Secondary battery

Abstract: A purpose of the present invention is to provide a secondary battery of high safety and high energy density. The battery of the present invention is a microcapsule containing lithium secondary battery at least formed of negative electrode active material, a separator, positive electrode active material, electrolytic solution (electrolyte), a collector and a battery case, characterized in that microcapsules are dispersed within the electrolytic solution or separator, said microcapsules discharging the chemical substance having hydroxyl group or chemical substance which is polymerization initiator, when the temperature within battery rises.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to batteries with high safety, and more particularly to secondary batteries maintaining high safety even after repeated uses and having higher energy density. Related Background Art Recently, it is foreseen that the earth will be increasingly warmer due to greenhouse effect with the increase of CO 2 , which makes it difficult to construct new thermal power plants, and thus a so-called load leveling has been devised which permits the effective use of generated electric power by storing night power into the secondary batteries installed in general homes to level the load for more efficient utilization. Also, there are increasingly the demand for developing small, lightweight secondary batteries having high energy density for use with the electric automobiles which exhaust no air pollutant, and the demand for developing secondary batteries of high performance for use with the power sources of the portable equipments such as book-type personal computer, word processor, video camera, and portable telephone. As the above-mentioned secondary battery of high performance, a rocking chair type lithium ion battery has been developed in which positive electrode active material has lithium ions introduced into intercalation compound, and negative electrode active material is made of carbon, and partially put to practical use. However, such lithium ion battery has lower energy density than lithium battery which uses metal lithium for the negative electrode active material. The reason why no lithium accumulator of high capacity which uses lithium metal for the negative electrode has not been practically used is considered due to the fact that the occurrence of lithium dendrite (dendritic crystal) which is produced by repetitive charge and discharge and mainly causes short-circuit has not been successfully suppressed. When dendrite of lithium grows to cause a short-circuit between positive and negative electrodes, the energy of battery will be consumed in a short time to produce the heat. The heating will decompose the solvent of electrolyte to produce gases, which increases the inner pressure and eventually may result in some explosion. Also, there is a problem of accident that heating may cause a fire. Accordingly, the development of safe accumulator not bringing about such accident is desired. Also, in the battery involving chemical reaction and having the possibility of firing, the development of safe battery not causing such accident is desired. The documents JP-A-63312624, JP-A-01161671, JP-A-63269461 and US-A-4,075,400 describe battery systems comprising encapsulating materials or microcapsules which contain active agents released under abnormal temperature rise, which may act as fire retardant, fire extinguisher, poisoning agent, reaction inhibitors or gelling agents. SUMMARY OF THE INVENTION It is an object of the present invention to resolve the above-mentioned conventional problems and provide a highly safe battery and a secondary battery having high energy density without decreasing battery performance. This object is solved by the battery according to claim 1. As a result of careful researches to solve the above-mentioned conventional problems, the present inventors have found, as the invention of this application, that by containing microcapsules emitting the chemical substance bringing about a curing reaction such as polymerization reaction or crosslinking reaction upon rising in temperature into electrolyte, the electrolyte can be solidified and the internal resistance of battery increased when the temperature abnormally rises, thereby preventing firing or bursting from occurring by the energy consumed in short time. The present invention is a microcapsule containing secondary battery comprising a negative electrode having negative electrode active material, a positive electrode having positive electrode active material with a separator sandwiched between it and said negative electrode active material, and electrolytic solution between said