COMPLEXATION-MEDIATED CRYSTAL-FORMING REACTIONS USING COMPLEXING AGENTS

Abstract: Methods and reaction systems are disclosed that are adapted for forming crystallites having novel crystal habits and/or morphologies compared to conventional crystallites of the same chemical composition. The methods and reaction systems involve chemical reactions between at least two reactant compounds occurring in a liquid (or gel) that form insoluble crystallite products. At least one of the reactants is rendered soluble in a solvent in which the reactant is not normally soluble by adding an agent that forms soluble molecular complexes of the agent and the reactant. The complexing agent not only facilitates dissolution of the reactant in the solvent but also plays a role in how the faces of crystals comprising the crystallite product are enlarged during formation of the product. Products having such altered crystallite structure have a number of possible uses.

Description: COMPLEXATION-MEDIATED CRYSTAL-FORMING REACTIONS USING COMPLEXING AGENTS FIELD OF THE INVENTION This invention pertains to methods of preparing new crystalline forms of various chemical compounds, both organic and inorganic. ACKNOWLEDGEMENT Research that resulted in this invention was supported by grant nos. N00014-88-K-O006and N-O0O14-91-J-1731 from the Office of Naval Research. The government has rights in this invention. BACKGROUND OF THE INVENTION Interest in crystallization, and in various ways for altering the shapes and structures of crystals, has a long history. Efforts to modify crystallization processes so as to generate new crystalline forms of substances continue to be of considerable importance for various reasons including, for example, improvement of mass-handling characteristics of particulate materials, production of materials that are stronger or more durable than existing materials, and production of materials having improved physical characteristics such as light transmissivity. One traditional way in which alteration of the shape (i.e., the "habit") or the crystal lattice (i.e., the "morphology") of a crystalline material has been achieved is by the use of additives. Weissbuch et al.. Science 253:637-645(1991.: Addadi et al.. Topics in Stereochem. 16:1-85 (1986): Addadi et ah. Angew. Chem. Int. Ed. Engl. 24:466-485(1985.: and Addadi et al.. Nature 296:21-26 (1982). Additive effects can be dramatic. A notorious example is the conversion of cubic NaCl to octahedral NaCl in the presence of traces of urea. Often, however, additives can incorporate into the crystals during growth, which is undesirable especially if a highly pure crystalline substance is needed. Another traditional way to alter the habit or morphology of a crystalline material is by changing the crystallization solvent (including crystallization from the gas phase) used to dissolve the crystallization solute. Unfortunately, changing the crystallization solvent may not be possible because the crystallization solute must be soluble in the solvent employed and few alternative solvents may be available. For example, very polar solutes such as salts are typically ciystallized from very polar solvents, especially water, because such solutes are insoluble in less polar solvents. Similarly, formation of materials for many electronic or optical uses (e.g., metal chalcogenides) via precipitation upon admixture of precursor salt solutions also requires very polar media in order to dissolve the precursor solutes. Although various ways of avoiding the requirement of aqueous solvents for the formation of such materials have appeared, these techniques often require the preparation of organo-element precursors or use of toxic and volatile inorganics and are far from being generally applicable. Salts such as potassium chloride, which are freely soluble in water, are insoluble in non-polar solvents. Solvent effects on the alteration of crystal growth of such salts have not been explored to any great extent simply because one must dissolve the salt before it can be crystallized from solution. Complexation using crown ethers provides a convenient method of solubilizing salts, in the form of their complexes, in non-polar solvents, as first reported by Pedersen, _____ Am. Chem. Soc. 89:2495-2496(1967); see also. Pedersen, J. Am. Chem. Soc. 89:7017-7036 (1967). Doxsee et al.. J. Indus. Phenom. & Molec. Recog. in Chem. 9:327-336(1990) reports the crystallization of a simple organic salt, sodium acetate, from cyclohexane solution in which sodium acetate is completely insoluble. The sodium acetate solute is solubilized as a crown- ether complex of the salt in the organic solvent. Slow evaporation of the solution results in precipitation of the free salt in crystalline form. When sodium acetate is conventionally crystallized from an aqueous solution, the crystals have a hexagonal plate habit. Crystallization of sodium acetate from the organic solution of its crown ether complex results in the formation of needle-shaped crystals. Despite their quite different crystal habits, the needles have an identical crystal lattice as the hexagonal crystals, as ascertained by x-ray diffraction analysis. Thus, addition of complexation agents, such as crown ethers, solubilizes compounds in solvents in which the compounds would normally be completely insoluble. Initiation of crystallization then provides an opportunity to observe crystal growth under solvation conditions that are quite different from those of "normal" crystal-growth conditions. Whereas crystallization of a simple inorganic salt from organic solution is intriguing, the method has substantial limitations. For example, it is limited to production of crystals of the particular solute already dissolved in the solution. Production of a large variety of other crystalline materials requires chemical reactions between reactants supplied by more than one solute. Production of many commercially important compounds using conventional reaction technology is often difficult, hazardous, and/or expensive. Suitable reaction precursors (i.e., "reactants") may be unavailable or very expensive; the reactants may be highly toxic or flammable or have some other undesirable property such as extreme volatility. Finally, certain reactants are inefficient and generate undesired by-products or require additional process steps to obtain the desired product at a suitable purity level. For example, zinc selenide is conventionally produced by reacting dimethyl zinc with hydrogen selenide. Dimethyl zinc is expensive, extremely volatile, and pyrophoric. It would be advantageous if zinc selenide could be produced from an inorganic salt such as zinc chloride that is inexpensive and safe to use. Therefore, there is a need for methods for producing, via a chemical reaction, materials having crystalline forms that are different in habit from crystalline materials produced by simple crystallization from solution. Materials having such different crystalline forms can be more suitable for particular applications. There is also a need for such method permitting production of such crystalline forms using reactants that are less hazardous to work with compared to reactants that must be used in conventional reaction systems. SUMMARY OF THE INVENTION The foregoing needs are met by the present invention which provides methods and reaction systems for forming crystallite products. According to one aspect of the present invention, such a method is provided wherein a first reactant is provided that is more soluble in a first solvent than in a second solvent. A second reactant is also provided that can react with the first reactant in the first solvent to form a crystallite product. In order to facilitate dissolution of the first reactant in the second