Colour display/detector

Abstract: A colour semiconductor display device in which optoelectronic elements capable of emitting/absorbing light of different predetermined wavelengths in the visible wavelength range (e.g. red, green, blue) are formed on a common substrate and comprise similar alloy compositions which are lattice matched to the substrate material. The alloy is preferably a III-V nitride alloy lattice matched to Si or GaP substrate material. In the disclosed embodiment, a colour display device comprises a silicon or GaP substrate with an array of pixels, each being formed by a group of three (red, green, blue) colour sub-pixels provided on the substrate. The pixels are formed of InAlNSb alloy, with a quantum well regions of InNSb and barrier regions of AlNSb, or are formed of AlGaAsSbN alloy, with quantum well regions of GaAsN and barrier regions of AlNSb. Tuning of the wavelength emission/ absorbtion characteristics of the sub-pixels is by doping of the quantum well material with aluminium and/or by quantum confinement.

Description: This invention relates to colour displays or detectors and to optoelectronic devices suitable for use therein. In particular it relates to semiconductor optoelectronic elements and to the manufacture thereof, and to a semiconductor colour display/detector comprising a plurality of such optoelectronic elements. The invention also concerns an alloy material for use in the fabrication of such optoelectronic elements, colour displays and detectors. Known colour displays can be split into two main types: i) vacuum or valve displays such as the cathode ray tube or gas discharge lamp and ii) thin, flat screen displays such as liquid crystal or electroluminescent displays. The foregoing display types have a number of drawbacks associated with their manufacture and use. Whilst the manufacture and mass production of CRTs and gas discharge lamps is a well established and reliable technology, these display devices are bulky and relatively fragile. Additionally, CRTs, gas discharge tubes and the like consume large amounts of power and are therefore unsuitable for portable or mobile applications. The aforementioned flat displays overcome some of these problems in that they are generally more robust, consume less power and are less bulky than CRTs and the like. They are also susceptible to mass production since similar techniques as are used in integrated circuit production can be applied to their manufacture. However, their manufacture is somewhat more complicated than IC production, since the optically active material has to be sandwiched between two substrates. In addition, the substrates support the electrodes necessary to stimulate the optically active material and their associated signal lines, thereby resulting in a complex multilayer structure. Drawbacks of known flat displays are that they have poor colour uniformity, low resolution, viewing angle and brightness, and are slow to respond to updated information in comparison to CRTs and the like. Known colour detectors can be split up into three main types: (i) vacuum or valve detectors such as Orthicon or Vidicon (TM) tubes; (ii) thin, flat detectors such as photo diodes optimised or doped to detect a particular wavelength, or band of wavelengths, of light; and (iii) thin, flat detectors such as Charge Coupled Devices (CCD) utilising colour filters. The foregoing colour detectors have a number of drawbacks associated with their manufacture and use, particularly when used as part of full colour detectors. In the case of Vidicon (TM) tubes, a full colour detector comprises either three separate tubes, each tube having one primary colour input thereto, or a single tube having a special target system in the form of a matrix having colour-discriminating properties. Light incident on a full colour detector utilising a Vidicon (TM) tube or tubes, is split into its primary colour components by optical filters. Consequently the detector is bulky and heavy due to the electrical components required to produce and control the scanning electron beam and the optical components required in the detector. It is also sensitive to vibrations causing misalignment of the electron beam and the optical components. Photo-diodes are unsuitable for use in a full colour detector because a triad of three photo-diodes, one of each optimised for a different primary colour, is necessary to form a single colour picture cell. Because the constituent materials, doping materials or amount of doping are different for photo-diodes optimised for different colours it is very difficult to fabricate triads where each photo-diode is close enough to its neighbours to appear to be part of the same picture cell. For this reason, photo-diodes and the like are unsuitable for colour camera applications. Full colour detectors utilising CCD's have a number of advantages over vacuum or valve devices, because they are of smaller size and have greater physical and optical ruggedness. Nevertheless, CCD full colour detectors still require some form of colour filtering in either the multi-tube or single tube format. Again this leads to undesirable bulkiness and weight. A further disadvantage of CCD full colour detectors, is that when they are used as the target in colour cameras they exhibit inadequate definition and have poor resolution. Many of the drawbacks associated with known colour displays and detectors are due to the fact that hitherto optoelectronic elements capable of being adapted to operate in the visible red to visible blue (and also U-V) region of the spectrum and made from substantially the same materials, were unknown. This resulted in optoelectronic devices being built on different substrates and having to have complicated and bulky interconnections therebetween. Furthermore, known optoelectronic devices were not fabricated