Method for producing a hydrogen absorbing alloy electrode

Abstract: A method for producing a hydrogen-absorbing alloy electrode including a step of treating the surface of a hydrogen-absorbing alloy. The surface treatment is applied to hydrogen-absorbing alloy having ununiform distortion of 3.5 x 10⁻³ or less by using only an acid solution whose pH value is between 0.5 and 3.5.

Description: BACKGROUND OF THE INVENTION (1) Field of the Invention The present invention relates to a method for producing a hydrogen-absorbing alloy electrode including a hydrogen-absorbing alloy that reversibly absorbs and desorbs hydrogen at atmospheric pressure, and more particularly to treating the surface of the hydrogen-absorbing alloy. (2) Description of the Related Art Lead storage cells and nickel-cadmium storage cells have been widely used so far; however, metal-hydrogen alkaline storage cells are now attracting attention. A metal-hydrogen alkaline storage cell is composed of a negative electrode using a hydrogen-absorbing alloy as an active material and a positive electrode using a metallic oxide such as a nickel hydroxide as an active material. These metal-hydrogen alkaline storage cells have advantages of being lighter in weight, larger in capacity, and higher in energy density than these conventional storage cells. The hydrogen-absorbing alloy used in a metal-hydrogen alkaline storage cell is applied various surface treatments in order to improve the cell characteristics. For example, Japanese Patent Publication No. 4-79474 discloses the use of an alkaline aqueous solution for a surface treatment of the hydrogen-absorbing alloy. The surface treatment realizes the formation of a nickel-rich layer over the surface of the hydrogen-absorbing alloy. The nickel-rich layer accelerates smooth absorption of oxygen gas generated from the positive electrode during overcharge because nickel works as a catalyzer in a reducing reaction of oxygen. Consequently, the rise in cell internal pressure is restricted and charge/discharge cycle characteristics are improved. Japanese Laid-open Patent Application No. 3-98259 discloses the use of hot water of 60°C or higher for a surface treatment of a hydrogen-absorbing alloy. This method also realizes the formation of a nickel rich layer with the same effects as the above case. However, these surface treatments to form a nickel rich layer have an undesirable side effect of producing hydroxide. The hydroxide increases the contact resistance among hydrogen-absorbing alloy particles or decreases the activity of the hydrogen-absorbing alloys, thereby deteriorating the high rate charge/discharge characteristics and low temperature discharge characteristics in the initial charge/discharge cycle. The following methods have been proposed for improving the high rate charge/discharge characteristics and low temperature discharge characteristics in the initial charge/discharge cycle. 1) Japanese Laid-open Patent Application No. 3-152868: A fine oxide layer which obstructs the initial activation of a hydrogen-absorbing alloy is removed through an acid treatment before an alkaline treatment is applied to the alloy. As a result, a hydrogen-absorbing alloy electrode with both excellent high rate charge/discharge characteristics and gas absorption characteristics is obtained. 2) Japanese Laid-open Patent Application No. 1-132048: An acid treatment is applied to a hydrogen-absorbing alloy, and a sintered electrode with excellent high rate charge/discharge characteristics and charge/discharge cycle characteristics is produced by using the alloy. However, according to the former method, the alkaline treatment results in the formation of hydroxide, and the low temperature discharge characteristics are not satisfactory. The latter method, on the other hand, has a problem that the complicated producing process of the sintered electrode leads to low productivity. If the acid treatment is applied to a non-sintered electrode, acid dissolves the alloy surface, thereby generating hydrogen. The generated hydrogen is re-absorbed by the alloy, and the alloy has cracks on its surface during the re-absorption. As a result, new active surfaces are formed which improve the activity of the alloy. If the cracks grow larger, however, the alloy may be deteriorated through oxidization with the progress of charge/discharge cycles. The deterioration of the alloy lowers the charge/discharge efficiency and the charge/discharge cycle characteristics. SUMMARY OF THE INVENTION In view of the foregoing problems, an object of the present invention is to provide a method for producing a hydrogen-absorbing alloy electrode with excellent high rate charge/discharge characteristics and excellent low temperature discharge characteristics in the initial charge/discharge cycle, and long charge/discharge cycle life. The above object can be achieved