Composite material for sliding purposes, process for its preparation and use thereof

Abstract: The invention discloses a long carbon fibre reinforced ceramic matrix composite in which the matrix is an engineering ceramic, characterised in that the engineering ceramic comprises Al₂O₃ and Y₂O₃ as highly refractory sinter additives, the composite has a high density of at least 95% theoretical, a high fibre content of at least 30% by volume, and that substantially all the fibres are uniformly distributed within the matrix with a uniform inter-fibre spacing of 10-15 micrometer. The invention also discloses a process for preparing such a composite, characterised in that unidirectionally wound fibre tapes are cut into sections, the sections are infiltrated by the matrix material in the form of a slurry of the ceramic itself or as a precursor material, the infiltrated fibre tape sections are successively stacked and pressed wet to achieve intermeshing of the tape sections, compacted, dried and hot pressed. The invention also relates to the use of said composite as a self-lubricating material for dry sliding applications, especially on metals.

Description: The present invention relates to a long carbon fibre reinforced ceramic matrix composite, a process for manufacturing the same, and the use of bodies of said composite for applications requiring low wear and friction properties. Ceramics are attractive candidate materials for wear applications owing to their excellent properties of thermal stability, high elasticity, hardness, resistance to chemical corrosion and low inertia. Monolithic oxide, nitride and carbide ceramics, as Al 2 O 3 , ZrO 2 , Si 3 N 4 , SiC and other have been recognised as potential materials for use in strucural applications such as seal rings, valve seats, dies for extrusion, guides, valve tram components bearing parts of cylinder liners (Czichos H, Woydt M, KLaffke D and Lexow J, Materiaux et Techniques, 1989). The major shortcoming of the materials is their low fracture toughness, resulting in inherently brittle components. In recent years considerable effort has been devoted world-wide to improving ceramic fracture toughness, primarily for structural engineering applications, by incorporating additional phases into the base materials generally in the form of fibres, whiskers or particles (Evans A G and Cannon R M, Acta Metall 34 (1986) 761). Very few studies have considered the development of Ceramic Matrix Composite (CMC) materials for tribological applications and most of these are focused to whisker re-inforced ceramics (Yust C S, Leitnaker J M and Devore C E, Wear 122 (1988) 156, Yust C S and Devore C E, Tribol Trans 34 (1991), Liu H, F E M E and Cheng H S, J. Am Ceram Soc 74 (1991) 2224). Nevertheless, the improvement of fracture toughness of ceramics designed for wear applications is of considerable industrial importance and the tailoring of the combined properties of the component phases offers an excellent opportunity to optimise the frictional and wear properties of the composite. Kodama et al, Journal of America Chemical Society 72 [4] pp. 551-558 (1989) disclose SiC monofilament reinforced SiC or Si 3 N 4 matrix composites produced by hot-pressing. The SiC and Si 3 N 4 matrix materials comprises Y 2 O 3 /Al 2 O 3 or AlN 3 sinter additives respectively. The SiC fibre content is 15 vol %. The fracture toughness of a Si 3 N 4 matrix composite is studied. Wear and friction properties are not disclosed. International application WO 93/20024 disclose a method of manufacturing fibre reinforced composites, wherein a fibre material is infiltrated with matrix material to preform a green body, the preformed green body is encapsulated and the encapsulated green body is consolidated and sintered. Examples of matrix materials include ceramic materials such as Si 3 N 4 , SiC, Al 2 O 3 , mullite, Y 2 O 3 and metallic materials. Examples of the fibrous material include carbon fibres. An example of a composite comprising Si 3 N 4 /Al 2 O/Y 2 O 3 matrix and carbon fibres is given. Fibre content and density are not disclosed. Wear and fraction properties are not mentioned. Sato et al., Journal of the Ceramic Society of Japan, Int. Ed. 100 (1992) pp. 450-453, disclose the use of a perhydropolysilazane which is converted to a silicon nitride matrix, as a matrix precursor. Carbon fibre reinforced Si 3 N 4 composites are prepared by infiltrating a carbon strand with the polysilazane, winding the infiltrated strand on a mandrell to obtain a unidirectional fibre aligned