A GLASS COMPOSITION

Abstract: A heat absorbing, neutral grey to green, soda-lime-silica glass having at 4 mm control thickness a light transmittance using illuminant A of 10.0 % to 60.0 %, ultraviolet transmittance less than 25.0 %, infrared transmittance is less than about 50.0 %, and the purity of excitation is less than 6.0 % which is produced from colourants consisting of 0.90 to 1.90 percent by weight total iron oxide as Fe2O3, 0.002 to 0.025 percent Co, 0.0010 to 0.0060 percent Se, and 0.1 to 2.0 percent TiO2. The flat glass products having such a composition is particularly suitable for use as a privacy glass or sun roof product in trucks and automobiles.

Description: A GLASS COMPOSITION This invention is directed to a heat absorbing, neutral grey-green coloured glass composition. More particularly, it comprises soda-lime-silica glass which uses titanium dioxide in combination with other colouring components which consist essentially of iron oxide, selenium and cobalt oxide to provide a particular excitation purity and colour to a glass composition. The majority of glass used in automotive vehicles, e.g., for the windshield and backlite, is green in colour and has heat absorbing properties. A glass of green colour is used because it coordinates well with a wide range of vehicle paint colours. It is desirable to have still other green or neutral grey-green glasses available which are similar in colour to such glass, yet in addition have lower infra red transmittance and lower total solar energy transmittance. This combination of properties would make these other glasses ideally suited be used as other windows of the vehicles, e.g., those back of the B-pillar or the sunroof while colour coordinating with the windshield glass. Such lower transmittance glasses would aid in reducing the heat gain in the vehicle interior while also providing privacy. Glass with these properties would be highly desirable -for not only automotive applications but for architectural use as well. It would further be desirable if the glass exhibited a broad range of visible transmittance and was also compatible with flat glass manufacturing methods. Those skilled in the art know that adding or substituting one colourant for another and/or changing the amount or relative proportion of colourants in a glass composition affects not only the colour of the glass, i.e., dominant wavelength and excitation purity, but also can affect the light transmission of the glass and its structural qualities. Furthermore, there is in many cases substantial complexity and unpredictability in these effects. Thus, for example, even if the proper alteration in the composition of a particular coloured glass were determined for achieving a desired colour shift, the same alteration, unfortunately, would also alter (for example, unacceptably reduce) the light transmission value of the glass. It may, of course, also undesirably alter the purity of the glass colour. In short, all these factors — dominant wavelength, purity and light transmission — are variable and may vary unpredictably with each other. In the case of heat absorbing glass, additional properties of ultraviolet transmittance and infra red transmittance are also to be considered. Developing a new glass composition, therefore, having a particular colour, certain low purity, appropriate light transmittance, ultraviolet transmittance and infra red transmittance, is in some cases very difficult. An experimental change in the amount or relative proportions of one or more colourants in a glass composition intended to bring one of these numerical values closer to a target value causes one or all of the other values simultaneously to drift off target (or further off target) . It is found that obtaining the desired glass composition embodying the present invention required maintaining the colouring components of iron oxide, selenium, cobalt oxide and titanium oxide within precise ranges. Grey coloured heat absorbing glasses relied, in the past, on the inclusion of nickel oxide as an active colouring agent. Nickel compounds, however, are known to react with other materials in soda-lime-silica glass and form nickel sulphide "stones" in the glass. These stones are usually small, thereby avoiding detection methods, but can produce an unacceptably high rate of breakage during tempering. U. S. Patent 5,023,210 to Krumwiede et. al. discloses the use of chrome oxide in combination with iron oxide, cobalt oxide and selenium to achieve a dark grey glass without nickel. U.S. Patent 3,300,323 to Plumat, et al. discloses a grey glass having