PROCESS FOR MAKING CROSS-LINKED ETHYLENIC POLYMER FOAM STRUCTURES

Abstract: Disclosed is a process for making a cross-linked ethylenic polymer foam structure of an ethylenic polymer material of a cross-linked, substantially linear ethylenic polymer. The substantially linear ethylenic polymer has in an un-crosslinked state: (a) a melt flow ratio, I10/I2 >/= 5.63; (b) a molecular weight distribution, Mw/Mn, defined by the equation: Mw/Mn </= (I10/I2) - 4.63; and (c) a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylenic polymer having about the same I2 and Mw/Mn. Further disclosed is a process for making the above foam structure.

Description: PROCESS FOR MAKING CROSS-LINKED ETHYLENIC POLYMER FOAM STRUCTURES 5 This invention relates to a composition of and a process for manufacturing a cross-linked ethylenic polymer foam structure having enhanced processabi ty and physical properties Commercially-available, cross-linked ethylenic polymer foam structures (XLPE) are typically made with conventional low density polyethylene (LDPE) resins made by high pressure j ø processes LDPE resins have found favor because of their relatively low melt temperatures and desirable processabihty It would be desirable to have an XLPE foam structure with enhanced strength and resiliency, yet retain the low foam density and desirable resin processabihty afforded by the use of LDPE resins One means of enhancing strength and resiliency is to employ a conventional - 5 linear low density polyethylene (LLDPE), a copolymer of ethylene and a C 10 alpha-olef in Unfortunately, LLDPE resin is difficult to process and to a XLPE foam, and results in a relatively high density foam structure with poor quality It would be desirable to have an XLPE foam structure similar in strength and resiliency to an XLPE foam structure of LLDPE while comprising a resin having in an un-crosshnked state processabihty similar to an LDPE resin 20 According to the present invention, there is a cross-linked ethylenic polymer foam structure of an ethylenic polymer material of a cross-linked, substantially linear ethylenic polymer The substantially linear ethylenic polymer has in an un-crosshnked state a- a) a melt flow ratio, I10 I2. ≥ 5 63; b) a molecular weight distribution, M w /M n , defined by the equation M w /M n < (l ιo/l 2 ) - 4 63; and c) a critical shear rate at onset of surface melt fracture of at least 25 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylenic polymer having about the same l 2 and M w /M n The foam structure is strong, resilient, and of low density The structure has high strength and resiliency similar to that of a foam structure comprised of cross-linked LLDPE, and has low density and quality similar to that of a foam structure of cross-linked LDPE 30 Further according to the present invention, there is a process for making a cross- linked ethylenic polymer foam structure First, a foamable melt polymer material is formed by blending and heating a decomposable chemical blowing agent and an ethylenic polymer material comprising a substantially ethylenic polymer having, a) a melt flow ratio, o^'2. — 5 63, b) a molecular weight distribution, M w /M n , defined by the equation- M w /M n < (lιo l 2 ) - 35 4 63, and c) a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylenic polymer having about the same l 2 and M w /M n Second, cross-linking is induced in the foamable melt polymer material Third, the foamable melt polymer material is expanded by exposing it to an elevated temperature to form the foam structure The substantially linear ethylenic polymer has better processabi ty and foamability than LLDPE and similar to that of LDPE The present cross-linked foam structure offers a number of advantages over cross- linked foam structures of the prior art The present structure has desirable high strength and resiliency similar to that of a foam structure of cross-linked LLDPE, and has a desirable low density similar to that of a foam structure of cross-linked LDPE The present structure has greater strength and resiliency than a cross-linked LDPE foam structure, can be made softer as well The present structure can have softness similar to foam structures of a soft ethylene o copolymer, for example, ethylene/vinyl acetate (EVA) copolymer or a blend of polyvinylchloπde and a nitπle rubber, but has greater strength and resiliency. In addition, the present structure, being more thermally stable than an EVA foam structure, does not liberate unpleasant smell during foam expansion, fabrication, and usage Soft, strong cross-linked foam structures are useful in sporting good, medical device, and cushioning applications 5 In the following paragraphs, the chemical and physical characteristics of the substantially linear ethylenic polymer in a substantially non-crosshnked or un-crosshnked state and methods for making same are described The substantially linear ethylenic polymer is cross-linked and expanded or foamed to form the present cross-linked foam structure The desirable characteristics of the non-crosshnked or un-crosshnked polymer aid in extrusion and 0 processing of the polymer prior to and during cross-linking and foaming Elastic, substantially linear ethylenic polymers have unusual properties, including an unusual combination of properties, which leads to enhanced processabihty of the novel polymers The substantially linear ethylenic polymers have processabihty similar to highly branched low density polyethylene, but the strength and toughness similar to linear low 5 density polyethylene The substantially linear ethylenic polymers preferably have a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylenic polymer having about the same l 2 and M w /M n 0 The elastic substantially linear ethylenic polymers also have a processing index (PI) less than or equal to 70 percent of the PI of a comparati e linear ethylenic polymer at about the same l 2 and M w /M n The elastic substantially linear ethylenic polymers also preferably have a melt flow ratio, ho/l 2 . ≥ 5 63, and preferably a molecular weight distribution, M w /M n , defined by the 5 equation. M w /M n < (l 10 /l 2 ) - 4 63 Elastic substantially linear ethylenic polymers comprising ethylene homopolymers or a copolymer of ethylene with at least one C 3 -C 2 oα-olefιnιc (alpha-olefinic) comonomer are especially preferred Other properties of the substantially linear polymers include: a) a density preferably from 0.85 grams/cubic centimeter (g/cm3) to 0.97 g/cm3; and b) a melt index, l , preferably from 0.01 grams/10 minutes to 1000 gram/10 minutes. Preferably the melt flow ratio, o/ϊ 2 , is from 7 to 20. The molecular weight distribution (M w /M n ) is preferably 3.5 or less, more preferably from 1.5 to 2.5, and most preferably from 1.7 to 2.3. Throughout this disclosure, "melt index" or "l " is measured in accordance with ASTM D-1238 (190°C/2.16 g); "l 10 " is measured in accordance with ASTM D-1238 (190°C 10 kg). The melt tension of these new polymers is also surprisingly good, for example, as high as 2 grams or more, especially for polymers which have a very narrow molecular weight distribution (that is, Mw/M n from 1.5 to 2.5). A preferred substantially linear ethylenic polymer useful in the present foam structure has the following properties: a