Mixed surfactant system as a durable fabric coating

Abstract: A composition for increasing the resistance to removal by an aqueous liquid of surfactants from a polymeric fabric including fibers having a plurality of fiber-fiber interstices at junctions of two or more fibers. The composition includes water, a first surfactant, and a second surfactant which is structurally dissimilar to and less soluble in water than the first surfactant. One of the first and second surfactants has a solubility in water at 20°C no greater than about 5 percent by weight, based on the weight of the water. In certain embodiments, the first and second surfactants are adapted to preferentially locate in the fiber-fiber interstices and resist removal therefrom by aqueous liquid. The preferential location of the surfactants in the fiber-fiber interstices of the fabric is accomplished by working the fabric after application of the composition to the fabric. The resulting fabric is wettable and demonstrates increased resistance to removal of surfactants by an aqueous liquid, compared to similar fabrics which have not been worked. The wettable fabrics are especially suited for incorporation in such disposable absorbent articles as diapers, feminine care products, such as sanitary napkins and tampons, incontinent care products, training pants, wipes, and the like.

Description: The present invention relates to a mixed surfactant system. Polymers are used extensively to make a variety of products which include blown and cast films, extruded sheets, injection molded articles, foams, blow molded articles, extruded pipe, monofilaments, and nonwoven webs. Some of such polymers, such as polyolefins, are naturally hydrophobic, and for many uses this property is either a positive attribute or at least not a disadvantage. There are a number of uses for polymers, however, where their hydrophobic nature either limits their usefulness or requires some effort to modify the surface characteristics of the shaped articles made therefrom. By way of example, hydrophobic polymers, such as polyolefins, are used to manufacture polymeric fabrics which are employed in the construction of such disposable absorbent articles as diapers, feminine care products, incontinent products, training pants, wipes, and the like. Such polymeric fabrics often are nonwoven webs prepared by, for example, such processes as meltblowing, coforming, and spunbonding. Frequently, such polymeric fabrics need to be wettable. Wettability can be obtained by spraying or otherwise coating (i.e., surface treating or topically treating) the fabric with a surfactant solution during or after its formation, and then drying the web. Some of the more common topically applied surfactants are nonionic surfactants, such as polyethoxylated octylphenols and condensation products of propylene oxide with propylene glycol by way of illustration only. These surfactants are effective in rendering normally hydrophobic polymeric fabrics wettable. However, the surfactant is readily removed from the fabric, often after only a single exposure to an aqueous liquid. Substantial efforts have been directed to increasing the durability of surfactants which are topically applied to a polymeric fabric. Such efforts include the following, by way of illustration: (1) use of a composition which includes water, a primary surfactant, and a cosurfactant which is functional to wet the fabric with the composition and which provides for substantially uniform distribution of the primary surfactant onto the polymeric fabric; (2) use of a surfactant, with or without a nonionic cosurfactant, which is the reaction product of an acid anhydride derivative, such as a substituted succinic anhydride, with a polyhydroxy compound, such as sorbitol, a polyethylene glycol, triethanolamine, a polyhydroxyamine, certain primary and secondary amines, and certain unsaturated aliphatic sulfo compounds; (3) use of a surfactant, with or without a nonionic cosurfactant, which is the reaction product of certain unsaturated aliphatic sulfo compounds with the reaction product of an acid anhydride derivative, such as a substituted succinic anhydride, with a polyamine having at least one NH group capable of addition to a double bond; (4) use of a surfactant mixture which includes an ester-acid, ester salt, or a mixture thereof, and an amidic-acid, amidic salt or mixture thereof with or without a nonionic cosurfactant; and (5) use of a surfactant mixture which includes a sorbitol succinate surfactant, such as an ethoxylated amino sorbitol succinate salt or an alkenyl succinate anhydride ethoxylated fatty amine salt, and a cowetting aid which can be, for example, a silicone polyether or a primary or secondary alcohol having up to about 8 carbon atoms. Notwithstanding the advances which have been made in rendering topically applied surfactants more durable on a polymeric fabric, i.e., more resistant to removal by an aqueous liquid, there still is a need for further improvement. Summary of the Invention It therefore is an object of the present invention to provide a composition for increasing the resistance to removal by an aqueous liquid of surfactants from a polymeric fabric. It also is an object of the present invention to provide a method for increasing the wettability of a polymeric fabric by the application of surfactants thereto with a concomitant increase in the resistance to removal of the surfactants from the polymeric fabric by an aqueous liquid. It is a further object of the present invention to provide a wettable polymeric fabric to which surfactants have been applied, which surfactants are resistant to removal by an aqueous liquid. It is another object of the present invention to provide a disposable absorbent article, at least one component of which is a wettable polymeric fabric to which surfactants have been applied, which surfactants are resistant to removal by an aqueous liquid. These and other objects will be apparent to those having ordinary skill in the art from a consideration of the specification and claims which follow. Accordingly, the present invention provides a composition for increasing the resistance to removal by an aqueous liquid of surfactants from a polymeric fabric composed of fibers having a plurality