CAPACITOR

Abstract: A capacitor including a metal container (1) having an inside surface and an outside surface and functioning as a cathode of the capacitor, a porous coating (13) including an oxide of one of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium disposed at the inside surface of the container in electrical communication with the container, an anode (6) selected from the group consisting of tantalum, aluminum, niobium, zirconium, and titanium, disposed within and spaced from the porous coating, and an electrolyte (14) within the container in contact with the porous coating and the electrode.

Description: CAPACITOR Field Of The Invention The present invention concerns improved capaci¬ tors and particularly hybrid capacitors employing a pseudocapacitor-type cathode and a wet slug-type capacitor anode to achieve improved performance in¬ cluding increased energy storage density. Background Of The Invention Tantalum wet slug capacitors have long been known in the capacitor arts. An example of the structure of a wet slug tantalum capacitor is de¬ scribed in U. S. Patent 4,780,797. Fundamentally, as described there, the wet slug capacitor includes a tantalum or tantalum-plated container that is the cathode or negative terminal of the electrolytic capacitor. An electrolyte and a porous sintered tantalum anode are disposed within the container. Tantalum forms a native oxide on exposed surfaces that may be increased in thickness by anodic oxida¬ tion. In the conventional wet slug capacitor, both the anode and cathode have insulating tantalum oxide coatings that are spaced apart from each other but are both in contact with the electrolyte, typically a sulfuric acid solution. Since sulfuric acid is electrically conductive, a conductor-insulator-con- ductor structure including metal, oxide coating, and electrolyte is present at both the anode and the cathode. Each of these conductor-insulator-conduc¬ tor structures is itself a,capacitor, i.e., an elec¬ trode capacitor such as an anode capacitor and a cathode capacitor. The capacitances of these elec- trode capacitors are to some degree determined by the thickness of the oxide layers formed on the an¬ ode and the cathode. Increasing the thickness of the anode oxide layer but not the cathode oxide lay- er, for example, by anodic oxidation, increases the breakdown voltage that a wet slug capacitor can withstand but reduces the overall capacitance of the capacitor. Typical breakdown voltages for a single capacitor can range from ten to one hundred twenty- five volts. In the wet slug capacitor, the anode capaci¬ tance is effectively electrically connected in se¬ ries with the cathode capacitance. As is well known, the net capacitance of two capacitors con- nected in series is smaller than the smaller of the capacitances of the two capacitors. Because the oxide layer at the anode of a wet slug capacitor is usually much thicker than the thickness of the oxide layer at the cathode, the anode capacitance of a wet slug capacitor is smaller than the cathode capaci¬ tance. For example, in a typical structure, the anode capacitance may be 3,100 microfarads and the cathode capacitance may be 8,700 microfarads. The resulting net capacitance of that capacitor is about 2,300 microfarads. Although wet slug capacitors having useful ca¬ pacitances and breakdown voltages can be readily produced, there is always a desire to increase the capacitance per unit volume of those capacitors, i.e., the energy storage density, without a reduc¬ tion in the breakdown voltage. One proposed method of increasing the energy storage density of a wet slug capacitor is described in the cited patent. In that patent, a number of metallic films are deposit- ed on the inside of the container of the capacitor. In particular, it is suggested that a metal film selected from the platinum group of metals, i.e., ruthenium, rhodium, palladium, and platinum, be al¬ loyed with the tantalum of the container in segre- gated islands where the native oxide has been re¬ moved from the tantalum. Various techniques can be employed to deposit the platinum group metal, such as sputtering and electrolytic or electroless plat¬ ing, followed by a heat treatment at a relatively high temperature, for example, from 925°C to 1,500°C. Preferably, a platinum group metal layer is subsequently deposited on the islands to form a spongy layer. The platinum group metals apparently improve the energy storage density of capacitors having the structure described in the patent. In U. S. Patent 4,942,500, a platinum group metal is applied to a capacitor cathode by cladding, i.e., by rolling a very thin layer of the platinum group metal with the tantalum metal. Explosive bonding is also mentioned. In U. S. Patent 5,043,847, electrolytic co-deposition of