melt flow ratio index l 2 (measured per ASTM method D-1238 condition E) of 0.5 to 20 dg/min, preferably, from 2.5 to 10 dg/min; a melt index ratio, l 10 /l 2 (per ASTM D1238) greater than 7.5, more preferably greater than 9; a single DSC (differential scanning calorimetry) melting peak. The substantially linear polymers can be homopolymers of ethylene (polyethylene) or they can be copolymers of ethylene with at least one C3-C20 α-olef inic and/or C 2 -C 2 o acetylenically compounds and/or C -Cιβ diolefinics and/or other unsaturated comonomers. Useful comonomers include ethylenically unsaturated monomers, conjugated or nonconjugated dienes, polyenes. Preferred monomers include the C 3 -Cιoα-olefinics especially 1-propene, isobutylene, 1-butene, 1-hexene, 4-methyl-1-pentene, and 1-octene. Other useful comonomers include styrene, halo- or alkyl substituted styrenes, tetrafluoroethylene, vinylbenzocyclobutane, 1,4-hexadiene, and naphtenics (for example, cyclo-pentene, cyclo- hexene and cyclo-octene). The term "substantially linear polymers" means that the polymer backbone is substituted with 0.01 long chain branches/1000 carbons to 3 long chain branches/1000 carbons, more preferably from 0.01 long chain branches/1000 carbons to 1 long chain branches/1000 carbons, and especially from 0.05 long chain branches/1000 carbons to 1 long chain branches/1000 carbons. The term "linear ethylenic polymers" means that the ethylenic polymer does not have long chain branching. That is, the linear ethylenic polymer has an absence of long chain branching, as for example the conventional linear low density polyethylene polymers or linear high density polyethylene polymers made using Ziegler polymerization processes (for example, U.S. Patent No. 4,076,698 or 3,645,992). The term "linear ethylenic polymers" does not refer to branched ethylenic polymers such as branched polyethylene, ethyl ene/vinyl acetate copolymers, or ethylene/ester copolymers which are made by high pressure processes and known to those skilled in the art to have numerous long chain branches. Long chain branching is defined herein as a chain length of at least 6 carbons, above which the length cannot be distinguished using 13 C nuclear magnetic resonance (NMR) spectroscopy. The long chain branch can be as long as about the same length as the length of the polymer back-bone. Long chain branching is determined by using 13C NMR spectroscopy and is quantified using the method of Randall (Rev. Macromol. Chem. Phvs.. C29 (2&3), p. 285-297). Excellent teachings regarding substantially linear ethylenic polymers and processes for making are seen in U.S. Serial Nos. 07/939,281 , filed September 9, 1992 and 07/776.130, filed October 15, 1992. "Melt tension" is measured by a specially designed pulley transducer in conjunction with the melt indexer. Melt tension is the load that the extrudate or filament exerts while passing over the pulley at the standard speed of 30 rpm. The melt tension measurement is similar to the "Melt Tension Tester" made by Toyoseiki and is described by John Dealy in Rheometers for Molten Plastics, published by Van Nostrand Reinhold Co. ( 1982) on page 250-251. The SCBDI (Short Chain Branch Distribution Index) or CDBI (Composition Distribution Branch Index) is defined as the weight percent of the polymer molecules having a comonomer content within 50 percent of the median total molar comonomer content. The CDBI of a polymer is readily calculated from data obtained from techniques known in the art, such as, for example, temperature rising elution fractionation (abbreviated herein as "TREF") as described, for example, in Wild et al. Journal of Polymer Science. Poly. Phvs. Ed.. Vol. 20, p. 441 (1982), or in U.S. Patent No. 4,798,081. The SCBDI or CDBI for the substantially linear ethylenic polymers of the present invention is preferably greater than 30 percent, especially greater than 50 percent. Thus, the substantially linear polymers are homogeneously branched. A unique characteristic of the present polymers is a highly unexpected flow property where the lιo l 2 value is essentially independent of polydispersity index (that is, M w /M n ). This is contrasted with conventional polyethylene resins having rheological properties such that as the polydispersity index increases, the lιo/l 2 value also increases. Forthe substantially linear ethylenic polymers described herein, the \-of value indicates the amount of long chain branching (that is, the higher the I10/I2 value, the more long chain branching). The density ot the ethylene or ethylene/α-olefinic substantially linear ethylenic polymers is measured in accordance with ASTM D-792 and is generally from 0.85 g/cm 3 to 0.97 g/cm 3 and preferably from 0.87 g/cm 3 to 0.95 g/cm 3 . The molecular weight of the ethylene or ethylene/α-olefinic substantially linear ethylenic polymers in the present invention is conveniently indicated using a melt index measurement according to ASTM D- 1238, Condition 190°C 2.16 kg (formally known as "Condition (E)" and also known as l 2 ). Melt index is inversely related to the molecular weight of the polymer. Thus, the higher the molecular weight, the lower the melt index, although the relationship is not linear. The melt index for the ethylene or ethylene/α-olefinic substantially linear ethylenic polymers used herein is generally from 0.01 grams/10 minutes (g/10 min) to 1000 g/10 min, preferably from 0.05 g/10 min to 100 g/10 min, and especially from 0.1 g/10 min to 20 g/10 min. Additives such as antioxidants (for example, hindered phenolics (for example, Irganox* 1010), phosphites (for example, Irgafos* 168)), pigments can also be included in the polyethylene compositions, to the extent that they do not interfere with the enhanced properties discovered by applicants. Ethylenic polymer materials of blends of the substantially linear ethylenic polymer and a suitable different ethylenic polymer or other natural or synthetic polymers are possible. Suitable different ethylenic polymers include low (LDPE) (for example, high pressure, free-radical polymerization techniques), medium (MDPE), and high density polyethylenes (HDPE) (for example, those made using Ziegler catalysts as in U.S. Patent No. 4,076,698), ethylene/ester copolymers, ethylene/vinyl acetate copolymers, copolymers of ethylene and ethylenically unsaturated carboxylic acid, homo and copolymers of alpha-ethylenics, etc. Other suitable polymers include polystyrene (including high impact polystyrene, styrene-butadiene block copolymers, polyisoprene, and other rubbers. Blends comprising a major proportion of the resin having the higher melting point are preferred. Regardless of composition, the ethylenic polymer material preferably comprises greater than 50 and more preferably greater i than 70 weight percent of ethylenic monomeric units. The ethylenic polymer material may be comprised completely or entirely of ethylenic monomeric units. Preferred blends are those with the substantially linear ethylenic polymer and other conventional ethylenic polymers such as LDPE, HDPE, ethylene/acrylic acid copolymer (EAA), and LLDPE. The improved melt elasticity and processibility of the. substantially linear polymers according to the present invention result, it is believed, from their method of