Build-up suppressor agent, compositons containing it and method of use in polymerization processes

Abstract: The present invention relates to build-up suppressor agents, compositions containing such suppressor agents, which are capable of inhibiting the formation of build-up in vinyl acetate or vinyl chloride polymerization processes, or in polymerization processes utilizing a mixture thereof, with or without other vinyl monomers polymerizable therewith, which processes are effected in aqueous suspension, aqueous emulsion or in bulk.

Description: The present invention relates to build-up suppressor agents and compositions containing such suppressor agents, which are capable of inhibiting the formation of build-up in vinyl acetate or vinyl chloride polymerization processes, or in polymerization processes utilizing a mixture thereof, with or without other vinyl monomers polymerizable therewith, which processes are effected in aqueous suspension, aqueous emulsion or in bulk. BACKGROUND OF THE INVENTION In all the above polymerization processes, part of the formed polymer tenaciously adheres to the reactor walls, thus forming so-called "build-up", with deleterious effects toward both the final product itself, due to small fragments of build-up which, by detaching from the reactor walls, can be included in the polymerized product and the safety of the reaction because the build-up slows the thermal exchange of the wall giving rise to safety problems for overheating. This build-up increases with repeated polymerization operations and eventually it becomes necessary to clean the walls after each repeated reaction. This cleaning is costly as it decreases the plant output and is dangerous for the operators due to the toxicity of the monomers, particularly vinyl chloride. Thus, the cleaning is carried out as infrequently as possible. A number of products and techniques have been developed to mitigate this problem, all of which are based on coating the reactor walls with products which inhibit adhesion of the build-up or even its formation, by impeding the polymerization of the monomers on the reactor walls. Phenol-formaldehyde condensation products (GB 1439339; JP 54-107991; CA 1181899; EP 0052421) or dye mixtures (alizarine, xanthones, natural flavonoids, naphthoquinones, hydroxyanthraquinones and others) with film-forming elements such as polysaccharides, polyvinyl alcohols, polyvinylpyrrolidone were proposed as reactor wall coating. See for example patents JP 04342701; JP 04154804; JP 04154801; JP 04154805; JP 04108805; JP 04159302 and JP 04031402. According to the literature, the products disclosed in EP 0052421 are particularly effective. All these products, in the industrial practice, are applied to the polymerization reactor walls in the form of a liquid, e.g. aqueous solutions, by means of spraying, using compressed nitrogen, or preferably water vapour, at pressures of 5-15 bar as the propellant for the solution. The build-up inhibitors, dissolved in the sprayable liquid, adhere to the reactor walls forming a very thin coating. However, part of the aqueous vehicle, flowing along the walls, gathers on the bottom of the reactor, carrying with it part of the inhibitor which is therefore lost to the purposes of its preventive action on the formation of the build-up. In addition to this economic loss , a technical difficulty occurs. In fact, the build-up inhibitors which have not adhered to the wall can interfere with the quality of the acetate or vinyl chloride polymers and copolymers obtained during a subsequent polymerization, e.g. deteriorated colour, decreased thermostability, and can also interact negatively with the initiator, suspending and dispersing agents and emulsifiers, used in the polymerization processes, causing the formation of anomalous lumps of particles and instability of the polymerization system. SUMMARY OF THE INVENTION It has now been found that if the phenol/formaldehyde condensation products, such as for example those cited in EP 0052421 and in JP-A-54-107991 are prepared in the presence of suitable carboxylation agents, or subsequently reacted with suitable carboxylation agents, a chemical modification of these condensates occurs, on the nature of which modification only hypotheses can be made being not even completely explained the structure of the starting precondensate which gives to the new products an improved adhesion capacity to the reactor walls and a higher specific anti build-up activity, with reduced sensitivity to pH variations of the polymerization processes. Moreover, the polymers obtained from polymerization carried out in reactors with such protected walls, show better physical characteristics. Therefore the present invention relates to the following objects: a) a build-up suppressor agent; b) compositions containing said agent; c) a method for inhibiting the build-up in a polymerization