HIGH PURITY THIOL-ENE COMPOSITION

Abstract: A treatment method for polyene resins used in thiol-ene formulations, especially norbornene resins, significantly stabilizes thiol-ene compositions made from batches of polyene resin which otherwise give compositions with poor dark stability. The treatment comprises contacting the polyene with an amphoteric treating agent selected from the group consisting of silicated magnesium oxide, basic aluminum oxide, silica gel, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, barium oxide, and barium hydroxide, and then separating the resin from the treating agent prior to mixture with a polythiol to form a thiol-ene composition. The treatment method significantly reduces ionic content in polyene resins, particularly chloride ion but also sodium and potassium ions. Consequently, treatment is also beneficial with polyene resins which do not produce substantial dark stability problems. Reduction of the ionic content of the resin is desirable to produce cured thiol-ene polymers with low electrical conductivity and low corrosiveness.

Description: HIGH PURITY THIOL-ENE COMPOSITION Background of the Invention Definitions As used herein: A polyene is a compound having a plurality of olefinically unsaturated groups. A polythiol is a compound having plurality of organic thiol groups. A thiol-ene composition is a mixture of a polyene and a polythiol formulated to cure at least predominately by addition of thiol groups across the olefinic double bond of the polyene. Generally the composition will include a free radical initiator such as a peroxy compound or a free radical photoinitiator to initiate the thiol-ene addition reactions. Norbornenyl groups, as used herein, are broadly defined to encompass organic functional groups of the formula: where Q is CR-, 1 , O, S, NR 1 or SO 2 , R 1 is H or alkyl; and m is 0-10. Thus the term should be understood to encompass, in addition to true norbornenyl groups, various substituted analogs, nadic groups and various other cyclopentadiene Diels-Alder polyadducts. Background Art In thiol-olefin cooxidation reactions it has been reported that chloride ion and bromide ion shortened an initial slow oxygen-absorbing phase while iodide ion prolonged the initial phase and decreased its rate. Bredereck et al, Chemische Berichte, 93 2415-2423 (1960); D'Souza et al, J. Org. Chem. 1987, 41, 1729-1740. Several hypotheses are offered in the latter reference as possible explanations of the difference between chloride/bromide and iodide in this reaction, but no conclusions are drawn as to which of the hypotheses are correct. Organohalo compounds, such as tris(2,3-dibromopropyl) phosphate and tetrabromophthalic anhydride (0.1-10%) in combination with mercaptans (0.05-5%) are said to improve melt spin properties of polyolefin compounds. Chem. Abst. , 80: 1222322 (abstracting JP 48004374). The polymerization of methacrylate ester monomers during neutralization, washing and/or extraction with base is reported to be inhibited by adding 0.03-0,3% NaNO 2 and/or KI to the solutions. Chem. Abst. , 106; 156990r (abstracting CS 229529). Heat stability of a nylon to polymer containing a copper stearate , KI, and 2-mercaptobenzimidazole is reported to be improved over comparable formulations omitting either the KI or the mercapto compound in Chem. Abst. , 81: 137494f (abstracting JP 49053944). Halogen containing compounds such as 2,4-bis(trichloromethyl)-6- methyl-s-triazine are reported as components of an initiator system, which also uses an organic thiol component, for anaerobically curing formulations in Chem. Abst. , 100: 69316h (abstracting US 4,413,108). In Bartlett et al, J CS, 72, 1051-1059 (1950), iodine was reported to have a dual effect on peroxide catalyzed polymerizations of vinyl acetate, rapidly accelerating polymerization at moderate concentrations but behaving as a rather strong inhibitor at low concentrations. I 3 - radical is postulated as a terminator of growing polymer chain to explain the inhibition affection. A polar mechanism is postulated to explain the acceleration at higher concentrations. Curable thiol-ene systems are described in US 3,661,744; US 4,119,617; US 4,289,867; US 3,445,419 and US 4,808,638. Such formulations employ a polyene functional resin, a polythiol and a free radical initiator. In US 