production. The polymers may be produced via a continuous (as opposed to a batch) controlled polymerization process using at least one reactor, but can also be produced using multiple reactors (for example, using a multiple reactor configuration as described in U.S. Patent No. 3,914,342) at a polymerization temperature and pressure sufficient to produce the polymers having the desired properties. According to one embodiment of the present process, the polymers are produced in a continuous process, as opposed to a batch process. Preferably, the polymerization temperature is from 20°C to 250°C, using constrained geometry catalyst technology. If a narrow molecular weight distribution polymer (M w /M n of from 1.5 to 2.5) having a higher lκ)/l 2 ratio (for example, \-oJ of 7 or more, preferably 8 or more, more preferably 9 or more) is desired, the ethylene concentration in the reactor is preferably not more than 8 percent by weight of the reactor contents, especially not more than 4 percent by weight of the reactor contents. Preferably, the polymerization is performed in a solution polymerization process. Generally, manipulation of o/l 2 while holding M w /M n relatively low for producing the novel polymers described herein is a function of reactor temperature and/or ethylene concentration. Reduced ethylene concentration and higher temperature generally produces higher IKJ/12- The molecular weight distribution (M w /M n ) of the individual polymer samples is analyzed by gel permeation chromatography (GPC) on a Waters 150°C high temperature chromatographic unit equipped with three mixed porosity columns (Polymer Laboratories 10 3 , 10 4 , 10 5 , and 10 6 ), operating at a system temperature of 140°C. The solvent is 1 ,2,4- trichlorobenzene, from which 0.3 percent by weight solutions of the samples are prepared for injection. The flow rate is 1.0 milliliters/minute and the injection size is 200 microliters. The molecular weight determination is deduced by using narrow molecular weight distribution polystyrene standards (from Polymer Laboratories) in conjunction with their elution volumes. The equivalent polyethylene molecular weights are determined by using appropriate Mark-Houwink coefficients for polyethylene and polystyrene (as described by Williams and Word in Journal of Polymer Science, Polymer Letters. Vol. 6, (621 ) 1968) to derive the following equation: M po | yet hyiene = a * ( M polystyrene) b - In this equation, a = 0.4316 and b = 1.0. Weight average molecular weight, M w , is calculated in the usual manner according to the following formula: M w = Σ w,*Mj, where w, and M, are the weight fraction and molecular weight, respectively, of the i h fraction eluting from the GPC column. The rheological processing index (PI) is measured by a gas extrusion rheometer (GER). The GER is described by M. Shida, R.N. Shroff and L.V. Cancio in Polym. Enq. Sci.. Vol. 17, no. 1 1 , p. 770 (1977), and in Rheometers for Molten Plastics by John Dealy published by Van Nostrand Reinhold Co. (1982) on page 97-99. The processing index is measured at a temperature of 190°C, at nitrogen pressure of 2500 psig using 0.0296 inch diameter, 20: 1 L/D die having an entrance angle of 180 degrees. The GER processing index is calculated in millipoise units from the following equation: PI = 2.15 X 10* dynes/cmVO 000 X shear rate), wherein: 2.15 X 10 6 dynes/cm^ is the shear stress at 2500 psi, and the shear rate is the shear rate at the wall as represented by the following equation: 32 Q7(60 sec/min)(0.745)(Diameter X 2.54 cm/inR wherein: Q' is the extrusion rate (gms/min), 0.745 is the melt density of polyethylene (gm/cm J ), and Diameter is the orifice diameter of the capillary (inches). The PI is the apparent viscosity of a material measured at apparent shear stress of 2.15 x 10" dyne/cm J . For the substantially linear ethylenic polymers disclosed herein, the PI is less than or equal to 70 percent of that of a comparative linear ethylenic polymer at about the same l 2 and M w /M n . Suitable constrained geometry catalysts for use herein preferably include constrained geometry catalysts as disclosed in U.S. Serial Nos.: 545,403, filed July 3, 1990; 758,654, filed September 12, 1991 ; 758,660, filed September 12, 1991 ; and 720,041, filed June 24, 1991. The monocyclopentadienyl transition metal ethylenic polymerization catalysts taught in U.S. Patent No. 5,026,798 are also suitable for use in preparing the polymers of the present invention. Constrained-geometry catalysts useful in making the substantially linear ethylenic polymer comprise a metal complex and a cocatalyst. Metal complexes correspond to the Formula (I): ( I ) 2 Y wherein: M is selected from the group consisting of groups 3- 10 or the Lanthanide series of the Periodic Table of the Elements; Cp* is selected from the group consisting of indenyl, tetrahydroindenyl, fluorenyl, octahydrofluorenyl, tetrahydrofluorenyl, cyclopentadienyl, and R-substituted cyclopentadienyl bound in an η5 bonding mode to M; x is, independently each occurrence, an anionic ligand group selected from the group consisting of hydride, halide, alkyl of up to 30 carbon atoms, alkoxy having up to a total of 30 carbon and oxygen atoms, cyanide, azide, acetylacetonate, aryl of up to 30 carbon atoms, aryloxy having up to a total of 30 carbon and oxygen atoms, norbomyl, and benzyl; n is O, 1 , 2, 3, or 4 and is 2 less than the valence of M; Y is NR", PR", 0, or S; Z is CR 2 *, CR 2 *CR 2 *. SiR 2 *. SiR 2 *SiR 2 *; R is selected from the group consisting of alkyl having 1 to 20 carbon atoms, cyano, norbornyl, benzyl, aryl of up to 20 carbon atoms, (R') 3 Si, and (R'^Ge; R' is selected from the group consisting of C C 2 o alkyl and aryl of up to 20 carbon atoms; R" is selected from the group consisting of C o alkyl, aryl of up to 20 carbon atoms, benzyl, haloaryl having up to a total of 20 carbon and halogen atoms, 2- methoxyphenyl, 4-methoxyphenyl, and norbornyl; and R* is selected from the group consisting of hydrogen, C-|-C 2 o alkyl, haloalkyl having up to a total of 20 carbon and halogen atoms, aryl of up to 20 carbon atoms, and haloaryl of up to a total of 20 carbon and halogen atoms. Preferred metal complexes are those of Formula (I) wherein: M is titanium, zirconium, or hafnium; X is, independently each occurrence, selected from the group consisting of halide, alkyl of up to 30 carbon atoms, aryl of up to 30 carbon atoms, and benzyl; n is 1 or 2; Y is R"; Z is CR 2 *CR 2 * or SiR 2 *; R is selected from the group consisting of alkyl having 1 to 20 carbon atoms, benzyl, aryl of up to 20 carbon atoms, and (R') 3 Si; R' is selected from the group consisting of C^C^ alkyl and aryl of up to 20 carbon atoms; R" is selected from the group consisting of C 1 -C20 alkyl, aryl of up to 20 carbon atoms, and benzyl; and R* is selected from the group consisting of hydrogen, C C 2 o alkyl, and aryl of up to 20 carbon atoms. It should be noted that the complex may exist as a dimer or higher oligomer. Further preferably, at least one of R, Z, or R" is an electron donating moiety. Thus, highly preferably Y is a nitrogen or phosphorus containing group corresponding to the formula -NR"- or -PR"- wherein R" is Cι-C 2 o alkyl, that is, an alkyl amido or alkyl phosphido group. Most highly