Method and furncace apparatus for bending and tempering a glass sheet supported on a ring mould

Abstract: The invention relates to a method and furnace apparatus for bending and tempering glass sheets. A glass sheet is supported on the same outline mould throughout the entire handling process. A bending furnace (10) is designed to be sufficiently long in the traveling direction for carrying a partially bent glass sheet towards a tempering section (16) in such a manner that the glass sheet reaches its final shape during the passage occurring within the bending furnace (10). For this purpose, the glass sheet is heated in the bending furnace (10) with such a high effect that it reaches its tempering temperature before reaching its final shape. The movements and heating of glass sheets are controlled individually on the basis of the thickness and measured temperature of each glass sheet.

Description: The present invention relates to a method for sag-bending and tempering glass sheets supported on a ring mould, in which method a cold glass sheet is placed on a ring mould, the ring mould mould along with its glass sheet is carried through at least one preheating section into a bending furnace, the preheated glass sheet is heated in the bending furnace to a bending and tempering temperature, and the bent glass sheet is carried into a tempering section, wherein chilling air is blown to its opposite surfaces. The invention relates also to a furnace apparatus for sag-bending and tempering glass sheets, said apparatus comprising a loading and unloading station, a plurality of outline moulds provided with carrier wagons therefor, a separate bending furnace and a separate tempering section provided with nozzles for blowing chilling air to the opposite surfaces of a bent glass sheet. The invention is particularly suitable for bending relatively simple glass shapes that can be bent by the gravitational use of an outline mould. Many of the automotive side windows are of such relatively simple shapes that they can be bent by the application of a method and apparatus of the invention. There is a prior known method for essentially the same purpose, wherein a hemothermal glass is dropped onto an outline mould and the glass assumes its proper shape by virtue of the inertial force and the configuration of the outline mould (sag-bending). This prior known method offers benefits such as high capacity and operational reliability but it also involves drawbacks, such as expensive price, a rather long shape replacement time (4-5 h), the marks caused by dropping on the edge areas of a glass, and the high price of tools for each particular glass. On the other hand, there are prior known single furnaces operating on the outline mould principle, wherein the glass is only heated from above and the glass bends to its shape whose bending or flexural depth is determined by adjusting the heating time. The advantage offered by single furnaces is simplicity and a low price but the notable drawbacks include low capacity, a relatively large minimum thickness (typically 5 mm, sometimes 4 mm), simple bending shapes and only a moderate bending accuracy (as the bending depth is only controlled by means of the heating time). An object of the invention is to provide an improved method and furnace apparatus having a favourable price and a compact size in relation to capacity as well as low mould-related costs, facilitating also the bending of glasses of varying thicknesses as well as thin glasses. This object is achieved by the invention as defined in claims 1, 2 and 7. Flexible production and a simple replacement of glass shapes are achieved by the invention especially by arranging the movements and heating of each glass sheet individually according to the thickness and the measured temperature of the glass. The key factor in providing this individual passage system is a sufficient length for a bending furnace for facilitating the commencement of the passage of glass sheets in an accelerating motion towards the tempering section and a relatively long accelerating motion in the bending furnace even prior to reaching a final bending shape. When the glass sheet reaches a predetermined tempering temperature, which is the higher, the thinner a glass sheet in question, the passage motion is instigated in the furnace, the glass sheet reaching its final shape during the passage and, at the same time, the glass sheet reaches a sufficiently high traveling speed in view of advancing from the furnace into the tempering section in a time as short as possible. This differs essentially from the prior known furnace assemblies, wherein the passage from the bending furnace to the tempering section is started when the leading edge of a glass sheet is as close to the discharge opening of the bending furnace as possible, so that the deformation between the commencement of passage and the tempering would be as slight as possible. The glass sheet is supported on the same outline mould throughout the handling process. Loading and unloading are effected at the same station, whereby the glass sheets proceeding from loading to preheating are forced to travel below the tempering section. Preheating sections are located on two levels and, thus, at least one preheating section is located below the bending