AN ASYMMETRICAL POROUS PTFE FORM AND METHOD OF MAKING

Abstract: An asymmetrical form of porous PTFE having substantially different dimensions at different points along the length of the form. If the form is, for example, a tubular form, the different dimensions may be thickness or diameter or both. The form is preferably a tubular form which is preferably tapered having opposing ends with large and small inside diameters respectively wherein the wall thickness of the large diameter end is greater than or equal to the wall thickness of the small diameter end. Tapered PTFE tubes of this type are particularly useful as implantable vascular grafts. A method of producing these asymmetrical porous PTFE forms is also described.

Description: TITLE OF THE INVENTION AN ASYMMETRICAL POROUS PTFE FORM AND METHOD OF MAKING FIELD OF INVENTION This invention relates to asymmetrical porous PTFE forms and particularly to tapered, porous PTFE tubes useful as vascular grafts, and to a method of making such forms. BACKGROUND OF THE INVENTION Porous polytetrafluoroethylene (hereinafter PTFE) forms have been known and used for some time. U.S. Patents 3,953,566 and 4,187,390 describe the manufacture of porous expanded PTFE forms such as tubes of substantially constant diameter wherein the porous expanded PTFE has a microstructure of nodes interconnected by fibrils. Tubes of this type subsequently found wide application, particularly as implantable vascular grafts. For some vascular graft applications, it was found desirable for the graft to be tapered between the opposing ends. Tapered porous PTFE tubes for use as vascular grafts (such as GORE-TEX* Vascular Grafts, Part Numbers V47020L and VT68110L, W. L. Gore & Associates, Inc., Flagstaff AZ) became available commercially. These tapered porous PTFE vascular grafts were made by methods that resulted in tubes having a wall thickness at the smaller diameter end of the tube that was greater than the wall thickness at the larger end of the tube. One such method is described by U.S. Patent 4,957,669 to Prim wherein a porous PTFE tube of substantially constant diameter 1s fitted over a tapered steel mandrel of round cross section to which ultrasonic energy is applied. The inside diameter of one end of the tube is increased with respect to the diameter of the opposite end by stretching the material of one end of the porous PTFE tube over the larger end of the mandrel. The result of such a stretching procedure is that the wall thickness of the larger diameter end of the tube is reduced, thereby becoming less than the wall thickness of the smaller diameter end of the tube. Because the larger diameter end of the tapered porous PTFE tube is made by stretching the smaller, original diameter thereby resulting in thinning of the wall thickness at the larger diameter end, it is seen that the original mass of the beginning smaller diameter end is maintained at the new, enlarged large diameter end. This can be confirmed by, for example, cutting ring-shaped samples of constant and equal width from each end of the tube with the samples cut perpendicular to the longitudinal axis of the tube. The large and small diameter, equal width samples can be expected to have substantially equal weights. To have a thinner wall thickness at the larger diameter end of a tapered tube containing liquid under pressure is clearly undesirable from a mechanical standpoint in view of the greater hoop stress on the larger end of the tube. A tapered porous PTFE tube having at least equal wall thicknesses at the opposing ends would be mechanically preferable to the presently available tubes, and such a tapered tube having a greater wall thickness at the larger diameter end would be even more preferred. This would be particularly true for larger diameter vascular grafts such as about 12 mm diameter and larger intended for aortic repair. SUMMARY QF THE INVENTION The present invention relates to asymmetrical porous PTFE forms wherein the porous PTFE form has at one end at least one dimension that is substantially different from the equivalent dimension of the opposite end. The present invention also relates to a method of making such a form. According to the method of the present invention, an extrudate is created from a mixture of PTFE fine powder and liquid lubricant using a ram extruder, all in conventional manner. The symmetrical form of the extrudate thus created is then modified into an asymmetrical form by compression between two dies of the desired shape. Again according to convention, the liquid is removed from the asymmetrical extrudate which is then expanded by stretching at a temperature less than the crystalline melt temperature of PTFE, and