Process for the conversion of a chlorinated alkane feedstock

Abstract: A process for the catalytic conversion of various chlorinated hydrocarbon byproducts and waste products especially to less chlorinated, useful or salable products, in which a chlorinated hydrocarbon feedstock containing two or more chlorines is reacted with hydrogen in the presence of a catalyst consisting essentially of an active hydrogenating metal component such as platinum in elemental or compound form, and a surface segregating metal component such as copper in elemental or compound form on a support.

Description: The present invention relates generally to processes for converting chlorinated hydrocarbons to less chlorinated products and to the catalysts used in such processes. European Patent Application EP-A-0496446 describes the preparation of chlorotrifluoroethylene and trifluoroethylene from 1,1,2-trichloro-1,2,2--trifluoroethane via a catalyst comprised of copper and a Group VIII or noble metal (palladium and platinum being preferred) on a carbon support. Several prior publications address the same conversion and describe the same or different catalysts, see, for example EP-B-0253410 , EP-B-0355907 and EP-A-0459463 . None of these publications describes or suggests, however, that other halogenated feedstocks might be suitably catalytically converted to less halogenated and more useful or more salable materials, and in particular none of these references suggest that the catalysts described therein might be useful outside of the fluorocarbon art. A seemingly separate course of development has occurred with respect to the class of chlorinated hydrocarbon feedstocks which are exclusive of the chlorofluorocarbon feedstocks (and which will henceforth and for simplicity be referred to generically as the chlorinated hydrocarbon feedstocks). With respect to such chlorinated hydrocarbon feedstocks, a number of references may be found which relate to the conversion of a chlorinated alkane feedstock to a less chlorinated alkene product. For example, EP 015665 describes the conversion of 1,1,2-trichloroethane to ethylene or to vinyl chloride via a catalyst including a noble metal chloride, an alkali metal chloride, iron chloride and optionally copper chloride on a silica or alumina support. An earlier Japanese patent publication JP 77/31005 which is referenced in the EP 015665 publication relates to the same overall process, but employs a catalyst of palladium chloride, copper chloride and an alkali metal chloride on a support. US-A-2,886,605 to McClure et al. describes processes for reducing the chlorine or bromine content of halohydrocarbons containing one or both of these halogens via a cuprous halide on porous active alumina catalyst. Specifically contemplated are processes for converting 1,2-dichloropropane to propylene and hydrogen chloride, for converting perchloroethylene to trichloroethylene, and for converting 1,1,2-trichloroethane to vinyl chloride. British patent GB 1,400,529 to Scharfe broadly relates to processes for converting byproduct and waste "hydrocarbon chlorides" to "chlorine-free hydrocarbons" via a rhodium-containing catalyst, and specifically describes the conversion of 1,2-dichloropropane to propane, as well as describing the conversion of chloropropane to propylene. Combinations of rhodium with other metals or metal compounds are contemplated, those being named including palladium, platinum, ruthenium, iridium, iron, cobalt, nickel, copper, gold, vanadium, chromium, molybdenum or tungsten, and the salts, hydroxides, oxides or carboxylates of the alkali and alkaline earth metals. Other known references are specifically addressed to the conversion of 1,2-dichloropropane (hereafter, PDC) to the less saturated, less chlorinated propylene. DE-A-235,630 ,for example, PDC is converted to propylene in a catalytic gas phase reaction at temperatures ranging from 170 degrees Celsius to 450 degrees Celsius. The catalyst is described as an activated carbon which has been treated with a suspension of iron oxides and/or iron oxide hydrates, and then dried at temperatures in the range of 80 degrees to 200 degrees Celsius. Other methods described in this publication include the conversion (preferably at 180-250 degrees Celsius) in the presence of hydrogen and of a rhodium catalyst of PDC to propylene, the dechlorination at normal temperatures of PDC to a mixture (9:1) of propylene and chloropropylene in the presence of a pure titanium