Fully substituted cyclopolysiloxanes and their use for making organosilicon polymers

Abstract: Disclosed are organosilicon crosslinked polymers and crosslinkable prepolymers that are the reaction product of (a) a cyclic polysiloxane in which each silicon atom is substituted with (i) a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, and (ii) a substituted or unsubstituted hydrocarbon group having at least one carbon-carbon double bond that is reactive in hydrosilation, (b) at least one organosilicon compound having at least two ≡SiH groups, and optionally (c) a hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation. A process for preparing the polymers and prepolymers and for preparing the cyclic polysiloxanes is also disclosed.

Description: This invention relates to the preparation of organosilicon polymers and prepolymers from cyclic polysiloxanes. The invention also relates to the preparation of cyclic polysiloxanes. Leibfried, in U.S. Patent Nos. 4,900,779, 4,902,731 and 5,013,809, and Bard and Burnier in U.S. Patent Nos. 5,008,360 and 5,068,303, describe crosslinked organosilicon polymers and crosslinkable organosilicon prepolymers comprising alternating polycyclic hydrocarbon residues and cyclic polysiloxane or siloxysilane residues linked through carbon-to-silicon bonds. These polymers are useful, for example, in structural and electronic applications. Although cyclic trisiloxanes were disclosed for use in the preparation of organosilicon polymers and prepolymers in U.S. Patent 5,013,809 (Leibfried) and in Research Disclosure 326103 (June, 1991), these cyclic trisiloxanes were required to have two or more hydrogen atoms bound to silicon. Only cyclosiloxanes containing four or more silicon atoms were used in the preparation of these polymers and prepolymers, because cyclotrisiloxanes are not readily available and are unstable. It is also known that cyclotrisiloxanes with hydrogen atoms and methyl groups bonded to every silicon atom are not storage-stable. In Chemical Abstracts Vol. 77, 1972, abstract No. 88573n 1,3,5-trimethyl-1,3,5-tridicyclopentadienylcyclotrisiloxane and a process for the preparation of this compound is disclosed. According to this invention organosilicon crosslinked polymers or crosslinkable prepolymers are prepared by a hydrosilation reaction and are characterized in that they are the reaction product of: (a) a cyclic polysiloxane having the formula: where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and n is 3, or a mixture of 3 and 4, and (b) at least one organosilicon compound having at least two ≡SiH groups selected from the group consisting of (1) cyclic polysiloxanes and (2) tetrahedral siloxysilanes. The reaction mixture can optionally contain as a third component (c) at least one hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation. Also according to the invention, a method is disclosed for preparing the fully-substituted cyclic polysiloxanes, and processes are disclosed for preparing prepolymers and polymers from the fully-substituted cyclic polysiloxanes, other organosilicon compounds, and, optionally, a polycyclic polyene. The organosilicon polymers prepared according to this invention have improved shear modulus and coefficient of thermal expansion compared with polymers made without the fully-substituted cyclic polysiloxanes. The invention also provides a simple method for preparing storage-stable cyclic polysiloxanes. The fully-substituted cyclic polysiloxanes used as component (a) in the preparation of the organosilicon polymers and prepolymers have the general formula: where R and R' are defined below and n = 3, or a mixture of 3 and 4. The notation "3 and 4" means that a mixture of a cyclic trisiloxane (n = 3) and a cyclic tetrasiloxane (n = 4) is used. The fully-substituted cyclic polysiloxanes are prepared by first reacting a dichlorosilane having the formula Cl 2 HSiR in which R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, with a substituted or unsubstituted hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation. The alkyl groups are preferably 1-10 carbon alkyl groups and the aryl groups are preferably 6-10 carbon aryl groups. The alkyl or aryl groups of the dichlorosilane, or the hydrocarbon polyene, can be substituted with any substituents that do not interfere with subsequent hydrosilation reactions. Examples of suitable hydrocarbon polyenes include polycyclic polyenes such as, for example, cyclopentadiene oligomers (e.g., dicyclopentadiene, tricyclopentadiene and tetracyclopentadiene), bicycloheptadiene (also known as norbornadiene) and its Diels-Alder oligomers with cyclopentadiene (e.g., dimethanohexahydronaphthalene), norbornadiene dimer, hexahydronaphthalene, and substituted derivatives of any of these, e.g., methyldicyclopentadiene. Other hydrocarbon polyenes such as those containing a single carbocyclic ring, e.g., divinylbenzene and divinylcyclohexane, or