Fluorsilicone release agent composition

Abstract: There is disclosed a fluorosilicone release agent composition which, when cured onto a substrate such as paper, provides a surface which readily releases such tacky materials as silicone pressure-sensitive adhesive, said composition comprising (A) 100 parts by weight of an organopolysiloxane that contains at least 1 fluorine-containing organic group and at least 2 alkenyl groups in each molecule; (B) 0.1 to 40 parts by weight of an organohydrogenpolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule; (C) 0.01 to 20 parts by weight of an organopolysiloxane that contains at least 1 fluorine-containing organic group in each molecule, with the proviso that said organopolysiloxane (C) contains neither alkenyl groups nor silicon-bonded hydrogen groups; and (D) a catalytic amount of a hydrosilylation catalyst.

Description: The present invention relates to a fluorosilicone release agent composition that cures to form a film that has very stable release properties with respect to tacky or sticky substances such as, for example, pressure-sensitive adhesives, particularly silicone-type pressure-sensitive adhesives. When cured on the surface of a variety of substrates, such as, paper, synthetic resin films, and synthetic fiber fabrics, the objective of, a release agent composition is to produce a cured film that is releasable with respect to tacky or sticky substances, such as pressure-sensitive adhesives and the like. Typical release agent compositions are exemplified by Japanese Patent Publications 63-48901 and 63-320 [U.S. 4,736,048]. The silicone composition of JP-A 63-48901 consists of dimethylvinylsiloxy-terminated methylvinylpolysiloxane, trimethylsiloxy-terminated methylhydrogenpolysiloxane, perfluoroalkyl-containing dimethylpolysiloxane, and platinum group metal catalyst. The fluorosilicone composition proposed in JP-A 63-320 consists of platinum group metal catalyst, organohydrogenpolysiloxane, and fluorosilicone that contains both fluoroalkyl and vinyl groups. These silicone compositions cure to form films that have a very stable release performance with respect to organic resin-based tacky or sticky substances. However, they have a poor release performance stability against silicone-type pressure-sensitive adhesives (SPSAs) whose base component is an organopolysiloxane such as dimethylpolysiloxane, or methylphenylpolysiloxane, and they are therefore not fully satisfactory for some applications. The present inventors have found that a very stable release performance against SPSAs is obtained from the cured film afforded by the cure of a fluorosilicone release agent composition that contains noncrosslinking fluorine-containing organopolysiloxane. The fluorosilicone release agent composition of this invention comprises (A) 100 weight parts of a organopolysiloxane that contains at least 1 fluorine-containing organic group and at least 2 alkenyl groups in each molecule, (B) 0.1 to 40 weight parts of an organohydrogenpolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule, (C) 0.01 to 20 weight parts of an organopolysiloxane that contains at least 1 fluorine-containing organic group in each molecule, with the proviso that organopolysiloxane (C) contains neither alkenyl groups nor silicon-bonded hydrogen; and (D) a hydrosilylation-reaction catalyst in a catalytic quantity. Component (A) of the present invention, is an organopolysiloxane that contains in each molecule at least 1 fluorine-containing organic group and at least 2 alkenyl groups. The fluorine-containing organic group in component (A) is exemplified by groups with the general formula C n F 2n+1 -R- wherein R is a divalent hydrocarbon group and n is an integer with a value of 1 to 20; groups with the general formula C n F 2n+1 -R-O-R- wherein R is a divalent hydrocarbon group and n is an integer with a value of 1 to 20; and groups with the general formula wherein R is a divalent hydrocarbon group and n is an integer with a value of 1 to 20. The divalent hydrocarbon group R is exemplified by alkylene groups such as methylene, ethylene, methylmethylene, propylene, and butylene; arylene groups such as phenylene, tolylene, and xylylene; alkylenearylene groups such as methylenephenylene, and ethylenephenylene; and arylenealkylene groups. The alkenyl group present in component (A) is exemplified by vinyl, allyl, butenyl, pentenyl, and hexenyl. No specific restrictions apply to the silicon-bonded organic groups present in component (A) in addition to the alkenyl and fluorine-containing