Platemaking process for a stencil printing sheet

Abstract: Disclosed is a process for platemaking a stencil printing sheet so that there may be no need of preliminarily preparing for manuscripts at a time of platemaking, the consumables, such as a lamp and others, may not be consumed, the stencil sheet can hardly crumple, there may be no sheet loss, and a brilliant printed matter may be obtained. The platemaking process according to the present invention is characterized by perforating a stencil sheet having a solvent-soluble resin layer by using the solvent, and feeding the solvent, at a time of platemaking, to the surface of the solvent-soluble resin layer by a solvent feed means selectively and in a non-contact condition thereof, resulting in the solvent-soluble resin layer brought in contact with the solvent is dissolved and perforated.

Description: The present invention relates to a platemaking process for a stencil printing sheet. Specifically, the present invention relates to a platemaking process for a stencil printing sheet which can perforate the stencil printing sheet without bringing the stencil printing sheet into contact with a platemaking machine. In the prior art, as a platemaking process for a stencil printing sheet, the following methods are known: (1) a process of writing letters or drawing pictures with a steel or ball pen on a stencil printing sheet prepared by impregnating a porous paper with a wax, to remove the wax portion corresponding to the letters or pictures; and (2) a process of melt-perforating the thermoplastic resin film of a heat-sensitive stencil sheet consisting of a thermoplastic resin film and a porous substrate by means of the heat from a flash lamp, infrared lamp or thermal head. However, according to the first method (1), platemaking depends upon manual operation and the resulting platemaking efficiency is thus low. Therefore, large numbers of plates could not be prepared. On the other hand, as the second method (2), there are exemplified processes of superimposing a hand written or preliminarily prepared manuscript on a heat-sensitive stencil sheet and then melt-perforating the thermoplastic resin film of the heat-sensitive stencil sheet by means of the heat generated from, for example, a flash lamp or an infrared lamp, and a process of bringing a thermal head which generates dot-like heat zones, in accordance with electrical signals from letter or picture information, into contact with a heat-sensitive stencil sheet, and melt-perforating the thermoplastic resin film of the heat-sensitive stencil sheet. However, both these processes exhibit disadvantages. The former process has the disadvantages that a new manuscript has to be used after every platemaking step, the operational property is inferior and the power consumption by the lamp is large. The latter process has the disadvantages that since the molten material of the thermoplastic resin film is left in the porous substrate, ink permeability is prevented, resulting in the inability to obtain brilliant printed matter, although replacement of manuscripts and lamps is reduced and fewer consumables are used. Furthermore, in such a process, as it is necessary to let the heat-sensitive stencil sheet sufficiently contact a thermal head under a high pressure at the time of platemaking, it has the disadvantage that a thin heat-sensitive stencil sheet crumples easily, resulting in damage and printing failure. It is thus a main aim of the present invention to provide a platemaking process for a stencil printing sheet which overcomes the above-mentioned problems of the prior art. Namely, to provide a process which eliminates the need for any preliminary preparation of manuscripts; renders consumables, such as a lamp, unnecessary; provides a heat-sensitive stencil sheet which is not easily crumpled; reduces sheet loss; and allows brilliant printed matter to be obtained. DE-C-456,101 discloses a method of perforating a stencil printing sheet composed of a highly porous substance and a coating predetermined portions of which are removed by subsequent treatment with a solvent. A protein, specifically gelatine, is used as the coating of the stencil printing sheet, and an acidic solution is used as the solvent. FR-A-2,206,704 discloses a process for the production of a relief image, which may be used for the production of a printing plate, by the ink jet process in which an electrically controlled Jet of liquid comprising a solution of a substance which is itself capable of altering the solubility properties of a polymer layer with respect to a given solvent, or which contributes to the alteration of the solubility properties of a polymer layer with respect to a given solvent, is sprayed onto a polymer layer with respect to a given solvent so that the solubility properties of the polymer are modified in those areas which are encountered by the jet of solution and this layer is then treated with said given solvent so that a relief image of the original is obtained. The present invention provides a platemaking process for a stencil printing sheet, comprising the steps of: providing a stencil printing sheet comprising a layer of a solvent-soluble resin; and feeding a solvent to a portion of said solvent-soluble resin layer using a solvent feed means so as to perforate said portion of said solvent-soluble resin layer; characterized in that said solvent-soluble resin is selected from polyester, polycarbonate and polyvinyl ether, said solvent comprises at least one organic solvent selected from alcohols, ketones and esters, and said solvent feed means is disposed