Oil-in-water type emulsion composition

Abstract: An oil-in-water type emulsion composition comprising: an amphiphile and a surfactant selected from the substances which can form a gel in an amphiphatic substance-surfactant-water system at a temperature of not lower than ordinary temperatures; oil and water, wherein substantially the total amount of amphiphile and surfactant exist on the boundary surfaces of emulsion particles. The emulsion composition has both the physical properties close to those of an aqueous solution and a creamy feel at the time of use.

Description: The present invention relates to an oil-in-water type emulsion composition and, more particularly, to an improvement of the physical properties of an oil-in-water type emulsion composition. [BACKGROUND OF THE INVENTION] Various emulsion compositions are generally used in the field of cosmetics and the like. Most of these emulsion compositions are creamy or milky, and emulsion compositions with the emulsion particle diameter reduced in order to improve the external appearance have been developed (e.g., Japanese Patent Laid-Open Nos. Sho 63-126542 (1988) and Hei 1-288330 (1989)). These emulsion compositions attract attention as a compound having an oily component stably mixed with the system without using a large amount of surfactant, ethanol, or the like. Although these conventional emulsion compositions are excellent in the stability and the transparency, various studies are further undertaken so as to provide more excellent feel, etc. at the time of use. More specifically, it is favorable that an emulsion composition for a cosmetic has physical properties close to those of an aqueous solution in the container because it provides an excellent transparent external appearance and the low viscosity improves the convenience at the time of packing or taking it out of the container. On the other hand, when the emulsion composition is applied to the skin, it preferably has a soft feel like cream. However, no emulsion composition having such antipodal physical properties has been produced in the related art. [SUMMARY OF THE INVENTION] Accordingly, it is an object of the present invention to eliminate the above-described problems in the related art and to provide an oil-in-water type emulsion composition having not only the physical properties close to those of an aqueous solution but also a creamy feel at the time of use. As a result of studies undertaken by the present inventors so as to achieve this aim, it has been found that an oil-in-water type emulsion composition having substantially the total amount of amphiphile and surfactant which can form a gel in a water phase on each boundary surface between an oil phase as the inner phase and a water phase as the outer phase has not only physical properties close to those of an aqueous solution but also a creamy feel at the time of use. On the basis of this finding, the present invention has been achieved. In general oil-in-water type emulsion compositions, it is considered that an amphiphile and a surfactant form gels in a water phase and solidify the base material (Barry, B.W., J. Colloid Interface Sci., 28, 82-91 (1968), etc.). A creamy feel of such an emulsion composition at the time of use is derived from the fluidity of the gels formed in a water phase by the amphiphile and the surfactant. The formation of a gel in a oil-in-water type emulsion composition is described as follows in p.112 to 116 of "Chemicophysics of Cetyl Alcohol " by Shoji Fukushima, published by Fragrance Journal (1992). In Fig. 1, oil phases 12 are dispersed in a water phase 10, and a surfactant 14 and an amphiphile 16 exist on each boundary surface between the water phase 10 and the oil phase 12 so as to stabilize the dispersion of the oil phases 12 in the water phase 10. The surfactant 14 and the amphiphile 16 also exist in the water phase 10 and a part thereof forms lamella structures 18. The gel structures thus produced not only solidify the base material but also provide an excellent creamy feel at the time of use. If the gel structures which solidify the base material in such an oil-in-water type emulsion composition are broken by an emulsifier having a strong shear force so that the lamella structure 18 is separated into fine dispersion systems (vesicles) 20, for example, as shown in Fig. 2, it is possible to obtain a liquid base material having a low viscosity (Michihiro Yamaguchi, Akira Noda, "Japan Chemis try" 26-32 (1989)). However, the system produced by finely dispersing the lamella structures suffers from a problem such as the generation of blobs due to agglomeration and the unstableness of the system such as an increase in the viscosity due to the reconstruction of the gel structure. The present inventors have succeeded in producing a liquid cream having a low viscosity and assuring the stability of the liquid cream as an article of commerce by finely dividing the emulsion particles of an oil-in-water type emulsion composition which is composed of the amphiphiles 16, the surfactants 14, the water 10 and the oil 12, transferring the amphiphile 16 and the surfactant 14 which form gels in the water phase 10 to the boundary surface of each emulsion particle so as to reduce the amount of gel in the water phase, and selecting a combination of the amphiphile 16 and the surfactant 14 which constitutes a stable gel and which is difficult to reconstruct a gel structure after the stable gel structure is broken. When approximately