Foamed drilling fluids, their process for preparation and the corresponding drilling method

Abstract: The present invention is directed to an aqueous foamed Drilling Fluid for drilling well bores into a subterranean formation, comprising water, at least one clay and at least one foaming agent. According to the invention, it further comprises at least one metal hydroxide. The invention further relates to a method for preparing said foamed drilling fluid.

Description: The present invention is directed to novel foamed drilling fluids, their preparation and their use. The present invention relates also to a method for breaking a foamed drilling fluid. Drilling fluids have been used for decades in the oilfield industry. As it is well known, such fluids are mainly based on a water and clay mixture plus various additives aimed at adjusting their rheology and suspending properties. The general composition and properties of drilling fluids (or drilling muds) are well known of the skilled man and shall not be repeated here. In the past decade, mixed metal hydroxides (or "MMH") have been developed, especially with reference to J.L. Burba et al in USP 4,664,843 and USP 4,790,954. Drilling fluids incorporating MMH are disclosed in EP-A-501069. The said fluids are made of MMH and a mineral clay, especially bentonite, so as to impart the desired rheological properties to the fluid, and of an effective amount of a fluid loss control additive which can be generically described as a carboxymethyl substituted starch (cross-linked or not) or cellulosic compound, having a defined degree of substitution, and water plus other common additives. With that technology, density can be as low as about 8.5 ppg (1.02 g/cm 3 ) without oil or about 7.9 ppg (0.95 g/cm 3 ) with some 40% by volume of emulsified diesel oil. Currently there are not known low density recirculating drilling fluids. In situations where low densities are required, the industry is forced to use air or foam drilling techniques. Foamed drilling fluids are known for instance from US-A-4,092,252 that discloses gas-containing clay free aqueous fluid comprising polyamines and metal hydroxides, suitable fro drilling strata containing high temperature fluids. However, such conventional foamed drilling fluids are normally not circulated. One foam process has been proposed which relies on a pH sensitive foaming agent: the foam is chemically broken on surface with an acid, the solids are removed, the pH is adjusted back to basic then the fluid is refoamed and pumped back downhole. This "chemical" process is of a complex nature, requires additional products to twice adjust the pH, and does not address static suspension of the cuttings or well bore support. Each one of these drawbacks is serious. There exists a definite need in the oilfield industry, and similar industries such as geothermal wells and depleted or low pressure reservoir etc..., for low density drilling fluids. However, this need was never matched in the past, or only with drawbacks so serious that the practical use on the field was barely possible or only with serious associated problems. It is an object of the present invention to provide drilling fluids covering a wide range of low densities, in particular from about 2.0 ppg (0.24 g/cm 3 ) to 8.0 ppg (0.96 g/cm 3 ). It is a further object of the present invention to provide such drilling fluids under the form of a foam. It is a further object of the present invention to provide a method for preparing such drilling fluids, and for using them for drilling operations. A further object of the present invention is to provide a method for mechanically breaking a foamed drilling fluid, which method can be incorporated into the above mentioned method for drilling a well. It has been surprisingly discovered that the use of metal hydroxides in a foamed drilling fluid allows to reach low densities of the foamed fluid while maintaining very efficient rheological and suspending properties. The source of metal hydroxide can be a single metal hydroxide, or a blend of such metal hydroxides, for example aluminium hydroxide and/or magnesium hydroxide and/or similar hydroxides, or mixed metal hydroxides such as disclosed in the prior art, or precursors of such hydroxides (for example a metal oxide to be used in basic conditions). According to a preferred embodiment, said metal hydroxide