catalyst, and the reductive dehalogenation with sodium sulfide and a phase transfer catalyst of chlorinated hydrocarbons to alkylenes. The production of alkylenes from halogenated phosphonate esters under the influence of sulfur and olefinating agents containing phosphorus is also described. EP-A-455 547 discloses a process for the dechlorination of chloromethane with hydrogen and oxygen in the presence of a catalyst on the basis of a Group IB metal or Group VIII metal. EP-A-485 246 relates to the conversion of chlorofluoroethane or chlorofluoroethylene to fluoroethylene or a less chlorinated chlorofluoroethylene in the presence of a catalyst containing a mixture of copper or silver with a Group VIII metal. WO-A-94/7827 which is a reference within the meaning of Art. 54(3) EPC describes a process for the conversion of a chlorinated alkane feedstock to reaction products including a less chlorinated alkene in a commercially substantial proportion in the presence of a supported catalyst including one or more Group IB metals and one or more Group VIII metals. Still other known references involve the conversion of a chlorinated alkane feedstock such as the aforementioned 1,2-dichloropropane to a corresponding less chlorinated alkane. The aforementioned British patent GB 1,400,529 to Scharfe is illustrative, and has been summarized previously. US-A-4,818,368 to Kalnes et al., 4,899,001 to Kalnes et al., and 5,013,424 to James, Jr. et al. are closely related in describing processes for the hydrogenation of halogenated hydrocarbons in the presence of hydrogenating metal or mixed hydrogenating metal catalysts involving a combination of Group VIB and Group VIII metals (the group designations here and throughout the present application deriving from the Periodic Table of the Elements, as published by Sargent-Welch Scientific Company, Skokie, Illinois USA as Catalog No. S-18806 (1979)). "Hydrogenation" in these patents is contemplated as including dehalogenation and olefin saturation in addition to other processes, such as desulfurization, denitrification, oxygenate conversion and hydrocracking. A common objective in each of these various references is the conversion of a chlorinated hydrocarbon feedstock which may be formed as a byproduct or waste material of another useful process into a more directly useful or more salable product or products. A prime example is the conversion of 1,2-dichloropropane or PDC (as a significant byproduct of the chlorohydrin process for producing propylene oxide) to propylene for recycle to a chlorohydrin process for producing propylene oxide, for use in the preparation of allyl chloride or for other uses and benefits. Applicants' inventive processes are similarly focused, and provide for the catalytic conversion of various less-desired chlorinated hydrocarbon feedstocks to corresponding, less-chlorinated products in commercially substantial proportions (that is, at yields (defined as the selectivity to a corresponding, less-chlorinated product multiplied by the conversion, on an hydrogen chloride- and hydrogen-free basis) of a given product of at least 10 percent, but more preferably at least 20 percent and most preferably at least 30 percent), in which a chlorinated hydrocarbon feedstock containing two or more chlorines is reacted with hydrogen in the presence of a supported catalyst which consists essentially of (and preferably consists entirely of) an active hydrogenating metal component in elemental or compound form with a surface segregating metal component, also in elemental or compound form. The desired product(s) is (are) then conventionally separated from those which are not desired, and may be further processed in a conventional, known manner to be placed in condition for an appropriate use or for sale. The reactions contemplated with these catalysts are: the conversion of a chlorinated alkane containing too or more chlorines to reaction products including a corresponding less chlorinated alkene, for example, PDC to propylene. More specifically the present invention relates to a process for the conversion of a chlorinated alkane feedstock containing two or more chlorines to reaction products including a less chlorinated alkene in a commercially substantial proportion, wherein the chlorinated alkane feedstock is reacted with hydrogen in the presence of a supported catalyst consisting essentially of an active hydrogenating metal component in elemental or compound form and a surface