finally and optionally, heat treated at a temperature greater than the crystalline melt temperature while being restrained to prevent shrinkage. The invention thus involves the additional step of modifying the extrudate to an asymmetrical form prior to removal of the liquid from the extrudate. By asymmetrical is meant that one end of the form has at least one dimension that is substantially different from the equivalent dimension of the opposite end. These dimensions may relate to, for example, diameters or wall thicknesses of a tubular porous PTFE form. The form is not limited to that of a tube. A sheet extrudate may be modified with dies, dried and expanded by stretching to create a porous PTFE sheet having different thicknesses at opposing ends. Alternatively, a tapered porous PTFE tube of the present invention may be slit longitudinally to form a sheet having different thicknesses at opposing ends. In still another embodiment, a tapered cylindrical form may be created having entirely different diameters at the opposing ends of the cylinder. In a preferred embodiment the present invention relates to a tapered porous PTFE tube having a wall thickness at the larger diameter end of the tube that is greater than or equal to the wall thickness at the smaller diameter end of the tube. Tubes made according to the present invention are anticipated to be particularly useful as vascular grafts. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 describes a cross sectional view of a tapered porous PTFE tube of the prior art wherein the wall thickness of the large diameter end of the tube is less than the wall thickness of the small diameter end of the tube. Figure 2 describes a cross sectional view of a tapered tube of the present invention wherein the wall thickness of the large diameter end of the tube is substantially equal to the wall thickness of the small diameter end of the tube. Figure 3 describes a cross sectional view of a tapered tube of the present invention wherein the wall thickness of the large diameter end of the tube is substantially greater than the wall thickness of the small diameter end of the tube. Figures 4A, 4B and 4C describe cross sectional views of the male and female dies used to modify constant diameter PTFE tubular wet extrudate to create the tapered porous PTFE tube of the present invention. Figure 5 describes a cross sectional view of a porous PTFE tube having a constant inside diameter and a greater wall thickness at one end of the tube than at the opposite end. Figure 6 shows a tapered porous PTFE tube having a helical wrapping of porous PTFE film. Figure 7 describes a cross sectional view of a porous PTFE tube having substantially different wall thicknesses at different locations along the length of the tube. DETAILED DESCRIPTION OF THE INVENTION Conventional porous PTFE tubes of substantially constant diameter and wall thickness are made by a process described by U.S. Patents 3,953,566 and 4,187,390, herein incorporated by reference. Briefly, this process involves blending fine powder PTFE resin with a lubricant, compressing the resulting mixture into a cylindrical pellet, extruding a tubu ar form from this pellet using a ram extruder, removing the lubricant from the tubular form, and then expanding the tube by stretching it parallel to its longitudinal axis after heating the tube to a temperature less than the crystalline melt point of PTFE. The resulting porous PTFE tube is then preferably heat-treated at a temperature above the crystalline melt point of PTFE while being restrained to prevent shrinkage. Porous PTFE tubing made by this process is of substantially constant diameter and wall thickness. Prior art, tapered tubes were made by, for example, increasing the diameter of one end of these constant diameter tubes by radial stretching, prior to the final step of heat-treating. The tapered porous PTFE tube of the present invention is made by using the above process through the step of extruding a tubular form. A step is then added to this process which requires taking the tubular extrudate which still contains the liquid lubricant and placing it between tapered male and female dies. The dies are preferably heated to a temperature such as about 60 * C. The diametrical relationship between the male and female dies can be such that when fitted concentrically together, the space between the dies at the opposing larger and smaller diameter ends is equal, or alternatively the space at the larger diameter end is greater than the space at the smaller diameter end. Preferably the diameter of the extrudate should approximately equal the mean of the large and small diameters of the dies. Axial compression is