Decolorization of polyethylene polyamines using cobalt/copper/chromium catalyst

Abstract: A process for reducing the color of a polyamine product, comprising contacting the product at elevated temperature and pressure with a catalytically effective amount of a cobalt on alumina hydrogenation catalyst promoted with copper and chromium in the presence of a hydrogen-containing atmosphere. The product may be further distilled.

Description: The invention relates to methods for decolorizing polyamines and more particularly relates, in one embodiment, to methods for decolorizing polyethylene polyamines using catalytic hydrogenation. In the various methods for making polyamines and mixtures thereof, often color bodies are formed which give the polyamine product an undesirable hue. Several processes have been proposed or used commercially for the removal of color bodies from mixed polyamine products. These processes encompass both physical and chemical methods. For example, US-A-4 766 247 relates to a process for the reduction of the color of polyamines by reacting at elevated temperature and pressure the colored polyamines, e.g. triethylenetetramine (TETA) or tetraethylenepentamine (TEPA), in the presence of a hydrogenation catalyst, e.g. Raney nickel, palladium or ruthenium on carbon, and a hydrogen atmosphere for a period of time sufficient to effectuate the desired reduction in color. In this process, the polyamines can either be distilled into a narrow product composition and then hydrogenated or a crude polyamine product can be hydrogenated and then distilled to produce the desired product composition. A process for decolorizing polyethylene polyamines, such as TETA, and higher homologues, such as TEPA, by treatment with active carbon at elevated temperatures followed by distillation is described in US-A-3 723 529. US-A-3,595,921 describes that the color content of the polyethylene polyamine products prepared by the reaction of ethylene dichloride with ammonia is reduced by refluxing the product in the presence of at least about 0.5 wt.% potassium hydroxide for at least one hour at a temperature of about 110° to about 190°C. at the reduced pressure corresponding to the refluxing temperature. Polyethylene polyamine product having a substantially reduced color content is recovered from the refluxing mixture. A process for decolorizing discolored polyethylene polyamines by distilling the polyamines in the presence of polyethylene polyamine hydrochloride is described in GB-A-1 351 050. Similarly, US-A-4 570 019 describes a process which may be run continuously for producing polyethylene polyamines having improved color characteristics which comprises treating discolored polyethylene polyamines with polyethylene polyamine hydrochloride in the presence of water at elevated temperatures for the time necessary to reduce the color of the polyethylene polyamines. The decolorized polyethylene polyamines are then flash evaporated from the treating mixture. A process for decolorizing discolored polyethylene polyamine by contacting the discolored polyamine with a chlorinated hydrocarbon, e.g. an alkyl chloride or an alkylene chloride, and then distilling the resultant mixture to separate the decolored polyamine is mentioned in EP-B-0 150 075. Finally, US-A-4 731 165 teaches a process of decoloring crude TETA through contact with a sulfonic acid ion exchange resin. Subsequent distillation at elevated temperature obtains decolored TETA. Some catalytic hydrogenation decoloration techniques use catalysts with short lifetimes. Others tend to be unduly complicated. Thus, there remains a need for new methods to decolorize polyamines without some of the disadvantages of the prior methods. JP-A-48 052 708 (Seitetsu) discloses a process for reducing the colour of polyamines, whereby the hydrogenation catalyst used is nickel. Accordingly, it is an object of the present invention to provide a method for decolorizing polyamines in the presence of hydrogen and a catalyst. It is another object of the present invention to provide a method for catalytic hydrogenation to decolorize polyethylene polyamines which uses a catalyst having a long life. In carrying out these and other