Method for increasing the density of a spray-dried polymeric composition

Abstract: A method for increasing the density of a spray-dried waterborne polymeric composition is provided, wherein a gas, such as, for example, carbon dioxide, having a solubility factor greater than one is used in spray-drying the waterborne composition.

Description: This invention relates to a method for increasing the density of a spray-dried waterborne polymeric composition. Waterborne compositions containing water-soluble or water-insoluble polymers may be spray dried to form dry powders. In certain uses of such dry powders it is advantageous that the powder have as high a density as possible. U.S.-A-4,842,900 discloses a method and apparatus for coating a liquid coating composition to a moving web in which air entrained on the web is replaced by a gas having a higher solubility than air in the liquid coating composition such as, for example, carbon dioxide. U.S.-A-3,661,605 discloses an aqueous aerosol composition composed of a homogenized dispersion of lecithin in water and contains a propellant, eg., carbon dioxide or nitrous oxide, for pressurizing the composition in an amount sufficient to produce a release coating of lecithin on a surface when the composition is sprayed. Further disclosed is spraying an aqueous dispersion of lecithin by other means such as squeezing from a flexible bottle. U.S.-A-4,869,878 discloses a device for the creation of an oxygen-free working atmosphere such as a device for the production of propellant and buffer gasses such as combustion waste gas for a spray gun with which molten metal or ceramic is applied to a workpiece. US-A-4,923,720 discloses a liquid coatings application process and apparatus in which supercritical fluids, such as supercritical carbon dioxide fluid, are used to reduce to application consistency viscous coatings compositions to allow for their application as liquid sprays. JP-A-60/85929 discloses a spraying composition containing a water-soluble resin, including vinyl acetate resin, and an oxygen-blocking agent such as silicone oil. The propellant gas used in spraying is fluorocarbon or carbon dioxide. GB-A-2,020,308 discloses a propellant for aerosol spray cans, particularly lacquer spray cans, which is based on the use of carbon dioxide/ propane/ butane mixture. None of the references disclose a method for increasing the density of a spray-dried waterborne composition. In accordance with the present invention, there is provided a method for increasing the density of a spray-dried waterborne polymeric composition which method comprises spray-drying a waterborne polymeric composition wherein the carrier gas used in the spraying operation is a gas having a solubility factor of greater than one, preferably greater than 35. The carrier gas is preferably nitrous oxide or carbon dioxide, most preferably carbon dioxide. The "solubility factor" of a gas as used herein is defined as: solubility factor of a gas = solubility of the gas in water solubility of nitrogen in water where solubility is measured at 25°C at 1 atmosphere gas pressure. Some solubility factors are presented below: Gas Solubility in water Solubility Factor Nitrogen 0.65 millimoles per litre - Carbon dioxide 34 millimoles per litre 52.3 Nitrous oxide 24 millimoles per litre 36.9 A "waterborne polymeric composition" herein is defined as a composition containing either a soluble polymer dissolved in or an insoluble polymer dispersed in a medium which is predominantly composed of water, or mixtures thereof. The waterborne polymeric composition may contain a solution of a polymer in water or in an aqueous medium, which aqueous medium may be, for example, a mixture of water and at least one water-miscible solvent such as, for example, isopropanol, ethylene glycol butyl ether, and propylene glycol propyl ether; the waterborne polymeric composition may contain an alkali-soluble polymer dissolved in an alkaline aqueous medium; or the waterborne polymeric composition may contain a dispersion of an insoluble polymer in an aqueous medium such as, for example, an emulsion-polymerized polymer. Polymers in the waterborne polymeric compositions are generally prepared by the addition polymerization of at least one ethylenically unsaturated monomer such as, for example, esters of (meth)acrylic acid, vinyl esters, styrene, and butadiene. Polar