A process for reduction of waste material during manufacture of acrylonitrile

Abstract: A process for the substantial reduction or complete elimination of ammonium sulfate generated during the production of acrylonitrile by the direct ammoxidation of propylene/propane, ammonia and an oxygen containing gas (e.g. air) over a fluid bed catalyst wherein the improvement comprises introducing methanol into said reactor in the upper portion of the reactor at a location where the methanol reacts with at least a portion if not substantially all of the excess ammonia without affecting the acrylonitrile yield. Preferably, methanol is introduced into the reactor at below its coking temperature. In particular, when an oxygen lean fluid bed catalyst is utilized, an additional oxygen containing gas is introduced into the reaction at a distance between about 8 to 14 inches from the methanol feed location.

Description: BACKGROUND OF THE INVENTION The present invention is directed to substantial reduction of unreacted ammonia and the corresponding reduction in ammonium sulfate and resulting waste products produced from the unreacted ammonia during the manufacture of acrylonitrile by the direct ammoxidation of an unsaturated or saturated hydrocarbon, preferably propylene or propane, ammonia and oxygen in a fluid bed reactor containing an ammoxidation catalyst. In particular, the present invention is directed to the addition of at least one oxygen containing compound, preferably methanol, at a specific location in the fluidized bed reactor during the manufacture of acrylonitrile to reduce substantially the amount of ammonia remaining in the gaseous effluents exiting the fluidized bed reactor which translates into a substantial reduction of the production of ammonium sulfate during the recovery and purification of the acrylonitrile so produced. This substantial reduction or complete elimination in the generation of ammonium sulfate during the practice of the manufacture of acrylonitrile leads to significant environmental and economic advantages. In another embodiment of the practice of the present invention the amount of unreacted ammonia can completely be eliminated leading to complete elimination of the production of ammonium sulfate during the recovery and purification of acrylonitrile. There are several patents which address the issue of the injection of methanol into a fluid bed reactor to produce hydrogen cyanide. In addition, these references further disclose the injection of methanol into an acrylonitrile fluid bed reactor to produce hydrogen cyanide while manufacturing acrylonitrile. For example, U.S. Patents 3,911,089 and 4,485,079 each teach the ammoxidation of methanol to produce hydrogen cyanide by injection of methanol into a fluid bed reactor containing an ammoxidation catalyst suitable for the manufacture of acrylonitrile. In addition, each of these references teach that the methanol injection can be made simultaneously with the manufacture of acrylonitrile. Moreover, Japanese Patent Applications 74-87,474, 79-08655 and 78-35232 all are related to similar methods of increasing or making hydrogen cyanide during the manufacture of acrylonitrile. Japanese Patent Application 74-87,874 also suggests that a secondary effect of their procedure is the decrease of the amount of sulfuric acid used for neutralization. All of these patents are primarily concerned with the production of additional hydrogen cyanide. The present invention is directed to a specific procedure for injection of at least one oxygenate compound or mixture or organic materials capable of reacting with ammonia, preferably methanol, into the fluid bed reactor at a specific location and direction to obtain a substantial reduction and, if desired, a complete elimination of the unreacted NH 3 exiting the fluid bed reactor with the reduction or elimination of the production of ammonium sulfate produced during the manufacture, recovery and purification of the acrylonitrile without any decrease in the acrylonitrile production. SUMMARY OF THE INVENTION It is a primary object of the present invention to substantially reduce the amount of ammonium sulfate generated during the manufacture of acrylonitrile. It is a further object of the present invention to substantially reduce the amount of unreacted ammonia exiting the reactor effluents during the manufacture of acrylonitrile. It is another object to eliminate the amount of unreacted ammonia present in the exiting reactor effluents during the manufacture of acrylonitrile. It is still another object of the present invention to