HIGH-CARBON STEEL WIRE OR STEEL THEREFOR EXCELLENT IN WORKABILITY IN WIRE DRAWING AND PROCESS FOR PRODUCING THE SAME

Abstract: A high-carbon steel wire or steel therefor excellent in workability in wire drawing and a process for producing the same. The wire contains on the weight basis 0.90-1.10 % of carbon, not more than 0.40 % of silicon and not more than 0.50 % of manganese; not more than 0.02 % of phosphorus, not more than 0.01 % of sulfur and not more than 0.003 % of aluminum; and the balance consisting of iron and inevitable impurities. Further it has a microstructure wherein the area rate of the upper bainite structure formed by two-stage transformation is 80 % or above and the Hv value is 450 or less. It may further contain 0.10-0.30 % of chromium as the alloying component.

Description: Technical Field This invention relates to high-carbon steel wire rod and wire excellent in drawability and methods of producing the same. Background Art Wire rod and wire are ordinarily drawn into a final products matched to the purpose of use. Before conducting the drawing process, however, it is necessary to put the wire rod or wire in a condition for drawing. As a conventional measure for this, Japanese Patent Publication No.Sho 60-56215 discloses a method for heat treatment of steel wire rod of high strength and small strength variance characterized in that wire rod of steel containing C : 0.2 - 1.0%, Si < 0.30% and Mn : 0.30 - 0.90% and at austenite formation temperature is cooled between 800 and 600 °C at a cooling rate of 15 - 60 °C/sec by immersion in fused salt of one or both of potassium nitrate and sodium nitrate fused by heating to a temperature of 350 - 600 °C and stirred by a gas. However, the wire rod of pearlite texture obtained by the heat treatment method described in the aforesaid patent publication involves the problems of ductility degradation during drawing at a high reduction of area and of cracking in twist testing (hereinafter referred to as "delamination"). JP-A-51 005 965 discloses ductile high strength steel wire rod having a composition overlapping that of the present invention, compositions according to the invention being exemplified. A bainitic structure is obtained by isothermal patenting at 450-500°C, leading to hardnesses remarkaby higher than Hv 450. The object of this invention is to provide high-carbon steel wire rod and wire excellent in drawability and methods of producing the same which advantageously overcome the aforesaid problems of the prior art. Disclosure of the Invention The invention is defined in terms of product in claim 1 ; processes for producing the product are defined in claims 3 and 4. The gist of the invention is as set out below. (1) High-carbon steel wire rod or wire excellent in drawability characterized in that it contains, in weight percent, C : 0.90 - 1.10%, Si : not more than 0.40% and Mn : not more than 0.50%, is limited to P : not more than 0.02%, S : not more than 0.01% and Al : not more than 0.003%, the remainder being Fe and unavoidable impurities, and has a microstructure of, in terms of area ratio, not less than 80% upper bainite texture obtained by two-stepped transformation and an Hv of not more than 450. (2) High-carbon steel wire rod or wire excellent in drawability according to paragraph 1 above further containing Cr : 0.10 - 0.30% as an alloying component. (3) A method of producing high-carbon steel wire rod excellent in drawability characterized by, rolling into wire rod a steel slab of a composition which contains, in weight percent, C : 0.90 - 1.10%, Si : not more than 0.40% and Mn : not more than 0.50%, is limited to P : not more than 0.02%, S : not more than 0.01% and Al : not more than 0.003%, the remainder being Fe and unavoidable impurities, cooling the rolled wire rod from the temperature range of 1100 - 755 °C to the temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C/sec, and holding it in this temperature range for a specified time period within the range in which bainite transformation does not begin or within a range from after the start of bainite transformation to prior to completion of bainite transformation, and increasing the temperature and holding it until bainite transformation is completely finished. (4) A method of producing high-carbon steel wire rod excellent in drawability according to paragraph 3 above wherein the starting slab further contains Cr : 0.10 - 0.30% as an alloying component. (5) A method of producing high-carbon steel wire rod excellent in drawability according to paragraph 3 or 4 above characterized by, after the starting slab has been rolled into wire rod, cooling