Synthesis of alkyl t-alkyl ether using alkylsulfonic acid-modified oxide catalysts

Abstract: A process for the preparation of alkyl tertiary-alkyl ether from tertiary alkyl alcohol and primary alcohol in the presence of a catalyst, characterized in that the catalyst is a heterogenous catalyst comprising an alkylsulfonic acid covalently bonded to an oxide of Group III or Group IV of the Periodic Table. The process is suited to the production of methyl tert-butyl ether. The oxide is preferably silica gel, the acid preferably propylsulfonic acid.

Description: This invention relates to the synthesis of alkyl t-alkyl ether using alkylsulfonic acid-modified oxide catalysts. In particular, this invention concerns an improved process for preparing methyl tertiary butyl ether (MTBE) by the reaction of tertiary butanol and methanol in the presence of a catalyst comprising an alkylsulfonic acid-modified oxide. MTBE has been generated in up to 40 percent concentration in the crude product effluent and product phase separation is in evidence at temperatures of 160°C or greater. It is known to those skilled in the art that ethers, including unsymmetrical ethers, may be prepared by reacting an alcohol with another alcohol to form the desired product. The reaction mixture, containing catalyst and/or condensing agent may be separated and further treated to permit attainment of the desired product. Such further treatment commonly includes one or more distillation operations. Alkyl tertiary-alkyl ethers, particularly methyl tert-butyl ether, are finding increasing use as a blending component in high octane gasoline as the current gasoline additives based on lead and manganese are phased out. Currently all commercial processes for the manufacture of methyl tert-butyl ether are based upon the liquid-phase reaction of isobutylene and methanol (Eq. 1), catalyzed by a cationic ionexchange resin with an organic polymer backbone (see, for example: Hydrocarbon Processing, Oct. 1984, p. 63; Oil and Gas J., Jan. 1, 1979, p. 76; Chem. Economics Handbook-SRI, Sept. 1986, p. 543-7051P). The cationic ion-exchange resins used in MTBE synthesis normally have the sulfonic acid functionality and a cross-linked styrene-divinylbenzene polymer backbone (see: J. Tejero, J. Mol. Catal., 42 (1987) 257; C. Subramamam et al., Can. J. Chem. Eng., 65 (1987) 613). With the expanding use of MTBE as an acceptable gasoline additive, a growing problem is the availability of raw materials. Historically, the critical raw material is isobutylene (Oil and Gas J., June 8, 1987, p. 55). It would be advantageous, therefore, to have a process to make MTBE that does not require isobutylene as a building block. It would be advantageous to have an efficient process for making MTBE by reaction of methanol with tertiary butyl alcohol, since t-butanol (tBA) is readily available commercially through isobutane oxidation. In U.S. Patent No. 4,822,921, to Texaco Chemical Co., there is described a method for preparing alkyl tertiary alkyl ethers which comprises reacting a C 1 -C 6 primary alcohol with a C 4 -C 10 tertiary alcohol over a catalyst comprising an inert support impregnated with phosphoric acid. U.S. Patent No. 4,827,048, to Texaco Chemical Co., describes a method for preparing alkyl tertiary alkyl ethers from the same reactants using a heteropoly acid on an inert support. U.S. Patent No. 5,099,072, to Texaco Chemical Co., discloses a method for preparing alkyl tertiary alkyl ethers over an acidic montmorillonite clay catalyst which possesses very specific physical parameters. U.S. Patent No. 5,081,318, to Texaco Chemical Co., discloses a method for preparing alkyl tertiary alkyl ethers by reacting a C 1 -C 6 primary alcohol with a C 4 -C 10 tertiary alcohol over a catalyst comprising a fluorosulfonic acid-modified zeolite. U.S. Patent No. 5,059,725, to Texaco Chemical Co., discloses a method for preparing alkyl tertiary alkyl ethers, including ethyl tertiary butyl ether, from C 1 -C 6 primary alcohols and C 4 -C 10 tertiary alcohols over a catalyst comprising ammonium sulfate or sulfuric acid on a Group IV oxide. U.S. Patent No. 5,157,162, to Texaco Chemical Co., discloses a fluorosulfonic acid-modified clay catalyst for the production of aliphatic ethers from C 1 -C 6 primary alcohols and C 4 -C 10 tertiary alcohols. In U.S. Patent No. 5,162,592, to Texaco Chemical Co. there is described a method for producing alkyl tertiary alkyl ethers