PROCESS FOR PREPARING A POLYURETHANE FOAM IN THE PRESENCE OF A HYDROCARBON BLOWING AGENT

Abstract: This disclosure relates to polyisocyanate-based foams, particularly to polyurethane or polyurethane-polyisocyanurate foam prepared in the presence of a certain blowing agent. The blowing agent, based on total amounts of a) and b), consists of: (a) from 5 to 80 mole percent of a C5-6 alicyclic alkane or mixtures of such; and (b) from 95 to 20 mole percent of a mixture of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80.

Description: PROCESS FOR PREPARING A POLYURETHANE FOAM IN THE PRESENCE OF A HYDROCARBON BLOWING AGENT This invention relates to a hydrocarbon mixture which consists of an alicyclic alkane with an aliphatic alkane, an isocyanate-reactive composition comprising the hydrocarbon mixture, and a process for preparing a polyurethane or polyurethane- polyisocyanurate foam prepared in the presence of the hydrocarbon mixture. It is well known to prepare cellular polyurethanes by reacting a polyisocyanate with an active hydrogen-containing material in the presence of a halocarbon blowing agent. In preparing flexible polyurethane foam, for example, halocarbons are often used to supplement water in generating a gas for blowing. However, the use of halocarbon blowing agents is particularly significant in making rigid foam. In rigid foam, the halocarbon blowing agent additionally provides thermal insulating properties and usually constitute the major proportion of the blowing agent when preparing a rigid foam. Of the halocarbons, trichlorofluoromethane (R-1 1 ), dichlorodifluoromethane (R-12) and trichlorotrifluoroethane (R-1 13) are of the most commercial importance; due to their advantageous thermal insulating properties, boiling points and stability. A disadvantage of these substances is that they are highly suspected of contributing to the depletion of atmospheric ozone. Accordingly, it would be highly desirable to replace the halocarbons with other blowing agents which are not believed to cause such environmental damage. Other blowing agents contemplated include hydrocarbons. The general use of hydrocarbons including aliphatic and alicyclic alkanes as blowing agents when preparing polyurethane foam is known. U.S. Patent 5,182,309 and European Patent Application EP-A-472,080 disclose the use of aliphatic alkanes including pentane as polyurethane blowing agent. U.S. Patent 3,586,651 discloses the use of a cyclopentane/acetone mixture as blowing agent when preparing rigid, closed celled, polyurethane foam. Similarly in U.S. Patents 5,096,933 and 5,034,424 the use of cyclopentane and/or cyclohexane in combination with other blowing agents to prepare polyurethane foam is disclosed. Combinations of halocarbons and hydrocarbons as polyurethane blowing agent are also disclosed in U.S. Patents 5,132,332 and 5,001 ,164. While the use of hydrocarbons as blowing agent frequently provides vis-a-vis ozone depletion a more environmentally acceptable system, they do not permit the preparation of foam with long term commercially attractive physical properties including thermal insulation and dimensional stability characteristics. Accordingly, it would be desirable to develop a process for the preparation of polyurethane foam in the presence of a halogen-free blowing agent and where the resulting foam exhibits long-term thermal insulation and dimensional stability characteristics better suited to present commercial and environmental demands. In one aspect, this invention relates to a hydrocarbon mixture, suitable for use as a physical blowing agent when preparing a polyurethane or polyisocyanurate foam, which based on total amounts of a) and b), consists of: a) from 5 to 80 mole percent of a C 5 -6 alicyclic alkane or mixtures of such; and b) from 95 to 20 mole percent of a mixture of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80. In a second aspect, this invention relates to an isocyanate-reactive composition for use in the preparation of polyurethane or polyisocyanurate foam which comprises a polyahl, water, and a hydrocarbon mixture characterized in that: a) the polyahl contains an aromatic-initiated polyether polyol present in an amount from 30 to 90 parts per 100 parts by total weight of polyahl; b) the water is present in