4,808,638 there are described photocurable thiol-ene compositions comprising a norbomene functional resin, a polythiol and a free radical photoinitiator. Further description of this system may be found in Jacobine et al, Proceedings of ACS Division of Polymeric Materials: Science and Engineering, Vol. 60, pp. 211-216 (1989). Norbornenyl functional resins and their uses are described in US Patent No. 4,808,638 and references cited therein. The disclosed use of such resins in this reference is as the polyene resin in radically cured thiol-ene formulations. The aforementioned US patent is incorporated herein by reference. Further norbornenyl functional compounds useful in thiol-ene compositions as described in US Pat. No. 4,808,638, US 5,034,490, US 5,171,816 and US 5,182,360 and copending applications Ser. No. 07/315,737 filed February 24, 1989 and Ser. No. 07/619,068 filed November 28, 1990. Dark stability of thiol-ene curable formulations has been a problem for a number of these systems, particularly those where the polyene is a plural norbomene compound. The norbornene-thiol system, however, is an especially desirable system because of its very high cure speed, good cured polymer properties and the ready availability of norbomene resins from acrylate ester precursors. Various attempts have been made to improve upon the dark stability of thiol-ene systems by use of improved stabilizers. References pertaining to these efforts include US 3,619,393; US 5,208,281; and EP 428,342. Such improvements, however, are not always satisfactory in achieving consistent, commercially acceptable shelf lives. In particular, it has been noticed that certain batches of ene resins are extremely difficult to formulate into shelf-stable thiol-ene compositions. Summary of the Invention It has now been discovered that treatment of a norbomene resin, prior to mixture with a polythiol to form a thiol-ene composition, significantly stabilizes compositions made from batches of ene resin which have previously given the greatest stability problems. The treatment comprises contacting the polyene with an amphoteric treating agent selected from the group consisting of silicated magnesium oxide, basic aluminum oxide, silica gel, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, barium oxide, and barium hydroxide, and then separating the resin from the treating agent. It has been found that treatment with such amphoteric substances significantly reduces ionic content in polyene resins, particularly chloride ion but also sodium and potassium ions " Consequently, treatment is considered beneficial even with polyene resins which do not produce substantial dark stability problems. Reduction of the ionic content of the resin is desirable to produce cured thiol-ene polymers with low electrical conductivity and low corrosiveness. Detailed Description of the Invention The amphoteric substance used to treat the polyene resins is selected from the group consisting of silicated magnesium oxide, basic aluminum oxide, silica gel, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, barium oxide and barium hydroxide. The average particle size of the amphoteric substance is preferably in the range of about 2 microns to about 200 microns. A particularly preferred amphoteric agent is Magnesol * Polysorb 30/40 hydrated silicated magnesium oxide, which has a particle size range of from about 2 to about 200 microns and an average particle size of 50 microns. Contact time with the polyene resin will vary depending upon the temperature employed and the moisture content and viscosity of the resin. The time should be for sufficient time to reach a Cl " content of less than 1.0 ppm, preferably to 0.5 ppm or less, or for sufficient time to improve the shelf life of a thiol-ene composition prepared by mixing the polyene with a polythiol after the amphoteric treating agent has been separated from the polyene. The treatment can also be used to reduce sodium and potassium levels below 1 ppm, suitably 0.5 or less. Typical contact times will be between 1 hour and 3 days. Treatment efficiency can be improved, lessening necessary contact time, if the polyene has a small moisture content, suitably, 0.01 % - 1.0%. When a dry resin is used and moisture can readily be removed subsequent to treatment, e.g. by vacuum stripping, it may be desirable