Method for forming an object of thermosetting synthetic material in a mould

Abstract: Method for forming an object (2) of thermosetting synthetic material in a mould (6), having at least one chamber (9), according to which method a mixture of components, which react and cure above a critical temperature, is put in liquid form in the chamber (9) through an inlet piece (1), which is provided with at least one filling duct (3,5) which opens into the chamber (9); whereby said mixture is allowed to react and cure by making sure that the temperature of the mould (6) is higher than said critical temperature; after which the object (2) with the inlet piece (1) is removed from the mould (6), characterized in that the liquid mixture is inserted in the mould (6) through the inlet piece (1) which sticks through a wall (8) in the mould (6) and which extends outside the mould (6), by means of a casting nozzle (14) which is kept at a temperature which is lower than said critical temperature, whereby the extremity of the casting nozzle fits liquid-tight on the filling opening (4) of the above-mentioned inlet piece (1), and one makes sure that, at least during the filling of the mould (6), the inlet piece (1) has a lower temperature than the above-mentioned critical temperature, such that the curing first takes place against the inner wall of the mould (6) and finally against the inlet piece (1), and during the curing in the mould (6) a pressure is exerted on the curing synthetic via said casting nozzle (14).

Description: The invention concerns a method for forming an object of thermosetting synthetic material in a mould, having at least one chamber, according to which method a mixture of components, which react and cure above a critical temperature, is put in liquid form in the chamber by means of a casting nozzle through an inlet piece, which is provided with at least one filling duct which opens into the chamber, and which has a filling opening on which the casting nozzle fits liquid-tight during the injection of said mixture, whereby said mixture is allowed to react and cure by making sure that the temperature of the mould is higher than said temperature, after which the object with the inlet piece is removed from the mould. Such a method is known from patent EP-A-492 477. The inlet piece is a hollow shaft which is entirely situated inside the mould, and the mould is filled by means of a nozzle which is inserted in a duct which opens into the mould on said hollow shaft. The synthetic and the shape must be specially selected so as to avoid shrinking problems. Moreover, only an example is given with thermoplastic. It is mentioned, however, that also thermosetting synthetic can be used, but how one should proceed in this case is not described. How the above-mentioned nozzle, which must be cooled off to prevent it from being stopped up, can be cooled while it is inserted in a duct in the heated mould is not explained. According to the described method, especially when thermosetting synthetic is used, no great accuracy can be obtained for the objects made. The invention aims to remedy the above-mentioned disadvantages and to provide a method for forming an object of thermosetting synthetic in a mould according to which also very precise mechanical parts can be made which require no further processing, for example a roll body with a very precise geometry provided with a shaft or another internal piece, which is preferably functional in the final product. To this aim an inlet piece is used which traverses a wall of the mould and which extends outside the mould, whereby the casting nozzle is maintained at a temperature which is lower than said critical temperature, and one makes sure that, at least during the filling of the mould, the inlet piece has a lower temperature than the above-mentioned critical temperature, such that the curing first takes place against the inner wall of the mould and finally against the inlet piece, and during the curing in the mould a pressure is exerted on the curing synthetic via said casting nozzle. As the synthetic starts to cure at the mould wall which has a temperature higher than the critical temperature, and the curing subsequently continues towards places situated further away from said wall, it is possible to manufacture an object of synthetic material with great precision by selecting the right position for the filling duct. Shrinkage which may lead to dimensional variation is compensated during the polymerization process and the curing, until the end of the rubber phase, by exerting an after-pressure on the liquid synthetic. Said after-pressure is brought about by means of the filling duct, and is preserved until the dimension-sensitive parts have cured. Shrinkage of the synthetic which was last injected may occur in the filling duct. Faults in the synthetic in this inlet piece are of no importance and do not require any final processing. Practically, an absolute pressure is exerted situated for example between 0.5 and 10 bar. In order to better explain the characteristics of the invention, the following preferred embodiments of a method for forming an object of thermosetting synthetic in a mould and of an object made in this manner are described according to the invention by way of example only and without being limitative in any way, with reference to the accompanying drawings, where: figure 1 is a longitudinal section of an object made according to the method of the invention; figure 2 shows a section of the mould for manufacturing the object from figure 1, during the filling; figure 3 shows a section of the mould analogous to that in figure 1, but with the mould in open position, as the formed object is being removed; figure 4 shows a part of a section