SUNSCREEN AGENTS

Abstract: Hydroxy salts of the formula [M(OH)(2-a)]<a+> X<b->a/b . zH2O, where M is zinc, copper or a mixture of the two and X denotes anions at least some of which display ultraviolet absorption over at least a portion of the wavelength range from 290 to 400 nanometres, their use as sunscreen agents and sunscreen compositions comprising them together with a cosmetically acceptable vehicle.

Description: SUNSCREEN AGENTS This invention relates to sunscreen agents, that is to say compounds capable of absorbing ultra violet radiation with a wavelength in the range from 290 to 400 nanometres. The invention also relates to sunscreen compositions for application to human skin incorporating the sunscreen agents. In general terms, harmful ultra-violet (UV) rays, particularly those originating from sunlight, which penetrate the upper atmosphere and reach the eart 's surface, can be classified into: i. the energy-rich UV-B rays (290-320nm wavelength) which possess an intense physiopathological activity on the skin; these are absorbed just above the dermis and they are responsible for erythema and skin pigmentation; and ii. UV-A rays (320-400nm wavelength) which penetrate deeper into the skin (to the dermis and beyond) . Their energy is much lower and the photobiological effects they cause are much more long term in nature, for example, they accelerate skin ageing. Sunscreen compositions should desirably provide protection against both UV-A and UV-B rays, but protection against UV- A rays is particularly desirable, in order to prevent the long term photobiological effects resulting from UV-A radiation. Meyn et al, in Inorganic Chemistry, Vol 32 pages 1209-1215 (1993) have described water-insoluble hydroxy salts which can be represented by a general formula M(OH) (2 . a) (NO, " ).. zH 2 0 where M is a mixture of divalent metals . It is described in this paper that these hydroxy double salts have a layered structure and will undergo ion exchange to replace nitrate ions with organic anions. The metal atoms lie in layers in which metal atoms are connected together through OH groups. The anions project into interlayers between the layers of metal ions. We have now found that ultraviolet absorbing anions can be introduced into hydroxy salts of this type, and then retain their ultraviolet absorbance. In a first aspect this invention provides a hydroxy salt of the formula M(OH) (2 . a) ] * ab zH 2 0 where M is zinc, copper or a mixture of the two and X denotes anions at least some of which display ultraviolet absorption over at least a portion of the wavelength range from 290 to 400 nanometres. In a second aspect the invention provides a sunscreen composition for application to human skin comprising a cosmetically acceptable vehicle incorporating a said hydroxy salt in which at least some of the anions X display ultraviolet absorption over at least a portion of the wavelength range from 290 to 400 nanometres. The invention also relates to the use of such hydroxy salts as sunscreen agents and to prepare sunscreen compositions. The value of z will generally lie in a range from 0 to 10, more preferably 0 to 1. In general it will be desirable that the ultraviolet absorbing anions have a fairly strong absorption in at least a portion of the stated range from 290 to 400 nanometres. This may be specified as a requirement that the acid form or a simple alkali metal or ammonium salt of the anion exhibits absorption with a molar extinction coefficient of at least 2 x IO 3 , preferably 3 x IO 3 , more preferably at least 5 x 10 3 and yet more preferably at least 8 x IO 3 over at least a portion of the stated wavelength range from 290 to 400nm. We have found that when such anions are incorporated into a hydroxy salt, their ultraviolet absorption is, in general, retained. However, there is often a broadening of the absorption, leading to enhanced UV-A absorption compared to the UV-A absorption displayed by these anions prior to their incorporation. Thus, in preferred embodiments of the invention, enhanced UV-A protection is attained by virtue of incorporating the anions into a hydroxy salt. Effective ultraviolet absorption may be provided by an absorption band whose maximum is outside the stated range. For example the p-methoxy cinnamate ion has an absorption maximum at 285 nanometres but the absorption band is broad enough to provide strong absorption over a range from 290 nanometres up to at least around 320 nanometres. It will often be the case that absorption in the range 290 to 400 nanometres will be provided by an absorption band with a