Silicon on insulator semiconductor device and its fabrication method

Abstract: A semiconductor device comprises an insulating region residing adjacent to a first semiconductor region, a control electrode residing via the insulating region, a second semiconductor region and a third semiconductor region, which have an opposite conduction type to that of the first semiconductor region, residing adjacent to and carrying therebetween the first semiconductor region. When the first, second and third semiconductor regions and the control electrode are grounded, the first semiconductor region in contact with the insulating layer is adjusted to be in weak inversion state, and the potential of the control electrode and that of the first semiconductor region are electrically coupled to be operable.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to semiconductor devices and fabrication methods thereof. In particular, the invention relates to semiconductor devices formed on an SOI (Silicon on Insulator) substrate and fabrication methods thereof. Also, the invention relates to bipolar transistors having a control electrode formed via an insulating film on a base region. Related Background Art In the development of advanced information society nowadays, there has been a great contribution of improved technology for semiconductor devices such as transistors. Among such devices is included a vertical bipolar transistor such as a planar bipolar transistor. The vertical bipolar transistor operates at high speed as a single element, and can act effectively for the current amplification and switching. However, when incorporated as an element into an integrated circuit, the vertical bipolar transistor is difficult to combine with condenser or other transistor from the problem of the process times. One method of constituting an integrated circuit by the combination of a bipolar transistor with other element is to arrange laterally the bipolar transistor to enhance coordination with the process times. There is a Bi-CMOS structure in which a MOS transistor is chosen as other element to combine with the bipolar transistor. Bi-CMOS allows for the design of logics with high speed and low consumption power, because the bipolar transistor operating at high speed and the MOS transistor operating at low consumption power can be incorporated into one IC. The process of incorporating the bipolar transistor as one element in IC of Bi-CMOS fabricated on silicon wafer is referred to as a silicon wafer bulk process. Conventionally, the vertical bipolar transistor and the lateral bipolar transistor has been formed through the silicon wafer bulk process, as shown in Figs. 67 and 68. In Fig. 67, an NPN-type vertical bipolar transistor 301 is electrically separated from other elements by an element separation region 302. Herein, 303 is a P-type silicon substrate, 304 is an N + -type region which is a collector region for the vertical bipolar transistor 301, 305 is an N - -type epitaxial region, 306 is a collector lead-out layer, 307 is a P-type region for element separation, 308 is a selective oxidation region, 309 is a P-type base region, 310 is an N + -type emitter region, 311 is an interlayer insulating layer, 312, 313, and 314 are Al electrodes, and 315 is a passivation insulating layer. In Fig. 68, a PNP-type lateral bipolar transistor is shown. The PNP-type lateral bipolar transistor 321 is electrically separated from other elements by an element separation region 322. Herein, 323 is a P-type silicon substrate, 324 is an N + -type region which is a base region for the lateral bipolar transistor 321, 325 is an N - -type epitaxial region, 326 is a base lead-out layer, 327 is a P-type region for element separation, 328 is a selective oxidation region, 329 is a P + -type emitter region, 330 is an P + -type collector region, 331 is an interlayer insulating layer, 332, 333, and 334 are AI electrodes, and 335 is a passivation insulating layer. In the silicon wafer bulk process, if the element separation region for separating transistor from other elements is not provided as above described, some elements bring about latch-up or a parasitic transistor is produced. Or even if the element separation region is provided, the element separation may not be successful. For these reasons, ICs sometimes bring about malfunction to be inoperable according to the design. In practice, Bi-CMOS is used for decoder unit such as a DRAM, and has a structure as illustrated in Figs. 69A and 69B. However, when this Bi-CMOS is formed of bulk silicon, the process becomes extremely complex because the fabrication of CMOS and vertical bipolar transistor and element separation must be performed. Therefore, the yield is reduced and the cost is increased. If the lateral bipolar transistor is fabricated on the bulk, the process times may be decreased, but the element separation region must be made. To resolve this problem, numerous researches have been made for forming Bi-CMOS on the SOI substrate. The fabrication of Bi-CMOS using the SOI substrate allows the dielectric separation between elements to be simpler. When fabricating bipolar transistor using the SOI substrate, the lateral bipolar transistor may be fabricated in smaller number of process times. The lateral bipolar transistor may be inferior in performance to the vertical bipolar transistor, but can be fabricated through the fabricating process which is also used for the CMOS fabrication. Further, since the lateral bipolar transistor is fabricated on the SOI structure, it can eliminate any external base between emitter and base which will cause a degradation of current amplification gain (h FE ) so that its characteristics can be improved. The method of forming MOS transistor on the SOI substrate is suitable from the respects of suppressing the short channel effect and making the microstructure of element. From the above reasons, the method of forming Bi-CMOS having lateral bipolar transistor on the SOI substrate is expected to be promising. In fabricating Bi-CMOS on the SOI substrate, the lower voltage is required from the point of the withstand voltage and consumption power of element for the microstructure of necessary elements. However, in the bipolar transistor, the potential V BE between emitter and base is not zero volt, and may be about 0.6 to 0.7 volt at minimum. Consequently, in a circuit as shown in Fig. 70, the amplitude of signal transferred is reduced 1.2 to 1.4 volts from the power source voltage of 3.3 volts, and it is necessary that the effective voltage for the driving is 1.9 to 2.1 volts. That is, the on-state voltage of bipolar transistor is about 0.7V while the on-state voltage of MOS transistor is about 0.3 to 0.4V. From such reasons, there is a problem that the driving power for Bi-CMOS is extremely degraded at low voltages, for which it is the only way in the state of the art to construct Bi-CMOS with the MOS circuit when the lower voltage ICs for use with portable commodities are made or the reduction of power voltage due to microstructure is obliged. The construction only with the MOS circuit may not allow the high speed IC to be fabricated. The present inventors have proposed one method of resolving this problem in which a bipolar transistor provided with a control electrode on the base region (hereinafter referred to as a bipolar transistor with control electrode) is used to reduce the on-state voltage equivalent to that of the MOS transistor. This transistor can provide an on-state current with a large threshold for the on-state voltage by applying a voltage to the control electrode to adjust the base region to be in weak inversion state (the p-type base region becomes i-type for the NPN transistor). Fig. 71 shows a structure of the bipolar transistor with control electrode. In Fig. 71, 501 is an oxide film, 502 is a collector, 503 is a base, 504 is an emitter, 505 is an oxide film (insulating film), 506 is a control electrode, 507 is an interlayer insulating film, and 508 is a metal electrode. Fig. 72 shows a gammel plot diagram of the bipolar transistor with control electrode. In Fig. 72, the solid line indicates the characteristic of the bipolar transistor with control electrode, and the dashed line indicates the characteristic of conventional bipolar transistor. The axis of ordinates indicates the base current (I B ) and the collector current (I O ), and the axis of abscissas indicates the base voltage. Supposing that the on-state current occurs when the collector current (I O ) flows at 1 µA, it will be found that the on-state voltage of conventional bipolar transistor not having control electrode is about 0.7V, while that of the bipolar transistor with control electrode is smaller such as about 0.4V. That is, the lateral bipolar transistor with control electrode can flow the equal on-state current with smaller on-state voltage than the bipolar transistor having no control electrode. On the other hand, it is desired that the bipolar transistor with control electrode may be operated at higher speed. But since the transistor of Fig. 71 is of lateral type, the base width (t B1 in Fig. 71) significantly affecting the high speed characteristic may be determined by photolithography technique. In the state of the art, the base width becomes about 0.5 µm at minimum, making it difficult to fabricate the high speed transistor. Hence, the present inventors have devised a fabrication method for reducing the base width of the bipolar transistor with control electrode. Also, the bipolar transistor with control electrode as shown in Fig. 71 must control the voltage between the control electrode and base region so that the base region may be in weak inversion state, and always maintain its voltage during operation. Therefore, the present inventors have devised a semiconductor device which needs no application of voltage between the control electrode for the bipolar transistor with control electrode and the base region. Document IEEE Ed-34(4), April 1987, pp. 845-849, discloses a SOI voltage-controlled bipolar-MOS device (VCBM transistor) with a gate region on a gate oxide, the gate oxide in turn being on a base region. The device according to this document further comprises two semiconductor regions adjacent to the base region, a source/emitter region and a drain/collector region. The base region and the two other semiconductor regions are laminated on an insulator. Further, document M. Rodder et al.: "Silicon-On-Insulator Bipolar Transistors", IEEE ELECTRON DEVICE LETTERS, Vol. EDL-4, No. 6, June 1983, New York, USA, pp. 193-195 discloses a device which is biased into a flatband state and then depleted during further transistor operation. Thus, a surface MOSFET is shown which is in weak inversion in parallel with the bipolar transistor when the device is operated. However, these devices suffer from the drawback that the voltage between the gate electrode and the base region must be controlled. Consequently, it is an object of the present invention to provide a semiconductor device which is free from the above drawbacks. This object is solved by a device and a method according to the appended independent claims 1 and 12. Advantageous modifications are as set out in the respective dependent claims. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-sectional view for explaining a fabrication process of semiconductor device. Fig. 2 is an explanation view showing a projection of a semiconductor device for understanding the present invention. Fig. 3 is a graphic representation for explaining the comparison between the semiconductor device for understanding the present invention and a conventional semiconductor device with the gammel plot. Fig. 4 is a graphic representation for explaining the comparison between the semiconductor device for understanding the present invention and the conventional semiconductor device with the gammel plot. Fig. 5 is a band diagram for explaining an operation principle of the semiconductor device according to the embodiment of the present invention. Fig. 6 is a cross-sectional view showing the constitution of a lateral bipolar transistor with control electrode fabricated by a fabrication method of the semiconductor device of the present invention. Fig. 7 is a cross-sectional view of the lateral bipolar transistor with control electrode showing a fabrication process thereof in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 8 is a cross-sectional view of the lateral bipolar transistor with control electrode showing a fabrication process thereof in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 9 is a cross-sectional view of the lateral bipolar transistor with control electrode showing a fabrication process thereof in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 10 is a cross-sectional view of the lateral bipolar transistor with control electrode showing a fabrication process thereof in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 11 is a cross-sectional view of the lateral bipolar transistor with control electrode showing a fabrication process thereof in accordance with the fabrication method of the semiconductor device of the present invention. Figs. 12A and 12B are a perspective view and a plan view of the lateral bipolar transistor with control electrode showing a fabrication process thereof in accordance with the fabrication method of the present invention. Fig. 13 is a cross-sectional view of a semiconductor device according to an embodiment of the present invention. Fig. 14 is a plan view of the semiconductor device according to the embodiment of the present invention. Figs. 15A and 15B are graphic representations for explaining the characteristics of the semiconductor device according to the embodiment of the present invention. Fig. 16 is a cross-sectional view of a semiconductor device according to another embodiment of the present invention. Fig. 17 is a cross-sectional view of the semiconductor device according to the embodiment of the present invention. Fig. 18 is a plan view of the semiconductor device according to the embodiment of the present invention. Figs. 19A and 19B are graphic representations for explaining the characteristics of the semiconductor device according to the embodiment of the present invention. Fig. 20 is an explanation view of the fabrication process of a semiconductor device for understanding the present invention. Fig. 21 is an explanation view of the fabrication process of semiconductor device for understanding the present invention. Fig. 22 is an explanation view of the fabrication process of semiconductor for understanding the present invention. Fig. 23 is an explanation view of the fabrication process of semiconductor device for understanding the present invention. Fig. 24 is an explanation view of the fabrication process of semiconductor device for understanding the present invention. Fig. 25 is an explanation view of the fabrication process of semiconductor device for understanding the present invention. Fig. 26 is a cross-sectional view showing the fabrication process of an embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 27 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 28 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 29 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 30 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of a semiconductor device of the present invention. Fig. 31 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 32 is a plan view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 33 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 34 is a plan view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 35 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 36 is a plan view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 37 is a plan view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 38 is a cross-sectional view showing the fabrication process of another embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 39 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 40 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 41 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 42 is a plan view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 43 is a cross-sectional view showing the fabrication process of another embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 44 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 45 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 46 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 47 is a plan view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 48 is a cross-sectional view showing the fabrication process of another embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 49 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 50 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 51 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 52 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 53 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 54 is a cross-sectional view showing the fabrication process of the embodiment in accordance with the fabrication method of the semiconductor device of the present invention. Fig. 55 is a plan view showing an embodiment of a bipolar transistor for understanding the present invention. Fig. 56 is a cross-sectional view taken along the line A-A in Fig. 55. Fig. 57 is a cross-sectional view for explaining the fabrication method of the bipolar transistor as shown in Figs. 55 and 56. Fig. 58 is a cross-sectional view for explaining the fabrication method of the bipolar transistor as shown in Figs. 55 and 56. Fig. 59 is a cross-sectional view for explaining the fabrication method of the bipolar transistor as shown in Figs. 55 and 56. Fig. 60 is a cross-sectional view for explaining the fabrication method of the bipolar transistor as shown in Figs. 55 and 56. Fig. 61 is a cross-sectional view for explaining the fabrication method of the bipolar transistor as shown in Figs. 55 and 56. Fig. 62 is a cross-sectional view for explaining the fabrication method of the bipolar transistor as shown in Figs. 55 and 56. Fig. 63 is a cross-sectional view showing another embodiment of a bipolar transistor of the present invention. Fig. 64 is a cross-sectional view showing another embodiment of a bipolar transistor of the present invention. Fig. 65 is a cross-sectional view showing another embodiment of a bipolar transistor of the present invention. Fig. 66 is a cross-sectional view showing another embodiment of a bipolar transistor of the present invention. Fig. 67 is an explanation view of a conventional example. Fig. 68 is an explanation view of the conventional example. Figs. 69A and 69B are explanation diagrams of one example of a Bi-CMOS circuit. Fig. 70 is an explanation diagram of input/output results of the Bi-CMOS circuit. Fig. 71 is a cross-sectional view of a lateral bipolar transistor with control electrode. Fig. 72 is a characteristic diagram for explaining the characteristics of the lateral bipolar transistor with control electrode. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in connection with a semiconductor device of the present invention, comprising an insulating region residing adjacent to a first semiconductor region, a control electrode residing via said insulating region, a second semiconductor region and a third semiconductor region, which have an opposite conduction type to that of said first semiconductor region, residing adjacent to and carrying therebetween said first semiconductor region, characterized in that in the state where said first, second and third semiconductor regions and said control electrode are grounded, said first semiconductor region in contact with said insulating layer is adjusted to be in weak inversion state, and the potential of said control electrode and that of said first semiconductor region are electrically coupled to be operable. The present inventors have thought that a lateral bipolar transistor capable of turning on at low voltages can be provided in such a way that a control electrode is made via an oxide film on a base region of conventional SOI lateral bipolar transistor, and the control electrode material, the thickness of oxide film, the impurity concentration of base region (channel region), and the oxide film are set so that the base region in contact with the oxide film may be placed in weak inversion state, with the control electrode, an emitter and a collector of the same device grounded, (i.e., in a sub-threshold region at a gate voltage V G =0 volt, when operated as a MOS transistor with the electrodes being a gate electrode, a source, a channel, and a drain of the MOS transistor), thereby electrically coupling the base electrode with the control electrode to be operable. Herein, the sub-threshold region is defined as the region where the drain current changes exponentially when the gate voltage is changed. To drive the