applied to the two dies with the tubular extrudate between them. After releasing the compression, the tubular extrudate is removed from between the male and female dies. The removed tubular extrudate is tapered with wall thickness corresponding to the space between the dies. The liquid lubricant is then removed from the tapered tubular extrudate, which is subsequently expanded by stretching in a direction parallel to the longitudinal axis and preferably heat-treated after stretching as described previously. As opposed to tapered porous PTFE tubes of the prior art, tubes of the present Invention have different masses at the opposite tube ends. Again, this can be confirmed by cutting equal width samples from each end of the tapered tube perpendicular to the longitudinal axis of the tube whereby each sample takes the form of a constant width ring with both samples being of equal width. The large diameter sample can be expected to have a weight at least ten percent greater than that of the smaller diameter sample. In order to be considered as a tapered tube, the diameter of the small end of the tube 1s expected to be equal to no more than ninety percent of the diameter of the large end of the tube. In an alternative embodiment, the tapered porous PTFE tube of the present invention may be mechanically reinforced by providing the tube with a helically-wrapped reinforcement of, for example, porous PTFE film, thereby increasing the hoop strength of the tube. Porous PTFE tubes having this type of reinforcement are presently available as GORE-TEX Vascular Grafts in the form of both straight, constant diameter tubes and tapered tubes. Porous PTFE films suitable for this reinforcement are made as taught by U.S. Patents 3,953,566 and 4,187,390. Briefly, the preferred films for this application are porous PTFE films having a microstructure containing fibrils oriented substantially parallel to each other, that is oriented substantially in one direction. These films are then slit Into long narrow tapes of, for example, 1.5 cm width with the orientation of the fibrils parallel to the length of the tape so that the greatest strength of the tape is along its length. This tape may then be helically wrapped about the outer surface of the tapered tube following the step of expanding the tube lengthwise by stretching and the additional step of fitting the tube over a tapered steel mandrel. Preferably, the edges of the tape should overlap during wrapping; the amount of overlap used will affect the thickness of the tape application and consequently the hoop strength of the finished tube. If desired, an Increased amount of overlap may be used on the large diameter end of a tapered tube in order to better accommodate the greater hoop stress at that end of the tube. The step of heat-treating at a temperature above the crystalline melt point of the PTFE is performed after the film application while the tube is still on the steel mandrel. By heating the film above the crystalline melt temperature of PTFE it 1s caused to adhere to the underlying tapered porous PTFE tube. The porous PTFE tube may also be provided with exterior reinforcement in the form of rings or spirals of a non-porous material such as fluorinated ethylene propylene applied to the exterior of the tube in the fashion of, for example, a Ringed GORE-TEX Vascular Graft (Part No. R05020100L). In still another alternative embodiment, the porous PTFE may be provided with rapid recovery properties as taught by U.S. Patent 4,877,661, also herein incorporated by reference. For tapered tubes of porous PTFE, the compression step of the rapid recovery process should be performed on a tapered steel mandrel such that the amount of mandrel taper corresponds with the degree of taper of the porous PTFE tube while longitudinally compressed in the desired amount. While the tapered porous PTFE tube of the present invention is primarily useful for implantable vascular graft applications, it is anticipated to have other uses as well, including non-medical applications as well as other medical applications. It is believed that the tubing may be useful for, for example, preventing adhesions around intramammary coronary grafts if the tubing has a small fibril length such as about five microns. If provided with a relatively thin wall such as less than about 0.25 mm, the tapered tube may be useful as an intraluminal vascular graft for aneurismal repair. Such a graft may be secured in place by the use of, for example, expandable stents. A tapered porous PTFE tube may also be useful in industrial applications as a filter or component in a filter system where the chemically inert character of the PTFE is of advantage. For purposes