Highly water-absorptive polymers having enhanced gel strength

Abstract: There is provided a highly water-absorptive polymer composition comprising: (A) 100 parts by weight of a highly water-absorptive polymer having a crosslinked structure, comprising as its constituent a carboxyl group and/or a carboxylate group; and (B) 0.05 to 10 parts by weight of an additive selected from the group consisting of an oxalic acid (salt) compound, a sulfate of a metal selected from titanium, zirconium and vanadium, and a crystalline or noncrystalline, high-purity particulate titania having a mean particle diameter of 1 µm or less, a specific surface area of 10 m²/g or more as determined by the Brunauer-Emmett-Teller method, and, when crystalline, a crystal structure of a mixed type of rutile and anatase. There is also provided a method for producing a highly water-absorptive polymer having enhanced gel strength, which comprises treating with an alkoxytitanium a highly water-absorptive polymer having a crosslinked structure, comprising as its constituent a carboxyl group and/or a carboxylate group.

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to water-absorptive polymers having enhanced gel strength. More particularly, this invention relates to water-absorptive polymer compositions exhibiting enhanced strength and stability of a gel impregnated with water, especially with a body fluid such as urine, and a method for producing water-absorptive polymers having such excellent gel properties. Background Art In recent years, water-absorptive polymers have been practically used not only in the field of sanitary goods such as sanitary napkins and disposable paper diapers but also for a variety of industrial materials such as water-retaining materials, dew condensation-preventing materials, freshness-preserving materials and solvent-dehydrating materials. They have been put to practical use also in the fields of afforestation, agriculture and horticulture. Thus, their application is now becoming wider. Of these application fields, sanitary goods such as sanitary napkins, disposable paper diapers and pads for those who are suffering from incontinence have been improved in a feeling upon use due to improvements in the materials used, various types of gathers, and the like. Therefore, the time during which the sanitary goods can be comfortably used is becoming longer. Also, a case where the water-absorptive polymers are used under extremely severe conditions is now being increased in the fields of industrial materials, agriculture and horticulture. A water-absorptive polymer takes the form of a gel when it absorbs body fluids such as urine, menstrual blood and sweat. Such a gel deteriorates and decomposes with time and loses its strength, and, at the same time, the surface and inner part of the gel become sticky. Namely, the liquid-retaining properties of the gel become worse with time. Such problems caused by this that a liquid runs out without being absorbed in a sanitary good upon use, and that a feeling upon use of a sanitary good becomes worse with time, are becoming more serious as the time during which a sanitary good is used is now becoming longer. Reasons for the deterioration and decomposition of the gel are not fully clarified so far. It is however assumed that an extremely small amount of active impurities contained in body fluids such as urine accelerate the decomposition of a water-absorptive polymer gel in accordance with a single mechanism or a plurality of mechanisms. The degree of and the behavior in the decomposition of the polymer gel vary widely depending upon the state of the gel when a liquid is absorbed therein and individuals' differences in a body fluid. Under these circumstances, there has been demanded a water-absorptive polymer having gel properties of excellent strength and stability with time, which is always stable to body fluids such as urine regardless of individuals' differences. As a method for improving the strength and stability of a gel, it may be considered to increase the crosslinking density of a water-absorptive polymer. This method, however, entails a problem of decrease in the water absorption capacity of the polymer. Japanese Patent Kokai Publication No. 63-118375 proposes a method in which an oxygen-containing reducing inorganic salt and/or an organic antioxidant is incorporated into a polymer; Japanese Patent Kokai Publication No. 63-153060 proposes a method in which an oxidizing agent is incorporated into a polymer; Japanese Patent Kokai Publication No. 63-127754 proposes a method in which an antioxidant is incorporated into a polymer; Japanese Patent Kokai Publication No. 63-272349 proposes a method in which a sulfur-containing reducing agent is incorporated into a polymer; Japanese Patent Kokai Publication