Thermal transfer image-receiving sheet

Abstract: A thermal transfer image-receiving sheet (1) comprising paper as a substrate sheet (2) and, provided on the substrate sheet in the following order, an expanded layer and a receptive layer, an undercoat layer being provided between the substrate sheet and the expanded layer. A thermal transfer image-receiving sheet comprising a substrate sheet of paper composed mainly of pulp and, provided on the substrate sheet in the following order, an expanded layer, an intermediate layer and a receptive layer, the intermediate layer having been formed by coating an aqueous coating solution.

Description: The present invention relates to a thermal transfer image-receiving sheet. More particularly, it relates to a thermal transfer image-receiving sheet having a dye-receptive layer of which the texture is similar to that of the so-called "plain paper." A thermal transfer sheet comprising a substrate sheet and a dye layer provided on one surface of the substrate sheet has hitherto been used in an output print for computers and word processors by a thermal sublimation dye transfer system. This thermal transfer sheet comprises a heat-resisting substrate sheet and a dye layer formed by coating an ink comprising a mixture of a binder with a sublimable dye on the substrate sheet and drying the resultant coating. Heat is applied to the thermal transfer sheet from the back surface thereof to transfer a number of color dots of three or four colors to a material on which an image is to be transferred, thereby forming a full color image. Since the colorant used is a dye, the image thus formed has excellent sharpness and transparency and high reproduction and gradation of intermediate colors, which enables a high-quality image comparable to the conventional full color photographic image to be formed. Such a high-quality image, however, cannot be formed on a transfer material undyable with a dye, such as plain paper. In order to solve this problem, a thermal transfer image-receiving sheet comprising a substrate sheet and a dye-receptive layer previously formed on the substrate sheet has been used in the art. EP-A-0 545 317 describes in a first aspect a thermal transfer image-receiving sheet comprising a substrate and, formed on one surface of the substrate sheet, a resin layer comprising at least a dye-receiving layer. Conventional thermal transfer image-receiving sheets are generally thick and have a dye-receptive layer of which the surface has a texture close to the so-called "photographic paper" rich in gloss, so that in some sense they can be said to give an impression of high grade. However, in the so-called "applications in office," the gloss of the surface of the dye-receptive layer and the hard texture of the sheet per se give a poor image to users. In order to overcome this problem, a thermal transfer image-receiving sheet, particularly one which has a surface having a texture close to plain paper and can be handled like copying paper, has been desired in the art. The present invention has been made under these circumstances, and an object of the present invention is to provide a thermal transfer image-receiving sheet, particularly one which particularly has a surface having a texture close to plain paper and can be handled like copying paper. An image-receiving sheet using a conventional paper substrate sheet with an image being formed thereon is comparable to a print obtained by the conventional printing in texture, such as surface gloss and thickness, and, unlike an image-receiving sheet using the conventional synthetic paper as the substrate sheet, can be bent, and a plurality of sheets thereof may be put on top of one another for bookbinding or filing, which renders the thermal transfer image-receiving sheet using paper as the substrate sheet suitable for various applications. Further, since plain paper is more inexpensive than synthetic paper, the image-receiving sheet can be produced at a lower cost. In such an image-receiving sheet, in order to compensate for the cushioning property of the substrate sheet, it is generally preferred to provide as an interposing layer a layer having a high cushioning property, for example, an expanded layer (foamed layer) comprising a resin and an expanding agent (foaming agent). However, when an expandable layer to be converted to an expanded layer is formed directly on plain paper by coating, the coating solution is unfavorably penetrated into the plain paper as the substrate sheet. This renders the resultant expandable layer so thin that the expansion of an expanding agent contained in the expandable layer provides only a low expansion ratio, which makes it difficult to impart a desired cushioning property. Further, when an expandable layer is formed on plain paper by coating an aqueous coating solution, the paper absorbs water, resulting in the occurrence of wrinkle and waviness on the paper. Accordingly, an object of the present invention is to provide such a thermal transfer image-receiving sheet that neither wrinkle nor waviness occurs at the time of forming an expandable layer, the expandable layer is highly expandable and the resultant expanded layer has a high cushioning property. Another object of the present invention is to provide a thermal transfer image-receiving sheet having excellent print quality, printing sensitivity and other properties and texture such as gloss