preferred complex compounds are amidosilane- or amidoalkanediyl- compounds corresponding to Formula (II): ( I! ) ' (X)n wherein: M is titanium, zirconium or hafnium, bound in an η5 bonding mode to the cyclopentadienyl group; R' each occurrence is independently selected from the group consisting of hydrogen, silyl, alkyl, aryl and combinations thereof, said R' having up to 10 carbon or silicon atoms; E is silicon or carbon; X independently each occurrence is hydride, halo, alkyl, aryl, aryloxy or alkoxy, said X having up to 10 carbons; m is 1 or 2; and n is 1 or 2. Examples of the above most highly preferred metal coordination compounds include compounds wherein the R' on the amido group is methyl, ethyl, propyl, butyl, pentyl, hexyl, (including isomers), norbornyi, benzyl, or phenyl; the cyclopentadienyl group is cyclopentadienyl, indenyl, tetrahydroindenyl, fluorenyl, or octahydrofluorenyl; R" on the foregoing cyclopentadienyl groups each occurrence is hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, (including isomers), norbornyi, benzyl, or phenyl; and X is chloro, bromo, iodo, methyl, ethyl, propyl, butyl, pentyl, hexyl, (including isomers), norbornyi, benzyl, or phenyl. Specific compounds include: (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)- 1,2-ethanediylzirconium dichloride, (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)-1,2- ethanediyltitanium dichloride, (methylamido)(tetramethyl-η5-cyclopentadienyl)-1,2- ethanediylzirconium dichloride, (methylamido)(tetramethyl-η5-cyclopentadienyl)-1,2- ethanediyltitanium dichloride, (ethylamido)(tetramethyl-η5-cyclopentadienyl)- methylenetitanium dichloro, (tertbutylamido)dibenzyl(tetramethyl-η5-cyciopentadienyl) silanezirconium dibenzyl, (benzylamido)dimethyl- (tetramethyl-η 5 - cyclopentadienyl)silanetitanium dichloride, (phenylphosphido)dimethyl(tetramethyl-η5- cyclopentadienyl)silanezirconium dibenzyl, and (tertbutylamido)dimethyl(tetramethyl-ηS- cyclopentadienyl)silanetitanium dimethyl. The complexes may be prepared by contacting a derivative of a metal, M, and a group I metal derivati e or Grignard derivative of the cyclopentadienyl compound in a solvent and separating the salt byproduct. Suitable solvents for use in preparing the metal complexes are aliphatic or aromatic liquids such as cyclohexane, methylcyclohexane, pentane, hexane, heptane, tetrahydrofuran, diethyl ether, benzene, toluene, xylene, ethylbenzene, or mixtures thereof. In a preferred embodiment, the metal compound is MX n + 1 , that is, M is in a lower oxidation state than in the corresponding compound, MX n + and the oxidation state of M in the desired final complex. A noninterfering oxidizing agent may thereafter be employed to raise the oxidation state of the metal. The oxidation is accomplished merely by contacting the reactants utilizing solvents and reaction conditions use in the preparation of the complex itself. By the term " noninterfering oxidizing agent" is meant a compound having an oxidation potential sufficient to raise the metal oxidation state without interfering with the desired complex formation or subsequent polymerization processes. A particularly suitable noninterfering oxidizing agent is AgCI or an organic halide such as methylene chloride. The foregoing techniques are disclosed in U.S. Serial Nos. 545,403, filed July 3, 1990 and 702,475, filed May 20, 1991. Additionally the complexes may be prepared according to the teachings of the copending U.S. Serial No. 778,433 entitled: "Preparation of Metal Coordination Complex (I)", filed in the names of Peter Nickias and David Wilson, on October 15, 1991 and the copending U.S. Serial No. 778,432 entitled: "Preparation of Metal Coordination Complex (II)", filed in the names of Peter Nickias and David Devore, on October 15, 1991. Suitable cocatalysts for use herein include polymeric or oligomeric aluminoxanes, especially methyl aluminoxane, as well as inert, compatible, noncoordinating, ion forming compounds. So-called modified methyl aluminoxane (MMAO) is also suitable for use as a cocatalyst. One technique for preparing such modified aluminoxane is disclosed in U.S. Patent No. 5,041 ,584. Aluminoxanes can also be made as disclosed in U.S. Patent Nos. 5,542, 199, 4,544,762, 5,015,749, and 5,041 ,585. Preferred cocatalysts are inert, noncoordinating, boron compounds. Ionic active catalyst species which can be used to polymerize the polymers described herein correspond to Formula (III): wherein: M, Cp*, X, Y, and Z are as defined for Formula (I) above; n is 1 , 2, 3, or 4 and is 2 less than the oxidation state of M; and A- is a noncoordinating, compatible anion. As used herein, the recitation "noncoordinating, compatible anion" means an anion which either does not coordinate to the monocyclopentadienyl or substituted monocyclopentadienyl group containing cation or which is only weakly coordinated to said cation thereby remaining sufficiently labile to be displaced by a neutral Lewis base. A noncoordinating, compatible anion specifically refers to a compatible anion which when functioning as a charge balancing anion in the catalyst system of this invention does not transfer an anionic substituent or fragment thereof to said cation thereby forming a neutral four coordinate metallocene and a neutral metal byproduct "Compatible anions" are anions which are not degraded to neutrality when the initially formed complex decomposes and are noninterfering with desired subsequent polymerization or other uses of the complex One method of making the ionic catalyst species which can be utilized to make the polymers of the present invention involve combining- a) at least one first component which is a mono(cyclopentadιenyl) derivative of a metal of Group 3-10 or the Lanthanide Series of the Periodic Table of the Elements containing at least one substituent which will combine with the cation of a second component (described hereinafter) which first component is o capable of forming a cation formally having a coordination number that is one less than its valence; and b) at least one second component which is a salt of a Bronsted acid and a noncoordinating, compatible anion More particularly, the non-coordinating, compatible anion of the Bronsted acid salt may comprise a single coordination complex comprising a charge-bearing metal or 5 metalloid core, which anion is both bulky and non-nucleophihc The recitation "metalloid", as used herein, includes non-metals such as boron, phosphorus which exhibit semi-metallic characteristics Illustrative, but not limiting examples of monocyclopentadienyl metal components (first components) which may be used in the preparation of cationic complexes are 0 derivatives of titanium, zirconium, vanadium, hafnium, chromium, lanthanum Preferred components are titanium or zirconium compounds. Examples of suitable monocyclopentadienyl metal compounds are hydrocarbyl-substituted monocyclopentadienyl metal compounds such as (tert-butylamιdo)(tetramethyl-η5-cyclopentadιenyl)- 1,2- ethanediylzirconium dimethyl, (tert-butylamιdo)(tetramethyl-η5-cyclopentadιenyl)-1,2- 5 ethanediyltitanium dimethyl, (methylamιdo)(tetramethyl-η5-cyclopentadιenyl)-1 ,2- ethanediylzirconium dibenzyl, (methylamιdo)(tetramethyl-η 5 -cyclopentadιenyl)-1,2- ethanediyltitanium