Granular multilayer magnetoresistive sensor

Abstract: A magnetoresistive read sensor incorporates a granular multilayer sensing element comprising a plurality of layers of generally flat particles (31) of a ferromagnetic material embedded in a nonmagnetic electrically conductive material. A bias layer (45) separated from the magnetoresistive sensing element by a spacer layer (43) provides a magnetic field to bias the magnetoresistive sensing element at a desired non-signal point. The ferromagnetic and the nonmagnetic materials are mutually immiscible, or may be miscible or partially miscible and processed in a manner to control interdiffusion. The magnetoresistive sensing element is formed by alternatively depositing layers of ferromagnetic material and layers of nonmagnetic conductive material on a substrate and then annealing the structure. During the annealing cycle, the layers of nonmagnetic material above and below the ferromagnetic layers penetrate at grain boundaries and break the continuity of the ferromagnetic layers to form layers or planes of ferromagnetic particles embedded in a matrix of nonmagnetic material.

Description: The present invention relates generally to magnetic transducers for reading information signals recorded in a magnetic medium. It is well-known in the prior art to utilize a magnetic read transducer referred to as a magnetoresistive (MR) sensor or head for reading high density recorded data from magnetic media. An MR sensor detects magnetic field signals through the resistance changes of a read element fabricated of a magnetic material as a function of the strength and direction of magnetic flux being sensed by the read element. These prior art MR sensors operate on the basis of the anisotropic magnetoresistive (AMR) effect in which a component of the read element resistance varies as the square of the cosine (cos 2 ) of the angle between the magnetization and the direction of sense current flow through the read element. A more detailed description of the AMR effect can be found in "Memory, Storage, and Related Applications", D.A. Thompson et al., IEEE Trans. Mag. MAG-11, p. 1039 (1975). U.S. Patent No. 4,896,235 entitle "Magnetic Transducer Head Utilizing Magnetoresistance Effect", granted to Takino et al on January 23, 1990, discloses a multilayered magnetic sensor which utilizes the AMR and comprises first and second magnetic layers separated by a non-magnetic layer in which at least one of the magnetic layers is of a material exhibiting the AMR effect. The easy axis of magnetization in each of the magnetic layers is set perpendicular to the applied magnetic signal such that the MR sensor element sensor current provides a magnetic field in the magnetic layers parallel to the easy axis thus eliminating or minimizing Barkhausen noise in the sensor. "Thin Film MR Head for High Density Rigid Disk Drive" by H. Suyama et al, IEEE Trans. Mag., Vol. 24, No. 6, 1988 (pages 2612-2614) discloses an multilayered MR sensor similar to that disclosed by Takino et al. A second, different and more pronounced magnetoresistive effect has also been described in which the change in resistance of a layered magnetic sensor is attributed to the spin-dependent transmission of conduction electrons between ferromagnetic layers via a nonmagnetic layer separating the ferromagnetic layers and the accompanying spin-dependent scattering at the layer interfaces. This magnetoresistive effect is variously referred to as the "giant magnetoresistive" or "spin valve" effect. Such a magnetoresistive sensor fabricated of the appropriate materials provides improved sensitivity and greater change in resistance than observed in sensors utilizing the AMR effect. In this type of MR sensor, the in-plane resistance between a pair of ferromagnetic layers separated by a non-magnetic layer varies as the cosine (cos) of the angle between the magnetization in the two layers. U.S. Patent No. 4,949,039 to Grunberg describes a layered magnetic structure which yields enhanced MR effects caused by antiparallel alignment of the magnetizations in the magnetic layers. As possible materials for use in the layered structure, Grunberg lists ferromagnetic transition metals and alloys, but does not indicate preferred materials from the list for superior MR signal amplitude. Grunberg further describes the use of antiferromagnetic-type exchange coupling to obtain the antiparallel alignment in which adjacent layers of ferromagnetic materials are separated by a thin interlayer of Cr or Y. Co-pending U.S. Patent Application serial no. 07/625,343 filed December 11, 1990, assigned to International Business Machines Corporation (IBM), discloses an MR sensor in which the resistance