maximum in the range 260 to 360 nanometres. Preferably the anions do not have strong absorption in the visible band from 400 to 700 nanometres, especially in the part of it from 450 nanometres upwards, notably from 450 or 500 to 650 nanometres. The extinction coefficient for absorption in such ranges may preferably be no greater than 5 x IO 2 throughout the ranges concerned. The molar extinction coefficient of a substance is usually measured in solution and is then given by the formula Io e log 10 cl where I is the intensity of radiation transmitted through the sample, I 0 is the intensity of radiation transmitted through a reference sample consisting of the same solvent but without the substance under test, c is molar concentration in moles/litre, and 1 is the path length through the solution, in centimetres. The proportion of anions X which absorb ultraviolet radiation may be fairly small, for example as little as 3 mole%, better at least 5 mole % of all the anions present, but may be higher such as a majority of the anions present and even up to 100%. The anions which absorb ultraviolet radiation may suitably be one or more of the following: para amino benzimidazole-5-sulphonate 3-imidazol-4-yl acrylate salicylate p-methoxy cinnamate 2 ethyl hexyl-2-cyano-3,3 diphenyl acrylate 3,3,5 trimethylcyclohexyl-2-acetamido benzoate p-aminobenzoate cinnamate 3,4-dimethoxy phenyl glyoxylate - (2-oxoborn-3-ylidene) -p-xylene-2-sulphonate a- (2-oxoborn-3-ylidene)toluene-4-sulphonate cϋ-cyano-4-methoxy cinnamate 2-phenyl benzimidazole-5-sulphonate. These anions, when in the free state, are known to display absorption in the wave length range from 290 to 400 nanometres. All of them are regarded as acceptable materials to serve as sunscreen agents. As mentioned above, we have now found that when they are incorporated as anions in a hydroxy salt, their ability to absorb ultraviolet radiation is retained. In most instances, when the above-listed anions are incorporated into a hydroxy salt, there is no major change in the ultraviolet absorption spectrum, although an advantageous enhancement of absorption in the UV-A region may occur. Another group of organic materials suitable for the purposes of this invention are those which contain weak acid functionality through the inclusion of a phenolic proton or other weakly acidic proton in the molecule. This proton can be removed to form an anion which can be incorporated into a hydroxy salt. The anions derived from such compounds may have absorption spectra significantly different from the parent compound, but nevertheless, these anions, upon incorporation into a hydroxy salt, display significant absorption of light between 290 and 400nm (UV-A region) . An important group of such phenolic compounds are hydroxylated benzophenone derivatives. Certain diketone compounds which can exist in a weakly acidic enol form may also be included. Examples of such compounds from which anions can be derived include ■ but are not limited to the following materials for which both CTFA and chemical names are given: CTFA Name Chemical Name Benzophenone-1 2,4-Dihydroxybenzophenone Benzophenone-2 2,2' ,4,4' -Tetrahydroxybenzophenone Benzophenone-3 2-Hydroxy-4-methoxy benzophenone Benzophenone-4 2-Hydroxy-4-methoxy benzophenone-5- sulphonic acid Benzophenone-5 2-Hydroxy-4-methoxy benzophenone-5- sulphonic acid; monosodium salt Benzophenone-6 2,2' -Dihydroxy-4,4 ' -dimethoxy benzophenone Benzophenone-7 5-Chioro-2hydroxy benzophenone Benzophenone-8 2,2' -Dihydroxy-4-methoxy benzophenone Benzophenone-9 2,2' -Dihydroxy-4,4 ' -dimethoxy benzophenone-3,3 ' -disulphonic acid; disodium salt Benzophenone-10 2-Hydroxy-4-methoxy-4 ' -methyl benzophenone Benzophenone-12 2-Hydroxy-4-octoxy benzophenone Homosalate Homomenthyl salicylate Octyl Salicylate 2-ethylhexyl salicylate Some tradenames and suppliers are:- CTFA Name Trade Name Supplier Benzophenone-1 UVINUL 400 BASF Chemical Co. Benzophenone-2 UVINUL D-50 BASF Chemical Co. Benzophenone-3 UVINUL M-40 BASF Chemical Co. Benzophenone-4 UVINUL MS-40 BASF Chemical Co. Benzophenone-5 Quest Benzophenone-6 UVINUL D-49 BASF Chemical Co. Benzophenone-7 Quest Benzophenone-8 SPECTRA-SORB American Cyanamide UV-24 Benzophenone-10 UVISTAT 2211 Ward Blenkinsop Benzophenone-12 CYASORB UV531 American Cyanamide Homosalate KEMESTER HMS Hunko Chemical Octyl Salicylate SUNARONE WMO Felton Worldwide Another compound which can provide anions is Butyl Methoxydibenzoylmethane available as PARSOL 1789 from Givaudan Corp. Also included in this form of the invention are anionic species derived from Pongomol which