Coating composition for a subbing layer on a polyester film for light sensitive material

Abstract: The present invention discloses a subbing coating composition for polyester films comprising: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO₃X and/or -PO₃XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO₃X and/or -PO₃XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the coating composition does not comprise addition polymerizable compounds.

Description: Field of the Invention This invention relates to a coating composition which, when applied to a polyester film, constitutes a subbing layer which imparts improved adhesion towards a subsequently applied light sensitive material. It also relates to a polyester film coated with the above coating composition as well as to photographic film comprising a polyester base film having on at least one surface thereof a layer of the above coating composition and a light sensitive photographic layer on top of this layer. Background of the Invention Due to its physical properties polyester film is an excellent support for photographic film. However, it has been difficult to obtain good adhesion towards hydrophilic photographic emulsions because polyester, as is known, is generally very hydrophobic since it does not have active functional groups for the hydrophilic emulsion to attach to. There have been suggested several ways in the prior art to render the surface of a polyester film hydrophilic so that a photographic emulsion can be directly applied onto that surface. Such methods comprised chemical treatments such as etching or corona, flame or plasma treating the polyester film surface. Another approach for rendering hydrophilicity to the film surface was to apply a subbing layer onto the polyester film. Such a subbing layer would perform a double function, i.e. it would have good adhesion towards the polyester base film on the one side and at the same time good adhesion towards the photographic emulsion. Other methods known in the art first apply an auxiliary primer layer to the polyester film surface and thereafter a subbing layer on top of the auxiliary layer. The photographic layer is then applied onto the subbing layer. The purpose of such primer layers is to enhance the adhesion of the subbing layer towards the polyester film. JP-A-1025051 (Derwent Abstract No. 89-072754) discloses the manufacture of a humidity sensitive element comprising crosslinking a polymer having sulphonic acid and/or carboxyl groups, and a polymer including hydroxyl group of polyvalent alcohol, and applying the composite onto a base having a comb-shaped electrode. Miller, U.S.-A-4,701,403 describes an antistatic coating for polyester film which coating comprises a water soluble copolymer of the sodium salt of styrenesulfonic acid and a carboxy containing monomer which copolymer is crosslinked after drying with an aziridine component. Cho, U.S.-A-4,960,687 also describes a subbing layer containing a polymer having functionally attached carboxylic acid groups such as poly- (sodium styrenesulfo nate-maleic-anhydride) and a polyfunctional aziridine crosslinking agent for such COOH-containing polymer, which crosslinking agent is dispersed in gelatin. Ochiai et al., U.S.-A-4,124,395 also suggests copolymers made from maleic acid anhydride and styrene sulfonic acid in combination with an addition polymerizable monomer which may be acrylic acid, itaconic acid or triazines. Optionally a crosslinking agent may be added to the subbing composition such as crosslinking agents having a hydroxy group. All of these known subbing layers either employ hazardous materials such as aziridines or require the use of organic solvents, the use of which in production plants is subject to severe restrictions. It was therefore an object of the instant invention to suggest a subbing layer composition which neither employs hazardous material nor requires the use of organic solvents. While accomplishing this the subbed films should at the same time provide sufficient adhesion towards a subsequently applied photographic layer. It further would be advantageous if the subbed film exhibited antistatic properties. Summary of the invention These an other objects of the invention are achieved by a subbing coating composition comprising: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or - PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the coating composition does not comprise addition polymerizable compounds. This coating composition for a subbing layer neither employs hazardous materials nor requires organic solvents and can be brought onto a polyester film surface with known methods. It provides good adhesion towards a subsequently applied light sensitive photographic layer. The invention further relates to a polyester base film, having on at least one surface thereof a subbing coating which subbing coating