Use of supported palladium/platinum catalysts in the preparation of tertiary butyl alcohol from tertiary butyl hydroperoxide

Abstract: A method for preparing tertiary butyl alcohol wherein a feedstock comprising a solvent solution of tertiary butyl hydroperoxide in tertiary butyl alcohol or a mixture of tertiary butyl alcohol with isobutane is charged to a hydroperoxide decomposition reaction zone containing a catalytically effective amount of a hydroperoxide decomposition catalyst consisting essentially of alumina having palladium and platinum deposited thereon and is brought into contact with the catalyst in liquid phase under hydroperoxide decomposition reaction conditions to convert the tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol.

Description: This invention relates to the catalytic decomposition of tertiary butyl hydroperoxide (TBHP). More particularly, this invention relates to a method for the preparation of tertiary butyl alcohol (TBA) by the catalytic decomposition of tertiary butyl hydroperoxide. Still more particularly, this invention relates to a method wherein an alumina supported palladium/platinum catalyst is used to catalyze the substantially selective decomposition of tertiary butyl hydroperoxide to tertiary butyl alcohol. It is known to react isobutane with oxygen, either thermally or catalytically, to form a peroxidation reaction product wherein the principal peroxide that is formed is tertiary butyl hydroperoxide. It is also known to thermally or catalytically decompose the tertiary butyl hydroperoxide to form tertiary butyl alcohol. Sanderson et al. disclose the use of a variety of catalysts for the decomposition of tertiary butyl hydroperoxide in a series of U. S. patents, including a catalyst composed of unsupported nickel, copper, chromia and iron (U. S. Patent No. 4,704,482), a catalyst composed of iron, copper, chromia and cobalt (U. S. Patent No. 4,705,903), a catalyst composed of a base treated hydrogenation catalyst from groups VIA or VIII of the Periodic Table (U. S. Patent No. 4,742,179), a catalyst consisting essentially of nickel, copper, chromium and barium (U. S. Patent No. 4,873,380), a catalyst composed of a metal phthalocyanine promoted with a rhenium compound (U. S. Patent No. 4,910,349), a catalyst composed of a base promoted metal phthalocyanine compound (U. S. Patent No. 4,912,269), a catalyst composed of a soluble ruthenium compound promoted with a bidentate ligand (U. S. Patent No. 4,912,033), a catalyst composed of a metal porphine such as iron (III) or manganese (III) promoted with an alkyl thiol or an amine, a catalyst composed of an imidazole promoted metal phthalocyanine compound (U. S. Patent No. 4,912,266), (U. S. Patent No. 4,922,034), a catalyst composed of a metal phthalocyanine promoted with a thiol and a free radical inhibitor (U. S. Patent No. 4,922,035), a catalyst composed of a borate promoted metal phthalocyanine (U. S. Patent No. 4,922,036), or a catalyst composed of a soluble ruthenium compound and an iron compound such as an acetate, a borate, a bromide, a chloride, a 1,3-propanedionate , a 2-ethyl-hexanoate, an iodide, a nitrate, a 2,4-pentanedionate, a perchlorate or a sulfate (U. S. Patent No. 5,025,113). As stated, when isobutane is reacted with molecular oxygen, the principal products of the reaction are tertiary butyl alcohol and tertiary butyl hydroperoxide. However, minor amounts of other contaminants are also formed. A minor amount of water will be formed, which will normally amount to 0.5 to 1 wt.% of the reactor effluent. The amount of byproduct water that is produced is a function of the severity of the reaction conditions employed and will tend to increase as the severity of the reaction conditions is increased. As indicated, tertiary butyl hydroperoxide is useful as a raw material for the manufacture of tertiary butyl alcohol. The tertiary butyl alcohol can be formed by catalytic decomposition of the tertiary butyl hydroperoxide. US-A-3,472,876 discloses a process wherein an oxygen-containing gas was charged to a reactor containing isobutane and an oxidation catalyst to provide a reaction mixture comprising tertiary butyl alcohol, tertiary butyl