Photosensitive resin composition

Abstract: There is disclosed a positive type photosensitive resin composition which comprises an alkali-soluble polymer (A) having a carboxyl group and/or a phenolic hydroxyl group, and a compound (B) which forms an amine compound with irradiation of light.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention This invention relates to a photosensitive resin composition, more specifically to a photosensitive resin composition having an excellent film property, heat-resistance, adhesivity and image-formability which does not require complex steps for preparation and does not cause contamination with chlorides. 2. Prior art In the semiconductor industries, inorganic materials have conventionally been used for interlaminar insulation. Recently, organic materials having an excellent heat-resistance such as a polyimide resin have been put to use as materials for interlaminar insulation because of properties thereof. A process for forming a pattern in a semiconductor integrated circuit or forming a pattern of a circuit on a print substrate comprises complex and various steps such as formation of a resist material film on the substrate surface; exposure of required portion to light; removal of unnecessary portion by etching or so; and washing of the base surface. Therefore, development of heat-resistant photosensitive materials have been desired, which enables the required portion of the resist material to be used as insulating materials even after the pattern is formed by exposure to light and development. As such a material, heat-resistant photosensitive materials comprising, for example, a photosensitive polyimide or a cyclized polybutadiene as a base polymer have been proposed. The photosensitive polyimide has attracted attentions since it has an excellent heat-resistance and impurities can easily be removed. As such a photosensitive polyimide, for example, a photosensitive polyimide precursor (a polyamic acid ester) in which a photosensitive group is introduced into the polyimide precursor by an ester bond is proposed in Japanese Patent Publication No. 30207/1980. This material which requires the use of an acid chloride group in synthesis of the photosensitive polyimide precursor has a disadvantage that a finally obtained photosensitive resin composition is easily contaminated with the chloride. Also, thermal cure of the polyamic acid ester to obtain the objective polyimide requires a high temperature, and therefore, the polyamic acid ester cannot be used when an element which cannot be heated at a high temperature is used. As another example, a photosensitive resin composition which mainly comprises a mixture of a polyamic acid, an amine having a photoactive functional group and an azide compound as a photosensitizer is proposed in Japanese Provisional Patent Publication No. 168942/1982. However, the photosensitive resin composition has a disadvantage that a thick film thereof cannot be formed. Japanese Provisional Patent Publication No. 95697/1979 proposes a photosensitive resin composition which mainly comprises a mixture of a polyamic acid and a polymerizable unsaturated compound having a photoactive functional group. This photosensitive resin composition, however, has a disadvantage that it has a lower resolving power as compared with a photosensitive resin composition which uses a photosensitive group-containing polyamic acid in which the photosensitive group is directly bound with the polyamic acid. European Patent Application No. 0425142A discloses photosensitive compositions comprising photobases which generate amines on exposure to light and polymers which are soluble in alkaline solution. Among the disclosed polymers are those containing at least one of a carboxyl group and a phenolic hydroxyl group, as well as novolak resins. European Patent Application No. 0555749 relates to a radiation sensitive composition comprising a photobase generator compound, a resin binder and a material capable of cross-liking in the presence of base. Preferred resin binders include compounds capable of imparting aqueous developability to the composition, for example resins containing polar functional groups such as hydroxyl and carboxylate. Homo- and co-polymers of N-hydroxyphenyl maleimides may be used. Among the various photobases which may be used are nitrobenzylcarbamates such as o-nitrobenzyl N-cyclohexylcarbamate. SUMMARY OF THE INVENTION The present invention is to overcome the above described problems of the prior art, and it is an object of the present invention to provide a photosensitive resin composition having an excellent film property, heat-resistance, adhesion