Polyimide resin composition having excellent fatigue resistance and injection molded article of same

Abstract: The present invention relates to an extremely fatigue-resistant polyimide resin composition comprising 100 parts by weight of polyimide having from 0.5 (exclusive) to 1.0 (inclusive) mole ratio of recurring structural units represented by the formula (1) and from 0 (inclusive) to 0.5 (exclusive) mole ratio of recurring structural units represented by the formula (2) : wherein X is in the formulas (1) and (2), and having an inherent viscosity of 0.45 dℓ /g or more ; and 5∼65 parts by weight of a carbon fiber, glass fiber, aromatic polyamide fiber and/or potassium titanate fiber, and an injection molded article made from the polyimide resin composition.

Description: The present invention relates to a fatigue-resistant polyimide resin composition and an injection molded article of the same, and more particularly relates to a polyimide resin composition having good melt-processing ability and excellent fatigue resistance and an injection molded article obtained from the polyimide resin composition. Conventionally, polyimide has a high heat resistance, excellent mechanical strength and outstanding dimensional stability and additionally has flame retardance and electrical insulation property. Thus, polyimide has been widely used in the fields of electric and electronic appliances, space and aeronautic equipment and transport machinery. Various kinds of polyimides which exhibit excellent properties have been conventionally developed. However, some polyimide has no distinct glass transition temperature although heat resistance is excellent, and must be processed with a specific means such as sinter molding in the case of being used as a molded material. Other polyimide is excellent in processing ability. On the other hand, such polyimide has a low glass transition temperature and additionally is soluble in halogenated hydrocarbon solvents, and is unsatisfactory in view of resistance to heat and solvent. Thus, conventional polyimide has exhibited both merits and drawbacks in terms of property. In order to solve these problems, the present inventors have developed polyimide and various copolyimides which can be melt-processed and are excellent in mechanical strengths, heat resistance, electrical property and chemical resistance (Japanese Laid-Open Patent SHO 61-143478 and HEI 3-47837). However, dynamic mechanical properties such as fatigue property have not been examined so much and almost no information can be found under the existing circumstances in the fields of an injection-moldable high-heat-resistance polyimide which has been developed particularly in recent years. EP-A-0511813 discloses a heat resistant adhesive comprising a polyamic acid and/or polyimide prepared using 1,3-bis(3-aminophenoxy)benzene as an aromatic diamine component and 3,3', 4, 4'-biphenyltetracarboxylic dianhydride, 3,3', 4, 4'-benzophenonetetracarboxylic dianhydride and/or 3,3', 4,4'-diphenylethertetracarboxylic dianhydride as tetracarboxylic acid dianhydrides. EP-A-0 294129 discloses polyimide resin compositions for moulding in which the polyimide is prepared from an etherdiamine component of formula: wherein x is a direct bond, thio radical or a phenylene dicarbonyl radical. The compositions of the reference are said to have good moulding ability, temperature stability, chemical resistance and mechanical strength. An object of the invention is to provide a polyimide resin composition which can be melt processed by injection molding and other means and which desirably has high fatigue resistance, and an injection molded article prepared from the composition. As a result of an intensive investigation in order to solve the above problems, the present inventors have found that a polyimide resin composition obtained by using polyimide having specific structure and a molecular weight above a certain level can exhibit excellent melt-flow characteristics and moldability and that an injection molded article having outstanding fatigue resistance can be obtained from the resin composition. Thus, the invention has been completed. That is, aspects of the invention are : (A) a polyimide resin composition, preferably extremely fatigue resistant, comprising 100 parts by weight of polyimide having from 0.5 (exclusive) to 1.0 (inclusive) mole ratio of recurring structural units represented by the formula (1) : and from 0 (inclusive) to 0.5 (exclusive) mole ratio of recurring structural units represented by the formula (2) : wherein X is in the formulas (1) and (2), and having an inherent viscosity of 0.45 dℓ /g or more, and 5 ∼ 65 parts by weight of a carbon fiber, glass fiber, aromatic polyamide fiber and/or potassium titanate fiber ; (B) a polyimide resin composition, preferably extremely fatigue-resistant, comprising 100 parts by weight of polyimide having a polymer of capped molecular chain end obtained by preparing the polyimide of the above (A) in the presence of an aromatic dicarboxylic anhydride represented by the formula (3) : wherein Z is a divalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or an aromatic monoamine represented by the formula (4) : V-NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and having an inherent viscosity of 0.45 dℓ /g or more, and 5 ∼ 65 parts by weight of a carbon fiber, glass fiber, aromatic polyaromatic fiber and/or potassium titanate fiber ; and (C) an injection molded article obtained from these polyimide resin compositions. The polyimide resin compositions of the present invention can provide an injection molded article which is extremely fatigue resistant. Polyimide used in the invention is a homopolymer or a copolymer of polyimide having in a polymer molecule from 0.5 (exclusive) to 1.0 (inclusive) mole ratio of recurring structural units represented by the formula (1) : wherein X is , and from 0 (inclusive) to 0.5 (exclusive) mole ratio of recurring structural units represented by the formula (2) : wherein X is That is, the polyimide homopolymer consists of recurring structural units represented by the formula (1) and does not contain recurring structural units represented by the formula (2). In practice, each polyimide homopolymer has recurring structural units of the formula (1-1) alone; or the formula (1-2) alone; Further, the polyimide copolymer used in the invention comprises more than 0 to less than 0.5 mole ratio of recurring structural units represented by the formula (2) and more than 0.5 to less than 1.0 mole ratio of recurring structural units represented by the formula (1). More particularly, representative copolymers include a polyimide copolymer which comprises recurring structural units of the formula (1-1) : in an amount of more than 0.5 to less than 1.0 mole per mole of the polymer molecule and recurring structural units of the formula (2-1) : and/or recurring structural units of the formula (2-2) : in an amount of more than 0 to less than 0.5 mole per mole of the polymer molecule ; and a polyimide copolymer which comprises recurring structural units of the formula (1-2) : in an amount of more than 0.5 to less than 1.0 mole per mole of the polymer molecule and recurring structural units of the formula (2-1) : and/or recurring structural units of the formula (2-2) : in an amount of more than 0 to less than 0.5 mole per mole of the polymer molecule. When the recurring structural units include both the formula (2-1) and the formula (2-2) in these polyimide copolymers, no particular restriction is imposed upon the proportion between these two kinds of units and they can be used in an arbitrary proportion. Other polyimide copolymers comprising recurring structural units of the formula (1-1) and those of the formula (1-2) in an arbitrary proportion are also included in the scope of the invention. The above homopolymers and copolymers of polyimide can comprise polyimide having other recurring structural units in a range of giving no hindrance on the effect of the invention. The above homopolymers and copolymers of polyimide are preferably capped at the polymer chain end with aromatic dicarboxylic anhydride represented by the formula (3) : wherein Z is a divalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or an aromatic monoamine represented by the formula (4) : V-NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or bridge member. Polyimide used in the invention has an inherent viscosity of 0.45 dℓ /g or more, Preferably 0.50 dℓ /g or more. The inherent viscosity is measured by heat-dissolving 0.5 g polyimide powder in 100 m ℓ of a solvent mixture of p-chlorophenol/phenol (9:1) and cooling the obtained solution to 35°C. When the inherent viscosity is less than 0.45 dℓ /g, the polyimide resin composition comprised of the polyimide resin and reinforcements cannot provide good fatigue resistance for the injection molded article obtained from the polyimide resin composition. Polyimide which can be used in the invention and has an inherent viscosity of 0.45 dℓ /g or more can be prepared by the following process. Diamines used are 1,3-bis(3-aminophenoxy)benzene of the formula (5) : and 4,4'-bis(3-aminophenoxy)biphenyl of the formula (6) : Tetracarboxylic dianhydrides used are pyromellitic dianhydride of the formula (7) : and 3,3',4,4'-biphenyltetracarboxylic dianhydride of the formula (8) : These diamines and tetracarboxylic dianhydrides are used by the following processes for preparing the homopolymers and copolymers of polyimide in the invention. In the case of preparing the polyimide homopolymer consisting of recurring structural units of the formula (1-1) or the formula (1-2), or the polyimide copolymer consisting of recurring structural units of the formula (1-1) and those of the formula (1-2), the diamine of the formula (5) is individually reacted with tetracarboxylic dianhydride of the formula (7) or that of the formula (8), or reacted with a mixture of tetracarboxylic dianhydride of the formula (7) and that of the formula (8). In the case of preparing the polyimide copolymer having recurring structural units represented by the formula (1) and those represented by the formula (2), a mixture of diamine of the formula (5) and diamine of the formula (6) is individually reacted with tetracarboxylic dianhydride of the formula (7) or that of the formula (8), or reacted with a mixture of tetracarboxylic dianhydride of the formula (7) and that of the formula (8). When the diamine of the formula (5) and the diamine of the formula (6) are used as a mixture, the amount of diamine of the formula (5), i.e., 1,3-bis(3-aminophenoxy)benzene, is more than 0.5 to less than 1.0 mole per mole of the total diamine, and the amount of diamine of the formula (6), i.e., 4,4'-bis(3-aminophenoxy)biphenyl is less than 0.5 mole per mole of the total diamine. When the amount of 4,4'-bis(3-aminophenoxy)biphenyl is 0.5 mole or more, the polyimide resin composition comprised of the polyimide resin and reinforcements has decreased processing ability and provides an injection molded article having low fatigue resistance. In the case of using tetracarboxylic dianhydrides of the formulas (7) and (8) as a mixture, no particular limitation is imposed upon the proportion of these anhydrides. These anhydrides can be mixed in an arbitrary proportion. One or more of other diamines and tetracarboxylic dianhydrides can be incorporated with the above raw materials in the polymerization as long as giving no adverse effect on the properties of polyimide. Representative other diamines which