Capillary made of plastics material for use in capillary electrophoresis and process for its production

Abstract: A capillary made of plastics material for use in capillary electrophoresis has its inner surface chemically modified for the generation of properties different from those of the original plastics capillary material. In a production process a premanufactured capillary is at least treated with a chemical reagent which generates functional groups directly on the capillary surface or generates attachment sites to which functional groups are bonded.

Description: This invention relates to a capillary made of plastics material for use in capillary electrophoresis. Capillary electrophoresis is widely applied in analytical and preparative separation processes in chemistry, biochemistry, and biotechnology. Conventional capillaries made of fused silica suffer from a number of drawbacks as they lack chemical stability with high pH values, lack physical stability under mechanical stress, and during operation they show poorly reproducible electroosmotic flow (EOF) values after an exchange of the buffer solution. Developments to overcome these drawbacks have provided capillaries made of synthetic polymer materials such as polyethylene (PE), polypropylene (PP), poly(vinyl chloride) (PVC), polyfluorocarbon (PFC), and the like, for example. Studies of the electrokinetic properties of PE, PVC and PFC capillaries in aqueous solutions in dependence on pH are reported by Schützner, W. and Kenndler, E. in: Anal. Chem. 64 (1992), p. 1991-1995. In the J. Microcolumn Separations, Vol. 5, No. 3, 1993, pages 246 and 247 it is described to coat the inner surface of hollow fibres of poly(butylene terephthalate) or polypropylene with polymers of acrylamide by graftcopolymerization. US patent 5,098,539 discloses a polymeric gel filled micro-capillary to the inner surface of which is adsorbed a bifunctional agent comprising ionic amine and active functional groups. EP application 452 055 A1 describes a capillary polymer surface provided with a covalently bonded interfacial layer with functional groups to reduce interactions with protein solutions. The capillaries made of silica or synthetic polymer materials both present another problem in the phenomenon of electro-endosmosis or electroosmotic flow which arises from an electrokinetic potential between the solid capillary wall and the liquid medium. A further problem with polymer capillaries is the adsorption of substrates to be separated to the capillary wall. These phenomena interfere with the mobility characteristics of the components involved and may deteriorate component separation efficiency and decrease resolution. It is an object of the present invention to provide a capillary made of plastics material for use in capillary electrophoresis which overcomes the problems known with capillaries as used in the state of the art, which can be prepared from commercially available base capillary material by easy procedure and in an inexpensive manner, which is reliable during application with a wide range of operational conditions, allows easy optical detection by means of common detectors, and has a long service life. This object is achieved by a capillary made of plastics material for use in capillary electrophoresis, wherein the inner surface thereof is chemically modified by the creation of active sites for the generation of functional groups chemically bonded to atoms of the base plastics material for the generation of properties different from those of the original plastics capillary material, characterized in that the amount of created functional groups is in the range of 3.5 x 10 -1 µM/m 2 to 3.5 x 10 -2 µM/m 2 . Suitable synthetic polymer materials for capillaries according to the invention are preferably non-conductive, thermoplastic polymers and copolymers, including polyethylene PE, polypropylene PP, polyamides PA, polyvinyl alcohol PVA, PVC, poly(butylene terephthalate) PBT, and the like, in particular polyfluorocarbon PFC, poly(tetrafluoroethylene) PTFE, and poly(etheretherketone) PEEK. In a perferred embodiment of the present invention the capillary is made of PEEK material. In another preferred embodiment the capillary is made of PTFE material. The base capillary material can be provided in the form of commercially available synthetic polymer hollow fibres having a cross section of substantially annular, or polygonal, or star shape, for example. In another embodiment of the present invention the capillary can be provided in the form of a plate made of synthetic polymer material with grooves introduced in an appropriate arrangement and an according cover to form a closed capillary system. In a further embodiment the capillary can be provided in the form of a plastic component of accordingly adapted shape with a capillary system comprised in the form of appropriate borings. The average inner diameters of the capillaries will usually be in the range of about 10 to 200 µm. According to the present invention, the created functional groups can be at least one or more types of hydrophilic groups. In another embodiment the created functional groups can be one or more types of hydrophobic groups. Advantageously the functional groups are part of created individual functional residues. Also, the functional groups can substantially be formed of the base plastics material. Preferably the amount of functional groups present in the modified polymer capillary material is multifold increased over the amount of functional groups found in general in the untreated original capillary material. In particular the amount