and image-formability which does not require complex steps for preparation and does not cause contamination with chlorides. The present invention relates to a positive type photosensitive resin composition which comprises an alkali-soluble polymer (A) having at least one carboxyl group, and a compound (B) which forms an amine compound with irradiation of light; characterised in that said alkali-soluble polymer (A) is EITHER (a) a polyamic acid resin having recurring units represented by the formula (I): wherein R 1 represents a tetravalent aromatic ring group which may have a substituent, R 2 represents a divalent aromatic ring group which may have a substituent; R 3 and R 4 are in the ortho-position of one of two carbonyl groups, respectively, and each independently represents a hydrogen atom or a carboxyl group, provided that at least one is a carboxyl group, OR (b) a reaction product of at least one alicyclic tetracarboxylic dianhydride selected from the group consisting of: and an aliphatic diamino compound represented by the formula: wherein R 9 and R 10 represent a divalent hydrocarbon group; R 11 and R 12 represent a monovalent hydrocarbon group; R 9 and R 10 , R 11 and R 12 each may be the same or different; and t represents an integer of 1 or more. In the following, the present invention is explained in detail. In one variant, the alkali-soluble polymer (A) of the present invention may be a polymer having recurring units represented by the formula (I): wherein R 1 represents a tetravalent aromatic ring group which may have a substituent, R 2 represents a divalent aromatic ring group which may have a substituent; R 3 and R 4 are in the ortho-position of one of two carbonyl groups, respectively, and each independently represents a hydrogen atom or a carboxyl group, provided that at least one is a carboxyl group. In the formula (I), the tetravalent aromatic ring group of R 1 may include, for example, the following groups: wherein A represents and the divalent aromatic ring group of R 2 may include, for example, the following groups: wherein B has the same meaning as A. The above aromatic rings may have a substituent such as an alkyl group having 1 to 6 carbon atoms and an alkoxy group having 1 to 6 carbon atoms. R 3 and R 4 exist at the ortho-position relative to one of the carbonyl groups bonded to R 1 , and at least one of which is a carboxyl group and the other is a hydrogen atom or a carboxyl group. The polyamic acid resin preferably has a number average molecular weight of 3,000 to 200,000, more preferably 5,000 to 100,000, most preferably 7,000 to 50,000. If the number average molecular weight is too low, the mechanical property is lowered. If the number average molecular weight is too high, the resolution is lowered. The polyamic acid resin having the recurring units represented by the formula (I) can be prepared by reacting, for example, a tetracarboxylic dianhydride as an acidic component and a diamine as an amine component in an organic solvent. In such a case, the aromatic ring represented by R 1 and R 2 in the formula (I) represents an acidic component residue as for R 1 and an amine component residue as for R 2 . As the above tetracarboxylic dianhydride, for example, pyrromellitic dianhydride, 3,3',4,4'-benzophenonetetracarboxylic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 2,3,6,7-naphthalenetetracarboxylic dianhydride, 2,3,5,6-pyridinetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 3,4,9,10-perylene-tetracarboxylic dianhydride, 4,4'-sulfonyldiphthalic dianhydride, m-terphenyl-3,3",4,4"-tetracarboxylic dianhydride, p-terphenyl-3,3",4,4"-tetracarboxylic dianhydride, 4,4'-oxydiphthalic anhydride, 1,1,1,3,3,3-hexafluoro-2,2-bis-(2,3- or 3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis-(2,3- or 3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis-[4-(2,3- or 3,4-dicarboxyphenoxy)phenyl]propane dianhydride, 1,1,1,3,3,3-hexafluoro-2,2-bis[4-(2,3- or 3,4-dicarboxyphenoxy)phenyl]propane dianhydride, an aromatic tetracarboxylic dianhydride such as tetracarboxylic dianhydride represented by the formula (III): wherein R 7 and R 8 may be the same or different from each other and each represent a monovalent hydrocarbon group; and s represents 0 or an integer of 1 or more, a hydrogenated compound of the above aromatic tetracarboxylic dianhydride, and an alicyclic tetracarboxylic dianhydride represented by the following formulae (IV): can preferably be used. The above tetracarboxylic dianhydride can be used singly or in combination. The compound of the formula (III) may preferably be used in an amount of 1 to 30 mole %, more preferably 2 to 