of describing tapered tubes, diameter refers to the inside diameter of the tube. Tube diameter is best determined by gently but snugly fitting the tube over a gradually tapered steel mandrel of circular cross section having indicated diameter graduations at appropriate Intervals. Wall thickness is determined by measuring thickness at three equally spaced points around the circumference of the exposed tube end using calipers with flat surface jaws of at least 3 mm width to avoid crushing the porous PTFE. The wall thickness is the mean of the three measurements. Figure 1 describes a cross sectional view of a tapered porous PTFE tube Ifi of the prior art having a wall thickness t L at the large diameter end 14 of the tube 1£ that 1s less than the wall thickness t s of the small diameter end 12. These are typically the result of modifying the diameter of one end of porous PTFE tubes of constant diameter that have been made by extruding a mixture of PTFE fine powder and a lubricant into a tubular form, removing the lubricant and expanding the tubular form by longitudinally stretching at a temperature less than the crystalline melt temperature of PTFE. Figures 2 and 3 describe cross sectional views of porous PTFE tubes of the present invention wherein the wall thickness t L of the larger end 14 of the tube £ 1s substantially equal to or greater than the wall thickness t s of the smaller end 12 of the tube. The inventive tube is made by extruding a tubular extrudate comprising a mixture of PTFE fine powder and lubricant, the extrudate having a substantially constant inside diameter and wall thickness. As shown by the cross sections of Figures 4A, 4B and 4C, the tubular extrudate 45, still containing liquid lubricant, is placed between tapered male die 46 and a tapered female die 4J., with axial compression C applied to the resulting assembly. It is preferred that the dies be heated such as to about 60"C in order to aid in conforming the tubular extrudate to the shape of the dies. Space t L at the large end 44 of dies 5 and 4£ and space t s at the small end 42 are proportioned according to the desired wall thicknesses of the respective large and small ends of the finished porous PTFE tube. For a porous PTFE tube having large and small ends of equal wall thickness, the spaces t L and t s should be equal which requires that male die 4£ and female die 4fi have tapers of the same angles. If a porous PTFE tube is desired having a greater wall thickness at the larger end than at the smaller end, then space t L at the large diameter end 44 of the dies 4£ and 4S should be greater than space t s at the smaller end 42 of dies 46 and 4fi. This necessitates that female die 4S should have a greater taper angle than male die 4£. After fitting the tubular extrudate containing liquid lubricant between male die 46 and female die 4S, a compressive force represented by arrows C is applied to the assembly until spaces t s and t L are equal to the desired wall thicknesses of the finished porous PTFE tube. Finally, the compressive force is removed, the resulting tapered tubular form is removed from the dies and expanded by longitudinally stretching as taught by U.S. Patents 3,953,566 and 4,187,390. The resulting tapered porous PTFE tube may then be heat treated if desired. While the transverse cross sections of Figures 4B and 4C indicate that the inventive form is transversely symmetrical, it is anticipated that the same method of modification of the shape of PTFE extrudate containing a liquid lubricant by the use of compressive dies to create a longitudinally asymmetrical shape may also be used to create a transversely asymmetrical shape if suitable dies are used. Tapered porous PTFE tubes may be made by the method of the present invention with tapers ranging from very gradual to relatively severe. For example, a tapered tube useful as a vascular graft may have opposing ends with respective diameters of 6 mm and 8 mm, tapering gradually over a length of 100 cm. Alternatively, a tube of length as short as 10 cm may be made having a severe taper with opposing ends of, for example, 2 mm and 100 mm diameters. In still other embodiments, the tube may be provided with a non-linear, stepped taper by using dies having matched, but non-straight sided tapers. Additionally, the tube may be made with straight, constant diameter portions of both large and small diameters separated by a tapered section. Figure 5 describes a cross sectional view of an asymmetrical porous PTFE tube Q having a constant inside diameter and a greater wall thickness t L at tube end 2 than the wall thickness t s at tube end 51. Figure 6 shows a tapered porous PTFE tube fi having a helical wrapping 6. of