Synthesis gas production employing particulate catalysts

Abstract: Hydrogen and carbon monoxide are produced from a low molecular weight hydrocarbon by contact thereof, at high temperature in the presence of oxygen, or steam and oxygen, with a fluidized bed comprising particulate, essentially nonleachable barium hexaluminate in admixture with a particulate catalyst containing a metal, e.g. nickel, catalytic for synthesis gas production.

Description: This invention relates to a process for the production of hydrogen and carbon monoxide from hydrocarbons in high temperature reactions utilizing fluidized beds of admixtures of synthesis gas generation catalysts and heat transfer solids. Particulate refractory inorganic oxide solids, e.g. alumina, have been employed for many years as catalyst supports, or carriers, in natural or synthetic form. For example, synthesis gas, or syn gas (hydrogen and carbon monoxide) is produced from low molecular weight hydrocarbons, primarily methane, by contact with a bed of fluidized catalyst, e.g. nickel on an alumina support, in the presence of steam (steam reforming process), or oxygen (partial oxidation process), or both steam and oxygen, at high temperature. Suitably, particulate refractory inorganic oxide solids, notably alpha alumina solids, are admixed with the catalyst of the fluidized bed as heat transfer solids to control the temperature of reaction. Processes wherein low molecular weight hydrocarbons are converted to syn gas within the presence of both steam and oxygen offer particular advantages in that the syn gas can be better controlled to provide hydrogen:carbon monoxide ratios particularly suitable for conducting Fischer-Tropsch reactions; i.e. about 2:1. Fluidized bed processes offer particular advantages in that they provide superior heat, and mass transfer characteristics as contrasted with fixed bed processes. They permit substantially isothermal reactor conditions in conducting exothermic and endothermic reactions, provided that the fluidized characteristics of the bed can be maintained throughout the operation. To maintain the required fluidization characteristics, it is essential that the particulate bed solids have the capacity to resist melting and agglomeration at the high temperatures required for syn gas operations. Sintering and agglomeration of the solids reduce fluidization quality, produce large gas bubbles, and decrease mass transfer. Moreover, the particulate bed solids must mechanically withstand the stress and strain of process operations since the amount of mechanical fracturing and attrition of the particles that can be tolerated is severely limited. Process economics often militates against the use of devices which prevent the escape of any fines from the process, and generally, with the devices that are used, some fines are lost from the reactor. In a fluidized bed operation a gas, or gases, must be injected upwardly into the bed at velocity sufficient to overcome the free fall velocities of the individual solid particles, expand the bed, and produce some bubble formation. Inevitably, as fluidization occurs, some of the solid particles are swept from the bed by the ascending gas, or gases. Whereas cyclone separators are widely used, and can be used to return major concentrations of the solid particles to the bed, no cyclone separator, or system of cyclone separators can be operated with one hundred percent efficiency; and, inevitably, a significant amount of the particulate solids may escape from the process. Where the particulate solids are toxic, however, advantageous their use in the fluidized bed operation, the threat of escape of the solids to the environment makes it necessary to use special handling facilities to prevent the escape of the toxic solids. Various inorganic metal oxides have been used as carriers, or supports, for catalytic metals in the production of catalysts; one of the most widely commercially used of which is alumina because of its good mechanical strength, heat resistance and chemical stability. Barium has also been disclosed in the literature as a carrier component, e.g. as exemplified by U.S. 4,988,661 which issued on January 29, 1991 to Arai et al. This patent discloses a steam reforming catalyst, the carrier component of which consists essentially of aluminum oxide, A1 2 0 3 , and a metal oxide expressed as MeO comprising about 3-35 moles of metal oxide, MeO, to 100 moles of aluminum oxide, Al 2 0 3 in the carrier, Me being at least one metal selected from the group consisting of calcium, strontium and barium. The supported catalytically active metals are at least one of nickel, cobalt or platinum group metals in concentration ranging from 3 to 50 parts by weight per 100 parts by weight of the carrier. In forming the carrier, aluminum oxide and/or aluminum hydroxide and a Me compound (wherein, e.g., Me is barium, and the compound is barium carbonate) in an A1 2 O 3 :MeO mole ratio of 100:(3-35) are mixed together, and calcined to form a mixture of complex oxides, or mixed oxides phases, including largely MeO·6A1 