SOLID PROTECTOR AGAINST UV, PROCESS FOR ITS PREPARATION AND USE THEREOF

Abstract: A less dusty, more stable and more easily handleable protector against UV light than previously is obtained by supplying it in the form of solid particles having a mean diameter of at minimum 10 mu m and containing, dispersed in 90-20 parts by weight of wax, 10-80 parts by weight of a pigment which reduces the penetration UV light and is made up of metal oxide particles of a mean primary particle diameter smaller than 0.150 mu m.

Description: Solid protector against UV, process for its preparation and us thereof The invention relates to a solid protector against UV light, comprising a pigment made up of metal oxide particles reducing the penetration of UV light and having an average primary par¬ ticle diameter smaller than 0.150 μm. Such solid protectors against UV light are used in the cosmetics industry. The inven tion also relates to the preparation and use of such a solid protector against UV light. The penetration of harmful ultraviolet radiation into the skin or other material is prevented according to state-of-the-art technology by using both organic and inorganic protectors against UV radiation. Inorganic UV-protectors include many ver fine-grained metal oxides. Corresponding metal oxides are in general also available in pigment grades, in which case they reflect or absorb mainly within the wavelength of visible light. Metal oxides protecting from UV radiation deviate from these pigments in that they are transparent to the wavelength of visible light but, instead, reflect or absorb ultraviolet light. They are called UV-pigments. The diameter of the primar particles of UV-pigments is clearly smaller than that of corre sponding pigment particles (for example, 0.1-fold), and the interface of their primary particles is considerably larger (for example 100-fold). UV-pigments are often also called "mic rocrystalline" pigments of "micropigments". Known inorganic UV-pigments include fine-grained titanium di¬ oxides. The diameter of their primary particles is in the orde of 0.020 μm (0.010-0.100 μm) , whereas the crystal size of pigment-grade titanium dioxide is in the order of 0.200 μm (0.160-0.250 μm) . UV titanium dioxide can be prepared, for ex¬ ample, by the method of publication EP-A-0 444 798 (Kemira Oy) , by methods referred to therein, or by other methods. UV tita- niu dioxide is available in anatase or rutile form or in amor phous form, and its particle shape is round, oblong or needle¬ like. UV titanium dioxide is available both coated and un- coated, the coatings being either hydrophilic or hydrophobic. Zinc oxide as a UV-pigment is known from the publication GB 21 84 356 (Kao Corporation) . Other known UV-pigments include oxides of cerium, zirconium and iron, having particle sizes below 0.150 μm and absorbing UV light. There are also known photochromatic UV-pigments in which the ability to protect against light increases under the effect of UV radiation (EP 526712, Kao Corporation). Though UV-pigments, when dry, are at least partly agglomerated their particle size is, nevertheless, so small that the prod¬ ucts are highly dust-producing, from which there follow many drawbacks. The working of such a very fine-grained UV-pigment into a well dispersed suspension is often difficult. The dust problem has been solved in patent publication GB 22 06 339 (Tioxide Group PLC) with respect to UV titanium di¬ oxide by grinding it in an oil phase with the help of an or¬ ganic dispersing agent in a bead mill. A corresponding method for UV-zinc oxide is known from patent publication EP-A 1- 535 972 (Tioxide Specialties Ltd.). However, the products thus obtained still have deficiencies, o which we mention limited storage stability, need for dispensin devices and for transportation and storage containers, need to mix the stored product or product container, such as a barrel, before dispensing, as well as difficulty of cleaning the said equipment and need to treat the waste slurry produced in their washing. In general it is also necessary to add preservatives to suspension-form UV-pigment dispersions in order to combat microbial growth, even if it would be desirable to have the product keep entirely without preservatives, or at least with substantially smaller preservative doses. Solid or semi-solid color pellets intended for cosmetics prod¬ ucts are known from patent publication PCT 93/00065 (Boots). This invention makes it possible to select a lipstick color from a large number of lipstick color shade alternatives by mixing equal-sized color pellets with an oil mixture, in a numerical quantity ratio indicated by a certain formula, and then by preparing lipsticks from these. The pellets contain a wax component 1-50 %, an oil or fat component 30-65 %, and pigment or mother-of-pearl 10-35 %. The pigments are color pigments conventionally used in lipsticks, such as iron oxide, titanium dioxide, substrate colors, ultramarines, and organic colors. The use of UV-pigment is not specifically mentioned; i is stated that, in addition to gloss control agents, skin-calm ing agents, skin-care agents, vitamins, preservatives and anti oxidants, the products may also contain sun-protectors. The object of the present invention is to eliminate the prob¬ lems of dust and stability mentioned above by providing a dust free and stabile solid protector against UV light, less sus¬ ceptible to microbes, the protector being based on the said metal oxide particles less than 0.150 μm in size and being mainly characterized in what is stated in the characterizing clause of Claim 1. It has thus been realized, that a dust-free and stable UV-protector is obtained if it is in the form of solid particles, having a minimum diameter of 10 μm and con¬ taining the said pigment reducing the penetration of UV light, dispersed in 90-20 parts by weight of wax. The pigment reducing the penetration of UV light used in the solid UV-protector according to the invention may be any pig¬ ment reducing the penetration of UV light, the pigment being made up of metal oxide particles having a mean primary particl diameter smaller than 0.150 μm. Typical usable metal oxide particles include the oxides of titanium, cerium, zirconium. iron, and zinc. The crystal form of the oxides may vary great ly, but all of these metal oxides are characterized in that t mean diameter of their primary particles is smaller than 0.150 μm. A preferred mean diameter of the primary particles 0.010-0.100 μm, and the most preferred in the order of approx. 