to add moisture to the treatment mixture. Contact temperatures will also vary depending on viscosity of the polyene. Effective ion removal can be obtained at temperatures between 0 °C and 100 °C provided that the polyene is sufficiently non-viscous at the temperature employed to allow for good agitation of the mixture. The amphoteric treating agent must be removed from the polyene resin prior to formulation into a curable composition, such as a thiol-ene composition. Separation can be " accomplished by filtration but in some cases where the amphoteric treating agent has a clay-like consistency addition of a filter aid such as Celite ® to the treatment mixture prior to filtration is necessary for effective filtration. Addition of the filter aid does not appear to influence the effectiveness of the amphoteric treating agent in removing ionic species or in improving shelf-life stability of thiol-ene compositions produced from the treated resin. The plural norbomene functional compounds useful in the invention are known from US 4,808,638, incorporated herein by reference, and have recently also been described in Jacobine et al, "Photoinitiated Cross-linking of Norbomene Resins with Multifunctional Thiols", Chapter 13 of Radiation Curing of Polymeric Materials, ACS Symposium Series #417, American Chemical Society, 1990, and US 5,167,882. Particularly preferred norbomene compounds are norbomenemethyl norbomene carboxylate and norbomene carboxylate esters of polyols such as 1,6-hexanediol, trimethylolpropane, ethoxylated bisphenol A, poly(tetramethyleneoxide) and mixtures thereof. The polythiol component of the inventive compositions may be any compound having two or more thiol groups per molecule. Suitable polythiols are described in US 3,661,744 at col.8, In 76 - col.9, In 46; in US 4,119,617, col.7, Ins 40-57; US 3,445,419; and US 4,289,867. Especially preferred are polythiols obtained by esterification of a polyol with an or β-mercaptocarboxylic acid such as thioglycolic acid, or /3-mercaptopropionic acid. Particularly preferred polythiols are pentaerythritol tetramercaptoacetate and pentaerythritol tetrakis-j3-mercaptopropionate (PETMP). The ratio of the polyene to the polythiol component can be varied widely. Generally it is preferred that the ratio of thiol to ene groups be between 0.7:1 and 1.3:1, but ratios outside this range may occasionally be usefully employed without departing from the invention hereof. While a curable composition using norbomene functional compounds of the invention may include both difunctional norbornenyl compounds and difunctional thiol compounds, it will be understood that at least a portion of at least one of these components should contain more than two functional groups per molecule to produce a crosslinked product when cured. That is, the total of the average number of norbomene groups per molecule of norbomene functional compound and the average number of coreactive thiol groups per molecule of the thiol functional compound should be greater than 4 when a crosslinked cured product is desired. This total is referred to as the "total reactive functionality" of the composition. The initiator used in the curable thiol-ene formulations is suitably a free radical photoinitiator. Examples of free radical photoinitiators include benzoin and substituted benzoin compounds, benzophenone, Michler's ketone, dialkoxybenzophenones, dialkoxyacetophenones, peroxyesters described in US 4,616,826 and 4,604,295, etc. The photoinitiator is employed in an amount effective for initiating cure of the formulation upon irradiation with UV light, suitably 0.1-10%, typically 0.5-5%. The formulations also preferably include a stabilizer. Preferred stabilizers are described in EP 428,342. Such stabilizers are non-acidic nitroso compounds, particularly N-nitrosoarylhydroxylamines and salts thereof. Particularity suitable stabilizer compounds are the ammomum and aluminum salts of N-nitrosophenylhydroxylamine which may be usefully employed at levels between about 10 ppm and 2%, preferably 10-5,000 ppm. As described in US 5,208,281, triiodide and other polyiodides are useful shelf-life stabilizers for thiol-ene formulations. The invention is illustrated by reference to the following non-limiting examples. Example 1 Dinorbornene resins were produced by Diels-Alder cycloaddition