comprises: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or - PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. In one embodiment said polyester base film has on at least one surface thereof a primer coating and on said at least one primer coating at least one subbing coating. The invention still further relates to a photographic film comprising a polyester base film, having on at least one surface thereof a subbing coating and on that at least one subbing coating at least one coating comprising a light sensitive material, wherein the subbing coating comprises: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or - PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. In one embodiment said photographic film comprises said polyester base film, having on at least one surface thereof a primer coating and on said at least one primer coating at least one subbing coating and on that at least one subbing coating at least one coating comprising the light sensitive material. The invention also relates to a process for applying a liquid subbing coating to a polymeric film in a process for manufacturing biaxially oriented polymeric films, comprising bringing a primer coating in-line directly upon a cast sheet of polymeric base film as that sheet is cooled upon extrusion in advance of a first drawing stage and after the first drawing stage, coating the primer coated film with said subbing coating, with said subbing coating comprising: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or - PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. Detailed description of the invention The coating composition according to the invention comprises a polymer A which has attached to its backbone carboxy groups and/or groups which will form carboxy groups upon hydrolysis. The term "backbone" as used herein means the chain which is built during polymerization of the corresponding monomers. Attached to this backbone are carboxy groups or groups which will form carboxy groups upon hydrolysis. Such groups are either attached directly to the backbone or via a spacer which can be an alkylene group having one to about 8 carbon atoms. Groups which form carboxy groups upon hydrolysis comprise anhydride, esters, carboxylic acid chlorides, nitriles and acid amides. Polymer A maybe a homopolymer or a copolymer. Specific examples of monomers which are suitable for forming polymer A are acrylic acid, acryloxy propionic acid, methacrylic acid, ethacrylic acid, maleic acid, maleic acid anhydride, itaconic acid, itaconic acid anhydride, vinyl benzoic acid, succinic acid or sorbic acid, with maleic acid anhydride being preferred. Copolymerizable comonomers suitable for forming a copolymer comprise esters of acrylic acid or methacrylic acid such as methyl-, ethyl-, butyl-, ethylhexyl- and phenyl-esters of acrylic acid and methacrylic acid; hydroxyalkyl acrylates and -methacrylate such as 2-hydroxyethylacrylate, 2-hydroxyethylmethacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropylmethacrylate and 3-hydroxypropylmethacrylate; vinyl esters such as vinyl acetate, vinyl propionate and vinyl benzoate; vinyl ethers such as methylvinyl ether, butylvinyl ether, and phenylvinylether. Preferred copolymerizable monomers are styrene, vinyl acetate and those containing a vinyl ether group. One especially preferred copolymer is poly(methylvinyl ether/maleic anhydride) commercialized by International Specialty Products (Wayne, New Jersey) under the tradename Gantrez®AN Copolymer. Polymer B is a polymer having attached to its backbone functional groups which impart water solubility and antistatic properties. Such functional groups comprise -SO 3 X, -PO 3 XY. X and Y represent metal ions, especially alkali metal ions such Li + , and Na + and K + , ammonium or a corresponding organic quaternary ammonium ion or a proton. X and Y preferably represent Na + , K + or H + . It is, however, understood that in a given polymer B not all X and/or Y radicals will have to be identical; i.e., also partial salts are within the scope of the invention. One preferred polymer B is polystyrene sulfonic acid which is commercialized by National Starch and Chemical Corporation under the tradename Versa® TL72. In case of the polyester base films and the photographic films according to the invention instead of using individual polymers A and B it is also possible to employ a copolymer A' which incorporates the functionality of both polymers A and B. Such a copolymer A' can be synthesized from the same monomers which are used to produce polymers A and B. Such a copolymer A' would have attached to its backbone carboxy functional groups as well as sulfonic acid and/or phosphonic acid functional groups. Organic compound C is a compound having at least two free hydroxy groups. Tri- and polyhydroxy compounds, i.e. compounds having three and more free hydroxy groups are within the scope of the invention. "Free