Electrochemical cells using a polymer electrolyte

Abstract: An article suitable for use as a cathode comprising active cathode material and an ionically nonconductive prepolymeric composition as a binder, as well as electrochemical cells comprising such a cathode and a process for their preparation are provided.

Description: The present invention relates to a process for preparing an electrochemical cell comprising a polymer electrolyte. Polymer electrolytes are typically either solid or semi-solid and their use in electrochemical cells may eliminate the need for a microporous separator in the cell, as well as rendering the resultant cell free of liquid electrolyte. Conventional cells in which the electrolyte is an organic liquid normally contain a microporous separator; however, these separators are an expensive component of the cell. Furthermore, such separators can increase the internal resistance of the cell and, consequently, may decrease the high rate performance of the cell. The liquid organic electrolytes used in such conventional cells are often highly volatile liquids and, if these liquids escape from the cell, a hazardous situation can occur. Polymer electrolytes are known and typically comprise a polymer matrix material and an ionically conductive salt. Examples of polymer matrix materials which are generally used in such electrolytes include the polyalkylene oxides, such as polyethylene oxide or polypropylene oxide; and substituted polyethylene glycols lonically conductive salts which form the second part of the electrolyte include, for example, LiCF 3 SO 3 , and LiClO 4 . The prior art describes several examples of solid polymeric electrolyte cells. U.S. Patent Number 4,925,751 discloses a solid state laminar cell containing an alkali metal anode, a solid ionically conducting electrolyte, a composite cathode and a carrier. The composite cathode comprises active material, a conductive filler and an ionically conductive electrolyte. The electrolyte comprises a liquid monomeric or prepolymeric curable composition and an ionisable alkali metal salt. During assembly of this cell, the composite cathode mixture is applied to a current collector and then a layer of polymer electrolyte is coated over this mixture. The polymer electrolyte layer and the polymer in the cathode are then cured in place, after which a thin foil anode layer is applied to the polymeric surface. U.S. Patent Number 4,748,542 and U.S. Patent Number 4,638,407 both disclose solid state capacitors and multicell batteries in which a layer of a solid polymer electrolyte is laminated to a layer of the cathode and anode. Another example of a solid electrolyte cell is disclosed in U.S. Patent Number 4,594,299. The cell disclosed in this patent is made by protecting an electrode, such as a lithium electrode, with an ionically conductive polymer. The resulting electrode can then be combined with a cathode to form the electrochemical cell. A further solid polymeric electrolyte is described in U.S. Patent Number 4,654,279. The electrolyte in this patent is a two phase interpenetrating network consisting of a mechanically supporting phase of a continuous network of a crosslinked polymer and an ionically conducting phase. A suitable amount of a metal salt is then added to the electrolyte to provide ionic conductivity. U.S. Patent Number 4,589,197 discloses a composite cathode sheet made from a solution of an active cathode material and a low molecular weight polymer, such as polyethylene oxide, in a solvent such as acetonitrile. The polymer preferably contains an electrolyte salt. Despite the advantages of polymer electrolyte cells, as discussed above, there are certain problems associated with the use of such electrolytes, and particularly with solid polymer electrolytes. Three common problems which are often encountered are: (1) the cells typically contain only a low volume of active cathode material; (2) the electrolyte has little mechanical stability; and (3) there are safety problems associated with the assembly of live high area cells without the ability to check for shorts. The cells described in each of U.S. Patents Number 4,925,751, 4,748,542 and 4,638,407 discussed above will exhibit each of these three problems. In the devices of each of these patents, the cathode mixture comprises a prepolymer and an ionisable salt. This mixture will not, therefore, have a sufficiently high volume of active cathode material, and certainly not as high a volume as a conventional cell. The active life of the cell will thus be reduced. An ionisable salt also forms part of the polymer electrolyte layer; therefore, when this is applied as a film to the cathode mixture, it will be in the form of a tacky viscous gel which will be difficult to work with and will be susceptible to puncture by any of the other cell components, such as the metallic current collector. Furthermore, the resulting cathode and electrolyte layer combination is ionically conductive and thus, when this combined component is assembled with the anode, the device becomes an active electrochemical cell during the assembly process. There are clear disadvantages associated with this. In U.S. Patent 4,589,197, which discloses a solution of active cathode material and low molecular weight polymer in a solvent, as discussed above, the choice of polymers is, in practice, limited to low molecular weight polymers, since the polymer must be dissolved in a solvent and cast to form a sheet. It is apparent, therefore, that there are problems associated with currently available electrochemical cells containing polymer electrolytes. The present invention overcomes the above problems and provides a process for preparing an electrochemical cell employing a polymer electrolyte, which cells have a high volume of active cathode material and which process allows easy and safe assembly of the cell. In accordance with