Method for recycling painted plastic materials

Abstract: A plastic material with a paint film is coarse-crushed, and a film decomposition agent, e.g. a heterocyclic compound such as imidazole, a triazine compound such as benzoguanamine, a phenylendiamine compound such as N-phenyl-N'-isopropyl-p-phenylene diamine, is added to the coarse-crushed material. The mixture is then heated and kneaded to dissolve the paint film and uniformly spread the particles of the paint film in the plastic material. The physical properties and surface quality of the plastic material are substantially the same as those of the original material.

Description: Background of the Invention and Related Art Statement The present invention relates to a method for recycling plastic products or plastic waste articles with painted surfaces. In recent years, plastic products are often used for automobile parts. For example, when plastic bumpers with unpainted surfaces are recycled, defectively molded bumpers and the bumpers recovered from scrapped vehicles are coarse-crushed to a size about 3 mm cube, which are then mixed with a virgin or new material and reused to mold bumpers. This is possible because the physical properties of recycled plastic materials are not substantially degraded. However, in the bumpers with painted surfaces, plastic materials recovered in the same manner can not be reused for bumpers. This is because, when the painted bumpers are crushed, paint films are mixed in the recycled plastic materials, so that the physical properties of the plastic materials, such as impact resistance, elongation and surface quality substantially degrade, resulting in a failure to satisfy the performance required as a bumper. Therefore, the painted plastic bumpers which are defectively molded or those recovered from scrapped vehicles are buried in the ground or burned to thereby cause environmental disruption. Some, however, are recycled for construction piles, in which requirements regarding physical properties are not so strict. Japanese Patent Publication (KOKAI) No. 3-23909 proposes a method for separating and recovering polyurethane and polyvinyl chloride from waste in which these compounds are laminated. In this method, the above waste composite materials are coarse-crushed to 20 to 50 mm masses, and are then pulverized by agitation in an agitator. In order to recover polyvinyl chloride, polyurethane with a particle size of 1 to 2 mm is separated by a sieve from sheet-like polyvinyl chloride with an overall size of 30 mm. Currently, for recycling the plastic bumpers with painted surfaces, techniques are being developed to separate the plastic portions from the paint film portions and to recover only the plastic portions for recycling. The following three major techniques are generally used: (1) Method for removing the paint film by blasting Abrasive materials are blown with compressed air against the paint film of the painted plastic bumper to mechanically remove the film. (2) Method for melting resin and separating the paint film with a screen A painted plastic bumper is coarse-crushed and fed into an extruder where the plastic part is melted. Since the paint film does not melt in the extruder due to its thermosetting property, the paint is separated by a screen installed at the outlet of the extruder. (3) Method using chemicals to release the paint film from plastic A mixed liquid of organic salts, polyhydric alcohol and water is heated to about 100 °C. A coarse-crushed painted plastic bumper is immersed in this liquid for several hours to release the paint film. Also, Japanese Patent Publication (KOKAI) No. 2-273207 discloses a method for using vegetable type soft abrasive materials to release paint films by blasting. Further, Japanese Utility Model Publication (KOKAI) No. 61-196021 discloses a foreign matter removing device for plastic molding material, wherein a foreign matter removal part formed of a wire gauze and a supporting body is serially located between an extruder and a mold. EP-A-0547249 discloses a method of recycling coated plastics waste to obtain a recycled resin composition for molding. In the method, plastics waste coated with, for example. a urethane film or an amino resin film is subjected to hydrolysis or alcoholysis and then kneaded to produce the recycled composition. The hydrolysis or alcoholysis is conducted by contacting the waste in pulverised form with a "treating agent" in the liquid or vapour state at an elevated temperature above or below the melting point of the waste. The process