Liquid crystal devices

Abstract: A liquid crystal device wherein the liquid crystal material is a siloxane-containing compound characterised by the the general formula wherein R is a C₁₋₁₀ alkyl or each R' is a C₁₋₄ alkyl, T is X is an alkyl or halogen-substituted alkyl group having at least one chiral centre, Y is F, m is 0, 1 or 2 and n is 10, 11 or 12. Also claimed is a device wherein the liquid crystal material is disposed between a pair of substrates.

Description: This invention relates to devices containing liquid crystal oligomeric siloxane materials. Polymeric liquid crystals consisting of a siloxane backbone and a mesogenic portion are known, see for example E.P. 029 162 which discloses the preparation of such polymers by the addition of a polysiloxane having silicon-bonded hydrogen atoms to vinyl-substituted mesogenic molecules. More recently chiral smectic liquid crystal materials having ferroelectric properties have been described, see for example JP 01144491 which discloses materials containing in which Me represents methyl, R represents an optically active alkyl or aralkyl group, m = 0 to 5 and n = 2 to 10. Desirable properties of ferroelectric liquid crystals include a low viscosity and a relatively high tilt angle which is also substantially independent of temperature. Low viscosities are related to reduced response times and are advantageous when a dye is to be incorporated into the liquid crystal material. A high tilt angle is advantageous with regard to the electro-optic properties of the liquid crystal. In a device based on birefringence effects the tilt angle is normally 22.5° whereas devices incorporating dyes require an angle greater than this for good optical contrast. Measurements of the tilt angle of liquid crystal materials of the kind disclosed in JP 01144491 have shown not only a variation from polymer to polymer but also a reduction of the tilt angle with increasing temperature. We have now surprisingly discovered that a certain narrowly defined group of oligomeric liquid crystal materials exist as neat compounds or in mixtures which exhibit relatively high tilt angles and that such angles are substantially independent of temperature over a broad temperature range including ambient. Accordingly this invention provides a liquid crystal device wherein the liquid crystal material is a siloxane-containing compound having the general formula wherein R represents an alkyl group having from 1 to 10 carbon atoms or the group each R' represents an alkyl group having from 1 to 4 carbon atoms, T is X represents an alkyl or halogen-substituted alkyl group having at least one chiral centre, Y represents a fluorine atom, m has a value of 0, 1 or 2 and n has a value of 10, 11 or 12. In the general formula of the liquid crystal material employed according to this invention R represents an alkyl group having from 1 to 10 carbon atoms, for example methyl, propyl, hexyl or decyl, and each R' may be methyl, ethyl, propyl or butyl. Preferably R' is methyl. The group X may be for example -CH(CH 3 )-C 2 H 5 , -CHClCH(CH 3 )C 2 H 5 or -CHClCH(CH 3 )CH 3 . The pref-erred compounds are those wherein n has a value of 11. Such preferred compounds are believed to be novel and are included per se within the scope of this invention. The liquid crystal materials employed according to the invention may be prepared by the addition of the appropriate unsaturated mesogen to the disiloxane RR' 2 SiOSi(R') 2 H. The addition may be performed employing conventional hydrosilylation techniques, for example in the presence of a platinum catalyst. The device according to this invention may be of any type which relies on the use of a smectic or ferroelectric liquid crystal material for its operation. An example of such a device is illustrated in Figure 1 of the accompanying drawings which is a schematic cross-sectional view. The siloxane-containing crystal material (17) is interposed between a pair of substrates (10) which may be constructed of glass or a suitable polymer. The inner surfaces are coated with a transparent conducting film (12, 13) of indium tin-oxide and aligning agent (14, 15). Such surface aligning agents are known to those practiced in the art. Spacers (16) define the film thickness of between 1 and 100µm and these may be polymeric films, photo-etched or glass fibre beads. The conducting film may cover the whole inner surface of the substrate or may be etched into a suitable pattern, for example a dot matrix or a seven segment display. Regions of the film may then be addressed by electrical fields to display information as required. These fields can be applied externally to the electrodes using suitable waveforms or internally using thin film transistor devices. Equally magnetic fields or thermal addressing using a suitably focused light source, including a laser, may be used to alter the appearance of the device. Appropriate optics and a beam steering system may be used to move the focus around to different regions of the film as to write information thereupon. Polarising films (19, 20) may be incorporated, if required, to observe the information. The chiral smectic structure of the liquid crystal materials employed in this invention and non-racemic mixtures