Heat-resistant, austenitic cast steel and exhaust equipment member made thereof

Abstract: Exhaust equipment members are made of a heat-resistant, austenitic cast steel with excellent castability and machinability having a composition consisting essentially, by weight, of 0.2-1% of C, 2% or less of Si, 2% or less of Mn, 8-20% of Ni, 15-30% of Cr, 0.5-6% of Nb, 1-6% of W, 0.01-0.3% of N, optionally 0.01-0.5% of S, C - Nb/8 being 0.05-0.6% and the balance being Fe and inevitable impurities.

Description: The present invention relates to a heat-resistant, austenitic cast steel with excellent castability and machinability containing C, Si, Mn, Ni, Cr, Nb, W, N and S. Some of conventional heat-resistant cast iron and heat-resistant cast steel have compositions shown in Table 1 as Comparative Examples. In exhaust equipment members such as exhaust manifolds, turbine housings, etc. for automobiles, heat-resistant cast iron such as NI-RESIST cast iron (Ni-Cr-Cu austenitic cast iron) and heat-resistant cast steel such as ferritic cast steel shown in Table 1 are employed because their operating conditions are extremely severe at high temperatures. Further, attempts have been made to propose various types of heat-resistant, austenitic cast steel. For instance, JP-A-61-87852 discloses a heat-resistant, austenitic cast steel consisting essentially of C, Si, Mn, N, Ni, Cr, V, Nb, Ti, B, W and Fe showing improved creep strength and yield strength. JP-A-61-177352 discloses a heat-resistant, austenitic cast steel consisting essentially of C, Si, Mn, Cr, Ni, Al, Ti, B, Nb and Fe having improved high-temperature and room-temperature properties by choosing particular oxygen content and index of cleanliness of steel. Japanese Patent Publication No. 57-8183 discloses a heat-resistant, austenitic cast Fe-Ni-Cr steel having increased carbon content and containing Nb and Co, thereby showing improved high-temperature strength without suffering from a decrease in high-temperature oxidation resistance. Further, JP-A-5-5161 corresponding to GP-A-471255 discloses a heat-resistant, austenitic cast steel of Fe-Ni-Cr containing Nb, W, Mo, B and Co for drastically improving high-temperature strength. Among these types of conventional heat-resistant cast iron and heat-resistant cast steel, for instance, the NI-RESIST cast iron is relatively good in a high-temperature strength at up to 900 °C, but it is poor in durability at 900 °C or higher and expensive because of a high Ni content. On the other hand, the heat resistant, ferritic cast steel is extremely poor in a high-temperature strength at 900 °C or higher. Since the heat-resistant, austenitic cast steel disclosed in JP-A-61-87852 has a relatively low C content of 0.15 weight % or less, it shows an insufficient high-temperature strength at 900 °C or higher. In addition, since it contains 0.002-0.5 weight % of Ti, harmful non-metallic inclusions may be formed by melting in the atmosphere. In addition, since the heat-resistant, austenitic cast steel disclosed in JP-A-61-177352 contains a large amount of Ni, it may suffer from cracks when used in an atmosphere containing sulfur (S) at a high temperature. Further, since the heat-resistant, austenitic cast steel disclosed in JP-B 57-8183 has a high carbon (C) content, it may become brittle when operated at a high temperature for a long period of time. The heat-resistant, austenitic cast steel disclosed in JP-A-5-5161 is suitable for exhaust equipment members exposed to high temperatures, but it is inherently poor in castability and machinability as austenitic cast steel. US-A-2 537 477 discloses austenitic alloys that may be used as cast, forged or machined engine valves und turbine vanes or buckets, that will withstand temperature variations. The alloy is suitable operable with a temperature range of 482 to 760 °C, the upper limit of the heat resistant tests was 816 °C. The austenitic alloys are optimized for corrosion resistance at high temperature without loss of strength. US-A-2 453 598 discloses a ferrous alloy particularly adapted for the manufacture of rotor forgings for gas turbines with the ranges of elements C: 0.05-0.3 %; Mn: 0.3-1.0 %; Si: 0.3-1 %; Ni: 9-15 %; Cr: 15-25 %; W: 2-5 %; Nb: 0.5-2 %; N: 0.05-0.3 %; Fe: 52-72 %. For good uniform properties in parts of widely differing