between two uncoupled ferromagnetic layers is observed to vary as the cosine of the angle between the magnetizations of the two layers and which is independent of the direction of current flow through the sensor. This mechanism produces a magnetoresistance that is based on the spin valve effect and, for selected combinations of materials, is greater in magnitude than the AMR. U.S. Patent No. 5,159,513 granted to Dieny et al on October 27, 1992, assigned to the instant assignee, discloses an MR sensor based on the above-described effect which includes two thin film layers of ferromagnetic material separated by a thin film layer of a non-magnetic metallic material wherein at least one of the ferromagnetic layers is of cobalt or a cobalt alloy. The magnetization of the one ferromagnetic layer is maintained perpendicular to the magnetization of the other ferromagnetic layer at zero externally applied magnetic field by exchange coupling to an antiferromagnetic layer. The spin valve structures described in the above-cited U.S. patent and patent application require that the direction of magnetization in one of the two ferromagnetic layers be fixed or "pinned" in a selected orientation such that under non-signal conditions the direction of magnetization in the other ferromagnetic layer is oriented perpendicular to the pinned layer magnetization. Additionally, in both the AMR and spin valve structures, in order to minimize Barkhausen noise, it is necessary to provide a longitudinal bias field to maintain at least the sensing portion of the read element in a single magnetic domains state. Thus, a means for both fixing the direction of the magnetization and providing a longitudinal bias field is required. For example, as described in the above-cited patent application and patents, an additional layer of antiferromagnetic material can be formed in contact with the ferromagnetic layer to provide an exchange-coupled bias field. Alternatively, an adjacent magnetically hard layer can be utilized to provide hard bias for the ferromagnetic layer. More recently, the giant magnetoresistance effect has been observed in both single- and multi-layer heterogeneous films of ferromagnetic particles embedded in a nonmagnetic metallic matrix. GMR has been reported in inhomogeneous, single layer alloy systems such as cobalt-copper (Co-Cu), cobalt-silver (Co-Ag) and nickel-iron-silver (NiFe-Ag). For example, see "GIANT MAGNETORESISTANCE IN NONMAGNETIC MAGNETIC SYSTEMS", John Q. Xiao et al, PHYSICAL REVIEW LETTERS , Vol. 68, No. 25,pages 3749-3752 (June 22, 1992); "GIANT MAGNETORESISTANCE IN HETEROGENEOUS CU-CO ALLOYS", A.E. Berkowitz et al, PHYSICAL REVIEW LETTERS , Vol. 68, No. 25, pages 3745-3748 (June 22, 1992); "'GIANT' MAGNETORESISTANCE OBSERVED IN SINGLE LAYER CO-AG ALLOY FILMS", J.A. Barnard et al, Letter to the Editor, JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS , 114 (1992), pages L230-L234; and J. Jaing et al, APPLIED PHYSICS LETTERS , Vol. 61, page 2362 (1992). The Co alloys are of materials that are immiscible at low temperatures. However, annealing the metastable alloy causes the formation of fine Co precipitates, i.e., "grains", in a Cu or Ag matrix. The MR effect appears to vary inversely with the diameter of the average particle diameter. While the "granular" alloy is an attractive approach to achieve a GMR sensor with only a single film in contrast to the more complex multilayered spin valve sensors, the Co alloys require saturation fields of several thousand Oersted (Oe) and would not be useful in a low field MR sensor application. Recently reported work with granular NiFe in a Ag matrix has yielded MR ((delta R)/R) of 10 percent at room temperature with the half-height width of the MR peak of about 400 Oe. More recent work with annealed NiFe multilayers in a Ag matrix has yielded a granular multilayer structure which exhibits an MR of approximately 17 percent at room temperature with a saturation field of about 100 Oe. See "MAGNETORESISTIVE PROPERTIES AND THERMAL STABILITY OF NI-FE/AG MULTILAYERS", B. Rodmacq et al, Letter to the Editor, JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 118(1993), pages L11-L16. Although the saturation fields for the single- and multiple-layer NiFe alloys are lower than the reported value for Co alloys, it is still above the range that is useful for MR devices (about 10 Oe or less). In accordance with the present invention, there is now provided a granular multilayer magnetoresistive sensor comprising a magnetoresistive sensing element having at least one discontinuous layer of oblate particles of ferromagnetic material embedded in a layer of nonmagnetic electrically conductive material. The invention