Diene polymers and copolymers having an alkoxysilane group

Abstract: The present invention provides a process for preparing a conjugated diene/vinyl aromatic hydrocarbon random copolymer or intermediate random copolymer whose vinyl aromatic hydrocarbon units are between random and block distribution, characterized by the steps of: (a) (co)polymerizing a conjugated diene hydrocarbon monomer and a vinyl aromatic hydrocarbon with an organic lithium initiator without a nitrogen atom, obtaining a conjugated diene/vinyl aromatic hydrocarbon copolymer having a lithium active end; and (b) adding at least one silane compound selected from an alkoxysilane compound having an epoxy group, an aryloxysilane compound having an epoxy group, an aralkyloxysilane compound having an epoxy group, to the copolymer obtained in step (a).

Description: FIELD OF THE INVENTION The present invention relates to a polymer and a composition using said polymer. More particularly, the present invention relates to a novel functionalized polymer having excellent fracture properties, good abrasion resistance and low hysteresis loss (low rolling resistance and low fuel consumption) and a novel elastomeric composition for a tire tread using the functionalized polymer. PRIOR ART OF THE INVENTION As tires for higher performance are being developed, a rubber having superior fracture properties, good abrasion resistance and low hysteresis loss (low rolling resistance) is desired as the rubber for the tire tread for such tires. For decreasing the hysteresis loss, cis-1,4-polybutadiene rubber and the like are used. However, the polybutadiene rubber and the like do not have good fracture properties even though they have good abrasion resistance. As a rubber having a remarkably lower hysteresis loss, a solution polymerized butadiene-styrene rubber having the tin-carbon bond in the molecular chain has been developed. However, this rubber does not always have a good balance between wet grip and low rolling resistance. An elastomeric composition for a tread in which carbon black alone is used as the filler for the rubber described above can realize the desired balance between various properties and performances to some degree. However, simultaneous improvement of wet grip and low rolling resistance to a higher degree has come to be required more urgently in recent years and it is difficult for the rubber described above to satisfy this requirement. In order to solve this problem, there have been disclosed elastomeric compositions in which white carbon such as silica is used alone or in combination with carbon black as the filler. An example of such elastomeric composition is an elastomeric composition containing a polymer modified with a silane compound at the end and silica (for example, Japanese Patent Publication Showa 52(1977)-5071, Japanese Patent Application Laid-Open Nos. Showa 56(1981)-104906, Showa 62(1987)-50346 and Showa 62(1987)-227908). However, satisfactory improvements in the reinforcing property and the dispersion of fillers such as silica, and consequent improvements in the mechanical properties, are not exhibited by this polymer because this polymer does not have a sufficient number of alkoxy groups remaining in the polymer and also because the modification is made only at one of the molecular ends. Even when, for example, a dilithium compound is used as the initiator for the preparation of the polymer to modify both molecular ends (Japanese Patent Application Laid-Open No. Showa 62(1987)-227908), the ends formed are modified with alkoxysilane groups. Because the alkoxysilane group has the property that a coupling reaction takes place between the groups, the molecular weight of the polymer is practically uncontrollable, and the viscosity of the polymer cement during and after the modification reaction is increased, which causes problems with respect to stability in steam stripping as well as with respect to the stability of the prepared polymer over time. Elastomeric composition comprising a polymer modified with a nitrogen compound at the end and silica are also known (for example, Japanese Patent Application Laid-Open No. Showa 64(1989)-22940). A diene-type polymer obtained by the alkyllithium-initiated polymerization is modified mainly at the terminated end part by copolymerization of a monomer containing nitrogen or by end modification using an aminobenzophenone compound or the like, and is used in these elastomeric compositions. Similarly to the polymer described above, only one end is modified with the compound containing nitrogen in this polymer, and the reinforcement with silica and the like is insufficient. An elastomeric composition (a pneumatic tire) comprising a solution polymerized butadiene-styrene rubber having a specific molecular structure and silica has also been proposed (for example, Japanese Patent Application Laid-Open No. Heisei 3(1991)-239737). Reinforcement with silica is improved in this elastomeric composition to some degree but is still insufficient. Furthermore, diene polymers are mainly used in the polymers described above. It has been known that diene polymers have low affinity with white carbon such as silica and it is difficult to obtain a homogeneously dispersed rubber composition by milling. To improve this drawback, a large amount of an expensive silane coupling agent is mixed together in many cases. Because the silane coupling agent is easily hydrolyzed in air, sufficient care must be taken in the handling thereof, and it is difficult to obtain a rubber composition with good reproducibility. Therefore, the elastomeric composition described above do not have sufficient affinity or dispersing property with silica, and it is difficult for the elastomeric compositions to exhibit sufficient reinforcement with silica, to exhibit sufficient fracture properties, and to achieve a high level of balance between various properties such as abrasion resistance, wet grip, low rolling resistance, and the like. Thus, the current situation in the field is that a polymer composition which satisfies various required properties with a good balance and which is advantageous for practical use has not yet been obtained. SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a novel functionalized polymer having excellent fracture properties and low hysteresis loss (low rolling resistance and low fuel consumption) and a process for the manufacture of the functionalized polymer. Thus the invention concerns a process for preparing a functionalized polymer of the formula wherein A represents a group derived from the organic lithium initiator used in step (a) defined below, P is a conjugated diene (co)polymer composed of at least one conjugated diene having 4-12 carbon atoms, optionally together with a vinyl aromatic hydrocarbon, R 1 and R 2 , which may be the same or different, represent an aliphatic, alicyclic and aromatic hydrocarbon group having 20 or less carbon atoms; R 3 is selected