DEHYDROGENATION CATALYST HAVING IMPROVED MOISTURE STABILITY, AND PROCESS FOR MAKING AND USING THE CATALYST

Abstract: A calcined dehydrogenation catalyst comprising at least one sodium compound and one calcium compound was disclosed. The catalyst exhibits improved moisture stability as evidenced by improved crush strength and resistance to swelling and cracking.

Description: DEHYDROGENATION CATALYST HAVING IMPROVED MOISTURE STABILITY. AND PROCESS FOR MAKING AND USING THE CATALYST This invention relates to improved catalysts for the dehydrogenation of hydrocarbons to a method of making such catalyst compositions, and to use of such catalysts. The catalysts of this invention exhibit improved moisture stability when subjected both to contact with hydrogen and steam at elevated temperatures during the dehydrogenation process and to contact with moisture at a temperature less than 100°C. This improved stability is evidenced by improved crush strength and resistance to swelling and cracking. Catalytic dehydrogenation of hydrocarbons using various catalyst compositions has been known from just prior to World War II. Commercial examples are the manufacture of styrene and butadiene from ethylbenzene and butylene. Promoted iron oxide catalysts have been found to be especially useful in the dehydrogenation of alkyl aromatic hydrocarbons to vinyl aromatic hydrocarbons. Most commercial iron oxide dehydrogenation catalysts include minor amounts of promoters, for example, salts or oxides of chromium, manganese, bismuth, tungsten, or molybdenum, with chromium being preferred, together with a compound of potassium, for example, potassium oxide or carbonate. The potassium compound gives the catalyst a self-regenerative property that prolongs its useful life for long periods of time without significant loss of activity. Recent improvements include the incorporation of minor amounts of vanadium and modifiers, such as carbon black or graphite and methyl cellulose, which can beneficially affect the pore structures of the catalysts. The catalyst life of dehydrogenation catalysts is often dictated by the pressure drop across a reactor. An increase in the pressure drop lowers both the yield and conversion to the desired product. Physical degradation of the catalyst typically increases the pressure drop across the reactor. For this reason, the physical integrity of the catalyst is of major importance. Dehydrogenation catalysts containing iron oxide can undergo substantial changes under process conditions which decrease their physical integrity. For example, in the dehydrogenation of ethylbenzene to styrene, the catalyst is subjected to contact with hydrogen and steam at high temperatures (for example, 500°C to 700°C, more typically 540°C to 650°C) and, under these conditions, Fe 2 θ3, the preferred source of iron for the production of styrene catalyst, is reduced to Fe 3 0 4 . This reduction causes a transformation in the lattice structure of the iron oxide, resulting in catalyst bodies which have poorer physical integrity and are very susceptible to degradation by contact with water at temperatures below 100°C. This degradation by contact with water is characterized by the catalyst bodies (for example, pellets or granules) becoming soft and/or swollen and/or cracked. The water which contacts the catalyst may be in the form of liquid or a wet gas, such as air with a high humidity. "High humidity" refers to a relative humidity above 50 percent. The catalysts in styrene production plants are often exposed to temperatures below 100°C during start-ups, shutdowns, and upsets. Because large amounts of steam are used in styrene production, there is significant potential for exposing the catalyst to moisture at low temperatures. As previously discussed, this exposure causes physical degradation of the catalyst, which increases pressure drop across the reactor, resulting in decreased catalyst life. Williams et al. , US 5,023,225-A assigned to United Catalysts Inc., teach a predominately iron oxide, chromium oxide modified dehydrogenation catalyst made by first forming a blend (or coprecipitate) of chromium oxide or a salt of chromium and a yellow iron hydrate and heating the blend to convert the yellow iron hydrate to red iron oxide, thereby forming a chromium oxide modified iron oxide precursor. The precursor is then blended