a base met¬ al and platinum group metal on the inside surface of a wet slug capacitor container is described. Addi¬ tion of the platinum group metal by these techniques is said to increase the energy storage density. A different type of capacitor, frequently re¬ ferred to as an electrochemical capacitor, employs so-called pseudocapacitive electrodes. These capac¬ itors generally have metal oxide electrodes includ- ing a substrate of titanium or tantalum. Typically, a hydrated chloride of the metal, which may be ru¬ thenium, is dissolved in isopropyl alcohol and sprayed on a heated titanium or tantalum substrate. The heat drives off the solvent, resulting in the deposition of a metal chloride. That chloride is heated to a high temperature in air to convert the metal chloride to an oxide. For example, the metal chloride film may be heated to about 250°C for ap¬ proximately one-half hour to completely remove the solvent and to drive off water. Thereafter, in a second elevated temperature step, for example, at approximately 300°C, a high surface area film of the oxide of the metal, for example, ruthenium oxide, is formed on the substrate. The oxide film is highly porous, meaning that it has a very high surface ar¬ ea. An electrochemical capacitor includes one such electrode as the anode and another such electrode as the cathode, typically with a sulfuric acid solution electrolyte. The electrical charge storage mecha- nism is not yet fully understood. Electrical charg¬ es may be stored on the very large surface areas of the two electrodes, providing the capacitance char¬ acteristic. Electrical charges may be stored by a reversible change in the oxidation state of a mate- rial in an electrode. No matter what the charge storage mechanism is, it is substantially different from the charge storage mechanism of a wet slug ca¬ pacitor electrode. Although electrochemical capacitors can provide much higher energy storage densities than wet slug capacitors, the breakdown voltage of individual cell electrochemical capacitors is very low, typically only about one volt, i.e., essentially the dielec¬ tric breakdown voltage of the electrolyte. Even if electrochemical capacitors are connected in series, it is difficult to produce a practical capacitor with a breakdown voltage comparable to the breakdown voltages of wet slug capacitors. Thus, electrochem¬ ical capacitors have not found wide usage. Summary Of The Invention It is an object of the invention to provide an improved capacitor having a practical breakdown vol- tage and a high energy storage density. According to one aspect of the invention, a capacitor comprises a cathode comprising a porous coating including an oxide of a metal selected from the group consisting of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium, an anode selected from the group consisting of tantalum, alu¬ minum, niobium, zirconium, and titanium, an electro¬ lyte in contact with the porous coating and the an¬ ode, and a container containing the anode and the electrolyte. According to another aspect of the invention, a capacitor includes a plurality of capacitor cells, each cell including a first metal body having op¬ posed first and second surfaces, a porous coating including an oxide of a metal selected from the group consisting of ruthenium, iridium, nickel, rho¬ dium, platinum, palladium, and osmium disposed on the first surface of the first metal body, an anode electrode selected from the group consisting of tan- talum, aluminum, niobium, zirconium, and titanium disposed on the second surface of the first metal body, a spacer disposed between the porous coating and the anode for preventing direct contact between the porous coating and the anode wherein the capaci- tor cells are disposed in a serial arrangement with the porous coating of one first metal body disposed opposite the anode of the next adjacent first metal body in the serial arrangement with the spacer dis¬ posed between, separating, and preventing direct contact between the opposed porous coatings and the anodes in the serial arrangement, a second metal body having first and second opposed sides disposed at one end of the serial arrangement and including a porous coating including an oxide of a metal select- ed from the group consisting of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium disposed on one side of the second metal body and opposite an anode of a first metal body in the se¬ rial arrangement, but no anode, and functioning as the cathode of the capacitor, a third metal body having opposed first and second sides disposed at another end of the serial arrangement and including an anode selected from the group consisting of tan¬ talum, aluminum, niobium, zirconium, and titanium disposed on one side of the third metal body and opposite