A method for purifying industrial sewage water

Abstract: The present invention relates to a method for purifying contaminated industrial sewage water solutions or other aqueous solutions having a similar contaminant profile, normally containing ions of several metals and other elements such as As, Bi, Sb, P and Se, by precipitation in two stages and by returning the precipitate separated from the second precipitation stage to the first precipitation stage. Precipitation is effected in a first stage by adding lime in a surplus quantity, wherewith the major part of the contaminant content is precipitated. The formed precipitated is isolated and removed together with residual lime. Precipitation of remaining contaminant content is effected by adding a suitable reagent for precipitation at a pH in the range of 4-11, and formed precipitate is isolated and returned to the first precipitation stage, either directly or indirectly.

Description: The present invention relates to a method for purifying contaminated industrial sewage water solutions or other aqueous solutions which have a similar contamination profile, normally comprising ions of several metals and other contaminating elements such as As, Bi, Sb, P and Se, comprising precipitating the contaminants in two stages and returning the precipitate isolated from the second stage to the first precipitation stage. Many known methods for purifying industrial sewage water are directed primarily to certain selected contaminants or impurities and are less effective in the case of other contaminants. These processes are often complicated or often contain stages which require the use of advanced and sensitive control equipment, for instance precipitation agent metering equipment or pH-regulating equipment. Because of their complexity, sensitivity and cost, such purification methods are only used to a limited extent, or are less effective than would be desired. Methods of the kind defined in the introduction are known from Boliden's earlier patent specifications, for instance from EP-B-O,139,622 and EP-B-0,364,423. A fundamental concept of both of these methods is that the major part of the precipitation reagent is added in the second stage under conditions in which a voluminous metal hydroxide-metal oxide precipitate is formed. This voluminous precipitate is separated and returned to the first precipitation stage and contains a substantial part of the contaminant content and is used as an auxiliary precipitation agent in the precipitation taking place in the first stage, from which there is taken a precipitate which includes essentially the entire contaminant content of the contaminated solution. According to EP-B-0,139,622, the contaminants removed are primarily As and/or P, wherein the precipitation process in the first stage is carried out in an alkaline environment to form an arsenic-containing and/or a phosphate-containing dumpable sludge. Publication EP-B-0,364,423 relates to the purification of industrial waste solutions, for instance solutions that contain As, P and also heavy metals, wherein after adding the voluminous hydroxide precipitate taken from the second stage, purification in the first stage is effected by adding sulphide ions at a pH such as to dissolve the hydroxide precipitate. This results in the formation of a metal sulphide precipitate which can be conveniently worked-up with respect to its valuable metal content. These known two-stage processes in which hydroxide precipitate is returned from the second stage purify industrial water sewage much more effectively and in a much simpler manner than the earlier purification processes, among other things with regard to the deficiencies of the known processes mentioned in the introduction and also with regard to general problems that occur in such purification processes. However, the aforesaid known two-stage processes can be considered too sophisticated from a technical aspect and also to be encumbered with other drawbacks in certain respects and in the case of certain uses. The problem associated with the choice of a method for purifying industrial waste effluents, sewage water or like contaminated aqueous solutions resides in the constant increase in the demands for generally low influence on the environment placed by the responsible authorities, for instance the limit values of the effluent to the recipient are made successively lower. The number of substances or elements to which the limit values apply also become successively larger in number. The tolerance with which industrial effluents are considered in operational breakdowns or abnormal situations is decreasing, and consequently even short stoppages in an industrial processes which results in the discharge of effluent above current limit values can have very serious consequences for those of responsibility in the industry concerned. These new and progressively growing requirements on reliable and operationally safe purification