METHOD OF AND APPARATUS FOR JOINING METAL PIECES

Abstract: According to the present invention, a rear end portion of a preceding metal piece and a front end portion of a subsequent metal piece are heated, pressed and joined prior to the finishing hot rolling thereof, by placing the two metal pieces so that the rear end portion of the preceding metal piece and the front end portion of the subsequent metal piece are spaced from and opposed to each other, heating the metal pieces with an alternating field, which passes through the metal pieces in the direction of the thickness thereof, generated in the opposed surface-side end regions of the metal pieces, and partially generating an alternating field, which extends in the direction opposite to the direction in which the previously-mentioned alternating field extends, in the opposed surface-side end regions which agree with either metal piece-existing regions or regions outside of the widthwise ends of the metal pieces, whereby the whole of widthwise parts of the opposed surface-side end regions of the metal pieces are heated uniformly to enable the two metal pieces to be joined reliably.

Description: TECHNICAL FIELD The present invention relates to a metal piece joining method useful for continuous hot rolling, by which a preceding metal piece and a succeeding metal piece are heated and joined with each other at their ends to continuously carry out hot finishing rolling, and also to a joining apparatus which is directly used for carrying out the method. BACKGROUND ART Conventionally, in a hot rolling line for metal pieces (for example, steel, aluminum or copper), since the metal pieces have been extracted one by one from a heating furnace, there occurred various problems particularly in the finishing rolling process, as follows. 1) A biting failure at the front end of a metal piece. 2) A defective stamping at the rear end of a metal piece (a phenomenon that a corner at the rear end of a thin metal piece is bent). 3) A traveling problem of the front end of a metal piece occurring on a run-out table. 4) A defective dimension at the front and rear ends of metal pieces. As means for solving the above-mentioned problems, there has been proposed a so-called endless rolling in which metal pieces to be rolled are joined at their rear and front ends before the finishing rolling, and continuously supplied to the fomoshinh rolling line to carry out the hot rolling. As prior documents in this regard, a number of propositions can be found, for example, in Japanese Patent Laid-open Publication Nos. 60-244401, 61-144203, 62-234679, 4-89109, 4-89115 and 4-89110. When carrying out the endless rolling of metal pieces, the following process has been generally performed. That is, firstly, on the entry side of a rolling equipment, a small gap is provided between a preceding metal piece and a succeeding metal piece at the ends thereof and these metal pieces are opposed substantially in parallel with each other. Further, a portion in the vicinity of the end of each metal piece is clamped and supported by clamps, and the end regions on the opposed faces of the metal pieces, which are portions to be joined, are heated by a heating means. The both metal pieces are then pressed against each other to be joined. In the joining method for metal pieces using such a process, various disadvantages which will be described below have still remained and an improvement in this regard has been desired. 1) In the joining form of this type, there is provided an inductor having a pair of magnetic poles vertically sandwiching the portions to be joined in the metal pieces. With the inductor, an alternating magnetic field running through the metal pieces in the thickness direction thereof is applied, and a surface layer at the portions to be joined, or on the opposed surfaces in particular is intensively heated by the induced current generated at this time. The induced current is, however, hard to flow at corners of the front and rear ends of the metal pieces, and the heating temperature at the portions to be joined thus gradually lowers toward the wide ends. Thus, there is such a disadvantage that the portions to be joined cannot be joined over the full width thereof when pressing the metal pieces against each other. In this case, the wide ends having a low temperature function as a resistance when pressing the metal pieces against each other, if the temperature at the portions to be joined does not reach a target heating temperature, so that a pressing apparatus having a capacity above a necessary level must be installed. Also, since a sufficient joining strength cannot be secured, the joined portions are gradually separated as the rolling proceeds and the metal plate are ruptured so that a serious accident may occur. In order to solve such a problem, it is most effective to continue the heating until the temperature at the corners of the steel pieces reaches a target value. However, since the temperature in regions other than the corners (i.e., central regions in the plate width direction) reaches a melting temperature and the metal pieces are melted down in these regions, excellent joined portions cannot be obtained. In addition, such a heating may deteriorate the surface quality of the plate at the portions after rolling which correspond to the joining portions or other portions close thereto, and the input electrical power has to be increased as well. 2) In the induction heating method using the inductor, since a variation rate of magnetic fluxes (a variation rate of the number of magnetic fluxes) is proportional to the current to be induced, the variation rate becomes large as the number of magnetic fluxes running through the metal pieces is large at the peak of the alternating current which flows in a coil of the inductor, thus increasing the scale of the current. Further, since a vertical component in the magnetic flux generated by the inductor for the surface of the magnetic pieces advantageously contributes to the generation of the induced current, the induced current can be increased as the magnetic flux running through the magnetic pieces becomes vertical. However, in the metal piece heating and joining to which the induction heating method is applied, if the positional relationship between the inductor and the ends of the respective metal pieces (the position of the inductor in the longitudinal direction of the metal pieces in particular) is inadequate, the number of magnetic fluxes running through the metal pieces is insufficient and the vertical component of the magnetic flux is also disadvantageously reduced. Further, for example, in a conventional method disclosed in Japanese Patent Laid-open Publication No. 62-234679 mentioned above, this kind of disadvantage is not considered therein, and the satisfactory heating speed cannot be obtained depending on the positional relationship between the inductor and each metal piece, involving a prolongation of the heating time. Also, since the preceding metal piece and the succeeding metal piece are not uniformly and equally heated, an excellent joining cannot be realized. 3) When heating the metal pieces, if the preceding metal piece and the succeeding metal piece are different in the initial temperature or in the plate thickness, or if the metal pieces having different melting points are heated, an appropriate heating cannot be performed in accordance with each metal piece, and a sufficient strength cannot be given to the joined metal pieces. In such a case, the plates may be ruptured from their joined portions during rolling, resulting in a serious accident. 4) There is proposed a joining method employing a so-called non-contact heating in which the preceding and succeeding metal pieces are heated with a space therebetween and the up-setting is then performed for joining (Japanese Patent Laid-open Publication No. 60-244401). According to this method, although the uniform magnetic flux must be given to the metal pieces over the full width thereof, the uniform magnetic flux is restrictedly given to the width of not more than 1000 mm mainly from a viewpoint of design in the power supply of the inductor. In the case of a larger width, for example, a width of 1900 mm, a pair of inductors are required (the limit in the capacity of one inductor is 2000 through 3000 kW, and practical use of an inductor which has a capacity of not less than 4000 kW and can deal with the width of 1900 mm is difficult). It is therefore difficult to give a uniform magnetic flux running through the metal piece over the full width thereof. 5) For heating the preceding and succeeding metal pieces in a relatively short time for joining, there is an induction heating rolling method, as a heating means, in which air-core type coil is used to induction-heat the rear end of the preceding metal piece and the front end of the succeeding metal piece and the both ends of these metal pieces are then pressed against each other for joining (Japanese Patent Laid-open Publication No. 60-244401). In this method, however, since the metal pieces to be joined are inserted into the coil and heated, this method cannot be applied to a metal piece whose dimension is larger than the inner dimension of the coil. On the other hand, in the case where both metal pieces have a small width, such a problem does not occur though a part of the magnetic fluxes does not contribute to heat the metal pieces, thereby deteriorating the heating efficiency for the input power. Further, in connection with the above item 4), in the case where the metal pieces are heated using a plurality of inductors, since the magnetic flux is not generated from a portion corresponding to a part between inductors adjacent to each other, the magnetic flux running through the metal piece is locally decreased and the temperature rise at this portion is insufficient. It is therefore important to make a space between the adjacent inductors as small as possible, but the space between the adjacent inductors cannot be reduced at a stage of securing facilities. Thus, the temperature distribution of the metal pieces in the width direction thereof inevitably becomes uneven. 