Polysaccharides bonded to a porous carrier, process for preparing them and their use

Abstract: A novel substance having a main structure represented by the following Formula: Also disclosed are a method of producing the substance in which an oligosaccharide having a degree of polymerization from 3 to 10 is chemically bonded to a silane agent at the reducing terminal of the oligosaccharide, the oligosaccharide derivative obtained is polymerized to an average degree of polymerization from about 11 to about 500 with the action of an enzyme; and a method in which the aldehyde group present at the reducing terminal of an oligosaccharide having a degree of polymerization from 3 to 10 is oxidized with an oxidizing agent, and the saccharide chain of the oxidized product is polymerized to a degree of polymerization from about 11 to about 500 by the action of an enzyme, followed by the addition of an acid. The substance is excellent in solvent resistance and useful as a separating agent for chromatography, in particular, for the separation of chiral compounds.

Description: The present invention relates to novel substances, methods of producing them and use of them. More particularly, it relates to novel substances in which a polysaccharide is chemically bonded to silica gel at its reducing terminal alone and in which part or all of the hydroxyl groups in the polysaccharide moiety are substituted with a particular substituent, as well as to methods of producing them and to a separating agent for use in chromatography containing the same. It has hitherto been known that a substance consisting of silica gel physically carrying a polysaccharide, such as cellulose, amylose or a derivative thereof, is useful as a separating agent for separating chiral compounds, in particular, as a separating agent for optical resolution. However, due to its poor solvent resistance, the substance suffers from the drawback that usable eluents are limited at the time when it is to be used in liquid chromatography, or the like. In addition, it is not possible to fully utilize the usefulness of the polysaccharide. There is also a limitation in solvents usable for the washing of contaminated columns, which can be a cause for the deterioration of columns. In order to solve such problems, it has been proposed to use a compound in which a polysaccharide is chemically bonded to silica gel. However, in this case, it is not possible to select the site at which the chemical bonding to silica gel takes place. This exerts influences on the higher structure of the polysaccharide per se and the usefulness of the polysaccharide is diminished. In addition, there occurs still another problem that the silica gel compound thus obtained shows a big difference in quality since the bonding does not take place at a specific site. Manssur Yalpani, Selective Chemical Modifications of Dextran, pages 1395 to 1405 in Journal of Polymer Science, vol. 23, Number 5, May 1985 mentions the specific modification of the reducing end group of dextran achieved by using the reductive amination procedure and solvent systems designed to optimize polymer reactivity. These end-group modifications afford chemically stable amine derivatives of known composition and structure without attendant ring-cleavage and other polymer degradation reactions. Thus, it is the object of the present invention to overcome above disadvantages of the prior art. This object has been achieved by the provision of a certain separating agent of the structure wherein silica gel is used as a porous carrier and polysaccharides are chemically bonded to the inner and outer surfaces of the pores of the silica gel at the reducing terminals of the polysaccharides. The reducing terminals of oligosaccharides have been lactonized and a reaction of the lactonized product performed with, for example, 3-aminopropyltriethoxysilane, to obtain a product containing a saccharide chain chemically bonded via an amide bond to a silane agent, as shown by the following Formula A: (wherein Rb represents a substituted or unsubstituted methylene group, a substituted or unsubstituted phenylene group or a group containing covalently bonded hetero atom(s); m 2 represents an integer of from 1 to 20; m 3 represents an integer of from 2 to 9; and n represents an integer of from 0 to 3, preferably 0. Part of the silane agents may be in a polymerized state). It has also been developed a method of polymerizing saccharide chains and succeeded, by using the method, in polymerizing the saccharide moieties of the compound represented by Formula A to an arbitrary polymerization degree by an enzymatic reaction using the compound as a primer. Further, the inventors have succeeded in obtaining compounds represented by Formula B set forth below, by allowing a polysaccharide derivative of a silane agent obtained by an enzymatic synthesis to bind to silica gel at the silane moiety. (wherein Z represents a member selected from the surface of a porous carrier, a halogen atom, an alkyl group, an alkoxy group, a phenyl group, a silane agent and a saccharide-bonded silane agent; m 1 represents the number of monosaccharide units, which may be in the range of from 10 to 500 on average; and Rb and m 2 have the same meanings as defined above). The compounds represented by Formula (1) according to the invention have been obtained by substituting part or whole of the hydroxy groups in the saccharide moiety of the compound represented by Formula B with, for example, an isocyanate derivative, or the like. Alternatively, the compounds represented by the above Formula B have been obtained in the following manner: The reducing terminal of an oligosaccharide is oxidized to a glucanate, and its saccharide moiety is polymerized to an arbitrary degree of polymerization with the action of an enzyme using the glucanate as a primer. An acid is added to the resulting reaction mixture to effect lactonization. The lactonized polysaccharide is then allowed to bond via amide bond to a surface-treated silica gel having amino groups on its surface. The compounds represented by the above Formula (1) have also been obtained by substituting part or whole of the hydroxyl groups in the saccharide moiety of the compounds of Formula B obtained as above with, for example, an isocyanate derivative, or the like. In the thus synthesized compounds of Formula (1), saccharides are chemically bonded via a silane agent to the inner and outer surface of the pores of a porous carrier, such as silica gel, only at the 1-positioned carbon in the reducing terminal of the saccharide moiety. It has been found that the compounds are capable of solving the above-mentioned problems, and the present invention has been completed on the basis of the finding. Accordingly, there is provided in accordance with the present invention a method for producing a substance having a main structure of the following Formula (1) in which a polysaccharide or a derivative thereof is chemically bonded to the inner and outer surfaces of a porous carrier at the reducing terminal of said polysaccharide or derivative thereof. [wherein R represents Ra, -CO-Ra or -CO-NH-Ra (in which Ra represents a hydrogen atom or a substituent selected from a substituted or unsubstituted alkyl group, a substituted or unsubstituted phenyl group and a substituted or unsubstituted heterocyclic residue); on the point of improving separation ability remarkably, substitution rate of R is preferably 30 to 100%. Rb represents a substituted or unsubstituted methylene group, a substituted or unsubstituted phenylene group or a group containing covalently bonded hetero atom(s); Z represents a member selected from the surface of a porous carrier, a halogen atom, an alkyl group, an alkoxy group, a phenyl group, a silane agent and a saccharide-bonded silane agent; m 1 represents the number of monosaccharide units, which may be in the range of from 10 to 500 on average; and m 2 represents an integer of from 1 to 20], in which an oligosaccharide having a degree of polymerization from 3 to 10 is chemically bonded to a silane agent at the reducing terminal of the oligosaccharide, the oligosaccharide derivative obtained is extended to an average degree of polymerization from about 11 to about 500 by the action of an enzyme, and then the resulting polysaccharide is chemically bonded to a porous carrier at the silane moiety present at the terminal of the polysaccharide; a method of producing the substance of the above Formula (1) in which the aldehyde group present at the reducing terminal of an oligosaccharide having a degree of polymerization from 3 to 10 is oxidized with an oxidizing agent, and the saccharide chain of the oxidized product is polymerized to a degree of polymerization about 11 to about 500 by the action of an enzyme, followed by the addition of an acid; and a separating agent for separating chiral compounds comprising the substance represented by Formula (1). Fig. 1 is an IR spectrum of {o-α-D-glucopyranosil-(1→4)} 4 -D-gluconolacton (which may hereinafter be referred to as lactone) obtained in Production Example 1 . Fig. 2 is an IR spectrum of a compound represented by Formula A 1 . Fig. 3 is an IR spectrum of oligosaccaride tris(4-methylphenyl carbamate) derivative obtained in Production Example 2 . Fig. 4 is an IR spectrum of a compound represented by Formula (2). Any oligosaccharide can