Method of manufacturing a polyimide optical waveguide

Abstract: A polyimide optical waveguide comprising a core (2) made of polyimide whose refractive index is controlled to a predetermined value by electron beam irradiation, and a cladding (1, 3) set in contact with the core and having a refractive index lower than that of the core.

Description: The present invention relates to a polyimide optical waveguide, and more particularly to a polyimide optical waveguide in which the polyimide, the refractive index of which is controlled by an electron beam irradiation to a desired value, is used as a core. As an optical communication system is put to practical, thanks to the development of a low loss optical fiber, it is desired that various kinds of devices for the optical communication be developed. Further, there are demands for an optical wiring technique, more particularly an optical waveguide technique by which the optical devices are packaged in high density. Generally, some conditions are required of an optical waveguide, for example, low optical losses, facile fabrication, controllable core-cladding refractive index ratio, and a high heat resistance. As material of the optical waveguide having low optical losses, a silica-based material can be cited. As already proved in optical fiber, silica which has a good optical transmittance achieves an optical loss of 0.1 dB/cm or less at wavelength of 1.3 µm, if used in an optical waveguide. Manufacture of quartz glass optical waveguides, however, presents a number of problems including a manufacturing processes lengthy in terms of time, the high temperatures needed during fabrication, and the difficulty of making optical waveguides with a large area. To solve these problems, attempts have been made to produce optical waveguides using plastics such as polymethylmethacrylate (PMMA), which can be manufactured at low temperatures and low cost. Conventional plastic optical waveguides, however, have low resistance to high temperature. Thus, there is a demand for plastic optical waveguide having an excellent heat resistance. Among the various organic polymers currently available, polyimides provide very high resistance to heat. Hence, these materials have been widely employed in the field of electronics, to form an insulating film between layers in the multilayer wiring or to form a flexible print board. Document. EP-A-0 454 590 describes a polyimide optical waveguide. In one embodiment an embedded type optical waveguide is described comprising a multi-layer structure with an upper cladding layer consisting of a polyimide layer which has a lower index of refraction than that of the polyimide core layer. In view of this, the inventors of the present invention have studied and developed a polyimide optical material which is applicable for an optical waveguide. When polyimide is used in optical communication applications as the optical material, there are two important points. First, its transparency in the visible and near infrared regions is excellent. Second, its refractive index can be controlled freely. The inventors disclose a fluorinated polyimide with excellent transparency in the visible and near infrared regions, in Jpn. Pat. Appln. KOKAI Publication No. 3-72528. Further, in Jpn. Pat. Appln. KOKAI Publication No. 4-8734, it is disclosed that the core-cladding refractive index ratio, as is needed for, for example, forming an optical waveguide, is quite controllable by copolymerizing such fluorinated polyimide. Furthermore, optical waveguides using fluorinated polyimide are disclosed in Jpn. Pat. Appln. KOKAI Publications Nos. 4-9807, 4-235505 and 4-235506. The control of the refractive index difference between the core layer for passing the light and the cladding layer for shutting the light is achieved by adjusting the fluorine content in the polyimide. Namely, two kinds of fluorinated polyimide having the different refractive indices for the core layer and for the cladding layer are used respectively. Therefore, there may be some problems with a kind of an optical waveguide; that is, the core layer and the cladding layer may be different in thermal properties or the birefringence. In the conventional method of manufacturing a polyimide optical waveguide, a reactive ion etching (RIE) method, which is used in a semiconductor manufacturing process, is generally employed. The RIE method is disadvantageous in that it comprises many steps. Therefore, a facile fabrication of polyimide optical waveguides, which comprises a smaller number of steps and by which the above-mentioned method may be replaced, has been desired. The inventors of the present invention have studied to solve the above-mentioned problems and have found it possible to change the refractive index of polyimide films by irradiating the films with an electron beam, as they disclose in Japanese Patent Application No. 4-226549. An object of the present invention is to provide an optical waveguide in which the problems caused by the difference in thermal properties and birefringence between the core and the cladding can be solved, with simple steps. In order to achieve the above-mentioned object, the polyimide optical waveguide according to the present invention comprises a polyimide core and a polyimide cladding in contact with said polyimide core, said polyimide core having a refractive index higher than that of said polyimide cladding, said polyimide cladding comprising a two-layer structure formed of a first polyimide layer and a second polyimide layer having the same refractive index as that of the first polyimide layer and stacked on the first polyimide layer wherein said core is formed in one of the first polyimide layer and the second polyimide layer by selectively irradiating an electron beam on said polyimide cladding to form an embedded channel waveguide. According to another aspect of the invention, there is provided a polyimide optical waveguide comprising a polyimide core and a polyimide cladding in contact with said polyimide core, said polyimide core having a refractive index higher than that of said polyimide cladding wherein said cladding comprises a two-layer structure formed of a first polyimide layer, a second polyimide layer having a lower refractive index than that of said first polyimide layer and stacked on the first polyimide layer, said polyimide core is formed in said first polyimide layer by selectively irradiating an electron beam on said polyimide cladding, and a first raised-index polyimide cladding region is formed in the second polyimide layer, beneath the polyimide core formed in the first polyimide layer, said first raised-index polyimide claddingregion having a refractive index greater than that of the adjacent parts of the second polyimide layer and formed by the same electron beam irradiation process used to form the polyimide core, thereby forming a channel waveguide. The subclaim defines a preferred embodiment of the polyimide optical waveguide of the invention. Having the above-mentioned structure, both the core and the cladding of the polyimide optical waveguides of the present invention can have almost the same thermal properties and birefringence. This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which: FIG. 1 is a sectional view showing one non-inventive example of an embedded channel waveguide in which a core having rectangular section is embedded in one layer of the cladding of a two-layer structure; FIG. 2 is a sectional view showing one non-inventive example of an embedded channel waveguide in which the core having rectangular section is embedded in the second layer of the cladding of a three-layer structure; FIG. 3 is a sectional view showing one non-inventive