A PROCESS FOR PREPARING A RIGID POLYURETHANE FOAM AND LAMINATE ARTICLES THEREWITH

Abstract: Rigid polyurethane foam and laminate articles comprising a facing material and the said polyurethane foam are prepared by contacting under reaction conditions a urethane-modified polyisocyanate with a polyahl in the presence of a blowing agent comprising water. The urethane-modified polyisocyanate has an isocyanate content of from 10 to 29 weight percent and is obtained by reacting a polymethylene polyphenylisocyanate with a polyether polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent. Use of this polyisocyanate provides for enhanced adhesion of the resulting foam, especially when it is an all-water blown foam, to facing materials such as metal.

Description: A PROCESS FOR PREPARING A RIGID POLYURETHANE FOAM AND LAMINATE ARTICLES THEREWITH This invention relates to a process for preparing a rigid polyurethane foam, and a laminate article containing such foam, from a urethane-modified polyisocyanate. Rigid polyurethane foam is extensively used in the appliance and construction industry where its attractive thermal insulation performance is valued. Unfortunately as such rigid polyurethane foam frequently can be friable it is often necessary to protect it from o physical damage by use of a protective facing material. The selection of suitable facing material is generally application related and can be for appliance units, a plastic; for rigid insulation boardstock, paper; or for refrigerated containers or roadstock, metal. End products comprising a facing material and rigid polyurethane foam desirably should exhibit an overall attractive structural strength and durability. To help provide for such traits, the foam 5 advantageously should exhibit attractive adhesion properties to the facing material and not be particularly susceptible to internal failure, for example tearing. The adhesion of foam to a facing material can be enhanced by pretreatment of the facing material using generally known methods including corona treatment. Alternatively, enhanced adhesion properties may be obtained by selection of the materials used to prepare 0 the polyurethane foam. Patent publication EP-A-462,438 discloses the use of certain urethane- modified polyisocyanates when preparing water-blown rigid polyurethane foam exhibiting improved adhesion properties to a solid surface, notably metal. Further improvement of the disclosed adhesion properties would be desirable to better meet the demanding industrial performance requirements. Additionally, it would be desirable to develop a foaming process 5 wherein an article comprising a facing material and a rigid polyurethane foam can be prepared under more convenient processing conditions including, for example, a lower process temperature without substantial loss of adhesion properties. In one aspect, this invention relates to a process for preparing a rigid polyurethane foam by contacting under reaction conditions a urethane-modified 0 polyisocyanate with a polyahl in the presence of a blowing agent characterized in that: a) the urethane-modified polyisocyanate has an isocyanate content of from 10 to 29 weight percent and is the reaction product of a polymethylene polyphenylisocyanate, having an average isocyanate functionality of from 2.5 to 3.5, with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent; b) the blowing agent comprises from 1 to 10 parts of water per 100 parts by weight of polyahl and is free of any perhalogenated hydrocarbon, with the exception of perfluoroalkanes, wherein the urethane-modified polyisocyanate is present in an amount to provide from 0.7 to 2 isocyanate groups per isocyanate-reactive hydrogen atom present from the polyahl and water. In another aspect, this invention relates to a process for preparing a rigid polyurethane foam by contacting under reaction conditions a urethane-modified polyisocyanate with a polyahl in the presence of a blowing agent which consists of water, characterized in that: a) the urethane-modified polyisocyanate has an isocyanate content of from 22 to 27 weight percent and is the reaction product of a polymethylene polyphenylisocyanate having an average isocyanate functionality of from 2.7 to 3.2, with