MULTILAYER FILM HAVING SELF-LIMITING HEAT SEAL

Abstract: The present invention relates generally to a multilayer packaging structure which: (1) has a relatively broad heat seal temperature, and (2) provides an easy open seal, even at very high heat seal temperatures. More specifically, the films of the present invention are preferably multilayer structures comprising: (1) a support film, such as polyester; (2) a homopolymer or copolymer interface layer; and (3) a heat seal outer layer.

Description: MULTI-LAYER FILM HAVING SELF-LIMITING HEAT SEAL Field of the Invention The present invention relates generally to multilayer packaging structures which: 1. have a relatively broad heat seal temperature, and 2. provide an easy open seal, even at very high heat seal temperatures. More specifically, the films of the present invention are preferably multilayer structures comprising: 1. a support film, such as polyester; 2. an olefinic (homopolymer or copolymer) interface layer, such as olefinic polymer (including olefinic copolymers); and 3. a heat seal outer layer. Background of The Invention Poly vinylidene chloride ("PVDC") coated polyester films are known and are often used as heat-sealable packaging films. However, halogenated films and coatings are increasingly coming under environmental attack and are being subjected to increasing government regulation. One possible solution to these problems is to replace the PVDC heat seal coating with other heat seal compositions. However, many heat seal compositions can be problematic. For example, copolyesters generally have a relatively narrow heat sealing range: 1. below this range the packaged product may have a tendency to leak; and 2. above this range, the packaged film can be difficult to open. The present invention is an innovative solution to the above problems. SUMMARY OF THE INVENTION Overview The present invention is directed to a novel and improved multilayer film comprising: 1. heat seal layer; 2. non-acrylic interface layer; and 3. a support layer. Once a heat sealing temperature is applied, the film's peel strength is advantageously limited by the interface layer. Hence, the film can be used in a wide range of heat seal applications, and the resulting heat seal will be effective in protecting the product but not so strong as to frustrate consumers as they attempt to open the package. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT AND BEST MODE Support Layer The support layer can be virtually any material capable of carrying the interface layer and heat-seal layer without interfering with the intended function of those two layers. The preferred support layer comprises polyester, most preferably biaxially oriented poly(ethylene terephthalate) ("oriented PET'). Useful polyester films of the present invention can be manufactured from various thermoplastic polyester resins, such as: 1. polyethylene terephthalate, 2. polytetramethylene terephthalate, 3. polyethylene, 2,6-napthalate, 4. poly-l,4-cyclohexylene dimethyl terephthalate, 5. and the like Polyester copolymers may also be used, such as: 1. polyethylene terephthalate/ isophthalate, 2. polyethylene terephthalate/adipate, 3. polyethylene terephthalate/sebacate, 4. polyethylene terephthalate/sulphoisophthalate, 5. polyethylene terephthalate/azelate, 6. and the like. Biaxially oriented polyethylene terephthalate homopolyester is preferred. The polyester films of the present invention can be manufactured by an extrusion process, such as a cast film or blown film process. In a cast film process, the polyester resin is first heated to a molten state and then extruded through a wide slot die in the form of an amorphous sheet. The sheet-like extrudate is rapidly cooled or "quenched" to form a cast sheet of polyester by contacting and traveling partially around a polished, revolving casting drum. Alternatively, the extrudate can be blown in a conventional blown film process. Regardless of the process however, the polyester sheet is preferably uni-axially or biaxially (preferably biaxially) stretched in the direction of film travel (machine direction) and/or perpendicular to the machine direction (transverse direction), while being heated to a temperature in the range of from about 80° C. to 160° C, preferably about 90° C. to 100° C. The degree of stretching may range from 3.0 to 5.0 times the original cast sheet unit dimension, preferably from about 3.2 to about 4.2 times the original cast sheet dimension. Interface Layer The interface layer is preferably derived from an olefinic homopolymer or copolymer composition. Preferred such compositions include acid copolymers, particularly ethylene/acrylic acid and ethylene/methacrylic acid, and acid copolymers wholly or partially neutralized with a cation, such as sodium or zinc (also called "ionomers"), low density polyethylene ("LDPE"), linear low density polyethylene ("Ϊ . DPE"), ultra low density polyethylene ("ULDPE") polyvinyl esters and carboxylic acid derivatives of polyvinyl esters. The most preferred polyvinyl ester is ethylene vinyl acetate ("EVA"), polyvinylacetate ("PVA") and copolymers thereof. Suitable EVA polymers include those having EVA contents ranging from about 5 to 50 weight percent