is a substituted 1,3- diketone whose systematic name is 1- (4-methoxy-5- benzofuranyl) -3-phenyl-l,3-propanedione. It has an ultra¬ violet absorption band within the range of from 250 to 500nm, and an extinction coefficient of from 5,000 to 70,000. The diketone is more fully described in US Patent 5,152,983 incorporated by reference herein. Among these materials, Benzophenone-4 and Benzophenone-9 have both a strong acid functionality conferred by a sulphonate group and weak acid functionality, conferred by the phenolic proton. For these materials (and for Benzophenone-5 which is the monosodium salt of Benzophenone-4) , multiple anionic forms of the material may be produced and incorporated into hydroxy salts. Thus, for example, with Benzophenone-4, both an mono- and dianion can be incorporated into hydroxy salts. Both monoanionic and dianionic forms of this material and any combinations thereof incorporated into hydroxy salts may be useful for sunscreens and are to be considered within the scope of this invention. Hydroxy salts of this invention are insoluble both in water and in other solvents. They can however be suspended as dispersions in solvents including water. A sunscreen composition according to this invention will therefore have the hydroxy salt, with ultraviolet-absorbing anions, dispersed in the vehicle. Preferably the vehicle is aqueous and the hydroxy salt is suspended in this. For use the composition is rubbed onto skin and the water then evaporates, along with any volatile organic compounds included in the vehicle. This leaves the hydroxy salt as a deposit on the skin. The layer structure of the material assists in the deposition of the material as a continuous layer on the skin. The aqueous vehicle may be an oil-in-water emulsion with the hydroxy salt suspended in that emulsion. The hydroxy salt may suspend in the aqueous phase of such an emulsion or, less likely, suspend in the oil phase. Hydroxy salts are insoluble materials and are macromolecules so that the molecular size is large compared with the size of the organic compounds which are conventional sunscreen agents. These properties are advantageous. Once hydroxy salts have been deposited on the skin, their large molecular size and/or their insolubility means that they should not be prone to penetrating into the skin, nor to moving about on the skin surface. (Penetration into the body through the skin and migration to sensitive areas such as the eyes are both potential hazards with water-soluble sunscreen active agents) . Because the materials of the invention are insoluble, they also cannot dissolve away while the user is swimming, which provides a further advantage. A sunscreen composition containing a hydroxy salt in accordance with this invention can be prepared by adding the hydroxy salt to an aqueous vehicle, which at its simplest may be water alone, and then mixing to form a suspension. It is envisaged that a sunscreen composition according to this invention will contain from 0.05 to 50% by weight of the hydroxy salt, more preferably from 0.1 to 30% by weight, yet more preferably 2 to 20% by weight. The amount which is incorporated will affect the amount of ultraviolet absorption achieved, of course. Therefore amounts towards the upper end of the range would be used for sunscreen compositions intended to give a high degree of protection against ultraviolet radiation. Other materials may be included in sunscreen compositions according to this invention. It is within the scope of this invention to incorporate an additional sunscreen agent. Possibilities include nonionic organic sunscreen agents, inorganic sunscreen agents such as finely divided titanium dioxide and particles of organic polymers. Other materials which may possibly be included in a sunscreen composition include thickening agents, emollient oils, humectants and fluids to enhance lubricity, notably silicone oils. Minor constituents which may be present include perfume and preservatives. Preparation of a hydroxy salt incorporating ultraviolet absorbing anions will generally take place in two stages: the first stage being the preparation of a hydroxy salt with some other anions and the second stage being ion exchange to replace at least some of the anions with ultraviolet absorbing anions. The preparation of some hydroxy salts has been described by Meyn et al, as referred to above. We have found it satisfactory to treat suspension of zinc oxide with zinc or copper nitrate, preferably at an elevated temperature, followed by filtering off the solid. The hydroxy salts can be identified by chemical analysis for the elements present and by X-ray diffraction. Ion exchange to introduce the ultraviolet absorbing anions can be carried out by suspending a hydroxy salt in an aqueous solution of the anions which it is desired to introduce. The process may be carried out at an elevated temperature to increase the speed of reaction. The hydroxy salt is then filtered off. It can be characterised by chemical analysis and by ultraviolet spectroscopy carried out on an aqueous suspension of the hydroxy salt. EXAMPLES Preparation 1: Preparation of Zinc hydroxy salt containing Nitrate ion 68g of zinc oxide was suspended in 200ml of distilled water in a one litre polypropylene screwcap bottle. 