HEAT-CURED FOUNDRY BINDERS AND THEIR USE

Abstract: This invention relates to heat-cured foundry binders comprising in admixture (1) a source of soluble silica, and (2) a source of soluble alumina, such that the source of silica, source of alumina, or both contain an alkali metal. The binder components form a saturated solution when they are mixed with an aggregate. The resulting mix is shaped and heated at an elevated temperature to form a cured foundry shape. Heat is applied by warm air with warm-box equipment, baking in an oven, microwave, and preferably from hot-box equipment.

Description: HEAT CURED FOUNDRY BINDERS AND THEIR USE FIELD OF THE INVENTION This invention relates to heat cured foundry binders comprising in admixture (a) a soluble source of silica, and (b) a soluble source of alumina, such that the source of silica, source of alumina, or both contain an alkali metal. The binder components form a saturated solution when they are mixed with an aggregate. The resulting mix is shaped and heated at an elevated temperature to form a cured foundry shape bonded together by a crystalline bonding phase. Heat is applied by warm air, baking in an oven, microwave, or preferably from hot-box equipment. BACKGROUND OF THE INVENTION The reaction between a soluble silica source and a soluble alumina source for making cation exchange systems and molecular sieves is known. However, the reaction product can vary widely depending upon the molar ratios of silica and alumina, and the reaction conditions. U.S. Patent 4,357,165 describes how to make self- setting, no-bake foundry binders, based upon a soluble silica source and a soluble alumina source, which cure under ambient conditions. These binders are amorphous hydrogels and remain amorphous hydrogels after curing because the water in the solution is not substantially removed during the curing process. The patent states at column 9, line 66 to column 10, line 4 that no heating or baking of the mold is required, and that, in fact, such treatment may significantly reduce subsequent moisture resistance, storage strength, and resistance to scabbing if introduced before the mold has had a chance to cure. Again at column 11, lines 15-16, the patent states that it is found that high temperatures during the cure period can cause a decrease in tensile strength. These binders have the following deficiencies: (1) low strength and long setting time; (2) excess of free alkalis which is disadvantageous for reclamation; (3) poor humidity resistance; (4) high binder level (up to 6 to 7 weight percent based upon the weight of the sand) is required for effective use; and (5) calcined kaolin must be added to improve the hot strength. Because of these deficiencies, these binder systems are not only impractical for self-setting, no-bake application, but are also useless for high production core and mold making. SUMMARY OF THE INVENTION The subject invention relates to heat cured foundry binders comprising in admixture: (1) a soluble source of silica, and (2) a soluble source of alumina, such that the source of silica, source of alumina, or both contain an alkali metal. The binder components form a saturated solution when mixed with an aggregate. The resulting mix is shaped and cured by heating with warm air, baking in oven, microwave, and preferably in hot-box equipment to form a crystalline binding phase by dehydration during heating. Most of the water is removed from the binder during curing. The foundry mixes prepared with these binders have a benchlife of up to five hours. These heat cured binders differ significantly from the self-setting binders disclosed in U.S. Patent 4,357,165 (see Figure 1) which are hydrogels and are cured at ambient temperature. The heat cured binders which are the subject of this invention form crystalline structures with a characteristic x-ray diffraction pattern (see Figure 2) , and are formed within a prescribed molar ratio of silica source and alumina source. Foundry mixes are prepared by mixing the binder components with a foundry aggregate. In contrast to the foundry mixes of U.S. Patent 4,357,165 which have zero or little benchlife, the foundry mixes made with the subject binders have a benchlife of up to five hours. The foundry mixes are shaped into molds, cores, and assemblies thereof. In contrast to the foundry shapes made with the binders described in U.S. Patent 4,357,165, the subject binders provide cured foundry shapes which set quickly at elevated temperatures, have good tensile strengths, do not require excess free alkali (which is disadvantageous for reclamation and shakeout) , show good humidity resistance, are used in commercially acceptable binder levels (generally