Process for the preparation of an acid functional polyester resin

Abstract: A process for the preparation of a linear tertiary aliphatic carboxyl functional polyester resin by reacting a) at least one compound A' comprising one monofunctional primary- or secondary hydroxyl group and/or at least one compound A'' comprising one primary- or secondary hydroxyl group and one tertiary aliphatic carboxyl group and b) at least one aromatic or cycloaliphatic dicarboxylic acid compound B comprising two aromatic- or secondary aliphatic carboxyl groups or the anhydride thereof and c) at least one diol compound C comprising two aliphatic hydroxyl groups which may each independently be a primary or a secondary hydroxyl group and d) at least one dihydroxymonocarboxylic acid compound D comprising a tertiary aliphatic carboxyl group and two aliphatic hydroxyl groups, which may each independently be primary or secondary hydroxyl, the molar ratio of compounds A' : A'': B : C : D being M : N : X+Y+1 : X : Y, wherein M + N = 2 X ranges from 2 to 8 and Y ranges from 2-N to 8, at a temperature of from 100 to 240 °C, until essentially all the non-tertiary carboxyl groups as initially present in the reaction mixture have been reacted.

Description: The present invention relates to polyglycidyl polyester resin and to powder coating compositions comprising said polyglycidyl functional polyester resin. Powder coating compositions which have been known for the longest time, namely those based on the solid reaction products of 2,2-bis-(4-hydroxyphenyl)propane and epichlorohydrin, show only minor ultraviolet resistance and are therefore not suitable for applications requiring a high outdoor durability such as automotive topcoats. Triglycidylesters which can be used in outdoor durable coatings and in moulding compositions are disclosed in European Patent Application No. 447360 (EP-A-447,360). Due to the secondary nature of the terminal carboxyl functions present in the tricarboxylic acid adduct precursors, strongly alkaline conditions should be avoided during glycidation of these tricarboxylic acid adducts. As a result thereof the triglycidylester produced will contain a relatively high level of hydrolizable chlorine. This is reflected by example 2 of EP-A-447,360 which relates to the glycidation of the 2:1 adduct of hexahydrophtalic anhydride and dimethylolpropionic acid. The product obtained has a chlorine content of 1.5%. Such a high level of residual chlorine is generally undesirable in coating compositions. In addition, due to the fact that the triglycidylesters reported in EP-A-447,360 are liquid, they can not be applied in powder coating compositions. The most commonly used system for outdoor durable powder coatings are polyester/triglycidylisocyanurate (TGIC). For health and safety reasons however the use of TGIC is viewed with suspicion. TGIC is relatively toxic (Rat Oral LD 50 of 0.4 g/kg) and is mutagenic according to the Ames Mutagenicity Test. From the above prior art discussion it follows that there is a need for resin systems, which are particularly suitable for use in powder coating compositions which are relatively non toxic as compared to the current polyester/TGIC systems and show excellent outdoor durability in the cured state. Therefore it is an object of the invention to provide a polyglycidyl polyester resin obtainable by reacting linear tertiary aliphatic carboxyl functional polyester resin with epihalohydrin. Said polyglycidyl ester resin has been found to be particularly suitable for use in outdoor durable powder coating compositions which are relatively environmentally friendly. Accordingly the invention provides polyglycidyl polyester resin with epihalohydrin, obtainable by reacting linear tertiary aliphatic carboxyl functional polyester resin, obtainable by a process comprising the reaction of a) at least one compound A' comprising one monofunctional primary- or secondary hydroxyl group and/or at least one compound A" comprising one primary- or secondary hydroxyl group and one tertiary aliphatic carboxyl group and b) at least one aromatic or cycloaliphatic dicarboxylic