Naphthalene alkylation process using mixed H/NH3 form catalyst

Abstract: Long chain alkyl substituted naphthalenes are produced by alkylating naphthalene with an olefin or other alkylating agent with at least 6, and usually 12 to 20 carbon atoms, in the presence of an alkylation catalyst comprising zeolite Y having both ammonium and protonic species associated with its exchangeable sites. The presence of both ammonium and protonic species increases selectivity for production of long chain mono-alkyl substituted naphthalenes in preference to more highly substituted products.

Description: This invention relates to the production of alkylated naphthalenes and substituted naphthalenes. Alkylaromatic fluids have been proposed for use as certain types of functional fluids where good thermal and oxidative properties are required. For example, US Patent No. 4,714,794 (Yoshida) describes the monoalkylated naphthalenes as having excellent thermal and oxidative stability, low vapor pressure and flash point, good fluidity and high heat transfer capacity and other properties which render them suitable for use as thermal medium oils. The use of a mixture of monoalkylated and polyalkylated naphthalenes as a base for synthetic functional fluids is described in US Patent No. 4,604,491 (Dressler) and Pellegrini US 4,211,665 and 4,238,343 describe the use of alkylaromatics as transformer oils. The alkylated naphthalenes are usually produced by the alkylation of naphthalene or a substituted naphthalene in the presence of an acidic alkylation catalyst such as a Friedel-Crafts catalyst, for example, an acidic clay as described in Yoshida US 4,714,794 or Dressier US 4,604,491 or a Lewis acid such as aluminum trichloride as described in Pellegrini US 4,211,665 and 4,238,343. The-use of a catalyst described as a collapsed silica-alumina zeolite as the catalyst for the alkylation of aromatics such as naphthalene is disclosed in Boucher US 4,570,027. The use of various zeolites including intermediate pore size zeolites such as ZSM-5 and large pore size zeolites such as zeolite L and ZSM-4 for the alkylation of various monocyclic aromatics such as benzene is disclosed in Young US 4,301,316. In the formulation of functional fluids based on the alkyl naphthalenes, it has been found that the preferred alkyl naphthalenes are the mono-substituted naphthalenes since they provide the best combination of properties in the finished product: because the mono-alkylated naphthalenes possess fewer benzylic hydrogens than the corresponding di-substituted or polysubstituted versions, they have better oxidative stability and therefore form better functional fluids and additives. In addition, the mono-substituted naphthalenes have a kinematic viscosity in the desirable range of 5-8 mm 2 /s (at 100°C) when working with alkyl substituents of 14 to 18 carbon atoms chain length. Although the mono-alkylated naphthalenes may be obtained in admixture with more highly alkylated naphthalenes using conventional Friedel-Grafts catalysts such as those mentioned above or by the use of zeolites such as USY, the selectivity to the desired mono-alkylated naphthalenes is not as high as desired. Several recent advances have been made in this area which improve the yields of the desired mono-alkylated naphthenes. US 5,034,563, Ashjian et al, teaches use of a zeolite containing a bulky cation. The use of, e.g., USY with cations having a radius of at least 25 nm (2.5 Angstroms) increases selectivity for desired products. Taught as suitable were zeolites containing hydrated cations of metals of Group IA, divalent cations, especially of Group IIA, and cations of the Rare Earths. The patent had examples in which H, NH4, Na were added to USY zeolite by a procedure involving forming a slurry of zeolite and liquid, 1 hour of stirring, decantation, and a repeat of the exchange procedure. US 5,177,284, Le et al, discusses the desirable properties of alkylated naphthalene fluids with higher alpha:beta ratios, including improved thermal and oxidative stability. Le et al found that several parameters influenced the alpha:beta ratio of the alkylated naphthalene products, including steaming the zeolite, lowering the alkylation temperature, or use of acid-treated clay. Steamed USY catalyst gave excellent results in the examples. The patentees also mentioned use of zeolites with reduced activity due to base exchange, alkaline earth ion exchange and use of boron-zeolite beta. US 5,191,135, Dwyer et al, discloses the effect of co-feeding water for this reaction