of fiber-fiber interstices at junctions of two or more fibers, according to claims 1 to 8. The present invention further provides a method for increasing the wettability of a polymeric fabric by the application of surfactants thereto with a concomitant increase in the resistance to removal of the surfactants from the polymeric fabric by an aqueous liquid, which method includes providing a polymeric fabric having a surface and composed of fibers having a plurality of fiber-fiber interstices at the junctions of two or more fibers; applying to the surface of the polymeric fabric a composition, as already defined. The present invention additionally provides a wettable polymeric fabric to which surfactants have been applied, which surfactants are resistant to removal by an aqueous liquid, which fabric includes fibers having a plurality of fiber-fiber interstices at the junctions of two or more of the fibers and a composition as already defined. In certain embodiments of the method of the present invention, the fabric is worked after the surfactant composition has been applied. The present invention also provides a disposable absorbent article, at least one component of which is the wettable polymeric fabric as described above. Examples of disposable absorbent articles include diapers; feminine care products, such as sanitary napkins and tampons; incontinent products; training pants; and wipes. In certain embodiments, the first and second surfactants are adapted, upon working of a polymeric fabric to which the composition has been applied, to preferentially locate in the fiber-fiber interstices and resist removal therefrom by an aqueous liquid. According to the invention, the first surfactant has a linear structure and the second surfactant has a comb-like structure. The first and second surfactants are polysiloxane polyethers. In preferred embodiments, each of the first and second surfactants has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water. In still other embodiments, the first surfactant has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water, and the second surfactant is essentially insoluble in water at 20°C. In yet other embodiments, the first and second surfactants are present in a ratio by weight of the first surfactant to the second surfactant which is in a range of from about 10:1 to about 1:2. In still further embodiments, the fibers of the polymeric fabric are composed of polyolefin fibers. Brief Description of the Drawings FIGS. 1 and 2 are three-dimensional plots of the maximum number of wash cycles achieved without losing wettability versus percent surfactant lost for five polymeric fabric samples having different surfactant compositions applied to the fabric with and without working, respectively. FIGS. 3-5 are plots of wash cycle versus percent surfactant lost for three different surfactant compositions applied to the fabric with and without a subsequent working step. FIG. 6 is a three dimensional plot which combines the data of FIGS. 1 and 2. FIG. 7 is a scanning electron photomicrograph of wettable polymeric fabric prepared in accordance with one embodiment of the present invention. FIG. 8 is a silicon map demonstrating the preferential location of surfactants in the fiber-fiber interstices of the polymeric fabric of FIG. 7. Detailed Description of the Invention As used herein, the term "polymeric fabric" means a fabric prepared from any polymeric material capable of being formed into a fabric. Thus, such material can be synthetic or natural, although the former are more likely to be employed in the present invention. Examples of natural polymeric materials include, cotton, silk, wool, and cellulose, by way of illustration only. Synthetic polymeric materials, in turn, can be either thermosetting or thermoplastic materials, with thermoplastic materials being more common. Examples of thermosetting polymers include, by way of illustration only, alkyd resins, such as phthalic anhydride-glycerol resins, maleic acid-glycerol resins, adipic acid-glycerol resins, and phthalic anhydride-pentaerythritol resins; allylic resins, in which such monomers as diallyl phthalate, diallyl isophthalate diallyl maleate, and diallyl chlorendate serve as nonvolatile cross-linking agents in polyester compounds; amino resins, such as aniline-formaldehyde resins, ethylene urea-formaldehyde resins, dicyandiamide-formaldehyde resins, melamine-formaldehyde resins, sulfonamide-formaldehyde resins, and urea-formaldehyde resins; epoxy resins, such as cross-linked epichlorohydrin-bisphenol A resins; phenolic resins, such as phenol-formaldehyde resins, including Novolacs and resols; and thermosetting polyesters, silicones, and urethanes. Examples of thermoplastic polymers include, by way of illustration only, end-capped polyacetals, such as poly(oxymethylene) or polyformaldehyde, poly(trichloroacetaldehyde), poly( n -valeraldehyde), poly(acetaldehyde) and poly-(propionaldehyde); acrylic polymers, such as polyacrylamide, poly(acrylic acid), poly(methacrylic acid), poly(ethyl acrylate) and poly(methyl methacrylate); fluorocarbon polymers, such as poly(tetrafluoroethylene), perfluorinated ethylene-propylene copolymers, ethylene-tetrafluoroethylene copolymers, poly(chlorotrifluoroethylene), ethylene-chlorotrifluoroethylene copolymers, poly(vinylidene fluoride) and poly(vinyl fluoride); polyamides, such as poly(6-aminocaproic acid) or poly(∈-caprolactam), poly-(hexamethylene adipamide), poly(hexamethylene sebacamide) and poly(11-amino-undecanoic acid); polyaramides, such as poly(imino-1,3-phenylene-iminoisophthaloyl) or poly( m -phenylene isophthalamide); polyarylenes. such as poly- p -xylylene and poly(chloro- p -xylylene); polyaryl ethers, such as poly(oxy-2,6-dimethyl-1,4-phenylene) or poly( p -phenylene oxide); polyaryl sulfones, such as poly(oxy-1,4-phenylenesulfonyl-1,4-phenyleneoxy-1,4-phenylene-isopropylidene-1,4-phenylene) and poly(sulfonyl-1,4-phenyleneoxy-1,4-phenylenesulfonyl-4,4'-biphenylene); polycarbonates, such as poly(bisphenol A) carbonate or poly(carbonyldioxy-1,4-phenyleneisopropylidene-1,4-phenylene); polyesters, such as poly(ethylene terephthalate), poly-(tetramethylene terephthalate), poly(cyclohexylene-1,4-dimethylene terephthalate) or