colouring components: 0.05 to 0.5 wt. % Fe 2 0 3 , 2.0 to 6.0 wt. % Ti0 2 , 0.005 to 0.010 CoO, and optionally manganese oxide. The Plumat, et al. glass does not contain selenium, however, as required in the present invention and has higher visible transmittance and limited heat absorbing properties. Other heat absorbing grey glass compositions contain selenium as an essential colouring component. For example, U.S. Patent 4,873,206 to Jones discloses a grey glass composition which includes as the colourants only iron oxide, cobalt, and selenium. This composition, however, uses less iron oxide than this invention and has substantially higher infra-red and ultraviolet transmittance which limits the value as an automotive product. European Patent 0 482 535 to Longobardo, et al. , while using iron oxide, cobalt oxide, and selenium in forming a grey glass, specifically excludes titanium oxide which is considered a vital part of the present invention glass composition to ensure its neutral grey to green colour. The present invention is a glass composition that is heat absorbing, grey to green in colour and possesses less than 6% excitation purity. The composition in its broadest embodiment comprises 68 to 75% Si0 2 , 10 to 18% Na 2 0, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% A1 2 0 3 , and 0 to 5% K 2 0, where CaO + MgO is 6 to 15% and Na 2 0 + K 2 0 is 10 to 20%, with traces of -melting and refining aids, if any, and colourants consisting essentially of: 0.90 to 1.90 wt.% total iron oxide as Fe 2 0 3 ; 0.006 to 0.025 wt.% cobalt oxide as Co; 0.0010 to 0.0060 wt.% selenium as Se; and 0.10 to 2.0% titanium oxide as Ti0 2 . Glass products made according to the broadest embodiments of the invention have the following spectral properties at 4 mm control thickness: less than 6% excitation purity, 10.0 to 60.0% light transmittance using illu inant A (LTA) , less than 25.0% ultra violet transmittance, and less than 50.0% infra red transmittance. This glass has a dominant wavelength between about 480 and - 4 - 575.5 nanometres. Generally, as the quantities of the colourants increase, the % transmittance will go down. Similarly, generally as the glass thickness increases for a given glass composition, the transmittance of the thicker glass will decrease. While glass made according to the float glass process, which is the preferred process for making the present invention glass composition, is typically between 2.0 to 12.0 millimetres, the glass produced according to this invention is not meant to be so limited. Flat soda-lime-silica glass, used in the automotive and architectural industries and conveniently made by the float glass process, is generally characterised by the following basic composition shown in Table I, the amounts of the components being based on a weight percentage of the total glass composition: Table I Oxide Component Weight % sio 2 68 to 75 A1 2 0 3 0 to 5 CaO 5 to 15 MgO 0 to 10 Na 2 θ 10 to 18 κ 2 o 0 to 5 The neutral grey-green glass composition of the present invention employs this basic soda-lime-silica glass composition wherein further in the present invention composition CaO + MgO is 6 to 15% and Na 2 0 + K 2 0 is 10 to 20%. The basic glass compositions often contain an amount of iron oxide as an impurity depending on the trace amounts i .n the batch materi .als. Preferably, S0 3 i.n the i.nventi.on glass composition is 0.10 to 0.30 wt. %, more preferably 0.14 wt. % to 0.25 wt. %. In addition, the neutral grey- - 5 - green glass composition consists essentially of the following colouring components: iron oxide; cobalt oxide; selenium; and titanium dioxide. The total iron oxide as Fe 2 0 3 is present in the invention composition glass in quantities of 0.9 to 1.90 weight %. All weight percents disclosed herein are based on the total weight of the invention glass composition. The iron oxide incorporated in the composition lowers both the ultra violet and the infra red transmittance of the glass products. More particularly, the iron oxide performs two functions in this glass system: (1) the oxidised form of iron oxide (Fe 2 0 3 ) absorbs in the ultra violet portion of the spectrum providing low ultra violet transmittance, and (2) the reduced form of iron oxide (FeO) absorbs in the infra red portion of the spectrum and the resultant glass thus has a lowered infra red transmittance. Both absorbing functions of the iron oxide are especially valuable when the glass product is used in automobiles. When heat is absorbed by the glass, the load on air conditioners is initially reduced and there is less total heat in the vehicle