objects of the invention, there is provided, in one form, a process for reducing the color of a polyamine product comprising contacting the product at elevated temperature and pressure with a catalytically effective amount of a cobalt on alumina hydrogenation catalyst promoted with copper and chromium in the presence of a hydrogen-containing atmosphere. Polyethylene amines such as triethylenetetramine (TETA) and tetraethylenepentamine (TEPA) can be produced by reacting an alkanolamine, an alkyleneamine and optionally either ammonia or a primary or secondary amine in the presence of a catalytic amount of a phosphorous containing catalyst, e.g. phosphoric acid on silica-alumina or Group IIIB metal acid phosphate. The reaction can be conducted at a temperature from 175°C to 400°C, under a pressure sufficient to maintain a substantial amount of ammonia or amine in the reaction zone and particularly under vapor phase conditions. The polyamine product rapidly develops a tan to brown color, i.e. 7-8 on the Gardner color scale, ASTM Method D-1544. Polyethylene polyamines made by reacting ethylene dichloride and ammonia or reacting an alkyl halide and a diamine also have varied color levels. Indeed, polyethylene polyamines tend to discolor when exposed to air for extended periods, and it is usually recommended that storage vessels be equipped with nitrogen blanketing when the color of the polyamine is important. Discoloration of the polyamine product produced by any method limits the applications for the discolored TETA and TEPA. The colored products thus have limited commercial potential. It has been discovered that the color of polyethylene polyamines or other polyalkylene polyamines, and perhaps polyamines in general, may be reduced or eliminated by subjecting them to a mild hydrogenation process. Basically, the polyethylene polyamines made by any process are reacted with a hydrogen atmosphere in the presence of a cobalt hydrogenation catalyst promoted with copper and chromium on an alumina support at elevated temperature and pressure. Without being bound by any particular explanation, it is believed that during the process the chromophores, i.e. color bodies, are reduced or eliminated; the exact mechanism of the process is unknown. More specifically, the process involves contacting a colored polyamine product with a catalytically effective amount of a Co/Cu/Cr on alumina hydrogenation catalyst in the presence of a hydrogen-containing atmosphere at elevated temperature and pressure. For the process, the polyamine product can be any polyalkylene polyamine. This polyamine product produced by any of the applicable preparation processes can either be treated for color reduction as a crude product, i.e. as produced from the applicable preparation process, or be distilled into selected cuts and then treated. In one embodiment of the invention, the polyamines have at least some compounds with the formula NH 2 -CH 2 CH 2 -(NH-CH 2 CH 2 ) n -NH 2 where n ranges from 2 to 6. It will be appreciated that often the polyethylene polyamine will be a mixture of amines. In one embodiment, the greatest single component in the polyamine product is triethylenetetramine; in another, the greatest single component is tetraethylenepentamine. The catalyst is Co/Cu/Cr on an alumina support. Preferably, the catalyst contains from 30-45, wt.% cobalt, from 5 -13 wt.% copper, from 0.1-3 wt.% chromium, with the balance alumina. The copper and chromium serve as promoters for the cobalt. Enough catalyst should be used to be effective in reducing or eliminating the color in the polyamine product. The process of the present invention can either be performed in a batch or continuous mode of operation utilizing either a fixed bed or slurry type reactor. Generally, the elevated temperature should be from 120 to 170°C, preferably from 120°to 160°C. The elevated pressure may range from 3.5 MPa to 41.5 MPa, preferably 7.0 to 34.5 MPa. If a batch process is used, the batch times may range from 0.1 to 4 hours. In a continuous process, the space velocity may range from 0.1 g/hr-cc catalyst to 1.0 g/hr-cc catalyst. The catalyst preferably has a lifetime of at least 1000 hours. The invention