Polyimide resin composition

Abstract: A polyimide resin composition comprises 1 ○ 99.9 ∼ 50 parts by weight of polyimide having recurring structural units of the formula and 2 ○ 0.1∼50 parts by weight of a polyimide having improved melt flowability and prepared by using 1,3-bis(3-aminophenoxy)benzene or 6,6'-bis(3-aminophenoxy)-3,3,3',3'-tetramethyl-1,1'-spirobiindane as essential diamine component, or polyether pyridine having recurring structural units of the formula: Further, a polyimide based resin composition comprising the polyimide resin composition or a polyimide copolymer obtained by using the above diamines and a fibrous reinforcement are disclosed. These composition have remarkably good processability, excellent heat stability and repeated fatigue characteristics.

Description: The present invention relates to a polyimide resin composition, in particular to a melt-processable composition and more particularly relates to an aromatic polyimide resin composition. The invention further relates to a polyimide copolymer and to a polyimide based composition containing the resin composition or copolymer. Conventionally, polyimide has been excellent in mechanical strengths and dimensional stability in addition to its high heat resistance and also outstanding in flame retardance and electrical insulation. Consequently, polyimide has been used in the field of electric and electronic appliances, space and aeronautic equipment and transport machinery and is expected in future for wide use in the field where heat resistance is required. Polyimide of various kinds which exhibit excellent characteristics has conventionally been developed. However, such polyimide has no distinct glass transition temperature though outstanding in heat resistance and thus must be processed by such means as sintering in order to use as a molding material. On the other hand, polyimide which has excellent processability is insufficient in heat and solvent resistances because of a low glass transition temperature and solubility in halogenated hydrocarbon solvents. Consequently, advantages and drawbacks have been simultaneously found in conventional polyimide. With the extended application of polyimide to various fields of use, it has been strongly desired to develop polyimide which can satisfy various kinds of performance. In particular, in the above industrial field, it has been desired to develop a polyimide having excellent dynamic repeated fatigue characteristic in addition to the above inherent excellent properties of polyimides as an industrial material instead of a metal, for mechanical parts, automobile parts, for example, parts for internal combustion engine such as impeller of centrifugal compressor, turbo-charger, parts for silencer and exhaust system such as manifold, and valve-guide, valve-system, piston, skirt, oil pan and the like. In order to meet such demands, the present inventors have previously found melt-processable polyimide which is excellent in mechanical and electrical properties and outstanding heat and chemical resistances, and had recurring structural units of the formula (1) : wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an aliphatic radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. (Japanese Laid-Open Patent Sho 61-143478, 62-86021, 62-205124, 62-235381 and 63-128025). The polyimide is a melt-processable and heat-resistant resin having many excellent fundamental properties which are specific for polyimide. However, the polyimide is somewhat inferior in processability although heat resistance and other properties are much superior to engineering plastic such as polyethylene terephthalate, polyether sulfone and polyphenylene sulfide. Another melt-processable polyimide having recurring structural units of the formula (5) : and having a glass-transition temperature of about 200°C has been already disclosed in USP 4,485,140 and Japanese Laid-Open Patent SHO 61-143477. A further polyimide having recurring structural units of the formula (6) : and having high heat-resistance and very excellent melt flowability has been disclosed by the present inventors in Japanese Laid-Open Patent SHO 61-143477. Still another polyimide having recurring structural units of the formula (7) : and having extremely excellent melt-flowability has been disclosed by the present inventors in Japanese Laid-Open Patent SHO 62-50375. Further, polyether pyridine having recurring structural units of the formula (4) wherein Y is a divalent radical represented by and having high heat-resistance and extremely outstanding melt-flowability has also been found by the present inventors (Japanese Laid-Open Patent SHO 63-37123). Some of polyether pyridine have a high melting point of 250 °C or above, initiate melt-flow in the neighborhood of 270°C , have a very low viscosity in the molten state and are thus excellent in melt-processability. Although polyimide and polyether pyridine have good melt-processability, other performance is still unsatisfactory cannot meet the demand for polyimide which is excellent in the above various performance and has good processability. Further, a polyimide instead of a metal, which has excellent dynamic repeated fatigue characteristic has not been disclosed. According to embodiments of the invention there is desirably provided a polyimide resin composition having good melt-processability in terms of melting temperature and flowability without giving adverse effect on the essential characteristics of polyimide. More specifically, embodiments of the invention desirably provide a polyimide resin composition which has much improved processability while holding various excellent properties of polyimide having recurring structural units of the above formula (1). Preferred embodiments on the invention preferably also provide a polyimide resin composition which affords formed articles having outstanding repeated fatigue characteristics. The present inventors have found that a polyimide resin composition which comprises polyimide having recurring structural units of the above formula (1) and a specific amount of melt-flowability enhancing polyimide having recurring structural units of the above formula (5), (6) or (3), which is selected from various kinds of polyimide, or polyether pyridine having recurring structural units of the above formula (4) can remarkably improve the melt-processability of polyimide of the formula (1) without impairing the essential characteristics of polyimide, and can also provide excellent fatigue characteristics of formed articles. That is, one aspect of the invention is a polyimide resin composition substantially comprising 99.9 ∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1): wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an aliphatic radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (2) : wherein R 1 is a tetravalent radical represented by or polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (3) : wherein R 2 is a tetravalent radical represented by and/or polyether pyridine comprising a requisite structural unit consisting of one or more recurring structural units of the formula (4) : wherein Y is a divalent radical represented by In a preferred embodiment there is provided a polyimide resin composition substantially comprising 99.9 ∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) : wherein X and R are the same as above, and 0.1∼50 parts by weight of polyimide having recurring structural units of the formula (5) : In another preferred embodiment there is provided a polyimide resin composition comprising substantially 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) and 0.1∼50 parts by weight of polyimide having recurring structural units of the formula (6) : In another preferred embodiment there is provided a polyimide resin composition substantially comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) and 0.1∼50 parts by weight of polyimide having recurring structural units of the formula (7): In yet another embodiment there is provided a polyimide resin composition substantially comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) and 0.1∼50 parts by weight of polyimide having recurring structural units of the formula (8) : In still another aspect of the invention there is provided a polyimide resin composition substantially comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) and 0.1∼50 parts by weight of polyether pyridine comprising a requisite