Organopolysiloxane and method for the preparation thereof

Abstract: An organopolysiloxane for modifying curable organic and silicone compositions is disclosed, said organopolysiloxane having the general formula wherein each R¹ is a monovalent group independently selected from alkyl radicals having 1 to 5 carbon atoms and phenyl radical; R² is a monovalent group independently selected from hydrogen, alkyl radicals having 1 to 5 carbon atoms and phenyl radical; R³ is selected from alkoxysilylalkyl groups and alkyl groups having at least 6 carbon atoms; a is zero or a positive number; b is a positive number; c is a positive number; a/c has a value of zero to <4; b/c has a value of 0.05 to 4; and (a + b)/c has a value of 0.2 to 4, with the proviso that organopolysiloxane has in its molecule at least one said alkoxysilylalkyl group and at least one alkyl group having at least 6 carbons.

Description: The present invention relates to an organopolysiloxane that is composed of monofunctional siloxane units (M units) and tetrafunctional siloxane units (Q units) and that contains in each molecule at least 1 alkoxysilylalkyl group and at least 1 alkyl group having at least 6 carbons. The invention also relates to a method for the preparation of this organopolysiloxane. Among the various organopolysiloxanes known in the art, MQ organopolysiloxane composed of the monofunctional siloxane unit (M unit) and the tetrafunctional siloxane unit (Q unit) is by virtue of its heat resistance used as a starting material for varnishes and pressure-sensitive adhesives JP-A 61-195129. More recently, hydroxyphenyl-containing MQ organopolysiloxane has been taught by JP-A 1-292036, and chloromethyl-containing MQ organopolysiloxane has been taught JP-A 2-153935. MQ organopolysiloxane has also been proposed that contains epoxy-functional organic and alkoxysilylalkyl groups (JP-A 5-105758 & EP-A-541988), and MQ organopolysiloxane has been proposed that contains epoxy-functional organic groups and diorganopolysiloxane residues (JP-A 3-331409). However, MQ organopolysiloxane having alkoxysilylalkyl and C≥6 alkyl groups on the monofunctional siloxane unit silicone (M unit) has heretofore been unknown. The present invention introduces an organopolysiloxane that is composed of the monofunctional siloxane unit (M unit) and tetrafunctional siloxane unit (Q unit) which contains in each molecule at least 1 alkoxysilylalkyl group and at least 1 alkyl group having at least 6 carbons. A method for the preparation of this organopolysiloxane is also provided. Our organopolysiloxane has the general formula given below and contains in each molecule at least 1 alkoxysilylalkyl group and at least 1 alkyl group having at least 6 carbons R 1 is the phenyl group or a lower alkyl group having 5 or fewer carbons. These lower alkyl groups are exemplified by methyl, ethyl, propyl, butyl, and pentyl. R 2 is a group selected from hydrogen atom, phenyl group, and lower alkyl groups having 5 or fewer carbons, such as methyl, ethyl, propyl, butyl, and pentyl. R 3 represents the alkoxysilylalkyl or C≥ 6 alkyl groups (i.e., alkyl groups having at least 6 carbon atoms). The alkoxysilylalkyl groups of R 3 are trimethoxysilylethyl, trimethoxysilylpropyl, trimethoxysilylbutyl, trimethoxysilylpentyl, triethoxysilylethyl, triethoxysilylpropyl, triethoxysilylbutyl, methyldimethoxysilylethyl, methyldimethoxysilylpropyl, dimethylmethoxysilylethyl, and dimethylmethoxysilylThe C≥6 alkyl groups of R 3 are hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, and octadecyl. Preferred here are n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, n-undecyl, n-dodecyl, n-tridecyl, n-tetradecyl, n-pentadecyl, n-hexadecyl, n-heptadecyl, and n-octadecyl. The alkyl group comprising R 3 in our organopolysiloxane must contain at least 6 carbons, but the upper limit on the number of carbons is not specifically restricted. However, when our organopolysiloxane is to be blended into a curable organic resin, the preferred range for the number of carbons in the alkyl group comprising R 3 is 6 to 30 because this yields good compatibility with organic resins and good flexibility on the part of the final cured resin. The subscript a in the preceding formula is zero or a positive number, and it represents the number of monofunctional siloxane units (M unit) that contain neither alkoxysilylalkyl nor C≥6 alkyl. The subscript b in the preceding formula is a positive number, and it represents the number of monofunctional siloxane units (M unit) that carry an alkoxysilylalkyl group or C≥6 alkyl group. The subscript c is a positive number that represents the number of tetrafunctional siloxane units (Q unit). The