Semiconductor light emitting device and its manufacturing method

Abstract: In a light emitting device made of a group II-VI semiconductor, a P-type interface film (15) including one or two layers is formed between the positive electrode (12) and the uppermost P-type layer (7) of the group II-VI semiconductor film (2), to make the energy band increase in steps from the electrode (12) to the semiconductor film (2), thereby realizing a structure where the current flows at a low voltage. The II-VI semiconductor film (2) is MBE-grown at a substrate temperature of 350°C or below. The P-type interface film (15) is formed to have a carrier concentration of 10¹⁹/cm³ or above by MBE growth at a substrate temperature lower than or equal to the substrate temperature at which the semiconductor film (2) is formed.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a semiconductor light emitting device and its manufacturing method, said light emitting device being used as a semiconductor laser device, as a blue light emitter which is one of the elements of a display panel for use in displays of various electronic apparatuses, as a blue light emitting device (LED) used individually in a display apparatus, as a signal reading and writing light emitting device for use in a compact disk (CD) player, a laser disk (LD) player and a magnetic optical disk player, and as a light emitting device for use in a bar code reader. Description of the Prior Art Fig. 1 schematically shows the basic structure of a semiconductor laser device which is a kind of such a semiconductor light emitting device, and the condition of a corresponding energy band. The general structure of the semiconductor laser device is as follows: a semiconductor film B is formed on the surface of an N-type semiconductor substrate A by MBE (molecular beam epitaxy)-growing an N-type semiconductor layer B 1 , an active layer B 2 and a P-type semiconductor layer B 3 in this order, and light is emitted from the active layer B 2 by applying a bias voltage in a forward direction between a metal electrode E 1 formed on the reverse surface of the substrate A and a metal electrode E 2 formed on the obverse surface of the P-type semiconductor layer B 3 which is the top surface of the semiconductor film B, i.e. from the electrode E 2 to the electrode E 1 . As well known, the energy band of the semiconductor laser device of the above-described structure is of a configuration such that the energy levels of the N-type semiconductor layer B 1 and the P-type semiconductor layer B 3 are high and that an energy level trough is formed at the active layer B 2 which is a P-N junction. An energy barrier ΔV is generated between the electrodes E 1 and E 2 and the semiconductor film B. Therefore, when a voltage necessary to obtain a current I which causes holes h to go over the energy barrier ΔV is applied between the electrodes E 1 and E 2 , the carriers i.e. holes h and electrons injected by the voltage application are shut up in the active layer B 2 where the energy level is low, so that an induced emission occurs vigorously. When the exciting current exceeds a threshold value, light resonates between the parallel end surfaces of the active layer B 2 to cause a laser oscillation. Fig. 2 shows an example of a more specific structure of a conventional semiconductor laser device. The device shown in this figure is what is called a blue light emitting semiconductor layer of ZnSe in which an N-type GaAs substrate 21 is used as the N-type semiconductor substrate and a group II-VI semiconductor film 22 of ZnCdSSe or MgZnCdSSe is formed on the substrate 21 as the semiconductor film. The group II-VI semiconductor film 22 is formed by MBE-growing an N-type ZnSe layer 23 which is a buffer layer, an N-type ZnSSe layer 24 which is a clad layer, a ZnCdSe layer 25 which is an active layer, a P-type ZnSSe layer 26 which is a clad layer and a P-type ZnSe layer 27 which is a buffer layer in this order on the substrate 21. A metal such as Au is directly deposited onto the P-type ZnSe layer 27 which is the top layer of the group II-VI semiconductor film to form a positive electrode 28. Reference numeral 29 represents a negative electrode formed on the reverse surface of the substrate 21. In the semiconductor laser device of the above-described conventional structure, the metal electrode 28 is directly formed on the P-type ZnSe layer 27. However, it is known that when the P-type semiconductor of ZnSe is directly joined to a metal, a Schottky-type voltage/current characteristic exists therebetween. Specifically, in the conventional structure, as is shown in the energy band configuration of Fig. 3, when a bias voltage is applied in a forward direction between the electrodes 28 and 29, a steep Schottky-type energy barrier ΔV is generated between the metal electrode 28 and the P-type ZnSe layer 27 forming the outermost layer of the group II-VI semiconductor film 22. For this