Coated golf ball

Abstract: A coated golf ball comprising a core, a cover layer covering said core and a white paint layer coated on said cover wherein said cover is mainly composed of trans-polyisoprene, said paint layer comprising one or more white coating layers and clear coating layers, the white paint for forming said white paint layer comprising 20 to 70% by weight of a white pigment and 0.005 to 0.10% by weight of a blue pigment based on the solid content of the white paint, wherein said blue pigment is selected from ε-phthalocyanine blue or indanthrone blue or a mixture of two or more thereof.

Description: FIELD OF THE INVENTION The present invention relates to a golf ball having a surface coated with a paint, i.e. a coated golf ball. More particularly, it relates to a coated golf ball having a stabilized color tone and improved weathering properties. A golf ball covered with a balata cover remains popular because of its superior performance. The golf baLl with a balata cover has poor whiteness in comparison with a golf ball covered with an ionomer resin cover, because the balata cover itself has dark and dull color and even if coated with a white paint, its whiteness is insufficient. In order to improve the whiteness of a golf ball with a balata cover. Japanese Kokai Publication Hei 4(1992)-500295 suggests formulating suitable amounts of blue and violet pigments in white paint. However, when two kinds of coloring pigments are formulated, it is necessary to control the amount of each pigment delicately. When the amount of one pigment becomes larger than that of the other one, the color tone of the resulting golf ball varies greatly, which results in variability of products. Furthermore, since two kinds of pigments are formulated, it takes a lot of time to disperse each pigment during a mixing process. Also, there is a problem that the balata cover is discolored due to weathering discoloration of the cover and paint. Under these circumstances, the present inventors have intensively studied in order to solve the above problem on the formulation of two kinds of pigments. As a result, the present invention has been completed. The main object of the present invention is to provide a coated golf ball having stabilized colour tone and improved weathering properties. This object as well as other objects and advantages of the present invention will become apparent to those skilled in the art from the following description. That is, the present invention provides a coated golf ball comprising a core, a cover layer covering said core and a white paint layer coated on the cover layer, wherein said cover layer is mainly composed of transpolyisoprene, said paint layer comprising one or more white coating layers and clear coating layers, characterised in that the white paint for forming the white paint layer comprises in the range of 20 to 70% by weight of a white pigment and, as sole coloured pigment, from 0.005 to 0.10% by weight of a blue pigment based on the solids content of the white paint, wherein the blue pigment is ε-phthalocyanine blue, indanthrone blue or a mixture thereof. The present invention provides the improvement of a golf ball covered with a balata cover. The golf ball of the present invention comprises a core and a cover covering the core. The core may be any one which has been used for golf balls, but generally a thread wound core made by winding rubber thread on a liquid center or a solid center. The cover of the present invention is mainly composed of trans-polyisoprene, i.e. so-called "balata cover" which has been used for golf balls. The white paint for coating the golf ball of the present invention generally comprises a main resin and a white pigment. The main resin can be any resin which has been used for golf balls, but generally includes epoxy resin, acrylic resin and urethane resin. The preferred main resin is urethane resin. The amount of the main resin is preferably within the range of 20 to 80% by weight, based on the solids content of the white paint. The term "solids content" means the amount of solid components in the white paint from which liquid components are excluded. The white paint comprises a white pigment in an amount of 20 to 70% by weight based on a solids content of the white paint. The white pigment may be those which have hitherto been used for golf balls, for example titanium oxide and barium sulfate. When the amount of the white pigment is smaller than 20% by weight, the coating hiding power becomes inferior and, therefore, the desired white colour cannot be obtained. When the amount exceeds 70% by weight, the physical properties of the coating become inferior. The amount is preferably 30 to 60% by weight. In addition to the above components, various additives, curing catalysts and diluents may be contained in the white paint. Examples of the additives include ultraviolet inhibitors, fluid agents, sealing pigments, fluorescent agents and fluorescent brighteners. The amount of these additives is generally 0.1 to 10% by weight based on the solids content of the paint. As the fluorescent agent or fluorescent brightener contained in the white paint, for example, there are those which are normally known and are used for golf balls. Examples include 2,5-bis[5'-t-butylbenzoxazolyl (2)]thiophene (commercially available from Japan Ciba Geigy Co. as Ubitex OB), 7-(2h-naphthol(1,2-d)-triazol-2-yl)-3-phenyl-cusline (commercially available from Sandz Co. as Leucopure EGM), biazoline derivative (commercially available from Morbey Chemical Corporation as Phorwhite K-2002), oxazoles (commercially available from Sumitomo Chemical Co., Ltd. as Whitefuilar HCS, PCS, B), and fluorescent brighteners (commercially available from Hoechst Japan Co. as Hostalux KCB). The amount thereof is 0.005 to 1.0% by weight based on the solids content of the paint. Examples of the diluent formulated in the white paint include ketones such as acetone and methyl ethyl ketone; aromatic hydrocarbons such as toluene and xylene; and esters such as ethyl acetate. The amount of the diluent is not specifically limited, but is preferably 30 to 80% by weight based on the solids content of the white paint. As the blue pigment which is a feature of the present invention ε-phthalocyanine blue, indanthrone blue or a mixture thereof is used. The amount of the blue pigment is 0.005 to 0.1% by weight, preferably 0.01 to 0.07% by weight based on the solids content of the white paint. When the above specific blue pigment (ie. ε-phthalocyanine blue or indanthrone blue) is used, a golf ball having an L* value, an a* value and a b* value representing the colour tone of, respectively, 85 to 95, 0 to -2.5 and -5 to -9.5, and Wcie is 100 to 120, can be obtained using Lab and Wcie. When these values are not within the above ranges, the resulting golf ball with a balata cover lacks whiteness. In the production of the coated golf ball of the present invention, the white paint containing the above blue pigment is applied on the body of the golf ball one or more times, and then a clear paint is applied thereon. The clear paint can be of an epoxy type, acrylic type or urethane type, but does not contain a pigment. The clear paint layer is known in the production of golf balls. According to the present invention, the colour tone of the golf ball after coating of paint can be controlled easily, and a preferable whiteness can be obtained even for a golf ball covered with a balata cover. Further, an excellent golf ball having little weathering discolouration can be obtained. The following non-limiting Examples and Comparative Examples illustrate the present invention in detail: Examples 1 to 5 and Comparative Examples 1 to 3 Paints A to D (Examples) and paints E to G (Comparative Examples) were prepared by mixing the components shown in table 1 according to a conventional method. Example No. Comparative Example No. A B C D E F G [Formulation] Resin to be used is urethane in all Examples and Comparative Examples (Amount: weight % based on the solids content of the coat) White pigment (titanium oxide) 40 50 55 40 50 15 40 Blue pigment (ε-Phthalocyanine blue) 0.05 0.015 0.05 Blue pigment (Indanthron blue) 0.06 0.04 Blue pigment (α-Phthalocyanine blue) 0.05 0.05 Violet pigment (Dioxazine) 0.025 On the golf ball covered with a balata cover obtained by a conventional method, a white coat having two layers was formed using the above paint. Thereafter, the colour tone, visual appearance, weathering discolouration, degree of visual discolouration, workability and variability of colour tone were evaluated. The kind of the paint used and the test results are shown in Table 2 below: Test method (1) Measurement of color tone Colorimeter CR221 manufactured by Minolta Co. (visual field of 2°, 3mm⊘, light source D 65 ), according to Y x y measurement The formula of whiteness degree of CIE·ISO: Wcie = Y + 800 (X 0 - X) + 1700 (Y 0 - Y) wherein X 0 and Y 0 are respectively chromaticity coordinate of perfect diffuser of D 65 lighting, X 0 is 0.3127 and Y 0 is 0.3291. (2) Discoloration after weathering After treating with a sunshine weather-o-meter for 120 hours, an L* value, an a* value and a b* value before and after treatment were measured by a colorimeter to determine ΔL*, , Δa*, Δb* and ΔE. Evaluation was conducted according to the obtained data and visual observation. (3) Workability After mixing with a homomixer for one hour, the obtained mixture was allowed to stand for twenty-four hours. Thereafter, a dispersion state of the pigment was confirmed by visual observation. Good: There is no problem about pigment dispersion.