from aliphatic and alicyclic hydrocarbon groups having 20 or less carbon atoms; R 4 .is an oxygen atom or an optionally substituted methylene group; R 5 is an aliphatic hydrocarbon group having 20 or less carbon atoms; n is 0 or 1; and x is an integer of 1-3; and z is an integer of 0-2; with 1 ≤ x + z ≤ 3; characterized by the steps of: (a) (co)polymerizing at least one conjugated diene hydrocarbon monomer and optionally a vinyl aromatic hydrocarbon with an organic lithium initiator without a nitrogen atom, obtaining a conjugated diene/vinyl aromatic hydrocarbon (co)polymer having a lithium active end; and (b) adding to the copolymer obtained in step (a) at least one silane compound selected from γ-(3,4-epoxycyclohexyl)ethyl trimethoxysilane, 3-glycidoxyethyl trimethoxysilane, 3-glycidoxypropyl trimethoxysilane, 3-glycidoxybutyl trimethoxysilane, 3-glycidoxypropyl triethoxysilane, 3-glycidoxypropyl tripropoxysilane, 3-glycidoxypropyl tributoxysilane, 3-glycidoxypropyl triphenoxysilane, 3-glycidoxypropyl methyl dimethoxysilane, 3-glycidoxypropyl ethyl dimethoxysilane, 3-glycidoxypropyl ethyl diethoxysilane, 3-glycidoxypropyl methyl diethoxysilane, 3-glycidoxypropyl methyl dipropoxysilane, 3-glycidoxypropyl methyl dibutoxysilane, 3-glycidoxypropyl methyl diphenoxysilane, 3-glycidoxypropyl dimethyl methoxysilane, 3-glycidoxypropyl diethyl ethoxysilane, 3-glycidoxypropyl dimethyl ethoxysilane, 3-glycidoxypropyl dimethyl phenoxysilane, 3-glycidoxypropyl diethyl methoxysilane, 3-glycidoxypropyl methyl diisopropeneoxysilane, bis(3-glycidoxypropyl) dimethoxysilane, bis(3-glycidoxypropyl) diethoxysilane, bis(3-glycidoxypropyl) dipropoxysilane, bis(3-glycidoxypropyl) dibutoxysilane, bis(3-glycidoxypropyl) diphenoxysilane, bis(3-glycidoxypropyl) methyl methoxysilane, bis(3-glycidoxypropyl) methyl ethoxysilane, bis(3-glycidoxypropyl) methyl propoxysilane, bis(3-glycidoxypropyl) methyl butoxysilane, bis(3-glycidoxypropyl) methyl phenoxysilane, tris(3-glycidoxypropyl) methoxysilane, β-(3,4-epoxycyclohexyl)ethyl trimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl triethoxysilane, β-(3,4-epoxycyclohexyl)ethyl tripropoxysilane, β-(3,4-epoxycyclohexyl)ethyl tributoxysilane, β-(3,4-epoxycyclohexyl)ethyl triphenoxysilane, β-(3,4-epoxycyclohexyl)propyl trimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl dimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl ethyl dimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl ethyl diethoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl diethoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl dipropoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl dibutoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl diphenoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl methoxysilane, β-(3,4-epoxycyclohexyl)ethyl diethyl ethoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl ethoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl propoxysiiane, β-(3,4-epoxycyclohexyl)ethyl dimethyl butoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl phenoxysilane, β-(3,4-epoxycyclohexyl)ethyl diethyl methoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl diisopropeneoxysilane, and a silane compound of the formula: wherein R 1 , R 4 and R 5 are as defined above, and E is a an epoxy group-containing moiety, which upon reaction with the conjugated diene/vinyl aromatic hydrocarbon (co)polymer having a lithium active end obtained in step (a) forms a group wherein R 3 is an aliphatic or alicyclic hydrocarbon group having 20 or less carbon atoms, and n is 0 or 1; and a functionalized polymer obtainable by this process. The elastomeric composition of the present invention comprises a rubber material containing a functionalized polymer in an amount of 10 or more parts by weight in 100 parts by weight of the rubber material, and a filler of 10 to 100 parts by weight based on 100 parts by weight of the rubber material, wherein the filler contains a white carbon, and the functionalized polymer comprises a diene-type polymer having an alkoxysilane group and has a molecular structure represented by at least one of and formula(3) described above. BRIEF DESCRIPTION OF THE DRAWINGS Figures 1A and 1B illustrate infrared spectra which show the presence of the Si-O bond and the Si-C bond in the polymer of the present invention. Figure 2 illustrates infrared spectra which show the presence of the Si-O bond and the Si-C bond in the polymer of the present invention. Figure 3 illustrates infrared spectra which show the presence of the OH group in the polymer of the present invention. DETAILED DESCRIPTION OF THE INVENTION The functionalized polymer represented by formula (3) described above has a molecular structure in which a moiety A representing the organic group derived from the organic lithium initiator is bonded to the end part of a conjugated diene polymer or a conjugated diene/vinyl aromatic hydrocarbon copolymer, a functional group having a hydroxyl group is bonded to another part of the polymer or the copolymer, and a silicon atom having at least one alkoxy group is bonded to the functional group having the hydroxyl group. It can be considered that the effect of the present invention arises due to the characteristic molecular structure of the functionalized polymer, which is related to at least one of the following three factors. The first factor is the reactivity of the alkoxy functional group in the molecular structure of the functionalized polymer with the surface of silica used as the filler. The second factor is the large affinity of the hydroxyl group in the molecular structure of the functionalized polymer which is located close to the alkoxy group, with silanol group at the surface of silica. The third factor is the presence of the secondary amino functional group or the imino functional group in the molecular structure of the functionalized polymer. P in formula (3), which represent the functionalized polymer of the present invention, represents a diene-type polymer which is selected from a conjugated diene polymer or a conjugated diene/vinyl aromatic hydrocarbon copolymer. The conjugated diene polymer is a polymer composed of a conjugated diene unit obtained by polymerization of a conjugated diene monomer. The conjugated diene monomer is a conjugated diene hydrocarbon having 4 to 12 carbon atoms, preferably 4 to 8 carbon atoms, in one molecule. Examples of the conjugated diene monomer include 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, octadiene, and the like. The conjugated diene monomer may be used singly or as a mixture of two or more types. Among these monomers, 1,3-butadiene is particularly preferable. The conjugated diene/vinyl aromatic hydrocarbon copolymer is a copolymer composed of a conjugated diene unit and a vinyl aromatic hydrocarbon unit which are obtained from a conjugated monomer and a vinyl aromatic hydrocarbon monomer, respectively, by copolymerization. Examples of the vinyl aromatic