is defined in the appended claims. Preferred embodiments of the present invention will now be described with reference to the accompanying drawings, in which: Figure 1 is a simplified block diagram of a magnetic disk storage system embodying the present invention; Figure 2 is a view in perspective of a preferred embodiment of a granular multilayer magnetoresistive sensing element according to the principles of the present invention; Figure 3 is a cross-sectional view illustrating the multilayer sensing element shown in Figure 2 prior to the anneal process; Figure 4 is a perspective view of the annealed multilayer sensing element shown in Figure 2 illustrating the orientation of the individual magnetic domains; Figure 5 is a cross-sectional view illustrating a specific embodiment after anneal of the multilayer sensing element shown in Figure 2; Figure 6 is a graph illustrating the magnetoresistance versus an applied magnetic field as a function of anneal temperature for a specific embodiment of the multilayer sensing element shown in Figure 2; Figure 7 is a graph which illustrates the magnetoresistance versus an applied magnetic field for a preferred embodiment of the magnetoresistive sensing element shown in Figure 2; Figure 8 is a graph which illustrates the magnetoresistance versus an applied magnetic field for a preferred embodiment of the magnetoresistive sensing element shown in Figure 2; Figure 9 is a graph which illustrates the magnetoresistance versus the anneal temperature as a function of silver layer thickness for a preferred embodiment of the magnetoresistive sensing element shown in Figure 2; Figure 10 is a graph which illustrates the magnetoresistance versus the anneal temperature as a function of nickel-iron layer thickness for a preferred embodiment of the magnetoresistive sensing element shown in Figure 2; Figure 11 is a graph which illustrates the magnetoresistance versus the number of bilayers for a preferred embodiment of the magnetoresistive sensing element shown in Figure 2; Figure 12 is a graph which illustrates the magnetoresistance versus an applied magnetic field as a function of anneal temperature for a preferred embodiment of the magnetoresistive sensing element shown in Figure 2; and Figure 13 is a sectional view of a preferred embodiment of a magnetoresistive magnetic sensor according to the principles of the present invention. Referring now to Fig. 1, although the invention is described as embodied in a magnetic disk storage system as shown in Fig. 1, it will be apparent that the invention is also applicable to other magnetic recording systems such as a magnetic tape recording system, for example, or other applications in which a sensor is utilized to detect a magnetic field. A magnetic disk storage system comprises at least one rotatable magnetic disk 12 is supported on a spindle 14 and rotated by a disk drive motor 18 with at least one slider 13 is positioned on the disk 12, each slider 13 supporting one or more magnetic read/write transducers 21, typically referred to as read/write heads. The magnetic recording media on each disk is in the form of an annular pattern of concentric data tracks (not shown) on disk 12. As the disks rotate, the sliders 13 are moved radially in and out over the disk surface 22 so that the heads 21 may access different portions of the disk where desired data is recorded. Each slider 13 is attached to an actuator arm 19 by means of a suspension 15. The suspension 15 provides a slight spring force which biases the slider 13 against the disk surface 22. Each actuator arm 19 is attached to an actuator means 27. The actuator means as shown in Fig.1 may be a voice coil motor (VCM), for example. The VCM comprises a coil moveable within a fixed magnetic field, the direction and velocity of the coil movements being controlled by the motor current signals supplied by a controller. During operation of the disk storage system, the rotation of the disk 12 generates an air bearing between the slider 13 and the disk surface 22 which exerts an upward force or lift on the slider. The air bearing thus counterbalances the slight spring force of the suspension 15 and supports the slider 13 off and slightly above the disk surface by a small, substantially constant spacing during operation. The various components of the disk storage system are controlled in operation by control signals generated by control unit 29, such as access control signals and internal clock signals. Typically, the control unit 29 comprises logic control circuits, storage means and a microprocessor, for example. The control unit 29 generates control signals to control various system operations such as drive motor control signals