example of an embedded channel waveguide in which the core having semicircle section is embedded in one layer of the cladding of a two-layer structure; FIG. 4 is a sectional view showing one non-inventive example of a channel waveguide in which the core having semicircle section is embedded in the cladding of a one-layer structure; FIG. 5 is a sectional view showing one non-inventive example of a channel waveguide in which the core having rectangular section is embedded in one layer of the cladding of a two-layer structure; FIG. 6 is a sectional view showing one non-inventive example of a ridge channel waveguide having the structure of forming the core having rectangular section on the surface of the cladding of a one-layer structure; FIG. 7 is a sectional view showing one non-inventive example of a slab waveguide having the structure of laminating the core as the second layer on the surface of the cladding of a one-layer structure; FIG. 8 is a view showing the steps of manufacturing the polyimide optical waveguide by performing electron beam lithography, which is one example; FIG. 9 is a view showing the steps of manufacturing an embedded channel polyimide optical waveguide having a three-layer structure which is one embodiment of the present invention; FIG. 10 is a sectional view of an embedded channel polyimide optical waveguide of three-layer structure, which is one embodiment of the present invention; FIG. 11 is a view showing the steps of manufacturing an embedded channel waveguide of a two-layer structure by an electron beam irradiation, which is another embodiment of the present invention; FIG. 12 is a sectional view of a subject portion of a polyimide optical waveguide of a two-layer structure, which is still another embodiment of the present invention; FIG. 13 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 12; FIG. 14 is a sectional view showing the subject portion of a polyimide optical waveguide of a three-layer structure, which is another embodiment of the present invention; FIG. 15 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 14; FIG. 16 is a sectional view showing the subject portion of a polyimide optical waveguide of a four-layer structure, which is a non-inventive example; FIG. 17 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 16; FIG. 18 is a sectional view of the subject portion of showing another non-inventive example of a polyimide optical waveguide of a four-layer structure; FIG. 19 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 18; FIG. 20 is a sectional view of the subject portion of the polyimide optical waveguide of a five-layer structure, which is a non-inventive example; FIG. 21 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 20; FIG. 22 is a sectional view of the subject portion for showing a non-inventive example of the polyimide optical waveguide of a five-layer structure; FIG. 23 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 22; FIG. 24 is a sectional view of the subject portion of a polyimide optical waveguide of a six-layer structure, which is a non-inventive example; FIG. 25 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 24; FIG. 26 is a sectional view of the subject portion of showing an example of a non-inventive polyimide optical waveguide of a six-layer structure; FIG. 27 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 26; FIG. 28 is a sectional view of the subject portion of showing an example of a non-inventive polyimide optical waveguide of a seven-layer structure; and FIG. 29 is a view showing the steps of manufacturing the polyimide optical waveguide shown in FIG. 28. FIG. 1 shows a sectional view of an embedded channel waveguide of a two-layer structure, wherein a core 2 is formed on one cladding 1 and another cladding 3 is laminated on the cladding 1 so as to embed the core 2. The core 2 used herein is made of polyimide whose refractive index is controlled by irradiating with an electron beam. The polyimide includes polyimides formed of a tetracarboxylic acid or a derivative thereof and a diamine, polyimide copolymers, and polyimide mixtures, whose refractive index can be controlled. A derivative of a tetracarbxylic acid includes an acid anhydride, an acid chloride, or an ester. Examples of a tetracarboxylic acid are (trifluoromethyl) pyromellitic acid, di (trifluoromethyl) pyromellitic acid, di(heptafluoropropyl)pyromellitic acid, pentafluoroethylpyromellitic acid, bis(3,5-di(trifluoromethyl)phenoxy)pyromellitic acid, 2,3,3',4'-biphenyltetracarboxylic acid, 3,3',4,4'-tetracarboxydiphenylether, 2,3',3,4'-tetracarboxydiphenylether, 3,3',4,4'-benzophenonetetracarboxylic acid, 2,3,6,7-tetracarboxynaphthalene, 1,4,5,7-tetracarboxynaphthalene, 1,4,5,6-tetracarboxynaphthalene, 3,3',4,4'-tetracarboxydiphenylmethane, 3,3',4,4'-tetracarboxydiphenylsulfone, 2,2-bis(3,4-dicarboxyphenyl)propane, 2,2-bis(3,4-dicarboxyphenyl)-hexafluoropropane, 5,5'-bis(trifluoromethyl)-3,3',4,4'-teracarboxybiphenyl, 2,2',5,5'-tetrakis(trifluoromethyl)-3,3',4,4'-tetracarboxybiphenyl, 5,5'-bis(trifluoromethyl)-3,3',4,4'-tetracarboxydiphenylether, 5,5'-bis(trifluoromethyl)-3,3',4,4'-tetracarboxybenzophenone, bis{(trifluoromethyl)dicarboxyphenoxy}benzene, bis{(trifluoromethyl)dicarboxyphenoxy}(trifluoromethyl) benzene, bis(dicarboxyphenoxy)(trifluoromethyl)benzene, bis(dicarboxyphenoxy)bis(trifluoromethyl)benzene, bis(dicarboxyphenoxy)tetrakis(trifluoromethyl)benzene, 3,4,9,10-tetracarboxyperylene, 2,2-bis(4-(3,4-dicarboxyphenoxy)phenyl)propane, butanetetracarboxylic acid, cyclopentanetetracarboxylic acid, 2,2-bis{4-(3,4-dicarboxyphenoxy)phenyl}hexafluoropropane, bis((trifluorotnethyl)dicarboxyphenoxy)biphenyl, bis{(trifluoromethyl)dicarboxyphenoxy}bis-(trifluoromethyl)biphenyl, bis{(trifluoromethyl) dicarboxyphenoxy}diphenylether, bis(dicarboxyphenoxy)bis(trifluoromethyl)biphenyl, bis(3,4-dicarboxyphenyl)dimethylsilane, 1,3-bis(3,4-dicarboxyphenyl)tetramethyldisiloxane, difluoropyromellitic acid, 1,4-bis(3,4-dicarboxytrifluorophenoxy)tetrafluorobenzene, 1,4-bis(3,4-dicarboxytrifluorophenoxy)octafluorobiphenyl. Examples of a diamine include m-phenylenediamine, 2,4-diaminotoluene, 2,4-diaminoxylene, 2,4-diaminodurene, 4-(1H,1H,11H-eicosafluoroundecanoxy)-1,3-diaminobenzene, 4-(1H,1H-perfluoro-1-butanoxy)-1,3-diaminobenzene, 4-(1H,1H-perfluoro-1-heptanoxy)-1,3-diaminobenzene, 4-(1H,1H-perfluoro-1-octanoxy)-1,3-diaminobenzene, 4-pentafluorophenoxy-1,3-diaminobenzene, 4-(2,3,5,6-tetrafluorophenoxy)-1,3-diaminobenzene, 4-(4-fluorophenoxy)-1,3-diaminobenzene, 4-(1H,1H,2H,2H-perfluoro-1-hexanoxy)-1,3-diaminobenzene, 4-(1H,1H,2H,2H-perfluoro-1-dodecanoxy)-1,3-diaminobenzene, p-phenylenediamine, 2,5-diaminotoluene, 2,3,5,6-tetramethyl-p-phenylenediamine, 2,5-diaminobenzotrifluoride, bis(trifluoromethyl)phenylenediamine, diaminotetra(trifluoromethyl)benzene, diamino(pentafluoromthyl)benzene, 2,5-diamino (perfluorohexyl)benzene, 2,5-diamino(perfluorobuthyl) benzene, benzidine, 2,2'-dimethylbenzidine, 3,3'-dimethylbenzidine, 3,3'-dimethoxybenzidine, 2,2'-dimethoxybenzidine, 3,3',5,5'-tetramethylbenzidine, 3,3'-diacetylbenzidine, 2,2'-bis(trifluoromethyl)-4,4'-diaminobiphenyl, octafluorobenzidine, 3,3'-bis(trifluoromethyl)-4,4'-diaminobiphenyl, 4,4'-diaminodiphenylether, 4,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylsulfone, 2,2-bis(p-aminophenyl)-propane, 3,3'-dimethyl-4,4'-diaminodiphenylether, 3,3'-dimethyl-4,4'-diaminodiphenylmethane, 1,2-bis(anilino)ethane, 2,2-bis(p-aminophenyl)-hexafluoropropane, 1,3-bis(anilino)hexafluoropropane, 1,4-bis(anilino)octafluorobutane, 1,5-bis(anilino)decafluoropentane, 1,7-bis(anilino)tetradecafluoroheptane, 2,2'-bis(trifluoromethyl)-4,4'-diaminodiphenylether, 3,3'-bis(trifluoromethyl)-4,4'-diaminodiphenylether, 