hydrocarbon monomer include styrene, α-methylstyrene, p-methylstyrene, o-methylstyrene, p-butylstyrene, vinylnaphthalene, and the like. Among these vinyl aromatic hydrocarbon monomers, styrene is particularly preferable. As the conjugated diene polymer, polybutadiene having excellent abrasion resistance is preferable. As the conjugated diene/vinyl aromatic hydrocarbon copolymer, butadiene/styrene copolymers having excellent abrasion resistance and aging resistance are preferable. The microstructure of the butadiene part (cis-1,4, trans-1,4, and vinyl) in the diene-type polymer, such as polybutadiene and butadiene/styrene copolymer, is not particularly limited, but can be in a range generally obtained by using an organolithium initiator. Composition of the conjugated diene/vinyl aromatic hydrocarbon copolymer, such as butadiene/styrene copolymer, is not particularly limited, but the ratio by weight of the conjugate diene unit to the vinyl aromatic hydrocarbon unit is generally 30/70 to 95/5. The distribution of the units in the copolymer may be a random distribution, a block distribution, or an intermediate distribution of these distributions. A random distribution and an intermediate distribution are generally preferable. R 1 in formula (3) represents a group selected from an aliphatic hydrocarbon group, an alicyclic hydrocarbon group, or an aromatic hydrocarbon group, each having 20 or less, preferably 10 or less, carbon atoms. Examples of the aliphatic hydrocarbon group include methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, octyl group, and the like. Examples of the alicyclic hydrocarbon group include cyclopentyl group, cyclohexyl group, cycloheptyl group, and the like. Examples of the aromatic hydrocarbon group include phenyl group, naphthyl group, biphenyl group, anthryl group, phenanthryl group, and the like. R 1 is preferably an aliphatic hydrocarbon group or an aromatic hydrocarbon group, each having 10 or less carbon atoms. R 1 most preferably is a methyl group, ethyl group, propyl group, or phenyl group. R 3 in formula (3) represents a group selected from an aliphatic hydrocarbon group and an alicyclic hydrocarbon group, each having 20 or less, preferably 6 or less, carbon atoms. Examples of the aliphatic hydrocarbon group include methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, octyl group, and the like. Methyl group, ethyl group, propyl group, and the like, are preferable among these groups. Examples of the alicyclic hydrocarbon group include cyclopentyl group, cyclohexyl group, cycloheptyl group, and the like. Cyclohexyl group is preferable among these groups. R 4 in formula (3) represents an oxygen atom, methylene group, or methylene group having substituents. Examples of the substituent include methyl group, ethyl group, propyl group, and the like. R 4 is preferably an oxygen atom or methylene group. R 5 in formula (3) represents an aliphatic hydrocarbon group having 1 to 20, preferably 1 to 10, carbon atoms. Examples of the aliphatic hydrocarbon group include methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, octyl group, and the like. Methyl group, ethyl group, propyl group, and butyl group are most preferable among these groups. In formula (3), x represents an integer of 1 to 3, z represents an integer of 0 to 2, and x + z each represent an integer of 1-3. The functionalized polymer may be a single compound having fixed values of x, and z in formula (3), or a mixture of compounds having various values of x, and z in formula (3). A mixture is generally used. In formula (3), n represents 0 or 1. This means that >R 3 -(CH 2 ) n -OH represents either >R 3 -CH 2 -OH or >R 3 -OH. When R 3 represents an aliphatic hydrocarbon group, R 3 represents a group in which n represents either 0 or 1, or a mixture of a group in which n represents 0 and a group in which n represents 1. When R 3 is an alicylic hydrocarbon, n is 0 and R 3 can have the structure of >R 3 -OH alone. The functionalized polymer of the present invention has a molecular structure comprising a combination of the molecular elements described above. In order to further improve various properties and remarkably increase the interaction with silica when an elastomeric composition comprising the functionalized polymer is formed as described later, the functionalized polymer preferably has a more specific molecular structure represented by formula (3), each comprising the following specific molecular elements. R 1 represents a group selected from an aliphatic hydrocarbon group and an aromatic hydrocarbon group, each having 10 or less carbon atoms; R 2 represents a group selected from an aliphatic hydrocarbon group having 1 to 3 carbon atoms and phenyl group; R 3 represents a group selected from an aliphatic hydrocarbon group and an alicyclic hydrocarbon group, each having 6 or less carbon atoms; R 4 represents an oxygen atom or methylene group; and R 5 represents a group selected from aliphatic hydrocarbon groups having 1 to 4 carbon atoms. Preferable examples of the functionalized polymer represented by formula (3) include functionalized polymers having molecular structures in which all combinations of the following specific diene-type polymers P and specific groups R 1 , R 2 , R 3 , R 4 , and R 5 are included. P: polybutadiene and butadiene/styrene copolymer R 1 : methyl group, ethyl group, propyl group, and phenyl group R 2 optionally: methyl group, ethyl group, and phenyl group R 3 : methyl group and cyclohexyl group R 4 : an oxygen atom and methylene group R 5 : methyl group, ethyl group, and propyl group R 2 may be present or absent in the molecule. "R 2 optionally" in the above description means that the listed groups are used for the combinations when R 2 is present in the molecule. R 2 is absent in the molecule when x + z = 3 in formula (3). Specific examples of the molecular structure of the functionalized polymer are shown in the following examples of preparation of the functionalized polymer. The method of preparation of the functionalized polymer of the present invention is not particularly limited, and is described hereinafter with reference to the examples. ethoxytriiodosilane, n-propoxytriiodosilane, phenoxytriiodosilane, and the like. The functionalized polymer represented by formula (3) can be obtained by steps of initiating polymerization of a monomer by using an organolithium compound, and adding an alkoxysilane compound having an epoxy group, such as a glycidoxy group, to the solution of the polymer having a lithium active end obtained in the step of polymerizing. Examples of the alkoxysilane compound having an epoxy group include 3-glycidoxyethyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxybutyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropyltripropoxysilane, 3-glycidoxypropyltributoxysilane, 3-glycidoxypropyltriphenoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 3-glycidoxypropylethyldimethoxysilane, 3-glycidoxypropylethyldiethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 3-glycidoxypropylmethyldipropoxysilane, 3-glycidoxypropylmethyldibutoxysilane, 3-glycidoxypropylmethyldiphenoxysilane, 3-glycidoxypropyldimethylmethoxysilane, 3-glycidoxypropyldiethylethoxysilane, 3-glycidoxypropyldimethylethoxysilane, 3-glycidoxypropyldimethylphenoxysilane, 3-glycidoxypropyldiethylmethoxysilane, 3-glycidoxypropylmethyldiisopropeneoxysilane, bis(3-glycidoxypropyl)-dimethoxysilane, bis(3-glycidoxypropyl)diethoxysilane, bis(3-glycidoxypropyl)dipropoxysilane, bis(3-glycidoxypropyl)dibutoxysilane, bis(3-glycidoxypropyl)diphenoxysilane, bis(3-glycidoxypropyl)methylmethoxysilane, bis(3-glycidoxypropyl)methylethoxysilane, bis(3-glycidoxypropyl)methylpropoxysilane, bis(3-glycidoxypropyl)methylbutoxysilane, bis(3-glycidoxypropyl)methylphenoxysilane, tris(3-glycidoxypropyl)methoxysilane, β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, β-(3,4-epoxycyclohexyl)ethyltriethoxysilane, β-(3,4-epoxycyclohexyl)ethyltripropoxysilane, β-(3,4-epoxycyclohexyl)ethyltributoxysilane, β-(3,4-epoxycyclohexyl)ethyltriphenoxysilane, β-(3,4-epoxycyclohexyl)propyltrimethoxysilane, β-(3,4-epoxycyclohexyl)ethylmethyldimethoxysilane, β-(3,4-epoxycyclohexyl)ethylethyldimethoxysilane, β-(3,4-epoxycyclohexyl)ethylethyldiethoxysilane, β-(3,4-epoxycyclohexyl)ethylmethyldiethoxysilane, β-(3,4-epoxycyclohexyl)ethylmethyldipropoxysilane, β-(3,4-epoxycyclohexyl)ethylmethyldibutoxysilane, β-(3,4-epoxycyclohexyl)ethylmethyldiphenoxysilane, β-(3,4-epoxycyclohexyl)ethyldimethylmethoxysilane, β-(3,4-epoxycyclohexyl)-ethyldiethylethoxysilane, β-(3,4-epoxycyclohexyl)ethyldimethylethoxysilane, β-(3,4-epoxycyclohexyl)ethyldimethylpropoxysilane, β-(3,4-epoxycyclohexyl)ethyldimethylbutoxysilane, β-(3,4-epoxycyclohexyl)-ethyldimethylphenoxysilane, β-(3,4-epoxycyclohexyl)ethyldiethylmethoxysilane, β-(3,4-epoxycyclohexyl)ethylmethyldiisopropeneoxysilane, and the like. Among these silane compounds, 3-glycidoxypropyltrimethoxysilane is preferable. The polymerization solvent used in the method of preparation is not particularly limited. Examples of the polymerization solvent include aromatic hydrocarbon solvents, such as benzene, toluene, xylene, and the like; aliphatic hydrocarbon solvents, such as n-pentane, n-hexane, n-butane, and the like; alicyclic hydrocarbon solvents, such as methylcyclopentane, cyclohexane, and the like; and mixtures of these solvents. Examples of the lithium compound used in the method of preparation as the polymerization initiator include alkyllithiums, such as n-butyllithium, ethyllithium, propyllithium, t-butyllithium, hexyllithium; alkylene dilithiums, such as 1,4-dilithiobutane; phenyllithium; stilbenedilithium; and other organolithium compounds, such as reaction products of butyllithium and divinylbenzene; organometallic lithium compounds, such as tributyltin lithium. The lithium initiator may be used singly or as a mixture of two or more types. When an alkyllithium is used, n-butyllithium and sec-butyllithium are preferably used as the alkyllithium because of better solubility in hydrocarbon solvents and a more suitable initiation rate. The lithium compound can be used in an amount in a range of 0.2 to 30 mmol per 100 g of the monomer. An amount of less than 0.2 mmol or more than 30 mmol is not preferable with respect to the processability of the resultant polymer. The conjugated diene monomer and the vinyl aromatic hydrocarbon monomer used in the polymerization are the same as those described above. In the present polymerization, a randomizer is preferably used in order to obtain a polymer having a desired molecular structure. The randomizer is a compound which controls, for example: the microstructure of a conjugated diene polymer, such as the amount of the 1,2-linkage in polybutadiene or in the butadiene part of a butadiene-styrene copolymer, and the amount of the 3,4-linkage in polyisoprene; and the distribution of monomer units in a conjugated diene-vinyl aromatic hydrocarbon copolymer, such as randomization of the butadiene unit and the styrene unit in a butadiene-styrene copolymer. The randomizer used in the present invention is not particularly limited, and all types of generally used randomizer may be used. Examples of the randomizer include: (1) ethers; (2) ortho-dimethoxybenzenes; (3) complexes of alkali metals and ketones or phosphorous acid triesters; (4) compounds represented by the following formulae: R(OM 1 ) n , (RO) 2 M 2 , R(COOM 1 ) n , ROCOOM 1 , RSO 3 M 1 , ROSO 3 M 1 wherein R is selected from an aliphatic hydrocarbon group, an alicyclic hydrocarbon group, and an aromatic hydrocarbon group, M 1 represents an alkali metal, such as lithium, sodium, potassium, rubidium, or cesium, M 2 represents an alkaline earth metal, such as calcium or barium, and n is an integer of 1 to 3; (5) tertiary amine. The randomizer is described more specifically hereinafter. The randomizer may be used singly or as a combination of two or more types. (1) Examples of the ether include: 1,2-dimethoxyethane, 1,2-diethoxyethane, tetrahydrofuran, 2-methoxymethyltetrahydrofuran, diethyl ether, triethylene glycol dimethyl ether, and the like. (2) Examples of the ortho-dimethoxybenzene include: veratrol, isohomoveratrol, and the like. (3) Examples of the complex of an alkali metal and a ketone or a phosphorous acid triester include: complexes of alkali metals, such as lithium, sodium, potassium, rubidium, cesium, and the like, and ketones, such as acetone, methyl ethyl ketone, diisopropyl ketone, benzophenone, acetophenone, dibenzyl ketone, fluorenone, xanthone, Michler's ketones, acetylacetone, and the like, or phosphorous acid triesters, such as triethyl phosphite, trioctyl phosphite, tribenzyl phosphite, trinonyl phosphite, and the like. (4) The randomizers represented by the general formulae are as follows. Examples of the alkali metal salt or the alkaline earth metal salt of an alcohol or a phenol represented by the general formula R(OM 1 ) n or (RO) 2 M 2 include: salts of lithium, sodium, potassium, rubidium, cesium, calcium, or barium, and methyl alcohol, ethyl alcohol, isopropyl alcohol, tert-butyl alcohol, tert-amyl alcohol, cyclohexyl alcohol, allyl alcohol, 2-butenyl alcohol, benzyl alcohol, phenol, catechol, resorcinol, hydroquinone, 1-naphthyl alcohol, p-nonylphenol, pyrrogalol, or the like. Examples of the alkali metal salt of a carboxylic acid or a hydrogen carbonic acid ester represented by the general formula (COOM 1 ) n or ROCOOM 1 include: salts of lithium, sodium, potassium, rubidium, or cesium, and isovaleric acid, lauric acid, palmitic acid, stearic acid, oleic acid, rosic acid, benzoic acid, pimelic acid, dodecyl hydrogen carbonate, phenyl hydrogen carbonate, or the like.Examples of the sulfonic acid salt or sulfuric acid salt of an alkali metal represented by the general formula RSO 3 M 1 or ROSO 3 M 1 include: salts of lithium, sodium, potassium, rubidium, or cesium, and dodecylbenzenesulfonic