THERMOSETTING COATING COMPOSITION AND COATED ARTICLE

Abstract: A thermosetting coating composition which permits two-coat-one-bake application of a primerless color base and a clear top coating on a polyolefinic base material and has excellent adhesiveness, weathering resistance and appearance, and an article coated with this composition. The composition comprises a melamine resin and a graft copolymer prepared by copolymerizing a chlorinated polyolefin containing an acid anhydride with an acrylic monomer, an unsaturated carboxylic acid and a hydroxylated acrylic monomer in an organic solvent. It can be used as a two-coat-one-bake primerless color base for a polyolefinic base material.

Description: The present invention concerns a thermosetting coating composition. To be more specific, it concerns a coating composition which is a colour base fit for polypropylene base materials such assuper high-strength polypropylene bumper base material, etc. and capable of providing the base material with excellent adhesion especially through coating and drying by baking made without primer by using this colour base and 2 coats of top coat clear and 1 bake (wet-on-wet system) and also capable of forming thermosetting coated film having long-term weatherability, chemical resistance, waterproofing and highly glossy and vivid coated film appearance. Conventional base colour paints for a car body, which are generally made of polyester, melamine, CAB resin or acrylic melamine resin, hardly have any adhesion to polyolefinic base materials consisting of so-called crystyalline polyolefins with small polarity. For that reason, paints containing modified or copolymerized chlorinated polyolefins containing anhydride are used as base colour for the coating on polyolefinic base materials. Though they all have good adhesion to such base materials, these paints are used only for primer coating and 1-coat painting because of such problems as no hardening, poor adhesion or poor secondary adhesion after washing with water, etc., which are vital problems for coating materials, in the coating made by the method of directly coating a colour base having painting pigment, and completing the coating with a single baking, i.e. primerless 2-coat 1-bake system (wet on wet system of colour base and top clear). Moreover, the paints containing modified or copolymerized chlorinated polyolefin containing anhydride which are supplied today are mostly of lacquer type or urethane crosslinking by polyisocyanate and of short working life and, therefore, it was practically very difficult to use them by the primerless 2-coat 1-bake method. Furthermore, the coated film obtained had a defect of yellowing regarding long-term weatherability and problems such as poor waterproofing, poor chemical resistance, etc. To be more specifically, they had a problem of producing dechlorination from polyolefinic base material and modified chlorinated polyolefin containing anhydride, causing yellowing of aluminium pigment and top coat clear, etc. JP-A-2 124 986 describes a composition containing a hydroxylated and chlorinated polyolefin and an amino resin. As attempts for improving polyolefinic base material itself, various trials are being made such as plasma treatment (surface oxidation by oxygen plasma), frame treatment (surface oxidation by frame), ultraviolet ray treatment (furnishing of functionality by ultrabiolet ray), etc. as measures for removing trichloroethane (improvement of adhesion). However, those measures also have problems such as non stability of adhesion, etc. depending on the kind of polyolefinic base material (degree of non polarity) and still remain in the stage of study. Moreover, while it is possible to improve adhesion by introducing functional group in polyolefinic base material, it makes the base material costly. Because of such defects, said formation of coated film is still insufficient in commercial value and has therefore not yet been put to practical use. For that reason, the present invention intends to provide a thermosetting coating composition provided with workability, excellent adhesion, weatherability, good appearance, etc. capable of primerless colour base and top coat clear by 2-coat 