METHOD OF EXTRACTING FLUORINE FROM MINERALS OR MINERAL SPECIES

Abstract: A method of extracting fluorine from a mineral or mineral species comprises, contacting the mineral or mineral species with a leachate solution which contains metal or metalloid ions capable of forming soluble fluoro-complexes of high bond strength with fluorine in the mineral or mineral species.

Description: Method of extracting fluorine from minerals or mineral species The present invention relates to a method of extracting fluorine from minerals or mineral species. The term "mineral species" is understood herein to mean any mineral-containing product formed by processing mineral ores, for example, mineral concentrates for pyrometallurgical processes such as smelting. The present invention is not mineral specific and applies to all fluorine containing minerals or mineral species. Fluorine is present in rocks in a range of minerals; for instance as discrete mineral grains, such as fluorite (CaF 2 ) and fluorapatite (Ca 5 [P0 4 ] 3 FOH) , or as sub- grains, veins or inclusions, often with a wide range of compositions. Fluorine can also occur dispersed throughout mineral species as a replacement ion or displacement anion, for example, by substitution for chloride or hydroxyl ions. Fluorine can also occur as complex ions such as (FeF 6 ) 3- or (A1F 6 ) 3~ in some mineral assemblages, usually at low concentrations. There is a need to reduce fluorine levels to less than 100 ppm (0.01 wt.%) in mineral concentrates such as lead, zinc and copper sulphides prior to smelting because at levels above 100 ppm fluorine may interfere with the smelting process and result in a cost penalty. An object of the present invention is to provide a method of extracting fluorine from minerals or mineral species, such as mineral concentrates, to reduce the fluorine levels to less than 100 ppm. According to the present invention there is provided a method of extracting fluorine from a mineral or mineral species comprising, contacting the mineral or mineral species with a leachate solution which contains metal or metalloid ions capable of forming soluble fluoro- complexes of high bond strength with fluorine in the mineral or mineral species. The term "metalloid" is understood to mean elements that exhibit properties that are characteristic properties of metals and properties that are characteristic properties of non-metals. The present invention is based on the realisation that the bond strength of some fluoro-complexes can be several orders of magnitude above the bond strength of fluorine in minerals, for example Ca-F in fluorite, and therefore can provide the chemical driving force for extracting fluorine from minerals. As a consequence, providing there are no kinetic, chemical, thermodynamic or solubility restrictions to the formation of fluoro- complexes, contact between a fluorine-containing mineral or mineral species and a suitable metal-containing or metalloid-containing leachate solution will result in the formation of a soluble fluoro-complex and thereby the removal of fluorine from the mineral or mineral species. A typical extraction reaction for a metal- containing leachate solution is as follows: Mineral-F + (metal (M)) γ+ ■ ϊ (M-F) (y_1> + Mineral soluble complex It is preferred that the method further comprises repeating the step of contacting the mineral or mineral species with the leachate solution. It is preferred that the method further comprises separating the leachate solution from the mineral or mineral species. It is preferred that the method further comprises removing the fluoride complex ions from the leachate solution by precipitation, absorption, displacement, ion exchange, ion exclusion, solvent extraction, or distillation. Alternatively, it is preferred that the method further comprises decomposing the soluble fluoro-complexes in the leachate solution to separate the metal or metalloid ions and the fluoride ions. It is preferred particularly that the method comprises recycling the metal or metalloid ions. It is preferred particularly that the method comprises, decomposing the soluble fluoro-complexes in the leachate solution by adjusting the acidity (pH) and/or oxidation potential (Eh) of the leachate solution. For example, the soluble fluoro-complexes may be decomposed by adjusting the acidity by contacting the leachate solution with lime, limestone, or other alkaline species to raise the pH above 6. Alternatively, the soluble fluoro-complexes may be decomposed by adjusting the oxidation potential by contacting the leachate solution with pyrites, carbonaceous material, or other oxidising or reducing species. It is preferred that the method further comprises removing the fluoride ions from the leachate solution by precipitation, absorption, displacement, ion exchange, ion exclusion, solvent extraction, or distillation. It is preferred that the method further comprises after separating the mineral or mineral species and the leachate solution, washing the mineral or mineral species with an acidic solution to remove any high stability fluoro complexes, such as iron-fluoride complexes or manganese- fluoride complexes. It is preferred that the acidic wash solution has a pH of 1.0 to 3.0. It is preferred that the acidic wash solution has a low oxidation potential. It is preferred particularly that the oxidation potential be +0.1 to -0.2 volts. It is preferred that the method further comprises, prior to contacting the mineral or mineral species with the leachate solution, crushing or