preform, pressing and curing the preform, cutting the preform in plates and firing the plates. To obtain a dense product the procedure is repeated. A density of 96% is obtained. Wear and friction properties are not disclosed. Wear damage in ceramic-metal couples in dry sliding conditions arises from mechanical and tribo-chemical interactions between the touching faces. Mechanical abrasive wear results from impact fracture of microscale features of the ceramic and the physical removal of particles from the ceramic surface. These particles may become trapped between the wear surfaces and further contribute to wear damage of the couple. Tribo-chemical, adhesive, wear arises from cold welding of asperity junctions in the contact faces. Further sliding leads to the fracture of these junctions in one or other of the contacting materials. In the case of ceramic/metal pairs, adhesive wear can result from high local surface temperatures. The location of the subsequent fracture will depend upon the particular materials involved. The intrinsic strength of engineering ceramic materials confers a high degree of wear resistance and unless the ceramic exhibits weakness or brittleness in the microscale of the weld zone, then the wear debris will contain a reasonable proportion of metallic component. Such debris can re-adhere to the contacting surfaces leading to the formation of an adherent transfer film of metal on the ceramic. Subsequent contact with the metal counter body may then lead to adhesive wear as the bulk metal adheres to the transfer film. The object of the invention is to reduce wear damage in these systems by reducing the propensity to brittle fracture by increasing fracture toughness, reducing crack initiating flaws, macrodefects etc., and by reducing tribo-chemical interaction. Now we have found that by impregnating unidirectionally wound tape consisting of long carbon fibres with an appropriate matrix material using a special process route dense, composites having a low brittleness, a reduced tribo-chemical interaction and excellent wear and friction properties can be obtained. Accordingly the invention provides a long carbon fibre reinforced ceramic matrix composite comprising long carbon fibres and a matrix of an Si 3 N 4 or SiC engineering ceramic wherein the Si 3 N 4 or SiC engineering ceramic comprises Al 2 O 3 and Y 2 O 3 as highly refractory sinter additives, the composite having a high density of at least 95% theoretically, a high fibre content of at least 30% by volume, substantially all the fibres being uniformly distributed within the matrix with a uniform inter-fibre spacing of 10-15 µm. In another aspect the invention provides a process for preparing a long carbon fibre reinforced ceramic matrix composite characterized in that unidirectionally wound fibre tapes are cut into sections, the sections are infiltrated by the matrix material in the form of a slurry of the ceramic itself or as a precursor material, the infiltrated fibre tape sections are successively stacked and pressed wet to achieve intermeshing of the tape sections, compacted, dried and hot pressed. In yet another aspect the invention provides the use of a long carbon fibre reinforced ceramic matrix composite as a self-lubricating material for dry sliding applications, especially on metals. The fabrication of a dense long-fibre ceramic composite can be achieved only by high temperature sintering. For composites of high fibre content, high density composite fabrication also requires the application of pressure at sintering temperatures. The compromise between on the one hand, the desired features of high total fibre content, the uniform distribution of fibres within the matrix, the complete infiltration of the matrix to eliminate the intrinsic flaws and macrodefects, and on the other the cost of processing, is difficult to realise. All fabrication routes depend upon the infiltration of fibre weaves by matrix material, in the form of the ceramic itself or as a precursor material which may be later pyrolysed to the ceramic. The process of the invention comprises liquid infiltration by ceramic dispersions (slurries), which is the cleanest and simplest method of forming green bodies. Densities of ca. 70% can be achieved in green bodies which contain minimum quantities of polymer additives which will need to be burned out during subsequent pressure sintering. The final composite should ideally have a maximum fibre content with a uniform inter fibre spacing of ca. 10-15 µm fully infiltrated by the ceramic