Catalytic conversion of direct process high-boiling component to chlorosilane monomers in the presence of hydrogen chloride

Abstract: The present invention is a process for converting a high-boiling component resulting from the reaction of an organochloride with silicon into commercially more desirable monosilanes. The process comprises contacting the high-boiling component with hydrogen chloride at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from activated carbon, platinum supported on alumina, zeolite, AlCl₃ and AlCl₃ supported on a support selected from carbon, alumina and silica.

Description: The present invention is a process for converting a high-boiling component, resulting from the reaction of an organochloride with silicon, into more commercially desirable monosilanes. The process comprises contacting the high-boiling component with hydrogen chloride at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from platinum supported on alumina, zeolite, AlCl 3 and AlCl 3 supported on a support selected from carbon, alumina and silica. The high-boiling component useful in our process results from a process typically referred to as the "Direct Process," where an organohalide is reacted with silicon in the presence of a suitable catalyst to form monosilanes. The Direct Process is described more fully in US-A 2,380,995 and US-A 2,488,487. It is the main commercial process by which organohalosilanes (i.e. monosilanes), for example dimethyldichlorosilane and trimethylchlorosilane, are formed. These organohalosilanes are reactive compounds which can undergo numerous reactions to form a variety of useful silicon containing compounds and polymers. A major commercial use of organohalosilanes is in the production of polysiloxane polymers which are useful as heat transfer fluids, lubricants and the like and which can be further processed, for example, to form silicone elastomers, resins, sealants and adhesives. Operation of the Direct Process results not only in the production of the desirable monosilanes, but also in a high boiling component typically considered to be all materials with a boiling point higher than the particular diorganodihalosilane produced in the process. The high-boiling component is a complex mixture that includes compounds containing SiSi, SiOSi, SiCSi, SiCCSi and SiCCCSi linkages in the molecules. Typical compounds are described in US-A 2,598,435 and US-A 2,681,355. The high-boiling component may also comprise silicon containing solids and soluble and insoluble compounds of copper, aluminum and zinc. In current commercial operations for performing the Direct Process, the high-boiling component can constitute as much as ten percent of the resultant product. Therefore, it is desirable to convert the high-boiling component into more commercially desirable products to both reduce low-value by-products and to improve raw material utilization. The prior art for converting the high-boiling component of the Direct Process into more usable monosilanes is represented by US-A 2,598,435; US-A 2,681,355; US-A 2,709,176 and US-A 2,842,580. The aforementioned problems of the prior art are solved by a catalyzed process for the high conversion of a high-boiling component produced by the Direct Process to monosilanes. Further, it is unexpected that such a catalyzed process could employ readily available and inexpensive catalysts which can be easily retained in a reactor and have a long life in said process. Our process may be run in any standard type reactor for contacting silanes and hydrogen chloride. The process may be run as a batch process, semi-continuous or continuous process. The process can be run, for example, in a fixed-bed reactor, a stirred-bed reactor or a fluidized-bed reactor. Preferred is when the process is run as a continuous process in a fluidized-bed reactor. This present process is useful for converting a high-boiling component resulting from the reaction of an organochloride with silicon to form monosilanes. The term "high-boiling component" refers to those materials with a boiling point above that of the diorganodichlorosilane formed by the reaction of the organochloride with silicon. For example when methyl chloride is reacted with silicon, the diorganodichlorosilane will be dimethyldichlorosilane and the high-boiling component will comprise those materials having a boiling point greater than that of dimethyldichlorosilane, i.e. greater than 70°C. In a typical process for reacting an organochloride with silicon, the reaction is conducted at a temperature of 270°C. to 350°C., in the presence of a suitable catalyst. Gaseous product and unreacted feed are continuously removed from the process. The removed gaseous product and unreacted feed are subsequently distilled to remove monosilanes leaving behind a high-boiling component. The high-boiling component is a complex mixture that can include compounds containing SiSi, SiOSi, SiCSi, SiCCSi and SiCCCSi linkages alone or in combination