BALL-AND-ROLLER BEARING

Abstract: A ball-and-roller bearing in which rolling elements, or rolling elements and a pair of races are formed out of a ceramic material obtained by sintering a sintering material of silicon nitride containing at least silicon oxide out of silicon oxide and silicon carbide, and a MgAl₂O₄ spinel structure as sintering assistants. Such a ball-and-roller bearing has a high thermal resistance and a high abrasion resistance, and displays an excellent corrosion resistance when it is used in a corrosive atmosphere, this bearing having a long service life.

Description: TECHNICAL FIELD This invention relates to rolling bearings and more particularly to rolling bearings wherein a rolling element, alternatively, a rolling element and a race are prepared from a ceramic material of silicon nitride. BACKGROUND ART As rolling bearings to be used under severe conditions such as high temperature, corrosive environment, vacuum or non-lubricant atmosphere in which normal metallic material cannot be used, there can be mentioned so-called ceramic bearings wherein at least a rolling element (and more preferably, a rolling element and a race) is/are made of a ceramic material. Such ceramic material preferred to use are those prepared by sintering a sintering material containing particles of silicon nitride(Si 3 N 4 ) because they are excellent in heat resistance and wear resistance. Silicon nitride itself is, however, relatively poor in sintering properties. Therefore, to a sintering material, a variety of sintering assistants which improves sintering properties of the silicon nitride are generally added in a desired amount. Examples of conventional sintering assistants include rare earth oxide such as yttrium oxide(Y 2 O 3 ), aluminum oxide (Al 2 O 3 ) and aluminum nitride(AlN), among others. As exemplary sintering material of silicone nitride containing the sintering assistants as described, those of Si 3 N 4 -Y 2 O 3 -Al 2 O 3 or Si 3 N 4 -Y 2 O 3 -Al 2 O 3 -AlN are known in the art. In the ceramic bearings prepared from the sintering material of silicon nitride, however, particularly sintering assistants and more particularly yttrium oxide is corroded when used in a corrosive atmosphere such as a strong acid atmosphere and a strong alkali atmosphere, reducing bonding strength between silicon nitride particles. This has been causing the problem that the strength of a ceramic bearing significantly reduces so that breakage occur before its design life. The document JP-A-1-037469 discloses ball bearings used at a high speed rotation portion wherein a ceramic material is used which is prepared by sintering a sintering material containing the following components: silicon nitride having at least 90 % alpha-type crystallisation ratio and up to 1 µm average particle size; 3 % to 10 % by weight of MgAl 2 O 4 of spinel structure; and 0.1 % to 1 % by weight of silicon oxide. The sintering process is performed in a normal pressure N 2 gas atmosphere and a temperature of 1600 °C to 1800 °C. It is accordingly the object of this invention to provide rolling bearings of a long service life, which are excellent in corrosion resistance when it is used under a corrosive atmosphere, as well as heat resistance and wear resistance. DISCLOSURE OF THE INVENTION The rolling bearing of this invention includes a pair of races and a plurality of rolling elements disposed between both races and has a structure as defined in claim 1. Further developments of the invention are set forth in the subclaims. The rolling elements, alternatively, the rolling elements and the races both comprising such a ceramic material, are excellent in durability in a corrosive atmosphere, as well as heat resistance and wear resistance. Thus this invention can provide rolling bearings being excellent in wear resistance, corrosion resistance in a corrosive atmosphere, and of a long service life. BRIEF DESCRIPTION OF DRAWINGS Fig. 1(a) is a perspective view illustrating appearance of a disc test piece for thrust test, which was prepared from a sintering material (Samples Nos. 1-3), in order to evaluate properties of the ceramic material for the rolling bearings of this invention and those of ceramic material for conventional ceramic bearings (Samples Nos. 4-5). Fig. 1(b) is a perspective view illustrating appearance of a stick test piece for strength test, which was prepared from a sintering material out of Samples Nos. 1-5. Fig. 2 is a graph illustrating weight lapse rate(%) of the disc test piece when conducting an acid dipping test wherein the disc test piece was dipped in acid to make it be corroded. Fig. 3 is a graph illustrating the transition of