Thermosetting silicone composition

Abstract: The thermosetting silicone composition of the instant invention is comprised of (a) a diorganopolysiloxane containing alkenyl groups, (b) an organohydrogenpolysiloxane, (c) a platinum catalyst-containing silicone resin fine particle catalyst comprised of (i) a thermoplastic silicone resin containing 5 to 90 moles% PhSiO 3/2 siloxane units and 5 to 20 mole% MeViSiO 2/2 siloxane units, wherein Ph denotes phenyl, Me denotes methyl and Vi denotes vinyl; said resin having a glass transition point of 40 to 70°C and (ii) 0.05 to 2 wt% as platinum atoms of a platinum catalyst; and (d) a hydrosilation reaction inhibiting compound. The thermosetting silicone compositions have excellent storage stability at about room temperature, and cure at a fast rate when heated.

Description: Several platinum catalyst-containing thermoplastic resin fine particle catalysts are known as curing acceleration catalysts for silicone compositions which cure by a hydrosilation reaction. Thus, the prior art is represented by US-A 4,481,341; US-A 4,766,176; JP-A 64-47442; JP-A 64-51140; US-A 5,015,691. However, these organic thermoplastic resin fine particle catalysts are inferior in heat resistance. Further, they have disadvantages in silicone compositions as a curing acceleration catalyst due to inferior mechanical properties and discoloration. These problems are caused when heated for curing and/or when exposed to high temperatures after curing. As a solution to this problem, platinum catalyst-containing thermoplastic silicone resin catalysts have been applied. For example, in JP-A 53-41707 and US-A 4,481,341, methods have been proposed to produce a silicone resin fine particle catalyst by mechanically grinding cured mixtures of a platinum catalyst and a silicone resin. Although these methods are effective for relatively low activity platinum catalysts, such as a 2-ethylhexanol solution of chloroplatinic acid or isopropyl alcohol-modified chloroplatinic acid, they are barely effective to inhibit catalyst activity when applied to high activity platinum catalysts. Furthermore, it is difficult to obtain fine particle catalysts of less than 10 µm in average particle size by these methods. Therefore, when used as a acceleration catalyst for silicone compositions, the requisite catalyst diffusion during the thermal curing reaction is not sufficient. This is a problem in that cure of the silicone composition may not be complete. Additional silicone resin catalysts containing high activity platinum catalysts are described in EP-A 0347895; US-A 5,017,654; JP-A 4-46962. In, EP-A 0347895 the resin containing the high activity platinum catalyst is pulverized to fine particles, and then the platinum catalyst existing on the surface is removed by washing. The catalyst activity is thereby suppressed at the surface. The high activity catalyst is then released by heating. US-A 5,017,654 and JP-A 4-46962 describe silicone compositions which cure quickly by the combined use of platinum catalyst-containing silicone resin fine particle catalyst and a particular kind of compound. By these methods, it is possible to manufacture thermosetting silicone compositions that can be stored stably at room temperature over a long period of time, and that quickly completes curing. Yet, the essential characteristics of the silicone compositions are not impaired. However, it remains difficult to control the curing rate and storage stability by these methods. Further, the storage stability is degraded with increasing the curing rate, and the curing rate is reduced with increasing the storage stability. It has now been found that when a special mixture of thermoplastic silicone resins is used to produce a platinum catalyst-containing silicone fine particle catalyst, it is possible to control the releasing temperature of the platinum catalyst when heated, so that it is possible to control both the curing rate and the storage stability. Therefore, the present invention introduces a thermosetting silicone composition which is excellent in storage stability in the vicinity of room temperature, and which is fast