METHOD OF MAKING POLYMERS HAVING SPECIFIC PROPERTIES

Abstract: A method of making a polymer having specific physiochemical properties by forming a first module having a structure which includes at least two structural diversity elements suitable to impart a desired physical property to a polymer which is made from said monomer; and reacting one or more modules to form a polymer having specific physiochemical properties. The base module can be formed by reacting a first compound having at least one structural diversity element and a first reactive group, with a second compound having at least one structural diversity element and a second reactive group, wherein the first and second groups combine by an addition reaction. Specifically, an aminimide compound, an oxazolone compound or derivatives thereof are useful as base modules in the invention.

Description: <Desc/Clms Page number 1> METHOD OF MAKING POLYMERS HAVING SPECIFIC PROPERTIES FIELD OF THE INVENTION The present invention relates to a novel method of controlled polymerization to produce encoded synthetic polymers, involving the stepwise assembly of discrete modules having selected structural features in a manner so as to produce a polymer having (1) a precisely ordered sequence of structural units; or (2) a precisely ordered sequence of structural units and a specific uniform chain length and molecular weight, depending on the particular strategy chosen; and (3) resultant physiochemical and biological properties which are the sum of the individual properties of the modules and their specific arrangement in the polymer. BACKGROUND OF THE INVENTION Existing polymeriztion methods fall into one of two basic types; (1) Addition or Chain Growth Polymerization; and (2) Condensation or Step-Growth Polymerization. Chain growth polymerizations most commonly utilize monomers possessing reactive carbon-carbon double bonds, although other species, such as cyclic ethers , e. g., ethylene and propylene oxide and aldehydes, e. g., formaldehyde, can be polymerized in this way. These chain-growth polymerizations are characterized by the fact that the free radical, ionic or metal complex intermediates involved in the process are transient and can not be isolated. A generalized example for a simple free radical initiated vinyl polymerization is shown below: <Desc/Clms Page number 2> EMI2.1 1. Formation of initiator (ocoo) Ocoo. U + C02 2. Initiation O. + -" &num; O/'yR 3. Propagation O/'yR R 01 ('YY G R Termination (capping) ' -''' 0" (CH2CHR) CH2CHR. &num;&num; by radical coupling, V 11 disproportionation or chain transfer processes POLYMER Step-growth polymerizations involve reactions which occur between molecules containing multiple reactive groups which can react with each other. An example of this is the well-known reaction of a glycol and a dibasic aromatic acid to give a polyester. It can be readily seen that the use of multiple reactive monomers posessing groups with similar or equivalent reactivities with this method produces a mixture of individual polymer species having random arrangements of monomeric sequences and only statistical control of the resulting stoichiometric make-up. While many different variations of these two classes of polymerization reaction schemes exist ,e.g. initiation may be cationic, radical, anionic, sequential aldol, ring-opening or displacement, and many different reactive species may be employed, e. g. electron deficient alkenes, epoxides, polyamines, <Desc/Clms Page number 3> hydroxyesters, etc. , all of these variations possess a common limiting feature - they all rely on a statistical or average stoichiometric control of the final polymeric product. This is achieved through the careful selection and control of the reaction conditions, such a concentration of monomers, agitation conditions, catalyst level, time/temperature cycles, etc.. These existing polymerization methods do not have any ability to control the exact constitution or length of any specific individual polymer chain. The properties of the polymers produced via these processes are, in fact, a statistical average of the properties of a complex mixture of subtly differing individual polymer species having a range of molecular weights and containing differing combinations and sequences of monomers along the chains..Even in the simplest example of a step growth polymerization involving only two reactants, where the product is a polymer containing a single repeating structural motif, the product obtained will consist of a statistical mixture of a large number of individual molecules each having differing lengths and molecular weights. In spite of these limitations, those skilled in the art have developed strategies by which these methods can be exploited. Average chain length can be controlled roughly by the ratio of initiator to monomer, or by quenching with an additive giving a range of molecular weights. Macroscopic properties can be modulated by the addition of comonomers which are incorporated randomly into the backbone. However, these methods possess no ability to have discreet or even reproducible microsequence control , and the "address" of a singular functionality added to the polymerization reaction is statistically determined. Most natural biological polymers, such as oligonucleotides, proteins and polysaccharides, on the other hand, contain precise sequences of monomer units which confer the polymer with highly specific functional properties, including a specific three dimensional structure. Recent advances in the understanding of the complex mechanisms of biochemical processes and of the underlying structure-function relationships of biological <Desc/Clms Page number 4> polymers involved in the replication (DNA-DNA), storage (DNA), transcription (DNA-RNA), translation (RNA-protein), communication, recognition, control (proteins, peptides, carbohydrates) and function (proteins, oligosaccharides) of all biological systems have illuminated the exquisite sensitivity of these polymers to microsequence variations. A classic example of this is sickle cell anemia which has been shown to be due to a single point mutation in the genetic sequence encoding for the beta chain of hemoglobin. As a result of this mutation, the abnormal hemoglobin contains a single valine in place of a glutamine in the sequence of the protein. This results in an abnormal shape for the hemoglobin, producing the characteristic sickle-shaped cells and the resulting tragic pathological consequences . The biosynthesis of these biopolymerscan be viewed, at a molecular level, to consist of a highly organized series of individual catenation steps, each carried out with specific reactants under highly controlled conditions and mediated by biocalytic agents, principally enzymes. All of the monomers necessary for the construction of these biological polymers are present in the vicinity of the reaction area and are carried by chaperone molecules to the site of their incorporation into the growing chain, where they are released and coupled. Since these polymers were designed by nature to carry out their highly specific functions under physiological conditions (water at pH 7 and physiological temperatures, etc. ), and have been programmed by nature to be subject to natural biochemical transformations, such as proteolytic decomposition, they are usually not robust (notable exceptions include structural polymers such as chitin, cotton, skin, silk, hair and other structural materials ) and are easily decomposed or denatured by exposure to non-physiological conditions, such as elevated temperatures, organic solvents, extremes of pH, etc.. As a result, these molecules are generally ill suited for tasks other than their proper biochemical ones. Simply put, the makers of polymers, while being able to statistically achieve good and consistent macroscopic properties <Desc/Clms Page number 5> in the polymeric materials which they produce, have not had any way, up to this point, to control the microscopic make-up of their product. Nature, in producing biomacromolecules, has evolved systems which allow exquisite control over both the microscopic make-up and the macro-structure of its functional polymers. However, these polymers are severely limited in the variety of uses to which they may be applied by their chemical constitution, their lack of stability towards chemical and biochemical agents and their sensitivity to changes in environmental conditions, such as temperature. In addition, the nature of natural scaffolds and substituents and their sensitivity to the chemical conditions necessary to manipulate and to transform them severely limits their utility in producing new materials from these components. SUMMARY OF THE INVENTION This invention relates to a method of making a polymer having specific physiochemical properties by forming a base module having a structure which includes at least two orthogonal reactivity or structural diversity elements suitable to impart a desired physiochemical property to a polymer which is made from said monomer; and reacting one or more modules to form a polymer having specific properties. The module is preferablyan aminimide compound, an oxazolone-compound, or a derivative thereof. The module is prepared from