Two-component composition for aqueous paint

Abstract: A resinous composition for two-liquid type water paint crosslinkable at the normal temperature which has a long pot life and which is superior in properties such as hardness, gloss, solvent resistance and water resistance is disclosed. A resinous composition comprises: (A) a colloidal dispersion or emulsion obtained by copolymerizing a monomer mixture comprising a carbonyl group-containing unsaturated monomer, carboxyl group-containing unsaturated monomer and other unsaturated monomers to form a copolymer, neutralizing the copolymer with an alkali, dissolving or emulsifying it into water, and adjusting the pH to above 7; and (B) an easily water soluble dihydrazide compound having from 1 to 5 carbon atoms.

Description: This invention relates to a resinous composition for two-liquid type water paint crosslinkable at normal temperatures, by which paint film having superior hardness, physical properties, gloss, solvent resistance, water resistance and the like can be formed. Disadvantages of the paint film obtained from an emulsion paint are that it shows tackiness at a high temperature state, and that its solvent resistance and initial water resistance before sufficient fusing of particles are poor. In order to improve these properties, it is generally known to introduce a carbonyl group and crosslink by adding dihydrazide as a crosslinking agent. As one method to utilize such emulsions, a process is disclosed in EP-A- 0 300 378 and in Japanese Laid-open Patent No. 4-372674/1992 wherein a carbonyl group is introduced into emulsion particles and the surfaces of the emulsion particles are controlled skillfully without contact with the crosslinking agent in the paint state, to obtain a one liquid type paint. Furthermore, an improved method is disclosed in Japanese Laid-open Patent No. 5-98071/1993 wherein a part of the emulsion is treated to be soluble and whereby contactability and water resistance are improved. However, in the processes to form a paint film by using the emulsion made by emulsion polymerization together with such surfactants to fuse particles, the properties of the paint film such as hardness, physical properties, gloss, solvent resistance and the like which are equivalent to those of a solvent type two-liquid resinous composition for urethane paints cannot be obtained. In order to obtain such properties, it is necessary to use resins such as a colloidal dispersion obtained by dispersing a polymer having a hydrophilic portion into water or a dispersive emulsion, wherein the main action of film formation is a crosslinking reaction. In such cases, there cannot be obtained one-liquid type paint by using the above mentioned particles because of non-clear particle states, and it unavoidably becomes a two-liquid type paint. It is an object of this invention to obtain a resinous composition for paint crosslinkable at normal temperatures which exhibits the equal hardness, physical properties, gloss, a solvent resistance and water resistance equivalent to those of a solvent type two-liquid urethane paint even as an aqueous resinous composition. Applicants have studied the crosslinking reaction between carbonyl group and dihydrazide in a disperse type aqueous resin for the purpose of forming a resinous composition for paint based on a resinous composition for a two-liquid type water paint having properties equal to the solvent type two-liquid paint. The first aspect of the present invention is a resinous composition for two-liquid type water paint crosslinkable at the normal temperature, which comprises (A) a colloidal dispersion or emulsion (referred simply to as "emulsion (A)" hereinafter) obtained by copolymerizing a monomer mixture comprising from 5 to 40% by weight of a carbonyl group-containing unsaturated monomer, from 1 to 20% by weight of a carboxyl group-containing unsaturated monomer from 5 to 40% by weight of an alkylester monomer of methacrylic acid having 9 to 30 carbon atoms and from 5 to 89% by weight of other unsaturated monomers to form a copolymer, neutralizing the copolymer with an alkali, dissolving