6) Although a preferred temperature at the opposed faces (the end faces) of the metal pieces can be usually within a range of approximately 1350 to 1400°C, in the case where the metal pieces joined at such a temperature are rolled by a finishing rolling mill composed of a plurality of stands which functions after joining with a draft percentage increased by 10 times or more, all kinds of steel cannot be rolled without causing rupture at the joining portions until the completion of rolling. In the endless rolling of the metal pieces, since the timing of the processing for joining the metal pieces must match with that of the rolling process, it is general to provide a movable joining apparatus placed on the entry side of a group of finishing rolling mills so that it can follow the movement of the steel pieces, or to provide an apparatus such as a looper having a timing buffer function between the joining apparatus and the rolling facilities. This involves an extension of the line or provision of new apparatuses, thereby disadvantageously increasing the facility cost. However, in regard of this problem, a proposition disclosed, e.g., in Japanese Patent Laid-open Publication No. 4-89120 has been given and the problem has been already improved. The present invention intends to achieve the following objects. 1) On the entry side of the hot finishing rolling facilities, the preceding metal piece and the succeeding metal piece are uniformly heated over the full width thereof and, when pressing the metal pieces against each other, the joining is carried out until a sufficient strength can be obtained (until such a strength that the plates are not ruptured during rolling can be secured), thereby performing a stable rolling operation. 2) The both metal pieces are heated in an appropriate range of temperature and joined with a sufficient strength being given thereto irrespective of temperature or thickness of the metal pieces to be joined or kinds of the plates. The above-mentioned objects are achieved according to the invention by the subject matters of claims 1, 6, 9, 10, 18 and 19. Embodiments of the invention are defined in the depending claims. Document JP-A-5-192 775, which is considered to represent the closest state of the art, forms the basis for the preambles of the independent claims. The invention is described in the following by way of example and with reference to the accompanying drawings in which Fig. 1 is an explanatory view showing the point of heating according to the present invention; Fig. 2 is an explanatory view showing the point of heating according to a prior art; Fig. 3 is an explanatory view showing the state of heating metal pieces; Fig. 4 is an explanatory view showing the state where cracks are generated in a joined portion of metal pieces; Fig. 5 is a view typically showing a structure of a circuit; Fig. 6 is a view showing a structure of an apparatus preferable for carrying out the present invention; Fig. 7 is a view showing the state of joining metal pieces; Fig. 8 is an explanatory view showing the state where joined metal pieces are ruptured; Fig. 9 is a view showing a structure of an apparatus according to the present invention; Fig. 10 is a view showing a primary part of the apparatus according to the present invention; Fig. 11 is an explanatory view showing the point of joining metal pieces according to the present invention; Fig. 12 is an explanatory view showing the point of joining metal pieces according to the present invention; Fig. 13 is a view showing an example of a conductive members; Fig. 14 is a view showing an example of a member consisting of magnetic substance; Fig. 15 is a view showing an example of a member consisting of magnetic substance; Fig. 16 is a view showing an example of a member consisting of magnetic substance; Fig. 17 is a view showing an example of a member consisting of magnetic substance; Fig. 18 is a view showing a reverse magnetic field generation portion of a circuit; Fig. 19 is a view showing a reverse magnetic field generation portion of a circuit; Fig. 20 is a view showing a structure of an equipment for performing continuous hot rolling to metal pieces; Fig. 21 is a view showing a structure of a primary part of a joining apparatus according to the present invention; Fig. 22 is an explanatory view showing the state where metal pieces are heated; Fig. 23 is a view showing a structure of a primary part of a joining apparatus according to the present invention; Fig. 24 is an explanatory view showing a case where metal pieces having different widths are joined; Figs. 25(a), (b) and (c) are explanatory views showing cases where metal pieces are heated and joined in accordance with the present invention; Figs. 26(a), (b) and (c) are explanatory views showing cases where metal pieces are heated and joined in accordance with the present invention; Fig. 27 is an explanatory view showing the point of joining metal pieces in accordance with the present invention; Fig. 28 is a view showing an example in which metal pieces are heated using a single inductor; Fig. 29 is a view showing an example in which metal pieces are heated using a single inductor; Fig. 30 is a view showing a distribution of a temperature rising speed in end portion of a metal piece in the width direction thereof; Figs. 31(a) and (b) are views showing an example in which metal pieces are heated and joined by arranging members consisting of magnetic substance; Fig. 32 is a view showing an example in which metal pieces are heated and joined by arranging members consisting of magnetic substance; Fig. 33 is a view showing the relationship between the width dimension of a member consisting of magnetic substance/osmotic depth of an induced current, and the length of joining failure; Fig. 34 is a view showing a structure of a primary part of a joining apparatus to which members consisting of magnetic substance are arranged; Fig. 35 is an explanatory view showing the point of movement of members consisting of magnetic substance; Fig. 36 is a view showing a structure of an electric circuit; Fig. 37 is a graph showing the relationship between the plate width and the temperature at a joining face; Fig. 38 is a graph showing the relationship between the plate width and the temperature rising speed ratio; Fig. 39 is a graph showing the relationship between the distance from an end of a plate and the temperature rising speed ratio; Fig. 40 is a graph showing the relationship between the distance in a width direction of a metal piece and the temperature at a joining face; Fig. 41 is a graph showing the relationship between the distance in a direction of a metal piece width and the temperature of a joining face; Fig. 42 is graph showing the relationship between the distance in a direction of a metal piece width and the calorific power ratio at a joining face; Fig. 43 is a view showing a state in which an inductor is arranged; BEST MODE FOR CARRYING OUT THE INVENTION In case of heating metal pieces to be joined by generating an alternating magnetic field running through the metal pieces in a thickness direction thereof, the present invention partially generates another alternating magnetic field reversed from the above alternating magnetic field in either of a region where the metal pieces exist or another region outside the width ends of the metal pieces to adjust the temperature distribution in the plate width direction. The present invention will now be described in detail hereinafter with reference to the drawings. Fig. 1 shows a structure of a joining apparatus preferable for adjusting the temperature distribution at ends of metal pieces in the width direction thereof in case of heating and joining the metal pieces. In the drawing, reference numeral 1 denotes a metal piece (referred to as a preceding metal piece hereinbelow) precedently carried; 2, a metal piece (referred to as a succeeding metal piece hereinbelow) carried after the preceding metal piece 1; 3, at least a pair of inductors for heating composed of a coil c and a core t and sandwiching the preceding metal piece 1 and the succeeding metal piece 2 in the thickness direction thereof with a gap D (although the gap D is a space, any electrical insulator may be provided thereto) therebetween. An alternating magnetic field running through the metal pieces in the thickness direction thereof is generated by the inductors 3 to heat the end region of the opposed faces until the temperature in this region reaches a predetermined value. Further, reference numeral 4 designates a power supply of the inductors 3; and 5, a reverse magnetic field generation portion of a reverse magnetic field generation circuit (an electric circuit). A lead wire 5a is connected to the both ends of the loop type reverse magnetic field generation portion 5 to form a closed circuit including these ends, and an alternating magnetic field reversed from the alternating magnetic field produced by the inductors 3 is generated by flowing an induced current when heating by the inductors 3 or by positively flowing a current (from any other power supply, for example). In addition, reference numeral 6 represents a switch having an open/close controller