OPTICAL AMPLIFIER AND LASER

Abstract: A laser has a resonant cavity defined by a pair of mirros (3, 5) butted to respective ends of a fluorozirconate optical fibre (1). The fibre (1) has a numerical aperture of 0.205 and an LP11 mode cut-off of about 2. 0 mu m. The fibre (1) is co-doped with thulium ions to a concentration of about 0.1%, and with terbium ions to a concentration of about 1 %. An optical pump source (6) provides a pump signal at 775 nm which excites the thulium ions into the <1>G4, energy level to provide lasing at about 475 nm. The pump source is preferably a high power semiconductor laser (16).

Description: OPTICAL AMPLIFIER AND LASER This invention relates to an optical amplifier, and in particular to a laser incorporating an optical amplifier. The impact that an efficient, inexpensive and reliable visible laser source would have on data storage, display technology, undersea communications and optical processing has provided the stimulus for much recent work on solid state visible lasers. One approach that has yielded much success is the use of upconversion processes within rare earth doped materials to produce laser emission at a wavelength significantly shorter than the pump wavelength. For example, there has been a recent demonstration of visible lasing at 3+ 480nm in Tm - doped fluoride fibre (see Allain, J. Y. , Monerie, M and Poignant, H. : ' Blue upconversion fluorozirconate fibre laser' , Electron. Lett. , 1990, 26 (3), pp. 166-168), and a demonstration of room temperature lasing at red, green and blue wavelengths in praseodymium doped fluorozirconate glass fibre (see Smart, R. G. , Hanna, D. C. , Tropper, A. C. , Davey, S. T. , Carter, S. F. , Szebesta, D, : ' CW upconversion lasing at blue, green and red wavelengths in an 3+ infrared-pumped Pr -doped fluoride fibre at room temperature' , Electron. Lett., 1991, 27, (14), pp 1307-1309). Forced oscillation on two transitions simultaneously has also been demonstrated (see Percival, R. M. , Szebesta, D. , and Davey, S. T. : "Highly efficient and tunable operation of two colour Tm-doped fluoride fibre laser" Electron. Lett. , 1992, 28, (7), pp. 671-672). These demonstrations have dramatically changed the viability of such upconversion pumped laser schemes, and recently a significant amount of time has been spent investigating the infrared emission which emanates from the 3 F 4 manifold in fluoride fibres doped with thulium. During the course of this work, it has become common knowledge that, when pumped at around 790nm, the fibres glow in the blue region of the electromagnetic spectrum. One explanation for this effect, is that a first pump photon results in population being excited into the 3 F 4 manifold (see Figure 1 which is an energy level diagram of a thulium/terbium co- doped fluoride fibre). From this level, there are three routes for radiative decay, 0.805μm ( 3 F 4 - 3 H 6 ), 1.475μm ( 3 F 4 - 3 H 4 ), and 2.310μm ( 3 F 4 - 3 H 5 ) with branching ratios of 0.893, 0.083 and 0.024 respectively. The energy gap to the next level is sufficiently large that non-radiative decay is precluded. Thus, besides the ground state ( 3 H 6 ) and the 3 F 4 manifold, there will be small populations in the 3 H 4 and 3 H 5 manifolds when under excitation. Moreover, the energy gap between the 3 H 5 and G 4 manifolds is quite closely matched to the pump photon energy. Consequently, the sequential absorption of two pump photons could lead to a small fraction of the population excited into the 3 H 5 manifold reaching a high enough level G- ) to give rise to a small amount of blue emission when the excited ion subsequently decays back down to the ground state manifold . The 1992 Electronics Letter paper referred to above observed that the blue emission intensity increased significantly when stimulated emission was obtained on the 2.31μm transition, since the population in the 3 H 5 manifold rapidly increased under these circumstances. However, this scheme is thought to be unworkable as a blue laser, since the fibre parameters for operation at mid-infrared and blue wavelengths are widely divergent. The applicants believe that significant gain at 475nm can be achieved when thulium/terbium co-doped fluorozirconate fibre is pumped at 775nm. The 475nm emission observed originates from the 1 G 4 level, and requires the sequential absorption of 775nm pump photons. The present invention is based on the observation by the applicants that there is blue fluorescence which is ascribed to a transition between the G 4 level and the 3 H 6 ground state of the system Fig. 1 represents the energy levels of the thulium and terbium ions, with the relevant blue lasing transition indicated between the 'G 4 level and the 3 H 6 ground state. The upper laser level may be populated by the sequential absorption of 775nm pump photons in a process which involves excitation of ground state ions into the 3 F 4 band, some of which then branch into the 3 H 5 level. These ions are then further excited