acid compound B comprising two aromatic- or secondary aliphatic carboxyl groups or the anhydride thereof and c) at least one diol compound C comprising two aliphatic hydroxyl groups which may each independently be a primary or a secondary hydroxyl group and d) at least one dihydroxymonocarboxylic acid compound D comprising a tertiary aliphatic carboxyl group and two aliphatic hydroxyl groups, which may each independently be primary or secondary hydroxyl, the molar ratio of compounds A': A": B : C : D being M : N : X+Y+1 : X : Y, wherein M + N = 2 X ranges from 2 to 8 and Y ranges from 2-N to 8, at a temperature of from 100 to 240 °C, until essentially all the non-tertiary carboxyl groups as initially present in the reaction mixture have been reacted, with an excess epihalohydrin in the presence of a suitable base and a catalyst. The linear tertiary aliphatic carboxyl functional polyester resin starting material is essentially free from non tertiary carboxyl groups when it has an acid value which practically corresponds to the theoretical acid value calculated on the basis of the amount of tertiary carboxyl groups of the reactants as initially present in the reaction mixture. The term practically is used herein to indicate a deviation from the theoretical value of ± 5% at most. This is determined by standard alkali metric titration. For those skilled in the art it will be understood that the molecular weight distribution and number average molecular weight of the carboxyfunctional polyester resin will depend on the specific reactants and the ratios applied in the process of the invention. Whilst the tertiary aliphatic carboxyl groups present in compounds A" and D practically do not react under the esterification conditions employed, glycidation of these tertiary aliphatic carboxyl groups with epihalohydrin can be performed under standard alkaline conditions whereby a polyglycidylester resin can be obtained which contains a low hydrolizable halogen content, usually lower than 0.5% by weight based on the total weight of the composition. The preparation of the carboxyfunctional polyester resin may be carried out according to conventional esterification methods, preferably by azeotropic condensation. In particular, the condensation is carried out by charging the compounds A to D simultaneously to the reactor whereafter the temperature is increased from room temperature to from 200 to 220 °C during a period of 6 to 8 hours, thus allowing the reaction to initiate and to proceed under continuous azeotropic removal of water. Generally the azeotropic removal of water is being continued until a reaction product is obtained which has an acid value which corresponds to the theoretical acid value as referred to above. An esterification catalyst known in the art, such as for example dibutyltinoxide, paratoluenesulfonic acid, tinoctoate, zincoctoate and lithiumricinoleate may be used in the esterification process but is in general not required. Suitable compounds A' are aliphatic and cycloaliphatic alcohols having one primary or one secondary hydroxyl group and having of from 1 to 6 carbon atoms, such as for example methanol, isopropanol, neopentanol, 2-butanol and cyclohexanol. Suitable compounds A" are aliphatic and cycloaliphatic alcohols having one primary or one secondary hydroxyl group and having of from 1 to 6 carbon atoms and having in addition one tertiary aliphatic carboxyl group such as for example cyclohexane-1-methyl-4-hydroxy carboxylic acid the 1:1 (molar ratio) reaction product of dimethylolpropionic acid and cyclohexanecarboxylic acid, and hydroxypivalic acid. Hydroxypivalic acid is a particularly preferred compound A". Suitable compounds B are for example phthalic acid (PA), tetrahydrophthalic acid, hexahydrophthalic acid (HHPA), methylhexahydrophthalic acid, terephthalic acid, isophthalic acid, endomethylenetetrahydrophthalic acid, methylendomethylenetetrahydrophthalic acid, 1,4-cyclohexanedicarboxylic acid and 1,3-cyclohexanedicarboxylic acid or combinations thereof; HHPA being particularly preferred. Suitable compounds C include branched aliphatic-, cycloaliphatic-, or