Polyolefin composition molded article

Abstract: Article obtained by blow molding or injection molding of a polyolefin composition, which comprises: (A) 1 to 99 % by weight of a polyolefin having the following properties of (a) to (e); (a) a ratio of kinematic viscosity η 1 at a frequency of 10 -1 rad/sec to kinematic viscosity η 2 at a frequency of 10 rad/sec at a temperature of 190°C according to a kinematic viscoelasticity determination method of 4 to 20, (b) a crystallization peak temperature Tcp according to a Differential Scanning Calorimetry of 110 to 130°C, (c) a ratio Tmp/(Tmp-Tcp)= 3.0 to 9.8 , and (d) a crystal structure exhibiting a-axial orientation in a diffraction pattern according to a X-ray diffraction method, and (B) 99 to 1 % by weight of a propylene resin having the following properties of (f) and (g); (f) a ratio of kinematic viscosity η 1 at a frequency of 10 -1 rad/sec to kinematic viscosity η 2 at a frequency of 10 rad/sec at a temperature of 190°C according to a kinematic viscoelasticity determination method of below 4, (e) and no crystallization structure exhibiting a-axial orientation in a diffraction pattern according to a X-ray diffraction method and (g) a ratio Mw/Mn of 8.0 or below.

Description: BACKGROUND OF THE INVENTION 1) Field of the Invention The present invention relates to a blow molded or an injection molded article. 2) Related Prior Art Propylene resin is generally cheap and excellent in characteristics such as transparency, mechanical strength, heat resistance, gloss, chemical resistance, oil resistance, rigidity, flex fatigue resistance, etc., and is used in wide fields as various industrial materials and packaging materials. When a propylene resin is molding-processed, its molecular chains are cooled to solidify in a stretched state toward a machine direction (hereinafter referred to as "M.D") by shear effects during molding-flowing, thereby generating remarkable anisotropy in properties. Generally, when orientation in a molded article is high, anisotropy in properties is generated in the molded article, whereby properties in a transverse direction to the flow (hereinafter referred to as "T.D") deteriorate. Moreover, sometimes, heat resistance, weathering resistance, etc. deteriorate owing to interior strains due to molecular orientation. In order to improve it, various improving methods have been so far proposed and practically applied. For example, in extrusion molded films, there has been conducted secondary processing in which after molding biaxially stretched processing is conducted to keep the balance between M.D and T.D. In injection molded articles and blow molded articles, there has been applied a method in which after molding a heat treatment is conducted. However, the secondary processing method for films has such problems that not only a high cost for the processing is necessary, but also the use is limited since heatsealability deteriorates. The method in which after molding a heat treatment is conducted provides complicated production steps and consequently has problems in economy and productivity. Hitherto, as a packaging material for articles requiring a sterilizing treatment step, e.g, typically processed foodstuffs, a parcel that is called "retort pouch" has been used. In the pouch, for long term-preservation, laminates having layers being excellent in gas barrier property have been used. Recently, as a material of a pouch being excellent in heat resistance, cold resistance and impact resistance, there have been used multilayered laminates comprising the combination of block copolymer of polypropylene used in most inner layer, a polyester film and an aluminum foil, e.g., layers of polyester/aluminum foil/block copolymer of polypropylene. However, the above-mentioned multilayered laminates have a drawback that tearabiliity thereof is inferior, thereby causing a problem that the pouch cannot be easily teared when it is opened. In attempts to improve tearability, it has been proposed to set a V-shaped or I-shaped cut, to provide unpierced sewing machine