Linear telechelic difunctional polymers and process for their preparation.

Abstract: This invention relates to a process for preparation of non-crosslinked linear monofunctional and telechelic difunctional unsaturated polymers wherein the functional groups are reactive terminal groups other than vinyl groups. The average functionality number of the monofunctional unsaturated polymers is at least 0.7, as determined by nuclear magnetic resonance spectroscopy (NMR). The average functionality number of the telechelic difunctional polymers is at least 1.6-1.7, as determined by NMR. Monofunctional olefins and difunctional olefins are reacted with cyclic olefins or unsaturated polymers to prepare difunctional polymers. The process is substantially free of side reactions comprising double bond migration and cyclization. The unsaturated functional polymers can be reacted in condensation, addition and transesterification reactions to prepare polyesters, graft copolymers, polyurethanes, polyureas, polyamides, thermoplastic and thermosetting resins, block copolymers, ion exchange resins, adhesives, films, fibers, foams and flocculants.

Description: Field of the Invention This invention relates to non-crosslinked linear telechelic polymers wherein the chain terminal groups are functional reactive groups, and to a process for preparation of these polymers. The functional reactive groups include ester groups such as acrylate, undecylenate, and methacrylate groups. The process uses olefin metathesis reactions wherein monofunctional acyclic olefins are reacted in a first step reaction in the presence of a catalyst comprising a transition metal compound, an organic tin compound or aluminum halide and an organic Lewis base to prepare a linear mono- or difunctional olefin which, optionally, in a second step reaction is reacted with a cyclic olefin or unsaturated polymer in the presence of the same catalyst to prepare linear telechelic low molecular weight polymers of high functional purity. Undesired side reactions such as double bond migration are minimized by the selected catalyst. Monofunctional linear acyclic olefins of up to 30 carbon atoms or unsaturated linear polymers with reactive endgroups are used to prepare non-crosslinked difunctional linear acyclic olefinic polymers with reactive terminal groups. The preparation of difunctional linear acyclic olefinic polymers with reactive terminal groups from readily available olefinic monofunctional compounds overcomes limitations of previous processes which relied upon the preparation of difunctional olefinic compounds by ring-opening reactions of cyclic olefins with ring-attached reactive groups. The resulting prior art compounds were typically crosslinked compounds. The linear telechelic low molecular weight polymers of high functional purity can be selectively reacted in a third reaction to prepare low and high molecular weight polymers with terminal ester, alcohol, amide, amine, or urea groups. Accordingly, this invention relates to non-crosslinked telechelic difunctional polymers and to their preparation by metathesis reactions of two olefins with each other, or wherein one olefin reactant is a long chain acyclic unsaturated polymer or cyclic olefin, and the other reactant is an acyclic olefin reactant having at least one terminal functional group, including an ester group such as an acrylate group or a methacrylate group or an undecylenate group. Background of the Invention Although the preparation of monomeric unsaturated mono- and difunctional compounds, such as mono- and dicarboxylic acid esters by an addition reaction of an olefin with a mono- or dicarboxylic acid ester is well known, as is taught in U. S. Patent 3,783,136, the preparation of linear alpha, omega difunctional polymers by an olefin metathesis reaction typically has been limited to a few special cases where the reaction is specific for a certain few reactants. The disproportionation of olefins bearing functional groups is an especially economically useful reaction in that compounds bearing functional groups are valuable for use in polymer formation and chemical transformations to yield industrially valuable products. Examples of functional reactive groups previously available are esters, alcohols, amines, halides. Monofunctional and difunctional hydrocarbon polymers of olefinic compounds having at least one internal carbon-to-carbon double bond wherein the functional groups are acrylates, methacrylates, or undecylenates have not been previously available by disproportionation of olefins. Polymers having terminal functional endgroups can be further reacted to form telechelic difunctional polymers. A halogen-terminated polymer can be reacted with an unilaterally metal-terminated chain of another polymer to produce block copolymers. Hydroxy-terminated polymer chains can be reacted with di-and/or tri- polyisocyanates and/or analogous polyfunctional compounds such as acid chlorides of polybasic acids. Ester-terminated polymer chains can be reacted with alcohols or other reactive functional groups for adhesive, coating, fiber, foam and other applications. Monofunctional and telechelic difunctional polymers have been prepared in the past by termination of living polymers with anionic, cationic and metathesis polymerizations of cyclic olefins. Functional groups in monofunctional and difunctional polymers derived from cyclic olefins can be limited to those present in the precursor cyclic olefins. With acyclic olefins, the olefin metathesis reaction can result in cleavage and reforming of carbon-to-carbon double bonds. The resulting redistribution of alkylidene moieties leads to a random product distribution at equilibrium (Kirk-Othmer, Ency. Chem. Tech. , 3rd ed. , 8 (597). Telechelic difunctional hydrocarbon polymers produced via anionic or free-radical polymerizations of acyclic olefins can be mixtures of polymer structures. Typically, the functionalities are less than difunctional, the functionality number (Fn) being less than 2; or greater than difunctional, the functionality number being greater than 2, and the products are mixtures of mono-functional, difunctional, trifunctional, and non-functional species. This invention relates to a process for preparation of non-crosslinked linear telechelic oligomers and polymers of high difunctional purity by olefin metathesis reactions in a two-reaction sequence. The first reaction (A) comprises a metathesis reaction wherein a linear acyclic olefin containing at least one terminal functional group can be reacted in a self-metathesis reaction to prepare a linear functional olefinic product. The second reaction (B) comprises a ring-opening polymerization of a cyclic olefin in the presence of the linear difunctional olefin product of reaction (A). The product of reaction (B) can be further reacted to prepare difunctional alcohols, acids and amines. The linear acyclic functional olefin of reaction (A) can be prepared by reacting a monofunctional linear olefin with a second olefin in a cross metathesis reaction wherein the second olefin is selected from the group consisting of a cyclic olefin of from 4 to 30 carbon atoms and an acyclic unsaturated polymer of number average molecular weight of up to about 1,000,000. The product of the reaction between the monofunctional olefin and a second olefin can be a mixture of species; i.e., monofunctional, difunctional and nonfunctional. The functional olefin which can be the reaction product of a polymer employed as a reactant in reaction (A) of the process of the instant invention can be reacted in reaction (B) in the process reactor in situ without separate purification. The instant invented process accordingly comprises methods for preparing the precursor functional olefins from acyclic and cyclic olefins and unsaturated polymers. Conversion of reactants is at least 10% of theoretical based on olefinic reactants. The invented process utilizes a catalyst composition comprising (a) a transition