with four additional components and calcined to form the catalyst. The four additional components are: (a) alkali metal hydroxides, carbonates, or bicarbonates, preferably alkali metal oxides, that is, sodium or potassium oxide, with potassium oxide being most preferred, in an amount of from 5 to 15 percent by weight of the catalyst; (b) alkaline earth metal oxides or hydroxides, preferably alkaline earth metal oxides, that is, magnesium oxide, calcium oxide, or strontium oxide, with both MgO and CaO being preferred, in an amount of from 2 to 10 percent by weight of the catalyst; (c) oxides and salts of the cerium subgroup having atomic numbers of 57 to 62, preferably oxides of the cerium subgroup, with cerium oxide being preferred, in an amount of from 2 to 10 percent by weight of the catalyst; and (d) molybdenum or tungsten oxides and salts, preferably oxides of molybdenum or tungsten, with molybdenum oxide being preferred, in an amount of from 1 to 5 percent by weight of the catalyst. Catalysts with higher amounts of potassium have been used: Chu, US 4,503,163-A assigned to Mobil Oil Company, for example, discloses catalysts for the production of p-methylstyrene from p-ethyltoluene which contain, by weight, 30 to 60 percent, preferably 35 to 55 percent iron oxide calculated as ferric oxide; 13 to 48 percent, preferably 27 to 41 percent, a potassium promoter compound, calculated as potassium oxide; 0 to 5 percent, preferably 1 to 4 percent a chromium compound, calculated as chromic oxide; and 1 to 15 percent, preferably 2 to 10 percent a calcium compound, calculated as CaO. Such catalysts are self regenerative catalysts which perform well at lower steam to oil ratios; for example, ratios of less than 2:1 (by weight) . The economic advantages of using less steam are obvious. The problem with using higher concentrations of potassium is that the vulnerability of the used iron oxide catalyst to moisture increases with increasing potassium concentration. O'Hara, US 3,904,552-A assigned to Girdler Chemical Inc., teaches a dehydrogenation catalyst consisting essentially of no chromium oxide and containing (a) iron oxide, from 30 to 90 percent by weight; (b) a water gas promoter—preferably, and in the Examples exclusively, potassium carbonate—selected from the oxides, hydroxides, carbonates, and bicarbonates, of potassium, cesium, rubidium and sodium, in amounts of from 1 to 40 percent; (c) cerium oxide, from 0.5 to 10 percent by weight. (d) molybdenum oxide, from 0.5 to 5 percent by weight, and (e) an hydraulic cement, such as a Portland cement which, after calcination, contains calcium oxide or another compound not chemically combined with aluminum or silicon compounds and which is therefore available to exert an effect upon the physical properties of the iron oxide, in an amount of from 5 to 30 percent by weight of the total weight of the catalys . Turley et al . , US 3,703,593-A assigned to The Dow Chemical Company discloses preparation of a dehydrogenation catalyst prepared from a paste containing a mixture of hydrates (yellow) iron oxide and anhydrous (red) iron oxide in particular ratios that is. 0.25:1 to 0.85:1 and 1.86:1 to 4:1 by weight, as the iron oxide component, together with an oxide of an alkali metal, preferably potassium oxide or carbonate, chromium oxide or an alkali metal chromate or dichromate, a refractory cement binder (preferably 2.6 to 3 percent by weight of the paste) , and preferably, 5 to 15 weight percent methyl cellulose, and 5 to 15 weight percent graphite. Turley et al . teach their calcined catalyst contained, by weight, 50 to 90 percent Fe 2 0 3 , 0.5 to 5 percent Cr 2 0 5 , and 9 to 18 percent K 2 0. Moore, US 4,684,619- A assigned to The Dow Chemical Company, teaches preparing a dehydrogenation catalyst having improved moisture stability by calcining conventional catalyst components in two steps. The first step is a partial calcination at 250°C to 600°C for a time sufficient to oxidize and remove porosity controlling organic materials, for example 30 minutes to 4 hours depending on temperature. The second step is carried out at 700°C to 800°C for a time sufficient to convert carbonates present to the corresponding oxides, for example 10 to 60 minutes depending on the amount of C0 2 evolved and its rate of removal. A need exists for a dehydrogenation catalyst that