and surface geometry comparable to paper. In order to solve the above problems, the present invention provides a thermal transfer image-receiving sheet comprising paper as a substrate sheet and, provided on said substrate sheet in the following order, an expanded layer and a receptive layer, an undercoat layer being provided between said substrate sheet and said expanded layer, said expanded layer containing microcapsules. In the thermal transfer image-receiving sheet of the present invention, an undercoat layer is first formed on a substrate sheet, and an expandable layer to be converted to an expanded layer is formed thereon by coating. By virtue of this constitution, the coating solution for an expanded layer does not penetrate into the substrate sheet and can be easily expanded, so that an expanded layer having a high cushioning property can be formed. Further, since the penetration of the coating solution for an expanded layer into paper can be prevented, it is possible to prevent the occurrence of wrinkle and waviness on the substrate sheet. Further, the provision of an intermediate layer between the expanded layer and the receptive layer is preferred for preventing the expanded layer from being collapsed by heating at the time of printing. According to the finding of the present inventors, however, when the intermediate layer is formed by coating a resin coating solution using an organic solvent, the coating solution for an intermediate layer collapses cells and voids of the expanded layer, so that a desired cushioning property cannot be attained. If an image is formed on such an image-receiving sheet, dropout or lack of uniformity in density occurs, so that no sharp image can be provided. An image is formed by the migration of a dye held in the dye layer of the thermal transfer sheet to the image-receiving sheet by heating. In this case, the collapse of the expanded layer lowers the heat insulating properties of the expanded layer, which causes the heat necessary for the transfer of the dye to be diffused towards the back surface of the image-receiving sheet. This results in a lowering in printing sensitivity. Particularly when the expandable layer is expanded with an expanding agent, such as a microsphere, the organic solvent in the intermediate layer dissolves a thermoplastic resin serving as the wall of the microsphere and consequently breaks the hollow of the microsphere, thus rendering the above phenomenon significant. The Invention Preferred embodiments of the thermal transfer image-receiving sheet according to the present invention will now be described in detail. Paper commonly used in the art may be used as the substrate sheet. The paper material for the substrate sheet is not particularly limited, and examples thereof include wood free paper, art paper, lightweight coated paper, slightly coated paper, coated paper, cast coated paper, paper impregnated with a synthetic resin or an emulsion, paper impregnated with a synthetic rubber latex, paper with a synthetic resin being internally incorporated therein and thermal transfer paper. Among them, wood free paper, lightweight coated paper, slightly coated paper, coated paper and thermal transfer paper are preferred. The coated paper and the like may be prepared by coating base paper with a resin such as an SBR latex containing calcium carbonate, talc or the like. This type of resin layer cannot be sufficiently prevent the penetration of the coating solution for an expanded layer. Although some of the resin-impregnated paper, cast coated paper and the like have water resistance imparted by the impregnation or coating treatment, they are undesirable from the viewpoint of texture and cost. When paper of the same type as used for proof reading in gravure printing, offset printing, screen printing and other various types of printing is used as the substrate sheet, trial printing may be directly carried out using the image-receiving sheet of the present invention without proof. Among others, offset printing paper and the like are designed to be dried at about 200°C, so that it is relatively resistant to heat and less likely to cause curling derived from heat wrinkle or heat shrinkage in the course of heating of the expandable layer (foamable layer) which will be described later. The thermal transfer paper too is less likely to cause curling derived from heat wrinkle and heat shrinkage in the course of heating of the expandable layer because it is designed to be heated by means of a thermal head when used. The thickness of the substrate sheet used is in the range of from 40 to 250 µm, preferably in the range of from 60 to 200 µm. When it is contemplated for the resultant thermal transfer image-receiving sheet to have a texture like plain paper, the thickness of the thermal transfer image-receiving sheet is desirably in the range of from about 80 to 200 µm. In this case, the thickness of the substrate sheet is a value obtained by subtracting the total thickness (about 30 to 80 µm) of the layers formed on the substrate sheet, such as the undercoat layer, expanded layer, intermediate layer and receptive layer, from the thickness of the thermal transfer image-receiving sheet. When the substrate sheet used has a relatively small thickness of not more than 90 µm, it is likely to wrinkle due to absorption of water. In such a case, the effect of providing an undercoat layer is significant. The