PROCESS FOR PREPARING IMPROVED LITHOGRAPHIC PRINTING PLATES

Abstract: Provided herein is an improved process to prepare lithographic printing plates. An embodiment of the process comprises mechanical graining of the substrate surface, followed by electrochemical graining in an acid medium using a symmetrical alternating current in the range of 10-500 coulombs/dm<2>, and then conditioning of the surface by treating it with a solution of partially neutralized polyvinylphosphonic acid maintained in a pH range of about 2.5 to 6. Such a process yields lithographic plates with high adhesion, excellent contrast and reduced background toning.

Description: PROCESS FOR PREPARING IMPROVED LITHOGRAPHIC PRINTING PLATES FIELD OF THE INVENTION This invention discloses a process for preparing improved lithographic plates and improved lithographs prepared therefrom. BACKGROUND OF THE INVENTION The art of lithography is well known and is practiced commercially in several fields including, for example, the electronic industry, newspaper industry, magazines, and the like. The field of lithography has been extensively written and commented upon in several books and articles. See, for example, Kirk-Othmer, Encyclopedia of Chemical Technology, Vol. 19, p. 140, John Wiley & Sons (1982); ibid, Vol. 20, p. 161 (1982); and Encyclopedia of Polymer Science and Engineering, Vol. 13, p. 373, John Wiley & Sons (1988) . A typical lithographic printing plate comprises a substrate surface, typically made of aluminum, silicon and the like, with a photosensitive layer on top. The preparation of the lithographic printing plate generally comprises cleaning the aluminum base, roughening it to make it suitable to receive the layers that go on top, anodically oxidizing it, followed by conditioning the surface and depositing the photosensitive layer on top. If defects occur in any of these steps, the quality of the printing plate suffers. Thus, for example, when the conditioning process is not of optimum quality, it affects the sensitivity to the background in the printed images, resulting in "toning". Copending patent application, Serial number , filed of even date herewith, describes an improved process for conditioning and improving the hydrophilicity of the plate. The roughening ("graining") step is another area of concern in the lithographic industry. Traditionally roughening of aluminum plates is performed by electrochemical or mechanical process. The mechanical process includes processes such as ball graining, brush graining, and the like. Copending patent application, Serial No. _, filed of even date herewith, describes an improved process for mechanical roughening of lithographic plates, the improved process resulting in fewer number of scratches on the plates. Electrochemical graining process to roughen plates has been described, for example, in U. S. Patents 5,174,869; 4,824,757; 4,786,381; 4,746,591; 4,714,528; 4,576,686; 4,545,866; 4,533,444; 4,294,672 and 4,272,342. U.S. Patent No. 4,561,944 discloses a graining process which employs both mechanical graining and electrochemical graining. The electrochemical graining uses HCl, nitric acid or a mixture thereof and applies an unsymmetrical alternating current so that the ratio of the electricity during the cathodic period versus the anodic period is 1:1 to 2.5:1 and the quantity of electricity during the anodic period is 300 coulombs/dm 2 or less. Preferred alternating current has voltage during the anodic period lower than the voltage during the cathodic period. Despite improvements being made to such processes, problems are still seen with the quality of lithographic plates, particularly with background toning. Toning occurs when a photosensitive layer penetrates too deeply into the surface of the plate, resulting in inked areas of the non- imaged portion of the plate. Thus, it would be desirable to have a process whereby good quality lithographic plates can be produced without the above toning problem. It would also be desirable to have a process whereby th hydrophilicity of the non-image areas in the surface of printing plate substrates can be improved, thus improving th quality of images printed therefrom. SUMMARY OF THE INVENTION Applicants have discovered that improved lithographi plates are produced by a process comprising: a mechanical graining process, an electrochemical graining process and conditioning process, wherein the electrochemical graining is performed in a suitable acid medium with symmetrical alternating current in the range of about 10-500 coulombs/dm 2 , and wherein the conditioning is performed wit a solution of polyvinylphosphonic acid, or with a solution of polyvinylphosphonic acid suitably partially neutralized to b in the pH range of about 2.5 to 6.6. The preparation and us of suitable partially