Blade for gas turbine, manufacturing method of the same, and gas turbine including the blade

Abstract: A gas-turbine moving blade made of a Ni-base superalloy containing less grain boundary strengthening elements, in which a blade portion (1) is formed of a single crystal and the rest is formed of columnar crystals, and a gas turbine including the moving blade. A thermal efficiency of the gas turbine can be improved to 35 % or more, and a thermal efficiency of complex power generation with a steam turbine can be improved to 45 % or more.

Description: The invention relates to a turbine blade for a gas turbine according to the first part of claim 1 having an excellent creep strength, to a manufacturing method of the same, and to a gas turbine including the blades. Conventionally, blades of a gas turbine for power generation have been mainly made of a Ni-base superalloy. However, in order to improve the thermal efficiency of the gas turbine, the temperature of the combustion gas has been increased year by year. Accordingly, to enhance a heat resistance of the blade, materials for the blade have been shifted from equiaxed structure by conventional casting to columnar grain metal structure by unidirectional solidification, and also, internal cooling of the blade has been tried by forming a complicated cooling hole inside of the blade. Most of columnar grain structure castings are manufactured by a unidirectional solidification method disclosed in JP-B-51-4186. In this method, a mold is withdrawn downwardly from a heated furnace so as to effect gradual solidification upwardly from the lower end. With this, a blade having columnar grains of a crystal orientation of 〈100〉, which are elongated in the longitudinal direction in which the centrifugal stress acts, has been manufactured to thereby improve the creep strength property and thermal fatigue strength property. As a blade which is more excellent in high-temperature properties than the columnar grain blade, manufacturing methods of blades for combustion turbines each comprising a blade portion of a single crystal and a root portion of fine grains are disclosed in JP-A-60-261659 and JP-A-61-71168. In order to further enhance the efficiency, it is the most effective method to increase the combustion gas temperature. For this purpose, the internal cooling must be improved, and the high-temperature strength of the material must be also increased. An inner cooling hole of a blade of a gas turbine is formed by use of a ceramic core. In order to further improve the cooling, not only the number of cooling paths has been increased but also the metal section has been decreased in thickness. The blade of a columnar crystal structure is manufactured by the unidirectional solidification method. Molten metal is solidified with the core incorporated therein, and then, it is cooled down to a room temperature. During cooling, thermal contraction occurs. When coefficients of thermal expansion of the core and the casting metal are compared, the core exhibits a value about a tenth smaller than the metal. In consequence, the metal contracts while the core which hardly contracts is kept inside of the metal, resulting in generation of a large tensile stress in the casting during cooling. Therefore, the casting is apt to have crackings in the longitudinal direction along grain boundaries which have low strength. Crackings in the longitudinal direction are particularly caused in a blade portion which is thin. For this reason, the blade portion of the conventional columnar grain blade can not be reduced in thickness, so that it can not be sufficiently cooled. Moreover, intergranular crackings are generated during casting, thus deteriorating the yield. A blade for use in a jet engine for an aircraft has a length of about 10 cm at the maximum and a weight of several hundred grams, and therefore, it can be easily single-crystallized. However, a blade for use in a gas turbine for power generation not only has a complicated configuration but also is extremely large and has a length of 15 to 40 cm and a weight of several kilogram to about 10 kg. According to the method disclosed in JP-B-51-4186, therefore, single-crystallization is extremely difficult because irregular grains and freckle defects are easily generated. The JP-A-60-261659 and JP-A-61-71168 disclose the manufacturing methods in which a blade portion is formed of a single crystal structure, and the remaining portion is formed of fine grains by utilizing magnetic stirring. However, when a conventional single crystal alloy is cast by these methods, there arises a problem that the strength of the portion of fine grains is low. Moreover, when an alloy containing a large amount of grain boundary strengthening elements is used for casting to maintain a certain strength of the portion of fine grains, the melting point of eutectic structure and eutectic γ'-phase formed during solidification is lowered, so that solution treatment can not be fully effected. As a result, the strength of the material can not be improved. As described above, the blade according to the prior art involves a problem that intergranular crackings are easily generated when the blade is decreased in thickness to improve the cooling efficiency, and a problem that the strength can not be improved when grain boundary strengthening elements are added to prevent intergranular cracking. Therefore, it has been impossible to enhance the efficiency of the gas turbine. Moreover, a single crystal blade which is excellent in high-temperature strength has an extremely low yield because irregular grains are easily formed. Further, since a large-size blade of a single crystal can not be manufactured, a single crystal blade can not be applied to blades of a gas turbine for power generation. Therefore, it has been impossible to enhance the efficiency of the gas turbine. In the document M.McLean, "Directionally Solidified Materials for High Temperature Service", Metals Society, London, 1983, pages 144 to 146 it is disclosed a producing process of a single crystal article wherein firstly a section of multiple crystal structure having a random distribution of orientations of the crystals and subsequently another section of columnar grains crystal is obtained under a unidirectional solidification. Further, one of the columnar grains is selected by means of a selector to produce a single crystal article as the object material (see FIG. 4.33). There are present a thin transition cavity or passage for solidifying between the both areas of columnar grains and the single crystal. The US-A-3 568 757 discloses a mold for simultaneously producing a plurality of single crystal castings whose process is likely the same as disclosed in the document cited above. An object of the invention resides in providing a turbine blade for a gas turbine which causes no intergranular cracking during the casting process and which has an excellent creep strength, a method for manufacturing such turbine blades and a gas turbine including said turbine blades. This object will be solved by the features of claim 1. A blade for a gas turbine according to the present invention preferably has a blade portion of a single crystal structure, and the rest other than the single crystal structure region including the blade portion is of unidirectionally solidified columnar grains structure. It is preferred that the blade for the gas turbine according to the invention should have a polycrystal portion of a columnar grains structure whose longitudinal orientations are within 15° from the 〈100〉 orientation, and that a difference of crystal orientations of adjacent columnar grains should be 8° or less. The blade for the gas turbine according to the invention preferably is a casting of a Ni-base superalloy containing, by weight, one