acid, diisopropylnaphthalenesulfonic acid, N-methyl-N-methanesulfonic acid salt laurylamide, sulfuric acid ester salts of lauryl alcohol, caproyl ethylene glycol sulfuric acid esters, and the like. (5) Examples of the tertiary amine include: triethylamine, tetramethylethylenediamine, and the like. Among these randomizers, (1) ethers, and (4) R(OM 1 ) n are preferable because the molecular structure of the diene-type polymers of the present invention can be controlled more easily by these randomizers. The randomizer is used in an amount of 0.01 to 1000 mol equivalent per 1 mol equivalent of the organolithium compound. The temperature of the polymerization is generally -20 to 150°C, preferably 0 to 100°C. The concentration of the monomer in the solution is generally 5 to 50 % by weight, preferably 10 to 35 % by weight. When a conjugated diene and a vinyl aromatic hydrocarbon are copolymerized, the content of the vinyl aromatic hydrocarbon in the initial monomer mixture is 5 to 70 % by weight, preferably 10 to 50 % by weight. The polymerization is conducted by bringing the monomers into contact with the initiator in the liquid phase. The polymerization is preferably carried out at a pressure essentially sufficient for keeping the polymerization system at the liquid phase. It is preferred that any substances having an adverse effect on the catalytic function are excluded from all of the materials used in the reaction system. The reaction by addition of an alkoxysilane compound having an epoxy group is conducted after the polymerization in an atmosphere in which the lithium active end of the polymer or the copolymer is not deactivated. After finishing the reaction, the functionalized polymer can be obtained by removing the solvent by blowing steam into the solution of the functionalized polymer, or by coagulating the functionalized polymer by addition of a poor solvent such as methanol, followed by drying with heated rolls or under a vacuum. The functionalized polymer can be obtained by removing the solvent directly from the solution of the functionalized polymer using heated rolls or under a vacuum, as well. In the rubber material comprised in the elastomeric composition of the present invention, the functionalized polymer described above is used by blending with natural rubber or other synthetic rubbers for practical purposes. When the functionalized polymer is used as a blend, it is necessary that the rubber material contains 10 parts by weight or more, preferably 40 parts by weight or more, of the functionalized polymer described above in 100 parts by weight of the rubber material. For example, when the content of the functionalized polymer of the present invention in a blend with natural rubber is less than 10 parts by weight, the balance in the properties required for the elastomeric composition of the present invention deteriorate, and accordingly, such a content is not preferable. Examples of the synthetic rubber used for blending with the functionalized polymer include cis-1,4-polyisoprene, styrene-butadiene copolymer, low cis-1,4-polybutadiene, high cis-1,4-polybutadiene, ethylene-propylene-diene terpolymer, chloroprene rubber, halogenated butyl rubber, acrylonitrile-butadiene rubber (NBR), and the like. Among these rubbers, natural rubber, high cis-1,4-polybutadiene, and halogenated butyl rubber are preferable from the standpoints of tensile strength, abrasion resistance, and processability. Fillers are comprised in the elastomeric composition of the present invention. White carbon is the essential component of the filler. Examples of the white carbon used in the elastomeric composition of the present invention include wet silica (hydrated silicic acid), dry silica (anhydrous silicic acid), calcium silicate, aluminum silicate, clay, talc, calcium carbonate, basic magnesium carbonate, hydrated alumina, diatomaceous earth, barium sulfate, mica, aluminum sulfate, titanium oxide, and the like. Among these white carbons, wet silica is preferable because the fracture properties are improved, and wet grip and low rolling resistance are simultaneously exhibited most remarkably. The content of the filler in the elastomeric composition is 10 to 100 parts by weight, preferably 20 to 60 parts by weight, based on 100 parts by weight of the rubber material. When the content is less than 10 parts by weight, the fracture properties are insufficient. When the content is more than 100 parts by weight, processability is inferior. The filler of the present invention may contain the white carbon alone. In this case, the content of the white carbon in the elastomeric composition is 10 to 100 parts by weight, preferably 20 to 60 parts by weight, based on 100 parts by weight of the rubber material. When the content is less than 10 parts by weight, the fracture properties are insufficient. When the content is more than 100 parts by weight, processability is inferior. The filler of the present invention may contain the white carbon and carbon black in combination. The effect of the filler on the improvement of the physical properties is remarkably enhanced by this combination. As the carbon black, FEF, SRF, HAF, ISAF, SAF, and the like, are used. Carbon blacks having an iodine adsorption number (IA) of 60 mg or more per g, and a dibutyl phthalate absorption number (DBP) of 80 ml or more per 100 g, are preferably used. HAF, ISAF and SAF having superior abrasion resistance are particularly preferable. The amount of the carbon black used is not particularly limited as long as it is within such a range that the effect of the white carbon is not adversely affected. From the standpoints of the reinforcing property and processability, it is preferred that 0.1 to 90 parts by weight of the carbon black and 9.9 to 99.9 parts by weight of the white carbon, each based on 100 parts by weight of the rubber material, are used as long as the content of the filler is within the range described above. In the elastomeric composition of the present invention, a silane coupling agent may be used in the preparation of the elastomeric composition for the purpose of further enhancing the reinforcement with the white carbon. Examples of the silane coupling agent include: bis(3-triethoxysilylpropyl) tetrasulfide, bis(2-triethoxysilylethyl) tetrasulfide, bis(3-trimethoxysilylpropyl) tetrasulfide, bis(2-trimethoxysilylethyl) tetrasulfide, 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 2-mercaptoethyltrimethoxysilane, 2-mercaptoethyltriethoxysilane, 3-nitropropyltrimethoxysilane, 3-nitropropyltriethoxysilane, 3-chloropropyltrimethoxysilane, 3-chloropropyltriethoxysilane, 2-chloroethyltrimethoxysilane, 2-chloroethyltriethoxysilane, 3-trimethoxysilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, 3-triethoxylsilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, 2-triethoxysilylethyl-N,N-dimethylthiocarbamoyl tetrasulfide, 3-trimethoxysilylpropylbenzothiazol tetrasulfide, 3-triethoxysilylpropylbenzothiazol