be used in the present invention, including synthetic oligosaccharides, naturally-occurring oligosaccharides and derivatives thereof, provided that a polysaccharide can be synthesized by using the oligosaccharide as a substrate in an enzymatic synthesis. Specific examples of usable oligosaccharides include α-1,4-glucan oligomers (maltooligosaccharides), β-1,4-glucan oligomers (cellooligosaccharides), α-1,6-glucan oligosaccharides (isomaltooligosac charides), β-1,6-glucan oligomers (gentiooligosaccharides), α-1,3-glucan oligomers (nigerooligosaccharides), β-1,3-glucan oligomers (laminalioligosaccharidesα-1,2-glucan oligomers, β-1,2-glucan oligomers (sophorooligosaccharides), β-1,4-chitooligosaccharides, β-1, 4-N-acetylchitooligosaccharides, β-1,4-galactans (lactooligosaccharide s), α-1,6-galactans (melioligosaccharides), β-2,1-fructans (inulooligosaccharides), β-2,6-fructans, β-1,4-xylans, β-1,3-xylans, β-1,4-mannans, α-1,6-mannans, and the like. These oligosaccharides have a number average degree of polymerization 3 or more, and there is no particular upper limit on the degree of polymerization. However, a degree of polymerization 3 to 10 can be preferred with regard to reactivity upon lactonization or reductive amination, and to easiness of handling. Examples of enzymes usable in the invention include hydrolases, saccharide transferases, polymerases, and the like. Any enzyme capable of synthesizing a polysaccharide from an oligosaccharide can be used, and microorganisms containing such an enzyme can also be used. Specific examples include phosphorylase, dextransucrase, levansucrase, pullulanase, and microorganisms capable of producing these enzymes. The polysaccharides have a mean degree of polymerization 11 or more. Although there is no particular upper limit, a mean degree of polymerization 500 or less is usually preferred. Specific examples of usable porous carriers include porous inorganic carriers, such as silica gel, diatomaceous earth, porous glass, hydroxyapatite, alumina, titanium oxide, magnesia, etc.. Of these carriers, silica gel is particularly preferred. Silica gel may have a particle size of from 1 to 1,000 µm, preferably from 2 to 100 µm, and a mean pore size from 10Å to 100 µm, preferably from 2 nm to 500 nm. When a porous membrane is used as the porous carrier, it is possible to obtain a novel separating membrane. As the silane agent is used an amino group-containing compound. In cases where the reducing terminals are lactonated or are reduced in the presence of a reducing agent to effect amination, a primary amine-containing silane agent can be preferred. Any commercially available silane coupling reagents and synthetic silane agents modified to have amine(s) can be used as the silane agent. It is also possible to employ a spacer capable of bonding a silane agent and a polysaccharide, such as a compound having two or more functional groups of either the same or different kinds, one functional group of said compound being capable of forming a chemical bond with the reducing terminal of a saccharide and the other (or another) functional group of said compound being capable of forming a chemical bond with a silane agent. Examples of such functional groups include vinyl, amino, hydroxyl, carboxyl, aldehyde, isocyanate, isothiocyanate, thiol, silanol, epoxy, ether, ester and amide groups, as well as halogen atoms. Any silane agents capable of bonding to these functional groups can be used. Typical examples of silane agents are set forth below. In the above Formula (1), Rb represents a substituted or unsubstituted methylene group, a substituted or unsubstituted phenylene group or a group containing covalently bonded hetero atom(s). Typically, Rb corresponds to part of side chains of silane agents, such as those set forth below, or to part of a moiety formed by chemical bonding between a spacer and a silane agent. [Formula 12] (H O - R 2 )n 1 - S i X(4-n 1 ) [Formula 13] (Y - R 2 )n 1 - S i X(4-n 1 ) [Formula 14] (H S - R 2 )n 1 - S i X(4-n 1 ) [Formula 15] (C O N -R 2 )n 1 - S i X(4-n 1 ) [Formula 17] (S C N - R 2 )n 1 - S i X(4-n 1 ) In the above formulae, n 1 represents an integer of from 1 to 3; R 1 represents a hydrogen atom, an alkyl chain having from 1 to about 20 carbon atoms or a derivative thereof; R 2 represents an alkyl chain having from 1 to about 20 carbon atoms or a derivative thereof; X represents a substituted or unsubstituted alkoxy group having from 1 to 10 carbon atoms, a halogen atom (preferably chlorine atom), a hydroxyl group or a substituted or unsubstituted phenoxy group, at least one X being a substituted or unsubstituted alkoxy group, a halogen atom , a hydroxyl group and a substituted or unsubstituted phenoxy group; and Y represents a halogen atom. The substituent R introduced into part or all of the hydroxyl groups in the polysaccharide moiety of the compounds represented by the above Formula (1) is to modify the hydroxyl groups. Two or more substituents of different kinds may be introduced into the hydroxyl groups of one polysaccharide moiety. Ra of the substituent R is selected from substituted or unsubstituted alkyl groups, substituted or unsubstituted phenyl groups and substituted or unsubstituted heterocyclic residues. Specific examples of substituents Ra include methyl, ethyl, propyl, t-butyl, phenyl, methylphenyl, dimethylphenyl, ethylphenyl, diethylphenyl, trimethylsilylphenyl, alkoxyphenyl, dialkoxyphenyl, halogenated phenyl, dihalogenated phenyl, phenylazophenyl, naphthyl, anthryl, pyridyl and furyl groups. Methods of producing compounds in which a silane agent is chemically bonded to an oligosaccharide (hereinafter referred to as Compound A or A') will be explained hereinbelow, taking maltopentose as an example of oligosaccharide. A KOH-methanol solution is added to an iodine-methanol solution of maltopentose to obtain potassium {O-α-D-glucopyranosyl-(1→4)} 4 -D-glucanate. The potassium ion of the glucanate is exchanged with a hydrogen ion by a known method using an ion exchange resin (H-type) to obtain (O-α-D-glucopyranosyl-(1→4)} 4 -D-glucono-1,5-lactone. The lactone is then reacted, for example, with 3-aminopropyltriethoxysilane in ethylene glycol to obtain a desired compound (Compound A). This reaction is based on the process described in Polymer Journal, Vol. 17, No. 4, p. 567-575 (1985). It is necessary to use anhydrous ethylene glycol and to perform the reaction in a nitrogen stream, so that the reaction could proceed under a moisture free condition. Alternatively, the reducing terminal of the oligosaccharide is reacted with a primary amine, for example, 3-aminopropyltriethoxysilane, to form a Schiff's base. It is then reduced to a secondary amine in the presence of a reducing agent to obtain a desired compound (Compound A') [See Elizabeth Kallin, Glycoconjugate J. (1986), 3, 311-319]. Methods of producing compounds of Formula Bs of the present invention will be explained hereinbelow. (wherein Z represents a member selected from the surface of a porous carrier, a halogen atom, an alkyl group, an alkoxy group, a phenyl group, a silane agent and a saccharide-bonded silane agent; m 3 represents the number of monosaccharide units, which may be in the range from 2 to 9 on average; and Rb and m 2 have the same meanings as defined above). (1) Compound A obtained as above is reacted, for example, with 4-methylphenyl isocyanate in a mixture of dimethylacetamide and pyridine to substitute all or part of the hydroxyl groups of the oligosaccharide. This reaction can be carried out according to a known method. The resulting compound is then chemically bonded to silica gel according to a known silane-treating method, to obtain Compound Bs. (2) Alternatively, Compound A is chemically bonded to silica gel by a known silane-treating method. The resulting compound is then reacted, for example, with 4-methylphenyl isocyanate in a mixture of dimethylacetamide and pyridine to effect substitution of all or part of the hydroxy groups of the oligosaccharide. In the present invention, any of the above methods (1) and (2) can be employed. In the case where the amount of compounds bonded to silica gel is to be increased, method (2) can be preferred. The amount of compound A or A' bonded to silica gel is preferably from 5 to 50% by weight, based on the weight of silica gel. However, the amount is not necessarily limited to the above range. The thus obtained Compound Bs can be subjected to an end capping treatment according to a known method, so as to remove the influence of remaining silanol groups. The introduction of the above substituents into the hydroxyl groups in the saccharide moieties of compounds represented by Formula Bs can be effected by any known method. Methods of producing the compounds of Formula (1) of the present invention will be illustrated hereinbelow. Process 1 Reaction (1): A method of synthesizing compounds represented by Formula A and Formula A' set forth below will be illustrated. (wherein Rb, m 2 , m 3 and n have the same meanings as defined above). Compounds represented by the above Formula A can be synthesized by lactonizing an oligosaccharide and then forming an amide bond with a silane agent, for example, by referring to the description of Japanese Patent Application JP-A-06-206895. In this case, the reaction is preferably carried out under a moisture free condition since polymerization