or more elements of 0.03 % or more carbon, 0.005 % or more boron and 0.005 % or more Zr, in which precipitated γ'-phase can be dissolved into the γ-phase without incipient melting due to local melting at grain boundaries of the alloy. The alloy containing 0.05 to 0.1 % carbon, and 0.005 to 0.025 % one or both of boron and Zr is suitable for preventing cracking. The blade for the gas turbine of the invention is preferably a casting of a Ni-base superalloy having the following suitable composition by weight %. The casting essentially consists of, by weight, up to 0.20 % C, 5 to 14 % Cr, 4 to 7 % Al, 2 to 15 % W, 0.5 to 5 % Ti, up to 3 % Nb, up to 6 % Mo, up to 12 % Ta, up to 10 % Co, up to 2 % Hf, up to 4 % Re, up to 0.035 % B, up to 0.035 % Zr, and the balance of 58 % or more Ni. The present invention preferably provides a blade for a gas turbine, which is formed of an integral casting and which comprises a blade portion, a platform having a flat portion connected to the blade portion, a shank portion connected to the platform, projection fins on both sides of the shank portion, and a dovetail connected to the shank portion, wherein the blade portion including its root portion connected to the platform, the platform and a part of the shank portion are of a continuous single crystal structure, and wherein the rest of the blade except for the fins is of a unidirectionally solidified columnar grains structure. The invention further preferably provides a blade for a gas turbine, which is formed of an integral casting and which comprises a blade portion, a platform having a flat portion connected to the blade portion, a shank portion connected to the platform, projection fins on both sides of the shank portion, and a dovetail connected to the shank portion, wherein the blade portion including its root portion connected to the platform, the platform and a part of the shank portion are of a continuous single crystal structure, and wherein the rest of the blade is of a unidirectionally solidified columnar grains structure. The blade of the invention preferably includes an integral coolant passage which is continuously provided therein. The invention preferably provides a blade for a gas turbine, essentially consisting of, by weight, up to 0.20 % C, 5 to 14 % Cr, 4 to 7 % Al, 2 to 15 % W, 0.5 to 5 % Ti, up to 3 % Nb, up to 6 % Mo, up to 12 % Ta, up to 10 % Co, up to 2 % Hf, up to 4 % Re, up to 0.035 % B, up to 0.035 % Zr, and the balance of 58 % or more Ni, in which one or both of the carbon content and the boron and Zr content are within a range defined by A (C = 0.20 %, B+Zr = 0 %), B (C = 0.05 %, B+Zr = 0 %), C (C = 0 %, B+Zr = 0.01 %), D (C = 0 %, B+Zr = 0.035 %) and E (C = 0.1 %, B+Zr = 0.025 %), and a difference of crystal orientations is 2 to 8 degrees. The invention preferably provides a blade for a gas turbine, wherein it essentially consists of, by weight, 0.03 to 0.1 % C, 5.5 to 7.0 % Cr, 8.5 to 9.5 % Co, 8 to 9 % W, 2.5 to 3.5 % Re, 0.3 to 1.0 % Mo, 3 to 4 % Ta, 5 to 6 % Al, 0.5 to 1.0 % Ti, 0.5 to 1.0 % Hf, 0.005 to 0.025 % one or both of boron and Zr, and the balance of Ni and unavoidable impurities, in which a difference of crystal orientations is 8 degrees or less. While the blade of the invention can be used for any stage of a three-stage or four-stage gas turbine, it is particularly suitable for the first stage which is exposed to the highest temperature. Conventional polycrystal blades or columnar grain blades are mainly used for the second and subsequent stages. Especially, the following composition is suitable (weight %): C : 0.03 - 0.1, Cr: 5.5 - 7.0, Co: 9 - 10.5, W : 8.0 - 11.0, Re: 1.0 - 3.5, Mo: 0.3 - 1.0, Ta: 3.0 - 4.0, Al: 5.0 - 6.0, Ti: 0.5 - 1.0, Hf: 0.5 - 1.0, one or both of boron and Zr: 0.005 - 0.025, and balance: Ni and unavoidable impurities. Preferably, the blade for the gas turbine of the invention should be subjected to a solution treatment for 2 to 60 hours in a temperature range not less than solvus temperature of the γ'-phase of the alloy after casting and not more than the in cipient melting temperature, and further subjected to a heat treatment at 1000 to 1150°C for 4 to 20 hours and at 800 to 920°C for 8 to 100 hours. A manufacturing method of a blade for a gas turbine of the invention is defined in claim 13, it includes the steps of setting a mold including a ceramic core on a water-cooled chill plate, melting a master ingot and pouring the molten metal into the preheated mold, withdrawing the mold from the heating furnace at a high temperature so as to effect unidirectional solidification from the blade portion toward the root portion successively, thereby forming the blade portion of a single crystal, and withdrawing the mold with respect to the root portion at a higher speed than the withdrawal speed of the mold with respect to the blade portion so as to solidify the root portion unidirectionally. The withdrawal speed of mold in producing the single crystal should preferably be 15 cm/hr or less, and the withdrawal speed of mold in producing the columnar grains should preferably be 20 to 45 cm/hr or less. Especially, the former should be made higher so long as the single crystal can be produced. However, considering the yield, about 10 cm/hr is preferred. When the latter exceeds 50 cm/hr, crystal orientations of the columnar grains have more than 10 degrees therebetween or the columnar grains become equiaxed structure, and consequently, 45 cm/hr or less is preferred. In order to limit a difference of the crystal orientations to 8 degrees or less, the higher the speed is, the better. Therefore, 30 to 45 cm/hr is preferred. The invention preferably provides an article of a unidirectionally solidified casting consisting of a single crystal and columnar grains integrally connected with each other in which a difference of crystal orientations perpendicular to a direction of the solidification of the single crystal and columnar crystals is 8 degrees or less, and the article can be used for other purposes than a moving blade for a gas turbine. The invention preferably provides a blade for a gas turbine, which is formed of an integral casting and which comprises a blade portion, a platform having a flat portion connected to the blade portion, a shank portion connected to the platform, projection fins on both sides of the shank portion, and a dovetail connected to the shank portion, wherein the blade portion including its root portion connected to the platform, the platform and a part of the shank portion are of a continuous single crystal structure, and wherein the rest of the blade is of a unidirectionally solidified columnar grains structure, and wherein an integral coolant passage is continuously provided in the blade from the dovetail to the blade portion, the casting essentially consisting of, by weight, up to 0.20 % C, 5 to 14 % Cr, 4 to 7 % Al, 2 to 15 % W, 0.5 to 5 % Ti, up to 3 % Nb, up to 6 % Mo, up to 12 % Ta, up to 10.5 % Co, up to 2 % Hf, up to 4 % Re, up to 0.035% B, up to 0.035 % Zr, and the balance of 58 % or more Ni, in which one or both of the carbon content and the boron and Zr content are within a range defined by A (C = 0.20 %, B+Zr = 0 %), B (C = 0.03 %, B+Zr = 0 %), C (C = 0 %, B+Zr = 0.01 %), D (C = 0 %, B+Zr = 0.035 %) and E (C = 0.1 %, B+Zr = 0.025 %), the casting has a structure in which γ'-phases are precipitated in γ-phase matrix, and a difference of crystal orientations of the γ-phase is 2 to 6 degrees. The invention preferably provides a gas turbine for revolving blades by striking the combustion gas compressed in a compressor through vanes against the blades embedded in disks, wherein the gas turbine has three or more stages of turbines, and wherein each of the first-stage blades is formed of an integral casting and comprises a blade portion, a