component is a mixed metal layered hydroxide compound of the following empirical formula: Li m D d T(OH) (m+2d+3+na) A a n , where m represents the number of Li ions present (preferably 0); D represents divalent metal ions such as Mg, Ca, Ba, Sr, Mn, Fe, Co, Ni, Cu, Zn, most preferably Mg, or mixtures thereof ; d is the number of ions of D in the formula, preferably from 0 to about 4, and most preferably about 1 ; T represents trivalent metal ions and may be Al, Ga, Cr or Fe, preferably Al; A represents monovalent or polyvalent anions other than OH ions and may be inorganic ions such as : halide, sulphate, nitrate, phosphate, carbonate, most preferably halide, sulphate, phosphate, or carbonate, or they may be hydrophilic organic ions such as glycolate, lignosulphate, polycarboxylate, or polyacrylates; a is the number of ions of A in the formula ; n is the valence of A ; and where (m+2d+3+na) is equal to or greater than 3. Particularly preferred is the mixed metal hydroxide of the formula Mg Al (OH) 4.7 Cl 0.3 . In their broad sense, the foamed drilling fluids according to the invention shall consist of: at least a "metal hydroxide" as above defined; at least a clay, such as bentonite, or a similar viscosifying agent ; at least a foaming agent ; water ; a foam-generating gas or a blend of such gases, such as air, N 2 , CO 2 , N 2 /CO 2 , etc... Apart from bentonite, similar suitable clays are for example sepiolite, hectorite, attipulgite (said listing being non-exhaustive), in concentration ranges from 3 to 20 pounds per barrel (8.56 g/l to 57.11 g/l). As foaming agent may be used non-ionic to cationic surfactants, in a range of about 0.01 to 1.5 % by volume. The process for generating the foamed drilling fluid shall consist of: blending the "metal hydroxide" component with the clay component, caustic soda or a similar alkali to set up an alkaline pH and water, then introducing an efficient quantity of the foaming agent and an efficient quantity of the foaming gas(es), optionally with appropriate amounts of other additives. The foam may be either formed before the injection or downhole. Among the said additives, one of particular interest is a fluid loss control agent. Suitable fluid loss control agents are for example polyanionic cellulose, starches, carboxycellulose or preferably a fluid loss control agent as described in EP-A-501069, i.e. a carboxymethylated starch or carboxymethylated cellulosic having a controlled degree of substitution. A preferred fluid loss control additive includes carboxymethylated starches where the starch source may be a crosslinked vegetable starch, such as potato, rice, corn, maize, or other starch containing products of carboxymethyl cellulose or an uncrosslinked vegetable starch as set forth above and where the crosslinked vegetable starch has a degree of substitution in the broad range of about 0.3 to about 0.8 and preferably in the narrow range of about 0.4 to about 0.7 ; and where the uncrosslinked vegetable starch and the carboxymethylcellulose have a degree of substitution in the broad range of about 0.3 to 0.57 and preferably in the narrow range of about 0.3 to 0.4. As used herein, the term "uncrosslinked" is intended to mean that the material is substantially free of crosslinking. The starches may be crosslinked or not as desired. Other conventional additives are for example polyanionic cellulose, common anti corrosive agents such as oxygen scavengers and antibacterial agents. According to another aspect of the invention, a well bore drilling process is provided, in which a drilling fluid is pumped under the form of a foam, for example, as described above, circulated downhole and up to the surface where it is mechanically broken, the valuable chemicals on the one side and the cuttings and debris on the other side are recovered, then a foamed drilling fluid is generated again and pumped back into the well. Optionally, the foam is formed in-situ, downhole. Recovered valuable chemicals such as metal hydroxides and especially MMH are most preferably reused in the process. Surprisingly, the present invention provides a low density foamed drilling fluid, as a stable, stiff foam having the desired set of rheological properties, which can be mechanically broken, and can be circulated. By "mechanically broken", it is meant that the foam arriving at the surface is passed through