segregating metal component in elemental or compound form on a support, the relative concentrations of the metal components being selected so that the less chlorinated alkene is produced in preference, provided that when the active hydrogenating metal component is a Group VIII metal or a plurality of such Group VIII metals, the surface segregating metal component is other than a Group IB metal or a plurality of such Group IB metals. "Less chlorinated" embraces still-chlorinated hydrocarbons as well as hydrocarbons having no remaining chlorine atoms associated therewith. The present invention thus embraces the catalytic conversion of chlorinated alkane feedstocks to corresponding, less-chlorinated alkenes. Examples of preferred chlorinated alkane feedstocks and their corresponding preferred, less chlorinated alkene products include: PDC and propylene; 1,2,3-trichloropropane and allyl chloride, propylene; 1,1,1,2-tetrachloroethane to vinylidene chloride and ethylene; and, 1,1,2-trichloroethane and vinyl chloride. The principles and theory behind surface segregation in catalytic alloys, and the experimental techniques which may be employed to determine surface segregation in such alloys are known in the art, as shown for example in Hegde and Sinha, "ESCA Study of Metals and Alloys", Applied Spectroscopy Reviews, Vol. 19, No. 1, pp. 1-25. Based on prior experimental observations, the general rule is expressed in the referenced publication that with respect to bimetallic alloys, the metal having the lower heat of sublimation and larger atomic radius will segregate preferentially on the surface of the alloy as compared to the bulk. The surface segregating behaviors of ternary systems and the effects of external agencies/catalyst environment and treatment are also discussed. Applicants have found by the present invention that a catalyst consisting essentially of an active hydrogenating metal component and of a surface segregating metal component can be effectively used for a variety of feedstocks and that the selectivity of the catalyst to a given less-chlorinated product over a less-favored such product can be controlled through a knowledge of the surface segregating tendencies of a selected hydrogenating metal component and a selected surface segregating metal component in a given environment and application. More particularly and by way of example, Applicants have found that a given, preferred supported bimetallic catalyst consisting essentially of, and more preferably consisting entirely of, an active hydrogenating metal (such as from Groups VIB or VIII of the above-referenced Periodic Table) and of a second metal determined by experimental surface analysis techniques or previously known to preferentially surface segregate in the presence of the hydrogenating metal, can be made to selectively convert a chlorinated alkane feedstock such as PDC to propylene depending on the relative concentrations of the two metals. The surface segregation behaviors of a number of alloys have already been studied and documented, as noted above with reference to the Hegde and Sinha article. In broad terms, however, the catalysts which are preferred for use in the processes of the present invention consist essentially of one or more active Group VIII hydrogenating metals in elemental or compound form, with one or more metals in elemental or compound form which will surface segregate in combinations with the one or more selected Group VIII metals. It is presently contemplated that the surface segregating component may preferably be selected from among the metals (in elemental or compound form) of Groups IIB, IIIA or IIIB, IVA or IVB, VA or VB, VIA or VIIA, or from the remaining Group VIII metals which will surface segregate with a selected Group VIII hydrogenating metal component (the aforementioned groups again corresponding to those provided in the Periodic Table of the Elements, as published by Sargent-Welch Scientific Company, Skokie, Illinois USA as Catalog No. S-18806 (1979)). Presently preferred catalysts will consist essentially of a selected Group IB surface segregating metal component in elemental or compound form and a selected, active Group VIII hydrogenating metal component in elemental or compound form on a support. More preferably, the catalysts employed in the processes of the present invention will consist entirely of a Group IB surface segregating metal with an active, Group VIII hydrogenating metal on a support. The Group