eliminate the amount of ammonium sulfate generated during the manufacture of acrylonitrile. Additional objects, advantages and novel features of the invention will be set forth in part in the description that follows, and in part will become apparent to those skilled in the art upon examination of the following or may be learned by practice of the invention. The objects and advantages of the invention may be realized and obtained by means of the instrumentalities and combinations particularly pointed out in the appended claims. To achieve the foregoing objects in accordance with the purpose of the present invention as embodied and described herein, the method of the present invention comprises introducing into the lower portion of a fluid bed reactor a hydrocarbon selected from the group consisting of propylene and propane, ammonia and oxygen containing gas to react in the presence of a fluid bed catalyst to produce acrylonitrile, introducing at least one oxygen containing compound capable of reacting with ammonia into the upper portion of the fluid bed reactor in an upward direction at a point where the oxygen containing compound does not substantially affect the reaction of the hydrocarbon, ammonia and oxygen containing gas to produce acrylonitrile and reacts with a substantial amount of the unreacted ammonia present in the reactor to substantially reduce the amount of free ammonia present in the reactor effluent exiting said reactor. In another embodiment of the process of the present invention the oxygen containing compound is introduced in an amount sufficient to react with substantially all of the unreacted ammonia to substantially eliminate unreacted ammonia from the reactor effluent exiting the reactor, passing the reactor effluent containing acrylonitrile and substantially free of any unreacted ammonia into a quench column to cool the reactor effluent with water in the absence of sulfuric acid to remove unwanted impurities and recovering the acrylonitrile from the quench column. In a preferred embodiment of the process of the present invention the oxygenate compound is selected from the group consisting of formaldehyde and methanol or mixtures thereof, most preferably methanol. In another preferred embodiment of the process of the present invention the oxygenate compound, preferably methanol, is introduced into the reactor at a temperature below its coking temperature, about 360-370°C (about 680° - 700°F). In still another preferred embodiment of the process of the present invention the oxygenate, preferably methanol, is injected into the reactor through a conduit which is capable of maintaining the temperature of the oxygenate below its coking temperature prior to exit into the reactor. Preferably, the conduit comprises an insulated sparger comprising at least one header pipe connected to at least one lateral tube containing at least one nozzle and/or alonized, ceramic or coated sparger. In a further preferred embodiment of the process of the present invention the point of injection of the oxygenate into the reactor is above at least 70% of the calculated expanded bed height, most preferably above 85%, especially preferred being above 90%. In another aspect of the present invention as embodied and broadly described herein, the method of the present invention comprises introducing a hydrocarbon selected from the group consisting of propylene and propane, ammonia and an oxygen containing gas into the lower portion of a fluid bed reactor containing a fluid bed ammoxidation catalyst to react in the presence of said catalyst to produce acrylonitrile wherein the improvement comprises introducing at least one oxygenate compound capable of reacting with ammonia into the upper portion of the fluid bed reactor at a temperature below the coking temperature of the oxygenate at a point where the oxygenate does not substantially affect the reaction of the hydrocarbon, ammonia and oxygen containing gas to produce acrylonitrile and reacts with a substantial amount of the unreacted ammonia present in the reactor to substantially reduce the amount of ammonia present in the reactor effluents exiting the reactor. In a preferred embodiment of the present invention the oxygenate is injected into the upper portion of the reactor at a location above at least 70% of the calculated expanded fluid catalytic bed height, most preferably at least 85%, especially preferred being at least 90%. In another preferred embodiment of the present invention the oxygenate is injected into the fluid bed reactor via a conduit which is capable of maintaining