Release agent composition

Abstract: The release agent compositions of the present invention comprise mixtures of amino-functional and amine-free polydimethylsiloxanes wherein the viscosity, amine equivalent and content of dimethylsiloxane oligomers containing up to 20 silicon atoms are within specified limits. The compositions do not evolve oily volatiles or silicon dioxide powder even during exposure to elevated temperatures.

Description: This invention relates to a release agent comprising organosilicon compounds which are based on an amino-functional diorganopolysiloxane. The various utilities of amino-functional diorganopolysiloxanes are disclosed in Japanese Patent Publication [Kokai] Sho 53-3992 [3,992/1978]; Sho 60-229719 [229,719/1985]; Hei 3-275710 [275,710/1991]; and Hei 4-230784 [230,784/1992]). The amino-functional diorganopolysiloxanes described in these publications contain large quantities, typically from 50,000 to 200,000 ppm, of dimethylpolysiloxane oligomers with up to 20 silicon atoms. During long-term use at elevated temperatures, these oligomers evaporate and stick to machinery such as exhaust fans and cause the formation of oily stains. In addition, this oil can drip on and stain moldings. Another very serious problem is that diorganopolysiloxane oligomers may undergo oxidation, producing a silicon dioxide powder, that can adversely affect surrounding electrical/electronic components. For xerographic copiers, the silicon dioxide powder produced by such oxidation sticks to the corotron, thereby preventing production of clear, crisp copies. In industrial processes using solvent-based paints, a binder resin is cured while evaporating solvent by heating and the gaseous by-products are completely combusted using a platinum catalyst. However, when an amino-containing diorganopolysiloxane is present in the solvent-based paint, the silicon dioxide powder coats the surface of the platinum catalyst honeycomb, thereby impairing the efficacy of the catalyst. As the result of extensive research directed at solving the aforementioned problems associated with prior art amino-functional diorganopolysiloxanes, the present inventors have found a solution by using mixtures of amino-functional diorganopolysiloxanes and amine-free diorganopolysiloxanes which exhibit specified limits on amine equivalent weight, viscosity, and concentration of the mixed oligomers containing up to 20 silicon atoms, represented in this specification by the expression Si ≤20 . Amino-functional diorganopolysiloxanes have heretofore generally been prepared by the equilibration polymerisation of a mixture of at least one cyclic diorganopolysiloxane oligomer and at least one cyclic amino-containing diorganopolysiloxane oligomer in the presence of alkali catalyst, followed by removal of the low boiling point materials in the reaction product by heating under reduced pressure. A disadvantage of this method is that the Si ≤20 diorganopolysiloxane oligomers present in this reaction product have high boiling points, and their removal, even by heating under high vacuum, is quite problematic. Moreover, heating at excessively high temperatures can decompose the amino group. As a result, removal of this oligomer is all but impossible, which explains why prior amino-containing diorganopolysiloxanes have contained from 50,000 to 200,000 ppm of undesirable diorganopolysiloxane oligomers. When Si ≤20 amino-containing cyclic diorganopolysiloxanes are converted into a thin film and distilled by heating under a high vacuum in our method, the content of Si ≤20 diorganopolysiloxane oligomers can be reduced to below 50,000 ppm. In the case of dimethylpolysiloxanes, after their preparation by continuous polymerization the content of Si ≤20 diorganopolysiloxane oligomer can be reduced to below 100 ppm by conversion into a thin film and distillation at elevated temperatures using high vacuum. The inventors have found that a diorganopolysiloxane blend with excellent release properties, which does not evolve oily material even when used at elevated temperatures, can be obtained by blending a dimethylpolysiloxane and an amino-functional dimethylpolysiloxane if both dimethylpolysiloxanes have been heated as thin films under reduced