Anaerobically-curable flexible sealant compositions

Abstract: One-part anaerobically curable compositions for producing flexible flange sealants comprising in combination: (A) a flexible urethane type (meth)acrylate prepolymer having a urethane structure in the main chain thereof and having (meth)acrylate end groups, the average molecular weight of the prepolymer (A) being more than 3,000 and less than 10,000, (B) a urethane type (meth)acrylate prepolymer having a urethane structure in the main chain thereof and having (meth)acrylate end groups, the average molecular weight of the prepolymer (B) being the range 1,000 - 3,000, (C) one or more phenyl substituted mono (meth)acrylate monomers which are miscible with or soluble in the prepolymers (A) and (B).

Description: This invention relates to anaerobically-curable sealant compositions which give flexible products when cured. Such compositions are particularly useful for forming a seal between two surfaces such as flanges which are subject to slight movement, for example as a result of differential heat expansion. Flange sealant materials can be subjected to high temperatures and solvent environments, particularly in a motor vehicle engine. It is desirable that the materials maintain their flexibility and integrity under such conditions and also when they return to normal, ambient conditions. U.S. Patent 4,985,523 Mochizuki et . al . describes an anaerobically curing adhesive sealing composition comprising (A) a methacrylate prepolymer having a urethane structure in the main chain thereof and having an average molecular weight of 10,000 or more, and (B) a (meth)acrylate prepolymer having a urethane structure in the main chain thereof and an average molecular weight of at most 5,000 (C) a mono (meth)acrylate monomer represented by the formula (I) wherein R 1 represents a hydrogen atom or a methyl group; and R 2 represents Resins having an average molecular weight of 10,000 or more are not readily available for use as prepolymer (A). Also the monomers (C) are quite specific. U.S. Patent 4,439,600 Moran describes polymerizable compositions which form highly flexible rubber-like polymers or elastomers. The compositions comprise (A) a moderate-to-long chain di or polyfunctional prepolymer having vinyl reactive ends, and (B) a mono(meth)acrylate monomer, such as 3-phenoxy-2-hydroxypropyl methacrylate. All of the prepolymers in the Moran examples were made by reacting a polyether diol or a polyester diol with an aromatic diisocyanate i.e. toluene diisocyanate. Tests have shown that while the products of the Moran examples have high flexibility when cured, this flexibility is lost on ageing at elevated temperature. U.S. Patent 5,116,558 Wrobel et. al. describes 2-part compositions for use in forming gaskets by injection. The compositions comprise (A) a moderate-to-long chain di or polyfunctional prepolymer having vinyl reactive ends, and (B) a mono (meth)acrylate monomer, such as phenyl substituted alkyl (meth)acrylates which are particularly preferred, especially phenyl propyl methacrylate, because the resulting polymers have better flexibility at high temperatures (up to 150°) than those made from other monomers. However it has now been found that the degree of flexibility is relatively low and the materials themselves are substantially weaker, especially after ageing as compared to the compositions of the present invention. The present invention provides a one-part anaerobically curable sealant composition comprising urethane (meth)acrylate prepolymers, one or more phenyl substituted mono (meth)acrylate monomers which are miscible with or soluble in the prepolymers, and conventional curatives for anaerobic compositions, characterized in that: i) the urethane (meth)acrylate prepolymers comprise a combination of (1) a flexible urethane type (meth)acrylate prepolymer (A) of from 4,000 to less than 10,000 average molecular weight and a second urethane type (meth)acrylate prepolymer (B) of from 1,000 to 3,000 average molecular weight or (2) a flexible urethane type (meth)acrylate prepolymer (A) of more than 3,000 to less than 10,000 average molecular weight and a second urethane type (meth)acrylate prepolymer (B) of from 1,000 to 2,000 average molecular weight, wherein both prepolymers (A) and (B) have a urethane structure in the main chain thereof and (meth)acrylate end groups and wherein the ratio of prepolymer (A) to prepolymer (B) is from 1:1 to 3:1 on a weight basis or from 1:10 to 1:1 on a molar basis, and ii) the phenyl substituted mono (meth)acrylate monomer component comprises from 35 to 60 percent by weight of the total