a polyoxyalkylene polyol that has a molecular weight of from 4000 to 12000 and an oxyethylene content of at least 50 weight percent; with b) the polyahl comprises a polyether polyol or a polyester polyol which has a molecular weight of from 200 to 15000; and c) the water is present in an amount of from 2 to 8 parts per 100 parts by weight of (W. wherein the urethane-modified polyisocyanate is present in an amount to provide from 0.9 to 1.5 isocyanate groups per isocyanate-reactive hydrogen atom present from the polyahl and water. In yet another aspect, this invention relates to a rigid polyurethane foam obtained according to the above mentioned process. In yet another aspect, this invention relates to a laminate comprising a facing material having contiguous to it a rigid polyurethane foam obtained by contacting under reaction conditions a urethane-modified polyisocyanate with a polyahl in the presence of a blowing agent to provide a polymerizing mixture which is brought into contact with the facing material and permitted to terminate its polymerization reaction, characterized in that: a) the urethane-modified polyisocyanate has an isocyanate content of from 10 to 29 weight percent and is the reaction product of a polymethylene polyphenylisocyanate, having an average isocyanate functionality of from 2.5 to 3.5, with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent; b) the blowing agent comprises from 1 to 10 parts of water per 100 parts by weight of polyahl and with the exception of perfluoroalkanes is free of any perhalogenated hydrocarbon, wherein the urethane-modified polyisocyanate is present in an amount to provide from 0.7 to 2 isocyanate groups per isocyanate-reactive hydrogen atom present from the polyahl and water, and wherein the facing material has a temperature of from 15°Cto 60°C. In yet another aspect, this invention relates to a two component rigid polyurethane foam-forming system, suitable for use in the above mentioned process which, based on total weight of (a) and (b) present, comprises: a) from 25 to 75 weight percent of a urethane-modified polyisocyanate that has an isocyanate content of from 10 to 29 weight percent and is the reaction product of a polymethylene polyphenylisocyanate having an average isocyanate functionality of from 2.5 to 3.5 with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent; and b) from 75 to 25 weight percent of a polyahl composition containing: (i) a polyether polyol or a polyester polyol which has a molecular weight of from 200 to 15000; and (ii) water in from 1 to 10 parts per 100 parts by weight of (b)(i). Polyurethane foam obtained according to this invention exhibits attractive adhesion properties to various facing materials including notably metal, and especially when such foam is prepared in the presence of a blowing agent consisting of water. The urethane-modified polyisocyanate required in the present invention has an isocyanate content of from 10 to 29, preferably from 20, more preferably from 22, and preferably up to 27, more preferably up to 26 weight percent. The urethane-modified polyisocyanate is the reaction product of a molar excess of polymethylene polyphenylisocyanate with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent. The polymethylene polyphenylisocyanate used has an average isocyanate functionality of from 2.5 to 3.5, preferably from 2.7, and preferably up to 3.2. Suitable polymethylene polyphenylisocyanates include mixtures of polymethylene polyphenylisocyanate with methylene diphenylisocyanate (MDI) including the 4,4'- and 2,4'-MDI isomers. In such mixtures, the polymethylene polyphenylisocyanate typically constitutes from 95 to 51 , preferably from 85 to 55 percent; and the MDI isomers from 5 to 49, more preferably from 15 to 45 percent based on total weight of the mixture. The ratio of the 4.4'-MDI to 2.4'-MDI typically is from 100:0 to 50:50, and more usually from 98:2 to 60:40. Exemplary of suitable polymethylene polyphenylisocyanates include those designated by the trademark VORANATE such as VORANATE M580 and especially VORANATE M220, available from The Dow Chemical Company. VORANATE M220 is understood to have an isocyanate functionality of 2.7 and to contain 60 weight percent polymethylene