an acyclic polyene such as isoprene can also be used. The preferred hydrocarbon polyenes are dicyclopentadiene (DCPD) and norbornadiene. The reaction of the dichlorosilane and the hydrocarbon polyene is carried out in the presence of a hydrosilation catalyst. Hydrosilation catalysts include those compounds discussed below in relation to the preparation of organosilicon polymers and prepolymers. In this reaction one of the carbon-carbon double bonds of the hydrocarbon polyene reacts with the ≡SiH group of the dichlorosilane, and the remaining double bond is unreacted. The product of this hydrosilation reaction is RCl 2 SiR', where R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, which is derived from the hydrocarbon polyene. RCl 2 SiR' is then cyclized by one of three methods to produce the cyclic polysiloxanes of this invention: (1) direct hydrolysis, for example, in ether or methyl ethyl ketone, (2) reaction with a secondary or tertiary alcohol and (3) oxidation with a metal oxide. Method (1) is preferred for cyclizing RCl 2 SiR' compounds where R' is derived from dicyclopentadiene. Suitable tertiary alcohols for use in method (2) include, for example, 2-methylbutan-2-ol, 3-methylpentan-3-ol, 3-ethylpentan-3-ol and t-butyl alcohol. Suitable secondary alcohols include, for example, 2-propanol, 2-butanol, 2-pentanol, 3-pentanol and 3,3-dimethylbutan-2-ol. Tertiary alcohols are preferred. t-Butyl alcohol is most preferred. Metal oxides preferred for use in method (3) include, for example, ZnO, MgO and CuO. Zinc oxide is most preferred. Reaction with ZnO is preferred for RCl 2 SiR' compounds where R' is derived from norbornadiene, and for compounds where R is an alkoxy or aryloxy group. The preparation of the fully substituted cyclic polysiloxanes can be summarized as follows, using the pure cyclic trisiloxane as an example. where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, and R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation. Pure cyclic trisiloxane can be obtained by standard processing techniques. However, 10% to 46% of the cyclic tetrasiloxane having the formula: where R and R' are the same as above, is typically also present in the cyclic polysiloxane reaction product. The amount of the cyclic tetrasiloxane present depends upon the synthesis method, reaction conditions and solvent used and on the size of the groups R and R' in the molecule. For example, when R' is derived from dicyclopentadiene, a smaller percentage of the cyclic tetrasiloxane is present when RCl 2 SiR' is reacted with t-butyl alcohol than when RCl 2 SiR' is hydrolyzed in methyl ethyl ketone. When RCl 2 SiR' is reacted with ZnO, a smaller percentage of the cyclic tetrasiloxane is obtained when R' is derived from dicyclopentadiene than when R' is derived from norbornadiene. The mixture of the cyclic trisiloxane and the cyclic tetrasiloxane can also be used in preparing the polymers and prepolymers of this invention. Any cyclic polysiloxane or tetrahedral siloxysilane with two or more hydrogen atoms bound to silicon can be used as component (b) in the preparation of the organosilicon polymers or prepolymers. The cyclic polysiloxanes have the general formula: wherein R 2 is hydrogen, a saturated, substituted or unsubstituted alkyl or alkoxy group, a substituted or unsubstituted aryl or aryloxy group, n is an integer from 2 to 20, and R 2 is hydrogen on at least two of the silicon atoms in the molecule. Suitable cyclic polysiloxane compounds include those disclosed in U.S. Patent No. 4,900,779; 4,902,731; 5,013,809; 5,077,134; 5,008,360; 5,068,303; and 5,025,048. Examples of reactants of Formula (I) include, for example, trimethylcyclotrisiloxane, tetraoctylcyclo-tetrasiloxane, and hexamethylcyclotetrasiloxane; tetra- and pentamethylcyclotetrasiloxanes; tetra-, penta-, hexa- and heptamethycyclopentasiloxanes; tetra-, penta- and hexamethylcyclohexasiloxanes, tetraethylcyclotetrasiloxanes and tetraphenylcyclotetrasiloxanes. Preferred cyclic polysiloxanes are the methylhydrocyclosiloxanes, for example, 1,3,5,7-tetramethylcyclotetrasiloxane; 1,3,5,7,9-pentamethylcyclopentasiloxane and 1,3,5,6,9,11-hexamethylcyclohexasiloxane, or mixtures thereof. In most cases, a mixture of a number of these species is used, wherein n can vary widely. Reference to "methylhydrocyclosiloxanes" is intended to refer to such mixtures. The tetrahedral siloxysilanes are represented by the structural formula: wherein R 2 is as defined above and is hydrogen on at least two of the silicon atoms in the molecule. Examples of reactants of Formula (II) include, e.g., tetrakisdimethylsiloxysilane, tetrakisdiphenylsiloxysilane, and tetrakisdiethylsiloxysilane. Tetrakisdimethylsiloxysilane is the best known and preferred species in this group. The hydrocarbon polyenes that can be used as optional component (c) in preparing the polymers and prepolymers are hydrocarbon polyenes