Catalytic preparation of beta-cyanoalkylsilane

Abstract: This invention provides a process for the catalytic addition of silicon hydrides to α,β-unsaturated olefinic nitriles to form β-cyanoalkylsilanes. The process is conducted at a temperature within a range of 50°C. to 250°C. Our process utilizes as a catalyst one of the following: 1) tertiary and quaternary amino ion exchange resins; 2) tetraalkylammonium halides supported on silica gel; 3) divinylbenzene/4-vinylpyridine copolymer based resins; 4) triorganophosphine oxide supported on an organic resin or 5) triorganophosphine compounds.

Description: The present invention is a process for the preparation of hydrolyzable beta-cyanoalkylsilanes by the catalytic addition of silicon hydrides to α,β-unsaturated olefinic nitriles to form β-cyanoalkylsilanes. This invention employs in the above process one of the following catalysts: 1) tertiary and quaternary amino ion exchange resins; 2) tetraalkylammonium halides supported on silica gel; 3) divinylbenzene/4-vinylpyridine copolymer based resins; 4) triorganophosphine oxide supported on an organic resin; or 5) triorganophosphine compounds. The prior art is represented by one or more of the following patents: US-A-2,906,764; US-A-2,906,765; US-A-2,907,784; US-A-2,908,699; US-A-2,971,970; US-A-2,971,972; US-A-3,257,440; US-A-5,126,468; US-A-5,126,469; US-A-5,247,110; US-A-3 153 662; US-A-3 099 670; US-A-3 448 135 and DE-A-1 087 603. The prior art in the literature is represented by Pike et al., J. Org. Chem. 24, 1939-42, 1959; Pike et al., J. Org. Chem. 27, 2190-92, 1962; Rajkumar et al., Organometallics 8, 549-550, 1989; Belyakova et al., Zhurnal. Obshchei. Khimii 35:1183-1186, 1965; Ojimia et al., J. Organomet. Chem. 111:43-60 (1976) and Capka et al., J. Mol. Catalysis 11:313-330 (1981). This invention provides a process for the catalytic addition of silicon hydrides to α,β-unsaturated olefinic nitriles to form β-cyanoalkylsilanes. The process is conducted at a temperature within a range of 50°C. to 250°C. Our process utilizes as a catalyst one of the following: 1) tertiary and quaternary amino ion exchange resins; 2) tetraalkylammonium halides supported on silica gel; 3) divinylbenzene/4-vinylpyridine copolymer based resins; 4) triorganophosphine oxide supported on an organic resin or 5) triorganophosphine compounds. The present invention is a process for preparation of beta-cyanoalkylsilanes described by formula: The process comprises contacting a silicon hydride described by formula HSiX 3 (2) with an unsaturated olefinic nitrile described by formula in the presence of a catalyst selected from a group consisting of tertiary amino ion exchange resins; quaternary amino ion exchange resins; divinylbenzene/4-vinylpyridine copolymer based resins; triorganophosphine supported on an organic resin; triorganophosphine oxide supported on an organic resin; triorganophosphine oxide and tetraalkylammonium halide described by formula R 4 NX (4) supported on silica gel, where each R is an independently selected alkyl comprising 1 to 20 carbon atoms, at a temperature within a range of 50°C. to 250°C.; where X is a halogen and each Y is independently selected from hydrogen and lower alkyl radicals comprising one to eight carbon atoms. The described process is applicable to the production of beta-cyanoalkylsilanes containing one silicon-bonded beta-cyanoalkyl radical, as described by Formula 1. Beta-cyanoalkylsilanes that can be made by the present process are beta-cyanoethyltrichlorosilane, beta-cyanopropyltrichlorosilane, beta-cyanobutyltrichlorosilane, beta-cyano-tert-butyltrichlorosilane, beta-cyanopentyltrichlorosilane, beta-cyanohexyltrichlorosilane, beta-cyanoheptyltrichlorosilane, beta-cyanooctyltrichlorosilane, alpha-methyl-beta-cyanoethyltrichlorosilane, alpha-ethyl-beta-cyanoethyltrichlorosilane, alpha-octyl-beta-cyanopropyltrichlorosilane, beta-cyanoethyltribromosilane and beta-cyanopropyltrifluorosilane. The preferred beta-cyanoalkylsilane made by the present process is beta-cyanoethyltrichlorosilane. The silicon hydride, described by Formula 2, contains one silicon-bonded hydrogen atom and three silicon-bonded halogen atoms. The halogen atom, X, is selected from bromine, chlorine, fluorine and iodine. The preferred halogen is chlorine. The silicon hydride is contacted with an α,β-unsaturated olefinic nitrile described by Formula 3. The α,β-unsaturated olefinic nitrile contains