Electrorheological fluid composition

Abstract: An electrorheological fluid composition wherein inorganic/organic composite particles comprising a core 1 comprising organic polymeric compound and a shell 3 comprising inorganic microparticles 2 which are electrically semiconducting in a semiconducting region in which conductivity is within a range of 10³-10⁻¹¹ Ω⁻¹/cm at room temperature, are dispersed in an electrically insulating medium. These inorganic/organic composite particles are produced by means of a method in which the cores 1 and the shells 3 are simultaneously formed, and the surfaces thereof are preferably polished. An electrorheological fluid composition possessing electrorheological effects, having superior storage stability, capable of use over long periods, having little abrasiveness, which is not affected by environmental temperature or humidity, a current value of which is stable, and which has little power consumption.

Description: Background of the Invention Field of the Invention The present invention relates to an electrorheological fluid composition which can be used, for example, in instruments for braking or for power transmission, such as clutches, dampers, shock absorbers, valves, actuators, vibrators, printers, vibrating devices, or the like, and more specifically, relates to an electrorheological fluid composition which stably generates large resistance to shearing flow by means of the application of an external electric field. Background Art Conventionally, compositions termed "electrorheological fluids" (hereinbelow referred to as "ER fluids") are known. These compositions are fluids which are obtained by dispersing solid particles in a medium having electric insulation properties, for example, and when an external electric field is applied thereto, the viscosity thereof increases markedly, and in certain cases, such a liquid may solidify; these are thus fluid compositions possessing the so-called "electrorheological effect" (hereinbelow referred to as the "ER effect"). This type of ER effect is also termed a "Winslow effect"; the effect is thought to be produced by the polarization of the solid particles dispersed in the electrically insulating medium by means of the action of the electric field produced between electrodes when voltage is applied to a composition disposed between the electrodes, and by the alignment and bridging in the direction of the electric field by means of electrostatic attraction based on this polarization, and the resistance to an external shearing flow. ER fluids possess the ER effect described above, so that they are expected to find applications in instruments for braking or for power transmission operating by electrical control, such as clutches, dampers, shock absorbers, valves, actuators, vibrators, printers, vibrating devices, or the like. However, conventionally known ER fluids possessed various problems. Conventionally, ER fluids were known in which solid particles having surfaces which adsorbed and retained water, such as silica gel particles, cellulose particles, starch particles, casein particles, or polystyrene-type ion exchange resin particles, or the like, were dispersed in electrically insulating oils such as silicone oil, diphenyl chloride, transformer oil, or the like; however, these possessed insufficient resistance to external shearing flow during the application of voltage (hereinbelow referred to as "the shearing resistance"), and furthermore, required a high applied voltage, had a large power consumption, and as a result of water adsorption of the solid particles or the like, current sometimes flowed abnormally, and the particles tended to migrate to one electrode and to precipitate thereon, and in addition, storage stability was also poor. Furthermore, when the water which was adsorbed by the particles was desorbed or evaporated as a result of heating and the water content of the particles changed, the electrorheological characteristics (hereinbelow referred to as "ER characteristics") changed as a result, and accordingly, there were problems in that the thermal resistance and resistance to moisture were poor. In order to solve these problems, for example, an ER fluid (Japanese Patent Application, First Publication, Laid-Open No. Hei 2-91194) was proposed in which inorganic solid particles incorporating semiconductors and having low electric conductivity were used as the solid particles and were dispersed in an electrically insulating oil, and an ER fluid (Japanese Patent Application, First Publication, Laid-Open No. Hei 3-200897) was proposed in which inorganic ion exchange particles comprising hydroxides of polyvalent metals, hydrotalcites, acid salts of polyvalent metals, hydroxyapatite, Nasicon (Na ion superionic conductor)-type compounds, clay minerals, potassium titanates, heteropoly-acid salts, or insoluble ferrocyanides were used as the solid particles and were dispersed in an electrically insulating oil: However, the difference in specific gravities between such inorganic solid particles and the electrically insulating oils which were used as the dispersion medium was large, so that when such a liquid was stored for a long period of time, the particles were precipitated, and the particles which were thus precipitated cohered to such an extent that they were not easily redispersed, and thus the storage stability of these fluids was poor. Furthermore, as these inorganic solid particles were extremely hard, when such particles collided with the electrodes which were used for the application of voltage or with the walls of apparatuses, they were abraded and damaged by the particles, and furthermore, the fragments which were scraped off by these collisions and were suspended in the ER fluid altered the ER characteristics, causing problems in that large, abnormal currents would flow from time to time, or suddenly, and thus the fluid could only be used for a short period of time. Furthermore, particularly in the case in which inorganic ion exchange particles were used which had a large electric conductivity, when a voltage was applied to the electrodes, a very large current flowed through the ER fluid and abnormal heating occurred, and this was undesirable in that it consumed an extremely large amount of electric power. In addition, a fluid was disclosed (Japanese Patent Application, First Publication, Laid-Open No. Hei 3-162494) which used, as the solid particles, particles which were obtained by using material having a specific gravity of 1.2 or less as a core, and then covering this core material with an organic polymeric compound having an anion group or a cation group which was dissociable in water. However, in this case, as the particles were water-bearing, when the water content of the particles changed as a result of an increase in the temperature of the system in which they were used or the like, the electric conductivity and polarization percentage of the liquid changed, and as a result, there were problems such as a change in the ER characteristics of the composition as a result of the temperature of the environment. EP -A - 0562 978, a document under Art. 54(3) EPC, discloses electrorheological fluids containing inorganic/organic composite particles, having a polymeric core and a shell of inorganic material. EP -A - 0394 049 concerns electrorheological fluids and discloses in its Example VII composite particles having a core of aluminium and a coating of silicate. Example V of the same document describes hollow aluminium microspheres coated with an aluminium oxide layer. EP - A - 0455 362 discloses electrorheological fluids containing composite particles obtained by dispersing minute particulates in a matrix. Summary of the Invention It is an object of the present invention to provide an electrorheological fluid composition which solves the problems described above, and which possesses a