Method of manufacturing semiconductor device utilizing selective CVD method

Abstract: A method of manufacturing semiconductor devices, which comprises the steps of forming a first conductive region of a first conductive material for effecting a growth of a conductive film thereon by a selective growth method. A second conductive region of a second conductive material for not effecting a growth of a conductive film is formed in the selective growth method. An insulating layer is covered with the first and second conductive regions. A through hole in the insulating layer for filling the hole with the conductive film is formed. The conductive film is grown within said through hole over the first conductive region, thereby filling the through hole with the conductive film.

Description: The present invention relates to a method of manufacturing a semiconductor device. US-A-5 192 713 discloses a method of manufacturing a semiconductor device, comprising the steps of forming a first conductive region consisting of a first conductive material for effecting a growth of a conductive film directly thereupon by a selective growth method, forming a second conductive region consisting of a second conductive material for not effecting a growth of a conductive film thereupon in said selective growth method, forming an insulating layer covering said first and second conductive regions, forming a through hole in said insulating layer for growing a conductive film over said first conductive region by said selective growth method, and growing said conductive film within said through-hole formed in said insulating layer directly over said first conductive region by said selective growth method and filling said through-hole with said conductive film. EP-A-0 427 254 discloses a method of manufacturing a semiconductor device, comprising the steps of depositing an insulating layer, forming contact holes therein, depositing a transition metal layer over the whole surface, forming a silicide in the holes by annealing, removing the remaining transition metal layer, and selectively growing tungsten plugs on the silicide. Therein, the transition metal layer may be formed of Ti, Ni, Co or W. Tungsten may be selectively grown on the transition metal silicide layer for forming a conductive film within said through-holes. EP-A-0 465 152 and aforementioned US-A-5 192 713, respectively, disclose a step of selectively filling some holes with a metal plug while leaving other openings unfilled. Moreover, aforementioned EP-A-0 465 152 discloses use of a selectively non-filled hole as an alignment mark. In general, within a recent trend of increased density of a semiconductor integrated circuit, a contact hole to be formed in the insulating layer on a semiconductor substrate becomes high in aspect ratio. As a result, a technique of burying a contact hole with a conductive material is now being adopted in an attempt to keep the surface of an insulating as flat as possible and to assure the reliability of a wiring layer to be formed on the insulating layer. As a means to bury a contact hole (through hole), there have been known a blanket method and a selective CVD method. According to the blanket method, a conductive material such as tungsten is deposited all over the surface of an insulating layer including the interior of a through hole formed in an insulating layer on a semiconductor substrate, and then the whole surface of the deposited layer is etched back so as to ultimately leave tungsten only in the through hole. On the other hand, according to the selective CVD method, a high-melting point metal such as tungsten is selectively grown only on a specific conductive material exposed on the bottom of a through hole. Both of the methods are different in process from each other, and have both merits and demerits, setting forth many problems to be solved. In the selective CVD method, the characteristics of a high-melting point metal halide that the reduction reaction rate thereof is dependent largely on an underlayer is utilized. For example, in the case of WF6, a tungsten film can be deposited only on a specific material such as Si and W, and can be hardly deposited on an insulating material such as SiO 2 . Therefore, this phenomenon is very useful in filling a through hole or via hole with a high-melting point metal. In this selective CVD method however, it is required in order to achieve a desirable selectivity to the underlayer to determine an optimum condition for effecting a reduction reaction such as hydrogen reduction or silane reduction of WF 6 by adjusting the deposition temperature or flow ratio of a mixed gas. This selective CVD method however has been found to have the following defects. It is very difficult to distinguish a film which allow the growth of for example tungsten from a film which does not allow the growth of tungsten among exposed films of conductive materials usually employed for semiconductor devices, such as silicon, a high-melting point metal and a metal silicide. A reason for this is that the deposition conditions such as deposition temperature and flow ratio of a mixed gas are required to be delicately adjusted, thus setting forth problems of stability and reproducibility in an actual process, and thereby causing tungsten to grow on every exposed surfaces of conductive materials during the step of the selective growth. As a result, it is no more possible under such circumstances to distinguish a film which allows the growth of for embodiment tungsten from a film which does not allow the growth of tungsten. Therefore, when there are a plurality of through holes different in depth from each other and if tungsten is indiscriminately grown burying the