CATALYST FOR POLYMERIZATION OF ETHYLENE

Abstract: The present invention concerns a heterogeneous catalyst for polymerization of olefins. The catalysts include at least one group IVa metal compound on a solid inorganic oxidic support. According to the invention the catalysts are prepared by vapourizing at least one solid group IVa metal halide compound and routing the vapour of the metal halide compound into a reaction chamber, wherein the vapour is reacted with the support at a temperature of about 250 to about 450 DEG C in order to bind said metal halide compound to said support. Any metal compound not bound to said support as well as any volatile reaction products emanating from the reaction between said metal halide compound and said support are then removed from the reaction chamber in the vapour phase. Optionally the product obtained is treated with an organic aluminum compound to increase the catalytic activity of said catalyst. The catalysts thus prepared are very well suited for polymerization of ethylene or copolymerization of ethylene with other alfa-olefins, such as propylene, butylene, 4-methyl-1-pentene and hexene. A polymerization process employing the novel catalyst will provide products of the Ultra High Molecular Weight-type (UHMWPE) having very broad MWD.

Description: CATALYSTFORPOLYMERIZATIONOFETHYLENE Background of the Invention Field of the Invention The present invention relates to a process for preparing polymerization catalysts for olefins. Said catalysts are particularly suited for the polymerization of ethylene. The present novel polymerization catalysts comprise a support consisting of an inorganic oxide or a mixture of inorganic oxides, the surface of said support having a group IVa metal compound bound to its surface. Furthermore, the present invention concerns a process for the homo- and copolymerization of olefins, in particular ethylene, in the presence of a heterogeneous catalyst. Description of Related Art It is known in the art that oligomerisation and polymerisation of ethylene can be catalysed by compositions comprising vanadium, titanium and or zirconium halides and possibly other components on an inorganic oxidic support. Typically, these heterogeneous catalysts are prepared by stirring the support, for instance silica or alumina, in a solution of the transition metal compound(s) used, evaporating the product and, if desired, suspending it in a solution of a suitable cocatalyst compound, such as an organo-Al compound, before polymerization. The prior art is hampered by considerable problems. For example, the use of solvents makes the processes complex because additional process steps (evaporation) are needed for separating the solvents from the products. Furthermore, as far as the preparation of Zr- and Hf-containing catalysts using chlorides is concerned, the reagents are solid substances, which are poorly soluble in non-polar solvents. Therefore, polar solvents, such as water and alcohols, will have to be used as reaction media. These solvents are, however, known to impair the activity of the catalysts. Summary of the Invention It is an object of the present invention to eliminate the problems of the prior art and to provide novel zirconium chloride -based catalysts, as well as novel processes for preparing supported group IVa metal catalysts, and for polymerization of olefins. The present invention is based on the concept of evaporating the group IVa metal reagent, preferably a group IVa metal halide, separately from the support and routing the vapour into a reaction chamber, wherein the vapour is reacted with the support. During the reaction, the support is kept at a temperature which is higher than the condensation temperature of the vapour and simultaneously so high as to achieve the thermal activation energy necessary for establishing chemical bonds between the metal compound and the support (chemisorption of the metal compound). Brief Description of the Drawings Figures 1 and 2 show the binding of ZrCl 4 as a function of the preheating temperature of the support, Figure 3 shows the activity of the catalysts as a function of the Al/Zr molar ratio, Figure 4 indicates the change in Zr concentration when silica preheated at 300 °C is pretreated with TiCl 4 at 175 - 300 °C, Figure 5 shows the XRD patterns for ZrCl 4 /silica catalysts treated at different temperatures, and Figure 6 shows the molecular weight distributions of PE produced by ZrC14 on silica with two different hydrogen ed ylene ratios. Detailed Description of the Invention The present catalysts