Improved double metal cyanide complex catalysts

Abstract: Improved double metal cyanide catalysts are disclosed. The substantially amorphous catalysts of the invention are more active for polymerizing epoxides than conventional DMC catalysts, which have a substantial crystalline component. Polyol products made with the catalysts are unusually clear, have exceptionally low unsaturations, and contain no detectable amount of low molecular weight polyol impurities. A method of making the improved DMC catalysts, which involves intimately combining the reactants, is also disclosed.

Description: FIELD OF THE INVENTION : The invention relates to double metal cyanide (DMC) complex catalyst compositions. The catalysts are highly active in epoxide polymerizations. The specification includes a method for preparing the compositions. Polyether polyol products made using the catalyst compositions have exceptionally low unsaturations. BACKGROUND OF THE INVENTION : Double metal cyanide complex compounds are well known catalysts for epoxide polymerization. The catalysts are highly active, and give polyether polyols that have low unsaturation compared with similar polyols made using basic (KOH) catalysis. Conventional DMC catalysts are prepared by reacting aqueous solutions of metal salts and metal cyanide salts to form a precipitate of the DMC compound. The catalysts can be used to make a variety of polymer products, including polyether, polyester, and polyetherester polyols. Many of the polyols are useful in various polyurethane coatings, elastomers, sealants, foams, and adhesives. Conventional DMC catalysts are usually prepared in the presence of a low molecular weight complexing agent, typically an ether such as glyme (dimethoxy-ethane) or diglyme. The ether complexes with the DMC compound, and favorably impacts the activity of the catalyst for epoxide polymerization. In one conventional preparation, aqueous solutions of zinc chloride (excess) and potassium hexacyanocobaltate are combined by simple mixing. The resulting precipitate of zinc hexacyanocobaltate is then mixed with aqueous glyme. An active catalyst is obtained that has the formula: Zn 3 [Co(CN) 6 ] 2 · xZnCl 2 · yH 2 O · zGlyme Other known complexing agents include alcohols, ketones, esters, amides, ureas. (See, for example, U.S. Patent Nos. 3,427,256, 3,427,334, 3,278,459, and Japanese Pat. Appl. Kokai Nos. 4-145123, 3-281529 and 3-149222). Generally, the catalyst made with glyme has been the catalyst of choice. The catalysts have relatively high surface areas, typically within the range of about 50-200m 2 /g. Thus, EPA 0555053 discloses double metal cyanide complex catalysts suitable for use in ring-opening polymerization reactions are prepared in filterable form by adding an aqueous solution of a stoichiometric excess of a first metal salt to an aqueous solution of an alkali metal cyanometallate while maintaining the temperature of the latter in the range of 30°C to 75°C, and arranging for either or both of the solutions to contain a water-miscible heteroatom-containing organic ligand or for the slurry obtained by combining the solutions to be contacted with such an organic ligand. Double metal cyanide compounds prepared in the absence of a complexing agent are highly crystalline (as shown by X-ray diffraction analysis), and are inactive for epoxide polymerization. When the complexing agents described above are used, the resulting catalysts actively polymerize epoxides. Our X-ray diffraction analyses of active DMC complexes prepared according to methods known in the art suggest that conventional DMC catalysts are actually mixtures of a highly crystalline DMC compound and a more amorphous component. Typically, conventional DMC catalysts--which are generally prepared by simple mixing--contain at least about 35wt.% of highly crystalline DMC compound. DMC compounds useful as epoxide polymerization catalysts and containing less than 30wt.