thickness and for high ductability the percentage of Cr substantially exceeds the percentage of Ni. An object of the invention is to provide a heat-resistant, austenitic cast steel with excellent castability and machinability without sacrificing high temperature strength. Another object of the invention is to provide an exhaust equipment member made of such heat-resistant cast steel. These objects are solved by the features of the independent claim. As a result of intense research in view of the above objects, the inventors have found that by adding Nb, W, N and S to the heat-resistant Ni, Cr-base austenitic cast steel, the austenitic cast steel can be improved in high-temperature strength, castability and machinability. The present invention has been completed based upon this finding. Thus, the first heat-resistant, austenitic cast steel with excellent castability and machinability according to the present invention has a composition consisting by weight, of: C 0.2-1 %, C-Nb/8 0.05-0.6 %, Si 2 % or less, Mn 2 % or less, Ni 8-20 %, Cr 15-30 %, Nb 1.08-6 %, W 2.94-6 %, N 0.01-0.3 %, S 0.10-0.5 % and Fe and inevitable impurities balance. Preferably a heat-resistant, austenitic cast steel with excellent castability and machinability according to the present invention has a composition consisting, by weight, of: C 0.3-0.6 %, C-Nb/8 0.07-0.3 %, Si 0.3-1.5 %, Mn 0.3-1.5 %, Ni 8-15 %, Cr 17-25 %, Nb 1.08-4 %, W 2.94-4 %, N 0.03-0.2 %, S 0.10-0.25 % and Fe and inevitable impurities balance. The exhaust equipment member according to the present invention is made of the above heat-resistant, austenitic cast steel. The reasons for restricting the composition range of each alloy element in the heat-resistant, austenitic cast steel of the present invention with excellent castability and machinability will be explained below. In the following explanation, the amount of each element is expressed simply by "%," but it should be noted that it means "% by weight." (1) C (carbon): 0.2-1% C has a function of improving the fluidity and castability of a melt and also partly dissolves into a matrix phase, thereby exhibiting a solution strengthening function. Besides, it forms primary and secondary carbides, thereby improving a high-temperature strength. C also forms eutectic carbides with Nb, enhancing castability. To exhibit such functions effectively, the amount of C should be 0.2% or more. However, if the amount of C exceeds 1%, various carbides including eutectic carbides are excessively precipitated, leading to a poor ductility and workability. Accordingly, the amount of C is 0.2-1%. The preferred amount of C is 0.3-0.6% when S is contained in amounts 0.10 - 0.25%. (2) C - Nb/8: 0.05-0.6% The heat-resistant, austenitic cast steel of the present invention has improved castability because of the existence of eutectic carbides of Nb, and improved high-temperature strength because of the precipitation of appropriate amounts of carbides. The eutectic carbides (NbC) are formed from C and Nb at a weight ratio of 1:8. To obtain appropriate amounts of other carbides than the eutectic carbides (NbC), there should be a larger amount of C than that consumed by the eutectic carbides (NbC). Thus, C - Nb/8 should be 0.05% or more. However, if C - Nb/8 exceeds 0.6%, the heat-resistant, austenitic cast steel would become brittle, resulting in poor ductility and workability. Accordingly, C - Nb/8 is within the range of 0.05-0.6%. The preferred range of C - Nb/8 is 0.07-0.3%. (3) Si (silicon): 2% or less Si has a function as a deoxidizer and also is effective for improving an oxidation resistance. However, when it is excessively added, the austenite structure of the cast steel becomes unstable, leading to a poor high-temperature strength. Accordingly, the amount of Si should be 2% or less. The preferred amount of Si is 0.3-1.5%. (4) Mn (manganese): 2% or less Mn is effective like Si as a deoxidizer for the melt. However, when it is excessively added, its oxidation resistance is deteriorated. Accordingly, the amount of Mn is 2% or less. The preferred amount of Mn is 0.3-1.5%. (5) Ni (nickel): 8-20% Ni is an element effective for forming and stabilizing an austenite structure of the heat-resistant cast steel of the present invention together with Cr, thereby improving castability. Particularly, to