Cosmetics with enhanced adherence to the skin

Abstract: A method of enhancing adherence to the skin or eyelash of a skin care preparation containing an active ingredient by incorporating into the skin care preparation a film forming agent as an ingredient and applying the skin care preparation containing the active ingredient and the film forming agent to the skin. Our method is characterized by the film forming agent being a silicone pressure sensitive adhesive. Sunscreen preparations and eye cosmetics are described.

Description: This invention is directed to personal care and, more particularly, to skin care products including color cosmetics, which have been found to possess improved skin substantivity characteristics. Water and wear resistance are vital properties to skin protection products, since contact with water by perspiration and swimming, can destroy the effectiveness of an otherwise beneficial skin care product. Where greater protective qualities, high water resistance and substantive barrier characteristics, are desired in a skin care product, it is customary in the art to incorporate various organic waxes, organic resins and organic polymers, into the skin care product in order to achieve these goals. EP-A-0 521 647 describes a cosmetic composition for the treatment of areas around the eyes to reduce, or at least cover, facial lines and wrinkles. The cosmetic product described in this reference comprises:- (i) from about 1 to about 90% of a volatile silicone fluid; (ii) from about 0.1 to about 20% by weight of a non-volatile silicone gum; and (iii) from about 0.5 to about 50% of a C 16 - C 22 fatty acid ester of citric acid. The citrate esters were found to be suitable for formulation with silicones to provide a clear composition with a slightly tacky feel. What has been discovered in accordance with the present invention is that certain silicone based materials can be employed as viable alternatives to the organic waxes, resins and polymers, customarily used heretofore. Specifically, the silicone based material is a silicone pressure sensitive adhesive. The invention relates to a method of enhancing the adherence to the skin or eyelash of a personal care preparation containing an active ingredient. The method involves incorporating into the skin care preparation a film forming agent as an ingredient thereof and applying the skin care preparation containing the active ingredient and the film forming agent to the skin. The film forming agent according to the present invention is a silicone pressure sensitive adhesive. The invention further relates to a sunscreen preparation containing a film forming agent and at least one ultraviolet light absorbing compound as an active ingredient. The invention is characterized by the use of a silicone pressure sensitive adhesive as the film forming agent in the sunscreen preparation. In addition, the invention relates to an eye cosmetic containing a film forming agent, a pigment, a wax, an oil and a preservative. Again, a silicone pressure sensitive adhesive is used as the film forming agent in the eye cosmetic to adhere the active ingredient to the eyelashes. The invention provides a personal care preparation comprising a film forming agent and either a pigment, optionally with a wax and an oil, or at least one ultraviolet light absorbing compound, characterized by the film forming agent being a non-flammable hot-melt silicone pressure sensitive adhesive composition comprising a mixture of (i) a silicone resin and (ii) a silicone fluid, the mixture of (i) and (ii) exhibiting tackiness and adhesiveness, the mixture of (i) and (ii) being blended with (iii) 0.5 to 20 weight percent, based on the total weight of the silicone resin and the silicone fluid, of a phenyl-containing polysiloxane fluid having a viscosity at 25°C. of 5 to 60,000 mm 2 /s (centistokes). The film forming agent which may be employed is a non-flammable hot-melt silicone pressure sensitive adhesive composition comprising a mixture of: (i) 40 to 70 parts by weight of a trimethylsilyl-endblocked low molecular weight hydrocarbon or benzene-soluble resinous copolymer containing silicon bonded hydroxyl radicals and comprises triorganosiloxy units of the formula R'''' 3 SiO 1/2 and tetrafunctional siloxy units of the formula SiO 4/2 in a ratio of 0.6 to 0.9 triorganosiloxy units per tetrafunctional siloxy unit present in the copolymer molecule and R'''' is a monovalent hydrocarbon radical of one to six carbon atoms; (ii) 30 to 60 parts by weight of a silanol-endblocked polydiorganosiloxane fluid, wherein the total parts by weight of the resinous copolymer and the silanol-endblocked