colorant-receptive layer comprises a varnish composed mainly of a resin having a high dyability with a colorant and, optionally added to the varnish, various additives such as a release agent. Examples of the dyable resin include polyolefin resins, such as polypropylene, halogenated resins, such as polyvinyl chloride and polyvinylidene chloride, vinyl resins, such as polyvinyl acetate and polyacrylic esters, and copolymers thereof, polyester resins, such as polyethylene terephthalate and polybutylene terephthalate, polystyrene resins, polyamide resins, copolymer resins comprising olefins, such as ethylene or propylene, and other vinyl monomers, ionomers and cellulose derivatives. They may be used alone or in the form of a mixture of two or more. Among them, polyester resins and vinyl resins are particularly preferred. Further, any composite of the above resins may also be used. It is also possible to incorporate a release agent into the colorant-receptive layer for the purpose of preventing the colorant-receptive layer being fused to a thermal transfer sheet at the time of formation of an image. Silicone oils, phosphoric ester plasticizers and fluorocompounds may be used as the release agent. Among them, silicone oils are preferred. Preferred examples of the silicone oils include modified silicone oils such as epoxy-modified, alkyl-modified, amino-modified, carboxyl-modified, alcohol-modified, fluorine-modified, alkylaralkyl-polyether-modified, epoxy-polyether-modified and polyether-modified silicone oils. Among others, a product of a reaction of a vinyl-modified silicone oil with a hydrogen-modified silicone oil provides goods results. The amount of the release agent added is preferably in the range of from 0.2 to 30 parts by weight based on the resin for forming the receptive layer. The colorant-receptive layer and other layers described below may be formed by roll coating, bar coating, gravure coating, gravure reverse coating and other conventional coating methods. The coverage of the colorant-receptive layer is preferably in the range of from 1.0 to 10 g/m 2 (on a solid basis; the coverage in the present invention being hereinafter on a solid basis unless otherwise specified). In the present invention, an undercoat layer is formed on the substrate sheet. By virtue of the provision of the undercoat layer, even when a coating solution for an expanded layer (foamed layer) is coated on the substrate sheet, the coating solution does not penetrate into the substrate sheet, so that an expandable layer having a desired thickness can be formed. Further, the expansion ratio in the expansion of the expandable layer by heating can be increased, which contributes to an improvement in cushioning property of the whole image-receiving sheet and, at the same time, is cost-effective because the amount of the coating solution necessary for the formation of an expanded layer having a desired thickness can be reduced. Resins usable as the undercoat layer include acrylic resins, polyurethane resins, polyester resins and polyolefin resins and modification products of the above resins. In the present invention, paper is used as the substrate sheet. Therefore, when an aqueous coating solution for an undercoat layer is coated directly on the paper as the substrate sheet, a wrinkle or waviness occurs due to uneven water absorption of the surface of the substrate sheet, which often has an adverse effect of the texture or print quality. This tendency is particularly significant when the substrate sheet used has a small thickness of not more than 100 µm. For this reason, the coating solution for an undercoat layer is preferably not aqueous but a coating solution in the form of a solution or a dispersion of the resin in an organic solvent. Organic solvents usable for this purpose include toluene, methyl ethyl ketone, isopropanol, ethyl acetate, butanol and other general industrial organic solvents. Further, extenders, such as talc, calcium carbonate, titanium oxide and barium sulfate, may be added to improve the coatability of the coating solution for an undercoat layer, improve the adhesion of the undercoat layer to the substrate sheet and the expanded layer (particularly when an aqueous expanding agent is used in the formation of the expanded layer) or impart whiteness. The coverage of the undercoat layer is preferably in the range of from 1 to 20 g/m 2 . When it is less than 1 g/m 2 , no contemplated effect as the undercoat layer can be attained. On the other hand, when it exceeds 20 g/m 2 , the effect is saturated and the large coverage effects the texture of the substrate to cause a texture like a synthetic resin sheet. This is also cost-uneffective. An expanded layer comprising a resin and an expanding agent (foaming agent) is formed on the undercoat layer. The cushioning property of the expanded layer is so high that a thermal transfer image-receiving sheet having a high printing sensitivity can be provided even when paper is used as the substrate sheet. Conventional resins, such as urethane resins, acrylic resins, methacrylic resins and modified olefin resins, or blends of the above resins may be used as a resin for constituting the expanded layer. A solution and/or a dispersion of the above resin in an organic solvent or water is coated to form an expandable layer. The coating solution for an expanded layer is preferably an aqueous coating solution which does not have any