Welding method and welded structure

Abstract: A method of welding two plates (1) together along a substantially vertical weld line between the two plates involves the use of a weld pool support device (8) having internally formed channels (13, 14, 15) through which flows a liquid coolant maintained considerably below ambient temperature by a cooling device (12).

Description: The invention relates to a method according to the preamble of claim 1 for joining two metal plates together by welding. Large spherical tanks are usually used for transportation and storing of liquefied natural gas (LNG). The temperature of LNG is about -163°C, which places special demands on the choice of material for an LNG-tank and on the technique used for producing such a tank. The diameter of a typical spherical LNG-tank is from 30 m to 40 m. Such a tank is preferably made of welded aluminium plates, because the extremely low temperature of the contents of the tank does not have a deleterious effect on the strength properties of aluminium. The thickness of aluminium plates used for manufacturing LNG-tanks of this kind is usually from about 25 mm to about 60 mm. The invention relates in particular to joining such aluminium plates through welding, but the invention is also applicable to other welding operations of a similar kind, e.g. to the welding of titanium plates. The material of weldable plates suitable for the production of an LNG-tank is, for instance, according to the DIN-standard AlMg4,5Mn, which corresponds to the U.S. ASTM-standard plate A-5083. The application of the invention is, however, not limited to these plate qualities, since the invention can generally be applied to weldable aluminium plates or other metal plates having substantially similar weldability properties, e.g. titanium plates. The invention relates to the production of a welded joint having a substantially vertical component. This means a weld line that is vertically disposed to such an extent, that the molten metal (or weld pool) has a tendency to run out of the weld groove due to gravity. This tendency appears of course most strongly when the weld groove extends vertically, but may also appear to some extent complicating the welding operation, when the angle of the weld groove to the horizontal is as small as 30°. According to the known art of vertical welding, a cooled weld pool support device is used, the dam member of which moves upwards in the direction of the weld groove as the welding proceeds in the same upward direction. When welding steel, a piece of copper has usually been used as the dam member in a weld pool support device, but when welding aluminium difficulties have occurred, because a copper dam member readily adheres to melted aluminium. For solving this problem it has been suggested to use as the dam member a piece of graphite, see US-A-3 585 343 or Welding Journal, July 1973, pages 440-448. However, a graphite dam member wears out far too rapidly to be a satisfactory solution to the problem. US-A-3582608 describes a method of welding iron and steel plates in which the dam member comprises a water-cooled copper shoe. The welding wire tip is reciprocated horizontally to fill the weld grove layer, thus reducing the welding speed to a very low value and putting high demands on shoe cooling. The object of the invention is to eliminate the difficulties typically experienced in the known art of vertical welding with a cooled weld pool support device. The characteristics of the invention are set out in the following claim 1. The invention is based on the observation that a considerable intensification of the cooling of the weld pool support device will make it possible to use a piece of copper as the dam member, not only for welding steel, but also in the welding of aluminium plates, without any substantial risk of adherence problems between the dam member and the weld fillet. Preferably, the temperature of the liquid coolant fed to the weld pool support device is kept in the range of +8°C to -20°C, more preferably in the range of 0°C to -10°C. Clean water may be used as the coolant, if the coolant is not cooled below the freezing-point of water, otherwise other fluids have to be used, such as an aqueous solution, to which at least one additive, such as glycol has been added to lower the freezing-point of water far enough to prevent freezing during use. The disposition of the cooling duct in the dam member, the rate at which liquid coolant is passed therethrough and the temperature of the liquid coolant supplied to the dam member should be chosen to create an intensity of cooling such that under steady-state conditions the molten metal of the weld forms a solidified layer on the side facing the dam member. At a distance of one or a few centimetres above the lower edge of the dam member, the solidified layer must be strong enough to hold the residual molten metal in place in the groove where it finally solidifies fully to form the fillet after the weld pool support device has passed. When applying the method of the invention, it is important that the length of the dam member, measured in the direction of the weld groove, is sufficient to provide effective cooling. The preferred length of the cooled portion of the dam member in the direction of the weld groove is from about 7 cm to about 12 cm, preferably from 8 cm to 10 cm. Of course a longer dam member may also be used, but this only makes the weld pool support device more expensive and possibly more difficult to use without providing any noticeable improvement in the welding process. The width of the dam member should exceed the width of the weld groove at the front surface of the plates (typically by between 20 and 40 mm) and for a groove of width 30 mm a dam member some 60 mm wide has proved to be suitable. When welding aluminium plates, it is desirable