Active matrix circuit board and method of manufacturing it

Abstract: An active matrix circuit board has on the surface side of an insulated substrate a drive circuit area comprising a CMOS circuit comprising a first thin-film transistor of a first conductive type and a second thin-film transistor of a second conductive type wherein the source-drain area is formed self-aligned to the gate electrode, and a pixel area comprising a third thin-film transistor (TFT-C) of the first conductive type. The third thin-film transistor has an offset gate structure whereby the source-drain area (332, 333) is in a position separated a predetermined distance in the lateral direction from the edge of the gate electrode (335).

Description: The present invention relates to a manufacturing method for an active matrix circuit board. Thin-film transistors (hereafter "TFT") using a polycrystalline silicon film are used as pixel transistors in liquid crystal display panels and other active matrix circuit boards. Of available liquid crystal display panels, built-in drive circuit type (built-in peripheral circuit type) active matrix circuit boards in which the drive circuit is formed using TFT in the area peripheral to the pixel area are used in liquid crystal display panels for viewfinders and projectors due to the packaging technology problem that making electrical connections to narrow pitch terminals is difficult. As a result, TFT for the drive circuit area and TFT for the pixel area are both formed on a single active matrix circuit board. Of these TFT, a low OFF current is required in the TFT of the pixel area so that the charge written through the pixel electrodes can be held. Polycrystalline silicon TFT, however, may use an offset gate structure wherein a source-drain area is provided at a position separated from the edge of the gate electrodes because the OFF current is high. In addition, a low concentration area may be provided at the edge of the drain area, and a drain structure (LDD structure) used with the field strength in this area reduced. The following manufacturing method is conventionally used to manufacture thin-film transistors with such a structure. When n-channel type TFT 1200a in the drive circuit area, p-channel type TFT 1200b in the drive circuit area, and n-channel type TFT 1200c in the pixel area are formed as shown in Fig. 8 (a) from left to right facing the figure, first, second, and third silicon films 1202, 1202, 1203 are first formed on the surface side of substrate 1201. The surface sides of the first, second, and third silicon films 1202, 1202, 1203 are then covered by gate insulation film 1211. After that, a conductive film forming the gate electrode is formed on the surface side of the gate insulation film 1211, this is masked with resist 1213 for patterning, and gate electrode 1212 is formed. Next, as indicated by arrow 1214, an impurity that will be the donor is ion implanted, and source-drain area 1207 is formed. Next, gate electrode 1212 is over-etched with resist 1213 as the mask, and gate electrode 1212 is narrowed as shown in Fig. 8 (b). As a result, the length of gate electrode 1212 is shorter than the length of the area (channel formation area) in first, second, and third silicon films 1202, 1202, 1203 in which the impurity is not introduced, and the offset gate structure is formed. Next, as shown in Fig. 8 (c), an impurity that will be the acceptor is ion implanted (arrow 1221) to the second silicon film 1202 with the first and third silicon films 1202, 1203 covered by resist 1215. Because the donor impurity was previously introduced to second silicon film 1202, the acceptor impurity is introduced at a high concentration. It is to be noted that when TFT 1200a and 1200c are formed with an LDD structure, resist 1215 is removed after injecting the acceptor impurity, and a donor impurity is ion injected at an appropriate dosage. In the TFT thus formed, the OFF current level can be sufficiently lowered because concentration of the electrical field at the drain edge can be alleviated due to the offset structure or LDD structure. The following problems exist with the conventional manufacturing method thus described, however. First, even though TFT electrical characteristics vary with the gate length, this method sets the gate length by over-etching the gate electrode, and it is therefore difficult to control the gate length. For example, when a gate electrode composed of polycrystalline silicon is plasma etched, it is possible to determine the completion of etching because the plasma emission strength changes at the etching end point if patterning is normal, but it is difficult to reliably control the end point because the plasma emission strength does not change with over-etching. In addition, it is also difficult to control over-etching when over-etching is controlled by the etching time because the etching speed varies slightly with the operating conditions, etc., of the etching equipment. As a result, the ON current characteristic and other electrical characteristics