Cable wrapping

Abstract: The invention relates to the use of a conductive fiber cloth comprising a conductive fibrous material and optionally a water-swellable material and/or a non-conductive, optionally reinforcing, fibrous material, which water-swellable material is provided on and/or in the fiber cloth, as cable wrapping, for providing conductance, shielding, or a combination of the two, in a cable.

Description: This invention relates to the manufacture of cables and more specifically to the use of electrically conductive cable wrapping in the manufacture of cables. The use of conductive wrappings in cables is known. In the manufacture of power cables, conductive wrapping is used in the screen range, in order to provide for a good electrical contact between the core screen, the metal screen and the metal water barrier, if any is present. In this type of cable wrapping it is only important that volume conductivity is provided in the wrapping. Well known are types of cable wrapping which are built up from a fibrous web (non-woven) which has been impregnated with conductive carbon black. In particular in the case where the wrapping must impart to the cable not only conductive properties but also longitudinal water impermeability, a problem arises in that in such cases the conductive properties sometimes come out insufficiently. A disadvantage of the use of conductive carbon black is that carbon black is noble in comparison with the metals which are present in cables. This means that galvanic corrosion of conductors and/or the screen can arise, which is undesirable. The object of the invention is to provide a conductive cable wrapping, which may optionally comprise a water-swellable material, to which wrapping have been imparted in a simple manner suitable conductive properties, such as volume conductance and optionally shielding, while a number of disadvantages of the prior art do not arise or arise to a minor extent only. The invention is based inter alia on the surprising insight that it is possible to provide a network by which electrical conduction and optionally shielding are obtained in a cable by the use of conductive fibers, for instance in the form of a blend of non-conductive fibers and conductive fibers, optionally in combination with a water-swellable material, or by an assembly of a conductive and a non-conductive cloth which have been bonded onto each other. The invention accordingly relates inter alia to the use of a conductive fiber cloth, as defined in claim 1. Surprisingly, it has been found that such a laminated conductive cloth is highly suitable for imparting conductive and optionally shielding properties to power cable. By the use of conductive fibers in the wrapping, the undesired galvanic corrosion caused by carbon black does not arise or arises to a minor extent only, since the conductive wrapping comprises metal fibers which are not nobler than the conductor and/or the shield, so that the conductor is not affected by galvanic corrosion. According to the invention, a number of embodiments of the (conductive) cable wrapping can be used for power cable, comprising swellable material or not. The invention relates in a first embodiment to the use of a laminate comprising at least one non-conductive or substantially non-conductive fiber cloth and at least one conductive fiber cloth provided on at least one side of the support material, with fibers of the conductive cloth optionally having been carried through the non-conductive fiber cloth into electrically conductive contact with the other side of that fiber cloth, as cable wrapping for providing volume conductance and optionally shielding, in the screen area of a power cable. The invention further relates to a layered system or laminate, comprising at least one non-conductive or substantially non-conductive fiber cloth and at least one conductive fiber cloth provided on at least one side of the support material, with fibers of the conductive cloth optionally having been carried through the non-conductive fiber cloth into electrically conductive contact with the other side of that fiber cloth, which assembly further comprises a material swellable in or by water ("superabsorber"). The invention also relates to a power or signal cable manufactured utilizing said laminate. Surprisingly, it has been found that a cable wrapping which is built up from conductive and non-conductive fibers is highly suitable for providing the desired conductive and shielding properties in a cable, optionally in combination with a good longitudinal water impermeability. Also, the invention solves the problem of galvanic corrosion resulting from the use of conductive carbon black. Finally, it can be advanced as an advantage that the manufacture of the cable wrapping is much simpler and hence cheaper in a number of cases, because it is often sufficient to use materials which are in fibrous form, so that the cloth (fibrous web) can be manufactured in a single passage. An advantage of the elimination of the use of conductive carbon black is that no additional treatment step is necessary, while at the same time the contamination resulting from the use of carbon black does not arise. The cable wrapping used according to the invention can comprise a combination of non-conductive, optionally reinforcing, fibers, conductive fibers and a water-swellable material. These three components are present in a laminate. As already indicated in the introduction, it is preferred, for the purpose of the power