Rubber composition

Abstract: A rubber composition including 100 parts by weight of natural rubber and/or diene synthetic rubber and 30 - 100 parts by weight of carbon black having the following characteristics: (1) 24M4DBP of 0.95 - 1.30 ml/g; (2) D st of 50 - 80 nm; (3) ΔD₅₀/D st of 0.55 - 0.75; (4) ΔD₁₀/D st of 1.0 - 1.5; (5) a component ratio of 20% or less; and (6) CTAB of 120 - 180 m²/g. The rubber composition is excellent in abrasion resistance without impairing the low heat generation property and the processability thereof.

Description: The present invention relates to a rubber composition suitable for use as a tire and, more particularly, to a rubber tire composition having improved abrasion resistance, and being especially suitable for use as a truck tire or a bus tire. Heretofore, the use of ISAF-grade carbon black as a highly reinforcing packing for rubber has been well known. Recently, however, there has been a great demand for carbon black which is capable of improving abrasion resistance of a tire, especially a pneumatic tire which experiences heavy loading, in the light of improved durability of a tire carcass and the desire to conserve natural resources. The grade of carbon black which is used as a reinforcing agent of a rubber composition for a tire tread used for heavy loading has been changed from ISAF-grade to SAF-grade. This is because SAF-grade carbon black particles are finer than those of ISAF-grade. In general, when carbon black is compounded into rubber to improve abrasion resistance, it is desirable to use a finely divided carbon black. However, even if the carbon black particles used are finer in comparison to SAF-grade particles, abrasion resistance is not necessarily improved since the dispersibility of the carbon black in the compounded rubber is remarkably lowered. In order to improve abrasion resistance, various investigations have been conducted focusing on the colloidal characteristics of carbon black. FR 2 635 108 provides rubber compositions which are suitable for manufacturing truck or bus tires comprising a carbon black having a 24M4DBP value of 95 to 135 ml/100g, a specific surface area (CTAB)of 120 to 160 m 2 /g, a D st value of 65 to 82 nm and a ΔD 50 /D st ratio of 0.64 to 0.81. Japanese Patent Application Laid-Open No. Sho 62-290738, for example, discloses a method for improving abrasion resistance by controlling, i.e., narrowing the aggregate distribution of carbon black. However, even these methods do not achieve satisfactory abrasion resistance to a level demanded at the present time. In addition, by narrowing the aggregate distribution, abrasion resistance is not remarkably improved and reaches a limit. An object of the present invention is to provide a rubber composition suitable for use as a tread, the rubber composition having improved abrasion resistance and being suitable for use as a tire, especially a truck tire or a bus tire without impairing the low heat generation property of the tire and the processability of the rubber composition. The present inventors have studied the relationship between the characteristics of carbon black and tire performance to solve the above-mentioned problems and found that abrasion resistance of a rubber composition can be improved to a great extent by compounding therewith carbon black having certain characteristics. Thus, the present invention provides a rubber composition including 100 parts by weight of one or more rubber components, the rubber components being natural rubber and/or diene-type synthetic rubber, and 30 - 100 parts by weight, more preferably 40 - 80 parts by weight of carbon black having the following characteristics: (i) 24M4DBP of 0.95 - 1.30 ml/g; (ii) D st of 50 - 80 nm; (iii) ΔD 50 /D st of 0.55 - 0.75; (iv) ΔD 10 /D st of 1.0 - 1.5; (v) component ratio of 20% or less; and (vi) CTAB of 120 - 180 m 2 /g wherein 24M4DBP, D st , ΔD 50 , ΔD 10 , the component ratio and CTAB are as defined below in connection with Fig. 1. In a specific embodiment of the invention, where the natural rubber and the diene-type synthetic rubber are both present as rubber components, the diene synthetic rubber is present in an amount of 10 - 80 parts by weight, more preferably 10 - 60 parts by weight, based upon 100 parts by weight of natural rubber. Fig. 1 is a graph of the aggregate distribution of carbon black particles