comprise compounds, in particular halides, of one or more group IVa metals deposited from the vapour phase on an oxidic support. Should the catalysts contain only one metal compound, then that compound is selected from the group consisting of the fluorides, chlorides, bromides and iodides of zirconium and hafnium. Likewise, if there are several metal compounds, men at least one of those compounds is selected from the group of compounds listed above. The oxidic supports are preferably selected from the group consisting of silica and alumina. According to a preferred embodiment, the novel zirconium chloride catalyst provided by the present invention comprises an essentially amorphous zirconium compound of the formula ZrY., wherein Y is a halo, preferably chloro or bromo, and x is 2 or 3, on an oxidic support selected from the group consisting of silica and alumina. From instrumental analysis of the catalysts it appears that, for instance, the zirconium chloride has reacted with the hydroxyl groups on the surface of the support, resulting in direct chlorination of the OH groups. Therefore, depending on whether the zirconium chloride molecule has reacted with one or two OH groups, the formula of the zirc'onium species bound to the support is either ZrCl 3 or ZrCl 2 . Because of the reaction, HY is released. The novel catalyst is capable of catalyzing the homo- and copolymerization of ethylene. According to one embodiment, the catalysts are capable of catalyzing ethylene polymerization in the gas phase at an increased pressure of at least 2000 kPa, producing polyethylene having a broad molecular weight distribution, the polydispersity being at least 15. According to the process of the present invention, the catalysts are prepared by vaporizing suitable group IVa metal compounds and reacting the vapours with an oxidic support so as to deposit them thereon. For the vaporization of zirconium and hafnium it is particularly preferred to use solid halides, in particular halides selected from the group consisting of ZrCl 4 , ZrBr 4 , HfCl 4 and HfBr 4 . It has surprisingly been found that many organic zirconium and hafnium compounds, which have suitable boiling points, cannot be used in the present invention because they tend to decompose in the vapour phase. However, the halides of the same elements, which are solid substances at ambient temperature, are readily vaporized at temperatures above 250 °C and are stable up to 500 °C. One preferred embodiment of the invention comprises providing an amorphous group IVa metal compound on silica support. According to that embodiment the temperature should not be allowed to rise above 350 °C during the reaction between the metal halide, in particular the metal chloride, and the support, because, e.g., the zirconium chloride species (ZrCl 3 and ZrCU) will start to form crystallites of the formula ZrO 2 on the surface of the support at temperatures over about 350 °C. The crystallites will impair the activity of the catalysts. At temperatures of about 600 °C, the catalysts prepared on silica support become practically inactivated. On alumina supports, higher reaction temperatures can be used. As mentioned above, the catalysts prepared can contain more than one group IVa metal compound. One of the compounds is always zirconium or haftiium fluoride, chloride, bromide or iodide, respectively, whereas the second and diird compounds may comprise a hafnium, zirconium or titanium halide. Titanium halides can be bound to die support from vaporized titanium halides, such as TiCl 4 , or from organometal compounds which are composed by reacting them with hydrohalo acids to form the corresponding halides on the support. Of the organic titanium compounds, in particular the alkoxides, such as the isopropoxide and the isobutoxide derivates, should be mentioned. Of me above-mentioned halogen compounds, ZrCl 4 and HfCl 4 are typically vaporized at a temperamre in the range from 250 to 350 °C, in particular 260 °C to 320 °C, whereas TiCl, is vaporized at a temperature above 25 °C. The reagents, ZrCl 4 , HfCl 4 and TiCl 4 compete with each other for the same bonding sites. That is the reason why the binding order of the reagents has an effect on the saturation level (cf . below) in addition to d e preheat temperamre of the support and die chemisorption temperamre. If, for instance, ZrCl 4 is first processed to silica (calcined at 300 °C) and then TiCl 4 , in a particular embodiment some 1 wt-% of Ti and 6 wt-% of Zr are bound to die support. However, if the pulsing order is reversed, ZrCl 4 