matrix. Optimum slurry infiltration of all filaments in the fibre weave demands a careful balance between the processing parameters. Examples are: the ceramic dispersion itself should balance a maximum solid content to obtain high green density and minimum flaw inclusion, against a low viscosity adequate to allow ingress between all filaments. The application of external pressure while promoting bulk ingress tends to compress fibres together, inhibiting infiltration of tightly woven filament bunches. Inadequate pressing of the wet green form leaves large pockets and lamellae of monolithic ceramic which provides sites of low fracture toughness in the final ceramic. During the pressure sintering, the timing of application of pressure is crucial to minimise chemical degradation of the chemical species, while not damaging the fibres. To achieve the required characteristics of the composite the fibres selected are high elastic modulus carbon fibres fabricated from meso-pitch precursors. These high stiffness fibres confer improved fracture toughness on the supporting ceramic while the high carbon content of the composite promotes the development of a graphitic lubricating debris during wear. The fibre content of the composite is at least 30 % by volume and preferably 35 %. The fibres are entrained within a high strength engineering ceramic matrix. The matrix material is a non-oxide ceramic, selected from Si 3 N 4 and SiC. The matrix comprises Al 2 O 3 and Y 2 O 3 , preferably in a content range of 2.5-3.5 and 7.5-6.5 wt % of matrix weight respectively. The composite is prepared by the spreading and winding of fibre tows into uniaxial tapes of two layers in which the individual filaments are closely parallel, the development of an aqueous ceramic dispersion of 65 wt % solid content containing a dispersant, preferably up to 0.2 wt % of solids weight, and/or a wetting agent, preferably up to 2.0 wt % of liquids, to obtain optimal viscosity and wetting conditions to allow full infiltration of fibre tape sections and spreading of fibre bunches to ensure penetration of the ceramic dispersion between all fibre filaments, and minimisation to approaching zero of areas of non-infiltration porosity, infiltrating of the spread and wound double layers, uniaxial fibre types with the aqueous ceramic slurry, both with and without ultrasonic agitation, successive stacking of infiltrated fibre tape sections and pressing with a ridged plate to promote interweaving of fibre filaments and minimise areas of residual monolithic ceramic, squeeze pressing of the final tape-section stack to obtain an optimised ration of fibre to matrix, and hot pressing the dried stack to a full density of at least 95 % theoretical and preferably 98-99 %. The hotpressing is preferably carried out at a temperature of 1750 to 1950 °C and a pressure up to 30 MPa. The final ceramic microstructure contains a maximum fibre volume content in which the individual fibre filaments are uniformly dispersed within the ceramic, as far as is allowed by the requirement to create a fully dense composite with a minimum population of internal macrodefects, either by cracking or porosity. The composite demonstrates superior friction/wear properties as compared to a corresponding monolithic ceramic and to a composite fabricated by a traditional slurry infiltration and hot pressing technique. The invention is now illustrated in more detail in the following example. EXAMPLE: Carbon Fibre - Silicon Nitride Composite Fibre preforms are prepared by winding a high modulus carbon fibre tow (TONEN FT 500), containing 3000 filaments, on to an octagonal mandrel (see Fig. 1). The filaments are uniformly spread during winding using a spreading device, yielding thin 55 mm width tapes. Two layers are applied per tape keeping the filaments of each layer parallel with the other. The double layer tapes are then divided into sections by pressure application of glue strips across the tapes on the mandrel at 120 mm lengths. The sections are cut and removed from the mandrel. The fibre tape sections are clamped and immersed in an aqueous ceramic slurry containing silicon nitride powder (SN-E-10) with the addition of 6.9 wt % aluminium oxide (source) and 3.1 wt % yttrium oxide (source) as sinter aids. The slurry is prepared by attrition milling an aqueous dispersion of the powders at 65 wt % solid content for 2 hours using the commercial dispersant Darvan C (0.2 wt % solid content) at 13°C. Following milling, the dispersion pH was adjusted to 10.5 using tetramethyl