10 mole % based on the total acid components, and the compounds of the formulae (IV) may preferably be used in an amount of 5 to 50 mole %, more preferably 5 to 20 mole % based on the same. Among them, the aromatic tetracarboxylic dianhydride is most preferred. The benzene ring of the tetracarboxylic dianhydride may be substituted by a substituent such as an alkyl group. In addition to the tetracarboxylic dianhydride, an aliphatic tetracarboxylic dianhydride may be used to such an extent that the heat-resistance and the mechanical property are not lowered. As the above diamine, there can be preferably used, for example, an aromatic diamino compound such as p-phenylenediamine, m-phenylenediamine, p-xylylenediamine, m-xylylenediamine, 1,5-diaminonaphthalene, 3,3'-dimethylbenzidine, 3,3'-dimethoxybenzidine, 4,4'- (or 3,4'-, 3,3'-, 2,4'- or 2,2'-)diaminodiphenylmethane, 4,4'- (or 3,4'-, 3,3'-, 2,4'-or 2,2'-)diaminodiphenyl ether, 4,4'- (or 3,4'-, 3,3'-, 2,4'- or 2,2'-)diaminodiphenylsulfone, 4,4'- (or 3,4'-, 3,3'-, 2,4'- or 2,2'-)diaminodiphenylsulfide, 4,4'-benzophenonediamine, 4,4'-di(4-aminophenoxy)phenylsulfone, 1,1,1,3,3,3-hexafluoro-2,2-bis(4-aminophenyl)propane, 2,2-bis [4-(4-aminophenoxy)phenyl]propane, 3,3'-dimethyl-4,4'-diaminodiphenylmethane, 3,3',5,5'-tetramethyl-4,4'-diaminodiphenylmethane, 4,4'-di(3-aminophenoxy)phenylsulfone, 3,3'-diaminodiphenylsulfone and 2,2-bis(4-aminophenyl)propane; and an alicyclic diamino compound which is a hydrogenated compound of the above aromatic diamino compounds. Also, an aliphatic diamino compound represented by the formula (V): wherein R 9 and R 10 represent a divalent hydrocarbon group; R 11 and R 12 represent a monovalent hydrocarbon group; R 9 and R 10 , R 11 and R 12 each may be the same or different; and t represents an integer of 1 or more, may be used in combination with the above diamine compounds. The above aliphatic diamino compound may preferably be used in an amount of 1 to 30 mole %, more preferably 2 to 10 mole % based on the total amount of diamine compounds. Also as the diamine, a hydroxyl group-containing diamine such as 3,3'-hydroxybenzidine, 3,4'-diamino-3',4-dihydroxybiphenyl, 3,3'-dihydroxy-4,4'-diaminodiphenyl oxide, 3,3'-dihydroxy-4,4'-diaminodiphenylsulfone, 2,2-bis(3-amino-4-hydroxyphenyl)propane, 1,1,1,3,3,3-hexafluoro-2,2-bis-(3-amino-4-hydroxyphenyl)propane, bis-(3-hydroxy-4-aminophenyl)methane, 3,3'-dihydroxy-4,4'-diaminobenzophenone, 1,1-bis-(3-hydroxy-4-aminophenyl)ethane, 2,2-bis-(3-hydroxy-4-aminophenyl)propane, 1,1,1,3,3,3-hexafluoro-2,2-bis-(3-hydroxy-4-aminophenyl)propane, 1,3-diamino-4-hydroxybenzene, 1,3-diamino-5-hydroxybenzene, 1,3-diamino-4,6-dihydroxybenzene, 1,4-diamino-2-hydroxybenzene and 1,4-diamino-2,5-dihydroxybenzene can preferably be used. The diamine may be used singly or in combination. As the organic solvent usable in the above reaction, a polar solvent which completely dissolves the forming polyamidic acid resin is generally preferred, and there may be mentioned, for example, N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-dimethylformamide, dimethylsulfoxide, tetramethylurea, hexamethylphosphoric triamide and γ-butyrolactone. In addition to these polar solvents, ketones, esters, lactones, ethers, halogenated hydrocarbons and hydrocarbons, for example, acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, methyl acetate, ethyl acetate, butyl acetate, diethyl oxalate, dimethyl malonate, γ-butyrolactone, diethyl ether, ethyleneglycol dimethyl ether, diethyleneglycol dimethyl ether, tetrahydrofurane, dichloromethane, 1,2-dichloroethane, 1,4-dichloroethane, trichloroethane, chlorobenzene, o-dichlorobenzene, hexane, heptane, octane, benzene, toluene and xylene can also be used. The organic solvent may be used singly or in combination. The compound (B) of the present invention which forms an amine compound with irradiation of light is not particularly limited, and a compound represented by the formula (II): wherein R 5 represents an aromatic ring group; R 6 represents a monovalent organic group; X represents a hydrogen atom or a monovalent substituent, Y represents a monovalent organic group; m represents an integer of 1 through 5, and when m is 2 or more, a plural number of X's may be the same or different, can preferably be used. The aromatic ring represented by R 5 is not particularly limited, and benzene (phenylene), naphthalene and anthracene rings are preferred. The monovalent organic group represented by R 6 is not particularly limited, and a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, preferably 1 to 3 carbon atoms are preferred. The monovalent substituent represented by