of functional groups is at least 10 times, preferably at least 100 times increased over the amount found with the untreated polymer capillary. In the modified capillary according to the invention the functional groups can be chemically bonded to atoms of the base plastics material. The functional groups can be created from or are directly chemically bonded to sites of the base polymer capillary material which are created in addition to natural occurring active sites of the polymer. The functional groups may be indirectly chemically bonded to these sites of the base polymer capillary material, preferably by a spacer. Also, the functional groups can be both directly and indirectly bonded to the capillary material. Naturally, the types and numbers of bondings present may depend on the types and amounts of reagents used. Preferably, the functional residues are predominantly hydrophilic groups. In particular the functional groups can be hydroxyl groups. Also in particular, the functional groups can be amino groups or ammonium groups. The created functional residues can be low-molecular components. In particular, individual created functional residues can have less than 10 functional groups, preferably less than 5 functional groups. Further in particular, individual created functional residues have less than 30 carbon atoms, preferably less than 15 carbon atoms. On the other hand, the created functional residues can be high-molecular components. In particular high-molecular residues can be based on polyethylene polyamine with a molecular size of about 50000 Daltons or more. With particular advantage the functional groups can be of a type and be present in an amount adapted to effect a desired variation in electrochemical behaviour. Preferably, the functional groups are adapted to control the electroosmotic flow (EOF). The type and number of functional groups created depends on the type and amount of modification in the EOF desired. A thus modified capillary according to the invention is particularly adapted for the separation of proteins. Further examples for the application of chemically modified capillaries in electrophoresis include chemical analysis in inorganic and organic chemistry, water analysis, environmental analysis, clinical analysis, monitoring and quality control of synthetic chemical, biochemical and biotechnological products, and drugs. The functional property of the inner surface of a capillary modified according to the invention can be such that proteins do at most only reversibly adhere, preferably they do not at all adhere thereon. In the modified polymer capillary according to the invention, the functional groups can be non-ionic and/or ionic. The functional groups can be ionic with positive charge. Also, the functional groups can be ionic with negative charge. Methods to create functional groups in the base polymer capillary material according to the present invention comprise any methods which alone or in combination are adapted to provide reactive sites or functional groups in the organic molecules of the surface of the plastics material. In particular, functional groups can be created in the capillary material by oxidation reactions. Also, functional groups can be created by reduction reactions. Further, functional groups can be created by elimination reactions. Carriers of functional groups and/or functional groups can be introduced to the capillary material by addition reactions. Also, they can be introduced by condensation reaction. Naturally, the type of reaction involved depends on the type of reactants used and can thus be selected according to the desired modification. With capillaries made of nontransparent plastics material, an optical passage is provided to allow optical detection. In particular according to the invention, an optical passage is provided by sealingly inserting an optically permeable member. In one embodiment of the present invention, a wall section of the capillary is substituted by optically permeable material. Preferably, an optically permeable capillary section, preferably made of plastics material, can sealingly be inserted. Advantageously such a detection capillary section has a length of about 1 cm, a minimum inner diameter larger than or equal to the inner diameter of the plastics capillary, and a maximum inner diameter smaller than or equal to the outer diameter of the plastics capillary. In another preferred embodiment of the present invention, there can be at least two optical windows on opposite sides of the capillary, whereby in particular at least one optical lens be inserted. Optionally, there can be two or more detection windows be provided in the capillary at appropriate locations. Any capillary materials which are permeable to the radiation used for detection, in particular to UV radiation, can be applied as detection window materials. Preferably, the detection window can be inserted in the capillary after completion of the capillary surface modification. The above described optical passage to allow optical detection with capillaries made of nontransparent materials can be provided with any capillary material, preferably made of plastics material, be it modified according to the present invention, or modified according to any other method known in the art, or unmodified. The present invention relates as well to a process for the production of a capillary made of plastics material for use in capillary electrophoresis, wherein a premanufactured capillary is at least treated with a chemical reagent to chemically modify the inner surface thereof for the creation of active sites for