Curable polymer release coating composition

Abstract: There is disclosed a polymer composition which can cure rapidly to provide a release coating that has a low surface tension, said composition comprising: (A) a fluorine-containing polymer that contains at least 2 alkenyl groups in each molecule, said polymer being obtained by the copolymerization of (a) an acrylic monomer having the general formula CH₂=CX-COOR' wherein X is selected from the group consisting of hydrogen and a methyl radical and R' denotes a monovalent hydrocarbon group having 4 to 15 carbon atoms which contain at least one -CF₂- group, and (b) a silicone macromonomer with the general formula CH₂=CX-COO-Q-(RMeSiO) n -Me₂SiR'' wherein X has its previously defined meaning, Q denotes a divalent hydrocarbon group having 1 to 8 carbon atoms, R is selected from the group consisting of methyl radical and fluorine-containing monovalent hydrocarbon group having 3 to 8 carbon atoms, Me represents a methyl radical, R'' denotes a alkenyl group having 2 to 6 carbon atoms and n is an integer having a value of at least 1; (B) an organohydrogenpolysiloxane that contains at least 3 silicon-bonded hydrogen atoms in each molecule; (C) a hydrosilylation catalyst; and (D) a hydrosilylation catalyst inhibitor.

Description: The invention relates to a fluorine-containing curable polymer composition that employs an organohydrogenpoly-siloxane crosslinker and that cures rapidly to give a low surface-tension release coating. Products capable of releasing tacky substances (e.g., pressure-sensitive adhesives) can be prepared by forming a cured release coating on the surface of many different types of substrates, such as paper, plastic films, and synthetic fiber fabrics. The curable organopolysiloxane composition disclosed in JP-A 63-320 is one example of an agent that will produce such a cured release coating. This particular composition is composed of a diorganopolysiloxane that contains both vinyl and fluoroalkyl groups, an organohydrogenpolysiloxane, and a platinum compound. Several drawbacks are associated with this curable organopolysiloxane composition; it has a slow cure rate and its release performance can be poor. Moreover, because its silicone component can migrate into tacky substances, it can impair the tack of pressure-sensitive adhesives. This invention introduces a curable polymer composition that solves the problems described above. In specific terms, the present invention provides a curable polymer composition that cures rapidly into a low surface-tension release coating. Our invention is a curable polymer composition comprising: (A) a fluorine-containing polymer that contains at least 2 alkenyl groups in each molecule which is obtained by the copolymerization of (a) an acrylic monomer with the general formula CH 2 =CX-COOR' wherein X denotes hydrogen or a methyl radical, and R' denotes a C 4 to C 15 monovalent organic group that contains the -CF 2 - group and (b) a silicone macromonomer with the general formula CH 2 =CX-C-O(O)-Q-(RMeSiO) n -Me 2 SiR'' wherein X is defined as above, Q denotes a C 1 to C 8 divalent hydrocarbon group, R is methyl or a C 3 to C 8 fluorine-containing monovalent hydrocarbon group, Me is methyl, R'' denotes a C 2 to C 6 alkenyl group, and n is an integer with a value of at least 1; (B) an organohydrogenpolysiloxane that contains at least 3 silicon-bonded hydrogen atoms in each molecule; (C) a hydrosilylation catalyst; and (D) a hydrosilylation catalyst inhibitor. The fluorine-containing polymer (A) of the present invention is our base component of the composition. It must contain at least 2 alkenyl groups in each molecule in order to crosslink with the organohydrogenpolysiloxane comprising component (B). This fluoropolymer consists of a copolymer of (a) an acrylic monomer with the general formula CH 2 =CX-COOR' and (b) a silicone macromonomer with the general formula CH 2 =CX-COO-Q-(RMeSiO) n -Me 2 SiR''. X in the general formula for component (a) denotes hydrogen or a methyl radical, and (a) is therefore an acrylate ester or methacrylate ester. R' denotes a C 4 to C 15 monovalent hydrocarbon group that contains the -CF 2 - group and is exemplified by the following: -CH 2 (CF 2 ) 4 F, -CH 2 (CF 2 ) 4 H, -CH 2 CH 2 (CF 2 ) 4 F, -CH 2 CH 2 (CF 2 ) 4 H, -CH 2 (CF 2 ) 6 F, -CH 2 (CF 