neutralized polyvinylphosphonic aci are described in copending patent application, Serial No. , referred to above. The inventive process not onl results in improved adhesion in the lithographic plates but also substantially improves the hydrophilicity of the non image areas in the surface as well as eliminates th background toning problem. This in turn results in printe images with excellent contrast, sharpness and brightness. DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention discloses process to prepare improved lithographic plates. Anothe embodiment includes improved lithographic printing plate prepared using the inventive process. The inventive proces comprises the steps of mechanical graining, electrochemica graining and conditioning of the substrate plate. The orde of the graining processes is preferably mechanical grainin first, followed by elctrochemical graining, in which case th mechanical graining produces a primary graining effect an the electrochemical graining produces a secondary grainin effect. Combining these steps with a suitable conditionin step produces a synergistic effect, yielding lithographi plates with excellent adhesion, contrast and no backgroun toning. The following description illustrates the advantages o using the inventive combination steps. For illustration, th primary graining described is mechanical, and the secondar graining is electrochemical, although the reverse may also b employed within the scope of this invention. The proces starts with a suitable substrate. Suitable substrates includ metal, silicon, and the like materials which are well know in the art. Suitable metals for lithographic use are steel, magnesium or aluminum and its alloys. Aluminum and its alloy are preferred because of their excellent mechanica properties and relatively light weight. Of particula interest are alloys which maintain the advantages of aluminu but offer mechanical strength to prevent cracking or tearin during long runs on printing presses. The substrate may be i the form of a plate, coil, web and the like. While th inventive process may be conceivably used on a wide variet of substrate materials, this description illustrates the us of the process with aluminum substrates. The aluminum substrate is first cleaned to remov milling oils and surface impurities. Cleaning may be done b a variety of solvent or aqueous alkaline treatments. Typical alkaline degreasing agents include: hot aqueou solutions containing alkalis such as potassium hydroxide, sodium hydroxide, trisodium phosphate, sodium silicate, an aqueous alkalis mixed with surfactants. Solvent typ degreasers such as trichloroethylene, 1,1,1 trichloroethane, perchloroethylene can be used but are less popular because o increasing environmental and health considerations. Th degreasing may be done by immersion, spray or vapor washin with the listed agents. The cleaned aluminum surface is then subjected to the mechanical graining process. Several mechanical graining processes are well known in the art may be used in the practice of the present invention. Such processes generally include ball graining, brush graining and the like. A suitable process is brush graining, wherein the lithographic substrate plate is generally brushed with a brush in a slurry comprising particles suitable for roughening the plate. For example, U.S. Patent No. 4,183,788 discloses a brush graining process wherein the lithographic base is grained with an aqueous slurry comprising unfused, platy crystalline alumina using a rotary brushing motion whose force is predominantly tangential to the surface of the base plate. Other processes use silica (quartz) as the particles. Copending patent application, Serial No. , filed of even date herewith, discloses a mechanical graining process which is preferred in the practice of the present invention. This brush graining process employs an aqueous slurry comprising a mixture of alumina and quartz, and results in advantages such as much fewer scratches on the plate than when using a slurry containing alumina alone. In this preferred process, the graining is done using one or more brushes in an aqueous slurry comprising a mixture of fine alumina and fine quartz. The terms "fine alumina" and "fine quartz" respectively refer to alumina and quartz particulates with a mean particle size generally in the range of about 1-20 microns, preferably about 1-10 microns and typically about 3-6 microns, as measured by the Microtrac instrument (supplied by Leeds and Northrup, St. Petersburg, Florida) . The amount of quartz in the mixture of alumina and quartz generally ranges from about 5-95 weight %, preferably about 5-50 weight % and typically about 10-20 weight %. The particulate alumina used in the invention is unfused, anhydrous, crystalline alumina having a plate-like or