0.020 μm. It is also possible to use photochromatic UV-pigmen in which the ability to protect against light increases under the effect of UV radiation. Such pigments have been disclosed, for example, in publication EP 526 712, which publication is appended hereto as a reference. As was pointed out above, the UV-protector according to the invention is obtained by dispersing 10-80 parts by weight of a pigment reducing the penetration of UV light into 90-20 parts by weight of wax. By parts by weight is meant in this context the weight ratio between the pigment reducing the penetration of UV light and wax, in which case there may be present any amount of other components, as long as the formed UV-protector will remain solid and in particle form. By the words "disperse and "dispersion" is meant the maximally fine distribution of a least one substance, in this case a pigment reducing the pene¬ tration of UV light, into another, continuous phase, i.e. in this case wax. By maximally fine distribution is in this case also meant an even distribution into the continuous phase, i.e wax. Preferably the proportion of the pigment which reduces the penetration of UV light is at minimum 36 % by weight, more preferably at minimum approx. 40 % by weight, and most prefer¬ ably at minimum approx. 44 % by weight, of the whole UV-protec tor. The UV-protector preferably contains the said pigment which reduces the penetration of UV light in an amount of at maximum 85 % by weight, more preferably at maximum 80 % by weight, and most preferably at maximum 75 % by weight. As was pointed out, the solid UV-protector according to the invention is in the form of solid particles having a mean di¬ ameter of at minimum 10 μm. In this manner there is obtained a dust-free, stable and easily handled material, which can easil be added to various products in which it is used, such as cos¬ metic products. Preferably the UV-protector according to the invention is in the form of solid particles having a mean di¬ ameter of 30-5000 μm, preferably approx. 50-3000 μm. In this context it is important to note that the solid UV-protector according to the present invention differs from, for example, a solid UV-protector coated with wax or some other substance in that it is in the form of solid particles so large that the particle material is made up, dispersed in wax, of a pigment reducing the penetration of UV light. The solid UV-protector according to the invention is thus made up of a wax with a pigment reducing the penetration of UV light dispersed in it. Wax is the common name of substances which are waxy in their physical properties. By wax is in general meant a naturally and/or synthetically produced substance the proper¬ ties of which at 20 °C range from solid but moldable to brittle and hard, from coarse to fine-grained, from transparent to opaque, but it is not glass-like. It melts without decomposing at a temperature above 40 °C, having a relatively low viscosity even at a point somewhat above the melting or congealing point. Its solidity and solubility are often strongly dependent on the temperature. Waxes differ from other solid natural and synthetic products mainly in that they usually melt and obtain low viscosity even within a temperature range of 50-90 °C, exceptionally up to a temperature of 200 °C. They usually burn evenly and give sur¬ faces treated with them a durable sheen. According to one embodiment of the invention, the wax is at room temperature a solid, waxy substance which becomes fluid at 40 °C minimum, preferably at 50 °C minimum, and most preferably at 55 °C minimum. On the other hand, according to one embodi¬ ment the wax is at room temperature a solid, waxy substance which becomes fluid at 200 °C maximum, preferably at 150 °C maximum, most preferably at 100 °C maximum. If the wax com¬ ponent according to the invention, or a dispersion thereof an a pigment reducing the penetration of UV light, melts at a te perature below 40 °C, it is necessary to use with that wax other waxes or waxy components by means of which the melting temperature in the mixture dispersion can be raised to above 40 °C, preferably above 50 °C, and most preferably above 55 ° Waxes can be classified into natural waxes, which also include waxes of mineral origin, and synthetic waxes, which also in¬ clude chemically modified natural waxes. Usable waxes according to the invention include those presente in the CRC Handbook of Chemistry and Physics, The Chemical Ru ber Company, 53rd Ed. 1972-3, page C-753. This work is appende hereto as a reference. Suitable vegetable waxes include car- nauba, candelilla, Japan wax and jojoba wax; animal waxes in¬ clude beeswax, spermaceti wax, and lanolin wax; and mineral waxes include paraffin wax, ceresin wax, ozocerite, montan wa and microcrystalline waxes. Synthetic waxes according to the invention include unsaponifi- able waxes prepared from natural ester waxes by decarboxyla- tion, synthetically prepared hydrocarbon waxes such as polyeth ylene waxes and/or propylene waxes and polyethylene and poly¬ propylene waxes modified by oxidation or by copolymerization with polar monomers, emulsifiable ester waxes formed from long chain fatty alcohols and long-chain carboxylic acids, hydrogen ated waxes obtained by hydrogenating drying oils such as casto oil, polyethylene oxide wax, polyethylene oxide/propylene oxid wax, phthalic imide wax and other waxy synthetic polymers, waxes made from saturated fatty acids by amide or imide conden sation, and silicon waxes. The waxes according to the invention also include waxy C- j ^-C^ chain solid fatty acids, di- and polycarboxylic acids and cor¬ responding alcohols, e.g. lauric, myristinic, palmitic, stear- ic, hydroxystearic, arachinic, behenic and erucic acids. Especially preferred natural waxes are carnauba wax, candelill wax, jojoba wax, hydrogenated jojoba wax and Japan wax, bees¬ wax, and/or lanolin. A preferred mineral or synthetic wax is paraffin wax. Other preferred waxes include cetyl palmitate, arachidyl behenate, behenyl erocant, pentaerythritol