by a method for producing a hydrogen-absorbing alloy electrode including a step of treating a surface of a hydrogen-absorbing alloy having non-uniform distortion of 3.5 x 10 -3 or less. The surface treatment step is carried out by using only an acid aqueous solution whose pH value is between 0.5 and 3.5. The method may be further include the following steps. A step of melting and cooling elements composing the hydrogen-absorbing alloy, thereby producing a hydrogen-absorbing alloy ingot. A step of pulverizing the hydrogen-absorbing alloy ingot into powder, the pulverization step including the surface treatment step. A step of producing a hydrogen-absorbing alloy electrode from the hydrogen-absorbing alloy powder. The surface treatment step may be composed of pulverizing the hydrogen-absorbing alloy ingot in the acid aqueous solution. The method may include the following steps. A step of producing a hydrogen-absorbing alloy electrode from the hydrogen-absorbing alloy powder, the surface treatment step being applied to the hydrogen-absorbing alloy powder between the pulverization step and the production step. The surface treatment step may be composed of soaking the hydrogen-absorbing alloy powder in the acid aqueous solution. The method may further comprise the following steps: A step of producing a hydrogen-absorbing alloy base electrode from the hydrogen-absorbing alloy powder, the surface treatment being applied to said hydrogen-absorbing alloy base electrode after the production step of the hydrogen-absorbing alloy base electrode. The above object can be achieved on the following grounds. When a hydrogen-absorbing alloy is applied the surface treatment with an acid aqueous solution whose pH value is between 0.5 and 3.5, the surface of the alloy dissolves and hydrogen is generated. The hydrogen thus generated is re-absorbed by the alloy, which has cracks on its surface during the re-absorption. As a result, new active surfaces are formed which improve the activity of the alloy. Thus, the high rate discharge characteristics and low temperature discharge characteristics are improved in accordance with the improvement of the alloy activity. In addition, the hydrogen-absorbing alloy of the present invention has excellent crystallization and its non-uniform distortion is 3.5 x 10 -3 or less. Consequently, the formation of large cracks are prevented through the acid treatment, and the pulverization does not proceed too much with the progress of the charge/discharge cycle. These features prevent the charge/discharge cycle to be shortened. Since other components of the alloy have higher solubility than nickel as the main component in an acid area, they easily dissolve in an acid solution. As a result, the nickel-rich layer is formed on the surface of the hydrogen-absorbing alloy. The layer accelerates smooth absorption of oxygen gas generated from the positive electrode during overcharge because nickel works as a catalyzer. As a result, the rise in cell internal pressure is restricted, and the oxygen gas is prevented from leaking out through a safety vent. Consequently, charge/discharge cycle characteristics are improved. Thus, according to the method for producing a hydrogen-absorbing alloy electrode of the present invention, discharge characteristics are improved by treating a hydrogen-absorbing alloy with acid. Then, non-uniform distortion is determined without the application of an alkaline treatment which gives bad effects to the discharge characteristics, thereby improving the charge/discharge cycle. Furthermore, controlling the cooling rate of hydrogen-absorbing alloy melt and applying anneal treatment to a resulting hydrogen-absorbing alloy ingot allows non-uniform distortion to be 3.5 x 10 -3 or less. The non-uniform distortion is a cause of broading Debye ring and is measured through Laue camera or the like. The value is defined through the following formula. [formula] η = β′ 2 tan  η : non-uniform distortion β' : integral amplitude  : Bragg's diffraction BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a graph showing the relationship between the non-uniform distortion and the charge/discharge cycle. FIG. 2 is a graph showing the relationship between pH values of an acid aqueous solution to be used in an acid treatment and the charge/discharge cycle. FIG. 3 is a graph showing the relationship between the pH values and high rate discharge characteristics. FIG. 4 is a graph showing the relationship between the non-uniform distortion and high rate discharge characteristics. DESCRIPTION OF THE PREFERRED EMBODIMENTS <EMBODIMENT 1> [Method for producing hydrogen-absorbing alloy electrode] First, commercially available Mm (misch metal, a mixture of rare-earth elements such as La, Ce, Nd, and Pr), Ni, Co, Al, and Mn were mixed in an elemental ratio of 1 : 3.4 : 0.8 : 0.2: 0.6 and melted in a high frequency