depolymerises the paint film, which is then evenly dispersed into the plastics waste. The "treating agent" which hydrolyses or alcoholyses the paint film is water or an alcohol. or a mixture thereof, optionally containing an acid or base catalyst. US-A-3972839 teaches a method for stripping paint films using a composition containing an alkaline material, for example an alkali metal hydroxide, and a mixture of amines. such as alkanolamines. The paint film is stripped by contacting it with the composition, usually at an elevated temperature. FR-A-2213969 describes a composition for removing protective organic coatings, such as paints. The composition contains an alkaline material, for example an alkali metal hydroxide, and an alkyl or aryl substituted imidazole. The paint film is removed by contacting it with the composition. usually at an elevated temperature. With the above method (1), it is very difficult to adjust the distance between an abrasive spraying nozzle and an object, the spraying angle, air pressure, and the diameter and shape of the nozzle, because the bumper has a three-dimensional variable surface shape. If the device is not properly adjusted, the paint film is not effectively removed. In addition, when the plastic parts are recycled, the abrasive materials remain on the plastic surface from which the paint film has been released as if cutting into the surface, so that the physical properties of the recycled material are degraded. With the method of (2), if a screen with fine mesh is installed at the outlet of the extruder to completely remove the crushed paint film pieces, the extruding pressure must be high, so that the screen is damaged. If a screen with coarse mesh is used, the fine film pieces can not be removed. The method of (3) can release the finished paint films but can not remove primer without degrading the physical properties of the plastic part. It is also difficult to use the method in industrial applications due to waste disposal problems. In the method of pulverizing the materials by the agitator rotating at high speed as described in the above Japanese Publication No. 3-23909, it is possible to separate the laminated materials, but the paint films can not be removed from the plastic materials. Accordingly, it is an object of the invention to provide a method for recycling painted plastic materials, which can omit an expensive step of releasing and separating a paint film by dissolving and uniformly spreading the paint film in the plastic material without adversely affecting the physical properties or surface quality of the plastic materials. Summary of the Invention In the method of the invention, painted plastic materials are coarse-crushed, and after a film decomposition agent is added to the coarse-crushed materials alone or a mixture of the coarse-crushed materials and virgin or new plastic materials, the resultant materials are heated and kneaded. As a result, the paint film is dissolved and uniformly distributed or spread in the plastic materials. The paint film decomposition agent is : (a) a heterocyclic compound selected from 2-mercaptoimidazoline, benzotriazole, 3-amino-1,2,4-triazole, 2-methylimidazole, N-cyclohexyl-2-benzothiazole sulfenamide and imidazole; (b) a triazine compound selected from 2-di-n-butylamino-4, 6-dimercapto-s-triazine, benzoguanamine, isomelamine, acetoguanamine, 2,4,6-trimercapto-s-triazine, isocyanuric acid and isocyanuric acid ester; or (c) a phenylenediamine compound selected from N-phenyl-N'-isopropyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenedimnine, N-phenyl-N'-1,3-dimethylbutyl-p-phenylenediamine, N,N'-di-beta-naphthyl-p-phenylenediamine and N,N'-diaryl-p-phenylenediamine. When the paint film decomposition agent reacts with the paint film, the film is dissolved, decomposed to the particle level, and uniformly spread in the plastic material. Consequently, this method does not adversely affect the physical properties or surface quality of the plastic materials. Brief Description of the Drawing Fig. 1 is a partial sectional view of a painted plastic bumper. Detailed Description of Preferred Embodiments The method according to the present invention is outlined with reference to a painted plastic bumper shown in Fig. 1. In Fig. 1, a plastic material 1 is a thermoplastic resin, such as polyolefine resin or ABS resin, and a primer paint 2 and a finish paint 3 are a polyolefine chloride resin and a polyester melamin resin, respectively, which are ordinary baking enamels. The painted plastic bumper as a waste is coarse-crushed by a crusher, and a paint film decomposition agent is added to the coarse-crushed material, which are heated to at least the temperature at which the paint film decomposition agent reacts with the paint film and then kneaded by a mixer. 