platform having a flat portion connected to the blade portion, a shank portion connected to the platform, projection fins on both sides of the shank portion, and a dovetail connected to the shank portion, and wherein the blade portion including its root portion connected to the platform, the platform and a part of the shank portion are of a continuous single crystal structure, and the rest of the blade is of a unidirectionally solidified columnar grain structure. The invention preferably provides the above-described gas turbine, wherein the temperature of the combustion gas is 1,500°C or more, the gas turbine has three stages or more of the turbines, the temperature of combustion gas at the inlet of the first stage of the blades is 1,300°C or more, the overall length of the first stage of the blades is 200 mm or more, wherein each of the first-stage blades is formed of an integral casting, the blade portion is of a single crystal structure and the rest other than the single crystal structure region including the blade portion is of a unidirectionally solidified columnar grain structure, and wherein the power generation capacity is 50,000 KW or more. The invention preferably provides a gas turbine for revolving blades by striking the combustion gas compressed in a compressor through vanes against the blades embedded in disks, wherein the temperature of the combustion gas is 1,500°C or more, the gas turbine has three stages or more of the turbines the temperature of the combustion gas at the inlet of the first stage of the blades is 1,300°C or more, the overall length of the first stage of the blades is 200 mm or more, each of the first-stage blades is formed of an integral casting, which comprises a blade portion, a platform having a flat portion connected to the blade portion, a shank portion connected to the platform, projection fins on both sides of the shank portion, and a dovetail connected to the shank portion, wherein the blade portion including its root portion connected to the platform, the platform and a part of the shank portion are of a continuous single crystal structure and the rest of the blade except for the fins is of a unidirectionally solidified columnar grain structure, and wherein the casting essentially consists of, by weight, 0.03 to 0.1 % C, 5.5 to 9.0 % Cr, 8.5 to 10.5 % Co, 8 to 11 % W, 1.0 to 3.5 % Re, 0.3 to 1.0 % Mo, 3 to 4 % Ta, 5 to 6 % Al, 0.5 to 1.0 % Ti, 0.5 to 1.0 % Hf, 0.005 to 0.025 % one or both of boron (B) and Zr, and the balance of Ni and unavoidable impurities, the casting has a structure in which γ'-phases are precipitated in γ-phase matrix, a difference of crystal orientations of γ-phase of said single crystal and γ-phase of said columnar grains is 8 degrees or less, and the power generation capacity is 50,000 KW or more. The invention preferably provides a combined power generation plant system comprising a gas turbine driven by the combustion gas which flows at a high speed, an exhaust heat recovery boiler to obtain steam from the combustion gas exhausted from the gas turbine, a steam turbine driven by the steam, and a power generator driven by the gas turbine and the steam turbine, wherein the gas turbine includes three or more-stages turbines, the temperature of the combustion gas at the inlet of the first-stage blades is 1,300°C or more, the temperature of the exhausted combustion gas at the outlet of the turbine is 560°C or more, the steam of 530°C or more is obtained by the exhaust heat recovery boiler, the steam turbine is of a high-and-low pressure integrated type, the temperature of the steam fed to a first stage of blades of the steam turbine is 530°C or more, the power generation capacity of the gas turbine is 50,000 KW or more, the power generation capacity of the steam turbine is 30,000 KW or more, and the total thermal efficiency is 45 % or more. The invention preferably provides a combined power generation plant system comprising a gas turbine driven by the combustion gas which flows at a high speed, an exhaust heat recovery boiler to obtain steam from the combustion gas exhausted from the gas turbine, a steam turbine driven by the steam, and a power generator driven by the gas turbine and the steam turbine, wherein the gas turbine includes three or more-stages turbines, the temperature of the combustion gas at the inlet of the first-stage blades is 1,300°C or more, the temperature of the exhausted combustion gas at the outlet of the turbine is 560°C or more, the steam of 530°C or more is obtained by the exhaust heat recovery boiler, the steam turbine is of a high-and-low pressure integrated type, the temperature of the steam fed to a first-stage blades of the steam turbine is 530°C or more, the power generation capacity of the gas turbine is 50,000 KW or more, the power generation capacity of the steam turbine is 30,000 KW or more, the total thermal efficiency is 45 % or more, the overall length of the first-stage blades is 200 mm or more, each of the first-stage blades is formed of an integral casting, which comprises a blade portion, a platform having a flat portion connected to the blade portion, a shank portion connected to the platform, projection fins on both sides of the shank portion, and a dovetail connected to the shank portion, wherein the blade portion including its root portion connected to the platform, the platform and a part of the shank portion are of a continuous single crystal structure, and the rest of the blade except for the fins is of a unidirectionally solidified columnar grain structure, and wherein the casting essentially consists of, by weight, 0.03 to 0.1 % C, 5.5 to 9.0 % Cr, 8.5 to 10.5 % Co, 8 to 11 % W, 1.0 to 3.5 % Re, 0.3 to 1.0 % Mo, 3 to 4 % Ta, 5 to 6 % Al, 0.5 to 1.0 % Ti, 0.5 to 1.0 % Hf, 0.005 to 0.025 % one or both of boron (B) and Zr, and the balance of Ni and unavoidable impurities, the casting has a structure in which γ'-phases are precipitated in γ-phase matrix, and a difference of crystal orientations of γ-phase of the single crystal and γ-phase of the columnar grains is 8 degrees or less. DETAILED DESCRIPTION OF THE INVENTION The moving blade for the gas turbine of the invention has a blade portion of a single crystal structure, and the rest other than the single crystal structure region is of a unidirectional solidified columnar grains structure. The difference of crystal orientations of adjacent columnar crystals is made as small as possible, and particularly, the difference is limited to 8° or less. Thus, even if amounts of grain boundary strengthening elements are decreased, a columnar grain blade in which intergranular cracking are not generated during casting can be obtained, and substantially the same level of strength as a single crystal blade can be maintained. Moreover, since the amounts of grain boundary strengthening elements are decreased, the melting point of the eutectic structure formed during casting is raised to increase the temperature of a solution heat treatment, thereby enabling a heat treatment of dissolving precipitated γ'-phases into γ-phase of the base. Therefore, a columnar grain blade having a high creep strength can be obtained. In contrast, if the difference of crystal orientations exceeds 10 degrees, the strength is drastically decreased to about 10 to 20 % of the strength of the single crystal blade. In order to improve a high-temperature strength of the material, a solution heat treatment after casting is effective. In the solution heat treatment, γ'-phases precipitated after solidification are fully dissolved into the base so that the size and configuration of the precipitated γ'-phases can be made the most suitable in the subsequent aging heat treatment, thus improving the high-temperature strength. However, large amounts of grain boundary strengthening elements such as