melting furnace under argon inert atmosphere. The resulting melt was cooled to produce a hydrogen-absorbing alloy ingot expressed by MmNi 3.4 Co 0.8 Al 0.2 Mn 0.6 . The non-uniform distortion of the alloy ingot at this point was 5.4 x 10 -3 , and the hydrogen-absorbing alloy ingot is hereinafter referred to as the alloy ingot M 1 . The alloy ingot M 1 was applied anneal treatment for eight hours at 1000°C in an inert gas and then pulverized into powder whose average diameter was 150µm under an inert gas atmosphere. The non-uniform distortion of the alloy powder thus produced was 2.5 x 10 -3 . The hydrogen-absorbing alloy powder is hereinafter referred to as the alloy powder M 2 . The alloy powder M 2 was soaked for twenty minutes in a hydrochloric acid aqueous solution whose pH value was 1, well rinsed with ion exchange water, and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The alloy powder for electrode was kneaded into a paste with 5wt% of polytetrafluoroethylene powder as a binder to the active material. The paste was applied over both surfaces of a collector made of punching metal and the collector was pressed to produce a non-sintered hydrogen-absorbing alloy electrode. [Assembling of a cell] The hydrogen-absorbing alloy electrode produced as above and a well-known sintered nickel electrode were coiled together via an unwoven cloth separator to produce an electrode assembly. The electrode assembly was put into an outer can, which was sealed after a potassium hydroxide aqueous solution of 30wt% was pored thereinto. Consequently, a cylindrical nickel-hydrogen storage cell with a theoretical capacity of 1000mAh was produced. The nickel-hydrogen storage cell thus produced is hereinafter referred to as A 1 cell. <EMBODIMENT 2> The hydrogen-absorbing alloy ingot M 1 (non-uniform distortion : 2.5 x 10 -3 ) which had been applied anneal treatment was primarily pulverized into powder whose average diameter was 500µm or smaller in an inert gas. The alloy powder was further pulverized into finer powder whose average diameter was 150µm or smaller by using a ball mill in a hydrochloric acid aqueous solution whose pH value was 1. Then, the finer alloy powder was well rinsed with ion exchange water and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The alloy powder thus produced was used to produce an electrode, and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as A 2 cell. (Comparative Example 1) The alloy powder M 2 was soaked for an hour at 80°C in a potassium hydroxide aqueous solution whose pH was 14, well rinsed with ion exchange water, and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The alloy powder thus produced was used to produce an electrode, and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 1 cell. (Comparative Example 2) After having been applied an acid surface treatment in the same manner as Embodiment 1, the alloy powder M 2 was further applied with an alkaline surface treatment in the same manner as Comparative Example 1 without drying. The alloy powder M 2 thus treated was well rinsed with ion exchange water and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The alloy powder thus produced was used to produce an electrode, and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 2 cell. (Comparative Example 3) The alloy powder M 2 was used to produce an electrode without applying any treatment and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 3 cell. (Comparative Example 4) The hydrogen-absorbing alloy ingot M 1 (non-uniform distortion : 5.4 x 10 -3 ) which had not been applied anneal treatment was pulverized into powder whose average diameter was 150µm or smaller under an inert gas, thereby producing hydrogen-absorbing alloy powder for electrode (ununiform distortion : 5.4 x 10 -3 ). The hydrogen-absorbing alloy powder is hereinafter referred to as the alloy powder M 3 . The alloy powder M 3 was applied acid surface treatment in the same manner as Embodiment 1, well rinsed with ion exchange water, and dried to produce a hydrogen-absorbing alloy powder for electrode. The alloy powder M 3 was used to produce an electrode and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 4 cell. (Comparative Example 5) The hydrogen-absorbing alloy ingot M 1 (non-uniform distortion : 5.4 x 10 -3 ) which had not been applied anneal treatment was primarily pulverized into powder whose average diameter was 500µm or smaller in the same manner as Embodiment 2. Then, the pulverized powder was further pulverized into finer powder whose average diameter was 150µm or smaller by using a ball mill in a hydrochloric acid aqueous solution whose pH value was 1. Then, the finer alloy powder was well rinsed with ion exchange water and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The hydrogen-absorbing alloy powder was used to produce an electrode and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 