Rapid-access medical x-ray film and process

Abstract: A medical X-ray film comprising a transparent base coated on at least one side with (a) a laminar grain silver halide emulsion and (b) a separate hydrophillic colloid layer containing a developing agent for silver halide in an amount corresponding to at least 0.5 moles per mole of the silver coated on that side of the base.

Description: This invention relates to medical X-ray films and to their processing. In particular the invention relates to medical X-ray films having significantly reduced processing time. Medical X-ray films typically comprise a transparent substrate coated on one or both sides with a light sensitive silver halide emulsion. Exposure is effected by means of fluorescent screens placed in contact with the emulsion-coated side(s) of the film. The screens absorb a proportion of the X-rays impinging on them and re-emit the energy as visible light, normally in the green portion of the spectrum, and the emulsions are sensitised accordingly. Laminar grain emulsions are increasingly used for X-ray films because of their ability to reduce crossover, i.e. the exposure of an emulsion on one side of the base by light emitted by the screen on the other side of the base. Although crossover decreases the overall exposure required to achieve a given Dmax, it degrades significantly the image resolution. Laminar emulsions have the desirable properties of reducing crossover without undue loss of speed. Even in the case of single-sided X-ray films, laminar emulsions are preferred because they enable the use of reduced amounts of silver. Dye-containing underlayers situated between the base and the emulsions are also frequently used to reduce crossover and halation in double-sided films. In single-sided films, an antihalation layer is normally coated on the back. Protective layers, e.g. of hardened gelatin, are normally coated on top of the emulsions to improve the durability of the film. The exposed films are typically processed by immersion in warm (about 35°C) alkaline developer solution containing developing agents e.g. hydroquinone, phenidone etc., stabiliser e.g. sulphite ion, antifoggants and a hardener e.g. a dialdehyde, such as, glutaraldehyde. Thereafter, the film is fixed, washed and dried, the entire process taking in the region of 90 to 110 seconds dry-to-dry, or longer. There is increasing interest in reducing this time to less than 60 seconds, preferably less than 45 seconds, in the interests of improved productivity, especially during mass screenings. Possible means for reducing the processing time include the use of more concentrated developer solutions and/or higher temperatures, both of which are undesirable from an environmental point of view. The incorporation of developing agents into photographic elements is disclosed widely in the literature. In most cases the developers are incorporated in the emulsion layer itself, but the possibility of incorporation in an adjacent layer is often mentioned. The bulk of the prior art relating to incorporated developers is directed to graphic arts films and plates involving high-chloride non-laminar-grain emulsions, with the object of reducing the amount of noxious chemicals the user must handle before, during and after the processing stage. Also, by using an activator, rather than a developer as the processing solution, replenishment/replacement during continuous operation is less critical. EP-A-281179 discloses a process for developing a photographic material containing on a support an imagewise exposed silver halide emulsion layer of which the silver halide is substantially silver chloride and in which the photographic material before its exposure contains already at least one silver halide developing agent in a hydrophillic colloid binder in waterpermeable relationship with the silver halide, the process containing the step of contacting the exposed photographic material with an aqueous alkaline liquid, called activator liquid, being initially substantially free from developing agent(s), said contacting being not followed by a silver complex diffusion transfer processing, in which the aqueous alkaline liquid contains a primary and/or secondary amine. JP01-072141 and U.S. 5,028,520 disclose photographic elements comprising a tabular (laminar) silver halide emulsion and a polyhydroxybenzene incorporated in the emulsion or in an associated hydrophillic colloid layer. U.S. 5,028,520 relates specifically to X-ray film. The Japanese application specifies a maximum concentration of 0.1 mole/mole Ag for the polyhydroxybenzene and claims a reduction in stress-sensitivity, while the US patent specifies a concentration in the range 0.03 to less than 0.50 moles/mole Ag and claims a reduction in reflectivity of the developed silver image. The preferred concentration range disclosed is 0.03 to 0.30 moles/mole