hydroperoxide, acetone, and tertiary butyl ether. The reported results in the patent indicate that there was a comparatively low rate of conversion and a comparatively poor selectivity of the reaction to tertiary butyl alcohol. There is a need for a catalytic decomposition of tertiary butyl hydroperoxide to tertiary alcohol at a higher conversion rate and an improved selectivity over the prior art. In accordance with the present invention, a solvent solution of a tertiary butyl hydroperoxide charge stock is brought into contact with a catalytically effective amount of a hydroperoxide decomposition catalyst in a hydroperoxide decomposition reaction zone in liquid phase to convert the tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol, the hydroperoxide decomposition catalyst being a supported hydroperoxide decomposition catalyst consisting essentially of alumina having deposited thereon from 0.01 to 5 wt.%, preferably 0.1 to 5 wt.%, of palladium and from 0.01 to 5 wt.%, preferably 0.1 to 5 wt.%, of platinum in the ratio of 0.1 to 10 parts of platinum per part of palladium, and tertiary butyl alcohol is recovered from the products of the hydroperoxide decomposition reaction. The tertiary butyl alcohol will not be the only decomposition product that is formed. Minor amounts of other oxygen-containing materials will also be formed. The starting materials for the process of the present invention are a tertiary butyl hydroperoxide feedstock and an alumina supported palladium/platinum catalyst. The Tertiary Butyl Hydroperoxide Feedstock The tertiary butyl hydroperoxide charge stock may comprise an isobutane oxidation product wherein the tertiary butyl hydroperoxide is dissolved in a mixture of isobutane and tertiary butyl alcohol or may comprise an isobutane oxidation product diluted by the addition of tertiary butyl alcohol, such that the solution of tertiary butyl alcohol in the mixture of isobutane with tertiary butyl alcohol contains from 5 to 30 wt.% of tertiary butyl hydroperoxide. Alternatively, the isobutane reaction product may be charged to a distillation zone where unreacted isobutane is removed as a distillate fraction for recycle to thereby provide a solution of tertiary butyl hydroperoxide in tertiary butyl alcohol containing 5 to 30 wt.% of tertiary butyl hydroperoxide. The Catalyst System The hydroperoxide decomposition catalyst to be used in accordance with the present invention is a supported hydroperoxide decomposition catalyst consisting essentially of alumina having deposited thereon from 0.01 to 5 wt.% of palladium and 0.01 to 5 wt.% of platinum in the ratio of 0.1 to 10 part of platinum per part of palladium. More preferably, the catalyst will consist essentially of alumina having from 0.1 to 1 wt.% of palladium and from 0.1 to 1 wt.% of platinum deposited thereon, based on the weight of the alumina support. Preferably, the platinum and palladium are present in the weight ratio of from 0.5 to 2 parts of platinum per part of palladium. Still more preferably, equal parts by weight of palladium and platinum are used. Catalytic Decomposition of Tertiary Butyl Hydroperoxide The process of the present invention may be conducted batchwise in kettles or by continuously passing the reactants through a tubular reactor. The catalytic decomposition of the tertiary butyl hydroperoxide is preferably conducted at a temperature within the range of 20° to 250°C, preferably 60° to 120°C, and more preferably, at a temperature within the range of 80° to 100°C. The reaction is preferably conducted at a pressure sufficient to keep the reactants and the reaction products in liquid phase. A pressure of 0.1 to 7 MPa (0 to 1,000 psig) may be used, if desired. Flow rates of the charge solution to the reaction zone should be adjusted in order to provide an appropriate contact time within the reactor. In a batch process, the holding time may suitably be from 0.5 to 10 hours, and more preferably 1 to 3 hours. In accordance with the most preferred embodiment of the present invention, isobutane is reacted with oxygen in an oxidation zone under oxidation reaction conditions including a temperature of 135 to 155°C., a pressure of 2.1 to 5.6 MPa (300 to 800 psig), and a holding time of 2 to 6 hours to provide an initial oxidation reaction product comprising unreacted isobutane, tertiary butyl hydroperoxide, tertiary butyl alcohol, and oxygen-containing by-products. The initial oxidation reaction product is then used as the tertiary butyl hydroperoxide charge stock of the present invention. If the concentration of tertiary butyl hydroperoxide in the tertiary butyl hydroperoxide charge stock is more than 30 wt.