bipolar transistor at low voltages, it is effective to provide a control electrode 105 to a lateral bipolar transistor on an SOI substrate 101 as shown in Fig. 1, and to electrically connect the control electrode 105 with a base electrode 107 to effect the driving (hereinafter such device is referred to as a "lateral bipolar with control electrode"). Such lateral bipolar transistor with control electrode is of the same constitution as the MOS transistor in which the control electrode corresponds to gate electrode, and the emitter, base and collector correspond to source, channel and drain, respectively. The way of driving this lateral bipolar transistor with control electrode is adapted to the lateral bipolar transistors on bulk Si, but its detailed mechanism is not yet fully grasped. To be operable at low voltages, it is necessary to lower the voltage V ON required to obtain on-state current. Accordingly, it is important to make clear the operation mechanism in the low voltage region. Note that Fig. 2 is a projection view of the lateral bipolar transistor as shown in Figs. 19A and 19B. The present inventors have found, as a result of researches, that the lateral bipolar transistor with control electrode can be divided into three regions in terms of the current component. Referring to Fig. 72 as previously used, its outline will be described. Fig. 72 shows the I C -V BE characteristic of the lateral bipolar transistor with control electrode by the solid line and the characteristic of conventional lateral bipolar transistor by the broken line. Among the three regions of current characteristic, the first region is a sub-threshold region of MOS transistor for the current component, the second region is a mixture of the on-state current region of MOS transistor and that of the lateral bipolar transistor, and the third region is a region of conventional lateral bipolar transistor for the current component. In the case of conventional bipolar transistor, it is necessary that a high current gain (h FE ) is attained to obtain a high collector current in the low voltage region. For this purpose, there is a need for the technology capable of making a base having a thickness of several thousands angstroms. On the contrary, in the lateral bipolar transistor with control electrode, the current value in the first region is determined by the position in the sub-threshold region when the lateral bipolar transistor with control electrode is operated as the MOS transistor, whereby the collector current can be controlled by other parameter than the base width. Fig. 3 shows the characteristic of the lateral bipolar transistor with control electrode fabricated so that the threshold voltage (in the sub-threshold region) may be different, when operated with the MOS transistor, and Fig. 4 shows the characteristic of MOS transistor. The lateral bipolar transistor with control electrode according to the present invention has the characteristic as represented by the curve B, and the conventional lateral bipolar transistor with control electrode has the characteristic as represented by the curve C. These two characteristics are compared in the following. In the curve C, the gate voltage V G =0 volt is not in the sub-threshold region, while in the curve B the gate voltage V G =0 volt is in the sub-threshold region. In the curve B, the collector current increases at the same time when the base voltage V BE becomes 0 volt or greater, whereby it can be found that the collector current reaches the on-state current (e.g., 1 µA) at a lower voltage than in the curve C. That is, the MOS transistor in the curve B is likely to turn on, but if further shifted to the on-state side to have the gate voltage V G =0 volt out of the sub-threshold region, the MOS transistor follows the curve A, whereby the collector current does not increase exponentially to have a device with smaller on/off ratio. That is, to obtain a lateral bipolar transistor with control electrode with high on/off ratio and low on-state voltage, it is important that the device is designed such that the gate voltage V G =0 volt may occur in the sub-threshold region when operated as the MOS transistor. Further, at which point of the sub-threshold region it is set should be determined in accordance with the specification of dark current to be given to the device (current value and dispersion). The above design items are given by the expression as follows, with reference to Fig. 5. Herein, the sub-threshold region of MOS transistor begins upon entering the weak inversion region. That is, this occurs when the surface potential  S and the Fermi potential  F satisfy the inequality  S ≧  F . Accordingly, each parameter is required to satisfy the following numerical expression 1. 2qε S N B  F /C OX +  F +  MS ∓ Q SS /C OX ≦ 0 Where ε S is a dielectric constant of silicon, N B is an impurity concentration for the base, q is a charge elementary quantity, and  F is a Fermi potential, given by the expression 2.  MS is the difference in work function between silicon and gate electrode, Q SS is an interface charge density, and C OX is an insulating film capacity between base region and control electrode. The "-" symbol indicates the NPN type while the symbol "+" indicates the PNP type. The present invention involves controlling the insulating capacity C OX with the thickness of oxide film and the insulating material and  MS with the substrate concentration N B and the control electrode material to satisfy the above condition. Also, when the semiconductor layer is thinner and the depletion layer spread at the gate voltage V G =0 volt reaches the insulating layer for backing, such controls can be made by the thickness of semiconductor film. KT/q • In (N B /N i ) The semiconductor device of the present invention may be a bipolar transistor constituted such that the first semiconductor region is a base region and the second and third semiconductor regions are the emitter and collector regions, respectively, with the distance from the emitter junction of the base region to collector junction being 0.3 µm or less. This semiconductor device can be fabricated by carrying out a fabrication method for the semiconductor device wherein an emitter region, a base region and a collector region are laterally formed on an SOI substrate having a semiconductor region on the surface of an insulating layer or insulator, and comprising an electrode for controlling the potential of the base region via an insulating film, characterized by including the following processes (A) to (E) which are performed in sequence: (A) a process of forming a first insulating film region and a second insulating film region having a greater thickness than that of said first insulating film region on said semiconductor layer of the first conduction type provided on the surface of said insulating layer or said insulator, (B) a process of introducing and activating impurities of the second conduction type into said second semiconductor region below said first insulating film region with said second insulating film region as a mask, (C) a process of depositing a conduction film on said first and second insulating film regions and forming a control electrode by anisotropic etching to leave behind at least a side wall conduction film deposited in a stepped side wall portion between said first insulating film region and said second insulating film region to be directly above the base region, (D) a process of making said emitter region and said collector region by introducing and activating impurities of the first conduction type with said control electrode and said second insulating film region as a mask, and (E) a process of electrically connecting said control electrode with a lead-out electrode of said base region. A fabrication method with the distance between emitter junction and collector junction made 0.3 µm or less will be described in detail. Fig. 6 is a cross-sectional view showing the constitution of a lateral bipolar transistor with control electrode fabricated by the fabrication method of semiconductor device of the present invention, and Figs. 7 to 12A and 12B are cross-sectional views showing the fabrication processes of the lateral bipolar transistor with control electrode by the fabrication method of semiconductor device of the present invention. Note that an NPN-type lateral bipolar transistor with control electrode will be specifically described herein in connection with its structure and the fabrication method. In Fig. 6, 101 is an insulating substrate, 102 is an N-type semiconductor layer, 103 is a second insulating film region having a film thickness T OX2 , 104, 105 are first insulating film regions having a film thickness T OX1 (T OX1 <T OX2 ), 106 is a P-type region serving as the base region, 108 is a side wall, 109, 110 are emitter regions, which are N-type high density regions serving as the collector lead-out electrode region. The lateral bipolar transistor with control electrode according to the present invention utilizes the side wall 108 as the control electrode. Next, the fabrication method of the lateral bipolar transistor with control electrode having the above constitution will be described below. First, the second insulating film region 103 having a film thickness T OX2 and the first insulating film regions 104, 105 having a film thickness T OX1 are provided on the N-type semiconductor layer 102 on the insulating substrate 101, as shown in Fig. 7. Then, T OX1 and T OX2 satisfy the following relation. T OX1 < T OX2 Next, ions of P-type impurity, such as boron are implanted, with the second insulating film region 103 as a mask, to form the P-type region 106, as shown in Fig. 8. Note that a part of the P-type region 106 is a base region, and this ion implantation can determine the base concentration of the lateral bipolar transistor. The concentration of P-type region 106 is preferably 1E17 cm -3 or greater. Thereafter, a conduction film 107 such as polycrystalline silicon of high impurity concentration is deposited (Fig. 9) to form a side wall 108 by anisotropic etching (Fig. 10). In this case, the side wall on the side of collector electrode is removed. The removal can be made by etching with a resist provided only on the base side, for example. The width of the second insulating film region 103 may be about 1 µm, and can be fully processed by exposure technique of micron order. Then, N-type high concentration regions 109, 110 are formed by ion implantation, with the side wall 108 and the second insulating film region 103 as mask member (Fig. 11). In Fig. 11, 109 is an emitter region, 110 is a collector lead-out electrode region, and 106 is a base region. Since the base width can be determined by the width of side wall 108, the base width of 0.3 µm or less can be realized without the use of micro exposure technique. Further, since the side wall which is a control electrode is masked, the control electrode can be formed directly above the base region in self-aligned manner. As a result, the capacity between control electrode and emitter can be suppressed to a small value. Also, owing to the existence of the second insulating film region 103, the capacity with respect to the collector can be reduced. Note that in forming the emitter region 109 by ion implantation, the emitter region may be constituted of SiC having a greater forbidden band width by implanting C ions. In this case, the emitter region may be also constituted of microcrystalline Si or amorphous Si having a great forbidden band width by implanting Si ions. There are several possible means for electrically coupling the control electrode with the base lead-out electrode, and one such means is shown in Figs. 12A and 12B, for example. Fig. 12A is a perspective view showing the coupled state, and Fig. 12B is a plan view. In the figure, 111 is a metallic wiring such as aluminum, 112 is a base lead-out electrode, and 113 is a border line for element separation such as an edge of selective oxide section. 