reason, a current which causes the holes h to go over the energy barrier ΔV cannot be obtained unless a considerably high voltage is applied. Therefore, in the conventional structure, since not only the power required to drive the device increases but also a current of several amperes flows in the device, the current density in the device is very high, so that it is inevitable for the device to generate heat while being driven. Thus, in the conventional device, in addition to the increase in power consumption, it is difficult to operate the device at ordinary temperature because of the possibility of thermal breakdown. To solve these problems, it is necessary for the device to have a structure where currents flow easily from the metal electrode 28 to the group II-VI semiconductor film 22 so that the bias voltage applied between the electrodes 28 and 29 may be as low as possible. To do so, for example, after the electrode 28 is formed, the group II-VI semiconductor film 22 may be maintained at a temperature higher than its growth temperature. Specifically, the MBE growth of the group II-VI semiconductor film 22 on the substrate 21 is performed normally at a substrate temperature of 350° or below. After the metal electrode 28 is deposited onto the group II-VI semiconductor film 22, the semiconductor film 22 is heated again to a temperature (e.g. approximately 400°C) higher than the growth temperature so that the metal constituting the electrode 28 is diffused into the group II-VI semiconductor film 22. Since the inclination of the energy barrier ΔV is gentler as shown by the broken line of Fig. 3 when the metal is diffused into the P-type ZnSe layer 27 which is the top layer of the group II-VI semiconductor film 22, the current flows more easily. However, the group II-VI semiconductor film 22 has the property of increasing in electric resistance when heated to a temperature higher than the growth temperature. For this reason, it is difficult under the present circumstances to perform the alloying by diffusing the electrode metal into the P-type ZnSe layer 27 while maintaining the electric resistance of the ZnSe layer 27 to be low. Therefore, to obtain the necessary current, a high voltage must be applied between the electrodes 28 and 29 like in the above-described conventional structure. Thus, the problems cannot be solved by this method. As another solution, a group II-VI semiconductor film 22 having a high carrier concentration of 10 19 /cm 3 or above may be grown on the substrate 21. According to this method, since the energy band of the P-type ZnSe layer 27 shifts to decrease the energy barrier as shown by the alternate long and short dash line of Fig. 3, a structure in which the current flows easily is realized. However, under the present circumstances, it is technically next to impossible to obtain a P-type group II-VI semiconductor film having such a high carrier concentration. JP-A-3 283 674 discloses a semiconductor light emitting device comprising a GaAs substrate, a semiconductor film including an N-type semiconductor layer, an active layer, and a P-type semiconductor layer which are formed in this order in lamination, said semiconductor film being formed so that the N-type semiconductor layer adjoins the GaAs substrate. This device further comprises a P-type interface film having an energy band gap smaller than the energy band gap of the P-type semiconductor layer and being formed on the P-type semiconductor layer of the semiconductor film and a positive electrode formed on the P-type interface film, wherein the P-type interface film includes a P-type AlGaAs film and a P-type GaAs film. JP-A-60 178 684 describes a semiconductor light emitting device of the same structure as JP-A-3 283 674, but with II-VI compound semiconductor films and an interface film comprising only a GaAs layer. SUMMARY OF THE INVENTION An object of the present invention is to improve the temperature characteristic of the whole semiconductor light emitting device by decreasing the power consumption and heat generation by improving the voltage/current characteristic between the P-type group II-VI semiconductor film and the electrode so that a necessary current flows at a low voltage. To achieve the above-mentioned object, in a semiconductor light emitting device where a semiconductor film including an N-type semiconductor layer, an active layer and a P-type semiconductor layer which are arranged in this order in lamination is formed on a GaAs substrate, the semiconductor film is made of a group II-VI semiconductor of ZnCdSSe or MgZnCdSSe, and a P-type interface film is formed between a positive electrode and the P-type semiconductor layer which is the top layer of the semiconductor film. The P-type interface film is of two layer structure including a P-type GaAs film and a P-type InGaAs film. Preferably, the P-type interface film has a carrier concentration of 10 19 /cm 3 or above. According to the