effect on the expanding agent, and examples of the coating solution include coating solutions using water-soluble or water-dispersible resins, SBR latex, emulsions, such as a urethane emulsion, a polyester emulsion, an emulsion of vinyl acetate or a copolymer thereof, an emulsion of acryl or a copolymer of acryl, such as acrylstyrene, and a vinyl chloride emulsion, or dispersions thereof. When a microsphere described below is used as the expanding agent, it is preferred to use an emulsion of vinyl acetate or a copolymer thereof, or an emulsion of acryl or a copolymer of acryl, such as acrylstyrene, among the above resins. Since the glass transition point, flexibility and film formability can be easily controlled as desired by varying the kind and ratio of monomers to be copolymerized, these resins are advantageous in that desired properties can be obtained without the addition of any plasticizer or film forming aid and the resultant film is less likely to cause a change in color during storage under various environments and less likely to cause a change in properties with the lapse of time. Further, among the above resins, SBR latex is not generally preferably used because it has a low glass transition point and is likely to cause blocking and the resultant film is likely to cause yellowing after the formation thereof during storage. The urethane emulsion is not preferably used because in many cases it contains solvents, such as NMP and DMF, which are likely to have an adverse effect on the expanding agent. Further, the emulsion or dispersion of a polyester and the vinyl chloride emulsion are not preferably used because they generally have a high glass transition point and hence deteriorate the expandability of the microsphere. Although some of them are flexible, they too are not preferably used because the flexibility is imparted by the addition of a plasticizer. The expanding property of the expanding agent is greatly influenced by the hardness of the resin. In order to attain a desired expansion ratio, the resin preferably has a glass transition point in the range of from -30 to 20°C or a minimum film forming temperature of 20°C or below. When the glass transition point is above 20°C, the flexibility is so low that the expanding property of the expanding agent is lowered. On the other hand, when the glass transition point is below -30°C, unfavorable phenomena often occur such as blocking (between the expanded layer and the back surface of the substrate sheet at the time of taking up the substrate sheet after the formation of the expanded layer) due to the tackiness of the resin and unsatisfactory cutting of the thermal transfer image-receiving sheet (occurrence of phenomena such as a deterioration in appearance of the thermal transfer image-receiving sheet due to sticking of the resin of the expanded layer to the cutting edge of a cutter or a deviation in cutting dimension at the time of cutting of the image-receiving sheet). When the minimum film forming temperature is above 20°C, a failure to form a film occurs during coating or drying, which results in occurrence of unfavorable phenomena such as surface cracking. Examples of the expanding agent (foaming agent) include conventional expanding agents, such as decomposable expanding agents, which decompose on heating to evolve oxygen, carbon dioxide gas, nitrogen or other gases, such as dinitropentamethylenetetramine, diazoaminobenzene, azobisisobutyronitrile or azodicarbonamide, or microspheres prepared by enmicrocapsulating a low-boiling liquid, such as butane or pentane, in a resin, such as polyvinylidene chloride or polyacrylonitrile. Among them, a microsphere prepared by enmicrocapsulating a low-boiling organic solvent, such as butane or pentane, in a thermoplastic resin, such as polyvinylidene chloride or polyacrylonitrile, is preferred. These expanding agents expands on heating after the formation of an expandable layer, and the resultant expanded layer has high cushioning property and heat insulating properties. The amount of the expanding agent used is preferably in the range of from 1 to 150 parts by weight, still preferably in the range of from 5 to 50 parts by weight, based on 100 parts by weight of the resin for forming the expanded layer. When it is less than 1 part by weight, the cushioning property of the expanded layer is so low that the effect of forming the expanded layer is lowered. On the other hand, when it exceeds 150 parts by weight, the percentage hollow after the expansion becomes so high that the mechanical strength of the expanded layer is lowered, which is disadvantageous in ordinary handling. Further, the surface of the expanded layer loses its smoothness, which is likely to have an adverse effect on the appearance and print quality. The thickness of the whole expanded layer is preferably in the range of from 30 to 100 µm. When it is less than 30 µm, the cushioning property and the heat insulating property become unsatisfactory. On the other hand, when it exceeds 100 µm, the effect of the expanded layer cannot be improved and the strength is unfavorably lowered. The expanding agent is preferably such that the volume average particle diameter before expansion is in the range of from about 5 to 15 µm and the particle diameter after expansion is in the range of from 20 to 50 µm. When the volume average particle diameter before expansion is less than 5 µm and the particle