Hydrothermal synthesis of octahedral molecular sieve

Abstract: A process of synthesizing synthetic manganese oxide hydrates having various structures including hollandite and todorokite structure by hydrothermal synthesis. The products have a high degree of crystallinity and thermal stability.

Description: This invention relates to the synthesis of octahedral molecular sieves, mainly manganese oxides, equivalent to the structures of the natural minerals, todorokite and hollandite. Hollandite (BaMn 8 O 16 ) , cryptomelane (KMn 8 O 16 ), manjiroite (NaMn 8 O 16 ), and coronadite (PbMn 8 O 16 ) are all naturally occurring manganese minerals with a 3-dimensional framework tunnel structure. The structure consists of MnO 6 octahedra which share edges to form double chains, and the octahedra of the double chains share corners with adjacent double chains to form a 2x2 tunnel structure. The size of these tunnels is 5.46 Å x 5.46 Å. Ba, K, Na and Pb ions are present in the tunnels and coordinated to the oxygens of the double chains. The identity of the tunnel cations determines the mineral species. The minerals are members of the hollandite-romanechite family. Zeolites and zeolite-like materials are well-known molecular sieves. These materials use tetrahedral coordinated species TO 4 , (T=Si, Al, P, B, Be, Ga, etc.,) as the basic structure unit. Through the secondary building units (SBU), a variety of frameworks with different pore structures are then built. Like tetrahedra, octahedra also can be used as the basic structural unit to form octahedral molecular sieves (OMS). Herein below, we will refer to the materials with a 2x2 tunnel structure as hollandites, and identify each member by the identity of the tunnel ions. Such minerals can be characterized by the general formula: A 2-y Mn 8 O 16 xH 2 O where A is the counter ion (alkali or alkaline earth metal or Pb +2 ), Mn represents Mn +4 and Mn +2 and x is 6 to 10 with y varying from 0.8 to 1.3. Because of their tunnel structure, the materials may be useful as shape selective catalysts and molecular sieves. K-hollandite and Ba-hollandite have reportedly been synthesized (as discussed by Parida et al, "Chemical Composition, Microstructure and other Characteristics of Some Synthetic MnO 2 of Various Crystalline Modifications", Electrochimica Acta , Vol. 26, pp. 435-43 (1981) and Strobel et al, "Thermal and Physical Properties of Hollandite-Type K 1.3 Mn 8 O 16 and (K,H 3 O) x Mn 8 O 16 ", J. Solid State Chemistry, Vol. 55, PP. 67-73 (1984). However, these syntheses are unreliable and considerable difficulties have been experienced by practitioners in this field. Villa et al discussed the synthesis of oxide systems containing Mn in combination with other elements in "Co-Mn-Ti-K OXIDE SYSTEMS" Applied Catalysis , Vol. 26, pp. 161-173 (1986). Torardi et al. discussed the synthesis of a hollandite-type molybdenum compound (K 2 Mo 8 O 16 ) by hydrothermal reaction of basic K 2 MoO 4 solutions with Mo metal in "Hydrothermal Synthesis of a new molybdenum hollandite," Inorganic Chemistry , Vol. 23, pp. 3281-84 (1984). The hollandites are representative of a family of hydrous manganese oxides with tunnel structures (also described as "framework hydrates") in which Mn can be present as Mn +4 and other oxidation states, the tunnels vary in size and configuration, and various mono- or divalent cations may be present in the tunnels. Such cations may serve to form and support the tunnels in some cases. Clearfield describes various hydrous manganese oxides with tunnel structures in "Role of Ion Exchange in Solid-State Chemistry," Chemical Reviews , Vol. 88, pp. 125-131 (1988). Pyrolusite or β-MnO 2 has tunnels only one MnO 6 octahedron square (1x1), or about 2.73 Å square, while in ramsdellite, MnO 2 , these octahedra form (2x1) tunnels, about 2.73 Å x 5.46 Å. Nsutite, γ-MnO 2 , is described as an intergrowth of pyrolusite and ramsdelite and also has (2x1) tunnels. Psilomelane, Ba 2 Mn 5 O 10 xH 2 O, and romanechite (with K +2 substituted for Ba +2 in the psilomelane formula) have (3x2) tunnels parallel to the cell b axes, about 5.46 Å x 8.19 Å. Todorokites, (Na,Ca,Mn) Mn 3 O 7 xH 2 O, have (3x3) tunnels, about 8.19 Å square, and monoclinic cells. Todorokites and other species are described by Turner et al. in "Todorokites: A New Family of