PROCESS AND APPARATUS FOR MANUFACTURING ABSORBENT GRANULAR MATERIAL

Abstract: In a process for making a granular material from a reject stream from a coated grade waste paper pulp stock recycling process, the pulp stock is screened so that the reject stream passes through a screen and long fibers are retained for use in making paper. Solid material in the reject stream is separated by flotation (18). Water is removed from the reject stream to increase its consistency to that of modeling clay (40). The reject stream is supplied to an agglomerator (46) which forms uniform granules of irregular but approximately spherical shape. The granules are then dried (50) so that the granules have a solids content greater than 95 %. Apparatus for performing the process and characteristics of granular material formed by the process and apparatus are also described.

Description: Process and Apparatus for Manufacturing Absorbent Granular Material Field of the Invention The present invention relates to recycling waste paper, and more particularly to :cycling processes for making absorbent granular materials from waste paper. Background of the Invention Paper recycling has, in recent years, become a more important and attractive option to disposal of waste paper by deposition in landfills or by incineration. It has been a common practice for many years to make paper, especially tissue, from recycled paper. Typically, the waste paper is supplied to a hydropulper where the paper is pulped with caustic, dispersants and large amounts of water to form a slurry of fibers, fines and fillers. The long fibers are concentrated in the slurry by various known means and the slurry passes through a de-inking treatment, and possibly other treatments, and then is supplied to a paper making machine where fibers are removed from the slurry to make the paper. The reject stream from the pulping process generally includes significant amounts of organic materials such as cellulosic fibers too short to be of use in making recycled paper, along with tannin, lignin, etc., and inorganic materials, particularly kaolin clay, calcium carbonate and titanium dioxide, which are suspended in the water used in the recycling process. In view of stringent water quality standards, it is desirable to recycle the water from the recycling process by removing the reject material from the waste stream. It is further desirable to provide a use for the reject materials removed from the waste stream. Various processes have been proposed for recovering long fibers from post-consumer waste paper and magazines for use in making paper. The shorter fibers (generally less than 0.1 mm in length) are not satisfactory for making paper and are removed with the reject stream. Often the reject stream is dewatered and then sent to a landfill or incinerator. However, restrictions on landfills and incinerators make the disposal of the rejects prohibitively expensive. As an alternative, it has been proposed to convert the reject into useful products. Such products include industrial absorbents for oil and water, and animal litter and feed. These products are also used as soil conditioners and agricultural carriers for spreading pesticides, and as fillers for building materials. U.S. Patent Nos. 3,980,050; 4,203,388; 4,560,527; and 4,621,011, for example, disclose processes for turning a waste material, such as waste paper, newsprint, etc., into useful products including animal litter, oil absorbent, mulch, or a carrier for other materials. The fibers from the waste material are formed into particles and dried. Summary of the Invention It is an object of the present invention to provide an efficient and economical process for utilizing waste paper materials in producing useful granular products. More particularly, an object of this invention is to beneficially reuse a portion of the waste paper that is not acceptable for papermaking. The process of this invention utilizes waste paper, preferably office waste that is printed with laser print, Xerox print, or other inks, and magazines that have a coated surface. The waste paper is pulped with water, caustic and surfactants to produce a slurry containing paper fibers, paper fines and fillers. After several washing steps, the slurry passes through a wire washer which separates long fibers from the fines and filler. The long fiber stream, also referred to as the "accepts stream", is directed to a conventional papermaking machine for processing into paper. The filtrate from the washer continues through the process of this invention by flowing into a flotation clarifier where the suspended solids (fines and filler) are concentrated as a flotate and clarified water is removed for reuse in the process. In order to sterilize the absorbent material without using biocidal chemicals, the flotate is pasteurized at a minimum temperature of 160°F. This flotate is then passed through a belt press where the water content is further reduced. The filter cake from the belt press is in the form of a gray, wet cake that resembles and has the consistency of modeling clay. The wet cake then passes, by means of a screw conveyor, to an