% of highly crystalline DMC compound are not known. Double metal cyanide catalysts generally have good activity for epoxide polymerizations, often much greater than conventional basic catalysts. However, because the DMC catalysts are rather expensive, catalysts with improved activity are desirable because reduced catalyst levels could be used. Double metal cyanide catalysts normally require an "induction" period. In contrast to basic catalysts, DMC catalysts ordinarily will not begin polymerizing epoxides immediately following exposure of epoxide and starter polyol to the catalyst. Instead, the catalyst needs to be activated with a small proportion of epoxide before it becomes safe to begin continuously adding the remaining epoxide. Induction periods of an hour or more are typical yet costly in terms of increased cycle times in a polyol production facility. Reduction or elimination of the induction period is desirable. An advantage of DMC catalysts is that they permit the synthesis of high molecular weight polyether polyols having relatively low unsaturation. The adverse impact of polyol unsaturation on polyurethane properties is well documented. (See, for example, C.P. Smith et al., J. Elast. Plast. , 24 (1992) 306, and R.L. Mascioli, SPI Proceedings, 32nd Annual Polyurethane Tech./Market. Conf. (1989) 139.) When a DMC catalyst is used, polyols having unsaturations as low as about 0.015 meq/g can be made. Polyether polyols with even lower unsaturations can be made if a solvent such as tetrahydrofuran is used to make the polyol. However, for commercial polyol production, the use of a solvent is not particularly desirable. Thus, other ways to further reduce polyol unsaturation are needed. When conventional DMC catalysts are used to polymerize epoxides, the polyether polyol products contain relatively low levels (about 5-10 wt.%) of low molecular weight polyol impurities. A way to eliminate these polyol impurities is desirable because improved polyurethanes could result from the use of more monodisperse polyols. Double metal cyanide complex catalyst residues are often difficult to remove from polyether polyols, and a wide variety of methods have been developed to cope with the problem. Removal of DMC catalyst residues from the polyols promotes long-term storage stability and consistent polyol performance in urethane formulation. Most methods involve some kind of chemical treatment of the polyol following polymerization. There has been little progress made in developing catalyst preparation methods that ultimately facilitate catalyst removal from the polyol products. SUMMARY OF THE INVENTION : The invention is an improved catalyst for polymerizing epoxides. We have surprisingly found that DMC complexes lacking a well-defined crystal structure are much more active than conventional DMC complexes for epoxide polymerization. In addition, the DMC complexes of this invention are more quickly activated (show reduced induction periods) compared with conventional DMC catalysts. According to one aspect of this invention, there is provided a double metal cyanide (DMC) complex which complex comprises i) up to 10wt% of a crystalline DMC component and ii) at least 90 wt-% of a DMC component which is amorphous to X-rays and which comprises a complexing agent which is a water-soluble aliphatic alcohol. More preferred compositions comprise at least 99 wt.% of component ii). Although conventional methods for making DMC complex catalysts have been known for about 30 hears, no one has previously appreciated that the method of combining the reactants is extremely important. We have now discovered, quite surprisingly , that highly active, DMC complexes of the invention are produced only when the reactants are intimately combined during catalyst preparation. Aqueous solutions of a water-soluble metal salt and a water-soluble metal cyanide salt are intimately combined in the presence of a complexing agent to produce an aqueous mixture containing the DMC complex catalyst. The catalyst, which is then isolated and dried, consists of at least 90 wt.