to ensure that the cooling induced by the weld pool support device does not have any harmful effect on the edge areas of the plates at the sides of the weld groove. The weldability of an aluminium plate improves when it is slightly warmed. This is true up to a temperature of about 150°C. For this reason, when applying the invention, the aim should be that the temperature of the edge area of the welded aluminium plates along each side of the weld groove clearly exceeds 100°C. This has a favourable effect on the welding speed. When applying the invention, the dam member of the weld pool support device can favourably be made of copper, but other materials can also be used, such as aluminium, stainless steel or a ceramic material. The resistance to wear of all these materials has proved to be sufficient to make a reliable device. If a weld joint length of at least 50 metres can be welded with one dam member, the resistance to wear of the weld pool support device is judged to be satisfactory. Because of the invention, the joining of relatively thick aluminium plates by means of a welded joint can be carried out from just one side. The use of one-sided welding instead of two-sided, noticeably lowers the welding costs. When using the method of the invention it is recommended to use, as known per se, a backing at the root side of the weld groove. The backing which can be moving or stationary can be of ceramic material or some other material resistant to heat. To prevent the backing from adhering to the weld it can be isolated from the welded joint by a layer of fibrous refractory material which, e.g. in the form of glass fibre tape, could be fastened to the root side of the weld groove or to the surface of the backing. Due to the invention, the welding speed can be increased noticeably compared to the speed achieved with known methods. In favourable cases the welding speed may even be nearly doubled. When applying the invention, the welding speed is advantageously from 2 to 5 cm/min when the thickness of the aluminium plates to be welded is from 25 to 60 mm. The welding speed is a very important factor, because there are typically between 300 and 400 m of joints to be welded according to the invention in one spherical LNG-tank. Further, relatively large variations in the form and width of the weld groove may be tolerated when applying the invention. These kinds of variations appear when the form of the plates to be welded together do not exactly correspond to one another. According to the known welding methods variations of only up to ± 1 mm in the crosswise direction of the weld groove have normally been acceptable, whereas, when applying the invention, variations of even up to ± 5 mm in the crosswise direction of the groove may be allowed. Further, it has been discovered that a structure welded according to the method of the invention usually has enhanced structural strength compared to a corresponding structure produced by conventional prior art welding methods. The invention also extends to a welded structure, especially to a spherical tank made of aluminium plates, which has been produced by applying the method of the invention. The invention will now be further described in greater detail, by way of example, with reference to the accompanying drawings, in which Figure 1 schematically shows, in longitudinal section, a weld groove during application of the method according to the invention, Figure 2 is a section on line II-II of Figure 1, and Figure 3 is a schematic view of a spherical LNG-tank made by the method of the invention. In the drawings, 1 indicates plates to be joined by welding, 2 a welding wire and 3 a feeder unit for advancing the welding wire 2 to a weld site. Between the free end of the welding wire 2 and the material to be welded a conventional welding arc 4 is formed, which causes melting of the metal required for the welding process in a weld groove 5. Thus, following start-up of a welding operation, there is a certain volume of molten metal 16 which forms a pool under the arc 4. The weld groove 5 is, as will be apparent from Figure 2, V-shaped and its welding side is to the right in Figure 2 and its root side is to the left. At the root side of the weld groove 5 there is a backing 6, which can be separated from the plates 1, e.g. with glass fibre tapes 7, to minimize risk of adherence of the backing 6 to the plates 1. Many isolating layers (such as tape 7) melt or burn at least partly during the welding process, producing gases and combustion products which may be deleterious to the welding process. Therefore it can be preferable to use a backing without an isolating layer. A stationary ceramic backing can usually be used without a separating layer 7. At the welding side of the plates 1, a copper dam member 8 of a weld pool support device is located carrying on its upper side a feeder unit 9 for supplying shielding gas 20 through a connection tube 18. The dam member 8 is efficiently cooled by a liquid coolant 21 pumped through it by means of a pump 19. The temperature of the coolant entering the dam member 8 is considerably below ambient or room temperature. The liquid coolant flows into the support device via a feed duct 10 and leaves the support device via a tube 11. The temperature of the liquid coolant 21 is controlled (e.g. by a separate cooling device 12 - see Figure 2) so that heat is continuously extracted from the elements in and adjacent to the weld groove 5. The cooling of the weld pool support device has been proved to be efficient enough, if an upwardly-extending cooling duct 13 rises from the feed duct 10 on one side of the dam member 8 to its upper portion, where it connects to a horizontally-extending channel 14 which terminates at a downwardly-extending outlet portion 15 on the other side of the dam member 8, the portion 15 communicating with