AZLACTONE-FUNCTIONAL POLYMER BLENDS, ARTICLES PRODUCED THEREFROM AND METHODS FOR PREPARING BOTH

Abstract: An azlactone-functional thermoplastic composition is disclosed. The composition is a blend of an azlactone-functional composition and a thermoplastic polymer. A method of making azlactone-functional homopolymers by bulk homopolymerization is disclosed, optionally also concurrent or sequential blending of a thermoplastic polymer. A method of blending azlactone-functional compositions and thermoplastic polymers is disclosed. Molded articles and adduct molded articles formed from the thermoplastic composition are disclosed.

Description: AZLACTONE-FUNCTIONAL POLYMER BLENDS, ARTICLES PRODUCED THEREFROM AND METHODS FOR PREPARING BOTH FIELD OF THE INVENTION This invention relates to polymer blends having azlactone- functional surfaces, useful articles formed from such blends, and methods to prepare the blends and the articles. BACKGROUND OF THE INVENTION European Patent Publication 0 392 783 (Coleman et al.) describes efforts to obtain azlactone graft copolymers via functionalization of a poly- alpha-olefin base polymer by grafting a monomeric 2-alkenyl azlactone using reactive extrusion processing. Compatibilized blends and blends with base polymer are also disclosed. Many desirable and useful graft copolymers result from this method. But there is an upper temperature limit of about 200°C in the grafting process because monomeric 2-alkenyl azlactones are volatile. The reactive extrusion temperature range limits the types of base polymer candidates for reactive extrusion. For example, nylon 6 and certain polyurethanes are not suitable candidates for reactive extrusion according to the method of Coleman et al. Another difficulty with graft copolymers prepared by reactive extrusion is the uncertainty of products and byproducts of the reactive extrusion process. Uncertain products can include degraded or crosslinked base polymer, homopolymer of the graft comonomer, and uncertain grafting configurations on the desired graft copolymer product. The presence of unreacted monomer is deleterious to performance of the resulting product, particularly when the resulting product is used for an article prepared by injection molding. Also, depending on the type of free radical initiator employed in the reactive extrusion process, crosslinking of thermoplastic polymer can occur that would otherwise deleteriously affect use of the graft copolymer for further processing. One purpose of preparing azlactone-functional graft copolymers is to provide azlactone-functional surfaces for subsequent reaction with nucleophilic groups, including biologically active substances. One method of providing azlactone-functional surfaces is to functionalize pre-existing surfaces of an article. But such methods are limited by the complexity of the process and the ability of the treatment to affect such pre-existing surfaces. An example of chemical treatment of a pre-existing surface to impart functionality is disclosed in Edelman et al. , Proc. Nat. Acad. Sci. USA 68, 2153 (1971), which describes how to functionalize nylon monofilament fibers using 3N HC1 to partially hydrolyze the fibers before protein could be coupled using a water-soluble carbodiimide. Partial hydrolysis can weaken the physical properties of the polymer, such as strength, flexibility, resiliency to stretching, etc. An English language abstract of Japanese Kokai 92,159 published by the American Chemical Society discloses the use of azlactones as compatibilizers in a blend of nylon and polycarbonate polymers. U.S. Pat. No. 4,695,608 (Engler et al.) discloses the bulk polymerization of vinyl monomers and alkenyl azlactones using free radical polymerization techniques. SUMMARY OF THE INVENTION The invention overcomes processing limitations associated with using processes that rely on the bulk copolymerization of monomeric 2-alkenyl azlactones that can result in uncertain byproducts and unreacted monomers. The invention provides the melt blending of azlactone-functional compositions, especially homopolymers, with thermoplastic polymers. When azlactone-functional copolymers are melt blended with thermoplastic polymers, a two phase, incompatible blended product usually results. However, this incompatibility does not have deleterious effects of an uncompatibilized product due to the ability of azlactone-functionality to react with desired nucleophilic ligands. This invention also provides a method of extrusion bulk polymerization of azlactone-functional monomers and the blending of their resultant homopolymers with thermoplastic polymers in a single step or in sequential steps. Because the melt blending process is non-reactive for the thermoplastic polymer so blended, the chemical properties of the thermoplastic polymer are substantially unaltered. Because the melt blending process can be used for molding operations, azlactone-functional articles can be prepared in any desired shape or exhibiting any desired surface contour. Azlactone-functional surfaces of the articles can be available for covalent reaction with nucleophilic groups, including biologically active substances, regardless of the shape or surface contour of the article so formed. Azlactone-functional homopolymers or copolymers are capable of being melt processed above 200°C, unlike monomeric azlactones. Thus, thermoplastic polymer candidates need not be limited to polymers which can be melt processed below 200°C. Nylon 6 and certain polyurethanes, among others, are now available for melt processing to make azlactone-functional articles. Melt blending and molding processes are advantageous over other means of surface modification because these processes avoid intermediate chemical activation of a surface required by standard chemical means of surface modification. One aspect of this invention is a method of melt blending a thermoplastic polymer with an azlactone-functional composition. Another aspect of this invention is a method of bulk homopolymerizing 2-alkenyl azlactones in a solventless and continuous process with little unreacted monomer remaining in the bulk homopolymer so formed. Another aspect of this invention is a method of melt blending the bulk homopolymerized 2-alkenyl azlactones with thermoplastic polymers. The method of melt blending can occur in a single step with bulk polymerization or can occur in a sequential step after bulk polymerization. Another aspect of this invention is an article produced from the melt blending of a thermoplastic polymer with an azlactone-functional polymer. For purposes of this invention, the following definitions apply. "Azlactone" means an oxazolinone moiety of Formula I: wherein R 1 and R 2 independently can be an alkyl group having 1 to 14 carbon atoms, a cycloalkyl group having 3 to 14 carbon atoms, an aryl group having 5 to 12 ring atoms, an arenyl group having 6 to 26 carbon atoms and 0 to 3 S, N, and nonperoxidic O heteroatoms, or R 1 and R 2 taken together with the carbon to which they are joined can form a carbocyclic ring containing 4 to 12 ring atoms, and n is an integer 0 or 1. "Azlactone-functional" means an least one azlactone moiety of Formula I is present at a surface of a polymeric composition, such that at least one azlactone moiety remains available for further nucleophilic reaction, especially with a biologically active substance. "Azlactone-functional composition" means a compound containing or comprising at least one azlactone moiety of Formula I above. It is within the scope of the invention to melt blend more than one azlactone- functional composition with a thermoplastic polymer according to the methods of the present invention. Therefore, reference to azlactone-functional composition should be deemed to include one or more azlactone-functional compositions as desired for end-use properties. "Biologically active substance" means a chemical composition having azlactone-reactive, nucleophilic-functional groups and capable of reacting in a manner which affects biological processes, especially mammalian cells. Nonlimiting examples of biologically active substances are substances which are biologically, immunochemically, physiologically, or pharmaceutically active. "Thermoplastic polymer" means a polymer which is capable of being melt blended at temperatures between about 50°C and about 350°C. Preferably, the melt blending temperatures can be between 75 °C and 300°C. Most preferably, the melt blending temperature can be between 100°C and 250° C. It is within the scope of the invention to melt blend more than one thermoplastic polymer with azlactone-functional compositions according to the methods of the present invention. Therefore reference to thermoplastic polymer should be deemed to include one or more thermoplastic polymers as desired for end-use properties. When azlactone copolymers are used as the azlactone- functional composition, a two phase, incompatible blended product can result. "Surfaces" means both outer surfaces of an article and any applicable interior surfaces forming pores and interstices within a porous article. A feature of the present invention is the ability to render the surface of an article azlactone-functional while retaining the physical properties of the base polymer used to form the article. An advantage of the present invention is the formation of articles which are azlactone-functional, which are reactive toward nucleophilic groups without intermediate chemical activation of surfaces of the article. Embodiments of the invention follow a brief description of the drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic illustration of a twin screw extruder useful in a one-step process of the present invention. FIG. 2 is a schematic illustration of a twin screw extruder useful in the first step of a two-step process of the present invention. FIG. 3 is a schematic illustration of a twin screw extruder useful in the second step of a two-step process of the present invention. EMBODIMENTS OF THE INVENTION Thermoplastic Polymers Any thermoplastic polymer that is non-reactive with an azlactone moiety of Formula I above is a candidate for melt blending with azlactone- functional compositions to render surfaces of an article, formed from the thermoplastic polymer, azlactone-functional. Nonlimiting examples of thermoplastic polymers include polyamides (e.g., nylon 6), polyurethanes, polyacrylates, polymethacrylates, polystyrene, polyolefins, ethylene- vinyl acetate copolymers, poly(N-vinyl lactams) (e.g., polyvinylpyrrolidone), polyvinyl acetates, polyoxyalkylenes, styrene-acrylonitrile copolymers, polyphenylene oxides, fluoroelastomers, polycarbonates, polyesters. (Polyvinyl alcohol homopolymers and copolymers are not suitable because the hydroxy groups can react with azlactone.) These thermoplastic polymers can be homopolymers or copolymers. Thermoplastic copolymers can include azlactone-functional copolymers, such as graft copolymers disclosed in U.S. Pat. No. 5,013,795 (Coleman et al.) and bulk copolymers disclosed in U.S. Pat. No. 4,695,608 (Engler et al.). Thermoplastic polymers are readily commercially available from a number of sources. Depending on the thermoplastic polymer to be used and the end-use contemplated for the article, care should be taken to select one or more thermoplastic polymers having the requisite quality and purity. While thermoplastic polymers can be melt blended at temperatures ranging from about 50°C to about 350°C, it is preferred to have such thermoplastic polymers be capable of melt blending at ranges from about 75°C to about 300°C, and more preferably 100°C to about 300°C. While articles formed from thermoplastic polymers need not exhibit any specific opacity, translucency, or transparency, some uses of articles can require such physical properties. Of the possible candidates, poly(methylmethacrylate) is preferred because it can provide an optically clear, azlactone-functional blended article, which is particularly useful in medical articles, such as medical tubing and in diagnostic articles, such as microtitration wells and plates. Azlactone-functional Compositions Azlactone-functional compositions can be any compound containing or comprising at least one azlactone moiety of Formula I above. Preferably, it is an azlactone-functional polymer or oligomer. Most preferably, it is a homopolymer of an azlactone-containing monomer, preferably 2-alkenyl azlactone. Azlactone-functional polymers and oligomers are typically prepared by free radical polymerization of azlactone-containing monomers, optionally with co-monomers as described in U.S. Pat. No. 4,378,411. Copolymers containing minor portions of azlactone moieties can be prepared by bulk copolymerization with other vinyl monomers as described in U.S. Pat. No. 4,695,608. Polymers having azlactone-functional side chains can be prepared by reactive extrusion grafting of azlactone-containing monomers to non- azlactone-containing polymers, using