the rolled wire rod from the temperature range of 1100 - 755 °C to the temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C/sec, holding it in this temperature range for not less than 1 sec and not more than a period within the range in which bainite transformation does not begin of X sec determined by the following equation (1), and increasing the temperature not less than 10 °C and not more than 600 - T 1 (T 1 : holding temperature after cooling) °C and holding it until bainite transformation is completely finished, X = exp (16.03 - 0.0307 x T 1 ) where T 1 : holding temperature after cooling. (6) A method of producing high-carbon steel wire rod excellent in drawability according to paragraph 3 or 4 above characterized by, after the starting slab has been rolled into wire rod, cooling the rolled wire rod from the temperature range of 1100 - 755 °C to the temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C/sec, holding it in this temperature range for a period from after the start of bainite transformation to prior to completion of bainite transformation, specifically for a period of not more than Y sec determined by the following equation (2), and increasing the temperature not less than 10 °C and not more than 600 - T 1 (T 1 : holding temperature after cooling) °C and holding it until bainite transformation is completely finished, Y = exp (19.83 - 0.0329 x T 1 ) where T 1 : holding temperature after cooling. (7) A method of producing high-carbon steel wire excellent in drawability characterized by, heating to the temperature range of 1100 - 755 °C wire of a composition which contains, in weight percent, C : 0.90 - 1.10%, Si : not more than 0.40% and Mn : not more than 0.50%, is limited to P : not more than 0.02%, S : not more than 0.01% and Al : not more than 0.003%, the remainder being Fe and unavoidable impurities, cooling the heated wire to the temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C/sec, and holding it in this temperature range for a specified time period within the range in which bainite transformation does not begin or within a range from after the start of bainite transformation to prior to completion of bainite transformation, and increasing the temperature and holding it until bainite transformation is completely finished. (8) A method of producing high-carbon steel wire excellent in drawability according to paragraph 7 above wherein the starting wire further contains Cr : 0.10 - 0.30% as an alloying component. (9) A method of producing high-carbon steel wire excellent in drawability according to paragraph 7 or 8 above characterized by, cooling the starting wire from the temperature range of 1100 - 755 °C to the temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C/sec, holding it in this temperature range for not less than 1 sec and not more than a period within the range in which bainite transformation does not begin of X sec determined by the following equation (1), and increasing the temperature not less than 10 °C and not more than 600 - T 1 (T 1 : holding temperature after cooling) °C and holding it until bainite transformation is completely finished, X = exp (16.03 - 0.0307 x T 1 ) where T 1 : holding temperature after cooling. (10) A method of producing high-carbon steel wire excellent in drawability according to paragraph 7 or 8 above characterized by, cooling the starting wire from the temperature range of 1100 - 755 °C to the temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C/sec, holding it in this temperature range for a period from after the start of bainite transformation to prior to completion of bainite transformation, specifically for a period of not more than Y sec determined by the following equation (2), and increasing the temperature not less than 10 °C and not more than 600 - T 1 (T 1 : holding temperature after cooling) °C and holding it until bainite transformation is completely finished, Y = exp (19.83 - 0.0329 x T 1 ) where T 1 : holding temperature after cooling. Brief Description of Drawings Figure 1 is a diagram showing a heat treatment pattern of the present invention. Best Mode for carrying out the Invention The invention will be explained in detail in the following. The reasons for the restrictions on the bainite high-carbon steel wire rod and wire for drawing and the method of producing the same according to this invention will now be discussed. The inventors discovered that in ordinary patenting treatment pro-eutectoid cementite is precipitated along the old austenite grain boundaries even in an eutectoid composition with a C content in the vicinity of 0.8% and that this pro-eutectoid