A pneumatic tire

Abstract: A pneumatic tire having carcass cords made of an organic fiber. The organic fiber is double-twisted and satisfies the following equations. n₂/n₁ > 1 √ D₂/D₁ < N₂/N₁ N₂/N₁ ≦ 8 N₂ < 0.68 N₁ = n₁ × (0.139 × D₁/ρ) 1/2 × 10⁻³ N₂ = n₂ × (0.139 × D₂/ρ) 1/2 × 10⁻³ where D₁ is the original denier, D₂ is the total of the original denier, N₁ is a ply-twisting coefficient, N₂ is a cable-twisting coefficient, n₁ is the ply-twisting number (turns/10 cm), n₂ is the cable-twisting number (turns/10 cm) and ρ is the specific gravity of the organic fiber.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pneumatic tire using a double-twisted organic fiber as a carcass cord, and having good tire side evenness, high tire side rigidity, high initial tensile rigidity, and reduced weight. 2. Background of the Invention In the past, when an organic resin fiber, such as a polyester fiber, was used as a carcass cord for a tire, only those having a twisting structure with the same ply-twisting number n 1 and cable-twisting number n 2 (i.e., a balanced cord), were selected in order to prevent deterioration in the wear strength of the cord. Usually, a cord having a cable-twisting coefficient N 2 of about 0.7 and a ply-twisting coefficient N 1 of about 0.5 was used, where both the cable-twisting and ply-twisting coefficients were fairly high (e.g., 0.5 ≤ N 1 and 0.7 ≤ N 2 ). For example, when a fiber having a twisting structure 1500D/2 (i.e., two 1500 denier filaments which have been twisted together) was used, the ply-twisting number was about 40 turns/10 cm and the cable-twisting number was about 40 turns/10 cm; and when a fiber having a twisting structure 1000D/2 was used, the ply-twisting number was about 50 turns/10 cm and the cable-twisting number was about 50 turns/10 cm. In order to prevent deterioration of the wear strength of the cord, a cord having a large twisting number and a ply-twisting number that is the same as its cable-twisting number has been used. However these are not the best properties of a tire carcass cord either for controlling the initial tensile rigidity of the cord, or for reducing the tire side unevenness (that is, increasing the unevenness index), or for heightening the rigidity of the tire side. Furthermore, the radius of the cord increases with a higher twisting number. This is disadvantageous for weight reduction because the gauge of the cord coating rubber is increased. As described above, for a balanced cord, that is, a cord having a ply-twisting number n 1 (turns/10 cm) that is the same as its cable-twisting number n 2 (turns/10 cm), it is difficult to satisfy both wear resistance and other properties, such as a good tire side evenness (i.e., a large unevenness index), high tire side rigidity, and reduced weight by reducing the radius of the cord. SUMMARY OF THE INVENTION In view of the above-described problems of the prior art, an object of the present invention is to provide a pneumatic tire having good tire side evenness (i.e., a large unevenness index), high tire side rigidity, high initial tensile rigidity and reduced weight, by using an unbalanced tire carcass cord having a cable-twisting number that is different from its ply-twisting number. The present inventor has found that the above objects are achieved by a pneumatic tire having carcass cords made of an organic fiber, wherein said organic fiber is double-twisted and the carcass cords satisfy the following equations: n 2 /n 1 > 1 D 2 /D 1 < N 2 /N 1 N 2 /N 1 ≤ 8 N 2 < 0.68 N 1 = n 1 × (0.139 × D 1 /ρ) 1/2 × 10 -3 N 2 = n 2 × (0.139 × D 2 /ρ) 1/2 × 10 -3 where: D 1 is the original denier; D 2 is the total of the original denier; N 1 is a ply-twisting coefficient; N 2 is a cable-twisting coefficient; n 1 is the ply-twisting number (turns/10 cm); n 2 is the cable-twisting number (turns/10 cm); and ρ is the specific gravity of the organic fiber. DETAILED DESCRIPTION OF THE INVENTION The present invention is described in greater detail below. A pneumatic tire of the present invention has a carcass ply. The structural components of a pneumatic tire for use in the present invention and a method for making the same are described, for example, in U.S. Patents 4,669,519 and 4,708,185. The carcass cord is made of a double-twisted organic fiber, that is, an organic fiber that is first twisted (ply-twisting) with a twisting coefficient N 1 which satisfies the following equations. Then, several of the ply-twisted fibers are gathered and twisted (cable-twisting) in a direction opposite the ply-twisting direction with a twisting coefficient N 2 which also satisfies the following equations. The equations which N 1 and N 2 satisfy are: n 2 /n 1 > 1 D 2 /D 1 < N 2 /N 1 N 2 /N 1 ≤ 8 N 2 < 0.68 where: D 1 is the original denier; D 2 is the total of the original denier; N 1 is a ply-twisting coefficient; N 2 is a cable-twisting coefficient; n 1 is the ply-twisting number (turns/10 cm); and n 2 is the cable-twisting number (turns/10 cm). Furthermore, N 1 , N 2 , D 1 , D 2 , n 1 , and n 2 also satisfy the following equations: N 1 = n 1 × (0.139 × D 1 /ρ) 1/2 × 10 -3 N 2 = n 2 × (0.139 × D 2 /ρ) 1/2 × 10 -3 where ρ is the specific gravity of the organic fiber (g/cm 3 ). N 1 is the ply-twisting coefficient which is the tangent of the angle between the axis