POLYETHER COPOLYMERS AND A PROCESS FOR PREPARING THEM

Abstract: A block copolymer containing one or more polyoxyethylene blocks and one or more polyoxy(higher alkylene) blocks wherein at least some of the blocks are linked together by an oxymethylene group can be prepared by reacting one or more dihydroxy terminated polymers selected from poly(ethylene glycol), poly(higher alkylene glycol) and block copolymers thereof in solution with a dihalomethane in the presence of a base. Such copolymers can be used as surfactants and surface modifiers.

Description: POLYETHER COPOLYMERS AND A PROCESS FOR PREPARING THEM Field of the Invention The invention relates to polyoxyalkylene block copolymers and a process for their preparation. Background of the Invention Dihydroxy terminated triblock copolymer surfactants are known having the general structure H- (E) a (P)fc > (E) a -0H wherein E represents oxyethylene and P represents oxypropylene. Such nonionic surfactants are commercially available e.g. Pluronic™ surfactants. US-A-4 072 704 describes the preparation of polyoxyalkylene block copolymer surfactants by reacting individual blocks of polymers and copolymers of alkylene oxides with formaldehyde or a dialkyl carbonate. For example, the surfactants can contain polyoxyethylene and polyoxypropylene polymers linked by formal or carbonate groups. Problem to be Solved by the Invention Alternative polyoxyalkylene block copolymers and a process for their production are required. In particular, a simpler process of preparation which makes it possible to prepare copolymers of higher molecular weight is desired. Summary of the Invention The invention provides a block copolymer containing one or more polyoxyethylene blocks and one or more polyoxy(higher alkylene) blocks wherein at least some of the blocks are linked together by a linking group characterised in that the linking group is an oxymethylene group. The invention also provides a process for preparing a block copolymer containing one or more polyoxyethylene blocks and one or more polyox (higher alkylene) blocks characterised in that one or more dihydroxy terminated polymers selected from -2- poly (ethylene glycol), poly (higher alkylene glycol) and block copolymers thereof are reacted in solution with a dihalomethane in the presence of a base. Advantageous Effect of the Invention The reaction can be carried out using an excess of the dihalomethane as a solvent for the other reactants. Heating is not required as the reaction proceeds at ambient temperature. Polyoxyalkylene block copolymers can be prepared having a higher molecular weight than those prepared using other processes. The methylene oxide linking groups closely resemble the chemical structure of the other groups forming the polymer blocks. Detailed Description of the Invention Preferred copolymers of the invention include those wherein the polyoxy (higher alkylene) blocks are selected from polyoxypropylene and polyoxybutylene blocks. In one embodiment of the invention, block copolymers are provided having the following repeating units in random order - ( [P n ]CH 2 0-) x ( [E m ]CH 2 0) y - wherein P is oxypropylene; E is oxyethylene; n is an integer from 2 to 70, preferably from 4 to 20; m is an integer from 2 to 250, preferably from 9 to 20; x is an integer from 1 to 100, preferably from 1 to 10; and, y is an integer from 1 to 100, preferably from 1 to 50. 96/1 -3- In another embodiment of the invention, block copolymers are provided having the following repeating units -[ (E r P s E r )CH 2 0] z - wherein P is oxypropylene; E is oxyethylene; r is an integer from 2 to 135, preferably from 75 to 135; s is an integer from 15 to 65, preferably from 30 to 50; and, z is an integer from 2 to 50, preferably from 5 to 20. The molecular weight of a block copolymer of the invention as measured by gel permeation chromatography against poly(oxyethylene) standards may range from 10,000 to 500,000, preferably from 50,000 to 250, 000. The polymers can be prepared by a process wherein one or more dihydroxy terminated polymers selected from poly(ethylene glycol), poly(higher alkylene glycol) and block copolymers thereof are reacted in solution with a dihalomethane in the presence of a base. Examples of suitable solvents in which the reagents can be dissolved include dihalomethanes and other known organic