Ag, and most preferred 0.05 to 0.10. Processing is by conventional developer solutions. In both cases, the formula for the polyhydroxybenzenes encompasses compounds such as resorcinols. There is no disclosure of the presence of auxiliary developers, such as phenidone, in the films. It has now been found that the use of incorporated developing agents, present in a layer separate from the emulsion, in an X-ray film having a laminar grain silver halide emulsion, enables rapid processing in simple activator solution. Surprisingly, this is achieved without detriment to the sensitometry of the film. According to one embodiment of the present invention there is provided a method of forming an image comprising the steps of: 1. providing an X-ray film comprising a transparent base coated on at least one side with (a) a tabular grain silver halide emulsion and (b) a separate hydrophillic colloid layer containing a developing agent for silver halide in an amount corresponding to at least 0.5 mole per mole of silver coated on that side of the base., 2. positioning a light-emitting phosphor screen in intimate contact with each emulsion-coated side of the film, 3. imagewise exposing the phosphor screen to X-rays, and 4. contacting the exposed film with an aqueous alkaline activator solution to develop an image. According to a second embodiment of the invention there is provided a medical X-ray film comprising a transparent base coated on at least one side with (a) a tabular grain silver halide emulsion and (b) a separate hydrophillic colloid layer containing a developing agent for silver halide in an amount corresponding to at least 0.5 moles per mole of the silver coated on that side of the base. The X-ray film may have a silver halide emulsion layer (a) and developer layer (b) on each side of the base. The invention enables X-ray images to be produced with greatly reduced processing time, e.g. 45 seconds, without recourse to high temperatures or high concentrations of noxious chemicals. A further advantage is a more consistent sensitometric response. Because each film contains its own complement of fresh developer, large numbers of films can be processed in identical fashion through the same solution. In conventional systems, the developer solution becomes progressively depleted and must be replenished periodically, so that in order to achieve consistent sensitometric results, adjustments in the development process and solution may be necessary depending on the position of the process on the depletion/replenishment cycle. Although the potential benefits of activation processing have long been recognised in the field of graphic arts films and plates, they have not hitherto been exploited in the field of X-ray films, least of all in tabular-grain X-ray films. In the case of graphic arts films, activation processing has not found widespread use due to problems such as high Dmin, low Dmax, low contrast, poor hardening, and staining. Generally speaking, the technique has not proved commercially viable except in the case of rapid-developing high-chloride fine-grain emulsions. X-ray films typically comprise coarse-grained high-bromide emulsions, and since laminar emulsions are known to be particularly prone to most of the above mentioned problems even with normal processing, it is very surprising that activation processing is possible in this case without detriment to the sensitometry. In principle, any of the well-known silver halide developing agents can be used in the invention, such as the compounds listed in Research Disclosure No. 92332 (Section VI) (Dec. 1971), but in practice the preferred compounds are dihydroxybenzenes such as catechol and hydroquinone. Substituted derivatives of these compounds may be used, e.g. with substituents, such as, alkyl groups, halogen atoms, and carboxylic acid groups. Ballasting substituents may be used, as described for example in Research Disclosure No. 17364 (1987), or the developing agent may form part of a polymer for ballasting purposes, as described in European patent Application No. 92307707.7 (filed 24th August 1992). Ballasted developers have the advantage of reduced diffusion into the processing solution, and hence reduced polluting properties, but so far the unsubstituted compounds have given the best sensitometric results, and hydroquinone itself is the most preferred developer. "Masked" developers, where the active developing species is released by reaction with the alkaline activator solution, may also be used. Such materials are described in Canadian Patent No. 766708 and generally comprise easily-hydrolysed esters of hydroquinone and analogous compounds. The concentration of developer in the coated layer is equivalent to at least 0,5 moles per mole of the silver coated on the same side of the base, more preferably at least 0.75 moles per mole of silver, most preferably at least 