Naturally Occurring Manganese Oxides," Science , May 29, 1981, pp. 1024 - 1026, in which it is noted that since todorokites are often found in deep-sea manganese nodules containing high concentrations of copper and nickel, "it seems probable that the smaller transition elements substitute for Mn +2 in the octahedral framework." The same article suggests a new partial nomenclature scheme for such manganese oxide structures - T(m,n), in which T donates a tunnel structure and the dimensions of the tunnels are indicated by (m,n). In this notation, the common dimensions responsible for intergrowth (m) is listed first, while (n) represents a variable dimension. D.C. Golden et al., discloses the synthesis of todorokite in SCIENCE 231.717 (1986). Herein below, we will refer to the (3X3) tunnel structure as OMS-1 and the (2X2) tunnel structure as OMS-2. Many of these tunnel or framework hydrates in addition to the (2x2) hollandites have potential for use in separations, absorbent materials or catalyst materials. Hence, reliable and systematic synthesis methods for their preparation are desired. A new hydrothermal synthesis has been discovered by which manganese oxide hydrates such as hollandites with high surface area (at least 300 m 2 /g) and good crystallinity (sharp X-ray diffraction patterns) can be synthesized. In accordance with the present invention a process is provided for the hydrothermal synthesis of manganese oxide hydrate comprising: (a) preparing a mixture of a manganous (Mn +2 ) salt and a permanganate salt; (b) aging said mixture; (c) rendering said mixture essentially chlorine-free; (d) ion exchanging said mixture with a magnesium salt; and (e) filtering, washing and autoclaving said exchanged material to form said product, with the proviso that when hollandite is produced it has a surface area of at least 300 m 2 /g. The reaction conditions such as the ratio of manganous ion to permanganate ion, temperature and pH can be varied to produce manganese oxide hydrates of various structures, including those known as pyrolusite, nsutite, romanechite, todorokite, and hollandite. Further in accordance with the invention, synthetic crystalline manganese oxide hydrates prepared in accordance with the claimed processes are provided, the products being similar in structure to various naturally occurring minerals, but offering greater purity and crystallinity. In addition to the reactants recited in the process above, optional templates selected from materials such as alkali or alkaline earth metal ions, tetraalkylammonium ions or organic polymer chains can be employed to form the products. In certain preferred embodiments, the product is a 2x2 tunnel structure described generally herein as a hollandite structure. BRIEF DESCRIPTION OF THE DRAWING The drawings provided for illustration are: Figs. 1a and 1b show the three-dimensional framework tunnel structures of hollandite (2x2) and todorokite (3x3), respectively; Figs 2A, 2B, 2C, 2D and 2E are XRD patterns of synthesized todorokite calcined at 100°C (A), 200°C (B), 300°C (C), 400°C (D) and 500°C (E); Fig. 3 is a TGA of synthesized todorokite; and Fig. 4 illustrates the temperature and pH effects of the synthesis of manganese oxide molecular sieves. According to the present invention, a soluble manganous salt and a permanganate are reacted under conditions of temperature, pressure and pH effective to produce the desired manganese oxide hydrates, with conditions varied to produce different structures of such minerals. The reaction mixture is heated in a closed system or vessel such as an autoclave so that a given temperature produces a predictable degree of autogenous pressure which is effective to complete the reaction in the desired time. In the present application, the term "autoclave" is used in a generic sense to indicate any closed reactant system providing a stable and predictable autogenous pressure for a given temperature. As to the reactants, in general any suitable soluble manganous salt, whether inorganic or organic, can be employed in the processes of the present invention. Suitable salts include for example, the sulfate, nitrate, perchlorate and salts of organic acids, such as acetates. The sulfate, nitrate and acetate salts are presently preferred because they have been used effectively in the examples. In