tetra- stearate, glycol distearate, and cetostearyl stearate. The wax used in a solid UV-protector according to the inventio may also be a waxy surfactant, which include non-ionic waxy surfactants such as the reaction products of fatty alcohols having 10-22 carbon atoms in their alkyl chain, such as layryl, cetyl and stearyl alcohols, with ethylene oxide (1-50 ethylene oxide units/alcohol), the fatty acid esters of ethoxylated fatty alcohols, ethoxylated glycerides such as ethoxylated glyceryl monostearate, ethoxylated sterols and the like such as ethoxylated cholesterol, and ethoxylated lanolin and its deriv¬ atives. Other waxes include anionic waxy surfactants such as the salts of long-chain fatty acids and long-chain dicarboxylic acids, long-chain alkyl sulfates; polyethoxylated anionic sur¬ factants such as polyethoxylated alcohol sulfates, sodium coco- yl cetionate, polyethoxylated phosphoric acid esters; N-acyl sarcosinates; polyethoxylated phosphate esters; taurates; salts of fatty acid esters and hydroxycarboxylic acid esters, such as Na and Ca stearoyl lactylates. Further waxes include cationic, amphoteric or zwitterionic wax surfactants and waxy salts formed by anionic and cationic com¬ ponents with each other. These include waxy phospholipids such as lecithin and its derivatives, imidazoline and betaine deri¬ vatives, alkyl amines, and alkyl ammonium compounds, polyethox¬ ylated amines, and pyridinium salts. Waxes used in a solid UV-protector according to the invention also include salts formed by anionic and cationic surfactants and polymers with each other, used either without other waxy components or in mixtures with other waxy components. By means of such "ancat" compounds it is possible to affect the struc¬ ture of the wax and of the products formulated from it and their adherence to a base, such as skin in the case of cosmeti products. Such waxes can be prepared in different ways. The following method is especially suitable for the preparatio of salts of anionic and cationic surfactants and polymers in the form of an inorganic salt. In the method, the anionic and cationic components are dissolved separately in water, where¬ after the solutions are combined. The formed "ancat" salt is separated from the aqueous solution by a suitable procedure, for example by filtering or washing with water clean of the initial components, or preferably by extracting in an organic solvent, whereupon the inorganic counter-ions of the initial components remain in the aqueous solution. The organic solvent can be removed, for example, by distillation. In another method for the preparation of "ancat" waxes, the anionic component and the cationic component are dissolved separately in a suitable solvent. The solutions are combined and the precipitated "ancat" product is separated, for example by filtration. Combination waxes of a basic wax component and an acid wax component may also be used. The components are either melted together, or they are melted separately into another molten wa component, such as a melt of paraffin wax or a surfactant, and are then combined. According to one embodiment of the invention, the solid UV-pro tector contains wax at minimum 15 % by weight, preferably at minimum 20 % by weight, and most preferably at minimum 30 % by weight. According to one embodiment, the solid UV-protector according to the invention contains wax at maximum 90 % by weight, preferably at maximum 75 % by weight, and most prefer¬ ably at maximum 63 % by weight. The dispersing of the UV-pigment into the melt of a waxy sub¬ stance according to the invention may preferably take place without specific dispersing agents, if the UV-pigment is coate with a coating agent especially well suited for the medium used. In order to obtain a maximally homogenous dispersion it is often preferable to use a suitable dispersing agent. Its type depends on the properties of the wax used as the medium, for example its polarity. When non-polar or only slightly pola waxes were used as the medium, surprisingly good results were obtained with W/O type emulsifiers. By means of these it prove to be possible to disperse into wax both UV-pigments which had been pretreated to make them hydrophobic and those pretreated to make them hydrophilic, both together and separately. This surprising observation is perhaps explained in part by the fac that it is not necessary to require a molten dispersion to hav as long stability periods in molten state as are required of a dispersion made in a liquid phase, such as an oil or aqueous phase. It is preferable to freeze a molten dispersion and to granulate it, without a long storage period, and thus the dis¬ persion is obtained rapidly in a solid, storage-stabile form. Examples of usable emulsifiers include the esters of alcohol o a polyhydroxide compound with fatty acids, e.g. fatty acids which contain 8-22 C atoms and preferably at minimum 12 C atom in their alkyl chain, such as solid or waxy esters of lauric, cetanic, and stearic acids with ethylene glycol, polyethylene glycol, glycerol, polyglycerol, sorbitol, sucrose, penta- erythritol, and other polyols. Preferred emulsifiers include the mono- and diglycerides of such fatty acids, the sorbitol esters of the fatty acids and their ethoxylates, diacetylated fatty acid monoglyceride tartrates, fatty acid lactylates, fatty acid polyglycerol esters, fatty acid propylene glycol esters, fatty acid sucrose esters, and the acetic acid, lactic acid, citric acid and tartaric acid esters of fatty acid mono- glycerides. Especially preferred dispersing agents include the monoglycerides of fatty acids containing at minimum 18 C atoms and their acetic acid, lactic acid, citric acid and tartaric acid esters. Such emulsifiers are in general non-hazardous to the environment. They are usually of food grade, but are, nevertheless, not especially vulnerable to microbial action. Usable dispersing agents include A-B-A block polymers, B stand ing for a functional group or polymer capable of being adsorbe to the pigment surface and A for a polymer chain well soluble in the medium, or dispersing agents of the "comb polymer" type, which have secondary chains well soluble in the medium and affixed to a polymer chain capable of being adsorbed to the pigment surface. A chain soluble in molten hydrophobic wax may in this case consist of, for example, polyhydroxycarboxylic acid or polymetacrylate and the chain adsorbing to the pigment surface may consist of polyethylene oxide or polyacrylate or a polyacrylate-rich copolymer. A suitable amount of dispersing agent, in case the pigment is not sufficiently well dispersible into the wax used without a dispersing agent, is approx. 