Multilayer wrapping films

Abstract: A multilayer wrapping film comprising (A) two outermost layers each formed of an ethylene-α-olefin copolymer having an ethylene content of at least 50 mol%, (B) layers each comprising a propylene polymer and being disposed between the outermost layers (A), and (C) a layer comprising recycled resins, for example trimming losses, and of layers (A) and (B), disposed between the layers (B). One or more other layers may be interposed.

Description: The present invention relates to multilayer wrapping films having good hygienic properties, good transparency, good mechanical strength, low-temperature heat-sealing properties, good automatic wrapping aptitude, and excellent economical properties. Methods of film wrapping include various wrapping methods utilizing the characteristics of each film, such as sealing in the form of a bag, an overlapping method, a stretch wrapping method and a spin packing method. A single layer film using forms of a common resin, such as polyethylene, polypropylene or polyvinyl chloride, is generally employed as the film in these methods. However, with the increasingly demanding specification now required for wrapping film, the variety of wrapping film, and the change in social needs, the number of applications in which these known films cannot be employed has increased. For example, in one wrapping method food, such as fruit, fresh fish, fresh meat or vegetables is directly placed onto a plastic tray, and stretch wrapped with a film which, hitherto, has usually been formed of vinyl chloride resin. Recently, because of hygiene safety standards and the increasing consciousness of the earth's environment, films of an ethylene resin, such as a low-density polyethylene resin or an ethylene-vinyl acetate copolymer have been employed in place of the conventional polyvinyl chloride, as these pose fewer problems in respect of hygiene safety standards and environmental pollution. However, in the case of using, for example, a low-density polyethylene resin alone, it is impossible to simultaneously satisfy the self-adhesive property, the low-temperature heat sealing property, and the flexibility required of a film. When employing an ethylene-vinyl acetate copolymer resin film, by suitably selecting the content of vinyl acetate and the molecular weight of the copolymer, the problems associated with the use of low-density polyethylene resin film described above, could be solved to some extent, but if a corner of the supporting tray was sharp or food having a sharp projection was being packed, the problem occurred that the film became torn. The present inventors have previously proposed a multilayer wrapping film aimed at simultaneously providing the necessary properties by combining an ethylene polymer layer and a propylene copolymer layer, as described in the specifications of Japanese Patent Application Nos. 4-195210, 5-150366, 5-150367, 5-150368, and 4-195214. However, although in order to produce such a multilayer film economically and efficiently, it is effective to incorporate an additional layer, for example a recycled resin layer containing trimming losses, etc, formed during the production of the films, the film is whitened on heat-sealing the film according to how the recycled resin layer is incorporated. As a result of various investigations to overcome the problems described above, it has been found that a multilayer wrapping film satisfying all requirements can be obtained by employing a specific resin layer construction and specifying the disposition of the resin layers. Accordingly, an object of the present invention is to provide a multilayer wrapping film which can be produced economically and efficiently by utilizing recycled resins, has good hygienic safety properties, good transparency, and high mechanical strength, excellent low-temperature heat-sealing properties during automatic wrapping, and which is difficult to whiten during heat sealing. According to the present invention, there is provided a multilayer wrapping film comprising at least five resin layers as follows:- (A) two outermost layers each comprising an ethylene-α-olefin copolymer having a melt-flow rate of from 0.1g/10 minutes to 30g/10 minutes and having an ethylene content of at least 50 mol%; (B) two layers each comprising a propylene polymer having a melt-flow rate of from 0.5g/10 minutes to 20g/10 minutes and disposed between the outermost layers (A); and (C) a layer including recycled resin obtained from trimming losses, etc., formed during the production of the multilayer wrapping film, whereby layer (C) contains said ethylene-α-olefin copolymer forming layer (A) and said propylene copolymer forming layer (B); said layer (C) being disposed between layers (B). The present invention is described