METHOD FOR THE NON-RESIN FLUID-ASSISTED INJECTION MOLDING OF A RESIN

Abstract: Disclosed is a method for the non-resin fluid-assisted injection molding of a resin to produce a shaped resin article having an improved surface finish, which comprises effecting an excess filling of a mold cavity of a sealed mold with a molten resin to form a molten resin mass having opposite, first and second surfaces respectively facing opposite inner walls of the mold cavity, wherein the excess filling is performed in a specific excess filling ratio which corresponds to an excess ratio of a resin by an amount corresponding to 30 to 90 % of a difference between the volume of the mold cavity and a volume exhibited by the resin in accordance with a shrinkage thereof when the molten resin filled in the mold cavity is cooled to a room temperature, and subsequently introducing a pressurized non-resin fluid into the mold cavity on a side of the first surface of the molten resin mass to thereby press the second surface of the molten resin mass against the cavity inner wall remote from the side of the introduction of the non-resin fluid. By the non-resin fluid-assisted injection molding method of the present invention, the occurrence of a sink mark on a front surface of a shaped resin article can be effectively prevented without causing the problem of occurrence of burrs (flashes).

Description: TITLE OF THE INVENTION Method for the non-resin fluid-assisted injection molding of a resin BACKGROUND OF THE INVENTION Field Of The Invention The present invention relates to a non-resin fluid-assisted injection molding method. More particu¬ larly, the present invention is concerned with a method for the non-resin fluid-assisted injection molding of a resin to produce a shaped resin article having an improved surface finish, wherein an excess filling of a mold cavity with a specific amount of a molten resin is effected to form a molten resin mass having opposite, first and second surfaces respectively facing opposite inner walls of the mold cavity, and a pressurized non- resin fluid is subsequently introduced into the mold cavity on a side of the first surface of the molten resin mass to thereby press the second surface of the molten resin mass against the cavity inner wall remote from the side of the introduction of the non-resin fluid. By the non-resin fluid-assisted injection molding method of the present invention, the occurrence of a sink mark on a front surface of a shaped resin article can be prevented without causing the problem of occurrence of burr (flash). The non-resin fluid- assisted injection molding method of the present inven¬ tion is especially effective for producing a shaped resin article which has, on a front surface thereof, a locally protruded portion, at which the shaped resin article has an increased thickness, such as a rib, a boss or the like. Discussion Of Related Art It is widely known that when a shaped resin arti¬ cle which has a relatively large thickness or has a locally protruded portion on a back surface thereof is produced by injection molding a molten resin, a dent, i.e., the so-called "sink mark" is likely to occur on a front surface of the shaped resin article in accordance with the volume shrinkage of the molten resin during the cooling thereof . As a method for preventing the occurrence of the sink mark on a front surface of a shaped resin article, a method has conventionally been known r wherein when an injection pressure is applied, an increased level of pressure is used, and, after the injection, the application of pressure is continued while cooling the injected molten resin (This method is hereinafter referred to as "resin pressure method".). In this resin pressure method, the applied injection pressure is generally in the range from 500 to 2,000 kgf/cm 7 in terms of the maximum resin pressure in the mold cavity . However, as described in Japanese Patent Applica¬ tion Laid-Open Specification No.50-75247, the above- mentioned resin pressure method has problems. For example, it is difficult to appropriately apply pres¬ sures in two stages so as to achieve the effects aimed at by the resin pressure method, so that the molding operation tends to become cumbersome and time-consum¬ ing. Furthermore, in the resin pressure method, the shaped resin articles produced are likely to have burrs formed along a parting line of the mold. Therefore, the removal of the burrs is necessary, thereby inevita¬ bly causing a problem such that additional works are necessary in a molding operation. On the other hand, when a relatively low pressure is employed in the resin pressure method in order to prevent the occurrence of burrs, sink marks are likely to occur at a portion of a shaped resin article, which is positioned away from a gate in a mold cavity, i.e., a portion on which a satisfactory resin pressure cannot be obtained. For solving the problems of the resin pressure method, the above-mentioned Japanese Patent Application Laid-Open Specification No. 50-75247 proposes a gas- assisted injection molding method in which there is used a mold comprising a fixed mold half and a movable mold half with its inner wall having a core protruding therefrom toward the inner wall of the fixed mold half, so that a concaved mold cavity defined by the fixed mold half and the movable mold half having the core portion is provided. The core has a hole extending in a direction of a longitudinal axis thereof, and the hole has a poppet valve disposed at a top thereof. In this method, after a molten resin has been injected into a mold cavity, the poppet valve is operated to push up the molten resin mass, so that a space is produced between the core and the inner surface of a concaved molten resin mass formed in the concaved mold cavity, and then a pressurized gas is injected through the poppet valve into the above-mentioned space, there- by pressing the outer surface of the molten resin mass against the cavity inner wall remote from the core. This gas-assisted injection molding method is intended to prevent the occurrence of sink marks by using a pressurized gas, instead of using the two-stage appli¬ cation of pressure as in the above-mentioned resin pressure method which, as described above, is likely to be unfavorably accompanied by the occurrence of burrs along a parting line of a mold cavity. In Japanese Patent Application Laid-Open Specification No. 50- 75247, there is no description about the amount of a molten resin to be injected. WO 90/06220 (corresponding to U.S. Patent No. 5,273,707 and EP No. 400135) discloses a gas-assisted injection molding method in which a molten resin is injected into the mold cavity in a volume smaller than the volume of a mold cavity, specifically in a volume of 90 % to 95 % of the volume of the mold cavity, and then a pressurized gas is introduced into the remaining space in the cavity. However, a gap is likely to be formed between the inner wall (remote from the side of the gas introduction) of the mold cavity and the molten resin injected in the mold cavity. Hence, the gas intrudes into the gap, causing occurrence of sink marks. As is apparent from the above, in the conventional gas-assisted injection molding methods, for preventing the occurrence of burrs and for assuring a space in a mold cavity into which a pressurized gas is to be introduced, a molten resin is injected into a mold cavity in a volume equal to or smaller than the volume of the mold cavity. International Patent Application Publication No. WO 93/14918 discloses the use of a mold having a sealed construction in which not only a parting line between a movable