FERROELECTRIC LIQUID CRYSTAL DEVICES

Abstract: Ferroelectric liquid crystal devices are described which contain liquid crystal mixtures comprising components A and B. Component A consists of one or more optically active compounds capable of imparting a spontaneous polarisation to the material. Component B is selected as one or more compounds having formula (I), wherein a, b and c are independently 0, 1, 2; R1 and R2 are C1-15 straight or branched chain alkyl or alkoxy, preferably C3-C12. In the above (for component B) CH=CH linking groups may be replaced by C2H4 and CH2O linking groups may be replaced by OCH2.

Description: FERROELECTRIC LIQUID CRYSTAL DEVICES This invention relates to ferroelectric liquid crystal devices and ferroelectric liquid crystal mixtures. Liquid crystal devices commonly comprise a thin layer of a liquid crystal material contained between two glass slides. Optically transparent electrodes are formed on the inner surface of both slides . When an electric voltage is applied to these electrodes the resulting electric field changes the molecular alignment of the liquid crystal molecules. The changes in molecular alignment are readily observable and form the basis for many types of liquid crystal device. In ferroelectric liquid crystal devices the molecules switch between different alignment directions depending on the polarity of an applied electric field. These devices often exhibit bistability where the molecules tend to remain in one of two states until switched to the other switched state. This allows the multiplex addressing of quite large and complex devices. One common multiplex display has display elements, ie pixels, arranged in an x, y matrix format for the display of eg, alpha numeric characters. The matrix format is provided by forming the electrodes on one slide as a series of column electrodes, and the electrodes on the other slide as a series of row electrodes. The intersections between each column and row form addressable elements or pixels. Other matrix layouts are known, eg seven bar numeric displays. There are many different multiplex addressing schemes. A common feature involves the application of a voltage, called a strobe voltage to each row or line in sequence. Coincidentally with the strobe applied at each row, appropriate voltages, called data voltages, are applied to all column electrodes. The differences between the different schemes lies in the shape of the strobe and data voltage waveforms. Other addressing schemes are described in GB-2,146,473-A; GB-2,173,336-A; GB-2.173.337-A: GB-2.173.629-A; WO 89/05025; Harada et al 1 85 S.I.D. Paper 8.4 pp 131-134; Lagerwall et al 198 I.D.R.C pp 213-221 and P Maltese et al in Proc 1988 IDRC p 90-101 Fast Addressing for Ferro Electric LC Display Panels. The material may be switched between its two states by two strobe pulses of opposite sign, in conjunction with a data waveform. Alternatively, a blanking pulse may be used to switch the material into one of its states. Periodically the sign of the blanking and the strobe pulses may be alternated to maintain a net d.c. value. These blanking pulses are normally greater in amplitude and length of application than the strobe pulses so that the material switches irrespective of which of the two data waveforms is applied to any one intersection. Blanking pulses may be applied on a line by line basis ahead of the strobe, or the whole display may be blanked at one time, or a group of lines may be simultaneously blanked. It is well known in the field of ferroelectric liquid crystal device technology that in order to achieve the highest performance from devices, it is important to use mixtures of compounds which give materials possessing the most suitable ferroelectric smectic characteristics for particular types of device. Devices can be assessed for speed by consideration of the response time vs pulse voltage curve. This relationship may show a minimum in the switching time (t-,- n ) -t a particular applied voltage (V ). At voltages higher or lower than Vmi.n the switching° time is long°er than tnu.n . It is well understood that devices having such a minimum in their response time vs voltage curve can be multiplex driven at high duty ratio with higher contrast than other ferroelectric liquid crystal devices. It is preferred that the said minimum in the response time vs voltage curve should occur