ammonium hydroxide. To the dispersion was added a fibre wetting agent Aerosol OT (1 wt % weight of water) and the dispersion degassed while stirring continuously for 24 hours before use. The slurry viscosity at time of infiltration is (45 cps) 45 MPa.s (128 s -1 shear rate). Infiltration of the fibres was achieved by vertical and/or horizontal immersion of the fibre tape sections in the slurry for 2 minutes under ultrasonic agitation. The sections are then removed from the slurry and stacked horizontally maintaining the parallelity of the fibres on to a flat plaster mould covered with a 149µm (100 mesh) filter cloth. Each successive tape section is pressed into the stack using a ridged grid, in order to promote intermeshing of the filaments between the successive layers, the elimination of layers of monolithic ceramic, and to squeeze out trapped air bubbles. 15 tape sections are stacked per sample yielding a 30 ply composite plate. The infiltrated tape stacks are then covered with a 149µm (100 mesh) filter cloth and a porous metal grid and are squeeze pressed to 6 mm thickness to achieve the optimum ratio of fibre to matrix content. Sample plates are dried for 3 hours under pressure cut to 45 x 45 mm plates and dried over 48 hours at room temperature and then fully dried by heating to 400°C/min, holding for 1 hour and recooling at 8°C per minute, to yield a green density of some 70% theoretical. The samples were densified by hot pressing at 1750°C for 2 hours at 27 MPA axial pressure in a nitrogen gas overpressure of 1 bar. The temperature and pressure cycle are shown in fig. 2. The application of mechanical and gas pressure was designed to cause minimum damage to the fibres while the ceramic was below sinter temperatures, while preventing decomposition of silicon nitride at higher temperatures. The final composite has a uniformly distributed fibre content of 35% and a density of ca 98-99 % theoretical and no visible macroporosity. Samples for wear and friction testing were prepared by cutting prismatic specimens (3 x 3 x 20 mm 3 ) from the composite plates and from a commercial hot pressed silicon nitride (Ceralloy). One end of each pin was rounded to a radius of curvature of 3 mm and polished in a hemispherical mould with diamond compounds to a final surface roughness of 12 µm R a for the monolithic ceramics and 13 µm R a for the composites. The counter-face discs were manufactured from a standard 100Cr6 steel. The discs were finished to a surface roughness of 0.15 R a . Prior to testing, both flat and pin specimens were ultrasonically cleaned in acetone. Tests were conducted using a pin-on-disk type arrangement. The pin was clamped in a holder arm, which was pivoted to allow normal loading and friction measurements. The pin was mounted in the specimen holder with the fibres perpendicular to the counterface. The test parameters are given in Table 1. In all tests the frictional force was continuously recorded by means of a strain-gauge device. Figure 3 shows the variation of friction coefficient (µ) with sliding distance for the combinations studied. In all cases test indicated in initial period, sometimes up to 200m, in which the friction coefficient changed considerably which was followed by a steady state of nearly constant friction value. The final friction and wear values of the various material combinations are shown in Table 2. These are the values taken at the end of each test. The friction and wear results from the composite pins are strongly dependent upon the quality of the C/Si 3 N 4 composite. The composites prepared by the process of the invention - labelled good composite - were compared with the material prepared using a less rigorous literature-reported (Prewo K M, Brennan J J and Layden H K (1986) Fiber reinforced glasses and gla-ceramics for high performance applications, Am. Ceram. Soc. Bull., 65, 305-322) slurry infiltration technique. These "poor" composite structures contain some fibre bunching in which the matrix walls between fibres are sometimes thin, and where occasionally the matrix is not fully infiltrated leaving small pores. The sliding surfaces of the pin and the disc were analysed by SEM/EDS after testing. The friction coefficient profiles for the monolithic Si 3 N 4 on 100Cr6 show a typical build up of a debris layer by adhesive wear. The debris adheres to the disc and acts as a constant source of interfacial fine powder leading to a steady state abrasive process, involving the recirculation of a non-adherent mixture of amorphous metal and