solvent, a complexing agent is provided that is soluble in the second solvent and that can form molecular complexes with the first reactant. The first and second reactants along with the complexing agent are added to the second solvent, wherein the first and second reactants are allowed to react and form a crystallite product that is insoluble in the second solvent. The crystallite product formed by reaction in the second solvent, as facilitated by the complexing agent, comprises crystals that are different from crystals of the crystallite product that would otherwise be formable by reaction of the first and second reactants in the first solvent. Such differences are particularly evident as differences in crystal habit and/or morphology. Otherwise, the crystals formed in the second solution are typically (with few exceptions known at the present time) chemically identical to crystals found in the crystallite formed in the first solution. Typically, in the foregoing method, the first solvent is polar and the second solvent is less polar than the first solvent. (Usually, the first solvent is water and the second solvent is an organic solvent). In such instances, the first and second reactants are typically salts that dissociate in the first solvent to form respective anions and corresponding cations. According to another aspect of the present invention, a second complexing agent can be used, if required, to facilitate dissolution of the second reactant in the second solution. According to another aspect of the present invention, the first reactant can be at least partially dissolved in a first solvent (using a complexing agent to facilitate said dissolution) to form a first solution, and a second reactant can be at least partially dissolved in a second solvent (using a complexing agent, if required, to facilitate dissolution) to form a second solution. The first and second solutions can be combined to trigger the crystallite-forming reaction. Alternatively, a region consisting substantially of the first solution can be formed, contacting a region consisting substantially of the second solution, wherein an interface is formed between the regions. Reaction between the first and second reactants thus occurs at the interface, principally by diffusion, to form a crystallite product that is insoluble in either solution. In such an instance, the solutions can be either miscible or immiscible with each other. According to another aspect of the present invention, reaction systems are provided that comprise a solvent, a first reactant normally poorly soluble to insoluble in the solvent, a first complexing agent dissolved in the solvent, and a second reactant capable of reacting with the first reactant in the solvent. The first complexing agent forms molecular complexes with the first reactant so as to facilitate dissolution of the first reactant in the solvent. According to another aspect of the present invention, other reaction-system embodiments are possible, including embodiments in which two solutions are provided. In such embodiments, a first solution comprises a first reactant, a first solvent, and a complexing agent to which the first reactant is complexed so as to render the first reactant soluble in the solvent. A second solution comprises a second solvent and a second reactant at least partially soluble therein. The two solutions can be either mixed together or formed into two regions in contact with each other at an interface. As the first and second reactants react, a precipitate is formed in the mixture or at the interface, respectively. According to yet another aspect of the present invention, one or both solutions (in reaction systems comprising two solutions) can be a gel. Alternatively, a gel can be placed between the first and second solutions which allows reactants to travel therethrough and can allow the crystallite product to be formed therein. The foregoing embodiments of methods and reaction systems according to the present invention make possible the production of crystallites comprised of crystals having novel habit and/or morphology compared to crystallites formed in solvents in which the reactants are soluble without the use of complexing agents. As discussed herein, these novel crystallites have a large number of possible uses, depending upon the composition of the crystallites. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a scanning electron micrograph of gold-coated, apparently amorphous PbS formed according to the prior art in a water solution by reaction of lead (II) acetate with sodium sulf.de as described in Example 5 (magnification 20,000x). FIG. 2 is a scanning electron micrograph of gold-coated crystalline PbS formed according the present invention in a solution of anhydrous tetrahydrofuran with dibenzo-18- crown-6 as described in Example 1 (magnification 10,000x). FIG. 3 is a scanning electron micrograph of gold-coated, apparently amorphous HgS formed according to the prior art in a water solution by reaction of mercuric chloride and sodium sulfide as described in Example 36 (magnification 20,000x). FIG. 4 is a scanning electron micrograph of gold-coated crystalline HgS formed according to the present invention in a two-phase system in which crown-ether (dibenzo-18- crown-6) solubilized sodium sulfide in methylene chloride was layered with an aqueous solution of mercuric chloride as described in Example 38 (magnification 10.000X). FIG. 5 is an optical photomicrograph showing whisker-like crystallites of cinnabar formed after prolonged reaction of the system that generated the crystallites shown in FIG. 4 (Example 38). DETAILED DESCRIPTION "Complex-mediated crystallization" has been reported. Doxsee et al.. J. Indus. Phenom. & Molec. Recog. in Chem. 9:327-336(1990). According to such a method, a solute (sodium acetate) that is freely soluble in water but not normally soluble in the non-polar solvent cyclohexane was dissolved in cyclohexane by addition of a crown ether (lS-crown-5) to the solvent. The crown ether was soluble in the solvent. Molecules of the crown ether formed complexes with the constituent sodium and acetate ions of the solute, thereby enabling the solute to "dissolve" (while still complexed with the crown ether) in the solvent. Subsequent evaporation of the solvent caused crystals of sodium acetate trihydrate to precipitate from the solution. The crystals were needle-shaped rather than the typical hexagonal plate habit produced by crystallization of this compound from an aqueous solution. However, the crystals had the same lattice parameters as hexagonal plate crystals of sodium acetate. The needle- crystal phenomenon was "explained" by the effect of the crown ether on the differential rates of solute adsorption on each of the faces of the sodium acetate crystals during crystal growth. In particular, it was hypothesized that the crown ether exerted a solvation effect on the relatively non-polar lateral faces (on which van der Waals contacts between methyl groups of the acetates apparently predominate). The crown ether exhibited very little solvation effect on the relatively polar axial faces (built up of alternating layers of Na + ions, water molecules, and acetate carboxylates). Thus, the axial faces were caused to grow more rapidly than the lateral faces. The present invention provides a way to produce crystalline products (i.e., "crystallites") by chemical reactions , not merely by recrystallization from a solution. In a reaction according to the present invention, crystals of the product can have an unusual crystalline shape (crystal habit) and/or crystalline lattice structure (crystal morphology) compared to crystals of the product formed by conventional methods. According to the present invention, a "reaction