high ER effect, has superior storage stability, and has a long service life, causes little abrasion, is little affected by environmental temperature or humidity, and which furthermore has a stable current value and consumes little power. The electrorheological fluid composition of the present invention comprises inorganic/organic composite particles dispersed in an electrically insulating medium. The inorganic/organic composite particles consist of a core comprising an organic polymeric compound and a shell formed on the core and comprising an inorganic material selected form the group consisting of metal oxides, metal hydroxides, hydroxides of metal oxides, and inorganic ion exchangers, and the said inorganic material is subjected to metallic doping to adjust the electrical conductivity thereof to 10 3 - 10 -11 Ω -1 /cm at room temperature. The ER fluid composition in accordance with the present invention is obtained by dispersing inorganic/organic composite particles comprising a core comprising organic polymeric compounds and a shell comprising an electrically semiconducting inorganic material, in an electrically insulating medium, so that high ER effects are obtained, the composition possesses superior stability over time, possesses low abrasion so that the electrodes or walls of apparatuses are not abraded, and the current which flows when voltage is supplied is small, so that there is no danger of abnormal heating, the power consumption is small, and the composition is thus economical. The surfaces of the inorganic/organic composite particles may be polished. Furthermore, if the inorganic/organic composite particles described above are manufactured according to a method in which the cores and the shells are simultaneously formed, durable inorganic/organic composite particles can be obtained, so that the electrorheological fluid composition employing these particles suffers little degradation as a result of abrasion during use, and the composition can be used for a long period of time. Preferably said inorganic ion exchanger is at least one selected from the group consisting of hydroxides of polyvalent metals, hydrotalcites, acid salts of polyvalent metals, hydroxyapatites, Nasicon-type compounds, clay minerals, potassium titanates, heteropolyacid salts, and insoluble ferrocyanides. Most preferably said inorganic material further comprises another supporting member on which said inorganic material subjected.to metallic doping is applied. Brief Description of the Drawings Fig. 1 is a cross sectional view showing an inorganic/organic composite particle which is employed in the electrorheological fluid composition in accordance with the present invention. Fig. 2 is a schematic cross sectional diagram showing a clutch in which the electrorheorogical fluid composition of the present invention is used as a power transmission fluid. Detailed Description of the Invention In the present invention, it is preferable that the electrically semiconducting inorganic material comprising the shells comprise at least one of an inorganic material, comprising at least one selected from metal oxides, metal hydroxides, hydroxides of metal oxides, and inorganic ion exchangers, subjected to metallic doping; and an inorganic material in which, at least one of the above is executed as an electrically semiconducting layer on another support member. Furthermore, it is preferable that the inorganic/organic composite particles in the present invention be particles manufactured in accordance with a method in which the cores and the shells thereof are simultaneously formed. In this case, it is preferable that the surfaces of the inorganic/organic composite particles described above be polished. The electrorheological fluid composition of the present invention is fundamentally obtained by dispersing inorganic/organic composite particles in an electrically insulating medium; these inorganic/organic composite particles are formed by means of a core comprising an organic polymeric compound and shells comprising the electrically semiconducting inorganic material described above. It was confirmed that the electrorheological fluid composition of the present invention having this type of structure possesses superior ER effects, can be used for a long period of time, and causes little abrasion of apparatuses. Next, the components comprising the present invention will be explained in detail. Examples of the organic polymeric compound which can be used as the core of the inorganic/organic composite particles include, for example, one or a mixture or copolymers of two or more of poly(meth)acrylic ester, (meth)acrylic ester-styrene copolymer, polystyrene, polyethylene, polypropylene, nitrile rubber, butyl rubber, ABS resin, nylon, polyvinyl butylate, ionomer, ethylene-vinyl acetate copolymer, vinyl acetate resin or polycarbonate resin. Furthermore, it is possible to use the organic polymeric compounds described above in a form in which they contain functional groups such as hydroxyl groups, carboxyl groups or amino groups; such organic polymeric compounds containing functional groups are preferable, as they increase the ER effects. Examples of the electrically semiconducting inorganic material which is preferably employed as the shells in the inorganic/organic composite particles include, for example an inorganic material choosen among metal oxides, metal hydroxides, hydroxides of metal oxides, and inorganic ion exchangers, said inorganic material being subjected to metallic doping to adjust the electrical conductivity thereof within a range of 10 3 - 10 -11 Ω -1 /cm at room temperature, or at least one of the above which has been subjected to metal doping is executed as an electrically semiconducting layer on another supporting member. Among these electrically semiconducting inorganic materials, examples of the inorganic ion exchanger include, for example, hydroxides of polyvalent metals, hydrotalcites, acid salts of polyvalent metals, hydroxyapatites, Nasicon-type compounds, clay minerals, potassium titanates, heteropoly acid salts, and insoluble ferrocyanides. These exhibit superior electrorheological effects when solid particles thereof are dispersed in an electrically insulating medium. Hereinbelow, detailed explanation will be given with respect to these various electrically semiconducting inorganic substances. (1) Metal oxides: these include, for example, SnO 2 , amorphous titanium dioxide (produced by Idemitsu Petrochemical Co., Ltd.). (2) Metal hydroxides: these include, for example, titanium hydroxide, and niobium hydroxide. Here, titanium hydroxide encompasses water-bearing titanium oxide (produced by Ishihara Sangyo Kaisya, Ltd.), metatitanic acid (also called β-titanic acid, TiO(OH) 2 ), and orthotitanic acid (also called α-titanic acid, Ti(OH) 4 ). (3) Hydroxides of metal oxides: examples hereof include, for example, FeO(OH) (gacite), and the like. (4) Hydroxides of polyvalent metals: these compounds are represented by the formula MO x (OH) y (where M represents a polyvalent metal, x indicates a number having a value of 0 or greater, and y represents a positive number); for example, zirconium hydroxide, bismuth hydroxide, tin hydroxide, lead hydroxide, aluminum hydroxide, tantalum hydroxide, molybdenum hydroxide, magnesium hydroxide, manganese hydroxide and iron hydroxide. (5) Hydrotalcites: these compounds are represented by the general formula M 13 Al 6 (OH) 43 (Co) 3 •12H 2 O (where M represents a bivalent metal); examples of the bivalent metal M include Mg, Ca, and Ni. (6) Acid salts of polyvalent metals: examples hereof include, for example, titanium phosphate, zirconium phosphate, tin phosphate, cerium phosphates, chromium phosphates, zirconium arsenate, titanium arsenate, tin arsenate, cerium arsenate, titanium antimonate, tin antimonate, tantalum antimonate, niobium antimonate, zirconium tungstate, titanium