Vinyl- and alkoxy-functional organosilicon compounds and method for the preparation thereof

Abstract: Vinyl- and alkoxy-functional organosilicon compounds with the general formula in which R denotes C₁ to C₄ alkyl and a is 1, 2, or 3, b is 0 or 1, and a + b is 2 or 3 are made by an exchange reaction between sym-divinyltetramethyldisiloxane and vinyltrialkoxysilane or tetraalkoxysilane. These novel vinyl- and alkoxy-functional organosilicon compounds exhibit a high condensation reactivity with the silanol group.

Description: The invention relates to vinyl- and alkoxy-functional organosilicon compounds that contain alkoxy group which is highly reactive with the silanol group and to a method for their preparation A large number of alkoxy-functional organosilicon compounds in which alkoxy is bonded to silicon are already known. These are widely used as coupling agents for bonding glass fibers and organic resins and as chain extenders and crosslinkers for silicone polymers and organic polymers. Examples of these alkoxy-functional organosilicon compounds include monofunctional alkoxysilanes (1 silicon-bonded alkoxy group is present), difunctional alkoxysilanes (2 silicon-bonded alkoxy groups are present), trifunctional alkoxysilanes (3 silicon-bonded alkoxy groups are present), and tetrafunctional alkoxysilanes (4 silicon-bonded alkoxy groups are present). EP-A 0 480 680 describes a silicone rubber laminate comprising a dielectric layer formed from a silicone rubber composition in cured form comprising an organopolysiloxane containing alkenyl groups and an organosilicon compound having an alkenyl group per molecule and a methoxy group. From Chemical Abstracts, vol. 116, no. 22, 01 June 1992, abstract no. 215 662, alkoxysilanes for crosslinking of siloxanes at room temperature are known. Chemical Abstracts, vol. 116, no. 14, 06. April 1992, abstract no. 129 932y relates to silicone powders and their manufacture which are prepared from silanes containing a vinyl group and alkoxy groups. Chemical Abstracts, vol. 115, no. 25, 23 December 1991, abstract no. 280 283n describes the preparation of alkylsilyl-containing organosiloxanes, ie 2-methyl-1,1-diphenyl-3,3,3-trimethoxydisiloxane. As the number of alkoxy groups in these alkoxysilanes diminishes, the hydrolyzability of the alkoxy groups and their condensation reactivity with the silanol group decline. As a consequence, the difunctional and trifunctional alkoxysilanes are substantially less reactive than the tetrafunctional alkoxysilanes. This has created demand for alkoxy-functional organosilicon compounds that exhibit high reactivity for tetrafunctional alkoxysilanes. The inventors have proposed an alkoxy-functional organosilicon compound with the following formula for use as a chain extender in US Patent 5,300,612, issued April 5, 1994, to Toshio Saruyama, ((CH 3 ) 3 SiO) 2 Si(OCH 3 ) 2 . However, the alkoxy groups in this particular organosilicon compound do not have a very high condensation reactivity with the silanol group, and this compound is therefore not fully satisfactory for some applications. The vinyl-containing alkoxysilanes, as typified by vinylmethyldimethoxysilane and vinyltrimethoxysilane, contain a different type of alkoxy-functional group in terms of the alkoxysilyl moiety, and one would expect that they could also be used as chain extenders and crosslinkers. Unfortunately, the alkoxy group in these vinyl-containing alkoxysilanes also exhibits an unsatisfactory condensation reactivity with the silanol group. The invention provides vinyl- and alkoxy-functional organosilicon compounds with the general formula in which R denotes C 1 to C 4 alkyl and a is 1, 2, or 3, b is 0 or 1, and a + b is 2 or 3. Another aspect of this invention is a method for the preparation of a vinyl- and alkoxy-functional organosilicon compound with a general formula in which R denotes C 1 to C 4 alkyl and a is 1, 2, or 3, b is 0 or 1, and a + b is 2 or 3, comprising mixing sym-divinyltetramethyldisiloxane and vinyltrialkoxysilane or tetraalkoxysilane in the presence of an acid catalyst and heating at a temperature of from 70°C and 150°C promoting an exchange reaction between sym-divinyltetramethyldisiloxane and vinyltrialkoxysilane or heating at a temperature of from 70°C to 200°C promoting an exchange reaction between sym-divinyltetramethyldisiloxane and tetraalkoxysilane. The vinyl- and alkoxy-functional organosilicon compounds according to the present invention are expressed by the following general