from C 1 -C 6 primary alcohols and C 4 -C 10 tertiary alcohols using a multimetal-modified catalyst. A hydrogen fluoride-modified montmorillonite clay catalyst is employed in U.S. Patent No. 5,157,161, to Texaco Chemical Co., to produce alkyl tertiary alkyl ethers. In U.S. Patent No. 5,183,947, to Texaco Chemical Co., fluorophosphoric acid-modified clays are employed as catalysts in a method to produce alkyl tertiary alkyl ethers. Sulfur promoted and "superacid" catalysts are known in the art. Superacid catalysts are particularly desirable for reaction where lower temperatures are favoured. In an article titled "Design of Sulfur-Promoted Solid Superacid Catalyst" by K. Tanabe and T. Yamaguchi in "Successful Design of Catalysts", Inui, T. (Editor) Elsevier Science Publishers B.V., Amsterdam, 1988, pg.99. there is discussion of the extremely high catalytic activities of sulfur-promoted superacids, including the factors controlling super acidity. Solid superacids such as SO 4 2- /ZrO 2 , SO 4 2- /TiO 2 and SO 4 2- /Fe 2 O 3 have been reported to exhibit extremely high catalytic activities for acylation and alkylation of aromatics, esterification of phthalic acid, skeletal isomerization of paraffins, dehydration of alcohols, polymerization of alkyl vinyl ethers, liquefaction of coal and rearrangement of oximes. It is noted that the strength of the superacid depends on the extent of losing the S=O double bond character by an electronic shift from an adsorbed basic molecule to the sulfur complex. The larger the shift, the higher the acid strength. The acid strength can vary depending on the preparation method, however the acid strength of SO 4 2- /ZrO 2 , is apparently 10,000 times higher than that of 100 percent H 2 SO 4 . The effect of the addition of SO 4 2- on catalytic activity is surprisingly large. Sulfate-containing solid superacids have been employed for acid-catalyzed hydrocarbon conversions by I. Rodriguez-Ramos et al., Division of Petroleum Chemistry, American Chemical Society, New York City Meeting, August 25-30, 1990, preprints, pg. 804. Here, a number of alumina and carbon carriers that had been impregnated with aqueous solutions of iron or zirconium nitrates, then reimpregnated with ammonium sulfate solutions, were tested in MTBE synthesis from methanol plus isobutene (Eq. 1). All catalysts were considerably less active than AMBERLYST® A-15, a styrene-divinylbenzene polymer with sulfonic acid functionality. This difference is activity appears from the data to be a factor of about 40, even where the AMBERLYST® A-15 was evaluated at a lower etherification temperature (70°C versus 95°-120°C). There is a discussion entitled "Dehydration of Alcohols Catalyzed by Metallic Sulphates Supported on Silica Gel", in J. Chem. Soc. Perkin Trans. I, 1989, 707, authored by T. Nishiguchi and C. Kamio. In this work, metallic sulphates and hydrogen sulphates supported on silica gel efficiently catalyzed dehydration of secondary and tertiary alcohols under mild conditions. The dehydration sulphates were examined in the case of cyclododecanol. The sulphates of Ce, Ti and Fe were most active. Silica gel was essential for the efficient dehydration in each case. The indication was that this type of catalyst was unsuitable for primary alcohols. On page 709, Col. 1, lines 3-5, it is stated that primary alcohols failed to react. The authors suggest that the greater the Lewis acidity of a sulphate, the greater its activity on silica gel, and further, that the proton liberated from hydrogen sulphates presumably contributes to the high activity of the salts because the salts of Na, K and NH 4 on silica gel were inactive. Silica gel is quite distinct from other forms of silica. The following charts describes the properties of silica gels and indicates how they are different from other forms of silica: Properties of Different Forms of Amorphous Silica Property Silica sols Dry silica gels Silica Precipitated from solution Pyrogenic Silica SiO 2 , % 10-15 96.5-99.6 80-90 99.7-99.9 CaO, % na na 0.1-4 na Na 2 O, % 0.1-0.8 0-1 0-1.5 na wt loss, % at 105°C 50-80 na 5-7 0.5-2.5 at 1200°C 50-90 2-17.5 10-14 0.5-2.5 ultimate particle size, nm 5-100 1-100 10-25 1-100 aggregate particle size, µm 3-25 1-10 2-3 surface area, m 2 /g 50-700 200-700 45-700 15-400 pH, aqueous suspension 3.5, 8-11 2.3-7.4 4-9 3.5-8 apparent or bulk density, g/cm 3 1.2-1.4 0.1-0.8 0.03-0.3 0.03-0.12 true density, g/cm 3 2.2-2.3 2.22 2.0-2.1 