between silane agents takes place if water is present in the reaction mixture. Chemical bonding between oligosaccharides and silane agents can also be formed by allowing an oligosaccharide to chemically bond to an amino group-containing silane agent in the presence of a reducing agent, without lactonizing the reducing terminal of the oligosaccharide [production of compounds represented by Formula A'. In the formula, n represents an integer of 0 to 3, preferably 0 (part of the silane agents may be polymerized up to a number of n), and m 3 represents an integer of 2 to 9] [see Elizabeth Kallin et al., Glycoconjugate J., 3, 311-319 (1986)]. Examples of reducing agents usable in the above production include borane compounds, such as NaBH 4 , NaBH 3 CN, borane-pyridine complex, borane-dimethylamine complex, borane trimethylamine, and the like. It is also possible to be chemically bonded to a silane agent via a spacer at the reducing terminal of the saccharide. That is to say, the reducing terminal of a saccharide can be subjected to amide bonding or reductive amination with one functional group (for example, an amino group) contained in the spacer, and then the spacer can be chemically bonded with a silane agent. Reaction (2): A method of enzymatically synthesizing the saccharide moiety of compounds of Formula A or A' obtained in (1) will then be illustrated. In cases where the saccharide chain of the compounds of Formula A or A' prepared by using maltooligosaccharides having 4 or more saccharide units is enzymatically synthesized, phosphorylase can be used as an enzyme. For example, phosphorylase derived from potato can be used [see Starch Chemistry, Vol. 36, No. 4, p. 257-264 (1989)]. The enzymatic synthesis can be conducted at a temperature of from room temperature to 55°C, preferably 35 to 45°C in sterilized water or in malate buffer, etc. by using a compound represented by Formula A or A', phosphorylase (enzyme) and potassium salt of glucose-1-phosphate (substrate) [pH 5 to 8, preferably 6 to 7. The pH is adjusted with hydrochloric acid, potassium hydroxide, or the like. It can be preferred, for the prevention of polysaccharide degradation, to add 10 to 30% (W/W) of dimethylsulfoxide (DMSO) in cases where a compound having a mean degree of polymerization 30 or more is to be synthesized]. The mean degree of polymerization (m 1 ) can be determined by measuring phosphoric acid liberated from glucose-1-phosphate, or an approximate value can be obtained from a standard curve of the GPC, using a commercially available amylose (produced and marketed by Nakano Vineger Co., Ltd.). The reaction is stopped by deactivating the enzyme at an arbitrary degree of polymerization (m 1 ). The polysaccharide derivatives are precipitated in ethanol, washed with ether, hexane, etc. and dried under reduced pressure, to obtain compounds represented by the following Formula C or C': (wherein Rb and m 1 have the same meanings as above; and n is an integer of from 0 to 3, preferably 3. Part of the ethoxy groups may be eliminated during the enzymatic synthesis). (wherein Rb, m 1 and n have the same meanings as above). Reaction (3): The bonding between a compound of Formula C or C' obtained in Reaction (2) and silica gel will be illustrated. A compound represented by Formula C or C' is dissolved into anhydrous DMSO, anhydrous LiCl-DMA solution, or the like. Pyridine as a catalyst is added thereto, and the compound is bonded to silica gel at the silane moiety of the compound by a conventional silane-treating method, to obtain a compound represented by the following Formula B or B': (wherein Rb, Z, m 1 and m 2 have the same meanings as defined above). Process 2 Reaction (1): Production of a polysaccharide derivative having a lactonized reducing terminal (which may hereinafter be referred to as lactonized polysaccharide) will be illustrated. The oligosaccharide chain of a glucanate salt obtained by oxidizing the reducing terminal of an oligosaccharide [Japanese Patent Application No. H4-311,042 (311,042/1992)] is polymerized by enzymatic synthesis, and the reducing terminal is then lactonized. For example, when a maltooligosaccharide is used as an oligosaccharide, the enzymatic synthesis is carried out at a temperature of from room temperature to 55 °C, preferably 35 to 45°C in sterilized water or in malate buffer, etc., using a glucanate solution obtained by the oxidation of the reducing terminal as a primer, phosphorylase as an enzyme, and potassium salt of glucose-1-phosphate as a substrate. [pH 5 to 8, preferably 6 to 7. The pH is adjusted with hydrochloric acid, potassium hydroxide, or the like. It can be preferred, for the prevention of polysaccharide degradation, to add 10 to 30% (W/W) of dimethylsulfoxide (DMSO) when a compound having a mean degree of polymerization 30 or more is to be synthesized]. The mean degree of polymerization (m 1 ) can be determined by measuring phosphoric acid liberated from glucose-1-phosphate, or an approximate value can be obtained from a standard curve of the GPC, using commercially available amylose (produced and marketed by Nakano Vineger Co., Ltd.). The reaction is stopped by inactivating the enzyme at an arbitrary degree of polymerization (m 1 ). Thereafter, the terminal of the resulting polysaccharide is lactonized by reducing its pH to 0 to 4, preferably 1 to 2 with the addition of a strong acid, such as hydrochloric acid, or the like. The polysaccharide derivative is precipitated in ethanol, washed with ether, hexane, etc. and then dried under reduced pressure, to obtain amylose having a lactonized reducing terminal (which may hereinafter be referred to as lactonized amylose). After a lactonized polysaccharide has been obtained, it can be bonded to the amino group of a spacer by forming an amide bond. It is also possible to carry out the enzymatic synthesis after the reducing terminal of an oligosaccharide has been lactonized and a spacer has been attached thereto. Reaction (2): Bonding between a lactonized polysaccharide and a surface-treated silica gel will be illustrated. Any conventional method can be used for the treatment of inner and outer surfaces of the pores of silica gel with a silane agent having an amino group, such as 3-aminopropyl-triethoxysilane. The lactonized polysaccharide obtained in the above Reaction (1) is dissolved into a solvent, such as DMSO, and an amide bond is formed by allowing the lactonized polysaccharide to react with an amino group functionalized silica gel at 50 to 70°C. Then, excess lactonized polysaccharide is removed by washing with DMSO, acetone, hexane or the like, and the reaction product is dried under reduced pressure to obtain a compound represented by the above-mentioned Formula B. In cases where a polysaccharide bonded with a spacer as mentioned in Reaction (1) is used, the surface of silica gel can be treated with (a) a silane agent capable of bonding with the spacer, or (b) a derivative of a silane agent modified to acquire the capability of bonding with the spacer. Process 3 The hydroxyl groups in the saccharide moieties of the compounds of Formula B or B' obtained by the above-described Process 1 or 2 are reacted, for example, with 4-methylphenyl isocyanate or 3,5-dimethylphenyl isocyanate or 3,5-dichlorophenyl isocyanate or phenyl isocyanate in an anhydrous DMA/pyridine solution or anhydrous DMSO/pyridine solution, to substitute all or part of the hydroxyl groups in the saccharide moieties of the compounds. This reaction can be performed according to a known method. There are no particular limitations on the amount of polysaccharide derivatives chemically bonded to silica gel. However, the amount of from 5 to 50% by weight is usually preferred. The thus obtainable compounds of the present invention can be subjected to an end capping treatment according to a known method, so as to remove the influence of remaining silanol groups and to improve their properties as a separating agent. In illustrating the chemical structures of the compounds according to the present invention, part of the structures indicating the positions of hydroxyl groups in saccharide moieties or the like is partly omitted or simplified for convenience' sake and to meet the universality of the compounds. EXAMPLES The present invention will be explained in more detail by means of examples. Production Example 1 Synthesis of Compound A 1 (m 3 =4 in Compound A) Into 30 ml of methanol was dissolved 4.0 g of iodine, and a solution prepared by dissolving 6 g of maltopentose into an appropriate quantity of distilled water was added thereto. Then, 100 ml of 4% KOH-methanol solution was dropped thereto, and the resulting mixture was stirred at 40°C for 30 minutes. The reaction mixture was cooled on an ice bath to form precipitate, which was then collected by filtration and dissolved into 100 ml of distilled water. Subsequently, powder of activated carbon was added thereto to remove excess iodine, the resulting mixture was subjected to filtration, and the filtrate was freeze-dried. The freeze-dried product was dissolved into 40 ml of distilled water and was treated with 80 mg-eq. of Amberlite 120-B (H-type). After being concentrated, the product was again freeze-dried to obtain 5.2 g of lactone. The product was identified by the C=O stretching vibration of lactone at 1,740 cm -1 in its IR spectrum shown in Fig. 1 and a