tetrasulfide, 3-triethoxysilylpropyl methacrylate monosulfide, 3-trimethoxysilylpropyl methacrylate monosulfide, and the like. Among these compounds, bis(3-triethoxysilylpropyl) tetrasulfide, 3-trimethoxysilylpropylbenzothiazol tetrasulfide, and the like, are preferable from the standpoint of improving the reinforcing property. Other examples of the silane coupling agent include: bis(3-diethoxymethylsilylpropyl) tetrasulfide, 3-mercaptopropyldimethoxymethylsilane, 3-nitropropyldimethoxymethylsilane, 3-chloropropyldimethoxymethylsilane, dimethoxymethylsilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, dimethoxymethylsilylpropylbenzothiazol tetrasulfide, and the like. When a silane coupling agent is used in the preparation of the elastomeric composition, the amount of the silane coupling agent can be made lower than that in conventional rubber compositions while the properties remain the same as those of the conventional rubber compositions. The amount of the silane coupling agent is varied depending on the amount of the white carbon used, and, from the standpoint of the reinforcing property, the amount is generally 0.1 to 10 parts by weight, preferably 0.1 to 5 parts by weight, based on 100 parts by weight of the rubber material. Examples of the vulcanizing agent include sulfur and the like. The amount of the vulcanizing agent used is 0.1 to 5 parts by weight, preferably 1 to 2 parts by weight, based on 100 parts by weight of the rubber material. When the amount is less than 0.1 parts by weight, the fracture properties, abrasion resistance, and low hysteresis loss of the vulcanized rubber are inferior. When the amount is more than 5 parts by weight, the rubber elasticity is lost. Examples of the process oil which can be used in the elastomeric composition of the present invention include paraffinic process oils, naphthenic process oils, and aromatic process oils. For applications in which tensile strength and abrasion resistance are important, aromatic process oils are used. For applications in which hysteresis loss and low temperature properties are important, naphthenic process oils and paraffinic process oils are used. The amount of the process oil used is 0 to 100 parts by weight based on 100 parts by weight of the rubber material. When the amount is more than 100 parts by weight, tensile strength and low hysteresis loss of the vulcanized rubber deteriorate significantly. Vulcanization accelerators used in the present invention are not particularly limited. Examples of the vulcanization accelerator include thiazol vulcanization accelerators, such as M (2-mercaptobenzothiazol), DM (dibenzothiazyl disulfide), CZ (N-cyclohexyl-2-benzothiazyl-sulfenamide) and the like; and guanidine vulcanization accelerators, such as DPG (diphenylguanidine) and the like. The amount of the vulcanization accelerator used is 0.1 to 5 parts by weight, preferably 0.2 to 3 parts by weight, based on 100 parts by weight of the rubber material. In the elastomeric composition of the present invention, additives, such as antioxidants, zinc oxide, stearic acid, antiozonants, and the like which are conventionally used in the rubber industry may be comprised. The elastomeric composition of the present invention can be obtained by milling the components by using a milling apparatus, such as a mill, an internal mixer, and the like. After being molded and vulcanized, the elastomeric composition may be applied to tires, such as tire treads, undertreads, carcasses, side walls, beads, and the like, as well as to other industrial rubbers, such as antivibration rubbers, belts, hoses, and the like. The elastomeric composition is particularly preferably used as a rubber for tire treads. To summarize the advantages of the present invention, the functionalized polymer and the elastomeric composition of the present invention exhibit excellent fracture properties, abrasion resistance, and low hysteresis loss (low rolling resistance and low fuel consumption) because the functionalized polymer and the elastomeric composition have the structure and the composition described above. EXAMPLES The invention will be understood more readily with reference to the following examples; however, these examples are intended to illustrate the invention and are not to be construed as limiting the scope of the invention. In the examples, part and % mean part by weight and % by weight, respectively, unless otherwise mentioned. Measurements were conducted in accordance with the following methods: The number-average molecular weight (M n ) and the weight-average molecular weight (M w ) of the copolymer were measured by gel permeation chromatography (GPC) (an instrument: HLC-8020, a product of Toso Co., Ltd.; columns: GMH-XL, two columns in the series arrangement, a product of Toso Co., Ltd.) using differential refractive index (RI) and were calibrated to polystyrene using monodisperse polystyrene samples as the references. The microstructure of the polybutadiene part of the polymer was obtained by Morero's method. The content of the bound styrene in a butadiene-styrene copolymer was obtained from the integration ratio in the 1 H-NMR spectrum. The Mooney viscosity of the elastomeric composition was measured in accordance with the method of Japanese Industrial Standard K6300 at 130°C. As the index for hysteresis loss and rolling resistance of a vulcanizate of the elastomeric composition, tan δ (50°C) was used. An elastomeric composition having a smaller tan δ was evaluated as having a lower hysteresis loss and a lower rolling resistance. Measurement of tan δ (50°C) was conducted by using a viscoelasticity measurement apparatus (a product of Rheometrix Company) at a temperature of 50°C, a strain of 8 %, and a frequency of 15 Hz. Measurement of tan δ (0°C) as the index for the wet grip was conducted by using the same apparatus at a temperature of 0°C, a strain of 1 %, and a frequency of 15 Hz. Fracture properties and 300 % modulus (M 300 ) were measured in accordance with the method of Japanese Industrial Standard K6301. Abrasion resistance was measured by using a Lambourn abrasion tester at room temperature with a slip rate of 60 %. The abrasion resistance of the elastomeric composition was compared with that of the reference composition which contained the same components except that 50 parts by weight of HAF carbon was used as the filler in the reference composition, and was expressed as an index based on the value of the reference composition set to 100. Example 1 Into a 800 ml pressure-resistant glass vessel dried and purged with nitrogen, 315 g of cyclohexane, 48 g of 1,3-butadiene monomer, 12 g of styrene monomer, and 27.5 mmol of tetrahydrofuran (THF) were added in accordance with the formulation shown in Table 1. To this mixture, 0.5 mmol of n-butyllithium (BuLi) was added and the polymerization was conducted at 50°C for 2 hours. Conversion by the polymerization was about 100 %. A portion of the copolymer