on line 23 and head position and seek control signals on line 28. The control signals on line 28 provide the desired current profiles to optimally move and position a selected slider 13 to the desired data track on the associated disk 12. Read and write signals are communicated to and from read/write heads 21 by means of recording channel 25. The above description of a typical magnetic disk storage system, and the accompanying illustration of Fig. 1 are for representation purposes only. It should be apparent that disk storage systems may contain a large number of disks and actuators, and each actuator may support a number of sliders. Referring now to Figs. 2, 3 and 4, Fig. 2 is a perspective view illustrating a granular multilayer magnetic structure 30 comprising layers of generally flat or oblate "pancake" or disc-like magnetic particles or islands 31 suspended or embedded in a nonmagnetic matrix 33 of an electrically conductive material. As shown in Fig. 3, a multilayer structure 34 of layers 35 of a ferromagnetic material alternatively deposited with layers 37 of a nonmagnetic conductive material is prepared, such as by sputter deposition, with the thickness of the individual layers being controlled by a quartz monitor, for example. The magnetic material and the nonmagnetic material are chosen such that the two materials are immiscible. Alternatively, the magnetic and nonmagnetic materials can be miscible or partially miscible under equilibrium conditions processed in a controlled manner to limit interdiffusion. After deposition, the structure 34 is then annealed. During the annealing process, the magnetic layers 35 break up into flat plate-like particles 31 as the immiscible layers 37 above and below the magnetic layers 35 penetrate at grain boundaries and break the continuity of the magnetic layers 35 thus forming layers or planes of magnetic particles 31 embedded in a matrix of nonmagnetic material 33. Other deposition or film-forming processes may also be used, such as, plating, ion deposition, evaporation, or pastes or other mechanical methods. Additionally, it is not required that the anneal process be performed after completion of the deposition process. Deposition may be dome at elevated temperatures or on heated substrates to achieve the desired granular magnetic structures. A substantial MR effect is achieved in the granular structure 30 if the spacing between the magnetic particles 31 is comparable to the mean free path of conduction electrons in the matrix material, preferably being less than the electron mean free path. As in the well-known magnetic/nonmagnetic multilayer spin valve systems described above, the origin of the MR observed in the granular multilayer structure 30 is believed to be primarily due to spin-dependent scattering of conduction electronics traversing the matrix between the magnetic regions or particles 31. While it is recognized that larger particles may comprise more than one or multiple magnetic moments, for analysis, it can be assumed that each of the flat particles 31 behave as if it constituted a single magnetic moment or domain, as shown in Fig. 4. If the magnetic moments of the particles 31 are randomly oriented, spin dependent scattering from particle to particle is increased resulting in a relatively high resistivity for the structure 30. The greatest resistivity is observed when the magnetic moments of the particles 31 are oriented antiparallel from layer to layer. On the other hand, if the magnetic moments of the particles 31 are aligned in a parallel orientation, the resistance decrease to a relatively low value. While it is recognized that magnetostatic and exchange coupling exists between the particles in the matrix, a single particle model analysis which neglects interactions between particles is sufficient to show the that the observed MR is strongly dependent on the particle 31 size, shape and anisotropy. It can be shown that an oriented collection of flat plate-like magnetic particles are much more easily polarized, i.e., aligned, than a similar collection of spherical magnetic particles. Additionally, a high width to thickness ratio reduces the effects of shape anisotropy on the field required for alignment of the particles moments. For example, for a plate thickness of 30 Angstroms (A), a major axis dimension of approximately 500 A is required. This particle size is quite large when compared to the 40 A particle size reported in the above-cited literature with large values of MR (and accompanying large values for the saturation fields). With continuing reference to Fig. 4, a conceptual diagram of an MR sensor 40 arranged in sensing relationship with a data track 44 defined on a magnetic