Preparation of silver vanadium oxide cathodes

Abstract: A cathode for an electrochemical cell containing as active component a silver vanadium oxide in the form of a mixed metal oxide having an amorphous content. Also provided is a method for preparing the cathode wherein the silver vanadium oxide is formed by chemical addition, reaction or otherwise intimate contact of a silver-containing compound and a vanadium containing compound to form a mixed metal oxide bronze that is thermally treated and rapidly cooled to form an amorphous product. The method of the present invention provides an alternate preparation technique for improving chemical control in the formation of a cathode for incorporation into an electrochemical cell.

Description: This invention relates to the manufacture of an alkali metal electrochemical cell or battery, and more particularly to new and improved methods of preparing silver vanadium oxide composite cathode material for use in high energy density batteries. Solid cathode, liquid organic electrolyte and alkali metal lithium anode cells or batteries are used as the power source for implantable medical devices. The cathode of such a cell may have as active material carbon fluoride, a metal oxide, a metal oxide bronze such as silver vanadium oxide, or other suitable material as disclosed in U. S. Patent 4,830,940 to Keister et al. , which patent is assigned to the assignee of the present invention and is incorporated herein by reference. Preparation of cathode material containing a metal oxide bronze such as silver vanadium oxide for use in a lithium cell or battery has been known by a decomposition reaction. However, the decomposition method of preperation is accompanied by the evolution of gaseous products. Typically, the synthesis is carried out by first thermally decomposing a vanadium salt to produce vanadium pentoxide. A decomposable metal salt, preferably containing silver, is then blended with the vanadium pentoxide in water and the mixture is oven-dried. Following drying, the mixture is again blended and ground to ensure thorough intermingling of the constituents and the resulting homogeneous mixture is subsequently baked for a final heating/decomposition period. Depending on the starting materials used, this final heating/decomposition period can result in the release of toxic by-product gases. For example, if silver nitrate (AgNO 3 ) is used as the silver source, nitrous oxide type gases may be formed. Such a decomposition reaction for the preparation of silver vanadium oxide is: AgNO 3 + V 2 O 5 → AgV 2 O 5.5 + NO 2 + ¼O 2 Upon cooling, the baked material is blended with appropriate amounts of carbon black and graphite powder to enhance conductivity, and with a binder material, and then pressed to form the cathode. Such a method is described in more detail in US Patent 4,310,609 to Liang et al. , which patent is assigned to the assignee of the present invention and is incorporated herein by reference. The present invention provides a cathode containing silver vanadium oxide as an active component, wherein the silver vanadium oxide is provided in the novel and improved form of a mixed metal oxide having an amorphous content. References related to the art of forming a mixed metal oxide bronze by reacting a vanadium containing compound with silver oxide (Ag 2 O) include the following P. Fleury ( Revue de Chimie minerale 6:819-851, 1969), describes the establishment of an equilibrium diagram between liquid and solid phases of three systems formed by the solid state reaction of V 2 O 5 and CuO, and Ag 2 O and Tl 2 O 3 , and the study of newly discovered solid phases. A. Casalot et.al. (Bulletin de la Societe Chimique de France 10:3817-3820, 1967), describes a study of the Ag 2 O-V 2 O 3 -VO 2 system in an alpha phase comprising a solid solution of Ag + ions in V 2 O 5 ; a monoclinic, beta phase being an isotope of homologous phases existing for the insertion of other monovalent elements, and a gamma, pseudo-orthorhombic phase. B. Raveau (Revue de Chimie minerale 4:735-758, 1967), describes the limited relations between the various phases of the V-Ag-O system formed under vacuum, formed in an inert atmosphere, formed in an oxygen atmosphere as well as reaction studies of oxidation and reduction in the V-Ag-O system to show that no new phases were obtained. P. Fleury et.al. (C.R. Acad. Sc. Paris 262: 475-477, 1966) describe the crystallization of melted (molten) mixtures of the Ag 2 O-V 2 O 5 system. W. Wenda (Journal of Thermal Analysis 879-889, 1985), discusses phase equilibria in the V 2 O 5 -Ag 2 O system at a constant oxygen pressure (20·2 kPa) (0.2 atm). The phase diagram found under these conditions was compared with the same system in vacuum and at an oxygen pressure of 101 kPa (1 atm) in an attempt to construct the hypothetical phase diagram of V 2 O 5 -AgO-O 2 . Published European patent application 0 478 303 A3 discloses a cathode material for electrochemical cells of a silver vanadium oxide prepared by a chemical combination or addition reaction but the silver vanadium oxide so prepared is not amorphous. JP-A-57662/1988 to Otsuka Kagaku KK describes an amorphous substance for use as a positive-electrode active substance, the amorphous substance being obtained by heat-melting a mixture, followed by rapid cooling, said mixture comprising V 2 O 5 and 1 to 30 mole % of at least one oxide selected from the following group, or a compound which when heat-melted can produce any of said oxides: Na 2 O, K 2 O, Rb 2 O, Cs 2 O, BeO, MgO, CaO, SrO, ZrO 2 , Nb 2 O 5 , Ta 2 O 5 , Cr 2 O 3 , MnO 2 , Fe 2 O 3 , Co 2 O 3 , NiO, ZnO, CdO, Ag 2 O, Al 2 O 3 , Ga 2 O 3 , As 2 O 3 , PbO, Tl 2 O 3 , CeO 2 , Nd 2 O 3 , Y 2 O 3 and Sc 2 O 3 . It is an object of the invention to provide a cathode for an electrochemical cell containing a new and improved form of silver vanadium oxide. It is another object of this invention to provide new and improved methods for preparing a silver vanadium oxide composite cathode for use in high energy density batteries. It is a further object of the present invention to provide new and improved methods for preparing silver vanadium oxide using Ag 2 O and V 2 O 5 as starting materials. It is still another object of the present invention to provide new and improved methods for preparing silver vanadium oxide as an amorphous material. It is a further object of this invention to provide improved chemical control for the formation of metal oxide bronze cathode material. According to the present invention, there is provided a cathode for an electrochemical cell and containing silver vanadium oxide as active component characterised in that the silver vanadium oxide is provided as a mixed metal oxide having an amorphous content with the proviso that the preparation of oxide(s) added to the vanadium oxide in the production of the silver vanadium oxide is greater than 30 mole % of the total amount of oxide(s) and the vanadium oxide. The invention also provides a cathode for an electrochemical cell and containing silver vanadium oxide as active component characterised in that the silver vanadium oxide is provided as a mixed metal oxide having a vanadium content in amorphous form. The silver vanadium oxide may have been treated in the presence of a dopant to provide the mixed metal oxide in amorphous form. Further according to the invention, there is provided a method of making a cathode for an electrochemical cell comprising (i) forming silver vanadium oxide in the form of a mixed metal oxide having an amorphous content and (ii) utilising said silver vanadium oxide to form the cathode. Step (i) of the process suitably comprises forming silver vanadium oxide in the form of a mixed metal oxide having a vanadium content in amorphous form. In one embodiment, step (i) comprises (a) forming a first combination comprising a vanadium compound and a dopant material (b) rendering said combination amorphous, (c) combining the amorphous first combination with a silver containing component selected from silver and compounds of silver to provide a second combination, and (d) heat-treating the second combination to form the mixed metal oxide. In another embodiment, step (i) comprises (a) forming an intimate combination comprising a vanadium compound, a silver-containing component selected from silver and compounds of silver, and a dopant to form a mixed metal oxide, and (b) rendering said mixed metal oxide amorphous. The step of making the first combination or mixed metal oxide amorphous may be effected by heating the material to an elevated temperature, suitably above the melting point of the material; followed by quenching. The cathode preferably comprises from 80 to 99 weight percent of said silver vanadium oxide. In a particularly preferred arrangement the cathode comprises 0 to 3 weight percent carbon, 0 to 3 weight percent