on Silicon substrates. As a result, well known Silicon VLSI technology techniques could not be monolithically incorporated into the optoelectronic devices. In particular, optoelectronic devices comprising semiconductor material having band-gaps which are wide enough to emit/absorb blue light have proven very difficult to grow and dope in a controlled and systematic manner. II-VI compound semiconductors whilst having suitable band-energies for blue light, are not suitable for depositing on a Silicon substrate and invariably have to operate at low temperatures. Wide band-gap nitride semiconductors have been studied as alternatives to II-VI compounds with varying degrees of success. Although blue light has been emitted from GaN devices, such devices had to be built on sapphire substrates, which is prohibitively expensive for commercial applications, and the quality of the resulting material was poor due to lattice mismatch with the substrate and the introduction of nitrogen vacancies due to the relatively high growth temperatures. Examples of certain known solid state colour detection devices which do not use colour filters, and which include arrays of detection devices sensitive to different colour portions of the electromagnetic spectrum are disclosed in EP-A-0166787, US-5138416. In EP-A-0166787, the devices are electrostatic induction phototransistors (SIT), which operate on the principle that the gate potential of the SIT is determined by light directed thereto. Structural dimensions of the SIT's, such as diffusion depths of the SIT gate regions, are varied to provide the required selectivity of spectral sensitivity. Blue light response is improved by limiting the depletion layer thickness. In US-5138416, a multilayer colour photosensitive element is made from group III-V alloy semiconductors. Charge is collected from the photosensitive element according to an amount of time it takes for red, green and blue light photoexcited carriers to travel through the layers. The resulting waveform obtained from the element will show temporal features which depend on the colours of illumination. Examples of certain known solid state colour display devices including electroluminescent elements emitting different colours are disclosed in US 3890170 and US 4211586. In US 3890170, two matrices of respectively, red LED's and green LED's are integrated and can provide a red, green or orange display. The red LED's are gallium arsenide phosphide and the green LED's are gallium phosphide, and the total LED array is formed on a monolethic semiconductor substrate of gallium arsenide or phosphide. Row and column address lines are provided on the substrate for each matrix so that a strobing logic address system can effect lighting of the individual LED's for producing an alphanumeric character or graphic display. In US 4211586, an array of Red, Green, Orange and Yellow light emitting diodes is formed on a common gallium arsenide substrate. A vertically graded epitaxial region of GaAs 1-x P x is selectively etched to different depths, and diodes of different colour emission are formed at selected concentration levels in the epitaxial region. In neither of these colour display devices is full colour display possible, as the materials employed are not capable of blue light emission. A semiconductor light emitting device which can be adapted for blue light emission is disclosed in EP-A-0496030. The device has mixed crystals of AlGaInN compound semiconductors formed as an epitaxial layer over, and lattice matched to, a substrate crystal of ZnO. Specific LED constructions for blue light emission are disclosed in GB-A-2250635 and US 5005057. In GB-A-2250635 a luminescent layer epitaxially grown on a buffer layer, in turn formed by epitaxy on a semiconductor substrate of zinc sulphide, zinc selenide or a mixed crystal thereof, is formed from aluminium nitride, indium nitride, gallium nitride or a mixed crystal of at least two of such nitrides. In US 5005057, a blue LED has either a superlattice structure of alternately stacked BP and Ga x Al 1-x N (0≤x≤1) layers, or a mixed crystal structure of Ga x Al y B 1-x-y N z P 1-z (0≤x,y,z≤1 and x+y≤1). Single and double heterojunction structures are disclosed. The present invention aims to alleviate the earlier-mentioned disadvantages of known colour displays and to provide a colour display that is thin, lightweight, robust, simple to manufacture, consumes low power and yet has high levels of brightness and resolution and a wide range of viewing angles. The present invention also aims to alleviate the earlier-mentioned disadvantages of known colour detectors and provide a colour detector that is lightweight, robust, simple to manufacture, has a simplified construction and has a high level of resolution. The present invention is based on the recognition that certain group III-V nitride alloys can, by suitable choice of elemental composition ratios, be fabricated so as to be substantially lattice matched to a commonly used material substrate (Si or GaP) and so as to form the basis of an optoelectronic element which can by appropriate doping or quantum confinement techniques be made to emit/absorb light at any desired wavelength in the visible red to ultra-violet region of the electromagnetic spectrum, including blue. In one aspect, the invention provides an optoelectronic element formed on a substrate and comprising a III-V nitride alloy, whereby said III-V nitride alloy is substantially lattice matched to the substrate, and is adapted to emit/absorb light at a desired wavelength in the range corresponding to visible light, said III-V nitride alloy comprising one of In p Al 1-p N 1-r Sb r , 0≤p≤1, 0<r<1, and Al a Ga 1-a N b (As c Sb 1-c ) 1-b , 0≤a≤1, 0<b<1, 0≤c≤1. In a preferred embodiment of the invention the substrate comprises either Silicon (Si) or