system" comprises at least two reactants, at least one solvent in which one or more of the reactants are to be dissolved (but in which at least one of the reactants to be dissolved is not normally freely soluble) and at least one chemical agent (i.e., a "complexing agent") suitable for effecting dissolution of the solute(s) in the solvent. The reactants, solvents, and complexing agents are discussed in further detail below. As stated above, at least one of the reactants is normally, at least, poorly soluble to substantially insoluble in the corresponding solvent. In order to dissolve a sufficient amount of the reactant in the solvent and thereby render molecules of the reactant available for reaction, a chemical agent is employed having molecules that are soluble in the solvent and that form molecular complexes with the reactant. Hence, such an agent is termed a "complexing agent. " A chemical reaction according to the present invention involves molecules of at least two reactants. Molecules of the reactants are presented to each other for reaction either in a single solution containing molecules of both reactants (i.e., solutes) or in separate solutions that are brought into contact with each other. The solvents need not be miscible with each other. Thus, in each instance, the reactants interact with each other while in a dissolved condition, but not necessarily in the same solvent. Also, in cases in which two different solvents are used, one for each reactant, it is not necessary for one solution to be mixed with the other. Interaction of the reactants can occur solely by diffusion or, if the solvents are immiscible, at an interface between the solvents. Whenever dissolution of a solute is facilitated by use of a complexing agent, it is not necessary that all the solute be dissolved before the onset of reaction. The complexing agent is typically not consumed during the reaction and can therefore serve as a "dissolution catalyst" for the corresponding solute. As solute molecules dissociate from molecules of the complexing agent and become incorporated into the crystalline product, the liberated molecules of the complexing agent become free to facilitate dissolution of more of the remaining unreacted solute. Thus, the complexing agent can be present in "catalytic" (i.e., substoichiometric) amounts. The product of the reaction forms as one or more crystalline masses (crystallites) that precipitate and are thus readily separable from the solution(s) using conventional separation techniques. The crystallite can be comprised of visually discernable crystals or of crystals that are so small that the crystallite appears to be amorphous. A key factor in determining whether or not a solute will dissolve in a solvent is the polarity of molecules of the solute relative to molecules of the solvent. In general, polar solutes, (such as salts that dissociate into their constituent ions upon dissolution) are more soluble in polar solvents than in non-polar solvents; and non-polar solutes are more soluble in non-polar solvents compared to polar solvents. Thus, at a given temperature, a greater amount of a polar solute will dissolve in a polar solvent than in a relatively non-polar solvent. Likewise, a greater amount of a non-polar solute will dissolve in a non-polar solvent than in a polar solvent. The complexing agent, by bonding to the solute, alters the polarity of the solute, usually by making the solute molecules (or constituent ions) less polar. In most instances and not intending to be limiting, at least one of the reactant solutes is normally soluble in water and has either limited solubility or is substantially insoluble in less polar solvents, including at least one of the solvents employed in the reaction. Thus, in such instances, at least one of the solvents is other than substantially pure water; i.e., a solvent substantially less polar than pure water. In order to dissolve the solute in such a solvent, a conφlexing agent is selected that is soluble in the solvent and that can form a complex with the solute to be dissolved in the solvent. It is also possible according to the present invention for a solute reactant to be normally soluble in an organic solvent. In such an instance, a suitable complexing agent can be used to dissolve the solute in a water-containing solvent. In a reaction system according to the present invention, it is possible for a first reactant to be soluble in the reaction solvent and a second reactant to have limited solubility in the solvent. In such an instance, the complexing agent is used to facilitate dissolution of the second reactant in the solvent. Reaction systems according to the present invention also include systems in which both the first and second reactants require complexing agents for dissolution. The complexing agents can be the same or different. In a representative example of such a system, a first solution containing a first complexed reactant is layered atop a second solution containing a second complexed reactant, wherein the reaction occurs at the interface of the first and second solutions. Additional "phases" are also possible. It is not necessary that the reaction system comprise a phase interface at all. "Single-phase" reactions involving a single solution containing all the reactants (and at least one complexing agent) are within the scope of the present invention. The complexing agent performs at least one of the following roles: (a) solubilizing a reactant in a solvent; and (b) influencing the habit and/or morphology of the crystalline product formed, presumably by affecting the differential rates of growth on certain crystal faces but not others. In reaction systems in which both reactants, in the absence of the complexing agent, are insoluble in the solvent, the complexing agent generally performs both roles. In reaction systems in which one reactant is insoluble in the solvent and requires complexation with the agent in order to be dissolved in the solvent, but the other reactant is soluble in the solvent, the complexing agent again performs both roles. In reaction systems in which both reactants are soluble in the solvent, the complexation agent mainly serves the second role. A molecule of the complexing agent facilitates dissolution of a reactant molecule by forming a complex with the reactant molecule. Due largely to the solubility of the complexing agent in the solvent employed, the resulting complex is also soluble in the solvent. Such complex formation can be exemplified by envisioning formation of a chelate, as known in the art, comprising a molecule of the complexing agent (serving as a chelating agent) interacting with a molecule of the reactant in a non-covalent way (i.e., by dative bonding) so as to form a coordination compound. In such a coordinating compound, an ion of the solute is attached by multiple coordination links to two or more usually non-metal atoms in the same complexing-agent molecule. Complexing agents offering two groups for attachment to the ion are termed "bidentate;" complexing agents offering three groups are termed "tridentate, " and so on. The chemical groups on the complexing agent that participate in bonding of the solute are typically election-donors. Complexing agents are also termed "ligands'in the art. As can be surmised from the foregoing, since molecules of complexing agents typically have bonding groups that are electron donors, the regions of the corresponding solute molecules that become bonded to such complexing agents are electron acceptors. That is, the corresponding solute "molecules" typically are cationic, and can be actual polyatomic or monoatomic cations. It is also possible for the solute "molecules" to interact with the complexing agent by other bonding