X is not particularly limited, and an alkyl group having 1 to 10 carbon atoms, an alkoxyl group having 1 to 10 carbon atoms, a halogen atom, a nitro group and a cyano group are preferred. The monovalent organic group represented by Y is not particularly limited, and an alkyl group having 1 to 10 carbon atoms, preferably 1 to 4 carbon atoms, a cycloalkyl group having 3 to 8 carbon atoms, preferably 3 to 6 carbon atoms, an aralkyl group having 7 to 17 carbon atoms, preferably 7 to 12 carbon atoms, and a hydroxyalkyl group having 1 to 10 carbon atoms, preferably 1 to 6 carbon atoms, are possible alternatives for Y. A process for preparation of the compound (B) represented by the formula (II) is not particularly limited, and can be carried out, for example, when the aromatic ring of R 5 in the formula (II) is a benzene ring, by reacting a benzylalcohol derivative and an isocyanate compound as shown by the formula (VI): wherein R 6 , X, Y and m have the same meaning as in the formula (II). In the reaction, a catalyst may be used if-necessary. The compound represented by the formula (II) may include, for example, the following compounds: In the present invention, it is particularly preferred to use the compound (A) wherein R 1 is R 2 is and R 3 and R 4 are both -COOH groups. Also, it is particularly preferred to use the compound (B) wherein R 5 is R 6 is -CH 3 , X is -OCH 3 , m is 2 and Y is -CH 2 CH 2 OH or a cyclohexyl group. In the photosensitive resin composition of the present invention, the compound (B) may preferably be used in the range of 1 to 250 % by weight, more preferably in the range of 50 to 170 % by weight based on the polymer (A). A coupling agent or a surfactant may be added to the photosensitive resin composition of the present invention in order to improve the adhesions to the substrate, if necessary. The photosensitive resin composition of the present invention contains the above described various components. The solid content of a coating solution containing said composition is preferably 5 to 50 % by weight, more preferably 10 to 30 % by weight, and the viscosity of the coating solution is preferably 1 to 300 poise, more preferably 30 to 200 poise. The order for mixing these components and the method for mixing these components are not particularly limited, and the composition may be applied to a substrate such as a copper-clad laminate and a silicon wafer by a dipping method, a spraying method, a screen printing method and a spinner coating method, and dried to form a film. Also, a dry film having a sandwich structure may be previously prepared by coating a flexible substrate, for example, a polyester film, with the photosensitive resin composition; drying it to laminate thereon; and then covering the laminate with a cover sheet made of polyethylene or so, and a film can be prepared on the substrate to be covered by peeling the cover sheet of the dry film. The cover sheet may not necessarily be used. By irradiating active rays on the film through a mask having required pattern, an amine compound originating from the component (B) generates at the portion of irradiation (exposed portion). The irradiated portion becomes water-soluble in the presence of the amine compound, whereas the non-irradiated portion (non-exposed portion) remains water-insoluble. As the above active rays, ultraviolet rays or visible rays are usually used. In some cases, a film can be formed similarly by irradiating ionizing radiation such as en electronic ray and a radiation. By treating the surface of thus treated film, with water as a developer, the irradiated portion which is made water-soluble in the presence of the amine compound can be removed, and the non-irradiated portion which remains insoluble remains so that the required resin pattern can be obtained. As the developer usable in the present invention, water can usually be used as above. In addition, an organic solvent, a mixed solvent of a water-soluble organic solvent and water and/or an alkali aqueous solution can be used. The organic solvent may include, for example, N-methylpyrrolidone, N-acetyl-2-pyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide, dimethylsulfoxide, hexamethylenephosphoric triamide, γ-butyrolactone, an alcohol such as methanol, ethanol and isopropanol, an aromatic hydrocarbon compound such as toluene and xylene, a ketone such as acetone, methyl ethyl ketone and methyl isobutyl ketone, an ester such as ethyl acetate and methyl propionate, and an ether such as tetrahydrofurane and dioxane. The alkali aqueous solution is a solution of a basic compound dissolved in water. As the basic compound, for example, a