processes accentuate still further those problems indicated in the introduction with regard to known processes for the purification of industrial water sewage. Thus, the demands for operational safety and reliability are in addition to the earlier requirements of a good precipitation result and low outgoing residual contents. The two known Boliden methods are able to well satisfy the modern demands placed on all of the aforesaid, conceivable parameters, with regard to their particular applications and with regard to the conditions stated, for instance the presence of relatively high concentrations of As. However, in purification situations in which the solutions or the water sewage to be purified contains highly varying concentrations of contaminants and/or a broad spectrum of contaminants, there is no method which can be applied in practice and which can be used generally to achieve accepted residual contents or concentrations while providing an operationally safe and reliable alternative at the same time. It has now surprisingly been found possible to utilize the principle of two-stage precipitation and the return of the precipitate from the second stage to the first stage and therewith provide a general process for purifying industrial sewage water and like contaminated aqueous solutions, whereby the problems described in the introduction can be eliminated to a great extent. To this end, the novel method is characterized by the features set forth in the following Claims, which are herewith incorporated in the descriptive part of this document. Thus, in accordance with the invention, precipitation is effected in the first stage, which can be divided into a number of sub-stages, by adding lime in a surplus quantity, i.e. in a quantity in which the solution is saturated with regard to lime. In this regard, the major part of the contaminant content is precipitated and the formed precipitate is isolated together with residual undissolved lime and removed together therewith. Continued precipitation of the remainder of the contaminant content is then effected by adding a suitable reagent for precipitation at a pH within the range of 4-11. The formed precipitate is isolated and then returned, either directly or indirectly, to the first precipitation stage, i.e. either directly to the actual precipitation stage or indirectly by adding said precipitate to the sewage water at a location upstream of the first stage and allowing the precipitate to accompany the input contaminated solution to the first precipitation stage. The lime is conveniently introduced to the system in the form of milk of lime, i.e. a slurry of CaO in water, and/or a saturated aqueous solution of hydrated lime (Ca(OH) 2 ). The precipitation reagent for the second precipitation stage is conveniently selected from the group consisting of ferro salt, ferri salt, mineral acid, such as HCl or H 2 SO 4 , or is comprised of a mixture of one or more reagents from this group. The second precipitation stage is conveniently effected at pH 7-11, preferably pH 9-10, although a lower pH -i.e. an acid solution- may be necessary in oxidized conditions when the presence of arsenic is substantial. The input solution or the input water sewage to this stage can be subjected to a preceding purification process, which may be a biological, mechanical or chemical process, before being introduced to the first precipitation stage according to the invention. In the second precipitation stage, the reagent is advantageously introduced in an amount which is proportional to the flow of aqueous solution entering this stage. In order to obtain an optimal yield, the reagent addition in the second stage may conveniently be in the form of a mixture of ferro salt, a deficit quantity of oxidation agent, and mineral acid. The invention will now be described in more detail with reference to the accompanying drawing which illustrates a preferred flowsheet relating to the inventive method, and also to trial examples carried out in practice. Figure 1 illustrates a preferred embodiment of the invention in the form of a flowsheet. Shown in the Figure is a receiving tank 10, a precipitation tank 11 and a sedimentation or settling tank 12 for the first precipitation stage. The second precipitation stage utilizes a precipitation tank 13 and a settling tank 14. Also shown is a tank 15 in which reagents introduced to the settling tank 13 are prepared, and a dewaterer 16 which dewaters sludge or mud taken from the settling tank 12. When practicing the invention, a contaminated solution is introduced into the receiving tank 10 together with sludge returned from the settling tank 14 of the second precipitation stage. The contaminated solution may be an industrial water sewage or may derive generally from an industrial manufacturing process or the like. Because of the general nature of the invention, the solution may, in principle, contain all conceivable metal ions and also other