grinding the mineral or mineral species into a particulate form having extensive micro or macro fractures so that the particles are essentially porous and therefore the mineral or mineral species are well exposed to the leachate solution. It is preferred particularly that 80% of the particles of mineral or mineral species pass a 75 microns screen or a finer screen. It is more particularly preferred that 80% of the particles of mineral or mineral species pass a 35 microns screen. It is preferred that the metal or metalloid ions be selected typically but not exclusively from the group comprising aluminium, boron, beryllium, uranium, titanium, and tungsten. It is preferred particularly that the metal or metalloid ions be aluminium. With aluminium the important chemical reactions are possibly, but not exclusively: Dilute acid \ . Dilute acid \ Mineral-F X — * Mineral + HF * H + + F " Al 3+ + F " ^ ^ (A1F) 2+ (soluble) Other AlF species are sparingly soluble or are insoluble, e.g. A1F 3 , Na 3 AlF 6 are insoluble A1F 3 + F " -^ —^ (AlF 4 ) ~ (sparingly soluble) (A1F 4 ) + F " ^ ^ (A1F 5 ) 2" (sparingly soluble) Overall the reaction is: Al 3+ + Mineral-F ^ — ^ (AlF) 111 + Mineral wherein "n" is an integer. It is noted that generally the anions present in the leachate solution are of minor importance and, for example, sulphate, chloride, or other soluble anions may be used. It is preferable not to use anions which form soluble complexes with the metal used to form the soluble fluoro-complex to avoid competition which could interfere with the rate of fluorine extraction by reducing the availability of the metal as a fluorine complexing agent. In situations where the anion is a sulphate and the acid is sulphuric acid, it is preferred that the leachate solution has a pH of 3.0 to 4.3 because aluminium is soluble as aluminium sulphate and fluorine can exist in the free ionic F " state. It is noted that at lower pH values the equilibrium changes to favour the combination of fluoride ions with hydrogen ions to form undissociated hydrogen fluoride. This change reduces the availability of fluoride ions and may slow the rate of fluorine extraction from minerals. It is also noted that the fluorine removal reaction can be carried out with anionic systems other than sulphate and sulphuric acid. For instance, chloride and hydrogen chloride can be used, but pH solutions lower than 3.0 to 4.3 will be required to avoid the loss of available aluminium by hydrolysis. These lower pH solutions (pH 1 to 2) may also cause the fluoride equilibrium to move toward hydrogen fluoride and the chloride will compete with fluoride in the combination reaction with aluminium. Thus the efficiency of the fluorine removal reaction will be reduced. It is preferred that the molecular ratio of Al:F be adjusted to minimise the formation of the insoluble or sparingly soluble A1F 3 , (A1F 4 ) " , (A1F 5 ) 2" and (A1F 6 ) 3" anions. It is preferred particularly that the molecular ratio of Al:F be 1:1 to 5:1. This should avoid the formation of Al-F precipitates which might slow the fluorine extraction reactions due to the formation of an impermeable surface deposit. It is more particularly preferred that the molecular ratio of A1:F be 2:1 to 5:1. It is noted that the formation of the sparingly soluble (A1F 4 ) " and (A1F 5 ) 2" species by disproportionation of (A1F) 2+ and (A1F 2 ) + may be used as a means of removing fluorine from the leachate solutions. At pH values above 5.5 the Al will tend to precipitate which will change the stoichiometry towards the less soluble (A1F 4 ) " and (A1F S ) 2" species. This effect may be used to remove soluble fluorine from the leachate solution prior to recycling the leachate solution. By the addition of potassium or calcium ions it may be possible to precipitate insoluble higher AlF salts. The need to minimise leachate solution losses in a large scale leaching operation is very important for overall plant water management. It is noted that fluorine is detectable by F 19 Nuclear Magnetic Resonance (F-NMR) . This technique can be used to monitor the progress of the fluorine removal reaction. F-NMR can be used to measure soluble fluorine in aqueous solutions and can distinguish between the species, F, HF and metal-F in complexes with a sensitivity down to at least 0.01% F. Therefore F-NMR can be used to study the rate of fluoro complex formation and can also be used to process control in plate operation for on-line monitoring. In principle, solid-state F-NMR can also be used to investigate the fluorine mineralogy in rocks and minerals, although in this case the sensitivity and chemical resolution may limit the usefulness of the technique. Example 1 An example of the method of the invention is the removal of fluorine from a central Queensland lead-zinc ore using an acidified solution of aluminium sulphate. In an experiment an amount of 25 gms of crushed ore containing 2.1% F was contacted in a stirred vessel with aluminium sulphate (20 gms) solution adjusted to pH 3 to 4.2 with dilute sulphuric acid. After stirring for about two hours at 20 to 22°C and pH 3 to 4.2 the mixture was filtered; the residue was washed (dilute H 2 S0 4 ), dried and analysed for total fluorine by X-ray fluorescence (XRF) . The fluorine level was found to have fallen to 0.15%. The leach solution was analysed for soluble Pb, Zn and Fe and the levels of these metals were less than 20 ppm. The residue from the leaching experiment was treated with 10 gms of aluminium sulphate solution (pH 3 to 4.2) and