Olefin resin-based articles having gas barrier properties

Abstract: An olefin resin-based article having good gas barrier properties is disclosed, comprising an α,β-ethylenically unsaturated carboxylic acid-grafted polyolefin (e.g., maleic anhydride-grafted polypropylene) having formed thereon an inorganic oxide deposite film, wherein the grafted polyolefin has an unsaturated carboxylic acid unit concentration of from 0.01 to 10% by weight, with or without an anchor coat being provided between the grafted polyolefin and the inorganic oxide film. The article suffers from no reduction in gas barrier properties even when heat or stress is applied thereto and is therefore useful as a wrapping or packaging material in the production of pouch-packed foods and IC packages.

Description: This invention relates to an olefin resin-based article having excellent gas barrier properties which is useful in packaging applications, such as in the protection of foods and electronic components. BACKGROUND OF THE INVENTION The packaging of foods, electronic components, and other oxygen sensitive entities in a film or a container which suppresses oxygen permeation has been proposed for protecting the packaged contents from oxidation, thereby maintaining the quality of the contents for a prolonged period of time. For example, JP-B-53-12953 (the term "JP-B" as used herein means an "examined published Japanese patent application") and JP-A-4-353532 (the term "JP-A" as used herein means an "unexamined published Japanese patent application") disclose a transparent flexible plastic film with low permeability to gases and moisture. This film is made of a flexible plastic film, such as polyethylene terephthalate, cellophane, nylon, polypropylene or polyethylene, having a thickness of from 5 to 300 µm and a transparent thin layer of a silicon compound represented by the general formula Si x O y (wherein x is 1 or 2; and y is 0, 1, 2 or 3) formed on at least one side thereof in a thickness of from 100 to 3,000 Å. JP-A-63-237940 discloses a transparent film having gas barrier properties made from the above-mentioned flexible plastic film with a metal oxide layer on at least one side thereof. The metal oxide layer comprises an oxide of at least one metal selected from the group consisting of In, Sn, Zn, Zr and Ti and is formed by sputtering. Additionally, a transparent heat-sealable resin film is provided thereon. Further, JP-A-3-218828 discloses a packaging material made from a low molecular weight polypropylene film with an SiO 2 deposite layer on at least one side thereof. When a film material made of a resin which has a polar group, such as a hydroxyl group, a carboxyl group or an amino group, therein, for example, polyethylene terephthalate, nylon or cellophane, is used in the above products, sufficient adhesion to the inorganic oxide films (i.e., the Si x O y and metal oxide layers) is obtained and the gas barrier properties provided are satisfactory, showing an oxygen permeability of from 0.5 to 8 cc/m 2 ·atm·day. When the above-mentioned inorganic oxides are deposited on the surface of a resin-based article comprising a non-polar olefin resin, such as polypropylene or polyethylene resins having an oxygen permeability of from 1,800 to 3,000 cc/m 2 ·atm·day, the gas barrier properties can be increased to an oxygen permeability of from 5 to 40 cc/m 2 ·atm·day. However, the inorganic oxide layers tend to become easily detached from the olefin resin upon the application of external stress or heat to the article. This detachment is primarily due to inadequate adhesion between the non-polar resin-based article and the deposited inorganic oxide. Such a situation occurs particularly in cases where a heat sealable layer is laminated on the oxide-coated non-polar resin article, when the laminated article (having a heat sealable layer) is fabricated into final form for bag making or cover sealing, when the bag is used, when the container made of the film is filled, or when the container and