3,3',5,5'-tetrakis(trifluoromethyl)-4,4'-diaminodiphenylether, 3,3'-bis(trifluoromethyl)-4,4'-diaminobenzophenone, 4,4"-diamino-p-terphenyl, 1,4-bis(p-aminophenyl)benzene, p-bis(4-amino-2-trifluoromethylphenoxy)benzene, bis(aminophenoxy)-bis(trifluoromethyl)benzene, bis(aminophenoxy)tetrakis (trifluoromethyl)benzene, 4,4'''-diamino-p-quarterphenyl, 4,4'-bis(p-aminophenoxy)biphenyl, 2,2-bis(4-(p-aminophenoxy)phenyl)propane, 4,4'-bis(3-aminophenoxyphenyl)diphenylsulfone, 2,2-bis{4-(4-aminophenoxy)phenyl}hexafluoropropane, 2,2-bis{4-(3-aminophenoxy)phenyl}hexafluoropropane, 2,2-bis{4-(2-aminophenoxy)phenyl}hexafluoropropane, 2,2-bis{4-(4-aminophenoxy)-3,5-dimethylphenyl}hexafluoropropane, 2,2-bis(4-(4-aminophenoxy)-3,5-ditrifluoromethylphenyl)hexafluoropropane, 4,4'-bis(4-amino-2-trifluoromethylphenoxy)biphenyl, 4,4'-bis(4-amino-3-trifluoromethylphenoxy)biphenyl, 4,4'-bis(4-amino-2-trifluoromethylphenoxy)diphenylsulfone, 4,4'-bis(3-amino-5-trifluoromethylphenoxy)diphenylsulfone, 2,2-bis{4-(4-amino-3-trifluoromethylphenoxy)phenyl}hexafluoropropane, bis({trifluoromethyl)aminophenoxy}biphenyl, bis[{(trifluoromethyl)aminophenoxy}phenyl]hexafluoropropane, diaminoanthraquinone, 1,5-diaminonaphthalene, 2,6-diaminonaphthalene, bis{2-(aminophenoxy) phenyl}hexafluoroisopropylbenzene, bis(2,3,5,6)-tetrafluoro-4-aminophenyl)ether, bis(2,3,5,6)-tetrafluoro-4-aminophenyl)sulfide, 1,3-bis(3-aminopropyl)tetramethyldisiloxane, 1,4-bis(3-aminopropyldimethylsilyl)benzene, bis(4-aminophenyl)diethylsilane, 1,3-diaminotetrafluorobenzene, 1,4-diaminotetrafluorobenzene, 4,4'-bis(tetrafluoroaminophenoxy)octafluorobiphenyl. A fluorinated polyimide obtained from a tetracarboxylic dianhydride and a diamine, either one of, or both of which contain a fluorine atom combined thereto, is particularly preferably used in the present invention. Namely, either one of, or both of a fluorinated dianhydride and a fluorinated diamine are used to produce a polyimide. The above mentioned embedded channel waveguide as shown in FIG. 1 can be manufactured by the following method A polyamic acid solution is spin-coated on a substrate such as of silicon, and is thermally cured to form a polyimide layer. An electron beam is irradiated on the entire surface of the polyimide layer to change the refractive index to a predetermined value. An electron beam-absorbed dose of the polyimide layer depends on the composition of the polyimide, an energy of the electron beam, and the applied amount of the electron beam irradiation. The refractive index changes in accordance therewith approximately. This polyimide layer irradiated with the electron beam is used as a core layer. Next, the same polyamic acid solution is spin-coated on the core layer, and is thermally cured. The material is separated from the substrate to obtain a polyimide film of a two-layer structure. Then, the polyimide film of a two-layer structure is made to reverse and the irradiated polyimide layer is made to the upper surface. The lower surface of the reversed film is adhered by a method such as a thermocompression bonding on the other silicon substrate. Next, the core layer is patterned into a desired shape, for example, a rectangular shape, by RIE (reactive ion etching) method. Finally, the same polyamic acid solution is spin-coated over the patterned core layer, as an upper cladding layer, and is thermally cured, thereby preparing an embedded channel waveguide. The step of irradiating the entire surface of the polyimide layer with the electron beam, as described above, can be applied in forming an embedded channel waveguide, a ridge channel waveguide, and a slab waveguide, respectively shown in FIGS. 1, 6, and 7. Further, if a metal mask or the like is used, the irradiation step can be applied in forming an embedded channel waveguide and a channel waveguide as shown in FIGS. 2, 3, 4, and 5. In the above-mentioned process, the entire surface of the polyimide film is irradiated with the electron beam to form the core layer, and the RIE method is used at the time of forming the core. Alternatively, the electron beam irradiation is applied partially on the polyimide layer by using the metal mask or the like. However, for example, there is another method of forming the core having the predetermined refractive index and size in which electron beam lithography is applied selectively on the polyimide layer by means of an electron beam lithography system used in LSI manufacturing, without using the RIE processing. For example, a polyimide solution or a solution of a precursor thereof is applied by spin-coating on a silicon substrate 10, heated to remove the solvent, and cured if necessary, thereby to obtain a polyimide film 11 in step A as shown in FIG. 8. Next, the electron beam lithography is performed in step B shown in FIG. 8, to form a core 12 having the predetermined refractive index and size. By these two steps B and C shown in FIG. 8, it is possible to obtain an optical waveguide approximately same as a ridge channel waveguide formed by using the conventional RIE method. That is, it is possible to reduce the number of steps. By using such electron beam lithography method, it is possible to obtain an embedded channel or channel waveguide as shown in FIGS. 2, 3, 4, and 5. The structure of the optical waveguide manufactured by the above-mentioned process will be explained with reference to sectional views of FIGS. 2 to 7. FIG. 2 is a sectional view showing one non-inventive example of the embedded channel waveguide in which the core 2 having a rectangular section is embedded in the second layer of the cladding layers 1, 3, and 4 forming a three-layer structure. FIG. 3 is a sectional view showing one non-inventive example of the embedded channel waveguide in which the core having a semicircle section is embedded in one of the cladding layers forming a two-layer structure. FIG. 4 is a sectional view showing one non-inventive example of the channel waveguide, in which the core having a semicircle section is embedded in the cladding forming a one-layer structure. In this case, one of the cladding layers forming two-layer structure as shown in FIG. 3 can be of air. FIG. 5 is a sectional view showing one non-inventive example of the channel waveguide in which the core having a rectangular section is embedded in one of the cladding layers forming a two-layer structure. In this case, the third cladding layer shown in FIG. 2 can be of air. The structure of the optical waveguide in this invention is an embedded optical waveguide and the channel optical waveguide, both mentioned above. A non-inventive example comprises a ridge channel waveguide having the structure wherein the core having a rectangular section is mounted on the surface of the cladding having a one-layer structure, as shown in the sectional view of FIG. 6. Further, as shown in the sectional view of FIG. 7, it can be applied for a slab waveguide having the structure wherein the core used as the second layer is laminated on the surface of the cladding having a one-layer structure. Furthermore, the manufacturing of a waveguide with a guiding condition such as single-mode or a multi-mode are realized by controlling a core-cladding refractive index ratio, using electron beam irradiation. Further, even if the above-mentioned electron beam lithography system is not used, it is possible to form the core layer by irradiating the polyimide with the electron beam through an ordinary photomask. Furthermore, as the means for forming an embedded channel waveguide, the core layer film can be sandwiched by polyimide films which will become claddings, and these components can be compressed or adhered through thin adhesive agent layers. Hereinafter, the reference will