hydroxy groups" are those OH-groups in an organic compound which are accessible for a chemical reaction. The function of compound C is to react with Polymer A and to a certain extent also with Polymer B, if present. Compound C contains a hydrocarbon nucleus to which at least two hydroxy groups are attached. The hydrocarbon nucleus itself may be represented by a branched or unbranched alkylene group which alkylene group may be interrupted by bivalent radicals such as carbonyl, carbonyloxy, oxy or thio. The hydrocarbon nucleus may also be represented by an arylene or alkylaryl which may in the same way be interrupted by bivalent radicals as are the alkylenes. Suitable arylenes are phenylene, naphthalene, biphenylene and benzylene. Suitable compounds C encompass dihydroxy substituted C 1 to C 8 alkylenes or C 1 to C 4 alkylene ethers such as diethylene glycol and triethylene glycol. Preferably triethylene glycol is used as compound C. If polymer A and polymer B is used instead of a polymer A', the function of compound C is such that it will react (crosslink) to a greater extent with compound A than with compound B. However, the degree to which compound C reacts with water soluble compound B is such that through this reaction compound B becomes water insoluble. Organic compound C is selected such that it does not react (crosslink) at a low temperature with either polymer A, polymer B or polymer A'. "Low" temperature in this context means that compound C does not react with either one of these polymers at or below room temperature (about 25°C). The term "not react" in this context means that it will not react to an extent which will yield effective crosslinking. Preferably compound C reacts with these compounds at or around the crystallisation temperature of the polymer of the base film, which is typically polyethyleneterephthalate (PET). This temperature therefore is in the range of 100°C to 300°C, preferably 150°C to 250°C, especially preferred 200°C to 230°C. If a combination of polymer A and polymer B is used, the presence of polymer B is critical because it significantly contributes to the adhesion towards the photographic layer. If Polymer A is used without Polymer B adhesion as well as antistatic properties are reduced to an extent which renders the primed film almost unusable for photographic purposes. In a most general sense Polymer A can be present in an amount ranging from 5 to 95 % by weight of the overall coating composition. More specific, Polymer A can represent from 35 to 70% by dry weight of the overall coating composition, preferably 45 to 60% by dry weight, and most preferably 55% by dry weight. In a most general sense Polymer B can be present in an amount ranging from 2.5 to 95 % by weight of the overall coating composition. More specific, Polymer B can represent from 10 to 40% by dry weight of the overall coating composition, preferably 20 to 25 %, and most preferably 22.5% by dry weight. In a most general sense Component C can be present in an amount ranging from 2.5 to 95 % by weight of the overall coating composition. More specific, Component C can represent from 10 to 50% by dry weight of the overall coating composition, preferably 20 to 35% by dry weight, and most preferably 22.5 % by dry weight. Further, it has been found that superior results are obtained if the ratio between component C and polymer B is within the range of 0.25 to 5, preferably 0.8 to 1.5, especially preferred is a ratio of 1.0. In addition, it might be useful to include additional components for specific purposes to the coating composition, provided such components do not materially interfere with the essential parts of the coating composition. Such additional components may include surfactants, especially anionic surfactants, e.g. sodium dodecylbenzene sulfonate (Rhodacal® LDS-10, Rhone-Poulenc, Cranbury, New Jersey) and nonionic surfactants, especially fluorosurfactants such as the combination of fluoroaliphatic oxyethylenes of carbon chain lengths from 4 to 8 and polyoxyethylene glycol (Fluorad® FC-170C, 3M, St. Paul Minnesota). The anionic surfactants may be present in a proportion of from 0.1 to 8% by dry weight (based on the total dry weight of the coating composition), and the nonionic surfactants may be present in a proportion of from 0.1 to 1.5% by dry weight (based on the total dry weight of the coating composition). All components of the coating composition are preferably uniformly blended with one another to produce the subbing coating composition. The subbing layer composition according to the present invention is applicable to any polyester base film which has photographic film uses as well as non-photographic film uses, such as reprographic film. Polyethylene terephthalate (PET) is the preferred polyester for the base film. The present invention may also utilize base films made of copolyesters, such as polyethylene