having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation. Preferably the polyenes are polycyclic polyenes where the double bonds are in the rings of the compounds. Suitable compounds include for example, cyclopentadiene oligomers (e.g., dicyclopentadiene, tricyclopentadiene and tetracyclopentadiene), norbornadiene dimer, bicycloheptadiene (i.e., norbornadiene) and its Diels-Alder oligomers with cyclopentadiene (e.g., dimethanohexahydronaphthalene), and substituted derivatives of any of these, e.g., methyldicyclopentadiene. Preferred are cyclopentadiene oligomers such as dicyclopentadiene and tricyclopentadiene, with dicyclopentadiene being most preferred. Two or more hydrocarbon polyenes can be used in combination. Other hydrocarbon compounds can also be used. For instance, according to one embodiment described in U.S. Patent No. 5,008,360, the hydrocarbon component comprises at least one low molecular weight (typically having a molecular weight less than 1,000, preferably less than 500) polyene having at least two nonaromatic carbon-carbon double bonds highly reactive in hydrosilation. The polyene can contain other less reactive (including unreactive) double-bonds, provided that those double bonds do not interfere with the reactivity of the highly reactive double bonds. Compounds having only two highly reactive double bonds are preferred. The carbon-carbon double bonds can be either in an alpha, beta or gamma position on a linear carbon moiety, next to two bridgehead positions in a strained polycyclic aliphatic ring structure, or in a cyclobutene ring. Examples include 5-vinyl-2-norbornene; o-, m- or p-diisopropenylbenzene; o-, m- or p-divinylbenzene, diallyl ether, diallylbenzene, dimethanohexahydronaphthalene and the symmetrical isomer of tricyclopentadiene. The reactions for forming the organosilicon polymers and prepolymers are described in U.S. Patent Nos. 4,900,779; 4,902,731; 5,013,809; 5,077,134; 5,008,360; 5,068,303; 5,025,048; and 4,877,820. When components (a) and (b), or (a), (b) and (c) are used to prepare the polymer or prepolymer, a mixture of all the components can be reacted in the presence of a catalyst. Alternatively, component (b), the silicon compound having at least two ≡SiH groups, and (c), the hydrocarbon polyene, are reacted in the presence of a catalyst to form an intermediate product, and the intermediate product is then reacted with (a), the fully substituted cyclic polysiloxane, in the presence of additional catalyst. Alternatively (a) the fully substituted cyclic polysiloxane and (b) the silicon compound having at least two ≡SiH groups, are reacted in the presence of a catalyst to form an intermediate product, and the intermediate product is then reacted with (c) the hydrocarbon polyene, in the presence of additional catalyst. The reactions for forming the polymers and prepolymers can be promoted thermally or by the addition of a hydrosilation catalyst or a free radical generator such as a peroxide or an azo compound. Hydrosilation catalysts include metal salts and complexes of Group VIII elements. The preferred hydrosilation catalysts contain platinum, e.g., bis(acetonitrile)platinum dichloride, bis(benzonitrile)platinum dichloride, platinum on carbon, platinum dichloride, platinum-divinyl complexes, cyclooctadieneplatinum dichloride, dicyclopentadieneplatinum dichloride and chloroplatinic acid. The platinum catalyst is present in an amount of 0.0005% to 0.05% by weight of platinum, based on the weight of the monomers, preferably 0.002% to 0.05%, and most preferably 0.005% to 0.01%. It is possible, by selection of reactants, reactant concentrations and reaction conditions, to prepare polymers exhibiting a broad range of properties and physical forms. Thus, it has been found possible to prepare tacky solids, elastomeric materials, and tough glassy polymers. Generally, the ratio of carbon-carbon double bonds in the fully substituted cyclic polysiloxane or mixtures thereof with the hydrocarbon polyene, to ≡SiH groups in the organosilicon compounds is in the range of 0.5:1 to 1.3:1, preferably 0.7:1 to 1.1:1, most preferably 0.95:1 to 1.05:1. The prepolymers are stable at room temperature for varying periods of time, and cure upon reheating to an appropriate temperature, e.g., 100° to 250°C. Frequently additional catalyst is added to the prepolymer prior to cure to further promote the reaction. When preparing the polymers and prepolymers, the reaction speed and its accompanying viscosity increase can be controlled by use of low levels of a cure rate retardant (complexing agent), such as N,N,N',N'-tetramethylethylenediamine, diethylenetriamine or phosphorus compounds, such as those described in "Phosphorus Based Catalyst Retardants for Silicon Carbon Resin Systems", Research Disclosure 326103 (June 1991). The cure rate retardants are also useful to maintain the storage stability and to control the viscosity profile