2.16 refractive index, n D 1.35-1.45 1.35-1.45 1.45 1.45 oil absorption, g/g 0.9-3.15 1-3 0.5-2.8 Silica gels are classified into three types, i.e., regular, intermediate and low-density. Regular density gel is made by gelling in an acid medium, which gives very small particles with high surface area. It generally contains about ca 6 wt% water as surface hydroxyl groups, which imparts a high capacity for water absorption and absorption of other polar molecules. It exhibits a high selectivity for polar molecules and contains a large percentage of small pores, see Kirk Othmer Encyclopedia of Chemical Technology, 3rd Ed., Vol. 20, p. 763. Intermediate density silica gel has a lower surface area, but larger pore volume. It has a high capacity for water absorption at high humidities. Low density silica gel has a lower surface area and large average pore diameter. It is usually prepared as a very fine powder of extremely low density. It is known in the art to use silica gel as a desiccant, as an adsorbent, as a catalyst base, to increase viscosity and thixotropy, for surfactant and optical effects, as a source of reactive silica, for cloud seeding, in chromatographic column packing, as an anticaking agent, and in paper coating. There is a desire in the art to identify catalysts which would be suitable for producing alkyl tertiary-alkyl ethers, particularly MTBE. It would be especially desirable to identify catalysts which allow the reaction to be accomplished in one step under relatively mild conditions and show good activity. Although some of the work discussed above suggests the isomerization of alkanes or dehydration of alcohols, there seems to be nothing in the art which would suggest reacting a primary and tertiary alcohol such as methanol and t-butanol over a heterogeneous catalyst where alkylsulfonic acid is bonded to an oxide to produce the alkyl tertiary-alkyl ether, e.g. MTBE, and coproduct, e.g. isobutylene. It has now been discovered that a catalyst composition comprising alkylsulfonic acid on a Group III or IV metal oxide provides an active catalyst for alkyl tertiary-alkyl synthesis. In accordance with certain of its aspects, the novel method of this invention for preparing alkyl tertiary-alkyl ethers from primary alcohols and tertiary alcohols, and especially methyl tert-butyl ether from tertiary butyl alcohol (t-butanol) and methanol in one-step, comprises reacting tertiary alcohol and primary alcohol in the presence of a heterogenous catalyst comprising Group III or Group IV oxide, e.g. a silica gel, having an alkylsulfonic acid moiety covalently bonded to it, whereby the composite acid has the following structure: wherein R is an alkyl group having from 1 to 10 carbon atoms and n is an integer in the range of 1 to 100, and M is the oxide of a Group III or Group IV metal, preferably of Silicon. Preparation of the product of this invention may be carried out typically by the etherification in one step of tertiary alcohols with primary alcohols in the presence of a catalyst which comprises an alkylsulfonic acid on a Group III or IV oxide. The reaction can be represented by the following: The reactants comprise mixtures of primary alcohols and tertiary alcohols which can be reacted over the catalyst to produce alkyl tertiary alkyl ethers. For example, methanol and t-butanol (tBA) coreactants are reacted to form MTBE and may be mixed in any proportion in order to generate the desired methyl t-butyl ether, but preferably the molar ratio of methanol to t-butanol in the feed mixture should be between 10:1 and 1:10, if the 2 / 3 yield of desired MTBE is to be maximized. In order to achieve maximum selectivity to MTBE, and optimum conversion per pass, an excess of methanol in the liquid feed is desirable. The most preferred methanol-to-tertiary butanol molar ratio is from 1:1 to 5:1. In certain circumstances, it may be particularly desirable that the t-butanol conversion be high enough (e.g. >40% per pass), such that the crude product mix phase separates into an isobutylene-MTBE product-rich phase and a heavier aqueous methanol phase. Preferably such a product phase separation would be achieved at as low an etherification temperature as possible, but particularly in the range 160-200°C. The same process may also be applied to the preparation of other alkyl tertiary alkyl ethers, such as, for example ethyl t-butyl ether (ETBE), and TAME. Said process may be applied to the reaction