Binders, their preparations and use

Abstract: A low formaldehyde, high gel fraction latex binder is made utilizing a compound having the formula or wherein R and R', independently, is an alkyl having from 1 to 10 carbon atoms, and R⁴ is hydrogen, or wherein R³ and R⁴, independently is an alkyl, an aromatic, or combinations thereof having from 1 to 10 carbon atoms, or wherein said R³ and R⁴ are connected to form an internal amide, and wherein the isopropenyl group is either in the ortho, meta or para position. The latex binder is generally an emulsion or latex copolymer made from various monomers including at least one or more conjugated dienes having a total of from 4 to 10 carbon atoms with butadiene being preferred and from one or more vinyl-substituted aromatics having from 8 to 14 carbon atoms, with styrene being preferred. The amount of the above formulation compounds is generally from about 0.25 to about 20 parts by weight based upon 100 parts by weight of the one or more conjugated dienes and the vinyl-substituted aromatic monomers. The latex binder has good stability, and has many applications such as to bind a paper-coating composition to a cellulose substrate, or to bind non-woven fibers together. The latex binder generally contains 10 parts or less by weight of formaldehyde per million parts by weight and desirably contains nil, that is, no detectable amounts of formaldehyde therein, even after extended periods of time, e.g., 28 days.

Description: This specification relates to high gel fraction polymeric binders and latex compositions thereof e.g. such as are utilized for paper coating compositions, for binding non-woven fibres together, and to processes for making and using the same. More particularly, the disclosure proposes such high gel fraction polymeric latex binder compositions wherein formaldehyde generation can be substantially eliminated. BACKGROUND Latex binder compositions have been used in a wide variety of applications such as adhering paper coatings to cellulosic substrates, in carpet and rug backings, and in various non-woven products which have gained broad acceptance as replacements for woven fabrics, including such articles as facings or top sheets in diapers, incontinence pads, sanitary napkins, hospital gowns, and other single and multiple-use non-woven products. Conventional latex binders have generally been prepared from acrylic polymers, styrene/acrylate copolymers, or styrene/butadiene copolymers containing N-methylol functionality which, upon curing, generate substantial quantities of formaldehyde, typically from 200 to 500 ppm or more. It is desirable to use binders which are essentially free of formaldehyde generation. Formaldehyde-free latex binders include various urethane polymers, acrylic polymers, styrene/acrylate copolymers, and the like, such as those disclosed in U.S. Patents Nos. 2,837,462; 4,207,367; 4,381,332; 5,030,507, and others. However, none of the prior art discloses a suitable conjugated diene/vinyl-substituted aromatic copolymer latex binder which is free of formaldehyde formation. Furthermore, coagulation stability and mechanical stability while imparting excellent wet tensile strength to cellulosic articles (such as paper) are desirable properties to achieve in a latex binder generally. We note that EP-A-596 291, with an earlier filing date but published after the filing date of the present application, discloses a range of room-temperature curable binder copolymers which may include oxime-blocked m- or p-isopropenyl-α,α'-dimethylbenzyl isocyanate for crosslinking. On removal of solvent this reacts with ketone or aldehyde-functional monomers included specially in the composition. Other monomers are typically acrylate, although styrene and butadiene are listed as options. In the present invention we provide in a first aspect a high gel fraction latex binder composition comprising an aqueous dispersion of a binder polymer which is the polymerisation reaction product of (a) 100 parts by weight of a primary comonomer combination consisting of from 10 to 90 wt% C 4-8 conjugated diene monomer and from 90 to 10 wt% C 8-12 vinyl-substituted aromatic monomer; (b) from 0.1 to 15 parts by weight of at least one functional-group-containing monomer; (c) from 0.5 to 20 parts by weight of ketoxime- or amide-blocked isopropenyl α,α-dimethyl benzyl isocyanate crosslinking agent of the formula in which R and R' independently are C 1-10 alkyl groups, or in which R 3 is C 1-10 alkyl, aryl