fluororesin powder and 94 to 99 weight percent of said silver vanadium oxide. The present invention relates to new and improved methods of preparing silver vanadium oxide composite cathode material for use in high energy density batteries. The present invention comprises various methods by which a cathode is formed from materials that include amorphous silver vanadium oxide prepared by the chemical addition, reaction or otherwise intimate contact of several metal oxides during thermal treatment in mixed states, followed by rapid cooling of the mixed metal oxide bronze, and may include an electronic conductor and binder materials. The silver vanadium oxide composite material prepared by the methods of the present invention results in the intercalation of silver ions into starting materials comprising one or more vanadium-containing compounds through intimate contact of the silver-containing compound, preferably Ag 2 O, with the vanadium-containing compound, followed by thermal treatment and then rapid cooling wherein a mixed metal oxide bronze is formed wherein at least the vanadium containing component of the mixed oxide is in amorphous form. Such vanadium-containing compounds include, but are not limited to, silver vanadate, vanadium oxide salt and vanadium oxides, with vanadium oxides being preferred. A particularly preferred vanadium-containing compound is vanadium pentoxide. The present invention also relates to an electrochemical cell comprising a cathode, an alkali metal anode, a non-aqueous electrolyte comprising a combination of an organic solvent and a lithium salt; and a separator electrically insulating the anode from the cathode and of sufficient porosity to allow for electrolyte flow characterised in that the cathode is as the cathode of the present invention or is obtained by the method of the present invention. Cathode plates can be formed by an entirely dry pressing procedure thereby enhancing the shelf life of the resulting plates. Alternatively, the procedure can include dropwise addition of liquid electrolyte to the cathode mixture prior to pressing to enhance the performance and discharge rate capability of an assembled cell incorporating the cathode. The discharge characteristic of the electrochemical cell containing the cathode of the present invention is a gradually sloping, rather than stepped discharge characteristic. Brief Description Of The Drawings The above and other objects, features, and advantages of the present invention will be apparent in the following detailed description of the preferred embodiments taken in conjunction with the accompanying drawings, in which: Fig. 1 is a graph showing the discharge curves of a cell containing silver vanadium oxide as a cathode made from AgNO 3 and V 2 O 5 according to the prior art decompostion method. Fig. 2 is a graph showing the discharge curve of a newly assembled cell containing crystalline silver-vanadium oxide as a cathode produced by the chemical combination or addition reaction of Ag 2 O and V 2 O 5 . Fig. 3 is a graph showing the discharge and internal impedance curves of a cell containing silver vanadium oxide as a cathode made from AgNO 3 and V 2 O 5 according to the prior art decomposition method. Fig. 4 is a graph showing the discharge curves and internal impedance of a newly assembled cell containing a cathode produced by the chemical combination or addition reaction of Ag 2 O and V 2 O 5 and in an amorphous state in accordance with the present invention. One method of the present invention comprises synthesizing silver vanadium oxide from starting materials including intimately combining in an addition reaction a vanadium-containing compound and a silver-containing compound. The silver-containing compound may include silver oxide, silver iodide, a silver vanadate, silver metal, silver carbonate, or a combination thereof, silver oxide being most preferred. The addition reaction is carried out by thoroughly grinding the starting materials together, thermally treating the combined starting materials and rendering the mixture amorphous by rapid cooling to a liquid nitrogen temperature, for example, by pouring the heated material onto a liquid nitrogen cooled foil. The reaction may be quenched by pouring the heated material into deionised water. Preferably a non-metallic oxide salt, preferably a phosphorus oxide salt such as P 2 O 5 , is added to the starting ingredients as a dopant to enhance the