an amount from 1.5 to 10 parts per 100 parts by total weight of polyahl ; and c) the hydrocarbon mixture present in an amount of from 1 to 25 parts per 100 parts of polyahl consists, based on total amounts of d ) and c2), of: d ) from 5 to 80 mole percent of a C5-6 alicyclic alkane or mixtures of such; and c2) from 95 to 20 mole percent of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80. | n a third aspect, this invention relates to a process for preparing a polyurethane or polyisocyanurate foam by reacting an organic polyisocyanate with a polyahl containing isocyanate-reactive hydrogens in the presence of a physical blowing agent characterized in that: a) the blowing agent present in an amount of from 1 to 25 parts per 100 parts by weight of polyahl is a hydrocarbon mixture consisting, based on total amounts of i) and ii), of i) from 5 to 80 mole percent of a C5-6 alicyclic alkane or mixtures of such; and ii) from 95 to 20 mole percent of a mixture of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80; and b) the polyisocyanate, having an average of from 2 to 3.5 isocyanate groups/molecule, is present in an amount to provide from 0.5 to 5 isocyanate groups per isocyanate reactive hydrogen present. Figure 1 illustrates the change with time of the thermal conductivity of polyurethane foam prepared in the presence of , with reference to the examples later described, different hydrocarbon blowing agent mixtures. Foam 10 is illustrative of the present invention; Foams 1 , 6 and 21 are comparative. In this invention, a hydrocarbon mixture is used as the physical blowing agent to prepare a polyurethane or polyisocyanurate foam. The blowing agent consists of, as first component, an alicyclic C5- 6 alkane or mixtures of such; and as a second component, a mixture of isopentane with n-pentane in a mole ratio of from 80:20 to 20:80. The blowing agent contains, based on total amount of first and second component present, the first component in from 5 to 80 mole percent; and the second component in from 95 to 20 mole percent. When it is intended to use the resulting foam in appliance applications, for reasons of long-term thermal insulation performance and dimensional stability, it is found advantageous to have the isopentane and n-pentane isomers present in a mole ratio of from 80:20 to 60:40. When it is intended to use the resulting foam in construction applications, having different performance requirements to an appliance application, it is found advantageous to have the isopentane and n-pentane isomers present in a mole ratio of from 40:60 to 20:80. As first component, suitable C5- 6 alicyclic alkanes include cyclopentane, methylcyclopentane, cyclohexane, or mixtures of two or more of these. Preferred is cyclopentane, and especially cyclohexane due to its lower gas thermal conductivity. When the first component is cyclopentane advantageously, for reasons or boiling point and partial pressure, it is present in from 5 to 80, preferably in from 15 to 60, and more preferably in from 20 to 45 mole percent. Conversely, the second component advantageously is present in from 95 to 20, preferably from 85 to 40, and more preferably from 80 to 55 mole percent. When the first component is methylcyclopentane or cyclohexane, or mixtures containing a majority of either of these alkanes, advantageously it is present in from 5 to 40, preferably in from 10 to 35, and more preferably in from 20 to 35 mole percent. Conversely, the second component advantageously is present in from 95 to 60, preferably from 90 to 65, and more preferably from 80 to 65 mole percent. The hydrocarbon mixture of this invention is useful in preparing cellular polymers such as, for example, polyisocyanate-based foam including microcellular elastomers and especially rigid, polyurethane and polyisocyanurate foams. In preparing such foam, an organic polyisocyanate is reacted with a polyahl in the presence of the hydrocarbon mixture, and optionally water. It is often convenient to preblend the mixture with the polyahl before contacting same with the polyisocyanate. It is, however, possible to simultaneously blend the polyisocyanate, polyahl and hydrocarbon mixture in the production of foam. In making cellular polymers, it is advantageous to employ sufficient blowing agent to