substituents Y which are independently selected from hydrogen and lower alkyl radicals comprising from one to eight carbon atoms. For example, Y is methyl, ethyl, propyl, butyl, tert-butyl, pentyl, hexyl, heptyl and octyl. Examples of the α,β-unsaturated olefinic nitrile include acrylonitrile, methacrylonitrile, crotononitrile, ethylacrylonitrile, 1-cyanobutene-1 and 2-cyanooctene-1. The preferred α,β-unsaturated olefinic nitrile is acrylonitrile. The molar ratio of the silicon hydride to the α,β-unsaturated olefinic nitrile may be varied within wide limits, however no particular advantage is derived from employing a molar excess of either reactant. The use of molar excesses of either of the two reactants is not precluded. It is preferred that the molar ratio of silicon hydride to α,β-unsaturated olefinic nitrile be within a range of 0.5 to 1.5. In the most preferred embodiment of the invention, the molar ratio of silicon hydride to α,β-unsaturated olefinic nitrile is near 1.0. The silicon hydride and α,β-unsaturated olefinic nitrile can be contacted in the presence of tetraalkylammonium halide, as described by formula (4), supported on silica gel as catalyst. In formula (4), each R is an independently selected alkyl comprising one to 20 carbon atoms. Preferred is when each R is an independently selected alkyl comprising one to ten carbon atoms. The substituent R is methyl, ethyl, propyl, butyl and decyl. Substituent X is a halogen selected from bromine, chlorine, fluorine and iodine. Preferred is when X is fluorine. The method of support of tetraalkylammonium halide on the silica gel is not critical and standard methods known in the art are applicable such as adsorption or absorption. The silica gel is typically in the form of powders or beads. Preferred is when the silica gel is from 0.29 mm to 1.0 mm (18 to 50 mesh) in size. More preferred is when sufficient tetraalkylammonium halide is supported on the silica gel to provide approximately 1.1 mmol of halogen per gram of silica gel. A preferred catalyst for our process of this type is tetrabutylammonium fluoride supported on silica gel. Alternatively, the silicon hydride and α,β-unsaturated olefinic nitrile are contacted in the presence of a catalyst selected from a group consisting of tertiary amino ion exchange resins; quaternary amino ion exchange resins and divinylbenzene/4-vinylpyridine copolymer based resins. General methods for making such catalysts are discussed in US-A 4,113,845. The tertiary and quaternary amino ion exchange resins useful in the present invention are polymeric materials which are insoluble in trichlorosilane, the α,β-unsaturated olefinic nitriles and the products of the present process. Such insolubility can be achieved, in the case of linear, thermoplastic ion exchange resins by using resin of sufficiently high molecular weight, i.e. greater than 10,000, such that the polymers possess the requisite insolubility. Insolubility can be achieved by employing a cross-linked ion exchange resin, which may be infusible as well. However for purposes of this invention the degree of cross-linking need only be sufficient to meet the requisite insolubility requirements. The amino functionality in the resin is a tertiary amino or quaternary amino group attached through carbon to the resin structure. Except for the nitrogen atoms or the halide ions of the amino functionality all of the resin is composed of carbon and hydrogen. The ion exchange resins used in the present invention are those made from the copolymerization of monoolefinically unsaturated hydrocarbons and a polyolefinically unsaturated hydrocarbons. The monoolefinically unsaturated compounds are typically styrene, 4-chlorostyrene, 3-chlorostyrene, vinyltoluene and 4-chloromethylstyrene. The polyolefinically unsaturated compounds may be, for example, 1,4-divinylbenzene, divinyltoluenes and trivinylbenzene. Such copolymers are well known and a number of them are commercial products which possess tertiary amino or quaternary amino functionality. They may be converted into cross-linked resins with conventional free radical addition catalysts such as peroxides. The chloro groups of the copolymer can be replaced by a condensation reaction with a secondary or tertiary alkylamine, arylamine or alkylarylamine; where each alkyl comprises one to 20 carbon atoms and each aryl comprises six to twelve carbon atoms. The tertiary amino ion exchange resin is formed by