Method of connecting a wiring with a semiconductor region and semiconductor device obtained by this method

Abstract: A method for fabricating a semiconductor device having a wiring part (113) connected via an opening portion formed in an insulating film (100,112) on a semiconductor region to the semiconductor region (109), includes the steps of depositing a polycrystalline semiconductor layer (111) over the opening portion on the semiconductor region (109), ion injecting impurities having large range on the polycrystalline semiconductor layer (111), ion injecting impurities having small range on the polycrystalline semiconductor layer (111), conducting heat treatment after the ion injection of the impurities, and depositing a metal or metal silicide containing a low-melting metal on the polycrystalline semiconductor layer (111) after the heat treatment.

Description: The present invention relates to semiconductor devices and fabrication methods thereof, and more particularly to semiconductor devices wherein the connection of semiconductor device with the wiring is improved and to fabrication methods thereof. In recent years, as the higher integration of semiconductor devices has been made, the area of each part within a chip has been reduced, wherein it is an important problem to reduce the area of the wiring part because it occupies a large percentage of chip area. Concerning the lead-out part to the wiring of semi-conductor device or a so-called contact part, while it was conventionally practiced that after an ohmic contact material composed of group IV polycrystalline semi-conductor material was laid down at a position directly above the element, the electrode of a metal or metal silicide containing a low-melting metal such as Al and the group IV polycrystalline semiconductor material were joined off the position directly above the element, it is contemplated that metal or metal silicide is also joined directly above the element at the same time. On the other hand, polycrystalline semiconductor material (e.g., group IV) is undesirable to use as the lead-out wiring, because as the operation frequency of element increases, the movement of carriers for carrying electric current can not follow it, whereby such a constitution is now being adopted that the electrode of metal or metal silicide is contacted directly above the element from the viewpoint of high speed operation. However, a low-melting point metal in the metal or metal silicide for use as low resistive wiring material greatly diffuses into polycrystalline semiconductor material, and when a metal or metal silicide contact is made directly above the element, the low-melting metal will diffuse into the element portion, bringing above degradation of element characteristics in some cases. Accordingly, to suppress the diffusion of low-melting metal, a barrier metal may be disposed between the metal or metal silicide and polycrystalline semiconductor material. With this constitution, the diffusion of low-melting metal is surely suppressed, and the degradation of element characteristics is not caused, but because of a step of depositing and patterning the barrier metal interposed, the process is more complex, with its costs increased. Document US-A-4 637 836 discloses a method to prevent diffusion of boron from a silicon by pre-doping the silicon with phosphorus ions. The publication IBM Technical Disclosure Bulletin, Vol. 27, No. 1B (June 1984), Armonk, New York, US, page 780, by C. Grovenor et. al. "Method for increasing grain size in silicon and germanium by successive doping" describes how large grain sizes in semiconductors can be obtained by multiple doping. It is an object of the present invention to provide a semiconductor device and a fabrication method thereof, wherein with a structure and a method not involving any complex process and increased costs at the contact part of semiconductor device, the diffusion of a low-melting point metal can be suppressed without degradation of the element characteristics. Also, it is another object of the present invention to provide a semiconductor device without degradation of the characteristics by preventing the diffusion of wiring metal to the element area of semiconductor device, while simplifying the process by disposing wiring metal directly above the element area to eliminate the leading of unnecessary wiring. This object of the present invention is achieved by a method for fabricating a semiconductor device as set out in claim 1. Also, this object of the present invention is achieved by a semiconductor device as defined in claim 11. Advantageous further developments are as set out in the dependent claims. Fig. 1 is a typical cross-sectional view for explaining a polysilicon/Al contact part. Figs. 2A and 2B are graphic representations for illustrating how polysilicon at the contact part and Al in the semiconductor region will diffuse. Figs. 3A to 3K are typical cross-sectional views for illustrating the fabrication procedure of a semi-conductor device according to the present invention. Fig. 4, Fig. 7, and Fig. 10 are graphic representations for illustrating the ion injection condition which is set to accomplish a predetermined impurity concentration in practicing the present invention, respectively. Figs. 5A and 5B and Figs. 11A and 11B are graphic representations for showing the effect of the present invention, and showing the Vbe-Ic, Ib characteristic of a bipolar transistor formed by applying the present invention, respectively. Fig. 6, Fig. 8, Figs. 9A and 9B, Fig. 12, Fig. 13 and Fig. 14 are schematic