organic groups. Said silicon-bonded organic groups are exemplified by alkyl groups, such as methyl, ethyl, propyl, and butyl; aryl groups such as phenyl, tolyl, and xylyl; and aralkyl groups such as benzyl and phenethyl. The methyl and phenyl groups are preferred. The organopolysiloxane comprising component (A) may also contain hydroxyl groups and/or alkoxy groups in small quantities. The molecular structure of organopolysiloxane (A) is not specifically restricted and may be any of straight-chain, cyclic, resin, and partially branched straight-chain. This component may also be partially cross linked. The degree of polymerization (DP) of component (A) is also not specifically restricted, and the organopolysiloxane used as component (A) can range from organopolysiloxane gums to low-viscosity organopolysiloxane fluids. Organopolysiloxanes with viscosities in the range of 100 to 1,000,000 mm2/s (centistokes) at 25°C are preferred from the standpoint of ease of formation of the cured release film. The organopolysiloxane comprising component (A) is selected from dimethylvinylsiloxy-terminated methyl(3,3,3-trifluoropropyl)siloxane-dimethylsiloxane-methylvin ylsiloxane copolymers, dimethylvinylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylvinyl siloxane copolymers, dimethylvinylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-dimethylsiloxane-methylvinyl siloxane copolymers, trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylvinyl siloxane copolymers, trimethylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-dimethylsiloxane-methylvinyl siloxane copolymers, dimethylvinylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymers, silanol-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylvinyl siloxane copolymers, and dimethylhexenylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylhexen ylsiloxane copolymers. Component (B) is a crosslinker in the present invention, and comprises an organohydrogenpolysiloxane that contains at least 2 silicon-bonded hydrogens in each molecule. The silicon-bonded organic groups present in component (B) in addition to the silicon-bonded hydrogen atoms are exemplified by non-alkenyl monovalent hydrocarbon groups, for example, alkyl groups, such as methyl, ethyl, propyl, butyl, and pentyl; aryl groups such as phenyl, tolyl, and xylyl; and aralkyl groups such as benzyl and phenethyl. Component (B) may contain fluorine-containing organic groups, these fluorine-containing organic groups being of the type described in connection with component (A). The organohydrogenpolysiloxane comprising component (B) is selected from trimethylsiloxy-terminated dimethylsiloxane-methylhydrogensiloxane copolymers, dimethylhydrogensiloxy-terminated methyl(perfluorobutylethyl)siloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-methylhydrogensiloxane copolymers, and copolymers composed of the methyl(perfluorobutylethyl)siloxane unit, dimethylhydrogensiloxane unit, and SiO 2 unit. Component (B) is present at 0.1 to 40 weight parts per 100 weight parts of component (A). The bases for this range are as follows: the composition has a very slow rate of cured film formation when component (B) is added at less than 0.1 weight parts per 100 weight parts component (A); and at an addition in excess of 40 weight parts, the cured film obtained from the corresponding composition will have a substantially degraded release performance. The organopolysiloxane of component (C) imparts to the cured film an excellent release performance and an excellent release performance stability with respect to SPSAs based on organopolysiloxane such as dimethylpolysiloxane. Component (C) consists of organopolysiloxane that contains in each molecule at least 1 fluorine-containing organic group but contains neither alkenyl groups nor silicon-bonded hydrogen groups. The fluorine-containing organic group in component (C) is exemplified by the same fluorine-containing groups as component (A). The silicon-bonded organic groups present in component (C) are exemplified by non-alkenyl monovalent hydrocarbon groups, alkyl groups, such as methyl, ethyl, propyl, and butyl; aryl groups such as phenyl, tolyl, and xylyl; and aralkyl groups, such as benzyl and phenethyl. Component (C) may also contain hydroxyl and/or alkoxy groups in small quantities. The molecular structure of the organopolysiloxane comprising component (C) is not specifically restricted and may be any of straight-chain, cyclic, resin, and partially branched straight-chain. This component may also be partially crosslinked. The DP of