agglomerator where the material is formed into a granular shape. The wet granules are then sent through a conveyor dryer to produce dry granules of irregular shape and having good absorbent characteristics. The granules produced by this process have a high absorbency toward liquids. Their composition, by weight, is approximately 50% inorganic fillers (kaolin clay, calcium carbonate, titanium dioxide) and 50% organic (cellulose fines, starches, tannins, lignin, etc.). Less than 10% of the cellulosic material is the form of fibers greater than 1 mm in length. The bulk ensity of the granules is between 28-35 lbs./cu.ft. These granules are useful as oil and water absorbents as well as carriers for agricultural chemicals. Description of the Drawing A preferred embodiment of the invention is illustrated in the accompanying drawing, in which: FIG. 1 is a schematic view of the process and apparati:._. for performing the process for manufacturing the granules according to the present invention. Detailed Description The process of this invention utilizes waste paper that is collected from offices or other sources that contain primarily recyclable paper grades, including magazines (with clay-based coatings) and writing grades (with laser print, Xerox print and other inks) . Long fibers that can be used to make paper are separated in this process from a reject stream which includes inks, fines (cellulose less than 0.1 mm in length) and fillers (kaolin clay, calcium carbonate, titanium oxide, etc.) . Referring to Fig. 1, waste paper is supplied to a hydropulper 2 along with clarified water, caustic agents, such as sodium hydroxide, and dispersants to separate the fiber from the other components of the waste paper. Plastics, debris and other foreign objects are removed by conventional means. The pulp slurry from the hydropulper, which contains more than 95% water, passes through a pipe 4 to a washer 6 where several conventional washing steps are performed. In the washer 6, the slurry flows over wire screens where long fibers are retained on the screens and the reject stream passes through the screen and is conducted out of the washer through a pipe 16. The long fibers that are retained on the screen are conducted through a pipe 8 and subject to further cleaning, de-inking and processing, indicated at 10, before being supplied through a pipe 12 to a papermaking machine 14. More than 95% of the long fibers in the pulp slurry are converted to tissue paper. The reject stream from the wire screen washer 6 is in the form of a slurry containing less than 1% solids, including cellulosic fines and fillers. Typically 50% of the solids are fillers such as kaolin clay, calcium carbonate and titanium dioxide. The remaining 50% is mostly cellulose fines which are less than 1 mm in length, with some sugars, tannins, lignins, etc. This slurry, which contains between 99% and 99.5% water, is conducted through the pipe 16 to a dissolved air flotation clarifier 18. Suitable clarifiers are commercially available (e.g., Supracell from Krofta, or Deltafloat from Meri) . A flocculating polymer, such as Drewfloc 441 from Drew Chemical Co., or Calgon TRP 945, and air are added to the reject stream in the pipe 16 before it enters the clarifier. The slurry fills the clarifier 18, and the flocculated suspended solids float on the air bubbles to the surface of the clarifier. At this point, the mat of solids, which has a consistency of 3-6%, is skimmed or raked off the surface and removed from the clarifier through the pipe 20. The clarified water from the clarifier 18 is conducted back into the hydropulper 2 through the pipe 22. In accordance with this invention, mill process effluent that contains long fibers may be utilized to increase the efficiency of the process. This effluent would include reject water streams, spills from pulp and paper mills, etc. In Fig. 1, the effluent stream would include a process white water stream 23 from the papermaking machine 14, an overflow stream 24 which would previously have been discharged to a sewer, and a white water stream 25. The process white water is returned to the washer 6. The overflow stream 24 is supplied to a fiber recovery process 26 where the stream passes through screens that separate the long fibers in a similar manner to the washer 6. Long fibers with water are supplied through the pipe 28 from the fiber recovery unit 26 to the washer 6. An essentially fiber-free slurry flows through the pipe 30 to a flotation clarifier 32 that operates in the same manner as t clarifier 18. The white water stream 25 from the papermaking machine is supplied to another flotat- n clarifier 27 where the flocculated suspended solids are re...jved in the same manner as in the clarifier 18. A stream containing 3-7% solids passes out of the clarifier 32 and the clarifier 27 through the pipe 34. Clarified water from the clarifier 32 flows through the pipe 33 and is available for use in the process. The flotate from the clarifiers 18, 27 and 32 is mixed to form a single concentrated stream and is supplied to a heater 36. The heater 36 may be of any suitable type, such as a steam injection unit, or a heat