the temperature of the oxygenate, preferably methanol, below its coking temperature prior to exit into the reactor. In a still preferred embodiment of the present invention the conduit means for the oxygenate comprises a sparger comprising at least one header pipe connected to at least one lateral tube containing at least one nozzle. In still another preferred embodiment of the present invention the inside of the conduit for said oxygenate is maintained at a temperature below the coking temperature of the oxygenate, by providing a blanket of thermal insulation about the outer surface of the conduit. Preferably, a second conduit is provided about the outside surface of the thermal insulation to further provide a protective surface for said thermal insulation. Oxygenate compounds suitable in the practice of the present invention are selected from the group of aldehydes, carboxylic acids, ketones, alcohols, esters or mixtures thereof. The mandatory requirement of the oxygenate compound is that it react with any excess ammonia in the reactor to substantially eliminate free ammonia from exiting the reactor and not compete with the efficiency of the primary reaction to produce acrylonitrile. The preferred oxygenate compounds are formaldehyde and methanol, especially preferred being methanol. In a still further preferred embodiment of the process of the present invention a mixture of organic compounds having at least one compound capable of reacting with substantially all of the excess ammonia in the reactor but not affecting the efficiency of the primary reaction to produce acrylonitrile is introduced into the reactor. Illustrative of such mixtures may be organic or aqueous waste stream containing olefinic compounds, substituted aromatics and/or oxygenates. The significance of the process in the present invention is that it provides a simple and economic procedure for the substantial reduction or, if desired, the substantial elimination of ammonia breakthrough (i.e. unreacted NH 3 ) in a fluid bed reactor along with the attendant advantage of reducing or substantially eliminating ammonium sulfate as a by-product during the manufacture of acrylonitrile. The reduction or elimination of ammonium sulfate from the waste stream during acrylonitrile manufacture means that the waste stream has significantly less or will contain only a minimal amount of inorganic salt. This leads to significant economic advantages in the practice of the acrylonitrile process if one cannot practice deepwell injection. Currently, the waste stream emanating from the quench column contains (NH 4 ) 2 S0 4 in a fairly high concentration which makes the disposal of these streams in an economic and environmental acceptable manner difficult. The elimination or minimization of this ammonium salt from this stream can make these streams acceptable to treatment by waste treatment procedures which do not require severe conditions or expensive materials of construction (e.g. incineration), or if deepwell injection isn't available leading to significant economic and environmental advantages. Reference will now be made in detail to the present preferred embodiment of the invention. DETAILED DESCRIPTION OF THE INVENTION The present invention minimizes the production of ammonium sulfate generated during the manufacture of acrylonitrile by adding at least one oxygenate compound(s) (preferably methanol) capable of reacting with ammonia, preferably methanol, to the fluid bed reactor at a location which allows for the substantial or complete reaction of excess ammonia in the reactor with the oxygenate compound without substantially affecting the efficiency of the acrylonitrile production. The substantial reduction or complete elimination of ammonium sulfate from the waste stream emanating from the quench column of an acrylonitrile plant dramatically improves the environmental impact and economics associated with the practice of the acrylonitrile process if deepwell injection is not available. In the preferred practice of the present invention, methanol is injected into the fluid bed reactor in the catalyst zone or above (i.e. a height above 100% of the expanded catalyst bed height) from a sparger at a position and under conditions where it will have an opportunity to react with a substantial amount or all of the excess ammonia but not be competitive with the main propylene ammoxidation reaction occurring in the lower portion-of the catalyst bed. For the purposes of the present invention, the term fluid bed reactor is intended to not only encompass conventional fluid bed