METHOD FOR DIRECT CHEMICAL ANALYSIS OF MOLTEN METAL

Abstract: The invention relates to a method for quantitative analysis of one or more elements in a molten metal bath. Light from one or more light sources are focused against the surface of the molten bath and is reflected from the surface of the metal bath to a monochromator or a polychromator connected to detectors for detecting absorbed light in a gas layer associated with the melt of a wavelength or wavelengths corresponding to the element or elements to be analyzed. The absorbtion signals are proportional to the atom- or molecular density of the components to be analyzed and a function of the thickness of the gas layer and the concentration of the element or elements in the molten metal bath. The concentration of the elements to be analyzed is the calculated based or known relations between absorption signal, the thickness of the gas layer and the temperature of the metal bath.

Description: Title of invention: "Method for direct chemical analysis of molten metal". Technical Field. The present invention relates to a method for direct chemical analysis of molten metal. Background Art During many years it has been tried to develop methods for rapid chemical analysis of molten metal, especially in the steel industry. The driving force in this work has been the substantial economical savings which are possible by faster smelting- and refining processes and the possibility for an improved process control, thereby obtaining metals and metal alloys having a chemical composition within specifications. The main amount of rapid chemical analysis in the metal industry, especially in the steel industry are being done by arc discharge optical emission spectrometry and x- ray fluorescence analysis on solid test specimens. The time interval from drawing a sample and until a final analysis is obtained is normally in the range from 2 to 10 minutes. It has been proposed a number of methods for direct analysis of molten metals. Most of these methods are, however, difficult to use under operation conditions in metal smelting plants. A group of proposed methods for direct analysis of molten metals are based on optical emission spectrometry. Thus use of arc discharge optical emission spectrometry on molten metal is described by Eizo Nonomura et al. in Transactions ISIJ, Vol. 25, 1985. Tests have shown that it is possible to use this principle for analysis of molten metal under controlled conditions, but that it is difficult to use under operation condition in smelting plants. Laser-induced optical emission spectrometry for direct analysis of molten metals is described by Kouzou Tsunoyama et al. in Transactions ISIJ Vol. 25, 1985. By this method a laser is used for discharging the specimen, Masao Saeki, Proceeding from CETAS meeting in Luxemburg May 12. - 14., 1987 has proposed to analyse the manganese content in a steel melt in a steel converter by using oxygen induced optical emission spectrometry. Another method for direct analysis of molten metal comprises production of a voltalized test specimen and transport of the specimen through a piping system to an IPC torch (Inductively coupled Plasma), wherein the test specimens is analysed. The test specimen can be obtained by a numer of technics, such as inserting a probe down into the metal bath and bubling an inert gas through the bath, by reacting an oxidizing gas such as HC1, O2 or CI2 with the bath, or by discharging an electric arc against the surface of the metal bath. Except for laboratory- and pilot plant tests, the method has not found any use. The method is described by G. Jecko and A. Golloch in Proceeding from CETAS meeting in Luxemburg May 12. - 14., 1987. Finally, LA. Majorov et al, Spectrochimica Acta, Vol. 36, No. 12, 1981, page 1223 - 1231, has shown that atomic absorption spectrometry (AAS) can be used for continuous analysis of a metal melt during vacuum refining. In this method a light beam is passed thorugh the gas phase above the molten metal bath in parallel with the surface of the molten metal bath. For some elements and gases it is possible to analyse the content of the elements in a molten metal by using electrochemical sensors. Such electrochemical sensors can, however, only be used for analysing one element at a time and a sensor can only be used once. Electrochemical sensors are widely used for analysing oxygen content in steel melts and there are also described electrocyhemical sensors for analysing hydrogen, silicon, aluminium and calcium in molten metals. Disclosure of Invention. It is an object of the present invention to provide a method for analysing the chemical composition of molten metals, which method gives a rapid and accurate analysis of the chemical composition of the molten metal and which method can be used during normal conditions in smelting plants. Accordingly, the present invention relates to a method for quantitative analysis of one or more elements in a molten metal bath, wherein light beams from one or more light sources are focused against the surface of the metal bath, whereafter the light is reflected from the surface of the molten metal bath to a monochromator or a polychromator connected to suitable detectors for detecting absorbed light in a gas layer associated with the melt of a wavelength or wavelengths corresponding to the element or elements to be