COMPOSITION CONTAINING CHOLESTYRAMINE AND METHOD OF PRODUCING THE SAME

Abstract: Cholestyramine and starch containing oil-free compositions with excellent organoleptic features are obtained by mixing cholestyramine and grain starch in a weight ratio of 1:1.8 to 2.9 with the addition of grain bran has a filler and optionally an aroma stuff with 10 to 35 % by weight of water (calc. on the starting materials) into a homogeneous moist mass, forming of the mass through extrusion into a string, whereby the temperature is 105 - 180 DEG C (measured in the mass in the extrusion head) and the pressure is 30 - 70 bars (measured in the extrusion head), and subsequently drying at a temperature above 100 DEG C to a remaining humidity of </= 3.5 % by weight, whereby the extruded material before or after the drying is divided into bars or is grinded into a powder.

Description: Composition containing cholestyramine and method of producing the same The invention relates to a method of producing oil-free composi¬ tions containing cholestyramine and starch, esp. in the form of bars for the immediate consumption by hypercholesterinaemie patients. Cholestyramine is the international free name (INN of WHO) for the chloride of a styrene-divinyl benzene-copolymerisate contai¬ ning quaternary ammonium groups. Cholestyramine is effective as ion exchanger for binding of gallic acids and at hypercholeste¬ rinaemie as lipid-lowering agent. In the last mentioned use quite large dosages have to be used, which might be as high as between 4 and 16 g for each separate delivery and up to 32 g daily. This is a problem because cholestyramine is present in the form of very fine, water-insoluble ion-exchange particles. When eating this in suspended or solid form a fishy smell and taste occurs and moreover an unpleasant sandy taste remains in the mouth thereafter, which sometimes is also called "drifting sand effect". Therefor it is difficult to get patients to take in cholestyramine preparations on a regular basis over a pro¬ longed time in required the high doses. The most varying attempts have already been made to transfer cholestyramine into a more patient-friendly form, which should be easy to use, i.e. could be eaten directly, and tasty. Among others, suspensions (e.g. in the form of fruit juices) , powder, bakery products and bars (for example in the form of sweet nougat or chocolate bars) have been developed. The cholestyramine compositions according to DE-A-38 08 191 are present in the form of an aquous suspension with fixed viscosi- ty. The EP-A-347 014 describes cholestyramine containing bakery pro¬ ducts, which are manufactured by baking for 20 minutes at about 150 - 180 °C from a dow, which, besides water contains a cooking oil, a mono- or polysaccharide, aroma stuffs as well as chole¬ styramine. From the EP-A-492 235 are previously known non-baked cholestyra- mine products with a humidity of < 11%. These products contain cholestyramine, cereals such as flour or bran, sugar, aroma stuffs, binding agents based on starch as well as optionally cooking oil. The working is performed in such a way that the mixture is not baked at temperatures of 150 °C or above, but instead is dried at about 70 °C under reduced pressure over a long time of about 16 to 48 hours, until the desired low humi¬ dity content has been achieved. None of the suggestions known sofar has led to a cholestyramine product in solid form, which fullfil the above mentioned claims regarding smell and taste, having a simple composition and being apt to be manufactured only with the aid of technologies at disposal. The object of the invention is to solve these prob¬ lems. Surprisingly it has been found that in view of nutritional physiology and also " iri view of taste and smell in all aspects satisfactory cholestyramine products are obtained in solid form, when the recipe as well as the manufacturing conditions are selected in a certain way and are adjusted to each other. Thus, the object of the invention is a method for manufacturing cholestyramine and starch containing compositions free of oil, preferably in the form of bars, especially for the immediate intake by hypercholesterinaemie patients, which is characterized in that cholestyramine and grain starch in a weight ratio of 1:1,8 - 2,9, pref. 1:2,2 - 2,7, under the addition of grain bran as filling agent and optionally an aroma stuff with 10 - 35 % by weight (in rel. to the