114 is a region having a concentration equal to that of the base region 106, wherein the base lead-out electrode 112 resides within a high density p-type impurity region 114. Metallic film is deposited on a part of the side wall 108 to take the potential of control electrode, and the control electrode and the base lead-out electrode are connected by the same metallic film. The present invention is to fabricate a lateral bipolar transistor with control electrode having the side wall portion as a control electrode, and a base region directly below the control electrode in self-aligned manner, with a base width of 0.3 µm or less, by including at least the above processes according to the present invention in the device fabrication process, whereby the lateral bipolar transistor with control electrode which is a low voltage, highly driving device with a base width of 0.3 µm or less can be fabricated in the inexpensive process without the use of micro exposure process technique. Further, the present inventors have developed a semiconductor device comprising an insulating region residing adjacent to a first semiconductor region, a control electrode residing via said insulating region, a second semiconductor region and a third semiconductor region, which have an opposite conduction type to that of said first semiconductor region, residing adjacent to and carrying therebetween said first semiconductor region, characterized in that in the state where said first, second and third semiconductor regions and said control electrode are grounded, said first semiconductor region in contact with said insulating layer is adjusted to be in weak inversion state, and the potential of said control electrode and that of said first semiconductor region are electrically coupled to be operable, and the base region which becomes said first semiconductor region is formed by diffusion of impurities from the substrate surface, said control electrode is formed via an insulating film on the side of said base region to constitute a bipolar transistor. By carrying out this invention, a semiconductor device can be fabricated wherein the impurity concentration profile in said base region is smaller from emitter junction to collector junction. Also, by carrying out this invention, two or more emitter regions serving as said second semiconductor region can be formed. Further, by carrying out this invention, a semiconductor device can be fabricated wherein a thin oxide film is provided between the emitter region serving as said second semiconductor region and the emitter electrode, and the conduction between said emitter region and said emitter electrode is made with a tunnel current. Also, an SOI (Silicon on Insulator) can be constituted with said semiconductor device made on an insulator. The emitter region serving as said second semiconductor region can be constituted from a semiconductor having a larger forbidden band width than the semiconductor constituting said base region. This semiconductor device can be obtained by carrying out a fabrication method of semiconductor device wherein an emitter region, a base region, and a collector region are vertically formed, and the conduction type of said base region is controlled via a control electrode, characterized by including at least the following processes (A) to (E) which are performed in sequence: (A) a process of implanting impurity ions from the surface and making heat treatment to make on a semiconductor substrate of the first conduction type, a well region of the second conduction type opposite to that of the semiconductor substrate, (B) a process of making epitaxial growth to deposit a region with small impurity concentration of the second conduction type equal to that of said well region on said well region (the region made through this process is hereinafter abbreviated as an epitaxial region), (C) a process of implanting impurity ions of the second conduction type into a part of said epitaxial region to make said emitter region a high concentration impurity region, (D) a process of removing selectively said epitaxial region, (E) a process of depositing an insulating region on said epitaxial region, (F) a process of depositing a low resistive region on said insulating region and removing it with only the portion serving as a control electrode left behind, (G) a process of depositing a new insulating region to cover said control electrode, (H) a process of making said base region by implanting impurity ions of the first conduction type into said epitaxial region, and (J) a process of making said emitter region by implanting impurity ions of the second conduction type into said epitaxial region. Example 1 A semiconductor device of example 1 is shown in Figs. 13 and 14. This semiconductor device was fabricated in the following steps (1) to (8). (1) An SIMOX substrate was used in which the thickness of an oxide film 502 for backing was 400 nm, and the thickness of a semiconductor film 503 was 500 nm. (2) By field oxidation, an active region 500 was left behind, and the remaining semiconductor region was oxidized. (3) Boron ions were implanted into an entire surface of the active region 500, which was then subjected to heat treatment at 1100°C for three hours. By this process, the base density was 2x10 16 cm -3 . (4) A silicon oxide film 504 having a thickness of 30 nm was formed by thermal oxidation as an insulating film between base region 507 and control region 505. (5) An N-type polycrystalline silicon of high density was made by ion implantation after depositing polycrystalline silicon to form a control electrode 505. (6) An emitter region 506 and a collector region 508 were formed in self-aligned manner with the control electrode 505 as a mask. In this case, the dose quantity was 2x10 15 cm -3 of arsenic, and consequently, an emitter-collector region of 2x10 19 cm -3 was formed. Also, to lead out the base electrode, boron ions were implanted into the lead-out portion with the same dose quantity. (7) An interlayer insulating film was formed by depositing PSG 600 nm thick by CVD. (8) Wiring was made to each electrode by sputtering Al-Si after opening a contact hole. In particular, a contact 509 belongs to base electrode and is connected by Al-Si with a contact of the control electrode nearby. Fig. 15A shows the characteristic of the lateral bipolar transistor with control electrode in the example 1 which is fabricated in the above manner and operated as the MOS transistor. This MOS transistor was assessed which was wired such that the base electrode and the gate electrode could be controlled independently without short-circuiting (four terminal device). In the characteristic of MOS transistor, it will be seen that the gate voltage V G =0 volt is in the sub-threshold region. Since the substrate density of the base region corresponding to the channel region of MOS transistor is 2x10 16 cm -3 ;  F is equal to 0.386. Accordingly, the left side of the numerical expression 1 is -0.187 by calculation, which can satisfy the numerical expression 1 as previously given. The characteristic of the lateral bipolar transistor with control electrode in the example 1 is shown in Fig. 15B. Supposing that the on-state current is 1 µA, the on-state current of the lateral bipolar transistor of this example is 0.4 volt, whereas that of conventional bipolar transistor is 0.7 volt. Thus, the bipolar transistor having the on-state current increasing exponentially from V G =0 volt with a high on/off ratio and operable at low voltages could be obtained. Example 2 A semiconductor device of example 2 was fabricated through the same process as in example 1, except that polycrystalline silicon was deposited on a quartz substrate, and an SOI substrate monocrystallized by laser recrystallization. Bipolar transistor with control electrode fabricated in example 2 is a bipolar transistor which has the on-state current exponentially increasing from V G =0 volt, as shown in Fig. 15B, with a high on/off ratio, and is operable at low voltages. Example 3 A semiconductor device of example 10 as shown in Figs. 16 to 18 was fabricated through the following steps of (1) to (8). (1) An SIMOX substrate was used in which the thickness of oxide film 702 for backing was 500 nm, and the thickness of semiconductor film 703 was 100 nm. (2) By field oxidation, an active region 700 was left bebind, and the remaining semiconductor region was oxidized. (3) Boron ions were implanted into an entire surface of the active region 700, and heat treatment was conducted at 1100°C for three hours. By this process, the base density was 1x10 16 cm -3 . (4) A silicon oxide film 704 having a thickness of 16 nm was formed by thermal oxidation method as an insulating film to be provided between base region 707 and control region 705. (5) A mask 710 having a width of 0.2 µm was formed by EB exposure and with a multi-layer resist. (6) An emitter region 706 and a collector