through holes, a shallowest through hole is first filled up with tungsten, and then next shallower through hole is filled up with tungsten, and so on. Accordingly, when the growth of tungsten is continued in this manner, tungsten filling the shallowest through hole is overflowed from the brim of the through hole. Therefore, with this selective growth method, the amount of tungsten to be grown is inevitably restricted according to the depth of the shallowest through hole. FIG. 1 explains one embodiment of the conventional selective CVD method. In this selective CVD method, a MOS transistor is formed on a silicon substrate 201, wherein the reference numeral 203 denotes a diffusion layer, 204 a gate insulating film, and 206 a gate electrode (wiring) consisting for embodiment of tungsten silicide-polycide. After depositing an oxide insulating film 218 all over the substrate, predetermined portions of the oxide insulating film 218 for embodiment over the silicon substrate 201, over the diffusion layer 203 or over the gate electrode 206 are perforated to form through holes 210-1, 210-3 and 210-6. The depth of each of the through holes 210-1, 210-3 and 210-6 is dependent upon the material of the underlayer disposed at the bottom of each through hole. When the conventional selective CVD method is subsequently executed to grow a layer of tungsten 216, the growth of tungsten is obstructed on the oxide insulating film 218, but the growth of tungsten is effected selectively as shown in FIG. 2 on the silicon substrate 201, the diffusion layer 203 and the gate electrode 206 exposed on the bottoms of these through holes. In this case, since the depth of each of through holes differs according to the material of the underlayer, if the growth of tungsten is effected to match with the depth of the through holes 210-1 and 210-3, tungsten 216 is overflowed from the brim of the shallow through hole 210-6. On the other hand, there is another technique different from that explained above in the selective growth of tungsten. According to this technique, as shown in FIG. 3, the growth of tungsten is effected to match with the depth of the shallowest through holes 210-6 so that the deep through holes 210-1 and 210-3 are incompletely filled with tungsten as in the case of a non-volatile memory wherein the shallowest through hole 210-6 is formed over a control gate electrode of memory cell having a stacked gate structure. FIG. 4 explains another embodiment of structure wherein the oxide insulating film 218 is a 2-ply layer consisting of layers 218-1 and 218-2, and a shallowest through hole 210-62 is formed over a wiring 206-2 formed on the first layer of the oxide insulating film 218-1, so that the depth of the shallowest through hole 210-62 much differs from the depths of the through holes 210-1 and 210-3 over the silicon substrate (a diffusion layer). When the growth volume of tungsten is matched with the depth of the shallowest through hole 210-6 or 210-62 in these two typical embodiments, the contact to a wiring layer at the deep through holes 210-1 and 210-3 may become insufficient, so that the effect of filling the through holes with tungsten would be substantially lost thus raising a problem. It can be said that the defects as mentioned above are brought about from the technique of discriminately growing tungsten over the whole through holes when there are a plurality of through holes having different depths from each other. There is another problem in the above-mentioned technique of the contact-filling when it is applied to the manufacture of semiconductor devices as explained below. Namely, in the step of forming aluminum wiring layer for obtaining a desired electric contact in subsequent to the perforation of a through hole, a pattern of a deep through hole 210-1 is generally utilized as an alignment mark for the patterning of a wiring layer. However, when the deep through hole 210-1 is filled with a conductive material by using the above-mentioned burying technique of realizing an excellent flatness, the step which is formed around the upper portion of the deep through hole 210-1 is now lost thereby causing the detection of the alignment mark (the pattern of the through hole 210-1) difficult, thus increasing the possibility of false detection. It is also pointed out as a problem that it is difficult according to the conventional selective CVD growth method to detect an alignment mark consisting of a through hole pattern in the step of forming aluminum wiring layer. The present invention has been accomplished in view of solving above problems, and its object is to provide a method of manufacturing a semiconductor device, which is capable of selecting desired one or ones of through holes among a plurality of through holes having different depths from each other, and allows a high-melting point metal such as tungsten to be filled into only desired one or ones of the through holes, and at the same time capable of easily detecting an alignment mark consisting of a through hole pattern. According to the present invention, there is provided a method of manufacturing a semiconductor device, which comprises steps as specified in claim 1. According to this method of manufacturing semiconductor devices, it is possible to select desired one or ones of through holes among a plurality of through holes having different depths from each other, and allows a high-melting point metal such as tungsten to be filled into only desired one or ones of the through holes, and at the same time to easily detect an alignment mark consisting of a through hole pattern. Further improvements according to the present invention are specified in the sub-claims. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: FIG. 1 is a partial sectional view of a wafer substrate representing a step of a selective CVD growth method to be utilized in the conventional manufacturing method of a non-volatile memory; FIG. 2 depicts a partial sectional view of a wafer substrate explaining a next step following the step shown in FIG. 1; FIG. 3 is a partial sectional view of a wafer substrate explaining a different step from that of the selective CVD growth method shown in FIG. 2; FIG. 4 is a partial sectional view of a wafer substrate explaining a different step from those shown in FIGS. 2 and 3; FIG. 5 is a partial sectional view of a wafer substrate representing a step of a selective CVD growth method to be utilized in the manufacturing method of a non-volatile memory according to the present invention; FIG. 6 is a partial sectional view of a wafer substrate explaining a next step following the step shown in FIG. 5; FIG. 7 is a partial sectional view of a wafer substrate explaining a next step following the step shown in FIG. 6; FIG. 8 is a partial sectional view of a wafer substrate explaining a next step following the step shown in FIG. 7; FIG. 9 is a partial sectional view of a wafer substrate explaining a next step following the step shown in FIG. 8; FIG. 10 is a partial sectional view of a wafer substrate explaining a next step following the step shown in FIG. 9; FIG. 11 is a partial sectional view of a wafer substrate explaining a final step following the step shown in FIG. 10; FIG. 12 is a partial sectional view of a wafer substrate explaining another embodiment wherein another constituent added to the construction shown in FIG. 11; FIG. 13 is a partial sectional view of a wafer substrate explaining a final step of another embodiment (which corresponds to the step shown in FIG. 11) according to the present invention; FIG. 14 is a partial sectional view of a wafer substrate explaining another embodiment wherein another constituent added to the construction shown in FIG. 13; FIG. 15 is a partial sectional view of a wafer substrate explaining a final step in another process; FIG. 16 is a partial sectional view of a wafer substrate explaining a final step in still another embodiment of the present invention; FIG. 17 is a partial sectional view of a wafer substrate explaining a final step in still another embodiment of the present invention; and FIG. 18 is a partial sectional view of a wafer substrate explaining a final step in still another process. This invention will be further explained with reference to the embodiments shown in the drawings. FIGS. 5 to 7, and FIGS. 8 to 10 represent sectional views showing major steps in the manufacturing process of a non-volatile memory for explaining a first embodiment of this invention. According to the manufacturing method of this invention, at first, a first conductive region consisting of a first conductive material is formed on part of the surface of a semiconductor substrate, then a second conductive region consisting of a second conductive material is formed on other part of the surface of the semiconductor substrate, and subsequently an insulating layer is formed all over the surface of the semiconductor substrate. Namely, as shown in FIG. 5, an element isolation oxide film 102 and a semiconductor element (for embodiment, MOS transistor) are formed on a p-type silicon (Si) substrate 101, and then a CVD oxide film 109 is deposited all over the surface of the semiconductor substrate. Further, a gate insulating film 100 is formed on the substrate 101, and a gate electrode 106 is formed on the gate insulating film 100. This gate insulating film 100 is for embodiment a polycide gate electrode comprising a polycrystalline silicon 104 and a layer of WSi 2 (tungsten silicide) 105 stacked on the polycrystalline silicon 104. Source and drain diffusion layers 103 are formed on the surface region of the substrate 101. Simultaneous with the formation of the MOS transistor, a wiring layer 107 consisting of a polycide layer which has been deposited in the same step as that of the gate electrode 106 is formed. This wiring layer 107 may be a single layer of WSi 2 deposited either in the same step as that of the gate electrode 106 or in a separate step. In any case, the effect of this invention as explained hereinafter will be obtained. In this embodiment however, this wiring layer 107 will be explained as being a stacked structure comprising a polycrystalline silicon 104 and a layer 105 of WSi 2 stacked on the polycrystalline silicon 104. An underlayer of this wiring layer 107 may be any kind of material, but in this embodiment, one embodiment wherein the wiring layer 107 is formed on an element isolation film 102 is shown. In an ordinary process of manufacturing a semiconductor device, an alignment mark is formed on the semiconductor substrate by utilizing a through hole pattern as explained hereinafter in the process of forming an aluminum wiring to be electrically connected to an under layer via a through hole which is perforated in advance in the aforementioned CVD oxide film 109. An underlayer of this through hole pattern to be utilized as an alignment mark may be any kind of material or structure, but in this embodiment, one embodiment wherein the underlayer comprises a single layer 108 of WSi 2 is shown. Subsequently, an etching resist pattern (not shown) is formed on the CVD oxide film 109, and then a prescribed portion of the CVD oxide film 109 is etched off by using the resist pattern as a mask, thereby forming a through hole 110-3 to bring into contact with the silicon diffusion layer 103, as well as forming through holes 110-5, 110-7 and 110-8 to bring into contact with the WSi 2 layers 105, 107 and 108 