polydiorganosiloxane fluid equals 100 parts; the mixture of (i) and (ii) exhibiting tackiness and adhesiveness and blended with: (iii) 0.5 to 20 weight percent, based on the total weight of the resinous copolymer and the silanol-endblocked polydiorganosiloxane fluid, of a phenyl-containing polysiloxane fluid of the formula A 3 SiO[Si(C 6 H 5 )(R')O] x [Si(R 2 )O] y SiB 3 wherein R is a monovalent radical selected from -OSiR'' 3 , hydrocarbon radicals of one to three carbon atoms and -OH; R' is a monovalent radical selected from -OSiR'' 3 , -OH and -CH 3 ; R'' is a monovalent hydrocarbon radical of one to three carbon atoms; A and B are endblocking units selected from -OSiR''' 3 where R''' is a hydrocarbon radical of one to eight carbon atoms, -OH, halide radicals and amine radicals; x is an integer having a value greater than zero; and the value of x and y is such that the phenyl-containing polysiloxane fluid has a viscosity at 25°C. of 5 to 60,000 mm 2 /s (centistokes) and has 1 to 100 phenyl groups per 100 siloxane units. Details of the adhesive and examples of a process for its manufacture are set forth in U.S. Patent No. 5162410. The adhesive is also available commercially from Dow Corning Corporation, Midland, Michigan, USA. For the purpose of illustrating the present invention in more detail, oil in water emulsion mascara compositions B-H were prepared containing the adhesive and these compositions are set forth in Table I. Mascara composition H was used as the control mascara. The various ingredients of the mascara compositions are arranged as Groups A-E as indicated in Table I. INGREDIENTS MASCARA COMPOSITIONS (WEIGHT %) B C D E F G H Group A: 1. Water 47.5 57.5 57.5 57.5 47.5 47.5 57.5 2. Magnesium Aluminum Silicate 1.5 1.5 1.5 1.5 1.5 1.5 1.5 3. Triethonolamine 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Group B: 4. Black Iron Oxide 10.0 10.0 10.0 10.0 10.0 10.0 10.0 5. Ultramarine Blue 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Group C: 6. Carnauba Wax 2.0 2.0 2.0 2.0 2.0 2.0 2.0 7. Candelilla Wax 5.0 5.0 5.0 5.0 5.0 5.0 5.0 8. Stearic Acid 4.0 4.0 4.0 4.0 4.0 4.0 4.0 9. Beeswax 5.0 - - - 5.0 5.0 5.0 10. Petroleum Distillate (ISOPAR®) 10.0 10.0 10.0 10.0 10.0 10.0 10.0 11A.Alkylmethyl Silicone Wax with C 30 + alkyl group - 5.0 - - - - - 11B.Same as 11A but shorter silicone backbone - - 5.0 - - - - 11C.Same as 11A but with C 22-24 alkyl group - - - 5.0 - - - Group D: 12A.Aqueous Silicone Latex 10.0 - - - - - - 12B.Silicone Pressure Sensitive Adhesive - - - - 10.0 - - 12C.High Molecular Weight Silicone Gum HOMe 2 SiO(Me 2 SiO) n SiMe 2 OH - - - - - 10.0 - Group E: 13. Diazolidinyl urea (Germaben®II-E) 1.0 1.0 1.0 1.0 1.0 1.0 1.0 In Table I, ingredient 2 of Group A is a thickener sold under the trademark VEEGUM® by R.T. Vanderbilt Co. Inc., of Norwalk, Connecticut. The petroleum distillate shown as ingredient 10 of Group C is a mixture of isoparaffins containing hydrocarbons having ten to twelve carbon atoms, sold under the trademark ISOPAR® L by the Exxon Chemical Company, Houston, Texas. The preservative GERMABEN® II-E shown as ingredient 13 in Group E, is a product and a trademark of Sutton Laboratories of Chatham, New Jersey. The silicone pressure sensitive adhesive used as the film forming agent in the mascara compositions in Table I appears in Group D as ingredient 12B. In Table I, an "in situ" emulsifier is employed in the form of the compound triethanolamine stearate which is formed by the combination of triethanolamine (Ingredient 3) and stearic acid (Ingredient 8). Example I Mascara compositions B-H in the form of oil in water emulsions were prepared by heating ingredient 1 and adding ingredients 2 and 3, in that order. The mixture of ingredients 1-3 was covered and heated to 85°C. The pigment ingredients 4 and 5 of Group B were added to the ingredients 1-3 of Group A and disperesed using a homomixer. The ingredients of Groups A and B were maintained at 85°C. All of the ingredients of Group C were heated together to 80°C. and added to Groups A and B using a propeller mixer. Groups A, B and C were mixed at 80°C. for fifteen minutes, cooled to 50°C. and the ingredients of Group D were added. Groups A, B, C and D were cooled to 35°C. and the preservative of Group E was added. The mascara compositions were filled into vials and evaluated in Examples II and III. Example II The mascara compositions in Table I were evaluated for shelf stability and found to be stable at temperatures of 40 and 45°C. after a period of six months. Example III Mascara compositions B-H in Table I were evaluated in vivo by volunteers. The volunteers applied the mascara compositions to their