analyzed, which absorbtion signal or signals are proportional to the atom- or molecular density for the gas component or components to be analysed and a function of the thickness of the gas layer, whereafter the concentration of the element or the elements in the molten metal bath is calculated based on known relations between the absorbtion signal, the thickness of the gas layer and the temperature of the metal bath. It is a basis for the present invention that any melt is associated with a gas layer above the melt which is in equilibrium with the melt. The composition of this gas layer is thus an indirect measure for the composition of the melt at a given temperature. By using the surface of the metal bath as a reflector or mirror for the light, one can in a very simple way measure the absorbtion of light in the gas layer associated with the melt. It has surprisingly been found that even for molten metal baths having a flowing surface, good reflection of light is obtained, as the light beam projected against the surface of the metal bath can be focused to a very small area, virtually eliminating the effect of movements on the surface of the metal bath. In order to obtain significant results, it is, however, necessary that at least the part of the surface of the metal bath on which the light beams are focused, is not covered by oxide layer, slag etc. Oxide layers and slag will also prevent the establishment of the gas-liquid equilibrium which is necessary in order to obtain correct results. For some melts it can thus be necessary to shield a part of the surface of the metal bath by using an open probe or the like and to supply inert gas to provide a clean metal surface on the part of the surface on which the light beam is being focused. Disturbances in the form of dust particles, smoke and geometrical disturbances in the surface of the metal bath can be corrected by using known correction technics, such as background correction using D2-lamp, Smith Hieftje back-ground correction and the Zeeman method. The detection of absorbed light can be done either sequecially or simultaneously. By sequential detection, the absorbtion for one gas component is detected at a time. By simultaneous detection of absorbed light, the absorbtion for a number of components in the gas layer are detected simultaneously. By simultaneous analysis of absorbed light, the signal for one or more of the components in the gas can be used as an internal standard or for relative determination of the ratio between components in the molten metal bath. If the measurements are made for a molten metal bath having one dominant element in a known amount, the absorbtion signal for this element in the gas layer above the melt can be used as an internal standard. The absorbtion signal from the internal standard can thus be used for corrections due to temperature changes and changes in the thickness of the gas layer. The present invention will now be further described with reference to the accompanying drawings. Description of Drawings. Figure 1 shows an apparatus which can be used for carrying out the method of the present invention, Figure 2 shows an apparatus used in the example described below, and where, Figure 3 shows a diagram for measured absorbtion as a function of the silver content in a copper-silver alloy. Detailed Description of Preferred Embodiments. In figure 1 there is shown an apparatus which can be used in connection with the method of the present invention. On the figure there is shown a molten metal bath 1 having an associated gas layer 2 in equilibrium with the molten metal bath 1. The molten metal bath can be contained in any suitable container intended to contain a bath of molten metal, or can for example consist of metal flowing on a tapping spout of a smelting furnace or the like. The apparatus for direct chemical analysis of the molten metal bath 1, comprises a light source 3, normally a hollow cathode lamp for emission of monochromatic light, a monochromator or polychromator 4 for selecting the actual wavelength for the element to be detected, a detector 5 for detecting light and lenses 6, 7 for focusing, guiding and catching the light beams. All units in the apparatus can be assembled in a housing and the apparatus can be connected to a computer for registration, treatment and storage of measured signals. Further, the apparatus can be connected to devices for displaying the measured results, such as a data screen or a printer. By use of the apparatus shown in figure 1, a light beam is sent from the light source 3 and focused against the surface of the molten metal bath by mean of the lens 6. The light from the light source 3 comprises light having a wavelength co esponding to the resonans line or lines for the element or elements to be detected. The light beam passes through the gas layer 2 and is reflected from the surface of the molten metal bath 1 to the lens 7 and is directed to the monochromator or polychromator and to the detector 5. When passing through the gas layer 2 a part of the light having the wavelength for an absorbtion line for an actual atom, will be absorbed by atoms in the gas layer. The amount of absorbtion will be dependent on the atomic density of the actual metal atom in the gas layer and of the length of the path which the light passes in the gas layer 2. The absorbtion will be in accordance