VIII and Group IB metal combinations which are generally favored include platinum (in elemental or compound form) and copper or silver (in elemental or compound form, with copper being preferred to silver) for processes in class (c), and platinum/gold or platinum/silver (platinum/gold being more preferred) for classes (a) and (b). Other Group VIII and Group IB metals can be included in other embodiments, but more preferably, the Group VIII and Group IB metals in a given catalyst will consist simply of platinum and copper in their elemental or compound forms on the one hand or platinum and gold on the other. The proportions and amounts of active hydrogenating metal and surface segregating metal in these catalysts will vary depending on the catalyst's intended use and on the method of catalyst preparation which is employed, but in general terms and for a catalyst prepared by solution impregnation (including more particularly coimpregnation) of the carrier, the selected surface segregating metal can be anywhere from 0.01 to 20 percent by weight (on an elemental basis) of the catalyst, with active hydrogeneting metal comprising from 0.01 to 5.0 percent by weight (also on an elemental basis) of the catalyst. More preferably, the surface segregating metal will be from 0.05 to 15 percent by weight of the catalyst (on an elemental basis) and the active hydrogeneting metal will be from 0.03 to 3.0 percent by weight of the catalyst. Most preferably, the surface segregating metal can be from 0.1 to 10 percent by weight of the catalyst (on an elemental basis) and the active hydrogeneting metal will be from 0.05 to 1.0 percent by weight of the catalyst. The support in each of these various catalysts can be any of the known conventional inert supports, but is preferably silica or carbon, with carbon being most preferred. The carbon is preferably a high surface area carbon, for example, a carbon having a specific surface area in an unimpregnated condition of 200 m 2 /g or more, especially 400 m 2 /g or more, and most especially 600 m 2 /g or more. An example of a commercially-available carbon which has been found to be well-suited for use in various of the contemplated processes is a coal-based carbon produced by Calgon Carbon Corporation, Pittsburgh, Pa. USA under the designation "BPLF3", and may generally be characterized as having a specific surface area of 1100 m 2 /g to 1300 m 2 /g, a pore volume of 0.7 to 0.85 cm 3 /g, and an average pore radius of 12.3 to 14 angstroms. Based on an X-ray fluorescence analysis of this carbon, a typical bulk composition of the BPLF3 carbon has been determined to be as follows (by weight percent): silicon, 1.5 percent; aluminum, 1.4 percent; sulfur, 0.75 percent; iron; 0.48 percent; calcium, 0.17 percent; potassium, 0.086 percent; titanium, 0.059 percent; magnesium, 0.051 percent; chlorine, 0.028 percent; phosphorus, 0.026 percent; vanadium, 0.010 percent; nickel, 0:0036 percent; copper, 0.0035 percent; chromium, 0.0028 percent; and manganese, 0.0018 percent (the remainder being carbon). Other carbons may be preferable for specific processes within the broader class. For example, either a coconut-based carbon such as produced by Calgon Carbon Corporation under the designation PCB (having a published specific surface area of from 1150 to 1250 m 2 /g and a pore volume of 0.72 cm 3 /g ) or a wood-based carbon such as produced by Calgon Carbon Corp. as WSIV Special carbon (having a published or reported specific surface area of 1400 m 2 /g, and a pore volume of 1.25 cm 3 /g) is preferred for the conversion of 1,2,3-trichloropropane to propylene because of the lower rate of catalyst deactivation observed with the use of these catalyst supports in this process application as compared to the aforementioned BPLF3 carbon. The reaction conditions preferred for the different processes of the present invention will again vary, depending for example on the particular catalyst and the particular chlorinated hydrocarbon feedstock involved, and whether the process is to be conducted in the gas phase or liquid phase. In general, however, in the gas phase processes reaction pressures can range from atmospheric up to 1500 psig (10.3 Pa, gauge), with temperatures of from 100 deg. C. to 350 deg. C., residence times of from 0.25 seconds to 180 seconds, and hydrogen/chlorinated alkane feed ratios ranging on a molar basis from 0.1:1 to 100:1. More preferably, reaction pressures will range from 5 psig (0.03 Pa, gauge) to 