Sulfur tolerant reforming catalyst system containing a sulfur-sensitive ingredient

Abstract: A sulfur-sensitive reforming catalyst is rendered substantially less sulfur-sensitive by use in a catalyst system comprising a physical mixture of such catalyst and a sulfur sorbent selected to accommodate small quantities of sulfur from a hydrocarbon feedstock. Preferably, the physical mixture comprises a sulfur-sensitive reforming catalyst protected from sulfur deactivation by a manganese-oxide sorbent. The invention shows substantial benefits over prior-art processes in catalyst utilization in a catalytic reforming process using a potassium-form L-Zeolite component to promote aromatic formation.

Description: BACKGROUND OF THE INVENTION The catalytic reforming of hydrocarbon feedstocks in the gasoline range is an important commercial process, practiced in nearly every significant petroleum refinery in the world to produce aromatic intermediates for the petro- chemical industry or gasoline components with high resistance to engine knock. Demand for aromatics is growing more rapidly than the supply of feedstocks for aromatics production. Moreover, the widespread removal of lead antiknock additive from gasoline and the rising demands of high-performance internal-combustion engines are increasing the required knock resistance of the gasoline component as measured by gasoline "octane" number. The catalytic reforming unit therefore must operate more efficiently at higher severity in order to meet these increasing aromatics and gasoline-octane needs. This trend creates a need for more effective reforming processes and catalysts. Catalytic reforming generally is applied to a feedstock rich in paraffinic and naphthenic hydrocarbons and is effected through diverse reactions: dehydrogenation of naphthenes to aromatics, dehydrocyclization of paraffins, isomerization of paraffins and naphthenes, dealkylation of alkylaromatics, hydrocracking of paraffins to light hydrocarbons, and formation of coke which is deposited on the catalyst. Increased aromatics and gasoline-octane needs have turned attention to the paraffin-dehydrocyclization reaction, which is less favored thermodynamically and kinetically in conventional reforming than other aromatization reactions. Considerable leverage exists for increasing desired product yields from catalytic reforming by promoting the dehydrocyclization reaction over the competing hydrocracking reaction while minimizing the formation of coke. The effectiveness of reforming catalysts comprising a non-acidic L-zeolite and a platinum-group metal for dehydrocyclization of paraffins is well known in the art. The use of these reforming catalysts to produce aromatics from paraffinic raffinates as well as naphthas has been disclosed. The increased sensitivity of these selective catalysts to sulfur in the feed also is known. It is believed that the extreme, unanticipated sulfur sensitivity of these reforming catalysts is primarily responsible for the lengthy development period and slow commercialization of this dehydrocyclization technology. Unit operations and processing costs would benefit from novel methods for sulfur management such as are provided by the catalyst system of the present invention. The desulfurization of naphtha feedstocks to a reforming process using sulfur sorbents is widely disclosed. US-A-4 225 417 and US-A-4 329 220 teach a reforming process in which sulfur is removed from a reforming feedstock using a manganese-containing composition. Preferably, the feed is hydrotreated and the sulfur content is reduced by the invention to below 0.1 ppm. US-A-4 534 943 and US-A-4 575 415 teach an apparatus and method, respectively, for removing residual sulfur from reformer feed using parallel absorbers for continuous operation; ideally, sulfur is removed to a level of below 0.1 ppm. US-A-4 456 527 discloses the reforming of a hydrocarbon feed having a sulfur content of as low as 50 ppb (parts per billion) with a catalyst comprising a large-pore zeolite and Group VIII metal. A broad range of sulfur-removal options is disclosed to reduce the sulfur content of the hydrocarbon feed to below 500 ppb. US-A-4 741 819 is drawn to a method for removing residual sulfur from a hydrotreated naphtha feedstock comprising contacting the feedstock with a less-sulfur sensitive reforming catalyst, a sulfur sorbent, and a highly selective reforming catalyst. US-A-5 059 304 shows a physical mixture of a conventional platinum on alumina catalyst and a Group IA or IIA metal-containing sulfur sorbent for purposes of desulfurization of a naphtha feed for a subsequent reforming unit. A platinum/L-zeolite catalyst having improved sulfur tolerance through the incorporation of rhenium is revealed in US-A-4 954 245. None of the above references, moreover, anticipate or suggest a catalyst system comprising a physical mixture of a sulfur-sensitive reforming catalyst and a sulfur sorbent. EP-A-0421584 discloses