r; and 7, a variable resistor. As shown in Fig. 2, the preceding metal piece 1 and the succeeding metal piece 2 are opposedly provided with a gap g therebetween, which is a gap of approximately a few to tens mm and may be an interval of space, or any other electrical insulator may be provided to this gap. When the alternating magnetic field running in the plate thickness direction is generated by the inductors 3, a current e as shown in Fig. 3 is induced by the alternating magnetic field in the end region of the opposed faces of the metal pieces which will be joined to each other, and this portion is heated in a extremely short time by the heat produced at this time. Since the current e is difficult to flow at corners f of the metal pieces 1 and 2, the degree of temperature rise is small at the corners f. If the heating and temperature rise are tried until the temperature at which the joining is possible, the central region in the plate width direction is likely to be melted down. On the other hand, even if the joining of the metal pieces only in the central region thereof is tried, cracks such as shown in Fig. 4 may be developed during rolling because of insufficiency of the joining strength in the width end region, and there is such a disadvantage that the rolling cannot be continued. In the present invention, since portions to be joined are heated by the inductors 3 and the alternating magnetic field reversed from the alternating magnetic field d produced by the inductors 3 is generated by such a reverse magnetic field generation circuit as shown in Fig. 5 (by flowing the induced current in the circuit by main magnetic fluxes of the inductors 3 or positively flowing such a current that the reverse magnetic field is generated) in a region where the temperature largely varies (a region which is located in the width direction of the metal pieces and where the temperature reaches a target heating temperature faster than in any other regions) and in a central region in the plate width direction where the temperature greatly raises in particular to weaken the strength of the magnetic field in the portions to be joined, an excessive heating in these portions can be suppressed. Although the heating time is prolonged to some extent because the heating is carried out with such a reverse magnetic field being generated, the corners of the metal pieces at which the temperature rise is difficult can be heated until the temperature reaches a predetermined range without a fear of melt down in the central region in the plate width direction. As a result, the temperature distribution in the width direction becomes substantially uniform, thereby ensuring the satisfactory joining strength. In a concrete structure of an apparatus for adjusting the temperature, as shown in Fig. 6, a plurality of reverse magnetic field generation portions 5 are previously arranged in parallel with the plate width direction of the metal pieces 1 and 2, and switches 6 to be connected to the reverse magnetic field generation portions 5 which are located in a region where suppression of the temperature rise is desired when heating are closed to generate a reverse magnetic field. Further, if the quantity of current flowing in the reverse magnetic field generation circuit is varied by adjusting a variable resistor 7 as shown in Fig. 1, for example, the scale of the reverse magnetic field is adjusted, thereby further accurately adjusting the temperature. In the case where a plurality of reverse magnetic field generation circuits are provided, it is effective to provide a variable resistor 7 for each circuit for adjusting an impedance of each circuit. It is also possible to additionally provide a coil, a capacitor or others, and at least one of these members may be used to adjust the impedance of each reverse magnetic field generation circuit. If a desired impedance is given to each reverse magnetic field generation circuit by a variable resistor 7, for example, a desired strength of the reverse magnetic field can be obtained. Also, phases of the respective circuits are unified, thereby relatively freely adjusting the temperature of the metal pieces in the width direction thereof. In the state of arrangement as shown in Fig. 6, in the case where the reverse magnetic field generation portions 5 are arranged outside the plate width ends of the metal pieces and the reverse magnetic generation circuits are closed to flow the induced current therethrough, magnetic fluxes outside the width ends of the magnetic pieces can be converged at the corners f of the magnetic pieces, and it is hence extremely advantageous to enhance the heating efficiency at the corners f. When heating the metal pieces, the metal pieces may be pressed against each other (the pressing may be carried out while heating or after heating). In such a case, the preceding metal piece 1 and the succeeding metal piece may be joined being shifted from each other (this state is referred to as dislocation). When the dislocated portion is caught in a roller, an end of one metal piece is bent toward an end of the other metal piece. The dislocated portion deeply encroaches upon a sound portion which will be a product as the number of rolling passes increases as shown in Fig. 8, whereby a thin portion is locally formed. On the other hand, the plate is ruptured due to a variation in a tensile force between stands during rolling, and the rolling may not be continued. In the present invention, therefore, a dislocation preventing plate 8 having notches u whose tips are opened along the width direction of the metal pieces 1 and 2 is provided as shown in Fig. 9 to join the metal pieces 1 and 2. In Fig. 9, by connecting the dislocation preventing plate 8 to each clamp 9 having a positioning function for the metal pieces 1 and 2, vertical dislocation of the metal pieces 1 and 2 which can be caused during pressing can be suppressed, so as to minimize the dislocation. The dislocation preventing plate 8 can avoid the temperature rise of itself during heating the metal pieces 1 and 2 and has the notches u for securing the strength as a pressure plate. When the reverse magnetic field generation portion 5 is engaged with each notch u and the reverse magnetic field is appropriately generated by each reverse magnetic field generation circuit including the reverse magnetic field generation portion, the entire area of the portions of the metal pieces which will be joined can be substantially uniformly heated. Fig. 10 shows a primary part in a state where the reverse magnetic field generation portions 5 are provided on the dislocation preventing plate 8. As shown in Fig. 10, when loops are formed by closing the switches 6 provided at positions where the suppression of heating is desired, a current e' flows in each reverse magnetic field generation portion 5 and each lead wire 5a in such a direction that the magnetic flux (reverse magnetic flux) which is directed to cancel out the main magnetic flux is generated by the action of electromagnetic induction. In this case, the main magnetic flux is weakened by the reverse magnetic flux to suppress the temperature rise of the metal pieces at portions where the switches 6 are closed. Fig. 11 shows a structural example of such an apparatus that the degree of temperature rise in the central region of the metal pieces 1 and 2 in the width direction thereof is decreased and the magnetic flux outside the width ends of the metal pieces is converged at the corners f. Further, Fig. 12 shows a structural example of an apparatus which can decrease the degree of temperature rise only in the central region of the metal pieces 1 and 2 in the width direction thereof. As the dislocation preventing plate, SUS304 and others can be adopted, though any other material having a strength at a high temperature such as titanium, tungsten and others may be used. In this invention, although the U-shaped conductive member (such as Cu) is exemplified as the reverse magnetic field generation portion 5 of the reverse magnetic field generation circuit, a coil type member such as that shown in Fig. 13 can be adopted. In this case, the effect is enhanced as the number of winds increases, though the winds are not restricted to any particular number. In order to increase a value of the current flowing in each reverse magnetic field generation circuit without additionally providing unnecessary units, in this invention, as shown in Fig. 14 or 15, a member M consisting of magnetic substance (a silicon steel plate or others) may be provided within each reverse magnetic field generation portion 5. Further, in order to prevent the member M from being heated, it is preferable to obtain a structure in which a plurality of members M are superimposed one above the other through insulating films as shown in Figs. 16 and 17. Note that such a plate type superimposed body (magnetic substance) as shown in Fig. 16 may be provided in each reverse magnetic field generation circuit having a coil type reverse magnetic field generation portion 5 shown in Fig. 17, instead of a cylindrical superimposed body (magnetic substance). Figs. 18 and 19 show examples in which the members M consisting of magnetic substance are assembled in the reverse magnetic field generation portions 5 of the reverse magnetic field generation circuits. Fig. 20 shows an equipment for performing continuous hot rolling to the metal pieces, and a joining apparatus A preferable for embodying this invention is provided, for example, between pinch rolls 11 and 12 on the delivery side of a cutting apparatus (a shear or others) 10. In Fig. 20, reference numeral 13 denotes a rewinder for rewinding a metal piece wound in