region 708 were formed using a mask 710 having a width of 0.2 µm and by ion implantation. In this case, the dose quantity was 2x10 15 cm -3 of arsenic, and consequently, an emitter-collector region of 2x10 19 cm -3 was formed. Also, a base lead-out portion was subjected to implantation of boron ions with the same dose quantity. (7) A contact hole was directly formed without providing an interlayer insulating film. (8) Yttrium Y was deposited by EB vapor deposition and patterning was made for wiring to provide a control electrode 705. Herein, the work function of yttrium is 3.15 eV, and the difference in work function between it and p-type silicon having a concentration of 1x10 16 cm -3 is 1.9 eV. To realize a bipolar transistor having a high cut-off frequency, it is necessary to form the transistor having a small base width. In recent years, the improved exposure technology permits the processing of as small as 0.2 µm, as in this example. If the base width is reduced, the concentration must be increased to about 10 16 cm -3 to suppress the punch-through from emitter to collector. As a result, in the lateral bipolar transistor with control electrode, the threshold voltage of MOS transistor having the base region as the channel rises, and it is quite difficult to have V G =0 within the sub-threshold region in the N-type polycrystalline silicon having conventional gate electrode material. The threshold voltage can be lowered by reducing the thickness of oxide film, in which case the oxide film thickness is required to be reduced to about 8 nm, giving rise to a problem in the reliability of the oxide film. Also, when the base concentration is high, the oxide film thickness can be increased to 16 nm by using a material having a small work function such as yttrium, whereby a high speed bipolar transistor can be provided with the reliability of the oxide film maintained. In this example, yttrium was used, but besides, strontium, lanthanum, and cesium can be employed. Example 4 A lateral bipolar transistor with control electrode, i.e., a semiconductor device of example 4, was fabricated through exactly the same process as in example 1, except that SIMOX substrate used comprised the oxide film for backing having a thickness of 500 nm and the semiconductor film having a thickness of 50 nm, and the base concentration was set at 2x10 17 cm -6 in the above process (3). In this example, the maximum width of depletion layer in base region formed by the MOS structure having a control electrode 505, an insulating film 504 and a base region 507 is 75 nm. And the depletion layer width when the sub-threshold region begins is 53 nm. In this case, the MOS transistor is operable with the semiconductor film in a totally depleted state. The threshold voltage of MOS transistor in such totally depleted state is lower than that of MOS transistor formed at the same channel density on the bulk silicon. This behavior is shown in Figs. 19A and 19B. Curve A of Fig. 19A shows the characteristic when the lateral bipolar transistor with control electrode of example 4 is operated as the MOS transistor, and curve B shows the characteristic for the MOS transistor on the bulk silicon having the same channel density. Fig. 19B shows the characteristic when these two devices are operated as the lateral bipolar transistor with control electrode. Herein, curve A and curve B show the characteristic of device on the bulk silicon for the example 4 and the comparison, respectively. Device in example 4 has the current value exponentially increasing simultaneously when the voltage is input, while device on the bulk silicon can not obtain the same collector current unless about 0.2 volt is applied in excess. This device is one in which V G =0 is not within the sub-threshold region by controlling the position of the sub-threshold region only with the oxide film thickness and the base density as was conventionally performed, but this example is designed such that by reducing the semiconductor film thickness of SOI below the maximum depletion layer width to lower the threshold voltage, V G =0 volt is within the sub-threshold region. As a result, the lateral bipolar transistor with control electrode can be provided in the high density base only by the material used in the conventional silicon process. Example 5 An example 5 will be described using Figs. 20 to 25. This example was fabricated through the following steps of (1) to (14). (1) A silicon wafer 901 made of bulk silicon was used. (2) Field oxidation was conducted to have D in Fig. 20 equal to 600 nm to form a field oxide film 900. (3) Boron ions were implanted into an entire surface and heat treatment was conducted at 1100°C for three hours. By this process, the base density was 1x10 16 cm -3 . (4) A silicon oxide film 904 having a thickness of 30 nm was formed by thermal oxidation method as an insulating film to be provided between base region 907 and control region 905. (5) After depositing polycrystalline silicon, high density N-type polycrystalline silicon was made by ion implantation to form a control electrode 905. (6) An emitter region 906 and a collector region 908 were formed in self-aligned manner with the control electrode 905 masked and by ion implantation. In this case, the dose quantity was 2x10 15 cm -3 of arsenic, and consequently, an emitter-collector region of 2x10 19 cm -3 was formed. Finally, the depth of junction was 600 nm. (7) PSG was deposited 600 nm thick by CVD to form an interlayer insulating film 909. (8) A silicon wafer was adhered to a support substrate 910 by using a polyimide adhesive 902 as shown in Fig. 21. (9) Bulk silicon was selectively etched, using an amine type etching solution and the field oxide film 900 as the stopper. (10) A silicon oxide film 911 was deposited at low temperature by photo assisted CVD. (11) Base portion was only opened by mask alignment method, p-type polycrystalline silicon 912 was deposited in an amount of 2x10 19 cm -3 , and was subjected to heat treatment for the recrystallization with monocrystalline silicon of the base region 907 as the seed. Herein, the mask alignment method is to provide a mask in accordance with an alignment mark, while viewing the alignment mark provided on the side of the control electrode 905 through the silicon film thickness of about 500 to 600 nm. By recrystallizing the p-type polycrystalline silicon of 2x10 19 cm -3 , the short-circuit between emitter/collector and base was suppressed to eliminate the area of life time killer such as polycrystalline silicon from the side of base region. As a result of the structure as presented in Fig. 23, the lateral bipolar transistor without external base was produced. (12) A through hole 913 was provided to take out the potential of control electrode 905. (13) A contact 914 was provided to take out the emitter-collector potential for the interlayer insulating film. (14) The control electrode 905 and the base electrode 912 were connected by Al-Si and other wirings for emitter-collector were made. In the above way, a device equivalent to that as shown in Fig. 1 was fabricated. Also, as a result of the structure of example 5, the base resistance could be decreased, and the high collector current could be obtained even in the high current area. Example 6 The same process as example 1 was performed using an N-type SIMOX substrate of 10 to 20Ω. However, a PNP-type bipolar transistor with control electrode was also fabricated in example 6. That is, in the PNP-type bipolar transistor with control electrode, an emitter/collector region was made at the time of ion implantation of boron for leading out the base, and an N + region for leading out the base was made at the time of ion implantation of arsenic for the formation of the NPN-type emitter/collector. Further, a Bi-CMOS transistor with a circuit as shown in Fig. 57 was fabricated by using a device formed on the substrate of example 1, having the base electrode as a substrate contact for the MOS transistor without short-circuiting the base electrode and the control electrode, and the control electrode as the gate electrode for the MOS transistor. Of course, the transistor as shown in the circuit diagram is a lateral bipolar transistor with control electrode. Fig. 58 shows an output diagram of the Bi-CMOS inverter. The output voltage at high level is lower by 0.45 volt than the voltage value of the power supply, and that at low level is higher by 0.45 volt than the ground voltage. For the comparison, the evaluation with the conventional bipolar transistor indicated that this value was 0.65 volt but not 0.45 volt. And the minimum drive voltage of Bi-CMOS using the conventional bipolar transistor was 1.5 volt, whereas that of the lateral bipolar transistor with control electrode of the present invention was 1.1 volt. Hence, with the example 6, Bi-CMOS circuit could be fabricated, with which a device fully drivable by a single cell can fabricated through a simple process of the conventional CMOS process. Example 7 This example will be described below using Figs. 26 to 37. First, complete dielectric separation between elements was performed by a separation method of selective oxidation for an SIMOX substrate in which the film thickness of silicon oxide film for backing 201 on a silicon substrate 200 was 400 nm and the film thickness of a silicon layer 202 was 200 nm, with the substrate density of 2E15 cm -3 . Then, a thermal oxide film 204 having a film thickness of 10 nm was formed on this substrate (Fig. 26), and then an NSG film 203 was deposited 500 nm thick, and removed partially (Fig. 27). R1 in Fig. 27 indicates a resist film. In the figure, the width of second insulating film region 203 was about 1 µm. After the resist film R1 was removed, thermal oxidation was performed again to form a 10 nm-thick silicon oxide film (Fig. 28). In Fig. 28, 205 is a first insulating film region (with a thickness of T OX1 ) and the NSG film 203 plus thermal oxide film 204 is a second insulating film region (with a thickness of T OX2 ). In this case, T OX1 is equal to 10 nm and T OX2 is equal to 510 nm, where T OX1 < T OX2 . As shown in Fig. 29, ion implantation of boron was performed with the second insulating film region (203+204) masked to form a P-type impurity region 206 corresponding to the base density. The conditions of ion implantation were such that the ion species was B 11+ , the implantation energy was 70 KeV and the dose quantity was 5E12 cm -2 . As a result, the