CYCLOPYMERIZATION POLYMERS FROM NON-CONJUGATED DIENES

Abstract: Novel polymer and copolymer compositions produced from the polymerization of non-conjugated dienes have been found. The novel compositions are produced by an equally novel process comprising cyclopolymerization of non-conjugated dienes employing reduced valence state Group VIB metal oxide catalyst on porous support. The preferred catalyst comprises carbon monoxide reduced chromium on silica. Copolymers are formed by copolymerization of non-conjugated dienes with 1-alkenes in contact with the activated chromium on silica catalyst. The compositions are useful as lubricants and additives.

Description: NOVEL CYCLOPOLYMERIZATION POLYMERS FROM NON-CONJUGATED DIENES This invention relates to novel polymer and copolymer compositions produced from the polymerization of non- conjugated symmetrical or unsymmetrical dienes and to the novel process for their production. The invention specifically relates to the cyclopolymerization of non- conjugated dienes employing reduced chromium on silica as catalyst and to copolymers formed with 1-alkenes. The compositions are useful, inter alia, as lubricants and additives. The polymerization of non-conjugated dienes to form polymers and copolymers that incorporate recurring units of cyclic moieties in the polymer or copolymer backbone is known. While it had been presumed that polymerization of non-conjugated dienes produces only cross-linked polymers, cyclopolymerization of diallyl quarternium salts to linear polymers was first reported by G. B. Butler in 1947 (J. Amer. Chem. Soc, 71, 3120). Since then, a large variety of non-conjugated dienes have been reported to undergo cyclopolymerization. For symmetrical, non-conjugated dienes, it has been shown that all of the well-known methods of polymerization can be employed to initiate cyclopolymerization. Polymerization by free radical initiation, cationic and anionic initiation have been demonstrated. Cyclopolymerization of divinyl benzene has been accomplished using Ziegler-Natta catalysis. Copolymerization of non-conjugated dienes with vinyl monomers is also known (G. B. Butler, et al., J. Poly. Sci. 48, 279 (I960)). Depending upon the comonomer pair and the copolymerization conditions, the product copolymer may contain recurring units of ring moieties plus vinyl moiety or the vinyl and diene moiety may combine to form a common recurring ring moiety. Additional examples of cyclopolymerization are abundant in the chemical literature. The technology is summarized in the Encyclopedia of Polymer Science and Engineering, Vol. 4, 1986, pp 543-598. Recently, a novel catalyst system has been reported (US Patent Nos. 4,827,064 and 4,827,073 to M. Wu) which has been found to be particularly effective for the polymeriza¬ tion and copolymerization of 1-alkenes. The catalyst is used for the preparation of superior hydrocarbon lubricants having low methyl to methylene branch ratio by oligomeriza- tion of alpha olefins. The catalyst comprises reduced valence state Group VIB metal oxide catalyst on porous sup¬ port. The specific method for lubricant preparation employs as catalyst an activated chromium catalyst comprising carbon monoxide reduced chromium on a silica support. The novel lubricant compositions which can be produced by activated chromium on silica catalysis comprise polyalpha- olefins polymers and/or copolymers. Although the versatility and effectiveness of activated chromium on silica catalysis for 1-alkene polymerization and benzene alkylation has been well documented, little has been known relative to the reactivity of the catalyst with polyenes, particularly non- conjugated dienes. Despite the abundance of research conducted on cyclopolymerization, activated chromium on silica catalyst has not been reported in the prior art as a catalyst for aliphatic non-conjugated diene cyclopo¬ lymerization. Indeed, the uniqueness of the activated chromium catalyst has tended to inhibit those skilled in its use to conclude how it would function in diene polymerization compared to known cyclopolymerization catalysts. Accordingly, the fact, as presented herein, of the activity of reduced chromium on silica catalyst in non- conjugated diene polymerization represents a distinctly unanticipated discovery. Novel polymer and copolymer compositions produced from the polymerization of non-conjugated dienes have been formulated. The novel compositions are produced by an equally