1-bake method against polyolefinic base materials. Moreover, the present invention intends to provide a painted body having excellent adhesion, weatherability, good appearance, etc. realized by 2-coat 1-bake method. In view of the current situation described above, the inventors of the present application assiduously made studies to solve said defects and found that formation of coated film by primerless 2-coat 1-bake method furnishing polyolefinic base materials with adhesion can be achieved properly by dispersing the pigment of paint with melamine resin (B) and bridging it with acrylic copolymers which graft copolymerization with chlorinated polyolefinic base materials (a-1) containing anhydride by means of this melamine resin (B) under a thermal energy, and finally achieved the present invention. Namely, the first to sixth inventions of the present application provide a thermosetting coating composition comprising graft copolymer obtained by copolymerizing acrylic monomers (a-4), unsaturated carboxylic acids (a-3), acrylic monomers (a-2) containing hydroxyl group with chlorinated polyolefin (a-1) containing anhydride under organic solvent, and melamine resin (B) and available for use as primerless colour base of 2-coat 1-bake coating against polyolefinic base materials. Moreover, the 7th and 8th inventions of the present application provide coated bodies comprising base material, colour base coated on the surface of this base material and top clear coated on the surface of this colour base and realized by the method of 2-coat 1-bake coating which consists in performing baking after the coating of colour base and top clear, characterized in that this base material is a polyolefinic base material with stable surface properties and that the colour base is said thermosetting coating composition. It is desirable that the base material be a bumper made of super high-strength polypropylene securing sufficient adhesion by washing with water. Here, primerless colour base of 2-coat 1-bake coating refers to a paint containing coating pigment to be directly coated on polyolefinic base materials the coating of which is completed by coating a top coat clear on it by wet-on-wet system and making a single baking. Said graft copolymer preferably comprises acrylic monomers (a-4) representing 30 to 94.5 5 wt% of total volume of single body, unsaturated carboxylic acids (a-3) representing 0.5 to 7.0 wt% of total volume of single body and acrylic monomers (a-2) containing hydroxyl group representing 5 to 25 wt% of total volume of single a body against chlorinated polyolefin (a-1) containing anhydride, and a number-average molecular weight of approximately 10,000 to 25, 000. Moreover, said melamine resin (B) is a butyl etherified melamine resin and the graft copolymer (A) to melamine resin ratio in solids content weight is preferably 70-90 to 30-10. Furthermore, a coated film formed on a polyolefinic base material is liable to produce dechlorination from the polyolefinic base material and the primerless formation of thermosetting coated film and cause deterioration of clear coated film and pigment (aluminium) under the influence of Cl ions. For that reason, it is also desirable to make the coating composition contain dechlorinating catcher such as basic magnesium, basic aluminium (CO32 is easily displaced by Cl), etc. to delay deterioration (yellowing of resin, discoloration of aluminium, storage stability). This dechlorinating catcher preferably represents 0.5 to 2.5 wt% against the total solid content weight of said graft copolymer (A) melamine resin (B). In so-called metallic paints, etc., there are cases where aluminium is contained in the paint. However, because ordinary aluminium deteriorates and causes discoloration and peeling by agglomeration under the influences of Cl ions brought about by said dechlorination, it is desirable to use resin coated aluminium as aluminium. This resin coated aluminium preferably represents 5 to 25 wt% against the total solid content weight of said graft copolymer and melamine resin. Still more, since polyolefinic base materials deteriorate very rapidly under the influences of ultraviolet ray, it is desirable to contain an ultraviolet ray