of the prepolymer as described in European Patent Application 479,310 (Babcock et al.). Stabilizers (antioxidants) are useful to maintain storage stability and thermal oxidative stability. Suitable stabilizers include, for example, bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-(3,5-di-tert-butyl-4-hydroxybenzyl)butyl-propanedioate (available as TINUVIN™ 144 from Ciba-Geigy Corp., Hawthorne, NY, U.S.A.), or a combination of octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate (also known as octadecyl 3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate) available as NAUGARD™ 76 from Uniroyal Chemical Co., Middlebury, CT, U.S.A., and bis(1,2,2,6,6-pentamethyl-4-piperidinyl sebacate), available as TINUVIN™ 765 from Ciba-Geigy Corp. Stabilizers and their use are described in U.S. Patent Nos. 5,025,048 and 5,118,735. An elastomer can be added to improve the toughness of the organosilicon polymer-containing compositions prepared according to the present invention. Although any elastomer can be added to impart toughness, hydrocarbon elastomers are preferred for use in the present invention. Preferred are ethylene-propylene-ethylidenenorbornene polymers having a molecular weight of 5500 to 7000. Elastomers are generally used in an amount of 0.5 to 20 weight %, preferably 3 to 12 weight % of the total composition. Elastomers can be added to the monomers or to the prepolymer. Use of elastomers is described in U.S. Patent No. 5,147,958 and European Patent Application 482,404 (Barnum & Brady), as well as "Organosilicon Compositions containing Hydrocarbon Elastomers", Research Disclosure 33082 (October 1991). One or more flame retardants can also be added to the compositions prepared according to this invention. The flame retardant preferably comprises at least one member selected from the group consisting of phosphorus-containing compounds and halogen-containing compounds. Exemplary are ammonium polyphosphates, phosphazenes, phosphine oxides, phosphate esters, elemental red phosphorus, brominated alkyls, brominated diphenyl oxides, brominated polystyrenes, brominated bisphenol A's, and hexachlorocyclopentadiene derivatives. Use of flame retardants is described in published European Patent Application No. 556,844 (Babcock et al.). Fillers can also be added to the compositions prepared according to this invention. Typical fillers include, for example, carbon black, vermiculite, mica, wollastonite, calcium carbonate, sand, glass spheres, glass beads, ground glass, waste glass, fused silica, fumed silica, synthetic silica, glass fibers, and glass flakes. Other useful fillers include the fiber reinforcements that are described in U.S. Patent Nos. 4,900,779, 4,902,731, 5,008,360 and 5,068,303. The polymers and prepolymers prepared according to this invention have excellent electrical insulating properties and resistance to moisture. They are therefore well suited for electronic applications, e.g., composites, adhesives, encapsulants, potting compounds and coatings. They are especially useful in applications requiring high shear modulus, low coefficient of thermal expansion and moderate glass transition temperature, for example, in the manufacture of printed circuit boards and high performance composites. All parts and percentages in this specification are by weight unless otherwise noted. EXAMPLE 1 This example describes the preparation of a fully substituted cyclotrisiloxane in which cyclization occurs after hydrolysis of the R'-substituted dichlorosilane in methyl ethyl ketone. Dicyclopentadiene (DCPD) (200 g, 1.52 mol) and 2,332 µ l (2.06 µ l = 10 ppm/g resin, 30 ppm) of a platinum-divinyl complex (a vinyl-terminated polydimethylsiloxane/toluene solution supplied by Huls American), were added to a three-necked 500 ml round bottom flask equipped with a condenser and a dropping funnel. Dichloromethylsilane (177.4 g, 1.54 mol) was added dropwise through the dropping funnel at room temperature with a magnetic stirrer. An exothermic reaction (2°C increase) was observed. After addition, the temperature was raised to 45-50°C and this temperature was maintained for three hours. The reaction mixture was cooled to room temperature. Vacuum distillation of the mixture was carried out using a Kugelrohr apparatus. The product, methyl (2,3-dihydro-2-dicyclopentadienyl)-dichlorosilane (312.3 g, 82.8%), was collected between 80° and 100°C at a vacuum of 1 mm Hg. An aqueous solution of methyl ethyl ketone (MEK) (7 g water in 150 ml MEK) was placed in a three-necked flask equipped with a condenser and a dropping funnel. Methyl (2,3-dihydro-2-dicyclopentadienyl)-dichlorosilane (40 g, 0.16 mol) was added through the dropping funnel. After addition, the solution was refluxed for two hours. The residue was dissolved in ether and washed with saturated sodium bicarbonate solution (100 ml) and distilled water (150 ml x 4). The solution was dried over anhydrous