of cyclopentadiene to ethoxylated bisphenol A. The same lot of aery late starting material was used in both the control and the treated samples. Resins were filtered at 50 °C through a course frit Celite ® C bed after synthesis. The treated sample was mixed with 2 wt% Magnesol ® Polysorb 30/40 silicated magnesium oxide, stirred three hours at 45 °C and allowed to sit overnight. Celite ® filter aid, 3 wt% was added, mixed for one hour at 45 °C and then the mixture filtered at 70 °C using a lμ filter pad. The dinorbornene resins were then formulated into thiol-ene formulations using equivalent weights of pentaerythritol tetramercaptopropionate, 2 wt% Darocure ® 1173 photoinitiator and 1000 ppm aluminum N- nitrosophenylhydroxylamine. Samples of the formulations were then stored at room temperature and at 5°C under nitrogen. Viscosities of the formulations were taken at periodic intervals to ascertain their relative storage stability. Results are given in Table I. TABLE I FORMULATION VISCOSITIES (Cumulative Change) STORAGE INTERVAL (Temperature) Example 1 Control 0 7178 6864 7 days (RT * ) 7904 (10%) 8024 (17%) 28 days (RT) 8595 (20%) 10441 (52%) 90 days (RT) 8985 (25%) 14728 (115%) 180 days (RT) 10218 (42%) 21627 (215%) 180 days (5 °C) 7520 (5%) 9809 (43%) * RT = room temperature (approximately 21 °C). Example 2 The procedure of Example 1 was repeated using the same batch of norbomene resin for both control and treated samples. Results are shown in Table II. TABLE II FORMULATION VISCOSITIES (Cumulative Change) STORAGE INTERVAL (Temperature) Example 2 Control 0 7187 7204 7 days (RT) 8418 (17%) 53520 (643%) 28 days (RT) 9714 (36%) 69865 (870%) 90 days (RT) 14431 (101 %) 92660 (1186%) 180 days (RT) 15302 (113%) 104348 (1348%) 180 days (5 °C) 8808 (23%) 33213 (361 %) Analysis for selected ions in the norbomene resins used in this Example gave the following results: Untreated control: 11.8 ppm CT; <0.5 ppm Br " ; 6.4 ppm Na + ; 1.5 ppm K + . Treated resin: <0.5 ppm Cl " ; <0.5 ppm Br; < 1 ppm Na + < 1 ppm K Example 3 (Comparative Example) The treated norbomene resin used in Example 2 was spiked with 7.2 ppm Cl " , as NaCl in a methanol solution using an equivalent weight of 18-Crown-6 to assure transfer of the salt into the resin. The spiked resin was then formulated as per Example II. After 7 days, the viscosity of the formulation had increased 44%, more than double the viscosity increase of the formulation made from the treated, unspiked resin. Example 4 The procedure of Example 2 was repeated except that the norbomene monomer used was hexanediol dinorbornene carboxylate and the viscosity was monitored for only seven days at room temperature. Results are given in Table III. TABLE III FORMULATION VISCOSITIES (Cumulative Change) STORAGE INTERVAL (Temperature) Example 4 Control 0 215 210 7 days (RT) 330 (53%) 917 (337%) Example 5 Treatment of triallyl-l,3,5-triazine-2,4,6(lH,3H,3H)-trione in the manner of Example I gave a reduction of chloride content from 5.2 ppm to 0.2 ppm. The treatment did not affect storage stability of a thiol-ene formulation prepared from this resin but the reduction in chloride content was considered desirable for electrical insulating and corrosion resistance properties of the formulation. Example 6 Samples of the untreated dinorbornene resin used in Example 2 were treated in the same manner as in that example except that the 2 wt% Magnesol ® Polysorb 30/40 and 3 wt% Celite ® filter aid, respectively, were replaced with, 2 wt% basic aluminum oxide and 1 wt% Celite ® ; 2 wt% silica gel and 1 wt% Celite ® ; and 3 wt% Magnesol ® Polysorb 30/40 and no Celite ® . Ηydrolyzable ion content was determined by ion chromatography on two trials for each sample and results are shown in Table IV. TABLE IV Sample Chloride Bromide Sodium Potassium Treatment (ppm) (ppm) (ppm) (ppm) None 9.8 None Detected 7.5 1.7 11.7 None Detected 9.3 2.0 2 wt% basic aluminum 0.1 None Detected <0.2 None Detected oxide and 1 wt% Celite ® <0.1 None Detected <0.2 None Detected 2 wt% silica gel and 1 0.1 None Detected <0.2 None Detected wt% Celite ® 0.1 None Detected <0.2 None Detected 3 wt% Magnesol ® <0.1 None Detected <0.2 None Detected Polysorb 30/40 and no <0.1 None Detected <0.2 None Detected Celite ® Estimated detection limits for bromide were 0.5 ppm and for potassium were 0.2 ppm.