less than about 5 weight percent based upon the weight of the aggregate) , and do not need calcined kaolin to improve the hot strength. BRIEF DESCRIPTION OF DRAWINGS FIGURE 1 is an x-ray diffraction pattern for a binder prepared in accordance with U.S. Patent 4,357,165. The x- ray diffraction pattern (scan:3-64/.05/4/^1221, anode CU, zero = 0.0) shows the binder is an amorphous, non crystalline material. FIGURE 2 is an x-ray diffraction pattern (scan:3- 64/.05/4/^1221, anode CU, zero = 0.0) for a binder prepared in accordance with the subject invention. The x-ray diffraction pattern shows the binder is a crystalline material. ENABLING DISCLOSURE AND BEST MODE The binder consists of two components: (1) a soluble silica source, and (2) a soluble alumina source, such that the source of silica, source of alumina, or both contain an alkali metal. Either component may be liquid or solid, but at least one component must be liquid. If either component is a solid component, the solid component will dissolve in the liquid component when the two components are mixed. The soluble silica source is preferably an alkali silicate in aqueous solution, more preferably sodium silicate, colloidal silica, or solid silica, fumed or precipitated. The soluble alumina source is preferably a solid alkali alu inate, or an alkali aluminate in solution, preferably where sodium aluminate is the alkali aluminate. Sodium aluminate can be used as a powder or as an aqueous solution without affecting curing time significantly. The powder, however, provides greater flexibility to the formulator when adding other components to the binder, but liquid components are easier to use. Although various combinations of soluble silica source and soluble alumina source are possible, the best results are obtained when a colloidal silica solution is used with solid or liquid sodium aluminate. The amount of solids in the aqueous solution containing the source of silica generally ranges from 40 to 55 weight percent, based upon the weight of the aqueous solution, preferably about 50 weight percent. The amount of solids in the source of alumina generally ranges from 40 to 50 weight percent, based upon the weight of the aqueous solution, preferably about 45 weight percent. The weight composition of alkali to alumina to silica, expressed as oxides, in the binder ranges from about 20 to about 40 weight percent alkali, from about 30 to about 50 weight percent alumina, and from about 20 to about 40 weight percent silica, said weight percents being based upon the total weight of the binder composition, preferably from about 28 to about 32 weight percent alkali, from about 38 to about 42 weight percent alumina, and from about 28 to about 35 weight percent silica. All weight ratios are expressed as if the source of silica and alumina were an oxide. This is common practice in the trade. The source of silica is first applied to the aggregate when making a foundry mix. Then the source of alumina is mixed with the aggregate. The binder is preferably incorporated with sand at binder levels of 1 to 5 weight percent based upon the weight of the aggregate. The aggregate used to prepare the foundry mixes is that typically used in the foundry industry for such purposes or any aggregate that will work for such purposes. Generally, the aggregate will be sand which contains at least 70 percent by weight silica. Other suitable aggregate materials include zircon, olivine, alumina-silicate sand, chromite sand, and the like. Particularly preferred sand is silica sand having a fineness grade of 70 to 105 for instance. It is believed systems based on such sand will be particularly useful for high pressure die casting. The sand mixture is compacted into cores and/or molds to form foundry shapes and heated to 100*C to 300*C, preferably 150 * C to 250*C until the foundry shapes can be handled without breaking, typically for 30 seconds to 20 minutes. Heating time is a function of the temperature and the heating process used. The heat source may be from the warm air, baking in a conventional oven, microwave, or preferably from hot-box equipment. Foundry shapes prepared with the binder exhibit adequate immediate strengths for handling and show added strength development during 24 hours after curing. The heat-cured foundry shapes also exhibit excellent humidity resistance, much better than the foundry shapes made with the alumino-silicate no-bake binders shown in U.S. Patent 4,357,165. The following abbreviations are used in the Examples and Tables which follow: bos = based on sand BP = blow pressure (psi) CH = constant humidity CT = constant temperature DT = dwell time (seconds) Imm. = immediate PI = Part I (source