250g of zinc nitrate were dissolved in 400ml of distilled water and the resulting solution was added, with stirring, to the zinc oxide suspension. The bottle was capped, shaken vigorously for 2 minutes and then placed in a thermostated oven for 23 hours at 90°C. At the end of this period the solid was filtered off, washed thoroughly with water and then freeze dried. The dried material was finally equilibrated with water vapour by storing in a desiccator over a saturated sodium chloride solution. The composition of this material was determined by thermal and chemical analysis. The results were as follows: % Zn = JU . J * 3 % N = 2. . !____.*o % hydration water = 3.65% This is consistent with a formula Zn(OH) 1.83 (N0 3 ) αι7 . 0.22HO The X-ray powder diffraction pattern of this material showed characteristic major peaks at 9.8A and 4.9A. Scanning electron microscopy showed the product to be composed of plate crystals of l-2μm diameter. The uv spectrum of a suspension of 50mg/litre of the material in water, measured over the range 250 to 450nm showed no appreciable absorption bands. Example 1: Ion-exchange of 4-Methoxy Cinnamate Anion into Zinc Hydroxy salt 5.71g of 4-methoxy cinnamic acid and 1.28g of sodium hydroxide were dissolved in 200ml of water. This solution was added to lOg of the product from Preparation 1 in a polypropylene screwcap bottle. The bottle was capped, shaken for 2 minutes, and then heated at 90°C for 18 hours. The solid was filtered off, washed with warm water and then oven dried at 90°C. Chemical analysis showed that the product contained 26.0% by weight of 4-methoxy cinnamate ions. The X-ray diffraction pattern of the product showed i) the characteristic peaks of the starting material were absent. ii) there were three new peaks at 27A, 13.5A and 9,0A which were not present in the starting material. The uv spectrum of a suspension of 50mg/litre of the material in water, showed a broad peak centred at 286nm with a tail extending to at least 400nm. The absorbance at 360nm was 19% of the absorbance at 286nm, whereas for sodium methoxycinnamate the absorbance at 360nm is less than 0.2% of the absorbance at 286nm. Example 2: Ion-exchancre of p-aminobenzoate into Zinc Hydroxy salt 4.4g of p-amino benzoic acid and 1.28g of sodium hydroxide were dissolved in 200ml of water and solution added to lOg of the product from Preparation 1. The suspension was then heated in a capped polypropylene bottle for 18 hours at 90°C. The solid product was filtered off, washed with warm water, and then oven dried at 90°C. X-ray powder diffraction of the product showed the two characteristic peaks within the starting material were absent but that new peaks, characteristic of the p-amino benzoate containing material, were present at 24A, 12A and 8A. The X-ray powder diffraction pattern also showed the product contained some zinc oxide. Chemical analysis showed the product contained 6.28% by weight p-amino benzoate. The uv spectrum of a suspension containing 50mg/l of the product in water showed a broad adsorption peak centred at 265nm and with a tail extending to at least 330nm. The absorbance at 330nm was 29.8% of the absorbance at 265nm, whereas for sodium p-aminobenzoate the absorbance at 330nm is less than 0.2% of the absorbance at 265nm. Preparation 2: Preparation of a zinc/copper Hvdroxy salt containing Nitrate Ion 72.48g of Cu(N0 3 ) 2 . 3^0 were dissolved in 300ml of water and added to a slurry of 29.4g ZnO in 50m of water. The mixture was shaken in a capped polypropylene bottle for 2 minutes and then heated at 90°C for 48 hours. The solid product was filtered off washed with warm water and then freeze dried. X-ray powder diffraction pattern of the product showed major peaks at 6.9A and 4.45A which are characteristic of this material. Scanning electron microscope imaging showed the product to be composed of 0.2 to 0.4um diameter plate crystals. Thermal and chemical analysis yielded the following chemical data % Zn = 21.8% % Cu = 31.4% % N = 4.78% % hydration water = <0.2% This is consistent with the chemical composition Z o . 