can be added include, for example, m-phenylenediamine, o-phenylenediamine, p-phenylenediamine, m-aminobenzylamine, o-aminobenzylamine, p-aminobenzylamine, 3-chloro-1,2-phenylenediamine, 4-chloro-1,2-phenylenediamine, 2,3-diaminotoluene, 2,4-diaminotoluene, 2,5-diaminotoluene, 2,6-diaminotoluene, 3,4-diaminotoluene, 3,5-diaminotoluene, 2-methoxy-1,4-phenylenediamine, 4-methoxy-1,2-phenylenediamine, 4-methoxy-1,3-phenylenediamine, benzidine, 3,3'-dichlorobenzidine, 3,3'-dimethylbenzidine, 3,3'-dimethoxybenzidine, 3,3'-diaminodiphenyl ether, 3,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl ether, 3,3'-diaminodiphenyl sulfide, 3,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenyl sulfide, 3,3'-diaminodiphenyl sulfoxide, 3,4'-diaminodiphenyl sulfoxide, 4,4'-diaminodiphenyl sulfoxide, 3,3'-diaminodiphenyl sulfone, 3,4'-diaminodiphenyl sulfone, 4,4'-diaminodiphenyl sulfone, 3,3'-diaminobenzophenone, 3,4'-diaminobenzophenone, 4,4'-diaminobenzophenone, 3,3'-diaminodiphenylmethane, 3,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylmethane, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 1,3-bis(3-aminobenzoyl)benzene, 1,4-bis(3-aminobenzoyl)benzene, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 3,3'-bis(3-aminophenoxy)biphenyl, 4,4'-bis(4-aminophenoxy)biphenyl, 3,3'-bis(4-aminophenoxy)biphenyl, 4,4'-bis(3-aminophenoxy)-3-methylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3'-dimethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dimethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetramethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3'-dichlorobiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dichlorobiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetrachlorobiphenyl, 4,4'-bis(3-aminophenoxy)-3,3'-dibromobiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dibromobiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetrabromobiphenyl, bis[3-(3-aminophenoxy)phenyl]methane, bis[3-(4-aminophenoxy)phenyl]methane, bis[4-(3-aminophenoxy)phenyl]methane, bis[4-(4-aminophenoxy)phenyl]methane, 1,1-bis[4-(3-aminophenoxy)phenyl]ethane, 1,1-bis[4-(4-aminophenoxy)phenyl]ethane, 1,2-bis[4-(3-aminophenoxy)phenyl]ethane, 1,2-bis[4-(4-aminophenoxy)phenyl]ethane, 1,1-bis[4-(3-aminophenoxy)phenyl]propane, 1,1-bis[4-(4-aminophenoxy)phenyl]propane, 1,2-bis[4-(3-aminophenoxy)phenyl]propane, 1,2-bis[4-(4-aminophenoxy)phenyl]propane, 1,3-bis[4-(3-aminophenoxy)phenyl]propane, 1,3-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 2-[4-(4-aminophenoxy)phenyl]-2-[4-(4-aminophenoxy)-3-methylphenyl]propane, 2,2-bis[4-(4-aminophenoxy)-3-methylphenyl]propane, 2-[4-(4-aminophenoxy)phenyl]-2-[4-(4-aminophenoxy)-3,5-dimethylphenyl]propane, 2,2-bis[4-(4-aminophenoxy)-3,5-dimethylphenyl]propane, 2,2-bis[4-(3-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 2,2-bis[4-(4-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 2,2-bis[3-(3-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 2,2-bis[3-(4-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 1,1-bis[4-(3-aminophenoxy)phenyl]butane, 1,1-bis[4-(4-aminophenoxy)phenyl]butane, 1,2-bis[4-(3-aminophenoxy)phenyl]butane, 1,2-bis[4-(4-aminophenoxy)phenyl]butane, 1,3-bis[4-(3-aminophenoxy)phenyl]butane, 1,3-bis[4-(4-aminophenoxy)phenyl]butane, 1,4-bis[4-(3-aminophenoxy)phenyl]butane, 1,4-bis[4-(4-aminophenoxy)phenyl]butane, 2,2-bis[4-(3-aminophenoxy)phenyl]butane, 2,2-bis[4-(4-aminophenoxy)phenyl]butane, 2,3-bis[4-(3-aminophenoxy)phenyl]butane, 2,3-bis[4-(4-aminophenoxy)phenyl]butane, bis[3-(3-aminophenoxy)phenyl]ketone, bis[3-(4-aminophenoxy)phenyl]ketone, bis[4-(3-aminophenoxy)phenyl]ketone, bis[4-(4-aminophenoxy)phenyl]ketone, bis[3-(3-aminophenoxy)phenyl]sulfide, bis[3-(4-aminophenoxy)phenyl]sulfide, bis[4-(3-aminophenoxy)phenyl]sulfide, bis[4-(4-aminophenoxy)phenyl]sulfide, bis[4-(3-aminophenoxy)-3-methoxyphenyl]sulfide, [4-(3-aminophenoxy)phenyl][4-(3-aminophenoxy)-3,5-dimethoxyphenyl]sulfide bis[4-(3-aminophenoxy)-3,5-dimethoxyphenyl]sulfide bis[3-(3-aminophenoxy)phenyl]sulfoxide, bis[4-(3-aminophenoxy)phenyl]sulfoxide, bis[4-(4-aminophenoxy)phenyl]sulfoxide, bis[3-(3-aminophenoxy)phenyl]sulfone, bis[3-(4-aminophenoxy)phenyl]sulfone, bis[4-(3-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone, bis[4-(3-aminophenoxy)phenyl]ether, bis[3-(3-aminophenoxy)phenyl]ether, bis[4-(4-aminophenoxy)phenyl]ether, bis[3-(4-aminophenoxy)phenyl]ether, 1,3-bis[4-(4-aminophenoxy)benzoyl]benzene, 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene, 1,4-bis[4-(4-aminophenoxy)benzoyl]benzene, 1,4-bis[4-(3-aminophenoxy)benzoyl]benzene, 1,3-bis[4-(4-aminophenoxy)-α,α-dimethylbenzoyl]benzene, 1,3-bis[4-(3-aminophenoxy)-α,α-dimethylbenzoyl]benzene, 1,4-bis[4-(4-aminophenoxy)-α,α-dimethylbenzoyl]benzene and 1,4-bis[4-(3-aminophenoxy)-α,α-dimethylbenzoyl]benzene. These diamines can be used singly or as a mixture. Exemplary tetracarboxylic dianhydrides which can be added to the above raw materials include ethylenetetracarboxylic dianhydride, butanetetracarboxylic dianhydride, cyclopentanetetracarboxylic dianhydride, pyromellitic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride, 2,2',3,3'-benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, 2,2',3,3'-biphenyltetracarboxylic dianhydride, 2,2-bis(3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)propane dianhydride, bis(2,3-dicarboxyphenyl)ether dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis(2,3-dicarboxyphenyl)sulfone dianhydride, bis(3,4-dicarboxyphenyl)sulfone dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, 1,1-bis(3,4-dicarboxyphenyl)ethane dianhydride, 1,2-bis(2,3-dicarboxyphenyl)ethane dianhydride, 1,2-bis(3,4-dicarboxyphenyl)ethane dianhydride, 1,3-bis(2,3-dicarboxyphenoxy)benzene dianhydride, 1,3-bis(3,4-dicarboxyphenoxy)benzene