solvents such as benzene, chlorobenzene and toluene or mixtures thereof. Preferably, an excess of the dihalomethane reagent is used as the solvent. Even though the dihalomethane is used in an amount which can far exceed the stoichiometric amount needed to couple with the polymeric reactants, products of high molecular weight can still be achieved. Although any dihalomethane or mixture thereof may be used such as dichloromethane, dibromomethane or diiodomethane, the preferred dihalomethane is dichloromethane. The required alkaline reaction conditions may be obtained by incorporating one or more bases such as sodium hydroxide and potassium hydroxide. Examples of the dihydroxy terminated polymer starting materials include the polyethylene glycols (PEGs) and the polypropylene glycols (PPGs) which are available commercially. Specific examples include PEG 400, PEG 6000 and PPG 1000 for which the number associated with the name "PEG" or "PPG" indicates the average molecular weight of the polymer and is proportional to the average number of repeating oxyethylene or oxypropylene units in the polymer. Preferred polyalkylene glycols have molecular weights ranging from 200 to 10,000. Further examples of the dihydroxy terminated polymer starting materials include the dihydroxy terminated E-P-E triblock copolymers of poly (oxyethylene) (E) and poly(oxypropylene) (P) which are commercially available in the form of Pluronic™ surfactants. Preferred triblock copolymers have molecular weights ranging from 4,000 to 15,000. The copolymers of the invention contain both hydrophilic polyoxyethylene blocks and hydrophobic polyoxy (higher alkylene) blocks. The balance between the hydrophilicity and hydrophobicity of the copolymers can be adjusted by appropriate choice of starting materials to give the optimum physical and chemical characteristics required. In addition to being suitable for a variety of surfactant applications such as antifoaming agents and dispersing aids, the block copolymers may be used as surface modifiers e.g. to reduce the level of protein adsorption to polystyrene. The copolymers are suited for use as biocompatible materials in biomedical devices. The invention is illustrated but not limited by the following Examples. Example 1 An oxymethylene linked, multiblock copolymer was prepared by the reaction of an E76P30E76 triblock copolymer of poly(oxyethylene) (-7g) and poly(oxypropylene) (P30) / having an average molecular weight of 8,400, with dichloromethane in the presence of potassium hydroxide. Finely ground potassium hydroxide (20g) was mixed with dichloromethane (250 ml) under a nitrogen atmosphere at room temperature in a one litre resin kettle equipped with a condenser and a mechanical stirrer. To this w3s added the triblock copolymer (20g) dispersed in dichloromethane (50 ml) . The whole was stirred for approximately two hours, then additional dichloromethane (500 ml) was added to reduce the viscosity of the polymer solution. The solution was filtered through diatomaceous earth and then rotary evaporated under vacuum to give a polymer. The polymer was characterised by gel permeation chromatography (GPC) . Dimethyl formamide (DMF) eluant and styragel columns were employed, calibrated with poly(oxyethylene) standards. Molecular weights and molecular weight distributions were obtained from the GPC curve by reference to this calibration. Values of Mw ~ 150,000 and Mw/Mn ~ 2 were obtained. The yield was >95%. Example 2 Oxymethylene linked Ei29 p 56 E 129 was prepared according to the method described in Example 1 using the following reagents: Potassium hydroxide 20g Dichloromethane 250 ml E 129 P 56 E 129 20 9 (in 0 ml dichloromethane) The polymer was isolated as described in Example 1. Values of Mw ~ 70,000 and Mw/Mn ~ 2 were obtained from GPC measurements. The yield was >95%. Example 3 Oxymethylene linked E9P56E9 was prepared according to the method described in Example 1 using the following reagents: Potassium hydroxide 20g Dichloromethane 30 ml E9P56E9 16g (in 15 ml dichloromethane) The polymer was isolated as described in Example 1. Values of Mw ~ 20,000 and Mw/Mn - 2 were obtained from GPC measurements. The yield was >80%. Example 4 An oxymethylene linked, multiblock copolymer was prepared by the reaction of polyethylene glycol with an average molecular weight of 400 (PEG 400) and