poly(oxymethylene-1,4-cyclohexylenemethyleneoxyterephthaloyl); polyaryl sulfides, such as poly( p -phenylene sulfide) or poly(thio-1,4-phenylene); polyimides, such as poly(pyromellitimido-1,4-phenylene); polyolefins, such as polyethylene, polypropylene, poly(1-butene), poly(2-butene), poly(1-pentene), poly(2-pentene), poly(3-methyl-1-pentene), poly(4-methyl-1-pentene), 1,2-poly-1,3-butadiene, 1,4-poly-1,3-butadiene, polyisoprene, polychloroprene, polyacrylonitrile, poly(vinyl acetate), poly(vinylidene chloride) and polystyrene; copolymers of the foregoing, such as acrylonitrile-butadiene-styrene (ABS) copolymers. In certain embodiments, the polymeric fabric will be prepared from a polyolefin. In other embodiments, the polyolefin will be polypropylene. The term "fabric" is used broadly herein to mean any fibrous material which has been formed into a sheet or web. That is, the fabric is composed, at least in part, of fibers of any length. Thus, the fabric can be a woven or nonwoven sheet or web, all of which are readily prepared by methods well known to those having ordinary skill in the art. For example, nonwoven webs are prepared by such processes as meltblowing, coforming, spunbonding, and carding. Moreover, the fabric can consist of a single layer or multiple layers. When multiple layers are present, only one needs to be fibrous. Thus, a multilayered fabric can include films, scrim, and other materials which do not have the requisite fiber-fiber interstices, described below. Regardless of whether the fabric is a woven or nonwoven fabric, the fibers of which the fabric is at least in part composed touch and/or cross in a plurality of locations. The spaces associated with these locations are referred to herein as "fiber-fiber interstices." Thus, the polymeric fabric has a plurality of fiber-fiber interstices. The spaces or interstices begin at the point where the fibers touch and extend outwardly or away from such point for a short distance along each fiber forming the interstice. Such distance is not fixed and can vary from interstice to interstice. As a practical matter, however, the distance generally can be up to perhaps ten times the diameter of the fibers involved in forming the interstices, with three or four times the diameters of the fibers being more typical. The composition of the present invention is as defined in claims 1 to 8. The second surfactants will have a solubility in water at 20°C which is no greater than 5 percent by weight, based on the weight of the water. In certain embodiments, the first and second surfactants are present in a ratio by weight of first surfactant to second surfactant which is in a range of from about 10:1 to about 1:2. In other embodiments, the ratio of first surfactant to second surfactant is in a range of from about 5:1 to about 1:1. In still other embodiments, the first and second surfactants are adapted, upon working of polymeric fabric to which the composition has been applied, to preferentially locate in the fiber-fiber interstices and resist removal therefrom by aqueous liquid. Simply stated, this means that the force which leads to or favors dissolution or dispersion of the surfactants in an aqueous liquid is less than the forces which favor retention of the surfactants on the surface of the fabric (i.e., on the surfaces of the fibers of which the polymeric fabric is composed) and/or in the fiber-fiber interstices of the fabric. At least three primary forces are believed to be involved. The first is the entropy or driving force of dissolution and dispersion. Entropy, it will be remembered, is a function of the state of a system. Its value depends upon the condition of the system and not upon its past history. For an infinitesimal reversible process, the entropy change dS is given by dS = dq rev /T where dq rev is the heat absorbed from the surroundings and T is the absolute temperature. For a process that occurs spontaneously, the entropy change is greater than the heat change divided by the absolute temperature. That is, dS > dq rev /T For a surfactant to render the polymeric fabric wettable by an aqueous liquid, at least some of the surfactant must dissolve spontaneously in the aqueous medium in order to lower the surface tension of the aqueous medium to a value which is equal to or less than that of the fabric. Thus, it is evident that equation 2 must control. However, the durability of a surfactant on the polymeric fabric, i.e., the ability of the surfactant to resist removal by an aqueous liquid, is inversely proportional to the value of dS. Stated differently, the more soluble a surfactant is in an aqueous liquid, the greater will be the value of dS for a given value of dq rev . It is for these reasons that at least the second surfactant has a solubility in water at 20°C which is no greater than 5 percent by weight, based on the weight of the water. In certain embodiments, each of the first and second surfactants has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water. In other embodiments, the first surfactant has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water, and the second surfactant is essentially insoluble in water. The second force is the force of adhesion or attraction of the surfactants on the fibers. This force is a function of the molecular attractions between the surfactants and the polymer of which the fabric is composed, e.g., dipole-dipole and van der Waals forces. The second force alone can counter the first force and, if sufficiently strong, can result in a relatively durable coating. The third is a capillary force which results from the formation of fiber-fiber interstices; it is a function of the surface tension of each surfactant and is in part responsible for the preferential movement of surfactant to the fiber-fiber interstices. The second and third forces work together to keep the surfactants in the fiber-fiber interstices, in opposition to the first force. The balancing of these three forces is what is meant by the phrase, "preferentially locate in the fiber-fiber interstices and resist removal therefrom by aqueous liquid." That is, the first and second surfactants are selected in some embodiments to provide strong second and third forces, in comparison to the first force. One factor in so doing, as noted above, is to