reactors but also any reactor capable of maintaining the catalyst in a fluid state such as transport line reactors, riser reactors or recycle reactors. In another preferred embodiment of the present invention the location of the methanol feed should be at a level calculated at 70% of the level of the expanded catalyst bed height, preferably 80% to 90% of the expanded catalyst bed height, most preferably being over 90% of expanded catalyst bed height. The term expanded catalyst bed height as used in this application means the catalyst bed height while the catalyst is in the fluidized bed state. That is, the bed height when the gaseous components are present in the fluidized bed reactor and mixing with catalyst. The oxygenate (preferably methanol) can be injected neat, or in the presence of other gases such as nitrogen, steam, air, recycled off gas, etc. or combination thereof. It can be injected in liquid or vapor form by one or several means such as a sparger or sprayer in any direction, preferably, in an upward mode. The feed pipes can enter the reactor at the proper level, higher or lower with the proper sparger/design/direction or from a pipe from the bottom or near bottom of the usual feed grids/spargers. The amount of methanol used can vary but should be enough to neutralize any excess ammonia breaking through into the reactor effluent. Any unreacted methanol obtained in the effluent can be recovered and recycled into the reactor or disposed by convention procedures (e.g. oxidation). In still another preferred embodiment of the present invention, methanol is introduced into the catalyst bed at a temperature below its coking temperature, about 360 - 370°C (about 680°C - 700°F). This is preferably accomplished by the utilization of a conventional sparger design (large header pipe, medium lateral pipes running off the header, and nozzles evenly distributed on the lateral pipes) which has been modified to prevent the temperature of the methanol from reaching its carbonization (coking) temperature before it is expelled into the catalyst bed. The sparger is modified by inclusion of a layer of insulation about the outside surface of the sparger to prevent the temperature of the inside surface of the sparger pipes/nozzles from reaching the methanol coking temperature. Most preferably the sparger is modified to include a first pipe having a second pipe disposed inside and spaced apart from the first pipe. The space between the conduits is filled with conventional thermal insulation. This design protects the insulation from abrasion of its surface by the fluidized bed catalyst. Each propylene/propane ammoxidation catalyst operates at somewhat different feed ratios and operating conditions for maximum acrylonitrile yield and/or economic considerations. The amount of excess ammonia exiting the reactor from propylene ammoxidation reactor will vary somewhat depending on the catalyst used. The level of methanol to be added will vary according to the catalyst types and the nature of the reactor. Accordingly, in the practice of the present invention the amount of methanol injected into the reactor will be dictated by the conditions and the catalyst used. In terms of a catalyst which operates in a lean oxygen phase (ratio of propylene to air of 1:9.5 or less), it may be necessary to add. additional oxygen to the reactor. However, catalyst which would operate in an excess of oxygen would not have the necessity for the addition of any oxygen to the reactor. Typically, any ammoxidation catalyst may be utilized in the practice of the present invention. For example, catalyst such as those disclosed in U.S. Patent Nos. 3,642,930; 4,485,079; 3,911,089; 4,873,215; 4,877,764; Japanese Patent Application Nos. 74-87474 and 78-35232 are suitable for the practice of the present invention and are incorporated herein by reference. As stated previously, each propylene/propane ammoxidation catalyst will operate at somewhat different feed ratios and operating conditions. During the practice of the process of the present invention the standard operating condition at which the existing propylene/propane catalyst has been operated should not have to be changed but can be changed depending upon feed and catalyst conditions. Conventional operating condition and feed ratio for the manufacture of acrylonitrile as set forth in U.S Patents 3,911,089 and 4,873,215 are suitable and herein incorporated by reference. However, if the catalyst utilized operates under a low or minimal oxygen environment there may be a necessity to increase the amount of oxygen into the