Curable resin compositions

Abstract: A vinyl copolymer is provided comprising a silanol group - containing (meth)acryl siloxane unit of formula (1): wherein R¹ is hydrogen or methyl, R², R³, and R⁴ are independently a monovalent C₁-C₈ hydrocarbon group or a siloxy group, R⁵ is a monovalent C₁- C₈ hydrocarbon group, n = 1 to 12, and a = 0 or 1. The vinyl copolymer is prepared by copolymerizing a polymerizable vinyl monomer with a silanol group-containing (meth)acryl siloxane in the presence of a radical initiator or by emulsion polymerizing a polymerizable vinyl monomer with a silanol group-containing (meth)acryl siloxane in an aqueous medium in the presence of a surfactant and a polymerization initiator. The copolymer is blended with a condensation catalyst to form a room temperature curable resin composition which crosslinks in the presence of moisture into a cured coating having weatherability, flexibility, and adherence.

Description: This specification relates to vinyl copolymers having a silanol group in a side chain, and preferably to silanol group-containing vinyl copolymers which offer a room temperature curable resin composition e.g. of one-pack type, which crosslink in the presence of moisture into a cured coating, desirably having weatherability, flexibility, and adherence and thus suitable as a coating agent. It also relates to methods for preparing such copolymers and room-temperature-curable resin compositions containing such copolymers. Prior Art In the prior art, acrylic urethane resins, acrylic silicone resins, and fluorinated resins are known as useful resins for paint, especially in room temperature curable coating compositions having weatherability. Among these resins, acrylic urethane resins are less expensive, but are made using isocyanates which are harmful to the human body. Fluorinated resins have weatherability, but are expensive. In contrast, acrylic silicone resins are in increasing demand because of a good compromise between performance and cost. Acrylic silicone resins have an alkoxysilyl group attached to an acrylic backbone. They can form stable cured coatings when applied to substrates because alkoxysilyl groups react with moisture in air at room temperature to produce siloxane bonds. See Coating and Paint, No. 429, pages 55-64. An alkoxysilyl group can be introduced into an acrylic backbone, for example, by copolymerizing a polymerizable vinyl group-containing silane compound in the presence of a radical initiator as disclosed in Japanese Patent Application Kokai (JP-A) No. 36109/1982. However, the conventional acrylic silicone resins fail to impart as much weatherability as fluorinated resins and are not flexible enough to meet a wide variety of applications. There is a need for an acrylic silicone resin having these properties. Most acrylic silicone resins and compositions thereof are prepared with organic solvent, contrary to the current trend towards non-pollution and resource saving. Known methods for carrying out copolymerization in aqueous media without using organic solvents include emulsion polymerization and suspension polymerization. With these methods, however, desired hydrolysable groups such as alkoxysilyl groups, react with water and crosslink during copolymerization or storage, leading to inconvenient thickening and gelation. A general aim herein is to provide new and useful room-temperature curable resin compositions of an acrylic-silicone type, methods of making the compositions and their use in coating. Preferred aims include improved weatherability and flexibility of such coatings. A first aspect of the invention is a room-temperature curable resin composition comprising: (a) vinyl copolymer comprising, in combination with units of copolymerised vinyl monomer, silanol group-containing (meth)acryl siloxane unit(s) of the following general formula (1) : wherein R 1 is hydrogen or methyl group, R 2 , R 3 , and R 4 are independently selected from substituted and unsubstituted monovalent hydrocarbon groups having 1 to 8 carbon atoms and siloxy groups of the formula - OSiR 6 R 7 R 8 wherein R 6 , R 7 and R 8 are independently selected from organic groups having 1 to 8 carbon atoms, R 5 is substituted or unsubstituted monovalent hydrocarbon group having 1 to 8 carbon atoms, n is an integer of 1 to 12 and a is 0 or 1; (b) condensation catalyst, and (c) crosslinking agent. Other aspects are methods of preparing the compositions in which the vinyl copolymer is prepared from silanol-containing (meth)acryl siloxane of formula (2), either using a radical initiator (see claim 18) or as an emulsion using a polymerisation initiator and surfactant (see claim 19). Further aspects are a product obtained by curing such a composition (claim 23), the use of such a composition for coating (claim 24) and coated articles obtained thereby (claim 23). We note that vinyl copolymers satisfying the above definitions are known as such, from EP-A-184924, EP-A-242080 and US-A-4419505. However these copolymers are preferably prepared by bulk polymerisation for use in optical lenses. As compared with conventional acrylic silicone polymers, we find that these vinyl copolymers are effective for imparting