cable, to use a thick wrapping which is properly conductive and, if desired, swells properly upon access of water. For this use, a laminate does provide the desired thickness, whereas also the extent of swelling is better than with single-layer systems. It is noted that the invention, in respect of the use of multilayer systems, is not limited to the presence of a water-swellable material. The cable wrapping which is used according to the invention comprises conductive fibers, in combination with the fibrous materials normally used. It is preferred to use a non-conductive or substantially non-conductive support material with a conductive fiber cloth provided thereon, with the conductive fibers being carried through the support material, for instance by needling. In this manner, conductance is obtained throughout the material. The cable wrapping so manufactured thus acquires a good volume conductance. The conductive fibers to be used in the fiber cloths to be used according to the invention are the known conductive fibers. Examples include metallized fibers and metal fibers, or fibers comprising conductive additives. When the fiber cloth consists wholly or partly of metal fibers, the metals for the fibers may be selected from the conductive metals and alloys thereof. Examples of suitable metals are steel, aluminum, copper and nickel. When using metallized fibers, it is preferred to use fibers which have been metallized with nickel, aluminum, steel, chromium, zinc, tin, copper or silver, with alloys based on one or more of these metals, or with two or more of these metals in succession. A suitable type of fiber is an acrylic fiber which has been metallized first with copper and then with nickel. The length of the conductive fibers can vary within wide limits, depending inter alia on the equipment to be used. To obtain a good conductance, the length is preferably 40-70-mm. The conductive fibers preferably have an aspect ratio of 500 or more. It will typically be in the neighborhood of 4000-5000. The amount of conductive fibers should be sufficient to provide the desired electrical properties. This can be determined on the basis of simple experiments. It has been established that for obtaining a good volume conductance, the absolute amount of conductive fibers is of importance, whilst for shielding, the amount per unit thickness is more relevant. Depending on the use, the amount of conductive fibers can be between 0.1 and 100 g/m 2 , starting from metallized plastic fibers. For other types of fibers, these amounts can be different, depending on weight and conductivity. The skilled worker can determine the desired amounts in a simple manner through routine experiments. For power cable the amount referred to will preferably be between 0.1 and 20 g/m 2 , more particularly between 0.25 and 15 g/m 2 , it being noted that the lower limit is mainly determined by the minimum desired conductance for the operation of the cable wrapping, whilst the upper limits have been set at values above which generally no additional advantages for the conductance are to be expected. Suitable amounts can accordingly be determined on the basis of a few tests. As a guideline, amounts from about 5-g/m 2 up to amounts of about 100 g/m 2 could be considered. The fibers to be used for the non-conductive fibrous material include, in particular, acrylic fibers, polyester fibers, glass fibers, carbon fibers, polyamide fibers and aramid fibers. Of course, the choice of the fibers is partly determined by the temperatures and the mechanical load which the materials should be able to withstand during manufacture and use. The conductive fibers, too, can be manufactured from these raw materials, in case fibers are used which have been rendered conductive through metallization or additives. The cable wrapping, or the support material in the cable wrapping, which is used according to the invention consists of a fiber cloth or a combination of cloths. Such fiber cloths can be wovens, knitted fabrics, nonwovens which may or may not be reinforced, etc. In the case where a monolayer system based on metal fibers, non-conductive fibers and water-swellable material, such as swelling powder, is used, it is preferred that the cable wrapping is a non-woven material. Fiber cloths provided with microbeads which may or may not be expanded can also be advantageously rendered electrically conductive in accordance with the invention. The formation of the cloths to be used according to the invention can be realized with all known techniques for fabricating a fibrous cloth, more particularly a non-woven. In the fabrication of non-wovens, virtually any desired dose can be set accurately and with a uniform distribution by blending conductive fibers with other fibers. This method moreover provides the advantage that the web is fabricated in a single passage through the machine, which constitutes a clear saving. A practical method for the fabrication of a fibrous web which can be used in accordance with the invention, which method provides a uniform fiber distribution, is, for instance, the fabrication of a card web. The web can be bonded thermally, chemically or mechanically. The fabrication of a laminate can be realized as follows. A card web as described hereinabove is anchored, for instance by needling, stitching, adhesion or welding, in and through the support material. This anchoring can be obtained, for instance, by means of needling machines or hydro-entanglement plants. Also, by stitching