has both high activity, selectivity and resistance to moisture. A way has now been discovered to enhance moisture resistance of these catalysts without any significant detrimental effects to catalyst performance. In one embodiment the present invention is a novel calcined dehydrogenation catalyst comprising (a) at least one iron oxide,- (b) at least one carbonate, bicarbonate, oxide or hydroxide of potassium and/or cesium,- (c) an oxide, carbonate, nitrate, or hydroxide of cerium, or a mixture of at least two thereof; (d) an hydraulic cement; (e) an hydroxide, carbonate, bicarbonate, acetate, oxalate, nitrate, or sulfate of sodium, in an amount sufficient to provide from 0.2 to 10 percent sodium, calculated as sodium oxide, by weight of the calcined catalyst; and (f) a carbonate, sulfate, or hydroxide, of calcium or a mixture of at least two thereof, in an amount sufficient to provide from 1.5 to 20 percent calcium, calculated as calcium oxide, by weight of the calcined catalyst. In a second embodiment, the invention is a process for preparing such improved dehydrogenation catalysts. This process comprises the steps of (A) preparing an extrudable mixture by admixing (a) at least one iron oxide; (b) a carbonate, bicarbonate, oxide or hydroxide of potassium or cesium, or a mixture of at least two thereof; (c) an oxide, carbonate, nitrate, or hydroxide of cerium, or a mixture of at least two thereof; and (d) an hydraulic cement; with sufficient water to form an extrudable mixture; (B) forming the extrudable mixture into pellets; and (C) calcining the pellets into a finished catalyst, characterized by including in the extrudable mixture, (e) an hydroxide, carbonate, bicarbonate, acetate, oxalate, nitrate, or sulfate of sodium, in an amount sufficient to provide from 0.2 to 10 percent sodium, calculated as sodium oxide, by weight of the calcined catalyst; and (f) a carbonate, sulfate, or hydroxide, of calcium or a mixture of at least two thereof, in an amount sufficient to provide from 1.5 to 20 percent calcium, calculated as calcium oxide, by weight of the calcined catalyst. The new catalyst compositions are useful for the dehydrogenation of an alkyl aromatic compound to form a vinyl aromatic compound by contacting the alkyl aromatic compound with the dehydrogenation catalyst under dehydrogenating conditions. The new catalysts have improved moisture stability, as evidenced by improved crush strength, which decreases catalyst degradation during process upsets. The invention resides in the discovery that the addition of sodium and calcium compounds to known dehydrogenation catalysts produce new dehydrogenation catalysts having improved stability. Thus, any of the known class of dehydrogenation catalyst compositions containing red or yellow iron oxides and various catalyst promoters (as disclosed, for example, in US 4,503,163; 3,703,593; and 4,684,619 may be used herein. Iron is generally added to the catalyst compositions of the invention as red iron oxide, Fe 2 θ3 # or yellow iron oxide, Fe 2 θ3»H 2 0. Particularly suited are pigment grades of red and yellow iron oxides. Likewise the catalyst promoter can be any potassium or cesium carbonate, bicarbonate, oxide or hydroxide or any mixture thereof taught by the art, that is converted to the corresponding oxide or oxides under calcination conditions. Potassium compounds are the preferred promoters. Potassium carbonate or a mixture of potassium carbonate with potassium oxide is most preferred. The catalyst compositions of the present invention also may contain, and preferably do contain, cerium to enhance selectivity. Cerium, if used in the catalyst compositions of the present invention, can be added to the catalyst in the form of cerium oxide or in the form of other cerium compounds that decompose upon calcination to form cerium oxide, as for example, cerium carbonate, cerium nitrate, cerium hydroxide or any combination thereof. The physical strength, activity and selectivity of the catalyst compositions of the present invention can be improved by adding certain binding agents. Binding agents can include and consist of hydraulic cements, for example, calcium aluminate or Portland cement. These cements can be added individually or in combination. The amount of sodium in the new catalyst, measured as sodium oxide and based on the weight of the calcined