COMPOSITION FOR A COVER MATERIAL OF A GOLF BALL

Abstract: There is provided a composition for a golf ball cover material, which has excellent softness and rebound resilience. A golf ball is provided which has excellent ball controllability, an excellent feeling, and excellent carrying distance when hit. A composition for a cover material of a golf ball which is suitable for the production of a golf ball having excellent softness, rebound resilience and controllability is provided.

Description: TITLE COMPOSITION FOR A COVER MATERIAL OF A GOLF BALL BACKGROUND OF THE INVENTION FIELD OF THE INVENTION This invention relates to a composition for a cover of a golf ball. More specifically, it relates to a composition for a cover material of a golf ball suitable for the production of golf balls which are easy to control, and have excellent softness and rebound resilience. PRIOR ART AND ITS PROBLEMS Golf balls having balata as a cover material have advantages that they have an excellent feel when struck by a golf club and are easy to control. They are especially preferred by the more skilled golfers, but have the defect that they have poor durability. The art teaches golf balls having improved cut resistance and having similar advantages to balata covered golf balls can be made by using a blend of a hard ionomer and a soft ionomer as a cover material (Research Disclosure 27103 (November 1987), Japanese Laid-Open patent Publication No. 308577/1989, and Japanese Laid Open Patent Publication No. 3931/1993). This art relates to blends of ionomers. What has been specifically considered have a somewhat higher hardness than balata. Cover materials having the same hardness as balata or having a hardness less than that ofbalata are desired. Also, higher rebound resilience with low hardness is desired. The present invention obtains a golf ball cover material having a high rebound resilience but a low hardness. The inventors have found that golf balls having a cover material made by compounding (A) and (B) components as defined below in a predetermined ratio has the desired properties. It is possible to design quality in a wide range in a balance of hardness and rebound resilience. SUMMARY OF INVENTION According to this invention, a composition which comprises 20 to 80 parts by weight of component (A) and 80 to 20 parts by weight of component (B) is used as a cover material of a golf ball. Component (A) comprises metal salts of an ethylene/ethylenically unsaturated monocarboxylic acid copolymer having an ethylenically unsaturated monocarboxylic acid content of 10 to 30% by weight and a degree of neutralization of at least 25 mole %. Component (B) comprises an ethylene/(meth) acrylate ester/ethylenically unsaturated monocarboxylic acid terpolymer having a (meth) acrylate ester content of 12 to 45% by weight and an ethylenically unsaturated monocarboxylic acid content of 0.5 to 5% by weight. In the present invention, by compounding a specified component (B), that is, an ethylene/(meth) acrylate ester/unsaturated monocarboxylic acid terpolymer having a (meth) acrylate ester content of 12 to 45% by weight and an unsaturated monocarboxylic acid content of 0.5 to 5% by weight, with a specified component (A), that is, an ionomer having a degree of neutralization of at least 25 mole% of an ethylene/unsaturated monocarboxylic acid copolymer having an unsaturated monocarboxylic acid content of 10 to 30% by weight, softness can be imparted to the cover of a golf ball without significant reductions in rebound resilience. By avoiding the use of an ionomer as component (B) as is provided in the art and by substituting the component (B) of the present invention, the golf ball obtained has excellent economy. Also, by doing so, the defects of decreased resilience and sacrifice of carrying distance experienced when the soft golf ball cover material is composed of two ionomer components are overcome without losing the advantageous controllability of a ball and a feeling when hit with a