in detail below. The ethylene-α-olefin copolymer having an ethylene content of at least 50 mol% used as the layer (A) in the present invention is obtained by copolymerizing ethylene and an α-olefin having from 3 to 18 carbon atoms using a transition metal catalyst. The copolymerization reaction is usually conducted at a temperature of from 30°C to 300°C under a pressure of from atmospheric pressure to 3,000 kg/cm 2 in the presence or absence of a solvent in a vapor-solid phase, a liquid-solid phase, or a homogeneous liquid phase. As the transition metal catalyst, a titanium catalyst and a vanadium catalyst are preferred from the standpoints of the copolymerizability and the quality of the ethylene-α-olefin copolymer obtained. The ethylene-α-olefin copolymer has a melt flow rate of from 0.1 to 30 g/10 minutes, and preferably from 0.3 to 20 g/10 minutes. If the melt flow rate is lower than 0.1 g/10 minutes, the processability of the film becomes undesirably difficult and if the melt flow rate is over 30 g/10 minutes, the working stability of the film in the inflation processing, etc., undesirably deteriorates. The ethylene-α-olefin copolymer obtained by using a titanium catalyst, used in the present invention is a copolymer of ethylene and an α-olefin having from 4 to 10 carbon atoms, and the density thereof is from 0.870/cm 3 to 0.935 g/cm 3 , and preferably from 0.880 g/cm 3 to 0.920 g/cm 3 . If the density of the copolymer is lower than 0.870 g/cm 3 , the processability of such a copolymer becomes undesirably difficult and if the density is over 0.935 g/cm 3 , the transparency and the low-temperature heat sealing property are undesirably reduced. The ethylene-α-olefin copolymer obtained by using a vanadium catalyst, used in the present invention is a copolymer of ethylene and an α-olefin having from 3 to 10 carbon atoms and can be obtained by the method described in, e.g., JP-A-2-77410 (the term "JP-A" as used herein means an "unexamined published Japanese patent application"). That is, the copolymer is obtained by copolymerizing ethylene and an α-olefin having 3 to 10 carbon atoms in a hydrocarbon solvent using a catalyst system of (a) a vanadium compound represented by the formula, VO(OR) n X 3-n (wherein R represents a hydrocarbon group, X represents a halogen atom, and 0 < n < 3) as a transition metal component, (b) an organoaluminum compound represented by the formula, R' m AlX 3-m (wherein R' represents a hydrocarbon group, X represents a halogen atom, and 1 < m < 3) as an organometal component, and (c) an ester compound (hereinafter referred to as "M") represented by the formula R"(C=O)OR" (wherein R" represents an organic group having from 1 to 20 carbon atoms, which is partially or wholly substituted with halogen atoms, and R'' represents a hydrocarbon group having from 1 to 20 carbon atoms) as a third component, wherein the copolymerization is conducted under a catalystic condition that Al/V (molar ratio) is at least 2.5 and M/V (molar ratio) is at least 1.5, at a molar ratio of ethylene and the α-olefin of from 35/65 to 60/40, at a temperature of from 40°C to 80°C, and in the state of a hydrocarbon solvent-insoluble polymer (slurry portion) and a hydrocarbon solvent-soluble polymer (solution portion). The ethylene-α-olefin copolymer can also be obtained by copolymerizing ethylene and an α-olefin in the same manner as described above using a vanadium compound obtained by reacting vanadium trichloride and an alcohol as the transition metal component (a), as described in JP-A-60-226514. The ethylene-α-olefin copolymer obtained using the vanadium catalyst has a density of from 0.870 g/cm 3 to 0.915 g/cm 3 and preferably from 0.880 g/cm 3 to 0.910 g/cm 3 . If the density is lower than 0.870 g/cm 3 , the tackiness of the surface of the film becomes undesirably too strong and if the density is over 0.915 g/cm 3 , the low-temperature sealing property is undesirably reduced. Of the ethylene-α-olefin copolymers obtained using the vanadium catalyst, the copolymer having the features that the content of the α-olefin is from 2 to 20 mol%, the maximum fusion peak temperature by a differential scanning calorimeter (DSC) is in the range of from 60°C to less than 100°C, and the proportion of the fusion heat at that peak in the total heat of fusion is at least 0.8 is preferred. Examples of the propylene polymer for forming the layer (B) in the present invention are a propylene homopolyer, a propylene-ethylene copolymer having an ethylene content of 20 mol% or less, a propylene-butene-1 copolymer, a propylenebutene-1-ethylene copolymer having an ethylene content of 20 mol% or less, and a propylene-α-olefin copolymer containing an α-olefin having at least 5 carbon atoms alone or together with the above-described α-olefin. Of these