POROUS CERAMIC AND PROCESS FOR PRODUCING THE SAME

Abstract: A porous ceramic mainly comprising silicon carbide or nitride, having strength, heat resistance and thermal shock resistance superior to the conventional products, containing many micropores wherein the pore diameter is 1 µm or less and the porosity is 35% or above, and having a flexural strength of 100 MPa or above. The production process comprises mixing a silicon oligomer capable of yielding silicon carbide or nitride by firing with powdery silicon carbide, silicon nitride or other ceramic each having an average particle diameter of 1.0 µm or less, forming the resultant mixture, and sintering the formed mixture in a suitable atmosphere at 1,200 °C or above.

Description: The present invention relates to a ceramic porous body having a large number of fine pores and high strength, and a method of producing the same. Ceramic porous bodies are used in a wide range of applications, such as catalyst carriers, filters, and sensors, as well as in building materials, such as heat insulation material. Various materials for ceramic porous bodies are known including alumina, silicon carbide, aluminum silicate, silica, and cordierite, which are suitably selected for use according to the intended end use. Recently, however, in applications such as filters and catalyst carriers, conventional ceramic porous bodies are experiencing difficulty in meeting the requirements for strength and heat resistance because the environments in which they are used are tending to become increasingly harsh due to factors such as increased stress applied and higher working temperatures. For example, as an automotive exhaust gas cleaning catalyst carrier there has been put in practical use a honeycomb filter of cordierite which is produced by sintering a cordierite molding made by extrusion to a honeycomb configuration; but with such a catalyst carrier, further improvement is desired in its characteristics, such as strength, heat resistance and thermal shock resistance. Silicon carbide and silicon nitride are known as examples of ceramics having high strength and high heat resistance, but at present there are only available for limited use porous bodies of such ceramics which have relatively large pores or have lower strength. For example, according to what is stated in "Powder and Powder Metallurgy", Vol. 38, No. 3, pp. 62 - 63, porous bodies of high strength have been produced by sintering a composite of SiC powder and polysilastyrene, but they are of about 1 µ m in pore diameter, with a porosity of the order of 34%. Ceramic Engineering and Science Proceedings, Volume 10, parts 7-8, 1989, pp. 833-836 disclose porous silicon carbide or silicon nitride bodies produced by a pyrolysis process at temperatures lower than 1400°C. The present invention consists in a ceramic porous body comprising silicon carbide or silicon nitride as a principal component, said ceramic porous body having a mean pore diameter of not more than 1 µm and a porosity of not less than 35%, and having a flexural strength of not less than 100 MPa. There can thus be provided a ceramic porous body which has a high strength, high heat resistance and high thermal shock resistance and, in addition, contains a large number of fine pores. Such a ceramic porous body is produced by using a silicon oligomer which is capable of producing silicon carbide or silicon nitride when calcined, mixing the silicon oligomer with a silicon carbide powder or silicon nitride powder and/or other ceramic powder which has a mean particle diameter of not more than 1.0 µ m, molding the mixture into shape, then sintering the molding in a suitable atmosphere at temperatures of not less than 1500°C. Specifically, a method of producing a ceramic porous body composed principally of silicon carbide or silicon nitride comprises admixing a silicon carbide or silicon nitride powder having a mean particle diameter of not more than 1.0 µ m with 1 to 99 % by weight, in terms of silicon content, of a silicon oligomer containing carbon atoms, molding the mixture into shape, then sintering the molding in a non - oxidative atmosphere at temperatures of not less than 1500 °C., preferably 1500 to 1900 °C and at a pressure of at least 202.65 kPa (2 atm). Where silicon carbide powder is not used, a ceramic porous body composed principally of silicon carbide or silicon nitride may be produced by admixing a silicon oligomer containing carbon atoms with 1 to 40 % by weight, preferably 10 to 30 % by weight, of a ceramic powder, other than silicon carbide