0.5 % by weight, preferably at minimum approx. 2 % by weight, of the amount of the UV-pigment. At the upper limit of the dispersing agent amount the medium consists entirely of a waxy emulsifier and/or dispersing agent, in which case the solid dispersion is made up of 10-80 parts b weight UV of pigment in 90-20 parts by weight of waxy emulsi¬ fier or dispersing agent. In one preferred embodiment of the invention the weight ratio of the wax to the waxy emulsifier and/or dispersing agent in solid UV-pigment dispersions is approx. 50:1-1:1, preferably approx . 10 : 1- 2 : 1 . According to one further embodiment of the invention, the waxy emulsifier and/or dispersing agent is made up of hydrophilic waxy surfactants which yield a solid UV-pigment dispersion. These include polyethoxylated nonionic surfactants, such as th waxy reaction products of fatty alcohols having 8-22 C atoms i their alkyl chain, such as lauryl, cetyl and stearyl alcohols, with ethylene oxide; the fatty acid esters of polyethoxylated fatty alcohols; polyethoxylated glycerides, such as polyethox¬ ylated glyceryl monostearate; polyethoxylated alcohol and poly alcohol esters such as polyethoxylated propyleneglycol mono¬ stearate, polyethoxylated glyceryl monostearate, polyethoxyl¬ ated fatty acid esters of sorbitan; polyethoxylated sterols an corresponding compounds, such as polyethoxylated cholesterol and polyethoxylated lanolin and their derivatives; solid block polymers of polyethylene oxide and polypropylene oxide and solid polypropylene oxide/polyethylene oxide derivatives of ethylene diamine, octyl or nonylphenyl polyethoxylates, taurates. When a hydrophilic emulsifier and/or dispersing agent is used, a preferred weight ratio of wax to emulsifier is approx. 0:1- 1:1. The solid protector against UV according to the invention may, in addition to a pigment reducing the penetration of UV light, wax, and possible dispersing agent, also contain additives. Such additives include color and mother-of-pearl pigments, melanin, radical scavenger compounds and vitamins, used either as admixtures or as powdering auxiliaries. It is also possible to add small amounts of oil or oily cosmetic auxiliary agents, as long as the lowering of the melting point caused by them is corrected by means of formulation. The lowering of the melting point of a solid UV-protector ac- cording to the invention can be inhibited by mixing in a wax which raises the melting point, such as a microcrystalline wa or, if the protector contains oil, a wax which binds oil well such as ozocerite, or a component which reinforces the struc¬ ture, for example an "ancat" compound such as mentioned above or a long-chain alcohol. According to one preferred embodiment of the invention, the solid protector against UV is a cosmetic, or it is used by precipitating it as part of a cosmetic, in which case the pig ment transparent to UV and the wax are cosmetically acceptabl substances. One important viewpoint in the invention is that new, easily handled products can be used for satisfying the world's increasing need for cosmetic protectors against UV light. According to one preferred embodiment, the UV-protecto according to the invention, which is at the same time a cos¬ metic substance or a component of a cosmetic substance, con¬ tains at least one of the following cosmetic auxiliaries: a cosmetically acceptable organic protector against UV, a cos¬ metically acceptable preservative, a cosmetically acceptable antioxidant, and a cosmetically acceptable perfume. Typical protectors against UV include organic UV-protectors such as 4 aminobenzoic acid, NNN-trimethyl-4-(2-oxoborn-3-yldene-methyl anilinemethyl sulfate, homosalate, oxybenzone, 2-phenyl- benzimidazole-5-sulfonic acid and its potassium, sodium and trimethanolamine salts, 3,3'-(l,4-phenylenedimethγdyn)bis(7,7 dimethyl-2-oxobicyclo)2,2,l(heptane-l-methanesulfonic acid) a salts, and l-(4-tert.butylphenyl)-3-(4-methoxyphenyl) propane 1,3-dione. When the components of a solid protector against U according to the invention are used, it should be borne in mi that they must be non-irritating and non-toxic and that they must fulfil the requirements set on cosmetic products in the legislation regarding cosmetic products. Methyl-butene parabe is an example of cosmetic preservatives to be mentioned. Buty ated hydroxyanisol is an example of cosmetic antioxidants to •mentioned. The invention also relates to a process for the preparation of any of the solid UV-protectors described above. An easily han¬ dled and practical solid protector against UV is obtained: a) by dispersing into 90-20 parts by weight of molten wax 10-8 parts by weight of a pigment which reduces the penetration of UV light and consists of metal oxide particles having a mean primary particle diameter smaller than 0.150 μm, and b) by converting the molten or solid dispersion obtained from step a) into the form of solid particles having a mean diamete of at minimum 10 μm. The ingredients usable in the process according to the invention were discussed above in connection with the description of the protector against UV. In the invention, the above-mentioned problems associated with UV-pigments are thus eliminated by formulating a solid protec¬ tor against UV in the form of solid particles by first dispers ing, and possibly grinding, a fine-grained UV-pigment at an elevated temperature into waxes which are liquid at that tem¬ perature but solid at room temperature, and by then cooling an granulating the obtained dispersion. In the preparation it is, of course, possible to use the kneading technique, in which case the raising of the temperature is not necessary, as long as sufficient mixing time is used to ensure the dispersing of the UV-pigment. A product prepared in the manner described above will not pro¬ duce dust, and it is easy to store and use. It is a further advantage that the use of a