the above, the present invention provides, in a first aspect, a process for the preparation of an electrochemical cell that contains a polymer electrolyte, comprising preparing a cathode by mixing an active cathode material with sufficient of an ionically nonconductive prepolymeric composition to bind the cathode material and applying the resulting ionically nonconductive mixture to an electrically conductive current collector, polymerising the prepolymeric composition, forming an electrode assembly with an anode and electrically insulating ion permeable material disposed between the cathode and anode, loading the resulting electrode assembly into a cell housing and, thereafter, adding an amount of an ionisable electrolyte salt solution sufficient to provide ionic conductivity to the polymer film in the cathode and between the cathode and anode to form an active electrochemical cell wherein, prior to placing the assembly in the housing, a continuity check can be made on the assembly to detect any shorts. The process of the present invention uses active cathode material. The precise nature of the active cathode material is not critical to the present invention so long as this can be bound with or by an ionically nonconductive prepolymeric composition. The choice of material depends on various factors, such as the type of anode material to be employed in the cell and the intended use of the cell. Examples of suitable active cathode materials include: the transition metal chalcogenides, particularly the transition metal oxides and sulphides, such as cupric sulphide (CuS), cupric oxide (CuO), iron sulphides, vanadium pentoxide (V 2 O 5 ), V 6 O 13 , cobalt oxides, titanium disulphide (TiS 2 ), tungsten trioxide (WO 3 ), molybdenum trioxide (MoO 3 ), molybdenum disulphide (MoS 2 ); transition-metal polysulphides; and lithiated metal oxides and sulphides, such as Li x FeS 2 , Li x TiS 2 , lithiated cobalt and/or nickel oxides or lithiated manganese oxides. Electrically conductive polymers, such as polypyrrole or polyaniline, may also be used. Preferred active cathode materials include iron sulphide (FeS 2 ), manganese dioxide (MnO 2 ), titanium disulphide (TiS 2 ), vanadium pentoxide (V 2 O 5 ), V 6 O 13 , and tungsten trioxide (WO 3 ). When using a lithium anode and a 1.5 volt cell, we generally prefer to use an iron sulphide (FeS 2 ) cathode material. The process of the present invention uses sufficient of an ionically nonconductive prepolymeric composition to bind the cathode material. By "prepolymeric", as used herein, is meant that the composition may be polymerised. Prepolymeric compositions suitable for use in the present invention are preferably both electrically insulating and ionically nonconductive. The composition may include any one or combination of a suitable polymerisable monomer, comonomer or oligomer. The composition may also be curable and crosslinkable. Suitable compositions include ethylenically unsaturated monomers, comonomers and oligomers, alkylene oxide monomers, comonomers and oligomers, acrylic acid-based monomers, comonomers and oligomers, and mixtures of such compounds. Specific examples of materials suitable for use in the prepolymeric composition include: polyalkylene oxides, such as polypropylene oxide, polyethylene oxide or polyethylene-polypropylene oxide; polyalkylene glycols, such as polyethylene glycol; mixtures of polyalkylene oxides and glycols; polyethylene glycol acrylates, diacrylates and triacrylates; modified siloxanes; urethanes with polyethylene glycol side chains; epoxides and acrylated epoxides. Mixtures of low molecular weight polyethylene oxide and one or more polyethylene glycol acrylates, e.g. diacrylates and triacrylates, are preferred. When the cathode material is dispersed in an ionically nonconductive polymer film, any of the conductive polymer electrolytes discussed above can be used as the film. In addition, any of the polymer electrolytes known in the art, for example as disclosed in U.S. Patents Number 4,638,407; 4,925,751; 5,011,501; and 5,041,346, may be used as the cathode polymer film, provided that the resultant polymer film is ionically nonconductive. This is achieved by omitting the ionisable electrolyte salt during preparation of the cathode polymer film. The composition is ionically nonconductive when mixed, polymerised, cured and crosslinked in the presence of the active cathode material. However, the composition may be rendered ionically conductive by the absorption of an ionisable electrolyte salt. This absorption may be carried out in any suitable fashion, and preferably, by absorption from a solution of the salt in an organic solvent. The composition may be polymerised, cured or crosslinked by the use of any conventional technique, such as radiation or heat. If desired, a polymerisation initiator may be present. The choice of initiator may depend, for example, on the types of monomers or prepolymers used in the composition. Examples of suitable polymerisation initiators are disclosed in Encyclopaedia of Polymer Science and Engineering, Vol. 2, "Anionic Polymerisation and Cationic Polymerisation", pp. 143 to 145. A preferred example is 2,2'-azobisisobutyronitrile. The process of the present invention may use components in addition to those discussed above. Examples of such additional components include electronic conductors and voltage regulators, such as reducible metal additives. Preferred electronic conductors include graphite, acetylene black, carbon fibres, compatible metal powders or fibres, or electrically conductive polymers, such as polypyrrole or polyaniline. Typically, when measured in the absence of the ionisable electrolyte salt, the amount of the active cathode material in the finished cathode is at least about 50%, preferably at least about 60%, and more preferably at least about 70% by volume The amount of the prepolymeric composition