addressed to realize new superconducting materials that wil 1 show higher critical temperatures. Background Art A recent innovation in this field is the discovery of superconductivity in cuprate perovskites that show critical temperatures of the order of hundred degree's Kelvin. However this class of ceramic superconductors has a limited industrial application because these materials are fragile, they are difficult to shape and it is difficult to keep under control the oxygen content. These difficulties generate limits for the industrial applications of superconducting electronic devices using these ceramic materials. Another difficulty for the advances in this field is due to the lack of a theory that explains the superconductivity at high temperature in these materials, therefore the progress in these materials advances by empirical approaches. Disclosure of Invention The present invention as claimed is intended to overcome said difficulties by definition of the physical parameters for the design of new superconducting heterostructures with a critical temperature larger by several times than that of the bulk metallic superconducting materials. In accordance with the present invention I provide a superconductor with high critical temperature characterized by being formed by a plurality of first portions of a superconducting material, forming a lattice of substantially equal elements with constant period λp, at least in a first direction y, and a plurality of second portions formed by not the same material as the plurality of first portions; said plurality of first portions having a size L and period λp, measured in said first direction y, as to satisfy the condition for the "shape resonance" of the electrons at the Fermi level; said plurality of second portions having a size W of the order of the superconducting Pippard coherence length ξø of the superconducting material (W< ξø) forming said plurality of first portions. The present invention is based on the discovery that the superconductivity with high critical temperature is related to a particular heterogeneous structure of the superconducting material; said heterogeneous structure can be found in a cuprate perovskite. This heterogeneous structure determines an "amplification" of the critical temperature in comparison with that of the homogenous superconducting material. Therefore by making artificial heterogeneous structures including any superconducting metal with a low critical temperature this is multiplied by an "amplification factor" related to the selected heterostructure, providing a superconductor with an artificial ordered heterogeneous structure with a critical temperature several times, up to 5 or 10, larger than that of the homogeneous material. The invention relates to a method to realize superconducting heterostructures with high critical temperature according with the principal claim characterized by the following phases: - to prepare a substrate made by a material that can be a metal, or a non metal. - formation on the substrate of a plurality of first portions of a superconducting material, which have at least in a direction y a selected dimension L and a selected spacing W. - formation on said first portions of second portions of a material with different electronic structure, that play the role of spacers. The spacing W should be of the order of the superconducting Pippard coherence length ξø of the superconducting material (W< ξø) forming said plurality of first portions. - repetition of said phases of formation by a selected number of times up to realize a three-dimensional heterostructure; said dimensions L and spacing W are selected in order to realize for the electrons at the Fermi level in the superconducting metal a "shape resonance" condition. In particular said heterostructure can be realized by molecular beam epitaxy. A second method to realize superconductors with high critical temperature according with the principal claim, but more simple, relates to the formation of a three- dimensional heterostructure made by a plurality of films of a superconducting material, first portions, separated by a plurality of non superconducting films (or superconductors with a lower critical temperature), second portions; the thickness L of the superconducting films, and the thickness W of the non superconducting films are such to realize a "shape resonance" condition for the electrons at the Fermi level in the superlattice of superconducting films. In order to realize a "shape resonance" condition the thickness of the superconducting metal film will be of the order of the thickness of few atomic layers, therefore the film thickness should be controlled to be uniform at the atomic limit. Brief Description of Drawings -Figure 1 shows the structure of the Cuθ2 plane in Bi2Sr2CaCu2 '~8 decorated by stripes of different Cu site conformations, distorted square pyramids, as determined by the author. -Figure 2 shows the structure of the superconducting