reactor; d) a polymerization process; and e) a polymer obtainable from said process. DETAILED DISCLOSURE OF THE INVENTION The phenol compound suitable for the present invention must have the ortho- and para-positions to the phenol function unsubstituted. The carboxylation agents useful for the purposes of the present invention are preferably aliphatic organic acids containing at least two carboxyl groups, as for example, one or more of oxalic, malonic, succinic acids, or carboxyl groups and hydroxyl groups, as for example citric and tartaric acids. Particularly suitable is citric acid. This improved specific activity can moreover be further enhanced if the above mentioned products include polyvinyl alcohols having high hydroxyl content. The molar ratio between the phenol compound and formaldehyde is between 1:0.8 and 1:1.2. The molar ratio between the starting phenol compound and the organic acid used in the present invention is between 1:1.5 and 1:0.5. Preferred phenol compounds are phenol and alpha-naphthol. The reaction between the polycarboxylic acids, phenols and formaldehyde, or between the polycarboxylic acids and pre-condensates between the phenols and the formaldehyde and, when used, the polyvinyl alcohols, takes place normally between 50 and 100°C, preferably between 75 and 95°C, in an aqueous solution. The reaction can be carried out also in situ , i.e. on the walls of the reactor or on any other part of the reactor that can come in contact with the vinyl acetate or chloride or with other polymerizable monomers, if any, also in their vapour form. The polyvinyl alcohols suitable to the present invention are polyvinyl alcohols having a hydrolysis degree equal to or higher than 96%, preferably 98% or more, and having a viscosity, in 4% aqueous solution, determined with Hoppler viscosimeter, of 20 mPa.s or more, preferably 40 mPa.s or more. The amount of polyvinyl alcohol to be used in the manufacture of these new build-up suppressor agents is between 2% and 20% by weight, based on the weight of the phenol-formaldehyde condensation product. According to the present invention, the build-up suppressor agents are obtainable in various ways. The phenol compound may be reacted directly with formaldehyde in the above mentioned conditions in the presence of the carboxylation agent. Alternatively, the formation of the condensate is carried out by reacting the phenol compound and formaldehyde in alkaline conditions, e.g, a pH of between 8 and 12, and subsequently the condensate is treated with the carboxylation agent. In the case the above mentioned polyvinyl alcohol is used, the condensation between the phenol compound and formaldehyde takes place in the presence of the polyvinyl alcohol in alkaline conditions, e.g. a pH of between 8 and 12, and finally the reaction with said carboxylation agent is carried out. In the case of in situ preparation of the build-up suppressor agent, it is obtained in the form of a 4% w/w aqueous solution. With respect to the already mentioned advantages, namely better adhesion of the suppressor agents and the non interference with the quality of the polymers to be made, the new build-up suppressor agents also have the advantage of being easily obtained in solid, handy and easily preservable form. As opposed to this, the well known phenol-formaldehyde derivatives, particularly those described in EP 0 052 421, are obtainable only in the form of a solution, which must be stored in a manner such as to be shielded from air. Atmospheric oxygen quickly oxides these known solutions, giving them a deep colour, probably corresponding to the quinone form of the phenols contained therein and transforming the phenol-formaldehyde condensates into water insoluble products which are, therefore, no longer useful. Such rapid oxidation does not takes place on the present solid product, obtained according to the present invention. The solution suitable for application on the reactor walls can be prepared at the moment of use by dissolving the product in water and alkali, e.g. a pH of between 8 and 13, which operation is very easy due to the presence of the carboxyl groups. The concentration of the suppressor agents in the aqueous solution for use in the application on the reactor walls is between 3 and 15%, preferably between 5 and 9% by weight of the solution. The amount of the build-up suppressor agents of the present invention which is to be applied on the reactor walls is particularly low, up to not more than 0.4 g of active substance per m 2 of surface and as low as 0.04 g per m 2 of surface. The product, after being dissolved by means of alkali as for example sodium hydroxide, potassium hydroxide or hydroxides of alkali-earth metals or also by means of ammonia or lower aliphatic amines or mono-di-tetraethanolamine, is generally applied by means of the known vapour-spraying technique, but can also be applied