5 cell. (Comparative Example 6) The alloy powder M 3 produced in Comparative Example 4 was applied alkaline surface treatment in the same manner as Comparative Example 1. The alloy powder M 3 was well rinsed with ion exchange water and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The hydrogen-absorbing alloy powder was used to produce an electrode and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 6 cell. (Comparative Example 7) The alloy powder M 3 produced in Comparative Example 4 was applied acid surface treatment in the same manner as Embodiment 1, and further applied alkaline surface treatment in the same manner as Comparative Example 1 without drying. Then, the alloy powder M 3 thus treated was well rinsed with ion exchange water and dried, thereby producing hydrogen-absorbing alloy powder for electrode. The hydrogen-absorbing alloy powder was used to produce an electrode and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 7 cell. (Comparative Example 8) The alloy powder M 3 produced in Comparative Example 4 was used as the hydrogen-absorbing alloy powder for electrode. The alloy powder was used to produce an electrode and the electrode was used to produce a cell in the same manner as Embodiment 1. The cell thus produced is hereinafter referred to as X 8 cell. The ununiform distortion and surface treatment conditions of the hydrogen-absorbing alloys used in the cells A 1 -A 2 of the present invention and cells X 1 -X 8 of Comparative Examples are listed in the following table 1. (Experiments 1) With regard to the cell A 1 -A 2 of the present invention and the cells X 1 -X 8 of Comparative Examples, their cell internal pressure, high rate discharge characteristics, low temperature discharge characteristics, and charge/discharge cycle life were examined. The results are shown on the following tables 2-5 respectively. Prior to the experiments, the cells were activated by charging for 16 hours at 100mA, resting for an hour, discharging at 200mA until the voltage dropped to 1.0V, and resting for another hour. This cycle was repeated three times at room temperature. Each of the experiments was conducted under the following conditions. (1) Cell internal pressure The cells were charged at 1000mA at room temperature and the internal pressure was measured when they were charged 200% (two hours after the start of charging). (2) High rate discharge characteristics At room temperature, the cells were charged for 16 hours at 100mA, rested for one hour, discharged at 4000mA until the voltage dropped to 1.0V, and rested for another hour. Then the discharge capacity of each cell was measured. (3) Low temperature discharge characteristics At room temperature, the cells were charged for 16 hours at 100mA, rested for one hour at 0°C, and discharged at 1000mA at 0°C until the voltage dropped to 1.0V. Then the discharge capacity of each cell was measured. (4) Charge/discharge cycle characteristics At room temperature, the cells were charged for 48 minutes at 1500mA, rested for one hour, discharged at 1500mA until the voltage dropped to 1.0V, and rested for another hour. The charge/discharge cycle was repeated until the cell capacity reached 500mAh in order to measure the cycle numbers. cell internal pressure cells internal pressure (kgf/cm 2 ) A 1 10.1 A 2 9.8 X 1 11.5 X 2 10.2 X 3 15.3 X 4 19.2 X 5 20.1 X 6 19.7 X 7 18.9 X 8 18.2 high rate discharge characteristics cells discharge capacities (mAh) A 1 905 A 2 895 X 1 752 X 2 767 X 3 800 X 4 915 X 5 904 X 6 793 X 7 815 X 8 850 low temperature discharge characteristics cells discharge capacities (mAh) A 1 904 A 2 897 X 1 318 X 2 420 X 3 615 X 4 917 X 5 906 X 6 431 X 7 487 X 8 895 charge/discharge cycle cells charge/discharge cycle (times) A 1 1123 A 2 1154 X 1 925 X 2 957 X 3 917 X 4 575 X 5 543 X 6 602 X 7 622 X 8 619 As apparent from Table 2, the increase in the internal pressure of the cells A 1 and A 2 of the present invention were lower than that of the other cells. As apparent from Table 5, the cells A 1 and A 2 of the present invention exhibited outstandingly long charge/discharge cycle life. The cells X 4 and X 5 , which had been applied the acid treatment in the same manner as the cells A 1 and A 2 , exhibited short charge/discharge cycle. It seems to result from that too large a non-uniform distortion of the acid-treated hydrogen-absorbing alloys caused too much pulverization. As a result, the alloys were deteriorated through oxidization, thereby spoiling the charge/discharge cycle characteristics. With respect to the high rate discharge characteristics and low temperature discharge characteristics shown in Tables 3 and 4, both the cells A 1 and A 2 of the present invention and the cells X 4 and X 5 of the Comparative Examples exhibited sufficient values. The discharge capacities of these cells A 1 , A 2 , X 4 , and X 5 were