dianhydride, 1,4-bis(2,3-dicarboxyphenoxy)benzene dianhydride, 1,4-bis(3,4-dicarboxyphenoxy)benzene dianhydride, 2,3,6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,2,3,4-benzenetetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride, and 1,2,7,8-phenanthrenetetracarboxylic dianhydride. These tetracarboxylic dianhydrides can be used singly or as a mixture. Polyimides used in the invention is a homopolymer or a copolymer having the above recurring structural units obtained by using these diamines and tetracarboxylic dianhydrides as monomer components. These polyimides also include those having unsubstituted polymer chain end and those substituted at the polymer chain end with aromatic monoamine and/or aromatic dicarboxylic anhydride which have no reactivity with amine or dicarboxylic anhydride. Polyimide substituted at the polymer chain end with aromatic monoamine and/or aromatic dicarboxylic anhydride can be prepared by reacting by reacting diamine of the formula (5), i.e., 1,3-bis(3-aminophenoxy)benzene, or a mixture of the same and diamine of the formula (6), i.e., 4,4'-bis(4-aminophenoxy)biphenyl, with tetracarboxylic dianhydride of the formula (7), i.e.,pyromellitic dianhydride, and/or tetracarboxylic dianhydride of the formula (8) i.e., 3,3',4,4'-biphenyltetracarboxylic dianhydride, in the presence of aromatic dicarboxylic anhydride of the formula (3) wherein Z is a divalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or aromatic monoamine of the formula (4) : V-NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or a bridge member. Exemplary aromatic dicarboxylic anhydrides of the formula (3) include phthalic anhydride, 2,3-benzophenonedicarboxylic anhydride, 3,4-benzophenonedicarboxylic anhydride, 2,3-dicarboxyphenyl phenyl ether anhydride, 3,4-dicarboxyphenyl phenyl ether anhydride, 2,3-biphenyldicarboxylic anhydride, 3,4-biphenyldicarboxylic anhydride, 2,3-dicarboxyphenyl phenyl sulfone anhydride, 3,4-dicarboxyphenyl phenyl sulfone anhydride, 2,3-dicarboxyphenyl phenyl sulfide anhydride, 3,4-dicarboxyphenyl phenyl sulfide anhydride, 1,2-naphthalenedicarboxylic anhydride, 2,3-naphthalenedicarboxylic anhydride, 1,8-naphthalenedicarboxylic anhydride, 1,2-anthracenedicarboxylic anhydride, 2,3-anthracenedicarboxylic anhydride and 1,9-anthracenedicarboxylic anhydride. These dicarboxylic anhydrides can be substituted with a radical having no reactivity with amine or dicarboxylic anhydride, and can be used singly or as a mixture. Phthalic anhydride is most preferred in these aromatic dicarboxylic anhydrides in view of properties and practical usage of resulting polyimide. The amount of aromatic dicarboxylic anhydride is 0.001∼1.0 mole per mole of 1,3-bis(3-aminophenoxy)benzene of the formula (5) or a mixture of the same with 4,4'-bis(3-aminophenoxy)biphenyl of the formula (6). When the amount is less than 0.001 mole, viscosity increase is observed in molding at high temperature and leads to deterioration of molding ability. On the other hand, the amount exceeding 1.0 mole causes reduction of mechanical properties. Preferred amount is 0.01 ∼ 0.5 mole. Exemplary aromatic monoamines of the formula (4) , for example, aniline, o-toluidine, m-toluidine, p-toluidine, 2,3-xylidine, 2,6-xylidine, 3,4-xylidine, 3,5-xylidine, o-chloroaniline, m-chloroaniline, p-chloroaniline, o-bromoaniline, m-bromoaniline, p-bromoaniline, o-nitroaniline, m-nitroaniline, p-nitroaniline, o-aminophenol, m-aminophenol, p-aminophenol, o-anisidine, m-anisidine, p-anisidine, o-phenetidine, m-phenetidine, p-phenetidine, o-aminobenzaldehyde, m-aminobenzaldehyde, p-aminobenzaldehyde, o-aminobenzonitrile, m-aminobenzonitrile, p-aminobenzonitrile, 2-aminobiphenyl, 3-aminobiphenyl, 4-aminobiphenyl, 2-aminophenyl phenyl ether, 3-aminophenyl phenyl ether, 4-aminophenyl phenyl ether, 2-aminobenzophenone, 3-aminobenzophenone, 4-aminobenzophenone, 2-aminophenyl phenyl sulfide, 3-aminophenyl phenyl sulfide, 4-aminophenyl phenyl sulfide, 2-aminophenyl phenyl sulfone, 3-aminophenyl phenyl sulfone, 4-aminophenyl phenyl sulfone, α-naphthylamine, β-naphthylamine, 1-amino-2-naphthol, 2-amino-1-naphthol, 4-amino-1-naphthol, 5-amino-1-naphthol, 5-amino-2-naphthol, 7-amino-2-naphthol, 8-amino-1-naphthol, 8-amino-2-naphthol, 1-aminoanthracene, 2-aminoanthracene, and 9-aminoanthracene. These aromatic monoamines can be substituted with a radical having no reactivity for amine or dicarboxylic anhydride and can be used singly or as a mixture. The amount of aromatic monoamine is 0.001 ∼ 1.0 mole per mole of tetracarboxylic dianhydride of the formula (7), i.e., pyromellitic dianhydride and/or tetracarboxylic dianhydride of the formula (8), i.e., 3,3',4,4'-biphenyltetracarboxylic dianhydride. When the amount is less than 0.001 mole, viscosity increases in the high temperature processing step and results in deterioration of processing ability. On the other hand, the amount exceeding 1.0 mole leads to reduction of mechanical properties. Thus, preferred amount is 0.01 ∼ 0.5 mole. Polyimide used in the invention can be prepared by any known processes. Known processes include, for example : 1) a process for preparing polyamic acid in an organic solvent, isolating polyamic acid by removing the solvent under reduced pressure or by pouring a resultant polyamic acid solution into a lean solvent, and imidizing the isolated polyamic acid by heating to obtain polyimide, 2) a process for obtaining a polyamic acid solution by the same procedures as described in 1), adding a dehydrating agent such as acetic anhydride and a catalyst, if required, to carry out chemical imidization, isolating polyimide by known procedures, and successively carrying out washing and drying when necessary, 3) a process for obtaining a polyamic acid solution by the same