a tape of porous PTFE film. As shown by the cross section of Figure 7, it is also anticipated that a tube 7J) may be made having a different wall thickness along the middle portion 21 of its length than at the ends 22• For example, a tubular vascular graft intended for arterlovenous access requiring frequent cannulation by dialysis needles can be expected to bleed less at the cannulation sites if the wall thickness of that middle portion of the length of the graft 1s of Increased thickness. To make such a graft by the method of the present invention would require that the female die be split longitudinally to allow for its removal from the extrudate. The precursor extrudate should have a wall thickness equal to or slightly greater than the desired wall thickness of the thickest part of the tube. The outside diameter of the precursor extrudate should be equal to or very slightly greater than the outside diameter of the smallest outside diameter portion of the desired tube. The male die should be of the same outside diameter as the desired inside diameter of the finished tube, and should have a gradual taper at the first end to be Inserted into the assembled split female die containing the precursor extrudate. The different wall thicknesses created by this method are continuous thicknesses, that is, are not the result of adding to the thickness by adding one or more layers of additional material to create extra thickness. It is apparent that these continuous, different wall thicknesses may have extra layers added such as reinforcing film which would not be included in determining thickness of the continuous, different wall thicknesses resulting from the method of the present invention. EXAMPLE 1 FFiinnee powder PTFE resin was blended with 340 cm 3 ISOPAR M, an odorless solvent (obtained from Exxon Corp., Ft. Allen, LA) per kg of the PTFE resin. The mixture was compressed into a tubular billet of 15.9 cm outside diameter, 3.8 cm inside diameter and 45.7 cm length, heated to about 40°C and extruded into tubes using a ram extruder having a reduction ratio of about 76:1. A 37 cm length of the resulting tubular extrudate, which had a wall thickness of 2.7 mm and inside diameter of 24 mm, was then placed between tapered male and female dies of circular cross section which had been heated to 60 * C. The female die was of 36.8 cm length, with a bore of 56.92 mm at the large diameter end and a 17.32 mm bore at the small diameter end. The male die was of 42.65 cm length, with a large end diameter of 54.89 mm and a small end diameter of 14.27 mm. Both dies therefore incorporated a 3.06 * taper measured from the longitudinal axis. Using a mechanical press, an axial compressive force of about 2500 kg was then applied to the assembly as shown by Figure 4A thus producing a tapered PTFE tube still containing the liquid lubricant. The lubricant was removed from the tapered PTFE tube by drying in forced convection air oven at 250 β C for thirty minutes. The tube was then expanded by stretching longitudinally 6:1, at a rate of 55% per second in a forced convection air oven set at a temperature of about 310 * C. The resulting tapered porous PTFE tube was subsequently heat treated in a gravity convection air oven set at about 393 * C for 90 seconds. EXAMPLE 2 Another porous PTFE tube was created using the same method, materials and equipment of Example 1, except that the tapered male die was replaced by another male die having the same length but having a large end diameter of 55.83 mm and a small end diameter of 13.41 mm. The male die thus had a taper of 2.85 * . The porous PTFE tubes of Examples 1 and 2 were approximately 130 cm in length. The ends were cut off transversely from each of these tubes to create a tapered tube of 90 cm length. These tubes were then cut transversely into 30 cm lengths with the ends labeled 0 cm, 30 cm, 60 cm and 90 cm respectively beginning from the small diameter end. Inside diameter and wall thickness were measured at each tube end. A 1 cm wide ring-shaped sample was cut from an end adjacent to each labeled 30 cm interval and weighed. These data are shown in Table 1. For comparison, the same measurements were made with a 4-7 mm tapered GORE-TEX Vascular Graft (Part No. V47050L) made by prior art methods. The 4 mm and 7 mm diameters of this graft are separated by a 5 cm long tapered section; measurements were made on constant diameter portions of the graft adjacent to the tapered section. At the 4 mm diameter end, the tube had an inside diameter of 3.8 mm, a wall thickness of 0.65 mm and the 1 cm wide ring-shaped sample weighed 0.064 g. At the 7 mm diameter end, the tube had an inside diameter of 6.8 mm, a wall thickness of 0.58 mm and the 1 cm wide ring-shaped sample weighed 0.061 g. TABU 1 EXAMPLE 1 EXAMPLE 2 Position ID MALI. MASS ID WAU. MASS (mm) <mn) ( S ) (mm) ( ■ ) 0 en 19.SO 1.19 0.S2 1*.57 0.11 0.02 30 cm 26.10 1.21 0.61 16.37 0.20 0.02 60 em 32.60 1.19 0.77 19.36 0.S9 0.11 | 90 em 38.35 1.13 1.06 26.97 0.79 0.69