500 psig (3.4 Pa, gauge), with temperatures of from 180 deg. C. to 300 deg. C., residence times of from 0.5 seconds to 120 seconds, and hydrogen/chlorinated alkane molar feed ratios of from 0.5:1 to 20:1. Most preferably, reaction pressures in the gas phase processes will range from 40 psig (0.28 Pa, gauge) to 300 psig (2.1 Pa, gauge), with temperatures of from 200 deg. C. to 260 deg. C., residence times of from 1 second to 90 seconds, and hydrogen/chlorinated alkane molar feed ratios of from 0.75:1 to 6:1. In the liquid phase processes (which can be conducted in a batchwise or continuous manner, as desired), it is anticipated that the reaction pressures will generally range from atmospheric up to 3000 psig (20.7 MPa, gauge), at temperatures of from 25 degrees Celsius to 350 degrees Celsius, residence times of from 1 to 30 minutes and hydrogen to chlorinated alkane molar feed ratios of from 0.1:1 to 100:1. The conversion of a chlorinated alkane feedstock including two or more chlorines to reaction products including (in a commercially substantial proportion) a corresponding less chlorinated alkene is particularly of interest, and of greater interest still is the direct conversion of such a feedstock to a corresponding non-chlorinated alkene. A preferred example is the gaseous-phase reaction of 1,2-dichloropropane or PDC with hydrogen to form reaction products including propylene in a commercially-substantial proportion. Preferably the catalyst for this process (and for other contemplated processes within the chlorinated alkane to less-chlorinated alkene class) will have been pretreated by exposure to a chloride source, for example, hydrogen chloride, to improve initial selectivity to propylene over propane, and to make the product stream immediately useful in an allyl chloride process (wherein impurity propane in the feed can react with chlorine to produce 1-chloropropane, which because of a similarity in boiling points to allyl chloride is difficult to separate therefrom), for example, or to minimize venting in a propylene oxide process of any propane in the product stream fed or recycled to the propylene oxide process. In this regard, catalysts of the present invention which have been impregnated, dried and reduced under hydrogen have been observed to produce propane with decreasing selectivity and propylene with increasing selectivity over time. The initial chloride source pretreatment substantially reduces, however, the amounts of venting or downstream processing involved in making use of the product stream in a propylene oxide process or allyl chloride process, respectively. Catalysts that have been pretreated by exposure to a chloride source and not reduced, or which have been merely dried and started up (and which have been in essence treated with hydrogen chloride in situ on start up), have been observed to produce the least amount of propane initially, albeit with a substantial penalty in conversion. For this reason, it is considered that it will generally be preferable to both reduce and pretreat (by exposure to a chloride source) a given catalyst, as opposed to reducing the catalyst solely, or not reducing the catalyst at all in favor of chloride-source pretreatment or treatment with HCl in situ on startup. It will also be preferred in the context of this process (and further, in each of the various processes contemplated herein) to employ hydrogen chloride in the feed to reduce coking and catalyst deactivation rates, as exemplified below. Preferably the rate of conversion loss experienced in the processes of the present invention is no more than 0.03 percent per hour, and especially no more than 0.01 percent per hour. The pressure under which the PDC to propylene reaction is conducted preferably ranges from atmospheric pressure to 1500 psig (10.3 MPa, gauge), more preferably from 5 psig (0.03 MPa, gauge) to 500 psig (3.4 MPa, gauge), and most preferably from 50 psig (0.34 MPa, gauge) to 300 psig (2.1 MPa, gauge). The temperature will preferably be from 100 deg. C. to 350 deg. C., more preferably will be from 180 deg. C. to 300 deg. C., and most preferably will be from 200 deg. C. to 260 deg. C. Preferred residence times will be from 0.25 seconds to 180 seconds, more preferably will be from 1.0 seconds to 20 seconds, and most preferably will be from 5 to 15 seconds. Hydrogen to 1,2--dichloropropane feed ratios will preferably be (again, on a molar basis) from 0.1:1 to 100:1. More preferably, the hydrogen