Triethylenediamine and bicyclic amidine based catalysts and use in thermosettable compositions

Abstract: Described are novel triethylenediamine adducts of certain 4-hydroxy-substituted, 3,5-hydroxy-substituted and 2,3,4-hydroxy-substituted benzoic acid derivatives, and novel boron trifluoride complexes with cyclic amidines, which are useful for the conversion of thermosettable compositions. Also described are novel thermosettable compositions incorporating the adducts and complexes.

Description: The present invention pertains to triethylenediamine adducts of certain benzoic acid derivatives and their use as catalysts in thermosettable compositions. Thermosettable compositions are useful in many applications including for example their use as adhesive and coating compositions. Thermosettable compositions are largely based upon epoxy and/or anhydride and/or acid functionality. To prepare the thermosettable composition, the curable resin is blended with one or more catalysts. Depending upon the application, the catalyst can be designed to provide a fairly rapid cure after blending with the resin, or, the curing agent may be designed to provide some measure of latency. That is, the thermosettable resin does not gel over a period of time, e.g. during storage, and only upon heating converts the resin from a liquid (or thermoplastic) state to a tough, hard thermoset solid. Various compositions have been used as catalysts in thermosettable compositions. One group of curing agents includes certain complexes of Lewis acids and amines. For instance, U.S. Patent No. 2,824,083 describes certain amine-BF 3 complexes used as curing agents for polyepoxides. U.S. Patent Nos. 4,933,422 and 4,614,788 describe the use of certain adducts of imidazoles with organic acids having pK a values of 0.5 to 5.0. U.S. Patent No. 2,824,083 describes the use of BF 3 addition products with certain amines, amides, phenol or ether, dissolved in a liquid polyol such as a liquid polyalkylene glycol. U.S. Patent No. 2,839,495 describes the use of the combination of an acid anhydride and a BF 3 complex such as a BF 3 -amine complex to resinify polyepoxides. U.S. Patent No. 3,519,604 describes the use of a polycarboxylic acid anhydride and certain 3- or 4-amino pyridines in combination with a polyepoxy compound to form a curable composition. Japanese KOKAI No. 64-3171A (January 6, 1989) describes certain amino pyridine acid addition salts with dihydroxybenzoic acid derivatives, used as accelerators for curing epoxy resins. Additional background information on catalysts and resins employed in thermosettable compositions can be found in U.S. Patent Nos. 4,816,500 and 4,871,806 and European Patent Application Nos. 90308471.3 (Published February 6, 1991) and 88119031.8 (Published May 24, 1989). A first aspect of the invention provides novel triethylenediamine adducts that are useful in preparing thermosettable compositions. The compounds of this aspect of the invention are triethylenediamine adducts of benzoic acid derivatives having the formula: wherein R 1 , R 2 , R 3 , R 4 , R 5 , R 6 and R 7 , which can be the same or can be different from one another, are H, C 1 to C 10 alkyl; phenyl; benzyl; halo; -OR 8 wherein R 8 is C 1 to C 10 alkyl or phenyl; -COOR 9 wherein R 9 is H, C 1 to C 10 alkyl or phenyl; or -NR 10 R 11 wherein R10 and R 11 can be the same or can differ from one another, are H or C 1 to C 10 alkyl. Another aspect of the present invention provides a thermosettable composition. The thermosettable composition comprises a curable resin material, such as a resin having epoxy and/or anhydride and/or acid functionality, and a catalytic amount of a triethylenediamine adduct in accordance with the first aspect of the invention. Additional aspects of the invention include processes for preparing the compounds of the invention and for preparing and curing the above-specified thermosettable compositions. The invention thus provides compounds that are useful as catalysts in thermosettable compositions, thermosettable compositions, and processes for their preparation and use. Additional embodiments, as well as features and advantages of the invention, will be readily apparent from the following description. For the purposes of promoting an understanding of the principles of the invention, reference will now be made to certain embodiments thereof and specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of the invention is thereby intended, such alterations, further modifications and applications of the principles of the invention as described herein being contemplated as would normally occur to one skilled in the art to which the invention pertains. The triethylenediamine (also sometimes referred to as TED, 1,4-diazabicyclo[2.2.2]octane, or Dabco) -employed in the invention can be obtained commercially or by known processes utilizing readily available starting materials (see, e.g., Krause et al., British Patent 871,754 (1958)). The triethylene diamine is reacted with a benzoic acid derivative of the formula: wherein R 1 , R 2 , R 3 , R 4 , R 5 , R 6 and R 7 , which can be the same or can be different from one another, are H, C 1 to C 10 alkyl; phenyl; benzyl; halo; -OR 8 wherein R 8 is C 1 to C 10 