heterostructure at the atomic limit, formed by a superlattice of quantum stripes realized in Bi2Sr2CaCu2C'~8 which according with the present invention gives an amplification of the critical superconducting temperature by about a factor 5. -Figure 3 shows the qualitative behavior of the density of states of the superlattice of quantum stripes in the Cuθ2 plane. The Fermi energy is tuned at a maximum in the density of states to increase the critical temperature. -Figures from n° 4 to n° 7 show several types of superconducting heterostructures at the atomic limit made by superlattices of quantum wells, quantum wires, and quantum dots, and quantum spheres respectively. -Figure 8 shows as an example a method to create a superlattice of quantum wires. Best Mode for Carrying Out the Invention The present invention is based on the idea that it is possible to rise the critical temperature Tc < » of bulk homogeneous superconductors (metallic elements, alloys, metallic compounds, doped semiconductors or oxides) by shaping the superconducting material in the form of a pluraUty of units forming a superlattice where the size L of each unit is so small to show the effect of quantization of the electron wave vector in at least one dimension, i.e. superlattices of quantum wells, quantum wires, or quantum dots, where the Fermi level of the said superconducting superlattice is tuned close and above the bottom of a superlattice subband, that is called a "shape resonance" condition for the electrons at the Fermi level. At the "shape resonance" condition the Fermi level is tuned to a maximum of the electronic density of states artificially created by the confinement of the electrons in the superconducting units. A similar idea (to increase the superconducting critical temperature by quantum confinement, i.e., by tuning the Fermi level at a "shape resonance" condition) in a single quantum well was proposed by Blatt and Thompson /. M. Blatt and C. J. Thompson Phys. Rev. Lett. 10, 332 (1963); C. J. Thompson andJ. M. Blatt, Phys. L ^ ett. 5, 6 (1963)] but it was discarded and forgotten by the scientific community because quantum fluctuations in low dimension, D<2, suppress the superconducting phase in a single quantum well or quantum wire. The applicant has addressed his studies to show that it is possible to increase the critical temperature T c by realizing the "shape resonance" condition not in a single superconducting unit but in a "superlattice" of units, showing the quantization effect due to the reduced size, to overcome the problems listed above. He has used for experimental verification the ceramic superconductors of the family Bi2212 (perovskites of copper oxides of chemical formula Bi2Sr2Caι_ x Y x Cu2θg + y). The fact that in these oxides the planes of Cu oxide were not homogeneous was known [A. Bianconi, et al. in ".Lattice Effects in High-T c Superconductors" edited by Y. Bar-Yam et al, World Scientific Pub., Singapore, 1992, pag. 65; A. Bianconi, in "Phase Separation in Cuprate Superconductors" edited by K. A. Muller & G. Benedek, World Scientific Pub., Singapore, 1992, pag. 125] in particular it was known that in this material there are domains where the distance between the Cu atom and the apical oxygen had different values. The applicant has demonstrated that the copper oxide plane in Bi2Sr2CaCu2θg + y at a temperature lower than 120K has the structure modulated as shown in figure 1, where there are a plurality of domains, i.e., stripes of width W, called barriers, formed by a lattice of distorted Cu site conformations where the bond of Cu with the apical oxygen is short ( < 2.4 A ), with constant period λp in the direction y, separated by stripes of width L, where the bond of Cu with the apical oxygen is long ( > 2.5 A ). The width L of the stripes has been obtained by the measure of the ratio between the - number of the long copper-apical oxygen bonds and the total number of copper-apical oxygen bonds by using the EXAFS method as described in [X Ray Absorption: Principle, Applications Techniques of EXAFS, SEXAFS andXANES edited by R. Prim andD. Koningsberger, J. Wiley and Sons, New York 1988 ]; the period λp in the y direction has been measured by electron diffraction; moreover the component of the wave vector of the electrons at the Fermi level in the y direction (k y ) has been measured by angular resolved photoemission [following Z. X. Shen J. Phys. Chem. Solids 53, 1583 (1992) ]. The measures carried out on a single crystal grown by the "floating zone" method with T c = 84° K have provided the period of the modulation λp=4.7a (where a= 5.4 A is the lattice constant); the width L = 2.7a; and the component of the wave vector of the electrons at the Fermi level kpy ~ 0.38 (±0.03) 2π/a. The width W of the stripes characterized by the Cu sites with the short Cu - apical oxygen bond has been found to be 2a in the temperature range lower than 120K. The width W=10.8 A of the barriers is of the order of the superconducting