Use of a post-surgical anti-adhesion device

Abstract: Surgical adhesion barriers and methods of using such surgical adhesion barriers are provided. Surgical adhesion barriers according to the present invention have at least one layer of a bioabsorbable material comprising copolymers and/or block copolymers derived from trimethylene carbonate. Alternatively, a multilayer surgical structure having one or more bioabsorbable layers superimposed on a non-absorbable layer is useful for minimizing or preventing formation of fibrous adhesions between a healing trauma site and adjacent surrounding tissue. Alternatively, a bioabsorbable non-woven fabric in adherent contact with at least one bioabsorbable layer of foam, film, mesh, web or woven fabric is also provided. One or more medicinal agents may be interposed between or disposed within any of the aforementioned layers.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to minimization and/or prevention of post-endosurgical adhesions and more particularly, to devices for preventing the formation of such adhesions between a healing trauma site and adjacent surrounding tissue. 2. Description of Related Art Injury, surgical incision or abrasion to the peritoneum, pleural or abdominal cavity results in an outpouring of a serosanguinous exudate. The exudate subsequently coagulates, producing fibrinous bands between abutting surfaces which can become organized by fibroblast proliferation to become collagenous adhesions. Adhesions are also known to form at bone fracture sites where jagged, irregular bone edges form in the area of the fracture. Bony spurs promote the growth of fibrous adhesions between the bone fracture surface and surrounding tissue. Adhesion formation following surgery or trauma is generally considered to be undesirable. For example, adhesions that form in relation to intestinal surgery, e.g., bowel resection, hernia repair, etc. may cause obstruction of the intestine. Adhesions that form near the bone fracture site may reduce or hinder the normal movement of the area of repair by restricting the natural movement of tendons over the adjacent bone. Adhesions may also form in the vicinity of nerves and disrupt nerve transmissions with a resultant diminution of sensory or motor function. Various methods and substances have been used in the hope of preventing post-operative adhesions. Certain drugs and surfactants have been suggested. For example, U.S. Patent No. 4,911,926 is directed to adhesion prevention by application of aqueous and non-aqueous compositions of a polyoxyalkylene block co-polymer to injured areas of the peritoneal or pleural cavity or organs situated therein subsequent to surgical injury. Another approach to adhesion prevention involves application of a physical barrier at the area of surgical injury. U.S. Patent No. 4,674,488 is directed to interposing a barrier layer of soft biological tissue, such as collagen, collagen-fabric films, collagen membranes, or reconstituted collagen or Dacron® mesh, at the interface of a bone fracture and the surrounding tissue. U.S. Patent No. 4,603,695 is directed to a molded polymeric material for preventing adhesion of vital tissues. The polymeric material is made of a biodegradable and absorbable polymer such as certain polyesters, collagen, amino acid polymers and chitin and may be placed where there is a possibility of adhesion setting in. Other materials have also been used to form physical barriers in an attempt to prevent adhesions, including silicone elastomers, gelatin films and knit fabrics of oxidized regenerated cellulose (hereinafter ORC). In some cases, it is suggested that heparin, heparinoid, or hexuronyl hexosaminoglycan be incorporated into a matrix of ORC fabric or other matrices of hyaluronic acid, cross-linked and uncrosslinked collagen webs, synthetic resorbable polymers, gelatin films, absorbable gel films, oxidized cellulose fabrics and films which are fabricated into a form that is said to be drapable, conformable and adherent to body organs and substantially absorbable within 30 days. See, e.g., U.S. Patent No. 4,840,626 or EPA Pub. No. 0 262 890 or EPA Pub. No. 0 372 969. EP 0 427 185 discloses copolymers of trimethylene carbonate and optically inactive lactides, and in particular their preparation and usage. Due to their elastic properties, these copolymers can be used as: 1) coating material for surgical sutures and fasteners. 2) resorbable sheets for covering wounds, for example for the treatment of burns and abrasions. The copolymers can also be employed as carriers for pharmaceuticals which can be inhibitory to inflammations. Since the copolymers are resorbable, they get absorbed as the tissue regenerates, while any non-resorbable copolymers will be rejected with the scab. 3) elastic resorbable implants such as bandages, sponges and cushions which are commonly used in surgery. The "in-vivo" properties and the rate of degradation of the copolymers can be manipulated by the composition and the sequence of the individual comonomers. 