of a C 1 -C 6 primary alcohol such as methanol, ethanol, n-propanol and n-hexanol with a C 4 -C 10 tertiary alcohol such as, for example, tertiary butanol and tertiary amyl alcohol. Reaction of methanol with tertiary amyl alcohol (2-methyl-2-butanol) would then yield methyl tertiary amyl ether (TAME). Alternatively a mixture of alcohols, e.g., a mixture of C 1 -C 5 alcohols, could be reacted to give a mixture of alkyl tert-alkyl ethers. The alkylsulfonic acids bonded to the oxide, e.g. the silica gel are considered derivatives of hydrocarbons in which a hydrocarbon atom has been replaced by the sulfonic acid group (·SO 2 ·OH), having the general formula R·SO 2 ·OH. They are viscous liquids or crystalline solids which are soluble in water. Industrial applications of the alkylsulfonic acids are rather limited, although the corresponding aryl derivatives are decidedly important. Examples of alkylsulfonic acids include methylsulfonic, ethylsulfonic, n-propylsulfonic, and hexylsulfonic acids. Particularly good results were observed using n-propylsulfonic acid. The catalysts used to effect this reaction are preferably silica gel alkylsulfonic acids. As used in this the term "silica gel alkylsulfonic acids" means silica having alkylsulfonic acid groups chemically bound thereto. In other words, the alkylsulfonic acids are not merely deposited on the silica, but covalently bonded to the silica. Other catalysts within the scope of the present inventive process include alkylsulfonic acids bound to other Group IV oxides, such as titania and zirconia, or bound to Group III oxides, such as alumina. Preferably, the silica gel alkylsulfonic acids used in the present invention have the following structure: wherein R is an alkyl group having from 1 to 10 carbon atoms, preferably 1 to 3 carbon atoms and n is an integer in the range of 1 to 100, but preferably 3 to 10. More preferably, the silica gel alkylsulfonic acid used in the present invention is silica gel propylsulfonic acid. The preparation of silica-bound sulfonic acids is exemplified herein by the preparation of silica gel propylsulfonic acid. The oxide support may be in the form of powders, pellets, spheres, shapes and extrudates. For some applications, the silica gel may be converted to pelletized or granular form by extruding pulverized gel with a binder, or shaping during drying. Freezing of a silica gel products silica-gel particles of nonspherical shapes. Silica gels can be prepared by the bulk-set process, the slurry process and hydrolysis of pure silicon compounds. Once a gel structure is formed, it can be modified in the wet state to strengthen the structure or enlarge pore size and reduce surface area. This is discussed in Kirk Othmer, supra , pg. 775. The examples described herein demonstrate the advantages of using granules. Silica gel can be prepared by extrusion or by compaction in conventional pelleting apparatus using a pelleting aid such as graphite. As will be demonstrated by the examples, the silica gel supports are preferably of high purity and >10 m 2 /g surface area, most preferably >100 m 2 /g. It has been found in the process of this invention that greater conversion of tertiary butanol and methanol is achieved where the surface area of the support is generally >10 m 2 /g. The weight percent of alkylsulfonic acid to oxide support should be such that the concentration of the sulfur in the formulated catalyst is in the range of 0.1 wt% to 30 wt%, although concentrations outside this range may also be employed. Where propylsulfonic acid, for example, is bonded to silica gel, a suitable quantity of sulfur is >0.1 wt%. Silica gels are commercially available in at least the following mesh sizes: 3-8; 6-16; 14-20; 14-42; and 28-200 and greater. A suitable commercially available silica gel is the grade 12, 28-200 mesh, silica gel available from Aldrich Chemical Co., Inc. having a surface area of 800 m 2 /g. Silica gel propylsulfonic acid may be prepared by treating silica gel with (3-mercaptopropyl)trimethoxysilane. The resulting surface-modified mercaptan is then oxidized using aqueous H 2 O 2 , to give the silica-bound sulfonic acid. This and other procedures are more fully described by R. D. Bradley and W. T. Ford, in "Silica-Bound Sulfonic Acid Catalysts," J. Org. Chem., Vol. 54, No. 23, pp. 5437-5443 (1989), and in Example I of this application. The silica gel alkylsulfonic acid composition of the present invention is