select surfactants having limited solubilities in water. As already stated, the first and second surfactants are linear and comb-like, respectively, by "comb-like" is meant a substantially linear backbone with at least two substituents which extend outwardly or away from the backbone. One of the first and second surfactants will have a linear structure. An example of a class of surfactants having a linear structure is what are commonly referred to as A-B-A polymers, in which A represents the moiety which imparts surfactant properties to the molecule and B represents the remainder of the molecule and often includes repeating units. Those having ordinary skill in the art will recognize that in many instances B can be represented as B'-C, in which C represents a group which links B' with A, and B' represents that portion of B which consists of repeating units. In other embodiments, one of the first and second surfactants is a polyether polysiloxane In still other embodiments, each of the first and second surfactants is a polyether polysiloxane. In certain embodiments, one of the first and second surfactants is an A-B-A polyether polysiloxane surfactant having general formula I, wherein: each of R 1 and R 6 independently is selected from the group consisting of hydrogen and C 1 -C 8 alkyl and aryl groups; each of R 2 -R 4 independently is selected from the group consisting of C 1 -C 8 alkyl and aryl groups; a represents an integer from about 8 to about 25; b represents an integer from about 8 to about 25; the ratio of b to a is in a range of from about 0.7 to about 1.5; c represents an integer from 1 to about 10; d represents an integer from about 40 to about 100; the ratio of d to two times the sum of a and b is in a range of from about 0.7 to about 1.5; and the number-average molecular weight of said first surfactant is in a range of from about 5,000 to about 35,000 . In other embodiments, each of R 1 and R 6 independently is selected from the group consisting of hydrogen and C 1 -C 3 alkyl and phenyl groups; each of R 2 - R 4 independently is selected from the group consisting of C 1 -C 3 alkyl and phenyl groups; a represents an integer from about 12 to about 18; b represents an integer from about 12 to about 18; the ratio of b to a is about 1; c represents an integer from about 2 to about 4; d represents an integer from about 50 to about 70; the ratio of d to two times the sum of a and b is about 1; and the number-average molecular weight of said first surfactant is in a range of from about 6,500 to about 18,500 . In yet other embodiments, each of R 1 and R 6 is hydrogen; each of R 2 - R 4 is a methyl group; a represents an integer which is about 15; b represents an integer which is about 15; c represents an integer which is 3; d represents an integer which is about 60; and the number-average molecular weight of the first surfactant is about 7,000. One of the first and second surfactants will have a comb-like structure. An example of a class of surfactants which has a comb-like structure is what are commonly referred to as (A-B) n polymers, in which A represents the moiety which imparts surfactant properties to the molecule and B represents the remainder of the molecule. In certain embodiments, one of the first and second surfactants is an (A-B) n polyether polysiloxane surfactant having general formula II, wherein: each of R 7 -R 16 independently is selected from the group consisting of C 1 -C 8 alkyl and aryl groups; R 17 is a C 10 -C 25 alkyl group; R 18 is hydrogen or a C 1 -C 4 alkyl group; e represents an integer from about 3 to about 15; f represents an integer from about 1 to about 6; g represents an integer from about 5 to about 30; the ratio off to g is in a range of from about 2 to about 10; h represents an integer from 1 to about 10; j represents an integer from about 4 to about 15; k represents an integer from about 1 to about 15; the ratio of j to k is in a range of from about 0.5 to about 4; and the number-average molecular weight of the second surfactant is in a range of from about 5,000 to about 60.000. In other embodiments, each of R 7 -R 16 independently is selected from the group consisting of C 1 -C 3 alkyl and phenyl groups; R 17 is a C 12 -C 20 alkyl group; R 18 is hydrogen or a C 1 -C 3 alkyl group; e represents an integer from about 3 to about 8; f represents an integer from about 2 to about 4; g represents an integer from about 10 to about 20; the ratio of f to g is in a range of from about 3 to about 8; h represents an integer from about 2 to about 4; j represents an integer from about 6 to about 12; k represents an integer from about 4 to about 8; the ratio of j to k is in a range of from about 1 to about 2; and the number-average molecular weight of the second surfactant is in a range of from about 7,000 to about 24,000 . In yet other embodiments, each of R 7 - R 16 is a methyl group; R 17 is a hexadecyl group; R 18 is hydrogen; e represents an integer which is about 5; f represents an integer which is about 3; g represents an integer which is about 15; h represents an integer which is 2; j represents an integer which is about 9; k represents an integer which is about 6; and the number-average molecular weight of the second surfactant is about 14,500. In certain additional embodiments, the first surfactant is an A-B-A polyether polysiloxane having general formula I and the second surfactant is an (A-B) n polyether polysiloxane having general formula II. While the description of the composition makes particular reference to a first surfactant and a second surfactant, such reference does not preclude the presence of more than two surfactant types, either in the composition or on the fibers of a polymeric fabric. In addition, either or both of the first surfactant and the second surfactant can include two or more surfactants. Moreover, the designation of the required two surfactants as first surfactant and second surfactant is for convenience only, and is not to be construed as limiting in any way the scope of the present invention. The levels of the first and second surfactants in the composition can vary over a wide range. In general, the level of the surfactants in the composition is a function of the amount of the surfactants which is desired to be added to