4) carriers of pharmaceuticals and retardation agents for the release of active components. Due to their high elasticity, the copolymers can be applied to sheets or adhesive bandages for releasing transdermal active components in a controlled manner. WO 92/10218 discloses an implantable bioabsorbable article comprised of a fibrous matrix laminally affixed to one surface of a cell barrier sheet material. When implanted it allows ingrowth of tissue into the fibrous matrix side of the material. Simultaneously the tissue to be regenerated at the tissue defect site is separated from the ingrowing tissue by the cell barrier sheet material. The biocompatible barrier material promotes the regeneration of tissue by the separation and isolation of the particular type of tissue to be regenerated from other competing undesirable tissues. EP 0 334 046 discloses a surgical composite structure manufactured from two or more biocompatible polymers. At least one of the polymers in the structure is non-absorbable. This non-absorbable portion of the composite structure acts as a reinforcement material. Further, the controlled degradation of the absorbable portion enhances the growth of natural tissue. This composite structure is useful in the repair of defects to the abdominal wall and may help to prevent hernia formation in an infected area. This reference teaches a film no thinner than 25µm in thickness. EP 0 460 439 discloses an absorbable and deformable surgical repair device. The device is manufactured from either a compolymer comprising a plurality of first and second linkages or a blend of a first and second polymer. The copolymer first linkages and the first polymer in the blend are selected from glycolic acid ester and lactic acid ester linkages and mixtures thereof. The copolymer second linkages and the second polymer in the blend are selected from 1,3- dioxan-2-one; 1,4-dioxan-2-one and ε- caprolactone linkages. The device is primarily constructed for use as a fracture fixation device, or a surgical clip or staple. US 4,603,695 discloses a molded polymeric material for preventing adhesion of vital tissues. The polymeric material is made of a biodegradable and absorbable polymer such as certain polyesters, collagen, amino acid polymers and chitin and may be placed where there is a possibility of adhesion setting in. The molded material is in the form of a sheet ranging from 10 to 1000µm in thickness. Physical barriers are also used to cover and protect wound sites. PCT/US91/08972 is directed to a surgical article having a bioabsorbable fibrous matrix in a laminar relationship with a bioabsorbable cell barrier sheet. U.S. Patent No. 5,092,884 and EPA Pub. No. 0 334 046 are directed to a surgical composite structure having absorbable and non-absorbable components which may be useful for repairing anatomical defects, e.g., preventing hernia formation in an infected area. The nonabsorbable portion of the composite acts as a reinforcement material. Ingrowth of natural tissue is said to be enhanced by controlled degradation of the absorbable portion. U.S. Patent No. 5,035,893 relates to a wound covering composition having a sheet of biopolymeric material and a film of polyurethane resin. An antibacterial agent may be provided between the polyurethane film and the sheet of biopolymeric material, thereby forming a three-layer wound covering material. With the cure of the wound, it is said that the biopolymeric material is taken in a living tissue and the polyurethane film can be peeled off from the sheet without hurting the surface of a wound. SUMMARY OF THE INVENTION According to the present invention, there is provided a post-endosurgical adhesion barrier as claimed in claim 1, hereinbelow. The present invention provides surgical adhesion barriers, and the present specification discloses methods of using surgical adhesion barriers of bioabsorbable material. The bioabsorbable material comprises co-polymers, block co-polymers or blends thereof. The co-polymers comprises carbonates and at least one other bioabsorbable polymer forming material. The block co-polymers comprise at least one block comprising trimethylene carbonate. In one embodiment the block co-polymer comprises a first block formed from a co-polymer having a predominant amount of trimethylene carbonate and a second block formed from a co-polymer having a predominant amount of lactide. The absorbable layer may be fashioned from mesh, web, woven fabric, non-woven fabric, porous film, non-porous film or foam. The bioabsorbable structure is in the form of film. The surgical adhesion barrier structure is flexible, resilient and conformable to various shapes such as body organs and tissues. During surgery, a surgical adhesion barrier according to the present invention is positioned at the area of injury to prevent adhesions as desired. As the bioabsorbable layer is absorbed, any adhesions which may have attached to the bioabsorbable layer lose their support and fall free of the injury site. The structures of the present invention may find application for open general surgery or less invasive surgical techniques such as endoscopic surgery, or both. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a diagram of a stuffer box / crimper suitable for processing filaments used in the manufacture absorbable non-woven fabric for use in the present invention. DETAILED DESCRIPTION OF THE INVENTION A surgical adhesion barrier according to the present invention prevents formation of surgical adhesions at a surgical wound by interposing a unique bioabsorbable barrier between the surgical wound and surrounding tissue. Suitable bioabsorbable polymer-forming materials which may be co-polymerized with a suitable carbonate include materials capable of forming hydrolyzable polyesters. Suitable materials capable of forming hydrolyzable polyesters include glycolide and lactide; hydroxyacids such as glycolic acid, lactic acid, hydroxy butyric acids, and hydroxyvaleric acids; lactones such as β-propio-lactone, δ-caprolactone, ε-caprolactone, methyl-caprolactone, dioxanone, p-dioxanone, methyl-p-dioxanone, dimethyl-p-dioxanone, and β-malolactone; and polyalkylene oxides such as polyoxyethylene glycol and polyoxypropylene glycol; and mixtures, blends, and co-polymers thereof. The single layer surgical adhesion barrier embodiment of the present invention preferably comprises a bioabsorbable co-polymer of trimethylene carbonate and glycolide, the trimethylene carbonate being present in a predominant amount. A "predominant amount", as used herein, is an amount greater than 50 mole percent of a composition. Preferably, the concentration of glycolide and trimethylene carbonate in this embodiment of the present invention is about 20 and 80 mole percent, respectively. Suitable single layer surgical adhesion barriers of the present invention can also be fabricated from block copolymers having one or more "A" blocks comprising a carbonate as described above and a bioabsorbable polymer forming material as described above, and one or more "B" blocks comprising a bioabsorbable polymer forming material as described above. Preferably the "A" blocks are present in amounts ranging from about 10% to about 90% and the "B" blocks are present in amounts ranging from about 10% to about 90%. In a still more preferred embodiment, the "A" blocks are present in an amount ranging from about 15 weight percent to about 85 weight percent and the "B" blocks present in an amount ranging from about 15 weight percent to about 85 weight percent. Most preferably, the "A" and "B" blocks are present in amounts of about 50 percent by weight each. Suitable "A" blocks include a predominant amount, i.e., greater than about 50 mole percent, of trimethylene carbonate. Preferably the trimethylene carbonate ranges from about 75 mole percent to about 95 mole percent. A more preferable concentration of trimethylene carbonate ranges from about 80 mole percent to about 90 mole percent and is most preferably about 80 mole percent. The trimethylene carbonate may be co-polymerized with any monomer which provides an absorbable co-polymer to form the "A" block. Such monomers include but are not limited to glycolide, lactide, dioxanone, epsilon caprolactone, with glycolide being preferred. Suitable "B" blocks include a predominant amount of lactide (i.e., greater than about 50 mole percent) but preferably ranging from about 75 mole percent to about 95 mole percent. A more preferable concentration of lactide ranges from about 80 mole percent to about 90 mole percent and is most preferably about 80 mole percent. The lactide may be co-polymerized with any monomer such that an absorbable co-polymer is provided to form the "B" block. Such monomers include but are not limited to glycolide, dioxanone, and epsilon caprolactone, trimethylene carbonate, with glycolide being preferred. An adhesion barrier according to the invention and constructed from a single layer of bioabsorbable material is in the form of film. A non-porous single layer adhesion barrier is least likely to allow adhesions to penetrate through to adjacent tissue. An adhesion barrier film made of the above-described materials can be made by standard polymer film forming techniques, e.g., compression of co-polymer resin between heated polytetrafluoroethylene (PTFE) coated plates. Other film forming techniques are described in, e.g., the Encyclopedia of Polymer Science and Engineering, Vol. 12, pp. 204-210 (1988). The thickness of the film can range from about 25 to about 75 µm (about 1 mil to about 3 mil). In another embodiment, a single layer foam bioabsorbable surgical adhesion barrier made of the above described materials can be made in accordance with known foam forming techniques such as those disclosed in U.S. Patent Nos. 3,902,497 