Catalytic conversion of direct process high-boiling component to chlorosilane monomers in the presence of hydrogen chloride and hydrogen

Abstract: The present invention is a process for converting a high-boiling component, resulting from the reaction of an organochloride with silicon, into more commercially desirable monosilanes. The process comprises contacting the high- boiling component with hydrogen chloride and hydrogen gas at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from activated carbon, alumina, silica, zeolite, AlCl₃, AlCl₃ supported on a support selected from carbon, silica and alumina; platinum supported on a support selected from carbon, silica and alumina; and palladium supported on a support selected from carbon, silica and alumina.

Description: The present invention is a process for converting a high-boiling component, resulting from the reaction of organochloride with silicon, into more commercially desirable monosilanes. The process comprises contacting the high-boiling component with hydrogen chloride and hydrogen gas at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from activated carbon, alumina, silica, zeolite, AlCl 3 , AlCl 3 supported on a support selected from carbon, silica and alumina; platinum supported on a support selected from carbon, silica and alumina; and palladium supported on a support selected from carbon, silica and alumina. The high-boiling component useful in the present process results from the "Direct Process," where an organohalide is reacted with silicon in the presence of a suitable catalyst to form monosilanes. The Direct Process is described by US-A 2,380,995 and US-A 2,488,487. It is the main commercial process by which organohalosilanes (i.e. monosilanes), for example dimethyldichlorosilane and trimethylchlorosilane, are formed. These organohalosilanes are reactive compounds which can undergo numerous reactions to form a variety of useful silicon containing compounds and polymers. A major commercial use of organohalosilanes is in the production of polysiloxane polymers which are useful as heat transfer fluids, lubricants and the like and which can be further processed to form silicone elastomers, resins, sealants and adhesives. Operation of the Direct Process results not only in the production of the desirable monosilanes, but also in a high boiling component typically considered to be all materials with a boiling point higher than the particular diorganodihalosilane produced in the process. The high-boiling component is a complex mixture that includes compounds containing SiSi, SiOSi, SiCSi, SiCCSi and SiCCCSi linkages in the molecules. Typical compounds found in a high-boiling component are described in US-A 2,598,435 and US-A 2,681,355. The high-boiling component may also comprise silicon containing solids and soluble and insoluble compounds of copper, aluminum and zinc. In current commercial operations for performing the Direct Process, the high-boiling component can constitute as much as ten percent of the resultant product. Therefore, it is desirable to convert the high-boiling component into more commercially desirable products to both reduce low value by-products and to improve raw materials utilization. The prior art for converting the high boiling component of the Direct Process into more useable monosilanes is represented by US-A 2,598,435, US-A 2,681,355, US-A 2,709,176, US-A 3,639,105, US-A 4,059,608 and US-A 4,079,071. Takeda et al., Kogyo Kagaku Zasshi (Journal of Industrial Chemistry), Vol. 60, No. 11, p. 1392-1395 (1957), also describe the use of alumina, carbon and pumice as catalyst for the catalytic cracking of disilane in a hydrogen stream. The solution sought by the present process is to provide a high yield process for the conversion of a high-boiling component produced by the Direct Process to monosilanes. The present inventors have unexpectedly found that the solution is achieved by the catalytic conversion of the Direct Process high-boiling component to chlorosilane monomers in the presence of hydrogen chloride and hydrogen gas. This discovery is even more unexpected in view of the present inventors observation that, in the absence of a catalyst, the combination of hydrogen chloride and hydrogen gas will result in a very poor yield of chlorosilane monomers. The present invention comprises contacting a high-boiling component, resulting from the reaction of an organochloride with silicon and hydrogen chloride and hydrogen gas at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from activated carbon, alumina, silica, zeolite, AlCl 3 , AlCl 3 supported on a support selected from carbon, silica and alumina; platinum supported on a support selected from carbon, silica and alumina; and palladium supported on a support selected from carbon, silica and alumina. The present process may be run in any standard type reactor for contacting silanes with a catalyst. The process may be run as a batch process, semi-continuous or continuous process. The process can be run, for example, in a fixed-bed reactor, a stirred-bed reactor or a fluidized-bed reactor. Preferred is when the process is run as a continuous process in a fluidized-bed reactor. The present process is useful for converting a high-boiling component resulting from the reaction of an organochloride with silicon to form monosilanes. The term "high-boiling component" refers to those materials with a boiling point above that