polyphenylisocyanate and 40 weight percent MDI, predominantly 4,4'-MDI. As mentioned, the polyoxyalkylene polyol used to prepare the urethane-modified polyisocyanate has a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent. The molecular weight of the polyoxyalkylene polyol preferably is from at least 3000, more preferably from at least 4000, and up to 15000, more preferably up to 12000, and yet more preferably up to 10000. To provide for a resulting foam with attractive adhesion properties the oxyethylene content of the polyoxyalkylene polyol preferably is from at least 50, and more preferably from 55 to 95, and yet more preferably from 55 to 85 weight percent. In a highly preferred embodiment of the invention, the polyoxyalkylene polyol has a molecular weight of from 4500 to 12000 and an oxyethylene content of from 55 to 80 weight percent. The balance of the molecular weight of the polyol when not derived from the oxyethylene content is normally attributed to the initiator and other oxyalkylene units as present including 5 oxybutylene, oxytetramethylene, and particularly oxypropylene. The polyoxyalkylene polyol advantageously has an average of from at least 2, preferably from at least 3, and preferably up to 8, more preferably up to 7 hydroxyl groups/molecule. In a preferred embodiment, the molecular weight and functionality of the polyol is such to provide a hydroxyl equivalent weight of at least 1000, and preferably from 1000 to 3500, and more preferably from 1500 to 10 2500. Suitable polyoxyalkylene polyols can be obtained by reacting ethylene oxide, and optionally other alkylene oxides including propylene oxide, with initiators such as water, glycerine, α-methylglucoside, α-(2-hydroxyethyl)glucoside, sorbitol or sucrose. Exemplary of suitable commercially available polyoxyalkylene polyols include those designated by the trademark VORANOL such as VORANOL CP 1421 of The Dow Chemical Company. Equally 15 suitable polyoxyalkylene polyols for preparation of the urethane-modified polyisocyanate include the glycerine initiated polyoxyethylene-oxypropylene adducts having an oxyethylene content of from 40 to 68 weight percent and a hydroxyl equivalent weight of from 2200 to 3500, as disclosed in U.S. Patent 5,1 14,989. The urethane-modified polyisocyanate may be prepared using conditions that 20 have already been described in the prior art such as, for example, EP-A-320,134, EP-A-344,551 and U.S. Patent 5,1 14,989. In the present invention, the above described urethane-modified polyisocyanate is reacted with a polyahl in the presence of a blowing agent and optionally other additives. The polyahl used in the process of this invention is an isocyanate-reactive substance which can 25 be an amine-terminated polyoxyalkylene, a polyol, or preferably a polyether polyol, or a polyester polyol, or mixtures of two or more thereof. Particularly suitable are polyester and especially polyether polyols having a molecular weight of from 200 to 15000. Such polyester and polyether polyols typically will contain an average of at least 2, and up to 8 hydroxyl groups/molecule. The presence of polyether polyols equivalent to the polyoxyalkylene polyol 30 as required forthe urethane-modified polyisocyanate is not excluded though preferred are polyether polyols as typically used in the production of rigid polyurethane foam and having a molecular weight of from 200 to 2000, preferably from 250 to 1500. Examples of these and other suitable isocyanate-reactive materials are described more fully in U.S. Patent 4,394,491 , particularly in columns 3-5 thereof. Exemplary of suitable commercially available polyether 35 polyols include those designated bythe trademark VORANOL such as VORANOL RN41 1 , VORANOL RN490, VORANOL RA640, VORANOL CP260, VORANOL CP450, VORANOL P1010 and VORANOL CP1055, from The Dow Chemical Company. Optionally, in addition to the above mentioned polyester and polyether polyols the polyahl may also comprise chain extending or cross linking agents of molecular weight less than 200, and typically from 60 to 180. Such agents include for example (di)ethylene glycol, (di)propylene glycol, glycerine, trimethylol propane and alkanolamines including (di)ethanolamine or (di)propanolamine. When present