2-di-n-butyl-amino-4,6-dimercapto-S-triazine is used as the paint film decomposition agent, and an extruder, a kneader or a Bambury mixer is used as the mixer. 2-di-n-butyl-amino-4,6-dimercapto-S-triazine, which is used as the paint film decomposition agent, is known as a cross-linking agent or a stabilizer for halogen-containing polymer or diene rubber. In the method according to the invention, however, the solvent does not adversely affect the physical properties and surface quality of the plastic material, because the solvent reacts with and dissolves the paint film, which is then decomposed to the particle level and uniformly spread in the plastic material. Therefore, an effect equivalent to the removal of the paint film can be provided without separating or removing the paint film from the plastic material, and physical properties equivalent to those of the new material can be obtained. Consequently, the recycling of the painted plastic material is made practical. Examples of the invention are shown below. Example I (1) Material of painted plastic bumper as samples Plastic: polypropylene resin Paint: primer - polyolefin chloride resin thickness: about 25 micro meter finish paint - polyester melamine resin thickness: about 30 micro meter (2) Treatment of samples The painted plastic bumper is coarse-crushed by the crusher to about 1 to 10 mm cube. 25% by weight of coarse-crushed material is added to a new material or a virgin polypropylene resin. (3) Paint film decomposition agent 2-di-n-butyl-amino-4,6-dimercapto-S-triazine (product name: Jisunetto DB by Sankyo Kasei Inc.)Amount added: 0.5 to 4% by weight of 2-di-n-butyl-amino-4,6-dimercapto-S-triazine is added to the aforementioned sample. (4) Heating and mixing treatment The mixing sample is fed into a kneader heated to 180 °C and is mixed for about one minute. The paint film decomposition agent is then added. The material is kneaded at 180 °C and about 70 rpm (rotor rotations) for about ten minutes. Embodiment 1 The material was injection-molded to provide test samples. A tension test was used to measure rupture elongation (breaking elongation), and the surface quality was visually evaluated. Table 1 shows the results. Table 1 indicates that the samples with 25% by weight of coarse-crushed material added to the virgin or new material can recover physical properties equivalent to those of an initial or new material when at least 2% by weight of the paint film decomposition agent is added. Therefore, the methods used for samples 5 to 7 are embodiments of this invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of paint film pieces] 1 ---------- 550 ------------------------- 2 ---------- 140 Film pieces were seen. 3 0.5 92 A few film pieces 4 1.0 202 No film pieces (good) 5 2.0 543 No film pieces (good) 6 3.0 534 No film pieces (good) 7 4.0 542 No film pieces (good) Note: Sample 1: Sample made by molding only a virgin or new material of plastic (no paint film) Sample 2: Sample made by remolding a material of 25% of coarse-crushed painted plastic bumper added to a virgin or new plastic material Example II Tables 2 to 11 show test examples in which various paint film decomposition agents were used. The test materials, treatment of samples, and evaluation method are shown below, and the film decomposition agents and amounts added are noted in the descriptions in the tables. (1) Materials of painted plastic bumper as samples Plastic: polypropylene resin Paint: primer - polyolefin chloride resin thickness: about 25 micro meter finish paint - polyester melamine resin thickness: about 30 micro meter (2) Treatment of samples The painted plastic bumper is coarse-crushed by a crusher to cubes of about 1 to 10 mm. 25% by weight of coarse-crushed material is added to a virgin or new material (polypropylene resin material), and the prescribed amount of a paint film decomposition agent is also added. (3) Heat and mix treatment The mixed sample is fed into a kneader and kneaded at 200 °C and about 70 rpm (rotor rotations) for 15 minutes. (4) Preparation, testing and evaluation of samples The material was injection-molded to provide test samples. A tension test was used to measure rupture elongation (breaking elongation), and the surface quality was visually evaluated. Table 2 and subsequent tables show the