conventional centrifuges or super centrifuges and similar, well-known equipment being present on the drilling rig, with no addition of chemical breakers such as acids. In the considered examples, MMH means an Al/Mg mixed hydroxide of the formula Mg Al (OH) 4.7 Cl 0.3 CCS means a fluid loss control agent consisting of a crosslinked carboxymethylated potato starch having a degree of substitution of 0.56 (such as disclosed in EP-A-501069) Foamant agent means a cationic surfactant (F 078 of the "Compagnie des Services Dowell Schlumberger, a French Registered Company). All lab analysis are as per API RP 13 B where applicable. All mixing was performed on Hamilton Beach Triple Spindle Mixers. The viscosity properties at various sheer rates (RPM of agitation) and other rheological properties were obtained using a fann viscosimeter. Mud weight can be checked using a standard mud scale or an analytical balance. It must be noted that the MMH foam is stiff enough and has sufficient half life to allow the rheology to be checked utilising a standard rheometer. Fluid loss can be checked with a standard API fluid loss cell. Example 1 Formulation # 1 (Order of addition as noted) 1) 116 mls Bentonite, pre hydrated in fresh water 2) 234 mls tap water 3) 1.0 g MMH 4) Caustic solution to pH 11.0 ± 0.2 5) 1.6 mls foamant Shear rates (rpm) 600 Dial reading or "Fann Units" 65 300 45 200 37 100 29 6 14 3 13 10-s Gel Strength 10 lb /100 ft 2 (48.8 kg / 100 m 2 ) 10-min Gel Strength 10 lb /100 ft 2 (48.8 kg / 100 m 2 ) Plastic Viscosity 20cp (20 mPas) Yield Point 25 lb /100 ft 2 (122 kg / 100 m 2 ) Density 3.49 ppg (0.42 g/cm 3 ) API Fluid Loss in 30 min. 11.5 cc Specific gravity 0.42 The foam generated appeared very stiff and would not pour out of the mixing cup without agitation. A formulation identical to formulation #1 except the addition of a fluid loss control additive (4 ppb CCS) produced a 6.8 cc API Fluid loss and a much stiffer foam as noted in the rheology values below. Shear rates (rpm) 600 Fann Units" 175 300 133 200 104 100 89 6 48 3 48 10-s Gel Strength 45 lb /100 ft 2 (219.6 kg / 100 m 2 ) 10-min Gel Strength 75 lb /100 ft 2 (366 kg / 100 m 2 ) Conclusions: The MMH system can easily be foamed producing a fluid of excellent quality. The system appears to produce excellent foam height and an unusually long half life. By adjusting the amounts of foamant and agitation applied, a wide range of densities may be produced. Example 2 Formulation #2: Formulation 2 was identical to Formulation 1 except that the MMH was not added. The resultant foam was thin and began to reduce immediately; Rheology and other properties were not measured as the foam did not last long enough for measurement. Test for Column Height Production and Foam Half Life: Formulation 1 was reduced from a 1 lab bbl formulation to 100 mls for the Column Height Production Test. A good foam should produce an increase in foam height from a base of 100 mls to a height of 300 mls or greater upon the addition of the foamant. 33 mls S18 API grade Wyoming bentonite, pre-hydrated in fresh water 66 mls Tap Water 0.29 g MMH Caustic to pH 11.0 ± 0.2 0.46 mls Foamant Base Vol. 100 mls Head Height after Foamant 350 mls (Petrolite KD-40 of International Drifting Fluids Inc.). The MMH foam produced quite an acceptable foam height. The foam half life (time in minutes for 50% of the original water to breakout) should be no less than 2 1/2 min. The MMH foam produced a half life of slightly more than 3 hours; a very stable foam. Once half life was obtained, the material was placed on a Hamilton Beach Blender for 30 seconds. The foam readily regenerated. Example 3 1. OPTIMUM DOSE OF FOAMING AGENT 1.1 Procedure Five standard MMH muds were mixed and foaming agent was added at the following concentrations: MUD No. 1 2 3 4 5 MMH : ppb (g/l) 1 (2.5) 1 (2.5) 1 (2.5) 1 (2.5) 1 (2.5) Bentonite : ppb (g/l) 10 (25) 10 (25) 10 (25) 10 (25) 10 (25) NaOH ⇒ pH 10.5 ⇒ pH 10.5 ⇒ pH 10.5 ⇒ pH 10.5 ⇒ pH 10.5 Foaming agent/ml 0.1 0.3 0.5 0.7 0.9 1.2 Mixing Procedure Using a Hamilton Beach mixer: 1. Mix Bentonite + Water 5 min @ low speed. 2. Add MMH. 3. Adjust pH ⇒ 10.5. 4. Mix 5 min @ low. 5. Add foaming agent, miss 2 min @ high. 6. Measure Rheology and density. 