respectively. A high melting point metal for embodiment Ti (titanium) 111 as a fourth conductive material is then formed as shown in FIG. 7 on all over the surface of the substrate 101 thereby depositing a layer of Ti 111, about 30 nm in thickness. Subsequently, the layer of Ti 111 is transformed into a silicide by heat-treating it at a temperature according to a silicide process. Unreacted portion of Ti 111 which is disposed on the CVD oxide film 109, and therefore is not transformed into a silicide in this step of heat treatment is then etched off by treating it with for embodiment an acid. As a result, a titanium silicide layer is formed respectively on the diffusion layer 103 of the silicon substrate and on the bottom surface of the contact hole of each WSi 2 layer 105, 107 and 108 as shown in FIG. 8. In this case, the titanium silicide layer which is disposed on the diffusion layer 103 of the silicon is in the form of TiSi 2 112, but the titanium silicide layers which are disposed on the WSi 2 layer 105, 107 and 108 are turned respectively into the form of TiSi x (x < 2) 113. Subsequently, a step is taken for forming, through natural oxidation, a silicon oxide film (SiO 2 ) 114, about 5 nm in thickness on the TiSi 2 112 layer disposed over the silicon diffusion layer 103, and a titanium oxide film (TiO x ) 115, about 20 nm in thickness on the TiSi x 113 layer disposed over the WSi 2 layer 105, 107 and 108 as shown in FIG. 9. This step of forming the oxide layers may be performed through a wet oxidation process using for embodiment a mixed solution of sulfuric acid and hydrogen peroxide. However, these oxide layers may be spontaneously formed without performing such a specific oxidation step as mentioned above during the aforementioned step of etching off the Ti 111 which is not yet transformed into a silicide. Subsequently, the silicon oxide film 114 is removed under a condition wherein only the silicon oxide film 114 can be etched off by making use of the difference in thickness between the silicon oxide film 114 and TiO x 115. For example, the silicon oxide film 114 can be etched off using an anisotropic RIE (reactive ion etching) method under a condition which allows only the silicon oxide film 114 to be selectively etched in preference to the TiO x 115. Since the thickness of the silicon oxide film 114 to be etched off is about 5 nm at most, a wet etching process may be employed other than the RIE method. A process of CVD selective growth is then performed to deposit W (tungsten) as a third conductive material on the TiSi 2 112 layer disposed over the silicon diffusion layer 103. In this case, since the TiO x 115 is still left as it is on the WSi 2 layer 105, 107 and 108 as shown in FIG. 10, W 116 is selectively grown only on the TiSi 2 112 layer over the silicon diffusion layer 103 thereby forming a buried plug. Thereafter, the TiO x 115 left on the WSi 2 layer 105, 107 and 108 is etched off thereby exposing the TiSi x 113. Finally, as shown in FIG. 11, a metallic wiring for embodiment a multi-layered wiring layer 117 is formed by depositing Ti, TiN and Al-Si-Cu in this order whereby electrically connecting it with the bottom of each through hole, and then a top passivation film 118 is formed thereon. In a first embodiment as explained above, a titanium silicide layer is respectively deposited on the silicon diffusion layer 103 substantially consisted of Si and constituting the bottom of a through hole and on the WSi 2 layer 105, 107 and 108 in subsequent to the formation of a through hole 110 in the CVD oxide film 109 disposed over the semiconductor substrate 101, and is then oxidized. As a result, a silicon oxide film (SiO 2 ) 114, about 5 nm in thickness is formed on the TiSi 2 112 layer disposed over the silicon diffusion layer 103, and a titanium oxide film (TiO x ) 115, about 20 nm in thickness is formed on the TiSi x (x < 2) 113 layer disposed over the WSi 2 layer 105, 107 and 108. After the silicon oxide film (SiO 2 ) 114 is removed under a condition wherein only the silicon oxide film 114 can be etched off by making use of the difference in thickness between the silicon oxide film 114 and TiO x 115, tungsten (W) is allowed to be selectively grown by means of CVD method. In this case, since the TiO x 115 is still left as it is on the WSi 2 layer 105, 107 and 108, W 116 is selectively grown only over the silicon diffusion layer 103. According to the first embodiment as explained above, it is possible to selectively grow tungsten only in a through hole over a silicon substrate (diffusion layer), which is largest in depth and most needed for performing a contact-burying process. Therefore, it is now possible to meet to the actual requirements in the introduction of selective contact-growth technique. Moreover, since tungsten is not grown in a through hole to be used for an alignment mark in the process of forming a wiring 117 of such as Al, it is possible to carry out the burying technique without setting forth problems of losing a step portion around the through hole and inviting inconvenience in detecting the alignment mark. In the aforementioned first embodiment, the explanation is made on a case where a through hole which is directly opened to silicon is formed only over the substrate (a diffusion layer), and any of the gate electrode, wiring layer and the underlayer of alignment mark pattern are provided as an uppermost layer with a WSi 2 layer, so that tungsten can be selectively grown only over the substrate (a diffusion layer). FIG. 12 illustrates another embodiment wherein an additional constituent is added to the construction shown in FIG.11. In this embodiment, the same portions as those explained in FIG. 11 are indicated