when using a large pore zeolite catalyst, such as zeolite Y. Adding from 1-3 wt% water to the feed improved the alkylation reaction, a result attributed to suppression of zeolite acid site activity. US 5,191,134, Le, discloses a similar alkylation process using MCM-41. The present inventors did additional work to see if this alkylation process can be improved. They wanted to increase the efficiency of the reaction both in terms of conversion and yields. It was found that a catalyst containing a roughly 50/50 (molar basis) of NH4 and H gave unexpectedly superior results. Phrased another way, catalyst which was exchanged with ammonia, and then only about half calcined, gave better results than catalyst which was wholly in the ammonium form, or wholly calcined to be in the protonic form. An effective way of preparing the catalyst was found to be to ammonium exchange the zeolite completely and then to calcine it at 300 to 400°C for a time sufficient to remove from 45 to 60% of the ammonia. Although the performance of the catalyst could be still further improved by the incorporation of rare earths, excellent catalyst with essentially no rare earths present can be prepared. Accordingly, the present invention provides a process for preparing long chain alkyl substituted naphthalenes which comprises alkylating a naphthalene with an alkylating agent possessing an alkylating aliphatic group having at least six carbon atoms under alkylation reaction conditions in the presence of an alkylation catalyst comprising zeolite Y containing exchangeable sites and both ammonium and protonic species associated with the exchangeable sites, and wherein the ratio of ammonium:protonic species is within the range of 95:5 to 5:95, molar basis, to form an alkylated naphthalene possessing at least one alkyl group derived from the alkylating agent. In a preferred embodiment, the molar ratio of ammonium:protonic species is from 65:35 to 35:65. The starting materials for the production of the alkylated naphthalenes are naphthalene itself as well as the substituted naphthalenes which may contain one or more short chain alkyl groups containing up to eight carbon atoms, such as methyl, ethyl or propyl. Suitable alkyl-substituted naphthalenes include alpha-methylnaphthalene, dimethylnaphthalene and ethylnaphthalene. Naphthalene itself is preferred since the resulting mono-alkylated products have better thermal and oxidative stability than the more highly alkylated materials for the reasons set out above. The alkylating agents which are used to alkylate the naphthalene include any aliphatic or aromatic organic compound having one or more available alkylating aliphatic groups capable of alkylating the naphthalene. The alkylatable group itself should have at least 6 carbon atoms, preferably at least 12 carbon atoms. For the production of functional fluids and additives, the alkyl groups on the alkyl-naphthalene preferably have from 12 to 30 carbon atoms, with particular preference to 14 to 18 carbon atoms. A preferred class of alkylating agents are the olefins with the requisite number of carbon atoms, for example, the hexenes, heptenes, octenes, nonenes, decenes, undecenes, dodecenes. Mixtures of the olefins, e.g. mixtures of C 12 -C 20 or C 14 -C 18 olefins are useful. Branched alkylating agents, especially oligomerized olefins such as the timers, tetramers, pentamers, etc., of light olefins such as ethylene, propylene, the butylenes, etc., are also useful. Other useful alkylating agents which may be used, although less easily, include alcohols (inclusive of monoalcohols, dialcohols, trialcohols, etc.) such as hexanols, heptanols, octanols, nonanols, decanols, undecanols and dodecanols; and alkyl halides such as hexyl chlorides, octyl chlorides, dodecyl chlorides; and higher homologs. Small crystal Y zeolite, in the 0.2 to 0.4 µm range is preferred, although the 0.6 to 1.3 µm material which is more typical of Y zeolite crystals may also be used. It is essential to put the zeolite in a form in which the cation exchange sites contain both ammonium and protonic species. Expressed as % of total ion exchange capacity, the zeolite should contain at least 35% ammonium and at least 35% protonic forms. Preferably, the ammonium and protonic forms each occupy at least 40% of the available sites. Most preferably the ammonium form is 55 to 50% of the available sites, with the protonic form being the remainder. As used herein, the total ion exchange capacity of the catalyst may be determined by the temperature programmed ammonia