PREPARATION OF SILVER VANADIUM OXIDE CATHODES USING Ag(O) AND V2O5 AS STARTING MATERIALS

Abstract: A method for preparing a cathode having as active material silver vanadium oxide formed by chemical addition, reaction or otherwise intimate contact of elemental silver and a vanadium-containing compound present in an anhydrous mixture, is described. The present invention provides alternate preparation techniques for improving chemical control in the formation of a cathode for incorporation into an electrochemical cell.

Description: PREPARATION OF SILVER VANADIUM OXIDE CATHODES USING Ag(0) AND V 2 0 5 AS STARTING MATERIALS BACKGROUND OF THE INVENTION Field Of Invention This invention relates to the manufacture of an alkali metal electrochemical cell or battery, and more particularly to new and improved methods of preparing silver vanadium oxide composite cathode material for use in high energy density batteries. Prior Art Solid cathode, liquid organic electrolyte alkali metal or lithium anode cells or batteries are used as the power source for implantable medical devices. The cathode of such a cell may have as active material carbon fluoride, a metal oxide, a mixed metal oxide such as silver vanadium oxide, or other suitable material as disclosed in U. S. Patent No. 4,830,940 to Keister et al., which patent is assigned to the assignee of the present invention and is incorporated herein by reference. Preparation of cathode material containing a metal oxide such as silver vanadium oxide (Ag0 2 V 5 . 5 , SV0) for use in a lithium cell or battery has been known by a decomposition reaction. However, the decomposition method of preparation is accompanied by the evolution of gaseous products. Typically, the synthesis is carried out by first thermally decomposing a vanadium salt to produce vanadium pentoxide. A decomposable metal salt, preferably containing silver, is then blended with the vanadium pentoxide and the mixture is oven-dried. Following drying, the mixture is again blended and ground to ensure thorough intermingling of the constituents and the resulting homogeneous mixture is subsequently baked for a final heating/decomposition period. Depending on the starting materials used, this final heating/decomposition period can result in the release of toxic by-product gases. For example, if silver nitrate (AgN0 3 ) is used as the silver source, nitrous oxide type gases may be formed. Such a decomposition reaction for the preparation of silver vanadium oxide is: AgN0 3 + V 2 0 5 → AgV 2 0 5 . 5 + N0 2 + 1/20 2 . Upon cooling, the baked material is blended with appropriate amounts of carbon black and graphite powder to enhance conductivity, and with a binder material, and then pressed to form the cathode. Such a method is described in more detail in U.S. Patent No. 4,310,609, to Liang et al., which patent is assigned to the assignee of the present invention and is incorporated herein by reference. Accordingly, the present invention provides an alternate preparation method for silver vanadium oxide by chemical addition, reaction, or otherwise intimate contact of a silver-containing component with a vanadium- containing compound to form a mixed metal oxide. One such method of the present invention comprises intimately combining elemental silver Ag(0) with vanadium pentoxide V 2 0 5 in about a 1:1 mole ratio followed by thermal treatment of the mixed metal oxide to produce an oxygen deficient silver vanadium oxide product. The addition reaction may be carried out at temperatures of from between about 300°C to 700°C, preferably at temperatures of between about 350°C to 550°C and most preferably at temperatures of between about 380°C to 400°C and may proceed to completion within about 2 to 22 hours. Lower temperatures require a longer reaction time. Longer reaction times and higher temperatures may lead to diminished rate capability in cells utilizing the silver vanadium oxide material due to undesirable grain growth. Therefore, in general, lower temperatures are preferred in order to limit grain growth in the silver vanadium oxide product. The reaction is preferably carried out in an oxidizing atmosphere that can include air and oxygen, or the reaction may be carried out in an inert atmosphere including for example argon, nitrogen and helium. In addition, the reaction is carried out in a manner so as to provide a preselected desired shape in the electrical discharge characteristics of the electrochemical cell having a cathode containing the silver vanadium oxide material. References related to the art of thermal treatment of silver and vanadium containing compound mixtures include: K. Takada et al. "Eur. J. Solid State Inorg. Chem.", 28:533-545, 1991, and K. Takada et al. "Solid State Ionics", 40/41:988-992, 1990, and U.S. Patent No. 4,965,151 to Takada et al., which describe the synthesis of silver