weatherability, presumably because a bulky substituent (siloxane) is positioned in the proximity of a crosslinking point in the unit of formula (1) to exert steric hindrance with which a crosslinking portion is protected. Also, these vinyl copolymers may have a higher content of siloxane bond than the conventional ones. Combination of the vinyl copolymer obtained by emulsion polymerization with a crosslinking agent is effective for imparting flexibility, because the bond distance of a crosslinking portion is longer by the length of the crosslinking agent and siloxane groups are localized from a structural aspect. As compared with conventional acrylic silicone copolymer compositions, this composition can be improved not only in weatherability and flexibility, but also in adhesion because the crosslinking agent also serves as a coupling agent between the cured coating and a substrate. The vinyl copolymer comprising a silanol group-containing (meth)acryl siloxane unit of formula (1) may be prepared by copolymerizing a polymerizable vinyl monomer with a silanol group-containing (meth)acryl siloxane of formula (2) in the presence of a radical initiator or emulsion polymerizing a polymerizable vinyl monomer with a silanol group-containing (meth)acryl siloxane of formula (2) in an aqueous medium in the presence of a surfactant and a polymerization initiator. DETAILED DESCRIPTION The present disclosure uses a vinyl copolymer having a silanol group in a side chain. More particularly, the vinyl copolymer is preparable by copolymerizing a polymerizable vinyl monomer with a silanol group-containing (meth)acryl siloxane of formula (2). Then the vinyl copolymer has a backbone consisting essentially of units derived from a polymerizable vinyl monomer and a side chain suspending therefrom, the side chain being a suspending portion of a unit of formula (1). Units of formula (1) may be random or block copolymerized with units of vinyl monomer. A vinyl polymer is thus representable as follows. In the formula, A and B are polymerized units of vinyl monomer, and ℓ is a positive number. A and B are identical or different, and polymerized units of one vinyl monomer or two or more vinyl monomers respectively. One reactant is a polymerisable vinyl monomer whose nature is not critical. It can easily be selected to form a thermoplastic polymer or rubbery elastomer. Examples of the monomer include (meth)acrylates such as methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, and 2-ethylhexyl (meth)acrylate; styrenes such as styrene, o-methylstyrene, p-methylstyrene, and α-methylstyrene; olefins such as ethylene and propylene; vinyl chloride and vinylidene chloride; fatty acid vinyls such as vinyl acetate; alkyl vinyl ethers such as methyl vinyl ether and ethyl vinyl ether; alkyl vinyl ketones such as methyl vinyl ketone and ethyl vinyl ketone; difficultly hydrolyzable silicon-containing polymerizable monomers such as vinyltrimethylsilane, 3-(meth)acryloxypropyltrimethylsilane, p-trimethylsilylstyrene, vinyltrimethoxysilane, 3-(meth)acryloxypropyltrimethoxysilane, p-trimethoxysilylstyrene, vinyl tris(trimethylsiloxy)silane, 3(meth)acryloxypropyltris(trimethylsiloxy)silane, and p-tris(trimethylsiloxy)silylstyrene; and fluorinated polymerizable monomers such as 3,3,3-trifluoropropyl (meth)acrylate and 3,3,3-trifluoro-2-trifluoromethylethyl (meth)acrylate, alone or in admixture of two or more. Preferred monomers are methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, styrene, and vinyl acetate. Where a polymerizable vinyl monomer is used as a comonomer, it is generally known that the use of a polymerizable vinyl monomer having a polar group in combination with the polymerizable vinyl monomer is effective for improving the adherence of a coating when the resultant vinyl copolymer is applied as a coating resin. Examples of the polymerizable vinyl monomer having a polar group include unsaturated organic acids and anhydrides thereof such as (meth)acrylic acid, maleic acid, itaconic acid, citraconic acid, maleic anhydride, and itaconic anhydride; hydroxyl-containing compounds such as 2-hydroxyethyl (meth)acrylate and 2-hydroxypropyl (meth)acrylate; epoxy-containing compounds such as glycidyl (meth)acrylate and 2-(3,4-epoxycyclohexyl)ethyl (meth)acrylate; amino-containing compounds such as 2-(diethylamino)ethyl (meth)acrylate and 2-aminoethyl vinyl ether, N-vinyl-2-pyrrolidone, (meth)acrylamide, and acrylonitrile, alone or in admixture of two or more. The amount of a compound having a polar group should preferably be limited to 0 to 20%, especially 0 to 10% by weight of the entire polymerizable vinyl monomers because it tends to take in moisture (water) from air to exacerbate storage stability. One reactant is a silanol group-containing (meth)acryl siloxane of the following general formula (2). A silanol group-containing (meth)acryl siloxane unit derived from this siloxane is of the following general formula (1). In formulae (1) and (2), R 1 is a hydrogen atom or methyl group, R 2 , R 3 , and R 4 are independently selected from substituted and unsubstituted monovalent hydrocarbon groups having 1 to 8 carbon atoms and siloxy groups of the formula: -OSiR 6 R 7 R 8 