tablet-like particle configuration. The flat dimension is generally three to five times greater than the thickness. This form of alumina can be obtained from hydrated alumina but is generally made from α-alumina trihydrate. Alumina useful in the practice of the invention is commercially available from suppliers such as, for example, Alcoa Surface Treatments, Bauxite, Arkansas. The particulate quartz used in the present invention has an angular configuration. Useful grade quartz is commercially available from Agsco Corporation, Hasbrouk heights, New Jersey. To form the mechanical graining medium, alumina and quartz are mixed in the desirable ratio described above, and made into a slurry in water. The solids concentration in the aqueous abrasive slurry is generally about 5-50 weight %, preferably about 10-40 weight % and typically in the range 15-30 weight %. The alumina and quartz may be first mixed together and then mixed with the water to prepare the slurry; alternatively, the two particulate materials may be added one after the other, in any order, to the water, to form the slurry. During the graining process, the slurry is kept in a continuously agitated condition. The mechanical graining of the aluminum base plate may be done by the brush graining technique. Conventional methods generally employ a plurality of rotating brushes. U. S. Patent No. 4,183,788, referred to above, describes such a process whereby the graining is done while applying a rotary brushing motion whose force vector is predominantly tangential to the surface of the aluminum, using a plurality of brushes. While the instant invention may be practiced using such conventional processes, inventors have found that use of a single brush moving counter to the base plate as disclosed in the afore-mentioned copending patent application, Serial No. , is generally adequate and also results in a superior quality grained plate. Whichever brushing technique is used, generally a mea roughness of about 0.2 to about 1.0 Ra is produced in typical graining process. Ra is a measurement of averag roughness of the surface and is defined as the arithmeti average of all departures of the roughness profile from th center line within the desired evaluation length. After the primary graining is done mechanically a described above, it is followed by electrochemical grainin of the plate. As in the case of the mechanical graining, th electrochemical graining may also be done by conventiona methods. For example, U.S. Patents 5,174,869 and 5,114,82 describe suitable elctrochemical graining processes. preferred process for the present invention employs an aci medium such as, for example, nitric acid, hydrochloric acid, mixtures thereof and the like. An electrolyte such as, fo example, aluminum nitrate is added to the medium. The proces employs symmetrical alternating current generally in th range of about 10-500 coulombs/dm 2 , preferably about 10-30 coulombs/dm 2 and typically about 20-200 coulombs/dm 2 . Th concentration of the acid is generally in the range of abou 2-50 g/1, preferably about 5-25 g/1 and typically about 10-2 g/1. The concentration of the electrolyte is generally in th range of about 10-200 g/1, preferably about 25-150 g/1 an typically about 40-80 g/1. After the graining step is completed, the substrat plate may be further processed through a series of steps. Some such further processing steps may include etching, rinsing, anodizing, conditioning, coating with photosensitive layer, and the like. Copending paten application, Serial No. , filed of even dat herewith, describes some of these steps. Sometimes it i advantageous to have the etching step immediately followin the primary graining step, but before the secondary grainin step. If etching of the substrate is desired, the substrate may be optionally etched in aqueous caustic or acid baths to remove surface deposits generated by graining and aerial oxide formed on the labile aluminum surface. Etching is followed by rinsing. Steps following surface roughening are preferably, though not exclusively, done with the metal kept wet. The metal surface may then be optionally anodized ("oxidized") to improve surface hardness and wear resistance of the final product. Anodization is typically carried out in aqueous inorganic electrolyte baths where the aluminum surface acts as the anode in an electrochemical process. Preferred electrolytes are the strong acids such as sulfuric and phosphoric. Organic acids and mixtures may additionally be used to impart specific properties to the final product. Anodization is generally performed at temperatures between ambient to about 212°F, as is well known to those skilled in the art. Generally an oxide weight of about 0.25-3.5 gram/m 2 is built on the surface in a typical lithographic plate process. The anodized