COATING COMPOSITIONS FOR ARTICLES OF GRAPHITE-ALUMINA REFRACTORY MATERIAL

Abstract: Coating compositions for coating articles of graphite-alumina refractory material to protect the articles against thermal shock comprise one or more minerals having a sheet structure such as talc, mica, vermiculite, antigorite, kaolinite, montmorillonite or pyrophyllite, a refractory oxide binder such as alumina gel, silica sol, alumina sol or zirconia sol and a carrier liquid such as water.

Description: COATING COMPOSITIONS FOR ARTICLES OF GRAPHITE-ALUMINA REFRACTORY MATERIAL This invention relates to coating compositions for articles such as nozzles or shrouds made from graphite-alumina refractory material and which are used in the casting of metals, especially steel. Articles such as pouring nozzles for molten metal- containing vessels, e.g. ladles and tundishes, and shrouds which surround the metal stream flowing from one vessel to another, e.g. a ladle to a tundish, are commonly made in a graphite-alumina refractory material having a carbon bond produced by the decomposition of a phenolic resin binder. Such a material has poor thermal shock resistance and tends to crack so it is necessary to treat nozzles and shrouds in some way so as to minimise the thermal shock produced when they are heated rapidly to elevated temperatures. One method of treatment which is commonly used is to subject the article to a decarburisation treatment prior to use. The article is heated in an oxidising atmosphere so as to oxidise or burn out carbon at the surface of the article and leave a surface layer of porous, essentially unbonded alumina. In the case of nozzles another practice is to apply a ceramic fibre-containing insulating paper around the outside of the nozzle. However, this practice is expensive and time-consuming as it is necessary to cut the paper sheet and wrap and wire it in order to fit it properly around the nozzle. It has also been proposed to coat nozzles with an insulating coating and Canadian Patent No. 1301780 describes the use of a coating composition comprising about 30% to about 85% by weight of a finely divided constituent selected from one or more of fused silica grains, alumina powder, zirconia powder, mullite powder and alumina bubbles; 0 to about 10% by weight of ceramic fibre selected from aluminosilicate fibre, zirconia fibre, titania fibre, alumina-chrome fibre, alumina bubbles and zirconia bubbles; about 15% to about 30% by weight water; 0 to about 7% by weight of a binder constituent selected from Glass H, sodium silicate and acrylic resins; and 0 to about 40% by weight of a glass forming frit material. It has now been found that a coating containing one or more minerals having a sheet structure and bonded with a refractory oxide is particularly satisfactory for protecting articles such as nozzles and shrouds against thermal shock. According to the invention there is provided a coating composition for coating articles of graphite-alumina refractory material, comprising one or more minerals having a sheet structure, a refractory oxide binder and a carrier liquid. According to a further feature of the invention, there is provided an article of graphite-alumina refractory material having a coating thereon comprising one or more minerals having a sheet structure and a refractory oxide bond. Suitable minerals having a sheet structure include talc, micas, vermiculite, antigorite (lamellar serpentine) and clays such as kaolinite, montmorillonite and pyrophylute. Graphite may also be used but only in combination with one or more other minerals. Suitable refractory oxide binders include alumina gel (which may be formed from alpha alumina monohydrate and a gelling agent such as aluminium chloride or aluminium nitrate) and colloidal oxide sols such as silica sol, alumina sol and zirconia sol. A combination of alumina gel and a cationic silica sol is preferred. For convenience and reasons of cost, the carrier liquid is preferably water but if desired, an organic carrier such as an alcohol could also be used. The coating composition will usually contain 5 - 50% by weight of mineral having a sheet structure, 20 - 60% by weight of refractory oxide binder and 20 - 50% by weight carrier liquid. The coating composition may be applied to the refractory article by any one of a variety of methods, for example, by spraying, by brushing, by dipping the article into the composition or by overpouring. The amount of carrier liquid present will be dependent partly on the chosen method of application and partly on the particular mineral or minerals used and on the particular refractory oxide binder. After application, the coating composition is dried to remove the carrier liquid, for example, in an oven. The coating composition may also contain other constituents such as wetting agents, anti-foaming agents or thickening agents to improve the Theological and application characteristics of the composition. The coating composition may also contain a minor proportion of a fibrous material such as aluminosilicate fibre in order to improve the strength of the coating after application and drying so as to allow coated nozzles or shrouds etc. to be transported before use without the coating becoming damaged. The coating composition may also contain a minor proportion of a particulate refractory filler other than a mineral having a sheet structure or a refractory oxide binder. However, refractory fillers such as zirconia, zircon or alumina will tend to reduce the porosity and heat-insulating property of the coating. When applied to graphite-alumina refractory articles the coating compositions of the invention produce porous, heat-insulating coatings which protect the articles from thermal shock when they are heated rapidly to elevated temperatures and which in use in contact with a molten metal such as steel, are sacrificial in that they are washed away by the molten metal once they have served their purpose. The following examples will serve to illustrate the invention :- EXAMPLE 1 (1) % by weight Talc 13.3 Mica 17.7 Expanded vermiculite 8.9 Alumina monohydrate 4.4 Aluminium chloride 1.3 Cationic colloidal silica 2.7 Aluminosilicate fibre 2.7 Wetting agent 0.2 Water 48.8 (2) % bv weight Molochite 50.0 Bubble alumina 21.0 Attapulgite clay 4.0 Polyacrylate binder 4.0 Antifoam 0.25 Wetting agent (sodium phosphate) 0.25 Water 20.5 (3) % by weight Graphite 65.0 Alumina monohydrate 9.0 Aluminium chloride 1.0 Water 25.0 (4) Proprietary glaze (available from Bayer) normally used as an antioxidation coating on graphite-containing articles and consisting of silicon and silicon carbide in a sodium borate glass. (1) is a coating composition according to the invention. (2), (3) and (4) are not according to the invention and were tested for the purpose of comparison. Solid cylindrical rods 5 cm in diameter and 20 cm long were produced by isostatic pressing from a mixture of 70% by weight alumina and 30% by weight graphite and a phenolic resin binder. After pressing, the rods were heated at 950°C for 30 minutes to cure and carbonise the resin to produce a carbon-carbon bond. A central hole was drilled in one end of each of the rods to a standard depth, the outside of the rods was coated with the coating compositions to a thickness of 3 - 4 mm and the coated rods were heated at 110°C for 2 hours to dry the coatings. A thermocouple was inserted in the hole, the coated rod was immersed in molten steel at 1600°C and the temperature was recorded at 10 second intervals over a period of 3 minutes, and the rate of heating was calculated. The results obtained are shown in the table below. COATING COMPOSITION RATE OF HEATING °C/SECOND (1) 6.68 (2) 8.57 (3) 9.38 (4) 8.93 The results show that coating composition (1) significantly reduced the thermal conductivity of the alumina/ graphite rod material and, hence, improved its thermal shock resistance compared with the other three compositions. The rate of heating of the rod coated with the graphite-based coating composition (3) differed very little from that of an uncoated rod of the same material. EXAMPLE 2 In a further test a test rod of the type used in Example 1 and coated with coating composition (1) was compared with an uncoated rod by heating the rods to a temperature of 1200°C over a period of 1 minute and measuring the temperature at intervals of 1 minute as the rods cooled to 600°C. The uncoated rod cooled to 600°C in only 8 minutes whereas the coated rod took 12 minutes to reach the same temperature, thus demonstrating the heat-insulating characteristics of the coating. EXAMPLE 3 The following are examples of two further coating compositions according to the invention for coating the external surface of tundish to mould nozzles for continuous casting equipmen - (5) % by weight Pyrophillite 37.2 Alumina monohydrate 4.6 Aluminium nitrate 1.1 Cationic colloidal silica 3.8 Expanded vermiculite 7.0 Wetting agent 0.3 Water 46.0 (6) % by weight Pyrophillite 49.5 Alumina monohydrate 5.0 Aluminium nitrate 1.2 Cationic colloidal silica 4.0 Wetting agent 0.3 Water 40.0