No. 63-146964 proposes a method in which a metal chelating agent is incorporated into a polymer; Japanese Patent Kokai Publication No. 63-15266 proposes a method in which a radical chain inhibitor is incorporated into a polymer; Japanese Patent Kokai Publication No. 1-275661 proposes a method in which a phosphinic acid group- or phosphonic acid group-containing amine compound or a salt thereof is incorporated into a polymer; Japanese Patent Kokai Publication No. 64-29257 proposes a method in which a polyvalent metal oxide is incorporated into a polymer; and Japanese Patent Kokai Publications Nos. 2-255804 and 3-179008 propose a method in which a water-soluble chain transfer agent is allowed to coexist when polymerization is conducted. However, all of the above-enumerated methods have problems such that the deterioration of a gel cannot be sufficiently prevented, or that an effect on preventing the deterioration of a gel is largely dependent upon individuals' differences in body fluids. Moreover, the gel strength is hardly improved when any of the above methods is employed. EP-A-0521355 discloses a process for producing water-absorptive polymers by polymerizing an acrylic monomer in the presence of a salt of a metal which may be inter alia vanadyl (II) oxalate. The resulting polymers show a very high water absorbing capacity. In view of the aforementioned situations in the prior art, an object of the present invention is to provide water-absorptive polymers which are improved both in the strength and stability of a gel after when water, in particular, a body fluid such as urine which is very different between individuals, is absorbed therein, without the water absorption capacity inherent in water-absorptive polymers being impaired. SUMMARY OF THE INVENTION The present invention provides a water-absorptive polymer composition comprising a mixture of the following components (A) and (B): (A) 100 parts by weight of a water-absorptive polymer having a crosslinked structure, comprising as its constituent a carboxyl group and/or a carboxylate group; and (B) 0.05 to 10 parts by weight, per 100 parts by weight of (A), of an oxalic acid (salt) compound selected from oxalic acid, potassium oxalate, sodium oxalate, potassium oxalate titanate, sodium oxalate titanate and ammonium oxalate titanate. According to a further aspect, the present invention provides a process for preparing such a water-absorptive polymer composition comprising the step of mixing the water-absorptive polymer with the oxalic acid (salt) compound and optionally a polyvalent metal compound. The water-absorptive polymer compositions according to the present invention are simultaneously improved in the gel strength, the stability of gel for a long time and "stickiness" on the surface of the gel, especially for the gel swollen with body fluids such as human urine or with an electrolytic solution, without the water absorption capacity inherent in water-absorptive polymers being impaired. Therefore, they can be advantageously used, in particular, in the fields of sanitary goods, and industrial, agricultural and horticultural materials for disposing strong electrolytic solutions. BRIEF DESCRIPTION OF THE DRAWINGS In the drawings, Fig. 1 is a schematic view of a device to be used to determine the rate of water absorption (under normal pressure) of a water-absorptive polymer; and Fig. 2 is a schematic view of a device to be used to determine the rate of water absorption (under pressure) of a water-absorptive polymer. Throughout the drawings, reference numeral 1 indicates a water-absorptive polymer (composition) (1 g); reference numeral 2, a support plate with a small hole; reference numeral 3, a nonwoven fabric; reference numeral 4, artificial urine; reference numeral 5, a burette; reference numeral 6, a rubber stopper; reference numerals 7 and 8, valves; reference numeral 9, an air inlet; reference numeral 10, a guide; and reference numeral 11, a weight. DETAILED DESCRIPTION OF THE INVENTION <Water-Absorptive Polymer> Any water-absorptive polymer can be used, irrespective of the type of the polymer and the polymerization method for preparing the polymer, as the water-absorptive polymer for use in the present invention, as long as it has a crosslinked structure, and comprises as its constituent a carboxyl group and/or carboxylate group. Preferable examples of such a polymer include a crosslinked polyacrylic acid salt, a crosslinked graft copolymer of starch and an acrylic acid salt, a saponified product of a crosslinked starch-acrylonitrile graft copolymer, a saponified product of a crosslinked acrylic ester-vinyl acetate copolymer, a crosslinked acrylic acid salt-acrylamide copolymer, and a saponified product of a crosslinked polyacrylonitrile. In addition to the above, polyethylene