impurity density of the P-type region 206 was equal to 4E17 cm -3 . Then, a 400 nm-thick polycrystalline silicon film was deposited as shown in Fig. 30, and ion implantation of phosphorus was performed with a dose quantity of 8E15 cm -2 and an implantation energy of 70 KeV to form a polycrystalline silicon conductive film 207. Side walls 208, 208' were then formed by anisotropic etching, with only the polycrystalline silicon on the side wall portion left behind (Fig. 31). Thereafter, a side wall 208 on the base portion was covered with a resist R2, as shown in Fig. 32, and a side wall 208' on the side of collector electrode was removed to form a structure as shown in Fig. 33. In Fig. 32, 213 is a selective oxide portion edge. In this case, the thickness of side wall was found to be about 260 nm from the SEM observation. Then, an element portion was opened with a resist R3, as shown in Fig. 34, and ion implantation was conducted into the emitter/collector electrode with the side wall 208 and the second insulating film region 203 masked. The conditions of ion implantation were such that the ion species was As, the implantation energy was 150 KeV and the dose quantity was 5E15 cm -2 . Also, to form a base electrode, a resist R4 was applied, except for a part of the base region to be opened, as shown in Fig. 36, and ion implantation was conducted under the conditions with the implantation energy of 20 KeV and the dose quantity of 1E15 cm -2 . After ion implantation, heat treatment was conducted in nitrogen atmosphere at 1000°C for ten minutes to activate impurities. Consequently, a structure as shown in Fig. 35 was formed. In the figure, P-type impurity region 206 was a base region, high density N-type impurity region 209 was an emitter region, and high density N-type impurity region 210 was a collector lead-out electrode region. The base width is determined by the thickness of side wall, and was about 260 nm in this example. Then, to couple electrically the control electrode and the base lead-out electrode, a contact 212 for the base lead-out electrode was opened. After Al was deposited by sputtering, an Al wiring 211 was formed to cover the base lead-out electrode 212 and the side wall 208, as shown in Fig. 36. After PSG was deposited 500 nm thick as an interlayer insulating film, a contact hole was opened to lead out each of emitter, base and collector electrodes, Al was deposited 800 nm thick as the second layer by sputtering, and the patterning was made to form electrodes and the wiring. Fig. 37 is a plan view. In the figure, 215, 216 and 217 are contact holes for emitter, base and collector electrodes, respectively, and 218, 219 and 220 are Al wirings on the second layer for emitter, base and collector electrodes. Example 8 This example will be described below using Figs. 38 to 42. First, complete dielectric separation between elements was performed by a separation method of selective oxidation for an SIMOX substrate in which the film thickness of a silicon oxide film for backing 301 on a silicon substrate 300 was 400 nm and the film thickness of a silicon layer 302 was 200 nm, with the substrate density of 2E15 cm -3 . Then, a thermal oxide film 305 having a film thickness of 10 nm was formed on this substrate, a silicon nitride film 304 was deposited 10 nm thick thereon, and further an NSG film 303 was deposited 500 nm thick thereon (Fig. 38). The NSG film 303 was removed partially to provide a second insulating film region 303 (Fig. 39). In the same figure, R1 indicates a resist film, and the width of second insulating film region 303 was about 1 µm. After the resist film R1 was removed, ion implantation of boron was conducted with the second insulating film region 303 as a mask to form a P-type impurity region 306 corresponding to the base density. A structure with the cross section and plan as shown in Figs. 41 and 42 was formed through the same process as example 7. In the figure, 309, 306 and 310 are emitter, base and collector regions, respectively, and a control electrode 308 directly above a base region 306 is composed of polycrystalline silicon on the side wall, with a width of about 260 nm. Accordingly, the base width in this example was about 260 nm. 313 is a selective oxide portion edge and 321 is an NSG interlayer insulating film. 311 is an Al wiring at the first layer which connects the control electrode to base lead-out electrode. 315, 316 and 317 are contact holes for leading out electrodes of emitter, base and collector, respectively. 318, 319 and 320 are Al wirings on the second layer. In the example 7, an oxide film near the control electrode located on the boundary section between the first insulating film region and the second insulating film region is an intermittent film, producing many defects, which may cause a slight problem concerning the leak current or withstand voltage in the insulating film. However, the insulating film interface near the control electrode is a continuous film composed of excellent thermal oxide film by virtue of the film structure as shown in Figs. 38 and 39, whereby the leak current or withstand voltage of insulating film could be improved. Example 9 This example will be described below using Figs. 43 to 47. Complete dielectric separation between elements was performed by a separation method of selective oxidation for an SIMOX substrate in which the film thickness of a silicon oxide film for backing 401 was 400 nm and the film thickness of a silicon layer 402 was 200 nm, with the substrate density of 2E15 cm -3 . Then, a thermal oxide film 404 having a film thickness of 10 nm was formed on this substrate, and a silicon nitride film 403 was deposited 600 nm thick thereon and partially removed to form a structure as shown in Fig. 43. Like the seventh and eighth examples, a P-type region 406 corresponding to the base impurity density was formed by ion implantation of boron. Then, polycrystalline silicon was deposited by CVD, but polycrystalline silicon was deposited more likely on the silicon nitride film 403 than on the silicon oxide film 404 by adjusting the partial pressure of etching gas or HCl. Consequently, polycrystalline silicon on the silicon nitride film was thicker than on the silicon oxide film, as shown in Fig. 44. A side wall was formed by anisotropic etching, and the side wall on the side of collector lead-out electrode region was removed in a similar way to that of the first and second examples. As a result, a structure as shown in Fig. 45 was formed. Because polycrystalline silicon on the silicon nitride film is thicker than that on the silicon oxide film, polycrystalline silicon is left behind on the silicon nitride film. A structure with the cross section and plan as shown in Figs. 46 and 47 was formed through the same process as the seventh and eighth examples. In the figure, 409, 406 and 410 are emitter, base and collector regions, respectively, and a control electrode 408 directly above a base region 406 is composed of polycrystalline silicon on the side wall, with its width of about 260 nm. Accordingly, the base width in this example was about 260 nm. 413 is a selective oxide portion edge and 421 is an NSG interlayer insulating film. 411 is an Al wiring on the first layer which connects the control electrode to the base lead-out electrode. 415, 416 and 417 are contact holes for leading out electrodes of emitter, base and collector, respectively. 418, 419 and 420 are Al wirings on the second layer. In the seventh and eighth examples, the control electrode is highly resistive, but in this example, the silicon nitride film is used for the second insulating film region 403, and further the deposition conditions of polycrystalline silicon for conductive film are optimized to also leave conductive film on the silicon nitride film 403. Consequently, its resistance could be made smaller than that of the control electrode. Example 10 In this example, tungsten silicide was used for the control electrode to make the resistance lower than in the ninth example. This example will be described below. A structure of Fig. 45 was formed through the same process as the ninth example. Thereafter, tungsten was deposited, and heat treatment was conducted in He gas atmosphere at 1000°C for twenty minutes. As a result, a side wall 408 of Fig. 45 became WSi 2 . The same process as the ninth example was employed, except for the annealing conditions for the activation of impurities of emitter/collector. The heat treatment for the activation of impurities of emitter/collector was conducted under the conditions of 900°C/30 minutes in He gas atmosphere. With this example, the control electrode having a resistance smaller roughly by one figure than the ninth example could be formed, and the AC characteristic improved. Example 11 This example is one in which an NPN-type bipolar transistor with control electrode and a CMOS circuit were fabricated simultaneously. This example will be described below, using Figs. 48 to 54. Complete dielectric separation between elements was performed by a separation method of selective oxidation for an SIMOX substrate in which the film thickness of a silicon oxide film for backing 501 was 400 nm and the film thickness of a silicon layer 502 was 200 nm, with the substrate density of 2E15 cm -3 . Then, using a resist mask having opened only the region for N-type MOS transistor of CMOS circuit to be made after forming the mask having a thickness of 10 nm by oxidation, ion implantation of boron was conducted with a dose quantity of 8E11 cm -2 , and an implantation energy of 20 KeV to form a P-type region having a substrate density of 3E16 cm -3 . Similarly, using a resist mask having opened only the region for P-type MOS transistor of CMOS circuit to be made, ion implantation of phosphorus was conducted with a dose quantity of 4E11 cm -2 and an implantation energy of 60 KeV to form an N-type region of 1E16 cm -3 . Then, a thermal oxide film 504 having a film thickness of 10 nm was formed on this substrate. Fig. 48 shows a cross-sectional structure after the formation of thermal oxide film. This figure shows, on the left hand, a lateral bipolar transistor with control electrode, and on the right hand, a CMOS portion (a typical view useful for both the N-type MOS transistor and the P-type MOS transistor). And a silicon nitride film 503 was deposited 600 nm thick thereon, and the silicon nitride film 503 in the lateral bipolar transistor region with control electrode