diameter after expansion is less than 20 µm, the cushioning effect is low. On the other hand, when the volume average particle diameter before expansion exceeds 15 µm and the particle diameter after expansion is in the range of from 20 to 50 µm or more, the surface of the expanded layer becomes uneven, which unfavorably has an adverse effect on the quality of the formed image. The expanding agent is particularly preferably such a low temperature expanding microsphere that the softening temperature of the wall and the expansion initiation temperature are each 100°C or below and the optimal expansion temperature (the temperature at which the highest expansion ratio is obtained with the heating time being 1 min) is 140°C or below. In this case, the expansion is preferably carried out at as low a heating temperature as possible. The use of a microsphere having a low expansion temperature prevents the substrate sheet from wrinkling or curling on heating at the time of expansion. The microsphere having a low expansion temperature can be prepared by regulating the amount of the thermoplastic resin incorporated for forming the wall of the microcapsule, such as polyvinylidene chloride or polyacrylonitrile. The volume average particle diameter of the microsphere is in the range of from 5 to 15 µm. The expanded layer formed using the above microsphere has advantages including that cells formed by the expansion are closed cells, the expansion can be carried out by simply heating the expandable layer and the thickness of the expanded layer can be easily controlled as desired by varying the amount of the microsphere incorporated. The microsphere, however, is less resistant to organic solvents, and the use of a coating solution containing an organic solvent for the formation of an expanded layer causes the wall of the microsphere to be attacked by the organic solvent, which lowers the expanding property. For this reason, when the microsphere of the type described above is used, it is preferred to use an aqueous coating solution not containing such an organic solvent as will attack the wall, for example, ketones, such as acetone and methyl ethyl ketone, esters such as ethyl acetate, and lower alcohols, such as methanol and ethanol. Therefore, the use of an aqueous coating solution, specifically a coating solution using a water-soluble or water-dispersible resin, an emulsion of a resin, preferably an acrylstyrene emulsion or a modified vinyl acetate emulsion, is preferred. Further, even when an expandable layer is formed using an aqueous coating solution, the addition of a high-boiling, high-polar solvent, for example, a co-solvent or film forming aid or a plasticizer, such as NMP, DMF or cellosolve, to the coating solution affects the microsphere, so that the composition of the aqueous resin used and the amount of the high-boiling solvent added should be properly selected by confirming that they do not have an adverse effect on the microcapsule. The expansion of the expanding agent contained in the expandable layer often causes a roughness in the order of several tens µm, and the surface of the receptive layer formed thereon also becomes uneven. Even though an image is formed on such a thermal transfer image-receiving sheet, the occurrence of dropouts and voids in the formed image is significant and an image having high sharpness and definition cannot be formed. In order to solve this problem, proposals have been made such as a method wherein a smoothening treatment is carried out by calendering with heating and pressing and other methods, a method wherein a large amount of a resin is coated on the expanded layer to smoothen the surface of the expanded layer and a method which comprises forming on a releasable substrate sheet a receptive layer and an expanded layer in that order, laminating the resultant laminate onto a separately provided substrate sheet and peeling off the releasable substrate sheet alone to form an image-receiving sheet. All the above methods, however, are not favorable because the number of process steps should be increased, a large amount of resin coating is necessary, or other members should be additionally used. A good method for eliminating the problem associated with the uneven surface of the expanded layer is to provide on the expanded layer an intermediate layer comprising a flexible and elastic material. By virtue of the provision of the intermediate layer, a thermal transfer image-receiving sheet, which does not affect the print quality, can be provided even when the surface of the receptive layer is uneven. The intermediate layer comprises a resin having excellent flexibility and elasticity, specifically a urethane resin, a vinyl acetate resin, an acrylic resin, a copolymer of the above resins or a blend of the above resins. Even when the above resin is used, the glass transition temperature is preferably in the range of from -30 to 20°C. When the glass transition temperature is below -30°C, the tackiness is so large that blocking (between the intermediate layer and the back surface of the substrate sheet) or unfavorable phenomena at the time of cutting of the thermal transfer image-receiving sheet occurs. On the other hand, when the glass transition temperature is above 20°C, the flexibility is so low that the above object cannot be attained. If the coating solution for a receptive layer is a coating solution using an organic