hydroxide, a carbonate, a hydrogencarbonate, a silicate, a phosphate, a pyrophosphate, an acetate and an amine of an alkaline metal or a quaternary ammonium can be used. As the concrete example, there may be mentioned lithium hydroxide, sodium hydroxide, potassium hydroxide, ammonium hydroxide, trimethylbenzylammonium hydroxide, tetramethylammonium hydroxide, sodium carbonate, potassium carbonate, sodium hydrogencarbonate, sodium silicate, sodium phosphate, sodium pyrophosphate, sodium acetate, monoethanolamine, diethanolamine and triethanolamine. The amount of the basic compound based on the amount of water is preferably such an amount that the sufficient difference in the solubility or in the dissolution rate is caused between the irradiated portion and the non-irradiated portion. Thus obtained pattern can be converted to a surface protective film or an interlaminar insulating film of a semiconductor, a multi-layer printed-wiring board and a high density packaging substrate each having a heat resistance by preliminarily drying at 50 to 250 °C, and then heating, i.e., post-curing at 300 to 400 °C. The photosensitive resin composition of the present invention is remarkably useful mainly in the above mentioned field of fine processing. EXAMPLES The present invention is described in detail by referring to Examples, but the scope of the invention is not limited by these Examples. Example 1 Synthesis of polyamic acid resin In a 100 ml separable flask with a stirrer, a thermometer and an inlet for introducing dry nitrogen gas, 7.8092 g (0.039 mol) of diaminodiphenyl ether (hereinafter abbreviated to as "DDE") was added to 75.4 g of N-methyl-2-pyrrolidone (hereinafter abbreviated to as "NMP") to dissolve it therein while stirring under the atmosphere of nitrogen. To the amine solution, 17.3253 g (0.039 mol) of 1,1,1,3,3, 3-hexafluoro-2,2-bis(3,4-dicarboxyphenyl)propane dianhydride (hereinafter abbreviated to as "6-FDA") was added, and the mixture was reacted at room temperature for 8 hours to have a viscous solution of a polyamic acid resin (hereinafter abbreviated to as "PA-1"). Preparation of photosensitive resin composition 1-(2-Nitrophenyl)ethyl-N-cyclohexylcarbamate in an amount of 3 g and 0.5 g of polyethyleneglycol were added to 10 g of the above synthesized polyamic acid resin solution (PA-1), and dissolved therein while stirring, followed by filtration with a 5 µm filter to have a photosensitive resin composition. Evaluation A silicon wafer was spin-coated with the above prepared photosensitive resin composition, and prebaked at 100 °C for 300 seconds to have a uniform film having a thickness of 5 µm. Then, the film was irradiated with an ultrahigh pressure mercury lamp (20 mW/cm 2 ) for 100 seconds through a mask. The film was then dipped in water to carry out a development, rinsed with water, and dried so that a positive type clear relief pattern having a high resolution was obtained. The relief pattern was thermally cured at 100 °C for 30 minutes, at 200 °C for 60 minutes, and then at 350 °C for 60 minutes to have a polyimide, without changes in the pattern. Further, on another silicon wafer was formed a coating film with a thickness of 20 µm and the film was cured by the above conditions without forming any pattern. When the cured film was peeled off from the wafer, it could be found that a tough polyimide film could be obtained. Also, a weight decrease-initiating temperature under heating of the film was 400 °C or higher whereby it can be found that the film is also excellent in heat resistance. Example 2 Synthesis of polyamic acid resin A polyamic acid resin solution (hereinafter abbreviated to as "PA-2") having the solid content of 25 % was obtained in the same manner as in Example 1 except for changing 6-FDA to 4,4'-oxydiphthalic acid (ODPA) and reacting them with equivalent amounts. Preparation of photosensitive resin composition To 10 g of the above synthesized polyamic acid resin solution (PA-2) were added 3 g of 1-(3,4-dimethoxy-6-nitrophenyl)ethyl-N-cyclohexylcarbamate and 0.5 g of polyethyleneglycol, and the mixture was dissolved while stirring, followed by filtration with a 5 µm filter to have a photosensitive resin composition. Evaluation A silicon wafer was spin-coated with the thus prepared photosensitive resin composition, and prebaked at 100 °C for 300 seconds to have a uniform film having a thickness of 5 µm. Then, the film was irradiated with an ultrahigh pressure mercury lamp (20 mW/cm 2 ) for 100 seconds through a mask. The film was then dipped in water to carry out a development, rinsed with water, and dried so that a positive type clear relief pattern having a high