eyelashes and attempted to wash off the mascara. Each mascara composition was evaluated on the basis of its difficulty to wash off the eye lashes using water, as well as soap and water. The volunteers reported that mascara composition F which is representative of the present invention, was one of the most difficult to wash off. In the tests, Composition F was evaluated against other compositions containing other types of silicone film forming materials shown as ingredients 11A-11C, 12A and 12C, in Table I. Ingredient 11A was an alkylmethyl functional silicone wax containing an alkyl group of thirty carbon atoms. Ingredient 11B was an alkylmethyl functional silicone wax containing an alkyl group of thirty carbon atoms and differed from silicone wax 11A only in the length of the siloxane backbone. The siloxane backbone of wax 11B was shorter than the siloxane backbone of wax 11A. Ingredient 11C was also an alkylmethyl functional silicone wax similar to silicone wax 11A, but wax 11C contained an alkyl group of 22-24 carbon atoms. Ingredient 12C was a high molecular weight silicone gum having the formula HOMe 2 SiO(Me 2 SiO) n SiMe 2 OH in which Me is methyl and n is an integer having a value of ten thousand. The film forming silicone Ingredient 12A was an aqueous latex of a crosslinked polydiorganosiloxane prepared by a method essentially consisting of: (A) homogenizing a mixture essentially consisting of (1) one hundred parts by weight of polydiorganosiloxane of the formula HO(R 2 SiO) x H wherein R is a radical selected from the group consisting of methyl, ethyl, propyl, phenyl, vinyl, allyl and 3,3,3-trifluoropropyl and x is an integer having an average value of three to one hundred; (2) 15-75 millimoles of surface active anionic catalyst per kilogram of polydiorganosiloxane wherein said catalyst is selected from the group consisting of dodecylbenzene sulfonic acid and hydrogen lauryl sulfate; and (3) water, to yield an oil in water emulsion; (B) admixing 0.5-15 parts by weight of an alkoxy silicon compound selected from the group consisting of (i) silanes of the formula R' a Si(OR 3 ) 4-a wherein R' is a monovalent hydrocarbon radical having up to twelve carbon atoms, R 3 is an alkyl radical having one to six carbon atoms and a has a value of zero or one; (ii) a partial hydrolyzate of the silane which is soluble in the polydiorganosiloxane; and (iii) mixtures of the silane and the partial hydrolyzate; (C) maintaining the emulsion at a temperature of 15 to 30°C. for at least five hours at a pH of less than five until a crosslinked polymer emulsion is formed; (D) admixing sufficient base to raise the pH of the crosslinked polymer emulsion to greater than seven; and optionally (E) admixing greater than one part by weight of collodial silica sol or colloidal silsesquioxane; to yield a latex which produces an elastomer upon removal of the water at room temperature. Details of the aqueous latex and examples of a process for its manufacture are set forth in U.S. Patent No. 4,584,341. The aqueous latex is also available commercially from Dow Corning Corporation, Midland, Michigan, USA. The testing results reported by the volunteers were confirmed by independent testing of mascara composition F against other mascaras containing organic film forming agents such as polyvinylpyrrolidone and acrylate based polymers. While Examples I-III and Table I are directed to mascara compositions in the form of oil in water emulsions, water in oil emulsions may be formulated as well. Further, the silicone pressure sensitive adhesive may be used in the preparation of other pigmented eye cosmetic preparations such as eyebrow pencils and liquids, eye shadow, eyeliner and eye cream. In addition, it is contemplated that mascara compositions containing the adhesive as the film forming agent may be formulated as cake or block mascara, liquid mascara or cream mascara products, as well as solvent compatible compositions and anhydrous preparations. Waxes which may be employed in preparing mascara compositions in accordance with the present invention include carnauba, beewax, ceresin, paraffin, candelilla, bayberry, montan, spermaceti, castor wax, ozokerite, Fisher-Tropsch waxes and microcrystalline waxes. Suitable oils include castor oil, olive oil, jojoba oil, stearic acid, lanolin alcohols, paraffin oil and silicone oils. Examples of pigments include iron oxide, titanium oxide, ultramarine, chromium oxide, carbon black and any of the United States Government Food & Drug Administration (FDA) certified organic dyes and lakes. Preservatives include methyl paraben, propyl paraben, butyl paraben, diazolidinyl urea and imidazolidinyl urea. It