absorber and a light stabilizer (in the paint) to delay deterioration of base material. The present invention will be described more in detail thereafter. The coating composition of the present invention is realized by blending melamine resins (B) with graft copolymer (A) obtained by copolymerizing acrylic monomers (a-4), unsaturated carboxylic acids (a-3), acrylic monomers (a-2) containing hydroxyl respective groups with chlorinated polyolefin (a-1) containing anhydride in the presence of an organic solvent and also blending a painting pigment (F) as colour base. Coated film is formed as a result of bridging between the graft copolymer (A) and the a melamine resins (B) produced with baking under a thermal energy. The solid content ratio of said chlorinated polyolefin (a-1) containing anhydride to said respective copolymers (a-2), (a-3), (a-4) shall be adjusted to 5:95 to 40:60 and more preferably to 10:90 to 20:80. Moreover, the present invention intends to provide a method of formation of a thermosetting coated film realized by blending a dechlorinating catcher (C), resin coating aluminium ( D) and ultraviolet ray absorber & light stabilizer (E) against the said solid content ratio of (A) and (B). Here, polyolefin with a chlorination ratio of 40 % or under, preferably 15 to 30%, is desirable as said chlorinated polyolefin (a-1). To enumerate only those which are particularly representative as such polyolefin, we may give the names of ethylene, propylene, ethylene-propylene copolymer, 1-butene, propylene-butene copolymer, ethylene- α -olefin copolymer, propylene-butadine copolymer, etc. Particularly desirable among them are propylene and ethylene- α -olefin copolymer, and we may cite copolymers chlorinated with carbon tetrachloride, etc. against acid modified polyolefins such as maleic anhydride, citraconic anhydride, itaconic anhydride, etc. as unsaturated carboxylic acids. As for proportion of this chlorinated polyolefin, 15 to 30 % is most desirable because no transparent coated film uniform in solubility with melamine resins can be obtained and the adhesion drops in case the rate of chlorination exceeds 40 %. Furthermore, to enumerate only those which are particularly representative as said acrylic monomers (a-2) containing hydroxyl group, we may cite 2-hydroxy ethyl (meta) acrylate, 2-hydroxy propyl (meta) acrylate, 3-hydroxy propyl (meta) acrylate, 2-hydroxy butyl (meta) acrylate, 3-hydroxy butyl (meta) acrylate, 4-hydroxy butyl (meta) acrylate, etc. When the quantity of use of these acrylic monomers (a-2) containing hydroxyl group is smaller than 5 wt %, bite resistance, interlaminar adhesion and chemical resistance are liable to become insufficient with a drop of hardening capacity. On the other hand, when this quantity is larger than 25%, adhesion with polyolefinic base material and weatherability of coated film, etc. are liable to drop. For that reason, it is desirable to keep the quantity of use of these acrylic monomers (a-2) containing hydroxyl group in the range of 5 to 25 wt % of the total weight of single bodies or at a hydroxyl value (solid content) of 22.3 to 111.4, more preferably 8 to 22 wt % of the total weight of single bodies or at a hydroxyl value (solid content) of 35.6 to 80.2. Still more, to enumerate only those which are particularly representative as said unsaturated carboxylic acids (a-3), we may cite (meta) acrylic acid as unsaturated monocarboxylic acid and various kinds of unsaturated monocarboxylic acids such as maleic acid anhydride, fumaric acid, itaconic acid, citraconic acid, mesaconic acid, etc. as un saturated dicarboxylic acids. The quantity of use of these unsaturated carboxylic acids is 0.5 to 7.0 wt %, and any quantity of these compounds smaller than 0.5 wt % leads to poor bridging with melamine resins, insufficient hardening capacity and poor gasoline resistance. On the other hand, if this quantity is larger than 7.0 w t %, the appearance and the waterproofing of the coated film obtained drop and the storage stability also deteriorates. Therefore, this quantity shall preferably be maintained in the range of 0.5 to 7.0 wt % of the total weight of single bodies or at an acid value (solid content) of 3.8 to 53.4, more