at low applied voltage and at short pulse length respectively to allow the device to be driven using a low voltage source and fast frame address refresh rate. Typical known materials (where materials are a mixture of compounds having suitable liquid crystal characteristics) which do not allow such a minimum when included in a ferroelectric device include the commercially available materials known as SCE13 and ZLI-3654 (both supplied by Merck UK Ltd, Poole, Dorset) . A device which does show such a minimum may be constructed according to PCT GB 88/01004 and utilising materials such as eg commercially available SCEδ (Merck UK Ltd.). Other examples of prior art materials are exemplified by PCT/GB/86/00040, PCT/GBδ7/Oθ44l and UK 2232416B. It is the aim of this invention to provide devices having a shorter switching time and/or a lower voltage than previously achieved. According to this invention a ferroelectric liquid crystal device (eg multiplex addressed) comprises two spaced cell walls each bearing electrode structures and treated on at least one facing surface with an alignment layer, a layer of a smectic liquid crystal material enclosed between the cell walls, a minimum in its response time versus voltage curve, characterised in that the liquid crystal material consists of two components; A and B, where the two components are given by: Component A being present in the range of 0.1-50 wt % and is one or more optically active compounds capable of imparting a spontaneous polarisation to the material. Component B is present m the range sufficient to enable A+B = 100 wt/., and is at least two compounds selected from: R. ■ <-C H >- -CCHH==CCHH--( 0 >-< 0 >-R, wherein a, b and c are independently 0, 1, 2; R l and R 2 are C χ _ 15 straight or branched chain alkyl or alkoxy, preferably C-C,.,. χ n the above (for Component B) CH=CH linking groups may be replaced by C 2 H ή and CH 2 0 linking groups may be replaced by 0CH 2 . provided that when A is : then component B may not be a combination of and provided that when A is a combination of: plus ,Me y / i , Me H.C - * C-CH,-( 0 X 0 >-C0,-< 0 >-CH,C * -C,H. ° 2 Ή 2 \_/\_ 2 \U 2 Ή 2 3 then component B may not be Preferably Component A is present in the range 1-15 wt % , even more preferably 1-5 wt%. Preferably any one compound constituting Component B is present in the range 5~6θ wt°», even more preferably 10-30%. Preferably the material contains optically active dopants of the formula below as described in PCT/GB88/01111; CN R.-[CH=CH— CH 2 ) r -0-^ r X-0CH 2 ) m C0 2 CH-R 2 including wherein R 1 is selected from hydrogen, C._ 12 alkyl, alkoxy, perfluoroalkyl and perfluoroalkoxy and may be straight chain or branched chain; R 2 is alkyl, which may be C 1 _ 8 straight chain, C 1 _ 1 , branched chain or cyclic, r is an integer 1-10, n and m are independently 0 or 1; X is a group of general formula: where (F) indicates that the relevant phenyl ring may carry 1 or 2 fluorine substituents, p is 0 or 1, Z is a single bond when p is 0 and COO or a single bond when p is 1. The CN group may be substituted by CH , CF , halogen, preferably F or Cl. The C0 2 group may be reversed. The chiral unit CH(CN)R 2 may be replaced by a chiral epoxide group. One or more of the phenyl groups may be replaced by a cyclohexyl group. Preferably the device has a V . less than 4 volts and/or a t . less than lOOμs. Component A may be further characterised in that it may combine one or more chiral components with (-) left-handed cholesteric twist sense with one or more chiral components with (+) right-handed twist sense. None of the (-) components can be the optical enantiomers of the (+) components. This chiral mixture may be a chiral smectic itself or maybe used as an additive to a non-chiral and or racemate tilted smectic liquid crystal host material. Alternatively the chiral component or components may have the same cholesteric twist sense providing the cholesteric pitch and Ps are characterised by a tilted chiral smectic liquid crystal material having a cholesteric phase at an elevated temperature above ambient between the chiral smectic and isotropic phases with a cholesteric pitch p greater than half the layer thickness d over a temperature range of at least 0.1°C above a cholesteric to smectic transition temperature and a significant spontaneous polarisation in the chiral smectic phase. US patent 5,061,047 