by the same reference numerals as in FIG. 11 for the sake of omitting the explanations thereof. Although it has been explained in the embodiment shown in FIG. 11 that the titanium silicide layer (TiSi 2 ) 112 is formed as an underlayer over the silicon diffusion layer 103, the underlayer is not limited to a single layer of the titanium silicide layer 112, but may be a multi-layer consisting of an conductive layer 120 made of, for example, epitaxially grown Si and a titanium silicide layer (TiSi 2 ) 112 provided on the conductive layer 120. Further, although it has been explained in the embodiment shown in FIG. 11 that the titanium silicide layer (TiSi x ) 113 is formed as a mask pattern underlayer over the tungsten silicide (WSi 2 ) layer 108, but the mask pattern underlayer may be formed into a structure wherein the titanium silicide layer 113 is electrically connected to the wiring layer 117 of Al and the like. FIG. 13 illustrates a partial sectional view of a wafer substrate explaining a final step of another embodiment (which corresponds to the step shown in FIG. 11) according to the present invention. This embodiment differs from that shown in FIG. 11 in that tungsten silicide (WSi 2 ) 108 is employed as a material for underlayers of the gate electrode, wiring layer and the underlayer of alignment mark pattern, which also constitute underlayers of through holes not to be filled with tungsten, and that a polycrystalline silicon 119 is employed as a material for the underlayer (such as a gate electrode or a wiring layer) of relatively deep through holes if tungsten is to be filled into the relatively deep through holes. If the underlayers of through holes (such as a gate electrode or a wiring layer) are formed in advance with a material which allows the deposition of tungsten in separate to underlayers on which the deposition of tungsten should not be allowed in the embodiment shown in FIG. 13, the manufacturing steps after the formation of the through holes would be the same as that of the embodiment shown in FIG. 11. Namely, in this embodiment, a layer of TiSi 2 and a layer of SiO 2 are formed in this order on the silicon substrate (a diffusion layer) and on the polycrystalline silicon, so that once the layer of SiO 2 is removed, tungsten can be selectively formed on the layer of TiSi 2 . On the other hand, since the TiSi x (x < 2) layer 113 and the TiO x layer are formed in this order on the WSi 2 layer, tungsten would not be deposited over the WSi 2 layer 113. In most of the actual semiconductor device, a plurality of through holes having a different depth from each other are coexisted in the same substrate, so that it is advisable not to fill a conductive material such as tungsten into a through hole which is relatively small in aspect ratio and shallow in depth, but to fill a conductive material in such a manner as to match the depth of a through hole which is relatively high in aspect ratio and the shallowest in depth among through holes to be filled with a conductive material. In the embodiments explained above, a silicon substrate (a diffusion layer) and polycrystalline silicon are selected as an embodiment of underlayer film of a through hole to be filled with tungsten. However, since the method of this invention is effective as long as the oxide film to be formed on the surface of a silicon film as a result of the reaction between the underlayer and Ti deposited on the underlayer is in the form of SiO 2 , a silicon-rich (a high silicon concentration) silicide film or a laminated film including the silicon-rich silicide film as an uppermost layer can also be employed. FIG. 14 illustrates a sectional view of a wafer substrate as obtained in the final step according to another embodiment of this invention. In this embodiment shown in FIG. 14, it is demonstrated that various structures explained in FIG. 12 and FIG. 13 can be concurrently realized in a single substrate. Accordingly, the explanations of these structures in FIG. 14 are omitted. In the embodiments explained above, a single layer of tungsten silicide or a polycide comprising WSi 2 (an upper layer) and polycrystalline silicon (a lower layer) is employed as an embodiment of the underlayer of a through hole not to be filled with tungsten (or an underlayer film which does not allow the growth of tungsten), i.e. the underlayer of the gate electrode, wiring layer or alignment mark pattern. However, the material for the underlayer inhibiting the growth of tungsten is not restricted to these embodiments. In the case where Ti is deposited on the underlayer for prohibiting growth of W, a silicon-poor silicide film, such as a TiSi x (x < 2) film, will be formed. This silicide film is silicon-poor (having low Si concentration). On the silicon-poor TiSi x film there can be formed an oxide film, e.g., a TiO x film or a film mainly consisting of TiO x , which is thicker than an SiO 2 film. Hence, the advantage of this invention can be achieved by using a material which can form such an oxide film on the silicon-poor TiSi x film. In other words, a material for the underlayer film which does not allow the growth of tungsten is not restricted to tungsten silicide (WSi 2 ) film, but any other silicide film or similar film which supplies only an insufficient amount of silicon during the formation of titanium silicide may be employed. For embodiment, a metal selected from W, Mo, Ti, Al and Cu, or a silicide thereof, or a laminated film including one of these metal as an uppermost layer may be employed for such an underlayer film. Further, a material for forming a silicide is not restricted to Ti employed in the above embodiments. Other high melting point metals such as Ti, Co, Ni or Mo may