structural unit consisting of one or more recurring structural units of the formula (4) : wherein Y is the same as above. A still further aspect of the invention is a polyimide resin composition wherein, in each of the above composition, polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1), polyimide having recurring structural units of the formula (2), (3), (5), (6), (7) or (8) and polyimide copolymer having one or more recurring structural units of these formulas comprise an end-capped polyimide polymer obtained by reacting diamine compound and tetracarboxylic dianhydride in the presence of aromatic dicarboxylic anhydride of the formula (9): wherein Z is a divalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or aromatic monoamine represented by the formula (10) : V - NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. Additionally, a polyimide copolymer also is included as the polyimide used in the present invention. In the polyimide copolymer, polyimide having the structural recurring units of the formulas (1): (wherein X and R are the same as above) and the structural recurring units of the formulas (2): (wherein R 1 is the same as above) is preferable, more preferably, is the polyimide copolymer comprising 0.5 to 0.95 mole of the recurring structural unit of the formula (1) and 0.5 to 0.05 mole of the recurring structural unit of the formula (2), and is the polyimide copolymer wherein the recurring structual units of the formula (1) is represented by the formula (1-a) : and/or the formula (1-b) and the recurring structual units of the formula (2) is represented by the formula (5) and/or the formula (6) and most preferable polyimide copolymer is the polyimide copolymer having the recurring structural units represented by the formula (1-a) and the recurring structural units represented by the formula (5). These polyimide copolymers also include a capped polyimide which is terminated at the end of the polymer chain with an aromatic ring which is unsubstituted or substituted with a radical having no reactivity with amine and dicarboxylic anhydride. Polyimide compositions of the invention may combine improved processability and excellent dynamic repeated fatigue characteristics without giving adverse effect on the essential characteristics of polyimide having recurring structural units of the formula(1). Polyimides used in the present invention are; 1 ○ a polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) : wherein X and R are the same as above , 2 ○ a polyimide having a requisite structural unit consisting of one or more recurring structural units of the formula (2) : wherein R 1 is the same as above, more specifically a polyimide having recurring structural units represented by the formula (5) : and/or the formula (6) : or 3 ○ a polyimide having a requisite structural unit consisting of one or more recurring structural units of the formula (3) : wherein R 2 is the same as above, more specifically a polyimide having recurring structural recurring units represented by the formula (7) : and/or the formula (8) : These polyimides represented by the formulas (2) and (3), that is, the polyimide having recurring structural unit of the formula (5), (6), (7) or (8), can be used singly or as a mixture, or may be a polyimide copolymer containing two or more of above recurring structural units. Preferred polyimide copolymer in the present invention is the polyimide copolymer having the recurring structural unit represented by the formula(1) and the recurring structural unit represented by the formula (2). The polyimide copolymer preferably contains 0.5 to 0.95 mole of the recurring structural units of the formula (1) and 0.5 to 0.05 mole of the recurring structural units of the formula (2) per mole of the polyimide copolymer. The polyimide copolymer which the recurring structural unit represented by the formula (1) is recurring structural unit of the formula (1-a): and/or the formula (1-b): and the recurring structural unit represented by the formula (2) is recurring structural unit of the formula (5) and/or the formula (6) is more preferable. The polyimide copolymer having recurring structural unit of the formula (1-a) and the formula (5) is most preferable. The polyimide copolymer also includes a capped polyimide copolymer which is terminated at the end of the polymer chain with an aromatic dicarboxylic dianhydride of the formula (9) and/or an aromatic monoamine of the formula (10). Polyimide having recurring structural units of the formula (1) can be prepared from the below-described diamine and tetracarboxylic dianhydride by the known process disclosed in Japanese Laid-Open Patent SHO 61-143478. Diamine used for the preparation of polyimide having recurring structural units of the formula (1) is represented by the formula (11) : Wherein X is a divalent radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl. Exemplary diamines which can be used include, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2-bis[4-(3-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 4,4'-bis(3-aminophenoxy)biphenyl, bis[4-(3-aminophenoxy)phenyl]ketone, bis[4-(3-aminophenoxy)phenyl]sulfide and bis[4-(3-aminophenoxy)phenyl]sulfone. These diamines can be used singly or as a mixture. Tetracarboxylic dianhydride which can be used is represented by the formula (12) : wherein R is a tetravalent radical having 2 ∼27 carbon atoms and being selected from the group consisting of an alkyl radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. In the formula (12) which illustrated tetracarboxylic dianhydride, R is more specifically : (a) an aliphatic radical having 4∼9 carbon atoms, (b) an alicyclic radical having 4∼10 carbon atoms, (c) a monoaromatic radical represented by the formula : (d) a condensed polyaromatic radical represented by the formula : (e) a noncondensed aromatic radical connected to each other with a direct bond or a bridge member and represented by the formula : wherein X i is a direct bond, -O-, -S-, -SO 2 -, -CH 2 -, Exemplary tetracarboxylic dianhydrides which can be practically used include ethylenetetracarboxylic dianhydride, butanetetracarboxylic dianhydride, cyclopentanetetracarboxylic dianhydride, pyromellitic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride, 2,2',3,3'-benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, 2,2',3,3'-biphenyltetracarboxylic dianhydride, 2,2-bis(3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)propane dianhydride, bis(2,3-dicarboxyphenyl)ether dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis(2,3-dicarboxyphenyl)sulfone dianhydride, bis(3,4-dicarboxyphenyl)sulfone dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)methane dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, 1,1-bis(3,4-dicarboxyphenyl)ethane dianhydride, 1,2-bis(2,3-dicarboxyphenyl)ethane dianhydride, 1,2-bis(3,4-dicarboxyphenyl)ethane dianhydride, 1,3-bis(2,3-dicarboxyphenoxy)benzene dianhydride, 1,3-bis(3,4-dicarboxyphenoxy)benzene dianhydride, 1,4-bis(2,3-dicarboxyphenoxy)benzene dianhydride, 1,4-bis(3,4-dicarboxyphenoxy)benzene dianhydride, 2...6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,2,3,4-benzenetetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride, and 1,2,7,8-phenanthrenetetracarboxylic dianhydride. These tetracarboxylic dianhydrides can be used singly or as a mixture. Polyimide of the formula (5) or (6) can be prepared by reacting diamine, 1,3-bis(3-aminophenoxy)benzene, represented by the formula (13) : with tetracarboxylic dianhydride, pyromellitic dianhydride of the formula (14) : or 3,3'4,4'-biphenyltetracarboxylic dianhydride of the formula(15) : Polyimide of the formula (7) or (8) can be prepared by reacting diamine, 6,6'-bis(3-aminophenoxy)-3,3,3',3'-tetramethyl-1,1'-spirobiindane, represented by the formula (16) : with tetracarboxylic dianhydride, pyromellitic dianhydride represented by the formula (14): or 3,3'4,4'-biphenyltetracarboxylic dianhydride represented by the formula (15) : Further, the polyimide copolymer can be prepared by using two or more diamine compounds or two or more tetracarboxylic dianhydrides as raw materials. That is, the polyimide copolymer having recurring structural units of the formula (1) and recurring structural units of the formula (2) is obtained by reacting diamine represented by the formula (11): wherein X is the same as above and diamine represented by the formula (13): as diamine component, with tetracarboxylic dianhydride