Process for the production of synthetic rutile

Abstract: The iron oxide content of ilmenite or other titanium ore is reduction to metallic iron by reaction with coal in a rotary kiln 1. The resulting iron metal content of the thus treated ore is oxidised in aqueous solution in an aerator 3 through which an oxidising gas containing oxygen and/or ozone is passed. Resulting particles of iron oxide are separated from the ilmenite solution in cyclone 5 and then by leaching the solution in vessel 7 with acid, the resulting product being filtered in vessel 8.

Description: This invention relates to the production of synthetic rutile by hydrometallurgical processes and, in particular, to the production of synthetic rutile by the Becher process. Titanium dioxide is, in its pure form, a valuable white pigment used in paints. Traditionally, the pigment has been obtained using the "chloride" or "sulphate" processing routes. The "sulphate" processing route, which has fallen into disfavour in recent times due to the environmental problems caused by the disposal of acidic ferrous sulphate liquors, involves the pug-roasting of ilmenite with concentrated sulphuric acid to form a solid sulphate cake which is then dissolved in hot dilute sulphuric acid to liberate iron. Ferric ion is removed from the solution by reduction with scrap iron and the ferrous ions are partially removed from the solution by crystallisation of hydrated ferrous sulphate (copperas). Hydrous titanium dioxide is calcined and further processed to produce the pigment. In order to overcome the environmental problems inherent in the "sulphate" route, the "chloride" route has become commonplace. The "chloride" process involves the chlorination of natural or synthetic rutile at high temperatures to form a mixture of titanium tetrachloride and ferric chloride vapours which are separated from each other by selective condensation and, if necessary, further refining steps. The titanium tetrachloride is then oxidised to produce pigment grade titanium dioxide or reduced to produce titanium metal in accordance with the Kroll process. It is clear that in both the above processing routes the removal of iron is a problem, which at the very least involves further capital costs to address. For example, ferric chloride may be oxidised in a costly further processing stage to iron oxides and the chlorine recovered for further use in a chloride process. Moreover, as the world reserves of natural rutile, containing approximately 95% by weight titanium dioxide fall, the iron removal problem becomes more acute. Therefore, alternative processes have been devised for the environmentally acceptable production of synthetic rutile from the abundant available reserves of ilmenite, a mixed iron and titanium oxide ore, represented approximately by the formula FeTiO 3 . Ilmenite contains about 53% by weight titanium dioxide. The majority of such processes include hydrometallurgical steps but generally commence with partial or complete reduction of the iron oxides present within the ilmenite to metallic iron by pyrometallurgical processing followed by selective leaching of the iron with hydrochloric or sulphuric acids, ferric chloride or aerated water. The process where aerated water is used is called the Becher Process, and is essentially an accelerated "rusting" process wherein, commonly, a salt such as ammonium chloride is also added as a corrosion promoter. The process commences with a carbothermic reduction step in a rotary kiln at 1150°C to which coal or a suitable carbonaceous agent is added, both as a reductant and as a fuel. The reduced ilmenite from the kiln is then cooled and further treated with an aerated aqueous solution, ideally containing 1% by weight ammonium chloride, in a stirred batch reactor in order to rust out the iron over a period of 12 to 16 hours. The ammonium chloride is believed to give benefits in terms of an accelerated iron corrosion rate for two major reasons. Firstly, the chloride ions can break down passive oxide films which may have formed on the metallic iron during the reduction stage while, secondly, the ammonium ion acts as a buffer against very high pH values near the surface of the reacting iron. This assists in the removal of hydroxyl ions by the reaction: NH 4(aq) + OH → NH 3 + H 2 O If the hydroxyl ions were not removed by this reaction they would react with ferrous ions produced by the half reaction: Fe → Fe 2+ + 2e- to produce a precipitate of hydrated ferrous oxide in the pores of the ilmenite, thus slowing and possibly completely stopping the rusting reaction by reducing or eliminating the supply of oxygen to the metallic iron within the ilmenite grains. This is a limitation of the conventional process. Upon