cementite becomes a cause of ductility degradation after drawing. C is an economical and effective strengthening element and is also an effective element for lowering the amount of this pro-eutectoid cementite precipitated. Therefore, the amount of added C has to be set at not less than 0.90% for an ultra-fine wire of a tensile strength of not less than 3500 MPa and enhanced ductility. Since ductility is reduced and drawability degraded when the amount of addition is too high, however, the upper limit is set at 1.10%. Si is an element required for deoxidizing the steel and the deoxidizing effect is therefore insufficient when the amount contained is too small. In addition, Si increases the strength after patenting by entering in solid solution into the ferrite phase in the pearlite formed after heat treatment. On the other hand, however, when the content is too large, it lowers the ductility of the ferrite and, in turn, lowers the ductility of the ultra-fine wire after drawing. The upper limit of its content is therefore set at 0.40%. A small amount of Mn is preferably added for securing hardenability. However, addition of a large amount of Mn induces segregation, leading to formation of supercooled textures, namely bainite and martensite, which thereafter impair drawability. The content is therefore set at not more than 0.50%. For securing ductility on a par with prior art ultra-fine wire, S content is set at not more than 0.01%. Since, like S, P also impairs the ductility of wire rod or wire, its content is set at not more than 0.02%. Presence of nonductile inclusions whose main component is Al 2 O 3 , such as Al 2 O 3 , MgO-Al 2 O 3 and the like, is a cause for reduction of ultra-fine wire ductility. In this invention, therefore, Al content is set at not more than 0.003% for avoiding ductility reduction by nonductile inclusions. In the case of a hypereutectoid steel such as that of this invention, a cementite network easily forms in the texture following patenting and thick cementite precipitates readily occur. For achieving high strength and high ductility in such a steel, it is necessary to make the pearlite fine and, further, to eliminate the aforesaid cementite network and the thick cementite. The Cr added as occasion demands in this invention suppresses the appearance of such abnormal cementite portions and has the further effect of making the pearlite fine. However, addition of a large amount increases the dislocation density in the ferrite following heat treatment and thus markedly degrades the ductility of the ultra-fine wire following drawing. The Cr content is therefore set at not less than 0.10%, at which its effect can be anticipated, and not more than 0.30%, at which ductility is not degraded by increased dislocation density in the ferrite. The reasons for the limitations in the production method of the present invention are as follows. The cooling start temperature (T 0 ) following wire rod rolling or following wire heating affects the texture following transformation. The lower limit is set at not less than the austenite transformation point (755 °C), which is the equilibrium transformation start temperature. The upper limit is set at 1100 °C for suppressing abnormal austenite grain growth. The cooling rate (V 1 ) following wire rod rolling or following wire heating is an important factor in suppressing the start of pearlite transformation. This was experimentally ascertained by the inventors. In the case of gradual cooling at an initial cooling rate of less than 60°C/sec, transformation starts on the high-temperature side of the pearlite transformation nose position, making it impossible to obtain a perfect bainite texture owing to formation of pearlite texture. While bainite texture forms at temperature under 500 °C, formation of a perfect bainite texture requires rapid cooling at the initial cooling stage. The lower limit of the cooling rate (V 1 ) is therefore set at 60 °C/sec, while the upper limit thereof is set at the industrially feasible 300 °C/sec. The isothermal holding temperature (T 1 ) after cooling is an important factor determining the formed texture. At a holding temperature exceeding 500 °C, pearlite texture forming at the center portion of the wire rod or wire increases tensile strength and degrades drawability. At a holding temperature below 350 °C, granulation of cementite in the bainite structure starts, increasing tensile strength and degrading drawability. The upper limit of the isothermal transformation temperature is therefore set at 500 °C and the lower limit thereof is set at 350 °C. Supercooled austenite texture is obtained by holding