of the diorganodichlorosilane formed by the reaction of the organochloride with silicon. For example, when methyl chloride is reacted with silicon, the diorganodichlorosilane will be dimethyldichlorosilane and the high-boiling component will comprise those materials having a boiling point greater than that of dimethyldichlorosilane, i.e. greater than 70°C. In a typical process for reacting an organo-chloride with silicon, the reaction is conducted at a temperature of 270°C. to 350°C., in the presence of a suitable catalyst and gaseous products. Unreacted feed is continuously removed from the process. The removed gaseous products and unreacted feed are subsequently distilled to remove monosilanes leaving behind a high-boiling component. The high-boiling component is a complex mixture that includes compounds containing SiSi, SiOSi, SiCSi, SiCCSi and SiCCCSi linkages alone or in combination in each molecule. The high-boiling component can include silicon containing solids and soluble and insoluble compounds of copper, aluminum and zinc. The high-boiling component may contain, for example, organic substituted and non-organic substituted silanes, disilanes, trisilanes, disiloxanes, silane oligomers, siloxane oligomers, silalkylenes and silicon containing solids, all of which may be converted to monosilanes by our process. The present process is especially useful for converting polysilanes in the high-boiling component to monosilanes, where the polysilanes are described by formula R a H b Si n Cl 2n+2-a-b and where each R is a radical independently selected from alkyls comprising one to six carbon, n=2 to 20, a=0 to 2n+2, b=0 to 2n+2 and a+b=0 to 2n+2. The polysilanes useful in the claimed process can consist of n number of silicon atoms where n is an integer from two to 20. Preferred is when n equals two. The polysilanes can be substituted with a=0 to 2n+2 number of R radicals, where each R is independently selected from alkyls of one to six carbon atoms. The radical R can be methyl, ethyl, propyl and t-butyl. Preferred is when R is methyl. The polysilanes in the high-boiling component can contain b number of hydrogen atoms substituted on the silicon atoms, where b=0 to 2n+2. The polysilanes in the high-boiling component can also contain from zero to 2n+2 chlorine atoms. The high-boiling component can contain silalkylenes, where each silalkylene molecule can comprise one or more silalkylene bonds described by formula Si(C) z Si and z is an integer from one to six. Preferred is when z is an integer from one to three. The silalkylene molecules can comprise SiSi bonds and SiOSi bonds as well as the silalkylene bonds. The silicon atoms of the silalkylene molecules can be further substituted with the radical R, where R is as previously described, with chlorine and with hydrogen. Preferred is when the silicon atoms of the silalkylenes are substituted with methyl. The preferred high-boiling component is one resulting from the reaction of methyl chloride with silicon, the high boiling component having a boiling point greater than 70°C. This high-boiling component can contain Me 2 ClSiSiMe 2 Cl, Me 2 ClSiSiMeCl 2 , MeCl 2 SiSiMeCl 2 , Me 2 Cl SiSi(Me)(Cl)SiMeCl 2 , Me 2 ClSiCH 2 SiMe 2 Cl, Me 2 ClSiCH 2 SiMeCl 2 , MeCl 2 SiCH 2 SiMeCl 2 , Me 2 ClSi(CH 2 ) 2 SiMeCl 2 , Me 2 ClSi(CH 2 ) 3 SiMeCl 2 , Me 2 ClSiCH 2 Si(Me)(Cl)SiMeCl 2 , Me 2 ClSiCH 2 Si (Me)(Cl)CH 2 SiMeCl 2 and Me 2 ClSiOSiMeCl 2 , where Me is methyl, all of which may be converted to monosilanes by the present process. The high-boiling component is contacted with hydrogen chloride and hydrogen gas, where the ratio of the weight of high-boiling component to the weight of hydrogen chloride added to the reactor is within a range of 5:1 to 0.05:1. Preferred is where the ratio of the weight of high-boiling component to the weight of hydrogen chloride is within a range of 3:1 to 1:1. The high-boiling component is contacted with hydrogen chloride and hydrogen gas, where the ratio of the weight of high-boiling component added to the reactor to the weight of hydrogen gas added to the reactor is within a range of 0.1:1 to 1000:1. Preferred is where the ratio of the weight of high-boiling component to the weight of hydrogen gas is within a range of about 1:1 to 500:1. The process is conducted at a temperature within a range of 250°C. to 1000°C. A preferred temperature is within a range of 270°C. to 650°C. While pressure is not critical to the present process, it is preferred that the process be run at a gauge pressure within a range of 0.14 to 6.9 MPa (20 to 1000 psi). The process is conducted in the presence of a catalyst selected from activated carbon, alumina, silica, zeolite, AlCl 3 , AlCl 3 supported on a support selected from carbon, silica and alumina; platinum supported on a support selected from carbon, silica and alumina; and palladium supported on a support selected from carbon, silica and alumina. The physical form of the catalyst is not critical to the present invention and can be powder, particles, flakes, chips and pellets. A preferred catalyst is activated carbon. By "activated carbon" it is meant a microcrystalline, nongraphite form of carbon, having an internal porosity, the carbon having been activated by any standard process known in the art for producing activated carbon, for example, chemical activation or gas activation as described in Kirk-Othmer, Concise Encyclopedia of Chemical Technology, John