recording media surface (not shown) is illustrated. The MR sensor 40 comprises an MR sensing element 41, a bias layer 45 separated from the sensing element 41 by a nonmagnetic spacer layer 43 and is connected to a current source (not shown) by conductors 49 to provide a sensing current I to the MR sensor 41. The MR sensing element 41 is a granular multilayer magnetic structure as described above with reference to Figs. 2 and 3 including a number of layers or planes of plate-like particles 31 in a metallic conductive matrix 33. The magnetic moments of the particles 31 may be partially oriented along an induced anisotropic axis, as shown by arrow 47. An anisotropic axis may be induced in the MR sensing element 41 by a second annealing cycle in the presence of a magnetic field in the direction of the desired anisotropic axis, as is known in the art. The bias field provided by the bias layer 45 will further align the moments of the particles 31 in a desired direction to adjust the operating point of the MR sensor at a linear portion of its response characteristic. The MR sensor 40 is suspended above a data track 44 by a suspension apparatus (not shown) such that the magnetic field H at a data transition 46 will be applied in the plane of the sensing element 41. When the field H is intercepted, the magnetic moments rotate to align with the applied field H resulting in a decrease in the resistivity in the sensing element 41. Since rotation of the magnetization of the magnetic particles occurs with limited domain wall motion, a longitudinal bias field for the sensing element is not required. Referring now also to Figs. 5 and 6, a multilayer structure 50 of layers 51 of a ferromagnetic material alternatively deposited with layers 53 of a nonmagnetic conductive material having the form Ag(y/2)/NiFe(x/2)[NiFe(x)/Ag(y)] n-1 /NiFe(x/2)/Ag(y/2) deposited over a Ta underlayer 55 on an oxidized silicon (Si) substrate 54. A 100 A Ta capping layer 57 minimizes oxidation during the anneal process. The anneal process promotes penetration on the non-magnetic material, Ag layers 53, at the grain boundaries 56 of the magnetic layers 51 producing discontinuities in the magnetic layers to provide planes of flat, island-like particles 59. Thus, each layer of magnetic material is broken-up into a multidomain or granular state. Within a magnetic layer, as long as the layer of magnetic material is discontinuous, the spacing between the particles does not appear to strongly influence the observed magnetoresistance for the structure provided that the spacing is less than the mean free path for the conduction electrons in the non-magnetic material. Discontinuities in the magnetic layers 51, particularly if the discontinuities are arranged into columns from layer to layer in the structure, prompts an interlayer magnetostatic interaction that strongly favors antiferromagnetic order. No significant MR was observed in any structure examined prior to annealing. As shown in Fig. 6, for a structure having 5 layers of NiFe of the form Ag(20A)/[NiFe(20A)/Ag(40A)] 4 /NiFe(20A)/Ag(20A) MR develops after annealing to achieve magnitudes of typically 5-6 percent. The applied magnetic field is in the plane of the structure and perpendicular to the sensing current. Arrow 58 indicate the ramping direction of the field. Typically, the resistance of the as-deposited structure decrease by about 15 percent after annealing at any temperature in the 300-400 degrees C range, and there is no significant difference in the resistance of any annealed structure. A difference in the magnitudes of the MR for magnetic fields applied parallel and perpendicular to the sense current direction indicates a persistent AMR effect of a magnitude of about 0.3-0.5 percent in both the unannealed and annealed structures. For the structure shown in Fig. 6, a maximum MR of 5.34 percent is observed after annealing at 335 degree C with a width at half maximum of 22 Oe. While exhibiting a lower maximum value for MR, when annealed at 315 degrees C the greatest change in resistance per unit field, 0.8 percent per Oe with a width at half maximum of about 5 Oe was observed. Referring now also to Figs. 7 and 8, Fig. 7 is a diagram illustrating the observed MR as a function of applied magnetic field for a granular multilayer structure 30 (as shown in Fig. 2) comprising 3 bilayers of NiFe(20 A)/Ag(40 A) sputter deposited on an oxidized Si substrate and annealed at 310 degrees C. The MR of the structure is defined as the ratio of the structure resistivity at the applied field, R(H), minus the resistivity of the structure at an applied field of 200 Oe, R(MIN), to the R(MIN). The structure exhibits a maximum value for the MR