catalyst may range from 0.2 to 10 percent. Preferably sodium is present in the catalyst in the range of 0.5 to 5 percent. Most preferably, sodium is present in amounts of from 0.8 to 3 percent. The sodium may be added to the catalyst mixture as sodium hydroxide or carbonate or bicarbonate or other salts such as acetate, oxalate, nitrate, or sulfate. The amount of calcium in the new catalyst, measured as calcium oxide and based on the weight of the calcined catalyst, may range from 1.5 to 20 percent. Preferably calcium is present in the range of 3 to 15 percent. Most preferably calcium is present in amounts from 4 to 12 percent. Calcium can be added to the catalyst mixture in the form of calcium carbonate, calcium sulfate, calcium hydroxide, or other salts. Other known catalyst additives can be included in the catalysts of the invention, but are not essential. A chromium compound which can serve as a stabilizer for the active catalytic components is illustrative of an optional but preferred additive. Chromium compounds have previously been added to alkali-promoted iron oxide catalysts to extend their life. Chromium, as used in the compositions of this invention, can be added to the catalyst in the form of a chromium oxide or in the form of chromium compounds which decompose upon calcination to chromium oxides. Another optional component, used to improve the selectivity of the catalyst, is molybdenum which can be added as its oxide or as a molybdate. Other metal compounds that may be added as promoters include compounds of aluminum, vanadium, cobalt, cadmium, copper, magnesium, manganese, and nickel, providing they can be calcined to the corresponding metal oxide. The density of the catalyst composition can be modified by the addition of various filler substances, for example, combustible materials such as graphite and methyl cellulose. Such materials can be added to the compositions during preparation, but are burned out after the catalyst pellets have been formed during the calcining step. Porosity promoting aids can also facilitate extrusion of catalyst pellets. The catalyst components can be mixed in various ways known to the art. One method comprises ballmilling together a mixture of desired compounds, adding a small amount of water, and extruding the composite to produce small pellets, which are then dried and calcined. Another method is mixing the components together with water, drying them to form a powder and tabletizing and calcining the tablets. Another procedure involves mixing the components together with an excess of water, partially drying, and then subsequently extruding, drying, and calcining the resulting pellets. The choice of the mixing method depends on the preference of the skilled artisan. A preferred method of preparing the catalysts is to blend the catalyst ingredients together, including the ingredients of the present invention, in the presence of sufficient water to make a moist extrudable mixture. This mixture is then extruded to produce extrudates between 3.175 mm (1/8-inch) and 6.35 mm (1/4-inch) in diameter. The extrudates are then calcined under conventional calcining conditions. Calcination temperatures can range from 500°C to 900°C, preferably from 600°c to 800°C. After calcination the extrudates are ready for use as catalysts. The amounts of components (a)-(d) employed, as well as the amounts, if any, of optional components described herein, are not critical so long as they are present in ranges and relative proportions known in the art, which persons skilled in the art will be able to optimize readily to provide practical dehydrogenation catalysts the moisture stability of which can be improved based on the teachings herein. Example An extrudable mixture in the following examples were prepared from commercially available chemicals. LUMNITE is the trade name for calcium aluminate cement manufactured by Lehigh Cement Company. An extrudable mixture was made by blending in a heated steam jacketed blade mixer 135 grams(g) red iron oxide (Fe θ3), 153.4 g yellow iron oxide (Fe 2 θ3«H2θ) , 120 g calcium aluminate cement (LUMNITE), 38 g gypsum (CaS0 4 * »2H 2 0) , 120 g calcium carbonate (CaC0 3 ), 10 g molybdenum oxide (M0O3), 190.5 g hydrated cerium carbonate (Ce 2 (Cθ3)3»5H 2 0) , 450 g potassium carbonate (K Cθ3), 10 g potassium dichromate (K 2 Cr 2 0 7 ), and.41.5 g of an aqueous 50 percent solution of sodium hydroxide (NaOH) . 