Silicone rubber composition for fixing roll service

Abstract: The present invention provides a silicone rubber composition for fixing roll service. More specifically, the invention relates to a silicone rubber composition for fixing roll service that is easily molded into a fixing roll as used in devices such as electrophotographic copiers, facsimile machines, and laser printers and that yields a fixing roll with an excellent mechanical strength and excellent toner release properties.

Description: The present invention relates to a silicone rubber composition for fixing roll service that is easily molded into a fixing roll as used in devices such as electrophotographic copiers, facsimile machines, and laser printers and that yields a fixing roll with an excellent mechanical strength and excellent toner release properties. Contact thermal fixing is widely used in the devices described above. In a typical process, the toner image, after its electrophotographic formation on a photoreceptor and transfer to copy paper, is fixed by a fixing roll. The fixing rolls used for contact thermal fixing are fabricated by coating a silicone rubber composition on the circumference of a metal shaft and then curing the composition. The prior art of silicone rubber compositions for fixing roll service are exemplified by the following: (i) the silicone rubber composition of JP-A 57-149354 [149,354/1982], which consists of alkenyl-containing organopolysiloxane with a viscosity of 100 to 100,000 mPa.s (centipoise) at 25°C, organohydrogenpolysiloxane with a viscosity of 1 to 5,000 mPa.s (centipoise) at 25°C, inorganic filler, alkenyl-free organopolysiloxane with a viscosity of 10 to 5,000 mPa.s (centipoise) at 25°C, and platinum catalyst; (ii) the silicone rubber composition of JP-A 63-186024 [186,024/1988], which consists of organopolysiloxane that contains at least 2 alkenyl groups in each molecule, organopolysiloxane resin that contains at least 2 silicon-bonded hydrogen atoms in each molecule, and platinum catalyst; and (iii) the silicone rubber composition of JP-A 4-164741 [164,741/1992], which consists of polyorganosiloxane that contains at least 2 vinyl groups in each molecule and has a viscosity at 25°C of 500 to 500,000 mPa.s (centipoise), organohydrogensiloxane that contains at least 3 silicon-bonded hydrogen atoms in each molecule, inorganic filler, and a platinum compound. However, the silicone rubber compositions for fixing roll service taught in this art contain an inorganic filler such as silica micropowder, quartz powder, and so forth. Fixing rolls obtained therefrom suffer from a gradual decline in their toner release properties with increasing copy mileage, and it eventually becomes impossible to obtain clear copies. In contrast, silicone rubber compositions for fixing roll service that lack an inorganic filler yield fixing rolls with a low mechanical strength that will not support practical applications. The present invention introduces an inorganic filler-free silicone rubber composition for fixing roll service that comprises: (A) 100 weight parts of diorganopolysiloxane mixture comprising essentially: (a) 10 to 90 weight% of diorganopolysiloxane that contains at least 2 alkenyl groups in each molecule and that has a viscosity at 25°C of 100 to 100,000 mPa.s (centipoise) and (b) 90 to 10 weight% of diorganopolysiloxane that contains at least 2 alkenyl groups in each molecule and that has a viscosity at 25°C of at least 1,000,000 mPa.s (centipoise), (B) 5 to 100 weight parts of organopolysiloxane resin with the general formula (R 3 SiO 1/2 ) x (SiO 4/2 ) 1.0 in which R denotes a monovalent hydrocarbon group, 3-chloropropyl or 3,3,3-trifluoropropyl and x has a value of 0.6 to 4.0, (C) organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule, in a quantity that yields 0.6 to 20 moles silicon-bonded hydrogen in component (C) per 1 mole total alkenyl groups in components (A) and (B), and (D) platinum catalyst in a catalytic quantity to provide 0.1 to 500 weight parts of platinum metal for each one million weight parts of (A) plus (B). The diorganopolysiloxane mixture (A) is the principal material of the invention composition. It is composed of diorganopolysiloxanes (a) and (b). Diorganopolysiloxane (a) must contain at least 2 alkenyl groups in each molecule. The molecular structure of component (a) is not specifically