METAL, ALLOY, OR METAL CARBIDE NANOPARTICLES AND A PROCESS FOR FORMING SAME

Abstract: A metal or alloy nanoparticle is provided which exhibits hysteresis at room temperature having a carbon coating. The nanoparticle has a diameter in the range of approximately 0.5 to 50 nm, and may be crystalline or amorphous. The metal, alloy, or metal carbide nanoparticle is formed by preparing graphite rods which are packed with the magnetic metal or alloy, or an oxide of the metal or alloy. The packed graphite rods are subjected to a carbon arc discharge to produce soot containing metal, alloy, or metal carbide nanoparticles and non-magnetic species. The soot is subsequently subjected to a magnetic field gradient to separate the metal, alloy, or metal carbide nanoparticles from the non-magnetic species.

Description: TITLE METAL, ALLOY, OR METAL CARBIDE NANOPARTICLES AND A PROCESS FOR FORMING SAME BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to the field of metal, alloy, or metal carbide compounds and carbon-coated magnetic metal alloy or metal carbide compounds. Particularly, the present invention relates to the field of carbon-coated metal, alloy, or metal carbide nanoparticles and the methods for preparing the same. Nanoparticles include crystalline or amorphous particles 0.5 to 50 nanometers in diameter and nanotubes up to 1 centimeter long and 0.5 to 50 nanometers in diameter. 2. Description of the Prior Art Small magnetic particles have many applications. Such particles are used as toner in xerography, in ferrofluid vacuum seals, in nuclear magnetic resonance imaging as contrast agents, and in magnetic data storage. These magnetic particles are typically micron-sized in diameter or larger. The large SUES ITUTE SHEET (RULE 26) size of these particles renders them less than satisfactory for several specialized applications. If the magnetic particles were smaller, cost reduction by reducing the number of processing steps would be achieved in xerographic applications. In ferrofluid applications, the enhanced solubility due to carbon coating provided by smaller particles may be advantageous. In magnetic data storage, high density may be enhanced by using smaller particles. Moreover, in magnetic ink applications, the carbon coating and ability to disperse the nanoparticles in aqueous solutions may provide advantages for wetting and coating. Consequently, there is a potential need for sub-micron sized metal, alloy, or metal carbide particles and a method for producing bulk amounts of these particles in a high yield process. In order to improve operation in magnetic data storage applications, it is desirable for the magnetic particles to exhibit hysteresis. Even more desirable is the exhibition of hysteresis at room temperatures. Recently, there has been increased investigation regarding the Kratschmer-Huffman carbon arc method of preparing fullerenes, or small hollow carbon clusters. These fullerenes are typically in the order of 1 nm in diameter. Recently, it has further been discovered that these hollow carbon clusters can be filled with metal ions. This can be accomplished by drilling out the graphite rods and packing them with a mixture -2- SUBSTmrrE SHEET (RULE 26) of metal oxide powder and graphite cement before generating the soot by the carbon arc. Rodney S. Ruoff, Donald C. Lorents, Bryan Chan, Ripudaman Malhotra, and Shekhar Subramoney, Science, Vol. 259, p. 346 (1993) discussed the production of 20-40 nm diameter carbon-coated lanthanum carbide nanocrystallites by this method. Similar results were reported by Masato Tomita, Yahachi Saito and Takayoshi Hayashi in Jpn. J.Appl. Phvs., Vol. 32, p. 280 (1993) . The carbon arc method of preparing lanthanum carbide nanocrystallites discussed above generates fullerenes and graphitic soot in addition to the lanthanum carbide nanocrystallites. In order to be useful, a means of separating the nanocrystallites is essential. So far, no chemical methods have been found to be successful in separating macroscopic amounts of nanoparticles from graphitic soot and fullerenes. Such separation processes are rendered extremely important when the yields achieved for the nanoparticles is in the order of ten percent or less of the soot. Accordingly, there is a need for a method to separate metal, alloy, or metal carbide nanoparticles from graphitic soot. SUMMARY OF THE INVENTION By using a modification of the Kratschmer-Huffman carbon arc method, carbon coated nanoparticles having a diameter in -3- SUBSTfTUTESHEET(RULE26) the range of approximately 0.5 to 50 nm were formed. If a magnetic rare earth metal, alloy or metal or alloy oxide is packed into a graphite rod and subsequently subjected to a carbon arc discharge, soot containing metal, alloy, or metal carbide nanoparticles and non-magnetic species is formed. The metal, alloy, or metal carbide nanoparticles