furnace. One exemplary embodiment of the invention will now be described in more detail with reference made to the accompanying drawing, which shows a bending furnace of the invention in a perspective view. A glass sheet to be bent is placed in a cold state upon an outline mould 3 at a combined loading and unloading station 1. The outline mould 3 is carried on a wagon 2 along a lower horizontal track extending below a tempering section 16 through an opening 4 into a preheating section 5. The opening 4 can be closed and opened by means of a cover, not shown. The preheating section 5 is provided with resistances 6 for heating a glass sheet at least from above with radiation heat. From the preheating section 5 said wagon 2, along with its mould 3 and glass sheet, is advanced into a space 7 below a second preheating section 8 and lifted with a hoist into the preheating section 8 provided with resistances 9 for continued heating. As prior known, the preheating can be performed quite rapidly since heat transfers effectively to cold glass. In preheating, the glass sheet typically reaches a temperature of about 500°C. Naturally, the final temperature of preheating may vary considerably one way or the other. The preheated glass is carried on the outline mould 3 into a bending furnace 10 which simultaneously serves as an effective heating chamber having a temperature typically within the range of 800° - 1000°C. The bending furnace 10 is provided with effective resistances 11, 12, 13 for heating a glass sheet so rapidly that it reaches a tempering temperature before it is deformed to its final shape. For example, the 4 mm glass heats from 500°C in about 15 - 20 seconds to a tempering temperature of 600° - 630°C, typically 615° - 620°C. During this rapid heating, the glass is also allowed to bend or sag. A pyrometer is used for monitoring the temperature of heating and bending glass. Upon reaching a predetermined temperature, which substantially corresponds to the tempering temperature or is close to it, the passage of the glass sheet towards a tempering section 16 is commenced at an accelerating speed before the glass sheet has bent to its final shape. Thus, the bending to a final shape occurs during the course of a relatively long passage within the bending furnace 10. In order to be able to carry out the above procedure, the bending furnace 10 as well as the assembly of resistance arrays above and below a glass sheet are made longer than usual in the traveling direction of a glass sheet. In a typical case, the bending furnace 10 has a length which is about 1,5 times the length of preheating sections 5 and 8. Accordingly, the upper resistance array 11, 12, 13 and lower resistance array 14, 15 in the bending furnace 10 have a length in the traveling direction of a glass sheet which is about 1,5 times the length of resistance arrays 6 and 9. Also the resistance arrays 6 and 9 have a length which clearly exceeds the length of a typical glass sheet (e.g. a rear window of a car) in its traveling direction. In the bending furnace 10, the resistance arrays have a length which is more than twice the height of a typical automotive backlight. This makes it possible that a glass sheet is capable of traveling within the furnace 10 between the upper and lower resistance arrays a distance corresponding to 10 dimensions thereof in the traveling direction. In other words, the passage towards the tempering section is commenced at a point when the leading edge of a glass sheet is a distance away from a discharge opening 20 of the bending furnace 10, said distance being at least equal to the height of a glass sheet, i.e. its dimension in the traveling direction. In view of the fact that a soft glass sheet supported on an outline mould can only be subjected to a certain limited acceleration, the glass sheet can be given a traveling speed of about 1 m/s (at least about 0,8 m/s) before the leading edge of a glass sheet leaves the bending furnace 10. The passage of a partially bent glass sheet can be commenced at that end of furnace 10, which is furthest away from the tempering section 16, or also in the middle of said furnace 10 with the glass sheet moving first backwards and then commencing an accelerating motion towards the tempering section 16. The former alternative is the simplest in view of operation control as a glass sheet arriving from preheating section 8 in bending furnace 10 stops in the inlet end of furnace 10 as soon as it is entirely between the resistance arrays. The heat distribution in furnace 10 is controlled by the disposition of resistances. Thus, it is preferable that the upper resistance array be provided with resistances 11 extending in the traveling direction substantially over the entire length of the furnace. The end sections of resistances 11 are further provided with crosswise resistances 12 and 13 for preventing too sharp a decline of heating effect at the ends of the resistance array. The lower resistance array of furnace 10 comprises crosswise resistances 14, which cover substantially the entire heating area of the furnace and whose ends are provided with longitudinal resistances 15. Predetermined resistances included in the resistance arrays 11, 12, 13 and 14, 15 of bending furnace 10 are adapted to switch on at a certain time before a glass