plate is then rendered more hydrophilic by a conditioning ("sealing") process. U.S. Patent No. 4,153,461 discloses the use of polyvinylphosphonic acid ("PVPA") as a conditioning agent. Copending patent application, Serial No. , referred to above, describes an improved conditioning process which comprises using a conditioning reagent comprising PVPA solution partially neutralized to, and maintained at, a pH of about 2.5 to 6.6. Such an improved conditioning process renders the surface more hydrophilic, thereby requiring fewer number of sheets to clean out when the lithographic printing plate is ultimately utilized to make prints. Following the above conditioning step, the substrate may be rinsed with water, then dried with forced hot air, and then coated with a photosensitive layer. Photosensitive layers are made from photosensitive compounds that may be optionally mixed with suitable additives such as, for example, binder resins, photoinitiators, colorants, acid stabilizers, exposure indicators, surfactants and the like, known to those skilled in the art. Photosensitive compounds ("light sensitive compounds") useful in the practice of the invention include, for example, those described, in U.S. Patent Nos. 3,849,392; 3,867,147; 4,157,918, and 4,183,788. Additives that may be used in combination with such light sensitive compounds include those described in U.S. Patent No. 3,679,419. Photosensitive compounds are of two types: positive and negative working types. Positive types are those where the area of the plate exposed by light radiation through a mask are removed in the development step. In negative types, the exposed areas are hardened and remain after development. Positive working photosensitive materials suitable in the practice of the invention are iminoquinone diazides, ortho-quinone diazides and the like, which contain sulfonic acid esters of such diazides, prepared by reacting the appropriate sulfonyl chlorides with one or more labile aromatic hydroxyl groups. Preferred are the ortho-quinone diazides containing the above-described sulfonic acid ester groups. These esters undergo a photo Wolff rearrangement whereby loss of nitrogen is followed by a ring contraction and generation of a carboxylic acid which is easily removed using alkaline developing solutions. Several such positive acting compounds are described in, for example, U.S. Patents 3,175,906 and 4,157,918. Negative type photosensitive materials are generally made by using the photo-labile crosslinking capabilities of oligomeric compounds such as, for example, the diazoniu compounds, or the photo-polymerization of reactive monomers, or a combination of both. Several are described, for example, in U.S. Patent Nos. 3,849,392; 3,867,147; 4,157,918; 4,183,788 and 5,200,291. These are generally free radical polymerizations which are inhibited by oxygen. Oxygen barrier coatings are generally made atop the photosensitive coating to prevent interference from aerial oxygen when using negative photopolymer products. Generally, the photosensitive layer is selected based on the actinic radiation that is going to be used for exposure, as is known to those skilled in the art. The present invention may be practiced with both positive and negative type photosensitive materials. The light sensitive compound may optionally be mixed with additives as described above to form a photosensitive coating material, if so desired. For example, acid stabilizers may be used with diazonium compounds; suitable acid stabilizers are generally organic or inorganic acids. Examples include phosphoric, citric, benzoic, m-nitrobenzoic, p-toluenesulfonic, and the like as well as mixtures thereof. Preferably, the acid stabilizer is phosphoric acid. When used, the acid stabilizer is present generally in the amount of from about 0.02 % to about 2 %, and preferably from about 0.05 % to about 1.0 % based on the weight of the composition. Exposure indicators (or photoimagers) which may be useful in conjunction with the present invention include 4- phenylazodiphenylamine, eosin, azobenzene, Calcozine Fuchsine dyes and Crystal Violet and Methylene Blue dyes. Preferably, the exposure indicator is 4-phenylazodiphenylamine. The exposure indicator, when one is used, is preferably present in the composition in an amount of from about 0.01% to about 0.35% by weight. A more preferred range is from about 0.02% to about 0.30% and, most preferably, the exposure indicator is present in an amount of from about 0.02% to about 0.20%, although the skilled artisan may use more or less as desired. Colorants useful herein include dyes such as Rhodamine, Calcozine, Victoria Blue and methyl violet, and such pigments as the anthraquinone and phthalocyanine types. Generally, the colorant is present in the form of a pigment dispersion which may comprise