the polymeric fabric. As a practical matter, the level of the surfactants in the composition typically will be in a range of from about 0.01 to about 3 percent by weight, based on the weight of water. Depending on the level of add-on desired, however, lower or higher levels can be employed. In certain embodiments, the level of surfactants in the composition will be in a range of from about 0.01 to about 1 percent by weight. The composition of the present invention described above is useful for increasing the wettability of a polymeric fabric by the application of surfactants thereto, with a concomitant increase in the resistance to removal of surfactant from the polymeric fabric by an aqueous liquid. The method for accomplishing such increases involves providing a polymeric fabric having a surface and composed of fibers having a plurality of fiber-fiber interstices at the junctions of two or more fibers, applying to the surface of the polymeric fabric a composition of the present invention as already described, and drying the polymeric fabric to which the composition has been applied. In the first step of the method of the present invention, a polymeric fabric is provided, which fabric has a surface and is composed of fibers having a plurality of fiber-fiber interstices at the junctions of two or more fibers. The polymeric fabric and its characteristics were described in detail earlier. The next step involves applying to the surface of the polymeric fabric a composition of the present invention as already described. In general, application of the composition can be by any means known to those having ordinary skill in the art. Such means include, by way of illustration only, dipping, doctor blading, spraying, and direct and offset gravure printing or coating. Drying of the treated polymeric fabric can be accomplished by any known means. Examples of known drying means include, by way of illustration only, convection ovens, radiant heat, infrared radiation, forced air ovens, and heated rolls or cans. Drying also includes air drying without the addition of heat energy, other than that present in the ambient environment. The polymeric fabric which is obtained after the drying step is wettable. Moreover, the surfactants are resistant to removal by an aqueous liquid. If desired, an additional step can be employed in order to increase the resistance of the surfactants to removal by an aqueous liquid. Such step involves working the polymeric fabric to which the composition has been applied to an extent sufficient to preferentially locate a substantial portion of the first and second surfactants in fiber-fiber interstices of the polymeric fabric. As used herein, the term "working" means subjecting the polymeric fabric to compressive forces after the surfactant composition has been applied thereto. Working can be carried out before, during, or after the drying step by any means which will subject the polymeric fabric to compressive forces. For example, the polymeric fabric can be passed through nip rolls, such as press or calendaring rolls. Alternatively, the polymeric fabric can be compressively sandwiched between a rotating drum or roll and an outer belt or web: the rotating drum or roll can be heated, if desired. Other methods will be apparent to those having ordinary skill in the art. The most effective means known for working the fabric involves simply subjecting the treated fabric to a compression step after the composition has been applied to a surface. The application of the composition to the surface and the subsequent working of the treated fabric are readily combined into a sequential operation, such as that involved in a dip-and-nip procedure. A dip-and-nip procedure has the added advantage of removing excess composition which reduces the energy and time required for the final drying step. When a working step is included, the surfactants preferentially are located in the fiber-fiber interstices at the junctions of two or more fibers. The amount of surfactants present on the polymeric fabric in general will be at least about 0.3 percent by weight, based on the weight of the polymeric fabric. As a practical matter, the amount of surfactant present typically will be in a range of from about 0.3 to about 5 percent by weight. In certain embodiments, the amount of surfactant present on the fabric will be in a range of from about 0.5 to about 3 percent by weight. In other embodiments, the amount of surfactant present on the fabric will be in a range of from about 0.7 to about 2 percent by weight. The wettable polymeric fabric of the present invention is well-suited as a component of a disposable absorbent article. Examples of disposable absorbent articles include, by way of illustration only, diapers; feminine care products, such a sanitary napkins and tampons; incontinent products; training pants; and wipes. The present invention is further described by the examples which follow. Such examples, however, are not to be construed as limiting in any way either the spirit or the scope of the present invention. In the examples, all parts are by weight, unless stated otherwise. Example 1 The polymeric fabric employed was a spunbonded polypropylene nonwoven web having a basis weight of about 1.6 ounces per square yard or osy (about 38 grams per square meter or g/m 2 ). A sample of the fabric 5 x 15 inches (about 13 x 38 cm) was weighed and placed in a 1-liter beaker containing 500 ml of a 0.1 percent by weight solution of surfactants in water. After 20 seconds, the sample was removed from the beaker and passed through an Atlas Laboratory Wringer with a 25-lb (11.4-kg) nip setting (Atlas Electric Devices Company, Chicago, Illinois). The sample was dried in a convection oven (Pro-Tronix® II, General Signal Company, Blue Island, Illinois) at about 85°C for about 20 minutes. The dried sample then was weighed and the add-on of surfactants calculated. Three surfactants were employed. The first, Surfactant A, was a linear polyether polysiloxane having the formula, The number-average molecular weight of the surfactant was about 7,000. It had a mean viscosity at 25°C of 1,850 centistokes and a mean specific gravity at the same temperature of 1.01 g/cm 3 . The second, Surfactant B, was a polyethoxylated