general, the permanganates can be an alkali or alkaline earth metal salt, including the permanganates of sodium, potassium, cesium, magnesium, calcium and barium. Permanganates including the ammonium or tetraalkyl-ammonium salts can also be used. However, the counter ion or the permanganate ion in some cases is more than a vehicle for achieving solubility of the permanganate. The larger counter ions such as potassium and barium serve as templates for crystallization and remain in the tunnel structures of certain manganese oxide hydrates, particularly the hollandites; therefore, the counter ion for the permanganate can be selected to facilitate the selection, forming and stabilizing of a desired product, such as a hollandite, or to have a lesser effect (as with the smaller alkaline earth cations such as sodium and magnesium) to allow other preferred structures to form and/or to permit the template materials other than the counter ion to act on the reactant solution. The ionic radii of some alkali and alkaline earth metal cations which can be thus employed are listed below: Cation Li Na K Cs Mg Ca Ba r (Å) 0.68 0.98 1.33 1.89 0.65 0.99 1.35 The molar ratio of permanganate ion to manganous ion, [MnO 4 - ]/[Mn +2 ], which can be expressed as [Mn +7 ]/[Mn +2 ] for convenience, is one of the factors or parameters in determining the nature of the product, and can range broadly from 0.2 to 3.0, preferably from 0.25 to 0.5, and most preferably from 0.3 to 0.4. In preferred embodiments, this ratio can range from 0.3 to 0.4 for the production of todorokite, from 0.2 to 1.4 for the production of hollandites, from 1.75 to 2.2 for mixtures of hollandites and nsutites, and from 2.5 to 3 for nsutites. The pH of the reaction mixture and the reaction temperature are interrelated parameters which can be varied in conjunction with the ratio of [MnO 4 - ]/[Mn +2 ] and the nature of the template to influence the structure and the quality of the product. Figure 4 provides a plot of pH versus temperature in which the regions in which certain structures can be expected to form are indicated, based upon observed results under various conditions and the results which are expected for reactions under slight variations of such conditions. The conditions for certain examples herein are also plotted. In general, the pH should be less than 4.5, since above pH 5 amorphous materials rather than crystalline structures tend to form. Preferably, the pH is in the range of from 0 to 4, more preferably, from 0.5 to 2. A pH range from 1 to 3 is presently preferred for the production of hollandites. At high pH of at least 13, todorokite is formed. The reaction temperature can range broadly from 40° to 255°C, with the lower extreme of this temperature range tending to produce slower reactions. As can be seen in Figure 4, given a pH range which is effective to produce crystalline products, temperatures in the range from 40° to 70°C would tend to produce the nsutite structures which have generally low crystallinities but contain structures characterized by tunnels of dimension (1xn), where the basic unit dimension is a manganese oxide octahedron, and n can be an integer of 1 or 2. Again, given an appropriate pH, the process of the invention can be carried out to produce materials of a hollandite structure (2x2) at temperatures ranging from 70°C to 155°C. Preferably, for the production of hollandites, the temperature is in the range from 80° to 120°C and most preferably from 90° to 110°C, and, for the production of todorokites, the temperate may range from 130°C to 170°C. Given an appropriate pH range, the reaction can be carried out at temperature ranges of from about 155° to 255°C to produce pyrolusite (1x1) structures. In the process of synthesizing todorokite, the manganous salt may be selected from the group consisting of MnCl 2 , Mn(NO 3 ) 2 , MnSO 4 and Mn(CH 3 COO) 2 . The permanganate salt may be selected from the group consisting of Na(MnO 4 ), KMnO 4 , C 5 MnO 4 , Mg(MnO 4 ) 2 , Ca(MnO 4 ) 2 and Ba(MnO 4 ) 2 . The basic material according to the present invention may be selected from the group consisting of KOH, NaOH and tetraalkyl ammonium hydroxides. As for the magnesium salt used to ion exchange the filtered material, this salt may be selected from the group consisting of MgCl 2 , Mg(CH 3 COO) 2 and MgSO 