contents are sterilized, such as in the production of pouch-packed foods. When detachment of the oxide layer occurs, the oxygen permeability increases to 200 to 400 cc/m 2 ·atm·day, and the practical utility of the article is severely decreased. Database WPI, AN 83-731544 describes a laminate comprising (a) a plastic layer, (b) a thin layer consisting of tin oxide and metal and/or metallic oxide (except forr tin oxide), and (c) a layer of carboxylated polyolefin; preferably the thin layer is formed on the plastic by vacuum deposition or sputtering. The laminate is described as having improved adhesive strength between plastic and polyolefin. SUMMARY OF THE INVENTION An object of the present invention is to provide a resin-based article having good gas barrier properties comprising an olefin resin-based article having an inorganic oxide deposited thereon, wherein the inorganic oxide deposit is prevented from detachment during fabrication or use, thereby maintaining good gas barrier properties. Subject matter according to the present invention is an olefin resin-based article having good gas barrier properties according to claim 1. Preferred embodiments thereof are subject matter of claims 2 and 3. Further subject matter of the present invention is the use of the olefin resin-based article according to the invention in packaging applications. In the present invention, the modified polyolefin is a maleic anhydride-grafted polypropylene resin which exhibits firm adhesion to the inorganic oxide deposit film owing to its carboxyl group (-COOH). According to the present invention, an anchor coat is provided between the modified polyolefin and the inorganic oxide deposite film. The adhesion between the modified polyolefin and the inorganic oxide deposit film is enhanced by both the carboxyl group of the modified polyolefin and the anchoring effect of the anchor coat. When the inorganic oxide deposited on the modified polyolefin has a thickness of from 50 to 400 Å, the deposit film is so dense that the gas barrier properties are greatly improved. DETAILED DESCRIPTION OF THE INVENTION The modified olefin resin which can be used in the present invention as a base material is obtained by graft polymerization of a maleic anhydride to a polypropylene resin. Graft polymerization can be carried out for example, by a process comprising melt-kneading a polypropylene resin, a maleic anhydride monomer, and a catalyst in an extruder (see JP-B-43-27421 and JP-B-59-15127) or by a process comprising adding a maleic anhydride monomer and a catalyst, e.g., benzoyl peroxide or t-butyl perbenzoate, to a polypropylene dissolved in an appropriate solvent, e.g., toluene or xylene, and heating the mixture with stirring (see JP-B-44-15422 and JP-B-52-30546 both incorporated herein by reference). Any graft polymerization method known in the art can be used to produce the invention modified olefin resin. A propylene homopolymer is used preferably from the standpoint of transparency. A combination of propylene with at least one of ethylene, 1-butene, 4-methyl-1-pentene, and 3-methyl-1-butene is also used. When using two or more α-olefins in combination, the α-olefins may be distributed randomly or in blocks. The terminology "block copolymer" as hereinafter used has the following meanings. To take an instance, a "block copolymer comprising homopolymer blocks of monomer A and random copolymer blocks of monomers A and B" includes not only a block copolymer which is built up through chemical bonding of homopolymer blocks of monomer A and random copolymer blocks of monomers A and B to form a structure of A···A-AABABAAAAB··· but a blend of polymers containing (i) a copolymer built up through chemical bonding of homopolymer blocks of monomer A and random copolymer blocks of monomers A and B and (ii) a homopolymer of monomer A, (iii) a random copolymer of monomers A and B or a combination of (ii) and (iii). Similarly, a "block copolymer comprising polymer blocks a and b " includes not only polymers with