can be separated from the soot by subjecting the soot to a magnetic field gradient. In the magnetic separation step, the nanoparticle- containing soot is ground to a fine powder and then dropped down an electrically grounded metal tube through a magnetic field gradient created by a pair of strong magnets. Non¬ magnetic material passes through the tube, but magnetic components are suspended if the field gradient force exceeds the gravitational force. When the apparatus is moved away from the magnets, the magnetic material is released into its own separate collection container. This process can be used to separate paramagnetic or ferromagnetic species from non¬ magnetic components of the soot produced by the carbon arc discharge process. Theories of monodomain magnetic particles predict that the blocking temperature, i.e., the temperature above which metastable hysteretic behavior is absent, depends on the product of the particle volume and the magnetocrystalline anisotropy constant for the material, K. The alloys manganese aluminum carbide (Mn 3 AlC) , T-phase manganese aluminide (MnAl) and several samarium cobalt (SmCo x ) phases are ferromagnetic in bulk form and have large anisotropy constants. The magnetization as a function of the applied field and temperature for the different alloy nanoparticles indicates that monodomain magnetic particles of these alloys exhibit room temperature hysteresis. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a transmission electron micrograph of a carbon-coated gadolinium carbide nanocrystallite formed in accordance with the present invention. Figure 2 is an electron diffraction pattern of a gadolinium carbide nanocrystallite formed in accordance with the present invention. Figure 3 is a SQUID magnetometer measurement of M(H,T) for a 10 mg nanocrystalline gadolinium carbide specimen separated in accordance with the present invention. Figure 4 is a SQUID magnetometer measurement of M(H,T) for a 30 mg nanocrystalline manganese-aluminum-carbide specimen formed in accordance with the present invention. Figure 5 is a plot of the measured coercivity as a function of T M for the specimen used in Figure 1. Figure 6 is a SQUID magnetometer measurement of M(H,T) for a samarium cobalt powder specimen formed in accordance with the present invention. Figure 7 is a curve showing the coercivity as a function of T* for the specimen used in Figure 3. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A process based on the Kratschmer-Huffman carbon arc method of preparing fullerenes can be used to generate carbon- coated metal, alloy, or metal carbide nanoparticles. When combined with a magnetic field gradient separation technique, bulk amounts of these nanoparticles can be isolated. If graphite rods which are packed with a magnetic rare earth metal, alloy or metal or alloy oxide are subsequently subjected to a carbon arc discharge, the soot produced by the Kratschmer-Huffman carbon arc process contains metal, alloy, or metal carbide nanoparticles and non-magnetic species. The graphite anode is hollowed out and packed with a mixture of metal, alloy, or metal or alloy oxide and graphite cement. In the arc, metal-containing clusters form. The cluster stoichiometry depends on the chemistry between the metal atoms, carbon, and oxygen. The clusters diffuse until they are deposited on a surface, either the high temperature cathode or the room temperature walls of the reactor. The nanocrystalline -6- SUBSTrTUTESHEET(RULE26) phases produced depend on the surface temperature and the cooling rate of the clusters determined by their diffusion path and the amount of helium buffer gas. This method is therefore useful in preparing metastable phases. The carbon coating arises when the particles cool. Since graphite melts at a higher temperature than the metals or metal carbides, phase segregation occurs in the cooling nanoparticle, forming a graphitic shell. The coating in some cases prevents degradation of air or water-sensitive compounds, a problem encountered with important magnetic materials such as Nd 2 Fe 14 B. A magnetic field gradient can be used to separate the metal, alloy, or metal carbide nanoparticles from the non¬ magnetic species included in the soot. Preferably, the soot produced by the carbon arc discharge method is further ground to a fine powder before being subjected to the magnetic field gradient. If the magnetic field gradient force is greater than the gravitational force, the magnetic nanoparticles will be suspended by the magnets in the separator tube whereas the non¬ magnetic species will pass through. This magnetic gradient separation technique removes non-magnetic byproducts of the carbon arc discharge process and enhances the magnetic response of the isolated material. This separation process separates all paramagnetic or ferromagnetic components from