Process for the production of powder catalysts

Abstract: Magnesium chloride, titanium chloride and at least an electron donor are introduced in a plasma torch. These chlorides being in solution or in suspension in a liquid that can be an electron donor. A very fine granulometry powder is collected after cooling. The powder is very fine, it has a controlled morphology and it can be used as catalyst for alpha-olefins polymerization.

Description: The present invention concerns a process for the production of powder catalysts comprising magnesium chloride and titanium chloride. Magnesium chloride (MgCl2) powder covered with titanium chloride (TiCl3, TiCl4) is an original material well-known as Ziegler-Natta type catalysts. The yield of these catalysts depends among other things on the particle size of the original material; the finer the particles are, the higher the yield is . There is thus a need for an improved process for the production of catalyst powders, more particularly of MgCl2 powder covered with titanium chloride that allows to obtain a very fine granulometry. In fact, it is particularly difficult to obtain a very fine granulometry powder by pulverizing MgCl2 under anhydrous conditions, although this fineness is desired when MgCl2 is used in the catalysts preparation. The morphology of polymer grains - and consequently, the polymer apparent density - is among other things determined by the catalyst morphology. It is then very desirable to be able to control the morphology of the catalyst powder that is ideally spherical. Patent GB-1279208-A (Standard Telephones; equivalent to DE-2217951-A, Deutsche ITT) discloses a process of powder production consisting in vaporizing the material or its components in an inductive coupling plasma (ICP) then in condensing the vapour. Patent US-4650778-A (Klabunde et al.) shows a process for the preparation of halogen metal particles consisting in vaporizing them by heating, then in condensing the vapour in the presence of a reactive diluant. The obtained solid must be activated by metal alkyls to be used as catalysts of olefin polymerizations. Belgian Patent BE-1005737-A (filed on 08.05.92 and published on 11.01.94) claims a process for the production of magnesium powder, characterized in that it consists essentially in introducing rough powder of magnesium chloride, with or without titanium chloride in a plasma torch and cooling the vapour in order to collect a very fine granulometry powder, eventually by covering this powder with an electron donor during the cooling. The process of the invention for the production of a magnesium chloride and titanium chloride based powder catalyst essentially consists in the introduction into a plasma torch (i) of magnesium chloride, (ii) of titanium chloride and (iii) at least one electron donor, the magnesium chloride being in solution or in suspension in a liquid L1, the titanium chloride being in solution or in suspension in a liquid L2 or being liquid TiCl 4 , the electron donor being L1 and/or L2 and/or another liquid compound or in solution or in suspension in a liquid, and to collect a powder after cooling. The preferred embodiments of the present invention can provide a process for the production of such a powder catalyst having a very fine granulometry. The preferred embodiments of the invention can also provide a process for the production of such a powder catalyst having a controlled morphology. The powder catalyst produced in accordance with the process of the present invention can be used in an olefins polymerization process. The obtained powder catalyst is described here as a MgCl2 and titanium chloride based powder catalyst, and without limiting the claims is thought to be composed of MgCl2 covered with titanium chloride. The magnesium and titanium chloride compounds can be partially (preferably to less than 50% in moles, even to less than 25 mol %) replaced by alcoholates (preferably with short chain, the most preferred being methanolate and ethanolate). According to a preferred embodiment, a solution containing the MgCl2 and the titanium chloride is used, which can be obtained by the introduction of rough MgCl2 powder in an appropriate solvent and after that by the addition of titanium chloride. As appropriate solvents, preferably those that allow to dissolve large quantities of MgCl2 (at least 1 g/l and preferably at least 10 g/l) and titanium chloride are chosen. For example, tetrahydrofuran and alcohols such as ethanol or methanol can be used. Methanol is preferably used. According to another embodiment, a suspension of the two components in a liquid is used. According to a third embodiment, a suspension of one of the components in a solution of the other is used. According to these three embodiments, it is preferred to use the electron donor as solvent or as liquid. Although it does not concern a preferred embodiment of the present invention, one can also introduce separately into the plasma the different required components : for example a suspension or a solution of MgCl2 at the same time as a suspension or a solution of titanium chloride or liquid TiCl4, the electron donor being one of these two solvents or liquids, being added to one of these two solutions or suspensions or being introduced separately in liquid, dissolved or suspended form. The electron donors are well-known in the art of the Ziegler-Natta catalysis, and it is not necessary to describe it here. As examples of electron donors, ethers, preferably cyclic ethers (the most prefered being tetrahydrofuran), alcohols (the most prefered being methanol and ethanol), benzoates (particularly ethyl benzoate) and phthalates (particularly dibutyl phthalate) can be quoted. Every suspension or solution or liquid may be introduced in the plasma by every appropriate means, preferably in an inert carrier gas flow such as nitrogen and/or argon. Generally, the suspension or the solution, compressed by an inert gas or by mechanical means, is admitted at the plasma level with aid of a capillary, a capillary system or a pulverization device. The solution flow is provided by an injection and/or a pulverization system, at a value dependent on the plasma generator power (the higher the power is high). Without intention to make a connection with any theory, it is possible to say that when a solution or a suspension is injected in the plasma, the energy of the plasma induces instantaneous evaporation of the solvent or the liquid, respectively. The solid obtained consequently to the evaporation of the solvent is pulverized in form of micro-droplets; these under enormous temperature gradient undergo quenching that does not allow any subsequent recristallisation of the solid. This quenching can be amplified by addition to the mechanism of cold surfaces on which the micro-droplets can condensate. Again, without intention to make a connection with any theory, it is assumed that good results are only obtained with the presence of an electron donor during the vaporization of magnesium chloride and/or titanium chloride. Consequently, the plasma energy must preferably be adjusted in order to avoid the degradation of the electron donor (that could by the way lead to the formation of carbonaceous residues undesirable in a catalyst of olefin polymerizations). A particular advantage is the constancy and the conservation of the ratio Mg/Ti (very important for a catalyst of olefin polymerization) through the plasma, which represents an unexpected advantage compared to usual processes (and for example compared to patent US-4650778-A in which this ratio isn't controllable). The process can be reactive or not, depending if the chemical sorts present in the plasma are able to react together or not. In this way, the liquid used for dissolving the titanium and magnesium components or for suspending them can eventually react with them. In the same way, hydrogen can be introduced in the plasma in order to reduce the titanium compound. The different parameters are adjusted, particularly the plasma temperature, the residence time of the plasma, the solution, suspension and/or liquid flows, the plasma gas and/or carrier gas flows, in the way to obtain the finest possible granulometry and/or the optimal morphology. The continuous process is preferably used. The particles obtained by the process of the invention have a very fine granulometry; they are collected by any appropriate means for the collection of fine particles, generally by means of a cyclone, by deposit on cool surfaces of a quenching system and/or by a filtration of cooled carrier gas flow. For several uses, and particularly when original material for Ziegler-Natta type catalysts are concerned, the very fine powder has to be conserved free from humidity, and it is then generally immersed in a solvent such as heptane. According to an embodiment of the invention, a second electron donor can be vaporized separately (i.e. outside of the plasma used for the catalyst preparation process) and this vapor can be brought into contact with the very fine granulometry powder during its cooling, in a way to cover this powder with electron donor. The Applicant has found that when the polymerization of alpha-olefins having from 2 to 20 carbon atoms, preferably from 2 to 8 carbon atoms, preferably ethylene, is carried out in presence of a catalyst prepared according to present invention, polyolefins in spherical particles form are obtained. This represents an advantage particularly important because it allows to transform directly the obtained polymer into final product without proceeding the intermediate stage of granulation. The invention is now illustrated with aid of the following example. Example 1 A. Preparation of the MgCl2 and TiCl4 solution A stainless steel container containing 200 cm3 of methanol is used and it is maintained under pressure of nitrogen. 18 g of commercial anhydride magnesium chloride in powder of a granulometry comprised between 0.04 and 0.25 mm is dissolved progressively. The obtained solution is cooled and 5 cm3 of titanium tetrachloride is added slowly by means of a syringe. B. Preparation of the powder A continuous flow plasma torch developing a current of 375 A under tension of 50V is used. The gas supplying the plasma is a mixture of argon and nitrogen. The inlet flows are of 15 l/min and of 17 l/min for nitrogen and for argon, respectively. The container mentioned above is relayed by means of a capillary at the output of the torch in such a way that the solution is introduced in the most hot region of the plasma. The solution flow is controlled by a micro-valve and is maintained at a value of 1600 cm3/h. The capillary oriented perpendicularly to the plasma torch, is surrounded with a tube through which nitrogen is injected, the nitrogen allows at the same time to avoid any overheating of the capillary and to guide the solution through the plasma. The MgCl2 powder covered with TiCl4 is collected on a wall; the powder granulometry obtained in this way is comprised between 0.005 and 0.2 mm. The atomic ratio Mg/Ti is 4. C. Polymerization An amount of 100 mg of catalyst obtained following the points A and B here above is pre-contacted during 5 minutes at 100°C with 2 cm3 of triethyl aluminum (TEAL) in 10% by weight solution of hexane. The conditions of polymerization are as follows: - diluent isobutane (3 litres) - temperature of polymerization 90°C - ethylene concentration 6% by weight - hexene concentration 0.4% by weight - hydrogen 15 Nl At first isobutane and 1 cm3 of TEAL (in a solution of 10% by weight in hexane) are introduced in the polymerization reactor of 6 liters. Then the pre-contacted catalyst and again 1 cm3 of TEAL solution as co-catalyst, then hydrogen and finally ethylene and hexene are introduced. The polymerization is carried out during 1 hour. The characteristics of the obtained polymer are as follows: - yield 321.5 g - productivity 3215 g/g.h - 1.3 g/10' - 38.88 g/10' - 0.9562 g/cm3 - apparent density 0.257 g/cm3