or silicon nitride, having a mean particle diameter of not more than 1.0 µ m, molding the mixture into shape, then sintering the molding in a non - oxidative atmosphere at temperatures of not less than 1500 °C., preferably 1500 to 1900 °C. Where silicon nitride powder is not used, a ceramic porous body composed principally of silicon nitride may be produced by admixing a silicon oligomer containing carbon atoms with 1 to 40 % by weight, preferably 10 to 30 % by weight, of a ceramic powder, other than silicon nitride, having a mean particle diameter of not more than 1.0 µ m, molding the mixture into shape, then sintering the molding in a nitrogen atmosphere or an inert atmosphere containing nitrogen at temperatures of not less than 1500°C., preferably 1500 to 1900 °C. A ceramic porous body in accordance with the present invention is composed principally of silicon carbide (SiC) or silicon nitride (Si 3 N 4 ), and in some case it may contain silicon carbonitride. Where so required, it may contain other ceramic components and some residue of a sintering aid, carbon, etc. Although SiC and Si 3 N 4 are materials having high strength and high heat resistance, hitherto there have been known only porous bodies of such material which are of the type having relatively large pores and low strength. In contrast, the porous body of the invention has a large number of fine open pores with a pore diameter of not more than 1 µ m, and has a large surface area. This, coupled with a high degree of porosity, i.e., not lower than 35 %, permits passage of fluid, such as gas, at a higher rate. Therefore, the porous body is able to function well in applications, such as filters and catalyst carriers. Further, the porous body has high flexural strength on the order of 100 MPa or more, which makes the porous body highly reliable for use as structural material. The ceramic porous body of the invention can be produced in several ways. Essentially, it may be produced by using a silicon oligomer which is capable of producing SiC or Si 3 N 4 when calcined, mixing the same with an SiC powder or Si 3 N 4 powder, and/or other ceramic powder which has a mean particle diameter of not more than 1.0 µ m, molding the mixture into shape, then sintering the molding in a suitable atmosphere at temperatures of not less than 1500°C in order to obtain a product of high strength. The sintering temperature is preferably 1500° to 1900°C. If the temperature is higher than 1900°C, there will result an excessively large pore diameter or a sintered body having lower strength. The term "silicon oligomer" refers to a low polymer of an organic silicon compound. In particular, silicon oligomers useful in the practice of the method of the invention which are capable of producing SiC or Si 3 N 4 are those in which the main chain or side chains do not contain other than carbon, hydrogen and silicon. For example, polycarbosilane, polysilazane, and polysilastyrene are preferred as such. Any polysiloxane in which the main chain or side chains contain oxygen is undesirable for use because no sufficient conversion to SiC or Si 3 N 4 can be effected. When silicon oligomer is calcined in an inert atmosphere of Ar or the like, there will be mainly produced SiC, while Si 3 N 4 is mainly produced when silicon oligomer is calcined in a nitrogen atmosphere. However, any SiC or Si 3 N 4 as produced from silicon oligomer alone has no sufficient strength and presents relatively large pores. Therefore, according to the method of the invention, such silicon oligomer is mixed with fine SiC powder or Si 3 N 4 powder, and/or other ceramic powder, whereby a porous body composed principally of SiC or Si 3 N 4 can be obtained which has a large number of fine pores with a pore diameter of not more than 1 µ m and a porosity of not less than 35 %, and which has a flexural strength of not less than 100 MPa. In order to produce a porous body having such fine pores and high strength, it is required that the ceramic powder to be mixed with the silicon oligomer should be of not more than 1.0 µ m in mean particle diameter. The method of the invention will be described in further detail for each principal component of such porous body. The method of producing a porous body composed principally of SiC, in essence, comprises mixing silicon oligomer and SiC powder together, and sintering a molding of the mixture in a non - oxidative atmosphere. The non-oxidative atmosphere may be of an inert gas, such as Ar, nitrogen gas, hydrogen gas, or a mixture gas thereof. It is noted, however, that