completion of the reaction, the iron oxides produced are removed from the reaction mixture by washing in hydrocyclones. The synthetic rutile is then subjected to a final hydrochloric acid leaching step to remove residual iron and produce a product grading 92 weight % titanium dioxide which is suitable as a feedstock to pigment or metal production processes. A clear disadvantage of the above process, however, is that it is rate-limited by the diffusion rate of oxygen to the metallic iron which comes about due to the low solubility of oxygen in aqueous solutions. With this object in view the present invention provides a process for the production of a synthetic rutile comprising the step of reducing a titanium ore containing iron oxides with a reducing agent to provide a reduced titanium ore containing metallic iron, the reduced titanium ore being contacted in a contacting step with an aqueous solution through which a gas containing ozone is passed during the said contacting step to oxidise said metallic iron. Most preferably ozone or ozonated oxygen, i.e. ozone in admixture with oxygen, is to be employed. Furthermore, the present invention provides the use of ozone according to claim 7 and a refining process according to claim 8. The dependent claims define preferred embodiments of the claimed process. Preferably, the aqueous solution contains between 0.1 and 5% ammonium chloride, most preferably 1% ammonium chloride. Conveniently the gaseous mixture contains up to 1%, preferably 0.001 to 1%, more preferably 0.005 to 0.015% and most preferably 0.01% volume basis ozone, though lower concentrations in oxygen may also be effective. The ozone may be produced on site at the synthetic rutile plant by any method production known to those skilled in the art. Conveniently, the pulp density of reduced ilmenite in the aqueous solution ranges between 10 and 60% solids by weight, preferably 40 to 60% solids by weight and the temperature at which the oxidation takes place ranges between 20 and 70° Celsius, most preferably 50% Celsius. The gas containing ozone may also contain other gases such as oxygen or other oxidising gases. The oxidising gas is introduced to the aqueous solution by any means suitable for introduction of gases to liquids and may be a simple sparging means or a more sophisticated type designed to form micron-sized swarms of gas bubbles thus enhancing gas solubility. The invention will be more clearly understood from the following description of a preferred embodiment thereof made with reference to the accompanying figures in which: Figure 1 is a process flowsheet showing one possible route to the production of synthetic rutile and incorporating ozone injection according to the process of the present invention. Figure 2 is a graph showing the effect of air, oxygen and ozone addition on iron removal kinetics from reduced ilmenite at 50°C. Figure 3 is a graph showing the dissolved oxygen levels as a function of time during iron rusting from reduced ilmenite for air, oxygen and ozonated oxygen. Referring now to Figure 1, ilmenite grading 54 weight % titanium dioxide is fed to a rotary kiln 1 heated to 1150°C and held there together with pulverised coal (or other source of carbon) for sufficient time to reduce iron oxides to metallic iron. The product metallised or reduced ilmenite-coal ash mixture is then separated into reduced ilmenite and ash by a magnetic separation step in magnetic separator 2. The reduced ilmenite is then fed to a batch stirred oxidation reactor 3 held at 50°C and a pulp density of 30 weight % reduced ilmenite and contacted with an aqueous ammonium chloride solution containing 1% by weight ammonium chloride. Ozone, possibly in admixture with air or, ideally, oxygen to increase the oxygen partial pressure, is sparged through the solution causing oxidation of the iron. Fine particles of insoluble iron oxides and ammonium chloride solution are removed as overhead 4 from the cyclone and the treated ilmenite is removed as underflow 5. The overhead 4 is clarified in a thickener from which ammonium chloride solution is recovered as overflow and recycled to the oxidation reactor 3. The iron oxide is removed from the thickener as underflow 6 and disposed of or sold, possibly as a feedstock to an iron or steelmaking process. Ozone is produced on-site using an ozonator or similar equipment understood by those skilled in the art of ozone production. The exact nature of the ozone production method is not critical to the success of the invention but, by way of example, may be mentioned the method in which an electrical discharge is passed through air or oxygen, the latter being more preferred for present purposes. The methods of production are not free of