Conductive in-mold coatings

Abstract: A thermosetting in-mold coating for molded fiber-reinforced plastic parts is disclosed. The binder for the thermosetting coating is comprised of least one polymerizable epoxy-based oligomer having at least two acrylate groups and at least one copolymerizable ethylenically unsaturated monomer. The coating includes graphite and titanium dioxide which results in the gray color. The coating composition has good flow and coverage during molding, good adhesion, uniform color, good surface quality, and good paintability.

Description: The present specification relates to thermosetting coating compositions, e.g. usable for in-mold coating of molded plastic such as polyester resin, vinyl ester resin, or poly(ethylene terephthalate) mouldings or parts. BACKGROUND Molded plastic parts can be in-mold coated with electrically conductive coatings. These parts can then be electrostatically painted. Conductive in-mold coatings using carbon black exclusively as the conductive pigment are black. When light coloured e.g. white paints are used, large amounts or multiple layers of the lighter coloured paints are required. An aim herein is to provide new and useful coating compositions, their preparation and use, and preferably enabling a lighter coloured conductive in-mold coating, requiring less light coloured paint for effective covering e.g. so that both time and materials may be saved. We have found that conductive in-mold coatings of lighter colour, such as grey, can be produced using graphite as part, a major portion or all of the conductive component and a lighter-coloured e.g. white pigment such as titanium dioxide to create a more light reflective surface. These in-mold coatings may be effectively painted with light coloured paints. Broadly, therefore, the invention provides in-mold coating compositions containing particulate graphite as a conductive filler (optionally in combination with carbon black) together with light-coloured e.g. white pigment. Corresponding methods of preparation and use are also included. The thermosetting coating compositions according to the invention are based upon a polymerizable epoxy-based oligomer having at least two acrylate (or methacrylate or ethacrylate) groups and are prepared by reacting acrylic acid, methacrylic acid, ethacrylic acid, with an epoxy based oligomer or resin such as bisphenol A epoxy, a tetrabromo bisphenol A epoxy, phenolic novalak epoxy, tetraphenylolethane epoxy, dicycloaliphatic epoxy and equivalents. Mixtures of these epoxy based oligomers can be used. The term (alkyl) acrylate shall be used to specify acrylate, methacrylate, or ethacrylate. Of these materials it is preferred to use a diacrylate terminated bisphenol A epoxy oligomer. They have weight average molecular weights of from about 500 to about 1,500. Such materials are well known to the art and to the literature, as for example, Cargill Resin 1570, a diacrylate ester of a liquid bisphenol A epoxy resin. Examples of other suitable materials can be found in "Heat Resistant Vinyl Ester Resin," M.B. Launikitis, Technical Bulletin, SC:116-76, Shell Chemical Company, June 1976 and Shell Chemical Company Technical Bulletins SC:16-76 and C:60-78. A copolymerizable ethylenically unsaturated monomer is used to copolymerize and to crosslink the polymerizable oligomers. Suitable monomers include styrene (preferred), alpha methyl styrene, vinyl toluene, t-butyl styrene, chlorostyrene, methyl methacrylate, diallyl phthalate (with styrene or methyl methacrylate and the like), triallyl cyanurate, triallyl isocyanurate, divinyl benzene, methyl acrylate and equivalents or mixtures thereof. The unsaturated monomer is usable in an amount of from 80 to 160 parts by weight and preferably from 80 to 120 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer. For further copolymerization and crosslinking and to improve hardness of the coating, there may be used in the in-mold coating composition a monoethylenically unsaturated compound having an group, at least one -NH 2 , -NH- or -OH group. Examples of such monomeric compounds are hydroxyl propyl methacrylate (preferred), hydroxyethyl methacrylate, hydroxy ethyl acrylate, hydroxy ethyl crotonate, hydroxypropyl acrylate, hydroxy polyoxypropylene acrylate, hydroxy polyoxypropylene methacrylate, hydroxy polyoxyethylene methacrylate, acrylamide, methacrylamide, N-hydroxymethyl acrylamide, N-hydroxymethyl methacrylamide, and mixtures of the same. These compounds are usable in an amount of from 10 parts to 120 parts by weight and preferably from 10 to 60 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer. Possible adhesion agents include