dimethyl, (ethylamιdo)(tetramethyl-η5- cyclopentadιenyl)methylenetιtanιum dimethyl, (tertbutylamιdo)dιbenzyl(tetramethyl-ηS- cyclopentadienyl) silanezirconium dibenzyl, (benzylamιdo)dιmethyl- (tetramethyl-η5- 0 cyclopentadieny silanetitanium diphenyl, (phenyiphosphιdo)dιmethyl(tetramethyl-η5- cyclopentadιenyl)sιlanezιrconιum dibenzyl Such components are readily prepared by combining the corresponding metal chloride with a dihthium salt of the substituted cyclopentadienyl group such as a cyclopentadienyl-alkanediyl, cyclopentadienyl-silane amide, or cyclopentadienyl-phosphide 5 compound The reaction is conducted in an inert liquid such as tetrahydrofuran, C 5 10 alkanes, toluene utilizing conventional synthetic procedures Additionally, the first components may be prepared by reaction of a group II derivative of the cyclopentadienyl compound in a solvent and separating the salt by-product Magnesium derivatives of the cyclopentadienyl compounds are preferred. The reaction may be conducted in an inert solvent such as cyclohexane, pentane, tetrahydrofuran, diethyl ether, benzene, toluene, or mixtures of the like. The resulting metal cyclopentadienyl halide complexes may be alkylated using a variety of techniques Generally, the metal cyclopentadienyl alkyl or aryl complexes may be prepared by alkylation of the metal cyclopentadienyl halide complexes with alkyl or aryl derivatives of group I or group II metals. Preferred alkylating agents are alkyl lithium and Grignard derivatives using conventional synthetic techniques. The reaction may be conducted in an inert solvent such as cyclohexane, pentane, tetrahydrofuran, diethyl ether, benzene, toluene, or mixtures of the like. A preferred solvent is a mixture of toluene and tetrahydrofuran. Compounds useful as a second component in the preparation of the ionic catalysts useful in this invention will comprise a cation, which is a Bronsted acid capable of donating a proton, and a compatible noncoordinating anion. Preferred anions are those containing a single coordination complex comprising a charge-bearing metal or metalloid core which anion is relatively large (bulky), capable of stabilizing the active catalyst species (the Group 3-10 or Lanthanide Series cation) which is formed when the two components are combined and sufficiently labile to be displaced by ethylenicic, diethylenicic and acetylenically unsaturated substrates or other neutral Lewis bases such as ethers, and nitrites. Suitable metals, then, include, but are not limited to, aluminum, gold, and platinum. Suitable metalloids include, but are not limited to, boron, phosphorus, and silicon. Compounds containing anions which comprise coordination complexes containing a single metal or metalloid atom are, of course, well known and many, particularly such compounds containing a single boron atom in the anion portion, are available commercially. In light of this, salts containing anions comprising a coordination complex containing a single boron atom are preferred. Highly preferably, the second component useful in the preparation of the catalysts of this invention may be represented by the following general formula: <L-H) + [A]- wherein: L is a neutral Lewis base; (L-H) + is a Bronsted acid; and [A)- is a compatible, noncoordinating anion. More preferably [A]- corresponds to the formula: [M'Q q ]- wherein: M' is a metal or metalloid selected from Groups 5- 15 of the Periodic Table of the Elements; Q independently each occurrence is selected from the Group consisting of hydride, dialkylamido, halide, alkoxide, aryloxide, hydrocarbyl, and substituted-hydrocarbyl radicals of up to 20 carbons with the proviso that in not more than one occurrence is Q halide; and q is one more than the valence of M'. Second components comprising boron which are particularly useful in the preparation of catalysts of this invention may be represented by the following general formula: [L-H] + [BQ 4 ]- wherein: L is a neutral Lewis base; [L-H] + is a Bronsted acid; B is boron in a valence state of 3; and Q is as previously defined. Illustrative, but not limiting, examples of boron compounds which may be used as a second component in the preparation of the improved catalysts of this invention are trialkyl- substituted ammonium salts such as triethylammonium tetraphenylborate, tripropyammonium tetraphenylborate, tris(n-butyl)ammonium tetraphenylborate, trimethylammonium tetrakis(p- tolyl)borate, tributylammonium tetrakis(pentafluorophenyl)borate, tripropylammonium tetrakis(2,4-dimethylphenyl)borate, tributylammonium tetrakis(3,5-dimethyphenyl)borate, and triethylammonium tetrakis(3,5-di-trifluoromethylphenyl)borate. Also suitable are N,N- dialkyl anilinium salts such as N,N-dimethyl-aniliniumtetraphenylborate, N.N-diethylanilinium tetraphenylborate, N,N-dimethyl-2,4,6-trimethylanilinium and tetraphenylborate; dialkylammonium salts such as di-(i-propyl)ammonium tetrakis(pentafluorophenyl)borate, and dicyclohexylammonium tetraphenylborate; triaryl phosphonium salts such as triphenylphosphonium tetraphenylborate, tri(ethylphenyl)phosphonium tetrakis- pentafluorophenylborate, and tri(dimethylphenyl)phosphonium tetraphenylborate. Preferred ionic catalysts formed in this manner are those having a limiting charge separated structure corresponding to Formula (IV): ( IV ) . Z Y / / Cp* M + XA * (X)n-1 wherein: M is a titanium, zirconium, or hafnium; Cp*, X, and Z are as defined for Formula (I); n is 1 , 2, 3, or 4 and is 2 less than the oxidation state of M; and XA*- is XB(C 6 F 5 ) 3 . This class of cationic complexes may be conveniently prepared by contacting a metal compound corresponding to Formula (V): ( V) z Y / / wherein: Cp*, M, and n are as previously defined for Formula (IV), with tris(pentafluorophenyl)borane cocatalyst under conditions to cause abstraction of X and formation of the anion -XB(C6F5) 3 . Preferably X in the foregoing ionic catalyst is Ci-Cio hydrocarbyl, most preferably methyl. Formula (V) is referred to as the limiting, charge separated structure. However, it is to be understood that, particularly in solid form, the catalyst may not be fully charge separated. That is, the X group may retain a partial covalent bond to the metal atom, M. Thus, the catalysts may be alternately depicted as possessing Formula (VI): n-1 The catalysts are preferably prepared by contacting the derivative of a Group 4 or Lanthanide metal with the tris(pentafluorophenyl)borane in an inert diluent such as an organic liquid. Tris(pentafluorophenyl)borane is a commonly available Lewis acid that may be readily prepared according to known techniques. The compound is disclosed in Marks, et al. J. Am. Chem. Soc. 1991 , 1 13, 3623-3625 for use in alkyl abstraction of zirconocenes. All reference to the Periodic Table of the Elements herein shall refer to the Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 1989. Also, any reference to a Group or Groups shall be to the Group or Groups as reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. Other compounds which are useful in the catalyst compositions of this invention, especially compounds containing other Group 4 or Lanthanide metals, will, of course, be apparent to those skilled in the art. The polymerization conditions for manufacturing the polymers of the present invention are