in each molecule. The high-boiling component can include silicon containing solids and soluble and insoluble compounds of copper, aluminum and zinc. The high-boiling component may contain, for example, organic substituted and non-organic substituted silanes, disilanes, trisilanes, disiloxanes, silane oligomers, siloxane oligomers, silalkylenes and silicon containing solids, all of which may be converted to monosilanes by our process. The present process is especially useful for converting polysilanes in the high-boiling component to monosilanes, where the polysilanes are described by formula R a H b Si n Cl 2n+2-a-b and where each R is a radical independently selected from alkyls comprising one to six carbon atoms, n = 2 to 20, a = 0 to 2n+2, b = 0 to 2n+2 and a+b = 0 to 2n+2. The polysilanes useful in the present process can consist of n number of silicon atoms where n is an integer from two to 20. Preferred is when n equals two. The polysilanes can be substituted with a=0 to 2n+2 number of R radicals, where each R is independently selected from alkyls of one to six carbon atoms. The radical R can be methyl, ethyl, propyl and t-butyl. Preferred is when R is methyl. The polysilanes in the high-boiling component can contain b number of hydrogen atoms substituted on the silicon atoms, where b = 0 to 2n+2. The polysilanes in the high-boiling component can also contain from zero to 2n+2 chlorine atoms. The high-boiling component can contain silalkylenes, where each silalkylene can comprise one or more silalkylene bonds described by formula Si(C) z Si and z is an integer from one to six. Preferred is when z is an integer from one to three. The silalkylene molecules can comprise SiSi bonds and SiOSi bonds as well as silalkylene bonds. The silicon atoms of the silalkylene molecules can be further substituted with the radical R, where R is as previously described, with chlorine and with hydrogen. Preferred is when the silicon atoms of the silalkylenes are substituted with methyl. The preferred high-boiling component is one resulting from the reaction of methyl chloride with silicon, the high-boiling component having a boiling point greater than 70°C. This high-boiling component can contain Me 2 ClSiSiMe 2 Cl, Me 2 ClSiSiMeCl 2 , MeCl 2 SiSiMeCl 2 , Me 2 ClSiSi(Me)(Cl)SiMeCl 2 , Me 2 ClSiCH 2 SiMe 2 Cl, Me 2 ClSiCH 2 SiMeCl 2 , MeCl 2 SiCH 2 SiMeCl 2 , Me 2 ClSi(CH 2 ) 2 SiMeCl 2 , Me 2 ClSi(CH 2 ) 3 SiMeCl 2 , Me 2 ClSiCH 2 Si(Me)(Cl)SiMeCl 2 , Me 2 ClSiCH 2 Si(Me)(Cl)CH 2 SiMeCl 2 and Me 2 ClSiOSiMeCl 2 , where Me is methyl, all of which may be converted to monosilanes by the present process. The high-boiling component is contacted with hydrogen chloride, where the ratio of the weight of high-boiling component added to the reactor to the weight of hydrogen chloride is within a range of 5:1 to 0.05:1. Preferred is where the ratio of the weight of high-boiling component to the weight of hydrogen chloride is within a range of 3:1 to 1:1. The process is conducted at a temperature within a range of 250°C. to 1000°C. A preferred temperature is within a range of 450°C. to 550°C. While pressure is not critical to the present process, it is preferred that the process be run at a gauge pressure not to exceed 6.9 MPa (1000 psi). More preferred is when the process is run at a pressure not exceeding 689.5 kPa (100 psi). The process is conducted in the presence of a catalyst selected from platinum supported on alumina, zeolite, AlCl 3 and AlCl 3 supported on a support selected from carbon, alumina and silica. Activated carbon catalyst is given as an example and is not within the scope of the present invention. By "activated carbon", it is meant a microcrystalline, nongraphite form of carbon, having an internal porosity, the carbon having been activated by any standard process known in the art for producing activated carbon, for example, chemical activation or gas activation as described in Kirk-Othmer, Concise Encyclopedia of Chemical Technology, John Wiley & Sons publishers, 1985, p. 204 to 205. The activated carbon can be in the form of, for example, flakes, chips, particles, powder or pellets. In general, it is preferred that the activated carbon have a diameter within a range of 0.001 mm to 20 mm. More preferred is when the activated carbon has a diameter within a range of 0.01 mm to 5 mm and a surface area greater than 1000 m 2 /g. The weight of activated carbon in relation to the weight of high-boiling component and hydrogen chloride added to the process will depend upon such factors as the type and size of the activated carbon, the chemical composition of the high-boiling component, the process temperature and the type of reactor employed. When the process is run as a batch or a semi-continuous process, a useful weight of activated carbon is considered to be within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component and the hydrogen chloride added to the process. The catalyst can be platinum supported on