a porous coating of a first metal body in the serial arrangement, but no porous coating, and functioning as the anode of the capacitor, an elec¬ trolyte disposed between and contacting the respec- tive opposed porous coatings and anodes in the seri¬ al arrangement, and a sealant disposed between and contacting adjacent metal bodies in the serial ar¬ rangement, sealing the electrolyte within the capac¬ itor and between adjacent metal bodies. In the invention, one electrode of a capacitor is a wet slug capacitor-type electrode, for example, the anode. The other electrode is an electrochemi¬ cal-type capacitor electrode employing a porous coating including an oxide of a metal selected from the group consisting of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium. For the same capacitance value, the cathode of a capacitor according to the invention is reduced in size com¬ pared to a conventional wet slug capacitor elec- trode. If the volume of the conventional wet slug capacitor for a particular capacitance is main¬ tained, then the anode of a capacitor according to the invention can be increased in size relative to the conventional wet slug capacitor anode, increas- ing the capacitance and the energy storage density as compared to a conventional wet slug capacitor. In addition, if the capacitance of a conventional wet slug capacitor is maintained, then the volume of a corresponding capacitor according to the invention can be made smaller than the conventional wet slug capacitor, increasing energy storage density. A high breakdown voltage, characteristic of the con¬ ventional wet slug capacitor, is obtained in the invention because of the presence of the convention- al wet slug capacitor anode while realizing in¬ creased energy storage density because of the presence of the pseudocapacitor cathode. Brief Description Of The Drawings Figure 1 is an exploded view of a capacitor according to an embodiment of the invention; Figure 2 is a cross-sectional view of an alter¬ native embodiment of a capacitor according to the invention; Figure 3 is a cross-sectional view of a single cell prismatic capacitor according to an embodiment the invention; and Figure 4 is a cross-sectional view of a multi- pie cell prismatic capacitor according to an embodi¬ ment of the invention. Description Of Preferred Embodiments Figure 1 is an exploded view of an embodiment of the invention and Figure 2 is a cross-sectional view of a related but different embodiment of the invention. Like reference numerals are used in those and all other figures to designate the same elements. In Figure 1, a capacitor according to the in- vention includes a metal container 1, typically a tantalum container. However, metals other than tan¬ talum may be used in embodiments of the invention. Typically, the container 1 is the cathode of the capacitor and includes a lead 2 that is welded to the container. An end seal, a cap 3, includes a second lead 4 that is electrically insulated from the remainder of the cap by a feedthrough 5 seen in Figure 2. In the assembled capacitor, the cap 3 is bonded to the container 1 by conventional means, for example, by welding. The insulating feedthrough 5 of the lead 4 is likewise conventional and may in¬ clude a glass-to-metal seal through which the lead 4 passes. A conventional porous sintered tantalum anode 6 that preferably has been anodically oxidized is electrically connected to the lead 4 and disposed within the container 1. Direct contact between the container 1 and the anode 6 is prevented by electri¬ cally insulating spacers 7 and 8 within the contain¬ er 1 that receive the ends of the anode 6. The re- taining insulators 7 and 8 are conventional. In the embodiment of the invention shown in Figure 1, a metal body 11, such as a metal foil, is disposed within and is in electrical communication with the metal container 1. The communication may be established, for example, by welding the metal body to the inside surface of the metal container 1. The inside surface of the metal body 11 includes a porous coating 12 including a metal oxide. The porous coating preferably includes an oxide of a first metal. The first metal is selected from the transition metals in Group VIII of the Periodic Ta¬ ble of Elements that have at least two stable oxidation states in the electrolyte used in the ca¬ pacitor. The metal is particularly selected from the group consisting of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium. The po¬ rous coating may also include an oxide of a second metal selected from the group consisting of tanta¬ lum, titanium, and zirconium. The second metal ox- ide is not believed to be electrically active but increases the surface area of the porous coating and/or extends the mixture used to form the porous coating. The second