perforations, to conduct a near infrared ray treatment or an electric discharge treatment (JP-A 62-158648) for tear-expecting portions, etc. However, these procedures have a problem that tearability is still insufficient, so that a considerable force for tear is required owing to resistance for tear. SUMMARY OF THE INVENTION An object of the present invention, under the above-mentioned circumstances, is to provide a polyolefin composition having well-balanced properties in which anisotropy in mechanical strength generating during molding-processing is small, furthermore great tearability, superior rigidity, and a molded article thereof, and a multilayered laminate being excellent in tearability, rigidity, impact resistance and heatsealability. As a result of extensive studies to solve the problems of prior art, the present inventors have found that a polyolefin composition comprising a propylene resin and polyolefin having a particular kinematic viscosity ratio and a particular crystal structure can solve the problems and have established the present invention. According to one aspect of the present invention, there is provided an article obtained by blow molding or injection molding of a polyolefin composition which comprises: (A) 1-99% by weight of a polyolefin having the following properties (a) to (d); (a) a ratio (η 1 /η 2 ) of the kinematic viscosity η 1 at an angular frequency of 10 -1 rad/s to the kinematic viscosity η 2 at an angular frequency of 10 rad/s at a temperature of 190°C of 4-20 according to a kinematic viscoelasticity determination method with a Mechanical Spectrometer, model RMS-800 of Rheometric Co., Ltd. at 190°C using a parallel plate, (b) a crystallization peak temperature Tcp (°C) of 110-130°C according to the Differential Scanning Calorimetry (DSC) method described in ASTM D3417-75, (c) a ratio Tmp/(Tmp-Tcp) of 3.0-9.8, wherein - Tmp(°C) represents the melting peak temperature according to a Differential Scanning Calorimetry (DSC) method described in ASTM D3417-75, and (d) a crystal structure exhibiting a-axial orientation in the diffraction pattern, when measured with a film having a thickness of 60 µm under the conditions of 50 kV and 40 mA using an X-ray diffraction apparatus RAD-II type C of K.K., Rigaku, Japan provided with a wide angle X-ray flat camera; and (B) 99-1% by weight of a propylene resin having the following properties (e) to (g); (e) a ratio (η 1 /η 2 ) of the kinemetic viscosity η 1 at an angular frequency of 10 -1 rad/s to the kinematic viscosity η 2 at an angular frequency of 10 rad/s at a temperature of 190°C of below 4 according to the kinematic viscoelasticity determination defined in (a), (f) no crystal structure exhibiting a-axial orientation in the diffraction pattern according to the X-ray diffraction method defined in (d), and (g) a ratio (Mw/Mn) of the weight average molecular weight Mw to the number average molecular weight Mn of 8.0 or below according to gel permeation chromatography. BRIEF DESCRIPTION OF THE DRAWINGS Fig.1 is a photograph showing a diffraction image of polypropylene (PP-2) in the present invention according to a X-ray diffraction method. Fig.2 is a photograph showing a diffraction image of conventional polypropylene (PP-4) according to a X-ray diffraction method. DETAILED DESCRIPTION OF THE INVENTION The present invention will be described in detail below. The (A) polyolefin for use in the present invention includes polyethylene, polypropylene, random copolymer of ethylene/propylene, block copolymer of ethylene/propylene, three-dimensional copolymer of ethylene/butene/propylene, copolymer of ethylene/α-olefin having 4 to 12 carbon atoms, etc. Examples of α-olefin include butene-1, 4-methylpentene-1, hexene-1, octene-1, etc. It is necessary that the (A) polyolefin has (a) a ratio ( η 1 /η 2 ) of kinematic viscosity η 1 at a frequency of 10 -1 rad/sec to kinematic viscosity η 2 at a frequency of 10 rad/sec at a temperature of 190°C according to a kinematic viscoelasticity determination method of 4 to 20. The term "kinematic viscoelasticity" herein