% of component ii). The invention also includes a method for preparing an epoxide polymer. The method comprises polymerizing an epoxide in the presence of a catalyst according to the present invention. The catalysts of this invention provide polyether polyol compositions that have exceptionally low unsaturations and contain unusually low levels of low molecular weight polyol impurities. Finally, the invention also includes a method for improving the filterability of a DMC complex catalyst from a polyether polyol product following epoxide polymerization. The method comprises using, as a polymerization catalyst, a DMC complex catalyst of the invention. BRIEF DESCRIPTION OF THE DRAWING: Figure 1 shows a plot of propylene oxide consumption versus time during a polymerization reaction with one of the catalyst compositions of the invention at 250 ppm catalyst. The induction time for the run is measured as discussed in Example 6 from the intersection of the extended baseline and slope measurements. DETAILED DESCRIPTION OF THE INVENTION : The catalysts of the invention, unlike conventional DMC compounds known in the art as useful for epoxide polymerization, consist of at least 90 wt.% of all component ii) as herein defined. More preferred catalysts of the invention consist of at least 99 wt.% of a component ii). The catalysts of this invention comprise at least 90 wt-% of a DMC component which is amorphous to X-rays; that is, lacking a well-definied crystal structure or characterised by the substantial absence of sharp lines in the X-ray diffraction pattern of the component. Powder X-ray diffraction (XRD) patterns of conventional double metal cyanide catalysts show characteristic sharp lines that correspond to the presence of a substantial proportion of a highly crystalline DMC component. Highly crystalline zinc hexacyanocobaltate prepared in the absence of an organic complexing agent, which does not actively polymerize epoxides, shows a characteristic XRD fingerprint of sharp lines at d-spacings of about 5.07, 3.59, 2.54, and 2.28 angstroms. When a DMC catalyst is made in the presence of an organic complexing agent according to conventional methods, the XRD pattern shows lines for the highly crystalline material in addition to broader signals suggesting that conventional DMC epoxidation catalysts are actually mixtures of highly crystalline DMC compound and a component lacking a well-defined crystal structure. Typically, conventional DMC catalysts, which are generally prepared by simple mixing, contain at least about 35 wt.% of highly crystalline DMC compound. The catalysts of the invention are distinguishable from conventional DMC compositions by their XRD pattern showing that little or no crystalline DMC compound is present. When a zinc hexacyanocobaltate catalyst is prepared according to the method of the invention using tert-butyl alcohol as a complexing agent, for example, the X-ray diffraction pattern shows essentially no lines for crystalline zinc hexacyanocobaltate (5.07, 3.59, 2.54, 2.28 angstroms), but instead has only two major lines, both relatively broad, at d-spacings of about 4.82 and 3.76 angstroms. Spiking experiments demonstrate that DMC catalysts prepared by the method of the invention typically contain less than about 1 wt.% of crystalline DMC compound. X-ray results appear in Table 1. Conventional DMC catalysts typically contain at least about 35 wt.% of crystalline DMC compound. No one has previously recognized the potential value of reducing the content of crystalline DMC compounds in these catalysts. It appears that the crystalline DMC compound acts as either a diluent or as a poison for the more active component of the catalyst, and its presence is preferably minimized or eliminated. The invention includes compositions which comprise at least 90 wt.% of component ii) as herein defined and up to 10 wt.% of a crystalline DMC compound. Most preferred are compositions that comprise at least 99 wt.% of component ii) and up to 1 wt.% of the crystalline material. The catalyst compositions of the invention have relatively low surface areas. Conventional DMC compounds have surface areas within the range of about 50 to about 200 m 2 /g. In contrast, the surface areas of the catalysts of the invention are preferably less than about 30 m 2 /g. More preferred compositions have surface areas less than about 20 m 2 /g. Double metal cyanide compounds useful in the invention are the reaction products of a water-soluble metal salt and a water-soluble metal cyanide salt. The water-soluble metal salt preferably has the general formula M(X) n in which M is selected from the group consisting of Zn(II), Fe(II), Ni(II), Mn(II), Co(II), Sn(II), Pb(II), Fe(III), Mo(IV), Mo(VI), Al(III), V(V), V(IV), Sr(II), W(IV), W(VI), Cu(II), and Cr(III). More preferably, M is selected