removes all Ti from the support and the Zr content becomes as high as 9.3 wt-%. Thus, it appears that TiC_ 4 creates new binding sites for ZrCl 4 (cf. the chemical treatment with A1C1 3 described below). The vapour pressure of HfCl 4 and ZrCl 4 can be regulated to the same level, and mese reagents can also be brought to the support simultaneously, although a more precise metal content regulation is achieved by alternate pulsing of the reagents. It is also possible to vaporize two of the reagents simultaneously. According to a preferred embodiment of the invention, the catalyst preparation comprises the following stages: 1) Pretreatment of the oxidic support, 2) vaporization of the reactant(s) and binding of it (them) to the support surface, 3) flushing with an inert gas and 4) an optional treatment of the catalyst with organic aluminium compounds. According to the invention all reagents for stages 1, 2 and 3 are brought into the reaction chamber in the vapour phase, typically one component at a time. In the first stage of the process, the support can be subjected to a pretreatment at elevated temperatures prior to the actual binding reaction. The heat treatment of the support can be applied to modify the number and character of the OH groups on the support and, thereby, the amount of metal species bound. The maximum temperature of the preheating process of silica supports is about 450 °C if ZrCl 4 'is to be bound thereto. Alumina supports can be preheated up to temperatures in the range of 800 to 900 °C. An elevated pretreatment temperature reduces the number of excess OH groups and diminishes side reactions catalyzed by acid sites. The heat pretreatment is carried out for 1 to 40 h, preferably for 2 to 24 hours. Instead of, or in addition to heating, the support can also be pretreated by contacting it with suitable compounds which will modify its surface in an advantageous way. Thus, the silica support can be treated with aluminium compounds. By reacting aluminium chloride and water vapour with silica, an Al 2 O 3 layer can be formed which prevents the formation of ZrO 2 crystallites onto the surface of the support. In addition to aluminium chloride organic aluminium compounds can be used. The following examples may be mentioned: TMA (trimethylaluminium), TEA (triethylaluminium), DEALOX (diethylalunώiium ethoxide, TEB (triethylboron) TIB A (triisobutylaluminium), EADC (ethylaliiminium dichloride) and MAO (methylalumoxane) In the second stage of the process, vaporized reagent(s) is (are) chemisorbed to die support by contacting the reagent vapours widi the support. The vapour pressure of the vaporized group IVa metal compound is kept sufficiently high during the process and the duration of interaction with the support material surface sufficiently long so as to achieve saturation or, preferably supersaturation, with the active material or its precursor, respectively, at the bonding sites of the support material. The partial pressure of the vaporized reagent is typically in the range from about 0,010 to about 95 kPa. Lower pressures will require longer reaction times. It is particularly preferred to use a partial pressure of at least 1 kPa. ZrCl 4 and HfCl 4 are preferably vaporized at temperatures in the range of 260 to 320 °C which corresponds to partial vapor pressures in the range of about 5 to 50 kPa (for ZrC ) and 10 to 95 kPa (for HfCl 4 ). TiCl 4 is preferably vaporized at temperatures in the range of about 23 °C to 70 °C (corresponding to partial pressures of about 1 to 15 kPa). The proportion of excess active material used in relation to the concentration necessary to achieve complete saturation of all available bonding sites on the suppport material surface (customarily called a monolayer coverage) is typically 1- to 100-fold, preferably 1- to 3-fold. The amount of the group IVa metal compound necessary før a monolayer coverage can be calculated from the area of the support determined with the help of, e.g., the BET method, and from the known molecular structure of the support. According to a preferred embodiment, the reaction temperature must not fall below the temperature necessary for the evaporation of the reagent; otherwise, condensation of die reagent could occur. Further, the reagent must not be allowed to condense on its way to the reaction chamber. Therefore, its temperamre must not be allowed to fall below the reaction temperature. The group IVa compound and the operating temperature must be selected so as to avoid the decomposition of the metal compound or a possible condensation