LITHIATED MANGANESE OXIDE

Abstract: Lithium manganese ternary oxide Li Mn2 O4+x is produced, where 0 </= x </= 0.2, by adding carbon to a manganese-containing solution such as manganese acetate and reacting the solution in an inert atmosphere with a lithium-containing compound such as lithium hydroxide and ammonia. Carbon is added in a proportion up to 8 percent of the weight of the Li Mn2 O4+x produced, and preferably the proportion of carbon added is in the range 2 to 6 percent by weight of Li Mn2 O4+x. The carbon is preferably carbon powder such as carbon black. Preferably, the Li Mn2 O4+x produced as a gelatinous precipitate is dried and heat treated. Alternatively, lithium manganese ternary oxide Li Mn2 O4+x is produced by reacting a manganese-containing compound with lithium carbonate. The reaction takes place in water and a precipitate is formed which is dried. The dried precipitate may be heat treated. The manganese-containing compound comprises manganese acetate. Carbon such as carbon powder may be added to the mixture before the reaction occurs.

Description: ITHIATED MANGANESE OXIDE This invention relates to a method for the preparation of lithium manganese oxide which is used as an intercalation compound in secondary batteries. A low temperature method for the preparation of lithiated manganese oxide LiMn 2 0 4 is described in US 5135732 in which solutions of manganese acetate and hydroxides of lithium and ammonium are reacted in amounts sufficient to yield the stoichiometric phase of LiMn 2 0 4 . The reaction is conducted in an inert atmosphere and results in a gelatinous precipitate which is dried to produce a pure LiMn 2 0 4 phase with a small grain size. An object of the present invention is to provide an improved method for the preparation of lithium manganese oxide, and a method of producing lithium manganese oxide which gives improved performance in secondary batteries. According to one aspect, the invention consists of adding carbon to a manganese-containing solution prior to reacting said solution with a lithium-containing compound in an inert atmosphere to produce LiMn 2 0 4+x , where 0 ≤ x ≤ 0.2. Preferably, the carbon takes the form of powder, such as carbon black, and is present in a proportion up to 8 per cent by weight of the LiMn 2 0 4+x produced; preferably, in the range 2 to 6 per cent by weight, with an optimum level of substantially 4 per cent by weight. A lithium manganese oxide prepared by this method gives improved performance when used in the cathode of a secondary battery, especially in regard to the rate of decline of battery capacity with repeated charge/discharge cycling. According to a second aspect, the invention consists in reacting a manganese-containing compound with a lithium carbonate to produce LiMn 2 0 4+x , where 0 ≤ x ≤ 0.2. Preferably, lithium carbonate Li 2 C0 3 is reacted with manganese acetate (CH 3 C0 2 ) 2 Mn.4H 2 0 to produce the LiMn 2 0 4+x as a precipitate, which is then dried. Carbon may be added to the solution to improve the performance of the LiMn 2 0 4+ -. when used in batteries. This method of preparation does not involve the need for an inert atmosphere, and thus it is easier to implement than the prior art method of US 5135732. The invention will now be described by way of example with reference to the accompanying drawings in which: Figure 1 is a graph showing the variation of the specific discharge capacity of a battery with repeated charge/discharge cycling, the cathode of the battery incorporating LiMn 2 0 4+x which in curve I, is prepared according to a first method of the invention, and in curve II is prepared according to the prior art method of US 5135732; Figure 2 is a graph showing the variation of the specific discharge capacity of a battery with repeated charge/discharge cycling, the cathode of the battery incorporating LiMn 2 0 4+x prepared according to the first method of the invention but with different proportions by weight of carbon in different samples; Figure 3 is a graph showing the variation of the specific discharge capacity of a secondary battery with repeated charge/discharge cycling, the cathode of the battery incorporating LiMn 2 0 4+x which in curve I, is prepared according to a second method of the invention, and in curve II is prepared according to the prior art method of US 5135732; and Figure 2 is a graph showing the variation of the specific discharge capacity of a secondary battery with repeated charge/discharge cycling, the cathode of the battery incorporating LiMn 2 0 4+ -; which in curve I, is prepared according to the second method of the invention but without carbon, and in curve II is prepared according to the second method of the invention but with carbon. In the first method of the invention, 0.3 grams of carbon black was added to 100 millilitres of manganese acetate solution (CH 3 C0 2 ) 2 Mn.4H 2 0 and stirred