from the group consisting of Zn(II), Fe(II), Co(II), and Ni(II). In the formula, X is preferably an anion selected from the group consisting of halide, hydroxide, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, isothiocyanate, carboxylate, and nitrate. The value of n is from 1 to 3 and satisfies the valency state of M. Examples of suitable metal salts include, but are not limited to, zinc chloride, zinc bromide, zinc acetate, zinc acetonylacetate, zinc benzoate, zinc nitrate, iron(II) sulfate, iron(II) bromide, cobalt(II) chloride, cobalt(II) thiocyanate, nickel(II) formate, nickel(II) nitrate, and the like, and mixtures thereof. The water-soluble metal cyanide salts used to make the double metal cyanide compounds useful in the invention preferably have the general formula (Y) a M'(CN) b (A) c in which M' is selected from the group consisting of Fe(II), Fe(III), Co(II), Co(III), Cr(II), Cr(III), Mn(II), Mn(III), Ir(III), Ni(II), Rh(III), Ru(II), V(IV), and V(V). More preferably, M' is selected from the group consisting of Co(II), Co(III), Fe(II), Fe(III), Cr(III), Ir(III), and Ni(II). The water-soluble metal cyanide salt can contain one or more of these metals. In the formula, Y is an alkali metal ion or alkaline earth metal ion. A is an anion selected from the group consisting of halide, hydroxide, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, isothiocyanate, carboxylate, and nitrate. Both a and b are integers greater than or equal to 1; the sum of the charges of a, b, and c balances the charge of M'. Suitable water-soluble metal cyanide salts include, but are not limited to, potassium hexacyanocobaltate(III), potassium hexacyanoferrate(II), potassium hexacyanoferrate(III), calcium hexacyanocobaltate(III), lithium hexacyanoiridate(III), and the like. Examples of double metal cyanide compounds that can be used in the invention include, for example, zinc hexacyanocobaltate(III), zinc hexacyanoferrate(III), zinc hexacyanoferrate(II), nickel(II) hexacyanoferrate(II), cobalt(II) hexacyanocobaltate(III), and the like. Further examples of suitable double metal cyanide compounds are listed in U.S. Patent No. 5,158,922. The catalyst compositions of the invention are prepared in the presence of a complexing agent which is a water-soluble aliphatic alcohol. The complexing agent is added either during preparation or immediately following precipitation of the catalyst. Usually, an excess amount of the complexing agent is used. Preferred complexing agents are selected from the group consisting of ethanol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, sec-butyl alcohol, and tert-butyl alcohol. The conventional method of preparing DMC compounds useful for epoxide polymerization is fully described in many references, including U.S. Patent Nos. 5,158,922, 4,843,054, 4,477,589, 3,427,335, 3,427,334, 3,427,256, 3,278,457, and 3,941,849, and Japanese Pat. Appl. Kokai No. 4-145123. The method of making the DMC catalyst compositions of the invention comprises two steps. First, aqueous solutions of a water-soluble metal salt and a water-soluble metal cyanide salt are intimately combined and reacted in the presence of the said complexing agent to produce an aqueous mixture that contains a precipitated DMC complex catalyst. Second, the catalyst is isolated and dried. The complexing agent can be included with either or both of the aqueous salt solutions, or it can be added to the DMC compound immediately following precipitation of the catalyst. It is preferred to pre-mix the complexing agent with either the water-soluble metal cyanide salt, or with the water-soluble metal salt, or both, before intimately combining the reactants. The resulting catalyst composition is lacking a well-defined crystal structure, as is evidenced by the substantial absence of crystalline DMC compound by X-ray diffraction analysis. We have surprisingly discovered that achieving an intimate combination of the reactants is essential to preparing catalysts having low crystallinity. In conventional methods, the water-soluble metal salt and the water-soluble metal cyanide salt are combined in aqueous media and are simply mixed together, typically with magnetic or mechanical stirring. This method of preparation results in catalysts having a substantial amount of crystalline DMC component, typically greater than 35 wt.