mechanisms such as hydrogen bonding. It is also possible that the complexing agent, which interacts with the cationic aspect of the corresponding solute in a bonding way, also interacts with solutes in other ways to facilitate dissolution of the solute. For example, the complexing agent in a relatively non- polar solvent may interact with non-polar regions of solutes by, for example, "hydrophobic" bonds. The bonding of solute to the complexing agent must not be so strong that, during the crystallite-forming reaction, the solute cannot dissociate from the complexing agent. Release of solute from complexing agent molecules to form crystallite product must be energetically favorable. Candidate complexing agents include, but are not limited to, the following: crown ethers (any of various cyclic polyethers in which the ether groups are connected by dimethylene or silicon linkages and the ether oxygen atoms serve as electron donors); ethylenediaminetetraacetic acid (EDTA) and analogs of this compound; nitrilotriacetic acid N(CH j COOH) 3 ; ethyleneglycol-bis(/^aminoethylether)-N,N-tetraacetic acid (HOOCCH 2 ) 2 NCH 2 CH 2 OCH 2 CH 2 OCH 2 CH 2 N(CH 2 COOH) 2 ; diethylene-triaminepentaacetic acid (DTP A); desferroxamine and analogs thereof; ammine derivatives; metallocenes; hydroxycarboxylic acids, polyethylene glycols and corresponding dimethyl ethers; polyethyleneimine; tris-(methoxyethoxyethyl)amine and related compounds; and even kojic acid (which is a manganese chelator). Candidate crown ethers include, but are not limited to, 12- crown-4, 15-crown-5, 18-crown-6, dicyclohexyl-18-crown-6,and dibenzo-18-crown-6. Each crown ether binds a particular range of cations, depending upon the size of the central cavity of the crown ether molecule. For example, 12-crown-4 binds Li + well but K + poorly; dibenzo-18- crown-6 binds K + well but Li + poorly. Similarly, dibenzo-18-crown-6 binds Sr 2+ and Hg 2+ well but Ca 2+ , Cd 2+ , Zn 2+ relatively poorly. Although crown ethers are conventionally used mostly for complexing simple cations, they can also complex amines, phenols, and other compounds. The complexing agent can also be a "macrocyclic'compound which is essentially a crown-ether analog containing nitrogen or sulfur atoms or more than one kind of the hetero atom. Such compounds include bicyclic molecules that can surround an enclosed ion in three, rather than two, dimensions. If one is having particular difficulty in achieving dissolution of a reactant, other possible complexing agents can be considered, such as any of various compounds termed "cryptands, "including "spherands," "calixarenes," "cryptophanes," "hemispherands," "podands," and "lariat ethers." A number of proprietary complexing agents are also available. The maximal amount of complexing agent to employ in a desired reaction system would be, for economic reasons, no greater than a stoichiometric amount relative to the amount of the corresponding reactant. Of course, if the complexing agent works "catalytically," substantially less than a stoichimetric amount would be required. In general, crown ethers and "cryptophane" complexing agents work well for dissolving solutes containing alkali-metal cations. For solutes containing transition-metal cations, the crown ethers can be satisfactory, but complexing agents having electron donor atoms other than oxygen work better. For a desired reaction, persons of ordinary skill in the art would be able to select a complexing agent that would perform the foregoing tasks. Many candidate complexing agents are commercially available and can be tested for efficacy in a given reaction by a sinφle test-tube experiment. It is also comprehended that many complexing agents, such as (but not limited to) crown ethers, can be made more soluble in certain hydrophobic solvents by chemically attaching lipophilic moieties to molecules of the agents. Bench-top experiments to test the efficacy of a particular complexing agent are within the skill of persons of ordinary skill in the relevant art. For example, many candidate solutes form colored solutions. For such solutes, if color is absent, while using a particular complexing agent, then it is probably that substantially no dissolution occurred. For example, solutions containing chromates tend to be yellow; solutions of CoCl 2 tend to be dark blue. If the solution is naturally colorless, a precipitating anion can be added, using techniques of classical analytical chemistry, to see if a visible precipitate forms. For example, with solutions of nickel salts, addition of a Na 2 S solution will form a precipitate if the solution being tested contains any nickel ions. Of course, modern analytical techniques can also be employed to test for dissolution, such as atomic absorption spectroscopy. With respect to reactant solutes that are normally soluble in water, candidate solvents for use in reaction systems according to the present invention include any of various solvents that are less polar than water, particularly relatively non-polar organic solvents. Such solvents include hydrophobic solvents and solvents that have some degree of hydrophilicity (normally less than water). Such solvents can also comprise mixtures of pure solvents. Such mixtures can include water. The solvent can also be one of the supercritical solvents, such as supercritical carbon dioxide. Choosing a solvent can be somewhat empirical. Basically, if a solute cannot be made to dissolve in the solvent, even after attempting to facilitate dissolution using various complexing agents, a different solvent should be selected. Sometimes, difficulties with a solvent can be solved by simply using a different complexing agent. If dissolution of the solute is too slow, agitation can be helpful, including use of an ultrasonicator. The solvent need not be a freely flowing liquid. It is also contemplated that the solvent can comprise, for example, a gel. In the usual instance where the solvent is non-polar, any of various non-polar gels can be used, including any of various organic polymer gels such as, but not limited to, polystyrene gel and PVC gel. Use of gel solvents can have particular utility in two-phase reactions (i.e., reactions involving one solution layered atop another wherein the reaction occurs at the interface) according to the present invention, wherein the gel can serve to slow the rate of reaction and can simplify setting up the phases prior to onset of the reaction. Solvent-swollen organic polymers can also be used, which function similarly to a gel in reaction systems according to the present invention. Inducing formation of a crystalline product in a reaction system according to the present invention can be, and usually is, spontaneous. However, crystallization can be triggered by introducing a seed crystal or other nucleation aid to the system. Other methods of inducing crystal formation include thermal shock, physical shock, and methods that achieve at least localized supersaturation. The products of reactions according to the present invention are crystalline materials (i.e., "crystallites") and can be organic or inorganic. Such materials can comprise an assemblage of individual crystals that are microscopic in size. Generally, the faster the reaction, the smaller the crystals of the product. The crystalline products of reactions according to the present invention are not necessarily comprised of crystals larger than products of corresponding reactions according to the prior art. Rather, the crystalline products of reactions according to the present invention have been found to exhibit an altered habit and/or morphology. In the case of reactions according to the present invention forming products consisting of smaller crystals, such crystallites can have unusual