araliphatic compounds, containing two aliphatic hydroxyl groups, each individually being either a primary or a secondary hydroxyl group, such as for example propylene glycol, neopentylglycol, hydrogenated diphenylolpropane (HDPP), hydrogenated 4,4'-dihydroxydiphenyl, 1,4-cyclohexanedimethylol, 1,4-dihydroxycyclohexane, hydroxypivalylhydroxypivalate and 2-butyl-2-ethyl-1,3-propanediol or mixtures thereof; HDPP being particularly preferred. A typical example of a suitable compound D is dimethylolpropionic acid. Most conveniently epichlorohydrin is being used for the conversion of the intermediate carboxyl functional polyester resin into the corresponding polyglycidylester resin. The polyglycidylester resin of the invention is suitable for use in powder coating compositions, which in the cured state shows good outdoor durability. Moreover in view of the polymeric nature of the polyglycidylester resin of the invention a lower level of toxicity as compared to TGIC is foreseen and therefore they can advantageously be used as an alternative to TGIC in powder coatings. It was found that those polyglycidylester resins derived from the linear tertiary aliphatic carboxyl functional polyester resins whilst X ranges from 3 to 6 and Y simultaneously ranges from 2 to 4 are particularly suitable for use in outdoor durable powder coating compositions. The curable powder coating compositions of the invention may be prepared by addition of a cross-linking resin to the polyglycidylester resin obtainable by glycidating the linear tertiary aliphatic carboxyl functional polyester resin. The amount of cross-linking compound used in the powder coating compositions of the invention will normally be such so as to provide about equal amounts of reactive groups of the cross-linking compound and of the tertiary aliphatic carboxyl groups present in the linear tertiary aliphatic carboxyl functional polyester resin or of the epoxy groups present in the polyglycidylester resin. Suitable cross-linking resins for use in combination with the polyglycidylester resins of the present invention are for example the (corresponding) acid functional polyester resin used as starting material for the preparation of the polyglycidyl polyester resins of the present invention, solid polyacids such a sebacic acid, adipic acid, 1,12-dodecanedioic acid; anhydrides such as polyazeleic polyanhydride and trimellitic anhydride; acid functional polyesters such as the reaction product of one mole of trimethylopropane and 3 moles of hexahydrophthalic anhydride, the reaction product of 1,6-hexanediol with a molar excess of 1,12-dodecanedioic acid, the reaction product of 4 mols 1,10-decanedicarboxylic acid, 1.49 mols hexanediol, 0.47 mols 1,1,1-tris-(hydroxymethyl)-propane and 0.27 mols pentaerythritol, the reaction product of 4 mols 1,10-decanedicarboxylic acid, 1.2 mols hexanediol, 0.45 mols trimethylolpropane, 0.29 mols pentaerythritol and 0.21 mols dimethylolpropionic acid and the reaction product of one mole of hexamethoxymethylmelamine and 3 moles of hydroxypivalic acid; cyanuric acid; and solid basic curing agents such as dicyandiamide and BF 3 -complexes. The powder coating compositions of the present invention may further comprise a catalyst and optionally other additives, as known in the art to be suitable for use in powder coating compositions. Suitable catalyst are for example quaternary ammonium and phosphonium salts; metal salts/compounds such as for example stannous(II)octoate; basic compounds such as for example the imidazoles; and tertiary amines such as for example diazabicycloundecene. The amount of catalyst used will usually somewhere in the range of from 0.1 to 2% by weight based on the weight of the total powder coating composition. Suitable cure times and cure temperatures of the powder coating compositions of the invention are those conventionally applied in connection with powder coating systems. The invention is illustrated by the following examples. Example 1 (control) Preparation of linear tertiary aliphatic carboxyl functional polyesters 1 to 5. Compounds A to D were charged in molar