such techniques as disclosed in European Patent Publication 0 392 783 (Coleman et al.) and in U.S. Pat. No. 5,013,795 (Coleman et al). Nonlimiting examples of azlactone-functional oligomers and polymers are disclosed in U.S. Pat. No. 5,081,197, and European Patent Publication 0 392 735. Other nonlimiting examples of azlactone-functional compositions and their methods of preparation by Michael Addition are disclosed in U.S. Pat. No. 4,485,236 (Rasmussen et al.), and in U. S. Pat. No. 5,149,806 (Moren et al.). Optionally, azlactone-functional compositions are homopolymers, copolymers, and oligomers prepared from azlactone-functional compounds having at least two azlactone moieties covalently connected to a bridging group, defined below, as shown in Formula II: wherein R 1 , R 2 , and n are as previously defined, wherein z is at least two, wherein R 3 is a bridging group capable of covalently connecting a plurality of azlactone moieties. Optionally, the azlactone-functional composition can be the compound of Formula II without polymerization or other further reaction. "Bridging group" means a group comprising (a) an alkylene group having up to 14 carbon atoms; (b) an arylene group having up to 10 carbon atoms; (c) a cycloalkylene group having up to 6 carbon atoms; (d) a group resulting from the Michael reaction of a Michael donor nucleophilic compound with a plurality of 2-alkenyl azlactone Michael acceptors, where the Michael donor nucleophilic compound has at least two nucleophilic moieties; or (e) a combination of the above-listed bridging groups. Nonlimiting examples of alkylene, arylene, and cycloalkylene groups are disclosed in "Polyazlactones" by J. K. Rasmussen, S. M. Heilmann, L. R. Krepski in Encyclopedia of Polymer Science and Engineering. Vol. 11, 2nd Ed., 1988. John Wiley & Sons, Inc., pp. 558-571. Nonlimiting examples of such Michael donor nucleophilic compounds include thiols and secondary amines as disclosed in U.S. Pat. No. 4,485,236 (Rasmussen et al.) or combinations thereof; or carbon acids, enamines, imides, and nitrogen heterocycles (as disclosed in U.S. Pat. No. 5,149,806 (Moren et al.)) or combinations thereof. Such azlactone-functional compositions can be prepared by the Michael Addition of 2-alkenyl azlactone monomers with nucleophilic group- substituted compounds having the formula (HX) n R 4 where R 4 is an organic group that has a valence of n and is the residue of a nucleophilic group- substituted compound, (HX) n R 4 , in which X is -O-, -S-, -NH-, or -NR 4 wherein R 4 can be alkyl or aryl, and n is defined below, the residue having a molecular weight up to 20,000, preferably selected from mono-and polyvalent hydrocarbyl (i.e. , aliphatic and aryl compounds having 2 to 20 carbon atoms and optionally zero to four catenary heteroatoms of oxygen, nitrogen or sulfur, e.g., piperazine, furan, and thiophene), polyoxyalkylene, polyester, polyolefin, polyacrylate, and polysiloxane residues that can optionally all be further substituted by at least one non-nucleophilic group such as cyano, halo, ester, ether, keto, nitro, silyl, sulfide (the carbon-containing groups having up to 10 carbon atoms), and nucleophilic groups including secondary amino groups, hydroxyl groups or mercapto groups; and n is an integer having a value of two to six. Optionally azlactone-functional compounds shown in Formula II can be used to form other compositions, using one of the azlactone moieties as a reaction site. Such compositions are represented by Formula III: wherein R 1 , R 2 , and n are as previously defined, wherein y at least one and is the number of azlactone moieties less one, wherein R 3 is a bridging group capable of covalently connecting a plurality of azlactone moieties, and wherein B is the reactant and A is the residue of the azlactone- reactive nucleophilic group on the reactant, such as O, S, or NR 5 , wherein R 5 is hydrogen or an alkyl group containing from 1 to 4 carbon atoms. Azlactone-containing Monomers Preferably, azlactone-functionality is provided to an azlactone- functional composition by 2-alkenyl azlactone monomers. The 2-alkenyl azlactone monomers are known compounds, their synthesis being described for example in U.S. Pat. No. 4,304,705; 5,081,197; and 5,091,489 (all Heilmann et al.). Suitable 2-alkenyl azlactones include: 2-ethenyl-4 ,4-dimethyl- 1 , 3-oxazolin-5-one, 2-isopropenyl-4,4-dimethyl-l,3-oxazolin-5-one, 2-ethenyl-4-methyl-4-ethyl- 1 ,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-butyl- 1 , 3-oxazolin-5-one, 2-ethenyl-4,4-dibutyl-l,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-dodecyl- 1 , 3-oxazolin-5-one, 2-isopropenyl-4,4-diphenyl- 1 ,3-oxazolin-5-one, 2-isopropenyl-4,4-pentamethylene-l ,3-oxazolin-5-one, 2-isopropenyl-4 ,4-tetramethylene- 1 , 3-oxazolin-5-one, 2-ethenyl-4,4-diethyl- 1 ,3-oxazolin-5-one, 2-ethenyl-4-methyl-4-nonyl- 1 , 3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-phenyl- 1 , 3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-benzyl- 1 ,3-oxazolin-5-one, 2-ethenyl-4 ,4-pentamethylene- 1 , 3-oxazolin-5-one, and 2-ethenyl-4,4-dimethyl-l,3-oxazolin-6-one. The preferred 2-alkenyl azlactones include 2-ethenyl-4,4-dimethyl-l,3-oxazolin-5-one (referred to herein as VDM) and 2- isopropenyl-4,4-dimethyl-l,3-oxazolin-5-one (referred to herein as IDM). Other azlactone-containing monomers include the 2-(4- alkenylphenyl)-5-oxazolones disclosed in U.S. Pat. No. 5,039,813. If an azlactone-functional copolymer is to be formed, a co- monomer having similar or different chemical or physical properties can be included, depending on the desired characteristics for the copolymer to be blended. Nonlimiting examples of co-monomers useful to be copolymerized with azlactone-functional moieties to form copolymers include methyl methacrylate (MMA); vinyl acetate, or any of vinyl aromatic monomers; alpha, beta-unsaturated carboxylic acids or their derivatives or vinyl esters; vinyl alkyl ethers; olefins; N-vinyl compounds; vinyl ketones; styrene; or vinyl aldehydes. Nonlimiting examples of such co-monomers are disclosed in European Patent Publication 0 392 735 and in European Patent Publication 0 392 783. Azlactone-containing copolymers can be prepared in bulk polymerization according to U.S. Pat. No. 4,695,608 (Engler et al.). Bulk Homopolymerization of Azlactone-Containing Monomers While the present invention can use azlactone-functional homopolymers prepared by solution polymerization or suspension polymerization according to known techniques described in the European Publications and the "Polyazlactones" article identified above and Almog et al. The British Polymer Journal. 14(4), 131, (1982), the present invention provides a method of bulk polymerizing azlactone-containing monomers in a reaction vessel to form azlactone homopolymers in a solventless and continuous procedure. In one embodiment, the one-step process, the solventless, bulk homopolymerization of azlactone-containing monomer occurs in situ in the same reaction vessel as blending and occurs concurrently with the blending of the azlactone homopolymer with the thermoplastic polymer, such that the blended polymers are extruded together. In this one-step embodiment, either a single- screw extruder or a twin-screw extruder can be used for the concurrent homopolymerization and blending. In a second embodiment, the two-step process, bulk homopolymerization of the azlactone-containing monomer occurs in one step and then the resulting polymer is blended with a thermoplastic polymer. In this two-step embodiment, a twin-screw extruder is used for homopolymerization and subsequent blending. Bulk homopolymerization is essentially solventless, continuous in production, and is essentially completely efficient in monomer conversion to homopolymer when using the two-step embodiment described above and at least 90% efficient in monomer conversion to homopolymer when using the one-step embodiment described above. Bulk homopolymerization is different from reactive extrusion graft copolymerization described in European Patent Publication 0 392 783 for at least two reasons: (1) Reactive extrusion graft copolymerization is a modification of an existing polymer, whereas bulk homopolymerization is the formation of a homopolymer. (2) The azlactone homopolymer once formed is not covalently attached to the thermoplastic polymer. Bulk homopolymerization employs a free radical initiation process. Acceptable free radical initiators include peroxide and azo compounds for the two-step embodiment described above and azo compounds for the one- step embodiment described above. During the one-step process, azo compounds thermally decompose to give radicals that are poor hydrogen atom abstractors. Thus, hydrogen atom abstraction is minimized and bulk homopolymerization of azlactone-containing monomer is favored over grafting, crosslinking or chain scission. Nonlimiting examples of azo compounds useful as homopolymerization initiators include azobis(substituted nitriles) (e.g., l,l'-azobis(cyclohexane carbonitrile) or 2,2'-azobis(isobutyronitrile)) commercially available as VAZO branded compounds from DuPont. Free radical initiators are present in the feedstream in weight percents ranging from about 0.05% to about 5% depending on whether the one- step process or two-step process is used. Bulk homopolymerization also optionally employs adjuvants. These adjuvants can assist in the formation of the homopolymer. Nonlimiting examples of adjuvants are triethylsilane, carbon tetrabromide, and isopropyl alcohol. Adjuvants are optionally present in the feedstream in weight percents ranging from about 0.05% to about 5% depending on whether the one- step process or two-step process is used. When the one-step process is used, the initial feedstream comprises alkenyl azlactone monomer, initiator, adjuvant, and thermoplastic polymer or preferably consists essentially of alkenyl azlactone monomer, initiator, and thermoplastic polymer. In this one-step process, alkenyl azlactone monomer comprises from about 0.5 weight percent to 10 weight percent of the initial feedstream. When the two-step process is used, the initial feedstream comprises alkenyl azlactone monomer, initiator and adjuvant or preferably consists essentially of alkenyl azlactone monomer and initiator. In this step alkenyl azlactone monomer comprises at least 95 weight percent of the initial feedstream. The subsequent feedstream has thermoplastic polymer added for melt blending. FIG. 1 is a schematic of an extruder 10, having a plurality of independently heated zones and a water cooled feed throat, useful for reactive extrusion processing as is those known to those skilled in the art and described in detail in European Patent Publication 0 392 783. Extruder 10 as shown is a twin-screw extruder but also can be a single screw extruder. Commercially available twin-screw extruders are a 34 mm Leistritz counter-rotating twin- screw extruder and a 40 mm Berstroff co-rotating twin-screw extruder. Extruder 10 is useful for the homopolymerization of azlactone monomer described in the first embodiment above. FIG. 2 is a schematic of a twin-screw extruder 20 similar to extruder 10 useful for the homopolymerization of azlactone monomer according to the second embodiment described above. FIG. 3 is a schematic of a twin-screw extruder 30 similar to extruder 10 useful for sequential melt blending of the product of extruder 20, except that azlactone homopolymer, rather than azlactone monomer, is introduced into the feed stream. When using the one-step embodiment, azlactone-containing monomer and initiator is introduced to the feedstream at zone 1 from a vessel 12, which can be a pressurized vessel or a syringe pump. Thermoplastic polymer in pelletized form or in a polymer solution is also introduced into the feedstream at or prior to zone 1 from vessel 14 through a feed throat. At the sixth and seventh zones of extruder 10, there is a vacuum port 15 to vent off residual monomer and volatiles present. Gear pump 16 is used to eliminate surging and produce a continuous strand of material. The blended polymer is quenched in a bath 17 of cooling fluid, such as Fluorinert™ branded heat transfer liquid commercially available from Minnesota Mining and Manufacturing Company of St. Paul, MN in dry ice, or in a bed of dry ice. A water bath is not preferred because water would hydrolyze the azlactone functionality. The cooled, blended polymer is then directed through a pelletizer 18, such as a Conair pelletizer commercially available from Con Air Group of Bay City, Michigan. When using a single screw extruder or a counter-rotating twin- screw extruder in the one-step embodiment, the independently heated zones range in temperature from about 140°C in the first zone to a high temperature of about 225°C in the eighth zone and cooling to a temperature of 180°C adjacent gear pump 16. When using a counter-rotating twin-screw extruder for the bulk homopolymerization/blending embodiment, the