that performance of a process, for catalytic conversion of a substantially contaminant-free hydrocarbon feed with a contaminant-sensitive catalyst using a conversion system having equipment contaminated through contact with a contaminant-containing prior feed, is substantially improved by using a sacrificial particulate bed to remove contaminants such as sulfur from the contaminated conversion system prior to loading the contaminant-sensitive catalyst. After contaminant removal is substantially complete, the sacrificial particulate bed is replaced with the contaminant-sensitive catalyst and the contaminant-free feed is charged to the conversion system at hydrocarbon conversion conditions. According to one embodiment, the conversion system is a catalytic reforming system, the contaminant removal conditions are reforming conditions, and the sacrificial particulate bed comprises a first reforming catalyst. According to another embodiment, the contaminant is sulfur, and the sacrificial bed comprises a sulfur-sorbent, preferably manganese oxide. It is an object of the present invention to provide a catalyst system for a catalytic reforming process effective for the dehydrocyclization of paraffins in the presence of small amounts of sulfur with high catalyst stability. A corollary objective is to avoid sulfur deactivation of a reforming catalyst having unusual sulfur intolerance. This invention is based on the discovery that a catalytic reforming process system utilizing a catalyst system comprising a physical mixture of a sulfur-sensitive conversion catalyst and a sulfur sorbent is surprisingly effective in arresting sulfur in order to avoid deactivation of the sulfur-sensitive catalyst. A broad embodiment of the present invention is a sulfur tolerant catalyst system comprising a physical mixture of a sulfur-sensitive reforming catalyst containing a platinum-group metal and a sulfur sorbent containing a metal oxide selective for sulfur adsorption. An embodiment of this catalyst system is a physical mixture of a platinum-containing reforming catalyst and a manganese oxide sulfur sorbent. A preferred embodiment of such reforming catalyst system contains potassium-form L-zeolite. Yet another embodiment is a catalytic reforming process utilizing at least in the initial conversion zone a catalyst system containing a physical mixture of a sulfur-sensitive reforming catalyst. DETAILED DESCRIPTION OF THE INVENTION To reiterate, a broad embodiment of the present invention is directed to a catalyst system comprising a physical mixture of a sulfur-sensitive conversion or reforming catalyst containing a platinum-group metal and a sulfur sorbent containing manganese oxide. This catalyst system has been found to be surprisingly effective, in comparison to the prior art in which the conversion catalyst and sulfur sorbent are utilized in sequence, in arresting sulfur from contacting a sulfur-sensitive reforming catalyst. The mutual co-action of the catalyst and sorbent provides excellent results in achieving favorable yields with high catalyst utilization in a dehydrocyclization operation using a sulfur-sensitive catalyst. First particles of conversion catalyst and second particles of sulfur sorbent are prepared as described hereinbelow. Preferably the first particles are essentially free of sulfur sorbent and the second particles are essentially free of conversion catalyst, and the first and second particles are mechanically mixed to provide the catalyst system of the invention. The particles can be thoroughly mixed using known techniques such as mulling to intimately blend the physical mixture. The mass ratio of conversion catalyst to sulfur sorbent depends primarily on the sulfur content of the feed, and may range from about 1:10 to 10:1. Preferably, a 100 cc sample of a contemporaneously mixed batch will not differ in the percentage of each component of the mixture relative to the batch by more than 10%. Although the first and second particles may be of similar size and shape, the particles preferably are of different size and/or density for ease of separation for purposes of regeneration or rejuvenation following their use in hydrocarbon processing. The conversion or reforming catalyst comprises a composite of a metallic hydrogenation-dehydrogenation component on a refractory support. This catalyst is effective to convert small amounts of sulfur in a hydrocarbon feedstock to a reforming process to H 2 S, which then can readily be arrested by sorption from deactivating a sulfur-sensitive catalyst. The conversion catalyst will tolerate episodes of up to about 10 ppm of sulfur in the feedstock with substantial recovery of activity. The conversion catalyst also preferably effects some dehydrogenation of naphthenes in the feedstock and may contain acid sites which effect isomerization, cracking and dehydrocyclization. The refractory support of the conversion catalyst should be a porous, adsorptive, high-surface-area