represented by the formula (12) wherein R is the same as above. Prefered polyimide copolymer having the above recurring structural unit of the formula (1-a) and/or the formula (1-b) and the above recurring structural unit of the formula (5) and/or the formula (6) can be obtained by reacting diamine represented by the formula (11-a) and diamine represented by the formula (13) as diamine component, with pyromellitic dianhydride represent by the formula (14) and/or 3,3',4,4'-biphenyltetracarboxylic dianhydride represented by the formula(15) Each polyimide or polyimide copolymer for use in the invention is prepared by using above diamine as a raw material. However, other diamines can also be used in combination with the above diamine in the range of giving no adverse effect on the good properties of polyimide. Other diamines which can be used in combination include, for example, m-phenylenediamine, o-phenylenediamine, p-phenylenediamine, m-aminobenzylamine, o-aminobenzylamine, 3-chloro-1,2-phenylenediamine, 4-chloro-1,2-phenylenediamine, 2,3-diaminotoluene, 2,4-diaminotoluene, 2,5-diaminotoluene, 2,6-diaminotoluene, 3,4-diaminotoluene, 3,5-diaminotoluene, 2-methoxy-1,4-phenylenediamine, 4-methoxy-1,2-phenylenediamine, 4-methoxy-1,3-phenylenediamine, benzidine, 3,3'-dichlorobenzidine, 3,3'-dimethylbenzidine, 3,3'-dimethoxybenzidine, 3,3'-diaminodiphenyl ether, 3,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl ether, 3,3'-diaminodiphenyl sulfide, 3,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenyl sulfide, 3,3'-diaminodiphenyl sulfoxide, 3,4'-diaminodiphenyl sulfoxide, 4,4'-diaminodiphenyl sulfoxide, 3,3'-diaminodiphenyl sulfone, 3,4'-diaminodiphenyl sulfone, 4,4'-diaminodiphenyl sulfone, 3,3'-diaminobenzophenone, 3,4'-diaminobenzophenone, 4,4'-diaminobenzophenone, 3,3'-diaminodiphenylmethane, 3,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylmethane, bis[4-(4-aminophenoxy)phenyl]methane, 1,1-bis[4-(4-aminophenoxy)phenyl]ethane, 1,2-bis[4-(4-aminophenoxy)phenyl]ethane, 1,1-bis[4-(4-aminophenoxy)phenyl]propane, 1,2-bis[4-(4-aminophenoxy)phenyl]propane, 1,3-bis[4-(4-aminophenoxy)phenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, 1,1-bis[4-(4-aminophenoxy)phenyl]butane, 1,2-bis[4-(4-aminophenoxy)phenyl]butane, 1,3-bis[4-(4-aminophenoxy)phenyl]butane, 1,4-bis[4-(4-aminophenoxy)phenyl]butane, 2,2-bis[4-(4-aminophenoxy)phenyl]butane, 2,3-bis[4-(4-aminophenoxy)phenyl]butane, 2-[4-(4-aminophenoxy)phenyl]-2-[4-(4-aminophenoxy)-3-methylphenyl]propane, 2,2-bis[4-(4-aminophenoxy)-3-methylphenyl]propane, 2-[4-(4-aminophenoxy)phenyl]-2-[4-(4-aminophenoxy)-3,5-dimethylphenyl]propane, 2,2-bis[4-(4-aminophenoxy)-3,5-dimethylphenyl]propane, 2,2-bis[4-(4-aminophenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 1,3-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)benzene, 1,4-bis(4-aminophenoxy)benzene, 4,4'-bis(4-aminophenoxy)biphenyl, bis[4-(4-aminophenoxy)phenyl]ketone, bis[4-(4-aminophenoxy)phenyl]sulfide, bis[4-(4-aminophenoxy)phenyl]sulfoxide, bis[4-(4-aminophenoxy)phenyl]sulfone, bis[4-(3-aminophenoxy)phenyl]ether, bis[4-(4-aminophenoxy)phenyl]ether, 1,3-bis[4-(3-aminophenoxy)benzoyl]benzene, 1,3-bis[4-(4-aminophenoxy)benzoyl]benzene, 1,4-bis[4-(3-aminophenoxy)benzoyl]benzene, 1,4-bis[4-(4-aminophenoxy)benzoyl]benzene, 4,4'-bis(3-aminophenoxy)biphenyl, 4,4'-bis(3-aminophenoxy)-3,3'-dimethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dimethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetramethylbiphenyl, 4,4'-bis(3-aminophenoxy)-3,3'-dichlorobiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dichlorobiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetrachlorobiphenyl, 4,4'-bis(3-aminophenoxy)-3,5-dibromobiphenyl, 4,4'-bis(3-aminophenoxy)-3,3',5,5'-tetrabromobiphenyl, bis[4-(3-aminophenoxy)-3-methoxyphenyl]sulfide, [4-(3-aminophenoxy)phenyl][4-(3-aminophenoxy)-3,5-dimethoxyphenyl]sulfide and bis[4-(3-aminophenoxy)-3,5-dimethoxyphenyl]sulfide. Polyimide prepared by using these aromatic diamines and aromatic tetracarboxylic dianhydrides as monomer components primarily has a requisite structural unit consisting of one or more recurring structural units of the formula (1), the formula (2), that is, the formula (5) or (6), or the formula (3), that is, the formula (7) or (8). Polyimide also includes a capped polyimide which is terminated at the end of the polymer chain having a requisite structural unit consisting of one or more recurring structural units of the formula (1), (2), (5), (6),(3), (7) or (8) with an aromatic ring which is unsubstituted or substituted with a radical having no reactivity with amine and dicarboxylic anhydride. Additionally, the said polyimide copolymer also may be terminated at the end of polymer chain with the aromatic ring. The capped polyimide having at the polymer chain end an aromatic ring which is unsubstituted or substituted with a radical having no reactivity with amine or dicarboxylic anhydride can be prepared by reacting the above diamine with the above tetracarboxylic dianhydride in the presence of aromatic dicarboxylic anhydride of the formula (9) : wherein z is a divalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or aromatic monoamine represented by the formula (10): V - NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. Exemplary aromatic dicarboxylic anhydrides of the formula (9) include phthalic anhydride, 2,3-benzophenonedicarboxylic anhydride, 3,4-benzophenonedicarboxylic anhydride, 2,3-dicarboxyphenyl phenyl ether anhydride, 3,4-dicarboxyphenyl phenyl ether anhydride, 2,3-biphenyldicarboxylic anhydride, 3,4-biphenyldicarboxylic anhydride, 2,3-dicarboxyphenyl phenyl sulfone anhydride, 3,4-dicarboxyphenyl phenyl sulfone anhydride, 2,3-dicarboxyphenyl phenyl sulfide anhydride, 3,4-dicarboxyphenyl phenyl sulfide anhydride, 1,2-naphthalenedicarboxylic anhydride, 2,3-naphthalenedicarboxylic anhydride, 1,8-naphthalenedicarboxylic anhydride, 1,2-anthracenedicarboxylic anhydride, 2,3-anthracenedicarboxylic anhydride and 1,9-anthracenedicarboxylic anhydride. These dicarboxylic acid anhydrides can be substituted with a radical having no reactivity with amine and dicarboxylic anhydride and can be used singly or as a mixture. Phthalic anhydride is most preferred in view of properties and utility of polyimide obtained. The amount of aromatic dicarboxylic anhydride used is 0.001 ∼1.0 mol per mol of the above diamine. The amount less than 0.001 mol leads to viscosity increase in processing at high temperatures and causes deterioration of processability. On the other hand, the amount exceeding 1.0 mol results in lowered mechanical properties. Preferred amount is in the range of 0.01 to 0.5 mol. Aromatic monoamines of the formula (10) includes, for example, aniline, o-toluidine, m-toluidine, p-toluidine, 2,3-xylidine, 2,6-xylidine, 3,4-xylidine, 3,5-xylidine, o-chloroaniline, m-chloroaniline, p-chloroaniline, o-bromoaniline, m-bromoaniline, p-bromoaniline, o-nitroaniline, m-nitroaniline, p-nitroaniline, o-aminophenol, m-aminophenol, p-aminophenol, o-anisidine, m-anisidine, p-anisidine, o-phenetidine, m-phenetidine, p-phenetidine, o-aminobenzaldehyde, m-aminobenzaldehyde, p-aminobenzaldehyde, o-aminobenzonitrile, m-aminobenzonitrile, p-aminobenzonitrile, 2-aminobiphenyl, 3-aminobiphenyl, 4-aminobiphenyl, 2-aminophenyl phenyl ether, 3-aminophenyl phenyl ether, 4-aminophenyl phenyl ether, 2-aminobenzophenone, 3-aminobenzophenone, 4-aminobenzophenone, 2-aminophenyl phenyl sulfide, 3-aminophenyl phenyl sulfide, 4-aminophenyl phenyl sulfide, 2-aminophenyl phenyl sulfone, 3-aminophenyl phenyl sulfone, 4-aminophenyl phenyl sulfone, α-naphthylamine, β-naphthylamine, 1-amino-2-naphthol, 2-amino-1-naphthol, 4-amino-1-naphthol, 5-amino-1-naphthol, 5-amino-2-naphthol, 7-amino-2-naphthol, 8-amino-1-naphthol, 8-amino-2-naphthol, 1-aminoanthracene, 2-aminoanthracene, and 9-aminoanthracene. These aromatic monoamines can be substituted with a radical having no reactivity with amine or dicarboxylic anhydride, and can be used singly or as a mixture. Aniline is most preferably used in view of properties and utility of polyimide obtained. The amount of aromatic monoamine is 0.001 ∼1.0 mol per mol of the aromatic tetracarboxylic dianhydride. The amount of less than 0.001 mol leads to viscosity increase in processing at high temperatures and causes deterioration of processability. On the other hand, the amount exceeding 1.0 mol results in lowered mechanical properties. Preferred amount