independently heated zones range in temperature from about 150°C in the first zone to about 180°C in zones 3 through 10. When using the two-step embodiment, extruder 20 is used with liquid azlactone-containing monomer being maintained in a nitrogen-purged, pressurized or preferably unpressurized vessel 22 and an azo initiator being dissolved in the monomer. Preferably, vessel 22 is stored in an ice bath. When pressurized, the nitrogen-purged environment is maintained at a pressure of about 14 kg/cm 2 [200 psi]. Then the monomer/initiator solution is introduced into the extruder from vessel 22 via a feed line to an open or preferably cooled feed throat. When an open feed throat is used, it is also kept under nitrogen purge conditions. The monomer solution feed rate is controlled by a valve and liquid flow meter or preferably a positive displacement pump, introducing monomer solution at a rate of about 10-150 g/min and preferably at a rate of about 38 g/min, depending on the type of equipment used and the ability of the equipment to vent the heat of the exothermic reaction of the bulk homopolymerization. Adjuvant can be introduced using a positive displacement pump 23 such as that commercially available from Ruska of Instruments Corp. of Houston, Texas. Vacuum ports (collectively 25) are present at the sixth and seventh zones for use in a similar manner as ports 15. The azlactone homopolymer proceeds through gear pump 25, corresponding to gear pump 15; bath 26, corresponding to bath 16; and pelletizer 28, corresponding to pelletizer 18. When using a counter-rotating, twin-screw extruder for the two- step embodiment, the independently heated zones range in temperature from about 15 * C in the feed throat to about 50°C in the first zone to about a maximum of 180 * C (preferably 100-150°C) in zones 3 through 10. The amount of thermoplastic polymer introduced depends on the ultimate weight blend desired for the azlactone-functional article. The weight ratio of thermoplastic polymer to azlactone homopolymer can range from about 99.99:0.01 to about 90: 10 and preferably from about 97:3 to about 94:6. In the two-step embodiment where melt blending follows in sequence after the step of bulk homopolymerization of alkenyl azlactone monomer, Fig. 3 shows an extruder 30 for blending. In this second step, polyazlactone homopolymer or other azlactone-functional composition in a pelletized form is introduced to extruder 30 from vessel 32. Thermoplastic polymer is introduced in pelletized form into extruder 30 from vessel 34, preferably corresponding to vessel 14 used in the one-step process. Vacuum ports 35, preferably corresponding to ports 15 and 25, vent off volatiles. If thermoplastic polymer were introduced into the extruder 30 in solution, then vacuum ports 35 would vent off the solvent also. Gear pump 36, bath 37, and pelletizer 38 correspond to pump 26, bath 27, and pelletizer 28, respectively, in type and function. Alternatively to using an extruder 30, melt blending can be conducted in a Brabender mixer. Melt blending of thermoplastic polymer with azlactone homopolymer can occur at temperatures which are required for the melting of the thermoplastic polymer. Because azlactone homopolymer does not degrade significantly at temperatures below about 275 °C in the time frame of the extrusion process, there are no appreciable deleterious byproducts of the melt blending process. Preferably the melt blending should occur below about 210°C to minimize discoloration of the resulting polymer blend. The temperature of melt blending must be at least at or above the glass transition temperature (Tg) of the thermoplastic polymer and preferably is at least about 25 °C above the Tg of amorphous or glassy polymers such as polystyrene or polymethylmethacrylate and at least about 10° C above the melting point of semicrystalline polymers such as polyethylene and polypropylene. Melt Blending Azlactone-functional Composition with Thermoplastic Polymer A third embodiment of the invention is the melt blending of azlactone-functional compositions, other than azlactone homopolymer prepared by bulk homopolymerization in either embodiment described above, with thermoplastic polymer using a twin-screw extruder, such as extruder 30 as seen in Fig. 3, or other mixing process. Melt blending of thermoplastic polymer with azlactone- functional compositions, prepared separately from the melt blending vessel, can occur at temperatures which are required for the melting of the thermoplastic polymer. Because azlactone-functional compositions do not degrade significantly at temperatures below about 275 °C, there are no deleterious byproducts of the melt blending process. However, care should be taken with azlactone-fiinctional compositions prepared by Michael Addition reaction to use only with lower melting thermoplastic polymers because of lower degradation temperatures of these types of compositions. Preferably to minimize discolorization, the melt blending should occur below about 210°C. The temperature of melt blending must be at least at or above the glass transition temperature (Tg) of the thermoplastic polymer and preferably is at least about 25 °C above the Tg of amorphous or glassy polymers such as polystyrene or polymethylmethacrylate and at least about 10°C above the melting point of semicrystalline polymers such as polyethylene and polypropylene. For example, the melt blending temperature for Nylon 6 commercially available from BASF is about 220°C, which exceeds a temperature that is practical for a reactive extrusion process to form a graft copolymer from VDM and Nylon 6 according to the disclosure of European Publication 0 392 783. The weight ratio of thermoplastic polymer to azlactone- functional composition can range from about 99.99:0.01 to about 50:50, and preferably about 95:5, when the azlactone-functional composition is azlactone homopolymer prepared according to the method described in "Polyazlactones" article or Example 5B of European Patent Publication 0 392 735. In addition to azlactone homopolymer prepared by bulk homopolymerization described above and azlactone homopolymer prepared by suspension or solution polymerization, any of the azlactone copolymers and oligomers described above in the section entitled Azlactone-functional Compositions can be used in melt blending with thermoplastic polymer. These blends need not be compatible. However, the reactivity of incompatible blends with biologically active substances is not comprimised by polymer blend incompatibility. Selections of thermoplastic polymer and the azlactone- functional composition are not limited, unless the azlactone-functional composition contains monomeric units of the thermoplastic polymer. In that instance, the azlactone-functional composition is melt blended with a different thermoplastic polymer having different monomeric units than found in the azlactone-functional composition. Generally, the mixing conditions and temperature conditions for melt blending are the same. A preferred comonomer for the azlactone-functional copolymer is styrene, preferably prepared by graft reactive extrusion according to the methods of European Patent Publication 0 392 783. Preferably, the graft copolymer reactively extruded is styrene with VDM grafted thereto, in a weight ratio ranging from about 99.99:0.01 to about 90:10 and preferably about 95:5 styrene: VDM. In that instance, a styrene: VDM graft copolymer can be blended with thermoplastic polymers that do not contain styrene. This unexpectedly results in blended polymers that have the advantages of all three monomeric components: the azlactone functionality, the styrene base polymer for the azlactone grafts, and the non-styrene polymer for blending. While azlactone-functional graft copolymers prepared by reactive extrusion are acceptable for melt blending, these copolymers are not as preferred as azlactone homopolymers because the reactive extrusion process using peroxide, free radical initiators can cause crosslinking and/or chain scission of the base polymer. Further, there can be unwanted, unreacted VDM remaining in the reactively extruded product, if the process is not properly controlled. Use of azlactone homopolymer and especially bulk homopolymerized azlactone avoids these possible difficulties. Melt Flow Index To make an azlactone-functional article suitable for further processing, the melt blending of the azlactone-functional composition with the thermoplastic polymer should not adversely alter bulk properties of the thermoplastic polymer. Melt flow index is a key bulk property. The azlactone- functional composition can have a melt flow index (g/10 min.) ranging from within about 50% of the melt flow index of the thermoplastic polymer alone to within about 99% of the melt flow index of the thermoplastic polymer alone. Preferably, the melt flow index of the azlactone-functional article is within about 75% of the melt flow index of the thermoplastic polymer alone. Usefulness of the Invention Azlactone-functional articles can have countless uses. As described in the European Publications identified above, azlactone-functional surfaces are particularly useful for nucleophilic reaction with nucleophilic, biologically active substances, defined in the Summary Section. Because a melt blending of thermoplastic polymer with azlactone-functional composition yields a product that is both azlactone- functional and melt processable, any shape of azlactone-functional article capable of being formed thermally can be made. Nonlimiting examples of molding techniques that can be employed include injection molding, blow molding, extruding, melt blowing, compression molding, thermoforming, and the like. Articles of the present invention are especially suited for molded medical articles, molded diagnostic articles, and other biochemical or biopharmaceutical molded equipment likely to be associated or in contact with biologically active substances. Because azlactone-functional moieties occupying a surface of a molded article are capable of multiple chemical reactions, azlactone-functional surfaces of the present invention can form adduct molded articles. Because azlactones do not require intermediate chemical activation for the formation of adducts, azlactones have exceptional versatility and efficiency. Electrophilic azlactone-functional moieties can react through a ring opening reaction at the carbonyl group with any of a myriad of nucleophilic reagents. The result is the formation of an adduct molded article having specific reactivities determined by the nature of the nucleophilic reagent employed in the reaction. Nonlimiting examples of nucleophilic reagents include biologically active substances, acids, bases, chelators, hydrophiles, lipophiles, hydrophobes, zwitterions, detergents, and any other chemical which can react with the azlactone-functionality to confer on the surfaces of the molded article a modified reactivity which differs from that which existed on the article prior to azlactone-functionality modification. For example, one can modify a hydrophobic surface by reacting an azlactone-functional molded article with a nucleophilic, hydrophilic moiety. Examples of nucleophilic, hydrophilic compounds include poly(oxyalkylene amines) commercially available as Jeffamines from Texaco, Inc. Thus, surfaces of an azlactone-functional article can be molded in any desired shape while remaining reactive toward nucleophilic reagents. Unexpectedly, a thermoplastic article can add all of the benefits of azlactone- functionality without an effective diminution of the physical and chemical characteristics of bulk properties of the thermoplastic polymer or its characteristics after molding. Ligands and Adduct Molded Articles Adduct molded articles have ligands coupled or otherwise tightly bound to azlactone-functional moieties extending from surfaces of molded articles to form biologically or chemically active reaction sites. For direct coupling, nonlimiting examples of nucleophilic ligands include primary and secondary amines, alcohols, and mercaptans. Of these, amine-functional ligands are especially preferred. While not being limited to a particular theory, it is believed that a ligand forms a covalent bond when coupled to an azlactone-functional moiety. Ligands useful for the preparation of adduct molded articles can also vary widely within the scope of the present invention. Preferably, a ligand is chosen based upon the contemplated end use of the adduct molded article. Once ligands are coupled to azlactone-functional surfaces of a molded article, such ligands are available for biological or chemical interaction, such as adsorbing, complexing, catalysis, or reagent end use. Adduct molded articles are useful as adsorbants, complexing agents, catalysts, reagents, as enzyme- and other protein-bearing molded articles, and as chromatographic articles. Azlactone-functional moieties will undergo nucleophilic attack