ratios among these subscripts are as follows: a/c = 0 to <4, b/c = 0.05 to 4, and (a + b)/c = 0.2 to 4. The bases for these ratios are as follows: (i) no more than 4 M units can be present per Q unit; (ii) the presence of less than 0.2 M units per Q unit results in a reduced compatibility with curable organic resins; and (iii) there must be present per Q unit at least 0.05 monofunctional siloxane units (M unit) that carry the alkoxysilylalkyl group or C≥ 6 alkyl group in order for the invention organopolysiloxane to exhibit good miscibility with, and a good stress-relaxation effect on, organic resins. The organopolysiloxane of our invention is a liquid or solid at room temperature. While its weight average molecular weight is not specifically restricted, this parameter preferably falls in the range of 500 to 500,000 because this affords good miscibility with organic resins. In the preparative method of this invention, the hydrosilylation-reaction catalyst comprising component (A) is a catalyst for the addition reaction of the silicon-bonded hydrogen atoms in component (B) across the aliphatically unsaturated bonds in components (C) and (D), as described infra. Component (A) comprises those compounds generally used as hydrosilylation-reaction catalysts, and no specific restrictions otherwise apply to this component. It is exemplified by platinum, rhodium, and palladium compounds, but platinum compounds are preferred. Preferred platinum compounds are chloroplatinic acid, alcohol solutions of chloroplatinic acid, complexes between platinum and aliphatically unsaturated hydrocarbon compounds, platinum-vinylsiloxane complexes, platinum black, and platinum on active carbon. The addition of component (A) in the present invention is not specifically restricted as long as a catalytic quantity is added. When, a platinum compound is used as component (A), it is preferably added in a quantity that provides 0.01 to 500 ppm as platinum metal atoms in component (A) relative to the organopolysiloxane comprising component (B). The organopolysiloxane comprising component (B) is the principal starting material of the present invention, and it is expressed by the following general formula R1 is the phenyl group or a lower alkyl group having 5 or fewer carbons, the latter being specifically exemplified by methyl, ethyl, propyl, butyl, and pentyl. The subscript d is zero or a positive number, and it represents the number of monofunctional siloxane units (M units) that do not carry silicon-bonded hydrogen. The subscript e is a positive number that represents the number of monofunctional siloxane units (M units) that carry silicon-bonded hydrogen. The subscript f is a positive number that represents the number of tetrafunctional siloxane units (Q units). The ratios among these subscripts are as follows: d/f = 0 to <4, e/f = 0.05 to 4, and (d + e)/f = 0.2 to 4. The bases for these ratios are as follows: (i) no more than 4 M units can be present per Q unit; (ii) there must be present per Q unit at least 0.05 SiH-containing monofunctional siloxane units (M units) in order for the invention organopolysiloxane (post-introduction of the alkoxysilylalkyl and C≥ 6 alkyl groups) to exhibit good miscibility with organic resins. Component (B) can be prepared by well-known methods, and are exemplified by: (i) cohydrolysis of tetrahalosilane with monohalosilane, (ii) cohydrolysis of tetraalkoxysilane with monoalkoxysilane, and (iii) hydrolysis of tetraalkoxysilane and tetraorganodisiloxane followed by a re-equilibration polymerization reaction. The method illustrated in JP-A 61-195129 is particularly preferred. This method consists of stirring organosilicon compound selected from hexaorganodisiloxane, tetraorganodisiloxane, triorganohalosilane, and diorganohalosilane in aqueous hydrochloric acid and dripping tetraalkoxysilane into this system. The alkoxysilylalkene of component (C) is the component that introduces the alkoxysilylalkyl group into our organopolysiloxane. Component (C) is exemplified by trimethoxyvinylsilane, trimethoxyallylsilane, trimethoxybutenylsilane, trimethoxypentenylsilane, triethoxyvinylsilane, triethoxyallylsilane, methyldimethoxyvinylsilane, methyldimethoxyallylsilane, methyldimethoxybutenylsilane, methyldiethoxyvinylsilane, methyldiethoxyallylsilane, dimethylmethoxyvinylsilane, dimethylmethoxyallylsilane, triethoxyvinylsilane, and methyldiethoxyvinylsilane. The C≥ 6 alkene comprising component (D) is the component that introduces the C≥6 alkyl group into the present invention. Our preparative method requires that component (D) contain at least 6 carbons. While the upper limit on the number of carbons is not specifically