be employed as long as an oxide (MOx) to be formed during a subsequent oxidation step of the material is relatively large in thickness as compared with the SiO 2 layer which is at most about 5 nm in thickness, and at the same time is capable of etching the SiO 2 under the condition wherein the etching selectivity of SiO 2 to MOx is enlarged. Additionally, if a silicon-poor silicide film (MSi x ) or a metal film which is capable of forming MOx (a film which is much thicker as compared with a SiO 2 layer having a thickness of at most about 5 nm, or a film which will be left after the etching step of SiO 2 due to its slow etching rate as compared with that of SiO 2 ) in preference to SiO 2 is employed, the step of forming a silicide may be dispensed with. FIG. 15 illustrates the final step in a process where the step of forming a silicide is omitted. In this FIG. 15, polycrystalline silicon 119 is employed as an example of an underlayer of a through hole to be filled with tungsten 116, while metallic molybdenum Mo 124 is employed as an example of an underlayer of a through hole not to be filled with tungsten 116. In this case, when a semiconductor substrate is exposed to a light oxidation atmosphere in subsequent to the formation of through holes, a SiO 2 layer is formed at the bottom of a through hole to be subsequently filled with tungsten, and at the same time a MOx layer is formed at the bottom of a through hole not to be filled with tungsten. The SiO 2 layer is subsequently removed thus leaving the MOx layer as it is. As a result, since the MOx layer is left unremoved, tungsten is selectively grown only on the regions where the SiO 2 layer is removed. As for the material to be selectively grown, any other metals (such as Al, Si or Cu) other than tungsten may be employed without hindering the effect of this invention as long as the metal has the same degree of selectivity as that of tungsten. In the above embodiments, an electric connection of a silicon substrate (a diffusion layer) or of electrodes to the wiring layer is effected through tungsten for instance which has been filled into a through hole. Further, the expression of through hole used throughout the above embodiments is described as an embodiment to be used for a structure of so-called contact hole. However, this through hole is also applicable to a via hole. For embodiment, FIG. 16 illustrates a laminated structure comprising a first insulating film (SiO 2 ) 130 and a second insulating film (SiO 2 ) 131, wherein tungsten 122 for embodiment is filled into through holes, i.e. via holes 410-1 and 410-2 formed in the second insulating film (SiO 2 ) 131 in order to realize an electrical connection between the electrodes or wirings 119, 120 formed on the first insulating film (SiO 2 ) 130 and the electrodes or wirings 123 formed on the second insulating film (SiO 2 ) 131. As clearly understood from FIG. 16, there is no substantial distinction between a contact hole and a via hole as far as the effect to be obtained by the application of this invention is concerned. The embodiment shown in FIG. 16 will be further explained in detail as follows. First, a diffusion layer 103 and electrodes 205, 206 are formed on a silicon substrate 110, and then the first insulating film (SiO 2 ) 130 is deposited. Thereafter, through holes (contact holes) 310-1 and 310-2 are formed in the first insulating film (SiO 2 ) 130, and tungsten 116 is selectively grown on a metal silicide 207 formed at the bottom of the through holes (contact holes) 310-1 and 310-2, in the same manner as described in the above embodiments. Then, electrodes or wirings 119, 120 are formed on the first insulating film (SiO 2 ) 130. In this case, polycrystalline silicon for embodiment is used as a material for the electrode or wiring 119, and tungsten silicide for embodiment is used as a material for the electrode or wiring 120. Subsequently, the second insulating film (SiO 2 ) 131 is deposited over the first insulating film (SiO 2 ) 130, and then via holes 410-1, 410-2 and 410-3 for forming a contact with the electrodes or wirings 119, 120 are formed in the second insulating film (SiO 2 ) 131. Subsequently, a conductive material for embodiment Ti (titanium) is deposited on the second insulating film (SiO 2 ) 131, and then processed to form a silicide thereof. As a result, TiSi 2 208 is formed on the electrodes or wirings 119, and TiSi x (x < 2) 209 is formed on the electrodes or wirings 120. Thereafter, a treatment is performed to expose only the silicide film 208 by making use of difference in thickness of these oxide films to be formed on the surfaces of silicide films 208 and 209, thereby allowing tungsten 122 for embodiment to be selectively deposited only in the via holes 410-1 and 410-2. Thereafter, a metallic multi-layered wiring 123 comprising for embodiment Ti/TiN/Al-Si-Cu is formed as a second electrode or wiring according to the ordinary process of manufacturing a semiconductor device. In this manner, tungsten can be selectively filled into a via hole by selecting the material for the underlayer of a through hole in the same manner as in the case of filling a contact hole. Accordingly, there is no distinction between the contact hole and via hole in the processing to be performed or effects to be obtained in exercising this invention. It should be noted that although polycrystalline silicon is selected as an underlayer of the via hole 410 to be filled with a conductive material, tungsten silicide is selected as an underlayer of the via hole 410 not to be filled with a conductive material, and titanium is selected as a conductive material to be deposited on the underlayer in the embodiment of FIG. 15, these materials can