wherein R 6 , R 7 , and R 8 are independently selected from organic groups having 1 to 8 carbon atoms, R 5 is a substituted or unsubstituted monovalent hydrocarbon group having 1 to 8 carbon atoms, n is an integer of 1 to 12, and a is equal to 0 or 1. Examples of the substituted or unsubstituted hydrocarbon group having 1 to 8 carbon atoms represented by R 2 to R 5 as well as R 6 to R 8 include alkyl groups such as methyl, ethyl, propyl and butyl; cycloalkyl groups such as cyclopentyl and cyclohexyl; aryl groups such as phenyl; aralkyl groups such as benzyl; alkenyl groups such as vinyl and allyl; and substituted ones of these with non-interfering substituents as easily identifiable from the skilled person's general knowledge, e.g. halo or cyano, giving typical substituted groups such as chloromethyl, 3,3,3-trifluoropropyl and 2-cyanoethyl groups. Examples of the siloxy group of -OSiR 6 R 7 R 8 include trimethylsiloxy, ethyldimethylsiloxy, phenyldimethylsiloxy, vinyldimethylsiloxy, chloromethyldimethylsiloxy, 3,3,3-trifluoropropyldimethylsiloxy, and 2-cyanoethyldimethylsiloxy groups. R 2 to R 8 may be either identical or different although it is most preferred from the standpoints of availability of reactants, ease of synthesis and properties of a copolymer that all or nearly all of R 2 to R 8 are methyl. The silanol group-containing (meth)acryl siloxane of formula (2) can be prepared by effecting dehydrohalogenation reaction between organohalosilanes and silanols followed by hydrolysis reaction as disclosed in Japanese Patent Application No. 226438/1993. For achieving the preferred aims herein, those siloxanes of formula (2) wherein n = 3 are preferred, as are those in which a=0. The vinyl copolymer contains units of formula (1), preferably in an amount of 1 to 50%, especially 5 to 20% by weight from the standpoints of hardness and flexibility. Also preferably the vinyl copolymer has a weight average molecular weight of about 5,000 to 1,000,000. According to the methods proposed herein, the vinyl copolymer is prepared by copolymerizing a polymerizable vinyl monomer with a silanol-containing (meth)acryl siloxane of formula (2) in the presence of a radical initiator (Method I) or by emulsion polymerizing a polymerizable vinyl monomer with a silanol-containing (meth)acryl siloxane of formula (2) in an aqueous medium in the presence of a surfactant and a polymerization initiator (Method II). In method I, any e.g. conventional radical initiators may be used. Exemplary radical initiators include azobis compounds such as 2,2'-azobis(isobutyronitrile), 2,2'-azobis(2-methylbutyronitrile), methylbutyronitrile), and 2,2'-azobis(2,4 and organic peroxides such as benzoyl peroxide, lauroyl peroxide, tert-butylperoxybenzoate, and tert-butylperoxy-2-ethylhexanoate, alone or in admixture of two or more. Preferably the radical initiator is used in an amount of about 0.1 to 5 parts by weight per 100 parts by weight of the total of the polymerizable vinyl monomer and silanol-containing (meth)acryl siloxane. More particularly, copolymerization is carried out by solution polymerization or bulk polymerization. Solution polymerization is to heat a solution of a polymerizable vinyl monomer and a silanol-containing (meth)acryl siloxane in a solvent in the presence of a radical initiator at about 50 to 150°C for about 3 to 20 hours for reaction. Since bulk polymerization is a solventless polymerization process, the resulting copolymers are often unacceptable with respect to viscosity and residual monomer. Then the solution polymerization process using a solvent is recommended. Examples of the solvent used in the solution polymerization include aliphatic hydrocarbons such as hexane, octane, decane, and cyclohexane; aromatic hydrocarbons such as benzene, toluene, and xylene; ethers such as diethyl ether, dibutyl ether, tetrahydrofuran, and dioxane; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, and cyclohexane; and esters such as methyl acetate, ethyl acetate, butyl acetate, and isobutyl acetate. It is preferred to use toluene and/or xylene among others. In synthesizing the vinyl copolymer a chain transfer agent may be further added. Exemplary are mercapto compounds such as 2-mercaptoethanol, butylmercaptan, n-dodecylmercaptan, and 3-mercaptopropyltrimethoxysilane; and halides such as methylene chloride, chloroform, carbon tetrachloride, butyl bromide, and 3-chloropropyltrimethoxysilane. It is preferably used in an amount of about 0.01 to 10 parts by weight per 100 parts by weight of the total of the polymerizable vinyl monomer and siloxane of formula (2). Method II uses a surfactant which serves as an emulsifying agent for emulsifying and dispersing a polymerizable vinyl monomer and a silanol-containing (meth)acryl siloxane of formula (2) in an aqueous medium. Typical surfactants are anionic surfactants including alkali metal salts of sulfonic acid such as sodium dodecylbenzenesulfonate, sodium laurylnaphthalenesulfonate, and sodium stearyldiphenyl ether disulfonate; and alkali metal salts of sulfates such as sodium laurylsulfate, sodium polyoxyethylene lauryl ether sulfate, and sodium polyoxyethylene octyl phenyl ether sulfate though not limited