the remaining soot. Figure 1 is a transmission electron micrograph of a gadolinium carbide nanocrystallite, enclosed by several curved graphitic sheets, which was formed in accordance with the present invention. In order to form the gadolinium carbide nanocrystallite shown in Figure 1, 1/4 inch diameter graphite rods were drilled and packed with a mixture of metal oxide power, in this case Gd 2 0 3 , and a combination of graphite powder and graphite cement . A 1 : 1 volume ratio of Gd 2 0 3 and graphite powder bound together with a minimum amount of graphite cement was used. The rods were baked overnight at 300°C to drive off water vapor. These graphite rods were then used in the upper electrode position in an AC carbon arc. The arc conditions were 100 A and 25 V, and a helium gas pressure of 125 Torr was applied. A DC carbon arc with the same conditions and the filled graphite rod as the positive electrode also yields these nanocrystallites. The carbon arc discharge process described above produced a soot which included a mixture of graphitic particles, carbon- coated gadolinium carbide nanoparticles and fullerenes. This raw soot was magnetically separated by first grinding it to a fine, micron-sized powder with a mortar and pestle. This ground soot was then passed through a magnetic field gradient to separate the magnetic from the non-magnetic species. In this example, the separator consisted of a funnel, an electrically-grounded aluminum tube with a pair of 1" x 1" x -8- SUBSTrrUTE SHEET (RULE 26) 1/2" neodymium iron boron magnets on either side, and a pair of collection flasks. The grounded metal tube prevents electrostatic charging of the powder. In the separator tube, a paramagnetic particle experiences a gravitational force in addition to a magnetic force proportional to the field gradient, the field ϊ_, and the susceptibility χ given by the following formula: In the separator tube, a ferromagnetic particle with a moment M experiences a magnetic force given by the following equation: f = (ϊ. • V) ϊ_ M The aluminum tube was positioned appropriately between the magnets in order to maximize the magnetic force, F . When small amounts of powder were poured through the apparatus, the magnetic species were suspended by the magnets, while the non¬ magnetic fraction passed through. The collection bottles were switched, and the tube was moved away from the magnets to release the magnetic powder. After the first pass, roughly l/8th of the original volume was found to be magnetic for the case of gadolinium. For cobalt, 95% of the soot produced was found to be magnetic after the first pass. This powder was passed through repeatedly to enhance the abundance of magnetic material. The final magnetic "filtrate" contained a mixture of magnetic nanocrystallites embedded in a carbon matrix, and possibly small amounts of endohedral fullerenes. The fullerenes were removed by extraction in carbon disulfide. No visible differences were observed between pure carbon soot and the gadolinium-containing mixture. Hence, separation of the gadolinium-containing compounds would have been difficult, if not impossible, without the magnetic separation technique. The structural properties of the magnetic powder were examined by electron microscopy. Energy dispersive spectroscopy indicated that the gadolinium was uniformly distributed in the magnetic soot. Closer inspection was made with a JEOL 4000 400 keV high resolution transmission electron microscope. Samples were prepared by dispersing the powder in methanol with the aid of ultrasound and drying a drop of the solution on an amorphous carbon-coated copper grid. A gadolinium carbide nanocrystallite encased in curved graphitic shells as shown in Figure 1, along with smaller crystallites enclosed in amorphous carbon, were observed. In some of the larger nanocrystallites with a diameter approximately 50 nm, up to 30 graphitic layers were seen, and some of the particles were faceted. X-ray diffraction of the nanocrystallites with a Rigaku diffractometer revealed sharp peaks indicating the presence of a single Gd 2 C 3 phase, along with the graphitic peaks and a broadened peak at small angles characteristic of the fullerenes. Comparison with tabulated crystal structures suggest that the most abundant phase is paramagnetic body- centered cubic Gd 2 C 3 . This structural assignment is on the basis of both x-ray diffraction peaks and on electron diffraction of a crystalline oriented in the [110] direction as shown in Figure 2. No evidence was seen for c_-Gd 2 C, Gd 2 C, or Gd 2 0 3 phases, or for Gd crystallites. This is different from the case of lanthanum doping, for which α-LaC, nanocrystallites were observed. Room temperature electron paramagnetic resonance spectra of the powder at 9.104 GHz showed a single broad derivative centered at 3130 G, corresponding to a g-value