7. Mix 1 min @ high. 8. Measure water break out. 1.3 Testing Procedure Rheology: Fann 35 @ 122° F (50° C) Density: Use a 10 ml tared syringe to measure wt of 10 ml foam and therefore the equivalent ppg can be determined. Water Breakout: Pour as much of the foam as possible into a 500 ml glass measuring cylinder, measure the foam height, and after 60 min measure any water breakout. 1.4 Optimum Dose Results MUD No. 1 2 3 4 5 Foam Height/mls 380 520 580 630 620 Water Breakout/60 mins 0 0 0 0 0 Rheology 600 rpm 58 96 122 126 115 300 rpm 53 82 100 104 94 200 rpm 50 75 88 94 86 100 rpm 44 67 81 85 80 6 rpm 30 49 43 32 39 3 rpm 28 43 25 24 29 10 s Gel Strength lb/100 ft 2 16 29 45 47 39 kg/100 m 2 78.08 141.52 219.6 229.36 190.32 10 min Gel Strength lb/100 ft 2 15 25 40 45 35 kg/100 m 2 73.2 122 195.2 219.6 170.8 Density ppg 7.85 5.03 4.87 4.44 4.79 g/cm 3 0.94 0.60 0.58 0.53 0.57 1.5 Conclusions A dose of 0.7 mls of foaming agent gave the greatest amount of foam and was the least dense. 2. FOAM STABILITY Three tests were to be used to gauge the stability of foam MMH. 2.1 Test 1 2.1.1 Procedure 1. Mix foam MMH as before but at these concentrations: Bentonite = 12 ppb (34.26 g/l) MMH = 1.2 ppb (3.43 g/l) Foaming agent = 1 ml 2. Check density of foam. 3. Pour into 500 ml measuring cylinder and measure foam generated. 4. Record Water Breakout/30 min. 5. Mix by inversion of cylinder. 6. Pour into bomb and hot roll @ 150°F (65°C) for 16 hrs. 7. Pour into cylinder and measure water breakout and appearance. 2.2 Test 2 - Procedure 1-5 As Test 1. 6. Pour into bomb and static age @ 150°F (65°C) for 16 hrs. 7. As Test 1. 2.3 Test 3 2.3.1 Procedure 1. Mix 2 BBL of Test 1 formulation. 2. Check density. 3. Using a Marsh funnel, pour foam through screen and catch in funnel. 4. Empty into beaker and check density. 5. Repeat steps 3+ 4 (7-10 times). 6. Re-mix mud to refoam. 7. Check density. 2.3.2 Results BEFORE HOT ROLL TEST 1 2 Foam Density 5.49 ppg (0.66 g/l). 5.61 ppg (0.67g/l) Foam Vol./mls 550 Vol. 500 mls 30 min Water Breakout 0 0 Appearance After Hot Roll Mud seems to have lost some volume. It has more "liquid" properties - not as stiff as before hot roll (BHR) foam. Foam is more pourable and seems to have held together. Density = 7.1 ppg. (0.85 g/l) After Static Ageing Mud looks as it did when put in. It didn't pour - had to be scraped out into cylinder where about 85 mls H 2 O was visible. 2.4 Test 4 ppg g/l Density after mixing/ppg 4.43 0.53 Density after 1 pass through screen 5.56 0.67 Density after 2 passes through screen 5.50 0.60 Density after 3 passes through screen 5.44 0.65 Density after 4 passes through screen 5.69 0.68 Density after 5 passes through screen 5.48 0.66 Density after 6 passes through screen 5.34 0.64 Density after 7 passes through screen 5.31 0.64 Density after remixing 2 min on HB @ high speed 5.13 0.61 Density after remixing 2 min on Silverson @ 6000 rpm 4.77 0.57 2.5 Conclusions Foamed MMH after hot rolling seemed to hold together as a mud system with no water breakout but it did gain density. It was also a lot more pourable than BHR foam which was probably due to foam being less aerated. After static ageing, the foam had stayed in place but there has been water breakout which could be a problem in the field. The stability of the foam to being put through a screen was high. Although there was an initial increase in density that was due to the big bubbles being knocked out of the foam. The foam was very stable after that. It was also shown that the foam could refoam. Example 4 FOAMED MMH MUD - FULL SCALE TESTING Objective: Based on the above lab data, it appears that a conventional MMH mud system can be foamed utilising a standard oil field foamant producing a functional recirculating drilling fluid of a density substantially lower than that of water. A full scale circulating system test was required to establish the viability of the concept. this test was designed to evaluate the potential for the following: 1. The ability to foam the MMH mud. 2. The ability to de-foam the mud, increasing it's density to a pumpable level using conventional solids control equipment; i.e., single deck shaker and med speed centrifuge. 