Oxide super-conductor

Abstract: An oxide superconductor composed of Cu, O and M (M is Ba, Sr and/or Ca) and including alternately arranged at least one rock-salt structure section and at least one infinite layer structure section, wherein the rock-salt structure section consists of two atomic layers each consisting of O and M and each having an atomic ratio O/M of 1 or less, and the infinite layer structure section consists of alternately arranged, first and second atomic layers. Each of the first atomic layers consists of O and Cu and has an atomic ratio O/Cu of 2, while each of the second atomic layers consists of the element M. The infinite layer structure section may consist of only one first atomic layer.

Description: This invention relates to an oxide superconductor having a superconducting transition temperature Tc higher than liquid nitrogen (Tc ≥ 77 K). Because of their peculiar characteristics such as zero resistivity, perfect diamagnetism and Josephson effect, superconductors are adapted for utilization in various applications such as electric power transmission, electric generators, nuclear fusion plasma containment, magnetic leviation trains, magnetic shield and high speed computers. An oxide superconductor (La 1-x Ba x ) 2 CuO 4 having Tc of about 30 K was found by Bendonorz and Muller in 1986. Since then, various superconductors such as YBa 2 Cu 3 O x (Tc = 90 K), Bi-Sr-Ca-Cu-O (Tc = 110 K) and Tl-Ba-Ca-Cu-O (Tc = 125 K) have been reported. From the standpoint of industrial application, these superconductors have a drawback that the raw material is not available at low costs or is toxic to human bodies. Recently, a new superconductor (Sr 1-x Ca x ) 1-y CuO 2+z having Tc of 110 K was found (M. Azuma et al, Nature, 356 , 775 (1992)). This superconductor has a simple crystal structure called an "infinite-layer" structure constituted from a Cu-O 2 layer and a (Sr/Ca) layer. Such a crystal structure was first found in a compound of Ca 0.86 Sr 0.14 CuO 2 in 1988 (T. Siegrist et al, Nature, 334 , 231 (1988)) and a large number of researchers had tried to prepare a superconductor of the infinite layer structure. The above infinite layer structure superconductor is obtained by a heat treatment of a raw material blend at 1,000 °C for 30 minutes under a super-high pressure of 6 GPa. This treatment is performed in a gold capsule in which KClO 4 is incorporated together with the raw material blend. During the heat treatment, KClO 4 decomposes to generate oxygen so that the inside space of the capsule is maintained at a high oxygen gas partial pressure. This causes such a layer defect that part of (Sr/Ca) is deficient and can impart superconductivity. No periodicity or regularity exists in this layer defect. There is provided in accordance with the present invention an oxide superconductor composed of Cu, O and at least least two alkaline earth metals selected from Ba, Si and Ca and comprising alternately arranged at least one rock-salt structure section and at least one infinite layer structure section, said rock-salt structure section consisting of two atomic layers each consisting of O and M and each having an atomic ratio O/M of 1 or less, wherein M is at least one alkaline earth metal selected from Ba, Sr and Ca, said infinite layer structure section consisting of j-number and k-number of first and second atomic layers, respectively, wherein j is an integer of 1 or more and k is an integer of 1 or more, said first and second atomic layers being alternately arranged, each of said first atomic layers consisting of O and Cu and having an atomic ratio O/Cu of 2, and each of said second atomic layers consisting of element M, wherein M is at least one alkaline earth metal selected from Ba, Sr and Ca. As just noted, the present invention provides an oxide superconductor composed of Cu, O and at least two alkaline earth metals selected from Ba, Sr and Ca. The superconductor includes alternately arranged, at least one rock-salt structure section and at least one infinite layer structure section. The rock-salt structure section consists of two atomic layers each of which consists of O and the