is in the range of 0.01 ∼0.5 mol. Polyimide of the invention can be prepared by any known process. For example, polyimide of the formula (1) can be prepared by Japanese Laid-Open Patent SHO 61-143478, and polyimide of the formula (3) can be prepared by Japanese Laid-Open Patent SHO 62-50375. Preparation is carried out by the following processes. (1) A process for preparing polyamic acid in an organic solvent isolating the polyamic acid by removing the solvent at a low temperature under reduced pressure or by pouring the resulting polyamic acid solution into a lean solvent, and imidizing the polyamic acid by heating to obtain polyimide. (2) A process for preparing a polyamic acid solution by the same procedures as (1), chemically imidizing polyamic acid by addition of a dehydrating agent such as acetic anhydride optionally in the presence of a catalyst, successively isolating resultant polyimide by known procedures and, if desired, washing and drying the polyimide. (3) A process for preparing polyamic acid solvent by the same procedures as (1) and successively conducting solution removal and thermal imidization at the same time by heating under reduced pressure. (4) A process for mixing raw materials and solvents, and simultaneously conducting preparation of aromatic polyamic acid and imidization reaction thereof by heating optionally in the presence of a catalyst, azeotropic agent or dehydrating agent. In the preparation of polyimide by these processes, it is particularly preferred to carry out the reaction in organic solvents. Organic solvents which can be used include, for example, N,N-dimethylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, N,N-dimethylmethoxyacetamide, N-methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, N-methylcaprolactam, 1,2-dimethoxyethane, bis(2-methoxyethyl)ether, 1,2-bis(2-methoxyethoxy)ethane, bis[2-(2-methoxyethoxy)ethyl]ether, tetrahydrofuran, 1,3-dioxane, 1,4-dioxane, pyridine, picoline, dimethyl sulfoxide, dimethyl sulfone, tetramethylurea, hexamethylphosphoramide, phenol, o-cresol, m-cresol, p-cresol, m-cresylic acid, p-chlorophenol, xylenols and anisole. These solvents can be used singly or as a mixture. When polyimide is prepared in a solvent by using diamines, tetracarboxylic dianhydrides and dicarboxylic anhydride or aromatic monoamine, these raw materials are charged and reacted by the following methods. (1) A method for reacting tetracarboxylic dianhydride with diamine and successively adding dicarboxylic anhydride or aromatic monoamine to continue the reaction. (2) A method for reacting diamine with dicarboxylic anhydride and successively adding aromatic tetracarboxylic dianhydride to continue the reaction. Alternatively, a method for reacting tetracarboxylic dianhydride with aromatic monoamine and successively adding diamine to continue the reaction. (3) A method for simultaneously charging tetracarboxylic dianhydride , diamine and dicarboxylic anhydride or aromatic monoamine to carry out the reaction. Any of the above methods can be employed for progressing the reaction. In these methods, the reaction temperature for polymerization and imidization is 300 °C or less. No particular limitation is imposed upon the reaction pressure, and the reaction can be sufficiently carried out under atmospheric pressure. The reaction time differs depending upon diamine, tetracarboxylic dianhydride, solvent, catalyst and reaction temperature. The reaction time of 4∼24 hours is usually sufficient. In the polyimide, the molar ratio of tetracarboxylic dianhydride to aromatic is usually controlled in order to adjust the molecular weight of the formed polyimide. In oder to obtain polyimide having good melt-flowability in the process of the invention, the molar ratio of diamine to tetracarboxylic dianhydride is suitably in the range of 0.8 to 1.2. When polyimide copolymer is prepared by reacting a mixture of diamine of the formula (11-a) and diamine of the formula (13) as a diamine component with tetracarboxylic dianhydride of the formula (14) and/or (15),the molar ratio of these diamines is preferably from 0.5 to 0.95 mole of diamine of the formula (11-a), that is, 4,4'-bis(3-aminophenoxy)diphenyl, and from 0.5 to 0.05 mole of the formula(13), that is, 1,3-bis(3-aminophenoxy)benzene, for one mole of total amount of diamine component. The above methods provide polyimide having recurring structural units of the formula (1) for use in the invention, polyimide having recurring structural units of the formula (2), that is, polyimide having recurring structural units of the formula (5) or (6), and polyimide having recurring structural units of the formula (3), that is, polyimide having recurring structural units of the formula (7) or (8), or polyimide copolymer having two or more recurring structural units, or capped polyimide or polyimide copolymer which is terminated the polymer chain end with dicarboxylic anhydride and/or aromatic monoamine. Polyether pyridine of the formula (4) for use in the invention can be prepared by the process described in Japanese Laid-Open Patent SHO 63-37123. Polyether pyridine is prepared by reacting 2,6-dihalogenopyridine represented by the formula (17) : wherein Q is chlorine atoms, bromine atom or fluorine atom, and may be same or different, with one or more dihydroxy compounds represented by the formula (18) : HO - Y - OH wherein Y is a divalent radical represented by in the presence of alkali metal carbonate and/or bicarbonate or hydroxide. One or more of other dihydroxy compounds can also be used combination in the range of giving no adverse effect on the properties of polyether pyridine. Polyether pyridine prepared by using 2,6-dihalogenopyridine and the dihydroxy compound as monomer components has recurring structural units of the formula (4). Polyether pyridine also includes a capped polyether pyridine which is terminated at the end of the polymer chain having recurring structural units of the formula (4) with an aromatic ring which is unsubstituted or substituted with a radical having no reactivity with amine and dicarboxylic anhydride. The favorably melt-processable polyimide resin composition of the present invention is : (1) a resin composition comprising : a. polyimide having a requisite structural unit consisting of one or more recurring structural units of the formula (1) and/or polyimide capped at the polymer chain end thereof, and b. polyimide having recurring structural units of the formula (2), specifically the formula (5) or the formula (6), and/or polyimide capped at the polymer chain end thereof (hereinafter referred to as polyimide B), (2) a resin composition comprising : a. polyimide having a requisite structural unit consisting of one or more recurring structural units of the formula (1) and/or polyimide capped at the polymer chain end thereof, and c. polyimide having recurring structural units of the formula (3), specifically the formula (7) or the formula (8), and/or polyimide capped at the polymer chain end thereof (hereinafter referred to as polyimide C), and (3) a resin composition comprising : a. polyimide a requisite structural unit consisting of one or more recurring structural units of the formula (1) and/or polyimide capped at the polymer chain end thereof (hereinafter referred to as polyimide A), and d. polyether pyridine having recurring structural units of the formula (4) and/or polyether pyridine capped at the polymer chain end thereof (hereinafter referred to a polyether pyridine D). The term "and/or" in the above cases means, for example, that "polyimide having recurring structural units of the formula (1) and/or polyimide capped at the polymer chain end thereof" is polyimide having recurring structural units of the formula (1) or polyimide capped at the polymer chain end thereof or a mixture of these polymers. Polyimide B, polyimide C or polyether pyridine D which is combined with polyimide A as described above can be used as a mixture in the range capable of attaining the effect of the invention. Copolyimide including two or more of recurring structural units of the formulae (2) and (3) and end-capped polymer thereof also can be used in the present invention as polyimide B or C. The polyimide resin composition of the invention is prepared so as to comprise from 99.9 to 50 parts by weight of polyimide A and from 0.1 to 50 parts by weight of polyimide B, polyimide C, polyether pyridine D or a mixture thereof. The polyimide resin composition of the invention exhibits good melt flowability at a high temperature region of 350 °C or above. The effect on the melt flowability improvement for the polyimide composition of the invention can be observed by addition of only a small amount of polyimide B, polyimide C or polyether pyridine D to polyimide A. The lower limit of addition is 0.1 part by weight, preferably 0.5 part by weight. Various properties of polyether pyridine of the formula (4) rank as one of the excellent in heat resistant resins. However, stability of polyether pyridine against thermal oxidation is inferior to that of polyimide of the formula (1) and thus unfavorably impairs essential characteristics of polyimide of the formula (1). As a result, the proportion of particularly polyether pyridine in the composition has an upper limit and is preferably 50 parts by weight. The polyimide resin composition of the invention can be prepared from polyimide A and polyimide B, polyimide C, polyether pyridine D or a mixture thereof by a known process. For example, following processes are preferred. 