4 CU o.6 (OH) 158 (NO 3 ) 0 . 42 The uv absorption spectrum of a 50mg/l suspension of the product in water showed no appreciable absorption bands in the region 250 to 450nm. Example 3 : Ion-exchange of 4-methoxy cinnamate into zinc/copper Hydroxy salt 5.71g of 4-methoxy cinnamic acid and 1.28g of sodium hydroxide were dissolved in 200ml of water and the solution added to lOg of the product from Preparation 2. The suspension was then heated in a capped polypropylene bottle for 18 hours at 90°C. The solid product was filtered off, washed with warm water, and then oven dried at 90°C. X-ray powder diffraction of the product showed that the two characteristic peaks of the starting material were still present, but were greatly diminished in intensity. New peaks, characteristic of the 4-methyoxy cinnamate- containing Zn/Cu hydroxy material, were also present at 23A, 11.5A, and 7.7A. Chemical analysis showed the product contained 43.07% by weight 4-methoxy cinnamate. This is consistent with the chemical composition Z- 4 Cu 06 (OH) ι58 (mcin) 039 (NO 3 ) α03 where mcin = 4-methoxy cinnamate. The uv spectrum of a suspension containing 50mg/l of the product in water showed a broad adsorption peak centred at 286nm with a tail extending to at least 400nm. The absorbance at 360nm was 15.9% of the absorbance at 286nm, whereas for sodium methoxycinnamate the absorbance at 360nm is less than 0.2% of the absorbance at 286nm. Example 4: Ion-exchange of 2-Phenylbenzimidazole-5-sulphonate into zinc/copper hydroxy salt 8.8g of 2-Phenylbenzimidazole-5-sulphonic acid and 1.28g of sodium hydroxide were dissolved in 200ml of water and the solution added to lOg of the product from Preparation 2. The suspension was then heated in a capped polypropylene bottle for 18 hours at 90°C. The solid product was filtered off, washed with warm water, and then oven dried at 90°C. X-ray powder diffraction of the product showed that the two characteristic peaks within the starting material were still present, but were diminished in intensity. New peaks, characteristic of the product containing 2- Phenylbenzimidazole-5-sulphonate were also present at 21.3A and 10.7. Chemical analysis showed the product contained 11.9% by weight 2-Phenylbenzimidazole-5-sulphonate. This is consistent with the chemical composition. Zno. Cu o.6 (OH) 158 (pbs) 006 (N0 3 ) 0.36 where pbs = 2-Phenylbenzimidazole-5-sulphonate The uv spectrum of a suspension containing 50mg/l of the product in water showed a broad adsorption peak centred at 302nm with a tail extending to at least 400nm. The absorbance at 360nm was 27% of the absorbance at 302nm, whereas for sodium 2-phenylbenzimidazole-5-sulphonate the absorbance at 360nm is less than 0.2% of the absorbance at 302nm. Example 5: Ion-exchange of a 2-Hydroxy-4-methoxy benzophenone-5- sulphonate into zinc/copper hydroxy salt 9.89g of 2-Hydroxy-4-methoxy benzophenone-5-sulphonic acid and 1.28g of sodium hydroxide were dissolved in 200ml of water and the solution added to lOg of the product from Preparation 2. The suspension was then heated in a capped polypropylene bottle for 18 hours at 90°C. The solid product was filtered off, washed with warm water, and then oven dried at 90°C. X-ray powder diffraction of the product showed the two characteristic peaks within the starting material were still present, but were diminished in intensity. A new peak, characteristic of the product containing 2-Hydroxy-4- methoxy benzophenone-5-sulphonate was also present at 22A. Chemical analysis showed the product contained 3.1% by weight 2-Hydroxy-4-methoxy benzophenone-5-sulphonate. The uv spectrum of a suspension containing 50mg/l of the product in water showed a broad adsorption band centred at 290nm and with a tail extending to at least 400nm. The absorbance at 360nm was 37% of the absorbance at 290nm, whereas for the monosodium salt of 2-hydroxy-4-methoxy benzophenone-5-sulphonic acid the absorbance at 360nm is less than 14% of the absorbance at 290nm. Example 6 The following formulations were prepared. wτ.% INGREDIENT Phase A 75.9% Water Phase B: 5% Zinc hydroxy salt of 4- methoxycinnamate (Example 1) 10% Finsolv 1% Brij 72 4% Brij 721 Phase C: 1% Xanthan Gum 3% Propylene glycol Phase D: 0.1% Glydant plus The process for formulation was Heat Phase B to 80°C and homogenise. Heat Phase A to 80°C and then slowly add Phase B while stirring. Add in Phase C and then cool to 40°C and add Phase D.