various polymers or copolymers made from an alkyl methacrylate wherein the alkyl portion has from 1 to 6 carbon atoms, desirably from 1 to 4 carbon atoms, and preferably 1 or 2 carbon atoms, that is methyl or ethyl. Thus, preferred polymers include methyl methacrylate and ethyl methacrylate. The molecular weight of the polymers generally are given in terms of inherent viscosity, that is, inherent viscosity of a solution containing 0.25 grams of the polymer and 50 milliliters of methylene chloride measured at 20°C using a number 50 Cannon-Fenske viscometer. The inherent viscosity of such polymers is from about 0.15 to 1.3 and preferably from about 0.2 to 0.6. Such alkyl methacrylate polymers are known to the art and can be commercially obtained from DuPont under the mark "ELVACITE." Another adhesive agent which is preferred is polyvinyl acetate which has a molecular weight of from about 50,000 to 200,000 and preferably from about 80,000 to 150,000. The amount of the adhesion agent is typically up to 30 parts by weight, desirably up to 25 parts by weight, and preferably up to 20 parts by weight, per 100 parts by weight of the epoxy based polymerizable oligomer. As a mould release agent as well as a secondary cure accelerator, various zinc salts of fatty acids having at least 10 carbon atoms can be utilized. Fatty acids are well known. See "Organic Chemistry," Fieser and Fieser, D.C. Health and Company, Boston, 1944, pages 88, 381-390, 398 and 401, "Hackh's Chemical Dictionary," Grant, McGraw Hill Book Company, New York, 1969, page 261, and Whittington's Dictionary of Plastics," Whittington, Technomic Publishing Co., Inc., Stamford, Conn., 1968, pages 35, 102 and 261. Mixtures of zinc salts of the fatty acids can be used. Examples of some zinc salts are zinc palmitate, zinc stearate and zinc ricinoleate. It is preferred to use the zinc salt of a saturated fatty acid such as zinc stearate. The zinc salt is used in an amount from about 0.2 to 5 parts by weight and preferably from about 0.2 to 2.5 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer. Optionally and desirably a calcium salt of a fatty acid having at least 10 carbon atoms can also be used in the in-mould coating composition as a mold release agent and to control the rate of the cure. Fatty acids are well known such as those set forth hereinabove. Mixtures of calcium salts of the fatty acids can be used. Examples of some calcium salts are calcium stearate, calcium palmitate and calcium oleate. It is preferred to use the calcium salt of a saturated fatty acid like calcium stearate. These calcium salts can be used, from about 0.2 to 5 parts by weight of calcium salt per 100 parts by weight of the polymerizable epoxy based oligomer. An accelerator is used for the peroxide initiator and is a material such as a drier, e.g., cobalt octoate (preferred). Other materials which can be used are zinc naphthenate, lead naphthenate, cobalt naphthenate and manganese naphthenate. Soluble Co, Mn and Pb salts of linoleic acid, also, can be used. Mixtures of accelerators can also be used. The accelerator is used in an amount of from about 0.01 to about 1 part and preferably from about 0.01 to about 0.5 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer. Graphite in an amount from 5 to 150 parts, desirably from 20 to 85 parts, and preferably from 40 to 70 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer is used in the in-mould coating to give conductivity. The graphite can be any graphite, e.g. mined graphite or that produced synthetically. The mined graphites contain various impurities. The mined graphites useful in this embodiment typically have from 60 to 100 wt. percent graphite and 0 to 40 wt. percent ash, which is believed to be impurities. The preferred graphite has a small particle size to produce a smooth molding composition. The preferred graphites have particle sizes less than the pore size in 100 mesh screens (150 µm), desirably less than the pore sizes in 325 mesh screen (45µm), preferably an average particle size of from about 5 to about 30 µm, or said particle ideally being about 15 µm. Conductive carbon black can optionally be used in the composition. Conductive carbon black can significantly reduce the amount of graphite required to achieve conductivity. The amount of conductive carbon black used in the composition is typically up to about 15 parts, desirably up to about 10 parts, and preferably up to about 5 parts by weight based on 100 parts by weight of the polymerizable epoxy-based oligomer. A desirable amount of conductive carbon black is from about 2 to 10 percent, or about 5 percent by weight based upon the amount of