first and second components which provide the orthogonal reactivity elements. The module may contain 2,3, 4 or more orthogonal reactivity elements, depending on the desired performance properties of the resultant polymer. The polymer chains are started with a terminus or starter module containg a single reactivity element and are capped at the desired point in the synthesis with a second terminus or capping module containing a single reactivity element in order to control the length of the chain. The base module can be formed by reacting a first compound having at least one structural diversity element and a <Desc/Clms Page number 6> first reactive group, with a second compound having at least one structural diversity element and a second reactive group, wherein the first and second groups combine by an addition reaction. Preferably, the first compound is produced by forming an oxazolone cdompound having at least one structural diversity element attached thereto and reacting it with a nucleophile or carbonyl compound which contains at least one structural diversity element to form a base module having one of the following structures: EMI6.1 and EMI6.2 wherein at least two of the unconnected lines are connected to structural diversity elements. Alternatively, it is also preferred to provide the first compound as an aminimide-forming compound having at least one structural diversity element attached thereto and to react it with an oxazolone or an oxirane compound, which contains at least one structural diversity element to form a base module having one of the following structures: <Desc/Clms Page number 7> EMI7.1 wherein at least two of the unconnected lines are connected to structural diversity elements. In particular, this method can be used to make polymers having a designed water solubility. This invention still further relates to the polymers produced according to these methods. Still further, this invention relates to uniform polymers comprising a multitude of long chain molecules each of which have the same molecular weight and the same length. This ability to produce polymeric chains of specific sequence and composition has great utility in the fabrication of a new generation of functional oligomeric and polymeric materials for a wide spectrum of applications, such as drugs, chiral recognition elements, catalysts, seperations tools, biomaterials, fibers, plastics, membranes, beads and gels. DETAILED DESCRIPTION OF THE INVENTION The present invention discloses a fundamentally new approach to the fabrication of oligomeric and polymeric molecules involving (1) the use of modular units which can contain at least two orthogonally reactive elements and are capable of bearing a wide variety of structural information, such as specific geometry, functionality, substituents, etc. (2) the stepwise assembly of polymers from these modules (a) by carrying out catenation or coupling reactions one step at a time or (b) by constructing "sub assemblies" of modular units one <Desc/Clms Page number 8> step at a time and connecting them together in a concerted manner in such a way that the resulting polymer has a controlled (encoded) microsequence and a resultant overall functional activity, which is the sum of the functional activities of the constituent modular parts. This approach involves the design and construction of a scaffolding superstructure which sets the basic spacing and geometry of the molecule and serves to arrange and orient the attached substituent groups in a manner suitable to achieve the desired functional property and, simultaneously, serves to allow the incorporation of desired pendant substituents in the appropriate positions having the appropriate desired relationships to each other and to the scaffold to produce the desired functional effect in the final polymer. In this application, the term "polymer" is used to refer to any catenated structure containing a sufficient number of modules to carry enough structural information to impart the desired property to the resulting polymer, usuallyconsisting of a minimum of three monomers plus two terminus (starter and capping) modules. A key element of this method is the presence of at least two orthogonal reactivity elements in the modules. Orthagonal reactivity elements are defined as those elements which are either (A) multiple reactive groups which are capable of being "turned on" independently of each other or (B) multiple differing reactive states which may be addressed or brought into being at different times or under different conditions in the catenation sequence. It is highly desirable, although not absolutely necessary, that the individual reactions be high-yielding addition reactions with no by-products, so that isolation and purification steps are not necesary between cycles. The two basic schemes are illustrated below: A. Multiple Reactive Groups <Desc/Clms Page number 9> EMI9.1 Step 1. Coupling of "Starter Module" with "Extender Module" A --R2 + R B R2 p-'U--R2 Step 2. Coupling of "Extender Module" with Chain B '-R2 +R&num;&num;Fcl&num;&num;'" B C R2 Step 3. Coupling of "Capping Module" with Chain A B C -R2 + R, ¯¯iE 3 FA ICMOEICE] Where Rl and R2 = groups capable of undergoing addition reactions with each other, and A, B, C, D are either monomeric modules or "sub assemblies" containing multiple modules stitched together in a sequence specific manner. B. Multiple Reactive States <Desc/Clms Page number 10> EMI10.1 Step 1. Coupling of "Starter Module" with "Extender Intennediate" 0- + R1--(X) !..-I Step 2. Transformation of Tenninal Intermediate Group to Reactive Group Bearing Module lJ v 2 8) & Step 3. Coupling of "Extender Intermediate" with Chain 0O&num;J-RI + R1--(X) - rnrn(X) Step 4. Transformation of Terminal Intermediate Group to Reactive Group Bearing Module A , J (3 / A J B C f$ Step 5. Coupling of "Capping Module" with Chain GI)&num;J:GJ--+ R1 Iy ---- U C D Where Rl and R2 are groups capable of undergoing addition reactions with each other, and A, B, C, D are either monomeric modules or "sub assemblies" containing multiple modules stitched together in a sequence specific manner. These reactive orthagonalities allow each discrete addition reaction to be carried to completion before the next individual addition reaction is undertaken. If desired, the intermediate products may be isolated following each individual step. In this critical respect this method is fundamentally different from both chain and step-growth polymerization methods. In addition to the stepwise sequential construction of polymers one unit at a time as illustrated, this method may be utilized to construct oligomeric "sub assemblies" having designed microsequences, and properties. These may then be connected <Desc/Clms Page number 11> together in a separate step to produce higher order assemblies, which may themselves again be connected together to, ultimately form a polymer having the desired set of properties. This strategy requires that one of the orthogonal reactivity elements on each sub-unit be either protected with an appropriate removable blocking group or contain a third orthogonally reactive group. These reactions may be carried out with modules containing > 2 orthogonally reactive elements to produce three dimensionally cross linked networks and structures. Alternatively these sub assemblies may be combined with appropriately functionalized "classical" modules to produce hybrid polymers. A new approach to the stepwise sequential construction of novel oligomeric and polymeric molecules is described. This approach involves the development of a process whereby molecular building blocks which contain appropriate atoms and functional groups and posses at least two orthogonally reactive elements are connected together in a stepwise sequential fashion to allow the modular assembly of oligomers and polymers with tailored properties; each module contributing to the overall properties of the assembled molecule. This approach to molecular construction is applicable to the synthesis of all types of molecules, including but not limited to mimetics of peptides, proteins, oligonucleotides, oligosaccharides, classical polymers, variants, hybrids of these and to fabricated structures and materials useful in materials science. It is analogous to the modular construction of a mechanical device that performs a specific operation wherein each module performs a specific task contributing to the overall operation of the device. Examples of suitable modules containing appropriate orthogonally reactive elements for utilization in this method are given below: Several of the specific modular chemistries chosen to illustrate and exemplify the invention are capable of bearing and maintaining chiral centers throughout the various steps <Desc/Clms Page number 12> involved. Where this is the case, the chirality will be shown. This is not intended to limit the scope of the invention to chiral materials, since there are a large number of variations and applications where structural stereocontrol is not required or where achiral materials are employed POLYMERS PRODUCED FROM OXAZOLONES Oxazolone Modules A type of oxazolone module appropriate for use in the present invention may be represented by the following general structure: EMI12.1 where R & R' are the same or different and X represents either a group having orthagonal reactivity to the oxazolone ring or a structural moiety, depending on which of two possible assembly strategies is chosen, as outlined below. R1 and R2 differ from one another and taken alone each signifies one of the followng: alkyl including cycloalkyl and substituted forms thereof; aryl, aralkyl, alkaryl, and substituted or heterocyclic versions thereof; preferred forms of Rl and R2 are the side chain substituents occuring in native polypeptides, oligonucleotides, variants or mimetics of these, carbohydrates, pharmacophores, variants or mimetics of these, or any other side chain substituent which can be attached to a scaffold or a backbone to produce a desired interaction with a target system. The substituents R & R' may be of a subset of hydrophilic substituents such as, but not limited to hydroxymethyl, <Desc/Clms Page number 13> hydroxyethyl, hydroxypropyl, thioethyl, thiomethyl; carboxymethyl, carboxyethyl, ethylcarboxamido, methylcarboxamido; aminomethyl, aminoethyl, aminopropyl, guanindinylpropyl, guanidinylbutyl; mono-, di-, and triaminobenzyl, mono-, di-, and trinitrobenzyl; mono-, di-, tri-, and tetrahydroxy benzyl, mono- or polyhydroxyaryl (e.g. pyrogallol) ; heteroaryl (e. g. alkylpyridines, imidazole, alkyltryptophans) ; alkyl nucleotides; all substituted pyrimidylalkyl and substituted purinealkyl moieties; mono-, di-, and oligosaccharide (e. g. N-methylfucosamine, maltose and the calicheamicin recognition sequence respectively); alkylsulfonates, alkylphosphonates; a-polyfluoroketones; secondary, tertiary and quaternaryamines; hydrazines and the hydrazinium salts. R and R' may also come from the subset consisting of hydrophobic substituents such as, but not limited to: hydrogen; methyl, ethyl propyl, isopropyl, butyl, sec-butyl, isobutyl, tert-butyl, pentyl, iso-, sec-, and neopentyl, hexyl, heptyl, octyl, nonyl, decyl, etc. ; vinyl, propenyl, butenyl or other alkenyl groups; acetylenic side chains; aromatic polycyclics (e. g. biphenyl, binaphthyl, naphthylphenyl, phenylnaphthyl); fused aromatic polycyclics (e.g. phenylene, pyrene, acenaphthene, azulenes) ; fused polycyclics (e. g. decalin, hydrindanes, steroids) ; phenyl, alkylphenyl, phenylalkyl; benzyl, mono-, di-, tri-, and tetraalkylbenzyl; mono-, di-, and trialkoxybenzyl; heteroaryl (e. g. furyl, xanthanyl, quinolyl); methoxyalkyl, ethoxyalkyl, aryloxy; methylmercaptans, ethylmercaptans, alkyl thioethers and arylthioethers; dyes and fluorescent tags (such as rhodamine or fluorescein); alkyl esters, aryl esters, aralkyl esters, and alkylaryl esters. Polymerization Strategies These oxazolone modules may be employed to construct oligomersand polymers in two different ways: A. Ring Opening Reaction/2-Position Substituent Addition- <Desc/Clms Page number 14> Oxazolones with suitable substituents at the 2position (X = an orthagonally reactive group) may act as orthogonally reactive agents suitable for the construction of the polymers which are the subject of the present invention. This may be accomplished by carrying out alternating ring opening and 2-position substituent addition reactions with suitable bifunctionally reactive species. One terminus of these reactive elements should contain an SH, OH or NH group capable of underegoing ring-opening addition reaction with the oxazolone ring. The second terminus of the reactive element should contain a group capable of undergoing addition reaction with X. The choice of this second group, obviously, depends on the nature of the specific X group chosen in each case. Appropriate 2-position substituents include vinyl groups, which make the oxazolone a Michael acceptor, haloalkyl and alkyl sulfonate esters and epoxide groups. This is shown below for the case of alternating ring opening and Michael additions to the double bond of a 4,4disubstituted-2-vinyloxazolone by appropriate dinucleophillic species produces polymeric chains, as shown <Desc/Clms Page number 15> EMI15.1 In the above sequence of reactions, HNul-Z-Nu2H represents a structure containing two differentially reactive nucleophilic groups, such as methylamino-ethylamine, I-amino propane-3thiol, and so on; groups Nul, Nu2, Nu3 and Nu4 need not be identical and Z is a generalized structural group connecting HNul and HNu2. HNul-Z-Nu2H may contain two nucleophilic groups of <Desc/Clms Page number 16> differential reactivity, as stated above, or if Nu and Nu2 are of comparable reactivity one of the nucleophilic groups is protected to prevent it from competing with the other and deprotected selectively following acylation; protecting groups commonly used in the art of peptide synthesis (e. g., for the nucleophilic groups such as amino, hydroxyl, thio, etc. ) are useful in the protection of one of the Nu substituents of the structure HNul-Z-Nu2H. The product of the acylation reaction with HNul-Z-Nu2H (after Nudeprotection, if necessary) is further reacted with a new oxazolone unit in a Michael fashion, and this addition is followed by ring opening acylation with an additional dinucleophile; repetition of this sequence of synthetic steps produces a growing polymeric molecule. The Michael reaction step is usually carried out using stoichiometric amounts of nucleophile AXH and the oxazolone in a suitable solvent, such as toluene, ethyl acetate, dimethyl formamide, an alcohol, and the like. The selectivities of the Michael and oxazolone ring-opening processes impose certain limitations on the choice of the nucleophiles shown above. Specifically, nucleophiles of the form ROH tend to add primarily via the ring-opening reaction, and usually require. acidic catalysts (e. g., BF3) ; thus, Nu2 should not be OH. Likewise, primary amines tend to add only via ring-opening, and Nu2 should therefore not be NH2. Secondary amines readily add to the double bond under appropriate reaction conditions. Nucleophiles of the form RSH will exclusively add via ringopening if the sulfhydryl group is ionized (i.e., if the basicity of the reaction mixture corresponds to pH > 9); on the other hand, such nucleophiles will exclusively add via Michael reaction under non-ionizing (i.e., neutral or acidic) conditions. During the Michael addition, it is important to limit the presence of hydroxylic species in the reaction mixture (e. g., moisture) to avoid ring-opening side-reactions. The ring-opening reactions can be carried out either in an organic solvent such as methylene chloride, ethyl acetate, dimethyl formamide (DMF) or in water at room or higher temperatures, in the presence or absence of acids, such as <Desc/Clms Page number 17> carboxylic, other proton or Lewis-acids, or bases, such as tertiary amines or hydroxides, serving as catalysts. An example of the application of this strategy is given below for the synthsis of a subunit containing four structural modules and the subsequent assembly of these modules into a polymer containing repeating sequences of these specific subunits: The required 4,4'-disubstituted oxazolone modules may be prepared from the appropriate N-acyl amino acid using any of a number of standard acylation and cyclization techniques well-known to those skilled in the art, e.g.: EMI17.1 Alternative reactive groups may be introduced at the 2-position of the oxazolone in this way, as shown for a benzyl substituted reactive substituent: EMI17.2 A wide variety of 4-monosubstituted azlactones may be readily prepared by reduction of the corresponding <Desc/Clms Page number 18> unsaturated derivatives obtained in high yield from the condensation reaction of aldehydes, ketones, or imines with the oxazolone formed from an N-acyl glycine (49 J. Org. Chem. 2502 (1984) ; 418 Synthesis Communications (1984)) EMI18.1 These may be converted to 4,4'-disubstituted oxazolones by alkylation of the 4-position, as in the following transformation (Synthesis Commun., Sept. 1984, at 763; 23 Tetrahedron Lett. 4259 (1982)): EMI18.2 Other important bifunctionally reactive oxazolone derivatives which may be employed in these schemes include: <Desc/Clms Page number 19> EMI19.1 B. Alternating Sequences of Nucleophilic Oxazolone-Ring-Opening Addition Reactions Followed by Oxazolone-Forming Cyclization Reactions Alpha,Alpha'-Disubstituted Sequences According to this approach, oxazolone modules are catenated via ring-opening nucleophilic attack by the amino group of an alpha,alpha'-disubstituted amino acid; the resulting adduct is subsequently recyclized to form a terminal oxazolone (with retention of chirality). This is then subjected to another nucleophilic ring-opening catenation reaction, producing a growing polymer as shown below. This procedure is repeated until the desired polymer is obtained. <Desc/Clms Page number 20> EMI20.1 Wherein M is an alkali metal; each member of the substituent pairs R1 and R2, R3 and R4, and R5 and R6 differs from the other and taken alone each signifies alkyl, cycloalkyl, or substituted versions thereof, aryl, aralkyl or alkaryl, or substituted and heterocyclic versions thereof; these substituent pairs can also be joined into a carbocyclic or heterocyclic ring; <Desc/Clms Page number 21> preferred forms of Rl and R2 are the side chain substituents occurring in native