starting materials) is mixed into a homogenous hu ide mass, which mass is processed by extrusion into a string, whereby the temperature (measured in the mass in the extrusion head) is 105 - 180°C and the pressure (measured in the extrusion head) is 30 - 70 bar, and in that subsequently a drying is performed at a temperature above 100°C to a remaining humidity of < 3,5 % by weight, whereby the extruded goods pre¬ ferably before or after the drying step is divided into bars or is grinded into a powder. With "bars" within the scope of the present invention is meant disc- or blockshaped articles. The dimensions are chosen so that a bar contains the single dose to be administered of cholestyra¬ mine. With a thickness of 1 - 12 mm the width may be e.g. 20 - 50 mm and the length 100 - 160 mm. Alternatively the extruded goods can be grinded into a powder (particle size preferably < 2 mm) and in this form be added to e.g. milk, water, juice containing compote or other drinks, youghurt and the like. The organoleptic characteristics of special advantage are obtai¬ ned with a surprisingly simply built recipe. Normal additives such as oils or fats, fermentative agents and taste pasting polymers or gelating agents are not needed. The optional addi- tion of aroma stuffs is substantially performed in order to achieve different trends in taste and less for pasting the taste and smell of the products per se. According to a preferred embodiment starch and bran from the same grain, that is for example wheat starch and wheat bran, are used in a recipe. The content of bran (referring to the starting materials) is usually less than 10 % by weight, preferably up to 7,5 % by weight. In case aroma stuffs are used, e.g. special dry aromas of bread type, the application on the bar might be per- formed right at the end of the manufacturing process after the drying of the bar. Wheat, rice and corn starch are especially well suited. Regar¬ ding the bran used this is preferably wheat or rice bran. Then the bran as such might be stabilized by the addition of starch. Especially preferred compositions consists of 30 % by weight of cholestyramine, 65 % by weight of wheat starch and 5 % by weight of wheat bran and of 25 % by weight of cholestyramine, 67,5 % by weight of wheat starch and 7,5 % by weight of wheat bran, re¬ spectively. Optionally, to this is also added the dry aroma. Further, for the advantages achieved according to the invention it is important to observe the above given process conditions, which differs clearly from those of a drying process or a conv¬ entional baking process. As well in drying as also in baking the water contained in the moist mass is evaporated, so that a final product with a corresponding low remaining humidity is obtained. Because of the higher temperatures used in baking the starch is degraded to a larger degree compared to in drying, whereby especially a ylose and amylopectin is formed. In contrast there¬ to in the extrusion used according to the invention the water cannot escape or only partly escape at higher temperatures (so called cocking extrusion) . Under these conditions (besides the temperature, the pressure is also substantially increased com¬ pared with a drying or baking process) the starch is degraded to a large extent, and especially dextrine is formed. It can be anticipated that for the success of the inventions besides the alternate recipe also these different process conditions are responsible. At the extrusion a substantial reduction of the water content takes place, e.g. from 35 to about 10 to 20 %. The drying to the final humidity of < 3,5 % is obtained through heating up to 130°c or through short time microwave treatment up to about 175°C. In the last case advantageously a further drying and careful cooling is performed in a following heating air tunnel until the product has the low temperature necessary for the packaging. Because of the low humidity the bars manufactured according to the invention are hygroscopic. Thus, it is advisable to pack the bars produced moisture-proof, e.g. by using suitable compound films with an aluminium layer as a water blocking layer. Com¬ pound films are available commersially, e.g. forms of paper/polyethylene/aluminium/polyethylene, polypropylene/- aluminium/polyethylene or polyethyleneterephtalate/aluminium/- polyethylene. The examples given below serve for a more detailed explanation of the invention, the