vanadate, zirconium molybdate, titanium selenate, and tin molybdate. (7) Hydroxyapatites: these include, for example, calcium apatite, lead apatite, strontium apatite, and cadmium apatite. (8) Nasicon-type compounds: these encompass compounds such as, for example, (H 3 O)Zr 2 (PO 4 ) 3 ; however, in the present invention, it is also possible to use a Nasicon-type compound in which (H 3 O) has been replaced by Na. (9) Clay minerals: these include, for example, montmorillonite, sepiolite, and bentonite; sepiolite is particularly preferable. (10) Potassium titanates: these are represented by the general formula aK 2 O•bTiO 2 •nH 2 O (where a represents a positive number such that 0 < a ≤ 1; b represents a positive number such that 1 ≤ b ≤ 6; and n represents a positive number); for example, these include K 2 •TiO 2 •2H 2 O, K 2 O•2TiO 2 •2H 2 O, 0.5K 2 O•TiO 2 •2H 2 O, and K 2 O•2.5TiO 2 •2H 2 O. In the general formula above, compounds in which a or b are not integers can be easily synthesized by the acid treatment of a compound in which a or b are appropriate integers, and the replacement of K with H. (11) Heteropoly-acid salts: these are represented by the general formula H 3 AE 12 O 40 •nH 2 O (where A represents phosphorus, arsenic, germanium, or silicon; E represents molybdenum, tungsten, or vanadium; and n represents a positive number); these include, for example, ammonium molybdophosphate, and ammonium tungstosphosphate. (12) Insoluble ferrocyanides: these are represented by the following general formula: M b-pxa A[E(CN) 6 ] (In the formula, M indicates an alkali metal or a hydrogen ion; A represents a heavy metal ion such as zinc, copper, nickel, cobalt, manganese, cadmium, iron (III), or titanium; E represents iron (II), iron (III), or cobalt (II); b represents 4 or 3; a represents the valence number of A; and p represents a positive number within a range of 0 - b/a.) Included in this are, for example, insoluble ferrocyanide compounds such as Cs 2 Zn[Fe(CN) 6 ] and K 2 Co[Fe(CN)] 6 . The inorganic ion exchangers of (4)∼(9) above all possess OH groups, and exchangers (hereinbelow termed "substitutional inorganic ion exchangers"), which have a portion or all of the ions at the ion exchange site of the inorganic ion exchanger substituted with other ions, are also included in the inorganic ion exchanger in accordance with the present invention. That is to say, when the inorganic ion exchangers described above are represented by the formula R-M 1 (where M 1 represents the ions of the ion exchange site), substitutional inorganic ion exchangers in which a portion or all of M 1 in R-M 1 has been substituted with ions M 2 , differing from M 1 , by means of the ion exchange reaction described hereinbelow, can also be used as the inorganic ion exchanger in accordance with the present invention. xR - M 1 + yM 2 → Rx - (M 2 )y + xM 1 (Here, x and y represent the valence numbers of ions M 2 and M 1 , respectively.) M 1 differs based on the type of inorganic ion exchanger containing an OH group; however, in inorganic ion exchangers which exhibit an ability to exchange cations, M 1 is typically H + , and in this case, M 2 represents at least one metal ion other than H + , such as alkali metal ion, alkali earth metal ion, polyvalent typical species metal ion, transition metal ion, or rare earth metal ion. In inorganic ion exchangers possessing OH groups which exhibit an ability to exchange anions, M 1 represents, in general, OH-, and this case, M 2 represents at least one anion selected from all anions other than OH - , such as, for example, I, Cl, SCN, NO 2 , Br, F, CH 3 COO, SO 4 , or CrO 4 , or a complex ion. Furthermore, with respect to inorganic ion exchangers which have temporarily lost their OH groups as a result of a high temperature heating process, but have re-acquired OH groups by means of immersion in water or the like, such post-high temperature heating process inorganic ion exchangers also represent a type of inorganic ion exchanger which may be used in the present invention; concrete examples thereof include Nasicon-type compounds, for example, HZr 2 (PO 4 ) 3 , which is obtained by heating (H 3 O)Zr 2 (PO 4 ) 3 , and high-temperature heat-processed hydrotalcite materials (heat processed at a temperature within a range of 500 - 700°C). (13) Metal-doped electrically semiconducting inorganic materials: these are materials in which an electrically semiconducting inorganic material is doped with a metal such as antimony (Sb) or the like, in order to increase the electric conductivity of the above-described electrically semiconducting inorganic materials (1) - (12); examples thereof include antimony (Sb)-doped tin oxide (SnO 2 ) and the like. (14) Materials in which an electrically semiconducting inorganic material is executed as an electrically semiconducting layer on another supporting member: examples hereof include, for example, materials in which inorganic particles such as titanium oxide, silica, alumina, silica-alumina, barium sulfate (BaSO 4 ), or the like, or organic polymeric particles such as polyethylene, polypropylene, or the like, are used as the support member, and antimony (Sb)-doped tin oxide (SnO 2 ) is executed thereon as an electrically semiconducting layer, and the like. Particles to which electrically semiconducting inorganic materials are applied in this manner function as electrically semiconducting inorganic materials as a whole. It is possible to use not merely one type of such electrically semiconducting inorganic materials, but rather to use two or more types thereof simultaneously in the shells. In order to sufficiently produce the effects particular to this invention, among the electrically semiconducting inorganic materials indicated in (1) - (14) above, it is particularly preferable to use (1) metal oxides, (2) metal hydroxides, (3) hydroxides of metal oxides, (4) hydroxides of polyvalent metals, All electrically insulating media which were used in conventional ER fluids may be used as the electrically insulating medium used in the composition of the present invention. For example, any fluid may be used which has high electric insulation and electric insulation breakdown strength, is chemically stable, and in which the inorganic/organic composite particles may be stably dispersed, examples thereof including diphenylchloride, butyl sebacate, aromatic polycarbonate higher alcohol ester, halophenylalkylether, transformer oil, paraffin chloride, fluorine-containing oil, silicone-containing oil, perfluoro carbon oil, or mixtures thereof. The inorganic/organic composite particles used in the present invention are formed by means of a coie comprising organic polymeric compound and a shell comprising electrically semiconducting inorganic material. That is to say, as is shown schematically in Fig. 1, the surface of a core 1 comprising organic polymeric compound is covered by the deposition of microparticles 2 of an electrically semiconducting inorganic material in a layer shape, and shell 3 is thus formed. This type of inorganic/organic composite particle may be manufactured by means of various methods. For example, a method is known in which core particles 1 comprising organic polymeric compound and microparticles 2 comprising electrically semiconducting inorganic material are blown in a'jet stream and caused to collide. In this case, the electrically semiconducting inorganic material microparticles 2 collide with the surface of the core particles 1 at high speed, adhere thereto, and form shells 3. Furthermore, a different manufacturing method is known in which core particles 1 are suspended in a gas and an electrically semiconducting inorganic material solution in spray form is sprayed onto the surfaces thereof. In this case, the solution is deposited on the surfaces of core particles 1 and is dried, and thereby shells 3 are formed. However, the preferable