structure described above, the gap of the energy band between the positive electrode and the semiconductor film is divided into three or two steps by the P-type interface film formed therebetween, and the Schottky-type energy barrier is reduced. As a result, the voltage necessary to obtain a current which causes the holes to go over the energy barrier between the positive electrode and the P-type layer which is the top layer of the semiconductor film is very low compared to the conventional structure. Further, since the P-type interface film has a high carrier concentration, the semiconductor film is capable of conducting a large quantity of current. The method of forming the semiconductor light emitting device of the present invention is as follows: First, the N-type semiconductor layer, the active layer and the P-type semiconductor layer are MBE-grown in this order to form the group II-VI semiconductor film of ZnCdSSe or MgZnCdSSe on the GaAs substrate while the temperature of the substrate is maintained at 350°C or below. Then, on the P-type semiconductor layer which is the top layer of the group II-VI semiconductor film, a P-type interface film is formed through MBE growth. At this time, the GaAs substrate is set at a temperature lower than or equal to the substrate temperature at which the group II-VI semiconductor film is formed. The P-type interface film having two layers of a P-type GaAs film and a P-type InGaAs film is formed, and the P-type GaAs film is formed first, and then, the P-type InGaAs film is formed thereon. According to the manufacturing method described above, since the P-type interface film is formed at a low temperature, the deterioration of the group II-VI semiconductor film is prevented. BRIEF DESCRIPTION OF THE DRAWINGS This and other objects and features of this invention will become clear from the following description, taken in conjunction with the preferred embodiments with reference to the accompanied drawings in which: Fig. 1 schematically shows the correspondence between a conventional structure and its energy band; Fig. 2 is a front cross-sectional view schematically showing the structure of a conventional semiconductor laser device; Fig. 3 is a characteristic diagram showing the energy band at the connection between a positive electrode and a semiconductor in the conventional semiconductor laser device; Fig. 4 is a front cross-sectional view schematically showing the structure of a background embodiment illustrating the present invention; Fig. 5 is a plan view schematically showing the structure of the embodiment of fig.4; Fig. 6 is a characteristic diagram showing the energy band at the connection between a positive electrode and a semiconductor in the embodiment of fig.4; Fig. 7 shows the voltage/current characteristics of the embodiment of fig.4 and the conventional device for comparison; Fig. 8 is a front cross-sectional view schematically showing the structure of a background embodiment illustrating the present invention; and Fig. 9 is a characteristic diagram showing the energy band at the connection between a positive electrode and a semiconductor in the second embodiment of fig. 8; Fig. 10 is a front cross-sectional view schematically showing the structure of an embodiment of the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments for explanation of the background of the present invention employed in a semiconductor laser device will be described with reference to the drawings (fig. 4-fig. 9). Fig. 4 schematically shows the structure of a first embodiment. The device shown in this figure is a blue light emitting semiconductor laser in which a group II-VI semiconductor film 2 of ZnCdSSe is formed on an N-type GaAs substrate 1. The group II-VI semiconductor film 2 is formed by MBE-growing an N-type ZnSe layer 3 which is a buffer layer, an N-type ZnSSe layer 4 which is a clad layer, a ZnCdSe layer 5, a P-type ZnSSe layer 6 which is a clad layer and a P-type ZnSe layer 7 which is a buffer layer in this order on the N-type GaAs substrate 1. The ZnCdSe layer 5 serving as the active layer is sandwiched at a P-N junction between an N-type semiconductor layer 8 including the N-type ZnSe layer 3 and the N-type ZnSSe layer 4, and the P-type semiconductor layer 9 including the P-type ZnSSe layer 6 and the P-type ZnSe layer 7. Between the group II-VI semiconductor film 2 and a positive electrode 12, a P-type interface film 15 including two P-type films is formed. Specifically, a P-type AlGaAs film 10 is formed on the P-type ZnSe layer 7 through MBE growth, and a P-type GaAs film 11 is formed on the P-type AlGaAs film 10 through MBE growth. A metal such as Au is deposited onto the P-type GaAs film 11 to form the positive electrode 12. Reference numeral 13 represents a negative electrode, which is formed by depositing a metal such as Au onto the reverse surface of the N-type GaAs substrate 1 like the positive electrode 12. In this embodiment, as