at 350 - 500 °C for a specified period of time. When the temperature is increased thereafter, the cementite precipitation in the bainite texture which appears is coarser than in isothermal transformation. As a result, the two-step-transformed upper bainite texture softens. In the case of complete two-stepped transformation, the supercooling time (t 1 ) required in the temperature range of 350 - 500 °C is not less than the time required for formation of supercooled austenite and the upper limit thereof is up to prior to the start of bainite transformation. It is preferably not less than 1 sec and not more than X sec indicated by the following equation: X = exp (16.03 - 0.0307 x T 1 ) (T 1 : holding temperature after cooling). The temperature rise (ΔT) in the case of conducting two-stepped transformation after supercooling is set at a lower limit of 10 °C, the temperature at which softening effect by two-stepped transformation appears, and since the upper limit of the temperature after temperature rise must not be more than 600 °C the lower limit is set at ΔT determined by the following equation: ΔT = 600 - T 1 (T 1 : holding temperature after cooling). The holding time (T 2 ) after temperature increase is set as the period up to complete finishing of the transformation. In the case of mixed two-stepped transformation after temperature increase, the supercooling time (t 1 ) required in the temperature range of 350 - 500 °C is set at a period after the start of bainite transformation and of not more than Y sec determined by the following equation: Y = exp (19.83 - 0.0329 x T 1 ) (T 1 : holding temperature after cooling). As in the case of complete two-stepped transformation, the temperature rise (ΔT) in the case of conducting two-stepped transformation after supercooling is set at a lower limit of 10 °C, the temperature at which softening effect by two-stepped transformation appears, and since the upper limit of the temperature after temperature rise must not be more than 600 °C the lower limit is set at ΔT determined by the following equation: ΔT = 600 - T 1 (T 1 : holding temperature after cooling). Pearlite texture forms at the wire rod or wire center portion in a pearlite wire rod or wire treated at a isothermal transformation temperature exceeding 500 °C. Since pearlite texture has a laminar structure of cementite and ferrite, it makes a major contribution to work hardening, but a decrease in ductility cannot be prevented. In the high area reduction region, therefore, tensile strength increases with an accompanying degradation of twist characteristics, causing the occurrence of delamination. In contrast, work hardening is suppressed in the wire rod or wire transformed in two steps according to this invention since it is in a state of coarse cementite dispersed in ferrite. As a result, it is possible to suppress occurrence of delamination and enable drawing up to the high area reduction region. The bainite texture area ratio is measured from the observed sectional texture using the lattice point method. The area ratio is an important index indicating the state of bainite texture formation and influences the drawability. The lower limit of the area ratio is set at 80%, where the two-stepped transformation effect noticeably appears. The Vickers hardness of the upper bainite structure is an important factor indicating the characteristics of the specimen. The cementite precipitation in a bainite wire rod or wire which has been two-step-transformed by conducting a cooling step and a temperature increasing step is coarser than in the case of isothermal transformation. As a result, the two-step-transformed upper bainite texture is softened. In consideration of effect on C content the upper limit of the Vickers hardness is set at not more than 450. EXAMPLES Example 1 Table 1 shows the chemical compositions of tested steel specimens. A - D in Table 1 are invention steels and E and F are comparison steels. Steel E has a C content exceeding the upper limit and steel F has a Mn content exceeding the upper limit. The specimens were produced by casting 300 x 500 mm slabs with a continuous casting machine and then bloom pressing them into 122 - mm square slabs. After these slabs had been rolled into wire rods, they were subjected to DLP (Direct Lead Patenting) cooling under the conditions indicated in Table 2. The wire rods were drawn to 1.00 mm  at an average reduction of area of 17% and subjected to tensile test and twist test. The tensile test was conducted using the No. 2 test piece of JISZ2201 and the method described in JISZ2241. In the twist test, the specimen was cut to a test piece