or 5,102,983. The foam may be sliced and/or cut to desired thickness and configuration before surgical use. The thickness of the foam layer can range from about 25 to about 75 µm (about 1 mil to about 3 mil). A single layer bioabsorbable surgical adhesion barrier according to the present invention is flexible, resilient and conformable to the shape of underlying tissue. Films and foams constructed from the above-described polymers are well suited for draping over and conforming to areas of surgical wounds or injury and are especially well suited for endoscopic surgery, e.g., laparoscopy. Bioabsorbable film made of any of the above-described bioabsorbable polymers, co-polymers, or blends thereof can be manufactured by standard polymer film forming techniques, e.g. compression of polymer resin between PTFE coated platens. Other film forming techniques are described in, e.g., the Encyclopedia of Polymer Science and Engineering, Vol. 12, pp. 204-210 (1988). In a most preferred embodiment the bioabsorbable polymer is dissolved in a suitable solvent, e.g., methylene chloride, acetone, etc., to form a mixture of desired viscosity which is coated onto release means such as release paper or the like to form a film. During evaporation of the solvent, a bioabsorbable non-woven fabric layer(s) is placed on the wet film. The film may range from 25 µm (0.1 mil) to 100 µm (4 mil) and is preferably about 50 µm (2 mil). The bioabsorbable film (which can be in the form of foam) may be fabricated from any of the well known bioabsorbable polymers used in medicine. A preferred bioabsorbable polymer for use in the film is described above in accordance with a surgical adhesion barrier constructed from a single layer of bioabsorbable material, i.e., co-polymers of carbonates and at least one other bioabsorbable material. A highly preferred bioabsorbable polymer for use in the film is fabricated from block co-polymers having about 50% by weight of an "A" block comprising about 40 mole percent glycolide and about 60 mole percent trimethylene carbonate and about 50% by weight of a "B" block comprising about 20 mole percent lactide and about 80 mole percent glycolide. Another highly preferred bioabsorbable polymer is fabricated from block co-polymers having about 20% by weight of an "A" block comprising about 20 mole percent glycolide and about 80 mole percent trimethylene carbonate and about 80% by weight of a "B" block comprising about 20 mole percent glycolide and about 80 mole percent lactide. The term "medicinal agent", as used herein, is meant to be interpreted broadly and includes any substance or mixture of substances which may have any clinical use in medicine. Thus medicinal agents include drugs, enzymes, proteins, peptides, glycoproteins, or diagnostic agents such as releasable dyes which may have no biological activity per se. Examples of classes of medicinal agents that can be used in accordance with the present invention include antimicrobials, analgesics, antipyretics, anesthetics, antiepileptics, antihistamines, anti-inflammatories, cardiovascular drugs, diagnostic agents, sympathomimetic, cholinomimetic, anti-muscarinics, antispasmodics, hormones, growth factors, muscle relaxants, adrenergic neuron blockers, anti-neoplastics, immunosuppressants, gastrointestinal drugs, diuretics, steroids and enzymes. It is also intended that combinations of medicinals can be used in accordance with the present invention. Thus, in one embodiment of the present invention focal delivery and application of a medicinal agent to the wound site is achieved. Focal application can be more desirable than general systemic application in some cases, e.g., chemotherapy for localized tumors, because it produces fewer side effects in distant tissues or organs and also concentrates therapy at intended sites. Focal application of growth factors, anti-inflammatories, immune system suppressants and/or antimicrobials by a the anti-adhesion device of the present invention is an ideal drug delivery system to speed healing of a wound or incision. A post surgical anti-adhesion device or structure of the present invention is generally used in the form of a sheet of a desired size and shape. A surgeon may cut a custom shape from preformed sheets to suit particular applications. After the device is shaped for a suitable fit, the flexible nature of the device enables the surgeon to conform the device to fit around the area of injury. In one embodiment, the device is formed into a strip which wraps around the organ, e.g., an intestine, to prevent formation of adhesions. An anti-adhesion device according to the present invention can incorporate ties or straps which connect to the device and which are used to tie or otherwise secure the device to an area of injury. It is further contemplated that the anti-adhesion devices of the present invention may be affixed to the wound site by surgical fasteners or sutures. The flexible nature