BiCMOS process

Abstract: A merged BiCMOS device 10 having a bipolar transistor 60 and a PMOS transistor 64 formed in the same well region 18. Bipolar transistor 60 is comprised of an emitter electrode 30, base region 26, and collector region formed by well region 18. Emitter electrode 30 is separated from base region 26 by thick oxide 24. Tungsten-silicide layer 32 covers emitter electrode 30. PMOS transistor 64 comprises source/drain regions 52 and 52a, gate electrode 40, and gate oxide 36. PMOS transistor 64 may optionally comprise LDD regions 44. Source/drain region 52a is in contact with base region 26. If desired, the emitter electrode 30 and gate electrode 40 may be silicided.

Description: FIELD OF THE INVENTION This invention generally relates to semiconductor processing and more specifically to BiCMOS processes. BACKGROUND OF THE INVENTION The integration of MOSFET structures and bipolar transistors on a single substrate has become very desirable. As is well known in the art, digital and linear functions are often performed by integrated circuits using either bipolar or metal-oxide semiconductor (MOS) technology. Bipolar integrated circuits, of course provide higher speed operation and greater drive currents than the MOS circuits, at the cost of higher power dissipation, especially when compared against complementary MOS (CMOS) circuits. Advances in manufacturing technology have allowed the use of both bipolar and CMOS transistors in the same integrated circuit (commonly referred to as BiCMOS devices). Bipolar transistors are typically formed by using a moat region for the base of the bipolar transistor, doped polysilicon for the emitter, and a well region for the collector. Additional moat regions are then used to form any source/drain regions of PMOS transistors. Further exploitation of the high current driving capabilities of the bipolar transistor is important to obtaining even higher levels of bipolar or merged bipolar CMOS integration. A BiCMOS device as defined in the precharacterizing part of claim 13 is known from US-A-4,868,135. That document further discloses a method for fabricating a BiCMOS device. The process steps include forming the reach-through N+ subcollector to the bipolar device without extra processing steps; combining into one mask the threshold adjust/well implants with self-aligned isolation leakage protection implants by using a self-aligned, removable oxide mask prior to field isolation; using a resist etch-back scheme to protect against emitter-to-base punch-through via self-aligning the pedestal and base; and also providing for the removal of the gate oxide at the emitter while maintaining it at the FET, without extra masks. To achieve a low resistivity, a silicide is formed on the polysilicon for the gates and emitters and a CVD oxide or intrinsic polysilicon is used to cap the silicide. The gate/emitter stacks are then patterned by directional etching. Reference is further made to US-A-5,031,020, which discloses a semiconductor device comprising a P channel MOSFET having a gate, a source, and a drain, and a bipolar transistor having a collector, a base, and an emitter. The semiconductor device also includes an N- collector diffusion layer formed in an epitaxial layer on a P-type semiconductor substrate and adjacent to an N+ buried collector diffusion layer, and an N+ electrode lead-out region formed in contact with the N+ buried collector diffusion layer having an impurity concentration higher than the N-collector layer. A gate electrode section constituted by a gate oxide film and a gate electrode is formed on the N- collector layer and the N+ electrode lead-out region, and a P-type impurity is iron-implanted into the source region of the P channel MOSFET and an N-type impurity is doped into the emitter region of the bipolar transistor, with the gate electrode section being used as a mask. Furthermore, a P-type impurity is iron-implanted into a common area of the drain region of the P channel MOSFET and the base region of the bipolar transistor and is diffused into the common area to a preset depth. SUMMARY OF THE INVENTION A BiCMOS device comprising the features of claim 13 is disclosed. The method of the invention comprises the steps of claim 1. An advantage of the invention is providing a simplified process forming a merged BiCMOS device. These and other advantages will be apparent to those of ordinary skill in the art having reference to this specification in conjunction with the drawings. BRIEF DESCRIPTION OF THE DRAWINGS In the drawings: FIG. 1 is a cross-sectional diagram of the preferred embodiment of the invention; and FIGs. 2a-j are cross-section diagrams showing various stages of fabrication of the preferred embodiment of the invention. Corresponding numerals and symbols in the different figures refer to corresponding parts unless otherwise indicated. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS The preferred embodiment of the invention is described herein as incorporated into a BiCMOS structure having a bipolar transistor and a PMOS transistor merged into the same well region. Figure 1 illustrates, in cross-section, bipolar transistor 60 and p-channel transistors 64 and 68. The structure is formed into a substrate 12 which, in this embodiment is p-type silicon. Buried n+ region 14 in bipolar transistor 60 serves as a subcollector, in the conventional manner, with n+ region 25 providing a surface contact thereto. N region 18a serves as the collector region in bipolar transistor 60 and as the well region for p-channel transistors 64. N region 18b is the well region for p-channel transistor 68. Intrinsic base 26 is a p-type region disposed within n region 18a-b. Emitter electrode 30 may be a doped polysilicon layer which extends through an opening in insulator layer 24 to intrinsic base region 26. Tungsten-silicide layer 32 covers emitter electrode 30. P+ region 52a serves as both the extrinsic base region of bipolar transistor 60 and as one of the source/drain regions for p-channel transistor 64. P+ regions 52 serve as the remaining source/drain regions for p-channel transistors 64 and 68. Doped polysilicon may be used to form gates 40 of transistors 64 and 68. Gate oxide 36 is disposed between gates 40 and n regions 18. Buried region 16 is located below region 20. Field insulating regions 22 isolate intrinsic base region 26 from collector contact 25 and p-channel transistors 64 and 68 from each other. Gates 40 may optionally be silicided to form TiSi 2 layer 56. N+ regions 14 below transistors 64 and 68 are separated by buried p region 16 and n regions 18a-b are separated by p region 20 to allow the n-type regions 18a-b of the two transistors to be at different potentials. Figure 2a illustrates structure 10 after the formation on n+ buried layers 14, p buried layers 16, n-type regions 18a-b, p-type regions 20, field insulating regions 22, and insulator layer 24. Methods for forming the buried layers are described in U.S. Patent No. 4,958,213, issued September 18, 1990 and assigned to Texas Instruments Incorporated. A method for forming field insulating regions 22 is described in U.S. Patent No. 4,541,167, issued September 17, 1985 and assigned to Texas Instruments Incorporated. Insulator layer 24 may be a dummy gate oxide formed via an Anti Kooi oxidation followed by a deglaze to a thickness of less than 2 nm (20 Å) followed by a thermal oxidation to a thickness on the order of 30 nm (300 Å). The formation of a merged BiCMOS device according to the invention into the structure of Figure 2a will now be described. The surface of structure 10 is patterned and implanted using a n-type dopant to form a deep n-type region (collector contact 25) that extends through n region 18 to contact the subcollector, n+ region 14, as shown in Figure 2b. Next, the V t adjust implants may be performed: one for NMOS transistors (not shown) and one for PMOS transistors 64 and 68. Still referring to Figure 2b, the base region 26 is patterned and implanted with a p-type dopant (e.g. boron 7.0E13 cm at 10Kev). Referring to Figure 2c, masking layer 27 is used to expose a region of dummy oxide layer 24. The exposed oxide is then etched to expose a portion of base region 26. Masking layer 27 is then removed and a deglaze is performed (e.g., 10% HF for 10 seconds) to minimize the interfacial oxide. Referring to Figure 2d, a layer of conductive material, such as polysilicon layer 29, is deposited to a thickness on the order of 250 nm (2500 A). Next, polysilicon layer 29 may be doped n-type via ion implantation. Alternatively, the polysilicon may be doped in-situ during deposition. A layer