reacting the chloro groups of the copolymer with a secondary amine. The quaternary amino ion exchange resin is formed by reacting the chloro groups of the copolymer with a tertiary amine. Quaternization of the tertiary amine containing resin can be effected, for example, by reaction with a hydrocarbon halide such as an alkyl halide or aryl halide, to form the corresponding quaternary amine halide. It is preferred that the amino ion exchange resin be of the macroreticular type described in Kirk-Othmer, Encyclopedia of Chemical Technology, Vol. 13, p. 689, 1981, John Wiley and Sons, Inc. A preferred amino ion exchange resin for use in the present process is a cross-linked styrene/divinylbenzene copolymer resin having tertiary amino ion functionality or quaternary amino functionality. More preferred is when the tertiary amino ion functionality is dimethylamino and the quaternary amino functionality is trimethylamino chloride. Examples of amino ion exchange resins useful in the present invention are typified by Amberlyst™ A-21, A-26, A-27 and A-29, Rohm and Haas Company, Philadelphia, Pa. Divinylbenzene/4-vinylpyridine catalysts are also available commercially as Reillex™ 402 and Reillex™ 425, Reilly Industries Inc., Indianapolis, IN. These catalysts may be employed in our process as beads or as powders. Generally, the smaller the size of the catalyst the greater the surface area and consequently the greater the activity of the catalyst. Examples of catalyst particle sizes useful in this invention are provided in the examples herein. The catalyst can be a macroreticulated resin formed from a divinylbenzene/4-vinylpyridine copolymer. Finally, the silicon hydride and α,β-unsaturated olefinic nitrile can be contacted in the presence of a catalyst selected from organic resin supported triorganophosphine, organic resin supported triorganophosphine oxide and triorganophosphine oxide. The organic resin support for this catalyst system can be any cross-linked hydrocarbon resin having carbon atoms capable of covalent bonding to phosphorous. For example, the support can be cross-linked resins made from copolymerized monoolefinically unsaturated hydrocarbons and polyolefinically unsaturated hydrocarbons as described for tertiary and quanternary amino ion exchange resins. A preferred organic resin support for triorganophosphine compounds is cross-linked styrene/divinylbenzene copolymer resin. Supported triorganophosphines useful in our process are described by formula Y-R 1 -PR 2 2 and supported triorganophosphine oxides which are useful in our process are described by formula Y-R 1 -PR 2 2 O, where Y is a carbon atom of the organic resin, R 1 is a divalent hydrocarbon radical comprising one to 10 carbon atoms and each R 2 is independently selected from monovalent hydrocarbon radicals comprising one to 10 carbon atoms. The divalent hydrocarbon radical R 1 is an alkylene of one to 10 carbon atoms or an arylene. Preferred is when R 1 is phenylene. The triorganophosphine or triorganophosphine oxide is covalently bonded to the support material through a divalent hydrocarbon radical. For example, R 1 can be the phenyl substituent of the styrene component of a styrene/divinylbenzene copolymer. The substituent R 2 is methyl, ethyl, butyl, tert-butyl and phenyl. A preferred supported catalyst in the present invention is a supported triorganophosphine where the organic resin support is a styrene/divinylbenzene copolymer resin, R 1 is a phenyl substituent of the styrene component of the copolymer resin and each R 2 is phenyl. The catalyst can also be an unsupported triorganophosphine oxide as described by formula PR 2 3 O, where R 2 is as previously described. A preferred unsupported triorganophosphine oxide catalyst is triphenylphosphine oxide. The amount of catalyst employed in the present process in relation to the amount of α,β-unsaturated olefinic nitrile may be varied within wide limits. It is dependent upon such conditions as the temperature at which the process is run, the structure of the reactants, the specific catalyst, the surface area of the catalyst and whether the process is run as a batch or continuous process. In general, the process can be run under conditions where the catalyst is present at 0.1 to 50 weight percent of a mixture comprising the catalyst, the α,β-unsaturated olefinic nitrile and the silicon hydride. Preferred is when the catalyst comprises 0.5 to 30 weight percent of