reactor to insure that the process of the present invention operates most efficiently. This may be accomplished by increasing the oxygen ratio in the feed or actually supplying oxygen to the reactor by a separate means. In particular, the additional oxygen added when utilizing a catalyst which operates in an oxygen lean environment should be added to the reactor via a separate sparger located adjacent to the methanol feed means. Preferably, the additional oxygen (preferably in the form of air) is injected into the reactor utilizing a convention air distribution pipe positioned about 20-36cm (8-14 inches)below the elevated methanol insulated sparger. The oxygen/air distribution pipe may inject the additional air into the reactor in any direction. However, it is preferred that the air/distribution pipe is positioned downshot (i.e. facing downward) about 22-33cm (9-13 inches) below the upshot methanol sparger, especially preferred being about 25-31cm (10-12 inches) below the methanol sparger. In addition, the optimum dilute phase air ratio (moles or air/moles of MeOH) when operating with an oxygen lean ammoxidation catalyst range from greater than 0 to about 6 depending on the amount of ammonia desired to be removed from the gaseous effluents exiting the reactor. For example, the dilute phase air ratio (DPAR) for 25% reduction in ammonia will range from about greater than 0.5 to 2.0, for 50% reduction DPAR may range from 2.5 to 3.5, preferably 3, for 75% reduction DPAR will range from 3.5 to 4.5 preferably 4, and for 100% ammonia reduction the DPAR will range from 4.6 to 6.0, preferably 5 to 5.6. For purposes of illustration only, the following examples are set forth to describe the process of the present invention. Comparative Example 1 A 1½" diameter reactor was charged with 550gm of a promoted BiMoFeO propylene ammoxidation catalyst. A feed of a propylene/air/ammonia with mole ratio of 1/10.5/1.15 was passed through the catalyst bed at 443°C, 12.0 psig, at a 0.045 WWH weight hourly space velocity. After two hours on stream, propylene conversion was 98.3%, per pass conversion to AN was 76.3%, to HCN was 7.1% and about 15% of the ammonia feed breaking through. (Similar tests conducted at the same conditions at 27 hours gave 97.8%, 75.1% and 8.7%, C 3 conversion, AN and HCN percent, and at 42 hours gave 99.1%, 73.8%, and 8.3%, respectively, both with about 15% ammonia breakthrough). Example 2 The procedure of Example 1 was followed except that methanol at a mole ratio of 0.18 to 1.0 for propylene was introduced into the catalyst bed 75% from the expanded catalyst bed top. A recovery run was conducted at 75 hours on stream (total operating time), and a propylene conversion of 98.4%, ppc to AN of 72.1%, HCN of 10.1% and about a 9% ammonia feed breakthrough (down 6% from Example 1). Example 3 An identical test as set forth in Example 2 was followed except that the methanol was injected at 70% of the expanded bed height in an upward direction yielding 96.3% propylene, 73.3% AN, 9.4% HCN and the ammonia breaking through (in the effluent) was only 2% of the amount fed into the reactor. Comparative Example 4 A 1½" diameter reactor was charged with 550 grams of a promoted BiMoFeO propylene ammoxidation catalyst having a different composition than that utilized in Examples 1 to 3. Feed in a propylene/air/ammonia mole ratio of 1/9.3/1.15 was passed over the catalyst at 440°C and 12 psig, at a weight hourly space velocity, WWH, of 0.075. After 283 hours on stream a recovery run was conducted to determine the level of products being formed; it was found that the total propylene conversion was 96.6%, per pass conversion (PPC) to acrylonitrile 78.7%, and to hydrogen cyanide 5.6%, with 5.4% of the ammonia breaking through. Example 5 The procedure of Example 4 was followed except that methanol at a mole ratio of 0.09 to 1.0 for propylene was introduced into the catalyst bed 30% from the top of the expanded catalyst bed in an upward direction. A recovery run was conducted at 332 hours on stream, and a total propylene conversion of 96.9%, PPC to acrylonitrile of 78.1%, HCN of 5.8% and zero percent of ammonia breaking through wash found. Methanol conversion was 100%. Example 6 Under the same conditions of introducing feed and using the same catalyst charge as set forth in Example 5 and conducting an additional test at alternate mole ratio conditions of propylene/air/ammonia/methanol of 1/9.3/1.08/0.09, propylene conversion was 96.1%, with PPC acrylonitrile of 77.9%, HCN of 4.9% and ammonia breakthrough of zero. Again, methanol conversion was 