negative electrode and said positive electrode, characterized by having microcapsules containing the chemical substance in said separator and/or said electrolytic solution. Also, said microcapsule containing secondary battery is characterized in that the microcapsule containing secondary battery is preferably a lithium secondary battery that said chemical substance preferably has at least polymerization initiator or cross linking agent, that said microcapsule contains, in addition to polymerization initiator or cross linking agent, one kind or more selected from monomer, oligomer, and polymer, that said chemical substance preferably has at least acid, that said microcapsule preferably has at least flame retardant, that the surface of the negative electrode composed of said negative electrode active material opposed to the positive electrode is preferably covered with a membrane capable of transmitting at least lithium ions, that the surface of the positive electrode composed of said positive electrode active material opposed to the negative electrode is preferably covered with a membrane capable of transmitting at least lithium ions, that said membrane is preferably made of a fire retarding material or incombustible material, and that said negative electrode active material preferably is lithium or lithium alloy. Further, said microcapsule containing secondary battery is characterized in that the melting point of said microcapsule is preferably from 70 to 150°C, that said microcapsule is preferably from 1 to 500 microns in size, and that the mixture amount of said microcapsule is preferably from 1 to 20 wt% of said electrolytic solution. By containing the chemical substance of monomer, oligomer, or polymer within said microcapsule, the internal resistance of battery is more easily increased when the temperature of battery abnormally rises. Also, by containing a flame retardant within said microcapsule, firing can be suppressed more securely when battery temperature abnormally rises. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a typical view showing the basic construction of a lithium secondary battery. Fig. 2 is a schematic cross-sectional view of a flat lithium secondary battery according to one embodiment of the present invention. Fig. 3 is a schematic cross-sectional view of a cylindrical lithium secondary battery according to another embodiment of the present invention. Fig. 4 is a graph representing the ion conductivity of electrolyte relative to the additive amount of flame retardant. Fig. 5 is a typical view showing the basic construction of a microcapsule containing secondary battery according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS (Shape and structure of battery) The practical shape of battery may be flat, cylindrical, rectangular or sheet-like. The spiral cylindrical type can have a larger electrode area by winding the electrode with a separator sandwiched between positive and negative electrodes to allow a larger electric current to flow in charging and discharging. Also, the rectangular type allows the effective use of storage space for the equipment where battery is stored. The structure may be of the single layer or multi-layer type. Figs. 2 and 3 illustrate schematic cross-sectional views of a single layer type flat battery and a spiral structure cylindrical battery. In Figs. 2 and 3, 201 and 301 are negative electrodes made of negative electrode active material, 202 and 302 are negative electrode collectors, 203 and 303 are positive electrodes made of positive electrode active material, 304 is a positive electrode collector, 206 and 306 are negative electrode terminals (negative electrode caps), 207 and 307 are outer packaging cans (positive electrode cans) which are also used as the battery case, 208 and 308 are separators holding the electrolytic solution holding microcapsules and the electrolytic solution, 210 and 310 are insulating packings, and 311 is an insulating plate. An example of assembling the battery of Figs. 2 and 3 involves incorporating a positive electrode 203, 303 and a negative electrode 201, 301, with a separator 208, 308 sandwiched therebetween, into a positive electrode can 207, 307, injecting the electrolytic solution with microcapsules containing chemical substance dispersed, placing a negative cap 206, 306 and an insulating packing 210, 310, and caulking to fabricate the battery. It should be noted that the preparation of lithium battery material and the assembling of battery are desirably made in the dry air with water contents removed sufficiently, or in the dry inert gas. Battery case (outer packaging can) Battery case may be a metallic outer packaging case which is also used as the output