or alkyl-aryl, and R 4 is H or C 1-10 alkyl, aryl or alkyl-aryl; R 3 and R 4 optionally being connected to form a cyclic amide; the binder being curable by heating to a crosslinking temperature at which thermal deblocking of the blocked isocyanate takes place to generate free isocyanate groups. Other aspects are a process of making the composition using emulsion polymerisation (claim 23), its use for binding paper coating to a cellulosic substrate and the product thereof (claims 26,27), and its use for binding non-woven non-cellulosic fibres and the resulting articles (claims 28,29). We have found that such high gel fraction latex binder compositions, made from one or more conjugated diene monomers, one or more vinyl-substituted aromatic monomers, a ketoxime or amide blocked isopropenyl-α-α-dimethyl benzyl isocyanate, and one or more monomers containing functional groups such as hydroxyl, carboxyl, or primary or secondary amides can be prepared without generating significant quantities of formaldehyde. In our work we have also found that the foregoing binder compositions, described in greater detail hereinafter. can exhibit unexpectedly good coagulation as well as mechanical stability, and impart notably good wet tensile strength when applied to cellulosic articles. The polymeric latex binder compositions may include residues of secondary monomer such as one or more ester monomers, vinyl chloride or vinylidene chloride monomers, and various stabilizer monomers. The above monomers when containing low amounts of conjugated diene, i.e. less than 60 percent by weight, are polymerized under acidic conditions and high temperatures High conversion levels of at least 90 percent form a high gel fraction (e.g. at least 70 percent) latex binder which upon application to a substrate can be cured, i.e. crosslinked, upon heating. BRIEF DESCRIPTION OF DRAWINGS Fig. 1 relates to a cross-sectional view of a paper coating bound to a cellulose substrate with a latex binder; Fig. 2 relates to a cross-sectional view of non-woven fibers bound to one another with a latex binder. DETAILED DESCRIPTION Binder-forming monomers suitable for forming the emulsion or latex binder composition (i.e., an aqueous suspension of a copolymer) are generally well known to the art and to the literature and include a primary, sizeable or main amount of at least a conjugated diene monomer and a vinyl-substituted aromatic monomer, as well as smaller amounts of various functional groups containing monomers. Optional monomers include various esters, vinyl chloride or vinylidene chloride, acrylonitrile, and the like. The conjugated diene monomers contain from 4 to 8 carbon atoms, and desirably from 4 to 6 carbon atoms. Examples of specific diene monomers include piperylene, isoprene, 2,3-dimethyl-1,3-butadiene, and preferably 1,3-butadiene. Mixtures of two or more conjugated dienes can also be utilized. The vinyl-substituted aromatic monomers which are utilized in association with the conjugated dienes to form copolymers have from 8 to 12 carbon atoms. Specific examples include α-methyl styrene, p-tertiary butyl styrene, methyl vinyl toluene, p-vinyl toluene, 3-ethyl styrene, and the like, with styrene being preferred. Mixtures of two or more vinyl-substituted aromatic monomers can also be utilized. The amount of the one or more conjugated diene monomers which can be utilized is generally small in comparison to latexes utilized for tyres, ranging from 10 to 90 percent based upon the total amount by weight of the conjugated diene monomers and the vinyl-substituted aromatic monomers. With regard to non-woven applications, the desired range is from 25 to 55 or 60 percent and preferably from 30 to 50 percent by weight. The amount of vinyl-substituted aromatic monomers is generally the difference, that is, from 10 to 90 percent by weight, and with regard to non-woven applications from 40 or 45 percent to 75 percent by weight, and preferably from 50 to 70 percent by weight. With regard to cellulose applications, the desired amount of conjugated diene monomers is from 15 to 50 percent by weight and preferably from 25 to 40 percent by weight. The amount of the vinyl-substituted aromatic monomers for cellulose applications is generally the difference, that is generally from 50 percent to 85 percent and preferably from 60 percent to 75 percent by weight based upon the total weight of vinyl-substituted aromatic and conjugated diene monomers. Examples of monomers containing functional