pressure to reduce the Si ≤20 dimethylsiloxane oligomer content, and if the amine equivalent weight and viscosity are maintained within specified limits. An objective of the present invention is to provide a release agent that evolves, neither oily volatile materials nor silicon dioxide powder, even when used at elevated temperatures. Our invention provides a release agent composition comprising a mixture of (A) an amino-functional diorganopolysiloxane having the formula wherein each R 1 is individually selected from monovalent hydrocarbon radicals with one to 20 carbon atoms, R 2 represents a hydrogen atom or a monovalent hydrocarbon radical, A is a monovalent hydrocarbon radical as defined for R 1 or an organic group with the formula -Q-(NHCH 2 CH 2 ) a NHR 2 where a is an integer with a value of zero to 10 and Q represents a divalent hydrocarbon radical selected from alkylene and alkarylene, m and n are both integers with values of at least 1 and the sum of m + n is equivalent to a viscosity at 25°C of from 50 to 30,000 mm 2 /s, wherein said diorganopolysiloxane contains no more than 50,000 ppm of diorganopolysiloxane oligomers with up to 20 silicon atoms and (B) an amine-free diorganopolysiloxane having a viscosity at 25°C of 50 to 50,000 mm 2 /s and containing no more than 500 ppm of diorganosiloxane oligomers with up to 20 silicon atoms, where said release agent exhibits an amine equivalent weight of 1,000 to 150,000, a viscosity of 50 to 30,000 mm 2 /s at 25 °C and contains not more than 5,000 ppm of diorganopolysiloxane oligomers containing up to 20 silicon atoms. In a preferred embodiment the release agent comprises an amino-functional diorganopolysiloxane wherein at least one R 1 on each silicon atom is methyl, R 2 represents hydrogen, methyl, ethyl, propyl, phenyl or cyclohexyl, Q represents an alkylene or an alkylene arylene radical, the viscosity of said aminofunctional diorganopolysiloxane is from 50 to 3,000 mm 2 /s, a is 0 or 1, and said aminofunctional diorganopolysiloxane contains no more than 10,000 ppm of said diorganopolysiloxane oligomers and wherein the viscosity of the amine-free diorganopolysiloxane is from 100 to 10,000 mm 2 /s. In the formula (A) R 1 includes methyl, ethyl, propyl, butyl, pentyl, vinyl, 3,3,3-trifluoropropyl, and phenyl. The R 1 groups in a molecule need not all be identical. R 1 is most typically methyl, however combinations of methyl with other hydrocarbon radicals is also used for R 1 . Preferably at least one of the R 1 substituents on each silicon atom is methyl. R 2 includes methyl, ethyl, propyl, phenyl, and cyclohexyl. The group represented by A is a monovalent hydrocarbon radical as defined for R 1 or an organic group with the formula -Q-(NHCH 2 CH 2 ) a NHR 2 where a is an integer with a value of zero to 10, preferably zero to 1 and Q represents alkylene such as -CH 2 -, -CH 2 CH 2 -, -CH 2 CH 2 CH 2 -, -CH 2 CH(CH 3 )CH 2 -, and -(CH 2 ) 4 -; and alkarylene such as -(CH 2 ) 2 C 6 H 4 -. Q is most preferably propylene, m and n are both integers with values of at least 1, and the sum m + n is equivalent to a viscosity at 25°C of from 50x10 -6 to 30x10 -3 m 2 /s, preferably from 1x10 -4 to 1x10 -3 m 2 /s. The broader viscosity range is considered optimal for the following reasons: the release performance is poor when the viscosity falls below 50 mm 2 /s and emulsification is highly problematic when the viscosity is above 30,000 mm 2 /s. The amino group is generally present on a non-terminal silicon atom, but it may also be present at one or both terminal silicon atoms or at both terminal and non-terminal silicon atoms. One method for preparing an amino-functional diorganopolysiloxane is described in Japanese Patent Publication Sho 53-9849 [9,849/1978]. The amino-functional diorganopolysiloxane reaction product is first neutralized with, for example, acetic acid, then stripped at 150°C - 180°C under a pressure of from 2.7 to 6.7 kPa (20 to 50 mm Hg), precision filtered using a filter aid, and subsequently stripped again at 180°C - 200°C under a pressure of from 1.3 to 4.0 kPa (10 - 30 mm Hg) in order to remove the Si ≤20 diorganopolysiloxane oligomers to the greatest extent possible. The product is then converted into a thin film