along a straight fiber before twisting and the axis along a twisted fiber (Θ 1 ). N 2 is the cable-twisting coefficient which is the tangent of the angle between the axis along a ply-twisted fiber and the axis along a cable-twisted fiber (Θ 2 ). When N 2 is equal to or more than 0.68, the radius of the cord increases, the initial tensile rigidity of the cord decreases, and the heat shrinkage of the cord increases. As a result, tire side unevenness increases (i.e., a decrease in the unevenness index), tire side rigidity decreases, and it is difficult to reduce the tire weight. When N 2 /N 1 > 8, the radius of the cord also increases, the initial tensile rigidity of the cord decreases, and the heat shrinkage of the cord increases. Consequently, tire side unevenness increases, tire side rigidity decreases, and it is difficult to reduce tire weight. Preferably, 1.7 < N 2 /N 1 < 3.6, and a preferred range of the ratio "n 2 /n 1 " is 1.2 to 2.6. The term "original denier" means the sum of the weights of the individual fibers in a ply-twisted fiber before they are ply-twisted, and the term "the total of the original denier" means the sum of the original deniers of each ply-twisted fiber in a cord. The ply-twisting number, the cable-twisting number, the ply-twisting coefficient and the cable-twisting coefficient, are described, for example, in U.S. Patent 5,115,854. When the radius of a filament in a ply-twisted fiber is r (cm) and the pitch of twisting is l, n 1 = 10/l (turns/10 cm), and D 1 = πr 2 × 9000 × 10 2 × ρ . From the above definition, when the twisting angle is Θ 1 , N 1 = tanΘ 1 = 2πr/l . The equation N 1 = n 1 × (0.139 × D 1 /ρ) 1/2 × 10 -3 is derived by incorporating the fisrt two equations into the above definition. In a similar manner, the equation N 2 = n 2 × (0.139 × D 2 /ρ) 1/2 × 10 -3 is also obtained. Now, by substituting N 1 and N 2 of the equation D 2 /D 1 < N 2 /N 1 into the equations for N 1 and N 2 , the relationship n 2 /n 1 > 1 is obtained. The organic resin fiber for use in the present invention is not particularly limited. Examples of useful organic resin fibers include polyester fibers, polyamide fibers and rayon fibers. Specific examples of the organic resin fibers for use in this invention are described, for example, in U.S. Patent 4,669,519. The radius of a cord is chosen depending upon the specific tire application and is not particularly limited. Also, preferably, the initial tensile rigidity is at least 30 gf/denier (D), more preferably, at least 70 gf/D. In general, in the case of a conventionally twisted cord, in which the direction of the ply-twisting and cable-twisting are not the same, and n 2 and n 1 are the same, the axis along the ply-twisted fiber in the finished cord becomes parallel to the direction of the strand of the cable-twisting regardless of the direction of twisting. This is called Z-twisting or S-twisting as described in JIS L1017-1983. The cord of the present invention satisfies the equations n 2 /n 1 > 1, N 2 ≤ 8 × N 1 , and N 2 < 0.68. As a result, the finished double-twisted cord has some twisting in the direction of the cable-twisting which leads to a reduction in the spiral radius of the cable-twisting and a reduction in the gap among filaments. Consequently, the radius of the cord is reduced, and less rubber is needed to obtain the same treat gauge as a conventional cord, which makes the resulting tire lighter. A treat is a rubber sheet containing a plurality of fiber cords. The cord of the present invention has less gap among filaments, and a smaller spiral radius of the cable-twisting. Thus, when the cord is stretched, the effect of the high tensile rigidity of the constituent filaments is apparent. This leads to higher initial tensile rigidity of the cord. As a result, the unevenness index of the tire side increases, and tire side rigidity increases. The initial tensile rigidity (gf/D) is measured as described in JIS L1017-1983. The strength of the cords is measured as described in JIS L1017-1983. The wear resistance index appearing in the Examples below is defined as follows. The wear resistance index measurement is based on the G.Y. type tube wear resistance test described in JIS L1017-1983. Index = t/T where t is the number (turns) that a tube made of the treat of the present invention rotates before it breaks; and T is the number (turns) that a tube made of a conventional reference treat rotates before it breaks. The higher the index, the better the wear resistance. The unevenness index is measured as follows. Test tires having a normal internal pressure of about 1.80 kgf/cm 2 are prepared. Test tires can be prepared, for example, as described in U.S. Patent 5,147,477. The maximum width of the tires is measured at four different points for each tire, and the average is calculated. Then, the maximum width of the tires at the joint is measured. If there is more than one joint in one tire, the maximum width at all the joints is measured and the smallest value is taken as the minimum of the maximum width. The maximum width of the tires is described, for example, in U.S. Patents 4,513,802 and 4,669,519. The unevenness index is calculated as follows. Index = {(W 1 - W 2 )/(w 1 - w 2 )} × 100 where W 1 is the average of the maximum width (cm) of a conventional reference