boron (B), carbon (C), Zr, Hf and so forth must be added to an alloy used for the conventional columnar grain blade so as to prevent crackings in the longitudinal direction along grain boundaries during casting. The grain boundary strengthening elements not only improve the strength of crystal grain boundaries but also partially segregate between branches of dendrite to lower the melting point of the segregated portion by a remarkable degree. In the case of a Ni-base superalloy, the segregated portion forms eutectic structure and generates coarse eutectic γ'-phase during solidification. The eutectic structure and the eutectic γ'-phase formed have the lowest melting point within the alloy structure. When temperature is elevated to perform a solution heat treatment, the eutectic structure melts at first. Therefore, temperature of solution heat treatment could not be made high enough so that solution heat treatment of the alloy used for the conventional columnar grain blade was not sufficient. As a result, the strength of the conventional alloy could not be improved. In an alloy of a single crystal without grain boundary strengthening elements, the elements are regarded as impurities, and their content is made as low as possible. Consequently, the melting point of eutectic γ'-phase is increased to enable a complete solution heat treatment. Therefore, the single crystal alloy exhibits an excellent high-temperature property which is 40 to 50°C higher than that of the conventional columnar grain materials, and is employed for a moving blade of a jet engine for an aircraft. However, the single crystal alloy contains grain boundary strengthening elements of an amount as small as possible, and therefore it is extremely weak when grain boundaries are formed. If irregular crystals having different crystal orientations are present, crackings are easily formed at grain boundaries. Normally, when grain boundaries are present, an alloy is weakened to such a degree that crackings are formed by mere cooling after casting. Therefore, the cast blade of the single crystal alloy must be of a complete single crystal with no irregular crystals. The function of each of the elements included in the Ni-base superalloy which constitutes the blade for the gas turbine will now be described. Carbon dissolves in matrix or grain boundaries in particular and forms carbides to improve high-temperature tensile strength. However, if it is added excessively, the melting point of grain boundaries is lowered, thereby deteriorating high-temperature strength and toughness. Consequently, an appropriate additive amount of carbon is in a range of 0.05 to 0.2 %, preferably 0.03 to 0.1 %. Co dissolves in matrix to improve high-temperature strength and also contributes to improvement of hot corrosion resistance. If it is added excessively, it promotes precipitation of harmful intermetallic compounds, thereby deteriorating high-temperature strength. An appropriate additive amount of Co is 10.5 % or less, preferably 9 to 10.5 %. Cr improves hot corrosion resistance. However, if it is added excessively, it causes precipitation of harmful σ-phase and coarsening of carbides, thereby deteriorating high-temperature strength. An appropriate additive amount of Cr is in a range of 5 to 14 %, preferably 5.5 to 9 %. Al and Ti contribute to improvement of high-temperature strength by forming γ'-phase, i.e., Ni 3 (Al, Ti), which is a strengthening factor of the Ni-base alloy. Appropriate additive amounts of Al and Ti are, respectively, in ranges of 4.0 to 7.0 % and 0.5 to 5.0 %, and preferably 5 to 6 % of Al and 0.5 to 1.0 % of Ti. Nb, Ta and Hf dissolve in γ'-phase which is a strengthening factor, and improve high-temperature strength of the alloy. However, if they are added excessively, they segregate at grain boundaries and deteriorate strength of the alloy. Appropriate additive amounts of Nb, Ta and Hf are, respectively, 3 % or less, 12 % or less and 2 % or less, and preferably 0.2 to 3.0 % of Nb, 3 to 4 % of Ta and 0.5 to 1.0 % of Hf. Zr and boron (B) strengthen grain boundaries and improve high-temperature strength of the alloy. However, if they are added excessively, ductility and toughness are degraded, and they lower the melting point of grain boundaries, thereby deteriorating high-temperature strength of the alloy. Appropriate additive amounts of Zr and B are, respectively, up to 0.035 % and up to 0.035 %. Preferably, considering the relationship with carbon content, they should be within a range defined by A (C = 0.20 %, B+Zr = 0 %), B (C = 0.05 %, B+Zr = 0 %), C (C = 0 %, B+Zr = 0.01 %), D (C = 0 %, B+Zr = 0.035 %) and E (C = 0.1 %, B+Zr = 0.025 %), or one or both of boron (B) and Zr should be 0.005 to 0.025 %. W (tungsten) and Mo dissolve in γ-phase of the matrix and strengthen it, and they are particularly effective for improving long-term strength of the alloy. However, if they are added excessively, they promote precipitation of a harmful phase such as σ-phase, thereby deteriorating strength of the alloy. Appropriate additive amounts of W and Mo are, respectively, 2 to 15 % and 6.0 % or less, and preferably 8.0 to 11.0 % of W and 0.3 to 1.0 % of Mo. Re improves hot corrosion resistance of the alloy. However, if it exceeds a certain amount, the effect is saturated, and ductility and the toughness of the alloy are degraded. An appropriate additive amount of Re is 4 % or less, and preferably 2.5 to 3.5 %. In the case where a difference of crystal orientations of the single crystal is 8 degrees or less, suitably there is no grain boundary in the Ni-base superalloy as the single crystal. If a difference of crystal orientations of columnar grains is 15 degrees or less, a satisfactory strength can be obtained as the columnar grains. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a perspective view showing a blade for a gas turbine according to the invention; Fig. 2 is a structural diagram schematically showing a manufacturing method of the blade for the gas turbine according to the invention; Fig. 3 is a plan view showing a core of the blade for explaining the positional relationship between the core and the blade in one embodiment of the invention; Fig. 4 is a graph for comparing a high-temperature strength of the columnar grain blade obtained according to the invention and a high-temperature strength of a conventional columnar grain blade; Fig. 5 is a drawing illustrative of a condition of intergranular cracking which were observed in a conventional columnar grain blade manufactured by a unidirectional solidification method; Fig. 6 is a characteristic graph illustrative of the relationship between the carbon content and the "B + Zr" content by which precipitated γ'-phases can dissolve into γ-phase without incipient melting of the alloy, and their relationship with intergranular cracking; Fig. 7 is a diagram showing the overall structure of a gas turbine according to another embodiment of the invention; and Fig. 8 is a diagram showing the overall system of a combined power generation plant according to a still other embodiment of the invention. Example 1 Fig. 1 is a perspective view showing a blade having single crystal structure for a gas turbine according to the invention, and Fig. 2 is a schematic view of an apparatus for explaining a manufacturing method of the blade. As shown in Fig. 2, a ceramic mold 8 mainly composed of alumina was first fixed on a water-cooled copper chill plate 11, and was set in a mold heating furnace 4 so that the ceramic mold 8 was heated to a melting point of an Ni-base superalloy or higher temperature. Subsequently, the molten Ni-base superalloy was poured in the ceramic mold 8, and then, the water-cooled copper chill plate 11 was withdrawn downwardly so as to conduct unidirectional solidification of the alloy. In the