shown in the plan view of Fig. 5, the positive electrode 12 and the P-type interface film 15 are formed to be of a belt shape having a constant width to prevent the current diffusion so that the current effectively contributes to the light emission. However, the configurations of the positive electrode 12 and the P-type interface film 15 are not limited to the belt shape. In this structure, when a bias voltage is applied in a forward direction between the positive and negative electrodes 12 and 13, i.e. from the positive electrode 12 to the negative electrode 13, the current flows from the positive electrode 12 to the group II-VI semiconductor film 2 by way of the P-type interface film 15 including the P-type GaAs film 11 and the P-type AlGaAs film 10. This current causes the holes to go over the energy barrier between the positive electrode 12 and the group II-VI semiconductor film 2 to flow from the P-type semiconductor layer 9 into the ZnCdSe layer 5 which is an active layer. The electrons flow from the N-type semiconductor layer 8 to the ZnCdSe layer 5. By the injection of the carriers, the recombination occurs of the electrons and holes which are shut up in the ZnCdSe layer 5 where the energy level is low, so that natural light is emitted from the ZnCdSe layer 5. When the exciting current exceeds a threshold value, the light emission of the ZnCdSe layer 5 is changed from the natural light emission to an induced emission, so that light resonates between the parallel end surfaces of the ZnCdSe layer 5 to cause a laser oscillation. Fig. 6 shows the condition of the energy band in this illustrative embodiment. As shown in the figure, the energy band gap of each layer compared to the positive electrode 12 increases in the following order: the P-type GaAs film 11 < the P-type AlGaAs film 10 < the P-type ZnSe layer 7 of the group II-VI semiconductor film 2. Therefore, the energy barrier between the positive electrode 12 and the P-type ZnSe layer 7 is divided into three steps. The potential differences are ΔV 1 between the positive electrode 12 and the P-type GaAs film 11, ΔV 2 between the P-type GaAs film 11 and the P-type AlGaAs film 10, and ΔV 3 between the P-type AlGaAs film 10 and the P-type ZnSe layer 7. The sum of the differences ΔV 1 to ΔV 3 is substantially equal to the potential difference ΔV between the electrodes 28 and the P-type ZnSe layer 27 of the conventional structure of Fig. 2. However, the quantity of current flowing through the P-N junction structure between the positive and negative electrodes 12 and 13 decreases exponentially with respect to the height of the energy barrier. Fig. 7 shows the voltage/current characteristics of this illustrative embodiment and a conventional structure. As is obvious from the figure, in this embodiment, even though the potential differences of the energy barriers are the same, the voltage necessary to obtain a current which causes the holes h to go over the energy barrier between the positive electrode 12 and the P-type ZnSe layer 7 is very low compared to the conventional structure. Subsequently, a method will be described of manufacturing a semiconductor laser device of the above-described structure. First, on the N-type GaAs substrate 1 which is set at a predetermined substrate temperature of 350°C or below, the N-type ZnSe layer 3, the N-type ZnSSe layer 4, the ZnCdSe layer 5, the P-type ZnSSe layer 6 and the P-type ZnSe layer 7 which constitute the group II-VI semiconductor film 2 of ZnCdSSe are formed through MBE growth in this order in lamination. Then, the P-type interface film 15 is formed on the group II-VI semiconductor film 2. In this case, the substrate temperature is set at a value (e.g. 300°C) less than or equal to the substrate temperature (i.e. 350°C) at which the group II-VI semiconductor film 2 is grown. Under this temperature, the P-type AlGaAs film 10 is MBE-grown on the P-type ZnSe layer 7. In this case, the carrier concentration of the P-type AlGaAs film 10 is 10 19 /cm 3 or above. Then, the P-type GaAs film 11 is MBE-grown on the P-type AlGaAs film 10. In this case, the film thickness of the P-type GaAs film 11 is less than or equal to a critical value, and the carrier concentration thereof is 10 19 /cm 3 or above like the P-type AlGaAs film 10. The substrate temperature is also set lower than or equal to the substrate temperature at which the group II-VI semiconductor film 2 is grown like at the time of the growth of the P-type AlGaAs film 10. By setting the growth temperature of the P-type AlGaAs film 10 and the P-type GaAs film 11 lower than or equal to the growth temperature of the group II-VI semiconductor film 2 of ZnCdSSe, the generation of a highly electrically resistant alloy layer due to the diffusion of the P-type AlGaAs film 10 and the P-type GaAs film 11 into the P-type ZnSe layer 7 is prevented, so that the deterioration of the P-type ZnSe layer 7 is prevented. In addition, by increasing