flexural strength before and after conducting the acid dipping test for the stick test piece. Fig. 4(a) is a sectional view illustrating the outline of a device used in a rolling life test for the disc test piece. Fig. 4(b) is a graph illustrating the load transition when conducting the rolling life test using the device of Fig. 4(a). Fig. 5 is a graph illustrating the rolling life of the disc test piece, which was obtained after conducting the acid dipping test using the device shown in Fig. 4(a). Fig. 6 is a graph illustrating weight lapse rate(%) of the disc test piece when conducting the alkali dipping test wherein the disc test piece was dipped in alkali to make it be corroded. Fig. 7 is a graph illustrating the transition of flexural strength between before and after conducting the alkali dipping test for the stick test piece. Fig. 8 is a graph illustrating the rolling life of the disc test piece, which was obtained after conducting the alkali dipping test using the device shown in Fig. 4(a). PREFERRED EMBODIMENT OF THE INVENTION In this invention, at least the rolling elements are made of a ceramic material prepared by sintering a sintering material of silicon nitride containing an MgAl 2 O 4 of spinel structure and at least silicon oxide and silicon carbide, as a sintering assistant. As the silicon nitride(Si 3 N 4 ), there may be used a variety of crystal systems such as α-type, β-type, etc. where the α-type is preferred. Although any limitation is not imposed to particle diameter of the silicon nitride when it is in the state of sintering material, namely, prior to sintering, its mean particle diameter preferably ranges from about 0.4 to about 1.5µm in order to form a denser sintered body. Of sintering assistants, the MgAl 2 O 4 of spinel structure links silicon nitride particles at the time of sintering to make a sintered structure denser, which is its major role, and it also acts to improve corrosion resistance of the ceramic material by forming a grain boundary phase that exhibits strong resistance, especially to strong acid or strong alkali, with the aid of silicon nitride particles. Silicon oxide strengthens the linkage between the silicone nitride particles and sintering assistants such as an MgAl 2 O 4 of spinel structure, so that corrosion resistance of the ceramic material increases further. Silicon carbide assists an MgAl 2 O 4 of spinel structure to improve corrosion resistance of the ceramic material, and also contributes to the improvement in mechanical properties of the ceramic material, particularly to its hardness, thus improving its rigidity. In addition, the silicon carbide reduces frictional resistance of the ceramic material to improve its surface lubricity. In this invention, it is possible to use other sintering assistants unless they affect on the actions of the compounds as described. As examples of such sintering assistants, without being limited thereto, there can mention oxides such as titanium oxide, hafnium oxide and tungsten oxide; carbides such as titanium carbide, hafnium carbide and tungsten carbide, among others. The exemplified sintering assistants act in combination with an MgAl 2 O 4 of spinel structure to promote densing, i.e., a sintering accelerator. In addition, they change, within a ceramic material, to independent particles whose melting point is higher than a sintered ceramic material, and then such particles disperse into the ceramic material structure to improve strength and wearing resistance of the ceramic material. Among those, titanium oxide also functions as black coloring agent. The proportion of MgAl 2 O 4 of spinel structure to the total weight of sintering material ranges from 0.5 to 6% by weight where from 2 to 5% by weight is preferred and near 3.5% by weight is most preferred. If it is less than 0.5% by weight, it would fail to dense the sintered structure, lowering heat resistance and wearing resistance of the ceramic material. Conversely, if it exceeds 6% by weight, corrosion resistance of the ceramic material might reduce. The proportion of silicon oxide ranges from 0.1 to 1% by weight where near 0.5% by weight is preferred. If it is less than 0.1% by weight, the blending effect would be insufficient, failing to obtain satisfactory improvement in corrosion resistance of the ceramic material. Conversely, if it exceeds 1% by weight, sintering properties might be inhibited. The proportion of silicon carbide ranges from 3 to 5% by weight where 5% by weight is preferred. If it is less than 3% by weight, the blending effect would be insufficient, failing to improve mechanical properties nor reduce frictional resistance. Conversely, if it exceeds 