was removed as a sample, and isopropyl alcohol was added thereto. The solid product was dried to obtain a rubbery copolymer. The microstructure and molecular weight of the copolymer thus obtained were measured. Results are shown in Table 3. Then, the molecular weight distribution was measured by using GPC and it was confirmed that the GPC curve had a single sharp peak at M w = 2 × 10 5 and that the molecular distribution was M w /M n = 1.06. To the polymer solution obtained above, 3-glycidoxypropyltrimethoxysilane (GPMOS) was added as the alkoxysilane compound having an epoxy group, and the modification was conducted at 60°C for 30 minutes. Isopropyl alcohol was added to this solution and the solid product formed was dried to obtain a rubbery functionalized polymer G-11. The molecular weight distribution of the functionalized polymer obtained here was measured by GPC. It was confirmed that the GPC curve had two peaks including the peak of the base polymer described above and a peak which is considered to have been obtained by the coupling of two or more polymers, and that the total weight-average molecular weight had jumped to 38 × 10 4 . It was confirmed from the results described above and other related data that the functionalized polymer obtained here was a mixture of compounds which were the same as C-1, C-2, and C-3 obtained in Preparation Example C described above except that the hexamethyleneimino groups in C-1, C-2, and C-3 were each replaced by a butyl group. The functionalized polymer obtained here was the polymer represented by formula (3). The functionalized polymer G-11 was milled with other components in accordance with the formulation shown in Table 2, and the composition was vulcanized at 145°C for 33 minutes. Physical properties of the vulcanizate thus obtained were evaluated. Results are shown in Table 3. Example 2 A rubbery functionalized polymer G-12 was obtained by the same method as that used in Example 5 except that the amounts of 1,3-butadiene monomer and styrene monomer were changed, and potassium t-amylate was used in place of THF. This functionalized polymer had the same molecular structure as that of G-11 except that the content of the bound styrene in the copolymer and the vinyl content of the butadiene part were different. Properties of the copolymer and results of the evaluation of the physical properties of the vulcanizate are shown in Table 3. Example 3 A rubbery functionalized polymer G-13 was obtained by the same method as that used in Example 1 except that the amounts of 1,3-butadiene monomer and styrene monomer were changed, potassium t-amylate was used in place of THF, and β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (EHMOS) was used as the alkoxysilane compound having an epoxy group in place of GPMOS. It was confirmed that the functionalized polymer obtained here was a mixture of compounds which were the same as D-1, D-2, and D-3 obtained in Preparation Example D described above except that the hexamethyleneimino groups in D-1, D-2, and D-3 were each replaced by a butyl group [the functionalized polymers represented by formula (3)]. Properties of the copolymer and results of the evaluation of the physical properties of the vulcanizate are shown in Table 3. Comparative Example 1 A rubbery polymer G-14 was obtained by the same method as that used in Example 1 except that the alkoxysilane compound having an epoxy group GPMOS was not used. This polymer was a conventional butadiene-styrene random copolymer. Properties of the copolymer and results of the evaluation of the physical properties of the vulcanizate are shown in Table 3. Comparative Example 2 A rubbery polymer G-15 was obtained by the same method as that used in Example 1 except that methyltriphenoxysilane having no epoxy group was used in place of the alkoxysilane compound having an epoxy group GPMOS. As can be easily understood from Preparation Example C described above, the phenoxysilane group alone was bonded to this copolymer, but neither a functional group containing a hydroxyl group nor a functional group containing nitrogen was bonded to this copolymer. Properties of the copolymer and results of the evaluation of the physical properties of the vulcanizate are shown in Table 3. monomer randomizer silane compound functionalized butadiene (g) styrene (g) type amount amount (mmol) type amount (mmol) polymer No. Example 1 48 12 THF 27.5 GPMOS 0.5 G-11 Example 2 36 24 KOR 0.025 GPMOS 0.5 G-12 Example 3 36 24 KOR 0.025 EHMOS 0.5 G-13 Comparative Example 1 48 12 THF 27.5 - - G-14 Comparative Example 2 48 12 THF 27.5 MTPOS 0.25 G-15 KOR: potassium t-amylate GPMOS: 3-glycidoxypropyltrimethoxysilane EHMOS: β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane MTPOS: methyltriphenoxysilane rubber material 100 parts by weight functionalized polymer of the present invention 75 parts by weight natural rubber 25 parts by weight silica 50 parts by weight spindle oil 5 parts by weight stearic acid 2 parts by weight Acting SL 1 parts by weight antioxidant 6C 1 parts by weight zinc oxide 3 parts by weight accelerator DPG 0.6 parts by weight accelerator DM 1.2 parts by weight sulfur 1.5 parts by weight functionalized polymer No. microstructure molecular compound styrene (%) vinyl (%) weight M w × 10 -4 ML 1+4 130°C Example 1 G-11 20 58 38 67 Example 2 G-12 40 12 38 77 Example 3 G-13 40 12 37 75 Comparative Example 1 G-14 20 58 20 73 Comparative Example 2 G-15 20 60 34 79 physical properties tensile strength (kg/cm 2 ) M 300 (kg/cm 2 ) elongation (%) Lambourn abrasion index tan δ at 50°C Example 1 240 80 620 90 0.100 Example 2 253 74 590 98 0.106 Example 3 255 70 580 97 0.105 Comparative Example 1 130 37 680 50 0.170 Comparative Example 2 210 66 640 68 0.115 It can be clearly understood from Table 3 that the elastomeric composition comprising the functionalized polymer represented by the formula (3) has excellent fracture properties, abrasion resistance, and low hysteresis loss (tan δ at 50°C) without any increase in the Mooney viscosity of the composition (compound ML 1+4 ). The effects of the elastomeric composition comprising the functionalized polymer represented by formula (3) described above can be more clearly seen by comparing the examples and the comparative examples. The differences are apparent from: the effect of the presence/absence of the functional group containing hydroxyl group in the functionalized polymer (present in Examples 1 to 3 as compared with absent in Comparative Example 2); the combined effect of the presence/absence of the functional group containing hydroxyl group and the alkoxysilane group in the functionalized polymer (present in Examples 1 to 3 as compared with absent in Comparative Example 1; and the effect exhibited by the functional group containing hydroxyl group without any particular restriction of the type thereof when it is used within the range of the present invention (Examples 1 and 3 compared with the comparative examples).