magnesium sulfate. The solvent was then evaporated in vacuo, first by a Rotovap, then by a Kugelrohr distillation apparatus at 80°C under a vacuum of 1 mm Hg. A mixture of the fully substituted cyclic trisiloxane (1,3,5-tris(2,3-dihydro-2-dicyclopentadienyl)-1,3,5-trimethylcyclotrisiloxane) and the corresponding fully substituted cyclic tetrasiloxane was obtained at 96% yield (30.0 g). The product was a colorless viscous oil, which turned to a white solid on standing. The ratio of cyclic trisiloxane to cyclic tetrasiloxane was 54/46 mol %. Example 2 This example describes the preparation of a fully substituted cyclotrisiloxane in which cyclization occurs after hydrolysis of the R'-substituted dichlorosilane in aqueous ether. Methyl (2,3-dihydro-2-dicyclopentadienyl)-dichlorosilane (38.0 g, 0.15 mol), prepared as described in Example 1, was added through a dropping funnel to an aqueous solution of ether (8 ml of water in 150 ml of ether). After addition, the solution was refluxed for four hours. The solution was cooled to room temperature and washed with distilled water (100 ml), saturated sodium bicarbonate (100 ml), and distilled water (100 ml x 4) in sequence. The organic layer was dried over anhydrous magnesium sulfate. The solvent was evaporated in vacuo. The product was a colorless viscous oil, which turned to a white solid on standing. A mixture of fully substituted cyclic trisiloxane (1,3,5-trimethylcyclotrisiloxane) and the corresponding fully substituted cyclic tetrasiloxane was obtained at 95% yield (28.0 g). The ratio of cyclic trisiloxane to cyclic tetrasiloxane was 90/10 mol %. Example 3 This example describes the preparation of a fully substituted cyclotrisiloxane in which cyclization occurs after reaction of the R'-substituted dichlorosilane with t-butyl alcohol. A solution of 32.0 g (0.44 mol) of t-butyl alcohol in 120 ml of hexane was added to a three-necked flask equipped with a condenser and a dropping funnel. Methyl (2,3-dihydro-2-dicyclopentadienyl) dichlorosilane (50 g, 0.20 mol), prepared as described in Example 1, was added through the dropping funnel. The reaction temperature was controlled below 15°C by an external ice bath and by the rate of addition. The solution was washed with saturated sodium bicarbonate solution (100 ml) and distilled water (100 ml x 5) and then dried over anhydrous magnesium sulfate. The solvent was evaporated in vacuo using a rotoevaporator and a Kugelrohr distillation apparatus in sequence. A mixture of the fully substituted cyclic trisiloxane (1,3,5-tris(2,3-dihydro-2-dicyclopentadienyl)-1,3,5-trimethylcyclotrisiloxane) and the corresponding fully substituted cyclic tetrasiloxane was obtained at 75% yield (28.8 g). The product was a white solid. The ratio of cyclic trisiloxane to cyclic tetrasiloxane was 65/35 mol %. Example 4 This example describes the preparation of a fully substituted cyclotrisiloxane in which cyclization occurs after reaction of the R'-substituted dichlorosilane with ZnO in ethyl acetate. Bicyclo[2.2.1]heptenylmethyldichlorosilane was prepared by the method described in Example 1, using norbornadiene instead of dicyclopentadiene. Bicyclo[2.2.1]heptenylmethyldichlorosilane (30.0 g, 0.12 mole) was added dropwise to a mixture of 11.9 g (0.145 mole) of zinc oxide and 100 ml of ethyl acetate at room temperature under a nitrogen atmosphere with agitation. The mixture was heated to reflux for five hours. The mixture was cooled to room temperature and the white solid was filtered off through CELITE™ filter aid supplied by Manville Corp. The organic solution was washed with brine (1 x 100 ml), saturated sodium bicarbonate (1 x 100 mol), and brine (3 x 100 ml) respectively. The solution was then dried over anhydrous magnesium sulfate and the solvent was evaporated under vacuum. A mixture of the fully substituted cyclic trisiloxane (1,3,5-trimethyl-1,3,5-trikis[5-bicyclo(2.2.1)heptenyl]cyclotrisiloxane) and the corresponding fully substituted cyclic tetrasiloxane was obtained at 81% yield (18.5 g). The product was a viscous liquid, which turned to a white solid on standing. The ratio of cyclic trisiloxane to cyclic tetrasiloxane was 60/40 mol %. COMPARATIVE EXAMPLE 1 This example describes the preparation of a prepolymer and cured polymer from a polycyclic polyene and a methylhydrocyclosiloxane without a fully substituted cyclic polysiloxane. Dicyclopentadiene (11.0 g), 10.4 g of 1,3,5,7-tetramethylcyclotetrasiloxane (Huls American), and 0.15 ml of a platinum-divinyl complex (Huls American PCO72, a xylene solution containing 0.56% of Pt, 35 ppm) were added to a round bottom one-neck flask. Heating the mixture to 70°C resulted in an exothermic reaction and formation of an organosilicon prepolymer. To this prepolymer was added 0.33 ml of PCO72 (75 ppm) in portions, followed by 8.4 ml of a solution of diethylenetriamine cure rate retardant (DETA) (5% in toluene, 20 ppm). The solvent was