incorporating them exhibit ferroelectric properties. When these materials are included in a device of the type described by Figure I fast electro-optic switching on the microsecond to millisecond time scales can be produced. In this phase the lamellar layers are aligned perpendicular to the substrate so that on application of an external field the molecules switch from one tilt angle at + to that at - as described in the literature. The initial field free planar alignment in which the molecules align on average parallel to the substrate is achieved using a polymer alignment layer. The polarisers are aligned crossed with each other but with one polariser polarisation direction aligned parallel to either +  or - . On application of the field the material switches to the opposite  state and the device transmits light due to the birefringent nature of the siloxane-containing liquid crystal materials. On removal of the electric field the alignment is retained. Chiral or non-chiral pleochroic dyes may be incorporated into the liquid crystal material whereby only one polariser may be required. The dye aligns in the same direction as the liquid crystal molecules at + or - . Thus in one alignment state, say +, the dye absorbs the polarised light whilst in the other alignment state, say - , the absorption is highly reduced. Thus the dyed chiral smectic material may be used in colour switches. In a further embodiment two dyed devices may be used in combination to give a colour switch that does not require external polarisers. Virtually any combination of colour may be achieved and the dyed devices act as switchable polarisers. The switched states are stable. In yet a further embodiment the dye may be absorbing and fluorescent leading to a bright display utilising one or no polarisers. For the polarisation direction aligned parallel to the absorption direction, say at +, the fluorescence is bright whereas for the absorption direction non-parallel to the polarisation direction the absorption and hence the fluorescence is decreased. This gives an optical coloured switch that is fast, bright and in which the switched states are stable. The input polariser may equally be replaced by a switchable polariser of the type described above. Close to the chiral smectic A to chiral smectic C phase transition the liquid crystal materials employed according to the invention have been seen to switch in a fashion known as electroclinic. In this mode a tilt angle is induced that is proportional to the applied field allowing its use in fast modulators or grey scale devices. This electroclinic switching is fast, depending on the field applied, but is not bistable. The effect may be enhanced using dichroic or fluorescent dyes. The compound was prepared in its chiral (C*) form by the addition of pentamethyldisiloxane to 4-[(S)-2-methylbutanoyloxy]phenyl-4'-(9-decenyloxy)benzoate in the presence as catalyst of a complex formed between chloroplatinic acid and tetramethyldisiloxane. The electro-optic properties, tilt angle (), spontaneous polarisation (Ps) and response times (T) were measured in cells with 3µm spacers with rubbed polyimide alignment layers deposited on indium-tin oxide electrodes (5mm x 5mm). The cell was cooled at 1°C per minute in the presence of 5Vµm -1 AC field at 100 Hz to give good planar uniform alignment of the liquid crystal compound. The aligned cell showed good optical switching in the presence of reverse polarity pulsed DC fields. Tilt angles were measured as a function of temperature for an applied continuous square wave field of 10Vµm -1 at 0.1 Hz and a probing wave length of 632.8mm. The results are shown in Figure 2 from which it can be seen that the tilt angle is virtually independent of temperature at a value of approximately 36°C. The spontaneous polarisation was measured via the current pulse technique using an applied triangular wave with a peak field of 10Vµm -1 . The Ps value at 25°C was 17nCcm -2 . At 20°C the square wave response time to 10Vµm -1 was approximately 210µs.

Claims: A liquid crystal device wherein the liquid crystal material is a siloxane-containing compound characterised by the the general formula wherein R represents an alkyl group having from 1 to 10 carbon atoms or the group each R' represents an alkyl group having from 1 to 4 carbon atoms, T is X represents an alkyl or halogen-substituted alkyl group having at least one chiral centre, Y represents a fluorine atom, m has a value of 0, 1 or 2 and n has a value of 10, 11 or 12. A device as claimed in Claim 1 further characterised in that each R' is methyl. A device as claimed in Claim 1 or Claim 2 further characterised in that R represents an alkyl group having from 1 to 6 carbon atoms. A device as claimed in any one of the preceding claims further characterised in that n = 11. A device as claimed in any one of the preceding claims further characterised in that it comprises a pair of substrates having the liquid crystal material disposed between the substrates.

Inventors: COLES HARRY JAMES, COLES, HARRY JAMES
Applicants: DOW CORNING, UNIV MANCHESTER, DOW CORNING LIMITED, THE VICTORIA UNIVERSITY OF MANCHESTER
Application year: 1994
Main classification: C09K19
IPC codes: C09K19, G02F1, C07F7