Pippard coherence length ξø of the superconducting material. The investigations carried out on different superconductors with different doping level, with different Y content have shown that the superstructure period changes and L changes with doping by keeping the Fermi level at the "shape resonance condition"; the width W has been assumed to be doping independent because it is associated with a lattice instability at the critical doping of one hole per 8 Cu sites δc=l /8 [W. E. Pickett et al. Phys. Rev. Lett. 62, 2751 (1989)] Therefore the electrons at the Fermi level in the stripes of width L are at the "shape resonance" condition, where they are trapped in the stripes of size L, defined by the barriers of size W, realizing a superlattice with period λp [see figure 2] and the Fermi level is tuned above the bottom of the m=2 subband with the wave vector kp y ~ 2π L. The "shape resonance" condition can be defined in a more general way with reference to figure 3 where the dashed line indicates the curve of the electronic density of states versus the electron energy for a two dimensional homogeneous conducting plane and the solid line is the "Density of states" versus "Energy" curve modified for the heterostructure shown in figure 1 and 2; therefore the density of states is modified in comparison with the homogeneous material by the confinement of the electrons in the superlattice of one-dimensional stripes and it shows new maxima at the energies E m (where m is the number of the resonance); for the "shape resonance" condition we intend the quantum state where the Fermi level is tuned in the range of a maximum of the density of states/energy curve above the bottom of a subband E generated by the heterostructure in a superconducting metal, as in figure 3. Following the standard theory for superconductivity (BCS theory) the critical temperature T C oo for the transition from the normal metallic phase to the superconducting phase in a infinite homogeneous material is (1) T c « ~ ωD exp(-l N 0 V) for the Cuθ2 superconducting plane the Debey temperature is known to be about 500 K, and the product NøV is known to be about 0.2, where No is the density of states at the Fermi level and V the electron-phonon coupling constant; therefore the critical temperature T Cα> for a homogeneous Cuθ2 plane has been estimated to be in the range of 7-15 K. For the heterogeneous Cuθ2 plane shown in figure 1, where the Fermi level is tuned to the m=2 maximum of the density of states of the m=2 subband of the superlattice of quantum stripes, the density of states No at the Fermi energy is enhanced and the critical temperature is enhanced. Following the approach of Thompson and Blatt [C. J. j Thompson and J. M. Blatt, Phys. Lett. 5, 6 (1963) ] the critical temperature for a superlattice of quantum stripes can be written as (2) T c ~ ω D exp(-l/NøV) exp{+k/(NøV)} j 5 where exp{ +k/(NøV) } is an "amplification factor" A= T c /T c » determined by the quantum confinement; k is related with the effective increase of the density of states at the Fermi level by the quantum confinement in the heterostructure relative to the homogeneous material and by the shape resonance number m. For the superlattice of quantum stripes with the Fermi level tuned above the bottom of the m=2 subband, as it 2ø has been found in Bi2212, the factor k has been estimated to be 1 3 and therefore an amplification factor A of the order of 5 has been obtained. The critical temperature is enhanced in the superlattice to the high temperature range of 35-85K from the normal expected value of 7-15K for the homogeneous Cuθ2 plane. From what it has been described above the applicant has deduced that the 25 superconductivity with high critical temperatures can be obtained in normal superconducting metals, as for example the largely used niobium compounds, if the physical structure of the superconductor is designed to follow the particular conditions which are verified for the copper oxide plane in Bi2212, the structure of the new metallic superconducting materials with high T c should reproduce the conditions of this ordered ™ non homogeneous phase which has been determined to be present in Bi2212. In accordance with the present invention a superconductor with high critical temperature shows a structure as in figure 2 where I give a pictorial view of the superconductor 1 shown at the level of atomic planes formed by a metal heterostructure made by a plurality of first portions 3 of any superconducting material, forming a lattice of substantially equal elements with constant period λp, at least in one direction (in this case the direction y) and a plurality of second portions 4, formed not by the same material as the plurality of first portions 3, disposed to separate the portions 3; in order to activate in this heterostructure the process of the amplification of the critical temperature characteristic of the material forming the portions 3 in the homogeneous phase it is necessary