results. For reference, each table includes the rupture elongation and surface quality of the sample made by molding only a new material of plastic (no paint film) and the sample made by remolding a material of 25 wt% of coarse-crushed painted plastic bumper and a new material. Embodiment 2 As a paint film decomposition agent, 0.1 to 0.3% by weight of 2-mercaptoimidazoline, a heterocyclic compound, is added. The compound is known and used as a vulcanization accelerator for chloroprene-hyperon rubber. Table 2 shows the results of the evaluation. Samples 4 and 5, to which 0.2% or more of the paint film decomposition agent was added, recovered their original physical properties, and sample 3, to which 0.1% of the paint film decomposition agent was added, recovered most of its original physical properties. Therefore, the methods used for samples 3 to 5 are embodiments of the invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 0.1 498 A few film pieces 4 0.2 540 No film pieces (good) 5 0.3 540 No film pieces (good) Embodiment 3 As a paint film decomposition agent, 1 to 3% by weight of N-phenyl-N'-isopropyl-p-phenylene diamine, a phenylene diamine compound, is added. This compound is known and used as an antioxidant or anti-aging agent to prevent rubber with a double bond from ozone degradation, flex-cracking and sun-cracking. Table 3 shows the results of the evaluation. Samples 4 and 5, to which 2% or more of the paint film decomposition agent was added, recovered their original physical properties (sample 1), and sample 3, to which 1% of the paint film decomposition agent was added, recovered most of its original physical properties. Therefore, the methods used for samples 3 to 5 are embodiments of the invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 1.0 465 A few film pieces 4 2.0 526 No film pieces (good) 5 3.0 595 No film pieces (good) Embodiment 4 As a paint film decomposition agent, 0.1 to 0.3% by weight of benzotriazole, a heterocyclic compound, is added. This compound is known and used as a corrosion inhibitor for copper and its alloys, silver and aluminum. Table 4 shows the results of the evaluation. Samples 4 and 5, to which 0.2% or more of the paint film decomposition agent was added, recovered their original physical properties (Sample 1), and sample 3, to which 0.1% of the paint film decomposition agent was added, recovered most of its original physical properties. Therefore, the methods used for Samples 3 to 5 are embodiments of the invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 0.1 430 A few film pieces. 4 0.2 520 No film pieces (good) 5 0.3 540 No film pieces (good) Embodiment 5 As a paint film decomposition agent, 0.1 to 0.3% by weight of 3-amino-1,2,4-triazole, a heterocyclic compound, is added. This compound is known and used for a disperse dye, photographic chemical, curing agent for resin and herbicide. Table 5 shows the results of the evaluation. Samples 3, 4 and 5, to which 0.1% or more of the paint film decomposition agent was added, recovered their original physical properties (Sample 1). Therefore, the methods used for samples 3 to 5 are embodiments of the invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 0.1 532 No film pieces (good) 4 0.2 666 No film pieces (good) 5 0.3 653 No film pieces (good) Embodiment 6 As a paint film decomposition agent, 0.1 to 1.0% by weight of 2-methylimidazole, a heterocyclic compound, is added. The compound is known and used as a resin hardening agent, an industrial disinfectant and a rust preventing agent. Table 6 shows the results of the evaluation. Sample 5, to which 1% of the paint film decomposition agent was added, recovered its original physical properties (Sample 1). Sample 4, to which 0.5% of the film decomposition agent was added, recovered most of its original physical properties. Therefore, the methods used for samples 4 and 5 are embodiments of the invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ------------ 550 ---------------------- 2 ------------ 140 Film pieces were seen. 3 0.1 245 A few film pieces. 