terminal, or a plastic resin case. Examples of the material for positive electrode can 207, 307 or negative cap 206, 306 of actual battery may include stainless steel, in particular, titanium clad stainless, copper clad stainless, and nickel plated steel plate. In Figs. 2 and 3, the positive electrode can 207, 307 is also used as the battery case, examples of the material of which may include, in addition to stainless steel, metals such as aluminum, plastics such as polypropylene, or composites of metal or glass fiber with plastics. Insulating packing Examples of the material for insulating packing 210, 310 may include fluororesin, polyamide resin, polysulphone resin, and a variety of rubbers. Sealing The sealing may be made by adhesive, welding, soldering, glass sealing, in addition to caulking using a gasket such as insulating packing. Insulating plate The material of insulating plate usable for the insulation or isolation within the battery may be any of a variety of organic resins, or ceramics. Safety valve The safety measure against increased inner pressure of battery, not shown in Figs. 2 and 3, involves providing a safety valve using rubber, spring, or metallic hole. (Constitution of battery according to the invention of his application) Fig. 5 shows the basic constitutional view of a secondary battery according to the present invention. In Fig. 5, 5101 is a negative electrode composed of negative electrode active material, 5102 is a negative collector, 5103 is a positive electrode composed of positive electrode active material, 5104 is a positive electrode collector, 5105 is an electrolytic solution (electrolyte), 5106 is a negative terminal, 5107 is a positive terminal, 5108 is a separator, 5109 is a battery case, and 5110 is a microcapsule containing the chemical substance. (Battery reaction) In a lithium battery in which the negative electrode active material of negative electrode 5101 is lithium or lithium alloy, with discharge reaction, lithium ions in electrolytic solution 5105 pass through the separator 5108 to enter the intercalation of positive electrode active material of positive electrode 5103, while dissolving into electrolyte 5105 from the negative electrode active material. On the other hand, with charge reaction, lithium ions in electrolytic solution 5105 pass through the separator 5108 to be deposited as lithium metal on the negative electrode active material (wherein dendrite is likely to grow), while lithium of the intercalation for the positive electrode active material 5103 of positive electrode dissolves into the electrolyte 5105. (Heating of battery) If there occurs any short-circuit, such as when dendrite grows to cause a short-circuit within the battery, the battery is broken to cause a short-circuit, or the external circuit connecting to the battery causes a short-circuit, the battery may be heated. In the battery of the present invention, the temperature elevation of the battery causes microcapsules to be dissolved or broken and opened to discharge the chemical substance. When the discharged chemical substance is a radical generating agent, there will occur polymerization reaction of the solvent in the electrolytic solution within the battery to increase the internal resistance of battery, if the temperature rises up to a decomposition temperature for the radical generating agent, resulting in the decrease in current to suppress the excessive heating. Chemical substance bringing about polymerization or crosslinking reaction Examples of other chemical substance reacting with lithium usable with the present invention may include radical generating agents which generate radical with thermal decomposition. The radical generating agent can bring about polymerization reaction and crosslinking reaction. Examples of radical generating agent may include peroxide, azo compound and metallic compounds. Specific examples may include benzoyl peroxide and azobisisobutyronitrile. Microcapsule The wall film material of microcapsule may be a material of which the microcapsule is broken or released and opened to discharge the chemical substance, when the battery reaches abnormal temperature. Specific examples thereof may include linear polyethylene, oligomer such as olefine, poly-benzylidenethiodecamethylene sulfide, poly-1,2-cyclohexylene sulfide, poly-cyclopropylenedimethyleneterephthalate, poly-decamethylenephthalamide, poly-ethylene2,2'-dibenzo-8, poly-(oxydiethylene)-oxy-p-phenyleneoxide, calcium stearate, and carnauba wax. Examples of the above oligomer for olefine may include oligo(methylene), oligo(ethylene), oligo(cycmealkane), oligo(perfluoro-n-alkane), oligo(w-chloro-perfluoro-n-alkane), oligo(semifulororinated-n-alkane), which