% of the initial oxidation reaction product, the initial oxidation reaction product can be diluted with an amount of tertiary butyl alcohol sufficient to lower the concentration of the tertiary butyl hydroperoxide to a desired percentage, to provide, for example, a tertiary butyl hydroperoxide charge stock containing from 15 to 25 wt.% of tertiary butyl hydroperoxide. Alternatively, the initial oxidation reaction product may be fractionated in any appropriate manner (e.g., by distillation in a distillation zone) to remove the isobutane therefrom for recycle and to provide a solution of tertiary butyl hydroperoxide and tertiary butyl alcohol which will normally contain from 5 to 30 wt.% of tertiary butyl hydroperoxide. The solution of tertiary butyl hydroperoxide in tertiary butyl alcohol is then charged to a catalytic hydroperoxide decomposition zone where it is brought into contact with an alumina supported palladium/platinum catalyst to substantially selectively convert the tertiary butyl hydroperoxide to tertiary butyl alcohol with high yields and selectivities. When the process of the present invention is practiced in a continuous manner by continuously charging the tertiary butyl hydroperoxide charge stock to a reactor containing a fixed bed of pelleted hydroperoxide decomposition catalyst, the space velocity is suitably in the range of 0.5 to 3 volumes of tertiary butyl hydroperoxide charge stock per volume of catalyst per hour. Preferably, the space velocity is within the range of 1 to 2 volumes of tertiary butyl hydroperoxide charge stock per volume of catalyst per hour. The reaction product from the tertiary butyl hydroperoxide decomposition step may then be fractionated in any suitable manner, such as by distillation to recover the tertiary butyl alcohol. EXAMPLES The invention will be further illustrated by the following non-limiting examples. Procedure The reactor that was used for the experiments was a stainless steel tube (12.3 x 360mm) which was electrically heated. Liquid feed was pumped into the bottom of the reactor using a Ruska® dual drive pump. Pressure was regulated using a Skinner® Uni-Flow valve and a Foxboro® controller. Samples were collected at the top of the reactor, cooled to ambient temperature, filtered and analyzed by Gas Chromatography. The analysis of the feed and of the products obtained is reported in the following tables. Example 1 In this example, the catalyst consisted essentially of palladium and platinium in a 1:1 ratio. CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDE TO TERT-BUTYLALCOHOL RUN A 1 2 3 4 Catalyst 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 Catalyst (cc) 50 50 50 50 Pressure (MPa) 3.5 3.5 3.5 3.5 Feed Rate (cc/Hr.) 25 25 25 25 Temperature (°C) 80 100 120 140 Time on Stream (Hr) 4 4 4 4 Space Vel. (cc/cc) 0.5 0.5 0.5 0.5 TBHP Conversion (mol.%) 74.2 89.1 99.3 99.8 Selectivity IC4= (mol.%) -0.0 0.0 0.0 -0.0 Sel. Acetone (mol.%) 10.9 21.3 20.2 19.9 Sel. Methanol (mol.%) 2.6 5.2 1.2 1.6 Sel. TBA (mol.%) 84.1 76.2 79.0 80.1 Sel. DTBP (mol.%) 5.0 2.5 0.8 -0.0 Remarks H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis Composition, wt% IC4= 0.001 0.000 0.001 0.002 0.000 MEOH/MF 0.016 0.148 0.329 0.094 0.125 Acetone 0.008 1.005 2.344 2.487 2.460 TBA 79.968 91.565 93.477 96.053 96.423 DTBP 0.055 0.634 0.402 0.182 0.048 TBHP 19.146 4.934 2.091 0.125 0.036 CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDE TO TERT-BUTYLALCOHOL RUN A 5 6 7 8 Catalyst 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 Catalyst (cc) 50 50 50 50 Pressure (MPa) 3.5 3.5 3.5 3.5 Feed Rate (cc/Hr.) 50 50 50 50 Temperature (°C) 80 100 120 140 Time on Stream (Hr) 4 4 4 4 Space Vel. (cc/cc) 1.0 1.0 1.0 1.0 TBHP Conversion (mol.