hazards and so the normal precautions should be taken. In the final step of the process the treated ilmenite is leached with hydrochloric acid in vessel 7 to remove residual iron and manganese and filtered in vessel 8 to separate the synthetic rutile grading 92% by weight or higher titanium dioxide. The synthetic rutile product is suitable for use in a titanium dioxide pigment production plant. The above description is generally illustrative of the process of the present invention and performance results of such a process as performed on the laboratory scale are reproduced herebelow as Table 1 and Figure 2. The conditions under which the tests were performed are as follows. A cylindrical vessel, having 18 litres capacity, was filled with 17.41 kg of water to which 8.77 kg of reduced ilmenite produced in accordance with the process as described above was added under agitation. It is to be appreciated, in this regard, the reduced ilmenite is a fine grained heavy mineral and the absence of a high degree of agitation may prove quite detrimental to the efficiency of the process. 176 grams of analytical grade ammonium chloride, sufficient to form a 1% aqueous solution, was then added to promote the iron liberation process. A turbine agitator of the Rushton type is suitable for the purpose of attaining the required levels of agitation and an impeller speed of 100 rpm was selected for the purposes of the tests. After two hours agitation, the impeller speed was reduced to 600rpm. Various gases and gas mixtures were then tested in accordance with the process of the invention. The gases and gas mixtures analysed as follows: A. Air at 14.7 litres per minute (3.09 litres per minute equivalent oxygen) B. Oxygen at 2.8 litres per minute. C. Oxygen/Ozone containing 0.01 volume percent ozone in 2.8 litres per minute flow of oxygen and were introduced by a sparger located 100 mm directly below the agitator. The sparger is ideally selected to enhance gas solubility and suitable sparing means are widely available to those skilled in the art. Iron liberation results in accordance with the process and as a function of time are reproduced in Table 1 below: Iron Liberation (% by wt Fe) as a function of Time Test A B C Time (hours) 0 0 0 0 1 9 18 42 2 18 30 60 3 22 37 82 4 27 46 96 5 38 53 - 6 48 58 - 7 58 64 - Figure 2 shows a possible mechanism for the improved performance of a process involving ozone. Without in any way wishing to limit the generality of the invention it appears that the solubility of oxidant is important. It is apparent that the solubility of ozonated oxygen in the aqueous ammonium chloride solution at 50°C as monitored by an Orion dissolved oxygen meter, approaches a limit of 8 mg.L -1 whereas the solubility of oxygen alone only reaches a limit of 4 mg.L -1 over the same duration of 4 hours. The solubility of air is substantially lower than this. Thus oxidant utilisation with ozonated oxygen is therefore essentially more efficient. Since the rusting reaction is diffusion controlled, higher temperatures would be expected to yield greater benefits in terms of reaction rate provided that such benefits were not offset by the reduction in ozonated oxygen or ozone solubility.

Claims: A process for the production of a synthetic rutile comprising the step of reducing a titanium ore containing iron oxides with a reducing agent to provide a reduced titanium ore containing metallic iron, said reduced titanium ore being contacted in a contacting step with an aqueous solution through which an oxidising gas is passed during said contacting step to oxidise at least part of said metallic iron, characterised in that the oxidising gas contains ozone. A process as claimed in claim 1, wherein the oxidising gas contains up to 1 percent by volume of ozone. A process as claimed in claim 2, wherein the oxidising gas contains 0.01 percent by volume of ozone. A process as claimed in any one of the preceding claims, wherein the oxidising gas comprises ozonated oxygen. A process as claimed in any one of the preceding claims, wherein said gas is sparged by sparing means through said aqueous solution. A process as claimed in claim 5, wherein an agitator is used to form a slurry of said aqueous solution and reduced titanium ore and said sparing means is located directly below said agitator. Use of ozone as the oxidising gas in a process as claimed in any one of the claims 1 to 6. A process for refining synthetic rutile comprising the step of treating synthetic rutile obtained from a process as claimed in any one of claims 1 to 6.

Inventors: HOECKER WALTER, HOECKER, WALTER
Applicants: BOC GASES AU LTD, BOC GASES AUSTRALIA LIMITED
Application year: 1994
Main classification: C22B34
IPC codes: C21B13, C22B34