Gallium Phosphide (GaP). Preferably the element has an active region comprising a quantum well region of InNSb or GaAsN and a barrier region of AlNSb. In one embodiment, the active region comprises an active quantum well region of InN 1-y Sb y , where y lies in the range 0.32≤y≤0.38 and barrier regions of AlN 1-x Sb x where x lies in the range 0.57≤x≤0.63. In another embodiment, the active quantum well region comprises GaAs z-1 N z where z lies in the range 0.17≤z≤0.23, and barrier regions of AlN 1-x Sb x where x lies in the range 0.57≤x≤0.63. In another aspect, the present invention provides a colour semiconductor display/detector device having a plurality of optoelectronic elements as defined above, said plurality including a first element and a second element, said first and second elements being formed on and substantially lattice matched to a common said substrate, and being capable of emitting/absorbing light having respective different predetermined wavelengths. A particular advantage of a display/detector according to the present invention is that it can be manufactured in a "one step" epitaxial growth process without the need to assemble separate components and inject optically active material between substrates. In a further aspect of the present invention, there is provided a colour semiconductor display device comprising a single substrate and an array of electroluminescent light emitting elements formed on and substantially lattice matched to the crystal structure of said single substrate, the elements of said array each being in the form of an optoelectronic element as defined above, and said array being adapted for full colour display and comprising red, green and blue said electroluminescent elements formed of substantially similar said III-V nitride alloy compositions tuned for their respective emission wavelengths by quantum confinement incorporation and/or by doping variation. A specific embodiment of the invention adapted for use as a colour display will now be described by way of example with reference to the accompanying drawings, in which: Figure 1 is a diagram of energy gap (eV) plotted against lattice constant (Å;1Å=0.1nm) for the semiconductor of interest; Figure 2 is a schematic diagram of a InN 0.65 Sb 0.35 / AlN 0.4 Sb 0.6 quantum well structure for three different well widths, to achieve red, green and blue emission; Figure 3 is a schematic diagram of a sub-pixel, vertical cavity laser structure, specifying the layer composition to form the quantum well active region; Figure 4 shows further details of the semiconductor layers within the sub-pixel structure shown in Fig. 3; Figure 5a shows a schematic diagram of 3 sub-pixels that form a red/blue/green assembly comprising a full colour display pixel; Figure 5b shows a portion of an array of full colour display pixels of Figure 5a forming a full colour flat panel display device; Figures 5c and 5d illustrate schematically other possible arrangements of sub-pixels in full colour pixel arrays; Figure 6 illustrates, with progressive magnification, the construction of a display from sub-pixels comprising quantum confinement structure(s), which assemble into RGB pixels which assemble into an array of colour pixels; Figure 7 illustrates how, typically a pixellated display according to the invention can be provided with a signal addressing scheme; Figure 8 illustrates, schematically a basic drive circuit for driving a display device according to the invention; Figure 9 shows a schematic sequence of steps for the manufacture of a pixellated array, and Figure 10 shows how a microlens may be placed over each pixel to enhance the apparent brightness of the display by restricting the emission solid angle. The following description describes a semiconductor colour display system comprising a plurality of optoelectronic devices fabricated from a nitride alloy. The optoelectronic devices are fabricated with band gaps suitable for light emission from red through to blue, and are supported by and lattice matched to a Silicon (Si) substrate. Wavelength tunability is achieved by the quantum confinement properties of the semiconductor nanostructure and/or by varying the alloy composition. High quality nanostructure crystals can be grown by Molecular Beam Epitaxy techniques. A description of quantum confinement techniques and semiconductor nanostructures, and an explanation of the terminology used in the following description can be found in, for example, "Physics and Applications of Semiconductor Microstructures", M Jaros, Oxford University Press. There follows a more specific description of the semiconductor system used in a colour semiconductor display to be described later. Figure 1 shows a diagram of energy gap (eV) against lattice constant (Å; 1Å=0.1 nm) for the semiconductors of interest. The vertical line at 0.54 nm corresponds to the lattice constant of Silicon. The open circle denotes the Γ point and crosses denote the X point conduction band minimum for each respective semiconductor. The X points shown are for AlSb and AlN. A linear interpolation between the binary compounds is used to achieve an estimate of the alloy band-gaps. It should be noted that the linear interpolation gives only an estimate of the band-gap energy since the phenomenon of alloy bowing (ie. in reality there is a non-linear interpolation between the band gap energy of respective binary compounds) will alter the band-gap energy by a few percent. In Figure 1, the point A on the InN-InSb line represents an InNSb alloy containing ∼ 65% nitrogen. It can be seen from the figure that such an InNSb alloy containing ∼ 65% nitrogen is lattice matched to Silicon and has a direct band gap corresponding to ∼1.5eV. Such an InNSb alloy can be quantum confined by an AlNSb barrier to form a quantum well structure. Also, the point B on the GaN-GaAs