polypeptides, oligonucleotides, variants or mimetics of these, carbohydrates, pharmacophores, variants or mimetics of these, or any other side chain substituent which can be attached to a scaffold or a backbone to produce a desired interaction with a target system. ; X represents an oxygen, sulfur, or nitrogen atom; and A and B are the substituents described above. A chiral oxazolone derivative containing a blocked terminal amino group may be prepared from a blocked, disubstituted dipeptide, that was prepared by standard techniques known to those skilled in the art, as shown: EMI21.1 wherein B1 is an appropriate protecting group, such as Boc (tbutoxycarbonyl) or Fmoc (fluorenylmethoxycarbonyl). One may then use this oxazolone to acylate an amine, hydroxyl, or sulfhydryl-group in a linker structure or functionalized solid support, represented generically by AXH, using the reaction conditions described above. This acylation is followed by deblocking, using standard amine deprotection techniques compatible with the overall structure of the amide (i.e., the amine protecting group is orthogonal with respect to any other protecting or functional groups that may be present in the molecule), and the resulting amino group is used for reaction with a new bifunctional oxazolone generating a growing chiral polymeric structure, as shown below: <Desc/Clms Page number 22> EMI22.1 In the reaction shown above, Y is a linker (preferably a functionalized alkyl group); X is a nitrogen of suitable structure; an oxygen or a sulfur atom; each member of the substituent pairs R1 and R2, R3 and R4, Rn-1and Rn differs from the other and taken alone each signifies alkyl, cycloalkyl, <Desc/Clms Page number 23> or functionalized versions thereof; aryl, aralkyl or alkaryl or functionalized including heterocyclic versions thereof (preferably, these R substituents mimic the side-chain of naturally occurring amino acids) ; substituent R can also be part of a carbocyclic or heterocyclic ring; A is a substituent as described above; and C is a substituent selected from the set of structures for A; and B1 is a blocking or protecting group. Sub Assemblies Alternatively, modular "sub assemblies" capable of conferring higher order structural properties may be preconstructed and assembled together using these same reaction sequences in a manner which allows control of the higher order structure. This is illustrated for the case of a polymer formed with a repeating pattern of alternating modules of the type:: EMI23.1 This polymer will form 3-10 helices, driven by the conformational restrictions imposed by the repetitive viscinal disubstitution. This triadic periodicity results in the formation of a helical superstructure which has charged sulfonate groups lined up regularly along one side of the helix: <Desc/Clms Page number 24> EMI24.1 This "sub assembly" strategy may be used to generate higher order polymers in the following manner: 1. An oxazolone dimer containing a blocked terminal amino group may be prepared from a blocked disubstituted peptide, prepared using standard techniques known to those skilled in the art, as shown: EMI24.2 2. This oxazolone may be coupled with a suitable c-terminal derivative of a second disubstituted dipeptide, as shown, to give the 4-mer module shown: EMI24.3 <Desc/Clms Page number 25> 3. This process may then be repeated with the 4-mers to produce an 8-mer module; repeated again to form a 16-mer module, and so on, until a molecule having the desired length is obtained. At any point in this sequence, the protecting groups can be removed and the modules can be catenated together to form a polymer with repeating sequences of modules, as shown: EMI25.1 where m = number ofiterative steps In cases where solubility problems are encountered as the size of the modules increases, the stability of the linkages allows the use of a broad array of standard or "exotic" reaction solvents, such as hexamethyl phosphoramide. If necessary, solubilizing groups can be incorporated as side chain substituents or connecting modules. Other Reactive Elements At any point in the polymer syntheses shown above, a structural species, possessing (1) a terminal OH, -SH or -NH2 group capable of ring-opening addition to the oxazolone and (2) another terminal group capable of reacting with the amino group of a chiral alpha, alpha'disubstituted amino acid, may be inserted in the polymer backbone as shown below ; EMI25.2 <Desc/Clms Page number 26> EMI26.1 This process may be repeated, if desired, at each step in the synthesis where an oxazolone ring is produced. The bifunctional species used may be the same or different in the steps of the synthesis. The experimental procedures described above for oxazolone formation and use of oxazolones as acylating agents are expected to be useful in the oxazolone-directed catenations. Solubility and coupling problems that may arise in specific cases can be dealt with effectively by one with ordinary skill in the art of polypeptide and peptide mimetic synthesis. For example, special solvents such as dipolar aprotic solvents (e. g., dimethyl formamide, DMF, dimethyl sulfoxide, DMSO, Nmethyl pyrollidone, etc.) and chaotropic (molecular aggregatebreaking) agents (e.g., urea) will be very useful as catenations produce progressively larger molecules. POLYMERS PRODUCED FROM AMINIMIDES Stepwise sequential Reactions of 1,1-Disubstituted Hydrazines or Hydrazine Derivatives with Bifunctionally Reactive elements. <Desc/Clms Page number 27> The aminimide monomer structure may be represented by the formula: EMI27.1 where R & R' are the same or different and X & X' are from the same groups as R or R: ' and/or represent the extension or remainder of a polymer chain.. The groups R & R' may be of a subset of hydrophilic substituents such as, but not limited to hydroxymethyl, hydroxyethyl, hydroxypropyl, thioethyl, thiomethyl; carboxymethyl, carboxyethyl, ethylcarboxamido, methylcarboxamido; aminomethyl, aminoethyl, aminopropyl, guanindinylpropyl, guanidinylbutyl; mono-, di-, and triaminobenzyl, mono-, di-, and trinitrobenzyl; mono-, di-, tri-, and tetrahydroxy benzyl, mono- or polyhydroxyaryl (e.g. pyrogallol); heteroaryl (e.g. alkylpyridines, imidazole, alkyltryptophans); alkyl nucleotides; all substituted pyrimidylalkyl and substituted purinealkyl moieties; mono-, di-, and oligosaccharide (e. g. N-methylfucosamine, maltose and the calicheamicin recognition sequence respectively); alkylsulfonates, alkylphosphonates; a-polyfluoroketones; secondary, tertiary and quaternaryamines; hydrazines and the hydrazinium salts. They may also come from the subset consisting of hydrophobic substituents such as, but not limited to hydrogen; methyl, ethyl propyl, isopropyl, butyl, sec-butyl, isobutyl, tert-butyl, pentyl, iso-, sec-, and neopentyl, hexyl, heptyl, octyl, nonyl, decyl, etc. ; vinyl, propenyl, butenyl or other alkenyl groups; acetylenic side chains; aromatic polycyclics (e. g. biphenyl, binaphthyl, naphthylphenyl, phenylnaphthyl); fused aromatic polycyclics (e.g. phenylene, pyrene, acenaphthene, azulenes) ; fused polycyclics (e. g. decalin, <Desc/Clms Page number 28> hydrindanes, steroids) ; phenyl, alkylphenyl, phenylalkyl; benzyl, mono-, di-, tri-, and tetraalkylbenzyl; mono-, di-, and trialkoxybenzyl; heteroaryl (e. g. furyl, xanthanyl, quinolyl); methoxyalkyl, ethoxyalkyl, aryloxy; methylmercaptans, ethylmercaptans, alkyl thioethers and arylthioethers; dyes and fluorescent tags (such as rhodamine or fluorescein); alkyl esters, aryl esters, aralkyl esters, and alkylaryl esters; polymeric support surfaces Polymerization of Aminimide Subunits via Acylation/Alkylation Cycles The following steps are involved in this synthesis: 1. Acylation of a hydrazinium salt with a molecule capable of functioning both as an acylating and as an alkylating agent producing an aminimide; BrCH2COCI and other bifunctional species, such as bromoalkyl isocyanates, 2-bromoalkyl oxazolones, etc. , may be used as acylating agents under the reaction conditions given above. EMI28.1 2. Reaction of the product of the above reaction with a 1,1disubstituted hydrazine to form an aminimide hydrazinium salt. EMI28.2 3 Acylation of the product from step 2 with a bifunctional acyl derivative similar to those listed in step 1 above producing a dimer. <Desc/Clms Page number 29> EMI29.1 54 Repetition of steps 2 and 4 the required number of times to build the desired aminimide polymeric sequence. 