views for explaining other semiconductor device of the present invention, respectively. Fig. 15 is a circuit diagram for illustrating a circuit configuration using a semiconductor device of the present invention. The present invention can accomplish the aforementioned objects by using a fabrication method including the steps of ion injecting impurities having large range into a polycrystalline semiconductor layer, and ion injecting impurities having small range thereinto. Thereby, the impurity concentration near the surface of polycrystalline semiconductor layer can be especially raised. Hence, the crystal having large crystal grain diameter can be formed particularly near the surface by heat treating the polycrystalline semiconductor layer such as polycrystalline silicon having such an impurity concentration distribution. Typically, the diffusion of low-melting metal in the polycrystalline silicon can be made mostly through the grain boundary. Accordingly, as the crystal grain diameter increases, metal diffusion passages are reduced and the amount of diffusion is suppressed to a smaller value. Thus, the present invention can suppress the diffusion of wiring metal formed on the upper layer by making the grain diameter of polycrystalline silicon larger than conventional. In the case of silicon, when n-type is made, there is a phenomenon that crystallization with heat treatment is promoted from the impurity concentration of 5 x 10 20 atoms/cm 3 at the boundary so that polycrystalline silicon of large grain diameter can be obtained (see "1988 Materials Research Society Symposium Proceedings p.135-141"). Accordingly, the present invention can securely realize the crystal of large grain diameter in such a manner that the total concentration of p-type impurities contained in the polycrystalline semiconductor layer through ion injection process of impurities is preferably greater than 5 x 10 19 atoms/cm 3 at a depth of 100nm from the surface of the polycrystalline semiconductor layer, and more preferably greater than 5 x 10 20 atoms/cm 3 . Since this phenomenon begins to be saturated at a concentration of 1 x 10 21 atoms/cm 3 or more, it is desirable to add impurities of 1 x 10 21 atoms/cm 3 or more to implement this phenomenon securely in accordance with the present invention. The present invention will be described below with reference to the drawings. Fig. 1 is a view typically showing the longitudinal structure of a contact part of a semiconductor device. In this example, AlSi is used as one metal or metal silicide electrode 205, and polycrystalline silicon (polysilicon) is used as a polycrystalline semiconductor layer 203. Figs. 2A and 2B are graphs showing the measurement results (i.e., concentration change of Al) of how wiring metal Al is diffused into polysilicon 203 and semiconductor region 201 provided underneath thereof in such contact part. Fig. 2A shows the Al concentration change from the surface of polycrystalline silicon 203 to semiconductor region 201 in the contact part made by a conventional fabrication method. Al has a concentration of 1 x 10 18 atoms/cm 3 or more within polycrystalline silicon 203, increasing at the interface between polycrystalline silicon 203 and semiconductor region 201. Also, it can be found that Al is also greatly diffused in the semiconductor region 201. On the contrary, Fig. 2B shows a distribution of Al concentration at the contact part made by fabrication method of the present invention. As shown in the figure, Al is blocked on the surface side of polycrystalline silicon 203, wherein the Al concentration in the polycrystalline silicon 203 decreases toward the semiconductor region 201. Also, within the semiconductor region 201, the Al concentration can be suppressed to 1 x 10 17 atoms/cm 3 or less, i.e., a lower concentration by one figure. As described above, the diffusion of low-melting metal in polysilicon is typically made mostly through the grain boundary. Therefore, as the crystal grain diameter increases, metal diffusing passages are reduced, so that the amount of diffusion can be suppressed to small value. In the present invention, since the grain diameter of polysilicon which is a polycrystalline semiconductor material is greater than conventional, the diffusion of metal has been suppressed. The grain diameter of polysilicon is determined by the recrystallization of polysilicon which occurs with the heat treatment after the injection of impurities, although recrystallization into large grain diameter is more likely to occur if polysilicon is more amorphous in the state before recrystallization. However, polysilicon will become amorphous upon impact of ion injection, but in the case of B which is a typical p-type impurity, for example, polysilicon does not greatly become amorphous only by the injection of B, because the mass of the ion is light. Accordingly, in the present invention, when p-type is made, polysilicon is made more amorphous by injecting in advance germanium, tin, phosphorus, arsenic, antimony, gallium, or indium having a greater mass than B and not producing many defect levels in the semiconductor, and then the crystal of large grain diameter is produced with the heat treatment after the injection of p-type impurities. Further, the channeling of B can be suppressed by making polysilicon more amorphous before the injection of B, wherein there is an additional effect that the region to be made p-type may not be deeper than necessary. Also, if the concentration of germanium, tin, phosphorus, antimony, gallium, or indium within polysilicon is 1 x 10 