have repeated units of about 10 to 500. The wall film material of the above microcapsule is necessary to be selected from materials indissoluble in the electrolytic solution for the battery. In accordance with the highest temperature to maintain the safety of battery, the wall film material is also necessary to be selected based on the melting point of material. The melting point of the wall film material for the microcapsule is preferably selected in the range from 70 to 150°C, and more preferably from 100 to 130°C. As to the size and mixing amount of microcapsule, in order to maintain the safety without decreasing the battery performance, the size of microcapsule is preferably from 1 to 500 microns, and more preferably from 5 to 50 microns. Also, the mixing amount of microcapsule is preferably from 1 to 20 wt% relative to the electrolytic solution. (Microcapsulation of chemical substance) An exemplary method for the microcapsulation of chemical substance involves adding and dispersing the chemical substance directly or the chemical substance dissolved in the solvent in which the wall film material for microcapsule is indissoluble into a solution having the wall film material for microcapsule dissolved in the solvent, dripping this dispersed solution to the solvent such as water or alcohol with agitation, and conducting percolation or centrifugation and drying under lower pressure to prepare the chemical substance containing microcapsule. In addition to the previous chemical substance, monomer or flame retardant may be mixed into the microcapsule. Flame retardant In addition to the chemical substance, flame retardant may be contained into the microcapsule. The use of flame retardant makes it possible to suppress any firing of electrolytic solution when the battery is heated. Examples of flame retardant may include phosphorus type flame retardants such as phosphorus compound, halogen type flame retardants such as iodine, bromine, chlorine, and halogen compound, and flame retardants,containing phosphorus and halogen element. Halogen type flame retardants are particularly effective because perfluorocarbon which is fluorine compound inert liquid has no influence on the electrolytic reaction. Examples of the above perfluorocarbon may include C 5 F 12 , C 6 F 14 , C 7 F 16 , C 8 F 18 , perfluorobutyltetrahydrofuran: C 8 F 16 O, perfluorotributylamine: (C 4 F 9 ) 3 N, perfluorotripropylamine: (C 3 F 7 ) 3 N, perfluorinatedether, perfluoromethyldecarine, and perfluorodecarine. Examples of the above phosphorus type flame retardant may include red phosphorus, trimethyl phosphate, triethyl phosphate, tris(chloroethyl) phosphate, and tri(dichloropropyl) phosphate. (Battery safety evaluation) The safety evaluation tests for the battery are as follows. Short-circuit test Confirmation test as to whether or not firing occurs when the battery temperature rises by short-circuiting the positive electrode and the negative electrode via copper wire after charging at 25°C and 85°C. Nailing test Confirmation test as to whether or not firing or explosion occurs when the battery temperature rises by penetrating a nail having a diameter of 3 millimeters into the charged battery. Burning test Confirmation test to ensure that no furious burning occurs by throwing a charged battery into carbide. Water immersion test Confirmation test to ensure that no burst or explosion occurs by immersing in city water having a temperature of 25°C for fourteen days. High temperature storage test Confirmation test to ensure that the battery temperature is not more than 130°C and there is no fuming, explosion and firing by storing a battery at 100°C for five hours. Overcharge Confirmation test to ensure that no firing occurs even if the battery temperature rises by charging for a rate of 10 hours with a terminal voltage of 5.0 volts, and for 24 hours with the cut-off. The present invention will be described in detail based on the examples. It should be noted that the present invention is not limited to such examples. (Ref. Example 1) First, using linear polyethylene for the wall film material for capsule and 1, 4-butanediol for chemical substance, microcapsule was prepared in the following way. Colloidal ethyl alcohol solution for microcapsule was prepared by dripping a solution prepared by dripping 1, 4-butanediol into xylene solution of linear polyethylene, into ethylene alcohol. Obtained colloidal solution was separated and percolated, and dried under lower pressure to prepare the microcapsule. Next, a lithium secondary battery of a structure having a schematic cross section as shown in Fig. 3 was fabricated. The positive electrode active material was formed by mixing electrolyzed manganese dioxide