1 ○ Polyimide A is premixed with polyimide B, polyimide C, polyether pyridine D or a mixture thereof by using a mortar Henschel mixer, drum blender, tumbling mixture, ball mill or ribbon blender. 2 ○ Polyimide A is previously dissolved or suspended in an organic solvent. Polyimide B, polyimide C, polyether pyridine D or a mixture thereof is added to the resulting solution or suspension and uniformly dissolved or suspended. Thereafter the organic solvent is removed. 3 ○ Polyimide B, polyimide C, polyether pyridine D or a mixture thereof is dissolved or suspended in an organic solvent solution of polyamic acid precursor of polyimide A. The resulting solution or suspension is successively heat-treated at 100∼ 400°C or chemically imidized by using a common imidizing agent. Thereafter the solvent is removed by a known method. 4 ○ Polyimide A is previously dissolved or suspended in an organic solvent. The resulting solution or suspension is mixed with an organic solvent solution of the polyamic acid precursor of polyimide B, polyimide C or a mixture thereof and successively heat-treated at 100 ∼ 400 °C or chemically imidized by using a common imidizing agent. Thereafter the solvent is removed by a known method. 5 ○ An organic solvent solution of the polyamic acid precursor of polyimide A is mixed with an organic solvent solution of the polyamic acid precursor of polyimide B, polyimide C or a mixture thereof and successively heat-treated at 100 ∼ 400°C or chemically imidized by using a common imidizing agent. Thereafter the solvent is removed by a known method. The polyimide resin composition thus obtained is applied as intact to various processing methods such as injection molding, compression molding, transfer molding and extrusion forming. It is more preferred to use the composition after molt kneading . Particularly in blending the above compositions, it is also a simple and effective method to melt-knead powder and powder, pellet and pellet, or powder and pellet. Melt-kneading can be conducted with equipment commonly used for melt-kneading rubber and plastics, for example, hot rolls, Banbury mixture, Brabender and extruder. The melt-kneading temperature is set above the melt-flow temperature of the formulation and below the decomposition initiating temperature of the formulation. The temperature is usually 250∼ 420 °C, preferably 300∼ 400 °C. The melt-processable resin composition of the invention can be preferably processed by injection molding or extrusion forming which provides a uniformly blended product and has high productivity. Other processing methods such as compression molding, transfer molding and sinter forming can also be employed. Other resins can also be formulated in a suitable amount depending upon the use of product as long as giving no adverse effect on the object of the invention. Other resins include, for example, thermoplastic resins such as polyethylene, polypropylene, polycarbonate, polyarylate, polyamide, polysulfone, polyether sulfone, polyether ketone, polyphenylene sulfide, polyamideimide, polyetherimide, modified polyphenylene oxide and other kinds of polyimide, and thermosetting resins. One or more solid lubricants such as molybdenum disulfide, graphite, boron nitride, lead monoxide and lead powder can be added to the polyimide resin composition of the invention. Further, other common additives such as antioxidants, heat stabilizers, ultraviolet absorbers, flame retardants, flame retarding adjuvants, antistatic agents and colorants can also be added to the composition in the range of not impairing the object of the invention. One or more reinforcements, for example, glass fiber, carbon fiber, aromatic polyamide fiber, potassium titanate fiber and glass can also be added to the composition. A polyimide based resin composition of the present invention comprise polyimide resin composition or polyimide copolymer of the present invention and one or more fibrous reinforcements. The fibrous reinforcements used in the invention include, for example, carbon fiber, glass fiber, aromatic polyamide fiber, potassium titanate fiber and the like. Carbon fiber is preferably used in practical. Amount of the fibrous reinforcements used in the polyimide based composition is 5 to 100 parts by weight, preferably 10 to 100 parts by weight for 100 parts by weight of the above polyimide resin composition or the polyimide copolymer. In case of the polyimide copolymer having recurring structural units of the formulas (1) and (2), especially, the polyimide copolymer having 0.5 to 0.95 molar ratio of recurring structural unit of the formula (1) and 0.5 to 0.05 molar ratio of recurring structural unit of the formula (2), amount of the fibrous reinforcements is preferably 5 to 65 parts by weight, more preferably 15 to 40 parts by weight, most preferably 25 to 35 parts by weight, for 100 parts by weight of the polyimide copolymer. An amount less than 5 parts by weight causes reduction mechanical strength and can not sufficient repeated fatigue strength. On the other hand, an amount exceeding 65 parts by weight lowers melt-processability. The polyimide based resin composition of the invention can be prepared by various known processes for blending fibrous reinforcements in resin. For example, the polyimide resin composition or the polyimide copolymer is premixed with fibrous reinforcement by using a mortar, Henschel mixer, drum blender, tumbling mixer, ball mill or ribbon blender and thereafter melt-kneaded with a melt mixer or hot rolls to obtain pellets or a powdery mixture. The polyimide based resin composition of the invention can provide various form of articles by changing mold of injection molding. Particularly, the polyimide based resin composition is excepted to employ as parts for automobile, for example, valve-lifter, impeller and the like, which is strongly desired dynamic repeated fatigue. The present invention will hereinafter be illustrated in detail by way of synthetic examples, examples and comparative examples. In these examples, properties were measured by the following methods. Inherent viscosity : After dissolving 0.50 g of polyimide powder in 100 ml of a solvent mixture of p-chlorophenol and phenol in a weight ratio of 90:10, the solution was cooled to 35 °C and viscosity was measured. Glass transition temperature (Tg) : Measured by DSC with a Shimadzu DT-40 series. 