of tungsten silicide WSi 2 32 is deposited over polysilicon layer 29. WSi 2 32 may have a thickness on the order of 50 nm (500 A) or greater. Next, WSi 2 layer 32 is annealed. Polysilicon layer 29 and WSi 2 32 are then patterned and etched as shown in Figure 2e to form emitter electrode 30. WSi 2 layer 32 prevents oxidation of emitter electrode 30 during subsequent processing steps. Referring to Figure 2f, the exposed portions of dummy oxide layer 24 are then removed using a deglaze and replaced with an insulator layer such as gate oxide layer 36. Gate oxide layer 36 maybe formed by thermal oxidation and have a thickness on the order of 10 nm (100 A). During the growth of gate oxide layer 36, oxide 37 will form on the vertical edges of emitter electrode 30 and silicon dioxide layer 35 will form on WSi 2 32, as shown in Figure 2f. The thermal oxidation maybe performed at a temperature high enough to also serve as the emitter anneal. In the preferred embodiment a temperature on the order of 900° is used. A second layer of conductive material, such as polysilicon layer 39, is deposited by way of LPCVD over the surface of structure 10, as shown in Figure 2f. Polysilicon layer 39 has a thickness on the order of 350 nm (3500 A). Polysilicon layer 39 may then be doped via ion implantation. Alternatively, polysilicon layer 39 may be doped y other means such as in situ doping or gas phase doping (with for example POCl 3 ) as is well known in the art. Polysilicon layer 39 is patterned and etched to form gates 40, as shown in Figure 2g. Silicon dioxide layer 35 will serve as an etchstop during the polysilicon gate etch. Referring to Figure 2h, a layer of tetraethoxysylane (TEOS)42 is deposited over the surface. Conventional techniques are then used to implant lightly doped drains (LDDs) 44, form sidewall spacers 48, and form source/drain regions 52. It should be noted that LDDs 44 are optional and need not be formed. Sidewall spacers 48 may be formed by depositing a dielectric layer and anisotropically etching the dielectric layer. Sidewall spacers 48 preferably comprise silicon nitride. However, oxide or disposable polysilicon may alternatively be used. After sidewall spacers 48 are formed, source/drain regions 52 are implanted and annealed. Because the doped emitter electrode was previously "annealed" during the formation of oxide layer 36, source/drain regions 52 may be annealed at lower temperatures (on the order of 850°C) thereby reducing short channel effects. TEOS layer 42 and silicon dioxide layer 35 are then removed as shown in Figure 2i. Next, the gates 40 and source/drain regions 52 and 52a may be silicided. A layer of refractory metal (not shown) is deposited over the surface of structure 10. The structure is annealed using a rapid thermal anneal, or alternatively a furnace anneal, in a nitrogen-containing ambient. This causes the layer of refractory metal to react with any exposed silicon to form silicide. Referring to Figure 2j, silicide layer 56 is formed above gates 40 and source/drain regions 52 and 52a. Elsewhere, a layer of refractory metal-nitride and/or unreacted metal (not shown) is formed. The layer of refractory metal-nitride is then removed. Subsequent to the completion of the methods described above, interconnecting metallization is then formed for making contact to the active regions of Figure 1. Methods for forming such interconnections are well known in the art. Individual circuits are then separated from portions of substrate 12 and external connections made thereto by way of wire bonding, direct bump bonding, or the like, as is well known in the art. The individual circuits may then be packaged into a dual-in-line package, a chip carrier, or another type of package. An example of such a package is described in U.S. Patent No. 4,495,376 issued January 22, 1985 and assigned to Texas Instruments, Inc. While this invention has been described with reference to illustrative embodiments, this description is not intended to be construed in a limiting sense. Various modifications and combinations of the illustrative embodiments, as well as other embodiments of the invention, will be apparent to persons skilled in the art upon reference to the description. It is therefore intended that the appended claims encompass any such modifications or embodiments.