composition. The compositions of the invention utilise a prepolymer (A) which is of lower molecular weight than that of the Mochizuki patent and yet provide highly flexible materials whose flexibility is retained after high temperature ageing. Preferably the prepolymer (A) has an average molecular weight in the range 4,000 - 9,000, more preferably 4,500-6,000. Preferably the prepolymer (B) has an average molecular weight in the range 1,000-2,000. The high molecular weight prepolymer (A) and the low molecular weight prepolymer (B) may suitably be present in the composition in a weight ratio of from 1:1 to 3:1 and/or a molar ratio of from 1:10 to 1:1. Preferably the prepolymer (A) has an aliphatic urethane structure in the main chain thereof. More preferably the prepolymer (B) also has an aliphatic urethane structure in the main chain thereof. This is in contrast to the usual urethane-type prepolymers which are made by use of an aromatic diisocyanate, particularly toluene diisocyanate. One or both of the prepolymers (A) and (B) is preferably synthesised by use of an aliphatic diisocyanate. More preferably the polyester diol or polyether diol reacted with the diisocyanate is also free of aromatic groups in the chain structure. Urethane-type prepolymers having an aliphatic backbone structure are generally more expensive than similar prepolymers with an aromatic backbone structure but they are preferred because it has been found that they impart better heat resistance to the flexible materials. The comonomer (C) may suitably be present in an amount of 35 - 60%, preferably 40-55%, by weight of the total composition. If the comonomer (C) is present in an amount exceeding 60% by weight, then the extensibility of the flexible product is reduced, while if the amount is less than 35% by weight the temperature resistance of the flexible product is affected. The presence of a phenyl substituent group on the comonomer (C) has been found to impart temperature resistance to the flexible product. Preferred comonomers (C) are phenyl substituted alkyl (meth)acrylates particularly 3-phenylpropyl methacrylate and/or 2-phenylethyl methacrylate. Phenoxyethyl acrylate or benzyl methacrylate may also be used, preferably in combination with 3-phenylpropyl methacrylate and/or 2-phenylethyl methacrylate. As well as helping to give flexible temperature resistant products the co-monomers being diluents in the composition act as viscosity control agents because the prepolymers (A) and (B) are generally of high viscosity. The prepolymers (A) and (B) preferably comprise polyether-urethane and/or polyester-urethane derivatives which may be synthesised in a well known manner by reacting a polyester diol or a polyether diol with a diisocyanate and reacting the resulting product with a polymerizable (meth)acrylate acid ester. In addition to the prepolymers (A) and (B) and the comonomers (C), the compositions of the invention also contain conventional ingredients of an anaerobic cure system including an initiator and accelerator(s) as well as other additives known to the art which may be employed as needed, including a stabiliser, chelator and/or inhibitor and a filter. Reference is directed to U.S. Patents 4 439 600 Moran and 5 116 558 Wrobel et al . for detailed information on the cure system and other additives. The ingredients in addition to the prepolymer (A) and B and comonomers (C) may suitably comprise 5-15% by weight of the total composition. The compositions of the present invention, when cured, provide products which combine flexibility with toughness, resistance to high temperatures, resistance to heat ageing and resistance to solvents or oils. They are particularly suitable for flange sealing applications. Typically acrylic materials which have the requisite toughness and heat resistance for a vehicle engine environment only have an extension to break of 60-70%. With the compositions of the invention flexible products having an extension to break of 70%, preferably over 100%, and particularly in the range 130-180% can be obtained. The invention is illustrated in the following examples. Except where otherwise specified, the prepolymers used in the examples were the following: Prepolymer (A) - Acrylate terminated aliphatic urethane polyether (M.W. 5000) - an aliphatic urethane acrylate commercially available as Ebecryl 230 from UCB,B - 1620 Drogenbos, Belgium. According to the manufacturer's information it has a Höppler viscosity at 25°C of 40,000 mPa s and a molecular weight of 5000. Prepolymer (B) - Acrylate terminated aliphatic urethane polyester (m.w. 1500) - an aliphatic polyester/urethane