solvent, coating of the coating solution on the expanded layer causes the expanded layer to be attacked by the organic solvent, so that a cushioning property and other effects cannot be often attained by the expanded layer. This problem can be solved by forming an intermediate layer using an aqueous coating solution between the expanded layer and the receptive layer. The aqueous coating solution does not contain organic solvents, for example, ketones, such as acetone and methyl ethyl ketone, esters such as ethyl acetate, and lower alcohols, such as methanol and ethanol. More specifically, the use of a coating solution using a water-soluble or water-dispersible resin, an emulsion of a resin, preferably an acrylic resin and/or acryl copolymer, is preferred. The intermediate layer or the expanded layer may further comprise calcium carbonate, talc, kaolin, titanium oxide, zinc oxide and other conventional inorganic pigments and brightening agents for the purpose of imparting shielding properties and whiteness and regulating the texture of the thermal transfer image-receiving sheet. The amount of these optional additives is preferably in the range of from 10 to 200 parts by weight based on 100 parts by weight of the resin (on a solid basis). When it is less than 10 parts by weight, the effect is unsatisfactory. On the other hand, when it exceeds 200 parts by weight, the dispersion stability is poor and the resin performance cannot often be attained. The coverage of the intermediate layer is preferably in the range of from 1 to 20 g/m 2 . When the coverage is less than 1 g/m 2 , the function of protecting the cells cannot be sufficiently exhibited. On the other hand, when it exceeds 20 g/m 2 , the heating insulating property, cushioning property and other properties of the expanded layer cannot be exhibited. When the substrate sheet according to the present invention is used, if a plurality of resin layers are formed on the substrate sheet on the side of the receptive layer with the substrate sheet, such as plain paper, being exposed as such on the side of the back surface, the thermal transfer image-receiving sheet is likely to curl due to environmental moisture and temperature. For this reason, it is preferred to provide a curl preventive layer composed mainly of a resin having a water retaining property, such as polyvinyl alcohol or polyethylene glycol, on the back surface of the substrate sheet. Further, it is also possible to provide a back surface layer having lubricity in the image-receiving sheet on its surface remote from the colorant-receptive layer according to a conveying system for the image-receiving sheet in a printer used. In order to impart the lubricity to the back surface layer, an inorganic or organic filler may be dispersed in the resin of the back surface layer. Examples of the resin used in the back surface layer having lubricity include conventional resins or a blend of the conventional resins. Furthermore, a lubricating agent, such as a silicone oil, or a release agent may be added to the back surface layer. The coverage of the back surface layer is preferably in the range of from 0.05 to 3 g/m 2 . Thermal transfer sheets usable in thermal transfer, which is carried out using the above thermal transfer image-receiving sheet, include, beside a sublimation dye thermal transfer sheet used in the sublimation dye transfer recording system, a hot-melt thermal transfer sheet wherein a hot-melt ink layer comprising a hot-melt binder bearing a pigment is formed on the a substrate sheet by coating and the ink layer is transferred by heating to a material on which an image is to be formed. Means for applying a thermal energy in the thermal transfer may be any conventional device. For example, an image can be formed by applying a thermal energy of about 5 to 100 mJ/mm 2 through the control of a recording time by means of a recording device, such as a thermal printer (for example, a video printer VY-100 manufactured by Hitachi, Limited). The present invention will now be described in more detail with reference to the following examples and comparative examples. Example B1 A coated paper having a basis weight of 104.7 g/m 2 (Mitsubishi New V Matt Kote manufactured by Mitsubishi Paper Mills Limited) was provided as a substrate sheet, and a coating solution having the following composition for an undercoat layer was gravure-coated on the substrate sheet at a coverage of 5 g/m 2 (weight on a dry basis; the same shall apply hereinafter). The resultant coating was dried by a hot-air drier to form an undercoat layer. Units for expressing the composition are parts by weight unless otherwise specified. Coating solution for undercoat layer Polyester resin (V600 manufactured by Toyobo Co., Ltd.) 100 parts Methyl ethyl ketone/toluene = 1/1 200 parts Then, a coating solution having the following composition for an expanded layer was gravure-coated on the undercoat layer at a coverage of 20 g/m 2 . Thereafter, the resultant coating was dried and heated at 140°C for 1 min by a hot-air drier to expand the microsphere. Coating solution for expanded layer EVA Emulsion (XB3647B manufactured by Tohpe Corporation) 100 parts Microsphere (551WU20 manufactured by Expancel; expansion initiation temp. = 99-104°C) 20 parts Water 20 parts Then, a coating solution having the following composition for an intermediate layer was gravure-coated on the expanded layer at a coverage