line represents a GaAsN alloy containing ∼ 20% nitrogen. It can be seen from the figure that such a GaAsN alloy containing ∼ 20% nitrogen is lattice matched to silicon and has a direct band gap corresponding to ∼ 1.83 eV (680 nm). Such a GaAsN alloy can be quantum confined by an AlSbN barrier to form a quantum well structure. AlSb is an indirect compound semiconductor with an X point of 1.6eV and a Γ point of 2.2eV from the valence band edge. Also from Figure 1, an interpolation of the Γ point from AlN to AlSb, shows that an alloy composition of AlN 0.4 Sb 0.6 represented by point C has a direct gap of ∼4.0eV and is lattice matched on the one hand to both InN 0.65 Sb 0.35 and Silicon and on the other hand to both GaAs 0.8 N 0.2 and Silicon. The emission wavelength of an optoelectronic device fabricated using InNSb can be tuned by replacing a small fraction of the indium by aluminium thereby increasing the energy gap of the structure without changing the lattice parameter significantly, or quantum confinement techniques can be used, wherein the quantum well width is changed by altering the thickness of the InNSb alloy layer, or quantum well wires and dots are fabricated from the semiconductor system. Alternatively, a combination of Al doping and quantum confinement can be used. Thus, it is possible to tune the band gap energy of the quantum well region material, InNSb, to correspond to energy transitions suitable for emitting light at red, green or blue wavelengths. This is particularly advantageous in relation to the emission of blue light, since a blue light emitting material, lattice matched to Silicon, has not been previously fabricated. In a particular preferred embodiment an InN 0.65 Sb 0.35 /AlN 0.4 Sb 0.6 quantum well structure is used, to provide optimum lattice matching to a silicon substrate. However, lattice mismatch of up to 5% or so is tolerable; larger mismatches usually introduce defects which degrade the performance of the device. The allowability of such lattice mismatch provides possible variation of the constituent ratios in the above alloys of the device. More particularly, the preferred alloy composition for the barrier can be represented as AlN 1-x Sb x where x satisfies the relation 0.57≤x≤0.63, while the preferred nitride alloy composition for the quantum well can be represented as InN 1-y Sb y , where y satisfies the relation 0.32≤y≤0.38. An alternative embodiment, using a GaAsN/AlNSb quantum well structure, can also be lattice matched to silicon as can be seen from Figure 1. Taking an allowable degree of lattice mismatch into account, the preferred alloy composition for the barrier can again be represented as AlN 1-x Sb x where x satisfies the relation of 0.57≤x≤0.63, while the preferred nitride alloy composition for the quantum well can be represented as GaAs 1-z N z , where z satisfies the relation 0.17≤z≤0.23. Wavelength tuning can be achieved by replacing a small fraction of the gallium by aluminium and/or by quantum confinement. A schematic diagram of an InN 0.65 Sb 0.35 /AlN 0.4 Sb 0.6 quantum well structure for three different well widths, namely 20nm, 10nm and 5nm is shown in Figures 2a to 2c. The structure 1 in each of these three figures comprises a quantum well region 2 formed by a well layer of InN 0.65 Sb 0.35 sandwiched between two barrier layers 3 of AlN 0.4 Sb 0.6 . From Figures 2a to 2c it can be seen that such a structure provides an increase in the band gap energy of the quantum well material for a corresponding decrease in the well width. This figure demonstrates the wavelength tunability using quantum confinement that can be achieved with the AlInNSb semiconductor system. As mentioned before, tunability can alternatively be achieved in a structure with the quantum well width kept constant by introducing aluminium into the well alloy to increase the band-gap energy. In this way, similar alloy compositions all with the basic InNSb composition but differently doped can be used to produce light at different visible wavelengths. Silicon is a very important material in electronics, and the specific embodiment is therefore based on quantum confinement structures utilising the InAlNSb alloy system and being substantially lattice matched to and constructed upon a Silicon wafer substrate. A further advantage of using a Silicon substrate is that wafers up to 8'' diameter have been reliably manufactured and such sized wafers would be suitable for use in displays for portable "hand held" type TV's. The stability of the alloys InN 1-y Sb y /AlN 1-x Sb x required to be lattice matched to silicon (0.57≤x≤0.63), (0.32≤y≤0.38) can be demonstrated theoretically using standard theory of Stringfellow (J. Electronic Materials Vol 11, No 5, Pg 903 etc 1982). Stringfellow gives a formula for the critical temperature Tc above which the alloy is stable against spinodal decomposition. Consider the Gibbs free energy which tends to destabilise the alloy with the strain energy which acts to stabilise it. From equation 6 of the above reference T c = T g - T s where T g = 8.75 K Δ a 2 x (1- x ) Ra 4.5 0 T s = EΔ a 2 2(1-ν) RN v a 2 0 where K = 1.15 x 10 7 cal/mol Å 2.5 R = Gas constant E = Youngs modulus ν = Poisson's ratio N v = number of moles/unit volume a 0 = lattice constant of the alloy Δ a = difference between the lattice constant of the binary end members x = fractional composition Gives T g = 5.05 x10 7 1 a 2.5 0 Δ a a 0 2 x (1- x ) (degrees K) T s = 1.36 x10 3 a 3 0 Δ a a 0 2 (degrees K) For the alloy to be stable at any temperature requires T S >T G or T S /T G >1. Therefore T S /T G = 2.69 x10 -5 a 5.5 0 x (1- x ) where a 0 is in Å. For growth on Silicon a 0 = 5.4 Gives InN 0.65 Sb 0.35 = 1.26 AlN 0.4 Sb 0.6 = 1.195 Thus the wells and barriers of an AlInNSb alloy are stable when lattice matched to Silicon. Similar calculations based on the Stringfellow theory have been performed to demonstrate the stability of the alloys proposed earlier for the AlGaAsNSb system, i.e. GaAs 1-z N z /AlN 1-x Sb x (0.57≤x≤0.63), (0.17≤z≤0.23). The method to be used for the fabrication of the alloy layers can be based upon existing techniques known in the art. For example, in the proposed AlInNSb system, techniques developed from those used to make InSb and nitride materials well known in the technical literature, [see (1) GaN, AlN and InN, a Review J Vac Sci Tech B 10 , 4, 1237 (1992); (2) Eg = 2.2 eV - Band Gap for InN D W Jenkins, R D Hong, J D Dow, Superlatt Microstruc. 