contaminants of a non-metallic nature deriving from said industrial processes. The solutions and the sludge products entering the purification process are stirred and mixed together in the receiving tank 10. The resultant solution/sludge mixture is passed through a conduit 17 to the precipitation tank 11, to which lime is introduced in the form of milk of lime (Ca0 slurry) and/or slaked lime (Ca(OH) 2 ) while stirring. The precipitation tank 11 may be comprised of one or more reactors. The lime is added in a quantity such as to maintain constantly a lime surplus in the tank 11. The contents of the tank 11 will therewith have a pH of about 12. The resultant lime-sludge-aqueous suspension is passed through a conduit 18 to the settling tank 12, and sludge sediment is removed from the lower part of the tank 12 and passed through a conduit 19 to the de-waterer 16, in which the sludge is dewatered to the extent desired and then removed from the dewaterer and passed to a suitable recipient. The dewatered sludge departing from the first stage has an acidification and carbonization buffer as a result of its solid lime content deriving from the lime surplus in this stage, which is advantageous and essential when dumping the sludge. The water separated from the sludge in the dewaterer 16 is returned through a conduit 20 to the precipitation tank 11. The major part of the majority of the contaminants present in the input solutions are precipitated in the first precipitation stage (11, 12). By adding lime in a calculated surplus in accordance with the invention, the sensitivity of the input contaminant concentrations to changes is very low. The water which is passed through a conduit 21 to the second precipitation stage (13, 14) after separating sludge in the settling tank 12 will thus have a generally constant composition and therewith relatively low levels of the majority of the contaminating elements. The solution containing the remainder of the contaminant content subsequent to purification in the first precipitation stage (11, 12) is passed from the settling tank 12 to the settling tank 13 of the second precipitation stage through a conduit 21. Reagent for precipitation contaminants in the second precipitation stage is prepared in the tank 15. The precipitation reagent is conveniently comprised of ferro salt and/or ferri salt. As indicated, these salts can be mixed with a mineral acid, such as H 2 SO 4 in the present case, and an oxidation agent, for instance Cl 2 . The prepared reagent mixture is introduced into the precipitation tank 13 through a conduit 22, while stirring the mixture. Since the composition of the solution entering through the conduit 21 is essentially constant, as indicated above, the addition of reagent to the second precipitation stage (13, 14) can be controlled very easily. In this regard, there can be applied a simple flow-proportional addition, optionally in combination with pH control in the precipitation tank 13. Precipitation in the second stage will preferably take place at a pH close to 10. The contents of the precipitation tank 13 are passed through a conduit 23 to the settling tank 14, from which there is removed a sludge and purified water that can be delivered to a suitable recipient. The sludge taken from the tank 14 is returned to the receiving tank 10 through a conduit 24. The returned sludge, however, may alternatively be delivered directly to the precipitation tank 11 or to the contaminated solution prior to delivering this solution to the tank 10, while remaining within the concept of the invention which is that the sludge taken from the second purification stage shall be present in the first precipitation stage. By returning the precipitate from the second stage, there is obtained a stabilizing effect with regard to the precipitate obtained in the first precipitation stage, which greatly facilitates sedimentation and dewatering of the precipitate. Another important advantage obtained by returning this secondary sludge is that it is unnecessary to subject the sludge to a separate dewatering process thereby enabling those difficulties that occur when dewatering alkaline ferro-precipitations and like voluminous precipitations that may often be obtained in the present context to be totally avoided. Examples A series of laboratory tests were carried out while practicing the inventive method. The following reagent was prepared prior to these tests: R1: Milk of lime, 120 g CaO/litre pH = 11.5 R2: Saturated aqueous solution FeSO 4 at t = 20°C, about 1 mole Fe/litre R3: Aqueous solution of FeCl 3 , about 0.5 mole Fe/litre R4: Aqueous solution containing 0.15% Praestof 2530 (Anionic polymer) R5: Saturated solution of Ca(OH) 2 A synthetic start solution (L1) containing, among other things, the following substances (mg/litre) was then prepared: H 2 SO 4 25,000 Cu 509 Fe 750 Zn 909 As 480 Na 100 Cl 1,400 F 600 In a first test series, 190 ml of R1 were first added to 1,500 