of 5 g/m 2 . Thereafter, the resultant coating was dried by a hot-air drier. Coating solution for intermediate layer Acrylic/styrene emulsion (RX832A manufactured by Nippon Carbide Industries Co., Ltd.) 100 parts Water 20 parts Then, a coating solution having the following composition for a receptive layer was gravure-coated on the intermediate layer at a coverage of 3 g/m 2 . Thereafter, the resultant coating was dried by a hot-air drier. Coating solution for receptive layer Vinyl chloride/vinyl acetate copolymer (#1000D manufactured by Denki Kagaku Kogyo K.K.) 100 parts Amino-modified silicone (X-22-349 manufactured by The Shin-Etsu Chemical Co., Ltd.) 3 parts Epoxy-modified silicone (KF-393 manufactured by The Shin-Etsu Chemical Co., Ltd.) 3 parts Methyl ethyl ketone/toluene = 1/1) 400 parts A coating solution having the following composition for a back surface layer was gravure-coated on the substrate sheet on its side remote from the receptive layer at a coverage of 0.05 g/m 2 . Thereafter, the resultant coating was dried by means of a cold-air drier, thereby preparing the thermal transfer image-receiving sheet of Example B1. Coating solution for back surface layer Polyvinyl alcohol (PVA124 manufactured by Kuraray Co., Ltd.) 2 parts Water 100 parts Example B2 A thermal transfer image-receiving sheet of Example B2 was prepared in the same manner as in Example B1, except that a coated paper having a basis weight of 127.9 g/m 2 (OK Coat manufactured by New Oji Paper Co., Ltd.) was provided as a substrate sheet, and the compositions of the undercoat layer, expanded layer and intermediate layer were varied as follows. Coating solution for undercoat layer Acrylic resin (EM manufactured by Soken Chemical Engineering Co., Ltd.) 100 parts Precipitated barium sulfate (#300 manufactured by Sakai Chemical Co., Ltd.) 30 parts Toluene 400 parts Expanded layer Styrene acrylic emulsion (RX941A manufactured by Nippon Carbide Industries Co., Ltd.) 100 parts Microsphere (F30VS manufactured by Matsumoto Yushi Kagaku K.K., expansion initiation temp. = 80°C) 10 parts Water 20 parts Coating solution for intermediate layer Acrylic emulsion (FX337C manufactured by Nippon Carbide Industries Co., Ltd.) 100 parts Water 20 parts Example B3 A thermal transfer image-receiving sheet of Example B3 was prepared in the same manner as in Example B1, except that a thermal transfer paper having a basis weight of 79.1 g/m 2 (TTR-T manufactured by Mitsubishi Paper Mills, Ltd.) was provided as a substrate sheet, and the compositions of the undercoat layer, expanded layer and intermediate layer were varied as follows. Coating solution for undercoat layer Urethane resin (NL2371M30 manufactured by Mitsui Toatsu Chemicals, Inc.) 100 parts Titanium oxide (TCA888 manufactured by Tohchem Products Corporation) 30 parts Ethyl acetate 100 parts Dimethylformamide 20 parts Isopropanol 300 parts Coating solution for expanded layer Acrylic emulsion (AE312 manufactured by Japan Synthetic Chemicals, Inc.) 100 parts Microsphere (F30SS manufactured by Matsumoto Yushi Kagaku K.K., Japan; expansion initiation temp. = 80°C) 15 parts Water 20 parts Coating solution for intermediate layer Styrene/acrylic emulsion (XA4270C manufactured by Tohpe Corporation) 100 parts Titanium oxide (TT-055 (A) manufactured by Ishihara Sangyo Kaisha Ltd.) 50 parts Water 30 parts Example B4 A thermal transfer image-receiving sheet of Example B4 was prepared in the same manner as in Example B1, except that 551WU manufactured by Expancel (expansion initiation temp. = 99-104°C) was used instead of the microsphere contained in the expanded layer in Example B1. Example B5 A thermal transfer image-receiving sheet of Example B5 was prepared in the same manner as in Example B2, except that the composition of the undercoat layer in Example B2 was varied as follows. Coating solution for undercoat layer Acrylic emulsion (AE932 manufactured by Japan Synthetic Chemicals, Inc.) 100 parts Water 20 parts Comparative Example B1 A thermal transfer image-receiving sheet of Comparative Example B1 was prepared in the same manner as in Example B1, except that the formation of the undercoat layer was omitted. Comparative Example B2 A thermal transfer image-receiving sheet of Comparative Example B2 was prepared in the same manner as in Example B2, except that the formation of the undercoat layer and the intermediate layer was omitted. Comparative Example B3 A thermal transfer image-receiving sheet of Comparative Example B3 was prepared in the same manner as in Example B3, except that the formation of the undercoat layer and back surface layer was omitted. Comparative Example B4 A thermal transfer image-receiving sheet of Comparative Example B4 was prepared in the same manner as in Example B4, except that the formation of the undercoat layer and expanded layer was omitted. The results of evaluation for the thermal transfer image-receiving sheets of Examples B1 to B5 and Comparative Examples B1 to B4 are given in Table B1. The evaluation was carried out by the following methods. 1) Thickness of expanded layer The section of the thermal transfer image-receiving sheet was observed using a photomicrograph thereof to measure the thickness of the expanded layer (unit: µm). 