alkyl or phenyl; -COOR 9 wherein R 9 is H, C 1 to C 10 alkyl or phenyl; or -NR 10 R 11 wherein R 10 and R 11 can be the same or can differ from one another, are H or C 1 to C 10 alkyl. The 4-hydroxy-substituted, 3,5-hydroxy-substituted or 2,3,4-hydroxy-substituted benzoic acid derivatives employed in the invention may be obtained commercially or may be prepared using conventional techniques well within the purview of the ordinarily skilled artisan. The triethylenediamine adducts can be prepared by reaction of triethylenediamine with the selected benzoic acid derivative so as to form the adduct. For example, The acid can be dissolved in a suitable solvent such as acetone, ethyl acetate or toluene. The triethylenediamine can then be added portionwise and the reaction promoted with heat. Water may be removed by azeotropic distillation when using toluene to form a dry solution. After cooling, the precipitated adduct can be recovered by filtration, washed with solvent, and dried. Thermosettable compositions of the invention are prepared by blending a triethylenediamine adduct of the invention into a curable resin material in the desired catalytic amount, typically about 1 to about 10 weight parts per 100 weight parts of resin. The curable resin material for use in the invention can for example contain epoxy functionality, and/or anhydride functionality and/or acid functionality, and have application in adhesive or coating compositions, among others. Where the catalyst has low solubility in the resin of interest, it is preferred to grind the catalyst to a small particle size prior to blending in order to assist in dispersing the catalyst in the resin. After its preparation, the thermosettable composition will be conventionally employed. The catalysts of the invention may, of course, be used in the thermosettable composition in combination with other conventional additives, for instance curing agents such as phenol-novolac, cresol-novolac and 3,3'-diallyl-4,4'-dihydroxybisphenol A; amine compounds such as 4,4'-methylenebis(2-ethylaniline), 4'4-methylenebis(2,6-diethylaniline) and 4,4'-methylenebis(2-ethyl-6-methylaniline); acid anhydrides such as Nadic Methyl Anhydride (methyl-bicyclo[2.2.1]heptene-2,3-dicarboxylic anhydride), phthalic anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, trimellitic anhydride, and pyromellitic anhydride; amide compounds such as dicyandiamide; and dihydrazide compounds such as adipic dihydrazide and isophthalic dihydrazide. Additional conventional additives include dyes, pigments, antioxidants, UV stabilizers, fillers, solvents, reinforcing materials and the like. The following Examples are provided by way of illustration and not by way of limitation. EXAMPLE I Preparation of TED Adducts The following procedure was used to prepare the adducts set forth and characterized below. A 1000 ml four-neck flask, equipped with a mechanical stirrer, thermometer, Dean Stark trap with condenser, and a powder funnel, was charged with the benzoic acid derivative (0.306 mole) and either acetone, ethyl acetate or toluene (600 ml). This mixture was warmed to 40 °C and the TED was added in portions through the powder funnel. A slight exothermic reaction occurs during the TED addition. After addition of all of the TED, the powder funnel was washed with solvent (50 ml) and replaced with a stopper. The reaction mixture was heated to reflux and the water removed by azeotropic distillation, when using toluene, until the solution was dry. A total of 50 ml of wet toluene was distilled off after no more water was detected coming over. The reaction mixture was then allowed to cool to room temperature. The precipitated solids were filtered, washed with solvent, and dried to give the desired TED adduct. The following compounds were prepared as above: TED-3,5-Dihydroxybenzoic Acid, m.p. 244-248 dec, Combustion analysis Actual (theory); C: 58.40 (58.64); H: 6.91 (6.81); N: 10.54 (10.52). TED-2,3,4-Trihydroxybenzoic Acid, m.p. 180-185 dec, Combustion analysis Actual (theory); C: 55.45 (55.31); H: 6.48 (6.43); N: 9.85 (9.92). TED-Gallic Acid, m.p. 199-200, Combustion analysis Actual (theory); C: 55.16 (55.31); H: 6.44 (6.43); N: 9.86 (9.92); O: 28.35 (28.34). TED-2 Gallic Acid, m.p. >200 dec, Combustion analysis Actual (theory); C: 53.21 (53.10); H: 5.37 (5.35); N: 6.20 (6.19). TED-4-Hydroxybenzoic Acid, m.p. 195 dec, Combustion analysis Actual (theory); C: 62.46 (62.38); H: 7.32 (7.25); N: 11.12 (11.19). EXAMPLE II Testing of TED Adducts The catalytic properties of the adducts prepared in Example I were evaluated as follows. The adducts were dispersed at 10 parts per 100 parts of resin (EPON 828, epoxy equivalent weight (EEW) about 185) along with 1.4% of a hydrophobic fumed silica rheology control agent. Dispersion was accomplished on 250 g batches of resin mix using a high shear disperser, or Dispermat CV equipped with a 20 mm blade and operated at 3000 rpm for a period of time sufficient to achieve adequate dispersion visually, generally about 3-6 minutes. Ratios of viscosity build were calculated at one and three day intervals by dividing the 1 and 3 day heat aged (at 55°C) viscosity values by the initial viscosities. Longer term latency was measured by continuing