3, 365, (1987): (3) a = 4.98 Å - Lattice constant for InN S Strite, J Ruan, David J Smith, J Soiel, N Manning, W T Choyke and N Morkoc Bull A.P.S. 37,346, (1992)] will be used. A method of fabrication of the alloy systems described in accordance with the invention would involve use of either CVD (chemical vapour deposition/epitaxy) or MBE/CBE (molecular or chemical beam epitaxy) technologies (see Crystal Growth by A W Vere, Plenum Press 1987). Elemental sources of Al, In and Sb are well known for use with these growth systems. Recently nitride materials have been under intensive study and two sources of nitrogen are known - use of ammonia and use of a radical ion source (or plasma). The operating parameters and sequencing for the layer growth system using a chosen machine can be readily established by those skilled in the art of growth to achieve the precise growth conditions and required alloy ratios, demonstrated earlier with reference to the Stringfellow theory to be stable. The above-described quaternary InAlNSb alloy system with InNSb wells and AlNSb barriers are generally easier to fabricate than the quinternary AlGaAsSbN alloy system with GaAsN wells and AlNSb barriers. One less elemental source overall is needed when employing the former alloy, and the control of the layer growing process is less complicated, since two of the elements, namely N and Sb continue to be deposited in both the well and barrier growing steps; only one element is switched, namely In↔Al. Having described the theoretical basis for the choice of particular semiconductor alloy systems which satisfy the requirement of lattice matching to a substrate, and range of wavelength of light emission/ detection, and having referred to the envisaged fabrication method, we will now describe suitable device structures embodying these systems. A colour element, or sub-pixel, of a semiconductor display comprises a quantum confined structure with the band-gap emission wavelength tuned to one of the three primary colour wavelengths, ie. red, green, blue. A schematic diagram of a typical 'sub-pixel', vertical cavity laser structure is illustrated in Fig. 3, and a full structure layer diagram for 1 sub-pixel is shown in Fig. 4. The InNSb/AlNSb structure of the vertical cavity laser or surface emitting laser shown in Figure 3 comprises a quantum well region 5 capped top and bottom by optical reflectors 6a,6b. As illustrated, the quantum well region 5 comprises an active quantum well layer 5a of InN 0.65 Sb 0.35 sandwiched between two barrier layers 5b of AlN 0.4 Sb 0.6 . The Bragg reflectors 6a, 6b at the top and bottom of the region 5 are arranged such that light propagates in the laser cavity in a direction substantially perpendicular to a silicon substrate 7 on which the laser structure is formed, which gives this particular type of laser its name. The laser cavity 5, 6 is surrounded by Si0 2 8 insulator having apertures 9 and 10 at the top and bottom of the laser cavity, such that light can be emitted through the top aperture, and an electrode 11 can be electrically connected to the bottom reflector 6b. A further electrode 12 is electrically connected to the top reflector 6a. The reflectors comprise a laminate of highly reflecting InAlNSb superlattices, the top reflector 6a being doped, possibly with Be, to yield a p type semiconductor and the bottom reflector 6b being doped, possibly with Si, to yield an n type semiconductor. In this embodiment the top electrode 12 is gold. Both top and bottom electrodes 11 and 12 lead to the Silicon substrate 7 where they can be connected to conventional Si based VLSI electronics. Such sub-pixels can be fabricated by standard photolithography and etching techniques. Each sub-pixel is addressed with wires laid onto or behind the Silicon substrate 7 wafer and connected to the respective electrodes 11, 12 by metal evaporation techniques as used in VLSI technology. The sub-pixels can be connected in a similar manner as standard LCD colour TV display arrangements or the like for distributing the relevant signals suitable for creating an image. Silicon VLSI technology can be embedded in the substrate and could be used for receiving and routing the video signal. This is a particular advantage for producing a compact display. Alternatively to the laser structure, an LED structure omitting the cavity reflectors 6a, 6b or a resonant cavity LED with a bottom reflector of about 99% reflectivity and a top reflector of about 90% or less reflectivity could be fabricated from the semiconductor system using the same alloy. In each case, three colour sub-pixels are combined to form a full colour pixel. Figure 5(a) is a schematic diagram showing three sub-pixels 13a, 13b, 13c such as described earlier, each tuned to a red, green or blue wavelength and assembled into a full colour pixel 13 suitable for use in a semiconductor display. Each sub-pixel is shown formed by a cylindrical cavity laser with a top ring contact 12, the individual sub-pixels being bundled together to form a full pixel. Such diameter pixels comprise sub-pixels having thicknesses which vary but are of the order of 1 µm, and diameters of approximately 30µm and can be manufactured using existing technology. The