specific dispersing agent is not always necessary for achieving a storage stabile concentrate. The wax medium is selected on the basis of the surface proper¬ ties of the formulated pigment reducing the penetration of UV light, the other components desired in the final product, and the desired oil or water extension of the final product, and other factors. The preparation of granules according to the invention, con¬ taining UV-pigment, takes place by dispersing the UV-pigment o pigments into a melted wax component, and by cooling and granu lating the dispersion. It is possible to use in the dispersing any device known from other pigment dispersion processes. When the aim is the highest UV-pigment concentrations, it is ad¬ vantageous to use slow-moving kneading devices and roll mecha¬ nisms suitable for the dispersing of stiff mixes. Dispersing devices of high shear strengths or ultrasound devices are suit able for more viscous mixes. The dispersing may also be carrie out by using grinding devices, such as a bead mill. In the dispersion step it is usually advantageous to use as an aid a suitable surfactant or a suitable combination of surfactants, preferably a mono- or diester of glycerol. When the agglome¬ rates of the UV-pigments have been divided, the dispersion is allowed to solidify either into large pieces, such as sheets, pellets, tablets, extruder granules, or prills, which can, whe so desired, be converted into a smaller particle size by a known method such as crushing, grinding or screening. In one preferred embodiment of the invention, spray cooling is used for the solidification, in which case the dispersion is obtained either directly or after possible pulverization and/o screening, in the desired product form. Spray cooling takes place in the same manner as currently in other arts, such as the preparation of surfactants. The apparatus includes an atom izer by means of which the molten dispersion is converted into droplets, and a chamber in which the drops congeal in so solid a form that they will not adhere to the base. It possibly also includes a cyclone in which the product is separated from the gaseous medium used in the cooling, the medium normally being air. The temperature of the cooling gas must be below the con¬ gealing temperature of the melt, and may in general be close t the ambient temperature. The apparatus may be a cylindrical container which has the atomizer in its upper section and on the bottom of which the solidified particles will fall. The atomizer may be a nozzle in which the molten dispersion is atomized either by pumping melt into the nozzle or by using as aid pressurized gas, such as compressed air. Furthermore, the atomization can be effected by a rapidly rotating dispersing device, such as a smooth or grooved plate, a wheel disc or a blade wheel, or a perforated cylindrical-surfaced prilling device. The molten dispersion is fed in at so high a tempera¬ ture that the heat carried in it will suffice to keep the tem¬ perature of the feeding device above the congealing temperatur of the melt dispersion, or the feeding device may also be equipped with a heating device, for example an electric resis¬ tor, hot-air blower, a liquid or steam mantle, etc. The granules produced are preferably screened to the desired particle size. To avoid agglomeration of the product during storage, the granules may be powdered with a fine-grained mate rial such as silica or silicic acid. Another preferred powder¬ ing substance is UV-pigment, although its efficiency in in¬ hibiting agglomeration is usually not of the same order as tha of silica. The amount of powdering substance depends on the softness of the granule and on at how high a temperature the product must be capable of being stored. A commonly used amoun is approx. 0.01-2 % of the weight of the granule. It is often preferable to carry out the powdering while the granules are warm, for example close to their maximum storage temperature. Solid dispersions according to the invention may be turned int tablets by using devices which are used for tabletting waxy substances. In these, the mix to be tabletted may, for example be cast onto a cooled perforated belt or cylinder, where the tablet is formed, and they may have a cooled belt conveyor on which the tablet will have time to harden. The tablet size may vary greatly, but a size of approx. 4-5 mm is preferable. The use of solid UV-protectors according to the invention for the preparation of cosmetic formulations, such as sunscreen emulsions and creams, lipsticks, and hair-care products takes place simply by heating them to so high a temperature that th solid UV-pigment dispersion melts, whereupon it can be mixed with the other components to be used in the formulation, in t same manner as the waxy substance used as the medium of the dispersion would even otherwise be used separately for the sa application. Except in cosmetic applications, granules according to the invention may also be used in coatings and plastics products which UV-pigment is added to improve their resistance to ligh In these applications, the amounts UV-pigments used are usual small, for example 0.05-0.5 % by weight. In UV-pigment granul according to the invention, intended for these applications, is preferable to use as the wax component waxes or softeners which are even otherwise used in the coating or plastic con¬ cerned. The following agents used in the examples are solid emulsifie manufactured by Grindsted A/S: Dimodan: monoglyceride, dis¬ tilled; Lactodan: lactic acid ester of monoglyceride; Panodan diacetyl tartrate of monoglyceride; Artodan: Na and Ca stearo lactates containing lactic acid 20-34 %; Famodan: sorbitan ester of fatty acid; E uldan: mono/diester of fatty acid. Examples In the formulae of the examples, all percentages refer to % b weight. The granule samples were prepared by the following methods. Granulation method 1: The waxy ingredients were mixed with each other and were melt by heating. UV-pigment was mixed in gradually. Then the mixtu was dispersed for 0.5-2 min by using a high-efficiency rod disperser, whereafter the obtained dispersion was poured onto slab to cool into sheet form. The sheet was crushed and ground was cooled, when necessary, before grinding, and was screened to the desired particle size. Granulation method 2: A molten dispersion was prepared as above, but the dispersing was carried out in the course of approx. 