such agents generally constitute from more than 3, and up to 25, and usually from 4 to 15, weight percent of the total weight of polyahl including such agent present. The blowing agent comprises from 1 to 10 parts of water per 100 parts by total weight of polyahl and is free of any perhalogenated hydrocarbon, with the possible exception of perfluoroalkanes. The water preferably is present in an amount of from 1.5 to 8, and more preferably in from 2 to 8 parts per 100 parts by total weight of polyahl. In a highly preferred embodiment of the invention, the blowing agent consists only of water. In a less preferred embodiment, water may be used in combination with one or more physical blowing agents including aliphatic hydrocarbons such as pentane, cyclopentane, hexane and cyclohexane; hydrogen-containing chlorofluorocarbons such as dichlorotrifluoroethane and dichlorofluoroethane; and polyfluorocarbons such astetrafluoroethane, decafluoropentane or dodecafluorohexane. In any event, advantageously the blowing agent is present in amount to provide the resulting foam with a free rise density of from 15 to 200, preferably from 20 to 150, more preferably from 20 to 100, and yet more preferably from 25 to 50 kg/m3. In addition to the foregoing critical components, it is often desirable to employ certain other ingredients when preparing the polyurethane foam. Among these additional ingredients are catalysts, surfactants, preservatives, colorants, antioxidants, reinforcing agents, fillers, and phosphorus-containing compounds which may function as adhesion promoters or flame retardants. In making polyurethane foam, it is generally highly preferred to employ a minor amount of a surfactant to stabilize the foaming reaction mixture until it cures. Such surfactants advantageously comprise a liquid or solid organosilicone surfactant. Other, less preferred surfactants include polyethylene glycol ethers of long chain alcohols, tertiary amine or alkanolamine salts of long chain alkyl acid sulfate esters, alkyl sulfonic esters and alkyl arylsulfonic acids. Such surfactants are employed in amounts sufficient to stabilize the foaming reaction mixture against collapse and the formation of large, uneven cells. Typically, from 0.2 to 5 parts of surfactant per 100 parts by weight polyahl is sufficient for this purpose. One or more catalysts for the reaction of the polyahl or water with the polyisocyanate are advantageously used. Suitable catalysts include tertiary amine compounds and organometallic compounds. Exemplary tertiary amine compounds include N- methyl morpholine, N-cocomorpholine, N-ethylmorpholine, triethylenediamine, pentamethyldiethylenetriamine. tetramethylethylenediamine, dimethyl cyclohexylamine, 1-methyl-4-dimethylaminoethylpiperazine, 3-methoxy-N- dimethylpropylamine, diethylethanolamine, N,N-dimethyl- N',N'-dimethyl isopropylpropylenediamine, N,N-diethyl-3- diethylaminopropylamine, and dimethylbenzylamine. Exemplary organometallic catalysts include organomercury, organolead, organoferric and organotin catalysts, with organotin catalysts being preferred among these. Suitable tin catalysts include stannous chloride, tin salts of carboxylic acids such as dibutyltin di-2-ethyl hexanoate, as well as other organometallic compounds such as are disclosed in U.S. Patent 2,846,408. A catalyst for the trimerization of polyisocyanates, such as an alkali metal alkoxide, carboxylate, including especially acetate, or quaternary amine salts, may also optionally be employed herein. Such catalysts are used in an amount which measurably increases the rate of reaction of the polyisocyanate. Typical amounts are from 0.001 to 3 parts of catalyst per 100 parts by weight of polyahl. Advantageously phosphorus-containing compounds may be present in an amount sufficient to impart a desired degree of flame retardancy to the foam. Typically such compounds are present in at least 4, preferably from 5 to 20, and more preferably from 7 to 15 parts per 100 parts by total weight of polyahl present. Suitable phosphorus-containing compounds, preferably halogen-free, for the purpose of flame retardancy include tris(chloroethyl)phosphate (TCEP), tricresylphosphate, tris(chloropropyl)phosphate TCPP), triethylphosphate (TEP), dimethylmethyl phosphonate (DMMP) and diethylethyl phosphonate (DEEP). Use of halogen-free phosphorus-containing compounds is preferred as this can reduce hazards associated with combustion products. Certain phosphorus-containing compounds have been observed to promote adhesion and cohesion properties of the foam and advantageously are present. Such compounds include cyclic organophosphorus-containing compounds including 1-alkyl, or aryl -1 - oxophospholene and -1 - thiophospholene compounds. Exemplary and preferred of such cyclic organophosphorus compounds include 1-methyl-1-oxophospholene, 1 -ethyl- 1 -oxophos¬ pholene, 1-propyl-1 -oxophospholene, or mixtures thereof. Advantageously, the cyclic phosphorus-containing compound is present in a quantity up to 5.0, preferably up to 4.0, and more preferably up to 3.0, and advantageously from at least 0.05, preferably from at least 0.1 , and more preferably from at least 0.2 weight percent based on total weight of polyahl(s). Other known adhesion promoting substances such as cyclic amide compounds including N-methyl pyrrolidinone may also be present. Mixtures of phosphorus-containing compounds for the purpose of promoting flame retardancy and foam adhesion may be present in the foaming process. To prepare polyurethane foam according to the present invention, the urethane- modified polyisocyanate, polyahl, blowing agent, and other optional additives are brought together at a temperature of from 15°C to and up to 60°C, preferably from 20°C to 40°C and more preferably from 20°C to 30°C and permitted to polymerize. The urethane-modified polyisocyanate is present in an amount to provide from 0.7 to 2, preferably from 0.9 to 1.5, and more preferably from 1.1 to 1.4 isocyanate group per isocyanate-reactive hydrogen atom present from the polyahl and water. The mixing apparatus and various types of mixing head and spray apparatus as conveniently used may be employed herein. It is often convenient, but not necessary, to preblend certain of the raw materials prior to reacting the polyisocyanate and polyahl. For example, it is often useful to blend the polyahl(s), blowing agent, surfactants, catalysts and other components except for polyisocyanates, and then contact this mixture with the polyisocyanate composition. Alternatively, all components can be introduced individually to the mixing zone where the polyisocyanate composition and polyahl(s) are contacted. Suitable procedures for the preparation of polyurethane foams are discussed in U.S. Patents RE 24514 and 3,821 , 130, and G .B. Patent 1 ,523,528. As mentioned in one aspect, this invention relates to a process for preparing a laminate article comprising a facing material having contiguous to it a rigid polyurethane foam prepared as above described. In such a process the above described urethane-modified polyisocyanate, polyahl, blowing agent and other optional additives are first brought together to give a polymerizing mixture which is then subsequently brought into contact with the facing material and permitted to terminate its polymerization reaction. To assist in termination of the polymerization reaction and promote optimum adhesion properties of foam to facing material, it is found advantageous to provide the facing material with a temperature of from 15°C to 60°C, preferably from 20°C, more preferably from 25°C, and preferably up to 45°C, more preferably up to 35 C C. The selection of the facing material is in accordance with suitability for its intended end application and can be a plastic resin, a cellulose-based material, a lignocellulose- based material or a metal sheet or foil. The polyurethane foam obtained as described hereinabove is observed to have attractive adhesion properties to notably metal surfaces and accordingly particularly suited to the manufacture of laminate articles comprising a metal facing material. The metal may be a metal sheet or metal foil of, for example, aluminum but preferably is steel. The average thickness of the metal sheet or foil is dependent on the application but typically will range from 0.001 to 10, usually from 0.1 to 5, and more usually from a bout 0.2 to 1.5 millimeters. Optionally, the surface of the metal which is to be in contact with the foam