AN APPARATUS AND METHOD FOR DEFIBRATING OPTICALLY DENSE GLASS MELTS

Abstract: An apparatus for defibrating optically dense glass melts, such as a glass melt from basalt by the jet process, is proposed which is equipped with feeding means (1) for the melt and defibrating aggregates (2), the feeding means (1) having a feed channel (3) and a subsequent distributing channel (4) with outlet ports (5) to the defibrating aggregates (2). To homogenize the glass temperature in the area before the defibrating aggregates (2) the feed channel (3) has on the bottom side at least in the area adjacent the distributing channel (4) a warming device (8) serving as a thermal barrier or active insulation and advantageously formed as an electric resistance heating device.

Description: An apparatus and method for defibrating optically dense glass melts The present invention relates to an apparatus for de¬ fibrating optically dense glass melts, such as a glass melt from basalt by the jet process, having feeding means (or "feeders") for the melt and defibrating aggregates, the feeding means having a feed channel and a subsequent dis¬ tributing channel with outlet ports to the defibrating ag¬ gregates, and the melt being heatable from the surface. The present invention further relates to a corresponding method for applying the inventive apparatus. Apparatus and methods of the type in question have been known for years from practice and are used for producing mineral wool. To prevent the melt flowing to the defibrating aggregates or jets, which are usually in linear arrangement, from cooling off the melt is heated from the surface, this generally being done by hot gas. With respect to the resulting temperature distribution in the melt stream it is essential that the heat transfer by radiation plays a much smaller part with optically dense or approximately dense glass than with clear glass. With opti¬ cally dense glass, which includes basalt melts, the thermal transport to the bottom of the feeding means takes place almost solely by thermal conduction. The result is that a considerable temperature difference arises in the melt be¬ tween the melt surface and the bottom of the feeding means, this difference being in turn dependent on the quality of the bottom insulation in the feeding means, or rather the feed channel. It has thus turned out in practice that the melt flowing through the feed channel has a vertical tem¬ perature gradient of up to 20° per cm of melt height. This enormous temperature gradient affects the flow behavior of the melt stream, which is due to the pronounced tempera¬ ture-dependent march of viscosity. A vertical velocity pro- file of the melt stream consequently arises, so that the melt located on the top in the feed channel, which is heated from above, flows faster than the melt near the bottom of the feed channel. Furthermore the mass flowing through the feed channel, which is often referred to as the glass power, itself in¬ fluences the temperature distribution. At high glass power, i.e. a high glass throughput through the feed channel, the above-mentioned temperature gradient is lower, which is due to a shorter sojourn time within the feed channel. However the vertical temperature gradient increases toward the bot¬ tom of the feed channel. The result of the abovementioned influences is that the defibrating aggregrates usually disposed in linear succes¬ sion are supplied with melt of different temperature. The temperature differences in the melt occurring at the defi¬ brating aggregates are sometimes so high that the operation of the first defibrating aggregate is interrupted by dis¬ continuation of the melt flow due to a temperature decreas¬ ing toward the bottom, while the last defibrating aggregate is usually operated at the limit of maximum flow due to overheating. Power differences of up to 100% based on the glass throughput can consequently be detected. This in turn results in different qualities of the wool produced by the successive defibrating aggregrates e.g. by the jet process, which are unacceptable. There have been attempts in the past to solve the above-described problem of interrupted operation of the first defibrating unit by discontinuation of the glass flow, which is also referred to as falling asleep, in different ways. For example DE-C 29 35 416 proposes an apparatus for uniformly heating a glass stream in a feeder wherein elec¬ tric heating means leading through the melt stream, among other places, are to ensure a horizontal temperature balance in the feeder. The electric energy is often guided directly through the melt. Due to different temperatures, however, the melt has different conductances, the conductance in¬ creasing at a higher melt temperature. Primarily the already hotter melt is consequently heated even further, which is precisely what was to be avoided. This counteracts a homog- enization of temperature, i.e. the vertical temperature gradient is largely retained. The present invention is therefore based on the problem of providing both an apparatus and a method for defibrating optically dense glass melts, such as a glass melt from ba¬ salt by the jet process or other methods, wherein a homog- enization of the melt temperature occurs in the area before the defibrating aggregates so that a vertical temperature gradient is at least largely avoided. A corresponding method is further stated. The inventive apparatus solves the above problem by the features of claim 1. The apparatus is thus designed in such a way that a warming device