signal of 170.8 ppm in its 13 C-NMR. Into 7 ml of anhydrous ethylene glycol was dissolved 1 g of the thus obtained lactone. To this was added 0.55 g of 3-aminopropyltrieth oxy-silane, and reaction was allowed to proceed at 70°C for 6 hours in a nitrogen stream. The product was precipitated in 200 ml of acetone, washed with 100 ml of acetone and dried under reduced pressure at 60°C for 3 hours, to obtain 1.08 g of Compound A 1 . The compound shows a peak of N-H deformation vibration of secondary acid amide at 1,540 cm -1 and a peak of C=O stretching vibration at 1, 640 cm -1 in its IR spectrum (Fig. 2). In 13 C-NMR, the compound shows a chemical shift of the carbon used for the amide bond at around 172 ppm, and a signal of the 6-position carbon shifted to lower magnetic field due to the opening of the terminal saccharide ring at around 62.7 ppm. These data show that the resultant compound has a structure shown by the above-described Compound A 1 . Production Example 2 Synthesis of Compound Bs 1 (wherein Z represents a member selected from the group consisting of the surface of a porous carrier, an alkoxy group, a silane agent and a saccharide-bonded silane agent; m 3 represents the number of monosaccharide units, which may be 4; and Rb represents methylene, m 2 represents 3 and R represents a hydrogen atom or Formula 27). Into a mixture of 20 ml of DMA and 5 ml of pyridine was dissolved 0.9 g of Compound A 1 synthesized in Production Example 1. To this was added 4 g of 4-methylphenyl isocyanate. After the resulting mixture had been stirred at 80°C for 5 hours, the presence of excess 4-methylphenyl isocyanate in the reaction mixture was confirmed by the C=N stretching vibration at 2,270 cm -1 in its IR spectrum. Part of the reaction mixture was taken out as a sample and was added to aqueous 70% methanol solution to form precipitate, which was then washed and dried. The IR spectrum of the precipitate showed an absorption of C=O of the secondary carbamic acid ester at 1,710 cm -1 (Fig. 3). Meanwhile, the rest of the above reaction mixture was added to 3 g of previously activated silica gel (produced by YMC Co. ; mean pore diameter, 120Å; mean particle size, 5 µm), and reaction was allowed to proceed at 90°C for 12 hours. The resultant silane-treated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane to remove the excess carbamate derivative of Compound A 1 not bonded to the silica gel, and then dried in vacuum at 60°C for 2 hours. The thus obtained compound was subjected to IR spectrometry and elementary analysis. Results of the elementary analysis are shown in Table 1. Separating Agent Elementary Analysis C (%) H (%) N (%) Bs 1 3.28 1.03 0.26 Bs 2 13.99 2.52 1.16 Bs 3 26.14 2.71 2.93 The IR spectrum showed a peak of stretching vibration of carbonyl group at 1,710 cm -1 , which proves the existence of polysaccharide derivatives on silica surface. Thus the compound Bs 1 was obtained. In order to improve the properties of the thus obtained Compound Bs 1 as a separating agent for chromatography, the compound was subjected to a conventional end capping treatment with trimethylchlorosilane. The resulting product was collected by filtration with a G4 glass filter and was washed with tetrahydrofuran, methanol, acetone and hexane, and then dried in vacuum at 60°C for 2 hours, to obtain a product to be used as a separating agent for chromatography. Production Example 3 Synthesis of Compound A 2 (m 3 =4 in Compound A) Into 30 ml of methanol was dissolved 4.0 g of iodine. To this was added a solution prepared by dissolving 6 g of maltopentose into an appropriate quantity of distilled water. Then, 100 ml of 4% KOH-methanol solution was dropped thereto, and the resulting mixture was stirred at 40°C for 30 minutes. The reaction mixture was cooled on an ice bath to form precipitate, which was then collected by filtration and dissolved into 100 ml of distilled water. Subsequently, powder of activated carbon was added thereto to to remove excess iodine, the resulting mixture was subjected to filtration, and the filtrate was freeze-dried. The freeze-dried product was dissolved into 40 ml of distilled water and treated with 80 mg-eq. of Amberlite 120-B (H-type). After being concentrated, the product was freeze-dried to obtain 5.2 g of lactone. The product was identified by its IR spectrum which showed a peak of C=O stretching vibration of lactone at 1,740 cm -1 as in Fig. 1, as well as by its 13 C-NMR spectrum which showed a signal at 170.8 ppm. Into 4.4 ml of anhydrous DMSO (dimethylsulfoxide) was dissolved 0.7 g of the thus obtained lactone. To this was added 0.25 g of 3-aminopropyltriethoxysilane, and reaction was allowed to proceed at 70°C for 6 hours in a nitrogen stream. Part of the product (about 0.6 ml) was taken out and used as a sample for IR and NMR analyses. In its IR spectrum obtained as in Production Example 1, the product showed a peak of N-H deformation vibration of secondary acid amide at 1,540 cm -1 and a peak of C=O stretching vibration at 1,640 cm -1 . In 13 C-NMR, the product showed a chemical shift of the carbon used for the amide bond at around 172 ppm, and a signal of the 6-position carbon shifted to lower magnetic field due to the opening of the terminal saccharide ring at around 62.7 ppm. These data show that the resultant compound has a structure shown by the above-described compound A 2 . The rest of the reaction mixture was used as it is in the following Production Example 4. Production Example 4 Synthesis of Compound Bs 2 (wherein Z represents a member selected from the group consisting of the surface of a porous carrier, an alkoxy group, a silane agent and a saccharide-bonded silane agent; m 3 represents the number of monosaccharide units, which may be 4; and Rb represents methylene, m 2 represents 3 and R represents a hydrogen atom or Formula 27). The reaction mixture obtained in Production Example 3 was added to 3 g of previously activated (by means of vacuum drying at 180°C for 2 hours) silica gel (produced by YMC Co. ; mean pore diameter, 120Å ; mean particle size, 5 µm). To this were additionally added 9.6 ml of DMSO and 4 ml of pyridine, and reaction was allowed to proceed at 90°C for 12 hours. To the resulting reaction mixture was added 4 ml of 4-methylphenyl isocyanate. After 5 hours of stirring at 80°C the presence of excess isocyanate groups remaining in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The resultant silane-treated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane to remove excess Compound A 2 , and then dried in vacuum at 60 °C for 2 hours. The thus obtained compound was subjected to IR spectrometry and elementary analysis. Results of the elementary analysis are shown in Table 1. Its IR spectrum showed a peak of stretching vibration of carbonyl group at 1,710 cm -1 , which proves the existence of polysaccharide derivatives on silica surface. Thus Compound Bs 2 was obtained. In order to improve the properties of the thus obtained Compound Bs 2 as a separating agent for chromatography, the compound was subjected to a conventional end capping treatment with trimethylchlorosilane. The resulting product was filtered with a G4 glass filter, and the residue was washed as above with tetrahydrofuran, methanol, acetone and hexane, and then dried at reduced pressure at 60°C for 2 hours, to obtain a product to he used as a separating agent for chromatography. The chiral resolution ability of the compound was investigated as a separating agent for various racemic compounds. Results obtained are shown in Table 2. Production Example 5 Synthesis of Compound A 3 (m 3 =4 in Compound A) Into 4.4 ml of anhydrous ethylene glycol was dissolved 0.7 g of the lactone obtained in Production Example 3. To this was added 0.25 g of 3-aminopropyltriethoxysilane, and reaction was allowed to proceed at 70 °C for 6 hours in a nitrogen stream. Part of the product (about 0.6 ml) was taken out and used as a sample for IR and NMR analysis. In its IR spectrum obtained as in Production Example 1, the product showed a peak of N-H deformation vibration of secondary acid amide at 1,540 cm -1 and a peak of C=O stretching vibration at 1,640 cm -1 . In 13 C-NMR, the product showed a chemical shift of the carbon used for the amide bond at around 172 ppm, and a signal of the 6-position carbon shifted to lower magnetic field due to the opening of the terminal saccharide ring at around 62.7 ppm. The structure of Compound A 3 can be estimated on the basis of these data. The rest of the reaction mixture was used as it is in the following Production Example 6. Production Example 6 Synthesis of Compound Bs 3 (wherein Z represents a member selected from the group consisting of the surface of a porous carrier, an alkoxy group, a silane agent and a saccharide-bonded silane agent; m 3 represents the number of monosaccharide units, which may be 4; and Rb represents methylene, m 2 represents 3 and R represents a hydrogen atom or Formula 30). The reaction mixture obtained in Production Example 5 was added to 3 g of previously activated (by means of vacuum drying at 180°C for 2 hours) silica gel (produced by YMC Co. ; mean pore diameter, 120Å mean particle size, 5 µm). To this were additionally added 9.6 ml of anhydrous ethylene glycol and 4 ml of pyridine, and reaction was allowed to proceed at 90°C for 12 hours. The surface-treated silica gel obtained was