be made to the specific Examples of the present invention. However, the present invention is not restricted to these Examples. Example 1 88.8 g (0.2 mol) of 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride, 64.0 g (0.2 mol) of 2,2'-bis(trifluoromethyl)-4,4'-diaminobiphenyl, and 1000 g of N,N-dimethylacetamide were added in a conical flask. The mixture was stirred for three days at the room temperature under nitrogen atmosphere to obtain a polyamic acid solution having a concentration of about 15% by weight. The polyamic acid solution was spin-coated on a silicon wafer, and heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minutes, and at 380°C for one hour in an oven to imidize it, thereby obtaining a polyimide layer with 10 µm thickness. As a result of measuring the refractive index of the film at wavelength of 1.3 µm, the refractive index in the direction parallel to the film surface (TE) was 1.521 and the refractive index in the direction perpendicular to the film surface (TM) was 1.513. Further, a thermal expansion coefficient was 8.2 × 10 -5 and a glass transition temperature was 335°C. The polyimide layer formed on the silicon substrate was irradiated with the electron beam having an energy of 400 kev for about 30 minutes at room temperature at a dose of 5 × 10 15 e/cm 2 . The measured refractive indices of this polyimide layer were 1.526 for TE direction and 1.517 for TM direction respectively. Further, the thermal expansion coefficient was 8 × 10 -5 , and the glass transition temperature was 330°C. After the same polyamic acid solution was spin-coated on the electron-beam irradiated polyimide, the solution was heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minutes, and at 380°C for one hour in the oven for imidization, thereby obtaining a polyimide film having a thickness of 30 µm and a two-layer structure. This polyimide film was separated from the silicon substrate, the irradiated polyimide surface was made to be an upper layer, and the lower layer was adhered to another silicon substrate. Next, using an electron beam vapor deposition system, a 0.3 µm thick aluminum film was formed on the polyimide film. After an usual positive resist was applied by the spin-coating method, prebake was performed. Then, ultraviolet rays were applied through a mask for forming a pattern having a line width of 10 µm and a length of 60 mm by using an ultra-high pressure mercury lamp, and the resist was developed by using a developer for positive resist. Thereafter, afterbake was performed. Next, the aluminum film was wet etched at each portion not coated with the resist. After washing and drying, the RIE processing of the polyimide was performed by using a dry etching system. The aluminum remaining on the polyimide was removed by applying the above-mentioned etching solution to obtain a ridge channel waveguide having a core width of 10 µm. Further, the same polyamic acid solution was spin-coated on the ridge channel waveguide, and was heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minutes, and at 380°C for one hour in the oven to achieve imidization. Thus, an upper cladding layer was formed. In this manner, an embedded channel waveguide was obtained in which the core-cladding refractive index ratio was almost same at TE and TM (0.005 for TE, 0.004 for TM). Further, the core and the cladding of this waveguide had almost the same thermal properties. As mentioned above, it is possible to manufacture a polyimide optical waveguide whose core and cladding have almost the same thermal properties and birefringence (ridge waveguides excluded). Next, another method of manufacturing a polyimide optical waveguide, using the polyimide multi-layer film of the present invention, will be described with reference to another embodiment. FIG. 9 is a view showing the steps in forming an embedded channel waveguide having a three-layer structure. FIG. 10 is a sectional view of the embedded channel waveguide. It is possible to form the waveguide in four steps. Unlike in the conventional method using the RIE method, it is possible to reduce the number of steps. Namely, a polyimide solution or a precursor solution is coated by, for example, spin-coating method on the substrate 10 of silicon or the like. The solution is heated to remove the solvent, and cured, if necessary, thereby to obtain a first polyimide layer as shown in step A shown in FIG. 9. Then, a second polyimide layer 13 is formed on the first polyimide layer 11, in step B shown in FIG. 9 by using a polyimide material whose refractive index is larger than that of the first layer. Further, a third polyimide layer 14 is formed on the second polyimide layer 13 in step C shown in FIG. 9 by using a polyimide material whose refractive index is smaller than that of the second layer 13. The desired pattern is drawn on the polyimide film having the three-layer structure with an electron beam, so as to have a predetermined refractive index and a predetermined size as shown in step D in Fig. 9. The relationship of refractive indices of these polyimide layers is n1<n2, and n3<n2, where the refractive index of the first polyimide layer is n1, that of the second polyimide layer is n2, and that of the third polyimide layer is n3. If changes of the refractive indices of the three polyimide layers are represented by Δn1, Δn2, and Δn3, respectively, by the electron beam irradiation, the refractive index of a region 1 of FIG. 10 is n3, that of a region 2 is n3 + Δn3, that of a region 3 is n3, that of a region 4 is n2, that of a region 5 is n1, that of a region 6 is n1 + Δn1, that of a region 7 is n1, that of a region 8 is n2, and that of a region 9 is n2 + Δn2. The materials and the irradiation condition are selected such that each difference (Δn1 - Δn2, Δn2 - Δn3, Δn3 - Δn1) of the refractive index change Δn1, Δn2, Δn3 caused by the electron beam irradiation is less than the refractive index difference between the original materials. Hence, the region 9 having the largest refractive index becomes the core in which the light is confined and guided. When the electron beam is applied onto the polyimide film, measures are taken, if necessary, to prevent deflection of the electron beam caused by a charge of a static electricity. To this end, for example, a conductive film may be deposited on the polyimide film, or a conductive mesh may be compressed on the polyimide film. Furthermore, it is possible to perform various pretreatments for the material to be irradiated with the electron beam. For example, the material can be left in the atmosphere which is filled with a substance and be irradiated with an electron beam to perform the electron beam irradiation effectively. It is possible to set the pretreatment conditions freely in accordance with the objective. After the core is formed by the electron beam lithography, if the core is sandwiched, at its upper and lower sides, between by the polyimide layers having lower refractive indices than that of the core, it is possible to obtain an embedded channel waveguide. The core is sandwiched through adhesive layers, by using thermocompression bonding, or by using spin-coating. The optical waveguide may have various shapes; it can be a linear, curved, folded, S-shaped, tapered, branched, or crossing optical directional coupler. It can be a two-mode waveguide coupler, or a grating. Further, the width of the core can be set freely. Hereinafter, the present invention will be described in detail, with reference to Examples. However, the present invention is not limited to these Examples. Typical Examples will be shown below though it is possible to manufacture the various kinds of polyimide optical waveguide by combining materials and shapes in