octylphenol surfactant, Triton® X-102 (Rohm and Haas Co., Philadelphia, Pennsylvania). The third surfactant, Surfactant C, was a comb-like polyether polysiloxane having the formula, The number-average molecular weight of the surfactant was about 14,500. The material had a mean viscosity at 25°C of 900 centistokes and a mean specific gravity at 20°C of 0.93 g/cm 3 . The mean refractive index of the material at 20°C was 1.438. Those having ordinary skill in the art will recognize that Surfactant A is of the type of polyether polysiloxane represented by general formula I. Similarly, Surfactant C is of the type of polyether polysiloxane represented by general formula II. Significantly, neither of these surfactants is considered to be a surfactant for aqueous systems. This is especially true of Surfactant C. Several different combinations and ratios of surfactants were studied. The first combination consisted of a 3:1 ratio by weight of Surfactant A to Surfactant C (Sample A). The second combination consisted of a 1:1 ratio by weight of the same surfactants employed for Sample A (Sample B). The third combination consisted of a 1:1 ratio by weight of Surfactant B to Surfactant A (Sample C) (comparative). In addition, two controls were included and consisted of Surfactant A alone (Sample D) and Surfactant B alone (Sample E). Each fabric sample to which one or more surfactants had been added was washed by placing the sample in a 1-liter conical flask containing 500 ml of tap water at ambient temperature. The flask was stoppered, placed on a wrist-action shaker (Burrell Scientific, Pittsburgh, Pennsylvania), and gently shaken for one minute. The sample was removed from the flask, carefully squeezed by hand, and passed through a laboratory wringer having a nip setting of 25 lb (11.4 kg). The sample then was dried and weighed as described above. The percent surfactant lost was calculated as follows: Percent lost = 100 x [(g TPF - g PF) - (g WTPF - g PF)/(g TPF - g PF)] wherein "g TPF" refers to the dry weight of the treated polymeric fabric, "g PF" refers to the dry weight of the original fabric sample before treatment, and "g WTPF" refers to the dry weight of treated polymeric fabric which has been washed. The washing procedure was repeated until a sample no longer was wettable with water. As can be seen from the above equation, all percent surfactant lost calculations are cumulative. The wettability of each sample was estimated by placing drops of water on the sample and measuring the time required for complete penetration of the water drops into the fabric (referred to hereinafter as "wetting time" or "WT"). Each sample was tested with a minimum of five drops of water placed in five different locations. The time for all of the drops to penetrate into the sample was measured. The results are summarized in Table 1. In the table, "WT" represents the wetting time in seconds and "Lost" represents the cumulative percent surfactant lost after the stated number of washings. The initial add-on values in percent by weight also are given for each sample. Summary of Washing Results for Worked Samples Sample A Sample B Sample C Sample D Sample E % Add-on -----1.0----- -----0.9----- -----1.2----- -----1.1----- -----1.0----- Status WT Lost WT Lost WT Lost WT Lost WT Lost 1st Wash < 1 4 < 1 11 < 1 47 < 1 18 < 1 83 2nd Wash < 1 9 < 1 20 < 1 59 < 1 32 NW 97 3rd Wash < 1 16 < 1 29 < 1 64 < 1 54 --- --- 4th Wash < 1 21 <1 35 < 1 72 < 1 62 --- --- 5th Wash < 1 29 < 1 42 NW 88 < 1 62 --- --- 6th Wash < 1 34 < 1 49 --- --- < 1 76 --- --- 7th Wash < 1 44 < 1 57 --- --- < 1 84 --- --- 8th Wash < 1 52 < 1 66 --- --- NW 96 --- --- 9th Wash < 1 61 < 1 73 --- --- --- --- --- --- 10th Wash < 1 67 PW 84 --- --- --- --- --- --- 11th Wash < 1 72 NW --- --- --- --- --- --- --- 12th Wash < 1 76 --- --- --- --- --- --- --- --- 13th Wash < 1 80 --- --- --- --- --- --- --- --- 14th Wash PW 86 --- --- --- --- --- --- --- --- From Table 1, it is clear that the mixed surfactants of Samples A and B, gave superior results. That is, the results for Samples A and B were superior to the results for Samples C, D and E. To better understand the data in Table 1, such results were plotted three dimensionally in FIG. 1 as the maximum number of wash cycles achieved without completely losing wettability versus percent surfactant lost for all five polymeric fabric samples. The figure clearly shows the improved resistance to removal of a mixed surfactant system of the present invention, when compared to a single surfactant. FIG. 1 also shows the advantages to be obtained when both the first surfactant and the second surfactant are polyether polysiloxane surfactants. Example 2 In order to demonstrate the need for the fabric to be worked after the composition of the present invention has been applied, the procedure of Example 1 was repeated, except that in each case the composition was applied to the fabric by spraying and the size of each sample was 5 x 5 inches (about 13 x 13 cm). Each sample was hung in a fume hood and sprayed by means of a 16-ounce (roughly 0.5-liter) Preval Power Unit (Precision Valve Corporation, Yonkers, New York) on both sides of the fabric with a 0.1 percent by weight solution of surfactants in water. The sprayed fabric then was dried, weighed, and washed as described in Example 1. Since the same surfactant compositions were employed in this example as in Example 1, the sample designations are followed by the letter "S" to indicate sprayed samples. Summary of Washing Results for Sprayed Samples Sample AS Sample BS Sample CS Sample DS Sample ES % Add-on -----1.0----- -----0.9----- -----1.1----- -----1.0----- -----1.1----- Status WT Lost WT Lost WT Lost WT Lost WT Lost 1st Wash < 1 9 < 1 20 < 1 85 <1 28 NW 96 2nd Wash < 1 18 < 1 30 NW 94 < 1 50 --- --- 3rd Wash < 1 29 < 1 40 --- --- < 1 70 --- --- 4th Wash < 1 36 < 1 56 --- --- PW 87 --- --- 5th Wash < 1 41 < 1 65 --- --- NW 96 --- --- 6th Wash < 1 49 < 1 74 --- --- --- --- --- --- 7th Wash < 1 56 PW 82 --- --- --- --- --- --- 8th Wash < 1 68 NW 91 --- --- --- --- --- --- 9th Wash < 1 77 --- --- --- --- --- --- --- --- 10th Wash PW 86 ----- --- --- --- --- --- --- 11th Wash NW --- --- --- --- --- --- --- --- --- Upon comparing the data in Table 2 with that in Table I, it is seen