5% by weight, sintering properties might be inhibited. When used, each proportion of other sintering assistants than those described above ranges from 0 to 1% by weight. If it exceeds 1% by weight, corrosion resistance of the ceramic material might reduce. Although the entire amount of the sintering assistants mentioned above is not particularly limited in this invention, the entire amount is preferably in a range of from 6 to 11% by weight. If the entire amount of the sintering assistants is less than the lower limit mentioned above, the blending effect of the sintering assistants would be insufficient, failing to obtain satisfactory improvement in corrosion resistance of the ceramic material. On the other hand, if it exceeds the upper limit, heat resistance and wearing resistance of the ceramic material might reduce. Sintering material for a system containing no silicon carbide has the advantage that an alterated layer in the surface of a sintered ceramic material would become small in amount, so that such a sintering material is excellent in cost performance and is suitable for rolling bearings for general purpose use. On the other hand, when using the inventive system containing silicon carbide, although such an alterated layer would become larger in amount than the system without silicon carbide, a sintered ceramic material performs its self-lubricating properties owing to frictional resistance reducing action derived from the silicon carbide. This system is, therefore, suitable for rolling bearings to be used in a non-lubricant condition prohibiting the use of lubricants such as grease. The increase of alterated layer when sintering the system containing silicon carbide may be caused by the following matter. Specifically, a complete sintering of silicon carbide requires a sintering temperature of 2000°C or more, whereas silicon nitride can generally be sintered at about 1800-1850°C. Therefore, when sintering the sintering material of the latter system at about 1800-1850°C, the sintering of silicon carbide tends to be incomplete, increasing alterated layer. The rolling bearings of this invention include a pair of races and a plurality of rolling elements provided between both races, at least the rolling elements being prepared from the ceramic material made of the specific composition, as previously mentioned. Specifically, the rolling bearings of this invention fall into two types, as follows: (I) One wherein only the rolling elements are prepared from the specific ceramic material; and (II) One wherein both the rolling elements and the races are prepared from the specific ceramic material. The rolling bearing of the type (II) is particularly excellent in heat resistance, wearing resistance and corrosion resistance. Depending upon performance or use, however, the rolling bearing of the type (I) may also be usable. In the cases where only the rolling elements are prepared from the specific ceramic material, the races are preferably made of a variety of conventional materials for the races, such as stainless steel(SUS440C). For both types of rolling bearings, it is desirable to have a retainer for holding the rolling elements. An appropriate retainer for a rolling bearing to be used in a non-lubricant atmosphere is one whose surface itself is excellent in self-lubricating properties. Examples of such a retainer include one which is entirely made of fluorocarbon polymers, and one prepared from stainless steel(SUS304) whose entire surfaces are being covered with baking film of fluorocarbon polymers. In order to prepare the rolling element or the race from the specific ceramic material, there can be employed normal ceramics molding and sintering techniques, such as the method wherein each given amount of the ingredients as described are blended to prepare a sintering material, which is then molded into a specific shape by mold press or the like, and the molding is sintered in an inert gas atmosphere for a predetermined period of time. As sintering technique, there can be employed any of well-known methods such as hot pressing(HP), atmosphere pressurization and hot isostatic pressing(HIP). INDUSTRIAL APPLICABILITY As discussed in the foregoing, the rolling bearings of this invention have excellent durability and corrosive resistance when used in a corrosive atmosphere, as well as heat resistance and wearing resistance. Thus they are well suited for applications under severe conditions such as high temperature, corrosive atmosphere, vacuum and non-lubricated atmosphere in which normal metal cannot be used. PREPARATION OF SAMPLES Samples Nos. 1 to 3 As an example of a ceramic material for the rolling bearing of