monomers such as (meth)acrylic acid, itaconic acid, acrylonitrile, dimethylaminoethyl (meth)acrylate, and hydroxyethyl (meth)acrylate may also be incorporated in the polymer. Low levels of multi-ethylenically unsaturated monomers may be incorporated in the polymer. Chain transfer agents such as, for example, mercaptans may be used in order to moderate the molecular weight of the polymer. When the polymer is in the form of an emulsion-polymerized polymer, the particles may be from about 40 nanometers to about 4000 nanometers in diameter. The solids content of waterborne polymeric compositions may be from about 20% to about 70% by weight. The viscosity may be from about 50 centipoises to about 10,000 centipoises (0.5 to 10 Pa.s.), as measured using a Brookfield viscometer (Model LVT using spindle #3 at 12 rpm); the viscosities appropriate for different spraying methods vary considerably. Waterborne polymeric compositions may contain, in addition to the polymer, conventional components such as, for example, emulsifiers, pigments, fillers, dispersants, coalescing agents, anti-migration aids, curing agents, thickeners, humectants, wetting agents, biocides, plasticizers, antifoaming agents, colourants, waxes, and anti-oxidants. In some uses a spray-dry prepared powder of increased density is desired. For example, in the ceramic industry the operation of dry pressing requires dry granules of ceramic powder mixed with dispersants and binders. Denser powder granules have improved flow properties and fill dry press moulds better than less dense powders. Denser powder granules are formed when aqueous slips containing pigment, dispersant, and polymeric binder are spray-dried using carbon dioxide rather than nitrogen as the atomizing and carrier gas. The following example is intended to illustrate the method for increasing the density of a spray-dried waterborne polymeric composition. EXAMPLE 1 Increased density of spray-dried powder A ceramic slip was prepared by ball milling 240.0g of alumina powder (Alcoa A-16SG), 150 ml. distilled water, and 2.88 g. 25% aqueous solution of dispersant (ACUMER 9500) at 85 rpm for 40 minutes ill a "OO"-jar with 1160 g. of grinding media. Then 15.32 g. of a 47% aqueous acrylic emulsion polymer (RHOPLEX B-60A) was added and the mixture was ball milled for an additional 20 minutes. The slip was divided into two equal portions one of which was spray-dried using carbon dioxide, the other using nitrogen. The slips were spray-dried in a Buchi Model 901 Mini Spray Drier, using an inlet temperature of 130°C, outlet temperature of 60°C, and a nozzle pressure of 413.4 kPa (60 psi). The spray drying was repeated three times using three independently prepared slips. Visual examination indicated that the powders formed using carbon dioxide were less agglomerated than those formed using nitrogen. To measure the packed density of the particles, a 5.00 g. portion of the powder was placed in a 10 ml., 1.27 cm.-diameter graduated cylinder. The cylinder was capped and then the cylinder was tapped 2,000 times using a Stampvolumeter Stav 2003 (J. Engelsmann A.-G., Ludwigshafen, Germany). The volume was then recorded and the tap density was calculated. The average tap density using carbon dioxide (mean of 9 density measurements) was 1.3 +/- 0.2g/cc.; the average tap density using nitrogen (mean of 10 density measurements) was 0.91 +/-0.2 g/cc. Using a gas with a with a solubility factor greater than about one in the method of this invention caused an increased density in a spray-dried powder.

Claims: A method for increasing the density of a spray-dried waterborne polymeric composition, which method comprises spray-drying a water borne polymeric composition, wherein the carrier gas used during the spray-drying operation is a gas having a solubility factor of greater than one. A method according to claim 1, wherein the carrier gas has a solubility factor of greater than 35. A method according to claim 9, wherein the carrier gas is nitrous oxide or carbon dioxide. A method according to any one of claims 1 to 3 wherein the polymer component of the waterborne polymeric composition is an emulsion polymerised polymer.

Inventors: GEBHARD MATTHEW STEWART, SIMON ETHAN SCOTT, GEBHARD, MATTHEW STEWART, SIMON, ETHAN SCOTT
Applicants: ROHM & HAAS, ROHM AND HAAS COMPANY
Application year: 1994
Main classification: B01D1
IPC codes: C09K3, C09D5