100%. Comparative Example 7 Approximately 18 tons of a propylene ammoxidation catalyst (promoted BiMoFeO) was charged to a larger acrylonitrile reactor. Feeds of propylene/air/ammonia at mole ratio of 1/10.0/1.2 were passed through tee catalyst bed at 840°F, 12.0 psig. After 24 hours onstream, propylene conversion was 99.8%, per pass conversion (PPC) to AN was 75.3%, and PPC to HCN was 8.2%. Notably, 12% of the feed ammonia breaking through and sulfuric acid usage in the downstream quench operation of the process at these conditions was 0.33 gpm in order to neutralize the reactor excess ammonia. After 3 days onstream at same conditions, the catalyst gave 99.6% conversion, 75.7% PPC to AN and PPC to HCN 8.2% conversion of propylene, with about 14% of ammonia feed breaking through. Example 8 The same reactor was run at the same conditions as Example 7, and pure, superheated methanol vapor was injected at ca. 0.05, 0.1, 0.15, 0.2, band 0.26 mol per mole of C 3 =, introduced into the catalyst bed at 95% of the reactor's expanded catalyst bed height. Recovery runs conducted at methanol ratios from 0 to 0.26 MeOH/C 3 = gave an average 99.6% propylene conversion, 76.1% per pass conversion to AN, 7.2% HCN from propylene. Total methanol conversion averaged 99.6% and per pass conversion of methanol to HCN averaged 65%. The relationship between methanol ratio, ammonia breakthrough, and sulfuric acid usage is set forth in Table 1 below: MeOH/C 3 =Ratio Sulfuric Acid (gpm) NH 3 B.T. (% of feed) Acrylo (%PPC) HCN from C 3 =(%PPC) HCN from MeOH (%PPC) 0.00 0.33 14.1 75.9 7.2 0 0.05 0.22 7.2 76.5 7.6 66.9 0.1 0.16 2.7 76.1 7.5 69.7 0.16 0.06 0.6 75.9 7.1 69.4 0.22 0.0 0.0 77.0 6.7 58.9 0.23 0.0 0.0 75.3 7.8 62.9 0.26 0.0 0.0 76.3 7.5 60.6 This demonstrates zero ammonium sulfate production (last three runs in Table 1) with no adverse effect on the normal acrylonitrile production. Example 9 Testing was repeated under a similar set of conditions as Example 8, except that methanol was introduced into the catalyst bed at 90% of the reactor's expanded catalyst bed height and at different ammonia feed ratios. The inventory of propylene ammoxidation catalyst was increased by about 1 ton, so that the relative position of the methanol sparger in the catalyst bed was about 90% of expanded bed height. Feeds of propylene/air/ammonia mole ratio of 1/10.0/1.1 were passed through the catalyst bed at otherwise similar conditions. At 14 days onstream, propylene conversion was 99.8%, PPC to AN was 74.4% and PPC to HCN was 8.3%. Unreacted ammonia was 8.4% of the reactor feed ammonia. The sulfuric acid usage in the downstream quench operation of the process was 0.26 gpm in order to neutralize the reactor excess ammonia. This example demonstrates that the relative position of the methanol injection point can be controlled easily by simply varying the reactor charge weight. Methanol vapor was introduced at 90% of the reactor bed height at the above conditions. Recovery runs at 0.09 ratio of MeOH/C 3 = gave 99.7% total conversion, 74.8% PPC to AN, 8.0% PPC to HCN from propylene, total methanol conversion of 99.8% and PPC of methanol to HCN of 58%, reducing the ammonia breakthrough to 4.1% of feed, and reducing the sulfuric acid consumption to 0.07 gpm. Recovery runs conducted at 0.12 ratio of MeOH/C 3 = gave 99.7% total conversion, 74.9% PPC to AN, 7.9% PPC to HCN from propylene, total methanol conversion of 99.8% and per pass conversion of methanol to HCN of 53%, reducing the ammonia breakthrough to 0% of feed ammonia, and requiring no sulfuric acid, and forming no ammonium sulfate. Example 10 Repeating the testing at a similar set of conditions as in Examples 8 and 9, except that methanol was injected at 85% of the reactor's normal expanded bed height resulting in a reduction of the percentage of reactor feed ammonia breaking through from 11% to 1.8%, and subsequent lowering of ammonium sulfate generated, but also raised the selectivity of methanol to HCN while lowering the yield of AN versus introduction at 90% above of the expanded bed height. Comparative Example 11 In a reactor (1½" diameter) a different bismuth molybdate type ammoxidation catalyst was charged (550 grams). Feed composed of a propylene/air/ammonia mole ratio of 1/9.5/1.2 was passed through the catalyst bed at 450°C, 10 psig, at a 0.060 WWH weight hourly space velocity. Water in the form of steam at a mole ratio of 0.3 to 1.0 for propylene was introduced into the catalyst bed. Acrylonitrile conversion was 72.6%, hydrogen cyanide of 4.3% at 89.4% propylene conversion, with 6.4% of the ammonia fed