means behaviors of the combination of viscosity and elasticity on vibrational (angular frequency) application of strains and stresses to a material. The kinematic viscoelasticity is determined by measuring a stress vs. a strain or a strain vs. a stress, e.g., according to the methods prescribed in ASTM D4065-90 and ASTM D4092-90. In the present invention, particularly, the kinematic viscoelasticity in the range of 10 -3 to 10 2 rad/sec was determined by Mechanical Spectromer, Model RMS-800, made by Rheometric Co., Ltd., at 190°C using a parallel plate. The kinematic viscosity ratio (η 1 /η 2 ) is 4 to 20, preferably 4 to 15, more preferably 5 to 15. When the kinematic viscosity ratio is below 4, anisotropy is large, whereby the balance between M.D and T.D deteriorates, whereas above 20 gel or fish-eyes increase, so that degradation of commodity's commercial value unpreferably occurs. It is necessary also that the (A) polyolefin has (b) a crystallization peak temperature Tcp of 110 to 130°C, and (c) Tmp/(Tmp-Tcp)=3.0 to 9.8 according to a Differential Scanning Calorimetry (DSC). Tcp is preferably 112 to 127°C, more preferably 113 to 125°C. When Tcp is below 110°C, anisotropy in mechanical strength becomes large, whereas above 130°C mechanical strength such as impact strength, etc., becomes unpreferably insufficient. When Tmp/(Tmp-Tcp) is below 3.0, anisotropy in mechanical strength is generated, whereas above 9.8 flexibility and mechanical strength such as impact strength etc., are unpreferably insufficient. The "Differential Scanning Calorimetry (DSC)" herein is a method in which a thermal change in a sample generating on elevating and lowering its temperature at a constant rate is determined as a thermal energy. The determination method is prescribed in ASTM D3417-75. The DSC for Tcp and Tmp is as follows. That is, in polyethylene, Tcp is a crystallization peak temperature in case of elevating a temperature to 190°C and then keeping at 190°C for 5 minutes, followed by lowering the temperature to 30°C at a temperature-lowering rate of 10°C/minute, and Tmp is a melting peak temperature in case of again elevating the temperature to 190°C at a temperature-elevating rate of 10°C/minute. In propylene resin, Tcp is a crystallization peak temperature in case of elevating a temperature to 230°C and then keeping at 230°C for 5 minutes, followed by lowering the temperature to 30° at a temperature-lowering rate of 20°C/minute, and Tmp is a melting peak temperature in case of again elevating the temperature to 230°C at a temperature-elevating rate of 20°C/minute. Furthermore, it is necessary that the (A) polyolefin has (e) a crystal structure exhibiting a-axial orientation in a diffraction pattern according to a X-ray diffraction method. The "X-ray diffraction method" herein is an analytical method applied phenomena that when a X-ray is irradiated to a crystal, scattered X-rays cancel each other in the direction wherein the wave phase is out of accord with each other and amplify each other in the direction wherein the wave phase is in accord with each other. There is a large number of researchs concerning analysis of crystal structure of polyolefin according to a X-ray diffraction pattern, e.g., L.E.Alexander, "X-Ray Diffraction Method in polymer" Interscience (1969), "Kobunshi" Vol. 14, No.158, P379 to 388, "Nihon Kagakukaishi", Vol 82, No.12, P1575 to 1577, etc. In the present invention, particularly, a film having a thickness of 60µm was irradiated in point focus for one hour under the conditions of 50KV and 40mA by a X-ray diffraction apparatus, made by K.K., Rigaku, Japan, RAD-II type C and then the diffraction pattern was measured with a wide angle X-ray flat camera. Fig.1 is an example of a X-ray pattern of polypropylene having a-axial orientation. The longitudinal direction corresponds to a film-flowing direction (M.D). In Fig.1, the meridian direction corresponds to a-axis and a diffraction image exhibiting orientation to the direction (one pair of white lines at a lower portion and an upper portion in the horizontal