19 atoms/cm 3 or more, amorphous conversion will significantly progress to make polysilicon in great grain diameter, and if the amorphous conversion is made to a depth of about 100nm, the diffusion of low-melting metal can be suppressed. Accordingly, to realize the present invention more securely, it is desirable to add at least one of the elements of germanium, tin, phosphorus, antimony, gallium and indium such that the amount is 5 x 10 19 atoms/cm 3 or more at a depth of 100nm from the surface of polysilicon, and the concentration of the element does not exceed the concentration of B over the entire area of polysilicon. The low-melting metal contained in metal or metal silicide for use with the present invention may be typically any of the metals belonging to groups IIB to IIIA, examples of which may include Al, Mg, Cu, Ag, Au, Zn and Cd. For the injection of n-type impurities into polycrystalline silicon or polycrystalline silicon germanium, the injection impurity having large range may be preferably high energy P, and the injection impurity having small range may be preferably low energy P, as well as As, Sb, and Bi. (Embodiment 1) Figs. 3A to 3K show the structure and fabrication process of an embodiment according to the present invention. First, As + ions were implanted into a p-type substrate 1 under the conditions with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 60keV by normal ion injection method, with a mask of desired shape, and thereafter the diffusion of As + ions was made by annealing in the N 2 atmosphere at 1000°C to form an N-type blocking layer 101. Subsequently, B + ions were implanted under the conditions with a dose of 2 x 10 13 atoms/cm 2 and an acceleration voltage of 60keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a P-type blocking layer 102 (Fig. 3A). Epitaxial growth was made on this substrate to form an epitaxial layer 103 having a thickness of 5 µm (Fig. 3B). Thereafter, B + ions were implanted by normal ion injection method under the conditions with a dose of 6 x 10 12 atoms/cm 2 and an acceleration voltage of 100keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a P well 104. Subsequently, P + ions were implanted by normal ion injection method under the conditions with a dose of 7 x 10 15 atoms/cm 2 and an acceleration voltage of 70keV, with a mask of desired shape applied, and the annealing was made in the N 2 atmosphere at 1000°C to form a contact region 105 of the N-type blocking layer 101 (Fig. 3C). Then, a silicon nitride film 106 was deposited 150nm thick by low pressure CVD and patterned in a desired shape. Subsequently, oxidation was made for five hours at 1000°C in the atmosphere of O 2 =4ℓ/min, H 2 =2ℓ/min and N 2 =5ℓ/min to form a field oxide film 107, and then the silicon nitride film 106 was removed (Fig. 3D). Thereafter, B + ions were implanted by normal ion injection method under the condition with a dose of 6 x 10 12 atoms/cm 2 and an acceleration voltage of 80keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a base region 108 (Fig. 3E). Further, As + ions were implanted under the conditions with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 40keV, with a mask of desired shape applied, and the diffusion of As + ions was made by annealing in the N 2 atmosphere at 1000°C to form an emitter region 109 (Fig. 3F). Thereafter, an SiO 2 film 110 was deposited 300nm thick by normal atmospheric pressure CVD to have an interlayer insulating film, and etched in a desired shape through a normal photolithography process to form an opening portion (Fig. 3G). Subsequently, a polysilicon layer 111 was deposited 440nm thick by normal low pressure CVD. Then, as the most characteristic process of the present invention, P + ions were implanted into the polysilicon layer 111 with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 80keV through a step of injecting impurities having great range, and As + ions were implanted with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 120keV through a step of injecting impurities having small range. The ion injection conditions are such that when the resistance of polysilicon layer is sufficiently decreased by setting the dose of P + ions at about 5 x 10 15 atoms/cm 2 , As + ions are injected into the region as indicated by the slanted line in Fig. 4 to accomplish a desired object. Thereafter, the diffusion of P + ions and As + ions was made by annealing in the N 2 atmosphere at 950°C to convert the polysilicon layer into N-type (Fig. 3H). Subsequently, the polysilicon layer 111 was etched in a desired shape through a normal photolithography process (Fig. 3I). Thereafter, an SiO 2 film was deposited 600nm thick by normal atmosphere pressure CVD to have an interlayer insulating film 112, and etched in a desired shape through a normal photolithography process to form an opening portion (Fig. 3J). Then, AlSi 113 was deposited 1000nm by normal sputtering method, and subsequently, etched in a desired shape through a normal photolithography process. Further, heat treatment was conducted in the N 2 atmosphere at 450°C for 30 minutes to make an alloy of AlSi 113 and polysilicon 111. Thereby, wiring electrodes 113 were formed and a semiconductor device of the present invention was completed (Fig. 3K). A comparison between the semiconductor device (semiconductor device A) formed in the above manner and the semiconductor device (semiconductor device B) formed without As injection into the polysilicon portion indicated that the leak current in low voltage range was very large in the Vbe-Ic, Ib characteristic for the