polypropylene glycol with an average molecular weight of 1000 (PPG 1000) with dichloromethane in the presence of potassium hydroxide. The polymer was prepared according to the method described in Example 1 using the following reagents: Potassium hydroxide 50g Dichloromethane 50 ml PEG 400 lOg PPG 1000 45g i.e. 35.7 mol% PEG and 64.3 mol% PPG 1000. The polymer was isolated as described in Example 1. Values of Mw ~ 11,000 and Mw/Mn ~ 2 were obtained from GPC measurements. The yield was >95%. Example 5 An oxymethylene linked, multiblock copolymer was prepared by the reaction of polyethylene glycol with an average molecular weight of 400 (PEG 400) and polypropylene glycol with an average molecular weight of 1000 (PPG 1000) with dichloromethane in the presence of potassium hydroxide. The polymer was prepared according to the method described in Example 1 using the following reagents: Potassium hydroxide 50g Dichloromethane 50 ml PEG 400 40g PPG 1000 11.25g i.e. 90 mol% PEG and 10 mol% PPG 1000. The polymer was isolated as described in Example 1. Values of Mw ~ 50,000 and Mw/Mn - 2 were obtained from GPC measurements. The yield was >95%. Example 6 An oxymethylene linked, multiblock copolymer was prepared by the reaction of an E r B s E r triblock copolymer wherein B is oxybutylene, having an average molecular weight of 4,200, with dichloromethane in the presence of sodium hydroxide. The copolymer was prepared according to the method described in Example 1 using the following reagents: Sodium hydroxide 20g Dichloromethane 160 ml E 37 B 11 E 37 10g ( in 50 ml dichloromethane) The polymer was isolated as described in Example 1. Values of Mw ~ 243,000 and Mw/Mn ~ 2 were obtained from GPC measurements. The yield was >95%. Example 7 An oxymethylene linked, multiblock copolymer was prepared by the reaction of an E r P s E r triblock copolymer, commercially available as Pluronic™ F108 and a polethylene glycol having an average molecular weight of 6000 (PEG 6000) with dichloromethane in the presence of sodium hydroxide. The copolymer was prepared according to the method described in Example 1 using the following reagents: Sodium hydroxide 30g Dichloromethane 200 ml E 129 P 56 E 129 15< ? < in dichloromethane*) PEG 6000 15g (in dichloromethane*) *The Ei29P56 E 129 and PEG 6000 were used as a mixture dissolved in 100 ml dichloromethane. The polymer was isolated as described in Example 1. Values of Mw ~ 170,500 and Mw/Mn - 2 were obtained from GPC measurements. The yield was >95%.

Claims: Claims 1. A block copolymer containing one or more polyoxyethylene blocks and one or more polyoxy(higher alkylene) blocks wherein at least some of the blocks are linked together by a linking group characterised in that the linking group is an oxymethylene group. 2. A copolymer according to claim 1 wherein the polyoxy(higher alkylene) blocks are selected from polyoxypropylene and polyoxybutylene blocks. 3. A copolymer according to claim 1 having the following repeating units in random order - ([P n ]CH 2 0-)x ([E m ]CH 2 0) y - wherein P is oxypropylene; E is oxyethylene; n is an integer from 2 to 70; m is an integer from 2 to 250; x is an integer from 1 to 100; and, y is an integer from 1 to 100. 4. A copolymer according to claim 1 having the following repeating units -[ (E r P s E r )CH 2 0] z - wherein P is oxypropylene; E is oxyethylene; r is an integer from 2 to 135; s is an integer from 15 to 65; and, z is an integer from 2 to 100. 5. A process for preparing a block copolymer containing one or more polyoxyethylene blocks and one or more polyoxy(higher alkylene) blocks characterised in that one or more dihydroxy terminated polymers selected from poly(ethylene glycol), poly(higher alkylene glycol) and block copolymers thereof are reacted in solution with a dihalomethane in the presence of a base. 6. A process according to claim 5 wherein an excess of dihalomethane is used as solvent. 7. A process according to claim 5 or claim 6 wherein the dihalomethane is dichloromethane.

Inventors: NICHOLAS CHRISTIAN VAUGHAN, PURBRICK MALCOLM DONALD, NICHOLAS, CHRISTIAN, VAUGHAN, PURBRICK, MALCOLM, DONALD
Applicants: EASTMAN KODAK CO, NICHOLAS CHRISTIAN VAUGHAN, PURBRICK MALCOLM DONALD, EASTMAN KODAK COMPANY, NICHOLAS, CHRISTIAN, VAUGHAN, PURBRICK, MALCOLM, DONALD
Application year: 1994
Main classification: C08G65
IPC codes: C08G65