material which is uniform in composition without composition gradients of the species inherent to its composition. Within the scope of the present invention are refractory supports containing one or more of: (1) refractory inorganic oxides such as alumina, silica, titania, magnesia, zirconia, chromia, thoria, boria or mixtures thereof; (2) synthetically prepared or naturally occurring clays and silicates, which may be acid-treated; (3) crystalline zeolitic aluminosilicates, either naturally occurring or synthetically prepared such as FAU, MEL, MFI, MOR, MTW (IUPAC Commission on Zeolite Nomenclature), in hydrogen form or in a form which has been exchanged with metal cations; (4) spinels such as MgAl 2 O 4 , FeAl 2 O 4 , ZnAl 2 O 4 , CaAl 2 O 4 ; and (5) combinations of materials from one or more of these groups. The preferred refractory support for the conversion catalyst is alumina, with gamma- or eta-alumina being particularly preferred. Best results are obtained with "Ziegler alumina," described in US-A-2 892 858 and presently available from the Vista Chemical Company under the trademark "Catapal" or from Condea Chemie GmbH under the trademark "Pural." Ziegler alumina is an extremely high-purity pseudoboehmite which, after calcination at a high temperature, has been shown to yield a high-priority gamma-alumina. It is especially preferred that the refractory inorganic oxide comprise substantially pure Ziegler alumina having an apparent bulk density of 0.6 to 1 g/cc and a surface area of 150 to 280 m 2 /g (especially 185 to 235 m 2 /g) at a pore volume of 0.3 to 0.8 cc/g. The alumina powder may be formed into any shape or form of carrier material known to those skilled in the art such as spheres, extrudates, rods, pills, pellets, tablets or granules. Spherical particles may be formed by converting the alumina powder into alumina sol by reaction with suitable peptizing acid and water and dropping a mixture of the resulting sol and gelling agent into an oil bath to form spherical particles of an alumina gel, as described in US-A-2 620 314, followed by known aging, drying and calcination steps. The preferred extrudate form is optimally prepared by mixing the alumina powder with water and suitable peptizing agents, such as nitric acid, acetic acid, aluminum nitrate and like materials, to form an extrudable dough having a loss on ignition (LOI) at 500 o C of 45 to 65 mass %. The resulting dough is extruded through a suitably shaped and sized die to form extrudate particles, which are dried and calcined by known methods. Alternatively, spherical particles can be formed from the extrudates by rolling the extrudate particles on a spinning disk. An essential component of the sulfur-sensitive conversion catalyst is one or more platinum-group metals, with a platinum component being preferred. The platinum may exist within the catalyst as a compound such as the oxide, sulfide, halide, or oxyhalide, in chemical combination with one or more other ingredients of the catalytic composite, or as an elemental metal. Best results are obtained when substantially all of the platinum exists in the catalytic composite in a reduced state. The platinum component generally comprises from about 0.01 to 2 mass % of the catalytic composite, preferably 0.05 to 1 mass %, calculated on an elemental basis. It is within the scope of the present invention that the catalyst may contain metal modifiers known to modify the effect of the preferred platinum component. Such metal modifiers may include metals of Group IVA (14) of the Periodic Table [See Cotton and Wilkinson, Advanced Organic Chemistry , John Wiley & Sons (Fifth Edition, 1988)], other Group VIII (8-10) metals, rhenium, indium, gallium, zinc, uranium, dysprosium, thallium and mixtures thereof. Catalytically effective amounts of such metal modifiers may be incorporated into the catalyst by any means known in the art. The conversion catalyst may in some cases contain a halogen component. The halogen component may be either fluorine, chlorine, bromine or iodine or mixtures thereof. Chlorine is the preferred halogen component. The halogen component is generally present in a combined state with the inorganic-oxide support. The halogen component is preferably well dispersed throughout the catalyst and may comprise from more than 0.2 to 15 wt.