was partially removed to form a structure as shown in Fig. 49. Like the seventh and eighth examples, a P-type region 506 corresponding to the base impurity density was formed by ion implantation of boron. Implantation of boron ions was not performed into the CMOS region which was masked with the silicon nitride film 503. The silicon nitride film 503 in the CMOS region was removed with only the bipolar transistor region with control electrode masked with a resist mask, and polycrystalline silicon was deposited by CVD, as in the ninth example. That is, polycrystalline silicon was deposited more likely on the silicon nitride film 503 than on the silicon oxide film 504 by adjusting the partial pressure of etching gas or HCl. Consequently, polycrystalline silicon on the silicon nitride film was thicker than on the silicon oxide film, as shown in Fig. 50. Ion implantation of phosphorus was performed to this polycrystalline silicon, as in the seventh, eighth and ninth embodiments, to enhance the conductivity of polycrystalline silicon. Then, a side wall was formed by anisotropic etching in the lateral bipolar transistor region with control electrode, with the CMOS region covered by a resist mask. Polycrystalline silicon in the CMOS region which was covered by the resist mask was left intact (Fig. 51). Then, the side wall on the collector side of the lateral bipolar transistor with control electrode was removed with resist R1 as a mask, as shown in Fig. 52, and a gate electrode 508' of CMOS was formed. Then, using a resist mask having opened the emitter/collector portion in the lateral bipolar transistor region with control electrode, the source/drain portion of N-type MOS transistor in the CMOS region, and the channel electrode portion of P-type MOS transistor, ion implantation of N-type impurities was conducted. The ion implantation conditions were such that the ion species was As, the implantation energy was 150 KeV, and the dose quantity was 5E15 cm -2 . As a result, an emitter region 509, a collector lead-out electrode region 510, a source region 509' of the N-type MOS transistor, a drain region 519', and a channel electrode of the P-type MOS transistor were formed. A resist film was newly formed having opened a base electrode portion of the lateral bipolar transistor with control electrode, a channel electrode portion of N-type MOS transistor in the CMOS region, and a source/drain portion of P-type MOS transistor after peeling off the resist, and ion implantation of boron was conducted with an implantation energy of 20 KeV and a dose quantity of 1E15 cm -2 . Consequently, a high density impurity region for each electrode was formed. After peeling off the resist, heat treatment was conducted in nitrogen atmosphere at 1000°C for ten minutes to activate impurities. As a result, a structure as shown in Fig. 53 was formed. As shown in Fig. 54, the control electrode and the base electrode were electrically coupled as in the ninth example. PSG film was deposited 500 nm thick as an interlayer insulating film 521. Then, contact holes were formed to lead out the emitter 509 and the base/collector electrode 510 for the lateral bipolar transistor with control electrode, and the source 509', drain 510' and channel electrode for the N-type MOS transistor and P-type MOS transistor. Al was deposited as the second layer, each electrode (518, 520, 518', 520', 519') was taken out and the wiring applied. PSG film was deposited 500 nm thick as a passivation film 522 and a contact hole for the pad was opened. Example 12 Fig. 55 is a plan view showing a twelfth example of bipolar transistor. And Fig. 56 is a cross-sectional view taken along the line AA of Fig. 55. In both figures, 1 is a P-type substrate, 2 is an N-type buried region for the reduction of collector resistance, and 3 is an N-type region formed for the lead-out of collector electrode. 4 is an N - region acting as the collector, 5 is a P-type base region, and 6 is an N-type emitter region. 7 and 8 are oxide films, and 9 is a control electrode for controlling the state of the side face of base region 5 in contact with the oxide film 8. 10 is an N-type polycrystalline silicon electrode for the lead-out of emitter electrode, 11 is an AL electrode, and 12 is an interlayer insulating film such as PSG. Note that the AL electrode 11 and the interlayer insulating film 12 are not shown for simplification in Fig. 55. 13 is a contact hole of collector region, 14 is a contact hole of base region, 15 is a contact hole of control electrode, and 16 is a contact hole of emitter region. As shown in Fig. 56, the bipolar transistor of this example is a vertical bipolar transistor comprised of an N - region 4 (collector region), a P-type region 5 (base region), and an N-type region 6 (emitter region), the control electrode 9 being formed via the oxide film on the side of base region 5. The base region 5 is formed by introducing impurities from the substrate surface, whereby the base width (t B2 ) can be smaller than the base width (t B1 ) in the conventional constitution as shown in Fig. 71. A fabricating method of this example will be now described using Figs. 57 to 62. First, N-type impurities were introduced by ion implantation to a desired site of P-type substrate 1, and heat treatment was conducted to form an N-type buried region 2, as shown in Fig. 57. Subsequently, an N - region 4 was formed by epitaxial growth. After a thermal oxide film 18 having a thickness of 200 Å was formed on the surface of N - region 4, N-type impurities were introduced by ion implantation and heat treatment was conducted to form the N + region 3. Subsequently, a 1500 Å-thick Si 3 N 4 film 19 and a 2000 Å-thick SiO 2 film 20 were deposited respectively. Anisotropic etching was conducted for other than a portion where the base, emitter, collector and collector lead-out electrodes were formed, so that a part of N - region was left behind. Then, thermal oxidation was conducted for the substrate surface to form a thermal oxide film 21, as shown in Fig. 4, and subsequently, Si 3 N 4 was deposited over an entire surface. Thereafter, anisotropic etching was conducted to leave Si 3 N 4 film 22 only on the side of silicon convex portion. Also, thermal oxidation was conducted to form a thick oxide film 7, as shown in Fig. 59. The N + region 3 was spread over the entire convex portion due to heat treatment. After Si 3 N 4 film 22 and an oxide film 21 on the side of substrate convex portion were removed by wet etching, oxidation was conducted again to form an oxide film 8 having a thickness of about 50 to 100 Å. Then, polycrystalline silicon 9 was deposited over the entire surface, as shown in Fig. 60, and subsequently, N-type impurities such as As + , P + were implanted and heat treatment was conducted. After a photo-resist 18 was applied flat, the photo-resist was removed until polysilicon of convex portion appeared by oxygen plasma etching. Then, a desired portion of polycrystalline silicon was removed by dry etching using a mixture gas of CF 4 and H 2 , as shown in Fig. 61. Subsequently, Si 3 N 4 film 19 was removed. Polycrystalline silicon was oxidized by thermal oxidation to obtain a structure as shown in Fig. 61. Then, P-type impurities such as B + were introduced by ion implantation and heat treatment was conducted to form a base region 5, as shown in Fig. 62. Then, a contact hole for leading out the emitter electrode was formed at a desired site on the oxide film and subsequently, polycrystalline silicon was deposited. Then, N-type impurities such as As + , P + were introduced by ion implantation and heat treatment was conducted. Thereafter, unnecessary portion was removed by etching to form an emitter region 6 and an emitter lead-out electrode 10. After an interlayer insulating film 12 such as PSG or BPSG was deposited by CVD, the interlayer was etched in a desired portion to form a contact hole. Subsequently, a metal such as AL was deposited by sputtering, and thereafter etched to form an electrode 11, whereby a vertical bipolar transistor with control electrode was fabricated as shown in Figs. 55 and 56. The vertical bipolar transistor with control electrode fabricated in the above process had an on-state current of 0.4V and a base width of 0.2 µm, resulting in the excellent characteristics with high speed. Example 13 Fig. 63 is a cross-sectional view showing a thirteenth example of bipolar transistor according to the present invention. In this example, the present invention is applied to SOI substrate. In Fig. 63, 101 is an oxide film, 102 is an N-type buried region, and 103 is an N-type region formed for the lead-out of collector electrode. 104 is an N - region acting as the collector, 105 is a P-type base region, and 106 is an N-type emitter region. 107 and 108 are oxide films, and 109 is a control electrode for controlling the state of the side face of base region 105 in contact with the oxide film 108. 110 is an N-type polycrystalline silicon electrode for the lead-out of emitter electrode, 111 is an AL electrode, and 112 is an interlayer insulating film such as PSG. The structure of this example can be fabricated by a fabrication method as shown in example 12. First, the N-type buried region 102 was formed at a desired site on the SOI substrate, and epitaxial growth was conducted. In the same way as the example 1 hereinafter, after forming a convex portion of silicon region, an oxide film 107 for element separation was formed by oxidation until all the silicon layer of the SOI substrate became an oxide film on field oxidation. After that, the bipolar transistor was fabricated in the same way as shown in the example 12. In this way, the present invention can be also applied to the SOI substrate, whereby a Bi-CMOS circuit with low consumption power and high speed can be formed in combination with a MOS transistor having a small parasitic capacity formed on SOI with high speed. Example 14 Fig. 64 is a cross-sectional view showing a fourteenth example of bipolar transistor according to the present invention. This example shows a case where the present invention is applied to the bipolar transistor of multi-emitter. In Fig. 64, three emitters are shown. With the conventional lateral bipolar transistor with control electrode, a multi-emitter structure is difficult to fabricate, but with the vertical bipolar transistor with control electrode, the bipolar transistor of multi-emitter is easily fabricated, and can have the large current to flow. In Fig. 64, 201 is a P-type substrate, 202 is an N-type buried region for the reduction of collector resistance, and 203 is an N-type region formed for the lead-out of collector electrode. 