a coil form; 14, a pinch roll; 15, a leveler; 16, a scale breaker; and 17, a group of finishing rolling mills. If the joining apparatus A is of a fixed type in this equipment, a looper is provided on the entry side of the scale breaker 16. Each reverse magnetic field generation circuit constituted by the reverse magnetic field generation portion 5 may be maintained closed (the switch 6 is closed) by the open/close controller r from an initial stage when heating the metal pieces, or may be closed during heating. The usage of the circuit is not restricted to a specific procedure. Although the above has been described in connection with the case where the degree of temperature rise is suppressed especially in the region where the temperature is locally increased when heating the metal pieces, the temperature in this region can be precedently increased by generating in the circuit the alternating magnetic field whose direction is same with that of the alternating magnetic field produced by the inductors 3 (in this case, the current is positively supplied to the circuit). The description will now be given as to a case where an apparatus having such a structure as shown in Fig. 21 is used to improve the heating efficiency at the width ends of the metal pieces. In Fig. 21, reference numeral 18 designates a conductive member which has been described as an example of the plate, and each member 18 is provided between magnetic poles of the inductor 3 and provided outside the ends of the metal pieces 1 and 2 in the width direction thereof with a gap t 1 between the members 18 and the metal pieces 1 and 2. In this case, the gap t 1 between may be an interval of space, or any electrical insulator may be provided herein. The preceding metal piece 1 and the succeeding metal piece 2 are clamped by clamps 19 and 20 with a space g, namely, a small gap being provided between the ends of the opposed faces of the metal pieces 1 and 2, and are heated by generating the alternating magnetic field running through the metal pieces 1 and 2 the thickness direction thereof by the inductor 3 having a pair of magnetic poles vertically sandwiching the metal pieces 1 and 2. At this time, the induced current caused due to the alternating magnetic field also flows in each conductive member 18, and the temperature is increased at the same speed with that in the central region of the pieces 1 and 2 at the corners of the metal pieces where the temperature is not likely to be increased. By providing each conductive member 18 in close proximity to one side of the metal pieces, the entire end region of the opposed faces to be joined can be heated at the same speed (a uniform heating over the full width). The reason thereof is as follows. In the first place, in the conventional heating and joining method in which the conductive members 18 are not provided, the quantity of magnetic fluxes is small at ends of the metal pieces, which will be joined, in the width direction thereof, so that the induced current e flows in the circular form as shown in Fig. 22. Even if the skin effect of the induced current flowing in each end of the metal pieces 1 and 2 can be expected, the induced current is difficult to flow through the end of each metal piece in the width direction thereof, whereby the temperature rise is insufficient. As a result, even though the rear end of the preceding metal piece and the front end of the succeeding metal piece are opposedly joined to each other, the joining strength is low at the ends of the joined portions in the width direction of the steel pieces. In the rolling operation to be subsequently performed, cracks produced at the ends propagate to the central portion in the width direction, resulting in the rupture. In the case where the conductive members 18 are provided with a space t 1 between the both width ends of at least one of the preceding metal piece 1 and the succeeding metal piece 2 and the conductive members 18 in accordance with the invention as shown in Fig. 21, however, the alternating magnetic field produced between the magnetic poles of the inductor 3 also runs through the conductive members 18, thereby generating the induced current e in each member 18. Since this induced current and the induced current generated in the metal pieces 1 and 2 flow in opposed directions in the region where these currents are in close proximity to each other, they are attracted to each other. The induced current produced in the metal pieces consequently flows to be closer to the ends of the metal pieces in the width direction thereof. The temperature rising speed at the ends of the metal pieces in the width direction thereof becomes closer to the temperature rising speed in the central region of the same in the width direction thereof, and hence the temperature can be substantially uniformly increased to a value in the entire region of the portions to be joined in the width direction. Further, by securing the sufficient pressing force when pressing the metal pieces against each other, the complete joining can be carried out over the full width of the metal pieces including the ends of the metal pieces in the width direction thereof. As for the conductive member suitable for the invention, the desired object can be attained only if any member can generate the induced current having a predetermined scale, the member is not thus restricted to a specific type. However, a copper plate produces less heat due to the induced current and is inexpensive, and hence it is preferable. Further, since a material having a high melting point such as a tungsten plate or a graphite plate has a durability against heat, such a material can also be used. Furthermore, a steel plate or an Al plate can be used for a long time if a cooling means is additionally provided. Although Fig. 21 shows an example in which each conductive member 18 is provided over the preceding metal piece 1 and the succeeding metal piece 2, the invention is not restricted to the example in this figure. The same effect can be obtained when separate conductive members 18a and 18b are provided to the rear end of the preceding metal piece and the front end of the succeeding metal piece, respectively. In this case, it is particularly advantageous when the metal pieces having different widths are joined. In regard of the width dimension of the conductive member, when the dimension is too small, generation of the induced current is difficult even though the magnetic flux runs through the member from the inductor, thereby requiring such a width that the induced current can be produced. The width of the conductive member can be appropriately changed only if this condition is satisfied. The member is not restricted to have specific thickness and length. The space t 1 between each conductive member and the metal piece must be provided so that the induced current produced in the metal piece and the induced current generated in the conductive member are attracted to each other and the conductive member and the metal piece are in close proximity to each other. Specifically, the space t 1 may be over 10 mm, though it may preferably be set to 3 through 5 mm. Fig. 24 illustrates an example in which the metal pieces having different width dimensions are joined with the centers of the metal pieces in the width directions thereof being matched. When the alternating magnetic field generated by the inductor 3 runs through each conductive member 18, the induced current is produced in the member 18. The induced currents produced in the metal pieces 1 and 2, therefore, flow in the vicinity of the ends of the metal pieces in the width direction thereof by the interaction of the induced current in the member 18 and the induced currents generated in the metal pieces, enabling a uniform heating over the entire area in the plate width direction. Although the desired object can be attained by providing the conductive members 18 only at the both width ends in the end portion of the narrow metal pieces as shown in Fig. 24, the effect can be further enhanced by additionally providing the conductive members at the both width ends of the wide metal piece as indicated by a two-dotted line in Fig. 24. As apparent from the above-mentioned action and effect of the conductive member 18, in the invention, the magnetic field generated by the inductor having at least a pair of magnetic poles must run through the conductive member 18. That is, the conductive member 18 must be provided in such a region that the magnetic flux produced between the magnetic poles of the inductor 3 runs therethrough. As viewed from the relationship between the width of each metal piece and the width of the inductor, in this invention, it is preferable to provide the inductor in such a manner that the inductor overlaps on the metal pieces and the magnetic flux generated by the inductor runs through the metal piece and at least a part of the conductive member. Specifically, it is preferable that the inductor (core) having a width dimension larger than that of the metal pieces to be joined is used so as to protrude from the metal pieces at the width ends thereof, and the opposed magnetic poles of the inductor face to the metal pieces and the conductive members provided to the width ends of the metal pieces. This means that the metal pieces are provided inside the ends in the width direction at which the quantity of magnetic fluxes is apt to be decreased, and this arrangement is extremely effective for uniformly heating the metal pieces in the width direction thereof. In the case where the width direction of the metal pieces used for joining is larger than that of the inductor, a plurality of inductors are