in accordance with the present invention in which the Stokes corresponding diameter of carbon black aggregates is plotted on the abscissa of the graph and the frequency of the presence of the carbon black aggregates, i.e., the amount of carbon black aggregates having a certain Stokes corresponding diameter, in terms of weight percent, is plotted on the ordinate of the graph. This graph shows the most frequent value D st of the Stokes corresponding diameter, the half-width ΔD 50 , the 10% width ΔD 10 , and the component ratio (as a hatched area), for the carbon black used in the present invention, as will be discussed below. Fig. 2 is a schematic, longitudinal, cross-sectional view of an apparatus which may be employed to produce carbon black suitable for use in the present invention. Carbon black for comparative purposes was also prepared in the apparatus shown in Fig. 2, as will be discussed below. Fig. 3 is a schematic, cross-sectional view of the apparatus along line A-A in Fig. 2. Fig. 4 is a schematic, cross-sectional view of the apparatus along line B-B in Fig. 2. The present invention is explained in greater detail hereafter. The term "24M4DBP" as used in the present invention means the amount of dibutylphthalate(DBP) oil absorbed by the carbon black which has been crushed four times at a pressure of 24,000 psi. In other words, 24M4DBP is an indication of the DBP oil absorption based on the structural form of a real, non-destructive structure (a primary structure) excluding the DBP oil absorption due to a deformed and destructive structure (a secondary structure) caused by so-called van der Waals force, and it is also an indication evaluating the skeleton structure characteristics of carbon black having mainly a primary structure. 24M4DBP may be measured pursuant to ASTMD3493, the disclosure of which is herein incorporated by reference. The term "D st " (nm), as used in the present invention, means (with reference to Fig. 1) a value representing the most frequent value, that is, the most frequent aggregate diameter, in terms of Stokes corresponding diameter for an aggregate distribution of carbon black in accordance with the present invention. D st may be measured by a centrifugal sedimentation method using a disk centrifuge apparatus manufactured by the Joyce Leble company. In such a method, dried carbon black is first weighed precisely and is mixed with a 20% aqueous ethanol solution containing a small amount of surface-active agents in order to prepare a dispersed system having a 50 mg/l carbon black concentration. The system is sufficiently dispersed by supersonic waves and then used as a sample solution. The revolution of the disk centrifuge may be set at 6000 rpm and after adding 10 ml of a spin liquid (2% aqueous glycerin solution) to the sample solution, 1 ml of a buffer solution (an aqueous ethanol solution) is poured therein. Subsequently, after having injected 0.5 ml of the sample with a syringe, the centrifugal sedimentation is immediately started. By the use of a photoelectric sedimentation method, a formed aggregate distribution curve may be drawn as shown in Fig. 1 and a Stokes corresponding diameter corresponding to a peak of the curve is defined as D st (nm) The term "ΔD 50 ", as used in the present invention, means (with reference to Fig. 1) the width in Stokes corresponding diameter (nm) of the distribution curve at a 50% frequency position, and the term "ΔD 10 ", as used in the present invention, means the width of the distribution curve in Stokes corresponding diameter (nm) at the 10% frequency position (see Fig. 1). In other words, ΔD 50 represents the difference in Stokes corresponding diameter between the two points on the distribution curve corresponding to a 50% frequency, and ΔD 10 similarly represents the difference in Stokes corresponding diameter between the two points on the distribution curve corresponding to a 10% frequency. The term "component ratio," in accordance with the present invention, means (with reference to Fig. 1) the ratio of the hatched area under the distribution curve to the whole area under the distribution curve, the hatched area representing carbon black aggregates having a Stokes corresponding diameter of at least 100 nm. With regard to CTAB, it must be recognized that although the nitrogen adsorption method which is usually employed in connection