204 is an N - region acting as the collector, 205 is a P-type base region, and 206 is an N-type emitter region. 207 and 208 are oxide films, and 209 is a control electrode for controlling the state of the side face of base region 205 in contact with the oxide film 208. 210 is an N-type polycrystalline silicon electrode for the lead-out of emitter electrode, 211 is an AL electrode, and 212 is an interlayer insulating film such as PSG. Example 15 Fig. 65 is a cross-sectional view showing a fifteenth example of bipolar transistor according to the present invention. This example shows a case where the present invention is applied to a device with a thin interfacial oxide film capable of readily flowing tunnel current which is formed between emitter region and emitter electrode. In Fig. 65, 313 is an interfacial oxide film having a thickness of about 10 Å (1 µm = 10 4 Å) capable of flowing tunnel current. Other portion is of the same constitution as the example 12. The interfacial oxide film 313 suppresses the inflow of minority carriers (base current: I B ) flowing from the base region into the emitter region, while maintaining the flow of majority carriers (emitter current: I E ) from the emitter electrode to the emitter region. Therefore, a bipolar transistor having a large current amplification factor (I E /I B -1) can be obtained. Hence, in this example, the bipolar transistor which is capable of being driven at low voltages and has high speed and high current amplification factor could be obtained. Example 16 Fig. 66 is a cross-sectional view showing a sixteenth example of bipolar transistor according to the present invention. This example shows a case where the present invention is applied to HBT (hetero bipolar transistor) in which the band gap of emitter region is wider than the band gap of base region. In Fig. 66, the emitter region 406 is composed of a material having a wider band gap than the base region, such as microcrystalline or amorphous semiconductor. This can be accomplished by ion implantation of Si into the emitter region. Other portion has the same constitution as the example 12. Also, SiC can be used for the material with large band gap. When Si 1-X C X is used for the emitter region, C in Si 1-X C X is formed by ion implantation of carbon ions C + into crystalline silicon. The upper limit of carbon C is 0.5, but it is desirable to satisfy the inequality X ≦ about 0.075 to reduce the stress of Si 1-X C X . The lower limit of carbon C is determined by the stopping ability of holes, wherein carbon C is necessary in an amount of 10 20 cm -3 or greater. In this way, forming Si 1-X C X by ion implantation, the quantity of C is reduced near the base interface, but crystal defects are conversely decreased, whereby there is no problem with the characteristic of bipolar transistor. A semiconductor device comprises an insulating region residing adjacent to a first semiconductor region, a control electrode residing via the insulating region, a second semiconductor region and a third semiconductor region, which have an opposite conduction type to that of the first semiconductor region, residing adjacent to and carrying therebetween the first semiconductor region. When the first, second and third semiconductor regions and the control electrode are grounded, the first semiconductor region in contact with the insulating layer is adjusted to be in weak inversion state, and the potential of the control electrode and that of the first semiconductor region are electrically coupled to be operable.

Claims: A semiconductor device on an insulator to constitute a SOI, Silicon On Insulator, structure, comprising an insulating layer (104) residing in contact with a first semiconductor region (106), a control electrode (108) residing on said insulating region (104), a second semiconductor region (109) and a third semiconductor region (110), which have an opposite conduction type to that of said first semiconductor region (106), residing in contact with and carrying therebetween said first semiconductor region (106), said control electrode (108) and said first semiconductor region (106) are electrically coupled, said control electrode (108) is disposed on an insulating layer (104) on a base region (106) being said first semiconductor region, characterized in that: in the state where said first, second and third semiconductor regions (106, 109, 110) and said control electrode (108) are grounded, the work function of said control electrode (108) material, the film thickness of said insulating layer (104), and the impurity concentration of said semiconductor region (106) of the first conduction type are set so that said first semiconductor region (106) in contact with said insulating layer (104) is in weak inversion state, and a depletion layer in the MOS structure reaches an insulating substrate (101). A semiconductor device according to claim 1, wherein said control electrode is a gate electrode, said first semiconductor region is a channel region directly below the gate electrode, and said second and third semiconductor regions are a source region and a drain region, respectively, to constitute a MOS transistor. A semiconductor device according to any one of claims 1 and 2, wherein said first semiconductor region is a base region, and said second and third semiconductor regions are an emitter region and a collector region, respectively, to constitute a bipolar transistor. A semiconductor device according to claim 3, wherein the distance from emitter junction of said base region to collector junction is equal to or less than 0.3 µm. A semiconductor device according to claim 1, wherein a base region of said first semiconductor region is formed by diffusion of impurities from the substrate surface, and said control electrode is formed on an insulating film on the side of said base region to constitute a bipolar transistor. A semiconductor device according to claim 5, wherein the impurity concentration profile in said base region is smaller from emitter junction to collector junction. A semiconductor device according to claim 5 or 6, wherein two or more emitter regions serving as said second semiconductor region are formed. A semiconductor device according to any one of claims 5 to 7, wherein a thin oxide film is provided between the emitter region serving as said second semiconductor region and the emitter electrode, the conduction between said emitter region and said emitter electrode being through the use of tunnel current. A semiconductor device according to any one of claims 5 to 8, wherein the emitter region serving as said second semiconductor region is constituted from a semiconductor having a larger forbidden band width than the semiconductor constituting said base region. A semiconductor device according to claim 9, wherein said semiconductor having larger forbidden band width is made of microcrystalline or amorphous semiconductor. A semiconductor device according to claim 9, wherein said semiconductor having large forbidden band width is made of SiC. A fabrication method for a semiconductor device on an insulator to constitute a SOI, Silicon On Insulator, structure, wherein an emitter region (109), a base region (106) and a collector region (110) are laterally formed on a SOI substrate having a semiconductor region (108) on the surface of an insulating layer (104) or insulator, and comprising an electrode (108) for controlling the conduction type of the base region (106) via an insulating film (104), characterized by including the following processes ( A ) to ( E ) which are performed in sequence: ( A ) a process of forming a first insulating film region ( 104, 105) and a second insulating film region (103) having a greater thickness than that of said first insulating film region ( 104 , 1059) on said semiconductor layer (102) of the first conduction type provided on the surface of said insulating layer (101) or said insulator; (B) a process of introducing and activating impurities of the second conduction type into said second semiconductor region (106) below said first insulating film region ( 104, 105) with said second insulating film (103) region as a mask; (C) a process of depositing a conduction film (107) on said first and second insulating film regions (103, 104, 105) and forming a control electrode (108) by anisotropic etching to leave behind at least a side wall conduction film (108) deposited in a stepped side wall portion between said first insulating film region (104) and said second insulating film region (103) to be directly above the base region ( 106 ); (D) a process of making said emitter region (109) and said collector region (110) by introducing and activating impurities of the first conduction type with said control electrode (108) and said second insulating film region ( 103 ) as a mask; and ( E ) a process of electrically connecting said control electrode (108) with a lead-out electrode (112) of said base region (106), and wherein the processes (A) to ( E ) are performed such that for the resulting semiconductor device, in the state where said base, emitter and collector regions and said control electrode are grounded, the work function of said control electrode (108) material, the film thickness of said insulating layer (104), and the impurity concentration of said semiconductor region (106) of the first conduction type are set so that said first semiconductor region (106) in contact with said insulating layer (104) is in weak inversion state, and a depletion layer in the MOS structure reaches said insulating substrate. A fabrication method of semiconductor device according to claim 12, further comprising a process of implanting C ions into the emitter region in performing said process (D) to constitute the emitter region of SiC. A fabrication method of semiconductor device according to claim 12, further comprising a process of implanting Si ions into said emitter region in performing said process (D) to constitute said emitter region of microcrystalline semiconductor or amorphous semiconductor.

Inventors: KOIZUMI TORU, TSUDA HISANORI, WATANABE HIDENORI, KOIZUMI, TORU, TSUDA, HISANORI, WATANABE, HIDENORI
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1994
Main classification: H01L29
IPC codes: H01L29, H01L21, H01L27