evaporated under vacuum. The catalyzed prepolymer was then poured into a mold. The sample was cured at 170°C for one hour and postcured at 240°C for four hours. The cured sample was a colorless and hazy solid. The shear modulus G' of the polymer was 8.80 x 10 9 dyne/cm 2 and was determined by dynamic mechanical analysis using a Rheometrics mechanical spectrometer Model RMS-605. The coefficient of thermal expansion (CTE) of the polymer was 95.8 ppm/°C between 60° to 100°C and was determined by thermal mechanical analysis (TMA) using a DuPont TMA Analyzer Model 220 (see Table 1). EXAMPLE 5 This example describes the preparation of a prepolymer in which a polycyclic polyene was first reacted with a methylhydrocyclosiloxane in the presence of a catalyst and the reaction product was then reacted with a fully substituted cyclic polysiloxane in the presence of additional catalyst. Dicyclopentadiene (6.1 g), 10.95 g of 1,3,5,7-tetramethylcyclotetrasiloxane, and 0.12 ml of a platinum-divinyl complex (Huls American PCO75, a vinyl-terminated polydimethylsiloxane/toluene solution containing 0.56% of Pt, 35 ppm) were added to a round bottom one-necked flask. Heating the mixture to 70°C resulted in an exothermic reaction and formation of an organosilicon prepolymer. 1,3,5-Tris(2,3-dihydro-2-dicyclopentadienyl)-1,3,5-trimethylcyclotrisiloxane (17.4 g) in 20 ml of toluene was added to the prepolymer, followed by 0.65 ml of the platinum catalyst (total 110 ppm). The solvent was evaporated under vacuum and the catalyzed prepolymer was poured into a mold. The sample was cured at 170°C for one hour and postcured at 240°C for four hours. The cured sample was a colorless and hazy solid. The shear modulus of the polymer was 1.10 x 10 10 dyne/cm 2 by dynamic mechanical analysis. The CTE of the polymer was 91.6 ppm/°C between 60° to 100°C (TMA) (see Table 1). COMPARATIVE EXAMPLE 2 This example describes the preparation of a prepolymer and cured polymer from dicyclopentadiene and a methylhydrocyclosiloxane without the use of a fully substituted cyclic polysiloxane. Dicyclopentadiene (11.0 g), 10.0 g of 1,3,5,7-tetramethylcyclotetrasiloxane (Huls American), and 0.13 ml of a platinum-divinyl complex (Huls American PC072, a xylene solution containing 0.56% of Pt, 30 ppm) were added to a round bottom one-neck flask. Heating the mixture to 70°C resulted in an exothermic reaction and formation of an organosilicon prepolymer. To this prepolymer was added 0.30 ml of PC072 (70 ppm) in portions, followed by 8.4 ml of a solution of diethylenetriamine cure rate retardant (DETA) (5% in toluene, 20 ppm). The solvent was evaporated under vacuum and the catalyzed prepolymer was poured into a mold. The sample was cured at 170°C for one hour and postcured at 240°C for four hours. The cured sample was a colorless and hazy solid. The shear modulus G' of the polymer was 8.20 x 10 9 dyne/cm 2 by dynamic mechanical analysis. The coefficient of thermal expansion (CTE) of the polymer was 102 ppm/°C between 60°C to 100°C (TMA) (see Table 1). EXAMPLE 6 This example describes the preparation of a prepolymer and cured polymer in which all of the components were added at the same time. Dicyclopentadiene (40 g), 7.5 g of 1,3,5,7-tetramethylcyclotetrasiloxane, 11.6 g of 1,3,5-tris(2,3-dihydro-2-dicyclopentadienyl)-1,3,5-trimethylcyclotrisiloxane, and 0.14 ml of a platinum-divinyl complex (Huls American PCO75, a vinyl-terminated polydimethylsiloxane/ toluene solution containing 0.56% of Pt, 30 ppm) were added to a round bottom one-necked flask. Heating the mixture to 70°C resulted in an exothermic reaction and the formation of an organosilicon prepolymer. The same platinum catalyst (0.33 ml, 100 ppm) was added to the prepolymer. The solvent was evaporated under vacuum and the catalyzed prepolymer was poured into a mold. The sample was cured at 170°C for one hour and postcured at 240°C for four hours. The cured sample was a colorless and hazy solid. The shear modulus of the polymer was 1.11 x 10 10 dyne/cm 2 by dynamic mechanical analysis. The CTE of the polymer was 97.9 ppm/°C between 60°C to 100°C (TMA) (see Table 1). The data from Comparative Examples 1 and 2 and Examples 5 and 6 are summarized in the following table. The data indicate that the shear modulus G' increases and the coefficient of thermal expansion (CTE) decreases for cured polymers made from fully substituted cyclic polysiloxanes compared with polymers made without them. Example DCPD/D 3 (weight ratio) PCO75 (ppm) G' (x10 9 ) (dynes/cm 2 ) CTE, ppm (60-100°C) Comp. Ex. 1 1/0 110 8.80 95.8 Ex. 5 1/3 110 11.0 91.6 Comp. Ex. 2 1/0 100 8.2 102.0 Ex. 6 1/3 100 11.1 97.9