of its decomposition products. Using experimental methods it is possible to determine a temperamre range, or temperature span, in which the reaction is most advantageously carried out. As explained above, if silica is used as support, the second stage of the process is preferably carried out at a temperature in the range from about 250 to about 350 °C, in particular about 260 to about 320 °C. The lower limit of the given temperamre span is determined by the condensation temperamre of the group IVa compound to be evaporated at the employed partial vacuum and by the activation energy necessary for establishing a desired surface bond. The upper limit is determined by the temperamre at which the transition metal compound chemisorbed on die support will start to form crystallites, which are catalytically less active. The reaction between the catalytically active material or its compound and die support can be carried out at ambient pressure, or alternatively, at overpressure. Preferably, the reaction is, however, carried out in a partial vacuum. Typically, the operating pressure of the process lies in the range from about 0.1 to about 1000 mbar (0,01 kPa to 100 kPa), preferably in the range from about 1 to about 100 mbar (0,1 kPa to 10 kPa). Also pre- and posttreatment steps, if any, are preferably carried out in partial vacuum. A benefit gained from the use of a partial vacuum is that the reaction space is kept cleaner and the diffusion rate is increased. The reaction time is not particularly critical as long as it is sufficient to allow the evaporated reagent to interact with all available binding sites of the support. Thus, in laboratory conditions the reaction time can be selected, for instance, in the range from about 1 min to 25 hours. Even shorter or longer periods of time are possible, depending on die intensity of the reaction between die reagent and th£ support and on the amount of the support. Conventionally a reaction time of some minutes up to 10 hours is sufficient for processing a 5 to 20 g amount of the support material. The vaporized transition compound can be introduced into the reaction space as such, or alternatively, using an inert carrier gas such as nitrogen or a noble gas. Preferably, a protective gas atmosphere formed by an inert gas is used, the same inert gas being used as the carrier gas for the transition metal vapour. Any unreacted transition metal reagent and the side products of the reaction between the metal and d e support (HC1 and organic residues of d e reagent, for instance) are removed from the reaction space in the vapour phase and preferably at the reaction temperature (to avoid potential condensation problems). The chemisorption reaction is therefore followed by a nitrogen purge at the reaction temperamre to remove unreacted reagent and released HC1. After the binding of d e transition metal catalytically active species to the support and prior to being used for polymerization, the catalyst can be modified, i.e. preactivated, by adding conventional organometal compounds, in particular Al-alkyl compounds typically used as cocatalysts. Suitable organometal compounds are, for example, TMA (trimemylaluminium), TEA (triethylaluminium), DEALOX (diediylaluminium ethoxide, TEB (triethylboron) TIBA (triisobutylalumimum), EADC (ethylalumimum dichloride) and MAO (methylalumoxane), to mention a few. TMA, TEA, TIBA and DEALOX are considered to be particularly advantageous for the purpose of the present invention. The reaction between die support containing me catalytically active transition metal species and die organometal compound is carried out by suspending die support in a solvent containing die suitable cocatalyst compound. The cocatalyst may of course also be added to the polymerization reactor, as known per se. In that case, the catalysts are transferred in nitrogen atmosphere from the reaction chamber for cocatalyst addition and polymerization. If, however, the catalysts are preactivated as described above, no cocatalyst addition is needed during polymerization. The polymerization is carried out according to known processes. Preferably, it is conducted at increased pressure in slurry or in vapor phase. The pressure depends on die process used. Typically, it varies from about 1,5 bar to 1000 bar (150 kPa to 100,000 kPa), preferably it is at least 5 bar (500 kPa). Thus, the pressure advantageously lies in the range from about 5 to 100 bar (500 kPa to 10,000 kPa), and in particular it is between about 10 and 75 bar (1,000 kPa - 7,500 kPa). The operational pressures of