graphite.Typically there is less black than graphite. Conductive carbon blacks are high structure carbon blacks such as Vulcan™ XC-72R from Cabot Corporation. They impart conductivity by creating a continuous carbon network which conducts electricity. Other conductive fillers can also be used. White pigments are used to lighten the color of the in-mould coating. Examples of white pigments that can be used with or without titanium dioxide are metal titanates, aluminium and calcium silicates, talcs, and particles with voids therein. The preferred white pigments are titanium dioxide and modified titanium dioxide pigments. One preferred titanium dioxide pigment is Zopaque™ RCL-9, a chloride process rutile type available from SMC Corp. A modified titanium dioxide is Zopaque™ RCL-2 also available from SCM, having a coating of alumina and silica oxides. As with the graphite, the pigments of small sizes such as diameters smaller than the pores of a 100 or 325 mesh screen are preferred. The white pigments are used in amounts from 5 to 120 parts, desirably from 10 to 80 parts, and preferably from 15 to 50 parts by weight per 100 parts of the polymerizable epoxy-based oligomer. A filler is desirablein the in-mould coating composition in an amount of from about to 20 to about 100 parts by weight and preferably from about 20 to about 80 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer. Examples of fillers are clay, MgO, Mg(OH) 2 , CaCO 3 , silica, calcium silicate, mica, magnesium silicate, aluminum hydroxide, barium sulfate, talc, hydrated silica, magnesium carbonate and mixtures of the same. The fillers should generally be of a small particle size. Of these fillers, talc is preferred. The fillers can be utilized to impart a desired viscosity and flow to the composition for molding and contribute to desired physical properties in the resulting thermoset in-mould coating. Fillers can also improve adhesion. However, care should be exercised in the use of high filler contents as this can yield high viscosities and result in flow and handling difficulties. Optionally, there is employed in the coating composition a copolymerizable or co-curable diacrylate compound having a weight average molecular weight of from about 250 to 5,000, in an amount of from about 5 to 120 parts by weight and preferably from about 5 to 60 parts by weight per 100 parts by weight of the polymerizable epoxy based oligomer. Such co-curable diacrylate compounds include (1) at least one polyoxyalkylene glycol based oligomer having two acrylate groups, and (2) at least one polyurethane based oligomer having two acrylate groups, and mixtures of (1) and (2). Although the above-noted amounts of (1) and (2) can be utilized, it has been found that it is desirable to eliminate such compounds or keep their amounts less than 5 parts by weight since they reduce hardness at high temperatures, e.g., at 149°C (300°F). Examples of said diacrylate compounds (1) include triethylene glycol diacrylate, tetraethylene glycol diacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol diacrylate, polypropylene glycol diacrylate, polyethylene glycol dimethacrylate or polyoxyethylene glycol dimethacrylate (preferred), polypropylene glycol diacrylate, and so forth, and mixtures thereof. These acrylates are made by reacting polyoxyalkylene glycols such as polypropylene ether glycol with acrylic acid and ethacrylic acid. Since some of these reactive difunctional materials can be made by reacting unsaturated acids and alcohols, they can contain some OH and/or COOH groups. Examples of diacrylate compounds (2) include a polyesterurethane diacrylate, a polyetherurethane diacrylate, a polyesteretherurethane diacrylate, or other polyurethane oligomer having two acrylate groups. These materials may be made by reacting a polyetherdiol (e.g., a polypropylene ether diol), a polyesterdiol (e.g., a polyethylene adipate diol), and/or a polyetherester diol (e.g., a polypropylene ether adipate diol) with a diisocyanate like tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, hexamethylene diisocyanate and the like in an amount sufficient to form a diisocyanate terminated polyurethane prepolymer which is then reacted with hydroxy propyl acrylate, hydroxy ethyl acrylate and hydroxy ethyl methacrylate to form the diacrylate terminated polyurethane oligomer or polymer. Mixtures of these acrylate terminated polyurethane oligomers can be used. The term "acrylate" as used here is intended to cover methacrylate and ethacrylates as well as acrylates. Of these materials it is preferred to use a diacrylate polyesterurethane oligomer. Acrylate terminated polyurethane oligomers, e.g., curable by