direction) is clearly observed. On the other hand, Fig.2 is an example of polypropylene having no a-axial orientation wherein its diffraction image displays a shape of ring since its crystal has no orientation. When the (A) polyolefin used in the present invention has no a-axial orientation, improvement effects in anisotropy are not provided. The (A) polyolefin used in the present invention includes, for example, polypropylene irradiated with electron beams or gamma-rays in vacuum or in an inert gas atmosphere, polypropylene obtained in the presence of δ type of porous titanium trichloride as a catalyst, high density polyethylene obtained in the presence of a fixed catalyst supported chromium or molybdenum on silica or alumina carrier and then sintered thereof at a high temperature, etc. The (B) propylene resin used in the present invention includes polypropylene, block copolymer of ethylene/propylene, random copolymer of ethylene/ propylene, copolymer of ethylene/butene/propylene and a mixture of at least two polymers thereof, furthermore having the following properties. That is, the (B) polypropylene resin has (f) a ratio (η 1 /η 2 ) of kinematic viscosity η 1 at a frequency of 10 -1 rad/sec to kinematic viscosity η 2 at a frequency of 10 rad sec at a temperature of 190°C according to a kinematic viscoelasticity determination method of below 4. Moreover, the (B) propylene resin has (g) no crystal structure exhibiting a-axial orientation in a diffraction pattern according to a X-ray diffraction method. The example of the X-ray diffraction pattern is shown in Fig.2. It is preferable that the (B) propylene resin has a ratio (Mw/Mn) of weight average molecular weight Mw to number average molecular weight Mn according to a gelpermeation gaschromatgraphy of 4.0 to 5.5. The mixing proportion of (A) polyolefin in the polyolefin composition according to the present invention is 1 to 99% by weight, preferably 3 to 50% by weight, more preferably 5 to 40% by weight. When a mixing proportion of the (A) polyolefin is below 1% by weight, improvement effects for anisotropy in mechanical strength is not provided, whereas above 99% by weight impact strength tends to deteriorate. MFR (measured under a load of 2.16kg at 230°C according to JIS K7210) of the polyolefin composition according to the present invention is not particularly limited, and is usually in a range of 0.1 to 100g/10minutes, depending on molding methods. The present polyolefin composition can contain conventional additives, if required. Examples of additives include a nucleating agent, an antioxidant, an ultraviolet absorber, an antistatic agent, a plasticizer, a lubricating agent, a coloring agent, various fillers, etc. As procedure for blending the above-mentioned components to prepare the present polyolefin composition, known conventional procedures, for example, a procedure for blending using a ribbon blender, a Henschel mixer, etc., and a procedure for melt-kneading using a kneader, mixing rolls, a Banbury mixer, an extruder, etc., are suitably applied. Method for molding applicable to the present resin composition is limited to injection molding and blow molding. By these methods, it is possible to mold films, sheets, tubes, bottles, etc. PREFERRED EMBODIMENTS OF THE INVENTION The present invention will be described in detail below, referring to Examples, which show embodiments of the present invention and are not limitative of the present invention. In the following Examples and Comparative Examples, the following test methods were employed. Film tensile strength test Tensile strength at yield, tensile strength at break and elongation at break were measured at a tensile velocity of 500mm/min according to JIS Z1707. Film Young's modulus test Measurement was made according to ASTM D882. Film tear strength test Ermendorf's tear strength was measured according to JIS K7128B. Film cuttingability test The situation in case of cutting a film into a form of circle with empty hands was observed and evaluation was made based on the following four standards: o ○ : Possible