physical properties compared to crystallites consisting of larger crystals. Preferred solutes usable according to the present invention are any of various water-soluble compounds that can react with other such compounds to form crystalline products. Such compounds are typically referred to as "salts" that can be dissociated to corresponding anions and cations. Representative anions and cations, not intended to be limiting, are listed in Tables I and II, respectively. Table I Representative Anions actinium hydrogen samarium aluminum indium scandium ammonium indium selenium antimony iron silicon barium lanthanum silver beryllium lead sodium bismuth lithium sulfur boron magnesium tantalum rjn-miiim manganese tellurium calcium mercury terbium cerium molybdenum thallium cesium neodymium thorium chromium nickel tin cobalt osmium titanium copper palladium tungsten dysprosium phosphorus uranium erbium platinum vanadium gadolinium potassium ytterbium germanium rhenium yttrium gold rhodium zinc hafnium rubidium zirconium holmium ruthenium Table II Representative Cations acetate hydrogen arsenate acetylide hydrogen carbonate aluminide hydrogen fluoride aluminum fluoride hydrogen phosphate arsenate hydrogen selenite arsenite hydrogen sulfate bicarbonate hydrogen sulfide biiodate hydrosulfite biphosphate hydroxide bismuth oxide iodide boride iron oxide bromate metabisulfite bromide metaborate carbide niobium oxide carbonate metasilicate chlorate tantalum oxide chloride metatungstate chloroacetate molybdenum oxide chlorodifluoroacetate nitrate chromate nitride chromite nitrite citrate orthosilicate cobalt oxide oxalate cyanotrihydroborate oxide dibromide dioxide pentacyanomtrosylferrate dichloride dioxide perborate dichromate perchlorate diethyldithiocarbamate peroxydisulfate dihydrogen diphosphate perrhenate dihydrogen phosphate phosphate disulfite potassium sulfate dit ionate potassium tartrate iron oxide pyrophosphate ferricyanide selenate fluoride selenide fluorophosphate selenite formate sulfate hexabromoiridate sulfide hexabromoplatinate sulfite hexachloroiridate tartrate hexachloroosmiate tellurate hexachloropalladate telluride hexachloroplatinate tetraborate hexachlororhodate tetrachloroaluminate hexafluoroaluminate tetrachloraurate hexafluoroarsenate tetrachlorpalladate hexafluoroferrate tetrachloroplatinate hexafluorophosphorus tetrafluorborate hexafluorosilicate thiocyanate hexafluorotitanate thiophosphate hexahydroplatinate thiosulfate hexametaphosphate tin oxide hexanitrocobaltate titanium oxide hexanitroiridate triphosphate hydride tungsten oxide vanadium oxide zirconium oxide The present invention can have utility in any application in which altered crystal form is a benefit. The following are representative applications and are not intended to be limiting in any way: (a) Production of composite materials having novel or improved properties: For example, ZnS is transparent to infrared radiation. Unfortunately, ZnS in its currently available form is brittle. The present invention allows one to produce ZnS having an unconventional crystalline habit, such as fibrous ZnS crystals, that could be used to make composite materials having infrared transparency and that are less brittle. (b) Production of improved photographic emulsions: Silver halide is a key ingredient in photographic emulsions. Alterations in crystal shape of this compound would likely be instrumental in improving the resolution, for example, of photographic films. (c) Explosives: In crystalline materials having explosive properties, it is usually desirable that the energy density of the crystal lattice of such a material be as high as possible. The present invention makes it possible to form explosive compounds having altered crystal habit and morphology, and therefore altered energy density, such as any of various explosive ammonium compounds. (d) Non-linear optical materials: Reaction systems according to the present invention can utilize so-termed "assymmetric" solvents which can be utilized to generate assymmetric crystalline products having possible utility as non-linear optical materials. For example, organic compounds often display very high non-linear optical properties. High polarizability of an organic molecule frequently contributes to enhanced non-linear properties (e.g.,p-nitroaniline). Unfortunately, the vast majority of organic compounds crystallize in centrosymmetric space groups, eliminating them as non-linear materials. Simply varying the solvent according to conventional methods in order to alter crystal habit or morphology is often limited, particularly for many of the more polarizable compounds of interest which are largely only soluble in quite polar media. Reaction systems according to the present invention can be used to eliminate these problems. (e) Semiconductors and other electronic materials: Formation of metal chalcogenides, such as CdSe, ZnS, and ZnSe, is conventionally performed using ionic precursors including, e.g.,CdS0 4 and Na-Se. As a result, these preparations are conventionally carried out in the condensed phase in aqueous solvents. Conventional technology also includes schemes for making such compounds utilizing gas-phase reactions or organic solvents. But, these methods often entail use of volatile and toxic precursors such as H 2 Se and CdMe-. The present invention permits solubilization of ionic-precursor compounds via complexation, followed by slow diffusion of reacting solutions leading to precipitation or crystallization of the desired product from solvents that have heretofore not been accessible due to the insolubilities of the reacting species. For example, sulfide, selenide, and telluride can be solubilized in hydrocarbon and ethereal solvents through formation of crown-either complexes of their lithium, sodium, or potassium salts. Commercially available crown ethers can also solubilize a number of salts of metal ions of interest, including Hg 2+ , Cd 2+ , and Pb 2+ . Simple synthetic complexation agents can be readily prepared to solubilize a number of other relevant ions. See, e.g.. Lindoy, The Chemistry of Macrocvclic Lieand Complexes . Cambridge Univ. Press (1989). Thus, codiffusion of reactant solutions can result in formation of the corresponding metal chalcogenides. The present invention also makes it possible to form semiconductor materials, such as CdS and ZnS, comprising very small crystallites. Such materials are currently the subject of considerable research pertaining to "quantum dot" or "quantum-confined" systems. The present invention also makes possible the synthesis of photocatalytically active semiconductor crystallites having altered properties. (f) Lubricants: Certain metal sulfides such as MoS 2 and WS 2 are useful as lubricants whose properties are dependent upon the crystal habits and morphologies of these compounds. The present invention makes it possible to modify the crystal forms of these compounds in possibly beneficial ways. (g) Display technology: Certain crystallites that can be formed according to the present invention, such as TiS 2 and ZrS 2 , are particularly useful for high-resolution video display technology. (h) Biological/medical applications: A number of medically important salts can be synthesized according to the present invention, wherein the crystalline habit and morphology of such materials can be beneficially altered. In nature, a number of crystallites of inorganic or predominantly inorganic nature are formed in non-aqueous environments and are therefore difficult to duplicate using conventional aqueous systems. (See, e.g- Bianconi et al.. Nature 349:315-317(1991).) The present invention, in which new forms of crystallites can be produced by reactions in non-aqueous environments, offers the capability of