collected by filtration with a G4 glass filter, washed with DMF, etc., and then dried in vacuum at 70°C for 3 hours. To 3.7 g of surface-treated silica gel obtained were added 13 ml of DMA and 3 ml of pyridine. Then, 3.7 g of 3,5-dimethylphenyl isocyanate was added thereto and reacted at 80°C for 12 hours. The presence of excess isocyanate groups remaining in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The resultant surface-treated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, ace tone and hexane, and then subjected to IR spectrometry and elementary analysis. Results of the elementary analysis are shown in Table 1. The compound shows a peak of carbonyl stretching vibration at 1,710 cm -1 in its IR spectrum, which proves the existence of polysaccharide derivatives on silica surface. Thus compound Bs 3 was obtained. In order to improve the properties of the thus obtained Compound Bs 3 as a separating agent for chromatography, the compound was subjected to a conventional end capping treatment with trimethylchlorosilane. The resulting product was collected by filtration with a G4 glass filter and the residue was washed as above with tetrahydrofuran, methanol, acetone and hexane, and then dried in vacuum at 60°C for 2 hours, to obtain a product to be used as a separating agent for chromatography. The chiral resolution ability of the compound was investigated as a separating agent for various racemic compounds. Results obtained are shown in Table 2. 3,5-Dimethylphenyl isocyanate used above can be readily obtained from 3,5-dimethylaniline by using phosgene, triphosgene, or the like. Example 1 (1-1) Synthesis of Compound A 1 of the Following Formula (wherein n has the same meaning as defined above). Compound A 1 was synthesized according to the method described in Japanese Patent Application No. H4-311,042 (311,042/1992), by using 5 g of maltopentose. A peak of N-H deformation vibration of secondary amide is observed at 1,540 cm -1 and a peak of C=O stretching vibration is observed at 1, 640 cm -1 in the IR spectrum of Compound A 1 shown in Fig. 2. In 13 C-NMR [solvent, DMSO-d6; concentration of Compound A 1 , 5%(W/V); standard substance, TMS; 60°C ; 400 MHz], and a peak assignable to carbons in the amide bonds is observed at 172 ppm, peaks assignable to 4- and 6-positioned carbons of open saccharide rings are observed at 82.7 ppm and 62.8 ppm, respectively, peaks assignable to ethoxy carbons in silane moieties are observed at 18.1 ppm and 57.7 ppm, and the peak assignable to the 3-position carbon of the propyl group is shifted to higher magnetic field of 41.0 ppm. These data indicate that the main structure of Compound A 1 is the same as that of Compound A described hereinabove. (1-2) Synthesis of Compound C 1 of the Following Formula; (wherein n has the same meaning as defined above. Mean degree of polymerization (m 4 ) of the compound based on the determination of phosphate = 19). Into 300 ml of sterilized ultra pure water were dissolved 1.2 g of Compound A 1 synthesized in (1-1) above and 12 g of glucose-1-phosphate (GIP) (pH was adjusted to 6). To this was added 180 units of crude phosphorylase derived from potato, and the resulting mixture was allowed to stand at 30°C for about 3 hours. The degree of polymerization of the saccharide chain was followed by sampling part of the reaction mixture and, after deactivating the enzyme with trichloroacetic acid, determining the amount of liberated phosphate by the Fiske-Subbarow method. After the enzyme had been inactivated by heating on a hot water bath, the reaction mixture was filtered. To the filtrate was added 100% ethanol of an amount equal to that of the filtrate, so as to precipitate the saccharide synthesized. The precipitate was washed with 50% ethanol, 100% ethanol and diethyl ether, and then dried in vacuum at 60°C for 2 hours, to obtain 2.2 g of Compound C 1 . Thereafter, the product was analyzed by gel filtration liquid chromatography. The mean degree of polymerization (m 4 ) of the product determined from the standard curve based on a standard amylose reagent (produced by Nakano Vineger Co., Ltd.) was 31, and that based on the determination of phosphate was 19. In 13 C-NMR [solvent, DMSO-d6; concentration of Compound B 1 , 5%(W/V); standard substance, TMS; 60°C; 400 MHz], peaks of 1- and 2-position methylene protons derived from the silane agent appear at 0.54 ppm and 1.53 ppm, respectively (the 3-position methylene protons are masked by the protons of the saccharides), and a peak of methyl protons of the ethoxy groups appears at 1.15 ppm (methylene protons are masked by the saccharide protons). These data indicate that the product is Compound C 1 . (1-3) Synthesis of Compound of the Following Formula (2); (wherein Rc represents a hydrogen atom or and Z 1 represents the surface of silica gel, an ethoxy group, a silane agent, or a polysaccharide-bonded silane agent to a saccharide moiety. Substitution rate based on elementary analysis = 41%. m 4 is estimated to be roughly the same as that of Compound C 1 ). Into 14 ml of anhydrous DMSO was dissolved 1.0 g of Compound C 1 synthesized in (1-2) above, and the resulting solution was added to 3 g of previously activated (by means of vacuum drying at 180°C for 2 hours) silica gel (produced by YMC Co. ; mean pore size, 12 nm; mean particle size, 5 µm). To this was added 4 ml of pyridine, and the resulting mixture was heated at 90°C for 12 hours in a nitrogen stream, to allow the silane moiety of the above Compound C 1 to chemically bond to the silanol groups of the silica gel. The thus obtained surface-treated silica gel was collected by filtration with a G4 glass filter and was washed with DMSO. tetrahydrofuran, methanol, ace tone and hexane to remove unbonded Compound C 1 , and then dried in vacuum at 60°C for 2 hours. The existence of the porysaccharide on silica surface was confirmed by elementary analysis, the results of which were: C. 6.25%; H, 1.53%; and N, 0.06%. The surface treated silica gel was dispersed into a mixture of 8 ml of anhydrous DMSO and 3 ml of anhydrous pyridine, and 3.0 ml of 4-methylphenyl isocyanate was added thereto and allowed to react at 80°C for 5 hours in a nitrogen atmosphere, to modify the hydroxyl groups in the saccharide moieties chemically bonded to the surface of silica gel. After the presence of excess isocyanate groups in the reaction mixture had been confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum, the polysaccharide derivative-conjugated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane to remove impurities, and then dried in vacuum at 60 °C for 2 hours. The resultant compound was then subjected to IR spectrometry and elementary analysis. Results are shown in Fig. 4 and Table 3. Compound Elementary Analysis C (%) H (%) N (%) Formula (2) 15.87 1.83 1.68 Formula (3) 7.15 0.70 0.41 Formula (4) 7.09 0.69 0.64 Formula (5) 7.08 0.69 0.62 Formula (6) 9.14 0.90 0.86 Formula (7) 9.00 0.90 1.01 Formula (8) 8.90 0.90 1.08 Formula (9) 12.18 0.97 1.81 Formula (10) 12.78 1.19 1.91 In its IR spectrum, a peak of carbonyl stretching vibration (C=O absorption of secondary carbamic acid ester) was observed at near 1,730 cm -1 and the existence of polysaccharide derivatives on silica surface was confirmed by elementary analysis. Thus a compound of Formula (2) was obtained. In order to improve the properties of the thus obtained Formula (2) as a separating agent for chromatography, the compound was subjected to a conventional end capping treatment with trimethylchlorosilane. The thus obtained product was collected by filtration with a G4 glass filter and was washed as above with tetrahydrofuran, methanol, acetone and hexane, and then dried in vacuum at 60°C for 2 hours, to obtain a product to be used as a separating agent for chromatography. The chiral resolution ability of the compound was investigated as a separating agent for various racemic compounds. Results obtained are shown in Table 4. In Tables 2 and 4, k 1 indicates capacity factor of the isomer eluted fast and is obtained by the following formula; and α indicates separation factor and is obtained from the following equation. k 2 , likewise k 1 , indicates capacity factor of the isomer eluted rate and is obtained from the following equation. α = k 1 /k 2 k 1 =[(retention time of isomer eluted earlier) - (dead time)]/(dead time) k 2 = [(retention time of isomer eluted later) - (dead time)]/(dead time) Example 2 (2-1) Synthesis of Compound C 2 of the Following Formula; (wherein n has the same meaning as defined above. Mean degree of polymerization (m 4 ) based on the determination of phosphate = 79) Compound C 2 of the above formula was synthesized in the same manner as in (1-2) of Example 1. That is, 0.3 g of Compound A 1 synthesized in (1-1) of Example 1 and 12 g of glucose-1-phosphate (GIP) were dissolved into a mixture of 105 ml of DMSO and 300 ml of sterilized ultra pure water (pH was adjusted to 6). To this was added 210 units of crude phosphorylase derived from potato, and the resulting mixture was allowed to stand at 30°C for about 4 hours. The polymerization of the saccharide chain was followed by sampling part of the reaction mixture and, after deactivating the enzyme with trichloroacetic acid, determining the amount of liberated phosphate by the Fiske-Subbarow method. After the enzyme had been inactivated by heating on a hot