HYDROSTATIC NUT AND LEAD SCREW ASSEMBLY, AND METHOD OF FORMING SAID NUT

Abstract: A method of forming a hydrostatic nut (36) that cooperates with a lead screw (38) for translating a cam grinder wheel head (26). An externally threaded lead screw master (66) is inserted into an internally threaded cylindrical mold (50). Beads of wax or tape (76, 78) are adhered to the external threads on the standard (66) while the rest of the standard (66) is treated with a release coating to define a continuous cavity (86, 88) between the internal threads of the nut (36) and the external threads on the standard (66). An epoxy resin is introduced into the cavity. The standard (66) is then removed and the wax or tape (76, 78) is removed to leave oppositely directed helical channels (86, 88) in the polymer. The helical channels are pressurized with a thin fluid film that prevents metal to metal contact.

Description: HYDROSTATIC NOT AND LEAD SCREW ASSEMBLY, AND METHOD OF FORMING SAID NUT TECHNICAL FIELD The present invention relates generally to a hydrostat- ic nut and lead screw assembly for a translatable carriage, such as may be used to support a grinding wheel. More particularly, the invention pertains to a method of forming the hydrostatic nut, to complement the threaded lead screw, while defining channels within the nut to receive pressurized fluid. BACKGROUND OF THE INVENTION In known grinding machines, an abrasive grinding wheel is rotatably mounted upon a wheel head for translation relative to a workpiece, such as a cam shaft, that is ground to a desired size and shape. The workpiece is retained in between a headstock and a footstock, and the wheel head, with the grinding wheel, is translated by a nut and lead screw arrangement. The nut is internally threaded and fits about, and coacts with, the externally threaded lead screw. The nut is secured to the wheel head, and the lead screw is driven by a motor, coupled to the end of the lead screw remote from the nut. The motor, which may be numerically controlled, rotates the lead screw relative to the nut, in either a clockwise or counter-clockwise fashion, and thus linearly translates the abrasive grinding wheel relative to the workpiece. Previously, the abrasive grinding wheels, which might be 16 inches in diameter and formed of carborundum, would be gradually abraded away, and reduced in diameter, by extended cycles of grinding operations. Over a period of time, the wheels might be reduced by three or four inches in diameter. As the wheels gradually "shrunk", the motor, in accordance with a program, would drive the lead screw to advance the wheel head and grinding wheel toward the workpiece to compensate for such shrinkage. As the lead screw was advanced, the wear attributable to continued operation in a hostile industrial environment, on a factory or job shop floor, would be distributed over a length of lead screw comparable to the extent of shrinkage of the abrasive grinding wheel. With the advent of more durable, harder, grinding wheels, made out of materials such as CBN (cubic-boron-nitride) , the grinding wheels are reduced in diameter almost imperceptibly. CBN grinding wheels grind with great precision, require fewer dressing operations, and infrequent replacement, and thus have met with widespread acceptance. However, utilization of CBN wheels, and other grinding wheels with diamond-like hardness, has intensified the problem of wear in the lead screw and nut assembly for the wheel head and grinding wheel. While wear is inherent in using conventional grinding wheel machines, the significant reduction in grinding wheel size tended to distribute the wear over a significant length of the lead screw; conversely, the minor reduction in diameter of CBN grinding wheels, in the order of fractions of an inch, concentrates the wear on a fragment of the lead screw. Such localization of wear causes premature failure. Repeated, precise translational movement of the wheelhead relative to the workpiece is inhibited, and the exacting tolerances demanded by current engineering requirements for cam shafts, and other mechanical movements, cannot be readily maintained. Numerous approaches have been made to address the problems of (1) localized wear, (2) excessive friction between the contacting metal surfaces of the threads of the nut and lead screw, and (3) backlash. One approach has relied upon introducing precisely sized ball bearings between the contacting threaded surfaces and circulating the balls throughout the nut. Such approach has satisfactorily addressed the problems of excessive friction and backlash. However, such approach is prone to premature failure and does not have any damping in the direction of motion. Another approach has relied upon hydrostatic bearings employing a thin film of fluid between the contacting threaded surfaces; such approach also requires the pressurized distribu¬ tion of the thin film throughout the nut to avoid metal to metal contact between the cooperating, helically arranged teeth on the nut and lead screw. Pressurized distribution calls for precise machining operations within the metallic body of the nut to form pockets, manifolds, distribution channels, etc. and other fluid flow circuits to deliver the appropriate quantities of fluid to the desired locations. Yet another approach has focused upon casting an epoxy material about a section of the lead screw, or a master form, that