provide a polymer having an overall density from 10 to 700, preferably 15 to 300, and more preferably 20 to 100 kg/nrι3. To provide for such density, typically the hydrocarbon mixture is present in an amount of from 1 to 25, preferably from 3 to 22, and more preferably from 10 to 20 parts per 100 parts by weight of polyahl. Polyahls which are useful in the preparation of the polyisocyanate-based cellular polymers include those materials having two or more groups containing an active hydrogen atom capable of undergoing reaction with an isocyanate. Preferred among such compounds are materials having at least two hydroxyl, primary or secondary amine, carboxylic acid, or thiol groups per molecule. Polyols, that is, compounds having at least two hydroxyl groups per molecule, are especially preferred due to their desirable reactivity with polyisocyanates. 5 Typically polyahls suitable for preparing rigid polyurethanes include those having an equivalent weight of 50 to 700, preferably 70 to 300 and more preferably 70 to 150. Such polyahls also advantageously have a functionality of at least 2, preferably 3, and up to 6, preferably up to 8, active hydrogen atoms per molecule. Representative of polyahls include polyether polyols, polyester polyols, polyhydroxy-terminated acetal resins, hydroxyl- 10 -terminated amines and polyamines. Examples of these and other suitable isocyanate-reactive materials are described more fully in U.S. Patent 4,394,491 , particularly in columns 3 to 5. Preferred for prepari ng rigid foams, on the basis of performance, availability and cost, is a polyol prepared by adding an alkylene oxide to an initiator having from 2 to 8, preferably 3 to 8 active hydrogen atoms. Exemplary such polyols include those commercially available under the 15 trademark designation VORANOL including VORANOL 202, VORANOL 360, VORANOL 370, VORANOL 446, VORANOL 490, VORANOL 575, VORANOL 800, all sold by The Dow Chemical Company, and PLU RACOL 824, sold by BASF Wyandotte. Other highly preferred polyols include alkylene oxide derivatives of Mannich condensates, as disclosed, for example, in U.S. Patents 3,297,597; 4,137,265 and 4,383,102; and aminoalkylpiperazine-initiated polyethers as 20 described in U.S. Patent 4,704,410 and 4,704,41 1. In a preferred embodiment of this invention, the polyahl is a composition comprising an aromatic-initiated polyether polyol in from 30 to 90 parts per 100 parts by total weight of the polyahl composition. Further to the aromatic-initiated polyether polyol, the composition may also comprise an amine-initiated polyether polyol in from 5 to 35 parts per 25 100 parts by total weight of the composition; or alternatively an aromatic polyester polyol, liquid at room temperature, in from 5 to 35 parts per 100 parts by total weight of the composition. In a highly preferred embodiment of this invention, the polyahl composition contains the aromatic-initiated polyether polyol in from 30 to 90 parts; the amine-initiated polyether polyol in from 5 to 35 parts; and the aromatic polyester polyol in from 5 to 35 parts 30 per 100 parts by total weight of the composition. Advantageously, the aromatic-initiated polyether polyol is an alkylene oxide adduct of a phenol/formaldehyde resin, frequently called a "novolac" polyol, such as disclosed in U.S. Patents 3,470, 1 18 and 4,046,721 , or an alkylene oxide adduct of phenol/formaldehyde/alkanolamine resin, frequently called a "Mannich" polyol such as disclosed in U.S. Patents 4,883,826; 4,939,182; and 5, 120,815. 35 Polyisocyanates useful in making polyurethanes include aliphatic and cycloaliphatic and preferably aromatic polyisocyanates or combinations thereof, advantageously having an average of from 2 to 3.5, and preferably from 2.4 to 3.2 isocyanate groups per molecule. Representative of suitable polyisocyanates include m- or p-phenylene diisocyanate, 2,4- or 2,6-toluene diisocyanate, hexamethylene-1 ,6-diisocyanate, tetramethylene-1,4-diisocyanate, cyclohexane-1 ,4-diisocyanate, hexahydrotoluene diisocyanate, naphthylene-1,5-di isocyanate, 1 -methyl phenyl-2,4-phenyldi isocyanate, diphenylmethane-4,4'-di isocyanate, diphenylmethane-2,4'-diisocyanate, 4,4'-biphenylenediisocyanate, 3,3'-dimethoxy-4,4'-biphenylenediisocyanate and 3,3'-dimethyldiphenyl-propane-4,4'-diisocyanate; tri