of TFT manufactured with conventional methods inevitably vary due to variations in gate length and offset length. Variations of this type are fatal defects in drive circuit TFT formed by the same process. Due to over-etching, it is also difficult to increase device pitch. More specifically, the active matrix circuit board must be designed with a large pattern dimension to accommodate variations in gate electrode over-etching, and designs with such large margins result in large waste in the active matrix circuit board design. In addition, conventional manufacturing methods are not suited to high resolution liquid crystal display panels, and are an obstruction to reducing the basic pattern dimension of the active matrix circuit board from 5 µm to 2 µm or 3 µm, or even smaller dimensions. Second, high temperature processing exceeding 600°C is required to activate the ion injected impurity in LDD structures. With such high temperature processing, however, it is not possible to use low-cost glass substrates. As a result, conventional manufacturing methods also interfere with increasing display panel screen size and reducing display panel cost. Furthermore, conventional ion injection technologies are not well suited to processing large circuit boards because of the narrow injection area. Technologies for implanting the generated ions without mass separation have been studied with the objective of solving these problems. For example, a method for using a mixture of an impurity gas diluted with hydrogen as the doping gas and implanting the ions generated from this mixture without mass separation has been studied, and the impurity has been activated at a relatively low temperature of about 300°C. However, this method cannot activate a silicon film implanted with a low ion concentration where the impurity concentration is 1 x 10 19 /cm 3 or less, and it is still not possible to manufacture an LDD structure TFT in a low temperature process. An active matrix circuit board having on the surface side of an insulated substrate a drive circuit area comprising a CMOS circuit comprising a first thin-film transistor of a first conductive type and a second thin-film transistor of a second conductive type , and a pixel area comprising a third thin-film transistor of the first conductive type, is disclosed in EP-A-0 342 925. JP-A-4-293023 discloses a similar active matrix circuit board in which the impurity density in the channel area of TFTs in the pixel area is greater than that in the channel area of TFTs in the drive circuit area. The document JP-A-63-204769 discloses a TFT having an LDD structure with source and drain regions each composed of two portions, a first portion next to the channel and a second portion contiguous to the first portion on the side remote from the channel. The second portions have a higher impurity concentration and are used as contact regions for contact with a source and drain electrode, respectively. The document EP-A-0 544 229 (prior art according to Article 54(3) EPC) discloses an active matrix circuit board having a drive circuit area equipped with a CMOS circuit comprising a first thin-film transistor of a first conductivity type and a second thin-film transistor of a second conductivity type, and a pixel area comprising a third thin-film transistor of said first conductivity type, wherein said source-drain area is not formed self-aligned to the gate electrode. All three transistors have an LDD structure with The low concentration region of the source-drain area of pixel transistor is lower than that of the first transistor though not specified. The document US-A-4,528,480 discloses an AC drive type electroluminescent display device comprising a combination of an electroluminescent element, a pixel transistor for driving the electroluminescent element, an AC current source, a switching transistor for on/off controlling the pixel transistor and a capacitor. To achieve a high breakdown voltage of the pixel transistor it has offset gate regions that separate source and drain regions from the edges of the gate electrode. EP-A-0 513 590 discloses a thin-film transistor for use in the pixel area of an active matrix circuit board. To obtain a high ION/IOFF ratio the document suggests to provide an offset between the gate and each of source and drain regions. The offset is obtained by first forming a gate and forming source and drain regions self-aligned to the gate. Subsequently the gate is subjected to anodic oxidation to form the offset. Considering the above problems, the object of the present invention is to provide a method allowing to improve the structure of the source-drain area, and to thus achieve an active matrix circuit board with thin-film transistors film in which the OFF current characteristics can be improved. This object is achieved by a method as claimed. In this invention, the first conductive type and second conductive type are opposite conductive types, meaning that if the first conductive type is an n-type, then the second conductive type is a p-type. Inversely, if the first conductive type is a p-type, then the second conductive type is an n-type. In addition, "impurity ions" in this invention mean ions that are either donors or acceptors. In an active matrix circuit board with an integrated drive circuit area obtained by the method according to the present invention, the thin-film transistor of the pixel area has an offset gate structure whereby the source-drain area is in a position laterally offset by a predetermined distance from the edge of the gate electrode. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a simple block diagram of an active matrix circuit board with a built-in drive circuit. Fig. 2 is a simple block diagram typically showing the structure of the pixel area of an active matrix circuit board. Fig. 3 is a cross sectional diagram typically showing the basic structure of a liquid crystal display panel. Fig. 4 is a cross sectional diagram typically showing the TFT structure formed in the pixel area and drive circuit area of an active matrix circuit board. Fig. 5 shows a process flow of the manufacturing method of the active matrix circuit board in Fig. 4. Fig. 6 is a cross sectional diagram typically showing the TFT structure formed in the pixel area and drive circuit area of an active matrix circuit board obtained according to an embodiment of the present invention. Fig. 7 shows a process flow of the manufacturing method of the active matrix circuit board in Fig. 6. Fig. 8 shows a process flow of the manufacturing method of conventional TFT. Before describing the structure of an active matrix circuit board manufactured according to the method of one embodiment of the present invention the basic structure of an active matrix circuit board with a built-in drive circuit and used in liquid crystal display panels is described. Fig. 1 is a simple block diagram of an active matrix circuit board with a built-in drive circuit, Fig. 2 is a simple block diagram typically showing the structure of the pixel area of an active matrix circuit board, and Fig. 3 is a cross sectional diagram typically showing the basic structure of a liquid crystal display panel. In Fig. 1, active matrix circuit board 10 is divided into a pixel area 10a and drive circuit areas 10b, 10c (peripheral circuit part). Pixel region 13 is divided and formed in pixel area 10a by scanning lines (gate lines) 11a, 11b... (11) connected to drive circuit area 10b (scanning line drive circuit), and data lines 12a, 12b... (12) connected to drive circuit area 10c (data line drive circuit) as shown in Fig. 2. TFT 10d, which switches between a state connecting and a state interrupting the data line 12 side and the pixel electrode side based on the scanning signal from scanning line 11, is formed in pixel region 13. A CMOS circuit is also formed in drive circuit areas 10b, 10c by thin-film transistors of a different conductive type. Of these thin-film transistors, a small OFF current characteristic is required in TFT 10d of pixel area 10a so that a sufficient charge can be held in liquid crystal capacitance 10f. Because high speed operation compatible with high quality display operation is required in the thin-film transistor of drive circuit areas 10b, 10c, a thin-film transistor with a self-alignment structure is generally used in drive circuit areas 10b, 10c. It is to be noted that, as shown in Fig. 2, there are cases in which storage capacitance 10e is formed in pixel region 13, and this storage capacitance 10e may be constructed overlaid with part of the preceding scanning line 11 as the top pole and part of the drain electrode of TFT 10d as the bottom pole. Therefore, if the OFF current of TFT 10d of pixel area 10a is large, it is necessary to increase storage capacitance 10e, and the aperture ratio of pixel region 13 is decreased. Note that liquid crystal capacitance 10f is the capacitance when active matrix circuit board 10 and counter circuit board 16 on which counter electrode 15 is formed are placed in opposition sandwiching liquid crystals 17 as shown in Fig. 3. Thus, three types of thin-film transistors, including a pair of opposite conductive type thin-film transistors in the drive circuit area and a thin-film transistor in the pixel area, are formed because the characteristics required in the thin-film transistors are different in a built-in drive circuit type active matrix circuit board 10. The following structure and manufacturing method can be used so that different types of thin-film transistors can be efficiently manufactured. Fig. 4 is a cross sectional diagram typically showing, of the thin-film transistors (hereafter "TFT") formed in the active matrix circuit board, the structure of the TFT formed in the pixel area and the n-channel type TFT and p-channel type TFT formed in the drive circuit area. In Fig. 4, in active matrix circuit board 100, n-channel type TFT-A of the drive circuit area, p-channel type TFT-B of the drive circuit area, and n-channel type TFT-C of the pixel area are formed on a transparent insulated substrate 101 in order from the