5 % weight loss temperature : Measured by DTA-TG in the air with a Shimadzu DT-40 series, Model 40M. Melt viscosity : Measured at 420 °C with a Koka type flowtester, Model Shimadzu CFT-500 by using an orifice of 0.1 cm in diameter and 1 cm in length under 100 Kg lond. Synthetic Example 1 To a reaction vessel equipped with a stirrer, reflux condenser, water separator and a nitrogen inlet tube, 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl, 2.08 kg (9.53 mol) of pyromellitic dianhydride, 138 g (1.5 mols) of γ -picoline and 23.0 kg of m-cresol were charged and heated to 145°C with stirring in a nitrogen atmosphere while distilling out about 340 g of water. The reaction was further continued at 140 ∼150 °C for 4 hours. Thereafter the reaction mixture was cooled to room temperature, poured into 81.2 kg of methyl ethyl ketone, and filtered. The precipitate thus obtained was further washed with methyl ethyl ketone and dried in a nitrogen atmosphere at 50 °C for 24 hours and successively at 200 °C for 6 hours. Polyimide powder obtained was 5.27 kg (98.5 % yield). The polyimide powder had an inherent viscosity of 0.49 dl /g, Tg of 249 °C and a 5 % weight loss temperature of 545 °C . Synthetic Example 2 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 1 except that 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl and 2.08 kg (9.53 mol) of pyromellitic dianhydride were replaced by 4.32 kg (10.0 mols) of bis[4-(3-aminophenoxy)phenyl]sulfone and 2.09 kg (9.6 mols) of pyromellitic dianhydride. Polyimide powder thus obtained was 5.96 kg (98.5 % yield). The polyimide powder had an inherent viscosity of 0.49 dl /g, Tg of 254 °C and a 5 % weight loss temperature of 540 °C. Synthetic Example 3 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 1 except that 2.08 kg (9.53 mols) of pyromellitic dianhydride was replaced by 2.10 kg (9.65 mols) of pyromellitic dianhydride and 103.6 g (0.7 mol) of phthalic anhydride was further added. Polyimide powder thus obtained was 3.88 kg (99.0 % yield). The polyimide powder had an inherent viscosity of 0.70 dl /g, Tg of 253 °C and a 5 % weight loss temperature of 548 °C. Synthetic Example 4 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 1 except that 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl and 2.08 kg (9.53 mol) of pyromellitic dianhydride were replaced by 2.92 kg (10.0 mols) of 1,3-bis(3-aminophenoxy)benzene and 1.96 kg(9.00 mols) of pyromellitic dianhydride, and 296 g (2.00 mols) of phthalic anhydride was further added. Polyimide powder thus obtained was 5.23 kg (95 % yield). The polyimide powder had an inherent viscosity of 0.24 dl /g, Tg of 194 °C and a 5 % weight loss temperature of 498 °C. Synthetic Example 5 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 1 except that 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl and 2.08 kg (9.53 mol) of pyromellitic dianhydride were replaced by 2.92 kg (10.0 mols) of 1,3-bis(3-aminophenoxy)benzene and 2.65 kg(9.00 mols) of 3,3',4,4'-biphenyltetracarboxylic dianhydride, and 296 g (2.00 mols) of phthalic anhydride was further added. Polyimide powder thus obtained was 5.23 kg (95 % yield). The polyimide powder had an inherent viscosity of 0.26 dl /g, Tg of 183 °C and a 5 % weight loss temperature of 502 °C. Synthetic Example 6 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 1 except that 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl and 2.08 kg (9.53 mol) of pyromellitic dianhydride were replaced by 4.91 kg (10.0 mols) of 6,6'-bis(3-aminophenoxy)-3,3,3',3'-tetramethyl-1,1'-spirobiindane and 2.12 kg (9.70 mols) of pyromellitic dianhydride, and 88.8 g (0.06 mol) of phthalic anhydride was further added. Polyimide powder thus obtained was 5.41 kg (80 % yield), The polyimide powder had an inherent viscosity of 0.31 dl /g, Tg of 243 °C and a 5 % weight loss temperature of 504 °C. Synthetic Example 7 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 1 except that 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl and 2.08 kg (9.53 mols) of pyromellitic dianhydride were replaced by 3.551 kg (9.65 mols) of 4,4'-bis(3-aminophenoxy)biphenyl and 2.18 kg (10.0 mols) of pyromellitic dianhydride, and 65.1 g (0.7 mol) of aniline was further added. Polyimide powder thus obtained was 5.66 kg. The polyimide powder had an inherent viscosity of 0.70 dl /g, Tg of 252 °C, and a 5 % weight loss temperature of 547°C. Synthetic Example 8 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 3 except that 2.10 kg (9.65 mols) of pyromellitic dianhydride was replaced by 2.84 kg (9.6 mols) of 3,3',4,4'-biphenyltetracarboxylic dianhydride. Polyimide powder thus obtained was 6.2 kg (99 % yield). The polyimide powder had an inherent viscosity of 0.76 dl /g, Tg of 221 °C, and a 5 % weight loss temperature of 536°C Synthetic Example 9 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 3 except that 2.10 kg (9.65 mols) of pyromellitic dianhydride was replaced by 2.99 kg (9.65 mols) of 3,3',4,4'-diphenylethertetracarboxylic dianhydride. Polyimide powder thus obtained was 6.35 kg (99 % yield). The polyimide powder had an inherent viscosity of 0.78 dl /g, Tg of 200 °C , and a 5 % weight loss temperature of 515°C. Synthetic Example 10 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 3 except that 2.10 kg (9.65 mols) of pyromellitic dianhydride was replaced by 1.912 kg (9.65 mols) of 1,2,3,4-butanetetracarboxylic dianhydride. Polyimide powder thus obtained was 5.23 kg (98 % yield). The polyimide powder had an inherent viscosity of 0.50 dl /g, Tg of 210 °C, and a 5 % weight loss temperature of 400°C. Synthetic Example 11 To a 10 liter reaction vessel equipped with a stirrer and water separator, 750 g (5.03 mols) of purified 2,6-dichloropyridine, 931 g (5.0 mols) of purified 4,4'-dihydroxybiphenyl, 760 g (5.5 mols) of anhydrous potassium carbonate, 2000 ml of 1,3-dimethyl-2-imidazolidinone and 2000 ml of benzene were charged. The mixture was heated with stirring under nitrogen gas ventilation and azeotropic dehydration was carried out for an hour under refluxing of benzene. Successively benzene was gradually removed from the reaction system while maintaining the refluxing state. The temperature of the mixture rose from 120 °C to 140 °C over 2 hours. Successively the reaction was carried out at 170∼180 °C for 3 hours with occasional and dropwise addition of toluene for azeotropic dehydration. The reaction was further continued at 200 °C for 3 hours and at 220 °C for 3 hours. After finishing the reaction, the reaction mixture which was in a partially crystallized state was directly poured into 4 liters of methanol, stirred for 10 minutes with a high speed mixture and filtered. The filter cake was washed with 4 liters of a 70 % aqueous methanol solution, filtered washed thoroughly with water, and dried. White powder thus obtained was 1.3 kg. Synthetic Example 12 Procedures of Synthetic Example 11 were repeated except that the raw material 4,4'-dihydroxydiphenyl was replaced by 550 g (5.0 moles) of hydroquinone. White polymer thus obtained was 900 g. Synthetic Example 13 Polyimide powder was prepared by repeating the procedures of Synthetic Example 1 except that 2.08 kg (9.53 mols) of pyromellitic dianhydride dianhydride was replaced by 2.16 kg (9.9 mols) of pyromellitic dianhydride. Polyimide powder thus obtained had an inherent viscosity of 0.90 dl /g, Tg of 261 °C, and a 5 % weight loss temperature of 553°C. Synthetic Example 14 To a reaction vessel equipped with a stirrer, reflux condenser, water separator and a nitrogen inlet tube, 1.84 kg (5.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl, 1.46 kg (5.0moles) of 1,3-bis(3-aminophenoxy)benzene, 2.15 kg (9.85 mol) of pyromellitic dianhydride, 44.4 g (0.3 mole) of phthalic anhydride, 138 g (1.5 mols) of γ -picoline picoline and 21.8 kg of m-cresol were charged and heated to 145°C with stirring in a nitrogen atmosphere while distilling out about 340 g of water. The reaction was further continued at 140 ∼ 150 °C for 4 hours. Thereafter the reaction mixture was cooled to room temperature, poured into 80 kg of methyl ethyl ketone, and filtered. The precipitate thus obtained was further washed with methyl ethyl ketone and dried in a nitrogen atmosphere at 50 °C for 24 hours and successively at 200 °C for 6 hours. Polyimide powder obtained was 5.01 kg (98.5 % yield). The polyimide powder had an inherent viscosity of 0.79 d ℓ/g, Tg of 235 °C and a 5 % weight loss temperature of 550 °C. Synthetic Example 15 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 14 except that 1.84 kg (5.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl, 1.46 kg (5.0 mols) of 1,3-bis(3-aminophenoxy)benzene, 2.15 kg (9.85 mol) of pyromellitic dianhydride, 44.4 g (0.3 mole) of phthalic anhydride was replaced by 2.944 kg (8.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.584 kg (2.0 mols) of 1,3-bis(3-aminophenoxy)benzene, 2.13 kg (9.75 mols) of pyromellitic dianhydride, 74 g (0.5 mols) of phthalic anhydride. Polyimide powder thus obtained was 5.32 kg (99 % yield). The polyimide powder had an inherent viscosity of 0.55 d ℓ/g , Tg of 240 °C, and a 5 % weight loss temperature of 550°C. Synthetic Example 16 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 15 except that 2.944 kg (8.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.58 kg (2.0 mols) of 1,3-bis(3-aminophenoxy)benzene was replaced by 3.68 kg (10.