and lithium carbonate at a ratio of 1 to 0.4, and heating at 800°Cto prepare lithium manganese oxide. After mixing graphite and powder fluororesin paint Superconac (made by Nippon Oil & Fats) to lithium manganese oxide, the mixture was molded under pressure to a nickel mesh 304, and subjected to thermal treatment at 170°C to form a positive electrode 303. A titanium mesh collector with lead 302 was connected under pressure from the back side to a lithium metal foil in the dry argon gas atmosphere, and covered with a fluororesin paint lumifron thin film (made by Asahi Glass) to prepare a lithium negative electrode 301. The electrolytic solution was prepared by dissolving borate tetrafluoride lithium salt by 1M(mol/l) into an equivalent mixture solvent of propylene carbonate (PC) and dimethoxyethan (DME) and mixing microcapsules prepared by the above method by 10 wt% thereto to prepare a microcapsule dispersion liquid. Separator 308 was composed of an alumina film, a polypropylene non-woven fabric, and a microporous separator of polypropylene which were bonded together. The assembling was performed in such a way as to sandwich a separator 308 between negative electrode 301 and positive electrode 303, then rolling and inserting the entirety into a positive electrode can 307 made of stainless material of titanium clad, connecting a collector lead, injecting electrolytic solution with microcapsules dispersed, and enclosing the whole structure by a negative electrode cap 306 with safety cap made of stainless material of titanium clad and an insulation packing 310 made of fluorine rubber to fabricate a spiral cylindrical lithium secondary battery. (Example 1) First, using oligo(semifluorinated-n-alkane): F-[CF 2 ] m -[CH 2 ] n -H (m=12, n=20) for the wall film material of capsule and azobisisobutyronitrile for chemical substance, microcapsule was prepared in the following way. Colloidal ethyl alcohol solution for microcapsule was prepared by dripping a solution prepared by dripping azobisisobutyronitrile into dimethylsulfoxide solution for oligo(semifluorinated-n-alkane), into ethyl alcohol. Obtained colloidal solution was separated and percolated, and dried under lower pressure to prepare the microcapsule. A spiral cylindrical type lithium secondary battery of Fig. 3 was fabricated in the same way as in Ref. example 1. The positive electrode active material was formed by mixing electrolyzed manganese dioxide and lithium carbonate at a ratio of 1 to 0.4, and heating at 800°C to prepare lithium manganese oxide. After mixing graphite and tetrafluoroethylene powder to lithium manganese oxide, the mixture was molded under pressure at 250°C to a nickel mesh 304 to form a positive electrode 303. A titanium mesh collector with lead 300 was connected under pressure from the back side to a lithium metal foil in the dry argon gas atmosphere, and covered with a polyphosphazene PPZ-R1001 thin film (Idemitsu Petrochemical) to prepare a lithium negative electrode 301. The electrolytic solution was prepared by dissolving borate tetrafluoride lithium salt by 1M(mol/l) into an equivalent mixture solvent of propylene carbonate (PC) and dimethoxyethan (DME) and mixing microcapsules prepared by the above method by 3 wt% thereto to prepare a microcapsule dispersion liquid. Separator 308 was composed of a polypropylene non-woven fabric and a microporous separator of polypropylene which were bonded together. The assembling was performed in such a way as to sandwich a separator 308 between negative electrode 301 and positive electrode 303, then rolling and inserting the entirety into a positive electrode can 307 made of stainless material of titanium clad, connecting a collector lead, injecting electrolytic solution with microcapsules dispersed, and enclosing the whole structure by a negative electrode cap 306 with safety cap made of stainless material of titanium clad and an insulation packing 310 made of fluorine rubber to fabricate a lithium secondary battery. (Ref. Example 2) Using oligo(ethylene): H[CF 2 ] n H (m=288) for the wall film material of capsule and cyclohexanol for the chemical substance, microcapsule was prepared in the following way. Colloidal ethyl alcohol solution for microcapsule was prepared by dripping a solution prepared by adding cyclohexanol and red phosphorus into xylene solution for oligo(ethylene), into ethyl alcohol. Obtained colloidal solution was separated and percolated, and dried under lower pressure to prepare the microcapsule. A spiral cylindrical type lithium secondary battery of Fig. 3 was fabricated in the same way as in Ref. example 1. The positive electrode active material was formed by mixing electrolyzed manganese dioxide and lithium carbonate