Claims: A cyclic siloxane characterized by the formula where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and n is 3, or a mixture of 3 and 4; with the exception of 1,3,5-trimethyl-1,3,5-tridicyclopentadienylcyclotrisiloxane. The cyclic siloxane of claim 1, further characterized in that R' is a hydrocarbon group containing one carbocyclic ring or a polycyclic hydrocarbon group. The cyclic siloxane of claim 2, further characterized in that R' is a polycyclic hydrocarbon group. The cyclic siloxane of claim 3, further characterized in that the polycyclic hydrocarbon group is derived from a polyene selected from the group consisting of cyclopentadiene oligomers, bicycloheptadiene and its Diels-Alder oligomers with cyclopentadiene, norbornadiene dimer and hexahydronaphthalene. The cyclic siloxane of claim 4, further characterized in that the polycyclic polyene is selected from the group consisting of dicyclopentadiene, tricyclopentadiene, tetracyclopentadiene, dimethanohexahydronaphthalene and methyldicyclopentadiene. The cyclic siloxane of any of the preceding claims, further characterized in that R is a 1-10 carbon alkyl group. The cyclic siloxane of claim 6, further characterized in that R is methyl and R' is a dicyclopentadienyl group. The cyclic siloxane of claim 6, further characterized in that R is methyl and R' is a 5-bicyclo[2.2.1]heptenylgroup. The cyclic siloxane of claims 1 to 5, further characterized in that R is a 6-10 carbon aryl radical. A process for preparing a cyclic polysiloxane, characterized by (1) reacting a dichlorosilane Cl 2 HSiR with a hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation in the presence of a hydrosilation catalyst, to produce RCl 2 SiR', where R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and then (2) cyclizing RCl 2 SiR' to produce a cyclic polysiloxane having the formula: where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and n is 3, or a mixture of 3 and 4; with the exception of 1,3,5-trimethyl-1,3,5-tridicyclopentadienylcyclotrisiloxane. The process of claim 10, further characterized in that RCl 2 SiR' is cyclized by reacting with a tertiary or secondary alcohol. The process of claim 11, further characterized in that the alcohol is a tertiary alcohol. The process of claim 12, further characterized in that the tertiary alcohol is t-butyl alcohol. The process of claim 12, further characterized in that R is a 1-10 carbon alkyl group and R' is a dicyclopentadienyl group. The process of claim 12, further characterized in that R is a 1-10 carbon alkyl group and R' is a 5-bicyclo[2.2.1]heptenyl group. The process of claim 10, further characterized in that RCl 2 SiR' is cyclized by reacting with a metal oxide. The process of claim 16, further characterized in that the metal oxide is selected from the group consisting of zinc oxide, magnesium oxide and copper oxide. The process of claim 17, further characterized in that the metal oxide is zinc oxide. The process of claim 18, further characterized in that R is an alkyl or alkoxy group. The process of claim 19, further characterized in that R is a 1-10 carbon alkyl group and R' is a 5-bicyclo[2.2.1]heptenylgroup. The process of claim 10, further characterized in that RCl 2 SiR' is cyclized by hydrolyzing. The process of claim 21, further characterized in that R is a 1-10 carbon alkyl group and R' is a dicyclopentadienyl group. The process of claim 10, further characterized in that R' is a hydrocarbon group containing one carbocyclic ring, or a polycyclic hydrocarbon group. The process of claim 23, further characterized in that R' is a polycyclic hydrocarbon group. The process of claim 24, further characterized in that the polycyclic hydrocarbon group is derived from a polycyclic polyene selected from the group consisting of cyclopentadiene oligomers, bicycloheptadiene and its Diels-Alder oligomers with cyclopentadiene, norbornadiene dimer, and hexahydronaphthalene. The process of claim 25, further characterized in that the polycyclic polyene is selected from the group consisting of dicyclopentadiene, tricyclopentadiene, tetracyclopentadiene, dimethanohexahydronaphthalene and methyldicyclopentadiene. The process of claim 10, further characterized in that R is a 1-10 carbon alkyl group. The process of claim 10, further characterized in that R is a 6-10 carbon aryl group. Use of a cyclic siloxane of the formula where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and n is 3, or a mixture of 3 and 4 to prepare an organosilicon crosslinked polymer or a crosslinkable organosilicon prepolymer, characterized by reacting (a) the above cyclic siloxane, and (b) at least one silicon compound having at least two ≡SiH groups selected from the group consisting of (1) cyclic polysiloxanes and (2) tetrahedral siloxysilanes, in the presence of a catalyst. The use of claim 29, further characterized in that the ratio of carbon-carbon double bonds in (a) to ≡SiH groups in (b) is 0.7:1 to 1:1. The use of claim 29, further characterized in that (c) at least one hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation, is additionally reacted. The use of claim 31, further characterized in that R in component (a) is a 1-10 