Claims: CLAIMS Hydroxy salt of the formula M (OH) (2-a) J x b a b zJL j O wherein M is Zn, Cu or a combination of both, and X denotes anions at least some of which display ultraviolet absorption over at least a portion of the wavelength range from 290 to 400 nanometres. 2. Hydroxy salt according to claim 1 wherein at least some of the anions X display ultraviolet absorption with a molar extinction coefficient of at least 2 x IO 3 over at least a portion of the wavelength range from 290 to 400 nanometres. 3. Hydroxy salt according to claim 1 wherein at least 5 mole % of the anions X are the anions of one or more of para amino benzimidazole-5-sulphonate 3-imidazol-4-ylacrylate salicylate p-methoxy cinnamate 2 ethyl hexyl-2-cyano-3,3 diphenyl acrylate 3,3,5 trimethylcyclohexyl-2-acetamido benzoate cinnamate p-aminobenzoate 3,4-dimethoxy phenyl glyoxylate a- (2-oxoborn-3-ylidene) -p-xylene-2-sulphonate oi- (2-oxoborn-3-ylidene)toluene-4-sulphonate α-cyano-4-methoxy cinnamate 2-phenyl benzimidazole-5-sulphonate. 4. Hydroxy salt according to claim 1 or claim 2 wherein at least 5 mole % of the anions X are anions of phenolic compounds, especially compounds comprising a hydroxylated benzophenone moiety, which display ultraviolet absorption over at least a portion of the wavelength range from 200 to 400nm. 5. Hydroxy salt according to claim 4 wherein at least 5 mole % of the anions X are anions of one or more of: ' Benzophenone-1 Benzophenone-2 Benzophenone-3 Benzophenone-4 Benzophenone-5 Benzophenone-6 Benzophenone-7 Benzophenone-8 Benzophenone-9 Benzophenone-10 Benzophenone-12 butyl methoxydibenzoylmethane 1- (4-methoxy-5-benzofuranyl)-3-phenyl-l,3-propanedione homomenthyl salicylate, or * 2-ethylhexyl salicylate. 6. Hydroxy salt according to claim 1 or claim 2 wherein at least a majority of the anions X are anions of any of the compounds named in claims 3 and 5. 7. Hydroxy salt according to any one of the preceding claims wherein a majority of the anions X display a molar extinction coefficient of at least 5 x 10 3 . 8. A sunscreen composition for application to human skin comprising a cosmetically acceptable vehicle incorporating hydroxy salt as set out in any one of the preceding claims.

Inventors: FRANKLIN KEVIN RONALD, NUNN CHARLES CRAIG, FRANKLIN, KEVIN, RONALD, NUNN, CHARLES, CRAIG
Applicants: UNILEVER NV, UNILEVER PLC, UNILEVER N.V.
Application year: 1994
Main classification: A61K7
IPC codes: A61K8, A61K31, A61Q17, A61Q19, C07F1, C07F3