the total amount of amphiphile 16 and surfactant 14 are transferred to the boundary surfaces of the oil drops 12, as shown in Fig. 3, the amphiphile 16 and the surfactant 14 are stably held on the boundary surfaces of the emulsion particles, and since finely dispersed lamella structures or the like do not exist in the water phase 10, there is no generation of blobs due to agglomeration nor the reconstructed of the gel structure. Therefore, the oil-in-water type emulsion composition of the present invention has a very low viscosity in the preserved state, so that it has an excellent producibility and is easy to take out of a container. On the other hand, when the emulsion composition shown in Fig. 3 is applied to the skin, for example, the emulsion particles are mechanically broken by the spreading operation, so that the area of the boundary surface of each emulsion particle is greatly reduced. As a result, the amphiphile 16 and the surfactant 14 are discharged into the water phase 10, and gel structures are reconstructed by the amphiphile 16, the surfactant 14 and the water 10, thereby providing a creamy feel to the skin. In this way, the present inventors have developed an oil-in-water type emulsion composition the emulsion of which is broken in the process of application and which provides a novel creamy feel when it is applied to the skin. In the present invention, there is provided an oil-in-water type emulsion composition as defined in claim 1. The structure of the present invention will be explained in more detail in the following. It is necessary that the amphiphile and the surfactant which are transferred to the boundary surface between the water phase and the oil phase and which are characteristic of the present invention specifically form a gel in an amphiphile-surfactant-water system. From the point of view of emulsion stability, the gel is preferably of the α-type, and it is more preferable that the transition temperature of the gel is not lower than 60°C. If a gel has a single peak of 21.4° by X-ray analysis, the gel is judged to be the α-type. Examples of a preferable combination of an amphiphile and a surfactant which form a gel in a water system at a temperature of not lower than ordinary temperatures are behenic acid and/or behenyl alcohol (amphiphile)-pottassium behenate (surfactant), stearic acid and/or stearyl alcohol (amphiphile)-pottassium stearate (surfactant), stearyl alcohol (amphiphile)-sodium cetyl sulfate (surfactant), behenyl alcohol (amphiphile)-behenyltrimethyl ammonium chloride (surfactant) and behenyl alcohol (amphiphile)-stearyltrimethyl ammonium chloride (surfactant). It is possible to further enhance the emulsion stability by using a combination of an amphiphile and a surfactant which have long and different carbon chain lengths. Although the amphiphile has surface activity, the amphiphile itself has a strong hydrophobic property and the surface activity thereof is not so strong as a general surfactant. Examples of an amphiphile are higher fatty acids, higher aliphatic alcohols, monoglycerides, glycerol monoalkyl ethers, monoalkylamines, and compounds (cholesterol, phytosterol, etc.) having a sterol skeleton. The amount of oil phase is not less than 1/2 of, preferably, equal to the total amount of amphiphile and surfactant. When the amount of oil phase is less than 1/2 of the total amount of amphiphile and surfactant, the emulsion stability with time is apt to be lowered. The average emulsion particle diameter is not more than 0.15 µ m, preferably not more than 0.10 µm. If the average emulsion particle diameter exceeds 0.15 µm, there is a fear of producing creaming when the emulsion has a low viscosity. The average particle diameter of the emulsion used in the present invention is measured by a dynamic light scattering method using NICOMF-270 (produced by HIAC/ROYCO). It is considered that the water phase is gelated when an oil-in-water type emulsion composition of the present invention is spread over the skin. For this reason, if the total amount of amphiphile and surfactant is less than 0.2% of the amount of water phase, the gelation is not caused, so that a creamy feel at the time of use may not be obtained. As the amount of amphiphile surfactant for forming a gel in a water phase, 0.2% is generally small. However, since part of the water content evaporates and disperses when the oil-in-water type emulsion composition is spread over the skin, about 0.2% of amphiphile and surfactant based on the amount of water phase can produce a creamy feel at the time of use. More preferably, the amount of amphiphile and surfactant is not less than 0.5% of the amount of water phase. In the present invention, the oily component mixed in the system may be any of liquid oils, solid oils, semisolid oils and slightly water-soluble substances. For example, the oily component is selected from liquid oils such as avocado oil, tsubaki oil, turtle oil, macadamia nut oil, corn oil, mink oil, olive oil, rape seed oil, yolk oil, sesame oil, persic oil, wheat germ oil, sazanque oil, castor oil, linseed oil, safflower oil, cottonseed oil, evening primrose oil, perilla oil, soybean oil, peanut oil, teaseed oil, kaya oil, rice bran oil, Chinese paulownia oil, Japanese paulownia oil, jojoba oil, germ oil, triglycerin, glycerin trioctanoate and glycerin triisopalmitate; solid oils such as cocoa butter, coconut oil, horseflesh tallow, hydrogenated coconut oil, palm oil, beef tallow, mutton tallow, hydrogenated