formula. in which R in the preceding formula denotes C 1 to C 4 alkyl and is exemplified by methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, and tert-butyl. Methyl and ethyl are preferred and the methyl group is particularly preferred. The subscript a has a value of 1, 2, or 3. the subscript b is 0 or 1. The sum of a - b is 2 or 3. The subject (vinyl + alkoxy)-functional organosilicon compounds are exemplified by compounds with the following formulas, (ViMe 2 SiO) 2 SiVi (OMe) 1 (ViMe 2 SiO) 1 SiVi(OMe) 2 (ViMe 2 SiO) 2 SiVi (OEt) 1 (ViMe 2 SiO) 1 SiVi (OEt) 2 (ViMe 2 SiO) 3 Si(OMe) 1 (ViMe 2 SiO) 2 Si(OMe) 2 (ViMe 2 SiO) 3 Si(OEt) 1 (ViMe 2 SiO) 2 Si(OEt) 2 As used herein, Vi represents a vinyl group, Me represents a methyl group, and Et represents an ethyl group. The (vinyl + alkoxy)-functional organosilicon compounds of this invention can be prepared by running an acid-catalyzed exchange reaction between symdivinyltetra-methyldisiloxane and vinyltrialkoxysilane or an acid-catalyzed exchange reaction between sym-divinyltetramethyldisiloxane and tetraalkoxysilane. The sym-divinyltetramethyldisiloxane, vinyltrialkoxy-silane, and tetraalkoxysilane used in our method are widely used in industry. Examples of such vinyltrialkoxysilanes are vinyltrimethoxysilane, vinyltriethoxy-silane, and vinyltri-n-propoxysilane. Examples of tetraalkoxy-silane are tetramethoxysilane, tetraethoxysilane, tetra-(n-propoxy)silane, and tetra-(isobutoxy)silane. In regard to the quantities of symdivinyltetramethyl-disiloxane and vinyltrialkoxysilane used in the method of the present invention, the standard addition is 1 or 2 moles of sym-divinyltetramethyldisiloxane per 1 mole of vinyltrialkoxysilane to introduce, respectively, 1 or 2 ViMe 2 SiO groups into the vinyltrialkoxysilane. In regard to the quantities of symdivinyltetra-methyldisiloxane and tetraalkoxysilane used in this method, when 2 or 3 ViMe 2 SiO groups are introduced into tetraalkoxysilane, the amount of sym-divinyltetramethyldisiloxane to be used with respect to 1 mole of tetraalkoxysilane is 2 or 3 moles, respectively. Any acid catalyst may be used in the method of the invention which does not have a negative influence on the reaction system. The acid catalyst is exemplified by acid-treated inorganic compounds such as activated clay, trifluorosulfonic acid, and dodecylbenzene-sulfonic acid. The reaction product afforded by the sym-divinyltetra-methyldisiloxane and vinyltrialkoxysilane exchange reaction comprises a mixture whose components are organosilicon compounds with the formula (ViMe 2 SiO) x SiVi(OR) 3-x . Hereinafter, R denotes C 1 to C 4 alkyl, x = 0 to 3. Vinyl- and alkoxy-functional organosilicon compounds of this invention can be obtained by distilling this mixture. One molecule of vinyldimethylalkoxysilane ViMe 2 SiOR is produced in this exchange reaction as by-product for each alkoxy group in the vinyltrialkoxysilane that is replaced by the group of the formula ViMe 2 SiO. Accordingly, the reaction is preferably promoted by distilling the former compound. The vinyldimethyl-alkoxysilane by-product can be hydrolyzed to make sym-divinyltetramethyldisiloxane, which can be re-used as starting material in the preparative method of our invention. Other organosilicon compound by-products can be re-used by addition to a subsequent exchange reaction. The subject exchange reaction begins at around 70°C and ultimately finishes at 100°C to 150°C. The temperature at which the vinyldimethylalkoxysilane by-product can be distilled rises as the reaction progresses. The acid catalyst is preferably eliminated from the reaction product after completion of the reaction, by neutralization and/or filtration of the reaction product. This reaction may be run in organic solvent. The product of the exchange reaction between symdivinyltetramethyldisiloxane and the tetraalkoxysilane is a mixture comprised of the organosilicon compounds represented by the formula (ViMe 2 SiO) y Si(OR) 3-y (where y represents a number 0, 1, 2, 3, or 4). By distilling said mixture, vinyl- and alkoxy-functional organosilicon compounds of this invention can be obtained. In this exchange reaction, each time one of the alkoxy groups in the tetraalkoxysilane is substituted by the group represented by the formula ViMe 2 SiO, one molecule of vinyldimethylalkoxysilane represented by formula ViMe 2 SiOR is generated as a by-product. Consequently, it is preferred that it be removed by distillation while the reaction is carried out. The