desorption method described by G.T. Kerr and A.W. Chester in Thermochimica Acta, 3 , 113-124 (1971). This ratio of ammonium to protonic forms may also be expressed in terms of a standardized calcination procedure after ammonium exchange. Thus the zeolite may be placed in the ammonium form using conventional techniques. Typically this involves contacting the zeolite, or catalyst, with 5 vol/vol of 1 N NH4NO3 and stirring for an hour, water washing, another exchange step, and a final wash. The catalyst then may be calcined for 5 hours in flowing air. When this procedure is used, calcining at 400-425°C gives optimum results. The above ratios, of ammonium to protonic forms, hold even if other ions are present. Thus the presence of Rare Earths, discussed below, may reduce the total amount of ammonium and protonic ions present, but will not alter the critical ratio of ammonium:protonic species. RARE EARTH EXCHANGE The selected zeolite catalyst preferably contains a limited amount of one or more of the Rare Earths. Suitable are Y, La and any of the Lanthanum Series of Rare Earths, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu. Especially preferred are Ce, Y and La. In most applications, mixtures of rare earths will be preferred, as these are readily available commercially and much less expensive than purified rare earth elements. The mixed rare earths typically used to produce zeolite Y based cracking catalysts serve well. If the zeolite does not contain the desired amount of rare earths they may be introduced by ion-exchange in the conventional manner using a solution of the exchanging cation. It is preferred to have less than 50% of the total number of exchangeable sites associated with Rare Earths. Preferably less than 35% of the exchangeable sites contain Rare Earths, and most preferably less than about 20% exchange is preferred. Optimum results are seen with 12.5 to 17.5% Rare Earth exchange, ideally with about 15% exchange. Binders may be used to improve crush strength and other physical properties. Suitable materials include naturally occurring clays, e.g. bentonite and kaolin as well as silica, alumina, and mixtures thereof. The relative proportions of zeolite, present in finely divided crystalline form, and oxide matrix may vary widely, with the crystalline zeolite content ranging from 1 to 90% by weight and more usually, particularly when the composite is prepared in the form of beads, in the range of 2 to 80 wt% of the composite. The stability of the alkylation catalyst of the invention may be increased by steaming. US Patent Nos. 4,663,492; 4,594,146; 4,522,929; and 4,429,176 describe conditions for the steam stabilization of zeolite catalysts which can be utilized to steam-stablilze the catalyst. Care should be taken to ensure that steaming conditions are not so severe as to convert too much of the ammonium species to protonic species. The alkylation process of this invention is conducted such that the organic reactants, i.e. the alkylatable aromatic compound and the alkylating agent, are brought into contact with the zeolite catalyst in a suitable reaction zone such as, for example, in a flow reactor containing a fixed bed of the catalyst composition, under effective alkylation conditions. Such conditions typically include a temperature of from 100 to 400°C, a pressure of from 20.3 to 25325 kPa (0.2 to 250 atmospheres), a feed weight hourly space velocity (WHSV) of from 0.1 hr -1 to 10 hr -1 and an alkylatable aromatic compound to alkylating agent mole ratio of from 0.1:1 to 50:1, preferably from 4:1 to 1:4 e.g. from 2:1 to 1:2. The WHSV is based upon the weight of the catalyst composition employed, i.e. the total weight of active catalyst (and binder if present). Preferred reaction conditions include a temperature within the approximate range of from 100 to 350°C, a pressure of from 101 to 2533 kPa (1 to 25 atmospheres), a WHSV of from 0.5 hr -1 to 5 hr -1 and an alkylatable aromatic compound to alkylating agent mole ratio of from 0.5:1 to 5:1. When using naphthalene as the aromatic compound, the pressure should preferably be maintained at a value of at least 448 kPa abs (50 psig) in order to prevent the naphthalene from subliming into the overhead of the alkylation reactor; the required pressure may be maintained by inert gas pressurization, preferably with nitrogen. The reactants can be in either the vapor phase or the liquid phase and can be neat, i.e. free from intentional admixture or dilution with other material, or they can be brought into contact with the zeolite