breakdown of the crystalline mixtures to render the product amorphous. The thermal treatment is preferbly carried out at between about 750°C to 775°C, more preferably at about 760°C, for about one to two hours. Following thermal treatment, the mixed metal oxide bronze is rapidly cooled to yield silver vanadium oxide in an amorphous state. (A crystalline silver vanadium oxide is formed by thermally treating the silver-containing compound combined with the vanadium-containing compound and then slowly cooling the resulting combination.) Alternatively, the vanadum-containing oxide compound can be rendered amorphous prior to being intimately combined with the silver containing-compound in an addition reaction. In this case, the dopant material is added to the vanadium-containing compound to retard formations of crystalline structure before the vanadium-containing compound is rendered amorphous by heating to between about 750°C to 775°C, preferably about 760°C for about one to two hours followed by rapid cooling. The amorphous vanadium-containing compound is finally combined with the silver-containing compound in an addition reaction to form the product. The addition reaction may be carried out at temperatures of from between about 300°C to 700°C, preferably at temperatures of between about 350°C to 550°C and most preferably at temperatures of between about 380°C to 400°C and may proceed to completion within about 5 to 24 hours. Lower temperatures require a longer reaction time. Longer reaction times and higher temperatures may lead to diminished rate capability in cells utilizing the silver vanadium oxide material due to undesirable grain growth. Therefore, in general, lower temperatures are preferred in order to limit grain growth in the silver vanadium oxide product. The reaction is preferably carried out in an oxidizing atmosphere that can include air and oxygen, or the reaction may be carried out in an inert atmosphere including for example argon, nitrogen and helium. Preparation of the electrochemical cell is completed by combining the amorphous silver vanadium oxide with an electronic conductor and with a binder material, and finally pressing the composite materials to form a cathode plate. The discharge curves for a cell or battery using the amorphous silver vanadium oxide material have different characteristics from cells incorporating a crystalline silver vanadium oxide. In addition, the use of silver oxide avoids the liberation of toxic fumes generated by use of silver nitrate (AgNO 3 ) as the silver starting material, such as is used in the the decomposition reaction previously discussed. Figs. 1 and 2, respectively, illustrate discharge curves for electrochemical cells using silver vanadium oxide made by decomposing AgNO 3 with a vanadium-containing compound according to the prior art (Fig. 1) and made according to an addition reaction by thermally treating Ag 2 O (Fig. 2) as the silver-containing compound intimately combined with a vanadium-containing compound in an addition reaction to form a crystalline silver vandium oxide. The electrochemical discharges were accomplished by applying pulse trains consisting of four ten-second, 1.5 ampere pulses every 15 seconds repeated every 30 minutes to the respective cells. Thus, Fig. 1 shows discharge curves for a high energy density cell containing silver vanadium oxide made according to the prior art decomposition method wherein curve 10 was recorded at open circuit with no load, curve 12 was constructed from the minima of the first pulse of each train and curve 14 was constructed from the minima of the fourth pulse of each train. In comparison, Fig. 2 shows a high energy density cell containing crystalline silver vanadum oxide as a cathode material made by an addition reaction between a silver-containing compound and a vanadium-containing compound, wherein curve 20 was recorded at open circuit with no load, curve 22 was constructed from the minimum of the first pulse of each pulse train and curve 24 was from the fourth pulse minima of each pulse train. The latter cell shows flattened plateau regions with less pronounced fall off in discharge approaching end of life in comparison to the former cell. Fig. 3 illustrates discharge and internal impedance curves 30 and 32, respectively, for an electrochemical cell using silver vanadium oxide made by a decomposition reaction between AgNO 3 and a vanadium-containing material while Fig. 4 