restricted, component (D) preferably contains 6 to 30 carbons because this affords good reactivity with component (B) as well as a good miscibility between the final organopolysiloxane product and curable organic resins. The position of the carbon-carbon double bond in component (D) is also not specifically restricted, but the preferred position is the end of the molecular chain. Component (D) can be hexene, heptene, octene, nonene, decene, undecene, dodecene, tridecene, tetradecene, pentadecene, hexadecene, heptadecene, and octadecene. Preferred as component (D) are 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene, 1-undecene, 1-dodecene, dodecene, 1-tridecene, 1-tetradecene, 1-pentadecene, 1-heptadecene, and 1-octadecene Neither the quantity of addition of component (C) nor the quantity of addition of component (D) is specifically restricted. However, when the removal of unreacted component (D) is problematic, component (D) is then preferably added in a quantity that will provide less than 1 alkenyl group in component (D) per silicon-bonded hydrogen in component (B). The organopolysiloxane product of this invention will contain silicon-bonded hydrogen plus alkoxysilylalkyl and C≥6 alkyl groups when using the preparative method of our invention. Moreover, components (C) and (D) will provide less than 1 aliphatically unsaturated bond per silicon-bonded hydrogen in component (B). When components (C) and (D) together provide more than 1 aliphatically unsaturated bond per silicon-bonded hydrogen in component (B), the organopolysiloxane that will be produced will contain alkoxysilylalkyl and C≥ 6 alkyl groups, but it will be almost free of silicon-bonded hydrogen. The reaction sequence is freely selectable in the preparative method of this invention. Specific examples of the reaction sequence are as follows: (i) components (A) and (B) are first mixed and components (C) and (D) are then added to this system in order to synthesize organopolysiloxane that contains SiH plus alkoxysilylalkyl and C≥6 alkyl groups; or (ii) components (A) and (B) are first mixed, component (C) is then added to this system in order to synthesize organopolysiloxane that contains SiH and alkoxysilylalkyl, and component (D) is subsequently added to the system in order to synthesize organopolysiloxane that contains alkoxysilylalkyl and C≥6 alkyl groups. The reaction temperature is not specifically restricted in our preparative method, but reaction temperatures in the range of 50°C to 150°C are preferred in order to rapidly bring the addition reaction to completion. In addition, organic solvent can be used during the preparative method of our invention. Organic solvents are exemplified by aromatic solvents such as toluene and xylene; aliphatic solvents such as hexane, heptane, and octane; and ketone solvents such as acetone and methyl ethyl ketone. The organopolysiloxane prepared as described above is obtained in the form of a reaction mixture, and it can be purified by distillation of unreacted component (C) or component (D) from the reaction mixture. Since each molecule of the invention organopolysiloxane contains at least 1 alkoxysilylalkyl group and at least 1 C≥6 alkyl group, this organopolysiloxane is useful as an internal stress-relaxing agent or internal release agent for curable resin compositions based on imide resin, phenolic resin, and epoxy resin, and for thermoplastic resins, such as acrylic resin, and polyethylene resin. Moreover, this organopolysiloxane can be used as an adhesion promoter for curable organic resin compositions and curable organopolysiloxane compositions. Finally, our organopolysiloxane can be expected to improve the adhesion between curable resin compositions and metals and also to exhibit the activity of a surfactant with the C≥6 alkyl group acting as hydrophobic group. The invention will be explained in greater detail below through working examples. The viscosity values reported in the examples were measured at 25°C, and the development of the reactions in the examples was monitored by infrared spectrochemical analysis. Example 1 Twenty-five weight parts tetrakis(dimethylsiloxy)silane having the formula 19.25 weight parts of 1-octadecene, and 100 weight parts of toluene were placed in a 1-liter four-neck flask equipped with a stirrer, reflux condenser, and thermometer. The moisture in the system was removed as the azeotrope by heating, and the system was then cooled under a nitrogen blanket. Five drops of a 2 weight% isopropanolic chloroplatinic acid solution were subsequently dripped into the system from a syringe followed by stirring for 1 hour while heating at 105°C and subsequently cooling to room temperature. Fifty