replicates such section of the lead screw. The epoxy is treated with special fillers that increase its strength, lubricity, and wear characteristics, while reducing its usual brittleness. After the casting has been allowed to cure, usually at room temperature and pressure, the casting is removed from the lead screw, and retained within a nut housing. When the lead screw is subsequently advanced relative to the nut, the internal- ly threaded nut closely conforms to the configuration of the lead screw, with attendant reductions in frictional losses and misalignments. The utilization of epoxy materials, such as castable polymers, is discussed in detail in U.S. Patent 4,790,971, granted December 13, 1988, to Ross A. Brown et al, and in U.S. Patent 5,152,948, granted October 6,1992, to Kevin J. Lizenby; both patents are assigned to TranTek Inc. of Traverse City, Michigan. Each of the foregoing proposed approaches has proven to be deficient in some manner, such as cost, complexity, operational characteristics, etc., and the need for a solution to all of the problems noted above, such as localized wear, excessive friction, and backlash, remains unfulfilled. SUMMARY OF THE INVENTION With the shortcoming of prior art approaches to the existing problems clearly in mind, a unique nut has been designed that combines the desirable characteristics of known hydrostatic bearings with the simplicity attributable to casting epoxy resins, and other castable polymers, about lead screw sections to serve as bearing materials. The resulting cast, internally threaded, nut has channels defined within the castable polymer material that permits the subsequent introduction of hydrostatic pressure into the nut. Ultimately, after the casting and curing operations have been completed, the nut rides on a thin fluid film and is suitable for use with lead screws having helical threads formed on their shanks. A unique method of forming an internally threaded nut with channels defined in a rigid polymer material adhered to within the nut is disclosed. The method includes that step of placing wax, or positioning folded-over tape, in beads, along the outer surfaces of the lead screw, or lead screw segment, prior to introducing the epoxy resin into the mold in the space defined between the exterior threads of the lead screw and the interior threads of the nut. The wax, or folded-over tape, defines voids on the exposed surfaces of the resultant casting. When the wax, or tape, is removed, channels are formed in the rigid polymer material adhered within the nut. The nut serves as a mold for the castable polymer material, and is then machined to size, prior to being secured within a depending ear on the wheel head of a grinding machine. The internally threaded nut, with a rigid coating of polymer material adhered to its internal threads, closely follows the externally threaded contour of the lead screw, as the lead screw is advanced, or retracted, through the nut. The channels are pressurized by fluid introduced into ports in the nut, and the fluid flows through the channels to form a thin-film fluid bearing between the cooperating surfaces on the nut and lead screw. The molding process is conducted at room temperature and pressure. The resultant nut and lead screw assembly combines the ease of using castable polymers to form rigid coatings, with the low friction, non-binding qualities, attributable to forming a fluid film between the cooperating threads on the nut and the lead screw. Other advances attributable to the castable nut, with its readily formed, internally situated channels, will become apparent to the skilled artisan, when the appended drawings are construed in harmony with the ensuring description. For example, the channels are reinforced and/or strengthened by the metal helical threads underlying the coating to insure long life and accurate operation. The casting technique is adaptable to diverse shapes of screw threads, multiple helical turns, and the like. Furthermore, the method of forming the hydrostatic nut allows the production of nuts, at a price competitive with commercially available ball screws, and obviates the need for complex, and difficult, machining operations. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a side elevational view of a conventional grinding machine that is characterized by a unique hydrostatic nut and lead screw assembly constructed in accordance with the principles of the instant invention; FIG.2 is an enlarged, cross-sectional view of the mold and lead screw standard for forming the hydrostatic nut, such view being taken prior to the introduction of the molding material; FIG. 3 is an enlarged, cross-sectional view of the mold and lead screw standard for forming the hydrostatic nut, such view being taken after the introduction of the molding material; and FIG. 4 is an enlarged, cross-sectional view of the unique hydrostatic nut secured to the grinding machine in operative relationship to the lead screw. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Referring now to the drawings described above, FIG. 1 depicts the key components of a grinding machine, indicated generally by reference numeral 10. A heavy metal bed 12, which may be filled with concrete, rests upon the floor (not shown) of the work place. The front end of the bed is higher than the remainder of the bed. A carriage 14 is moved transversely across the front of bed 12, and a swivel table 16 may be operatively associated with carriage 14. A headstock 18 and a footstock (not shown) are secured to swivel table 16 by a dove-tail connection 20. A workpiece 22 is secured between the headstock and footstock, and one lobe on the workpiece, which is a cam shaft, is visible. A slide 24 moves longitudinally along the upper surface of bed 10, and a wheel head 26 moves along the upper surface of slide 24. Grinding wheel 28 is secured to axle 30, proximate the leading end of wheel head 26, and motor 32 drives wheel 28 via endless belt 34. The center line of axle 30 is aligned with the center line of work piece 22. A post 36 depends from wheel head 26, and a passage 38 extends longitudinally therethrough. A hydrostatic nut 40 is secured within passage 38, and the nut is internally threaded. The forward end of an elongated lead screw 42 passes through the nut; the lead screw is externally threaded. A small motor 44 may be secured to the rear end of the lead screw 42 by coupling 46, and the motor drives the lead screw relative to nut 40, to translate wheel head 26 and grinding wheel 28 relative to work piece 22. Motor 44 is responsive to signals supplied, usually in digital format, from a computerized control program that correlates the positioning, and operation of, grinding wheel 28 and work piece 22. Grinding machine 10 is conventional in most respects, and forms the environment within which unique hydrostatic nut 40 functions most satisfactorily. The method of forming hydrostatic nut 40 is also innovative, and represents a departure from known forming techniques. FIG. 2 illustrates, generally, a mold 50, which is converted into hydrostatic nut 40, by a distinctive sequence of operative steps. Mold 50 comprises a metallic, generally cylindrical body with a central bore that is open at opposite ends. A small retainer cap 52 seals one end of the mold, while a larger retainer cap 54 seals the opposite end thereof. An internal bore 56 extends through retainer cap 52, and a pressure plate 58 can be adjusted within the bore by rotating threaded stud 60. After pressure plate 58 has been adjusted, set screw 62 is tightened to engage stud 60 and retain same in fixed position. Larger retainer cap 54 includes an annular body with a projecting flange 64 that extends into mold 50. Pressure plate 66 moves within flange 64, and the movement of plate 66 is controlled by central stud 68, and adjusting screws 70, 72\ A lead screw standard 74 is secured within mold 50 by applying pressure to opposite ends thereof. Standard 74 conforms in size and shape to the section of the lead screw 42 that will pass through hydrostatic nut 40, and is operatively associated therewith. Standard 74 is precisely machined, with exceedingly tight tolerances, and is used repeatedly, over extended periods of time, to form hydrostatic nuts 40. Standard 74 is externally threaded, with helical threads. The helical threads are selected to be complementary to the internal threads defined in the interior wall of mold 50, as shown in FIG. 2. A first bead 76 of wax is applied, in a helical fashion, to the first or leading side of each thread on standard 74. Similarly, a second bead 78 of wax is applied, in a helical fashion, to the second or trailing side of each thread. Beads 76, 78 are applied to the threads of standard 74 prior to inserting same into cylindrical mold 50. After the beads 76, 78 of wax have been applied, standard 74 is inserted into mold 50, and plates 58, 66 are adjusted inwardly to lock standard 74 is fixed position within mold 50. A release coating may be applied to the surfaces of standard 74 that are not covered by the beads of wax, prior to inserting standard 74 into mold 50. An epoxy resin, or other castable polymer material 80, is introduced through inlet port 82 of mold 50 and into the space defined between the external teeth on standard 74 and the complementary internal teeth in mold 50. Spacing of a minute fraction of an inch exists between the complementary teeth at all points for metal to metal contact must be avoided. Air is withdrawn, from the mold through outlet port 84, so that air bubbles are avoided. Also, excess material may exit through port 84. The polymer material flows into the continuous cavity, or spacing, exactingly defined between the external threads on standard 74 and the internal threads on mold 50. Beads 76, 78 of wax adhere tightly to the external threads on standard 74, and are impervious to attack by polymer material 80 and the release coating (not shown) on standard 74. After the polymer material has filled the continuous cavity, mold 50 is allowed to sit for 12-18 hours, at room temperature and ambient pressure. Castable polymer material 80 cures, and assumes a rigid form. Retainer caps 52, 54 are then disengaged from opposite ends of mold 50, and lead screw standard 74 is unthreaded from mold 50. The release coating previously applied to standard 74 prevents adhesion of castable polymer material 80 to standard 74. Several castable polymer materials might, ultimately, prove to be capable of meeting the requirements for successful operation of mold 50, and/or the ultimate operational character¬ istics of hydrostatic nut 40. However, one epoxy material that has proven to be most satisfactory is sold under the trademark "Moglice", and is available from the Devit Corporation. After the lead screw standard 74 