preferably employed as a fixed bed of catalyst in a continuous reaction system. In a continuous process of this nature, the time of contact of the reactants with the catalyst is one of the interrelated factors that those skilled in the art will adjust, along with temperature, pressure, bed geometry, pellet size in order to obtain a desired rate of reaction and, hence, a desired percentage of conversion of the reactants. Thus, in a continuous process, it is not necessary to drive the reaction to completion because unreacted feedstock components can be recycled to the reactor. Catalyst life is an important factor in conducting a continuous reaction. For example, if a catalyst is easily poisoned, or if catalyst pellets do not have good structural properties, the economics of the process will be adversely affected. The catalysts of the present invention are relatively insensitive to poisoning, so this should not present a problem. As a consequence, the catalyst compositions of the present invention are advantageously used in a continuous process for the continuous production of methyl t-butyl ether reaction products from tertiary butanol and methanol. Such catalyst compositions should be suitable for use for prolonged periods without the need for regeneration. Nevertheless, with the passage of time deactivation will tend to slowly occur. Deactivation can be measured qualitatively by the loss of butanol conversion, or as the increase of temperature required to maintain an essentially constant conversion rate for the t-butanol and methanol. The fact that this method can be achieved under relatively mild operating conditions is an attractive feature of this invention. Etherification can generally be conducted at temperatures from 20° to 250°C. The preferred range is 100° to 200°C. The total operating pressure may be from 0.1 to 7.0 MPa (0 to 1000 psig), or higher. The preferred pressure range is 0.45 to 3.5 MPa (50 to 500 psig). Typically, MTBE is generated continuously in up to ca. 40 wt% concentration in the crude liquid product at total liquid hourly space velocities (LHSV) of at least 0.1 and up to ten, and relatively mild conditions, where: LHSV = Volume Of Total Liquid Feed Run Through The Reactor Per Hour Volume of Catalyst In Reactor The examples which follow illustrate the one-step synthesis of MTBE from tBA and MeOH (Eq. 2) using propylsulfonic acid-modified silica gel. The examples are only intended as a means of illustration and it is understood the invention is not meant to be limited thereby. Conversion of t-butanol (tBA, wt%) is estimated in the following examples using the equation: (Wt% Conc. of tBA in Feed - Wt% Conc. of tBA in Product) Wt% Conc of tBA in Feed x 100 Selectivities to methyl t-butyl ether (MTBE, mole %) are estimated from: Moles of MTBE in Product Liquid Moles of tBA Converted x 100 Comparing the MTBE/isobutylene production in Table 1 and Example 2 using the propylsulfonic acid-modified silica gel catalyst prepared by the method of Example 1, with data for the untreated silica gel of Example 3 and Table II, it may be noted that: a) Only the propylsulfonic acid-treated silica gel gave significant quantities of the desired MTBE/isobutylene products. b) Only the propylsulfonic acid-treated silica gel achieves product phase separation into an isobutylene-MTBE product-rich phase and a heavier aqueous methanol place at the 160°-180°C operating temperatures. Only the propylsulfonic acid-treated silica gel gives near equilibrium tBA conversion levels over the full operating temperature range (120°-180°C) when using a 1.1:1 MeOH/tBA feed mix. EXAMPLE 1 This example illustrates the preparation of a propylsulfonic acid-modified silica gel. To 500g of silica gel (Grade 12, 28-200 mesh, 800 m 2 /g surface area) was added 1000g of 10% hydrochloric acid solution and the mixture heated to reflux for 4 hours. The product solids were washed with distilled water until the washings were pH neutral and then dried in vacuo at 100°C. About 500g of the acid-treated silica gel was next refluxed with toluene (1000g) for 5 hours, 125g of (3-mercaptopropyl)trimethoxysilane added and the new mix refluxed for an additional 25-30 hours. Solids from the crude product were recovered by filtration, washed with acetone and toluene and dried in vacuo at 100°C. The mercapto silica gel from above was then added to an aqueous solution of hydrogen peroxide (30%, 1500g) in distilled water (400g) and