Wiley & Sons publishers, 1985, p. 204 to 205. In general, it is preferred that the activated carbon have a diameter within a range of 0.001 mm to 20 mm. More preferred is when the activated carbon has a diameter within a range of 0.01 mm to 5 mm and a surface area greater than 1000 m 2 /g. The catalyst can be alumina, i.e. Al 2 O 3 . The size of the alumina is not critical to the present process and is generally determined by commercial availability and the ability to be handled. Generally, alumina with a particle size within a range of 0.001 mm to 10 mm is considered useful. The catalyst can be silica. The silica can be either precipitated silica or fumed silica. Generally silica with a particle size within a range of 0.001 to 10 mm is considered useful. The catalyst can be a zeolite. The zeolite catalyst can be of the natural occurring type chabazite, mordenite, erionite, faujasite and clinoptilolite. The zeolite catalyst can be a synthetic zeolite of the zeolite A, X, L or Y types or of the high silica synthetic zeolite types, such as ZSM-5 and ZSM-11. Preferred is when the zeolite catalyst is selected from synthetic zeolite catalysts consisting of LZ-Y-64, LZ-Y-74 and LZ-M-8. The weight of activated carbon, alumina, silica or zeolite catalyst added to the process in relation to the weight of high-boiling component, hydrogen chloride and hydrogen will depend upon such factors as the type of catalyst, chemical composition of the high-boiling component, process temperature, type of reactor employed, desired conversion and product selectivity. When the process is run as a batch process or a semi-continuous process a useful weight of catalyst is considered to be within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component, hydrogen chloride and hydrogen gas added to the process. The catalyst can be AlCl 3 . The concentration of AlCl 3 used in the process will depend upon such factors as discussed for the use of activated carbon. When the process is run as a batch or semi-continuous process, a useful concentration of AlCl 3 catalyst is within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component, the hydrogen chloride and the hydrogen added to the process. The AlCl 3 catalyst can be retained on a support selected from carbon, silica and alumina. The amount of AlCl 3 supported on the support can be from 0.1 to 30 weight percent AlCl 3 . Preferred is when the amount of AlCl 3 supported on the support is within a range of 0.5 to 5.0 weight percent AlCl 3 . The concentration of supported AlCl 3 used in the process will depend upon such factors as discussed for the use of activated carbon. If the process is run as a batch or semi-continuous process, a useful concentration of supported AlCl 3 catalyst is considered to be that which provides a concentration of AlCl 3 within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component, the hydrogen chloride and the hydrogen added to the process. The catalyst can be platinum supported on a support selected from carbon, silica and alumina or it can be palladium also supported by carbon, silica and alumina. The amount of platinum or palladium supported on the support can be from 0.1 to 10 weight percent. Preferred is when the amount of platinum or palladium is within a range of 0.5 to 2.0 weight percent. The concentration of supported platinum or supported palladium used in the process will depend upon such factors as discussed for the use of activated carbon. The optimum contact time for the high-boiling component, hydrogen and hydrogen chloride with the catalyst will depend, for example, on factors such as the type of catalyst, chemical composition of the high-boiling component and the degree of conversion and product selectivity desired. In general, a contact time within a range of one second to five hours is considered useful. Longer contact times may be employed, but appear to offer no advantage and may result in excessive scission of silicon-carbon bonds and silicon-hydrogen bonds present in the monosilanes. If desired, the monosilane containing product of the present process can be further separated by standard means, for example, distillation to separate the monosilanes from a high-boiling component and the high-boiling component can then be recycled to the process. The following examples are provided to facilitate understanding and to demonstrate the effectiveness of the present invention. Example 1 (Not within the scope of the present invention). A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the absence of catalyst. The reactor consisted of a 2.5 cm diameter by 50 cm length quartz tube maintained at 500°C. The high-boiling component comprised by weight, 55% methylchlorodisilane, 5% disilmethylenes, 35% other polysilanes and silalkylenes and 5% silicon containing solids. The high-boiling component was fed at a rate of 117 g/h to the reactor and hydrogen chloride was fed to the reactor at 50 g/h. The process was conducted for one hour with gaseous product exiting the reactor being collected in a cold condenser. The condensed product was analyzed by gas chromatography using a thermal conductivity detector (GC-TC). Chlorosilane monomers detected included HSiCl 3 , SiCl 4 , MeHSiCl 2 , Me 3 SiCl,MeSiCl 3 and Me 2 SiCl 2 . The condensed product also contained methylchlorodisilanes, disilmethylenes and other polysilanes and silalkylenes. The chlorosilane monomer yield of the process was calculated