restricted and may be straight chain, partially branched straight chain, resin, network, or cyclic. Straight chain and partially branched straight chain are preferred. The alkenyl group in component (a) is exemplified by vinyl, allyl, butenyl, pentenyl, and hexenyl, and the vinyl group is preferred. The alkenyl group may be bonded in any position on the molecular chain in terminal or nonterminal positions. There are no limitations on the non-alkenyl organic groups in component (a), and these groups are alkyl groups, such as methyl, ethyl, and propyl; aryl groups, such as phenyl, tolyl, and xylyl; aralkyl groups, such as benzyl, and phenethyl; and substituted alkyl groups, such as 3-chloropropyl, and 3,3,3-trifluoropropyl. Methyl and phenyl are the preferred non-alkenyl organic groups. The viscosity of component (a) at 25°C must fall in the range of 100 to 100,000 mPa.s (centipoise). The resulting fixing roll will have a sharply reduced mechanical strength when component (a) has a viscosity below 100 mPa.s (centipoise), while a component (a) viscosity in excess of 100,000 mPa.s (centipoise) makes the resulting silicone rubber composition difficult to handle and substantially impairs its ability to be molded into a fixing roll. Component (a) is: dimethylvinylsiloxy-endblocked dimethylpolysiloxanes, dimethylvinylsiloxy-endblocked methylvinylpolysiloxanes, dimethylvinylsiloxy-endblocked methylphenylpolysiloxanes, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylphenylsiloxane copolymers, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane-methylphenylsiloxane copolymers, trimethylsiloxy-endblocked methylvinylpolysiloxanes, trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane-methylphenyls iloxane copolymers, dimethylhydroxysiloxy-endblocked methylvinylpolysiloxanes, dimethylhydroxysiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, and dimethylhydroxysiloxy-endblocked dimethylsiloxane-methylvinylsiloxane-methylphenyls iloxane copolymers. Diorganopolysiloxane is component (b) that equips the fixing roll product with toner release properties. This component must contain at least 2 alkenyl groups in each molecule. The molecular structure of component (b) is not specifically restricted and may be straight chain, partially branched straight chain, resin, network, or cyclic. Straight chain and partially branched straight chain are preferred. The alkenyl group in component (b) is exemplified by vinyl, allyl, butenyl, pentenyl, and hexenyl, and the vinyl group is preferred. The alkenyl group may be bonded in any position on the molecular chain in terminal or nonterminal position. There are no limitations on the non-alkenyl organic groups in component (b), and these groups are alkyl groups, such as methyl, ethyl, and propyl; aryl groups, such as phenyl, tolyl, and xylyl; aralkyl groups, such as benzyl, and phenethyl; and substituted alkyl groups, such as 3-chloropropyl, and 3,3,3-trifluoropropyl. Methyl and phenyl are the preferred non-alkenyl organic groups. Component (b) must have a viscosity at 25°C of at least 1,000,000 mPa.s (centipoise). The fixing roll product has sharply reduced toner release properties as well as a diminished mechanical strength when component (b) has a viscosity below 1,000,000 mPa.s (centipoise). Component (b) is: dimethylvinylsiloxy-endblocked dimethylpolysiloxane gums, dimethylvinylsiloxy-endblocked methylvinylpolysiloxane gums, dimethylvinylsiloxy-endblocked methylphenylpolysiloxane gums, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymer gums, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylphenylsiloxane copolymer gums, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane-methylphenylS iloxane copolymer gums, trimethylsiloxy-endblocked methylvinylpolysiloxane gums, trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymer gums, trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane-methylphenyls iloxane copolymer gums, dimethylhydroxysiloxy-endblocked methylvinylpolysiloxane gums, dimethylhydroxysiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymer gums, and dimethylhydroxysiloxy-endblocked dimethylsiloxane-methylvinylsiloxane-methylphenyls iloxane copolymer gums. Component (A) is to contain 10 to 90 weight% component (a) with component (b) making up the remainder. The toner release properties of the fixing roll product are sharply reduced when