to cool. Cobalt as Co is present as a colouring component in the glass composition in an amount of 0.002 to 0.025 wt. %, the cobalt functioning to absorb light from about 580 to 680 nanometres in the visible portion of the spectrum. The cobalt is generally included in the batch materials in the form of cobalt oxide (Co 3 0 4 ) . Selenium (Se) is present as a colouring component in an amount of 0.001 to 0.0060 wt. %, the selenium functioning to absorb light from about 430 to 540 nanometres of the visible spectrum. It is necessary to carefully balance the amount of absorption from selenium with that of cobalt oxide to achieve a neutral grey appearance. The desire and difficulty of this invention is to make glass products that are below 6.0 % excitation purity while simultaneously having a dominant wavelength between 480 and 575.5 nanometres, i.e, being grey to green in colour. As mentioned above, the importance of the present invention glass having a grey-green colour is that the majority of other truck and automotive glasses, used for example as the windshield, are a green to grey colour; therefore glass of this invention is desirably able to be used in a vehicle with these other green products since it is of similar colour. Glasses with a very low light transmittance (10 to 25% using illuminant A (LTA) ) are somewhat less dependent on the particular dominant wavelength because it is difficult to readily see through these glasses at 3.8 to 4.8 mm. thickness, typical window thicknesses, making their precise colour less discernable. However, for glasses of the present invention having LTAs that would optimally be used in vehicles (between 25 and 60% LTA) , it would be most desirable to have such glass appear to be of green colour by transmittance. The problem of precise colour control described above was solved by employing titanium dioxide in particular amounts between about 0.1 and 2.0 wt. %, in combination with the other colourants disclosed above, in the grey-green glass of the invention composition. To be the desired grey-green colour, the dominant wavelength using Illuminant C must be between 480 and 575.5 nanometres using the C. I. E. convention with a 2° observer. Titanium dioxide was found to shift the dominant wavelength within the range of 480 to 575.5 nanometres using Illuminant C while still allowing the maintenance of the other desired optical properties. Titanium dioxide as incorporated in the present invention glass composition, in addition to controlling the dominant wavelength of the glass compositions, performs two other important functions: (1) it absorbs light in the ultra violet portion of the spectrum, and (2) it aids in lowering the excitation purity of the glass product. In addition to having the required dominant wavelength disclosed, glass products within the scope of this invention have the following spectral properties when measured at 4.0 mm control thickness: less than 6% excitation purity, 10.0 to 60.0% light transmittance using illuminant A (LTA), less than 25.0% ultra violet transmittance, preferably less than about 10.0% when the glass has less than 35.0% LTA, and infra red transmittance is less than 50.0%. Generally as the glass transmittance at 4 mm. control thickness increases, the percent excitation purity desirably is lower to ensure a grey to green colour by transmission. As would be appreciated by those skilled in the art, processing aids are generally added to the glass batch during the melting and processing, e.g., to maintain the proper balance of redox conditions or as fining agents. For example, carbocite (anthracite coal) when added to the glass composition has the effect of reducing a portion of the Fe 2 0 3 to FeO to achieve lower infra red transmittance. Sodium and/or potassium nitrate are used in glass batches of the invention to maintain oxidising conditions early in the melting process which aids in selenium retention. Nitrates have been used by others to improve selenium retention. Careful balance must be maintained between the reducing conditions from the carbocite and the oxidising conditions from the nitrates used to improve selenium retention in the glass, because the oxidisers also act upon the iron oxide to shift the redox from FeO toward F 2 0 3 while carbocite shifts the iron oxide equilibrium in the opposite direction. Table II lists the preferred raw material batch ingredients for providing compositions according to embodiments of the present invention. Table II BATCH MATERIAL RANGE MASS (LBS.) Sand 1000 Soda Ash 290 to 320 Dolomite 215 to 260 Limestone 75 to 90 Salt Cake 8 