light, ultraviolet, electric beam and/or infrared and so forth, are well known, and sometimes are referred to as irradiation or radiation curable materials. The diacrylate compounds (1) and/or (2), above, reduce the hardness of the in-mould coating. An organic free-radical initiator or a free radical generator (catalyst) such as a peroxide is used to catalyze the polymerization, copolymerization and/or crosslinking of the ethylenically unsaturated oligomers and the other ethylenically unsaturated materials. Examples of free-radical initiators, include tertiary butyl perbenzoate, tertiary butyl peroctoate in diallyl phthalate, diacetyl peroxide in dimethyl phthalate, dibenzoyl peroxide, butyl perisobutyrate, di(p-chlorobenzoyl) peroxide in dibutyl phthalate, di(2,4-chlorobenzoyl) peroxide with dibutyl phthalate, dilauroyl peroxide, methyl ethyl ketone peroxide, cyclohexanone peroxide in dibutyl phthalate, 3,5-dihydroxy-3,4-dimethyl-1,2-dioxacyclopentane, t-butylperoxy(2-ethyl hexanoate), caprylyl peroxide, 2,5-dimethyl-2,5-di(benzoyl peroxy) hexane, 1-hydroxy cyclohexyl hydroperoxide-l, t-butyl peroxy (2-ethyl butyrate), 2,5-dimethyl-2,5-bis(t-butyl peroxy) hexane, cumyl hydroperoxide, diacetyl peroxide, t-butyl hydroperoxide, ditertiary butyl peroxide, 3,5-dihydroxy-3,5-dimethyl-1,2-oxacyclopentane, 1,1-bis (t-butyl peroxy)-3,3,5-trimethyl cyclohexane and mixtures thereof. It is desirable sometimes to use mixtures of initiators to take advantage of their different decomposition rates and times at different temperatures and the like. A preferred initiator to use is tertiary butyl perbenzoate. The peroxide initiator should be used in an effective amount to overcome the effect of the inhibitor and to cause crosslinking or curing of the ethylenically unsaturated materials. In general, the peroxide initiator is used in an amount of up to about 5 percent and preferably up to about 2 percent, by weight based on the weight of the ethylenically unsaturated materials employed in the in-mould coating composition. The unsaturated materials mentioned above, thus, are used in an effective amount to provide on cure (e.g., polymerization, copolymerization and/or crosslinking) a thermoset composition. To prevent premature gelation of the ethylenically unsaturated materials and to provide for improved shelf-life or storageability inhibitors are added in the desired amount to the composition or are provided in the raw materials before use. Examples of inhibitors include hydroquinone, benzoquinone, p-t-butyl catechol and the like and mixtures thereof. Optionally, the in-mould composition can be compounded with other mould-release agents, antidegradants, UV absorbers, paraffin wax, solid glass or resin microspheres, thickening agents, low shrink additives and the like. These compounding ingredients should be used in amounts sufficient to provide satisfactory results with respect to their intended purpose. It is not desirable to use in the in-mould composition materials like butadiene-styrene block copolymers or fatty alcohol phosphates. For ease in handling, materials such as polyvinyl acetate may be dissolved in a reactive monomer like styrene. The viscosity of the oligomers can be reduced by dilution with styrene and the like. The ingredients of the composition should be readily mixed and handled at ambient or room temperature or temperatures below the polymerization temperature so that they may be readily pumped to and injected into the mould. The ingredients can be warmed or heated before or during mixing and mixed in steps to facilitate thorough mixing, dispersion and solution. Also, the bulk of the ingredients can be thoroughly mixed and the remainder including the catalyst separately mixed and then both can be pumped to a mixing head to be mixed together and then injected into the mould. With the peroxide initiator or catalyst the in-mould composition exhibits a shelf-life at room temperature (about 25°C) of several weeks, and without the initiator it exhibits a shelf life of several months at room temperature. Thus, the initiator is preferably added to the composition and thoroughly mixed therewith just before moulding. All of the ingredients of the coating composition should be kept dry or have a minimal amount of moisture or the water content should be controlled to obtain reproducible results and to prevent pore formation. Mixing of the ingredients of the composition should be thorough. Injection moulding, compression moulding, transfer moulding, or other moulding apparatus or machines can be used for the in-mould coating. Moulding apparatus and methods may be found in US-A-4,081,578. The coating composition can be