may be desirable to incorporate in the mascara composition other conventional ingredients such as emulsifiers and surfactants; humectants such as glycerine; perfumes, sunscreen compounds; vitamins; hormones; amino acids; antioxidants such as propyl, octyl and dodecyl, esters of gallic acid, butylated hydroxyanisole, butylated hydroxytoluene and nordihydroguaiaretic acid; extenders such as talc, mica, kaolin and cericite; feel modifiers such as organic esters and silicone fluids; opacifiers such as titanium dioxide and fatty alcohols; fragrances; and solvents such as ethanol, isopropanol and volatile silicones such as hexamethyldisiloxane and octamethylcyclotetrasiloxane. A mascara formulation in accordance with the present invention will preferably contain 5-20 percent by weight or, most preferably, ten percent by weight, of the silicone pressure sensitive adhesive; 20-60 percent by weight or most preferably 30-50 percent by weight, of water; 4-10 percent by weight of a wax or a mixture of waxes; 10-20 percent by weight of one or more pigments; one percent by weight or less of a preservative; 5-15 percent by weight of one or more surfactants or emulsifiers; 0.2-3.0 percent by weight of a thickener; zero to one percent by weight of a feel modifier; and 1-4 percent by weight of an opacifier. The concept of the present invention is further illustrated by reference to Table II which shows five (5) sunscreen compositions A-E which were prepared. The various ingredients of the sunscreen compositions A-E are grouped as Phases A, B and C. Ingredients in Table II which correspond to ingredients in Table I above are similarly identified. Any differences are noted below. INGREDIENTS SUNSCREEN COMPOSITIONS (WEIGHT PERCENT) PHASE A: A B C D E 1. Water 68.21 63.21 70.71 68.57 70.71 2. Polyacrylate (CARBOPOL®940) 0.14 0.14 0.14 0.14 0.14 3. GLYCERIN 2.50 2.50 2.50 2.50 2.50 4. Methyl Paraben 0.15 0.15 0.15 0.15 0.15 5. Triethanolamine 1.40 1.40 1.40 1.40 1.40 PHASE B: 6. Stearic Acid 4.00 4.00 4.00 4.00 4.00 7. Cetyl Alcohol 1.00 1.00 1.00 1.00 1.00 8. DEA-Cetyl Phosphate (AMPHISOL) 1.00 1.00 1.00 1.00 1.00 9. Propyl Paraben 0.10 0.10 0.10 0.10 0.10 PHASE C: 10. C 12 -C 15 Alkylbenzoate (FINSOLV®TN) 4.00 4.00 4.00 4.00 4.00 11. 2-ethylhexyl-p-methoxycinnimate PARSOL®MCX 7.00 7.00 7.00 7.00 7.00 12. 2-hydroxy-4-methoxybenzophenone UVINUL®M-40 3.00 5.00 3.00 3.00 3.00 13A.Silicone Pressure Sensitive Adhesive 7.50 - - - - 13B.Acrylates Polymer POLYTRAP® - 12.50 - - - 13C.Silicone Polymer - - 5.00 - - 13D.Crosslinked Cationic Emulsion of Polydimethylsiloxane - - - 7.14 - 13E.Aqueous Silicone Latex - - - - 5.00 In Table II, the polyacrylate thickener CARBOPOL® 940 in Phase A is a product and trademark of the B.F. Goodrich Company of Cleveland, Ohio. Glycerin was present in Phase A as a humectant. The anionic surfactant AMPHISOL® in Phase B is a trademark and a product of Givaudan Corporation, Clifton, New Jersey. Cetyl alcohol was present in Phase B as an opacifier. The solubilizer FINSOLV® TN in Phase C is a product and a trademark of Finetex Incorporated of Elmwood Park, New Jersey. The sunscreen compound PARSOL® MCX in Phase C is a product and a trademark of Givaudan Corporation of Clifton, New Jersey. The sunscreen compound UVINUL® M-40 in Phase C is a product and a trademark of BASF Corporation of Parsippany, New Jersey. The acrylates polymer POLYTRAP® in Phase C is a product and trademark of the Dow Corning Corporation, Midland, Michigan. POLYTRAP· is a micrometer sized powder of macroporous particulates and is described in various patents including U.S. Reissue Patent 33429 and U.S. Patent No. 5,035,890. The silicone polymer 13C was a dimethylvinyl endblocked trifluoropropylmethyl siloxane polymer. The silicone ingredient 13D was a water thin white emulsion which had a silicone content of thirty-five percent by weight in water and a pH of six. Example IV Sunscreen compositions A-E in Table II were prepared by mixing together the ingredients of Phase A and heating the mixture to 76°C. The ingredients of Phase B were mixed together in order and heated to 75°C. Phase B was added to Phase A and the temperature was maintained. Ingredients 10-12 of Phase C were mixed together in order and heated until dissolved. This portion of Phase C was added to ingredient 13A-E as appropriate and all of Phase C was added to Phases A and B at 50°C. The sunscreen compositions were stirred until a temperature of 40°C. was reached and filled into vials for evaluation. Example V Sunscreen compositions A-E were evaluated in vivo by volunteers. The amount of sunscreen composition remaining on the skin after eighty minutes of soaking