2 ) 8 H, -CH 2 CH 2 (CF 2 ) 8 F, and -CH 2 CH 2 (CF 2 ) 6 H. The silicone macromonomer (b) has the general formula CH 2 =CX-COO-Q-(RMeSiO) n -Me 2 SiR'', in which Me is methyl, X is hydrogen or a methyl radical, and n is an integer with a value of at least 1. The preferred range for n is 20 to 500 because this range affords compositions with particularly good curabilities. R denotes a methyl radical or a C 3 to C 8 fluorine-containing monovalent hydrocarbon group. In addition to methyl, R is exemplified by 3,3,3-trifluoropropyl, 3,3,4,4,5,5,6,6,6-nonafluorohexyl, and so forth. Q denotes C 1 to C 8 divalent hydrocarbon groups, and Q is exemplified by methylene, ethylene, and propylene. R'' denotes a C 2 to C 6 alkenyl, and is vinyl, allyl, propenyl, butenyl, pentenyl, and hexenyl, with vinyl, allyl, and hexenyl being preferred. The copolymerization reaction between acrylic monomer (a) and silicone macromonomer (b) is run as a radical reaction in the presence of an initiator. The polymerization initiator (radical source) used is not critical, and is exemplified by organoperoxides such as dicumyl peroxide, di(tert-butyl) peroxide, benzoyl peroxide, or cumene hydroperoxide; and by azo compounds such as azobisisobutyronitrile, azobisisobutyrate esters, azodibenzoyl, and tetramethyltetrazene. Azo compounds are preferred from the standpoint of preserving the alkenyl in the silicone macromonomer. This copolymerization reaction can be run with or without solvent. The use of solvent is safer and more reliable since it facilitates control of the reaction. The following solvents are recommended: aromatic solvents such as benzene, toluene, and xylene; aliphatic solvents such as hexane and heptane; ethers such as tetrahydrofuran and diethyl ether; alcohols such as methanol, ethanol, propanol, and butanol; ketones such as acetone, methyl ethyl ketone, and methyl isobutyl ketone; esters such as ethyl acetate and butyl acetate; chlorinated hydrocarbons such as carbon tetrachloride, trichloroethane, and chloroform; fluorinated aromatic hydrocarbons such as trifluoromethylbenzene, 1,3-bis(trifluoromethyl)benzene, methylpentafluorobenzene; dimethylformamide; and dimethyl sulfoxide. The preceding solvents may also be used in combinations of two or more. The copolymerization reaction is run at a temperature at which the initiator is decomposed and is run until monomer conversion reaches a desired value. This reaction may be run at elevated, reduced, or ambient pressure, and it is desirable to monitor monomer conversion, for example, by gas chromatography. Since monomer conversion is strongly dependent on the particular reaction conditions, such as the type of initiator, type of solvent, and monomer concentration, the optimal conditions must typically be determined by experiment. The component (B) used in our composition functions as a crosslinker and consists of an organohydrogenpolysiloxane that contains on average at least 3 silicon-bonded hydrogen atoms in each molecule to obtain an excellent curability. The silicon-bonded organic groups present in component (B) are exemplified by non-alkenyl monovalent hydrocarbon groups, for example, alkyl groups such as methyl, ethyl, propyl, butyl, and pentyl; aryl groups such as phenyl, tolyl, and xylyl; and aralkyl groups such as benzyl, and phenethyl. The pendant groups in component (B) may also include fluorine-containing organic groups, as exemplified by groups with the general formulas C k F 2k+1 -R 3 - and C k F 2k+1 -R 3 -O-R 3 - in which R 3 denotes a divalent hydrocarbon group and k is an integer with a value of 1 to 20. The divalent hydrocarbon groups encompassed by R 3 alkylene such as methylene, ethylene, methylmethylene, propylene, and butylene; arylene such as phenylene, tolylene, and xylylene; alkylenearylene such as methylenephenylene, and ethylenephenylene; and arylenealkylene. For purposes of compatibility with component (A) of the invention, each molecule of component (B) preferably contains at least 1 perfluoroalkyl-containing C 3 to C 12 monovalent hydrocarbon group. The organohydrogenpolysiloxane (B) is exemplified by trimethylsiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, dimethylhydrogensiloxy-endblocked methyl(perfluorobutylethyl)siloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-endblocked methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-endblocked methyl(perfluorohexylethyl)siloxane-methylhydrogensiloxane copolymers, and copolymers composed of methyl(perfluorobutylethyl)siloxane, dimethylhydrogensiloxane, and SiO 2 units. The mixing proportions for components (A) and (B) in the invention composition are not critical. However, these two components are mixed to obtain values of 0.2/1 to 5/1 for the molar ratio of alkenyl groups in component (A) to silicon-bonded hydrogen in component (B). Outside this range, either the rate of cured film formation by our composition is very slow or the cured film produced by the composition has a substantially diminished release performance. The hydrosilylation catalyst comprising component (C) used in our invention is a catalyst for the crosslinking and curing of components (A) and (B). Component (C) is exemplified by finely divided platinum adsorbed on a carbon carrier, chloroplatinic acid, alcohol-modified chloroplatinic acid, olefin complexes of chloroplatinic acid, chloroplatinic acid/divinyldisiloxane coordination compounds, platinum black, palladium catalysts, and rhodium catalysts. This component should be added in a catalytic quantity, and is in the range of 0.1 to 100 weight parts per 1,000,000 weight parts component (A). The hydrosilylation catalyst inhibitor comprising component (D) of this invention is used to improve the room-temperature stability of our composition by inhibiting the catalytic activity of the hydrosilylation catalyst at room temperature. Component (D) is exemplified by alkynyl alcohols such as 3-methyl-1-butyn-3-ol, 3,5-dimethyl-1-hexyn-3-ol, 3-methyl-1-pentyn-3-ol, and phenylbutynol, or 3-methyl-3-penten-1-yne, 3,5-dimethyl-1-hexyn-3-ene, cyclotetra(methylvinylsiloxane), bis(2-methoxyisopropyl) maleate, and benzotriazole. The composition of this invention may be diluted with organic solvent as desired. Said organic solvent is exemplified by ethers such as tetrahydrofuran; ketones such as methyl isobutyl ketone; aromatic hydrocarbons such as trifluorotoluene, and hexafluoroxylene; halogenated hydrocarbons such as trichloroethylene, perchloroethylene, 1,1,1-trichloroethane, dichloroethane, and 1,1,2-trichlorotrifluoroethane; HCFC solvents such as CHCl 2 CF 3 (HCFC123) and CH 3 CCl 2 F (HCFC141b); and fluorinated aromatic hydrocarbons such as trifluoromethylbenzene, 1,3-bis(trifluoromethyl)benzene, and methylpentafluorobenzene. The use of organic solvent is preferred in view of the corresponding improvements in the storage stability of the composition and in its coatability on various substrates. The invention composition is prepared by mixing (A) - (D), or components (A) - (D) plus organic solvent, to homogeneity. However, various additives may also be added insofar as the object of the invention is not impaired. These additives are inorganic fillers such as fumed silica, precipitated silica, fused silica, quartz powder, silica gel, silica balloons, carbon black, mica, talc, calcium carbonate, glass fiber, iron oxide, titanium oxide, alumina, aluminum hydroxide, and diatomaceous earth; oils such as silicone oils, mineral oils, and hydrocarbon oils; as well as dyes, coloring pigments, oxidation inhibitors, heat stabilizers, and flame retardants. The curable polymer composition of the invention will form a low surface-tension cured film on the surface of a variety of substrates, such as glass, metal, paper, plastic films, fabrics, and so forth, when heated after having been coated thereon. Heating is suitably carried out for 20 seconds to 30 minutes at temperatures of 120°C to 150°C. The resulting cured film has a low surface-tension. The present composition therefore provides a cured film that has an excellent releasability as well as excellent water repellency and oil repellency. In addition, the cured film afforded by our curable polymer composition also exhibits excellent release properties against pressure-sensitive adhesives and particularly silicone-based pressure-sensitive adhesives. Thus, its ability to cure into a low surface-tension coating allows our curable polymer composition to be useful for providing cured release films that are water repellent, and/or oil repellent. Examples The invention is explained below in greater detail through working examples, in which "parts" designates "weight parts", the viscosity is the value measured at 25°C, and Me indicates the methyl group. Example 1 The following were mixed and heated to 90°C: 100 g of a mixture of acrylic monomers with the formulas CH 2 =CH-COOC 2 H 4 (CF 2 ) m F in which m = 6, 8, 10, and 12, 10 g of silicone macromonomer with the formula CH 2 =CHCOOC 2 H 4 -(CF 3 C 2 H 4 SiMeO) n -Me 2 SiCH=CH 2 in which the average value of n was 50, and 100 g of methyl isobutyl ketone. This was followed by the addition of 0.2 g azobisisobutyronitrile and heating for an additional 6 hours with stirring. The polymer subsequently precipitated by the addition of 300 g of methanol was recovered and designated as Synthesis Sample 1. The following were dissolved in 494 parts of 1,3-bis(trifluoromethyl)benzene: 100 parts of Synthesis Sample 1, 3 parts of dimethylhydrogensiloxy-endblocked methyl(perfluorobutylethyl)siloxane-methylhydrogensiloxane copolymer with a viscosity of 20 mPa.s (centipoise), and 1 part of cyclotetra(methylvinylsiloxane). A curable polymer composition was then prepared by the addition of sufficient chloroplatinic acid/divinyltetramethyldisiloxane complex to give 500 ppm of platinum metal. This composition was coated on the surface of a glass plate and heated for 3 minutes at 150°C to give a cured film. The contact angles of water, methylene iodide, and n-hexadecane on this cured film were measured by the droplet method using a contact-angle meter from Kyowa Kaimen Kagaku Kabushiki Kaisha. In each case, measurements were carried out on 10 droplets, and the value reported for the contact angle is the average of the 10 measurements. The following results were obtained. substance contact angle water 120° methylene iodide 102° n-hexadecane 70° Example 2 The following were mixed and heated to 90°C: 100 g of perfluorooctylethyl methacrylate, 10 g of silicone macromonomer with the formula CH 2 =CHCOOC 2 H 4 -(Me 2 SiO) n -Me 2 SiCH=CH 2 in which the average value of n was 80, and 100 g of 1,3-bis(trifluoromethyl)benzene. This was followed by the addition of 0.2 g of azobisisobutyronitrile and heating for an additional 6 hours while stirring. The polymer subsequently precipitated by the addition of 300 g of methanol was recovered and designated as Synthesis Sample 2. The following were dissolved in 494 parts of 1,3-bis(trifluoromethyl)benzene: 100 parts of Synthesis Sample 2, 3 parts of trimethylsiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymer with a viscosity of 3 mPa.s (centipoise), and 1 part of cyclotetra(methylvinylsiloxane). A curable polymer composition was then prepared by the addition of sufficient chloroplatinic acid/divinyltetramethyldisiloxane complex to give 500 ppm of platinum metal. This composition was coated on the surface of a glass plate and heated for 3 minutes at 150°C to give a cured film. This cured film was submitted to contact angle measurement as in Example 1, and the following results were obtained. substance contact angle water 122° methylene iodide 101° n-hexadecane 71° Example 3 A curable polymer composition as prepared in Example 2 was coated at a rate of 0.2 g/m 2 on the surface of polyethylene resin film, and a cured film was obtained by heating for 3 minutes at 150°C. The surface of this cured film was then coated with a dimethylpolysiloxane-based addition reaction-type silicone pressure-sensitive adhesive (SD4580™ from Dow Corning Toray Silicone Company, Limited, Japan) followed by heating for 3 minutes at 100°C. Polyethylene resin film (Lumilar S-10™ from Toray Kabushiki Kaisha, Japan) was applied to the treated surface to serve as backing material, and a measurement sample was fabricated by aging for a prescribed period of time at 25°C under a load of 20 g/cm 2 . The measurement sample was then cut to a width of 2.5 cm to give a test specimen. The backing film was easily peeled off when peeled at 180° and a peel velocity of 0.3 m/minute using a tensile tester. After this peeling test, the test specimen was adhered on a stainless steel plate, and the force (in grams) required to peel the test specimen from the stainless steel was measured (180°, peel velocity = 0.3 m/minute). This force was the same as the force required to peel an untreated reference tape, which indicated that no drop in adhesive strength due to silicone migration had occurred.