to PDC feed ratios will be from 0.3:1 to 10:1, and most preferably from 0.5:1 to 3:1. Preferably this process will on a commercial-scale further include a recycle stream comprised of any unreacted PDC and 2-chloropropane (as a by-product of the reaction), although as suggested above the amount of 2-chloropropane that is produced is preferably minimized by reduction and chloride source pretreatment of the bimetallic catalyst. Those skilled in the art will of course recognize that the processes of the present invention may be combined with other, perhaps conventional processes if expedient for the handling and disposition of various chlorinated feedstocks, and particularly for the expedient processing of streams including a mixture of chlorinated alkane or alkene byproducts. Thus, for example, a process of the present invention for converting chlorinated alkanes to less-chlorinated, useful alkenes could be employed with a preceding process for saturating chlorinated alkenes from within a mixed stream of chlorinated alkanes and chlorinated alkenes, for example a process of the type disclosed in the earlier-cited US-A-4,818,368 to Kalnes et al., 4,899,001 to Kalnes et al., and 5,013,424 to James, Jr. et al. Illustrative Examples The present invention is more particularly illustrated by the examples which follow hereafter. Examples 1-14 Examples 1-14 below focus on the dechlorination of 1,2-dichloropropane over various supported bimetallic catalysts having the same atomic metal ratios of the hydrogenating metal and surface segregating metal, with the catalysts each having been prepared by coimpregnation from an aqueous solution of the chloride salts of the metals involved on the Calgon BPLF3 activated carbon, air-drying for eighteen hours at ambient temperatures, then oven-drying for 2 hours at 120 degrees Celsius. A catalyst charge as thus prepared (0.6 grams in each of Examples 1-14 was then generally placed in a tubular reactor (comprised of Monel™ nickel alloy (unless specifically noted below all of the components, tubing and fittings of the test reactor apparatus were also made of Monel™ nickel alloy (Huntington Alloys, Inco Alloys International, Inc.), having a diameter (O.D.) of 1/2 inch (1.27 cm), and being 12 inches (30.5 cm) in length and located within an aluminum block heated by a cartridge heater and regulated via a computer to maintain a selected reaction temperature of 220 degrees Celsius) over a glass wool support contained in the center of the reactor tubing. The catalyst was then covered with a plug of glass wool and dried for from 1 to 24 hours at 120 degrees Celsius under a nitrogen purge. The catalyst was then reduced by passing hydrogen through the reactor at a flow rate of 90 mL/minute for from 1 to 24 hours. The reaction temperature of 220 degrees Celsius was achieved, and the reaction temperature and hydrogen gas flow were allowed to equilibrate for about 1 hour before the liquid PDC feedstock flow was started into the apparatus. In each instance, PDC was pumped via a high pressure syringe pump through 1/16 inch (1.6 mm (O.D.)) Monel™ nickel alloy tubing into a packed sample cylinder serving as a feed evaporator. The 1/16th inch (1.6 mm) tubing extended almost to the center of the packed cylinder, which was heated to a vaporizing temperature of 180 degrees Celsius using electrical heat tracing. Vaporization of the PDC feedstock was accomplished in the feed line, so that the PDC was superheated when combined with the hydrogen feed stream. Thermocouples were used to monitor the skin temperature of the feed evaporator and the temperature of the gas exiting the feed evaporator, and the temperature of the feed evaporator was controlled by computer. The hydrogen feed stream was metered (at a 3 to 1 molar ratio of hydrogen to PDC) to a preheater using a Model 8249 linear mass flow controller from Matheson Gas Products, Inc. Secaucus, N.J., with the preheater consisting of a packed sample cylinder wrapped with electrical heat tracing. Thermocouples were used to monitor both the skin temperature of the preheater and the temperature of the gas exiting the preheater. The preheater temperature was set and maintained at 140 degrees Celsius. Vaporized PDC exiting the evaporator was mixed with the hydrogen gas from the preheater in a 2 foot (0.61 meter) long section of 1/4 inch (0.64 cm) tubing maintained at a temperature of 140 degrees Celsius. The mixed gases then were passed into and reacted within the