blocks a and b chemically bonded to each other but a polymer blend containing (i) a block copolymer comprising chemically bound polymer blocks a and b , and (ii) a polymer solely comprising polymer blocks a and/or (iii) a polymer solely comprising polymer blocks b . Therefore, the terminology "block copolymer" has the same meaning as when referring to polymers synthesized with a Ziegler-Natta catalyst. Maleic anhydride is grafted onto the polypropylene resin or the resin comprising the above combination of polypropylene with another monomer. If desired, the modified polypropylene resin may be diluted with an unmodified olefin resin until the unsaturated maleic anhydride unit concentration of the diluted resin falls within the range of from 0.01 to 10% by weight, and preferably from 0.1 to 5% by weight. If the maleic anhydride unit concentration is less than 0.01% by weight, sufficient adhesion to an inorganic oxide film cannot be obtained. If it exceeds 10% by weight, no further improvement in adhesion is produced. Besides, a polypropylene-based resin tends to undergo degradation. It will follow that the polypropylene-based resin has an increased proportion of low-molecular weight components, resulting in a reduction of bonding power. The modified polypropylene resin, either as such or as diluted with an unmodified olefin resin, has an MFR (JIS K-7210) usually of from 0.1 to 100 g/10 min, and preferably of from 0.5 to 20 g/10 mm, from the viewpoint of moldability in extrusion, injection, vacuum forming and compression molding. Articles which can be formed from the modified polypropylene resin include films, sheets, containers, and cases. These articles may be obtained by conventional processes, such as extrusion, injection molding, vacuum forming, and blow molding. The molded maleic anhydride-grafted polypropylene articles may have a laminate structure composed of the modified polypropylene resin and a thermoplastic resin, such as polyethylene, polypropylene, an ethylene-vinyl acetate copolymer, polyamide, polybutylene terephthalate, polyethylene terephthalate, polyphenylene sulfide, polyphenylene ether or polycarbonate. The films or sheets may be subjected to stretching. It is preferable that the polypropylene resin film or sheet on which an inorganic oxide layer is to be deposited is uniaxially or biaxially stretched. Stretching makes the surface of the film or sheet more smooth and reduces the maximum surface roughness, thereby improving adhesive strength to an inorganic oxide deposit film and minimizing any reduction in gas barrier properties of the resulting composite film after fabrication. The article made from the modified polypropylene resin preferably has a Bekk's surface smoothness (JIS P-8119) of 20,000 sec or more, preferably from 40,000 to 100,000 sec, and a maximum surface roughness (R max ) (JIS B 0601-1982) of not more than 1 µm, preferably not more than 0.5 µm, and more preferably from 0.01 to 0.4 µm. Such surface properties of the article can be provided by, for example, avoiding use of (or at least minimizing the amount of) compounding additives which would form fine projections on the surface of the molded article, such as nucleating agents (e.g., talc and silicon oxide) and lubricants (e.g., zinc stearate and calcium stearate) or by giving a mirror finish to the cavity wall of the mold with an aluminum-plated surface or to the die lip of an extrusion die. The films of the invention usually have a thickness of from 5 to 200 µm. The sheets usually have a thickness of from 200 to 1,500 µm. Small containers or cases usually have a wall thickness of from 300 to 2,500 µm. Tanks or 20 ℓ-volume chemical storage vessels usually have a wall thickness of from 1 to 10 mm. If desired, the molded articles may be subjected to an oxidation treatment prior to being overcoated, such as a corona discharge treatment, an ozone treatment, a glow discharge treatment, a plasma treatment, or a treatment with a chemical. It is preferable to first provide an anchor