unidirectional solidification, a large number of crystals were generated first by a starter 10. Next, only one crystal was selected by a selector 9. The one selected crystal was enlarged in an enlarging portion, and a blade portion was solidified at a withdrawal speed of 10 cm/h, to thereby form it of a single crystal. After the blade portion solidified to a single-crystal, the remaining portion was not grown into a single crystal but formed into columnar grains by increasing the withdrawal speed of the mold to 40 cm/h after a position of a platform 15. According to this method, a columnar grain blade comprising a blade portion of a single crystal structure and the remaining portion of a columnar grain structure was obtained. The single crystal structure of the blade portion does not suddenly and entirely change to the columnar grains structure at the platform, but the platform connected to the blade portion and a part of the shank portion are of the single crystal structure, while a peripheral region of the section of the platform which is just connected to the blade portion, the rest of the shank and the dovetail are of the columnar grains structure. In this case, the columnar grains were grown from the single crystal of the blade portion serving as the seed so that a difference in orientations of the columnar grains could be made as small as about 5°. The mold heating furnace 4 was kept at a high temperature until the ceramic mold 8 was completely withdrawn and the solidification was finished. The above-described melting and solidifying processes were both carried out under vacuum. Table 1 shows casting conditions of the invention blade, and Table 2 shows a composition of the Ni-base superalloy used in casting. After casting, the blade cast by the foregoing method was subjected to a solution heat treatment at a temperature of 1260 to 1280°C under vacuum for 2 to 60 hours, and precipitated γ'-phases formed in the cooling process after solidification was changed into γ-phase. Thereafter, the blade was subjected to an aging heat treatment at a temperature of 1000 to 1150°C for 4 to 20 hours and at a temperature of 800 to 950°C for 8 to 100 hours, thereby precipitating γ'-phases of the average size of 0.3 to 2 µm in γ-phase of the matrix. PREHEATING TEMPERATURE OF MOLD 1540°C POURING TEMPERATURE 1550°C MOLD WITHDRAWAL SPEED 10 cm/h AT BLADE PORTION; 40 cm/h FROM A PLATFORM POSITION MOLD MATERIAL ALUMINA CERAMIC MOLD C 0.05 - 0.1 Cr 5.5 - 7.0 Co 9.0 - 9.5 W 8.0 - 9.0 Re 2.8 - 3.1 Mo 0.3 - 0.7 Ta 3.0 - 4.0 Al 5.5 - 6.0 Ti 0.5 - 0.9 Hf 0.7 - 1.0 B 0.005 - 0.01 Zr 0.005 - 0.01 Ni BALANCE - - A thermocouple was inserted into the mold 8 at a zone corresponding to the platform 15, and a temperature of the zone was measured. When the temperature reached the solidifying temperature, the withdrawal speed of the mold was changed. A partition plate of graphite was provided under the heating furnace 4, and a water-cooled copper pipe was wound in a spiral form around a lower portion of the partition plate, so as to cool the mold. The blade obtained according to the above-described method had a blade portion 1 of a single crystal structure, and a portion 2 of the blade under the platform 15 was a columnar grain structure. Air-cooled fins 14 were formed of grains having a diameter of about 10 mm which could not be called columnar grains. Although the surface of a shank 18 was a columnar grain structure, large columnar grains which had grown from the single crystal of the blade portion 1 and gradually reduced into small columnar grains were formed inside of the shank. The width of the columnar grains on the surface was 5 to 10 mm, and the average width was 5 to 6 mm. Fig. 3 is a plan view showing a core of the blade for explaining the positional relationship between the core and the moving blade. The blade of this embodiment is hollow to cool the blade itself. Although the air is used as a cooling medium, steam cooling can also be applied. The cooling air is supplied from a core 21 of a dovetail 16 and divided into a flow discharged from a distal end portion 17 of the blade and a flow discharged from a trailing edge 23 of the blade. The core includes holes 20, and two blade surfaces are connected with each other by these holes. The trailing edge 23 has a slit-like discharge port of the cooling air. The core includes holes 22 in which molten metal is filled. In the embodiment, the length of the blade portion 1 is about 100 mm, and the length of the remaining portion of the blade under the platform is 120 mm. The creep rupture strength of the blade thus obtained is shown in Fig. 4, using Larson-Miller parameter P. A commercial CM186LC alloy of columnar grains was used as a comparative material. The invention blade was single-crystallized and subsequently subjected to a solution heat treatment and an aging heat treatment whereas the comparative blade having the conventional columnar grain structure was only subjected to an aging heat treatment. A temperature capability of the invention blade with respect to the creep at a stress of 14.0 kgf/mm 2 for 100,000 hours was improved by about 20°C as compared with the comparative blade. The commercial alloy had substantially the same composition as shown in Table 2 except for 0.016 % B, 0.016 % Zr and 0.15 % carbon. Example 2 The blade of the invention could be subjected to a solution heat treatment because the melting point of the eutectic structure of the alloy was raised by controlling amounts of carbon (C), boron (B) and Zr. A method of raising the melting point of the eutectic structure will now be described. A conventional alloy containing grain boundary strengthening elements, which contains large amounts of C, B, Zr, Hf and so forth, could not be subjected to a solution heat treatment. Therefore, using a Ni-base alloy essentially consisting of, by weight, Cr: 5.0 - 14.0 %, Co: 0 - 12.0 %, W : 5.0 - 12.0 %, Re: 0 - 3.5 %, Mo: 0.5 - 3.0 %, Ta: 3.0 - 7.0 %, Al: 4.0 - 6.0 %, Ti: 0.5 - 3.0 %, Hf: 0 - 2.0 % a ratio of the carbon content and the "Zr + B" content of the alloy was changed, and the relationship between the melting point of the eutectic structure and the solidus temperature of precipitated γ'-phases was investigated. As a result, it was found that when the carbon content was 0.1 % or less and the "B + Zr" content was 0.025 % or less, precipitated γ'-phases could dissolve into the base phase without incipiene melting of the eutectic structure. However, with regard to a Ni-base superalloy containing 0.1 % or less of carbon and total 0.025 % or less of "B + Zr", when a unidirectionally solidified blade having a columnar grain structure was cast intergranular crackings generated. Fig. 5 illustrates intergranular cracking of a blade having a columnar grain structure manufactured according to the conventional unidirectional solidification method. That is to say, if a columnar grain structure blade was manufactured of the alloy whose carbon content was 0.1 weight % or less and "B + Zr" content was 0.025 weight % or less according to the conventional unidirectional solidification method, crackings generated at grain boundaries, and consequently, the blade could not be provided as a product. The relationship of a difference in crystal orientations of columnar grains, the carbon content and the "Zr + B" content of the alloy, and intergranular cracking was investigated. When the difference in crystal orientations of columnar grains was within 8°, and when the carbon content was 0.03 % or more and the "Zr + B" content was 0.005 % or more by weight, a favorable columnar grain blade without intergranular cracking could be obtained. However, when the difference in crystal orientations of columnar grains was 8° or more, intergranular cracking were generated even if the carbon content was 0.03 % or