Claims: Process for the production of a magnesium chloride and titanium chloride based powder catalyst, characterized in that it consists essentially in the introduction into a plasma torch (i) of magnesium chloride (ii) of titanium chloride and (iii) at least one electron donor, the magnesium chloride being in solution or in suspension in a liquid L1, the titanium chloride being in solution or in suspension in a liquid L2 or being liquid TiCl 4 , the electron donor being L1 and/or L2 and/or another liquid compound or in solution or in suspension in a liquid, and to collect a powder after cooling. Process according to claim 1, in which less than 50 mol% of chlorides are replaced by alcoholates. Process according to any of claims 1 and 2, in which the magnesium chloride and the titanium chloride are in solution in the electron donor. Process according to any of the preceding claims, in which an electron donor chosen among ethers, preferably cyclic ethers, and alcohols is used. Process according to claim 4, in which an electron donor chosen among methanol, ethanol and tetrahydrofuran is used. Use of the process according to any of the preceding claims to produce an olefin polymerization catalyst.

Inventors: DATH JEAN-PIERRE, DEBRAS GUY, DATH, JEAN-PIERRE, DEBRAS, GUY
Applicants: FINA RESEARCH, FINA RESEARCH S.A.
Application year: 1994
Main classification: C08F4
IPC codes: C08F4, C08F10