6. Capping of the assembled sequence if desired, for example, by reaction with an acylating agent, such as acetyl chloride. The experimental conditions (e.g. reaction-solvent, temperature and time, and purification procedures for products) for all of the above reactions were described above and are also well-known and practiced in the art. As the molecular weight of the products increases (e.g. in step 5 above) solubility and reaction-rate problems may develop if the reactions are run under the conditions that successfully gave products of much smaller molecular weight. As is well known from the art of peptide synthesis, this is probably due to conformational (folding) effects and to aggregation phenomena, and procedures found to work in the related peptide cases are expected to be very useful in the case of aminimide catenations. For example, reaction solvents such as DMF, or N-methyl pyrollidone, and chaotropic (aggregate-breaking) agents, such as urea, are expected to be helpful in alleviating reactivity problems as the molecular-weight of the product increases. EMI29.2 Polymerization of Aminimide Subunits via Acylation/Alkylation Cycles The following steps are involved in this synthesis; e. <Desc/Clms Page number 30> 1. Alkylation of an asymmetrically disubstituted hydrazide, prepared as outlined above, with a molecule capable of functioning both as an alkylating and an acylating agent to form a racemic mixture of aminimides; as before the use of BrCH2COCI is shown below, but other bifunctional species, such as bromoalkyl isocyanates, 2-bromoalkyl oxazolones, etc. may also be used. 2. Reaction of the racemate from above with an asymmetrically disubstituted hydrazine to form the hydrazide: 3. Alkylation of the product from step 3 with a bifunctional molecule capable of alkylation and acylation, which may be the same as that used in step 1 or different, to form a mixture of diastereomeric aminimides. 4. Reaction of the product from step 4 with a suitable asymmetrically disubstituted hydrazine to form the hydrazide, as shown: EMI30.1 6. Repetition of steps 4, and 5 to build the desired aminimide polymer sequence. 8. Capping of the sequence, if desired, using e.g. methyl bromide to produce a sequence such as shown below. EMI30.2 Polymerization of Aminimide Subunits Using Hydrazinolysis of an Ester in the Presence of an Epoxide The following steps are involved in this synthesis: <Desc/Clms Page number 31> 1. Formation of an aminimine from the reaction of an 1,1-asymmetrically disubstituted hydrazine with an epoxide;: EMI31.1 2. The aminimine is reacted with an ester-epoxide to give an aminimide; EMI31.2 3. Reaction of the aminimide with an asymmetrically disubstituted hydrazine to form an aminimide-aminimine EMI31.3 4. Repetition of steps 2 and 3 using the appropriate hydrazines and epoxy-esters in each step to produce the desired aminimide sequence. 5. "Capping" of the final sequence, if desired, by acylation with a simple ester, such as methyl acetate, to produce the designed aminimide ligand shown: EMI31.4 <Desc/Clms Page number 32> Synthesis of Hydrazides 1,1-disubstituted hydrazine with an activated acyl derivative or an isocyanate, in a suitable organic solvent, e. g. methylene chloride, toluene, ether, etc. in the presence of a base such as triethylamine to neutralize the haloacid generated during the acylation. EMI32.1 Activated acyl derivatives include acid chlorides, chlorocarbonates, chlorothiocarbonates, etc.; the acyl derivative may also be replaced with a suitable carboxylic acid and a condensing agent such as dicyclohexylcarbodiimide (DCC). An example of the latter is the synthesis of the trifluor omethylhydr azides shown below: EMI32.2 In this reaction a solution of 2trifluoroacetamidoisobutyric acid in dry THF is stirred and an equivalent amount of dicyclohexylcarbodiimide is added. The reaction is subsequently strirred for three minutes, after which an equimolar quantity of the 1 -substituted- 1 -methylhydrazine is added neat. Dicyclohexylurea precipitates immediately. The resultant suspension is stirred for one hour, filtered to remove <Desc/Clms Page number 33> the insoluble urea and the solvent is removed on a rotary evaporator to afford the crude hydrazide. The desired 1,1-disubstituted hydrazines may be readily prepared in a number of ways well known in the art; one is the reaction of a secondary amine with NH2CI in an inert organic solvent. EMI33.1 A second synthetic route for the preparation of hydrazines is alkylation of monoalkyl hydrazines, shown below for methyl hydrazine: EMI33.2 This reaction is carried out by reacting a solution of methylhydrazine in THF, cooled at 0 C with a solution of an equimolar amount of the alkyl halide in THF added dropwise with stirring over a period of 30 minutes. The reaction is stirred at 0 OC for another 15 minutes, then heated to reflux and held at reflux for two hours. A water-cooled downward condenser is set up and approximately half of the solvent is removed by distillation. The residue is poured into water, which is then made basic by the addition of concentrated aqueous NaOH. The layers are separated, the aqueous phase is extracted with ether and the combined organic phases are washed with water, dried over MgS04 and concentrated by distillation. Distillation at reduced pressure affords thel-substituted-1-methylhydrazine as a colorless liquid. <Desc/Clms Page number 34> Polymers Produced by Hydrazides Polymers containing designed sequences of substituted hydrazones may be produced using the following steps: EMI34.1 R DCC R AC02H + H2NIi -co2Bu-t &num;&num;&num;&num;&num;&num;*" ACONHIJ L C02Bu-t 1 trifluoroacetic acid R H2NN( R C02Bu-t R ACONH \&num;CONHK R 6 ACONHJ -- CONH C02Bu-t -LCH trifluoroacetic acid R H2N/¯ CO2BU-t ' etc., etc. etc., etc. H2NNRB ACO- -Nf; R O -NHNRB base ACO- ./ N ;N ./".... f /"'} -N] &num;&num;\ n base R' n Mixed Modules All of the oxazolone, aminimide and hydrazide modules and monomers illustrated above may be mixed and matched to provide a variety of mixed-backbone polymers having specific properties, functionalities and sequences. <Desc/Clms Page number 35> Substituents Any of the various R and R' groups illustrated in all of the oxazolone, aminimide and hydrazide structures may be selected from among the following list: 1) Amino acid derivatives of the form (AA) N, which would include, for example, natural and synthetic amino acid residues (N=1) including all of the naturally occuring alpha amino acids, especially alanine, arginine, asparagnine, aspartic acid, cysteine, glutamine, glutamic acid, glycine, histidine, isoleucine, leucine, lysine, methionine, phenylalanine, proline, serine, threonine, tryptophan, tyrosine; the naturally occuring disubstituted amino acids, such as amino isobutyric acid, and isovaline, etc. ; a variety of synthetic amino acid residues, including alpha-disubstituted variants, species with olefinic substitution at the alpha position, species having derivatives, variants or mimetics of the naturally occuring side chains; N-Substituted glycine residues; natural and synthetic species known to functionally mimic amino acid residues, such as statine, bestatin, etc. Peptides (N=2-30) constructed from the amino acids listed above, such as angiotensinogen and its family of physiologically important angiotensin hydrolysis products, as well as derivatives, variants and mimetics made from various combinations and permutations of all the natural and synthetic residues listed above. Polypeptides (N=31-70), such as big endothelin, pancreastatin, human growth hormone releasing factor and human pancreatic polypeptide. Proteins (N > 70) including structural proteins such as collagen, functional proteins such as hemoglobin, regulatory proteins such as the dopamine and thrombin receptors. 2) Nucleotide derivatives of the form (NUCL) N, which includes natural and synthetic nucleotides (N=1) such as adenosine, thymine, guanidine, uridine, cystosine, derivatives of these and a variety of variants and mimetics of the purine ring, the sugar ring, the phosphate linkage and combinations of some or all of these. Nucleotide probes (N=2-25) and oligonucleotides (N > 25) including all of the various possible homo and heterosynthetic combinations and permutations of the naturally occuring nucleotides, derivatives <Desc/Clms Page number 36> and variants containing synthetic purine or pyrimidine species or mimics of these, various sugar ring mimetics, and a wide variety of alternate backbone analogues including but not limited to phosphodiester, phosphorothionate, phosphorodithionate, phosphoramidate, alkyl phosphotriester, sulfamate, 3'thioformacetal, methylene (methylimino), morpholino carbamate and peptide nucleic acid analogues. 3) Carbohydrate derivatives of the form (CH) n. This would include natural physiologically active carbohydrates such as including related compounds such as glucose, galactose, sialic acids, beta-D-glucosylamine and nojorimycin which are both inhibitors of glucosidase, pseudo sugars, such as 5a-carba-2-Dgalactopyranose, which is known to inhibit the growth of Klebsiella pneumonia (n=l), synthetic carbohydrate residues and derivatives of these (n=l) and all of the complex oligomeric permutations of these as found in nature, including high mannose oligosaccharides, the known antibiotic streptomycin (n > l). 4) A naturally occurring or synthetic organic structural motif. This term is defined as meaning an organic molecule having a specific structure that has biological activity, such as having a complementary structure to an enzyme, for instance. This term includes any of the well known base structures of pharmaceutical compounds including pharmacophores or metabolites thereof. These include betalactams, such as pennicillin, known to inhibit bacterial cell wall biosynthesis; dibenzazepines, known to bind to CNS receptors, used as antidepressants; polyketide macrolides, known to bind to bacterial ribosymes, etc. These structural motifs are generally known to have specific desirable binding properties to ligand acceptors. 