used is an amount sufficient to bind the active cathode material and preferably to form a polymer film having the active cathode material dispersed throughout. This amount can vary, but typically ranges from about 10% to about 45% by volume, and preferably, from about 20% to about 35% by volume. The present invention also provides a process for making an electrochemical cell comprising a polymer electrolyte, as prepared in accordance with the process described above. The above process will be explained in more detail below, with relation to the preparation of an electrochemical cell. In one embodiment, the above process of the present invention comprises: (i) preparing a cathode by contacting active cathode material with a binding amount of an ionically nonconductive prepolymeric composition; (ii) applying the resulting composition to an electrically conductive current collector; (iii) polymerising the prepolymeric composition to form a film in which the active cathode material is dispersed; (iv) placing an active anode material next to the cathode; (v) disposing an electrically insulating material between the cathode and anode to form an electrode assembly; (vi) placing the electrode assembly inside a housing for the cell; and (vii) adding an amount of an ionisable electrolyte salt solution sufficient to provide ionic conductivity to the polymer film in the cathode and between the cathode and the anode. In an alternative embodiment, the present invention provides a process for making an electrochemical cell that contains a polymer electrolyte comprising: a) preparing a cathode by contacting active cathode material with a binding amount of an ionically nonconductive prepolymeric composition, the active cathode material forming at least 50% of the mixture by volume; b) applying the cathode and prepolymeric composition mixture to an electrically conductive carrier and polymerising the prepolymeric composition to provide a polymer film having active cathode material dispersed throughout; c) placing an active anode material next to the ionically nonconductive cathode with an electrically insulating ion permeable material disposed between the cathode and the anode to form an electrode assembly; and d) placing the electrode assembly inside a housing for the cell, and adding an amount of an ionisable electrolyte salt solution sufficient to provide ionic conductivity to the polymer film in the cathode and between the cathode and anode to form an active electrochemical cell. The process of the present invention includes contacting the active cathode material with a binding or film-forming amount of the prepolymeric composition. If desired, an organic solvent or plasticiser may be employed to improve the viscosity of the mixture. Typically the solvent employed will also act as a plasticiser and, in such cases, a solvent with a high boiling point is desired. Examples of suitable solvents include: alkylene carbonates, such as propylene carbonate or ethylene carbonate; 3-methyl-2-oxazolidone; dimethoxy tetraglycol (tetraglyme) and sulpholane or mixtures thereof. The precise amount of the plasticising solvent used is not essential to the present invention, provided that sufficient of the solvent is used to plasticise the mixture. Solvents which do not also act as plasticisers may also be used and, in this case, we prefer to use a low boiling point solvent, such as trichloroethylene, dimethoxyethane, triethylene glycol dimethyl ether (triglyme), dioxolane or tetrahydrofuran. The amount of such solvent used is not critical to the present invention, so long as this is sufficient to improve the viscosity of the mixture and so long as this can be removed easily after application of the cathode mixture to the current collector. We generally find that only a small amount of solvent is required. Mixtures of solvents may also be used and, in certain circumstances mixtures are preferred, providing a balance and diversity of properties to the mixture. Alternatively, an amount of the ionisable electrolyte salt may be used to alter the viscosity of or to plasticise the cathode mixture, so long as the amount used is less than that needed to render the cathode ionically conductive. This method of altering the viscosity or plasticising the mixture is less preferred. Once the cathode mixture has been prepared, it is applied to an electrically conductive current collector. The choice of current collector is not essential to the present invention, so long as it is electrically conductive. Typical such collectors include: a metal foil, for example a foil of aluminium, nickel or copper; a metal screen; a metallic or carbon foam, for example a nickel foam; or a metallic or carbon mat, for example a nickel or carbon fiber mat. An example of a preferred carrier is a metallic foil, such as aluminium foil. The cathode mixture may be applied to the current collector by any one of several different methods. Examples of appropriate methods of application include roll coating, doctor blading and imbed-extrusion. Once the cathode mixture has been applied to the current collector, any solvent used to affect the viscosity may be removed, for example by standard techniques, and the prepolymer composition may be polymerised, cured and/or crosslinked, for example using the techniques discussed above. The resultant article is a solid, dry, flexible, ionically nonconductive polymer film with active cathode material dispersed throughout, adhered to an electrically conductive current collector. The thickness of the polymer film may vary and is not critical to the present invention. Typically the thickness ranges from about 0.0508 to about 0254 mm (about 2 to about 10 mils), and preferably from about 0.0762 to about 0.154 mm (about 3 to about 6 mils). Polymerisation, curing or crosslinking of the prepolymer composition in the cathode may result in the formation of a