metal oxide component may be omitted from the capacitor cathode. In a preferred embodiment of the invention, the porous coating in¬ cludes oxides of ruthenium and tantalum. In the embodiment of the invention shown in Figure 2, a porous coating 13, i.e., the same as the porous coating 12 of the embodiment of Figure 1, is formed directly on the surface of the metal contain¬ er 1. The metal body 11 employed in the embodiment of the invention shown in Figure 1 is thus eliminat¬ ed, reducing costs. In the capacitors of Figures 1 and 2, each ca- pacitor includes two electrodes. One of the elec¬ trodes, the anode 6, is preferably a conventional sintered porous tantalum anode similar to and of the type used in conventional wet slug tantalum capaci¬ tors. In addition, the anode may be made of another one of the so-called valve metals, i.e. aluminum, niobium, zirconium, and titanium. The other elec¬ trode includes the metal container 1, the metal body 11 with the porous coating 12 or the porous coating 13 on the container 1 and is similar to one of the electrodes used in a pseudocapacitor. As a result of that combination, advantages of a pseudocapacitor and of a wet slug capacitor are achieved without the disadvantages of either of those known capacitor structures. The cathode capacitance is greatly in- creased over the cathode capacitance of a conven¬ tional wet slug capacitor because of the very large surface area and the very small effective "plate separation". (Plate separation refers to modeling of the cathode as a theoretical parallel plate ca- pacitor with two plates having areas A separated from each other by a distance d.) Because of the increased capacitance contributed by the pseudocapa¬ citor cathode for a particular volume, the cathode can be reduced in size, providing space for an anode of increased size, larger than the wet slug capaci¬ tor anode of a conventional wet slug capacitor hav¬ ing the same capacitance. Alternatively, for the same volume as a conventional wet slug capacitor, a much larger capacitance can be achieved. As already described with respect to one exam¬ ple of a conventional wet slug capacitor, a sintered tantalum anode has a capacitance of 3,100 micro¬ farads. A pseudocapacitor cathode replacing the cathode of the conventional tantalum electrolytic capacitor (having a capacitance of 8,700 micro¬ farads) has a capacitance of 0.2 farads. Since, as in the conventional apparatus, these electrode ca¬ pacitances are electrically connected in series, in the capacitor according to the invention, the over- all capacitance is calculated as 3,050 microfarads, an increase in capacitance of one-third over the conventional wet slug capacitor. Measured capaci¬ tances of capacitors in accordance with the inven¬ tion confirm the accuracy of this calculation. When a voltage is applied to a capacitor ac¬ cording to the invention, the voltage is divided across the oxide film on the anode and the pseudo¬ capacitor cathode. Because the capacitance of the anode is much smaller than the capacitance of the pseudocapacitor cathode, the voltage applied to the capacitor naturally divides unequally across the electrodes. A large proportion of the applied volt¬ age appears across the anode oxide film and not across the electrolyte. A much smaller proportion of the applied voltage appears across the pseudo¬ capacitor electrode. As a result, a capacitor ac¬ cording to the invention can sustain a much higher voltage, i.e, has a much higher breakdown voltage, than a conventional pseudocapacitor. In other words, increased capacitance as observed in a pseu¬ docapacitor is achieved in the invention without the disadvantage of the low breakdown voltage observed in those known capacitors. As well known in the art, the native oxide film on the anode, made of a valve metal, and particularly tantalum or aluminum, can be increased to a desired thickness, increasing the capacitor breakdown voltage, in an electrolytic, anodic oxidation process. The porous coating, whether formed on a metal body or directly on the inside surface of a metal container of a capacitor according to the invention, is formed using conventional processes. Examples of methods of forming such porous coatings on metal bodies are described in numerous publications. For example, the formation of similar capacitor elec- trodeε is described in U. S. Patent 4,766,522. Electrolysis cell electrodes including similar but very thick coatings are described in some of the examples appearing in U. S. Patent 3,632,498. In a preferred process, hydrated ruthenium chloride (RuCl 3 -3H 2 0) is dissolved in isopropyl alco¬ hol to form a solution having a concentration of one to three percent. Preferably, an enhancing agent, such as a chloride of tantalum, is added to the so- lution. A mixture having