3. The ability to pick up the de-foamed mud with a triplex pump. Mixing and Pumping: A total of 40 BBL of MMH mud was mixed as follows: Bentonite 440 lbs (199.76 kg) MMH 50 lbs (22.7 kg) NaOH to pH 12.8 Fresh water 40 barrels (6.360 l). Foaming agent 14 litres (0.3%) The pumping schedule as below: Pumping Schedule: Pressure test the lines up to 5000 psi (2.39 10 5 Pa). Start pumping MMH at rate of 0.5 bpm through 1.5" CTU REEL @ 2000 psi (0.957 10 5 Pa). After pumping 5 BBL (14.2 g / l) of mud, Nitrogen introduced to the system through foam generator at rate of 200 SCF per min, maintaining the same pumping rate at 0.5 bpm and pumping pressure increased to 4000 psi (1.915 10 5 Pa). At the end of 12 BBL (34.26 g / l) nitrefied mud return observed on the shale shaker, the return was slugs of gas and clear mud without any foam. Stop pumping and add surfactant to the system 0.3% of foaming agent. Pump 5 BBL (14.2 g / l) of mud at rate of 0.5 bpm @ 2000 psi (0.957 10 5 Pa). Introduce the nitrogen at rate of 200 SCF per min to achieve 65% foam quality @ 4300 psi (2.058 10 5 Pa). After pumping 14 BBL (40 g / l) of nitrefied mud return observed on the shale shaker, the return has very high rheology, showing uniform and very stable foam Return line Choke manifold pressure maintained at 500 psi (0.24 10 5 Pa). The return density measured and found equal to 3.7 ppg (0.44 g / l). By passing the stable foam through the centrifuge the density increased up to 5.5 ppg (0.66 g/l). Sampling was attempted for MMH mud both with and without foamant. Ax samples are without foamant while Bx samples contain 0.3% foamant. The sampling points were: 1. Mix tank 2. Post coil tubing 3. Pre shaker screen 4. Post centrifuge. Sample/Property A1 A2 A3 A4 B1 B2 B3 B4 Rheology (Fann Unit) 600 rpm 88 77 57 178 79 300 rpm 61 57 40 142 61 200 rpm 48 47 35 128 38 100 rpm 39 39 29 92 29 6 rpm 25 24 19 45 18 3 rpm 10 9 6 45 13 10 s Gel Strength lb/100 ft 2 11 12 7 82 22 kg/100 m 2 53.68 58.56 34.16 400.16 107.36 Density ppg 7.91 8.32 8.27 8.52 3.6 3.14 5.5 g/l 0.95 1.00 0.99 1.02 0.43 0.38 0.66 Note: the density in the coil was measured at 4.72 ppg by extraction of a sample and direct measurement Half life was determined using a 500 ml graduate. Sample B2 B4 start time 11:30 am 9/4/94 12:30 pm start vol. mls 535 500 stop time 9:00 am 11/4/94 9:00 am 11/4/94 elapsed time 45.5 hrs 44.5 hrs total vol. at end mls 350 mls 500 foam vol. at end mls 230 mls 340 water break out at end in mls 120 mls 160 Half life was not reached on either sample. Conclusions and Recommendations: Each objective was reached. The MMH mud can be foamed utilising foamant. De-foaming was not completely accomplished utilising the available equipment. The single deck shaker was found to be somewhat useless, however, in retrospect the mud was mixed twice as thick as would normally be necessary. The centrifuge did produce a density increase of 2.0 ppg (0.24 g / l) in one pass. Even with the foam as stiff as it was, the C-pump picked up and delivered the foam to the centrifuge with no problem. Subsequent passes through the centrifuge produced no increase in density indicating that the G-force of the unit was most likely responsible for the density change. Example 5 5.1 Preparation of single metal hydroxides Single metal hydroxides were made in the lab using the reactions below which precipitate out the insoluble metal hydroxide. 1. Mg SO 4 . 7 H 2 O + 2 NaOH  Mg (OH) 2 + Na 2 SO 4 + 7 H 2 O 2. Al 2 (SO 4 ) 3 . 16 H 2 O + 6 NaOH  2 Al (OH) 3 + 3 Na 2 SO 4 + 16H 2 O The reaction was carried out by dissolving the metal sulphate in water. The sodium hydroxide was then added to precipitate out the metal hydroxide. The resultant solution was filtered, washed and dried in oven at 105° C. 5.2 Formulations Fresh water 350.0 g Bentonite (dry) 12.0 g Metal hydroxide 1.2 g Foamant 1.0 ml 5.3 Results 5.3.1 Magnesium hydroxide Unfoamed Foamed Temperature 50°C Ambient Rheology (Fann Unit) 600 rpm 57 149 300 rpm 52 129 200 rpm 47 117 100 rpm 41 110 6 rpm 27 78 3 rpm 20 34 10 s Gel Strength 76.1 kg/100 m 2 10 min Gel Strength 110.9 kg/100m 2 Foam volume : start 450 ml 18 hours 450 ml Water break out 10 ml This combination worked giving a good foam ; however the foam was not as stiff as the MMH foam. 5.3.2 Aluminium hydroxide Unfoamed Foamed Temperature 50°C Ambient Rheology (Fann Unit) 600 rpm 105 112 300 rpm 96 91 200 rpm 88 81 100 rpm 80 79 6 rpm 40 38 3 rpm 22 28 10 s Gel Strength 147.8 kg/100 m 2 152.3 kg/100 m 2 10 min Gel Strength 147.8 kg/100 m 2 147.8 kg/100 m 2 Foam volume : start 470 ml 18 hours 470 ml Water break out 30 ml This combination gave a stiffer foam than the magnesium foam but it was still not as stiff as the MMH foam.