%. calculated on an elemental basis, of the final catalyst. A preferred ingredient of the conversion catalyst is a nonacidic large pore molecular sieve. Suitable molecular sieves generally have a uniform pore opening or "pore size" of about 7 Å or larger and include those characterized as AFI, FAU or LTL structure type by the IUPAC Commission on Zeolite Nomenclature. The LTL structure is preferred, and the sulfur-sensitive catalyst optimally is a reforming catalyst comprising L-zeolite, an alkali-metal component and a platinum-group metal component. It is essential that the L-zeolite be non-acidic, as acidity in the zeolite lowers the selectivity to aromatics of the finished catalyst. In order to be "non-acidic," the zeolite has substantially all of its cationic exchange sites occupied by nonhydrogen species. Preferably the cations occupying the exchangeable cation sites will comprise one or more of the alkali metals, although other cationic species may be present. An especially preferred nonacidic L-zeolite is potassium-form L-zeolite. It is necessary to composite the L-zeolite with a binder in order to provide a convenient form for use in the catalyst of the present invention. The art teaches that any refractory inorganic oxide binder is suitable. One or more of silica, alumina or magnesia are preferred binder materials of the present invention. Amorphous silica is especially preferred, and excellent results are obtained when using a synthetic white silica powder precipitated as ultra-fine spherical particles from a water solution. The silica binder preferably is nonacidic, contains less than 0.3 mass % sulfate salts, and has a BET surface area of from about 120 to 160 m 2 /g. The L-zeolite and binder may be composited to form the desired catalyst shape by any method known in the art. For example, potassium-form L-zeolite and amorphous silica may be commingled as a uniform powder blend prior to introduction of a peptizing agent. An aqueous solution comprising sodium hydroxide is added to form an extrudable dough. The dough preferably will have a moisture content of from 30 to 50 mass % in order to form extrudates having acceptable integrity to withstand direct calcination. The resulting dough is extruded through a suitably shaped and sized die to form extrudate particles, which are dried and calcined by known methods. Alternatively, spherical particles may be formed by methods described hereinabove for the conversion catalyst of the physical mixture. An alkali metal component is an essential constituent of the sulfur-sensitive reforming catalyst when it contains an L-Zeolite. One or more of the alkali metals, including lithium, sodium, potassium, rubidium, cesium and mixtures thereof, may be used, with potassium being preferred. The alkali metal optimally will occupy essentially all of the cationic exchangeable sites of the non-acidic L-zeolite. Surface-deposited alkali metal also may be present as described in US-A-4 619 906, incorporated herein by reference thereto. The sulfur-sensitive reforming catalyst generally will be dried at a temperature of from 100 o to 320 o C for 0.5 to 24 hours, followed by oxidation at a temperature of 300 o to 550 o C (preferably 350 o C) in an air atmosphere for 0.5 to 10 hours. Preferably the oxidized catalyst is subjected to a substantially water-free reduction step at a temperature of about 300 o to 550 o C (preferably 350 o C) for 0.5 to 10 hours or more. The duration of the reduction step should be only as long as necessary to reduce the platinum, in order to avoid pre-deactivation of the catalyst, and may be performed in-situ as part of the plant startup if a dry atmosphere is maintained. Further details of the preparation and activation of embodiments of the sulfur-sensitive reforming catalyst are disclosed, e.g., in US-A-4 619 906 and US-A-4 822 762, which are incorporated into this specification by reference thereto. In this embodiment, as described hereinbelow, the catalyst also contains an alkali metal component and the preferred binder is a nonacidic amorphous silica. The final conversion catalyst, as formed into first particles for preparation of the present physical mixture, generally will be dried at a temperature of from 100 o to 320 o C for 0.5 to 24 hours, followed by oxidation at a temperature of 300 o to 550 o C in an air atmosphere for 0.5 to 10 hours. Preferably the oxidized catalyst is subjected to a substantially waterfree reduction step at a temperature of about 300 o to 550 o C for 0.5 to 10 hours or more. The sulfur sensitivity of the conversion catalyst is measured as a Sulfur-Sensitivity Index or "SSI." The SSI is a measure of the effect of sulfur in a hydrocarbon feedstock to a catalytic reforming process on catalyst performance, especially on catalyst activity. The SSI is measured as the relative deactivation rate with and without sulfur in the feedstock for the processing of a hydrocarbon feedstock to achieve a defined conversion at defined operating conditions. Deactivation rate is expressed as the rate of operating temperature increase per unit of time (or, giving equivalent results, per unit of catalyst life) to maintain a given conversion; deactivation rate usually is measured from the time of initial operation when the unit reaches a steady state until the "end-of-run," when deactivation accelerates or operating temperature reaches an excessive level as known in the art. Conversion may be determined on the basis of product octane number, yield of a certain product, or, as here, feedstock disappearance. In the present application, deactivation rate