groups include various unsaturated acids and various unsaturated amides or derivatives thereof having a total of from about 3 to about 12 carbon atoms with the exception of N-methylol-functional ethylenically unsaturated monomers. Acid monomers are desired since they improve colloidal stability as well as adhesion to a substrate. The amount of such monomers is from 0.1 to 15 parts by weight, desirably from 0.5 to 10 parts, and preferably from 1.0 to 5.0 parts by weight for every 100 parts by weight of the one or more conjugated diene and vinyl-substituted aromatic monomers. Examples of such suitable monomers include acrylic acid (preferred), methacrylic acid, maleic acid, fumaric acid, itaconic acid (preferred), hydroxyethyl acrylate (a preferred compound), hydroxyethyl methacrylate, hydroxymethyl acrylate, hydroxymethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, (meth)acrylamide (preferred), dimethylacrylamide, derivatives of the various amide containing monomers, and combinations of the foregoing. The present compositions are generally free from N-methylol-functional ethylenically unsaturated monomers including N-methylolamides of ethylenically unsaturated carboxylic acids having 3-10 carbons, such as N-methylolacrylamide, N-methylolmethacrylamide, N-methylolmaleimide, N-methylolmaleinamic acid, N-methylolmaleinamic acid esters, N-methylolamides of the vinyl aromatic acids such as N-methylol-p-vinylbenzamide, and the like. Also essentially excluded or absent from the present latex-forming monomers are mixtures of various N-methylol-functional monomers such as mixtures of N-methylolacrylamide and acrylamide and mixtures of N-methylolmethacrylamide and methacrylamide. If any of such compounds are utilized, the amount is very minute, such as 0.1 part or less and desirably 0.05 parts or less by weight based upon 100 parts by weight of the total monomers, or effective amounts which yield generally 10 parts or less per million and desirably 5 parts or less, or 3 parts or less, or even 2 parts or less of formaldehyde per million of latex binder. The binders can thus be essentially free of any chemical functional group (e.g. OH, NH 2 , COOH) crosslinks, although perhaps contain very minor inherent crosslinking obtained by the reaction of the various unsaturated, non-functional groups (i.e. solely hydrocarbon) such as those in divinyl benzene. The chemical crosslinking which does occur to form the high-gel content of the latex binder composition is thought generally to occur through the remaining unsaturated groups of the reacted diene monomer Should the gel content not be high enough, monomers generating non-functional crosslink structures can be utilized such as divinyl benzene discussed more fully hereinbelow. Optional esters which are often utilized to improve ink gloss coating properties in paper applications include the various alkyl (meth)acrylate and hydroxyl derivatives thereof, wherein the alkyl portion has from 1 to 10, preferably from 1 to 4 carbon atoms with specific examples including butyl acrylate, 2-ethylhexyl acrylate, propyl acrylate, ethyl acrylate, and the like. The amount of such ester monomers is generally from 0.1 to 10 parts by weight, and preferably from 1.0 to 5 parts by weight for every 100 parts by weight of the one or more vinyl substituted aromatic and conjugated diene monomers. Optionally, vinyl chloride and vinylidene chloride monomers or combinations thereof can be utilized in amounts from 0.1 up to 35 parts by weight and preferably from 5 percent to 20 parts by weight for every 100 parts by weight of the one or more vinyl-substituted aromatic and conjugated diene monomers. Another optional monomer is acrylonitrile which can be utilized in an amount of from 0.1 to 25 and desirably from 5 to 15 parts by weight for every 100 parts by weight of the one or more vinyl-substituted aromatic and conjugated diene monomers. Other conventional monomers can optionally be utilized in conventional amounts such as various organic salts, for example sodium styrene sulfonate or the 3-sulfopropyl(meth)acrylate salt of sodium or potassium to control particle size. The above monomers can be polymerized in the presence of water to form the latex binder, e.g. in accordance with conventional emulsion polymerization procedures and techniques. In addition to these monomers, free-radical initiators, optional chain transfer agents, various emulsifiers (such as anionic surfactants), chelating agents, and the like can be