15-30 min by using a circular disperser blade. The molten dispersion was granulated in a rapidly rotating atomizer into droplets, which upon cool¬ ing in air hardened into round granules. The granules were screened to the desired particle size. Example 1. A nonionic surfactant (Solan E)/hydrophilic UV-Ti0 2 Into 200 g of molten PEG-75 lanolin (Solan E/Croda Chemicals, HLB approx. 16) there was dispersed 170 g of UV-Titan M212 which had been given a hydrophilic surface treatment. The UV- Tiθ2 concentration in the mixture was 45.9 %. The product was granulated with good results by both method 1 and method 2. Th functioning of the product was ascertained in a cosmetic prepa ration. Example 2. UV-Ti0 2 64 %, Solan E Into molten PEG-75 lanolin (Solan E/Croda Chemicals) there was dispersed UV-Titan M262 which had been given a hydrophobic coating, whereupon the UV-Tiθ2 concentration of the dispersion was 64 %. The granulation was by method 1. Example 3. Nonionic surfactant Solan E/hydrophobic UV-Tiθ2 Into 200 g of molten PEG-75 lanolin (Solan E/Croda Chemicals) there was dispersed 170 g of UV-Titan M262 which had been ren¬ dered hydrophobic by a surface treatment. The UV-Tiθ2 con¬ centration of the mixture was 45.9 %. The product was granu¬ lated with good results both by method 1 and by method 2. The functioning of the product was ascertained in a cosmetic prepa ration. Example 4. Various nonionic surfactants Solid dispersions containing UV-Titan M262 40 % and UV-Titan M212 40 % were prepared by method 1 in the following media: a propyleneoxy-ethyleneoxide derivative of ethylene diamine (Tet- ronic 908), Poloxamer 338, Poloxamer 407, polyoxyethylene(20) tallow fatty alcohol and polyoxyethylene (50) tallow fatty alcohol. The melt viscosities obtained with the ethoxylated fatty alcohols were so low that these dispersions were assesse to be suitable also for granulation method 2. Example 5. Surfactant Acidan N12, melting in a microwave oven 40 g of Acidan N12 (a citric acid ester of monoglyceride, HLB approx. 11) and 40 g of UV-Titan were mixed while dry. 10 g of ion-exchanged water was added. The mixture was melted in a microwave oven, most of the water evaporating. The obtained viscous paste was stirred vigorously and was poured onto a slab, on which it was shaped into a sheet approx. 3 mm thick. The sheet was hardened by cooling, was crushed, and was screened with a 1-mm mesh screen. Examples 6a-6c 40 parts by weight of hydrophobic UV-Titan M262 was dispersed into 60 parts by weight of a melt which had been prepared by heating together at approx. 110 °C for approx. 20 min the fol¬ lowing components: Marlophor T (waxy polyethoxylated alkyl ester of phosphoric acid) , Noram S (waxy alkylamine) and paraf¬ fin wax. Example 6a: Marlophor:Noram = 2:1 Example 6b: Marlophor:Noram = 1:1 Example 6c: Marlophor:Noram:paraffin wax = 1:1:1. The viscosities of the melt dispersions were so low that they were assessed to be suitable for granulation by granulation method 2. Example 7. "Ancat" 1 "Ancat" compound dodecyltrimethylammoniumdodecyl sulfate was prepared by dissolving separately in water equal molar amounts of sodium dodecyl sulfate and dodecyltrimethylammonium bromide, by combining the solutions, by extracting the "ancat" salt wit diethyl ether, and finally by evaporating the ether. The ob¬ tained fine-grained solid compound was added to molten paraf¬ fin, into which it dispersed, increasing the viscosity of the melt even when used in a dose of a few per cent. Example 8. "Ancat" 2. An "ancat" compound was prepared by dissolving in diethyl ethe separately equal molar amounts of laurinic acid and dodecyl- amine. By combining the solutions a precipitate was obtained, which was separated by filtration. The remainder of the solvent was dried off by evaporation. The obtained fine-grained "ancat" salt was added on a hot plate into molten paraffin, in which it dissolved well. The adding was continued until a 1:1 mixture with paraffin was obtained. Then UV-Titan M262 was dispersed into this approximately 100 ° melt until a mixture containing UV-Tiθ2 45 % was obtained, which mixture was cast onto a slab to form a sheet, which upon cooling was easily crushed into granules. Example 9. "Ancat" 2, further experiment The "ancat" compound of Example 9 was melted as such on a hot plate, and the melt was heated to approx. 100 °C. UV-Titan M262 was dispersed into the melt until a mixture containing UV-Tiθ2 45 % was obtained. This mixture was cast onto a slab to form a sheet, which upon cooling was easily crushed into granules. Example 10. Wax + cetyl alcohol, no dispersing agent A melt was prepared which contained 52 g of paraffin wax, 4 g of beeswax and 2 g of cetyl alcohol (Crodacol C-90/Croda Chemi¬ cals). 42 g of UV-Titan M262 was dispersed into the mixture. The obtained dispersion was granulated by method 1. Example 11. Dispersing agent 14.7 % Lactodan B30, hydrophobic UV-Ti0 2 360 g of paraffin wax, 30 g of beeswax, and 150 g of surfacta Lactodan B30 were melted at approx. 100 °C. Into this melt there was dispersed 480 g of hydrophobic UV-Titan M262, where upon the UV-Tiθ2 content of the dispersion was 47 %. The mix¬ ture was granulated by method 2, with good results. Example 12. Dispersing agent Lactodan B30 20 %, various wax components Different waxes were experimented with in granulation accordi to method 1. Good results were obtained with all of the formulae. Example 12a 12b 12c 12d 12e 12 Lactodan B30 20 20 20 20 20 2 Paraffin wax 30 30 30 — — 15 Beeswax 5 — — — -- 1 Carnauba wax — 5 — 35 35 1 Candelilla wax — -- 5 — -._ — UV-Titan M262 45 45 45 45 __ 45 UV-Titan M212 — — — — 45 — Example 13. Dispersing agent Lactodan 1.8 %; testing in cos¬ metic preparations A molten approx. 80 °C UV-Tiθ2 dispersion was prepared, which contained paraffin wax 48.2 %, beeswax 3.8 %, Lactodan B30 1.8 %, and UV-Titan M262 46.5 %. The mixture was dispersed by using an Ultra-Turrax disperser and was granulated by using a cylindrical prilling device rotating at 1400 r/min. Its 5 mm high cylindrical surface was equipped with 0.7 mm diameter perforations, its 200 mm diameter lower surface was closed, a its upper surface was open in the center for the feeding in of the melt dispersion. The molten dispersion solidified in the air chamber into round particles having an average particle size of approx. 