in non-contacting relation to said portion of said solvent-soluble resin layer. A stencil printing sheet to be used in the platemaking process of the present invention may be composed of only a resin layer, such as a resin film produced by the film formation of a solvent-soluble resin. From the viewpoint of providing a stencil printing sheet with a certain strength, the sheet is preferably composed of a solvent-soluble resin layer and a porous substrate. As a method for forming a resin layer on a porous substrate, a method of laminating a resin film on a porous substrate, a method of coating a resin solution dissolved or dispersed in a solvent onto a substrate and then drying the resulting substrate, and a method of impregnating a substrate with a resin solution dissolved or dispersed in a solvent and then drying the resulting substrate, are exemplified. Once a solvent which dissolves the resin is fed to the surface of the resin layer by a solvent feed means, which will be described later, the resin at the solvent-supplied portion starts dissolving in the solvent and is dissolved in the solvent up to the solubility limit of the resin in the solvent. When the stencil printing sheet includes a porous substrate, the resulting solution which contains dissolved resin permeates into the interior of the porous substrate and the resin layer is perforated. When the stencil printing sheet does not include a porous substrate, the solution which contains dissolved resin is wiped off by a sponge, leaving the perforated resin layer. The perforation of the resin layer can be altered by controlling both the resin solubility of the solvent for the resin layer and the quantity of solvent to be fed. The thickness of the solvent-soluble resin layer is preferably in the range of from 0.1 µm to 100 µm, and more preferably in the range of from 1 µm to 50 µm. When the thickness of the resin layer is less than 0.1 µm the strength of the resin layer is insufficient, and when the thickness of the resin layer exceeds 100 µm a large quantity of solvent may be required to dissolve the resin layer and the perforation achieved by dissolving the resin layer is often insufficient. Furthermore, dyestuffs, pigments, fillers, binders and curing agents can be contained in the resin layer, if necessary. There is no particular limitation to the porous substrate to be adhered to the solvent-soluble resin layer. For example, known porous substrates, such as polyester fiber cloth and Japanese paper, can be used. In the platemaking process of the present invention solvents can be used independently or in admixture, and if necessary, dyestuffs, pigments, fillers, binders, hardeners, antiseptics, wetting agents, surfactants and pH conditioners can be contained in the solvent. In the present invention, the solvent is fed to a predetermined surface portion of the resin layer described above in a non-contact condition by a solvent feed means in correspondence to letter and picture information. There is no particular limitation to the solvent feed means so long as it can feed a solvent without being in contact with the surface of the resin layer. Examples of such an apparatus are a nozzle, a slit, an injector, a porous material and a porous film which are connected to a piezoelectric element, a heating element or a liquid feed pump so as to release the solvent intermittently or continuously in a dot or line pattern according to letter and picture signals. The space between a solvent feed port of the solvent feed means and the stencil printing sheet may be properly determined depending on the feed means and the output of the solvent discharge. According to the present invention, the solvent which perforates the resin layer is fed to a stencil printing sheet in a non-contact condition by a solvent feed means, and therefore there is no generation of wrinkles in the obtained plate at the time of platemaking, thereby avoiding sheet loss. Differently from a conventional heat-sensitive stencil sheet, no molten material is left in the sheet of the present invention at the time of platemaking, and therefore ink permeability is improved and brilliant printed matter can be obtained. A stencil printing sheet perforated by the process of the present invention can be applied to a general stencil printing process to obtain printed matter. For example, printed matter can be obtained by providing an ink on a stencil printing sheet after platemaking, passing the ink through each perforated portion by press rolls, reduced pressure means or squeegee rolls, and transcribing the ink to a printing paper. As a printing ink, an oily ink usually used in stencil printing, a water-based ink, a water-in-oil emulsion ink and an oil-in-water emulsion ink can be used. The present invention will be illustrated in more detail by way of the following non-limiting Examples. Example 1 A stencil printing sheet having a solvent-soluble resin layer was obtained by coating a resin solution consisting of polyester resin (polyethylene terephthalate resin) of 20 weight parts, toluene of 50 weight parts and ethyl acetate of 30 weight parts on a polyester fiber cloth having a sieve opening of 200 mesh with a roll coater, and drying to form a resin layer of 5 µm in thickness on the polyester fiber cloth. A mixture solution of toluene of 50 weight parts, 1,4-dioxane of 30 weight parts and methylethyl ketone of 20 weight parts was ejected in letter shape onto the surface of the resin layer of the stencil printing sheet by using a liquid discharging apparatus equipped with a nozzle of 8 dots/mm connected to a piezoelectric element. The