tire, W 2 is the minimum of the maximum width (cm) of a conventional reference tire at the joint, w 1 is the average of the maximum width (cm) of the tire of the present invention at four different places, and w 2 is the minimum of the maximum width (cm) of the tire of the present invention at the joint. Because the difference between the average and minimum of the maximum width of a conventional reference tire is given as the numerator, the index increases as the tire side unevenness of a tire under evaluation decreases. A joint is a place where the end of a treat overlaps with another end of a treat. A tire can contain more than one joint. The weight reduction index is measured as follows. Sample treats having the same coating rubber gauge on both sides of the cord, the same cord number per unit area, and the same size of the area are prepared and each sample is weighed. The weight reduction index is calculated as follows. Index = (W/w) × 100 where W is weight (g/m 2 ) of a conventional reference treat and w is the weight of the treat of a tire under evaluation. Because the weight of a conventional reference treat is given as the numerator, the index increases as the treat gauge decreases. EXAMPLES The present invention is further described in the following Examples, but the invention should not be construed as being limited thereto. (1) Examples 1 - 3, Comparative Examples 1 - 4 Tires having a carcass cord using a four-denier-per-filament, multi-filament polyethylene terephthalate fiber (i.e., 4dpf-PET) carcass cord were prepared in size 155/70R12. The tires thus prepared were evaluated with respect to initial tensile rigidity, strength of the cord, wear resistance, tire side unevenness and weight reduction as described above. The characteristics of the cord used in each Example and Comparative Example, and the test results are shown in Table 1. (2) Examples 4 - 6, Comparative Examples 5 - 8 Tires having a carcass cord using a 4dpf-PET carcass cord were prepared in size 185/70R14. The tires thus prepared were evaluated with respect to initial tensile rigidity, strength of the cord, wear resistance, tire side unevenness and weight reduction as described above. The characteristics of the cord used in each Example and Comparative Example, and the test results are shown in Table 2. (3) Example 7, Comparative Example 9 Tires having a carcass cord using a Nylon 66 carcass cord were prepared in size 155/70R12. The tires thus prepared were evaluated with respect to initial tensile rigidity, strength of the cord, wear resistance, tire side unevenness and weight reduction as described above. The characteristics of the cord used in each Example and Comparative Example, and the test results are shown in Table 3. (4) Examples 8-9, Comparative Example 10 Tires having a carcass cord using a Nylon 66 carcass cord or a rayon carcass cord were prepared in size 185/70R14. The tires thus prepared were evaluated with respect to initial tensile rigidity, strength of the cord, wear resistance, tire side unevenness and weight reduction as described above. The characteristics of the cord used in each Example and Comparative Example, and the test results are shown in Table 4. The unbalanced cord of the present invention has a ply-twisting number n 1 that is smaller than n 2 . As a result, the tire side unevenness is reduced, the tire side rigidity and initial tensile rigidity of the cord is increased, and the tire weight is reduced. As compared to a conventional balanced cord, the cost of the twisting step is reduced. This is because the total twisting number (n 1 + n 2 ) is reduced. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the scope thereof as defined in the appended claims.

Claims: A pneumatic tire having carcass cords made of an organic fiber, wherein said organic fiber is double-twisted and satisfies the following equations: n 2 /n 1 > 1 D 2 /D 1 < N 2 /N 1 N 2 /N 1 ≤ 8 N 2 < 0.68 N 1 = n 1 × (0.139 × D 1 /ρ) 1/2 × 10 -3 N 2 = n 2 × (0.139 × D 2 /ρ) 1/2 × 10 -3 where: D 1 is the original denier; D 2 is the total of the original denier; N 1 is a ply-twisting coefficient; N 2 is a cable-twisting coefficient; n 1 is the ply-twisting number (turns/10 cm); n 2 is the cable-twisting number (turns/10 cm); and ρ is the specific gravity of the organic fiber. The pneumatic tire of claim 1, wherein the fiber of the carcass cord is selected from the group consisting of polyester fibers, polyamide fibers and rayon fibers. A carcass cord comprising a double twisted organic fiber which satisfies the following equations: n 2 /n 1 > 1 D 2 /D 1 < N 2 /N 1 N 2 /N 1 ≤ 8 N < 0.68 N 1 = n 1 × (0.139 × D 1 /ρ) 1/2 × 10 -3 N 2 = n 2 × (0.139 × D 2 /ρ) 1/2 × 10 -3 where: D 1 is the original denier; D 2 is the total of the original denier; N 1 is a ply-twisting coefficient; N 2 is a cable-twisting coefficient; n 1 is the ply-twisting number (turns/10 cm); n 2 is the cable-twisting number (turns/10 cm); and ρ is the specific gravity of the organic fiber. The use of a carcass cord according to claim 3 in a pneumatic tire for good tire side evenness, high tire side rigidity, high initial tensile regidity and reduced weight.

Inventors: SAWADA HIROKI, SAWADA, HIROKI
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1994
Main classification: B60C9
IPC codes: B60C9