and the Si ≤20 diorganopolysiloxane oligomers containing up to 20 silicon atoms are removed by evaporation. The concentration in ingredient A of diorganopolysiloxane oligomers containing up to 20 silicon atoms should be no greater than 50,000 ppm, preferably no greater than 20,000 ppm, and most preferably no greater than 10,000 ppm. The dorganopolysiloxane used as ingredient B in the present compositions must contain no more that 500 ppm of diorganopolysiloxane oligomers containing up to 20 silicon atoms. The diorganopolysiloxane oligomers that should be excluded from the present compositions include both straight-chain dimethylpolysiloxane oligomers with the general formula R 3 [(CH 3 ) 2 SiO] m Si(CH 3 ) 2 R 3 where R 3 represents a hydroxyl radical or a methyl radical, m is an integer with a value of zero to 19, and cyclic dimethylpolysiloxane oligomers containing from 3 to 20 dimethylpolysiloxane units per molecule. When ingredient B contains more than 500 ppm of Si ≤20 diorganopolysiloxane oligomers, these oligomers will evaporate from the diorganopolysiloxane during application of the release agent at elevated temperature to cause the problems discussed earlier in this specification. The linear diorganopolysiloxane oligomer containing 20 silicon atoms has a boiling point of 830°C and is volatile. The content of Si ≤20 diorganopolysiloxane oligomers in ingredient B is preferably ≤ 400 ppm, most preferably ≤ 100 ppm. The diorganopolysiloxane used as ingredient B has a viscosity at 25°C of 5x10 -5 to 5x10 -2 m 2 /s. When the viscosity is below 50 mm 2 /s at 25°C, this ingredient will be volatile and the release performance will therefore be unsatisfactory; when the viscosity exceeds 50,000 mm 2 /s, the release agent becomes difficult to handle due to its excessively high viscosity. Viscosities of 1x10 -4 to 1x10 -2 m 2 /s are preferred. Ingredient B preferably has a straight-chain or partially branched chain structure and contains hydroxyl or methyl radicals at its molecular chain terminals. Ingredient B can be prepared by polymerization of a cyclic dimethylpolysiloxane oligomer. The reaction product is then stripped to yield a dimethylpolysiloxane containing from 5,000 to 30,000 ppm Si ≤20 dimethylpolysiloxane oligomer. The dimethylpolysiloxane oligomer fraction is subsequently removed using a thin-film evaporator operating at a temperature of, for example from 270°C to 350°C and a pressure of 13.3 Pa to 2.0 kPa (0.1 to 15 mm Hg). Alternatively, the dimethylpolysiloxane oligomer can be removed by extraction with various organic solvents such as an alcohols, including methanol, ethanol, n-butanol and isopropanol; ketones such as acetone and methyl ethyl ketone; hydrocarbons such as hexane, benzene, toluene, and xylene; or with mixtures containing two or more of these organic solvents. Alternative purification methods can also be used in combination. Removal of the dimethylpolysiloxane oligomer by organic solvent extraction is a preferred method, while removal of the dimethylpolysiloxane oligomer using both a thin-film evaporator and organic solvent extraction is a particularly preferred method. The release agent compositions of the present invention comprise mixtures of ingredients A and B. The mixtures have an average amine equivalent weight of 1,000 to 150,000, a Si ≤20 dimethylpolysiloxane oligomer content not exceeding 5,000 ppm, and a viscosity of 50 to 30,000 5x100 -4 to 3x10 -2 m 2 /s at 25°C. The "amine equivalent weight" is defined as the weight of release agent composition containing one mole of amine group. For example, a release agent composition in accordance with the present invention containing an average amine equivalent weight of 38,000, a concentration of oligomers containing no more that 20 silicon atoms of 2,400 ppm, and a viscosity of 138 mm 2 /s at 25°C can be prepared by blending 80 weight parts of ingredient B containing 0 ppm of oligomers containing no more that 20 silicon atoms and a viscosity of 138 mm 2 /s with 20 weight parts of an amino-functional diorganopolysiloxane having a viscosity of 138 mm 2 /s at 25°C, an amino equivalent weight of 7,600, the average formula and containing 12,000 ppm of dimethylsiloxane oligomer containing not more than 20 