may be pretreated to enhance the adhesion between the foam and metal. As mentioned in another aspect, this invention is a two component polyurethane foam-forming system which comprises: (a) a urethane-modified polyisocyanate as described hereinabove; and (b) a polyahl composition. The polyahl composition comprises a polyahl as described hereinabove, and water in from 1 to 10 parts per 100 parts by weight of polyahl. Component (a) is present in from 25 to 75, preferably from 35 to 65 percent; and component (b) in from 75 to 25, preferably from 65 to 35 percent, based on total weight of components (a) and (b). The invention is illustrated by the foil owing examples in which all parts and percentages are by weight, unless otherwise stated. Where reported, properties of foams as obtained are observed according to the following test procedures; tensile strength - DIN 53292. Examples 1 to 13 A number of urethane-modified polyisocyanate compositions are prepared according to the following general procedure. An excess of Isocyanate A is reacted, at a temperature of 45°C to 60°C, with a given polyol; the resulting crude urethane-modified polyisocyanate is stabilized by addition of a trace amount of benzoyl chloride. Quantities of reacting components and characterizing data of the urethane-modified polyisocyanate so obtained are given in Table 1. Iso. A -VORANATE M220, a polymethylene polyphenyl- isocyanate mixture with an NCO content of 31.6 wt%, average functionality of 2.7, and containing 40 wt% methylene diphenylisocyanate isomers, available from The Dow Chemical Company. Polyol A - VORANOL P400, a 400 molecular weight polyoxypropylene diol, available from The Dow Chemical Company. Polyol B - VORANOL P1010, a 1000 molecular weight polyoxypropylene diol, available from The Dow Chemical Company. Polyol C - VORANOL P2000, a 2000 molecular weight polyoxypropylene diol, available from The Dow Chemical Company. Polyol D - VORANOL EP-1900, a 3800 molecular weight polyoxypropylene-oxyethylene diol (20 wt% oxyethylene), available from The Dow Chemical Company. Polyol E - VORANOL E400, a 400 molecular weight polyoxyethylene diol, available from The Dow Chemical Company. Polyol F - VORANOL CP1000, a 1000 molecular weight polyoxypropylene triol, available from The Dow Chemical Company. Polyol G - VORANOL CP3001, a 3000 molecular weight polyoxypropylene-oxyethylene triol (10 wt% oxyethylene), available from The Dow Chemical Company. Polyol H - VORANOL CP4702, a 4800 molecular weight polyoxypropylene-oxyethylene triol (18 wt% oxyethylene), available from The Dow Chemical Company. Polyol J - VORANOL CP6001 , a 6000 molecular weight polyoxypropylene-oxyethylene triol (14 wt% oxyethylene), available from The Dow Chemical Company. Polyol K - An experimental polyoxyethylene-oxypropylene triol (75 wt% oxyethylene; randomly distributed) with molecular weight of 1000. Polyol L - VORANOL CP1421 , a 5000 molecular weight polyoxypropylene-oxyethylene triol (75 wt% oxyethylene), available from The Dow Chemical Company. Polyol M - An experimental polyoxyethylene-oxypropylene triol (68 wt% oxyethylene; randomly distributed) with molecular weight of 7800. Polyol N - An experimental polyoxyethylene-oxypropylene polyol (68 wt% oxyethylene; randomly distributed) with molecular weight of 12000 obtained from an carbohydrate initiator mixture which has an average hydroxyl functionality of 6.9. The so prepared urethane-modified polyisocyanate composition are used to prepare a laminate comprising a steel facing sheet and contiguous to said sheet a polyurethane foam. The polyisocyanate is intimately mixed with the below given polyahl composition in an amount to provide for an isocyanate reaction index of 130 and the resulting reacting mixture poured in to a mold thermostated to 20°C and having dimensions of 200 x 200 x 40 mm, which is then subsequently closed. One face of the mold contains a steel facing of thickness of 1 mm. The amount of reacting mixture poured into the mold is sufficient to provide for a molded foam having an overall molded density of 70 kg/m 3 . The laminate comprising metal facing and molded polyurethane foam is removed from the mold after 15 minutes. Polyahl Composition: 32.5 parts VORANOL RN482, a sorbitol -initiated oxypropylene polyol with a molecular weight of 700, available from The Dow Chemical Company. 