to easily cut a film. ○ : Possible to cut a film with some resistance. Δ : Managed to cut a film somehow or other, though it is difficult to cut the film since a portion of the film has stretched. × : Impossible to cut a film because the film has stretched. Flexural modulus test Measurement was made at 23°C and a relative humidity of 50% according to JIS K7203. Falling impact test 290ml of water was charged into each ten cylindrical bottles having a capacity of 300ml (inner diameter; 55mm, thickness; 1.0mm), prepared by blow molding. Then, the cylindrical bottles were allowed to fall from a height of 1 m at 0°C. The proportion of the breaks was represented by %. Heatsealability test Each other of X layers in a multilayered laminate was heat-sealed by a heatsealer, made by Tester Sangyo, K.K., under a pressure of 2 kg/cm 2 at a seal time of 1 second to prepare a test piece having a width of 15mm and a strip-shape of paper. Then, its heatseal strength was measured at a tensile speed of 300mm/minute by a tensile tester, made by Orientic K.K. and then a temperature at which the heatseal strength came to be a width of 1kg/15mm or above was determined. In this case, the temperature was changed in the interval of 5°C. Film impact strength test Measurement was made by a pendulum-type, impact tester (1/2-inch hemisphere), made by Toyo Seiki Seisakusho, K.K., Japan. (A) Preparation of polyolefin Powders of polypropylene having MFR of 0.6g/10min. (at 230°C under a load of 2.16 kg) were subjected to irradiation with 5 Mrad as a dose of radioactivity by an electron ray irradiation apparatus, made by Nissin Highvoltage K.K., Japan, in a bag of a multilayered film (polyethylene/copolymer of ethylene-vinylalcohol/polyethylene) having a thickness of 100µm replaced with nitrogen, and then to a heat treatment at 130°C for 60 minutes to prepare polypropylene (PP-1). In the same manner as in PP-1, the powders of polypropylene were subjected to irradiation with 10 Mrad as a dose of radioactivity and then to a heat treatment at 130°C for 60 minutes to prepare polypropylene (PP-2). A δ type-titanium trichloride obtained by the following process was used for preparation of propylene (PP-3). This is, β type-titanium trichloride obtained by reduction of titanium tetrachloride with diethylaluminum chloride was treated with isoamylether to extract aluminum trichloride contained as an eutectic crystal and then treated with titanium tetrachloride, whereby a δ type-titanium trichloride catalyst was obtained. Propylene gas was charged in a stainless autoclave of 5ℓ at 80°C in the presence of the above-mentioned δ type-titanium trichloride catalyst to prepare polypropylene (PP-3) having MFR of 8.8g/10min. Isobutane was charged in an autoclave of 5ℓ in the presence of a fixed catalyst supported chromium trioxide on a silica-aluminum carrier and sintered thereof at 820°C and then ethylene gas was charged thereto at 80°C to prepare polyethylene (PE-1) having MFR of 11.3g/10min. (JIS K7210, at 190°C, under a load of 2.16kg). The solid catalyst obtained by the following process was used for preparation of polyethylene (PE-2) for comparison. That is, aluminum chloride anhydride, diphenyldiethoxysilane and magnesium ethylate were reacted to wash with n-hexane and then reacted titanium tetrachloride, whereby a solid catalyst was obtained. Ethylene gas was charged in an autoclave of 5ℓ at 80°C in the presence of the above-mentioned solid catalyst to prepare polyethylene (PE-2) for comparison having MFR of 12.5kg/10min.. (B) Preparation of propylene resin The catalyst obtained by the following process was used for preparation of polypropylene (PP-4). That is, a crystal obtained by adding aluminum trichloride to titanium trichloride and γ-butylolactone were pulverized together, whereby a catalyst was obtained. Propylene gas was charged in an autoclave of 5ℓ at 80°C in the presence of the above-mentioned catalyst to prepare polypropylene (PP-4) having MFR of 7.8g/10min. (JIS K7210, at 230°C, under a load of 2.16 kg). Moreover, in the same manner as in