preferably aligned in the width direction of the metal pieces so as to protrude from the metal pieces at their width ends. Figs. 25(a), (b) and (c) show an example in which a current whose phase is substantially same with that of the induced current generated in the metal pieces positively flows in the conductive members from outside. Fig. 25(a) is a top plan view showing a region in which the rear end of the preceding metal piece and the front end of the succeeding metal piece are opposed to each other; Fig. 25(b), a sectional view taken along the A-A line in Fig. 25(a); and Fig. 25(c), a sectional view taken along the B-B line in Fig. 25(a). The inductor 3 shown in Fig. 25 is obtained by winding coils c around a core t constituting a pair of magnetic poles sandwiching the metal pieces and has a width larger than those of the preceding metal piece 1 and the succeeding metal piece 2. According to the inductor having such a structure, since the entire area of the metal pieces in the width direction are positioned between the magnetic poles, the magnetic field generated by the inductor 3 can effectively act on the metal pieces. Note that such an inductor is also disclosed in Japanese Patent Laid-open Publication No. 4-89109. In Fig. 25, when the (alternating) current whose phase is the same with, but whose direction is reversed from, those of the induced current is supplied from an external power supply 22 to the conductive members 18, the induced current circulating in the metal pieces flows to the width ends thereof, enabling heating the entire region in the width direction. As similar to Fig. 25, Figs. 26(a), (b) and (c) show an example in which the current is supplied from outside to the conductive members 18 to uniformly heat the metal pieces in the full width direction. Figs. 26 shows the case where the metal pieces each having a width larger than that of the inductor 3 are heated. In the example illustrated herein, a pair of inductors 3 shown in Figs. 25 are prepared and arranged along the width direction of the metal pieces to carry out heating. Fig. 26(a) is a top plan view showing an apparatus; Fig. 26(b), a sectional view taken along the A-A line in Fig. 26(a); and Fig. 26(c), a sectional view taken along the B-B line in Fig. 26(a). In the example shown in Fig. 26, as similar to Fig. 25, the inductors 3 each having a substantially C-shaped core t are provided at the ends of the metal pieces to be joined, and the conductive members 18 are provided at the both ends of the metal pieces at an interval of space. Also, the current whose phase is same with that of the induced current generated in the metal pieces is supplied from the external power supply 22 to the members 18. In Figs. 25 and 26, although the description has been given to the case where the inductor having a larger width dimension than those of the metal pieces to be joined is used or the case where at least a pair of inductors are used to heat the metal pieces, the present invention is not restricted to the illustrated examples. Since the scale of the current supplied from the external power supply to the conductive members is not limited, it is possible to flow the current which is sufficiently large for uniformly heating the ends of the metal pieces in the full width direction, and there is no problem if an inductor whose width is smaller than those of the metal pieces is used. In the present invention, the metal pieces are heated and joined in accordance with the above-mentioned points. As a combination of these points, there is adopted a method by which the rear end of the preceding metal piece and the front end of the succeeding metal piece are positioned in close proximity with a space (small gap) therebetween and, after heating is performed until the temperature reaches a target value, the power input to the inductor is stopped to carry out the pressing, or a method by which the input power is lowered to such a level that no spark is produced if the temperature at the portions to be joined reaches the target value, and pressing is started while continuing heating. The description will now be given as to the case where the conductive members are brought into contact with the both width ends of either the rear end of the preceding metal piece or the front end of the succeeding metal piece and the heating efficiency at the width ends of the metal pieces is improved by the members. Referring to Fig. 27, in case of heating the preceding steel piece 1 and the succeeding steel piece 2, when the conductive members 23 are previously pressed against the both width ends of at least one of the metal pieces in the vicinity of the end thereof, the induced current generated in the preceding metal piece 1 and the succeeding metal piece 2 also flow in the members 23. The temperature at the both width ends, i.e., the corners of the metal pieces increases at the same speed with that in any other regions by the Joule heat generated at this time, and the problems that the joining failure occurs or the strength in the joining portions is insufficient due to the resistance at the heat defective portion are eliminated. Since each conductive member 23 shown in Fig. 27 is likely to be melted and fused during heating the metal pieces if its melting point is same with or lower than that of the metal pieces, it is preferable to use a material having a higher melting point than that of the metal pieces, for example, tungsten or carbon. Further, in regard of a size of each conductive member, the thickness of the member is preferably equal to that of the metal pieces to be joined, and it is preferable to adapt such a width that the temperature rise at the ends of the metal pieces in the width direction thereof is not insufficient when heating is carried out without the conductive members. Further, the length of the member is preferably not less than a lapping length as viewed from the top plan of the core of the inductor and the metal pieces to be heated. In case of heating the metal pieces, the spark is likely to be generated between the conductive members and the metal pieces, Thus, it is particularly preferable to increase the bearing to or above 2 kg/mm 2 and push the conductive members against the metal pieces in advance. Although Fig. 27 shows the example in which the metal pieces are heated by using a pair of inductors, it is needless to say that the same effect can be obtained by using a single inductor such as that shown in Fig. 28 to perform heating. Fig. 30 shows for reference a distribution of the temperature rising speed (which is measured at a point spaced apart from the end face by 1.5 mm and positioned in the center in the plate thickness direction on the metal piece) in the plate width direction in the case where two metal pieces each consisting of stainless steel of SUS304 and having a thickness of 30 mm are heated by using the inductor having a core whose size is 240 × 1000 mm as shown in Fig. 29 under such conditions that distances between the metal pieces and the core is 90 mm on the upper side and 90 mm on the lower side and the input power is 980 kW. The degree of the temperature rise is particularly small at the corners of the metal pieces as compared with any other regions. Therefore, even when the metal pieces are subjected to continuous rolling after being joined by the inductor having such a heating characteristic, cracks are developed in the joined portion as the rolling proceeds, and it is obvious that the joined portion is inevitably ruptured over the full width. The description will now be given as a case where, when heating the metal pieces, the density of magnetic fluxes of the alternating magnetic field is increased and the heating efficiency at the width ends of the metal pieces is improved by members each consisting of magnetic substance provided between each metal piece and the inductor to uniformly heat the entire region in the width direction with reference to Figs. 31(a) and (b) and Fig. 32. In case of heating the metal pieces by the inductor 3, members 24 consisting of magnetic substance are provided at corners where the degree of temperature rise is small and the magnetic influx density at the corners is increased by the members 24. The induced current then flows closer to these portions, and the degree of heating is also increased. A satisfactory joining strength can thus be secured at the both width ends without a fear that the metal pieces are melted down in the central region thereof in the plate width direction. In this invention, each of the members 24 consisting of magnetic substance must be provided at a position in a region which is extending from the width end of each metal piece and whose length is not more than ten times as long as the osmotic depth d 0 of the induced current. That is because the temperature rise is insufficient in the region and, if each member 24 consisting of magnetic substance is inwardly provided beyond this region, the degree of temperature rise of the metal piece becomes too large in such a region where the member 24 is provided, causing such a problem as melt down. A width dimension W of the member 24 is set to be two to ten times as long as the osmotic depth d 0 . That is because the effect obtained by placing the magnetic substance is reduced when the range in which the degree of heating and temperature rise can be increased is small, if the width dimension W is not more than two times as long as the osmotic depth d 0 . On the other hand, if it is more than 10 times as long as the osmotic depth d 0 , the temperature rising speed is extremely increased in the portion extending beyond the depth d 0 , thereby causing melt down. In order