a mixture of one or more pigments and/or one or more dyes dispersed in a suitable solvent or mixture of solvents. When a colorant is used, it is preferably present in the composition of this invention in an amount of from about 2.0% to about 35.0% by weight, more preferably from about 5.0% to about 30.0% and most preferably from about 5.0% to about 20% although the skilled artisan may use more or less as desired. Resin binders may be used in the coating to increase the functional lifetime of the printing plates. If resin binders are desired, suitable binder resins are chosen based upon their compatibility with other coating components, the ability to be cleaned away during the development step in non-image areas of the plate and their resistance to wear on press. Resins with acid end groups are especially desirable since the acid helps stabilize the coatings based upon diazonium compounds and provides alkaline solubility for development. In order to form a coating composition for the production of the photosensitive layer, the light sensitive compound is coated from a solution in a suitable solvent, wherein the light sensitive compound is present in amounts such that the concentration of the light sensitive compound is generally in the range 10-100% of the total solids in the dried coating upon drying (see below) , preferably in the range 30-75%, and typically in the range 40-60%. Suitable solvents for this purpose include water, tetrahydrofuran, butyrolactone, glycol ethers such as propylene glycol monomethyl ether and methyl cellosolve, alcohols such as ethanol and n-propanol, and ketones such as methyl ethyl ketone, or mixtures thereof. Preferably, the solvent comprises a mixture of propylene glycol monomethyl ether and butyrolactone. In general, after the solution is applied to an appropriate substrate by a suitable coating process, the solvent system is evaporated from the coating by a suitable drying process; some insignificant amount of solvent may, however, remain as residue. The process to coat the light sensitive layer may be a batch or continuous process as is known to those skilled in the art. Some useful coating processes include dip coating, roller coating, slot type coating, spin coating, and the like, which deposit a thin uniform dry photosensitive coating on the surface once the solvents have been driven off. At the end of the coating operation and drying, generally a coating weight of from about 0.5g/m 2 to about 2.5g/m 2 , preferably from about 0.8 g/m 2 to about 2.0 g/m 2 and typically about 1.0 g/m 2 is obtained. The advantages of the instant invention may generally be tested at this stage. An important criterion for the performance of the printing plate is the number of sheets needed for cleanout during use. The fewer the number of sheets that are required to clean out the better is the performance of the printing plate. The number of sheets needed for cleanout and to give acceptable impressions may be tested by a toning test in a dry scum cycle using Kohl Madden magenta ink and RC651 fountain solution. Typical experiments using the inventive combinations of mechanical and electrochemical graining and conditioning steps generally yield plates which require less than 50 sheets for cleanout, whereas experiments employing mechanical graining only combined with a conditioning step yielded plates requiring at least 100 sheets for cleanout. In a process to prepare improved lithographic plates according to another embodiment of the present invention, the photographic element prepared as described above is then exposed to suitable actinic radiation through a negative mask so as to yield a solid 5 on a 21 step Stouffer exposure wedge (supplied by Stouffer Graphic Arts Equipment Company, South Bend, Indiana) after development. Generally a radiation in the range of 300-400 nm is employed. The exposed plate is then developed with a suitable developer. Suitable developer may be aqueous developer, or aqueous developer mixed with a suitable organic solvent. An aqueous developer useful in the present invention comprises an aqueous solution containing one or more of the following groups: (a) a sodium, potassium or lithium salt of octyl, decyl or dodecyl monosulfate; (b) a sodium, lithium, potassium or ammonium metasilicate salt; (c) a lithium, potassium, sodium, or ammonium borate salt; (d) an aliphatic dicarboxylic acid, or sodium, potassium or ammonium salt thereof having from 2 to 6 carbon atoms; and (e) mono-, di-, or tri-sodium, or -potassium phosphate. Other suitable developers include water, benzoic acid or sodium, lithium and potassium benzoates and the hydroxy substituted analogs thereof as well as those developers described in U. S. Patent No. 4,436,807. In conventional use, the developed plate is finished with a subtractive finisher