golf club. In the present invention, by selecting component (B), the ethylene/(meth(acrylate ester/unsaturated monocarboxylic acid terpolymer, and compounding it with component (A), the copolymer ionomer, we have succeeded in increasing softness without significantly decreasing rebound resilience. That is to say, a golf ball with the cover made using the composition of this invention has good controllability, good feel and excellent ball carrying distance when hit with a golf club. PREFERRED EMBODIMENTS OF THE INVENTION Component (A), the metal salts of the ethylene/unsaturated monocarboxylic acid copolymer, has an unsaturated monocarboxylic acid content of 10 to 30 % by weight, preferably 13 to 25% by weight, and is an ionomer which is neutralized with metal cations so that the degree of neutralization of the ethylene/unsaturated monocarboxylic acid copolymer is at least 25 mole %, preferably 30 to 80 mole %. The unsaturated monocarboxylic acids preferable include aliphatic monocarboxylic acids with 3 to 8 carbon atoms. Acrylic acid and methacrylic acid are especially preferred. Copolymers having an unsaturated monocarboxylic acid content smaller than the above-mentioned range are not preferred because the resulting compositions have lower rebound resilience. Furthermore, when copolymers having an unsaturated monocarboxylic acid content exceeding 30% by weight are used, moisture absorption becomes higher and it is not preferred. Component (A) can comprise blends of two or more copolymers. The degree of neutralization in this case may be adjusted so that the degree of neutralization of the blend as a whole becomes at least 25 mole %. Examples of metal cation species in the ionomer include monovalent metal cations such as lithium, sodium, and potassium, and divalent metals such as magnesium, calcium and zinc. The ionomers may be only one kind of metal salts, but preferably, the metal salts may be a mixture containing at least one kind of monovalent metal cation and at least one kind of the divalent metal cation. The ratio of the monovalent metal salts to the divalent metal salts may be in the range of 9:1 to 1:9, preferably 7:3 to 3:7 in weight. Degree of neutralization in the ionomer of less than 25 mole % is not preferred because the resulting composition would not have good rebound resilience and cutting resistance. The copolymer which is partially neutralized to form component (A) may be produced by copolymerizing ethylene with the unsaturated monocarboxylic acid at a high temperature under a high pressure using a radical initiator. This production method is already well known. Component (A) ionomer preferably has a melt flow rate of 0.1 to 30 g/10 minutes, especially 0.5 to 15 g/10 minutes, at 190°C under a load of 2160 g. Preferably, it has a Shore D hardness of 50 to 80, especially 55 to 75. Component (B), the ethylene/(meth)acrylate ester/unsaturated monocarboxylic acid terpolymer used in this invention, has a (meth) acrylate ester content of 12 to 45% by weight, preferably 15 to 40% by weight, and an unsaturated monocarboxylic acid content of 0.5 to 5% by weight, preferably 1 to 4.5% by weight. By (meth) acrylate ester, it is meant an acrylate ester and or a methacrylate ester. Specific examples include ester groups having alkyl groups of 4 to 12 carbon atoms such as methyl acrylate, ethyl acrylate, isobutyl acrylate, n-butyl acrylate, 2-ethyl hexyl acrylate, methyl methacrylate, and isobutyl methacrylate. Typical examples of the unsaturated monocarboxylic acid in component (B) terpolymer include those having about 3 to 10 carbon atoms, for example acrylic acid, methacrylic acid, and monoalkyl esters of dicarboxylic acids such as monomethyl maleate, monoethyl maleate, and monoisobutyl maleate. Among these, it is preferred to select monoalkyl esters of dicarboxylic acids. Component (B) terpolymers can be obtained by copolymerizing the respective monomers at a high temperature under high pressure using a radical initiator. This production