has been removed, mold 50, with a rigid coating of polymer material 80 adhered to its internal threads, is machined to its desired size and shape. In such final configuration, as shown in FIG. 4, mold 50 is transformed into hydrostatic nut 40. The beads 76, 78 of wax are manually removed from cured, rigid material 80, thus forming channels 86, 88, on the exposed surfaces of the material 80 which face the external threads of lead screw 42. The wax may be dissolved, and washed away, by suitable solvents. The hydrostatic nut is then positioned within passage 38 in post 36 that depends below wheel head 26, as shown in FIG. 4. The forward end of elongated lead screw 42 passes through, and cooperates with, nut 40 to translate wheel head 26 and grinding wheel 28 relative to work piece 22. FIG. 4 illustrates nut 40 in operative relationship to a fragment of lead screw 42. As previously noted, the removal of the beads 76, 78 of wax defines oppositely wound helical channels 86, 88 on the exposed surfaces of cured polymer material 80. The metal threads of the nut provide structural support to the channels. First inlet conduit 90 delivers fluid to helical channel 86 so that nut 40 floats, on a thin film of air, relative to lead screw 42 as the lead screw is advanced relative to the nut. Second inlet conduit 32 delivers fluid to helical channel 88 so that nut 40 floats, on a thin film of fluid, as the lead screw is retracted relative to the nut. The films of fluid, in concert with the formed polymer material 80, insure that nut 40 operates in a substantially friction free manner. While a preferred embodiment of the instant invention has been provided, other modifications, revisions and refinements will undoubtedly occur to the skilled artisan. For example, the wax used to form beads 76, 78 may be beeswax. The tape used for the same purpose may be a heavy duty tape, such as electrician's tape, or duct tape, which is formed into a semi-circular shape and adhered to the helical threads on lead screw standard 74 to define beads 76, 78. In some instances, the removal of lead screw standard 74 from mold 50 shears the beads 76, 78 of wax in the cured polymer material 80, and only limited amounts of residue must be washed away with solvents, or manually be removed from material 80. Furthermore, while hydrostatic nut 40 has found applicabili- ty within cam grinding machines, the same nut may find applica¬ tions in nut and lead screw assemblies for work carriages of other precision machine tools. Consequently, the appended claims should be construed broadly, in a liberal fashion commensurate with the meaningful advance in the useful arts and sciences, achieved by the hydrostatic nut, and the hydrostatic nut and lead screw assembly employing same.

Claims: IN THE CLAIMS: 1. A method of forming a hydrostatic nut for use with a lead screw for a machine tool, such method comprising the steps of: a) inserting a lead screw standard with at least one helical thread extending therealong into a mold, b) said mold having at least one helical thread defined on its inner surface that is complementary to, and spaced from, the helical thread on the exterior of said lead screw, c) adhering at least one bead of material along the said helical thread on the external surface of said standard, d) introducing a castable polymer material into said mold to fill the space between the internal thread on the mold and the exterior thread on the lead screw standard, e) said bead being formed of a material that is resistant to physical degradation and chemical attack by said polymer material, f) curing said polymer material into a rigid mass, and g) removing said bead from said cured polymer material so that a helical channel is defined on the outer surfaces of said cured polymer material. 2. The method of forming a hydrostatic nut as defined in claim 1 , further comprising the steps of: h) positioning said mold, with said rigid polymeric material adhered thereto, over the lead screw, and i) introducing pressurized fluid into said helical channel so that said mold floats on a thin film of fluid to function as a hydrostatic nut relative to said lead screw. 3. The method of forming a hydrostatic nut as defined in claim 1 , further comprising the step of treating said lead screw standard with a release coating prior to inserting same into said mold. 4. The method of forming a hydrostatic nut as defined in claim 1 , wherein the mold comprises a generally cylindrical body with retainer caps at opposite ends thereof, said method further comprising the step of adjusting said retainer caps to hold said standard in fixed position within said mold. 5. The method of forming a hydrostatic nut as defined in claim 1 , wherein the material that is resistant to physical degradation and chemical attack comprises a wax. 6. The method of forming a hydrostatic nut as defined in claim 1 , wherein the material that is resistant to physical degradation and chemical attack comprises duct tape that is folded into a bead-like configuration. 7. The method of forming a hydrostatic nut as defined in claim 1 , wherein said polymer material is cured at room temperature and under ambient pressure. 