be replaced by other kinds of materials in the same manner as explained with the contact hole of the previous embodiments. In the embodiment shown in FIG. 16, polysilicon 119 and tungsten silicide 120 are respectively employed as a single layer for an electrode or wiring of the first layer. However, it is of course possible to employ a multi-layered electrode or wiring as already explained with reference to the embodiments of filling the contact holes. FIG. 17 illustrates such an embodiment. Since the sole difference between the embodiment shown in FIG. 16 and the embodiment shown in FIG. 17 is the structure of the first electrode or wiring layer, the detailed explanation of the structure of FIG. 17 is omitted. In this embodiment, polycrystalline silicon 119 is formed as the first electrode or wiring layer disposed below the via holes 410-1, 410-2 to be filled with tungsten 122, and a stacked layer comprising polycrystalline silicon 119 and tungsten silicide 120 is formed as the first electrode or wiring layer disposed below the via holes 410-3. FIG. 18 illustrates still another process, wherein a stacked layer comprising Al-Si-Cu-/TiN/Ti 121 and polycrystalline silicon 119 is deposited on the first insulating film 130, and, after performing the patterning of the stacked layer, interlaminar insulating film 131 is deposited. Subsequently, via holes 410-1, 410-2 and 410-3 are formed. In this case, the etching of the interlaminar insulating film 131 is terminated as the polysilicon 119 is exposed. Then, a region including via holes 410-1, 410-2 is covered with for embodiment a resist, and then polycrystalline silicon 119 which is disposed and exposed at the bottom of the via hole 410-3 is etched off. Subsequently, titanium is deposited and subjected to silicidation. Thereafter, tungsten is selectively grown thereon. By the way, there is another method wherein Al-Si-Cu-/TiN/Ti 121 is deposited, and then polycrystalline silicon 119 is deposited thereon. Subsequently, polycrystalline silicon 119 disposed below the via hole 410-3 not to be filled with tungsten is removed thus leaving only Al-Si-Cu-/TiN/Ti 121. Then, the interlaminar insulating film 131 is deposited, and the via hole 410-3 is again formed in the insulating film 131. This method is not illustrated in the processes described in relative to the contact hole (FIGS. 1 to 15). However, it would be apparent that this method is also applicable to the process of filling the contact hole. The gist of this invention resides in arbitrarily selecting which through hole should be or should not be filled with a conductive material by selecting the material of the underlayer of a through hole. Accordingly, in the technical viewpoint of this invention, there is no distinction between a contact hole and a via hole. Therefore, the expression of a via hole is used in the processes shown in FIGS. 16 to 18 merely for the convenience of explaining the invention. Accordingly, the three different methods employed for filling the via hole explained above can be also applicable to the processes of filling the contact hole.

Claims: A method of manufacturing a semiconductor device, comprising the steps of: forming on a semiconductor substrate (101) a first conductive region (103) consisting of a first conductive material and including silicon; forming on said semiconductor substrate (101) a second conductive region (106) consisting of a second conductive material; forming an insulating layer (109) covering said first and second conductive regions (103, 106); forming a first through hole (110-3) in said insulating layer (109) to bring into contact with said first conductive region (103); forming a second through hole (110-5) in said insulating layer (109) to bring into contact with said second conductive region (106); depositing a metal layer (111) on the whole surface of the semiconductor device; transforming the metal of said metal layer to a silicide on the bottom of the contact holes by heat treatment; removing unreacted metal by an etch process; performing an oxidation step, thereby forming silicon oxide in the first contact hole, and metal oxide in the second contact hole; removing the silicon oxide in the first contact hole, thereby exposing the silicide, while not removing the metal oxide in the second contact holes; and selectively growing metal on the silicide in the first contact hole, but not on the oxide in the second contact hole. The method according to claim 1, comprising the steps of forming said metal layer (111) deposited on the whole surface of said semiconductor device of a fourth conductive material; heat-treating said fourth conductive material of said metal layer (111) to transform said fourth conductive material into a first silicide layer (112) in said first through hole (110-3) and into a second silicide layer (113) in said second through hole (110-5); and removing said fourth conductive material of said layer (111) in regions outside said through holes (110-3, 110-5) where it has not been transformed into a silicide in the previous step. The method according to claim 2, further comprising the steps of oxidizing said first and second silicide layers (112, 113) in said first and second through holes (110-3, 110-5), respectively, so as to form a first oxide layer (114) in said first through hole (110-3) and a second oxide layer (115) in said second through hole (110-5); and removing said first oxide layer (114) in said first through hole (110-3). The method according to claim 3, wherein said first oxide layer (114) disposed on said first conductive material of said first conductive region (103) in said first through hole (110-3) is removed by etching under a condition where said oxide