of 2.08. This is consistent with the g-value predicted for a J=S=7/2 ground state for a Gd +3 ion. Magnetization data were obtained for powder samples using a Quantum Design SQUID Magnetometer. M(H,T) has been determined in solenoidal fields between +5T and for temperatures from 4 to 300°K. Figure 3 shows magnetization data for different temperatures scaled as a function of H/T. The data fall on a paramagnetic response curve. Fits of this data taken at several temperatures allow assignment of a J=7/2 ground state consistent with the EPR results. Ferromagnetic behavior was observed in similar cobalt nanocrystallites. The encapsulation method, in combination with the magnetic separation technique, has been used to prepare ferromagnetic transition metal complexes containing iron, cobalt, nickel and manganese bismuth, and paramagnetic rare earth metal complexes containing gadolinium and holmium. The phases produced appear to be specific to the metal used. However, the production and separation processes are generally applicable to all magnetic species. In a refinement of the present process, increasing the magnetic separator field of the separation has been found to differentiate among the various magnetic nanoparticles. By varying the field, magnetic nanoparticles having different magnetic moments per volume may be segregated. Such a process can be used to further separate the magnetic nanoparticles to isolate those having desired properties. It has been discovered that if the helium pressure is increased during the carbon arc discharge process, the carbon- coated magnetic particles are formed in the shape of nanotubes instead of nanocrystallites. The application of such nanotubes in composite materials may provide certain advantages. In another modification of the present invention, it has been discovered that amorphous magnetic nanoparticles can be formed by packing the graphite rods with appropriate mixtures of two oxide powders. If the particles are formed from a ferromagnetic material, their size is small enough to support only a single magnetic domain. These particles are said to be superparamagnetic, and all the atomic spins align to yield a large particle moment . The particle moment rotates not through domain wall motion, but by rotating all the atomic spins together. Theories of superparamagnetism show that the temperature dependence of the coercivity, H c , for a spherical particle with a single magnetic domain is govern by the equation: H c =H ci [l - (T/T B ] 12 , (1) where H ci is the coercivity at 0 °K and T B is the blocking temperature. Above the blocking temperature, the particle's magnetic moment can flip due to thermal fluctuations during the time it takes to measure the bulk magnetization, which can be on the order of an hour. Above this temperature, the particle is superparamagnetic and no hysteresis is observed in the time frame of the measurement. Below the blocking temperature, the particle doesn't have enough thermal energy to spontaneously flip its magnetic moment in this time frame, and nonzero coercivity is expected, with the temperature dependence given by equation 1. The energy, E, of the single domain spherical magnetic particle, is: E = V[K sin 2 . + H M cos φ] , (2) where V is the particle volume, K is the magnetocrystalline anisotropy, H is the applied field, M is the particle magnetic moment, . is the angle between the particle moment and the nearest easy axis direction, and φ is the angle between the applied field and the particle moment . In the absence of an applied field, the particle moment will lie along an easy axis to minimize the energy; but in a strong applied field, the moment will align with H. In order to rotate the moment to align with the field, the particle must overcome an energy barrier on the order of KV. Above the blocking temperature, the particle's magnetic moment may switch directions spontaneously due to thermal fluctuations. The blocking temperature may be related to the inverse time for measuring the magnetization, ω; the attempt rate to surmount the barrier, ω 0 , which is on the order of the precession frequency of the moment; and the height of the barrier, KV, according to the following relationship: ω=ω 0 exp [-KV/kT B ] . (3) Fine particle magnets may have hysteresis up to a critical temperature, just like their bulk counterparts. However, the physics responsible for the hysteretic behavior is quite different. For monodomain particles, the comparison between the thermal energy and the anisotropy energy is important, while for bulk ferromagnets the comparison between the thermal energy and the exchange energy determines the magnetic behavior. The present invention can be more readily understood in connection with the following examples wherein alloys having large magnetocystalline anisotropy are examined. EXAMPLE 1 In earlier