of the present anti-adhesion device allows the device to flex and bend along with normal movements of the body without being overly restrictive. All embodiments of surgical adhesion barriers or structures as described herein are well-suited for application by techniques involving endoscopy. Endoscopic surgical procedures involve the use of cannulas or tubes which provide narrow openings into a body and allow minimally invasive access to surgical targets. In laparoscopic procedures, surgery is performed in the interior of the abdomen through small tubes inserted therein. Endoscopes are frequently used as viewing devices inserted through the cannulas which allow surgeons to see the interior of the body. Certain endoscopic and laparoscopic procedures may require that the surgical region be insufflated. Accordingly, any instrumentation inserted into the body should be substantially sealed to ensure that gases do not enter or exit the body through the incision. Moreover, endoscopic and laparoscopic procedures often require the surgeon to operate on organs, tissues and/or vessels far removed from the incision. Thus, instruments used in such procedures are typically long and narrow while being functionally controllable from a proximal end of the instrument. In accordance with the present invention an apparatus for deploying and positioning any of the adhesion barriers or structures disclosed herein may be inserted through a cannula and deposited at a target site. Once the barrier is positioned as desired, it may optionally be sutured, stapled or otherwise fastened to the target site with instruments designed to be inserted through a cannula. In order that those skilled in the art may be better able to practice the present invention, the following examples are given as an illustration of the preparation and superior characteristics of the anti-adhesion devices of the present invention. It should be noted that the invention is not limited to the specific details embodied in the examples. EXAMPLE 1 Co-polymer of Glycolide/Trimethylene Carbonate (Polymer I) A 20/80 mole percent glycolide/trimethylene carbonate co-polymer was prepared in a reactor by combining previously dried 53.13 grams of glycolide and 186.87 grams of trimethylene carbonate and polymerizing at 160°C for 24 hours in the presence of 0.05 grams of stannous octoate. The polymer was extruded from the reactor and post treated to remove any residual monomer present in the polymer. The inherent viscosity of the polymer was 0.9. EXAMPLE 2 Co-polymer of Glycolide/Trimethylene Carbonate/Lactide (Polymer II) A block co-polymer having one block containing 20 mole percent glycolide and 80 mole percent trimethylene carbonate and another block containing 20 mole percent glycolide and 80 mole percent lactide, wherein both blocks are present in equal weight ratios was prepared in a reactor. 553.4 grams of glycolide and 1946.6 grams of trimethylene carbonate were added to the reactor along with 1.0 grams of stannous octoate and dried under vacuum in the reactor for about 16 hrs. After drying, the reactants were heated at 150°C and polymerized for about 24 hrs. At this stage 419.1 grams of dried glycolide and 2080.9 grams of lactide were added and continued polymerizing of additional 24 hrs. The polymer is extruded and post treated to remove any residual monomers present in the polymer. The inherent viscosity of this polymer was 1.32. EXAMPLE 3 Co-polymer of Glycolide/Trimethylene Carbonate/Lactide (Polymer III) A block co-polymer having 50% by weight of one block containing 40 mole percent glycolide and 60 mole percent trimethylene carbonate and 50% by weight of another block containing 20 mole percent glycolide and 80 mole percent lactide was prepared in a reactor. 646.7 grams of glycolide and 853 grams of trimethylene carbonate were added to the reactor along with 0.6 grams of stannous octoate and dried under vacuum in the reactor for about 24 hours at 160°C. At this stage 251 grams of glycolide and 1248 grams of lactide were added and polymerized for an additional 24 hours at 170°C. The polymer was extruded and post treated to remove any residual monomers present in the polymer. The inherent viscosity of this polymer was in the range of 0.4-0.8 dl/g. EXAMPLE 4 Co-polymer of Glycolide/Trimethylene Carbonate/Lactide (Polymer IV) A block co-polymer having 20% by weight of one block containing 20 mole percent glycolide and 80 mole percent trimethylene carbonate and 80% by weight of another block containing 20 mole percent glycolide and 80 mole percent lactide was prepared in a reactor. 