alumina. The amount of platinum can be from 0.1 to 10 weight percent platinum. Preferred is when the amount of platinum is within a range of 0.5 to 2.0 weight percent. The concentration of platinum retained on an alumina support used in the process will depend upon such factors as discussed for the use of activated carbon. In general, when the process is run as a batch or semi-continuous process a useful concentration of platinum on alumina support is considered to be that which provides a catalyst concentration within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component and the halogen chloride added to the process. The catalyst can be a zeolite. The zeolite catalyst can be of the natural occurring type, for example, chabazite, mordenite, erionite, faujasite and clinoptilolite. The zeolite catalyst can be a synthetic zeolite of the zeolite A, X, L or Y types or of the high silica synthetic zeolite types such as ZSM-5 and ZSM-11. Preferred is when the zeolite catalyst is selected from a group of synthetic zeolite catalyst consisting of LZ-Y-64, LZ-Y-74 and LZ-M-8. The concentration of zeolite catalyst used in the process will depend upon such factors as discussed for the use of activated carbon. In general, when the process is run as a batch or semi-continuous process, a useful concentration of zeolite is considered to be within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component and the hydrogen chloride added to the process. The catalyst can be AlCl 3 . The concentration of AlCl 3 catalyst used in the process will depend upon such factors as discussed for the use of activated carbon. In general, when the process is run as a batch or semi-continuous process, a useful concentration of AlCl 3 catalyst is considered to be within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling components and the hydrogen chloride added to the process. The catalyst can be AlCl 3 supported on a support selected from carbon, alumina and silica. The amount of AlCl 3 retained on the support is within a range of 0.1 to 30 weight percent. Preferred is when the amount of AlCl 3 is within a range of 0.5 to 5.0 weight percent. The concentration of supported AlCl 3 will depend upon such factors as discussed above for the use of activated carbon. In general, when the process is run as a batch or a semi-continuous process, a useful concentration of supported AlCl 3 catalyst is considered to be within a range of 0.1 to 30 weight percent of the combined weight of the high-boiling component and the hydrogen chloride added to the process. The optimum contact time for the high-boiling component and hydrogen chloride with the catalyst will depend on factors such as the type of catalyst, chemical composition of the high-boiling component and the degree of conversion and product selectivity desired. In general, contact times within a range of one second to five hours are useful. Longer contact times may be employed, but appear to offer no advantage and may result in excessive scission of silicon-carbon bonds and silicon-hydrogen bonds present in the monosilanes. A preferred contact time in a continuous reactor system is within a range of one second to five minutes. If desired, the monosilane containing product of the present process can be further separated by standard means, for example, distillation to separate the monosilanes from a high-boiling component and the high-boiling component can then be recycled to the process. The following examples are provided to facilitate understanding and to demonstrate the effectiveness of the present invention. Example 1 (Not within the scope of the present invention). A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the absence of catalyst. The reactor consisted of a 2.5 cm diameter by 50 cm length quartz tube maintained at 500°C. The high-boiling component consisted of, by weight, 55% methylchlorodisilane, 5% disilmethylenes, 35% other polysilanes and silalkylenes and 5% silicon containing solids. The high-boiling component was fed at a rate of 117 g/h to the reactor and hydrogen chloride was fed to the reactor at 50 g/h. The process was conducted for one hour with gaseous product exiting the reactor being collected in a cold condenser. The condensed product was analyzed by gas chromatography using a thermal conductivity detector (GC-TC) and found to consist of 59 weight percent chlorosilane monomers. Chlorosilane monomers detected included HSiCl 3 , SiCl 4 , MeHSiCl 2 , Me 3 SiCl, MeSiCl 3 and Me 2 SiCl 2 . Other species detected in the condensed product included methylchlorodisilanes, disilmethylenes, polysilanes and silalkylenes. Example 2 (Not within the scope of the present invention). A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the presence of a packed bed of activated carbon catalyst. The process was conducted similar to that described in Example 1, with the high-boiling component composition, reactor design and reaction temperature being the same. The reactor