the mixture. For the tetraalkylammonium halide catalyst, the amounts given are expressed as the combined weight of silica gel and tetraalkylammonium halide. The silicon hydride, the α,β-unsaturated olefinic nitrile and the catalyst are contacted in a suitable reactor of standard design. The type of reactor is not critical. The process can be run as a batch process, a semi-batch process or a continuous process. A preferred process is where the reaction is conducted as a continuous process in a packed-bed reactor. The temperature for conducting the process can be within a range of 50°C. to 250°C. It is preferred that the temperature be within a range greater than 80°C. to 200°C. Generally, higher temperatures allow the use of a lower catalyst concentration. The pressure under which the process is conducted is not critical. Generally, the process can be run at a gauge pressure within a range of 0 to 6.9 MPa (0 psig to 1000 psig). Preferred is a gauge pressure within a range of 0 to 0.69 MPa (0 psig to 100 psig). The time required for conducting the process may vary depending on the particular silicon hydride, α,β-unsaturated olefinic nitrile, temperature and catalyst concentration employed. In general, reaction times of 0.1 to 30.0 hours are useful. A preferred reaction time is 0.5 to 20.0 hours. The following examples are given to illustrate the present invention. Example 1 The ability of tetrabutylammonium fluoride supported on silica gel to catalyze the addition of trichlorosilane to acrylonitrile to form β-cyanoethyltrichlorosilane was evaluated. The evaluation was conducted in a sealed glass tube purged with argon. About 0.026 g catalyst was placed in the tube and 2 mL of a mixture of 0.0122 mole of trichlorosilane and 0.0116 mole of acrylonitrile was added to the tube. The tube was sealed and heated for 2 hours at 150°C. The catalyst tested consisted of tetrabutylammonium fluoride supported on silica gel, Aldrich Chemical Company, Milwaukee, WI, stated to have 1.1 mmol fluorine per gram of silica gel. A similar comparison run was made using 0.083 g of a material consisting of tetrabutylammonium fluoride supported on alumina, Aldrich Chemical Company. This material was not catalytic in the process. The results of these runs are presented in Table 1. The contents of individual tubes were analyzed by gas liquid chromatography (GLC) using a thermal conductivity detector (TCD). The results are expressed as the area percent (Area %) under the GLC-TCD trace for β-cyanoethyltrichlorosilane, as a percentage of the total area under the GLC-TCD trace. Reaction of Trichlorosilane with Acrylonitrile in Presence of Supported Tetrabutylammonium Fluoride Run No. Support Material Area % β-Cyanoethyltrichlorosilane 1 silica gel 79.3 2 alumina 0.0 Example 2 The ability of a styrene/divinylbenzene copolymer based resin containing tertiary amino functionality to catalyze the addition of trichlorosilane to acrylonitrile to form β-cyanoethyltrichlorosilane was evaluated in a series of runs. The runs were conducted in sealed glass tubes purged with argon. The runs were conducted by placing the weight of dry catalyst given in Table 2 into a tube, then adding to each tube 2 mL of a mixture of 0.0124 mole of trichlorosilane and 0.0113 mole of acrylonitrile. The tubes were sealed and then heated for 2 hours at either 120°C. or 170°C. The catalyst tested consisted of Amberlyst™ A-21, Rohm and Haas Company, Philadelphia, Pa. Amberlyst™ A-21 is described as a styrene/divinylbenzene copolymer based resin having dimethyl tertiary amino functionality and an effective size of 0.40 mm to 0.55 mm. The results of these runs are presented in Table 2. The contents of individual tubes were analyzed by GLC using TCD. The results are expressed as the Area % under the GLC-TCD trace for beta-cyanoethyltrichlorosilane, as a percentage of the total area under the GLC-TCD trace. Amberlyst™ A-21 Catalyzed Reaction of Trichlorosilane with Acrylonitrile Run No. Catalyst Weight(g) Temperature °C. Area % β-Cyanoethyltrichlorosilane 1 0.0142 120 2.0 2 0.0184 170 80.0 Example 3 The ability of a styrene/divinylbenzene copolymer based resin containing quaternary amino functionality to catalyze the addition of trichlorosilane to acrylonitrile to form β-cyanoethyltrichlorosilane was evaluated in a series of runs. The runs were conducted in sealed glass tubes purged with argon. The runs were conducted by placing the weight of dry