beef tallow, palm kernel oil, pork tallow, beef bone tallow, Japan wax and hydrogenated castor oil; waxes such as bees wax, candelilla wax, cotton wax, carnauba wax, bayberry wax, Chinese wax, spermaceti wax, montan wax, rice bran wax, lanolin, kapok oil, lanolin acetate, liquid lanolin, sugarcane wax, lanolin fatty acid isopropyl, hexyl laurate, reduced lanolin, jojoba wax, hydrogenated lanolin, shellac wax, POE lanolin alcohol ether, POE lanolin alcoholacetate, lanolin fatty acid polyethylene glycol and POE hydrogenated lanolin alcohol ether; hydrocarbons such as liquid paraffin, ozocerite, squalene, pristane, paraffin, ceresin, squalane, vaseline and microcrystalline wax; synthetic esters such as isopropyl myristate, cetyl octoate, octyldodecyl myristate, isopropyl palmitate, butyl stearate, hexyl laurate, myristyl myristate, decyl oleate, hexyldecyl dimethyloctoate, cetyl lactate, myristyl lactate, lanolin acetate, isocetyl stearate, isocetyl isostearate, cholesteryl 12-hydroxystearate, ethylene glycol di-2-ethylhexylate, dipentaerythritol fatty acid ester, N-alkl glycol monoisostearate, neopentyl glycol dicaprate, diisostearyl malate, glycerin di-2-heptylundecandate, trimethylolpropane tri-2-ethylhexylate, trimethylolpropane triisostearate, pentaerythritol tetra-2-ethylhexylate, glycerin tri-2-ethylhexylate, cetyl-2-ethylhexandate, 2-ethylhexyl palmitate, glycerin trimyristearate, glyceride tri-2-undecandate, castor oil fatty acid methyl ester, oil oleate, cetostearyl alcohol, acetoglyceride, 2-heptylundecyl palmitate, diisopropyl adipate, N-lauroyl-L-glutamic acid-2-octyldodecyl ester, di-2-heptylundecyl adipate, ethyl laurate, di-2-ethylhexyl cebacate, 2-hexyldecyl myristate, 2-hexyldecyl palmitate, 2-hexyldecyl adipate, diisopropyl cebacate, 2-ethylhexyl succinate, ethyl acetate, butylacetate, amyl acetate and triethyl citrate; higher fatty acids such as lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, 12-hydroxystearic acid, undecylenic acid, Tall acid, lanolin fatty acid, isostearic acid, linoleic acid, linolenic acid and eicosapentaenoic acid; straight-chain or branched higher alcohols such as laurin alcohol, cetyl alcohol, stearyl alcohol, behenyl alcohol, myricyl alcohol, cetostearyl alcohol, monostearyl glycerin ether (batyl alcohol), 2-decyltetradecynol, lanolin alcohol, cholesterol, hexyldodecanol, isostearyl alcohol and octyldodecanol; chained polysiloxanes such as dimethyl polysiloxane, methylphenyl polysiloxane, methylhydrogen polysiloxane; Cyclic polysiloxanes such as octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, tetramethyltetrahydrogencyclotetrasiloxane; amino denatrued silicone oil, epoxy denatured silicone oil, epoxy polyether denatured silicone oil, polyether denatured silicone oil, carboxy denatured silicone oil, alcohol denatured silicone oil, alkyl denatured silicone oil, ammonium salt denatured silicone oil, silicone resin which has a network structure or can form the network structure such as trimethylsiloxy cinnamate; silicone rubber such as highly polymerized dimethyl polysiloxane, highly polymerized methylphenylsiloxane, highly polymerized methyl vinil polysiloxane; perfluorocarbon such as perfluoro decarine, perfluorohexane, triperfluoro-n-butylamine; perfluoropolyether; vitamins such as vitamin A and derivatives thereof; vitamin D and derivatives thereof, vitamin E and derivatives thereof, vitamin K and derivatives thereof; sterols; and natural and synthetic perfumes. In these oily components, those having a melting point of lower than ordinary temperatures are treated as liquid oils, and those having a melting point of not lower than ordinary temperatures are treated as solid or semisolid oils. Examples of a slightly water-soluble sobstances as the oily component are vitamins such as ubiquinone and vitamin P; bactericides such as chlorhexdin hydrochloride, trichlorocarbanilide and Imegassan DP 300; medicines such as dexamethazone acetate; ultraviolet absorbers such as paraaminobenzoic acid (hereinunder referred to as "PABA") and N,N-dimethyl PABA octyl ester; and preservatives such as parahydroxybenzoate. A mixed dispersion of the above-descrihed essential materials is treated with a strong shear force by an emulsifier having a stronger shear force than a homomixer, thereby improving the transparency, the safety and the stability. As examples of such an emulsifier will be cited Mantongaulin, French press, colloid mill, microfluidizer and ultrasonic emulsifier. In the case of using a high-pressure homogenizer such as Mantongaulin, French press and microfluidizer, emulsification is conducted under a pressure of not less than 6895 kPa (1000 psi), more preferably not less than 20685 kPa (3000 psi). In the present invention, the total amount of mixed dispersion may be emulsified. It is also possible to emulsify part of the mixed dispersion and dilute the emulsion with water or another component such as a polyvalent alcohol, as occasion demands. Emulsification is preferably conducted at a temperature of not lower than the transition temperature of the gel which is formed by the surfactant and the amphiphile together with water in the system. The emulsion composition of the present invention may contain other components. For example, ethylene glycol, propylene glycol, 1,3-butylene glycol, dipropylene glycol, glycerol, polygrycerin such as digrycerin, trigrycerin and tetragrycerin, glucose, maltose, maltitol, sucrose, fructose, xylitol, inositol, pentaerythritol, sorbitol, maltotriose, amylolysis