terephthalate/isophthalate. Generally, however, any polyester film based on a polymer resulting from the polycondensation of a glycol or diol such as ethylene glycol, diethylene glycol, polyethylene glycol, neopentyl glycol, and polyols such as butanediol with a dicarboxylic acid (or its ester equivalents) such as terephthalic, isophthalic, sebacic, malonic, adipic, azelaic, glutaric, suberic, succinic acid, and the like, or mixtures of these, can be employed in the present invention. Any of the above polymeric films can contain conventional additives, such as antistatic additives, fillers such as silica, calcium carbonate, kaolin, titanium dioxide, pigments, delusterants, etc., all of which are well known in the art. Additionally, the polymeric film may comprise a polymeric laminate such as a polymer-polymer laminate like polyester-polyolefin, for example, or a polymer-metallic laminate such as polyester-aluminum, or a polymeric paper laminate, or the like. Any of these films may be produced by any well known techniques in the art. Depending on the method of application of the coating composition the solids levels within the liquid containing the coating composition can vary over a broad range. The subbing coating composition of the invention is typically applied to the base film as an aqueous solution at a solids concentration within the range of 2.0 to 13.5 % by weight, and preferably from 5 to 10% by weight. At a solids level below 2.0, it is believed that proper adhesion of the aqueous composition will be adversely effected because of incomplete surface coverage. Solids levels higher than the range given may be employed. However, as the solids level increases, coatability of the aqueous composition can become problematic due to an increase in viscosity. The preferred solids level, as it is applied to the polymeric substrate (base film), is preferably such that the final dry coating thickness of the dried subbing coating is from 1x10 -7 to 1x10 -4 cm with 5x10 -6 cm being the target thickness. The amount of coating on the final dried film is in the range of 0.005 to 0.2 g/m 2 , preferably 0.01 to 0.1 g/m 2 with 0.05 g/m 2 being the target amount. This subbing coating solution may be applied to the polymeric base film by any suitable known method. For example, roll coating, reverse roll coating, gravure roll coating, air knife coating, dipping, slot, slide curtain or meniscus coating may be employed. In-line coating is not mandatory, however, it gives the best results and is by far the most economic coating technique known today and is therefore preferred. "In-line coating" in this context refers to coating the surface of a film at various stages of the film making process. The subbing coating may be applied to one or both sides of the base film, depending on its final application. For example, in those situations where it is desirable to have adhesion to both sides of a polyester film for a photographic film usage, the film may be coated on each side with a layer of said subbing coating and then - optionally after a drying and curing process - overcoated with the necessary gelatinous layers, including the light-sensitive photographic gelatinous layer. Best adhesion towards a subsequently applied photographic layer is obtained when the polymeric base film is first coated with a primer layer and thereafter with the subbing coating composition according to the present invention. Many primer coating compositions may be employed in the present invention. A preferred primer is disclosed in U.S.-A-4,493,872. This primer composition comprises a water dispersible copolyester, preferably made from isophthalic acid and 5-sodium-sulfoisophthalic acid (and equimolar amounts of ethylene glycol). For best results it has been proven advantageous to add an anionic surfactant to the copolyester primer composition and a crosslinker such as melamin formaldehyde. Suitable anionic surfactants include sodium lauryl sulfate, sodium dodecylbenzene sulfonate, and sodium alkylarylpolyether sulfonate. The proportion of the anionic surfactant to the copolyester may be in a range from 1% to 15% by weight of the copolyester. The preferred range is 2 to 3% by weight. Another preferred copolyester primer composition is disclosed in U.S.