5) A reporter element such as a natural or synthetic dye or a residue capable of photographic amplification which possesses reactive groups which may be synthetically incorporated into the oxazolone structure or reaction scheme and may be attached through the groups without adv,ersely interfering with the reporting functionality of the group. Preferred reactive groups are amino, thio, hydroxy, carboxylic acid, carboxylic acid ester, <Desc/Clms Page number 37> particularly methyl ester, acid chloride, isocyanate alkyl halides, aryl halides and oxirane groups. 6) An organic moiety containing a polymerizable group such as a double bond or other functionalities capable of undergoing condensation polymerization or copolymerization. Suitable groups include vinyl groups, oxirane groups, carboxylic acids, acid chlorides, esters, amides, lactones and lactams. Other organic moiety such as those defined for R and R' may also be used. 7) A macromolecular component, such as a macromolecular surface or structures which may be attached to the oxazolone modules via the various reactive groups outlined above in a manner where the binding of the attached species to a ligand-receptor molecule is not adversely affected and the interactive activity of the attached functionality is determined or limited by the macromolecule. This includes porous and nonporous inorganic macromolecular components, such as, for example, silica, alumina, zirconia, titania and the like, as commonly used for various applications, such as normal and reverse phase chromatographic separations, water purification, pigments for paints, etc. ; porous and non-porous organic macromolecular components, including synthetic components such as styrenedivinyl benzene beads, various methacrylate beads, PVA beads, and the like, commonly used for protein purification, water softening and a variety of other applications, natural components such as native and functionalized celluloses, such as, for example, agarose and chitin, sheet and hollow fiber membranes made from nylon, polyether sulfone or any of the materials mentioned above. The molecular weight of these macromolecules may range from about 1000 Daltons to as high as possible. They may take the form of nanoparticles (dp=100-1000Angstroms ), latex particles (dp=1000-5000Angstroms), porous or non-porous beads (dp=0.5- 1000 microns), membranes, gels, macroscopic surfaces or functionalized or coated versions or composites of these. 8) A structural moiety selected from the group including cyano, nitro, halogen, oxygen, hydroxy, alkoxy, thio, straight or branched chain alkyl, carbocyclic aryl and substituted or <Desc/Clms Page number 38> heterocyclic derivatives thereof, wherein R and R' may be different in adjacent n units and have a selected stereochemical arrangement about the carbon atom to which they are attached; As used herein, the phrase linear chain or branched chained alkyl groups means any substituted or unsubstituted acyclic carbon-containing compounds, including alkanes, alkenes and alkynes. Alkyl groups having up to 30 carbon atoms are preferred. Examples of alkyl groups include lower alkyl, for example, methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl or tert-butyl; upper alkyl, for example, cotyl, nonyl, decyl, and the like; lower alkylene, for example, ethylene, propylene, propyldiene, butylene, butyldiene; upper alkenyl such as 1-decene, 1-nonene, 2,6-dimethyl-5-octenyl, 6-ethyl-5-octenyl or heptenyl, and the like; alkynyl such as I-ethynyl, 2-butynyl, I-pentynyl and the like. The ordinary skilled artisan is familiar with numerous linear and branched alkyl groups, which are within the scope of the present invention. In addition, such alkyl group may also contain various substituents in which one or more hydrogen atoms has been replaced by a functional group. Functional groups include but are not limited to hydroxyl, amino, carboxyl, amide, ester, ether, and halogen (fluorine, chlorine, bromine and iodine), to mention but a few. Specific substituted alkyl groups can be, for example, alkoxy such as methoxy, ethoxy, butoxy, pentoxy and the like, polyhydroxy such as 1,2-dihydroxypropyl, 1,4-dihydroxy-1-butyl, and the like; methylamino, ethylamino, dimethylamino, diethylamino, triethylamino, cyclopentylamino, benzylamino, dibenzylamino, and the like; propanoic, butanoic or pentanoic acid groups, and the like; formamido, acetamido, butanamido, and the like, methoxycarbonyl, ethoxycarbonyl or the like, chloroformyl, bromoformyl, 1,1-chloroethyl, bromoethyl ,and the like, or dimethyl or diethyl ether groups or the like. As used herein, substituted and unsubstituted carbocyclic groups of up to about 20 carbon atoms means cyclic carbon-containing compounds, including but not limited to cyclopentyl, cyclohexyl, cycloheptyl, admantyl, and the like. such cyclic groups may also contain various substituents in which one or <Desc/Clms Page number 39> more hydrogen atoms has been replaced by a functional group. Such functional groups include those described above, and lower alkyl groups as described above. The cyclic groups of the invention may further comprise a heteroatom. For example, in a specific embodiment, R2 is cycohexanol. As used herein, substituted and unsubstituted aryl groups means a hydrocarbon ring bearing a system of conjugated double bonds, usually comprising an even number of 6 or more (pi) electrons. Examples of aryl groups include, but are not limited to, phenyl, naphthyl, anisyl, toluyl, xylenyl and the like. According to the present invention, aryl also includes aryloxy, aralkyl, aralkyloxy and heteroaryl groups, e. g., pyrimidine, morpholine, piperazine, piperidine, benzoic acid, toluene or thiophene and the like. These aryl groups may also be substituted with any number of a variety of functional groups. In addition to the functional groups described above in connection with substituted alkyl groups and carbocylic groups, functional groups on the aryl groups can be nitro groups. As mentioned above, these structural moieties can also be any combination of alkyl, carbocyclic or aryl groups, for example, 1-cyclohexylpropyl, benzylcyclohexylmethyl, 2cyclohexyl-propyl, 2,2-methylcyclohexylpropyl, 2,2methylphenylpropyl, 2,2-methylphenylbutyl, and the like. Reactive Groups Specifically preferred reactive groups to generate the aminimide and oxazolone structures and the resulting base modules are listed below in tables 1,2 and 3. The bonds in the structures in these figures represent potential points of attachment to the first and second compounds and to the base modules. Specifically preferred reactive groups to generate the aminimide and oxazolone structures and the resulting base modules are listed below in tables 1,2 and 3. The bonds in the structures in these figures represent potential points of attachment for the attachment of the structural diversity elements to the first and second compounds and to the base modules. <Desc/Clms Page number 40> Table 1. Oxazolone Modules EMI40.1 Reactivity Groups Base Modules HIL- l'fl ( Y, 0 N > y (Y = N, S, O) H 0 Ou/ C=O O / 0 HY- Y\ (Y=N.S.O) " 0 0 C02H/Cl Ni 2/ \ CO " - C02H/Ct \/ V NH2 CC&commat;d (CIC02Et/Et3N) 0 / zain Z\r ! / X "- "-v X (X=S-.!) 0 (Z = CH2=CH-, etc.) Represents potential points of attachment <Desc/Clms Page number 41> Table 2. Aminimide Modules EMI41.1 Reactivity Groups Base Modules - COOH H2N &num;CONHN' -NCO H2N < &num;NHCONHN. - OCOCI H2N - SCOCI H2N &num;SCONHN. / els &num;CONHN. &num;&num;X -CONN- ' (neutr.) e b &num;CONHN. &num;&num;r-y &num;CONN " o OH - X ob - NHCONHN" (neutr.) - NHCON i - &num;NHCONHN -\7 --NHCoSN""T" \ 0 - x ek - OCONHN/ (neutr.) X -OCON Ob i - / ob.. ,- &num;OCONHN. &num;&num;-y OH / e k - SCONHN/ - X - SCONN- (neutr.) / 0 - SCONHN, &num;&num; &num;SCONN Represents potential points of attachment <Desc/Clms Page number 42> Table 2. Continued - Aminimide Modules EMI42.1 Reactivity Groups Base Modules 10 o H2NN - X Ire X (neutr.) H2N T H N N 0 I OU I O+ X C BASE H2NIrF- X BASE 1 ele C & R O 10 mr- - COOR -CONNCOOR ob HNNT &num;&num;COOR L-. GO) OH I OH 0)0 O C 2H -0 0 C02H 0 ,e/ o C02H 0' OH 0'. C02H 0 ,e/ OH H 10 8H 0 N-" 0 @ Represents potential points of attachment <Desc/Clms Page number 43> Table 3. Aminimide-Oxazolone Modules EMI43.1 Reactivity Groups Base Modules N 0 Q&commat; OH .H'N ;4--- N \\hf' N/ \ N OH 0 O H 0 O H2N / -1-Irrx N 0 ",- N¯, X 0 0 H (Base) Represents potential points of attachment EXAMPLE 1. This example describes preparation of a tetramer by alternating ring-opening/Michael-addition reactions followed by chain polymerizations. Step 1. EMI43.2 0 0 THF, then TBSCI, \/ r-110 THF, then TBSC), vs fez O HZN imidazole MeOH t ) \¯¯. 