semiconductor device B (Fig. 5B), while in the semiconductor device A, it was almost suppressed, and there was clearly seen a relation that Ic, Ib depends exponentially on Vbe in the range of Vbe from 0 to 0.5V (Fig. 5A) (Embodiment 2) Fig. 6 shows the structure of a second embodiment according to the present invention. Each portion is similarly numbered to the embodiment 1. In this embodiment, a semiconductor device was fabricated in the same way as the embodiment 1, except that Sb ions were injected instead of As ions in the process as shown in Fig. 3H. Accordingly, the following explanation is given only regarding the process of Fig. 3H. After the process was performed up to Fig. 3G in the same way as the embodiment 1, P + ions were implanted into the polysilicon layer 111 with a dose of 7.5 x 10 15 atoms/cm 2 and an acceleration voltage of 80keV through a step of injecting impurities having great range, and Sb + ions were implanted with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 180keV through a step of injecting impurities having small range. The ion injection conditions are such that when the resistance of polysilicon layer is sufficiently decreased by setting the dose of P + ions at about 7.5 x 10 15 atoms/cm 2 , Sb + ions are injected into the region as indicated by the slanted line in Fig. 7 to accomplish a desired object. Thereafter, the diffusion of P + ions and Sb + ions was made by annealing in the N 2 atmosphere at 950°C to convert the polysilicon layer into N-type. After that, the same process as the embodiment 1 was performed to fabricate a semiconductor device. A comparison between the semiconductor device (semiconductor device C) formed in the above manner and the semiconductor device (semiconductor device B) formed without Sb injection into the polysilicon portion indicated that the leak current in low voltage range was very large in the Vbe-Ic, Ib characteristic for the semiconductor device B, while in the semiconductor device A, it was almost suppressed, and there was clearly seen a relation that Ic, Ib depends exponentially on Vbe in the range of Vbe from 0 to 0.5V. (Embodiment 3) Figs. 8 and 9A and 9B show the structure of a third embodiment according to the present invention. Fig. 8 is a plan view and Figs. 9A and 9B are typical cross-sectional views taken along the line A-A' and B-B' in Fig. 8. In this embodiment, a CCD was formed on a P-type silicon substrate through a normal CCD process. Fig. 8 only shows a photodiode portion 31 and a vertical CCD (hereinafter referred to as a VCCD) portion 32. In Figs. 9A and 9B, a PN junction is formed between an N-type region 302 and a P-type substrate 301 to have a photodiode for detecting photo signal. Also, a VCCD is formed from an N-type region 303 and polysilicon gate electrodes 305, 306, and the N-type region 303 becomes a potential well in performing storage or transfer of electric charges. Herein, a method of the present invention is used for the doping of polysilicon gates 305, 306. That is, after a polysilicon layer 305 is deposited 440nm thick by normal LP-CVD, P + ions are implanted by normal ion injection method with a dose of 7.5 x 10 15 atoms/cm 2 and an acceleration voltage of 80keV, and further As + ions are implanted with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 120keV. The ion injection conditions are such that when P + ions are implanted with a dose of about 7.5 x 10 15 atoms/cm 2 , As + ions are injected into the region as shown in Fig. 4, similarly to the embodiment 1, to accomplish a desired object. Thereafter, the diffusion of P + ions and As + ions was made by annealing in the N 2 atmosphere at 950°C to convert the polysilicon layer into N-type. After the polysilicon layer 305 was etched in a desired shape through normal photolithography process, an SiO 2 film was deposited 200nm thick by normal atmospheric pressure CVD to have an interlayer insulating film. Then, a polysilicon layer 306 was deposited under the same conditions as the polysilicon layer 305, subjected to ion injection, further annealed similarly, and etched in a desired shape through normal photolithography process to form electrode shape. Subsequently, SiO 2 was deposited 600nm thick by normal atmospheric pressure CVD and SiO 2 film was selectively opened through normal photolithography process to form a contact area with Al. Thereafter, AlSi was deposited 1000nm thick by normal sputtering method, and subsequently, etched in a desired shape through a normal photolithography process. Further, heat treatment was conducted in the N 2 atmosphere at 450°C for 30 minutes to make an alloy of AlSi and polysilicon. Thereby, wiring electrodes 307 were formed and a semiconductor device of the present invention was completed. The semiconductor device as fabricated in the above way allows for very high speed operation because the length of polysilicon as the wiring is short and the most portion is connected via Al wiring. And owing to no diffusion of Al into the lower portion of polysilicon gate, the dispersion in transfer characteristic of charges was eliminated. Also, the contact between polysilicon and Al can be made directly above VCCD without interposition of the diffusion preventing layer of Al, whereby the fabrication process could be simplified. (Embodiment 4) The process as indicated in Fig. 3A to Fig. 3D was performed in the same manner as in the embodiment 1. Thereafter, a silicon nitride film 106 was removed. Then, P + ions were implanted by normal ion injection method with a dose of 4 x 10 13 atoms/cm 2 and an acceleration voltage of 