method is widely known. If component (B) terpolymer has a (meth) acrylate ester content lower than the above-mentioned range, it is difficult to obtain a fully soft composition. Furthermore, when a component (B) terpolymer has a (meth) acrylate ester content higher than the above-mentioned range, the compositions becomes too soft, and unpreferably the cutting resistance becomes poor. If component (B) terpolymer has an unsaturated monocarboxylic acid content lower than the above-mentioned range, its compatibility with component (A) becomes poor, and unpreferably the cutting resistance becomes poorer. Furthermore, when component (B) terpolymer has an unsaturated monocarboxylic acid content higher than the above-mentioned range, unpreferably the rebound resilience becomes poor. Preferably, the component (B) terpolymer has a melt flow rate of 0.1 to 30g/10 minutes at 190°C under a load of 2160 g, especially 0.3 to 20 g/10 minutes, and a Shore D hardness of not more than 45, especially 10 to 35. Typical examples of preferred component (B) terpolymers include ethylene/acrylic acid/methyl acrylate terpolymer, ethylene/acrylic acid/isobutyl acrylate terpolymer, and ethylene/methacrylic acid/isobutyl acrylate terpolymer, and ethylene/methacrylic acid n-butyl acrylate terpolymer, ethylene/methyl acrylate/monomethyl maleate random terpolymer, ethylene/methyl acrylate/monomethyl/maleate random terpolymer, ethylene/methyl acrylate/monoethyl maleate random terpolymer, and ethylene/methyl methacrylate/monomethyl maleate random terpolymer. Component (B) may be a blend of two or more components. The ratio of the component (A) metal salts of an ethylene/unsaturated monocarboxylic acid copolymer to the component (B) terpolymer is 20 to 80 parts by weight, preferably 30 to 70 parts by weight, to 80 to 20 parts by weight, preferably 70 to 30 parts by weight. When the unsaturated monocarboxylic acid in the terpolymer is an unsubstituted monocarboxylic acid, preferably component (A) is 50 to 80 parts by weight, more preferably 55 to 70 parts by weight, and the amount of component (B) is 50 to 20 parts by weight, especially 45 to 30 parts by weight. By compounding component (A) with component (B) in such proportions, a composition having excellent softness and rebound resilience can be obtained. Other polymers may be compounded in the composition of this invention within small ranges which do not impair the objects of the present invention. Various additives usually compounded into golf ball cover material may be added. Examples of such additives are various coloring agents, inorganic fillers, antioxidants, and weather resistance stabilizers. Typical additives may include pigments such as titanium oxide, zinc oxide, barium sulfate and zinc sulfate, various dyes, and colors. The composition of this invention (containing no additives) preferably has a Shore D hardness of 30 to 60, especially 32 to 58, a strffiiess of 40 to 200 MPa, especially 45 to 190 MPa, and a rebound resilience of at least 52, especially at least 54. The resin composition of this invention may be used as a cover material of a three-piece golf ball and a two-piece golf ball. The three-piece golf ball consists of a center, a rubber thread wound up on the center and a cover on it. The cover material of this invention may be molded onto the thread-wound center of a three-piece ball employing techniques known in the art, particularly compression molding half shells over the thread-wound center. Various dimple patterns can be molded into the cover. The two piece golf ball consists of a core and a cover thereon. The cover material of this invention may be molded onto the core of a two-piece ball employing techniques known in the art, particularly injection molding the cover material onto the core supported on retractable pins in a cavity of an injection mold to form a two-piece golf ball. Various dimple patterns can be molded into the cover. EXAMPLES The present invention will be illustrated by the following examples. The compositions used in the examples are as shown in Table 1. TABLE I Melt Flow Hardness Rebound MFR Shore D Resilience Composition (g/10 min.) (23° C) Ethylene 30 mole % sodium neutralized Ionomer A ethylene/methacrylic acid 2.8 61 63 (85/15 wt.