as the gram moles of monomer in the product divided by the gram moles of silicon fed to the process with the quotient multiplied by 100. The chlorosilane monomer yield for this Example was 48 percent. Example 2 (Not within the scope of the present invention) A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the presence of a packed bed of activated carbon catalyst. The process was conducted similar to that described in Example 1, with the high-boiling component composition, reactor design and reaction temperature being the same. The reactor was packed with 12 g of Calgon™ BPL 1 mm by 3.3 mm activated carbon pellets (Calgon, Pittsburgh, PA). The high-boiling component was fed to the reactor at a rate of 92 g/h and hydrogen chloride was fed to the reactor at a rate of 57 g/h. Gaseous product exiting the reactor was collected and analyzed as described in Example 1. The chlorosilane monomer yield was 79 percent. Example 3 (Not within the scope of the present invention) A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen gas in the presence of a packed bed of activated carbon catalyst. The process was conducted similar to that described in Example 1, with the high-boiling component composition, reactor design and reaction temperature being the same. The reactor was packed with 17 g of Calgon™ BPL 1 mm by 3.3 mm activated carbon pellets (Calgon, Pittsburgh, PA). The high-boiling component was fed to the reactor at a rate of 101 g/h and hydrogen gas was fed to the reactor at a rate of 3 g/h. Gaseous product exiting the reactor was collected and analyzed as described in Example 1. The chlorosilane monomer yield was 29 percent. Example 4 (Not within the scope of the present invention) A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride and hydrogen gas. The process was conducted similar to that described in Example 1, with the high-boiling component composition, reactor design and reaction temperature being the same. The high-boiling component was fed to the reactor at a rate of 94 g/h, hydrogen chloride was fed to the reactor at a rate of 60 g/h and hydrogen gas was fed to the reactor at a rate of 0.1 g/h. The process was conducted for one hour with gaseous product exiting the reactor being collected and analyzed as described in Example 1. The chlorosilane monomer yield was 21 percent. Example 5 A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride and hydrogen gas in the presence of a packed bed of activated carbon catalyst. The process was conducted similar to that described in Example 1, with the high-boiling component, reactor design and reaction temperature being the same. The reactor was packed with 16 g of Calgon™ BPL 1 mm by 3.3 mm activated carbon pellets (Calgon, Pittsburgh, PA). The high-boiling component was fed to the reactor at a rate of 66 g/h, hydrogen chloride was fed to the reactor at a rate of 61 g/h and hydrogen gas was fed to the reactor at a rate of 0.4 g/h. The process was conducted for one hour with gaseous product exiting the reactor being collected and then analyzed as described in Example 1. The chlorosilane monomer yield was 84 percent.

Claims: A process for converting a high-boiling component, resulting from the reaction of an organochloride with silicon, to monosilanes, the process comprising: contacting the high-boiling component with hydrogen chloride and hydrogen gas at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from activated carbon, alumina, silica, zeolite, AlCl 3 , AlCl 3 supported on a support selected from carbon, silica and alumina; platinum supported on a support selected from carbon, silica and alumina; and palladium supported on a support selected from carbon, silica and alumina. A process according to claim 1 where the high-boiling component, the hydrogen chloride and the hydrogen gas are contacted at a gauge pressure within a range of 0.14 to 6.9 MPa (20 to 1,000 psi). A process according to claim 1 where the ratio of the weight of high-boiling component added to the reactor to the weight of hydrogen chloride is within a range of 5:1 to 0.05:1. A process according to claim 1 where the ratio of the weight of high-boiling component added to the reactor to the weight of hydrogen added to the reactor is within a range of about 0.1:1 to 1000:1. A process according to claim 1 where the high-boiling component results from the reaction of methyl chloride with silicon and the high-boiling component comprises polysilanes, silalkylenes, silicon containing solids and soluble and insoluble compounds of copper, aluminum and zinc. A process according to claim 5 where the catalyst is activated carbon having a diameter within a range of about 0.01 mm to 5 mm and a surface area greater than about 1000 m 2 /g. A process according to claim 5 where the polysilanes are described by formula R a H b Si n Cl 2n+2-a-b , where each R is a radical independently selected from alkyls comprising one to six carbon atoms, n=2 to 20, a=0 to 2n+2, b=0 to 2n+2 and a+b=0 to 2n+2. A process according to claim 5 where the silalkylenes contain one or more silalkylene bonds and are described by formula Si(C) z Si and z=1, 2 or 3.

Inventors: CHADWICK KIRK MICHAEL, DHAUL AJAY KUMAR, HALM ROLAND LEE, JOHNSON RICHARD GORDON, CHADWICK, KIRK MICHAEL, DHAUL, AJAY KUMAR, HALM, ROLAND LEE, JOHNSON, RICHARD GORDON
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1994
Main classification: C07F7
IPC codes: B01J29, B01J23, C01B33, C07F7