various ways Example 2 (non-inventive) 88.8 g (0.2 mol) of 2,2-bis(3,4-dicarboxyphenyl)-hexafluoropropane dianhydride, 64.0 g (0.2 mol) of 2,2-bis(trifluoromethyl)-4,4'-diaminobiphenyl, and 1000 g of N,N-dimethylacetamide were added in a conical flask. The mixture was stirred for three days at room temperature under nitrogen atmosphere to obtain a polyamic acid solution having a concentration of about 15% by weight. After the polyamic acid solution was spin-coated on a silicon wafer, it was heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minutes, and at 350°C for one hour in an oven to achieve imidization, thereby forming a polyimide layer with 10 µm thickness. Then, aluminum was deposited on the polyimide layer to a thickness of 10 nm within a vacuum deposition system, and the resultant structure was introduced into an electron beam lithography system. Further, a pattern having a width of 8 µm and a length of 66 mm was drawn on the polyimide layer by using an electron beam having energy of 25 keV at a dose of 1500 µC/cm 2 . Thereafter, the aluminum film was removed by using an etching solution to obtain a polyimide optical waveguide. End of the obtained polyimide optical waveguide was optically polished, and a light having a wavelength of 633 nm was introduced thereinto. It was confirmed that the light was confined in the core and was guided. Further a light having a wavelength of 1.3 µm was introduced within the core of the waveguide via a single mode optical fiber, and the output light was received by a multi-mode optical fiber. When the intensity of the output light was measured, it was confirmed that the loss was 1 dB/cm or less, including the coupling loss. Example 3 (non-inventive) Aluminum was deposited on the polyimide film formed in the same way as in Example 2, and was introduced into the electron beam lithography system. A pattern having a width of 10 µm and a length of 66 mm was drawn on the film by using an electron beam having energy of 25 kev at a dose of 900 µC/cm 2 . Thereafter, the loss of the light having 1.3 µm of wavelength was measured for the waveguide prepared in this Example. It was 1 dB/cm or less, including the coupling loss. Example 4 88.8 g (0.2 mol) of 2,2-bis(3,4-dicarboxyphenyl)-hexafluoropropane dianhydride, 64.0 g (0.2 mol) of 2,2-bis(trifluoromethyl)-4,4'-diaminobiphenyl, and 1000 g of N,N-dimethylacetamide was added in a conical flask. The mixture was stirred for three days at room temperature under nitrogen atmosphere to obtain a polyamic acid solution having a concentration of about 15% by weight (hereinafter referred to as Solution A). Solution A was spin-coated on an optically polished aluminum plate and heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minutes, and at 350°C for one hour in the oven to achieve imidization, thereby forming a polyimide layer having a thickness of 10 µm. The mean refractive index of this layer relative to light having a wavelength of 1.3 µm was 1.519. Instead of 0.2 mol of 2,2-bis(3,4-dicarboxyphenyl) hexafluoropropane dianhydride, 0.14 mol of 2,2-bis (3,4-dicarboxyphenyl)hexafluoropropane dianhydride and 0.06 mol of pyromellitic acid dianhydride were used to prepare a polyamic acid solution (hereinafter referred to as Solution B) and a polyimide layer in the manner described above. The refractive index of this layer exhibited to the light having 1.3 µm wavelength was 1.527. Solution A was spin-coated on an optically polished aluminum substrate, such that a cured layer has a thickness of 20 µm. The solution was heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minute, and at 380°C for one hour in the oven to obtain a first polyimide layer. Further, Solution B was spin-coated thereon such that a cured layer has a thickness of 8 µm, and a second polyimide layer was prepared under the same curing condition. Aluminum was deposited to a thickness of 10 nm on the film having the two-layer structure in the vacuum deposition system, and the resultant structure was introduced into the electron beam lithography system. The polyimide film was irradiated with an electron beam having energy of 25 keV, over a width of 8 µm and a length of 66 mm, at a dose of 1500 µc/cm 2 . Then, the aluminum film was removed by an etching solution, thereby obtaining a polyimide optical waveguide. The end of the obtained polyimide optical waveguide were optically polished, and a light having a wavelength of 633 nm was introduced thereinto. It was confirmed that the light was confined in the second layer and was guided. Further, a light having a wavelength of 1.3 µm was found to be confined in the region (8 µm × 8 µm) and be guided to the output end of the waveguide. Example 5 Solution A was spin-coated on the film having the two-layer structure prepared in the same way as in Example 4, and thermally cured under the same curing conditions to form a third polyimide layer having a thickness of 20 µm. On the thus obtained polyimide film having the three-layer structure, the electron beam lithography was performed in the same manner as in Example 4, by using the electron beam lithography system. The end of the obtained polyimide optical waveguide was optically polished, and a light having a wavelength of 633 nm was introduced thereinto. It was confirmed that the light was confined in the second layer and was guided. Further, as for the light having a wavelength of 1.3 µm, it was confirmed that the light was confined in the region of 8 µm x 8 µm, and was guided to the another end of the waveguide. Example 6 (non-inventive) On the film having a three-layer structure prepared in the same way as in Example 5, Solution B was spin-coated so as to obtain a thickness of 8 µm after the heat curing, and cured under the same curing condition to form a fourth layer. Further, Solution A was spin-coated thereon so as to obtain a thickness of 20 µm after the heat curing, and cured under the same curing condition to form a fifth layer. Electron beam lithography was performed on the polyimide film having the five-layer structure in the same condition as in Example 4, by using the electron beam lithography system. The end of the obtained polyimide optical waveguide having the multi-layer structure was optically polished, and a light having a wavelength of 633 nm was introduced thereinto. It was confirmed that the light was confined in the second and fourth layers. Further, as for the light having a wavelength of 1.3 µm, it was confirmed that the light was confined in the regions of 8 µm x 8 µm of the second and fourth layers and was guided to the another end of the waveguide. Example 7 Solution A was spin-coated on a film having a two-layer structure prepared in the same way as in Example 4, so as to obtain a thickness of 20 µm after the heat curing, and cured under the same curing condition to form a third layer. Aluminum was deposited to a thickness of 10 nm on the film having the three-layer structure within the vacuum deposition system. The resultant structure was introduced into the electron beam lithography system. Then, this film was irradiated with an electron beam having energy of 50 kev, over a region of 8 µm (width) x 66 mm (length) at a dose of 1500 µC/cm 2 . Thereafter, the aluminum film was removed by using an etching solution to obtain a polyimide optical waveguide. The end of the obtained polyimide optical waveguide was polished optically, and a light having a wavelength of 633 nm was introduced thereinto. It was confirmed that the light was confined in the second layer and was guided. Further, as for the light having a wavelength of 1.3 µm, it was confirmed that the light was confined in the region of 8 µm x 8 µm, and was guided to the another end of the waveguide. Example 