Lithium secondary battery

Abstract: A lithium secondary battery comprises a natural graphite as a negative electrode capable of occluding and discharging lithium ion, in which the natural graphite has been heat treated at a temperature of at least 1,800°C. The heat treatment removes impurities from natural graphite. As a result, the electrolyte solution used for the battery hardly decomposes during charge and discharge and self discharge hardly occurs during storage of the battery.

Description: The present invention relates to a lithium secondary battery and, more specifically to an improvement of the negative electrode material used therefor to achieve better cycle characteristics and storage capability. In recent years, lithium secondary batteries utilizing nonaqueous electrolytes have become spotlighted because of a possible high-voltage design without taking decomposition voltage of water into consideration, thus differing from water-based secondary batteries utilizing aqueous electrolyte solutions, such as nickel-cadmium batteries. Metallic lithium has been used as the negative electrode material of these lithium secondary batteries. In recent years, however, it has been pointed out that metallic lithium causes poor cycle characteristics due to the growth of dendritic deposits of lithium. Carbon materials, that occlude and discharge lithium ion solely during charge and discharge and have no such problem, and now studied as replacement of metallic lithium. Among these carbon materials, natural graphite having particularly high crystallinity and a large discharge capacity of 370 mAh/g, is one of the most promising negative electrode materials. However, natural graphite, being a natural product, contains in the crystals thereof impurities such as bound water and active terminal groups. These impurities react, during charge or discharge or during storage, with the electrolyte solution used to decompose and degrade it, whereby lithium secondary batteries with a negative electrode of natural graphite have had the problem of poor cycle characteristics and storage characteristics. Accordingly, an object of the present invention is to provide a lithium secondary battery with a negative electrode of natural graphite having excellent cycle characteristics and storage characteristics. The present invention provides a lithium secondary battery (hereinafter referred to as "the battery of the present invention") comprising natural graphite as a negative electrode capable of occluding and discharging lithium ion, said natural graphite having been heat treated at a temperature of at least 1800°C. A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same become better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein: FIGURE 1 is a schematic cross-sectional view of the battery of the present invention; FIGURE 2 is a graph showing the relationship between the cycle characteristics and the heat treatment temperature of natural graphite; and FIGURE 3 is a graph showing the relationship between the storage characteristics and the heat treatment temperature of natural graphite. This application claims the priority of Japanese Patent Application No. 5-96875 filed March 30, 1993, which is incorporated herein by reference. In the battery of the present invention, utilizing natural graphite from which impurities have been removed by heat treatment at a high temperature of at least 1,800°C, the electrolyte solution used hardly decomposes even by repeated cycles of charge and discharge. Besides, self discharge caused by impurities during storage is minimized. These facts constitutes the grounds for the battery of the present invention having better cycle characteristics and storage characteristics as compared with lithium secondary batteries utilizing natural graphite as it is, without heat treatment. The above heat treatment is carried out by heating natural graphite in a heating oven at a temperature of at least 1,800°C under an atmosphere of inert gas such as nitrogen or argon. It is particularly desirable, as shown in the Examples to be described later herein, to conduct the heat treatment at a temperature of at least 2,400°C, for the purpose of obtaining batteries having excellent cycle characteristics and storage characteristics. The heat treatment time varies according to the type of natural graphite but, generally, the usual impurities can be removed by heat treatment for about 24 hours. It is desirable that the natural graphite to be heat treated have high crystallinity, with a d-value (d 002 ) in the lattice plane of (002) of not more than 3.37 and a crystal size in the c-axis direction (Lc) of