acrylate commercially available under the Trade Mark Genomer D1500B from Hans Rahn & Co., Zurich, Switzerland. According to the manufacturer's information it is a molecular weight of approximately 1500 and a Brookfield viscosity at 25°C of 900,000 and at 60°C of 20,000. In each of the examples, anaerobic compositions were made up in accordance with the formulation listed. Each composition (with a copper salt actuator added thereto in the usual manner) was cured anaerobically at room temperature and the resulting flexible materials were subjected to standard tests for Elongation at Break (EB) at room temperature and after various forms of heat ageing, the tests being in accordance with ASTM D412 at a separation speed of 50 mm per minute. NQ Stabiliser is naphthoquinone EDTA Stabiliser is ethylene - diamine tetracetic acid EXAMPLE 1 % By Weight Formulation (A) - Acrylate Terminated Urethane Polyether (m.w.5000) 27.2 (B) - Acrylate Terminated Urethane Polyester (m.w.1500) 12.2 3-Phenylpropyl Methacrylate 51.9 NQ Stabiliser 0.1 EDTA Stabiliser 0.8 Saccharin 0.9 Acetyl Phenyl Hydrazine 0.5 Maleic Acid 0.9 Cumene Hydroperoxide 1.9 Silica 3.6 Material Properties % By Weight %Elongation to Break at RT - 134% %EB after 7 days at 150°C - 108% EXAMPLE 2 Formulation (A) - Acrylate Terminated Urethane Polyether (m.w. 5000) 26.3 (B) - Acrylate Terminated Urethane Polyester (m.w. 1500) 13.4 2-Phenylethyl Methacrylate 30.7 Phenoxyethyl Acrylate 19.0 NQ Stabiliser 0.1 EDTA Stabiliser 0.8 Saccharin 0.9 Acetyl Phenyl Hydrazine 0.5 Maleic Acid 0.9 Cumene Hydroperoxide 1.8 Silica 5.6 Material Properties %Elongation to Break at RT - 135% %EB after 7 days at 150°C - 108% %EB after 7 days in Motor Oil at 150°C - 136% %EB after 7 days in Water/Glycol at 150°C - 160% %EB after 7 days in ATF at 150°C - 152% EXAMPLE 3 (a) Formulation with a 1 : 1 weight ratio of Prepolymers (A) and (B) (A) - Acrylate Terminated Urethane Polyether (m.w. 5000) 16.08 (B) - Acrylate Terminated Urethane Polyester (m.w. 1500) 16.08 3-Phenyl Propyl Methacrylate 57.14 NQ Stabiliser 0.13 EDTA Stabiliser 0.78 Saccharin 0.91 Acetyl Phenyl Hydrazine 0.46 % By Weight Maleic Acid 0.91 Cumene Hydroperoxide 1.87 Silica 3.64 Colour 2.0 Material Properties Elongation to Break at RT = 114% Elongation to Break after 7 days at 150°C -86% (b) Formulation with a 1 : 1 weight ratio of Prepolymers (A) and (B) and lower and higher monomer levels Lower Higher (A) - Urethane Polyether (m.w. 5000) 30 Parts 20 Parts (B) - Urethane Polyester (m.w. 1500) 30 Parts 20 Parts 3-Phenyl Propyl methacrylate 40 Parts 60 Parts A Cure system similar to Example 3(a) was used to make up the formulation in both cases Material Properties Elongation to Break at RT 100% 84% Elongation to Break after 7 days at 150°C 52% 60% These examples 3(a) and (b) show the maintenance of flexibility although the extension values are not as high as earlier examples. EXAMPLE 4 (Comparative) Aromatic Urethane/Phenyl substituted Methacrylate combination Parts by Weight Aromatic Urethane Polyester (m.w. 3000) 44.0 3-phenoxy-2-hydroxy propyl methacrylate 56.0 The aromatic urethane polyester (m.w. 3000) was based on polydiethylene glycol adipate reacted with toluene diisocyanate and capped with hydroxyethyl methacrylate. A cure system similar to Example 3(a) was used to make up the formulation. Material Properties Elongation to Break at RT 152% Elongation to Break after 7 days at 150°C 16% Elongation to Break after 7 days in Motor Oil at 150°C 0% These results indicate the good initial flexibility but poorer heat ageing performance of this type of formulation. EXAMPLE 5 (Comparative) Aliphatic Urethane Resin/Aliphatic substituted methacrylate Parts by Weight (A) - Aliphatic Urethane Resin (Ebecryl 230) 50 Isobornyl Methacrylate 50 Material Properties Elongation at Break RT 265% Elongation at Break after 7 days at 150°C 0% A cure system similar to Example 3(a) was used to make up the formulation. The heat ageing performance is poor; the product becomes brittle after the heat ageing test. EXAMPLE 6 (Comparative) A formulation was made up in accordance with Example 1 of U.S. Patent 4,439,600 Moran and cured. The resulting flexible material was compared with the product of Example 2 of the present application. Moran Patent Present Application Example 1 Example 2 Initial % Extension to Break 112 134 After 7 Days at 150°C 8 108 After 7 Days in Oil at 150°C 36 136 After 7 Days in Glycol at 150°C Broken 160 The results show that while the Moran product has high flexibility when cured, this flexibility is lost on ageing. Similar results were found with other Examples in the Moran patent.