preparations of elemental and carbide nanocrystals, the reactor conditions were adjusted to control the specific phases made. In order to obtain microscopic chemical homogeneity in the carbon arc, a Mn-Al-0 spinel phase starting material was prepared. Stoichiometric quantities of Mn 2 0 3 and Al 2 0 3 were mixed, sintered at temperatures on the spinel phase field and quenched to retain the spinel phase, which was characterized by X-ray diffraction and TEM analysis. The spinel phase of variable composition is identified using a Vegard's law dependence of the lattice constant on Mn:Al ratios between the two end compositions. Mn-Al-0 was a 2:1 ration was packed in graphite rods used in the carbon arc to generate Mn- Al-C nanoparticles. Based on the Mn-Al-C phase diagram, only 1-2% carbon dissolves into the alloy, and we anticipated that the metastable phase analogous to the τ-phase of MnAl would also be ferromagnetic. The only other ferromagnetic phase of Mn-Al-C was Mn 3 AlC, which has a Curie temperature of 15°C. Since the T-phase is the only known ferromagnetic phase of Mn-Al-C at room temperature, raw soot from different parts of the reactor was tested with a Nd 2 Fe 14 B magnet to quickly optimize the production of this ferromagnetic phase. The best arc conditions were found to be 100 A and 40 V with a 1 mm gap spacing. This led to abundant ferromagnetic material in the pancake region of the deposit which forms on the cathode. -IB- Based on a growth model for the nanocrystals made in a carbon arc, both the temperature of the surface and the cooling rate of the alloy cluster before it deposits determines the nanocrystal phase produced. Here the temperature of the cathode is believed to be slightly cooler in the pancake region than in the central core deposit, but the main factor is the difference in the cooling rate of a cluster. Bulk τ-MnAl has been made by melt cooling with a cooling rate of 10 5 -10 8 °C/s, of the e phase, followed by annealing. The phases present in the sample were determined by several methods. Structural characterization by X-ray diffraction (XRD) indicated the presence of Mn 3 AlC, γ-Mn, and graphite, but did not show peaks corresponding to the τ-phase. Calibration of the X-ray apparatus indicated that the maximum abundance of the T- phase without being able to detect it would be on the order of 4 weight percent. Energy dispersive spectroscopy (EDS) was used to determine the Mn:Al relative abundance. Here the electron beam was large enough to excite transitions in several nanocrystals simultaneously. The fact that the ratio ranged from 3:1 to 4:1 over a wide area is consistent with the predominant species seen by XRD. Based on the response to the magnet at room temperature, at least some T-MnAl-C is present in our samples. However, to test the evidence that a large amount of Mn 3 AlC was also present, a sample was placed in a freezer well below the Curie temperature for this phase. It was found that cooling significantly increased the magnetic response. High resolution TEM showed the particle shape, size, and size distribution. All particles were found to have carbon coatings, and the encapsulated nanoparticles were crystalline. An unusual feature was the presence of elongated as well as spherical particles, but the phases corresponding the different shapes were not assigned. In the elongated particles, typical aspect ratios were on the order of three to one. If these particles are ferromagnetic, than shape anisotropy as well as magnetocrystalline anisotropy would play a role in the magnetic behavior. Both the size (average diameter approximately 20nm) and the size distribution were similar to that seen in metal and metal carbide materials made by the carbon arc process. The magnetization as a function of the applied field and temperature was determined using SQUID magnetometry. For SQUID measurements, approximately 30 mg of platelets from the Mn-Al-C sample were immobilized, so that the nanoparticles would not move in the applied magnetic field. Magnetization curves were measured between 5 and 200 °K and 0 to ± 5 °T. Hysteresis was observed at all temperatures within this range. The shape of the hysteresis loop in Figure 4 is indicative of two ferromagnetic contributions with different coercivities, most likely Mn 3 AlC and τ-MnAl. The measured coercivity was plotted as function of T 12 in Figure 5, clearly indicating a departure from the behavior predicated by equation 1. This difference is believed to be due to the presence of multiple components. In this case the saturation magnetization M sat , would equal the sum of the two contributions, normalized for relative abundance. The measured coercivity would be intermediate between those for the two components, but the specific value would depend on the shape of the contributing hysteresis loops. The slope of any fit to