1.0 moles per mole of silver. In theory there is no upper limit to the amount of developer to be used, but in practice it is found that concentrations greater than 1.5 moles/mole Ag give no further increase in Dmax or speed, and indeed may interfere with the adhesion of the layer to the base. Also, as larger amounts of developer are added, the thickness of the relevant colloid layer increases, which may cause drying problems. A range of 0,5 to 2.0 moles per mole of silver coated on the same side of the base therefore represents a reasonable operating range. The developer is coated in one or more layers, preferably one layer, distinct from the silver halide emulsion layer(s). Although the prior art on activation development of graphic arts films generally advocates incorporation of the developer in the emulsion layer itself, this is found to be unsuitable for the present invention, causing unacceptably high fog. Normally, in the practice of the present invention the developer layer is situated between the base and the emulsion. The developer is coated as a solution or dispersion in an aqueous colloid, normally gelatin, although this may be blended with other materials, such as, dextran, poly(ethyl acrylate), and poly(vinyl alcohol). The developer layer may be hardened with any of the well-known hardening agents such as formaldehyde, vinyl sulphones, and triazine derivative but rapid hardeners such as divinyl sulphone are preferred. The developer layer may also contain an auxiliary developer, also known as an electron transfer agent or super additive developer. Such materials are well known in the art and serve to increase significantly the speed and efficiency of the development process. They are generally used in much lower concentrations than the primary developer, and in the context of this invention a suitable concentration is in the range 4 to 25, preferably 8 to 15 millimoles per mole of silver coated on the same side of the base. The use of auxiliary developers is described, for example, in "The Theory of the Photographic Process" (4th ed.) (ed. T.H. James) chapter 14(II), p.432, and any of the compounds mentioned therein may be used, but the preferred auxiliary developer is phenidone. As an alternative, or in addition, to placement in the developer layer, an auxiliary developer may be added to the activator solution used to process the film. Tabular emulsions, are well known in the art. A tabular emulsion is one in which at least 50% of the grains have an aspect ratio i.e. ratio of diameter to thickness of 3 :1 or greater. There is no particular upper limit for the aspect ratio (AR), but values greater than 15 : 1 are uncommon. A preferred AR range is 3 : 1 to 12 : 1, most preferably from 5 : 1 to 8 : 1. Any of the known methods for preparing such emulsions may be used, but a preferred method is described in U.S. patent No. 5,028,521. The grains may comprise chloride, bromide or iodide ions in any combination, including those in which the different halide ions are distributed unevenly within individual grains, i.e. core-shell emulsions or epitaxial-growth emulsions. Preferably the grains are predominantly silver bromide (e.g. at least 60% bromide), most preferably silver iodobromide with a maximum iodide content of 3.5 mol%. Typical grain sizes are in the range 0.2 to 3.0 µm diameter and 0.05 to 0.3 µm thickness. The emulsion is preferably chemically sensitised by any of the conventional methods, and spectrally sensitised to match the output of the intended phosphor screens (normally green or blue). Any of the commonly used sensitising dyes may be used for this purpose. The emulsion may also contain further ingredients such as antifoggants, hardeners, stabilisers, preservatives, and surfactants, in accordance with known techniques. The base normally comprises polyester (clear or blue tinted) of 50 to 200 µm thickness. It may be surface-treated and/or subbed by any of the conventional methods to increase the wettability and adhesion of the coated layers. The developer and emulsion layers may be coated by any of the standard methods, but are most conveniently coated simultaneously via a multislot coater. Typical silver coating weights are in the range of 1 to 5 g/m 2 on each side. In a preferred embodiment of the invention, the medical X-ray film has a silver halide emulsion layer (a) and a developer layer (b) on each side of the base. Preferably a protective top layer is included comprising gelatin and a relatively high concentration of hardener. Antihalation and/or filter dyes may be incorporated in an underlayer nearest to the base, or such dyes may be incorporated in the developer layer. Suitable dyes absorb strongly at the wavelength of the exposing light (the wavelength of maximum sensitivity of the emulsion), but must bleach or wash out completely during processing of the film. Suitable dyes are