at least 200 Å. Raw natural graphite of this type hardly changes its d 002 and Lc by heat treatment. As described above, the key feature of the present invention lies in the use, to obtain a lithium secondary battery having excellent cycle characteristics and storage characteristics, of natural graphite having little impurities as a negative electrode material. Accordingly, there are no particular restrictions with respect to other materials constituting the battery, such as positive electrode material and electrolyte solution and various materials that have been used or proposed can be used without limitation. Thus, examples of usable positive electrode materials (active materials) are modified MnO 2 , LiCoO 2 , LiNiO 2 , LiMnO 2 , LiMn 2 O 4 and LiFeO 2 . Examples of usable electrolyte solutions are those of electrolyte solutes such as LiPF 6 , LiBF 4 , LiClO 4 and LiCF 3 SO 3 each dissolved in a organic solvent such as ethylene carbonate, vinylene carbonate or propylene carbonate, or in a mixed solvent of any one of the above organic solvents with a low-boiling-point solvent such as dimethyl carbonate, diethyl carbonate, 1,2-dimethoxyethane, 1,2-diethoxyethane or ethoxymethoxyethane. Other features of the invention will become apparent in the course of the following descriptions of exemplary embodiments which are given for illustration of the invention and are not intended to be limiting thereof. EXAMPLES Examples 1 through 7 AA-size lithium secondary batteries according to the present invention were prepared as follows. Positive electrode A slurry was prepared by dispersing a mixture obtained by mixing LiCoO 2 as a positive electrode active material and artificial graphite as a conductive agent in a ratio by weight of 9:1 in a 5% by weight solution of polyvinylidene fluoride in N-methylpyrrolidone (NMP) . The slurry thus prepared was applied by a doctor blade to both sides of an aluminum foil as a positive electrode collector, and then vacuum-dried at 100°C for 2 hours, to obtain a positive electrode. Negative electrodes Natural graphite (d 002 = 3.360 Å, Lc = 1,500 Å) was heat treated in a heating oven under an atmosphere of nitrogen (upper limit of heating temperature in the oven: 3,000°C) at a temperature of 1,800, 2,000, 2,200, 2,400, 2,600, 2,800 or 3,000°C for 24 hours. The d 002 and Lc were obtained after each heat treatment, all of which were the same as those before heat treatment. Slurries were prepared by dispersing each of the above heat-treated graphite in a 5% by weight solution of polyvinylidene fluoride as a binder in NMP. The slurries thus obtained were each applied by doctor blade method to both sides of a copper foil as a negative electrode collector, which were then vacuum-dried at 100°C for 2 hours, to give 7 types of negative electrodes. Electrolyte solution LiPF, was dissolved in a 1/1 by volume mixed solvent of ethylene carbonate and dimethyl carbonate in a concentration of 1 mole/l, to prepare an electrolyte solution. Preparation of batteries Seven types of AA-size batteries, BA1 through BA7 (larger numbers mean higher heat treating temperatures), of the present invention having different negative electrodes were prepared with the above positive electrode and electrolyte solution. A polypropylene microporous film (trade name: CELGARD, made by Celanese Corp.) was used as separator, which was impregnated with the above electrolyte solution. FIGURE 1 is a schematic cross-sectional view of the battery BA1 of the present invention (BA2 through BA7 have a similar structure) . In the FIGURE, the battery BA1 comprises a positive electrode 1, a negative electrode 2, a separator 3 separating the two electrodes, a positive electrode lead 4, a negative electrode lead 5, a positive electrode external terminal 6 and a negative electrode can 7. The positive and negative electrodes 1 and 2, between which the separator 3 is sandwiched, are spirally wound and housed in the negative electrode can 7. The positive electrode 1 is connected, via the positive electrode lead 4, to the positive electrode external terminal 6, and the negative electrode 2 to the negative electrode can 7 via the negative electrode lead 5, so that chemical energy that generates inside the battery can be taken out as electric energy. Comparative Examples 1 through 5 The procedure for Examples 1 through 7 was repeated except that natural graphite without heat treatment, or that heat treated at 1,000°C, 1,200°C, 1,400°C or 1,600°C was used, to prepare comparison batteries, in the above order, BC1 through BC5. Relationship between the cycle characteristics and the heat treating temperature The batteries were each