sugar and amylolysis sugar reduced alcohol are usable as a water-phase component. The water phase here is exemplified by an aqueous solution of at least one selected from the group consisting of: water-soluble active substances such as vitamins, e.g., vitamin B, vitamin C and derivatives thereof, pantothenic acid and derivatives thereof and biotin; buffers such as sodium glutamate, alginine, aspartic acid, citric acid, tartaric acid and lactic acid; chelates such as EDTA; ultraviolet absorbers; and various pigments. The above and other objects, features and advantages of the present invention will become clear from the following description of the preferred embodiments thereof, taken in conjunction with the accompanying drawings. [BRIEF DESCRIPTION OF THE DRAWING] Fig. 1 is a schematic view of a general oil-in-water type emulsion composition in the emulsified state; Fig. 2 is an explanatory view of the factor of the deterioration of the emulsion stability of a general oil-in-water type emulsion composition; Fig. 3 is an explanatory view of an oil-in-water type emulsion composition according to the present invention in the emulsified state; Fig. 4 is an explanatory view of the DSC temperature rise curve of an oil-in-water type emulsion composition according to the present invention. [DESCRIPTION OF THE PREFERRED EMBODIMENTS] The present invention will be explained hereinunder in more detail with reference to preferred embdiments of the present invention. It is to be understood, however, that the present invention is not restricted thereto. Amount of amphiphile and surfactant existent on the surfaces of the emulsion particles As described above, the amount of surfactant and amphiphile existent on the surfaces of the emulsion particles and the amount thereof remaining in the water phase exert a great influence on the physical properties of the emulsion composition during preservation and the creamy feel thereof at the time of application to the skin. Therefore, the present inventors first produced oil-in-water type emulsion compositions in Comparative Examples 1, 2 and 3, and Example 1, and the physical properties of the products, the change thereof with time and the feel of the products when they were applied to the skin were examined. The amount of surfactant and amphiphile existent on the surfaces of the emulsion particles can be estimated from a change in the area of the peak of the gel transition. The transition temperature was measured by a differential scanning calorimeter (DSC). DSC 120 (produced by Seiko Instruments Ltd.), and the temperature at the peak of heat absorption observed from the DSC temperature rise curve was regarded as the transition temperature. Comp.1 Comp.2 Comp.3 Ex. 1 1) Behenyl alcohol (%) 1.0 1.0 1.0 1.0 2) Stearyl alcohol (%) 0.5 0.5 0.5 0.5 3) Behenic acid (%) 0.5 0.5 0.5 0.5 4) Stearic acid (%) 0.5 0.5 0.5 0.5 5) Liquid paraffin (%) - 5.0 5.0 5.0 6) KOH (%) 0.15 0.15 0.15 0.15 7) 1,3-butylene glycol (%) 10.0 10.0 10.0 10.0 8) Ion-exchanged water (%) 15.0 15.0 15.0 15.0 9) Ion-exchanged water (%) Balance Balance Balance Balance (Process) Comparative Example 1: The components (1) to (4) were mixed and stirred at 80°C. The mixture of the components (6) to (9) was heated and dissolved at 70°C. The mixture of the components (1) to (4) was mixed under stirring with the mixture of the components (6) to (9), and emulsified at 80°C by a homomixer. Comparative Examples 2 and 3, and Example 1: The components (1) to (5) were mixed and stirred at 80°C. The mixture of the components (6) to (9) was heated and disolved at 70°C. The mixture of the components (1) to (4) was mixed under stirring with the mixture of the components (6) to (9). In Comparative Example 2, after the resultant mixture was emulsified at 80°C by a homomixer, the component (9) was mixed with the emulsion under stirring. In Comparative Example 3, after the resultant mixture was emulsified at 80°C under a pressure of 3448 kPa (500 psi) by a high-pressure homogenizer, the component (9) was mixed with the emulsion under stirring. In Example 1, after the resultant mixture was emulsified at 80°C under a pressure of 4827 kPa (700 psi) by a high-pressure homogenizer, the component (9) was mixed with the emulsion under stirring. In this manner, samples having different average emulsion particle diameters were obtained. Fig. 4 shows a change in the DSC curve obtained in heating scan with a change in average emulsion particle diameter. In Fig. 4, the curve (1) represents transition curve of the sample in Comparative Example 1 in which the system did not contain any oily component. On the curve (1), a single transition peak was observed at 75°C. Since no emulsion is formed in the system which does not contain an oily component, the amphiphile and the surfactant formed a gel in the water phase, and the curve (1) represents this state. In Comparative Examples 2 and 3 and Example 1, the system contained the oily component, and the average emulsion particle diameters were 1 to 10 µm, 0.24 µm and 0.07 µm, respectively. With the reduction in the average emulsion particle diameter, the peaks on the high-temperature side reduces on the DSC curve, and in Example 1, only one peak was observed at the lowest temperature in all the peaks. This suggests that the amphiphile and the surfactant which constitute the gel in the water phase transfer to the interfaces in the emulsion with the expanding in the area of the