more and the "Zr + B" content was 0.005 % or more. When the carbon content was 0.03 % or less, intergranular cracking generated even if the difference in crystal orientations of columnar grains was within 8°. The foregoing results are shown in Fig. 6. It should be noted that when the difference in crystal orientations of columnar grains is within 6°, a blade without incipient melting and no intergranular cracking can be obtained from an alloy within a range defined by A (C = 0.20 %, B+Zr = 0 %), B (C = 0.05 %, B+Zr = 0 %), C (C = 0 %, B+Zr = 0.01 %), D (C = 0 %, B+Zr = 0.035 %) and E (C = 0.1 %, B+Zr = 0.025 %). A preferable range is within a pentagon defined by A (C = 0.2 %, B+Zr = 0 %), B (C = 0.04 %, B+Zr = 0.002 %), C (C = 0 %, B+Zr = 0.01 %), D (C = 0 %, B+Zr = 0.02 %) and, E (C = 0.1 %, B+Zr = 0.02 %). In order to prevent generation of intergranular cracking in the alloy whose carbon content is 0.1 weight % or less and "B + Zr" content is 0.025 weight % or less, the difference in crystal orientations must be within 8°. In the conventional unidirectional solidification method, however, lateral crystal orientations of columnar grains were at random and could not be controlled to be within 8°. On the other hand, in the method according to the present invention, the blade portion was formed of a single crystal, and columnar grains were grown from the single crystal serving as a seed, so that the difference in orientations of columnar crystals could be within 8°. That is to say, when the blade portion was formed of a single crystal and the other portions were formed of columnar grains having an orientation difference within 8° as in the invention, a favorable columnar grain blade without intergranular cracking could be obtained even if the carbon content was 0.1 weight % or less and the "B + Zr" content was 0.025 weight % or less. Substantially the same effect was exhibited with either one or both of boron (B) and Zr. Table 3 shows comparison results of characteristics of a columnar grain blade and a single crystal blade according to the conventional method and a blade according to the present invention when the blades were manufactured to have a blade length of 22 cm (100 mm in the blade portion, 120 mm in the root portion). A commercial alloy was employed for casting the columnar grain blade and the single crystal blade. KIND OF BLADE CASTING TEMP. (°C) CASTING TIME (h) GENERATION RATE OF INTERGRANULAR CRACKING (%) GENERATION RATE OF DEFECTS (%) YIELD (%) TEMP. CAPABILITY (°C) COLUMNAR GRAINS BLADE 1520 1.0 75 20 15 900 SINGLE CRYSTAL BLADE 1600 3.0 0 95 5 940 INVENTION BLADE 1540 1.5 0 30 70 920 Since no intergranular cracking were generated in the columnar grain blade of the invention, the yield was 70 % and about five times higher than that of the blade which was 15 %, and the temperature capability with respect to the creep at a stress of 14.0 kgf/mm 2 for 100,000 hours was increased by about 20°C. When only the temperature capabilities were compared, the blade of the invention was inferior to the single crystal blade. However, in this invention, the other portions than the blade portion were of a columnar grain structure so that the casting time could be shortened, and that the mold heating temperature could be lowered. As a result, less reactions between the alloy with the mold occurred, and the ratio of defects was decreased, thereby improving the yield of production of blades. Therefore, the present invention provides a significantly practical columnar grains blade and a significantly practical manufacturing method. Obviously, even if an entirety blade is formed of a single crystal by use of the invention alloy, no actual problems will arise although the productivity and the yield are deteriorated. Example 3 According to the method described in Example 1, a Ni-base superalloy having a chemical composition (weight %) shown in Table 4 was cast, and a columnar grain blade in which a blade portion was formed of a single crystal and the other portions were substantially perfectly formed of columnar grains was manufactured. A mold in this embodiment was designed in such a manner that a straight mold bypassed from a single crystal enlarging portion with respect to the projection fins as shown in Fig. 2, was formed so that the projection fins will be of columnar grains. No intergranular cracking was observed in the cast blade. The blade was subjected to a solution heat treatment at 1270 to 1285°C for 2 to 60 hours and an aging heat treatment at 1000 to 1150°C for 4 to 20 hours and at 800 to 950°C for 8 to 100 hours. Temperature capabilities of the foregoing blade and a comparative sample with respect to the creep at a stress of 14.0 kgf/mm 2 for 100,000 hours were compared. The comparative sample was only subjected to an aging heat treatment at 1000 to 1150°C for 4 to 20 hours and at 800 to 950°C for 8 to 100 hours. As a result, it was found that the temperature of the blade was increased by about 15°C. In this embodiment, the difference in crystal orientations of columnar grains was about 5°. C 0.1 - 0.15 Cr 8.0 - 9.0 Co 9.5 - 10.5 W 10.0 - 11.0 Re 1.0 - 1.5 Mo 0.3 - 0.7 Ta 3.0 - 4.0 Al 5.5 - 6.0 Ti 0.5 - 1.5 Hf 0.7 - 1.0 B 0.005 - 0.01 Zr 0.005 - 0.01 Ni BALANCE - Example 4 Fig. 7 is a cross-sectional view showing a rotor portion of a gas turbine which includes the gas-turbine blade of the present invention described in the example 2. Reference numeral 30 denotes a turbine stub shaft, 33 a turbine blade, 43 a turbine stacking bolt, 38 a turbine spacer, 49 a distant piece, 40 a turbine vane, 36 a compressor disk, 37 a compressor blade, 38 a compressor stacking bolt, 39 a compressor stub shaft, 34 a turbine disk, and 41 a hole. The gas turbine of the invention includes 17 stages of the compressor disk 36 and three stages of the turbines 33. The turbines may be a four-stage one. In either case, the invention alloy the can be applied. The main types of the gas turbine in this embodiment is a heavy duty type, and had a single shaft, a horizontal division casing and a stacking type rotor. The compressor has a 17-stage axial flow type, the turbine has a three-stage impulse type. The first and second-stage blades and vanes are air-cooled. The combustor is a reverse flow type, and had 16 tubular combustor portions and a slot cool. The entirety tempered martensitic steel essentially consisting of, by weight, 0.06 to 0.15 % C, 1 % or less Si, 1.5 % or less Mn, 9.5 to 12.5 % Cr, 1.5 to 2.5 % Ni, 1.5 to 3.0 % Mo, 0.1 to 0.3 % V, 0.03 to 0.15 % Nb, 0.04 to 0.15 % N (nitrogen) and the balance of Fe is used for the distant piece 39, the turbine disk 34, the spacer 38 and the stacking bolt 33. As characteristics of this embodiment, tensile strength was 90 to 120 kg/mm 2 , 0.2 % yield strength was 70 to 90 kg/mm 2 , elongation rate was 10 to 25 %, area reduction rate was 50 to 70 %, V-notch impact value was 5 to 9.5 kg-m/cm 2 , creep rupture strength at 450°C for 105 hours was 45 to 55 kg/mm 2 . The turbine blades 33 had three stages, and the blade manufactured in the embodiment 1 was used for the first stage. The compressor had a compression pressure of 14.7 and a temperature of 400°C, the temperature at the inlet of the first stage of the blades was 1,300°C, and the temperature of the gas of combustion by the combustor was at a level of 1450°C. Blades made of a polycrystal structure having substantially the same composition as the first-stage blades which have a length of 280 mm (160 mm of a blade portion and the remaining 120 mm from a platform portion) was manufactured for the second stage of the turbine moving blade 33. The third-stage blades were made of the same alloy as that of the second-stage. The blade had a poly crystal structure which had a length of 350 mm (230 mm of a blade portion and the remaining 120 mm). The third-stage blades were a solid type. A conventional precision casting method with the lost wax process was adopted. A known Co-base alloy was used for the first to third-stages turbine vanes 40. The vanes each including a single vane portion were formed by the vacuum precision casting. The vane portion had a length equivalent to the length of the blade portion of the each blade, and included a structure of pin-fin cooling, impingement cooling and film cooling. The first-stage vanes were retained at both ends whereas the second-stage and third-stage vanes were retained at one side by the side wall. An inter-cooler was provided for the gas turbine. 