Claims: CLAIMS 1. A coating of composition for coating articles of graphite- alumina refractory material characterised in that the composition comprises one or more minerals having a sheet structure, a refractory oxide binder and a carrier liquid. 2. A coating composition according to Claim 1, characterised in that the mineral is talc, a mica, vermiculite, antigorite, kaolinite, montmorillonite or pyrophyllite. 3. A coating composition according to Claim 1 or Claim 2, characterised in that graphite constitutes a proportion of the mineral content of the composition. 4. A coating composition according to any one of Claims 1 to 3, characterised in that the refractory oxide binder is alumina gel, silica sol, alumina sol or zirconia sol. 5. A coating composition according to Claim 4, characterised in that the refractory oxide binder is a combination of alumina gel and cationic silica sol. 6. A coating composition according to any one of Claims 1 to 5, characterised in that the composition comprises 5 - 50% by weight of mineral having a sheet structure, 20 - 60% by weight of refractory oxide binder and 20 - 50% by weight of carrier liquid. 7. A coating composition according to any one of Claims 1 to 6, characterised in that the composition also contains a minor proportion of a fibrous material. 8. A coating composition according to any one of Claims 1 to 7, characterised in that the composition also contains a minor proportion of a particulate refractory filler other than the mineral having a sheet structure. 9. A coated article of graphite-alumina refractory material characterised in that the coating comprises one or more minerals having a sheet structure and a refractory oxide bond. Sϋ STiTUTE SHEET RULE 26

Inventors: JUMA KASSIM, JUMA, KASSIM
Applicants: FOSECO INT, JUMA KASSIM, FOSECO INTERNATIONAL LIMITED, JUMA, KASSIM
Application year: 1994
Main classification: C04B41
IPC codes: C04B41