left side as looking at the figure. The CMOS circuit is formed in the drive circuit area by TFT-A and TFT-B. Gate insulation film 114 is formed on the surface side of channel formation area 111 and source-drain areas 112, 113, and gate electrode 115 is formed on the surface side of this gate insulation film 114 in TFT-A. Source-drain areas 112, 113 are n + high concentration areas with an impurity concentration equal to or greater than 1 x 10 19 /cm 3 , e.g., 1 x 10 20 /cm 3 , and are formed self-aligned to gate electrode 115. Gate insulation film 124 is formed on the surface side of channel formation area 121 and source-drain areas 122, 123, and gate electrode 125 is formed on the surface side of this gate insulation film 124 in TFT-B. Source-drain areas 122, 123 are p + high concentration areas with an impurity concentration equal to or greater than 1 x 10 19 /cm 3 , e.g., 1 x 10 20 /cm 3 , and are formed self-aligned to gate electrode 125. Gate insulation film 134 is formed on the surface side of channel formation area 131 and source-drain areas 132, 133, and gate electrode 135 is formed on the surface side of this gate insulation film 134 in TFT-C. Source-drain areas 132, 133 are formed as n - low density areas with an impurity concentration equal to or less than 1 x 10 19 /cm 3 , e.g., 5 x 10 18 /cm 3 , and are formed self-aligned to gate electrode 135. Therefore, a large ON current can be obtained in TFT-A and TFT-B of the drive circuit area. In addition, the OFF current is small in the TFT-C of the pixel area because source-drain areas 132, 133 are low concentration of impurities. As a result, high resolution, high quality display can be achieved in a liquid crystal display panel using the active matrix circuit board 100 of this example because high speed operation is possible in the drive circuit area and the written charge can be sufficiently maintained in the pixel area. The manufacturing method of active matrix circuit board 100 of such a structure is described with reference to Fig. 5. Fig. 5 shows a process flow of a manufacturing method of the active matrix circuit board. First, as shown in Fig. 5 (a), after forming a polycrystalline silicon film on the surface side of insulated substrate 101, this is patterned to form silicon films 110, 120, 130. Silicon film 110 is a first silicon film for forming TFT-A in the drive circuit area, and silicon film 120 is a second silicon film for forming TFT-B in the drive circuit area. Silicon film 130 is a third silicon film for forming TFT-C in the pixel area (first process). Next, gate insulation films 114, 124, 134 are formed on the surface side of each silicon film 110, 120, 130 (second process). Next, after forming a polycrystalline silicon film on the surfaces of gate insulation films 114, 124, 134 (the entire surface of insulated substrate 101), a high concentration impurity is introduced into it. The polycrystalline silicon film into which an impurity was introduced is then patterned using photoetching technologies to form gate electrodes 115, 125, 135. The gate lines are simultaneously formed with the same materials when forming gate electrodes 115, 125, 135 (third process). It is to be noted that because the etching end point can be positively confirmed due to dry etching using CF 4 plasma being used in the present example for patterning the polycrystalline silicon film, the dimensions of the silicon film after patterning can be precisely controlled. Next, as shown by arrow P + , low concentration phosphorus ions are implanted at a 5 x 10 13 /cm 2 dose into silicon films 110, 120, 130 using gate electrodes 115, 125, 135 as a mask (low concentration area formation process). As a result, low concentration areas 110a, 120a, 130a with a 5 x 10 18 /cm 3 impurity concentration are formed self-aligned to gate electrodes 115, 125, 135 in silicon films 110, 120, 130. Low concentration area 130a becomes source-drain areas 132, 133 of TFT-C without further ion implanting in the following processes. In addition, that part of silicon film 130 positioned directly below gate electrode 135 becomes channel formation area 131. Next, as shown in Fig. 5 (b), after masking the side with silicon films 120. 130 with resist 140, high concentration phosphorus ions are implanted at a 1 x 10 15 /cm 2 dose to silicon film 110 (low concentration area 110a) as shown by arrow P + (fourth process). As a result, low concentration area 110a becomes source-drain area 112, 113 (n + high density area) with a 1 x 10 20 /cm 3 impurity concentration formed self-aligned to gate electrode 115. In addition, that part of silicon film 110 positioned directly below gate electrode 115 becomes channel formation area 111. Next, as shown in Fig. 5 (c), after masking the sides with silicon films 110, 130 with resist 150, high concentration boron ions are implanted at a 1 x 10 15 /cm 2 dose to silicon film 120 (low concentration area 120a) as shown by arrow B + (fourth process). As a result, low concentration area 120a becomes source-drain areas 122, 123 (p + high density area) with