Threading tap

Abstract: A threading tap comprises a cylindrical shaft and a threading portion (2). At least the threading portion consists of a compound material comprising a core of high speed steel or tool steel and a cover of "Coronite" (registered trademark), i.e., a hard material with 30 to 70% by volume of submicronic hard materials in the form of carbides, nitrides and/or carbonitrides of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and/or W in a metallic matrix based on Fe, Co and/or Ni. The chip surfaces (13) adjacent to the cutting edges (12) of the cutting threads (9) have a negative rake angle (α). The threading tap has proven to be excellent at the threading of titanium-based alloys.

Description: The present invention relates to a threading tap for cutting threads in primarily titanium and titanium-based metal alloys, comprising an elongate shaft of a metallic compound material, which within a certain distance from its one end is provided with two or more lands preferably extending helically around the central axis of the tap, which lands on their envelope surfaces are provided with cutting threads of similar profile and which are separated by equally helically twisted chip flutes. Threads are produced by chip-cutting or plastic forming methods. Threading by threading taps belongs to the chip-cutting methods. One may use either ready taps or series taps, depending upon the hardness and cutting data of the workpiece. Using ready taps, the thread is made by one single tap while using series taps, several taps are used in sequence for obtaining a ready thread. Threading taps are normally made of high speed steel. In order to improve their function, these have sometimes been subjected to some sort of surface treatment. The most common surface treatments are steam tempering, nitration and coating with TiN. These treatments contribute to the counteracting of built-up edges, the increasing of surface hardness and wear strength and to lowering the friction. In spite of this, it has often turned out to be difficult to attain perfectly satisfactory in some difficult to machine materials. In particular in tough materials, such as titanium and titanium-based alloys, the usual threading taps of HSS have demonstrated insatisfactory tool lives. Also the quality of the thread has often been inadequate, which in first hand is caused by portions of the relatively tough material being stuck upon the threading tap, in particular at low cutting speeds. Such inconveniences are of course particularly aggravating in technical fields with so strict safety requirements as the aircraft industry. The closest prior art document GB-A-2 174 031 discloses a threading tap according to the preamble of claim 1, which has a negative rake angle of -5°. However, it does not mention the use of "Coronite" (registered trademark). Thus, a first object of the present invention is to provide a threading tap with an increased tool life in tough materials, such as titanium-based alloys, in comparison with previous threading taps. A second object of the present invention is to provide a threading tap which makes possible an efficacious threading without any material being stuck on the tap also at low cutting speeds. Another object of the present invention is to provide a threading tap that makes possible increased cutting data. A further object of the present invention is to provide a threading tap which can easily be bored away at a possible tool breakdown. These and further objects have been attained by the present invention by forming the threading tap with a negative chip angle in a compound material according to the features defined in claim 1. For illustrative but non-limiting purposes, a prefered embodiment of the invention will now be described with reference to the appended drawings, in which: Figure 1 shows a straight frontal view of the threading tap according to the invention. Figure 2 shows the cross-section II-II in Figure 1. In Fig. 1 a threading tap according to the invention is shown, a part of the uniform shaft having been cut away. At the front portion of the threading tap is the operative threading portion 2. At least this portion 2, however preferably the whole threading tap, is made of a metallic compound material which will now be further described. By the term "compound material" is meant a composite product with different materials in different parts. According to the present invention the compound material consists of a composition according to SE-C-440 753 which has been prepared by the process as described in said patent specification. Thus, the inner core of the threading tap, of a substantially circular cross-section, consists of high speed steel or tool steel, preferably of the latter. Outside this core there is a cover whose thickness normally amounts to 10 to 20%, preferably about 15%, of the diameter of the tool (however, preferably at least 0,5 mm), which cover is made of a specific hard material as described in SE-B-392 482. This hard material, normally named "Coronite" (registered trademark), consists of 30 to 70% by volume of submicronic hard materials in the form of carbides, nitrides and/or carbonitrides of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and/or W in a metallic matrix based on Fe, Co and/or Ni. Preferably, this hard material consists of 30 to 70% b.v. of hard materials of mainly TiN in a matrix of HSS-type in which the enriched hard materials have a grain size of <1 µm, preferably <0,5 µm. Preferably, the threading tap is used with at least the operative portion 2 coated, which further prolongs the tool life. By its fine grain size and good dispersion of the hard materials in the binding phase, the cover of hard material has an exceptionally good adhesion in relation to deposited, pure coatings of hard materials which have been deposited by the so called PVD process (PVD means Physical Vapour Deposition). Normally, this process gives a lesser adhesion in comparison with the more metallurgical binding that is created at the so called CVD process (CVD means Chemical Vapour Deposition). The reason for this is mainly that CVD takes place at higher temperatures. The layers being deposited are mainly based on titanium and particularly good properties have been attained with TiN, Ti(C,N) and (Ti,Al)N. Particularly fine properties have been obtained with 2 to 4 µm Ti(C,N). Returning to the geometrical shape of the tool, the rear portion of the shaft 1 is formed to be fastened in a chuck, bushing or similar. Thus, according to the illustrated embodiment, this end has been provided with four plane chamfers 3 which jointly form a substantially square cross-section with rounded corners. Shaft portion 1 with the diameter 5 transposes into the narrower, operative threading portion 2 via a step or dimension transition 4. Alternatively, the threading tap may be formed uniformly thick, without any change of diameters. The operative threading portion 2 is formed with two or more chip-conveying flutes 6, which may be straight in an axial direction, but are preferably helically twisted around the central axis 7 of the threading tap, substantially equally formed, and located substantially equidistantly. Preferably, the tool comprises between two and five such flutes, preferably three. The pitch angle of the flutes may lie between -25 and +25°, preferably between +12 and +18° at a positive pitch, and between 0 and -15° at negative (neutral at 0) pitch. Between these flutes or grooves 6 are protruding lands 8, on whose rounded, peripheric envelope surface are formed threads 9. Suitably, these correspond any of the normal standards, i.e., threads between M4 and M12. However, this is not an essential feature of the present invention and other threads may occur. At its front end, the threading tap is formed with a cutting chamfer 10, in order to easy the entering into a pre-drilled core hole in a workpiece. Suitably, the length of the cutting chamfer varies between 2 and 8 leads, inter alia depending upon whether through or bottomed holes are to be threaded. According to the illustrated embodiment, the threading tap is finished at its front end by a conical point, which however may also be disposed of. The threading tap may be threading either to the right or to the left. In Fig. 2 a left-threading tap is shown. Further, the chip-flutes may be either straight or be twisted, either in the same direction as the direction of rotation, or in the opposite direction. When the flutes are twisted in a direction opposite the direction of rotation, then the flutes become chip-driving, i.e., they convey the chips in front of the threading tap and, thereby, they diminish the risk for chip jamming at the reversion. This construction is used for threading through holes. On the other hand, if the chip-flutes are twisted in the same direction as the direction of rotation, then the chips are forced backwards and out of the hole. This embodiment is primarily suitable for holes with bottom. The toothed break line between a chip-flute and the front edge of a land, in the direction of rotation, forms the cutting edge 12. It is an essential feature of the present invention that the chip face 13 adjacent to the cutting edge is negative and has a negative rake angle α. This angle is measured between the negative chip face 13 and a radius touching the break line between said chip face and the curved surface of the chip-flute. The negative chip surface should preferably extend from the thread tops of cutting edge 12 towards the central axis of the threading tap, at least to a distance that corresponds to the depth of the thread profile, i.e., to the line 15 as may be seen in Fig. 2. The negative chip angle α may lie between -4 and -14°, suitably between -6 and -12°, and preferably between -8 and -10°. The clearance surface 14, which is situated behind each land 8 in the direction of rotation and forms an angle β with a radius that intersects a line 15 corresponding to the depth of the thread profile, is not critical for the present invention and may be varied within relatively wide limits. For instance, an angle β between -5 and +5° may be chosen, suitably between -3 and +3°. The combination of a special compound material and a negative chip geometry is characterizing for the present invention and has brought about several advantages. In particular, the threading taps according to the invention have a surprisingly long tool life at threading of cored holes in titanium and titanium-based metallic alloys, inclusively at so HIP conditions (HIP stands for High Isostatic Pressure and tells that the workpiece has been condensed at high pressure and high temperature) . The following comparative tests were made between a threading tap according to the invention and a normal threading tap of high speed steel (HSSE) with a positive rake angle: Workpiece: Titanium alloy TiAl 6 V 4 , with a tensile strength of 1150 N/mm 2 Predrilled core hole diameter: 5 mm Made thread: M6 Hole depth (hole with bottom): 12 mm Cooling liquid: cutting oil, vertically Cutting speed: HSSE: 2 m/min Threading tap according to the invention: 5 m/min Number of threaded holes with HSSE: 60 Number of threaded holes by a threaded tap according to the invention: 640 Thus, more than a tenfold increase of the number of threaded holes, and moreover, at a higher cutting speed. This results in several obvious advantages, such as decreased tool costs and shortened downtimes at tool changes. Moreover, the threading tap according to the invention cuts more neatly and without any sticking material from the workpiece, which means that the tap does not bind in the threaded hole after the threading, and that the threading tap may be reversed by hand if desired. A comparison was also made with a threading tap of the same compound material that was used in the threading tap according to the invention, but with the usual positive rake angle used in HSS taps. Tests in the same titanium alloy demonstrated that such a threading tap was broken already after a small number of holes. In those cases where only the operative threading portion 2 is made of the special compound material according to the invention, this portion can be welded upon a shaft portion 1. The shaft portion may then be made of another suitable material, such as tool steel. Thus, the threading tap according to the invention has demonstrated excellent results with increased cutting data at different applications in titanium-based alloys. Moreover, the tool has proven to be surprisingly capable also in other smeary materials, such as aluminum and aluminum-based alloys.