layer (115) including at least a metal oxide layer on said second conductive material of said second conductive region (106) in said second through hole (110-5) is left and only said first oxide layer (114) on said first conductive material can be etched off. The method according to claim 4, wherein said first oxide layer (114) in said first through hole (110-3) is removed under a condition wherein said first oxide layer (114) can be etched off in preference to said second oxide layer (115) by making use of a difference in thickness between said first oxide layer (114) in said first through hole (110-3) and said second oxide layer (115) in said second through hole (110-5). The method according to any of claims 3 to 5, wherein after growth of a film (116) of metal in said first through hole (110-3), said second oxide layer (115) in said second through hole (110-5) is removed. The method according to any of the preceding claims, comprising the steps of: forming said first conductive region (103) on a first portion of said semiconductor substrate (101) and said second conductive region (106) on a second portion of said semiconductor substrate, which second portion is different from said first portion where said first conductive region is formed; forming said insulating layer (109) on the whole surface of said semiconductor substrate; simultaneously forming a silicon oxide layer as said first oxide layer (114) on a bottom surface of said first through hole (110-3) where said first conductive material is exposed, and forming a second oxide layer (115) including at least a metal oxide layer on a bottom surface of said second through hole (110-5) where said second conductive material is exposed; removing said first oxide layer (114) disposed on said first conductive material by etching under a condition where said second oxide layer (115) including at least a metal oxide layer on said second conductive material is left, and only said first oxide layer (114) on said first conductive material can be etched off; depositing metal for forming said conductive film (116) on said first conductive material in said first through hole (110-3) by using a selective growth method; and removing said second oxide layer (115) including at least a metal oxide layer on said second conductive material in said second through hole (110-5). The method according to any of claims 1 to 7, wherein the step of forming a through-hole (110-3, 110-5) is performed by forming a contact hole in said insulating layer (109) disposed on said silicon substrate (101). The method according to any of claims 1 to 7, wherein the step of forming a through-hole (110-3, 110-5) is performed by forming a via hole in said insulating layer (109) disposed directly on said silicon substrate (101). The method according to any of the preceding claims, wherein said through-holes formed in said insulating layer (109) include at least one contact hole; and at least one of said contact holes is used as an alignment mark in a subsequent step of the manufacturing method. The method according to any of the preceding claims, wherein said first conductive material comprises a silicon film. The method according to claim 11, wherein said silicon film is made of monocrystalline silicon (103). The method according to claim 11, wherein said silicon film is made of polycrystalline silicon (119). The method according to claim 11, wherein said first conductive material comprises a stacked film including as an uppermost layer said silicon film. The method according to any of claims 1 to 10, wherein said first conductive material comprises a silicon-rich silicide film. The method according to claim 15, wherein said first conductive material comprises a stacked film including as an uppermost layer said silicon-rich silicide film. The method according to any of claims 1 to 16, wherein said second conductive material comprises a film of a metal selected from the group consisting of W, Mo, Ti, Al and Cu. The method according to any of claims 1 to 16, wherein said second conductive material comprises a silicide film of a metal selected from the group consisting of W, Mo, Ti, Al and Cu. The method according to any of claims 1 to 16, wherein said second conductive material comprises a stacked film including as an uppermost layer a silicide film of a metal selected from the group consisting of W, Mo, Ti, Al and Cu. The method according to any of claims 1 to 16, wherein said second conductive material is either silicon-poor silicide film or a metal film. The method according to any of claims 1 to 16, wherein said second conductive material comprises a stacked film including as an uppermost layer either a silicon-poor silicide film or a metal film, wherein said step of forming an oxide film comprises a step of exposing said semiconductor substrate (101) to an oxidizing atmoshere thereby forming said oxide layer. The method according to any of the preceding claims, wherein said third conductive material is a metal selected from the group consisting of W, Al, Si and Cu. The method according to any of claims 2 to 22, wherein said fourth conductive material is a high melting point metal selected from the group consisting of W, Mo, Ti, Al and Cu. The method according to any of the preceding claims, wherein said first bottom layer (112) is of TiSi 2 and said the material of said conductive film (116) grown on said first bottom layer (112) is of W.

Inventors: AOCHI HIDEAKI, OHSHIMA YOICHI, AOCHI, HIDEAKI, OHSHIMA, YOICHI, AOCHI, HIDEAKI, C/O INTELLECTUAL PROPERTY DIV., OHSHIMA, YOICHI, C/O INTELLECTUAL PROPERTY DIV.
Applicants: TOSHIBA KK, KABUSHIKI KAISHA TOSHIBA
Application year: 1994
Main classification: H01L21
IPC codes: H01L23, H01L21