method for the manufacture of the inorganic/organic composite particles is a method in which core 1 and shell 3 are simultaneously formed. In such a method, for example, when the organic polymeric compound monomer forming core 1 is subjected to emulsion polymerization, suspension polymerization, or dispersion polymerization in a polymerization medium, the electrically semiconducting inorganic material microparticles 2 are placed in the monomer described above, or are caused to be present in the polymerization medium. Water is preferable as the polymerization medium; however, it is also possible to use a mixture of water and a watersoluble organic solvent, or to use an organic poor solvent. In accordance with such a method, simultaneously with the polymerization of the monomers in a polymerization medium and the formation of the core particles 1, the electrically semiconducting inorganic material microparticles 2 are arranged in a layer form on the surface of the core particles 1 and cover these core particles 1, thus forming shells 3. In the case in which the inorganic/organic composite particles are produced by means of emulsion polymerization or suspension polymerization, by means of combining the hydrophobic characteristics of the monomer and the hydrophilic characteristics of the electrically semiconducting inorganic material, it is possible to orient the majority of the electrically semiconducting inorganic material microparticles on the surface of the core particles. By means of this method in which core 1 and shell 3 are simultaneously formed, the electrically semiconducting inorganic material particles 2 are minutely, discretely and strongly adhered to the surface of the core particles 1 comprising organic polymeric compound, and thus durable inorganic/organic composite particles are formed. The shape of the inorganic/organic composite particles used in the present invention is not necessarily limited to a spherical shape; however, in the case in which the core particles are manufactured by means of a regulated emulsion or suspension polymerization method, the form of the inorganic/organic composite particles which are obtained is nearly completely spherical. The particle diameter of the inorganic/organic composite particles is not particularly restricted; however, a range of 0.1 - 500 µm, and in particular, a range of 5 - 200 µm, is preferable. The particle diameter of the electrically semiconducting inorganic material microparticles 2 is not particularly restricted; however, a range of 0.005 - 100 µm is preferable, and a range of 0.01 - 10 µm is still more preferable. In this type of inorganic/organic composite particle, the weight ratio (%) of the electrically semiconducting inorganic material forming the shells 3 and the organic polymeric compound forming cores 1 is not particularly restricted; however, it is preferable that the ratio [electrically semiconducting inorganic material]:[organic polymeric compound] be within a range of 1:99 - 60:40, and it is still further preferable that it be within a range of 4:96 - 30:70. If the weight ratio of the electrically semiconducting inorganic material is less than 1%, the ER effects of the ER fluid composition which is obtained will be insufficient, while when this ratio exceeds 60%, an excessively large current will flow in the fluid composition which is obtained. When the inorganic/organic composite particles are manufactured by means of the methods described above, especially the method in which cores 1 and shells 3 are simultaneously formed, it has become clear through analysis that a portion or entirety of surfaces of the shells 3 of the inorganic/organic composite particles are covered with a thin layer of an organic polymeric material or an additive used in the process of manufacturing, such as a dispersant, an emulsifier, or the like. Accordingly, it is observed that the ER effects of the electrically semiconducting inorganic material microparticles cannot be sufficiently exhibited (see Example 14). This type of thin layer of inactive material can be removed by means of polishing the surfaces of the particles. Accordingly, in the preferable electrorheological fluid composition in accordance with the present invention, inorganic/organic composite particles having polished surfaces are employed. However, in the case in which the inorganic/organic composite particles are produced by means of a method in which cores 1 are first formed and then shells 3 are formed thereon, no inactive material is present on the surfaces of shells 3, and the ER effects of the electrically semiconducting inorganic material are sufficiently large, so that polishing is not absolutely necessary. The polishing of the particle surfaces can be accomplished by a variety of methods. For example, it is possible to conduct this polishing by means of dispersing the inorganic/organic composite particles in a dispersion medium such as water or the like, and by agitating this. At this time, it is possible to conduct this polishing by means of a method in which a polishing material such as grains of sand or balls is mixed into the dispersion medium and is agitated along with the inorganic/organic composite particles, or by means of a method in which agitation is conducted using a grinding stone. Furthermore, it is possible to conduct agitation without the use of a dispersion medium by employing a dry process using the inorganic/organic composite particles and a polishing material or a grinding stone such as those described above. A more preferable polishing method is a method in which the inorganic/organic composite particles are subjected to airstream-blown agitation in a jet air stream or the like. This is a method in which the particles themselves collide violently with one another in the gas and are thus polished, so that other polishing material is unnecessary, and the inactive materials which are separated from the particle surfaces can be easily separated by means of classification, so that such a method is preferable. In this jetstream-blown agitation, it is difficult to specify the type of apparatus employed, the agitation speed, and the polishing conditions, as a result of the qualities of the inorganic/organic composite particles; however, in general, an agitation speed of 6000 rpm and a jetstream-blown agitation time within a range of 0.5 - 15 minutes are preferable. It is possible to produce the electrorheological fluid composition of the present invention by agitating and mixing the above-described inorganic/organic composite particles uniformly in an electrically insulating medium, and where necessary, together with other components such as dispersants or the like. Any agitator which is normally used for dispersing solid particles in a liquid dispersion medium may be used as an agitator for this purpose. The percentage of inorganic/organic composite particles present in the electrorheological fluid composition of the present invention is not particularly restricted; however, a range of 1 - 75 weight percent is preferable, and in particular, a range of 10 - 60 weight percent is more preferable. When the percentage contained thereof is less than 1%, sufficient ER effects cannot be obtained, while when the percentage contained exceeds 75%, the initial viscosity of the composition when a voltage is not applied is excessively large, so that the use thereof is difficult. The electrorheological fluid composition in accordance with the present invention having the composition described above comprises solid particles, the shells of which comprise electrically semiconducting inorganic material, dispersed in an electrically insulating medium, so that the composition possesses ER effects. These inorganic/organic composite particles are formed with a shell comprising electrically semiconducting inorganic material possessing strong ER effects, so that