water bath, the reaction mixture was filtered. To the filtrate was added 100% ethanol of an amount equal to that of the filtrate, so as to precipitate the saccharide synthesized. The precipitate was washed with 50% ethanol, 100% ethanol and diethyl ether, and then dried in vacuum at 60°C for 2 hours, to obtain 2.2 g of Compound C 2 . Thereafter, the product was analyzed by gel filtration liquid chromatography. The mean degree of polymerization (m 4 ) of the product determined from the standard curve based on a standard amylose reagent (produced by Nakano Vineger Co., Ltd.) was 85, and that based on the determination of phosphate was 79. (2-2) Synthesis of Compound of Formula (3) (wherein Rc represents a hydrogen atom or and Z 1 has the same meaning as defined above. The substitution degree of hydroxy group from the weight analysis = 90% or above. m 4 is estimated to be roughly the same as that of Compound C 2 ). Into 14 ml of anhydrous DMSO was dissolved 1.0 g of Compound C 2 synthesized in (2-1) above, and the resulting solution was added to 3 g of previously activated (by means of vacuum drying at 180°C for 2 hours) silica gel (produced by Daiso Co. ; mean pore size, 100 nm; mean particle size, 7 µm). To this was added 4 ml of pyridine, and the resulting mixture was heated at 90°C for 12 hours in a nitrogen stream, to allow the silane moiety of Compound C 2 to chemically bond to the silanol groups of the silica gel. The thus obtained surface-treated silica gel was collected by filtration with a G4 glass filter and the residue was washed with DMSO, tetrahydrofuran, methanol, acetone and hexane to remove unbonded Compound C 2 , etc. and then dried in vacuum at 60°C for 2 hours. The surface-treated silica gel was dispersed into a mixture of 8 ml of anhydrous DMSO and 3 ml of anhydrous pyridine, and 1.5 ml of 3,5-dimethylphenyl isocyanate was added thereto and allowed to react at 80°C for 5 hours in an nitrogen stream, to modify the hydroxyl groups in the saccharide moieties chemically bonded to the surface of silica gel. After the presence of excess isocyanate groups in the reaction mixture had been confirmed by the peak of C=N stretching vibration at 2, 270 cm -1 in its IR spectrum, the polysaccharide derivative-conjugated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane to remove impurities, and then dried in vacuum at 60°C for 2 hours. The resultant compound was then subjected to IR spectrometry and elementary analysis. Results of elementary analysis are shown in Table 3. The existence of the polysaccharide derivatives on silica surface was confirmed by the peak of carbonyl stretching vibration (absorption of C=O in the secondary carbamic acid ester) at near 1,730 cm -1 in its IR spectrum, as well as by elementary analysis. Thus the compound of Formula (3) was obtained. In order to improve the properties of the thus obtained compound as a separating agent for chromatography, the compound was subjected to a conventional end capping treatment with trimethylchlorosilane. The thus obtained product was collected by filtration with a G4 glass filter and was washed as above with tetrahydrofuran, methanol, ace tone and hexane, and then dried in vacuum at 60°C for 2 hours, to obtain a product to be used as a separating agent for chromatography. The chiral resolution ability of the compound was investigated as a separating agent for various racemic compounds. Results obtained are shown in Table 4. Example 3 (3-1) Synthesis of Lactonized Amylose (1) of the Following Formula; (mean degree of polymerization m 5 based on the determination of phosphate = 15). A KOH-methanol solution is added to an iodine-methanol solution of 18.9 g maltopentose in accordance with a known method to obtain 19.7 g of potassium {O-α-D-glucopyranosyl-(1→4)} 4 -D-glucanate (which may hereinafter be referred to as potassium G5 glucanate). Into 800 ml of sterilized ultra pure water was dissolved 2.1 g of the potassium G5 glucanate and 32 g of glucose 1-phosphate (G1P) (pH was adjusted to 6). To this was added 240 units of crude phosphorylase derived from potato, and the resulting mixture was allowed to stand at 45°C for about 2 hours. The degree of polymerization of the saccharide chain was followed by sampling part of the reaction mixture and, after inactivating the enzyme with trichloroacetic acid, determining the amount of liberated phosphate by the Fiske-Subbarow method. The enzyme was inactivated by heating on a hot water bath, and the reaction mixture was filtered. Thereafter, the glucanate salt was converted into lactone by adding concentrated hydrochloric acid to the reaction mixture to pH 1. To the resulting reaction mixture was added 100% ethanol of an amount equal to that of the reaction mixture, so as to precipitate the saccharide synthesized. The precipitate was washed with 50% ethanol, 100% ethanol and diethyl ether, and then dried in vacuum at 60°C for 2 hours, to obtain 3.0 g of lactonized Amylose (1) of the above formula. The product was analyzed by gel filtration liquid chromatography. The mean degree of polymerization (m 5 ) of the product determined from the standard curve based on a standard amylose reagent (produced by Nakano Vineger Co., Ltd.) was 37, and that based on the determination of phosphate was 15. In its IR spectrum, a peak of C=O stretching vibration of lactone was observed at 1,740 cm -1 . (3-2) Synthesis of Lactonized Amylose (2) of the Following Formula; (mean degree of polymerization based on the determination of phosphate = 29). Into a mixture of 240 ml of sterilized ultra pure water and 105 ml of DMSO were dissolved 0.53 g of potassium G5 glucanate and 16 g of glucose 1-phosphate (G1P). After its pH had been adjusted to 6,400 units of crude phosphorylase derived from potato was added thereto, and the resulting mixture was allowed to stand at 45°C for about 2 hours. The degree of polymerization of the saccharide chain was followed by sampling part of the reaction mixture and, after deactivating the enzyme with trichloroacetic acid, determining the amount of liberated phosphate by the Fiske-Subbarow method. The enzyme was inactivated by heating on a hot water bath, and the reaction mixture was filtered. Thereafter, the glucanate salt was converted into lactone by adding concentrated hydrochloric acid to the reaction mixture to pH 1. To the resulting reaction mixture was added 100% ethanol of an amount equal to that of the reaction mixture, so as to precipitate the saccharide synthesized. The precipitate was washed with 50% ethanol, 100% ethanol and diethyl ether, and then dried in vacuum at 60°C for 2 hours, to obtain 3.0 g of lactonized Amylose (2) of the above formula. The product was analyzed by gel filtration liquid chromatography. The mean degree of polymerization (m 5 ) of the product determined from the standard curve based on a standard amylose reagent (produced by Nakano Vineger Co. Ltd.) was 47, and that based on the determination of phosphate was 29. (3-3) Synthesis of Lactonized Amylose (3) of the Following Formula; (mean degree of polymerization m 5 based on the determination of phosphate = 92). Into a mixture of 240 ml of sterilized ultra pure water and 105 ml of DMSO were dissolved 0.265 g of potassium G5 glucanate synthesized in (3-1) above and 16 g of glucose 1-phosphate (G1P). After its pH had been adjusted to 6,550 units of crude phosphorylase derived from potato was added thereto, and the resulting mixture was allowed to stand at 45°C for about 5 hours. The degree of polymerization of the saccharide chain was followed by sampling part of the reaction mixture and, after inactivating the enzyme with trichloroacetic acid, determining the amount of liberated phosphate by the Fiske-Subbarow method. The enzyme was inactivated by heating on a hot water bath, and the reaction mixture was filtered. Thereafter, the glucanate salt was converted into into lactone by adding concentrated hydrochloric acid to the reaction mixture to pH 1. To the resulting reaction mixture was added 100% ethanol of an amount equal to that of the reaction mixture, so as to precipitate the saccharide synthesized. The precipitate was washed with 50% ethanol, 100% ethanol and diethyl ether, and then dried in vacuum at 60°C for 2 hours, to obtain 2.48 g of lactonized Amylose (3) of the above formula. The product was analyzed by gel filtration liquid chromatography. The mean degree of polymerization (m 5 ) of the product determined from the standard curve based on a standard amylose reagent (produced by Nakano Vineger Co.,Ltd.) was 147, and that based on the determination of phosphate was 92. (3-4) Synthesis of Surface-Treated silica Gel (No. 1) To 10 g of previously activated (by means of vacuum drying at 180 °C for 2 hours) silica gel (produced by Daiso Co. ; mean pore diameter, 100 µm; particle size, 7 µm) were added 36 ml of anhydrous benzene and 3 ml of anhydrous pyridine. Then, 2 ml of 3-amin opropyltriethoxysilane was added thereto and allowed to react at 90°C for 12 hours. The thus obtained surface-treated silica gel was washed with methanol, acetone and hexane, and then dried in vacuum at 60°C for 2 hours. (3-5) Synthesis of Surface-Treated silica Gel (No. 2) To 10 g of previously activated (by means of vacuum drying at 180 °C for 2 hours) silica gel (produced by Daiso Co. ; mean pore diameter, 100 µm; particle size, 7 µm) were added 12 ml of anhydrous