copolymers, a propylene-ethylene copolymer having an ethylene content of from 3 to 12 mol% is preferred from the point of view of the balance between transparency and mechanical strength. The propylene polymer used in the present invention has a melt flow rate of from 0.5 g/10 minutes to 20 g/10 minutes, and preferably from 1.0 g/10 minutes to 10 g/10 minutes. If the melt flow rate thereof is lower than 0.5 g/10 minutes, the processability of the film becomes undesirably difficult and if the melt flow rate is over 20 g/10 minutes, the stability in the inflation film processing undesirably becomes poor. The recycled resins for forming the layer (C) used in the present invention are resins containing trimming losses, etc., formed during the production of the multilayer wrapping film of the present invention. Accordingly, the layer comprising the recycled resins contains the ethylene-α-olefin copolymer having an ethylene content of 50 mol% or more for forming the layer (A) and the propylene polymer for forming the layer (B), as the trimming losses, but may further contain other resin or resins. In the film construction in the present invention, the multilayer film comprising at least five layers has the characteristic that each of the outermost layers (A) which is the layer comprising the ethylene-α-olefin copolymer, the layers (B) comprising the propylene polymer, and the layer (C) comprising the recycled resins, are successively disposed towards the opposite side. Namely, the layers (B) are disposed between the outermost layers (A), and the layer (C) is disposed between the layers (B). The reason for disposing the layers (A) of the ethylene-α-olefin copolymer having the ethylene content of at least 50 mol% as both the outermost layers of the multilayer film in the present invention is that the multilayer film of the present invention is required to have a low-temperature heat-sealing property and a self-adhesive property. Further, the reason that the layers (B) comprising the propylene polymer are disposed on the outside of the layer (C) comprising the recycled resins, is mainly to prevent the occurrence of whitening on heat sealing. As a result of various investigations into the cause of the occurrence of whitening of the sealing portion on heat sealing, it has been found that the layer (C) comprising the recycled resins used in the present invention comprises the ethylene-α-olefin copolymer having an ethylene content of at least 50 mol% for forming the layers (A) and the propylene polymer for forming the layers (B), as the trimming losses thereof, etc, but since the ethylene-α-olefin copolymer is incompatible with the propylene polymer, they exist in a phase-separated structural state; and when relaxing during heat sealing the molecular orientation formed in the film processing step, the phase comprising the ethylene-α-olefin copolymer having the ethylene content of at least 50 mol% for forming the layer (A) is not uniformly relaxed with the phase comprising the propylene polymer for forming the layer (B), whereby unevenness is formed on the surface of the layer (C), which propagates to the surface of the multilayer film to cause whitening. Furthermore, it has been found that by disposing on each side of the layer (C) comprising the recycled resins, the layers (B) comprising the propylene polymer having a relatively high heat resistance, as compared with other layers, and thereby maintaining the rigidity of the multilayer film at the heat sealing temperature, the formation of the surface unevenness of the whole multilayer film occurring during heat sealing can be prevented. The practical embodiments of the layer structure of the multilayer film of the present invention are, for example, (A)/(B)/(C)/(B)/(A), (A)/(x-1)/(B)/(C)/(B)/(A), (A)/(B)/(X-2)/(c)/(B)/(A), (A)/(B)/(X-3)/(C)/(X-4)/(B)/(A), (A)/(B)/(X-5)/(C)/(X-6)/(B)/(X-7)/(A), etc., wherein X-1, X-2, ----, X-7 means a layer of an optional other polymer such as polyethylene or polypropylene. In the thickness construction of the multilayer film of the present invention, it is preferred from the point of the balance of various properties of the multilayer film that the thickness ratio of the layers (A) comprising the ethylene-α-olefin copolymer is from 20 to 50%, that of the layers (B) comprising the propylene polymer is from 20 to 50%, and that of the layer (C) comprising the recycled resins is from 20 to 60%. The total thickness of the multilayer film of the present invention is preferably from 6 to 40 µm. The resin or the resin composition of each layer constituting the multilayer film of the present invention can, if necessary, contains a resin-modifier such as polybutene, polyisobutylene, a petroleum resin, a polyethylene wax or atactic polypropylene. The resin or the