an ER fluid composition in accordance with the present invention using such particles generates a large shearing resistance even with respect to a low applied voltage. Furthermore, in the case in which a electrically semiconducting inorganic material having a large electric conductivity is employed, it is possible to adjust the weight ratio of the shell material with respect to the core material of the inorganic/organic composite particles, so that by means of this, it is possible to adjust the conductivity, and thus to restrain abnormal heating and power consumption while the ER fluid composition is electrically charged. In the present invention, the cores of the inorganic/organic composite particles are comprising organic polymeric compounds, so that it is possible to cause the specific gravity thereof to approach the specific gravity of the above-described electrically insulating medium, and by means of this, the precipitation of the particles can be prevented over long periods of time. Furthermore, the cores of these inorganic/organic composite particles comprise organic polymeric compound, so that the particles as a whole are soft, even though these particles have shells which are comprising hard inorganic material, and such particles will not cause abrasion of electrodes or instrument walls during use. In a preferred form of the present invention, the inorganic/organic composite particles are manufactured by means of a method in which the cores and the shells are formed simultaneously, so that the bond between the cores and the shells are strong, and the shells will not strip away from the core as a result of friction and the like during use, which would lead to changes in the characteristics thereof, so that the particles may be used for a long period of time. At this time, the surfaces of the inorganic/organic composite particles are polished, so that it is possible to maintain ER effects without interfering with the activity of the electrically semiconducting inorganic material which forms the shells. In the case in which nonaqueous electrically semiconducting inorganic material is employed, the inorganic/organic composite particles are a water-free type of dispersion particles, and it is possible to make the ER fluid composition obtained a water-free type of ER fluid composition. What is meant here by "water-free type" is that water is not added in a positive manner in order to apply ER effects, not that no water is included in the system. This type of water-free ER fluid composition possesses the advantage of maintaining stable ER characteristics even if the temperature thereof rises during use and the amount of water contained changes. The ER fluid composition of the present invention possesses superior ER effects and good stability and low abrasiveness, so that it can be used effectively as a fluid for power transmission or for braking which can be electrically controlled in instruments such as clutches, dampers, shock absorbers, valve, actuators, vibrators, printers, vibrating devices, or the like. Fig 2 shows a preferred embodiment of the ER fluid of the present invention; a clutch utilizing the ER fluid of the present invention as a power transmission fluid is shown as an example. Reference numeral 4 in the diagram indicates the ER fluid of the present invention; clutch case 14 is filled therewith. Within this clutch case 14, a clutch plate 11, which is on the engine side, and a clutch plate 12, which is on the vehicle axis side, both of which are disk-shaped, are disposed. And an axle 10 is provided integrally in the center of the clutch plate 11. Furthermore, the engine side clutch plate 11 rotates about the axle 10. Normally, ER fluid 4 is in a state in which the inorganic/organic composite particles 6 are randomly dispersed within electrically insulating medium, and thus possesses fluidity. Accordingly, clutch plate 11 rotates freely within this fluid, and this rotation is not transmitted to the other clutch plate 12. However, when voltage is applied between these two clutch plates 11 and 12, the inorganic/organic composite particles 6 within the ER fluid are polarized, and are aligned and bridged in the direction of the applied electric field; that is to say, they are aligned and bridged in a direction perpendicular to both clutch plates. Along with this, the viscosity of the ER fluid increases, and the shearing resistance between the clutch plates is increased. In the ER fluid of the present invention, the shearing resistance is large, and exceeds the force at which clutch plate 11 rotates, so that vehicle axle side clutch plate 12 also rotates in concert with the engine side clutch plate 11. That is to say, both axles become firmly bonded, and the rotation of the engine side clutch plate is transmitted to the vehicle side clutch plate. It is possible to add components other than those described above to the composition of the present invention. Examples thereof include polymeric dispersants, surfactants, polymeric thickeners, or the like, which are used to increase the dispersibility of the inorganic/organic composite particles in the above-described medium, to adjust the viscosity of the fluid composition during application of voltage, and to increase the shearing resistance. Furthermore, the fluid composition in accordance with the present invention may be used in a mixture with conventional ER fluids in which solid particles comprising polymers or bridging materials of, for example, cellulose, starch, casein, polystyrene-type ion exchange resin, polyacrylate bridger, or azeridine compounds, are dispersed in an electrically insulating oil, such as silicone oil, diphenyl chloride, transformer oil, or the like, insofar as the characteristics of the fluid composition are not thereby lost. [Examples] Hereinbelow, the present invention will be explained in greater detail by way of embodiments. [Example 1] [According to the invention] A mixture of 40 g of antimony-doped tin oxide (produced by Ishihara Sangyo Kaisha, Ltd., SN-100, conductivity: 1.0 × 10 0 Ω -1 /cm), 300 g of butyl acrylate, 100 g of 1,3-butylene glycol dimethacrylate, and polymerization initiator was dispersed in 1800 ml of water containing 25 g of tertiary calcium phosphate as a dispersion stabilizer; this was agitated for a period of 1 hour at a temperature of 60°C and suspension polymerization was conducted. The product thus obtained was subjected to filtration, and where necessary, acid cleaning, water rinsing, and drying, and inorganic/organic composite particles (1-A) were obtained. The water content of these particles was measured at 0.30 weight percent by means of Karl Fisher's titration method. Furthermore, the average particle diameter was 23.2 µm. The inorganic/organic composite particles (1-A) which were thus obtained were subjected to jetstream-blown agitation for a period of 5 minutes at 6,000 rpm using a jetstream agitator (a hybridizer manufactured by Nara Machinery Company, Ltd.), the surfaces thereof were polished, and inorganic/organic composite particles (1-B) were obtained. The water content of these particles was 0.41 weight percent, and the average particle diameter thereof was 25.3 µm. The inorganic/organic composite particles (1-A) and (1-B) were uniformly dispersed in silicone oil (produced by Toshiba Silicone Company, TSF 451-1000) having a viscosity of 1 Pa•s at room temperature, so that the amount of particles obtained was 33 weight percent, and the ER fluid compositions of Examples (1-A) and (1-B) were thus obtained. These ER fluid compositions were placed in a coaxial cylinder viscometer, a direct current voltage was applied between the inner and outer cylinders at a temperature of 25°C, and a torque was applied to the inner cylinder electrode, and the shear stress (Pa) at various shear rates (s -1 ), and current density (µA/cm 2 ) between the inner and outer cylinder