of approximately 3.0 percent with the curve 52 having a half-height width of approximately 10 Oe for fields applied along the hard axis. Similarly, the structure exhibits a maximum value for the MR of approximately 2.7 percent with the curve 54 having a half-height width of approximately 7 Oe for fields applied along the easy axis. Fig. 8 is a diagram illustrating the observed MR for a granular multilayer structure 30 comprising 5 bilayers of NiFe(20 A)/Ag(35 A) on an oxidized Si substrate and annealed at a temperature of 315 degrees C. This structure exhibits a maximum MR value of approximately 3.4 percent with the MR curve having a half-height width of approximately 4.75 Oe and a slope of 0.71 percent per Oe. Referring now also to Figs. 9-12, the value of MR obtained for the granular multilayer structure 30 is dependent on a number of factors in addition to the materials chosen for the ferromagnetic and nonmagnetic layers. For example, the number of ferromagnetic/nonmagnetic bilayers, the thickness of the ferromagnetic layers, the thickness of the nonmagnetic layers and the temperature at which the structure 30 is annealed all affect the MR characteristics obtained for a specific structure. Fig. 9 is a diagram illustrating the value of MR versus anneal temperature as a function of the nonmagnetic layer thickness for a granular structure comprising 5 bilayers of Ag(t x A)/NiFe(20 A) deposited on an oxidized Si substrate. Generally, the maximum MR for a given nonmagnetic layer thickness is obtained at an anneal temperature of about 335 degrees C, with the maximum MR obtained being about 5.3 percent for a nonmagnetic layer (Ag) thickness of 35 A. Fig. 10 is a diagram illustrating the value of MR versus anneal temperature as a function of the thickness of the ferromagnetic layer thickness for a granular structure 30 comprising 5 bilayers of Ag(40 A)/NiFe(t x A) deposited on an oxidized Si substrate. Generally, the maximum MR value for a given thickness was achieved at an anneal temperature in the range of 315 to 335 degrees C, with a maximum MR value of about 5.3 percent observed for a ferromagnetic layer (NiFe) thickness of 20 A at 335 degrees C. Fig. 11 is a diagram illustrating the value of MR versus the number of ferromagnetic/nonmagnetic bilayers for a granular structure comprising bilayers of NiFe(20 A)/Ag(40 A) deposited on an oxidized Si substrate. The function starts with a relatively low MR value of about 0.2 percent for a single bilayer, deposited on a layer of Ag, increases rapidly to about 5.3 percent for 5 bilayers, and then flattens out having a value of about 6.1 percent for 10 bilayers. The low value for MR observed for a structure having a single bilayer compared to the relatively high MR values observed for multiple bilayers appears to indicate that scattering of conduction electrons at the particles 31 in the layers above and below the layer in which the conduction electrons originate is much more important than the scattering at particles 31 within the same layer. Fig. 12 is a diagram illustrating the MR value versus applied magnetic field as a function of anneal temperature for a granular structure 30 comprising 5 bilayers of NiFe(20 A)/Ag(40 A) deposited on an oxidized Si substrate. As would be expected from the curves shown by Figs. 9 and 10, the maximum value 61 of about 5.3 percent for MR is observed at an anneal temperature of 335 degrees C. However, while the maximum observed MR value is lower, about 3.2 percent, at an anneal temperature of 305 degrees C, a much sharper characteristic curve 63 having a half-height width of less than 5 Oe is produced. Referring now also to Fig. 13, an MR magnetic sensor incorporating a granular multilayer sensing element according to the principles of the present invention is shown. The MR sensor 70 comprises a bias layer 73 of a suitable magnetic material, a nonmagnetic spacer or isolation layer 75 and granular MR sensing layer 79 deposited on a suitable substrate 71. The substrate provides a major surface 72 which functions as a support or carrier for the subsequent layers making up the MR sensor. The substrate 71 may be glass, sapphire, quartz, magnesium oxide, silicon, silicon dioxide or other suitable material. An underlayer 73 is first deposited over the substrate surface 72. The purpose of the underlayer 73 is to optimize the texture, grain size and morphology of the subsequent layers 75, 77 and 79. The underlayer 73 must have a high resistivity to minimize electrical current shunting effects. Generally, nonmagnetic, high resistivity materials such as tantalum (Ta), ruthenium (Ru) or aluminum oxide, for example, are suitable materials. The granular MR sensing layer 79 comprises