procedures as described in 1) and successively carrying out solvent removal and heat imidization at the same time by heating under reduced pressure, and 4) a process for charging raw materials into an organic solvents, heating the mixture to simultaneously carry out preparation and imidization of polyamic acid in the presence of, if necessary, a catalyst, azeotropic agent and dehydrating agent. Preparation of polyimide is particularly preferred to carry out in a solvent. Exemplary organic solvents which can be used include, for example, N,N-dimethylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, N,N-dimethylmethoxyacetamide, N-methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, N-methylcaprolactam, 1,2-dimethoxyethane, bis(2-methoxyethyl)ether, 1,2-bis(2-methoxyethoxy)ethane, bis[2-(2-methoxyethoxy)ethyl]ether, tetrahydrofuran, 1,3-dioxane, 1,4-dioxane, pyridine, picoline, dimethyl sulfoxide, dimethyl sulfone, tetramethylurea, hexamethylphosphoramide, phenol, o-cresol, m-cresol, p-cresol, m-cresylic acid, p-chlorophenol and anisole. These solvents can be used singly or as a mixture. In the preparation process of polyimide, addition and reaction of diamines, tetracarboxylic dianhydrides and aromatic dicarboxylic anhydride or aromatic monoamine in an organic solvent can be carried out by the following methods. (a) A method for reacting tetracarboxylic dianhydride with diamine and successively adding aromatic dicarboxylic anhydride or aromatic monoamine to continue the reaction. (b) A method for reacting aromatic dicarboxylic anhydride with diamine and successively adding tetracarboxylic dianhydride to continue the reaction, or reacting tetracarboxylic dianhydride with aromatic monoamine and successively adding diamine to continue the reaction. (c) A method for adding tetracarboxylic dianhydride, diamine and aromatic dicarboxylic anhydride or aromatic monoamine are added at the same time to carry out the reaction. Any of the above methods can be carried out without difficulty. The polymerization and imidization reaction is usually carried out at the temperature of 300°C or less. No particular limitation is imposed upon the pressure in the polymerization and imidization reaction. The reaction can be satisfactorily carried out under atmospheric pressure. The reaction time of polymerization and imidization differs depending upon the kind of diamine, tetracarboxylic dianhydride and solvent and reaction temperature. Reaction time of 4 ∼ 24 hours is usually sufficient. Polyimide used for the invention can be prepared by the above processes. The polyimide composition of the invention is prepared by blending 100 parts by weight of the above polyimide resin, that is, a homopolymer or copolymer of polyimide having an inherent viscosity of 0.45 dℓ /g or more, preferably 0.50 dℓ /g or more, with 5∼65 parts by weight, preferably 10 ∼ 50 parts by weight of reinforcements such as a carbon fiber, glass fiber, aromatic polyamide fiber and/or potassium titanate fiber. When the amount of the reinforcements is less than 5 parts by weight, sufficient reinforcing effect cannot be obtained. On the other hand, the amount exceeding 65 parts by weight deteriorates injection molding ability of the polyimide resin composition itself, and cannot provide a good injection molded article. Addition of the reinforcements to the polyimide resin can be carried out by usually known methods. For example, in the most common method, polyimide powder and reinforcements are premixed with a mortar, Henschel mixer, drum blender, ball mill and ribbon blender and successively kneaded with a melt mixer or hot rolls to obtain pellets or powdery mixture. The polyimide resin composition of the invention can be practically applied to melt-processing such as injection molding, extrusion forming, compression molding, rotary molding and other various known processing methods. Polyimide used in the invention has excellent melt flowability in particular, and thus the polyimide resin composition of the invention can be most preferably applied to injection molding process in view of operation efficiency. Other resin components can be added to the polyimide resin composition of the invention in the range giving no adverse effect on the object of the invention. Exemplary other resins which can be formulated in a suitable amount depending upon the object include thermoplastic resin such as polyethylene, polypropylene, polycarbonate, polyarylate, polyamide, polysulfone, polyether sulfone, polyether ketone, polyphenylene sulfide polyamideimide, modified polyphenyleneoxide, polyimide, polyetherimide, and thermosetting resins. Solid lubricants such as molybdenum disulfide, graphite, boron nitride, lead monoxide and lead powder can also be added singly or as a mixture. Further, antioxidant, heat stabilizer, ultraviolet absorber, flame retardant, antistatic agent, colorant and other usual additives can also be added singly or as a mixture. The injection molded article of the invention can be obtained in a variety of shapes from the polyimide resin composition of the invention by changing the form of the mold in an injection molding machine. That is, the molded article of the invention can be expected to use for automobile parts such as a bubble lifter and impeller which require particularly excellent dynamic fatigue properties. The present invention will hereinafter be illustrated further in detail by way of synthetic examples, examples and comparative examples. In these examples, properties were measured by the following methods. Inherent viscosity : Measured after dissolving 0.50 g of polyimide powder in 100 mℓ of a solvent mixture composed of p-chlorophenol and phenol in a weight ratio of 90 : 10 and cooling the obtained solution to 35°C. Glass