Method of crosslinking polysilazane polymers

Abstract: The present invention describes a novel method for crosslinking polysilazane polymers having Si-H or N-H bonds. The method comprises mixing the polysilazane with a silazane crosslinker having at least 2 boron functional groups which can react with the Si-H or N-H bonds of the polysilazane and then facilitating crosslinking.

Description: The present invention relates to a method of crosslinking polysilazane polymers in which a certain boron modified silazane is used as a crosslinker. The invention also relates to a crosslinker comprising boron-modified tris-(trimethylsilylamino)silane and a method for manufacture. A variety of polysilazane oligomers, cyclics, resins and linear polymers are known in the art. They are characterized as having backbones with alternating silicon and nitrogen atoms. They have broad utility as precursors to a variety of ceramic materials such as ceramic monoliths, ceramic fibers and matrices for ceramic matrix composites. To be ceramic precursors, however, these polysilazanes must be curable (infusible) to prevent deformation of the ceramic upon heating. Various approaches to providing curability have been suggested. For instance, U.S. Patent No. 5,086,126 discloses a process for adding vinyl groups to a polysilazane such that the polymer would rapidly cure upon addition of a free radical precursor. EP-A-0 519 496 discloses a thermosetting copolymer useful as a ceramic precursor, obtained by copolymerising a silicon-containing polymer with a polyborosilazane or perhydropolysilazane. The polyborosilazanes used have number average molecular weights exceeding 2000. EP-A-0 448 432 discloses pyrolysing a carbon based substrate impregnated with a ceramic precursor mixture to form a ceramic coating on the substrate. The ceramic precursor mixture comprises a polysilazane and a polyborazane. Similarly, various references disclose the addition of boron compounds to polysilazanes to provide curability, such as U.S. Patent No. 5,169,908, U.S. Patent No. 5,030,744 and U.S. Patent No. 4,910,173. Seyferth et al. in J. Am. Ceram. Soc. 73, 2131-2133 (1990) and Noth in Z. Naturforsch, B. Anorg. Chem., Org. Chem., 16 [9] 618-621 (1961) describe similar addition processes in journals. Each of these references teaches the addition of boron to a polysilazane to render it infusible or to increase the molecular weight of the resultant polymer. By contrast, we have now found that a certain boron-modified silazane crosslinker can be utilized to render infusible nearly any polysilazane having Si-H or N-H bonds. The present invention therefore relates to a crosslinker of the formula: The present invention further provides a method for crosslinking a polysilazane having Si-H or N-H bonds. The method comprises mixing the polysilazane with a crosslinker having the formula given in claim 1 and exposing the mixture to conditions sufficient to facilitate crosslinking of the polysilazane. Finally, the invention relates to a method of forming the crosslinker which comprises reacting tris(trimethylsilylamino)silane with borane for a time and at a temperature sufficient to form the boron modified silane. The present invention introduces a boron-modified silazane crosslinker that can be used to crosslink polysilazanes and, thus, render them more useful as ceramic precursors. The claimed invention allows for better control over the crosslinking reaction and can lower the glass transition temperature (T g ) and the temperature storage modulus of the resin to impart a controllable tack depending on the extent of crosslinker addition. The method of curing the polysilazanes of this invention involves mixing the polysilazane with the crosslinker followed by facilitation of the crosslinking reaction by heating. Upon initiation, the boron of the crosslinker reacts with the Si-H and/or N-H bonds of the polysilazane to form Si-B and/or N-B bonds, respectively, and thus causes crosslinking. The useful polysilazanes herein are any which have N-H or Si-H bonds for reaction. Representative examples include those of U.S. Patent Nos. 4,312,970, 4,395,460, 4,340,619, 4,540,803, 4,543,344, 5,030,744, 4,656,300 and 4,689,252, or those of EP-A 0 332 374 and 0 351 747. The preferred polysilazane polymers are those of U.S. Patent No. 4,540,803. These polysilazanes are prepared by contacting and reacting in an inert, essentially anhydrous atmosphere, trichlorosilane and a disilazane at a temperature in the range of 25°C. to 