amounts as indicated in table 1 in a roundbottom glass reactor, equipped with Dean & Stark Trap with reflux-condensor, temperature control, nitrogen inlet and stirrer. The mixture was then heated to 150 °C in 30 minutes and xylene was added (5% weight on the total weight of the reaction mixture). The temperature of the reaction mixture was increased in two hours to 210 °C and kept at 210 °C until the theoretical acid value as referred to above was reached. The acid functional polyester thus formed was discharged and allowed to cool down to room temperature. Linear acid functional polyester resin 1 2 3 4 5 HPA (A") 2 2 2 2 2 HHPA (B) 9 6 4 - 11 DMPA (D) 2 1 - 2 4 HDPP (C) 6 4 3 6 6 PA (B) - - - 9 - 1) Numbers given represent the amount of moles of a particular compound charged to the reactor in the process of example 1 for the preparation of the linear tertiary carboxyl functional polyester resins 1 to 5. 2) The chemical compounds represented by the abbreviations used are: HPA: hydroxypivalic acid HHPA: hexahydrophthalic anhydride DMPA: dimethylolpropionic acid HDPP: hydrogenated diphenylolpropane PA: phthalic anhydride. Example 2 Preparation of polyglycidylester resins I to V. An amount equalling 1 carboxyl group equivalent of a linear tertiary aliphatic carboxyl functional polyester resin 1 to 5 as prepared in example 1 was dissolved in 8 moles epichlorohydrin (ECH) and isopropylalcohol (IPA). The solution was charged to a 3 litre glass-reactor equipped with a temperature control, stirrer and reflux condensor. Next the temperature was raised to 70 °C, followed by the gradual addition of an aqueous solution of 1.2 moles NaOH over a period of time of 60 minutes. After an additional reaction period of 10 minutes the reactor content was allowed to settle and the aqueous phase was separated from the organic phase. The organic phase was vacuum flashed to remove water, IPA and ECH. The resulting product was dissolved in toluene and the organic phase was washed three times with water whereafter the organic phase was vacuum flashed to remove toluene. The glycidylester thus obtained was discharged and allowed to cool down. Characteristics of the solid polyglycidylester resins prepared are presented in table 2. Resin Characteristics Acid-functional polyester resin 1 2 3 4 5 Acid value (mmol/kg) Found 1200 1320 1280 1250 1550 Theoretical 1200 1330 1260 1280 1550 Softening point (°C) 115-125 95-110 90-105 130-140 105-119 Polyglycidyl- ester resin I II III IV V EGC (mmol/kg) 1000 970 1020 1000 1180 Softening point (°C) 85-90 75-85 75-85 90-95 60-76 Hydrolyzable Chlorine content (%w) < 0.32 < 0.35 < 0.5 < 0.5 <0.5 Example 3 Powder coating compositions A and B according to the invention. All ingredients as indicated in Table 3 were mixed at room temperature, then melt-blended on a Buss single screw extruder at 110 °C. The extrudate was chilled, flaked, ground in a micromill and classified through 106 micrometre mesh. The powder was electrostatically sprayed onto chromate pretreated, 2 mm thick aluminium panels. The coated panels were baked at 200 °C for 15 minutes. The resultant coatings (thickness 40-60 micrometres) were very smooth, hard, glossy and exhibited good mechanical properties and good weathering resistance, that is less than 10% reduction in gloss after exposure for 1200 hours in a Xenon type weather-O-meter running the SAE J1960 test method. Ingredients A B Polyglycidylester resin I 181 181 Semi crystalline-acid functional polyester 607 Semi crystalline-acid functional polyester 607 Titaniumdioxide 167 167 Modaflow 10.1 10.1 Benzoin 6.8 6.8 Actiron SNO 30 29.0 29.0