or emulsifying it into water, and adjusting pH value above 7, as well as (B) from 0.05 to 1.0 mole equivalent (based on the carbonyl group content contained in the said emulsion (A)) of readily water soluble dihydrazide compound (hereinafter referred to as "dihydrazide compound") having from 1 to 5 carbon atoms. The second aspect of the present invention is the resinous composition for two-liquid type water paint crosslinkable at the normal temperature according to the first aspect, wherein the copolymer to form particles of the emulsion (A) has a number average molecular weight of 500 - 150,000. The hydrazide compound (B) is one or two compounds selected from the group consisting of those expressed by the general formula (1) and (2) below: (n=0 to 3), as well as malonic dihydrazide, maleic dihydrazide, itaconic dihydrazide and fumaric dihydrazide. The third aspect of the present invention is the resinous composition for two-liquid type water paint crosslinkable at normal temperatures, wherein the hydrazide compound (B) is either (1) or (2) above. The invention is based on the following three novel findings. (1) In order to obtain the objective of good properties, it is necessary to increase the crosslinking density and thus increase the amount of a crosslinking agent. As a result, the crosslinking reaction proceeds faster and pot life becomes too short, but the time of the pot life can be controlled by increasing pH value upwardly. (2) By using adipic dihydrazide as is conventionally used in this field, the surface gloss is lost when dried in the case of large amounts of it being used. This tendency is strong particularly in a high pH range, but it can be solved by using a specific strong hydrophilic dihydrazide. (3) The dispersive type emulsion (A) used in the inversion may include long chain monomers of higher alkylesters of methacrylic acid having 9 to 30 carbon atoms (hereinafter referred to as "long chain monomer"). By including the long chain monomer in the dispersive emulsion (A), water resistance and adhesion capability by means of entanglement of long chain monomer which is the hydrophobic component of the paint coating, even though the paint coating contains plenty of hydrophilic component. The emulsion (A) used in the invention is prepared by copolymerizing a mixture of a carbonyl group-containing unsaturated monomer, a carboxyl group-containing unsaturated monomer, the long chain monomer and other unsaturated monomers or the mixture excluding the long chain monomer by means of any known polymerization method such as solution polymerization or bulk polymerization, to obtain a polymer, neutralizing the polymer with an alkali, and dissolving or dispersing it into water. The said emulsion (A) is different considerably in molecular weight of the polymer which is to constitute the emulsion particles front the emulsion formed by an emulsion polymerization method using a surfactant. For example, the number average molecular weight is advantageously within a range of 500 - 150,000, preferably 1,000 - 80,000 in order to obtain a stable emulsion. On the other hand, the number average molecular weight prepared by an emulsion polymerization method is generally 150,000 - 1,000,000, and furthermore those having higher molecular weight are also included, wherein a part becomes a gel. As the carbonyl group-containing monomer used in synthesis of the emulsion according to the invention, there may be mentioned acrolein, diacetone acrylamide, diacetone methacrylamide, formyl styrol, vinyl alkyl ketones having 4 - 7 carbon atoms (such as vinyl methyl ketone, vinyl ethyl ketone, vinyl butyl ketone), diacetone acrylate, diacetone methacrylate, acetonitrile acrylate, 2-hydroxypropyl acrylate acetyl acetate, butane diol 1,4-acrylate acetyl acetate, acryl (or methacryl) oxyalkyl propenal, acetoacetoxyethyl methacrylate and acetoacetoxyethyl acrylate. Particularly preferable are diacetone acrylamide and diacetone methacrylamide which are easily controllable in their reaction rates by means of pH. The amount used thereof is 5 - 40% by weight, preferably 7 - 30 % by weight, more