Coated golf ball

Abstract: The present invention provides a coated golf ball having beautiful appearance, wherein whiteness is enhanced by inhibiting enhancement of blueness. The golf ball body of the coated golf ball is coated with a white paint containing titanium oxide as a main pigment. The white paint comprises 45 to 60% by weight of titanium oxide, 0.005 to 0.20% by weight of a blue pigment and 0.001 to 0.06% by weight of a red pigment, based on 100% by weight of a solid content of a coating. The weight ratio of the blue pigment to the red pigment is 0.9 to 5.

Description: The present invention relates to a coated golf ball in which the golf ball body is coated with a paint. More particularly, it relates to a coated golf ball wherein whitening of the color tone of the golf ball is enhanced and weathering properties are improved. Since a golf ball is used on green grass in sunlight, it is necessary to enhance the whiteness in order to provide a good appearance. The golf ball body is generally coated only with a clear paint, or coated with an enamel paint containing a white pigment and clear paint. In order to enhance the whiteness thereof, the amount of titanium oxide as a white pigment can be increased. However, the amount of titanium oxide which can be formulated in the paint is limited. In order to improve the whiteness of golf balls, Japanese Patent Publication No. 4-50029 suggests to formulate a suitable amount of blue and violet pigments in a white paint containing titanium oxide as a main pigment. However, the blueness is also enhanced in addition to whiteness, which results in a blackish color. We have now developed a coated golf ball having a good appearance, wherein the whiteness is enhanced by inhibiting the enhancement of the blueness of the paint. Accordingly, the present invention provides a coated golf ball in which a golf ball body is coated with a white paint containing titanium oxide as the main pigment thereof, the white paint comprising 45 to 60% by weight of titanium oxide, 0.005 to 0.20% by weight of a blue pigment and 0.001 to 0.06% by weight of a red pigment based on the solids content of the paint and the weight ratio of the blue pigment to the red pigment is 0.9 to 5. The white paint used in the present invention may be an epoxy, acrylic or urethane paint. A urethane paint is particularly preferred. For example, a white paint prepared by reacting an active hydrogen-containing compound (e.g. a polyester polyol, polyether polyol, etc.) as a main material with an isocyanate compound as a curing agent is preferred. As the isocyanate compound, a 1,6-hexamethylene diisocyanate modified material (e.g. biulet material, trimethylolpropane modification, trimer, etc.) is preferred. A tolylene diisocyanate modified material is also preferred. The white paint contains titanium oxide as a white pigment. The amount is suitably 45 to 60% by weight based on the solids content of the coating. When the amount of white pigment is below 40% by weight, the coating hiding power becomes inferior and, therefore, the preferred white color cannot be obtained. When the amount exceeds 60% by weight, the physical properties of the coating become inferior, and it is not preferred. The amount is preferably 45 to 55% by weight, particularly preferred is an amount of 50 to 55% by weight. In addition to the above components, various additives, curing catalysts and diluents are formulated in the white paint. Examples of the additive include ultraviolet inhibitors, fluid agents, sealing pigments, fluorescent agent and fluorescent brighteners. The amount of these additives is 0.1 to 10% by weight based on the solid content of the coat. As the fluorescent agent or fluorescent brightener contained in the white paint, for example, there are those which are normally known and are used for the golf ball. Examples thereof include 2,5-bis[5'-t-butylbenzoxazolyl (2)]thiophene (commercially available from Japan Ciba Geigy Co., Ltd. as Yubitex OB), 7-(2h-naphthol(1,2-d)-triazol-2-Y1)-3-phenyl-cusline (commercially available from Sanzos Co. as Leucopure EGM), biazoline derivative (commercially available from Mobey Chemical Corporation as Phorwhite K-2002), oxazoles (commercially available from Sumitomo Chemical Co., Ltd as Whitefullar HCS, PCS, B) and fluorescent brightener (commercially available from Hoechst Japan Co. as Hostalux KCB). The amount thereof is 0.005 to 1.0% by weight based on the solid content of the coating. Examples of the diluent formulated in the white paint include ketones such as acetone and methyl ethyl ketones aromatic hydrocarbons such as toluene and xylene; esters such as ethyl acetate. The amount of the diluent is not specifically limited, but is 30 to 80% by weight. As the blue pigment, for example, phthalocyanine blue, ultramarine blue or indanthron blue, or a mixture thereof can be suitably used. The amount of the blue pigment is 0.005 to 0.20% by weight, preferably 0.01 to 0.08% by weight, based on the solid content of the coat. As the red pigment, for example, quinacridone magenta or permanent red, or a mixture thereof can be suitably used. The amount of the red pigment is 0.001 to 0.06% by weight, preferably 0.008 to 0.04% by weight, based on the solid content of the coat. Such a paint is applied on the golf ball body in a thickness of 5 to 30 µm. The golf ball body may be an one-piece golf ball obtained by vulcanizing and molding a cis-1,4-polybutadiene rubber. Further, the golf ball body may also be a thread wound golf ball comprising a thread wound core and a cover layer mainly composed of transpolyisoprene provided thereon. By coating the above paint on the golf ball body, a coated golf ball of which color tone shows a Tw value of not more than 10, an a value of 0.01 to 0.6 and a Tw/Wcie value of 0.005 to 0.05 can be obtained. When these values are not within the above range, the resulting coated golf ball lacks in whiteness. Preferably, the a value is 0.1 to 0.5 and the Tw/Wcie value is 0.02 to 0.04. These Tw a and Tw/ Wcie values are measured by a colorimeter (available from Minolta Co., Osaka, Japan). In the production of the coated golf ball of the present invention, the clear paint may be applied after the white paint is applied on the golf ball body. The clear paint is one which essentially contains no pigment, and there can be used an epoxy, acrylic or urethane paint. The clear paint is known as to the production of the golf ball. According to the present invention, a coated golf ball having beautiful appearance, wherein whiteness is enhanced by inhibiting enhancement of blueness can be obtained. EXAMPLES The following Examples and Comparative Examples further illustrate the present invention in detail. Examples 1 to 5 and Comparative Examples 1 to 3 Paints A to E (Examples) and paints F to H (Comparative Examples) were prepared by mixing the components shown in Table 1 according to a conventional method. On the golf ball obtained by a conventional method, the above white paint was coated. Thereafter, the color tone was measured by a colorimeter and further visually observed. The kind of the paint used and test results are shown in Table 2, below. Test method (1) Measurement of color tone Colorimeter CR221 manufactured by Minolta Co. (visual field of 2°, 3 mm, light source D 65 ), according to Y x y measurementFormulas of whiteness (Wcie), blueness (Tw) and redness (a) of CIE•ISO are as follows: Wcie = Y + 800 (X 0 - X) + 1700 (Y 0 - Y) Tw = 1000 (X 0 - X) - 650 (Y 0 -Y) a (JIS Z8730) = 500 (X/X 0 ) 1/3 - (Y/Y 0 ) 1/3 wherein X 0 and Y 0 are respectively chromaticity coordinate of perfect diffuser of D 65 lighting, X 0 is 0.3127 and Y 0 is 0.3291. (2) Visual observation (feature of appearance) Whiteness was evaluated by 200 random panelists according to the following criteria: 4: considerably white 3: white 2: white but contains some other color 1: yellowish white