during the measurement of shear stress, were measured. In the case of the ER fluid composition of Example (1-B), the current value became excessively large during measurement of shear stress, so that the applied voltage was set at 1 KV/mm. The results are shown in Table 1. Shear Rate (s -1 ) Example Applied Voltage 320 191 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 1-A Shear Stress (Pa) E=0 950 575 350 221 129 79.4 47.1 28.5 13.6 8.68 5.95 E=2KV/mm 1030 662 464 360 303 265 243 223 206 201 191 Current Density (µA/cm 2 ) 13.0 18.1 31.1 54.5 88.3 125 161 197 260 291 312 1-B Shear Stress (Pa) E=0 908 546 327 198 117 70.7 43.4 26.0 12.4 7.44 E=1KV/mm 1070 749 560 434 332 273 228 200 186 174 166 Current Density (µA/cm 2 ) 36.4 67.5 117 161 213 265 286 312 306 265 286 (Example 2] [According to the invention] The conditions of Example 2 were identical to those of Example 1, with the exception that 40 g of rutile-type titanium oxide (produced by Ishihara Sangyo Kaisha, Ltd., Taipeegu ET-300W, conductivity: 5.0 × 10 -2 Ω -1 /cm) having antimony-doped tin oxide applied to the surface thereof was used in place of the antimony-doped tin oxide used in Example 1; inorganic/organic composite particles (2-A), the surfaces of which were not polished, were obtained. The water content of these particles was 0.36 weight percent, and the average particle diameter was 13.2 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (2-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.28 weight percent, and the average particle diameter was 15.0 µm. These inorganic/organic composite particles (2-A) and (2-B) were uniformly dispersed in silicone oil following a procedure identical to that of Example 1 so as to produce a percentage contained of 33 weight percent, and thus the ER fluid compositions of Examples (2-A) and (2-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 2. Shear Rate (s -1 ) Example Applied Voltage 320 191 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 2-A Shear Stress (Pa) E=0 918 553 335 206 126 79.4 49.6 32.2 16.4 11.2 8.18 E=2KV/mm 982 613 397 260 187 136 102 76.9 57.0 44.6 42.2 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 1.3 1.3 1.3 1.3 2.6 2-B Shear Stress (Pa) E=0 905 558 335 206 124 76.9 47.1 29.8 15.4 9.92 7.44 E=2KV/mm 1030 695 503 382 315 268 236 213 174 124 112 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 3] [Not according to the invention] A process was followed which was identical to that of Example 1, with the exception that 40 g of titanium hydroxide (common name: water-containing titanium oxide, produced by Ishihara Sangyo Kaisha, Ltd., C-II, conductivity: 9.1 × 10 -6 Ω -1 /cm) was used in place of the antimony-doped tin oxide used in Example 1, and inorganic/organic composite particles (3-A), the surfaces of which were not polished, were obtained. The water content of these particles was 0.66 weight percent, and the average particle diameter was 17.3 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (3-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.72 weight percent, and the average particle diameter was 17.3 µm. These inorganic/organic composite particles (3-A) and (3-B) were uniformly dispersed in silicone oil following a procedure identical to that of Example 1 so that the percentage contained thereof was 33 weight percent, and thus the ER fluid compositions of Examples (3-A) and (3-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 3. Shear Rate (s -1 ) Example Applied Voltage 320 191 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 3-A Shear Stress (Pa) E=0 980 593 357 219 135 81.8 52.1 31.5 16.6 11.9 7.94 E=2KV/mm 1000 620 392 243 154 96.7 64.5 42.7 24.8 17.4 10.7 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 3-B Shear Stress (Pa) E=0 868 521 315 191 114 70.7 39.7 26.0 12.9 7.94 5.46 E=2KV/mm 1020 759 578 496 382 293 231 188 143 122 107 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 4] [Not according to the invention] A process was followed which was identical to that of Example 1, with the exception that niobium hydroxide (produced by Mitsui Mining & Smelting Co., Ltd., niobium hydroxide, conductivity: 1.0 × 10 -7 Ω -1 /cm) was used in place of the antimony-doped tin oxide which was used in Example 1, and inorganic/organic composite particles (4-A), the surfaces of which were not polished, were obtained. The water content of these particles was 1.86 weight percent, and the average particle diameter was 15.7 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (4-B), the surfaces of which were polished, were obtained. The water content of these particles was 1.10 weight percent, and the average particle diameter was 15.4 µm. These inorganic/organic composite particles (4-A) and (4-B) were uniformly dispersed in silicone oil following a manner identical to that of Example 1 so that the percentage contained thereof was 33 weight percent, and thus the ER fluid compositions of Examples (4-A) and (4-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 4. Shear Rate (s -1 ) Example Applied Voltage 115 68.5 40.9 24.9 14.2 8.9 4-A Shear Stress (Pa) E=0 452 290 186 127 80.7 55.4 E=2KV/mm 463 295 190 131 91.0 63.3 Current Density (µA/cm 2 ) <5 <5 <5 <5 <5 <5 4-B Shear Stress (Pa) E=0 414 259 164 108 72.8 51.4 E=2KV/mm 430 281 206 174 154 134 Current Density (µA/cm 2 ) <5 <5 <5 <5 <5 <5 [Example 5] [Not according to the invention] A process was followed which was identical to that of Example 1, with the exception that 40 g of an amorphous-type titanium dioxide (produced by Idemitsu Petrochemical Co., Ltd., Idemitsu Titania IT-PC, conductivity: 9.1 × 10 -11 Ω -1 /cm) was used in place of the antimony-doped tin oxide used in Example 1, and inorganic/organic composite particles (5-A), the surfaces of which were not polished, were obtained. The water content of these particles was 1.24 weight percent, and the average particle diameter was 18.0 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (5-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.94 weight percent, and the average particle diameter was 17.9 µm. These inorganic/organic composite particles (5-A) and (5-B) were uniformly dispersed in silicone oil in a manner identical to that of Example 1 so that the percentage contained thereof was 33 weight percent, and thus the ER fluid compositions of Examples (5-A) and (5-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 5. Shear Rate (s -1 ) Example Applied Voltage 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 5-A Shear Stress (Pa) E=0 382 228 139 84.3 53.5 33.5 16.6 9.42 E=2KV/mm 456 312 226 171 136 115 91.8 83.1 78.1 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 5-B Shear Stress (Pa) E=0 350 210 126 78.1 45.9 29.8 14.9 9.48 E=2KV/mm 558 451 397 377 342 310 285 270 268 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 6] [Not according to the invention] A process was followed which was identical to that of Example 1, with the exception that 40 g of amorphous-type titanium dioxide (produced by Idemitsu Petrochemical Co., Ltd., Idemitsu Titania IT-S, conductivity: 7.7 × 10 -11 Ω -1 /cm) was used in place of the antimony-doped tin oxide used in Example 1, and inorganic/organic composite particles (6-A), the surfaces of which were not polished, were obtained. The water content of these particles was 0.66 weight percent, and the average particle diameter was 16.1 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (6-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.58 weight percent, and the average particle diameter was 16.9 µm. These inorganic/organic composite particles (6-A) and (6-B) were uniformly dispersed in silicone oil in a manner identical to that of Example 1 so that the percentage contained thereof was 33 weight percent, and thus the ER fluid compositions of Examples (6-A) and (6-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 6. Shear Rate (s -1 ) Example