62 parts VORANOL CP1055, a 1000 molecular weight polyoxypropylene triol, available from The Dow Chemical Company. 1 part a 50:50 wt blend of silicon-based surfactants TEGOSTAB B1048 and B8427 available from Th Goldschmidt AG. 1.05 parts Catalyst mixture containing CURITHANE 206, a proprietary amine-based trimerization catalyst available from The Dow Chemical Company; NIAX A1 a proprietary amine-based catalyst available from Union Carbide Corp; and N,N-dimethylcyclohexylamine, present in a weight ratio of 12:8: 1. 3.5 parts water Properties, where observed, for the resulting foam are also given in Table 1. With reference to the "Saw test" the percentage value provides an indication of the number of laminate articles which broke at the foam/metal interface when being cut. A low percentage value or zero is indicative of a foam exhibiting strong adhesion to the metal. A foam exhibiting a high tensile strength is indicative of a product having attractive cohesive properties and being less susceptible to internal stress-strain failure. The reported data indicates demonstrates that use of urethane-modified polyisocyanates which are adducts of polyoxyalkylene triols result in better tensile strengths of the resulting foam than when using urethane-modified polyisocyanates which are adducts of polyoxyalkylene diols, as does use of polyoxyalkylene diols or triols having a higher molecular weight. When using urethane-modified polyisocyanates which are adducts of polyoxyalkylene polyols that have a significant oxyethylene content, the resulting foams exhibit an unexpectedly superior tensile strength. This is particularly well illustrated by Example 1 1 in comparison to Example 8 or 9 which relate to urethane-modified polyisocyanates that are adducts of polyoxyalkylene triol having a similar molecular weight but a substantially lower oxyethylene content. Example 14. Individual molded polyurethane foam laminates are prepared as described for Example 13, only in this case the mold temperatures are respectively 20°C, 30°C, 35°C, 40°C and 45°C. The maximum observed tensile strengths for the resulting foam are observed to be: 20°C Foam; 287 kPa 30°C Foam; 290 kPa 35°C Foam; 470 kPa 40°C Foam; 450 kPa 45°C Foam; 430 kPa Optimum tensile strength is observed at a temperature in the range of from 30°C to 35°C. Table 1. Example Example Example Example Example Example Example Example Example Example Example Example Example 1* 2* 3* 4* 5* 6* 7* 8* 9* 10* 11 12 13 VORANATE 2000 2000 2000 2000 2000 2000 2000 2000 2000 2000 2000 M220 (pbw) 2000 2000 Polyol (Type / pbw) A/214 B/292 C/333 D/356 E/212 F/263 G/330 H/349 J/356 K/263 L/349 M/361 N/324 Molecular weight 400 1000 2000 3800 400 1000 3000 4800 6000 1000 5000 7800 12000 Equivalent weight 200 500 1000 1900 200 333 1000 1600 2000 333 1666 2600 1740 wt % EO : PO 0: 100 0: 100 0: 100 20:80 100:0 0: 100 10:90 18:82 18:82 75:25 75:25 68:32 68:32 NCO % of 25.5 25.0 25.4 25.4 26.3 25.6 25.3 25.7 24.0 25.4 25.2 25.5 25.3 Polyisocyanate Viscosity of Polyisocyanate 2560 2040 972 852 2088 2280 1092 996 1140 / 1092 1140 1120 (cStat25°C) Foam Tensile / 35 97 134 / / 145 132 143 / 243 207 287 Strength (kPa) Saw Test, % 100 77 55 55 100 100 77 39 0 100 0 0 0 failure Not an example of this invention

Claims: 1. A process for preparing a rigid polyurethane foam by contacting under reaction conditions a urethane-modified polyisocyanate with a polyahl in the presence of a blowing agent characterized in that: a) the urethane-modified polyisocyanate has an isocyanate content of from 10 to 29 weight percent and is the reaction product of a polymethylene polyphenylisocyanate, having an average isocyanate functionality of from 2.5 to 3.5, with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent; b) the blowing agent comprises from 1 to 10 parts of water per 100 parts by weight of polyahl and is free of any perhalogenated hydrocarbon, with the exception of perfluoroalkanes, wherein the urethane-modified polyisocyanate is present in an amount to provide from 0*7 to 2 isocyanate groups per isocyanate-reactive hydrogen atom present from the polyahl and water. 