by brush or, in the case of vinyl chloride, using the monomer itself as a carrier. The application can be carried out on hot or cold walls, using pre-warmed or room temperature solutions, although the temperature is not critical. The vinyl acetate and vinyl chloride polymerizations which are referred to in the present invention are homopolymerizations or copolymerizations with one or more copolymerizable monomers as for example other vinyl esters or aryl, alkyl, cycloalkyl esters of mono or polycarboxylic unsaturated acids having 3-15 carbon atoms. The process of the invention is particularly useful when applied to polymerizations in aqueous suspension or emulsion, but also in bulk polymerizations the reduction of the build-up on the walls occurs. In the suspension polymerizations of vinyl acetate and chloride, suspending agents with colloidal-protective properties are used, as for instance partially hydrolyzed polyvinyl alcohols, cellulosic ethers, gelatine, fatty acids esters of sorbitole. The amounts used are generally between 0.05% and 2% by weight on the total amount of the monomers. In the emulsion polymerizations, surfactants as polyglicolic ethers of the nonyl-phenol or sodium or ammonium salts of C 12 -C 18 fatty acids, alkylphosphates, alkylsulfosuccinates, sulfonated alkylbenzenes, sulfonated olefins, sulfuric esters of fatty alcohols are used as emulsifying agents. The amounts generally vary between 0.05% and 0.5% by weight based on the total of the monomers. Any suitable polymerization initiator which is soluble in the vinyl monomers can be used. Examples of these catalysts, in the suspension polymerizations, are peroxides such as lauroyl peroxide, acetylcyclohexylsulfonyl peroxide, azo compounds such as azo-bis(dimethylvaleronitrile) and peroxodicarbonates such as dicetylperoxodicarbonate, diisopropylperoxodicarbonate. These initiators and every other conventional agent can be used in the usual amounts of 0.01%-1% w/w, based on the total amount of the monomers. In emulsion polymerization, oleosoluble initiators, such as diacyl or dialkyl peroxides, as lauroyl or benzoyl peroxide, per-esters such as the t-butyl peroxypivalate or t-butyl per-2-ethylhexanoate, peroxidicarbonate or dicetyl peroxidicarbonate or hydrosoluble redox initiating systems based on persulfates, hydrogen peroxide, hydroperoxides combined with sodium metabisulfite, sulfoxylated sodium formaldehyde can be used. Polymerization operative conditions are those well known and commonly used for the vinyl acetate and chloride emulsion and suspension polymerization. The temperatures are within the range 40-80°C and the pressure is generally between 5 and 14 bar for the vinyl chloride and between 65 and 95°C and at atmospheric pressure for vinyl acetate. The following examples further illustrate the invention. EXAMPLE 1 Preparation of build-up suppressor agents. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 500 1-naphthol (equal to 0.7 moles) 100 polycarboxylic aliphatic acid 0.6 moles The suspension was warmed to 98°C and stirred for three hours at this temperature. Subsequently, 70 parts by weight of 30% formaldehyde were added within 70 minutes and the temperature was maintained for three hours. At the end, the mixture was cooled down to 25°C and the solid was recovered by filtration. According to this process, the products derived from the following acids were prepared: oxalic acid (Example 1A) malonic acid (Example 1B) succinic acid (Example 1C) citric acid (Example 1D) tartaric acid (Example 1E) EXAMPLE 2 Preparation of build-up suppressor agents. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 600 1-naphthol (equal to 0.7 moles) 110 30% caustic soda 93 The suspension was warmed to 80°C till to obtain a solution. Subsequently, 80 parts by weight of 30% formaldehyde were added within about 70 minutes, raising the temperature to 95°C and stirring for a further hour . Then, 0.55 moles of polycarboxylic aliphatic acid were added and the mixture was warmed at 95°C for further two hours. At the end, the mixture was cooled down to 25°C and the solid was recovered by filtration. According to this process, the products derived from the following acids were prepared: oxalic acid (Example 2A) malonic acid (Example 2B) succinic acid (Example 2C) citric acid (Example 2D) tartaric acid (Example 2E) EXAMPLE 3 Preparation of build-up suppressor agents. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 500 phenol 66 (equal to 0.7 moles) polycarboxylic aliphatic acid 0.6 moles The suspension was warmed to 98°C and stirred for three hours at this temperature. Subsequently, 70 parts by weight of 30% formaldehyde were added within 70 minutes and the temperature was maintained for three hours. At the end, the mixture was cooled down to 25°C and the solid was recovered by filtration. According to this process, the products derived from the following acids were prepared: oxalic acid (Example 3A) malonic acid (Example 3B) succinic acid (Example 3C) citric acid (Example 3D) tartaric acid (Example 3E) EXAMPLE 4 Preparation of build-up suppressor agents. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 600 phenol (equal to 0.7 moles) 66 30% caustic soda 93 The suspension was warmed to 90°C till to obtain a solution. Subsequently, 80 parts by weight of 30% formaldehyde were added within about 90 minutes, maintaining the temperature at 90°C and stirring for a further hour . Then, 0.55 moles of polycarboxylic aliphatic acid were added and the mixture was warmed at 95°C for further two hours. At the end, the mixture was cooled down to 25°C and the solid was recovered by filtration. According to this process, the products derived from the following acids were prepared: oxalic acid (Example 4A) malonic acid (Example 4B) succinic acid (Example 4C) citric acid (Example 4D) tartaric acid (Example 4E) EXAMPLE 5 Polymerization of vinyl acetate monomer (VAM) in aqueous suspension. In a stainless steel 25 liter-reactor, equipped with a reflux condenser and anchor stirrer, the following ingredients were loaded in parts by weight: VAM 100 Water 50 PVOH (26/88) 0.05 Acetaldehyde 0.4 Sodium acetate 0.01 Benzoyl peroxide 0.03 The mixture was warmed to reflux at atmospheric pressure and the polymerization was carried out for 4 hours until a conversion not lower than 99% was reached. According to this procedure several polymerizations were carried out with and without the build-up suppressor agents of the present invention being present. The agents were applied in the amount of 0.3 g of active matter per m 2 of reactor surface. The build-up amount was determined after emptying and washing the reactor, collecting and weighing it. The obtained results are reported in the following Table 1, and are expressed as part per million (ppm) referred to the loaded monomers. Example Coating type Application mode Build-up (ppm) 5A none --- 12,000 5B 1C spray 515 5C 1B spray 1,750 5D 2B spray 975 5E 1D spray 10 5F 4D spray 110 5G 2C spray 215 5H 2E spray 80 5I 4C spray 1,600 5L 3B spray 2,010 5M 2A spray 875 5N 2D vapour 10 5O 1E vapour 175 5P 3D vapour 425 EXAMPLE 6 polymerization of vinyl chloride monomer (VCM) in aqueous suspension. In a internally glass lined 100 liter-reactor, equipped with Pfaudler stirrer, after having eliminated oxygen, the following ingredients were loaded in parts by weight: VCM 100 Water 150 Polyvic S 404 W® 0.04 Polyvic SP 808® 0.04 Methylhydroxypropylcellulose 0.04 Sodium hydrogencarbonate 0.03 Bis(4-tert-butylcyclohexyl)peroxy dicarbonate 0.04 The system was warmed to 54°C, corresponding to a K value of the PVC polymer of about 70, while the pressure raised to 7-8 metric atmospheres and the polymerization was carried out for about 7 hours. When the pressure decreased of 2-3 metric atmospheres, the reaction was interrupted venting out the unreacted monomer and recovering it. According to this procedure several polymerizations were carried out with and without the build-up suppressor agents of the present invention being present. Moreover, further two polymerizations were carried out but using as build-up suppressing agents the products disclosed in Example 1 of EP 0052421 (herein Examples 6H and 6I). The build-up suppressors were applied in the amount of 0.25 g of active matter per m 2 of reactor surface. The build-up amount was determined after emptying and washing the reactor, collecting and weighing it. The obtained results are reported in the Table 2 below and are expressed as part per million (ppm) referred to the loaded monomer. Example Coating type Application mode Build-up (ppm) 6A none --- 6,500 6B 2D spray traces 6C 2E spray 25 6D 4D spray 75 6E 4E spray 80 6F 1D spray traces 6G 2B spray 215 6H EP0052421 spray 530 6I EP0052421 vapour 310 PVCs obtained from Examples 6A, 6B, 6H, 6I was stabilized against thermo-oxidative degradation with calcium and zinc stearate and were pressure-molded into plates having 1.5 mm thickness. The yellow index (YI) of the plates was measured with a reflection spectrophotometer obtaining the values reported in Table 3 below: Example YI 6A 7.8 6B 7.7 6H 10 6I 10.5 The polymers obtained according to the present invention showed better appearance. EXAMPLE 7 Copolymerization of vinyl acetate monomer (VAM)/Vinyl esters in aqueous dispersion. In a stainless steel 25 liter-reactor, equipped with a reflux condenser and anchor stirrer, the 30% of the monomer mixture below described and the 50% of the redox initiator system were loaded in parts by weight: VAM 70 Dibutyl maleate 30 Water 70 Hydroxyethylcellulose (WP 300) 2 Ethoxylated nonyl-phenol 2.3 NaHCO 3 0.07 tert-Butylhydroperoxide 0.18 Sodium formaldehyde sulfoxilate 0.089 The mixture was warmed to reflux at atmospheric pressure and the remaining of the matter was loaded within 5 hours