oxide crosslinked with acrylic acid, a crosslinked sodium carboxymethyl cellulose, a crosslinked copolymer of a salt of maleic anhydride and isobutylene, and a copolymer of an acrylic acid salt and a comonomer such as a maleic acid salt, an itaconic acid salt, a salt of 2-acrylamide-2-methylsulfonate, 2-acryloylethanesulfonic acid or 2-hydroxyethyl acrylate can be mentioned. The carboxylate group contained in the water-absorptive polymer may be of the type of an alkali metal salt, an alkaline earth metal salt, an ammonium salt, or the like. Of these, an alkali metal salt is preferred. The above-described water-absorptive polymer can be obtained, in general, by polymerizing a polymerizable monomer having a carboxyl group and/or a carboxylate group, such as acrylic acid (or a salt thereof) or maleic anhydride (or a salt thereof) in the presence or absence of water, a radical polymerization initiator and a crosslinking agent by a known method such as an aqueous solution polymerization method, a solution polymerization method, or a reverse-phase suspension polymerization method. For instance, the polymer can be obtained by any one of the methods described in Japanese Patent Kokoku Publication No. 60-25045, Japanese Patent Application No. 59-210198, Japanese Patent Kokai Publications Nos. 57-158210 and 57-21405, Japanese Patent Kokoku Publication No. 53-46199, and Japanese Patent Kokai Publications Nos. 58-71907, 55-84304, 56-91837, 2-49002, 61-157513 and 62-62807. The crosslinking conducted during the polymerization is the internal crosslinking of the water-absorptive polymer, and it is different from the crosslinking which will be described later in the surface treatment of the polymer in both the operation and the nature. Thus, the internal crosslinking is to uniformly crosslink the inner portion of the polymer by uniformly dispersing a crosslinking agent in the monomer or polymer either before or during the polymerization. Even when a crosslinking agent is not used, the internal crosslinking may occur due to the so-called "self-crosslinking" of polymerizable monomers initiated by heat during the polymerization. As a crosslinking agent, use may be made of a compound which has two or more double bonds in its molecule and is copolymerizable with the polymerizable monomer; or a compound which has two or more functional groups in its molecule, which groups can react with a functional group such as a carboxyl group and/or carboxylate group contained in the polymerizable monomer, during the polymerization or in the treatment after the polymerization such as drying of the polymer. Examples of a crosslinking agent of the former type include N,N-methylene-bis(meth)acrylamide, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, polypropylene glycol di(meth)acrylate, diallyl phthalate, diallyl maleate, diallyl terephthalate, triallyl cyanurate, triallyl isocyanurate and triallyl phosphate. Examples of a crosslinking agent of the latter type include ethylene glycol diglycidyl ether, polyethylene glycol glycidyl ether, and a di- or polyglycidyl ether of an aliphatic polyhydric alcohol. In addition, N-methylol acrylamide and glycidyl (meth)acrylate can be mentioned as crosslinking agents which have the functions both of the former and the latter types. When the polymerization is completed, the above-described water-absorptive polymer is, in general, obtained as a water-containing gel. This water-containing gel is usually dehydrated as it is, or by azeotropy with an inert solvent, and finally dried. The resultant is subjected, according to necessity, to pulverization, classification or the like to obtain a final product. The water-absorptive polymer for use in the present invention may be one which has undergone a surface crosslinking or modification treatment during the above-described production processes, or after the final product is obtained. Any crosslinking agent can be used for the surface crosslinking of the water-absorptive polymer as long as it has two or more functional groups which can react with a carboxyl group and/or a carboxylate group. For example, a polydiglycidyl ether compound, a haloepoxy compound, an aldehyde compound, an isocyanate compound or the like can be used as -the crosslinking agent, and a polydiglycidyl ether compound is commonly used. There is no particular limitation on the amount of the crosslinking agent used. In general, however, it is used in the range of 0.005 to 5.0% by weight based on the polymer. As an agent usable for the surface modification of the polymer, mention may be made of a silane compound represented by the following general formula: X(R) m Si(Y) 3-m wherein X represents a functional group which can react with the carboxyl group and/or the carboxylate group contained in the water-absorptive