Applied Voltage 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 6-A Shear Stress (Pa) E=0 402 239 145 88.0 53.3 31.5 14.9 9.18 E=2KV/mm 451 312 236 193 159 134 109 102 95.5 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 6-B Shear Stress (Pa) E=0 345 206 124 75.6 45.9 27.3 12.4 7.44 E=2KV/mm 553 469 422 419 374 335 295 273 263 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 7] [Not according to the invention] A process was followed which was identical to that of Example 1, with the exception that 40 g of FeO(OH) (common name: gacite, produced by Ishihara Sangyo Kaisha, Ltd., gacite A, conductivity: 9.4 × 10 -8 Ω -1 /cm) was used in place of the antimony-doped tin oxide used in Example 1, and inorganic/organic composite particles (7-A), the surfaces of which were not polished, were obtained. The water content of these particles was 0.42 weight percent, and the average particle diameter was 10.1 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (7-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.68 weight percent, and the average particle diameter was 10.1 µm. These inorganic/organic composite particles (7-A) and (7-B) were uniformly dispersed in silicone oil in a manner identical to that of Example 1 so that the percentage contained thereof was 33 weight percent, and thus the ER fluid compositions of Examples (7-A) and (7-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 7. Shear Rate (s -1 ) Example Applied Voltage 320 191 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 7-A Shear Stress (Pa) E=0 1030 625 389 241 155 102 69.4 47.1 28.5 19.8 12.4 E=2KV/mm 1040 637 402 263 181 135 109 91.8 73.2 62.0 52.1 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 7-B Shear Stress (Pa) E=0 915 526 322 195 118 73.2 43.4 27.3 13.6 8.68 E=2KV/mm 1290 608 357 211 134 104 107 102 91.8 81.8 62.0 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 8] [Not according to the invention] A process was followed which was identical to that of Example 1, with the exception that 20 g of the titanium hydroxide employed in Example 3, and 20 g of the niobium hydroxide employed in Example 4 were mixed and used in place of the antimony-doped tin oxide used in Example 1, and inorganic/organic composite particles (8-A), the surfaces of which were not polished, were obtained. The water content of these particles was 0.89 weight percent, and the average particle diameter was 17.8 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 1, and inorganic/organic composite particles (8-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.59 weight percent, and the average particle diameter was 20.0 µm. These particles were uniformly dispersed in silicone oil in a manner identical to that of Example 1 so that the percentage contained thereof reached 33 weight percent, and thus the ER fluid compositions of Examples (8-A) and (8-B) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 1. The results thereof are shown in Table 8. Shear Rate (s -1 ) Example Applied Voltage 320 191 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 8-A Shear Stress (Pa) E=0 1030 615 365 218 134 84.3 52.1 32.2 16.1 10.4 6.70 E=2KV/mm 1040 633 370 220 135 87.0 55.0 33.5 16.6 10.7 6.90 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 8-B Shear Stress (Pa) E=0 952 670 397 236 143 89.3 53.3 32.2 16.1 9.92 5.70 E=2KV/mm 1560 734 476 347 211 179 181 186 171 164 161 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 9] [Not according to the invention] A mixture of 40 g of the titanium hydroxide which was employed in Example 3, 260 g of butyl acrylate, 40 g of hydroxyethyl methacrylate, 100 g of 1,3-butylene glycol methacrylate, and polymerization initiator was dispersed in 1800 ml of water containing 25 g of tertiary calcium phosphate as a dispersion stabilizer; this was agitated for a period of 1 hour at a temperature of 60°C and suspension polymerization was conducted. The product thus obtained was subjected to filtration, and where necessary, acid cleaning, and water rinsing and drying, and inorganic/organic composite particles (9-A) were obtained. The water content of these particles was measured at 1.00 weight percent by means of Karl Fisher's titration method. Furthermore, the average particle diameter was 16.3 µm. The inorganic/organic composite particles (9-A) which were thus obtained were subjected to jetstream-blown agitation for a period of 5 minutes at 6,000 rpm using a jetstream agitator (a hybridizer manufactured by Nara Machinery Company, Ltd.), and inorganic/organic composite particles (9-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.64 weight percent, and the average particle diameter was 15.4 µm. These inorganic/organic composite particles (9-A) and (9-B) were uniformly dispersed in silicone oil having a viscosity of 1 Pa·s at room temperature, so that the amount contained thereof was 33 weight percent, and the ER fluid compositions of Examples (9-A) and (9-B) were obtained. These compositions were placed in a coaxial cylinder viscometer, a direct current voltage was applied between the inner and outer cylinders at a temperature of 25°C, and a torque was applied to the inner cylinder electrode, and the shear stress (Pa) at various shear rates (s -1 ), and the current value (µA/cm 2 ) between the inner and outer cylinder during the measurement of shear stress, were measured. The results thereof are shown in Table 9. Shear Rate (s -1 ) Example Applied Voltage 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 9-A Shear Stress (Pa) E=0 372 228 138 84.3 52.1 32.2 16.1 9.92 E=2KV/mm 389 248 159 102 65.7 44.6 24.8 15.6 10.6 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 9- B Shear Stress (Pa) E=0 335 203 122 75.6 44.6 26.5 12.4 7.44 E=2KV/mm 670 603 533 466 372 337 273 248 226 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 10] [Not according to the invention] A process was followed which was identical to that of Example 9, with the exception that 40 g of methacrylic acid was used in place of the hydroxyethyl methacrylate which was used in Example 9 and inorganic/organic composite particles (10-A), the surfaces of which were polished, were obtained. The water content of these particles was 1.44 weight percent, and the average particle diameter was 18.0 µm. Next, these particles were subjected to jetstream-blown agitation in a manner identical to that of Example 9, and inorganic/organic composite particles (10-B), the surfaces of which were polished, were obtained. The water content of these particles was 0.91 weight percent, and the average particle diameter was 17.0 µm. The inorganic/organic composite particles (10-A) and (10-B) were uniformly dispersed in silicone oil in a manner identical to that of Example 9 so that the percentage contained thereof was 33 weight percent, and thus the ER fluid compositions of Examples (10-A) and (10-8) were obtained. The ER effects of these fluid compositions were measured in a manner identical to that of Example 9. The results thereof are shown in Table 10. Shear Rate (s -1 ) Example Applied Voltage 115 68.5 40.9 24.9 14.2 8.9 4.2 2.5 1.4 10-A Shear Stress (Pa) E=0 372 228 142 86.8 52.1 31.5 15.4 9.18 E=2KV/mm 404 236 145 88.5 54.7 33.5 16.6 11.2 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 10-B Shear Stress (Pa) E=0 342 203 122 74.4 45.9 26.0 11.7 6.94 E=2KV/mm 526 404 330 283 238 203 161 139 131 Current Density (µA/cm 2 ) <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 <1.3 [Example 11] [Not according to the invention] A process was followed which was identical to that of Example 3, with the exception that 80 g of titanium hydroxide was used in place of the 40 g of titanium hydroxide which was used in Example 3, and inorganic/organic composite particles (11-A), the surfaces of which were not polished, and inorganic/organic composite particles (11-B), the surfaces of which were polished, were obtained. Using the