preferably 10 - 25% by weight. The carboxyl group-containing monomers are monomers generally used in the synthesis of water-soluble resins, and include for example acrylic acid, methacrylic acid, itaconic acid and maleic acid. The amount used thereof is 1 - 20% by weight, preferably 2 - 10% by weight. Further, the long chain monomer of the present invention as a copolymerizing component is used to improve water resistance of the paint coating and adhesion capability of the coating on a metal surface adhered after the metal surface is dipped into water. As the long chain monomer, methacrylic acid of higher alkyl ester having 9 to 30 carbon atoms is used. The hydrophobic side chains of the long chain monomer are entangled enough with each other to remarkably increase the water resistance of the paint coating. Further, the long chain monomer has a strong hydrophobic property which prevents copolymerization, and may not normally be introduced into an emulsion for emulsion polymerization in which a surfactant is used. However, in accordance with the present invention, the long chain monomer may be copolymerized by means of the solution polymerization, and the resultant copolymer may easily become an emulsion by means of neutralization by alkali and water dispersion. The long chain monomer is an alkyl ester having C 9 to C 30 of methacrylic acid, preferably C 12 to C 26 and more preferably C 16 to C 22 . For example, nonyl methacrylate (C 9 ), decyl (C 10 ), undecyl (C 11 ), dodecyl (lauryl) (C 12 ), tridecyl (C 13 ), hexadecyl (C 16 ), heptadecyl (C 17 ), octadecyl (stearyl) (C 18 ), eicocyl (C 20 ) or behenyl (C 22 ) may be used. The content of the long chain monomer is 5 to 40% by weight. The other monomers to be copolymerized with the above mentioned three monomers include, for example, styrene, acrylic or methacrylic esters with side-chains having 1 to 8 carbon atoms, acrylonitrile, butadiene, vinyl toluene, methacrylonitrile, vinyl acetate, vinyl chloride, vinylidene chloride and olefins. The amount used thereof is 5 to 89% by weight, preferably 20 to 80% by weight. The dihydrazide compound (B) used as a crosslinking agent according to the invention should have sufficient water-solubility. The carbodihydrazide is expressed by the following chemical formulae: (n=0 to 3). Furthermore, there is mentioned malonic dihydrazide, maleic dihydrazide, itaconic dihydrazide and fumaric dihydrazide. Preferably, n=0 or 1 in the above-mentioned formula, and carbodihydrazide is preferable. The amount used thereof is 0.05 to 1 mole equivalent based on carbonyl group content (0.1 to 2 as functional group ratio), preferably 0.1 to 0.6 and more preferably 0.15 to 0.5 mole equivalent. The neutralizing agent used in the invention is ammonia, a low molecular weight amine or an alkali metal. The pH value of the emulsion (A) is adjusted above 7, preferably 8 to 11. It is more preferably 8.5 to 10.5. If the amount of the crosslinking agent used in the invention is less than the above-mentioned range, the desired properties thereof are less effectively obtained, but even if too much, the effect is relatively small. If the pH value is below 7, the reaction proceeds too fast to shorten the pot life. The invention has developed a resinous composition for two-liquid type water paint crosslinkable at the normal temperature, but crosslinking can be carried out more thoroughly by heating. During paint forming, pigments, extenders, thickeners, and other conventional additives are added. Furthermore, adhesives and the like may be applied. The invention is illustrated in more detail by the following examples. Comparative Example 1 150 parts by weight of ethylene glycol monobutyl ether was introduced into a 2 liter flask, heated to 110°C, and substituted by nitrogen, and the following mixture was added dropwise for 1 hour: Acrylic acid 10 parts by weight Diacetone acrylamide 30 parts by weight Butyl acrylate 50 parts by weight Styrene 30 parts by weight Methyl methacrylate 29 parts by weight Allyl methacrylate 1 part by weight Azobisisobutyronitrile 3 parts by weight After the end of addition, it was