Light emitting device and method of manufacturing the same

Abstract: A light emitting device comprises a luminous region (2) comprising a luminous porous material comprising a crystalline semiconductor and a non-porous region (1) adjacent to the luminous region, wherein a conductive type between both the regions is different at an interface (4) between the luminous region and the non-porous region and the crystal structure between both the regions is continuous.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a light emitting device and a light emitting device manufacturing method. Related Background Art Recently, porous materials have been remarkable as a new functional material used for an active structure factor in a device. The porous structure of IV-group semiconductor crystal, for example, has been chiefly used for the conventional SOI (Silicon On Insulator) structure forming process (refer to T. Unagami and M. Seki, J. Electrochem. Soc. 125, 1339 (1978)) because of its rapid oxidation capability. In this case, raw material has been used only as a structural material, in no connection with its electronic and optical properties. However, recently, a research and development has been vigorously made as for an application to light emitting devices which originates from a luminous phenomenon at room temperatures and with high efficiency (refer to L. T. Canham, Appl. Phys. Lett. 56, 1046 (1990)) because of the luminous phenomenon at low temperature (refer to C. Pickering, et al., J. Phys. C17, 6535 (1984)) due to a micro-structure with a desirable carrier quantum closing effect. Generally, the porous structure itself can be easily shaped by processing a raw material. If some problems are overcome to put into a practical use, applying functionally such porous materials may provide a very attractive new technology. One large obstacle which impedes putting the porous material to practical use is that it is difficult to inject current to the porous region. An active light emitting device must function as an electroluminescence (EL) device. In order to realize an EL device with higher efficiency, it is desirable to use a current injection-type device. It has been so far reported that a light emitting diode (LED) using a solid-state electrode on a current injection layer indicates far lower efficiency, in comparison with the potential high photoluminescence (PL) efficiency of the same porous material. For example, a naked eye can clearly recognize under an illumination in a room that a porous silicon layer which is formed by anodizing the surface of a monocrystalline silicon substrate in a hydrofluoric acid solution is luminous over visible rays range in response to an illumination by a several-watt ultraviolet rays lamp so that the PL energy efficiency exceeds several %. However, since the current injection which is performed via a Schottky junction between a semi-transparent gold electrode and the same porous layer has less than a quantum efficiency of 10 -3 % (refer to N. Koshida, et al., Appl. Phys., Lett. 60, 347 (1992)), a very high applied voltage of several hundred volts is needed to recognize a feeble luminescence with a naked eye in a dark place (refer to A. Richter, et al., IEEE Electron Device Lett. 12, 691 (1991)). An remarkable improvement is not seen in the LED including a conductive transparent electrode (refer to F. Namavar, et al., Appl. Phys. Lett. 60, 2514 (1992)) of an injection electrode of indium tin oxide, an n-type micro-crystalline silicon carbide film (µc-SiC) (refer to T. Futagi, et al., Jpn. J. Appl. Phys. 31, L616 (1992)), and a pn-heterojunction, in order to overcome such a situation. In the example where an n-type gallium phosphorus (GaP) is used for the same purpose, even a current injection has not been yet succeeded in an actual case (refer to J. C. Campbell, et al., Appl. Phys. 60, 889 (1992)). On the other hand, it has been reported that the current injection in which a porous silicon layer is immersed in an electrolytic solution used for an anodization to utilize the solid-liquid interface in the internal walls in pores of the porous silicon improves the luminous efficiency, compared with the above solid-state electrode (refer to A. Halimaoui, et al., Appl. Phys. Lett. 59, 304 (1991), P. M. M. C. Bressers, et al., Appl., Phys., Lett, 61, 108(1992), E. Bustarret, et al., Appl. Phys. Lett. 61, 1552(1992), L. T. Canham, et al., Appl. Phys. Lett. 61, 2563 (1992). The above method is poor in practical use because the porous silicon layer is etched at a light emission so that the light emission disappears soon. However, it is noted that there is a possibility that the current injection efficiency dominates largely the injection-type EL efficiency of porous silicon. From this viewpoint, it is considered that the poor interface between the electrode and the luminous porous silicon layer impedes the current injection, thus causing the poor emitting efficiency of the solid-state injection electrode type LED. Therefore, it is desirable to introduce a new injection electrode material with good interface property over the above heterojunction example. DE-A-41 26 955 discloses a light emitting device comprising an electrode, a p-type substrate, a p + -type porous layer, an n + -type porous layer and an electrode. Moreover, IBM