4 0.5 432 No film pieces (good) 5 1.0 541 No film pieces (good) Embodiment 7 As a paint film decomposition agent, 5% by weight of N-cyclohexyl-2-benzothiazole sulfenamide, a heterocyclic compound, is added. This compound is known and used as a vulcanization accelerator for rubber. Table 7 shows the results of the evaluation. Sample 3, to which 5% of the paint film decomposition agent was added, recovered most of its original physical properties. Therefore, the method used for sample 3 is an embodiment of this invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 5.0 462 A few film pieces. Embodiment 8 As a paint film decomposition agent, 5% by weight of benzoguanamine (2,4-diamine-6-phenyl-1,3,5-triazine), a triazine compound, is added. This compound is known and used as a vehicle for baking enamel, a cosmetic board, and fiber and paper processing resin. The heating and mixing of this sample were exceptionally performed at 250 °C. Table 8 shows the results of the evaluation. Sample 3, to which 5% of the paint film decomposition agent was added, recovered its original physical properties and provided good surface quality. Therefore, the method used for sample 3 is an embodiment of this invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 5.0 280 No film pieces (good) Embodiment 9 As a paint film decomposition agent, 5% by weight of imidazole, a heterocyclic compound, is added. The compound is known and used as a resin hardening agent and a rust preventing agent. Table 9 shows the results of the evaluation. Sample 3, to which 5% of the film decomposition agent was added, recovered its original physical properties and provided a good surface quality. Therefore, the method used for sample 3 is an embodiment of this invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 550 ---------------------- 2 ----------- 140 Film pieces were seen. 3 5.0 530 No film pieces (good) Example III is described below. (1) Material of painted plastic bumper as samples Plastic: polypropylene resin Paint: primer - polyolefin chloride resin thickness: about 25 micro meter finish paint - polyester melamine resin thickness: about 30 micro meter (2) Treatment of samples The painted plastic bumper in (1) is coarse-crushed by the crusher to cubes of about 1 to 10 mm. A prescribed amount of film decomposition agent is added to 100% coarse-crushed material which is a recycled material. The mixed material is fed into the kneader and kneaded at 200 °C and 70 rpm (rotor rotations) for 15 minutes. (3) Film decomposition agent 0.3 to 1.5% by weight of benzotriazole is added to the coarse-crushed material, which is a 100% recycled material. (4) Preparation, testing and evaluation of samples The test pieces were prepared from the above mixture by using an injection molding machine. A tension test was performed to measure rupture elongation (breaking elongation), and the surface quality was visually evaluated. Embodiment 10 As a paint film decomposition agent, 0.3 to 1.5% by weight of benzotriazole is added. The compound is known and used as a corrosion inhibitor for copper and its alloys, silver, and aluminum. Table 10 shows the results of the evaluation. Samples 4 to 6, to which 0.5 to 1.5% by weight of the paint film decomposition agent was added, recovered the original physical properties of a virgin or new material (containing no paint) and provided a good surface quality. Therefore, the methods used for samples 4 to 6 are embodiments of this invention. Sample 1 was made by molding only a virgin or new material of plastic (no paint film), and sample 2 was made by molding a coarse-crushed material which is a 100% recycled material. These samples are included in the table for comparison. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 660 ---------------------- 2 ----------- 140 Film pieces were seen. 3 0.3 132 A few film pieces 4 0.5 510 No film pieces (good) 5 1.0 586 No film pieces (good) 6 1.5 600 No film pieces (good) Embodiment 11 The same painted plastic bumper as in the previous test example was used as a sample and treated in the same manner as in the previous test example. 0.1 to 0.6% by weight of 3-amino-1,2,4-triazole was added to a coarse-crushed material which is a 100% recycled material. The preparation, testing, and evaluation of test pieces were executed in the same manner as in the previous test example. 3-amino-l,2,4-triazole is known and usually used as a disperse dye, photographic chemical, resin hardening agent, and herbicide. Table 11 shows the results of the evaluation. Samples 5 and 6, to which 0.4 to 0.6% by weight of the paint film decomposition agent was added, recovered the original physical properties of an initial material shown in sample 1 (containing no paint) and provided a good surface quality. Therefore, the methods used for Samples 5 and 6 are embodiments of this invention. Sample No. Amount of film decomposition agent added % Rupture elongation % Surface quality [visually evaluated for the presence of film pieces] 1 ----------- 660 2 ----------- 140 Film pieces were