isocyanates such astoluene-2,4,6- -tri isocyanate and polyisocyanates such as 4,4'-dimethyldiphenylmethane-2, 2', 5', 5'- -tetraisocyanate and the diverse polymethylene polyphenyl polyisocyanates. A crude polyisocyanate may also be used in the practice of this invention, such as the crude toluene diisocyanate obtained by the phosgenation of a mixture of toluene diamines or the crude diphenylmethane diisocyanate obtained by the phosgenation of crude diphenylmethanediamine. Especially preferred, due to their ability to crosslink the polyurethane, are methylene-bridged polyphenylpolyisocyanates. The ratio of equivalents of isocyanates to equivalents of active hydrogen atoms is advantageously from 0.5 to 5, preferably 0.9 to 2, more preferably 1.0 to 1.5. When the same ratio is expressed as a multiple of 100 this is then the isocyanate index. In addition to the foregoing critical components, it is often desirable to employ certain other ingredients in preparing cellular polymers. Among these additional ingredients are water, catalysts, surfactants, flame retardants, preservatives, colorants, antioxidants, reinforcing agents and fillers. Advantageously, water is present to supplement the blowing capacity al ready provided by the hydrocarbon mixture. Water reacts with isocyanate leading the production of carbon dioxide. When present, the water is preferably used in amounts of from 1 to 10, preferably from 1.5 to 8, and more preferably from 2 to 6, and yet more preferably in from 2.5 to 5 parts per 100 parts by total weight of the polyahl. Other auxiliaries useful when producing polyurethanes include surfactants, pigments, colorants, fullers, fibers, antioxidants, catalysts, flame retardants and stabilizers. In making polyurethane foam, it is generally highly preferred to employ a minor amount of a surfactant to stabilize the foaming reaction mixture until it cures. Such surfactants advantageously comprise a liquid or solid organosilicone surfactant. Other, less preferred surfactants include polyethylene glycol ethers of long-chain alcohols, tertiary amine or alkanolamine salts of long-chain alkyl acid sulfate esters, alkyl sulfonic esters and alkyl arylsulfonic acids. Such surfactants are employed in amounts sufficient to stabilize the foaming reaction mixture against collapse and the formation of large, uneven cells. Typically, 0.2 to 5 parts of the surfactant per 100 parts by weight polyahl are sufficient for this purpose. One or more catalysts for the reaction of the polyol (and water, if present) with the polyisocyanate are advantageously used. Any suitable urethane catalyst may be used, including tertiary amine compounds and organometallic compounds. Exemplary tertiary amine compounds include tπethylenediamine, N-methylmorpho ne, N,N-dιmethylcyclohexylamιne, pentamethyldiethylenetπamme, tetramethylethylenediamme, 1 -methyl-4-dιmethylamιnoethylpιperazιne, 3-methoxy-N-dιmethylpropylamιne, N-ethylmorpho ne, diethylethanolamine, N-cocomorpho ne, N,N-dιmethyl-N',N'-dιmethyl isopropylpropylenediamme, N,N-dιethyl-3-dιethylamιnopropylamιne and dimethylbenzylamme Exemplary organometal c catalysts include organomercury, organolead, organoferπc and organotin catalysts, with organotin catalysts being preferred among these Suitable tin catalysts include stannous chloride, tin salts of carboxylic acids such as dibutyltin dι-2-ethyl hexanoate, as well as other organometalhc compounds such as are disclosed in U S Patent 2,846,408. A catalyst for the trimerization of polyisocyanates, resulting in a polyisocyanurate, such as an alkali metal alkoxide may also optionally be employed herein Such catalysts are used in an amount which measurably increases the rate of polyurethane or polyisocyanurate formation Typical amounts are 0 001 to 1 parts of catalyst per 100 parts by weight of polyahl In making a polyurethane foam, the polyol(s), polyisocyanate and other components are contacted, thoroughly mixed and permitted to expand and cure into a cellular polymer The particular mixing apparatus is not critical, and various types of mixing head and spray apparatus are conveniently used. It is often convenient, but not necessary, to preblend certain of the raw materials prior to reacting the polyisocyanate and active hydrogen- -containing components