polymer, R represents a hydrocarbon group, Y represents a hydrolyzable group, and m is 0, 1 or 2. Specific examples of the silane compound having the above formula include γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane, β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, γ-(2-aminoethyl)aminopropyltrimethoxysilane, γ-(2-aminoethyl)aminopropylmethyldimethoxysilane, γ-aminopropyltriethoxysilane, N-phenyl-γ-aminopropyltrimethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, γ-chloropropyltrimethoxysilane, γ-chloropropylmethyldimethoxysilane and octadecyldimethyl[3-(trimethoxysilyl)propyl]ammonium chloride. There is no particular limitation on the amount of the above silane compound used. In general, however, it is in the range of 0.001 to 10.0% by weight based on the polymer. The mean particle diameter of the water-absorptive polymer for use in the present invention is, in general, from 10 to 2,000 µm, preferably from 50 to 1,000 µm. <Oxalic Acid (Salt) Compound> The oxalic acid (salt) compound can be used either singly or in combination of two or more. This compound is one or more of oxalic acid, potassium oxalate, sodium oxalate, potassium oxalate titanate, sodium oxalate titanate and ammonium oxalate titanate. The amount of the oxalic acid (salt) compound used varies depending upon the type, properties and mean particle diameter of the highly water-absorptive polymer used. However, in general, it is from 0.05 to 10 parts by weight, preferably from 0.1 to 5 parts by weight per 100 parts by weight of the highly water-absorptive polymer. When the oxalic acid (salt) compound is used in combination with a polyvalent metal compound as described later, the total amount of the two should fall within the above ranges. In the case where the above amount is less than 0.05 parts by weight, the intended effects cannot be sufficiently attained. On the other hand, the use of an amount in excess of 10 parts by weight will not appreciably increase the intended effects. Most of the above-described oxalic acid (salt) compounds are in the state of powder at room temperature under normal pressure. When the compound is used in the form of powder, it is preferred that the mean particle diameter thereof be as small as 10 µm or less, particularly 1 µm or less. <Polyvalent Metal Compound> The polyvalent metal compound is an oxide or a sulfate of a metal selected from silicon, titanium, zirconium and vanadium, such as silicon oxide, titanium oxide, vanadium oxide, zirconium oxide, titanium sulfate, titanyl sulfate, zirconium sulfate and vanadyl sulfate. The above polyvalent metal compound is used in such an amount that the total amount of the polyvalent metal compound and the oxalic acid (salt) compound is from 0.05 to 10 parts by weight, preferably from 0.1 to 5 parts by weight per 100 parts by weight or the highly water-absorptive polymer. The blend ratio (weight basis) of the oxalic acid (salt) compound to the polyvalent metal compound is from 10:90 to 90:10, preferably from 30:70 to 70:30. When the above polyvalent metal compound is used in the form of powder, it is preferred that the mean particle diameter of the powder be as small as 10 µm or less, particularly 1 µm or less. <Production of Water-Absorptive Polymer Composition> The water-absorptive polymer composition of the present invention may be produced in such a manner that a predetermined amount of the oxalic acid (salt) compound, or a mixture of the oxalic acid (salt) compound and the polyvalent metal compound, is added to and uniformly mixed with the highly water-absorptive polymer. The mixing may be conducted by any conventionally known method or means. It can be readily conducted by using a mixing apparatus that is usually employed for the mixing of powders, for example, a tank-type mixer having agitation elements, a fluid mixer, an air stream-type mixer, a vibrating mixer or a high-speed rotary paddle agitator. Further, as the case may be, the above additive can be added to and dispersed in the water-absorptive polymer during the step of aging, dehydration, surface modification or granulation of the polymer. The temperature at which the polymer and the additive are mixed is, in general, from room temperature to 150°C, preferably from room temperature to 50°C. The following examples further illustrate the present invention but are not intended to limit it. In the examples, the following measurements were carried out: <Water absorption capacity> 1 g of a water-absorptive polymer (composition) was placed in a 250-mesh nylon bag (10 cm × 20 cm), and immersed in 1 liter of artificial urine for 30 minutes. Thereafter, the nylon bag was withdrawn, allowed to drain for 15 minutes, and weighed. The water absorption capacity was determined, by making a blank correction, as the weight of the artificial urine absorbed in 1 g of the water-absorptive polymer (composition). The formulation of the artificial urine used is as follows: Formulation of artificial urine: Urea 1.94% Sodium chloride 0.80% Calcium chloride 0.06% Magnesium sulfate 0.11% Pure water 97.09% <Rate of water absorption (under normal pressure)> Measurement was carried out by using the device shown in Fig. 1. 