by bubbling argon through it. A measure of 40 millilitres of a solution of lithium hydroxide LiOH.H 2 0 and ammonia NH 4 0H was added to the manganese acetate solution and stirred vigorously by bubbling argon through it for half an hour, thereby producing a gelatinous precipitate. The manganese acetate solution was a 0.8 Mol solution (Aldrich 99+%), and the lithium hydroxide and ammonia solution comprised 1 Mol LiOH (Aldrich 99.9%) and 3 Mol NH 4 OH (33% solution). Water was removed from the gelatinous precipitate using a rotary evaporator operating at 85°C so as to produce a xerogel. The xerogel was then further dried at 60-80°C under a dynamic vacuum for 2 hours in order to ease removal of the xerogel from the vessel in which it was prepared. Finally, 2 grams of the xerogel were packed in a 25 millilitre alumina crucible and heated in air at 300°C for 48 hours. Following this heat treatment the xerogel takes the form of lithium manganese oxide spinel LiMn 2 0 4+x , where 0 ≤ x < 0.2. The heat treatment can be effected in the temperature range 200°C to 700°C. The performance of the LiMn 2 0 + -. was tested by incorporation in the cathode of a battery. A dry mixture of LiMn0 2 0 4+x (80% by weight), carbon (13.3% by weight) and polytetrafluoroethylene (6.7% by weight) was compressed on a nickel mesh grid to produce a cathode with an area of 0.9 cm 2 containing 12 milligrams of the mixture. This cathode was incorporated into a battery with a lithium anode and electrolyte of lithium hexafluoroarsenate and propylene carbonate LiAsF 6 /PC. This battery was subject to a charging/discharging cycling test and its specific discharge capacity measured for various cycles during the test. The test employed cut-off potentials of 3.7 volts and 2 volts and a discharge current of 440 microamps. The test results are shown in Figure 1 as curve I, and are compared with the test results (curve II) for a similar battery incorporating LiMn 2 0 4+x prepared by a similar process to that described above, but without the carbon black, i.e. LiMn 2 0 4+x prepared according to the prior art method of US 5135732. Curve 1 in Figure 1 shows that the battery with the cathode formed from LiMn 2 0 4+x prepared using carbon, has a lower rate of decline of specific discharge capacity, than that of the battery with a cathode incorporating LiMn 2 0 4+x prepared without using carbon (curve II). In order to investigate the effect of using different amounts of carbon in preparing the LiMh 2 0 4+x , the same preparation method described above was used with different amounts of carbon black, and these samples were all tested in the manner described above by measuring the specific discharge capacity of a battery having a cathode made from the sample. The samples contained 0%, 1.3%, 4% and 7.5% by weight of carbon black, and the specific discharge capacity was measured on the 1st, 32nd, 52nd and 104th cycle of the test. The results are shown in Figure 2, which indicates an optimum level of carbon black at about 4% by weight of the LiMn 2 0 < , + -. sample. It will be appreciated that in alternative embodiments of the invention, other forms of carbon may be used instead of carbon black, for example, graphite and pitch coke. In a second method of the invention, 0.5 grams of lithium carbonate Li 2 C0 3 (BDH AnalaR, 99.5%) was added to 20- 30 millilitres of distilled water and stirred for half an hour. Manganese acetate (CH 3 C0 2 ) 2 Mn.4H 2 0 (Aldrich 99+%) was added to the lithium carbonate solution and stirred for one hour. The amount of manganese acetate added was 6.6339 grams so that the ratio of manganese to lithium is 2:1. A precipitate was formed from the solution. Water was removed from the precipitate using a rotary evaporator operating at 85°C. The precipitate may then be pre-dried at 60-80°C under vacuum conditions for 2 hours. Finally, 1-2 grams of the precipitate was packed in a 25 millilitre alumina crucible and heated in air at a temperature that was increased at a rate of 4°C per minute from room temperature to 300°C and held at 300°C for a period of 48 hours. Following the heat treatment, the precipitate takes the form of lithium manganese oxide spinel LiMn 2 0 4+x , where 0 < x 0.2. The heat treatment can be effected within the temperature range 200°C to 700°C. The performance of the LiMn 2 0 4+x was tested by incorporation in the cathode of a battery. A dry mixture of LiMn0 2 0 4 (80% by weight), carbon (13.3% by weight) and polytetrafluoroethylene (6.7% by weight) was compressed on a nickel mesh grid to produce a cathode with an area of 0-9 cm 2 containing 12 milligrams of the mixture. This cathode was incorporated into a battery with a lithium anode and electrolyte of lithium hexafluoroarsenate and propylene carbonate LiAsF 6 /PC. This battery was subject to a charging/discharging cycling test and its specific discharge capacity measured at various