at a ratio of 1 to 0.4, and heating at 800°C to prepare lithium manganese oxide. After mixing acetylene black and tetrafluoroethylene powder to lithium manganese oxide, the mixture was molded under pressure at 250°C to a nickel mesh 304 to form a positive electrode 303. A titanium mesh collector with lead 302 was connected under pressure from the back side to a lithium metal foil in the dry argon gas atmosphere to prepare a lithium negative electrode 301. The electrolytic solution was prepared by dissolving borate tetrafluoride lithium salt by 1M (mol/l) into an equivalent mixture solvent of propylene carbonate (PC) and dimethoxyethan (DME) and mixing microcapsules prepared by the above method by 5 wt% thereto to prepare a microcapsule dispersion liquid. Separator 308 was composed of a titanium oxide film, a polypropylene non-woven fabric and a microporous separator of polypropylene which were bonded together. The assembling was performed in such a way as to sandwich a separator 308 between negative electrode 301 and positive electrode 303, then rolling and inserting the entirety into a positive electrode can 307 made of stainless material for titanium clad, connecting a collector lead, injecting electrolytic solution with microcapsules dispersed, and enclosing the whole structure by a negative electrode cap 306 with safety cap made of stainless material of titanium clad and an insulation packing 310 made of fluorine rubber to fabricate a lithium secondary battery. (Comparative example 1) A lithium secondary battery was fabricated in the same way as in Ref. example 2, with the exception that no microcapsule was dispersed and a lithium foil undergoing no surface treatment was used for the negative electrode. (Example 2) Using oligo(semifluorinated-n-alkane): F-[CF 2 ] m -[CH 2 ] n -H (m=12, n=20) for the wall film material of capsule and benzoyl peroxide for chemical substance, microcapsule was prepared in the following way. Colloidal ethyl alcohol solution for microcapsule was prepared by dripping a solution prepared by adding benzoyl peroxide into dimethylsulfoxide solution for oligo(semifluorinated-n-alkane), into ethyl alcohol. Obtained colloidal solution was separated and percolated, and dried under lower pressure to prepare the microcapsule. A spiral cylindrical type lithium secondary battery of Fig. 3 was fabricated in the same way as in Ref. example 1. The positive electrode active material was formed by mixing electrolyzed manganese dioxide and lithium carbonate at a ratio of 1 to 0.4, and heating at 800°C to prepare lithium manganese oxide. After mixing acetylene black and tetrafluoroethylene powder to lithium manganese oxide prepared, the mixture was molded under pressure at 250°C to a nickel mesh 304 to form a positive electrode 303. A titanium mesh collector with lead 302 was connected under pressure from the back side to a lithium metal foil in the dry argon gas atmosphere and covered with a polyphosphazene PPZ-R1001 thin film (Idemitsu Petrochemical) to prepare a lithium negative electrode 301. The electrolytic solution was prepared by dissolving borate tetrafluoride lithium salt by 1M(mol/1) and mixing microcapsules prepared by the above method by 5 wt% thereto to prepare a microcapsule dispersion liquid. Overcharge It was confirmed that no firing occurred even if the battery temperature rose by charging for a rate of 10 hours at a terminal voltage of 5.0 volts and for 24 hours at the cut-off. From the results of safety evaluation test, it has been found that the lithium secondary battery of the present invention has high safety even after the repetition of charge and discharge, despite the use of metal lithium for the negative electrode active material. With the present invention, it is possible to supply the battery involving no risk of firing and having high safety. Also, it is possible to supply the secondary battery in which the repetition of charge and discharge is allowed at the high energy density with metal lithium used for the negative electrode active material and with the safety retained. Separator 308 was composed of a glass non-woven fabric, a polypropylene non-woven fabric and a microporous separator of polypropylene which were bonded together. The assembling was performed in such a way as to sandwich a separator 308 between negative electrode 301 and positive electrode 303, then rolling and inserting the entirety into a positive electrode can 307 made of stainless material of titanium clad, connecting a collector lead, injecting electrolytic solution with microcapsules dispersed, and enclosing the whole structure by a negative electrode cap 306 with safety cap made of stainless material of titanium clad and an insulation