1.0 g of a water-absorptive polymer (composition) 1 was placed on a nonwoven fabric 3 spread over a support plate 2 having a small hole, and brought into contact with the above-described artificial urine as shown in Fig. 1. The rate of water absorption (under normal pressure) was determined as the amount of the artificial urine absorbed in the water-absorptive polymer 1 for the first 10 minutes. <Rate of water absorption (under pressure)> Measurement was carried out by using the device shown in Fig. 2. 1.0 g of a water-absorptive polymer (composition) 1 was placed on a nonwoven fabric 3 spread over a support plate 2 having a small hole, and a guide 10 was provided around the sample polymer. A weight 11 (corresponding to 12 g/cm 2 ) was placed on the water-absorptive polymer 1. The polymer 1 was brought into contact with the above-described artificial urine as shown in Fig. 2. The rate of water absorption (under pressure) was determined as the amount of the artificial urine absorbed in the water-absorptive polymer 1 for the first 10 minutes. <Gel strength> a. 1 g of a water-absorptive polymer (composition) was impregnated with 25 g of human urine (a mixture of urines of 5 adults), and allowed to stand at 25°C for 30 minutes. The gel thus obtained was placed on a rheometer (Model "NRM-2002J" manufactured by Fudo Kogyo), and the gel strength was determined as the strength at the time when a cell penetrated into the gel. b. The procedure of the above "a" was repeated except that the human urine used in the above "a" was replaced by the same artificial urine as used in the above-described measurement of the water absorption capacity. <Stability of gel> A sample which was the same as one used in the above-described measurement of the gel strength was prepared, and allowed to stand in a thermostatic bath at a preset temperature of 40°C for 16 hours. Thereafter, the strength of the gel was measured by the above-described method to evaluate the stability of the gel. It is noted that when the data obtained from a plurality of runs are shown in the following Tables, the urine sample was changed at each run with consideration of individuals' differences in human urine. <Stickiness on gel surface> The "stickiness" of the swollen gel after the above measurement of the stability of gel was evaluated in accordance with the following standard, by touching it with fingers: ○: The swollen gel has a dry feel. Δ: The swollen gel is partially sticky. ×: The swollen gel is sticky, and the fingers are slimed. The following water-absorptive polymers were used in Examples and Comparative Examples which will be described later. Water-Absorptive Polymer (A) In a four-necked 5,000 ml round flask, equipped with a stirrer, a reflux condenser, a thermometer and a nitrogen gas supply tube was placed 1,210 g of cyclohexane. 9 g of sorbitan monostearate was added to the cyclohexane and dissolved therein, and dissolved oxygen was then expelled by blowing nitrogen gas into the flask. Separately, 143.1 g of sodium hydroxide with 95% purity dissolved in 727.7 g of water was added to 350 g of acrylic acid placed in a 2,000 ml beaker while externally cooling with ice, thereby neutralizing 70% of the carboxyl groups. In this case, the concentration of the monomer in the aqueous solution corresponds to 35% by weight, as measured for the neutralized monomer. Subsequently, 0.37 g of N,N'-methylenebisacrylamide and 0.94 g of potassium persulfate were added to the solution, and dissolved therein. Dissolved oxygen was then expelled by blowing nitrogen gas into the solution. The content of the 2000 ml beaker was added to the content of the four-necked round flask, followed by mixing under agitation. The internal temperature of the flask was raised in an oil bath while bubbling nitrogen gas. After the internal temperature reached approximately 60°C, it rose rapidly and finally reached 75°C after several tens of minutes. While the internal temperature of the flask was maintained at 60 to 65°C, reaction was carried out for 3 hours with stirring at 145 rpm. When the stirring was stopped, wet polymer particles settled down on the bottom of the round flask. These particles could be easily separated from the cyclohexane phase by decantation. The separated wet polymer was transferred into a vacuum dryer, and heated to a temperature of 90°C to remove the extraneous cyclohexane and water therefrom, whereby 400 g of a highly water-absorptive polymer was obtained as a dry powder. 