the generation of functional groups which are chemically bonded to atoms of the base plastics material for the generation of properties different from those of the original plastics capillary material, characterized in that the functional groups are generated in an amount in the range of 3.5 x 10 -1 µM/m 2 to 3.5 x 10 -2 µM/m 2 . Preferably, according to the invention, active sites can be created on base polymer material chains. The active sites thus created can serve as functional groups to form a modified capillary material. In another embodiment of the present invention, the creation of active sites is a pretreatment step, with the thus created sites serving as attachment points for functional groups. The amount of reactive sites created exceeds the amount of reactive sites in the untreated polymer capillary material considerably. Preferably, the number of functional reactive sites is multifold increased over the amount of functional groups found in the untreated capillary material, preferably it is at least 10 times, preferably at least 100 times increased over the amount found with the untreated polymer capillary. As compared to silica capillaries which have an amount of functional groups, e. g. OH groups, corresponding to about 3.5 µM/m 2 , the amount of functional groups present in a capillary modified according to the invention is considerably lower, in particular in the range of 1/10 to 1/100, i. e. 3.5 x 10 -1 µM/m 2 to 3.5 x 10 -2 µM/m 2 , even after activation treatment. Pretreatment methods for chemical activation of capillaries made of polymer material according to the present invention comprise redox reactions, preferably oxidation reactions using strong oxidants or reduction reactions using strong reductive agents. Appropriate reagents for the aforementioned redox reactions are usually known as corrosive media including chlorate, sulphuric acid, metal hydrides, metal organic compounds, for example. Also, pretreatment methods for capillaries made of polymer material comprise elimination reactions. Appropriate elimination reactants include metal organic compounds. These pretreatments usually have an erosive action on the base polymer capillary material. The chemically activated polymer material can be modified by subjecting it to at least one or more subsequent reaction steps. In one embodiment of the process according to the present invention, preformed carriers of functional groups can be introduced to the base polymer capillary material. In another embodiment, residues can be generated directly from the base plastics material on the capillary surface. Advantageously, carriers of functional groups are chemically bonded to polymer chains in the capillary surface. Also, the carriers of functional groups or functional groups can be chemically bonded via a spacer to polymer chains in the capillary surface. Further in the process according to the invention, the carriers can be chemically bonded via a linking member to polymer chains in the capillary surface, wherein preferably the linking member is introduced first and subsequently the functional group is bonded thereon. Advantageously, the linking member can act as a spacer. Examples of further modification steps with PEEK capillaries subsequent to oxidative activation comprise further activation using carbonyl diimidazole or carbodiimide followed by reaction with an amine or polyamine to yield a PEEK amine derivative, or amidation using a polyamine to yield a PEEK amine derivative which results to an inversion of the EOF behaviour. Another modification step for PEEK pretreated by oxidation is esterification using chitosan, which results to an elimination of the EOF effect. Examples of further modification steps with PTFE capillaries subsequent to a fluorine elimination pretreatment step comprise hydroboration using boran in tetrahydrofuran to yield OH functional groups, or bromation followed by amination to yield NH 2 functional groups, or reaction with maleic acid anhydride to form reactive COOH groups followed by reaction with carbonyl diimidazole to yield carbodiimide functional groups, or oxidation using oxygen or H 2 SO 4 and KClO 3 to yield oxidized PTFE, or reaction using acrylamide to yield polyacrylamide functional groups. The present invention is further described with reference to the accompanying drawings in which: figure 1 is a comparison of an untreated and an oxidized PEEK capillary under separation conditions of L = 20/27, E = 540 V/cm, 10 mM phosphate buffer pH 7, trimethylphenylammonium bromide (1), benzyl alcohol (2) figure 2 is an electropherogram of an autolysate of trypsin in an oxidized PEEK capillary under separation conditions of L = 29/35.5 cm, 50 µm ID, 10 mM phosphate buffer pH 3.0 figure 3 is a separation of carboanhydrase in an oxidized PEEK capillary under separation conditions of L = 29/35.5 cm, 50 µm ID, 100 mM TRIS/boric acid pH 8.3, carboanhydrase (2), benzyl alcohol (1) figure 4 is a diagram of the measurement of stability of a PEEK capillary covered with polyimine under separation conditions of L = 20/27 cm, E = 500 V/cm, phosphate buffer 10 mM pH 6, EOF marker: benzyl alcohol, detection window: 1.5 cm silica capillary, 50 µm ID, PEEK capillary: 50 µm ID figure 5 is an electropherogram of tosylate and benzyl alcohol on a TEPA capillary with inversed EOF under separation conditions of L = 20/27 cm, 50 µm ID, 10 mM phosphate buffer pH 3 (TEPA = tetraethylenepentamine) figure 6 is a comparison of migration times on an untreated and a TEPA-PTFE capillary under separation conditions of L = 20/27 cm, 10 mM phosphate buffer pH 3 figure 7 is an