catalyst given in Table 3 into a tube, then adding to each tube 2 mL of a mixture of 0.0124 mole of trichlorosilane and 0.0113 mole of acrylonitrile. The tubes were sealed and heated for 2 hours at either 120°C. or 170°C. The catalyst tested consisted of Amberlyst™ A-27, Rohm and Haas Company, Philadelphia, Pa. Amberlyst™ A-27 is described as a styrene/divinylbenzene copolymer based resin having trimethyl tertiary amino functionality, with chloride as the cation and an effective size of 0.40 mm to 0.50 mm. The results of these runs are presented in Table 3. The contents of individual tubes were analyzed by GLC-TCD. The results are expressed as Area % under the GLC-TCD trace for beta-cyanoethyltrichlorosilane, as a percentage of the total area under the GLC-TCD trace. Amberlyst™ A-27 Catalyzed Reaction of Trichlorosilane with Acrylonitrile Run No. Catalyst Weight (g) Temperature °C. Area % β-Cyanoethyltrichlorosilane 1 0.0316 120 7.1 2 0.0366 170 75.7 Example 4 The ability of a divinylbenzene/4-vinylpyridine copolymer based resin to catalyze the addition of trichlorosilane to acrylonitrile to form β-cyanoethyltrichlorosilane was evaluated in a series of runs. The runs were conducted in sealed glass tubes purged with argon. The runs were conducted by placing the weight and type of catalyst given in Table 4 into a tube, then adding to each tube 2 mL of a mixture of 0.0122 mole of trichlorosilane and 0.0116 mole of acrylonitrile. The tubes were sealed then heated for two hours at 150°C. The catalyst tested consisted of Reillex™ 425 (Reilly Industries Inc., Indianapolis, IN) and Reillex™ 402. Reillex™ 425 is divinylbenzene/4-vinylpyridine copolymer resin beads of size 0.29 mm to 1.0 mm (18-50 mesh). Reillex™ 402 is divinylbenzene/4-vinylpyridine copolymer resin powder of approximately 0.25 mm (60 mesh). The catalyst used in run number 4 was reused for run number 5. The results of these runs are presented in Table 4. The contents of individual tubes were analyzed by GLC using TCD. The results are expressed as Area % under the GLC-TCD trace for β-cyanoethyl-trichlorosilane, as a percentage of the total area under the GLC-TCD trace. Divinylbenzene/4-Vinylpyridine Copolymer Based Resin Catalyzed Reaction of Trichlorosilane With Acrylonitrile Run No. Catalyst Type Catalyst Wt. (g) Area % β-Cyanoethyltrichlorosilane 1 Reillex 425 0.326 67.0 2 Reillex 425 0.034 21.3 3 Reillex 425 0.011 5.5 4 Reillex 425 0.304 66.2 5 Reillex 425 *.* 63.9 6 Reillex 402 0.011 28.5 Example 5 The ability of triphenylphosphine supported on a styrene/divinylbenzene copolymer based resin to catalyze the addition of trichlorosilane to acrylonitrile to form β-cyanoethyltrichlorosilane was evaluated in a series of runs. The runs were conducted in sealed glass tubes purged with argon. The runs were conducted by placing a weight of catalyst as described in Table 5 into a tube, then adding to each tube 2 mL of a mixture of 5 mole percent excess trichlorosilane and acrylonitrile. The tubes were sealed then heated for 2 hours at 150°C. Unsupported triphenylphosphine was tested for comparison purposes. The test catalyst comprised triphenylphosphine supported on a cross-linked styrene/divinylbenzene copolymer resin. The supported catalyst was purchased from Alfa, Ward Hill, MA. The supported catalyst is reported to comprise 3-7 percent phosphorous and have the formula {CH(C 6 H 4 P(C 6 H 5 ) 2 )CH 2 } x . The results of these runs are presented in Table 5. The contents of individual tubes were analyzed by GLC using TCD. The results are expressed as Area % under the GLC-TCD trace for beta-cyanoethyltrichlorosilane, as a percentage of the total area under the GLC-TCD trace. Triorganophosphine Catalyzed Reaction of Trichlorosilane with Acrylonitrile Catalyst Catalyst Weight(g) Area % β-Cyanoethyltrichlorosilane Ph 3 P 0.029 68.4 Supported Ph 3 P 0.590 66.2 Example 6 The ability of unsupported triphenylphosphine oxide to catalyze the addition of trichlorosilane to acrylonitrile to form β-cyanoethyltrichlorosilane was evaluated. The evaluation was conducted by placing 0.037 g of triphenylphosphine oxide into a tube, then adding to the tube 2 mL of a mixture of 5 mole percent excess trichlorosilane and acrylonitrile. The tube was sealed and heated for two hours at 150°C. The composition of the tube content was analyzed as described in Example 5. The content of the tube was found to comprise 78.4 Area % β-cyanoethyltrichlorosilane.