utilized as set forth in U.S. Patent No. 5,166,259, to Schmeing and White. The free-radical initiators utilized to polymerize the various above latex binder-forming monomers include sodium persulfate, ammonium persulfate, potassium persulfate, and the like. Other free-radical initiators can be utilized which decompose or become active at the temperature utilized during polymerization such as various peroxides, e.g., cumene hydroperoxide, dibenzoyl peroxide, diacetyl peroxide, dodecanoyl peroxide, di-t-butyl peroxide, dilauryl peroxide, bis(p-methoxy benzoyl) peroxide, t-butyl peroxy pivalate, dicumyl peroxide, isopropyl percarbonate, di-sec-butyl peroxidicarbonate; various azo initiators such as azobisdimethylvaleronitrile, 2,2'-azobisisobutyronitrile, 2,2'-azobis(2-amidinopropane) dihydrochloride, 2,2'-azobis-2-methyl-butyronitrile, 2,2'-azobis(methylisobutyrate), and the like, and mixtures thereof. The amount of the free-radical initiators is generally from about 0.25 to about 2.0, and preferably from about 0.5 to about 1.5 parts by weight for every 100 parts by weight of the total monomers. Optional chain transfer agents include mercaptans such as the alkyl and/or aryl mercaptans having from 8 to about 18 carbon atoms and preferably from about 12 to about 14 carbon atoms. The tertiary alkyl mercaptans having from 12 to 14 carbon atoms are highly preferred. Examples of suitable mercaptans include n-octyl mercaptan, n-dodecyl mercaptan, t-octyl mercaptan, t-dodecyl mercaptan, tridecyl mercaptan, tetradecyl mercaptan, hexadecyl mercaptan, and the like, as well as mixtures thereof. The amount of the chain transfer agent utilized is generally from about 0.01 to about 5 parts by weight and desirably from about 0.1 to about 1.0 part by weight for every 100 parts by weight of the total monomers. The emulsifiers can generally be any surfactant, soap, or the like, which are well known to the art and to the literature and stable at the pH of the present latexes, that is, from about 1.5 to about 7.0, and include the various alkyl sulfates, the various alkyl sulfosuccinates, the various alkyl aryl sulfonates, the various α-olefin sulfonates, the various quaternary ammonium salts, the various amine salts, nonyl or octyl phenol reaction products of ethylene oxide and the like. The alkyl portion of the various emulsifiers generally has from 8 to 18 carbon atoms. Examples of suitable surfactants which desirably are anionic include sodium lauryl sulfate, various sodium sulfosuccinates such as sodium dimethylamyl sulfosuccinate, e.g., Aerosol MA80, disodium dodecyl diphenyl oxide disulfonate (Dowfax 2A1), sodium dicyclohexyl sulfosuccinate, Aerosol A-196, and the like. Naturally, an amount of an emulsifier is utilized to obtain an aqueous emulsion of the various monomers. Such an amount is typically from about 0.5 to about 5 or 6 parts by weight for every 100 parts by weight of the monomers. Other surfactants can be utilized such as those set forth in Surface Active Agents, Schwartz and Perry, Vol. I, Interscience Publishers, Inc., New York, 1958; Surface Activity , Moilliet, Collie and Black, D. Van Nostrand Company, Inc., New York, 1961; Organic Chemistry, Fieser and Fieser, D.C. Heath and Company, Boston, 1944; and The Merck Index, Seventh Edition, Merck & Co., Inc., Rahway, NJ, 1960. Chelating agents can be utilized during polymerization to tie up various metal impurities as well as to achieve a uniform polymerization. The amounts of such chelating agents is generally small, such as from about 0.01 to about 0.25 parts by weight for every 100 parts by weight of the total weight of the monomers. Examples of suitable chelating agents include ethylene diamine tetraacetic acid, nitrilotriacetic acid, citric acid, and their ammonium, potassium, and sodium salts. Monomers capable of generating non-functional crosslinked structures during the polymerization of the various monomers to thereby contribute to the creation of a high gel fraction latex are optionally incorporated in amounts of from about 0.5 to about 5 parts by weight, desirably from about 0.1 to about 2 parts by weight and preferably from about 0.1 to about 1 part by weight per 100 parts by weight of the conjugated diene and vinyl substituted aromatic monomers. Examples of such compounds include divinyl benzene, ethylene glycol dimethacrylate, di(isopropenyl) benzene, and the like. An important aspect of the present proposals is the utilization of a ketoxime or amide blocked isopropenyl