mold half and a fixed mold half, but also a space between an ejector pin and an inner wall of an ejector pin slide hole provided in the movable mold half, is sealed. In addition, this patent document teaches that a weir formed of a protrusion (having, for example, a rib-like configuration) is provided around a 5 portion of the inner wall of a mold cavity on which it is intended to receive a gas pressure, so that a gas pressure can be effectively applied to a desired por¬ tion of an injected molten resin for preventing the occurrence of a sink mark. • *-° However, with the use of the mold having a sealed construction and with the provision of the weir, it is impossible to prevent an unfavorable intrusion of a pressurized gas into a portion of the mold cavity on a side of the surface of an injected molten resin mass • *- 5 which surface should be pressed against a cavity inner wall facing it. Therefore, close contact between the above-mentioned surface of the molten resin mass and the cavity inner wall facing it cannot be achieved, resulting in an unsatisfactory surface finish of the 20 resultant shaped resin article. In addition, since a weir is provided on the inner wall of the mold cavity, a freedom of a design of a shaped article to be pro¬ duced is inevitably limited. Further, it is noted that in International Patent Application No. WO 93/14918, it 25 is described that the mold cavity is filled or nearly filled with a molten resin. Recently, large-size shaped articles, such as automobile parts and casings of home electric appli¬ ances, have been in increasing demand. In order that the production cost may be reduced by rendering it unnecessary to conduct finishing works, such as paint¬ ing and plating, it has been desired to produce a shaped resin article having an excellent surface fin¬ ish, in which a sink mark is suppressed to a visually unnoticeable level and which exhibits excellent and uniform gloss and luster. However, as described hereinabove, in the conven¬ tional injection molding methods, when a shaped resin article to be produced has a locally protruded portion on a back surface thereof at which the article has an increased thickness, the occurrence of a sink mark defect on a front surface thereof at a portion corre¬ sponding to the locally protruded portion cannot be satisfactorily suppressed without causing the problem of the occurrence of burrs. SUMMARY OF THE INVENTION From the above context, the present inventors have made extensive and intensive studies with a view toward solving the above-mentioned problems inevitably accom- panying the prior art method. As a result of the above studies, it has unexpect¬ edly been found that, in a method for the non-resin fluid-assisted injection molding of a resin, when an excess filling of the mold cavity of a sealed mold with a molten resin is effected, under preselected tempera¬ ture and pressure conditions for the injection, in a specific excess filling ratio [corresponding to an excess ratio of a resin by an amount corresponding to 30 to 90 % of a difference between the volume of the mold cavity and a volume exhibited by the resin in accordance with a shrinkage thereof when the molten resin filled in the mold cavity is cooled to a room temperature], to thereby form a molten resin mass having opposite, first and second surfaces, and a pressurized non-resin fluid is introduced into the mold cavity on a side of the first surface of the molten resin mass to thereby press the molten resin mass against a cavity inner wall facing the second surface (which cavity inner wall is remote from the side of the introduction of the non-resin fluid), the occurrence of a sink mark can be effectively prevented without occurrence of a burr, thereby produc¬ ing a shaped resin article having an excellent surface finish. Based on this novel finding, the present inven¬ tion has been completed. Accordingly, it is a primary object of the present invention to provide a novel method for the non-resin fluid assisted injection molding of a resin, which is free not only from the occurrence of a sink mark, but also from the occurrence of a burr, and which is there- fore extremely useful for producing a shaped resin article having an improved surface finish. The foregoing and other objects, features and advantages of the present invention will be apparent to those skilled in the art from the following detailed description and appended claims taken in connection with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS In the accompanying drawings: Fig. 1 is a diagrammatic cross-sectional view of one form of a sealed mold to be used in the present invention; Fig. 2(a) and Fig. 2(b) are enlarged diagrammatic cross-sectional views of two forms of the ejector pin, shown with ejector pin slide holes, respectively, slidably receiving ejector pins therein, which holes are, respectively, provided in movable mold halves; Fig. 3 is a diagrammatic, partial, cross-sectional view of one form of a shaped resin article having a locally protruded portion; Fig. 4 is a diagrammatic cross-sectional view of another form of a sealed mold to be used in the present invention; Fig. 5 is an enlarged longitudinal cross-sectional view of one form of an ejector pin having a non-resin fluid channel provided therein, shown with a part of the movable mold half and a part of an ejector pin- supporting plate; Fig. 6 is a diagrammatic view showing how a cavity inner wall facing a second surface of a molten resin mass is heated prior to the injection of a resin in a molten form; Fig. 7(a) is a diagrammatic plan view of one form of a shaped resin article; Fig. 7(b) is a cross-sectional view, taken along line VII-VII of Fig. 7(a); Fig. 8 is a graph showing the surface finish condition of the shaped resin article obtained in Example 3, in which the excess filling ratio is 57 %; Fig. 9 is a graph showing the surface finish condition of the shaped resin article obtained in Comparative Example 3, in which the excess filling ratio is 0 %; and Fig. 10 is a graph showing the surface finish condition of the shaped article obtained in Comparative Example 8, in which the resin pressure method was employed . In Fig. 1 through Fig 10, like parts or portions are designated by like numerals and characters. DETAILED DESCRIPTION OF THE INVENTION According to the present invention, there is provided a method for the non-resin fluid-assisted injection molding of a resin to produce a shaped resin article having an improved surface finish, which com¬ prises: (1) providing a mold comprising a fixed mold half and a movable mold half mating with the fixed mold half to thereby provide a mold cavity defined by an inner wall of the fixed mold half and an inner wall of the movable mold half, the mold cavity being communicated with a resin inlet and with a non-resin fluid inlet, the mold being sealed to prevent a non-resin fluid from leakage out of the mold when the non-resin fluid is introduced to the mold cavity; (2) injecting a resin in a molten form, under preselected temperature and pressure conditions for the injection, into the mold cavity of the mold through the resin inlet in an amount ( 2) represented by the fol¬ lowing formula (I): W 2 (g) = W χ (g) + W χ (g) (I) wherein : W! is defined by formula ^ = J° • V^- in which j° is a density (g/cm 3 ) of the resin as meas¬ ured at room temperature under atmospheric pressure, and V^ is defined by formula V^ = V Q • (1-x) in which V Q is a volume (cm 3 ) of the mold cavity, and x is a volume shrinking ratio of the resin, the volume shrinking ratio being v a - v b defined by formula in which Va V a is a volume (cm 3 ) of a predeter¬ mined weight of the resin in a molten form under the preselected temperature and pressure conditions for the injection, and V j - is a volume (cm 3 ) of the predetermined weight of the resin in a solidified form upon cooling to room tempera- ture; and W χ is defined by formula (II): w x = f ' γ * (v 0 - v l ) (IJ) wherein ° is as defined above, Y is from 0.3 to 0.9, and V Q and V^ are as defined above, thereby effecting an excess filling of the mold cavity with the molten resin to form a molten resin mass having opposite, first and second surfaces respectively facing opposite inner walls of the cavity; and (3) introducing a pressurized non-resin fluid, which is inert to the resin, into the mold cavity on a side of the first surface of the molten resin mass to thereby press the second surface of the molten resin mass against the cavity inner wall facing said second surface. Hereinafter, the method of the present invention will be described in detail, with reference to Fig. 1 through Fig. 10. In step (1) of the method of the present inven- tion, a mold is provided. The mold is usually made of a metallic material, e.g., steel. Fig. 1 shows one form of a mold to be used in the present invention. As shown in Fig. 1, mold 1 to be used in the method of the present invention comprises fixed mold half la and movable mold half lb mating with fixed mold half la to thereby provide mold cavity 2 defined by inner wall 2a of fixed mold half la and inner wall 2b of movable mold half lb. Mold cavity 2 is communicated with a resin inlet (sprue 4a of sprue bush 4) and with a non-resin fluid inlet. Mold 1 is sealed by means of seal means 3a to 3e to prevent a non-resin fluid from leakage out of mold 1 when the non-resin fluid is introduced to mold cavity 2. Each of seal means 3a to 3e can be an O-ring made of rubber. With respect to mold 1, on a side of movable mold half lb, remote from mold cavity 2, is provided sealed chamber 7 which is defined by an outer wall of movable mold half lb, an inner wall of spacer block 8 and an inner wall of bottom plate 9. Sealed chamber 7 con¬ tains ejector pin-supporting plate 6 and a plurality of ejector pins 5 each securely connected to ejector pin- supporting plate 6 on a side of movable mold half lb as depicted in Fig. 1, and movable mold half lb has a plurality of ejector pin slide holes 5a, respectively, slidably receiving the plurality of ejector pins 5 therein. Ejector pin-supporting plate 6 is made by connecting two plates to each other by means of, for example, bolts and nuts. Each ejector pin 5 passes through ejector pin slide hole 5a and extends between mold cavity 2 and sealed chamber 7, so that a non-resin fluid channel is provided between an inner wall of each ejector pin slide hole 5a and a longitudinally extend¬ ing periphery of each ejector pin 5, and each ejector pin 5 has its forward end exposed to mold cavity 2. Ejector pin-supporting plate 6 is securely connected. on a side thereof opposite to the side thereof having the plurality of ejector pins 5, to pushing rod 10 for pushing ejector pin-supporting plate 6. The non-resin fluid channel has an open end in inner wall 2b of movable mold half lb, which open end serves as the non-resin fluid inlet. Sealed chamber 7 is fluid-tightly communicated with mold cavity 2 through the non-resin fluid channel, and communicated with a source (not shown) for the pressurized non-resin fluid through port 11. The pressurized non-resin fluid is introduced into and withdrawn from mold cavity 2 through port 11, sealed chamber 7 and the non-resin fluid channel. Rod 10 for pushing ejector pin-supporting plate 6 is reversibly movable. After a shaped resin article has been produced in mold cavity 2, movable mold half lb having the shaped resin article attached to its inner wall 2b is separated from fixed mold half la to open mold 1. Next, rod 10 is moved to push ejector pin-supporting plate 6 toward movable mold half lb, so that the forward ends of the plurality of ejector pins 5 connected to ejector pin-supporting plate 6 are caused to protrude outwardly of ejector pin slide holes 5a, thereby ejecting the shaped resin article from movable mold half lb. More specifically, mold 1 to be used in the method of the present invention is a mold which is able to be kept in a fluid-tightly sealed state for the period of time from the injection in step (2) to the solidifica- tion of the molten resin by cooling. In the present invention, the term "fluid-tightly sealed state" means a state in which a fluid is prevented from leakage out of mold 1 except that the pressurized non-resin fluid can be introduced into and withdrawn out of mold cavity 2 through the non-resin fluid inlet. In mold 1 of Fig. 1, in order to achieve the sealing of the mold, seal means 3a to 3e are provided, as shown in Fig. 1. Seal means 3a is for sealing a parting line between fixed mold half la and movable mold half lb. Seal means 3b is for sealing an inter¬ face between fixed mold half la and sprue bush 4. Seal means 3c is for sealing an interface between movable mold half lb and spacer block 8. Seal means 3d is for sealing an interface between spacer block 8 and bottom plate 9. Seal means 3e is for sealing an interface between ejector pin-supporting plate 6 and bottom plate 9. With respect to mold 1 of Fig. 1, since the pres¬ surized non-resin fluid is to be introduced into mold cavity 2 from the side of movable mold half lb, to thereby press the second surface of the molten resin against inner wall 2a of fixed mold half la, seal means 3b on the side of fixed mold half la can be omitted. In step (2) of the method of the present inven- tion, a resin is injected in a molten form, under preselected temperature and pressure conditions for the injection, into mold cavity 2 of mold 1 through the resin inlet (sprue 4a) in an amount (W ) represented by the formula: W 2 (g) = W-^(g) + W χ (g) wherein W 2 , j _ and W χ are as defined above, thereby effecting an excess filling of the mold cavity 2 with the molten resin, so that opposite, first and second surfaces of the result¬ ant molten resin mass do, respectively, closely face opposite inner walls 2b, 2a of mold cavity 2. in step (3) of the method of the present inven¬ tion, a pressurized non-resin fluid is introduced into mold cavity 2 on a side of the first surface of the molten resin mass to thereby press the second surface of the molten resin mass against cavity inner wall 2a facing the second surface. In the conventional gas-assisted injection molding method, an excess-filling of a mold cavity with a molten resin is avoided in an attempt to solve the problem of the resin pressure method, i.e., the occur- rence of burrs along a parting line which is caused by an excess filling effected in the resin pressure method for applying an increased resin pressure. However, one of the most characteristic features of the method of the present invention is to effect an excess filling of the mold cavity with the molten resin in a specific filling ratio. The reason why a mold cavity can be filled in excess with a molten resin resides in that a molten resin can be compressed by the action of the continued application of injection pres¬ sure. The reason why the injection of an excess amount of a molten resin (i.e., an excess filling of the mold cavity) is effective is as follows. When a pressurized non-resin fluid is introduced into the excess-filled mold cavity on a side of the first surface of the molten resin mass, the pressurized non-resin fluid is completely prevented from flowing and intruding into a portion of the mold cavity on the side of the