%. We have found that combining the reactants in a manner effective to achieve an intimate combination of the reactants results in catalysts that are exceptionally useful for epoxide polymerization. Suitable methods of achieving this intimate combination of reactants include homogenization, impingement mixing, high-shear stirring, and the like. When the reactants are homogenized, for example, the level of crystalline material in the catalyst composition is minimized or eliminated, and is much lower than the amount of crystalline material present in a catalyst made by simple mixing. The invention includes a process for making an epoxide polymer. This process comprises polymerizing an epoxide in the presence of a double metal cyanide catalyst composition of the invention. Preferred epoxides are ethylene oxide, propylene oxide, butene oxides, styrene oxide, and the like, and mixtures thereof. The process can be used to make random or block copolymers. The epoxide polymer can be, for example, a polyether polyol derived from the polymerization of an epoxide in the presence of a hydroxyl group-containing initiator. Other monomers that will copolymerize with an epoxide in the presence of a DMC compound can be included in the process of the invention to make other types of epoxide polymers. Any of the copolymers known in the art made using conventional DMC catalysts can be made with the catalysts of the invention. For example, epoxides copolymerize with oxetanes (as taught in U.S. Patent Nos. 3,278,457 and 3,404,109) to give polyethers, or with anhydrides (as taught in U.S. Patent Nos. 5,145,883 and 3,538,043) to give polyester or polyetherester polyols. The preparation of polyether, polyester, and polyetherester polyols using double metal cyanide catalysts is fully described, for example, in U.S. Patent Nos. 5,223,583, 5,145,883, 4,472,560, 3,941,849, 3,900,518, 3,538,043, 3,404,109, 3,278,458, 3,278,457, and in J.L. Schuchardt and S.D. Harper, SPI Proceedings, 32nd Annual Polyurethane Tech./Market. Conf. (1989) 360. The DMC catalysts of the invention are highly active compared to conventional DMC catalysts (see Table 2). For example, a zinc hexacyanocobaltate catalyst made using tert-butyl alcohol as a complexing agent and made by homogenization (and containing less than 1 wt.% of crystalline DMC compound by X-ray analysis) is about 65% more active at 100 ppm, and 200% more active at 130-250 ppm, than the same catalyst made by simple mixing (and containing about 35 wt.% crystalline DMC compound). A consequence of higher polymerization rates is that polyol producers can use less of the relatively expensive DMC catalyst and save money. More active catalysts also permit the producer to reduce batch times and increase productivity. The catalyst compositions of the invention show a reduced induction period compared with conventional catalysts in a polyether polyol synthesis (see Table 3). Conventional DMC catalysts are not immediately active toward epoxide polymerization. Typically, a starter polyol, the catalyst, and a small amount of epoxide are combined and heated to the desired reaction temperature, and no epoxide polymerizes immediately. The polyol manufacturer must wait (often for several hours) until the catalyst becomes active and the charged epoxide begins to react before additional epoxide can safely be continuously added to the polymerization reactor. The catalysts of the invention are more rapidly activated than conventional catalysts that contain up to 35 wt.% of crystalline DMC compound. This feature of the catalysts is also an economic advantage because delays in adding the epoxide are reduced. Polyether polyols prepared using the catalysts of the invention have exceptionally low unsaturations, consistently less than about 0.007 meq/g. These unsaturations are at least about 50% lower than polyol unsaturations available from the DMC catalysts previously known (see Table 4). Preferred polyols of the invention have unsaturations less than about 0.006 meq/g, and more preferably less than about 0.005 meq/g. The reduction in unsaturation compared with polyols previously available from conventional DMC catalysts should offer some advantages for polyurethanes made