-A-4,476,189. This primer composition comprises a water dispersible copolyester, preferably made from terephthalic acid and 5-sodium-sulfoisophthalic acid (and equimolar amounts of ethylene glycol). When employing this copolyester there is no need for an additional crosslinker. All components of the primer composition are uniformly blended with one another to produce the primer coating. Compared with known photographic films, which usually employ halide containing primers (e.g. vinylidene chloride), the copolyester primed and later subbed films according to the present invention provide much better reclaimability. Like the coating composition according to the present invention this primer coating is typically applied to the base film as an aqueous solution or dispersion. Solids concentration is usually within the range of 0.5 to 15% by weight, preferably from 5 to 10% by weight. The preferred solids level, as it is applied to the polymeric substrate, is such as to yield a final dry coating thickness within the range of from 0.005 g/m 2 to 0.2 g/m 2 . The preferred range is from 0.01 to 0.1 g/m 2 . The preferred thickness range of the dried primer coating is from 1x10 -7 to 1x10 -4 cm with 1x10 -6 cm being the target thickness. Like the coating composition according to the present invention this primer coating may be applied to the polymeric substrate by any suitable known method. For example, roll coating, reverse roll coating, gravure roll coating, air knife coating, dipping, slot, slide curtain or meniscus coating may be employed. The primer coating may be applied to one or both sides of the base film, depending on its final application. It is preferred to apply the primer coating in-line at any stage during the manufacturing process of the base film, however, before the subbing coating composition is applied. Such stages include pre-draw, after longitudinal stretch and after stretching in the transverse direction. For the present invention this first primer coating was provided in-line, in advance of the machine drawing stage, directly upon the cast sheet of polyester base film sheet, as that sheet is cooled upon extrusion. While it is an advantage of the coating composition according to the present invention that surface treatment such as corona treatment is not necessary, it may nevertheless be applied when deemed necessary. To produce a photographic film, the subbed film of the present invention must be overcoated with one or more gelatinous layers. Various gelatinous compositions for photographic film use are well known in the art and may consist of porkskin gelatin based composition, bone gelatin compositions, etc. Suitable photographic gelatinous compositions are typically made by the Croda Company, the Rousselot Company, the Kind & Knox Co., and many others. Coating the subbed film with the gelatin occurs generally after the film has been heat set. The gelatin composition can be applied by any of the methods described regarding the primer and subbing coating. The general process employed for the present invention comprises: if employed, in-line coating the polymeric base film with the primer coating, either before, during or after drawing the film; drying the primer coating composition to form a (first) primer coated film; in-line coating the polymeric base film, or the (first) primer coated film, with the subbing composition according to the present invention before, during, or after drawing the film, but preferably after drawing the film in the machine direction, and before heat setting; drying the subbing coating composition to form a (second) subbed film; and over-coating the (second) subbed film after heat setting with one or more gelatinous layers, including at least one light-sensitive photographic gelatinous layer. For example, a polyester film substrate can optionally be coated with a primer coating composition, then coated with a subbing composition, and overcoated with a light-sensitive photographic gelatinous layer. In the above example, the light-sensitive photographic layer is bonded directly to the subbing layer of the present invention. It is certainly possible, however, to have the light-sensitive photographic gelatinous layer bonded to an underlying gelatin layer through a gelatin-gelatin bonding mechanism, with such underlying gelatin layer bonded to the subbing layer of the present invention. The light-sensitive photographic layer is usually based on a Type B gelatin. Typically, the light-sensitive gelatin contains a light-sensitive composition based upon a silver halide. As discussed in Chapter 2, Section III, pages 79-80 of "The Theory of the Photographic Process", Fourth Edition, formaldehyde and glyoxal are commonly used hardeners (crosslinkers) for gelatin. In "Glyoxal", a product information bulletin published by Societe Francaise Hoechst, glyoxal is described on page 26 as an excellent hardener for gelatin and it is reported that glyoxal can be used in combination with formaldehyde to harden gelatin. The Photographic Test Coating used in the following examples is a solution of gelatin containing glyoxal and formaldehyde as hardeners. GENERAL TESTING CONDITIONS For determining the suitability of the subbed film of the present invention for photographic uses, three adhesion tests are performed. The first of these three tests is "dry adhesion" of unprocessed photographic layers. In this test, the samples of the subbed polyester film are coated with a Photographic Test Coating. The Photographic Test Coating is dried