kept at 110°C for 30 minutes, and then the following mixture was added dropwise for 1 hour: Diacetone acrylamide 30 parts by weight Butyl acrylate 55 parts by weight Styrene 33 parts by weight Methyl methacrylate 32 parts by weight Azobisisobutyronitrile 1.5 parts by weight. One hour and one hour-and-half after the end of addition, 0.5 parts by weight of azobisisobutyronitrile was added, the mixture was kept 110°C for further 2 hours, then cooled to 70°C, and 14 parts by weight of triethylamine was added, 500g of deionized water was added with stirring, to obtain an aqueous solution having high viscosity. The pH value thereof was 8.6. The number average molecular weight calculated from the result of gel chromatography was 13,800. To 50 parts by weight of the solution, 10 parts by weight of deionized water and 0.8 parts by weight carbodihydrazide were added. The solution was shown in Table 1 respectively. After the retention period, the solution was coated on the treating plate, dried for 3 days, and thereafter the painting properties were tested. The results are shown in Table 1. Hours/Days after Adding Carbodihydrazide Mixing Properties of Three Days After Painting Film thickness (µm) Pencil Hardness Solvent Resistance Erichsen Value Gloss Immediately after 20 2H ○ 7 mm < ○ 2 hours after 19 2H ○ 7 mm < ○ 6 hours after 18 2H ○ 7 mm < ○ 1 day after 18 2H ○ 7 mm ○ - 2 days after (Thickened) 21 H ○ - 5 mm ○ Solvent resistance was obtained by rubbing with a cloth moistened with xylene for 10 times and observing the change. In the case that 1.6 parts by weight or 0.8 parts by weight of adipic dihydrazide was added, there was no gloss observed. "○" in table 1, as well as tables below, shows that satisfactory results have been obtained. Comparative Example 2 150 parts by weight of propylene glycol monoethyl ether was introduced into a 2 liter flask, heated to 110°C, and substituted by nitrogen, and the following mixture was added dropwise for 2 hours: Acrylic acid 10 parts by weight Diacetone acrylamide 60 parts by weight Butyl acrylate 105 parts by weight Styrene 65 parts by weight Methyl methacrylate 60 parts by weight Azobisisobutyronitrile 9 parts by weight. After the end of addition, it was kept at 110°C for 30 minutes, and 30 minutes and 1 hour after, 0.5 parts by weight of azobisisobutyronitrile was added respectively, kept at 110°C for 2 hours, cooled, and then 14 parts by weight of triethylamine and 50 parts by weight of isopropanol were added, stirred thoroughly, and thereafter 600g of deionized water was added dropwise. The aqueous solution was concentrated to solid content of 36% under a decreased pressure, to obtain an aqueous solution having pH of 8.8. The number average molecular weight calculated from the result of gel chromatography was 6,529. Test results of the painted film obtained by using 50 parts by weight of the solution and blending carbodihydrazide shown in Table 2 are also shown in Table 2. Carbodihydrazide (Parts by weight) Film thickness (µm) Water resistance 2 hrs. submerged Gloss Pencil hardness 0.8 20 ○ - ○ 2H 0.6 21 ○ ○ H - 2H 0.4 19 ○ - ○ F Tests were carried out 2 days after painting. The results of Erichsen test were determined after 7 days, and for that wherein 0.6 parts by weight of carbohydrazide being added, the result was 7mm. Comparative Example 3 150 parts by weight of propylene glycol monoethyl ether was introduced into a 2 liter flask, heated to 110°C, and substituted by nitrogen, and the following mixture was added dropwise for 2 hours: Acrylic acid 10 parts by weight Diacetone acrylamide 90 parts by weight Butyl acrylate 70 parts by weight Butyl methacrylate 65 parts by weight Styrene 65 parts by weight Azobisisobutyronitrile 9 parts by weight After the end of addition, it was kept at 110°C, and 30 minutes and 1 hour after, 0.5 parts by weight of azobisisobutyronitrile was added respectively, kept at 110°C for 2 hours, cooled, and then 14 parts by weight of triethylamine and 50 parts by weight of isopropanol were added, stirred thoroughly, and thereafter 450g of deionized water was added dropwise. The aqueous solution was concentrated