at the temperature of 85°C. After completion of the reaction, cooling and unloading of the reactor, the latter was washed with water at 5 metric atmospheres. According to this procedure several polymerizations were carried out with and without the build-up suppressor agents of the present invention being present. The agents were applied in the amount of 0.35 g of active matter per m 2 of reactor surface. The build-up amount was determined after emptying and washing the reactor, collecting and weighing them. The obtained results are reported in the following Table 4, and are expressed as part per million (ppm) referred to the loaded monomers. Example Coating type Application mode Build-up (ppm) 7A none --- 21,000 7B 2D spray 60 7C 1E spray 220 EXAMPLE 8 Copolymerization of vinyl chloride monomer (VCM)/vinyl acetate monomer (AVM) in aqueous suspension. In a internally glass lined 100 liter-reactor, equipped with Pfaudler stirrer, after having eliminated oxygen, the following ingredients were loaded in parts by weight: VCM 85 AVM 15 Water 150 Polyvic S 404 W® 0.07 Polyvic SP 808® 0.2 Gohsenol KH17® 0.03 Sodium hydrogencarbonate 0.05 Bis(4-tert-butylcyclohexyl)peroxy dicarbonate 0.025 Lauroyl peroxide 0.04 The system was warmed to 62°C, corresponding to a K value of the VCM/VAM copolymer of 58. The polymerization was carried out for about 8 hours until an 85% monomer conversion was achieved. According to this procedure several polymerizations were carried out with and without the build-up suppressor agents of the present invention being present. The agents were applied in the amount of 0.4 g of active matter per m 2 of reactor surface. The results are reported in Table 5 below. Example Coating type Application mode Build-up (ppm) 8A none --- 15,750 8B 3D spray 15 8C 1E spray 275 EXAMPLE 9 In-situ preparation of a build-up suppressor agent. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 600 l-naphthol (equal to 0.7 moles) 110 30% caustic soda 93 The suspension was warmed to 80°C to obtain a solution. Subsequently, 80 parts by weight of 30% formaldehyde were added within 70 minutes raising the temperature to 95°C and stirring was maintained for one hour. The obtained solution, having a solid content of about 20%, was diluted with water till 4% solid content and was added with 0.5 moles of citric acid, keeping pH at 11/13 with sodium hydroxide. The new solution was sprayed by nitrogen pressure on a 25 liter-reactor walls, which were kept at 90°C by heating the reactor jacket, in the amount of 0.4 mg/m 2 . In the coated reactor a polymerization of the VAM was carried out according to the procedure of the example 5. The build-up collected according to the usual method was 220 ppm. In the so treated reactor, the polymerization of vinyl acetate monomer was carried out according to the procedure of Example 5. The amount of build-up collected was 220 ppm. EXAMPLE 10 Preparation of a build-up suppressor agent. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 500 1-naphthol (equal to 0.7 moles) 100 Sodium hydroxide 22 The suspension was warmed to 98°C and stirred for three hours at this temperature. Subsequently, 70 parts by weight of 30% formaldehyde were added within 70 minutes and the temperature was maintained for three hours. At the end, the mixture was cooled down to 25°C and 140 parts by weight of a 10% water solution of PVAOH (Polyvinylalcohol) having a saponification degree of 98% and a viscosity of a 4% aqueous solution of 40 mPa.s were added. After a maturation period of three hours at 90°C the system was cooled to 80°C, added with 0.6 moles of polycarboxylic acid and warmed for further two hours. The formed suspension was cooled and the solid was recovered by filtration and dried. According to this process, the products derived from the following acids were prepared: oxalic acid (Example 10A) malonic acid (Example 10B) succinic acid (Example 10C) citric acid (Example 10D) tartaric acid (Example 10E) EXAMPLE 11 Preparation of build-up suppressor agents. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 600 phenol (equal to 0.7 moles) 66 30% Sodium hydroxide 93 The suspension was warmed to 90°C to obtain a solution. Subsequently, 80 parts by weight of 30% formaldehyde were added within 90 minutes always keeping the temperature at 90°C and stirring was maintained for one hour. At the end, the mixture was cooled down to 25°C and 90 parts by weight of a 10% water solution of a PVAOH having a saponification degree of 96% and a 4% solution viscosity of 30 mPa.s were added. After a maturation period of three hours at 90°C the system was cooled. 