Claims: A coated golf ball in which a golf ball body is coated with a white paint containing titanium oxide as the main pigment thereof, the white paint comprising 45 to 60% by weight of titanium oxide, 0.005 to 0.20% by weight of a blue pigment and 0.001 to 0.06% by weight of a red pigment based on the solids content of the paint and the weight ratio of the blue pigment to the red pigment is 0.9 to 5. A coated golf ball as claimed in claim 1, wherein the color tone of the coated golf ball has a Tw value of not more than 10, an a value of 0.01 to 0.61 and a Tw/Wcie value of 0.005 to 0.05. A coated golf ball as claimed in claim 1 or claim 2, wherein the golf ball body is a one-piece golf ball made from a cis-1,4-polybutadiene rubber. A coated golf ball as claimed in claim 1 or claim 2, wherein the golf ball body is a thread wound golf ball comprising a thread wound core and a cover layer provided thereon, the cover layer being composed of transpolyisoprene as the main component thereof. A coated golf ball as claimed in any one of the preceding claims wherein the white paint comprises from 45 to 55% by weight of titanium dioxide. A coated golf ball as claimed in claim 5, wherein the white paint comprises from 50 to 55% by weight of titanium dioxide. A coated golf ball as claimed in any one of the preceding claims wherein the white paint comprises from 0.01 to 0.08% by weight of the blue pigment. A coated golf ball as claimed in any one of the preceding claims wherein the white paint comprises from 0.008 to 0.04% by weight of the red pigment. A coated golf ball as claimed in any one of the preceding claims wherein the color tone has an a value of 0.1 to 0.5. A coated golf ball as claimed in any one of the preceding claims wherein the Tw/Wcie value is 0.02 to 0.04.

Inventors: HORIUCHI KUNIYASU, MARUOKA KIYOTO, HORIUCHI, KUNIYASU, MARUOKA, KIYOTO
Applicants: SUMITOMO RUBBER IND, SUMITOMO RUBBER INDUSTRIES, LTD.
Application year: 1994
Main classification: C09D7
IPC codes: A63B37, C09D7