thereto. The surfactant used may be an anionic surfactant alone although the use of an anionic surfactant in combination with a nonionic surfactant is effective for further improving the stability of an aqueous emulsion during polymerization and storage. Examples of such nonionic surfactant include polyoxyethylene nonyl phenyl ether, polyoxyethylene octyl phenyl ether, polyoxyethylene distearate, and polyoxyethylene cetyl ether. The nonionic surfactant should preferably have a HLB value of at least 10 because some surfactants with a HLB value of less than 10 would not allow for smooth progress of emulsion polymerization. Preferred is a mixture of an anionic surfactant and a nonionic surfactant in a weight ratio of from 1/9 to 4/6. Preferably the surfactant is used in an amount of about 0.1 to 10 parts by weight per 100 parts by weight of the total of the polymerizable vinyl monomer and siloxane of formula (2). Any e.g. conventional polymerization initiator may be used as long as it undergoes cleavage to generate a radical. Exemplary are azobis compounds such as 2,2'-azobis-(isobutyronitrile), 2,2'-azobis(2-methylbutyronitrile), 2,2'-azobis(2,4-dimethylvaleronitrile), and 2,2'-azobis(2-amidinopropane) dihydrochloride; organic peroxides such as benzoyl peroxide, lauroyl peroxide, tert-butylperoxybenzoate, tert-butylperoxy-2-ethylhexanoate, tert-butylhydroperoxide, succinic peroxide, and maleic mono-tert-butyl peroxide; persulfates such as ammonium persulfate and potassium persulfate; redox systems such as aqueous hydrogen peroxide/ferric chloride and aqueous hydrogen peroxide/L-ascorbic acids. In general, emulsion polymerization uses water-soluble polymerization initiators while the present proposal favors the same. Since the peroxides generate oxygen radicals which tend to withdraw hydrogen atoms to form undesirable crosslinkages during polymerization and thus require careful handling, the azobis compounds are preferred. Most preferred is 2,2'-azobis(2-amidinopropane) dihydrochloride. Preferably the polymerization initiator is used in an amount of about 0.1 to 10 parts by weight per 100 parts by weight of the total of the polymerizable vinyl monomer and siloxane of formula (2). In method II, the silanol-containing vinyl copolymer is synthesized by emulsion polymerization of the above-mentioned reactants in an aqueous medium. The medium is water alone, typically deionized water while any water-soluble organic solvent may be additionally used if desired for reactant solubility and emulsion stability. Organic solvents which can be used along with water include methanol, ethanol, isopropanol, acetone, methyl ethyl ketone, acetonitrile, and tetrahydrofuran. However, the water-soluble organic solvent should preferably be used in a minimal amount and limited to at most 50%, especially at most 20% by weight of the aqueous medium. In synthesizing the vinyl copolymer according to Method II, a chain transfer agent may be further added for adjustment of a degree of polymerization. Exemplary are mercapto compounds such as 2-mercaptoethanol, butylmercaptan, and n-dodecylmercaptan; and halides such as methylene chloride, chloroform, carbon tetrachloride, and butyl bromide. It is preferably used in an amount of about 0.01 to 10 parts by weight per 100 parts by weight of the total of the polymerizable vinyl monomer and siloxane of formula (2). Emulsion polymerization may be carried out by any of well-known methods, for example, by dispersing predetermined amounts of a polymerizable vinyl monomer, silanol group-containing (meth)acryl siloxane, surfactant, polymerization initiator and optional chain transfer agent in an aqueous medium in a reactor, and heating the reactor. Alternatively, emulsion polymerization is carried out by dissolving a surfactant in an aqueous medium heating the solution, and adding dropwise the remaining components to the solution. Usually reaction is carried out at a temperature of 50 to 150°C for about 3 to 20 hours. Polymerization can take place at room temperature to 50°C when a redox polymerization initiator is used. Each of the components may be a single compound or a mixture of two or more compounds. The respective components can be dispersed in an aqueous medium by means of a homo-mixer or homogenizer or by ultrasonic agitation, thereby achieving a micelle size. This results in resin particles having a reduced particle size at the end of polymerization. As a result of these methods, there is obtained a silanol group-containing vinyl copolymer having a varying molecular weight (Mw), molecular weight dispersity (Mw/Mn), and glass transition temperature (Tg) complying with a particular application. For example, the molecular weight and molecular weight dispersity can be controlled by suitably selecting the type and amount of a radical initiator, solvent and chain transfer agent. Any desired glass transition temperature can be obtained by changing the type of polymerizable vinyl monomer(s). In this regard, note that a copolymer obtained by radical polymerization and a copolymer obtained by emulsion polymerization are represented by the same general formula although the emulsion polymerized copolymer generally has a higher