Technical Disclosure Bulletin, vol 36, no. 3 (March 1993), Armonk, New York, US, pp. 289 and 290: "Electroluminescent Device Based on Silicon Semiconductor", discloses a method for fabricating a silicon-based electroluminescent device comprising an n-type layer, a p-type layer as well as electrode contacts. The p-type layer is made porous and acts as the luminous layer. Moreover, this document discloses a method for making a further silicon-based electroluminescent device comprising an electrode, a p + -type non-porous region, a p-type porous region, and n + -type non-porous region and an electrode. In order to overcome the above mentioned technical problems, an object of the present invention is to provide a light emitting device which has a reduced contact resistance between its electrode and its luminous region. Another object of the present invention is to provide a light emitting device which can perform a current injection with high efficiency. It is a further object of the present invention to provide a light emitting device having an excellent luminous efficiency. Moreover, it is an object of the present invention to provide a method for manufacturing such a light emitting device. According to the present invention, the above objects are achieved by a light emitting device comprising a luminous region comprising a porous semiconductor having a first conductivity type, a contact region comprising a non-porous semiconductor having a second conductivity type and being electrically connected to the luminous region, and an electrode provided at the contact region, the luminous region being light-emitting as a result of a current flowing into the luminous region through the contact region, wherein an intermediate region comprising a non-porous semiconductor of a first conductivity type is provided between the luminous region and the contact region and that the current flows into the luminous region through the intermediate region. In addition, the above objects are achieved by a method for manufacturing a light emitting device as defined above, comprising the steps of epitaxially growing a p-type silicon layer on an n-type silicon substrate, causing a part of the p-type silicon layer in the thickness direction to be made porous, and providing the n-type silicon substrate and the p-type silicon layer having been made porous with an electrode. These and other objects of the present invention will become apparent from the following drawings and detailed description taken in connection with the drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic diagram showing a structural explanatory example of a light emitting device which is not according to the present invention; Figs. 2A and 2C are schematic diagrams each showing explanatory examples not according to the present invention, and Figs. 2B and 2D are schematic diagrams each showing an embodiment of the light emitting device according to the present invention. Figs. 3A and 3C are schematic diagrams each showing explanatory examples not according to the present invention, and Figs. 3B and 3D are schematic diagrams each showing an embodiment of the light emitting device according to the present invention; Figs. 4A to 4C are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Figs. 5A to 5C are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Fig. 6 is a schematic diagram showing an embodiment of a light emitting device manufacturing process according to the present invention; Fig. 7 is a schematic diagram showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Figs. 8A to 8C are schematic diagrams showing an embodiment of a light emitting device manufacturing process according to the present invention; Figs. 9A to 9C are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Figs. 10A to 10D are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Fig. 11 is a schematic diagram showing an explanatory example of a light emitting device manufacturing process not acccording to the present invention; Figs. 12A to 12D are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Fig. 13 is a schematic diagram showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Figs. 14A to 14F are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Figs. 15A to 15D are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; Figs. 16A to 16E are schematic diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention; and Figs. 17A to 17D are model diagrams showing an explanatory example of a light emitting device manufacturing process not according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention results from that the present inventors have zealously studied to overcome the above problems. An explanation will be made below in detail as for the light emitting device and the light emitting device manufacturing method according to the present invention, with reference to the drawings. Fig. 1 is a schematic cross sectional view showing the most conceptual element structure of an explanatory light emitting device not according to the present invention. The light emitting device has a structure where the luminous region 2 comprising a luminous porous material is sandwiched between the current injection electrode regions 1, 3. The injection electrode region 1 is formed of a non-porous material with a low resistance