catalyst composition with the aid of carrier gases or diluents such as, for example, hydrogen or nitrogen. The alkylation can be carried out as a batch-type reaction typically employing a closed, pressurized, stirred reactor with an inert gas blanketing system or in a semi-continuous or continuous operation utilizing a fixed or moving bed catalyst system. The presence of some water may improve selectivity, e.g. operation with water addition to the feed or hydration of the catalyst. For a fluid bed reactor operation with about 0.75 wt% water in the reaction mixture is preferred. The products comprising alkylated aromatics are characterized by exceptional oxidative and thermal stability. They may be separated from the reaction mixture by stripping off unreacted alkylating agent and naphthalene compound in the conventional manner. It has also been found that the stability of the alkylated product may be improved by filtration over activated charcoal and by alkali treatment to remove impurities, especially acidic by-products formed by oxidation during the course of the reaction. The alkali treatment is preferably carried out by filtration over a solid alkali material, preferably calcium carbonate (lime). In a typical product work-up it has been found, for example, that the RBOT (Rotating Bomb Oxidation Test) stability can be increased from a value of 184 minutes for an unstripped product (C 14 -alkylnaphthalene) to 290 minutes if the unreacted materials are removed by striping and to 350 minutes if the stripped product is filtered over lime (CaCO 3 ). EXAMPLE Two samples of Zeolite Y of crystal size 0.2-0.4 µm were used, namely: HSZ-320NAA - Standard NaY zeolite (UCS = ∼2.46 nm (∼24.64 A)) HSZ-320HOA - Partially NH 4 + exchanged and calcined NaHY Properties of as-received crystals are given in Table 1. Matrix The zeolites were incorporated into a silica-clay matrix at a 40 wt% zeolite level. To produce this matrix, one part of colloidal silica (Nalco 1034A) was mixed with one part of a Thiele RC-32 clay, charged as a slurry. The zeolite was added to the clay-silica mixture and the formulation was spray dried at 177°C (350°F), pH = 3 to 4.5 and then either calcined at 538°C (1000°F); or ammonium exchanged twice with 1 N NH 4 NO 3 solution, 5 volume of solution/volume catalyst, and then calcined at 400°C (752°F). Final Calcination The 400°C calcination consisted of heating the samples in flowing air (5 vol air/vol catalyst/min) from room temperature to the target temperature at 2.8°C/min (5°F/min). The catalysts were then held at the final temperature in flowing air for 5 hours. The fully calcined samples (1000°F) were produced in a similar manner but were not ammonium exchanged prior to final calcination. Analysis of the Reaction Products All alkylation runs were carried out in stirred flasks at 392°F (200°C). The runs consisted of charging the naphthalene and 1-hexadecene (in a 1:1.2 molar ratio). The catalyst was then charged and the mixture was heated to the reaction temperature. Samples were taken at 2, 4, 6 and 8 hours and analyzed by gas chromatography (GC). The amount of dimer was difficult to ascertain since it co-eluted with the monoalkylated naphthalene. In an attempt to deconvolute the amount of dimer and alkylated naphthalene, we calculated a predicted naphthalene and C 16 = Conversion based upon the analysis of the mono- and dialkylated naphthalenes. When the naphthalene conversion was higher than that measured from the naphthalene peak area, the excess was assumed to be dimer. This was the convention used to calculate the conversions shown in the table below. TPAD Analysis Temperature programmed ammonia desorption (TPAD) was carried out using the method described by Kerr and Chester. Typically, the sample was heated in the DuPont Model 951 TGA from room temperature to 700°C at 10°C/minute under a 150 ml/minute flow of high purity helium. The stream of helium containing the desorbed ammonia was passed through a buffered solution where the excess base was titrated with sulfamic acid solution of known concentration (usually ∼0.017 g N/1). The exchange capacity is reported as milliequivalents of ammonia per gram of catalyst (meq/g) based on the weight of the catalyst determined at 700°C. These data show it is essential for optimum performance to have both ammonium and protonic cations on the exchangeable sites. It is also beneficial to have some rare earths, and some water, but the amount of water found in most commercial grade naphthalene supplies (typically 0.75 wt%) is enough.