Claims: We Claim: 1. A tapered porous polytetrafluoroethylene tube comprising a tube of porous polytetrafluoroethylene having a microstructure of nodes Interconnected by fibrils and having opposing first and second ends wherein said first end has an inside diameter and a wall thickness and said second end has an inside diameter and a wall thickness, and wherein the inside diameter of said first end is less than or equal to ninety percent of the inside diameter of said second end and the wall thickness of said second end is greater than or equal to the wall thickness of said first end. 2. A tapered porous polytetrafluoroethylene tube according to claim 1 comprising a vascular graft. 3. A vascular graft according to claim 2 having an exterior helical wrapping of porous polytetrafluoroethylene film. 4. A vascular graft according to claim 3 wherein the Inside diameter of the first end is at least 12 mm. 5. A vascular graft according to claim 3 wherein the inside diameter of the first end is at least 16 mm. 6. A vascular graft according to claim 2 wherein the inside diameter of the first end is at least 12 mm. 7. A vascular graft according to claim 2 wherein the inside diameter of the first end 1s at least 16 mm. 8. A vascular graft according to claim 2 wherein said tube at ambient temperature is capable of being stretched and then rapidly recovering more than about 6 percent of its stretched length. 9. A vascular graft according to claim 8 wherein said tube at ambient temperature is capable of being stretched and then rapidly recovering more than about 10 percent of its stretched length. 10. A vascular graft according to claim 8 wherein the inside diameter of the first end is at least 12 mm. 11. A vascular graft according to claim 8 wherein the inside diameter of the first end is at least 16 mm. 12. A vascular graft according to claim 8 having an exterior helical wrapping of porous polytetrafluoroethylene film. 13. A tapered porous polytetrafluoroethylene tube according to claim 1 wherein the wall thickess of said second end is at least 20 percent greater than the wall thickness of said first end. 14. A tapered porous polytetrafluoroethylene tube comprising a tube of porous polytetrafluoroethylene having a lcrostructure of nodes interconnected by fibrils and having opposing first and second ends wherein said first end has an inside diameter and a wall thickness and said second end has an inside diameter and a wall thickness, wherein the inside diameter of said first end 1s less than 90 percent of the inside diameter of said second end and wherein a first ring-shaped sample having a fixed width cut perpendicular to the longitudinal axis of the tube from the first end of the tube has a weight at least ten percent less than the weight of a second ring-shaped sample having the fixed width cut perpendicular to the longitudinal axis of the tube from the second end of the tube. 15. A tapered porous polytetrafluoroethylene tube according to claim 14 comprising a vascular graft. 16. A vascular graft according to claim 15 having an exterior helical wrapping of porous polytetrafluoroethylene film. 17. A vascular graft according to claim 16 wherein the inside diameter of the first end is at least 12 mm. 18. A vascular graft according to claim 16 wherein the Inside diameter of the first end is at least 16 mm. 19. A vascular graft according to claim 16 wherein the inside diameter of the first end is at least 12 mm. 20. A vascular graft according to claim 15 wherein the inside diameter of the first end is at least 16 mm. 21. A vascular graft according to claim 15 wherein said tube at ambient temperature is capable of being stretched and then rapidly recovering more than about 6 percent of its stretched length. 22. A vascular graft according to claim 15 wherein said tube at ambient temperature is capable of being stretched and then rapidly recovering more than about 10 percent of its stretched length. 23. A vascular graft according to claim 22 wherein the inside diameter of the first end is at least 12 mm. 24. A vascular graft according to claim 22 wherein the inside diameter of the first end is at least 16 mm. 25. A vascular graft according to claim 22 having an exterior helical wrapping of porous polytetrafluoroethylene film. 26. A tapered porous polytetrafluoroethylene tube according to claim 14 wherein the weight of the first ring-shaped sample 1s at least 20 percent less than the weight of the second ring-shaped sample. 