at a typical feedstock sulfur content of 0.4 ppm (400 ppb) is compared to deactivation rate with a sulfur-free feedstock: SSI = D S / D O D S = deactivation rate with 0.4 ppm sulfur in feedstock D O = deactivation rate with sulfur-free feedstock "Sulfur-free" in this case means less than 50 ppb, and more usually less than 20 ppb, sulfur in the feedstock. As a ratio, SSI would not be expected to show large variances with changes in operating conditions. The base operating conditions defining SSI in the present application are a pressure of 456 kPa (4.5 atmospheres), liquid hourly space velocity (LHSV) of 2 h -1 , hydrogen to hydrocarbon molar ratio of 3, and conversion of hexanes and heavier hydrocarbons in a raffinate from aromatics extraction as defined in the examples. Other conditions are related in the examples. Operating temperature is varied to achieve the defined conversion, with deactivation rate being determined by the rate of temperature increase to maintain conversion as defined above. A sulfur-sensitive catalyst has an SSI of over 1.2, and preferably at least about 2.0. Catalysts with an SSI of about three or more are particularly advantageously protected from sulfur deactivation according to the present invention. It is essential that the sulfur sorbent of the invention not only be effective for removal of small amounts of sulfur compounds from hydrocarbon streams at conversion-catalyst operating conditions, but also that the sorbent be compatible with the conversion catalyst in order to maintain the activity of the catalyst. The sulfur sorbent comprises a metal oxide, preferably selected from oxides of the metals having an atomic number between 19 and 30 inclusive; these metals, particularly potassium, calcium, vanadium, manganese, nickel, copper and zinc are known to be effective for sulfur removal in various circumstances. The sorbent preferably comprises a manganese component. Manganese oxide has been found to provide reforming catalyst protection superior to the zinc oxide of the prior art, it is believed, due to possible zinc contamination of associated reforming catalyst. The manganese oxides include MnO, Mn 3 O 4 , Mn 2 O 3 , MnO 2 , MnO 3 , and Mn 2 O 7 . The preferred manganese oxide is MnO (manganous oxide). The manganese component may be composited with a suitable binder such as clays, graphite, or inorganic oxides including one or more of alumina, silica, zirconia, magnesia, chromia or boria in order to provide a second particle for the physical mixture of the present catalyst system. Preferably, the manganese component is unbound and consists essentially of manganese oxide. Even more preferably the manganese component consists essentially of MnO, which has demonstrated excellent results for sulfur removal and has shown adequate particle strength without a binder for the second particle of the present invention. As an alternative embodiment of the present invention, the physical mixture of conversion catalyst and sulfur sorbent is contained within the same catalyst particle. In this embodiment, the catalyst and sorbent may be ground or milled together or separately to form particles of suitable size, preferably less than 100 microns, and the particles are supported in a suitable matrix. Preferably, the matrix is selected from the inorganic oxides described hereinabove. The physical mixture of conversion catalyst and sulfur sorbent is contained either in a fixed-bed reactor or in a moving-bed reactor whereby catalyst may be continuously withdrawn and added. These alternatives are associated with catalyst-regeneration options known to those of ordinary skill in the art, such as: (1) a semiregenerative unit containing fixed-bed reactors maintains operating severity by increasing temperature, eventually shutting the unit down for catalyst regeneration and reactivation; (2) a swing-reactor unit, in which individual fixed-bed reactors are serially isolated by manifolding arrangements as the catalyst become deactivated and the catalyst in the isolated reactor is regenerated and reactivated while the other reactors remain on-stream; (3) continuous regeneration of catalyst withdrawn from a moving-bed reactor, with reactivation and substitution of the reactivated catalyst, permitting higher operating severity by maintaining high catalyst activity through regeneration cycles of a few days; or: (4) a hybrid system with semiregenerative and continuous-regeneration provisions in the same unit. The preferred embodiment of the present invention is fixed-bed reactors in a semiregenerative unit. The present catalyst system may be utilized in a hydrocarbon-conversion process, and preferably in a reforming process which also utilizes a catalyst which is highly sulfur-sensitive. The catalyst system may be contained in one reactor or in multiple reactors with provisions known in the art to adjust inlet temperatures to individual reactors. The feed may contact the catalyst system in each