preferably 1.0 to 3.0 wt % of the total weight of single bodies or at an acid value (solid content) of 7.6 to 22.9. Next, to enumerate only those which are particularly representative as acrylic monomers (a-4) copolymerizable with said (a-2), (a-3) respectively, we may cite various kinds of (met a) acrylates such as methyl (meta) acrylate, ethyl (meta) acrylate, n-propyl (meta) acrylate, i-propyl (meta) acrylate, n-butyl (meta) acrylate, i-butyl (meta) acrylate, tert-butyl (met a) acrylate, 2-ethyl-hexyl (meta) acrylate, lauryl (meta) acrylate, cyclo-hexyl (meta) acrylate, benzyl (meta) acrylate, dibromopropyl (meta) acrylate, tribromopropyl (meta) acrylate, aceto-acetoxyl ethyl (meta) acrylate, etc. Furthermore, the solid content ratio of said chlorinated polyolefin containing anhydride and acrylic copolymer (A) to melamine resins (B) is (A):(B) = 70 to 90/30 to 10 wt%, preferably a solid content ratio of (A):(B) = 75 to 85/25 to 15 wt% . Here, when (B) becomes 10 wt % or under, the waterproofing and the bite resistance drop. On the other hand, if (B) is 30 wt% or over, the appearance and the shock resistance will drop. In addition, because the present invention is characterized in that the dispersion of pigment (F) in particular is made with melamine resins (B), it can naturally disperse pigments of small absorption quantity such as titanium oxide or iron oxide based pigments. However, with pigments of poor dispersion and comparatively large absorption quantity such as quinacridone pigments, phthalocyanine pigments and carbon black which are organic pigments in particular, 20 to 25 % is a proper quantity of melamine resins (B) for securing good dispersion of pigment without affecting the coated film performances. Here, to enumerate only those which are particularly representative as pigments, we may cite titanium oxide as white pigment, rancidity, flavanthrone, azoic dyestuff, isoindolinone, benzimidazolone, titanium oxide based dyestuff as yellow pigment, isoindolinone, iron oxide, indanthrene as orange pigments, perylene, monoazoic dyestuff, benzimidazolone, quinacridone, anthroquinone, diketo pyrro pyrrole, indanthrene as red pigments, phthalocyanine pigments, azoic dyestuff as green pigments, carbon as black pigments, etc. Moreover, said dechlorinating catcher may well be used in the range of 0.5 to 2.0 wt % against the total solid content weight of chlorinated polyolefin containing anhydride and acrylic copolymer (A) to melamine resins (B). While the effect becomes too large, the gloss and the waterproofing drop if this quantity of use exceeds 2 wt %. To enumerate examples of such dechlorinating catcher, we may cite basic magnesium, aluminium, hydroxy, carbonate, hydrate, epoxy resin based materials. As typical epoxy resin product, there is so-called bisphenol A type epoxy resin (epoxy equivalent 170 to 250, molecular weight 300 to 400) which is a condensate of bisphenol A and epichlor(o)hydrine. Furthermore, said resin coating aluminium (D) may well be used in the range of 5 to 25 wt% against the total solid content weight of (A) and (B). No discoloration or interfacial separation due to deterioration of aluminium are produced even with ordinary aluminium at a proportion under 5 wt % but the appearance quality deteriorates at over 25 wt %. To enumerate examples of such resin coating aluminium, we may cite FZ or FM series (products of Toyo Aluminium K.K.), CR series (products of Asahi Chemical Metals K.K.), etc. Still more, said ultraviolet ray absorber and light stabilizer (E) may well be used in the range up to 5 wt% against the total solid content weight of (A) and (B). When they are used in excess of 5 wt%, the waterproofing drops with occurrence of precipitation though the effect becomes greater and it is also disadvantageous in respect of costs. To enumerate examples of such ultraviolet ray absorber and light stabilizer, we may cite as ultraviolet ray absorber 3-[3-(2H-benzotriazol-2-yl)-5-t-butyl-A-hydroxyphenyl] benzotriazole, 2-[2-hydroxy-3, 5-bis (1, 1-dimethylbenzyl) phenyl] -2H-benzotriazole, ethane diamide-N-(2-ethoxy phenyl) -N'-N'-(4-isododexyl phenyl), etc. As for light stabilizer, we may cite bis (2, 2, 6, 6tetra methyl-1-octyl