such as a hydrophilic polymer. Examples include cold water soluble dextrin and/or polyvinyl pyrrolidone, a nonionic surfactant, a humectant, an inorganic salt and water, as taught by U. S. Patent No. 4,213,887. For the purpose of improving the press performance of a plate prepared as described above, it is known that baking of the exposed and developed plate can result in an increase in the number of quality impressions over that otherwise obtainable. To properly bake the plate, it may be first treated with a suitable solution designed to prevent loss of hydrophilicity of the background during baking. An example of a suitable solution is disclosed in U. S. Patent No. 4,355,096. The plate prepared as above may then be heat treated by baking at temperature of from about 180"C up to the annealing temperature of the substrate, preferably about 240 * C. The effective baking time is inversely proportional to the temperature and averages in the range of from about 2 to about 15 minutes. The following Examples are illustrative of the invention but it is understood that the invention is not limited thereto. EXAMPLES B-x-a pie 1. Process using mechanical graining only; comparative example: A degreased aluminum substrate (web of 1050 alloy) was mechanically roughened by brushing it with a single 24 inch diameter brush rotating at 250 rpm counter to the web direction while using a slurry made of fine grade alumina (~5 micron mean article size) and fine grade quartz (~5 micron) (70:30 weight ratio of alumina to quartz) at 15% solids concentration as the abrasive medium. The substrate was then etched, anodized and conditioned with polyvinyl phosphonic acid as described in U.S. Patent No. 4,153,461. Then the substrate was coated with a light sensitive coating. The light sensitive coating consisted of a diazo resin which is the polycondensation product of 3-methoxy-4-diazo diphenyl amine sulfate and 4,4'-bismethoxy methyl-diphenyl ether, precipitated as mesitylene sulfonate, described in U.S. Patent 4,157,918, and a modified polyvinylacetal resin described in U.S. Patent 4,940,646. The coated plate was subjected to a toning test in a dry scum cycle using Kohl Madden magenta ink (Supplied by Kohl Madden Corp., Lodi, New Jersey and RC651 fountain solution (Supplied by Hoechst AG Kalle Werk, Wiesbaden, Germany) . The control plate took more than 100 sheets to provide acceptable print impressions. w-x-awipies 2-8 demonstrate the inventive process practiced under various conditions within the scope of the present invention. p -Trampi-■> 9 , Demonstration of the improved inventive process: A 1050 aluminum alloy web was degreased, mechanically grained as in Example 1 and etched. The mechanically grained and etched substrate web was then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The electrochemical graining was performed using nitric acid and aluminum nitrate under the following conditions: Nitric acid concentration: 15.5 g/1 Aluminum nitrate concentration: 60.0 g/1 A.C. graining current: 30 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) was anodized to an oxide weight of 1.4 g/m 2 and the surface was then sealed with polyvinylphosphonic acid as in Example 1. The sealed substrate was coated with a light sensitive coating as described in Example 1. The coated plate was tested for a toning test as described in Example 1. This test plate took 40 sheets to provide acceptable print impressions. ExamBle__3: A 1050 aluminum alloy web was degreased, mechanically grained and etched. The mechanically grained and etched substrate web was then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The secondary grain structure was obtained under the following conditions: Nitric acid concentration: 14.5 g/1 Aluminum nitrate concentration: 50.0 g/1 A.C. graining current: 75 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) was anodized to an oxide weight of 1.4 g/m 2 and the surface was then sealed with polyvinylphosphonic acid. The sealed substrate was coated with a light sensitiv coating as described in Example 1. The coated plate was tested for a toning test as described in Example 1. This test plate took 40 sheets to provide acceptable print impressions. Examp_le__4: A 3103 aluminum alloy web was degreased, mechanically grained and etched. The mechanically grained an etched substrate web was then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The secondary grain structure was obtained under the following conditions: Nitric acid concentration: 16.5 g/1 Aluminum nitrate concentration: 70.0 g/1 A.C. graining current: 150 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) was anodized to an oxide weight of 1.4 g/m 2 and the surface was then sealed with polyvinylphosphonic acid. The sealed substrate was coated with a light sensitive coating as described in