inorganic/organic composite particles (11-A), the ER fluid composition of Example (11-A) was obtained, and using the inorganic/organic composite particles (11-B), the ER fluid composition of Example (11-B) was obtained. Next, the shear stresses (Pa) at various shear rates (s -1 ), and the current value (µA/cm 2 ) at these times, were measured in a manner identical to that of Example 1. The results thereof are shown in Table 11. Shear Rate (s -1 ) Example Applied Voltage 115 68.5 40.9 24.9 14.2 8.9 11-A Shear Stress (Pa) E=0 403 249 158 103 71.2 47.5 E=2KV/mm 427 269 174 119 83.1 63.3 Current Density (µA/cm 2 ) <5 <5 <5 <5 <5 <5 11-B Shear Stress (Pa) E=0 403 245 150 94.9 59.3 37.1 E=2KV/mm 728 566 447 360 293 249 Current Density (µA/cm 2 ) <5 <5 <5 <5 <5 <5 [Example 12] [Not according to the invention] The ER fluid composition of Example (11-B) above was placed in a tightly sealed transparent vessel, this was stored at room temperature, and the sedimentation state thereof was visually evaluated. The results thereof are shown in Table 12 as Example 12. [Comparative Example 1] [Not according to the invention] 5.5 weight percent of a powder consisting solely of titanium hydroxide was caused to be contained in the ER fluid composition of Example (11-B) in place of the inorganic/organic composite particles (11-B), and this was used as the ER fluid composition of Comparative Example 1. The sedimentation state of this was visually evaluated in a manner identical to Example 12. The results thereof are shown in Table 12 for the purposes of comparison with Example 12. In Table 12, a ○ indicates that sedimentation was not observed, while an X symbol indicates that sedimentation was observed. After 1 Day After 3 Days After 3 Weeks Example 11-B o ○ o ○ o ○ Comparative Example 1 o ○ X X o ○: Sedimentation was not observed X: Sedimentation was observed [Example 13] [Not according to the invention] A reciprocating motion level surface abrasion test was conducted in accordance with JIS H8682 (testing method for resistance to abrasion of the layer subjected to anodic oxidation of aluminum and aluminum alloy) using the ER fluid composition of Example (11-B) as the subject thereof. That is to say, on an aluminum plate in accordance with JIS H4000 A1050P, in place of a friction ring, a 4 cm 2 friction sliding device having placed thereon 10 sheets of gauze on which 1 g of the fluid was placed, was moved back and forth for 10 strokes under a load of 55 g/cm 2 , and the state of the surface of the aluminum plate was visually evaluated. The results thereof are shown in Table 13 as Example 13. [Comparative Example 2] [Not according to the invention] A powder consisting solely of titanium hydroxide was uniformly dispersed in silicone oil so that the percentage contained thereof was 33 weight percent, in place of the inorganic/organic composite particles (11-A) in the ER fluid composition of Example (11-A), and the fluid composition of Comparative Example 2 was obtained. A reciprocating motion level surface abrasion test was conducted with respect to the fluid composition which was thus obtained by a method which was identical to that of Example 13. The results thereof are shown in Table 13 for the purposes of comparison with Example 13. In Table 13, a ○ indicates that there was no change in the surface of the aluminum plate, and evidence of damage was not observed, while an X symbol indicates that multiple traces of damage were observed. State of Aluminum Plate Surface Example 13 o ○ Comparative Example 2 X o ○: No change (evidence of damage was not observed) X: Multiple traces of damage were observed [Example 14] [Not according to the invention] The surface atomic ratio of carbon, oxygen, and titanium atoms of the inorganic/organic composite particles (3-A) having unpolished surfaces, and the inorganic/organic composite particles (3-B) having polished surfaces which were obtained in Example 3 were measured (the measurement conditions were such that the excitation source was Mg(Kα) and the output was 260 W) in a high resolution X-ray photoelectron spectrograph (ESCALAB MKII, manufactured by the VG Scientific Company of England), and the measurement results of the composite particles (3-A) having unpolished surfaces are shown in Table 14 as Example (14-A), while the measurements of the composite particles (3-B) having polished surfaces are shown in Table 14 as Example (14-B). Inorganic/Organic Composite Particles Carbon Atoms (%) Oxygen Atoms (%) Titanium Atoms (%) Example 14-A (3-A) 64.83 28.27 6.90 Example 14-B (3-B) 47.06 39.49 13.46 From the results of Table 14, it can be seen that in comparison with the inorganic/organic composite particles (3-A) which were not subjected to jetstream blown agitation, the inorganic/organic composite particles (3-B) which were subjected to jetstream blown agitation had a surface carbon atom ratio which was small, while the titanium atom ratio was large. This corresponds to the fact that, as can be seen in Table 3, the ER fluid composition utilizing the inorganic/organic composite particles (3-B) which were subjected to jetstream blown agitation exhibits ER effects which are greater than those of the ER fluid composition which utilized the inorganic/organic composite particles (3-A) which were unpolished. From these results, it can be concluded that in the inorganic/organic composite particles shown in the above examples, which were produced by means of a method in which the core and the shell were simultaneously formed, there is a possibility that a part of the shell will be covered by a thin film of core material or an additive material such as dispersant or emulsifier, and that by the means of the removal of this layer covering this shell using friction polishing by means of jetstream blown agitation, the effective active surface of the electrically semiconducting inorganic material particle layer is increased, so that when an ER fluid composition is made therefrom, greater ER effects are exhibited.

Claims: An electrorheological fluid composition comprising inorganic/organic composite particles dispersed in an electrically insulating medium, characterized in that said inorganic/organic composite particles consist of a core comprising an organic polymeric compound and a shell formed on the core and comprising an inorganic material selected from the group consisting of metal oxides, metal hydroxides, hydroxides of metal oxides, and inorganic ion exchangers, and that said inorganic material is subjected to metallic doping to adjust the electrical conductivity thereof to 10 3 -10 -11 Ω -1 /cm at room temperature. An electrorheological fluid according to claim 1, characterized in that said inorganic ion exchanger is at least one selected from the group consisting of hydroxides of polyvalent metals, hydrotalcites, acid salts of polyvalent metals, hydroxyapatites, Nasicon-type compounds, clay minerals, potassium titanates, heteropolyacid salts, and insoluble ferrocyanides. An electrorheological fluid according to anyone of claims 1 and 2, characterized in that said inorganic material further comprises another supporting member on which said inorganic material subjected to metallic doping is applied . An electrorheological fluid according to anyone of claims 1 to 3, characterized in that said inorganic/organic composite particles are produced by a method in which cores and shells thereof are formed simultaneously. An electrorheological fluid according to anyone of claims 1 to 4, characterized in that the surfaces of the inorganic/organic composite particles are polished.

Inventors: EDAMURA KAZUYA, OTSUBO YASUFUMI, EDAMURA, KAZUYA, OTSUBO, YASUFUMI, EDAMURA, KAZUYA, C/O FUJIKURA KASEI CO., LTD.
Applicants: FUJIKURA KASEI KK, FUJIKURA KASEI CO., LTD.
Application year: 1994
Main classification: C10M171
IPC codes: C10N10, C10M161, C10N30, C10M177, C10N40, C10N70, C10N20, C10M169, C10M171