boundary surface of each emulsion particle in the process of reducing the particle size diameters and that the amount of amphiphile and surfactant in the water phase reduces. The average emulsion particle diameter was measured through a microscope when the particle diameter was not less than 1 µm. When the particle diameter was less than 1 µm, the average emulsion particle diameter was measured by a dynamic light scattering method using NICOMP-270 (produced by HIAC/ROYCO). On the DSC curve (4) of Example 1 in which the average emulsion particle diameter was 0.07 µm, a single transition peak was observed at 63°C, which indicates that almost all of the amphiphile and the surfactant transferred to the interfaces in the emulsion. The fact that the ratio of the peak on the high-temperature side increases with the increase in the particle diameter indicates that the amount of gel component in the water phase, namely, the amount of amphiphile and surfactant in the water phase increases. From the point of view of the external appearance of the emulsion composition close to that of an aqueous solution and the assurance of the stability as an article of commerce, it is desirable that the DSC curve has only one peak on the low-temperature side, but it is permitted that the area of the peaks on the high-temperature side is about 10% of the total peak area. The emulsion compositions produced in this manner in Comparative Examples 1, 2 and 3 and Example 1 had the following physical properties. The feels thereof at the time of use were also evaluated and the results are shown in Table 2. Comp. 1 Comp. 2 Comp. 3 Ex. 1 Average emulsion particle diameter (µm) - 1 to 10 0.24 0.07 Viscosity (immediately after production)(cps) 55 220 25 12 External appearance Cloudy Cloudy Slightly Cloudy Translucent Stability (left at 40°C for 1 month) - ○ Δ (Increased turbidity·creaming) ○ Creamy feel at the time of the application - ○ ○ ○ As is clear from Table 2, although the emulsion compsition in Comparative Example 2 pruduced a creamy feel, the viscosity was so high that the physical properties close to those of an aqueous solution was not obtained. The emulsion composition in Comparative Example 3 had a high transparency and a low viscosity, in other words, it had physical properties close to those of an aqueous solution, but since the amphiphile and the surfactant remained in the water phase, the stability was lowered (generation of blobs, increase in the turbidity, generation of creaming, etc.). In contrast, in Example 1, not only did the emulsion composition have a high transparency and a low viscosity, but also the stability thereof was good, and an excellent creamy feel was obtained at the time of use. Average emulsion particle diameter The present inventors then investigated the relationship between the average emulsion particle diameter and the stability and the external appearance of the emulsion composition. When the average emulsion particle diameter of the oil phase, which corresponds to the inner phase of the emulsion composition of the present invention, is large, there is a fear of losing the physical properties close to those of an aqueous solution and lowering the stability (generation of creaming, etc.) due to the increase in the turbidity and the increase in the viscosity. The present inventors produced an oil-in-water type emulsion composition which is suitable as an external preparation in accordance with the following prescription. The composition was emulsified by a Mantongaulin while varying the shear force so as to obtain the average emulsion particle diameters shown in Table 3. (%) (1) Behenyl alcohol 1.0 (2) Stearyl alcohol 0.5 (3) Behenic acid 0.5 (4) Stearic acid 0.5 (5) Liquid paraffin 5.0 (6) Potassium hydroxide 0.15 (7) 1,3-butylene glycol 10.0 (8) Ion-exchanged water 10.0 (9) Ion-exchanged water balance (Process) The components (1) to (5) were mixed and stirred at 80°C. The mixture of the components (6) to (8) was heated and dissolved at 80°C. The mixture of the components (1) to (5) was mixed under stirring with the mixture of the components (6) to (8), and emulsified at 80°C by the high-pressure homogenizer while varying the pressure. Thereafter, the component (9) was mixed with the resultant emulsion under stirring. In this manner, samples having different average emulsion particle diameters were obtained. In the prescription, behenic acid, stearic acid and potassium hydroxide form fatty acid soap, which functions as a surfactant. The behenic acid and stearic acid which have not been neutralized, behenyl alcohol and stearyl alcohol function as amphiphiles. Table 3 shows the results of the investigation. Average emulsion particle diameter (µ) Viscosity (mPas) Stability External appearance 0.05 13.5 ○ Translucent 0.06 13.5 ○ Translucent 0.09 14.5 ○ Translucent 0.11 13.0 ○ Translucent 0.14 15.2 ○ Slightly cloudy 0.17 17.1 ▵ Slightly cloudy 0.20 18.5 Δ Cloudy 1 to 5 37.0 X Cloudy The stability was visually evaluated after each sample was left for one month. As is clear from Table 3, both the stability and the external appearance were very good when the average emulsion particle diameter was less than about 0.1 µm . When the average emulsion particle diameter reached about 0.15 µm , although there was no problem in the stability, the whiteness degree of the external appearance became slightly strong. When the average emulsion particle diameter exceeded 0.15 µm, the stability was lowered (creaming was produced) and the