was determined by Fourier-Transform Infrared Spectroscopy (FTIR). The sunscreen compositions A-E were evaluated against a commercial sunscreen product containing a GANEX® resin as the film forming agent. GANEX® is a polyvinylpyrrolidone based polymer commonly used in consumer sunscreen products and is a product and trademark of International Specialty Products of Wayne, New Jersey. It was determined that the sunscreen composition A of the present invention was one of the best performers against GANEX®. Slightly more than thirty-five percent of the sunscreen composition A which contained the adhesive remained on the skin. By comparison, only thirty percent of the sunscreen containing GANEX® as the film forming agent remained on the skin. Sunscreen compositions according to the present invention may be formulated as oils, lotions, creams or gels. In those instances where a composition is in the form of an oil in water emulsion or a water in oil emulsion, one or more surfactants may be required. Suitable surfactants include one or more of the various categories of silicon-free organic emulsifiers. These emulsifiers, it is noted, may be used in combination with certain polydiorganosiloxane-polyoxyalkylene copolymers, as explained in U.S. Patent No. 4,122,029 and in U.S. Patent No. 4,311,695. Sunscreen agents according to the invention are used in amounts which are within the restricted limits or less, as established by the US Government Food & Drug Administration. Representaive sunscreen agents or mixtures of such agents which may be used in the preparation of the compositions of the invention include 4-aminobenzoic acid; homomethyl salicylate; 2-hydroxy-4-methoxy benzophenone; 2-phenylbenzimidazol-5-sulfonic acid; 4-dimethyl amino benzoic acid-2-ethylhexyl ester; 4-methoxy cinnamic acid isoamyl ester; 4-methoxy cinnamic acid-2-ethylhexyl ester; 3-(4'-methyl) benzylidine-bornane-2-one; 1-(4'-isopropylphenyl)-3-phenyl-1-propane-1,3-dione; and 1-(4'-t-butylphenyl)-3-(4-methoxyphenyl)-propane-1,3-dione. Among the various moisturizing oils which may be used in order to formulate sunscreen compositions are mineral oil, peanut oil, sesame oil, avocado oil, coconut oil, cocoa butter, almond oil, safflower oil, corn oil and cotton seed oil. Other oils may be added for the purpose of improving the spreadability of the sunscreen composition such as silicone fluids; and fatty acid esters such as isopropyl myristate, isopropyl palmitate, isopropyl stearate, butyl stearate and cetyl stearate. Other conventional adjuvants necessary to produce acceptable consumer sunscreen products may be included in the compositions such as antioxidants, preservatives, fragrances and perfumes, emulsifiers, humectants and solvents. A sunscreen formulation in accordance with the present invention will preferably contain 5-20 percent by weight or, most preferably, ten percent by weight, of the silicone pressure sensitive adhesive; 20-60 percent by weight or, most preferably, 30-50 percent by weight, of water; one percent by weight or less of a preservative; 4-8 percent by weight of one or more surfactants or emulsifiers; 0.1-2.0 percent by weight of a thickener; zero to five percent by weight of a feel modifier; 0.2-1.0 percent by weight of a fragrance; and 1-4 percent by weight of an opacifier. The cosmetic compositions set forth above in Tables I and II and in Examples I-V, when applied to the skin, leave a flexible and stretchable film on the surface of the skin. Therefore, active ingredients included in these cosmetic products such as sunscreen compounds for example, will tend to be bound in the flexible film and will remain in place on the skin significantly longer, despite sweating, swimming and exercise. Further, the compositions exhibit improved physical resistance and hence are physically difficult to rub off from the skin. These obvious advantages of the compositions according to the present invention can be attributed to the presence in the compositions of the silicone pressure sensitive adhesive. Non-volatile silicone fluids which may be used in the preparation of the compositions of the present invention are organic polysiloxanes having a viscosity in the range of 5 to as high as several million mm 2 /s (centistokes), preferably 100 to 10,000 mm 2 /s (centistokes). A mixture of polysiloxanes having relatively higher and relatively lower viscosities can employed. Such polysiloxanes have the repeating unit wherein n is an integer having a value greater than 1; R 1 and R 2 are alkyl radicals of one to seven carbon atoms or a phenyl group; and R 1 and R 2 may be the same or different. Illustrative polysiloxanes are