50 MW of the power generation output could be obtained from this embodiment, and the thermal efficiency was 33 % or higher. Example 5 Fig. 8 is a schematic view showing a single shaft type combined cycle power generation system in which the gas turbine of the example 4 is used and a steam turbine is also used. When power generation is carried out by employing a gas turbine, it is likely that a so-called combined power generation method is employed these days in which the gas turbine is driven by liquefied natural gas (LNG) as a fuel, and also, a steam turbine is driven by the steam obtained by recovering energy from the exhaust gas of the gas turbine, so that a power generator is driven by the steam turbine and the gas turbine. In the combined power generation method, the following system structure enables a thermal efficiency of about 45 % or more, which is higher than the thermal efficiency of the conventional system provided with a steam turbine alone which is 40 %. Lately, such a combined power generation plant has been shifted from exclusive combustion of liquefied natural gas (LNG) to selective combustion of either liquefied natural gas (LNG) or liquefied petroleum gas (LPG), and mixed combustion of LNG and LPG has been realized, to thereby enable smooth operation of the plant and improve the economical effect. First, the air is introduced to an air compressor of a gas turbine through a suction filter and a suction silencer. The air compressor compresses the air and supply the compressed air to a low NOx combustor. In the combustor, fuel is injected into the compressed air and burned to produce high-temperature gas of 1400°C or more. This high-temperature gas fulfills its task in the turbine, and motive power is generated. The gas at a temperature of 530°C or more exhausted from the turbine is supplied to an exhaust heat recovery boiler by way of an exhaust gas silencer, and the thermal energy in the exhaust gas from the gas turbine is recovered to produce high-pressure steam of 530°C or more. The boiler is provided with a denitration device of dry ammonia catalytic reduction. The exhaust gas is discharged to the outside through a triple smoke passage combined type flue of several hundred meters. The produced high-pressure and low-pressure steam is supplied to a steam turbine composed of a high-and-low pressure integrated rotor. The steam discharged from the steam turbine is introduced into a condenser and deaerated in a vacuum to as to be transformed into a condensed water. The condensed water is pressurized by a condensate pump and delivered as feed water to a boiler. Then, the gas turbine and the steam turbine drive a power generator from opposite ends of the shaft, thus performing power generation. In order to cool a gas turbine blade for such combined power generation, the steam used in the steam turbine is sometimes used as a cooling medium as well as the air. In general, the air is used as a cooling medium for a blade. However, because a specific heat of the steam is by far larger than that of the air, and because the steam has a light weight, the cooling effect is superior. According to the combined power generation system, a total of 80,000 KW power generation output composed of 50,000 KW from the gas turbine and 30,000 KW from the steam turbine can be obtained. Since the steam turbine of the embodiment is compact, it can be manufactured at a lower cost than a large-scale steam turbine having the same power generation capacity, which results in a great advantage that economical operation in accordance with a change of the generation output can be performed. The steam turbine according to the present invention is a high-and-low pressure integrated type. The single-machine output of the turbine can be increased by raising the steam pressure at the inlet of the main steam of the high-and-low pressure integrated type steam turbine to 100 atg and by raising the temperature to 538°C. In order to raise the single-machine output, it is necessary to increase the blade length of the final stage of the moving blade to 30 inches or more and to increase the steam flow rate. The steam turbine according to the present invention includes 13 stages or more of the blades which are embedded in the high-and-low pressure integrated type rotor shafts. The steam flows in the turbine at a high temperature of 538°C and a high pressure of 88 atg from the steam inlet, as described above, by way of a steam control valve. The steam flows in one direction from the inlet to the final stage blades at a temperature of 33°C at 722 mmHg and is exhausted from the outlet. Forged steel of Ni-Cr-Mo-V low alloy steel is used for the high-and-low pressure integrated type rotor shaft according to the present invention. The portion where the blades are firmly connected on a rotor shaft is disk-shaped and produced totally by cutting from the rotor shaft. The shorter the length of the blade, the longer the width of the disk portion is arranged so as to cause the least vibration. The high-and-low pressure integrated type rotor shaft according to this embodiment essentially consists of 0.18 to 0.30 % C, up to 0.1 % Si, up to 0.3 % Mn, 1.0 to 2.0 % Ni, 1.0 to 1.7 % Cr, 1.0 to 2.0 % Mo, 0.20 to 0.3 % V and the balance of Fe. The rotor shaft is quenched at 900 to 1050°C by water spray cooling, and is thereafter tempered at 650 to 680°C. The construction of the plant can be arranged as a single-shaft type which combines six sets of power generation systems, one set comprising a gas turbine, an exhaust heat recovery boiler, a steam turbine and a power generator. Also, the construction of the plant may be arranged as a multi-shaft type in which a power generator combined with a gas turbine makes one set, and six sets thereof are combined to obtain the steam from the exhaust gas and introduce it into a steam turbine and a power generator. The combined power generation is realized by a combination of a gas turbine which can be started and stopped in a short time and easily and a small-size and simple steam turbine. Therefore, the output control can be readily effected, and the combined power generation is suitably used for an intermediate-load thermal power generator which responds to the changing demand. The reliability of the gas turbine is remarkably enhanced due to the development of the latest technology. Further, the combined power generation plant is a system constituted of a combination of machines with small capacities. Thus, when a machine fault occurs, the damage thereof can be contained to local parts, thereby providing a highly reliable power source. According to the present invention, a blade for a gas turbine having a high creep strength can be obtained to lengthen the durability of the blade and to increase the combustion gas temperature, thereby producing a remarkable effect that a thermal efficiency of the gas turbine and a thermal efficiency of a combined power generation plant system including the gas turbine can be improved. Further, according to the manufacturing method of the blade for the gas turbine of the invention, the yield of the manufacture of blades can be enhanced.