generally those useful in the solution polymerization process, although the application of the present invention is not limited thereto. Slurry and gas phase polymerization processes are also believed to be useful, provided the proper catalysts and polymerization conditions are employed. Multiple reactor polymerization processes are also useful in the present invention, such as those disclosed in U.S. Patent No. 3,914,342. The multiple reactors can be operated in series or in parallel, with at least one constrained geometry catalyst employed in at least one of the reactors. o In general, the continuous polymerization according to the present invention may be accomplished at conditions well known in the prior art for Ziegler-Natta or Kaminsky- Sinn type polymerization reactions, that is, temperatures from 0°C to 250°C and pressures from atmospheric to 1000 atmospheres ( 100 MPa). Suspension, solution, slurry, gas phase or other process conditions may be employed if desired. A support may be employed but preferably the 5 catalysts are used in a homogeneous (that is, soluble manner. It will, of course, be appreciated that the active catalyst system, form in situ if the catalyst and the cocatalyst components thereof are added directly to the polymerization process and a suitable solvent or diluent, including condensed monomer, is used in said polymerization process. It is, however, preferred to form the active catalyst in a separate step in a suitable solvent prior to adding the same to o the polymerization mixture. The present foam structure may take any physical configuration known in the art, such as sheet, plank, or bun stock. Other useful forms are expandable or foamable particles, moldable foam particles, or beads, and articles formed by expansion and/or coalescing and welding of those particles. 5 Excellent teachings to processes for making ethylenic polymer foam structures and processing them are seen in CP. Park, "Polyolefin Foam", Chapter 9, Handbook of Polymer Foams and Technology, edited by D. Klempner and K.C. Frisch, Hanser Publishers, Munich, Vienna, New York, Barcelona (1991 ). The present foam structure may be prepared by blending and heating an 0 ethylenic polymer material and a decomposable chemical blowing agent to form a foamable plasticized or melt polymer material, extruding the foamable melt polymer material through a die, inducing cross-linking in the melt polymer material, and exposing the melt polymer material to an elevated temperature to release the blowing agent to form the foam structure. The polymer material and the chemical blowing agent may be mixed and melt blended by any 5 means known in the art such as with an extruder, mixer, or blender. The chemical blowing agent is preferably dry-blended with the polymer material prior to heating the polymer material to a melt form, but may also be added when the polymer material is in melt phase. Cross-linking may be induced by addition of a cross-linking agent or by radiation. Induction of cross-linking and exposure to an elevated temperature to effect foaming or expansion may occur simultaneously or sequentially If a cross-linking agent is used, it is incorporated into the polymer material in the same manner as the chemical blowing agent Further, if a cross-linking agent is used, the foamable melt polymer material is heated or exposed to a temperature of preferably less than 150°C to prevent decomposition of the cross-linking agent or the blowing agent and to prevent premature cross-linking If radiation cross-linking is used, the foamable melt polymer material is heated or exposed to a temperature of preferably less than 160°C to prevent decomposition of the blowing agent The foamable melt polymer material is extruded or conveyed through a die of desired shape to form a foamable structure The foamable o structure is then cross-linked and expanded at an elevated or high temperature (typically, 150°C-250°C) such as in an oven to form a foam structure If radiation cross-linking is used, the foamable structure is irradiated to cross-link the polymer material, which is then expanded at the elevated temperature as described above The present structure can advantageously be made in sheet or thin plank form according to the above process using either cross-linking 5 agents or radiation The present foam structure may also be made into a continuous plank structure by an extrusion process utilizing a long-land die as described in GB 2, 145,961 A In that process, the polymer, decomposable blowing agent and cross-linking agent are mixed in an extruder, heating the mixture to let the polymer cross-link and the blowing agent to decompose in a 0 long-land die; and shaping and conducting away from the foam structure through the die with the foam structure and the die contact lubricated by a proper lubrication material The present foam structure may also be formed into cross-linked foam beads suitable for molding into articles To make the foam beads, discrete resin particles such as granulated resin pellets are suspended in a liquid medium in which they are substantially 5 insoluble such as water; impregnated with a cross-linking agent and a blowing agent at an elevated pressure and temperature in an autoclave or other pressure vessel; and rapidly discharged into the atmosphere or a region of reduced pressure to expand to orm the foam beads A version is that the polymer beads is impregnated with blowing agent, cooled down, discharged from the vessel, and then expanded by heating or with steam In a derivative of the 0 above process, styrene monomer may be impregnated into the suspended pellets along with the cross-linking agent to form a graft interpolymer with the ethylenic polymer material Blowing agent may be impregnated into the resin pellets while in suspension or, alternately, in non-hydrous state The expandable beads are then expanded by heating with steam and molded by the conventional molding method for the expandable polystyrene foam beads The foam beads may then be molded by any means known in the art, such as charging the foam beads to the mold, compressing the mold to compress the beads, and heating the beads such as with steam to effect coalescing and welding of the beads to form the article Optionally, the beads may be pre-heated with air or other blowing agent prior to charging to the mold Excellent teachings of the above processes and molding methods are seen in C P Park, above publication, pp 227-233, U S Patent No 3,886, 100, U S Patent No 3,959, 189, U S Patent No 4, 168,353, and U S Patent No 4,429,059 The foam beads can also be prepared by preparing a mixture of polymer, cross-linking agent, and decomposable mixtures in a suitable mixing device or extruder and form the mixture into pellets, and heat the pellets to cross-link and expand There is another process for making cross-linked foam beads suitable for molding into articles The ethylene polymer material is melted and mixed with a physical blowing agent in a conventional foam extrusion apparatus to form an essentially continuous foam strand The o foam strand is granulated or pelletized to form foam beads The foam beads are then cross- linked by radiation The cross-linked foam beads may then be coalesced and molded to form various articles as