EVA incorporation. As the vinyl acetate content increases, clarity improves and low-temperature flexibility, stress- crack resistance and impact strength all generally increase; on the other hand, there generally is an accompanying decrease in softening and sealing temperatures, as well as barrier properties. Above about 50% by weigh vinyl acetate incorporation, the material is generally completely amorphous. The EVAs of the present invention are advantageous, because of their flexibility, toughness (even at low temperatures), adhesion characteristics and stress-crack resistance. Other compositions having similar such features could be appropriate according to the present invention, depending upon the particular end use. EVAs are made by the copolymerization of ethylene and vinyl acetate. Most often, this free radical polymerization (initiated by either a peroxide or perester) is done in a conventional stirred autoclave or a high pressure tubular reactor. The acetate side chain brings polarity to the EVA resin. As polarity increases, tackiness generally also increases, as well as, adhesion to a variety of substrates and solubility in common solvents. As the molecular weight of EVAs increases, so does melt viscosity, heat seal strength, toughness, flexibility, stress-crack resistance, and hot tack strength. Preferred melt index of the EVAs of the present invention range from about 2 dg/min to over 500 dg/min. Molecular weight can be controlled by the addition of chain transfer agents, such as propylene or isobutylene during polymerization. The EVAs of the present invention should be processed at relatively low temperatures, since acetoxy bonds tend to break and acetic acid is formed at temperature above about 450PF. Support Layer + Interface Layer The interface layer is preferably applied to the support layer by conventional coating techniques. Prior to coating the polyester film surface, the film may be surface-treated in any conventional manner, depending upon the particular application and performance required from the final product. Electric corona discharge is a conventional surface treatment which is commonly performed on polyester films to enhance the film's surface qualities, especially its adhesive and printing properties. Electric corona discharge methods and apparatus are described in U.S. Pat. Nos. 3,057,792 and 4,239,973. For uniaxially oriented film, the corona treatment followed by the coating may occur during the in-line manufacturing process, either before stretch orientation or after. If the corona treatment and coating occurs before stretch orientation, heating the film before stretch orientation will generally be necessary to drive off the coating solvent. The polyester sheet can be coated with the interface layer using any of the well known coating techniques. For example, the film may be coated by roller coating, spray coating, gravure coating, slot coating, or extrusion coating preferably gravure or roller coating. The heat applied to the film during the subsequent preheating, stretching, and heat-setting stages is generally sufficient to evaporate the coating solvent. The coated, oriented polyester film may then be heat treated for a period of time necessary to crystallize the film. Crystallization imparts dimensional stability and good tensile properties to the polyester film. Oriented polyethylene terephthalate film may be heat-set at a temperature ranging from 190° C. to 240° C, preferably from 21^ C. to 23- C. The coated crystalline, oriented polyester film is generally then wound into a roll. An alternative to this on-line process is to coat the film off-line (after manufacture of the film is complete). Off-line operations can be conducted by a secondary facility, such as a converter, who obtain intermediate films and further processes it for specific customers. The two layers can also be coextruded. Preferred coextrusion methods include tubular-blown film processes and flat die, chill-roll casting processes. Both such processes are well known, conventional co-extrusion processes. Heat Seal Coating The preferred heat seal coating is a copolyester. The preferred copolyester component of the present invention is derived from at least the following components: (I), about 10-60 mole % terephthalic acid (hereafter, monomer "A") (II). about 10-60 mole % ethylene glycol (hereafter, monomer "B"); and (III), about 5-60 mole % of third monomer being a secondary di-acid (hereafter, monomer "C") and/or a secondary diol (hereafter, monomer "D"), wherein: 1. the intrinsic viscosity of the final copolyester composition is preferably in the range of about 0.5-1.0, more preferably 0.58-0.8; and 2. the glass transition temperature of the final composition is less than about 100° C, more preferably, less than about 80 C, and most preferably less than about 7^C. Examples of monomer C include: 1. succinic acid, 2. adipic acid, 3. azelaic acid, 4. sebacic acid, 5. 1,10 decanedicarboxylic acid, 6. phthalic acid, 7. isophthalic acid, 8. dodecanedioic acid, 9. methoxypolyalkylene glycol 10. neopentyl glycol, 11. propylene glycol, 12. 