polydimethylsiloxane, polydiethylsiloxane, polymethylethylsiloxane, polymethylphenylsiloxane, polydiphenylsiloxanes and copolymers of two or more of the foregoing siloxanes. In some instances, it may be desirable to include a volatile silicone fluid in the compositions of the present invention. Suitable fluids are low viscosity methylsilicone fluids. The volatile low viscosity methylsilicone fluid corresponds to the average unit formula (CH 3 ) a SiO (4-a)/2 wherein a is an integer having an average value of from two to three. The methylsilicone fluid contains siloxane units joined by Si-O-Si bonds. Representative units are (CH 3 ) 3 SiO 1/2 , (CH 3 ) 2 SiO 2/2 , (CH 3 )SiO 3/2 and SiO 4/2 . These units are present in molar amounts such that there is provided an average of from two to three methyl groups per silicon atom in the methylsilicone fluid, whereby the methylsilicone fluid has a viscosity of less than one hundred mm 2 /s (centistokes) measured at 25°C. The volatile, low viscosity methylsilicone fluid contains dimethylsiloxane units and optionally trimethylsiloxane units. Preferably, the methylsilicone fluid has a viscosity of less than ten mm 2 /s (centistokes). Representative compounds are cyclopolysiloxane compounds of the general formula [(CH 3 ) 2 SiO] x and linear siloxane compounds of the general formula (CH 3 ) 3 SiO[(CH 3 ) 2 SiO] y Si(CH 3 ) 3 , in which x is an integer having a value of from three to ten and y is an integer having a value of from zero to four. The volatile, low viscosity methylsilicones have boiling points generally less than 250°C. and possess viscosities preferably generally less than ten mm 2 /s (centistokes) measured at 25°C. Most preferably, the viscosity is 0.65 to 5.0 mm 2 /s (centistokes). The cyclopolysiloxane compounds have been assigned the adopted name "CYCLOMETHICONE" by The Cosmetics, Toiletries and Fragrance Association, Inc., Washington, D.C. (CTFA). Both the cyclopolysiloxanes and the linear siloxanes are clear fluids and are essentially odorless, nontoxic, nongreasy and nonstinging. Cosmetically, these methylsilicone fluids are nonirritating to skin and exhibit enhanced spreadability and ease of rub-out when applied. Once applied, the materials evaporate leaving behind no residue. Methylsilicone fluids which are operable in accordance with the present invention leave substantially no residue after thirty minutes at room temperature when one gram of fluid is placed at the center of a No. 1 circular filter paper having a diameter of 185 mm supported at its perimeter in open room atmosphere. By methylsilicone fluid is meant a composition containing two or more silicon atoms, all of which are bonded by way of at least one oxygen atom to at least one other silicon atom and at least one methyl radical, each silicon valence not satisfied by oxygen being satisfied by a methyl radical. Representative methylsilicone fluids found to be especially useful in accordance with the present invention are hexamethyldisiloxane which has a boiling point of 99.5°C. and the formula Me 3 SiOSiMe 3 ; octamethyltrisiloxane which has a boiling point of 152°C. and the formula Me 3 SiOMe 2 SiOSiMe 3 ; hexamethylcyclotrisiloxane which has a boiling point of 133°C. and the formula [(Me 2 )SiO] 3 ; octamethylcyclotetrasiloxane which has a boiling point of 171°C. and the formula [(Me 2 )SiO] 4 ; and decamethylcyclopentasiloxane which has a boiling point of 205°C. and the formula [(Me 2 )SiO] 5 . These methylsilicone fluids may be used alone or as mixtures in combinations of two or more. Mixtures of the methylsilicone fluids will result in a volatile material having an evaporating behavior different from any one of the individual methylsilicone fluids. The methylsilicone fluids and methods for their preparation are known in the art and such fluids are commercially available. In some instances, it may be desirable to replace one or more of the methyl groups in the methylsilicone fluid with other groups. Thus, there may be substituted groups such as alkyl radicals having two to twelve carbon atoms; aryl radicals having six to ten carbon atoms; amine groups; vinyl; hydroxyl; haloalkyl groups; aralkyl groups; and acrylate groups, for example. The compositions of this invention may contain a surfactant such as an anionic and amphoteric surfactant. Suitable anionic surfactants include sulfonated and sulfated alkyl, aralkyl and alkaryl anionic surfactants; alkyl succinates; alkyl sulfosuccinates and N-alkyl sarcosinates. Representative surfactants are the sodium, magnesium, ammonium and the mono-, di- and triethanolamine salts of alkyl and aralkyl sulfates as well as the salts of alkaryl sulfonates. The