9 OBn 3. Clcyt, TBSCI, I "N 3. CICÇEt. E\N, PhH In the first synthetic step, a solution of b-butyrolactone (8.61 g, 0.1 mole, 8.15 mL) in THF (150 mL) is cooled at 0 C while a solution of benzyl 2-aminoisobutyrate (19.3 g, 0.1 mole) in THF (100 mL) is added. The mixture is stirred at 0 C for two hours , then room temperature for four hours, then is treated with tert-butyldimethylsilyl chloride ( 15.1 g, 0.1 mole) and <Desc/Clms Page number 44> imidazole (13.6 g, 0.2 mole) added in alternating portions as the solids. The mixture is stirred overnight at room temperature, the solids are removed by filtration, and the filtrate is concentrated in vacuo. The residue is dissolved in methanol (100 mL), palladium on carbon catalyst (5 % Pd, 500 mg) is added, and the solution stirred under an atmosphere of hydrogen gas until the ester is exhausted (reaction is monitored in progress by volume of absorbed H2 gas and by TLC). Following complete removal of the benzyllic functionality, the catalyst is removed by filtration with the aid of celite. The precipitate is washed with methanol (3 x 100 mL) and the combined filtrates are concentrated in vacuo. The residue is crystallized, then recrystallized from ethyl acetate to afford the protected acid (21.7 g, 0.072 mole, 72 %). This acid is dissolved in ethyl acetate (300 mL) and cooled at 0 C while ethyl chloroformate (7.77 g, 0.072 mole, 6.85 mL) is added, followed by triethylamine (7.25 g, 0.072 mole, 9.98 mL). After cessation of gas evolution (ca. four hours), the triethylamine hydrochloride is removed by filtration and the filtrate is concentrate to afford crude 2-(2tert-butyldimethylsilyloxy propyl)-4,4-dimethyl-5-oxazolone as a yellow oil (23.4 g). Recrystallization from ethyl acetate affords the pure product (13.7 g, 67 %, 0.048 mole). The material gave satisfactory spectral data (300 MHz NMR proton signals corresponding to silyl group butyl : silyl group methyls : oxazolone gem-dimethyl integrals 9:6:6; IR 1820 cm -1 azlactone band). Step 2. EMI44.1 A solution of of 95% N-methylethylenediamine (3.56 g, 48 mmol, 4.23 mL) in methylene chloride (75 mL) is cooled in an ice bath while a solution of 2-(2-tertbutyldimethylsilyloxy propyl) -4,4-dimethyl-5-oxazolone (13.7 <Desc/Clms Page number 45> g, 48 mmol) in methylene chloride (100 mL) is added such that the temperature remains below 5 C. The solution is stirred at room temperature for 15 minutes while a white precipitate forms. The mixture is stirred for an additional 2 h at 0 C. The solids are removed by filtration and washed with methylene chloride (25 mL) and air dried to yield the ring-opened adduct (12.87 g, 36 mmol, 75%), identified by nuclear magnetic resonance (NMR) and Fourier transform infrared (FTIR) spectroscopy as follows: NMR (CDCI3): CH-N/gem (CH3)2 ratio 1:2; tert-butyldimethylsilyl - splitting pattern in 0-1 ppm region, integration ratios and D20 exchange experiments diagnostic for structure. FTIR (nujol mull): azlactone CO band at 1820 cm-1 absent; strong amide bands present in 1670 - 1700 cm-1 region. EMI45.1 Step 3. OTBS OBn OTBS Bn ptmer Pentameri -I-0 NH n/ Phi, 7=-rt0 NH Rentamer phH. 7QC-r1 --7y ,,0 &num;&num;&num;&num;&num;&num; 0 NH 1 N 1 )--I-0 A solution of of the ring-opened adduct (8.98 g, 25 mmol) and 4,4-dimethyl-2-vinylazlactone ( 3.48 g, 25 mmol) in benzene (50 mL) is heated to 70 C for 4 hours. The flask is cooled to room temperature and allowed to stand under an inert atmosphere for 3 days. The solvent is decanted off from the thick oil that forms. This oil is dissolved in acetone (ca 50 mL) and concentrated to produce another thick oil, which is concentrated under vacuum at I torr overnight to yield 9.34 g of a white crystalline solid (25 mmol), identified by NMR and FTIR spectroscopy as 2-(N-(2-(2-(3-tert-butyldimethylsilyloxy butyramido)-isobutyramido)-ethyl)-N-methyl-2-aminoethyl)-4,4dimethyl-5-oxazolone: NMR: CH-N/gem (CH3)2 ratio 1: 4; tert- <Desc/Clms Page number 46> butyldimethylsilyl- splitting pattern in 0-1 ppm region, integration ratios and D20 exchange experiments diagnostic for structure. FTIR (nujol mull) : strong azlactone CO band at 1820 cm- 1 Construction of the Poly(pentamer) EMI46.1 Pentamer 1 TBAF, THF p 0 I Pentamer 0 C-70 C H n Polymerization of the mono(pentamer) -This material is dissolved in THF (500 mL) and cooled at 0 C while a solution of tetra-n-butylammonium fluoride (1.OM in THF, 25 mL, 25 mmol) is added. The exotherm is controlled by the rate of addition of the fluoride reagent. The mixture is then heated briefly to 70 C and cooled to room temperature. Water 100 mL) is added and the layers are stirred, then separated. The organic phase is dried (sat'd aq NaCI, MgS04), and concentrated in vacuo (18 torr, then 0.1 torr 10 hours) to afford the polymer (9.60 g). This material showed no signals for the tert-butyldimethylsilyl group in the proton NMR spectrum and the azlactone band was absent in the infrared spectrum. EXAMPLE 2. This example illustrates the preparation of a tris(pentameric) module and its assembly into a polymer. Step 1. <Desc/Clms Page number 47> EMI47.1 A solution of of the ring-opened adduct (8.98 g, 25 mmol) and benzyl 3-phenyl-2-methyl-2-acrylamidopropionate ( 8.03 g, 25 mmol) in benzene (50 mL) is heated to 70 C for 4 hours. The flask is cooled to room temperature and allowed to stand under an inert atmosphere for 3 days. The solvent is decanted off from the thick oil that forms. The residue is crystallized, then recrystallized from ethyl acetate. to afford the protected benzyl ester adduct (15.34 g, 23 mmol, 90%) Step 2. EMI47.2 <Desc/Clms Page number 48> The product is dissolved in THF (250 mL) and a solution of TBAF (1.OM, 23 mmol, 23 mL) is added and the reaction stirred for one hour at room temperature, then cooled at 0 C while a solution of 2-(N-(2-(2-(3-tert-butyldimethylsilyloxy butyramido)-isobutyramido)-ethyl)-N-methyl-2-aminoethyl)-4,4dimethyl-5-oxazolone (11.45 g, 23 mmol) in THF (150 mL) is added with stirring. The reaction is stirred overnight at room temperature, then partitioned between water (200 mL) and THF. The aqueous phase is separated and extracted with ether (2 x 200 mL) and the combined organics are dried (sat'd aq NaCI, MgS04) and concentrated to afford a solid (22.0 g). A suspension of this solid and palladium on carbon catalyst (5 % Pd, 500 mg) in methanol (200 mL) is stirred under an atmosphere of hydrogen gas until the ester is exhausted (reaction is monitored in progress by volume of absorbed H2 gas and by TLC). Following complete removal of the benzylic functionality, the catalyst is removed by filtration with the aid of celite. The filter pad is washed with methanol (3 x 100 mL) and the combined filtrates are concentrated in vacuo to afford a viscous syrup that is used directly. This acid is dissolved in ethyl acetate (100 mL) and cooled at 0 C while ethyl chloroformate (2.32 g, 23 mmol, 2.04 mL) is added, followed by triethylamine (2.16 g, 23 mmol, 2.98 mL). After cessation of gas evolution (approximately two hours), the triethylamine hydrochloride is removed by filtration and the filtrate is concentrated to afford the crude product as a yellow oil (23.4 g). A pure sample of this product is obtained Purified by chromatographic purification on RP-C18 silica gel (methanol-water gradient elution) to give 2-(N-(2-(3- (2-(N-(2-(2-(3-tert-butyldimethyl silyloxybutyramido)- isobutyramido)-ethyl)-N-methyl-3-propanamido)- isobutyroxy)-butyramido)-isobutyramido)-ethyl-N-methyl-2aminoethyl)-ethyl-4,4-dimethyl-5-oxazolone (11.43 g, 61%, 14 mmol) as an amorphous powder. The material gave satisfactory spectral data (300 MHz NMR proton signals corresponding to silyl group butyl : silyl group methyls : <Desc/Clms Page number 49> oxazolone gem-dimethyl integrals 9: 6:6; IR 1820 cm -1 azlactone band). Step 3. EMI49.1 A solution of of the ring-opened adduct (8.98 g, 25 mmol) and benzyl 2,4-dimethyl-2-acrylamidopentanoate ( 7.18 g, 25 mmol) in benzene (50 mL) is heated to 70 C for 4 hours. The flask is cooled to room temperature and allowed to stand under an inert atmosphere for 3 days. The solvent is decanted off from the thick oil that forms. The residue is crystallized, then recrystallized from ethyl acetate to afford the protected benzyl ester adduct (13.41 g, 21 mmol, 83%) Step 4. <Desc/Clms Page number 50> EMI50.1 A solution of this product (8.94 g, 14 mmol) in THF (250 mL) and a solution of TBAF (l.OM, 14 mmol, 14 mL) is added and the reaction stirred for one hour at room temperature, then cooled at 0 C while a solution of the previously prepared dipentamer oxazolone (11.43 g, 14 mmol) in THF (150 mL) is added with stirring. The reaction is stirred overnight at room temperature, then partitioned between water (200 mL) and THF. The aqueous phase is separated and extracted with ether (2 x 200 mL) and the combined organics are dried (sat'd aq NaCI, MgS04) and concentrated to afford a solid (22.0 g). A suspension of this solid and palladium on carbon catalyst (5 % Pd, 250 mg) in methanol (200 mL) is stirred under an atmosphere of hydrogen gas until the ester is exhausted (reaction is monitored in progress by volume of absorbed H2 gas and by TLC). Following complete removal of the benzylic functionality, the catalyst is removed by filtration with the aid of celite. The filter pad is washed with methanol (3 x 100 mL) and the combined filtrates are concentrated in vacuo to afford a viscous syrup that is used directly. This acid is dissolved in ethyl acetate (100 mL) and cooled at 0 C while ethyl chloroformate (1.41 g, 14 mmol, 1.24 <Desc/Clms Page number 51> mL) is added, followed by triethylamine (1.31 g, 14 mmol, 1.81 mL). After ten hours, the triethylamine hydrochloride is removed by filtration and the filtrate is concentrated to afford the crude product as a tan solid (23.4 g). Purification by column chromatography on RP-C18 silica gel (methanol-water gradient