Claims: A method for forming a BiCMOS device comprising the sequential steps of: forming a first insulator layer (24) over a surface of a semiconductor body having a well region (18a); implanting a base region (26) in a first portion of said well region (18a); etching said first insulator layer (24) to expose a portion of said base region (26); forming a first doped conductive layer (29) over the surface of said semiconductor body; depositing a tungsten-silicide layer (32) over said first conductive layer (29); etching said tungsten-silicide layer (32) and said first conductive layer (29) to form an emitter electrode (30) and to expose a portion of said first insulator layer (24); and then, forming a plurality of PMOS transistors (64, 68), wherein at least one of said PMOS transistors (64) has a first source/drain region (52a) formed in said well region (18a) and in contact with said base region (26), wherein said step of forming said plurality of PMOS transistors comprises the steps of: removing a portion of said first insulator layer (24) not covered by said emitter electrode (30); growing a second insulator layer (36) on the surface of said semiconductor body and said tungsten-silicide layer (32); forming a plurality of gate electrodes (40) on said second insulator layer, wherein at least one gate electrode is formed over said well region (18a); and forming a plurality of source/drain regions (52) at the surface of said semiconductor body, wherein said plurality of source/drain regions (52) includes said first source/drain region (52a), said first source/drain region (52a) formed between said at least one gate electrode (40) and said emitter electrode (30). The method of claim 1, wherein said step of forming said gate electrodes (40) comprises the step of: forming a second doped conductive layer (39) over the surface of said semiconductor body; and etching said second doped conductive layer (39) to form said plurality of gate electrodes (40), wherein said etch stops on said second insulator layer (36) over said tungsten-silicide layer (32). The method of claim 1, wherein said second insulator layer (36) is grown at a temperature greater than 850° C. The method of claim 1, further comprising the steps of: implanting lightly doped drains (44) on opposite sides of each gate electrode (40) after said step of forming said gate electrodes (40); and forming sidewall spacers (48) adjacent each of said gate electrodes (40) and said emitter electrode (30). The method of claim 1, further comprising the step of siliciding said gate electrodes (40), and said source/drain regions (52). The method of claim 5, wherein said step of siliciding said gate electrodes (40) and said source/drain regions (57) comprises the steps of: depositing a layer of refractory metal over the surface of said semiconductor body; annealing said layer of refractory metal in a nitrogen containing ambient to form a layer (56) of silicide over said gate electrodes (40) and said source/drain regions (52); and etching any unsilicided layer. The method of any preceding claim, wherein said step of forming said source/drain regions (52) comprises the steps of: implanting said source/drain regions; and annealing said source/drain regions at a temperature less than 900° C. The method of any preceding claim wherein said first insulator layer (24) comprises oxide on the order of 30 nm (300 Å) thick and said second insulator (36) layer comprises oxide on the order of 10 nm (100 Å) thick. The method of any preceding claim and wherein said first insulator (24) is formed as an oxide over said surface. The method of any preceding claim and wherein said first conductive layer (29) is formed as a layer of poly-silicon. The method of any preceding claim and including the steps of: growing a gate oxide layer (36) as the second insulator layer over the surface of said semiconductor body; depositing a second conductive layer (39) of polysilicon over said gate oxide layer (36); etching said second polysilicon layer (39) to form a plurality of gate electrodes (40), wherein at least one of said gate electrodes (40) is formed over said first well region (18a); forming sidewall spacers (48) adjacent to said gate electrodes (40) and said emitter electrode (30); implanting source/drain regions (52) at the surface of said semiconductor body on opposite sides of each gate electrode (40); and annealing said source/drain regions (52) at a temperature less than 900° C. A BiCMOS device produced with the method of any preceding claim, comprising a well region (18a), a bipolar transistor (60) having an emitter electrode (30) comprising a layer (29) of polysilicon and a layer (32) of tungsten-silicide located in said well region, and a PMOS transistor (64) located in said well region, said PMOS transistor (64) having a gate (40) comprising doped polysilicon with an overlying layer (56) of silicide other than tungsten-silicide. The BiCMOS device of claim 12, wherein said PMOS transistor (64) has a source/drain region (52a) in contact with a base region (26) of said bipolar transistor (60). The BiCMOS device of claim 12, wherein said bipolar transistor (60) comprises a base region (26), a collector region (18a), an emitter electrode (30) and an oxide region (24) located between said emitter electrode and said base region. The BiCMOS device of claim 14, wherein said PMOS transistor (64) comprises a gate oxide (36), said gate oxide (36) being thinner than said oxide region (24).

Inventors: EKLUND ROBERT H, EKLUND, ROBERT H.
Applicants: TEXAS INSTRUMENTS INC, TEXAS INSTRUMENTS INCORPORATED
Application year: 1994
Main classification: H01L21
IPC codes: H01L21, H01L27