which is same as the mother material for the luminous region 2. The interface 4 between both the regions has a continuous crystal structure. Both the regions have a different conductivity type from each other, and homogeneous pn-type junction is formed there. The injection electrode region 3 does not depend on its structure if it is of a low resistance. The injection electrode region 3 has the same conductivity type as that of the luminous region 2. The interface between both the regions has a continuous crystal structure. When a DC current is conducted between the injection electrode regions 1 and 3 via the extracting electrode 5 and 5' connected to the device, electric charges are injected from the homogeneous pn-junction interface 4 to the luminous region 2 so that light emission occurs. When the extracting electrode 5' is directly bonded to the light emitting region 2 with a low contact resistance, the injection electrode region 3 can be omitted. The point of this explanatory device will be described by studying how the interface property affects the current injection efficiency of the entire element. First, (1) the good ohmic contact between the extracting metal contact 5 and the injection electrode region 1 is confirmed because the injection electrode region 1 is formed of a non-porous material with low resistance. (2) A good homogeneous pn-junction can be formed because the crystal structure continues at the junction interface 4 between the injection electrode region 1 and the luminous region 2 of the same material and along both the regions sharing a common mother material. As described in Related Background Art, the interface characteristics dominate current injection efficiency and the luminous efficiency of the element. Hence, the explanatory light emitting device has a high efficiency by forming an injection electrode region which is in "non-porous structure", which has "a crystal structure" continuous to the luminous region 2, and which is of "the same material" and of "heterojunction-type". Moreover, when the injection electrode region 3 is provided, (3) the contact between the luminous region 2 and the injection electrode region 3 is no matter because of "continuity of crystal structure", and (4) it is expected that the good ohmic contact between the injection electrode region 3 and the extracting electrode 5' results from the low resistivity of the injection electrode region 3. It is not necessarily needed that the luminous region 2 is made of an uniform luminous porous material along the whole region. The luminous region may be formed of plural porous or non-porous regions of different structure. It is required that at least one of the regions must be a luminous material. Therefore, if other regions are offered for other uses except the luminous function, both the device characteristics and the device manufacturing method may be convenient in some cases. For example, the vicinity of the interface of the injection electrode region 1 is made non-porous or non-luminous porous material having relatively large residual structure, whereby the pn-junction can further be improved at the interface 4. Of the light emitting device manufacturing methods according to the present invention (to be described later), the method which uses an epitaxial growth can further improve the epitaxial interface and the film quality of an epitaxial layer. In the porous material existing in the light emitting region 2, the structure is formed of the same mother material as the injection electrode region 1 or 3, whereby it is not important that a hetero-material may be formed on the surfaces facing pores in the residual structure. Moreover, all spaces in a pore may be filled with a hetero-material. Generally, in some cases, the mechanical and thermal stability is not enough because the luminous porous material has a very fine residual structure. Hence, in some cases, an effective reinforcement may be made using the above hetero-material. Figs. 2A to 2D illustrate a spatial arrangement of a luminous region comprising a non-porous region and a luminous porous material. In particular, Figs. 2B and 2C illustrate embodiments of a light emitting device according to the present invention. Figs. 2A to 2D show an example where a current route is vertically formed on the surface of a monocrystalline substrate in a wafer form. In the most simplified device structure, shown in Fig. 2A, a pn-junction is formed between the non-porous layer 1 of a first conductivity type and the luminous porous layer 2 of a second conductivity type, with a continuous crystal structure in the pn-junction. The extracting electrodes 5 and 5' are provided on the ends of the element structure, respectively. Like numerals represent regions corresponding to those in Fig. 1. According to the present invention, the intermediate layer 2' is arranged between the nonporous layer 1 and the luminous porous layer 2 (Fig. 2B). This embodiment shows that the luminous region 2 includes an region other than the luminous porous region in the structure shown in Fig. 1. That is, the intermediate layer 2' includes the luminous region 2 shown in Fig. 1. The intermediate region 2' comprises a non-porous material including monocrystal. However, the conductive type of the intermediate region 2' is the same as that of the