For example, it is often useful to blend the polyol(s), blowing agent, surfactants, catalysts and other components except for polyisocyanates, and then contact this mixture with the polyisocyanate Alternatively, all components can be introduced individually to the mixing zone where the polyisocyanate and polyol(s) are contacted It is also possible to prereact all or a portion of the polyol(s), in the absence of water, with the polyisocyanate to form a prepolymer, although such is not preferred The polyurethane foam of this invention is useful in a wide range of applications, such as in spray insulation, appliance foam, rigid insulating boardstock, laminates, and many other types of rigid foam The following examples are given to illustrate the invention and are not intended to limit the scope thereof. Unless stated otherwise, all parts and percentages are given by weight Example 1 Molded polyurethane foam is prepared by reacting, at an NCO index of 1.25, VORANATE M220 a crude methylene diphenylisocyanate, average NCO functionality 2.7, available from The Dow Chemical Company with a polyahl composition in the presence of water, catalyst, and surfactant as detailed below. The components, at about 20°C, are mixed and stirred for 10 seconds at about 3000 rpm using a propeller mixer prior to pouring the reacting mixture into a mold having dimensions 30 x 30 x 10 cm. Sufficient reacting mixture is poured into the mold to provide molded foam having an overall density of about 34 kg/m 3 The hydrocarbon blowing agent composition used to prepare the individual foams along with the physical properties of the free-rise foam is reported in Table 1. 78.7 pbw oxyethylene-oxypropylene adduct of a phenol/formaldehyde resin, Hydroxyl Number 196. 26.2 pbw NIAX APP 315, an aromatic polyester polyol with Hydroxyl No 315, available from Union Carbide Co. 26.2 pbw VORANOL RA640, an oxypropylene adduct of ethylene diamine, Hydroxyl Number 640, available from The Dow Chemical Company. 13 pbw diethylene glycol 1.8 pbw water 3.25 pbw TEGOSTAB B8408, a proprietary silicon-based surfactant available from Th. Goldschmidt AG. 1.17 pbw dimethylcyclohexylamine 1.3 pbw CURITHANE 206, a proprietary urethane catalyst available from The Dow Chemical Company. Where reported the physical properties of the foams are observed according to the following test procedure for; core density, DIN 53420; thermal conductivity, ISO 2581 ; compressive strength, DIN 53421 ; and dimensional stability ISO 2796. When reported, the average cell size diameter, is determined from inspection of a thin section using a polarized- light optical microscope in combination with a Quantimet 520 Image Analysis system. The accuracy of the measurement is considered to be ± 0.02 mm (20 micrometers). When the thermal conductivity performance of Foam 10 and Comparative Foams 1 , 6 and 21 is followed for an extended period of time, the advantageous long-term thermal insulation performance of foams prepared with the herein defined hydrocarbon blowing agent mixture becomes apparent. When compared to the other foams after the extended period of time, Foam 10 starts to exhibit a minimum loss of thermal insulation performance relative to its initial value and to exhibit a minimum thermal conductivity value. Thermal Conduct ivity (mW/m.K) Days Foam 1* Foam 6* Foam 10 Foam 21* 1 21.7 19.7 20.3 21.2 58 24.6 23.0 23.1 23.9 104 25.2 23.9 23.8 24.6 Difference after 104 days 3.5 4.2 3.5 3.4 These observations along with the reported dimensional stability performance indicate that polyurethane foam prepared according to this invention is superior to that of the art. Table I 1* 2* 3* 4* 5* 6* 7* 8 9 10 11* 12* 13 14 15* 16* 17 18* 19* 20* 21* Blowinq Aqent Cyclopentane (pbw) 0 2.93 5.86 8.8 11.73 14.66 0 2.93 5.86 8.8 11.73 0 2.93 5.86 8.8 0 2.93 5.86 0 2.93 0 (mole %) 0% 21% 41% 61% 81% 100% 0% 21 % 41 % 60% 81 % 0% 21% 41% 61% 0% 21% 41% 0% 21% 0% Pentane pbw) 14.25 11.4 8.55 5.7 2.85 0 14.25 11.4 8.55 5.7 2.85 14.25 11.4 8.55 5.7 14.25 11.4 8.55 14.25 11.4 14.25 (mole%) 100% 79% 59% 39% 19% 0 % 100% 79% 59% 40% 19 % 100% 79% 59% 39% 100% 79% 59% 100% 79% 100% Ratio iso-pentane/ 0/ 0/ 0/ 0/ 0/ / 20/ 25/ 33/ 50/ 100/ 40/ 50/ 66/ 100/ 60/ 75/ 100/ 80/ 100/ 100/ n-pentane 100 100 100 100 100 80 75 66 50 0 60 50 33 