producing materials that more closely mimic what is produced in nature. (i) Production of materials having altered bulk properties as a result of changes in crystal habit or morphology of the material (but not the chemical composition of the material): Changes in crystallites made possible by the present invention can yield beneficial alterations in packing behavior, e.g., making particulate materials in a form that is less likely to result in clumping or packing; i.e., having more "free-flow" characteristics. The following examples are provided: Examples 1-35 These Examples pertain to reactions involving catalytic solubilization of a solute in a single-solvent phase. Stoichiometric amounts of solid comminuted reactants as set forth in Table III were mixed with the corresponding anhydrous organic solvent (Table III), either with or without a complexing agent (the crown ether dibenzo-18-crown-6). In view of the rather sparing solubility of heavy-metal complexes of dibenzo-18-crown-6, suspensions of the solid metal salt and sodium sulfide were stirred in the corresponding organic solvent with a "catalytic" amount of the complexing agent. Crystalline products produced with and without the complexing agent were examined by scanning electron microscopy and x-ray powder diffraction (see, e.g- Hilgenfeld et aL. Top. Curr. Chem. 101: 1-82.1982Y. and compared with crystalline products produced in controls containing water solvent (Examples 5, 10, 15, 20, 25, 30, and 35) or controls containing no complexing agent (e.g., Examples lc, 2c, 3c, and 4c). Reaction temperature was ambient room temperature. Crystalline products were harvested from the solvent liquid using conventional techniques. After harvesting, the crystals were washed using additional solvent lacking the complexing agent. Table III Example Solvent Complexinσ Aσt Reactants Product 1 THF dibenz-18-C-6 Pb(OAc) 2 + Na 2 S PbS lc THF none " PbS 2 toluene dibenz-18-C-6 " PbS 2c toluene none " PbS 3 N,N-DMF dibenz-18-C-6 " PbS 3c N,N-DMF none " PbS 4 acetonitrile dibenz-18-C-6 PbS 4c acetonitrile none PbS 5 water none PbS 6 THF dibenz-18-C-6 HgCl 2 + Na 2 S HgS 7 toluene HgS 8 N,N-DMF HgS 9 acetonitrile HgS 10 water none HgS 11 THF dibenz-18-C-6 ZnCl 2 + Na 2 S ZnS 12 toluene ZnS 13 N,N-THF ZnS 14 acetonitrile ZnS 15 water none ZnS 16 THF dibenz-18-C-6 Mn(OAc) 2 + Na 2 S MnS 17 toluene MnS 18 N-N-DMF MnS 19 acetonitrile MnS 20 water none MnS 21 THF dibenz-18-C-6 FeCl 2 + Na 2 S FeS 22 toluene FeS 23 N,N-DMF FeS 24 acetonitrile FeS 25 water none FeS 26 THF dibenz-18-C-6 CU(OAC) 2 + Na 2 S CuS 27 toluene CuS 28 N,N-DMF CuS 29 acetonitrile CuS 30 water CuS 31 THF dibenz-18-C-6 CdCl 2 + Na 2 S CdS 32 toluene CdS 33 N,N-DMF CdS 34 acetonitrile CdS 35 water none CdS In Table III, "THF" is anhydrous tetrahydrofuran, "N,N-DMF"is anhydrous N,N- dimethylformamide, and "dibenz-18-C-6"is the crown ether dibenzo-18-crown-6. Dibenzo-18-crown-6 was chosen as an inexpensive, commercially available crown ether displaying somewhat enhanced lipophilicity compared to the parent crown ether, 18- crown-6. Despite this enhanced lipophilicity, the heavy metal salt complexes of dibenzo-18- crown-6 displayed only a limited solubility in common organic solvents. In all the foregoing examples, crystalline product formed in the corresponding organic solvent. However, presence of the complexing agent in the organic solvent generally resulted in the formation of more clearly defined crystals than were observed in the organic solvent lacking the complexing agent. In addition, crystals formed in an organic solvent with the complexing agent were substantially more defined than the crystalline products formed in an aqueous solvent. For example, in Example 5, precipitation of PbS by admixture of aqueous solutions of lead (II) acetate and sodium sulfide yielded a nearly amorphous precipitate as observed under scanning electron microscopy (FIG. 1). X-ray powder diffraction analysis revealed that the precipitate comprised extremely fine crystals of cubic-phase lead sulfide commonly known as "galena. " Precipitation of PbS from anhydrous tetrahydrofuran (Example lc) in the absence of complexing agent yielded a microcrystalline product that was qualitatively similar to the product of Example 5. In contrast, the presence of a catalytic amount of dϊbenzQ-18-crown-6 (Example 1) in the anhydrous THF yielded precipitate exhibiting much greater crystallinity (FIG. 2), thereby providing a dramatic example of the impact of complexation on the formation of crystalline product from a reaction according to the present invention. Examples 2c, 3c, and 4c, which lacked the complexation agent, exhibited formation of a microcrystalline galena product similar to Examples lc and 5. In Examples 2-4, the presence of the complexing agent resulted in formation of PbS product that was coarser and had a distinctive crystal structure. Also, the crystals obtained in the presence of complexing agent were affected by the choice of solvent. In particular, crystals obtained in DMF were more prismatic than crystals obtained in toluene or THF. Therefore, the qualitative yield of crystalline product depended upon not only the coordinating ability of the complexing agent but also upon the solvent. The remaining examples that included a complexing agent (i.e., Examples 6-9, 11-14, 16-19, 21-24, 26-29, and 31-34) exhibited results that were similar to, but less pronounced than, the results obtained with PbS. The foregoing results also indicate that the complexing agent serves not only to enhance solubility of the reactants in the solvent(s) but also exerts an influence on crystal shape and size of the product of the reaction. Examples 36-38: These Examples, shown in Table IV, were an investigation of a reaction according to the present invention occurring in a two-phase solvent-solvent reaction system. Table IV Ex. Solvent Complexing Aσt Reactants Product 36 water none HgCl 2 + Na 2 S metacinnabar 3 377 tt:: wwaatteerr nnoonnee HgCl 2 b: meth. chlor. none Na 2 S metacinnabar 38 t: water none HgCl 2 cinnabar and : meth. chlor. d-_18- C -6 Na 2 S metacinnabar In Table IV, "t" signifies the top phase layer in the reaction system, and "b" signifies the bottom phase layer; "d-18-C-6"signifies the complexing agent dibenzo-18-crown-6; and "meth. chlor. " signifies methylene chloride. In Example 36, which served as a control, the reaction system comprised HgCl 2 and Na 2 S in aqueous solution. The reaction system of Example 37 comprised a top phase containing an aqueous solution of HgCl 2 , and a lower phase consisting essentially of a mixture of chloroform and methylene chloride solvents, with Na 2 S dissolved in the lower phase. The reaction system of Example 38 was the same as Example 37 except that the complexing agent 18-crown-6 was also present in the lower phase. In all three reaction systems, a precipitate formed at the interface of the liquid phases. In Examples 36 and 37, the precipitate when viewed by scanning electron microscopy appeared substantially amorphous (FIG. 3) and consisted only of metacinnabar. In Example 38, the precipitate consisted of about equal amounts of cubic metacinnabar and hexagonal cinnabar crystals. In addition, the crystals were substantially coarser with clearly defined faceting (FIG. 4). On prolonged contact time with Example 38, macroscopic crystals of cinnabar were obtained in the form of fibrous bundles of whisker-like crystallites, as shown in FIG. 5. Thus, the presence of the complexing agent in this reaction system facilitated the production of substantially altered crystal forms of HgS. Examples 39-40: In these Examples, homogeneous solutions of mercuric iodide (Hgl 2 ) and sodium sulfide (Na-S) were prepared in dimethylsulfoxide (DMSO) either with (Example 