metal chloride, oxyhalide, oxide or ammonium salt, (b) an organic tin compound or aluminum halide reagent, and (c) an organic Lewis base, wherein undesired side reactions such as double bond migration are minimized. The non-reactivity of certain unsaturated compounds in the olefin metathesis reaction, such as methyl methacrylate, has been documented, K. J. Ivin, Olefin Metathesis , Academic Press, London, N.Y., (1983), 151. Dialkyl maleates or fumarates have been reported to be virtually unreactive in olefin metathesis reactions, Verkuijlen, et al. Recl. Trav, Chim. , Pays-Bas (1977), 96 , M86. However, dimethyl-3-hexene-1,6-dioate, which is costly and is not commercially available in bulk quantities, has been reported to cross-metathesize with 1,5-cyclooctadiene, Reyx, et al. Makromol. Chem. (1982), 183 , 173-183, cyclopentene, Reyx, et al., J. Molecular Catal. , (1986), 36 , 101-105, or norbornene, and has been shown to yield oligomers/polymers which are not high in difunctional purity, Cramail, et al., J. Molecular Catal. , (1991), 65 , 193-203. It has been found that linear functional acyclic olefins comprising monofunctional unsaturated polymers containing groups such as acrylates, methacrylates and undecylenates can be prepared in the presence of the catalyst composition of the instant invented process in metathesis reactions of alkyl acrylates or alkyl methacrylates or alkyl undecylenates with acyclic or cyclic olefins. In the process of the instant invention, in the presence of reactants comprising cyclic olefins and functional olefins such as acrylates or methacrylates or alkyl undecylenates, linear difunctional telechelic unsaturated polymers are prepared with at least one internal carbon-to-carbon double bond and ester groups such as acrylate, methacrylate or undecylenate terminal groups. These linear non-crosslinked difunctional telechelic unsaturated polymers with reactive terminal groups are suitable for further functionalization or incorporation into other polymers for preparation of block copolymers, polyesters, polyamides, polyureas, graft copolymers thermoplastic resins, films, fibers, foams, ion exchange resins, adhesives and flocculants. The linear non-crosslinked difunctional telechelic unsaturated polymers prepared by the process of this invention are true linear compounds of strictly regular structure with exactly defined terminal groups. Such polymers with acrylate, undecylenate, and methacrylate endgroups have not heretofore been produced. Although acyclic unsaturated compounds containing functional groups have been prepared by the olefin metathesis reaction, it has been indicated that when the functional group is too close to the double bond, the metathesis reaction does not work. The non-reactivity of methyl methacrylate has been ascribed to this, K. J. Ivin, Olefin Metathesis , Academic Press, London, N.Y., (1983), 149-151. It has been found that in the process of the instant invention, olefinic compounds such as methyl methacrylate can be reacted to prepare telechelic difunctional oligomers or polymers by olefin metathesis reactions. As is well known, side reactions can occur during olefin metathesis reactions. These side reactions include alkylation, isomerization, cyclization and addition across double bonds present in the molecular structure. It has been found that in cross-metathesis reactions under the conditions of the present invention, these side reactions are minimal. Description of the Prior Art Previous procedures to prepare polymeric hydrocarbons having reactive functional terminal groups frequently have utilized cyclic olefinic compounds in conjunction with a ring opening step. Ofstead, U.S. Patent 3,597,403, teaches a process for ring-opening polymerization of unsaturated alicyclic compounds, preferably unsaturated alicyclic compounds of a single unsaturated alicyclic ring containing at least four carbon atoms and not more than five carbon atoms wherein the carbon-to-carbon double bonds in the ring are not adjacent and are non-conjugated in the presence of a catalyst system comprising an alkylaluminum halide, molecular oxygen, and a compound of tungsten or molybdenum. Streck, et al., U.S. Patent 3,798,175 teaches a process for ring opening polymerization of cyclic olefins and forming terminal carbalkoxy groups by employing a catalyst system consisting essentially of (1) a tungsten or molybdenum compound, (2) an organoaluminum compound, (3) an unsaturated carboxylic acid ester. Streck '175 teaches that an unsaturated carboxylic acid ester containing at least one carbon-carbon double bond varies the molecular weight of the resulting polymer by reaction with the double bond of the ring-opened cyclic olefin to produce side chains. Streck, et al., U. S. Patent 3,857,825, discloses a similar reaction in the presence of a polymeric hydrocarbon having an unsubstituted non-conjugated ethylene double bond for production of polymeric hydrocarbons having reactive silyl end groups by a ring-opening polymerization of a cyclic olefin in the presence of a catalytic amount of a halogenated compound of a metal selected from the group consisting of niobium, tantalum, molybdenum, tungsten and rhenium and a halogen, alkoxy, carboxylate or Lewis acid. Wagener, et al. Makromol. Chem. 191, 365-374 (1990) reported a successful acylic diene metathesis polymerization wherein vinyl terminated oligo(octenylene)s were synthesized using a Lewis acid -free catalyst, W(CH-t-Bu) (N-2,6-C 6 H 3 -i-Pr 2 )(OCMe(CF 3 ) 2 ) 2 , the catalyst taught by Schrock, et al.. J. Am. Chem. Soc . 110, 1423 (1988). Ratio of reactant to catalyst was in a mole ration of 500:1. Yields were reported as essentially quantitative. Preparation of difunctional terminated unsaturated polymers by olefin metathesis from a polyene and a olefin containing a functional group has been reported by Wagener, et al., Macromolecules, 26, 2137-2138 (1993); Wagener, et al, Polymer Preprints , 34, 469-470 (1993), using the catalyst taught by Schrock, et al. J. Am, Chem, Soc. , 110, 1423 (1988) as noted above. The catalyst composition reported as used by Wagener has not been disclosed as commercially available and is difficult and expensive to prepare. Olefin metathesis Lewis acid catalyst systems have been extensively reported in the prior art. Calderon, et al., U.S. Patent 3,597,406, teach the polymerization of hydrocarbon substituted cyclic compounds to prepare polymers with side chains by a ring-opening polymerization of hydrocarbon substituted cyclooctadienes in the presence of a Lewis acid catalyst system comprising (A) at least one organometallic compound wherein the metal is selected from the group consisting of la, IIa, IIb, and IIIa of the Periodic Table of Elements, (B) at least one transition metal salt selected from the group consisting of tungsten and molybdenum halides, and (C) at least one compound of the general formula R-Y-H wherein Y is oxygen, H is hydrogen and R is a radical selected from the group consisting of (1) hydrogen (2) alkyl, (3) aryl, (4) arylalkyl, (5) alkaryl, (6) alkenyl and radicals thereof. Ofstead, U.S. Patent 3,935,179, teaches a ring-opening polymerization of alicyclic hydrocarbons in the presence of a Lewis acid catalyst comprising (A) tungsten or molybdenum halides, (B) alkyl aluminum halides, and (C) an alcohol which may optionally contain a halogen constituent, and (D) an alcohol which has a nitrite substituent for ring opening polymerization of cycloolefins by cleavage of the carbon-to-carbon double bonds. The resulting polymers have repeating units derived from opening of the ring. Similar ring-opening polymerizations of cyclic olefins in presence of a Lewis acid catalyst are also taught in U.S. Patents 3,974,092; 3,974,094; 4,010,224; 4,020,254; and 4,172,932. Olefin metathesis Lewis acid catalyst systems for polymerizing and copolymerizing diolefins have been taught in the prior art wherein the catalyst system is comprised of a Lewis acid and a particular