with the polyols of the invention. Polyether polyols made with the catalysts of the invention preferably have average hydroxyl functionalities from about 2 to 8, more preferably from about 2 to 6, and most preferably from about 2 to 3. The polyols preferably have number average molecular weights within the range of about 500 to about 50,000. A more preferred range is from about 1,000 to about 12,000; most preferred is the range from about 2,000 to about 8,000. Polyols prepared with the catalysts of the invention also have substantially lower levels of low molecular weight polyol impurities compared with polyols prepared with conventional catalysts. Gel permeation chromatography (GPC) analysis of these polyols shows no detectable low molecular weight polyol impurities. In contrast, conventional DMC catalysts made in the usual way with glyme as a complexing agent show a marked GPC peak corresponding to about 5-10 wt.% of a low molecular weight polyol impurity. Interestingly, polyols made with the catalysts of the invention are usually clearer than polyols made with conventional glyme catalysts; the former typically remain clear even after weeks of storage at room temperature, while the latter tend to quickly develop a haze during storage. Another advantage of the catalysts of the invention is that they are more easily removed from polyether polyols following polyol synthesis compared with conventional DMC compounds. The problem of how to remove DMC compounds from polyether polyols has been the subject of many investigations (see, for example, U.S. Patent Nos. 5,144,093, 5,099,075, 5,010,047, 4,987,271, 4,877,906, 4,721,818, and 4,355,188). Most of these methods irreversibly deactivate the catalyst. The catalysts of the invention can be isolated by simply filtering the polyol. Another way to isolate the catalyst is to first dilute the polyol with a solvent such as heptane to reduce viscosity, then filter the mixture to recover the catalyst, and then strip the polyol/heptane mixture to obtain the purified polyol. The methods described in U.S. Patent No. 5,010,047 can also be used to recover the catalysts of the invention from polyols. An advantage of the catalysts of the invention is that they can be removed cleanly from polyols even with a hot filtration in the absence of any solvent. In contrast, when a polyol made with a conventional glyme catalyst is hot-filtered, substantial amounts of the DMC compound remain in the polyol. If desired, the isolated catalyst composition of the invention can be recovered and reused to catalyze another epoxide polymerization reaction because these simple filtration methods do not generally deactivate the catalysts. The following examples merely illustrate the invention. Preparation of Zinc Hexacyanocobaltate Catalysts by Homogenization Example 1. Tert-butyl Alcohol as the Complexing Agent (Catalyst D) Potassium hexacyanocobaltate (8.0 g) is added to deionized water (150 mL) in a beaker, and the mixture is blended with a homogenizer until the solids dissolve. In a second beaker, zinc chloride (20 g) is dissolved in deionized water (30 Ml). The aqueous zinc chloride solution is combined with the solution of the cobalt salt using a homogenizer to intimately mix the solutions. Immediately after combining the solutions, a mixture of tert-butyl alcohol (100 mL) and deionized water (100 mL) is added slowly to the suspension of zinc hexacyanocobaltate, and the mixture is homogenized for 10 min. The solids are isolated by centrifugation, and are then homogenized for 10 min. with 250 mL of a 70/30 (v:v) mixture of tert-butyl alcohol and deionized water. The solids are again isolated: by centrifugation, and are finally homogenized for 10 min with 250 mL of tert-butyl alcohol. The catalyst is isolated by centrifugation, and is dried in a vacuum oven at 50°C and 30 in. (Hg) to constant weight. This catalyst is identified as Catalyst D. Preparation of Zinc Hexacyanocobaltate Catalysts by Homogenization Example 2. Isopropyl Alcohol as the Complexing Agent (Catalyst E) The procedure of Example 1 is modified as follows. Isopropyl alcohol is substituted for tert-butyl alcohol. Following combination of the zinc chloride and potassium hexacyanocobaltate solutions and homogenization in the presence of isopropyl