to perform heating in such a manner that the temperature rising speed similar to that in the central region of the metal pieces in the width direction thereof can be obtained and the temperature distribution is substantially uniform in the entire area in the width direction, the width W of each member 24 consisting of magnetic substance is restricted to a width which is two to ten times as long as the osmotic depth d 0 . Fig. 33 shows the relationship between the width dimension of the member 24 consisting of magnetic substance/the osmotic depth d 0 and a length of defective joining. As an example of a continuous hot rolling equipment to which the joining apparatus having the structure shown in Fig. 31 is incorporated, it is possible to adopt one shown in Fig. 20 by which the metal pieces are joined while matching with a timing for rewinding a coil type metal piece provided between the pinch rolls and a timing for effecting the rolling process. A dimension L m of the member 24 consisting of magnetic substance along the longitudinal direction of the metal pieces may preferably be 2d 0 + g + α (α is a clearance and set to be approximately 100 to 200 mm), in the case where a space between the metal pieces which is firstly formed when joining the metal pieces is represented as g. Further, when heating the metal pieces 1 and 2, in order to prevent the temperature rise of the member 24 consisting of magnetic substance itself, the member 24 may be obtained by superimposing a plurality of insulated thin plates one above the other. As the member 24, simple substance such as iron, nickel, cobalt or others, alloys thereof or non-crystallized substance can be used in addition to silicon steel. Fig. 34 shows an example in which the members 24 consisting of magnetic substance are adapted in the notches u in the joining apparatus provided with the dislocation preventing plates 8 each having the notches u. In the apparatus having such a structure, the metal pieces are uniformly heated over the entire region in the width direction. Also, it is extremely advantageous for completely preventing fluctuations in the vertical direction which are likely to be caused during pressing the metal pieces 1 and 2 against each other. In the case where there is provided such dislocation preventing plates 8 as shown in Fig. 34, if there is provided such a structure as shown in Fig. 35 that each member 24 consisting of magnetic substance can be temporarily removed from each notch u and shifted in parallel with the width direction of the metal pieces 1 and 2 to be again inserted in each notch u at a predetermined position, it is possible to easily cope with joining of metal pieces having different widths, thereby performing the effective continuous hot rolling. EMBODIMENT 1 Embodiment (1) Sheet bars (low carbon steel) each having a width of 1000 mm, a thickness of 30 mm and a temperature of 1000°C were joined by using an equipment (provided with dislocation preventing plates of SUS304 each having a thickness of 40 mm and 20 notches each having a width of 30 mm and a length of 900 mm (a width at a portion for suppressing deformation of the plate is 20 mm), and a finishing roller mill group having seven stands) such as shown in Fig. 20 under the succeeding conditions, and hot finishing rolling for obtaining a finished plate width of 3 mm was carried out. Further, the temperature distribution of the sheet bars in the width direction thereof at the time of completion of joining and the state of rupture of the plates during rolling were examined. Conditions: a. The distance between a preceding sheet bar and a succeeding sheet bar: 5 mm. b. The size of a core of an inductor: width = 1000 mm, dimension along the longitudinal direction of the sheet bars = 240 mm. c. The power supplied to the inductor: 1000 kw, and a frequency: 650 Hz. d. Ten constitutive members having a size of a = 200 mm, b = 20 mm and c = 20 mm (see Fig. 62) are disposed to a space between the inductor and the sheet bars at an interval of 50 mm along the plate width direction, and each reverse magnetic field generation circuit positioned at a central portion in the plate width direction (the circuit inwardly positioned from the width end by 250 mm) is closed to perform heating for 12 seconds and increase the temperature. e. The pressing force: 2 kg/mm 2 (pressed after heating and increasing the temperature). As a result, it was confirmed that the temperature distribution in the plate width direction was improved as shown in Fig. 37 and the stable hot rolling was enabled without causing rupture of the plates during rolling. Embodiment (2) Sheet bars (low carbon steel) each having a width of 1000 mm, a thickness of 30 mm and a temperature of 1000°C were joined by using an equipment (provided with dislocation preventing plates of SUS304 each having a thickness of 40 mm and 20 notches each having a width of 30 mm and a length of 900 mm (a width at a portion for suppressing deformation of the plate is 20 mm), and a finishing roller mill group having seven stands) such as shown in Fig. 20 under the succeeding conditions, and hot finishing rolling for obtaining a finished plate width of 1.2 mm was carried out. Further, the temperature up speed ratio in the width direction of the sheet bars at the time of heating and the state of rupture of the plates during rolling were examined. Conditions: a. The distance between a preceding sheet bar and a succeeding sheet bar: 5 mm. b. The size of a core of an inductor: width = 1000 mm, dimension along the longitudinal direction of the sheet bars = 240 mm. c. The power supplied to the inductor: 1000 kw, a current: 6120 A, a frequency: 650 Hz, and a magnetic flux density: 0.21T. d. Constitutive members each including magnetic substance (formed by superimposing 70 thin plates of silicon steel having an insulating film one on another) and having a size of a = 200 mm, b = 1 mm and c = 20 mm (see Fig. 62) are provided to notches of the dislocation preventing plate (see Fig 11) at a space between the inductor and the sheet bars, and all the reverse magnetic field generation circuits are opened for eight seconds from the start of heating, and a circuit positioned at a central portion in the plate width direction (the circuit inwardly placed at a position distanced from the width end by 250 mm) is closed to perform heating for 2 seconds. e. The pressing force: 50 tons (pressed after heating and increasing the temperature). Fig. 38 is a graph in which the temperature rising speed ratios are compared, and it was confirmed that the effective heating was enabled and no rupture of the plates occurs during rolling in the case where the members consisting of magnetic substance were provided as the constitutive members. EMBODIMENT 2 Embodiment (1) An apparatus such as shown in Fig. 21 was used on the entry side of the rolling equipment for hot rolling, and joining of metal pieces having the same width dimension was tried. Both the preceding metal piece and the succeeding metal piece are extremely-low carbon steel and have a thickness of 30 mm, a width of 800 mm and a length of 6000 mm. These preceding and succeeding metal pieces were opposed with a space of 5 mm being formed therebetween, and copper plates as conductive members were provided at the both width ends of the metal pieces in close proximity with each minute gap of 4 mm therebetween. Further, the alternating current was supplied to such an inductor as shown in the drawing, and the alternating magnetic field running through the magnetic pieces in the width direction thereof was generated to perform heating. A temperature of the metal pieces before heated is 1000°C; a thickness, a width and a length of each copper plate extending over the preceding metal piece and the succeeding metal piece are 30 mm, 200 mm and 600 mm, respectively; and a length and a width of each core of the inductor in cross section parallel with the metal pieces are 240 mm and 1000 mm, respectively. A distance between each magnetic pole and the metal pieces is 90 mm on the upper side and 90 mm on the lower side; a frequency of the alternating magnetic field is 1000 Hz; and an input power is 980 kW. After the induction heating was carried out for ten seconds under these conditions, the preceding and succeeding metal pieces were opposed to and pressed against each other using the clamps with the pressing force of 40 t applied to complete the joining. As a comparative example, the metal pieces were joined under the same conditions with those of the embodiment except that the copper plates were not provided to the sides of the both metal pieces. Fig. 39 shows a result of measuring the temperature rising speeds at the portions to be joined in the embodiment and the comparative example (the temperature was measured by embedding double bevel thermometer at a position inwardly distanced from the end of each metal piece by 1.5 mm in the longitudinal direction thereof). Fig. 39 illustrates the temperature rising speed ratio in the vicinity of the end of each metal piece in the width direction thereof assuming that a central portion of the metal piece in the width direction is 1. As obvious from the drawing, when the conductive member was provided to the side of each metal piece in close proximity according to the present invention, the temperature up speed at the end in the width direction approximated the temperature rising speed at the central portion. That is because the induced current generated directly below a core of the inductor flows to the end of the metal pieces in the width direction. Thus, the end of each metal piece in the width direction was heated and softened at a temperature such