coat (also termed a "primer coat") on the surface of the molded article to improve the adhesion of the inorganic oxide deposite film, before application of the inorganic oxide deposite film. Known anchoring agents, such as polyisocyanate compounds, polyurethanes, polyesters, polyethylene-imines, alkyl titanates, can be used for formation of an anchor coat. Preferred anchoring agents are polyisocyanate compounds, polyurethanes, urethane prepolymers or mixtures thereof or reaction products thereof, and mixtures of a polyester polyol or a polyether polyol and a polyisocyanate compound. These anchoring agents are applied in an amount usually of from 0.01 to 0.5 g/m 2 , and preferably of from 0.1 to 0.3 g/m 2 , on a solid weight basis. In the present invention, an inorganic oxide is deposited on the surface of the maleic anhydride-modified polypropylene molded article or on an anchor coat provided thereon to form an inorganic oxide deposite film. Preferred oxygen permeabilities of the invention article are from 0.1 to 20 cc/m 2 ·atm·day. The inorganic oxide deposite film is formed of SiO x , SnO x , ZnO x , IrO x , etc. (where x is from 1 to 2) to a thickness of from 200 to 4,000 Å, preferably from 300 to 3,000 Å. The thickness of the inorganic oxide film is decided by transparency, deposition rate, gas barrier properties, and take-up properties of the film. Deposition methods for applying the inorganic film include a method in which an inorganic oxide is deposited on the molded article made of the maleic anhydride-grafted polypropylene in vacuo (1 x 10 -3 to 1 x 10 6 Torr) in a vacuum deposition apparatus utilizing a high-frequency induction heating system (see JP-B-53-12953 incorporated herein by reference) and a method in which a gas stream containing an organosilicon compound, oxygen and an inert gas is generated in a vacuum deposition apparatus which has been evacuated and a plasma is then generated in the gas stream by a magnetron glow discharge to deposit SiO x on the molded article in the vacuum deposition apparatus (see JP-A-64-87772 and U.S. Patents 4,557,946 and 4,599,678 all incorporated herein by reference). Additionally, various deposition methods which may be used in the preparation of the article of the present invention are described in KOGYO ZAIRYO , Vol. 38, No. 14, pp. 104-105 (Nov., 1990) incorporated herein by reference under the classifications of ion plating, high-frequency plasma CVD, electron beam (EB) deposition, and sputtering. The present invention will now be illustrated in greater detail with reference to Examples, the present invention is not limited thereto. All the percents are by weight unless otherwise specified. The maximum surface roughness (R max ) and the center-line average surface roughness (R a ) of the films prepared were measured with a three-dimensional center-line roughness meter "SE-3AK" and an analyzer "Model SPA-11" both manufactured by Kosaka Kenkyusho. SYNTHESIS EXAMPLE Preparation of Catalyst-on-Carrier: To a flask thoroughly purged with nitrogen was added 100 mℓ of dehydrated and deoxidized n-heptane, 0.1 mol of magnesium chloride and 0.20 mol of titanium tetrabutoxide, followed by allowing the mixture to react at 100°C for 2 hours. The temperature was lowered to 40°C, and 15 mℓ of methyl hydrogen polysiloxane was added thereto and reacted for 3 hours. After completion of the reaction, the solid component produced was washed with n-heptane. Composition analysis on an aliquot of the solid component revealed a Ti content of 15.2% and an Mg content of 4.2%. Into a flask thoroughly purged with nitrogen was charged 100 mℓ of dehydrated and deoxidized n-heptane, and 0.03 mol, converted to an Mg atom, of the above-prepared solid component was added thereto. To the flask was further introduced 0.05 mol of silicon tetrachloride at 30°C over a period of 15 minutes, and the mixture was allowed to react at 90°C for 2 hours. After completion of the reaction, the reaction mixture was washed with purified n-heptane. A