0.5 mm. Granules made according to the formula of Example 13, from which particles having a size greater than 0.83 mm had been removed by screening, were tested for cosmetic preparations, with the following results: - The sun protection factor of a gloss lip-care rouge without the addition was low, 3, and its UVA:UVB ratio was mediocre, 0.54. When granules (0.9 % UV-Ti0 2 ) in an amount of 2 % were dispersed into the gloss rouge mix, the value of the sun pro¬ tection factor rose to 6 and the UVA:UVB ratio to an excellent level, 0.69. - The sun protection factor of lipstick without the addition was mediocre, 4-5, whereas with a granule amount of 4 % (1.8 % UV-Tiθ2) the coefficient rose to a level of 16-19. - A sun-protector cream was prepared by using granules (4.9 % UV-Tiθ2) in an amount of 10.6 %. The sun protection factor was at a level of 29-31. Example 14. UV-Ti0 2 71 %, Lactodan B30 Into a melt which contained 25 g of paraffin wax, 5 g of car- nauba wax and 15 g of Lactodan B30 there was dispersed 110 g of hydrophobically coated UV-Titan M262, whereupon the UV-Tiθ2 concentration in the mix was 71.0 %. After prolonged kneading at a low speed, a clear-surfaced homogenous dispersion was obtained. Granules were prepared by method 1. Example 15. UV-Tiθ2 was dispersed into molten wax/emulsifier mixtures 15a)-15f). Dispersions were obtained the viscosities of which were suitable for both granulation methods 1 and 2. Example: 15a 15b 15c 15d 15e 15f Lactodan P22 20 Artodan AM - 20 Panodan AM - 20 Famodan MS - Di odan PV - Emuldan HA40 - Paraffin wax 35 35 35 15 24 24 Carnauba wax - 2 2 UV-Titan M262 45 45 45 45 23 23 Example 16a-16c 45 parts by weight of hydrophobic UV-Titan M262 was dispersed into melt mixtures which contained 46 parts by weight of paraf fin wax, 4 parts of beeswax and 5 parts of the following emul¬ sifiers: Example 16a) Artodan CF 40 Example 16b) Artodan CP 80 Example 16c) Artodan NP 55 Well spreading melt dispersions were obtained, which were as¬ sessed to be suitable for both granulation methods 1 and 2. Example 17. A mixed granule of hydrophobic and hydrophilic UV- τio 2 Granules were prepared by using as the raw materials paraffin wax 23.8 %, carnauba wax 4.8 %, Lactodan B30 14.3 %, UV-Titan M262 28.6 %. and UV-Titan M212 28.6 %. The UV-Ti0 2 concentra¬ tion in the mix was 57.2 %. Example 18. Compatibility of hydrophobic and hydrophilic UV- τi0 2 Granules were prepared by method 1 by dispersing 45 g of hydro phobic UV-Titan M262 into a melt consisting of 20 g of Lactoda B30 and 35 g of paraffin wax. Another batch of corresponding granules was prepared by using hydrophilic UV-Titan M212. The mutual compatibility of these granules was tested by first mixing them together and by then melting this mixture. A well flowing, beautiful dispersion was obtained. Example 19. The following UV-pigments were mixed with a 100 °C wax melt which consisted of mixtures of paraffin wax, beeswax and Lacto dan B30 at the weight ratio 30:5:20: Example 19a) UV-ZnO (Sachtotec LA 10) Example 19b) UV-ZnO + UV-Titan M262 1:1 Example 19c) UV-Titan M262 The zinc oxide dispersed into the wax melt, forming a low- viscosity mixture, whereupon the UV-pigment concentration in mixture a) was 50.3 % by weight. The corresponding UV-pigment concentrations in mixtures b) and c) were 45 % by weight. The mixtures were dispersed for 1 min by means of an Ystral rod disperser and they were cast into sheets. The cooled sheets were crushed, were ground in a Philips coffee grinder, and particles larger than 0.84 mm were screened off. Example 20. The functioning of the granules of Example 19 was tested in a W/O sunscreen emulsion. The oil phase of the emulsion was made up of the following components: Arlacel 780 (PEG3/PPG2/- Glyceryl/Sorbitol/Hydroxystearate/Isostearate) 4.0 parts by weight, mineral oil 12 parts by weight, Miglyol 812 (Caprylic/Capric Triglyceride) 6 parts by weight, Crill 6 (Sorbitan Isostearate) 2 parts by weight, and UV-pigment gran¬ ules in case a) 8.9 parts by weight and in cases b) and c) 10.6 parts by weight. The aqueous phase of the emulsion consisted o sorbitol 1.25 parts by weight, propylene glycol 1.25 parts by weight, Mg sulfate 0.7 parts by weight, and water in case a) 63.65 parts by weight and in cases b) and c) 61.95 parts by weight. Both the oil phase and the aqueous phase were heated t 75 °C. The aqueous phases were added to the oil phases gradual ly, while mixing. Finally 0.25 parts by weight of perfluoro- polymethyl-isopropyl ether (Fomblin HC/25) was added. The functioning as a protector against UV light of these emul¬ sions which contained UV-pigment approx. 5 % by weight was tested, with the following results: Sample UV protection factor (SPF in vitro, FDA) 19a) 3 19b) 16-19 19c) 17-20 The granules 19b), containing UV-ZnO and UV-Ti0 2 , and the gran ules 19c), containing UV-Tiθ2, yielded excellent protection results. It can also be seen that the result obtained with the combination granule 19b) was unexpectedly good as compared wit the results obtained with the granules 19a) and 19c), which contained only UV-ZnO or only UV-Ti0 2 . Example 21. Solid dispersions were prepared from UV-Titan M160, which is a rutile pigment strongly surface modified with aluminum oxide and stearic acid. The pigment dispersed easily into ester waxes, such as carnauba wax, or into mixtures of such waxes an paraffin waxes. The following solid dispersions were prepared: Example: 21a) 21b) 21c) Carnauba wax 50 25 5 Candelilla wax - 25 - Paraffin wax - - 50 UV-Titan M160 50 50 45 The dispersing was successful. Dispersions 21a) and 21b) were granulated by method 1, dispersion 21c) by both method 1 and method 2. Example 22. The solid UV-Titan M160 dispersion of Example 21c) was used for making a test emulsion having a UV-Titan M160 concentration of 5 %. The in vitro sun protection factor measured for the pre¬ paration was 23-27 (FDA) and its UV-A/UV-B ratio 0.66. The dispersing was successful. Dispersions 22a) and 22b) were gran¬ ulated by method 1, dispersion 22c) by both method 1 and method 2, or alternatively dispersions 22a) and 22b) were tabletted.