α,α-dimethyl benzylisocyanate (TMI) compound, having the formula or wherein R and R', independently, is an alkyl containing from 1 to 10 carbon atoms, more desirably from 1 to 4 carbon atoms, and more preferably 1 or 2 carbon atoms with the ketoxime blocking group, being e.g. acetone oxime, methyl ethyl ketoxime, methyl isobutyl ketoxime or methyl amyl ketoxime, with methyl ethyl ketoxime being preferred. Other suitable blocking agents include various primary or secondary amide compounds, wherein R 4 is hydrogen, or wherein R 3 and R 4 , independently, is an alkyl, an aryl, or combinations thereof, having from 1 to 10 carbon atoms with 2 to 5 being preferred and wherein R 3 can be connected to R 4 to form an internal, i.e. cyclic, amide. Examples of suitable amides include caprolactam, pyrrolidone, acetamide, butyramide, benzylamide, and the like. In either formulation, the isopropenyl group is in either the meta, ortho, or para position with the meta position being preferred. The amount of the ketoxime-blocked or amide-blocked TMI utilized in the composition is usually from 0.5 to 20 parts; desirably from 0.5 to 5.0 parts; and preferably from 0.5 to 2.5 parts by weight per 100 parts by weight of the conjugated diene and the vinyl-substituted aromatic monomers. The various latex-forming monomers can be polymerized by free radicals e.g. according to any conventional method including batch, incremental, or continuous, in the presence of an effective amount of water to enable the formation of an emulsion as well as proper mixing of the various additives, heat transfer, and the like. Polymerization is generally carried out at from 50°C to 90°C, and desirably from 65°C to 75°C. Polymerization is generally conducted in an acidic medium when acidic monomers are utilized and the pH of the latex binder is generally from about 1.0 to about 6.5, desirably from about 1.5 to about 4.0, and preferably from about 1.5 to about 3.0 being preferred. Such high polymerization temperatures result in high conversion levels of monomer to copolymer such as at least 90 percent, desirably at least 95 or 98 percent and preferably at least 99 percent. Such latex polymers also contain high gel fractions. That is, generally at least 70 percent by weight to about 95 or 97 percent by weight, desirably at least 80 percent by weight and preferably at least 90 percent by weight, that is of insoluble weight percent fraction in toluene at 20°C. The amount of solids, that is, the copolymer or binder, is generally from about 35 to about 60, and preferably from about 40 to about 50 percent by weight based upon the total weight of the binder and the remaining ingredients, for example, water. The average particle size of the binders after filtering is generally from about 100 to about 300 nm and desirably from about 120 to about 150 nm. An important advantage of the latex binder composition is that it, as well as the binder per se, can have very low amounts of aldehyde therein and generally can be aldehyde-free. That is, the amount of aldehyde, e.g., formaldehyde, is generally 10 parts or less, desirably 5 parts, 3 parts, or 2 parts or less, and preferably 1 part or 0.7 part or less per million parts by weight of the latex binder composition. Accordingly, the amount of aldehyde in the binder per se is the same as the ranges set forth above, e.g., 10 parts or less by weight based upon one million parts by weight of binder. We noted unexpected advantage in that the latex binders have good storage stability: the aldehyde content thereof essentially remained the same after one day, one week, two weeks, three weeks, and even four weeks. For example, after 28 days, the amount of aldehyde in the latex binder composition is still appreciably the same, i.e., within 5 or 7 percent of the original or initial aldehyde content. We have also noted good coagulation stability. Thus, very low levels of coagulant, especially fine-size coagulant such as that retained on 325 Tyler mesh, exist after filtering of the latex, that is, 0.1 percent or less, desirably 0.05 percent or less, more desirably 0.02 percent or less, and preferably 0.01 percent or less by weight based upon the total weight of the latex solids. Low levels of coagulant exist even after extended periods of time, for example, three months, six months, and even nine months. At six months, the amount of coagulant retained on 325 Tyler mesh, after filtering the latex, is generally 0.05 percent or less, desirably 0.02 percent or