vanadium oxides prepared by mixing powdered silver and vanadium pentoxide heated under vacuum in a sealed quartz tube. As shown in Fig. 1, heating the starting ingredients under vacuum gives a much different material than that formed by the method of the present invention (Fig. 2) , as evidenced by the X-ray diffraction patterns. Fig. 1 shows X-ray powder diffraction data from silver vanadium oxide made according to Takada under vacuum and at various ratios of silver to vanadium. In comparison, Fig. 2 is a compilation of actual patterns plotted as intensity percent (1%) versus the X-ray diffraction angle (20) , wherein Ar is derived from silver oxide (Ag 2 0) and vanadium oxide (V 2 0 5 ) combined under argon for 24 hours at 375°C for a final stoichiometry of Ag 07 V 2 0 x ; Amb is derived from silver oxide and vanadium oxide combined under ambient atmosphere at 375° for a final ratio of Ag 0 _ 7 V 2 0..; Ag is derived from silver metal and vanadium oxide combined at 600°C under argon for 48 hours for a final ratio of Ag α7 V 2 0 x ; and AgN0 3 is derived from silver nitrate and vanadium oxide combined in water and then baked for 16 hours at 375° under ambient atmosphere for a final composition of Ag 07 V 2 0 x . Published European patent application 0 478 302 A2 discloses silver vanadium oxide cathode material for electrochemical cells and prepared by a chemical combination or addition reaction, but it does not disclose carrying out the reaction in a manner so as to provide a preselected desired shape for the electrical discharge characteristics of the electrochemical cell having a cat ode containing the silver vanadium oxide. It is, therefore, an object of this invention to provide new and improved methods for preparing a silver vanadium oxide composite cathode for use in high energy density batteries. It is a further object of this invention to provide improved chemical control for the formation of mixed metal oxide cathode material. It is still another object of this invention to provide new and improved methods for preparing silver vanadium oxide using elemental silver powder and V 2 0 5 as starting materials. SUMMARY OF THE INVENTION The present invention relates to a new and improved method of preparing silver vanadium oxide composite cathode material for use in high energy density batteries. The present invention comprises a cathode formed from materials that include silver vanadium oxide prepared by the thermal treatment of anhydrous formations in mixed metal states, and may include an electronic conductor and binder materials. The silver vanadium oxide composite material prepared by the method of the present invention results in the intercalation of silver ions into starting materials comprising one or more vanadium- containing compounds through intimate contact of silver powder with the vanadium-containing compound, followed by thermal treatment wherein a mixed metal oxide is formed. Such vanadium-containing compounds include, but are not limited to, vanadium oxide salt, silver vanadate, polyvanadic acid and vanadium oxides. The use of elemental silver avoids the liberation of toxic fumes generated by use of silver nitrate, as in the previously discussed decomposition method. The foregoing is carried out in a manner, for example by varying the silver content of the starting material, so as to provide a preselected desired shape in the electrical discharge characteristic of the electrochemical cell containing the silver vanadium oxide composite cathode material. Cathode plates can be formed by an entirely dry pressing procedure thereby enhancing the shelf life of the resulting plates. Alternatively, the procedure can include dropwise addition of liquid electrolyte to the cathode mixture prior to pressing to enhance the performance and discharge rate capability of an assembled cell incorporating the cathode. BRIEF DESCRIPTION OF THE DRAWINGS The above and other objects, features, and advantages of the present invention will be apparent in the following detailed description of the preferred embodiments taken in conjunction with the accompanying drawing, in which: Fig. 1 is a set of X-ray diffraction patterns of a silver vanadium oxide cathode material made according to the prior art. Fig. 2 is a compilation of diffraction patterns plotted as intensity percent for silver vanadium oxide according to the methods of the present invention. Fig. 3 is a graph showing the discharge curves of electrochemical cells containing silver vanadium oxide as a cathode made from AgN0 3 and V 2 0 5 according to the prior art decomposition method and made from silver powder and vanadium oxide in accordance with the present invention. Fig. 4 is a graph showing the discharge curves of a newly assembled cell containing a silver vanadium oxide cathode material produced by the chemical combination or