component (A) contains more than 90 weight% component (a). At the other extreme, the resulting silicone rubber composition suffers from a sharply reduced curability and is also extremely difficult to handle when component (A) contains less that 10 weight% component (a). The organopolysiloxane resin (B) functions to improve the mechanical strength of the fixing roll product. This component has the general formula. (R 3 SiO 1/2 ) x (SiO 4/2 ) 1.0 The group R denotes monovalent hydrocarbon groups exemplified by alkyl groups, such as methyl, ethyl, and propyl; alkenyl groups, such as vinyl, allyl, butenyl, pentenyl, and hexenyl; aryl groups such as phenyl, tolyl, and xylyl; aralkyl groups, such as benzyl, and phenethyl; and 3-chloropropyl or 3,3,3-trifluoropropyl. At least one group R is preferably alkenyl. The subscript x in the preceding formula has a value of 0.6 to 4.0. The bases for this range are as follows: the use of organopolysiloxane resin having a value of x less than 0.6 yields a fixing roll with a sharply reduced mechanical strength, while organopolysiloxane resin in which x exceeds 4.0 does not exist. Component (B) is added to the invention composition at 5 to 100 weight parts per 100 weight parts component (A). The addition of component (B) at less than 5 weight parts per 100 weight parts component (A) yields a fixing roll product with a reduced mechanical strength. At the other extreme, silicone rubber compositions produced using more than 100 weight parts component (B) per 100 weight parts component (A) become very difficult to mold into fixing rolls. Organopolysiloxane (C) is a crosslinker that functions to cure the invention composition, and it must contain at least 2 silicon-bonded hydrogen atoms in each molecule. While the viscosity of component (C) is not particularly restricted, viscosities in the range of 10 to 5,000 mPa.s (centipoise) are preferred. The molecular structure of component (C) is also not particularly restricted and is exemplified by straight chain, partially branched straight chain, resin, network, and cyclic. Straight-chain and partially branched straight-chain molecular structures are preferred. No particular restrictions apply to the bonding position for the silicon-bonded hydrogen in component (C), and it may be bonded, for example, in terminal or nonterminal position on the molecular chain. The organic groups in component (C) are not particularly restricted and are monovalent hydrocarbon groups such as alkyl groups, methyl, ethyl, and propyl; aryl groups, phenyl, tolyl, and xylyl; aralkyl groups, benzyl, and phenethyl; and 3-chloropropyl or 3,3,3-trifluoropropyl. Component (C) is: dimethylhydrogensiloxy-endblocked dimethylpolysiloxanes, dimethylhydrogensiloxy-endblocked methylhydrogenpolysiloxanes, dimethylhydrogensiloxy-endblocked methylphenylpolysiloxanes, dimethylhydrogensiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, dimethylhydrogensiloxy-endblocked dimethylsiloxane-methylphenylsiloxane copolymers, trimethylsiloxy-endblocked methylhydrogenpolysiloxanes, trimethylsiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-endblocked methylhydrogensiloxane-methylphenylsiloxane copolymers, dimethylhydroxysiloxy-endblocked methylhydrogenpolysiloxanes, dimethylhydroxysiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, dimethylhydroxysiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane-methylphenylsil oxane copolymers, and dimethylhydroxysiloxy-endblocked methylhydrogensiloxane-methylphenylsiloxane copolymers. Component (C) is added to the invention in a quantity that yields 0.6 to 20 moles silicon-bonded hydrogen from component (C) per 1 mole total alkenyl group from components (A) and (B). When component (C) is added in a quantity that provides less than 0.6 moles silicon-bonded hydrogen from component (C) per 1 mole total alkenyl group from components (A) and (B), the resulting silicone rubber composition will not undergo an adequate cure and the fixing roll afforded thereby will be unusable in practical applications. When component (C) is added in a quantity that provides more than 20 moles silicon-bonded hydrogen from component (C) per 1 mole total alkenyl group from components (A) and (B), large amounts of hydrogen gas will be produced during curing, which sharply reduces the mechanical strength of the fixing roll product, and the heat resistance of the