by pump photons into the ! G 4 level. A direct transition from this level to the ground state is responsible for the blue emission. The present invention is based on an optical amplifier comprising a fluorozirconate waveguide co-doped with thulium and terbium ions, and an optical pump means coupled to the waveguide for providing an optical pump signal capable of exciting the thulium ions into the G 4 energy level, whereby the amplifier provides optical gain at about 475nm, said optical pump means being adopted to provide an optical pump signal having a wavelength in the range of 770nm to 790nm, preferably about 775nm. The waveguide may conveniently comprise a fluorozirconate optical fibre waveguide such as a standard 2BLAN fluorozirconate fibre, but other types of waveguide may be employed. For example, it is expected that a useful configuration would be a planar waveguide structure formed by doping a fluorozirconate glass substrate. High dopant concentration would lead to compact (short waveguide length) devices. The pump, preferably a semiconductor laser diode, may be coupled to the fibre by any known appropriate technique. For example, the high numerical aperture fluorozirconate fibre may be jointed to a silica fibre so that readily- available fused couplers, for example, can be used to couple pump and signal sources to the doped fibre. Advantageously, the fluorozirconate waveguide is doped with thulium ions to a concentration of about 0.1%, and with terbium ions to a concentration of about 1%. The thulium ions are excited into the ! G 4 level by sequential absorption of two pump photons. The first pump photon is absorbed by a thulium ion to excite that ion from the ground state ( 3 H 6 ) to the level 3 F 4 . The excited ions thereafter decay into the 3 H 5 level and this decay is assisted by energy transfer to the terbium ions. After decay, the second pump photon is absorbed by the thulium ion to exc that ion to the 1 G 4 level. The invention also provides a laser comprising optical amplifier and a pair of reflectors, the opti amplifier being as defined above, and the reflectors be positioned one at each end of the waveguide, the reflect defining a resonant cavity and having reflectivities such to provide lasing action at about 475nm when the waveguide pumped by the pumping means. The reflectors, which may be mirrors or ot reflectors such as Sagnac loop reflectors, define a Fab Perot cavity, and in known manner are selected to prov reflections sufficient to sustain lasing only at the desi wavelength. The invention also provides for the amplification attenuated optical signals at about 475nm. This requires optical amplifier as described above which is provided wi an input port for accepting attenuated signals at s wavelengths and an output port for providing said sign after amplification. For amplification of attenua signals, it is necessary to minimise , ideally to elimina reflections and feedback of the amplified signal beca reflections tend to cause self sustaining generation of li and this constitutes an unacceptable noise. The invention also includes a method of amplifyi optical signal which method comprises providing p radiation at wavelengths in the range 770nm to 790nm int fluorozirconate waveguide co-doped with thulium and terbi ions whereby said pump radiation produces a populati inversion in the terbium ions said population inversion bei capable of amplifying radiation having a wavelength of abo 475nm. The invention will now be described in greater detai by way of example, with reference to the accompanyi drawings, in which: Figure 1 is a diagram showing the energy levels thulium and terbium ions in a ZBLAN host; Figure 2 is a graph of the intensity against wavelength for blue emission from the J G 4 manifold; Figure 3 is a schematic diagram of a first form of laser constructed in accordance with the invention; and Figure 4 is a schematic diagram of a second form of laser constructed in accordance with the invention. Referring to Figure 1, lasing at a wavelength of 475nm is achieved by establishing a population inversion between the 'G 4 upper level and the 3 H 6 ground state. Pump light at a wavelength of about 775nm is used to excite ions into the 3 F 4 level. As mentioned above, a proportion of these excited ions decay into the 3 H 5 level, from where excitation to " the G 4 level is possible by absorption of pump light. In order to increase the probability of this second excitation of pump energy, the applicants have found that there should be several terbium ions close to every thulium ion, so that cross-relaxation of population from the 3 H 4 manifold in thulium over to the 7 F 0 manifold in terbium is enhanced, thus preventing population build up in the 3 H 4 manifold. However, a second cross-relaxation mechanism also operates, this arising as result of the of a close energy match between the 2.26μm ground state absorption transition ( 7 F 6 - 7 F 3 ) in terbium and the 2.31μm emission transition ( 3 F 4 - 3 H 5 ) in thulium (see Figure 1). Due to this coincidence, the lifetime of the 3 F 4 manifold is reduced from around 1.5ms to around 0.5ms, that is to say about two thirds of the population excited to the 3 F 4 manifold now decays non- radiatively into the 3 H 5 manifold. Thus, there is much greater probability that a second pump photon will be excited up to the *G 4 manifold, leading to much larger amounts of spontaneous blue emission. Figure 2 shows a plot of the variation in observed blue fluorescence intensity with wavelength. Referring to Figure 3, a first form of laser according to the present invention is based on a length of standard formulation ZBLAN fluorozirconate fibre 1 co-doped with thulium (0.1%) and terbium (1%) ions (ZBLAN denotes fluorides of Zr, Ba, La, Al and Na). The fibre 1 has a numeric aperture of 0.205, a mode cut-off of about 2. Oμm, and a co diameter of 7.5μm. The fibre background loss at both pu and signal wavelengths is estimated to be around 1.2dB/m. simple Fabry-Perot laser cavity is formed by butting an inp end 2 of the fibre 1 against a dielectric mirror 3, and butting an output end 4 of the fibre against a dielectri mirror 5, the mirrors being highly reflecting (HR ≥ 99.5%) between 460nm and 490nm, and highly transmitting (HT ≥ 80 at between 760nm and 800nm. 775nm pump light is derived fr a laser 6 which is end-fire launched through the input mirr 3. A pump blocking filter 7 is used to separate the remna pump and blue emission after transmission through the outp mirror 5. The level of reflectivity of the output mirror can be reduced so that greater amounts of power are availabl for use. Figure 4 shows a second form of laser according to t invention. This laser is tunable, and is a modified versio of the laser of Figure 3. Accordingly, like referenc numerals will be used for like parts, and only th modifications will be described in detail. Thus, the cavit of the laser of Figure 4 is provided with a cover slide 8 t prevent reflections, a microscope objective 9 to collimat the laser output, and a three-plate birefrigent filter 10 t provide wavelength selection within the cavity.

Claims: - 1 - CLAI MS 1. An optical amplifier comprising a fluorozirconate waveguide co-doped with thulium and terbium ions, and an optical pump means coupled to the waveguide for providing an optical pump signal capable of exciting the thulium ions into the l G. energy level, whereby the amplifier provides optical gain at about 475nm, said optical pump means being adapted to provide an optical pump signal having a wavelength in the range of 770nm to 790nm. 2. An amplifier as claimed in claim 1, wherein the optical pump signal has a wavelength of about 775nm. 3. An amplifier as claimed in claim 1 or claim 2, wherein the waveguide is in the form of a fibre. 4. An amplifier as claimed in any one of claims 1 to 3, wherein the fluorozirconate waveguide is doped with thulium ions to a concentration of about 0.1%, and with terbium ions to a concentration of about 1%. 5. An amplifier as claimed in any one of claims 1 to 4, wherein the optical pump means is a semiconductor laser diode. 6. A laser comprising an optical amplifier and a pair of reflectors, the optical amplifier being as claimed in any one of claims 1 to 5, and the reflectors being positioned one at each end of the waveguide, the reflectors defining a resonant cavity and having reflectivities such as to provide lasing action at about 475nm when the waveguide fibre is pumped by the pumping means. 7. A laser as claimed in claim 6, wherein the reflectors are mirrors. 8. A method of amplifying optical signals which metho comprises providing pump radiation having a wavelength withi the range of 770nm to 790nm into a fluorozirconate waveguid co-doped with thulium and terbium ions whereby said pum radiation produces a population inversion in the thuliu ions, said population inversion supporting amplification a about 475nm. 9. A method as claimed claim 8, wherein the thulium ions are excited from the ground state ( 3 H 6 ) into the ! G 4 level b sequential absorption of two pump photons, said absorptio producing a population inversion between said G 4 level an the ground date. 10. A method as claimed in claim 9, wherein the first pum photon is absorbed by a thulium ion to excite that ion fro the ground state ( 3 H 6 ) to the level 3 F 4 , said excited io decays to the 3 H 5 level by energy transfer to the terbiu ions, and the second pump photon is absorbed by a thulium io that has decayed to the 3 H 5 level to excite that ion to the ! G 4 level.

Inventors: DAVEY STEVEN TERRENCE, PERCIVAL ROBERT MICHAEL, SZEBESTA DARYL, DAVEY, STEVEN, TERRENCE, PERCIVAL, ROBERT, MICHAEL, SZEBESTA, DARYL
Applicants: BRITISH TELECOMM, DAVEY STEVEN TERRENCE, PERCIVAL ROBERT MICHAEL, SZEBESTA DARYL, BRITISH TELECOMMUNICATIONS PUBLIC LIMITED COMPANY, DAVEY, STEVEN, TERRENCE, PERCIVAL, ROBERT, MICHAEL, SZEBESTA, DARYL
Application year: 1994
Main classification: H01S3
IPC codes: G02F1, H01S3