100 g of the dry polymer thus obtained was placed in a 500 ml egg plant-type flask, and to this was added 122.5 g of cyclohexane to obtain a slurry. While stirring the slurry, a dispersion of 0.44 g of γ-glycidoxypropyltrimethoxysilane in 22.5 g of water was added, and the mixture was stirred at room temperature for 30 minutes. Subsequently, the flask was placed in an oil bath at a temperature of 105°C for 30 minutes. Thereafter, while the temperature of the oil bath was maintained at 105°C, the content of the flask was dried under reduced pressure. As a result, 95 g of a dry polymer was obtained. Water-Absorptive Polymer (B) The procedure for the synthesis of the water-absorptive polymer (A) was repeated except that the γ-glycidoxypropyltrimethoxysilane was replaced by 0.8 g of ethylene glycol diglycidyl ether, whereby 95 g of a dry polymer was obtained. Water-Absorptive Polymer (C) A crosslinked starch/acrylic acid salt graft polymer, "Sunwet IM-1000" manufactured by Sanyo Chemical Industries, Ltd., was used as the water-absorptive polymer (C). Water-Absorptive Polymer (D) A crosslinked polyacrylic acid salt, "Alialic CAW-4" manufactured by Nippon Shokubai Kagaku Kogyo Co., Ltd., was used as the water-absorptive polymer (D). Water-Absorptive Polymer (E) Out of 400 g of the water-absorptive polymer obtained during the synthesis of the water-absorptive polymer (A), 100 g of the polymer was taken, and added to a solution consisting of 5 g of calcium nitrate, 80 g of ethyl alcohol and 10 g of water. The mixture was stirred at 25°C for 5 minutes, and then filtered. The powder thus obtained was dried at 90°C under reduced pressure for 3 hours, whereby 95 g of a dry polymer was obtained. Examples I-1 to I-24 An oxalic acid (salt) compound was added to and uniformly mixed with each one of the above-described water-absorptive polymers (A) to (E) in a twin-cylinder mixer (Model "S-5", manufactured by Tsutsui Rikagaku Kikai Co., Ltd.) at room temperature for 30 minutes, whereby water-absorptive polymer compositions were obtained. The types and amounts of the water-absorptive polymers and of the oxalic acid (salt) compounds are as shown in Table I-1. The water-absorptive polymer compositions obtained were subjected to the above-described measurements. The results are shown in Table I-2. Comparative Examples I-1 to I-5 The above-described highly water-absorptive polymers (A), (B), (E), (C) and (D), to which no oxalic acid (salt) compound was added (Comparative Examples I-1, I-2, I-3, I-4 and I-5, respectively), were subjected to the above-described measurements. The results are shown in Table I-2. Examples II-1 to II-68 An oxalic acid (salt) compound and a polyvalent metal compound were added to and uniformly mixed with each of the above-described water-absorptive polymers (A), (B), (C) and (D) in a twin-cylinder mixer (Model "S-5", manufactured by Tsutsui Rikagaku Kikai Co., Ltd.) at room temperature for 30 minutes, whereby water-absorptive polymer compositions were obtained. The types and amounts of the water-absorptive polymers, of the oxalic acid (salt) compounds and of the polyvalent metal compounds are as shown in Table II-1. The highly water-absorptive polymer compositions obtained were subjected to the above-described measurements. The results are shown in Tables II-2 and II-3. The details of the polyvalent metal compounds shown in Table II-1 are as follows: Titania 1) : "Titanium Oxide P-25" manufactured by Nippon Aerosil Co., Ltd., having a mean particle diameter of 0.021 µm and a specific surface area of 50 m 2 /g. Titania 2) : "Taipake R-780" manufactured by Ishihara Kogyo Co., Ltd., having a mean particle diameter of 0.25 µm. Titania 3) : "Kronos KR-460" manufactured by Titan Kogyo Kabushiki Kaisha, having a mean particle diameter of 0.2 to 0.4 µm. Silica 1) : "Aerosil #380" manufactured by Nippon Aerosil Co., Ltd., having a mean particle diameter of 0.007 µm and a specific surface area of 380 m 2 /g. Silica 2) : "Silysia #770" manufactured by Fuji-Silysia Chemical, Ltd., having a mean particle diameter of 6.0 µm and a specific surface area of 700 m 2 /g. Silica 3) : "Carplex CS-500" manufactured by Shionogi & Co., Ltd., having a mean particle diameter of 2.1 µm. Zirconium oxide 1) : Zirconium oxide manufactured by Nippon Aerosil Co., Ltd., having a mean particle diameter of 0.03 µm and a specific surface area of 40 m 2 /g. Zirconium oxide 2) : Guaranteed reagent manufactured by Wako Pure Chemical Industries, Ltd. Alumina 1) : "Aluminum Oxide C" manufactured by Nippon Aerosil Co., Ltd., having a mean particle diameter of 0.013 µm and a specific surface area of 100 m 2 /g. Alumina 2) : Guaranteed reagent manufactured by Wako Pure Chemical Industries, Ltd.