silicon atoms. In addition to a mixture of ingredients A and B the present release agent compositions can also contain inorganic powders such as mica, talc, zinc oxide, and calcium carbonate; organic compounds such as paraffins and waxes; and organic solvents such as toluene, xylene, hexane, heptane, and rubber volatile oil. The compositions of this invention can be emulsified and used in this form. Thus, the present compositions can be emulsified by conventional methods by blending the composition with water and at least one surfactant. Useful surfactants include non-ionic surfactants such as polyoxyalkylene alkyl ethers, polyoxyalkylene alkylphenol ethers, polyoxyalkylene alkyl esters, sorbitan alkyl esters, and polyoxyalkylene sorbitan alkyl esters, and cationic surfactants such as aliphatic amine salts, quaternary ammonium salts, and alkylpyridinium salts. The release agent compositions of the present invention are useful as release-improving additives for thermosetting resins such as phenolic resins, epoxy resins, polyester resins, phenol novolac resins, urea resins, and melamine resins; thermoplastic resins such as polyvinyl chloride, polyethylene, polypropylene, vinyl acetate and its copolymers, nylon, polyesters, polystyrenes, acrylonitrile/styrene copolymers, acrylonitrile/butadiene/styrene copolymers, poly(meth)acrylates , polycarbonates, polyurethanes, and polyacetals; and organic rubbers such as natural rubber, isoprene, styrene/butadiene rubber, and chloroprene polymers. The present compositions are also useful as a release agents for the spinnerets used to produce synthetic fibers; as a release agent for the toner in xerographic copiers; as an internal addition-type release agent for plastics, organic rubbers, and silicone rubbers; as a release agent for die-casting and cast-metal molding; as a release agent for the molding of articles including rubber mats, hoses, and tires; and as a release agent for the molding of plastics. EXAMPLES The following examples describe preferred embodiments of the present invention. Unless otherwise specified, all parts and percentages are by weight and viscosities were measured at 25° C. The concentrations of diorganopolysiloxane oligomers were determined by gas-liquid chromatography. Reference Example 1 This example describes the preparation of the two amino-functional diorganopolysiloxanes used as ingredient A. Compound 1 Compound 1 was an amino-functional diorganopolysiloxane with an amine equivalent weight of 15,200, a viscosity of 138 mm 2 /s and the average formula Compound 1 contained 9,750 ppm of dimethylpolysiloxane oligomers containing no more than 20 silicon atoms. An amino-containing diorganopolysiloxane synthesized by a conventional method and containing 145,800 ppm of dimethylpolysiloxane oligomers containing up to 20 silicon atoms was passed twice through a bench-top thin-film distillation unit manufactured by Shinko Pfaudler Kabushiki Kaisha using a temperature of 200°C and a pressure of 266-399 Pa (2 - 3 mm Hg) to reduce its dimethylpolysiloxane oligomer content to 9,750 ppm (Sample a). Compound 2 Compound 2 was an amino-functional diorganopolysiloxane exhibiting an amine equivalent weight of 7,330, a viscosity of 2,820 mm 2 /s and the average formula Compound 2 was prepared by passing an amino-functional diorganopolysiloxane synthesized by a conventional method twice through the same unit described for the purification of Sample a using a temperature of 220°C and a pressure of from 266-399 Pa (2 to 3 mm Hg) to reduce its dimethylpolysiloxane oligomer content (≤ 20 silicon atoms) to 7,770 ppm from the initial value of 133,000 (Sample b). Reference Example 2 This example describes the preparation of the two diorganolpolysiloxanes used as ingredient B. Compound 3 Compound 3 was a dimethylpolysiloxane oil that contained 7 ppm Si ≤20 dimethylpolysiloxane oligomer and had a viscosity of 108 mm 2 /s. This compound was prepared by synthesizing a dimethylpolysiloxane oil synthesized by a conventional method. The dimethylpolysiloxane oil contained 28,700 ppm of oligomers containing up to 20 silicon atoms, exhibited a viscosity of 100 mm 2 /s and was passed twice through a thin-film evaporator with a column length of 4.5 m using a