illustrates discharge and internal impedance curves 40 and 42, respectively, for an electrochemical cell having a cathode containing an amorphous silver vanadium oxide made by an addition reaction of Ag 2 O and V 2 O 5 according to the present invention. The respective cells were run down using a 5 kohm load. The sloping discharge curve of Fig. 4 indicates that crystalline silver vanadium oxide is not present in the amorphous material. This contrasts with the stepped discharge of the decomposition product in Fig. 3. The difference in the shape of the discharge curves of a cell using silver vanadium oxide product by an addition reaction in a crystalline state (Fig. 2) and amorphous state (Fig. 4) also illustrate that the discharge curve can be tailored to a desired shape. This may be important for particular applications and uses. Varying the silver content also allows the shape of the discharge curve to be adjusted. A cathode, containing cathode active material prepared by the methods of the present invention, can be used in a nonaqueous lithium battery as described by Keister et al. , wherein the battery also contains an alkali metal anode, preferably lithium or alloys thereof; a nonaqeuous electrolyte which preferably is comprised of a combination of lithium salt and an organic solvent; and a separator material electrically insulating the anode from the cathode while having sufficient porosity to allow for electrolyte flow. The methods of preparation of silver vanadium oxide composite material for use as cathode active material in a cathode, and an electrochemical cell incorporating the cathode according to the present invention, are illustrated further by the following examples. EXAMPLE I A cathode was formed from materials including silver vanadium oxide prepared by intimate contact of the silver-containing compound with the vanadium-containing compound in the following manner. A 1 mole % phosphorous pentoxide (P 2 O 5 ) in vanadium pentoxide (V 2 O 5 ) mixture was heated at 760°C for one hour and then poured onto a titanium foil cooled over liquid nitrogen. Silver oxide (Ag 2 O) was added to the amorphous P 2 O 5 /V 2 O 5 mixture with the Ag:V ratio being 1:2. The resulting mixture was baked at 400°C for 16 hours to form silver vanadium oxidr according to the present invention. The silver vanadium oxide thus formed was mixed with carbon black and graphite as conductive diluents and polytetrafluoroethylene (PTFE) powder as a binder material to form a depolarizer which was pressed into cathodes for use in electrochemical cells. A cathode comprising 3% conductive materials, 3% PTFE and 94% silver vanadium oxide made according to the method of the present invention was thus prepared. A battery cell was assembled using the foregoing cathode, lithium as the anode, 1M LiAsF 6 in propylene carbonate and dimethoxyethane as the electrolyte and a microporous polypropylene sheet as a separator. The weight of the cathode was 2.0g. The open circuit voltage was 3.722V. The cell delivered 0.542Ah or 0.297 Ah/g based on the cathode active material to a 2V cut-off under a drain rate of 0.5 mA/cm 2 . The discharge curve was generally sloped. EXAMPLE II Silver vanadium oxide was prepared in the following manner. A 10 mole % P 2 O 5 in AgV 2 O 5 mixture was heated to 760°C for one hour. The heated mixture was then poured onto a titanium foil cooled over liquid nitrogen to form amorphous silver vanadium oxide according to the present invention. The silver vanadium oxide thus formed was mixed with carbon black and graphite as conductive diluents and PTFE powder as a binder material to form a depolarizer which was pressed into cathodes for use in electrochemical cells. A cathode comprising 3% conductive material, 3% PTFE and 94% silver vanadium was made according to the method of the present invention. A battery cell was assembled using the foregoing cathode, lithium as the anode, 1M LiAsF6 in propylene carbonate and dimethoxyethane as the electrolyte and a microporous polypropylene sheet as a separator. The weight of the cathode was 2.5g. The open circuit voltage of the resulting cell was 3.67V. The cell delivered 0.602Ah or 0.270Ah/g based on the cathode active material to a 2V cut-off under a drain rate of 0.2 mA/cm 2 . The discharge curve was generally sloped. EXAMPLE III Silver vanadium oxide was prepared in the following manner. A mixture of 1.77g P 2 O 5 , 20.46g of V 2 O 5 and 13.04g of Ag 