to solid content of 45.1% under a decreased pressure to obtain an aqueous solution having pH of 8.66. The number average molecular weight calculated from the result of gel chromatography was 7,274. To 40 parts by weight of the solution, 0.12 parts by weight of carbohydrazide was added, and after 40 minutes, the paint film coated on the treating plate expressed the following properties: Film thickness 25µm Water resistance (2 hours after submerged into water) ○ Gloss ○ Pencil hardness 2H Erichsen test value 5mm Comparative Example 4 300 parts by weight of propylene glycol monoethyl ether was introduced into a 2 liter flask, heated to 110°C, and substituted by nitrogen, and the following mixture was added dropwise for 2 hours: Acrylic acid 60 parts by weight Diacetone acrylamide 60 parts by weight Butyl acrylate 90 parts by weight Methyl methacrylate 90 parts by weight Azobisisobutyronitrile 9 parts by weight. After the end addition, it was kept at 110°C, and after 1 hour and 2 hours, 1 part by weight of azobisisobutyronitrile was added respectively, kept at 110°C for 2 hours, cooled, and then 84 parts by weight of triethylamine was added, and 300g of demineralized water was added, to obtain an aqueous solution having pH of 10.50. The number average molecular weight calculated from the result of gel chromatography was 15,050. 1 part by weight of carbohydrazide was added to 50 parts by weight of the solution to form a product useful for 3 hours. Hardness of the paint film with paint thickness of 23µm was 2H after 7 days. Comparative Example 5 Polymerization was carried out analogously to Example 4, and after cooled, 25 parts by weight of triethylamine was added with stirring, and then 300 parts by weight of deionized water was added, to obtain an aqueous solution with pH of 6.12. The number average molecular weight calculated from the result of gel chromatography was 15,050. 1 part by weight of carbodihydrazide was added to 50 parts by weight of the aqueous solution to form a product, which was gelled after 5 minutes. Example 1 270 parts by weight of propylene glycol monoetyl ether was introduced into a 5 liter separable flask, heated to 110°C, and substituted by nitrogen, and the following mixture was added dropwise for 1.5 hours: Acrylic acid 31.5 parts by weight Diacetone acrylamide 270.0 parts by weight Styrene 180.0 parts by weight Stearyl methacrylate 270.0 parts by weight n-butyl methacrylate 343.5 parts by weight n-butyl acrylate 30.0 parts by weight i-butyl methacrylate 225.0 parts by weight PER-BUTYL-O 2.7 parts by weight (PER-BUTYL-O is a polymerization initializing agent provided by Nippon Oil and Fats Co., Ltd.) After the end of addition, PER-BUTYL-O was added dropwise again for 2 hours. Further, it was kept heated for 4 hours, and then 54 parts by weight of triethylamine was added with stirring well to the resultant material above. Then 1575 parts by weight of water was added with stirring, to have the mixture emulsionized. The emulsion obtained through reduced-pressure distillation had 48.4% of solid content, 0.12µm of particle diameter, (4.6 Pa.s) viscosity (46 Poise) (measured by a B type viscosity meter at 20°C and 60rpm, the same condition of which was used below) and 8.97 pH value. Example 2 An emulsion was obtained by the same method of example 1, with the monomers below: Acrylic acid 31.5 parts by weight Diacetone acrylamide 270.0 parts by weight Styrene 270.0 parts by weight Stearyl methacrylate 270.0 parts by weight n-butyl methacrylate 508.5 parts by weight The emulsion obtained had 47.8% of solid content, 0.17µm of particle diameter, (3.3 Pa.s) viscosity (33 Poise) and 9.01 pH value. Example 3 An emulsion was obtained by the same method of example 5, using 2 liter flask in lieu of 5 liter one, in the one third scale. The monomers used are as follows: Acrylic acid 10.5 parts by weight Diacetone acrylamide 90.0 parts by weight Styrene 60.0 parts by weight Stearyl methacrylate 45.0 parts by weight n-butyl methacrylate 94.5 parts by weight n-butyl acrylate 75.0 parts by weight i-butyl methacrylate 75.0 parts by weight The emulsion obtained had 