benzene and 1 ml of anhydrous pyridine. Then, 0.7 ml of 3-(2-aminoethylaminopropyl)trimethoxysilane was added thereto and allowed to react at 90°C for 12 hours. The thus obtained surface-treated silica gel was washed with methanol, acetone and hexane, and then dried in vacuum at 60°C for 2 hours. (3-6) Synthesis of Surface-Treated silica Gel (No. 3) To 10 g of previously activated (by means of vacuum drying at 180 °C for 2 hours) silica gel (produced by Daiso Co. ; mean pore diameter, 100 µm; particle size, 7 µm) were added 12 ml of anhydrous benzene and 1 ml of anhydrous pyridine. Then, 0.7 ml of 3-(2-aminoethylaminoethylamino)propyltrimethoxysilane was added thereto and allowed to react at 90°C for 12 hours. The thus obtained surface-treated silica gel was washed with methanol, acetone and hexane, and then dried in vacuum at 60°C for 2 hours. (3-7) Synthesis of compound of the Following Formula (4) To 3 g of the aminopropyl functionalized silica gel obtained in (3-4) was added a solution prepared by dissolving 1 g of lactonized Amylose (1) into 8 ml of anhydrous DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bonds. The resulting polysaccharides-conjugated silica gel was collected by filtration with a G4 glass filter and was washed with DMSO, tetrahydrofuran, methanol, acetone and hexane to remove the excess lactonized Amylose (1), etc. and dried in vacuum at 60°C for 2 hours. Subsequently, the polysaccharides-conjugated silica gel was dispersed into a mixture of 8 ml of anhydrous DMSO and 3 ml of anhydrous pyridine, and then 1.5 ml of 3,5-dimethylphenyl isocyanate was added thereto and allowed to react at 80°C for 5 hours. The presence of excess isocyanate groups in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The polysaccharides-conjugated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane and then dried in vacuum at 60°C for 2 hours. The resultant compound Formula (4) was then subjected to IR spectrometry and elementary analysis. Results of elementary analysis are shown in Table 3. The existence of polysaccharide derivatives on silica surface was confirmed by the carbonyl stretching vibration (absorption of C=O in the secondary carbamic acid ester) at near 1,730 cm -1 in its IR spectrum, as well as by elementary analysis. Thus the compound of Formula (4) was obtained. The chiral resolution ability of the compound was investigated as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 4. (wherein Rc represents a hydrogen atom or and Z 1 has the same meaning as defined above. The substitution degree of hydroxyl groups from weight analysis = 90% or above. m 4 is estimated to be roughly the same as m 5 of Compound C 5 ). Example 4 Synthesis of Compound of the Following Formula (5); [wherein Rc represents and Z 1 has the same meaning as defined above. The substitution degree of hydroxyl groups from weight analysis = 90% or above. m 4 is estimated to be roughly the same as m 5 of lactonized Amylose (2)]. To 3 g of aminopropyl functionalized silica gel obtained in (3-4) of Example 3 was added a solution prepared by dissolving 1 g of lactonized Amylose (2) into 8 ml of anhydrous DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bond. The resulting polysaccharides-conjugated silica gel was collected by filtration with a G4 glass filter and was washed with DMSO, tetrahydrofuran, methanol, acetone and hexane to remove excess lactonized Amylose (2), etc. and dried in vacuum at 60°C for 2 hours. Subsequently, the polysaccharides-conjugated silica gel was dispersed into a mixture of 8 ml of anhydrous DMSO and 3 ml of anhydrous pyridine, and then 1.5 ml of 3,5-dimethylphenyl isocyanate was added thereto and allowed to react at 80°C for 5 hours. The presence of excess isocyanate groups in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The polysaccharides derivatives conjugated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane and then dried in vacuum at 60°C for 2 hours. The resultant compound was subjected to IR spectrometry and elementary analysis. Results of elementary analysis are shown in Table 3. The existence of the polysaccharide derivatives was confirmed by the carbonyl stretching vibration (absorption of C=O in the secondary carbamic acid ester) at near 1,730 cm -1 in its IR spectrum, as well as by elementary analysis. Thus the compound of the above described Formula (5) was obtained. The chiral resolution ability of the compounds was investigated as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 4. Example 5 Synthesis of Compound of the Following Formula (6); [wherein Rc represents and Z 1 has the same meaning as defined above. The substitution degree of hydroxyl groups from weight analysis = 90% or above. m 4 is estimated to be roughly the same as m 5 of lactonized Amylose (3)]. To 3 g of aminopropyl functionalized silica gel obtained in (3-4) of Example 3 was added a solution prepared by dissolving 1 g of lactonized Amylose (3) into 8 ml of anhydrous DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bonds. The resulting polysaccharides-conjugated silica gel was collected by filtration with a G4 glass filter and was washed with DMSO, tetrahydrofuran, methanol, acetone and hexane to remove excess lactonized Amylose (3), etc. and dried in vacuum at 60°C for 2 hours. Subsequently, the polysaccharides-conjugated silica gel was dispersed into a mixture of 8 ml of anhydrous DMSO and 3 ml of anhydrous pyridine, and then 1.5 ml of 3,5-dimethylphenyl isocyanate was added thereto and allowed to react at 80°C for 5 hours. The presence of excess isocyanate groups in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The polysaccharide derivatives-conjugated silica gel contained in the reaction mixture was washed with tetrahydrofuran, methanol, acetone and hexane and then dried in vacuum at 60°C for 2 hours. The resultant compound was subjected to IR spectrometry and elementary analysis. Results of elementary analysis are shown in Table 3. The existence of polysaccharide derivatives on silica surface was confirmed by the carbonyl stretching vibration (absorption of C=O in the secondary carbamic acid ester) at near 1,730 cm -1 in its IR spectrum, as well as by elementary analysis. Thus the compound of the above described Formula (6) was obtained. The chiral resolution ability of the compounds was investigated as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 4. Example 6 Synthesis of Compound of the Following Formula (7); [wherein Rc represents a hydrogen atom or and Z 2 represents the surface of silica gel, a methoxy group, a silane agent or a saccharide-bonded silane agent. Substitution degree of hydroxyl groups from the weight analysis = 90% or above. m 4 is estimated to be roughly the same as m 5 of lactonized Amylose (3)]. To 3 g of the amino groups functionalized silica gel obtained in (3-5) of Example 3 was added a solution prepared by dissolving 1 g of lactonized Amylose (3) synthesized in a similar manner as in (3-3) of Example 3 into 8 ml of anhydrous DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bonds. Thereafter, the procedure of Example 5 was followed to obtain a compound of the above-described General Formula (7). The chiral resolution ability of the compounds was investigated as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 4. Example 7 Synthesis of Compound of the Following Formula (8); (wherein Rc represents a hydrogen atom or and Z 2 has the same meaning as defined above. Substitution degree of hydroxyl group from the weight analysis = 90% or above. m 4 is estimated to be roughly the same as m 5 of lactonized Amylose (3)). To 3 g of the amino groups-fanctionalized silica gel obtained in (3-6) of Example 3 was added a solution prepared by dissolving 1 g of lactonized Amylose (3) synthesized in a similar manner as in (3-3) of Example 3 into 8 ml of dried DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bonds. Thereafter, the procedure of Example 5 was followed to obtain a compound of the above-described Formula (8). The chiral resolution ability of the compound was investigation as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 4. Example 8 Synthesis of Compound of the Following Formula (9); (wherein Rc represents a hydrogen atom or degree of hydroxyl group from the weight analysis is 90 % or above; m 4 is estimated to be roughly the same as m 5 of lactonized Amylose (3); and Z 2 represents any of the surface of silica gel, a methoxy group, a silane agent and a saccharide-bonded silane agent). (8-1) Synthesis of Surface-Treated Silica Gel: To 10 g of silica gel (made by Fuji Silicia Co. - having a mean pore size of 50 nm and a mean particle size of 5 µm) that had been previously activated (by drying in vacuum at 180°C for 2 hours), added were 12 ml of anhydrous benzene and 1 ml of anhydrous pyridine. 