slurry processes are somewhat higher than those used in gas phase polymerization processes. The polymerization temperature is from about 20 to about 300 °C, preferably from about 50 to 275 °C. The partial hydrogen pressure is in the range from about 0,1 bar (10 kPa) to about 20 bar (2,000 kPa), preferably from about 0,5 bar (50 kPa) to about 10 bar (1,000 kPa). The present invention provides significant benefits. The catalysts are readily prepared witii me process according to die present invention. Since no solvents are used in the reaction of the transition metal and the support, no separate evaporation stage is needed, and die activity of the heterogeneous catalysts prepared is high. The catalyst systems are very well suited to polymerization of ethylene or copolymerization of ethylene widi other alfa-olefins, such as propylene, butylene, 4-metyl-l-pentene and hexene. They can be used in the gas phase or in slurry polymerization. Surprisingly, it has been found that the polymerization process employing the novel catalyst will provide products of die Ultra High Molecular Weight -type (UHMWPE) having very broad MWD and often having a bimodal molecular weight distribution. The molecular weight of the HDPE produced is often over 350,000 at a hydrogen-to-ethylene partial pressure ratio of less than 0.20. MFR*,-, 6 is 0.01 to 5, typically less than 1. The broad molecular weight distribution improves the mechanical properties of the polymers prepared, which can be used, in particular, as high-strength films and sheets. By treating the catalyst prepared in the gas phase with aluminium alkyl compounds, die activity of the catalyst may be improved significantly. Below, me invention will be examined in more detail witii the aid of the following working examples. Experimental A. Catalyst preparation The processing equipment consists of a reaction chamber for 1 - 20 g of catalyst. ZrCζ and HfCl 4 were vapourized at 260 - 320 °C, TiCl t at 25 °C. Chemisorption temperature was 150 - 550 °C for TiCl 4 and 270 - 550 °C for ZrCl 4 and HfCl 4 . The selected metal halide was brought in nitrogen flow through heated lines to the reaction chamber and was reacted with die support (5 - 10 g) in nitrogen flow at a pressure of 50 - 1000 mbar for 1 to 3 hours. A purge with nitrogen for 1 to 3 hours was made after the reaction. The number of bonding sites of d e preheated (300 - 900 °C) support can be determined by H-NMR, if necessary. The chloride compounds used react with isolated OH groups according to diffuse reflectance Fourier infra-red spectrometry (FTIR) measurement. The amount of reagent needed can ti s be calculated, when die number of bonding sites is known. An overdose (1 to 2 times the number of the bonding sites) is vapourized. The samration level of the metal concerned is not effected by die overdosing. The saturation level of d e samples was momtored by determining the metal concentrations of samples taken from the upper part and die bottom of the solid support bed. Zr was determined by X-ray fluorescence spectrometry (XRF) or by instrumental neutron activation analysis (INAA). Hf and Ti were determined by INAA. UV-VIS spectrophotometry was used for Ti determinations. Chloride was determined in the samples by potentiometric titration. X-ray diffraction (XRD) was used to determine if crystallization of ZrCl species to ZrO 2 took place. Diffuse reflectance FT R was used to analyze die bonding sites of ZrCt, on silica. B. Polymerization conditions Polymerizations were carried out in isobutane slurry, 1800 ml of 1 -butane being added to a 3-1 reactor. A catalyst and a cocatalyst were fed to the reactor under nitrogen pressure. Polymerization temperatures were 95 °C and 105 °C, and total pressures 3,100 and 4,100 kPa, respectively. Hydrogen was charged from a 500 ml bomb (pressure 5 bar) to the reactor at the beginning of me polymerization with ethylene flow. The reaction mixmre was agitated first at 500 rpm, and after 10 minutes, the agitation speed was raised to 600 rpm, after a further 20 minutes, tiiis was raised to 700 rpm. C. Cocatalyst addition The influence of the amount of cocatalyst on die catalyst activity and melt flow rates of polymer solutions was studied by feeding various amounts of me cocatalyst to the reactor. The cocatalysts used comprised a 10 wt-% solution of triethylaluminium (TEA) in heptane (supplied by Schering) and metiiylalumoxane (MAO) in toluene (7.32 wt-% Al, p = 0.863 g/cm 3 ) (supplied by Texas Alkyl, Inc.). The ZrCl 4 /SiO 2 system was not active without cocatalyst. D. Catalyst