40) or without (Example 39) the complexing agent dibenzo-18-crown-6. The crystalline precipitate formed in Example 39 consisted of metacinnabar only. The crystalline precipitate formed in Example 40 consisted of equal amounts of cinnabar and metacinnabar. Examples 41-44: These Examples constitute investigations into reaction systems according to the present invention that pertain to crystalline product formation in a gel. In Examples 41 and 42, PVC (polyvinylchloride) gels in DMF solvent were prepared using conventional techniques. The gels also contained dissolved HgCl 2 . The gels were overlaid with DMF also containing Na 2 S and either containing dibenzo-18-crown-6 as a complexing agent (Example 42) or lacking a complexing agent (Example 41). After allowing for diffusion to occur in the gels at room temperature, a precipitate was observed in each. Subsequent washing with DMF caused the gel to dissolve, thereby permitting harvesting of the precipitate. When formed in the presence of the complexing agent (Example 42), the precipitate comprised prismatic crystals of HgS. When formed in the absence of the complexing agent (Example 41), the precipitate lacked any visible crystalline structure. In Examples 43 and 44, similar gels were produced as in Examples 41 and 42 except that, in Examples 43 and 44, DMSO was used as the gel solvent. The gels also contained dissolved HgCl 2 . The gels were overlaid with DMSO also containing Na 2 S and either containing dibenzo-18-crown-6 as a complexing agent (Example 44) or lacking a complexing agent (Example 43). After allowing for diffusion to occur in the gels at room temperature, a precipitate was observed in each. The gels were dissolved and the precipitate collected. In both Examples, the precipitate appeared similar, with little crystallinity. These results suggest that both the solvent and the complexing agent play a role in determining the crystallinity of the product in reaction systems according to the present invention. Examples 45-46: In these examples, an aqueous solution of CaCl, was placed on one side of a PVC-DMSO gel. An aqueous solution of (NH 4 ) 2 C0 3 was placed on the opposite side of the gel. The gel either contained the complexing agent dibenzo-18-crown-6 (Example 46) or lacked any complexing agent (Example 45). The solutions were allowed to diffuse through the gel for a sufficient amount of time to react with each other. In Example 45, no precipitate formed at all. In Example 46, in contrast, CaC0 3 crystals were formed in the gel. Examples 47-48: In these Examples, a two-phase reaction system was investigated and found to effect a deprotonation reaction in which solvent served as a reactant. In Example 47, an aqueous solution of dipotassium tartrate was layered above a solution of 18-crown-6 in methylene chloride. Upon prolonged contact of these two solutions, single crystals appeared at the interface. Infrared, nuclear magnetic resonance, and solubility analysis of the precipitate indicated that the crystals were not dipotassium tartrate but rather potassium hydrogen tartrate. This was confirmed by single-crystal x-ray diffraction analysis. In contrast, recrystallization of dipotassium tartrate from water (Example 48) did not form potassium hydrogen tartrate but rather re-formed dipotassium tartrate crystals. Apparently, solubilization of tartrate in the methylene chloride solvent, where the tartrate behaves as a stronger base, may be responsible for the formation of the monoprotonated salt precipitate. Interestingly, the prismatic crystal form displayed by the potassium hydrogen tartrate formed in Example 47 was distinct from the crystal form of the same salt crystallized from water. Example 49: This Example was similar to Example 47, except that carbon tetrachloride was used as the solvent rather than methylene chloride. The resulting precipitate was comprised of block-shaped crystals of potassium hydrogen tartrate. Examples 50-51: These Examples were an investigation of crystal formation according to the present invention using solvents containing water (i.e. , solvents not consisting essentially of pure water). Exanφles 50 and 51 comprised the preparation of two samples of silver chromate (Ag 2 Cr0 4 ) by admixture of solutions of AgN0 3 and K 2 Cr0 4 . In Example 50, which served as a control, an AgN0 3 solution in water was added dropwise to a solution of K 2 Cr0 4 in water, resulting in immediate precipitation of a red-brown powder. The powder was isolated by filtration, washed with water, washed with ethanol, and washed with diethyl ether, yielding Ag 2 Cr0 4 as a brown powder in a high yield. In Example 51, AgN0 3 was dissolved in 0.5 mL water, then diluted with 4 mL ethanol. This solution was added dropwise to 6 mL of a solution of K 2 Cr0 4 in ethanol containing three equivalents of 18-crown-6, resulting in immediate precipitation of a red powder. (Note: K 2 Cr0 appears to be completely insoluble in ethanol in the absence of 18- crown-6.) The powder was isolated by filtration, washed with ethanol, washed with water, washed with ethanol, and washed with diethyl ether, yielding Ag 2 Cr0 4 as a red powder in high yield. The brown powder of Example 50 and the red powder of Example 51 were examined by x-ray powder diffraction and were found to be the known orthorhombic phase of Ag 2 Cr0 4 . Each powder appeared crystalline. However, Example 50 (prepared from water) appeared to be composed of significantly larger crystallites, as evidenced by sharper lines in the powder diffraction pattern. Scanning electron microscopy confirmed the x-ray powder diffraction results: Example 50 consisted entirely of apparently well-faceted crystallites having a mean diameter of about 0.5 to 1.0 μm. Example 51 displayed a crystallite structure in which individual crystals were substantially smaller than Example 50, so small as to confer an almost amorphous appearance to the crystallite. Although Example 51 in this instance yielded crystals that were smaller than the control (Example 50), these Examples again show that crystallization of reaction product from a solution containing a complexing agent used to facilitate dissolution of at least one reactant yielded an alteration of the crystalline form of the product compared to controls lacking the complexing agent. In fact, these Examples illustrate that the present invention can have particular utility for use in making "quantum dots" or "nanoparticles," many of which display a number of unusual properties of potential significance in contemporary technology. Examples 52-54: These Examples are an investigation of the use of complexing agents other than crown ethers. Each of the following Examples involved the use of tris(methoxyethoxyethyl)amine: N(CH 2 CH 2 θCH 2 CH 2 OCH 3 ) 3 as a complexing agent. This complexing agent (or any of various other complexing agents that could have been used) was necessary in order to achieve dissolution of sufficient amounts of AgN0 3 in diethyl ether so as to form satisfactory amounts of reaction product. In Example 52, AgN0 3 was dissolved in diethyl ether containing tris(methoxyethoxyethyl)amine. This solution was layered into an aqueous solution of K 2 Cr0 4 , resulting in formation of red-brown Ag 2 Cr0 4 at the interface between the solutions. In Example 53, AgN0 3 was dissolved in diethyl ether containing tris(methoxyethoxyethyl)amine. This solution was layered onto an aqueous solution of NaBr, resulting in formation of white AgBr at the interface between the two solutions. In Example 54, AgN0 3 was dissolved in diethyl ether containing tris(methoxyethoxyethyl)amine. This solution was layered onto an aqueous solution of (NH 4 ) 2 Mo0 4 , resulting in formation of white Ag 2 Mo0 4 at the interface between the two solutions.