by amines, thiols, and alcohols. Thus, ligands having at least one amine, thiol, or alcohol group thereon are candidates for coupling to azlactone-functional surfaces. In a preferred aspect of the present invention, the ligand desired for coupling is a biologically active substance having azlactone-reactive, nucleophilic functional groups. Nonlimiting examples of biologically active materials are substances which are biologically, immunochemically, physiologically, or pharmaceutically active. Examples of biologically active substances include proteins, peptides, polypeptides, antibodies, antigenic substances, enzymes, cofactors, inhibitors, lectins, hormones, receptors, coagulation factors, amino acids, histones, vitamins, drugs, cell surface markers, and substances which interact with them. Of the biologically active substances, proteins, enzymes and antigenic substances are desired for coupling to azlactone-functional molded articles. Nonlimiting examples of proteins, enzymes, and antigenic substances include natural and recombinant Protein A (ProtA), Immunoglobulins such as rat (rlgG), human (hlgG), bovine (blgG), rabbit (rblgG), and mouse (mlgG), Concanavalin A (Con A), Bovine Serum Albumin (BSA), Thyroglobulin (TG), Apoferritin (Af), Lysozyme (Ly), Carbonic Anhydrase (CA), Lipase, Pig Liver Esterase, Penicillin acylase, and Bacterial Antigen (BA). Uses for immobilized proteins, enzymes and antigenic substances are disclosed in European Patent Publication 0 392 735. Alternatively, a molded article of the present invention can comprise a coupled enzyme to catalyze a chemical transformation of substances recognized by the enzyme. Also, a molded article comprising a coupled antigenic substance can be utilized for affinity purification of a corresponding antibody from a complex biological fluid. In other examples, an adduct molded article having Protein A coupled to internal and external surfaces can adsorb biologically active materials such as Immunoglobulin G for affinity separation processes. In other examples, an adduct molded article can be used for immobilization of antibodies or be used for immunodiagnostics or for Western blotting. Alternatively, the ligand can be a hydrophile for improving compatibility of mammalian body implants, such as intraocular lenses, with adjoining tissues. One example of a ligand especially suitable for chemically modifying body implants is an anticoagulant, such as a chemically-modified heparin, e.g. , an amine-terminated heparin. Nonlimiting examples of body implants, with which the molded articles of the present invention could be useful, include artificial organs, heart valves, left ventricular assist devices, and the like. Alternatively, the molded article can be an anticoagulant-treated tubing, connectors, fittings, biosensors, and the like used in association with blood and blood products. Nonlimiting examples include blood oxygenators, dialysis machines and the like. Diagnostic uses of molded articles of the present invention could rely on the capability of specific surface interaction provided by azlactone-functional surfaces. Nonlimiting examples include microtitration wells and plates, chemosensors, and nylon membranes which are widely used in biochemical binding studies, such as in clinical, chemical, or medical diagnostics operations. Optical clarity is particularly desired in clinical, chemical, and medical diagnostic applications. Depending on the type of thermoplastic polymer selected for blending, azlactone-functional articles can be effectively translucent and preferably optically clear and colorless. Unexpectedly, melt blends of poly(methyl methacrylate) and azlactone homopolymer form optically clear, colorless moldable blends. Even though the blends are optically clear, the two polymers are not miscible. Scanning electron microscopy shows dispersed spheres of polyVDM of 0.1-0.3 μ diameter in a matrix of poly(methyl methacrylate). Nonetheless, the surfaces of the blend appear identical to the poly(methyl methacrylate) alone. For example, a blend of poly(methyl methacrylate) and poly(vinyldimethylazlactone) homopolymer in a weight ratio of 95:5 yields an optically clear and colorless article formed by thermal processing. There are also numerous potential uses outside of medical applications. Often multilayered devices need to be fabricated with tie layers, intermediate coatings to bond two functional layers together. Use of azlactone- functional articles of the present invention would allow one skilled in the art to design the two functional layers so that the layers retained their inherent function while also directly bonding with one another, eliminating the need for the tie layer and simplifying the manufacturing process. Another potential application is a bio-active blown microfiber web, preferably using a polyolefin blended with a azlactone-functional composition, and then extruded through web-forming equipment to form a nonwoven, azlactone-functional web. Coupling of ligands to preferred azlactone-functional surfaces can use methods of using inorganic or organic polyanionic salts in such concentrations as to achieve high bound specific biological activity for the coupled ligand, such as methods disclosed in U.S. Pat. No. 5,200,471 (Coleman et al.). Coupling of ligands to azlactone moieties of Formula I above results in adduct molded articles having activated surfaces having the formula wherein R 1 , R 2 , and n are as previously defined, X can be -O-, -S-, -NH-, or -NR 5 wherein R 5 can be alkyl or aryl, and G is the residue of HXG which performs the adsorbing, complexing, catalyzing, separating, or reagent function of the adduct molded article. HXG is a nucleophilic reagent and can be a biologically active substance, dye, catalyst, reagent, and the like. Ligands having azlactone-reactive, amine, hydroxy, or thiol nucleophilic functional groups react, either in the presence or absence of suitable catalysts, with azlactone-functional groups by nucleophilic addition as depicted in the equation. wherein R 1 , R 2 , n, X, and G are as previously defined. Depending on the functional group present in the ligand, catalysts may be required to achieve effective attaching reaction rates. Primary amine functional groups require no catalysts. Acid catalysts such as trifluoroacetic acid, ethanesulfonic acid, toluenesulfonic acid, and the like are effective with hydroxy and secondary amine functional groups. In other aspects of the invention, the ligand is not biologically active but has other properties which lead to its end use. For example, the ligand can contain ionic functional groups. In that event, the resultant adduct article may be utilized in ion exchange type applications. Suitable ionic groups include carboxylic acid, sulfonic acid, phosphonic acid, tertiary amine, and quaternary amine groups. Examples of useful ionic group containing ligands include aminocarboxylic, sulfonic, or phosphonic acids such as glycine, alanine, leucine, valine, β-alanine, 7-aminobutyric acid, 1- and 3-aminopropyl phosphonic acid, taurine, γ-amino octanoic acid, aminomethylphosphonic acid, amino methanesulfonic acid, and the like; hydroxy-acids such as isethionic acid, 3-hydroxy propane sulfonic acid, lactic acid, glycolic acid, hydroxymethylphosphomc acid, p-hydroxybenzoic acid, and the like; and amino- and hydroxy-functional tertiary and quarternary amines such as 2-diethylaminoethylamine, 3-dimethyl aminopropylamine, N,N-diethylethanol amine, and the like, and quatemized versions thereof. When the amine-, hydroxy- or thiol-functional ligand is a simple aliphatic and/or aromatic hydrocarbon, the resultant adduct article may be useful in reverse phase or hydrophobic interaction type chromatographic processes. Reaction of a molded article of this invention with very hydrophilic or hydrophobic ligands can be used to produce adduct articles displaying highly absorbant properties towards aqueous or oily fluids, respectively. Other types of ligands and uses will be obvious to one skilled in the art and are considered to be within the scope of the present invention. Embodiments of the invention are further described in the following examples. Examples 1 - 7: Melt Blending of PVDM With Various Thermoplastic Polymers The mixing chamber of a Brabender Plasticorder mixer (Model EPL-V5501, equipped with a RE.E.6 mixing head, a type SP-T1002 temperature control console and a torque rheometer) was preheated to 180°C under a nitrogen purge. Polyethylene (PE in Table 1) (38 g; Dow LLDPE 2517) was added to the mixing chamber under a nitrogen purge and mixed at 50 rpm until melted. Poly(2-vinyl-4,4-dimethylazlactone), PVDM, (2 g; prepared according to Example 5B of European Patent Publication 0 392 735) was added to the mixing polyethylene. The two polymers were mixed at 50 m for 4 min. The resulting blend was removed from the mixer and stored in a desiccator at room temperature. The blend compositions shown in Table 1 below were prepared using the same equipment and methods as used to prepare the polyethylene blend. PS is polystyrene. PUR is polyurethane. PMMA is poly(methyl methacrylate). Table 1 Blend Compositions Example Base Polymer Wt% Blend PVD Temp M 2 PP (FINA 8771) 5 180°C 3 PS (Polysar 101-300) 2 180°C 4 PS (Polysar 101-300) 5 180°C 5 PUR (Dow 2363) 5 210°C 6 Nylon 6 (BASF B4) 5 220°C 7 PMMA (Rohm & Haas VO44) 5 200°C All blends with the exception of the PMMA blend appear cloudy in the melt state and at room temperature. The PMMA/PVDM blend appears optically clear to the naked eye. The presence of intact azlactone rings in the blends was confirmed by the presence of a strong absoφtion band at 1827 cm "1 in the infrared spectra. The melt flow index of the polymer blends was determined using a Tinius-Olsen Extrusion Plastometer equipped with a MP987 controller and WL 987 lifter. The results are shown in Table 2 below. Table 2 Melt Flow Index (g/10 min) Measurements Sample Conditions Melt Flow Index Example 1 190°C/2160 g 15.9 PE control 190°C/2160 g 20.8 Example 2 190°C/7.4 Kg 39.2 PP control 190°C/7.4 Kg 35.8 Example 3 210°C/7.4 Kg 12.6 Example 4 210°C/7.4 Kg 15.3 PS control 210°C/7.4 Kg 9.4 Example 6 225°C/7.4 Kg 2.6 Nylon control 225°C/7.4 Kg 16.4 Example 7 220°C/8.5 Kg 3.6 PMMA control 220°C/8.5 Kg 3.3 As can be seen from the values shown in Table 2, blending in PVDM does not significantly change the melt flow index of the base polymer except in the case of the nylon blend. It is believed that the significant decrease in the melt flow index of the nylon/PVDM blend as compared to nylon is due to the reaction of the terminal amine groups of the nylon with the azlactone ring resulting in chain extension and branching of the nylon. Films for protein binding studies were prepared by pressing several grams of the polymer blend between TEFLON™ coated aluminum sheets at a pressure of 5,000 psi (350 Kg/cm 2 ) and a temperature of 180°C (210°C for PUR and nylon blends; 200°C for the PMMA blend) for 10 sec in a Wabash heated press. Pressed samples were cooled from the molten state by blotting the metal sheets with a wet paper towel with care being taken to avoid wetting the films. The films were stored in a desiccator. The ability of films prepared from the blends of Examples 1 - 7 to bind protein was determined using the following procedure. Protein A (Repligen, Cambridge, MA) was radioiodonated with Nal 125 using lodo-Beads (Pierce Chemical Co., Rockford, IL) and diluted to give a specific radioactivity of 4900 - 5800 cpm/μg of protein dissolved in buffer with a final protein concentration of 250 μg/mL. Two different buffers were employed. The chloride buffer contained 25 mM sodium phosphate and 150 raM sodium chloride with a pH of 7.5. The sulfate buffer contained 25 mM sodium phosphate and 1.5 M sodium sulfate with a pH of 7.5. Discs (8 mm diameter) were punched from each film using a standard office paper punch. Each disc was placed in a 2.0 mL polypropylene microfuge tube then incubated with 200 μL of Protein A solution for 2 hours at ambient temperature with rocking. Each blend and control were run in triplicate. After 2 hours the protein solution was removed and unreacted azlactone was inactivated by incubating the disc with 1.0 M ethanolamine (500 μh solution in 25 mM sodium pyrophosphate, pH 9.0) for 1 hour with rocking. All discs were rinsed for a minimum of 15 minutes with 500 μL of the chloride buffer. Bound radioactivity was determined with a Packard Gamma Scintillation Spectrometer (Model 5230; Packard Instruments, Downers Grove, IL). Following the initial radioactivity determination, the discs were incubated with 500 μL of a 1 % aqueous solution of sodium dodecyl sulfate (SDS) for 4 hours at 37°C. The discs were rinsed 3 times with the warm SDS solution and the residual radioactivity was determined. SDS is a protein denaturing detergent and serves to remove adsorbed (as opposed to covalently coupled) protein from the film. The results of the protein binding