described above for the other foam bead process Additional teachings to this process are seen in U S Patent No 3,616,365 and C P Park, above publication, pp 224-228 The present foam structure may be made in bun stock form by two different 5 processes One process involves the use of a cross-linking agent and the other uses radiation The present foam structure may be made in bun stock form by mixing the ethylenic polymer material, a cross-linking agent, and a chemical blowing agent to form a slab, heat the mixture in a mold so the cross-linking agent can cross-link the polymer material and the blowing agent can decompose, and expand by release of pressure in the mold Optionally, 0 the bun stock formed upon release of pressure may be re-heated to effect further expansion Cross-linked polymer sheet is made by either irradiating polymer sheet with high energy beam or by heating a polymer sheet containing chemical cross-linking agent The cross- linked polymer sheet is cut into the desired shapes and impregnated with nitrogen in a higher pressure at a temperature above the softening point of the polymer, releasing the pressure 5 effects nucleation of bubbles and some expansion in the sheet The sheet is re-heated at a lower pressure above the softening point, and the pressure is then released to allow foam expansion Blowing agents useful in making the present foam structure include decomposable chemical blowing agents Such chemical blowing agents decompose at elevated 0 temperatures to form gases or vapors to blow the polymer into foam form The agent preferably takes a solid form so it may be easily dry-blended with the polymer material Chemical blowing agents include azodicarbonamide, azodiisobutyro-nitnle, benzenesulfonhydrazide, 4,4-oxybenzene sulfonyl-semicarbazide, p-toluene sulfonyl semi- carbazide, barium azodicarboxylate, N,N'-dιmethyl-N,N'-dιnιtrosoterephthalamιde, N,N'- 5 dinitrosopentamethylenetetramine, 4-4-oxybιs (benzenesulfonylhydrazide), and tnhydrazino tπazine Azodicarbonamide is preferred Additional teachings to chemical blowing agents are seen in C P Park, above publication, pp 205-208, and F A Shutov, "Polyolefm Foam", Handbook of Polymer Foams and Technology, pp. 382-402, D. Klemper and K.C. Frisch, Hanser Publishers, Munich, Vienna. New York, Barcelona ( 1991 ). The chemical blowing agent is blended with the polymer material in an amount sufficient to evolve 0.2 to 5.0, preferably from 0.5 to 3.0, and most preferably from 1.0 to 2.50 moles of gas or vapor per kilogram of polymer. Cross-linking agents useful in making the present foam structure are the organic peroxides. Useful organic peroxides corss-linking agents include 1 , 1-di-t-butyl peroxy-3,3,5- trimethylcyclohexane, dicumyl peroxide, 2,5-dimethyl-2,5-di(t-buyl peroxy) hexane, t-butyl- cumyl peroxide, α,α'-di(butyl peroxy)-diisopropyl benzene, di-t-butyl peroxide, and 2,5- dimethyl-2,5-di-(t-butyl peroxy) hexyne. Dicumyl peroxide is the preferred agent. Additional teachings to organic peroxide cross-linking agents are seen in CP. Park, above publication, pp. 198-204. Cross-linking by radiation may be effected by any of the conventional types. Useful radiation types include an electron beam or beta ray, gama rays, x-rays, or nuetron rays. Radiation is believed to effect cross-linking by generating polymer radicals, which may combine and cross-link. Additional teachings concerning radiation cross-linking are seen in CP. Park, above publication, pp. 198-204. In some processes for making the present structure, a physical blowing agent may be used. Physical blowing agents include organic and inorganic agents. Suitable inorganic blowing agents include carbon dioxide, nitrogen, argon, water, air, nitrogen, and helium. Organic blowing agents include aliphatic hydrocarbons having 1-9 carbon atoms, aliphatic alcohols having 1-3 carbon atoms, and fully and partially halogenated aliphatic hydrocarbons having 1 -4 carbon atoms. Aliphatic hydrocarbons include methane, ethane, propane, n- butane, isobutane, n-pentane, isopentane, and neopentane. Aliphatic alcohols include methanol, ethanol, n-propanol, and isopropanol. Fully and partially halogenated aliphatic hydrocarbons include fluorocarbons, chlorocarbons, and chlorofluorocarbons. Examples of fluorocarbons include methyl fluoride, perfluoromethane, ethyl fluoride, 1 , 1 -difluoroethane (HFC-152a), 1 , 1 , 1-trifluoroethane (HFC-143a), 1 , 1 , 1 ,2-tetrafluoro-ethane (HFC- 134a), pentafluoroethane, difluoromethane, perfluoroethane, 2,2-difluoropropane, 1 , 1 , 1 - trifluoropropane, perfluoropropane, dichloropropane, difluoropropane, perfluorobutane, perfluorocyclobutane. Partially halogenated chlorocarbons and chlorofluorocarbons for use in this invention include methyl chloride, methylene chloride, ethyl chloride, 1 , 1 , 1 - trichloroethane, 1 , 1-dichloro-1-fluoroethane (HCFC- 141 b), 1 -chloro- 1 , 1 -difluoroethane (HCFC- 142b), chlorodifluoromethane (HCFC-22), 1 , 1 -dichloro-2,2,2-trifluoroethane (HCFC-123) and 1-chloro- 1 ,2,2,2-tetrafluoroethane (HCFC-124). Fully halogenated chlorofluorocarbons include trichloromonofluoromethane (CFC- 1 1 ), dichlorodifluoromethane (CFC-12), trichlorotrif luoroethane (CFC-1 13), 1 , 1 , 1 -trif luoroethane, pentafluoroethane, dichlorotetrafluoroethane (CFC- 1 14), chloroheptafluoropropane, and dichlorohexafluoropropane. The amount of blowing agent incorporated into the polymer melt material to make a foam-forming polymer gel is from 0.2 to 5.0, preferably from 0.5 to 3.0, and most preferably from 1.0 to 2.50 moles per kilogram of polymer. The present foam structure has a cross-linked density of from 5 to 90 percent and more preferably from 30 to 70 percent percent according to ASTM D-2765-84, method A. The present foam structure has density of less than 500, more preferably less than 250 and most preferably from 10 to 150 kilograms per cubic meter. The foam has an average cell size of from 0.05 to 5.0, more preferably from 0.1 to 2.0, and most preferably 0.2 to 1.0 millimeters according to ASTM D3576. The present foam structure may be closed cell or open cell. Preferably, the present foam is greater than 90 percent closed-cell according to ASTM D2856-A. Various additives may be incorporated in the present foam structure such as inorganic fillers, stability control agents, nucleating agents, pigments, antioxidants, acid scavengers, ultraviolet absorbers, flame retardants, processing aids, and extrusion aids. The following are examples of the present invention, and are not to be construed as limiting. Unless otherwise indicated, all percentages, parts, or proportions are by weight. Example 1 Cross-linked ethylenic polymer foam structures of the present invention are made according to the process set forth below. A substantially linear ethylenic polymer prepared with a constrained geometry catalyst (CGCT resin) is cross-linked with dicumyl peroxide (DCP), and expanded with azodicarbonamide to form the foam structures. The CGCT resin, DCP, and azodicarbonamide were processed in a Model System 90 Torque Rheometer mixing bowl (Haake Buchler Instruments, Inc.). The CGCT resin was an ethyl ene/octene copolymer 76/24 (measured by infrared technique of ASTM 2238, method B) having a density of 0.873 g/cc, melt index (l 2 ) of 5.2 