15 percent (wt) of water was then blended into the formulation. The mixture was mixed and dried in the heated steam jacketed mixer until the formula reaches a consistency suitable for extrusion. The hot extrudable mixture was transferred to a California Model CL-3 laboratory Pellet Mill and extruded (4 mm (5/32 inch) in diameter and 8 mm (10/32 inch) in length) . Four additional extrudates formulations were prepared according to the above procedure, but with different amounts of ingredients. Table 1 lists the formulations of Examples 1-5. The extrudates of Examples 1-5 were then calcined by slowly ramping the temperature to 775°C over a period of two hours, and maintaining at 775°C for 30 minutes. The finished compositions of the calcined catalysts, expressed as shown, are given in Table 2. TABLE 1 *A11 weights in grams TABM. 2 Components of Calcined Catalyst *Weight percent Comparative Runs 1 to 4 The same procedure employed in Examples 1-5 was used to make all the comparative catalysts. Table 3 lists the formulations of the extrudates for the comparative catalysts. Table 3 Comparative Extrudate Formulation *A11 weights in grams The finished compositions of the calcined comparative catalysts, expressed as shown, are given in Table 4. TABLE 4 Components of Calcined Comparative Catalysts *Weight percent The catalysts of the invention and those prepared for comparison were tested for activity and selectivity in the reaction for dehydrogenating ethylbenzene to styrene by placing 70 or 100 milliliters (ml) of the above calcined catalyst extrudates in a fixed bed reactor and passing a preheated mixture of steam and ethylbenzene at a weight ratio of 1.5:1 (called the steam to oil ratio) through the bed which was maintained at a temperature of 580 to 590°C. The LHSV (liquid hourly space velocity) was 1.0 and the pressure was maintained at atmospheric. The liquid hourly space velocity was a number denoting residence time in a reactor commonly used by those skilled in the art. After a minimum of 5 days, the weight ratio of steam to ethylbenzene was reduced to 1.2 and the bed temperature adjusted so that an ethylbenzene conversion of 50 percent was achieved. This temperature adjustment was continued each day until a constant conversion of 50 percent was achieved at a fixed bed temperature, that temperature being an indication of the activity of the particular catalyst; that is, the lower the temperature, the higher the activity. The results of the dehydrogenation reaction for Examples 1-5 and Comparative Runs 1-4 are shown in Table 5. TABLE 5 The moisture resistance of the used catalyst was measured by the following method. After approximately two to three weeks of operation, the catalyst was unloaded from the reactor and twenty randomly chosen extrudates were placed in a glass dish with a flat bottom. The extrudates were separated so that they do not touch each other. The glass dish was then placed in a controlled relative humidity chamber (Vapor-Temp Model No. VP-lOOAT-1) made by Blue M, a unit of General Signal, adjusted to 30°C and 70 percent relative humidity. After 20 hours the glass dish was removed from the humidity chamber. The excess water in the dish was removed, and the extrudates were placed in a drying oven at 150°C for 24 hours. The extrudates were removed and the average crush strength of the extrudates determined. Crush strength was a common physical measurement that indicates the strength of the catalyst body, that is, tablet, pellet, or extrudate. In this test, catalyst bodies were compressed between two flat metal surfaces or blocks, and the pressure required to crush the body was measured. A Comten crush strength machine, model no 922T-10- OP, serial no. 830202, was used according to the following procedure. The length of the extrudate was first measured, then the extrudate was crushed between the two blocks of the Comten unit and the pressure required to crush the extrudate was recorded. The crush strength per one-quarter inch length of extrudate was then calculated. This procedure was done on twenty randomly chosen extrudates from each catalyst sample which were all preconditioned as noted in the preceding paragraph. Averaged crush strength was expressed as "PSIG/0.25 inch". The average of these twenty measurements was