component (C) is also not specifically restricted, and the organopolysiloxane used as component (C) can range from organopolysiloxane gums to low-viscosity organopolysiloxane fluids. Organopolysiloxanes with viscosities in the range of 100 to 1,000,000 mm2/s (centistokes) at 25°C are preferred from the standpoint of ease of formation of the cured release film. Specific examples of component (C) are trimethylsiloxy-terminated methyl(3,3,3-trifluoropropyl)siloxane-dimethylsiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-dimethylsiloxane copolymers, and silanol-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymers. Component (C) is present at 0.01 to 20 weight parts, preferably at 1 to 10 weight parts, per 100 weight parts component (A). If component (C) additions are below 0.01 weight parts per 100 weight parts component (A), the cured film yielded by the corresponding composition has a very reduced release performance and exhibits a diminished release performance stability with respect to SPSAs. Component (C) additions in excess of 20 weight parts per 100 weight parts component (A) yield cured films that suffer from a major decline in strength. Component (D) is a hydrosilylation-reaction catalyst and functions crosslinking components (A) and (B). No specific restrictions apply to the hydrosilylation-reaction catalyst of component (D), and this component is exemplified by microparticulate platinum adsorbed on a carbon powder carrier, chloroplatinic acid, alcohol-modified chloroplatinic acid, chloroplatinic acid/olefin complexes, chloroplatinic acid/vinylsiloxane coordination compounds, platinum black, palladium catalysts, and rhodium catalysts. Component (D) is added in the present invention in a catalytic quantity sufficient to facilitate a hydrosilylation reaction, this quantity being readily determined by routine experimentation. Typically, the amount ranges from 1-500 parts of metal per one million parts of Component (A). The fluorosilicone release agent composition of the present invention is composed of components (A), (B), (C), and (D), and this composition is prepared by mixing these components to homogeneity. In addition to components (A) - (D), the composition of the present invention may also contain organic solvent. Organic solvent is a desirable component to increase the storage stability of the composition as well as its coatability with respect to various substrates. Any solvent can be used that can dissolve the claimed composition to homogeneity. Operable organic solvents are exemplified by aromatic hydrocarbons, such as trifluorotoluene, and hexafluoroxylene; aliphatic hydrocarbons, such as heptane, hexane, pentane, and isooctane; halogenated hydrocarbons, such as trichloroethylene and perchloroethylene; and methyl ethyl ketone. In order to improve the storage stability at room temperature, the composition of the present invention may contain a small quantity of a component that inhibits the catalytic activity of component (D). Such hydrosilylation-reaction inhibitors are exemplified by alkynyl alcohols, such as 3-methyl-1-butyn-3-ol, 3,5-dimethyl-1-hexyn-3-ol, and 3-methyl-1-pentyn-3-ol, and phenylbutynol; and by 3-methyl-3-penten-1-yne; 3,5-dimethyl-1-hexyn-3-ene; tetra(methylvinylsiloxane) cyclic; and benzotriazole. Application of the claimed composition to the surface of various substrates (e.g., paper, synthetic resin films, and textiles) followed by curing at 120°C to 150°C for 20 to 120 seconds, will produce a cured film (e.g., a release liner construction) that has a very stable release performance with respect to tacky or sticky substances such as, pressure-sensitive adhesives, and particularly silicone PSA's. Moreover, the cured film thus obtained is itself strongly adherent to the surface of such substrate. Examples The present invention is explained in greater detail below through working examples. In the examples, parts indicates weight parts and the value reported for the viscosity was measured at 25°C. Molecular weight is number average molecular weight. Measurement of the curability The fluorosilicone release agent composition was coated in the reported quantity on the surface of the specified film or sheet substrate. The specimen was then heated in a hot-air circulation oven at the given temperature, and the time for formation of the completely cured film was measured. Measurement of the peel resistance The fluorosilicone release agent composition was applied in the reported quantity on the specified film or sheet substrate. A cured film was prepared by