alkyl groups of the surfactants generally have a total of from 12 to 21 carbon atoms, may be unsaturated and are preferably fatty alkyl groups. The sulfates may be sulfate ethers containing one to ten ethylene oxide or propylene oxide units per molecule. Preferably, the sulfate ethers contain 2 to 3 ethylene oxide units. Typical anionic surfactants include, among others, sodium lauryl sulfate, sodium lauryl ether sulfate, ammonium lauryl sulfate, triethanolamine lauryl sulfate, sodium C14-16 olefin sulfonate, ammonium pareth-25 sulfate (ammonium salt of a sulfated polyethylene glycol ether of a mixture of synthetic C12-15 fatty alcohols), sodium myristyl ether sulfate, ammonium lauryl ether sulfate, disodium monooleamidosulfosuccinate, ammonium lauryl sulfosuccinate, sodium dodecylbenzene sulfonate, triethanolamine dodecylbenzene sulfonate and sodium N-lauroyl sarcosinate. Organic compounds of phosphoric acid may also be used such as diethanolamine salts of cetyl phosphate, one of which is DEA-Cetyl Phosphate. Surfactants generally classified as amphoteric or ampholytic include cocoamphocarboxyglycinate, cocoamphocarboxypropionate, cocobetaine, N-cocamidopropyldimethylglycine and N-lauryl-N-carboxymethyl-N-(2-hydroxyethyl)-ethylenediamine. Other suitable amphoteric surfactants include the quaternary cycloimidates, betaines and sultaines disclosed in U.S. Patent No. 3,964,500. The betaines may have the structure: R 1 R 2 R 3 N + (CH 2 ) m COO - wherein R 1 is an alkyl group having 12 to 18 carbon atoms or a mixture thereof, R 2 and R 3 are independently lower alkyl groups having 1 to 3 carbon atoms and m is an integer from 1 to 4. Specific betaines are alpha-(tetradecyldimethylammonio)acetate, beta-(hexadecyldiethylammonio)propionate and gamma(dodecyldimethylammonio)butyrate. The sultaines may have the structure: R 1 R 2 R 3 N + (CH 2 ) m SO 3 - wherein R 1 , R 2 , R 3 and m are defined as above. Specific useful sultaines are 3-(dodecyldimethylammonio)-propane-1-sulfonate and 3-(tetradecyldimethylammonio)ethane-1-sulfonate. The compositions of this invention may contain a nonionic surfactant which is a fatty acid alkanolamide or amine oxide surfactant. The fatty acid alkanolamides are nonionic surfactants obtained by reacting alkanolamines such as monoethanolamine, diethanolamine, monoisopropanolamine or diisopropanolamine with a fatty acid or fatty acid ester to form the amide. The hydrophobic portion of the nonionic surfactant is provided by a fatty acid hydrocarbon chain which generally has from 10 to 21 carbon atoms. The fatty acid alkanolamide surfactants include, fatty acid diethanolamides such as isostearic acid diethanolamide, lauric acid diethanolamide, capric acid diethanolamide, coconut fatty acid diethanolamide, linoleic acid diethanolamides, myristic acid diethanolamide, oleic acid diethanolamide and stearic acid diethanolamide; fatty acid monoethanolamides such as coconut fatty acid monoethanolamide; and fatty acid monoisopropanolamides such as oleic acid monoisopropanolamide and lauric acid monoisopropanolamide. The amine oxides are known nonionic surfactants obtained by oxidizing a tertiary amine to form the amine oxide. They are sometimes referred to as polar nonionic surfactants. Amine oxide surfactants include, the N-alkyl amine oxides such as N-cocodimethylamine oxide, N-lauryl dimethylamine oxide, N-myristyl dimethylamine oxide and N-stearyl dimethylamine oxide; the N-acyl amine oxides such as N-cocamidopropyl dimethylamine oxide and N-tallowamidopropyl dimethylamine oxide; and N-alkoxyalkyl amine oxides such as bis(2-hydroxyethyl) C 12-15 alkoxy-propylamine oxide. The hydrophobic portion of the amine oxide surfactants is generally provided by a fatty hydrocarbon chain containing from 10 to 21 carbon atoms. Representative surfactants include lauric acid diethanolamide, N-lauryl dimethylamine oxide, coconut acid diethanolamide, myristic acid diethanolamide and oleic acid diethanolamide. Additional categories of surfactants may be included such as cationic and zwitterionic surfactants and representative compounds are set forth in detail in U.S. Patent No. 4,902,499. Suitable thickeners which may be employed are sodium alginate, gum arabic, polyoxyethylene, guar gum, hydroxypropyl guar gum, cellulose derivatives such as methylcellulose, methylhydroxypropylcellulose, hydroxypropylcellulose, polypropylhydroxyethylcellulose, starch and starch derivatives such as hydroxyethylamylose and starch amylose, locust bean gum, electrolytes such as sodium or ammonium chloride, saccharides such as fructose and glucose and derivatives of saccharides such as PEG-120 methyl glucose dioleate.