132.8 grams of glycolide and 467.2 grams of trimethylene carbonate were added to the reactor along with 0.6 grams of stannous octoate and dried under vacuum in the reactor for about 24 hours. At this stage 402 grams of glycolide and 1998 grams of lactide were added and polymerized for an additional 24 hours. The polymer was extruded and post treated to remove any residual monomers present in the polymer. The inherent viscosity of this polymer was of 0.0 to 1.1 dl/g. EXAMPLE 5 Manufacture of a Film Polymer I, made in accordance with Example 1, was pressed into a film by means of a vacuum press supplied by Technical Machine Products, Cleveland, Ohio, a standard commercial press having PTFE coated platens. The temperature of the platens was maintained at about 130°C. The platens were pressed together at a load of about 11350 Kg (about 25,000 pounds) for about 12 minutes. The resulting film was then removed from the press. EXAMPLE 6 Manufacture of a Film Polymer II, made in accordance with Example 2,is pressed into a film in a manner similar to that described in Example 5 except that the platens were heated to a temperature of about 190°C and pressed together at a load of about 1362 Kg (about 3000 pounds). EXAMPLE 7 Implantation of Polymer I Adhesion Barrier Twelve female Sprague-Dawley rats weighing between 255-250 gm each were monitored for at least one week prior to surgery to insure good health and stability. The animals were anesthetized with intraperitoneal sodium pentobarbital and their abdomens prepared for surgery. The abdominal cavity was exposed through a midline incision. On the abdominal wall overlying the cecum, a 1 cm x 2 cm area of parietal peritoneum was carefully excised from the abdominal wall, removing a thin layer of muscle along with the peritoneum. The cecum was elevated and isolated by moist gauze. The proximal end of the cecum was emptied of its contents. A 1 cm x 2 cm area on the anterior surface of the proximal end of the cecum was gently abraded by rubbing 10 times with dry gauze. The cecum was then scraped with a scalpel blade to cause minute petechial hemorrhages. The cecal abrasion was left exposed for 15 minutes. After 15 minutes, the cecal abrasion and the abdominal wound were blotted with a gauze sponge to gently remove any excess blood and ensure complete hemostasis. Placement of these two wounds together normally leads to reproducible formation of an adhesion. A 2 cm x 3 cm film of Polymer I approximately 178 µm (7 mil) thick made in a manner according to Example 3 was placed between the wounds before they were placed in contact and the abdomen closed. The procedure was repeated on all twelve rats. Seven days following surgery, the animals' peritoneum was evaluated for the development of an adhesion between the peritoneal defect and the cecal surface. Examination of the wound site revealed that one of twelve rats had developed an adhesion. EXAMPLE 8 Implantation of Polymer II Adhesion Barrier Polymer II in accordance with Example 2 was formed into a single layer film approximately 178 µm (7 mil) thick and implanted in a manner similar to that described in Example 5. Examination of the wound site after seven days revealed that one of twelve rats had developed an adhesion. COMPARATIVE EXAMPLE 1 2 cm x 3 cm Hyaluronic acid pads (commercially available from Med Chem) were implanted in seventeen rats in a manner similar to that described in Example 7. Examination of the wound site after seven days revealed that twelve of seventeen rats developed adhesions. COMPARATIVE EXAMPLE 2 3 cm diameter Hylan NWM discs (commercially available from Biomatrix, Inc.), circulars disc containing hyaluronic acid, were implanted in eleven rats in a manner similar to that described in Example 7. Examination of the wound site after seven days revealed that two of eleven rats developed adhesions. COMPARATIVE EXAMPLE 3 Hylan solution (commercially available from Biomatrix, Inc.), a hyaluronic acid gel, was applied to both wound surfaces of twelve rats caused in a similar manner as the wound surfaces created in Example 7. Seven of twelve rats developed adhesions at the wound site. COMPARATIVE EXAMPLE 4 3% methylcellulose solution was applied to both wound surfaces of eleven rats caused in a similar manner as the wound surfaces created in Example 7. Five of eleven rats developed adhesions at the wound site. COMPARATIVE EXAMPLE 5 1 cm x 2 cm pads of uncoated SURGIPRO® polypropylene mesh (commercially available from U.S. Surgical Corp.) were implanted into fifteen rats in a manner similar to that described in Example 7 except that certain of the rats were analyzed at three specified time intervals: at 7, 21, and 55 days, respectively. It is believed that one of the fifteen rats was mislabeled and discounted in the group analyzed at 7 days; at day 7 three of four rats developed cecal adhesions; at day 21 three of five rats developed cecal adhesions; at day 55 three of five rats developed cecal adhesions. In sum, nine of fourteen remaining rats developed cecal adhesions at the wound site. COMPARATIVE EXAMPLE 6 1 cm x 2 cm pads of SURGIPRO® polypropylene mesh (commercially available from U.S. Surgical Corp.) coated with film of hydroxyethylmethacrylate (HEMA) were implanted into fifteen rats in a manner similar to that described in