analogous to that in figure 3, but with relation to another embodiment of the object and method according to the invention. The object represented in figure 1 consists of an inlet piece which is formed in particular of a steel shaft 1, which is surrounded over part of its length by a part, namely a cylinder 2, of thermosetting synthetic to which the usual additives and fillers such as glass fibres were added. The shaft is provided with an axial duct 3 which opens into an extremity of the shaft by means of a funnel-shaped filling opening 4 on the one hand, and which is connected to one or several radially directed ducts 5 which open into the cylinder 2 on the other hand. Suitable thermosetting synthetics are for example polyurethanes resulting from the reaction of one or several isocyanates with a polyol. The object from figure 1 is manufactured by putting a thermosetting mixture made up of components which react and cure above a critical temperature and possibly also additives and/or fillers in a closed, heated mould 6. As represented in the figures 2 and 3, said mould 6 consists of a tub-shaped body 7 and a removable lid 8 which closes off said body 7 in its closed position. Inside the mould 6 is thus created a central round chamber 9 which corresponds to a part of the object to be formed, namely the cylinder of synthetic material 2 and the part of the steel shaft 1 which is situated in the cylinder 2 and protrudes outside said cylinder 2 at the extremity which is turned away from the filling opening 4. The wall of the mould 6 and in particular the lid 8 is provided with a central opening 10 through which the extremity of the shaft 1 which protrudes outside the cylinder 2, the side with the funnel-shaped filling opening, sticks. An axially directed duct 11 extends through the bottom of the body 7 in which an ejector bar 12 is mounted in a slidable manner. Said ejector bar 12 ends in tub-shaped part in which an extremity of the shaft 1 fits. In the non-extended position of the ejector bar 12, said tub-shaped part forms a part of the wall of the above-mentioned chamber 9. Ducts 13 for heating or cooling liquid extend both through the body 7 and through the lid 8, as a result of which the temperature of the mould 6 can be adjusted. Before the mixture of synthetic components is inserted, the metal shaft 1 is applied such in the mould 6 that, after the lid 8 has been applied, when the mould is closed, the extremity with the filling opening 4 is situated outside the mould. Naturally, the ejector bar 12 is hereby maximally slid back, as represented in figure 2. Its tub-shaped extremity receives the other extremity of the shaft 1. Moreover, the shaft 1 is fixed to the ejector bar 12 by means of a pen 16 which is placed axially in the tub-shaped extremity and which is screwed in an extremity of the shaft 1. By means of liquid which is pumped through the ducts 13 or by means of any other heating systems, the mould 6 is maintained at a temperature which is higher than the critical temperature at which the synthetic components start to react and thus at which the curing starts. For an isocyanate moulding resin, for example, said temperature of the mould 6 amounts to 130 degrees Celsius. The shaft 1 itself is not or only little heated, such that it has a temperature which is significantly lower than the above-mentioned critical temperature. The synthetic components are inserted in the closed mould 6 via the duct 3 and the radial ducts 5 in the shaft 1, by means of a cooled casting nozzle 14 which is provided with a duct 15. Said casting nozzle 14 has an extremity which has the complementary shape of the filling opening 4, such that said casting nozzle 14 fits perfectly on this filling opening, as represented in figure 2. The casting nozzle 14 is connected to a mixer, which is not represented in the figures 2 and 3 for clarity's sake, in which the components of the thermosetting synthetic are mixed, possibly together with the usual additives such as for example a catalyst, and the usual fillers, such as for example glass fibres. The casting nozzle 14 may be cooled off for example by blowing air over the nozzle or by pumping cooling liquid around the casting nozzle. In any case, the casting nozzle 14 has a temperature which is significantly lower than the above-mentioned critical temperature, such that the reaction between the components cannot take place in the duct 15, and the casting nozzle 14 does not become stopped up by curing synthetic. This casting nozzle 14 only makes contact with the shaft 1 which, as already mentioned, also has a temperature which is lower than the above-mentioned critical temperature. The components are inserted at an absolute pressure between 0.5 and 10 bar, which pressure is maintained as long as the casting nozzle 14 is connected to the shaft 1, which is both during the filling of the mould 1 and during the curing of the injected synthetic around the shaft 1. The filling may take about one to two minutes, the curing some ten to twenty minutes, depending among others on the amount of resin, the type of catalyst, the fillers, the geometry of the object, the temperature, etc. The mixture of components which is inserted is at room temperature or is slightly heated, but in any case at a temperature which is significantly lower than the above-mentioned critical temperature. Once inserted, the warm mould wall makes the temperature of said mixture rise and, when the temperature of the mixture against the wall of the mould has reached the critical temperature, the reaction of the components starts, whereby the polymerization of the thermosetting synthetic goes first through a gel and a rubber-like phase to finally become a complete, three-dimensional network of cured