weight parts of allyltrimethoxysilane were then dripped into the system followed by stirring the system for 1 hour while heating at 110°C. Another 2 drops of the 2 weight% isopropanolic chloroplatinic acid solution were then dripped into the system, which was thereafter heated for 1 hour at 110°C. The toluene and unreacted substances were removed by heating under reduced pressure at 120°C and 267 Pa (2 mm Hg) to afford 80.6 weight parts of product. This product was a transparent brown liquid having a viscosity of 24 mPa.s (centipoise). The characteristic absorption of the Si-H bond was almost completely absent from the product when measured by infrared spectrochemical analysis. The product had a refractive index of 1.4358. The gel permeation chromatogram of the product gave a weight-average molecular weight (Mw) of 1,530 (standard polystyrene basis) and a dispersity (Mw/Mn) of 1.07. Structural analysis of the product by 1H-nuclear magnetic resonance spectroscopy (NMR), 13C-NMR, and 29Si-NMR confirmed this product to be an organopolysiloxane mixture with the average formula Example 2 One hundred weight parts of organopolysiloxane having the average formula 29.5 weight parts of 1-octadecene, 43.2 weight parts of vinyltrimethoxysilane, and 50.8 weight parts toluene were placed in a 1-liter four-neck flask equipped with a stirrer, reflux condenser, and thermometer. The moisture in the system was removed as the azeotrope by heating, and the system was then cooled under a nitrogen blanket. Five drops of a 2 weight% isopropanolic chloroplatinic acid solution were subsequently dripped into the system from a syringe. After heating while stirring at 120°C - 130°C for 1 hour, 112.9 weight parts of vinyltrimethoxysilane were dripped in at 120°C - 125°C, and the system was again heated for 2 hours at 120°C - 125°C. The toluene and unreacted substances were removed by heating under reduced pressure at 120°C and 267 Pa (2 mm Hg) to afford 257.1 weight parts of product. This product was a colorless transparent liquid with a viscosity of 96.5 mPa.s (centipoise). The characteristic absorption of the Si-H bond was not observed when the product was subjected to infrared spectrochemical analysis. The refractive index of the product was 1.4386. The gel permeation chromatogram of the product gave a weight-average molecular weight (Mw) of 2,580 (standard polystyrene basis) and a dispersity (Mw/Mn) of 1.14. Structural analysis of the product by 1H-NMR, 13C-NMR, and 29Si-NMR confirmed it to be an organopolysiloxane having the average formula

Claims: An organopolysiloxane having the general formula wherein each R 1 is a monovalent group independently selected from alkyl radicals having 1 to 5 carbon atoms and phenyl radical; R 2 is a monovalent group independently selected hydrogen atom, alkyl radicals having 1 to 5 carbon atoms and phenyl radical; R 3 is selected from alkoxysilylalkyl groups and alkyl groups having at least 6 carbon atoms; a is zero or a positive number; b is a positive number; c is a positive number; a/c has a value of zero to <4; b/c has a value of 0.05 to 4; and (a + b)/c has a value of 0.2 to 4, with the proviso that said organopolysiloxane has in its molecule at least one alkoxysilylalkyl group and at least one alkyl group having at least 6 carbons. The organopolysiloxane according to claim 1, wherein said alkyl group having at least 6 carbon atoms is an alkyl group having 6 to 30 carbon atoms. The organopolysiloxane according to claim 2, wherein said alkoxysilylalkyl group is selected from trimethoxysilylethyl, trimethoxysilylpropyl, trimethoxysilylbutyl, trimethoxysilylpentyl, triethoxysilylethyl, triethoxysilylpropyl, triethoxysilylbutyl, methyldimethoxysilylethyl, methyldimethoxysilylpropyl, dimethylmethoxysilylethyl, and dimethylmethoxysilylpropyl radicals. The organopolysiloxane according to claim 1, wherein a = 0. A method for the preparation of an organopolysiloxane comprising reacting in the presence of (A) a hydrosilylation-reaction catalyst: (B) an SiH-containing organopolysiloxane having the general formula wherein each R 1 is a monovalent group independently selected from alkyl radicals having 1 to 5 carbon atoms and phenyl radical; d is zero or a positive number; e is a positive number; f is a positive number; d/f has a value of zero to <4; e/f has a value of 0.05 to 4; and (d + e)/f has a value of 0.2 to 4, (C) an alkoxysilylalkene, and (D) an alkene that contains at least 6 carbons.

Inventors: MORITA YOSHITSUGU, TANAKA KEN, MORITA, YOSHITSUGU, TANAKA, KEN, MORITA, YOSHITSUGU, DOW CORNING TORAY, TANAKA, KEN, DOW CORNING TORAY
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: C08G77
IPC codes: C08G77