less, and preferably 0.01 or less by weight based upon the total weight of the latex solids. Such latex binder compositions have many applications and can be utilized on cellulosic nonwoven materials such as paper, e.g., offset printing paper, towels, various paper tapes, paper containers, and the like, and are particularly well suited for industrial wipes and toweling. When utilized as a paper coating, the binder generally comprises about 10 percent by weight of the paper coating formulation with a great majority of the same being comprised of clay, and the like, whereby the binder serves to bind the clay to the paper surface. The latex binder can also be applied to other non-woven substrates such as non-woven fibers, e.g., polyester, polypropylene, rayon, or nylon, or combinations of cellulosic and synthetic fibers, to non-woven textiles such as mats, to carpet backings, to various disposable products for use in the medical industry such as face masks, gowns, gloves, and the like. Although the high gel fraction binders are generally highly crosslinked, application of the same to a substrate, and the like, resulting in the formation of a laminate, etc., and the subsequent application of heat results in deblocking of the ketoxime- or amide-blocked TMI with further crosslinking. The same results in the improvement of various properties such as wet tear strength of the composite or laminate, improved bond strength between various fibers or laminates, and the like. The cure temperature with regard to the application of the binder to a non-woven, non-cellulosic substrate is generally from 100°C to 170°C whereas the cure temperature with respect to cellulose or paper substrates is generally from 70 to 100°C. During cure, the generated free isocyanate groups generally react with functional groups such as amide or hydroxyl located in other polymers thereby crosslinking the same, with hydroxyl groups as contained in the cellulose substrate, and thereby form chemical bonds yielding good adhesion, improved wet tensile strength, wet rub, and the like. One specific use of the latex binder is to bind a paper coating composition to a cellulose substrate as shown in Fig. 1 wherein the cellulose is generally indicated by the number 10. The paper coating composition 12 is known to the art and to the literature and generally includes various fillers such as high brightness clay pigments, calcium carbonate, titanium dioxide, small amounts of sodium hydroxide to control the pH, small amounts of calcium stearate to act as a lubricant, water, sodium polyacrylic acid to act as a dispersant for the clay, starch, for example, oxidized starch, protein binders such as soybean protein, polyvinyl alcohol binders, and the like. From about 4 to about 25 parts by weight and desirably from about 5 to about 20 parts by weight of the latex binder solids, i.e., dry binder, per 100 parts of filler (e.g., clay, calcium carbonate, titanium dioxide, etc.) is generally utilized and the same are mixed along with the above-noted other paper coating additives in any conventional mixer, e.g., a Cowles blade mixer or a ball mill. The paper-coating composition containing a small amount of the latex binder is then coated on a paper substrate as by using an air knife coater, a blade coater, or a roll coater. The substrate is then dried in a conventional hot-air oven and/or infrared drying oven. The paper is then generally super-calendered at elevated temperatures as from 70°C to 100°C, and at high pressure whereby cure of the binder 15 occurs binding the paper coating composition to the cellulose substrate. The coating or laminate thus produced has good wet tear strength. The high gel fraction latex binder 15 can be applied to non-woven fibers 20 such as polyester, cellulosic, or mixtures of cellulosic and synthetic fibers to bind the same together, see Fig. 2. The binder can be applied to the fibers in any conventional manner as by spraying an approximately 20 percent solid latex solution, and the like. Upon heating the high gel fraction binder to cure temperatures of 100 to 170°C, the TMI becomes unblocked and reacts in a manner as set forth above thereby binding the various fibers or strands together. Our proposals will be better understood by reference to the following examples. Apparatus A 4.55 ℓ (one-gallon) stainless steel pressure reactor equipped with monomer addition ports, stirrer, and temperature and pressure measurement devices was used. Cooling was provided by an