resolution was obtained. The relief pattern was thermally cured at 100 °C for 30 minutes, at 200 °C for 60 minutes, and then at 350 °C for 60 minutes to have a polyimide, without changes in the pattern. Further, on another silicon wafer was formed a coating film with a thickness of 20 µm and the film was cured by the above conditions without forming any pattern. When the cured film was peeled off, it could be found that a tough polyimide film could be obtained. Also, a weight decrease-initiating temperature under heating of the film was 400 °C or higher whereby it can be found that the film is also excellent in heat resistance. Example 3 Synthesis of polyamic acid resin A polyamic acid resin solution (hereinafter abbreviated to as "PA-3") having the solid content of 25 % was obtained in the same manner as in Example 1 except for changing DDE to m-phenylenediamine (hereinafter abbreviated to as "MPD") and 6-FDA to pyrromellitic acid dianhydride (PMDA) and reacting them with equivalent amounts. Preparation of photosensitive resin composition To 10 g of the above synthesized polyamic acid resin solution (PA-3) were added 3 g of 1-(3,4-dimethoxy-6-nitrophenyl)ethyl-N-cyclohexylcarbamate and 0.5 g of polyethyleneglycol, and the mixture was dissolved while stirring, followed by filtration with a 5 µm filter to have a photosensitive resin composition. Evaluation A silicon wafer was spin-coated with the thus prepared photosensitive resin composition, and prebaked at 100 °C for 300 seconds to have a uniform film having a thickness of 5 µm. Then, the film was irradiated with an ultrahigh pressure mercury lamp (20 mW/cm 2 ) for 100 seconds through a mask. The film was then dipped in water to carry out a development, rinsed with water, and dried so that a positive type clear relief pattern having a high resolution was obtained. The relief pattern was thermally cured at 100 °C for 30 minutes, at 200 °C for 60 minutes, and then at 350 °C for 60 minutes to have a polyimide, without changes in the pattern. Further, on another silicon wafer was formed a coating film with a thickness of 20 µm and the film was cured by the above conditions without forming any pattern. When the cured film was peeled off, it could be found that a tough polyimide film could be obtained. Also, a weight decrease-initiating temperature under heating of the film was 400 °C or higher whereby it can be found that the film is also excellent in heat resistance. Example 4 Synthesis of polyamic acid resin A polyamic acid resin solution (hereinafter abbreviated to as "PA-4") having the solid content of 25 % was obtained in the same manner as in Example 1 except for changing DDE to 4,4'-diaminodiphenylsulfone (hereinafter abbreviated to as "p-DDS") and 6-FDA to 3,3',4,4'-biphenyltatracarboxylic acid dianhydride (s-BPDA) and reacting them with equivalent amounts. Preparation of photosensitive resin composition To 10 g of the above synthesized polyamic acid resin solution (PA-4) were added 3 g of 1-(2-nitrophenyl)ethyl-N-cyclohexylcarbamate and 0.5 g of polyethyleneglycol, and the mixture was dissolved while stirring, followed by filtration with a 5 µm filter to have a photosensitive resin composition. Evaluation A silicon wafer was spin-coated with the thus prepared photosensitive resin composition, and prebaked at 100 °C for 300 seconds to have a uniform film having a thickness of 5 µm. Then, the film was irradiated with an ultrahigh pressure mercury lamp (20 mW/cm 2 ) for 100 seconds through a mask. The film was then dipped in water to carry out a development, rinsed with water, and dried so that a positive type clear relief pattern having a high resolution was obtained. The relief pattern was thermally cured at 100 °C for 30 minutes, at 200 °C for 60 minutes, and then at 350 °C for 60 minutes to have a polyimide, without changes in the pattern. Further, on another silicon wafer was formed a coating film with a thickness of 20 µm and the film was cured by the above conditions without forming any pattern. When the cured film was peeled off, it could be found that a tough polyimide film could be obtained. Also, a weight decrease-initiating temperature under heating of the film was 400 °C or higher whereby it can be found that the film is also excellent in heat resistance. The photosensitive resin composition of the present invention can easily be prepared without complex steps and contamination with ionic impurities. Also, it hardly affects the environment since water can be used as a developer. Furthermore, the photosensitive resin composition of the present invention has a high image-forming ability, film property and heat-resistance.