Claims: CLAIMS 1. A method for forming a crystallite product, comprising: (a) providing a first reactant compound that is more soluble in a first solvent than in a second solvent; (b) providing a second reactant compound that can react with the first reactant compound in the first solvent to form a crystallite product; (c) providing a complexing agent that is soluble in the second solvent, the complexing agent being comprised of molecules that can form molecular complexes with the first reactant, thereby enabling the complexing agent to facilitate dissolution of the first reactant in the second solvent; (d) adding the first and second reactant compounds along with the complexing agent to the second solvent; and (e) allowing the first and second reactant compounds to react with each other in the second solvent, wherein the complexing agent facilitates formation of a crystallite product that is insoluble in the second solvent and that comprises crystals that are different from crystals of the crystallite product foπnable in the first solvent by reaction of the first and second reactant compounds in the first solvent. 2. A method as recited in claim 1 wherein, in step (a), the first solvent is a polar solvent and the second solvent is less polar than the first solvent. 3. A method as recited in claim 2 wherein, in step (a), the first solvent is water. 4. A method as recited in claim 3 wherein the first and second reactant compounds are salts that dissociate in the first solvent to form respective anions and corresponding cations. 5. A method as recited in claim 2 wherein, in step (a), the second solvent is an organic solvent. 6. A method as recited in claim 5 wherein, in step (a), the second solvent is substantially non-polar. 7. A method as recited in claim 1 wherein, in step (d), the first and second reactant compounds and the complexing agent are added to the second solvent that is a gel. 8. A method as recited in claim 1 wherein, in step (e), the crystallite product formed in the second solvent has a different crystalline habit than the crystallite product formable in the first solvent. 9. A method as recited in claim 1 wherein, in step (e), the crystallite product formed in the second solvent has a different crystalline morphology than the crystallite product formable in the first solvent. 10. A method for forming a crystallite product, comprising: (a) providing a first reactant compound that is more soluble in a first solvent than in a second solvent; (b) providing a second reactant compound that can react with the first reactant compound in the first solvent to form a crystallite product, the second reactant compound being more soluble in the first solvent than in the second solvent; (c) providing a first complexing agent that is soluble in the second solvent, the first complexing agent being comprised of molecules that can form molecular complexes with the first reactant, thereby enabling the first complexing agent to facilitate dissolution of the first reactant in the second solvent; (d) adding the first and second reactant compounds along with the first complexing agent to the second solvent; and (e) allowing the first and second reactant compounds to react with each other in the second solvent, wherein the first complexing agent facilitates formation of a crystallite product by reaction of the first and second reactant compounds in the second solvent, the crystallite product formed in the second solvent being insoluble in the second solvent and comprising crystals that are different from crystals of the crystallite product formable in the first solvent by reaction of the first and second reactant compounds in the first solvent. 11. A method as recited in claim 10 further comprising the step, after step (c), of providing a second complexing agent that is soluble in the second solvent, the second complexing agent being comprised of molecules that can form molecular complexes with the second reactant, thereby enabling the second complexing agent to facilitate dissolution of the second reactant in the second solvent. 12. A method for forming a crystallite product, comprising: (a) providing a first reactant compound and a second solvent, wherein the first reactant is more soluble in a first solvent than in the second solvent; (b) providing a second reactant compound that can react with the first reactant compound in the first solvent to form a crystallite product, the second reactant compound being more soluble in the first solvent than in the second solvent; (c) providing a third solvent in which the second reactant compound is at least partially soluble; (d) providing a first complexing agent that is soluble in the second solvent, the first complexing agent being comprised of molecules that can form molecular complexes with the first reactant in the second solvent, thereby enabling the first complexing agent to facilitate dissolution of the first reactant in the second solvent; (d) adding the first reactant compound and the first complexing agent to the second solvent so as to achieve at least partial dissolution of the first reactant compound in the second solvent, thereby forming a first solution; (e) adding the second reactant compound to the third solvent so as to achieve at least partial dissolution of the second reactant compound in the third solvent, thereby forming a second solution; (f) forming a region consisting substantially of the first solution contacting a region consisting substantially of the second solution so as to form an interface intermediate the regions; and (g) allowing the first and second reactant compounds to react with each other at the interface to form a crystallite product at said interface, the crystallite product being substantially insoluble in the second and third solvents, the first complexing agent serving to facilitate formation of the crystallite product having crystals that are different from crystals of the crystallite product formable in the first solvent by reaction of the first and second reactant compounds in the first solvent. 13. A method as recited in claim 12 wherein, in step (c), the third solvent is substantially immiscible with the second solvent. 14. A method as recited in claim 13 wherein step (f) comprises forming a layer of the first solution contacting a layer of the second solution so as to form a phase interface intermediate the layers. 15. A method as recited in claim 12 wherein at least one of the first and second solutions is a gel. 16. A method as recited in claim 12 including the step of providing a second complexing agent that is insoluble in the third solvent, the second complexing agent being comprised of molecules that can form molecular complexes with the second reactant in the third solvent, thereby enabling the second complexing agent to facilitate dissolution of the second reactant in the third solvent; and step (e) further comprises adding the second reactant and the second conφlexing agent to the third solvent, thereby forming the second solution. 17. A reaction system capable of forming a crystallite material by reaction of at least two reactants, the reaction system comprising: (a) a solvent; (b) a first reactant compound normally poorly soluble to insoluble in the solvent; (c) a first complexing agent dissolved in the solvent, to which first complexing agent the first reactant compound has formed molecular complexes that facilitate solubility of the first reactant compound in the solvent; and (d) a second reactant compound capable of reacting with the first reactant compound in the solvent, the reaction system adapted to produce, by reaction of the first reactant compound with the second reactant compound in the solvent, a crystallite product comprising crystals that are different from crystals in a crystallite product formable by reaction of the first and second reactant compounds in a solvent in which both the first and second reactant compounds are soluble without use of die first complexing agent. 18. A reaction system as recited in claim 17 in which the solvent is a gel. 19. A reaction system as recited in claim 17 in which the solvent is an organic solvent. 20. A reaction system as recited in claim 19 in which the solvent is a substantially non-polar solvent. 21. A reaction system as recited in claim 19 in which the first reactant is a first salt normally soluble in water and the first complexing agent is a crown ether. 22. A reaction system as recited in claim 19 in which the second reactant is a second salt normally soluble in water. 23. A reaction system as recited in claim 22 further comprising a second complexing agent dissolved in the solvent, to which second complexing agent the second reactant compound has formed molecular complexes that facilitate solubility of the second reactant compound in the solvent. 24. A reaction system capable of forming a crystallite material by reaction of at least two reactants, the reaction system comprising: (a) a first solution comprising a first solvent, a first reactant, and a first complexing agent to which the first reactant is complexed so as to render the first reactant soluble in the first solvent; (b) a second solution comprising a second solvent and a second reactant at least partially dissolved in the second solution, the first solution forming a first region and the second solution forming a second region contacting the first region so as to form an interface between the first and second regions, at which interface the first and second reactants can undergo a chemical reaction that forms a crystallite product that is insoluble in either the first or second solutions. 25. A reaction system as recited in claim 24 wherein the second solution further comprises a second complexing agent to which the second reactant is complexed so as to render the second reactant soluble in the second solvent. 26. A reaction system as recited in claim 24 wherein the second solution is immiscible with the first solution. 27. A reaction system as recited in claim 24 wherein the interface comprises a gel. 28. A reaction system as recited in claim 24 wherein at least one of the first and second solutions is a gel.

Inventors: DOXSEE KENNETH M, DOXSEE, KENNETH, M.
Applicants: OREGON STATE, THE STATE OF OREGON ACTING BY AND THROUGH THE STAT
Application year: 1994
Main classification: B01D9
IPC codes: B01D9, B82B1, C01F11, C01G5, C09K3, C30B7, G03C1