4 , the preferred magnesium salt being MgCl 2 . According to the present process the ion exchanged material may be autoclaved at a temperature ranging from 100°C to 200°C for at least 10 hours or preferably at 130°C to 170°C for 2 to 5 days. The basic material is generally aged for at least 7 days. And, the product, todorokite, resulting from the present process is represented by the formula M m+ a Mn 2+ b Mn 4+ c O 12 nH 2 O wherein M m+ is a +1 or +2 metal ion, a = 0 - 2.0, b = 0 - 2.0, c = 4.0 - 6.0, and n = 4.47 to 4.55 Various organic templates can be employed for synthesizing structures with tunnels ranging from 1x1 to 3x3 by the processes of the present invention. A preferred group of organic templates is selected from tetraakylammonium salts, in which the alkyl groups can have from 1 to about 5 carbon atoms. The alkyl groups associated with the cation can be the same or different and can be normal or branched in structure. Cations including methyl, ethyl or propyl groups are presently preferred. The anion can be any suitable inorganic or organic (e.g. acetate) ion which will allow the required solubility and either remain in solution without interfering with the reaction or, optionally, form a precipitate with the cation employed in the permanganate salt. Exemplary anions are the halides, hydroxides, bisulfates, sulfates, perchlorates and the like. The materials have acid sites, including Lewis and Bronsted sites. Possible applications include acid catalyzed reactions such as isomerization and polymerization. Manganese oxide materials are well known oxidation catalysts and the methane activation experiments reported in co-pending U.S. Application Serial No. 08/092,103 suggest that coupling to (C 3 -C 5 ) hydrocarbons can be enhanced by the use of OMS-1. Adsorption of hydrocarbons as large as 6.9A by OMS-1 has also been demonstrated. Other applications in the area of adsorption include use in separations. Also useful as organic templates are polymer chains containing synthetic polymers such as those described as cationic polymers, quaternary ammonium polymers and ionene polymers by Daniels et al. in "Cationinic Polymers as Templates in Zeolite Crystallization," J. Am. Chem. Soc. 100 , pp. 3097-3100 (1978). A preferred polymer having the structure as shown below is synthesized by the reaction of 1,4-diazabicyclo [2.2.2] octane with the bromoalkanes Br(CH 2 ) n Br, where n may be 3, 4, 5, 6 or 14. x is preferably 2 to 6. Such cationic polymers and their use as templates for zeolite synthesis are further described by Davis et al. in "Synthesis of Gmelinite and ZSM-12 Zeolites with a Polymer Template," J. Chem. Soc., Chem. Commun. 1988, pp. 920-921. Although the two structures of OMS-1 and OMS-2 are similar, the syntheses are quite different. The synthesis of OMS-1 uses layered manganese oxides as precursors. OMS-2 and layered materials are prepared by the redox reaction of Mn +2 and MnO 4 - . The products are dependent on the reaction conditions: Temperature, pH of solution, ratio of MnO 4 - /Mn +2 , template, time of reaction. The purity of products is characterized by XRD, TEM, TGA, FTIR, and adsorption studies. The present synthesis has a greater thermal stability than that reported by D.C. Golden et al., in Science 231 ,717 (1986) which is thermally stable up to only 300°C. Natural todorokite is stable up to 500°C., but the purity of the natural material is questionable. The material might contain layer materials, such as birnessite and buserite, which are the precursors of todorokite and have similar XRD patterns as those of todorokite. The synthesized material based on the present process has a good crystallinity and thermal stability according to TGA and XRD results. Todorokite also can be synthesized under the following conditions: 1. The Mn(+2) salt can be any suitable soluble manganous salt, such as Mn(NO 3 ) 2 , MnSO 4 , and Mn(CH 3 COO) 2 . 2. The base material can be any soluble inorganic or organic base, such as KOH and tetraalkylammounium hydroxides. 3. The oxidizing agent can be permanganate, H 2 O 2 , and O 2 . The preferable oxidizing agent is a permanganate salt such as NaMnO 4 , KMnO4, CsMnO4, Mg(MnO 4 ) 2 , Ca(MnO 4 ) 2 , and Ba(MnO 4 ) 2 ,. 4. If permanganate was used, the molar ratio of MnO 4 /Mn(+2) is between .25 to .50, and the preferable ratio is 0.3 to 0.4. 