1,4 butane diol, 13. trimethylene glycol 14. propylene glycol, 15. tetramethylene glycol, 16. hexamethylene glycol, 17. diethylene glycol, 18. and the like. Preferred such comonomers include azelaic and isophthalic. Support Layer + Interface Layer + Heat Seal Layer The heat seal layer is preferrably applied to the interface layer in a solution coating process similar to the coating process for applying the interface layer to the support layer. Such solution coating processes are well known and any conventional such process can be used. EXAMPLE 1 Support Layer: biaxially oriented polyethylene terephthalate, 0.5 mil thickness (hereafter, SUPPORT LAYER) 1. Interface Layer: an EVA polymer from Morton International sold under the trademark "ADCOTEX 17." (hereafter, "INTERFACE MATERIAL 1"); and 2. an EVA supplied by Pierce & Stevens sold under the trademark "PROXMELT E4020" (hereafter, "INTERFACE MATERIAL 2") Heat Seal Layer: 1. 49002PT copolyester available from Morton International which is believed to be the polymerization product of ethylene glycol with a diacid composition comprising about 45 mole% azealaic acid and about 55 mole% terephthalic acid (hereafter, "COPOLYESTER A"), and 2. VTTEL 1200™ available from Shell Chemical which is believed to be the polymerization product of ethylene glycol with diacid composition comprising about 45 mole % isophthalic acid and 55 mole % terephthalic acid (hereafter, "COPOLYESTER B") CONTROL FILM: a 50/50 weight blend of COPOLYESTER A and COPOLYESTER B was solution coated onto the SUPPORT LAYER in an amount of about 0.5 gram copolyester per square meter of support layer. SAMPLE 1: the SUPPORT LAYER was solution coated with the INTERFACE MATERIAL in an amount of about 0.4 grams INTERFACE MATERIAL 1 per square meter of SUPPORT LAYER; thereafter the interface coating was solution coated with the copolyester material used in the CONTROL in an amount of 0.8 grams copolyester per square meter. SAMPLE 2: was substantially the same as SAMPLE 1, except that about 0.5 grams of INTERFACE MATERIAL 2 (per square meter of SUPPORT LAYER) was substituted for INTERFACE MATERIAL 1 and the copolyester top coating was in an amount of about 0.6 grams per square meter. The target coating weight for each layer in each sample was 0.5 grams/m2. Equipment The coating equipment used 12 inch wide feed rolls, coating rolls, and a drying tower at about 104 C (220° F) (counter-current air drying). The interface coating solutions were about 7.5 to about 15 weight percent solids in a 23/77 wt.% ratio tetrahydrofuran/toluene solution at 50PC temperature. The copolyester coating solutions were about 10 to about 20 weight percent solids in a tetrahydrofuran solution comprising about 1.5 weight percent fillers, waxes, stabilizers and the like at about 50°C. An 11 inch wide PET film was fed into the coating bath at about 50 feet per minute, and a dwell time during drying of about 0.2 minutes. Results: Each of the multi-layer films was heat sealed (coated side-to-coated side) at temperatures ranging from about 100-200° C. A multiple of three sealed samples for each film were tested at each condition as a reproducibility check. The average results are shown below: Film Average Heat Seal Strength (g/in. (a 0.25 sec- 1 & 5 psig? 100° C 12QPC 140PC 160PC 18QPC 2Q(PC CONTROL 142 217 247 312* 267* 370* SAMPLE 1 242 208 182 207 227 160 SAMPLE 2 -- 123 88 170 125 123 dwell time 2 - pressure • Sealed sample films tore when heat seals were pulled apart. Peel strengths above about 50 g/inch are generally sufficient to seal a package for typical use, and seals having peel strengths above about 250 g/inch are generally rather difficult for an average consumer to pull apart. SAMPLES 1 and 2 indicate excellent heat seal performance over a wide seal temperature range. The seal strength values of the control film were a strong function of heat seal temperature and seals were stronger than desired over the higher temperature range.

Claims: WHAT IS CLAIMED IS: 1. A multilayer film comprising: a) heat seal layer; b) an olefinic polymer or copolymer interface layer; and c) a support layer, whereby the bond strength between (i) the interface layer; and (ii) the support layer or the heat seal layer; less than the bond strength between two heat seal layers which have been heat sealed together. 2. The multilayer film of Claim 1, wherein upon heating said film above its heat sealing temperature, the resulting heat seal of the entire film defines a peel strength of less than about 250 g/inch over a broad heat seal temperature range. 3. The film of Claim 2 wherein the support layer comprises oriented polyethylene terephthalate. 4. The film of Claim 3 wherein the interface layer is derived from a vinyl ester or the acid derivative of a vinyl ester. 5. The film of Claim 3 wherein the interface layer comprises ethylene vinyl acetate. 6. The film of Claim 4 wherein the heat seal layer is derived from terephthalic acid and ethylene glycol and one or more diacids or diols other than terephthalic acid and ethylene glycol. 7. The film of Claim 4 wherein the heat seal layer is a blend of polyesters or copolyesters.

Inventors: CHANG CLIFFORD CHENG-SHIOU, CHANG, CLIFFORD, CHENG-SHIOU
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1994
Main classification: B32B27
IPC codes: B32B27, B65D65, C08J7