2) Wrinkle and waviness of substrate sheet The wrinkle and waviness of the substrate sheet were evaluated by visually inspecting the thermal transfer image-receiving sheet. ○ Good Δ Somewhat wrinkle and waviness observed x Significant wrinkle and waviness observed 3) Surface texture The surface texture was evaluated by visually inspecting the thermal transfer image-receiving sheet. ○ Natural matte feeling like plain paper Δ Somewhat glossy x Highly glossy, and different in texture from plain paper 4) Environmental curling The thermal transfer image-receiving sheet was cut into a 10-cm square form. The cut sheets were allowed to stand on a floor with 1 ○ the surface of the receptive layer facing upward for one sheet and 2 ○ the surface of the receptive layer facing downward for another sheet in two types of environments, that is, an environment of a temperature of 20°C and a humidity of 30% for 2 hr and an environment of a temperature of 40°C and a humidity of 90% for 2 hr. Thereafter, the height from the floor was measured with respect to four corners of the thermal transfer image-receiving sheet, and the average of the measured values was calculated. ○ Not more than 10 mm in both environments for both sheets 1 ○ and 2 ○ X Not less than 10 mm in either or both environments for either or both sheets 1 ○ and 2 ○ 5) Quality of print A solid image of 64/256 gradation for each of four colors of yellow, magenta, cyan and black was formed on the thermal transfer image-receiving sheet by using a sublimation'dye transfer printer PHOTOMAKER manufactured by Seiko Instruments Inc. and a sublimation dye transfer sheet CH743, and the resultant print was evaluated by visual inspection. ○ Good quality with dropout and lack of uniformity being unobserved Δ Somewhat unsatisfactory X Remarkable dropout and lack of uniformity 6) Printing sensitivity A solid image of 256/256 gradation for magenta was formed on the thermal transfer image-receiving sheet by using the above printer and transfer sheet, and the reflection density was measured with a Macbeth densitometer RD-918. O : Reflection density of not less than 1.7 Δ: Reflection density of 1.5 to less than 1.7 X: Reflection density of less than 1.5 Samples Thickness of expanded layer Wrinkle etc. Surface texture Environmental curling Quality of print Printing sensitivity Ex. B1 70 ○ ○ ○ ○ ○ Ex. B2 65 ○ ○ ○ ○ ○ Ex. B3 80 ○ ○ ○ ○ ○ Ex. B4 65 ○ ○ ○ ○ ○ Ex. B5 65 Δ ○ ○ ○ ○ Comp. Ex. B1 45 X ○ ○ Δ Δ Comp. Ex. B2 40 X Δ ○ X X Comp. Ex. B3 45 X ○ X Δ Δ Comp. Ex. B4 - ○ X ○ X X In the thermal transfer image-receiving sheet of the present invention, an undercoat layer is first formed on a substrate sheet, and an expanded layer is formed thereon by coating. By virtue of this constitution, the coating solution for an expanded layer does not penetrate into the substrate sheet and can be easily expanded, so that an expanded layer having a high cushioning property can be formed. Further, since the penetration of the coating solution for an expanded layer into paper is prevented, it is possible to prevent the occurrence of wrinkle and waviness on the substrate sheet. Furthermore, the functions of the undercoat layer, expanded layer and intermediate layer enable a thermal transfer image-receiving sheet having excellent print quality, printing sensitivity and other properties and paper-like texture in respect of gloss, surface geometry and the like to be provided even when ordinary paper is used as the substrate sheet.

Claims: A thermal transfer image-receiving sheet comprising paper as a substrate sheet and, provided on said substrate in the following order, an expanded layer and a receptive layer, an undercoat layer being provided between said substrate sheet and said expanded layer, said expanded layer containing microcapsules. The thermal transfer image-receiving sheet according to claim 1, wherein said undercoat layer further comprises a pigment. The thermal transfer image-receiving sheet according to claim 1 or 2, wherein the cell diameter of said expanded layer is in the range of from 20 to 50 µm. The thermal transfer image-receiving sheet according to anyone of claims 1 to 3, wherein said expanded layer contains microcapsules comprising a low-boiling organic solvent surrounded by the wall of a thermoplastic resin. The thermal transfer image-receiving sheet according to anyone of claims 1 to 4, wherein said expanded layer has a thickness in the range of from 30 to 100 µm. The thermal transfer image-receiving sheet according to anyone of claims 1 to 5, which further comprises a curl preventive layer on the other surface of said substrate sheet. A process for producing a thermal transfer image-receiving sheet according to anyone of claims 1 to 6, wherein the undercoat layer is formed by coating a coating solution comprising a resin and an organic liquid. A process for producing a thermal transfer image-receiving sheet according to anyone of claims 1 to 6, wherein the expanded layer is formed by coating an aqueous coating solution. Use of a thermal transfer image-receiving sheet according to anyone of claims 1 to 6 for proof printing.

Inventors: IMOTO KAZUNOBU, KAMIKUBO YOSHINORI, NARITA SATOSHI, UENO TAKESHI, IMOTO, KAZUNOBU, KAMIKUBO, YOSHINORI, NARITA, SATOSHI, UENO, TAKESHI, IMOTO, KAZUNOBU, C/O DAI NIPPON PRINTING CO., LTD., Kamikubo, Yoshinori, Dai Nippon Printing Co., Ltd., NARITA, SATOSHI, C/O DAI NIPPON PRINTING CO., LTD., UENO, TAKESHI, C/O DAI NIPPON PRINTING CO., LTD.
Applicants: DAINIPPON PRINTING CO LTD, DAI NIPPON PRINTING CO., LTD.
Application year: 1994
Main classification: B41M5
IPC codes: B41M5