in the curing rate when heated. The thermosetting silicone compositions of the instant invention are comprised of (a) a diorganopolysiloxane containing alkenyl groups; (b) an organohydrogenpolysiloxane; (c) a platinum catalyst-containing silicone resin fine particle catalyst having an average particle size 0.01 to 10.0 µm wherein said platinum catalyst-containing silicone resin fine particle catalyst is comprised of (i) a thermoplastic silicone resin mixture of two or more silicone resins comprising a silicone resin containing vinyl groups and a silicone resin not containing a vinyl group such that the overall formula contains 5 to 90 mole% PhSiO 3/2 siloxane units and 5 to 20 mole% MeViSiO 2/2 siloxane units; said resin having a glass transition point of 40 to 70°C and (ii) 0.05 to 2 wt% as platinum atoms of a platinum catalyst; and (d) a hydrosilation reaction inhibiting compound. As used hereinafter Ph denotes phenyl, Me denotes methyl and Vi denotes vinyl. The instant invention provides a thermosetting silicone composition comprised of (a) 100 parts by weight of a diorganopolysiloxane containing at least 2 alkenyl groups in a molecule; (b) an organohydrogenpolysiloxane containing at least 3 silicon atom-bonded hydrogen atoms in a molecule wherein said organohydrogenpolysiloxane is present in an amount sufficient to crosslink diorganopolysiloxane (a); (c) 0.1-100 ppm as platinum atoms based on (a) of a platinum catalyst-containing silicone resin fine particle catalyst having an average particle size 0.01 to 10.0 µm wherein said platinum catalyst-containing silicone resin fine particle catalyst is comprised of (i) a thermoplastic silicone resin mixture of two or more silicone resins comprising a silicone resin containing vinyl groups and a silicone resin not containing a vinyl group such that the overall formula contains 5 to 90 mole% PhSiO 3/2 siloxane units and 5 to 20 mole% MeViSiO 2/2 siloxane units, said resin having a glass transition point of 40 to 70°C and (ii) 0.05 to 2 wt% as platinum atoms of a platinum catalyst; and (d) 0.0001-1 parts by weight of a hydrosilation reaction inhibiting compound. Diorganopolysiloxane (a) is the major ingredient in our composition and it requires at least 2 silicon atom-bonded alkenyl groups in a molecule. The alkenyl groups are exemplified by vinyl, allyl, and hexenyl. The remaining groups on diorganopolysiloxane (a) are silicon-bonded organic groups. The silicon-bonded organic groups, other than the alkenyl groups, are monovalent hydrocarbon groups which are exemplified by alkyl groups such as methyl, ethyl, propyl, butyl, hexyl, and octyl; aryl groups such as phenyl; and substituted hydrocarbon groups such as 3,3,3-trifluoropropyl. The number of silicon-bonded organic groups on the average should preferably be 1.0-2.3. Diorganopolysiloxane (a) is usually straight chain, but it can also be a branched siloxane structure. The degree of polymerization of diorganopolysiloxane (a) is not limited, however, it is preferred to use a diorganopolysiloxane having a viscosity in the range of 10-1,000,000 mPa·s at 25°C. Organohydrogenpolysiloxane (b) is the crosslinking agent for diorganopolysiloxane (a). For our composition to form a network structure, it is required that organohydrogenpolysiloxane (b) have at least 3 silicon-bonded hydrogen atoms per molecule. The remaining groups on the organohydrogenpolysiloxane are silicon-bonded organic groups. The silicon-bonded organic groups, other than the hydrogen atoms, are the same as those described for the diorganopolysiloxane (a). Such organic groups can be a single kind, or can be a mixture of two or more kinds. The molecular structure of organohydrogenpolysiloxane (b) can be straight chain, network, or 3-dimensional. Further, organohydrogenpolysiloxane (b) can be a single polymer, copolymer, or a mixture of two or more kinds of polymers. The viscosity of organohydrogenpolysiloxane (b) is usually in the range of 0.5-50,000 mPa·s at 25°C, preferably in the range of 1-10,000 mPa·s. Organohydrogenpolysiloxane (b) is added at an amount such that the ratio of the silicon-bonded hydrogen atoms in organohydrogenpolysiloxane (b) and the silicon-bonded alkenyl groups in diorganopolysiloxane (a) are in the range of 0.5/1 - 10/1. Preferably there is present 0.1-10 parts by weight organohydrogenpolysiloxane (b) per 100 parts by weight diorganopolysiloxane (a). The platinum catalyst-containing thermoplastic silicone resin fine particle catalyst (c) functions as the catalyst to cure the composition of the present invention. The platinum catalyst-containing silicone resin fine particle catalyst is comprised of (i) a thermoplastic silicone resin mixture of two or more silicone resins comprising a silicone resin containing vinyl groups and a silicone resin not containing a vinyl group such that the overall unit formula contains 5 to 90 mole% PhSiO 3/2 siloxane units and 5 to 20 mole% MeViSiO 2/2 siloxane units, said resin having a glass transition point of 40 to 70°C and (ii) 0.05 to 2 wt% as platinum atoms of a platinum catalyst As for the platinum catalyst (ii), known platinum catalysts, which show the hydrosilation catalyst activity, are used. Specifically, the platinum catalyst can be chloroplatinic acid, alcohol-modified chloroplatinic acid, complex of platinum and olefin, complex of platinum and ketone, complex of platinum and vinylsiloxane, platinum supported by alumina, silica, carbon black, and, platinum black. Among these, the complex of platinum and vinylsiloxane is preferred because of its high activity and its compatibility with the diorganopolysiloxane (a) and organohydrogenpolysiloxane (b). The thermoplastic silicone resin mixture (i) used in the platinum catalyst-containing silicone resin fine particle catalyst (c) contains 5-90 mole % PhSiO 3/2 siloxane units and 5-20 mole % MeViSiO 2/2 siloxane units. If there is less than 5 mole % PhSiO 3/2 siloxane units the storage stability of the composition of the present invention is degraded, and if it exceeds 90 mole % sufficient curing activity cannot be obtained. If there is less than 5 mole % MeViSiO 2/2 siloxane units, the thermal curing rate of the composition of the present invention becomes low, and if it exceeds 20 mole % the curing activity is impaired. Furthermore, the thermoplastic silicone resin mixture used in the platinum catalyst-containing silicone resin fine particle catalyst has to have a glass transition point in the range of 40-70°C. If the glass transition point is below 40°C, the storage stability of our composition is degraded drastically. If the glass transition point is higher than 70°C, a sufficient thermal curing rate cannot be obtained. The glass transition point can be determined by a Differential Scanning Calorimeter (DSC). The silicone resins optimal for this invention are exemplified by the following average unit formulas: (PhSiO 3/2 ) 0.78 (MeViSiO) 0.22 , (PhSiO 3/2 ) 0.78 (MeViSiO) 0.11 (Me 2 SiO) 0.11 , (PhSiO 3/2 ) 0.78 (MeViSiO) 0.06 (Me 2 SiO) 0.16 , (PhSiO 3/2 ) 0.65 (MeViSiO) 0.17 (Ph 2 SiO) 0.18 and (PhSiO 3/2 ) 0.65 (MeViSiO) 0.06 (Me 2 SiO) 0.1 (Ph 2 SiO) 0.19 . These silicone resins are used as a mixture of a silicone resin containing vinyl groups and a silicone resin not containing a vinyl group. If the mixture of silicone resins used are compatible, and the overall unit formula is within the above range, the objective of the present invention is achieved. The platinum catalyst-containing silicone resin fine particle catalyst (c) is required to have an average particle size of 0.01-10.0 µm. If the average particle size exceeds 10.0 µm, when the composition of the present invention is heated, the curing is incomplete and the heat resistance. of the silicone composition is impaired. And, if the average particle size is less than 0.01 µm, it becomes difficult to attain sufficient storage stability for the composition. The average particle size can be measured by the centrifugal sedimentation method or by the laser scattering method. The platinum catalyst-containing silicone resin fine particle catalyst (c) used in the instant invention can be manufactured by methods known in the art. US-A 4,481,341; EP-A 0347895; and US-A 5,153,160. Among these, the method of US-A 5,153,160 is preferred since it is easier