polypropylene (PP-4) except that titanium tetrachloride, triethylaluminum and cyclohexylmethyldimethoxysilane were used as components of a catalyst, polypropylene (PP-5) having MFR of 6.1g/10min. was prepared. In the same manner as in polypropylene (PP-5), polypropylene (PP-6) having MFR of 8.5g/10min. and random copolymer of ethylene/propylene (PP-7) having an ethylene content of 3.0% by weight and MFR of 0.5g/10min. were prepared. The ratio of Mw/Mn of PP-4, -5, -6 and -7 each was 6.1, 4.8, 6.8 and 6.2. The kinematic viscosity ratio of η 1 /η 2 , Tmp/Tcp, Tmp/(Tmp-Tcp) and existence or no existence of a-axial orientation are in table 1. Example 1. 5 parts by weight of PP-1 as (A) component, 95 parts by weight of PP-4 as (B) component, 0.35 parts by weight of 1, 3, 2, 4-di(methylbenzylidene)sorbitol as a nucleating agent, 0.1 parts by weight of pentaery-thrityl-tetrakis [3-(3,5-di-t-butyl-4-hydroxylphenyl) propionate] and 0.05 parts by weight of octadencyl-3-(3,5-di-t-butyl-hydroxyphenyl)propionate as antioxidants and 0.1 parts by weight of calcium stearate as a stabilizer were mixed by a super mixer, SMV-20, made by Kawata Seisakusho K.K., Japan and then pelletized through a vent-type twin screw extruder, AS-302, made by Tanifuji Kikai Kogyo K.K., Japan. From the thus obtained pellets, films having a thickness of 40µm were obtained through a die film unit, 40mm T, made by Yosii Tekko K.K., Japan, and the films were tested for tensile strength, Young's modulus, tear strength, cuttingability and flexural modulus. The results are shown in table 2. Examples 2 to 11 and Comparative Examples 1 to 5 Films were prepared and evaluated in the same manner as in Example 1 except that (A) component and (B) component in species and blending amounts shown in table 2 were used. The results are shown in Table 2. Falling impact was tested for Examples 4, 5, 8 and 11 and Comparative Examples 5 and 6, in which blow molding can be conducted.

Claims: Article obtained by blow molding or injection molding of a polyolefin composition which comprises: (A) 1-99% by weight of a polyolefin having the following properties (a) to (d); (a) a ratio (η 1 /η 2 ) of the kinematic viscosity η 1 at an angular frequency of 10 -1 rad/s to the kinematic viscosity η 2 at an angular frequency of 10 rad/s at a temperature of 190°C of 4-20 according to a kinematic viscoelasticity determination method with a Mechanical Spectrometer, model RMS-800 of Rheometric Co., Ltd. at 190°C using a parallel plate, (b) a crystallization peak temperature Tcp (°C) of 110-130°C according to the Differential Scanning Calorimetry (DSC) method described in ASTM D3417-75, (c) a ratio Tmp/ (Tmp-Tcp) of 3.0-9.8, wherein Tmp(°C) represents the melting peak temperature according to a Differential Scanning Calorimetry (DSC) method described in ASTM D3417-75, and (d) a crystal structure exhibiting a-axial orientation in the diffraction pattern, when measured with a film having a thickness of 60 µm under the conditions of 50 kV and 40 mA using an X-ray diffraction apparatus RAD-II type C of K.K., Rigaku, Japan provided with a wide angle X-ray flat camera; and (B) 99-1% by weight of a propylene resin having the following properties (e) to (g); (e) a ratio (η 1 /η 2 ) of the kinemetic viscosity η 1 at an angular frequency of 10 -1 rad/s to the kinematic viscosity η 2 at an angular frequency of 10 rad/s at a temperature of 190°C of below 4 according to the kinematic viscoelasticity determination defined in (a), (f) no crystal structure exhibiting a-axial orientation in the diffraction pattern according to the X-ray diffraction method defined in (d), and (g) a ratio (Mw/Mn) of the weight average molecular weight Mw to the number average molecular weight Mn of 8.0 or below according to gel permeation chromatography.

Inventors: IWAMOTO SATOSHI, WATANABE KAZUYUKI, IWAMOTO, SATOSHI, WATANABE, KAZUYUKI, Iwamoto, Satoshi, Showa Denko K.K., Watanabe, Kazuyuki, Showa Denko K.K.
Applicants: SHOWA DENKO KK, SHOWA DENKO KABUSHIKI KAISHA
Application year: 1994
Main classification: C08L23
IPC codes: C08L23