above-mentioned at least one alkaline earth metal and has an atomic ratio O/M (where M represents the alkaline earth metal or metals) of 1 or less, while the infinite layer structure section consists of j-number of first atomic layer and k-number of second atomic layer, wherein j is an integer of 1 or more and k is an integer of 1 or more, the first and second atomic layers being alternately arranged, i.e. j = k or j = k+1. The first atomic layer consists of O and Cu and has an atomic ratio O/Cu of 2, while the second atomic layer consists of the above-mentioned at least one alkaline earth metal. The total number (j+k) of the first and second atomic layers of the infinite layer structure section is preferably 2n-1 wherein n is an integer of 2 or more, i.e. preferably j = k+1. The present invention will now be described in detail below with reference to the accompanying drawings, in which: Fig. 1 is a powder X-ray diffraction pattern (using alpha rays of CuK) of a sample of (Sr0 .7 Ca 0.3 ) 0.9 CuO 2+z + "a" % by weight (a = 0.0 to 6.0) of KCl 3 obtained in one embodiment of the present invention; Fig. 2 is a graph showing temperature-magnetic susceptibility characteristics of the sample of Fig. 1; Fig. 3 is a graph showing temperature-specific resistivity characteristics of (Sr 0.7 Ca 0.3 ) 0.9 CuO 2+z + 2 % by weight of KCl 3 used in the embodiment of Fig. 1; Fig. 4 is a powder X-ray diffraction pattern (using alpha rays of CuK) of a sample of Sr 0.6 Ca 0.333 CuO 2+z (z = 0.00 to 0.20) in another embodiment of the present invention; Fig. 5 is a graph showing temperature-magnetic susceptibility characteristics of the sample of Fig. 4; Fig. 6 is a graph showing temperature-specific resistivity characteristics of the sample of Fig. 4; Fig. 7 is an electron beam diffraction pattern of the sample of Sr 0.6 Ca 0.333 CUO 2.10 in the embodiment of Fig. 4; Fig. 8 is a powder X-ray diffraction pattern (using alpha rays of CuK) of the sample of Sr 0.6 Ca 0.333 CuO 2.10 in the embodiment of Fig. 4; Fig. 9 is a high resolution, transmission electron photomicroscope of the sample of Sr 0.6 Ca 0.333 CuO 2.10 in the embodiment of Fig. 4; Fig. 10 is a schematic illustration explanatory of the crystal structure of the superconductor of the present invention; Fig. 11 is schematic illustration of a high resolution, transmission electron photomicroscope of the sample of Sr 0.6 Ca 0.333 CuO 2.10 in the embodiment of Fig. 4; and Fig. 12 is an illustration explanatory of the general crystal structure of the superconductor of the present invention. Example 1 Production of Superconductor of (Sr 0.7 Ca 0.3 ) 0.9 CuO 2+z + KCl 3 : Powders of SrCO 3 , CaCO 3 and CuO each having a purity of 99 % or more were blended in amounts providing a composition (Sr 0.7 Ca 0.3 ) 0.9 CuO 2+z and calcined at 1,000 °C for 24 hours in an oxygen stream, and the calcined product was pulverized. Such calcination and pulverization steps were repeated several times. The resulting calcined powder was admixed with a quantity ("a" % by weight where "a" is 0.0, 1.00, 2.00, 3.00, 4.00, 5.00 or 6.00) KCl 3 (oxidizing agent) to obtain 7 kinds of precursors. Each precursor was charged in a gold capsule and heat-treated at 930 °C and 5 GPa for 20 minutes using a super-high pressure generator of a hexagonal cubic anvil type. The gold capsule was placed in a graphite sleeve heater through a BN layer. After pressurization through a pyrophyrite, an electric current was fed to the graphite for performing the heat treatment. Fig. 1 is a powder X-ray diffraction pattern (using alpha rays of CuK) of the thus obtained products. When no oxidizing agent was used (a = 0.00), the product had a single layer of an infinite-layer structure. Peaks attributed to impurities appeared when the amount of the oxidizing agent was increased. Thus, with an amount of the oxidizing agent greater than 4 % by weight (a ≥ 4.0), no peaks ascribed to the infinite layer structure were present. Fig. 2 is a graph showing temperature-magnetic susceptibility characteristics of the above samples. The measurement was performed using SQUID in the magnetic field of 7.955x10 3 A/m (100 Oe) in a cooled