ml of L1 to obtain a pH of about 6. The reaction time was 0.75 h, after which it was established that the content of As had fallen to 31 Mg/l and the content of Fe had fallen to 2 Mg/l. A further 60 ml of R1 was then added to the solution, to obtain a pH in the range of 11-12. After a reaction time of 0.75 h, the sample was filtered and the filtrate (L3) analyzed, which gave the following (mg/l): Fe 2.4 Zn 11 As 1.2 Pb 0.05 Se <0.03 In a second test series, 10 g/l of As was added to L1, which was diluted to twice its volume. This solution was designated L9 and is calculated to contain, among other things, (mg/l): As 5,240 Fe 375 Zn 455 F 11.6 A surplus quantity of R1 was added to the solution L9 to obtain pH = 10.6, whereafter the sample was filtered and analyzed, giving the following result (mg/l): As 10 Fe 1.4 Ca 1,145 Zn 2.9 Pb <0.02 Se <0.05 Hg <0.001 F 11.6 The filtrate L3 was mixed in roughly equal parts with R5 and As was added in an amount corresponding to 15 mg/l. After stirring for 1 h. at 60°C and pH 10.5, the suspension was filtered with the addition of 1 droplet of R4. The filtrate L8 was analyzed and found to contain, among other things, the following quantities (mg/l): As 3.1 Fe <0.1 Ca 1,100 Zn 3.4 In a further test series, reagents were added to effect a second precipitation of contaminants in the filtrate L8. There were first mixed together 80 ml of L8 and 9 ml of R2, and 2 droplets of R4 were added. The mixture was stirred for 5 min. at a temperature of 50°C and a pH of 9.1, whereafter the mixture was filtered to obtain a filtrate having the following contents (mg/l): As <0.05 Fe <0.1 Ca 1,100 Zn 0.01 The same tests were repeated, but in this case stirring was continued for 40 min. In this case, the zinc content fell to <0.01, whereas the Fe content rose slightly to 0.38. Thus, it was shown that the proposed combination of solely two precipitation stages results in unexpected high separation of the majority of contaminants or impurities occurring in industrial sewage water and like sewage solutions. Because the control strategy is so simple and so easy to realize, the purification result is extremely good and reliable. The addition of lime in surplus quantities in the first precipitation stage in accordance with the invention thus provides a filtrate to the second precipitation stage which has practically constant composition and with relatively low concentrations of the majority of contaminating elements. This enables the addition of precipitating reagents in the second precipitation stage to be easily controlled so as to achieve a predetermined purification effect.

Claims: A method for purifying contaminated industrial sewage water solutions or other aqueous solutions having a similar contaminant profile, normally containing ions of several metals and other elements such as As, Bi, Sb, P and Se, by precipitating in two stages and returning the precipitate separated from the second precipitation stage to the first precipitation stage, characterized in that precipitation is effected in a first stage by adding lime in a surplus quantity, wherein the major part of the contaminant content is precipitated; in that the formed precipitate is isolated and removed together with residual lime; in that the second stage precipitation of residual contaminant contents is effected by adding a suitable reagent for alkaline precipitation at a pH in the range of 4-11; and in that formed precipitate is isolated and returned to the first precipitation stage, either directly or indirectly. A method according to Claim 1, characterized in that the lime is added in the form of milk of lime and/or saturated aqueous solution of Ca(OH) 2 . A method according to Claim 1 and 2, characterized in that the precipitation reagents used in the second precipitation stage are chosen from the group consisting of ferro salt, ferri salt, mineral acid, or are comprised of a mixture of one or more reagents taken from said group. A method according to Claims 1-3, characterized in that the second precipitation stage is carried out at pH 7-11, preferably pH 9-10. A method according to Claims 1-4, characterized in that the solution (sewage water) to be purified is subjected to a chemical or mechanical pre-purification process prior to being introduced to the first precipitation stage. A method according to Claims 1-5, characterized in that reagent is supplied to the second precipitation stage in an amount which is proportional to the flow of aqueous solution entering said precipitation stage. A method according to Claims 1-6, characterized in that the reagent added in the second stage is comprised of a mixture of ferro salt, a deficit of oxidation agent, and mineral acid. A method according to Claims 1-7, characterized in that the first stage includes several sub-stages.

Inventors: ALLGULIN TORKEL, ALLGULIN, TORKEL
Applicants: BOLIDEN CONTECH AB
Application year: 1994
Main classification: C02F1
IPC codes: C02F9, C02F1