the carrier concentration, the current flows more easily. After the P-type GaAs film 11 is formed on the P-type AlGaAs film 10, a metal such as Au is deposited onto the P-type GaAs film 11 to form the positive electrode 12. Then, unnecessary portions of the positive electrode 12, the P-type GaAs film 11 and the P-type AlGaAs film 10 are removed by a method such as etching to form the P-type AlGaAs film 10, the P-type GaAs film 11 and the positive electrode 12 in a belt shape as shown in Fig. 5. While the semiconductor film 2 is made of a group II-VI semiconductor of ZnCdSSe in this embodiment, the same workings and advantages are obtained when the semiconductor film 2 is made of a group II-VI semiconductor of MgZnCdSSe. Fig. 8 shows the structure of a second background embodiment. In this device, the P-type interface film 15 of the first background embodiment is replaced by a film including one layer. In Fig. 8, the same elements as those of the first embodiment are denoted by the same reference designations and no description thereof are given. In this structure, between the positive electrode 12 and the P-type ZnSe layer 7 which is the top layer of the group II-VI semiconductor film 2, a P-type GaAs film 14 is provided as the P-type interface film 15. While the positive electrode 12 and the P-type GaAs film 14 are formed to be of a belt shape to prevent the current diffusion like in the first embodiment, they may be of another shape. Fig. 9 shows the condition of the energy band in this structure. The energy gap of each layer compared to the positive electrode 12 increases in the following order: the P-type GaAs film 14 < the P-type ZnSe layer 7 of the group II-VI semiconductor film 2. Therefore, the energy barrier from the positive electrode to the P-type ZnSe layer 7 is divided into two steps. The potential differences are ΔV 1 between the positive electrode 12 and the P-type GaAs film 14 and ΔV 2 between the P-type GaAs film 14 and the P-type ZnSe layer 7. The sum of ΔV 1 and ΔV 2 is substantially equal to the potential difference ΔV between the positive electrode 28 and the P-type ZnSe layer 27 of the conventional structure shown in Fig. 2. With this structure, a voltage/current characteristic similar to that of the first embodiment shown in Fig. 1 is obtained. As a result, the voltage is much lower which is necessary to obtain a current which causes the holes h to go over the energy barrier between the positive electrode 12 and the P-type ZnSe layer 7. The semiconductor laser device according to this embodiment is manufactured in substantially the same method as the first embodiment. First, the group II-VI semiconductor film 2 is formed on the N-type GaAs substrate 1 by the method described previously. Then, at a substrate temperature lower than or equal to the substrate temperature at which the group II-VI semiconductor film is grown, the P-type GaAs film 14 is MBE-grown on the P-type ZnSe layer 7 as the P-type interface film 15. In this case, the carrier concentration of the P-type GaAs film 14 is 10 19 /cm 3 or above. Then, a metal such as Au is deposited onto the P-type GaAs film 14 to form the positive electrode 12, and unnecessary portions of the positive electrode 12 and the P-type GaAs film 14 are removed by a method such as etching. While the semiconductor film 2 is made of a group II-VI semiconductor of ZnCdSSe in this embodiment, the same workings and advantages are obtained when the semiconductor film 2 is made of a group II-VI semiconductor of MgZnCdSSe. Moreover, instead of the P-type GaAs film 14, a P-type InGaAs film may be formed in a similar manner to the P-type interface film 15. The embodiment of the present invention (shown in Fig. 10) would be described. The semiconductor laser device of this embodiment has a P-type interface film 15 including two P-type films like the semiconductor laser device of the first embodiment shown in Fig. 4, but the materials for the two P-type films 10 and 11 are different from those of the first background embodiment. Specifically, in this embodiment, the film 10 adjoining the Group II-VI semiconductor film 2 is made of P-type GaAs instead of P-type AlGaAs, and the film 11 adjoining the positive electrode 12 is made of PP-type GaAs. The other parts of the semiconductor laser device are the same as those of the first embodiment. In this semiconductor laser device, the energy band gap of each layer compared to the positive electrode 12 increases in the following order: the P-type InGaAs film 11 < the P-type GaAs film 10 < the P-type ZnSe layer 7 of the group II-VI semiconductor film 2, and the energy barrier between the positive electrode 12 and the P-type ZnSe layer 7 is divided into three steps like in the first embodiment shown in Fig. 6. Therefore, this device has voltage/current characteristics similar to those of the first embodiment shown in Fig. 7, and requires only a very low voltage to cause the holes h