disclosed, for example, in U.S. Patents Nos. 4,900,652, 5,028,520 and 5,079,134. The photographic elements of the invention may be exposed using conventional X-ray imaging equipment and appropriate phosphor screens. Processing is effected by contacting the exposed emulsion(s) with an alkaline activator solution. Activator solutions are well known in the art, a commercially available example being "RAPIDOPRINT", sold by Agfa for use with graphic arts films. A typical activator comprises an aqueous solution of an alkaline material, e.g. KOH, NaOH, NH 4 OH, K 2 CO 3 , and Na 2 CO 3 etc, together with a preservative such as sodium sulphite and optionally, a restrainer such as sodium bromide. The activator solution generally has a pH in the range 8 to 14, but preferably at least 9, more preferably at least 10.5. The activation development may be carried out at various temperatures, e.g., at a temperature in the range 10 to 40°C and for various times. Development times of less than 10 seconds are readily achieved. The activator solutions may be applied to the film by any of the known methods such as dipping, spraying, transfer from roller. The film may be immersed in a comparatively large volume of activator, or a thin film of activator may be applied to the surface of the film. Surfactants and/or thickening agents may be added to the activator solution to improve the efficiency of contact with the film surface. Following the activation development process, the film is subjected to fixing, washing and drying in the normal manner. The entire process can be carried out in 45 seconds or less, dry-to-dry. The films can be processed in conventional developer solutions, but there is no particular advantage in doing so. The invention will now be illustrated by the following Examples. Glossary The following abbreviations and trade names are used in the Examples:- HOSTAPUR® - wetting agent available from Hoechst (10% aqueous solution). DEXTRAN® 40 - polysaccharide available from Fisons. PEA - poly(ethyl acrylate) (aqueous dispersion). Sp-1 - log speed at density 0.25 above base + fog. Sp-2 - log speed at density 1.0 above base + fog. Sp-3 - log speed at density 3.0 above base + fog. Acon - average contrast at density 0.25 to 2.0 above base + fog. C.W. - total silver coating weight (i.e. both sides) in g/m 2 . DN - Dornberg Number (an indication of hardness, measured by standard techniques). XP505 - conventional X-ray film processor, available from Minnesota Mining and Manufacturing Company. XAD3 - conventional X-ray film processing chemistry, available from Minnesota Mining and Manufacturing Company. RA - "Rapidoprint" activation processor, available from Agfa (with 8 second activation cycle and 22 second fix/wash cycle). The emulsions were prepared in accordance with the method disclosed in U.S. Patent No. 5,028,521, and were chemically sensitised and spectrally sensitised (to green light) by conventional procedures. Test exposures were of 0.1 seconds on a purpose-built double sided sensitometer equipped with two Wratten No. 99 filters, and sensitometric evaluations were performed with the aid of a modified Macbeth TR924 densitometer. Example 1 (i) Developer Underlayer a) gelatin 12g b) distilled water 190g c) aqueous filter dye solution 40ml d) hydroquinone 4.5g e) phenidone, 4% solution in MeOH 4.5ml f) vinyl sulphone hardener, 1% aqueous solution 20ml Components a) to e) were mixed at 40°C and water added to a total weight of 255g and f) was added prior to coating. (ii) Emulsion Layer a) pure silver bromide emulsion AR = 8 : 1 (as in Example 12 of U.S. Patent No. 5,028,521) 0.4mol b) gelatin 6g c) distilled water 80ml d) resorcinol, 20% aqueous solution 6ml e) azodicarbonamide M/40 in DMF 9ml f) Hostapur®, 10% aqueous solution 16ml g) Dextran® 40, 10% aqueous solution 216ml h) PEA, 10% solids aqueous dispersion 88ml i) vinyl sulphone hardener 1% aqueous solution 80ml Component a), b) and c) were mixed and held for 20 minutes; component d) was added and held for 15 minutes and thereafter component e) to h) were added and held for 30 minutes before adjusting the pH to 6.7 and adding distilled water to give a total weight of 880g. The hardener was added prior to coating. (iii) Topcoat a) gelatin 50g b) distilled water 800g c) Hostapur®, 10% aqueous solution 24ml d) Fluorosurfactant, 1% aqueous solution 24ml e) polymethylmethacrylate, 6.5% solids aqueous dispersion 10ml f) vinyl sulphone hardener 1% aqueous solution 100ml Components a) to e) were mixed, the pH adjusted to 6.7 and water added to bring the weight to 900g and f) was added prior to coating. The three solutions (i), (ii) and (iii) were applied to both sides of transparent polyester base by a multislot coater at 85/65/45 ml/min respectively at 1.5m 2 /min (Sample 1). A further sample was made without the developing agents, hydroquinone and phenidone (Sample 2) present. Sample 