full colour pixels 13 comprising bundles of sub-pixels 13a, 13b, 13c can be arranged into an array 14 of full colour pixels all fabricated on a Silicon substrate 7 as shown in Figure 5b. Other possible arrangements of individual pixels are shown in Figures 5c and 5d. In these Figures a full colour pixel 13 again comprises a group of 3 sub-pixels 13a, 13b, 13c, each capable of emitting a different primary colour, and each sub-pixel forms a part of a "column" 15 of sub-pixels capable of emitting the same colour. A semiconductor display having such an arrangement of pixels would be more simple to fabricate using photolithography sequences than the arrangement shown in Figures 5a and 5b. Such a full colour pixel forms the basic unit of a colour display and arrays of 1000 x 1000 pixels can easily be fabricated by standard photolithographic and etch techniques to provide a full colour display suitable for use as a TV computer screen. The way in which constituent elements are built to form such a full colour display is illustrated schematically in Figure 6. An individual quantum confined well, wire or dot structure 13a, built on a Silicon substrate 7 forms part of a bundle of such structures 13 each individual structure emitting light having a wavelength corresponding to one of blue, green or red light and fabricated on a common substrate 7, which forms a full colour pixel. The full colour pixels 13 can be arranged into array 14, the array forming a, or a part of a, display screen 16. The display screen unit can be enclosed in a thin plastic film to protect the surface from damage. A typical pixel arrangement is for example, 480 rows x 640 columns which is a standard 3 colour LC-TV aspect ratio and format having a total of 921,600 sub-pixels. HDTV configuration is also possible. If the display is to be used in a standard TV system or the like, the values of the emission wavelengths are usually chosen to satisfy the CIE chromaticity diagram, in order to produce a good "white" colour. With reference to Figure 7, a typical semiconductor display using display elements as hereinbefore disclosed, is described and comprises lasers constructed on a Silicon substrate. The semiconductor material is pixellated using lithography and etching techniques in order to create row and column region pixels, each pixel containing at least 3 sub-pixel lasers whose output colours are red, green and blue respectively; such sub-pixellation is not illustrated in Figure 7. The diametric dimension of a sub-pixel can be of the order of a few microns. A simple x-y matrix addressing scheme which is standard in flat panel T.V. construction can be used, and which is applicable here in the manner shown by accessing respective pixel column 20 and row 21 pads. Examples of two possible alternative addressing schemes are described hereinafter: (i) single x-y pixel interaction in which the brightness of each sub-pixel 13a, 13b, 13c is encoded in the signal sent to each pixel pad 20, 21 and decoded in VLSI located in the Silicon substrate 7 at or near the pixel 13, respective control signals being then sent to the appropriate laser contacts 12; or (ii) a system in which both or one or other column or row pads are split into separate sections, one section for each sub-pixel of a pixel and three separate wires are connected to the respective split pixel pad sections and are thereby connected to the laser contact 12 of the appropriate sub-pixel to control colour brightness. Separation of adjacent columns of pixels can be achieved by forming isolation grooves 22 which extend into the substrate 7 and are then filled with dielectric material 18 to provide a flat top surface on which row drive lines 19 each connecting a row pad 21 to the contacts 12 of a pixel row can be formed. Alternatively separation can be achieved by creating elongate isolation zones by ion implantation. An example of a possible circuit for driving a display operated in accordance with one or other of the above addressing schemes is shown schematically in Figure 8. In Figure 8 row 25 and column 26 drivers apply voltage signals to the display 24. Two sets of waveforms are generated for supplying the row and column drivers 25, 26. A strobe wave form generator 27 supplies row waveforms, and a data waveform generator 28 supplies ON and OFF waveforms to the column driver 26. Overall control of timing and display format is controlled by a control logic unit 23. Not only the display array 24, but also the control electronics can be integrally formed on a common substrate 7. Such a semiconductor display can be fabricated in the following fashion employing generally known techniques, with reference to Figure 9. A Silicon substrate 7 already formed with the appropriate VLSI electronics for T.V. receiving and display control signal generation is coated with silicon dioxide (not shown in Fig. 9) to form a semi-insulating layer. Then a stack of layers 29 alternately InNSb and AlNSb are deposited on the silicon dioxide to form an InAlNSb superlattice, which provides a very short period quantum well/barrier structure. These stacked layers will eventually form the bottom reflectors 6b in the finished sub-pixels. The InNSb layers can be doped with an impurity such as Si during their deposition to yield a n type semiconductor. The layers which will form the barrier layers 5b of AlNSb and the well layer 5a of InNSb of each of the quantum well regions 5 in the finished sub-pixels are then deposited. These are layers 30, 31, respectively. Though only one is shown in Fig. 9, three different quantum well regions are deposited one on top of the other, each quantum well region being adapted to emit light of a different primary colour from the primary colour emitted by the other quantum well regions. It is possible to employ the InAlSbN alloy for only the blue emitting