continuous polymer film over the surface of the cathode. In this case, no active cathode material is exposed on the surface and the polymer film may then be used as the separator between the cathode and the anode. However, in order to ensure proper separation between the cathode and the anode, it may be desirable to employ another electrically insulating ion permeable separator between the cathode and the anode. This separator may be a microporous membrane or sheet, paper, plastic screen or a polymer film. When it is desired to include a separator, we prefer to use a polymer film, and preferably a film which includes the same or similar components to those that form the prepolymer composition in the cathode. Thus, when using a lithium foil anode, for example, we prefer to use a film of polyethylene oxide. It is preferred that the polymer film used for the separator does not contain any ionisable salt, thus preventing the cell from being electrochemically active until after assembly is completed. The separator may be applied to either the cathode or the anode, so long as it is disposed between them in the completed electrode assembly. When a polymer film is employed as separator, this is preferably applied to one or both surfaces of the anode. The polymer film forming the separator may be sprayed, laminated or roll coated, to form a tough thin amorphous flexible film on the electrode. The active anode material used in the process of the present invention may include active metals, such as zinc or aluminium; alkali metals; alkaline earth metals; and alkali metal interchelated carbon or graphites, such as lithium interchelated carbon or graphite, or composites thereof. Preferred active anode materials include alkali metals, especially lithium. Preferably, the anode is a foil of the metal, although the anode may also be a composite of a foil of the metal laminated with a layer of a polymeric composition. The anode and separator, when used, are placed next to the cathode to form the completed electrode assembly. If present, the separator is disposed between the cathode and the anode, as discussed above. Any type of electrode assembly may be used in the electrochemical cells of the present invention. Suitable electrode assemblies include: a jelly roll; flat single multicell assemblies and stacked flat multicell assemblies. When using a jelly roll assembly, the cathode, separator (when used) and anode are wound and then placed in the cell housing. Prior to placing the assembly in the housing a continuity check can be made on the assembly to detect any shorts. The cell housing may be of any material conventionally used for this component, for example plastic or metal, such as stainless steel or nickel plated steel, metal coated plastic, plastic-metal laminate sheets, and impermeable inorganic-coated plastic, such as SiO or SiO x -coated plastic. The assembly of the cell may be completed by the addition of an amount of an ionisable electrolyte salt to render the polymer film in the cathode and the separator between the cathode and the anode (when used) ionically conductive. Examples of suitable salts for non-aqueous cell systems include alkali metal salts that have the same cation as the anode metal, such as LiCF 3 SO 3 , LiClO 4 , LiBF 4 , LiAsF 6 , Li(CF 3 SO 2 ) 2 N, and the like. For aqueous cells systems, ZnCl 2 , AlCl 3 , KOH, and the like are suitable salts. The amount of the salt employed will vary depending on, for example, the type of active cathode material, the type of active anode material, the type of polymer employed in the cell, and the intended use of the cell. Typically, the amount will range from about 0.1 M to about 10.0 M, preferably from about 0.5 M to about 3.0 M, and more preferably from about 1.0 M to about 1.5 M. The salt is suitably added to the cell as a solution of the salt in a solvent. This solvent may, if desired, be that solvent acting as a plasticiser for the cathode mixture. For non-aqueous cells, suitable solvents include non-aqueous organic solvents such as dioxolane, dimethoxyethane, 3-methyl-2-oxazolidone, propylene carbonate, ethylene carbonate, triethylene glycol dimethyl ether (triglyme), diemethoxy tetraglycol (tetraglyme), sulpholane and 3,5-dimethylisoxazole. For aqueous cell systems, water may be used as the solvent. The cell is suitably sealed by using a cover with a sealing gasket. The cover, if metallic, may be in contact with one of the electrodes to provide a terminal for the cell and may contain a pressure relief vent. For flat cell constructions, the housing may be sealed with metal or plastic sheets, or plastic-metal laminate sheets. The electrochemical cells prepared by the process of this invention may be aqueous or non-aqueous, primary or rechargeable and have a solid polymer electrolyte. The electrolyte is formed after the prepolymer composition in the cathode is polymerised, and the electrode assembly is made and placed in the cell, at which point the ionisable salt is added. Since the ionisable salt is not added until after the electrode assembly is completed, if any short is present, no current will flow, and any potentially hazardous situations are avoided. Another advantage of the process of the present invention is that since the salt is not added until after assembly of the cell is completed, the cathode can contain a large volume of active cathode material. Yet another advantage of the process of the present invention is that after the prepolymeric composition is polymerised, the cathode is in the form of a solid dry flexible film that can be easily assembled with the anode. Still yet another advantage of the process of the present invention is that when the salt is added as a solution in a solvent which serves as a plasticiser for the polymer the polymer composition in the cathode mixture will swell to provide good electrode and electrolyte interfacial contact.