Claims: Claims What is claimed is: 1) A treatment method for a polyene comprising contacting the untreated polyene with an amphoteric treating agent selected from the group consisting of silicated magnesium oxide, basic aluminum oxide, silica gel, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, barium oxide, and barium hydroxide for a contact time and then separating the treated polyene from the treating agent, the contact time being a sufficient time to yield a Cl- level in the polyene of less than 1.0 ppm after separation from the treating agent. 2) A method as in claim 1 wherein said untreated polyene has a Cl " level of 3 ppm or greater. 3) A method as in claim 1 wherein said contact time is a sufficient time to produce a Cl" level of 0.5 ppm or less. 4) A method as in claim 1 wherein said amphoteric treating agent is selected from the group consisting of silicated magnesium oxide, basic aluminum oxide and silica gel. 5) A method as in claim 4 wherein said contact time is a sufficient time to produce a Cl " level of 0.1 ppm or less and is further sufficient to produce a Na + level of 0.5 ppm or less and a K + level of 0.5 ppm or less. 6) A method as in claim 1 wherein said contact time is further sufficient to produce a Na + level of 1.0 ppm or less. 7) A method as in claim 1 wherein said contact time is further sufficient to produce a K + level of 1.0 ppm or less. 8) A method as in claim 1 wherein the treating agent has an average particle size between 2 microns and 200 microns. 9) A method as in claim 1 wherein the polyene is a plural norbomene functional compound. 10) A method as in claim 1 wherein the polyene is a plural allyl functional compound. 11) A method as in claim 1 wherein the amphoteric treating agent is silicated magnesium oxide. 12) A polyene prepared by the method of claim 1. 13) A polyene prepared by the method of claim 2. 14) A polyene as in claim 13 wherein the polyene is a plural norbomene functional compound. 15) A polyene as in claim 14 wherein the amphoteric treating agent is silicated magnesium oxide and said contact time is a sufficient time to produce a Cl " level of 0.1 ppm or less and is further sufficient to produce a Na + level of 0.5 ppm or less and a K + level of 0.5 ppm or less. 16) A method of preparing a thiol-ene composition comprising: contacting a polyene with an amphoteric treating agent selected from the group consisting of silicated magnesium oxide, basic aluminum oxide, silica gel, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, barium oxide, and barium hydroxide; separating the resin from the treating agent; and then, mixing the polyene with a polythiol; the polyene being contacted with the treating agent for sufficient time improve the shelf-life of the thiol-ene composition. 17) A method as in claim 16 wherein the treating agent has a particle size between 2 microns and 200 microns. 18) A method as in claim 16 wherein the polyene is a plural norbomene functional compound. 19) A method as in claim 16 wherein the amphoteric treating agent is silicated magnesium oxide. 20) A method for improving the storage stability of a thiol-ene composition, the composition comprising a mixture of a polythiol and a polyene in amounts effective to cure by addition reaction of thiol groups of the polythiol to ene groups of the polyene so as to form a crosslinked polythioether, the polyene being a compound having plural norbomene groups thereon, the method comprising: prior to mixing said polyene and said polythiol, contacting the untreated polyene with an amphoteric treating agent selected from the group consisting of silicated magnesium oxide, basic aluminum oxide, silica gel, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, barium oxide, and barium hydroxide for a contact time, and then separating the treated polyene from the treating agent, the contact time being a sufficient time to yield a Cl" level in the polyene of less than 1.0 ppm after separation from the treating agent, and then mixing the thus treated polyene and the polythiol to form the 5 thiol-ene composition.

Inventors: GLASER DAVID M, GRABEK PAUL J, JACOBINE ANTHONY F, GLASER, DAVID, M., GRABEK, PAUL, J., JACOBINE, ANTHONY, F.
Applicants: LOCTITE CORP, LOCTITE CORPORATION
Application year: 1994
Main classification: C08F6
IPC codes: C08F6, C08F8, C08G75