1 with a developer underlayer contained a dye that did not bleach, so obscuring Dmin values. The hydroquinone was coated in a hydrophillic colloidal (gelatin) underlayer at a coverage of 0.93 g/m 2 , hence 0.45 moles/mole silver, with phenidone at 0.037 g/m 2 . The samples were exposed and processed as reported in the following Table. Sample Sp-2 Acon Dmax C.W. DN. Processor 1 1.83 2.16 3.71 4.1 74 XP505 90'' 2 1.90 1.94 3.76 4.1 103 XP505 90'' 1 1.62 2.22 3.95 RA® 30'' + 15'' drying 3M 9014 CAD Dryer = 45'' As can be seen the contrast was improved by use of the developer underlayer. The Dmax is excellent i.e. over 3.4. The toughness of the film is also acceptable i.e. over 35 Dornberg units; which is surprising since films prepared with developer incorporated sometimes have difficulty in hardening. Example 2 A tabular grain crystal was used in this Example; which had an aspect ratio of 4.5 : 1, it was digested before the desalting step in an effort to decrease the need for hardener in the coating. The emulsion had a high Dmin. A simple 2 2 factorial design experiment was run on the levels of hydroquinone and phenidone in the developer underlayer. The levels of each in g/m 2 are shown below. plus centre minus Hydroquinone (HQ) 1.23 0.93 0.62 Phenidone (Ph) 0.05 0.037 0.025 Samples were prepared as in Example 1 except that the hardener in the emulsion layer was reduced to 40ml, the difference in weights being corrected with water. The results for the Rapidoprint processing are: Sample HQ Ph Dmin Sp-2 Acon Dmax DN 3 - - 0.25 1.83 2.34 3.42 90 4 + - 0.26 1.93 2.45 3.62 85 5 - + 0.32 1.91 2.31 3.72 93 6 + + 0.32 1.94 2.42 3.85 93 7 0 0 0.27 1.94 2.45 3.76 98 8 0 0 0.29 1.94 2.33 3.76 91 From this set of results it is possible to identify routes to higher speed and lower Dmin. Speed is dependent both on the developer and the electron transfer agent, it will increase by 0.04 units with each 0.3 g/m2 of hydroquinone and by 0.03 with each 0.013 g/m 2 of phenidone. Dmin had very little dependence on hydroquinone but will increase by 0.03 units with each 0.013 g/m 2 increase in phenidone. Note here the quite high speed attained in this set of samples compared to Example 1. Again there is a very good Dmax even with films that are quite tough. Analysis of these Examples would predict that speed could be increased by increasing the coverage of the hydroquinone and Dmin reduced by lowering the amount of phenidone. Example 3 The emulsion used in Example 1 was coated with and without a developer underlayer (Samples 9 and 10) which had a wetting agent added (Hostapur) and would give a coverage of 1.45 g/m 2 of hydroquinone and 0.030 g/m 2 of phenidone. This time after coating the films were not subjected to a calidarium as in the previous Examples. This is a process which heats the film to decrease the time of hardening. Since a rapid hardener was used in the coating a Calidarium is not actually required, the film being quite hard a few days after coating. The results are as follows: Sample Dmin Sp-1 Sp-2 Acon Dmax Process 9 0.22 2.32 2.04 3.73 4.72 XP505 90'' 10 0.19 2.21 1.93 3.48 4.24 XP505 90'' 9 0.22 2.35 2.03 3.16 4.08 RA 45'' In this case the increase in speed predicted by the previous Example was verified even though this is a different emulsion. The Dmin of samples in accordance with the invention is acceptable i.e. less than 0.23. A quite high contrast was attained with samples in accordance with the invention with a high Dmax, over 4.0, which coupled with the rapid access capability would make this type of element suitable for a mammographic application. This result shows the unexpected advantage of having the hydroquinone and phenidone in a discrete underlayer. Example 4 This Example demonstrates different binders for the developer layer. The binders employed were dextran, gelatin and PEA with a total coverage of 6 g/m 2 . The amount of hydroquinone was kept constant at 1.45 g/m 2 and phenidone at 0.020 g/m 2 . The use of the gelatin extenders PEA and dextran allows the coating of relatively thick underlayers with a high HQ content without causing drying problems. The following coating solutions were prepared as follows: Sample 11 12 13 Gelatin 13.9g 12.4g 15.5g water 51ml 45ml 57ml 20% Dextran® 34.8ml 46.4ml 34.8ml 20% PEA 19.3ml 15.5ml 11.6ml 10% Hostapur® 4ml 4ml 4ml 4% (MeOH) Phenidone 2ml 2ml 2ml 4% Hydroquinone 150ml 150ml 150ml pH 6.7 Sample 14 15 16 17 Gelatin 10.8g 10.8g 13.9g 9.3g water 39ml 39ml 51ml 32ml 20% Dextran® 58.0ml 52.2ml 40.6ml 58.0ml 20% PEA 11.6ml 17.4ml 13.5ml 19.3ml 10% Hostapur® 4ml 4ml 4ml 4ml 4% (MeOH)Phenidone 2ml 2ml 2ml 2ml 4% Hydroquinone 150ml 150ml 150ml 150ml pH 6.7 The following emulsion formulation was used: - emulsion (as in Example 1) 311g azodicarbonamide (M/40 in DMF) 9ml Hostapur® (10wt%) 14.4ml Dextran® (20wt% solution) 108ml PEA (20% solids dispersion) 44ml The ingredients