dg/min, and o/l 2 of 10.4. Forty grams of the granular resin is mixed, under nitrogen blanket, with 6 grams of azodicarbonamide in the Haake mixer maintained at 140°C and 20 rpm motor speed for 5 minutes. Subsequently, predetermined amounts of DCP were added and mixed for an additional 5 minutes. The foamable mixture was pressed into sheet of approximately 0.080 inch (2 millimeters (mm)) in thickness on a hot press at 150°C. The sheet was cut to approximately 1/2 inch X 1/2 inch (1.3 centimeters X 1.3 centimeters) size specimens. The foamable specimens were then expanded in a hot air oven maintained at 230°C for various lengths of time to determine the optimum expansion time. As shown in Table 1 , the resin provided reasonably low density foams having small cell size at a relatively wide range of DCP level and oven exposure time. Foams having densities as low as 4.8 pounds per cubic foot (pcf) (77 kg/m3) was achieved at 0 8 DCP level The foam was very flexible, tough and resilient TABLE 1 DCP Expansion Foam Foam Cell Test No Level' Time- Density^ Density Size 5 1.1 0.5 180 24 6 423 ND 1 2 0.5 220 23 1 370 ND 1 3 0.7 180 18 5 296 ND 1 4 0.7 190 5 7 90 ND 1.5 0.7 200 14.5 232 ND 1.6 0.8 190 5.3 85 0.35 1.7 0.8 230 4.8 77 0.30 1.8 0.9 150 7 4 119 ND 1 9 0.9 180 7.8 125 ND 1.10 1.0 180 8 00 128 ND 1.1 1 1.0 190 37 4 599 ND 1 Parts of dicumyl peroxide mixed in per one hundred parts of polymer 2 Time specimen allowed to expand in the oven in seconds 3 Density of foam body in pounds per cubic foot 4 Density of foam body in kilograms per cubic meter 5 Cell size in millimeters determined per ASTM D3576, ND = not determined Example 2 Cross-linked ethylenic polymer foam structures of the present invention were made substantially according to the process of Example 1 except a different CGCT resin was used The CGCT resin had a density of 0.888 g/cc, a melt index of 3 0, and a o/l 2 of 7.9 As shown in Table 2, good quality foam structures of relatively low density were obtained The minimum density obtained was 6 1 pcf (98 kg/m 3 ) in Test 2 9, which was somewhat higher than the minimum obtained in Example 1 (Test 1 7) The cell size of the foam structure in Test 2.9 was 0.39 mm The foam structures of Example 1 , which utilized a higher l 10 /l 2 resin than those of Example 2, were more desirable than those of Example 2 because of their lower density The higher l 10 /l 2 resin provides a higher melt elasticity, which is apparently beneficial for foam expansion TABLE 2 i Parts of dicumyl peroxide mixed in per one hundred parts of polymer 2 Time specimen allowed to expand in the oven in seconds 3 Density of foam body in pounds per cubic foot 4 Density of foam body in kilograms per cubic meter Example 3 Cross-linked ethylenic polymer foam structures of the present invention were made substantially in accordance with Example 1 except a resin blend was employed The resins employed were blends of a CGCT LLDPE resin and a conventional LDPE resin The resin blend was a 50/50 blend by weight of the CG3 resin having a density of 0 92, a melt index of 1 1 , an 0i 7 2 and a conventional LDPE resin having 0 916 g/cc density and 5 5 melt index A good quality foam of 4 1 pcf (66 kg/m 3 ) and 0 41 mm cell size was achieved at a DCP level of 0 4 pph The results demonstrated that a low melt index CGCT resin could be used with an LDPE resin to make a low density foam Example 4 A cross-linked ethylenic polymer foam structure of the present invention was made substantially in accordance with Example 1 with the same CGCT resin The DCP level and expansion time were 0 8 pph and 230 seconds, respectively The resulting foam structure had a reasonably low density ot 4.2 pcf (67.2 kgm) and a reasonably small cell size of 0.8 mm. The foam structure exhibited desirable strength and toughness characteristics. The structure had a compressive strength at 25 percent (ASTM D-3575B) of 2.8 psi (pounds per square inch), a compressive set at 50 percent deflection (ASTM D-3575A) of 18 percent, a tensile strength (t.s.) (ASTM D-3575E) of 92 psi (630 kPa), and a tensile elongation (t.e.) (ASTM D- 3575E) of 394 percent. Toughness may be calculated according to (t.s.)x(t.e.)/(2)(100) to yield a desirably high value of 362 psi (2500 kPa). While embodiments of the foam structure and the process for making it of the o present invention have been shown with regard to specific details, it will be appreciated that depending upon the manufacturing process and the manufacturer's desires, the present invention may be modified by various changes while still being fairly within the scope of the novel teachings and principles herein set forth. 5 0 5 0 5

Claims: I A process for making a cross-linked ethylenic polymer foam structure, comprising a) forming a foamable melt polymer material by blending and heating a decomposable chemical blowing agent and an ethylenic polymer material containing a substantially linear ethylenic polymer, b) inducing cross-linking in the foamable melt polymer material; and c) expanding the foamable melt polymer material by exposing it to an elevated temperature to form the foam structure; the process being characterized in that the substantially linear ethylenic polymer has in an un-crosshnked state: i) a melt flow ratio, lιo/l 2 , ≥ 5 63, ii) a molecular weight distribution, M w /M n , defined by the equation: M w /M n ≤ (I 10 /l2) - 4 63; and iii) a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear ethylenic polymer having about the same l 2 and M w /M n 2. The process of Claim 1 , wherein the cross-linking is induced by radiation 3. The process of Claim 1 , wherein the cross-linking is induced by a cross-linking agent 4 The foam structure of Claim 1, wherein the M w /M n is from 1.5 to 2.5 5 The foam structure of Claim 1 , wherein the substantially linear ethylenic polymer having from 0.01 to 3 long chain branches/1000 carbons along the polymer backbone 6 The foam structure of Claim 5, having 0 01 to 1 long chain branches/1000 carbons along the polymer backbone 7 The foam structure of Claim 5, having 0 05 to 1 long chain branches/1000 carbons along the polymer backbone 8 The foam structure of Claim 1 , wherein the substantially linear ethylenic polymer is an ethylene/alpha-olefinic copolymer 9 The foam structure of Claim 8, wherein the substantially linear ethylenic polymer is a copolymer of ethylene monomer and a comonomer selected from the group consisting of 1-octene, 1-butene, 1 -hexene, and 4-methyl-1-pentene 10 The foam structure of Claim 1 , wherein the 1 κ> '2 is 8 or more I I The foam structure of Claim 1 , wherein the lιo/l 2 is 9 or more 12 The foam structure of Claim 1. wherein the rheological processing index is less than or equal to 70 percent of that of a linear ethylenic polymer which lacks long-chain branching at about the same l 2 and M w /M n 13 The foam structure of Claim 1 , wherein the ethylene polymer material further contains a polymer selected from the group consisting of a low density polyethylene, linear low density polyethylene, and ethylene/acryhc acid copolymer

Inventors: CHUM PAK-WING STEVE, KNIGHT GEORGE W, PARK CHUNG P, CHUM, PAK-WING, STEVE, KNIGHT, GEORGE, W., PARK, CHUNG, P.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1994
Main classification: C08J9
IPC codes: C08J9