therein to obtain fine particles of uniform particle size, the production efficiency is high, and the chance of contamination is less. The ratio of platinum catalyst to silicone resin should be such that the content of the platinum catalyst in the platinum catalyst-containing silicone resin fine particle catalyst (c) is 0.05-2.0 wt % as platinum atoms. If the ratio is less than 0.05 wt %, the ratio of silicone resin in our composition becomes too high, and the physical characteristics after cure may be impaired. Also, if the ratio exceeds 2.0 wt %, it becomes difficult to keep the platinum catalyst inside of the fine particles. This can result in a drastic degradation of the storage stability of the composition of the present invention. The amount of platinum catalyst-containing silicone resin fine particle catalyst (c) is in the range of 0.1-100 ppm as platinum atoms based on diorganopolysiloxane (a) and preferably in the range of 0.5-50 ppm. Since the amount used in a silicone composition, of (c), is dependent on the platinum catalyst in the fine particle catalyst (c), the amount of (c) is not particularly limited. Usually, the amount of (c) is in the range of 0.005-10 parts by weight per 100 parts by weight of diorganopolysiloxane (a). The hydrosilation reaction inhibiting compound (d) is a compound which has a catalyst inhibition effect against the hydrosilation reaction catalyst. Any compound known in the art to have an effect to delay curing or an effect to improve storage stability of the silicone elastomer compositions which cure by hydrosilation reaction can be used. The hydrosilation reaction inhibiting compound (d) are exemplified by phosphorus-containing compounds such as triphenylphosphine and others; nitrogen-containing compounds such as tributylamine; tetramethylethylenediamine and benzotriazole; sulfur-containing compounds; acetylene compounds; compounds containing 2 or more alkenyl groups; hydroperoxy compounds; and maleic acid derivatives; and other compounds. Among these, the compounds containing alkenyl groups or alkynyl groups are preferred. In particular, more preferred are compounds containing 2 or more alkynyl groups in a molecule, compounds containing an alkenyl group and an alkynyl group in a molecule, compounds containing an alkenyl group and an alcoholic hydroxyl group in a molecule, maleic diester and organic silicon compounds which have a bonding unit in which alkenyl groups are bonded to both silicon atoms which are adjoined via an oxygen atom. The degree of the curing acceleration effect by the hydrosilation reaction inhibiting compound (d) differs greatly depending on the chemical structure of the compound (d). Therefore, the amount of compound (d) should be adjusted to the optimal amount for each of the inhibiting compounds (d) used. If the amount is too small, the curing acceleration effect will not be obtained, and, if it is too much, it would inhibit the cure. Therefore, the preferable range for compound (d) is 0.0001-1 part by weight per 100 parts by weight of diorganopolysiloxane (a). Although the composition of the present invention is the thermosetting silicone composition comprised of the above components (a) - (d), additional components can be added as long as the objective of the present invention is not impaired. The additional components are exemplified by fine powder silica such as fumed silica and wet method silica, surface-hydrophobicized fine powder silica, crepe hardening inhibitors, organic polymers other than silicone, organic solvents, iron oxide, heat-resisting agents such as rare earth compounds, manganese carbonate, flame retardant agents such as fine powder titanium oxide; diatomaceous earth, calcium carbonate, glass fiber, and carbon black. The composition of this invention can be easily obtained by uniformly mixing the above components (a) - (d). Although there is no particular limitation for the order of mixing the components, the preferable method is to mix the platinum catalyst-containing silicone resin fine particle catalyst (c) and a small amount of diorganopolysiloxane (a) to uniform dispersion, and then to add the mixture