oxy-4-piperizyl) decanodioate, 1, 3, 8-triaza spiro (4, 5,) decane-2, 4-dione-8-acetyl-3; -dodecyl-7, 7, 9, 9-tetramer, 2, 2, 4, 4-tetra methyl-20- (β-lauryl-oxycarbonyl)-ethyl-7-oxa-3, 20-diaza dispiro (5, 1, 11, 2) heneicosan-21-on, bis (1, 2, 2, 6, 6-pentamethyl-4-piperidyl) sebacate, bis (1, 2, 2, 6, 6-pentamethyl-4-piperidyl 1-2-butyl-2 -(4-hydroxy-3, 5-di-tertiary butylpenzyl) propanedioate, 2-(3-5-di-t-butyl-4-hydroxy benzyl)-2-n-butyl maronic acid bis (1, 2, 2, 6, 6-pentamethyl-4-piperidyl), bis (1, 2, 2, 6, 6-pentamethyl-4-piperidyl) sebacate, etc. Yet more, as top clear coated on said colour base, one may select as desired a product which is usually used for 2-coat 1-bake coating and we may cite thermosetting acrylic melamine based clear, thermosetting fluororesin clear, thermosetting silicon acrylic clear, thermosetting acid-epoxy bridging clear, thermosetting acrylic resin clear, thermosetting oil-free resin clear, thermosetting aminoalkyd resin clear, 2-part liquid type acryl urethane clear, 2-part liquid type fluororesin urethane clear, 2-part liquid type silicon urethane clear, etc. PREFERRED EXAMPLE OF THE INVENTION Next, the present invention will be explained concretely with examples and references. All parts and percentages given there are those in weight. <Example 1> Put 500 parts of chlorinated polyolefin containing anhydride obtained by chlorinating maleic anhydride with carbon tetrachloride; rate of chlorination = 24%, solid content = 30% (or under, hereinafter indicated simply as chlorinated polyolefin containing anhydride in this example and tables) and 850 parts of toluene in a 4-neck flask provided with agitator, thermometer and cooler, maintain the temperature inside the flask at 75 to 85 ° C, and drip in it a mixture consisting of 450 parts of isobutyl meta-acrylate, 250 parts of cyclohexyl meta-acrylate, 130 parts of acrylic acid-2-hydroxyl ethyl and 20 parts of acrylic acid and a solution obtained by melting 5 parts of benzoyl peroxide and 5 parts of azobisisobutyronitrile in 300 parts of toluene for 3 hours, and maintain for another 10 hours at the same temperature even after the end of dripping to let continue the reaction. From this, we got a chlorinated polypropylene modified acrylic resin with a non-volatile content of 40.4 % and a number-average molecular weight of 18,000 (Example 1). Table 1 indicates those results. Moreover, Table 1 also indicates products of the same composition with said example 1 but with different loads as examples 2 to 7. In the explanation given hereafter, specific chlorinated polyolefin containing anhydride and acrylic copolymers of examples 1 to 7 will be abbreviated as chlorinated polyolefin arid acrylic copolymers (A1) to (A7). Next, we obtain various kinds of colour base by dispersing 60.18 parts of these chlorinated polyolefin and acrylic copolymers (A1) to (A7), 13.37 parts of butylated melamine resin (B) and 0.90 parts of dechlorinating catcher (C) in advance with a sand mill and then agitating and dispersing 800 parts of resin coated aluminium (B) and 0.90 and 0.45 parts respectively of ultraviolet ray absorber and light stabilizer with the agitator. Table 2 indicates those colour bases. Name of type of colour base A-1 A-2 A-3 A-4 A-5 A-6 A-7 A-8 A-9 Polyolefin acrylic graft copolymer containing anhydride (40%) 60.18 ← ← ← ← ← ← ← ← Butylated melamine resin (60%) 13.37 ← ← ← ← ← ← ← ← Resin coated aluminium 8.00 ← ← ← ← ← ← ← None Dechlorinating catcher 0.90 ← ← ← ← ← ← None 0.90 UVA 0.90 ← ← ← ← ← ← ← ← HALS 0.45 ← ← ← ← ← ← ← ← Additive (Dispersing agent RC) 8.00 ← ← ← ← ← ← ← ← Flow levelling agent 0.20 ← ← ← ← ← ← ← ← Solvent 8.00 ← ← ← ← ← ← 8.90 8.00 Ordinary aluminium None ← ← ← ← ← ← ← 8.00 Total 100.00 ← ← ← ← ← ← ← ← Example 1 to 7 correspond to colour base types A-1 to A-7 (type name). However, colour base type A-8 is a case where no dechlorinating catcher is used for example 1, while colour base type A-9 is a case where ordinary aluminium is used in substitution for resin coated aluminium for example 1. After that, the respective colour bases are coated in the following process: Process 1: Submitted super high-strength polypropylene bumper base material (70 x 150 x 20mm) to surface