8 (non-inventive) On a film having a three-layer structure prepared in the same way as in Example 5, Solution B was spin-coated so as to obtain a thickness of 8 µm after the heat curing, and cured under the same curing condition to form a fourth layer. Further, Solution A was spin-coated thereon so as to obtain a thickness of 10 µm after the heat curing, and cured under the same curing condition to form a fifth layer. Electron beam lithography was performed on the polyimide film having the five-layer structure, in the same way as in Example 7, by using the electron beam lithography system. An end of the obtained polyimide optical waveguide having the multi-layer structure was polished optically, and light having a wavelength of 633 nm was applied to the end. It was confirmed that the light was confined in the second and fourth layers and was guided. As for the light having a wavelength of 1.3 µm, it was confirmed that the light was confined in the regions of 8 µm x 8 µm of the second and fourth layers and was guided to the another end of the waveguide. Next, a method of preparing the polyimide optical waveguide according to another embodiment of the present invention will be described with reference to FIG. 11. After a polyimide solution or a polyamic acid solution was applied by spin-coating on a substrate 10 as shown in FIG. 11, the resultant structure was heated, the solvent was removed, and the structure was cured, if necessary, thereby to obtain a polyimide film 11 in step A shown in FIG. 11. Then, an electron beam energy was selected, and the electron beam was applied to the film 11, thus changing the refractive index of the film 11 to a predetermined value and forming the predetermined size thereof, to form a core 12 having the predetermined depth in step B shown in FIG. 11. The electron beam must be applied in such a condition as not to permeate to the rear surface of the polyimide film 11. In this manner, a channel waveguide can be prepared. Further, an upper cladding 14 in step C shown in FIG. 11 is formed by means of spin-coating a polyimide solution or a polyamic acid solution on the lower cladding. With the manufacturing method described above, it is possible to omit the step of bonding the polyimide films and to omit the step of performing spin-coating on the polyimide film separated from the substrate. This further simplifies the manufacturing method. In the steps A to C shown in FIG. 11, the polyimide material can be treated in various ways before electron beam irradiation. For example, the electron beam irradiation can be achieved effectively by holding the material in an atmosphere filled with a substance. It is possible to perform pretreatment freely, in accordance with the objective. As for the shape of the optical waveguide, the path can be a liner, curved, folded, S-shaped, tapered, branched or crossing optical direction coupler. Furthermore, it can be a two-mode waveguide coupler, or a grating. Further, the core can have any width and depth desired. Specific examples will be explained. Although it is possible to manufacture the various kinds of polyimide optical waveguides by changing the combination of the material and the shape, typicial examples are as follows. Example 9 (non-inventive) 88.8 g (0.2 mol) of 2, 2-bis(3,4-dicarboxyphenyl)-hexafluoropropane dianhydride, 64.0 g (0.2 mol) of 2,2-bis(trifluoromethyl)-4,4'-diaminobiphenyl, and 1000 g of N,N-dimethylacetamide were added in a conical flask. The mixture was stirred for three days at room temperature under nitrogen atmosphere to obtain polyamic acid having a concentration of about 15% by weight. The polyamic acid solution was spin-coated on a silicon wafer, and heated at 70°C for two hours, at 160°C for one hour, at 250°C for 30 minutes, and at 350°C for one hour in an oven, to achieve imidization. Thus, a polyimide film having a thickness of 50 µm was obtained. This film was introduced into an electron beam lithography system. Then, this film was irradiated with an electron beam having energy of 10 kev at a dose of 1500 µC/cm 2 , thus forming a pattern having a width of 8 µm and a length of 60 mm. An end of the polyimide optical waveguide, thus formed was polished optically, and a light having a wavelength of 1.3 µm was introduced thereinto. When the another end of the waveguide was observed by using a microscope with an infrared camera, it was confirmed that the light was confined in the waveguide. Example 10 88.8 g (0.2 mol) of 2,2-bis(3,4-dicarboxyphenyl)-hexafluoropropane dianhydride, 64.0 g (0.2 mol) of 2,2-bis(trifluoromethyl)-4,4'-diaminobiphenyl, and 1000 g of N,N-dimethylacetamide were added in a conical flask. The mixture was stirred for three days at room temperature under nitrogen atmosphere, to obtain a polyamic acid solution having a concentration of about 15% by weight. This polyamic acid solution was spin-coated on a silicon wafer, and heated at 70°C for two hour, at 160°C for one hour, at 250°C for 30 minutes, and at 350°C for one hour in the oven to achieve imidization. Thus, a polyimide layer having a thickness of 50 µm was obtained. This layer was introduced into an electron beam lithography system. Then, an electron beam having an energy of 10 keV was applied onto this film at a dose of 1500 µC/cm 2 , thereby forming a pattern having a width of 8 µm a length of 60 mm. Thereafter, the polyamic acid solution was spin-coated on the polyimide layer formed above and cured to obtain an embedded channel polyimide optical waveguide. The end of the polyimide optical waveguide was polished optically, and light having a wavelength of 1.3 µm was introduced thereinto. When the another end of the waveguide was observed using a microscope with an infrared camera, it was confirmed that the light was confined in the core of the waveguide. This embedded channel polyimide optical waveguide is in only three steps, in less steps than in the conventional method. Further, it can be manufactured without bonding between polyimide films and without performing spin-coating on the separated polyimide film. Embodiments of the polyimide optical waveguides having two or more polyimide layers, and a method of manufacturing waveguides, wherein cores and cladding are formed alternately in the predetermined regions of the layers will be explained with reference to FIGS. 12 to 29. FIG. 12 is a sectional view of the subject portion of a polyimide optical waveguide having a two-layer structure. The optical waveguide has a polyimide layer 20 having a predetermined refractive index. A second polyimide layer 21 having a refractive index higher than that of the polyimide layer 20 is formed on the layer 20. A cladding 23 is formed in the polyimide layer 20 by applying an electron beam from the upper side to the predetermined region, and a core 24 is formed in the polyimide layer 21. The process of manufacturing the core and the cladding of the waveguide shown in FIG. 12 will be described with reference to FIG. 13. The polyimide layer 20 is formed on the substrate 10 in step A shown in FIG. 13, and the polyimide layer 21 is formed on the layer 20 in step B shown in FIG. 13. Then, an electron beam is directed from above the upper side of the polyimide layer 21 and hence to the substrate 10. The cladding 23 is thereby formed in the polyimide layer 20, and the core 24 is thus formed in the second polyimide layer 21 over the region irradiated with the electron beam, in step C shown in FIG. 13. FIG. 14 is a sectional view of the subject portion of a polyimide optical waveguide having a three-layer structure. The waveguide has a polyimide layer 21 having a predetermined refractive index. A second polyimide layer 20 having a refractive index lower than that