27. A porous polytetrafluoroethylene tube comprising a tube of porous polytetrafluoroethylene having a microstructure of nodes interconnected by fibrils, said tube having a substantially constant Inside diameter and having opposing first and second ends wherein said first end has a wall thickness and said second end has a wall thickness, and wherein the wall thickness of said first end is less than or equal to ninety percent of the wall thickness of said second end. 28. A porous polytetrafluoroethylene tube comprising a tube of porous polytetrafluoroethylene having a microstructure of nodes interconnected by fibrils and having a length, and further having a first wall thickness at a first point along said length that is at least 20 percent greater than a second wall thickness at a second point along said length, wherein the first wall and second wall thicknesses comprise a continuous thickness without layers connected by seams. 29. A tube according to claim 28 wherein said first wall thickness is at least 50 percent greater than said second wall thickness. 30. A tube according to claim 28 wherein said first wall thickness is at least 100 percent greater than said second wall thickness. 31. A method of making a tapered porous polytetrafluoroethylene tube having a microstructure of nodes interconnected by fibrils and having first and second opposing ends wherein said first end has an Inside diameter and a wall thickness and said second end has an inside diameter and a wall thickness, and wherein the inside diameter of said first end is less than ninety percent of the inside diameter of said second end and the wall thickness of said second end is greater than or equal to the wall thickness of said first end, said method comprising: a) blending fine powder polytetrafluoroethylene resin with a lubricant to create a mixture; b) compressing the mixture into a pellet; c) extruding a tubular form from the pellet; d) axially compressing the tubular form between tapered male and female dies to create a tapered tubular form; e) removing the tapered tubular form from between the tapered male and female dies; f) removing the lubricant from the tapered tubular form; and g) heating the tapered tubular form to a temperature less than the crystalline melt temperature of polytetrafluoroethylene and expanding the tapered tubular form by stretching longitudinally, thereby creating the tapered porous polytetrafluoroethylene tube. 32. A method according to claim 31 wherein the tapered porous polytetrafluoroethylene tube is heated to a temperature greater than the crystalline melt temperature of porous polytetrafluoroethylene while being restrained to prevent shrinkage. 33. A method according to claim 32 wherein the tapered porous PTFE tube 1s a vascular graft. 34. A method according to claim 31 wherein the tapered porous PTFE tube is a vascular graft. 35. A method of making an asymmetrical porous polytetrafluoroethylene form having a microstructure of nodes interconnected by fibrils, said method comprising: a) blending fine powder polytetrafluoroethylene resin with a lubricant to create a mixture; b) compressing the mixture into a pellet; c) extruding extrudate from the pellet; d) compressing the extrudate between two dies to create an asymmetrical extrudate; e) removing the asymmetrical extrudate from between the two dies; f) removing the lubricant from the asymmetrical extrudate; and g) heating the asymmetrical extrudate to a temperature less than the crystalline melt temperature of polytetrafluoro¬ ethylene and expanding the asymmetrical extrudate by stretching, thereby creating the asymmetrical porous polytetrafluoroethylene form. 36. A method according to claim 35 wherein the asymmetrical porous polytetrafluoroethylene form is heated to a temperature greater than the crystalline melt temperature of porous polytetrafluoroethylene while being restrained to prevent shrinkage. 37. A method according to claim 35 wherein the form is selected from the group of shapes consisting of tapered tubes, tubes of different wall thicknesses at opposing ends, sheets of different thickness at opposing ends and tapered cylinders. 38. A method according to claim 36 wherein the form is selected from the group of shapes consisting of tapered tubes, tubes of different wall thicknesses at opposing ends, sheets of different thickness at opposing ends and tapered cylinders.

Inventors: KASIC JAMES F, SIMMS WILLIAM J, KASIC, JAMES, F., SIMMS, WILLIAM, J.
Applicants: GORE & ASS, W.L. GORE & ASSOCIATES, INC.
Application year: 1994
Main classification: A61F2
IPC codes: A61F2, A61L27, B29C33, B29C53, B29C55, B29C67