with Beer's law stating that the absorbtion is proportional to the concentration or the atomic density and the length of the path which the light passes through the absorbtion medium. As the gas layer associated with the surface of the molten metal bath approximately satisfies the requirements to an ideal gas, the atomic density for the actual element will be proportional to the partial pressure of the element and inverse proportional to the absolute temperature for the system. The partial pressure in the gas layer associated with a bath of molten metal is, according to Raoult's law, given as the concentration of that element in the melt for an ideal system and as the activity of the element in the melt for non-ideal system. The activity for an element in a molten metal bath is a function of the concentration of the element in the melt and of the temperature of the melt. The atomic absorbtion signal registered by the detector 5 will thus be a function of the chemical composition of the melt, the temperature of the melt and of the thickness of the gas layer 2 associated with the molten metal bath. EXAMPLE 1 An apparatus as shown in figure 2 was used to determine the correlation between detected atomic absorbtion signals for silver and the silver consentration in a copper- silver alloy. The apparatus comprises a Perkin Elmer 303 atomic absorbsion spectrometer 10, having a hollow cathode lamp 11 with a D2-lamp 12 for correction of background noise, a monochromator 13 and a detector 14. The detector 14 was connected to a printer 15. About 100 grams of pure copper was melted in the resistance furnace 16. The light from the hollow cathode lamp 11 was thereafter focused against the surface of the copper melt 24 by means of mirrors 17, 18 and two UV lenses 19, 20. The light passed through the gas layer 25 and the light reflected from the surface of the copper melt was by the use of a mirror 21 and a lens 23 guided against the monochromator 23 of the AAS instrument. After having adjusted the mirrors and the lenses, the absorbsion signal for silver (328.1 nm) was adjusted to zero. Silver was thereafter added to the copper melt at intervals in amounts given in table 1. The temperature of the melt was during the test measured by a thermocouple 26. Table 1 Concentration Measured absorbtion Ag (ppmw) 328.1 nm 338.3 nm 1.3 0.000 0 23.6 0.087 79.3 0.220 244.8 0.626 418.3 0.825 0.412 601.4 0.533 803.2 0.666 1060 0.731 1380 0.794 When the first silver was added to the copper melt an immediate increase in the absorbtion was recorded. At each addition of silver to the melt the absorbtion was registered for a period of the two to three minutes. The absorbtion signal varied about a mean value with about ± 0.05 absorbance units. It is not known if the observed variation in the detected absorbance is due to the AAS apparatus, non-optimal adjustment of mirrors and lenses or other effects. Silver was added in small amounts to the melt until the absorbtion (328.1 nm) reached about 0.800. The monochromator was thereafter adjusted to a less sensitive absorbtion line for silver (338.3 nm) and the absorbtion was detected. Additional silver was added to the melt and again the absorbtion was recorded for each addition. The temperature of the rrielt was kept constant during the test. When the test was finished the metal was weighed and the silver concentration in the copper was calculated. The measured absorbtion figures and the corresponding concentrations of silver are shown in table 1 and in figure 3. The results show a good correlation between the recorded absorbtion figures and the concentration of silver in the melt. During the test no precautions were taken in order to maintain a defined gas layer above the melt. The test shows that the thickness of the gas layer is relatively constant. ,

Claims: CLAIMS 1. A method for quantitative analysis of one or more elements in a molten metal bath, characterized in that light beams from one or more light sources are focused against the surface of the metal bath, whereafter the light is reflected from the surface of the molten metal bath to a monochromator or a polychromator connected to suitable detectors for detecting absorbed light in a gas layer associated with the melt of a wavelength or wavelengths corresponding to the element or elements to be analyzed, which absorbtion signal or signals are proportional to the atom- or molecular density for the gas component or components to be analysed and a function of the thickness of the gas layer, whereafter the concentration of the element or the elements in the molten metal bath is calculated based on known relations between the absorbtion signals, the thickness of the gas layer and the temperature of the metal bath. 2. Method according to claim 1, characterized in that at least the part of the surface of the metal bath on which the light beam is focused, is shielded against formation of oxide layers and slag. 3. Method according to claim 2, characterized in that a part of the surface of the metal bath is shielded by using a probe. 4. Method according to claim 2, characterized in that an inert gas is supplied to the surface of the metal bath.

Inventors: EIVINDSON TORKILD, EIVINDSON, TORKILD
Applicants: EIVINDSON TORKILD, ELKEM AS, EIVINDSON, TORKILD, ELKEM A/S
Application year: 1994
Main classification: G01N33
IPC codes: G01N21, G01N33