multiple layers of flat, plate-like magnetic particles 31 embedded or suspended in a nonmagnetic conductive matrix 33 as described above with reference to Figs. 2, 3 and 4. The granular structure is made up of multiple ferromagnetic/nonmagnetic bilayers formed depositing thin layers of a nonmagnetic material alternatively with thin layers of a ferromagnetic material and then annealing the structure at a temperature within the range of about 100 to 500 degrees C. While the granular MR sensing layer 79 preferably comprises 5 or 6 bilayers, MR values suitable for use in an MR sensor can be obtained with as few as 3 or more bilayers. As deposited, prior to the anneal cycle, the ferromagnetic layers are of a thickness in the range of about 10 to 30 A, while the thickness of the nonmagnetic layers are in the range of about 20 to 50 A. The ferromagnetic layer is preferably of NiFe, but can be of any suitable ferromagnetic material such as Ni, Co, Fe and ferromagnetic alloys based on Ni, Fe or Co, for example. The matrix 33 is a nonmagnetic, conductive material and should allow a long mean free path for conduction electrons in the material. Additionally, the ferromagnetic material and the matrix material are mutually immiscible. Alternatively, the magnetic and non-magnetic materials can be miscible or partially miscible under equilibrium conditions and processed in a controlled manner to limit interdiffusion. The matrix material is preferably Ag, but may be selected from the group consisting of Cu, Ru and Au and other conducting metals and alloys. Suitable semiconductor, conductive oxides and intermetallic compounds may also provide materials which are potential candidates. Alloying the ferromagnetic material with a suitable material can enhance the breakup of the layer into particles during the anneal cycle. For example, alloying NiFe with 1 to 20 percent Ag or 0.1 to 20 percent lead (Pb) enhances the breakup of the NiFe layer in a Ag matrix. Since, for example, Ni-Pb and Fe-Pb have very limited mutual solubility, it appears that the Pb concentrates at the NiFe grain boundaries during processing thus enhancing the NiFe layer breakup and allowing the use of lower process temperatures. The use of NiFePb at lower process temperatures may allow the use of other materials, such as Cu, as the matrix material in which the rate of solubility with NiFe is less at lower temperatures than at higher temperatures. The bias layer 73 provides a bias field for the MR sensing layer 79 to provide a linear response for the sensor. As is known in the art, the bias layer may be of a magnetically hard material (hard bias), such as CoPt or CoPtCr, for example, or of a magnetically soft material (soft bias), such as NiFe or NiFeRh, for example. The spacer layer 77 serves to magnetically decouple the bias layer 75 from the MR sensing layer 79 and also to optimize the texture, grain size and morphology of the MR sensing layer. The spacer layer 77 should be of a nonmagnetic, high resistivity material such as Ta, Zr, Ti, y, Hf or other suitable material having the desired crystalline structure. A preferred embodiment of the MR sensor 70 comprises an granular MR sensing layer 79 of 5 bilayers of NiFe(20A)/Ag(35A) annealed at 315 degrees C, a soft bias layer 75 of NiFe deposited on an underlayer 73 of Al 2 O 3 and separated from the MR sensing layer 79 by a spacer layer 77 of Ta having a thickness of approximately 50 A. The sensor 70 is deposited on a ceramic substrate 71 by sputter deposition or other suitable deposition process as is known in the art. The thickness of the underlayer 73 preferably is in the range of 50 to 100 A, while the NiFe soft bias layer 75 thickness is 100 A. Conductor terminals 81 of Cu or other suitable material, such as Ag or Au, formed at opposite ends of the sensor 70 connect the sensor to current source 85 and signal sensing circuitry 83 via lead conductors 87. The current source 85 provides a sense current to the MR sensor 70 which senses the changes in resistance of the MR sensing element 79 when an external magnetic field is applied (for example, as described above with reference to Fig. 4). A capping layer (not shown) of a high resistivity material such as Ta or Zr, for example, can also be deposited over the MR sensor 70. While the present invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the invention. For example, while the preferred embodiment shown is described as an unshielded device, the MR sensor of the present invention is equally applicable to a shielded or flux-guided structure. Accordingly, the invention herein disclosed is to be considered merely as illustrative and limited in scope only as specified in the appended claims.