studies are shown in Table 3 below. Table 3 Protein A Binding Results (chloride/sulfate) Sample Bound Protein % SDS Coupled (μg/cm 2 ) Resistance Protein (μg/cm 2 ) Example 1 0.20/0.31 72/71 0.14/0.22 PE Control 0.25/0.26 8/8 0.02/0.02 Example 2 0.34/0.38 67/68 0.23/0.26 PP Control 0.36/0.30 10/8 0.04/0.02 Example 3 0.34/0.51 58/67 0.20/0.35 Example 4 0.40/0.54 56/62 0.22/0.34 PS Control 0.43/0.32 23/22 0.10/0.07 Example 5 0.25/0.41 68/65 0.17/0.26 PUR Control 0.23/0.23 17/14 0.04/0.03 Example 6 0.28/0.58 47/60 0.13/0.34 Nylon Control 0.25/0.36 26/21 0.06/0.07 Example 7 0.23/0.34 52/72 0.12/0.25 PMMA Control 0.19/0.19 18/14 0.03/0.03 Example 8: Retention of PVDM in the Melt Blend A film sample of the PVDM/PE blend prepared in Example 1 was extracted for 48 hours in tetrahydrofuran using a Soxhlet extraction apparatus. Infrared spectrograms were taken before and after extraction. Integration of the azlactone ring band at 1824 cm 1 was used to quantify the percent of the PVDM extracted from the film. The infrared analysis showed that 91 % of the PVDM was retained in the blend after extraction. The percent of PVDM retained in the blend was increased further by partially cross-linking the PVDM. This was accomplished by adding 5 wt% of Jeffamine D-400 (a 400 molecular weight diamine terminated polypropylene oxide available from Texaco) to the blend during processing in the Brabender mixer. Extraction with tetrahydrofuran of a film of the resulting blend showed 100 percent retention of the PVDM in the blend. Examples 9 - 12: Bulk Homopolymerization of VDM and Melt Blending with LLDPE Using a Single Screw Extruder The polymerization/blending process was carried out in a Killion 1.25 inch (3.2 cm), 42: 1 Length/Diameter single screw extruder. VAZO™ 88 (l,r-azobis(cyclohexanecarbonitrile), 5.2 g; from DuPont) was dissolved in 100 g of monomeric 2-ethenyl-4,4-dimethyl-2-oxazoline-5-one, VDM (available from SNPE) and purged with nitrogen. LLDPE (Dow 2517) was starve fed into the feed throat of the extruder under a nitrogen atmosphere. The monomer/initiator was fed into the extruder feed throat via a Sage model 355 syringe pump. Table 4 shows the extruder conditions used to prepare the blends of examples 9 - 12. For all four examples the LLDPE feed rate was 40 g/min, the VDM feed rate was 114 cc/hr, the VDM concentration in the blend was 5% by weight and the initiator concentration was 0.25% by weight. Table 4 Single Screw Extruder Conditions Example 9 Example Example Example 10 11 12 Zone 1 130°C 130°C 130°C 130°C Zone 2 130°C 130°C 130°C 130°C Zone 3 130°C 130°C 130°C 130°C Zone 4 145°C 145°C 145°C 145°C Zone 5 170°C 170°C 200°C 200°C Zone 6 180°C 200°C 200°C 200°C Zone 7 180°C 210°C 210°C 210°C Zone 8 180°C 210°C 210°C 210°C RPM 30 30 20 50 The melt flow index of the polymer blends was determined using a Tinius-Olsen Extrusion Pastometer equipped with a MP987 controller and WL 987 lifter. All measurements were made at 180°C, 2.5 Kg. The values obtained are shown in Table 5 below. Table 5 Melt Flow Index Measurements Sample Melt Flow Index (g/10 min) PE Control 24.5 Example 9 23.9 Example 10 21.5 Example 11 22.1 Example 12 21.4 As can be seen from the velues in Table 5, little cross-linking of the PE takes place during in-situ blending as evidenced by the small decrease in the melt flow index of the blends of Examples 9 - 12. Films for protein binding studies were prepared by pressing several grems of the polymer blend between chrome plates at a pressure of 20,000 psi (1400 Kg/cm 2 ) and a temperature of 180 - 200°C in a Wabash heated press. The ability of films prepared from the blends of Examples 9 - 12 to bind protein was determined using human IgG (Sigma Chemical Co. , St. Louis, MO). The procedure used was similar to that described above for Protein A with the following changes: the sulfate buffer consisted of 0.75M sodium sulfate, 25 mM sodium phosphate, pH$7.5 since higher sulfate concentrations caused IgG precipitation; and 250 μL of protein incubation solution was used. The results are shown in Table 6 below. Table 6 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PE Control 1.57/2.18 34/28 0.55/0.61 Example 9 0.80/1.22 78/68 0.62/0.82 Example 10 0.84/1.57 72/70 0.61/1.10 Example 11 1.09/1.65 65/64 0.71/1.04 Example 12 1.03/1.93 66/63 0.66/1.19 Examples 13 & 14: Bulk Homopolymerization of VDM and Melt Blending with LLDPE in a One-Step Process Using a Twin Screw Extruder The polymerization/blending process was carried out in a Leistritz 34 mm, 35:1 L/D counter rotating twin-screw extruder (Leistritz™ model LSM 30.34GG, Nuremburg, Germany). Vazo 88(5.2 g) was dissolved in lOOg of monomeric VDM and purged with nitrogen. LLDPE (Dow 2517) was starve fed into the feed throat of the extruder under a nitrogen atmosphere. The monomer/initiator was fed into the extruder throat via a Sage model 355 syringe pump. Table 7 below shows the extruder conditions. Both blends were prepared with 5% by weight of VDM and 0.25 % by weight of VAZO 88. Table 7 Twin Screw Extruder Conditions Example 13 Example 14 Temp (°C) Zone 1 145 140 Temp (°C) Zone 2 160 150 Temp (°C) Zone 3 160 150 Temp (°C) Zone 4 167 170 Temp (°C) Zone 5 200 170 Temp (°C) Zone 6 195 200 Temp (°C) Zone 7 190 200 Temp (°C) Zone 8 225 200 Temp (°C) Zone 9 205 200 Temp (°C) Zone 10 215 200 Temp (°C) Block 180 200 RPM 102 50 LLDPE feed rate (g/min) 40 13 VDM feed rate (cc/hr) 114 44 The melt flow index (MI) of each blend was determined using the method and conditions described for Examples 9 -12. The blend of Example 13 had a MI of 21.3 and that of Example 14 had a MI of 14.8. Films for protein binding studies were prepared by pressing several grams of the polymer blend between chrome plates at a pressure of 20,000 psi (1400 Kg/cm 2 and a temperature of 180 - 200°C in a Wabash heated press. The ability of films prepared from the blends of Examples 13 and 14 to bind human IgG was determined using the procedure described above. The results are shown in Table 8 below. Table 8 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PE Control 1.57/2.18 34/28 0.55/0.61 Example 13 1.19/2.09 67/63 0.79/1.31 Example 14 1.26/2.11 65/64 0.82/1.30 Example 15 The mixing chamber of a Brabender Plasticorder mixer (Model EPL-V5501) equipped with a RE.E.6 mixing head, a type SP-T1002 temperature control console and a torque rheometer was preheated to 180°C. PMMA (38 g; Rohm & Haas VM100) was added to the chamber and melted. Vazo 88 (0.10 g) was dissolved in 2.0 g of monomeric VDM. The VDM/initiator mixture was added to the PMMA melt with mixing at 55 φm under a nitrogen purge. The polymer was mixed for 4 minutes. The resulting blend was removed from the mixer and stored in a desiccator at room temperature. Films for protein binding studies were prepared by pressing several grams of the polymer blend between chrome plates at a pressure of 20,000 psi (1400 Kg/cm 2 ) and a temperature of 180-200°C in a Wabash press. The ability of films prepared from the blend of Example 15 to bind human IgG was determined using the procedure described above. The results are shown in Table 9 below. Table 9 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PMMA Control 1.71/1.30 25/33 0.42/0.43 Example 15 1.97/1.95 45/49 0.88/0.94 Examples 16 - 20: Higher Molecular Weight PVDM Melt Blended with PUR Using a Brabender Mixer Monomeric VDM (30 g) was combined with 90 g of tetrahydrofuran and 0.06 g 2,2'-azobis(isobutyronitrile) (AIBN) in a 250 mL round bottom flask and heated under a nitrogen purge at 55-60°C for 24 hours. The resulting polymer solution was poured into approximately 370 g of hexane. The precipitated polymer was collected by filtration and dried under vacuum at 60 °C overnight. The resulting PVDM homopolymer was found by gel permeation chromatography to have a number-average relative molecular mass (M N ) of 34,600. This homopolymer was blended with polyurethane (Pellethane 2363 65D; Dow) in a Brabender mixer, equipped as described above, at 210°C for 3 minutes. The blend compositions and melt flow index values (2.5 Kg; 210°C) are shown in Table 10 below. Table 10 PUR/PVDM (M N = 34,600) Blends Sample % PVDM Melt Flow Index (g/10 min) PUR Control 0 6.7 Example 16 1 10.8 Example 17 2 10.7 Example 18 3 6.8 Example 19 5 8.9 Example 20 10 3.9 Films for protein binding studies were prepared by pressing several grams of the polymer blend between chrome plates for 5 seconds at a pressure of 20,000 psi (1400 Kg/cm 2 ) and a temperature of 225 °C. The plates were chilled in dry ice to facilitate the removal of the films. The ability of films prepared from the blends of Examples 16 - 20 to bind human IgG was determined using the procedure described above. The results are shown in Table 11 below. Table 11 Human IgG Binding Results (chloride/sulfate) Sample Bound Protein % SDS Coupled Protein (μg/cm 2 ) Resistance (μg/cm 2 ) PUR Control 1.24/1.13 20/15 0.24/0.16 Example 16 1.41/1.20 32/34 0.45/0.41 Example 17 1.35/1.15 33/31 0.44/0.36 Example 18 1.40/1.17 46/46 0.65/0.55 Example 19 1.44/1.20 52/47 0.76/0.57 Example 20 1.22/1.05 64/63 0.78/0.66 Examples 21 - 25: Lower Molecular Weight PVDM Melt Blended with PUR Using a Brabender Mixer Monomeric VDM (30 g) was combined with 90 g of tetrahydrofuran and 0.30 g of AIBN and heated under a nitrogen purge at 65 °C for 24 hours. The resulting polymer solution was poured into approximately 360 g of hexane. The precipitated polymer was collected by filtration and dried under vacuum at 60°C overnight. The resulting PVDM homopolymer was found by gel permeation chromatography to have a number-average relative molecular mass (M N ) of 15,700. This homopolymer was blended with polyurethane (PELLETHANE™ 2363 65D; Dow) in a Brabender mixer, equipped as described above, at 210°C for 3 minutes. The blend compositions and the melt flow index values (2.5 Kg; 210°C) are shown in Table 12 below. Table 12 PUR PVDM (M N = 15,700) Blends Sample % PVDM Melt Flow Index (g/10 min) PUR Control 0 6.7 Example 21 1 9.5 Example 22 2 9.7 Example 23 3 9.4 Example 24 5 10.0 Example 25 10 6.4 Films for protein binding studies were prepared as described above for Examples 16 - 20. The ability of films prepared from the blends of Examples 21 25 to bind human IgG was determined using the procedure described above. The results are shown in Table 13 below. Table 13 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PUR Control 1.24/1.13 20/15 0.24/0.16 Example 21 1.37/1.06 62/56 0.85/0.59 Example 22 1.33/1.06 66/64 0.88/0.67 Example 23 1.40/1.12 64/69 0.89/0.78 Example 24 1.30/1.00 72/67 0.93/0.68 Example 25 1.36/1.01 74/73 1.01/0.74 Examples 26 - 30: Lower Molecular Weight PVDM Blended with PMMA Using a Brabender Mixer PMMA (Rohm & Haas VM100) was blended with a PVDM homopolymer having a M N = 15,700 in a Brabender mixer at 200 °C. The blend compositions and melt flow index values (200°C; 7.4 Kg) are shown in Table 14 below. Table 14 PMMA/PVDM (M N = 15,700) Blends Sample % PVDM Melt Flow Index (g/10 min) PMMA Control 0 5.4 Example 26 1 5.4 Example 27 2 5.9 Example 28 3 6.5 Example 29 5 6.8 Example 30 10 7.9 10 Films for protein binding studies were prepared by pressing several grams of the polymer blend between chrome plates at a pressure of 20,000 psi (1400 Kg/cm 2 ) and a temperature of 200°C. The ability of films prepared from the blends of Examples 26 15 30 to bind human IgG was determined using the procedure described above. The results are shown in Table 15 below. Table 15 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PMMA Control 1.91/1.51 16/15 0.30/0.22 Example 26 1.70/1.36 48/44 0.81/0.60 Example 27 1.46/1.33 57/55 0.83/0.73 Example 28 1.62/1.15 64/65 1.03/0.75 Example 29 1.46/1.18 63/64 0.91/0.76 Example 30 1.42/1.11 79/76 1.13/0.85 Examples 31 -35: Higher Molecular Weight PVDM Melt Blended with PMMA Using a Brabender Mixer PMMA (Rohm & Haas VM100) was blended with PVDM homopolymer having a M N = 34,600 in a Brabender mixer at 200°C. The blend compositions and melt flow index values (200°C; 7.4 Kg) are shown in Table 16 below. Table 16 PMMA/PVDM (M N = 34,600) Blends Sample % PVDM Melt Flow Index (g/10 min) PMMA Control 0 5.4 Example 31 1 5.4 Example 32 2 5.3 Example 33 3 5.5 Example 34 5 5.9 Example 35 10 5.5 Films for protein binding studies were prepared as described for Examples 26 - 30. The ability of films prepared from the blends of Examples 31 - 15 to bind human IgG was determined using the procedure described above. The results are shown in Table 17 below. Table 17 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PMMA Control 1.73/1.40 13/13 0.22/0.18 Example 31 1.51/1.12 37/38 0.57/0.43 Example 32 1.49/1.24 36/27 0.54/0.34 Example 33 1.47/1.27 48/32 0.70/0.40 Example 34 1.45/1.16 53/40 0.77/0.46 Example 35 1.24/1.10 64/61 0.80/0.66 Examples 36 - 40: Very Low Molecular Weight PVDM Melt Blended with PMMA Using a Brabender Mixer PMMA (Rohm & Haas VM100) was blended with PVDM homopolymer having a M N = 4000 in a Brabender mixer at 200°C. The