packing 310 made of fluorine rubber to fabricate a lithium secondary battery. (Safety evaluation of lithium secondary battery) For each of the lithium secondary batteries fabricated in the examples 1 and 2 and reference examples 1 and 2 and comparative example 1, charge and discharge was repeated by 20 cycles, and after charging, the safety was evaluated in accordance with the following test method. Excellent test results were obtained in the above test for any of the lithium secondary batteries in the examples. Short-circuit test It was confirmed that no firing occurred when the battery temperature rose by short-circuiting the positive electrode and the negative electrode via a copper wire after charging at 25°C and 85°C. Nailing test It was confirmed that no firing or explosion occurred when the battery temperature rose by penetrating a nail having a diameter of 3 millimeters into charged battery. Burning test It was confirmed that no furious burning occurred by throwing a charged battery into carbide. Water immersion test It was confirmed that no firing or explosion occurred by immersing in city water at a temperature of 25°C for fourteen days. High temperature storage test It was confirmed that the battery temperature was not more than 130°C and there was no fuming, explosion and firing by storing a battery at 100°C for five hours. A purpose of the present invention is to provide a secondary battery of high safety and high energy density. The battery of the present invention is a microcapsule containing lithium secondary battery at least formed of negative electrode active material, a separator, positive electrode active material, electrolytic solution (electrolyte), a collector and a battery case, characterized in that microcapsules are dispersed within the electrolytic solution or separator, said microcapsules discharging the chemical substance which is polymerization initiator, when the temperature within battery rises.

Claims: A secondary battery containing microcapsules comprising a negative electrode having negative electrode active material, a positive electrode having positive electrode active material with a separator sandwiched between said negative electrode and said positive electrode, and an electrolyte solution between said negative electrode and said positive electrode, wherein microcapsules containing a chemical substance, which is discharged when the temperature within the battery abnormally rises, are comprised in said separator and/or electrolyte solution, characterized in that said chemical substance comprises at least a compound having radical generating agents, which are capable of bringing about polymerisation or crosslinking reaction; and the microcapsules contain further one kind or more selected from monomer, oligomer and polymer. A secondary battery containing microcapsules according to claim 1, characterized in that said microcapsule containing secondary battery is a lithium secondary battery. A secondary battery containing microcapsules according to claim 1 or 2, characterized in that said chemical substance comprises further a flame retardant. A secondary battery containing microcapsules according to any of claims 1 to 3, characterized in that the surface of the negative electrode composed of said negative electrode active material opposed to the positive electrode is covered with a membrane capable of transmitting at least lithium ions. A secondary battery containing microcapsules according to any of claims 1 to 4, characterized in that the surface of the positive electrode composed of said positive electrode active material opposed to the negative electrode is covered with a membrane capable of transmitting at least lithium ions. A secondary battery containing microcapsules according to claim 4 or 5, characterized in that said membrane is made of fire retarding material or incombustible material. A secondary battery containing microcapsules according to any of claims 1 to 6, wherein said negative electrode active material is lithium or a lithium alloy. A secondary battery containing microcapsules according to any of claims 1 to 7, characterized in that the melting point of said microcapsule is from 70 to 150 °C. A secondary battery containing microcapsules according to any of claims 1 to 8, characterized in that said microcapsule is from 1 to 500 microns in size. A secondary battery containing microcapsules according to any of claims 1 to 9, characterized in that the mixture amount of said microcapsule is from 1 to 20 wt.% of said electrolyte solution.

Inventors: KAWAKAMI SOICHIRO, KAWAKAMI, SOICHIRO
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1994
Main classification: H01M10
IPC codes: H01M10, H01M2, H01M6