compound which permits carrying out the polymerization and copolymerization reactions starting with diolefins to give products of desired properties. U.S. Patent 4,429,089 teaches a catalytic system for polymerizing and copolymerizing diolefins comprising a Lewis acid, an aluminum compound and a particular compound belonging to the lanthanide series to give products having a high content of 1,4-cis units and high molecular weights from aliphatic conjugated diolefins such as 1,3-butadiene, 1,3-pentadiene, isoprene and their mixtures. U.S. Patent 4,469,809 teaches a two-part-metathesis catalyst system wherein the first part of the catalyst system is comprised of a metathesis catalyst, preferably, WOCl 4 , WCl 6 , and a Lewis base to moderate the polymerization rate of a tungsten/monomer solution, the monomer preferably dicyclopentadiene. The second part of the catalyst system comprises an activator such as tetrabutyltin, triethylaluminum and similar compounds. The activator solution includes an ester, ether, ketone or nitrile which serves to moderate the rate of polymerization. Similar catalyst systems are taught in U.S. Patents 4,520,181; 4,699,963; and 4,918,039 wherein a Lewis base was used to moderate the polymerization reaction of a Lewis acid. U.S. 4,918,039 teaches that in the presence of a transition metal halide and a catalyst activator comprising an alkyl tin reagent, the presence of a Lewis base to stabilize the polymerization reaction can be omitted since an alkyl tin activator is a poorer Lewis acid. U.S. Patent 4,977,226 teaches a ring-opening process for polymerizing a norbornene monomer in the presence of a metathesis catalyst system comprising a tungsten compound such as tungsten hexachloride in the presence of a Lewis base to prevent premature polymerization. K. Ichikawa, et al., J. Org. Chem. , 41,2633-2635 (1976) taught use of a Lewis base catalyst as being effective for reactions of 1-alkenes using a WCl 6 /Bu 4 Sn catalyst with addition of esters, acetonitrile, phenylacetylene, dicyclopentadiene and ethers to improve the selectivity to the metathesis reaction by depressing side reactions. The reactants were 1-pentene, 1-hexene, 1-heptene, 1-octene and 1-decene. The optimum range of the Sn/W mole ratio was from 2:1 to 8:1. The ratio of 1-octene to WCl 6 was 20-400. Products were ethylene and a symmetric internal alkene. The telechelic difunctional polymers prepared by the process of the instant invention are prepared by metathesis reactions which are cross-metathesis reactions between acyclic olefins or cross-metathesis reactions between cyclic and acyclic olefins. Cross-metathesis reactions have been generally classified as being of three categories: (1) exchange of atoms between two olefin compounds to produce two different olefins, (2) ring-opening of a cyclic olefin to produce acyclic polymers, and (3) degradation of olefin polymers to produce oligomers of lower molecular weight. The reactions of the present invention are of the three categories. With the exception of the teachings of Wagener, Makromol, Chem, 191, 365-374 (1990); Macromolecules, 26, 2137-2138 (1993); Polymer Preprints , 34,469-470 (1993), prior investigators have not dealt with the problem of preparing monofunctional or difunctional polymers by a metathesis reaction wherein the functional groups are terminal reactive groups from acyclic monofunctional olefin compounds and which previously had been found non-reactive in a metathesis reaction. As detailed above, Lewis acid catalysts are taught in the preparation of olefinic compounds via a ring opening reaction. The effect of the presence of Lewis base upon the rate of polymerization by a Lewis acid of an olefinic compound has been recognized but there has been no teaching or inference that a metathesis catalyst system comprising a Lewis acid, an activator and a Lewis base can be used to prepare monofunctional or difunctional polymers by cross-metathesis reactions between acyclic olefins and between acyclic olefins and cyclic-olefins. It is therefore an object of this invention to provide a metathesis catalytic process for preparing linear telechelic difunctional polymers having at least one internal carbon-to-carbon double bond from monofunctional olefins. It is further an object of this invention to provide difunctional unsaturated polymers wherein the functional groups are reactive terminal groups and thus are positioned for further functionalization and/or incorporation into other reactive compounds. It is further an object of this invention to prepare difunctional polymers wherein the functional component comprises a terminal functional group, particularly an ester group such as an acrylate group, methacrylate group, or undecylenate group. The reactive terminal groups can be reacted to prepare block copolymers, polyurethanes, polyesters, polyamides, polyureas, and polyacrylics, for such applications as coatings, adhesives, reactants, elastomers, fibres, foams, thermoplastic and thermosetting resins. It is therefore an object of this invention to prepare functional polymers from monofunctional olefins wherein the monofunctional olefin heretofore has been taught as unreactive in an olefin metathesis reaction. Summary of the Invention The invention provides a linear telechelic difunctional non-cross-linked polymer having at least one internal carbon-to-carbon double bend and containing terminal functional reactive groups, said polymer being free of any side chains or pendant groups which would cause cross-linking, said polymer having an average functionality number of 2.0, as determined by nuclear magnetic resonance spectroscopy, said reactive functionality selected from the group of moieties consisting of a nitrile, ester, acid, acyl halide, ketone, aldehyde, borane, amide, acid anhydride, ether, imide, halogen, atom, alkene, alkyne, and substituted aryl group of up to 30 carbon atoms, said aryl group containing at least one reactive substituent of said functional reactive group of moieties, and combinations thereof, wherein said linear telechelic weight of up to 1,000,000. The invention also provides a process for the preparation of a linear telechelic difunctional unsaturated polymer having at least one internal carbon-to-carbon double bond and containing terminal functional reactive groups from olefinic reactants in a process comprising a two reaction sequence of reactions (A) and (B) in which reaction (B) is carried out in the presence of a product of reaction (A), wherein: (I) reaction (A) is an olefin metathesis reaction of acyclic linear olefinic compound reactants comprising at least one of said acyclic olefinic compounds containing up to 30 carbon atoms and containing at least one functional reactive group selected from (i) nitrile, ester, acid, acyl halide, ketone, aldehyde, borane, amide, acid anhydride, ether, imide, halogen atom, alkene and alkyne reactive moieties, (ii) substituted aryl group containing up to an additional 30 carbon atoms, the substituents of said substituted aryl group comprising at least one reactive substituent of said reactive moieties of (i), and (iii) combinations thereof, to prepare a linear functional olefinic product having at least one functional terminal reactive moiety, (II) reaction (B) is a ring-opening polymerization of a cyclic olefin in the presence of the linear functional olefinic product having at least one functional terminal reactive moiety of reaction (A) and wherein said reactions (A) and (B) are metathesis reactions in the presence of a catalyst composition comprising a metathesis catalyst (a) comprising a transition metal compound selected from the group consisting of halides, oxyhalides, oxides and organic ammonium salts; an activator (b) selected from the group consisting of organic tin compounds, alkylaluminum halides, alkoxyalkylaluminum halides and aryloxy-alkylaluminum halides, and an organic Lewis base (c), said metathesis catalyst (a) is present in an amount of from 0.01 to 