novel process comprising cyclopolymerization of non-conjugated dienes employing reduced valence state Group VIB metal oxide catalyst on porous support. The preferred catalyst comprises carbon monoxide reduced chromium on silica. Copolymers are formed by copolymerization of non- conjugated dienes with 1-alkenes in contact with the activated chromium on silica catalyst. The compositions are useful as lubricants and additives. More particularly, an atactic polymeric hydrocarbon composition useful as a lubricant has been produced comprising randomly recurring 1-methylene 3-cycloalkyl units. The composition has a bromine number of at least 1.5 and at least one terminal vinylidene olefin group. The recurring unit has the following structure: The composition contains recurring units having cis and trans isomers of the R. and R 2 groups. The process for the production of the polymeric hydrocarbon composition comprises contacting at least one non-conjugated diene having the structure wherein R 3 comprises alkyl or hydrogen and x is 1-3, with a reduced valence state Group VIB metal catalyst on a porous support under polymerization conditions whereby the polymeric hydrocarbon composition is produced having a molecular weight of at least 1000. The preferred catalyst comprises Cr0 3 supported on silica having a pore size of at least 4 nm (40 Angstroms) and reduced by CO or H 2 containing gas or metal alkyl reducing agent. Hydrocarbon lubricants are produced by a process comprising copolymerizing a mixture comprising between 1 and 99 weight percent of a non-conjugated diene having the foregoing depicted structure, and between 1 and 99 weight percent of at least one C 3 -C 10 1-alkene in contact with a reduced valence state Group VIB metal catalyst on a porous support under copolymerization conditions; and separating a C 30 + lubricant fraction. The cyclopolymerization reactions of the instant invention are catalyzed by supported metal oxide catalysts, such as Cr compounds on silica or other supported IUPAC Periodic Table Group VIB compounds as described in U. S. Patent 4,827,064 to M. Wu. The catalyst most preferred is a lower valence Group VIB metal oxide on an inert support. Preferred supports include silica, alumina, titania, silica alumina, magnesia and the like. The support material binds the metal oxide catalyst. Those porous substrates having a pore opening of at least 4 nm (40 Angstroms) are preferred. The support material usually has high surface area and large pore volumes with average pore size of 4 to 35 nm (40 to about 350 Angstroms) . The high surface area are beneficial for supporting large amount of highly dispersive, active chromium metal centers and to give maximum efficiency of metal usage, resulting in very high activity catalyst. The support should have large average pore openings of at least 4 nm (40 Angstroms) , with an average pore opening of >6 to 30 nm (>60 to 300 Angstroms) preferred. For this catalyst to be used in fixed bed or slurry reactor and to be recycled and regenerated many times, a silica support with good physical strength is preferred to prevent catalyst particle attrition or disintegration during handling or reaction. The supported metal oxide catalysts are preferably prepared by impregnating metal salts in water or organic solvents onto the support. Any suitable organic solvent known to the art may be used, for example, ethanol, methanol, or acetic acid. The solid catalyst precursor is then dried and calcined at 200 to 900°C by air or other oxygen-containing gas. Thereafter the catalyst is reduced by any of several various and well known reducing agents such as, for example, CO, H 2 , NH 3 , H 2 S, CS 2 , CH 3 SCH 3 , CH 3 SSCH 3 ,metal alkyl containing compounds such as R 3 A1, R 3 B,R 2 Mg, RLi, R 2 Zn, where R is alkyl, alkoxy, aryl and the like. Preferred are CO or H 2 or metal alkyl containing compounds. Alternatively, the Group VIB metal may be applied to the substrate in reduced form, such as Cr(II) compounds. The catalyst can be used in a batch type reactor or in a fixed bed, continuous-flow reactor. In general the support material may be added to a solution of the metal compounds, e.g., acetates or nitrates, etc. , and the mixture is then mixed and dried at room temperature. The dry solid gel is purged at successively higher temperatures to about 600°C for a period of about 16 to 20 hours. Thereafter the catalyst is cooled down under an inert atmosphere to a