length of 100d + 100 and rotated at a rotational speed of 10 rpm between chucks spaced at 100d. d represents the wire diameter. The characteristic values obtained in this manner are also shown in Table 2. No. 1 - No. 4 are invention steels. No. 5 - No. 10 are comparative steels. In comparative steel No. 5, pearlite which formed because the cooling rate was too slow reduced the drawability, leading to breakage during drawing. In comparative steel No. 6, two-step-transformed bainite texture did not form because the temperature rise was too low, reducing the drawability and leading to breakage during drawing. In comparative steel No. 7, martensite formed because a sufficient isothermal transformation period was not secured, reducing the drawability and leading to breakage during drawing. In comparative steel No. 8, the ratio of two-step-transformed bainite texture decreased because the supercooling treatment time was long, reducing the drawability and leading to breakage during drawing. In comparative steel No. 9, pro-eutectoid cementite which formed because the C content was too high reduced the drawability. In comparative steel No. 10, micromartensite which formed in conjunction with central segregation caused by an excessively high Mn content reduced the drawability. Chemical Compositions of Tested Steel Specimens Symbol Chemical Compositions (wt%) Remark C Si Mn P S Cr Al A 0.95 0.18 0.40 0.006 0.008 - 0.002 Invention B 0.98 0.15 0.30 0.006 0.008 0.19 0.002 Invention C 1.10 0.16 0.39 0.006 0.007 0.21 0.001 Invention D 1.02 0.20 0.35 0.005 0.008 0.21 0.002 Invention E 1.30 0.11 0.40 0.005 0.008 0.11 0.001 Comparison F 0.98 0.30 1.50 0.006 0.007 0.11 0.002 Comparison Example 2 Table 3 shows the chemical compositions of tested steel specimens. A - D in Table 3 are invention steels and E and F are comparison steels. The specimens were produced by casting 300 x 500 mm slabs with a continuous casting machine, bloom pressing them into 122 - mm square slabs, and producing wire from these slabs. After heating, these wires were subjected to DLP (Direct Lead Patenting) cooling under the conditions indicated in Table 4. The wire were drawn to 1.00 mm  at an average reduction of area of 17% and subjected to tensile test and twist test. The tensile test was conducted using the No. 2 test piece of JISZ2201 and the method described in JISZ2241. In the twist test, the specimen was cut to a test piece length of 100d + 100 and rotated at a rotational speed of 10 rpm between chucks spaced at 100d. d represents the wire diameter. The characteristic values obtained in this manner are also shown in Table 4. No. 1 - No. 4 are invention steels. No. 5 - No. 10 are comparative steels. In comparative steel No. 5, pearlite which formed because the cooling rate was too slow reduced the drawability, leading to breakage during drawing. In comparative steel No. 6, two-step-transformed bainite texture did not form because the temperature rise was too low, reducing the drawability and leading to breakage during drawing. In comparative steel No. 7, martensite formed because a sufficient isothermal transformation period was not secured, reducing the drawability and leading to breakage during drawing. In comparative steel No. 8, the ratio of two-step-transformed bainite texture decreased because the supercooling treatment time was long, reducing the drawability and leading to breakage during drawing. In comparative steel No. 9, pro-eutectoid cementite which formed because the C content was too high reduced the drawability. In comparative steel No. 10, micromartensite which formed in conjunction with central segregation caused by an excessively high Mn content reduced the drawability. Chemical Compositions of Tested Steel Specimens Symbol Chemical Compositions (wt%) Remark C Si Mn P S Cr Al A 0.95 0.18 0.40 0.006 0.008 - 0.002 Invention B 0.98 0.15 0.30 0.006 0.008 0.19 0.002 Invention C 1.10 0.16 0.39 0.006 0.007 0.21 0.001 Invention D 1.02 0.20 0.35 0.005 0.008 0.21 0.002 Invention E 1.30 0.11 0.40 0.005 0.008 0.11 0.001 Comparison F 0. 98 0.30 1.50 0.006 0.007 0.11 0.002 Comparison Industrial Applicability As discussed in the foregoing, since the wire rod or wire produced in accordance with this invention can be drawn to an appreciably higher reduction of area than possible by the prior art method, it has improved delamination resistance property. The invention enables production of bainite wire rod and wire excellent in drawability, elimination of intermediate heat treatment in the secondary processing step, a large reduction in cost, a shortening of production period, and a reduction of equipment expenses.