have a good castability at 900°C or higher, the amount of Ni should be 8% or more. As the amount of Ni increases, such effects increase. However, when it exceeds 20%, the effects level off, meaning that the amount of Ni exceeding 20% is economically disadvantageous. Accordingly, the amount of Ni is 8-20%. The preferred amount of Ni is 8-15%. (6) Cr (chromium): 15-30% Cr is an element capable of austenizing the cast steel structure when it coexists with Ni, improving high-temperature strength and oxidation resistance. It also forms carbides, thereby further improving the high-temperature strength. To exhibit effectively such effects at a high temperature of 900°C or higher, the amount of Cr should be 15% or more. However, if it exceeds 30%, secondary carbides are excessively precipitated and a brittle σ-phase, etc. are also precipitated, resulting in an extreme brittleness. Accordingly, the amount of Cr should be 15-30%. The preferred amount of Cr is 17-25%. (7) Nb (niobium): 1.08 - 6 %. Nb forms fine carbides when combined with C, increasing the high-temperature strength and thermal fatigue resistance. Also, by suppressing the formation of the Cr carbides, it functions to improve the oxidation resistance. Further, by forming eutectic carbides, it serves to improve the castability which is important for the cast articles having complicated shapes such as exhaust equipment members. For such purposes, the amount of Nb should be 1.08 % or more. However, if it is excessively added, there are large amounts of eutectic carbides precipitated in the grain boundaries, resulting in deteriorated strength and ductility. Accordingly, the upper limit of Nb is 6%. The preferred amount of Nb is 1-4%. (8) W (tungsten): 2.94-6 % W has a function of improving the high-temperature strength. To exhibit such an effect effectively, the amount of W should be 2.94% or more. However, if it is excessively added, the Oxidation resistance is deteriorated. Thus, the upper limit of W is 6%. The preferred amount of W is 2.94-4 %. (9) N (nitrogen): 0.01-0.3% N is an element effective to produce an austenite structure and to stabilize an austenite matrix. It is also effective to make crystal grains finer. Thus, it is particularly useful for casting materials of the present invention which cannot be provided with fine crystal grains by forging, rolling, etc. The finer crystal grain structure makes it possible to have good ductility which is important for structural materials. N is also effective to eliminate the problem of poor machinability inherent in austenitic cast steel. In addition, since N is effective to retard the diffusion of C and the condensation of precipitated carbides, it is effective to prevent embrittlement. To exhibit such functions effectively, the amount of N should be 0.01% or more. However, if the amount of N exceeds 0.3%, Cr 2 N-Cr 23 C 6 is precipitated in the crystal grain boundaries, causing embrittlement and reducing an amount of effective Cr, thereby deteriorating the oxidation resistance. Thus, the upper limit of N should be 0.3%. Accordingly, the amount of N is 0.01-0.3%. The preferred amount of N is 0.03-0.2%. (10) S (sulfur): 0.01-0.5 % S is contained in the second heat-resistant, austenitic cast steel of the present invention. S has a function of forming fine spheroidal or granular sulfide particles in the cast steel, thereby improving machinability thereof, namely accelerating the separation of chips from a work being machined. Sulfides formed from S and Mn, etc. contribute to the improvement of castability like the eutectic carbides such as NbC, etc. To exhibit such an effect, the amount of S is 0.10 % or more. However, when it is excessively added, sulfide particles are excessively precipitated in grain boundaries, leading to a poor high-temperature strength. Thus, the upper limit of S is 0.5%. Therefore, the amount of S is 0.1-0.5%. The preferred amount of S is 0.10-0.25%. The heat-resistant, austenitic cast steel of the present invention is particularly suitable for thin cast parts such as exhaust equipment members, for instance, exhaust manifolds, turbine housings, etc. for automobile engines which should be durable without suffering from cracks under heating-cooling cycles. The present invention will be explained in detail by way of the following