Claims: A water-absorptive polymer composition comprising a mixture of the following components (A) and (B); (A) 100 parts by weight of a water-absorptive polymer having a crosslinked structure, comprising as its constituent a carboxyl group and/or a carboxylate group; and (B) 0.05 to 10 parts by weight, per 100 parts by weight of (A), of an oxalic acid (salt) compound selected from oxalic acid, potassium oxalate, sodium oxalate, potassium oxalate titanate, sodium oxalate titanate and ammonium oxalate titanate. A water-absorptive polymer composition according to Claim 1, further comprising a polyvalent metal compound which is an oxide or a sulfate of silicon, titanium, zirconium or vanadium; the total amount of the oxalic acid (salt) compound and the polyvalent metal compound being from 0.05 to 10 parts by weight per 100 parts by weight of the water-absorptive polymer, and the blend ratio (weight basis) of the oxalic acid (salt) compound to the polyvalent metal compound being from 90:10 to 10:90. A water-absorptive polymer composition according to Claim 1 or Claim 2, wherein the water-absorptive polymer is selected from a crosslinked polyacrylic acid salt, a crosslinked graft copolymer of starch and an acrylic acid salt, a hydrolyzate of a crosslinked starch-acrylonitrile graft copolymer, a hydrolyzate of a crosslinked acrylate-vinyl acetate copolymer, a crosslinked copolymer of an acrylic acid salt and acrylamide, and a hydrolyzate of a crosslinked polyacrylonitrile. A water-absorptive polymer composition according to any preceding Claim, wherein the water-absorptive polymer is one which has undergone surface-crosslinking with a crosslinking agent having two or more functional groups reactive with the carboxyl group and/or the carboxylate group. A water-absorptive polymer according to Claim 4, wherein the crosslinking agent is a polydiglycidyl ether compound. A water-absorptive polymer composition according to any of Claims 1 to 3, wherein the water-absorptive polymer is one which has undergone surface modification with a silane compound represented by the following general formula: X(R) m Si(Y) 3-m wherein X represents a functional group which can react with the carboxyl group and/or the carboxylate group in the highly water-absorptive polymer, R represents a hydrocarbon group, Y represents a hydrolyzable group, and m is 0, 1 or 2. A water-absorptive polymer composition according to Claim 6, wherein the silane compound is selected from γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane, β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, γ-(2-aminoethyl)aminopropyltrimethoxysilane, γ-(2-aminoethyl)aminopropylmethyldimethoxysilane, γ-aminopropyltriethoxysilane, N-phenyl-γ-aminopropyltrimethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, γ-chloropropyltrimethoxysilane, γ-chloropropylmethyldimethoxysilane and octadecyldimethyl[3-(trimethoxysilyl)propyl]ammonium chloride. A process for preparing a water-absorptive polymer composition as defined in any preceding Claim, comprising the step of mixing the water-absorptive polymer with the oxalic acid (salt) compound and optionally a polyvalent metal compound.

Inventors: ITO KIICHI, KITAGAWA SHOZO, NAKAMURA TOSHIKO, TANAKA MIHO, YOSHINAGA KENJI, ITO, KIICHI, KITAGAWA, SHOZO, NAKAMURA, TOSHIKO, TANAKA, MIHO, YOSHINAGA, KENJI, ITO, KIICHI, C/O MITSUBISHI PETR.CO.LTD., KITAGAWA, SHOZO, C/O MITSUBISHI PETR.CO.LTD., NAKAMURA, TOSHIKO, C/O MITSUBISHI PETR.CO.LTD., TANAKA, MIHO, C/O MITSUBISHI PETR.CO.LTD., YOSHINAGA, KENJI, C/O MITSUBISHI PETR.CO.LTD.
Applicants: MITSUBISHI CHEM CORP, MITSUBISHI CHEMICAL CORPORATION
Application year: 1994
Main classification: A61L15
IPC codes: C08K3, A61L15, C08K5