85keV, with a mask of desired shape applied, and the diffusion of P + ions was made by annealing in the N 2 atmosphere at 1000°C to form a base region 108 (Fig. 3E). Further, BF + 2 ions were implanted with a dose of 2 x 10 15 atoms/cm 2 and an acceleration voltage of 85keV, with a mask of desired shape applied, and subsequently, the diffusion of BF + 2 ions was made by annealing in the N 2 atmosphere at 1000°C to form an emitter region 109 (Fig. 3F). Thereafter, the process was performed in the same way as in Fig. 3G of embodiment 1, and as a lower layer structure of the wiring portion, a polysilicon layer 111 was deposited 440nm thick as group IV polycrystalline semiconductor material by normal low pressure CVD. Then, Ge + ions were implanted into the polysilicon layer 111 with a dose of 5 x 10 14 atoms/cm 2 and an acceleration voltage of 150keV through the first injection process of the present invention, and further B + ions as p-type impurities were implanted thereinto with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 30keV through the second injection process. Then, the diffusion of Ge + ions and B + ions was made by annealing in the N 2 atmosphere at 950°C to convert the polysillicon layer into P-type. The injection of Ge + ions is desirably effected in the range as shown in Fig. 10 (Fig. 3H). Thereafter, the process was performed in the same manner in embodiment 1 to fabricate a semiconductor device D. A comparison between the semiconductor device (semiconductor device D) formed in the above manner and the semiconductor device (semiconductor device B) formed without Ge injection into the polysilicon portion indicated that the leak current in low voltage range was very large in the Vbe-Ic, Ib characteristic for the semiconductor device B (Fig. 11B), while in the semiconductor device D, it was almost suppressed, and there was clearly seen a relation that Ic, Ib depends exponentially on Vbe in the range of Vbe from 0 to 0.5V (Fig. 11A). (Embodiment 5) Fig. 12 shows the structure of a fifth embodiment according to the present invention. In this embodiment, the process up to Fig. 3D and from Fig. 3I to the end was the same as the embodiment 1. Accordingly, only the process as shown in Figs. 3E to 3H will be described below. After the process proceeded to Fig. 3D, As + ions were implanted with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 40keV, with a mask of desired shape applied, and subsequently, the diffusion of As + ions was made by annealing in the N 2 atmosphere at 1000°C to form an emitter region 207 and a collector region 208. Thereafter, SiO 2 209 was deposited 300nm thick by normal atmospheric pressure CVD to have an interlayer insulating film, and etched in a desired shape through normal photolithography process to form an opening portion. Subsequently, a polysilicon layer 210 was deposited 440nm thick by normal low pressure CVD. And Ge + ions were implanted into the polysilicon layer 210 with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 150keV, and further B + ions were implanted thereinto with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 30keV. Then, the diffusion of Ge + ions and B + ions was made by annealing in the N 2 atmosphere at 950°C to convert the polysillicon layer into P-type. In the figure, 201 is an N-type blocking layer, 202 is a P-type blocking layer, 203 is an epitaxial layer, 204 is a P well, 205 is a silicon nitride film, 206 is a field oxide film, 211 is an interlayer insulating film, and 212 is a wiring electrode. The material, thickness and fabrication method for each film, not specifically described, are the same as in embodiment 1. A comparison between the semiconductor device (semiconductor device E) formed in the above manner and the semiconductor device (semiconductor device F) formed without Ge injection into the polysilicon portion indicated that the leak current in low voltage range was very large in the Vbe-Ic, Ib characteristic for the semiconductor device B, while in the semiconductor device E, it was almost suppressed, and there was clearly seen a relation that Ic, Ib depends exponentially on Vbe in the range of Vbe from 0 to 0.5V. (Embodiment 6) Fig. 13 shows the structure of a sixth embodiment according to the present invention. First, As + ions were implanted into a p-type substrate under the conditions with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 60keV by normal ion injection method, with a mask of desired shape, and thereafter the diffusion of As + ions was made by annealing in the N 2 atmosphere at 1000°C to form an N-type blocking layer 1301. Subsequently, B + ions were implanted under the conditions with a dose of 2 x 10 13 atoms/cm 2 and an acceleration voltage of 60keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a P-type blocking layer 1302. Then, N-type epitaxial growth was made on this substrate to form an epitaxial layer 1303 having a thickness of 5 µm. Thereafter, B + ions were implanted by normal ion injection method under the conditions with a dose of 6 x 10 12 atoms/cm 2 and an acceleration voltage of 100keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a P well 1304. Subsequently, B + ions are implanted by normal ion injection method under the conditions with a dose of 7 x 10 15 atoms/cm 2 and an acceleration voltage of 30keV, with a mask of desired shape applied, and the annealing was made in the N 2 atmosphere at 1000°C to form a contact region 1305 of the P-type blocking layer 1302. Then, a silicon nitride film 1306 was deposited 150nm thick by normal low pressure CVD and patterned in a