was packed with 12 g of Calgon™ BPL 1 mm by 3.3 mm activated carbon pellets (Calgon, Pittsburgh, PA). The high-boiling component was fed to the reactor at a rate of 92 g/h and hydrogen chloride was fed to the reactor at a rate of 57 g/h. Gaseous product exiting the reactor was collected and analyzed as described in Example 1. The collected product was found to comprise 93 weight percent chlorosilane monomers and included those chlorosilane monomers described for the product of Example 1. Example 3 (Not within the scope of the present invention). A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the presence of activated carbon catalyst in a fluidized-bed reactor. The composition of the high-boiling component, reactor design and process temperature was similar to that described in Example 1. The reactor was filled with 25 g of a 0.1 mm to 0.3 mm pulverized activated carbon (North American, Columbus, OH). The high-boiling component was fed to the reactor at a rate of 75 g/h and hydrogen chloride was fed to the reactor at a rate of 57 g/h. The process was conducted for 24 hours with gaseous product exiting the reactor being collected and analyzed as described in Example 1. The collected product was determined to consist of similar species as identified in Example 1. Of the product collected, 88 weight percent was chlorosilane monomers. Example 4 A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the presence of a zeolite catalyst. The process was conducted similar to that described in Example 1, with the high-boiling component composition, reactor design and reaction temperature being the same. The reactor was packed with 15 g of zeolite LZ-Y-74 extruded 1.6 mm pellets (UOP Inc., Tarrytown, NY). The high-boiling component was fed to the reactor at a rate of 75 g/h and hydrogen chloride was fed to the reactor at a rate of 57 g/h. The process was conducted for one hour with gaseous product exiting the reactor being collected and analyzed as described in Example 1. The collected product was determined to consist of similar species as described in Example 1. Of the product collected, 81 weight percent was chlorosilane monomers. Example 5 A high-boiling component resulting from the reaction of methyl chloride with silicon was contacted with hydrogen chloride in the presence of a platinum on alumina. The process was conducted similar to that described in Example 1, with the high-boiling component composition, reactor design and reaction temperature being the same. The reactor was packed with 16 g of a one weight percent platinum on 1.6 mm alumina spheres (UOP Inc., Tarrytown, NY). The high-boiling component was fed to the reactor at a rate of 88 g/h and hydrogen chloride was fed to the reactor at a rate of 57 g/h. The process was conducted for one hour with gaseous product exiting the reactor collected and analyzed as described in Example 1. The collected product was determined to consist of similar species as described in Example 1. Of the product collected, 82 weight percent was chlorosilane monomers.

Claims: A process for converting a high-boiling component, resulting from the reaction of an organochloride with silicon, to monosilanes, the process consisting of contacting the high-boiling component with hydrogen chloride at a temperature within a range of 250°C. to 1000°C. in the presence of a catalyst selected from platinum supported on alumina, zeolite, AlCl 3 and AlCl 3 supported on a support selected from carbon, alumina and silica. A process according to claim 1 where the process is conducted at a gauge pressure not to exceed 6.9 MPa (1000 psi). A process according to claim 1 where the ratio of the weight of the high-boiling component to the weight of the hydrogen chloride added to the process is within a range of 5:1 to 0.05:1. A process according to claim 1 where the high-boiling component results from the reaction of methyl chloride with silicon and the high-boiling component comprises polysilanes, silalkylenes, silicon containing solids and soluble and insoluble compounds of copper, aluminum and zinc. A process according to claim 1 where the high-boiling component comprises polysilanes described by formula R a H b Si n Cl 2n+2-a-b , where each R is a radical independently selected from alkyls comprising one to six carbon atoms, n = 2 to 20, a = 0 to 2n+2, b = 0 to 2n+2 and a+b = 0 to 2n+2. A process according to claim 4, where the high-boiling component comprises silalkylenes which contain one or more silalkylene bonds and are described by formula Si(C) z Si and z = 1, 2 or 3. A process according to claim 1 where the catalyst is selected from zeolite LZ-Y-74 and platinum supported on alumina.

Inventors: CHADWICK KIRK MICHAEL, DHAUL AJAY KUMAR, HALM ROLAND LEE, JOHNSON RICHARD GORDON, CHADWICK, KIRK MICHAEL, DHAUL, AJAY KUMAR, HALM, ROLAND LEE, JOHNSON, RICHARD GORDON
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1994
Main classification: C07F7
IPC codes: C01B33, B01J29, B01J21, C07F7, B01J23