compared with those of the cells X 3 and X 8 which had been applied no treatment. The comparison reveals that the difference in the discharge capacities is greater among cells A 1 , A 2 , and X 3 having less non-uniform distortion than among cells X 4 , X 5 , and X 8 having larger non-uniform distortion. This means that the acid treatment worked more effectively on the cells A 1 , A 2 , and X 3 . As apparent from the results of these experiments, the most excellent cells from the view point of the high rate discharge characteristics, low temperature discharge characteristics, and charge/discharge cycle characteristics were cells A 1 and A 2 which used acid-treated alloys having non-uniform distortion of 2.5 x 10 -3 as an electrode material. (Experiment 2) The results of the Experiments 1 proved that the acid treatment did not work on a cell which used a hydrogen-absorbing alloy with large non-uniform distortion to improve its charge/discharge cycle. FIG. 1 shows the relationship between non-uniform distortion and charge/discharge cycle life. Experiment 2 was conducted under the same conditions as the measurement of the charge/discharge cycle characteristics of Experiment 1. The same electrodes and cells were produced as Embodiment 1 and the same acid treatments as Embodiment 1 were applied to hydrogen-absorbing alloys with different non-uniform distortion sizes. For an additional comparison, the hydrogen-absorbing alloys that had not been applied an acid treatment were used to form electrodes and cells in the same manner to examine the charge/discharge cycle characteristics. The non-uniform distortion was adjusted through the cooling rate of hydrogen-absorbing alloy melt and the anneal treatment. As apparent from FIG. 1, alloys whose non-uniform distortion was 3.5 x 10 -3 or less showed satisfactory cycle times. Furthermore, cells including hydrogen-absorbing alloys which were not applied acid treatments were compared with cells including hydrogen-absorbing alloys that had been applied acid treatments of the present invention. As a result, acid treatment worked effectively on alloys whose non-uniform distortion was less than 4.0 x 10 -3 to increase their cycle numbers. However, when the non-uniform distortion was over 4.0 x 10 -3 , non-acid-treated alloys exhibited more charge/discharge cycle numbers than acid-treated alloys. Thus, alloys whose non-uniform distortion is 3.5 x 10 -3 or less are best because of their long charge/discharge cycle life and satisfactory effects of the acid treatment. (Experiment 3) The relationship between the charge/discharge cycle life and the pH value of a solution to be used for acid treatment was examined. The results are shown in FIG. 2. Experiment 3 was conducted under the same conditions as the measurement of the charge/discharge cycle characteristics of Experiment 1 by producing electrodes and cells in the same manner as Embodiment 1 except that the pH values in the acid treatment for the alloy powder M 2 (non-uniform distortion : 2.5 x 10 -3 ) were variously changed. As apparent from FIG. 2, satisfactory charge/discharge cycle life was obtained when the pH value is in a range of between 0.5 and 3.5. (Experiment 4) The relationship between the high rate discharge characteristics and pH values of an acid aqueous solution used for the acid treatment was examined. The results are shown in FIG. 3. Experiment 4 was conducted under the same conditions as the measurement of the high rate discharge cycle characteristics of Experiment 1 by producing electrodes and cells in the same manner as Embodiment 1 except that the pH values in the acid treatment were variously changed. As apparent from FIG. 3, satisfactory high rate discharge characteristics were obtained when the pH value was in a range of between 0.5 and 3.5. (Experiment 5) As apparent from the high rate charge/discharge characteristics obtained in Experiment 1, the acid treatment works more effectively on alloys with less non-uniform distortion than those with larger non-uniform distortion for the purpose of raising the high rate charge/discharge characteristics. FIG. 4 shows the relationship between non-uniform distortion and effects of the acid treatment in the high rate discharge characteristics. Experiment 5 was conducted as follows. Hydrogen-absorbing alloy powders having various non-uniform distortion were prepared to produce electrodes and cells. Of two alloy powders having a common non-uniform distortion, one was applied an acid treatment and the other was not. The non-uniform distortion was adjusted through the cooling rate of hydrogen-absorbing alloy melt and anneal treatment. As apparent from FIG. 4, alloys that had not been applied a treatment has a low high-rate discharge characteristics because of low alloy activation. On the other hand, cells using hydrogen-absorbing alloys whose non-uniform distortion was small