resin composition can further contain additives such as a tackifier, an antioxidant, an antistatic agent, a lubricant, an antiblocking agent and an antifogging agent. For producing the multilayer film of the present invention, a method wherein after making films by an ordinary method such as an inflation method or a T-die method, the films are heat-laminated, or a method of forming the multilayer film by an inflation film molding machine or T-die film molding machine of the co-extrusion type of five layers of three different kinds or six layers of four different kinds can be used. Further, the multilayer film can be formed by laminating other films on either film formed by a conventional method such as extrusion lamination. For imparting a sufficient elasticity to the wrapping multilayer film of the present invention, it is preferred to stretch the film to at least one axial direction after forming the film. Stretching may be uniaxial stretching or biaxial stretching. In the case of uniaxial stretching, a conventional roll stretching method is preferred. In the case of biaxial stretching there may be employed a successive stretching method, wherein after stretching the film to one axial direction, the film is then stretched in another direction, or a method of simultaneously biaxially stretching the film by, for example, tubular stretching. The stretching ratio at stretching is preferably from 2 to 30 times, and more preferably from 3 to 25 times, as an area ratio. The present invention is explained in more detail by reference to the following Examples, but it should be understood that the invention is not construed as being limited thereto. The measurement methods of properties in the Examples and the Comparative Examples are explained below. (1) Density: Measured according to the method defined by JIS K6760. After annealing each material in water at 100°C for 1 hour, the density was measured. (2) Melt Flow Rate (MFR): MFR of the ethylene-α-olefin polymer for the layer (A) was measured according to the method defined by JIS K6760.MFR of the propylene polymer for the layer (B) was measured according to the method defined by JIS K6758. (3) α-Olefin content in the ethylene-α-olefin copolymer for the layer (A): The content was obtained from the material balance. In addition, the content of butene-1 was determined from the characteristic absorption thereof at 770 cm -1 using an infrared spectrophotometer and the result of the material balance was confirmed. (4) Ethylene content in the propylene polymer for the layer (B): The content was obtained from the material balance. Further, the ethylene content was determined from the characteristic absorptions of ethylene at 732 cm -1 and 720 cm -1 using an infrared spectrophotometer and the result of the material balance was confirmed. In addition, in the measurement by the infrared spectrophotometer, a calibration curve was prepared by the determined values by the radiation measurement of an ethylene copolymer labelled with 14 C. (5) Haze: Measured according to the method defined by ASTM D1003. As the value is smaller, the transparency is better. (6) Gloss: Measured according to the method defined by ASTM D523. As the value is larger, the gloss is better. (7) Tensile Strength: Measured according to the method defined by ASTM D882. (8) Shearing Tackiness: Two test pieces each having a width of 1 cm and a length of 3 cm were adhered each other by the tackiness of themselves and the largest load at pulling them to the shearing direction was measured. (9) Heat Sealing Property: Two films were superposed each other and heat-sealed using a heat sealer manufactured by Tester Sangyo K.K., under the conditions of 120°C, a sealing surface pressure of 1.0 kg/cm 2 , and a sealing time of 2.0 seconds with a sealing width of 10 mm. The sample was cut at a right angle to the sealed surface to obtain a test piece of 15 mm and the 180° peeling strength was measured at a rate of 200 mm/minute using a Schopper type tensile tester. (10) Sealable Temperature Width: A wrapping test was conducted using a tray stretch lapper STCIII-B manufactured by Ohmori Kikai K.K. under the following conditions and the interval between the lowest temperature at which a sufficient sealed strenth can be obtained and the temperature at which whitening or a hole opening began with melting at heat sealing at the bottom of the tray performed in automatic wrapping was defined as a sealable width. Film width: 300 mm Tray size: length 195 mm x width 110 mm x height 25 mm Weight of wrapping material: 500 g Wrapping speed: 50 packages/minute Chute belt speed: about 15 meters/minute EXAMPLE 1 A tubular coextruded laminate layer unstretched raw sheet composed of both the outermost layers (A) each composed of an ethylene-butene 1 copolymer