5. The pH of the suspension is at least 13. 6. The suspension age can be at least 8 hrs at room temperature. The preferable aged time is at least 7 days. 7. The manganous Mg(+2) can be any suitable soluble salt, such as MgCl 2 , Mg(CH 3 COO) 2 , or MgSO 4 . 8. The autoclave temperature is between 100 to 200°C, and the preferable temperature is 130-170°C. 9. The autoclavation time is at least 10 hrs, or preferably 2 to 5 days. The following example is provided to illustrate the present invention. EXAMPLE I Synthesis of Todorokite 50 ml of 5.0 M NaOH solution was added to 40 ml of 0.50 M MnCl 2 solution with vigorously stirring to form Mn(OH) 2 sol at room temperature. Another 40 ml of 0.1 M Mg(MnO 4 ) 2 solution was added dropwisely to the sol with stirring. The final pH of the suspension was about 13.8. After the suspension was aged for 8 days at room temperature, the solid material was filtered and washed with water until no C1 was detected. The material was ion exchanged with 1L of 1.0 M MgCl 2 at room temperate for 10 hours. The exchanged produce was filtered and washed with water and then autoclaved at 155°C for 10 hours. The autoclaved product was filtered and washed with water, then dried at room temperature. XRD and TGA were used to study the crystallinity and thermal stability of the synthesized material. Figure 3 shows the XRD of the synthesized todorokite with different calcination temperatures. The peaks at 9.5 and 4.7 A are the characteristic reflections of (100) and (200) planes. The 9.5 A peak intensity decreases with the calcination temperature. At 500° calcination, the peak has a small intensity. The results are consistent with the natural todorokite. Figure 2 shows the TGA of the synthe-sized todorokite. Water is removed first before 400°C. The material is thermally stable up to 500°C. At higher temperatures, Mn 4+ is reduced with concomitant evolution of oxygen and structural transformation, like natural todorokite.

Claims: A process for the hydrothermal synthesis of manganese oxide hydrate comprising: (a) preparing a mixture of a manganous salt (Mn +2 ) and a permanganate salt; (b) aging said mixture; (c) rendering said material essentially chlorine-free; (d) ion exchanging said material with a magnesium salt; and (e) filtering, washing and autoclaving said exchanged material to form said product, with the proviso that when hollandite is produced it has a surface area of at least 300 m 2 /g. A process as claimed in Claim 1, wherein said manganous salt is selected from the group consisting of MnCl 2 , Mn(NO 3 ) 2 , MnSO 4 and Mn(CH 3 COO) 2 . A process as claimed in Claim 1 or Claim 2, wherein said permanganate salt is selected from the group consisting of Na(MnO 4 ), KMnO 4 , C 5 MnO 4 , Mg(MnO 4 ) 2 , Ca(MnO 4 ) 2 and Ba(MnO 4 ) 2 . A process as claimed in any one of Claims 1 to 3, wherein the molar ratio concentration of permanganate ion to manganous ion is in the range of from 0.2 to 3.0. A process as claimed in any one of Claims 1 to 4, wherein said filtered material is ion exchanged with a magnesium salt selected from MgCl 2 , Mg(CH 3 COO) 2 and MgSO 4 . A process as claimed in any one of Claims 1 to 5, wherein said ion exchanged material is autoclaved at a temperature of 40° to 255°C for at least 10 hours. A process as claimed in any one of Claims 1 to 6 for the synthesis of todorokite wherein the manganous salt and permanganate salt are reacted in a basic environment. A process as claimed in Claim 7 wherein the molar ratio concentration of permanganate ion to manganous ion is in the range of from 0.2 to 0.5. A process as claimed in Claim 7 or Claim 8 wherein the ion exchanged material is autoclaved at a temperature of from 100° to 200°C for from 2 to 5 days. A process as claimed in any one of Claims 7 to 9 wherein said product todorokite is represented by the formula M m+ a Mn 2+ b Mn 4+ c O 12 nH 2 O wherein M m+ is a +1 or +2 metal ion, a = 0 - 2.0, b = 0 - 2.0, c = 4.0 - 6.0, and n = 4.47 - 4.55

Inventors: O'YOUNG CHIN-LIN, SHEN YAN-FEI, SUIB STEVEN LAWRENCE, ZERGER RICHARD PAUL, O'YOUNG, CHIN-LIN, SHEN, YAN-FEI, SUIB, STEVEN LAWRENCE, ZERGER, RICHARD PAUL
Applicants: TEXACO DEVELOPMENT CORP, TEXACO DEVELOPMENT CORPORATION
Application year: 1994
Main classification: C01G45
IPC codes: C01G45, C01B37, C01B39, B01J20