this invention, α-type silicon nitride whose mean particle diameter is 0.7µm and each given amount of sintering assistants illustrated in Table 1 were blended to prepare a mixture, to which ethanol was added as a solvent and agitated by a ball mill for 48 hours. There was obtained each sintering material of silicone nitride (Samples 1 to 3). Please note that Sample No. 1 is not an embodiment of the invention. Sample No. 1 2 3 Si 3 N 4 (% by weight) 95 91 90 Sintering Assistants (% by weight) MgAl 2 O 4 3.5 3.5 3.5 SiO 2 0.5 0.5 0.5 SiC - 5 5 TiO 2 1 - 1 Subtotal 5 9 10 Sample Nos. 4 and 5 As an example of a ceramic material for conventional bearings, an α-type silicon nitride whose mean particle diameter is 0.7µm and each given amount of sintering assistants illustrated in Table 2 were blended to prepare a mixture, to which ethanol was added as a solvent and agitated by a ball mill for 48 hours. There was obtained each sintering material of silicone nitride (Samples 4 and 5). Sample No. 4 5 Si 3 N 4 (% by weight) 87 95 Sintering Assistants (% by weight) Al 2 O 3 4.5 2 Y 2 O 3 5.5 1.5 TiO 2 1 0.5 AlN 2 1 Subtotal 13 5 PREPARATION OF TEST PIECES Disc Test Pieces To each sintering material(Samples Nos. 1-5), the fixed amount of organic binder was added with stirring to prepare a mixture. The mixture was subjected to pressure molding with a molding pressure of 1000kgf/cm 2 to obtain a molding. The molding was degreased in a nitrogen gas atmosphere raised to 500°C and further subjected to sintering at atmospheric pressure in a nitrogen gas atmosphere raised to 1800°C for 2 hours. Prepared were disc test pieces for thrust test (60mm in diameter d 1 , 25mm in diameter of the center hole d 2 , 5mm in thickness t ), as shown in Fig. 1(a). Stick Test Pieces The above steps were repeated to prepare stick test pieces for flexural strength test (3mm in height h , 4mm in width w , 40mm in length L ), as shown in Fig. 1(b). TESTS Physical Properties Test Physical properties such as density(g/cm 3 ), Vickers hardness Hv, flexural strength(kgf/mm 2 ) and fracture toughness Klc(MPam 1/2 ) for each stick test piece were determined in the usual way. Measurement of Alterated Layer Each test piece was observed by a microscope to determine the thickness of alterated layer in its surface. Table 3 gives the results. Sample No. Density (g/cm 3 ) Vickers hardness (Hv) Flexural strength (kgf/mm 2 ) Fracture toughness (MPam 1/2 ) Thickness of alterated layer (mm) 1 3.16-3.18 1490-1500 111 6.2-6.4 near 0.2 2 3.16-3.18 1510-1550 96 6.5-6.7 near 0.3 3 3.16-3.18 1480-1540 107 6.4-6.6 near 0.3 4 3.22-3.24 1420-1490 115 6.5-6.9 near 0.3 5 3.17-3.19 1510-1610 76 5.4-5.6 near 0.3 Acid Dipping Test Each disc test piece for thrust test as shown in Fig. 1(a) was dipped in a 35% solution of hydrochloric acid raised to 80°C and was allowed to stand for 100 hours. Then, weight lapse rate was obtained according to the equation: (weight before dipping) - (weight after dipping) (weight before dipping) × 100 Fig. 2 and Table 4 give the test results. It can be seen that every disc test piece made of a ceramic material prepared by sintering Sample 1, 2 or 3, had a very small weight lapse rate compared with that using Sample No. 4 or 5. Flexural Strength Test I For each test piece for flexural strength test as shown in Fig. 1(b), the same acid dipping test was conducted to determine its flexural strength. Fig. 3 and Table 4 give the test results accompanying the corresponding results before the acid dipping test. In Fig 3, the left and right bar graphs for each Sample show flexural strength obtained before and after the acid dipping test, respectively. It can be seen that the test piece using Sample 5 did not attain the desired value of 90kgf/mm 2 even before the acid dipping test, whereas that using Sample 4 had the desired value (not less than 90kgf/mm 2 ) before the test, but after the test, the flexural strength fell below the desired value due to significant drop. In contrast to this, the flexural strength for every test piece using Sample 1, 2 or 3, was above the desired value before the test, and so it was even after the test although a slight drop occurred. Rolling Life Test after the acid dipping test As shown in Fig. 4(a), there was prepared a sample wherein the combination of three pieces of ball 2 for bearing (3/8 inch (9.5 mm) in diameter, made of bearing steel SUJ2), a race 3 made of bearing steel SUJ2 and a retainer 4 made of brass was placed on the disc test piece 1 for thrust test which had been used in the acid dipping test. The sample thus prepared was mounted on a disc 5 of a device for thrust test and was rotated in the direction illustrated