molecular weight. The present invention provides a room temperature curable resin composition combining the above-defined vinyl copolymer, condensation catalyst and crosslinking agent. Examples of the condensation catalyst include organic tin compounds such as dibutyltin dilaurate and dibutyltin diacetate; organic titanium compounds such as tetraisopropoxytitanium and tetrabutoxytitanium; amines such as 1,4-diazabicyclo(2.2.2)octane, 1,8-diaza-bicyclo(5.4.0)undecene- 7,3-(2-amino-ethyl)aminopropyltrimethoxysilane, and 3-aminopropyltriethoxysilane; inorganic acids such as hydrochloric acid and sulfuric acid; organic acids such as p-toluenesulfonic acid and phthalic acid; and alkali metal hydroxides such as sodium hydroxide and potassium hydroxide, with the organic tin compounds being especially preferred. The condensation catalysts may be used alone or in admixture of two or more. When the copolymer emulsion resulting from emulsion polymerization is used as a curable resin composition without further treatment, the condensation catalyst should be microcapsulated because the emulsion can be destroyed by addition of the catalyst or the catalyst can be deactivated in water. Any of well-known methods may be used for microcapsulation. For example a condensation catalyst, liquid paraffin and water are thoroughly agitated by a homomixer or homogenizer, thereby forming an emulsion containing microcapsules, which will cleave upon drying. Microcapsules may be used alone or in admixture of two or more. Preferably about 0.01 to 1 part by weight of the condensation catalyst is blended with 100 parts by weight of the silanol group-containing vinyl copolymer. We find that aqueous emulsion compositions of an aqueous emulsion of the silanol group-containing vinyl copolymer resulting from emulsion polymerization and a condensation catalyst for the silanol group are improved in storage stability and upon drying, form a siloxane crosslinked, cured film. The silanol group-containing vinyl copolymer includes a backbone consisting essentially of a vinyl copolymer, for example, an acrylic backbone, to which is attached a side chain containing a silanol group of a specific structure as defined above. Regardless of whether the condensation catalyst is present or absent, this crosslinking reaction does not proceed in an emulsion system, that is, a system in which the silanol group-containing vinyl copolymer is dispersed in water as independent emulsion particles in the presence of a surfactant. The emulsion composition is thus found to be stable during storage. The probable reason is that the surfactant stably covers emulsion particles to prevent the condensation catalyst from acting on the silanol groups. If the emulsion is destroyed, crosslinking reaction proceeds at once. This suggests that gelation can occur during storage if the emulsion loses storage stability. For use as a coating composition, the emulsion composition of the silanol group-containing vinyl copolymer can be applied and dried whereupon the aqueous medium volatilizes to destroy the emulsion, allowing the condensation catalyst to act on silanol groups and crosslinking reaction to take place. Room temperature drying insures sufficient curing although curing can be promoted by heating. Advantageously an aqueous emulsion of the silanol group-containing vinyl copolymer resulting from the emulsion polymerization method may be used directly as the application composition, without any treatment. A cross-linking agent is blended in the room temperature curable resin composition. Any e.g. known crosslinking agent may be used as long as it has two or more hydrolysable groups in a molecule. Preferably alkoxy, acyloxy, oxime and amine compounds of Si, Ti, Al, and Zr, and hydrolysates thereof are used. Examples include silanes such as tetramethoxysilane, tetraethoxysilane, methyltriacetoxysilane, methyltri(ethylmethylketoxime)silane, vinyltri(ethylmethylketoxime)silane, and methyltri(n-butylamino)silane and partially hydrolyzed oligomers thereof. Inter alia, tetramethoxysilane and partially hydrolysed oligomers thereof are preferred. When the crosslinking agent is blended in an emulsion system, careful attention should be paid to the stability of emulsion particles, that is, a choice should be made of an agent which does not destroy the emulsion. Preferably about 1 to 10 parts by weight of the crosslinking agent is blended with 100 parts by weight of the silanol group-containing vinyl copolymer. On curing the composition, silanol groups are bonded through the crosslinking agent with the aid of moisture (water) in air at room temperature to form a three dimensional structure according to the following reaction scheme. ZX m is a crosslinking agent, X is a hydrolysable group, m is 2 or more, Cat. is a condensation catalyst, and the remaining symbols are as previously defined. Additionally the resin composition may have inorganic or organic fillers, pigments and other additives blended therein insofar as the properties sought herein are not impaired. The resin composition may be used as a blend with other e.g. conventional resins, because the composition is well compatible with conventional resins. A resin