were mixed, the pH adjusted to 6.7, and the weight made up to 960g with water. The following topcoat formulation was used: - gelatin 25g water 700ml fluorosurfactant (1% solution) 24ml Hostapur® (10% solution) 24ml polymethylmethacrylate (6.5% solids dispersion) 20ml vinyl sulphone hardener (1% solution) 200ml The first five ingredients were mixed, the pH adjusted to 6.7 and the weight to 800g, and the hardener added prior to coating. (No hardener was added to the developer or emulsion layers). Each developer formulation was coated in turn on both sides of subbed polyester base along with emulsion and topcoat formulations at pump rates of 40, 62 and 100ml/mn respectively at a speed of 1.5sq.m/min. The coated samples were dried and evaluated as before. The results showed the robustness of the sensitometric results to gross changes in binder compositions since all values of Dmin, and speed, were identical within normal experimental error. The samples were compared with a Fuji S-HRG film which is representative of current diagnostic film. Since the sensitometry was the same for all samples used in the method of the invention, only one Example is presented here and compared to S-HRG film. Sample Dmin Sp-1 Sp-2 Sp-3 Acon Dmax C.W. Process 16 0.21 2.39 2.05 1.53 3.28 4.16 3.5 XAD3 110'' S-HRG 0.24 2.38 2.05 1.34 2.89 3.79 3.7 XAD3 110'' 16 0.21 2.32 2.01 1.52 3.22 4.13 XAD3 60'' S-HRG 0.23 2.32 1.98 1.15 2.63 3.80 XAD3 60'' 16 0.21 2.16 1.83 1.14 2.84 3.92 RA 45'' S-HRG No development RA 45'' The sample in accordance with the invention shows Dmin, speed, contrast, Dmax, coating weight and processing latitude advantages over the Fuji film. The sample in accordance with the invention can also be processed in an activator (RA®) processor. The words "Hostapur", "Dextran" and "Rapidoprint", are registered trade marks.

Claims: A medical X-ray film comprising a transparent base coated on at least one side with (a) a tabular grain silver halide emulsion and (b) a separate hydrophillic colloid layer containing a developing agent for silver halide in an amount corresponding to at least 0.5 moles per mole of the silver coated on that side of the base. A medical X-ray film as claimed in Claim 1 in which the layer (b) is between the base and the silver halide emulsion. A medical X-ray film as claimed in Claims 1 or 2 in which the developing agent is a dihydroxybenzene. A medical X-ray film as claimed in Claim 3 in which the developing agent is hydroquinone or catechol. A medical X-ray film as claimed in any preceding Claim in which the developing agent is present in an amount corresponding to at least 0.75 moles per mole of silver coated on that side of the base. A medical X-ray film as claimed in any preceding Claim in which layer (b) additionally comprises an auxiliary developer. A medical X-ray film as claimed in Claim 6 in which the auxiliary developer is phenidone. A medical X-ray film as claimed in any preceding Claim in which the grains of the silver halide emulsion have an aspect ratio in the range 3 : 1 to 12 : 1. A medical X-ray film as claimed in any preceding Claim in which the grains of the silver halide emulsion have a diameter in the range 0.2 to 3.0 µ m and a thickness in the range 0.05 to 0.3 µ m. A medical X-ray film as claimed in preceding Claim having a silver halide emulsion layer (a) and developer layer (b) on each side of the base. A method of forming an image comprising the steps of: 1. providing an X-ray film comprising a transparent base coated on at least one side with (a) a tabular grain silver halide emulsion and (b) separate hydrophillic colloid layer containing a developing agent for silver halide in an amount corresponding to at least 0.5 mole per mole of silver coated on that side of the base. 2. positioning a light-emitting phosphor screen in intimate contact with each emulsion-coated side of the film, 3. imagewise exposing the phosphor screen to X-rays, and 4. contacting the exposed film with an aqueous alkaline activator solution to develop an image. A method of forming an image as claimed in Claim 11 in which the activator solution has a pH of at least 9 and comprises one or more of KOH, NaOH, NH 4 OH, K 2 CO 3 and Na 2 CO 3 . A method of forming an image as claimed in Claim 11 or Claim 12 in which the activator solution additionally comprises a preservative and/or restrainer and/or an auxiliary developer. A method of forming an image as claimed in Claim 13 in which the activator solution comprises sodium sulphite and/or sodium bromide and/or phenidone. A method of forming an image as claimed in any one of Claims 11 to 14 in which the X-ray film is as defined in any one of Claims 2 to 10.

Inventors: SLATER SEAN D, WALLIS JULIAN M, SLATER, SEAN D., WALLIS, JULIAN M.
Applicants: EASTMAN KODAK CO, EASTMAN KODAK COMPANY
Application year: 1994
Main classification: G03C5
IPC codes: G03C5, G03C1