carbon alkyl group, and R' is a polycyclic hydrocarbon group having at least one carbon-carbon double bond that is reactive in hydrosilation; (b) is a cyclic polysiloxane, and (c) is selected from the group consisting of dicyclopentadiene, tricyclopentadiene, tetracyclopentadiene, dimethanohexahydronaphthalene and methyldicyclopentadiene. The use of claim 32, further characterized in that R in component (a) is a methyl group, and R' is a dicyclopentadienyl group or a 5-bicyclo[2.2.1]heptenyl group; (b) is a cyclic polysiloxane selected from the group consisting of 1,3,5,7-tetramethylcyclotetrasiloxane; 1,3,5,7,9-pentamethyl-cyclopentasiloxane; 1,3,5,6,9,11-hexamethylcyclohexasiloxane and mixtures thereof, and (c) is dicyclopentadiene. The use of any of claims 31 to 33, further characterized in that the ratio of carbon-carbon double bonds in (a) and (c) to ≡SiH groups in (b) is 0.7:1 to 1.1:1. Use of a cyclic siloxane of the formula where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and n is 3, or a mixture of 3 and 4 to prepare a crosslinked organosilicon polymer or a crosslinkable organosilicon prepolymer characterized by (1) reacting at least one silicon compound having at least two ≡SiH groups selected from the group consisting of cyclic polysiloxanes and tetrahedral siloxysilanes, and at least one hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation in the presence of a catalyst to produce an intermediate reaction product, and then (2) reacting the intermediate reaction product with the above cyclic siloxane in the presence of additional catalyst. The use of claim 35, further characterized in that the silicon compound in step (1) is a cyclic polysiloxane, and the hydrocarbon polyene is selected from the group consisting of dicyclopentadiene, tricyclopentadiene, tetracyclopentadiene, dimethanohexahydronaphthalene and methyldicyclopentadiene; R in the cyclic polysiloxane of step (2) is a 1-10 carbon alkyl group and R' is a polycyclic hydrocarbon group having at least one carbon-carbon double bond that is reactive in hydrosilation. The use of claim 36, further characterized in that the silicon compound in step (1) is a cyclic polysiloxane selected from the group consisting of 1,3,5,7-tetramethylcyclo-tetrasiloxane; 1,3,5,7,9-pentamethylcyclopentasiloxane; 1,3,5,6,9,11-hexamethylcyclohexasiloxane and mixtures thereof, and the hydrocarbon polyene is dicyclopentadiene; R in the cyclic polysiloxane of step (2) is a methyl group and R' is a dicyclopentadienyl or a 5-bicyclo[2.2.1]heptenyl group. The use of claims 35 to 37, further characterized in that the ratio of carbon-carbon double bonds to ≡SiH groups is 0.7:1 to 1.1:1. Use of a cyclic siloxane of the formula where R is a saturated, substituted or unsubstituted alkyl or alkoxy group or a substituted or unsubstituted aryl or aryloxy group, R' is a substituted or unsubstituted hydrocarbon group having at least one nonaromatic carbon-carbon double bond that is reactive in hydrosilation, and n is 3, or a mixture of 3 and 4 for preparing a crosslinked organosilicon polymer or a crosslinkable organosilicon prepolymer characterized by (1) reacting the above cyclic siloxane with at least one silicon compound having at least two ≡SiH groups selected from the group consisting of cyclic polysiloxanes and tetrahedral siloxysilanes, in the presence of a catalyst to produce an intermediate reaction product, and then (2) reacting the intermediate reaction product with at least one hydrocarbon polyene having at least two nonaromatic carbon-carbon double bonds that are reactive in hydrosilation, in the presence of additional catalyst. The use of claim 39, further characterized in that R in the cyclic polysiloxane of step (1) is a 1-10 carbon alkyl group, and R' is a polycyclic hydrocarbon group having at least one carbon-carbon double bond that is reactive in hydrosilation; the silicon compound is a cyclic polysiloxane, and the hydrocarbon polyene is selected from the group consisting of dicyclopentadiene, tricyclopentadiene, tetracyclopentadiene, dimethanohexahydronaphthalene, and methyldicyclopentadiene. The use of claim 40, further characterized in that R in the cyclic polysiloxane of step (1) is a methyl group, and R' is a dicyclopentadienyl or a 5-bicyclo[2.2.1]heptenyl group; the silicon compound is a cyclic polysiloxane selected from the group consisting of 1,3,5,7-tetramethylcyclotetrasiloxane; 1,3,5,7,9-pentamethylcyclopentasiloxane; 1,3,5,6,9,11-hexamethylcyclohexasiloxane and mixtures thereof, and the hydrocarbon polyene is dicyclopentadiene. The use of any of claims 39 to 41, further characterized in that the ratio of carbon-carbon double bonds to ≡SiH groups is 0.7:1 to 1.1:1.

Inventors: LOO DE-KAI, LOO, DE-KAI
Applicants: NAT STARCH CHEM INVEST, NATIONAL STARCH AND CHEMICAL INVESTMENT HOLDING CORPORATION
Application year: 1994
Main classification: C07F7
IPC codes: H05K3, C08G77, C07F7