composition as disclosed herein may be of one pack type wherein all the components are blended together or of two pack type wherein the condensation catalyst is a separate pack. As opposed to prior art acrylic silicone resin compositions, especially of one pack type, which suffer from the problems of thickening and gelation because crosslinking gradually proceeds during storage, in the present resin composition the crosslinking agent can serve as a moisture scavenger, to improve storage stability even when it is of one pack type, indicating that the composition is advantageously applied as weather resistant paint and coating. The vinyl copolymer having a silanol group in a side chain is useful as a major component in formulating a room temperature curable resin composition which cures into a coating having weatherability, flexibility and adherence. Even in one pack form, a room temperature curable resin composition can have good storage stability and cure into a coating having weatherability, flexibility and adherence. The composition is thus useful as paint for coating purposes. The methods explained herein enable simple preparation of such vinyl copolymers. EXAMPLE Examples of the proposals are given below together with Comparative Examples by way of illustration. All parts are by weight. Example 1 A flask equipped with a dropping funnel, condenser, thermometer and stirrer was purged with nitrogen, charged with 100 parts of toluene, and heated to 80°C. Separately a solution was prepared by mixing and dissolving 85 parts of methyl methacrylate, 7 parts of butyl acrylate, 8 parts of silicone methacrylate (I) shown in Table 1, and 1 part of 2,2'-azobis(isobutyronitrile). The solution was added dropwise to the toluene through the dropping funnel in a nitrogen stream at 80 to 90°C over 2 hours. The reaction solution was ripened at 80°C for 5 hours before a sample was taken therefrom for determining a reactivity, which was calculated to be 99.5% from a weight loss on drying. The reaction solution was cooled down to room temperature, obtaining a vinyl copolymer as a colorless clear liquid. Analysis was made on the copolymer. It had a weight average molecular weight of 40,000 as measured by GPC. A peak of Si-OH was observed in IR spectroscopy, indicating the presence of a silanol group. Examples 2-3 & Comparative Examples 1-2 Vinyl copolymers were prepared as in Example 1 using a polymerizable vinyl monomer, silicone methacrylate, radical initiator, and solvent and a temperature as reported in Table 1. The weight average molecular weight was measured by GPC and the presence of a silanol group was confirmed by IR spectroscopy. The results are shown in Table 1. Note that with respect to the silanol group, "+" indicates its presence and "-" indicates its absence. Examples 4-7 & Comparative Examples 3-6 A room temperature curable resin composition was prepared by mixing 100 parts of a vinyl copolymer, 5 parts of a crosslinking agent, and 0.2 part of a condensation catalyst and diluting with toluene to give a non-volatile content of 25% by weight. Using a bar coater (#36), the composition was applied to a cold rolled steel strip so as to provide a film thickness of about 10 µm after drying and allowed to stand at room temperature for 7 days for curing to take place. The cured coating was evaluated for hardness, adherence, flexibility, solvent resistance, and weatherability by the following methods. Also the room temperature curable resin composition was evaluated for storage stability. Hardness Pencil hardness was measured using a Mitsubishi Uni pencil. Adherence A crosshatched adhesive tape test was carried out by scribing the cured coating to define 10 × 10 sections of 1 mm square, applying adhesive tape (Celophan Tape by Nichiban K.K.) thereto, and stripping the tape. Adherence was evaluated in terms of the number of unstripped sections. Flexibility A 6-mm diameter mandrel test was carried out to evaluate a sample according to the following criterion. ○: no change in outer appearance Δ : microscopic cracks × : cracked and peeled Solvent resistance Xylene rubbing was carried out 10 cycles to evaluate a sample according to the following criterion. ○ : no change in outer appearance Δ : a little change in outer appearance × : a change in outer appearance Weatherability Using a sunshine weatherometer (manufactured by Suga Tester K.K.), the outer appearance of a sample after 300 hour exposure was evaluated according to the following criterion. ○ : no change in outer appearance Δ : a little change in outer appearance × : a change in outer appearance Storage stability A room temperature curable resin composition was placed in a container and stored at 40°C in a sealed condition to determine the time (days) taken until gelation. Example 8 In a reactor equipped with a condenser, thermometer and stirrer, 1 part of sodium dodecylbenzenesulfonate and 2 parts of polyoxyethylene nonyl phenyl ether (HLB = 15.5) were dissolved in 100 parts of deionized water. A premix of 85 parts of methyl methacrylate, 7 parts of butyl acrylate, and 8 parts of silicone (meth)acrylate I was added to the reactor. Agitation at room temperature resulted in a suspension. To the