Claims: An Aqueous Foamed Drilling Fluid for drilling well bores into a subterranean formation, comprising water, at least one clay and at least one foaming agent, characterized in that it further comprises at least one metal hydroxide. Drilling fluid according to claim 1, characterized in that the said metal hydroxide is selected among: single metal hydroxide(s) mixed metal hydroxides ("MMH") precursors of metal hydroxide(s) blends thereof. Drilling fluid according to claim 1 or 2, characterized in that the mixed metal hydroxide(s) or MMH hydroxide compound are of the following empirical formula : Li m D d T(OH) (m+2d+3+na) A a n , where m represents the number of Li ions present ; preferably 0 D represents divalent metal ions such as Mg, Ca, Ba, Sr, Mn, Fe, Co, Ni, Cu, Zn, most preferably Mg, or mixtures thereof, d is the number of ions of D in the formula, preferably from 0 to about 4, and most preferably about 1, T represents trivalent metal ions and may be Al, Ga, Cr or Fe, preferably Al, A represents monovalent or polyvalent anions other than OH ions and may be inorganic ions such as : halide, sulphate, nitrate, phosphate, carbonate, most preferably halide, sulphate, phosphate, or carbonate, or they may be hydrophilic organic ions such as glycolate, lignosulphate, polycarboxylate, or polyacrylates, a is the number of ions of A in the formula, n is the valence of A ; and where (m+2d+3+na) is equal to or greater than 3. Drilling fluid according to any of the preceding claims, characterized in that the metals are selected among Al and/or Mg. Drilling fluid according to any of claims 1 to 4, characterized in that the metal hydroxide is an MMH of formula Mg Al (OH) 4.7 Cl 0.3 Drilling fluid according to any of the preceding claims, characterized in that it further comprises a fluid loss control agent Drilling fluid according to any of the preceding claims, characterized in that said fluid loss control agent is selected among: carboxy methyl starch, cross linked or not carboxy methyl cellulosic compounds having a low degree of substitution. Drilling Fluid according to any of the preceding claims, characterized in that the clay is in concentration ranges from 8.56 to 57.11 g/l. Drilling Fluid according to any of the preceding claims, characterized in that the foaming agent is in concentration ranges from 0.01 to 1.5% per volume. Drilling Fluid according to any preceding claim characterized in that the foam generating gas is selected among air, CO 2 , N 2 and their mixtures. A Method for preparing a foamed drilling fluid according to any of preceding claims, characterized in that it consists of: blending the "metal hydroxide" component with the clay or similar component caustic soda or a similar alkali to set up an alkaline pH water then introducing an efficient quantity of the foaming agent and an efficient quantity of the foaming gas(es), optionally with appropriate amounts of other additives. A method for drilling a well bore into a subterranean formation, characterized in that a foamed drilling fluid according to any one of claims 1 to 10 is injected into the well bore. A method for drilling a well bore into a subterranean formation, comprising the steps of injecting a fluid comprising water, at least one clay and at least one metal hydroxide/or metal hydroxide precursor(s) and then introducing a foam generating gas for forming a foam downhole. A method for drilling a well bore according to claim 12 or 13, further comprising the step of mechanically breaking the foam after it arrives at the surface. A method for drilling a well bore according to claim 14, wherein the foam is mechanically broken when passing through such an equipment as a centrifuge or a super centrifuge. Method according to anyone of claims 12 to 15 further comprising the step of recovering the valuable chemicals on the one side and the cuttings and debris on the other side, and the de-foamed mud is picked-up by a pump. Method according to anyone of claims 12 to 16 further comprising the step of re-foaming the drilling fluid and circulate it back into the well bore.

Inventors: WILLIAMSON LARRY DON, WILLIAMSON, LARRY DON
Applicants: SCHLUMBERGER CIE DOWELL, SOFITECH NV, COMPAGNIE DES SERVICES DOWELL SCHLUMBERGER S.A., SOFITECH N.V.
Application year: 1994
Main classification: C09K7
IPC codes: C09K8