sheet arrives in the bending furnace 10. Predetermined resistances are also adapted to switch off as a glass sheet leaves the bending furnace. During the intermission while the furnace is empty, the only resistances maintained switched on are those required for keeping the temperature of an unloaded bending furnace 10 substantially stable. The object of this arrangement is that, although the glass sheets are manipulated and heated as individuals, it is possible to maintain a stable and reproducible environment in the furnace, i.e. the effect of the inertial mass delay of the resistances will be eliminated. As prior known, the thinner a glass in question, the higher a tempering temperature is required. Accordingly, the furnace must be hotter. Thus, the ideal temperature in the furnace must be found individually for each glass thickness. This also requires the use of such an operation control that each glass sheet travels as an individual, i.e. the movements of glass sheets are temporally and locally independent of each other. The operating cycle is typically about 1 minute or the furnace produces approximately 60 bent and tempered glass sheets per hour. The number can be less, e.g. 40 sheets/h, if an unloaded wagon is run after every two glass sheets for equalizing the temperature. The dwelling time of a thin glass sheet in the bending furnace 10 is typically only about 10 - 15 seconds. During the interval, the bending furnace 10 is empty. The required resistances in the resistance arrays of furnace 10 are switched on e.g. about 10 seconds before another glass sheet arrives in the empty furnace. In order not to become overheated in furnace 10, a glass sheet must be transferred as quickly as possible to tempering. This is assisted by the above-described accelerating motion in furnace 10 during the final bending of a glass sheet. The transfer from bending to tempering can be further sped up by timing the approaching action of nozzle boxes 17 and 18 in the tempering section 16 to commence as soon as the leading edge of a glass sheet has passed the lowest point located in the mid-section of the nozzle boxes. Thus, the question is about nozzle boxes conforming to the bent outline of a glass sheet, said nozzles being capable of blasting from a position sufficiently close to a glass sheet. When a glass sheet stops between nozzle boxes 17 and 18, the latter have already drawn near the final position thereof. Fans 19 supply chilling air to the nozzle boxes 17 and 18. As soon as the tempering is finished, said nozzle boxes 17 and 18 are drawn away from each other for carrying the glass sheet to a location alongside and above the loading and unloading station 1. When the loading and unloading station is empty, the bent and tempered glass sheet can be lowered down on the lower track level for carrying it into said loading and unloading station 1. The bent and tempered glass sheet is removed from mould 3 and it is replaced with a flat, cold glass sheet which is carried below tempering section 16 into preheating section 5. Thus, the glass sheets are supported on the same outline mould throughout the entire handling process. This simplifies substantially the construction and operation of the apparatus as compared to cases, wherein the glass sheet must be transferred from one supporting bed onto another. Operation of the furnace apparatus can be completely automated and the operator is only required to input information about the thickness of any given glass sheet to be bent.

Claims: A method for sag-bending and tempering glass sheets supported on a ring mould, in which method a cold glass sheet is placed on a ring mould (3), the ring mould mould along with its glass sheet is carried through at least one preheating section (5, 8) into a bending furnace (10), the preheated glass sheet is heated in the bending furnace (10) to a bending and tempering temperature, and the bent glass sheet is carried into a tempering section (16), wherein chilling air is blown to its opposite surfaces, characterized in that a partially bent glass sheet is carried through the bending furnace between resistance arrays (11-15) at an accelerating speed towards the tempering section and that this passage towards the tempering section is commenced at a point when the leading edge of the glass sheet is a distance away from a discharge opening (20) of the bending furnace (10), said distance being at least equal to the dimension of the glass sheet in the traveling direction, the commencing moment of said passage being determined on the basis of the temperature and/or degree of bending of the glass sheet in such a manner that the glass sheet reaches its final shape in the bending furnace (10) at the end of said passage towards the tempering section, before entering into the tempering section. A method for sag-bending and tempering glass sheets supported on a ring mould, in which method a cold glass sheet is placed on a ring mould (3), the ring mould mould along with its glass sheet is carried through at least one preheating section (5, 8) into a bending furnace (10), the preheated glass sheet is heated in the bending furnace (10) to a bending and tempering temperature, and the bent glass sheet is carried into a tempering section (16), wherein chilling air is blown to its opposite