one of these three quantum well regions. The other two, namely red and green emitting, quantum well regions may be made from other alloy systems. However, the use of similar alloys in all three quantum well regions is preferred as it simplifies the fabrication process. Next, a further stack of layers 32 alternately InNSb and AlNSb are deposited over the quantum well active region layers 30, 31 thereby forming a further InAlSbN superlattice. The InNSb layers are doped with an impurity such as Be to yield a P type semiconductor. The technique used to deposit the materials onto the Silicon substrate is typically Molecular Beam Epitaxy (MBE). Once the respective layers have been deposited, photo lithography and etch techniques employing photoresist 33 are used to form an array of individual sub-pixel lasers, as shown in Figure 9(b). This stage is essentially a three stage process. Three different mask patterns are used in sequence, each one exposing areas of the top layer region corresponding to the location of one type of colour emitting laser. Etching is carried out for respective mask patterns, to a depth corresponding to the respective quantum well region adapted to emit light of the colour corresponding to the respective mask pattern. The resulting individual laser elements are schematically shown in Figure 9(b). Then all the individual laser elements are masked off as shown in Figure 9(c), and ion etching is carried out to separate the individual laser elements as shown in Figure 9(d). The bottom contacts are then deposited on to the laser element, such that the lower exposed barrier region of respective laser elements are contacted. Then a polyimide layer 34 is deposited over and between the individual laser elements, as shown in Figure 9(e). Then oxy-plasma etching exposes the upper laser contact as shown in Figure 9(f). Photo-resist 33 is deposited over the upper laser contacts and gold 35 is deposited over the laser contacts as shown in Figures 9(g) and 9(h). An important aspect of any display is the display luminance and its corresponding power consumption. These are calculated here below for a sub-pixel having a vertical laser cavity structure. For such a structure, the active region size is typically a 10nm quantum well having a diameter of 30 µm. Such an emitter in AlInNSb would consume approximately 1 µA , and have a resistivity at worst ∼10 -6 Ω, yielding a power consumption of approximately 1 µW . A million element display will therefore consume approximately one watt, excluding display driving circuitry. The luminance of such a structure, would be approximately 0.2 mLm based on 30% quantum efficiency at worst, and yield a worst emission of ∼0.03 mcd at a green wavelength. Typically, normal TV has a luminance of 200 cd/m 2 . Therefore, each of the million pixels in, for example, a 8 x 6 cm palm-sized colour semiconductor display screen must output 10 -6 cd, which is nearly one and a half orders of magnitude less than the 0.03 mcd expected from a vertical cavity laser. At red and blue wavelengths, between one and two orders of magnitude more emission is needed from each sub-pixel to satisfy the CIE colour response and balance. Clearly, the approximately one and a half orders extra available from the laser can satisfy this need. These calculations are for worst case values. However, if the emission was found to be deficient by one or two orders of magnitude, then use of an array of quantum dots to make up a single sub-pixel or a different, lower resistivity, semiconductor material could restore the performance requirements to those necessary for a successful screen display. In addition, as shown in Figure 10, an array of microlenses can be provided, each microlens 40 being placed over a corresponding pixel 13 in order to enhance the apparent brightness of the display. The apparent enhancement of the brightness of the display is due to the lens reducing the solid angle over which light is emitted and hence more light is projected towards the viewer. The invention is not limited to the foregoing specific embodiment, and a number of alternative structures and applications and materials are envisaged. The quantum well active layer material, for example, can be lattice matched to a GaP wafer substrate relatively easily without having to make major changes to the nitride alloy, since GaP has a similar lattice constant to Silicon. The structure of the optoelectronic devices can also be varied to increase the band-gap energy by decreasing the dimensions of the quantum confinement. This would result in the quantum wire and quantum dot structures mentioned earlier. Another type of optoelectronic device that can be used is the so-called "threshold-less laser", which would reduce the power consumption of each sub-pixel and hence result in a very low power display. Although the specific embodiment described hereinbefore relates to a full colour display, it will be evident to the skilled addressee that the complementary characteristics of the light emitting elements could be utilised to form a full colour light detector. Industrial applications of the invention include not only TV or HDTV displays, wrist watches and telephone displays or cameras, but general display/detector types and also 3-D and virtual reality displays which require fast response times. Other applications are in low power displays such as those used in portable TV's, mobile telephones or videophones. A particularly useful application for short wavelength emitters (i.e. blue or U-V) is in high density optical storage systems. The invention is also applicable to image formation in Optoelectronic Neural Network systems and pattern recognition systems. The invention being thus described, it will be obvious that the same may be varied in many ways without departure from the scope of the following claims.