Claims: A polyglycidyl polyester resin obtainable by reacting linear tertiary aliphatic carboxyl functional polyester resin, obtainable by a process comprising the reaction of: a) at least one compound A' comprising one monofunctional primary- or secondary hydroxyl group and/or at least one compound A" comprising one primary- or secondary hydroxyl group and one tertiary aliphatic carboxyl group and b) at least one aromatic or cycloaliphatic dicarboxylic acid compound B comprising two aromatic- or secondary aliphatic carboxyl groups or the anhydride thereof and c) at least one diol compound C comprising two aliphatic hydroxyl groups which may each independently be a primary or a secondary hydroxyl group and d) at least one dihydroxymonocarboxylic acid compound D comprising a tertiary aliphatic carboxyl group and two aliphatic hydroxyl groups, which may each independently be primary or secondary hydroxyl, the molar ratio of compounds A' : A" : B : C : D being M : N : X + Y + 1 : X : Y, wherein M + N = 2, X ranges from 2 to 8, and Y ranges from 2-N to 8, at a temperature of from 100 to 240 °C, until essentially all the non-tertiary carboxyl groups as initially present in the reaction mixture have been reacted, with an excess epihalohydrin in the presence of a suitable base and a catalyst. polyglycidyl polyester resin according to claim 1, derived from a linear tertiary aliphatic carboxyfunctional polyester resin, obtainable by charging the compounds A to D simultaneously to the reactor whereafter the temperature is increased of from room temperature to of from 200 to 220 °C during a period of time of from 6 to 8 hours, thus allowing the reaction to initiate and to proceed under continuous azeotropic removal of water, whereafter the reaction is being continued under similar conditions, if necessary. A polyglycidyl polyester resin according to claim 1 or 2, derived from a tertiary aliphatic carboxyfunctional polyester resin, obtainable by a process wherein the reactants A) to D) are reacted in presence of an esterification catalyst. A polyglycidyl polyester resin as claimed in any one of the claims 1 to 3, wherein reactant A" is hydroxypivalic acid. A polyglycidyl polyester resin according to any one of the claims 1 to 4, wherein reactant B is hexahydrophthalic acid. A polyglycidyl polyester resin according to the claims 1 to 5, wherein reactant C is hydrogenated diphenylolpropane. A polyglycidyl polyester resin according to the claims 1 to 6, wherein reactant D is dimethylolpropionic acid. A polyglycidyl polyester resin according to the claims 1 to 7, wherein X is 6 and Y is 2 in the starting polyester. A polyglycidyl polyester resin as claimed in claims 1-8, wherein the epihalohydrin used is epichlorohydrin. A polyglycidyl polyester resin according to claims 1-8, containing a hydrolyzable halogen content lower than 0.5% by weight, based on the total weight of the composition. A powder coating composition comprising a polyglycidyl polyester resin as claimed in claims 1-10 and a cross-linking agent. A powder coating composition according to claim 11, comprising as cross-linking agent a linear tertiary aliphatic carboxyfunctional polyester resin, obtainable by a process comprising the reaction of: a) at least one compound A' comprising one monofunctional primary- or secondary hydroxyl group and/or at least one compound A" comprising one primary- or secondary hydroxyl group and one tertiary aliphatic carboxyl group and b) at least one aromatic or cycloaliphatic dicarboxylic acid compound B comprising two aromatic- or secondary aliphatic carboxyl groups or the anhydride thereof and c) at least one diol compound C comprising two aliphatic hydroxyl groups which may each independently be a primary or a secondary hydroxyl group and d) at least one dihydroxymonocarboxylic acid compound D comprising a tertiary aliphatic carboxyl group and two aliphatic hydroxyl groups, which may each independently be primary or secondary hydroxyl, the molar ratio of compounds A' : A" : B : C : D being M : N : X + Y + 1 : X : Y, wherein M + N = 2, X ranges from 2 to 8, and Y ranges from 2-N to 8, at a temperature of from 100 to 240 °C, until essentially all the non-tertiary carboxyl groups as initially present in the reaction mixture have been reacted.

Inventors: FRERIKS JAN, GROENVELD PIETER, KOOIJMANS PETRUS GERARDUS, RAUDENBUSCH WERNER THEODOR, FRERIKS, JAN, GROENVELD, PIETER, KOOIJMANS, PETRUS GERARDUS, RAUDENBUSCH, WERNER THEODOR
Applicants: RESOLUTION RES NEDERLAND BV, RESOLUTION RESEARCH NEDERLAND B.V.
Application year: 1994
Main classification: C08G63
IPC codes: C09D167, C09D163, C08G63, C08G59