alcohol, the catalyst slurry is filtered through a 0.45 micron filter at 20 psi. The washing steps of Example 1 are also repeated, but filtration rather than centrifugation is used to isolate the catalyst. The washed catalyst is dried to constant weight as described above. The catalyst is identified as Catalyst E. Preparation of Zinc Hexacyanocobaltate Catalysts by Simple Mixing Comparative Example 3. Tert-butyl Alcohol as the Complexing Agent (Catalyst B) The procedure of Japanese Pat. Appl. Kokai No. 4-145123 is generally followed. Potassium hexacyanocobaltate (4.0 g) is added to deionized water (75 mL) in a beaker, and the mixture is stirred until the solids dissolve. In a second beaker, zinc chloride (10 g) is dissolved in deionized water (15 mL). The aqueous zinc chloride solution is combined with the solution of the cobalt salt using a magnetic stirring bar to mix the solutions. Immediately after combining the solutions, a mixture of tert-butyl alcohol (50 mL) and deionized water (50 mL) is added slowly to the suspension of zinc hexacyanocobaltate, and the mixture is stirred for 10 min. The solids are isolated by centrifugation, and are then stirred for 10 min. with 100 mL of a 70/30 (v:v) mixture of tert-butyl alcohol and deionized water. The solids are again isolated by centrifugation, and are finally stirred for 10 min with 100 mL of tert-butyl alcohol. The catalyst is isolated by centrifugation, and is dried in a vacuum oven at 50°C and 30 in. (Hg) to constant weight. This catalyst is identified as Catalyst B. Preparation of Zinc Hexacyanocobaltate Catalysts by Simple Mixing Comparative Example 4. Isopropyl Alcohol as the Complexing Agent (Catalyst C) The procedure of Comparative Example 3 is followed, except that isopropyl alcohol is used in place of tert-butyl alcohol, and the solids are isolated by filtration using a 0.8 micron filter rather than by centrifugation. The catalyst is isolated and dried as described above. This catalyst is identified as Catalyst C. Comparative Example 5. Preparation of Crystalline Zinc Hexacyanocobaltate No Complexing Agent (Catalyst A) Potassium hexacyanocobaltate (4.0 g) is dissolved in deionized water (150 mL) in a beaker. Zinc chloride (10 g) is dissolved in deionized water (15 mL) in a second beaker. The aqueous solutions are quickly combined and magnetically stirred for 10 min. The precipitated solids are isolated by centrifugation. The solids are reslurried in deionized water (100 mL) for 10 min. with stirring, and are again recovered by centrifugation. The catalyst is dried in a vacuum oven at 50°C and 30 in. (Hg) to constant weight. This catalyst is identified as Catalyst A. Example 6. Epoxide Polymerizations: Rate Experiments--General Procedure A one-liter stirred reactor is charged with polyoxypropylene triol (700 mol. wt.) starter (70 g) and zinc hexacyanocobaltate catalyst (0.057 to 0.143 g, 100-250 ppm level in finished polyol, see Table 2). The mixture is stirred and heated to 105°C, and is stripped under vacuum to remove traces of water from the triol starter. The reactor is pressurized to about 1 psi with nitrogen. Propylene oxide (10-11 g) is added to the reactor in one portion, and the reactor pressure is monitored carefully. Additional propylene oxide is not added until an accelerated pressure drop occurs in the reactor; the pressure drop is evidence that the catalyst has become activated. When catalyst activation is verified, the remaining propylene oxide (490 g) is added gradually over about 1-3 h at a constant pressure of 20-24 psi. After propylene oxide addition is complete, the mixture is held at 105°C until a constant pressure is observed. Residual unreacted monomer is then stripped under vacuum from the polyol product, and the polyol is cooled and recovered. To determine reaction rate, a plot of PO consumption (g) vs. reaction time (min) is prepared (see Fig. 1). The slope of the curve at its steepest point is measured to find the reaction rate in grams of PO converted per minute. The intersection of this line and a horizontal line extended from the baseline of the curve is taken as the induction time (in minutes) required for the catalyst to become active. The results of reaction rates and induction times measured for various catalysts at 100-250 ppm