Claims: A process for the preparation of an electrochemical cell that contains a polymer electrolyte, comprising preparing a cathode by mixing an active cathode material with sufficient of an ionically nonconductive prepolymeric composition to bind the cathode material and applying the resulting ionically nonconductive mixture to an electrically conductive current collector, polymerising the prepolymeric composition, forming an electrode assembly with an anode and electrically insulating ion permeable material disposed between the cathode and anode, loading the resulting electrode assembly into a cell housing and, thereafter, adding an amount of an ionisable electrolyte salt solution sufficient to provide ionic conductivity to the polymer film in the cathode and between the cathode and anode to form an active electrochemical cell wherein prior to placing the assembly in the housing, a continuity check can be made on the assembly to detect any shorts. A process for making an electrochemical cell according to Claim 1 comprising: a) preparing a cathode and prepolymeric composition mixture by contacting active cathode material with a binding amount of an ionically nonconductive prepolymeric composition, the active cathode material forming at least 50% of the mixture by volume; b) applying the cathode and prepolymeric composition mixture to an electrically conductive carrier and polymerising the prepolymeric composition to provide a polymer film thereon having active cathode material dispersed throughout; c) placing an active anode material next to the ionically nonconductive cathode with an electrically insulating ion permeable material disposed between the cathode and the anode to form an electrode assembly; d) placing the electrode assembly inside a housing for the cell, and e) adding an amount of an ionisable electrolyte salt solution sufficient to provide ionic conductivity to the polymer film in the cathode and between the cathode and anode to form an active electrochemical cell. A process according to Claim 1 or 2, wherein polymerising the prepolymeric composition comprises curing and crosslinking. A process according to any preceding Claim, in which the active cathode material is dispersed in an ionically nonconductive polymer film, which film is in contact with an electrically conductive current collector. A process according to any preceding Claim, wherein the active cathode material is a transition metal chalcogenide. A process according to Claim 5, wherein the active cathode material is FeS 2 , MnO 5 , TiS 2 , V 2 0 5 , V 6 O 13 or WO 3 . A process according to any preceding Claim, wherein the prepolymeric composition comprises ethylenically unsaturated monomers, comonomers and oligomers; alkylene oxide monomers, comonomers and oligomers; acrylic acid-based monomers, comonomers and oligomers; or mixtures of such monomers, comonomers and oligomers, as the polymerisable component. An process according to Claim 7, wherein the polymerisable component is selected from polypropylene oxide, polyethylene oxide, polyethylene-polypropylene oxide, polyethylene glycol, polyethylene glycol acrylates, diacrylates and triacrylates, modified siloxanes, urethanes with polyethylene glycol side chains, epoxides and acrylated epoxides, and mixtures of such compounds. A process according to any preceding Claim, wherein the current collector is a metallic foil. A process according to any preceding Claim, wherein the active cathode material is FeS 2 , the prepolymeric composition is a mixture comprising polyethylene glycol acrylate, polyethylene oxide and polyethylene glycol diacrylate, and the current collector is aluminium foil. A process according to any preceding Claim, wherein the active cathode material is FeS 2 ; the prepolymeric composition is comprised of polyethylene oxide, polyethylene glycol acrylate, and polyethylene glycol diacrylate; the cathode current collector is aluminium foil, the anode is lithium; the electrically insulating ion permeable material is a polymer film of polyethylene oxide; the electrode assembly is a jelly roll assembly and the ionisable electrolyte salt solution is 1.5 M LiCF 3 SO 3 in a solvent comprising dioxolane, propylene carbonate, and dimethoxyethane.

Inventors: BAILEY JOHN C, BAILEY, JOHN C
Applicants: EVEREADY BATTERY INC, EVEREADY BATTERY COMPANY, INC.
Application year: 1994
Main classification: H01M4
IPC codes: H01M6, H01M4, H01M10