Claims: A personal care preparation comprising a film forming agent and a pigment or at least one ultraviolet light absorbing compound, characterized by the film forming agent being a non-flammable hot-melt silicone pressure sensitive adhesive composition comprising a mixture of (i) a silicone resin and (ii) a silicone fluid, the mixture of (i) and (ii) exhibiting tackiness and adhesiveness, the mixture of (i) and (ii) being blended with (iii) 0.5 to 20 weight percent, based on the total weight of the silicone resin and the silicone fluid, of a phenyl-containing polysiloxane fluid having a viscosity at 25°C. of 5 to 60,000 mm 2 /s (centistokes). A personal care preparation according to claim 1 in which said non-flammable hot-melt silicone pressure sensitive adhesive composition comprises a mixture of: (i) 40 to 70 parts by weight of a trimethylsilyl-endblocked low molecular weight hydrocarbon or benzene soluble resinous copolymer containing silicon bonded hydroxyl radicals and comprising triorganosiloxy units of the formula R'''' 3 SiO 1/2 and tetrafunctional siloxy units of the formula SiO 4/2 in a ratio of 0.6 to 0.9 triorganosiloxy units per tetrafunctional siloxy unit present in the copolymer molecule and R'''' is a monovalent hydrocarbon radical of one to six carbon atoms; (ii) 30 to 60 parts by weight of a silanol-endblocked polydiorganosiloxane fluid, wherein the total parts by weight of the resinous copolymer and the silanol-endblocked polydiorganosiloxane fluid equals 100 parts; the mixture of (i) and (ii) exhibiting tackiness and adhesiveness and blended with: (iii) 0.5 to 20 weight percent, based on the total weight of the resinous copolymer and the silanol-endblocked polydiorganosiloxane fluid, of a phenyl-containing polysiloxane fluid of the formula A 3 SiO[Si(C 6 H 5 )(R')O] x [Si(R 2 )O] y SiB 3 wherein R is a monovalent radical selected from -OSiR'' 3 , hydrocarbon radicals of one to three carbon atoms and -OH; R' is a monovalent radical selected from -OSiR'' 3 , -OH and -CH 3 ; R'' is a monovalent hydrocarbon radical of one to three carbon atoms; A and B are endblocking units selected from -OSiR''' 3 where R''' is a hydrocarbon radical of one to eight carbon atoms, -OH, halide radicals and amine radicals; x is an integer having a value greater than zero; and the value of x and y is such that the phenyl-containing polysiloxane fluid has a viscosity at 25°C. of 5 to 60,000 mm 2 /s (centistokes) and has 1 to 100 phenyl groups per 100 siloxane units. The personal care preparation according to claim 1 or claim 2 which includes 5-20 percent by weight of the silicone pressure sensitive adhesive composition. The personal care preparation according to any of claims 1 to 3 which comprises an ultraviolet light absorbing compound which is 2-ethylhexyl-p-methoxycinnamate or 2-hydroxy-4-methoxybenzo-phenone. Use of a cosmetic personal care preparation according to claim 4 as a cosmetic sunscreen preparation. Use of a cosmetic personal care preparation according to claims 1 to 3, in which said cosmetic personal care preparation comprises a pigment, a wax and an oil, as an eye cosmetic. Use according to claim 6, in which said eye cosmetic is in the form of an eyebrow pencil, eyebrow liquid, eyeshadow, eyeliner, eyecream or mascara. An eye cosmetic selected from an eyebrow pencil, eyebrow liquid, eyeshadow, eyeliner, eyecream or mascara comprising a personal care preparation according to any of claims 1 to 3. A sunscreen preparation comprising a personal care preparation according to claim 4.

Inventors: KRZYSIK DUANE G, KRZYSIK, DUANE G.
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1994
Main classification: A61K7
IPC codes: A61Q1, A61K8, C08L83, A61Q17