%) 63.2 93.2 99.5 99.7 Selectivity IC4= (mol.%) -0.0 -0.0 0.0 0.0 Sel. Acetone (mol.%) 10.5 20.3 22.4 27.2 Sel. Methanol (mol.%) 2.7 2.9 1.7 2.1 Sel. TBA (mol.%) 84.6 78.0 76.9 72.7 Sel. DTBP (mol.%) 4.9 1.7 0.7 0.1 Remarks H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis Composition, wt% IC4= 0.001 0.000 0.000 0.001 0.006 MEOH/MF 0.016 0.131 0.197 0.130 0.161 Acetone 0.008 0.827 2.343 2.754 3.356 TBA 79.968 89.584 94.549 95.827 95.424 DTBP 0.055 0.538 0.295 0.169 0.066 TBHP 19.146 7.050 1.297 0.088 0.064 CATALYTIC CONVERSION OF TERT-BUTYLHYDROPEROXIDE TO TERT-BUTYLALCOHOL RUN A 9 10 11 Catalyst 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 0.15% Pd, Pt /Al 2 O 3 Catalyst (cc) 50 50 50 Pressure (MPa) 3.5 3.5 3.5 Feed Rate (cc/Hr.) 100 100 100 Temperature (°C) 80 100 120 Time on Stream (Hr) 4 4 4 Space Vel. (cc/cc) 2.0 2.0 2.0 TBHP Conversion (mol.%) 62.9 91.2 99.3 Selectivity IC4= (mol.%) 0.0 0.0 0.0 Sel. Acetone (mol.%) 12.6 25.0 25.9 Sel. Methanol (mol.%) 3.0 3.9 2.2 Sel. TBA (mol.%) 82.7 73.3 73.5 Sel. DTBP (mol.%) 4.7 1.7 0.7 Remarks H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis H 2 O Free Basis Composition, wt% IC4= 0.001 0.001 0.002 0.006 MEOH/MF 0.016 0.146 0.256 0.165 Acetone 0.008 0.985 2.824 3.175 TBA 79.968 89.366 93.583 95.302 DTBP 0.055 0.517 0.290 0.160 TBHP 19.146 7.108 1.682 0.142 A 19.1% solution of TBHP in TBA decomposed over a commercial 0.15% Pd, 0.15% Pt on alumina gave (80°C, 0.5 space velocity) 74.2 TBHP conversion with selectivity to TBA of 84.1%, DTBP 5.0%, acetone 10.9%, and methanol 2.6%. Minor products including carboxylic acids were also formed. At 140°C (0.5 space velocity), 99.8% TBHP conversion was observed with a selectivity to TBA of 80.1%, DTBP ∼0%, acetone 19.9% and methanol 1.6%. Thus, at higher temperatures more TBHP is decomposed, but the selectivity to TBA is decreased somewhat. The same trend is observed at other space velocities: i.e., a higher selectivity to the desired TBA at lower temperatures.

Claims: A method for the decomposition of tertiary butyl hydroperoxide to tertiary butyl alcohol, wherein a solvent solution of a tertiary butyl hydroperoxide charge stock is brought into contact with a hydroperoxide decomposition catalyst, characterized in that said hydroperoxide decomposition catalyst comprises a mixture of palladium and platinum supported on alumina. A method as claimed in Claim 1, wherein the solvent comprises tertiary butyl alcohol, or a mixture thereof with isobutane. A method as claimed in Claim 1 or Claim 2, wherein a solution of a tertiary butyl hydroperoxide charge stock that contains from 5 to 30 wt.% of tertiary butyl hydroperoxide is brought into contact with a catalytically effective amount of a hydroperoxide decomposition catalyst in a hydroperoxide decomposition reaction zone in liquid phase under hydroperoxide conversion conditions including a temperature within the range of 20° to 250°C. and a pressure of 0.1 to 7 MPa (0 to 1,000 psig) to convert said tertiary butyl hydroperoxide to decomposition products, principally tertiary butyl alcohol, characterized in that said hydroperoxide decomposition catalyst consists essentially of alumina having deposited thereon from 0.1 to 5 wt.% of palladium and 0.1 to 5 wt.% of platinum in the ratio of 0.1 to 10 part of platinum per part of palladium. A method as in claim 3, wherein the temperature is in the range of 40° to 150°C. and the pressure is about 0.1 MPa. A method as claimed in anyone of Claims 1 to 4, wherein the catalyst consists essentially of alumina having from 0.1 to 10 wt.% of palladium and from 0.1 to 10 wt.% of platinum deposited thereon, based on the alumina, the palladium and platinum being present in the weight ratio of 0.5 to 2 parts of platinum per part of palladium. A method as claimed in claim 5, wherein the palladium and platinum are present in equal proportions.

Inventors: DURANLEAU ROGER GEORGE, KNIFTON JOHN FREDERICK, SANDERSON JOHN RONALD, DURANLEAU, ROGER GEORGE, KNIFTON, JOHN FREDERICK, SANDERSON, JOHN RONALD
Applicants: TEXACO DEVELOPMENT CORP, TEXACO DEVELOPMENT CORPORATION
Application year: 1994
Main classification: C07C29
IPC codes: C07C27, C07C29, B01J23, C07B61, C07C31