vinyldimethylalkoxysilane by-product is hydrolyzed to sym-divinyltetramethyldisiloxane, which is recycled as the feed material in the manufacturing method of this invention. Also, other organosilicon compound by-products may be recycled to the exchange reaction. This exchange reaction starts at near 70°C, and it finally reaches completion at 150°C to 200°C. As the reaction progresses, the temperature at which the vinyldimethylalkoxysilane by-product can be removed by distillation is increased. After the reaction is complete, it is preferred that the reaction product be neutralized or filtered, to remove the acidic catalyst. Also, it is possible to carry out this reaction in the presence of an organic solvent. In the vinyl- and alkoxy-functional organosilicon compounds of this invention, a single silicon atom carries the alkoxy groups, vinyl group in some compounds, and dimethylvinylsiloxy groups. The alkoxy group has a high condensation reactivity with the silanol group as a result, while these compounds can also participate in other reactions by virtue of the presence of the vinyl group. The utilization of these distinguishing technical features makes the invention compounds extremely useful as coupling agents for bonding glass fibers and organic resins and as chain extenders and crosslinkers for silicone polymers and organic polymers. Compositions which cure at room temperature can be obtained by using the vinyl- and alkoxy-functional organosilicon compounds of this invention in combination with polydiorganosiloxanes with condensable groups, such as hydroxyl endblocked polydimethylsiloxane. Other ingredients can also be present with the condensable polydiorganosiloxane and vinyl- and alkoxy-functional organosilicon compounds of this invention, such as crosslinkers, fillers, and catalysts. These ingredients are well known in the art of making silicone sealants. The invention is further explained through the following working examples. The vinyl-and alkoxy-functional organosilicon compounds were determined by 1 H-nuclear magnetic resonance analysis and infrared spectroscopic analysis. The values reported for the viscosity were measured at 25°C. Figure 1 contains the infrared absorption spectrogram of the (vinyl + alkoxy)-functional organosilicon compound synthesized in Example 1. Figure 2 contains the 1 H-nuclear magnetic resonance spectrogram of the (vinyl + alkoxy)-functional organosilicon compound synthesized in Example 1. Figure 3 contains the infrared absorption spectrogram of the (vinyl + alkoxy)-functional organosilicon compound synthesized in Example 2. Figure 4 contains the 1 H-nuclear magnetic resonance spectrogram of the (vinyl + alkoxy)-functional organosilicon compound synthesized in Example 2. Figure 5 contains the IR absorption spectrum of the (vinyl + alkoxy)-functional organosilicon compound manufactured in Application Example 3 of this invention. Figure 6 contains the 1 H-NMR spectrum of the (vinyl + alkoxy)-functional organosilicon compound manufactured in Application Example 3 of this invention. Figure 7 contains the IR absorption spectrum of the (vinyl + alkoxy)-functional organosilicon compound manufactured in Application Example 4 of this invention. Figure 8 contains the 1 H-NMR spectrum of the (vinyl + alkoxy)-functional organosilicon compound manufactured in Application Example 4 of this invention. Example 1 The following were introduced into a 1-liter four-neck flask equipped with a stirrer, thermometer, and simple distillation setup: 296.4 g (2.0 moles) vinyltrimethoxysilane, 372.4 g (2.0 moles) sym-divinyltetramethyldisiloxane, and 6.7 g cation-exchange resin (Diaion™ RCP150HD from Mitsubishi Chemical Co. Ltd., Japan). A reaction was run with stirring and heating until the liquid temperature reached 100°C. Vinyldimethylmethoxysilane by-product was distilled from the reaction system during the course of the reaction. The reaction mixture was sampled at intervals during the reaction and the samples were analyzed by gas chromatographic analysis. The (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO)SiVi(OMe) 2 accounted for 35 to 40 weight% of the reaction mixture 20 hours after the start of the reaction. The reaction was stopped at this point, and, after cooling, the reaction mixture was filtered to eliminate the cation-exchange resin. The filtered reaction mixture was then fractionated on a Vigreux distillation setup to give 170 g of a crude fraction with a high content of (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO)SiVi(OMe) 2 . This crude fraction was subjected to vacuum distillation using a spinning band precision distillation apparatus to give 36 g (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO)SiVi(OMe) 2 at boiling point 71°C and 2.7 kPa (20 mmHg). This (vinyl + alkoxy)-functional organosilicon compound had a purity of 99% and a refractive index of 1.4080. Figure 1 shows the infrared absorption spectrogram of the (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO)SiVi(OMe) 2 produced in this example. Figure 2 depicts the 1 H-nuclear magnetic resonance spectrogram of the (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO)SiVi(OMe) 2 produced in this example. Example 2 A filtered reaction mixture obtained according to Example 1 was fractionated on a Vigreux distillation setup to give 45 g of a crude fraction with a high content of (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO) 2 SiVi(OMe). This crude fraction was subjected to vacuum distillation using a spinning band precision distillation apparatus to give 28 g (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO) 2 SiVi(OMe) at bp 102°C/20 mmHg (2.7 kPa). This (vinyl + alkoxy)-functional organosilicon compound had a purity of 98% and a refractive index of 1.4161. Figure 3 shows the infrared absorption spectrogram of the (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO) 2 SiVi(OMe) produced in this example. Figure 4 depicts the 1 H-nuclear magnetic resonance spectrogram of the (vinyl + alkoxy)-functional organosilicon compound with the formula (ViMe 2 SiO) 2 SiVi(OMe) produced in this example. Application Example 1 A (vinyl + alkoxy)-functional organosilicon compound according to the invention was evaluated for its reactivity with silanol-endblocked dimethylpolysiloxane. A mixture of 0.3 g of the (vinyl + alkoxy)-functional organosilicon compound prepared in Example 1 and 0.03 g dibutyltin dilaurate were mixed to homogeneity into 5 g silanol-endblocked dimethylpolysiloxane (viscosity = 12.5 Pa.s) to give a room-temperature curable organopolysiloxane composition. This composition was then held at ambient temperature. Its viscosity change, calculated according to the following equation, was determined after 3 hours to be 1280%. Viscosity Change (%) = Viscosity After 3 hours - Viscosity Immediately After Preparation Viscosity Immediately After Preparation x 100 For purposes of comparison, a room-temperature curable organopolysiloxane composition was prepared as above, but in this case using an organosilicon compound with the formula (Me 3 SiO) 2 Si(OMe) 2 in place of the (vinyl + alkoxy)-functional organosilicon compound prepared in Example 1 and used in Application Example 1. The viscosity change of this comparison composition, measured after 3 hours as above, was only 210%. Also for the purposes of comparison, a room-temperature curable organopolysiloxane composition was prepared, but in this case using methylvinyldimethoxysilane in place of the (vinyl + alkoxy)-functional organosilicon compound prepared in Example 1. The viscosity change of this composition, measured after 3 hours as above, did not exceed 101%. The preceding results make it clear that the (vinyl + alkoxy)-functional organosilicon compound of this invention, as prepared in Example 1, has a very high condensation reactivity with the silanol group. Example 3 152 g (1.0 mol) of tetramethoxysilane, 558.6 g (3.0 mol) of sym-divinyltetramethyldisiloxane, and 7.1 g of a cation-exchange resin (Diaion™ RCP150HD, a product of Mitsubishi Chemical Co., Ltd., Japan) were loaded into a 1-L four-necked flask equipped with a stirrer, a thermometer and a simple distillation apparatus. The contents were heated to a liquid temperature of 100°C, and the reaction was carried out with stirring. During the reaction process, the vinyldimethyl-methoxysilane by-product was removed from the reaction system by distillation. During the heated reaction process, the reaction product was sampled frequently for gas chromatographic analysis. It was found that at 36 hours after the beginning of the reaction, the content of the (vinyl + alkoxy)-functional organosilicon compound represented by formula (ViMe 2 SiO) 3 SiOMe was 25-30 wt%. The reaction was stopped at this point. After cooling, the obtained reaction mixture was filtered, and the cation-exchange resin was removed. Then, the filtered reaction mixture was loaded into a Vigreux fractionating apparatus for fractionation, from which 53.7 g of a