mixture of 25 mℓ of n-heptane and 0.004 mol of o-C 6 H 4 (COCℓ) 2 was added to the reaction mixture at 50°C, and 0.05 mol of silicon tetrachloride was then added thereto, followed by allowing the mixture to react at 90°C for 2 hours. After completion of the reaction, the reaction mixture was washed with n-heptane to obtain a catalyst component having a Ti content of 2.05%. Preparation of Olefin Copolymer (1): In a 10 ℓ autoclave thoroughly purged with propylene were charged 3.3 ℓ of n-heptane, and 1.0 g of triethylaluminum, 0.44 g of diphenyldimethoxysilane, and 0.7 g of the above-prepared catalyst-on-carrier were added thereto in this order. To the autoclave was fed 800 Nmℓ of hydrogen, and propylene was then introduced under pressure to a final inner pressure of 0.5 kg/cm 2 G. The mixture was stirred at 50°C at that pressure. Thereafter, 700 mℓ of 7-methyl-1,6-octadiene was added thereto, the temperature was elevated while introducing propylene under pressure to a final inner pressure of 5.5 kg/cm 2 G, and the mixture was kept at 65°C under that pressure for 5 hours to conduct polymerization. The catalyst was inactivated with n-butanol, the residual catalyst was extracted with water, and the copolymer was recovered by centrifugation and dried to obtain 1940 g a dry powder having a bulk density of 0.50 g/cc and an amorphous polymer content of 54 g. The copolymer had an MFR (measured at 230°C, 2.16 kg load; hereinafter the same) of 2 g/10 min, a density of 0.895 g/cm 3 , a crystallinity of 42%, and a modulus of elasticity of 8,100 kg/cm 2 . The 7-methyl-1,6-octadiene unit concentration was 2.7 mol% as analyzed by H 1 -NMR. The diene monomer unit formed no chain and had a 1,2-addition structure. Preparation of Olefin Copolymer (2): A random copolymer comprising 96.7 mol% of propylene and 3.3 mol% of 1,4-hexadiene was prepared in the same manner as for olefin copolymer (1), except for replacing 7-methyl-1,6-octadiene with 1,4-hexadiene. Olefin copolymer (2) had an MFR of 2 g/10 min, a density of 0.903 g/cm 3 , a crystallinity of 36%, and a modulus of elasticity of 5,500 kg/cm 2 . Preparation of Modified Olefin Resin (1): To 100 parts of a propylene homopolymer powder (MFR: 2 g/10 min; density: 0.905 g/cm 3 ) were added 0.8 part of benzoyl peroxide, 1.2 parts of maleic anhydride, and 0.2 parts of silicon oxide, and the mixture was mixed in a Henschel mixer. The mixture was extruded into strands from an extruder at a temperature of 220°C, cooled with water, and cut to pellets. The resulting pellets were dissolved in boiling xylene and re-precipitated with a large quantity of acetone. The solid was analyzed by infrared spectrophotometry. As a result, the grafted maleic anhydride unit concentration in the modified polypropylene was 0.7%. Preparation of Modified Olefin Resin (2): To 100 parts of a propylene homopolymer powder (MFR: 2 g/10 min; density: 0.905 g/cm 3 ) were added 0.8 part of benzoyl peroxide and 1.2 parts of maleic anhydride, and the mixture was mixed in a Henschel mixer. The mixture was extruded into strands from an extruder at a temperature of 220°C, cooled with water, and cut to pellets. The grafted maleic anhydride unit concentration in the modified polypropylene was 0.7% as measured in the same manner as described above. Preparation of Modified Olefin Resin (3): To 100 parts of an ethylene-propylene random copolymer powder (ethylene content: 5%; MFR: 1 g/10 min; density: 0.89 g/cm 3 ) were added 0.8 part of benzoyl peroxide and 1.2 parts of maleic anhydride, and the mixture was mixed and extruded to obtain pellets in the same manner as for modified olefin resin (1). The grafted maleic anhydride unit concentration in the modified polypropylene was 0.9% as measured in the same manner as described above. Preparation of Modified Olefin Resin (4): A graft copolymer having an MFR of 2.2 g/10 min and a maleic anhydride unit concentration of 1.0% was prepared in the same manner as for modified olefin resin (1), except for replacing the propylene homopolymer