2 O 3 , e.g. BaO·6A1 2 O 3 , with other aluminates, e.g. BaO· A1 2 O 3 many of which are water soluble or leachable. Albeit carriers constituted of mixtures of complex barium oxides may be useful as steam reforming catalysts in conventional fixed bed reactors wherein the catalyst is physically constrained in the reaction zone, water soluble forms of barium are not useful in fluidized bed operations. This is because such forms of barium are toxic, and airborne particles of these materials would inevitably find their way into the environment. In Chemistry Letters, pp 231-234, 1991 of The Chemical Society of Japan there is disclosure of steam reforming methane to carbon monoxide and hydrogen in a conventional flow system. A nickel on barium hexaaluminate catalyst may be employed and the barium hexaaluminate support is reported to be effective in suppressing sintering of Ni particles during the steam reforming reaction. In EP-A-335668, synthesis gas is produced from methane plus steam and oxygen, employing a fluid bed reaction zone. The catalyst employed is nickel on an alumina base having defined particle density, thereby improving catalyst attrition-resistance. The present invention relates to a process for the production of hydrogen and carbon monoxide from a low molecular weight hydrocarbon by contact thereof, at high temperature in the presence of oxygen, or steam and oxygen, with a fluidized bed comprising (i) a catalyst comprised of a particulate barium hexaaluminate (BaO·6Al 2 O 3 ) solid composited with a metal, or metals, component catalytic for the production of hydrogen and carbon monoxide from low molecular weight hydrocarbons when contacted with a fluidized bed of the catalyst at high temperature and (ii) a particulate barium hexaluminate (BaO·6Al 2 O 3 ) heat transfer solid. The particulate catalyst characterized in (i) is comprised of barium hexaaluminate composited with a metal, or metals, suitably nickel, platinum or ruthenium catalytic for the production of hydrogen and carbon monoxide from low molecular weight hydrocarbons contacted with a fluidized bed of the catalyst at high temperature hydrothermal conditions. The particulate catalyst characterized in (i), and the barium hexaaluminate heat transfer solids characterized in (ii), respectively, are preferably of average particle diameter ranging from 30 microns to 150 microns, preferably from 60 microns to 90 microns in diameter. The barium component of the barium hexaaluminate carrier portion of the catalyst and the particulate barium hexaaluminate heat transfer solid constituting a part of the bed, is essentially non-leachable with water and free of water leachable forms of barium. In its preferred form the carrier component or catalyst, and heat transfer component will contain a maximum of 100 milligrams of barium per liter of leachant, and more preferably a maximum of 50 milligrams of barium per liter of leachant when tested in accordance with the Environmental Protection Agency's: Test Methods For Evaluating Solid Waste, SW-846, with revisions given in the Federal Register Vol. 55, No. 126, dated June 29, 1990, with Barium Method 7080, dated July 1982 in the Toxicity Characteristic Leaching Procedure, Method No. 1311 described in the Federal Register Vol. 55, No. 126, Appendix II. A 100 gram specimen of the carrier, catalyst, or heat transfer solid when tested in accordance with this procedure is leached with two liters of the leaching solution, which will provide a leachant which will preferably contain from 0 to 100 milligrams per liter of barium, and more preferably from 0 to 50 milligrams per liter of barium. This is equivalent to leaching from 0 to 0.2 wt% barium, and preferably from 0 to 0.1 wt% barium, from the specimen. The particulate barium hexaaluminate carrier component of the catalyst and the particulate barium hexaaluminate heat transfer solids are typically prepared by mixing aluminum oxide, or aluminum hydroxide, or both, and a barium compound, suitably barium carbonate, barium nitrate, barium acetate, barium nitrite, barium oxide or the like, in an Al 2 O 3 :BaO mole ratio of 100:(1-16), and then calcining the mixture at temperatures ranging from 1200°C to 1700°C, and higher, preferably from 1400°C to 1600°C, for a period sufficient to convert essentially the entire amount of the mixture to barium aluminate phases, and the barium aluminate phases that are formed to essentially barium hexaaluminate. At these temperatures the barium aluminate phases that are produced are generally converted to essentially barium hexaaluminate, an essentially non-leachable form of barium, in from 0.5 to 16 hours, and more often from 1 hour to 4 hours. The catalyst, where the barium hexaaluminate is to be used to form a catalyst, is composited with a metal, or metals, catalytic for the conversion of low molecular weight hydrocarbons to hydrogen and carbon monoxide when contacted with a fluidized bed of the catalyst at high temperature hydrothermal conditions, e.g. nickel, platinum, ruthenium and the like. Or, the particulate barium hexaaluminate