resulting fixing roll. The platinum catalyst (D) accelerates the cure of the invention composition. No particular restrictions apply to component (D), and it is chloroplatinic acid, alcohol solutions of chloroplatinic acid, chloroplatinic acid-olefin complexes, chloroplatinic acid-vinylsiloxane complexes, platinum supported on silica, platinum supported on active carbon, and platinum black. Component (D) is added to the invention composition in a catalytic quantity to provide 0.1 to 500 weight parts platinum metal from component (D) for each 1 million weight parts of the total of components (A) and (B). The particularly preferred addition of component (D) provides 1 to 50 weight parts platinum metal from component (D) for each 1 million weight parts of the total of components (A) and (B). When component (D) is added at less than 0.1 weight parts platinum metal from component (D) for each 1 million weight parts of the total of components (A) and (B), the resulting silicone rubber composition will have a very slow cure rate. On the other hand, it is economically undesirable to add component (D) at more than 500 weight parts platinum metal from component (D) for each 1 million weight parts of the total of components (A) and (B). The composition of the present invention is prepared by blending components (A) to (D) to homogeneity. The invention composition is characterized by its lack of inorganic filler. The procedure for preparing the invention composition is not specifically restricted. The invention composition can be prepared by mixing components (A) to (D) to homogeneity in a stirring device such as a Ross mixer, planetary mixer, Henschel mixer, butterfly mixer, Hobart mixer, and so forth. Additives that may be used in the composition of this invention on an optional basis are cure inhibitors, such as acetylenic compounds, hydrazines, triazoles, phosphines, and mercaptans; which may be added in order to regulate or adjust the storage stability and the use time of the invention composition; unreactive organopolysiloxane oils, which may be added in order to improve the toner release performance; organopolysiloxanes that contain only a single alkenyl group in each molecule, which may be used to lower the modulus of the silicone rubber; heat stabilizers; flame retardants; and plasticizers. The method for fabricating fixing rolls from our invention composition is not specifically restricted. Fixing rolls can be fabricated by uniformly coating the invention composition over the circumference of a metal shaft and heating the assembly, or by forming a layer of inorganic filler-containing silicone rubber over the circumference of a metal shaft and then coating the invention composition on the surface of this silicone rubber layer and heating. The curing conditions for our composition are also not specifically restricted and are exemplified by heating at 100°C to 200°C for 2 to 30 minutes followed on an optional basis by post-curing the fixing roll for 30 minutes to 4 hours at 150°C to 220°C. No specific restrictions apply to the hardness of the silicone rubber on fixing rolls fabricated as described above, but the A hardness as specified in JIS C 2123 is preferably 10 to 70. Finally, the thickness of the silicone rubber on the fixing roll is not specifically restricted and should be selected as appropriate as a function of the device in which the fixing roll will be used. Because fixing rolls afforded by the cure of the invention composition have excellent toner release properties and excellent mechanical strength, they can be used as fixing rolls in electrophotographic copiers, facsimile machines, and laser printers. Moreover, fixing rolls with excellent toner release properties can be prepared by layering the invention composition over the circumference of a conventional fixing roll and then curing the invention composition. The silicone rubber composition in accordance with the present invention for fixing roll service is explained in greater detail hereinafter through working examples. In the examples, the viscosity was measured at 25°C, and the physical properties of the silicone rubbers were measured by the methods in JIS C 2123. In order to evaluate the toner release performance of the fixing rolls, each fixing roll was installed in an electrophotographic copier and copying (A4 size) was carried out on a continuous