of the respective reactors in either upflow, downflow, or radial-flow mode. Since the preferred reforming process operates at relatively low pressure, the low pressure drop in a radial-flow reactor favors the radial-flow mode. Operating conditions used in the process of the present invention include a pressure of from 101.3 to 6078 kPa (1 to 60 atmospheres), with the preferred range being from 101.3 to 2026 kPa (1 to 20 atmospheres) and a pressure of below 10 atmospheres being especially preferred. Free hydrogen preferably is supplied to the process in an amount sufficient to correspond to a ratio of from 0.1 to 10 moles of hydrogen per mole of hydrocarbon feedstock. By "free hydrogen" is meant molecular H 2 , not combined in hydrocarbons or other compounds. Preferably, the reaction is carried out in the absence of added halogen. The volume of the physical mixture of catalyst and sorbent corresponds to a liquid hourly space velocity of from 0.5 to 40 h -1 . The operating temperature generally is in the range of 260 o to 560 o C. This temperature is selected to convert sulfur compounds in the feedstock to H 2 S in order to arrest sulfur from contacting a subsequent sulfur-sensitive catalyst. Hydrocarbon types in the feedstock also influence temperature selection, as naphthenes generally are dehydrogenated over the first reforming catalyst with a concomitant decline in temperature across the catalyst bed due to the endothermic heat of reaction. The temperature generally is slowly increased during each period of operation to compensate for inevitable catalyst deactivation. The hydrocarbon feedstock will comprise paraffins and naphthenes, and may comprise aromatics and small amounts of olefins, preferably boiling within the gasoline range. Feedstocks which may be utilized include straight-run naphthas, natural gasoline, synthetic naphthas, thermal gasoline, catalytically cracked gasoline, partially reformed naphthas or raffinates from extraction of aromatics. The distillation range may be that of a full-range naphtha, having an initial boiling point typically from 40 o -80 o C and a final boiling point of from 160 o -210 o C, or it may represent a narrower range within a lower final boiling point. Light paraffinic feedstocks, such as naphthas from Middle East crudes having a final boiling point of from 100 o -160 o C, are preferred due to the specific ability of the process to dehydrocyclize paraffins to aromatics. Raffinates from aromatics extraction, containing principally low-value C 6 -C 8 paraffins which can be converted to valuable B-T-X aromatics, are especially preferred feedstocks. The hydrocarbon feedstock to the present process contains small amounts of sulfur compounds, amounting to generally less than 10 parts per million (ppm) on an elemental basis. Preferably the hydrocarbon feedstock has been prepared from a contaminated feedstock by a conventional pretreating step such as hydrotreating, hydrorefining or hydrodesulfurization to convert such contaminants as sulfurous, nitrogenous and oxygenated compounds to H 2 S, NH 3 and H 2 O, respectively, which then can be separated from the hydrocarbons by fractionation. This pretreatment step preferably will employ a catalyst known to the art comprising an inorganic oxide support and metals selected from Groups VIB(6) and VIII(9-10) of the Periodic Table. Alternatively or in addition to the conventional hydrotreating, the pretreating step may comprise contact with sorbents capable of removing sulfurous and other contaminants. These sorbents may include but are not limited to zinc oxide, iron sponge, high-surface-area sodium, high-surface-area alumina, activated carbons and molecular sieves; excellent results are obtained with a nickel-on-alumina sorbent. Preferably, the pretreating step will provide the reforming catalyst system with a hydrocarbon feedstock having low sulfur levels disclosed in the prior art as desirable reforming feedstocks, e.g., 1 ppm to 0.1 ppm (100 ppb); sulfur levels of 0.5 to 0.15 ppm are usual in modern pretreating units. Hydrocarbon product from the processing of the hydrocarbon feed in the present catalyst system generally will be essentially sulfur-free. Sulfur-free is defined as containing less than 20 parts per billion (ppb), and preferably less than 14 ppb, sulfur. In another aspect, sulfur-free is defined as containing no detectable sulfur. The repeatability of the American National Standard test ASTM D 4045-87 is 20 ppb at a sulfur level of 0.02 ppm (20 ppb), and "sulfur free" according to this test therefore would be defined as less than 20 ppb sulfur. It is believed, however, that one laboratory testing a series of similar samples can detect differences at lower sulfur levels, e.g., 10 µg/ml or 14 ppb sulfur. The catalyst system may be utilized in a first conversion zone containing the physical mixture of the sulfur-sensitive conversion catalyst and sulfur sorbent with one or more subseqnent conversion