electrically conductive yarns/wires/filaments through the reinforcement material, the armor could be made electrically conductive. All anchoring methods where conductive fibers extend through the reinforcement material are suitable. It is also possible to use a knitting or weaving technique, whereby a so-called 2-1/2- or 3-dimensional knitted fabric or woven fabric is obtained, provided that an electrically conductive wire or yarn is utilized through the cloth. Chemical anchoring can be effected by treatment with a binder, whilst thermal anchoring is effected with a suitable type of fiber or powder. As stated, the invention also encompasses the use of a cable wrapping comprising water-swellable material, such as swelling powder or swelling fibers. By the use of such water-swellable materials in a wrapping, the cable acquires longitudinal water impermeability, since the swelling material, upon contact with water, closes off the remainder of the cable, thereby preventing further penetration of water along the length of the cable. The use of such water-swellable materials for obtaining longitudinal water impermeability in cable wrapping is already known, though not in combination with the conductive fibers used according to the present invention. Current water-swellable materials are swelling fibers and swelling powder, as described in Jicable 1991, Communication A.7.1, R.S. de Boer and P. Vogel, "The use of waterswellable materials in the design of power cables". Hereinafter the invention will be further described and illustrated in and by a number of examples, without being limited thereto. Example 1 A fibrous web comprising 10-wt.% of coppered and nickeled acrylic fiber was applied to a swelling web (3E116/Firet¬ Cable wrapping) through needling. The properties of the material obtained are summarized in Table 1. Weight (g/m 2 ) 228 Thickness (mm) 2.1 Tensile strength (N/cm) 20 Elongation (%) 12 Swelling capacity (mm) 17 Swelling speed (mm/1st min) 5 Volume resistance (Ω) <1.0 Example 2 A card web of a weight of 20 g/m 2 was placed and needled on a polyester spunbond of about 70 g/m 2 . The card web contains about 65-wt.% metallized fibers (coppered and nickeled acrylic fiber) and about 35-wt.% unstretched polyester fibers. The needled composite material is then calendered, whereby the density of the product is strongly increased. In the same manner as described hereinabove, a product is fabricated comprising about 20 wt.% metallized fibers in the card web of 20 g/m 2 . The shielding action of the two webs is shown in Table 2. Shielding (dB) Content of 400 600 800 1000 metallized fiber in 20 g/m 2 card web MHz MHz MHz MHz 65-g/m 2 47 47 52 50 20-g/m 2 32 32 37 35 Examples 3 and 4 A number of conductive swelling webs were applied to a spunbond support of 25-g/m 2 by needling. In the first series of tests a conductive swelling web was used comprising 99-wt.% superabsorbing fiber based on acrylic fiber and 1-wt.% coppered and nickeled acrylic fiber (Table 3). In the second series of tests, this ratio was 90/10 (Table 4). In both series of tests, the amount of needled-on conductive swelling web was varied. Tables 3 and 4 show the results. Weight g/m 2 Thickness mm Dens. g/cm 3 Vol. res. Ω Swell sp. 1 min (mm/min) Swell height mm 90 0.26 0.346 7 3.9 4.0 104 0.25 0.416 15 4.8 5.4 106 0.26 0.408 19 4.8 5.0 118 0.26 0.454 7 5.4 6.0 118 0.27 0.437 30 5.4 6.0 Weight g/m 2 Thickness mm Dens. g/cm 3 Vol.res. Ω Swell speed 1 min (mm/min) Swell height mm 86 0.23 0.374 1.3 3.7 3.9 100 0.25 0.400 1.3 3.9 4.1 114 0.27 0.422 1.3 4.2 4.4 116 0.28 0.414 1.3 4.0 4.3 120 0.29 0.414 1.3 4.3 4.5 120 0.27 0.444 1.3 4.3 4.5 122 0.27 0.452 1.3 4.2 4.5 126 0.29 0.434 1.3 4.5 5.2 132 0.26 0.508 1.3 4.1 4.5 132 0.27 0.489 1.3 4.1 4.5

Claims: Use of a laminate comprising at least one conductive fibre cloth comprising metal fibres or metallized fibres, and at least one non-conductive or substantially non-conductive fibre cloth, said at least one conductive fibre cloth being provided on at least one side of said non-conductive or substantially non-conductive fibre cloth, with metal fibres or metallized fibres of the conductive fibre cloth having been carried through said one non-conductive or substantially non-conductive fibre cloth into electrically conductive contact with the other side of the of the said non-conductive or substantially non-conductive fibre cloth, for providing low electrical volume resistance in the screen range of power cable. Use according to claim 1, wherein further a water swellable material is present in the laminate. Use according to claim 2, wherein said water swellable material is chosen from swelling powders and swelling fibres. Use according to claims 1-3, wherein the metallised fibres are metallised with nickel, aluminium, steel, copper, chromium, zinc, tin, silver or alloys thereof. Use according to claims 1-4, wherein the conductive fibre cloth further comprises reinforcing fibres, preferably selected form the group of glass fibres, polyester fibres, carbon fibres, polyamide fibres, aramid fibres, acrylic fibres and blends thereof. Power cable containing in the screen range a laminate as defined in any one of the claims 1-5.

Inventors: BOER RINTSJE SYBOLT DE, BOVENSCHEN DIRK ALBERTUS, VOGEL PETRUS GOVARDUS JOHANNES, BOVENSCHEN, DIRK ALBERTUS, DE BOER, RINTSJE SYBOLT, VOGEL, PETRUS GOVARDUS JOHANNES
Applicants: LANTOR BV, LANTOR B.V.
Application year: 1994
Main classification: H01B1
IPC codes: D04H13, H01B11, H01B1, H01B3, H01B7, G02B6