50 millimoles per mole of said reactants, activator (b) is present in a molar ratio to metathesis catalyst (a) of from 0.001:1 to 200:1, and organic Lewis base (c) is present in a molar ratio to metathesis catalyst (a) of from 0.1:1 to 10,000:1, said reactions (A) and (B) are conducted at a temperature of from 0°C to 200°C and a pressure of from 1 x 10 -6 mm Hg to 30 atmospheres, and wherein the reactants are sufficiently pure that a linear telechelic difunctional non-crosslinked polymer according to the invention is obtained. The process in the presence of a particular catalyst system also comprises the conversion of monofunctional olefins to difunctional olefins or to polymeric functional olefins which are then reacted with cyclic olefins or unsaturated polymers to prepare low molecular weight difunctional polymers. The process is substantially free of side reactions comprising double bond migration and cyclization. The catalyst comprises a composition of a transition metal chloride, oxychloride, oxide, or ammonium salt, an organic tin compound or an aluminum halide, and an organic Lewis base. This invention also relates to the non-crosslinked linear telechelic difunctional unsaturated polymers of high functional purity prepared by the process of this invention. The difunctional telechelic unsaturated functional polymers prepared by the process of this invention wherein the functional groups are terminal reactive groups can be further reacted to prepare block copolymers, graft copolymers, polyurethanes, polyesters, polyamides, and polyureas, for such applications as coatings, adhesives, sealants, elastomers, films, fibers, foams, thermoplastic and thermosetting resins. Detailed Description of the Invention This invention relates to a process for preparation of non-crosslinked linear monofunctional polymers in a first reaction and telechelic polymers of high difunctional purity by olefin metathesis reactions in a second reaction, and to the compositions obtained thereby. The first reaction (A) of the process of this invention comprises an acyclic olefin metathesis reaction wherein linear acyclic olefins containing up to 30 carbon atoms and each containing at least one functional group selected from the group consisting of a nitrile, ester, acyl halide, ketone, aldehyde, borane, amide, acid anhydride, ether, imide, halogen atom, alkene, alkyne, and substituted aryl group of up to an additional 30 carbon atoms, are reacted to prepare linear mono- and difunctional olefinic products. The second reaction (B) comprises a ring-opening polymerization of a cyclic olefin in the presence of the linear mono- and difunctional olefin products of reaction (A). The compositions obtained thereby can be further reacted in condensation polymerization reactions to form macromolecules, transesterification reactions to prepare alcohols, or amination reactions to form amines, which, in turn, can be further reacted to prepare additional compounds suitable for further reactions. Non-crosslinked linear telechelic polymers obtained by the process of this invention are defined as polymers consisting essentially of strictly linear hydrocarbon chains comprising repeating units of 3 to 30 carbon atoms, said hydrocarbon chains without any side chains or pendant groups which would cause cross-linking. The number of repeating units can be from 3 to about 10,000. Methyl acrylate and methyl methacrylate do not react in self-metathesis reactions to prepare dimers of methyl acrylate and methyl methacrylate but alkyl undecylenates do react in a self-metathesis reaction. Methyl acrylate and methyl methacrylate therefore are unsuitable as self-metathesis reactants for reaction (A) but are suitable as reactants with an acyclic hydrocarbon polymer in reaction (A) and as reactants for reaction (B) whereas alkyl undecylenates can react in a self-metathesis reaction in reaction (A) and are suitable reactants for both reaction (A) and reaction (B). In the preparation of a polymer comprising a linear functional unsaturated polymer with terminal reactive moieties comprising acrylate and methacrylate moieties, the instant invented process comprises reaction (B). Accordingly, a linear acyclic functional olefinic composition which can comprise a mixture of monofunctional, difunctional, and nonfunctional compounds is suitable for use in reaction (A) wherein the functional group is either an acrylate group or a methacrylate group or an undecylenate group e.g., methyl acrylate or methyL methacrylate or methyl undecylenate, and the other reactant is an acyclic unsaturated hydrocarbon polymer of number average molecular weight of up to about 1,000,000. The reaction is in the presence of a catalyst composition comprising a transition metal chloride, oxyhalide, oxide or ammonium salt, an organic tin compound or aluminum halide reagent, and an organic Lewis base. In reaction (B), the resulting mixture can be reacted with a cyclic olefin to prepare a difunctional oligomer or polymer without purification of the mixture. Surprisingly and unexpectedly, it has been found that acrylate, or methacrylate, or undecylenate-terminated functional polymers can be prepared in the presence of the above catalyst. The functional acyclic olefin can serve as the Lewis base. The ratios of the three catalyst components are in the range of from about 1.0:0.1:0.1 to about 1.0:20:1000. In reaction (B) the acyclic olefin containing a functional group is also a chain terminating agent. Product molecular weight is controlled by the molar ratio of the cyclic olefin reactant and the functional olefin reactant in reaction (B). The molar ratios of the two reactants are in the range of from about 1:1 to 10,000:1, cyclic olefin to functional acyclic olefin. A low molar ratio yields lower molecular weight products, while a higher ratio yields higher molecular weight products. Accordingly, the process of the instant invention utilizes a metathesis reaction between acyclic olefins which may be the same or different olefins to prepare an acyclic functional olefin, and a metathesis reaction between an acyclic difunctional olefin produced thereby and a cyclic olefin, or unsaturated polymer, the process reactions being in one and two steps, i.e., olefins possessing functional groups are metathesized to yield a mono-or difunctional olefin which is metathesized in a second step with a cyclic olefin or an unsaturated polymer to yield a difunctional polymer product. The olefin possessing a functional group also can be prepared by metathesizing a cyclic olefin of up to 30 carbon atoms or an unsaturated high molecular weight polymer with a monofunctional olefin such as methyl methacrylate or methyl acrylate or methyl undecylenate by a cross-metathesis reaction. The following general reactions wherein X is a functional group other than a vinyl group and R is a portion of a cyclic molecule or a linear carbon chain of a molecule of up to 30 carbon atoms illustrate the process of the invention: wherein n is a number from 1 to about 10,000 and wherein k is a number from 1 to about 200,000 and n is a number from 1 to about 10,000 The process of the instant invention can use a ring-opening metathesis reaction of a cyclic olefin in the presence of a functional olefin or a metathesis reaction of an unsaturated high molecular weight polymer with a functional olefin at a temperature of from about 0°C to about 200°C and a pressure from about 1 x 10 -6 mm Hg to about 30 atmospheres. The two reactions of the invented process to prepare the non-crosslinked linear telechelic oligomers and polymers are by the following reactions: and wherein n is a number from 1 to about 10,000. The process reactions can be performed sequentially, including the preparation of the precursor compounds, with or without isolation and purification of the products of each step. If desired, the same reaction vessel can be employed for both reactions. All reactions should be liquid phase reactions, using neat liquid