describes some relevant methods for making liquid crystal display devices. The value of Ps is at least 0.1 and preferably 1 or more nC/cm 2 . The layer thickness may be up to 15μm or more but is typically l-12μm. The invention will now be described by way of example only with reference to the accompanying drawings of which: Figure 1 is a diagrammatic view of a time multiplex addressed x, y matrix; Figure 2 is a cross section of part of the display of Figure 1 to an enlarged scale; Figure 3 is a representation of a turnaround in a (t . /V . ) feature. Figures 4-6 are graphs of t/μs versus V/V at 30°C for mixtures 1,2 and 3 respectively, (see Table 1 for mixtures). The display 1 shown in Figures 1, 2 comprises two glass walls 2, 3 spaced about l-6μm apart by a spacer ring 4 and/or distributed spacers. Electrode structures 5. of transparent tin oxide are formed on the inner face of both walls. These electrodes are shown as rows and columns forming an X, Y matrix but may be of other forms. For example, of segments formed into a digital seven bar display. A layer 7 of liquid crystal material is contained between the walls 2, 3 and spacer ring . Polarisers 8, are arranged in front of and behind the cell 1. Row 10 and column 11 drivers apply voltage signals to the cell. Two sets of waveforms are generated for supplying the row and column drivers 10, 11. A strobe wave form generator 12 supplies row waveforms, and a data waveform generator 13 supplies ON and OFF waveforms to the column drivers 11. Overall control of timing and display format is controlled by a contrast logic unit l4. Prior to assembly the walls 2, 3 are surface treated for example by spinning on a thin layer of polyamide or polyimide, drying and where appropriate curing; then buffing with a soft clean cloth (eg rayon) in a single direction Rl , R2. This known treatment provides a surface alignment for liquid crystal molecules. In the absence of an applied electric field the molecules align themselves along the rubbing direction; Rl and R2 are parallel (+/- 30°) in the same or opposite directions. When suitable unidirectional voltages are applied the molecular director aligns along one of two directors Dl, D2 which are at an angle of about 4 ° to each other. The device includes means of discriminating the states optically, eg 1 or more polarisers. It may operate in a transmissive or reflective mode. In the former, light passing through the device eg from a tungsten bulb is selectively transmitted or blocked to form the desired display. In the reflective mode a mirror is placed behind the second polariser 9 to reflect ambient light back through the cell 1 and two polarisers. By making the mirror partly reflecting the device may be operated both in a transmissive and reflective mode. Pleochroic dyes may be added to the material 7. In this case, only one polariser is needed and the layer thickness may be 4-10 μm. For a typical thickness of 2 μm the material at, for example, 22°C is switched by a dc pulse of + or - 0 volts for 100 μs. The two switched states Dl, D2 may be arbitrarily defined as ON after receiving a positive pulse and OFF after receiving a negative pulse of sufficient magnitude. Polarisers 8, 9 are arranged with their polarisation axes perpendicular to one another and with one of the axes parallel to the director in one of the switched states. In operation, strobe waveforms are applied to each row in turn whilst appropriate ON or OFF data waveforms are applied to each column electrode. This provides a desired display pattern formed by some x, y intersection in an ON state and another in an OFF state. Such addressing is termed multiplex addressing. The following compounds and mixtures are examples illustrative of the invention. CoH,_0-( 0 )-C0,C * H(CN)CH(CH 3'2 R' Bi ,τ τ> CO. 0 >-R * R' % B 2 RO <°x°>*- c 7 H 15 c 9 H 19 33.3 C 9 H 19 C 9 H 19 66.6 B ft 3Hi7 ° "cθ2 \ " C5Hi1 Table 1: Mixtures containing compound B L = Smectic A - Smectic C phase transition temperature. Q = Cone Angle. Ps = Spontaneous Polarisation. E = Electric field. cell thickness (d/μm) for the three different mixtures 1.2 and 3 s 2.3. 1-9 and I.65 respectively. When analysing the data presented in Table 1 it is perhaps most instructive to consider the column headed E /Ps and t x Ps~ . Tables 2 and 3 list Ps and Θ data at different temperatures for Mixtures 1 and 2. Table 2: Mixture 1 Table 3: Mixture 2 Various mixtures are assessed below, at 30°C unless otherwise stated, Units for Vmm are V, units for tin l n are μ r-s, , units for Ps are nCcrrf 2 : ZLI 5014-000 is a commercially available mixture from Merck. 