exchanger. The flow rate of the stream and the heat applied should be sufficient to raise the temperature of the stream for sufficient time to achieve pasteurization of the stream. Preferably, the stream should be heated to a temperature of at least 160°F. The stream passes out of the heat exchanger 36 through a pipe 38, and a second flocculating polymer (such as Drewfloc 453 from Drew Chemical Co.) is added to the slurry to cause the solids to agglomerate before the slurry enters a belt press 40. The belt press can be any one of the commercially-available units (e.g., Kompress Belt Filter Press, Model GRS-S-2.0 from Komline Sanderson). At the outlet of the belt press, the filter cake is 35-40% solids and has the consistency of moist modeling clay. Process white water from the belt press is returned to the hydropulper 2 through the pipe 42. The filter cake from the belt press 40 is conveyed by means of a screw conveyor 44 to a pin-mixer type agglomerator 46. In the agglomerator 46 (such as Dust-Maler Model #020 from Feeco International) , the filter cake is broken up by the rotating pins, so that uniform granules are formed as the material progresses from the inlet of the agglomerator to the outlet. It has been found that the agglomerator 46 produces optimum size particles by running in the middle of its speed range, which is at 540 RPM. Higher speeds give larger particles than desired. Lower speeds yield a larger variability in sizes, with no net increase in smaller sized granules. It is important that no additional water be added to the agglomerator, since the slurry passing through should have a consistency of 35 - 45% in order to yield the desired size and texture of the granules. A higher consistency produces more fines and a lower consistency produces larger and more variable sized granules. The lignin, tannin and starch in the slurry serve as the binder for the granules. From the agglomerator 46, the granulated, but still moist stream material moves, preferably under the force of gravity onto a swing conveyor 48, to the belt of a conveyor drier 50, such as a Proctor & Schwartz two-stage conveyor dryer. The conveyor dryer 50 preferably includes a housing through which the granular material moves while supported on the belt. The belt is porous and a heater blows hot air though the belt to dry the granules. At the outlet, the granules have a minimum solids content of 90% by weight, and preferably greater than 95%. Vibrating screens 52, such as manufactured by Sweco, are used to classify the material by size according to product specifications. The granules produced by this process contain approximately 50% by weight of organic materials, such as cellulosic fines, starches, tannins and lignins. This process removes at least 90% of fibers over 1 mm in length, and the granules contain less than 10% long fiber. The inorganic fillers comprise about 50% by weight of the granules and are made up primarily of kaolin clay, calcium carbonate and titanium dioxide. The granules have an irregular, generally spherical shape. The granules from the conveyor dryer vary in size. Typically, 50% will be retained on an 8 X 16 mesh screen, i.e., 50% would pass through an U.S. Sieve No. 8 mesh screen but would be retained on a 16 mesh screen. Typically, the remaining portion would be 44% in the 16 X 30 mesh size range, and 6% in the 30 X 60 mesh size range. The granules have a bulk density of between 28 - 35 lbs/cu. ft. The granular material according to the present invention is preferably able to withstand agitation such as might occur during shipment, handling, and storage. Resistance to attrition of the granules is between 90 and 95%. This percentage is based on the following test procedure. A weight of 75 grams of sample is shaken on a 60 mesh screen for ten minutes and 50 grams of the material retained is then shaken in a pan for ten minutes with ten steel balls (5/8" in diameter) . The entire sample is then shaken on a 60 mesh screen for ten minutes. The percentage of the original 50 grams retained on the 60 mesh screen is the resistance to attrition cited above. Granular material according to the present invention has been found to generally have a pH between 9.0 - 9.4. For an agricultural carrier application, pH must be no higher than 8.0. The pH of the agricultural carrier may be lowered by adding a pH lowering additive. Granular material according to the present invention is adapted to absorb various liquids to desired degrees as a function of percentage of weight of the granules. The granular material according to the present invention for use as an agricultural carrier preferably has a liquid holding capacity (LHC) toward chlorobenzene of between 26 - 29%. The material for use as a floor absorbent, when tested with material retained on an 8 X 35 mesh, preferably is able to absorb between 73 - 81% of its weight of water, and preferably between 51 - 62% of its weight of oil. While this invention has been illustrated and described in accordance with preferred embodiments, it is recognized that variations and changes may be made therein without departing from the invention as set forth in the claims.