external water bath. Example 1 A mixture of deionized water 1045g, Dowfax 2A1 (15 percent) 25g, itaconic acid 22g, Aerosol A196 (10 percent) 105g, EDTA solution (40 percent) 4g and styrene 112g were stirred and heated to 65°C (under nitrogen). A solution of sodium persulfate 7.5g in deionized water 142g was then added to the reactor. After 30 minutes the monomer and aqueous streams as set forth in Table I were added to the reactor at 60°C over a period of 6 hours. AQUEOUS STREAM MONOMER STREAM DI water 320g Styrene 576g Dowfax 2A1 (15%) 60g Butadiene 690g Acrylamide (50%) 60g Divinyl Benzene (55%) 6.25g Hydroxyethyl Acrylate 30g TMI/MEKO 30g Dodecyl mercaptan 3.75g After 6 hours the temperature was raised to 71°C and the reaction continued for 3 hours (total solids approximately 44 percent). The pH of the high gel fraction latex binder was 2.1 and the amount of gel at 20°C in toluene was 90 percent. The conversion of monomers to polymer was at least 99 percent. Post-Addition re Storage and Stability The following was added to the reactor and then the latex was steam-stripped and filtered in a conventional manner. Dowfax 2A1 (15 percent) 20g, D.I. water 85g, 28% ammonia 25g DREW L 198 antifoam 4g Proxel GXL (25%) biocide 8g, Bostex 490B (35%) antioxidant 20g. Properties Total solids content 44.2 percent pH 7.3 Surface tension 0.4 N/m (40 dynes/cm) Brookfield viscosity 50 mPa.s (50 cps) Particle size approx 145 nm (1450 Å) Coagulation collected on 325 Tyler mesh 3.0 grams The binder contained less than 0.7 part by weight of formaldehyde per million parts by weight of the latex binder. The amount of formaldehyde after 28 days of aging was also less than 0.7 parts per million. Example 2 A conventional latex binder composition control (Latex 1 of Table II) was prepared in a manner similar to Example I as were latexes A, B and C embodying our proposals. The amounts indicated are in weight units, i.e., control contained 46 parts by weight styrene, 50 parts by weight butadiene, 2 parts by weight acrylic acid, 1.5 parts by weight itaconic acid and 0.5 parts by weight divinyl benzene. Each of the above latexes were applied to Whatman® sheets and dried for 5 minutes at 315°F (158°C). The amount of latex applied in each case was 20 percent by weight (45 percent solids) of the total weight of the latex and paper. The dried sheets were then tested for yellowness, wet tensile strength (in water), and solvent tensile strength using a variety of different solvents such as toluene, heptane, mineral spirits. The solvent tensile test is an average tensile strength of paper soaked in toluene, heptane and mineral spirits for a period of 3 hours and tested immediately thereafter without drying. The results indicate that the novel latex compositions have a lower yellowness index and much better wet tear strength and average solvent tear strength than the first control. The second control shows that a conventional or typical styrene-butadiene polymer made utilizing N-methylol acrylamide and acrylamide while having good wet tensile strength and average solvent tensile properties having exceeding high amounts, that is 120 parts per million of formaldehyde. Example 3 Two latex binder compositions embodying our proposals were prepared in a manner as set forth in Example 1 and had the composition shown in Table III. The samples were then tested for mechanical stability by determining the amount of coagulum formed after 30 minutes of shearing in a high speed blender. The data shows that the inclusion of carboxylic acids results in dramatic improvements in coagulation stability. It was also observed that the inclusion of carboxylic acids in the latex composition provides for better processing in the reactor. LATEX COMPOSITION REACTOR "CLEANLINESS" MECHANICAL STABILITY STY/BD/IA/AA/TMI.MEKo 48.5/46/1.5/2/2 Good 16 PPM (0.0016 %) STY/BD/TMI.MEKo 52/46/2 Build up of Polymer on Walls of Reactor 178,071 PPM (17.81 %) NOTE: IA = Itaconic Acid AA = Acrylic Acid Example 4 COMPARATIVE EXAMPLE USING UNBLOCKED TMI MONOMER When a latex was prepared in a manner similar to Example 1 except that the TMI.MEKO and hydroxyethyacrylate were omitted and 30g of TMI monomer were substituted, the polymer emulsion was very unstable in a colloidal sense and the product flocculated in the reactor was approximately 60 percent of the reaction ingredients. The polymer emulsion changed to a solid thick mass which could not be further processed. Thus, physical test data could not be obtained.