blend compositions and melt index values (conditions: 200°C; 7.4 Kg) are shown in Table 18 below. Table 18 PMMA/PVDM (M N = 4,000) Blends Sample % PVDM Melt Flow Index (g/10 min) PMMA Control 0 5.4 Example 36 1 5.2 Example 37 2 5.4 Example 38 3 5.8 Example 39 5 6.4 Example 40 10 8.6 Films for protein binding studies were prepared as described for Examples 26 -30. The ability of films prepared from the blends of Examples 36 - 40 to bind human IgG was determined using the procedure described above. The results are shown in Table 19 below. Table 19 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) PMMA Control 1.54/0.94 7/8 0.11/0.07 Example 36 1.41/0.95 37/37 0.51/0.35 Example 37 1.36/0.87 61/57 0.83/0.50 Example 38 1.27/0.84 70/62 0.89/0.52 Example 39 1.26/0.81 74/68 0.94/0.56 Example 40 1.07/0.84 90/87 0.96/0.73 Example 41: MMA-co-VDM Copolymer Melt Blended with PMMA Using a Brabender Mixer Monomeric methylmethacrylate (MMA, 13.0 g), 13.0 g of monomeric VDM, and 0.125g AIBN were combined then added dropwise over a period of 3.5 hours to 75 g of toluene maintained at 75°C. After the addition, the temperature was raised to 85 °C for 4 hours. The resulting polymer solution was poured into 3 - 4 volumes of hexane. The precipitated polymer was collected by filtration and dried under vacuum at 50 - 60°C overnight. A 4.0 g portion of the resulting methylmethacrylate-vinyl dimethylazlactone copolymer was blended with 36 g of PMMA (Rohm & Haas VO44) in a Brabender mixer, equipped as described above, at 200°C at 55 φm for 2 minutes. Films for protein binding studies were prepared by pressing several grams of the blend between TEFLON™ coated aluminum sheets at 5,000 psi (350 Kg/cm 2 ) and 200°C. The ability of films prepared from the blend of Example 41 to bind Protein A and human IgG was determined using the procedures described above. The results are shown in Table 20 below. Table 20 Protein Binding Results (chloride/sulfate) Sample Bound Protein % SDS Coupled (μg/cm 2 ) Resistance Protein (μg/cm 2 ) Protein A PMMA Control 0.19/0.19 18/14 0.03/0.03 Example 41 0.26/0.34 69/73 0.18/0.25 Human IgG PMMA Control 1.35/1.38 30/26 0.41/0.36 Example 41 1.11/1.38 56/50 0.62/0.66 Examples 42 - 47: PS-g-VDM Graft Copolymers Melt Blended with Various Thermoplastic Polymers PS-g-VDM was prepared according to Example 10 described in European Patent Publication 0 392 783. The PS-g-VDM was used to prepare blends with several thermoplastic resins: styrene-acrylonitrile copolymer (SAN; LUSTRAN™ 31 from Monsanto), polyurethane (PUR; PELLETHANE™ 2363-80A from Dow), a modified polyphenylene oxide (PPO; NORYL™ HP 41 from GE), an engineering thermoplastic (VALOX™ HP 200 from GE), polyoxymethylene (POM; DELRIN™ II from DuPont) and a fluoroelastomer (TEFZEL™ from DuPont). The PS-g-VDM was dry blended with the thermoplastic resin, the dry blend was melt processed in a Baker-Perkins twin screw extruder and the resulting blend was pelletized. The blend compositions and process conditions are shown in Table 21 below. Percentages are by weight. Comparative blends were prepared by blending ungrafted polystyrene with the thermoplastic resin. Table 21 Blend Compositions Example Base % PS % PS-g-VDM Melt Temp Resin (C°) 42 SAN 0 25 220 SAN/PS SAN 25 0 220 43 PUR 0 25 200 PUR/PS PUR 25 0 200 44 PPO 0 25 220 PPO/PS PPO 25 0 220 45 VALOX 0 25 230 VALOX/PS VALOX 25 0 230 46 POM 0 25 175 POM/PS POM 25 0 175 47 TEFZEL 0 25 260 TEFZEL/PS TEFZEL 25 0 260 Films for protein binding studies were prepared by pressing several grams of the polymer blend between chrome-plated aluminum plates at a pressure of 41.4 kPa and a temperature of 200°C. The ability of films prepared from the blends shown in Table 21 to bind Protein A and/or human IgG was determined using the procedures described above. The results are shown in Tables 22 and 23 below. Table 22 Protein A Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) Example 42 1.91/1.13 26/19 0.50/0.22 SAN/PS 2.07/0.98 14/12 0.29/0.12 SAN 2.20/1.14 11/12 0.25/0.13 Example 43 0.16/0.24 34/62 0.05/0.15 PUR/PS 0.17/0.26 28/39 0.05/0.10 PUR 0.21/0.28 35/38 0.07/0.11 Example 44 0.23/0.26 45/46 0.10/0.12 PPO/PS 0.23/0.22 44/31 0.10/0.07 PPO 0.21/0.22 44/32 0.09/0.07 Example 45 0.24/0.21 17/16 0.04/0.04 VALOX/PS 0.26/0.19 12/15 0.03/0.03 VALOX 0.28/0.26 16/16 0.04/0.04 Example 46 0.40/0.35 30/45 0.12/0.16 POM/PS 0.40/0.32 21/21 0.08/0.07 POM 0.30/0.26 7/21 0.08/0.05 Example 47 0.35/0.31 23/31 0.08/0.09 TEFZEL/PS 0.42/0.35 12/11 0.05/0.04 TEFZEL 0.29/0.19 12/9 0.04/0.02 Table 23 Human IgG Binding Results (chloride/sulfate) Sample Bound % SDS Coupled Protein Resistance Protein (μg/cm 2 ) (μg/cm 2 ) Example 42 0.49/0.48 33/32 0.16/0.16 SAN/PS 0.47/0.49 25/24 0.12/0.12 SAN 0.43/0.46 22/22 0.09/0.10 Example 43 0.49/0.49 60/60 0.29/0.29 PUR/PS 0.50/0.48 21/13 0.11/0.06 PUR 0.65/0.59 14/11 0.09/0.06 Example 44 0.45/0.44 33/31 0.15/0.14 PPO/PS 0.43/0.42 25/24 0.11/0.10 PPO 0.46/0.48 29/28 0.13/0.14 Example 45 0.57/0.57 20/22 0.12/0.12 VALOX/PS 0.67/0.54 16/19 0.10/0.10 VALOX 0.60/0.55 14/17 0.08/0.10 Example 46 0.92/1.19 28/34 0.25/0.41 POM/PS 1.17/1.39 25/24 0.30/0.33 POM 1.00/1.46 26/29 0.26/0.43 Comparison Examples 48 and 49 and Examples 50-55: Polymerization of Vinyldimethylazlactone in First Step of Two-Step Process The polymerization was carried out in a Leistritz 34 mm, 35: 1 L/D counter rotating twin-screw extruder (Leistritz™ model LSM 30.34GG, Nuremburg, Germany) and corresponding to Fig. 2 except that no positive displacement pump nor adjuvant was used. Lupersol 101 peroxide initiator was dissolved in VDM monomer. The monomer was purged with nitrogen and placed in a kettle 22, pressurized with nitrogen to about 0.7 kg/cm 2 [10 psi]. The monomer was fed into the feed throat of the extruder and Table 24 shows the conditions used for both Comparison Examples 48 and 49 and Examples 50- 55. For Comparison Examples 48 and 49, the monomer was flood fed into the feed throat of the extruder with all zones heated to 150°C and the block and die pump heated to 180°C, and it appeared that polymerization occmred at the entrance to the first zone of the extruder forming a partial seal and causing a reduction in throughput. In Examples 50-55, the first zone was run cooler at 50°C and the second zone was run at 100°C (all other zones and block and die pump otherwise unchanged), and the monomer was starve fed into the extruder. The polymer formed was extruded through a strand die, quenched on a bed of dry ice, and pelletized. Polymerization was successful. The polymer formed is clear, brittle, and yellow in color. Table 24 RPM Percent Initiator Throughput (g/min) Comparison Ex. 48 180 0.5 60 Comparison Ex. 49 100 0.5 30 Example 50 200 0.25 — Example 51 100 0.25 — Example 52 100 0.5 — Example 53 200 0.5 — Example 54 100 0.75 ~ Example 55 200 0.75 — From Table 24 it is seen that vinyldimethylazlactone can be polymerized using a twin-screw extruder, even though residence time or reaction time was quite short in duration (about 2-4 minutes). The use of reduced temperature zones and starved feeding reduced premature polymerization. Examples 56-155 The following abbreviation chart shows the materials used for Examples 56-155 and their commercial source. Material Chemical Name Trade Name/No. /Prop. Company PMMA Poly(methyl methacrylate) VM100(Injection Moldable Grade) Rohm & Haas PE Poly(ethylene) PE9205(Fract. Melt Flow) Hoechtz PP Poly(propylene) PP6723 Profax(Fract. Melt Flow) HiMont PP Poly(propylene) PP3860(Melt Flow Index50) Fina PS Poly(stryene) PS68S Stryon(Inj. Mold. Grade) Dow Chem. VAZO-52 2,2'-Azobis(2,4-Dimethylpentane nitrile) VAZO 52(Free Rad. Initiator) DuPont AIBN 2,2 , -Azobis(2-Methylpropanenitrile) VAZO 64(Free Rad. Initiator) DuPont PVDM Poly(vinyldimethyl azlactone) Description of various lots below Polv(vinyldϊmethyl azlactone) (PVDM) Preparation Examples 56-58: Solution Polymerized PVDM For Example 56, white PVDM powder was solution polymerized with 0.5wt% 2,2'-Azobisisobutyronitrile (AIBN, VAZO 64) in tetrahydrofuran. The polymer was precipitated in heptane and dried in a vacuum oven. The number average molecular weight (M was 11,000. The PVDM for Example 57 was prepared by high temperature, solution polymerization in toluene. The samples were highly viscous, yellow resins with M„ around 11,000. PVDM for Example 58 was prepared by solution polymerization in a 35% solids mixture of methyl ethyl ketone and triethyl silane using VAZO-64 as the initiator. Various lots with M„ ranging from 12,000 to 23,000 were obtained by adjusting the wt% of VAZO-64. Example 59: Bulk Polymerized PVDM The following example demonstrates the bulk polymerization of VDM in a 34 mm Leistritz counter-rotating, twin screw extruder. Variations were made in the type of initiator, initiator amount, temperature, the effect of vacuum, and amount of adjuvant. The initiator types studied were VAZO-64 (AIBN) and VAZO-52. The adjuvant was isopropyl alcohol (IPA). The process scheme is outlined in Figure 1. The initiator or combination of initiators were dissolved in the VDM monomer. The monomer batch was then purged with N 2 and stored in an ice bath. The monomer stream was fed at 53 g/min into the cooled feed throat of the extruder. The adjuvant was fed into the same throat by using a Ruska positive displacement pump at various flow rates. The temperatures in the zones were set at 50 °C in the first zone, 100 °C in the second zone, and 150 °C in the remaining zones, except for Examples 59c-59i where the temperature after the second zone was 180°C. Zone 6 contained a vacuum port to vent off residual monomer and adjuvant. A gear pump was used at the end of the extruder to eliminate surging and produce a continuous strand of material. The polymer was quenched in a Fluorinert ® heat transfer liquid bath with dry ice and pelletized. Table 25 Process conditions for Examples 59a-59q Example # Initiator IPA Temp Vacuum Residual Mn (wt ) (wt%) CO (%) 59a 0.5 0 150 No 11.70 28,200 59b 0.5 0.96 150 No 11.55 28,600 59c 0.5 1.94 150 No 12.64 27,900 59d 0.5 0 180 No 9.43 24,900 59e 0.5 1.94 180 No 8.71 24,000 59f 0.5 0.96 180 No 9.55 23,100 59g 0.5 1.94 180 Yes 5.93 23,700 59h 0.75 0.96 180 Yes 7.06 19,400 59i 0.75 1.94 180 Yes 5.93 18,300 59j 0.5 0.45 150 Yes NA 29,400 59k 0.5 0.45 150 Yes 12.55 29,100 591 0.5 1.79 150 Yes 10.60 30,800 Example # Initiator IPA Temp Vacuum Residual Mn (wt ) (wt%) CO (%) 59m 0.5 3.1 150 Yes NA 27,600 59n 0.5 4.5 150 Yes 8.98 27,000 59o 0.75 4.5 150 Yes 9.80 24,100 59p* 1.0 4.5 150 Yes 9.95 20,500 59q** 0.75 4.5 150 Yes 8.79 19,300 * VAZO 52 ** VAZO 64/52 all others: VAZO 64 NA = not available Example 60: Bulk Polymerized PVDM From the results of the Example 59, Example 60 considered the feasibility of using a combination of initiators to lower the molecular weight and reduce the level of residuals. The process scheme for the bulk polymerization was the same as in Example 59 with one exception. Two consecutive vacuum ports were used to vent off any unreacted monomer or adjuvant; in Example 59, only one vacuum port had been used. The IPA concentration was maintained at 2.5 weight percent, and the extruder temperatures were set at 50 °C and 100°C in the first two zones and thereafter at 150°C. The temperature in the melt pump was adjusted to remain in the range of 150 * C-160 β C. The monomer feed rate was 37.9 g/min. Except as noted, the polymerization conditions were identical to those used in Example 59. With this slight equipment modification, the residuals decreased considerably. Generally, with the combination of initiators, lower molecular weights (Mn) were prepared. The lowest molecular weights were obtained for samples prepared with higher initiator concentrations and with higher VAZO 52 content. The process conditions are given in Table 26. Increased vacuum venting reduced the residual VDM monomer content of the polymer. With the initiator combination of VAZO 64 and VAZO 52, the M n decreased even at the lower processing temperature. In Examples 60j-60q, VAZO-64 was replaced with VAZO-67; the decomposition byproducts of VAZO-67 are significantly less toxic than those from VAZO-64. Table 26. Process conditions for Examples 60a-60q. Example φ Initiator I ratio IPA Temp Vacuum Residual Mn (wt%) (52/64) (wt%) < * C) (%) 60a 1.0 1.48/1 2.5 150 Yes 5.46 21,500 60b 1.2 0.26/1 2.5 150 Yes 1.33 15,300 60c 1.2 8.58/1 2.5 150 Yes 3.24 19,100 60d 1.78 1/0 2.5 150 Yes 1.42 15,400 60e 2.56 1.51/1 2.5 150 Yes 1.46 11,100 60f 2.33 8.58/1 2.5 150 Yes 1.27 11,900 60g 1.27 1.51/1 2.5 150 Yes 0.68 16,200 I o 60h 2.33 0.26/1 2.5 150 Yes 0.71 14,000 I 60i 1.78 0/1 2.5 150 Yes 0.55 18,800 60j* 2.28 7.32/1 2.5 150 Yes 0.28 14,400 60k* 1.0 1.29/1 2.5 150 Yes 2.63 21,800 601* 2.5 1.29/1 2.5 150 Yes 1.10 11,900 60m* 1.75 1.34/1 2.5 150 Yes 1.31 15,400 60n* 1.22 0.23/1 2.5 150 Yes 2.69 18,400 60o* 1.22 0.23/1 5.0 150 Yes 1.10 21,200 60p* 1.22 0.23/1 7.5 150 Yes 1.20 19,400 60q* 2.28 0.23/1 2.5 150 Yes 0.59 14,600 * VAZO-64 replaced