an atomic ratio of about one ruthenium atom to three tantalum atoms produces a higher capacitance film than do mixtures with dif¬ ferent ratios of tantalum to ruthenium atoms. The rate of dissolution of the chlorides in alcohol can be increased by the addition of about 10 milliliters of hydrochloric acid per 100 milliliters of isopro¬ pyl alcohol. Titanium, nickel, and zirconium com¬ pounds may also be used in place of the tantalum chloride to improve performance of the capacitors according to the invention. While the preferred process employs chlorides because of their solubili¬ ty, other inorganic and organic salts of the metals can also be employed in the formation of the porous coating. Whether the substrate on which the porous coat¬ ing is disposed is a metal body or the inside sur¬ face of a metal capacitor container, the substrate is preferably roughened before deposition of the coating to increase the adhesion of the solution subsequently applied to the substrate in forming the coating. The surface may be roughened by chemical treatment, for example, with sulfuric acid, hydro¬ chloric acid, or oxalic acid, or by a mechanical process, such as sand blasting, although mechanical processes are not preferred over chemical treat- ments. If a native oxide is present on the surface, the method described in U. S. Patent 5,098,485 may be employed to ensure a good electrical contact be¬ tween the substrate and the porous coating. The tantalum or titanium substrate is then heated to about 85°C and the solution is applied by spraying. The elevated temperature of the substrate results in rapid evaporation of the alcohol solvent, leaving the formerly dissolved chlorides in place as a film on the substrate. As an alternative to spraying, the substrate may be dipped in the solution. Howev¬ er, spraying a heated substrate results in prompt drying that permits the deposition of relatively thick films quickly by repeated spraying of the sub- strate. After the formation of the metallic chloride film, the substrate is heated to a temperature of about 250°C in air to drive off any remaining sol¬ vent and the water contained in the hydrated chlo- ride. In addition, some of the chlorine may be driven off at that time. The heating continues in air for about one hour after which the temperature is increased to approximately 300°C for a time suf¬ ficient to oxidize the metal components of the coat- ing. For example, the oxidizing treatment in air may continue for about two hours. The resulting coating is insoluble in water and sulfuric acid, has pores as small as 50 Angstroms, and has a surface area of up to about 120 square meters per gram. The completed capacitor includes an electrolyte 14, shown in Figure 2, disposed between and in con¬ tact with both of the electrodes to provide a cur¬ rent path between the electrodes 6 and 11 or 6 and 13. The electrolyte may be any of the conventional electrolytes employed in electrolytic capacitors, most typically a sulfuric acid solution when the anode is tantalum. In other constructions, differ¬ ent electrolytes are used. For example, when the anode is aluminum, an ammonium salt dissolved in glycol or a glycol-like solvent may be employed because sulfuric acid attacks aluminum. When the cathode is nickel, then potassium hydroxide is pre¬ ferred over sulfuric acid as an electrolyte. As is conventional, the materials of construction of the capacitor that are contacted by the electrolyte are chosen to be impervious or extremely resistant to the effects of the particular electrolyte employed. The embodiments of the capacitor according to the invention shown in Figures 1 and 2 are similar in shape and arrangement to conventional tantalum wet slug capacitors. Other embodiments of the in¬ vention resemble the "jelly roll" structure of con¬ ventional foil capacitors. In that configuration, the anode slug is replaced by a conventional foil of tantalum or aluminum, or any of the other valve met¬ als, wound in jelly roll fashion as the anode. Some decrease in capacitance is experienced in replace¬ ment of the anode slug with the rolled foil. Howev¬ er, an increased capacitance over the conventional jelly roll foil capacitors is achieved in the inven¬ tion because of the presence of the cathode includ¬ ing the porous coating. Capacitor cells of still different geometrical configuration according to embodiments of the inven- tion can be easily made. The capacitor cells can be interconnected in series to form a capacitor having a higher breakdown voltage than an individual cell. An example of an embodiment of the invention includ¬ ing a single cell is shown in Figure 3. A capacitor according to an embodiment of the invention and in- eluding a plurality of cells arranged and intercon¬ nected serially is shown in Figure 