300°C. while distilling volatile byproducts. The disilazane used in the process has the formula (R 3 Si) 2 NH where R is selected from vinyl radical, hydrogen atom, phenyl and alkyl radicals of 1 to 3 carbon atoms. The trichlorosilane is treated with the disilazane in sufficient amounts to react with all of the chlorine in the chlorine-containing silane. This is usually an equimolar amount based on the chlorine content of the trichlorosilane. The R' groups are independently selected from hydrogen atom, methyl, ethyl, propyl, vinyl and phenyl. Examples of suitable disilazanes include [(CH 3 ) 3 Si] 2 NH, [C 6 H 5 (CH 3 ) 2 Si] 2 NH, [(C 6 H 5 ) 2 CH 3 Si] 2 NH, [CH 2 =CH(CH 3 ) 2 Si] 2 NH, [CH 2 =CH(CH 3 )C 6 H 5 Si] 2 NH, [CH 2 =CH(C 6 H 5 ) 2 Si] 2 NH, [CH 2 =CH(C 2 H 5 ) 2 Si] 2 NH, [H(CH 3 ) 2 Si] 2 NH and [CH 2 =CH(C 6 H 5 )C 2 H 5 Si] 2 NH. An especially preferred embodiment of U.S. Patent No. 4,540,803 involves the reaction of trichlorosilane with hexamethyldisilazane. The resultant polymer produced thereby, hydridopolysilazane, has been shown to have valuable preceramic properties. The above reactants are brought together in an inert, essentially anhydrous atmosphere. By inert it is meant that the reaction is carried out under a blanket of inert gas such as argon, nitrogen or helium. What is meant by essentially anhydrous is that the reaction is preferably carried out in an absolutely anhydrous atmosphere but minute amounts of moisture can be tolerated. When the reactants are contacted with each other, an intermediate amino compound is formed. It is preferred that the reactants are brought together in such a manner to keep the initial reaction exotherm to a minimum. Upon continued heating additional amino compound is formed and, with further heating, R 3 SiCl is distilled from the reaction mixture and the silazane polymer is formed. For best results, the rate of heating should be controlled at a rate of less than 1°C./min. A heating rate of 0.5°C./min. or less is preferred. As the temperature of the reaction is raised, more condensation takes place and crosslinking occurs with residual and undistilled R 3 Si from the mixture acting as a chain stopper. This control allows one to stop the reaction at any point to obtain almost any desired viscosity. The desired temperature range for the reaction is 25°C to 300°C. with a temperature in the range of 125°C. to 275°C. being more preferred. The length of time that the reaction requires depends on the temperature employed and the viscosity one wishes to achieve. The crosslinker for use in the method of the present invention has the formula: Since each of the B-H bonds of the crosslinker are potential sites for reacting with Si-H or N-H bonds of a polysilazane, the crosslinker is hexafunctional and can effectively infusibilize the polymer even when used in small amounts. This crosslinker can be prepared by a number of techniques. For convenience, however, it is formed by reacting tris(trimethylsilylamino)silane with borane to produce the desired crosslinker. Both reactants are known in the art and commercially available. Generally, any source of borane may be used. For instance, borane is available from Aldrich Chemical Co. as complexes with various Lewis bases. These include borane complexes with various amines, such as pyridine, butylamine or diethylamine; complexes with sulfides such as methyl sulfide: complexes with phosphines such as triphenylphosphine and complexes with ethers such as tetrahydrofuran. Although any source of borane may be used, the present inventor has found it convenient to use boranetetrahydrofuran complex. The stoichiometric amount of borane used in this invention is three moles of borane per mole of tris(trimethylsilylamino)silane. It is generally preferred to use two to three moles of borane per mole of tris(trimethylsilylamino)silane. However, greater or lesser amounts may be used. If less than a stoichiometric amount is used, residual N-H will be present. If greater than a stoichiometric amount is used, excess borane may be present after the reaction that could cause other, undesired reactions. The reaction of the silane can be conducted with or without a solvent. The solvents which may be used herein include any which can act as a solvent for the borane, the silane and the boron-modified silane, without adversely affecting any of the above reactants. Examples of such solvents include alkanes such as pentane, hexane, heptane and octane, ethers, such as tetrahydrofuran or