a 1 x 10 20 /cm 3 impurity concentration formed self-aligned to gate electrode 125. In addition, that part of silicon film 120 positioned directly below gate electrode 125 becomes channel formation area 121. In this way, even when three types of TFT are formed on one active matrix circuit board 100, a low concentration impurity is also implanted to the drive circuit area side in the process forming the low concentration area on the pixel area side, and a high concentration area is formed there by the high concentration impurity implanted to the drive circuit area side. Therefore, the impurity concentration of each area can be separately controlled while holding the number of masking operations to a minimum. Therefore, a TFT having an optimal structure can be manufactured by this manufacturing method without side etching the gate electrode. As a result, the display definition of the liquid crystal display panel can be improved because the ON current characteristic of the drive circuit area TFT and the OFF current characteristic of the pixel area TFT can be improved, and the electrical characteristics are stable. When the impurity concentration of the source-drain area is varied in an n-channel type TFT, the ON current drops because the electrical resistance of the source-drain area increases as the dose is reduced. Furthermore, the OFF current drops because electrical field strength between the drain area and gate electrode is decreased in addition to the electrical resistance of the source-drain area increasing as the dose is reduced. Therefore, it is sufficient to form the source-drain area as a low concentration area in the pixel area TFT where a small OFF current is required. Because a low OFF current is required in the TFT-C in the pixel area through the gate voltage Vg range from 0 V to approximately -10 V, the impurity dose to the source-drain areas 132, 133 is less than or equal to 1 x 10 14 /cm 2 , and preferably less than 5 x 10 13 /cm 2 . However, because the level of the TFT-C OFF current differs according to the setting conditions and the specifications of the liquid crystal display panel in which active matrix circuit board 100 is mounted, the impurity concentration of source-drain areas 132, 133 is set to an optimal level according to the specifications and setting conditions. The ON current of TFT-A and TFT-B in the drive circuit area is generally, however, preferably greater, and when gate voltage Vg is 10 V, drain current Id must be 10 µA or greater. Therefore, the impurity dose to the source-drain area of TFT-A and TFT-B must be approximately 1 x 10 14 /cm 2 or greater. It is to be noted that the TFT ON current and OFF current are also dependent on the film thickness of the polycrystalline silicon film in the channel formation area and the film thickness of the gate insulation film, in addition to the impurity concentration of the source-drain area. Furthermore, the electrical resistance of the source-drain area affecting the ON current and OFF current is also dependent on the film thickness and polycrystallinity of the source-drain area. Moreover, in addition to the dosage, the impurity concentration of the source-drain area is also affected by the ion energy during implantation and the film thickness of the gate insulation film. Therefore, the dosage is set as may be required with consideration for the ion energy and the film thickness of the gate insulation film. Embodiment The structure of the active matrix circuit board of this embodiment is characterized by forming a pad area, which is a high concentration area, only in the source-drain area of the n-channel type TFTS. Fig. 6 is a cross sectional diagram typically showing the structure of the TFT formed in an active matrix circuit board according to the present embodiment. In active matrix circuit board 400 of this embodiment, gate insulation film 414 is formed on the surface side of channel formation area 411 and source-drain areas 412, 413 in TFT-A, and gate electrode 415 is formed on the surface side of this gate insulation film 414. Source-drain areas 412, 413 are n + high concentration areas with an impurity concentration of 1 x 10 19 /cm 3 , e.g., 1 x 10 20 /cm 3 , formed self-aligned to gate electrode 415. Source-drain areas 412, 413 comprise thin top layer source-drain areas 412a, 413a formed from the same polycrystalline silicon film as channel formation area 411, and thick bottom layer source-drain areas 412b, 413b. Gate insulation film 124 is formed on the surface side of channel formation area 121 and source-drain areas 122, 123, and gate electrode 125 is formed on the surface side of this gate insulation film 124 in TFT-B. Source-drain areas 122, 123 are p + high density areas with an impurity concentration equal to or greater than 1 x 10 19 /cm 3 , e.g., 1 x 10 20 /cm 3 , and are formed self-aligned to gate electrode 125. Gate insulation film 434 is formed on the surface side of channel formation area 431 and source-drain areas 432, 433, and gate electrode 435 is formed on the surface side of