Comparative Examples. Comparative Examples 1-15 With respect to various types of heat-resistant, cast steel and iron having compositions shown in Table 1, Y-block test pieces (No. B according to JIS) were prepared by a casting process comprising melting the steel and iron in a 100-kg high-frequency furnace in the atmosphere, removing the resulting melt from the furnace while it was at a temperature of 1550°C or higher, and pouring it into a mold at about 1500°C or higher. The test pieces of the heat-resistant, austenitic cast steel (Comparative Examples 1-10) showed good fluidity at casting, thereby generating no cast defects such as voids. Next, test pieces (Y-blocks) of Comparative Examples 1-15 were subjected to a heat treatment comprising heating them at 1000 °C for 2 hours in a furnace and leaving them to be cooled in the air. In Table 1, the test pieces of Comparative Examples 11-14 are those used for heat-resistant parts such as turbo charger housings, exhaust manifolds, etc. for automobiles. The test pieces of Comparative Examples 11 and 12 are D2 and D5S of NI-RESIST cast iron. The test piece of Comparative Example 13 is a conventional heat-resistant, austenitic cast steel SCH-12 according to JIS. The test piece of Comparative Example 14 is a heat resistant, austenitic cast steel disclosed in JP-A-5-5161. Additive Component (Weight %) No. C Si Mn Ni Cr W Nb N C-Nb/8 Comparative Example 1 0.22 0.75 0.75 8.21 16.88 1.21 1.20 0.03 0.07 2 0.41 0.58 0.98 10.10 20.02 3.01 2.02 0.09 0.16 3 0.52 0.63 0.82 19.55 29.72 5.95 2.66 0.18 0.19 4 0.41 0.52 0.88 10.15 20.05 3.05 1.88 0.09 0.16 5 0.56 0.82 1.05 10.65 21.25 3.38 3.95 0.06 0.06 6 0.49 1.01 0.75 10.33 20.54 3.15 2.11 0.27 0.23 7 0.72 0.95 0.66 10.51 20.23 2.88 1.12 0.18 0.58 8 0.94 1.01 0.75 10.31 19.92 3.11 5.66 0.09 0.23 9 0.62 0.85 0.48 9.65 20.85 3.25 1.68 0.10 0.41 10 0.47 0.92 0.66 10.09 21.23 2.66 2.02 0.12 0.22 11 2.77 2.12 0.88 21.10 2.44 - - - - 12 1.89 5.32 0.41 34.50 2.35 - - - - 13 0.21 1.24 0.50 9.10 18.80 - - - - 14 0.41 1.02 0.48 10.50 20.08 3.01 0.49 - 0.34 15 0.21 1.01 0.58 8.45 16.55 1.02 0.68 0.03 0.12 Next, with respect to each cast test piece, the following evaluation tests were conducted. (1) Tensile test at a room temperature Conducted on a rod test piece (No.14 test piece according to JIS) having a gauge distance of 50 mm and a gauge diameter of 14 mm. (2) Tensile test at a high temperature Conducted on a flanged test piece having a gauge distance of 50 mm and a gauge diameter of 10 mm at 1000°C. (3) Thermal fatigue test Using a rod test piece having a gauge distance of 20 mm and a gauge diameter of 10 mm, a heating-cooling cycle was repeated to cause thermal fatigue failure in a state where expansion and shrinkage due to heating and cooling were completely restrained mechanically, under the following conditions: Lowest temperature: 150°C, Highest temperature: 1000°C, Each 1 cycle: 12 minutes, and Test machine: Electric-hydraulic servo-type thermal fatigue test machine. (4) Oxidation test A rod test piece having a diameter of 10 mm and a length of 20 mm was kept at 1000°C for 200 hours in the air, and its oxide scale was removed by shot blasting to measure a weight loss per a unit surface area. By calculating oxidation weight loss (mg/mm 2 ) after the oxidation test, the oxidation resistance was evaluated. (5) Machinability test A drilling test was conducted to evaluate machinability which was most critical at drilling a work made of this kind of material. A test piece made of each cast steel or iron was drilled ten times to measure the amount of flank wear of the drill and calculate the flank wear per one cut hole under the following conditions: Machine tool: Vertical Machining Center (5.5 kW), Drill: Solid Carbide Drill (6.8 mm in diameter), Cutting Speed: 40 m/min, Feed Speed: 0.2 mm/rev., step feed, Hole Depth: 20 mm, Entire Length of Drill: 42 mm, and Cutting Fluid: Oil. The results of the tensile test at a room temperature, the tensile test at 1000°C, the thermal fatigue test and the oxidation test, and the drilling test are shown in Tables 2, 3, 4, and 5, respectively. at Room Temperature No. 0.2% Offset Yield Strength (MPa) Tensile Strength (MPa) Elongation (%) Hardness (H B ) Comparative Example 1 250 460 17 179 2 295 525 14 187 3 360 575 7 197 4 300 545 11 192 5 365 590 7 