temperature of 270°C and a pressure of 399-532 Pa (3 - 4 mm Hg) in order to reduce its Si ≤20 dimethylpolysiloxane oligomer content to 3,500 ppm. This content was further reduced to 7 ppm by repeating the following alcohol extraction 7 times: shaking for 2 hours with 3 times the sample weight of ethanol, then allowing the mixture stand for 2 hours (Sample c). Compound 4 Compound 4 was a dimethylpolysiloxane oil that contained 0 ppm Si ≤20 dimethylpolysiloxane oligomer and had a viscosity of 10,002 mm 2 /s. This compound was prepared by synthesizing a dimethylpolysiloxane oil by a conventional method. The Si ≤20 dimethylpolysiloxane oligomer content was 3,350 ppm, and viscosity was 10,000 mm 2 /s. The initial dimethylpolysiloxane oil was treated as described for Sample c to reduce its Si ≤20 dimethylpolysiloxane oligomer content to 0 ppm (Sample d). Example 1 Compounds 1 and 3 prepared as described in the reference examples were blended in the amounts reported in Table 1 to prepare a release agent in the form of a diorganopolysiloxane composition. This release agent was comprehensively evaluated for its suitability as a release agent by examining its release performance, the molding surface condition, and oligomer evaporation as described in the following paragraphs. Release performance The release agent was applied to a steel mold with a mirror finish and designed for the molding of a 25 x 25 x 0.5 cm rubber article. This was followed by heating the mold for 15 hours at 200°C. After cooling, the mold was immersed in a bath of toluene solvent and cleaned by gentle shaking. Unvulcanized styrene/butadiene rubber was filled into the mold and vulcanized for 15 minutes at 150°C under a pressure of 1,9 MPa (20 kgf/cm 2 ). The releasability of the molding (release performance) was then evaluated. Molding surface condition The surface of the molding was visually inspected for irregularities in order to determine whether or not a mirror-smooth molding had been obtained. Evaporation of dimethylsiloxane oligomer 25 cm 3 of the release agent was placed in a 100 cm 3 beaker, which was covered with a 200 cm 3 beaker and heated for 5 hours at 200°C. The interior surfaces of the beakers were then examined for dimethylpolysiloxane oligomer that had evaporated out during heating. The results are reported in Table 1. The compositions corresponding to the present invention gave an excellent release performance. Moreover, the surface of the molding conformed to the mold and lacked irregularities and had a mirror finish. Finally, no evaporation of dimethylpolysiloxane oligomer was observed. Thus, the invention sample gave an excellent performance as a release agent. By comparison, evaporation of dimethylpolysiloxane oligomer was observed for compound 1 by itself (Comparison Example 1), which was therefore unqualified for application as a release agent. In the case of compound 3 by itself (Comparison Example 2), no release was obtained because the release agent had been almost completely washed off by the solvent (toluene). The mixture of 5 parts compound 1 and 95 parts compound 3 (Comparison Example 3) contained too little amino group. As a result, only a small amount was adsorbed or adhered to the mold, and the release performance was therefore unsatisfactory. Present Invention Comparison Examples Example 1 Comparison Example 1 Comparison Example 2 Comparison Example 3 sample mixture of 85 parts parts Compound 3 with 15 parts Compound 1 Compound 1 Compound 3 mixture of 95 parts Compound 3 with 5 parts Compound 1 amine equivalent weight 101,300 15,200 - 304,000 oligomer (ppm) 1,470 9,750 7 495 viscosity mm 2 /s 112 138 108 109 release performance excellent excellent no release partial sticking by the surface, unsatisfactory release molding surface condition excellent, surface had mirror finish excellent, surface had mirror finish - partial cohesive rupture dimethylpolysiloxane oligomer evaporation no evaporated oligomer observed small amount of oil droplets adhered on interior beaker surfaces no evaporated oligomer observed no evaporated oligomer observed overall evaluation as a release agent highly qualified unqualified unqualified unqualified Example 2 Compounds 2 and 4, which were prepared as