basis. The copy count was determined and recorded when a clear copy could no longer be obtained. Example 1. A silicone rubber composition in accordance with the present invention for fixing roll service was prepared by mixing the following to homogeneity: 80 weight parts dimethylvinylsiloxy-endblocked dimethylpolysiloxane with a viscosity of 2,000 mPa.s (cP), 20 weight parts dimethylvinylsiloxy-endblocked dimethylpolysiloxane with a viscosity of 10,000,000 mPa.s (cP), 10 weight parts methylpolysiloxane resin (viscosity = 230 mPa.s [cP]) with the formula [(CH 3 ) 3 SiO 1/2 ] 1.38 [CH 2 =CH(CH 3 ) 2 SiO 1/2 ] 0.44 (SiO 4/2 ) 1.0 , 7 weight parts methylhydrogenpolysiloxane (silicon-bonded hydrogen content = 0.7 weight%) with the formula [(CH 3 ) 3 SiO 1/2 ] 20 [(CH 3 ) 2 SiO 2/2 ] 20 [(CH 3 )HSiO 2/2 ] 45 [CH 3 SiO 3/2 ] 10 , and 0.5 weight parts chloroplatinic acid/1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex (platinum metal content in the complex = 0.4 weight%). This composition was cured by hot-pressing for 5 minutes at 150°C and post-cured for 4 hours in a 200°C forced circulation oven. The tensile strength of the resulting silicone rubber was 25.0 kgf/cm 2 . A fixing roll was also fabricated using this composition. First, a fixing roll primer (DY39-032A/B Primer from Dow Corning Toray Silicone Company, Limited) was coated and dried over the circumference of a cylindrical steel roll core. The roll core was set into a roll-fabrication mold and the composition was filled under pressure into the cavity. After filling, the composition was cured by heating for 10 minutes at 150°C, and the fixing roll was then de-molded. The fixing roll was thereafter held in a 200°C forced circulation oven for 4 hours. The fixing roll labelled (A) in Table 1 was cooled and the toner release capacity tested. The toner release results for this fixing roll are reported in Table 1. Example 2. (Comparative Example) A comparative silicone rubber composition for fixing roll service was prepared by mixing the following to homogeneity: 100 weight parts dimethylvinylsiloxy-endblocked dimethylpolysiloxane with a viscosity of 2,000 mPa.s (cP), 20 weight parts methylpolysiloxane resin (viscosity = 230 mPa.s [cP]) with the formula [(CH 3 ) 3 SiO 1/2 ] 1.38 [CH 2 =CH(CH 3 ) 2 SiO 1/2 ] 0.44 (SiO 4/2 ) 1.0 , 12 weight parts methylhydrogenpolysiloxane (silicon-bonded hydrogen content = 0.7 weight%) with the formula [(CH 3 ) 3 SiO 1/2 ] 20 [(CH 3 ) 2 SiO 2/2 ] 20 [(CH 3 )HSiO 2/2 ] 45 [CH 3 SiO 3/2 ] 10 , and 0.5 weight parts chloroplatinic acid/1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex (platinum metal content in the complex = 0.4 weight%). The silicone rubber afforded by curing this composition under the same conditions as in Example 1 had a tensile strength of 35.0 kgf/cm 2 . A fixing roll (B) was also fabricated under the same conditions as in Example 1, and the toner release results for this fixing roll are reported in Table 1. Example 3. (Comparative Example) A comparative silicon rubber composition for fixing roll service was prepared by mixing the following to homogeneity: 100 weight parts dimethylvinylsiloxy-endblocked dimethylpolysiloxane with a viscosity of 2,000 mPa.s (cP), 20 weight parts methylpolysiloxane resin (viscosity = 230 mPa.s [cP]) with the formula [(CH 3 ) 3 SiO 1/2 ] 1.38 [CH 2 =CH(CH 3 ) 2 SiO 1/2 ] 0.44 (SiO 4/2 ) 1.0 , and 50 weight parts quartz powder. A base compound was prepared by heating this mixture for 2 hours at 170°C in a vacuum and then cooling. Twelve weight parts methylhydrogenpolysiloxane (silicon-bonded hydrogen content = 0.7 weight%) with the formula [(CH 3 ) 3 SiO 1/2 ] 20 [(CH 3 ) 2 SiO 2/2 ] 20 [(CH 3 )HSiO 2/2 ] 45 [CH 3 SiO 3/2 ] 10 and 0.5 weight parts chloroplatinic acid/1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex (platinum metal content in the complex = 0.4 weight%) were subsequently mixed to homogeneity into 150 weight parts of the base compound to yield a comparative silicone rubber composition for fixing roll service. The silicone rubber afforded by curing this composition under the same conditions as in Example 1 had a tensile strength of 50.0 kgf/cm 2 . A comparative fixing roll (C) was also fabricated under the same conditions as in Example 1, and the toner release results for this fixing roll are reported in Table 1. Example 4. (Comparative Example) A