Example 1. The coated plate was tested for a toning test as described in Example 1. This test plate took 40 sheets to provide acceptable print impressions. Example 5: A 3103 aluminum alloy web was degreased, mechanically grained and etched. The mechanically grained and etched substrate web was then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The secondary grain structure was obtained under the following conditions: Nitric acid concentration: 14.5 g/1 Aluminum nitrate concentration: 50.0 g/1 A.C. graining current: 255 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) was anodized to an oxide weight of 1.4 g/m 2 and the surface was then sealed with polyvinylphosphonic acid. The sealed substrate was coated with a light sensitive coating as described in Example 1. The coated plate was tested for a toning test as described in Example 1. This test plate took 40 sheets to provide acceptable print impressions. wvampio fi » A 1050 aluminum alloy web was degreased, mechanically grained and etched. The mechanically grained and etched substrate web was then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The secondary grain structure was obtained under the following conditions: Nitric acid concentration: 15.0 g/1 Aluminum nitrate concentration: 40.0 g/1 A.C. graining current: 375 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) was anodized to an oxide weight of 1.4 g/m 2 and the surface was then sealed with polyvinylphosphonic acid. The sealed substrate was coated with a light sensitive coating as described in Example 1. The coated plate was tested for a toning test as described in Example 1. This test plate took 40 sheets to provide acceptable print impressions. Examp_le_7: A 1050 aluminum alloy web was degreased, mechanically grained and etched. The mechanically grained and etched substrate web was then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The secondary grain structure was obtained under the following conditions: Nitric acid concentration: 15.0 g/1 Aluminum nitrate concentration: 80.0 g/1 A.C. graining current: 500 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) was anodized to an oxide weight of 1.4 g/m 2 and the surface was then sealed with polyvinylphosphonic acid. The sealed substrate was coated with a light sensitive coating as described in Example 1. The coated plate was tested for a toning test as described in Example 1. This test plate took 40 sheets to provide acceptable print impressions. T- jy ampi a fl• A 1050 aluminum alloy web is degreased, mechanically grained and etched. The mechanically grained and etched substrate web is then grained with alternating current in nitric acid to form a secondary grain on top of primary mechanical grain. The secondary grain structure is obtained under the following conditions: Nitric acid concentration: 15.5 g/1 Aluminum nitrate concentration: 60.0 g/1 A.C. graining current: 30 Coulombs/dm 2 The web having combo grain (mechanical grain + electrochemical grain) is anodized to an oxide weight of 1.4 g/m 2 and the surface is then sealed with partially neutralized polyvinylphosphonic acid (PVPA neutralized with sodium hydroxide to a pH of 4.5). The sealed substrate is then coated with a light sensitive coating as described in Example 1. The coated plate is tested for a toning test as described in Example 1. This test plate takes about 20 sheets to provide acceptable print impressions.

Claims: CLAIMS What is claimed is: 1. A process to prepare a lithographic printing plate, comprising the steps of: (a) providing a substrate made of a suitable metal; (b) graining said substrate mechanically; (c) graining said substrate electrochemically in a suitable acid medium with symmetrical alternating current in the range of about 10-500 coulombs/dm 2 ; (d) conditioning said surface with a conditioning agent selected from either polyvinylphosphonic acid or partially neutralized polyvinylphosphonic acid, wherein said partially neutralized polyvinylphosphonic acid is maintained at a pH in the range of about 2.5 to 6; (e) applying a photosensitive layer; (f) exposing said photosensitive layer to suitable actinic radiation; and (g) developing said exposed layer in a suitable developer. 2. The process as described in claim 1, wherein said substrate is made of aluminum or steel . 3. The process as described in claim 1, wherein said substrate is made of aluminum. 4. The process as described in claim 1, wherein said mechanical graining in step (b) comprises brush graining in an aqueous slurry comprising a mixture of alumina particulates . 5. The process as described in claim 1, wherein said mechanical graining step comprises brush graining in an aqueous slurry comprising a mixture of quartz particulates. 