transition temperature (Tg) : Measured by DSC with a Shimadzu DT-40 Series, DSC-41M at a temperature rise rate of 16 °C/min. 5 % Weight loss temperature : Measured by DTA-Tg in the air with a Shimadzu DT-40 Series, DSC-40 M at a temperature rise rate of 10°C/min. Synthetic Example 1 To a reaction vessel equipped with a stirrer, reflux condenser, water separator and nitrogen inlet tube, 2.338 kg (8.00 moles) of 1,3-bis(3-aminophenoxy)benzene, 736.8 g (2.00 moles) of 4,4'-bis(3-aminophenoxy)biphenyl, 2.159 kg(9.90 moles) of pyromellitic dianhydride, 138 g (1.5 moles) of γ-picoline and 20.9 kg of m-cresol were charged. The mixture was heated to 145 °C with stirring in a nitrogen atmosphere while distilling out about 340 g of water. The reaction was further continued at 140 ∼ 150 °C for 4 hours. Thereafter the reaction mixture was cooled to room temperature, poured into 72.9 g of methyl ethyl ketone, and filtered. The filtered mass was further washed with methyl ethyl ketone, and dried at 50 °C for 24 hours and then at 200 °C for 6 hours in a nitrogen atmosphere. Polyimide powder thus obtained was 4.79 g (98.2 % yield). The polyimide powder had an inherent viscosity of 0.74 dℓ /g, Tg of 220 °C, and 5 % weight loss temperature of 549 °C in the air. Synthetic Example 2 The same procedures as described in Synthetic Example 1 were carried out except that 2.159 kg (9.90 moles) of pyromellitic dianhydride was replaced by 2.883 kg (9.80 moles) of 3,3',4,4'-biphenyltetracarboxylic dianhydride was used. Polyimide powder obtained was 5.49 kg (98.0 % yield). The polyimide powder had an inherent viscosity of 0.76 dℓ /g, Tg of 206 °C, and 5 % weight loss temperature of 545°C in the air. Synthetic Example 3 The same procedures as described in Synthetic Example 1 were carried out except that 2.338 kg (8.00 moles) of 1,3-bis(3-aminophenoxy) benzene and 736.8 g(2.00 moles) of 4,4'-bis(3-aminophenoxy)biphenyl were replaced by 2.923 kg (10.0 moles) of 1,3-bis(3-aminophenoxy)benzene. Polyimide powder thus obtained was 4.64 kg (98.2 % yield). The polyimide powder had an inherent viscosity of 0.74 dℓ /g, Tg of 213 °C, and 5 % weight loss temperature of 536 °C in the air. Synthetic Example 4 The same procedures as described in Synthetic Example 3 were carried out except that 2.159 kg (9.90 moles) of pyromellitic dianhydride was replaced by 2.883 kg (9.80 moles) of 3,3',4,4'-biphenyltetracarboxylic dianhydride. Polyimide powder thus obtained was 5.36 kg (98.5 % yield). The polyimide powder had an inherent viscosity of 0.80 dℓ /g, Tg of 199 °C, and 5 % weight loss temperature of 545°C in the air. Synthetic Example 5 The same procedures as described in Synthetic Example 1 were carried out except that 29.5 g (0.20 mole) of phthalic anhydride was added in the reaction. Polyimide powder thus obtained was 4.83 kg (98.6 % yield). The polyimide powder had an inherent viscosity of 0.73 dℓ /g, Tg of 218 °C, and 5 % weight loss temperature of 558°C in the air. Synthetic Example 6 The same procedures as described in Synthetic Example 2 were carried out except that 59.0 g (0.4 mole) of phthalic anhydride was added in the reaction. Polyimide powder thus obtained was 5.59 kg (98.8 % yield). The polyimide powder had an inherent viscosity of 0.74 dℓ /g, Tg of 205 °C, and 5 % weight loss temperature of 559°C in the air. Synthetic Example 7 The same procedures as described in Synthetic Example 3 were carried out except that 29.5 g (0.2 mole) of phthalic anhydride was added in the reaction. Polyimide powder thus obtained was 4.69 kg (98.7 % yield). The polyimide powder had an inherent viscosity of 0.72 dℓ /g, Tg of 212 °C, and 5 % weight loss temperature of 556°C in the air. Synthetic Example 8 The same procedures as described in Synthetic Example 4 were carried out except that 59.0 g (0.4 mole) of phthalic anhydride was added in the reaction. Polyimide powder thus obtained was 5.41 kg (98.2 % yield). The polyimide powder had an inherent viscosity of 0.78 dℓ /g, Tg of 198 °C, and 5 % weight loss temperature of 555°C in the air. Synthetic Example 9∼40 Polyimide was prepared from various diamines and acid anhydrides. Results are illustrated in Table 1∼5. Synthetic Example Diamine (mol) Acid anhydride (mol) Capping agent (mol) Yield (%) η inh (dl/g) Tg (°C) Td 5 (°C) 9 APB/m-BP 5.10/4.90 PMDA 9.90 PA 0.20 98.0 0.73 232 556 10 APB/m-BP 5.10/4.90 BPDA 9.80 PA 0.40 98.5 0.77 214 558 11 APB/m-BP 4.00/6.00 PMDA 9.90 PA 0.20 98.3 0.74 238 562 12 APB/m-BP 4.00/6.00 BPDA 9.80 PA 0.40 98.8 0.77 221 556 13 APB/m-BP 8.00/2.00 PMDA 9.75 PA 0.50 98.8 0.48 214 553 14 APB/m-BP 8.00/2.00 BPDA 9.60 PA 0.80 98.7 0.51 198 552 15 APB 10.0 PMDA 9.80 PA 0.40 98.8 0.51 210 552 Synthetic Example Diamine (mol) Acid anhydride (mol) Capping agent (mol) Yield (%) η inh (dl/g) Tg (°C) Td 5 (°C) 16 APB 10.0 BPDA 9.60 PA 0.80 98.5 0.50 195 560 17 APB 10.0 PMDA 9.70 PA 0.60 97.3 0.43 209 550 18 APB 10.0 BPDA 9.40 PA 1.20 97.2 0.43 192 555 19 APB/m-BP 8.00/2.00 PMDA 9.90 NA 0.20 98.0 0.73 218 556 20 APB 10.0 PMDA 9.90 NA 0.20 98.0 0.73 213 545 21 APB 10.0 BPDA 9.80 NA 0.40 98.5 0.79 200 564 22 APB/m-BP 7.92/1.98 PMDA 10.0 AN 0.20 98.3 0.74 217 556 Synthetic Example Diamine (mol) Acid anhydride (mol) Capping agent (mol) Yield (%) η inh (dl/g) Tg (°C) Td 5 (°C) 23 APB/m-BP 7.84/1.96 BPDA 10.0 AN 0.40 98.6 0.73 203 555 24 APB/m-BP 7.84/1.96 PMDA 10.0 AN 0.40 98.3 0.50 214 552 25 APB/m-BP 7.68/1.92 BPDA 10.0 AN 0.80 98.2 0.49 201 551 26 APB/m-BP 7.76/1.94 PMDA 10.0 AN 0.60 98.0 0.43 211 550 27 APB/m-BP 7.52/1.88 BPDA 10.0 AN 1.20 97.8 0.43 199 551 28 APB 9.90 PMDA 10.0 AN 0.20 98.4 0.72 212 549 29 APB 9.80 BPDA 10.0 AN 0.40 98.6 0.78 198 562 Synthetic Example Diamine (mol) Acid anhydride (mol) Capping agent (mol) Yield (%) η inh (dl/g) Tg (°C) Td 5 (°C) 30 APB 9.80 PMDA 10.0 AN 0.40 