modification with Al-alkyl-compounds In some experiments an Al-alkyl compound was added straight to the catalyst and not to the reactor as normally. These modifications were done in inert atmosphere as follows: the catalyst was mixed witii anhydrous pentane to obtain a slurry. An Al-alkyl solution was injected to the slurry and a colour change to yellow could immediately be observed. Mixing was continued for 2 hours at room temperamre and after that the pentane was evaporated using standard Schlenk technique. Polymerization was carried out without cocatalysts. Example 1. Preparation of ZrCI,-, and HfCl,, catalysts Under the experimental conditions described under section A above, a number of group IVa catalysts were prepared. Tables 1A to ID indicate the results of the preparation processes. Table 1A. ZrCI 4 catalysts on silica or aluminium Sample Support and pre- Zr t- treatment T/°C Hf 2.0 t- Ti 3.8 wt- Table IB. ZrCI 4 catalysts on silica and further containing Ti Ti-i-pro = titanium-isopropoxide Table 1C. Binding of HfCl 4 and ZrCl 4 on silica preheated at 300 °C. Concentrations in percent by weight ZrO 2 was formed according to XRD measurements (cf. figure 5), when ZrC^ reacted with silica preheated at higher than 450 °C or at reaction temperatures at or over 450 °C. Amorphous ZrCl x (x is 2 or 3) leads to better polymerization activity than crystalline ZrO 2 species. From these tests, it appeared that the reagent ZrCl 4 contained a small amount of HfCl, as an impurity. The Hf:Zr ratio of the catalysts prepared remained constant (0.01) and was not dependent on the reaction conditions used. This is probably due to the similar vapour pressure of these two compounds. The surface saturation level of Hf+Zr on silica preheated at 300 °C was 0.77 +/- 0.03 mmol/g (Table ID). Figures 1 and 2 show the binding or ZrCl 4 as a function of die preheating temperature of the support. It can be noted tiiat the concentration of Zr can be regulated either by preheating the support or by varying the reaction temperamre. Example 2. Ti with ZrCl, The ZrCl 4 /SiO 2 catalysts were treated with titanium compounds in order to modify die catalytic activity thereof, in particular to increase the amount of short-chained polymers. Two different Ti reagents were used when processing Ti-Zr/silica catalysts: TiCl 4 and Ti-isopropoxide. TiCl 4 was vaporized at 25 °C and Ti-isopropoxide at 120 °C. Silica was preheated at 300 °C in all samples. Tables 2A and 2B show the samration levels of Zr and Ti in samples processed in different ways. HCl gas was used to remove the ligand in Ti-isopropoxide. Both Ti reagents can be used togetiier with ZrCl 4 , but lower Ti samration levels were measured when TiCl 4 was used instead of Ti-isopropoxide. I. TiCl^ ZrCl 4 is capable of removing TiClQ on silica almost totally. ZrCl 4 must be bound to silica first and TiCl 4 after that at 300 °C in order to get Ti bound from TiCl,. The saturation level of Ti is 1.3 wt-% and part of Zr is released from the surface. ZrCl 4 removes totally or partly both Ti and Hf bound from chlorides The metal concentration of the catalysts can be regulated by varying die preheating temperamre of the support and die reaction temperature Table 2A. Binding of Ti and Zr on Si0 2 from TiCI 4 and ZrCl 4 It appears from the results tiiat the TiCl 4 treatment of the silica surface obviously opens part of the hydrogen bonded OH groups, thus providing increased amounts of bonding sites to ZrCl 4 as compared with plain silica. Fig. 4 presents the change in Zr concentration when silica preheated at 300 °C is pretreated with TiCl 4 at 175 - 300 °C. II. Ti-isopropoxide The saturation level of Ti on silica preheated at 300 °C was 3.3 wt-%. HCl can be used to remove the organic part bound to Ti. Ti itself was not released with HCl pulsing at 210 - 300 °C. Neitiier was Ti released when ZrCl 4 was bound after HCl treatment. Isolated OH groups and part of the hydrogen-bonded OH groups serve as bonding sites to Ti-isopropoxide. ZrCl 4 pulsed straight after Ti-isopropoxide binding witiiout HCl treatment between the pulses removes part of the Ti from the surface. Table 2B. Binding of Ti and Zr on SiO, from Ti-isopropoxide and ZrCl 4 . Sample Pretreatment Rection Concentration (wt-° T °C/h T °C/h Zr Ti Cl C Example 3. Polymerization of ethylene Polymerizations were carried out under the conditions described in section B above. The results are indicated in Table 3. Table 3. Polymerization of ethylene with ZrC silica or alumina catalysts at 95 °C and 31 bar When a cocatalyst was fed to the