subjected to a cycle test to study the relationship between the cycle characteristics and the heat treating temperature for natural graphite. One cycle comprised charging with a charge current of 200 mA to a charge termination voltage of 4.1 V, followed by discharging with a discharge current of 200 mA to a discharge termination voltage of 2.75 V. The results are shown in FIGURE 2. FIGURE 2 is a graph showing the relationship between the cycle characteristics and the heat treating temperature of natural graphite, with the ordinate representing the cycle deterioration ratio (%/cycle) at the 500-th cycle and the abscissa representing the heat treating temperature (°C). Zero (0) on the abscissa means no heat treatment. The cycle deterioration ratio is obtained by dividing the ratio (%) of the discharge capacity at the 500-th cycle to that at the initial stage of cycles by the total number of cycles repeated, i.e. 500. It is understood from the FIGURE that the batteries of the present invention, BA1 through BA7, utilizing as their negative electrode natural graphite heat treated at a temperature of at least 1,800°C, have smaller cycle deterioration ratios, i.e. better cycle characteristics than those of comparison battery BC1 with a negative electrode utilizing natural graphite as it is, without heat treatment, and comparison batteries BC2 through BC5, utilizing natural graphite heat treated at a temperature of not more than 1,600°C. It is also understood from the FIGURE that, in particular, the batteries of the present invention BA4 through BA7, with the heat treating temperature exceeding 2,400°C have markedly small cycle deterioration ratios, i.e. markedly excellent cycle characteristics. Relationship between the storage characteristics and the heat treating temperature Each of the above batteries was, after being stored for 1 year, charged with a charge current of 200 mA to a charge termination voltage of 4.1 V and then discharged with a discharge current of 200 mA to a discharge termination voltage of 2.75 V, to study the relationship between the storage characteristics and the heat treating temperature for the natural graphite used for their negative electrode. The results are shown in FIGURE 3. FIGURE 3 shows the relationship between the storage characteristic and the heat treating temperature of natural graphite, with the ordinate representing the capacity retention (%) after 1-year storage and the abscissa representing the heat treating temperature (°C). Like in FIGURE 2, zero (0) on the abscissa means no heat treatment. The capacity retention means the ratio (%) of the discharge capacity after 1-year storage to that before storage. From the FIGURE it is understood that the batteries of the present invention BA1 through BA7, utilizing as their negative electrode natural graphite heat treated at a temperature exceeding 1,800°C, have larger capacity retentions, i.e. better storage characteristics compared with comparison batteries BC1 through BC5. It is also understood from the FIGURE that the batteries of the present invention BA4 through BA7, utilizing natural graphite heat treated at a temperature of, in particular, at least 2,400°C have markedly excellent storage characteristics. Although the present invention has been described hereinabove by reference to AA-size batteries alone, the invention can apply to batteries of any other shape, such as flat or square, with no particular limitation. Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.

Claims: A lithium secondary battery comprising natural graphite as a negative electrode capable of occluding and discharging lithium ion, said natural graphite having been heat treated at a temperature of at least 1,800°C. The lithium secondary battery according to Claim 1, wherein said natural graphite has been heat treated at a temperature of at least 2,400°C. The lithium secondary battery according to either Claim 1 or Claim 2, wherein said natural graphite has a d-value (d 002 ) in the lattice plane of (002) of not more than 3.37 Å and a crystal size in the c-axis direction (Lc) of at least 200 Å.

Inventors: NISHIO KOJI, OHSHITA RYUJI, SAITOH TOSHIHIKO, TAKAHASHI MASATOSHI, UENO KOJI, NISHIO, KOJI, OHSHITA, RYUJI, SAITOH, TOSHIHIKO, TAKAHASHI, MASATOSHI, UENO, KOJI, NISHIO, KOJI, C/O SANYO ELECTRIC CO., LTD., OHSHITA, RYUJI, C/O SANYO ELECTRIC CO., LTD., SAITOH, TOSHIHIKO, C/O SANYO ELECTRIC CO., LTD., TAKAHASHI, MASATOSHI, C/O SANYO ELECTRIC CO., LTD., UENO, KOJI, C/O SANYO ELECTRIC CO., LTD.
Applicants: SANYO ELECTRIC CO, SANYO ELECTRIC CO., LTD.
Application year: 1994
Main classification: H01M4
IPC codes: H01M6, H01M4, C01B31, H01M10