98.0 0.52 210 540 31 APB 9.60 BPDA 10.0 AN 0.80 98.5 0.49 194 560 32 APB 9.70 PMDA 10.0 AN 0.60 98.2 0.43 208 536 33 APB 9.40 BPDA 10.0 AN 1.20 98.3 0.44 191 552 34 APB/m-BP 7.92/1.98 PMDA 10.0 p-T 0.20 98.7 0.72 223 559 35 APB 9.90 PMDA 10.0 p-T 0.20 98.2 0.73 213 538 36 APB 9.80 BPDA 10.0 p-T 0.40 98.0 0.79 198 559 Synthetic Example Diamine (mol) Acid anhydride (mol) Capping agent (mol) Yield (%) η inh (dl/g) Tg (°C) Td 5 (°C) 37 APB 10.0 PMDA/BPDA 4.8/5.0 PA 0.40 98.2 0.62 208 550 38 APB 9.80 PMDA/BPDA 2.0/8.0 AN 0.40 98.4 0.70 202 556 39 APB/m-BP 8.0/2.0 PMDA/BPDA 4.8/5.0 PA 0.40 98.3 0.65 210 551 40 APB/m-BP 7.84/1.96 PMDA/BPDA 2.0/8.0 AN 0.40 98.5 0.72 204 557 Examples 1∼3 To 100 parts by weight of polyimide powder obtained in Synthetic Example 1, 40 parts by weight of the carbon fiber, HTA-C6 (Trade Mark of Toho Rayon Co.) was added and mixed with a drum blender (manufactured by Kawata Seisakusho Co.). Successively the mixture was melt kneaded at 400 °C with a single screw extruder having a bore diameter of 30 mm. Extruded strand was cooled in the air and cut into pellets. The pellets were injection molded into a tensile test specimen with an Arburg injection molding machine at the injection pressure of 500 kg/cm 2 , cylinder temperature of 410 °C and mold temperature of 180°C. The number of repeated deflection to fatigue (fatigue life) was measured on the specimen by using a partial pulsating method in accordance with JIS-K 7118. Load (exciting stress) and fatigue life are summarized in Table 6. Examples 4 ∼ 84 The same procedures as described in Example 1 were carried out by using the polyimide powder obtained in Synthetic Examples 2∼10, 13∼ 16, 19∼25, 28∼31 and 34∼36. Fatigue life was measured by using the tensile test specimens thus prepared. Results are illustrated in Table 6 ∼ 9. Examples 85∼102 The same procedures as described in Example 1 were carried out except that the polyimide powder obtained in Synthetic Examples 5∼8 was used and carbon fiber, HTA-C 6 (Toho Rayon Co.) was replaced by the glass fiber, MICROGLASS-RES (Trade Mark of Nippon Sheet Glass Co.) or the Aramide fiber, KEBLER CHOPPED STRAND K-49 (Trade Mark of E. I. Du Pont de Nemours & Co.). Fatigue life was measured by using the tensile test specimens thus prepared. Results are illustrated in Table 10. Comparative Examples 1 ∼ 6 The same procedures as described in Example 1 were carried out by using polyimide powder obtained in Synthetic Examples 11 and 12. Fatigue life was measured on the tensile test specimens thus prepared. Results are illustrated in Table 11. AS seen in the above results, polyimide of Synthetic Example 11 or 12 wherein the proportion of APB is less than 50 mol % leads to lower fatigue resistance of the resulting resin compositions. That is, fatigue life (the number of repeated deflections to fatigue) of these compositions under a certain load (exciting stress) is one order or more of magnitude shorter than that of polyimide having 50 mol % or more in APB proportion. Comparative Examples 7 ∼ 24 The same procedures as described in Example 1 were carried out by using the polyimide powder obtained in Synthetic Examples 17, 18, 26, 27, 32 and 33. Fatigue life of the tensile test specimens thus obtained was measured and results are illustrated in Table 12. As seen in the above results, the resin composition having an inherent viscosity of 0.45 dℓ /g or more has excellent fatigue resistance. On the other hand, polyimide of Synthetic Examples 17, 18, 26, 27, 32 and 33 having an inherent viscosity of less than 0.45 dℓ /g leads to lower fatigue resistance of resulting resin compositions. That is, fatigue life of these resin compositions under a certain load is one order or more of magnitude shorter than that of polyimide having an inherent viscosity of 0.45 dℓ /g or more. Examples 103 ∼ 120 The same procedures as described in Example 1 were carried out by using 100 parts by weight of the polyimide powder obtained in Synthetic Example 5 or 7 and changing the amount of fiber added. Load and fatigue life were measured on the test specimens thus obtained. Results are illustrated in Tables 13 and 14. Comparative Examples 25∼36 The same procedures as described in Examples 103 ∼ 120 were carried out by using resin compositions outside the scope of the invention. Load and fatigue life were measured on the test specimens thus obtained. Results are illustrated in Tables 13 and 14. When the amount of carbon fiber used was in the range of the invention, the resin composition exhibited excellent fatigue resistance. On the other hand, when the amount of carbon fiber was lower than the range of the invention, good fatigue resistance could not be obtained. When the amount of the carbon fiber exceeded the range of the invention, injection molding became impossible and molded articles could not be obtained. Examples 121 ∼ 132 The same procedures as described in Example 1 were carried out by using 100 parts by weight of the polyimide powder obtained in Synthetic Examples 37∼40 and changing the amount of carbon fiber added. Load and fatigue life were measured on the test specimens thus obtained. Results are illustrated in Table 15. Example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 1 1 carbon 14 26 2 1 ↑ 13 182 3 1 ↑ 12 1010 4 2 ↑ 14 28 5 2 ↑ 13 196 6 2 ↑ 12 1130 7 3 ↑ 14 34 8 3 ↑ 13 210 9 3 ↑ 12 1240 10 4 ↑ 14 42 11 4 ↑ 13 320 12 4 ↑ 12 5310 13 5 ↑ 14 27 14 5 ↑ 13 188 15 5 ↑ 12 1060 16 6 ↑ 14 30 17 6 ↑ 13 203 18 6 ↑ 12 1150 19 7 ↑ 14 35 20 7 ↑ 13 213 21 7 ↑ 12 1250 Example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 22 8 carbon 14 53 23 8 ↑ 13 320 24 8 ↑ 12 5380 25 9 ↑ 14 21 26 9 ↑ 13 100 27 9 ↑ 12 1100 28 10 ↑ 14 29 29 10 ↑ 13 185 30 10 ↑ 12 1250 31 13 ↑ 14 25 32 13 ↑ 13 176 33 13 ↑ 12 1030 34 14 ↑ 14 28 