with VAZO-67 Example 61: VDM Homopolymerization in a Co-rotating Extruder VDM was successfully polymerized on a Berstorff 40 mm co- rotating, twin screw extruder. A designed experiment was used to investigate the effect of different adjuvants. The reactions were performed by feeding N 2 purged VDM containing 1 wt% Vazo 52 to the feed throat of the extruder at a controlled flow rate of 37.9 g/min. The adjuvant was either tri-ethyl silane (TES) or carbon tetrabromide; the TES was fed to the extruder with a Gilson pump, while the CBr 4 was dissolved directly in the monomer. The barrel temperatures used for these experiments were 15 "C for zone 1, 60 "C for zone 2, and 100 * C for the remaining zones, with temperatures in the three zones of the melt pump set at 100 o C, 110°C, and 100°C, respectively. Actual temperatures in the zones varied in each zone during the course of the homopolymerization. A single vacuum port was used in zone 8 to help remove residual monomer. The polymer was passed through a gear pump to a strand die, quenched in a Fluorinert ® heat transfer liquid /dry ice bath, and then pelletized. Table 27. Process conditions for Examples 61a-61i. Example # Initiator TES CBr 4 Temp Vacuum Residual Mn Amps (wt%) ( t%) (wt%) ( * C) 61a 1.0 0.0 0.0 100 Yes 7.89 10,500 23.8 61b 1.0 0.0 0.0 100 Yes 10.7 9,360 12.0 61c 1.0 0.0 0.0 100 Yes 8.47 18,200 13.8 61d 1.0 0.34 0.0 100 Yes 6.61 20,200 15.7 I CTi 61e 1.0 0.52 0.0 100 Yes 6.40 19,400 12.9 NJ I 61f 1.0 2.57 0.0 100 Yes 6.24 19,400 20.4 61g 1.0 0.0 0.1 100 Yes 4.25 18,600 11.7 61h 1.0 0.0 0.05 100 Yes 8.95 19,100 13.5 61i 1.0 0.0 0.15 100 Yes 5.88 18,700 18.2 The polymers made in the co-rotating, twin screw extruder were clear and had a slight residual monomer odor. F/j-ramples 62-67 Blends Prepared via Brabender Mixer A 40 g Brabender mixing head with a N 2 purge was heated to 180° C. A known amount of an injection moldable grade PMMA (Rohm & Haas VM100) or PS (Dow PS685) was added and mixed at 55 m for 2 min. PVDM, either in solid form or dissolved in THF at 35% solids, was added at various wt% to the molten polymer and mixed for an additional 4 min. Torque measurements were recorded. The blend was removed and placed in a sealed, glass jar. Tables 28 and 29 outline blends prepared on the Brabender mixer. Table 28. Brabended PMMA/PVDM blends. Example No. PVDM lot % PVDM PMMA (g) PVDM (g) Solvent Torque Mn Comparison 62 None 0 40.01 0.00 none 22.7 11,000 63a Example 56 1.94 39.96 0.79 none 18.1 11,000 63b Example 56 4.76 40.22 2.01 none 20.2 11,000 63c Example 56 4.76 39.88 5.69 anhy THF 13.4 11,000 64a Example 57 1.95 40.19 2.29 THF 19.4 11,000 64b Example 57 4.76 40.77 5.82 THF 14.2 11,000 65a Example 58 1.71 39.99 1.99 mek/tesh 13.1 12,300 65b Example 58 1.71 40.37 2.02 mek/tesh 19.5 16,300 I 65c Example 58 4.76 39.99 5.71 mek/tesh 17.5 18,900 I 65d Example 58 4.76 40.77 5.82 mek/tesh 19.2 12,300 65e Example 58 4.76 39.87 5.69 mek/tesh 19.0 16,300 65f Example 58 4.76 40.31 8.76 mek/tesh 18.1 20,400 65g Example 58 4.76 40.26 5.75 mek/tesh 18.6 23,000 Table 29. Brabended PS/PVDH blends. Example No. PVDM lot % PVDM PS(g) PVDM(g) Solvent Torque Mn Comparison 66 None 0 40.00 0.00 none 13.2 NA I cn 67 Example 59 1 40.00 0.40 none 14.1 27,000 I 67 Example 59 3 40.00 1.20 none 14.7 27,000 67 Example 59 5 40.00 2.00 none 14.2 27,000 F-vamplf-s 68-93 Blends Prepared on the 34 mm or 40 mm Twin Screw Extruders (With Examples 68. 74. 76. 79. 82. and 87 as Comparison Examples) Blends were also prepared on the 34 mm Leistritz counter- rotating extruder and/or the 40 mm Berstorff co-rotating, twin screw extruder. The scheme for processing the blends is illustrated in Figure 2. Three different processes for producing PVDM polymer blends were investigated. The first process utilized a 35% solids solution of PVDM in THF. Both the high temperature polymerized PVDM prepared according to Example 57 above (Examples 69 and 70) and the PVDM powder prepared according to Example 56 (Examples 71-73 and 75) were used. The PMMA was dried at 170 °F for 8 hr and then weigh fed into a cooled feed throat. The solution of PVDM was also fed into the feed throat. Bridging of the two materials and sample color were both major problems for this process. In order to extrude the blend on the 34 mm Leistritz extruder, a processing temperature above 210° C was required. Azlactone functional compounds discolor at or above this temperature. The 40 mm Berstorff co-rotating extruder has much more power than the Leistritz. As a result, the processing temperature for this extruder in center zones was lβCC, and the materials appeared clear. The second process utilized the same PVDM solution lots (Examples 77-81) but fed them into zone 3 of the extruder. This eliminated the problem of bridging in the feed. However, zone 3 was not cooled. By the time the solution reached the barrel where the temperature was above 70 °C, the solvent volatilized, and solid PVDM built up on the tip of the feed line and injection port. The third process completely eliminated the use of solvent. PVDM batches prepared by extrusion polymerization as described in Example 60 (Examples 88-90) were used in pelletized form and fed into the cooled feed port with a small vibratory feeder. PMMA was gravimetrically fed into the same port; bridging was not a problem with this process. Powdered PVDM as described in Example 56 (Examples 91-93) was also conveyed by a vibratory feeder at different rates to produce a PMMA/PVDM blend. Table 30 summarizes the process conditions and blend compositions investigated. The following temperatures in successive zones were set: Examples 68-73: all 5 zones 210°C; Examples 74-75: all zones 165°C, except the last zone at 160°C; Example 81: sequentially 25 °C, 170 °C, 180°C (through next six zones), 195°C, 200 β C, and 205°C with 210°C in the melt pump; Examples 82 and 83: same as Example 81, except 20 °C in the first zone; Examples 84-86: same as Example 81, except 50 °C in the first zone, 70 °C in the second zone, and 10 205 °C in the melt pump; and Examples 87-93: same as Example 81 except 15 "C in the first zone, 70 °C in the second zone, 100 "C in the third zone, and 205 °C in the melt pump. The following temperatures were measured, (to demonstrate some variation during processing occurs): Example 76: sequentially 25 °C, 15 183°C, 180°C, 180°C, 180°C, 170°C, 180°C, 177°C, 185°C, 195°C, 201 °C, and 206 °C with all three zones in the melt pump measured at 210° C; Example 77: sequentially 25 * C, 172°C, 182°C, 183°C, 167°C, 181 β C, 177°C, 183°C, 196 β C, 199'C, and 205°C with 246°C in the melt pump; Example 78: sequentially 25 °C, 170°C, 180 , 180°C, 181 °C, 180 , 178°C, 185 , 20 196 °C, 200 'C, and 205° C with 210° C in the melt pump; Example 79: sequentially 25 °C, 171 °C, 181 °C, 179°C, 179°C, 181 °C, 180°C, 185°C, 195 °C, 200°C, and 206°C with 210°C in the melt pump; and Example 80: sequentially 25°C, 169°C, 180°C, 182°C, 178°C, 178°C, 180°C, 184°C, 195°C, 200°C, and 204°C with 210°C in the melt pump. 25 Table 30 Extruded compositions and process conditions for PVDM blends. Example No. Blend Wt% PVDM Lot PVDM Process AMPS T( * C) 68-L PMMA 0 210 13.9 69-L PMMA/PVDM 2 Example 57 210 15.0 70-L PMMA/PVDM 2 Example 57 210 12.4 71-L PMMA/PVDM 2 Example 56 210 12.8 72-L PMMA/PVDM 2 Example 56 210 13.0 73-L PMMA/PVDM 2 Example 56 210 12.8 74-L PP3860 0 165 9.4 75-L PP3860/PVDM 2 Example 56 165 9.4 76-B PE9255 0 Example 57 180 50 77-B PE9255/PVDM 2.5 Example 57 180 31 78-B PE9255/PVDM 5 Example 57 180 33 79-B PP6723 0 Example 57 180 25 80-B PP6723/PVDM 5 Example 57 180 26 81-B PP6723/PVDM 2.5 Example 57 180 26 82-B PMMA 0 180 50 83-B PMMA/PVDM 2 Example 56 180 50 84-B PMMA/PVDM 2 Example 56 180 50 85-B PMMA/PVDM 5 Example 56 180 50 86-B PMMA/PVDM 7.5 Example 56 180 50 87-B PMMA 0 180 45 88-B PMMA/PVDM 2 Example 60 180 71 89-B PMMA/PVDM 5 Example 60 180 69 90-B PMMA/PVDM 7 Example 60 180 67 91-B PMMA/PVDM 2 Example 56 180 74 92-B PMMA/PVDM 5 Example 56 180 76 93-B PMMA/PVDM 7 Example 56 180 66 L or B after sample # represents L= 34 mm Leistritz extruder or B = 40 mm Berstorff extruder. Comparison Example 94 and Examples 95-106 Protein Binding for Blends Examples 63-65 Prepared with PVDM from Examples 56-58. Table 31 shows the results of protein binding on blends from Comparison Example 62 and Examples 63-65 with PVDM from Examples 56- 58. Table 31. Protein binding for blends prepared with Examples 56-58. Example Blend Sample Type PVDM Type Bound Protein SDS Coupled Coupled No. Example (μg/cm 2 ) Resistance (%) Protein in Protein in NaCl C1S0 4 NaCl Na^ Na^ (μg/cm 2 ) (μg/cm 2 ) Comparison Comparison PMMA Control none 0.60 5±1 0.03 ±.01 0.03 ±.01 94 62 0.42 7±2 95 63a 1.94% PVDM Example 56 0.60 10±4 0.06 ±.03 0.10±.03 0.32 31±10 96 63b 4.76%PVDM Example 56 0.35 17±10 0.06 ±.03 0.10±.04 0.33 30±11 99 63c 4.76% PVDM Example 56 0.43 46 ±6 0.20±.01 0.20±.04 0.31 63±7 o 96 64a 1.95% PVDM Example 57 0.50 38±4 0.19±.01 0.16±.04 I 0.38 42±8 98 64b 4.76% PVDM Example 57 0.41 51±5 0.21±.06 0.19 ±.02 0.37 52±7 100 65a 1.71% PVDM Example 58 0.65 26 ±6 0.17 ±.05 0.15±.01 0.34 44±1 101 65b 1.71% PVDM Example 58 0.60 28 ±4 0.17 ±.02 0.15 ±.04 0.38 40±11 102 65c 1.71% PVDM Example 58 0.58 48±6 0.28 ±.003 0.12 ±.02 0.26 46±6 103 65d 4.76% PVDM Example 58 0.59 39±12 0.23 ±.08 0.18±.04 0.39 46±13 104 65e 4.76% PVDM Example 58 0.52 50±6 0.26 ±.05 0.23 ±.01 0.40 57±4 Example Blend Sample Type PVDM Type Bound Protein SDS Coupled Coupled No. Example (μg/cm 2 ) Resistance (%) Protein in Protein in NaCl C1S0 4 NaCl NajSO.-, Na 2 S0 4 (μg/cm 2 ) (μg/cm 2 ) 105 65f 5.0% PVDM Example 58 0.59 37 ±4 0.22 ±.01 0.14± .02 0.27 51 ±7 106 65g 5.0% PVDM Example 58 0.52 54±4 0.28 ±.004 0.18 ±.005 0.28 64 ±.4 I I Comparison Example 107 and Examples 108-113 Quenchmg Effects Quenching the polymer blends in a Fluorinert ® heat transfer liquid/dry ice bath improved the protein binding and SDS resistance of the blends slightly. More importantly, a Fluorinert ® heat transfer bath with a small amount of dry ice facilitated the pelletizing process. A water bath was unsatisfactory since the water can open the azlactone ring and deactivate the polymer. Table 32 shows the results for Comparison Example 107 and Examples 108-113. Table 32. The Effect of Quenching on Protein Binding for PMMA blends. Example Quench PVDM Bound Cl SDS Coupled PVDM No. Type Type Protein Resistance Protein Mn (μg/cm 2 ) (%) (μg/cm 2 ) in in NaCl NaCl Comp. dry ice None 1.86 7.38± 1.6 0.137 ±.022 107 108 dry ice Example 56 0.44 31.1 ±3.3 .0510 ±.057 11,000 109 dry ice Example 56 1.67 19.6 ±5.3 0.328 ±.102 11,000 110 dry ice Example 56 1.57 20.3 ±4.1 0.320±.071 11,000 111 Fluorinert Example 56 1.56 27.9±3.7 0.423 ± .040 11,000 liquid/dry ice 112 Fluorinert Example 56 1.53 31.4± 1.1 0.479 ±.012 11,000 liquid/dry ice 113 Fluorinert Example 56 1.39 31.6±0.7 0.440±.O01 11,000 liquid/dry ice Comparison Examples 114. 115. 133. 144 and Examples 116-132 and 134- 143 Protein Binding Effects for Bulk Polymerized PVDM from Examples 59 and 60. The protein binding and SDS resistance for the polymer blends prepared in the Brabender from Bulk Polymerized PNDM of Examples 59 and 60 were generally higher than for blends prepared from solution polymerizated PNDM. These trends are shown in Tables 33 and 34 for Comparison Examples 114, 115 and Examples 116-132 for blends of PNDM from Example 59 and for Comparison Example 137 and Examples 134-142 for blends of PNDM from Example 60 blended using a Brabender Mixer and Example 143 and Comparison Example 144 blended using a 40 mm Berstorff extruder. Table 33. Protein binding of 5% PVDM/PMMA blends with PVDM from Example 59. Bound Cl SDS Coupled Color Ranking Example No. PVDM type Protein in Resistance(%) Protein in PVDM Mn (l=clearest) NaCl (μg/cm 2 ) NaCl (μg/cm 2 ) Comparison 114 PMMA-1 1.85 7.4±1.6 0.137±.022 Comparison 115 PMMA-2 5.22 9±3 0.47±.18 116 59a 1.57 54.2±8.7 0.853±.068 28,200 2 117 59b 1.63 47.2±3.4 0.771±.044 28,600 8 118 59c 1.62 54.4±0.2 0.883±.048 27,900 16 119 59d 1.60 50.0±5.7 0.804+.074 24,900 10 120 59e 1.61 50.6±10.0 0.813±.175 24,000 11 I 121 59f 1.78 32.7±3.7 0.581±.039 23,100 9 I 122 59g 1.78 38.2±2.0 0.680+.048 23,700 3 123 59h 1.64 43.1±2.6 0.707+.074 19,400 6 124 59i 1.52 43.8±4.8 0.664+.063 18,300 7 125 59j 1.69 40.2+4.3 0.683±.068 29,400 1 126 59k 1.55 49.4±6.5 0.768±.046 29,100 4 127 591 1.59 42.2±1.3 0.670±.008 30,800 5 128 59m 1.60 51.1±3.1 0.818+.055 27,600 12 129 59n 1.74 46.1+3.7 0.800+.045 27,000 17 130 59o 1.42 50.1+5.1 0.709+.066 24,100 13 131 59p 1.59 49.3±7.4 0.782±.129 20,500 14 132 59q 1.63 44.2+3.6 0.719+.039 19,300 15 Table 34. Protein Binding for 5 PVDM/PMMA blends with PVDM from Example 60. Example No. Sample No. Type PVDM Bound Protein Cl SDS Coupled Protein PVDM Mn (μg/cm 2 ) in Resistance(%) (μg/cm 2 ) NaCl Comparison 133 PMMA Control 4.88 8±4 0.39±0.19 134 5%PVDM/PMMA 60a 4.23 40+2 1.69±0.10 21,500 135 5%PVDM/PMMA 60b 3.91 56+2 2.19±0.14 15,300 136 5%PVDM/PMMA 60c 4.46 41+5 1.83±0.10 