crude fraction of distillate containing a large amount of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 3 SiOMe were obtained. The crude fraction of distillate was then subjected to distillation under a reduced pressure using a spinning-band precision fractionating apparatus, from which 36 g of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 3 SiOMe with a boiling point of 112°C/10 mm Hg (1.3 kPa) were obtained. The purity of the (vinyl + alkoxy)-functional organosilicon compound was 99.9%, and its refractive index was 1.4129. Figure 5 shows the IR absorption spectrum of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 3 SiOMe produced in this example. Figure 6 depicts the 1 H-NMR spectrum of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 3 SiOMe produced in this example. Example 4 The filtered reaction mixture, prepared in the same way as in Example 3, was loaded into a Vigreux fractionating apparatus for fractionation, from which 112.6 g of a crude fraction of distillate containing a large amount of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 2 Si(OMe) 2 were obtained. The crude fraction of distillate was then subjected to distillation under a reduced pressure using a spinning-band precision fractionating apparatus, from which 60 g of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 3 Si(OMe) 2 with a boiling point of 100°C/20 mm Hg (2.7 kPa) were obtained. The purity of the (vinyl + alkoxy)-functional organosilicon compound was 100%, and its refractive index was 1.4060. Figure 7 shows the IR absorption spectrum of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 2 Si(OMe) 2 produced in this example. Figure 8 depicts the 1 H-NMR spectrum of the (vinyl + alkoxy)-functional organosilicon compound represented by the formula (ViMe 2 SiO) 2 Si(OMe) 2 produced in this example. Application Example 2 The reactivity of the (vinyl + alkoxy)-functional organosilicon compound of this invention with respect to a dimethylpolysiloxane with both terminals blocked by silanols was evaluated. 5 g of dimethylpolysiloxane with both terminals blocked by silanols (viscosity of 12.5 Pa.s) were blended with a mixture of 0.3 g of the (vinyl + alkoxy)-functional organo-silicon compound obtained in Example 4 and 0.03 g of dibutyltin laurate to form an organopolysiloxane that can be cured at room temperature. After the composition was set at room temperature for 3 hours, the rate of change in the viscosity was measured, and was found to be 320%. The relative viscosity was determined by the formula as described in Application Example 1. In view of the comparisons shown in Application Example 1, it can be concluded that the alkoxyfunctional organosilicon compound obtained in Example 4 of this invention has a very high reactivity with respect to condensation with silanols. The (vinyl + alkoxy)-functional organosilicon compounds of the present invention are novel compounds that contain both the vinyl group and alkoxy, which is characterized by a high condensation reactivity with the silanol group. The preparative method of the invention has the capacity to produce the subject (vinyl + alkoxy)-functional organosilicon compounds in a highly efficient manner.

Claims: A vinyl- and alkoxy-functional organosilicon compound with a general formula in which R denotes C 1 to C 4 alkyl and a is 1, 2, or 3, b is 0 or 1, and a + b is 2 or 3. The vinyl- and alkoxy-functional organosilicon compound according to claim 1 in which R is methyl. A method for the preparation of the vinyl- and alkoxy-functional organosilicon compound of claim 1 comprising mixing symdivinyltetramethyldisiloxane and vinyltrialkoxysilane or tetraalkoxysilane in the presence of an acid catalyst and heating at a temperature of from 70°C and 150°C promoting an exchange reaction between symdivinyltetramethyldisiloxane and vinyltrialkoxysilane or heating at a temperature of from 70°C to 200°C promoting an exchange reaction between sym-divinyltetramethyldisiloxane and tetraalkoxysilane. A composition curable at room temperature comprising a polydiorganosiloxane with silicon bonded hydrolyzable groups and the vinyl- and alkoxy-functional organosilicon compound of claim 1.

Inventors: SARUYAMA TOSHIO, SUZUKI MASAHIKO, SARUYAMA, TOSHIO, SUZUKI, MASAHIKO, SARUYAMA, TOSHIO, C/O DOW CORNING TORAY SILICONE, SUZUKI, MASAHIKO, C/O DOW CORNING TORAY SILICONE
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LIMITED
Application year: 1994
Main classification: C07F7
IPC codes: C07F7, C08K5