Claims: A granular multilayer magnetoresistive sensor comprising a magnetoresistive sensing element (41) having at least one discontinuous layer of oblate particles (31) of ferromagnetic material embedded in a layer (33) of nonmagnetic electrically conductive material. A sensor as claimed in claim 1 wherein said ferromagnetic material and said nonmagnetic material are mutually immiscible. A sensor as claimed in Claim 1 further comprising: a bias layer (45) of a magnetic material for providing a magnetic bias field for said magnetoresistive sensing element; and a spacer layer (43) of a nonmagnetic material disposed between said bias layer and said magnetoresistive sensing element magnetically decoupling said bias layer from said magnetoresistive sensing element (41). A sensor as claimed in Claim 1 wherein said magnetoresistive sensing element (41) comprises a number N of said layers of said ferromagnetic particles embedded in N+1 layers of said nonmagnetic conductive material. A sensor as claimed in Claim 4 wherein said number N is selected from a range of 2 to 10. A sensor as claimed in Claim 5 wherein said number N is 5. A sensor as claimed in Claim 1 wherein said ferromagnetic particles (31) are comprised of a ferromagnetic material selected from the group consisting of iron, cobalt, nickel, nickel-iron and ferromagnetic alloys based on iron, cobalt, nickel or nickel-iron. A sensor as claimed in Claim 7 wherein said ferromagnetic particles are comprised of nickel-iron. A sensor as claimed in Claim 7 wherein said ferromagnetic particles are comprised of nickel-iron-cobalt. A sensor as claimed in Claim 4 wherein said ferromagnetic particles are comprised of nickel-iron-lead. A sensor as claimed in Claim 10 wherein the amount of lead contained in said nickel-iron-lead alloy is selected from the range of 0.1 to 20 percent by weight. A sensor as claimed in Claim 4 wherein said ferromagnetic particles are comprised of nickel-iron-silver. A sensor as claimed in Claim 12 wherein the amount of lead contained in said nickel-iron-silver alloy is selected from the range of 1 to 20 percent by weight. A sensor as claimed in Claim 1 wherein said nonmagnetic electrically conductive layer is of a material selected from the group consisting of silver, gold, copper and ruthenium. A sensor as claimed in Claim 14 wherein said nonmagnetic electrically conductive layer (33) is of silver. A sensor as claimed in Claim 3 wherein said bias layer comprises a layer of magnetically soft material for providing said magnetic bias field. A sensor as claimed in Claim 16 wherein said magnetically soft material comprises a material selected from the group consisting of nickel-iron and nickel-iron-rhodium. A sensor as claimed in Claim 3 wherein said bias layer comprises a layer of magnetically hard material for providing said magnetic bias field. A sensor as claimed in Claim 18 wherein said magnetically hard material comprises a material selected from the group consisting of cobalt-platinum and cobalt-platinum-chromium. A sensor as claimed in Claim 1 wherein said ferromagnetic particles have a thickness within the range of about 10 angstroms to about 30 angstroms. A sensor as claimed in Claim 1 wherein said ferromagnetic particles have a thickness of about 20 angstroms. A sensor as claimed in Claim 1 wherein said nonmagnetic conductive layer (33) has a thickness less than the mean free path length of conduction electrons in said nonmagnetic conductive material. A sensor as claimed in Claim 22 wherein said nonmagnetic conductive layer (33) has a thickness within the range of about 10 angstroms to about 50 angstroms. A sensor as claimed in Claim 23 wherein said nonmagnetic conductive layer (33) has a thickness of about 35 angstroms. A sensor as claimed in Claim 3 wherein said spacer layer (43) comprises a material selected from the group consisting of tantalum, zirconium, titanium, yttrium and hafnium. A sensor as claimed in Claim 25 wherein said spacer layer (43) comprises tantalum. A magnetic storage system comprising: a magnetic storage medium (12) having a plurality of tracks defined on a surface thereof for recording of data; a magnetic transducer (13) maintained in a closely spaced position relative to said magnetic storage medium during relative motion between said magnetic transducer and said magnetic storage medium, said magnetic transducer including sensor as claimed in any preceding claim; actuator means (27) coupled to said magnetic transducer for moving said magnetic transducer to selected data tracks on said magnetic storage medium; and detection means (83) coupled to said sensor for detecting resistance changes in said magnetoresistive sensing element responsive to applied magnetic fields representative of data bits recorded in said magnetic storage medium intercepted by said sensor. A magnetic storage system as in Claim 27 wherein the magnetic easy axis for said magnetoresistive sensing element is oriented substantially parallel to said data track trackwidth, said easy axis parallel to said magnetoresistive sensing element longitudinal axis.

Inventors: COFFEY KEVIN ROBERT, HOWARD JAMES KENT, HYLTON TODD LANIER, PARKER MICHAEL ANDREW, COFFEY, KEVIN ROBERT, HOWARD, JAMES KENT, HYLTON, TODD LANIER, PARKER, MICHAEL ANDREW
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1994
Main classification: G11B5
IPC codes: H01F10, H01L43, G01R33, G11B5