of (a) and (c) to a mixture of the organohydrogenpolysiloxane (b) and the hydrosilation reaction inhibiting compound (d). Any method can be used as long as the fine particle catalyst (c) is not destroyed. The temperature at which the components are mixed varies depending on the component (c) used and cannot be generally specified. However, the components should not be mixed at a temperature of more than 50°C above the glass transition point of the silicone resin used in the platinum catalyst-containing silicone resin fine particle catalyst (c). The composition of our invention has excellent storage stability at room temperature, cures quickly by heating to form cured silicone, and the mechanical characteristics of the cured silicone are not degraded in high temperature use. Moreover, it does not discolor or cause discoloration. Consequently, it is appropriately used in the areas where such characteristics are required. For example, as a silicone adhesive for electric-electronic equipment, as a silicone rubber gasket, and as the silicone rubber composition for various other silicone rubber parts. Examples So that those skilled in the art can understand and appreciate our invention, the following examples are presented. In the following examples, viscosity is the value at 25°C, and % denotes weight %, Ph. Preparation Example 1 Preparation of platinum-vinylsiloxane complex composition 6 grams of a chloroplatinic acid aqueous solution (platinum content 33 %) and 16 grams of 1,3-divinyltetramethyldisiloxane were dissolved in 35 grams of isopropyl alcohol. 10 grams of sodium hydrogencarbonate was added to this solution, and while stirring in suspension state, the mixture was reacted at 70-80°C for 30 minutes. After cooling, a solid was removed by filtering, and an isopropyl alcohol solution of platinum-vinylsiloxane complex composition (platinum content 4.2 %) was obtained. Preparation Example 2 Preparation of platinum catalyst-containing fine particle catalyst (No. 2) 900 grams of a thermoplastic silicone resin of the formula (PhSiO 3/2 ) 0.78 (MeViSiO) 0.22 and having a glass transition point of 65.2°C, 500 grams of toluene and 4,600 grams of dichloromethane were loaded into a glass container with an attached stirrer and mixed uniformly. 44.4 grams of the platinum-vinylsiloxane complex composition obtained in Preparation Example 1 was added and mixed and a uniform solution of platinum-vinylsiloxane complex composition and the thermoplastic silicone resin was obtained. This solution was then sprayed continuously into a spray-dryer (manufactured by Ashizawa Niro Atomizer Co.) with hot nitrogen gas flow using a # 2 fluid nozzle. The temperature of the hot nitrogen gas flow was 95°C at the inlet of the spray dryer and 45°C at the outlet of the spray dryer. The hot gas flow rate was 1.3 m 3 /min. After 1 hour operation, 450 grams of a platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the bag filter. The average particle size of the resulting fine particle catalyst was 1.4µm, and the platinum content was 0.40 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. Preparation Example 3 Preparation of platinum catalyst-containing fine particle catalyst (No. 3) A platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the same manner as in Preparation Example 2 except that the silicone resin used in Preparation Example 2 was replaced by a silicone resin of the formula (PhSiO 3/2 ) 0.78 (MeViSiO) 0.11 (Me 2 SiO) 0.11 and having a glass transition point of 69.8°C. The average particle size of the resulting fine particle catalyst was 1.7 µm and the platinum content was 0.40 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. Preparation Example 4 Preparation of platinum catalyst-containing fine particle catalyst (No. 4) A platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the same manner as in Preparation Example 2 except that the silicone resin used in Preparation Example 2 was replaced by a silicone resin of the formula (PhSiO 3/2 ) 0.78 (MeViSiO) 0.06 (Me 2 SiO) 0.16 and having a glass transition point of 62.3°C. The average particle size of the resulting fine particle catalyst was 1.5 µm and the platinum content was 0.40 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. Preparation Example 5 Preparation of platinum catalyst-containing fine particle catalyst (No. 5) 450 grams of a thermoplastic silicone resin of the formula (PhSiO 3/2 ) 0.78 (MeViSiO) 0.22 and having a glass transition point of 65.2°C, 450 grams of a resin of the formula (PhSiO 3/2 ) 0.78 (Me 2 SiO) 0.22 and having a glass transition point of 64.8°C, 500 grams of toluene and 4,600 grams dichloromethane were loaded into a glass container with an attached stirrer, and mixed uniformly. 