2. A process as claimed in Claim 1 wherein the urethane-modified polyisocyanate is the reaction product of a polyoxyalkylene polyol which has at least 3 hydroxyl groups/molecule and a molecular weight of at least 3000. 3. A process as claimed in Claim 2 wherein the polyoxyalkylene polyol has a molecular weight of from 4000 to 12000 and an oxyethylene content of at least 50 weight percent. 4. A process as claimed in Claims 2 or 3 wherein the blowing agent consist of water. 5. A process for preparing a rigid polyurethane foam by contacting under reaction conditions a urethane-modified polyisocyanate with a polyahl in the presence of a blowing agent which consists of water, characterized in that: a) the urethane-modified polyisocyanate has an isocyanate content of from 22 to 27 weight percent and is the reaction product of a polymethylene polyphenylisocyanate having an average isocyanate functionality of from 2.7 to 3.2, with a polyoxyalkylene polyol that has a molecular weight of from 4000 to 12000 and an oxyethylene content of at least 50 weight percent; with b) the polyahl comprises a polyether polyol or a polyester polyol which has a molecular weight of from 200 to 15000; and c) the water is present in an amount of from 2 to 8 parts per 100 parts by weight of (b), wherein the urethane-modified polyisocyanate is present in an amount to provide from 0.9 to 1.5 isocyanate groups per isocyanate-reactive hydrogen atom present from the polyahl and water. 6. A process as claimed in Claim 5 in which is present a fire retardant additive comprising tricresyl phosphate, tri ethyl phosphate (TEP), dimethylmethyl phosphonate (DMMP) or diethylethyl phosphonate (DEEP). 7. A process as claimed in Claims 5 or 6 in which is present a phosphorus- containing foam adhesion or cohesion promoter compound comprising an 1 -alkyl- - oxophospholene, 1-aryl-1-oxophospholene orthe equivalentthiophospholene compounds. 8. A rigid polyurethane foam obtained according to the process of any one of the preceding claims. 9. A laminate comprising a facing material having contiguous to it a rigid polyurethane foam obtained by contacting under reaction conditions a urethane-modified polyisocyanate with a polyahl in the presence of a blowing agent to provide a polymerizing mixture which is brought into contact with the facing material and permitted to terminate its polymerization reaction, characterized in that: a) the urethane-modified polyisocyanate has an isocyanate content of from 10 to 29 weight percent and is the reaction product of a polymethylene polyphenylisocyanate, having an average isocyanate functionality of from 2.5 to 3.5, with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent; b) the blowing agent comprises from 1 to 10 parts of water per 100 parts by weight of polyahl and with the exception of perfluoroalkanes is free of any perhalogenated hydrocarbon, wherein the urethane-modified polyisocyanate is present in an amount to provide from 0.7 to 2 isocyanate groups per isocyanate-reactive hydrogen atom present from the polyahl and water, and wherein the facing material has a temperature of from 15°C to 60°C. 10. A laminate as claimed in Claim 9 wherein the blowing agent consists of water and wherein the facing material is a metal foil or sheet. 11. A two component rigid polyurethane foam-forming system which, based on total weight of (a) and (b) present, comprises: a) from 25 to 75 weight percent of a urethane-modified polyisocyanate that has an isocyanate content of from 10 to 29 weight percent and is the reaction product of a polymethylene polyphenylisocyanate having an average isocyanate functionality of from 2.5 to 3.5 with a polyoxyalkylene polyol having a molecular weight of at least 2000 and an oxyethylene content of at least 35 weight percent; and b) from 75 to 25 weight percent of a polyahl composition containing: (i) a polyether polyol or a polyester polyol which has a molecular weight of from 200 to 15000; and (ii) water in from 1 to 10 parts per 100 parts by weight of (b)(i).

Inventors: KELLER PETER, MUELLER ULRICH, OTTENS ANDREAS, KELLER, PETER, MUELLER, ULRICH, OTTENS, ANDREAS
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1994
Main classification: C08G18
IPC codes: B32B5, B32B27, C08G18, C08G101, C08J9