Claims: Claims 1. A solid protector against UV light, comprising a pigment made up of metal oxide particles having a mean primary particl diameter smaller than 0.150 μm and reducing the penetration of UV light, characterized in that it is in the form of solid particles which have a mean diameter of at minimum 10 μm and which contain 10-80 parts by weight of the said pigment reduc¬ ing the penetration of UV light dispersed in 90-20 parts by weight of wax. 2. A protector against UV light according to Claim 1, charac¬ terized in that the pigment reducing the penetration of UV light is made up of metal oxide particles having a mean primar particle diameter of 0.010-0.100 μm, preferably approx. 0.020 μm. 3. A protector against UV light according to Claim 1 or 2, characterized in that the pigment reducing the penetration of UV light is made up of titanium dioxide (Ti0 2 ) particles and/o zinc oxide (ZnO) particles or of mixtures thereof, preferably of titanium dioxide (Tiθ2) particles. 4. A protector against UV light according to Claim 1, 2 or 3, characterized in that it contains at minimum 36 % by weight, preferably at minimum 40 % by weight, and most preferably at minimum approx. 44 % by weight of the said pigment reducing th penetration UV light. 5. A protector against UV light according to any of the above claims, characterized in that it contains at maximum 85 % by weight, preferably at maximum 80 % by weight, most preferably at maximum 75 % by weight of the said pigment reducing the penetration of UV light. 6. A protector against UV light according to any of the above claims, characterized in that it is in the form of particles having a mean diameter of 30-5000 μm, preferably approx. 50- 3000 μm. 7. A protector against UV light according to any of the above claims, characterized in that the wax is a substance which is solid and waxy at room temperature and becomes fluid at 40 °C minimum, preferably at 50 °C minimum, and most preferably at 55 °C minimum. 8. A protector against UV light according to Claim 7, charac¬ terized in that the wax is a substance which is solid and waxy at room temperature and becomes fluid at 200 °C maximum, pref¬ erably at 150 °C maximum, most preferably at 100 °C maximum. 9. A protector against UV light according to any of the above claims, characterized in that the wax is a natural wax, a min¬ eral wax, or a mixture thereof, preferably paraffin wax, car¬ nauba wax, candelilla wax, jojoba wax, Japan wax, beeswax, and/or lanolin, preferably carnauba wax, candelilla wax, jojob wax, or mixtures thereof, or corresponding hardened (hydrogen¬ ated) waxes. 10. A protector against UV light according to any of Claims 1 8, characterized in that the wax is a polyethoxylated alcohol or monoglycerol, preferably an alcohol containing 12-22 carbon atoms in its chain, a polyethoxylated hydrogenated ricinic aci and/or a polyethoxylated lanolin. 11. A protector against UV light according to any of the abov claims, characterized in that it contains wax at minimum 15 % by weight, preferably at minimum 20 % by weight, and most pref erably at minimum 30 % by weight. 12. A protector against UV light according to any of the abov claims, characterized in that it contains wax at maximum 90 % by weight, preferably at maximum 75 % by weight, and most pref erably at maximum 63 % by weight. 13. A protector against UV light according to any of the abo claims, characterized in that it is a cosmetic or constitutes part of a cosmetic, in which case the pigment transparent to light and the wax are cosmetically acceptable substances. 14. A protector against UV light according to Claim 13, char acterized in that it contains at least one of the following cosmetic auxiliary substances: cosmetically acceptable organi protectors against UV light, cosmetically acceptable preserva tives, antioxidants, vitamins and radical scavenger compounds, cosmetically acceptable color, mother-of-pearl and melanin pigments, and cosmetically acceptable perfumes. 15. A method for the preparation of a solid protector agains UV light according to any of Claims 1-14 for, characterized i that it comprises the following steps: a) 10-80 parts by weight of a pigment which reduces the pene¬ tration of UV light and is made up of metal oxide particles having a mean primary particle diameter smaller than 0.150 μm is dispersed into 90-20 parts by weight of a molten or viscou wax, and b) the molten or solid dispersion obtained from step a) is converted into the form of solid particles having a mean diameter of at minimum 10 μm. 16. A method according to Claim 15, characterized in that in step a) the pigment reducing the penetration of UV light is dispersed into a stiff wax by using a kneading device or a roller mechanism, into a viscous wax by using a mixing device having a high shear speed or an ultrasound device or, if a completely non-agglomerated pigment reducing the penetration UV light is desired, by using a grinding device. 17. A method according to Claim 15 or 16, characterized in that in step a) the pigment reducing the penetration of UV light is dispersed into the wax by using as an aid a sur¬ factant, preferably esters of fatty acids with glycol, glyce- rol, polyglycerol or sorbitol, most preferably mono- and di- glycerides of fatty acids, or their esters with small-molecule hydroxy acids. 18. A method according to Claim 15, 16 or 17, characterized in that in step b) the molten or soft dispersion obtained from step a) is molded into a form capable of being comminuted, preferably into the form of a sheet, a bar or pellets, is har¬ dened, when necessary, by cooling to below the congealing point of wax, is comminuted by cutting, chopping, crushing and/or grinding. 19. A method according to Claim 15, 16 or 17, characterized in that in step b) the melt obtained from step a) is converted into drops, and the drops are solidified by cooling to below the congealing point of the wax, preferably by using spray cooling, in which the molten dispersion is atomized into drop¬ lets, which are cooled in air or gas into solid form and are recovered. 20. A method according to any of Claims 15-19, characterized in that it includes a step c) in which the solid particles obtained from step b) are screened to the desired size. 21. A method according to any of Claims 15-20, characterized in that it includes a step d) in which the solid particles obtained from step b) or c) are powdered with a powder which inhibits agglomeration, preferably with silica, silicic acid or most preferably with a pigment reducing the penetration of UV, the amount of the powder inhibiting agglomeration being pref¬ erably 0.01-2 % of the weight of the solid protector against UV light. 22. The use of a solid protector against UV light according any of Claims 1-14, or prepared by a method according to any Claims 15-21, as a raw material in cosmetic products, prefera ly sunscreen creams, lip pomades, and hair-care products.

Inventors: AHLNAES JOHN THOMAS, LOEFGREN TIMO VALDEMAR, AHLNAES, JOHN, THOMAS, LOEFGREN, TIMO, VALDEMAR
Applicants: AHLNAES JOHN THOMAS, KEMIRA PIGMENTS OY, LOEFGREN TIMO VALDEMAR, AHLNAES, JOHN, THOMAS, LOEFGREN, TIMO, VALDEMAR
Application year: 1994
Main classification: A61K7
IPC codes: A61K8, A61K47, A61Q17, C01G23, C09D5