44.4 grams of the platinum-vinylsiloxane complex composition obtained in Preparation Example 1 was added to the mixture and a uniform solution of platinum-vinylsiloxane complex composition and the silicone resin was obtained. The average unit formula of the two silicone resins was (PhSiO 3/2 ) 0.78 (MeViSiO) 0.11 (Me 2 SiO) 0.11 . This solution was then sprayed continuously into the spray-dryer (manufactured by Ashizawa Niro Atomizer Co.) with hot nitrogen gas flow using a # 2 fluid nozzle. The temperature of the hot nitrogen gas flow was 95°C at the inlet of the spray dryer and 45°C at the outlet of the spray dryer. The hot gas flow rate was 1.3 m 3 /min. After 1 hour operation, 450 grams of a platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the bag filter. The average particle size of the resulting fine particle catalyst was 1.3µm, and the platinum content was 0.40 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. Preparation Example 6 Preparation of platinum catalyst-containing fine particle catalyst by a silicone resin not containing vinyl group (No. 6) A platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the same manner as Preparation Example 2 except that the silicone resin used in Preparation Example 2 was replaced by a silicone resin of the formula (PhSiO 3/2 ) 0.78 (Me 2 SiO) 0.22 and having a glass transition point of 64.8°C. The average particle size of the resulting fine particle catalyst was 1.5 µm and the platinum content was 0.40 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. Preparation Example 7 Preparation of platinum catalyst-containing fine particle catalyst by the silicone resin not containing vinyl group (No. 7) A platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the same manner as in Preparation Example 2 except that the silicone resin used in Preparation Example 2 was replaced by a silicone resin of the formula (PhSiO 3/2 ) 0.90 (Me 2 SiO) 0.10 and having a glass transition point of 95.6°C. The average particle size of the resulting fine particle catalyst was 1.5 µm and the platinum content was 0.40 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. Preparation Example 8 Preparation of platinum catalyst-containing fine particle catalyst by the silicone resin not containing vinyl group (No. 8) A platinum-vinylsiloxane complex-containing silicone resin fine particle catalyst was manufactured in the same manner as in Preparation Example 2 except that the silicone resin used in Preparation Example 2 was replaced by a silicone resin of the formula (PhSiO 3/2 ) 0.60 (MePhSiO) 0.40 and having a glass transition point of 58.1°C. The average particle size of the resulting fine particle catalyst was 1.7 µm and the platinum content was 0.41 %. It was confirmed that the resulting fine particle catalyst was spherical by observation using a scanning electron microscope. EXAMPLE 1 Thermosetting silicone compositions were prepared using the platinum catalyst-containing fine particle catalysts obtained in Preparation Examples 2-8. A base compound was prepared by uniformly mixing 12 grams of a fumed silica which was hydrophobicized with hexamethyldisilazane and a mixture containing 25 grams of α,ω-divinylpolydimethylsiloxane having a viscosity of 1,500 mPa·s and 50 grams of a α,ω-divinylpolydimethylsiloxane having a viscosity 10,000 mPa·s, 1.2 grams of an organopolysiloxane having the average molecular formula Me 3 SiO(Me 2 SiO) 3 (MeHSiO) 5 SiMe 3 and 0.03 grams of phenylbutynol. Thermosetting diorganopolysiloxane compositions were then prepared by individually adding 