desired shape. Subsequently, oxidation was made for five hours at 1000°C in the atmosphere of O 2 =4ℓ/min, H 2 =2ℓ/min and N 2 =5ℓ/min to form a field oxide film 1307, and then the silicon nitride film 1306 was removed. Thereafter, P + ions were implanted by normal ion injection method under the conditions with a dose of 4 x 10 13 atoms/cm 2 and an acceleration voltage of 85keV, with a mask of desired shape applied, and the diffusion of P + ions was made by annealing in the N 2 atmosphere at 1000°C to form a base region 1308. Further, BF + 2 ions were implanted under the conditons with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 85keV, with a mask of desired shape applied, and Ge + ions were implanted under the conditions with a dose of 5 x 10 14 atoms/cm 2 and an acceleration voltage of 100keV. Further, the diffusion of BF + 2 ions and Ge + ions was made by annealing in the N 2 atmosphere at 1000°C to form an emitter region 1309. Thereafter, an SiO 2 film 1310 was deposited 300nm thick by normal atmospheric pressure CVD to have an interlayer insulating film, and etched in a desired shape through a normal photolithography process to form an opening portion. Subsequently, a polysilicon layer 1311 was deposited 440nm thick by normal low pressure CVD. Subsequently, Ge + ions were implanted into the polysilicon layer 1311 with a dose of 5 x 10 14 atoms/cm 2 and an acceleration voltage of 150keV, and further B + ions were implanted with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 30keV. Thereafter, the diffusion of Ge + ions and B + ions was made by annealing in the N 2 atmosphere at 950°C to convert the polysilicon layer into P-type. The injection of Ge + ions is desirably effected in the range as shown in Fig. 10. Subsequently, the polysilicon layer 1311 was etched in a desired shape through a normal photolithography process. Thereafter, an SiO 2 film was deposited 600nm thick by normal atomospheric pressure CVD to have an interlayer insulating film 1312, and etched in a desired shape through a normal photolithography process to form an opening portion. Then, AlSi was deposited 1000nm thick by normal sputtering method, and subsequently, etched in a desired shape through a normal photolithography process. Further, heat treatment was conducted in the N 2 atmosphere at 450°C for 30 minutes to make an alloy of AlSi and polysilicon. Thereby, wiring electrodes 1313 were formed and a semiconductor device of the present invention was completed. A comparison between the semiconductor device formed in the above manner and the semiconductor device B formed in the embodiment 4 indicated that the short-circuit between emitter and base due to diffusion of Al electrode was eliminated and the yield was much improved. (Embodiment 7) Fig. 14 shows the structure of a seventh embodiment according to the present invention. First, As + ions are implanted into a p-type substrate under the conditons with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 60keV by normal ion injection method, with a mask of desired shape, and thereafter the diffusion of As + ions was made by annealing in the N 2 atmosphere at 1000°C to form an N-type blocking layer 401. Subsequently, B + ions were implanted under the conditions with a dose of 2 x 10 13 atoms/cm 2 and an acceleration voltage of 60keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a P-type blocking layer 402. Epitaxial growth was made on this substrate to form an epitaxial layer 403 having a thickness of 5 µm. Thereafter, B + ions were implanted by normal ion injection method under the conditions with a dose of 6 x 10 13 atoms/cm 2 and an acceleration voltage of 100keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a P well 404. Subsequently, P + ions were implanted by normal ion injection method under the conditions with a dose of 8 x 10 13 atoms/cm 2 and an acceleration voltage of 150keV, with a mask of desired shape applied, and the diffusion of P + ions was made by annealing in the N 2 atmosphere at 1000°C to form an N well 405. Subsequently, B + ions were implanted by normal ion injection method under the conditions with a dose of 8 x 10 15 atoms/cm 2 and an acceleration voltage of 150keV, with a mask of desired shape applied, and the diffusion of B + ions was made by annealing in the N 2 atmosphere at 1000°C to form a collector contact portion 406. Then, a silicon nitride film 407 was deposited 150nm thick by normal low pressure CVD and patterned in a desired shape. Subsequently, oxidation was made for five hours at 1000°C in the atmosphere of O 2 =4ℓ/min, H 2 =2ℓ/min and N 2 =5ℓ/min to form a field oxide film 408, and then the silicon nitride film 407 was removed. Thereafter, P + ions were implanted by normal ion injection method under the conditions with a dose of 6 x 10 13 atoms/cm 2 and an acceleration voltage of 50keV, with a photo-resist mask of desired shape applied, and the diffusion of P + ions was made by annealing in the N 2 atmosphere at 950°C to form a base region 409 of PN BJT portion 41. Then, SiO 2 410 was formed 50nm thick on the surface by normal thermal oxidation to have a gate insulating film. Subsequently, a polysilicon layer 411 was deposited 440nm thick by normal low pressure CVD. Then, P + ions were implanted into the polysilicon layer 411 with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 80keV, and the diffusion of P + ions was performed by annealing in the N 2 atmosphere at 950°C to convert the polysilicon layer into N-type. Subsequently, the polysilicon layer 411 was etched in a desired shape through normal photolithography