that the described heterostructure realizes a superlattice of quantum units as described for the copper oxide plane in figure 1. This is obtained, following the present invention, by making the portions 3 with a size L, measured in the direction y, such that it realizes the conditions of the shape resonance for the electrons at the Fermi level, with wave length λp, this condition in the described heterostructure means that the size L should satisfy the simplified formula: m λp (3) L Moreover from the comparison between the theory of the superconductivity state in a superlattice and the heterostructure found in Bi2212 we deduce that a second condition to realize the invention is that the portions 4 should have a size W of the order of the Pippard coherence length ξø of the superconducting material forming the portions 3 in order to stabilize the superconducting quantum state. For "size of the order of we intend to say, here and in the following, that the value of W should be ξø A where x should be in the range of 1 to 100 in order to have a Josephson coupling between the superconducting portions. In the case of Bi2212, we have x~l, but for systems with larger ξø it is possible to use x>l and to decrease W, but in any case W should be large enough to reduce the probability for single particle hopping between the superconducting portions and to reduce the dispersion of the superlattice subbands. By going in the detail of the realization of the heterostructure shown in figure 2 the superconductor with high critical temperature is formed by a plurality of parallel atomic planes 2 and each plane 2 includes a plurality of stripes 3 formed by the superconducting metallic material (including in this definition also the doped oxides) that have, according with (3), the width L equal to an integer number of half of the wave length of the electrons at the Fermi level in the stripes 3. Moreover the planes 2 include a plurality of second stripes 4, alternated to the stripes 3 and formed by a material with an electronic structure different from that forming the first stripes, that can be a metal with lower critical temperature or a non metal (a non metal indicates any material also an organic compound). The stripes 4 have, according with the requirements listed above, a width W of the order of the Pippard coherence length ξø of the superconducting material forming the stripes 3; moreover in order to stabilize the three-dimensional superconducting phase it is necessary to have also in the z direction neighboring parallel superconducting planes decorated by the superlattice of quantum stripes at a distance h of the order of the Pippard coherence length ξø. For the superconductor 1, with the structure shown in figure 2, it is possible to apply the formula (2), therefore it is possible to predict the enhanced critical temperature once the superconducting material forming the stripes 3 is known; in other words it is possible "a priori" to realize a superconductor with the desired critical temperature, by selecting the superconducting material forming the stripes 3 and the size of the components of the superlattice forming the heterostructure shown in figure 2 in order to tune the Fermi level at the desired order of the shape resonance. The larger amplification is obtained for the smaller size of the superconducting stripes tuning the Fermi level to the lower orders m of the shape resonances. Moreover the amplification factor in the heterostructure in formula (2) quenches the effect of the term exp(- 1 NoV) on the formula (1) which reduces the critical temperature, therefore the amplification factor will be more effective in the heterostructures formed by the superconducting material with a larger COD- With reference to the drawing in figure 4, a superconductor with high critical temperature 10 is shown, which have a structure different from that shown in figure 2, but it is designed in accordance with the parameters of the invention; in particular it is formed by a plurality of first superconducting layers 11 altemated with second layers 12 formed not by the same material as the first layers; the layers 11 have a selected thickness L, and the layers 12 have a selected thickness W in order to tune the Fermi level to the shape resonance condition of the superlattice and W < ξø. With reference to the drawing in figure 5, a third example of a superconductor 20 with high critical temperature realized according with the present invention is shown; the superconductor 20 is formed by a pluraUty of wires 21, formed by a superconducting material, paraUel to each other forming a three-dimensional lattice; they are embedded in a matrix 22 formed not by the same material as the wires 21. The section of wires, a square or a circle, has a selected size L in order to satisfy the selected shape resonance condition and they are separated in the matrix 22 by the spacing W. In general in order to determine the size L which should satisfy the "shape