the data in Figure 5 cannot be interpreted in terms of a blocking temperature. However, extrapolation of the data suggests that hysteresis would be present at room temperature, a novelty for monodomain magnetic particles. EXAMPLE 2 Samarium cobalt has multiple stable ferromagnetic phases. In preparing alloy nanocrystals of samarium cobalt in the carbon arc, metallic Sm 2 Co 7 powder, rather than an oxide material, was used. A strong magnetic response was observed with a Nd 2 Fe 14 B magnet in material from all parts of the reactor. Data was taken from the pancake region of the cathode deposit, the same region studied for Mn-Al-C. Structural characterization by XRD revealed the presence of SmCo 5 , Sm 5 Co 2 , fee Co, and graphite, but not Sm 2 Co 7 or Sm 2 Co 17 , or samarium carbide phases. EDS indicated a Sm:Co ratio of approximately 1:2 in the sample. The difference between this ratio and that in the starting material may be due to the relatively high vapor pressure of Sm. TEM showed that most particles were approximately spherical, with an average size on 20 nm. In general, the Curie temperature rises with the proportion of cobalt. While the cobalt Curie temperature was above the detection range, it was expected that Sm 2 Co 7 (420°C) and SmCo 5 (710°C) would be observable, even with small increases due to the addition of carbon. However, TMA showed no transitions between 25°C and 875°C. The addition of carbon has also been shown to increase the Curie temperature by over 260 C C in Sm 2 Co 17 cobalt magnets, and a similar effect may be occurring in SmCo 5 . SQUID magnetization measurements were made on powder samples immobilized in epoxy. The hysteresis loops presented in Figure 6 show a more characteristic shape than for Mn-Al-C, and nonzero coercivity was demonstrated above room temperature. Fitting the temperature dependence of the coercivity to equation 1 as shown in Figure 7 yielded a blocking temperature of approximately 3800 °K, far in excess of the Curie temperature for any samarium cobalt alloy. The model used to understand the loss of hysteresis above the blocking temperature breaks down above T c where the exchange coupling between spins on neighboring atoms is disrupted by thermal fluctuations and the particle ceases to have a giant magnetic moment. Above T c , regardless of the calculated blocking temperature, hysteresis will cease to exist . The phenomenon of nonzero coercivity in monodomain ferromagnets at and above room temperature is real and has potential significance for particulate recording media. Small ferromagnetic particles are commonly used in magnetic recording tapes, but these particles are typically much larger than those discussed in this article. Larger particle sizes have previously been used in order to obtain stability against thermal fluctuations and small changes in the applied field. Stable alloy magnet nanocrystals, such as the SmCo x [C] particles prepared in a carbon arc, meet the stability requirements with smaller sizes, and are therefore a possibility for higher density data storage medium. In the foregoing specification certain preferred practices and embodiments of this invention have been set out, however, it will be understood that the invention may be otherwise embodied within the scope of the following claims.

Claims: We claim : 1. A magnetic metal or metal carbide nanoparticle having a carbon coating, said nanoparticle having a diameter -in the range of approximately 5 to 60 nm. 2. The nanoparticle of claim 1 wherein said nanoparticle is one of a crystallite having a diameter in the range of approximately 5 to 60 nm, an amorphous particle having a diameter in the range of approximately 5 to 60 nm and a nanotube having a length less than 1 cm and having a diameter in the range of 5 to 60 nm. 3. The nanoparticle of claim 1 wherein said nanoparticle is one of a paramagnetic and ferromagnetic compound. 4. The nanoparticle of claim 3 wherein said ferromagnetic compound is selected from the group consisting of iron, cobalt, nickel, and manganese bismuth. 5. The nanoparticle of claim 3 wherein said paramagnetic compound is selected from the group consisting of the transition metals . 6. The nanoparticle of claim 5 wherein said paramagnetic compound is selected from the group consisting of the rare earth metals except lanthanum, lutetium and promethiu . 7. A magnetic metal or metal carbide nanoparticle formed by preparing graphite rods, said graphite rods being packed with a magnetic metal oxide, subjecting said packed graphite rods to a carbon arc discharge to produce soot containing magnetic metal or metal carbide nanoparticles and non-magnetic species, and applying a magnetic field gradient to said soot to separate said magnetic metal or metal carbide nanoparticles from said non-magnetic species. 