the mixture stirred slowly at ambient temperature, overnight. The red-brown product granules were recovered by filtration, washed with water, acetone and toluene, then dried in vacuo at 100°C, overnight. Analyses were as follows: H 2 O : 0.54% Acidity : 0.48 meq/g Sulfur : 1.7% EXAMPLE 2 This example illustrates the production of methyl t-butyl ether from t-butanol and methanol using a propylsulfonic acid-modified silica gel catalyst. Synthesis was conducted in a tubular reactor (12.7 mm. int.diam., 305 mm (12") long) constructed of 316 stainless steel, operated upflow and mounted to a furnace controllable to ±1.0°C and fitted with pumps allowing flow control to ±1 cc/hr. The reactor was also fitted with a pressure regulating device and equipment for monitoring temperature, pressure and flow rate. The reactor was charged at the beginning of the experiment with 25cc of propylsulfonic acid-modified silica gel granules, prepared by the method of Example 1. A screen of glass wool was placed at the top and bottom of the reactor to ensure the catalyst would remain in the middle portion. The catalyst bed was treated with a methanol/t-butanol (1.1:1 molar mix), upflow, at a rate of 50 cc/hr, while the reactor held at a series of operating temperatures (120-180°C). Pressure was maintained at 2070 kPa (300 psi). Samples of crude product effluent were collected on stream at each temperature and analyzed by glc and gc-ir. Sample analyses data are given in Table I. Calculated tBA conversions and C 4 H 8 /MTBE selectivities for typical samples are as follows: Sample Operating Temp(°C) tBA Conv.(%) Molar Selectivity (%) C 4 H 8 MTBE 2 120 67 21 74 3 140 71 34 67 6 160 91 EXAMPLE 3 This comparative example illustrates the performance of an unmodified silica gel in the production of methyl t-butyl ether from t-butanol and methanol over a range of conditions. Using the equipment and procedures of Example 2, 25cc of silica gel granules (Aldrich Chemical, Grade 12, 28-200 mesh) was charged to the reactor system and performance was monitored over a range of operating temperatures (120°-180°C). The results are summarized in Table II, only trace quantities of isobutylene/MTBE products were detected. MTBE/ISOBUTYLENE SYNTHESIS Ex. Catalyst MeOH/tBA Molar Ratio Feed Rate (cc/hr) Temp. (°C) Time On Stream (Days) <― PRODUCT COMPOSITION (WT%) ―> SAMPLE H 2 O MeOH C 4 H 8 tBA MTBE 3 SiO 2 1.1:1 50 FS-1 31.2 68.6 120 1 1 0.9 30.2 0.5 66.5 1.7 2 0.7 30.2 0.4 67.3 1.2 140 2 3 30.9 0.1 68.8 4 30.9 0.1 68.7 160 3 5 30.8 0.1 68.7 6 0.2 30.7 0.2 68.7 7 0.1 31.3 0.1 68.2 180 4 8 0.1 31.1 0.1 68.5

Claims: A process for the preparation of alkyl tertiary-alkyl ether from tertiary alkyl alcohol and primary alcohol in the presence of a catalyst, characterized in that the catalyst is a heterogenous catalyst comprising an alkylsulfonic acid covalently bonded to an oxide of Group III or Group IV of the Periodic Table, and of formula wherein R is an alkyl group having from 1 to 10 carbon atoms, n is an integer in the range of 1 to 100 and M is the oxide of a Group III or Group IV metal. A process as claimed in Claim 1 for the preparation of methyl tertiary-butyl ether from t-butanol and methanol. A process as claimed in Claim 1 or Claim 2, wherein the Group III or Group IV oxide is selected from zirconia, titania, silica, and alumina. A process as claimed in any one of Claims 1 to 3, wherein the oxide is silica gel. A process as claimed in any one of Claims 1 to 4, wherein the alkylsulfonic acid is selected from methylsulfonic, ethylsulfonic, and n-propylsulfonic. A process as claimed in Claims 1 or Claim 2, wherein the oxide is silica gel and the silica alkylsulfonic acid moiety has the following structure: wherein R is an alkyl group having from 1 to 10 carbon atoms and n is an integer in the range of 1 to 100. A process as claimed in any one of the preceding claims, wherein the temperature is from 100°C to 200°C. A process as claimed in any one of Claims 1 to 7, wherein the operating temperature is in the range of 160°C to 200°C and the product comprises a two-phase mix of an isobutylene-MTBE product rich phase and a heavier aqueous methanol-rich phase.

Inventors: KNIFTON JOHN FREDERICK, SANDERSON JOHN RONALD, KNIFTON, JOHN FREDERICK, SANDERSON, JOHN RONALD
Applicants: HUNTSMAN SPEC CHEM CORP, HUNTSMAN SPECIALTY CHEMICALS CORPORATION
Application year: 1994
Main classification: C07C43
IPC codes: C07C43, C07C41, C07B61, B01J31