Claims: A coated golf ball comprising a core, a cover layer covering said core and a white paint layer coated on said cover layer, wherein said cover layer is mainly composed of a trans-polyisoprene, said paint layer comprising one or more white coating layers and clear coating layers, characterised in that the white paint for forming the white paint layer comprises in the range of from 20 to 70% by weight of a white pigment and, as sole coloured pigment, from 0.005 to 0.10% by weight of a blue pigment based on the solids content of the white paint, wherein the blue pigment is ε-phthalocyanine blue, indanthrone blue or a mixture thereof. A coated golf ball as claimed in claim 1 wherein the white paint comprises in the range of from 30 to 60% by weight of a white pigment. A coated golf ball as claimed in claim 1 or claim 2 wherein the white pigment is titanium oxide, barium sulfate or a mixture thereof. A coated golf ball as claimed in any one of claims 1 to 3 wherein the white paint comprises in the range of from 0.01 to 0.07% by weight of the blue pigment based on the solids content of the white paint. A coated golf ball as claimed in any one of claims 1 to 4 wherein the white paint further comprises additives, curing catalysts, diluents or a mixture of two or more thereof. A coated golf ball as claimed in claim 5 wherein the additives comprise ultraviolet inhibitors, fluid agents, sealing pigments, fluorescent agents, fluorescent brighteners or a mixture of two or more thereof. A coated golf ball as claimed in claim 5 or claim 6 wherein the amount of the additives is in the range of from 0.1 to 10% by weight based on the solids content of the paint.

Inventors: HORIUCHI KUNIYASU, MARUOKA KIYOTO, HORIUCHI, KUNIYASU, MARUOKA, KIYOTO
Applicants: SUMITOMO RUBBER IND, SUMITOMO RUBBER INDUSTRIES, LTD.
Application year: 1994
Main classification: A63B37
IPC codes: C09D133, C09D175, A63B37, C08J7, B32B25, C09D7, C09D163, B05D7