Claims: Process for preparing a functionalized polymer of the formula wherein A represents a group derived from the organic lithium initiator used in step (a) defined below, P is a conjugated diene (co)polymer composed of at least one conjugated diene having 4-12 carbon atoms, optionally together with a vinyl aromatic hydrocarbon, R 1 and R 2 , which may be the same or different, represent an aliphatic, alicyclic and aromatic hydrocarbon group having 20 or less carbon atoms; R 3 is selected from aliphatic and alicyclic hydrocarbon groups having 20 or less carbon atoms; R 4 is an oxygen atom or an optionally substituted methylene group; R 5 is an aliphatic hydrocarbon group having 20 or less carbon atoms; n is 0 or 1; and x is an integer of 1-3; and z is an integer of 0-2; with 1 ≤ x + z ≤ 3; characterized by the steps of: (a) (co)polymerizing at least one conjugated diene hydrocarbon monomer and optionally a vinyl aromatic hydrocarbon with an organic lithium initiator without a nitrogen atom, obtaining a conjugated diene/vinyl aromatic hydrocarbon (co)polymer having a lithium active end; and (b) adding to the copolymer obtained in step (a) at least one silane compound selected from γ-(3,4-epoxycyclohexyl)ethyl trimethoxysilane, 3-glycidoxyethyl trimethoxysilane, 3-glycidoxypropyl trimethoxysilane, 3-glycidoxybutyl trimethoxysilane, 3-glycidoxypropyl triethoxysilane, 3-glycidoxypropyl tripropoxysilane, 3-glycidoxypropyl tributoxysilane, 3-glycidoxypropyl triphenoxysilane, 3-glycidoxypropyl methyl dimethoxysilane, 3-glycidoxypropyl ethyl dimethoxysilane, 3-glycidoxypropyl ethyl diethoxysilane, 3-glycidoxypropyl methyl diethoxysilane, 3-glycidoxypropyl methyl dipropoxysilane, 3-glycidoxypropyl methyl dibutoxysilane, 3-glycidoxypropyl methyl diphenoxysilane, 3-glycidoxypropyl dimethyl methoxysilane, 3-glycidoxypropyl diethyl ethoxysilane, 3-glycidoxypropyl dimethyl ethoxysilane, 3-glycidoxypropyl dimethyl phenoxysilane, 3-glycidoxypropyl diethyl methoxysilane, 3-glycidoxypropyl methyl diisopropeneoxysilane, bis(3-glycidoxypropyl) dimethoxysilane, bis(3-glycidoxypropyl) diethoxysilane, bis(3-glycidoxypropyl) dipropoxysilane, bis(3-glycidoxypropyl) dibutoxysilane, bis(3-glycidoxypropyl) diphenoxysilane, bis(3-glycidoxypropyl) methyl methoxysilane, bis(3-glycidoxypropyl) methyl ethoxysilane, bis(3-glycidoxypropyl) methyl propoxysilane, bis(3-glycidoxypropyl) methyl butoxysilane, bis(3-glycidoxypropyl) methyl phenoxysilane, tris(3-glycidoxypropyl) methoxysilane, β-(3,4-epoxycyclohexyl)ethyl trimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl triethoxysilane, β-(3,4-epoxycyclohexyl)ethyl tripropoxysilane, β-(3,4-epoxycyclohexyl)ethyl tributoxysilane, β-(3,4-epoxycyclohexyl)ethyl triphenoxysilane, β-(3,4-epoxycyclohexyl)propyl trimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl dimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl ethyl dimethoxysilane, β-(3,4-epoxycyclohexyl)ethyl ethyl diethoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl diethoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl dipropoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl dibutoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl diphenoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl methoxysilane, β-(3,4-epoxycyclohexyl)ethyl diethyl ethoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl ethoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl propoxysiiane, β-(3,4-epoxycyclohexyl)ethyl dimethyl butoxysilane, β-(3,4-epoxycyclohexyl)ethyl dimethyl phenoxysilane, β-(3,4-epoxycyclohexyl)ethyl diethyl methoxysilane, β-(3,4-epoxycyclohexyl)ethyl methyl diisopropeneoxysilane, and a silane compound of the formula, : wherein R 1 , R 4 and R 5 are as defined above, and E is a an epoxy group-containing moiety, which upon reaction with the conjugated diene/vinyl aromatic hydrocarbon (co)polymer having a lithium active end obtained in step (a) forms a group wherein R 3 is an aliphatic or alicyclic hydrocarbon group having 20 or less carbon atoms, and n is 0 or 1. Process according to claim 1, wherein the diene monomer(s) to be (co)polymerized in step (a) is at least one conjugated diene C 4-12 -hydrocarbon monomer. Process according to any of the preceding claims, wherein the polymer is a butadiene/styrene random copolymer or intermediate random copolymer. Process according to any of the preceding claims, wherein the organic lithium initiator is at least one selected from alkyl lithium compounds, alkylene dilithium compounds, phenyl lithium, stilbene dilithium, reaction products of butyl lithium and divinylbenzene, and organometallic lithium compounds. Functionalized polymer of the formula wherein A, P, R 1 , R 2 , R 3 , R 4 , R 5 , n, x and z are defined as in claim 1, obtainable by the process of any of the claims 1-4.

Inventors: SHIMIZU TAKASHI, SHIMIZU, TAKASHI
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1994
Main classification: C08C19
IPC codes: C08C19, C08L19, C08F36