Claims: A process for preparing long chain alkyl substituted naphthalenes which comprises alkylating a naphthalene with an alkylating agent possessing an alkylating aliphatic group having at least six carbon atoms under alkylation reaction conditions in the presence of an alkylation catalyst comprising zeolite Y containing exchangeable sites and both ammonium and protonic species associated with the exchangeable sites, and wherein the ratio of ammonium:protonic species is within the range of 95:5 to 5:95, molar basis, to form an alkylated naphthalene possessing at least one alkyl group derived from the alkylating agent. The process of claim 1 wherein the ratio of ammonium:protonic species is in the range 90:10 to 10:90. The process of claim 2 wherein the ratio of ammonium:protonic species is in the range 65:35 to 35:65. The process of claim 2 wherein the ratio of ammonium:protonic species is in the range 40:60 to 60:40. The process of claim 2 wherein the ratio of ammonium:protonic species is in the range 40:60 to 50:50. The process of any preceding claim wherein the zeolite is ammonium exchanged zeolite Y calcined until the ratio ammonium:protonic species is within the said range. The process of claim 6, wherein the zeolite is ammonium exchanged zeolite Y calcined until from 45 to 60% of the ammonium form is converted to the protonic form. The process of claim 6 or claim 7 wherein the ammonium exchanged zeolite subjected to calcination is completely ammonium exchanged. The process of any of claims 6 to 8 wherein the calcination is performed at 300 to 425°C. The process of claim 9 wherein the calcination is performed at 300 to 400°C. The process of any preceding claim wherein the alkylating aliphatic group contains at least 8 carbon atoms. The process of claim 11 wherein the alkylating aliphatic group contains at least 12 carbon atoms. The process of claim 12 wherein the alkylating aliphatic group contains from 14 to 20 carbon atoms. The process of any preceding claim wherein the alkylating agent comprises an olefin. The process of any preceding claim wherein the alkylation reaction conditions include a temperature of 100 to 400°C, pressure of 20 to 2532 kPa, a WHSV of 0.1 to 10 and an alkylatable aromatic:alkylating agent mole ratio of 0.1:1 to 50:1. The process of claim 15 wherein the alkylation reaction conditions include a temperature of 100 to 300°C, a pressure of 101 to 506 kP a WHSV of 0.5 to 5 and an alkylatable aromatic:alkylating agent mole ratio of 0.5:1 to 5:1. The process of claim 15 or claim 16 wherein the ratio of ammonium:protonic species is 46 to 54.

Inventors: ARDITO SUSAN CHMURA, ASHJIAN HENRY, DEGNAN THOMAS F, HELTON TERRY EUGENE, LE QUANG NGOC, QUINONES AUGUSTO RUDOLFO, ARDITO, SUSAN CHMURA, ASHJIAN, HENRY, DEGNAN, THOMAS F., HELTON, TERRY EUGENE, LE, QUANG NGOC, QUINONES, AUGUSTO RUDOLFO
Applicants: EXXONMOBIL OIL CORP, EXXONMOBIL OIL CORPORATION
Application year: 1994
Main classification: C07C2
IPC codes: C07C2, B01J29, B01J37