zones containing only the sulfur-sensitive catalyst. The first and one or more of the subsequent conversion zones may be contained in separate reactors or in the same reactor. It is within the scope of the invention that the catalyst system is utilized. in a reactor system containing multiple successive reactors, two or more of which contain both a first conversion zone containing the catalyst system and a second conversion zone containing only the sulfur-sensitive conversion catalyst. Multiple reactors, each containing the physical mixture as well as the sulfur-sensitive catalyst, would be effective where sulfur-contaminated equipment may release sulfur into the feed to the reactors or sulfur is injected into the feed to the reactor. For example, sulfur amounting to about 0.1 ppm relative to the feedstock may be injected to passivate equipment surfaces such as heater tubes. The second and subsequent conversion zones operates at a pressure, consistent with that of the first conversion zone described hereinabove, of from 101.3 to 6078 kPa (1 to 60 atmospheres) and preferably from 101.3 kPa to 2026 kPa (1 to 20 atmospheres). Excellent results have been obtained at operating pressures of less than 1013 kPa (10 atmospheres). The free hydrogen to hydrocarbon mole ratio is from about 0.1 to 10 moles of hydrogen per mole of hydrocarbon from the first conversion zone. Preferably, the reaction is carried out in the absence of added halogen. Space velocity with respect to the volume of sulfur-sensitive reforming catalyst is from about 0.2 to 10 h -1 . Operating temperature is from about 400 o to 560 o C, and may be controlled independently of temperature in the first conversion zone as indicated hereinabove. Reactants preferably contact the physical mixture and the sulfur-sensitive catalyst consecutively in a downflow manner and it is within the scope of the invention that a vapor, liquid, or mixed-phase stream is injected between the zones to control the inlet temperature of the reactants to the sulfur-sensitive catalyst. Using techniques and equipment known in the art, the aromatics-containing effluent from the second conversion zone usually is passed through a cooling zone to a separation zone. In the separation zone, typically maintained at about 0 o to 65 o C, a hydrogen-rich gas is separated from a liquid phase. The resultant hydrogen-rich stream can then be recycled through suitable compressing means back to the first conversion zone. The liquid phase from the separation zone is normally withdrawn and processed in a fractionating system in order to adjust the concentration of light hydrocarbons and produce an aromatics-containing reformate product. The following examples are presented to illustrate the present invention in comparison to the prior art. Comparative Example I The Sulfur-Sensitivity Index of a reforming catalyst of the prior art was determined. The extruded platinum-rhenium on chlorided alumina reforming catalyst used in this determination was designated Catalyst A and contained 0.25 mass % platinum and 0.40 mass % rhenium. The SSI of this catalyst was tested by processing a hydrotreated naphtha in two comparative pilot-plant runs, one in which the naphtha was substantially sulfur-free and a second in which the naphtha was sulfur-spiked with thiophene to obtain a sulfur concentration of about 0.4 mass parts per million (ppm) in the feed. The naphtha feed had the following characteristics: Sp. gr. 0.746 ASTM D-86, o C: IBP 85 50% 134 EP 193 The naphtha was charged to the reactor in a downflow operation, with operating conditions as follows: Pressure, Kpa 1520 Hydrogen/hydrocarbon, mol 2 Liquid hourly space velocity, h -1 2.5 Target octane number was 98.0 Research Clear. The tests were carried out to an end-of-run temperature of about 535 o C. The Sulfur-Sensitivity Index was calculated on the basis of the relative deactivation rates with and without 0.4 ppm sulfur in the feed. Within the precision of the test, the deactivation rates were the same with and without sulfur in the feed at 3.0 o C/day, and the SSI for Catalyst A therefore was 1.0. Catalyst A therefore represents a control catalyst of the prior art with respect to Sulfur-Sensitivity Index. Comparative Example II The Sulfur-Sensitivity Index of a second non-zeolitic reforming catalyst was determined. The spherical platinum-rhenium on chlorided alumina reforming catalyst used in this determination was designated Catalyst B and contained 0.22 mass % platinum and 0.44 mass % rhenium. The SSI of this catalyst was tested by processing hydrotreated naphtha in two sets of comparative pilot-plant runs, one each in which the naphtha was substantially sulfur-free (Runs B-1 and B-1') and one each in which the naphtha was sulfur-spiked with thiophene (Runs B-2 and B-2') to obtain a sulfur concentration of about 0.4 mass parts per million (ppm) in the feed. The naphtha feed differed in each of the sets of runs and had the following