reported, respectively, in Reference Examples 1 and 2, were mixed as reported in Table 2 to prepare a release agent, and the properties of this release agent were evaluated as described in Example 1. As reported in Table 2, the release agent of the invention, a mixture of 20 parts of compound 2 and 80 parts compound 4, was rated as an excellent release agent because it gave an excellent release performance, was free of dimethylpolysiloxane oligomer evaporation, and yielded a molding whose surface intimately conformed to the mold. In contrast to this, compound 2 (Comparison Example 4), compound 4 (Comparison Example 5), and the mixture of 2.5 parts compound 2 and 97.5 parts compound 4 (Comparison Example 6) were in each case rated as unqualified for application as a release agent. Present Invention Comparison Examples Example 2 Comparison Example 4 Comparison Example 5 Comparison Example 6 sample mixture of 80 parts Sample d with 20 parts Sample b Sample b Sample d mixture of 97.5 parts Sample d with 2.5 parts Sample b amino equivalent weight 36,650 7,330 - 293,000 oligomer (ppm) 1,550 7,770 0 202 viscosity mm 2 /s 7,760 2,820 10,002 9,690 release performance excellent excellent no release partial sticking by the surface, unsatisfactory release molding surface condition excellent, surface had mirror finish excellent, surface had mirror finish - partial cohesive rupture dimethylpolysiloxane oligomer evaporation no evaporated oligomer observed small amount of oil droplets adheres on interior beaker surfaces no evaporated oligomer observed no evaporated oligomer observed overall evaluation as release agent highly qualified unqualified unqualified unqualified Example 3 To 30 parts of the release agent described in Example 1, (mixture of 15 parts of compound 1 and 85 parts compound 3) were added 1.3 parts polyoxyethylene (8.5 mol adduct) nonylphenol ether emulsifying agent, 3.5 parts polyoxyethylene (6 mol adduct) lauryl ether emulsifying agent, and 65.2 parts water. This was followed by emulsification in a colloid mill emulsifier to prepare an emulsion. This emulsion was diluted 30-fold with water to yield a release agent for application to the molding of passenger snow tires with complex tread. Compound 1 from Example 1 was also formulated into an emulsion using the same procedure to give a release agent. There was no difference between the two emulsions in terms of initial release performance. However, during continuous operations using the emulsion prepared using compound 1, a small quantity of tar and Si ≤20 dimethylpolysiloxane oligomer were detected on the upper mold of the vulcanizer. During continuous operations beyond this point, splotchy stains caused by dimethylpolysiloxane oligomer were produced on the tire surfaces. Tires molded using the emulsified release agent of the present invention were completely free of stains caused by dimethylpolysiloxane oligomer. Example 4 The following ingredients were mixed to homogeneity over 10 minutes in a Henschel mixer: 40 parts of the release agent of the present invention described in Example 2, 2,000 parts polyethylene terephthalate chips, and 0.5 parts organic pigment (Sumiplast Blue-OR™ from Sumitomo Kagaku Kabushiki Kaisha). Using the resultant composition as a release agent, 500 injection molding operations were carried out using a small-scale injection molder at 270°C. This molding experiment was conducted using a mold for the fabrication of an Izod impact test specimen and was run without the use of external release agent. The results of the evaluation demonstrated that injection molding could be carried out using the release agent of the present invention in an entirely problem-free manner even in the absence of an external release agent. Moreover, the perimeter around the injection section was free of dimethylpolysiloxane oligomer staining. For comparison, compound 2 described in Comparison Example 4 was tested in the same experiment. The release performance was entirely problem-free just as for the addition of the release agent in accordance with the invention, and the release performance was almost on the same level. However, dimethylpolysiloxane oligomer was detected in the volatiles (tar) evolved from around the injection material.