35 14 ↑ 13 192 36 14 ↑ 12 1070 37 15 ↑ 14 32 38 15 ↑ 13 204 39 15 ↑ 12 1180 40 16 ↑ 14 51 41 16 ↑ 13 351 42 16 ↑ 12 5190 Example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 43 19 carbon 14 26 44 19 ↑ 13 190 45 19 ↑ 12 1090 46 20 ↑ 14 34 47 20 ↑ 13 210 48 20 ↑ 12 1220 49 21 ↑ 14 54 50 21 ↑ 13 372 51 21 ↑ 12 5090 52 22 ↑ 14 25 53 22 ↑ 13 192 54 22 ↑ 12 1130 55 23 ↑ 14 31 56 23 ↑ 13 212 57 23 ↑ 12 1180 58 24 ↑ 14 26 59 24 ↑ 13 182 60 24 ↑ 12 1090 61 25 ↑ 14 26 62 25 ↑ 13 186 63 25 ↑ 12 1050 Example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 64 28 carbon 14 33 65 28 ↑ 13 211 66 28 ↑ 12 1240 67 29 ↑ 14 52 68 29 ↑ 13 348 69 29 ↑ 12 5160 70 30 ↑ 14 32 71 30 ↑ 13 200 72 30 ↑ 12 1190 73 31 ↑ 14 53 74 31 ↑ 13 338 75 31 ↑ 12 5020 76 34 ↑ 14 24 77 34 ↑ 13 186 78 34 ↑ 12 1050 79 35 ↑ 14 34 80 35 ↑ 13 213 81 35 ↑ 12 1230 82 36 ↑ 14 55 83 36 ↑ 13 352 84 36 ↑ 12 5260 Example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 85 5 Glass 14 25 86 5 ↑ 13 175 87 5 ↑ 12 1010 88 6 ↑ 14 28 89 6 ↑ 13 196 90 6 ↑ 12 1080 91 7 ↑ 14 32 92 7 ↑ 13 205 93 7 ↑ 12 1150 94 8 ↑ 14 49 95 8 ↑ 13 359 96 8 ↑ 12 4820 97 5 Aramide 14 31 98 5 ↑ 13 192 99 5 ↑ 12 1160 100 6 ↑ 14 31 101 6 ↑ 13 219 102 6 ↑ 12 1250 Comparative example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 1 11 Carbon 14 2.0 2 11 ↑ 13 12 3 11 ↑ 12 93 4 12 ↑ 14 2.2 5 12 ↑ 13 14 6 12 ↑ 12 95 Comparative example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 7 17 Carbon 14 2.3 8 17 ↑ 13 13 9 17 ↑ 12 98 10 18 ↑ 14 3.9 11 18 ↑ 13 26 12 18 ↑ 12 157 13 26 ↑ 14 1.2 14 26 ↑ 13 9 15 26 ↑ 12 78 16 27 ↑ 14 1.5 17 27 ↑ 13 10 18 27 ↑ 12 108 19 32 ↑ 14 2.5 20 32 ↑ 13 15 21 32 ↑ 12 94 22 33 ↑ 14 4.3 23 33 ↑ 13 32 24 33 ↑ 12 162 Example(E) or Comparative example (C.E.) Polyimide synthetic example Fiber Weight parts Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) C.E.-25 5 carbon 3 13 11 E-103 5 ↑ 10 13 152 E-104 5 ↑ 30 13 188 E-105 5 ↑ 50 13 204 C.E.-26 5 ↑ 70 13 C.E.-27 5 Glass 3 13 9 E-106 5 ↑ 10 13 148 E-107 5 ↑ 30 13 175 E-108 5 ↑ 50 13 194 C.E.-28 5 ↑ 70 13 C.E.-29 5 Aramide 3 13 12 E-109 5 ↑ 10 13 161 E-110 5 ↑ 30 13 193 E-111 5 ↑ 50 13 205 C.E.-30 5 ↑ 70 13 Example(E) or Comparative example (C.E.) Polyimide synthetic example Fiber Weight parts Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) C.E.-31 7 carbon 3 13 12 E-112 7 ↑ 10 13 195 E-113 7 ↑ 30 13 208 E-114 7 ↑ 50 13 240 C.E.-32 7 ↑ 70 13 C.E.-33 7 Glass 3 13 10 E-115 7 ↑ 10 13 183 E-116 7 ↑ 30 13 195 E-117 7 ↑ 50 13 218 C.E.-34 7 ↑ 70 13 C.E.-35 7 Aramide 3 13 13 E-118 7 ↑ 10 13 201 E-119 7 ↑ 30 13 211 E-120 7 ↑ 50 13 246 C.E.-36 7 ↑ 70 13 Example Polyimide synthetic example Fiber Fatigue resistance of injection molded article Load (kg/mm 2 ) Fatigue life (× 10 4 cycle) 121 37 Carbon 14 42 122 37 ↑ 13 294 123 37 ↑ 12 3260 124 38 ↑ 14 49 125 38 ↑ 13 338 126 38 ↑ 12 4380 127 39 ↑ 14 31 128 39 ↑ 13 220 129 39 ↑ 12 1370 130 40 ↑ 14 37 131 40 ↑ 13 293 132 40 ↑ 12 3010

Claims: A polyimide resin composition comprising 100 parts by weight of polyimide having from 0.5 (exclusive) to 1.0 (inclusive) mole ratio of recurring structural units represented by the formula (1) : and from 0 (inclusive) to 0.5 (exclusive) mole ratio of recurring structural units represented by the formula (2) : wherein X is in the formulas (1) and (2), and having an inherent viscosity of 0.45 dℓ /g or more, as measured after dissolving 0.50g of polyimide powder in 100 ml of a solvent mixture composed of p-chlorophenol and phenol in a weight ratio of 90:10 and cooling the obtained solution to 35°C; and 5∼65 parts by weight of a carbon fiber, glass fiber, aromatic polyamide fiber and/or potassium titanate fiber. A polyimide resin composition according to claim 1 wherein said polyimide is a polymer with a capped molecular chain end as obtainable by reaction of the diamine 1,3-bis(3-aminophenoxy)benzene, or a mixture of the said diamine and 4,4'-bis(4-aminophenoxy)biphenyl, with pyromellitic dianhydride and/or 3,3', 4, 4' - biphenyltetracarboxylic dianhydride in the presence of an aromatic dicarboxylic anhydride represented by the formula (3): wherein Z is a divalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or a bridge member, said aromatic dicarboxylic anhydride being used in an amount of 0.001 - 1.0 mole per mole of 1,3-bis(3-aminophenoxy)benzene or mixture thereof with 4,4'-bis(3-aminophenoxy)biphenyl, and/or an aromatic monoamine represented by the formula (4): V - N H 2 wherein V is a monovalent radical having 6∼15 carbon atoms and is a monoaromatic radical, condensed polyaromatic radical or noncondensed aromatic radical connected to each other with a direct bond or abridge member, said aromatic monoamine being used in an amount of 0.001-1.0 mole per mole of pyromellitic dianhydride and/or 3,3',4,4'-biphenyltetracarboxylic dianhydride. A polyimide resin composition according to claim 1 wherein said polyimide has recurring structural units represented by the formula (1-1) : A polyimide resin composition according to claim 2 having recurring structural units as set out in claim 3. A polyimide resin composition according to claim 1 wherein said polyimide has recurring structural units represented by the formula (1-2) : A polyimide resin composition according to claim 2, having recurring structural units as set out in claim 5. An injection molded article as obtainable from the polyimide resin composition as in any one of the preceding claims.

Inventors: IIYAMA KATSUAKI, OKAWA YUICHI, SAKATA YOSHIHIRO, TAMAI SHOJI, YAMAGUCHI AKIHIRO, YAMASHITA WATARU, IIYAMA, KATSUAKI, OKAWA, YUICHI, SAKATA, YOSHIHIRO, TAMAI, SHOJI, YAMAGUCHI, AKIHIRO, YAMASHITA, WATARU, YAMASHITA, WATARU, 311 MITSUI TOATSU KAGAKU
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1994
Main classification: C08L79
IPC codes: C08G73, C08L79