tubular reactor at the aforementioned reaction temperature of 220 degrees Celsius, under atmospheric pressure, with a 3:1 molar feed ratio of hydrogen to PDC and a 1 second residence time. After reacting the PDC and hydrogen in the vapor phase in the tubular reactor thus prepared, the products from the reaction were passed to a gas sampling valve, which provided gaseous aliquots for online gas chromatographic analysis in a Hewlett-Packard Model 5890 Series II gas chromatograph (Hewlett-Packard Company). The gas chromatograph was equipped with a flame ionization detector, and used 30 meter by 0.53 millimeter (I.D.) 100 percent methyl silicone/fused silica and 30 meter by 0.53 millimeter (I.D.) porous polymer-lined fused silica columns to separate the various reaction products. Response factors were conventionally determined by injections of gravimetrically-prepared standards of the individual reaction products. These response factors were applied in conjunction with individual peak areas and the total mols of all reaction products to determine the mol percents of individual components in the reactor effluent, and the selectivity to individual reaction products. The results from Examples 1-14 are reported in Table 1 below: HM/SSM (Wt. Pct.) PDC Conversion (Pct.) C 3 H 6 Selectivity (Pct.) C 3 H 8 Selectivity (Pct.) 0.5 Pt/2.0 La 2 28 43 0.5 Pt/0.7 Ti 2 59 24 0.5 Pt/0.7 V 8 22 75 0.5 Pt/0.7 Cr 30 3 96 0.5 Pt/0.8 Mn 40 2 98 0.5 Pt/0.8 Fe 85 1 99 0.5 Pt/0.8 Co 30 3 96 0.5 Pt/0.9 Ni 38 38 60 0.5 Pt/0.9 Zn 30 3 96 0.5 Pd/1.7 Zn 22 53 33 0.5 Pd/2.9 Cd 12 92 2 0.5 Pt/1.6 In 1 41 47 0.5 Pt/1.7 Sn 25 96 1 0.5 Pt/2.9 Bi 5 92 1

Claims: A process for the conversion of a chlorinated alkane feedstock containing two or more chlorines to reaction products including a less chlorinated alkene in a commercially substantial proportion, wherein the chlorinated alkane feedstock is reacted with hydrogen in the presence of a supported catalyst consisting essentially of an active hydrogenating metal component in elemental or compound form and a surface segregating metal component in elemental or compound form on a support, the relative concentrations of the metal components being selected so that the less chlorinated alkene is produced in preference, provided that when the active hydrogenating metal component is a Group VIII metal or a plurality of such Group VIII metals, the surface segregating metal component is other than a Group IB metal or a plurality of such Group IB metals. A process as defined in claim 1, wherein the catalyst consists of an active hydrogenating metal component and a surface segregating metal component on a support. A process as defined in claims 1 or 2, wherein hydrogen chloride is incorporated in the feed to the process. A process as defined in any of claims 1 to 3, wherein the active hydrogenating metal component consists of one or more Group VIII metals in elemental or compound form and the surface segregating metal component is selected from among the metals, in elemental or compound form, of Groups IIB, IIIA or IIIB, IVA or IVB, VA or VB, VIA or VIIA, or from remaining Group VIII metals which will surface segregate with the selected one or more Group VIII active hydrogenating metals. A process as defined in any of claims 1 to 4, wherein the catalyst has been pretreated by exposure to a chloride source. A process as defined in claim 1, wherein the chlorinated alkane feedstock is 1,2,3-trichloropropane and one or both of allyl chloride and propylene are produced in a commercially substantial proportion. A process as defined in claim 1, wherein the chlorinated alkane feedstock is 1,1,1,2-tetrachloroethane and one or both of vinylidene chloride and ethylene are produced in a commercially substantial proportion. A process as defined in claim 1, wherein the chlorinated alkane feedstock is 1,1,2-trichloroethane and vinyl chloride is produced in a commercially substantial proportion. A process as defined in claim 1, wherein the chlorinated alkane feedstock is 1,2-dichloropropane and propylene is produced in a commercially substantial proportion.

Inventors: CISNEROS MARK D, HARLEY DALE A, HOLBROOK MICHAEL T, ITO LARRY N, MURCHISON CRAIG B, SMITH DAVID D, CISNEROS, MARK D., HARLEY, DALE A., HOLBROOK, MICHAEL T., ITO, LARRY N., MURCHISON, CRAIG B., SMITH, DAVID D.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1994
Main classification: C07C1
IPC codes: C07C9, C07C1, C07C11, A62D3, C07C17, C07C21, C07C19, B01J23, C07B61