heating at the given temperature in a hot-air circulation oven for the listed heating time. A commercial dimethylpolysiloxane-based SPSA (SD4580™ from Dow Corning Toray Silicone Company, Limited, adhesive strength for stainless steel sheet = 55.1 g/mm) (1,400 g/inch) was applied to the surface of the cured film and heated for 3 minutes at 100°C. A polyethylene resin film backing (Lumilar™ S-10 From Toray Kabushiki Kaisha) was adhered on the treated surface, and the assembly was then aged for a time at 25°C under a load of 20 g/cm 2 to give the measurement sample. The test specimen was prepared by cutting the measurement sample to a width of 2.5 cm. Using a tensile tester, the backing film was peeled at an angle of 180° and a peel velocity of 0.3 m/minute, and the force (g) required for peeling was measured. Measurement of the residual adhesion After measurement of the peel resistance described above, the test specimen was applied to a stainless steel sheet. The force (g) required to peel this test specimen was again measured using an angle of 180° and a peel velocity of 0.3 m/minute. This force is reported as a percentage of the force required to peel the untreated reference tape. Example 1 The following were dissolved in 994 parts isooctane: 100 parts dimethylvinylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylvinyl siloxane copolymer with a viscosity of 65 Pa.s (650 poise) (methyl(perfluorobutylethyl)siloxane unit = 40 mole%, methylvinylsiloxane unit = 1.0 mole%, vinyl content = 0.2 weight%), 3 parts dimethylhydrogensiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylslioxane-methylhydro gensiloxane copolymer with a viscosity of 20 mPa.s (centipoise) (methyl(perfluorobutylethyl)siloxane unit = 40 mole%, dimethylsiloxane unit = 40 mole%, silicon-bonded hydrogen content = 0.3 weight%), 2 parts trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymer with a viscosity of 650 65 Pa.s (poise) (methyl(perfluorobutylethyl)siloxane unit = 40 mole%), and 1 part tetra(methylvinylsiloxane) cyclic. A fluorosilicone release agent composition was then prepared by the addition of chloroplatinic acid/divinyltetramethyldisiloxane complex in a quantity sufficient to give 500 ppm as platinum metal. The resulting composition was coated at 0.2 g/m 2 on the surface of polyethylene resin film. The curability was measured at 120°C and 140°C. The peel resistance and residual adhesion were measured on the cured film obtained by heating for 120 seconds at 150°C. These measurement results are reported in Table 1. Comparison Example 1 A fluorosilicone release agent composition was prepared as in Example 1, but in this case omitting the trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymer with a viscosity of 650 65 Pa.s (poise) (methyl(perfluorobutylethyl)siloxane unit = 40 mole%) that was used in Example 1. This composition was subjected to measurement of the curability, peel resistance, and residual adhesion as in Example 1, and the measurements are reported in Table 1. Comparison Example 2 A fluorosilicone release agent composition was prepared as in Example 1, but in this case adding hydroxyl-terminated dimethylpolysiloxane with a viscosity of 350 mPa.s (centipoise) in place of the trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymer with a viscosity of 65 Pa.s (650 poise) (methyl(perfluorobutylethyl)siloxane unit = 40 mole%) that was used in Example 1. This composition was subjected to measurement of the curability, peel resistance, and residual adhesion as in Example 1, and the results are reported in Table 1. Comparison Example 3 The following were dissolved in 994 parts toluene: 100 parts of a mixture of hydroxyl-terminated dimethylsiloxane-methylvinylsiloxane copolymer (methylvinylsiloxane unit = 2.5 mole%, vinyl content = 0.1 weight%) and dimethylvinylsiloxy-terminated dimethylpolysiloxane (vinyl content = 0.02 weight%), said mixture having a number average molecular weight = 400,000 (80 parts hydroxyl-terminated dimethylsiloxane-methylvinylsiloxane copolymer and 20 parts dimethylvinylsiloxy-terminated dimethylpolysiloxane), 2 parts dimethylhydrogensiloxy-terminated methylhydrogenpolysiloxane (silicon-bonded hydrogen content = 1.5 weight%) with a viscosity of 20 mPa.s (centipoise), and 1 part tetra(methylvinylsiloxane) cyclic. A silicone release agent composition was then prepared by the addition of chloroplatinic acid/divinyltetramethyldisiloxane complex in a quantity sufficient to give 500 ppm as platinum metal. The resulting composition was coated at 0.2 g/m 2 on the surface of