breaking through. Example 12 The procedure of Example 11 was followed except that an aqueous (59% by volume water) stream at a mole ratio of 0.3 organics to 1.0 for propylene was introduced into the catalyst bed at 70% of the expanded bed height. It contained by mole %, 0.5 acrolein, 4.3 ethanol, 0.4 oxalic acid, 3.4 acetone, 6.9 methyl formate and 1.8 acrylic acid as well as other trace components. A recovery run was made after five hours on stream to determine the reactivities and showed a propylene conversion of 89.7%, per pass conversion to acrylonitrile of 68.2%, to hydrogen cyanide of 3.9%, and an ammonia reduction to 2.8% of that fed, breaking through. This waste stream obviously had an impact on lowering the ammonia remaining in the reactor effluent by over 50%, resulting in less neutralization required, and/or generating less ammonium sulfate, generating no additional hydrogen cyanide, and at the same time utilizing a hazardous waste by-product such as acrylic acid, and converting it to a more valuable product. Example 13 An identical test to Example 12 except using a non-aqueous feed, was conducted at 0.5 mole of waste. organics to 1.0 mole of propylene. It contained components by mole % of 5.3 n-propanol, 3.3 isobutyl formate, 11.0 ethylene glycol, 12.8 iso-butanol, 1.5 ethyl ether, 0.6 m-xylene, 0.5 1-methyl-1-cyclohexene, and traces of other components thought capable of reaction with ammonia over a bismuth molybdate type catalyst. Analysis of the reactor effluent showed that these components were converted, in many instances to valuable products such as acrylonitrile, acetonitrile or methacrylonitrile, and a corresponding reduction in their organic waste. Dicyano benzenes were found from the m-xylene, showing that this is applicable to selected aromatics in a waste solution, as was a nitrile derivative of the olefinic substituted cyclohexene. Example 14 set forth below illustrates the practice of the present invention where methanol is injected above the catalyst bed height. Example 14 Methanol at a mole ratio of 0.4 to 1.0 for propylene was introduced into the reactor above the catalyst dense phase (>100% of the expanded catalyst bed height) into the dilute zone. Comparative analysis of the products and effluent before and after the introduction of methanol showed an ammonia reduction of 15% of that breaking through prior to the use of methanol. The above examples clearly illustrate the dramatic improvements (ammonia breakthrough reduction ranging from 15% to 100%) during the practice of the process of the present invention. Each of the examples shows a significant decrease (at least 15%) in the amount of NH 3 breakthrough thereby substantially reducing the amount of (NH 4 )2 S O 4 generated without any significant impact in acrylonitrile yield. While these examples are illustrative of the practice of the present invention they are not intended to limit applicants' invention to that illustrated and obviously many modifications and variations may be utilized in light of the above teaching. It is intended that the scope of applicants' invention be defined by the claims appended hereto.

Claims: A method for the substantial reduction of ammonia breakthrough during the manufacture of acrylonitrile comprising introducing a hydrocarbon selected from the group consisting of propane and propylene, ammonia and an oxygen containing gas into the lower portion of a fluid bed reactor containing a fluid bed ammoxidation catalyst to react in the presence of said catalyst to produce acrylonitrile which comprises introducing at least one oxygenate selected from the group of aldehydes, carboxylic acids, ketones, alcohols, esters or mixtures thereof and capable of reacting with ammonia into the upper portion of the fluid bed reactor at a point where the oxygenate does not substantially effect the reaction of the hydrocarbon, ammonia and oxygen containing gas to produce acrylonitrile and reacts with at least a portion of the unreacted ammonia present in the reactor to substantially reduce the amount of ammonia present in the reactor effluent exiting the reactor wherein the at least one oxygenate is introduced in an upward direction into the upper portion of the fluid bed reactor and/or the at least one oxygenate is capable of reacting with ammonia below its coking temperature. A method as claimed in claim 1 wherein the at least one oxygenate is introduced in an upward direction into the upper portion of the fluid bed reactor. A method as claimed in claim 1 wherein the at least one oxygenate is capable of reacting with ammonia below