4. In Figure 3, a capacitor according to an em¬ bodiment of the invention includes opposed metal bodies 21 and 22, preferably thin metal plates or foils. The plates are separated by an insulating sealant 23 that is adhered to both of the plates 21 and 22. Figure 3 (and Figure 4) is a sectional view and the capacitor can have any desired shape in plan. For example, if the capacitor has a circular shape in plan view, then preferably the sealant 23 is a unitary, annular body adhered to both plates, sealing and forming a sealed package. If the capac¬ itor has other shapes in plan view, it is still pre- ferred that the sealant 23 be a unitary body follow¬ ing the perimeter of the plates, i.e., the capaci¬ tor, defining a closed volume between the two plates 21 and 22. The sealant may extend beyond the plates. The sealant may be a laminate of resin lay- ers that are thermally sealed to each other. The plates 21 and 22 are preferably tantalum, although other metals, such as titanium, may be em¬ ployed. A porous tantalum anode 24 or an anode of another valve metal is formed on plate 21 and dis- posed within the sealed volume defined by the plates 21 and 22 and the sealant 23. The inside surface of the plate 22 is coated with a porous coating includ¬ ing a metal oxide prepared as described above, thereby forming a pseudocapacitor cathode. In order to avoid direct contact between the anode 24 and the porous coating on the inside surface of the plate 22, a spacer is interposed between the anode 24 and the plate 22. Most preferably, the spacer includes a plurality of masses of an electrically insulating material disposed between and contacting the anode 24 and the plate 22. An electrolyte, such as a so¬ lution of sulfuric acid, potassium hydroxide, or an ammonium salt, is present between and in contact with the anode 24 and the plate 22. The electrolyte directly contacts the spacer 25 so that the spacer material must be impervious or extremely resistant to the electrolyte. In the capacitor of Figure 3, the plate or met¬ al body 22 has a porous coating including a metal oxide formed on one surface in the same manner that the porous coating is formed on metal body 11 or on the inside surface of the container 1 of the embodi¬ ments of the invention already described. After the formation of that porous coating, the spacer 25 is deposited on the porous coating. The individual spacing masses may be formed by printing, such as silk screening, while dissolved in a solvent that is subsequently removed, for example, by the applica¬ tion of heat, or by the deposition of individual masses of a melted electrically insulating material. If the electrolyte is sulfuric acid, then the spacer may be made of polyolefin, polyethylene, or polypro¬ pylene, for example. Other kinds of spacers can be employed instead of the individual masses illustrat- ed in Figure 3. For example, a glass fiber paper, plastic fibers, or an ion-permeable material, such as NAFION, may be inserted between the anode 24 and the plate 22 to prevent direct contact of the elec¬ trodes. The spacing masses may be located on the anode 24 rather than on the porous coating or may not be fixed to either electrode. The plate 21, which is preferably the same size and shape as the plate 22, is masked over the area where the sealant 23 will be adhered. Plate 21 may be a thin metal foil, for example, 1 mil in thick- nesε. Tantalum powder held together by a binder, such as stearic acid, if needed, is applied to the plate 21 under pressure. The tantalum powder binder is driven off, for example, by heat, and the powder is sintered in an inert atmosphere to produce a high surface area porous anode. Finally, that anode is anodically oxidized to form tantalum oxide over the surface of the sintered powder to a desired thick¬ ness. Similar anodes may be made of aluminum, nio- bium, zirconium, and titanium. The plates 21 and 22 are then brought together with the spacer 25 preventing direct contact of the plate 22 and the anode 24. The spacer masses may be about 1 mil high, 5 mils in diameter, and spaced about 50 mils apart in a regular pattern. In order to form a stable assembly, the sealant 23 is then applied at the periphery of the two plates 21 and 22 to form a closed package for retaining the electro¬ lyte. A hot melt polyolefin may be employed as the sealant 23. Subsequently, the sealant can be broken or opened so that the electrolyte 26 can be injected into the package. The interior of the package may be evacuated in advance of injecting the electro¬ lyte. After the electrolyte is in place, the seal- ant is resealed with additional sealant material. Leads can be easily attached to the plates 21 and 22 before, during, or after assembly of the capacitor. A capacitor according to an embodiment of the invention