temperature of 250 to 450"C and a stream of pure reducing agent is contacted therewith for a period when sufficient CO has passed through to reduce the catalyst as indicated by a distinct color change from bright orange to pale blue. Typically, the catalyst is treated with an amount of CO equivalent to a two-fold stoichiometric excess to reduce the catalyst to a lower valence Cr(II) state. Finally, the catalyst is cooled to room temperature and is ready for use. The non-conjugated dienes useful in the present invention include those C 6 + non-conjugated aliphatic hydrocarbon dienes wherein at least one of the olefinic bonds is an alpha olefin. The second olefinic bond may be an internal olefin or an omega, i.e., terminal olefinic bond. The terminal olefinic bond may be substituted on the penultimate carbon atom with an alkyl group, thereby forming a vinylidene terminal group. Suitable alkyl substituent groups on the penultimate carbon atom include C--C 12 alkyl groups with methyl ethyl, propyl and butyl being preferred. Methyl is the most preferred. The non- conjugated dienes particularly useful in the present invention have the structure wherein R 3 comprises alkyl or hydrogen. Non-conjugated dienes useful in the present invention include 1,4-hexadiene, 1,5-hexadiene, 4-methyl-l,5- hexadiene, 1,7-octadiene and 1,9-decadiene. Non-conjugated dienes, such as 1,5-hexadiene, 1,4-hexadiene and substituted 4-methyl-l,5-hexadiene or the longer alkadienes can be polymerized by a reduced chromium on silica catalyst to yield novel polymers with unique structures and properties. The polymerization of the non-conjugated dienes proceeds via cyclopolymerization of the dienes polymers, some of which have the following structure: where m is 1-3, n is 1-1000, R. and R 2 groups are alkyl or hydrogen with at least one of the R. and R 2 groups comprising hydrogen,and a is 1-3. The polymer is atactic with the cycloalkyl moiety randomly distributed throughout the polymer backbone. There is no consistent pattern of head-to-tail cyclopolymerization. Depending on the degree of polymerization, the products can be recovered as liquids or solids. It has also been discovered that non-conjugated dienes can be copolymerized with 1-alkenes, i.e., alpha olefins, in contact with reduced chromium on silica catalyst to produce copolymers containing randomly recurring cycloalkyl groups and 1-alkene moieties. C 3 -C 12 are useful comonomers for copolymerization with C 6 + non-conjugated aliphatic hydrocarbon dienes to produce the cyclopolymerization copolymers of the invention. The preferred alpha olefins include propylene and 1-butene. 1-decene is the most preferred. The cyclopolymerization and copolymerization process of the invention can be carried out at temperatures between 0°C and 300"C. The preferred temperature for homopolymerization of non-conjugated dienes is between 25°C and 200°C while the preferred temperature for copolymerization with 1-alkenes is between 25 °C and 200°C. The cyclo-polymerization of diene by itself or copolymerization with alpha-olefin over activated chromium on silica catalyst is very unexpected. The reaction is not previously reported and the products with unique chemical structures have unusual properties for application as lubricants, additives or chemical intermediates. The following Examples are provided to illustrate the instant invention. The active chromium on silica catalyst used in the following Examples of cyclopolymerization was prepared as generally described herein and specifically described in Examples 1 or 4 of U. S. Patent 4,827,064. Example 1 Polymerization of 1,5-hexadiene 50 grams of 1,5-hexadiene in 120 gram hexane solvent and 10 grams of an activated Cr/Si02 catalyst were mixed and heated to about 60"C for 16 hours. The product was isolated in 20% yield by filtration to remove the catalyst and distilled to remove the light end. The product was recovered as a clear, semi-solid and had a molecular weight (MW) of about 1000 by GPC using polystyrene as calibration standards. The solid has the following polymeric structure as determined by 13 C NMR, the results of which are presented in Table 1: The structure is consistent with formation from cyclization of the 1,5-hexadiene over the catalyst. The polymer also had a small amount of unsaturated double bonds at the end of each polymer chain. Table 1 Chemical shift Relative Chemical shift Relative (in ppm) intensity in ppm intensity 24.80 