invention, however, not being limited thereto. Examples The following recipes were made: Recipe A: Cholestyramine 4000 mg (30 % by weight) wheat starch 8600 mg (65 % by weight) wheat bran 700 mg ( 5 % by weight) For the manufacture of about 100 000 bars the mixture had the following composition: Cholestyramine 400 kg wheat starch 860 kg wheat bran 70 kg pur. water 332.6 kg dry aroma 0,4 kg Recipe B: Cholestyramine 4000 mg (25 % by weight) wheat starch 10800 mg (67,5 % by weight) wheat bran 1200 mg ( 7,5 % by weight) Manufacturing process: Firstly, cholestyramine, wheat starch, wheat bran as well as optionally dry aroma is mixed homogenously in an intense mixer. Experiment 1 to 3 This mass were homogenized after the addition of the sufficient amount of water, extruded through a round die and formed into bars. The extrusion was performed with the aid of a single extruder screw. The control of the process parameters (tempera¬ ture and pressure) was made according to a predetermined recipe (important are especially starch and water contents) through the selection of temperature as well as screw velocity, screw geometry and screw arrangement. The extruder used did have three heatable zones around the screw, which were heated through heating elements connected after one another. Firstly, the whole mass was compressed and kneaded at a rotational speed of 15 r.p.m., which led to a quick heating and melting of the mass. At about 170°C temperature of the mass and a pressure of 50 bar (measured in the extruder head at a steady production phase) the soft, "gelatinized" mass became a viscous fluid. This was extruded through a circular nozzle. At the egress of the string from the nozzle the expansion phase of the mass began, whereby small, mainly open cells are formed through the escaping water vapor. The pressure build-up in the extruder before the nozzle head depends on the temperature, the throughput and the nozzle geometry, whereby the pressure again is important for the form¬ ing and expansion conditions, respectively, of the mass after leaving through the nozzzle. On the round string nozzle, which in the present case had a diameter of 5.0 mm, a diffusor nozzle was welded, in order to give the expanded material the desired flat bar form. A string with a width of 35 mm and a height of 10 mm was formed and divided into the desired length sections. With the extruder used a mass throughput of about 10 - 11 kg/h was obtained. Pressure and temperature of the mass were measured at the extruder head. For recipes A and B the following process parameters were used: Experiment no 1 2 3 Recipe A A B Nozzle 5.0 mm circu¬ 5.5 mm circu¬ 5.0 mm circu¬ lar nozzle lar nozzle lar nozzle Torque [Nm] 243.1110.1 222.3116.3 245.4113.8 R.p.m. 151.210,4 150.710.3 150.710.5 Pressure [bar] 49.411.0 56.315.5 49.4+1.0 Temp. [ °C] 174.210.4 168.411.9 174.511.7 The bars were subsequently post-dried in a drying plant (Horden- trockner) at 130°C during 15 - 25 minutes to "a remaining water content av 2.5 to 3.5 % by weight. Through this post-drying a loose and crispy product is obtained and at the same time the remaining humidity is reduced to below equilibrium humidity, which prevents a microbiological destruction. Experiment 4 and 5 The mass homogenized in the shearing mixer was extruded with the aid of a double screw extruder (Berstorff ZE 40A - 330; screw diameter 40 mm, screw length 1530 mm) . This "cooking extruder" with double screw characteristics has the advantage that a fur¬ ther thorough mixing and contemporary a reduced mechanical strain of the mass is obtained. The necessary amount of water would be supplied with the aid of a dosing pump after the first heating step in the extruder. The extruder plant has 7 heating zones and a heatable head piece. The last heating zones were set at a temperature of 130°C, the head zone on a somewhat lower temperature. It was possible to cool the extruder by a water supply in order to guarantee an exact temperature control. The crossing from the head piece to the forming nozzle was made through a bevelled slit nozzle (length 40 mm, height 10 mm) . In the connected nozzle the slit tapered over a distance of 15 mm to 30 mm length and 6 mm height. The temperature of the mass and the pressure of the mass was registered at the extruder head and was recorded. After leaving the nozzle the extruded material had a size of 40 mm width and 14 mm height. In the experiments the