shown in Table 6. The metric equivalent, kPa/cm, was calculated by multiplying by 10.858 and rounding. The data show the catalysts of this invention after exposure to operating conditions have a superior resistance to physical degradation upon contact with water at temperatures below 100°C than a catalyst prepared in the same manner except for the absence of at least one of the sodium compound or calcium compound, and exposed to substantially the same operating conditions. Table 6 Catalyst Average Crush Strength Physical Appearance PSIG/0.25 inch. kPa/cm Example 1 18.5 201 Hard, No Cracking or Swelling Example 2 18.0 195 Hard, No Cracking or Swelling Example 3 13.5 147 Hard, No Cracking or Swelling Example 4 15.5 168 Hard, No Cracking or Swelling Example 5 18.8 204 Hard, No Cracking or Swelling Comp. Ex. 1 less than 5 less than 54 Soft, Cracked, Swoll Comp. Ex. 2 less than 5 less than 54 Soft, Cracked, Swoll Comp. Ex. 3 less than 5 less than 54 Soft, Cracked, Swoll Comp. Ex. 4 6 65 Soft, Cracked, Swoll

Claims: CLAIMS: 1. A calcined dehydrogenation catalyst comprising a calcination product of (a) at least one iron oxide; (b) a carbonate, bicarbonate, oxide or hydroxide of potassium or cesium, or a mixture of at least two thereof; (c) an oxide, carbonate, nitrate, or hydroxide of cerium, or a mixture of at least two thereof; (d) an hydraulic cement; (e) an hydroxide, carbonate, bicarbonate, acetate, oxalate, nitrate, or sulfate of sodium, in an amount sufficient to provide from 0.2 to 10 percent sodium, calculated as sodium oxide, by weight of the calcined catalyst; and (f) a carbonate, sulfate, or hydroxide, of calcium or a mixture of at least two thereof, in an amount sufficient to provide from 1.5 to 20 percent calcium, calculated as calcium oxide, by weight of the calcined catalyst. 2. The calcined dehydrogenation catalyst of Claim 1 wherein (e) is sodium hydroxide and (f) is calcium carbonate. 3. The calcined dehydrogenation catalyst of Claim 1 containing from 0.5 to 5 percent sodium calculated as sodium oxide and from 3 to 15 percent calcium calculated as calcium oxide, by weight of the calcined catalyst. 4. The calcined dehydrogenation catalyst of Claim 1 wherein (b) is a carbonate, bicarbonate, oxide or hydroxide of potassium, or a mixture of at least two thereof. 5. The calcined dehydrogenation catalyst of Claim 4 wherein (b) is potassium carbonate or a mixture of potassium carbonate and potassium oxide. 6. The calcined dehydrogenation catalyst of Claim 5 wherein (c) is a carbonate of cerium; (d) is a calcium aluminate hydraulic cement; (e) is sodium hydroxide, in an amount so that the catalyst contains from 0.8 to 3.0 percent by weight sodium, calculated as sodium oxide; and (f) is a carbonate or sulfate of calcium or a mixture thereof, in an amount so that the catalyst contains from 4 to 12 percent by weight calcium, calculated as calcium oxide. 7. The calcined dehydrogenation catalyst of Claim 1 further comprising one or more oxides of chromium, molybdenum, aluminum, vanadium, cobalt, cadmium, copper, magnesium, manganese, or nickel . 8. A process for preparing a calcined dehydrogenation catalyst comprising: (A) preparing an extrudable mixture by admixing (a) at least one iron oxide; (b) a carbonate, bicarbonate, oxide or hydroxide of potassium or cesium, or a mixture of at least two thereof; (c) an oxide, carbonate, nitrate, or hydroxide of cerium, or a mixture of at least two thereof; (d) an hydraulic cement; (e) an hydroxide, carbonate, bicarbonate, acetate, oxalate, nitrate, or sulfate of sodium, in an amount sufficient to provide from 0.2 to 10 percent sodium, calculated as sodium oxide, by weight of the calcined catalyst; and (f) a carbonate, sulfate, or hydroxide, of calcium or a mixture of at least two thereof, in an amount sufficient to provide from 1.5 to 20 percent calcium, calculated as calcium oxide, by weight of the calcined catalyst, with sufficient water to form an extrudable mixture; (B) forming the extrudable mixture into pellets; and (C) calcining the pellets into a finished catalyst. 9. The process of Claim 8 wherein (e) is sodium hydroxide and (f) is calcium carbonate. 10. The process of Claim 8 containing from 0.5 to 5 percent sodium calculated as sodium oxide and from 3 to 15 percent calcium calculated as calcium oxide, by weight of the calcined catalyst. 