aromatic hydrocarbons, such as benzene, toluene and xylene. Generally, if the borane-tetrahydrofuran complex is used in the reaction, it is convenient to use tetrahydrofuran or mixtures of tetrahydrofuran with aromatic hydrocarbons as the solvent. The reaction of the silane and borane is conducted by mixing the silane and the borane in a suitable reaction vessel. This reaction can be performed at any suitable temperature or pressure and in any convenient atmosphere. For simplicity, however, it is generally run at room temperature under an inert atmosphere and at atmospheric pressure. Since an exotherm generally occurs when the silane and the borane are mixed, it is often preferred to control the exotherm by slowly adding the borane to a solution of the silane. Continued stirring of this mixture (for 1-24 hours) results in formation of the desired modified silane. The boron-modified silane produced by the above reaction is then recovered from solution. Numerous methods such as simple evaporation or stripping of the solvent under heat and/or vacuum are known in the art and useful herein. The above crosslinker is then mixed with the polysilazane and the crosslinking reaction is initiated. The polysilazane and the crosslinker may be mixed together in their liquid state or, alternatively, they may be blended in a solvent. The solvents which may be used herein include any which act as a solvent for both the polysilazane and the crosslinker and which do not cause their rearrangement. Examples of such solvents include alkanes; such as pentane, hexane, heptane and octane; ethers such as tetrahydrofuran; or aromatic hydrocarbons such as benzene, toluene or xylene. The crosslinker and the polysilazane may be blended in nearly any ratio desired to provide sufficient tack, flow and final cure. Generally, however, the crosslinker is present in an amount of at least 0.01 wt. % crosslinker based on the weight of the polysilazane with a range of 0.01 to 50 wt. % being preferred. In addition, it is also contemplated herein that several polysilazanes (varying viscosity), several crosslinkers or other desirable materials (ceramic fillers) may be blended with the mixture to provide highly desirable properties. The polysilazane/crosslinker mixture is then exposed to conditions which facilitate the crosslinking reaction. Generally, this involves merely heating the mixture to a sufficient temperature. Temperatures in the range of 50-500°C. are generally sufficient. Other means of inducing crosslinking such as radiation or crosslinking catalysts are, however, also contemplated. The polysilazane and crosslinker blend is useful for many purposes such as in the formation of fibers, monoliths and as matrices for ceramic matrix composites. In addition, the material may be used to impregnate porous ceramic bodies to increase density. The following examples are provided so that one skilled in the art may more fully understand the invention. In these examples, 1 H NMR spectra were recorded on a Varian or EM390 spectrometer. FTIR data were recorded on a Perkin Elmer Series 1600 spectrometer. Gel permeation chromatography (GPC) data were obtained on a Waters GPC equipped with a model 600 E systems controller, a model 490 UV and model 410 Differential Refractometer detectors; all values are relative to polystyrene. TMA data were recorded on a Du Pont 940 thermomechanical analyzer (TMA) interfaced to an Omnitherm 2066 computer. Carbon, hydrogen and nitrogen analyses were performed on a Control Equipment Corporation 240-XA Elemental Analyzer. Boron and silicon was determined by a fusion technique which consisted of converting the silicon material to soluble forms of silicon and analyzing the solute for total silicon by atomic absorption spectrometry. All furnace firings were done in an Astro graphite furnace equipped with Eurotherm temperature controllers. The furnace was equipped with an Ircon Modeline Plus optical pyrometer to monitor the temperature above 900°C. Example 1 Preparation of Boron-Modified Tris(trimethylsilylamino)silane Route A A 500 ml 3 necked flask fitted with an argon inlet, an overhead stirrer and an addition funnel was charged with 29.3 g tris(trimethylsilylamino)silane (0.10 mole) distilled from the reaction of trichlorosilane and hexamethyldisilazane under argon. The addition funnel was charged with 300 ml of a 1.0 M BH 3 -THF solution in THF (obtained from Aldrich Chemical Company). This borane solution was added to the flask over a 2 hour period which was accompanied