reactants, solvents, or diluents. The invented process utilizes a catalyst composition comprising (a) a transition metal chloride, oxyhalide, oxide or ammonium salt, (b) an organic tin compound or aluminum halide reagent, and (c) an organic Lewis base wherein undesired side reactions such as double bond migration are minimized. As the transition metal catalyst component, (a), there can be mentioned halides, oxyhalides, oxides and organic ammonium salts, preferably of tungsten, ruthenium, molybdenum, rhenium and tantalum. As preferred examples, there can be mentioned tungsten compounds such as tungsten hexachloride, tungsten oxytetrachloride, tungsten oxide, tridodecylammonium tungstate, methyltricaprylammonium tungstate, tri(tridecyl)ammonium tungstate and trioctylammonium tungstate, molybdenum compounds such as molybdenum pentachloride, molybdenum oxytrichloride, tridecylammonium molybdate, methyltricaprylammonium molybdate, tri(tridecyl)ammonium molybdate and trioctylammonium molydate, rhenium compounds such as rhenium pentachloride, rhenium oxide, rhenium oxide supported on an oxide such as alumina, silica, or silica-alumina, rhenium oxide together with a promoter such as boron oxide on an oxide support, and tantalum compounds such as tantalum pentachloride. Organic tin compounds, alkylaluminum halides, alkoxyalkylaluminum halides and aryloxy-alkylaluminum halides can be used as the activator (b). As preferred examples, there can be mentioned tetrabutyltin, tetramethyltin, tetraethyltin, tetraphenyltin, ethylaluminum dichloride, diethylaluminum monochloride, ethylaluminum sesquichloride, diethylaluminum iodide, ethylaluminum diiodide, propylaluminum dichloride, propylaluminum diiodide, isobutylaluminum dichloride, ethylaluminum dibromide, methylaluminum sesquichloride, methylaluminum sesquibromide, and precondensates of alkylaluminum halides with alcohols. The Lewis base (c) useful in this invention includes linear functional olefins having at least one functional terminal reactive group as a reactant in reaction (A), ethers, esters, nitriles, ketones, amides, amines, alkynes, phosphorus compounds, and alcohols, of up to 30 carbon atoms. Examples are alkyl and aryl acetates, alkyl acrylates, alkyl methacrylates, alkyl undecylenates, acetonitrile, benzonitriles, acrylonitriles, acetylacetone, tetrahydrofuran, pyridine, N,N'-dimethylformamide, thiophene, ethyl ether, propyl ethers, diphenyl ether, triethylamine, phenylacetylene, organic phosphorus compounds of from 1 to 30 carbon atoms and monohydric and dihydric alcohols of from 1 to 30 carbon atoms such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, tert-butyl alcohol, n-pentyl alcohol, isopentyl alcohol, 2-methyl-1-butyl alcohol, 2-methyl-2-butyl alcohol, n-hexyl alcohol, n-heptyl alcohol, n-octyl alcohol, isooctyl alcohol, 2-ethylhexyl alcohol, n-nonyl alcohol, n-decyl alcohol, 1,5-pentanediol, 1,6-hexanediol, allyl alcohol, crotyl alcohol, 3-hexene-1-ol, citronellol, cyclopentanol, cyclohexanol, salicyl alcohol, benzyl alcohol, phenethyl alcohol, cinnamyl alcohol, and the like. The Lewis base (c) is preferably an ester, such as an alkyl acetate, instead of an alcohol. A nitrile such as acetonitrile is preferable to pyridine. The functionalized olefin having at least one functional reactive group contains at least one or more reactive moiety selected from the group consisting of a nitrile, ester, acyl, acid, halide, ketone, aldehyde, borane, acid anhydride, ether, amide, imide, halogen atom, alkene, alkyne, moiety, and substituted aryl moieties of up to 30 carbon atoms containing at least one reactive substituent. Olefinic unsaturates of the above-named Lewis base compounds can suitably serve as the functional olefin reactant. Typically, the preferred functional olefins contain no more than about 30 carbon atoms per molecule. Suitable functional olefins for use in the process of the instant invention include 1,5-hexadiene, 1,9-decadiene, 1,5,9-decatriene, 1,3-butadiene, divinylbenzene, and mixtures thereof, methyl acrylate, methyl methacrylate, methyl or ethyl 2,4-hexadienoate, ethyl cinnamate, 4-penten-1-yl acetate, methyl or ethyl vinylacetate, isobutyl vinylacetate, cyclohexyl vinylacetate, phenyl vinylacetate, methyl or ethyl 4-pentenoate, amyl 4-pentenoate, benzyl 4-pentenoate, propyl 3-decenoate, methyl 10-undecenoate, ethyl 10-undecenoate, methyl oleate, ethyl oleate, butyl oleate, methyl isooleate, ethyl 6-octadecenoate, butyl 6-ocatdecenoate, ethyl elaidate, butyl elaidate, methyl brassidate, methyl linolate, diethyl 2-allylmalonate, allyl acetate, oleyl acetate, 3-hexenyl acetate, oleyl oleate, 2-hexenyl 2-methylpropionate, 3-hexenyl valerate, 2-hexenyl acetate, allyl propionate, oleyl benzoate, 9-octadecenenitrile, 6-octadecenenitrile, 3-butenenitrile, 1,4-dicyano-2-butene, 4-pentenenitrile, octadecenedinitrile, 9,12-octadecadienenitrile, 9-decenenitrile, 10-undecenenitrile, 9-octadecenyl ethyl ether, 9-octadecenyl isopropropyl ether, crotyl isopropyl ether, trimethylallyloxysilane, allylanisole, allyl phenyl ether, 8-heptadecenyl ethyl ketone, 5-heptadecenyl ethyl ketone, 5-hexen-2-one, 6-methyl-5-hepten-2-one, N,N-diethyloleamide N,N-diethylvinylacetamide, alkyl acrylates, alkyl methacrylates, alkyl undecylenates, 3-buten-1-yl acetate, vinyl acetate, and alkyl sorbates. In general, any cyclic olefin of from 4 to about 30 carbon atoms can be polymerized in the presence of a functionalized olefin in the process of this invention. The cyclic olefins include both mono- and polycyclic unsaturated hydrocarbon compounds. Representative examples of polycyclic unsaturated hydrocarbon compounds include norbornene, norbornadiene, 2,2,2-bicyclooctene-2, dicyclopentadiene and the like. The preferred unsaturated alicyclic compounds of this invention are those comprising a single unsaturated alicyclic ring. These alicyclic rings may be mono- or multi-substituted by such groups as alkyl, aryl, arylalkyl, and halogen groups. Representative examples of unsaturated alicyclic compounds containing a single alicyclic ring having at least 4 and not more than 5 carbon atoms in the cyclic ring and containing one double bond in said ring are cyclobutene and cyclopentene. Representative examples of unsaturated alicyclic compounds containing at least seven carbon atoms in the cyclic ring and containing one or more non-conjugated carbon-to-carbon double bonds in the cyclic ring include cyclooctene; 1,4- and 1,5-cyclooctadiene; 1,4,7-cyclononatriene, cyclodecene, cyclododecene, 1,4-, 1,5- and 1,6-cyclodecadiene: 1,4-, 1,5-, 1,6- and 1,7-cyclododecadiene; 1,4,7- and 1,5,9-cyclododecatriene and the like. The most preferred unsaturated alicyclic compounds of this invention are those containing from one to three carbon-to-carbon double bonds in the ring and in which the double bonds are located in relation to each other in a manner that they are not adjacent and are non-conjugated. Representative examples of such preferred materials are cyclobutene, cyclopentene, cyclooctene, cyclododecene, and 1,5-cyclooctadiene, 1,5,9-cyclododecatriene and 1,9,17-cyclotetracosatriene. Representative examples of substituted alicyclic compounds are alkyl-substituted compounds such as 1-methyl-1,5-cyclooctadiene; aryl-substituted compounds such as 3-phenyl-1-cyclooctene: aralkyl-substituted compounds such as 3-benzyl-1-cyclooctene; alkaryl-substituted compounds such as 3-tolyl-1-cyclooctene and halogen-substituted compounds such as a 5-chloro-1-cyclooctene, 1-chloro-1,5-cyclooctadiene; 5-chloro-1-cyclododcene and 5,6-dichloro-1-cyclooctene. Mixtures of the unsaturated alicyclic compounds may be polymerized, including both substituted unsaturated alicyclic compounds and the unsubstituted unsaturated alicyclic compounds. The olefinic polymer useful as a reactant can be high molecular weight polybutadienes, polyisoprene, butyl rubber, and the like, and mixtures thereof. The metathesis catalyst comprising (a), the transition metal compound, is used in an