Claims: A turbine blade for a gas turbine, which is formed of an integral casting and comprises a blade portion (1), a platform (15) having a flat portion connected to said blade portion (1), a shank portion (18) connected to said platform (15), projection fins (14) on both sides of said shank portion (18), and a dovetail (10) connected to said shank portion (18), characterized in that said blade portion (1) including its root portion connected to said platform (15), a part of said platform (15) and a part of said shank portion (18) are of a continuous single crystal structure, said dovetail (10), the rest of said shank portion (18) and the rest of said platform (15) are of a unidirectionally solidified columnar grains structure, and said fins (14) are of a unidirectionally solidified columnar grains structure or of a grains structure. Turbine blade according to claim 1, characterized in that an integral coolant passage is continuously provided in the blade from said dovetail (10) to said blade portion (1). Turbine blade according to claim 1 or 2, characterized in that the longitudinal orientations of columnar grains structure are within 15° from the 〈100〉 - Orientation. Turbine blade according to any one of the claims 1 to 3, characterized in that, the difference of crustal orientations of adjacent columnar grains is 8° or less. Turbine blade according to one of the preceeding claims, characterized in that said casting comprising, by weight, up to 0.20 % C, 5 to 14 % Cr, 4 to 7 % Al, 2 to 15 % W, 0.5 to 5 % Ti, up to 3 % Nb, up to 6 % Mo, up to 12 % Ta, up to 10.5 % Co, up to 2 % Hf, up to 4 % Re, up to 0.033 % B, up to 0.035 % Zr, and the balance of 58 % or more Ni. Turbine blade according to claim 5, characterized in that one or both of the carbon content and the "B and Zr" content are within a range defined by A (C = 0.20 %, B+Zr = 0 %), B (C = 0.03 %, B+Zr = 0 %), C (C = 0 %, B+Zr = 0.01 %), D (C = 0 %, B+Zr = 0.035 %) and E (C = 0.1 %, B+Zr = 0.025 %), and a difference of crystal orientations is 2 to 6 degrees. Turbine blade according to one of claims 1 to 4, characterized by, 0.03 to 0.1 % C, 5.5 to 9.0 % Cr, 8.5 to 10.5 % Co, 8 to 11 % W, 1.0 to 3.5 % Re, 0.3 to 1.0 % Mo, 3 to 4 % Ta, 5 to 6 % Al, 0.3 to 1.3 % Ti, 0.5 to 1.0 % Hf, 0.005 to 0.025 % one or both of B and Zr, and the balance of Ni (by weight) and unavoidable impurities, in which a difference of crystal orientations is 8 degrees or less. Turbine blade according to claim 6, characterized in that the casting having a structure in which γ'-phases precipitate in γ-phase matrix, and a difference of crystal orientations of said γ-phase being 2 to 6 degrees. A gas turbine comprising revolving turbine blades by striking the combustion gas compressed in a compressor (36, 37) through vanes (40) against said blades (33) embedded in disks, wherein said gas turbine has three or more stages of turbines, wherein characterized in that the first-stage turbine blades are formed according to anyone of the preceding claims. Gas turbine according to claim 9, characterized in that said casting comprising by weight, 0.03 to 0.1 % C, 5.5 to 9.0 % Cr, 8.5 to 10.5 % Co, 8 to 11 % W, 1.0 to 3.5 % Re, 0.3 to 1.0 % Mo, 3 to 4 % Ta, 5 to 6 % Al, 0.5 to 1.0 % Ti, 0.5 to 1.0 % Hf, 0.005 to 0.025 % one or both of B and Zr, and the balance of Ni and unavoidable impurities, said casting having a structure in which γ'-phases precipitate in γ-phase matrix, a difference of crystal orientations of the γ-phase of said single crystal and the γ-phase of said columnar grains being 8 degrees or less, and the power generation capacity being 50,000 KW or more. Gas turbine according to claim 9 or 10, characterized in that the temperature of the combustion gas is 1,500 °C or more, the temperature of said combustion gas at the inlet of the first-stage blades is 1.300 °C or more, and the overall length of said first-stage blades is 200 mm or more, and the power generation capacity of said gas turbine is 50,000 KW or more. A combined power generation plant system comprising a gas turbine driven by the combustion gas which flows at a high speed, and exhaust heat recovery boiler to obtain steam from the combustion gas exhausted from said gas turbine, a steam turbine driven by said steam, and a power generator driven by said gas turbine and said steam turbine, wherein said gas turbine includes three or more-stages turbine blades (33), the temperature of said combustion gas at the inlet of the first-stage blades is 1,300 °C or more, the temperature of the exhausted combustion gas at the outlet of said turbine is 560 °C or more, the steam of 530 °C or more is obtained by said exhaust heat recovery boiler, said steam turbine is of a high-and-low pressure integrated type, the temperature or said steam fed to a first-stage blades or said steam turbine is 530 °C or more, the power generation capacity of said gas turbine is 50,000 KW or more, and the power generation capacity of said steam turbine is 30,000 KW or more, the total thermal efficiency is 45 % or more, the overall length or each of said first-stage blades being 200 mm or more, wherein the first-stage blades (33) are formed according to any one of the claims 1 to 8. Method for manufacturing a turbine blade for a gas turbine, which is formed of an integral casting and comprises a blade portion and a dovetail, wherein the method comprises the steps of: setting a mold for forming said blade on a water-cooled chill plate, heating said mold in a heating furnace to a predetermined temperature, melting a master ingot in a vacuum and pouring the molten metal in said heated mold, withdrawing the mold containing said molten metal from said heating furnace so as to solidify it successively from said blade portion toward said dovetail, thereby forming said blade portion of a single crystal structure, and subsequently withdrawing the mold at a higher speed than the withdrawal speed of the mold for said blade portion, thereby forming said root portion of a columnar grain structure. Method according to claim 13 characterized in that, the turbine blade is subjected to a solution heat treatment and to an aging heat treatment for precipitating γ'-phases in the γ-phase of the matrix.

Inventors: IIJIMA KATSUMI, KANO KIMIO, KOBAYASHI MITSURU, MATSUZAKI HIROYUKI, SAITO TOSIAKI, TAMAKI HIDEKI, WADA KATSUO, YOSHINARI AKIRA, IIJIMA, KATSUMI, KANO, KIMIO, KOBAYASHI, MITSURU, MATSUZAKI, HIROYUKI, SAITO, TOSIAKI, TAMAKI, HIDEKI, WADA, KATSUO, YOSHINARI, AKIRA
Applicants: HITACHI LTD, TOHOKU ELECTRIC POWER CO, HITACHI, LTD., TOHOKU ELECTRIC POWER CO., INC.
Application year: 1994
Main classification: B22D27
IPC codes: F01D5, C30B11, B22D27, C22C19