cycles during the test. The test employed cut-off potentials of 3.7 volts and 2 volts a charge current of 450 microamps and a discharge current of 900 microamps. The test results are shown in Figure 3 as curve I. A similar battery having a cathode incorporating LiMn 2 0 4 prepared by the prior art method of US 5135732 was also tested using a similar charging/discharging cycling test except that the discharge current was 440 microamps instead of 900 microamps. Curve I in Figure 3 shows that the battery with the cathode formed from LiMn 2 0 4+x according to the invention, has a higher specific discharge capacity than that (curve II) of a battery with the cathode formed from LiMn 2 0 4 according to the prior art US 5135732. This is so, even though the higher discharge current of the tests of curve I would be expected to reduce the specific discharge capacity compared to the test results of curve II. In a second series of tests, LiMn 2 0 4+x was prepared by the same method described above using lithium carbonate Li 2 C0 3 , but with the addition of 50 milligrams of carbon black to the lithium carbonate solution. A sample was tested in the manner described above by measuring the specific discharge capacity of a battery having a cathode made from the sample. The discharge current in the test was 1 milliamp/cm 2 and the charging current was 0.5 milliamp/cm 2 . The test results, shown as curve I in Figure 4, are compared with test results (curve II) for a similar battery having a cathode made from LiMn 2 0 4+x prepared using lithium carbonate as in the first embodiment without the addition of carbon black. These test results demonstrate that the addition of carbon in the preparation of LiMn 2 0 4+x produces a material which gives an increased specific discharge capacity when used as a cathode in a secondary battery.

Claims: CLAIMS 1. A method for the preparation of lithium manganese ternary oxide Li Mn 2 0 4+x , where 0 ≤ x ≤ 0.2, which is characterised in comprising reacting a manganese-containing compound with a lithium carbonate. 2. A method as claimed in claim 1 in which the manganese- containing compound comprises manganese acetate. 3. A method as claimed in claim 1 or 2 in which the reaction occurs in water. 4. A method as claimed in claim 3 in which the Li Mn 2 0 4+x is formed as a precipitate and is dried. 5. A method as claimed in claim 4 in which the Li Mn 2 0 4 precipitate is heat treated in the temperature range 200°C to 700°C. 6. A method as claimed in any one of claims 11 to 15 in which carbon is added to the manganese-containing compound and lithium carbonate before they react. 7. A method as claimed in claim 6 in which the carbon comprises carbon powder. 8. A method for the preparation of lithium manganese ternary oxide Li Mn 2 0 4+x , where 0 ≤ x ≤ 0.2, which comprises reacting a manganese-containing solution with a lithium- containing solution with a lithium-containing compound in an inert atmosphere, characterised in that carbon is added to the manganese-containing solution prior to reacting with the lithium-containing compound. 9. A method as claimed in claim 8 in which the carbon is in the form of powder. 10. A method as claimed in claim 9 in which the proportion of the carbon added is up to 8 percent by weight of the Li Mn 2 0 4+x produced. 11. A method as claimed in claim 10 in which the proportions of the carbon added is within the range 2 to 6 percent by weight of the Li Mn 2 0 4+x produced. 12. A method as claimed in claim 11 in which the proportion of the carbon added is substantially 4 percent by weight of the Li Mn 2 0 4+x produced. 13. A method as claimed in any one of the claims 8 to 12 in which the manganese-containing solution comprises manganese acetate. 14. A method as claimed in any one of claims 8 to 13 in which the lithium-containing compound comprises lithium hydroxide . 15. A method as claimed in claim 14 in which ammonia is added to the lithium-containing compound. 16. A method as claimed in any one of claims 8 to 15 in which a gelatinous precipitate is produced by the reaction between the manganese-containing solution and the lithium- containing compound, and the gelatinous precipitate is dried. 17. A method as claimed in claim 16 in which the dried precipitate is heat treated in the temperature range 200°C - 700°C to form Li Mn 2 0 +3t . 18. Lithium manganese ternary oxide produced by a method as claimed in any one of the preceding claims. 19. An electrode for a battery incorporating lithium manganese ternary oxide produced by a method as claimed in any one of claims 1 to 17. 20. A battery incorporating an electrode as claimed in claim 19.

Inventors: BRUCE PETER GEORGE, BRUCE, PETER, GEORGE;
Applicants: BRUCE PETER GEORGE, DOWTY ELECTRONIC COMPONENTS, BRUCE, PETER, GEORGE;, DOWTY ELECTRONIC COMPONENTS LIMITED
Application year: 1994
Main classification: C01G45
IPC codes: C01G45, H01M4