19,100 137 5%PVDM/PMMA 60d 4.15 40+14 1.66+0.44 15,400 I Ul 138 5%PVDM/PMMA 60e 4.28 40+1 1.71±0.06 11,100 I 139 5%PVDM/PMMA 60f 4.31 52±4 2.24±0.08 11,900 140 5%PVDM/PMMA 60g 4.22 41+1 1.73±0.03 16,200 141 5%PVDM/PMMA 60h 3.68 57+3 2.10+0.05 14,000 142 5%PVDM/PMMA 60i 4.35 40+3 1.74+0.02 18,800 143 2.5% PVDM/PMMA 60j 4.08 63+4 0.68+0.10 14,400 Comparison 144 PMMA Control — 1.44 18+0.03 0.25+0.05 — for Ex. 143 Comparison Example 145 and Examples 146-154 Protein Binding Effects for Bulk Polymerized PVDM for Example 61. The samples produced according to Example 61 had 5 significantly lower molecular weights and levels of residual monomer. The bioactivity of blends made from these polymers was also substantially higher. PVDM from Example 61 was blended with PMMA on the Berstorff extruder in the solvent-free process described above in Examples 76- 93. The temperatures were set sequentially at 15°C, 130°C, 150°C, 180°C, 10 180°C, 180°C, 180°C, 185°C, 195 , 200°C, and 205 , and 205°C in the melt pump. The flow rate was 37.9 g/min (except for Example 144 where the flow rate was 49.4 g/min). The protein binding results for these blends are given in Table 35 for Comparison Example 143 and Examples 144-151. These blends contained only 2.5% PNDM. 15 Table 35. Protein Binding for 2.5%PVDM/PMMA blends from Example 61. Example Sample No. Type of Bound Protein Cl SDS Coupled PVDM Mn Amps No. PVDM (μg/cm 2 ) in NaCl Resistance Protein (%) (μg/cm 2 ) Comparison PMMA Control 2.12±0.35 25+8 0.55±0.24 41 143 143 2.5%PVDM/PMMA 61a 1.46±0.54 60+2 0.87±0.31 10,500 45 144 2.5%PVDM/PMMA 61b 1.66±0.24 53±3 0.87±0.08 9,360 39 145 2.5%PVDM/PMMA 61c 166±0.18 52+4 0.87*0.12 18,200 46 I 146 2.5%PVDM/PMMA 61d 1.56±0.09 58±6 0.90±0.13 20,200 47 I 147 2.5%PVDM/PMMA 61e 1.76±0.97 63+6 1.07±10.47 19,400 45 148 2.5%PVDM/PMMA 61f 1.51±0.68 71+1 1.08±0.49 19,400 44 149 2.5%PVDM/PMMA 61g 1.59±0.24 50+10 0.80±0.26 18,600 49 150 2.5%PVDM/PMMA 61h 1.60±0.06 66+2 1.05±0.04 19,100 43 151 2.5%PVDM/PMMA 61i 1.38±0.30 67±1 0.92±0.20 18,700 47 The blends prepared with bulk polymerized PVDM according to Examples 59 through 61 had consistently superior protein binding and SDS resistance than blends prepared with PVDM dissolved in solvent according to Examples 56-58. Coupled Protein for PMMA/PVDM blends containing as little as 2.5 PNDM significantly exceeded coupled protein for PMMA alone. Solid or pellet conveying eliminated the use of solvent and significantly reduced the variability in feeding PNDM with thermoplastic polymers. As a result, improved and consistent protein binding results were obtained. COMPARISON EXAMPLES 152 AND 154 AND EXAMPLES 153 AND 155: DETERMINATION OF PERCENT HAZE AND COLOR Samples of 100% PMMA (as Comparison Example 152 and 154) and a 95% PMMA/ 5% PVDM blend of the invention (as Examples 153 and 155) were measured for percent haze according to ASTM method D1003 and for color according to ASTM method E308. Samples of Example 153 and Example 155 were prepared using PVDM prepared according to Example 60j and blended with PMMA using the method according to Examples 88-90 using the Berstorff extruder, except that the zones were sequentially set at 10°C, 130'C, 150 , 180°C, 180°C, 180°C, 180'C, 185°C, 195 , 200°C, and 205 * C, with 205° C in the melt pump. All measurements were made on a Perkin Elmer Lambda 19 Spectrophotometer with RSA-19a integrating sphere accessory. ASTM method D1003 was applied as follows: (1) The calculation was performed according to Procedure B of ASTM method D1003; and (2) A wavelength range of 780 nm to 380 nm at 5 nm intervals was chosen for compatibility with available luminosity tables. (ASTM method D1003 allowed user-defined wavelength range, and 380 to 780 nm is one of the ranges recommended in ASTM method E308). Other instrument parameters for ASTM method E308 are shown in Table 37. Table 36 shows the results that this blend of the invention is nearly 97% clear. TABLE 36 EXAMPLE COMPOSITION % HAZE* THICKNESS Comp. 152a 100% PMMA Unblended 0.45% 0.40 mm Comp. 152b 100% PMMA Unblended 0.46% 0.34 mm 153a 95% PMMA/5% PVDM Blend 3.07% 0.37 mm 153b 95% PMMA/5% PVDM Blend 2.62% 0.36 mm ♦Percent haze was reported to two decimal places, but the variance in sample thickness and measurement errors make precision of these measurements about +/- 0.05%. Color data are reported in Table 37 below. The color data were calculated form total (diffuse) transmission data. Tristimulus and chromaticity values described the color through wavelength range 380 nm to 780 nm at spectral intervals every 5 nm using observer angles 2 degrees and 10 degrees and Illuminant CIE A. Table 37 shows how little difference in color exists between unblended PMMA and an azlactone-functional blend of the present invention. TABLE 37 COMPARISON EXAMPLE 154 EXAMPLE 155 (100% PMMA Unblended) (95% PMMA/5% PVDM Blend) Observer Anσle: 2 deσrees Illuminant CIE A Tristimulus: X=l.01536 Y=0.92403 Z=0.328218 X=l.00243 Y=0.911103 Z=0.315998 Chromaticity: x=0.447767 y=0.407491 z=0.144742 x=0.449616 y=0.408651 z=0.141732 Observer Anαle: 2 deσrees Illuminant CIE C Tristimulus: X=0.905924 Y=0.923844 Z=l.08955 X=0.8896 Y=0.909339 Z=l.04584 I oo Chromaticity: x=0.310319 y=0.316458 z=0.373222 x=0.312712 y=0.319651 z=0.367636 ό I Observer Anσle: 10 deσrees Illuminant CIE A Tristimulus: X=l.02727 Y=0.923991 Z=0.324664 X=l.01392 Y=0.910639 Z=0.31206 Chromatici y: x=0.451365 y=0.405983 z=0.142651 x=0.453328 y=0.407149 z=0.139523 Observer Anσle: 10 deσrees Illuminant CIE C Tristimulus: X=0.898629 Y=0.923752 Z=l.07034 X=0.882004 Y=0.90817 Z=1.0259 Chromaticity: x=0.310651 y=0.319336 z=0.370011 x=0.313203 y=0.322494 z=0.364302 While embodiments of the invention have been described, the invention is not limited thereto. The claims of the invention follow.

Claims: What is claimed is: 1. An azlactone functional thermoplastic composition, comprising: a blend of an azlactone-functional composition and a thermoplastic polymer wherein the azlactone-functional composition is selected from the group consisting of homopolymers of 2-alkenyl azlactone monomers, azlactone-functional compounds having at least two azlactone moieties, azlactone-functional compounds prepared by Michael Addition of 2-alkenyl azlactone monomers and a nucleophilic group substituted compound, and combinations thereof. 2. An azlactone functional thermoplastic composition, comprising: a blend of an azlactone-functional copolymer and only one thermoplastic polymer. 3. A molded article, comprising: the thermoplastic composition of Claim 1 or Claim 2 molded into the article by a molding technique. 4. An adduct molded article comprising a molded article according to Claim 3 and ligand comprising a biologically active substance having azlactone-reactive, nucleophilic-functional groups. 5. The composition according to Claims 1 or 2 or the article according to Claims 3 or 4, wherein the azlactone-functional composition comprises a homopolymer of vinyldimethylazlactone. 6. The composition according to Claims 1 or 2 or the article according to Claims 3 or 4, wherein the thermoplastic polymer comprises poly (methyl methacrylate). 7. The composition according to Claims 1 or 2 or the article according to Claims 3 or 4, wherein the azlactone-functional composition comprises an oxazolinone moiety of the formula: wherein R 1 and R 2 independently can be an alkyl group having 1 to 14 carbon atoms, a cycloalkyl group having 3 to 14 carbon atoms, an aryl group having 5 to 12 ring atoms, an arenyl group having 6 to 26 carbon atoms and 0 to 3 S, N, and nonperoxidic O heteroatoms, or R 1 and R 2 taken together with the carbon to which they are joined can form a carbocyclic ring containing 4 to 12 ring atoms, and n is an integer 0 or 1; or wherein the azlactone-functional composition comprises wherein R 1 , R 2 , and n are as previously defined, wherein z is at least two, wherein R 3 is a bridging group capable of covalently connecting a plurality of azlactone moieties. 8. The composition according to Claims 1 or 2 or the article according to Claims 3 or 4, wherein the thermoplastic polymer is selected from the group consisting of polyamides, polyurethanes, polyacrylates, polymethacrylates, polystyrene, ethlene-vinyl acetate copolymers, poly (N-vinyl lactams), polyvinyl acetates, polyolefms, polyoxyalkylenes, styrene-acrylonitrile copolymers, polyphenylene oxides, fluoroelastomers, polycarbonates, and polyesters, and wherein the azlactone-functional composition comprises from about 0.001 to about 50 weight percent of the azlactone functional thermoplastic composition. 9. The composition according to Claims 1 or 2 or the article according to Claims 3 or 4, wherein the biologically active substance is biologically, immunochemically, physiologically, or pharmaceutically active. 10. A method of making azlactone-functional homopolymers, comprising the steps of: a. introducing an azlactone-functional monomer and free radical initiator into a mixing device having independently heated zones, and b. mixing the monomer and initiator through successive heated zones to cause the monomer to bulk homopolymerize. 11. The method according to Claim 10, wherein the azlactone-functional composition is derived from one or more 2-alkenyl azlactones selected from the group consisting of 2-ethenyl-4,4-dimethyl-l,3-oxazolin-5-one, 2-isopropenyl-4 ,4-dimethyl- 1 , 3-oxazolin-5-one, 2-ethenyl-4-methyl-4-ethyl- 1 ,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-butyl- 1 ,3-oxazolin-5-one, 2-ethenyl-4,4-dibutyl-l ,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-dodecyl-l ,3- oxazolin-5-one, 2-isopropenyl-4,4-diphenyl-l ,3-oxazolin-5-one, 2-isopropenyl-4,4-pentamethylene- 1 ,3-oxazolin-5-one, 2-isopropenyl-4,4-tetramethylene-l,3-oxazolin-5-one, 2-ethenyl-4,4-diethyl-l ,3-oxazolin-5-one, 2-ethenyl-4-methyl-4-nonyl-l,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-phenyl- 1 ,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-benzyl- 1 , 3-oxazolin-5-one, 2-ethenyl-4,4-pentamethylene-l ,3-oxazolin-5-one, and 2-ethenyl-4,4-dimethyl-l ,3-oxazolin-6-one. 12. The method according to Claims 10 or 11, further comprising in step (a) the introduction of a thermoplastic polymer into the extruder, and wherein the azlactone-functional monomer is bulk homopolymerized and blended with the thermoplastic polymer in the extruder. 13. The method according to Claims 10 or 11, wherein the thermoplastic polymer is selected from the group consisting of polyamides, polyurethanes, polyacrylates, ethylene-vinyl acetate copolymers, poly (N-vinyl lactams), polyvinyl acetates, polymethacrylates, polystyrene, polyolefins, polyoxyalkylenes, styrene-acrylonitrile copolymers, polyphenylene oxides, fluoroelastomers, polycarbonates, and polyesters. 14. The method according to Claims 10-13, further comprising steps of: c. quenching extruded product emerging from the extruder, and d. pelletizing the extruded product for later use. 15. The method according to Claims 10-14, wherein the weight ratio of thermoplastic polymer to azlactone-functional composition ranges from about 99.99:0.01 to about 50:50, and wherein the azlactone- functional composition has a melt flow index ranging from within about 50% of the melt flow index of the thermoplastic polymer alone to within about 99% of the melt flow index of the thermoplastic polymer alone. 16. The method according to Claims 10 or 12, wherein the azlactone-functional composition comprises an oxazolinone moiety of the formula: wherein R 1 and R 2 independently can be an alkyl group having 1 to 14 carbon atoms, a cycloalkyl group having 3 to 14 carbon atoms, an aryl group having 5 to 12 ring atoms, an arenyl group having 6 to 26 carbon atoms and 0 to 3 S, N, and nonperoxidic O heteroatoms, or R 1 and R 2 taken together with the carbon to which they are joined can form a carbocyclic ring containing 4 to 12 ring atoms, and n is an integer 0 or 1. 17. The method according to Claims 12-16, wherein the thermoplastic polymer is selected from the group consisting of polyamides, polyurethanes, polyacrylates, ethylene-vinyl acetate copolymers, poly (N-vinyl lactams), polyvinyl acetates, polymethacrylates, polystyrene, polyolefins, polyoxyalkylenes, styrene-acrylonitrile copolymers, polyphenylene oxides, fluoroelastomers, polycarbonates, and polyesters. 18. The method according to Claim 12-17, wherein the thermoplastic polymer is poly(methyl methacrylate) and the azlactone- functional composition is a homopolymer of vinyldimethyl azlactone.

Inventors: COLEMAN PATRICK L, HEILMANN STEVEN M, KANGAS STEVEN L, MENZIES ROBERT H, RASMUSSEN JERALD K, ROLANDO RICHARD J, SAHLIN JENNIFER J, STAHL JULIE B, COLEMAN, PATRICK, L., HEILMANN, STEVEN, M., KANGAS, STEVEN, L., MENZIES, ROBERT, H., RASMUSSEN, JERALD, K., ROLANDO, RICHARD, J., SAHLIN, JENNIFER, J., STAHL, JULIE, B.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1994
Main classification: C08L101
IPC codes: C07D263, C08F2, C08K5, C08L23, C08L33, C08L45, C08L77, C08L101, G01N33