serving as a thermal barrier or active insulation is associated with the feed channel - on the bottom side - at least in the area adjacent the dis¬ tributing channel, whereby the term "warming device" refers to a device that both keeps warm and slightly heats - if necessary - in the manner of an additional heating device. It was found according to the invention that the abovementioned problem lies in the temperature drop toward the bottom. In a next step it was found that this problem can be fundamentally remedied by warming at least the bottom of the feed channel in the area adjacent the distributing channel in such a way that it acts as a kind of active in¬ sulation. This refers to heating to such an extent as to at least largely avoid cooling toward the bottom in the melt flowing within the feed channel, by heat transition. Finally it was found that such active insulation acts like a thermal barrier against the flow of colder melt since, when cooling is avoided across a sufficiently large area of the feed channel bottom, the melt flowing faster due to differences in viscosity flows from the middle or upper layers to the bottom, while the colder, slower-flowing melt more or less stops at the beginning of the warming zone. Consequently a vertical homogenizing of temperature is obtained in the melt directly before the first defibrating aggregate so that a discontinuation of the melt flow of the first defibrating aggregate is excluded by avoiding a lower melt temperature arising in the bottom area. The inventive apparatus accordingly achieves a verti¬ cally oriented, cascade-like rolling effect within the melt so as to ensure that the warmer, upper temperature layers of the melt spread fast in the direction of transport. Since the otherwise viscous bottom layer can no longer creep across the first, or even several, defibrating aggregrates or jets but already heats up before the first defibrating aggregate due to heating and liquefaction, the term "thermal barrier" introduced above is justified. The warming device claimed as inventive could be dis¬ posed advantageously within the feed channel on its bottom so that it is flowed over directly by the melt. It could also be integrated in the walling of the feed channel so that it is protected by the walling and thus has no direct contact with the melt. It is also conceivable to dispose the warming device below the feed channel, preferably directly on its outer walling, the outer walling usually being made of a ceramic material referred to as "bottom stone". In comparison to conventional apparatus of the type in question, the area of the feed channel having the warming device could be formed as a prolongation of the conventional feed channel adjacent the actual distributing channel. A kind of warming plate would accordingly be inserted between feed channel and distributing channel, over which the melt stream passes from the actual feed channel into the dis¬ tributing channel. With respect to a specific design of the warming device it is advantageous in particular with respect to a simple constructional design to form it as an electric heating de- vice. Specifically, it could be a heating element preferably designed as a resistance heating element, whereby the latter can be designed as a resistance wire, heating resistor or tubular heating element. In particular if the warming device is disposed within the feed channel on its bottom it is recommendable to use a tubular heating element since this element, due to its coaxial arrangement of the actual heat conductor, is at least largely protected against outside influences by the outer tube and the ceramic insulation lo¬ cated therein. To guarantee a sufficiently large warming path it is advantageous to dispose and design one or more heating ele¬ ments in the direction of melt flow in such a way that their minimum heating capacity at least largely corresponds to the heat emission from the feed channel downward. In other words, the warming device in the form of an additional heating device is not for originally heating the melt but rather for avoiding a heat emission to the walling of the feed channel or to the surroundings. Consequently the ca¬ pacity of the warming device could be designed just so as to compensate the actual heat emission to the outside. With respect to the inventive method the abovementioned problem is solved by the features of claim 8. The feed channel, or the melt, is accordingly heated on the bottom side at least in the area adjacent the distributing channel to compensate heat losses. It was also found within the framework of the inventive method that the heat losses causing the abovementioned problems can be compensated by a kind of "active insulation", namely by additionally heating the bottom area of the feed channel causing the heat losses. The capacity of the bottom heating is advantageously de¬ signed just so as to at least largely avoid a downward di¬ rected heat emission from the feed channel. There are different possibilities for advantageously designing and developing the teaching of the present inven¬ tion. Reference is made, on the one hand, to the claims de- pendent on claims l and 8 and, on the other hand, to the following explanation of an embodiment example of the in¬ vention with reference to the drawing. Generally preferred designs and developments of the teaching will also be ex¬ plained in conjunction with the explanation of the preferred embodiment example of the invention with reference to the drawing. In the drawing the single