60 26 Ps 2.7nCcm 2 , LB7 is a 1:1 mixture of the following: 2 parts 1 part this mixture is then mixed with one part of the following: plus 5% of BE80F2N { 1% active) V = 46 = 29 Ps = 1.9nCcm " AJS20 is a mixture of the following: relative proportions F F plus 5% of BE80F2N (1.75% active) V • i .n = 21.4 t «ι .n = 3 J 8 Ps = 2.3 -'nCcπT 2 . AJS62 is a mixture of the following: relative proportions F F plus 5.1% of BE80F2N (1.8% active) V . = 70 t . = 19.6 AJS64 is a mixture of the following: relative proportions F F plus 5-2% of BE80F2N (2.3% active). V nu .n = 5 ^5 -^ t mi .n = 19.6 AJS67 is a mixture of the following: relative proportions F F plus 5% of BE80F2N (2.25% active). V nu .n = 6.5 -^ t mm . = 19 Ps = 6.9 ^nCcπT 2 . (7-5Vac bias) AJS32 is a mixture of the following: proportion plus 1.75% of BE80F2N V nu .n = 46 t 1. n = 15 -^ Ps = 4.2nCcrrf VH53 i a mixture of the following: relative proportions plus 5% of BE80F2N (1% active) V i .n = 44 t mi .n = 61 Ps = 2.5nCcπf 2 . LPM68 is a mixture of the following: plus 1% of IGS97 V n ,i n = 50 t m . n = 36 Ps = 3- OnC cm 2 . 13/291-1 is a mixture of the following: F F V . = 40 t nu . n = 33 Ps = 6.4nCcπf 2 . (36°C 031291-1 is a mixture of the following: F V . = 38 t . = 35 Ps = 6.5nCcrrf 2 . (25°C) HI is a mixture of the following: plus 1.75% of BE80F2N Vnu.n = 3 - J 5- J tnu.n = 9 J 0 Ps = 9 J .0nCcm " VH50 is a mixture of the following: plus 10% of BE80F2N (1.71% active) V mi .n = 3-'5- ^ t nu .n = 163 Ps = 7.4nCcπf 2 . VF9 is a mixture of the following: NC plus 2% of BE80F2N V mi .n = 61 t nu .n = 41 Ps = 9.2nCcπT BDH 835 i a commercially available mixture from Merck V . = 45 t . = 33 Ps = 9-5nCcm " SCEδ is a commercially available mixture from Merck 50 46 Ps = 5-7nCcπr 2 (25°C LT4 is a mixture of the following: plus 2% of BE80F2N Vmi.n = 5 -*2 tmi.n = 26 Ps = 6.6nCcπf 2 (0°C)' VH51 is a mixture of the following: plus 10% of BE80F2N (1.75% active) V„ mi,.„n = 3 -*0 t mi .n = 66 Ps = 7.1nC cm VH52 is a mixture of the following: plus 10% of BE80F2N (1.7% active) Vnu.n = 3 -*5 *' tnu.n = 121 Ps = 5.7nCcπT- AS452 is a mixture of the following: F F F F F F plus 1.75% of BE80F2N V min = 41 tmnunn = 13—' AS407 is a mixture of the following: F F F F plus 2.5% of IGS97 V mi .n = 5 -'0 t nu .n = 29 J Ps = 7.74nCcm "2 AS436 is a mixture of the following: F F F F plus 2.5% of IGS97 V n . n = 5 -^0 t nu .n = 17 ' Ps = 6.6nCcπT 2 AS435 is the same as AS436 except that there is 1.28% of IGS97 present. = 4 31 Ps = 2.7nCcπ wherein: IGS97 is: BE80F2N CN I C o H,_0- C0„CHCH_

Claims: CLAIMS A ferroelectric liquid crystal device comprising two spaced cell walls each bearing electrode structures and treated on at least one facing surface with an alignment layer, a layer of a smectic liquid crystal material enclosed between the cell walls, a minimum in its response time versus voltage curve, characterised in that the liquid crystal material consists of two components; A and B, where the two components are given by: Component A being present in the range of 0.1-50 wt% and is one or more optically active compounds capable of imparting a spontaneous polarisation to the material. Component B is present in the range sufficient to enable A+B = 100 wt%, and is at least two compounds selected from: wherein a, b and c are independently 0, 1, 2; R ; and R 2 are C 1 _ 1 - straight or branched chain alkyl or alkoxy, preferably C--C 12 . In the above (for Component B) CH=CH linking groups may be replaced by 2 H h and CH,0 linking groups may be replaced by 0CH 2 . provided that when A is : then component B may not be a combination of and provided that when A is a combination of: plus then component B may not be iι Ϊ ^ "coo )' R. 2. A device according to claim 1 wherein one of the compounds constituting component B consists of one or more compounds selected from: A device according to claim 1 or 2 wherein component A is given by the following general formula: R 1 -[CH=CH- -CH 2 ) r -0- -X-(OCH-) YL wherein R χ is selected from hydrogen, C 1 _ 12 alkyl, alkoxy, perfluoroalkyl and perfluoroalkoxy and may be straight chain or branched chain; r is an integer 1-10, n and m are independently 0 or 1; X is a group of general formula: or A, B and C may be independently <pXhenyl or cyclohexyl; (F) indicates that the relevant ring may carry 1 or 2 fluorine substituents; p is 0 or 1; Z is a single bond when p is 0 and COO or a single bond when p is 1; Y may be C0 2 or 0 2 C; L may be a chiral epoxide or is given by the formula: J I CH-R„ J may be CN, F, Cl, CH 3 , or CF 3 ; R 2 is alkyl, which may be C._ 8 straight chain, C._ 15 branched chain or cyclic. 