2 O was heated to 760°C for one hour. The heated mixture was then poured into deionized water to form amorphous silver vanadium oxide according to the-present invention. The silver vanadium oxide thus formed was mixed with carbon black and graphite as conductive diluents and Teflon powder as a binder material to form a depolarizer which was pressed into cathodes for use in electrochemical cells. A cathode comprising 3% conductive material, 3% PTFE and 94% silver vanadium oxide made according to the method of the present invention was thus prepared. A battery cell was assembled using the foregoing cathode, lithium as the anode, 1M LiAsF6 in propylene carbonate and dimethoxyethane as the electrolyte and a microporous polypropylene sheet as a separator. The weight of the cathode was 0.75g. The resulting cell delivered 0.17 Ah or 0.241 Ah/g based on the cathode active material to a 2V cut-off under a drain rate of 0.1 mA/cm 2 . The discharge curve was generally sloped. EXAMPLE IV Silver vanadium oxide was prepared by heating a homogeneous mixture of AgV 2 O 5 at 760°C for one hour. The heated mixture was then poured into deionized water to form amorphous silver vanadium oxide according to the present invention. The silver vanadium oxide thus formed was mixed with carbon black and graphite as conductive diluents and Teflon powder as a binder material to form a depolarizer which was pressed into cathodes for use in electrochemical cells. A cathode comprising 3% conductive materials, 3% PTFE and 94% silver vanadium oxide made according to the method of the present invention was thus prepared. A battery cell was assembled using the foregoing cathode, lithium as the anode, 1M LiAsF6 in propylene carbonate and dimethoxyethane as the electrolyte and a microporous polypropylene sheet as a separator. The weight of the cathode was 0.75g The cell delivered 0.198Ah or 0.282 Ah/g based on the cathode active material to a 2V cut-off under a drain rate of 0.1 mA/cm 2 . The discharge curve was generally sloped. The above detailed description and examples are intended for the purposes of illustrating the invention and are not to be construed as limiting. For example, depending on the application of the electrochemical cell, the range of cathode compositions used can vary from 100% silver vanadium oxide to 80% silver vanadium oxide with 10% carbon/graphite and PTFE or other suitable conductor and binding materials known in the art. The invention can be embodied otherwise without departing from the principles thereof, and such other embodiments are meant to come within the scope of the present invention as defined by the appended claims.

Claims: A cathode for an electrochemical cell and containing silver vanadium oxide as active component characterised in that the silver vanadium oxide is provided as a mixed metal oxide being substantially amorphous with the proviso that the proportion of oxide(s) added to the vanadium oxide in the production of the silver vanadium oxide is greater than 30 mole % of the total amount of oxide(s) and the vanadium oxide. A cathode for an electrochemical cell and containing silver vanadium oxide as active component characterised in that the silver vanadium oxide is provided as a mixed metal oxide having a vanadium content in amorphous form with the proviso that the proportion of oxide(s) added to the vanadium oxide in the production of the silver vanadium oxide is greater than 30 mole % of the total amount of oxide(s) and the vanadium oxide. A cathode according to claim 1 or 2 wherein the amorphous characteristics are provided by the presence of a dopant. A cathode for an electrochemical cell and containing silver vanadium oxide as active component characterised in that the silver vanadium oxide has been treated in the presence of a dopant to provide a mixed metal oxide in amorphous form. A cathode as claimed in any one of claims 1 to 4 which comprises from 80 to 99 weight percent of said silver vanadium oxide. A cathode as claimed in any one of claims 1 to 5 which comprises 0 to 3 weight percent carbon, 0 to 3 weight percent fluororesin powder and 94 to 99 weight percent of said silver vanadium oxide. A method of making a cathode for an electrochemical cell comprising: (i) forming silver vanadium oxide in the form of a mixed metal oxide being substantially amorphous wherein the proportion of oxide(s) added to the vanadium oxide in the production of the silver vanadium