this gate insulation film 434 in TFT-C. Source-drain areas 432, 433 comprise thin top layer source-drain areas 432a, 433a formed from the same polycrystalline silicon film as channel formation area 431, and thick bottom layer source-drain areas 432b, 433b. Top layer source-drain areas 432a, 433a are non-doped areas. Bottom layer source-drain areas 432b, 433b, however, are n + high concentration areas with an impurity concentration of 1 x 10 19 /cm 3 , e.g., 1 x 10 20 /cm 3 . As a result, that part of top layer source-drain areas 432a, 433a positioned near the edge of gate electrode 435 becomes non-doped offset areas 432c, 433c. It is to be noted that while not shown in the figures, the source electrodes and drain electrodes of TFT-A and TFT-C are connected to bottom layer source-drain areas 412b, 413b, 432b, 433b. In TFT-A and TFT-B of the drive circuit area thus formed, source-drain areas 412, 413, 122, 123 are formed self-aligned to gate electrodes 415, 125, and are formed as high concentration areas with a low electrical resistance. Furthermore, because source-drain areas 412, 413 are formed in two layers with a thick film thickness, the electrical resistance is low. Therefore, a high ON current can be obtained in TFT-A and TFT-B of the drive circuit area. In the same way, because the film thickness is thick in source-drain areas 432, 433 of TFT-C in the pixel area, and source-drain areas 432b, 433b, which are high concentration areas, are formed, a high ON current can be obtained because the electrical resistance there is low. Nevertheless, because TFT-C in the pixel area has an offset gate structure and the film thickness of offset areas 432c, 433c is thick, the OFF current is sufficiently low. As a result, high speed operation is possible in the drive circuit area, and the written charge can be sufficiently held in the pixel area. In the manufacturing method of an active matrix circuit board 400 of such structure, after first forming a thick film thickness, non-doped silicon film on the surface side of insulated substrate 101, the silicon film is patterned to form silicon films 401, 402, 403 as shown in Fig. 7 (a). Next, as shown in Fig. 7 (b), with silicon film 402 masked by resist 420, high concentration phosphorus ions are implanted at a 1 x 10 15 /cm 2 dose to silicon films 401, 403 as shown by arrow P + to form source-drain areas 412b, 413b, 432b, 433b of the bottom layer. Next, as shown in Fig. 7 (c), after forming a thin polycrystalline silicon film over the entire surface of insulated substrate 101, it is patterned to form non-doped silicon films 410, 421, 430. Silicon film 421 combines with silicon film 402 here to form silicon film 120. Silicon film 410 is the first silicon film for forming TFT-A, and silicon film 421 is a second silicon film for forming TFT-B. Silicon film 430 is the third silicon film for forming TFT-C (first process). Next, gate insulation films 414, 124, 434 are formed on the surface side of each silicon film 410, 120, 430 (second process), and then gate electrodes 415, 125, 435 are formed (third process). Next, as shown in Fig. 7 (d), the side with silicon films 120, 430 is masked by. resist 440. In this state, high concentration phosphorus ions are implanted at a 1 x 10 15 /cm 2 dose into silicon films 410, 430 as shown by arrow P + (fourth process). As a result, source-drain areas 412, 413 with a 1 x 10 20 /cm 3 impurity concentration formed self-aligned to gate electrode 415. A resist mask with openings formed in that part of silicon film 430 corresponding to where source-drain areas 432b, 433b of the bottom layer are to be formed can be used here. In this case, all of source-drain areas 432, 433 except for the offset area can be formed as n + high concentration areas. Next, after masking silicon films 410, 430 with resist 450 as shown in Fig. 7 (e), high concentration boron ions are implanted at a 5 x 10 15 /cm 2 dose to silicon film 120 as shown by arrow B + (fifth process). As a result, source-drain areas 122, 123, which are p + high concentration areas, are formed self-aligned to gate electrode 125 in silicon film 120. It is to be noted that the thicker the film thickness of source-drain areas 412, 413, the higher the ON current of TFT-A, and thus the better, the overall thickness of source-drain areas 412, 413 and channel formation area 411 can be increased as in TFT-B. In addition, the order of the fourth and fifth processes can be reversed. Possibilities for use in industry As described above, the TFT of the pixel area is built with an offset gate structure, and in the drive circuit area the source-drain area of the TFT is formed as a high concentration area and with a self-aligned structure in an active matrix circuit board relating to the present invention. Therefore, according to the present invention, the quality of the display of a liquid crystal display panel can be improved because the ON current characteristics of the TFT in the drive circuit area and the OFF current characteristics of the TFT in the pixel area can both be improved.