146878 28.447 178717 29.785 224112 31.415 269853 31.658 171668 32.072 169424 32.218 173894 32.607 289969 32.948 683349 33.483 261031 33.726 376643 33.896 306500 36.329 153019 37.058 171026 37.326 602095 37.642 314152 37.813 257264 38.664 367105 38.786 397618 43.432 160422 43.626 202057 The small amount of unsaturated carbons have 13 C NMR at 114.12 114.825, 129.882, 140.245 and 144.453 ppm. Copolymerization of non-conjugated dienes with 1- decene using activated chromium on silica catalyst produces copolymer products with important lubricant properties. Various dienes were copolymerized with l-decene as depicted in Example 2 and 3 to produce lubricants with unexpectedly high viscosity indices. The results are tabulated in Tables 2 and 3. Copolymers of dienes and 1-alkenes can be produced from mixtures containing between 1 and 99 weight percent non-conjugated diene and 1-99 weight percent 1-alkene. Example 2 Copolymerization of Dienes with l-decene 10 grams of various dienes and 90 grams of l-decene grams were mixed with five grams of activated Cr/Si02 catalyst and heated to 55°C for 16 hours. The product was isolated by filtration and distillation to remove light ends. The reaction yields and lube product properties are summarized in Table 2. Table 2 Reaction Conditions, Yields and Product Properties Run no. 2A 2B 2C diene 1,9-decadiene 1,7-octadiene 1,5 hexadiene none weight of diene 10 grams 10 grams 10 grams 0 weight of l-decene 90 grams 90 grams 90 grams 100 gram lube yield, wt% 36 48 69 >90 lube properties Vise at 100°C, 638.78 1689.39 409.1 ~ 1000 mm 2 /s Vise at 40°C,mm 2 /s 7279.22 26948.94 6120.62 VI 283 306 227 Bromine No. 9 4 5 <2 The lubricant product produced in this manner has high VI and high bromine number, indicating a high degree of unsaturation. Compared to the run without diene, the lube product will have a bromine number of <2. This unsaturation is useful for further functionalization, for example, to couple with maleic anhydride for ashless detergent synthesis. Example 3 Copolymerization of 1-butene with 1,5-Hexadiene 1,5-hexadiene and 1-butene of different proportion were added to an autoclave at 140°C. The reaction conditions, liquid product properties and yields are summarized in Table 3. The products produced from copolymerization of diene have higher bromine number than -li¬ the product without diene addition. This unsaturation is useful for other functionalization reaction. Table 3 Copolymerization of 1-butene with 1,5-Hexadiene Sample No. 3A 3B 3C 3D 3E 3F 3G Reaction Conditions Temp, °C 140 140 140 140 140 140 140 Feed Rates 1-C4, g/hr 120 120 120 120 120 60 60 1,5 Hexadiene 0 13.8 13.8 13.8 13.8 22 22 molar ratio of diene/1-butene 0 0.08 0.08 0.08 0.08 0.25 0.25 conversion to 94 83 77 67 100 100 100 liq. Liquid composition C 12- 11 3 5 8 7 C 12-20 7 18 6 7 8 14 C20-30 6 6 10 10 9 C30+ 76 82 86 78 74 71 C30+ Residue properties V100°C, mm 2 /s 69.96 72.94 59.19 67.16 44.97 40.4 33.59 V40°C, 2191.63 2010.95 1788.3 1949.31 1222.12 838.03 635.77 VI 81 90 75 84 68 84 81 Bromine no C30+ residual 11 26 33 29 32 31 40 distillate 74 78 67 67 76 63 80 % 1,5HD- cyclization 0 87 84 84 81 93 90 Unexpectedly, the process of the invention polymerizes non-conjugated dienes via cyclopolymerization even when the dienes are a combination of alpha olefin and internal olefin. Example 4 presents the polymerization of 1,4- hexadiene as an illustration of this capability of activated chromium on silica support. Example 4 1,4-hexadiene Polymerization over Cr/Si02 Catalyst. 1,4-Hexadiene polymerized over an activated Cr/Si02 catalyst to give a solid polymer, the results of which are presented in Table 4. The polymer is a cyclo-polymerized product and is a solid at room temperature. The product structure was confirmed by 1 H-NMR and 13 C-NMR. The proton NMR showed that the product polymer contained very little olefinic double bond unsaturation. This is important evidence that the product was a cyclic product with no olefinic double bond remaining in the structure. Based on the proton NMR, it was calculated that at least 80% of the diene produced cyclic product. Furthermore, the spectra indicated that the cyclic product had no structural regularity. The backbone of the polymer was atactic and contained cis and trans cyclic polymer with no head-to-tail regularity. The product has a low molecular weight and a relatively narrow molecular weight distribution which rules out the possibility of a