polymerization, maximum activities were obtained at low Al/Zr ratios. Figure 3 shows the activity as a function of die Al/Zr molar ratio. The cocatalyst did not change die polymer MFR 21 6 values. The influence of hydrogen to catalyst activity was also evaluated. It appeared that the MFR 21 6 values of the produced polymers grew as the ratio H 2 /C 2 H 4 increases. The weight average molecular weight (M w ) decreased from 416,000 to 315,000 as the ratio was raised. Hydrogen broadened the molecular weight distribution, and the polydispersity increased from 15 to 21. A bimodal distribution was also observed, as indicated by Figure 6. Two ZrCl 4 /silica catalysts, whose supports had been pretreated at 600 or 750 °C and having Zr concentrations of 3.4 and 2.0 wt-%, respectively, were also tested for catalytic activity. It appeared tiiat they were not at all active in the polymerization of ethylene. Example 4. Catalyst modification with Al-alkyl-compounds Table 4 presents the polymerization results using three different Al-alkyls for modifying die activity of catalyst No. 2 of Example 1. Using TEA as a modifier, the activity increased remarkably from 330 to 750 g PE/g cat h compared to the normal run with cocatalyst. When trimethylalumimum (TMA) was used as a modifier, activity was further increased to 1,230 g PE/g cat h. Also, MFR 21 6 increased a little. Diethylaluminium methoxide (DEALOX) changed MFR 21 6 values considerably, but not the catalyst activity. The ethoxide group could have some kind of different effect on ttre termination process. Table 4. Modification of catalyst with Al-alkyl-compounds Example 5. Catalyst modification with Al-alkyl-compounds Further preactivation tests with aluminiiim alkyl compounds were carried out for Ti-modified catalysts. The polymerization results are indicated in Table 5. Example ft. Copolymerization and polymer properties Copolymerization of ethylene with 1-hexene was carried out using TMA preactivated ZrCl x /SiO 2 catalysts. The comonomer was added as a batch to the hot reactor simultaneously with the ethylene and hydrogen. The polymerization conditions and results, including me effect of polymerization temperature and comonomer on melting point, crystallinity and crystallization temperature are indicated in Table 6. The comonomer incorporation was about 1 wt-%, according to NMR results. 1-hexene did not affect the activity in cocatalyst run, but its effect on M,, was clear. The comonomer lowered the melting point from 133.3 °C to 130.1 °C; crystallinity and crystallization temperature were lower with comonomer. Table 5. Polymerization results of Zr,Ti/Si0 2 -catalysts. Silica pretreated at 300 °C; Run conditions: T=95 °C, p 101 = 3100 kPa, H 2 500 kPa/500 cm 3 and medium isobutane 1.8 cm 8 (Zr=ZrCI 4 , Ti=TiCI 4> Ti-i=Ti(i-OPr) 4 Table 6. Copolymerizations with 1 -hexene using Zr/Si0 2 (sample 6) -catalysts. Polymerization conditions: T = 95 °C and 3100 kPA. Al/Zr = 10 during cocatalyst runs and 2.5 during preactivation. t-o a) Temperature 105 °C and pressure 3500 kPa. SCE = saturated chain ends/1000 C (NMR), UCE = unsaturated chain ends/1000 C (NMR), T m = polymer melting point (DSC), T„ = polymer crystallization temperature (DSC), Cryst. = crystallinity (DSC). Example 7. Modification of the support with an organir aliiminium compound Zr-catalyst were prepared by vaporizing ZrCl 4 at 270 °C and TMA at room temperature and binding the compounds from vapor phase to a silica support (Grace 955). The following tables indicate me reaction conditions, including the order of introduction of the reagents, and die elemental concentrations of the catalysts (Table 7) as well as the results of polymerization of ethylene (Table 8). Table 7. Preparation of catalysts Table 8. Polymerization results * cocatalyst added (1.5 ml 30 % MAO), other samples did not contain cocatalyst

Claims: CLAIMS: 1. A process for preparing a heterogeneous catalyst for polymerization of olefins, said catalyst comprising at least one group IVa metal compound on a solid inorganic oxidic support, comprising: a) vapourizing at least one solid group IVa metal halide compound; b) routing the vapour of said metal halide compound into a reaction chamber, wherein said vapour is reacted witii said support at about 250 to about 500 °C in order to bind said metal halide compound to said support; c) removing any metal compound not bound to said support as well as any volatile reaction products emanating from the reaction between said metal halide compound and said support from said reaction chamber in the vapour phase; and d) optionally treating the product obtained from reacting said metal halide compound and said support with an organic aluminum compound to increase the catalytic activity of said catalyst. 