electropherogram of lysocyme, cytochrome C, trimethylphenylammonium bromide (TMA) on an PTFE capillary activated by reaction with linear polyacrylamide under separation conditions of L = 20/27 cm, 50 µm ID, 10 mM phosphate buffer pH 7, separation current 15 kV figure 8 is a schematic illustration of a detection capillary showing the connecting portion of two capillaries unpermeable to UV radiation figure 9 is a schematic illustration of a detection capillary including spherical lenses. The detection capillary shown in fig. 8 is made of PEEK capillary material (1) which is unpermeable to UV radiation. The base capillary is cut off and has a capillary section made of silica (2) which is permeable to UV radiation inserted. Pieces of capillary made of plastics material (3) are provided as sealing connecting parts. The connecting portion does not exhibit a dead space. The detection capillary shown in fig. 9 is comprised of a nontransparent plastics capillary (4) which is cut off, an outer plastics capillary (5) with borings which include each a focusing spherical lens (6). The outer plastics capillary is sealingly arranged and has a relatively thicker wall. The boring is provided in transvere direction to the capillary axis, and in each of the openings is inserted a spherical lens to focus radiation in the capillary axis. The present invention is further described in more detail by the following examples of preferred embodiments which are, however, in no way intended as limitations. Example 1 A premanufactured untreated PEEK hollow fibre capillary is first subject to an oxidative treatment. A solution of 2.5 % KClO 3 in H 2 SO 4 /H 2 O (1 : 1 v/v) is passed through the capillary at room temperature. The thus effected change in electroosmotic flow properties are illustrated in the electropherograms as shown in the accompanying figures 1, 2 and 3. Example 2 A PEEK capillary pretreated by oxidation as described in example 1 is reacted with polyethylene polyamine. The preoxidized PEEK capillary is filled with 10 % polyethylene polyamine solution in methanol/water (4 : 1 v/v) which is subsequently sucked out and the capillary then dried at 200 °c in an air stream. At pH 6 thus treated capillaries show an inverted EOF which remains constant over numerous measureing cycles. Results are presented in figure 4. Example 3 A PEEK capillary pretreated by oxidation as described in example 1 is further activated by reaction with carbodiimide solution. Subsequently the carbodimide derivated PEEK capillary is reacted with an amine solution to form the according amine derivative. Example 4 A PEEK capillary pretreated by oxidation as described in example 1 is further reacted with SOCl 2 , subsequently followed by an amidation reaction. Example 5 A PEEK capillary pretreated by oxidation as described in example 1 is further treated with SO 3 vapours to effect sulphonation of the polymer capillary material on the inner surface. Example 6 A premanufactured untreated PTFE hollow fibre capillary is activated by a strong reductive agent in the presence of a strong base. 0.77 % (w/v) benzoin solution in a 2.9 % potassium tertiary butylate solution in dimethylsulfoxide are passed through the capillary at 50 °C under exclusion of air. Fluor elimination results to unsaturated polymer chains on the capillary inner surface which are adapted for furhter derivatization. Example 7 A PTFE capillary pretreated as described in example 6 is reacted with 0.2 molar bromine solution in CCl 4 . Following to this further activation step of Br addition, the capillary material is reacted with a 20 % hexamethylene diamine solution in diethylene glycol monoethyl ether at 80 °C. This results to the according amine derivative of the capillary polymer material. At pH 7 the EOF is considerably decreased as compared to the EOF of the untreated PTFE capillary.At pH 3 there is an inversed EOF found. Results for the anion tosylate are presented in the electropherogram as shown in figure 5. A comparison of migration times for the untreated and treated PTFE capillary is shown in figure 6. Example 8 A PTFE capillary pretreated as described in example 6 is reacted with borane in tetrahydrofuran (THF) and subsequently oxidized to the alcohol derivative. Example 9 A PTFE capillary pretreated as described in example 6 is reacted with ammonium persulphate and tetraethyl methylene diamine (TEMED) to introduce acrylamide to the activated polymer capillary material. The performance of the thus modified PTFE capillary in the separation of cytochrome C and lysozyme is presented in figure 7. Example 10 A PEEK capillary is reacted in a reduction step with lithium organic hydride dissolved in dry tetrahydrofuran at room temperature for up to 10 h. Subsequently the capillary is flushed first with aqueous basic and then with acidic solutions, then flushed with organic solvents like tetrahydrofuran. The capillary is subject to drying at room temperature for 25 h. Thus the original carbonyl groups of the base polymer capillary material are modified to OH groups showing improved hydrophilic properties. Example 11 A PEEK capillary is reacted in a Wittig reaction using methyltriphenyl phosphonium bromide and dimethylsulfoxide in a strong basic solution which is passed through the capillary at elevated temperature. Subsequently the capillary is flushed with dimethylsulfoxide and then with organic solvents like tetrahydrofuran. The capillary is subject to drying at room temperature. Thus the ketone groups of the polymer chains of the capillary inner surface are modified to olefin groups showing improved hydrophobic properties.