0.125 grams of each platinum catalyst-containing fine particle catalyst No. 2-5 prepared in Preparation Examples 2-5 to the resulting base compound. Similarly, thermosetting diorganopolysiloxane compositions were manufactured by individually adding 0.125 grams of each platinum catalyst-containing fine particle catalyst No. 6-8 prepared in Preparation Examples 6-8 to the above base compound. Thermal curing characteristics of these compositions were measured at 130°C and 150°C by a Curastometer Type 5 (manufactured by Orientec Co.). The thermal curing characteristics were determined by measuring the time to which the torque reaches 10% of the final value (T 10 ) and the time to which the torque reaches 90% of the final value (T 90 ) . Here, T 10 can be regarded as the curing initiation time, and T 90 as the curing completion time. Also, the storage stability of these thermosetting silicone compositions was studied by an accelerating test comprising aging the thermosetting silicone compositions at 50°C and measuring the viscosity at intervals of several days. The number of days before the viscosity value doubled was defined as the stable storage period. These measurement results are shown in Table 1. Comparison Examples Example Comparison Examples Catalyst Used No.2 No.3 No.4 No.5 No.6 No.7 No.8 Thermal Curing Characteristics (sec) 130°C T 10 112.2 143.4 70.8 118.2 150.6 333.0 52.4 T 90 143.4 165.0 85.2 139.2 170.4 372.4 77.0 150°C T 10 29.4 36.0 22.8 30.0 36.0 75.0 27.4 T 90 42.6 46.8 29.4 40.2 46.8 90.0 37.6 Stable Storage Period (days) 44 66 38 67 38 58 5 The thermosetting silicone composition in the present invention is characterized in that it is excellent in storage stability and its curing rate is fast when heated since it consists of the above components (a) - (d). In particular, the platinum catalyst-containing silicone resin fine particle catalyst (c) is comprised of (i) a thermoplastic silicone resin mixture containing 5 to 90 mole% PhSiO 3/2 siloxane units and 5 to 20 mole% MeViSiO 2/2 siloxane units, said resin mixture having a glass transition point of 40 to 70°C and (ii) 0.05 to 2 wt% as platinum atoms of a platinum catalyst.

Claims: A thermosetting silicone composition comprising (a) 100 parts by weight of a diorganopolysiloxane containing at least 2 alkenyl groups in a molecule; (b) an organohydrogenpolysiloxane containing at least 3 silicon atom-bonded hydrogen atoms in a molecule wherein said organohydrogenpolysiloxane is present in an amount sufficient to crosslink diorganopolysiloxane (a); (c) 0.1-100 ppm as platinum atoms based on the weight of (a) of a platinum catalyst-containing silicone resin fine particle catalyst having an average particle size 0.01 to 10.0 µm wherein said platinum catalyst-containing silicone resin fine particle catalyst is comprised of (i) a thermoplastic silicone resin mixture of two or more silicone resins comprising a silicone resin containing vinyl groups and a silicone resin not containing a vinyl group such that the overall unit formula contains 5 to 90 mole% PhSiO 3/2 siloxane units and 5 to 20 mole% MeViSiO 2/2 siloxane units, wherein Ph denotes phenyl, Me denotes methyl and Vi denotes vinyl; said resin having a glass transition point of 40 to 70°C and (ii) 0.05 to 2 wt% as platinum atoms of a platinum catalyst; and (d) 0.0001-1 parts by weight of a hydrosilation reaction inhibiting compound. The composition of claim 1 wherein diorganopolysiloxane (a) has a viscosity of 10-1,000,000 mPa·s at 25°C. The composition of claim 1 wherein organohydrogenpolysiloxane (b) has a viscosity of 0.5-50,000 mPa·s at 25°C, The composition of claim 1 wherein the silicon-bonded hydrogen atoms in organohydrogenpolysiloxane (b) and the silicon-bonded alkenyl groups in diorganopolysiloxane (a) are in a range of 0.5/1 to 10/1.

Inventors: NAKANISHI JUNJI, SARUYAMA TOSHIO, TOGASHI ATSUSHI, NAKANISHI, JUNJI, SARUYAMA, TOSHIO, TOGASHI, ATSUSHI, NAKANISHI, JUNJI, DOW CORNING TORAY SILICONE, SARUYAMA, TOSHIO, DOW CORNING TORAY SILICONE, TOGASHI, ATSUSHI, DOW CORNING TORAY SILICONE
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: C08L83
IPC codes: C08L83, C08K9