ceramic particles, the majority of which is dumped ahead of the leading edge of the pin. For the composite pins the initial friction coefficient goes through a distinct peak associated with the development of a steady state debris layer by adhesive wear mechanisms. The "good" and "poor" composites show rather different behaviour. The "good" composites have a homogeneous distribution of fibres. The pin surfaces remain virtually completely clean of adherent deposit and no craters are formed on the pin surface. Since the adhesion between graphite and iron is relatively poor it is assumed that silicon nitride from the composite pin is transferred to the steel disk. The initial friction is probably due to the adhesion between the matrix composite and the steel disk. This adhesion is gradually decreased by the formation of a Si(nitride)-Fe-C powder film at the interface. In steady state the film is thick enough to reduce adhesion and to confer some degree of lubrication. The improvement of the lubrication of the debris mix is confirmed by the dramatic reduction in steady state friction coefficient from 0.65 for the monolithic Si 3 N 4 to 0.12 for the composite. The "poor" composite pins are rapidly covered by an adherent layer during the initial friction coefficient peak, which is then retained for the lifetime of the test. The formation of the adherent layer, in the initial stage of wear, takes place at defects, created either by areas of incomplete infiltration of the fibre preform or by fracture in the thin matrix walls surrounding the fibres in the fibre bunches. These defects can be found in areas where the volume content of fibre is very high.

Claims: A long carbon fibre reinforced ceramic matrix composite comprising long carbon fibres and a matrix of an Si 3 N 4 or SiC engineering ceramic, wherein the Si 3 N 4 or SiC engineering ceramic comprises Al 2 O 3 and Y 2 O 3 as highly refractory sinter additives, the composite having a high density of at least 95% theoretical, a high fibre content of at least 30% by volume, substantially all the fibres being uniformly distributed within the matrix with a uniform inter-fibre spacing of 10-15 µm. A composite according to claim 1, characterised in that the fibres are high elastic modulus carbon fibres. A composite according to claim 1, characterized in that the content of Al 2 O 3 is in the range of 2.5-3.5 wt % and the content of Y 2 O 3 is in the range of 7.5-6.5 wt % of solids weight. A composite according to any of the preceding claims, characterised in that the density of the composite is at least 98% theoretical. A composite according to any of the preceding claims, characterised in that the fibre content is at least 35% by volume. A process for preparing a composite as defined in any of the claims 1-5, characterised in that unidirectionally wound fibre tapes are cut into sections, the sections are infiltrated by the matrix material in the form of a slurry of the ceramic itself or as a precursor material, the infiltrated fibre tape sections are successively stacked and pressed wet to achieve intermeshing of the tape sections, compacted, dried and hot pressed. A process according to claim 6, characterised in that the unidirectionally wound fibre tapes comprise two layers in which the filaments are closely parallel. A process according to any of the claims 6 and 7, characterised in that the slurry has a solid content of at least 65 wt %. A process according to any of the claims 6-8 characterised in that the slurry contains a dispersant and/or a wetting agent. A process according to claim 9, characterised in that the content of the dispersant is up to 0.2 wt % of solids weight. A process according to claim 9, characterised in that the content of the wetting agent is up to 2.0 wt % of liquids. A process according to any of the claims 6-11, characterized in that the slurry is prepared under attrition milling. A process according to any of the claims 6-12, characterised in that the tape sections are infiltrated under ultasonic agitation. A process according to any of the claims 6-14, characterized in that the hotpressing is carried out at 1750 - 1950 °C and a pressure up to 30 MPa. Use of a composite as defined in any of the claims 1-5 as a self-lubricating material for dry sliding applications, especially on metals.

Inventors: BULLOCK EDWARD, VEYRET JEAN-BERNARD, BULLOCK, EDWARD, VEYRET, JEAN-BERNARD
Applicants: EURATOM, EUROPEAN ATOMIC ENERGY COMMUNITY (EURATOM)
Application year: 1994
Main classification: C04B35
IPC codes: C04B35