resonance condition" in the superlattice a formula can be used in the limit of negUgible single particle hopping between the stripes, layers or wires: (4) k F ~ (2π/L) (m 2) where kp is the wave vector of the electrons at the Fermi level of the superconducting material. More in general the condition for the "shape resonance" shown in figure 3 can be written as (5) E F ~ E, m which means that the Fermi energy is tuned to an artificial maximum of the electronic density of the states and it takes into account of the possible shift of the condition (4) due to dispersion of the superlattice subband for a non negligible hopping between the superconducting units. Moreover in the case that the values of L obtained by using the formula (4) are so small that is difficult to realize the superconducting portions it is possible to use for the "shape resonance" condition: (6) | kF-G | ~ (2π L) (m/2) where G is the vector of the reciprocal lattice of the superconducting material, kp is wave vector of the electrons at the Fermi level and m is an integer number. Figure 6 shows another example of a superconductor 30 with high critical temperature realized according with the present invention; the superconductor 30 is formed by a plurality of spherical nuclei 31 formed by a superconducting material forming a three-dimensional lattice 32; they are embedded in a matrix 33 formed not by the same material as the superconducting nuclei 31. The size of the nuclei is L and they are separated by W. Finally figure 7 shows a superconductor 40 with high critical temperature realized according with the present invention similar to 30, but the superconducting material is formed by a plurality of empty spheres 41 of size L forming a three-dimensional lattice embedded in a matrix 42 formed not by the same material as the superconducting spheres 41 that provides the separation W between the spheres. Another choice to realize the superconducting heterostructure with the high critical temperature according with the present invention is to copy the structure of the superconducting planes in Bi2212 (figure 1) forming a superlattice as in figure 2 where the material that forms the second portions 4 is different from the material forming the first portions only at the level of the crystal lattice. In conclusion, the superconductor with high critical temperature according with the present invention should have one of the structures described above, where L should satisfy the "shape resonance" condition according with one of the given formulas (4), (5) and (6) and where W is smaUer or of the order of the superconducting Pippard coherence length ξø. The superconducting materials described in figures 2, 4, 5, 6 and 7 can be realized by chemical reactions, and/or doping homogeneous materials as in the case of cuprates, or they can be realized "artificiaUy" by making the heterostructure foUowing the present invention as it is described below for a superlattice of quantum wires (figure 8); first a flat surface at the atomic level of a substrate 50, made by a metal, or a non metal is prepared; in the following phase a plurality of superconducting units 51 made by a superconducting material different from the substrate; the units 51 are obtained by molecular beam epitaxy or by other equivalent techniques (as for example sputtering, lithography, chemical synthesis, electrochemical deposition). The units 51 are disposed to reaUze a lattice of identical units of size L forming a superlattice in at least one direction y separated by the selected spacing W in such a way to satisfy the described condition for the "shape resonance" in the superlattice; a good lattice mach of the crystalUne surfaces of the different components is required in order to reduce the stress at the interface; in the next step a material 52 is disposed to cover the substrate 50 and the superconducting units 51 ; the last two phases are repeated a fixed number of times in order to make a three-dimensional metalUc heterostructure 60. In the case of the superconductor 10 in figure 4 the method to create an artificial superlattice of superconducting layers with thickness satisfying the "shape resonance" condition (quantum weUs) consists mainly in the alternate deposition of layers 11 and 12 by molecular beam epitaxy or by other equivalent techniques (as for example sputtering, lithography, chemical synthesis, electrochemical deposition) by a fixed number of times in order to reatize a three-dimensional metaUic heterostructure 10; care should be taken to find materials 11 and 12 with good crystal lattice matching at the interface and to grow flat surfaces at the atomic level. Industrial Applicability The metalUc heterostructures with high critical temperature will found their appUcations in the production of electronic devices using superconducting materials, we cite only few examples but the Ust is larger: SQUID, Josephson junctions, infrared detectors, particle detectors, radiofrequency filters.