Comparative Example 7. At day 7, one of five rats was observed with a cecal adhesion and three of the five rats were observed with retroperitoneal fat adhesions. At day 21 two of five rats were observed with cecal adhesions. At day 55 two of five rats were observed with cecal adhesions. In sum, five of fifteen rats were observed with cecal adhesions at the wound site. COMPARATIVE EXAMPLE 7 2cm x 3cm pads of Marlex® polypropylene mesh (commercially available from C.R. Bard, Inc.) were implanted into twelve rats in a manner similar to that described in Example 7 except that the pads were sutured to the abdominal wall using size 7/0 polypropylene suture in each corner of the pad. The stitches were placed so that the knots were under the sample and not exposed. After seven days, all twelve rats were observed with adhesions at the wound site. COMPARATIVE EXAMPLE 8 2cm x 3cm pads of Surgipro® polypropylene mesh (commercially available from U.S. Surgical Corp.) were implanted into twelve rats in a manner similar to that described in Comparative Example 8. After seven days, all twelve rats were observed with adhesions at the wound site. COMPARATIVE EXAMPLE 9 2cm x 3cm pads of Interceed® oxidized regenerated cellulose (commercially available from Ethicon, Inc.) were implanted into twelve rats in a manner similar to that described in Comparative Example 8. After seven days, all twelve rats were observed with adhesions at the wound site. COMPARATIVE EXAMPLE 10 2cm x 3cm pads of Gore-Tex® soft tissue patch (commercially available from W.C. Gore & Co.) were implanted into twelve rats in a manner similar to that described in Comparative Example 8. After seven days, eight of twelve rats (about 67%) were observed with adhesions at the wound site. Comparative Examples 7-10 also included observations of adhesions which are considered to be less important than cecal adhesions. Adhesions of lesser importance are categorized herein as Type 1, Type 2 and Type 3. Type 1 include fat, liver, or intestines adhered to the face of the test surface. Type 2 include fat, liver, or intestines adhered to a free edge of a test surface or to suture knots. Type 3 include adherence of the cecal defect to peritoneal wall caudal or lateral to the test site. The results of the observations relating to adhesions of lesser importance are summarized in Table IV. INCIDENCE OF ADHESIONS OTHER THAN THE CECUM ADHERING TO THE OVERLYING TEST MATERIAL. TEST MATER INCIDENCE OF OTHER ADHESIONS (Approximate %) DAY 7 DAY 14 DAY 21 Type 1 Type 2 Type 3 Type 1 Type 2 Type 3 Type 1 Type 2 Type 3 SURGIPRO 100 100 0 N/A N/A MARLEX 100 100 0 INTERCEED 92 0 GORE-TEX 75 58 8 SURGIPRO+ 2 mil fi 0 100 33 100 42 33 92 17 42 SURGIPRO+ 4 mil fi 0 100 25 91 9 18 91 36 18 50.8 µm (2 mil) film 0 92 25 0 78 11 0 89 22 101.6 µm (4 mil) film 0 83 17 0 75 0 0 100 33 The claims which follow identify embodiments of the invention additional to those described in detail above.

Claims: The use, in the manufacture of a surgical adhesion barrier, of a drapable film capable of being passed through a cannula and having a wholly bioabsorbable structure comprising a layer of a bioabsorbable material comprising a copolymer of trimethylene carbonate, the film having a thickness of from 2.5µm (0.1 mil) to 175 µm (7 mil), wherein the bioabsorbable material comprises a block copolymer having at least one block formed from a copolymer having a predominant amount of trimethylene carbonate and at least another block. Use according to claim 1 wherein the first block comprises about 80 mole percent trimethylene carbonate. Use according to claim 1 or 2, wherein the second block comprises a copolymer having a predominant amount of lactide. Use according to claim 1, 2 or 3, wherein said first block comprises from about 10 to about 90 percent by weight of the block copolymer. Use according to claim 4 wherein the first block comprises about 50 percent by weight of the block copolymer. Use according to any one of the preceding claims, wherein said first block is present in about 50% by weight and comprises about 40 mole percent glycolide and about 60 mole percent trimethylene carbonate and said second block is present in about 50% by weight and comprises about 20 mole percent glycolide and about 80 mole percent lactide. Use according to any one of the preceding claims, wherein said first block is present in about 20% by weight and comprises about 20 mole percent glycolide and about 80 mole percent trimethylene carbonate and said second block is present in about 80% by weight and comprises about 20 mole percent glycolide and about 80 mole percent lactide.

Inventors: GRAVENER ROY D, HAIN MATTHEW, KOYFMAN ILYA S, MUTH ROSS R, TOTAKURA NAGABUSHANAM, GRAVENER, ROY D., HAIN, MATTHEW, KOYFMAN, ILYA S., MUTH, ROSS R., TOTAKURA, NAGABUSHANAM
Applicants: UNITED STATES SURGICAL CORP, UNITED STATES SURGICAL CORPORATION
Application year: 1994
Main classification: A61L31
IPC codes: A61L31