surfaces, characterized in that the glass sheet is heated in the bending furnace (16) with such a high heating rate that the glass sheet reaches a tempering temperature before reaching its final shape and that the passage of the glass sheet through the bending furnace towards the tempering section is commenced as soon as the glass sheet has reached a predetermined temperature which is at least near the tempering temperature, the bending of the glass sheet to its final shape occurring during the passage within the bending furnace before entering into the tempering section. A method as set forth in claim 1 or 2, characterized in that the length of the passage for a glass sheet in the bending furnace, before the leading edge of the glass sheet leaves the bending furnace, is at least 1,5 times the dimension of the glass sheet in the traveling direction and that the traveling speed of the glass sheet is increased throughout the passage until the glass sheet has partially left the bending furnace (10). A method as set forth in claim 1 or 2, characterized in that the loading and unloading of glass sheets are effected at a common station (1), a cold glass sheet is carried below the tempering section (16) into a first preheating section (5) located below the bending furnace (10), and the glass sheet is supported on the same outline mould (3) throughout the entire handling process. A method as set forth in any of claims 1-4, characterized in that the temperature of the bending furnace (10) is adjusted individually according to the glass thickness in such a manner that each glass thickness has a predetermined temperature, which is the higher the thinner the glass is. A method as set forth in any of claims 1-5, characterized in that the movements and heating of each glass sheet are controlled individually on the basis of the thickness and measured temperature of a glass sheet. A furnace apparatus for sag-bending and tempering glass sheets, said apparatus comprising a loading and unloading station (1), a plurality of outline moulds (3) carried by carrier wagons (2), at least one preheating section (5, 8), a separate bending furnace (10) and a separate tempering section (16) provided with nozzles (17, 18) for blasting chilling air to the opposite surfaces of a bent glass sheet, characterized in that a resistance array (11) included in the bending furnace (10) has a length in the traveling direction of the glass sheet which is at least 1,5 times the dimension of the glass sheet in traveling direction and, at the final stage of bending, the glass sheet is adapted during the bending thereof to be movable in horizontal direction within the boundaries of the resistance array (11) towards the tempering section (16) and that the furnace comprises monitoring means for monitoring the temperature and/or the degree of bending in the bending furnace, and operation control means responsive to the monitoring means, for starting the movement of the glass sheet towards the tempering section and accelerating the glass sheet so that the glass sheet reaches its final shape just before entering the tempering section. An apparatus as set forth in claim 7, characterized in that the glass sheet is set in the bending furnace in an accelerating motion so that the glass sheet reaches a traveling speed of at least 0,8 m/s before the leading edge of the glass sheet leaves the bending furnace. An apparatus as set forth in claim 7, characterized in that at least one preheating section (5) is located below the bending furnace (10) and the passageway for glass sheets from the loading station (1) to said preheating section (5) is located below the tempering section (16). An apparatus as set forth in claim 7, characterized in that predetermined resistances included in the resistance array (11) of the bending furnace (10) are adapted to switch on at a certain moment in advance of the arrival of a glass sheet in the bending furnace (10) and to switch off when the glass sheet leaves the bending furnace, whereby during the interval when the furnace is empty, the only resistances (11) being switched on are those required for maintaining the temperature of the empty bending furnace (10) substantially stable. An apparatus as set forth in any of claims 7-10, characterized in that the bending furnace (10) is provided with an upper resistance array (11), which includes resistances whose longitudinal direction is the same as the traveling direction, and a lowqer resistance array (14), which includes resistances whose longitudinal direction is transverse to the longitudinal direction of the upper resistances. An apparatus as set forth in claim 11, characterized in that the ends of the resistances included in said resistance arrays (11, 14) are provided with resistances (13, 12 and 15) which are transverse relative to the above resistances. An apparatus as set forth in any of claims 7-9, characterized in that the bending furnace (10) has a length in the traveling direction of a glass sheet which is substantially longer, preferably about 1,5 times longer than the length of each preheating section (5, 8).

Inventors: PAAVOLA JUHA, VEHMAS JUKKA, PAAVOLA, JUHA, VEHMAS, JUKKA
Applicants: TAMGLASS ENG OY, TAMGLASS ENGINEERING OY
Application year: 1994
Main classification: C03B23
IPC codes: C03B23, C03B35, C03B27