where nitrogen gas is used, SiCN, Si 3 N 4 and the like may be produced in addition to SiC. In place of a portion of SiC powder, other ceramic powder may be added in an amount of not more than 40 % by weight, preferably 10 to 30 % by weight, based on the total powder weight. The term "other ceramic powder" refers to powder other than SiC, which may be a nitride, such as Si 3 N 4 , TiN, or AlN; an oxide, such as Al 2 O 3 , SiO 2 , or ZrO 2 ; or a carbide, such as TiC, WC, or ZrC. The method of producing a porous body composed principally of Si 3 N 4 , in essence, comprises mixing silicon oligomer and Si 3 N 4 powder together, and sintering a molding of the mixture in a nitrogen atmosphere or an inert atmosphere containing nitrogen. For the inert atmosphere, an inert gas, such as Ar, is used. It is noted, however, that since silicon oligomer contains carbon, SiCN, SiC or the like may be produced simultaneously with production of Si 3 N 4 . In place of a part of the Si 3 N 4 powder, other ceramic powder may be added in an amount of not more than 40 % by weight, preferably 10 to 30 % by weight, based on the total powder weight. The term "other ceramic powder" refers to powder other than Si 3 N 4 , which may be a nitride, such as AlN or TiN; an oxide, such as Al 2 O 3 , SiO 2 , or ZrO 2 ; or a carbide, such as SiC or TiC. In both of the above two methods, the proportion of silicon oligomer is 1 to 99 % by weight in terms of silicon content. If the proportion of silicon oligomer is less than 1 % by weight in terms of Si content, the porosity is rendered small. If the proportion is more than 99 % by weight, the strength of the porous body is extremely lowered. The silicon oligomer acts as a forming binder and also functions as a sintering aid. In the method of the invention, therefore, any conventional type of binder or sintering aid need not necessarily be used. Porous bodies of the invention may be produced without using Sic powder or Si 3 N 4 . In this case, the method of the invention comprises admixing a silicon oligomer containing carbon atoms with 1 to 40 % by weight of a ceramic powder other than SiC or Si 3 N 4 which has a mean particle diameter of not more than 1.0 µ m, molding the mixture into shape, then sintering the molding in a non - oxidative atmosphere where the porous body being produced is one composed principally of SiC, or in a nitrogen atmosphere or an inert atmosphere containing nitrogen where the porous body being produced is one composed principally of Si 3 N 4 , at temperatures of not less than 1500 °C., preferably 1500 to 1900 °C. Where this method is employed, the ceramic powder used is other than SiC powder or Si 3 N 4 powder. If the proportion of the ceramic powder is less than 1 % by weight relative to the total powder weight, the resulting porous body is of lower strength. If the proportion is more than 40 % by weight, the thermal shock resistance of the porous body will be low and, at same time, the porosity of the porous body will be small. Therefore, the proportion of the ceramic powder is within the range of 1 to 40 % by weight. According to the above described method of the invention, sintering can be effected at lower temperatures as compared with the prior art method in which silicon oligomer is not used. The resulting porous body involves less residue of silicon (Si) and/or carbon (C) and is of high purity despite the fact that it contains SiC or Si 3 N 4 as produced from the silicon oligomer. Therefore, the porous body has good flexural strength, high heat resistance, and high thermal shock resistance. The SiC or Si 3 N 4 produced from the silicon oligomer may be either crystalline or non-crystalline. In the method of the invention, the atmosphere during the sintering stage may be at least 2 atm. pressure, but it is preferable that the atmosphere be pressurized to 50 atmospheres or more so that sintering is accelerated while pores of the work are maintained as such, it being thus possible to obtain a porous body having higher strength characteristics. It is noted in this connection that while the pressure applied is desirably higher, it should be limited to 2000 atmospheres from the standpoint of manufacturing cost. In proportion as the Sic powder or Si 3 N 4 powder, and/or other ceramic powder to be added is made smaller in particle diameter, the ceramic porous body to be obtained can be rendered finer in pore diameter. For example, where a powder having a mean particle diameter of not more than 0.05 µ m is used, a sintered porous body having a pore diameter of not