resin layer portion where the mixture solution was ejected was dissolved and perforated. Subsequently, after superimposing a printing paper on the resin layer of the stencil printing sheet, a black water-in-oil emulsion ink was provided on the side of the polyester fiber cloth and squeegeed by a blade, resulting in the printing on the printing paper of letters similar to those of the perforated portions. Example 2 Following the same procedure as described in Example 1, with the exception of using a liquid feed apparatus equipped with a nozzle of 12 dots/mm connected to a piezoelectric element, a stencil printing sheet was prepared for platemaking and then stencil printing was carried out. As a result, the resin layer in contact with the mixture solution was dissolved and perforated. Printing was carried out using the perforated plate, resulting in the printing of letters similar to those of the perforated portions. Example 3 A mixture solution consisting of methylethyl ketone of 50 weight parts, toluene of 30 weight parts and isopropyl alcohol of 20 weight parts was charged into an ejector and then ejected in a pictorial pattern onto the surface of a polycarbonate film of 10 µm in thickness. The film brought into contact with the mixture solution was dissolved in the pictorial pattern and then perforated. Subsequently, after superimposing a printing paper on the perforated film, a black water-in-oil emulsion ink was provided on the other surface of the film and squeegeed by a blade, resulting in the printing thereon of a pictorial pattern similar to that of the perforated portion. Example 4 A porous film of 0.5 mm in thickness and having pores with an average pore size of 50 µm was impregnated with the same mixture solution as used in Example 3, and the resulting impregnated porous film was arranged at a distance of 2 mm from the surface of a polycarbonate film of 10 µm in thickness. The porous film impregnated with the mixture solution was heated to eject the mixture solution from the film onto the surface of the polycarbonate film to perforate the same, resulting in the printing thereon of a pattern similar to that of the perforated portion in the same manner as described in Example 3 to obtain good printed matter. Example 5 A Japanese paper having a basis weight of 10 g/m 2 was superimposed on a polyvinyl ether film of 7 µm in thickness, and the superimposed film was passed through heat rollers at a temperature of 120°C to prepare a stencil printing sheet having a solvent-soluble resin layer. Then, a mixture solution consisting of isopropyl alcohol of 20 weight parts, ethylene glycol of 5 weight parts and water of 75 weight parts was supplied to the ink feed portion of an ink jet printer instead of ink, and then ejected from the nozzle of this jet printer onto the surface of the polyvinyl ether film of the stencil printing sheet in correspondence to letter and picture information generated by a personal computer. The polyvinyl ether film corresponding to the portion in contact with the mixture solution was dissolved and perforated. Subsequently, the sheet thus perforated was mounted on PRINT GOKKO PC-10 (a portable stencil printing device of Riso Kagaku Corporation, Trade mark) to carry out stencil printing, resulting in the printing of brilliant letters and pictures generated by the personal computer. According to the platemaking process of the present invention, a stencil printing sheet can be perforated in a non-contact condition. Therefore, there is no need to prepare manuscripts in advance, and wrinkles are not generated at the time of platemaking, thereby avoiding sheet loss. Since the resin layer of the stencil printing sheet is perforated by dissolution, in contrast to conventional heat-sensitive stencil sheets, melted material is not left in the porous substrate. Therefore, ink permeability is improved and brilliant printed matter can be obtained.

Claims: A platemaking process for a stencil printing sheet, comprising the steps of: providing a stencil printing sheet comprising a layer of a solvent-soluble resin; and feeding a solvent to a portion of said solvent-soluble resin layer using a solvent feed means so as to perforate said portion of said solvent-soluble resin layer; characterized in that said solvent-soluble resin is selected from polyester, polycarbonate and polyvinyl ether, said solvent comprises at least one organic solvent selected from alcohols, ketones and esters, and said solvent feed means is disposed in non-contacting relation to said portion of said solvent-soluble resin layer. A platemaking process for a stencil printing sheet according to claim 1, wherein said stencil printing sheet further comprises a porous substrate disposed on said solvent-soluble resin layer. A platemaking process for a stencil printing sheet according to claim 1 or 2, wherein said solvent-soluble resin is a polyester resin and said solvent is a mixture of toluene, dioxane and methylethyl ketone. A platemaking process for a stencil printing sheet according to claim 1 or 2, wherein said solvent-soluble resin is a polycarbonate resin and said solvent is a mixture of methylethyl ketone, toluene and isopropyl alcohol. A platemaking process for a stencil printing sheet according to claim 1 or 2, wherein said solvent-soluble resin is a polyvinyl ether and said solvent is a mixture of isopropyl alcohol, ethylene glycol and water.

Inventors: WATANABE HIDEO, WATANABE, HIDEO, WATANABE, HIDEO, RISO KAGAKU CORPORATION
Applicants: RISO KAGAKU CORP, RISO KAGAKU CORPORATION
Application year: 1994
Main classification: B41C1
IPC codes: B41C1