Claims: A curable polymer composition comprising: (A) a fluorine-containing polymer that contains at least 2 alkenyl groups in each molecule, said polymer being obtained by the copolymerization of (a) an acrylic monomer having the general formula CH 2 =CX-COOR' wherein X is selected from the group consisting of hydrogen and a methyl radical and R' denotes a monovalent hydrocarbon group having 4 to 15 carbon atoms which contain at least one -CF 2 - group, and (b) a silicone macromonomer with the general formula CH 2 =CX-COO-Q-(RMeSiO) n -Me 2 SiR'' wherein X has its previously defined meaning, Q denotes a divalent hydrocarbon group having 1 to 8 carbon atoms, R is selected from the group consisting of methyl radical and fluorine-containing monovalent hydrocarbon group having 3 to 8 carbon atoms, Me represents a methyl radical, R'' denotes an alkenyl group having 2 to 6 carbon atoms and n is an integer having a value of at least 1; (B) an amount of organohydrogenpolysiloxane that contains at least 3 silicon-bonded hydrogen atoms in each molecule sufficient to provide a molar ratio of silicon-bonded hydrogen atoms in (B) to alkenyl groups in (A) of from 0.2:1 to 5:1; (C) from 0.1 to 100 parts per million parts by weight of component (A)of a hydrosilylation catalyst; and (D) a hydrosilylation catalyst inhibitor. The composition according to claim 1, wherein R' of said component (a) is selected from the group consisting of the structures -CH 2 (CF 2 ) 4 F, -CH 2 (CF 2 ) 4 H, -CH 2 CH 2 (CF 2 ) 4 F, -CH 2 CH 2 (CF 2 ) 4 H, -CH 2 (CF 2 ) 6 F, -CH 2 (CF 2 ) 8 H, -CH 2 CH 2 (CF 2 ) 8 F and -CH 2 CH 2 (CF 2 ) 6 H. The composition according to claim 2, wherein R of said component (b) is selected from the group consisting of 3,3,3-trifluoropropyl, 3,3,4,4,5,5,6,6,6-nonafluorohexyl and methyl radicals. The composition according to claim 3, wherein R'' of said component (b) is selected from the group consisting of vinyl, allyl and hexenyl radicals. The composition according to claim 4, wherein n of said component (b) is 20 to 500, and wherein Q of said component (b) is selected from methylene, ethylene and propylene groups. The composition according to claim 5, wherein said organohydrogenpolysiloxane (B) is selected from the group consisting of trimethylsiloxy-endblocked dimethylsiloxane-methylhydrogensiloxane copolymers, dimethylhydrogensiloxy-endblocked methyl(perfluorobutylethyl)siloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-endblocked methyl(perfluorobutylethyl)siloxane-dimethylsiloxane-methylhydrogensiloxane copolymers, trimethylsiloxy-endblocked methyl(perfluorohexylethyl)siloxane-methylhydrogensiloxane copolymers and copolymers composed of methyl(perfluorobutylethyl)siloxane units, dimethylhydrogensiloxane units and SiO 2 units. The composition according to claim 1, further comprising an organic solvent. A substrate coated with the cured composition according to claim 1.

Inventors: KOBAYASHI HIDEKI, KOBAYASHI, HIDEKI, KOBAYASHI, HIDEKI, DOW CORNING TORAY SILICONE
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE CO., LTD.
Application year: 1994
Main classification: C08F283
IPC codes: C08L83, C08F290, C09D183