treatment by washing with water. Process 2: Next, after coating this base material by spraying the coating compositions (colour bases) of examples 1 to 7 to a film thickness of 15 µ respectively, left the materials under normal temperature for 4 minutes for flushing. Process 3: Further coat Elastometric 2000 Clear (thermosetting solvent type paint consisting of acrylic copolymer and melamine resin) of T B L Co., Ltd. on this wet coat film by spraying to a film thickness of 30 µ and, after 10 minutes of setting, performed baking at 120° C for 30 minutes. Table 3 indicates the results of evaluation of such products. Name of type of colour base A-1 A-2 A-3 A-4 A-5 A-6 A-7 A-8 A-9 Base material Super high-strength polypropylene bumper base material (surface treatment by washing with water) Baking conditions Bake at 120°C for 30 minutes. Results of Evaluation Primary adhesion (Evaluation of adherence) 100 / 100 ← ← ← ← ← ← ← ← Secondary adhesion Evaluation of adherence after moisture resistance 100 / 100 ← ← ← ← ← ← ← ← Evaluation of adherence after hot water resistance 100 / 100 ← ← ← ← ← ← ← ← Evaluation of heat resistance ○ ← ← ← ← ← ← Δ Δ Evaluation of storage stability ○ ← ← ← ← ← ← ← ← Evaluation of workability ○ ← ← ← ← ← ← ← ← Evaluation of gasoline resistance ○ ← ← ← ← ← ← ← ← Next, to explain references which are also comprised in the invention, we obtained chlorinated polyolefin and acrylic copolymers in the same way as in example 1, except that the polymerizing conditions were changed as shown in Table 4 and that chlorinated polyolefin, polymerization initiator and various kinds of acrylic monomers were used in the presence of polymerizing solvent as shown in Table 4. Table 4 indicates those conditions as references 1 to 6. After that, we obtained various kinds of colour base in the same way as in example 1, except that we changed polyolefin acrylic copolymers, butylated melamine resin (B), dechlorinating catcher, resin coated aluminium, ultraviolet ray absorber and light stabilizer indicated in Table 5 under the conditions as indicated there at the same time. Table 5 indicates those details. References 1 to 6 correspond to different types of colour base or B-1 to B-6 (type name). Name of type of colour base B-1 B-2 B-3 B-4 B-5 B-6 Polyolefin acrylic graft copolymer containing anhydride (40%) 60.18 ← ← ← ← ← Butylated melamine resin (60%) 13.37 ← ← ← ← ← Resin coated aluminium 8.00 ← ← ← ← ← Dechlorinating catcher 0.90 ← ← ← ← ← UVA 0.90 ← ← ← ← ← HALS 0.45 ← ← ← ← ← Additive (Dispersing agent RC) 8.00 ← ← ← ← ← Flow levelling agent 0.20 ← ← ← ← ← Solvent 8.00 ← ← ← ← ← Ordinary aluminium None ← ← ← ← ← Total 100.00 ← ← ← ← ← Those references (colour base types B-1 to B-6) were coated under the same conditions as example. The results of evaluation are indicated in Table 6. Name of type of colour base B-1 B-2 B-3 B-4 B-5 B-6 Base material Super high-strength polypropylene bumper base material (surface treatment by washing with water) Baking conditions Bake at 120°C for 30 minutes. Results of Evaluation Primary adhesion (Evaluation of adherence) 80 / 100 60 / 100 100 / 100 100 / 100 100 / 100 100 / 100 Secondary adhesion Evaluation of adherence after moisture resistance 80 / 100 60 / 100 90 / 100 90 / 100 95 / 100 90 / 100 Evaluation of adherence after hot water resistance 80 / 100 60 / 100 90 / 100 90 / 100 95 / 100 90 / 100 Evaluation of heat resistance ○ Δ ○ ○ ○ ○ Evaluation of storage stability Δ ○ ○ Δ ○ ○ Evaluation of workability ○ Δ ○ ○ ○ ○ Evaluation of gasoline resistance ○ Δ Δ ○ Δ ○ As shown in Table 6, the colour bases of references were all confirmed to be inferior to that of the example in respect of adhesion. To evaluate them individually, B-1 is believed to have deteriorated in adhesion because of improper chlorinated polyolefin to acrylic copolymer ratio. B-2 has poor compatibility with melamine because of improper chlorinated polyolefin to acrylic copolymer ratio. B-3 is poor in both low-temperature hardening capacity and gasoline resistance for reason of low oxidation. B-4 dropped in waterproofing and became poor in storage stability because of high oxidation. B-5 has poor interlaminar adhesion due to low OH value. B-6 dropped in