elution), pooling of the appropriate fractions and concentration in vacuo affords pure 2-(3-(N-(2-(2-(2-(3-(N- (2-(3-(2-(N-(2-(2-(3-tert-butyldimethylsilyloxybutyramido)isobutyramido)-ethyl)-N-methyl-2-aminoethyl)propanoylamido)-isobutyroxy)-butyramido)-isobutyramido)ethyl)-N-methyl-2-aminoethyl)-propanoylamido)isobutyroxy)-propanoylamido)-isobutyramido)-N-methylethylamino)-ethyl)-4-isobutyl-4-methyl-5-oxazolone z(3.72 g, 22%, 3 mmol) as an amorphous powder. The material gave satisfactory spectral data (300 MHz NMR proton signals corresponding to silyl group butyl : silyl group methyls : oxazolone gem-dimethyl integrals 9:6:6; IR 1820 cm -1 azlactone band). Construction of the Polytris(pentamer) EMI51.1 Polymerization of the tris(pentamer) -This material is dissolved in THF (200 mL) and cooled at 0 C while a solution of tetra-n-butylammonium fluoride (1.0M in THF, 3 mL, 3 mmol) is added. The exotherm is controlled by the rate of addition of the fluoride reagent. The mixture is then heated briefly to 70 C and <Desc/Clms Page number 52> cooled to room temperature. Water (100 mL) is added and the layers are stirred, then separated. The organic phase is dried (sat'd aq NaCI, MgS04), and concentrated in vacuo (18 torr, then 0.1 torr 10 hours) to afford the polymer (3.38 g). This material showed no signals for the tert-butyldimethylsilyl group in the proton NMR spectrum and the azlactone band was absent in the infrared spectrum. Further details on the reaction possibilities for the oxazolone and aminimide compounds can be found in two PCT applications PCT/US93/0--- and PCT/US93/0---, each filed on December 28,1993, and entitled Modular Design And Synthesis of Aminimide-Derived Molecules, respectively. The content of each of those applications is expressely incorporated herein by reference thereto to the extent necessary to understand the metes and bounds of this invention.

Claims: THE CLAIMS What is claimed is: 1. A method of making a polymer having specific physiochemical properties which comprises: forming a first module having a structure which includes at least two structural diversity elements suitable to impart a desired physical property to a polymer which is made from said monomer; and reacting one or more modules to form a polymer having specific physiochemical properties. 2. A method according to claim 1 which further comprises forming the base module from an aminimide compound, an oxazolone compound or derivatives thereof. 3. A method according to claim 1 which further comprises forming the base module by reacting a first compound having at least one structural diversity element and a first reactive group, with a second compound having at least one structural diversity element and a second reactive group, wherein the first and second groups combine by an addition reaction. 4. The method according to claim 3 which further comprises producing the first compound by forming an oxazolone compound having at @ least one structural diversity element .attached thereto. 5. The method according to claim 4 which further comprises providing the second compound as a nucleophile or carbonyl compound which is capable of reaction with the oxazolone contains and which contains at least one structural diversity element. 6. The method according to claim 5 which further comprises combining the first and second compounds to form a base module having one of the following structures: <Desc/Clms Page number 54> EMI54.1 wherein at least two of the unconnected lines are connected to structural diversity elements. 7. The method according to claim 3 which further comprises providing the first compound as an aminimide-forming compound having at least one structural diversity element attached thereto. 8. The method according to claim 7 which further comprises providing the second compound as an oxazolone or ether compound which is capable of reaction with the aminide-forming compound and which contains at least one structural diversity element. 9. The method according to claim 8 which further comprises combining the first and second compounds to form a base module having one of the following structures: EMI54.2 <Desc/Clms Page number 55> EMI55.1 wherein at least two of the unconnected lines are connected to structural diversity elements. 10. The method of claim 9 which further comprises selecting the first and second structural diversity elements to be one of the following: an amino acid derivative of the form (AA)n: a nucleotide derivative of the form (NUCL)n; a carbohydrate derivative of the form (CH)n; an organic moiety of an alkyl, cycloalkyl, aryl, aralkyl or alkaryl group or a substituted or heterocyclic derivative thereof, or of a naturally occurring or synthetic organic structural motif, optionally containing a reporter element, an electrophilic group, a nucleophilic group or a polymerizable group; or a macromolecular component. 11. The method according to claim 3 which further comprises providing at least one of the first and second compounds with at least two structural diversity elements. 12. The method according to claim I which further comprises providing each of the first and second compounds with at least two structural diversity elements. 13. A method according to claim I which further comprises sequentially reacting modules to form the polymer. 14. A method according to claim I which further comprises reacting a plurality of the same modules to form the polymer. <Desc/Clms Page number 56> 15. A method according to claim 1 which further comprises reacting a plurality of different modules to form the polymer. 16. A method according to claim I which further comprises selecting the module to be a derivative or mimic of a peptide, protein, oligonucleotide, oligosaccharide, carbohydrate, pharmaceutical or pharmacophore. 17. A method according to making a polymer having a desired water solubility which comprises: forming a first base module having a having a hydrophobic moiety attached thereto; forming a second base module having a having a hydrophilic moiety attached thereto; and reacting one or more of the first and second base modules to form a polymer having a specific molecular weight, a specific length and a particular water solubility. 18. A method according to claim 17 which further comprises sequentially reacting said modules to control the addition of each modules to the polymer. 19. A method according to claim 17 which further comprises: selecting a first base module having the formula EMI56.1 <Desc/Clms Page number 57> wherein R and R' are the same or different and are alkyl, carboxylic, aryl or an organic moiety exhibiting hydrophobicity; selecting a second base module having the formula EMI57.1 wherein R and R' are the same or different and are alkyl, carbocyclic, aryl or an organic moiety exhibiting hydrophilicity; polymerizing said modules in a manner which is effective to control the addition of each module to a developing polymer chain until a polymer having the desired water solubility is produced. 20. A method according to claim 19 wherein R and R' of the first base module are selected from the group of hydrophobic moieties consisting of long chain alkyl groups. 21. A method according to claim 19 wherein R and R' of the second base module are selected from the group of hydrophilic moieties comprising alkyl, carbocyclic and aryl groups that also contain carboxylic acid groups. 22. A method according to claim 17 which further comprises: selecting a first base module having the formula <Desc/Clms Page number 58> EMI58.1 wherein R and R' are the same or different and are alkyl, carboxylic, aryl or an organic moiety exhibiting hydrophobicity; selecting a second base module having the formula EMI58.2 wherein R and R' are the same or different and are alkyl, carbocyclic, aryl or an organic moiety exhibiting hydrophilicity; polymerizing said modules in a manner which is effective to control the addition of each module to a developing polymer chain until a polymer having the desired water solubility is produced. 23. A method according to claim 22 wherein R and R' of the first base module are selected from the group of hydrophobic moieties consisting of long chain alkyl groups. 24. A method according to claim 22 wherein R and R' of the second base module are selected from the group of hydrophilic moieties comprising alkyl, carbocyclic and aryl groups that also contain carboxylic acid groups. <Desc/Clms Page number 59> 25. A polymer comprising at least three connected modules wherein at least one module has a structure which includes at least two structural diversity elements. 26. A polymer according to claim 25 wherein each module has a structure which includes at least two structural diversity elements. 27. A polymer according to claim 25 wherein the first and last modules have less than two structural diversity elements. 28. A polymer made according to the method of claim 17. 29. A polymer made according to the method of claim 19. 30. A polymer made according to the method of claim 22.

Inventors: HOGAN JOSEPH C JR, HOGAN, JOSEPH, C., JR.
Applicants: ARQULE INC, HOGAN JOSEPH C JR, ARQULE, INC., HOGAN, JOSEPH, C., JR.
Application year: 1994
Main classification: A61K37
IPC codes: A61K38, A61K45, A61K47, C07D263, C07D413, C07K1, C08B37, C08G69, C08G73