2. The process according to claim 1, wherein steps a) to c) are repeated at least once using a halide of another group IVa metal compound. 3. The process according to claim 1, wherein said product obtained from the reaction between said metal halide compound and said support is treated with a titanium compound in order to modify me catalytic properties of said catalyst. 4. The process according to claim 1, wherein said group IVa metal halide compound is selected from the group consisting of a chloride and a bromide of zirconium or hafnium. 5. The process according to claim 4, wherein said chloride of zirconium is ZrCl . 6. The process according to claim 4, wherein said chloride of hafnium is HfC^. 7. The process according to claim 1, wherein a silica support is used and step b) is carried out at a temperature of 250 to 350 °C in order to produce a catalyst comprising an amorphous group IVa metal compound on a silica support. 8. The process according to claim 1, wherein the vapour pressure of said group IVa metal halide compound is maintained sufficiently high and d e duration of the reaction with said support material is sufficiently long so as to provide at least an equal amount of said metal halide compound with respect to the number of available bonding sites of said support. 9. The process according to claim 1, wherein, prior to step a), the surface of said support is modified by reacting said support with an aluminum compound. 10. The process according to claim 1, wherein, subsequent to step c), said catalyst is preactivated with a compound selected from the group consisting of TMA, TEA, TIBA, DEA, MAO, and DEALOX in order to increase its activity . 11. The process according to claim 10, wherein me preactivating is carried out in a liquid phase. 12. The process according to claim 1, wherein said reaction chamber is purged witii nitrogen in step c). 13. The process according to claim 1, wherein step b) is carried out at a temperature of from about 260 to about 320 °C. 14. A heterogeneous catalyst for polymerization of one or more olefins, optionally in the presence of a cocatalyst, comprising at least one group IVa metal compound on a solid oxidic support, wherein said group IVa metal compound is a Zr or Hf compound deposited on said support from the vapour phase. 15. The catalyst according to claim 14, further comprising an aluminum alkyl compound selected from the group consisting of TMA, TEA, TIBA, DEA, MAO, and DEALOX. 16. The heterogeneous catalyst according to claim 14, wherein: said group IVa metal compound is amorphous and has the formula ZrY x , wherein Y is halo and x is 2 or 3; said support comprises a compound selected from the group consisting of silica and alumina; and said catalyst catalyzes homo- or copolymerization of ethylene at a pressure of at least 500 kPa, producing polyethylene having a broad molecular weight distribution. 17. The catalyst according to claim 14, further comprising at least one titanium compound. 18. A process for polymerization of olefins in order to produce a polymer having a broad molecular weight distribution, comprising contacting, in one or more polymerization reactors in die slurry or gas phase, olefin monomers or mixtures thereof at an increased pressure of at least 500 kPa with a heterogeneous catalyst comprising at least one group IVa metal compound on a solid inorganic oxidic support, wherein said group IVa metal compound is a Zr or Hf compound deposited on said support from the vapour phase. 19. The process according to claim 18, wherein said polymerization is carried out at a partial hydrogen pressure of at least 10 kPa. 20. The process according to any one of claims 18 or 19, wherein a cocatalyst is fed into me polymerization reactor separately or together with said catalyst. 21. The process according to claim 20, wherein said cocatalyst is selected from the group consisting of TMA, TEA, TIBA, DEA, MAO, and DEALOX. 22. The process according to claim 18, wherein said olefin monomer is ethylene, and said polymer is polyethylene having a bimodal molecular weight distribution.

Inventors: HOKKANEN HARRI, IISKOLA EERO, KNUUTTILA HILKKA, LAKOMAA EEVA-LIISA, SORMUNEN PEKKA, HOKKANEN, HARRI, IISKOLA, EERO, KNUUTTILA, HILKKA, LAKOMAA, EEVA-LIISA, SORMUNEN, PEKKA
Applicants: NESTE OY
Application year: 1994
Main classification: C08F4
IPC codes: B01J37, C08F10