with olefin copolymer (1) (propylene/7-methyl-1,6-octadiene copolymer). Preparation of Modified Olefin Resin (5): A graft copolymer having an MFR of 2.1 g/10 min and a maleic anhydride unit concentration of 0.8% was prepared in the same manner as for modified olefin resin (1), except for replacing the propylene homopolymer with olefin copolymer (2) (propylene/1,4-hexadiene copolymer). Preparation of Modified Olefin Resin (6): To 100 parts of a linear low-density polyethylene (MFR: 2 g/10 min; density: 0.920 g/cm 3 ; ethylene content: 91.0%; hexene content: 9.0%) were added 0.04 part of 2,5-dimethyl-2,5-di(t-butylperoxy)hexane and 2 parts of maleic anhydride, and the mixture was mixed in a Henschel mixer. The mixture was extruded into strands from an extruder at a temperature of 180°C, cooled with water, and cut to pellets. The grafted maleic anhydride unit concentration in the modified polyethylene was 1.9% as measured in the same manner as described above. COMPARATIVE EXAMPLE 1 Modified olefin resin (1) was melt-kneaded in an extruder and extruded through a T-die at 238°C. The extruded sheet was cooled on a metallic roll to obtain a 1 mm thick sheet. The sheet was heated to 120°C and 5-fold stretched in the machine direction by making use of a difference in peripheral speed of rolls. The stretched film was then re-heated to 157°C in a tentering oven and 10-fold stretched in the transverse direction by means of a tenter frame. The resulting biaxially stretched film was subjected to annealing at 163°C and then to a corona discharge treatment to obtain a biaxially stretched film having a thickness of 20 µm. The biaxially stretched film had a surface smoothness of 40,200 sec, a maximum surface roughness (R max ) of 1.2 µm, and a center-line average surface roughness (R a ) of 0.35 µm. The biaxially stretched film was placed in a plasma deposition apparatus. After evacuating the apparatus to 1 x 10 -6 Torr, a mixed gas consisting of 3 parts by volume of hexamethyldisiloxane, 3 parts by volume of oxygen, 20 parts by volume of helium, and 13 parts by volume of argon was introduced into the apparatus and subjected to a glow discharge by a non-equilibrium magnetron to generate plasma. A SiO 2 thin layer was thus deposited on the biaxially stretched film. The deposited SiO 2 had a thickness of from 300 to 360 Å and a particle size of from 100 to 300 Å. The glow discharge conditions were set so that the SiO 2 -deposited film would have an oxygen permeability of 5.0 cc/m 2 ·atm·day as measured in accordance with JIS 1707-35. COMPARATIVE EXAMPLE 2 An SiO 2 -deposited biaxially stretched film was prepared in the same manner as in Comparative Example 1, except for replacing modified olefin resin (1) with modified olefin resin (2). The biaxially stretched film before SiO 2 deposition had a surface smoothness of 50,800 sec, a maximum surface roughness (R max ) of 0.48 µm, and a center-line average surface roughness (R a ) of 0.32 µm. The deposited SiO 2 had a thickness of from 180 to 260 Å. COMPARATIVE EXAMPLE 3 An SiO 2 -deposited biaxially stretched film was prepared in the same manner as in Comparative Example 1, except for replacing modified olefin resin (1) with 5 parts of modified olefin resin (1) diluted with 95 parts of unmodified polypropylene (MFR: 0.8 g/10 min; density: 0.950 g/cm 3 ), the diluted olefin resin material having a maleic acid unit concentration of 0.035%. COMPARATIVE EXAMPLE 4 Modified olefin resin (3) and the same unmodified polypropylene as used in Comparative Example 3 were melt-kneaded in separate extruders, fed to one die, laminated together in the die, and co-extruded to obtain a 1 mm thick sheet composed of a 0.1 mm thick modified olefin resin (3) layer and a 0.9 mm thick unmodified polypropylene layer. The sheet was stretched in the same manner as in Example 1 to obtain a biaxially stretched film having a thickness of 20 µm. The modified olefin resin (3) side of the laminate film was subjected to a corona discharge treatment, and SiO 2 was