by an arrow while loading a load to the race 3 through a load axis 6. Setting the upper limit of rotation time to 400 hours, the life of the disc test piece 1 was defined as the moment when a vibrometer installed in the device indicated a value exceeding the fixed value. There was also observed the rolling contact surface in the disc test piece 1 after the rolling life test. Test Conditions Lubricating Oil: Spindle oil #60 Load: It was increased gradually as shown in Fig. 4(b), that is, 100kgf for 24 hours; 250kgf for 48 hours; 400kgf for 328 hours: totalled 400 hours Rotation Speed: 1200r.p.m. Testing Time : Max. 400 hours Fig. 5 and Table 4 give the test results. It can be seen that every disc test piece using Sample 4 or 5 was broken in less than 100 hours due to wear accompanied by peeling over the entire rolling contact surface. In contrast to this, every disc test piece using Sample 1, 2, or 3 had no peeling on its rolling contact surface even after 400-hour test, retaining sufficient strength after the acid dipping test. Sample No. Weight lapse rate (%) Flexural strength (kfg/mm 2 ) Life (hr) Conditions of rolling contact surface Before dipping After dipping 1 slight 111 97 400 no flaking Good 2 slight 96 94 400 no flaking Good 3 slight 107 92 400 no flaking Good 4 0.2 115 77 81.0 Entire wear (peeling) 5 0.015 76 64 82.8 Entire wear (peeling) Alkali Dipping Test Each disc test piece similar to that used in the acid dipping test was dipped in a 35% solution of potassium hydroxide raised to 80°C and was allowed to stand 100 hours. There was obtained a weight lapse rate (%) according to the equation: (weight before dipping) - (weight after dipping) (weight before dipping) × 100 Fig. 6 and Table 5 give the test results. It can be seen that every weight lapse rate for the disc test piece using Sample 1, 2 or 3, was extremely smaller than that using Sample 4 or 5. Flexural Strength Test II Using similar test pieces used in the previous flexural strength test, another alkali dipping test was conducted under the same conditions as in the foregoing to determine each flexural strength. Fig. 7 and Table 5 give the test results accompanying the corresponding results before the alkali dipping test. In Fig. 7, the left and right bar graphs for each Sample show flexural strength obtained before and after the alkali dipping test, respectively. It can be seen that the flexural strength for the test piece using Sample 5 was less than the desired value of 90kgf/mm 2 even before the alkali dipping test. On the other hand, that of the test piece using Sample 4 exceeded the desired value of not less than 90kgf/mm 2 , but after the alkali dipping test, it fell below the desired value due to significant drop. In contrast to this, the flexural strength for the test piece using Sample 1, 2 or 3 was above the desired value, and so it was even after the alkali dipping test although a slight drop occurred. Rolling Life Test after Alkali Dipping Test Using the device illustrated in Fig. 4(a), there was determined rolling life for each disc test piece after the alkali dipping test under the same conditions as described in the rolling life test after the acid dipping test. There was also observed the rolling contact surface in each disc test piece after the alkali dipping test. Fig. 8 and Table 5 give the test results. It can be seen that every disc test piece using Sample 4 or 5 was broken in less than 200 hours, whereas that using Sample 1, 2 or 3 had life over 300 hours and also exhibited sufficient strength after the alkali dipping test. Sample No. Weight lapse rate (%) Flexural strength (kfg/mm 2 ) Life (hr) Conditions of rolling contact surface Before dipping After dipping 1 0.004 111 95 301.5 Wearing-out (peeling) 2 0.004 96 91 349.1 Wearing-out (peeling) 3 0.004 107 96 361.0 Wearing-out (peeling) 4 0.042 115 80 50.5 Wearing-out (peeling) 5 0.006 76 67 175.2 Wearing-out (peeling) EXAMPLES EXAMPLE 1 Using the sintering material of Sample 3, an inner and an outer ring and balls for a radial ball bearing corresponding to Reference No. 6206 defined in Japanese Industrial Standard(JIS) were prepared and combined with a retainer made of polytetrafluoroethylene to obtain a bearing, which was then continuously rotated in an atmosphere of a 10% hydrochloric acid and a 30% nitric acid with a radial load of 5kg at a rotation speed of 10r.p.m. As a result, it was confirmed that it had been satisfactorily rotating over 4000 hours. COMPARATIVE EXAMPLE 1 The steps in Example 1 were repeated except the use of Sample 4. As a result, it was confirmed that a gap between the bearing became greater in 4000 hours, failing to serve as a bearing.