that working results in significant increases in the durability of the surfactant treatment, i.e., the resistance to removal of the surfactants from the fabric by an aqueous liquid. As with Example 1, the results were plotted three dimensionally as the maximum number of wash cycles achieved without completely losing wettability versus percent surfactant lost for all five polymeric fabric samples. Such plot is shown as FIG. 2. Even without working, a mixed surfactant system of the present invention has increased resistance to removal from the fabric by an aqueous liquid. In addition to FIG. 2, the data for Samples A and AS from Tables 1 and 2 were plotted as wash cycle versus percent surfactant lost, as shown in FIG. 3. Similar plots were prepared for Samples B and BS and for the comparative Samples C and CS, as shown in FIGS. 4 and 5, respectively. Finally, the data in FIGS. 1 and 2 were combined in the three-dimensional plot shown in FIG. 6 to emphasize the advantages obtained from working the fabric after a surfactant composition has been applied to a surface. In order to determine the location of the surfactants on the fabric after it has been worked and dried, dot element maps were prepared in accordance with known procedures. A scanning electron photomicrograph was obtained for a portion of the fabric of Sample A and is shown in FIG. 7. A set of element maps then was obtained, in which each showed an image that appeared at the same 128 pixel resolution as the x-ray data. Thus, there is an exact correspondence between the electron and x-ray images. The purpose of the maps is to graphically illustrate variations in the local concentrations of any given element. There are, however, several factors which affect the measured x-ray intensity. Most notable are the high x-ray background associated with silicon and the surface roughness of the fabric which creates shadows in the element maps. These image artifacts were compensated for by mapping for an element that is not present in the sample, such as argon or aluminum, which has an x-ray background similar to that of the element in question, i.e., silicon. The background map then was subtracted from the silicon map to produce a true rendition of the silicon distribution. The image was further enhanced by using a "thermal" pseudocolor look up table (LUT) and is shown in FIG. 8. This highly intuitive color scale shows areas of high silicon concentration as yellow, areas of little or no silicon as black or blue, and intermediate silicon levels as magenta. Because the maps were 30-minute maps, there was a significant level of statistical noise. The statistical variability can be reduced by acquiring the maps over a longer period of time. It is clear from FIGS. 7 and 8 that the silicon-containing surfactants were distributed preferentially in regions of high capillary tension, i.e., in the fiber-fiber interstices of the fabric. In addition, some surfactant was distributed along the surfaces of the fibers, but not uniformly and not at the high levels found in the interstices.

Claims: Claims for the following Contracting States : BE, DE, ES, FR, GB, IT, NL A composition comprising: water; a first polyether polysiloxane surfactant; and a second polyether polysiloxane surfactant which is less soluble in water than said first surfactant; in which said second surfactant has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water; and in which one of said first and second surfactants has a linear structure and the othes of said first and second surfactants has a comblike structure, with the proviso that a composition consisting of 45 to 98% by weight of a water soluble or water dispersible polyether polysiloxane, the polyether groups of which consist of 30 to 100 mole % of oxyethylene units, the remainder being oxypropylene units, and the polysiloxane block of which has a 10 to 100 siloxane units; 1 to 20 % by weight of water soluble or water dispersible organopolysiloxane with at least one ammonium group linked over a carbon atom; 1 to 20 % by weight of water; and up to 10% by weight of a water dispersible or insoluble organopolysiloxane selected from a siloxane of the general, average formula wherein R 20 represents a polyether group -(C n H 2n O) x R 30 , wherein R 30 is a hydrogen, hydroxyl, alkyl or acyl group and n has a numerical value of 2 to 2.7 and x has a numerical value of 2 to 200; R 40 represents an alkyl group -(CH 2 ) y CH 3 where y is a number from 7 to 21; a 1 has a number value of 1 to 50; b 2 has a number value of 1 to 98; c 3 has a number value of 1 to 25; and a 1 +b 2 + c 3 is 3 to 150; is excluded. The composition of claim 1, in which each of said first and second surfactants has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water. The composition of claim 2, in which said second surfactant is essentially insoluble in water at 20°C. The composition of claim 1, in which said first and second surfactants are present in a ratio by weight of said first surfactant to said second surfactant which is in a range of from 10:1 to 1:2. The composition of claim 1, in which one of said first and said second surfactants has the general formula, wherein: each of R7 - R 16 independently is selected from the group consisting of C 1 - C 8 alkyl and aryl groups; R 17 is a C 10 - C 25 alkyl group; R 18 is hydrogen or a C 1 - C 4 alkyl group, e represents an integer from 3 to 15; f represents an integer from 1 to 6; g represents an integer from 5 to 30; the ratio of f to g is in a range of from 2 to 10; h represents an integer from 1 to 10; j represents an integer from 4 to 15; k represents an integer from 1 to 15; the ratio of j to k is in a range of from 0.5 to 4; and the number-average molecular weight of the second surfactant is in a range of from 5,000 to 60,000. The composition of claim 5, in which: each of R 7 -R 16 independently is selected from the group consisting of C 1 - C 3 alkyl and phenyl groups; R 17 is a C 12 - C 20 alkyl group; R 18 is hydrogen or a C 1 - C 3 alkyl group; e represents an integer from 3 to 8; f represents an integer from 2 to 4; g represents an integer from 10 to 20; the ratio of f to g is in a range of from 3 to 8; h represents an integer from 2 to 4; j represents an integer from 6 to 12; k represents an