the fluorine level was further reduced to about 0.02% F. This shows that very low levels of fluorine can be achieved in oxide and sulphide mineral materials by chemical leaching, particularly if multistage or counter current techniques are applied. Further leaching experiments at lower pH values (pH 1.5, 2 and 2.5) failed to show major increases in fluorine extraction. However, increasing both the temperature and the amount of available aluminium and raising the particle to particle collision rate did have a beneficial effect. Also, reducing the mineral particle size to less than 25 microns using a rolls crusher or rod mill or fine grinding equipment such as ball mills or disc pulverisers enabled the leach time to be shortened whilst obtaining the same fluorine removal efficiency. Example 2 A series of experiments was carried out to investigate the preferred parameters for fluorine removal from lead and zinc concentrates obtained from the central Queensland lead-zinc ore referred to in Example 1 selected from the following experimental conditions. Particle size range ideally 90% < 37 micron Leach reagent Al 2 (S0 4 ) 3 .solution A1:F ratio at least 1:1 Solid:liquid ratio 20 to 60% solids pH 2.8 to 3.8 pH control by H 2 S0 4 or NaOH Washing of residue by dilute H 2 S0 4 Number of leaching stages 1, 2 or 3 Agitation continuous or shear mixing Temperature 25°C to 60°C The best results obtained in the experimental work and the parameters that produce those results are set out in Table 1 below. Table 1 Leach conditions Pb concentrate Zn concentrate Residual F (ppm) Residual F (ppm) nil 4550 1890 4 x 2hr leaches 370 37 at 50°C and Al:F ratio of 2:1 2 x 2hr leaches 410 50 at 50°C and Al:F ratio of 2:1 grinding and 2 x 222 2hr leaches at 50°C and Al:F of 2:1 Example 3 A series of experiments was carried out to investigate the effect of Al:F ratio and single and multiple leaching on fluorine removal from lead and zinc concentrates obtained from the central Queensland lead-zinc ore referred to in previous examples. The experimental work was carried out with Al:F ratios of 5:1 and 2:1 and single and multiple leaching with each leach step being of 2 hours duration. The results of the experimental work are set out in Table 2 below. Table 2: Effect of single and multiple leaching at A1:F ratios of 5:1 and 2:1 Leaching Pb concentrate Zn concentrate conditions* Residual F (ppm) Residual F (ppm) nil 1329 1890 Al/F = 5:1 1 x 2hr 151 175 2 x 2 hr 122 51 Al/F = 2:1 1 x 2hr 393 252 2 x 2hr 119 50 * at 50°C and 20% solids load Table 2 shows that the higher Al:F ratio of 5:1 improved leaching markedly for both Pb and Zn concentrates at the 1 x 2hr leach, although this was not as effective as 2 x 2hr leaches. Table 2 also shows that similar results were obtained for the 2 x 2hr leaches when either an A1:F ratio of 5:1 or 2:1 was used. This suggests that similar fluorine leaching limits have been reached. Example 4 A series of experiments was carried out to investigate further the effect of multiple leaching on fluorine removal from lead and zinc concentrates obtained from the central Queensland lead-zinc ore referred to in previous examples. Multiple leaching experiments on the Pb and Zn concentrates were performed (2hr per leach) at 50°C with a starting A1:F ratio of 2:1. The Pb and Zn concentrates were exposed to up to four leach steps at 2 hr per leach. Between each step the solid residue was washed and releached with fresh aluminium sulfate solution. The washings from each run were combined and analysed in total. The fluorine remaining in the leached residue was measured. The results obtained from the multileach trials are summarised in Figure 1 and Table 3 below. With reference to Figure 1 and Table 3, the fluorine levels in both concentrates decreased rapidly in the first two leaches and further leaching after the second leach did not have a significant effect. Table 3: Residual fluorine levels achieved in multiple leaching trials Number of 2 hr Residual F (ppm) leaches Pb concentrate nil 4550 1 leach 661 2 leaches 410 3 leaches 380 4 leaches 370 1 x 24hr leach 761, 721 Zn concentrate nil 1890 1 leach 252 2 leaches 50 3 leaches 41 4 leaches 37 Example 5 A series of experiments was carried out to investigate the effect of particle size on fluorine removal from lead and zinc concentrates obtained from the central Queensland lead-zinc ore referred to in previous examples. Portions of Pb concentrate were ground in a ring grinder for time intervals of 20 seconds, 60 seconds, and 10 minutes. Subsamples were taken and the particle size distribution determined by laser sizing. Various sized samples were subsequently leached at 50°C using an Al:F ratio of 2:1 for 2 x 2 hr leach steps. The results obtained are shown in Table 4. With reference to Table 4, when compared with the un-ground sample, grinding was found to improve fluorine extraction significantly thus yielding a residue with a minimum 222ppm fluorine compared with 344ppm when no grinding was used. Table 4: Effect of Pb concentrate particle size on fluorine extraction after 2 x 2hr leaches at 50°C Sample/grinding 10% 50% 90% Mean Residual time size F(ppm) Pb concentrate/ <2.8μ <14.9μ <45.5μ 20.6μ 344 no grinding Pb concentrate/ <0.6μ <6.9μ <28.4μ 11.4μ 318 /20s grind Pb concentrate/ <0.4μ <5.2μ <24.8μ 9.6μ 285 60s grind Pb concentrate/ <0.3μ <2.3μ <12.4μ 4.5μ 222 10 min grind Many modifications may be made to the preferred method of the invention described above without departing from the spirit and scope of the invention.