Claims: A process for preparation of beta-cyanoalkylsilanes described by formula the process comprising contacting a silicon hydride described by formula HSiX 3 , with an unsaturated olefinic nitrile described by formula in the presence of a catalyst selected from a group consisting of tertiary amino ion exchange resins; quaternary amino ion exchange resins; divinylbenzene/4-vinylpyridine copolymer based resins; triorganophosphine supported on an organic resin; triorganophosphine oxide supported on an organic resin; triorganophosphine oxide and tetraalkylammonium halide described by formula R 4 NX supported on silica gel, where each R is an independently selected alkyl comprising 1 to 20 carbon atoms, at a temperature within a range of 50°C. to 250°C.; where X is a halogen and each Y is independently selected from hydrogen atom and lower alkyl radicals comprising one to eight carbon atoms. A process according to claim 1 where the unsaturated olefinic nitrile is selected from acrylonitrile, methacrylonitrile, crotononitrile, ethylacrylonitrile, 1-cyanobutene-1 and 2-cyanooctene-1. A process according to claim 1 where the prepared beta-cyanoalkylsilane is beta-cyanoethyltrichlorosilane. A process according to claim 1 where the silicon hydride is trichlorosilane, the olefinic nitrile is acrylonitrile and the temperature is within a range of 80°C. 200°C. A process according to claim 1 where the mole ratio of silicon hydride to unsaturated olefinic nitrile is within the range of 0.5 to 1.5. A process according to claim 1 where the process is conducted for a time period of 0.1 to 30 hours. A process according to claim 1 where the catalyst is a cross-linked styrene/divinylbenzene copolymer resin having tertiary amino functionality formed by attachment of a dialkylamino group through a carbon atom to the resin. A process according to claim 1 where the catalyst is a cross-linked styrene/divinylbenzene copolymer resin having a quaternary amino functionality formed by attachment of a trialkylamino group through carbon to the resin. A process according to claims 7 or 8 where the trialkylamino group is trimethylamino. A process according to claims 7 or 8 where the resin is of the macroreticular type. A process according to claim 1 where the silica gel has supported on it sufficient tetraalkylammonium halide to provide about 1.1 mmol of halogen per gram of silica gel and the particle size of the silica gel is from 0.29 to 1.0 mm (18 to 50 mesh). A process according to claim 1 where the catalyst is present at 0.1 to 50 weight percent of a mixture comprising the catalyst, the α,β-unsaturated olefinic nitrile and the silicon hydride. A process according to claim 1 where the process is conducted as a continuous process in a packed-bed reactor. A process according to claim 1 where the catalyst is an organic resin supported triorganophosphine described by formula Y-R 1 -PR 2 2 , Y is a carbon atom of the organic resin, R 1 is a divalent hydrocarbon radical comprising one to 10 carbon atoms and each R 2 is independently selected from monovalent hydrocarbon radicals comprising one to 10 carbon atoms. A process according to claim 14 where the organic resin is a cross-linked styrene/divinylbenzene copolymer, R 1 is a phenyl substituent of the styrene component of the copolymer and each R 2 is phenyl. A process according to claim 14 where the catalyst is an organic resin supported triorganophosphine oxide. A process according to claim 1 where the catalyst is triphenylphosphine oxide.

Inventors: BANK HOWARD MARVIN, BANK, HOWARD MARVIN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1994
Main classification: C07F7
IPC codes: C07F7, B01J31, C07B61