applied to the substrate and cured at a temperature of from about 270° to 330°F (132 to 166°C) and at a pressure of about 500 to 1500 or about 1,000 psi (35 to 105 or 70 kg/cm 2 ) for from about 0.25 to 3 minutes. Processes and products disclosed herein may be used in the manufacture of automobile parts such as grille and headlamp assemblies, deck hoods, fenders, door panels and roofs as well as in the manufacture of parts for recreational all-terrain vehicles, motorized water vehicles, food trays, appliance and electrical components, furniture, machine covers and guards, bathroom components, structural panels and so forth. The moulded plastic substrate can be a moulded part or a glass fiber reinforced plastic (FRP) substrate based on thermoset resins or thermoplastic resins. The thermoset resins such as polyester resin or vinyl ester resin, to which the in-mould composition is applied, can be made from a sheet moulding compound (SMC) or a bulk moulding compound (BMC), or other FRP material as well as a high strength moulding composition (HMC) or a thick moulding compound. The FRP substrate can have from about 10 to about 75 percent and desirably from about 25 to 35 or from about 55 to 60 percent by weight of glass fibers. The glass fiber reinforced thermoset plastic (FRP) substrate can be rigid or semirigid. In lieu of glass fibers, other conventional fibers can also be utilized either separately, or in combination. Examples include carbon fibers, boron fibers, graphite fibers, nylon fibers, and the like. The substrate can contain flexibilizing polymers, e.g., contain a flexibilizing moiety such as an adipate group in the polyester, elastomers such as the styrene-butadiene block copolymers, plastomers, conventional impact modifiers and the like. Examples of unsaturated polyester glass fiber thermosets are set forth in "Modern Plastics Encyclopedia, 89," mid October 1988, Vol. 65, No. 11, McGraw-Hill, Inc., New York, pages 208-214, and in various Shell Chemical Company Technical Bulletins on vinyl esters, noted hereinabove. Examples of thermoplastic resin substrates include polyurethanes, polyesters, polycarbonates, polysulphones, polyamides, polyimides, polyacrylates, poly(alkylenes) and polyethers. Aromatic groups within these polymers would tend to increase their potential use temperature. We find that the compositions generally exhibit good pumpability and flow in the mould. They can give rapid cures as low as 12 to 50 seconds at 150°C (300°F). They also show good adhesion to paints and can be used not only as an in-mould coating to cover blemishes but as a good conductive coating for electrostatic painting and as a primer for most paint finish systems such as soluble acrylic lacquers, acrylic dispersion lacquers, water borne acrylic enamels, high solids solution acrylic enamels, acrylic non-aqueous dispersions and urethanes. The concepts will be better understood by reference to the following examples wherein parts noted are parts by weight unless otherwise indicated. EXAMPLES In-mould coating compositions were formulated as in Table I. The first 4 components were added to a reactor and blended with heating to 38°C. The next three ingredients were added and blended in using a high shear mixer. The carbon black, silica, diacrylate ester were then mixed in under high shear for 30 min. with heat until reaching 44°C. Once 44°C was reached, heating was discontinued and cooling was started. Then the last components were added and mixed for one hour at 38°C. Formulations 1 through 6 were prepared by this process. CONDUCTIVE IN-MOLD COATINGS Formulation: 1 2 3 4 5 6 85 wt. % Diactylate ester of bisphenol A Epoxy in 15 wt. % Styrene (100 parts oligomer) 117.65 117.65 117.65 117.65 117.65 117.65 Low Profile Additive 40 wt. % poly(vinyl acetate) in 60 wt. % styrene 25g 75g 25g 25g 25g 50g Hydroxylpropyl Methacrylate 30 30 30 30 30 30 Styrene 45.35 15.35 45.35 45.35 45.35 30.35 2 wt. % Benzoquinone in Styrene 7.0 7.0 7.0 7.0 7.0 7.0 Zinc Stearate 1.85 1.85 1.85 1.85 1.85 1.85 Calcium Stearate 0.45 0.45 0.45 0.45 0.45 0.45 Cobalt Hex-Chem 12 wt. % in Mineral Spirits 0.15 0.15 0.15 0.15 0.15 0.15 Carbon Black Vulcan™ XC-72R 8.5 9.0 8.5 2.0 2.0 3.0 Cab-O-Sil M-5 (silica) - - - - - 2.5 Hydrous Magnesium Silicate 80.0 50.0 80.0 40.0 40.0 30.0 #508 Graphite Powder 40.0 #8535 Graphite Powder 40.0 #8635 Graphite Powder 60.0 ZOPAOUE™ RCL-9TiO 2 30.0 30.0 20.0 20.0 20.0 Formulations 1-6 were then in-mould coated onto conventional fiberglass reinforced sheet-moulded thermoset polyester-styrene sheets having 25 wt. % glass fibers at 6.89 MNm -2 (1000 psi) and 149°C (300°F) for about 45 seconds. The tests on the in-mould coatings