catalyst levels appear in Tables 2 and 3. Example 7. Polyether Polyol Synthesis: Effect of Catalyst on Polyol Unsaturation, Catalyst Removal, and Polyol Quality A two-gallon stirred reactor is charged with polyoxypropylene triol (700 mol. wt.) starter (685 g) and zinc hexacyanocobaltate catalyst (1.63 g). The mixture is stirred and heated to 105°C, and is stripped under vacuum to remove traces of water from the triol starter. Propylene oxide (102 g) is fed to the reactor, initially under a vacuum of 30 in. (Hg), and the reactor pressure is monitored carefully. Additional propylene oxide is not added until an accelerated pressure drop occurs in the reactor; the pressure drop is evidence that the catalyst has become activated. When catalyst activation is verified, the remaining propylene oxide (5713 g) is added gradually over about 2 h while maintaining a reactor pressure less than 40 psi. After propylene oxide addition is complete, the mixture is held at 105°C until a constant pressure is observed. Residual unreacted monomer is then stripped under vacuum from the polyol product. The hot polyol product is filtered at 100°C through a filter cartridge (0.45 to 1.2 microns) attached to the bottom of the reactor to remove the catalyst. Residual Zn and Co are quantified by X-ray analysis. Polyether diols (from polypropylene glycol starter, 450 mol. wt.) and triols are prepared as described above using zinc hexacyanocobaltate catalysts made by conventional methods (stirring) and by the method of the invention (homogenization). The impact of the catalysts of the invention on epoxide polymerization rate (Table 2), induction period (Table 3), polyol unsaturation (Table 4), catalyst removal (Table 5), and polyol quality (Table 6) are shown in the tables. The preceding examples are meant only as illustrations. The scope of the invention is defined by the claims. Effect of Catalyst on Epoxide Polymerization Rate (105°C) ID Catalyst Cat. amt. (ppm) Rate of polymerization (g/min) F glyme , 250 3.50 130 1.78 100 1.46 B TBA stirred 250 3.64 130 2.50 100 2.29 D TBA homog. 250 10.5 130 7.40 100 3.84 C IPA stirred 250 < 0.3 E IPA homog. Effect of Catalyst on Induction Period (105°C) ID Catalyst Catalyst concentration (ppm) Induction Time (min) F glyme , 100 230 250 180 B TBA stirred 100 220 130 180 250 90 D TBA homog. 100 140 130 130 250 85 Effect of Catalyst on Polyol Unsaturation ID Catalyst Polyol OH # (mg KOH/g) and functionality Solvent Polyol unsaturation (meq/g) F glyme , 54 (Triol) none 0.016 27 (Triol) none 0.017 15 (Triol) none 0.019 B TBA stirred 35 (Triol) none 0.011 27 (Triol) none 0.010 14 (Triol) none 0.011 D TBA homog. 27 (Triol) none 0.005 56 (Diol) none 0.004 27 (Diol) none 0.005 14 (Diol) none 0.004 31 (Triol) THF 0.003 12 (Triol) heptane 0.006 Effect of Catalyst on Catalyst Removal ID Catalyst Polyol OH # (mg KOH/g) and functionality Filtration Temp. (°C) Solvent Residual catalyst (ppm) Zn Co F glyme , 27 (Triol) 100 none 28 12 B TBA stirred 25 (Triol) 100 none 6 3 D TBA homog. 25 (Triol) 100 none 5 < 2 14 (Diol) 100 none 4 < 2 29 (Diol) 100 none 3 < 2 14 (Triol) 100 none 4 < 2 27 (Triol) 25 heptane 3 < 2 14 (Diol) 25 heptane 6 < 2 Effect of Catalyst on Polyol Purity and Clarity ID Catalyst Low Mol. Wt. Polyol Impurity (Wt.%, by GPC) Appearance (25°C, after 3 weeks) F glyme 5-10 hazy D TBA none detected clear

Claims: A double metal cyanide (DMC) complex comprising i) up to 10 wt% of a crystalline DMC component and ii) at least 90 wt.% of a DMC component which is amorphous to X-rays and which comprises a complexing agent which is a water-soluble aliphatic alcohol. A complex as claimed in claim 1 comprising at least 99 wt.% of said amorphous DMC component. A complex as claimed in any preceding claim having a surface area of less than 30 m 2 /g. A complex as claimed in claim 3 having a surface area of less than 20 m 2 /g. A complex as claimed in any preceding claim wherein the DMC complex is a zinc hexacyanocobaltate. The use of a catalyst as claimed in any preceding claim for polymerising epoxides, for example to polyether polyols.

Inventors: LE-KHAC BI, LE-KHAC, BI
Applicants: BAYER ANTWERPEN NV, BAYER ANTWERPEN N.V.
Application year: 1994
Main classification: B01J27
IPC codes: C08G65, C08L63, C08G59, B01J31, B01J23, B01J27