Claims: A one-part anaerobically curable sealant composition comprising urethane (meth)acrylate prepolymers, one or more phenyl substituted mono (meth)acrylate monomers which are miscible with or soluble in the prepolymers, and conventional curatives for anaerobic compositions, characterized in that: i) the urethane (meth)acrylate prepolymers comprise a combination of (1) a flexible urethane type (meth)acrylate prepolymer (A) of from 4,000 to less than 10,000 average molecular weight and a second urethane type (meth)acrylate prepolymer (B) of from 1,000 to 3,000 average molecular weight or (2) a flexible urethane type (meth)acrylate prepolymer (A) of more than 3,000 to less than 10,000 average molecular weight and a second urethane type (meth)acrylate prepolymer (B) of from 1,000 to 2,000 average molecular weight, wherein both prepolymers (A) and (B) have a urethane structure in the main chain thereof and (meth)acrylate end groups and wherein the ratio of prepolymer (A) to prepolymer (B) is from 1:1 to 3:1 on a weight basis or from 1:10 to 1:1 on a molar basis, and ii) the phenyl substituted mono (meth)acrylate monomer component comprises from 35 to 60 percent by weight of the total composition. The composition as claimed in claim 1 wherein the urethane (meth)acrylate prepolymers comprise a combination of a flexible urethane type (meth)acrylate prepolymer (A) of from 4,000 to less than 10,000 average molecular weight and a second urethane type (meth)acrylate prepolymer (B) of from 1,000 to 3,000 average molecular weight. The composition as claimed in claim 1 wherein the urethane (meth)acrylate prepolymers comprise a combination of a flexible urethane type (meth)acrylate prepolymer (A) of more than 3,000 to less than 10,000 average molecular weight and a second urethane type (meth)acrylate prepolymer (B) of from 1,000 to 2,000 average molecular weight. A composition as claimed in any of Claims 1 to 3 wherein the prepolymer (A) has an average molecular weight of from 4,500 to 6,000. A composition as claimed in Claim 2 wherein the prepolymer (B) has an average molecular weight of from 1,000 to 2,000. A composition as claimed in any of Claims 1 to 5 wherein prepolymer (A), prepolymer (B), or both prepolymer (A) and (B) have an aliphatic urethane structure in the main chain thereof. A composition as claimed in any of Claims 1 to 6 wherein the urethane (meth)acrylate prepolymers (A) and (B) are independently (meth)acrylate terminated polyester urethanes, (meth)acrylate terminated polyether urethanes, or mixtures thereof. A composition as claimed in any of Claims 1 to 7 wherein the phenyl substituted mono (meth)acrylate monomer component (C) comprises from 40 to 55 percent by weight of the total composition. A composition as claimed in any of Claims 1 to 8 wherein the phenyl substituted mono (meth)acrylate monomer component (C) is 3-phenylpropyl methacrylate, 2-phenylethyl methacrylate or a mixture thereof. A composition as claimed in any of Claims 1 to 8 wherein the phenyl substituted mono (meth)acrylate monomer component (C) is phenoxyethyl acrylate benzylmethacrylate or combinations thereof with 3-phenylpropyl methacrylate, 2-phenylethyl methacrylate, or both. A composition as claimed in any of Claims 1 to 10 wherein the ratio of prepolymer (A) to prepolymer (B) is from 1:1 to 3:1 on a weight basis. A composition as claimed in any of Claims 1 to 11 further comprising conventional stabilizers and additives. A composition as claimed in Claim 12 wherein the conventional curatives, stabilizers and additives comprise from 5 to 15 percent by weight of the total composition. A composition as claimed in Claim 1 wherein prepolymer (A) has an average molecular weight of from 4,500 to 6,000, prepolymer (B) has an average molecular weight of from 1,000 to 2,000, and the weight ratio of prepolymer (A) to prepolymer (B) is from 1:1 to 3:1. A composition as claimed in any of Claims 1 to 14 wherein the urethane (meth)acrylate prepolymers (A) and (B) are independently (meth)acrylate terminated polyester urethanes, (meth)acrylate terminated polyether urethanes or mixtures of the foregoing. A composition as claimed in Claim 14 wherein one of the urethane (meth)acrylate prepolymers (A) and (B) is a (meth)acrylate terminated polyester urethane and the other is a (meth)acrylate terminated polyether urethane.

Inventors: HOULIHAN JAMES, WROBEL PETER, HOULIHAN, JAMES, WROBEL, PETER
Applicants: LOCTITE IRELAND LTD, LOCTITE (IRELAND) LIMITED
Application year: 1994
Main classification: C09J4
IPC codes: C09K3, C09J4, C09D175, C09J175