oxide is greater than 30 mole % of the total amount of oxide(s) and the vanadium oxide; and (ii) utilising said silver vanadium oxide to form the cathode. A method as claimed in claim 7 characterised in that step (i) comprises forming silver vanadium oxide in the form of a mixed metal oxide having a vanadium content in amorphous form. A method of making a cathode for an electrochemical cell comprising: (i) combining a silver-containing component with a vanadium-containing component to provide silver vanadium oxide as a mixed metal oxide having amorphous characteristics, wherein the amorphous characteristics are provided by the presence of a dopant material; and (ii) utilizing said silver vanadium compound to form the cathode. A method as claimed in any one of claims 7 to 9 in which step (i) comprises (a) forming a first combination comprising a vanadium compound and a dopant material (b) rendering said combination amorphous, (c) combining the amorphous first combination with a silver containing component selected from silver and compounds of silver to provide a second combination, and (d) heat-treating the second combination to form the mixed metal oxide. A method as claimed in any one of claims 7 to 9 in which step (i) comprises (a) forming an intimate combination comprising a vanadium compound, a silver-containing component selected from silver and compounds of silver, and a dopant to form a mixed metal oxide, and (b) rendering said mixed metal oxide amorphous. A method as claimed in any one of claims 9 to 11 in which the step of making the combination or mixed metal oxide amorphous comprises heating it to an elevated temperature followed by quenching. A method as claimed in claim 12 in which the heating to an elevated temperature comprises heating above the melting point of the vanadium compound. A method as claimed in claim 12 or claim 13 wherein the heating to an elevated temperature comprises baking at a temperature in the range 750°C to 775°C for 1 to 2 hours. A method as claimed in claim 14 wherein the heating to an elevated temperature comprises baking at about 760°C for about one hour. A method as claimed in any one of claims 12 to 15 wherein the quenching is effected by pouring the heated material into deionized water or rapidly lowering it to a liquid nitrogen temperature. A method as claimed in any one of claims 12 to 15 in which the quenching is effected by pouring the heated material on to a liquid nitrogen cooled foil. A method as claimed in any one of claims 9 to 17 wherein the dopant material is a non-metallic oxide salt. A method as claimed in claim 18 wherein non-metallic oxide salt is a phosphorus oxide salt. A method as claimed in any one of claims 10 to 19 wherein the silver-containing component is selected from silver oxide, silver vanadate, silver metal, silver carbonate, and combinations thereof. A method as claimed in any one of claims 10 to 20 wherein the vanadium compound is selected from silver vanadate, vanadium pentoxide and combinations thereof. A method as claimed in any one of claims 10 to 21 wherein the silver containing component is silver oxide and the vanadium compound is vanadium pentoxide. A method as claimed in any one of claims 7 to 22 wherein the silver vanadium oxide forms 80 to 99 percent by weight of the cathode. A method as claimed in any one of claims 7 to 23 wherein the cathode comprises 0 to 3 weight percent carbon, 0 to 3 weight percent fluororesin powder and 94 to 99 weight percent of said silver vanadium oxide. A method as claimed in any one of claims 7 to 24 wherein the cathode is formed from a composition comprising the silver vanadium oxide by pressing. A method as claimed in claim 25 wherein liquid electrolyte is added dropwise to the composition prior to pressing. An electrochemical cell comprising a cathode, an alkali metal anode, a nonaqueous electrolyte comprising a combination of an organic solvent and a lithium salt; and a separator electrically insulating the anode from the cathode and of sufficient porosity to allow for electrolyte flow characterised in that the cathode is a cathode as claimed in any one of claims 1 to 6 or obtained by a method as claimed in any one of claims 7 to 26.

Inventors: TAKEUCHI ESTHER S, THIEBOLT III WILLIAM C, TAKEUCHI, ESTHER S., THIEBOLT III, WILLIAM C.
Applicants: GREATBATCH W LTD, WILSON GREATBATCH LTD.
Application year: 1994
Main classification: H01M4
IPC codes: H01M4, H01M6, C01G31