second surface of the molten resin mass. Therefore, the entire area of the second surface of the molten resin mass in the mold cavity can be pressed closely against the cavity inner wall facing the second surface, so that a shaped resin article having an improved surface finish can be produced. A person skilled in the art may presume that after an excess amount of a molten resin has been injected into a mold cavity, there would be no space left in the mold cavity, so that even if it is attempted to intro¬ duce a pressurized non-resin fluid into the mold cavity on a side of the first surface of the molten resin mass in step (3), the introduction of the non-resin fluid would be difficult, or the.pressure of the pressurized non-resin fluid can be exerted only on limited portions of the first surface of the molten resin mass. Thus, a person skilled in the art may presume that it would be impossible to press the entire area of the second surface of the molten resin mass closely against the cavity inner wall facing the second surface. However, it has unexpectedly, surprisingly been found by the present inventors that such a problem as described above does not occur in step (3) of the method of the present invention as long as the degree of excess filling is within the range as specified in the present invention and that the pressurized non- resin fluid introduced into the mold cavity on a side of the first surface of the molten resin mass success¬ fully serves to uniformly press the entire area of the second surface of the molten resin mass against the cavity inner wall facing the second surface, with satisfactory force. Further, although it is generally known that the larger the amount of a more molten resin to be injected into a mold cavity, the more likely the occurrence of burrs , the present inventors have for the first time found that even when an excess filling of a mold cavity with a molten resin is effected, the occur¬ rence of burrs can be well prevented by using a sealed mold as long as the degree of excess filling is within the range as specified in the present invention. As mentioned above, in step (2) of the method of the present invention, a resin is injected in a molten form, under preselected temperature and pressure condi¬ tions for the injection, into the mold cavity of the mold through the resin inlet in an amount (W 2 ) repre¬ sented by the following formula (I): w 2 (g) = W χ (g) +W χ (g) (I). In formula (I), W^(g) represents a weight of the molten resin which fills (not excess-filling) the mold cavity under the preselected temperature and pressure conditions for the injection, without being compressed. W χ (g) in formula (I) represents an excess portion of the amount [W 2 (g)] of the molten resin to be injected. ^ can be determined, for example, by the following method. First, a relatively small weight amount of the resin is injected in a molten form, under the prese- lected temperature and pressure conditions for the injection, into the mold cavity of the mold through the resin inlet, followed by injection molding, to thereby confirm that the injected molten resin does not yet fill the mold cavity. (With respect to the appropriate temperature and pressure conditions for the injection, when the resin is, for example, polystyrene, the tem¬ perature is generally in the range from 190 to 250 °C, and the pressure is generally in the range from 500 to 2,000 kgf/cm . ) The injection molding is repeated while gradually, slightly increasing the weight of the resin, until it can be confirmed that the injected molten resin fills the mold cavity, without being com¬ pressed. The thus determined weight of the resin can be used as W-_ in formula (I). As mentioned above, W χ (g) is defined by formula (II): wherein P is as defined above, Y is from 0.3 to 0.9, and V Q and V-^ are as defined above. In formula (II), Y corresponds to an excess filling ratio. When Y is expressed in terms of weight percentage, the excess filling ratio in the present invention is in the range from 30 % to 90 %. The excess filling ratio is preferably in the range from 50 % to 80 %. When the excess filling ratio is less than 30 %, a pressurized non-resin fluid introduced is likely to intrude into a portion of the mold cavity on a side of the second surface of the molten resin mass, so that the pressurized non-resin fluid cannot satisfactorily press the entire area of the second surface of the molten resin mass enough against the cavity inner wall facing the second surface and, therefore, it becomes difficult to obtain a uniformly improved surface finish of a shaped resin article. On the other hand, when the excess filling ratio exceeds 90 %, burrs are likely to occur. For removal of the burrs, time-consuming fin¬ ishing works are needed. Further, when the excess filling ratio exceeds 90 %, there is a danger that the mold would sustain damage. In addition, the uniformity of the surface finish of a shaped resin article is deteriorated since the transfer of the configuration of the cavity inner wall facing the second surface of the molten resin mass to the second surface of the molten resin mass is locally, excessively urged. However, when the excess filling ratio is in the range from 30 % to 90 %, especially from 50 % to 80 %, the occurrence of sink marks can unexpectedly be reduced to a visually unnoticeable level, without causing the occurrence of burrs and non-uniform surface finish. With respect to the resin to be employed in the present invention, there is no particular limitation. The resin to be used in the method of the present invention can be selected from those which are generally employed in the conventional injection molding method and the extrusion molding method. Examples of resins which can be used in the method of the present invention include thermo¬ plastic resins, such as polystyrene, an acrylonitrile/ butadiene/styrene terpolymer resin, an acrylonitrile/ styrene copolymer resin, a methacrylate resin, an acetal resin, polyethylene, polyamide, polycarbonate, modified polyphenylene ether and polyphenylene sulfide; and thermosetting resins. The resin to be used in the present invention may contain various types of custom¬ ary additives, such as plasticizers; stabilizers; ultraviolet absorbers; colorants; mold release agents; fibrous reinforcing agents, such as glass fibers and carbon fibers; and fillers, such as glass beads, calci¬ um carbonate and talc. These additives can be used in such amounts as usually employed in the art. Hereinbelow, step (3) of the method of the present invention, i.e., the introduction of the pressurized non-resin fluid, will be explained in detail. Referring now to Fig. 1, after completion of step (2), a pressurized non-resin fluid, which is inert to the resin, is introduced into mold cavity 2 on a side of the first surface of the molten resin mass to there¬ by press the second surface of the molten resin mass against cavity inner wall 2a facing the second surface. 