Claims: A positive type photosensitive resin composition which comprises an alkali-soluble polymer (A) having at least one carboxyl group, and a compound (B) which forms an amine compound with irradiation of light; characterised in that said alkali-soluble polymer (A) is EITHER (a) a polyamic acid resin having recurring units represented by the formula (I): wherein R 1 represents a tetravalent aromatic ring group which may have a substituent, R 2 represents a divalent aromatic ring group which may have a substituent; R 3 and R 4 are in the ortho-position of one of two carbonyl groups, respectively, and each independently represents a hydrogen atom or a carboxyl group, provided that at least one is a carboxyl group, OR (b) a reaction product of at least one alicyclic tetracarboxylic dianhydride selected from the group consisting of: and an aliphatic diamino compound represented by the formula: wherein R 9 and R 10 represent a divalent hydrocarbon group; R 11 and R 12 represent a monovalent hydrocarbon group; R 9 and R 10 , R 11 and R 12 each may be the same or different; and t represents an integer of 1 or more. The photosensitive resin composition according to claim 1, wherein the alkali-soluble polymer (A) has a number average molecular weight of 3,000 to 200,000. The photosensitive resin composition according to claim 1, wherein the polyamic acid resin is a reaction product of a tetracarboxylic dianhydride and a diamine. The photosensitive resin composition according to claim 3, the tetracarboxylic dianhydride comprises, as part of an acid component, an aromatic tetracarboxylic dianhydride represented by the formula: wherein R 7 and R 8 may be the same or different from each other and represent a monovalent hydrocarbon group; and s represents 0 or an integer of 1 or more, or a hydrogenated compound thereof. The photosensitive resin composition according to claim 3, wherein the diamine is a hydroxyl group-containing diamine compound. The photosensitive resin composition according to claim 1, wherein the compound (B) is a compound represented by the formula: wherein R 5 represents an aromatic ring group; R 6 represents a monovalent organic group; X represents a hydrogen atom or a monovalent substituent, Y represents a monovalent organic group; m represents an integer of 1 through 5 and when m is 2 or more, X's may be the same or different. The photosensitive resin composition according to claim 6, wherein R 5 is a benzene, naphthalene or anthracene ring. The photosensitive resin composition according to claim 6, wherein R 6 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; X is an alkyl group having 1 to 10 carbon atoms, an alkoxyl group having 1 to 10 carbon atoms, a halogen atom, a nitro group or a cyano group; and Y is an alkyl group having 1 to 10 carbon atoms, a cycloalkyl group having 3 to 8 carbon atoms, an aralkyl group having 7 to 17 carbon atoms or a hydroxyalkyl group having 1 to 10 carbon atoms. The photosensitive resin composition according to Claim 6, wherein the compound (B) is a compound selected from the group consisting of: The photosensitive resin composition according to Claim 1, which comprises 1 to 250 % by weight of the compound (B) based on the polymer (A). The photosensitive resin composition according to Claim 3,wherein the tetracarboxylic acid anhydride is at least one selected from the group consisting of pyrromellitic dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride and 4,4'-oxydiphthalic anhydride. The photosensitive resin composition according to Claim 3, wherein the diamine is at least one selected from the group consisting of m-phenylenediamine, 4,4'-diaminodiphenyl ether, 3,4'-diaminodiphenyl ether, 4,4 '-diaminodiphenylsulfone and 3,4'-diaminodiphenylsulfone.

Inventors: HAGIWARA HIDEO, KAJI MAKOTO, KOJIMA YASUNORI, HAGIWARA, HIDEO, KAJI, MAKOTO, KOJIMA, YASUNORI
Applicants: HITACHI CHEMICAL CO LTD, HITACHI CHEMICAL CO., LTD.
Application year: 1994
Main classification: G03F7
IPC codes: G03F7