4. A device according to claim 1 or 2 wherein component A is given by the following general formula: J H-R 2 wherein R χ is selected from hydrogen, C 1 12 alkyl, alkoxy, perfluoroalkyl and perfluoroalkoxy and may be straight chain or branched chain; R 2 is alkyl, which may be C l 8 straight chain, C χ branched chain or cyclic, r is an integer 1-10, n and m are independently 0 or 1 ; Y may be C0 2 or 0 2 C; J may be CN, F, Cl, CH 3 or CF, ; X is a group of general formula: A, B and C may be independently phenyl or cyclohexyl; (F) indicates that the relevant ring may carry 1 or 2 fluorine substituents; p is 0 or 1; Z is a single bond when p is 0 and COO or a single bond when p is 1. 5. A device according to claim 4 wherein J is CN and Y is CO 6. A device according to claim 5 wherein A, B and C are phenyl rings. A device according to claim 6 wherein component A is given by the following general formula: A device according to claim 6 wherein component A is given by one of the following general formulae: F CN R <,.-(D0 <0-VcOOCH-R. t t CN I -COOCH-R, 9. A device according to claim 6 wherein component A is given by the following general formula: where n is 0 or 1; r is 1-6; R j is C 1 J2 alkyl or alkoxy and R 2 is a branched chain alkyl. 10. A device according to claim 9 wherein R is isopropyl. 11. A device according to any one of claims 1-10 wherein one of the compounds constituting component B is of the following formula: 12. A device according to any one of claims 1-10 wherein one of the compounds constituting component B is of the following formula: 13- A device according to any one of claims 1-10 wherein one of the compounds constituting component B is of the following formula: *> L &' 14. A device according to any one of claims 1-10 wherein one of the compounds constituting component B is of the following formula: 15- A device according to any one of claims 1-10 wherein one of the compounds constituting component B is of the following formula: 16. A device according to any one of claims 1-10 wherein one of the compounds constituting component B is of the following formula: > <d -R-, 17. A device according to claim 1 wherein one or more of the compounds constituting component A is present in the range 1-15 wt%. 18. A device according to claims 2-l6 wherein one or more of the compounds constituting component A is present in the range 1-15 wt%. 1 . A device according to claim 1 wherein one or more of the compounds constituting component B is present in the range 5~6θ wt%. 20. A device according to claims 2-16 wherein one or more of the compounds constituting component A is present in the range 10-30 wt%. 21. A device according to claim 1 wherein the ferroelectric liquid crystal device is multiplex addressed. 22. A device according to claims 2-20 wherein the ferroelectric liquid crystal device is multiplex addressed. 23. A device according to claim 1 wherein component A when added to component B gives rise to a tilted chiral smectic liquid crystal material having a cholesteric pitch which is greater than half the layer thickness d over a temperature range of at least 0.1°C above a cholesteric to smectic transition temperature and a significant spontaneous polarisation Ps in the chiral smectic phase. 24. A device according to claim 23 wherein component A comprises (+) and (-) chiral materials such that the resultant mixture has a substantial spontaneous polarisation in the chiral tilted smectic phases.

Inventors: JONES JOHN CLIFFORD, MCDONNELL DAMIEN GERARD, SAGE IAN CHARLES, SLANEY ANDREW, JONES, JOHN, CLIFFORD, MCDONNELL, DAMIEN, GERARD, SAGE, IAN, CHARLES, SLANEY, ANDREW
Applicants: JONES JOHN CLIFFORD, MCDONNELL DAMIEN GERARD, SAGE IAN CHARLES, SECR DEFENCE, SLANEY ANDREW, JONES, JOHN, CLIFFORD, MCDONNELL, DAMIEN, GERARD, SAGE, IAN, CHARLES, SLANEY, ANDREW, THE SECRETARY OF STATE FOR DEFENCE
Application year: 1994
Main classification: C09K19
IPC codes: C09K19, G02F1