46.7% of solid content, 0.08µm of particle diameter, (4 Pa.s) viscosity (40 Poise) and 9.01 pH value. Example 4 An emulsion was obtained by the same method of example 1, with the monomers below: Acrylic acid 31.5 parts by weight Diacetone acrylamide 270.0 parts by weight Styrene 180.0 parts by weight BLENMER SLMA 270.0 parts by weight (BLENMER SLMA is a synthesized lauryl methacrylate provided by Nippon oil and Fats Co., Ltd.) Stearyl methacrylate 270.0 parts by weight n-butyl methacrylate 508.5 parts by weight n-butyl acrylate 30.0 parts by weight i-butyl methacrylate 225.0 parts by weight PER-BUTYL-O 2.7 parts by weight The emulsion obtained had 48.2% of solid content, 0.11 µm of particle diameter, (4.8 Pa.s) viscosity (48 Poise) and 9.00 pH value. Comparative Example 6 An emulsion was obtained by the same method of example 1, with the monomers below: Acrylic acid 31.5 parts by weight Diacetone acrylamide 270.0 parts by weight n-butyl methacrylate 283.5 parts by weight n-butyl acrylate 30.0 parts by weight Styrene 180.0 parts by weight i-butyl methacrylate 225.0 parts by weight The emulsion obtained had 42.8% of solid content, 0.08 µm of particle diameter, (3.59 Pa.s) viscosity (35.9 Poise) and 9.22 pH value. 0.4 mole equivalent amount of carbohydrazide as to the amount of carbonyl group contained in each of the emulsions of examples 1 to 4 and Comparative Example 6 (0.8 mole equivalent amount of carbohydrazide as to the amount of functional group of the emulsion) was added to each of the emulsions of examples 1 to 4 and Comparative Example 6, and viscosity of each of the emulsions was adjusted by adding water. The resultant emulsions were coated with a bar coater on a treatment panel for checking the coating properties. The results are shown in Table 3. Characteristics of Coating Seven Days After Painting Example 1 2 3 4 Comparative 6 Thickness of Coating (µm) 23 30 26 27 23 Pencil Hardness 2H 2H 2H 2H 2H Anti- solubility ○ ○ ○ ○ ○ Erichsen Value (µm) 7 mm < 7 mm < 7 mm < 7 mm < 7 mm < Gloss ○ ○ ○ ○ ○ Water Resistance (submerged into water) 1 Month OK 1 Month OK 1 Month OK 1 Week OK 12 Hours OK Note: Tests could not be achieved for those samples which were left aside for one day after hydrazide was added. Obviously from the examples, the resinous composition for paint obtained by adding an easily water soluble dihydrazide compound with 1 - 5 carbon atoms to a emulsion having pH adjusted above 7 with an alkali has long pot life, and provides paint film having superior properties such as hardness, gloss, solvent resistance, water resistance and the like.

Claims: A resinous composition for two-liquid type water paint cross-linkable at the normal temperature, comprising: a colloidal dispersion or emulsion containing a carbonyl group and being obtained by copolymerising a monomer mixture comprising from 5 to 40% by weight of a carbonyl group-containing unsaturated monomer, from 1 to 20% by weight of a carboxyl group-containing unsaturated monomer, from 5 to 40% by weight of an alkyl ester monomer of methacrylic acid having 9 to 30 carbon atoms and from 5 to 89% by weight of other unsaturated monomers to form a copolymer, neutralising the copolymer with an alkali, dissolving or emulsifying it into water, and adjusting pH above 7; and a readily water soluble dihydrazide compound having from 1 to 5 carbon atoms selected from the group consisting of those expressed by the general formula (1) and (2) of: (n=0 to 3), malonic dihydrazide, maleic dihydrazide, itaconic dihydrazide and fumaric dihydrazide, in an amount of 0.05 to 1.0 mole equivalent based on the carbonyl group content contained in the emulsion. A resinous composition according to claim 1, wherein said emulsion contains particles formed by the copolymer which has a number average molecular weight of 500 - 150,000. A resinous composition according to claim 1, wherein the hydrazide compound is: or

Inventors: NAKAYAMA YASUHARU, NISHIDA REIJIRO, NAKAYAMA, YASUHARU, NISHIDA, REIJIRO
Applicants: KANSAI PAINT CO LTD, KANSAI PAINT CO. LTD.
Application year: 1994
Main classification: C09D133
IPC codes: C09D133, C08F8, C08K5