seen. 3 0.1 167 A few film pieces 4 0.2 133 A few film pieces 5 0.4 627 No film pieces (good) 6 0.6 630 No film pieces (good) These tests suggest that a heterocyclic compound, such as 2-mercaptoimidazoline, benzotriazole, 2-amino-1,2,4-triazole, 2-methylimidazole, N-cyclohexyl-2-benzothiazole sulfenamide or imidazole is effective as a film decomposition agent. It is supposed that these compounds would still be effective if two or more compounds were mixed. The film decomposition agent may be a triazine compound, such as isomelamine, acetoguanamine, 2,4,6-trimercapto-s-triazine, isocyanuric acid or isocyanuric acid ester (triaryl cyanurate or triisocyanurate) in addition to 2-di-n-butyl-amino-4, 6-dimercapto-S-triazine, or benzoguanamine, which were used in the above tests. In addition to N-phenyl-N'-isopropyl-P-phenylene diamine used in the above tests, a phenylendiamine compound, such as N,N'-diphenyl-P-phenylendiamine, N-phenyl-N'-1,3-dimethylbutyl-P-phenylendianine, N,N'-di-Beta-naphthyl-P-phenylendiamine or N,N'-diaryl-P-phenylendiamine can also be used. The conventional recycling of the painted plastic materials depends on the separation and removal of paint film from the plastic materials. However, in the invention, the paint film is completely dissolved and uniformly spread in the plastic material to avoid adverse effects on the physical properties and surface quality of the plastic material by adding a paint film decomposition agent to a coarse-crushed plastic material. Consequently, the most expensive steps of releasing and separating the paint film can be omitted to substantially reduce recycling costs. Although the above embodiments have been described in conjunction with a painted plastic bumper, this invention is also applicable to the recycling of other automobile parts, such as wheel covers or side mirror covers. This invention also allows the recycling of plastic parts other than the automobile parts when their surfaces are painted or treated by other techniques. In the present invention, the paint film is completely dissolved and uniformly spread in the plastic material in order to avoid adverse effects on the physical properties and surface quality of the plastic material to be recycled. It also eliminates the most expensive step of releasing and separating film to thereby substantially reduce recycling costs. While the invention has been explained with reference to the specific embodiment of the invention, the explanation is illustrative and the invention is limited only by the appended claims.

Claims: A method of recycling painted plastic articles comprising, coarse-crushing the plastic articles having a paint film on a surface thereof, supplying a paint film decomposition agent to the coarse-crushed plastic articles, characterised in that said coarse-crushed plastic articles are heated and kneaded with the film decomposition agent to dissolve the paint film and uniformly spread particles of the paint film in the plastic articles, and in the that said film decomposition agent is: (a) a heterocyclic compound selected from 2-mercaptoimidazoline, benzotriazole, 3-amino-1,2,4-triazole. 2-methylimidazole, N-cyclohexyl-2-benzothiazole sulfenamide and imidazole; (b) a triazine compound selected from 2-di-n-butylamino-4, 6-dimercapto-s-triazine, benzoguanamine, isomelamine, acetoguanamine, 2,4,6-trimercapto-s-triazine, isocyanuric acid and isocyanuric acid ester; or (c) a phenylenediamine compound selected from N-phenyl-N'-isopropyl-p-phenylenediamine. N,N'-diphenyl-p-phenylenediamine, N-phenyl-N'-1,3-dimethylbutyl-p-phenylenediamine, N,N'-di-beta-naphthyl-p-phenylenediamine and N,N'-diaryl-p-phenylenediamine. A method according to Claim 1, further comprising moulding the plastic articles containing the particles of the paint film for reuse. A method according to Claim 2, further comprising adding new plastic articles to said coarse-crushed plastic articles with the paint film to provide a mixture thereof. A method according to Claim 3, wherein said plastic articles are crushed to have a cubic shape with a size of 1-10mm in one length. A method according to any of the preceding Claims wherein the step of heating and kneading the coarse-crushed plastic articles with the paint film decomposition agent is performed at a temperature of at least 180°C.

Inventors: OOHORI NORIKO, YAMAMOTO NAOTAKA, OOHORI, NORIKO, YAMAMOTO, NAOTAKA, YAMAMOTO, NAOTAKA, ISUZU AYASE NO. 2
Applicants: ISUZU MOTORS LTD, ISUZU MOTORS LIMITED
Application year: 1994
Main classification: C08J11
IPC codes: C08J11