8. A method of forming a hydrostatic nut adapted to be used with a lead screw, such method comprising the steps of: a) forming a cylindrical mold with at least one helical thread defined on its inner surface, b) inserting a lead screw standard having at least one helical thread extending along the exterior surface of its shank for insertion into said mold, c) adhering at least one bead of material along the surface of said helical thread on said standard prior to inserting same into said mold, d) introducing castable polymer material into said mold to fill the space between the internal thread on the mold and the helical thread on the exterior of said standard, except for said bead, e) curing said polymer material into a rigid mass, f) removing said standard from said mold to expose the rigid mass of said polymer material adhered to said mold, and g) removing said bead of material from the exterior surface of said rigid casting to define at least one channel therein, h) said channel being capable of receiving pressurized fluid therein so that said mold can function as a hydrostatic nut when operatively associated with an elongated lead screw. 9. The method of forming a hydrostatic nut as defined in claim 8, wherein said cylindrical mold has a plurality of helical threads defined on its inner surface, and said lead screw standard has a plurality of complementary helical threads defined on the exterior surface of its shank. 10. The method of forming a hydrostatic nut as defined in claim 9, wherein said helical threads have a first surface and a second surface, and one continuous bead is adhered to the first surface of said helical threads, while a second continuous bead is adhered to the second surface of such helical threads. 11. The method of claim 10, further including the steps of applying a release coating to said lead screw standard prior to insertion into said mold, said release coating allowing the lead screw standard to be withdrawn from said mold without damaging the rigid coating. 12. The method of claim 10, further including the step of selecting the internal thread of the mold and the external thread of the lead screw standard to be compatible in configura- tion, and in size, so that the rigid coating prevents contact between the mold and the standard. 13. The method of claim 8, wherein said polymer material is cured at room temperature and under ambient pressure. 14. A hydrostatic nut for a machine tool comprising: a) a cylindrical body with a central bore that is open at opposite ends thereof, said body being formed of metal, b) at least one helical thread defined on the wall of said central bore, c) a thick, rigid plastic coating adhered to all exposed surfaces of said thread, and d) said nut being characterized by a void that follows the contour of said thread defined in the exposed side of said plastic coating, said void being adapted to function as a channel to carry pressurized fluid when said nut is operatively associat¬ ed with a lead screw. 15. A hydrostatic nut and lead screw assembly for a machine tool comprising: a) said hydrostatic nut comprising a cylindrical body with a central bore that is open at opposite sides thereof, said body being formed of metal, b) at least one helical thread defined on the wall of said bore, c) a rigid plastic casting adhered to all exposed surfaces of said thread in said nut, d) a void defined in the exposed side of said casting, e) a lead screw including an elongated shank with at least one helical thread formed therealong on its exterior surface, said lead screw being formed of metal, f) said casting preventing metal-to-metal contact between said thread on said nut and said thread on said nut when said nut and lead screw are operatively associated with one another, the invention being characterized by: g) said void in said casting and the exterior surface of said helical thread on said lead screw defining a continuous helical channel therebetween, and h) means for introducing pressurized fluid through the cylindrical body of said nut into said channel so that said nut floats on a thin film of fluid as the lead screw moves relative to said nut. 16. The hydrostatic nut and lead screw assembly as defined in claim 15, wherein said machine tool is a grinding machine, including a work holder for receiving a work piece, a grinding wheel, a wheel head, a slide supporting said wheel head, an axle extending through said grinding wheel to secure same to said wheel head for rotation thereabout, a post depending below said wheel head, said nut secured within said post, said lead screw extending through said nut, and a motor coupled to said lead screw for rotating same to thereby position said wheel head and grinding wheel relative to the work holder. 17. The hydrostatic nut and lead screw assembly as defined in claim 16, wherein the work piece is cylindrical in shape, and said grinding machine is a cam grinder. 18. The hydrostatic nut and lead screw assembly as defined in claim 15, wherein said machine tool includes a bed, a work piece holder secured upon said bed, a carriage that can be translated relative to said bed, said nut secured to said carriages, a grinding wheel secured to said carriage, said hydrostatic nut being secured to said carriage, and a motor for driving said lead screw so that said lead screw moves relative to said nut to translate said carriage and grinding wheel relative to said work piece holder.

Inventors: PFLAGER WILLIAM W, PFLAGER, WILLIAM, W.
Applicants: WESTERN ATLAS INT INC, WESTERN ATLAS INC.
Application year: 1994
Main classification: B24B19
IPC codes: B24B19, B24B47, B29C70, B29D1, F16H25