Claims: A high gel fraction latex binder composition comprising an aqueous dispersion of a binder polymer which is the polymerisation reaction product of (a) 100 parts by weight of a primary comonomer combination consisting of from 10 to 90 wt% C 4-8 conjugated diene monomer and from 90 to 10 wt% C 8-12 vinyl-substituted aromatic monomer; (b) from 0.1 to 15 parts by weight of at least one functional-group-containing monomer; (c) from 0.5 to 20 parts by weight of ketoxime- or amide-blocked isopropenyl α,α-dimethyl benzyl isocyanate crosslinking agent of the formula in which R and R' independently are C 1-10 alkyl groups, or in which R 3 is C 1-10 alkyl, aryl or alkyl-aryl, and R 4 is H or C 1-10 alkyl, aryl or alkyl-aryl; R 3 and R 4 optionally being connected to form a cyclic amide; the binder being curable by heating to a crosslinking temperature at which thermal deblocking of the blocked isocyanate takes place to generate free isocyanate groups. A binder composition according to claim 1 in which the binder polymer also comprises residues of (d) from 0.1 to 35 parts by weight of vinyl chloride and/or vinylidene chloride monomer. A binder composition according to claim 1 or claim 2 in which the binder polymer also comprises residues of (e) from 0.1 to 10 parts by weight of C 1-10 alkyl (meth)acrylate monomer or hydroxy-derivative thereof. A binder composition according to any one of the preceding claims in which the binder polymer also comprises residues of (f) from 0.1 to 25 parts by weight of acrylonitrile monomer. A binder composition according to any one of the preceding claims in which the conjugated diene monomer constitutes from 15 to 60 wt% and the vinyl-substituted aromatic monomer constitutes from 40 to 85 wt% of the primary comonomer combination. A binder composition according to claim 5 in which the conjugated diene monomer constitutes from 25 to 55 wt% and the vinyl-substituted aromatic monomer constitutes from 45 to 75 wt% of the primary comonomer combination. A binder composition according to any one of the preceding claims in which the conjugated diene monomer is 1,3-butadiene. A binder composition according to any one of the preceding claims in which the vinyl-substituted aromatic monomer is styrene. A binder composition according to any one of the preceding claims in which the functional-group-containing monomer is present at from 0.5 to 10 parts by weight. A binder composition according to claim 9 in which the functional-group-containing monomer is present at from 1.0 to 5 parts by weight. A binder composition according to any one of the preceding claims in which the at least one functional-group-containing monomer is selected from C 3-12 unsaturated carboxylic acids and C 3-12 unsaturated amides and derivatives thereof. A binder composition according to claim 11 in which the at least one functional-group-containing monomer is selected from acrylic acid, itaconic acid and acrylamide. A binder composition according to any one of the preceding claims in which the blocked isocyanate is present at from 0.5 to 5.0 parts by weight. A binder composition according to any one of the preceding claims in which the blocked isocyanate comprises said ketoxime-blocked isocyanate in which both R and R' are selected from methyl and ethyl. A binder composition according to any one of the preceding claims in which the blocked isocyanate comprises said amide-blocked isocyanate in which R 3 and R 4 join together to form a caprolactam ring. A binder composition according to any one of the preceding claims in which in the blocked isocyanate the isopropenyl group is in the meta position. A binder composition according to any one of the preceding claims containing less than 5 parts per million of formaldehyde. A binder composition according to claim 17 containing less than 5 parts per million of aldehyde. A binder composition according to any one of the preceding claims in which the binder polymer contains from 70 to 97 wt% gel fraction insoluble in toluene at 20°C. A binder composition according to claim 19 in which said gel fraction is at least 80 wt%. A binder composition according to claim 20 in which said gel fraction is at least 90 wt%. A binder composition according to any one of the preceding claims, essentially free of crosslinking by functional groups other than unsaturated hydrocarbon. A process of making a binder composition according to any one of claims 1 to 22, comprising emulsion polymerising the monomers at a temperature in the range from 50 to 90°C. A process according to claim 23 in which the level of coagulant in the resulting composition is such that not more than 0.1 wt% of the latex solids is retained by a 325 Tyler mesh after filtering A process according to claim 23 in which the resulting composition has a coagulant stability such that after six months not more than 0.05 wt% of the latex solids is retained by a 325 Tyler mesh after filtering. An article comprising a cellulosic substrate and a paper coating composition bound to the substrate by a cured binder composition according to any one claims 1 to 22. A method of making an article as defined in claim 26 in which said primary comonomer combination contains from 15 to 50 wt% of the non-conjugated diene and from 50 to 85 wt% of the vinyl-substituted aromatic, and the binder composition is cured at a cure temperature in the range from 70 to 100°C. An article comprising non-woven, non-cellulosic fibres bound together by a cured binder composition according to any one of claims 1 to 22. A method of making an article as defined in claim 28 in which said primary comonomer combination contains from 25 to 55 wt% of the non-conjugated diene and from 45 to 75% wt% of the vinyl-substituted aromatic, and the binder composition is cured at a cure temperature in the range from 100 to 170°C.

Inventors: HAYES PETER C, HAYES, PETER C.
Applicants: GENCORP INC, GENCORP INC.
Application year: 1994
Main classification: D21H17
IPC codes: C08F236, C08L25, C08L9, D06M15, D04H1, D21H19, C08F212, C09J125, C08L21, C09D125