with the measurement of the specific surface area of carbon black, is a good evaluation method, carbon black has several Å-diameter fine pores over a large part of all of the surface area thereof. Thus, rubber can not penetrate into the pores. Therefore, the evaluation of the specific surface area of the pores into which rubber can penetrate should be carried out by the use of a so-called "large adsorption molecule," such as cetyltrimethylammonium bromide. The term "CTAB," in accordance with the present invention, means the evaluation of the specific surface area of fine pores in carbon black into which rubber may penetrate, and is indicated in terms of m 2 /g. The carbon black according to the present invention can be produced using a conventional oil furnace. One suitable method is discussed below. Other furnaces and methods will be apparent to one skilled in the art. A raw material having a uniform composition may be sprayed into a narrow region in a reaction furnace using a nozzle capable of controlling the oil drop distribution. The temperature in the furnace may be set at a high temperature, i.e., about 1800°C at the inner side of the furnace wall and kept uniform so as to optimize the production of fine particle size carbon black. Also, by controlling furthermore the combustion gas flow distribution, the reaction time can be reduced and made uniform. As mentioned above, D st of the carbon black in accordance with the invention is in the range of 50 - 80 nm. When D st is less than 50 nm, the operability and the low heat generation property of the tire tread composition are deteriorated remarkably. On the other hand, when D st is more than 80 nm, only a small further improvement of abrasion resistance is achieved. D st preferably ranges from 55 to 70 nm. ΔD 50 /D st is related to the unevenness of the aggregate distribution of the carbon black, i.e., whether the peak of the distribution curve is sharp or broad. When the value of ΔD 50 /D st becomes smaller, the uniformity of the carbon black and the reinforcing effect of the carbon black in the rubber composition increase. However, when the value of ΔD 50 /D st is less than 0.55, the operability and the low heat generation property of the rubber composition are deteriorated remarkably. On the other hand, when ΔD 50 /D st is more than 0.75, there is only a small further improvement in the abrasion resistance. Therefore, ΔD 50 /D st of the carbon black in accordance with the invention is in the range of 0.55 - 0.75, more preferably 0.60 - 0.70. Moreover, the present inventors have investigated in detail the aggregate distribution of carbon black as shown in Fig. 1 and found that even if ΔD 50 /D st is in the above-mentioned range, the uniformity of the distribution curve is not maintained, i.e., the lower part of the aggregate distribution curve is broadened at a region of large values of Stokes corresponding diameter focusing especially on abrasion resistance. While not wishing to be bound by theory, it is believed that this phenomenon is due to two things: (1) broadening of the distribution curve between a 1/2 value of the maximum frequency and 1/10 value thereof; and (2) "tailing" to a large-size-particle side of the distribution curve at a lower part thereof as shown in a hatched area of Fig. 1. In order to maintain the uniformity of the distribution curve, ΔD 10 /D st of the carbon black in accordance with the present invention is in the range of 1.0 - 1.5, preferably 1.1 - 1.4. When ΔD 10 /D st is less than 1.0, the workability and the low heat generation property of the rubber composition are deteriorated remarkably. When ΔD 10 /D st exceeds 1.5, only a small further improvement of the abrasion resistance is achieved. In order to avoid tailing of the distribution curve, it is necessary that the component ratio be 20% or less, preferably 15% or less. When the component ratio is more than 20%, only a small further improvement of abrasion resistance is achieved. Further, CTAB is in the range of 120 - 180 m 2 /g. If the value of CTAB is less than 120 m 2 /g, only a small further improvement of the abrasion resistance is achieved. On the other hand, when the value of CTAB is more than 180 m 2 /g, the low heat generation property and the workability of the rubber composition are deteriorated remarkably. The rubber component employed in the present