192 6 350 560 12 192 7 275 610 8 207 8 380 620 8 223 9 365 585 9 207 10 340 560 12 192 11 190 455 16 179 12 255 485 9 163 13 250 560 20 170 14 350 560 4 201 15 290 500 19 170 at 1000°C No. 0.2% Offset Yield Strength (MPa) Tensile Strength (MPa) Elongation (%) Comparative Example 1 40 64 68 2 47 75 49 3 72 115 37 4 52 90 42 5 68 105 38 6 62 100 26 7 75 110 26 8 78 115 22 9 70 105 20 10 64 100 33 11 33 41 33 12 33 44 29 13 35 55 49 14 66 108 26 15 55 62 75 No. Thermal Fatigue Life (Cycle) Weight Loss by Oxidation (mg/mm 2 ) Comparative Example 1 120 38 2 130 32 3 185 15 4 175 30 5 180 28 6 185 33 7 205 22 8 220 46 9 195 48 10 175 25 11 56 765 12 85 55 13 80 85 14 180 25 15 145 35 No. Flank Wear per One Cut Hole (mm) Comparative Example 1 0.062 2 0.052 3 0.052 4 0.045 5 0.058 6 0.035 7 0.045 8 0.040 9 0.035 10 0.041 11 0.005 12 0.005 13 0.095 14 0.105 15 0.015 As is clear from Table 2, the test pieces of Comparative Examples 1-10 are comparable to or even superior to those of Comparative Examples 11 and 12 (NI-RESIST D2 and D5S) and Comparative Example 13 (SCH12) with respect to properties at a room temperature. Also, as is clear from Tables 3 and 4, the test pieces of Comparative Examples 1-10 are superior to those of Comparative Examples 11-13 with respect to the high-temperature properties (0.2 % offset yield strength, tensile strength, thermal fatigue life and weight loss by oxidation). In addition, the test pieces of Comparative Examples 1-10 are comparable to the heat resistant, austenitic cast steel disclosed in JP-A-5-5161 (Comparative Example 14) in mechanical properties. As is clear from Table 5, since the heat resistant, austenitic cast steel contains an appropriate amount of N and has well balanced amounts of C and Nb expressed by (C-Nb/8), it is much superior in machinability to the heat resistant, austenitic cast steel of Comparative Examples 13 and 14. Next, an exhaust manifold (thickness: 2.0-2.5 mm) and a turbine housing (thickness: 2.5-3.5 mm) were produced by casting the heat-resistant, austenitic cast steel of comparative Example 2. All of the resulting heat-resistant cast steel parts were free from casting defects. These cast parts were machined to evaluate their machinability. As a result, no problem was found in any cast parts. Further, the exhaust manifold and the turbine housing were mounted to a high-performance, straight-type, four-cylinder, 2000-cc gasoline engine (test machine) to conduct a durability test. The test was conducted by repeating 500 heating-cooling (Go-Stop) cycles each consisting of a continuous full-load operation at 6000 rpm (14 minutes), idling (1 minute), complete stop (14 minutes) and idling (1 minute) in this order. The exhaust gas temperature under a full load was 1050°C at the inlet of the turbo charger housing. Under this condition, the highest surface temperature of the exhaust manifold was about 980°C in a pipe-gathering portion thereof, and the highest surface temperature of the turbo charger housing was about 1020°C in a waist gate portion thereof. As a result of the evaluation test, no gas leak and thermal cracking were observed. It was thus confirmed that the exhaust manifold and the turbine housing made of the heat-resistant, austenitic cast steel of the present invention had excellent durability and reliability. Examples 1-9 Test pieces were prepared from various types of heat-resistant cast steel having compositions shown in Table 6 and tested in the same manner as in Comparative Example 1. The results of the tensile test at a room temperature, the tensile test at 1000°C, the thermal fatigue test and the oxidation test, and the drilling test are shown in Tables 7, 8, 9, and 10, respectively. Additive Component (Weight %) No. C Si Mn Ni Cr W Nb N S C-Nb/8 1 0.45 0.85 1.02 10.55 20.88 3.02 2.50 0.12 0.10 0.14 2 0.98 0.52 0.75 18.55 28.44 5.80 3.18 0.24 0.20 0.58 3 0.43 0.75 0.60 10.02 20.12 2.94 1.53 0.08 0.41 0.24 4 0.80 0.66 0.78 10.32 21.02 3.50 5.95 0.14 0.13 0.06 5 0.44 1.05 0.85 9.83 20.33 3.02 1.62 0.09 0.11 0.24 6 0.45 0.54 1.05 10.11 20.52 3.14 2.02 0.06 0.15 0.20 7 0.50 1.11 0.70 10.51 19.58 3.08 1.75 0.06 0.13 0.28 8 0.55 0.95 0.51 9.96 20.75 3.35 1.08 0.07 0.21 0.41 9 0.42 1.09 0.92 10.54 21.02 2.98 2.70 0.06 0.18 0.08 at Room Temperature Example No. 0.2% Offset Yield Strength (MPa) Tensile