Claims: A capillary made of plastics material for use in capillary electrophoresis wherein the inner surface thereof is chemically modified by the creation of active sites for the generation of functional groups chemically bonded to atoms of the base plastics material for the generation of properties different from those of the original plastics capillary material, characterized in that the amount of created functional groups is in the range of 3.5 x 10 -1 µM/m 2 to 3.5 x 10 -2 µM/m 2 . A capillary according to claim 1, wherein the created active sites are used as such as functional groups in capillary electrophoresis. A capillary according to claim 1, wherein the created active sites are used as attachment sites to which functional groups or carriers of functional groups are bonded. A capillary according to any of claims 1 to 3, wherein the capillary material is made of poly(etheretherketone) (PEEK). A capillary according to any of the preceding claims, wherein the functional groups are ionic and/or non-ionic groups present in a number and surface distribution to effect a desired variation in electrochemical behaviour, in particular in respect to define a specific electroosmotic flow (EOF). A capillary according to any of the preceding claims, wherein the functional groups are one or more types of hydrophilic groups to allow separation of proteins. A capillary according to any of the preceding claims, wherein the functional groups are one or more types of hydrophobic groups to allow separation of proteins. A capillary according to any of the preceding claims, wherein with nontransparent plastics material, an optical passage is provided to allow optical detection. A capillary according to any of the preceding claims, wherein an optical passage is provided by sealingly inserting an optically permeable member. A capillary according to claim 9, wherein the optically permeable member is at least one optical lens. A process for the production of a capillary made of plastics material for use in capillary electrophoresis, wherein a premanufactured capillary is at least treated with a chemical reagent to chemically modify the inner surface thereof for the creation of active sites for the generation of functional groups which are chemically bonded to atoms of the base plastics material for the generation of properties different from those of the original plastics capillary material, characterized in that the functional groups are generated in an amount in the range of 3.5 x 10 -1 µM/m 2 to 3.5 x 10 -2 µM/m 2 . Process according to claim 11, wherein this treatment generates functional groups directly in the base polymer material of the capillary. Process according to claim 11, wherein this treatment generates attachment sites to which functional groups are bonded directly in the base polymer material of the capillary. A process according to any of claims 11 to 13, wherein preformed carriers of functional groups are introduced. A process according to any of claims 11 to 14, wherein functional groups and/or carriers of functional groups are chemically bonded to the capillary surface. A process according to any of claims 11 to 15, wherein carriers of functional groups are chemically bonded via a spacer to the capillary surface. A process according to any of claims 11 to 16, wherein the carriers are chemically bonded via a linking member to the capillary surface. A process according to claim 17, wherein the linking member is introduced first and subsequently the functional groups is bonded thereon. A process according to claims 17 and 18, wherein the linking member acts as a spacer. A process according to any of claims 11 to 19 wherein the functional groups are created by an erosive pretreatment of the inner surface of the capillary base polymer material and bonding of functional groups thereon.

Inventors: ENGELHARDT HEINZ, SCHMITT THOMAS, SHOIKET KONSTANTIN, ENGELHARDT, HEINZ, SCHMITT, THOMAS, SHOIKET, KONSTANTIN
Applicants: HEWLETT PACKARD GMBH, HEWLETT-PACKARD GMBH
Application year: 1994
Main classification: G01N27
IPC codes: G01N27