of the polyimide layer 21 is formed on the layer 21. Further a third polyimide layer 22 having a refractive index higher than that of the second polyimide layer 20 is formed on the second polyimide layer 20. A core 24 is formed in the polyimide layer 21 by applying an electron beam onto the upper side and hence to the substrate 10. A cladding 23 is formed in the polyimide layer 20, and another core 25 is formed in the polyimide layer 22. The process of manufacturing the core and the cladding of the waveguide shown in FIG. 14 will be described with reference to FIG. 15. The polyimide layer 21 is formed on the substrate 10 in step A shown in FIG. 15. The second polyimide layer 20 is formed on the polyimide layer 21 in step B shown in FIG. 15. Further, in step C shown in FIG. 15, the third polyimide layer 22 is formed on the second polyimide layer 20. Then, in step D shown in FIG. 15, an electron beam is directed from above the upper side of the polyimide layer 22 and hence to the substrate 10. The core 24 is thereby formed in the polyimide layer 20, the cladding 23 is thereby formed in the second polyimide layer 21, and the core 25 is formed in the third polyimide layer 22 over the region irradiated with the electron beam in step D shown in FIG. 15. The following polyimide waveguides are non-inventive examples. FIG. 16 is a sectional view of the subject portion of a polyimide optical waveguide having a four-layer structure. A second polyimide layer 20 having a refractive index lower than that of the polyimide layer 21 is formed on a first polyimide layer 21 having a predetermined refractive index. A third polyimide layer 22 having a refractive index higher than that of the second polyimide layer 20 is formed on the second polyimide layer 20, and the fourth polyimide layer 26 having a refractive index lower than that of the polyimide layer 22 is formed on the third polyimide layer 22. In a prescribed region, a core 24 formed by irradiating the upper side with an electron beam is located in the polyimide layer 21, a cladding 23 is formed in the polyimide layer 20, a core 25 is formed in the polyimide layer 22, and a cladding 27 is formed in the polyimide layer 26. The process of manufacturing the cores and the claddings of the waveguide shown in FIG. 16 will be explained with reference to FIG. 17. The polyimide layer 21 is formed on the substrate 10 in step A shown in FIG. 17. The second polyimide layer 20 is formed on the polyimide layer 21 in step B shown in FIG. 17. Further, in step C shown in FIG. 17, the third polyimide layer 22 is formed on the second polyimide layer 20. Then, in step D shown in FIG. 17, the fourth polyimide layer 26 is formed on the third polyimide layer 22. In step E shown in FIG. 17, an electron beam is applied to the upper side of the polyimide layer 26 and hence to the substrate 10. As a result, the core 24 is formed in the polyimide layer 21, the cladding 23 is formed in the second polyimide layer 20, the core 25 is formed in the third polyimide layer 22, and the cladding 27 is formed in the fourth polyimide layer 26, over the region irradiated with the electron beam. Next, another example of a polyimide optical waveguide having a four-layer structure will be described with reference to the sectional view of FIG. 18. On a polyimide layer 20 having a predetermined refractive index, a second polyimide layer 21 having a refractive index higher than that of the polyimide layer 20 is formed. A third polyimide layer 26 having a refractive index lower than that of the second polyimide layer 21 is formed on the second polyimide layer 21, and the fourth polyimide layer 22 having a refractive index higher than that of the polyimide layer 26 is formed on the third polyimide layer 26. A cladding 23 is formed in the polyimide layer 21 by irradiating an electron beam to the upper side and hence to a predetermined region. A cladding 27 is formed in the polyimide layer 26, and the core 25 is formed in the polyimide layer 22. The step of manufacturing the cores and the claddings of the waveguide shown in FIG. 18 will be explained with reference to FIG. 19. The polyimide layer 20 is formed on the substrate 10, in step A shown in FIG. 19: The second polyimide layer 21 is formed on the polyimide layer 20 in step B shown in FIG. 19. Further, in step C shown in FIG. 19, the third polyimide layer 26 is formed on the second polyimide layer 21. As shown in step D shown in FIG. 19, the fourth polyimide layer 22 is formed on the third polyimide layer 26. Then in step E shown in FIG. 19, an electron beam is applied to the upper side of the polyimide layer 22 and hence to the substrate 10. As a result, the cladding 23 is formed in the polyimide layer 20, the core 24 is formed in the second polyimide layer 21, the cladding 27 is formed in the third polyimide layer 26, and the core 25 is formed in the fourth polyimide layer 22, over the region irradiated with the electron beam. FIG. 20 is a sectional view of the subject portion of a polyimide optical waveguide having a five-layer structure, wherein a fifth polyimide layer 28 is formed on the fourth layer 26 of the waveguide of FIG. 16. The fifth layer 28 has a refractive index higher than that of the fourth layer 26. A core 24 is formed in the polyimide layer 21 by applying an electron beam to the upper side of the fifth polyimide layer 28. A cladding 23 is formed in the polyimide layer 20, a core 25 is formed in the polyimide layer 22, a cladding 27 is formed in the polyimide layer 26, and a core 29 is formed in the fifth polyimide layer 28. The steps of manufacturing the cores and the claddings of the polyimide optical waveguide shown in FIG. 20 will be explained with reference to FIG. 21. The polyimide layer 21 is formed on the substrate 10 in step A shown in FIG. 21. The second polyimide layer 20 is formed on the polyimide layer 21 in step B shown in FIG. 21. Further, in step C shown in FIG. 21, the third polyimide layer 22 is formed on the second polyimide layer 20. In step D shown in FIG. 21, the fourth polyimide layer 26 is formed on the third polyimide layer 22. Then, in step E shown in FIG. 21, the polyimide layer 28 is formed on the polyimide layer 26. In step F shown in FIG. 21, an electron beam is applied to the upper side of the fifth polyimide layer 28 and hence to the substrate 10. As a result, the core 24 is formed in the polyimide layer 21, the cladding 23 is in the second polyimide layer 20, the core 25 is in the third polyimide layer 22, the cladding 27 is in the fourth polyimide layer 26, and the core 29 is in the fifth polyimide layer 28. A further non-inventive example of a polyimide optical waveguide having a five-layer structure will be described with reference to the sectional view of FIG. 22. The first to fourth layers of this embodiment are formed in the same way as the layers of the polyimide optical waveguide (FIG. 19) having a four-layer structure, which are formed in steps A to D shown in FIG. 19. A step E shown in FIG. 23 is the step of forming the fifth polyimide layer 30 having a refractive index lower than that of the polyimide layer 22, on the fourth polyimide layer 22. An electron beam is applied to the upper side of the fifth polyimide layer 30 and hence to the substrate 10 in step F shown in FIG. 23, a cladding 23 is formed in the polyimide layer 20, a core 24 is in the second polyimide layer 21, a cladding 27 is in the third polyimide layer 26, a core layer 25 is in the fourth polyimide layer 22, and a cladding 31 is in the fifth polyimide layer 30, over the region irradiated with the electron beam. FIG. 24 is a sectional view of the subject portion of a polyimide optical waveguide having a six-layer structure, wherein a sixth polyimide