0.55 moles of polycarboxylic aliphatic acid were added and the system was warmed to 95°C for further two hours. The formed suspension was cooled to 25°C and the solid was recovered by filtration. According to this process, the products derived from the following acids were prepared: oxalic acid (Example 11A) malonic acid (Example 11B) succinic acid (Example 11C) citric acid (Example 11D) tartaric acid (Example 11E) EXAMPLE 12 Polymerization of vinyl acetate monomer (VAM) in aqueous suspension. In a stainless steel 25 liter-reactor, equipped with a reflux condenser and anchor stirrer, the following ingredients were loaded in parts by weight: VAM 100 Water 50 PVOH (26/88) 0.05 Acetaldehyde 0.4 Sodium acetate 0.01 Benzoyl peroxide 0.03 The mixture was warmed to reflux at atmospheric pressure and the polymerization was carried out for 4 hours until a conversion not lower than 99% was reached. According to this procedure several polymerizations were carried out with and without the build-up suppressor agents of the present invention being present. The agents were applied in the amount of 0.3 g of active matter per m 2 of reactor surface in the form of 5% solution in 1% aqueous sodium hydroxide. The solution were applied by whether nitrogen or vapour spraying. Build-up amount was determined after emptying and washing the reactor, collecting and weighing them. The obtained results are reported in the following Table 6, and are expressed as part per million (ppm) referred to the loaded monomers. Example Coating type Application mode Build-up (ppm) 12A none --- 15,000 12B 10C spray 485 12C 10B spray 1,520 12D 11B spray 1,020 12E 10D spray not detectable 12G 11C spray 250 12H 11E spray 75 12M 11A spray 830 12N 11D vapour not detectable 12O 10E vapour 160 12P 10A vapour 350 EXAMPLE 13 Polymerization of vinyl chloride monomer (VCM) in aqueous suspension. In a internally glass lined 100 liter-reactor, equipped with Pfaudler stirrer, after having eliminated oxygen, the following ingredients were loaded in parts by weight: VCM 100 Water 150 Polyvic S 404 W 0.04 Polyvic SP 808 0.04 Methylhydroxypropylcellulose 0.04 Sodium hydrogencarbonate 0.03 Bis(4-tert-butylcyclohexyl)peroxy dicarbonate 0.04 The system was warmed to 54°C, corresponding to a K value of the PVC polymer of about 70, while the pressure raised to 7-8 metric atmospheres and the polymerization was carried out for about 7 hours. When the pressure decreased of 2-3 metric atmospheres, the reaction was interrupted by exhausting the non reacted monomer and recovering it. According to this procedure several polymerizations were carried out with and without the build-up suppressor agents of the present invention being present. Moreover, further two polymerizations were carried out but using as build-up suppressing agents the products disclosed in Example 1 of EP 0052421 (herein Examples 13H and 13I), The build-up suppressing agents were applied in the amount of 0.25 g of active matter per square meter of surface after having prepared 5% solutions in 1% aqueous sodium hydroxide. The solutions were sprayed on the walls by whether nitrogen or vapour spraying. The results are reported in Table 7 below. Example Coating type Application mode Build-up (ppm) 13A none --- 7,200 13B 11D spray not detectable 13C 11E spray 35 13D 10B spray 95 13E 10E spray 70 13F 10D spray not detectable 13G 11B spray 255 13H EP0052421 spray 420 13I EP0052421 vapour 350 PVC obtained from Examples 13A, 13B, 13H, 13I was stabilized against thermo-oxidative degradation with calcium and zinc stearate and were pressure-molded into plates having 1.5 mm thickness. Yellow index (YI) of the plates was measured with a reflection spectrophotometer obtaining the values reported in Table 8 below: Example YI 13A 7.6 13B 7.8 13H 9.5 13I 10 The polymers obtained according to the present invention showed better appearance. EXAMPLE 14 In-situ preparation of a build-up suppressor agent. In an internally glass lined reactor, equipped with a reflux condenser, a Pfaudler stirrer, cooling and warming system, the following ingredients were loaded in parts by weight: water 600 1-naphthol (equal to 0.7 moles) 110 30% caustic soda 93 The suspension was warmed to 80°C to obtain a solution. Subsequently, 80 parts by weight of 30% formaldehyde were added within 70 minutes raising the temperature to 95°C and stirring was maintained for one hour. The solution was cooled to 25°C and 90 parts by weight of a water solution containing 10% PVAOH, having a saponification degree of 98% and a viscosity of a 4% water solution of 40mPa.s, were added. After a maturation period of three hours at 90°C, the solution was cooled. The obtained solution was diluted with water till 4% solid content and was added with 0.5 moles of citric acid, keeping pH at 11/13 with sodium hydroxide. The new solution was sprayed by nitrogen pressure on a 25 liter-reactor walls, which were kept at 90°C by heating the reactor jacket, in the amount of 0.4 g of active matter per m 2 . In the so treated reactor, the polymerization of vinyl acetate monomer was carried out according to the procedure of Example 12. The amount of build-up collected was 50 ppm.