before further processing. The samples are then torn to expose a rough edge. A piece on No. 810 Scotch® tape is placed over the torn edge and pulled away sharply. If no removal of the Photographic Test Coating occurs, the sample is ranked Grade 1. If limited removal in small pieces occurs, the sample is rated Grade 2. If removal greater than or equal to the tape area occurs, the sample is ranked as a Grade 3. Only grade 1 is considered acceptable. The second important adhesion test is called the "wet adhesion" of processed photographic layers. Samples of the subbed film are subsequently over-coated with a Photographic Test Coating and are processed through the following sequences of photo processing chemicals, namely: 1) submerged in developer for 2.5 minutes; 2) rinsed with water for 30 seconds; 3) submerged in a fixer for 3 minutes; and, 4) rinsed with water for 3 minutes. The temperature of the water rinse in both steps 2 and 4 is ambient (ca 25°C ). The developer employed is Reprolith® 200, a commercially available developer produced by Anitec Image Corporation (Binghamton, New York). At the end of the four steps, the sample is scored with a scribing tool and a rubber stopper is rubbed across the sample several times, applying 2 kilogram weight of pressure. Samples are examined for degree of failure. No removal of test gelatin coating beyond the score line is Grade 1, very limited removal is Grade 2, and general loss of the gelatin coating is Grade 3. Only Grade 1 is considered acceptable. The third adhesion test is called the "processed dry adhesion" test. Samples of the subbed film are overcoated with a Photographic Test Coating and processed through the same four sequence steps as mentioned for "wet adhesion". After drying the film for 15 minutes at 40°C., adhesion is tested by taping a torn edge with a piece of No. 810 Scotch® tape as is described with respect to the "dry adhesion" test of unprocessed photographic layers. The same ratings apply for this test as with the "dry" and "wet adhesion" test mentioned previously. Only Grade 1 is considered acceptable. For the following Examples, the polymeric base film was produced with an unfilled polyethylene terephthalate resin made by the Hoechst Diafoil Corporation. None of the samples was corona treated prior to coating. The various coatings were applied either to the cast sheet (primer coating) or interdraw (subbing coating) as noted. Antistatic properties were derived from a measurement of the surface resistivity at a relative humidity of 50 % at 23°C and is given in Ω/square (ASTM D257). Surface resistivities below 10 12 Ω/square are considered acceptable. Antistatic properties were measured on the film according to example XXIX and determined to be 1.2 x 10 10 Ω/square. The film was then rinsed with deionized water (25°C) for 2 minutes and dried at 49°C for 15 minutes. Thereafter the surface resistivity was measured again and was determined to be 2.4 x 10 11 Ω/square. Such marginal drop in surface resistivity was unexpected and surprising and demonstrated that the subbing layer on the finished film was water insoluble. One skilled in the art would understand that the present invention does not depend upon the Photographic Test Coating composition. The Photographic Test Coating employed in all Examples was the same composition and was made of gelatin, using glyoxal and formaldehyd as hardeners. EXAMPLES Example 1 An amorphous, unfilled polyethyleneterephthalate (PET) film was formed, stretched 3.25 times in the machine direction, stretched to about 3.8 times the original width in the transverse direction, and heat set at a temperature between 190°C and 240°C. One coating station (Coating Station 1) was set up to coat the cast sheet prior to the first stretching step (machine draw, longitudinal draw), and another coating station (Coating Station 2 ) was set up to coat the longitudinally drawn sheet prior to the second stretching step (transverse stretching). Both coating stations coated the same side of the film with drying between each coating step. Aqueous primer and subbing coating compositions identified in Table 1 were applied to the polyester sheet as set out in Table 2. The subbed film was subsequently coated to a dry coating weight of approximately 5 g/m 2 with the Photographic Test Coating and dried with hot air at 49°C. Then the adhesion tests were carried out. The determination of surface resistivity was carried out on the subbed base film without applying the Photographic Test Coating. All percentage values given in Table 1 are weight percentages if not otherwise indicated. Thus, it is apparent that there has been provided, in accordance with the invention, a subbing composition, a subbed film, a subbed film coated with a gelatin composition, and a process for producing a photographic film that fully satisfies the object, aims, and advantages set forth above.