invention may be selected from natural rubber and diene synthetic rubber. If both natural rubber and diene synthetic rubber are used in the present invention, it is preferable that the amount of the diene synthetic rubber is in the range of 10 - 80 parts by weight, more preferably 10 - 60 parts by weight, based on 100 parts by weight of the natural rubber. Any suitable diene synthetic rubber may be used in the present invention. For example, the diene synthetic rubber may be styrene-butadiene rubber, isoprene rubber, butadiene rubber. Other diene synthetic rubbers will be apparent to one skilled in the art. The compounding amount of the carbon black in accordance with the present invention is in the range of 30 - 100 parts by weight based on 100 parts by weight of the rubber component. When the amount of carbon black is less than 30 parts by weight, a sufficient abrasion resistance cannot be obtained. On the contrary, when the amount exceeds 100 parts by weight, the workability of the resulting rubber composition is deteriorated remarkably, and the dispersion of the carbon black in the rubber composition cannot be sufficiently attained and therefore, abrasion resistance is also deteriorated. Preferably, the carbon black is present in the rubber composition in an amount of 40 - 80 parts by weight based upon 100 parts by weight of the rubber component. The rubber composition according to the present invention may further contain an inorganic filler, such as silica, a vulcanizer, a vulcanizing accelerator, a softener and an antioxidant, each of which being added in an amount conventionally used in the rubber industry. According to the present invention, a pneumatic tire having a tread which includes the rubber composition of the present invention simultaneously and considerably improves the rolling resistance and the wear resistance of the tire without impairing the workability when producing the pneumatic tire. The present invention is explained in greater detail hereinafter by reference to specific examples, but the invention is not to be construed as being limited by the following examples. All percentages indicated herein are weight percentages unless otherwise defined. EXAMPLES Carbon blacks in accordance with the present invention (designated A - C) and carbon blacks for comparison purposes (designated D - G) were produced as shown below. Carbon blacks A - G were produced using the manufacturing apparatus shown in Figs. 2, 3 and 4. Referring now to Figs. 2, 3 and 4, wherein same numbers illustrate same elements, the carbon black manufacturing apparatus 1 includes combustion gas filling chamber 2, Venturi portion 3, reaction chamber 4 and reaction continuation and rapid cooling chamber 5. Further, a gas flue 6 is provided as is an opening 7 and inspection window 8. Gas inlets 9, 9', fuel fluid inlets 10, 10', 11, 11', 12, 12' (see Fig. 3), inlets 13, 13', and gas inlets 14-14''' (see Fig. 4) and 15-15''' are also provided in apparatus 1. Although not shown, inlets 15-15''' may be arranged in a manner similar to inlets 14-14'''. Insertion openings a-g are provided in apparatus 1 for cooling water-forcing spray apparatus. The dimensions and locations of each of the components of the manufacturing apparatus (1) may be as follows: Combustion gas filling chamber (2) inside diameter 420 mm ⊘ length 230 mm; Oxygen-containing gas inlet (9, 9') inside diameter 80 mm ⊘ center position 50 mm from the front end; Fuel fluid inlets (10 - 12') inside diameter 6 mm ⊘ six inlets were located at regular intervals; Venturi portion (3) entrance length 100 mm diameter at the narrowest position 140 mm ⊘ exit length 150 mm; Reaction chamber (4) diameter 200 mm ⊘ and crude oil inlets (13 - 13') diameter larger than those of spray nozzles center position anywhere in Venturi portion (3) Gas inlet (14 - 14''' and 15 - 15''' diameter 50 mm ⊘ center position 50 mm and 150 mm downstream from the exit of Venturi (3), respectively. If desired, a natural gas may be introduced into chamber (2) during the formation of the carbon black by an introduction pipe having a diameter of 13 mm located, for example, at a center of inlets 9 - 9'. A spray apparatus for introducing cooling water may be located at openings a - g in the reaction continuation and rapid cooling chamber (5) situated downstream of the reaction chamber (4). Stock oil having the characteristics and composition shown in Table 1 may be used to prepare the carbon black in accordance with the present invention. Natural gas including 86.3 vol.