figure shows schematically and in part a longitudinal section of an embodiment example of an inventive apparatus for defibrating a basalt or glass melt by the jet process, showing only the feeding means and the first defibrating aggregate as well as the march of temperature in the melt stream. The apparatus shown in the single figure has substan¬ tially feeding means 1 and defibrating aggregrates 2 or jets. Feeding means 1 in turn include feed channel 3 and subsequent distributing channel 4 with outlet ports 5 to defibrating aggregates 2. Arrows 6 indicate that melt 7 is heatable by gas from the surface. According to the invention, warming device 8 in the form of an additional heating device and serving as a ther¬ mal barrier or active insulation is associated with feed channel 3 on the bottom side in the area adjacent distrib¬ uting channel 4. In the embodiment example selected here, additional heating device 8 is integrated or received in walling 9 of feed channel 3. The figure further shows clearly that the area of feed channel 3 having additional heating device 8 is formed as prolongation 10 of conven¬ tional feed channel 3 adjacent distributing channel 4. Additional heating device 8 shown is designed as an electric heating device, more precisely as a resistance heating element, altogether two resistance heating elements being disposed successively in the direction of melt flow. This realizes a sufficient warming path, the capacity of additional heating device 8 being designed in such a way as to at least largely exclude a downward directed heat emis¬ sion from feed channel 3. Along with the specific constructional design the sin¬ gle figure further shows melt stream 11 which results due to differences in viscosity of faster-flowing melt 7. In ac¬ cordance with melt stream 11 shown, faster-flowing melt from the middle or upper layers flows around cooler areas of melt 7 to the bottom, while colder, slow-flowing melt 7 almost stops at the beginning of the heating surface or in the area of additional heating device 8. A temperature balance con¬ sequently takes place in the melt in the area before first defibrating aggregate 2, at least largely eliminating the formerly vertical temperature gradient. This effectively avoids a discontinuation of flow of melt 7 in the area of first defibrating aggregate 2, thereby excluding power dif¬ ferences at the individual defibrating aggregates. This ul¬ timately ensures a sufficiently homogeneous quality of the wool produced with the inventive apparatus and by the in¬ ventive method. Finally it should be emphasized that the present in¬ vention is not limited to glass melts defibrated by the jet process. It is also advantageously applicable for example with glass melts defibrated by the so-called TEL method (centrifugal drum principle) .

Claims: Claims 1. An apparatus for defibrating optically dense glass melts, such as a glass melt from basalt by the jet process, having feeding means (1) for the melt and defibrating ag¬ gregates (2) , the feeding means (1) having a feed channel (3) and a subsequent distributing channel (4) with outlet ports (5) to the defibrating aggregates (2), and the melt (7) being heatable from the surface, characterized in that at least one warming device (8) serving as a thermal barrier or active insulation is provided on the bottom side of the feed channel (3) at least in the area adjacent the distrib¬ uting channel (4) . 2. The apparatus of claim 1, characterized in that the warming device (8) is disposed within the feed channel (3) on its bottom. 3. The apparatus of claim 1, characterized in that the warming device (8) is integrated in the walling (9) of the feed channel (3). 4. The apparatus of any of claims 1 to 3, characterized in that the warming device (8) is formed as an electric heating device with relatively low heating capacity. 5. The apparatus of any of claims 1 to 4, characterized in that the area of the feed channel (3) having the warming device (8) is formed as a prolongation (10) of the conven¬ tional feed channel (3) adjacent the distributing channel (4). 6. The apparatus of claim 4 or 5, characterized in that the warming device (8) is formed as an electric heating de¬ vice with one or more heating elements in such a way that it has a minimum heating capacity largely corresponding to the heat emission from the feed channel (3) downward. 7. The apparatus of claim 6, characterized in that at least two heating elements are provided that are designed as resistance heating elements and disposed successively in the direction of melt flow. 8. A method for defibrating optically dense glass melts, such as a glass melt from basalt by the jet process, using the apparatus of any of claims 1 to 7, the glass being melted and the melt (7) fed to the defibrating aggregates (2) via the feed channel (3) and the subsequent distributing channel (4) through the outlet ports (5) , and the melt (7) being heated from the surface, characterized in that the feed channel (3), or the melt (7), is kept warm on the bot¬ tom side at least in the area adjacent the distributing channel (4) to compensate heat losses. 9. The method of claim 8, characterized in that the capacity of the bottom heating is designed in such a way as to at least largely avoid a downward directed heat emission from the feed channel (3) .

Inventors: MELLEM JOACHIM, MELLEM, JOACHIM
Applicants: MELLEM JOACHIM, SAINT GOBAIN ISOVER, ISOVER SAINT-GOBAIN, MELLEM, JOACHIM
Application year: 1994
Main classification: C03B7
IPC codes: C03B7, C03B37