to monitor viscosity build over time, with daily checks to monitor polymerization. Gel times were tested on twenty gram portions of the above mixes in 18 by 150 mm test tubes, using a Sunshine gel meter equipped with a thermostatically controlled silicone oil bath. The oil bath permitted precise temperature regulation of the test sample to within plus or minus 0.2°C. Gelation is noted in this instrument by measurement of viscosity build during polymerization. At a predetermined viscosity point, a highly reproducible torque is registered by the instrument, i.e., gel point. The results of the Sunshine gel time (min.) and latency ratio testing are set forth in Table 1. TED Adduct of /--Sunshine Gel Time--/ Heat Aged (55°C) Latency Ratio 120 °C 150 °C 3 day 1 day Gallic Acid 19.9 5.4 0.9 1.0 2,3,4-THBA 14.1 5.3 1.11 0.98 3,5-DHBA 13 9.7 0.94 1.05 4-HBA 8.3 4 14.2 1.6 * Abbreviations: THBA = trihydroxybenzoic acid; DHBA = dihydroxybenzoic acid; HBA = hydroxybenzoic acid. These data show that the TED adducts tested successfully catalyzed the hardening of the epoxy resin upon heating. Further, the data show that the TED adducts with 3,5-hydroxy-substituted benzoic acid and derivatives thereof (e.g. gallic acid) and with 2,3,4-trihydroxybenzoic acid and derivatives thereof unexpectedly provide superior latency for applications in which high latency and long pot lives are required. TED adducts with 4-hydroxybenzoic acid and derivatives thereof show the advantageous combination of intermediate latency and very high reactivity upon heating. Additionally, in the 55°C aging testing, the TED adducts with 3,5-hydroxy-substituted benzoic acid derivatives and 2,3,4-hydroxy-substituted derivatives proved very highly latent. For example, the thermosettable composition containing the TED-gallic acid adduct remained non-gelled for a period of 84+ days, retaining substantially the same viscosity values over this period. The TED-3,5-dihydroxybenzoic acid and TED-2,3,4-trihydroxybenzoic acid adducts remained non-gelled for a period of more than 24 days. All publications cited herein are indicative of the level of ordinary skill in the art and are hereby incorporated by reference herein in their entirety as if each had been individually incorporated by reference. While the invention has been illustrated and described in detail in the foregoing description, the same is to be considered as illustrative and not restrictive in character, it being understood that only the preferred embodiments have been described and that all changes and modifications that come within the spirit of the invention are desired to be protected.

Claims: A compound suitable for use as a catalyst in thermosettable compositions, the compound being a triethylenediamine adduct of a benzoic acid derivative having the formula I, II or III: wherein R 1 , R 2 , R 3 , R 4 , R 5 , R 6 and R 7 , which can be the same or can be different from one another, are H, C 1 to C 10 alkyl; phenyl; benzyl; halo; -OR 8 wherein R 9 is H, C 1 to C 10 alkyl or phenyl; or -NR 10 R 11 wherein R 10 and R11 can be the same or can differ from one another, are H or C 1 to C 10 alkyl. The compound of claim 1 which is a triethylenediamine adduct of a 3,5-hydroxy-substituted benzoic acid derivative of the formula I. The compound of claim 2 wherein R 2 is -OH. The compound of claim 2 which is a triethylenediamine adduct of 3,5-dihydroxybenzoic acid. The compound of claim 3 which is a triethylenediamine adduct of 3,4,5-trihydroxybenzoic acid. The compound of claim 1 which is a triethylenediamine adduct of 2,3,4-trihydroxy-substituted benzoic acid derivative of the formula II. The compound of claim 6 which is a triethylenediamine adduct of a 4-hydroxy-substituted benzoic acid derivative of the formula III. A thermosettable composition, comprising a curable resin material and a catalytic amount of a triethylenediamine adduct of a benzoic acid derivative having the formula I, II or III: wherein R 1 , R 2 , R 3 , R 4 , R 5 , R 6 and R 7 , which can be the same or can be different from one another, are H, C 1 to C 10 alkyl; phenyl; benzyl; halo; -OR 8 wherein R 8 is C 1 to C 10 alkyl or phenyl; -COOR 9 wherein R 9 is H, C 1 to C 10 alkyl or phenyl; or -NR 10 R 11 wherein R 10 and R 11 can be the same or can differ from one another, are H or C 1 to C 10 alkyl. The thermosettable composition of claim 8 which includes a triethylenediamine adduct of a 3,5-hydroxy-substituted benzoic acid derivative of the formula I. The thermosettable composition of claim 9 wherein R 2 is -OH. The thermosettable composition of claim 9 which includes a triethylenediamine adduct of 3,5-dihydroxybenzoic acid. The thermosettable composition of claim 10 which includes a triethylenediamine adduct of 3,4,5-trihydroxybenzoic acid. The thermosettable composition of claim 8 which includes a triethylenediamine adduct of a 2,3,4-hydroxy-substituted benzoic acid derivative of the formula II. The thermosettable composition of claim 13 which includes a triethylenediamine adduct of 2,3,4-trihydroxybenzoic acid.

Inventors: JOHNSON JOHN R, JOHNSON, JOHN R.
Applicants: REILLY IND INC, REILLY INDUSTRIES, INC.
Application year: 1994
Main classification: C08G59
IPC codes: C07C65, C08G59, C07D487