suspension was added an aqueous solution of 0.5 part of 2,2'-azobis(2-amidinopropane) dihydrochloride in 50 parts of deionized water. With stirring, the reaction solution was heated to 60°C over 30 minutes and ripened at 60 to 70°C for 5 hours. At this point, a sample was taken out for determining a reactivity, which was calculated to be 98.7% from a non-volatile content as determined from a weight loss on heating. The resulting aqueous emulsion was a milky white colloidal liquid. Filtration through a 200-mesh net left a residue which was less than 1% by weight of the resinous value. The copolymer resin isolated from the emulsion was determined for weight average molecular weight by GPC and for the presence of a silanol group by IR spectroscopy. The average particle size of resin particles was also measured. The results are shown in Table 3. Examples 9-12 Emulsion polymerization was carried out by the same procedure as in Example 8 except that the components were changed as shown in Table 3. A milky white colloidal liquid was obtained in every run. The copolymer resins isolated from the emulsions were determined for weight average molecular weight, the presence of a silanol group, and average particle size as in Example 8. The results are also shown in Table 3. Comparative Example 7 Emulsion polymerization was carried out by the same procedure as in Example 8 except that the components were changed as shown in Table 3 to include silicone (meth)acrylate ( III ) having an alkoxysilyl group. The reaction solution gradually thickened during ripening and gelled after 4 hours of ripening. Comparative Example 8 Emulsion polymerization was carried out by the same procedure as in Example 8 except that the surfactant was omitted. Resin particles precipitated out after 2 hours of ripening. Comparative Example 9 Emulsion polymerization was carried out by the same procedure as in Example 8 except that the silicone (meth)acrylate was omitted. There was obtained a milky white colloidal liquid. No silanol was confirmed. The results are shown in Table 3. Note that with respect to the silanol group, "+" indicates its presence and "-" indicates its absence. The components in Table 3 are shown below. 1) Silicone methacrylate 2) Surfactant A: sodium dodecylbenzenesulfonate (anionic surfactant) N: polyoxyethylene nonyl phenyl ether (nonionic surfactant, HLB = 15.5) 3) Polymerization initiator 2,2'-azobis(2-amidinopropane) dihydrochloride 4) Chain transfer agent n-dodecylmercaptan 5) Water-soluble organic solvent acetone Examples 13 & Comparative Examples 10-14 Compositions (emulsions) were prepared by uniformly mixing 100 parts of a vinyl copolymer (in the form of an emulsion having a solids content of 40% by weight), 1 part of a condensation catalyst, and 10 parts of a crosslinking agent as shown in Table 4. Each composition, about 2 grams, was cast into an aluminum dish having a diameter of 60 mm and a depth of 5 mm and allowed to stand at room temperature for 3 days for curing. The film had a thickness of about 0.3 mm after drying. The cured film was determined for crosslinking by carrying out Soxhlet extraction with toluene for 24 hours to determine a gel fraction. The emulsion composition was evaluated for storage stability by placing the emulsion composition in a container in a sealed manner, storing at 40°C, and determining the time taken until separation occurred between the vinyl copolymer and the aqueous medium. The results are shown in Table 4. The condensation catalyst and crosslinking agent used are shown below. A: microcapsulated dioctyltin dilaurate/water emulsion (active ingredient 30%) B: 30% dioctyltin dilaurate/acetone solution C: 2N aqueous hydrochloric acid D: 2N sodium hydroxide solution E: organosilica sol (Snowtex O manufactured by Nissan Chemical K.K.) Japanese Patent Application Nos. 5-301221 and 6-53670 are incorporated herein by reference. Although some specific embodiments have been described, many modifications and variations may be made thereto in the light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the proposals may be practised otherwise than as specifically described in the embodiments.

Claims: A room-temperature curable resin composition comprising: (a) vinyl copolymer comprising, in combination with units of copolymerised vinyl monomer, silanol group-containing (meth)acryl siloxane unit(s) of the following general formula (1) : wherein R 1 is hydrogen or methyl group, R 2 , R 3 , and R 4 are independently selected from substituted and unsubstituted monovalent hydrocarbon groups having 1 to 8 carbon atoms and siloxy groups of the formula - OSiR 6 R 7 R 8 wherein R 6 , R 7 and R 8 are independently selected from organic groups having 1 to 8 carbon atoms, R 5 is substituted or unsubstituted monovalent hydrocarbon group having 1 to 8 carbon atoms, n is an integer of 1 to 12 and a is 0 or 1; (b) condensation catalyst, and (c) crosslinking agent. A composition according to claim 1 in which the units of formula (1) form a copolymer backbone with units of said copolymerised vinyl monomer which are selected from (meth)acrylates, styrenes, olefins, vinyl chloride, vinylidene chloride, fatty acid vinyls, alkyl vinyl