% methane, 7.3 vol.% ethane, 3.1 vol.% propane and 3.3 vol.% others was used as a fuel fluid. In the manufacturing of carbon black in accordance with the invention, the characteristics thereof may generally be controlled by the following: The value of CTAB may be controlled by varying the ratio of the whole amount of hydrocarbons to the whole amount of air introduced in the furnace. The CTAB value of the carbon black increases when the whole amount of air is increased. The value of 24M4DBP may be controlled by varying the amount of K + contained in the stock oil. 24M4DBP decreases when the amount of K + added to the stock oil is increased. The aggregate distribution may be controlled by introducing a revolving flow into the reaction chamber so as to suppress the occurrence of large aggregates, wherein the combustion flow and the revolving direction were the same as those of the upstream side. As a result, the amount of carbon black aggregates having a size of 100 nm or more were especially reduced. However, this amount is decreased when the position of the introduction of the revolving flow is moved downstream. The diameter of oil particles in the furnace apparatus may be decreased by increasing the introduction pressure of the stock oil and by making the diameter of the oil introducing nozzles small. In this manner, the diameter of sprayed particles is reduced and the distribution thereof is narrowed. In accordance with the above-mentioned controlling conditions, carbon blacks A - C of the present invention and carbon blacks D - F for comparison purposes were produced under the manufacturing conditions shown in Table 2, and the characteristics of the carbon blacks are shown in Table 3, respectively. Manufacturing conditions Examples A B C D E F G Supply amount of stock oil (l/h) 307 307 352 323 295 279 --- Number of spray nozzles for stock oil 2 2 3 3 3 3 --- Diameter of spray nozzles for stock oil (mm) 1.0 1.0 1.0 1.2 1.2 1.1 --- Spray pressure of stock oil (kg/cm 2 ) 35 35 30 20 20 25 --- Preheating temperature of stock oil (°C) 230 230 210 180 180 210 --- Amount of air introduced into combustion chamber (kg/h) 1699 1699 1699 2240 2240 1770 --- Amount of NG introduced into combustion chamber (kg/h) 72 72 72 81 81 51 --- Whole amount of air introduced into reaction chamber (kg/h) by: 451 451 451 0 0 470 --- Inlet No. 1 451 451 0 0 0 0 --- Inlet No. 2 0 0 451 0 0 470 --- Whole amount of NG introduced into reaction chamber (kg/h) by: 19 19 19 0 0 14 --- Inlet No. 1 19 19 0 0 0 0 --- Inlet No. 2 0 0 19 0 0 14 --- Amount of K + (based on stock oil, PPM) 18 15 14 14 19 19 --- Distance of the position of the cooling water spray from the position of stock oil spray, mm 1500 1500 1600 1500 1500 1400 --- Characteristics of carbon black Examples A B C D E F G CTAB (m 2 /g) 141 141 132 142 147 157 124 24M4DBP (mℓ/100g) 105 109 110 110 104 104 100 D st (nm) 59 65 71 62 57 57 75 ΔD 50 /D st 0.61 0.66 0.69 0.64 0.65 0.63 0.79 ΔD 10 /D st 1.36 1.29 1.32 1.70 1.94 1.33 1.75 Component ratio (%) 9.6 8.5 16.5 28.5 29.7 22.4 32.1 Table 3 shows the characteristic of carbon blacks in accordance with invention and comparative carbon black. The samples of carbon black designated A - C correspond to carbon blacks used according to the present invention and the samples of carbon black designated D - G correspond to comparative carbon blacks. The comparative carbon blacks have the following characteristics. The value of ΔD 10 /D st and the component ratio of carbon blacks D and E were more than 1.5 and 20%, respectively. The value of ΔD 10 /D st and the component ratio of carbon black F were less than 1.5 and more than 20%, respectively. Carbon black G is commercially available as Mitsubishi Kasei DIA-A and ΔD 50 /D st, ΔD 10 /D st and the component ratio of carbon black G are very different from those of carbon blacks employed in the present invention. Table 4 shows examples of rubber compositions in accordance with the invention and comparative examples of rubber compositions. The basic compounding formula of ingredients of the examples and comparative examples was as follows: natural rubber 100.0 parts by weight; carbon black 50.0 parts by weight; stearic acid 2.0 