its coking temperature. The method of claim 2 wherein the hydrocarbon is selected to be propylene. The method of claim 3 wherein the hydrocarbon is selected to be propylene. The method of claim 4 wherein said oxygenate consists essentially of methanol. The method of claim 5 wherein said oxygenate consists essentially of methanol. The method of claim 6 wherein the methanol is injected into the upper portion of the fluid bed reactor at a location above at least 85 percent of the calculated expanded fluid catalytic bed height. The method of claim 7 wherein the methanol is injected into the upper portion of the fluid bed reactor at a location above at least 85 percent of the calculated expanded fluid catalytic bed height. The method of claim 8 wherein the methanol is injected into the upper portion of the fluid bed reactor at a location above at least 90 per cent of the calculated expanded fluid catalytic bed height. The method of claim 9 wherein the methanol is injected into the upper portion of the fluid bed reactor at a location above at least 90 per cent of the calculated expanded fluid catalytic bed height. The method of claim 6 wherein the methanol is injected into the fluid bed reactor through a conduit which maintains the temperature of the methanol below its coking temperature prior to exit into the reactor. The method of claim 12 wherein the inside of the conduit for said methanol is maintained at a temperature below the coking temperature of the methanol by providing a blanket of themal insulation about the outer surface of the conduit. The method of claim 12 wherein a second conduit is provided about the outside surface of the thermal insulation to further provide a protective surface for said thermal insulation. A method as claimed in claim 2 in which a fluid bed reactor contains a fluid bed ammoxidation catalyst capable of operating in an oxygen lean environment which comprises introducing into the upper portion of the fluid bed reactor (1) at least one oxygenate capable of reacting with ammonia and (2) an additional oxygen containing gas in an amount sufficient to enable said oxygenate to react with at least a portion of said ammonia at a point where the oxygenate and additional oxygen do not substantially affect the reaction of the propylenes, ammonia and oxygen containing gas to produce acrylonitrile, but reacts with at least a portion of the unreacted ammonia present in the reactor to substantially reduce the amount of ammonia present in the reactor effluent exiting the reactor. The process of claim 15 wherein the hydrocarbon is propylene. The method of claim 16 wherein the oxygenate is injected into the upper protion of the fluid bed reactor through a conduit which maintains the temperature of the oxygenate below its coking temperature prior to exit into the reactor. The method of claim 17 wherein the oxygenate is injected into the fluid bed reactor in an upward direction. The process of claim 18 wherein the oxygenate consists essentially of methanol. The process of claim 19 wherein the additional oxygen is added to the fluid bed reaction between the point of injection of the methanol and the point of injection for the hydrocarbon, ammonia and oxygen containing gas. The process of claim 20 wherein the additional oxygen containing gas is introduced into the reactor between 20 to 36cm (8 to 14 inches) from the point of introduction of the methanol. The process of claim 21 wherein the additional oxygen containing gas is introduced into the reactor in a downward direction. The process of claim 22 wherein the additional oxygen containing gas is introduced into the reactor at a point between 25 to 31cm (10 to 12 inches) from the methanol injection. The process of claim 22 wherein the mole ratio of additional oxygen containing gas per moles of methanol ranges from greater than 0 to 6. The process of claim 24 wherein the oxygen containing gas is air.

Inventors: BIGLER KENNETH L, BOTT PAUL E, FRIEDRICH MARIA S, KECKLER KENNETH P, KOCJANCIC FRANK J, MIKO STEVE J, REILING VINCENT G, ROWE STEVEN J, SEELY MICHAEL J, SHAW WILFRID G, SHUKI ALBERT R JR, SOCKELL EDWARD J, SURESH DEV D, TROTT LOUIS R, BIGLER, KENNETH L., BOTT, PAUL E., FRIEDRICH, MARIA S., KECKLER, KENNETH P., KOCJANCIC, FRANK J., MIKO, STEVE J., REILING, VINCENT G., ROWE, STEVEN J., SEELY, MICHAEL J., SHAW, WILFRID G., SHUKI, ALBERT R., JR., SOCKELL, EDWARD J., SURESH, DEV D., TROTT, LOUIS R.
Applicants: STANDARD OIL CO OHIO, THE STANDARD OIL COMPANY
Application year: 1994
Main classification: C07C253
IPC codes: C07C5, C01C3, B01J23, C07C253, C07B61, C07C255