Claims: An optoelectronic element (13a, b or c) formed on a substrate (7) and comprising a III-V nitride alloy, whereby said III-V nitride alloy is substantially lattice matched to the substrate, and is adapted to emit/absorb light at a desired wavelength in the range corresponding to visible light, said III-V nitride alloy comprising one of In p Al 1-p N 1-r Sb r , 0 ≤p≤1, 0<r<1, and Al a Ga 1-a N b (As c Sb 1-c ) 1-b , 0≤a≤1, 0<b<1, 0≤c≤1. An optoelectronic element as claimed in claim 1, wherein said substrate (7) comprises one of silicon and Gallium Phosphide. An optoelectronic element as claimed in claim 1, said element having an active region (5a) comprising InNSb. An optoelectronic element as claimed in claim 3, wherein said active region (5) comprises InN 1- y Sb y where y lies in the range 0.32≤y≤0.38. An optoelectronic element as claimed in claim 3 or claim 4, wherein said active region (5) comprises an active quantum well (5a) of InNSb, and barrier regions (5b, 5b) of AlNSb. An optoelectronic element as claimed in claim 5, wherein said barrier regions comprise AlN 1-x Sb x where x lies in the range 0.57≤x≤0.63. An optoelectronic element as claimed in claim 1, said element having an active region (5) comprising an active quantum well region (5a) of GaAsN and barrier regions (5b, 5b) of AlNSb. An optoelectronic element as claimed in claim 7, said active quantum well region comprising GaAs 1-z N z where z lies in the range 0.17≤z≤0.23, and said barrier regions comprising AlN 1-x Sb x where x lies in the range 0.57≤x≤0.63. An optoelectronic element as claimed in any of claims 1 to 8, wherein an emission/absorption wavelength of said element is selected by doping said active region with Al and/or quantum confining said active region. An optoelectronic element according to any of claims 1 to 9, for emitting or absorbing blue light. A colour semiconductor display/detector having a plurality of optoelectronic elements (13a, 13b, 13c) as claimed in any preceding claim, said plurality including a first element and a second element, said first and second elements being formed on and substantially lattice matched to a common said substrate (7), and being capable of emitting/absorbing light having respective different predetermined wavelengths. A colour semiconductor display/detector as claimed in claim 11, wherein the optoelectronic elements comprise quantum confinement type structures selected from the group consisting of lasers, LEDs, wires and dots. A colour semiconductor display/detector as claimed in claim 11 or claim 12, wherein said first and second optoelectronic elements each form a part of a group (13) of such elements, and are each adapted to emit/absorb light at a wavelength of a respective primary colour. A colour semiconductor display/detector as claimed in claim 13, wherein the group comprises three said optoelectronic elements (13a, 13b, 13c), each of which is adapted to emit/absorb light of a different respective primary colour, namely red, green or blue. A colour semiconductor display/detector as claimed in claim 13 or claim 14, comprising an array (14) of said groups of individual optoelectronic elements. A colour semiconductor display/detector as claimed in claim 15, wherein said array is adapted for use as a display for a TV, a computer or the like, or for use as an image detector. A colour semiconductor display/detector as claimed in any of claims 13 to 16, wherein light emitted from each individual optoelectronic element has a wavelength corresponding to that defined by the CIE chromaticity diagram for the respective primary colour emitted from that element. A colour semiconductor display/detector as claimed in any of claims 11 to 17, including processing, control and drive circuitry (VLSI) for said display/detector, said circuitry being located on said common substrate (7). A colour semiconductor display/detector as claimed in claim 18, said processing circuitry being adapted to process TV signals and drive said display/ detector in accordance therewith, thereby forming a substantially planar, thin and compact TV receiver/transmitter and display/camera. A colour semiconductor display/detector as claimed in claim 11, wherein one of said first and second optoelectronic elements is a blue light emission/absorption element. A colour semiconductor display device comprising a single substrate (7) and an array (14) of electroluminescent light emitting elements (13a, 13b, 13c) formed on and substantially lattice matched to the crystal structure of said single substrate, the elements of said array each being in the form of an optoelectronic element as claimed in any of claims 1 to 10, and said array being adapted for full colour display and comprising red, green and blue said electroluminescent elements formed of substantially similar said III-V nitride alloy compositions tuned for their respective emission wavelengths by quantum confinement incorporation and/or by doping variation. A full colour semiconductor display device as claimed in claim 21, wherein said electroluminescent elements each comprise a vertical cavity laser (5, 6) of double heterojunction configuration, said laser including a quantum confinement structure (5) having an active region (5a) between two barrier regions (5b, 5b), and first and second reflectors (6a, 6b) on opposite sides of said quantum confinement structure (5) , said vertical cavity laser being oriented with said reflectors spaced apart in a direction perpendicular to the plane of the substrate (7) so that light is emitted transverse to said plane. A full colour semiconductor display device as claimed in claim 21 or claim 22, including an array of microlenses (40) superposed over the substrate with each individual microlens formed and positioned so as to reduce the solid angle over which light emitted from a corresponding electroluminescent element (13) is projected from the device.

Inventors: BROWN ROBERT GEORGE WATLING, NAJDA STEPHEN PETER, BROWN, ROBERT GEORGE WATLING, NAJDA, STEPHEN PETER
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1994
Main classification: H01L33
IPC codes: H01S5, H01L33, H01L27