Claims: WHAT 1-. CLAIMED IS; 1. A process for making a granular absorbent material from waste paper containing kaolin clay, long fibers and fine cellulosic material, and other solid components, comprising the steps of: (a) forming pulp slurry from waste paper containing kaolin clay, long cellulose fibers, and other solid components; (b) screening the pulp slurry so as to produce a main stream containing long fibers for papermaking and to produce a main reject stream containing water, kaolin clay and other solid material; (c) clarifying the main reject stream by flotation to produce a main concentrated stream of solid components; (d) de-watering the concentrated stream to a consistency of between about 35 and 40 percent; (e) agglomerating the concentrated stream to form granules; (f) drying the granules until the granules have a solids content greater than 90%. 2. The process according to claim 1, wherein the reject stream is heated to pasteurization temperature before the agglomerating step. 3. The process according to claim 1, wherein the drying step is carried out in a belt dryer. 4. The process according to claim 1, wherein the reject stream before said clarifying step contains less than 1% solids. 5. The process according to claim 4, wherein said concentrated stream produced in said clarifying step has a consistency of between 3% and 6%. 6. The process according to claim 1 including heating the concentrated stream between said clarifying step and said agglomerating step to a temperature greater than about 160° F. 7. The process according to claim 1 including passing mill process effluent through a fiber recovery unit to produce a first stream containing long fibers for papermaking and to produce a second stream containing water, kaolin clay and other solid material; clarifying the second stream by flotation to produce a second concentrated stream; and mixing the main concentrated stream and the second concentrated stream before the de-watering step. 8. The process according to claim 1, wherein the agglomerating step is carried out without the addition of any liquid. 9. The process according to claim 1 including classifying the granules after the drying step. 10. The process according to claim 1, wherein the screening step removes more than 90% of the long fibers from the pulp slurry to the main stream. 11. An apparatus for making a granular absorbent material from waste paper containing kaolin clay, long fibers and cellulosic fines and other solid components comprising: (a) pulping means for producing a pulp slurry from waste paper containing kaolin clay, long fibers, cellulosic fines and solid components; (b) screen means for screening the pulp slurry from the pulping means to retain long fibers for papermaking and to produce a reject stream; (c) clarifier means for floating and concentrating solid material in the reject stream from the screen means; (d) press means for removing water from the concentrated solid material from the clarifier means; (e) agglomerating means for forming granular material containing the solid material from the press means; and (f) drying means for drying the granules of solid material from the agglomerating means so that the granules have a solids content greater than 90%. 12. The apparatus according to claim 11 including heat exchanger means between the clarifier means and the press means for heating the concentrated solid material to a temperature of at least about 160° F. 13. The apparatus according to claim 11, wherein the agglomerating means has a housing with a rotary shaft mounted in the housing, the rotary shaft has a plurality of radial pins and the housing has an inlet adjacent one end of the housing for receiving solid material and has an outlet spaced longitudinally of the shaft from the inlet for discharging the granular material. 14. The apparatus according to claim 11 including classifying means for classifying the granules by size after passing through the drying means. 15. The apparatus according to claim 11 including conveyor means for transferring the concentrated stream from the press means to the agglomerating means. 16. An absorbent material comprising: irregularly shaped generally spherical granules formed from a reject stream from a coated grade waste paper pulp stock recycling process, said granules having a bulk density between 28 - 35 lb/cu. ft. 17. The absorbent material according to claim 16, wherein the granules are of a size such that about one-half of the granules would pass through an 8-mesh screen and be retained on a 16-mesh screen, the balance of the granules being a smaller size. 18. The absorbent material according to claim 16, wherein the granules contain less than 10% long fibers. 19. The absorbent material according to claim 16, wherein the granules have a resistance to attrition of at least 90%. 20. An absorbent material comprising: irregularly shaped generally spherical granules containing about 50% by weight of inorganic fillers, including kaolin clay and about 50% by weight of organic materials, including starches, tannins, lignins and cellulose fines; the granules containing less than 10% long cellulose fibers. 21. The absorbent material according to claim 20, wherein the granules are of a size such that about one-half of the granules would pass through an 8-mesh screen and be retained on a 16-mesh screen, the balance of the granules being of a smaller size; and the granules having a resistance to attrition of at least 90%. 22. The absorbent material according to claim 20, wherein the granules have a liquid holding capacity toward chlorobenzene of between about 26% and about 29%; and when tested with granules having a size between 8 mesh and 35 mesh has the ability to absorb between about 73% and about 81% of its weight in water and between about 51% and about 62% of its weight in oil. 23. The absorbent material according to claim 20, wherein the granules have a pH of 8.0 or less.

Inventors: KNAPICK EDWARD G, WILLEMSEN BRENT, KNAPICK, EDWARD, G., WILLEMSEN, BRENT
Applicants: MARCAL PAPER MILLS INC, MARCAL PAPER MILLS, INC.
Application year: 1994
Main classification: D21B1
IPC codes: A01K1, C05D3, C05D9, C05G3, D21B1, D21C5, D21F1