to 18 Rouge 16 to 26 Titanium Dioxide 1.4 to 7.0 Sodium Nitrate 5 to 15 Carbocite (70% C) 0.3 to 1.0 Cobalt Oxide (72% Co) 0.25 to 0.36 Selenium 0.20 to 0.70 Table III contains the preferred ranges of resultant oxide constituents for my new glass compositions. Table III Oxide Component Weight % sio 2 71 to 74 A1 2 0 3 0.15 to 0.25 Fe 2 0 3 1.20 to 1.85 CaO 8.40 to 8.70 MgO 3.5 to 4.00 Na 2 0 13.00 to 13.80 κ 2 o 0 to 0.10 τio 2 0.10 to 0.50 so 3 0.14 to 0.25 Co (metal) 0.0130 to 0.0190 Se (metal) 0.0010 to 0.0040 The preferred glass compositions disclosed above, preferably have the following properties. Preferred Glass Property Ranges C4 mm. thick glass sheet) Visible Transmission (111. A) : 16-20 % Ultraviolet Transmission: 5-10 % Infrared Transmission: 8-19 % Total Solar Transmission: 12-20 % Dominant Wavelength: 488-560 nm. Excitation Purity: 0.0-6.0 % FeO/Total Iron Oxide as Fe 2 0 3 Ratio: 0.15-0.30 Certain preferred embodiments of the invention composition glass were made from the batch ingredients (in grams) listed in the table directly below. The compositions were made according to the following procedure. The batches were weighed (typically about 170 grams total) on a laboratory balance and mixed with in a glass jar with a laboratory shaker for 10 minutes each. Each mixed batch was placed into a platinum-rhodium crucible which is about 2" tall with about a 2.5" inside diameter and 4.5 ml. of water is mechanically mixed into the raw batch. Crucibles were placed into a natural gas/air furnace pre-heated to 2600° F with 3 to 5 other crucibles. Furnace temperature recovered to 2600° F in about 30 minutes. After two hours melting, each. crucible was removed in turn, glass in the crucible was fritted by quenching in cold water, and the fragments were mixed in the crucible and all crucibles were returned to the furnace. Furnace temperature was brought back to 2600° F and the fritting procedure was repeated as above once the operating temperature was attained, about 45 minutes. All glass samples were melted for another 3 hours and each sample was poured into a 2.5" inside diameter graphite mould to shape the glass samples for subsequent grinding and polishing. All samples were placed into an annealing furnace, brought up to 1050° F, held for 4 hours, then allowed to slowly cool to room temperature in about 16 hours. Samples were ground and polished and spectral properties were measured on each sample; spectral properties were calibrated to a control thickness of 4 mm. Samples were then chemically analysed via X-ray fluorescence or other tests conducted as needed. Spectral properties of the compositions are also listed in the table. Table IV Example Example Example Example Example 1 2 3 4 5 Sand 100.76 100.00 100.78 100.00 100.00 Soda Ash 31.65 31.41 31.65 31.41 31.41 Limestone 7.30 7.25 7.31 7.25 7.25 Dolomite 26.03 25.83 26.03 25.83 25.83 Salt Cake 1.1043 1.0971 1.1052 1.0961 1.0952 Sodium Nitrate 0.5234 0.5226 0.5239 0.5204 0.5203 Rouge 1.6906 2.1031 1.6911 2.5430 2.1042 Carbocite 0.0917 0.0913 0.0925 0.0914 0.0918 Cobalt Oxide 0.0344 0.0302 0.0345 0.0266 0.0338 Selenium 0.1341 0.0699 0.0993 0.0646 0.0839 Titanium Dioxide 0.6786 0.2496 0.6784 0.5298 0.5298 % LTA 18.9 17.8 19.0 18.9 18.2 % UV 9.2 7.3 9.9 5.3 7.8 ' % IR 18.5 13.5 18.0 9.5 14.5 % TSET 18.8 15.1 18.6 12.8 16.0 Dominant Wavelength 500.9 559.0 487.9 544.1 490.5 Excitation Purity, % 1.3 3.8 4.0 4.9 5.2 In the tables here, % LTA is defined to be the luminous transmittance measured under CIE standard illuminant A. The % UV is the % ultra violet transmittance measured between 280 and 400 nanometres while the % IR is the % infra red transmittance measured over the range of 720 to 2120 nanometres. The % TSET is the % total solar energy transmittance as defined in U. S. Patent # 4,792,536 by the equation: %TSET = 0.44 %LTA + 0.53 %IR + 0.03 %UV. Still other embodiments of heat absorbing glasses within the scope of this invention, which display a wide range of % LTA, are listed in Table V based on their batch ingredients (grams) . The table also lists the resultant glasses spectral properties. - 13 Table V Example Example Example Example Example 6 7 8 9 10 Sand 100.76 100.79 100.99 100.00 100.00 Soda Ash 31.65 31.65 31.72 31.41 31.41 Limestone 7.30 7.31 7.32 7.25 7.25 Dolomite 26.03 26.03 26.08 25.83 25.83 Salt Cake 1.1047 1.1036 1.1068 1.0960 1.0961 Sodium Nitrate 0.5228 0.5244 0.5249 0.5204 0.5202 Rouge 2.1195 2.1200 1.4003 1.3810 1.3810 Carbocite 0.0916 0.0922 0.0922 0.0913 0.0914 Cobalt Oxide 0.0390 0.0366 0.0194 0.0095 0.0038 Selenium 0.1266 0.0919 0.0708 0.0210 0.0210 Titanium