Means for stabilizing deproteinized natural rubber latex

Abstract: A means for stabilizing a deproteinized natural rubber latex is disclosed, comprising adding a stabilizer selected from the group consisting of (a) an anionic surfactant, (b) an amphoteric surfactant, (c) a nonionic surfactant, (d) a nonionic or amphoteric oligomer or polymer, and (e) an anionic oligomer or polymer. By adding the stabilizer, the mechanical stability of a deproteinized natural rubber latex can be markedly improved.

Description: This invention relates to a means for stabilizing a deproteinized natural rubber latex. Natural rubber has hitherto been used widely as industrial products, such as automobile tires, belts and pressure-sensitive adhesives, and household goods, such as gloves. These natural rubber articles are generally produced by coagulating the rubber content of a natural rubber latex to obtain raw rubber called crepe rubber or smoked sheet rubber, and further processing the raw rubber through steps of mastication, compounding of additives, molding, and vulcanization. It was recently reported that medical tools made of natural rubber, such as surgical gloves, various catheters, and analgesic masks, provoke labored respiration or anaphylactoid symptoms, such as vascular edema, nettle rash, detelectasis and cyanosis, in patients. Cases were also reported in which women with a history of allergy suffered a pain in the hands, nettle rash or vascular edema around the eyes when they used rubber gloves made of natural rubber. These symptoms seem to be attributed to the protein present in natural rubber. Food and Drug Administration (FDA), U.S.A. has called on manufactures of natural rubber articles to reduce the protein content. It has therefore been demanded to remove protein from natural rubber. Natural rubber is obtained from Hevea trees as a latex containing a rubber content, water, protein, inorganic salts, and other impurities. The latex oozing out from the tapped trunk of a rubber plant is collected in a cup, gathered at a refining factory where it is coagulated to obtain raw rubber (crepe rubber or smoked sheet rubber) or concentrated by centrifugation to obtain a purified latex. The protein content in natural rubber has usually been expressed in terms of a nitrogen content (N %) determined by a Kjeldahl method multiplied by 6.3. The present inventors discovered that the proteins in raw rubber obtained from a latex can be confirmed by infrared absorption at 3280 cm -1 characteristic of polypeptide. The present inventors previously found that a deproteinized natural rubber latex showing no IR absorption at 3280 cm -1 can be obtained by a process comprising treating a natural rubber latex with a protease and a surfactant either simultaneously or successively and, after allowing the system to stand for a given period of time, recovering the rubber content by centrifugation (see Japanese Patent Application Nos. 208754 to 208758/92 (corresponding to EP-A-0 584 597)). General natural rubber latex on the market are stable (not coagulated) against mechanical stimulation, such as vigorous stirring or friction. Such stability of latex is measured as mechanical stability (JIS K-6381). The above-mentioned deproteinized latex has a disadvantage in that the mechanical stability is seriously poorer than general latex on the market. While the reason for the serious reduction in mechanical stability has not yet been clarified, it is considered that the protein contained in general latex is adsorbed by rubber particles and assumes strong negative charges under a condition made alkaline by ammonia addition so that the rubber particles are present in the latex in a considerably stabilized state. To the contrary, not containing such protein acting as a protective layer, the deproteinized latex seems to be labile and apt to undergo agglomeration on receipt of mechanical stimulation. Additionally, the surfactant which has been used for protein removal is almost removed by subsequent centrifugation and scarcely remains in the deproteinized latex. A.D. Roberts, Natural Rubber Science and Technology, 1990, p. 102-103, discloses that the stability of natural latex may be enhanced by the addition of e.g. potassium, sodium or ammonium salts of fatty acids having from 8 to 18 carbon atoms. It is stated that the use of anionic surfactants other than fatty acid soaps is much more limited and that non-ionic surfactants of the ethylene oxide condensate type are not widely used in latex technology, but have limited applications. Accordingly, an object of the present invention is to provide a means for stabilizing a deproteinized natural rubber latex free from a fear of eliciting allergy, by which the mechanical stability of a deproteinized natural rubber latex can be improved. The present invention relates to use of sodium polyoxyethylene (3) dodecyl ether sulfate or an alkylbenzene sulfonate having an alkyl moiety of from 8 to 20 carbon atoms as a stabilizer for a deproteinized natural rubber latex. The present invention also relates to a method for