Claims: High-carbon steel wire rod or wire excellent in drawability containing, in weight percent, C : 0.90 - 1.10 % Si: not more than 0.40 % and Mn: not more than 0.50 % is limited to P : not more than 0.02 % S : not more than 0.01 % and Al: not more than 0.003 %, the remainder being Fe and unavoidable impurities, and has a microstructure of, in terms of area ratio, not less than 80 % upper bainite texture in a state of coarse cementite dispersed in ferrite and an Hv of not more than 450, said structure being obtainable by the process according to any of claims 3-5. High carbon steel wire rod or wire excellent in drawability according to claim 1, further containing Cr : 0.10 - 0.30 % as an alloying agent. A method of producing high-carbon steel wire rod or wire excellent in drawability with the following steps: rolling into wire rod a steel slab or heating a wire to a temperature range of 1100 - 755 °C, both the slab and the wire having a composition which contains, in weight percent, C : 0.90 - 1.10 %, Si : not more than 0.40 % and Mn : not more than 0.50 %, is limited to P : not more than 0.02 %, S : not more than 0.01 % and Al : not more than 0.003 %, the remainder being Fe and unavoidable impurities, cooling the rolled wire rod or the heated wire from a temperature range of 1100 - 755 °C obtained either after hot rolling or heating to this temperature, to a temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C /sec, holding it in this temperature range for not less than one second and not more than a period of X sec within the range in which the bainite transformation does not begin, X being determined by the following equation (1), and increasing the temperature not less than 10 °C and not more than 600 - T 1 °C (T 1 : holding temperature after cooling) and holding it until the bainite transformation is completely finished, X = exp (16.03 - 0.0307 x T 1 ) where T 1 : holding temperature after cooling. A method of producing high-carbon steel wire rod or wire excellent in drawability with the following steps: rolling into wire rod a steel slab or heating a wire to a temperature range of 1100 - 755 °C, both the slab and the wire having a composition which contains, in weight percent, C : 0.90 - 1.10 %, Si : not more than 0.40 % and Mn : not more than 0.50 %, is limited to P : not more than 0.02 %, S : not more than 0.01 % and Al : not more than 0.003 %, the remainder being Fe and unavoidable impurities, cooling the rolled wire rod or the heated wire from a temperature range of 1100 - 755 °C obtained either after hot rolling or heating to this temperature, to a temperature range of 350 - 500 °C at a cooling rate of 60 - 300 °C /sec, holding it in this temperature range for a period beginning after the start of the bainite transformation to a point of time prior to completion of the bainite transformation, namely for a period of not more than Y sec as determined by the following equation (2), and increasing the temperature not less than 10 °C and not more than 600 - T 1 °C (T 1 : holding temperature after cooling) and holding it until the bainite transformation is completely finished, Y = exp (19.83 - 0.0329 x T 1 ) where T 1 : holding temperature after cooling. A method of producing high-carbon steel wire rod or wire according to one of claims 3 or 4, wherein the starting slab or the starting wire further contains Cr : 0.10 - 0.30 % as an alloying component.

Inventors: KAWANA AKIFUMI, NISHIDA SEIKI, OBA HIROSHI, OCHIAI IKUO, KAWANA, AKIFUMI, NISHIDA, SEIKI, OBA, HIROSHI, OCHIAI, IKUO
Applicants: NIPPON STEEL CORP, NIPPON STEEL CORPORATION
Application year: 1994
Main classification: C22C38
IPC codes: C21D8, C21D9, C21D1, C22C38