addition reaction of AgN0 3 and V 2 0 5 in accordance with one of the methods of the present invention and in an inert argon atmosphere. Fig. 5 is a graph showing the discharge curves of a newly assembled cell containing a cathode produced by the chemical combination or additional reaction of AgV0 3 and V 2 0 5 in accordance with the present invention and in an oxidizing atmosphere. DETAILED DESCRIPTION OF THE INVENTION The method of the present invention comprises synthesizing silver vanadium oxide from starting materials including elemental silver powder and vanadium pentoxide (V 2 0 5 ) . This method comprises combining the starting materials by thoroughly grinding them together to ensure homogeneity and thermally treating the ground mixture. A cathode for a high energy density battery is then formed by combining the silver vanadium oxide mixture with an electronic conductor and binder materials, and finally pressing the composite materials to form a cathode plate. This synthesis avoids the liberation of toxic fumes generated by use of silver nitrate as the silver starting material. A cathode, containing cathode active material prepared by the method of the present invention, can be used i.. a nonaqueous lithium battery as described by U.S. Patent No. 4,830,940 to Keister et al. wherein the battery also contains an alkali metal anode, preferably lithium or alloys thereof; a nonaqueous electrolyte which preferably is comprised of a combination of lithium salt and an organic solvent; and a separator material electrically insulating the anode from the cathode while having sufficient porosity to allow for electrolyte flow. An important aspect of the method of the present invention is that it can be carried out in a manner so as to provide a preselected desired shape in the electrical discharge characteristic of the electrochemical cell containing the vanadium oxide composite cathode material. One way of accomplishing this is by varying the silver content of the starting materials. Fig. 3 illustrates the tailoring effect of a discharge curve through manipulation of the silver content of the starting materials, wherein discharge curve 10 exhibits a step shape and is derived from a high energy density cell containing silver vanadium oxide as a cathode made from AgN0 3 according to the prior art decomposition method. As previously mentioned, this material has a stoichiometric composition of AgV 2 0 55 . Curve 20 has a plateau shape and was derived from a high energy density cell having silver vanadium oxide made from an addition reaction of silver powder as the silver- containing compound intimately combined with a vanadium-containing compound, followed by thermal treatment to synthesize an oxygen deficient silver vanadium oxide having the stoichiometric composition Ag 07 V 2 0 5 , and without the undesirable toxic by-product gases characteristic of the prior art decomposition method. The difference in the shape of the stepped-shaped discharge curve 10 and the plateau shaped discharge curve 20 shows that by stoichiometrically varying the amount of silver to vanadium present in the mixed metal oxide product, the shape of the resulting discharge curve can be manipulated. Even though the silver content of the present invention is lower than the silver vanadium oxide produced by the decomposition method, this is not a necessity. Figs. 4 and 5 show discharge curves for comparative high energy density cells containing silver vanadium oxide made according to the methods of the present invention, but under varying atmospheres. The discharge curves were recorded by applying pulse trains consisting of four ten-second, 1.5 ampere pulses every 15 seconds repeated every 30 minutes to the cells. Thus, Fig. 4 shows silver vanadium oxide made by an addition reaction of a silver-containing component and a vanadium-containing compound under an argon atmosphere wherein curve 30 was recorded at open circuit with no load, curve 32 was constructed from the minima of the first pulse of each train and curve 34 was constructed from the minima of the fourth pulse of each train. In comparison, Fig. 5 shows a silver vanadium oxide made by an addition reaction under an oxygen atmosphere wherein curve 40 was recorded at open circuit with no load, curve 42 constructed from the minima of the first pulse of each pulse train and curve 44 was constructed from the fourth pulse minima of each pulse train. The end of life shape of the respective cells is different with the inert argon atmosphere exhibiting a more flattened and stretched out shape than the cathode material produced in a oxidizing atmosphere, having a much sharper drop-off. Additional suitable inert atmospheres include nitrogen and helium in addition to argon while suitable oxidizing atmospheres include air in addition to oxygen. In particular, methods of preparation of