process. Then, after masking in a desired shape with a photoresist, As + ions were implanted by normal ion injection with a dose of 1 x 10 15 atoms/cm 2 and an acceleration voltage of 80keV to inject ions into the portion corresponding to a source 412 and a drain 413 of an NMOS portion 42. Subsequently, after masking in a desired shape with a photoresist, BF + 2 ions were implanted by normal ion injection with a dose of 2 x 10 15 atoms/cm 2 and an acceleration voltage of 50keV to inject ions into the portion corresponding to a source 414 and a drain 415 of a PMOS portion 43 and the portion corresponding to an emitter 416 of a PNP BJT portion 41. Then, the diffusion of As + ions and B + ions was performed by annealing in the N 2 atmosphere at 950°C. Thereafter, an SiO 2 film was deposited 600nm thick by normal atmospheric pressure CVD to have an interlayer insulating film 417, and etched in a desired shape through a normal photolithography process to form an opening portion. Subsequently, a polysilicon layer 418 was deposited 440nm thick by normal low pressure CVD. Ge + ions were implanted into the polysilicon layer 418 with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 150keV, and further B + ions were implanted with a dose of 5 x 10 15 atoms/cm 2 and an acceleration voltage of 30keV. Then, the diffusion of Ge + ions and B + ions was perfomed by annealing in the N 2 atmosphere at 950°C to convert the polysilicon layer into P-type. The injection condition of Ge + ion injection should be contained in the range as shown in Fig. 10. Subsequently, the polysilicon layer 418 was etched in a desired shape through a normal photolithography process. Thereafter, an SiO 2 film was deposited 600nm thick by normal atmospheric pressure CVD to have an interlayer insulating film 419, and etched in a desired shape through a normal photolithography process to form an opening portion. Then, AlSi was deposited 1000nm thick by normal sputtering method, and subsequently, etched in a desired shape through a normal photolithography process. Further, heat treatment was conducted in the N 2 atmosphere at 450°C for 30 minutes to make an alloy of AlSi and polysilicon. Thereby, wiring electrodes 420 were formed and a semiconductor device of the present invention was completed. The evaluation for the semiconductor device (semiconductor device G) as formed in the above way for the delay time with a circuit configuration as shown in Fig. 15 indicated that the time constant was reduced by about 70 to 80%, as compared with the semiconductor device (semiconductor device H) fabricated with the emitter electrode of PNP BJT formed off the position directly above the base portion. While polysilicon was used as polycrystalline semiconductor material in the above embodiments 4 to 7, it should be noted that germanium can be used as the main component. Also, while Ge was used as the injection material in the first injection process in the above embodiments 4 to 7, it should be noted that the same effects can be also obtained by using tin, phosphorus, arsenic, antimony, gallium, or indium. As described above, with the present invention, the structure or method without involving any complex process or increase of cost in the contact portion of semiconductor device can be used to suppress the diffusion of low-melting metal, and it is possible to provide a semiconductor device without degradation in element characteristics and a fabrication method thereof. Further, with the present invention, the impurity concentration near the surface of a polycrystalline semiconductor layer can be especially increased by practicing a step of ion injecting impurities having great range into the polycrystalline semiconductor layer such as polycrystalline silicon and a step of ion injecting impurities having small range to form the crystal having large crystal grain diameter particularly near the surface by subsequent heat treatment. In this way, with the present invention, the diffusion passages of wiring metal formed on the upper layer can be reduced by making the grain diameter of polycrystalline silicon larger than conventional, and the diffusion of wiring metal into the semiconductor element region can be suppressed, whereby the degradation of element characteristics can be prevented. Also, the step of forming barrier metal which was conventionally provided can be eliminated, so that there is the effect that the process can be simplified and the cost is reduced. Also, the contact portion can be disposed directly above the element, but not at the position far away from the element region in fear of metal diffusion, thereby eliminating the need of leading the excess wiring, whereby there is the effect that the high speed operation as well as the stable characteristic can be realized. More specifically, referring to the Vbe-Ic, Ib characteristic, it will be found that the lead current in the low voltage range has been almost suppressed, and the characteristic improved. Also, the short-circuit between emitter and base due to the diffusion of Al electrode can be completely eliminated, so that the yield has been greatly improved. A comparison of a semiconductor device having the emitter electrode of PNP BJT placed off the site directly above the base portion with a delay circuit indicated that the time constant was reduced by about 70 to 80%. It will be understood that the present invention is not limited to the embodiments and the drawings as above stated, and various variations and combinations can be appropriately effected within the scope of the appended claims.