Claims: A rolling bearing comprising a pair of races and a plurality of rolling elements provided between both races, wherein at least the rolling elements are made of a ceramic material prepared by sintering a sintering material of silicon nitride containing MgAl 2 O 4 of spinel structure, silicon oxide and silicon carbide as sintering agents and optionally containing a further sintering assistant selected from the group comprising titanium oxide, hafnium oxide, tungsten oxide, titanium carbide, hafnium carbide and tungsten carbide, wherein the MgAl 2 O 4 of spinel structure is present in an amount of 0.5 % to 6 % by weight based on the total amount of the sintering material, wherein silicon oxide is present in an amount of 0.1 % to 1 % by weight based on the total amount of the sintering material, wherein silicon carbide is present in an amount of 3 % to 5 % by weight based on the total amount of the sintering material, and wherein each of the optional further components is present in an amount of not more than 1 % by weight based on the total amount of the sintering material, the balance of the total amount of the sintering material being silicon nitride. The rolling bearing according to claim 1, wherein the sintering material contains α-type silicon nitride. The rolling bearing according to claim 1 or 2, wherein the sintering material contains silicon nitride whose mean particle diameter ranges from 0.4 µm to 1.5 µm. The rolling bearing according to any of claims 1 to 3, wherein the sintering material contains three types of sintering assistants comprising silicon oxide, silicon carbide and an MgAl 2 O 4 of spinel structure, the sintering assistants being present in an amount of 6 % to 11 % by weight based on the total amount of the sintering material. The rolling bearing according to any of claims 1 to 3, wherein the sintering material contains other components than the three types of sintering assistants comprising silicon oxide, silicon carbide and an MgAl 2 O 4 of spinel structure. The rolling bearing according to any of claims 1 to 5, wherein the sintering material contains MgAl 2 O 4 of spinel structure in an amount of 3.5 % by weight and silicon oxide in an amount of 0.5 % by weight. The rolling bearing according to any of claims 1 to 6, wherein the sintering material contains silicon carbide in an amount of 5 % by weight. The rolling bearing according to any of claims 1 to 3 and 5 to 7, wherein the sintering material contains titanium oxide in an amount of 1 % per weight. The rolling bearing according to any of claims 1 to 8, which includes a retainer for holding the rolling element, the retainer being entirely made of fluoro carbon polymers, alternatively, the retainer surfaces being entirely covered with a baking film made of fluoro carbon polymers.

Inventors: HAYASHIDA KAZUNORI, IKEDA ISAO, TAKEBAYASHI HIROAKI, YABE HISAO, HAYASHIDA, KAZUNORI, IKEDA, ISAO, TAKEBAYASHI, HIROAKI, YABE, HISAO, IKEDA, ISAO, 502, EKUSHIDO-TSURUMI
Applicants: KOYO SEIKO CO, KOYO SEIKO CO., LTD.
Application year: 1994
Main classification: F16C33
IPC codes: F16C33, C04B35