Claims: A threading tap consisting of an elongate, substantially cylindrical shaft (1), which within a certain distance from one of its ends is provided with two or more lands (8) which are straight or helically twisted around the central axis (7) of the threading tap, which lands are provided with cutting threads (9) of substantially equal profiles on their envelope surfaces and which are separated by straight or equally twisted chip-conveying flutes (6), the chip surfaces (13) adjacent to the cutting edges (12) of the cutting threads (9) having a negative rake angle (α), characterized in that at least the portion of the threading tap being provided with lands (8) consists of a core of high speed steel or tool steel and a cover of a hard material with 30 to 70% by volume of submicronic hard materials in the form of carbides, nitrides and/or carbonitrides of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and/or W in a metallic matrix based on Fe, Co and/or Ni, and in that said rake angle (α) is between -6 and -12°. Threading tap according to claim 1, characterized in that it is formed with 2 to 5 lands (8), preferably 3. Threading tap according to claim 1 or 2, characterized in that its outer surface at least partially is coated with a thin layer of TiN, Ti(C,N) and/or (Ti,Al)N. Use of a threading tap according to any of claims 1 to 3 for threading of holes in titanium and titanium-based metal alloys.

Inventors: GIESSLER JOSEF, VON HOLST PEDER, GIESSLER, JOSEF, VON HOLST, PEDER
Applicants: SANDVIK AB, SANDVIK AKTIEBOLAG
Application year: 1994
Main classification: B23G5
IPC codes: B23G5