were able to improve the high rate discharge characteristics by applying acid treatment. The relationship between low temperature discharge characteristics and the pH value of the acid aqueous solution and the relationship between non-uniform distortion and low temperature discharge characteristics were not shown. The low temperature discharge characteristics, however, contributes to the activity of the hydrogen-absorbing alloy like the high rate discharge characteristics. Consequently, the low temperature discharge characteristics shows the same tendency as the high rate discharge characteristics, obtaining the same results. Thus, the results of Experiments 2 through 5 have proved that it is preferable to apply an acid treatment to hydrogen-absorbing alloy whose non-uniform distortion is 3.5 x 10 -3 or less by using an acid solution having a pH value of between 0.5 and 3.5. (Others) 1) Instead of hydrochloric acid used in the Embodiments, another acid may be used as long as its pH value is equivalent because the effects of the present invention results from pH value. 2) Instead of rare-earth metal-Ni hydrogen-absorbing alloy, for example Ti-Ni hydrogen-absorbing alloy may be used to obtain the same effects. 3) The acid treatment is applied when or after a hydrogen-absorbing alloy ingot is pulverized in the embodiments; however, a hydrogen-absorbing alloy that has not applied the treatment may be used to produce an electrode and the electrode may be applied acid treatment to obtain the same effects. In this case, the electrode is soaked in an acid aqueous solution for surface treatment, and then rinsed with water and dried. Although the present invention has been fully described by way of examples with reference to the accompanying drawings, it is to be noted that various changes and modifications will be apparent to those skilled in the art. Therefore, unless such changes and modifications depart from the scope of the present invention, as defined by the appended claims, they should be construed as being included therein.

Claims: A method for producing a hydrogen-absorbing alloy electrode including a step of treating a surface of a hydrogen-absorbing alloy having non-uniform distortion, defined by the following formula:- η = β′ 2 tan  η : non-uniform distortion β' : integral amplitude  : Bragg's diffraction of 3.5 x 10 -3 or less, the surface treatment step being carried out by using only an acid aqueous solution whose pH value is between 0.5 and 3.5. The method of claim 1 further comprising the steps of: melting and cooling elements composing said hydrogen-absorbing alloy, thereby producing a hydrogen-absorbing alloy ingot; pulverizing said hydrogen-absorbing alloy ingot into powder, the pulverization step including the surface treatment step; and producing a hydrogen-absorbing alloy electrode from the hydrogen-absorbing alloy powder. The method of claim 2, wherein the surface treatment step is composed of pulverizing said hydrogen-absorbing alloy ingot in the acid aqueous solution. The method of claim 2, wherein to said hydrogen-absorbing alloy ingot is applied an anneal treatment. The method of claim 2, wherein a rate of said cooling is controlled. The method of claim 1 comprising the steps of: melting and cooling elements composing said hydrogen-absorbing alloy, thereby producing a hydrogen-absorbing alloy ingot; pulverizing said hydrogen-absorbing alloy ingot into powder; and producing a hydrogen-absorbing alloy electrode from the hydrogen-absorbing alloy powder, said surface treatment step being applied to said hydrogen-absorbing alloy powder between the pulverization step and the production step. The method of claim 6, wherein said surface treatment step is composed of soaking said hydrogen-absorbing alloy powder in said acid aqueous solution. The method of claim 6, wherein to said hydrogen-absorbing alloy ingot is applied an anneal treatment. The method of claim 6, wherein a rate of said cooling is controlled. The method of claim 1 further comprising the steps of: melting and cooling elements composing said hydrogen-absorbing alloy, thereby producing a hydrogen-absorbing alloy ingot; pulverizing said hydrogen-absorbing alloy ingot into powder; and producing a hydrogen-absorbing alloy base electrode from the hydrogen-absorbing alloy powder, the surface treatment being applied to said hydrogen-absorbing alloy base electrode after the production step of the hydrogen-absorbing alloy base electrode. The method of claim 10, wherein to said hydrogen-absorbing alloy ingot is applied an anneal treatment. The method of claim 10, wherein a rate of said cooling is controlled.

Inventors: FUKUDA HIROSHI, MIZUTAKI FUSAGO, TADOKORO MOTOO, FUKUDA, HIROSHI, MIZUTAKI, FUSAGO, TADOKORO, MOTOO
Applicants: SANYO ELECTRIC CO, SANYO ELECTRIC CO., LTD.
Application year: 1994
Main classification: H01M4
IPC codes: H01M4, B22F1