parts by weight; zinc white 4.0 parts by weight; antioxidant 2.0 parts by weight; vulcanization accelerator 1.0 parts by weight; sulfur 1.5 parts by weight; where the antioxidant was N-(1,3-dimethylbutyl)-N'-phenyl-P-phenylenediamine and the vulcanization accelerator was N-cyclohexyl-2-benzothiazylsulfenamide. A Mooney viscosity test based on JIS K 6300-1974 was carried out and the following formula was used for calculation: Mooney viscosity index = (the Mooney value of a test sample) / (the Mooney value of a sample of Comparative Example 1) The smaller the Mooney viscosity index, the better the workability. As far as an abrasion resistance test is concerned, first, a TBR 10,00 R 20 tire was manufactured and after 30,000 km of driving, the depth of the remaining tire tread was measured to determine the amount of abrasion (mm) using the following formula: Abrasion resistance index = (mileage of the test tire / the amount of abrasion) / (mileage of the tire of Comparative Example 1 / the amount of abrasion) The larger the abrasion resistance index, the better the abrasion resistance. A heat generation test was carried out using a spectrometer manufactured by TOYOSEIKI at a dynamic strain amplitude of 1.0 %, a frequency of 52 Hz, a measurement temperature of 25°C, and tanδ was determined by the following formula: Heat generation index = (tanδ of a test sample) / (tanδ of a test sample of Comparative Example 1) The smaller the heat generation index, the better the low heat generation property, that is, the lower the calorific value. Vulcanization of a sample for a rubber physical properties test was carried at 145°C and 35 minutes. Examples Comparative Examples 1 2 3 4 5 1 2 3 4 5 6 Carbon black used A B C A B D E F G D F Natural rubber (part by weight) 100 100 100 70 70 100 100 100 100 70 70 cis-1,4 polybutadiene (part by weight) - - - 30 30 - - - - 30 30 Carbon black (part by weight) 50 50 50 50 50 50 50 50 50 50 50 Mooney viscosity index 102 100 100 105 104 100 127 96 92 104 108 Low heat generation property index 92 94 90 87 86 100 94 104 94 96 103 Abrasion resistance index 110 109 107 111 112 100 100 101 90 104 105 As shown in Examples 1 - 5, the rubber compositions containing carbon blacks A - C representing the present invention have better abrasion resistance without deteriorating the low heat generation property and the processability in comparison to the rubber composition of Comparative Examples 1-6 containing conventional carbon blacks. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims: A rubber composition, comprising 100 parts by weight of a rubber component selected from the group consisting of natural rubber, diene synthetic rubber and mixtures thereof, and 30 - 100 parts by weight of carbon black having the following characteristics: (a) 24M4DBP of 0.95 - 1.30 ml/g; (b) D st of 50 - 80 nm; (c) ΔD 50 /D st of 0.55 - 0.75; (d) ΔD 10 /D st of 1.0 - 1.5; (e) a component ratio of 20% or less; and (f) CTAB of 120 - 180 m 2 /g wherein 24M4DBP represents the amount of DBP oil absorbed by the carbon black which has been crushed four times at a pressure of 165.5 MPa (24,000 psi) D st represents the most frequent Stokes corresponding diameter of aggregates of the carbon black, ΔD 50 and ΔD 10 represent the width in Stokes corresponding diameter in the aggregate distribution curve of the carbon black (abscissa: Stokes corresponding diameter of carbon black aggregates; ordinate: the weight percentage of carbon black aggregates) at the 50 % frequency position and the 10 % frequency position, respectively, component ratio represents the ratio of the area under the aggregate distribution curve corresponding to a Stokes corresponding diameter of at least 100 nm to the whole area under the distribution curve and CTAB represents the specific surface area of pores in the carbon block capable of having the rubber component penetrate therein. The rubber composition according to claim 1, wherein the rubber component includes both the natural rubber and the diene synthetic rubber, the diene synthetic rubber being present in an amount of 10 - 80 parts by weight based upon 100 parts by weight of natural rubber.

Inventors: KUSANO TOMOHIRO, OHASHI MASAYUKI, KUSANO, TOMOHIRO, OHASHI, MASAYUKI
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1994
Main classification: C08K3
IPC codes: C08L21, B60C1, C09C1, C08K3