silver vanadium oxide composite material for use as cathode active material in a cathode, and an electrochemical cell incorporating the cathode according to the present invention, are illustrated further by the following example. EXAMPLE I A cathode was formed from silver vanadium oxide prepared by intimate contact of the silver containing component with the vanadium containing compound in the following manner. A 1:1 molar mix of elemental Ag(0) powder and V 2 0 5 was heated in a sealed borosilicate tube at 600°C for 24 hours to form silver vanadium oxide according to the present invention. The silver vanadium oxide thus formed was mixed with carbon black and graphite as conductive diluents and polytetrafluoroethylene (PTFE) powder as a binder material to form a depolarizer which was pressed into cathodes for use in electrochemical cells. A cathode comprising 3% conductive materials, 3% PTFE and 94% silver vanadium oxide made according to the method of the present invention was thus prepared. A battery cell was assembled using the foregoing cathode, lithium as the anode, 1M LiAsF 6 in propylene carbonate and dimethoxyethane as the electrolyte and a microporous polypropylene sheet as a separator. The weight of the depolarizer used in the cathode was 0.5g. The open circuit voltage of the cell was 3.45V and the cell delivered 0.06Ah or 0.12 Ah/g to a 2V cut-off under a drain of 0.5 mA/cm 2 . The shape of the discharge curve was stepped with a large plateau at about 2.5 volts. The above detailed description and example are intended for the purposes of illustrating the invention and are not to be construed as limiting. For example, depending on the application of the electrochemical cell, the range of cathode compositions used can vary from 100% silver vanadium oxide to 80% silver vanadium oxide with 10% carbon/graphite and PTFE or other suitable conductor and binding materials known in the art. The invention can be embodied otherwise without departing from the principles thereof, and such other embodiments are meant to come within the scope of the present invention as defined by the appended claims.

Claims: AMENDED CLAIMS [received by the International Bureau on 20 September 1994 (20.09.94); original claims 2, 15-16 amended; new claims 17-19 added; remaining claims unchanged (2 pages)] 2. (Amended) The method of claim 1 wherein the inert atmosphere is selected from one of the group [groups] consisting of argon, nitrogen and helium. 15. (Amended) A method for preparing a cathode of an electrochemical cell, wherein the cathode contains as active material silver vanadium oxide prepared by a chemical addition or reaction of starting materials, which comprises: a) combining the starting materials comprising a silver-containing component with at least one vanadium-containing compound to form an intimate combination of the staring materials comprising an anhydrous mixed metal oxide; [b) the step of combining the starting materials is performed in an atmosphere selected to provide a preselected desired shape in the electrical discharge characteristic of the electrochemical cell;] b) Tc) 1 thermally treating the anhydrous mixed metal oxide in an inert atmosphere to form an oxygen deficient silver vanadium oxide [the mixed metal oxide] ; and c) [d) ] forming a cathode from the oxygen deficient silver vanadium oxide. [by pressing the oxygen deficient silver vanadium oxide into a desired shape,] wherein the forming [pressing] step includes the dropwise addition of a liquid electrolyte. 16. (Amended) The method of claim 1 wherein [said] the step of combining the starting materials is performed in a manner so as to provide a preselected desired shape in the electrical discharge characteristic of the electrochemical cell. 17. (New) The method of claim 15 wherein the step of combining the starting materials is performed to provide a preselected shape in the electrical discharge characteristic of the electrochemical cell. 18. (New) A cathode comprising as an active material oxygen deficient silver vanadium oxide prepared by thermally treating an anhydrous mixed metal oxide according to the method of claim 15. 19. (New) A nonaqueous electrochemical cell comprising a cathode containing active material comprising an oxygen deficient silver vanadium oxide prepared by thermally treating a mixed metal oxide prepared from an anhydrous combination of elemental silver and a vanadium-containing compound according to claim 15, the cell further comprising an alkali metal anode and a nonaqueous electrolyte comprising a combination of an organic solvent and a lithium salt.

Inventors: TAKEUCHI ESTHER S, THIEBOLT WILLIAM C III, TAKEUCHI, ESTHER, S., THIEBOLT, WILLIAM, C., III
Applicants: GREATBATCH W LTD, WILSON GREATBATCH LTD.
Application year: 1994
Main classification: H01M4
IPC codes: C01G31, C04B35, H01B1, H01M4, H01M6