condition. Only a weak minor signal was detected in the case of the sample containing no oxidizing agent. The signal intensity increased with the increase in the content of the oxidizing agent and became maximum when the content of the oxidizing agent was 4.0 % by weight (a = 4.0). The superconductive volume fraction of this sample (a = 4.0) at a temperature of 5 K is estimated to be about 6 %. When the amount of the oxidizing agent was further increased, the superconductivity was lost. Since, as described previously with reference to Fig. 1, the peaks attributed to the infinite layer structure are lost when the content of the oxidizing agent is 4.0 % by weight, it is believed that a novel superconductive crystallographic phase other than of an infinite layer structure is present in the sample (Sr-Ca-Cu-O system or Sr-Ca-Cu-O-K-Cl system) obtained using 4.0 % by weight of the oxidizing agent. At present, the infinite layer structure is the only known superconductive crystallographic phase in the Sr-Ca-Cu-O system. In view of the fact that such a novel superconductive phase is obtained in a highly oxidizing atmosphere and shows high Tc of about 100 K, it is believed that the novel superconductor is a p-type oxide having a CuO 2 layer as a conductive layer. Any known p-type oxide superconductor having Tc of higher than 77 K has a CuO 2 layer as a conductive layer and has a periodical structure of 1x10 -9 m (10 Å) or more in the direction normal to the CuO 2 layer. Such a periodical structure gives, in a powder X-ray diffraction pattern thereof, a characteristic peak at a low angle side (2 < 10°). As shown in Fig. 1, samples giving a relatively strong Meissner signal (a = 2.0 to 4.0) show small peaks at 2 of about 8.5°. These peaks are considered to have a relation with the novel superconductive phase. Fig. 3 is a graph showing a relationship between the temperature and the specific resistivity of a sample obtained using 2.0 % by weight of the oxidizing agent. As the temperature is lowered from room temperature, the resistivity is increased in a pattern similar to a semiconductor but is decreased at a temperature of about 100 K or less due to superconductivity. At a temperature of 4.2 K, however, the resistivity is not zero. The reason for this is considered to be because an impurity phase contaminates the superconductive phase of the sample. The formation of such an impurity phase is considered to be attributed to the deposition of KCl formed by the decomposition of KClO 3 on the grain boundary during the heat treatment. Example 2 Production of Superconductor of Sr 0.6 Ca 0.333 CuO 2+z : Powders of Sr 2 CUO 3 , Ca 2 CO 3 , CaO 2 and CuO each having a stable phase under ambient pressure were blended in amounts providing a composition Sr 0.6 Ca 0.333 CuO 2+z (z = 0.00, 0.05, 0.10, 0.15 or 0.20) to obtain 5 kinds of precursors. Each precursor was charged in a gold capsule and heat-treated at 930 °C and 5 GPa for 30 minutes. It is reported that homogeneous oxidation may be carried out using CaO 2 as both a raw material and an oxidizing agent for the production of a Sr-Ca-Cu-O series p-type superconductor (Adachi et al, 5th International Superconductivity Symposium, ISS's 92, Nov. 16-19, 1992, Kobe, CEP-24). The use of CaO can also avoid the formation of a KCl impurity. The powder X-ray diffraction patterns of the thus obtained samples are shown in Fig. 4. When z is 0.00, the oxide sample shows mixed phases of an infinite layer structure and CuO. With an increase of the oxygen, the peak attributed to the infinite layer structure becomes small. Thus, in the case of the samples having z of 0.05-0.15, a small peak appears at 2 of 6.5°. When z is 0.20, a peak appears at 2 of 8.5°. It is also seen that the 101 reflection at 2 of 35° gradually decreases with an increase of the oxygen content. Since the 101 reflection peak coincides with the main peak of CuO, the 101 peak of the infinite layer structure almost completely disappears when z is 0.10 or more. Fig. 5 is a graph showing temperature-magnetic susceptibility characteristics of the above samples. The measurement was performed in a magnetic field of 7.955x10 