having a density of 0.895 g/cm 3 , a melt flow rate of 2.0 g/10 minutes, and a butene 1 content of 13% by weight, produced using a vanadium catalyst, interlayers (B) composed of a propylene-ethylene copolymer having a melt flow rate of 3.0 g/10 minutes and an ethylene content of 4.6 % by weight each disposed between both the outermost layers, and a core layer (C) composed of recycled resins obtained as trimming losses disposed between the interlayers was obtained by an extruding machine (for the outermost layers) having a screw inside diameter of 65 mm, an extruding machine (for the interlayers) having a screw inside diameter of 50 mm, an extruding machine (for the core layer) having a screw inside diameter of 40 mm, and a co-extruding annular die of 5 layers having an inside diameter of 180 mm. The thickness of the laminate layer unstretched raw sheet obtained was about 120 µm, the thickness ratios of the layers were that both the outermost layers were 30%, the interlayers were 40%, and the core layer was 30%. Further, the tube width was 300 mm. The laminate layer unstretched raw sheet was stretched to 3.3 times in the lengthwise direction and to 3.1 times in the width direction by a tubular stretching and thereafter, heat fixing was conducted while giving a relaxation to some extent, thereby obtaining a laminate stretched film having a total thickness of about 12 µm. The various characteristic values of the film obtained are shown in Table 1 below. In addition, the occurrence of whitening at heat sealing was not observed. EXAMPLE 2 A laminate stretched film having a total thickness of about 12 µm was obtained by following the same procedure as in Example 1 except that an ethylene-butene 1 copolymer having a density of 0.905/cm 3 , a melt flow rate of 2.0 g/10 minutes, and a butene-1 content of 9% by weight obtained using a vanadium catalyst was used for the outermost layers (A) in place of the ethylene-butene 1 copolymer used in Example 1. The various characteristic values of the film obtained are shown in Table 1 below. In addition, the occurrence of whitening at heat sealing was not observed. EXAMPLE 3 A laminate stretched film having a total thickness of about 12 µm was obtained by following the same procedure as in Example 1 except that a resin composition composed of 95% by weight of an ethylene-hexene-1 copolymer [Sumikathene α (registered trade name) FZ102-0, made by Sumitomo Chemical Company, Limited, density 0.912 g/cm 3 and melt folow rate 0.8 g/10 minutes] produced using a titanium catalyst and 5% by weight of polyisobutylene was used for the outermost layers (A) in place of the ethylene-butene 1 copolymer used in Example 1. The various characteristic values of the film obtained are shown in Table 1 below. In addition, the occurrence of whitening at heat sealing was not observed. EXAMPLE 4 A laminate stretched film having a total thickness of about 12 µm was obtained by following the same procedure as in Example 1 except that the thickness ratios of the layers were changed to that the both the outermost layers (A) were 30%, the interlayers (B) were 30%, and the core layer (C) was 40%. The various characteristic values of the film obtained are shown in Table 1 below. In addition, the occurrence of whitening at heat sealing was not observed. COMPARATIVE EXAMPLE 1 A laminate layer stretched film having a total thickness of 12 µm was obtained by following the same procedure as in Example 1 except that the copolymer for the interlayers (B) was replaced with the recycled resins for the core layer in Example 1, that is, the recycled resins obtained as trimming losses were used for the interlayers and the propylene-ethylene copolymer having a melt flow rate of 3.0 g/10 minutes and an ethylene content of 4.6% by weight was used for the core layer. The various characteristic values of the film obtained are shown in Table 1. In addition, since the film was poor in the stretching stability, unstretched portions were formed and the occurrence of whitening at heat sealing was observed. COMPARATIVE EXAMPLE 2 A laminate layer stretched film having a total thickness of about 12 µm was obtained by following the same procedure as in Example 2 except that the copolymer for the interlayers (B) was replaced with the recycled resins for the core layer in Example 2, that is, the recycled resins obtained as the trimming losses were used as the interlayers and the propylene-ethylene copolymer having a melt flow rate of 3.0 g/10 minutes and an ethylene content of 4.6% by weight was used as the core layer. The various characteristic values of the film obtained are shown in Table 1 below. In addition, since the stretching stability of the film was poor in the stretching stability, unstretched portions were formed and the occurrence of whitening