%) copolymer Ethylene 60 mole % zinc neutralized Ionomer B ethylene/methacrylic acid 0.7 60 57 (80/20 wt.%) copolymer Ethylene 60 mole % sodium neutralized Ionomer C ethylene/methacrylic acid 1.0 67 68 (80/20 wt.%) copolymer Ethylene 52 mole % lithium neutralized Ionomer D ethylene/methacrylic acid 1.0 63 67 (85/15 wt.%) copolymer Ethylene 54 mole % magnesium neutralized copolymer E ethylene/methacrylic acid 0.7 62 64 (85/15 wt.%) copolymer Ethylene Ethylene/methyl acrylate/monoethyl terpolymer A maleate (74.7/2/2.3 wt %) terpolymer 3.6 19 60 Ethylene Ethylene/methacrylic acid/isobutyl terpolymer B acrylate (74/2/24 wt. %) terpolymer 5.0 25 53 Ethylene ethylene/methacrylic acid/isobutyl terpolymer C acrylate (76/4/20 wt %) terpolymer 12.0 30 45 Ethylene Ethylene/methacrylic acid/isobutyl terpolymer D acrylate (72/8/20 wt %) terpolymer 25.0 25 43 Ethylene Ethylene/methacrylic acid/isobutyl terpolymer E acrylate (85/5/10 wt %) terpolymer 10.0 40 36 Test Methods The methods of testing the resin compositions and the starting materials were as follows: 1. Melt Flow Rate (MFR) Using a tester made by Toyo Seiki Seisakusho, MFR was measured at a temperature of 190°C under a load of 2160 g. 2. Hardness It was measured by using a Shore D hardness tester (made by Zwick Gmbh & Co.) at 23°C (ASTM D2240). 3. Stiffiiess Using a Tinious Olsen-type stiffness measuring machine made by Toyo Seiki Seisakusho, it was measured at 23°C (ASTM D747). 4. Rebound Resilience Using a rebound resilience tester (pendulum-type) made by Ueshima Seisakusho Co., Ltd. it was measured at 23°C. Reference Example 1 The ethylene ionomers A and B (50 to 50 parts by weight) were melt- blended at a resin temperature of 200°C with an extruding amount of 4.0 kg/hr in the compounding ratios shown in Table 2 by using a 30 mm-diameter biaxial extruder (made by Ikegai Tekko Co., Ltd.). The properties ofthe obtained resin compositions were evaluated. The results are shown in Table 2. The results show that rebound resilience was high, but the composition had high hardness and poor softness. Examples 1 to 9 and Comparative Examples 1 to 5 Reference Example 1 was repeated, except that the starting materials shown in Table 1 were compounded in the proportions shown in Tables 2 and 3. The results are shown in Tables 2 and 3. Comparative Examples 1 and 2 showed high rebound resilience, but too low stiffness. Hence, when they were used as a golf ball cover, they are liable to be scratched, and therefore are unsuitable. Comparative Example 3 had too low in hardness and stiffness, and low rebound resilience. Comparative Examples 4 and 5 had suitable hardness, but since they had too low in rebound resilience, they are unsuitable as a golf ball. In contrast, the compositions obtained in the Examples had suitable hardness, and high rebound resilience. Effect of the Invention According to this invention, there can be provided a composition for a golf ball cover material, which has excellent softness and rebound resilience. When such a composition is used as a cover material of a two-piece ball or a three-piece ball, there an be provided a golf all having excellent ball controllability, an excellent feeling, and excellent carrying distance when hit. TABLE 2 Experiment No. R Reeff.. EEx l1 E Exx ll E Exx 22 E Exx 33 E Exx 44 E Exx 55 E Exx 66 E Exx 77 E Exx 8l Ex 9 Compounded compositon Ethylene copolymer ionomer A 5 500 2 255 1 155 3 355 3 300 2 255 3 355 2 255 25 Ethylene copolymer ionomer B 50 25 15 35 30 25 35 25 Ethylene copolymer ionomer C 25 Ethylene copolymer ionomer D 30 Ethylene copolymer ionomer E 30 Ethylene terpolymer A 50 70 30 Ethylene terpolymer B 40 50 30 40 Ethylene terpolymer C 50 50 Properties MFR(g/10 minutes) 1.7 1.7 1.7 1.5 2.7 3.2 2.4 2.7 