of silica) PII = Part II (source of alumina) RH = room humidity RT = room temperature Examples A, B, and C are controls introduced for comparative purposes. The foundry shapes are allowed to cure at room temperature substantially in the manner as disclosed in U.S. Patent 4,357,165. Examples 1-3 relate to a binder system wherein the Part II is a solid sodium aluminate while Examples 4-15 relate to a binder system using a liquid Part II. Examples 4-15 also show the effects of using different sand in binder systems where the Part I and Part II components are liquids. The conditions of use are set forth in Tables I to III which follow. The foundry aggregate was prepared by mixing the sand with the Part I and Part II using a paddle style mixer (Hobart N-50) and cured with hot-box equipment. The colloidal silica solution (Part I) contains about 50% solids and only small amount of sodium. The aqueous sodium aluminate solution (Part II) contained 45% solids and has a Na 2 0/Al 2 0 3 molar ratio of 1.26:1.0. The calculated molar ratio of Na 2 0:Al 2 0 3 :Si0 2 is 1.3:1.0:1.3. Mixing the solutions of the silica source and the alumina source resulted in the formation of a saturated solution on the sand mix. The sand mixes were made into the shape of dogbones for tensile strength measurements with a Thwing-Albert TA 500. The dogbone shapes were cured by heating them in hot-box equipment. The temperature of the heated core box, sand type, blow pressure, and the blow time are shown in the tables. The humidity resistance was tested by placing samples which had cured for 24 hrs into a humidity chamber at 25 C * and 99% relative humidity (RH) for 1 hr. The test conditions and the results are summarized in the tables. Metal castings made with the binders showed excellent resistance against erosion and veining while penetration and surface finish were good. Shakeout for aluminum castings was on the average about 45 seconds. Examples A, B, and C are controls introduced for comparative purposes. In these examples, the foundry shape is allowed to cure at room temperature substantially in the manner as disclosed in U.S.* Patent 4,357,165. Table I indicates that tensile strengths of the foundry shapes made with binders according to U.S. Patent 4,357,165 were unacceptable for commercial use. TABLE I (Control) (Foundry Shapes Made According to U.S. Patent 4,357,165) Sand Lab: 24°C, 40% RH CT/CH Room: 25'C, 50% RH Sand: Wedron 540 Part I: Sodium silicate solution (Si0 2 /Na,0 = 2.0) Part II: Sodium aluminate solution, Na 2 0/Al 2 0 3 = 1.26) Part III: 0.4% clay mixture bos as disclosed in U.S. Patent 4,357,165 Box Temp: 21 to 22*C Table II, Examples 1-3, shows the test results using binder systems within the scope of this invention where the Part I is liquid. Part II is solid, and hot-box equipment was used for curing. Foundry shapes with acceptable tensile strengths were made from this binder. TABLE II (Tensile Strengths of Test Foundry Shapes Made with Solid Sodium Aluminate) Sand Lab: 21'C, 51% RH CT/CH Room: 25'C, 50% RH Sand: Badger Part I: LUDOX HS-40 colloidal silica solution/deionized water at a 64/36 ratio Part II: Solid NaAl0 2 (GU-55) , 50 mesh (Na 2 0/Al 2 0 3 = 1.26) Blow Time: 0.5 sec. § 60 psi Box Temp: 232*C Binder TENSILE STRENGTHS Level DT EX PI/PII (sec) Imm. 1 hr 24 hrs 24 +1 (% bos) hrs 1 2.25/1.35 45 32 229 183 165 2 2.25/1.35 60 49 181 169 122 3 2.25/1.35 75 52 225 232 167 Examples 4-15 show test results using binder systems within the scope of this invention where both the Part I and Part II are liquid. Unless otherwise stated, the procedure used was the same as that set forth in Examples 1- 3. TABLE III (Foundry Shapes Made with Liquid Sodium Aluminate Using Different Sands) Sand Lab: 21 * C, 51% RH CT/CH Room: 25 * C, 50% RH Sand: See Table IV Part I: LUDOX TM colloidal silica (50% solution) Part II: Sodium aluminate (45 % solution Na 2 0/Al 2 0 3 1.26) Ratio: Part I/Part II is 1.00/2.50% bos Blow Time: 0.5 sec. § 60 psi Box Temp: 232 * C TENSILE STRENGTHS DT EX. Sand (sec) Inun. 1 hr 24 hrs 24 +1 hrs 4 45 3 276 195 84 5 WEDRON 540 60 12 259 197 73 6 90 17 202 173 92 7 45 33 374 286 127 OKLAHOMA 90 8 60 48 384 310 148 9 90 41 375 287 198 10 45 8 256 184 47 11 MANLEY 1L5 60 12 251 194 85 12 90 17 189 142 60 13 45 5 331 226 120 14 BADGER 5574 60 15 325 221 164 15 90 19 232 207 161 The data in Table IV shows that Oklahoma 90 sand, a high purity silica sand having a fineness grade of 90, produces test foundry shapes which have higher immediate tensile strengths. It is believed systems based on such sand will be particularly useful for high pressure die casting. Other fine silica sands, such as Wedron 710 and Wedron 720, can also be used.