to go over the energy barrier between the positive electrode 12 and the P-type ZnSe layer 7. The semiconductor laser device of this embodiment is manufactured as follows. First, the group II-VI semiconductor film 2 is formed on the N-type GaAs substrate 1 in the same way as described above. Then, the P-type GaAs film 10 is MBE-grown on the group II-VI semiconductor film 2 so that the carrier concentration is 10 19 /cm 3 or above, while the substrate temperature is maintained lower than or equal to the temperature at which the group II-VI semiconductor film 2 is formed. Next, the P-type InGaAs film 11 is MBE-grown on the P-type GaAs film 10 so that the carrier concentration is 10 19 /cm 3 or above and that the film thickness is less than or equal to a critical value, while the substrate temperature is maintained lower than or equal to the temperature at which the group II-VI semiconductor film 2 is formed. Lastly, the belt-shaped positive electrode 12 is formed with a metal such as Au. As described above, according to the semiconductor light emitting device of the present invention, by forming the P-type interface layer 15 including one or two layers between the positive electrode 12 and the group II-VI semiconductor film 2 of ZnCdSSe or MgZnCdSSe MBE-grown on the GaAs substrate 1, the energy barrier between the positive electrode 12 and the semiconductor film 2 is divided into steps. With this arrangement, even though the potential differences of the energy barriers are the same, the voltage necessary to obtain a current which causes the holes h to go over the energy barrier between the positive electrode 12 and the P-type semiconductor layer 9 is very low compared to the conventional structure. As a result, the generation of heat is decreased and the temperature characteristic of the whole semiconductor light emitting device is improved. In addition, the deterioration speed of the device is restrained to prolong the life of the device. Moreover, the interface film, which can be formed to have a carrier concentration of 10 19 /cm 3 or above, is very useful to realize a structure where the current flows more easily, under the circumstances where it is impossible to obtain a P-type group II-VI semiconductor film having such a high carrier concentration. A semiconductor device having a larger current at a lower voltage can be produced through this feature as well as the improved voltage/current characteristic mentioned above. Further, since the group II-VI semiconductor film 2 is MBE-grown on the GaAs substrate 1 at a substrate temperature of 350°C or below, and the P-type interface film 15 is MBE-grown at a substrate temperature lower than or equal to the substrate temperature in the semiconductor film 2 formation, the generation of a highly electrically resistant alloy layer due to the diffusion of the P-type interface film 15 is prevented. As a result, the deterioration of the group II-VI semiconductor film is prevented. Obviously, many modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced other than as specifically described.

Claims: A semiconductor light emitting device comprising: a GaAs substrate (1); a group II-VI semiconductor film (2) including an N-type semiconductor layer (8), an active layer (5) and a P-type semiconductor layer (9) which are formed in this order in lamination, said semiconductor film (2) being formed so that the N-type semiconductor layer (8) adjoins the GaAs substrate (1); a P-type interface film (15) having an energy band gap smaller than an energy band gap of the P-type semiconductor layer (9), and being formed on the P-type semiconductor layer (9) of the group II-VI semiconductor film (2); and a positive electrode (12) formed on the P-type interface film (15), wherein said P-type interface film (15) includes a P-type GaAs film and a P-type InGaAs film which adjoins the positive electrode (12). A method of manufacturing a semiconductor light emitting device comprising the steps of: forming a group II-VI semiconductor film (2) including an N-type semiconductor layer (8), an active layer (5) and a P-type semiconductor layer (9) on a GaAs substrate (1) through molecular beam epitaxy growth at a substrate temperature of at most 350°C; forming, on the P-type semiconductor layer (9) of the group II-VI semiconductor film (2), a P-type interface film (15) having an energy band gap which is smaller than an energy band gap of the P-type semiconductor layer (9) through molecular beam epitaxy growth of a P-type GaAs film and a P-type InGaAs film in this order at a substrate temperature lower than or equal to the substrate temperature at which the group II-VI semiconductor film (2) is formed; and forming a positive electrode (12) on the P-type interface film (15).

Inventors: SHAKUDA YUKIO, SHAKUDA, YUKIO, SHAKUDA, YUKIO, C/O ROHM CO.LTD.
Applicants: ROHM CO LTD, ROHM CO., LTD.
Application year: 1994
Main classification: H01L33
IPC codes: H01S5, H01L33