following process parameters were used. Experiment No 4 5 Recipe B B Nozzle slitnozzle 30x6 mm slitnozzle 30x6 mm r.p.m. 170 170 Temperature [°C] 111 115 Pressure [bar] 35 - 46 34 - 37 The extruded material was transferred to a cutting device with the aid of a conveyor. The drying was performed with the aid of a microwave dryer and a subsequent hot air tunnel. During the microwave treatment a temperature of 170°C was reached for a short time and a remaining humidity of about 5 % was obtained. The object of the subsequent hot air tunnel was a further drying to a remaining humidity of < 3,5 % and a cooling down to 80°C, in order to make possible the subsequent packaging. In the experiments 1 to 5, bars having a width of 40 mm, a height of 6 mm and a length of 150 mm were manufactured. The bars had, when using a special dry aroma, such as of the type "bayrisches Gewϋrzbrot", a pleasant breadlike taste. It lacked the otherwise appearing unpleasant fishlike flavour and smell, and the bars did not show the feared driving sand effect, i.e. there was no furry or sandy feeling in the mouth. The ready, dried bars were packed in a moisture-proof compound sheeting of polyethylene terephtalat/aluminium/polyethylene (HELIOnal® aluminium-kombinationsfolie) , air and moisture- tight, which was necessary in view of the hygroscopic features of the products. By grinding the extruded material and subsequent screening (< 2 mm) a composition in powder form was obtained, which like prod¬ ucts existing on the market can be consumed in ample fluid or by addition to food-stuffs (such as milk or youghurt) . The "driving sand effect" does not occur here either, which have been shown through blind experiments with a patients collective.

Claims: Claims 1. Oil-free composition containing cholestyramine and starch, preferably in the form bars, especially for the immediate con- sumption by hypercholesterinaemie patients, obtainable by mixing of cholestyramine and grain starch in a weight ratio of 1:1.8 to 2.9 with the addition of grain bran as a filler and optionally an aroma stuff with 10 to 35 % by weight of water (calculated on the starting materials) to a homogenous moist mass, extruding to form the mass into a string, whereby the temperature is 105 to 180°C (measured in the mass in the extruder head) and the pres¬ sure is 30 to 70 bars (measured in the extruder head) , as well as subsequent drying at a temperature exceeding 100°C to a remaining moisture content < 3.5 % by weight, as well as divid- ing the extruded material before or after the drying into bars or grinding the extruded material into a powder. 2. Method of manufacturing cholestyramine and starch containing, oil-free compositions, preferably in the form of bars, especial- ly for the immediate consumption by hypercholesterinaemie patients, characterized in mixing cholestyramine and grain starch in a weight ratio of 1:1.8 to 2.9 with the addition of grain bran as a filler and optionally an aroma stuff with 10 to 35 % by weight of water (calc. on the starting materials) into a homogenous moist mass, forming of the mass through extrusion into a string, whereby the temperature is 105 - 180°C (measured in the mass in the extrusion head) and the pressure is 30 - 70 bars (measured in the extrusion head) , and subsequently drying at a temperature above 100°c to a remaining humidity of < 3.5 % by weight, whereby the extruded material before or after the drying is divided into bars or is grinded into a powder. 3. Method according to claim 2, characterized in using starch and bran from the same grain. 4. Method according to claim 2 or 3, characterized in using wheat starch and wheat bran. 5. Method according to claim 2 - 4, characterised in adding up to 7.5 % by weight of bran (cal. on the starting materials). 6. Method according to claim 2 - 5, characterized in drying to a remaining humidity of 2.5 to 3.5 % by weight. 7. Method according to claim 2 - 6, characterized in applying the aroma stuff on the bar after the drying. 8. Method according to claim 2 - 7, characterized in that the bars are packaged using a water-vapor impenetratable compound sheeting.

Inventors: FRIESS STEFAN, HECKENMUELLER HARALD, FRIESS, STEFAN, HECKENMUELLER, HARALD
Applicants: ASTRA AB, FRIESS STEFAN, HECKENMUELLER HARALD, AKTIEBOLAGET ASTRA, FRIESS, STEFAN, HECKENMUELLER, HARALD
Application year: 1994
Main classification: A61K31
IPC codes: A61K9, A61K31, A61K47, A61P3