that the joined portion having a sufficient strength was able to be obtained without causing the melt down in the central region in the width direction. Thereafter, when the rolling was carried out, it was confirmed that no cracks were developed at the joined portion to bring about the rupture and the excellent rolling was enabled. Embodiment (2) As shown in Fig. 23, individual copper plates were provided to the both width ends of the preceding metal piece and the both width ends of the succeeding metal piece in close proximity. A thickness, a width and a length of each copper plate were 30 mm, 200 mm and 300 mm, respectively, and a gap between the respective metal pieces and the respective copper plates was all 4 mm. In regard of other conditions, the type and size of steel used as the preceding and succeeding metal pieces, the size of an inductor, an input power, a frequency and other were all the same with those in Embodiment (1). When the temperature rising speed in the vicinity of the portions of the metal pieces which will be joined was measured during heating and the temperature rising speed ratio of the both width ends with respect to that of the central portion in the width direction was calculated, the result equal to that of Embodiment (1) was obtained. No cracks was generated and developed by the rolling thereafter performed, and the plates were excellently joined. Embodiment (3) In this embodiment, an examination was carried out about a case where the current whose phase is the same with that of the induced current was supplied to the conductive members. By using such an inductor as shown in Fig. 25, the preceding and succeeding metal pieces both having a width of 800 mm were joined. At the time of heating, the inductor having a substantially-C-shaped core (a sectional dimension parallel with the metal pieces: a length = 1000 mm, a width = 240 mm) was used so that the copper plates which are the conductive members overlap on the magnetic poles of the inductor. The preceding metal piece and the succeeding metal piece were of SUS 304 steel type and had a temperature of 900°C before heating, and the copper plates were provided to the both width ends of the metal pieces in close proximity so as to connect the rear end of the preceding metal piece to the front end of the succeeding metal piece. Each of the copper plates had a thickness of 30 mm, a width of 200.mm and a length of 600 mm. Further, a frequency of the alternating magnetic field in a range of 500 Hz to 10 kHz was set to 500 Hz, 1kHz and 10 kHz, and an input power was 780 kW. Under these conditions, the induction heating was performed for ten seconds and the preceding metal piece and the succeeding metal piece were then pressed against each other with a pressing force of 40 t by using clamps to complete the joining. The temperature rising speed in the vicinity of the joining portion of the succeeding metal piece was measured during heating in each frequency, and the temperature rising speed ratio of the end portion in the width direction with respect to that of the central portion in the width direction was obtained as a mean value. As a result, the temperature rising speed at the end portion in the width direction further approximated to the temperature rising speed in the central portion as compared to Embodiment (1). Thus, the preceding metal piece and the succeeding metal piece was able to be joined in the entire region in the width direction thereof, and no cracks were developed from the joined portion to lead to rupture in the rolling thereafter performed. EMBODIMENT 3 Embodiment (1) In order to join the preceding metal piece and the succeeding metal piece both having a plate thickness of 30 mm and a plate width of 800 mm and being of low carbon steel type, heating (conditions for heating and increasing the temperature: a longitudinal dimension of a core = 240 mm, a width dimension of the core = 1000 mm, a gap between upper and lower magnetic poles = 210 mm, an input power = 200 Kw and alternating magnetic field frequency = 2000 Hz, a conductive member: material = graphite, a thickness = 30 mm, a width = 200 mm and a length = 250 mm, and four conductive members were pressed against the preceding and succeeding metal pieces at four width end portions) and pressing (pressing condition: pressing force of 60 ton) were carried out in the state shown in Fig. 28 to join the both metal pieces. The obtained metal piece was supplied to a hot rolling equipment to be subjected to finishing rolling, and rupture of the plate which might be caused by rolling was checked. As a result, it was confirmed that there was no rupture of the plate caused due to cracks at a joined portion. EMBODIMENT 4 Embodiment (1) After the sheet bars (low carbon steel) each having a plate width of 1000 mm and a thickness of 30 mm were joined by using an equipment provided with an apparatus having such a structure as shown in Fig. 34 under the succeeding conditions, hot finishing rolling for obtaining a plate having a finished plate thickness of 3 mm was carried out, and examinations were made into an existence/absence of rupture of the plate during rolling and a temperature distribution in the plate width direction immediately after joining of the sheet bars. Conditions for joining the sheet bars: a. A temperature of the sheet bars before finishing rolling is approximately 900 through 1000°C, and an electric resistivity in this temperature range is approximately 120 × 10 -8 Ωm. Therefore, when the alternating magnetic field was applied with a frequency of 500 Hz, the osmotic depth d 0 is approximately 25 mm. Each member consisting of magnetic substance (dimension: a width of 100 mm × a length of 150 mm × a height of 30 mm) was thus disposed at a position distanced from the width end of the plate by 10 to 110 mm. b. A space between a preceding sheet bar and a succeeding sheet bar: 10 mm. c. Size of an inductor (core): an inductor having a dimension along the width direction of the sheet bars of 1000 mm and a dimension along the longitudinal direction of the same of 240 mm was used. d. A power input to the inductor: 1500 kW, a frequency : 500 Hz. e. A heating time: 10 seconds. f. A pressing force: 3 kg/mm 2 . Fig. 66 shows the result of comparison between the temperature distributions in the width direction of the sheet bar before and after heating when the both sheet bars were joined in accordance with the present invention, and Fig. 41 shows the temperature distributions when the usual heating was performed (a comparative example: when members consisting of magnetic substance were not disposed). As apparent from Figs. 40 and 41, it was confirmed that the application of heat to the metal pieces extremely reduced portions in which the application of heat was insufficient which would lead to an existence of non-joined portions. Fig. 42 shows a comparison of calorific power ratios on the joined face of the sheet bar. 1) For heating and joining metal pieces, since an alternating magnetic field whose direction is opposed to that of an alternating magnetic field generated in the metal pieces is produced, corner portions of the metal pieces are sufficiently heated without a fear of melting down in a central region of the metal pieces in the plate width direction, and uniform heating over the entire region in the width direction of the metal pieces consequently enables a length of the incompletely-joined portion of the metal pieces which may lead to rupture of the plate during rolling to be extremely short, thereby performing stable continuous hot rolling. Specifically, each reverse magnetic field generation circuit for generating a reverse magnetic field operates by only opening and/or closing a switch provided thereto in the joining apparatus, thus prominently simplifying structure and control of the apparatus. 2) By lapping the inductor over each conductive member provided to each width end of the metal pieces, the magnetic flux directly runs through the inductive member to flow the induced current thereto, and a heating efficiency at the width ends of the metal pieces can be hence greatly improved. 3) Since the induced current can flow in the vicinity of corners of the metal pieces more than ever by positively flowing the current having the same phase with that of the induced current generated in the metal pieces from an external power supply to the conductive members, a heating efficiency can be improved at the width ends of the metal pieces.