amount of about 0.01 to about 50 millimoles, preferably 0.1 to 10 millimoles, of metal per mole of the olefin reactant. The activator (b) is used at a molar ratio of from 0.001 to 200:1 preferably from about 0.1 to about 10, per mole of the catalyst component (a). The organic Lewis base is used at a molar ratio of from about 0.1:1 to about 10,000:1 moles, preferably from about 1:1 to about 100:1 per mole of the catalyst component (a). Preferably both the metathesis catalyst and the activator are used when dissolved or suspended in the reactants, but the catalyst and activator can be used when suspended or dissolved in a small amount of a solvent, as long as the properties of the product are not substantially degraded. Preferred solvents are benzene, toluene, xylene, pentane, hexane, heptane, cyclohexane, methylcyclohexane, chlorobenzene, dichlorobenzene, and mixtures thereof. Any reagent for deactivating the activator or the metathesis catalyst system, for example, an alkylaluminum chloride, or the catalyst component of the metathesis catalyst system, for example, a tungsten compound catalyst or a molybdenum compound catalyst, can be used as the stopper for the polymerization reaction. As preferred examples, there can be mentioned alcohols such as methanol, ethanol, n-propyl alcohol and n-butanol, amines such as ammonia, organic acids such as acetic acid and propionic acid, oxygen, carbon dioxide, and water. If an appropriate amount of an alcohol is used as the stopper for the reaction, only the activator such as an aluminum compound is deactivated but the catalyst component such as a molybdenum catalyst is left in the liquid product in a reusable state. Of course, a stopper capable of deactivating both of the activator and the catalyst component can be used. In the polymerization reaction, the metathesis catalyst component is used in an amount of 0.01 to 50 millimoles, preferably 0.1 to 10 millimoles, per mole of the monomers as a whole. The activator (is used at a molar ratio of from 0.01 to 200, preferably from 1 to 10, to the catalyst component. It is sufficient if the stopper for the polymerization reaction is used in an amount enough to deactivate the catalyst system. The amount differs according to the kind of the activator or the catalyst component, but the amount can be easily determined by preliminary experiments. For example, where a dialkylaluminum halide is used as the activator and an alcohol is used as the stopper for the viscosity-increasing reaction, it is sufficient if the alcohol is used in an amount of at least 2 moles per mole of the activator. The metathesis polymerization is preferably performed in liquid phase, with catalyst components dissolved or suspended in a solvent or liquid olefin reactant. Reaction temperatures are preferably from about 0°C to 200°C. Pressure can be in the range of from about 1 x 10 -6 mm Hg to about 30 atmospheres, preferably from about 1 x 10 -6 mm Hg to about 1 atmosphere. Any light olefin coproduct (ethylene in the case of polyene reactants with terminal carbon-to-carbon double bonds) should be removed efficiently to drive the reaction to high conversion. In the practice of this invention, the catalyst composition preferably comprises a tungsten metal chloride, a tetraalkyltin reagent and an organic Lewis base selected from the group consisting of the functional olefin reactant, an alkyl acetate, a nitrite, and an ether. Inasmuch as the tungsten catalyst in the presence of an activator such as a tetraalkyltin compound, in the absence of a Lewis base, can catalyze side reactions in a metathesis reaction of an olefin compound, a sequence of mixing the components of the catalyst system is preferred. The tungsten compound is preferably suspended or dissolved in a small amount of a suitable solvent, preferably in an olefin monomer if the tungsten compound is soluble in the monomer. An alcoholic or phenolic compound is also suitable, phenolic compounds being preferred over an alcoholic compound. Suitable phenolic compounds include phenol, alkyl phenols, and halogenated phenols, with tert-butyl phenol, tert-octyl phenol and nonyl phenol most preferred. The preferred molar ratio of the tungsten compound/phenolic compound is from about 1:1 to about 1:3. The tungsten compound/phenolic compound solution can be prepared by adding the phenolic compound to the tungsten compound, stirring the solution and then blowing a stream of a dry inert gas through the solution to remove any hydrogen chloride. The addition of the Lewis base or a chelating agent can be in an amount of from about 0.1 to about 10,000 moles of Lewis base or chelating agent per mole of tungsten compound. Preferred chelants include acetylacetone and alkyl acetoacetates where the alkyl group contains from 1 to 10 carbon atoms. Preferred Lewis bases include nitriles, ethers and esters such as alkyl acetates, benzonitrile, acetonitrile, tetrahydrofuran. In some metathesis reactions, one of the products of the metathesis reaction is an olefin of a lower molecular weight than the starting monomer. In the instant process, it has been found that removal of the olefin of the lower molecular weight is essential to obtain high reaction conversion. This may be accomplished by suitable means such as purging the reaction vessel with inert gas, by applying a low or high vacuum to the system, or by any combination of these methods during the reaction, including the omission of one or more of these procedures, the said steps being in any sequence and capable of being omitted individually. The inert gas can comprise nitrogen, the low vacuum from about 1 mm Hg to about 400 mm Hg, and the high vacuum to about 1 x 10 -6 mm Hg. Graft copolymers can be prepared by reacting linear non-crosslinked mono functional unsaturated polymers with a reactive terminal group wherein the terminal group is an ester moiety with excess vinyl or acrylic monomer to prepare a macromolecule copolymer with a graft-type architecture. Similarly, a block copolymer can be prepared by reacting linear non-crosslinked difunctional unsaturated polymers with reactive terminal groups in a block-type architecture wherein the terminal groups are ester moieties with excess unsaturated monomer such as styrene, isoprene, and butadiene. Example 1 relates to preparation of telechelic difunctional polymers according to the present invention. Examples 2 and 3 relate to the influence of amount of catalyst and reagent purity on the functionality of the resulting polymers. Example 1 The following illustrates the preparation of a telechelic difunctional oligomer with a two-step process from an acyclic olefin and a cyclic olefin. Chlorobenzene (Aldrich Chemical Co., Milwaukee, WI, HPLC grade) was purified by passage through a column of silica gel and 13X sieves, and stored over 4A sieves. Tetramethyltin (Aldrich, 99+%) was dried over 4A sieves. Tungsten hexachloride (Aldrich, 99.9+%) was used as obtained. Methyl undecylenate (methyl 10-undecenoate, 97%) was obtained from Elf Atochem, Philadelphia, PA, and purified by treatment with aqueous NaOH and water followed by drying (with magnesium sulfate) and vacuum distillation; the purified material was stored over 4A sieves. 