stabilizing a deproteinized natural rubber latex comprising adding to the deproteinized natural rubber latex sodium polyoxyethylene (3) dodecyl ether sulfate or an alkylbenzene sulfonate having an alkyl moiety of from 8 to 20 carbon atoms in an amount to give a concentration of from 0.01 to 10 % by weight based on the total weight of the latex. The solid content of the latex is normally from 5 to 60 % by weight. The stabilizer according to the present invention is added to a deproteinized natural rubber latex so as to give a concentration of from 0.01 to 10 % by weight, and preferably from 0.1 to 5 % by weight based on the total weight of the latex. If the concentration of the stabilizer is less than 0.01 %, sufficient stabilizing effect may not be obtained. Concentrations exceeding 10 % are uneconomical. The present invention will now be illustrated in greater detail with reference to Examples. All the percents and ratios are given by weight unless otherwise noted. EXAMPLES AND COMPARATIVE EXAMPLES A high ammonia latex of natural rubber was treated with a protease (alkali protease) and a surfactant (a 60:40 mixture of sodium dodecylbenzenesulfonate and polyoxyethylene (9 mol) lauryl ether) to prepare a deproteinized natural rubber latex showing no polypeptide absorption at 3280 cm -1 in the IR spectrum. Each of the stabilizers shown in Table 1 below was added thereto in the concentration shown therein, and the total solids content was adjusted to 55±0.2 % to obtain a stabilized deproteinized natural rubber latex. The mechanical stability of the resulting latex was evaluated according to the following test method (JIS K 6381). For comparison, a latex prepared by adding sodium laurylsulfate to a concentration of 0.005 % as a stabilizer and, as a control, a latex containing no stabilizer were tested in the same manner. The results obtained are shown in Table 1. The Examples 1 to 12 and 15 to 17 are for comparison purposes, whilst the Examples 13 and 14 are the Examples of the present invention. Mechanical Stability Test Method: A latex is put in a sample container and vigorously agitated by rotating a shaft at a prescribed speed. The mechanical stability is represented by the time (MST; sec) from the start of agitation to the end point where a visually distinguishable aggregate begins to form. In general, a latex having an MST of not less than 500 seconds is regarded stable. Example No. Stabilizer Concentration (wt.%) MST (sec) 1 Sodium laurylsulfate (Emal 10 powder* 1 ) 1.0 1200 2 Potassium oleate (FR-14* 2 ) 0.5 600 3 Sodium dodecylbenzenesulfonate (Neopelex F-65* 3 ) 0.5 1300 4 Polyoxyethylene (9) nonylphenyl ether (Emulgen 909* 4 ) 3.0 1100 5 Polyoxyethylene (20) sorbitan oleyl ester (Rheodor TWO-120* 5 ) 5.0 1400 6 Sodium lauryl phosphate 2.0 1000 7 Hexaglycerin monooleate (polymerization degree: 6) 2.5 900 8 Polyoxyethylene (10) monooleate (Emanon 4110* 6 ) 3.0 1200 9 Laurylglucoside 1.0 700 10 Sodium salt of formalin-naphthalenesulfonic acid condensate (Demol N* 7 ) (number of condensation (n) =5) 1.0 800 11 Lauryl acetobetaine (Amphitol 20BS* 8 ) 2.0 1100 12 Polyvinyl alcohol (saponification degree: 78.5-81.5 mol%) 2.5 1000 13 Sodium polyoxyethylene (3) dodecyl ether sulfate 0.5 1800< 14 Sodium polyoxyethylene (20) nonylphenyl ether sulfate 3.0 800 15 Sodium bis(2-ethylhexyl)sulfosuccinate 2.0 600 16 Sodium polyacrylate (Mw = about 8,000) 1.0 900 17 Acrylic acid/maleic acid copolymer (Mw = about 4,000) 1.0 650 Comparative Example Sodium laurylsulfate 0.005 210 Control None 70 Note: (1) *1 to *8 are all trade names of products of Kao Corp. (2) The numbers in the parentheses are the number of moles of an added alkylene oxide unless otherwise specified. As can be seen from the results in Table 1, addition of the stabilizer according to the present invention brings about remarkable improvement in mechanical stability of a deproteinized natural rubber latex. As described and demonstrated above, the stabilizer according to the present invention improves mechanical stability of a deproteinized natural rubber latex, whereby it is possible to provide a stabilized latex which has stable quality and entertains no fear of causing allergy.

Claims: A method for stabilizing a deproteinized natural rubber latex comprising adding to the deproteinized naturel rubber latex sodium polyoxyethylene (3) dodecyl ether sulfate or an alkylbenzene sulfonate having an alkyl moiety of from 8 to 20 carbon atoms in an amount to give a concentration of from 0.01 to 10% by weight based on the total weight of the latex. Use of sodium polyoxyethylene (3) dodecyl ether sulfate or an alkylbenzene sulfonate having an alkyl moiety of from 8 to 20 carbon atoms as a stabilizer for a deproteinized natural rubber latex.

Inventors: HAYASHI MASAHARU, HIOKI YUICHI, ICHIKAWA NAOYA, SAKAKI TOSHIAKI, TANAKA YASUYUKI, HAYASHI, MASAHARU, HIOKI, YUICHI, ICHIKAWA, NAOYA, SAKAKI, TOSHIAKI, TANAKA, YASUYUKI
Applicants: KAO CORP, SUMITOMO RUBBER IND, KAO CORPORATION, SUMITOMO RUBBER INDUSTRIES LTD.
Application year: 1994
Main classification: C08C1
IPC codes: C08C1