deposited thereon in the same manner as in Comparative Example 1 to prepare an SiO 2 -deposited biaxially stretched film. COMPARATIVE EXAMPLE 5 An SiO 2 -deposited biaxially stretched film was prepared in the same manner as in Comparative Example 1, except for replacing modified olefin resin (1) with unmodified polypropylene (MFR: 0.8 g/10 min; density: 0.905 g/cm 3 ). The deposited SiO 2 had a thickness of from 450 to 510 Å. COMPARATIVE EXAMPLE 6 An SiO 2 -deposited biaxially stretched film was prepared in the same manner as in Comparative Example 1, except for replacing modified olefin resin (1) with 1 part of modified olefin resin (1) diluted with 99 parts of unmodified polypropylene (MFR: 0.8 g/10 min; density: 0.905 g/cm 3 ), the diluted olefin resin material having a maleic acid unit concentration of 0.007% COMPARATIVE EXAMPLE 7 Modified olefin resin (6) was melted in an extruder and extruded into a cylinder through a blown-film die at 160°C, and the parison was inflated with air to a blow-up ratio of 2. The blown film was subjected to a corona discharge treatment to obtain a modified polyethylene film having a thickness of 40 µm. An SiO 2 was deposited on the modified polyethylene film in the same manner as in Comparative Example 1. COMPARATIVE EXAMPLE 8 An SiO 2 -deposited biaxially stretched film was prepared in the same manner as in Comparative Example 7 except for replacing modified olefin resin (6) with unmodified linear low-density polyethylene (MFR: 2 g/10 min; density: 0.920 g/cm 3 ). In all the foregoing Examples, the glow discharge conditions were varied so that the SiO 2 -deposited film would have an oxygen permeability of 5.0 cc/m 2 ·atm·day. Each of the SiO 2 -deposited biaxially stretched films obtained in Comparative Examples 1 to 7 evaluated as follows. The results of evaluation are shown in Table 1 below. 1) Permeation Change with External Stress: A repeated torsion tester " Gelbo Flex Tester" manufactured by Meiritsu Keiki K.K. was used. The film was rolled into a cylindrical form, and the ends of the cylinder were fixed to the clamps of the tester. After torsion of ±90° was given to the cylinder ten times, an oxygen permeability was determined. 2) Permeation Change on Fabrication: Low-density polyethylene having a melt index of 5 g/10 min and a density of 0.922 g/cm 3 was extruded from a T-die at a resin temperature of 320°C into a 20 µm thick film and laminated on the SiO 2 -deposited side of each of the films by means of a laminator. The oxygen permeability of the resulting laminated film was measured. Oxygen Permeability (cc/m 2 ·atm·day) Example No. Initial After External Stress After Laminating SiO 2 thickness (Å) Comp. Example 1 5.0 9.8 5.5 300-360 Comp. Example 2 5.0 5.2 5.0 180-260 Comp. Example 3 5.0 12.5 6.0 - Comp. Example 4 5.0 10.2 5.8 - Comp. Example 7 5.0 13.2 7.0 - Compar. Example 5 5.0 270 14.3 450-510 Compar. Example 6 5.0 240 13.6 - Compar. Example 8 5.0 307 15.8 - EXAMPLE 1 A biaxially stretched film of modified olefin resin (1) (annealed and corona discharge-treated; thickness: 20 µm) was prepared in the same manner as in Comparative Example 1. The corona discharge-treated side of the film was coated with a polyurethane type anchoring agent "Titabond T120" (a product of Nippon Soda Co., Ltd; a mixture consisting of 7% of polyisocyanate polyether polyol; 0.6% of a hardening agent; and 92.4% of ethyl acetate) by roll coating. The solvent was removed by drying with a drier to form an anchor coat. The biaxially stretched film having an anchor coat was placed in a plasma deposition apparatus, and SiO 2 was deposited on the anchor coat in the same manner as in Example 1. The glow discharge conditions were set so that the SiO 2 -deposited film would have an oxygen permeability of 5.0 cc/m 2 ·atm·day as measured in accordance with JIS 1707-35. EXAMPLE 2 An SiO 2 -deposited biaxially stretched film was prepared in the same manner as in Example 1, except for replacing modified olefin resin (1) with 5 parts of modified olefin