1,5-Cyclooctadiene (Aldrich, 99.3%) was fractionally distilled using a 20-tray Oldershaw column at a reflux ratio of 15:1. The distilled product was determined to be 99.9% pure by gas chromatography, containing less than 0.01% 4-vinyl-1-cyclohexene. The distilled cyclooctadiene was further purified by passage through a column of basic activated alumina LaRoche Chemicals A-204-4, LaRoche Chemicals, Baton Rouge, La., then stored over 4A sieves under nitrogen. Process Step (1): Tungsten hexachloride (3.2 g, 8.0 mmol) was dissolved in methyl undecylenate (90 mL, 400 mmol) under nitrogen. The solution was syringed into a 500 mL flask with attached reflux condenser which had been purged with nitrogen and preheated to 50 deg C using an oil bath. After 30 minutes, tetramethyltin (2.2mL, 16 mmol) was syringed into the solution and the temperature was raised to 75 deg C. The solution was stirred at 75 deg C for 19 hours under a slow flow of nitrogen, then cooled to room temperature. Dry gaseous ammonia was bubbled through the solution for 30-40 minutes to quench the reaction. Hexane was added to the solution, and precipitated catalyst residue was removed by filtration. The filtrate was then subjected to rotary evaporation at 90-150 deg C using a mechanical vacuum pump to remove hexane and unreacted methyl undecylenate. Upon cooling, an orange crystalline solid was obtained. It was dissolved in methanol and decolorized by treatment with charcoal. The product was then recrystallized several times from aqueous methanol at 0 deg C, affording 22.3 g (60 mmol) of white, crystalline dimethyl 10-eicosene-1,20-dioate (m.p. 44 deg C). Process Step (2): Reaction of dimethyl 10-eicosene-1,20-dioate with excess 1,5-cyclooctadiene to yield ester-terminated, difunctional 1,4-polybutadiene oligomer. Under nitrogen, a 250-mL flask was charged with dimethyl 10-eicosene-1,20-dioate (7.0 g, 19 mmol), chlorobenzene (85 mL), 1,5-cyclooctadiene (56.5 mL, 460 mmol), tungsten hexachloride (37 mg, 0.093 mmol), and tetramethyltin (26 uL, 0.19 mmol). The solution was then heated to 100 deg C and stirred under a nitrogen atmosphere. After 4.5 hours at 100 deg C, additional catalyst solution (37 mg tungsten hexachloride and 26 uL tetramethyltin dissolved in 2 ml chlorobenzene) was syringed into the reaction flask. The solution was then stirred for an additional 17.5 hours (22 hours total) at 100 deg C, then cooled to room temperature. Gas chromatoographic analyses indicated 99.9% conversion of 1,5-cyclooctadiene and 87% conversion of dimethyl 10-eicosene-1,20-dioate. Gaseous ammonia was bubbled through the reaction solution for 10 minutes. The solution was degassed and then filtered to remove precipitated catalyst residue. The filtered solution was then subjected to rotary evaporation at 100-110 deg C using a mechanical vacuum pump to remove volatile liquids, leaving a viscous liquid product. To remove unreacted dimethyl eicosene dioate and very low molecular weight products, the viscous liquid was dissolved in dichloromethane and then precipitated by addition of a large quantity of methanol. The precipitated viscous liquid was collected and washed with additional methanol. The dissolution/precipitation procedure was repeated. The final precipitated (methanol-insoluble) viscous liquid product was clear and pale yellow; yield was 44 g (77% yield based on weight of reactants). No dimethyl 10-eicosene-1,20-dioate was detected by gas chromatography in this product, but it was detected in the methanol washings from the dissolution/precipitation procedure. A quantitative carbon-13 NMR was performed of the product dissolved in chloroform-d with chromium acetylacetonate added as a relaxation agent. The NMR spectrum was consistent with the following ester-terminated, difunctional 1,4-polybutadiene oligomer structure: MeO 2 C(CH 2 ) 7 -(CH 2 CH=CHCH 2 ) n -(CH 2 ) 7 CO 2 Me Strong resonances were observed in the spectrum in the 128-132 ppm range, assigned as internal olefinic carbons of a 1,4-polybutadiene backbone: (-CH 2 -CH=CH-CH 2 -) n . Strong singlet resonances were observed at 32.5 ppm and 27.5 ppm in a 59/41 integrated intensity ratio, assigned as methylene carbons adjacent to trans (59%) and cis (41%) internal backbone carbon-carbon double bonds, respectively. The relative intensity of the combined backbone olefinic carbon resonances was equal (to within 1%) to that of the combined adjacent methylene carbon resonances, consistent with a 1,4-polybutadiene structure. The spectrum indicated that the product possessed ester endgroups of the structure -(CH 2 ) 7 CO 2 Me: weak singlet resonances of equal intensity were observed at 173.5 ppm (carbonyl carbon of the ester), 51.1 ppm (methoxy carbon of ester), 33.8 ppm (methylene carbon alpha to carbonyl), and 24.8 ppm (methylene carbon beta to carbonyl); a broad resonance was observed at 29.1 ppm with 5-fold greater intensity (five methylene carbons). Although the signal-to-noise ratio of the spectrum was very high (about 100:1 for the carbonyl carbon endgroup signal), no other resonances were detected other than sidebands of major peaks. No other endgroup types were detected, such as saturated methyl or ethyl endgroups (10-24 ppm) or vinyl endgroups (110-120 ppm, 132-142 ppm). Neither were vinyl endgroups detected in a proton NMR spectrum of the product. The NMR data thus indicate the acyclic oligomer product to be purely difunctional with respect to ester endgroups (Fn = 2.0). Number-average molecular weight (M n ) of the product was computed at 4,030 g/mole using relative integrated intensities from the carbon-13 NMR spectrum (carbonyl carbon = 6.87; methoxy carbon = 6.70; combined backbone olefinic carbon = 466) and the relation, M n = n(54.1) +314.5, which is based upon the product structure shown above. Example 2 This example illustrates the effect of the amount of catalyst charge upon difunctional oligomer product purity. A procedure was followed similar to that of Example 1, except that a greater amount of catalyst (relative to monomer amounts) was employed in the second process step (reaction of dimethyl 10-eicosene-1,20-dioate with 1,5-cyclooctadiene). The molar 1,5-cyclooctadiene/WCl 6 /SnMe 4 ratio employed in this example was 500/1/2 (vs. 2500/1/2 in Example 1). The reaction was terminated after 2.5 hours at 100 deg C, at which point 1,5-cyclooctadfiene conversion was 99.9% and dimethyl 10-eicosene-1,20-dioate conversion was 94% as determined by gas chromatography. The viscous liquid oligomer product was isolated by the procedure of Example 1, and analyzed by carbon-13 NMR. The NMR spectrum was similar to that of Example 1 with the addition of two very weak singlet resonances of equal intensity at 138.0 ppm and 114.3 ppm, assigned as the =CHR and =CH 2 carbons, respectively, of a vinyl endgroup: RHC=CH 2 . The integrated intensity of each vinyl endgroup carbon resonance was 1-2% of the intensity of the ester endgroup carbonyl carbon resonance. This indicates that 1-2% of the oligomer endgroups of this product were non-functional (meaning non-ester), and thus the product was not as difunctionally pure as that of Example 1. Number-average molecular weight of this product was determined to be 3,680 g/mole by vapor pressure osmometry (VPO), and was calculated by carbon-13 NMR to be 3,860 g/mole. Example 3 This example illustrates the effect of reactant purity, in particular the purity of the cyclic olefin monomer, upon difunctional oligomer product purity. A procedure was followed similar to that of Example 1, except that the 1,5-cyclooctadiene employed in the second process step was less pure. In this example, 1,5-cyclooctadiene (Aldrich, 99.3% pure by gas chromatographic analysis) was used without further purification by distillation. GC analysis indicated the presence of several organic impurities, including 0.2% 4-vinyl-1-cyclohexene. In this example, the amount of catalyst employed in the second process step was the same as in Example 2: 500/1/2 1,5-cyclooctadiene/WCl 6 /SnMe 4 . The reaction was terminated after 4 hours at 100 deg C, at which point 1,5-cyclooctadiene conversion was 99.6% and dimethyl 10-eicosene-1,20-dioate conversion was 85% as determined by gas chromatography. The viscous liquid oligomer product was isolated by the procedure of Example 1, and analyzed by carbon-13 NMR. The NMR spectrum was similar to that of Example 2, except that the two vinyl endgroup carbon resonances (138.0 ppm and 114.3 ppm) were more intense, each with an integrated intensity of 7-8% of the intensity of the ester endgroup carbonyl carbon resonance. This indicates that 7-8% of the oligomer endgroups of this product were vinyl and non-functional (meaning non-ester), and thus the product was less difunctionally pure than that of Example 2.