5 Step (3 ) can be conducted immediately after step (2) . Alternatively, there may be an appropriate time lag between step (2) and step (3) as long as step (3) is conducted before the molten resin mass solidifies. In the case of mold 1 of Fig. 1, when the pressur- ° ized non-resin fluid is supplied from a source (not shown) for a non-resin fluid, the pressurized non-resin fluid enters sealed chamber 7 from non-resin fluid port 11. Examples of non-resin fluids usable in the present 5 invention include a substance which is gaseous at room temperature, such as nitrogen, air, carbon dioxide and argon; and a substance which is liquid at room tempera¬ ture, such as water. An inert gas, such as nitrogen, is preferable. The appropriate pressure of the pres- surized non-resin fluid varies depending on factors, such as the type of a resin used, and the shape and size of a shaped article to be produced. However, the pressure of the non-resin fluid is generally in the range from 5 to 100 kg/cm"- G. By increasing the pressure of the pressurized non-resin fluid in sealed chamber 7, the pressurized non-resin fluid in sealed chamber 7 is introduced into mold cavity 2 through a non-resin fluid channel formed between the inner wall of each ejector pin slide hole 5a and the longitudinally extending periphery of each ejector pin 5. More specifically, the pressurize non- resin fluid is introduced into mold cavity 2 on a side of the first surface of the molten resin mass facing cavity inner wall 2b. As a result, the second surface of the molten material mass is pressed against the cavity inner wall 2a facing the second surface. Thus, upon cooling to solidify the molten resin mass, a shaped article having an improved surface finish, i.e., a shaped article which exhibits excellent gloss and luster and an excellent reproduction of the configura¬ tion of cavity inner wall 2a and which is free from sink marks, can be obtained. Generally, a space is necessarily formed between ejector pin 5 and the inner wall of ejector pin slide hole 5a formed in movable mold half lb, so that the non-resin fluid can freely pass through the space. Therefore, there is, in principle, no need to provide a further space there. However, by changing a generally round shape of ejector pin 5 into as shown in Figs. 2(a) and 2(b), a more ample space can be provided for the pressurized non-resin fluid to enter more smoothly. In either case, it is required that the space between ejector pin 5 and the inner wall of ejector pin slide hole 5a of movable mold half lb do not permit the molten resin to intrude thereinto, but permit only the pressurized non-resin fluid to flow smoothly there¬ through. It is not necessary that the pressurized non-resin fluid be introduced from the side of movable mold half lb. If desired, the pressurized non-resin fluid may be introduced from the side of fixed mold half la. Howev¬ er, in this case, it is necessary that an appropriate non-resin fluid supply route be provided in fixed mold half la. For example, a non-resin fluid supply route (having a similar structure to that of a route consti¬ tuted by port 13, and horizontal and vertical non-resin fluid channels 12 and 12a indicated in Fig. 4) can be provided in fixed mold half la in a manner such that a non-resin fluid inlet, which opens to mold cavity 2, is provided in cavity inner wall 2a of fixed mold half la. As mentioned above, in a preferred embodiment of the present invention, the pressurized non-resin fluid is introduced into the mold cavity on a side of the first surface of the molten resin mass, and the second surface of the molten resin mass is pressed against a cavity inner wall facing the second surface, so that a surface of a shaped resin article corresponding to the second surface of the molten resin mass has an improved surface finish. Therefore, the first and second sur- faces of the molten resin mass, respectively, corre¬ spond to back and front surfaces of a shaped resin article. After the pressurized non-resin fluid is injected, the molten resin in mold cavity 2 is cooled and solidi¬ fied. Thereafter, the pressurized non-resin fluid is discharged from mold cavity 2. Subsequently, mold 1 is opened and then, the shaped resin article is ejected from movable mold half lb. The method of the present invention is especially useful in producing a shaped resin article having, on a side thereof corresponding to the first surface of the molten resin mass, a locally protruded portion at which the shaped resin article has an increased thickness (i.e., protruded portions, such as rib, boss, and a combination thereof). Specifically, the method of the present invention is especially effective for producing a shaped article in which the wall thickness (indicated by character t. in Fig. 3), the width of a local protru¬ sion (indicated by character w in Fig. 3), and the height of the local protrusion (indicated by character in Fig. 3) have the following relationships: ——t < w < lOt; and -t < h. When a shaped resin article satisfying the above two formulae is produced by the conventional injection molding methods, it is very likely that the shaped resin article has sink marks at a portion of the flat- side surface of the shaped resin article, which portion corresponds to a reverse side portion relative to the locally protruded portion at which the shaped resin article has an increased thickness (the above-mentioned portion of the flat-side surface is hereinafter fre- quently referred to simply as the "increased thickness portion"). Further, in this case, it is very likely that uniform luster of the increased thickness portion of the shaped resin article cannot be obtained. Fig. 4 is a diagrammatic cross-sectional view of another form of a sealed mold usable in the present invention. Mold of Fig. 4 is similar to but different in several points from mold 1 of Fig. 1. One difference between these two molds reside in that movable mold half lb of mold 1 has therein an additional route for the introduction of a pressurized non-resin fluid into mold cavity 2, as depicted in Fig. 4. This additional route is constituted by port 13, horizontally extending channel 12 and vertically extending channel 12a. With respect to this additional route, a pressurized non- resin fluid supplied from a source (not shown) flows through port 13 and horizontal and vertical non-resin fluid channels 12 and 12a to enter mold cavity 2. Vertically extending non-resin fluid channel 12a has an open end in inner wall 2b of movable mold half lb, the open end serving as a second inlet for the non- resin fluid. The upper open end portion of vertical non-resin fluid channel 12a has metallic porous materi¬ al 14 fittedly inserted therein. It is required that metallic porous material 14 do not permit the molten resin to intrude thereinto, but permit the pressurized non-resin fluid to flow smoothly therethrough. Metal¬ lic porous material 14 is advantageously made of, for example, sintered granular stainless steel. The second inlet for a non-resin fluid is communicated with a source for the non-resin fluid, and this source may be the same as or may be different from the other source which is communicated with the other non-resin fluid inlet (first inlet) positioned at the upper open end of ejector pin slide hole 5a. The other differences between mold 1 of Fig. 1 and mold 1 of Fig. 4 reside in that mold 1 of Fig. 4 have center plate 15 and seal means 3f. Seal means 3f seals as interface between center plate 15 and movable mold half lb. Center plate 15 is useful in that horizontal and vertical non-resin fluid channels (not shown) which are fluid-tightly connected to vertical non-resin fluid channel 12a and which lead to a port (not shown) commu¬ nicated with a source (not shown) for a non-resin fluid, can be provided within center plate 15. In such a case, port 13 and horizontal non-resin fluid channel 12 can be omitted. In the case of mold 1 shown in Fig. 4, sealed chamber 7 can be omitted, if the space between an inner wall of each ejector pin slide hole 5a and a longitudi¬ nally extending periphery of each ejector pin 5 is satisfactorily sealed. However, it is generally diffi¬ cult to seal the above-mentioned space while allowing ejector pin 5 to be slidable in ejector pin slide hole 5 . Therefore, even when a pressurized non-resin fluid is introduced only through port 13 and horizontal and vertical non-resin fluid channel 12 and 12a, it is preferred to provide sealed chamber 7. When the number of ejector pins 5 is relatively small, it is preferred to effect the introduction of the pressurized non-resin fluid by using both of the two routes, i.e., the route which involves sealed chamber 7 and the route which involves horizontal and vertical non-resin fluid chan¬ nels 12 and 12a. 5 in mold 1 of Fig. 4, a solid metallic piece (not shown) may be employed in place of the above-mentioned metallic porous material 14, as long as an appropriate space for flowing a pressurized non-resin fluid can be provided between an inner wall of vertical non-resin 10 fluid channel 12a and a vertically extending periphery of such a solid metallic piece. The solid metallic piece may have, for example, a cross-section similar to those of two forms of ejector pin 5 shown in Figs. 2(a) and 2(b). If desired, the solid metallic piece may -*- 5 extend along the entire length of vertical non-resin fluid channel 12a. Fig. 5 is an enlarged diagrammatic longitudinal cross-sectional view of another form of ejector pin 5 having a non-resin fluid channel provided therein, 20 shown with a part of movable mold half lb and a part of ejector pin-supporting plate 6. As depicted in Fig. 5, ejector pin 5 may be designed to have a hollow struc¬ ture serving as a non-resin fluid channel 12a having metallic porous material 14 fittedly inserted in its 2 ^ open end portion on the side of mold cavity 2. In this case, non-resin fluid channel 12 is provided in ejector pin-supporting plate 6 as shown in Fig. 5. A pressur¬ ized non-resin fluid, supplied through horizontal non- resin fluid channel 12 inside ejector plate 6, is led through vertical non-resin fluid channel 12a formed within ejector pin 5 to flow into mold cavity 2. In the method of the present invention, when the mold is made of a metallic material, it is preferred that a heat insulating material layer be provided on the cavity inner wall 2a, so that the second surface of the molten resin mass is pressed against cavity inner wall 2a through the heat insulating material layer provided thereon. With this preferred mode of the method of the present invention, the degree and uni- formity of luster of the front surface (including the increased thickness portion) of a shaped resin article can be markedly improved. The reason for this advanta¬ geous effect resides in that the heat insulating mate¬ rial layer provided on cavity inner wall 2a serves to prevent the second surface of the molten resin mass from being rapidly cooled upon being contacted with cavity inner wall 2a, so that at the time when the second surface of the molten resin mass is pressed against cavity wall 2a under the force of the intro- duced pressurized non-resin fluid, a good fluidity of the second surface of the molten resin mass is not rapidly lost and, hence, the pressing effect of the pressurized non-resin fluid on the second surface can be markedly improved. The above-mentioned heat insulating material layer is preferably made of a heat-resistant material having a thermal conductivity of from 60 to 0.06 W«m~ 1 k~ * *'. Examples of representative heat insulating materials include polyimide, epoxy resin, phenol resin, polytet- rafluoroethylene, and ceramics. The appropriate thick¬ ness of a heat insulating material layer varies depend¬ ing on the type of the heat insulating material but, is preferably in the range from 10 to 500 μm, more prefer¬ ably from 30 to 200 μm. Alternatively, in the present invention, cavity inner wall 2a facing the second surface of the molten resin mass may preferably be heated prior to the injec¬ tion of the molten resin in step (2). By this alterna¬ tive mode of the method which involves a pre-heating of cavity inner wall 2a, the same advantageous effect as achieved with the above-mentioned preferred mode in¬ volving the use of a heat insulating material layer can be obtained. The heating of cavity inner wall 2a prior to the injection in step (2) can be effected by means of, for example, an inductor coil covered with an electrically insulating material. Fig. 6 is a diagrammatic view showing how a cavity inner wall facing a second surface of a molten resin mass is heated prior to the injection of a resin in a 5 molten form. As shown in Fig. 6, inductor coil 16 is closely contacted with cavity inner wall 2a, and induc¬ tion heating of cavity inner wall 2a is effected. Since inductor coil 16 can selectively heat only cavity inner wall 2a instead of heating the entire movable - 1 " 0 mold half la, the cooling of the molten resin mass after the injection can be conducted efficiently. It is preferable that the temperature for the above-mentioned heating of cavity inner wall 2a prior to the injection in step (2) be equal to or higher than 5 a temperature at which a modulus of elasticity of a resin is lowered to a level which is 1/3 of a modulus of elasticity to be exhibited by the resin at room temperature. The heating of cavity inner wall 2a by means of 0 inductor coil 16 can also be effected in a manner different from the above. For example, inductor 16 can be embedded in fixed mold half la just below cavity inner wall 2a to be heated. Using this embedded induc¬ tor coil 16, cavity inner wall 2a can be heated from 5 within movable mold half la prior to the injection of a resin. By employing the manner in which inductor coil 16 is embedded in movable mold half la, it is possible to effectively heat only a portion of cavity inner wall 2a corresponding to an increased thickness portion of a shaped resin article to be produced. BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail with reference to Examples, which should not be construed as limiting the scope of the present inven¬ tion. Example 1 Using a sealed mold made of steel, a shaped resin article as shown in Fig.7 was produced, and the surface finish condition of the shaped resin article was evalu- ated. The sealed mold employed had the same structure as shown in Fig. 1 except that the mold used did not have seal means 3b. The volume of the mold cavity was 202 cm 3 . The shaped resin article had the following dimen¬ sional characteristics: a width [indicated by charac¬ ter A in Fig. 7(a)] of 200 mm, a length [indicated by character B in Fig. 7(a)] of 300 mm, a depth [indicated by character C in Fig. 7(b)] of 40 mm, and a wall thickness [indicated by character D in Fig. 7(b)] of 2.5 mm. The shaped article had, on a back surface thereof, a rib which had a width [indicated by charac¬ ter E in Fig. 7(a)] of 6 mm and a height of 10 mm. The procedure conducted in Example 1 is described in detail below. The conditions for the injection molding were as follows . Resin : Asahi Chemical Polystyrene (tradename of a high impact polystyrene, manufactured and sold by Asahi Kasei Kogyo Kabushiki Kaisha, Japan, having a specific gravity of 1.05 as measured at room temperature under atmospheric pressure) Volume of the mold cavity : 202 cm 3 Cylinder temperature : 230 °C Temperature of the mold : 45 °C Injection pressure : 50 kg/cm 2 (gauge pressure of the injection molding machine) Resin pressure in the mold cavity : 500 kg/cm (maximum value) Pressurized non-resin fluid : N 2 (nitrogen gas) Pressure of the pressurized non-resin fluid : 40 kg/cirr (gauge pressure) Cooling time (period of time as measured from comple¬ tion of the injection of the resin) : 50 seconds In Example 1, W } , W χ and W 2 in formula (I) were as follows: W χ : 200 g W χ : 6 g, and W 2 : 206 g In Example 