8. The nanoparticle of claim 7 wherein said nanoparticle is one of a paramagnetic and ferromagnetic compound. 9. The nanoparticle of claim 8 wherein said ferromagnetic compound is selected from the group consisting of iron, cobalt, nickel, and manganese bismuth. 10. The nanoparticle of claim 8 wherein said paramagnetic compound is selected from the group consisting of the transition metals. 11. The nanoparticle of claim 10 wherein said paramagnetic compound is selected from the group consisting of the rare earth metals except lanthanum, lutetiu and promethium. 12. The nanoparticle of claim 8 wherein said nanoparticle is segregated by magnetic moment per volume by varying the magnetic field gradient applied to said soot. 13. A method for forming a magnetic metal or metal carbide nanoparticle comprising the steps of : a. preparing graphite rods, said graphite rods being packed with a magnetic metal oxide; b. subjecting said packed graphite rods to a carbon arc discharge to produce soot containing magnetic metal or metal carbide nanoparticles and non-magnetic species; and c. applying a magnetic field gradient to said soot to separate said magnetic metal or metal carbide nanoparticles from said non-magnetic species. 14. The method of claim 13 wherein said nanoparticle is one of a paramagnetic and ferromagnetic compound. 15. The method of claim 14 wherein said ferromagnetic compound is selected from the group consisting of iron, cobalt, nickel, and manganese bismuth. 16. The method of claim 14 wherein said paramagnetic compound is selected from the group consisting of the transition metals. 17. The method of claim 16 wherein said paramagnetic compound is selected from the group consisting of the rare earth metals except for lanthanum, lutetium and promethium. 18. The method of claim 14 further comprising the step of varying the magnetic field gradient applied to said soot to segregate said magnetic metal or metal carbide nanoparticle according to its magnetic moment per volume. 19. A metal or alloy nanoparticle formed by preparing a graphite rod, said graphite rod being packed with said metal or alloy, or an oxide of said metal or alloy, subjecting said packed graphite rod to a carbon arc discharge to produce soot containing metal, alloy, or metal carbide nanoparticles and non-magnetic species, and applying a magnetic field gradient to said soot to separate said metal, alloy, or metal carbide nanoparticles from said non-magnetic species. 20. The nanoparticle of claim 19 wherein said nanoparticle is one of a ferromagnetic and paramagnetic compound. 21. The nanoparticle of claim 20 wherein said nanoparticle exhibits hysteresis at room temperature. 22. The nanoparticle of claim 21 wherein said metal alloy is samarium cobalt. 23. The nanoparticle of claim 22 wherein said samarium cobalt is in the form of at least one of SmCo 5 , Sm-Co 2 , Sm 2 Co 7 , and Sm 2 Co 17 . 24. The nanoparticle of claim 21 wherein said metal alloy is a manganese-aluminum compound. 25. The nanoparticle of claim 24 wherein said manganese-aluminum compound is manganese-aluminum-carbide. 26. A method for forming a metal or alloy nanoparticle comprising the steps of: a. preparing a graphite rod, said graphite rod being packed with said metal or alloy or an oxide of said metal or alloy; b. subjecting said packed graphite rod to a carbon arc discharge to produce soot containing magnetic metal alloy nanoparticles and non-magnetic species; and c. applying a magnetic field gradient to said soot to separate said magnetic metal alloy nanoparticles from said non-magnetic species. 27. The method of claim 26 wherein said nanoparticle is one of a ferromagnetic and paramagnetic compound. 28. The method of claim 27 wherein said nanoparticle exhibits hysteresis at room temperature. 29. The method of claim 28 wherein said metal alloy is samarium cobalt. 30. The method of claim 29 wherein said samarium cobalt is in the form of at least one of SmCo s , Sm 2 Co 7 , and Sm 2 Co 17 . 31. The method of claim 28 wherein said metal alloy is a manganese-aluminum compound. 32. The method of claim 31 wherein said manganese- aluminum compound is manganese-aluminum-carbide . 33. A metal alloy nanoparticle which exhibits hysteresis at room temperature, wherein said metal alloy is one of samarium cobalt and a manganese-aluminum compound. 34. The nanoparticle of claim 33 wherein said samarium cobalt is in the form of at least one of SmCo 5 , Sm 2 Co 7 , and Sm 2 Co 17 . 35. The nanoparticle of claim 33 wherein said manganese-aluminum compound is manganese-aluminum-carbide.

Inventors: BRUNSMAN ELAINE, KIRKPATRICK SCOTT, MAJETICH SARA, MCHENRY MICHAEL, SCOTT JOHN HENRY, BRUNSMAN, ELAINE, KIRKPATRICK, SCOTT, MAJETICH, SARA, MCHENRY, MICHAEL, SCOTT, JOHN, HENRY
Applicants: UNIV CARNEGIE MELLON, CARNEGIE MELLON UNIVERSITY
Application year: 1994
Main classification: H01F1
IPC codes: B22F1, B22F9, C01B31, H01F1