resin. The warmth spreads from the heated wall, and thus the reaction is continued towards the centre. As soon as the reaction has reached the shaft 1 and the components in the ducts 5 or 3 begin to cure, the filling is stopped and the casting nozzle 14 is removed from the shaft 1. The last inserted amount of mixture can now cure and after-shrink freely and pressureless in the duct 3 in the shaft 1. Residual shrinkage which appears around the filling holes of the ducts 5 can be absorbed by the content of said duct 3, and has no further influence on the accuracy of the cylinder 2 and thus of the entire object which is manufactured. Finally, the lid 8 is removed and, by means of the ejector bar 12, the formed object 1,2 is pushed out of the body 7. The pressure during the insertion and curing of the composite is not high. Working at a low pressure is favourable when manufacturing precision products, as there is no deformation of the mould, and, moreover, the thermosetting synthetic remains perfectly pressed against the wall in the rubber phase, which immediately precedes the definite curing, whereby the shrinking effect is compensated. The thus obtained high accuracy is about 0.02 mm, and no further processing of the synthetic is required. Also other shapes than a cylinder 2 can be made in the above-described manner around a metal shaft 1. Thus, the synthetic part may be a screw as represented in figure 4. After the curing this cured synthetic part 2 is screwed out of the body 7 by means of the ejector bar 12 which is rotated with the help of means which are not represented in the figures during the pushing out. Said bar takes along the shaft 1 with the screw 2 by means of the pin 16 which is situated in the middle of the tub-shaped extremity of the bar 12 and which is screwed in an opening at the extremity of the shaft 1 during the insertion of the shaft 1 in the open mould 6. The above-described method makes it possible to manufacture products consisting of a shaft surrounded by a synthetic part with much precision and without any final processing being required. The cured synthetic sticks very well to the metal shaft 1. The present invention is by no means limited to the embodiments described above and represented in the figures; on the contrary, such a method for forming an object of thermosetting synthetic in a mould and the thus manufactured object can be made according to various variants while still remaining within the scope of the appended claims. In particular, the critical temperature should not necessarily be 130 degrees Celsius. This temperature depends on the composition of the mixture used and thus among others of the reacting components, the catalyst, the fillers, etc. Also the shape of the synthetic part must not necessarily be a cylinder or a screw. Other shapes are possible, even shapes which are not round. Neither should the shaft be necessarily situated centrally in this synthetic part. Nor should the shaft necessarily protrude on two sides of the synthetic. Nor should it necessarily be made of metal. It may for example be made of the same synthetic as the synthetic which is inserted in the mould. The inlet piece should not even necessarily be a shaft. It may have another shape.

Claims: Method for forming an object (2) of thermosetting synthetic material in a mould (6), having at least one chamber (9), according to which method a mixture of components, which react and cure above a critical temperature, is put in liquid form in the chamber (9) by means of a casting nozzle (14) through an inlet piece (1), which is provided with at least one filling duct (3,5) which opens into the chamber (9) and which has a filling opening (4) on which the casting nozzle (14) fits liquid-tight during the injection of said mixture; whereby said mixture is allowed to react and cure by making sure that the temperature of the mould (6) is higher than said critical temperature; after which the object (2) with the inlet piece (1) is removed from the mould (6), characterized in that an inlet piece (1) is used which traverses a wall (8) of the mould (6) and which extends outside the mould (6), whereby the casting nozzle (14) is kept at a temperature which is lower than said critical temperature, and one makes sure that, at least during the filling of the mould (6), the inlet piece (1) has a lower temperature than the above-mentioned critical temperature, such that the curing first takes place against the inner wall of the mould (6) and finally against the inlet piece (1), and during the curing in the mould (6) a pressure is exerted on the curing synthetic via said casting nozzle (14). Method according to the above claim, characterized in that an absolute pressure is exerted situated between 0.5 and 10 bar. Method according to any of the above claims, characterized in that the inlet piece (1) is applied centrally in the mould (6). Method according to any of the above claims, characterized in that an inlet piece (1) is used whose duct (3,5) contains a part (3) fitting on the filling opening (4) which extends according to the axis of symmetry of the inlet piece (1). Method according to any of the above claims, characterized in that a shaft is used as an inlet piece (1) around which the synthetic (2) is applied in the mould (6). Method according to any of the above claims, characterized in that the insertion of synthetic material is stopped when the curing has reached the inlet piece (1).

Inventors: DEN UIJL HENDRIK, GORIS JOOST, PEETERS GUIDO, DEN UIJL, HENDRIK, GORIS, JOOST, PEETERS, GUIDO
Applicants: ATLAS COPCO AIRPOWER NV, TPP AXXICON BV, ATLAS COPCO AIRPOWER N.V., TPP AXXICON B.V.
Application year: 1994
Main classification: B29C45
IPC codes: B29C45, B29C70, B29K105, B29K101, B01D53