ethers and alkyl vinyl ketones. A composition according to claim 2 in which the copolymerised vinyl monomer is selected from methyl, ethyl, butyl and 2-ethylhexyl (meth)acrylates, styrene and vinyl acetate. A composition according to claim 2 or claim 3 in which the copolymerised vinyl monomer includes copolymerised vinyl monomer having a polar group, selected from unsaturated organic acids and anyhydrides thereof, vinyl monomers having a hydroxyl, epoxy or amino group, N-vinyl-2-pyrrolidone, (meth)acrylamide and acrylonitrile, in an amount not more than 20% by weight of the total vinyl monomer. A composition according to any one of the preceding claims in which the vinyl copolymer contains from 1 to 50 wt% units of formula (1). A composition according to claim 5 in which the vinyl copolymer contains from 5 to 20 wt% units of formula (1). A composition according to any one of the preceding claims in which the vinyl copolymer has weight average molecular weight in the range 5000 to 1000000. A composition according to any one of the preceding claims in which the condensation catalyst is selected from organic tin compounds, amines, inorganic acids, organic acids and alkali metal hydroxides. A composition according to claim 8 in which the condensation catalyst is selected from dibutyltin dilaurate, dibutyltin diacetate, tetraisopropoxytitanium, tetrabutoxytitanium, 1,4-diazabicylo(2.2.2)octane, 1,8-diazabicyclo(5.4.0)undecene-7-3-(2-aminoethyl)aminoproppyltrimethoxysilane, 3-aminopropyltriethoxysilane, hydrochloric acid, sulphuric acid, p-toluenesulphonic acid, phthalic acid, sodium hydroxide and potassium hydroxide. A composition according to any one of the preceding claims in which the condensation catalyst is microcapsulated. A composition according to any one of the preceding claims in which 0.01 to 1 parts by weight of the condensation catalyst is blended with 100 parts by weight of the vinyl copolymer. A composition according to any one of the preceding claims in which the crosslinking agent is an alkoxy, acyloxy, oxime, or amine compound of Si, Ti, Al, or Zr, or hydrolysate thereof. A composition according to any one of the preceding claims wherein the crosslinking agent is selected from tetramethoxysilane, tetraethoxysilane, methyltriacetoxysilane, methyltri(ethylmethylketoxime)silane, vinyltri-(ethylmethylketoxime)silane, methyltri(n-butylamino)silane, and partially hydrolysed oligomers thereof. A composition according to claim 13 wherein the crosslinking agent is tetramethoxysilane or partially hydrolysed oligomer thereof. A composition according to any one of the preceding claims in which 1 to 10 parts by weight of the crosslinking agent is blended to 100 parts by weight of the vinyl copolymer. A composition according to any one of the preceding claims in which groups R 2 , R 3 , R 4 and R 5 are selected from methyl, ethyl, propyl, butyl, cyclopentyl, cyclohexyl, phenyl, benzyl, vinyl and allyl, and R 2 , R 3 and R 4 may additionally be selected from trimethylsiloxy, ethyldimethylsiloxy, phenyldimethylsiloxy, vinyldimethylsiloxy, chloromethyldimethylsiloxy, 3,3,3-trifluoropropyldimethylsiloxy and 2-cyanoethyldimethylsiloxy. A composition according to claim 16 in which all of R 2 to R 8 are methyl. A method of preparing a composition according to any one of the preceding claims in which the vinyl copolymer is prepared by a method comprising the step of copolymerising polymerisable vinyl monomer with a silanol group-containing (meth)acryl siloxane of the following general formula (2) : wherein R 1 to R 8 , n and a are as defined above, in the presence of a radical initiator. A method of preparing a composition according to any one of claims 1 to 17 in which the vinyl copolymer is prepared by a method comprising the step of emulsion polymerising polymerisable vinyl monomer with a silanol group-containing (meth)acryl siloxane of the following general formula (2): wherein R 1 to R 8 , n and a are as defined above, in an aqueous medium in the presence of surfactant and polymerisation initiator. A method according to claim 19 which the surfactant is a mixture of (a) anionic surfactant and (b) nonionic surfactant having an HLB value of at least 10, in a weight ratio of from 1/9 to 4/6. A method according to claim 19 or claim 20 in which the polymerisation initiator is water soluble. A cured product obtained by curing a composition according to any one of claims 1 to 17. A coated article having a cured coating obtained by curing a composition according to any one of claims 1 to 17 on the article. The use of a composition according to any one of claims 1 to 17 for coating an article. Use according to claim 24 in which the composition is applied as an aqueous emulsion composition.

Inventors: ICHINOHE SHOJI, MORIOKA SHINICHI, SUZUKI NOBUYUKI, YAMAZAKI TOSHIO, ICHINOHE, SHOJI, MORIOKA, SHINICHI, SUZUKI, NOBUYUKI, YAMAZAKI, TOSHIO, ICHINOHE, SHOJI, C/O SILICONE-ELEC. MATERIALS LAB, MORIOKA, SHINICHI, C/O SILICONE-ELEC.MATERIALS LAB, SUZUKI, NOBUYUKI, C/O SILICONE-ELEC. MATERIALS LAB, YAMAZAKI, TOSHIO, C/O SILICONE-ELEC. MATERIALS LAB
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1994
Main classification: C08F230
IPC codes: C08F230