cross linked polymer structure. The product is very unexpected because internal olefins are usually inert toward the Cr/Si02 catalyst. However, in the present case, the internal double bond participated in the polymerization reaction and, even more surprisingly, the two double bonds cyclized to give an unusual polymer useful as additives for lube or plastic processing. The polymerization reaction of 1,4-hexadiene was carried out by addition of 2.5 g of catalyst to 10 g of 1,4-hexadiene in a 50 ml-Schlenk flask at 60°C. The reaction mixture was stirred for 2 hour and the polymer became viscous and solidified when cooled to room temperature. Hot tetrahydrofuran was used to dissolve the polymer. The solution was filtered to remove the catalyst. After evaporation of solvent, the product was dried in vacuum to give 6 g of white solid. Table 4 1,4-hexadiene Polymerization over Cr/Si02 Catalyst Run No 4A 4B 4C Reaction Temp.°C 90 60 70 Conversion,wt% 16 60 58 Product MWn 2000 4000 2900 MWw/M n 3 5 3.4 Internal olefins that can be employed in the present invention include those having the structure where y is 1-3 and z is at least 1. Substituted dienes can also be utilized in the process of the invention to produce polymers by cyclopolymerizat¬ ion. Example 5 depicts this capability by the polymerization of 4-methyl-l,5-hexadiene (MND) in contact with activated chromium catalyst on silica support. The results are tabulated in Table 5. Example 5 2-Methyl-l,5-hexadiene (MHD) polymerization over Cr/Si02 MHD polymerized over Cr/Si02 catalyst to give a liquid product with cyclized structure in the polymer backbone. The product structure was confirmed by 1 H-NMR and 13 C-NMR spectra. The proton NMR spectrum showed that the product polymer contained very little unsaturation. This is important evidence that the product is a cyclized polymer with little olefinic double bond unsaturation left in the polymer. Based on X H-NMR integration, it was calculated that at least 70% of the second double bond participated in the cyclization reaction. Furthermore, the polycyclic product has no structural regularity. The backbone of the polymer was atactic with no head-to-tail regularity and contained both cis and trans isomers. The polymerization reaction of 2-methyl-l,5-hexadiene was carried out by addition of 2.0 g of catalyst to 10 g of 2-methyl-l,5-hexadiene in a 50 ml-Schlenk flask at 80°C. The reaction mixture was stirred at 80°C for 20 hours. The mixture was filtered to remove catalyst. The filtrate was distilled to remove any volatile light fractions to yield 0.75 g of colorless oil. The analytical results are presented in Table 5. The liquid polymer is much more viscous at room temperature than polymers of similar molecular weight from l-decene. The polymer product can be used as VI improver or lube basestock with novel properties. Table 5 Polymerization of MHD over Cr/Siθ2 catalyst Run No 5A 5B Reaction Temp.°C 90 80 Conversion, wt% 10 7.5 M n 1000 1100 M w/M n 3 3 MHD and similarly substituted non-conjugated dienes can also be copolymerized with 1-alkenes over Cr/Si0 2 catalyst, analogous to the capability of unsubstituted dienes in the present invention. Example 6 depict this capability with results presented in Table 6. Example 6 Copolymerization of 4-methyl-l,5-hexadiene (MHD) and l-decene The copolymerization reactions were carried out by addition of catalyst (10-15% by wt.) to the mixture of 1- decene and the diene. The diene:decene ratio employed were 0:100, 5:95, 10:90, 100:0, as presented in Table 6 along with reaction temperature and results. The product was isolated by filtration and vacuum distillation to remove catalyst and volatile light fractions. The products are colorless oils with analysis shown in Table 6. Table 6 Run No. 6A 6B 6C 6D Reaction temp. °C 75-80 75-80 75-80 90 wt% MHD 0 5 10 100 wt% 1- decene 100 95 90 0 Conversion wt% 93 60 50 10 Product M n 4800 2700 1500 1000 Bromine No 15 15 20 — The bromine numbers of the runs of Example 6 with diene incorporation show higher bromine number than without any diene addition. The cyclo-polymerization of diene over an activated chromium on silica catalyst produced novel polymer with cyclic structure in the backbone or with higher degree of unsaturation. This cyclic polymers have unusual properties and can be used in lube or plastic additives. The polymers with higher degrees of unsaturation may also be used as starting material for additive synthesis.