and including a plurality of individual capacitor cells 30 interconnected in series is il¬ lustrated in Figure 4. The serial arrangement of the cells 30 is terminated at opposite ends of the arrangement by plates 21 and 22, respectively. With the exception of those two plates, which are identi- cal to the corresponding elements of the capacitor shown in Figure 3, the remainder of the capacitor units in the capacitor of Figure 4 are identical cells 30. Since plate 22 on which spacers 25 are disposed and plate 21 on which the anode 24 is formed have already been described, no repetition of the description of those elements is required. Each cell 30 includes a bipolar metal plate or metal body 31. On one side of the metal body 31, a porous coating including a metal is formed in accor- dance with the preceding description. For example, a porous ruthenium oxide film containing tantalum oxide is present on one side of the plate 31. Elec¬ trically insulating spacing masses 32 are disposed in a pattern on that porous oxide coating. A porous tantalum anode 33, or an anode of a different mate¬ rial, is formed on the opposite side of the plate 31, completing the bipolar element of the cell 30. Generally, the anode 33 is formed first while a mask is present on the opposite side of the plate 31 to prevent the formation of excessive tantalum oxide. After the anode is completed, the mask is removed and the oxide coating is formed on the side of the plate 31 opposite the anode. Thereafter, the spacer masses 32 are formed on the oxide coating. Finally, the sealant 34 is applied to one side of the plate 31, completing the cell 30. The order of the fabri¬ cation steps can be changed and the spacing masses can be formed on the anode rather than on the oxide coating provided appropriate changes are made in the cells at the ends of the serial arrangement. The cells are then assembled by attaching the sealant to the plates of adjacent cells. The seal¬ ant may extend beyond individual cells and may merge into a single body along the whole length of the capacitor. The sealant may include laminated resin layers that are heat sealed together beyond the edg¬ es of the plates 31. After the serial arrangement of the unit cells is assembled, the end units, i.e., the plate 21 with the attached anode 24 and the plate 22 with the attached spacer masses 25 on the porous coating, are applied to opposite ends of the serial arrangement of identical unit cells to com¬ plete the mechanical assembly of the capacitor. Electrolyte is added to each of the cells through openings made in the sealant. The volume occupied by the electrolyte may be evacuated before the elec¬ trolyte is introduced. After injection of the elec¬ trolyte, the sealant is again closed, finishing the capacitor. When a capacitor like the embodiment shown in Figure 4 includes a number of cells, it is not al¬ ways possible to produce cells having identical characteristics. Particularly in capacitors accord¬ ing to the invention, where one electrode of each cell is significantly different in one or more of capacitance, resistance, and leakage current from the other electrode of that cell, excessive voltages may be applied to various cells. In order to avoid application of excessive voltages, a resistor, such as the resistors 35 illustrated in Figure 4, can be connected across the plates of each cell. If resis¬ tors are so employed, one such resistor should be connected across each pair of metal plates in the entire serial arrangement rather than the partial connection shown in Figure 4 which is shown only for illustrative purposes. The resistors should each have essentially the same resistance and provide a current path carrying substantially more current, for example, larger by a factor of ten, than the leakage current that flows through the capacitor. Although the resistors 35 are illustrated as dis¬ crete elements in Figure 4, distributed resistors between adjacent capacitor plates can be provided by employing a sealant with a desired, finite resistiv- ity. Alternatively, an electrically conducting paint can be applied to the sealant in one or more stripes interconnecting the capacitor plates, i.e., electrodes, of the capacitor embodiments of Figures 3 and 4. Capacitors according to the invention are nei¬ ther traditional electrolytic nor electrochemical capacitors but are a novel hybrid of parts of both of these kinds of capacitors. While the mechanism of charge storage and improved performance is not fully understood, the porous metal oxide may func¬ tion as a dielectric electrically connected in se¬ ries with the anode, electrolyte, and cathode of the capacitor, increasing the working cell voltage. This improvement permits, for the first time, the practical use of an electrochemical-type capacitor.