layer 30 is formed on the fifth polyimide layer 28 of the waveguide of FIG. 20. The sixth layer 30 has a refractive index lower than that of the fifth layer. A core 24 is formed in the polyimide layer 21 by applying an electron beam to the upper side of the sixth polyimide layer 30. A cladding 23 is formed in the polyimide layer 20, a core 25 is in the polyimide layer 22, a cladding 27 is in the polyimide layer 26, a core 29 is in the fifth polyimide layer 28, and a cladding 31 is in the sixth polyimide layer 30. The step of manufacturing the cores and the claddings of the waveguide shown in FIG. 24 will be explained with reference to FIG. 25. The first to fifth layers of this embodiment are formed in the same way as the layers of the polyimide optical waveguide (FIG. 21) having a five-layer structure are formed in steps A to E shown in FIG. 21. The step F shown in FIG. 25 is the step of forming the sixth polyimide layer 30 having a refractive index lower than that of the polyimide layer 28, on the fifth polyimide layer 28. An electron beam is applied to the upper side of the sixth polyimide layer 30 and hence to the substrate 10, in step G shown in FIG. 25. As a result, the core 24 is formed in the polyimide layer 21, the cladding 23 is in the second polyimide layer 20, the core 25 is in the third polyimide layer 22, the cladding 27 is in the fourth polyimide layer 26, the core 29 is in the fifth polyimide layer 28, and the cladding 31 is in the sixth polyimide layer 30, over the region irradiated with the electron beam. Next, another non-inventive example of a polyimide optical waveguide having a six-layer structure will be described with reference to the sectional view of FIG. 26. The first to fifth layers of this embodiment are formed in steps A to E shown in FIG. 27 in the same way as the fist to fifth layers of the polyimide optical waveguide (FIG. 22) having a five-layer structure are formed in steps A to E shown in FIG. 23. The step F shown in FIG. 27 shows the step of forming the sixth polyimide layer 28 having a refractive index higher than that of the polyimide layer 30, on the fifth polyimide layer 30. An electron beam is applied to the upper side of the sixth polyimide layer 28 and hence to the substrate 10 in step G shown in FIG. 27. As a result, the cladding 23 is formed in the polyimide layer 20, the core 24 is in the second polyimide layer 21, the cladding 27 is in the third polyimide layer 26, the core 25 is in the fourth polyimide layer 22, the cladding 31 is in the fifth polyimide layer 30, and the core 29 is in the sixth polyimide layer 28, over the region irradiated with the electron beam. FIG. 28 is a sectional view of the subject portion of a polyimide optical waveguide having a seven-layer structure, wherein a seventh polyimide layer 32 is formed on the sixth layer 28 of the waveguide of FIG. 26. The seventh layer 28 has a refractive index lower than that of the sixth layer 28. The cladding 23 is formed in the polyimide layer 20 by irradiating the upper side of the seventh polyimide layer 32 with an electron beam. The core 24 is formed in the polyimide layer 21, the cladding 27 is in the polyimide layer 26, the core 25 is in the polyimide layer 22, the cladding 31 is in the fifth polyimide layer 30, the core 29 is in the sixth polyimide layer 28, and the cladding 33 is in the seventh polyimide layer 32. The step of manufacturing the cores and claddings of the waveguide shown in FIG. 28 will be described with reference to FIG. 29. The first to sixth layers of this embodiment are formed in steps A to F shown in FIG. 27 in the same way as the first to sixth layers of the polyimide optical waveguide (FIG. 26) having a six-layer structure. The step G shown in FIG. 29 shows the step of forming the seventh polyimide layer 32 having a refractive index lower than that of the sixth layer, on the sixth polyimide layer 28. An electron beam is applied to the upper side of the seventh polyimide layer 32 and hence to the substrate 10, in step H shown in FIG. 29. As a result, the cladding 23 is formed in the polyimide layer 20, the core 24 is in the second polyimide layer 21, the cladding 27 is in the third polyimide layer 26, the core 25 is in the fourth polyimide layer 22, the cladding 31 is in the fifth polyimide layer 30, the core 29 is in the sixth polyimide layer 28, and the cladding 33 is in the seventh polyamide layer 32. As mentioned above, the present invention provides a improved polyimide optical waveguide having two or three polyimide layers, and also a method of manufacturing the waveguide in which any core and any cladding are formed alternately in a predetermined region of each layer.

Claims: A polyimide optical waveguide comprising a polyimide core (12) and a polyimide cladding (11, 14) in contact with said polyimide core (12), said polyimide core (12) having a refractive index higher than that of said polyimide cladding (11, 14), said polyimide cladding (11, 14) comprising a two-layer structure formed of a first polyimide layer (11) and a second polyimide layer (14) having the same refractive index as that of the first polyimide layer (11) and stacked on the first polyimide layer (11), characterized in that said core (12) is formed in one of the first polyimide layer (11) and the second polyimide layer (14) by selectively irradiating an electron beam on said polyimide cladding (11, 14), to form an embedded channel waveguide. A polyimide optical waveguide comprising a polyimide core (24, 25) and a polyimide cladding (20, 21, 22, 23) in contact with said polyimide core (24, 25), said polyimide core (24, 25) having a refractive index higher than that of said polyimide cladding (20, 21, 22, 23), characterized in that said cladding comprises a two-layer structure formed of a first polyimide layer (21, 22), a second polyimide layer (20) having a lower refractive index than that of said first polyimide layer (21, 22) and stacked on the first polyimide layer (21, 22), in that said polyimide core (24, 25) is formed in said first polyimide layer (21, 22) by selectively irradiating an electron beam on said polyimide cladding (21, 22), and in that a first raised-index polyimide cladding region (23) is formed in the second polyimide layer (20), beneath the polyimide core (24, 25) formed in the first polyimide layer (21, 22), said first raised-index polyimide cladding region (23) having a refractive index greater than that of the adjacent parts of the second polyimide layer (20) and formed by the same electron beam irradiation process used to form the polyimide core (24, 25), thereby forming a channel waveguide. The polyimide optical waveguide according to claim 2, further comprising a third polyimide layer (26) formed on the opposite side of said first polyimide layer (22) from said second polyimide layer (20), said third polyimide layer (26) having a refractive index lower than that of said polyimide core (25) and including a second raised-index polyimide cladding region (27) formed above the polyimide core (25), said second raised-index polyimide cladding region (27) having a refractive index greater than that of adjacent regions of the third polyimide layer (26) and formed by the same electron beam irradiation process used to form the polyimide core (25), thereby forming an embedded channel waveguide.

Inventors: ANDO SHINJI, MARUO YASUKO, MATSUI SHINSUKE, MATSUURA TOHRU, SHIGEKUNI SASAKI, TAMAMURA TOSHIAKI, YAMAMOTO FUMIO, ANDO, SHINJI, MARUO, YASUKO, MATSUI, SHINSUKE, MATSUURA, TOHRU, SHIGEKUNI, SASAKI, TAMAMURA, TOSHIAKI, YAMAMOTO, FUMIO
Applicants: NIPPON TELEGRAPH & TELEPHONE, NIPPON TELEGRAPH AND TELEPHONE CORPORATION
Application year: 1994
Main classification: G02B6
IPC codes: G02B6, G02B1