2 A/m (10 Oe). A significantly larger Meissner signal was observed as compared with the samples obtained using KClO 3 as an oxidizing agent. In particular, the superconductivity volume fraction at 5 K is as high as 20 % when z is 0.05-0.15. These results indicate that the periodical structure showing the peak at 2 of 6.5° is a superconductive phase having a high class of Tc of about 90 K. When z is 2.0, the peak at 2 of 6.5° disappears but a new peak is present at 2 of 8.5°. This new peak is also considered to be attributed to a novel superconductive phase. The sample having z of 2.0 shows superconductivity (Tc = about 100 K) and the superconductivity volume fraction at 5K thereof is about 10 %. The foregoing results indicate that in the Sr-Ca-Cu-O series samples, there is formed novel superconductive phases having periodical structures of 1.36x10 -9 m (13.6 Å) and 1.03x10 -9 m (10.3 Å) which correspond to the peaks at 2 of 6.5° and 8.5°, respectively. Fig. 6 shows temperature-specific resistivity characteristics of the above samples. In the case of the samples having z of 0.05 or more, the resistivity decreases in a pattern similar to a metal as the temperature decreases and abruptly decreases around 100 K. At about 80 K, the resistivity becomes zero. Fig. 7 is an electron beam diffraction pattern of the sample having z of 0.10. The diffraction image indicates that the superconductive phase showing a peak at 2 of 6.5° has lattice constants along the a-axis of 3.86 A and along the b-axis of 2.72x10 -9 m (27.2 Å). Fig. 8 is a powder X-ray diffraction pattern (indexed) of the sample having z of 0.10. The main phase is the novel superconductive phase. There are impurity phases attributed to CuO (marked with *), the infinite layer structure phase (parenthesized index) and unknown phases (marked with o and +). As described previously, the content of the infinite layer structure phase is very small. Such a small amount of the infinite layer structure phase would not provide a superconductive volume fraction at 5 K of 20 % or more. Fig. 9 is a high resolution, transmission electron photomicroscope showing the lattice structure of the sample in which z = 0.10. The lattice structure is composed of periodical structure units each having a width of 1.36x10 -9 m (13.6 Å) and consisting of seven atomic layers. The foregoing results suggest that the novel superconductive crystallographic phase has lattice constants of a = 3.86 and c = 27.2 and is constituted from a series of the following 7 atomic layers arranged in the direction normal to the c-axis: /(M-O)/(M-O)/(Cu-O 2 )/(M)/(Cu-O 2 )/(M)/(Cu-O 2 )/ The double layer (M-O)/(M-O) forms a rock-salt structure while the other 5 layers constitute an infinite layer structure. The rock-salt structure section gives the oxygen atoms thereof to the adjacent (Cu-O 2 ) layers so that each of the (Cu-O 2 ) layers forms a (Cu-O 5 ) pyramid which is commonly observed in p-type copper oxide superconductors (other than infinite layer structure superconductors). The crystal structure of the superconductor of the present invention is shown in Fig. 10 in which the black circle designates a copper atom and the white circle designates an atom of an alkaline earth metal. Each of the corners or apices is a position at which an oxygen atom is located. The non-stoichiometry of oxygen serves to control the amount of holes in the (Cu-O 2 ) layers. In view of the similarity to Bi-series or Tl-series superconductors, the novel superconductive phase is considered to include a series of superconductive phases in which the thickness of respective infinite layer structure sections varies by intergrowth. In fact, as seen from Fig. 11 which is a schematic illustration of a high resolution, transmission electron photomicroscope of the sample of Sr 0.6 Ca 0.333 CuO 2.10 , a number of lattice defects are observed. The periodical structure of 1.03x10 -9 m (10.3 Å) confirmed in the powder X-ray diffraction pattern of Fig. 4 is a substance having a crystal structure in which one unit lattice portion (two atomic layers of /(M)/(Cu-O 2 )) is removed from the layer of 1.36x10 -9 m (13.6 Å), i.e. which is