0 40 25 0 20 0 0 Molded 34.3 34.3 34.7 34.9 33.9 33.8 34.1 34.3 33.7 33.8 34.9 34.2 34.4 33.8 34 34.4 33.9 33.7 34.3 34.4 33.9 density (kg/m3) Thermal Conductivity, parallel to rise I (mW/m.K): I Initial 21.7 20.8 21.1 20.4 19.8 19.7 21.0 20.9 20.6 20.3 20.4 21.4 20.8 20.4 20.8 21.6 21.4 20.7 21.5 20.9 21.2 58 days 24.6 23.8 24.2 23.7 22.8 23.0 24.0 23.8 23.3 23.1 23.8 24.0 23.8 23.3 23.5 24.4 24.0 23.5 24.2 23.5 23.9 % change 13.3 14.4 14.7 16.2 15.2 16.8 14.3 13.9 13.1 13.8 16.7 12.1 14.4 14.2 13 13 12.1 13.5 12.5 12.4 12.7 Cell Size 374 372 400 387 379 378 373 372 376 383 373 397 353 381 392 370 369 390 370 369 386 (microns) Dimensional Stability at 0°C a) 1 day 0 -2.0 -1.4 -0.2 -0.9 -14.0 -0.2 -2.0 -1.3 -1.0 -6.2 -0.6 -2.7 -10.4 -0.8 -0.6 -0.8 -6.6 -1.7 -0.6 0 b) 57 days - 1.5 -6.6 -15.7 -0.4 -12.4 -24.6 -24.6 -3.1 -11.6 -3.0 -23.1 -2.3 -17.1 -24.0 -2.0 -1.5 -2.2 -21.9 -11.4 -1.1 -1.1 Not an example of this invention

Claims: Claims : 1. A hydrocarbon mixture, suitable for use as a physical blowing agent when preparing a polyurethane or polyisocyanurate foam, which based on total amounts of (a) and (b) present, consists of: a) from 5 to 80 mole percent of a C5-6 alicyclic alkane or mixtures of such; and b) from 95 to 20 mole percent of a mixture of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80. 2. An isocyanate-reactive composition for use in the preparation of polyurethane or polyisocyanurate foam which comprises a polyahl, water, and a hydrocarbon mixture characterized in that: a) the polyahl contains an aromatic-initiated polyether polyol present in from 30 to 90 parts per 100 parts by total weight of polyahl; b) the water is present in from 1.5 to 10 parts per 100 parts by total weight of polyahl; and c) the hydrocarbon mixture present in an amount of from 1 to 25 parts per 100 parts of polyahl consists, based on total amounts of (d) and (c2) present, of: d) from 5 to 80 mole percent of a C 5 . 6 alicyclic alkane or mixtures of such; and c2) from 95 to 20 mole percent of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80. 3. A process for preparing a polyurethane or polyisocyanurate foam by reacting an organic polyisocyanate with a polyahl containing isocyanate reactive hydrogens in the presence of a physical blowing agent characterized in that: a) the blowing agent present in an amount of from 1 to 25 parts per 100 parts by weight of polyahl is a hydrocarbon mixture consisting, based on total amounts of (i) and (ii), of i) from 5 to 80 mole percent of a C5-6 alicyclic alkane or mixtures of such; and ϋ) from 95 to 20 mole percent of a mixture of isopentane and n-pentane present in a mole ratio of from 80:20 to 20:80; b) the polyisocyanate having an average of from 2 to 3.5 isocyanate groups/molecule is present in an amount to provide from 0.5 to 5 isocyanate groups per isocyanate reactive hydrogen present. 4. The invention as claimed in Claims 1 to 3 wherein the alicyclic alkane of the hydrocarbon mixture is cyclopentane, methylcyclopentane or cyclohexane. 5. The invention as claimed in Claim 4 wherein the hydrocarbon mixture consists of: a) from 5 to 40 mole percent of cyclohexane; and b) from 95 to 60 mole percent of the mixture of isopentane and n-pentane. 6. The invention as claimed in Claim 4 wherein the hydrocarbon mixture consists of: a) from 15 to 60 mole percent of cyclopentane; and b) from 85 to 40 mole percent of the mixture of isopentane and n-pentane. 7. The invention as claimed in Claims 2 and 3 wherein the polyahl comprises an aromatic-initiated polyether polyol present in from 30 to 90 parts per 100 parts by weight of total polyahl. 8. The invention as claimed in Claims 2 and 7 wherein the polyahl further comprises an amine-initiated polyether polyol present in from 5 to 35 parts per 100 parts by total weight of polyahl. 9. The invention as claimed in Claims 2, 7 and 8 wherein the polyahl further comprises a liquid aromatic polyester polyol present in from 5 to 35 parts per 100 parts by total weight of polyahl. 10. The invention as claimed in Claims 3 to 1 1 which further comprises water in from 1.5 to 10 parts per 100 parts by total weight of polyahl.

Inventors: SMITS GUIDO F, SMITS, GUIDO, F.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1994
Main classification: C08J9
IPC codes: C08J9