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl. Polyimide powder thus obtained was 5.47 kg (99 % yield). The polyimide powder had an inherent viscosity of 0.54 d ℓ/g, Tg of 240 °C, and a 5 % weight loss temperature of 550°C. Comparative Synthetic Example 1 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 15 except that 2.944 kg (8.0 mols) of 4,4'-bis(3-aminophenoxy)biphenyl, 0.58 kg (2.0 mols) of 1,3-bis(3-aminophenoxy)benzene was replaced by 2.98 kg (10.0 mols) of 1,3-bis(3-aminophenoxy)benzene. Polyimide powder thus obtained was 4.71 kg (98 % yield). The polyimide powder had an inherent viscosity of 0.55 d ℓ/g, Tg of 240 °C, and a 5 % weight loss temperature of 218°C. Synthetic Example 17 Polyimide was prepared by carrying out the same procedures as described in Synthetic Example 14 except that 2.15 kg (9.85 mol) of pyromellitic dianhydride, 44.4 g (0.3 mole) of phthalic anhydride was replaced by 2.21 kg (10.15 mols) of pyromellitic dianhydride, 27.9 g (0.3 mols) of aniline. Polyimide powder thus obtained was 5.35 kg (98.5 % yield). The polyimide powder had an inherent viscosity of 0.79 d ℓ/g, Tg of 235 °C, and a 5 % weight loss temperature of 550°C. Examples 1 ∼ 6 The polyimide powder obtained in Synthetic Example 1 or 2 was dry-blended with the polyimide powder obtained in Synthetic Example 4 for improving melt flowability in various proportions illustrated in Table 1. Melt viscosity of the mixture was measured at 420°C . Results are illustrated in Table 1 together with the 5 % weight loss temperature of the strand obtained. Comparative Examples 1∼ 4 The same procedures as described in Examples 1∼6 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 1. Examples 7 ∼ 9 Polyimide powder obtained in Synthetic Example 3 was dry blended with polyimide powder obtained in Synthetic Example 4 for improving melt flowability in various proportions illustrated in Table 2. Melt viscosity of the mixture was measured at 420 °C at 5-minute residence and 30-minute residence. Results are summarized in Table 2. Comparative Example 5 The same procedures as described in Examples 7∼9 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 2. Examples 10 ∼ 15 The polyimide powder obtained in Synthetic Example 1 or 2 was dry-blended with the polyimide powder obtained in Synthetic Example 5 for improving melt flowability in various proportions illustrated in Table 3. Melt viscosity of the mixture was measured at 420 °C. Results are illustrated in Table 3 together with the 5 % weight loss temperature of the strand obtained. Comparative Examples 6 ∼ 9 The same procedures as described in Examples 10 ∼ 15 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 3. Example 16∼18 Polyimide powder obtained in Synthetic Example 3 was dry blended with polyimide powder obtained in Synthetic Example 5 for improving melt flowability in various proportions illustrated in Table 4. Melt viscosity of the mixture was measured at 420°C at 5-minute residence and 30-minute residence. Results are illustrated in Table 4. Comparative Example 10 The same procedures as described in Examples 16 ∼18 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 4. Examples 19 ∼ 24 The polyimide powder obtained in Synthetic Example 1 or 2 was dry blended with the polyimide powder obtained in Synthetic Example 6 for improving melt flowability in various proportions illustrated in Table 5. Melt viscosity of the mixture was measured at 420 °C. Results are illustrated in Table 5 together with the 5 % weight loss temperature of the strand obtained. Comparative Examples 11 ∼14 The same procedures as described in Examples 19 ∼ 24 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 5. Examples 25 ∼ 27 Polyimide powder obtained in Synthetic Example 3 was dry blended with polyimide powder obtained in Synthetic Example 6 for improving melt flowability in various proportions illustrated in Table 6. Melt viscosity of the mixture was measured at 420 °C at 5-minute residence and 30-minute residence. Results are illustrated in Table 6. Comparative Example 15 The same procedures as described in Examples 25 ∼ 27 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 6. Examples 28 ∼ 33 The polyimide powder obtained in Synthetic Example 7, 8, or 9 was dry-blended with the polyimide powder obtained in Synthetic Example 6 for improving melt flowability in various proportions illustrated in Table 7. Melt viscosity of the mixture was measured at 420 °C. Results are illustrated in Table 7 together with the 5 % weight loss temperature of the strand obtained. Comparative Examples 16 ∼ 21 The same procedures as described in Examples 28 ∼ 33 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 7. Examples 34 ∼ 35 Polyimide powder obtained in Synthetic Example 10 was dry blended with polyimide powder obtained in Synthetic Example 6 for improving melt flowability in various proportions illustrated in Table 8. Melt viscosity of the mixture was measured at 360°C Results are illustrated in Table 8 together with the 5% weight loss temperature of the strand obtained. Comparative Example 22 The same procedures as described in Examples 34 ∼ 35 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 8. Examples 36 ∼ 41 The polyimide powder obtained in Synthetic Example 1 or 2 was dry-blended with polyether pyridine powder obtained in Synthetic Example 11 in various proportions illustrated in Table 9. Melt viscosity of the mixture was measured at 420 °C. Results are illustrated in Table 9 together with the 5 % weight loss temperature of the strand obtained. Comparative Examples 23 ∼ 26 The same procedures as described in Examples 36 ∼ 41 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 9. Examples 42 ∼ 44 Polyimide powder obtained in Synthetic Example 3 was dry blended with polyether pyridine powder obtained in Synthetic Example 12 in various proportions illustrated in Table 10. Melt viscosity of the mixture was measured at 420 °C at 5-minute residence and 30-minute residence. Results are illustrated in Table 10. Comparative Examples 27 ∼ 28 The same procedures as described in Examples 42 ∼ 44 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 10. Examples 45 ∼ 54 The polyimide powder obtained in Synthetic Example 7, 8, 9 or 10 was dry-blended with polyether pyridine powder obtained in Synthetic Example 11 in various proportions illustrated in Table 11. Melt viscosity of the mixture was measured at 420 °C. Results are illustrated in Table 11 together with the 5 % weight loss temperature of the strand obtained. Comparative Examples 29 ∼ 35 The same procedures as described in Examples 45 ∼ 54 were carried out by using compositions outside the scope of the invention. Results are illustrated in Table 11. Examples 55 ∼ 59 Polyimide powder obtained in Synthetic Example 4.5 or 6, or polyether pyridine powder obtained in Synthetic Example 11 or 12 was dry blended with polyimide powder obtained in Synthetic Example 1 or 3 in various proportions illustrated in Table 12. To 70 parts by weight of the resulting mixture, 30 parts by weight of carbon fiber HTA-C6 (manufactured by TOHO RAYAON CO.) were added, mixed with a drum blender (manufactured by KAWATA SEISAKUSHO Co.) and successively melt-kneaded at 400 °C with a single screw extruder having a diameter of 30 mm. The delivered strand was air cooled and cut into pellets. The pellets thus obtained were injection molded with an Arburg injection molding machine at the injection pressure of 500 kg/cm 2 , cylinder temperature of 410 °C and mold temperature of 180°C to obtain tensile specimens. The number of repeating times to fatigue was measured by using these specimens in accordance with JIS K-7118. Results are illustrated in Table 12. Comparative Example 36 Only the polyimide powder obtained in Synthetic Example 1 was blended with carbon fiber by the same procedures as carried out in Examples 55∼ 59 and similarly injection molded to obtain test specimens. The number of repeating times to fatigue was measured. Results are illustrated in Table 12. These specimens had a low repeating number to fatigue of 1.5×10 5 times at the maximum vibrational stress of 12 kg/mm 2 Comparative Example 37 Only the polyimide powder obtained in Synthetic Example 3 was blended with carbon fiber by the same procedures as carried out in Examples 55∼ 59 and injection molding was similarly tried. However, injection molded specimen could not be obtained because melt viscosity was too high. Examples 60 ∼ 64 Polyimide powder obtained in Synthetic Example 4, 5 or 6, or polyether pyridine