will be further illustrated in the following Examples which are not intended to limit the scope of the invention. Example 1 and Comparative Examples A and B Color Reduction of TEPA Polyamines The tests were carried out in a 100 cc electrically heated stainless steel tubular up-flow reactor which was filled with the indicated catalyst (see Table I). TEPA and hydrogen were continuously fed to the heated reactor. Reactor pressure was maintained at 17.3 MPa with a back pressure regulator. Reactor effluent samples were analyzed by GLC and are given in Table II. Color numbers of reactor effluent samples are listed in Table I. Example 2 Catalyst Life Study A catalyst life study on Co/Cu/Cr on alumina for TEPA decolorization was also conducted. The spent catalyst from Example 1 was charged back to the reactor and run at the same conditions for 1000 hours. The reactor effluents were distilled. No significant catalyst activity loss was noted throughout the run. After distillation, TEPA products with colors of Pt-Co 100-125 (green hue) were obtained. The particular catalysts used in these Examples are extrudates, but the catalysts do not have to be limited to those formed by extrusion. TEPA Decolorization Ex. Catalyst Temp., °C. LHSV, g/hr-cc H 2 LHSV (l/hr-cc) Color (Gardner) Feed Product 1 Co-Cu-Cr/alumina 135 0.3 0.1 9 2+ A G-62RS (United) 135 0.3 0.15 9 6 B Co-0164 (Engelhard) 140 0.3 0.1 9 5 Catalyst G-62RS is 34.5% cobalt on a silica-based support; Co-0164 catalyst is 25% cobalt on a silica-based support. Thus, the catalyst of the present invention results in better color reduction and, as shown in Table II, lower degredation of TEPA. The catalyst was 40.3 wt.% Co, 5.1 wt.% Cu, and 1.0 wt.% Cr on alumina. TEPA Compositions (wt.%) Component Feed Ex. 1 Ex. 2 Ex. 3 Diethylenetriamine (DETA) 0.251 0.376 0.629 0.541 Triethylenetetramine (TETA) 1.184 1.470 1.029 1.579 Hydroxyethyl DETA (HEDETA) 1.509 1.333 1.002 1.457 Piperazinoethylenediamine (PEEDA) 0.187 2.351 2.692 3.697 Aminoethyl TETA (AETETA) 10.141 9.540 9.916 9.331 Tetraethylenepentamine (TEPA) 66.491 63.579 63.038 61.236 Aminoethyl PEEDA (AEPEEDA) 6.553 6.914 6.043 6.060 Piperazinoethyl DETA (PEDETA) 8.153 8.164 7.802 8.724 Pentaethylenehexamine (PEHA) 1.314 1.380 1.701 1.896 Total Others 4.217 4.896 6.148 5.479 Many modifications may be made in the process of this invention without departing from the spirit and scope thereof which are defined only in the appended claims. For example, one skilled in the art may discover that particular reaction conditions, sequences, and Co-Cu-Cr/ alumina catalysts which may not be explicitly recited herein, but which are nevertheless anticipated, would give optimal or otherwise desirable results.

Claims: A process for reducing the color of a polyalkylene polyamine product, comprising contacting the product at a temperature of 120°C - 170°C and a pressure of 3.5 MPa - 41.5 MPa with a catalytically effective amount of a cobalt on alumina hydrogenation catalyst promoted with copper and chromium in the presence of a hydrogen-containing atmosphere. A process as claimed in Claim 1, wherein the elevated temperature is in the range of 120°C to 160°C. A process as claimed in any preceding Claim, wherein the elevated pressure is in the range of 7.0 to 34.5 MPa. A process as claimed in any preceding Claim, wherein the hydrogenation catalyst contains from 30-40 wt.% cobalt, 7-13 wt.% copper, 0.1-3 wt.% chromium and the balance alumina. A process as claimed in any preceding Claim, wherein the polyalkylene polyamine product comprise at least some polyamine compounds of formula NH 2 -CH 2 CH 2 -(NH-CH 2 CH 2 ) n -NH 2 where n ranges from 2 to 6. A process as claimed in any preceding Claim, wherein the greatest single component in the polyalkylene polyamine product is triethylenetetramine or tetraethylenepentamine. A process as claimed in any preceding Claim, further comprising distilling the polyalkylene polyamine product following the contacting step to further reduce color.

Inventors: SU WEI-YANG, SU, WEI-YANG
Applicants: TEXACO DEVELOPMENT CORP, TEXACO DEVELOPMENT CORPORATION
Application year: 1994
Main classification: C07C209
IPC codes: C07B61, C07C209, C07C211, B01J23