Claims: CLAIMS : 1. An atactic polymeric hydrocarbon composition useful as a lubricant comprising randomly recurring 1-methylene 3-cycloalkyl units, the composition having a bromine number of at least 1.5, at least one terminal vinylidene olefin group and the recurring unit having the structure where m is 1-3, n is 1-1000, R x and R 2 groups are alkyl or hydrogen with at least one of the R x and R 2 groups comprising hydrogen,and a is 1-3. The hydrocarbon composition of claim 1 wherein the composition contains recurring units having cis and trans isomers of the R. and R 2 groups. The composition of claim 1 having a molecular weight of at least 1000. 4. The composition of claim 1 wherein the cycloalkyl comprises cyclopentyl and the composition exhibits the following 13 C NMR spectra: Chemical shift Relative Chemical shift Relative (in ppm) intensity intensity 24.80 146878 28.447 178717 29.785 224112 31.415 269853 31.658 171668 32.072 169424 32.218 173894 32.607 289969 32.948 683349 33.483 261031 33.726 376643 33.896 306500 36.329 153019 37.058 171026 37.326 602095 37.642 314152 37.813 257264 38.664 367105 38.786 397618 43.432 160422 43.626 202057 with unsaturated carbons have C13 NMR at 114.12 114.825, 129.882, 140.245 and 144.453 ppm. 5. The composition of claim 1 wherein the cycloalkyl comprises cyclohexyl or cycloheptyl. The composition of claim 1 wherein the randomly recurring units of cycloalkyl comprise cyclopentyl, cyclohexyl and/or cycloheptyl. The composition of claim 4 wherein R x or R 2 is methyl, The composition of claim 1 also containing randomly recurring units of l-alkene. The composition of claim 8 wherein the l-alkene is selected from C 3 _C 10 l-alkene. 10. A process for the production of the polymeric hydrocarbon composition of claim 1 comprising contacting at least one non-conjugated diene having the structure wherein R 3 comprises alkyl or hydrogen with a reduced valence state Group VIB metal catalyst on a porous support under polymerization conditions. 11. The process of claim 10 wherein the metal catalyst comprises Cr0 3 on silica support having a pore size of at least 40 Angstroms, the catalyst reduced by carbon monoxide, hydrogen containing gas or metal alkyl reducing agent. 12. The process of claim 10 wherein the polymerization conditions comprise temperature between 25°C-and 200°C. 13. The process of claim 10 wherein the temperature is between 50°C and 95°C. 14. The process of claim 10 wherein the non-conjugated diene is selected from 1,4-hexadiene, 1,5-hexadiene, 4-methyl-l,5-hexadiene, 1,7-octadiene and 1,9- decadiene. 15. A process for the production of hydrocarbon lubricant, comprising copolymerizing a mixture comprising between 1 and 99 weight percent of a non-conjugated diene having the structure wherein R 3 is alkyl and x is 1-3, and between 1 and 99 weight percent of at least one C 3 -C 10 l-alkene in contact with reduced Cr0 3 on silica support having a pore size of at least 4.0 nm under copolymerization conditions; and separating a C 30 + lubricant fraction containing randomly recurring units of cyclic hydrocarbon moieties. 16. The process of claim 15 wherein the catalyst comprises reduced Cr0 3 and the support comprises silica having a pore size of at least 4.0 nm. 17. The process of claim 15 wherein the copolymerization conditions comprise temperature between 50"C and 150°C. 18. The process of claim 15 wherein the mixture comprises 10 weight percent of 1,9-decadiene and 90 weight percent of l-decene and the lubricant fraction has a viscosity index greater than 250 with a viscosity grater than 600 mm 2 /s at 100 °C. 19. The process of claim 15 wherein the mixture comprises 10 weight percent of 1,7-octadiene and 90 weight percent of l-decene and the lubricant fraction has a viscosity index greater than 300 with a viscosity greater than 1600 mm 2 /s at 100 °C. 20. The process of claim 15 wherein the mixture comprises 10 weight percent of 1,5-hexadiene and 90 weight percent of l-decene and the lubricant fraction has a viscosity index grt ter than 200 with a viscosity greater than 400 mm 2 /s at 100 "C. 21. The process of claim 15 wherein the mixture comprises 10 weight percent of 1,5-hexadiene and 90 weight percent of l-decene and the lubricant fraction has a viscosity index greater than 200. 22. The process of claim 15 wherein the diene comprises 1,5-hexadiene and the l-alkene comprises 1-butene whereby the lubricant fraction is produced having a bromine number greater than 25. 23. The process of claim 15 wherein the mixture comprises 10 weight percent of 1,5-hexadiene and 90 weight percent of l-decene and the lubricant fraction has a viscosity index greater than 200.

Inventors: HO SUZZY C, WU MARGARET MAY-SOM, XIONG YUSHENG, HO, SUZZY, CHEN, HSI, WU, MARGARET, MAY-SOM, XIONG, YUSHENG
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1994
Main classification: C08F4
IPC codes: B01J23, C07C2, C07C13, C08F2, C08F4, C08F36, C08F210, C08L47, C10M107, C10M143, C10N20