comparative silicone rubber composition for fixing roll service was prepared by mixing the following to homogeneity: 100 weight parts trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymer (10,000 mPa.s [cP], 99.0 mole% dimethylsiloxane unit, 1 mole% methylvinylsiloxane unit), 5 weight parts fumed silica with a specific surface area of 200 m 2 /g, 20 weight parts quartz powder, 4 weight parts hexamethyldisilazane (for treatment of the surface of the silica), and 1 weight part water were mixed to homogeneity. A base compound was prepared by heating this mixture for 2 hours at 170°C in a vacuum and then cooling. Three weight parts trimethylsiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymer (silicon-bonded hydrogen content = 0.7 weight%) and 0.5 weight parts chloroplatinic acid/1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex (platinum metal content in the complex = 0.4 weight%) were subsequently mixed to homogeneity into 125 weight parts of the base compound to yield a comparative silicone rubber composition for fixing roll service. The silicone rubber afforded by curing this composition under the same conditions as in Example 1 had a tensile strength of 25.0 kgf/cm 2 . A comparative fixing roll (D) was also fabricated under the same conditions as in Example 1, and the toner release results for this fixing roll are reported in Table 1. Example 5. A primer was painted on the circumference of a fixing roll (D) as prepared in Example 4. The primer was dried and the fixing roll was set into a roll-fabrication mold. A silicone rubber composition for fixing roll service as prepared in Example 1 was filled into the cavity under pressure. After filling, the composition was cured by heating for 10 minutes at 150°C and the fixing roll was then de-molded. Holding this fixing roll for 4 hours in a 200°C forced circulation oven and subsequently cooling yielded a fixing roll (E). The thickness of this silicone rubber layer was 0.5 mm. The toner release results for this fixing roll are reported in Table 1. Fixing Roll No. of Copies A 120,000 B 70,000 C 30,000 D 40,000 E 130,000

Claims: An inorganic filler-free silicone rubber composition for fixing roll service comprising: (A) 100 weight parts of diorganopolysiloxane mixture comprising essentially: (a) 10 to 90 weight% of diorganopolysiloxane that contains at least 2 alkenyl groups in each molecule and that has a viscosity at 25°C of 100 to 100,000 mPa.s (centipoise) and (b) 90 to 10 weight% of diorganopolysiloxane that contains at least 2 alkenyl groups in each molecule and that has a viscosity at 25°C of at least 1,000,000 mPa.s (centipoise), (B) 5 to 100 weight parts organopolysiloxane resin with the general formula (R 3 SiO 1/2 ) x (SiO 4/2 ) 1.0 in which R denotes a monovalent hydrocarbon group, 3-chloropropyl or 3,3,3-trifluoropropyl and x has a value of 0.6 to 4.0, (C) organopolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule, in a quantity that yields 0.6 to 20 moles silicon-bonded hydrogen in component (C) per 1 mole total alkenyl group in components (A) and (B), and (D) platinum catalyst in a catalytic quantity to provide 0.1 to 500 weight parts of platinum metal for each one million weight parts of (A) plus (B). A composition according to Claim 1, where the platinum catalyst is a chloroplatinic acid/1,3-divinyl-1,1,3,3-tetramethyldisiloxane complex. A composition according to Claim 1, where the alkenyl groups of component (A) (a) are vinyl, the non-alkenyl groups of component (A) (a) are selected from methyl and phenyl, the alkenyl groups of component (A) (b) are vinyl, the non-alkenyl groups of component (A) (b) are selected from methyl and phenyl, at least one of the R groups of component (B) is alkenyl, and the viscosity of component (C) is within a range of 10 to 5,000 mPa.s (centipoise) at 25°C. A fixing roll comprising: a metal core coated with the composition of Claim 1 where the composition is cured by heating to 100 to 200 °C for 2 to 30 minutes. The fixing roll of Claim 4 optionally post-cured for 0.5 to 4 hours at 150 to 220°C.

Inventors: KURUSU HIDETOSHI, NAKAMURA AKITO, USHIO YOSHITO, KURUSU, HIDETOSHI,, NAKAMURA, AKITO,, USHIO, YOSHITO,, KURUSU, HIDETOSHI, DOW CORNING TORAY, NAKAMURA, AKITO, DOW CORNING TORAY, USHIO, YOSHITO, DOW CORNING TORAY
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: C08L83
IPC codes: C08L83, G03G15