6. The process as described in claim 1, wherein said mechanical graining step comprises brush graining in an aqueous slurry comprising a mixture of particulates, wherein said mixture comprises alumina and quartz in a weight ratio in the range 95:5 to 5:95 and wherein said particulates have particle size in the range 1-20 microns. 7. The process as described in claim 6, wherein said aqueous slurry has a solids concentration of about 5-50 weight percent. 8. The process as described in claim 1, wherein said acid medium in step (c) comprises nitric acid, hydrochloric acid or mixtures thereof. 9. The process as described in claim 1, wherein said acid medium in step (c) comprises nitric acid. 10. The process as described in claim 1, wherein said acid medium in step (c) comprises hydrochloric acid. 11. The process as described in claim 1, wherein said symmetrical alternating current in step (c) is in the range of about 10-300 coulombs/dm 2 . 12. The process as described in claim 1, wherein said symmetrical alternating current in step (c) is in the range of about 20-200 coulombs/dm 2 . 13. The process as described in claim 1, wherein said photosensitive layer in step (e) comprises a photosensitive compound of positive type. 14. The process as described in claim 1, wherein said photosensitive layer comprises a photosensitive compound of negative type. 15. The process as described in claim 13, wherein said positive photosensitive compound is a sulfonic acid ester of an ortho-quinone diazide. 16. The process as described in claim 14, wherein said negative photosensitive compound is a diazonium compound. 17. The process as described in claim 16, wherein said diazonium compound is a polycondensation product of 3- methoxy-4-diazo diphenyl amine sulfate and 4, 4 ' -bismethoxy methyl-diphenyl ether, precipitated as mesitylene sulfonate. 18. The process as described in claim 1, wherein said actinic radiation in step (f) has a wavelength range 300-400 n . 19. The process as described in claim 1, wherein said developer in step (g) is an aqueous developer selected from the group consisting of sodium octyl monosulfate, potassium decyl monosulfate, lithium dodecyl monosulfate and combinations thereof. 20. A process to prepare a lithographic printing plate, comprising the steps of: (a) providing an aluminum substrate; (b) graining said substrate mechanically in an aqueous slurry comprising a mixture of particulates, wherein said mixture comprises alumina and quartz in a weight ratio in the range 95:5 to 5:95 and wherein said particulates have particle size in the range 1-20 microns; (c) graining said substrate electrochemically in a suitable acid medium with symmetrical alternating current in the range of about 10-500 coulombs/dm 2 , • (d) conditioning said surface with polyvinylphosphonic acid as the conditioning agent; (e) applying a photosensitive layer; (f) exposing said photosensitive layer to suitable actinic radiation; and (g) developing said exposed layer in a suitable developer. 21. The process as described in claim 20, wherein said acid medium in step (c) is nitric acid. 22. The process as described in claim 20, wherein said alternating current in step (c) is in the range of 10-300 coulombs/dm 2 . 23. A process to prepare a lithographic printing plate, comprising the steps of: (a) providing an aluminum substrate; (b) graining said substrate mechanically in an aqueous slurry comprising a mixture of particulates, wherein said mixture comprises alumina and quartz in a weight ratio in the range 95:5 to 5:95 and wherein said particulates have particle size in the range 1-20 microns; (c) graining said substrate electrochemically in a suitable acid medium with symmetrical alternating current in the range of about 10-500 coulombs/dm 2 ,* (d) conditioning said surface with partially neutralized polyvinylphosphonic acid as the conditioning agent wherein said partially neutralized polyvinylphosphonic acid has a pH in the range of about 2.5 to 6,* (d) applying a photosensitive layer; (e) exposing said photosensitive layer to suitable actinic radiation; and (f) developing said exposed layer in a suitable developer. 24. The process as described in claim 23, wherein said acid medium in step (c) is nitric acid. 25. The process as described in claim 23, wherein said alternating current in step (c) is in the range of 10-300 coulombs/dm 2 . 26. A lithographic printing plate prepared by the process described in claim 1. 27. A lithographic plate prepared by the process described in claim 20. 28. A lithographic plate prepared by the process described in claim 23.

Inventors: DHILLON MAJOR S, KING DENNIS A, LOVELAND ALLEN W, SPRINTSCHNIK GERHARD, WANAT STANLEY F, DHILLON, MAJOR, S., KING, DENNIS, A., LOVELAND, ALLEN, W., SPRINTSCHNIK, GERHARD, WANAT, STANLEY, F.
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1994
Main classification: B41N3
IPC codes: B41N3, G03F7