an infinite layer structure section consisting of 3 atomic layers. The present invention also provides a superconductor having a periodical structure of 1.7x10 -9 m (17.0 Å) in which one unit lattice portion is inserted into the infinite layer structure section and which, therefore, consists of 7 atomic layers. Fig. 12 is an illustration of the general crystal structure of the superconductor of the present invention. In Fig. 12, the black circle designates a copper atom, the white circle designates an atom of an alkaline earth metal, and each of the corners or apices is a position at which an oxygen atom is located. Example 3 Preparation of Other M 1-y CuO 2+z Superconductors: Oxides having a composition of (Sr 0.7 Ca 0.3 ) 1-y CuO 2.10 were produced. When (1-y) was greater than 1 (1-y > 1.0), the samples obtained showed a superconductive volume fraction at 5 K of 2 % or less. When (1-y) was less than 0.7 (1-y < 0.7), the samples contained a plurality of impurities and showed a superconductive volume fraction at 5 K of 3 % or less. Superconductors having a satisfactory superconductive volume fraction were obtained when (1-y) was between 0.7 and 1. Oxides having a composition of (Sr 1-x Ba x ) 0.95 CuO 2.10 were produced. When x was between 0 and 0.30 (0 ≤ x ≤ 0.30), novel superconductors having a superconductive volume fraction at 5 K of more than 10 % were obtained. When x exceeded 0.3, the superconductivity was lowered due to the inclusion of a BaO 2 impurity phase. Oxides having a composition of (Sr 1-x Ca x ) 0.95 CuO 2.10 were produced. When x was between 0 and 0.60 (0 ≤ x ≤ 0.60), novel superconductors having a superconductive volume fraction at 5 K of more than 10 % were obtained. When x exceeded 0.6, the superconductive volume fraction of resulting superconductors was lower than 10 % but the infinite layer structure was stabilized. In the above oxide superconductors of (Sr,Ca) 1-y CuO z series, satisfactory superconductive volume fractions of 10 % or more were obtained when the amount of excess oxygen z was within the range of between 0.02 and 0.24. A value of z below 0.02 was insufficient to provide the superconductive volume fraction of 10 % or more because the infinite layer structure was stable. When, the value exceeds 0.24, on the other hand, impurities of non-superconductive phases were formed. The foregoing procedures were repeated under various pressures of 1-8 GPa, revealing that these pressures were suited for the production of superconductors of the present invention.

Claims: An oxide superconductor composed of Cu, O and at least two alkaline earth metals selected from Ba, Sr and Ca and comprising alternately arranged at least one rock-salt structure section and at least one infinite layer structure section, said rock-salt structure section consisting of two atomic layers each consisting of O and M and each having an atomic ratio O/M of 1 or less, wherein M is at least one alkaline earth metal selected from Ba, Sr and Ca, said infinite layer structure section consisting of j-number and k-number of first and second atomic layers, respectively, wherein j is an integer of 1 or more and k is an integer of 1 or more, said first and second atomic layers being alternately arranged, each of said first atomic layers consisting of O and Cu and having an atomic ratio O/Cu of 2, and each of said second atomic layers consisting of element M, wherein M is at least one alkaline earth metal selected from Ba, Sr and Ca. A superconductor as claimed in Claim 1, wherein the total number of (j + k) of said first and second atomic layers is 2n-1 wherein n is an integer of 2 or more. A superconductor as claimed in Claim 1 or Claim 2, and composed of Cu, O and either (Sr, Ca) or (Sr, Ba).

Inventors: ADACHI SEIJI, MOURI NOBUO, TANAKA SHOJI, YAMAUCHI HISAO, ADACHI, SEIJI, MOURI, NOBUO, TANAKA, SHOJI, YAMAUCHI, HISAO, TANAKA, SHOJI, C/O SUPERCONDUCT. RES. LAB.
Applicants: INT SUPERCONDUCTIVITY TECH, MATSUSHITA ELECTRIC IND CO LTD, INTERNATIONAL SUPERCONDUCTIVITY TECHNOLOGY CENTER, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1994
Main classification: H01L39
IPC codes: H01L39, C01G3, C01G1, H01B12