are shown in Table II. In-mould coatings A-F all showed good adhesion by a scalpel screening test, and excellent conductivity for electrostatic painting of >165 by the Ransberg meter reading. In-mould coating A which does not have TiO 2 pigment is used as a control and is black. In-mould coating B which has TiO 2 but no graphite is lighter in color than A but non-uniform in color and unacceptable as a grey primer coat. In-mould coating C which also has no graphite but more hydrous magnesium silicate is also non-uniform in color. In-mould coatings D, E, and F, which use three different graphites from two different suppliers, all produced uniform light grey coatings. PHYSICAL PROPERTIES OF IN-MOLD COATINGS In-Mold Coating A B C D E F Coating Formulation Used 1 2 3 4 5 6 Adhesion Good Good Good Good Good Good Conductivity @1.0 mil >165 >165 >165 >165 >165 >165 Color Black Non-uniform dark gray Non-uniform dark gray Uniform light gray Uniform light gray Uniform light gray

Claims: A thermosetting in-mould coating composition curable to form a grey conductive coating, comprising: at least one epoxy-based oligomer having at least two (alkyl)acrylate groups selected from acrylate, methacrylate and ethacrylate; copolymerisable ethylenically-unsaturated monomer; 5 to 150 parts by weight particulate graphite, and 5 to 120 parts by weight white pigment; the parts by weight being relative to the amount of epoxy-based oligomer as 100 parts. A composition according to claim 1 comprising from 20 to 85 parts by weight graphite. A composition according to claim 2 comprising from 40 to 70 parts by weight graphite. A composition according to any one of the preceding claims in which the average particle size of the graphite is in the range 5 to 30 µm. A composition according to any one of the preceding claims comprising from 10 to 80 parts by weight white pigment. A composition according to claim 5 comprising from 15 to 50 parts by weight white pigment. A composition according to any one of the preceding claims in which the white pigment is selected from titanium dioxide and modified titanium dioxide pigments. A composition according to any one of the preceding claims comprising conductive carbon black, in an amount not more than 10 parts by weight based upon 100 parts by weight of the epoxy-based oligomer. A composition according to claim 8 comprising not more than 5 parts by weight conductive carbon black. A composition according to any one of the preceding claims in which the epoxy-based oligomer has weight average molecular weight in the range 500 to 1500. A composition according to any one of the preceding claims in which the epoxy-based oligomer is di(alkyl)acrylate-terminated bisphenol A epoxy oligomer. A composition according to any one of the preceding claims in which the ethylenically-unsaturated monomer is styrene. A composition according to any one of the preceding claims comprising from 80 to 160 parts by weight of the ethylenically-unsaturated monomer. A composition according to claim 13 comprising from 80 to 120 parts by weight of the ethylenically-unsaturated monomer. A composition according to any one of the preceding claims comprising a monoethylenically unsaturated compound having a C=0 group and at least one -NH 2 , -NH- or -OH group. A composition according to claim 15 comprising from 10 to 120 parts by weight of the monoethylenically unsaturated compound. A composition according to claim 16 comprising from 10 to 60 parts by weight of the monoethylenically unsaturated compound. A composition according to any one of claims 15 to 17 in which the monoethylenically unsaturated compound is hydroxypropyl methacrylate. A composition according to any one of the preceding claims comprising from 20 to 100 parts by weight filler. A composition according to claim 19 in which the filler is selected from talc and hydrous magnesium silicates. A process comprising in-mould coating a moulded plastics substrate with a composition according to any one of claims 1 to 20. A process according to claim 21 in which the moulded plastics substrate is a thermoset or thermoplastics fibre-reinforced plastics (FRP) substrate. A process according to claim 22 in which the FRP substrate contains from 10 to 75 wt% fibres. A process according to any one of claims 21 to 23 comprising painting over the in-mould coating. A laminated product obtainable by a process according to any one of claims 21 to 24.

Inventors: COBBLEDICK DAVID S, REICHENBACH DONALD F, COBBLEDICK, DAVID S., REICHENBACH, DONALD F.
Applicants: GENCORP INC, GENCORP INC.
Application year: 1994
Main classification: C08F299
IPC codes: C09D163, B32B27, B32B7, C08J5, C08F290