can be admixed with this, or other catalysts similarly useful for syn gas production, e.g. a nickel-on-alumina catalyst, and employed to great advantage as a heat transfer solid. An admixture of from 10 percent to 99.9 percent, preferably from 80 percent to 99.5 percent, of said particulate barium hexaaluminate solid, and from 0.1 percent to 90 percent, preferably from 0.5 percent to 20 percent, of the catalyst, based on the total weight of the admixture (dry basis), can be fluidized at temperatures ranging to 1430°C particularly at temperatures ranging between 870°C and 1090°C, and contacted with a low molecular weight hydrocarbon, e.g. C 1 -C 4 alkanes, predominantly methane, in the presence of oxygen (air), or both steam and oxygen (air), to produce syn gas without significant sintering of the particulate barium hexaaluminate heat transfer solids or catalyst components of the admixture. Likewise, there is no significant disintegration of either the heat transfer or catalyst components of the admixture to fines, or degradation of the particles of the admixture to produce agglomerates. The barium hexaaluminate particles, in either its catalyst form or heat transfer solids form, are highly resistant to sintering, attrition and agglomeration per se, and in its heat transfer solids form, when admixed with a catalyst the support component of which is not barium hexaaluminate, imparts high resistance to sintering and agglomeration of the catalyst, particularly at the severe high temperature hydrothermal conditions common to fluid bed syn gas operations. In its most preferred form, the catalyst component of the fluidized mixture, contains generally from 1 percent to 20 percent nickel, preferably from 5 percent to 10 percent nickel, composited with a barium hexaaluminate support, or carrier, suitably by impregnation or coprecipitation methods. The mean average diameter of the catalyst particles ranges from 30 microns to 150 microns, preferably from 60 microns to 90 microns; particles of size distribution which can be per se readily fluidized with the heat transfer barium hexaluminate solids particles, and contacted, e.g. with a light hydrocarbon feed, C 1 -C 4 alkanes, predominantly methane and an oxygen-containing gas (air), or methane and both steam and oxygen, at elevated temperature sufficient to convert the hydrocarbon feed to syn gas without significant degradation of the particles of the bed to fines, and without sintering, or catalyst agglomeration. This invention will be better understood via the following illustrative examples, which demonstrate specific and preferred embodiments. EXAMPLES A series of runs were made with a commercially obtained barium aluminate having a nominal stoichiometry BaO·6Al 2 O 3 , and mesh size ranging between about 45 microns and 106 microns. Specimens of the material were investigated after calcination at temperatures ranging from 1300°C to 1600°C, as indicated in the first column of the Table. Each portion of the BaO·6Al 2 O 3 tested was heated at the temperature given for a period of about 3 hours, and thereafter tested by leaching a 5 gram sample with distilled water in a Soxhlet extractor for 24 hours; the extracted liquid was acidified with HCl to a pH of about 0.3 and then analyzed on a direct coupled plasma (DCP) emission spectrometer to determine the weight percent of leachable barium. Reference is made to the second column of the Table. In addition, each of the heated specimens was tested to determine its agglomeration characteristics, and its ability to resist attrition as described in the third and fourth columns of the Table, respectively. Thus, in one series of tests specimens of the heated barium hexaaluminate solids were subjected to agglomeration tests at 1650°C. Each of the specimens, weighing about 8 to 10 grams, was placed in a Coor's alumina boat, put into a high temperature Lindbergh furnace heated from room temperatures to 1650°C over a period of about 5 hours, and then held at this temperature for three hours to induce thermal agglomeration. Each of the specimens was then cooled over a period of about 6 to 12 hours to about 100°C, removed from the furnace, and then transferred to a sonic sieve operated at constant power. Measurement by weighing the fractions collected on a 150 mesh size screen was then made to determine the conversion of the 45 to 106 micron particles to fused agglomerates greater than 106 microns in size. Specimens were subjected to treatment in a jet attritor to determine the Davison Attrition Index, D.I., of the particles; a measure of attrition resistance of a particle which has been found to correlate well with the attrition, and production of fines which occurs in a large fluidized bed syn gas generation pilot plant. The Davison Index, D.I., is an attrition index method based on that developed by Davison Chemical Division of W.R. Grace & Company. The method uses a jet cup attrition technique that reports as the D.I. the wt% of <20 µm fines produced in a controlled attrition test. The D.I. test apparatus consists of two main vessels, the