integer from 4 to 8; the ratio of j to k is in a range of from 1 to 2; and the number-average molecular weight of the second surfactant is in a range of from 7,000 to 24,000. The composition of claim 5, in which the ratio of said first surfactant to said second surfactant is in a range of from 10:1 to 1:2. The composition of claim 7, in which the ratio of said first surfactant to said second surfactant is in a range of from 5:1 to 1:1. A method for increasing the wettability of a polymeric fabric by the application of surfactants thereto, which method comprises: providing a polymeric fabric; and applying to the surface of the polymeric fabric a composition according to any one of claims 1 to 8. The method of claim 9, in which the polymeric fabric to which the composition has been applied is worked before the drying step. The method of claim 9, in which said fibers are comprised of polyolefin fibers. The method of claim 9, in which said one of said first and said second surfactants has the general formula according to claims 5 or 6. A wettable polymeric fabric to which a composition according to any one of claims 1 to 8 has been applied. The wettable polymeric fabric of claim 13, in which said first and second surfactants preferentially are located in the fiber-fiber interstices. The wettable polymeric fabric of claim 13, in which said fibers are comprised of polyolefin fibers. The wettable polymeric fabric of claim 13, in which said one of said first and said second surfactants has the general formula according to claims 5 or 6. A disposable absorbent article, at least one component of which is the wettable polymeric fabric of any one of claims 13 to 16. The disposable absorbent article of claim 17, in which said disposable absorbent article is selected from the group consisting of a diaper, a feminine care product, a sanitary napkin, a tampon, an incontinent product, a training pant and a wipe. Claims for the following Contracting States : PT, SE A composition comprising: water; a first polyether polysiloxane surfactant; and a second polyether polysiloxane surfactant which is less soluble in water than said first surfactant; in which said second surfactant has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water; and in which one of said first and second surfactants has a linear structure and the othes of said first and second surfactants has a comblike structure. The composition of claim 1, in which each of said first and second surfactants has a solubility in water at 20°C no greater than 5 percent by weight, based on the weight of the water. The composition of claim 2, in which said second surfactant is essentially insoluble in water at 20°C. The composition of claim 1, in which said first and second surfactants are present in a ratio by weight of said first surfactant to said second surfactant which is in a range of from 10:1 to 1:2. The composition of claim 1, in which one of said first and said second surfactants has the general formula, wherein: each of R7 - R 16 independently is selected from the group consisting of C 1 - C 8 alkyl and aryl groups; R 17 is a C 10 - C 25 alkyl group; R 18 is hydrogen or a C 1 - C 4 alkyl group, e represents an integer from 3 to 15; f represents an integer from 1 to 6; g represents an integer from 5 to 30; the ratio of f to g is in a range of from 2 to 10; h represents an integer from 1 to 10; j represents an integer from 4 to 15; k represents an integer from 1 to 15; the ratio of j to k is in a range of from 0.5 to 4; and the number-average molecular weight of the second surfactant is in a range of from 5,000 to 60,000. The composition of claim 5, in which: each of R 7 -R 16 independently is selected from the group consisting of C 1 - C 3 alkyl and phenyl groups; R 17 is a C 12 - C 20 alkyl group; R 18 is hydrogen or a C 1 - C 3 alkyl group; e represents an integer from 3 to 8; f represents an integer from 2 to 4; g represents an integer from 10 to 20; the ratio off to g is in a range of from 3 to 8; h represents an integer from 2 to 4; j represents an integer from 6 to 12; k represents an integer from 4 to 8; the ratio of j to k is in a range of from 1 to 2; and the number-average molecular weight of the second surfactant is in a range of from 7,000 to 24,000. The composition of claim 5, in which the ratio of said first surfactant to said second surfactant is in a range of from 10:1 to 1:2. The composition of claim 7, in which the ratio of said first surfactant to said second surfactant is in a range of from 5:1 to 1:1. A method for increasing the wettability of a polymeric fabric by the application of surfactants thereto, which method comprises: providing a polymeric fabric; and applying to the surface of the polymeric fabric a composition according to any one of claims 1 to 8. The method of claim 9, in which the polymeric fabric to which the composition has been applied is worked before the drying step. The method of claim 9, in which said fibers are comprised of polyolefin fibers. The method of claim 9, in which said one of said first and said second surfactants has the general formula according to claims 5 or 6. A wettable polymeric fabric to which a composition according to any one of claims 1 to 8 has been applied. The wettable polymeric fabric of claim 13, in which said first and second surfactants preferentially are located in the fiber-fiber interstices. The wettable polymeric fabric of claim 13, in which said fibers are comprised of polyolefin fibers. The wettable polymeric fabric of claim 13, in which said one of said first and said second surfactants has the general formula, according to claims 5 or 6. A disposable absorbent article, at least one component of which is the wettable polymeric fabric of any one of claims 13 to 16. The disposable absorbent article of claim 17, in which said disposable absorbent article is selected from the group consisting of a diaper, a feminine care product, a sanitary napkin, a tampon, an incontinent product, a training pant and a wipe.

Inventors: MACDONALD JOHN GAVIN, NOHR RONALD SINCLAIR, MACDONALD, JOHN GAVIN, NOHR, RONALD SINCLAIR
Applicants: KIMBERLY CLARK CO, KIMBERLY-CLARK WORLDWIDE, INC.
Application year: 1994
Main classification: D06M15
IPC codes: D06M101, C11D17, D06M15, A61F13, A61L15