characteristics: B-1,B-2 B-1',B-2' Sp. gr. 0.746 0.744 ASTM D-86, o C: IBP 85 79 50% 134 130 EP 193 204 The naphtha was charged to the reactor in a downflow operation, with operating conditions as follows: B-1,B-2 B-1',B-2' Pressure, kPa 1520 1823 Hydrogen/hydrocarbon, mol 2 2 Liquid hourly space velocity, h -1 2.5 2.5 Target octane number was 98.0 Research Clear. The tests were carried out to an end-of-run temperature of about 535 o C. The Sulfur-Sensitivity Index was calculated on the basis of the relative deactivation rates with and without 0.4 ppm sulfur in the feed, with the following results: B-1 1.6 o C/day B-2 2.5 o C/day SSI = B-2/B-1 = 1.6 B-1' 0.85 o C/day B-2' 1.1 o C/day SSI = B-2'/B-1' = 1.3 Comparative Example III The Sulfur-Sensitivity Index of a highly sulfur-sensitive reforming catalyst was determined. The silica-bound potassium-form L-zeolite reforming catalyst used in this determination was designated Catalyst C and contained 0.82 mass % platinum. The SSI of this catalyst was tested by processing a hydrotreated naphtha in two comparative pilot-plant runs, one in which the naphtha was substantially sulfur-free (Run C-1) and a second in which the naphtha was sulfur-spiked with thiophene to obtain a sulfur concentration of about 0.4 mass parts per million (ppm) in the feed (Run C-2). The naphtha feed had the following additional characteristics: Sp. gr. 0.6896 ASTM D-86, o C: IBP 70 50% 86 EP 138 The naphtha was charged to the reactor in a downflow operation, with operating conditions as follows: Pressure, kPa 456 Hydrogen/hydrocarbon, mol 3 Liquid hourly space velocity, h -1 2 The tests were carried out to an end-of-run temperature of about 480 o C. The Sulfur-Sensitivity Index was calculated on the basis of the relative deactivation rates with and without 0.4 ppm sulfur in the feed, with the following results: C-1 0.3 o C/day C-2 4.0 o C/day SSI = C-2/C-1 = 13 EXAMPLE The advantage of the catalyst system of the invention in comparison to the prior art is illustrated via the comparative processing of 1000 metric tons per day of naphtha containing 0.5 mass ppm sulfur as thiophene. Equal volumes of a conversion catalyst and a sulfur sorbent are loaded in reactors to achieve an overall liquid hourly space velocity of 5 for both the illustration of the invention and the comparative case of the prior art. The catalyst and sorbent are physically mixed to illustrate the invention, and the conversion catalyst is loaded above the sulfur sorbent to illustrate the prior art. The relative quantities of catalyst and sorbent are as follows: Conversion catalyst 4.8 tons Sulfur sorbent 9.6 tons The conversion catalyst is a sulfur-sensitive reforming catalyst as described hereinabove which suffers a rapid decline in dehydrocyclization capability in the presence of sulfur but retains capability for sulfur conversion up to its sulfur capacity, which is about 0.1 mass %. The conversion catalyst contains platinum on silica-bound potassium-form L-zeolite. As shown in Comparative Example III, it had a sulfur-sensitivity index of approximately 13. The sulfur sorbent is essentially pure manganous oxide, with a sulfur capacity of about 5 mass %. The days of operation until full sulfur loading is achieved illustrates the advantage of the invention: Invention: 970 days Prior art 9.6 days

Claims: A catalyst system comprising a sulfur-sensitive reforming catalyst comprising a nonacidic large-pore molecular sieve, at least one platinum-group metal component and a refractory inorganic-oxide support, characterized in that the sulfur-sensitive reforming catalyst is in physical admixture with a sulfur sorbent comprising a manganese oxide. The catalyst system of Claim 1 comprising a physical mixture of (i) first particles comprising the conversion catalyst and essentially free of the sulfur sorbent and (ii) second particles comprising the sulfur sorbent and essentially free of the conversion catalyst. The catalyst system of Claim 1 or 2 wherein the nonacidic large-pore molecular sieve comprises nonacidic L-zeolite and wherein the platinum-group metal component comprises a platinum component. The catalyst system of Claim 1, 2 or 3 wherein the sulfur-sensitive reforming catalyst consists essentially of a nonacidic L-zeolite, an alkali metal component, a platinum-group metal component and an inorganic-oxide binder. The catalyst system of any one of Claims 1 to 4 comprising a physical mixture of the conversion catalyst and sulfur sorbent on the same catalyst particle. A process for the reforming of a hydrocarbon feedstock comprising contacting the feedstock at reforming conditions with the catalyst system defined in any one of Claims 1 to 5. The process of Claim 6 wherein the naphtha feedstock contains less than 10 mass ppm sulfur.

Inventors: RUSS MICHAEL B, SECHRIST PAUL A, RUSS, MICHAEL B., SECHRIST, PAUL A.
Applicants: UOP INC, UOP
Application year: 1994
Main classification: B01J23
IPC codes: C10G35, B01J23, B01J29