by a mild exotherm and gas- evolution. The resulting solution was stirred 16 hours and then stripped of volatiles at 60°C. in vacuo resulting in 32 g of a liquid product. The IR spectrum of tris(trimethylsilylamino)silane was compared with the above boron modified product. The spectrum of the boron-modified product showed stretches at 2450 cm -1 and 1350 cm -1 indicating the presence of B-H and N-H bonds respectively. Additionally, stretches at 3350 cm -1 indicating the presence of N-H bonds were decreased in the boron modified product. Route B A 1 l 3 necked flask fitted with an argon inlet, an overhead stirrer and an addition funnel was charged with 500 ml of a 1.0 M BH 3 -THF solution in THF (obtained from Aldrich Chemical Company). The addition funnel was charged with 54 g tris(trimethylsilylamino)silane (0.18 mole) distilled from the by-products of the reaction of trichlorosilane and hexamethyldisilazane under argon. The silane was added to the flask over a 1 hour period which was accompanied by a mild exotherm and gas evolution. The resulting solution was stirred 48 hours and then stripped of volatiles at 60°C. in vacuo resulting in 57 g of a liquid product. Example 2 Cure Properties Hydridopolysilazane made by the method of U.S. Patent No. 4,540,803 was blended with the boron-modified tris(trimethylsilylamino)silane of Example 1 at 30 parts per weight crosslinker per 100 parts hydridopolysilazane in a toluene solution. As a control, tris(trimethylsilylamino)silane was also blended with the hydridopolysilazane in the same amounts. These solutions were then used to impregnate fiber braids suitable for torsional braid analysis (TBA). The braids were dried, placed in a TBA spectrometer for testing and heated to 288°C. for 6 hours. The data acquired is shown graphically in Figure 1. The storage modulus is equivalent to the stiffness of the sample and shows that the sample containing the boron modified crosslinker increases in stiffness corresponding to the crosslinking reaction. The fact that little increase in stiffness is seen with the control implies that very little crosslinking is occurring in that system. Example 3 Char Composition Hydridopolysilazane (HPZ) made by the method of U.S. Patent No. 4,540,803 (Mw = 10,000) was blended with the boron-modified tris(trimethylsilylamino)silane of Example 1 at varying ratios. The blends were fired at 1400°C. to determine the effect of the crosslinker on the composition of the final ceramic. The results are presented in the following table. It should be noted that the crosslinker does not have a significant impact on the final ceramic char, especially the carbon content which could be detrimental to the composite oxidation properties. Parts Crosslinker/ 100 parts HPZ Char Yield %C %N - 69.60 11.82 28.17 10 70.08 12.40 26.54 20 70.19 12.49 25.76 30 71.11 12.32 24.60

Claims: A crosslinker of the structure: A method of crosslinking a polysilazane having Si-H or N-H bonds which comprises the steps of mixing the polysilazane with a crosslinker according to claim 1 and exposing the mixture to conditions sufficient to facilitate crosslinking of the polysilazane. The method of claim 2 wherein the polysilazane comprises hydridopolysilazane. The method of claim 2 or claim 3 wherein the crosslinking reaction is facilitated by a means selected from heating the mixture to a sufficient temperature, exposing the mixture to radiation and adding a crosslinking catalyst. The method of claim 4 wherein the crosslinking reaction is facilitated by heating the mixture to a temperature in the range of 50-500°C. The method of claim 2 wherein the crosslinker is mixed with the polysilazane in an amount of from 0.01 to 50 wt % based on the weight of the polysilazane. A method of forming a crosslinker according to claim 1 which comprises reacting tris(trimethylsilylamino)silane with borane for a time and at a temperature sufficient to form the crosslinker. The method of claim 7 wherein the amount of borane is from two to three moles of borane per mole of tris(trimethylsilylamino)silane. The method of claim 7 wherein the reaction is run at room temperature under an inert atmosphere and at atmospheric pressure. The method of claim 7 wherein the reaction is conducted in a solvent.

Inventors: BARNARD THOMAS DUNCAN, BUJALSKI DUANE RAY, ZANK GREGG ALAN, BARNARD, THOMAS DUNCAN, BUJALSKI, DUANE RAY, ZANK, GREGG ALAN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1994
Main classification: C08G77
IPC codes: C08G77, C07F7, C08J3