polyethylene resin film. The curability was measured at 120°C and 140°C. The peel resistance and residual adhesion were measured on the cured film obtained by heating for 120 seconds at 150°C. These measurements are also reported in Table 1. Comparison Example 4 The following were dissolved in 994 parts toluene: 100 parts of a mixture of hydroxyl-terminated dimethylsiloxane-methylvinylsiloxane copolymer (methylvinylsiloxane unit = 2.5 mole%, vinyl content = 0.1 weight%) and dimethylvinylsiloxy-terminated dimethylpolysiloxane (vinyl content = 0.02 weight%), said mixture having average molecular weight = 400,000 (80 parts hydroxyl-terminated dimethylsiloxane-methylvinylsiloxane copolymer and 20 parts dimethylvinylsiloxy-terminated dimethylpolysiloxane), 2 parts dimethylhydrogensiloxy-terminated methylhydrogenpolysiloxane (silicon-bonded hydrogen content = 1.5 weight%) with a viscosity of 20 mPa.s (centipoise), 2 parts trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymer with a viscosity of 65 Pa.s (650 poise) (methyl(perfluorobutylethyl)siloxane unit = 40 mole%), and 1 part tetra(methylvinylsiloxane) cyclic. A silicone release agent composition was then prepared by the addition of chloroplatinic acid/divinyltetramethyldisiloxane complex in a quantity sufficient to give 500 ppm as platinum metal. The resulting composition was coated at 0.2 g/m 2 on the surface of polyethylene resin film. The curability was measured at 120°C and 140°C. The peel resistance and residual adhesion were measured on the cured film obtained by heating for 120 seconds at 150°C. These results are also reported in Table 1. Present Invention Comparison Examples Example 1 Comp. Example 1 Comp. Example 2 Comp. Example 3 Comp. Example 4 curability 120°C 30 30 30 30 30 140°C 20 20 20 20 20 peel resistance (g/2.5 cm) after 1 day 10 40 100 500 500 after 10 days 10 50 100 650 650 residual adhesion (%) 98 97 80 70 70

Claims: A fluorosilicone release agent composition comprising: (A) 100 parts by weight of an organopolysiloxane that contains at least 1 fluorine-containing organic group and at least 2 alkenyl groups in each molecule; (B) 0.1 to 40 parts by weight of an organohydrogenpolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule; (C) 0.01 to 20 parts by weight of an organopolysiloxane that contains at least 1 fluorine-containing organic group in each molecule, with the proviso that said organopolysiloxane (C) contains neither alkenyl groups nor silicon-bonded hydrogen groups; and (D) a catalytic amount of a hydrosilylation catalyst. The composition according to claim 1, wherein said fluorine-containing organic groups are independently selected from groups having the formula C n F 2n+1 -R-, groups having the formula C n F 2n+1 -R-O-R- and groups with the general formula wherein R is a divalent hydrocarbon group and n is an integer having a value of 1 to 20. The composition according to claim 1, wherein said organopolysiloxane (A) is selected from the group consisting of dimethylvinylsiloxy-terminated methyl(3,3,3-trifluoropropyl)siloxane-dimethylsiloxane-methylvinylsiloxane copolymers, dimethylvinylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylvinylsiloxane copolymers, dimethylvinylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-dimethylsiloxane-methylvinylsiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylvinylsiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-dimethylsiloxane-methylvinylsiloxane copolymers, dimethylvinylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymers, silanol-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxanemethylvinylsiloxane copolymers, and dimethylhexenylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylhexenylsiloxane copolymers. The composition according to claim 1, wherein said organopolysiloxane (C) is selected from the group consisting of trimethylsiloxy-terminated methyl(3,3,3-trifluoropropyl)siloxane-dimethylsiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorobutylethyl)siloxane-dimethylsiloxane copolymers, trimethylsiloxy-terminated methyl(perfluorohexylethyl)siloxane-dimethylsiloxane copolymers, and silanol-terminated methyl(perfluorobutyiethyl)siloxane-dimethylsiloxane copolymers. A release liner construction comprising a substrate coated with the composition of claims 1-4.

Inventors: HAMADA YUJI, SHIMODA KEIICHI, HAMADA, YUJI, SHIMODA, KEIICHI, HAMADA, YUJI, C/O DOW CORNING TORAY SILICONE, SHIMODA, KEIICHI, C/O DOW CORNING TORAY SILICONE
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: C08L83
IPC codes: C09D183, C08L83