Claims: A release agent comprising a mixture of (A) an amino-functional diorganopolysiloxane having the formula wherein each R 1 is individually selected from monovalent hydrocarbon radicals with one to 20 carbon atoms, R 2 represents a hydrogen atom or a monovalent hydrocarbon radical, A is a monovalent hydrocarbon radical as defined for R 1 or an organic group with the formula -Q-(NHCH 2 CH 2 ) a NHR 2 where a is an integer with a value of zero to 10 and Q represents a divalent hydrocarbon radical selected from alkylene and alkarylene, m and n are both integers with values of at least 1 and the sum of m + n is equivalent to a viscosity at 25°C of from 50 to 30,000 mm 2 /s, wherein said diorganopolysiloxane contains no more than 50,000 ppm of diorganopolysiloxane oligomers with up to 20 silicon atoms and (B) an amine-free diorganopolysiloxane having a viscosity at 25°C of 50 to 50,000 mm 2 /s and containing no more than 500 ppm of diorganosiloxane oligomers with up to 20 silicon atoms, where said release agent exhibits an amine equivalent weight of 1,000 to 150,000, a viscosity of 50 to 30,000 mm 2 /s at 25 °C and contains not more than 5,000 ppm of diorganopolysiloxane oligomers containing up to 20 silicon atoms. A release agent according to Claim 1 in which the amino-functional diorganopolysiloxane contains less than 20,000 ppm of diorganopolysiloxane oligomers and is represented by the general formula (A) wherein R 1 R 2 , Q and A are as defined in claim 1, a is an integer with a value of zero to 10, m and n are both integers with values of at least 1, m + n is a number that gives a viscosity at 25°C of 50 to 30,000 mm 2 /s, and the viscosity of said diorganopolysiloxane (B) is from 50 to 50,000 mm 2 /s. A release agent according to claim 2 where in (A) at least one R 1 on each silicon atom is methyl, R 2 represents hydrogen, methyl, ethyl, propyl, phenyl or cyclohexyl, Q represents an alkylene or an alkylenearylene radical, the viscosity of said amino-functional diorganopolysiloxane is from 50 to 3000 mm 2 /s, a is 0 or 1, said amino-functional diorganopolysiloxane contains no more than 10,000 ppm of said diorganopolysiloxane oligomers, and the viscosity of said diorganopolysiloxane (B) is from 100 to 10,000 mm 2 /s. A release agent according to claim 3 where Q is propylene, the viscosity of said amino-functional diorganopolysiloxane (A) is from 100 to 1000 mm 2 /s and A is methyl.

Inventors: ISHIKAWA HIROKI, NAGANAWA TSUTOMU, ONA ISAO, ISHIKAWA, HIROKI, NAGANAWA, TSUTOMU, ONA, ISAO, ISHIKAWA, HIROKI, DOW CORNING TORAY SILICONE, NAGANAWA, TSUTOMU , DOW CORNING TORAY SILICONE, ONA, ISAO, DOW CORNING TORAY SILICONE
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: B29C33
IPC codes: C08L83, C08K5, B29C33