0.7 ml of 3-(2-aminoethylaminopropyl)triethoxysilane were added thereto and reacted at 90°C for 12 hours. The amino groups-functionalized silica gel thus obtained was washed with methanol, acetone and hexane and dried in vacuum at 60°C for 2 hours. (8-2) To 8 g of the amino groups-functionalized silica gel, obtained in (8-1) above, added was a solution obtained by dissolving 1 g of lactonized Amylose (3) that had been produced in the same manner as in Example 3 (3-3) in 8 ml of anhydrous DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bonds. The resulting surface-treated silica gel was collected by filtration through a G4 glass filter, and the residue was washed with DMSO, tetrahydrofuran, methanol, acetone and hexane to remove the excess lactonized Amylose (3), etc. and dried in vacuum at 60°C for 2 hours. The saccharide-bonded silica gel was dispersed into a mixture of 8 ml of anhydrous DMA-LiCl and 3 ml of pyridine, and 5 g of 3,5-dichlorophenyl isocyanate (this was formed from 3,5-dichloroaniline by an ordinary method) dissolved in 5 ml of DMA were added thereto and reacted at 80°C in nitrogen for 12 hours. The presence of excess isocyanate groups in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The saccharide-bonded, surface-treated silica gel was washed with tetrahydrofuran, methanol, acetone and hexane and dried in vacuum at 60 °C for 2 hours. The resultant compound was then subjected to IR spectrometry and elementary analysis. Results of elementary analysis are shown in Table 1. The formation of bonding to silica gel, or the production of the compound of Formula (9) set forth above was confirmed by the carbonyl stretching vibration (absorption of C=O in the secondary carbamic acid ester) at 1,710 cm -1 in its IR spectrum, as well as by elementary analysis. The compound was tested and evaluated with respect to its function as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 5. Example 9 Synthesis of Compound of the Following Formula (10); (wherein Rc represents a hydrogen atom or substitution degree of hydroxyl group from the weight analysis is 90 % or above; m 4 is estimated to be roughly the same as m 5 of lactonized Amylose (3); and Z 2 represents any of the surface of silica gel, a methoxy group, a silane agent and a saccharide-bonded silane agent). To 3 g of the amino groups functionalized silica gel obtained in Example 8 (8-1), was added a solution obtained by dissolving 1 g of lactonized Amylose (3) that had been produced in the same manner as in Example 3 (3-3) in 8 ml of dry DMSO, and reaction was allowed to proceed at 80°C for 12 hours to form amide bonds. The resulting surface-treated silica gel was collected by filtration through a G4 glass filter, and the residue was washed with DMSO, tetrahydrofuran, methanol, acetone and hexane to remove the excess lactonized Amylose (3), etc. and dried in vacuum at 60°C for 2 hours. The saccharide-bonded silica gel was dispersed into a mixture of 8 ml of anhydrous DMA-LiCl and 3 ml of pyridine, and 2 ml of phenyl isocyanate were added thereto and reacted at 80°C for 12 hours in nitrogen. The presence of excess isocyanate groups in the reaction mixture was confirmed by the peak of C=N stretching vibration at 2,270 cm -1 in its IR spectrum. The saccharide-bonded, surface-treated silica gel was washed with tetrahydrofuran, methanol, acetone and hexane and dried in vacuum at 60°C for 2 hours. The resultant compound was then subjected to IR spectrometry and elementary analysis. Results of elementary analysis are shown in Table 1. The formation of bonding to silica gel, or the production of the compound of Formula (10) set forth above was confirmed by the carbonyl stretching vibration (absorption of C=O in the secondary carbamic acid ester) at 1,710 cm -1 in its IR spectrum, as well as by elementary analysis. The compound was tested and evaluated with respect to its function as a chromatographic separating agent for various racemic compounds. Results obtained are shown in Table 6. Application Example Preparation of Column for Optical Resolution and Optical Resolution Power The novel substances obtained in Examples 1 to 9 were packed into empty, stainless steel columns of 0.46 cm x 25 cm, by the slurry packing method. For the packing was used PS-10 and PS-20 Autopacking Systems manufactured by Kyoto Chromato Co. The chiral resolution powder of the substances was evaluated by high performance liquid chromatography, using the columns, a Waters 515 Pump, a 484 UV Detector, etc. As a control was cited a separating agent prepared by physically coating an amylose tris (3,5-dimethylphenyl carbamate) derivative onto aminopropyl functionalized silica gel. Results cited are shown in Table 2, 3 and 4 [see Chemistry Letters, pp.1857-1860 (1987)]. The results shown in Table 2 show that any of the compounds represented by Formulae (6), (7) and (8) obtained in Examples 5, 6 and 7 give particularly improved α-values for Racemates (7) and (8), in comparison with the control. The results shown in Table 3 show that the compound represented by Formula (9) could be separated , by using an eluate containing tetrahydrofuran, Racemates (10) and (11) which could not be separated with the compound of Comparative Example. Further, the results shown in Table 4 show that the compound represented by Formula (10) could be separated Racemate (5) which could not be separated with the compound of Comparative Example. The α-values for Racemate (3) were improved remarkably in comparison with the control. To examine the solvent resistance of the chiral resolution columns prepared by using the novel substances according to the present invention, a tetrahydrofuran (THF) solution was passed though the columns at a flow rate of 1 ml/min for 2 hours and thereafter the optical resolution powder of the columns was measured. No changes were recognized. This proves that the substances have excellent solvent resistance. The above analysis was carried out by using an eluent of hexane/IPA (= 90/10) at room temperature. # denotes 90:5 and denotes an eluent → hexane/THF = 80:20, respectively. The flow rate was 0.5 ml/min. As explained hereinabove, the novel substances of the present invention have excellent solvent resistance and are useful as a chromatographic separating agent for separating chiral compounds substances. In addition, the novel substances can be efficiently produced in a convenient manner in accordance with the present invention.

Claims: A method of producing a substance having a main structure of the following Formula (1) in which a polysaccharide or a derivative thereof is chemically bonded to the inner and outer surfaces of a porous carrier at the reducing terminal of said polysaccharide or derivative thereof, wherein R represents Ra, -CO-Ra or -CO-NH-Ra (in which Ra represents a hydrogen atom or a substituent selected from a substituted or unsubstituted alkyl group, a substituted or unsubstituted phenyl group and a substituted or unsubstituted heterocyclic residue); Rb represents a substituted or unsubstituted methylene group, a substituted or unsubstituted phenylene group or a group containing covalently bonded hetero atom(s); Z represents a member selected from the surface of a porous carrier, a halogen atom, an alkyl group, an alkoxy group, a phenyl group, a silane agent and a saccharide-bonded silane agent; m 1 represents the number of monosaccharide units, which may be in the range of from 10 to 500 on average; and m 2 represents an integer of from 1 to 20, wherein an oligosaccharide having a degree of polymerization of from 3 to 10 is chemically bonded to a silane agent at the reducing terminal of the oligosaccharide, the oligosaccharide derivative obtained is polymerized to an average degree of polymerization of from about 11 to about 500 with the action of an enzyme, and the resulting polysaccharide derivatives are then chemically bonded to a porous carrier at the silane moiety present at the terminal of the polysaccharide. The method according to Claim 1, wherein the aldehyde group present at the reducing terminal of an oligosaccharide having a degree of polymerization of from 3 to 10 is oxidized with an oxidizing agent. and the saccharide chain of the oxidized product is polymerized to a degree of polymerization of from about 11 to about 500 by the action of an enzyme, followed by the addition of an acid. The method according to Claim 1 or 2, wherein said enzyme is a member selected from hydrolases, saccharide transferases and polymerases. The method according to Claim 1 or 2, wherein said enzyme is phosphorylase. The method according to Claim 1 or 2, wherein said enzyme is phosphorylase and dimethylsulfoxide is added to the reaction mixture upon enzymatic reaction using said enzyme. The method according to any of Claims 1 to 5, wherein substituents are introduced into all or part of the hydroxyl groups of the saccharide moieties by ether, ester or urethane bonds. A separating agent for separating chiral compounds comprising the substance obtained according to Claim 1. A substance having the structure of the following Formula (A') wherein m 3 represents an integer of from 2 to 9, n represents an integer of from 0 to 3, preferably 0, and Rb and m 2 have the same meanings as defined in claim 1. A substance having the structure of the following Formula (B') wherein m 1 , m 2 , Rb and Z have the same meanings as defined in claim 1. A substance having the structure of the following Formula (C') wherein m 1 , m 2 and Rb have the same meanings as defined in claim 1 and n has the same meaning as defined in claim 8.

Inventors: AKANO HIROFUMI, ENOMOTO NAOKI, FURUKAWA SACHIKO, KAWAMURA YOSHIYA, OGASAWARA YASUSHI, OKAMOTO YOSHIO, AKANO. HIROFUMI, ENOMOTO, NAOKI, FURUKAWA, SACHIKO, KAWAMURA, YOSHIYA, OGASAWARA, YASUSHI, OKAMOTO, YOSHIO
Applicants: DAICEL CHEM, DAICEL CHEMICAL INDUSTRIES, LTD.
Application year: 1994
Main classification: C08B37
IPC codes: B01J20, C08B37, C07B57