Claims: Claims 1. A capacitor comprising: a cathode comprising a porous coating in- eluding an oxide of a metal selected from the group consisting of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium; an anode spaced from the porous coating and selected from the group consisting of tantalum, alu- minum, niobium, zirconium, and titanium; an electrolyte in contact with the porous coating and the anode; and a container containing the anode and the electrolyte. 2. The capacitor of claim 1 wherein the con¬ tainer comprises a metal container. 3. The capacitor of claim 2 including a metal body that is electrically connected to the container and on which the porous coating is disposed. 4. The capacitor of claim 1 wherein the porous coating is disposed directly on an inside surface of the container. 5. The capacitor of claim 1 wherein the anode is aluminum coated with an oxide of aluminum. 6. The capacitor of claim 1 including a first metal body having opposed first and second surfaces, the porous coating being disposed on the first sur¬ face of the first metal body, and a second metal body on which the anode is disposed, wherein the container comprises a sealant disposed between and contacting the first and second metal bodies. 7. The capacitor of claim 1 or claim 6 wherein the anode is porous sintered tantalum having an ox- ide coating. 8. The capacitor of claim 6 including electri¬ cally insulating spacing means disposed between the porous coating and the tantalum electrode for pre- venting direct contact between the porous coating and the tantalum electrode. 9. The capacitor of claim 8 wherein the spac¬ ing means is a material selected from the group con- sisting of polyolefin, polyethylene, and polypropy¬ lene. 10. A capacitor comprising: a plurality of capacitor cells, each cell including: a first metal body having opposed first and second surfaces; a porous coating including an oxide of a metal selected from the group consisting of ruthe- nium, iridium, nickel, rhodium, platinum, palladium, and osmium disposed on the first surface of said first metal body as a cathode; an anode selected from the group consist¬ ing of tantalum, aluminum, niobium, zirconium, and titanium disposed on the second surface of the first metal body; and spacing means disposed between the porous coating and the anode for preventing direct contact between the porous coating and the anode wherein the plurality of capacitor cells are disposed in a seri- al arrangement with the porous coating of one first metal body being disposed opposite the anode of the next adjacent first metal body in the serial arrangement with the spacing means disposed between, separating, and preventing direct contact between the opposed porous coatings and the anodes in the serial arrangement; a second metal body having first and sec¬ ond opposed surfaces disposed at one end of the se- rial arrangement and including a porous coating in¬ cluding an oxide of a metal selected from the group consisting of ruthenium, iridium, nickel, rhodium, platinum, palladium, and osmium disposed on one side of the second metal body and opposite an anode of a first metal body in the serial arrangement, but no anode, and functioning as a cathode of the capaci¬ tor; a third metal body having first and second opposed surfaces and disposed at the other end of the serial arrangement and including an anode se¬ lected from the group consisting of tantalum, alumi¬ num, niobium, zirconium, and titanium disposed on one side of the third metal body and opposite a po¬ rous coating of a first metal body in the serial arrangement, but no porous coating, and functioning as an anode of the capacitor; an electrolyte disposed between and con¬ tacting the opposed porous coatings and the tantalum electrodes in the serial arrangement; and a sealant disposed between and contacting adjacent metal bodies in the serial arrangement, sealing the electrolyte within the capacitor and between adjacent metal bodies. 11. The capacitor of claim 10 wherein each anode is a porous sintered tantalum body coated with an oxide of tantalum. 12. The capacitor of any of claims 1, 6, or 10 wherein the porous coating includes a mixture of at least one oxide chosen from the group consisting of oxides of ruthenium, iridium, nickel, rhodium, plat¬ inum, palladium, and osmium and at least one oxide chosen from the group consisting of oxides of tanta¬ lum, titanium, and zirconium. 13. The capacitor of any of claims 1, 6, or 10 wherein the porous coating includes a mixture of oxides of ruthenium and tantalum. 14. The capacitor of claim 10 wherein the spacing means is a material selected from the group consisting of polyolefin, polyethylene, polypropy- lene, glass fiber paper, and an ion-permeable mem¬ brane. 15. The capacitor of claim 8 or claim 10 wherein the spacing means comprises a plurality of spaced apart masses of an electrically insulating material that is stable in the electrolyte. 16. The capacitor of claim 6 or claim 10 wherein the sealant is a hot melt polyolefin. 17. The capacitor of claim 10 including means for electrically interconnecting said first, second, and third metal bodies in series. 18. The capacitor of claim 17 wherein said means for electrically interconnecting comprises an electrically conductive material disposed within the sealant and contacting the first, second, and third metal bodies. 19. The capacitor of claim 17 including an electrically conductive film disposed on the sealant and contacting the first, second, and third metal bodies.

Inventors: EVANS DAVID A, EVANS, DAVID, A.
Applicants: EVANS FINDINGS CO INC, THE EVANS FINDINGS COMPANY, INC.
Application year: 1994
Main classification: H01G9
IPC codes: H01G9