Dioxide 0.2525 0.2530 0.6782 0.5259 0.5259 % LTA 12.6 15.0 34.1 49.2 59.6 % UV 5.6 6.7 17.9 23.9 27.0 % IR 12.5 13.3 22.5 23.4 26.7 % TSET 12.6 14.0 27.0 33.1 38.5 Dominant Wavelength 570.7 527.9 497.8 497.9 547.5 Excitation Purity, % 4.4 1.2 2.3 3.6 3.8 The glass compositions made within the scope of this invention and listed in Table VI show the manner in which titanium dioxide changes the composition's dominant wavelength and excitation purity. In the table, the batch ingredients (in grams) used to make the glass composition as well as their spectral properties are listed. - 14 - Table VI Example Example Example 11 12 13 Sand 100.00 100.00 100.00 Soda Ash 31.41 31.41 31.41 Limestone 7.25 7.25 7.25 Dolomite 25.83 25.83 25.83 Salt Cake 1.0966 1.0967 1.0969 Sodium Nitrate 0.5203 0.5208 0.5209 Rouge 2.0968 2.1006 2.1047 Carbocite 0.0915 0.0916 0.0911 Cobalt Oxide 0.0327 0.0318 0.0337 Selenium 0.0841 0.0843 0.0840 Titanium Dioxide 0.0 0.2497 0.5304 % LTA 19.4 19.1 18.3 % UV 10.7 9.2 7.7 % IR 13.4 13.8 16.3 % TSET 16.1 15.9 17.1 Dominant Wavelength 484.6 492.0 541.4 Excitation Purity, % 9.3 3.7 1.8 1 In Examples 11, 12, and 13 of Table VI essentially all of the batch quantities are similar in amount except for the titanium dioxide. Analysis of these glasses for Ti0 2 showed 0.013 wt. % Tiθ 2 in Example ll (which is from trace amounts in the sand source), 0.19 wt. % Tio 2 in Example 12 and 0.39 wt. % Tiθ 2 in Example 13. Example 11 is not within the scope of this invention because it does not contain added titanium dioxide within that required in the invention nor is the excitation purity low enough to be considered part of this invention. However, Examples 12 and 13 demonstrate the improvement that titanium dioxide adds to the batch to lower excitation purity and shift the dominant wavelength. Examples 11 through 13 also demonstrate the improvements in lowering the ultra violet transmittance as provided by the titanium dioxide enhanced Examples 12 and 13 glasses of this invention.

Claims: - 16 - CLAIMS 1. A heat absorbing, neutral grey to green coloured glass composition having a base glass composition comprising: 65 to 75% Siθ 2 , 10 to 18% Na 2 θ, 5 to 15% CaO, 3 to 5% MgO, 0 to 5% A1 2 0 3 , and 0 to 5% K 2 0 with traces of melting and refining aids, if any, and colourants consisting essentially of: 0.90 to 1.90 wt.% total iron oxide as Fe 2 0 3 ; 0.002 to 0.025 wt.% cobalt oxide as Co; 0.0010 to 0.0060 wt.% selenium as Se; and 0.1 to 2.0% titanium oxide as Ti0 2 , the glass at 4 mm. control thickness having light transmittance using illuminant A of 10.0% and 60.0%, ultra violet transmittance less than 25.0%, infra red transmittance is less than about 50.0%, dominant wavelength with illuminant C between 480 and 575.5 nanometres, and an excitation purity of less than 6.0 %. 2. A glass composition according to claim 1, wherein S0 3 present in said composition is about 0.1 to 0.3 wt. %. 3. A glass composition according to claim l, wherein said visible transmission is between about 16-20%. 4. A glass composition according to claim 1, wherein said ultraviolet transmission is about 5-10 % and said infrared transmission is about 8-19%. 5. A glass composition according to claim 1, wherein said dominant wavelength is about 488-560 nanometres. 6. A glass composition according to claim 1, wherein the FeO/total iron oxide as Fe 2 0 3 is 0.15 to 0.30. 7. A heat absorbing, neutral grey to green coloured glass composition having a base glass composition comprising: 65 to 75% Si0 2 , 10 to 18% Na 2 θ, 5 to 15% CaO, 3 to 5% MgO, 0 to 5% A1 2 0 3 , and 0 to 5% K 2 0 with traces of melting and refining aids, if any, and colourants consisting essentially of: 1.2 to 1.85 wt.% total iron oxide as Fe 2 0 3 ; 0.0130 to 0.0190 wt.% cobalt oxide as Co: 0.0010 to 0.0040 wt.% selenium as Se; and 0.10 to 0.50% titanium oxide as Ti0 2 ; the glass at 4 mm. control thickness having light transmittance using illuminant A of 16.0% and 20.0%, ultra violet transmittance less than 10.0%, infra red transmittance is less than about 19.0%, dominant wavelength with illuminant C between 488 and 560 nanometres, and an excitation purity of less than 6.0 %. 8. Glass useful for automotive or architectural glazings made from the composition of any one of the preceding claims. 9. Glass useful for automotive or architectural glazings made from the composition of any one of claims 1 to 7.

Inventors: JONES JAMES VICTOR, JONES, JAMES, VICTOR
Applicants: FORD MOTOR CO, FORD MOTOR COMPANY, FORD MOTOR COMPANY LIMITED
Application year: 1994
Main classification: C03C3
IPC codes: C03C3, C03C4