both waterproofing and hardening capacity because of high OH value. As explained so far, the present invention can provide a thermosetting coating composition demonstrating excellent adhesion to base material in the case where colour base and top coat clear are coated on polyolefinic base material by 2-coat 1-bake method without primer and dried by baking. Moreover, by containing dechlorinating catcher, the present invention can delay deterioration of coated film (yellowing of resin, discoloration of aluminium, instability during storage). Furthermore, it can also prevent discoloration, peeling by agglomeration due to deterioration of aluminium, by using resin coated aluminium as aluminium. Still more, it can prevent deterioration of base material by containing ultraviolet ray absorber and light stabilizer. In this way, the present invention can provide an excellent thermosetting coating composition which can be coated an polyolefinic base material by 2-copat 1-bake method without primer, providing excellent long-term weatherability, durability as well as coated film appearance with excellent gloss and vividness. Yet more, the 7th and 8th inventions of the present application can provide painted body having excellent adhesion, weatherability, good appearance, etc. realized by 2-coat 1-bake method coated on polyolefinic base material by 2-coat 1-bake method without primer.

Claims: A thermosetting coating composition comprising graft copolymer (A) obtained by copolymerizing acrylic monomers (a-4), unsaturated carboxylic acids (a-3), acrylic monomers (a-2) containing hydroxyl group with chlorinated polyolefin (a-1) containing anhydride under organic solvent, and melamine resin (B) and available for use as primerless colour base of 2-coat 1-bake coating against polyolefinic base materials. A thermosetting coating composition as defined in Claim 1, wherein said graft copolymer (A) comprises acrylic monomers (a-4) representing 30.0 to 94.5 wt % of total volume of single body, unsaturated carboxylic acids (a-3) representing 0.5 to 7.0 wt% of total volume of single body and acrylic monomers (a-2) containing hydroxyl group representing 5 to 25 wt% of total volume of single body against chlorinated polyolefin (a-1) containing anhydride, and a number-average molecular weight of approximately 10,000 to 25,000. A thermosetting coating composition as defined in Claims 1 or 2, wherein said melamine resin (B) is butyl etherified melamine resin and the graft copolymer (A) to melamine resin (B) ratio in solids content weight is 70-90 to 30-10. A thermosetting coating composition as defined in Claims 1 to 3, wherein the coating composition contains dechlorinating catcher representing 0.5 to 2.5 wt % against the total solid content weight of said graft copolymer (A) and melamine resin (B). A thermosetting coating composition as defined in Claims 1 to 4, wherein the coating composition contains resin coated aluminium representing 5 to 25 wt% against the total solid content weight of said graft copolymer (A) and melamine resin (B). A thermosetting coating composition as defined in Claims 1 to 5, wherein the coating composition contains an ultraviolet ray absorber and a light stabilizer. A coated body comprising base material, colour base coated on the surface of this base material and top clear coated on the surface of this colour base and realized by the method of 2-coat 1-bake coating which consists in performing baking after the coating of colour base and top clear, characterized in that this base material is a polyolefinic base material with stable surface properties and that the colours base is said thermosetting coating composition indicated in either of Claims 1 to 6. A coated body comprising base material as defined in Claim 7, wherein the base material is a bumper made of super high-strength polypropylene securing sufficient adhesion by washing with water.

Inventors: INA TOSHIRO, SASAKI RYO, INA, TOSHIRO, SASAKI, RYO, INA, TOSHIRO TBL CO., LTD., SASAKI, RYO NISSAN MOTOR CO.,LTD. GIJUTSUKAIHATSU
Applicants: NISSAN MOTOR, TBL CO LTD, NISSAN MOTOR CO., LTD., TBL CO., LTD.
Application year: 1994
Main classification: C09D151
IPC codes: C09D151, C08L61, C09D161, B05D1, C08L51