Claims: CLAIMS: 1. A method of extracting fluorine from a mineral or mineral species comprises, contacting the mineral or mineral species with a leachate solution which contains metal or metalloid ions capable of forming soluble fluoro-complexes of high bond strength with fluorine in the mineral or mineral species. 2. The method defined in claim 1 further comprises repeating the step of contacting the mineral or mineral species with the leachate solution. 3. The method defined in claim 1 or claim 2 further comprises separating the leachate solution from the mineral or mineral species. . The method defined in claim 3 further comprises removing the fluoride complex ions from the leachate solution by precipitation, absorption, displacement, ion exchange, ion exclusion, solvent extraction, or distillation. 5. The method defined in claim 3 further comprises decomposing the soluble fluoro-complexes in the leachate solution to separate the metal or metalloid ions and the fluoride ions. 6. The method defined in claim 5 further comprises recycling the metal or metalloid ions. 7. The method defined in claim 6 comprises decomposing the soluble fluoro-complexes in the leachate solution by adjusting the acidity (pH) and/or oxidation potential (Eh) of the leachate solution. 8. The method defined in claim 7 comprises adjusting the acidity by contacting the leachate solution with lime, limestone, or other alkaline species to raise the pH above 6. 9. The method defined in claim 7 comprises adjusting the oxidation potential by contacting the leachate solution with pyrites, carbonaceous material, or other oxidising or reducing species. 10. The method defined in any one of claims 5 to 9 further comprises removing the fluoride ions from the leachate solution by precipitation, absorption, displacement, ion exchange, ion exclusion, solvent extraction, or distillation. 11. The method defined in any one of claims 4 to 10 further comprises, after separating the mineral or mineral species and the leachate solution, washing the mineral or mineral species with an acidic solution to remove any high stability fluoro complexes, such as iron- fluoride complexes or manganese-fluoride complexes. 12. The method defined in claim 11 wherein the acidic wash solution has a pH of 1.0 to 3.0. 13. The method defined in any one of the preceding claims further comprises, prior to contacting the mineral or mineral species with the leachate solution, crushing or grinding the mineral or mineral species into a particulate form having extensive micro or macro fractures so that the particles are essentially porous and therefore the mineral or mineral species are well exposed to the leachate solution. 14. The method defined in any one of the preceding claims, wherein 80% of the particles of mineral or mineral species pass a 75 microns screen or a finer screen. 15. The method defined in any one of the preceding claims, wherein the metal or metalloid ions are selected from the group comprising aluminium, boron, beryllium, uranium, titanium, and tungsten. 16. The method defined in claim 15, wherein the metal is aluminium. 17. The method defined in claim 16, wherein the leachate solution has a pH of 3.0 to 4.3. 18. The method defined in claim 16 or claim 17, wherein the molecular ratio of A1:F is selected to minimise the formation of insoluble or sparingly soluble A1F 3 , (A1F 4 ) " , (A1F 5 ) 2" and (AlF 6 ) 3" anions. 19. The method defined in claim 18, wherein the molecular ratio of Al:F is 1:1 to 5:1. 20. The method defined in claim 19, wherein the molecular ratio of A1:F is 2:1 to 5:1.

Inventors: HUGHES TERRENCE CHARLES, JOMOTO KIMITAKA, HUGHES, TERRENCE, CHARLES, JOMOTO, KIMITAKA
Applicants: BROKEN HILL PTY CO LTD, HUGHES TERRENCE CHARLES, JOMOTO KIMITAKA, HUGHES, TERRENCE, CHARLES, JOMOTO, KIMITAKA, THE BROKEN HILL PROPRIETARY COMPANY LIMITED
Application year: 1994
Main classification: C22B1
IPC codes: C01B9, C01F7, C22B1, C22B3