11. The process of Claim 8 wherein (b) is a carbonate, bicarbonate, oxide or hydroxide of potassium, or a mixture of at least two thereof. 12. The process of Claim 11 wherein (b) is potassium carbonate or a mixture of potassium carbonate and potassium oxide. 13. The process of Claim 12 wherein (c) is a carbonate of cerium,- (d) is a calcium aluminate hydraulic cement; (e) is sodium hydroxide, in an amount so that the catalyst contains from 0.8 to 3.0 percent by weight sodium, calculated as sodium oxide; and (f) is a carbonate or sulfate of calcium or a mixture thereof, in an amount so that the catalyst contains from 4 to 12 percent by weight calcium, calculated as calcium oxide; and the finished catalyst has a superior resistance to physical degradation upon contact with water at temperatures below 100° C than a catalyst prepared in the same manner except that the conditions of at least one of (e) and (f) were not met. 14. The process of Claim 8 wherein one or more compounds of chromium, molybdenum, aluminum, vanadium, cobalt, cadmium, copper, magnesium, manganese, or nickel, as the respective oxide or calcinable to the respective oxide, is included in the extrudable mixture prepared in step (A) . 15. A process of dehydrogenating an alkyl aromatic compound to form a vinyl aromatic compound by contacting the alkyl aromatic compound with steam in the presence of a dehydrogenation catalyst which is a catalytically active product of calcining a mixture including (a) at least one iron oxide, (b) a carbonate, bicarbonate, oxide or hydroxide of potassium or cesium, or a mixture of at least two thereof, (c) an oxide, carbonate, nitrate, or hydroxide of cerium, or a mixture of at least two thereof, and (d) an hydraulic cement, characterized by employing as the dehydrogenation catalyst, the catalytically active product of calcining a mixture which includes, in addition to components (a) through (d) : (e) an hydroxide, carbonate, bicarbonate, acetate, oxalate, nitrate, or sulfate of sodium, in an amount sufficient to provide from 0.2 to 10 percent sodium, calculated as sodium oxide, by weight of the calcined catalyst; and (f) a carbonate, sulfate, or hydroxide, of calcium or a mixture of at least two thereof, in an amount sufficient to provide from 1.5 to 20 percent calcium, calculated as calcium oxide, by weight of the calcined catalyst. 16. The process of Claim 15 wherein (e) is sodium hydroxide and (f) is calcium carbonate. 17. The process of Claim 15 wherein the catalyst contains from 0.5 to 5 percent sodium calculated as sodium oxide and from 3 to 15 percent calcium calculated as calcium oxide, by weight of the calcined catalyst. 18. The process of Claim 15 wherein (b) is a carbonate, bicarbonate, oxide or hydroxide of potassium, or a mixture of at least two thereof. 19. The process of Claim 18 wherein (b) is potassium carbonate or a mixture of potassium carbonate and potassium oxide. 20. The process of Claim 19 wherein (c) is a carbonate of cerium,- (d) is a calcium aluminate hydraulic cement; (e) is sodium hydroxide, in an amount so that the catalyst contains from 0.8 to 3.0 percent by weight sodium, calculated as sodium oxide; and (f) is a carbonate or sulfate of calcium or a mixture thereof, in an amount so that the catalyst contains from 4 to 12 percent by weight calcium, calculated as calcium oxide. 21. The process of Claim 20 wherein one or more compounds of chromium, molybdenum, aluminum, vanadium, cobalt, cadmium, copper, magnesium, manganese, or nickel, as the respective oxide or calcinable to the respective oxide, is included in the mixture calcined to form the catalyst. 22. The process of any one of Claim 15 through 19 wherein the alkyl aromatic compound is ethylbenzene and the vinyl aromatic compound is styrene. 23. The process of any one of Claim 15 through 22 wherein the catalyst is reused after both (i) prior exposure of the catalyst to hydrogen and steam at dehydrogenation reaction conditions and (ii) subsequent to such prior exposure, contact of the catalyst with water at a temperature below 100 a C.

Inventors: DELLINGER PHILLIP W, MOORE REBECCA G, SHERROD FRED A, SMITH ALLEN R, DELLINGER, PHILLIP, W., MOORE, REBECCA, G., SHERROD, FRED, A., SMITH, ALLEN, R.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1994
Main classification: B01J23
IPC codes: B01J23, B01J27, B01J37, C07C5, C07C15