Strength (MPa) Elongation (%) Hardness (H B ) 1 350 570 17 179 2 420 625 5 223 3 355 555 9 187 4 390 625 8 187 5 345 570 10 192 6 360 560 12 192 7 365 590 8 197 8 370 590 6 197 9 355 565 10 187 at 1000°C Example No. 0.2% Offset Yield Strength (MPa) Tensile Strength (MPa) Elongation (%) 1 60 110 55 2 80 125 26 3 67 108 37 4 78 115 32 5 64 105 31 6 66 110 38 7 69 115 48 8 68 105 40 9 66 105 29 Example No. Thermal Fatigue Life (Cycle) Weight Loss by Oxidation (mg/mm 2 ) 1 160 30 2 210 18 3 185 28 4 200 26 5 165 30 6 170 40 7 180 48 8 160 50 9 175 22 Example No. Flank Wear per One Cut Hole (mm) 1 0.010 2 0.008 3 0.005 4 0.009 5 0.010 6 0.008 7 0.012 8 0.010 9 0.007 As is clear from Table 7, the test pieces of Examples 1-9 are comparable to or even superior to those of Comparative Examples 11-13 with respect to properties at a room temperature. Also, as is clear from Tables 8 and 9, the test pieces of Examples 1-9 are superior to those of Comparative Examples 11-13 with respect to the high-temperature properties (0.2% offset yield strength, tensile strength, thermal fatigue life and weight loss by oxidation). In addition, the test pieces of Examples 1-9 are comparable to the heat-resistant, austenitic cast steel of Comparative Example 14 in mechanical properties. As is clear from Table 10, since the heat-resistant, austenitic cast steel of the present invention contains appropriate amounts of S and N and has well balanced amounts of C and Nb expressed by (C - Nb/8), it is much superior in machinability to the heat-resistant, austenitic cast steel of Comparative Examples 13 and 14. Next, the same exhaust manifold and turbine housing as in Comparative Example 11 were produced by casting the heat-resistant, austenitic cast steel of Example 6. All of the resulting heat-resistant cast steel parts were free from casting defects. These cast parts were machined to evaluate their machinability. As a result, no problem was found in any cast parts. Further, the exhaust manifold and the turbine housing were mounted to a high-performance, straight-type, four-cylinder, 2000-cc gasoline engine to conduct a durability test in the same manner as in Comp.Example 1. As a result of the evaluation test, it was observed that there were no gas leak and thermal cracking, and that the exhaust manifold and the turbine housing made of the heat-resistant, austenitic cast steel of the present invention had excellent durability and reliability. As described above in detail, the heat-resistant, austenitic cast steel of the present invention has excellent castability, machinability and high-temperature strength without deteriorating a room-temperature ductility, and it can be produced at a low cost. The heat-resistant, austenitic cast steel of the present invention is particularly suitable for exhaust equipment members for engines, such as exhaust manifolds, turbine housings, etc. The exhaust equipment members made of such heat-resistant, austenitic cast steel according to the present invention show excellent castability, machinability and durability.

Claims: A heat-resistant austenitic cast steel with excellent castability and machinability containing C, Si, Mn, Ni, Cr, Nb, W, N, and S, said austenitic cast steel has a composition, by weight, of: C 0.2 - 1 %, C - Nb/8 0.05 - 0.6 %, Si 2 % or less, Mn 2 % or less, Ni 8-20%, Cr 15 - 30 %, Nb 1.08 - 6 %, W 2.94-6%, N 0.01 - 0.3 %, S 0.10 - 0.50 %; and Fe and inevitable impurities balance. A cast exhaust equipment member made of the heat-resistant, austenitic cast steel according to claim 1. The cast exhaust equipment member according to claim 2, wherein said austenitic cast steel has a composition, by weight, of: C 0.3 - 0.6 %, C - Nb/8 0.07 - 0.3 %, Si 0.3 - 1.5 %, Mn 0.3 - 1.5 %, Ni 8 - 15 %, Cr 17 - 25 %, Nb 1.08-4%, W 2.94-4%, N 0.03 - 0.2 %, S 0.10 - 0.25 %; and Fe and inevitable impurities balance. The cast exhaust equipment member according to claim 2 or 3 is a cast exhaust manifold. The cast exhaust equipment member according to claim 2 or 3 is a cast turbine housing.

Inventors: FUJITA TOSHIO, KIMURA HIROFUMI, TAKAHASHI NORIO, WATANABE RIKIZOU, FUJITA, TOSHIO, KIMURA, HIROFUMI, TAKAHASHI, NORIO, WATANABE, RIKIZOU
Applicants: HITACHI METALS LTD, HITACHI METALS, LTD.
Application year: 1994
Main classification: C22C38
IPC codes: C22C38