emulsion composition was apt to become cloudy. Accordingly, it is to be understood that the suitable average emulsion particle diameter of the emulsion composition of the present invention is not more than 0.15 µm, preferably not more than 0.10 µm. The ratio of the total amount of amphiphile and surfactant to the amount of oil The present inventors then investigated the ratio of the total amount of amphiphile and surfactant to the amount of oil. As described above, it is necessary to transfer substantially the total amount of amphiphile and surfactant to the boundary surfaces of the emulsion particles in the emulsion composition of the present invention. There is a limit to the reduction in the emulsion particle size, and if the amount of oil mixed with the other components is small, the area of the boundary surface of each emulsion particle becomes relatively small. It is therefore difficult to sufficiently transfer the amphiphile and the surfactant to the boundary surfaces. As a result, the gel components remain in the water phase, and there is a fear of greatly lowering the stability of the emulsion composition. The present inventors produced oil-in-water type emulsion compositions. each of which is suitable as an external preparation in accordance with the following prescription so as to examine the emulsion particle diameters and the emulsion stability with time. 1) Behenyl alcohol (%) 1.0 1.0 1.0 1.0 1.0 1.0 2) Stearyl alcohol (%) 0.5 0.5 0.5 0.5 0.5 0.5 3) Behenyl trimethyl ammonium chloride (%) 1.0 1.0 1.0 1.0 1.0 1.0 4) Liquid paraffin (%) 1.0 1.25 2.5 5 10 20 5) 1,3-butylene glycol (%) 15.0 15.0 15.0 15.0 15.0 15.0 6) Ion-exchanged water (%) 15.0 15.0 15.0 15.0 15.0 15.0 7) Ion-exchanged water (%) Balance Balance Balance Balance Balance Balance Average emulsion particle diameter 0.020 0.023 0.025 0.035 0.070 0.140 Satbility with time X ○ ○ ○ ○ ○ (Process) The components (1), (2) and (4) were mixed and stirred at 80°C. The mixture of the components (3), (5) and (6) was heated and dissolved at 80°C. The mixture of the components (1), (2) and (4) was mixed under stirring of the components (3), (5) and (6), and emulsified at 80°C by a high-pressure homogenizer under a pressure of 5000 psi. Thereafter, the component (7) was mixed with the resultant emulsion under stirring, thereby obtaining samples. As is clear from Table 4, when the amount of liquid paraffin as the oil phase was varied between 2.0 to 10.0% with respect to the total amount (2.5%) of amphiphile and surfactant, the smaller the amount of liquid paraffin, the smaller the average emulsion particle diameter. However, the emulsion stability with time was lowered when the amount of liquid paraffin was 1.0%. It is suggested that the ratio of the total amount of amphiphile and surfactant to the amount of oil phase in the present invention is not less than 1/0.5, more preferably not less than 1/1. The present inventors also produced samples in accordance with the following prescription so as to investigate the relationship between the total amount of amphiphile and surfactant and the creamy feel of the product at the time of use. 1) Behenyl alcohol (%) 1.0 0.2 0.08 0.06 2) Stearyl alcohol (%) 0.5 0.1 0.04 0.03 3) Behenyl-trimethyl ammonium chloride (%) 1.0 0.2 0.03 0.06 4) liquid paraffin (%) 4.0 4.0 4.0 4.0 5) Vaseline (%) 1.0 1.0 1.0 1.0 6) 1,3-butylene glycol (%) 15.0 15.0 15.0 15.0 7) Ion-exchanged water (%) 15.0 15.0 15.0 15.0 8) Ion-exchanged water Balance Balance Balance Balance Creamy feel at the time of application o ○ o ○ ○ X o ○: Creamy feel ○: Slightly creamy feel Δ: Scarcely any creamy feel X: No creamy feel (Process) The components (1), (2), (4) and (5) were mixed and stirred at 70°C. The mixture of the components (3), (6) and (7) was heated and dissolved at 70°C. The mixure of the components (1), (2), (4) and (5) was mixed under stirring with the mixture of the components (3), (6) and (7), and emulsified at 70°C by a high-pressure homogenizer under a preessure of 5000 psi. Thereafter, the component (8) was mixed with the resultant emulsion under stirring, thereby obtaining samples. As is clear from Table 5, when the total amount of amphiphile and surfactant was varied between 2.5 to 0.15% with respect to the amount (5%) of oil phase, the smaller the total amount of amphiphile and surfactant, the more the loss of the creamy feel of the emulsion composition at the time of application. It is suggested that the total amount of amphiphile and surfactant is not less than 0.2%, preferably not less than 0.5% of the amount of oil phase in the present invention. Composition of the amphiphile and the surfactant The present inventors next investigated the composition of the amphiphile and the surfactant used in the present invention. It is necessary that the amphiphile and the surfactant used in the present invention form a gel in a surfactant-ampphiphatic substance-water system at least in a temperature range of the solidification point of water phase to ordinary temperatures. The transition temperature of the gel is preferably not lower than 60°C. The transition temperature of the gel formed in a surfactant-amphiphile-water system is generally a temperature 10 to 20°C higher than the temperature at which no gel is formed (the system begins to flow). It is considered that when the transition temperature of a gel is not lower than 60°C, the gel is formed at normal temperatures. The present inventors produced oil-in-water type emulsion compositions