at heat sealing was observed. COMPARATIVE EXAMPLE 3 A laminate stretched film having a total thickness of about 12 µm was obtained by following the same procedure as in Example 3 except that the copolymer for the interlayers (B) was replaced with the recycled resins for the core layer in Example 3, that is, the recycled resins obtained as trimming losses were used as the interlayers and the propylene-ethylene copolymer having a melt flow rate of 3.0 g/10 minutes and an ethylene content of 4.6% by weight was used as the core layer. The characteristic values of the film obtained are shown in Table 1 below. In addition, since the film was poor in the stretching stability, unstretched portions were formed and the occurrence of whitening at heat sealing was observed. COMPARATIVE EXAMPLE 4 A laminate stretched film having a total thickness of about 12 µm was obtained by following the same procedure as in Example 1 except that the copolymer for the interlayers (B) was replaced with the recycled resins for the core layer in Example 1, that is, the recycled resins obtained as trimming losses were used as the interlayers and the propylene-ethylene copolymer having a melt flow rate of 3.0 g/10 minutes and the ethylene content of 4.6% by weight was used as the core layer, and further, the thickness ratios of the layers were changed such that the thickness ratio of both the outermost layers (A) was 30%, the thickness ratio of the interlayers was 30%, and the thickness ratio of the core layer was 40%. The characteristic values of the film obtained are shown in Table 1 below. In addition, since the film was poor in the stretching stability, unstretched portions were formed and the occurrence of whitening at heat sealing was observed. Haze (%) Glass (%) Tensile strength (kg/cm 2 ) Shearing tackiness (kg/cm 2 ) Heat sealing property (kgf) Sealable temperature width (°C) Example 1 0.4 145 950 1020 0.65 25 Example 2 0.5 143 1000 980 0.52 25 Example 3 0.5 145 1150 960 0.50 20 Example 4 0.4 144 920 1090 0.65 20 Comparative Example 1 0.9 133 900 950 0.63 10 Comparative Example 2 0.8 144 910 820 0.51 5 Comparative Example 3 0.8 143 920 860 0.50 0 Comparative Example 4 0.9 136 910 940 0.60 10 As described above, according to the present invention, a multilayer wrapping film, which has excellent hygiene safety properties, self-adhesive properties, low-temperature heat sealing properties, flexibility for automatic wrapping, and excellent transparency and mechanical strength, and which is difficult to whiten on heat sealing, can be provided economically and efficiently.

Claims: A multilayer wrapping film comprising at least five layers as follows:- (A) two outermost layers each comprising an ethylene-α-olefin copolymer having a melt-flow rate of from 0.1g/10 minutes to 30g/10 minutes and having an ethylene content of at least 50 mol%; (B) two layers each comprising a propylene polymer having a melt-flow rate of from 0.5g/10 minutes to 20g/10 minutes and disposed between the outermost layers (A); and (C) a layer including recycled resin obtained from trimming losses, etc., formed during the production of the multilayer wrapping film, whereby layer (C) contains said ethylene-α-olefin copolymer forming layer (A) and said propylene copolymer forming layer (B); said layer (C) being disposed between layers (B). A film as claimed in Claim 1, wherein said ethylene-α-olefin copolymer is a copolymer of ethylene and an α-olefin having from 4 to 10 carbon atoms. A film as claimed in Claim 2, wherein said ethylene-α-olefin copolymer is produced using a titanium catalyst and has a density of from 0.870 g/cm 3 to 0.935 g/cm 3 . A film as claimed in Claim 1, wherein said ethylene-α-olefin copolymer is a copolymer of ethylene and an α-olefin having from 3 to 10 carbon atoms. A film as claimed in Claim 4, wherein said ethylene-α-olefin copolymer is produced using a vanadium catalyst and has a density of from 0.870 g/cm 3 to 0.915 g/cm 3 . A film as claimed in Claim 1, wherein said polypropylene polymer is a propylene-ethylene copolymer having an ethylene content of less than 20 mol%. A film as claimed in any preceding claim, wherein the film has been subjected to a stretching treatment. A film as claimed in any preceding claim, wherein said wrapping is stretch wrapping.

Inventors: HAYASHIDA HARUO, ICHIGE AKIHIRO, KONDO KAZUO, OGAWA TADATOSHI, TADA TERUO, WANO TOYOKI, YAMADA TAKESHI, ZENIGAME MASAAKI, HAYASHIDA, HARUO, ICHIGE, AKIHIRO, KONDO, KAZUO, OGAWA, TADATOSHI, TADA, TERUO, WANO, TOYOKI, YAMADA, TAKESHI, ZENIGAME, MASAAKI
Applicants: OKURA INDUSTRIAL CO LTD, SUMITOMO CHEMICAL CO, OKURA INDUSTRIAL CO. LTD, SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1994
Main classification: B32B27
IPC codes: C08F10, B29L9, B32B27, B29C55, C08F210, C08F4, B65D75, B29K23