Claims: A linear telechelic difunctional non-crosslinked polymer having at least one internal carbon-to-carbon double bond and containing terminal functional reactive groups, said polymer being free of any side chains or pendant groups which would cause cross-linking, said polymer having an average functionality number of 2.0, as determined by nuclear magnetic resonance spectroscopy, said reactive functionality selected from the group of moieties consisting of a nitrile, ester, acid, acyl halide, ketone, aldehyde, borane, amide, acid anhydride, ether, imide, halogen atom, alkene, alkyne, and substituted aryl group of up to 30 carbon atoms, said aryl group containing at least one reactive substituent of said functional reactive group of moieties, and combinations thereof, wherein said linear telechelic difunctional unsaturated polymer has a number average molecular weight of up to 1,000,000. The polymer of Claim 1 wherein said reactive functionality is an ester moiety, wherein said moiety is selected from the group consisting of an acrylate moiety, a methacrylate moiety an allyl acetate moiety, and allyl propionate moiety, a vinyl acetate moiety and an undecylenate moiety. A process for the preparation of the polymer of Claim 1 from olefinic reactants said process comprising a two reaction sequence of reactions (A) and (B) in which reaction (B) is carried out in the presence of a product of reaction (A), wherein: (I) reaction (A) is an olefin metathesis reaction of acyclic linear olefinic compound reactants comprising at least one of said acyclic olefinic compounds containing up to 30 carbon atoms and containing at least one functional reactive group selected from (i) nitrile, ester, acid, acyl halide, ketone, aldehyde, borane, amide, acid anhydride, ether, imide, halogen atom, alkene and alkyne reactive moieties, (ii) substituted aryl group containing up to an additional 30 carbon atoms, the substituents of said substituted aryl group comprising at least one reactive substituent of said reactive moieties of (i), and (iii) combinations thereof, to prepare a linear functional olefinic product having at least one functional terminal reactive moiety, (II) reaction (B) is a ring-opening polymerization of a cyclic olefin in the presence of the linear functional olefinic product having at least one functional terminal reactive moiety of reaction (A) and wherein said reactions (A) and (B) are metathesis reactions in the presence of a catalyst composition comprising a metathesis catalyst (a) comprising a transition metal compound selected from the group consisting of halides, oxyhalides, oxides and organic ammonium salts; an activator (b) selected from the group consisting of organic tin compounds, alkylaluminum halides, alkoxyalkylaluminum halides and aryloxy-alkylaluminum halides, and an organic Lewis base (c), said metathesis catalyst (a) is present in an amount of from 0.01 to 50 millimoles per mole of said reactants, activator (b) is present in a molar ratio to metathesis catalyst (a) of from 0.001:1 to 200:1, and organic Lewis base (c) is present in a molar ratio to metathesis catalyst (a) of from 0.1:1 to 10,000:1, said reactions (A) and (B) are conducted at a temperature of from 0°C to 200°C and a pressure of from 1 x 10 -6 mm Hg to 30 atmospheres, and wherein the reactants are sufficiently pure that a linear telechelic difunctional non-crosslinked polymer according to claim 1 is obtained. The process of Claim 3 wherein the metal of the transition metal compound is selected from tungsten, molybdenum, rhenium, tantalum and ruthenium. The process of Claim 3 or 4 wherein the Lewis base (c) is selected from the group consisting of acyclic linear olefinic compound reactants of reactions (A), esters, ethers, nitriles of up to 30 carbon atoms comprising alkyl and aryl acetates, alkyl acrylates, alkyl methacrylates, alkyl undecylenates, ethyl ether, propyl ethers, diphenyl ether, acetonitrile, benzonitrile, and compounds comprising acetylacetone, tetrahyrofuran, pyridine, N,N'- dimethylformamide, thiophene, triethylamine, phenyl acetylene, organic phosphorus compounds of from 1 to 30 carbon atoms, or monohydric or dihydric alcohols of from 1 to 30 carbon atoms. The process of Claim 3 wherein said process comprises reaction (A) between two acyclic linear olefinic compound reactants, one linear olefinic compound reactant comprising an unsaturated polymer of number average molecular weight of up to 1,000,000 selected from the group consisting of low molecular weight oligomers and high molecular weight polymers of polybutadiene, polyisoprene, butyl rubber, and mixtures thereof, and a second linear olefinic compound reactant containing up to 30 carbon atoms and containing at least one functional reactive group selected from said reactive moieties. The process of Claim 3 wherein said linear functional olefin is selected from the group consisting of an alkyl undecylenate of up to 30 carbon atoms, allyl acetate, allyl propionate, and vinyl acetate and the cyclic olefin comprises 1,5-cyclooctadiene. The process of Claim 3 wherein said cyclic olefin is selected from the group consisting of cycloheptene; 1,3-cyclooctadiene; 1,4-cyclooctadiene: 1,5-cyclooctadiene, norbornene, norbornadiene, 2,2,2-bicyclooctene-2; cyclooctene; cyclodecene; methyl cyclooctadienes; dimethyl cyclooctadienes; methyl cyclooctenes: dimethyl cyclooctenes; 1,4,7-cyclononatriene; 1,4-cyclodecadiene; 1,5-cyclododecadiene; 1,6-cyclodecadiene; 1,7-cyclodecadiene; 1,4,7-cyclododecatriene; 1,5,9-cyclododecatriene; trimethyl 1,5,9-cyclododecatriene; cyclopentene; cyclododecene; cyclobutene; 1,9,17-cyclotetrasatriene; 1-methyl-1,5-cyclooctadiene; 3-phenyl-1-cyclooctene; 3-benzyl-1-cyclooctene; 3-tolyl-1-cyclooctene; 5-chloro-1-cyclooctene; 1-chloro-1,5-cyclooctadiene; 5-chloro-1-cyclododecene; 5,5-dichloro-1-cyclooctene; and mixtures thereof. The process of any of Claims 3-8 wherein said olefin metathesis reactions are driven to conversion by removal of low molecular weight co-product olefins produced by said olefin metathesis reactions of said acyclic olefins from said olefin metathesis reaction, wherein said low molecular weight co-product olefins from said polymers are removed from said process by a combination of steps comprising a purge of the olefin metathesis reaction with an inert gas, application of a low vacuum in the range of from 1 mm Hg to 400 mm Hg during said reaction, and an application of a high vacuum to about 1 x 10 -6 mm Hg, said steps being in any sequence and capable of being omitted individually, said polymers containing less than 100 parts per million of tungsten, said polymers being free of a predominant color. The process of any of Claims 3-9 wherein catalyst (a) is tungsten hexachloride. The process of any of Claims 3-10 wherein activator (b) is tetramethyltin. The process of any of Claims 3-11 wherein Lewis base (c) is an ester. The process of any of Claims 3-12 wherein catalyst (a) is present in an amount of 0.1 to 10 millimoles of metal per mole of olefin reactant, activator (b) is present at a molar ratio of 0.1 to 10 per mole of catalyst (a), and Lewis base (c) is present at a molar ratio of 1 to 100 per mole of catalyst (a).

Inventors: BAGHERI VAHID, BEHRENDS RAYMOND T, BOUSLOG WILLIAM G, COHEN STEVEN A, MORELAND ROBERT B, NELSON JAMES P, NUBEL PHILIP O, YOKELSON HOWARD B, BAGHERI, VAHID, BEHRENDS, RAYMOND T., BOUSLOG, WILLIAM G., COHEN, STEVEN A., MORELAND, ROBERT B., NELSON, JAMES P., NUBEL, PHILIP O., YOKELSON, HOWARD B.
Applicants: CALIFORNIA INST OF TECHN, CALIFORNIA INSTITUTE OF TECHNOLOGY
Application year: 1994
Main classification: C08G61
IPC codes: C08G61, C08G63, C08G18, C08C19