Claims: A method for fabricating a semiconductor device having a wiring part connected via an opening portion formed in an insulating film ( 110 ) on a semiconductor region ( 108, 109 ) to said semiconductor region, including the steps of depositing a polysilicon layer ( 111 ) over said opening portion on said semiconductor region ( 109 ); ion injecting impurities into said polysilicon layer ( 111 ) under injection conditions leading to a large range, thereby converting at least a part of said polysilicon layer into an amorphous state; ion injecting impurities into said polysilicon semiconductor layer ( 111 ) under injection conditions leading to a small range; conducting a heat treatment after the ion injection of said impurities; and depositing a metal or metal silicide ( 113 ) containing a low-melting point metal on said polysilicon layer after said heat treatment. A method for fabricating a semiconductor device according to Claim 1, characterized in that through said ion injection process of impurities, the total concentration of impurities contained in said polycrystalline semiconductor layer is greater than 5 x 10 19 atoms/cm 3 at a depth of 100nm from the surface of said polycrystalline semiconductor layer. A method for fabricating a semiconductor device according to Claim 1, characterized in that said polycrystalline semiconductor is polycrystalline silicon or polycrystalline silicon germanium. A method for fabricating a semiconductor device according to Claim 2, characterized in that the total concentraion of impurities is greater than 5 x 10 20 atoms/cm 3 . A method for fabricating a semiconductor device according to Claim 1, characterized in that said impurity having great range is an n-type impurity. A method for fabricating a semiconductor device according to Claim 5, characterized in that said n-type impurity is an element selected from phosphorus, arsenic and antimony. A method for fabricating a semiconductor device according to Claim 1, characterized in that said impurity having great range is an element selected from germanium, tin, phosphorus, arsenic, antimony, gallium and indium. A method for fabricating a semiconductor device according to Claim 1, characterized in that said impurity having small range is an n-type or p-type impurity. A method for fabricating a semiconductor device according to Claim 8, characterized in that said n-type impurity is an element selected from phosphorus, arsenic, antimony and bismuth. A method for fabricating a semiconductor device according to Claim 8, characterized in that said p-type impurity is boron. A semiconductor device comprised of a semiconductor region ( 108, 109 ); an insulating film ( 110 ) applied on said semiconductor region, and a wiring part connected via an opening portion formed on said insulating film to said semiconductor region, said wiring part comprising: a polysilicon layer of large grain size ( 111 ) containing p-type impurities disposed on the semiconductor region ( 109 ); with said polysilicon layer additionally containing at least one of the elements of germanium, tin, phosphorus, arsenic, antimony, gallium, and indium; and a metal or metal silicide ( 113 ) at least containing a low-melting point metal disposed directly on said polysilicon layer. A semiconductor device according to Claim 11, characterized in that the concentration of germanium, tin, phosphorus, arsenic, antimony, gallium, or indium contained in said group IV polycrystalline semi-conductor material exceeds 5 x 10 19 atoms/cm 3 at a depth of 100nm from the surface of said group IV polycrystalline semiconductor material and does not exceed the p-type impurity concentration over the entire region of said group IV polycrystalline semiconductor material. A semiconductor device according to Claim 11, characterized in that said group IV polycrystalline semiconductor material has at least one of silicon and germanium as the main component.

Inventors: GOFUKU IHACHIRO, GOFUKU, IHACHIRO, GOFUKU, IHACHIRO, C/O CANON KABUSHIKI KAISHA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1994
Main classification: H01L21
IPC codes: H01L21