attrition vessel and the elutriation vessel. The attrition and elutriation vessels have diameters 22.86 cm of (9 in.) and 11.43 cm (4.5 in.), respectively. Each vessel is 60.96 cm (24 in.) high and has a cone shaped bottom that slopes about 15° from vertical. The jet cup attritor which holds the sample for attrition attaches to the bottom of the attrition vessel and is 2.62 cm (1.03 in.) I.D. by 5.08 cm (2 in.) deep. A 0.16 cm (0.0625 in.) diameter hole forms the jet that enters the cup's wall horizontally and is tangent to the inside wall and bottom of the cup. A sample of 6 ± 0.3 g is attrited for 20 minutes with N 2 (35% relative humidity) at a flow rate of about 21 Liters/minute, L/min (this flow rate is fine-tuned to give a D.I. of 27 ± 2 for a standard CZB-1 Davison catalyst). Fines (wt 1) escaping the attrition vessel are collected in an extraction thimble. After the attrition the sample is transferred to the elutriation unit to separate the remainder of the <20 µm fines from the sample. The sample is placed in a cup with similar dimensions to the jet cup but with a sintered metal distributor at the bottom to uniformly fluidize the sample in the elutriator. This cup with the attrited sample is connected to the bottom of the elutriator, and the sample is elutriated for 20 min with N 2 (35% relative humidity) at 9 L/min. The elutriation removes the <20 µm fines from the sample to give a remaining coarse fraction (wt 3). The elutriated fines (wt 2) are collected in an extraction thimble connected to the exit of the elutriation vessel. In a separate measurement, the wt% of <20 µm fines (% Pre Att) is determined in a fresh sample. The D.I. which represents the wt% of <20 µm fines formed by the attrition is calculated given by the expression DI = [(wt 1) + (wt 2)] [(wt 1) + (wt 2) + (wt 3)] x 100 - (% Pre Att) 100 - (% Pre Att) x 100. Properties of Barium Aluminates Precalcination T (°C) Leachable Ba (Wt %) Agglomeration (Wt % + 106 µm) Attrition DI (Wt %) 1300 2.5 0.1 6.9 1400 0.13 0.1 8.4 1550 0.031 0.1 4.9 1600 0.026 0.5 5.7 These data show that the amount of leachable barium of the commercially obtained barium hexaaluminate specimen could be greatly reduced with increased calcination temperature to less than 0.1 wt% per 100 grams of barium hexaaluminate. The data show that the agglomeration resistance showed little dependence on calcination severity, and that the agglomeration resistance of the material is acceptable in all cases. The attrition resistance overall was improved, at least slightly, with high temperature calcination. Thus, in the production of syn gas in fluidized bed operations the strength of the particles are particularly important. Fines will be entrained, and removed from the bed regardless of the presence of cyclones used for fines recovery. This represents waste even where there is no toxicity problem, and leads to fouling of downstream equipment, e.g. heat exchangers. D.I. indexes greater than 15 are unacceptable, and preferably the D.I. index should be no greater than about 6. The barium solubility is thus lowered, by heating, to a value which renders a barium hexaaluminate without significant water solubility; a form providing, by virtue of this and other of its characteristics, a material suitable as the carrier component of a catalyst, or heat transfer solid in syn gas fluidized bed operations.

Claims: A process for the production of hydrogen and carbon monoxide from a low molecular weight hydrocarbon, comprising contacting the hydrocarbon in the presence of oxygen or oxygen and steam with a fluidized bed of catalyst at high temperature, wherein the fluidized bed is comprised of (i) a catalyst which is a particulate, nonleachable, barium hexaaluminate solid of fluidizable particle diameter composited with a metal, or metals, component catalytic for the said production of hydrogen and carbon monoxide and (ii) a heat transfer solid which is a said particulate barium hexaaluminate without said metal(s) component. The process of claim 1, wherein the average particle size diameter of the catalyst and the heat transfer solid ranges from 30 microns to 150 microns. The process of claim 2, wherein the average particle size diameter of the catalyst and the heat transfer solid ranges from 60 microns to 90 microns. The process of any preceding claim, wherein the metal, or metals, component of the catalyst is selected from nickel, platinum or ruthenium. The process of claim 4, wherein the metal is nickel. The process of claim 4, wherein the nickel is present in concentration ranging from 1 percent to 20 percent, based on the weight of the catalyst. The process of claim 6, wherein the nickel is present in concentration ranging from 5 percent to 10 percent.

Inventors: CLAVENNA LEROY RUSSELL, DAVIS STEPHEN MARK, FIATO ROCCO ANTHONY, SAY GEOFFREY RHYS, CLAVENNA, LEROY RUSSELL, DAVIS, STEPHEN MARK, FIATO, ROCCO ANTHONY, SAY, GEOFFREY RHYS
Applicants: EXXON RESEARCH ENGINEERING CO, EXXON RESEARCH AND ENGINEERING COMPANY
Application year: 1994
Main classification: C01B3
IPC codes: B01J37, C01B3, C01B31