resin (1) diluted with 95 parts of unmodified polypropylene (MFR: 0.8 g/10 min; density: 0.905 g/cm 3 ), the diluted olefin resin material having a maleic acid unit concentration of 0.35%. EXAMPLE 3 Modified olefin resin (3) and the same unmodified polypropylene as used in Example 2 were melt-kneaded in separate extruders, fed to one die, laminated together in the die, and co-extruded to obtain a 1 mm thick sheet composed of 0.1 mm thick modified olefin resin (3) layer and a 0.9 mm thick unmodified polypropylene layer. The sheet was stretched in the same manner as in Example 1 to obtain a biaxially stretched film having a thickness of 20 µm. The modified olefin resin (3) side of the laminate film was subjected to a corona discharge treatment. Then an anchor coat was formed on this side in the same manner as in Example 1, and SiO 2 was deposited thereon in the same manner as in Example 1. COMPARATIVE EXAMPLE 9 An SiO 2 -deposited biaxially stretched polypropylene film was prepared in the same manner as in Example 1, except for replacing modified olefin resin (1) with unmodified propylene homopolymer (MFR: 0.8 g/10 min; density: 0.905 g/cm 3 ). EXAMPLE 4 An SiO 2 -deposited biaxially stretched polypropylene film was prepared in the same manner as in Example 1, except for replacing modified olefin resin (1) with modified olefin resin (4). EXAMPLE 5 An SiO 2 -deposited biaxially stretched polypropylene film was prepared in the same manner as in Example 1, except for replacing modified olefin resin (1) with modified olefin resin (5). EXAMPLE 6 (not included in the invention) Modified olefin resin (6) was melted in an extruder and extruded into a cylinder through a blown-film die at 160°C, and the parison was inflated with air to a blow-up ratio of 2. The blown film was subjected to a corona discharge treatment to obtain a modified polyethylene film having a thickness of 40 µm. An anchor coat was formed on the corona discharge-treated side in the same manner as in Example 1, and SiO 2 was deposited on the anchor coat in the same manner as in Example 6. COMPARATIVE EXAMPLE 10 An SiO 2 -deposited polyethylene film was prepared in the same manner as in Example 6, except for replacing modified olefin resin (6) with unmodified linear low-density polyethylene (MFR: 2 g/10 min; density: 0.920 g/cm 3 ). Each of the SiO 2 -deposited olefin resin films obtained in Examples 1 to 6 and Comparative Examples 9 and 10 was evaluated in the same manner as in Comparative Example 1. The results obtained are shown in Table 2 below. As described and demonstrated above, the modified olefin resin-based article having deposited thereon an inorganic oxide film suffers from no reduction in gas barrier properties even when heat or stress is applied thereto. Accordingly, it is more useful as a wrapping or packaging material in the production of pouch-packed foods, IC packages, etc.

Claims: An olefin resin-based article having good gas barrier properties, consisting of a maleic anhydride-grafted polypropylene resin or a copolymer formed of a combination of propylene with at least one of ethylene, 1-butene, 4-methyl-1-pentene and 3-methyl-1-butene having formed thereon an anchor coat, and, on said anchor coat, a 200-4000 Angstrom thick silicon oxide deposit film, wherein the concentration of anhydride units in said maleic anhydride-grafted polypropylene is from 0.01 to 10 % by weight. An olefin resin-based article as claimed in Claim 1 wherein said anchor coat has a thickness of from 0.01 to 0.5 g/m 2 . An olefin resin-based article as claimed in claim 1 or 2 in the form of a film. The use of the olefin resin-based article as claimed in any one of the previous claims in packaging applications.

Inventors: EGAMI MASAYUKI, HATTORI MASAFUMI, MAYUMI JUNJI, MIZUNO AKIRA, NAKANO TOMOMI, EGAMI, MASAYUKI, HATTORI, MASAFUMI, MAYUMI, JUNJI, MIZUNO, AKIRA, NAKANO, TOMOMI
Applicants: MITSUBISHI CHEM CORP, MITSUBISHI CHEMICAL CORPORATION
Application year: 1994
Main classification: C08J7
IPC codes: C08J7