Claims: A method of manufacturing an active matrix circuit board having on the surface side of an insulated substrate (101) a drive circuit area (10b , 10c) comprising a CMOS circuit comprising a first thin-film transistor (TFT-A) of a first conductive type and a second thin-film transistor (TFT-B) of a second conductive type whose source-drain areas (412, 413, 122, 123) are self-aligned to the respective gate electrode (415, 125), and a pixel area (10a) comprising a third thin-film transistor (TFT-C) of the first conductive type, characterized by a) forming non-doped first, second, and third silicon films (401, 402, 403) for said first, second, and third thin-film transistors, respectively, on the surface side of the insulated substrate (101), each of said first and third silicon films (401, 403) comprising a pair of spaced-apart partial films. b) masking the second silicon fim (402) and ion-implanting an impurity of the first conductivity type into the first and third silicon films (401, 403) thereby forming bottom layers (412b, 413b, 432b, 433b) of a source region and a drain region for each of the first and the third thin-film transistors (TFT-A, TFT-C), c) forming a non-doped first polycrystalline silicon film (410), as top layers for the source and drain regions, on the bottom layers (412b, 413b) for the first thin-flim transistor and, as channel region, in the space between these bottom layers, forming a non-doped second polycrystalline silicon film (421) on said second silicon film (402), and forming a non-doped third polycrystalline silicon film (430), as top layers for the source and drain regions, on the bottom layers (432b, 433b) for the third thin-film transistor and, as channel and offset regions in the space between these bottom layers, the thickness of the first to third polycrystalline silicon films (410, 421, 430) being smaller than that of said first to third silicon films (401, 402, 403), d) forming a gate insulation film (414, 124, 434) on the surface of each of the polycrystalline silicon films formed in step c), e) forming a gate electrode (415, 125, 435) on the surface side of each of the gate insulation films (414, 124, 434), each gate electrode (415, 435) located over the respective channel region between the bottom layer (412b, 413b, 432b, 433b) for each of the first and third thin film transistors (TFT-A, TFT-C) f) ion-implanting an impurity of the first conductive type at a dose of 1 x 10 14 /cm 2 or greater into the first polycrystalline silicon film (410) using the respective gate electrode (415) as a mask with the second and third polycrystalline silicon films (421, 430) covered by a first mask (440) and that part (440a) of the first mask corresponding to the intended formation area of the source and drain regions of the third thin-film transistor (TFT-C) open, thereby obtaining the source and drain regions (412, 413) of the first thin-film transistor (TFT-A) self-aligned to the respective gate (415), and the source and drain regions (432, 433) of the third thin-film transistor (TFT-C) offset relative to the respective gate (435), and g) ion-implanting an impurity of the second conductive type at a dose of 1 x 10 14 /cm 2 or greater into the second polycrystalline silicon (421) film and the second silicon film (402) using the respective gate electrode (125) as a mask and keeping the first and third polycrystalline silicon films (410, 430) covered by a second mask (450), thereby obtaining the source and drain regions (122, 123) of the second thin-film transistor (TFT-B) self-aligned to the respective gate (125), wherein step g) may either follow or precede step f) and the impurity concentration of the source and drain regions is 1x10 19 /cm 3 or

Inventors: MATSUO MINORU, TAKENAKA SATOSHI, YUDASAKA ICHIO, MATSUO, MINORU, TAKENAKA, SATOSHI, YUDASAKA, ICHIO
Applicants: SEIKO EPSON CORP, SEIKO EPSON CORPORATION
Application year: 1994
Main classification: H01L27
IPC codes: H01L27, H01L21