Claims: CLAIMS We claim: 1. A heat curable foundry binder comprising in admixture: (a) a soluble source of silica, and (b) a soluble source of alumina, such that the source of silica, source of alumina, or both contain an alkali metal, and such that the weight ratio of alkali to alumina to silica in the binder ranges from about 20 to about 40 weight percent alkali, from about 30 to about 50 weight percent alumina, and from about 20 to about 40 weight percent silica, said weight percents being based upon the total weight of the binder composition. 2. The foundry binder of claim 1 wherein the source of silica is selected from the group consisting of sodium silicate, colloidal silica solution, solid silica, and mixtures thereof. 3. The foundry binder of claim 2 wherein the source of alumina is solid or liquid sodium aluminate. 4. The foundry binder of claim 2 wherein the weight ratio of alkali to alumina to silica, expressed as oxides, in the binder ranges from about 28 to about 32 weight percent alkali, from about 38 to about 42 weight percent alumina, and from about 28 to about 35 weight percent, said weight percents being based upon the total weight of the binder composition. 5. A heat-cured foundry mix comprising in admixture: (a) a major amount of a foundry aggregate; (b) a source of silica; and (c) a soluble source of alumina, such that the source of silica, source of alumina, or both contain an alkali metal, and such that the weight ratio of alkali to aluminum to silicate in the binder ranges from about 20 to about 40 weight percent alkali, from about 30 to about 50 weight percent alumina, and from about 20 to about 40 weight percent silica, said weight percents being based upon the total weight of the binder composition. 6. The foundry mix of claim 5 wherein the source of silica is selected from the group consisting of sodium silicate, colloidal silica solution, solid silica, and mixtures thereof. 7. The foundry mix of claim 6 wherein the source of alumina is sodium aluminate. 8. The foundry mix of claim 6 wherein the weight ratio of alkali to alumina to silica in the binder ranges from about 28 to about 32 weight percent alkali, from about 38 to about 42 weight percent alumina, and from about 28 to about 35 weight percent, said weight percents being based upon the total weight of the binder composition. 9. A process for preparing a workable foundry shape comprising: (a) forming a foundry mix by mixing a foundry aggregate with a bonding amount of up to about 10 percent by weight, based upon the weight of the aggregate, of a binder composition comprising: (1) a soluble source of silica, and (2) a soluble source of alumina, such that the source of silica, source of alumina, or both contain an alkali metal, and such that the weight ratio of alkali to alumina to silica in the binder ranges from about 20 to about 40 weight percent alkali, from about 30 to about 50 weight percent alumina, and from about 20 to about 40 weight percent silica, said weight percents being based upon the total weight of the binder composition; (b) shaping the foundry mix of (a) into a foundry shape; (c) contacting the foundry shape of (b) with a source of heat at a temperature of 100*C to 250 * C; and (d) allowing the foundry shape to harden into a workable foundry shape. 10. The process of claim 9 wherein the source of silica is selected from the group consisting of sodium silicate, colloidal silica solution, solid silica, and mixtures thereof. 11. The process of claim 10 wherein the source of alumina is sodium aluminate. 12. The process of claim 11 wherein the weight ratio of alkali to alumina to silica in the binder ranges from about 28 to about 32 weight percent alkali, from about 38 to about 42 weight percent alumina, and from about 28 to about 35 weight percent, said weight percents being based upon the total weight of the binder composition. 13. A foundry shape prepared in accordance with claim 9. 14. A foundry shape prepared in accordance with claim 12.

Inventors: LANGER HEIMO J, TWARDOWSKA HELENA, LANGER, HEIMO, J., TWARDOWSKA, HELENA
Applicants: ASHLAND OIL INC, ASHLAND OIL, INC.
Application year: 1994
Main classification: B28B7
IPC codes: B22C1, B28B7, C04B12, C04B28