Claims: Claims 1. Superconductor with high critical temperature, characterized by being formed by a heterostructure made by a plurality of first portions (3, 11, 21, 31, 41) of a superconducting material, forming a lattice of substantiaUy equal elements with constant period λp, at least in a first direction (y), and a plurality of second portions (4, 12, 22, 32, 42) formed not by the same material, intercalated to the first portions to realize the separation between said first portions; said plurality of first portions (3, 11, 21, 31, 41) having a size L and a period λp, measured on said direction (y), as to satisfy the condition for the shape resonance condition for the electrons at the Fermi level; said plurality of second portions (4, 12, 22, 32, 42) having a size W smaller or of the order of the superconducting Pippard coherence length ξø of the superconducting material forming the first portions. 2. Superconductor with high critical temperature in accordance with the claim 1, characterized by being formed by a pluraUty of first layers(l 1) alternated with second layers (12), the first layers (11), first portions, have a thickness L and the second layers (12), second portions, a thickness W to tune the Fermi level to a shape resonance. 3. Superconductor with high critical temperature in accordance with the claim 1, characterized by being formed by a pluraUty of parallel atomic planes (2) separated by the distance (h) in the direction (z); each plane is decorated by a plurality of stripes (3) of a superconducting material, running in the direction (x) with a width (L) and a period λp, measured the direction (y), as to satisfy the condition for the shape resonance condition for the electrons at the Fermi level, and by a plurality of second stripes (4) alternated to the first stripes (3) formed not by the same material; said pluraUty of second stripes (4) having a width W smaUer or of the order of the superconducting Pippard coherence length ξø of the superconducting material forming the first portions; said plurality of planes being separated by the distance h of the order of the superconducting Pippard coherence length ξø of the superconducting material forming the superconducting stripes (3). 4. Superconductor with high critical temperature in accordance with the claim 1, characterized by being formed by a plurality of parallel superconducting wires (21) forming a three-dimensional lattice, embedded in a matrix (22) formed not by the same material; said pluraUty of wires (21) have a section of size (L) of the order of an integer multiple of the half of the wavelength of the electron at the Fermi level in order to realize a shape resonance condition, and they are separated by the distance (W) smaller or of the order of the superconducting Pippard coherence length ξø of the superconducting material forming the superconducting wires (21). 5. Superconductor with high critical temperature in accordance with the claim 1, characterized by being formed by a plurality of nuclei (31) with a substantiaUy spherical form, formed by a superconducting material separated by the distance (W) one from the other, forming a three-dimensional lattice embedded in a matrix (32); said pluraUty of nuclei (31) have a section of size (L) of the order of an integer multiple of the half of the wavelength of the electron at the Fermi level in order to realize a shape resonance condition, and they are separated by the distance (W) smaUer or of the order of the superconducting Pippard coherence length ξø of the superconducting material forming the superconducting nuclei (31). 6. Superconductor with high critical temperature in accordance with the claim 1 , characterized by being formed by a plurality of empty spheres (41) formed by a superconducting material; as for example fullerenes, separated by the distance (W) one from the other, forming a three-dimensional lattice embedded in a matrix (42); said pluraUty of empty spheres (41) have a section of size (L) in order to realize a shape resonance condition, and they are separated by the distance (W) smaUer or of the order of the superconducting Pippard coherence length ξø of the superconducting material. 7. Superconductor with high critical temperature in accordance with the claim n.1 , reaUzed by a superlattice of superconducting first portions, according with the claims listed above, characterized by the fact that the second portions are formed by a material different from that forming the first portions only for a different crystal lattice, or for a different composition, or for a different concentration of chemical dopants. 8. Method to realize superconductor heterostructures with high critical temperature characterized by the following main phases: -preparation of the surface of the substrate formed by a metal or a non metal, and deposition of a buffer, if it is necessary for lattice matching and/or smoothing the surface. - formation of the first superconducting portions of size L controlled at atomic level. . formations of the second portions, playing the role of spacers, in order to separate the first portions by the spacing W, by forming well-defined domain waUs at the atomic level between the first and second portions. - repetition of the phases listed above for the established number of times in order to reaUze a three-dimensional superlattice. The size L of the first portions and the separation w are such that the Fermi level is tuned to a "shape resonance" condition of the superlattice of superconducting portions. 9. Method to reaUze a superconducting heterostructure with high critical temperature characterized by the use of the molecular beam epitaxy method to obtain said heterostructure. 10. Method to realize superconductor with high critical temperature characterized by a three-dimensional heterostructure formed by alternated parallel layers of a superconducting (first portions) and non superconducting (second portions) layers in accordance with claim 1 by molecular beam epitaxy or by other equivalent techniques as sputtering, lithography, chemical synthesis, electrochemical deposition by using two materials with good crystal lattice matching at the interface and by controlUng the grow of flat interfaces at the atomic level of the layers of selected thickness to obtain the "shape resonance" condition in the superlattice of superconducting units. Antonio Bianconi

Inventors: BIANCONI ANTONIO, BIANCONI, ANTONIO
Applicants: BIANCONI ANTONIO, BIANCONI, ANTONIO
Application year: 1994
Main classification: H01L39
IPC codes: C01G1, C01G29, C23C14, C25D9, C30B29, H01L39