5.3 1.8 Hardness (Shore D) 63 41 33 55 52 44 54 50 47 50 00 Stiffness (MPa) 340 78 34 174 155 107 188 152 100 124 Rebound Resilience (%) 66 60 60 65 60 55 64 59 54 57 TABLE 3 Comp Comp Comp Comp Comp Experiment No. Exam 1 Exam 2 Exam 3 Exam 4 Exam 5 Compounded Composition 25 25 Ethylene terpolymer ionomer A 25 25 Ethylene terpolymer ionomer B Ethylene terpolymer A 100 Ethylene terpolymer B 100 Ethylene terpolymer D 100 50 Ethylene terpolymer E 50 Properties MFR (g/10 minutes) 1.0 3.6 25.0 10.0 4.3 Hardness (Shore D) 41 19 25 46 53 Stiffness (MPa) 34 9 16 87 157 Rebound resilience (%) 56 60 43 48 49

Claims: WHAT IS CLAIMED IS: 1. A composition for a golf ball cover material which comprises (A) 20 to 80 parts by weight of metal salts of an ethylene/ethylenically unsaturated monocarboxylic acid copolymer having an ethylenically unsaturated monocarboxylic acid content of 10 to 30 percent by weight and a degree of neutralization of at least 25 mole percent and (B) 80 to 20 parts by weight of an ethylene/(meth)acrylate ester/ethylenically unsaturated monocarboxylic acid terpolymer having a (meth)acrylate ester content of 12 to 45 percent by weight and an ethylenically unsaturated monocarboxylic acid content of 0.5 to 5% by weight. 2. The composition according to Claim 1 wherein the ethylenically unsaturated monocarboxylic acid in the terpolymer (B) is selected form the group consisting of acrylic acid, methacrylic acid and monoalkyl esters of maleic acid. 3. The composition according to Claim 1 wherein the metal salts ofthe ethylene/ethylenically unsaturated monocarboxylic acid copolymer (A) is a mixture of monovalent metal salts and divalent metal salts. 4. The composition according to Claim 3 wherein the ratio ofthe monovalent etal salts is in the range of 7:3 to 3:7 in weight. 5. The composition according to Claim 1, wherein the metal salts ofthe ethylene/ethylenically unsaturated monocarboxylic acid copolymer has a melt flow rate of 0.5 to 15 g/10 minutes at 190°C under a load of 2160 g and a Shore D hardness of 55 to 75. 6. The composition according to Claim 1 wherein the terpolymer (B) has a melt flow rate of 0.3 to 20g/10 minutes at 190°C under a load of 2160 g and a Shore D hardness of 10 to 35. 7. A golf ball having a core and a cover wherein the cover material comprises (A) 20 to 80 parts by weight of metal salts of an ethylene/ethylenically unsaturated monocarboxylic acid copolymer having an ethylenically unsaturated monocarboxylic acid content of 10 to 30 percent by weight and a degree of neutralization of at least 25 mole percent and (B) 80 to 20 parts by weight of an ethylene/(meth)acrylate ester/ethylenically unsaturated monocarboxylic acid terpolymer having a (meth)acrylate ester content of 12 to 45 percent by weight and an ethylenically unsaturated monocarboxylic acid content of 0.5 to 5% by weight. 8. The golf ball of Claim 7 wherein the ethylenically unsaturated monocarboxylic acid in the terpolymer (B) is selected form the group consisting of acrylic acid, methacrylic acid and monoalkyl esters of maleic acid. 9. The golf ball of Claim 7 wherein the metal salts of the ethylene/ethylenically unsaturated monocarboxylic acid copolymer (A) are a mixture of monovalent metal salts and divalent metal salts. 10. The golf ball of Claim 9 wherein the ratio ofthe monovalent metal salts is in the range of 7:3 to 3:7 in weight. 11. The golf ball of Claim 7 wherein the metal salts of the ethylene/ethylenically unsaturated monocarboxylic acid copolymer have a melt flow rate of 0.5 to 15 g/10 minutes at 190°C under a load of 2160 g and a Shore D hardness of 55 to 75. 12. The golf ball of Claim 7 wherein the terpolymer (B) has a melt flow rate of 0.3 to 20g/10 minutes at 190°C under a load of 2160 g and a Shore D hardness of 10 to 35.

Inventors: FUJITA SUMIO, HIRASAWA EISAKU, IWASE YOSHIYUKI, FUJITA, SUMIO, HIRASAWA, EISAKU, IWASE, YOSHIYUKI
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1994
Main classification: C08L23
IPC codes: A63B37, C08L23