the tube 11. This "n-shaped" arrangement of cooling ducts has the disadvantage that the dam member 8 is cooled slightly more at its incoming side than at its outgoing side but this usually causes no harm. However, if a more uniform cooling is desired, an "m- or T-shaped" arrangement can be used in which a feed duct 10 is located in the centre of the dam member 8 which duct leads upwards from the bottom portion of the member 8 and branches into two sideways-extending cooling ducts in the upper portion of the member leading to two outgoing tubes 11 for the coolant, one at each side of the member 8.The cooling efficiency level for the edge areas of the dam member 8 should desirably be chosen so that the cooling occurring in the edge area of the plates 1 adjacent to the weld groove 5 is not excessive. In these edge areas the temperature should preferably clearly exceed 100°C, more preferably be between 100° and 150°C. The length L of the cooled part of the weld pool support device in the direction of the weld groove 5 is most suitably at least 7 cm and preferably about 10 cm. As welding proceeds in the upward direction as shown in Figure 1, the welding wire 2 and its feeder unit 3 are moved upwardly in synchronism with the gas feeder unit 9 and the weld pool support device. In a particular case welding speeds of 4.8 cm/min were achieved with aluminium plates of 30 mm thickness, 3.8 cm/min with plates of 42 mm thickness and 3.4 cm/min with plates of 45 mm thickness. The coolant supply is controlled to ensure equilibrium temperature conditions such that, at least on the welding side, the pool of liquid weld material 16 extends only part way down the length L of the dam member 8. The edge regions of the plates 1 close to the open weld groove 5 are continuously warmed by the welding process. The cooling influence of the dam member 8 should not be allowed to interfere too strongly with this warming process. The temperature of the plates to be welded should preferably not drop below 100°C. Figures 1 ard 2 show a small clearance between the dam member 8 and the plates 1 and this is desirable but it must not be so large as to allow downward spillage of pool material 16 during the welding process. In Figure 3, numeral 30 indicates a spherical LNG-tank formed from many curved plates 1 joined by welds 31 each of which has been formed with the weld line extending in a vertical direction using the method described with a coolant-cooled copper dam member 8. Several hundred metres of weld line are needed to form a tank of a diameter of 40 metres. Only one segment 32 of the spherical tank 30 is shown in full lines as an example of a portion where the invention is applied. Using the invention for welding a spherical LNG-tank can occasion cost savings for the welding operation of about one third. In place of a copper plate for the dam member 8, a plate of aluminium, stainless steel or ceramic material could be used. The invention is not limited to the embodiment shown, since several modifications thereof are feasible within the scope of the following claims.

Claims: A method for joining two metal plates (1, 1), by means of a one-sided weld (31) filling a weld groove (5) having a substantially vertical component and being formed between the two plates (1, 1), which joining is produced by using a dam member (8) of a weld pool support device moving in the direction of the weld groove (5), a liquid coolant (21) being passed through a cooling duct (13-15) in the dam member (8), characterised in that the plates (1, 1) are of aluminium or of other metal having substantially similar weldability properties to aluminium and in that the temperature of coolant fed to the duct (13-15) is maintained substantially below ambient temperature by means of a cooling device (12). A method according to claim 1, characterised in that the temperature of the liquid coolant (21) fed to the cooling duct (13-15) of the weld pool support device is kept within the range of +8°C to -20°C, preferably within the range of 0°C to -10°C. A method according to claim 1 or claim 2, characterised in that the dam member (8) of the weld pool support device is dimensioned to have a cooled portion with a length (L) in the direction of the weld groove (5) of from 7 to 12 cm, preferably from 8 to 10 cm. A method according to any one preceding claim, particularly when welding aluminium plates, characterised in that the cooling of the dam member (8) is so controlled, that cooling of the edge areas of the plates (1) at the sides of the weld groove (5) is limited so that the temperature of the said edge areas during continuous welding exceeds 100°C. A method according to any one preceding claim, characterised in that the dam member (8) is made of a material which has little tendency to adhere to liquid weld material (16). A method according to claim 5, characterised in that the said material of the dam member (8) has a wear resistance in use permitting a weld joint length of at least 50 metres before replacement is required. A method according to claim 5 or claim 6, characterised in that the said material of the dam member (8) is copper, aluminium, stainless steel or a ceramic material. A method according to any one preceding claim, characterised in that a moving or stationary backing (6, 7) is used at the root side of the weld groove (5), preferably a stationary ceramic backing. A method according to any one preceding claim, characterised in that the welding speed is controlled to be in the range of 2 to 5 cm/min.

Inventors: HEINAEKARI MATTI, ILOLA ISMO, KAUKONEN KYOESTI, NIEMINEN JARI, HEINAEKARI, MATTI, ILOLA, ISMO, KAUKONEN, KYOESTI, NIEMINEN, JARI, Heinäkari, Matti, Kaukonen, Kyösti
Applicants: KVAERNER MASA YARDS OY, KVAERNER MASA-YARDS OY
Application year: 1994
Main classification: B23K9
IPC codes: B23K37, B23K23, B23K9, F17C1, B23K31