Claims: A subbing coating composition comprising: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or -PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the coating composition does not comprise addition polymerizable compounds. Coating composition according to claim 1, wherein polymer A is made from one or more monomers selected from the group consisting of acrylic acid, acryloxy propionic acid, methacrylic acid, ethacrylic acid, maleic acid, maleic acid anhydride, itaconic acid, itaconic acid anhydride, vinyl benzoic acid, succinic acid and sorbic acid. Coating composition according to claim 1, wherein polymer A is a copolymer made from: one or more monomers selected from the group consisting of acrylic acid, acryloxy propionic acid, methacrylic acid, ethacrylic acid, maleic acid, maleic acid anhydride, itaconic acid, itaconic acid anhydride, vinyl benzoic acid, succinic acid and sorbic acid, and one or more monomers selected from the group consisting of styrene, esters of acrylic acid or methacrylic acid, hydroxyalkyl acrylates and -methacrylates, vinyl esters and vinyl ethers. Coating composition according to claim 2, wherein polymer A is a copolymer made from maleic acid anhydride and methylvinyl ether. Coating composition according to claim 1, wherein X and Y are identical or different and represent Na, K or H. Coating composition according to claim 1, wherein polymer B is polystyrene sulfonic acid. Coating composition according to claim 1, wherein compound C is a dihydroxy substituted C 1 to C 8 alkylene or C 1 to C 4 alkylene ether. Coating composition according to claim 7, wherein compound C is diethylene glycol or triethylene glycol. Coating composition according to claim 8, wherein compound C is triethylene glycol. Coating composition according to claim 1, wherein compound C is selected such that it reacts with either polymer A or polymer B at a temperature in the range of 100 to 300°C. Coating composition according to claim 1, wherein polymer A represents from 35 to 70% by dry weight of the overall coating composition. Coating composition according to claim 1, wherein polymer B represents from 10 to 40% by dry weight of the overall coating composition. Coating composition according to claim 1, wherein compound C represents from 10 to 50% by dry weight of the overall coating composition. Coating composition according to claim 1, wherein the coating composition further comprises surfactants. Coating composition according to claim 14, wherein the surfactants are anionic and/or nonionic. Coating composition according to claim 15, wherein the anionic surfactant is sodiumdodecylbenzene sulfonate and wherein the nonionic surfactant is a combination of fluoro-C 4 -C 8 -alkyl oxyethylenes and polyoxyethylene glycol. Polyester base film, having on at least one surface thereof a subbing coating which subbing coating comprises: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or -PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having-attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. Polyester base film having on at least one surface thereof a primer coating and on that at least one primer coating at least one subbing coating which subbing coating comprises: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or -PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. Polyester base film according to claim 17 or 18, wherein the polyester is polyethyleneterephthalate (PET). Polyester base film according to claim 17 or 18, wherein the subbing coating has a thickness of 1x10 -7 to 1x10 -4 cm. Polyester base film according to claim 17 or 18, wherein the primer coating is a coating based on a water dispersible copolyester. Polyester base film according to claim 21, wherein the copolyester is made from isophthalic acid and 5-sodium-sulfoisophthalic acid. Polyester base film according to claim 22, wherein the copolyester further comprises an anionic surfactant. Polyester base film according to claim 17 or 18, wherein the primer coating has a thickness of 1x10 -7 to 1x10 -4 cm. Polyester base film according to claim 17 or 18, wherein A' is a copolymer made from maleic acid anhydride and styrene sulfonic acid. Photographic film comprising a polyester base film, having on at least one surface thereof a subbing coating and on that at least one subbing coating at least one coating comprising a light sensitive material, wherein the subbing coating comprises: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or -PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. Photographic film, comprising a polyester base film having on at least one surface thereof a primer coating and on that at least one primer coating at least one subbing coating and on that at least one subbing coating at least one coating comprising a light sensitive material, wherein the subbing coating comprises: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or -PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. A process for applying a liquid subbing coating to a polymeric film in a process for manufacturing biaxially oriented polymeric films, comprising bringing a primer coating in-line directly upon a cast sheet of polymeric base film as that sheet is cooled upon extrusion in advance of a first drawing stage and after the first drawing stage, coating the primer coated film with said subbing coating, with said subbing coating comprising: I a polymer A having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis and a polymer B having attached to its backbone -SO 3 X and/or -PO 3 XY groups wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen or II a polymer A' having attached to its backbone carboxyl groups and/or groups which form carboxyl groups upon hydrolysis, and -SO 3 X and/or -PO 3 XY groups, wherein X and Y are identical or different and denote an alkali metal, ammonium, organic quaternary ammonium or hydrogen and III an organic compound C having at least two free hydroxy groups, wherein the subbing coating does not comprise addition polymerizable compounds. The process according to claim 28, wherein the polymeric base film is a polyester film.

Inventors: DONALD ROBIN M, HEBERGER JOHN M, KREJCI JAMES J, MOORE CATHY R, DONALD, ROBIN M., HEBERGER, JOHN M., KREJCI, JAMES J., MOORE, CATHY R.
Applicants: MITSUBISHI POLYESTER FILM LLC, MITSUBISHI POLYESTER FILM, LLC
Application year: 1994
Main classification: C09D157
IPC codes: C08L35, C08L25, C09D133, C08L31, C08J7, C09D129, C09D5, C09D135, C09D201, C09D125, G03C1, C08L29