1, Y in formula (II) was 0.43, and 5 therefore, the excess filling ratio was 43 %. The injection molding was conducted as follows. The high impact polystyrene was charged into the cylinder of an injection molding machine through a hopper thereof, and was heated in the cylinder (cylin- 10 d r temperature: 230 °C), thereby obtaining a molten resin. Then, 206 g of the molten resin (the excess filling ratio: 43 %) was injected into the mold cavity (volume: 202 cm 3 ; temperature of the mold: 45 °C) with an injection pressure of 500 kg/cm *1 (gage pressure). ■ *-5 After completion of the injection of the molten resin, a pressurized nitrogen gas (gauge pressure: 40 kg/cirr) which was supplied from a source therefor (pressure tank) was immediately introduced into the mold cavity 2 through inlet 11, sealed chamber 7 and the non-resin 20 fluid channel formed between an inner wall of each ejector pin slide hole 5a and a longitudinally extend¬ ing periphery of each ejector pin 5. Specifically, the gas valve of the pressure tank was opened for 5 seconds and then, the valve was closed. After the closing of 2 ^ the gas valve, the pressurized N gas was retained in the mold cavity for 20 seconds and then, withdrawn from the mold cavity. The molten resin in the mold cavity was cooled for 50 seconds from completion of the injec¬ tion, to thereby allow the molten resin to solidify. Next, the movable mold half lb was separated from the fixed mold half la to open the mold. The pushing rod 10 was moved to push the ejector pin-supporting plate, so that the ejector pins served to eject the shaped article from movable mold half lb. The shaped resin article was visually observed to check whether or not there was occurrence of burrs along a parting line of the mold. Subsequently, the shaped article was allowed to stand for three days at room temperature under atmospheric pressure. Then, the front surface of the shaped resin article (corresponding to the second surface of the molten resin mass) was tested for occur¬ rence of sink marks by means of a surface roughness tester (SURFTEST-500, manufactured and sold by Mitutoyo Corporation, Japan). That is, displacement on the front surface of the shaped resin article in a direc¬ tion orthogonal thereto was measured, and was taken as a depth (μm) of a sink mark. The measurement of dis¬ placement was effected with respect to a portion [as indicated by a broken line with arrows in Fig. 7(b)] of the front surface around the axis of the rib formed on the back surface. Results are shown in Table 1. Examples 2 through 6 Substantially the same procedure as in Example 1 was repeated except that the weight of the resin to be injected was changed by varying the excess filling ratio, as indicated in Table 1. Results are shown in Table 1. The surface finish condition of the shaped resin article obtained in Example 3 is shown in the graph of Fig. 8. Comparative Examples 1 through 7 Substantially the same procedure as in Exam¬ ple 1 was repeated except that the weight of the resin to be injected was changed by varying the excess fill¬ ing ratio, as indicated in Table 1. Results are shown in Table 1. The surface finish condition of the shaped resin article obtained in Comparative Example 3 is shown in the graph of Fig. 9. As is apparent from Table 1, in Examples 1 to 6 in which the excess filling ratio is within the range 30 to 90 %, the displacement (depth of sink mark) was as small as 5 to 55 μm, indicating that a sink mark cannot be visually observed. Further in Example 1 to 6, occurrence of burrs was not observed. As is also apparent from Table 1, in Compara- tive Examples 1 to 6 in which the excess filling ratio is less than 30 %, the depth of the sink mark is as large as 70 μm to more than 1,000 μm, indicating that the sink mark is clearly observable by the naked eye. Further, in Comparative Example 7 in which the excess filling ratio is 93 %, the occurrence of burrs was observed. Comparative Example 8 (Resin pressure method) Injection molding, using the resin pressure method was conducted by the following procedure to produce the shaped resin article shown in Fig. 7. In this experi¬ ment, a non-sealed mold was used which had the same structure as that of the mold of Fig. 1 except that seal means 3a and 3b were not present. With respect to the type of the resin employed, the cylinder tempera¬ ture, the temperature of the mold, the injection pres¬ sure, and the pressure of the molten resin in the cavity, the same conditions as employed in Example 1 were employed. The resin was charged into the cylinder and heated therein to obtain a molten resin. 210 g of the molten resin was injected into the mold cavity in the same manner as in Example 1. Following the injection, a secondary pressure described below was applied to the molten resin in the mold cavity for 10 seconds. Secondary pressure : 50 kg/cm" (gauge pressure of the molding machine), which corresponds to a resin pressure of about 400 kg/cm 2 . After the molten resin was solidified, the mold was opened and the obtained shaped resin article was re¬ moved from the mold cavity. With respect to the shaped resin article, occurrence of burrs and sink marks was evaluated in the same manner as in Example 1. Results are shown in Table 1. The surf ce finish condition of the shaped resin article obtained in Comparative Exam¬ ple 8 is shown in the graph of Fig. 10. Comparative Example 9 Substantially the same procedure as in Comparative Example 8 was repeated except that the weight of the resin to be injected was changed to 211 g. Results are shown in Table 1. As shown in Table 1, in Comparative Example 8, in which optimum molding conditions were selected for preventing occurrence of burrs, the depth of the sink mark of the shaped resin article was as large as 75 μm, indicating that the sink mark was visually easily observable. In Comparative Example 9, the depth of the sink mark was as large as 75 μ and, in addition, occurrence of burrs was observed. Example 7 Substantially the same procedure as in Example 3 was repeated except that a heat insulating material layer was provided on the cavity inner wall 2a, so that the second surface of the molten resin mass was pressed against the cavity inner wall 2a through the heat insulating material layer provided thereon. Illustra¬ tively stated, as the heat insulating material layer, a polyimide film having a thickness of 50 μm was em¬ ployed, and this film was attached, by means of an adhesive tape, to the cavity inner wall 2a facing the second surface of the molten resin mass corresponding to the front surface of a shaped resin article to be produced. With respect to the front surface of the obtained shaped resin article, the degree and uniformity of luster were evaluated. The degree of luster was measured by a gloss meter (Digital Variable Gloss Meter, manufactured and sold by Suga Test Instrument Co., Japan). Criteria of evaluation of uniformity of luster were as follows. x: Large non-uniformity in luster is observed and/or a distinct flow mark is observed. Δ: Some non-uniformity in luster is observed and/or a flow mark is observed. Q: Uniform luster is observed over the entire area of the front surface of a shaped resin article, and no flow mark is observed. Results are shown in Table 2. Referential Example With respect to the shaped resin article obtained in Example 3, the degree and uniformity of luster were evaluated in the same manner as in Example 7. Results are shown in Table 2. Comparative Example 10 with respect to the shaped resin article obtained in Comparative Example 8, the degree and uniformity of luster were evaluated in