each having the following basic composition while varying the combination of the surfactant and the amphiphile, and the change in the physical properties were examined. Emulsion composition (%) (1) Liquid paraffin 5.0 (2) Surfactant 1.0 (3) Amphiphile 1.5 (4) 1,3-butylene glycol 10.0 (5) Ion-exchanged water 20.0 (6) Ion-exchanged water balance Gel (%) (1) Surfactant 1.0 (2) Amphiphile 1.5 (3) Ion-exchanged water balance (Process) Emulsion composition: The components (1) and (3) were mixed and stirred at 70 to 80°C. The mixture of the components (2), (4) and (5) was heated and dissolved at 80°C. The mixture of the components (1) and (3) was mixed under stirring with the mixture of the components (2), (4) and (5) so as to emulsify the resultant mixture. The emulsion was further emulsified at 70 to 80°C by a high-pressure homogenizer under a pressure of 7000 psi. Thereafter, the component (6) was mixed with the resultant emulsion under stirring, thereby obtaining samples. Gel: The component (2) was stirred at 80°C. The mixture of the components (1) and (3) was heated and dissolved at 80°C. The component (2) was mixed under stirring with the mixture of the components (1) and (3) and treated by a homomixer. The results are shown in Tables 6 to 8. In each of Tables 6 to 8, when there are two types of surfactant or amphiphile, the mixing ratio thereof was 1 : 1. Each emulsion was left at 40°C and at 50°C for 1 month and the stability thereof was evaluated. ○: Good ▵: Increase in the turbidity or generation of agglomerates X: Solidification Surfactant Sodium cetyl Sodium lauryl Behenyltrimethyl Stearyltrimethyl sulfate sulfate ammonium chloride ammonium chloride Amphiphatic substance Behenyl alcohol Behenyl alcohol Behenyl alcohol Behenyl alcohol Stearyl alcohol Transition temperature of gel 75°C 68°C 79°C 77°C Stability of emulsion composition (40°C, 1 month) ○ ○ ○ ○ (5°C, 1 month) ○ ○ ○ ○ Surfactant POE (15) Pottasium behenate Potassium stearate Potassium stearate Oleyl ether Potasium stearate Amphiphatic substance Cetyl alcohol Behenyl alcohol Behenyl alcohol Behenyl alcohol Stearyl alcohol Stearyl alcohol Stearyl alcohol Stearyl alcohol Transition temperature of gel 57°C 78°C 73°C 67°C Stability (40°C, 1 month) X ○ ○ ▵ (5°C, 1 month) ▵ ○ ○ ○ Surfactant Potassium stearate Pottasium behenate Potassium atearate Potassium palmitate Amphiphatic substance Cetyl alcohol Stearyl alcohol Cetyl alcohol Stearyl alcohol Transition temperature of gel 64°C 69°C 64°C Stability (40°C, 1 month) ▵ ▵ X (5°C, 1 month) ○ ○ ▵ As is clear from each of Tables 6 to 8, when a combination of a surfactant and an amphiphile which forms a gel having a high transition temperature was used, the stability of the emulsion composition was good. In addition, when a combination of a surfactant and an amphiphile which have different carbon chain lengths was used, the stability was very good. Preferred embodiments of an emulsion composition according to the present invention will now be explained. Embodiment 1 Skin Lotion (%) (1) Behenyl alcohol 2.0 (2) Behenic acid 1.5 (3) Liquid paraffin 7.0 (4) Vitamin E acetate 0.5 (5) Butyl parahydroxybenzoate 0.2 (6) KOH 0.15 (7) Ethanol 5.0 (8) Glycerol 5.0 (9) Perfume 0.05 (10) Ion-exchanged water 15.0 (11) Trisodium edetate 0.01 (12) Sodium 2-hydroxy-4-methocybenzophenon-5-sulfonate 0.05 (13) Ion-exchanged water balance The components (1) to (5) were mixed and stirred at 70°C. The mixture of the components (6) to (10) was heated and dissolved at 70°C. The mixture of the components (1) to (5) was mixed under stirring with the mixture of the components (6) to (10) so as to emulsify the resultant mixture. The emulsion was further emulsified at 75°C by a high-pressure homogenizer under a pressure of 41370 kPa (6000 psi). Thereafter, the mixture of the components (11) to (13) was mixed with the resultant emulsion under stirring, thereby obtaining a translucent skin lotion having a low viscosity. The average emulsion particle diameter of the skin lotion which was measured by a dynamic light scattering method was 0.05 µm, and the viscosity thereof was 10 mPas (cps). When it was actually spread over the skin, it had a creamy feel. Embodiment 2 Whitening Skin Lotion (%) (1) Behenyl alcohol 1.5 (2) Behenic acid 1.0 (3) Liquid paraffin 5.0 (4) Vitamin E acetate 0.5 (5) Butyl parahydroxybenzoate 0.2 (6) KOH 0.13 (7) 1,3-butylene glycol 7.0 (8) Glycerol 8.0 (9) Perfume 0.05 (10) Ion-exchanged water 15.0 (11) Arbutin 3.0 (12) Ion-exchanged water balance The components (1) to (5) were mixed and stirred at 70°C. The mixture of the components (6) to (10) was heated and dissolved at 70°C. The mixture of the components (1) to (5) was mixed under stirring with the mixture of the components (6) to (10) so as to emulsify the resultant mixture. The emulsion was further emulsified at 75°C by a high-pressure homogenizer under a pressure of 55160 kPa (8000 psi). Thereafter, the mixture of the components (11) and (12) was mixed with the resultant emulsion under stirring, thereby obtaining a translucent skin lotion having a low viscosity. The average emulsion particle diameter of the skin lotion was 0.04 µm, and the viscosity thereof was 10 mPas (cps). When it was actually spread over the skin, it had a creamy feel. Embodiment 3 Skin Lotion (%) (1) Behenyl alcohol 2.0 (2) Stearyl alcohol 1.5 (3) Behenic acid 1.0 (4) Stearic acid 1.0 (5) Liquid paraffin 8.0 (6) Vaseline 2.0 (7) Vitamin E acetate 0.5 (8) Butyl parahydroxybenzoate 0.2 (9) KOH 0.2 (10) 1,3-butylene glycol 7.0 (11) Glycerol 10.0 (12) Perfume 0.05 (13) Ion-exchanged water 40.0 (14) Ion-exchanged water balance The components (1) to (8) were mixed and stirred at 70°C. The mixture of the components (9) to (13) was heated and dissolved at 70°C. The mixture of the components (1) to (8) was mixed under stirring with the mixture of the components (9) to (13) so as to emulsify the resultant mixture. The emulsion was further emulsified at 80°C by a high-pressure homogenizer under a pressure of 27580 kPa (4000 psi). Thereafter, the component (14) was mixed with the resultant emulsion under stirring, thereby obtaining a translucent skin lotion having a low viscosity. The average emulsion particle diameter of the skin lotion which was measured by a dynamic light scattering method was 0.07 µm , and the viscosity thereof was 25 mPas (cps). When it was actually spread over the skin, it had a creamy feel. Embodiment 4 Hair Lotion (%) (1) Behenyl alcohol 1.5 (2) Stearyl alcohol 0.3 (3) Dimethyl silicone (20 cps) 10.0 (4) Behenyltrimethyl ammonium chloride 1.0 (5) 1,3-butylene glycol 5.0 (6) Glycerol 10.0 (7) Perfume 0.05 (8) Methylparahydroxybenzoate 0.2 (9) Ion-exchanged water balance The components (1) to (3) were mixed and stirred at 70°C. The mixture of the components (4) to (9) was heated and dissolved at 70°C. The mixture of the components (1) to (3) was mixed under stirring with the mixture of the components (4) to (9) so as to emulsify the resultant mixture. The emulsion was further emulsified at 75°C by a high-pressure homogenizer under a pressure of 55160 kPa (8000 psi), thereby obtaining a transparent hair lotion having a low viscosity. The average emulsion particle diameter of the hair lotion which was measured by a dynamic light scattering method was 0.12 µm, and the viscosity thereof was 20 mPas (cps). When it was actually spread over the hair, it had a creamy feel. Embodiment 5 Sunscreening Lotion (%) (1) Behenyl alcohol 1.0 (2) Stearyl alcohol 0.5 (3) Behenic acid 0.5 (4) Stearic acid 0.5 (5) Neopentyl glycol dicaprate 5.0 (6) Grycelylmono-2-ethylhexanoyldiparamethoxycinnamate 1.0 (7) Butylparahydroxybenzoate 0.2 (8) KOH 0.2 (9) 1,3-butylene glycol 7.0 (10) Glycerol 8.0 (11) Perfume 0.05 (12) Ion-exchanged water 15.0 (13) Ion-exchanged water balance The components (1) to (7) were mixed and stirred at 70°C. The mixture of the components (8) to (12) was heated and dissolved at 70°C. The mixture of the components (1) to (7) was mixed under stirring with the mixture of the components (8) to (12) so as to emulsify the resultant mixture. The emulsion was further emulsified at 70°C by a high-pressure homogenizer under a pressure of 41370 kPa (6000 psi). Thereafter, the component (13) was mixed with the resultant emulsion under stirring, thereby obtaining a translucent sunscreening lotion having a low viscosity. The average emulsion particle diameter of the skin lotion which was measured by a dynamic light scattering method was 0.05 µm, and the viscosity thereof was 15 mPas (cps). When it was actually spread over to the skin, it had a creamy feel. As described above, an oil-in-water type emulsion composition according to the present invention has a comparatively high transparency and a low viscosity, in other words, it has physical properties close to those of an aqueous solution in the preserved state. On the other and, at the time of application, it has a creamy feel. That is, an oil-in-water type emulsion composition having substantially the total amount of amphiphile and surfactant on the interface between each oil phase and a water phase can have not only physical properties close to those of an aqueous solution but also a creamy feel at the time of use.

Claims: An oil-in-water emulsion comprising, in addition to the oil and water, an amphiphile and a cationic or anionic surfactant selected from substances which can form a gel having a transition temperature not below 60°C in an amphiphile-surfactant-water system; wherein not less than 90%, by differential scanning calorimetry, of the amphiphile and the surfactant exist on the boundary surfaces of the emulsion particles; wherein the average emulsion particle diameter is not more than 0.15 µm; wherein the amount of the oil is not less than ½ of the total amount of the amphiphile and the surfactant; wherein the total amount of the amphiphile and the surfactant is not less than 0.2 wt % of the water phase; and wherein the amphiphile comprises an alcohol and/or a fatty acid having a carbon chain length of not less than 16. An emulsion according to claim 1, obtainable by emulsification at a pressure of not less than 6895 kPa (1000 psi). An emulsion according to claim 2, obtainable by emulsification at a pressure of not less than 20685 kPa (3000 psi). An emulsion according to any of claims 1 to 3, obtainable by emulsification at a temperature not lower than the transition temperature of said gel.

Inventors: KAKOKI HIROYUKI, NAKAJIMA HIDEO, NISHIYAMA SHOJI, OKAMOTO TORU, TOMOMASA SATOSHI, KAKOKI, HIROYUKI, NAKAJIMA, HIDEO, NISHIYAMA, SHOJI, OKAMOTO, TORU, TOMOMASA, SATOSHI, KAKOKI, HIROYUKI, C/O SHISEIDO RES. CENTER, NAKAJIMA, HIDEO, C/O SHISEIDO RES. CENTER, NISHIYAMA, SHOJI, C/O SHISEIDO RES. CENTER, OKAMOTO, TORU, C/O SHISEIDO RES. CENTER, TOMOMASA, SATOSHI, C/O SHISEIDO RES. CENTER
Applicants: SHISEIDO CO LTD, SHISEIDO COMPANY LIMITED
Application year: 1994
Main classification: A61K7
IPC codes: A61K8, A61K9, A61Q5, A61K47, A61Q19, A61Q17, B01J13