Claims: A method for joining metal pieces wherein a rear end of a preceding metal piece (1) and a front end of a succeeding metal piece (2) are heated and the metal pieces (1,2) are pressed against each other for joining before hot finishing rolling, the rear end of the preceding metal piece (1) and the front end of the succeeding metal piece (2) are opposed to each other with a space therebetween, and an alternating magnetic field running through the metal pieces (1,2) in the thickness direction thereof is generated at end regions of the opposed faces of the respective metal pieces (1,2) to perform heating; characterized in that another alternating magnetic field reverse with respect to the former alternating magnetic field is partially generated in the end regions of the opposed faces of the metal pieces (1,2) and in either a region where the metal pieces exist or a region outside width ends of the metal pieces, thereby adjusting a temperature distribution in the end regions of the opposed faces of the metal pieces (1,2) in the width direction thereof. A method for joining metal pieces according to claim 1, wherein the other alternating magnetic field reverse with respect to the former alternating magnetic field is partially generated in either a region where the metal pieces (1,2) exist or a region outside width ends of the metal pieces (1,2) by arranging reverse magnetic field generation portions (5) of a plurality of reverse magnetic field generation circuits each having the reverse magnetic field generating portion (5) and a switch (6) connected to the reverse magnetic field generating portion (5) in the end regions of the opposed faces of the metal pieces (1,2) in the width direction thereof and controlling to open and/or close the switch (6) of each reverse magnetic field generation portion (5), thereby adjusting a temperature distribution in the end regions of the opposed faces of the metal pieces (1,2) in the width direction thereof. A method according to claim 1 or 2, wherein the region in which a reverse alternating magnetic field is generated is a central region of the metal pieces (1,2) in the width direction thereof. A method according to claim 1 or 2, wherein the region in which a reverse alternating magnetic field is generated is outside the width ends of the metal pieces (1,2). A method according to claim 1 or 2, wherein the region in which a reverse alternating magnetic field is generated is a central region of the metal pieces (1,2) in the width direction thereof or outside the width ends of the metal pieces (1,2). A method for joining metal pieces wherein a rear end of a preceding metal piece (1) and a front end of a succeeding metal piece (2) are heated and the metal pieces (1,2) are pressed against each other for joining before hot finishing rolling, the rear end of the preceding metal piece (1) and the front end of the succeeding metal piece (2) are opposed to each other with a space therebetween, and an alternating magnetic field running through the metal pieces (1,2) in the thickness direction is generated at end regions of the opposed faces of the respective metal pieces (1,2) to perform heating, characterized in that conductive members (18) are provided to both width ends of at least one of the rear end of the preceding metal piece (1) and the front end of the succeeding metal piece (2), thereby improving the heating efficiency of the metal piece in the width direction thereof by the conductive members (18). A method according to claim 6, wherein conductive members (18) are provided over both the preceding metal piece (1) and the succeeding metal piece (2). A method for joining metal pieces according to claim 6, wherein the both width ends of at least one of the rear end of the preceding metal piece (1) and the front end of the succeeding metal piece (2) are brought into contact with conductive members (18), thereby improving the heating efficiency of the metal piece in the width direction thereof by the conductive members (18). A method for joining metal pieces wherein a rear end of a preceding metal piece (1) and a front end of a succeeding metal piece (2) are heated and the metal pieces (1,2) are pressed against each other for joining before hot finishing rolling, the rear end of the preceding metal piece (1) and the front end of the succeeding metal piece (2) are opposed to each other with a space therebetween, and an alternating magnetic field running through the metal pieces (1,2) in the thickness direction thereof is generated in an end region on the opposed faces of the respective metal pieces (1,2) by an inductor (3) to perform heating, characterized in that members (24) each consisting of magnetic substance whose depth is two to 10 times as large as an osmotic depth do of which can be represented by the following expression is provided in a gap between the metal pieces (1,2) and the inductor (3) and in a region which is not more than 10 times as large as the osmotic depth d 0 and is inside the width ends of each metal piece (1,2), thereby enhancing the density of magnetic flux of the alternating magnetic field to improve the heating efficiency at the width ends of the metal piece by these members, do = {ρ x 10 7 / (µ x f)} 1/2 /2π, where d 0 : osmotic depth of the induced current (m) f: frequency of the alternating magnetic field (Hz) ρ: electric resistivity (Ω * m) µ: relative magnetic permeability An apparatus for joining metal pieces (1,2) comprising an inductor (3) having at least a pair of magnetic poles sandwiching the metal pieces in the thickness direction thereof with a gap therebetween, characterized in that reverse magnetic field generation portions (5) of reverse magnetic field generation circuits for generating an alternating magnetic field whose direction is reversed from that of an alternating magnetic field generated by the inductor (3) are provided between the magnetic poles of the inductor (3). An apparatus for joining metal pieces (1,2) according to claim 10 comprising: clamps (9) for vertically clamping a preceding metal piece (1) and a succeeding metal piece (2) between the magnetic poles of the inductor (3) for fixing and holding the metal pieces (1,2), wherein each of the clamps (9) protrudes from a region where the metal pieces (1,2) are fixed and held toward the ends of the metal pieces (1,2) and has a plurality of notch portions obtained by notching each clamp (9) in the form of a comb at an interval of space in the width direction of the metal pieces (1,2), and a reverse magnetic field generation portion (5) of a reverse magnetic field generation circuit for generating an alternating magnetic field whose direction is reversed from that of an alternating magnetic field generated by the inductor (3) is provided to each of the notch portions. An apparatus according to claim 10 or 11, wherein a plurality of reverse magnetic generation portions (5) are provided along the width direction of the inductor (3). An apparatus according to claim 10 or 11, wherein each of the reverse magnetic generation portions (5) is composed of a coil of one wind or of a plurality of winds or a U-shaped conductive member. An apparatus according to claim 10 or 11, wherein each of the reverse magnetic generation portions (5) includes a member consisting of magnetic substance. An apparatus according to claim 10 or 11, wherein the reverse magnetic field generation circuit includes a switch. An apparatus according to claim 10 or 11, wherein the reverse magnetic field generation circuit includes a variable resistor (7). An apparatus for joining metal pieces (1,2) according to claim 10, wherein the reverse magnetic field generation circuit comprises: the reverse magnetic field generation portion (5) for generating an alternating magnetic field whose direction is reversed from that of an alternating magnetic field generated by the inductor (3); a switch (6); a lead wire (5a) for connecting the switch (6) and the reverse magnetic field generation portion (5); and an open/close controller for opening and/or closing the switch (6). An apparatus for joining metal pieces (1,2) comprising an inductor (3) having at least a pair of magnetic poles sandwiching the metal pieces (1,2) in the thickness direction thereof with a gap therebetween, characterized by a member (24) consisting of magnetic substance which is provided between the magnetic poles and increases the density of magnetic flux of an alternating magnetic field generated by the inductor (3) at width ends of the metal pieces (1,2). An apparatus for joining metal pieces (1,2) comprising an inductor (3) having at least a pair of magnetic poles sandwiching the metal pieces (1,2) in the thickness direction thereof with a gap therebetween, characterized by a conductive member (18) which is provided between the magnetic poles and outside width ends of the metal pieces (1,2) in the width direction thereof with a gap therebetween or provided contacting with the width ends.

Inventors: AMAGASA TOSHIAKI, AMANUMA SHUJI, HAYASHI KANJI, HIRABAYASHI TAKESHI, ISOYAMA SHIGERU, KURODA AKIO, MITO YOSHIKI, MIYAMOTO KUNIO, MORIMOTO KAZUO, NIKAIDO HIDEYUKI, NITTA JUNZO, OSADA MASASHI, SAKAMOTO HIDEO, TAKASHIMA NORIO, TAKECHI TOSHISADA, TAMURA NOZOMU, TSURUSAKI KAZUYA, WAKAMOTO IKUO, YAMADA HIROSUKE, YAMASAKI TAKAHIRO, AMAGASA, TOSHIAKI, AMANUMA, SHUJI, HAYASHI, KANJI, HIRABAYASHI, TAKESHI, ISOYAMA, SHIGERU, KURODA, AKIO, MITO, YOSHIKI, MIYAMOTO, KUNIO, MORIMOTO, KAZUO, NIKAIDO, HIDEYUKI, NITTA, JUNZO, OSADA, MASASHI, SAKAMOTO, HIDEO, TAKASHIMA, NORIO, TAKECHI, TOSHISADA, TAMURA, NOZOMU, TSURUSAKI, KAZUYA, WAKAMOTO, IKUO, YAMADA, HIROSUKE, YAMASAKI, TAKAHIRO, AMAGASA, Toshiaki, Kawasaki Steel Corp., AMANUMA, Shuji, Kawasaki Steel Corp., Eguchi, Toshinobu, Mitsubishi Denki K. K., HASHIMOTO, Michio, Mitsubishi Denki K. K., HAYASHI, Kanji, Mitsubishi Jukogyo K. K., HIRABAYASHI, Takeshi, Kawasaki Steel Corp., ISOYAMA, Shigeru, Kawasaki Steel Corp., KURODA, Akio, Mitsubishi Jukogyo K. K., MAEDA, Fumihiro, Mitsubishi Denki K. K., MITO, Yoshiki, Mitsubishi Jukogyo K. K., MIYAMOTO, Kunio, Mitsubishi Jukogyo K. K., MORIMOTO, Kazuo, Mitsubishi Jukogyo K. K., NAKANO, Hiroyuki, Mitsubishi Denki K. K., NIKAIDO, Hideyuki, Kawasaki Steel Corp., NITTA, Junzo, Kawasaki Steel Corp., OSADA, Masashi, Kawasaki Steel Corp., SAKAMOTO, Hideo, Mitsubishi Denki K. K., TAKASHIMA, Norio, Kawasaki Steel Corp., TAKECHI, Toshisada, Kawasaki Steel Corp., TAMURA, Nozomu, Kawasaki Steel Corp., TSURUSAKI, Kazuya, Mitsubishi Jukogyo K. K., WAKAMOTO, Ikuo, Mitsubishi Jukogyo K. K., YAMADA, Hirosuke, Kawasaki Steel Corp., YAMASAKI, Takahiro, Kawasaki Steel Corp.
Applicants: KAWASAKI STEEL CO, MITSUBISHI ELECTRIC CORP, MITSUBISHI HEAVY IND LTD, KAWASAKI STEEL CORPORATION, MITSUBISHI DENKI KABUSHIKI KAISHA, MITSUBISHI JUKOGYO KABUSHIKI KAISHA
Application year: 1994
Main classification: B21B1
IPC codes: B21B1, B21B15, B23K13