powder obtained in Synthetic Example 11 or 12 was dry blended with polyimide powder obtained in Synthetic Example 13 in proportions illustrated in Table 13. The mixture was melt-kneaded at 400 °C with a single screw extruder having a diameter of 30 mm. The delivered strand was air cooled and cut into pellets. The pellets thus obtained was injection molded at the injection pressure of 500 kg/cm 2 , cylinder temperature of 410°C and mold temperature of 180°C to obtain various test specimens. Tensile strength elongation at break, flexural strength, flexural modulus, Izod impact strength and heat distortion temperature were measured by using these specimens. Comparative Example 38 Polyimide powder obtained in Synthetic Example 1 was injection molded by carrying out the same procedures as described in Examples 60 ∼ 64. Various mechanical properties were measured by using specimens thus obtained. Results are shown in Table 13. Comparative Example 39 Polyimide powder obtained in Synthetic Example 13 was tried to carry out injection molding by the same procedures as described in Examples 60 ∼ 64. However, injection molding was impossible and specimens could not be obtained. Examples 65 ∼ 67 To 70 parts by weight of Polyimide powder obtained in Synthetic Example 14, 30 parts by weight of carbon fiber HTA-C6 (manufactured by TOHO RAYAON CO.) were added, mixed with a drum blender (manufactured by KAWATA SEISAKUSHO Co.) and successively melt-kneaded at 400°C with a single screw extruder having a diameter of 30 mm. The delivered strand was air cooled and cut into pellets. The pellets thus obtained were injection molded with an Arburg injection molding machine at the injection pressure of 500 kg/cm 2 , cylinder temperature of 410 °C and mold temperature of 180°C to obtain tensile specimens. The number of repeating times to fatigue was measured by using these specimens in accordance with JIS K-7118. Results are illustrated in Table 14. Examples 68 ∼ 70 Only the polyimide powder obtained in Synthetic Example 15 was blended with carbon fiber by the same procedures as carried out in Examples 65 ∼67 and similarly injection molded to obtain test specimens. The number of repeating times to fatigue was measured. Results are illustrated in Table 14. Comparative Examples 40 ∼42 Only the polyimide powder obtained in Synthetic Example 16 was blended with carbon fiber by the same procedures as carried out in Examples 65 ∼67 and similarly injection molded to obtain test specimens. The number of repeating times to fatigue was measured. Results are illustrated in Table 14. Examples 71 ∼ 73 Only the polyimide powder obtained in Synthetic Example 17 was blended with carbon fiber by the same procedures as carried out in Examples 65 ∼67 and similarly injection molded to obtain test specimens. The number of repeating times to fatigue was measured. Results are illustrated in Table 14.

Claims: A polyimide resin composition comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1) : wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an aliphatic radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼ 50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (2) : wherein R 1 is a tetravalent radical represented by or a polyimide comprising a requisite structural unit consisting of one or more recurring structural units the formula (3) : wherein R 2 is a tetravalent radical represented by and/or polyether pyridine comprising a requisite structural unit consisting of one or more recurring structural units of the formula (4) : wherein Y is a divalent radical represented by A polyimide resin composition according to claim 1 comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1): wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an aliphatic radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼ 50 parts by weight of polyimide having recurring structural units of the formula (5) : A polyimide resin composition according to claim 1 comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1): wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an alkyl radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼ 50 parts by weight of polyimide having recurring structural units of the formula (6) : A polyimide resin composition according to claim 1 comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1): wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an alkyl radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼ 50 parts by weight of polyimide having recurring structural units of the formula (7) A polyimide resin composition according to claim 1 comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1): wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an alkyl radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼ 50 parts by weight of polyimide having recurring structural units of the formula (8) A polyimide resin composition according to claim 1 comprising 99.9∼50 parts by weight of polyimide comprising a requisite structural unit consisting of one or more recurring structural units of the formula (1): wherein X is a radical selected from the group consisting of a direct bond, isopropylidene, hexafluoroisopropylidene, carbonyl, thio and sulfonyl, and R is a tetravalent radical having 2∼27 carbon atoms and being selected from the group consisting of an alkyl radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and 0.1∼ 50 parts by weight of polyether pyridine comprising a requisite structural unit consisting of one or more recurring structural units of the formula (4) wherein Y is a divalent radical represented by A polyimide resin composition of claim 1, 2, 3, 4, or 5 wherein the polyimide having recurring structural units of the formula (1), (2) , (3), (5), (6), (7) or (8) comprises an end-capped polymer obtained by preparing said polyimide in the presence of aromatic dicarboxylic anhydride represented by the formula (9): wherein Z is a divalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or aromatic monoamine represented by the formula (10) : V - NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. A polyimide copolymer obtainable by reacting 0.5 to 0.95 mole of diamine represented by the formula (11) and 0.5 to 0.05 mole of diamine represented by the formula (13): with tetracarboxylic dianhydride represented by the formula (12): wherein R is a tetravalent radical having 2 ∼27 carbon atoms and being selected from the group consisting of an alkyl radical, alicyclic radical, monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. A polyimide copolymer of claim 8 wherein the diamine of the formula (11) is 4,4-bis(3-aminophenoxy)biphenyl and the tetracarboxylic dianhydride of the formula (12) is pyromellitic dianhydride and/or biphenyltetracarboxylic dianhydride. A polyimide copolymer of claim 8 or 9 wherein the polyimide copolymer comprises an end-capped polymer obtained by preparing said polyimide in the presence of aromatic dicarboxylic anhydride represented by the formula (9) : wherein Z is a divalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member, and/or aromatic monoamine represented by the formula (10): V - NH 2 wherein V is a monovalent radical having 6∼15 carbon atoms and being selected from the group consisting of a monoaromatic radical, condensed polyaromatic radical and noncondensed aromatic radical connected to each other with a direct bond or a bridge member. A polyimide based resin composition comprising 100 parts by weight of the polyimide resin composition of any of claims 1 ∼ 6 or the polyimide copolymer of any of claims 7 ∼ 10 and 5 to 65 parts by weight of a fibrous reinforcement. A polyimide based resin composition of claim 11 wherein the fibrous reinforcement is carbon fiber, glass fiber aromatic polyamide fiber or potassium titanate fiber.

Inventors: ASANUMA TADASHI, MATSUO MITSUNORI, OIKAWA HIDEAKI, OKAWA YUICHI, SAKATA YOSHIHIRO, TAMAI SHOJI, YAMAGUCHI AKIHIRO, YAMAGUCHI KEIZABURO, YAMASHITA WATARU, ASANUMA, TADASHI, MATSUO, MITSUNORI, OIKAWA, HIDEAKI, OKAWA, YUICHI, SAKATA, YOSHIHIRO, TAMAI, SHOJI, YAMAGUCHI, AKIHIRO, YAMAGUCHI, KEIZABURO, YAMASHITA, WATARU, OIKAWA, HIDEAKI, 3-42-7 HIRADO, OKAWA, YUICHI, 1-22 MITSUI TOATSU AP, SAKATA, YOSHIHIRO, 214 MITSUI TOATSU KAGAKU, TAMAI, SHOJI, 2-17 MITSUI TOATSU AP, YAMASHITA, WATARU, 311 MITSUI TOATSU KAGAKU
Applicants: MITSUI TOATSU CHEMICALS, MITSUI TOATSU CHEMICALS, INC.
Application year: 1994
Main classification: C08L79
IPC codes: C08G73, C08L79, C08L71