more than 0.01 µ m may be obtained. Therefore, it is very important to select a suitable particle size with respect to respective ceramic powders to be added. (Example 1) Using the silicon oligomers and ceramic powders as shown in Tables 1 and 2 were produced porous bodies composed principally of SiC and porous bodies composed principally of Si 3 N 4 , respectively. That is, silicon oligomers and ceramic powders were mixed in such combinations as shown in Tables 1 and 2, and the respective mixtures were each molded to a plate - like shape having a length of 30 mm, a width of 30 mm, and a thickness of 3 mm. Then, the respective moldings were sintered for one hour under the sintering conditions shown in Tables 1 and 2. In Tables 1 and 2, mixing proportions (wt. %) of silicon oligomers are values expressed in terms of Si content. SiC Porous Body Mixing Proportion (wt. %) Sintering Conditions Silicon oligomer Ceramic powder (mean particle size) Temp. (°C) Atmosphere (atm.) 1 Polysilastyrene 95 SiC (0.5µm) 5 1600 Ar (500atm) 2 Polysilastyrene 70 SiC (0.3µm) 30 1600 Ar (500atm) 3 Polycarbosilane 90 SiC (0.5µm) 10 1600 Ar (500atm) 4 Polysilazane 90 SiC (0.5µm) 10 1600 Ar (500atm) 5 Polysilastyrene 70 SiC (0.5µm) 30 1800 Ar (500atm) 6 Polysilastyrene 70 SiC (0.5µm) 30 1600 Ar (50atm) 7 Polysilastyrene 80 Al 2 O 3 (0.7µm) 20 1600 Ar (50atm) 8 Polysilastyrene 80 Si 3 N 4 (0.5µm) 20 1700 Ar (100atm) 9 Polysilastyrene 80 Si 3 N 4 (0.5µm) 20 1600 N 2 (500atm) 10 Polysilastyrene 70 SiC (0.5µm) 30 1600 Ar (500atm) 11* Polysilastyrene 30 SiC (0.5µm) 70 1250 Ar (1atm) 12 Polysilastyrene 20 SiC (0.5µm) 80 1800 Ar (2atm) 13 Polysilastyrene 5 SiC (0.5µm) 95 1600 Ar (500atm) 14 Polysilastyrene 100 - 1400 N 2 (2atm) 15 Polycarbosilane 50 Al 2 O 3 (0.7µm) 50 1800 Ar (2atm) 16 Polysilastyrene 0.1 SiC (0.5µm) 99.9 1600 Ar (500atm) 17 Polysilastyrene 99.9 SiC (0.5µm) 0.1 1600 Ar (500atm) 18 Polysilastyrene 80 SiC (0.5µm) 20 2000 Ar (500atm) Si 3 N 4 Porous Body Mixing Proportion (wt. %) Sintering Conditions Silicon oligomer Ceramic powder (mean particle size) Temp. (°C) Atmosphere (atm.) 19 Polysilastyrene 95 Si 3 N 4 (0.5µm) 5 1550 N 2 (500atm) 20 Polysilastyrene 70 Si 3 N 4 (0.3µm) 30 1550 N 2 (500atm) 21 Polycarbosilane 90 Si 3 N 4 (0.5µm) 10 1550 N 2 (500atm) 22 Polysilazane 90 Si 3 N 4 (0.5µm) 10 1550 N 2 (500atm) 23 Polysilastyrene 70 Si 3 N 4 (0.5µm) 30 1800 N 2 (500atm) 24 Polysilastyrene 70 Si 3 N 4 (0.5µm) 30 1600 N 2 (50atm) 25 Polysilastyrene 80 Al 2 O 3 (0.7µm) 20 1550 N 2 (50atm) 26 Polysilastyrene 80 Si 3 N 4 (0.5µm) 20 1700 N 2 (100atm) 27 Polysilastyrene 80 Si 3 N 4 (0.5µm) 20 1600 N 2 +Ar(100atm) 28 Polysilastyrene 70 SiC (0.5µm) 30 1600 N 2 (500atm) 29* Polysilastyrene 30 Si 3 N 4 (0.1µm) 70 1200 N 2 (1atm) 30 Polysilastyrene 20 Si 3 N 4 (0.5µm) 80 1800 N 2 +Ar (2atm) 31 Polysilastyrene 5 Si 3 N 4 (0.5µm) 95 1550 N 2 (500atm) 32 Polysilastyrene 100 - 1400 N 2 (2atm) 33 Polycarbosilane 50 Al 2 O 3 (0.7µm) 50 1800 N 2 (2atm) 34 Polysilastyrene 0.1 Si 3 N 4 (0.5µm) 99.9 1550 N 2 (500atm) 35 Polysilastyrene 99.9 Si 3 N 4 (0.5µm) 0.1 1600 N 2 (500atm) 36 Polysilastyrene 80 Si 3 N 4 (0.5µm) 20 2000 N 2 (500atm) For each porous body obtained, porosity was measured, and also pore diameter measurement was made by using a scanning electron microscope (SEM). With a sample of 4 mm x 2 mm x 30 mm cut from each porous body, measurement was made of three point bending strength over a span of 20 mm, The measurement results are shown in Tables 3 and 4. The porous bodies were all found as having good oxidation resistance in the atmosphere at 1000 °C. Then, each porous body was locally heated to ignition by a natural gas burner for observation as to whether cracking would occur or not, whereby the porous body was evaluated as to its thermal shock resistance. For comparison purposes, similar measurements were made with conventional Al 2 O 3 and SiC porous bodies, and Cerafoam which are commercially available. The measurement results are also shown in Tables 3 and 4. SiC Porous Body Porosity (%) Mean Pore Size (µm) Flexural Strength (MPa) Thermal Shock Resistance Crack found or not 1 45 <1 250 No 2 40 <0.5 400 No 3 48 <1 150 No 4 50 <0.5 170 No 5 45 <1 300 No 6 40 <0.5 200 No 7 40 <1 200 No 8 55 <0.5 300 No 9 58 <0.5 200 No 10 52 <0.5 350 No 11 55 <0.5 150 No 12 35 <1 250 No 13 40 <0.5 350 No 14 55 2-5 50 Yes 15 8 <0.5 400 Yes 16 10 <0.5 400 No 17 50 <0.5 80 Yes 18 40 1 150 No Commercial Al 2 O 3 45 2∼5 50 Yes Commercial SiC 30 2∼10 400 Yes Cerafoam 70 >10 5 Yes SiC Porous Body Porosity (%) Mean pore Size (µm) Flexural strength (MPa) Thermal Shock Resistance Crack found or not 19 48 <1 200 No 20 45 <0.5 350 No 21 49 <1 150 No 22 53 <0.5 170 No 23 49 <1 250 No 24 42 <0.5 200 No 25 44 <1 180 No 26 56 <0.5 220 No 27 58 <0.5 160 No 28 55 <0.5 300 No 29 58 <0.5 160 No 30 35 <1 250 No 31 42 <0.5 300 No 32 56 2∼5 50 Yes 33 8 <0.5 300 Yes 34 10 <0.5 350 No 35 50 <0.5 50 Yes 36 40 1 150 No Commercial Al 2 O 3 45 1∼5 50 Yes Commercial SiC 30 2∼10 400 Yes Cerafoam 70 >10 5 Yes (Example 2) Sample Nos. 2 and 19, SiC and Si 3 N 4 porous bodies, in Example 1 were subjected to penetration by diesel engine combustion gas at 1000 °C . As a result, it was found that capture ratio exceeded 90 % with respect to solid content of fine carbon particles and the like, and that there was no thermal damage occurrence. For comparison purposes, gas penetration tests were made with commercial porous bodies composed respectively of Al 2 O 3 , cordierite, and SiC. With all these porous bodies, capture ratio was not more than 50 % and, in addition, there occurred damages (cracks) due to heating. This tells that they can never withstand use conditions. From the foregoing data, it is apparent that the ceramic porous body of the present invention has good advantage over conventional ceramic porous bodies, not only in separation performance for filter service, but also in heat resistance and thermal shock resistance. Therefore, it is believed that the ceramic porous body is an industrially useful material. From the foregoing results of Examples 1 and 2, it can be seen that the ceramic porous body of the invention is a highly porous material with fine pores and high porosity and, in addition, has excellent heat resistance, thermal shock resistance and oxidation resistance. According to the invention, a ceramic porous body can be provided which is composed principally of silicon carbide or silicon nitride and has higher strength, higher heat resistance and higher thermal shock resistance than any conventional one, and which has large porosity with a large number of fine pores.

Claims: A ceramic porous body comprising silicon carbide or silicon nitride as a principal component, said ceramic porous body having a mean pore diameter of not more than 1 µm and a porosity of not less than 35%, and having a flexural strength of not less than 100 MPa. A ceramic porous body as claimed in claim 1, which contains 1 to 40% by weight of a ceramic component other than the principal component of silicon carbide or silicon nitride. A method of producing a ceramic porous body as claimed in claim 1 which comprises admixing a silicon carbide or silicon nitride powder having a mean particle diameter of not more than 1.0 µm with 1 to 99% by weight in terms of silicon content, of a silicon oligomer containing carbon atoms, molding the mixture into shape, then sintering the molding in a non-oxidative atmosphere at temperatures of not less than 1500°C and a pressure of at least 202.65 kPa (2 atm). A method as claimed in claim 3, wherein a ceramic powder other than silicon carbide or silicon nitride powder, which has a mean particle diameter of not more than 1.0 µm, is added to the silicon carbide powder in an amount of not more than 40% by weight relative to the total powder weight. A method as claimed in claim 3 or claim 4, wherein said non-oxidative atmosphere is a nitrogen atmosphere or an inert atmosphere containing nitrogen. A method of producing a ceramic porous body as claimed in claim 2, which comprises admixing a silicon oligomer containing carbon atoms with 1 to 40% by weight of a ceramic powder other than silicon carbide or silicon nitride, which has a mean particle diameter of not more than 1.0 µm, molding the mixture into shape, then sintering the molding in an non-oxidative atmosphere at temperatures of not less than 1500°C. A method as claimed in claim 6, wherein the non-oxidative atmosphere is a nitrogen atmosphere or an inert atmosphere containing nitrogen. A method as claimed in any one of claims 3 to 7, wherein the sintering atmosphere is pressurized to 50 atmospheres or more. A method as claimed in any one of claims 3 to 8 wherein the sintering temperature is 1500 to 1900°C. A method as claimed in any one of claims 3 to 9, wherein the silicon oligomer is polycarbosilane, polysilazane, or polysilastyrene.

Inventors: NIIHARA KOICHI, YAMAKAWA AKIRA, NIIHARA, KOICHI, YAMAKAWA, AKIRA
Applicants: NIIHARA KOICHI, SUMITOMO ELECTRIC INDUSTRIES, NIIHARA, KOICHI, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1994
Main classification: C04B38
IPC codes: C04B35, C04B38