Claims: A build-up suppressor agent useful in vinyl acetate and/or vinyl chloride polymerization, comprising a condensation product of a phenol compound and formaldehyde, wherein the phenol compound has the ortho- and para-positions unsubstituted with respect to the phenol function, and a carboxylation agent. An agent according to claim 1, wherein the carboxylation agent is an organic aliphatic acid having at least two carboxyl groups. An agent according to claim 2, wherein the organic acid is selected from the group consisting of oxalic, malonic, succinic, citric and tartaric acid. An agent according to claim 3, wherein the organic acid is citric acid. An agent according to claim 1, wherein a molar ratio between the phenol compound and the carboxylation agent is between 1:1.5 and 1:0.5. An agent according to claim 1, wherein the phenol compound is phenol. An agent according to claim 1, wherein the phenol compound is alpha-naphthol. An agent according to claim 1, wherein the molar ratio between the phenol compound and formaldehyde is between 1:0.8 and 1:1.2. A method for producing the suppressor agent of claim 1, comprising condensing the phenol compound and the formaldehyde in the presence of the carboxylation agent at temperatures between 50 and 100°C. An agent according to claim 1, wherein the suppressor agent includes a polyvinyl alcohol having a hydrolysis degree not lower than 96% and a 4% water-viscosity not lower than 20 mPa.s. An agent according to claim 10, wherein the polyvinyl alcohol is present in an amount based on said condensation product of between 2 and 20% by weight. An agent according to claim 10, wherein the polyvinyl alcohol has a hydrolysis degree higher than or equal to 98% and 4% aqueous solution viscosity higher than or equal to 40 mPa.s. A method according to claim 9, wherein the phenol compound is condensed with the formaldehyde in the presence of said carboxylation agent. A method according to claim 9, wherein the phenol compound is condensed with the formaldehyde in alkaline conditions, and then treated with said carboxylation agent. An agent obtainable according to the method of claim 14. A method according to claim 9, wherein the phenol compound is condensed with the formaldehyde in alkaline conditions, polyvinyl alcohol is added thereto, and then treated with the carboxylation agent. An agent obtainable according to the method of claim 16. An agent according to claim 1, wherein the suppressor agent is in the form of a 4% w/w alkaline aqueous solution. A composition having anti build-up activity, containing the agent of claim 1 and a carrier therefor. A composition according to claim 19, in the form of an alkaline aqueous solution containing from 3 to 15% by weight of said agent. A method of treating vinyl acetate and/or vinyl chloride polymerization reactor surfaces such as to render the surfaces resistant to formation of build-up therein, comprising applying to said surfaces the suppressor agent of claim 1. A method according to claim 21, wherein an amount of said agent applied to the surfaces is not higher than 0.4 g per m 2 of surface to be treated. A polymerization or copolymerization process of vinyl acetate, vinyl esters or vinyl chloride monomers, comprising carrying out the process in a reactor treated according to the method of the claim 21.

Inventors: QUINTINI MASSIMO, QUINTINI, MASSIMO
Applicants: 3V SIGMA SPA, 3V SIGMA S.P.A
Application year: 1994
Main classification: C08F2
IPC codes: C08F2