the same manner as in Example 7. Results are shown in Table 2. Example 8 Substantially the same procedure as in Example 3 was repeated except that the cavity inner wall 2a facing the second surface of the molten resin mass was heated prior to the injection in step (2). The heating of the cavity inner wall 2a was effected by means of an inductor coil covered with an electrically insulating material. As shown in Fig. 6, the inductor coil was closely contacted with the cavity inner wall 2a and induction heating of the cavity inner wall 2a was effected. After the cavity inner wall 2a was heated to about 120 °C, the inductor coil was removed, and the injection of a molten resin was immediately conducted. With respect to the front surface of the obtained shaped resin article, the degree and uniformity of luster were evaluated in the same manner as in Example 7. Results are shown in Table 2. As is apparent from Table 2, when a heat insulat¬ ing material layer is provided on the cavity inner wall 2a, facing the second surface of the molten resin mass, as in Example 7, or when the cavity inner wall 2a facing the second surface of the molten resin mass is heated prior to the injection in step (2), as in Exam¬ ple 8, the degree and uniformity of luster are markedly improved. Table 1 Weight of in¬ Wx Excess filling Depth of sink Occurrence jected resin (g) (g) ratio (%) mark (H ) of burrs Comparative Example 1 196 - - ≥ 1000 None Comparative Example 2 198 - - ≥ 1000 None Comparative Example 3 200 0 0 ≥ 1000 None Comparative Example 4 201 1 7 200 None Comparative Example 5 202 2 14 82 None Comparative Example 6 204 4 29 70 None Example 1 206 6 43 55 None Example 2 207 7 50 18 None Example 3 208 8 57 10 None Example 4 210 10 71 5 None Example 5 211 11 79 5 None Example 6 212 12 86 5 None Comparative Example 7 213 13 93 5 Observed Comparative Example 8 210 10 71 75 None Comparative Example 9 211 11 79 75 Observed Note Examples 1 to 6 and Comparative Examples 1 to 7 are arranged so that the excess filling ratios are successively shown from smaller to larger values. Table 2 Degree of luster (%) Depth of Uniformity sink mark Increased Around increase of luster (μm) thickness thickness portion * portion Example 7 8 98 97 o Referential Example 10 35 31 Δ Comparative Example 10 75 43 28 X Example 8 5 95 96 O Note "Increased thickness portion" means a portion of the front surface corresponding to the rib on the back surface

Claims: CLAIMS 1. A method for the non-resin fluid-assisted injection molding of a resin to produce a shaped resin article having an improved surface finish, which com- 5 prises: (1) providing a mold comprising a fixed mold half and a movable mold half mating with said fixed mold half to thereby provide a mold cavity defined by an inner wall of the fixed mold half and an inner wall of 10 the movable mold half, said mold cavity being communicated with a resin inlet and with a non-resin fluid inlet, said mold being sealed to prevent a non-resin fluid from leakage out of the mold when the non-resin -'-5 fluid is introduced to said mold cavity; (2) injecting a resin in a molten form, under preselected temperature and pressure conditions for the injection, into the mold cavity of said mold through said resin inlet in an amount (W ) represented by the 0 following formula (I): W 2 (g) = W χ (g) + w χ (g) (I) wherein: Wi is defined by formula W^ = j 2 • V^ in which Pis a density (g/cm 3 ) of the resin as meas- 25 ured at room temperature under atmospheric pressure, and V j is defined by formula Vi = V Q • (1-x) in which V Q is a volume (cm^) of the mold cavity, and x is a volume shrinking ratio of the resin, said volume shrinking ratio being v a " v b defined by formula in which Va • 3 V a is a volume (c J ) of a predeter- mined weight of the resin in a molten form under said preselected temperature and pressure conditions for the injection, and V j - is a volume (cm J ) of the predetermined weight of the resin in a solidified form upon cooling to room tempera¬ ture; and W χ is defined by formula (II): w x = f ' Y * ( 0 " v l ) (ιχ) wherein P is as defined above, Y is from 0.3 to 0.9, and V Q and V^ are as defined above, thereby effecting an excess filling of said mold cavity with the molten resin to form a molten resin mass having opposite, first and second surfaces respectively facing opposite inner walls of said cavity; and (3) introducing a pressurized non-resin fluid, which is inert to said resin, into said mold cavity on a side of said first surface of the molten resin mass to thereby press said second surface of the molten resin mass against the cavity inner wall facing said second surface. 2. The method according to claim 1, wherein said Y in formula (II) is from 0.5 to 0.8. 3. The method according to claim 1 or 2, which is used for producing a shaped resin article having, on a side thereof corresponding to the first surface of said molten resin mass, a locally protruded portion at which the shaped resin article has an increased thickness. 4. The method according to any one of claims 1 to 3, wherein on a side of said movable mold half, remote from the mold cavity, is provided a sealed chamber which contains an ejector pin-supporting plate and a plurality of ejector pins each securely connected at its rear end to one surface of the ejector pin- supporting plate on a side of said movable mold half, and the movable mold half has a plurality of ejector pin slide holes, respectively, slidably receiving said plurality of ejector pins therein, said sealed chamber being fluid-tightly communi¬ cated with the mold cavity through a non-resin fluid channel formed between an inner wall of each ejector pin slide hole and a longitudinally extending periphery of each ejector pin, and communicated with a source for the pressurized non-resin fluid, wherein said pressur¬ ized non-resin fluid is introduced into and withdrawn from the mold cavity through said sealed chamber and the non-resin fluid channel. 5. The method according to claim 4, wherein said mold cavity is further provided with a second inlet for a non-resin fluid. 6. The method according to any one of claims 1 to 5, wherein said first and second surfaces of the molten resin mass, respectively, correspond to back and front surfaces of a shaped resin article. 7. The method according to claim 1 or 2, wherein said mold is made of a metallic material. 8. The method according to claim 7, wherein said second surface of the molten resin mass is pressed against said cavity inner wall facing said second surface through a heat insulating material layer pro¬ vided on said cavity inner wall. 9. The method according to claim 8, wherein said heat insulating material layer is made of a heat-resistant material having a thermal conductivity of from 60 to 0.06 W.m "1 k~ 1 . 10. The method according to claim 7, wherein said cavity inner wall facing the second surface of the molten resin mass is heated prior to the injection in step (2). li. The method according to claim 10, wherein the temperature for heating said cavity inner wall facing the second surface of the molten resin mass is equal to or higher than a temperature at which a modulus of elasticity of the resin is lowered to a level which is 1/3 of a modulus of elasticity to be exhibited by the resin at room temperature.

Inventors: HORIKOSHI MAKI, IMAI SHOJI, MATSUMOTO YUICHI, HORIKOSHI, MAKI, IMAI, SHOJI, MATSUMOTO, YUICHI
Applicants: ASAHI CHEMICAL IND, HORIKOSHI MAKI, IMAI SHOJI, MATSUMOTO YUICHI, ASAHI KASEI KOGYO KABUSHIKI KAISHA, HORIKOSHI, MAKI, IMAI, SHOJI, MATSUMOTO, YUICHI
Application year: 1994
Main classification: B29C45
IPC codes: B29C45