luminous porous layer 2, and the layers on the front and back of the intermediate layer 2' should be continued in crystal structure. However, it is not necessarily needed that the interface between the intermediate layer 2' and other layer in the luminous region 2 is sharp, but it may be varied restrictively and continuously. According to a further illustrative example not according to the present invention, depending on the characteristics of the interface between the extracting electrode 5' and the luminous porous layer 2, an additional injection electrode layer 3 may be provided (Fig. 2C). This is an explanatory example showing the injection electrode 3 which is provided in the device structure shown in Fig. 1. The injection electrode layer 3 is formed of, for example, a non-luminous porous material or non-porous material including monocrystal. However, the conductivity type of the injection electrode layer 3 should be same as the luminous non-porous layer 2. The crystal structure between the injection electrode layer 3 and the luminous non-porous electrode layer 2 should be continued in crystal structure. However, the interface is not necessarily needed to be sharp, but may restrictively and continuously vary. Fig. 2D illustrates an embodiment of the invention comprising the injection electrode layer 3. Figs. 3A to 3D are explanatory examples and embodiments showing that an electrode route is formed in a direction parallel to a surface of noncrystal film provided on the insulating surface of, for example, the substrate in wafer form 0. Each structural element and its function correspond to those shown in Figs. 2A to 2D. The extracting electrodes 5 and 5' are in contact with the film surface. However, the geometric arrangement should not be limited to the present example. Next, as for the light emitting device manufacturing method which may be used for the manufacture of the above explained devices, the device of an embodiment shown in Figs. 2A to 2D and 3A to 3D will be explained in accordance with a process for forming a light emitting region comprising a luminous porous material and a non-porous region each having a different conductivity type, so as to form a continuous crystal structure. The first explanatory method of manufacturing a device with the structure shown in Fig. 2A is shown in Figs. 4A to 4C. First, a non-porous substrate 1 having a desired conductivity type and a resistance is prepared (Fig. 4A). The layer 20, which has a conductivity type different from that of the substrate 1 but has the same mother material and has a continuous structure at the interface 4, is provided on the surface of the substrate 1 (Fig. 4B). In a concrete method, the layer 20 may be formed by epitaxial growth on the surface of the substrate 1 with impurity elements being introduced to control the conductivity type, or the layer 20 is internally formed from the surface of the substrate 1 by effecting counter-doping by an ion implantation from the surface of the substrate 1, a solid-phase diffusion from a deposited, or a diffusion from a gas-phase film. Moreover, it is possible to combine the above methods. Next, the luminous region 2 comprising a luminous porous material can be made by making the layer 20 porous from the surface to the interface 4 by using a method of converting a non-porous material into a porous material, such as anodization or a photo-formation (Fig. 4C). Next, the extracting electrodes 5 and 5' are formed. Finally, a device with the structure shown in Fig. 2A can be formed. Since the pn-junction interface 4 has a continuous crystal structure before a porous structure formation, the original state is maintained even after a final step. Next, the second explanatory method of manufacturing a device with the structure shown in Fig. 2A is shown in Figs. 5A to 5C. First, a non-porous substrate 1 with a desired conductivity type and a desired resistance is prepared (Fig. 5A). A porous structure formation is effected from the surface of the substrate 1 to a desired depth (Fig. 5B). Next, a counter doping is carried out from the surface of the porous structure formation layer 20 to make the luminous porous layer 2 having a different conductivity type from that of the substrate 1 (Fig. 5C). Then a device with the structure shown in Fig. 2A can be formed by forming the extracting electrodes 5 and 5'. In the same manner as those in Figs. 4A to 4D, the crystal structure, needless to say, is continuous at the pn-junction interface 4. Explanatory methods of manufacturing the device shown in Fig. 2B will be described as follows. The first methods can be performed by slightly modifying the methods each which forms the device shown in Fig. 2A explained by referring to Figs. 4A to 4C and 5A to 5C. First, in the step as shown in Fig. 4B, the intermediate layer 2' is left to a desired thickness by terminating porous structure formation just before the formation reaches the interface 4 from the surface of the layer 2 (Fig 6). In the step shown in Fig. 4C, a counter doping is effected over the surface of the porous structure formation layer 20 to the non-porous region of the substrate 1 to form the intermediate layer 2' having a desired thickness (Fig. 7). In either case, the intermediate layer 2' is made of a non-porous material of the same conductive type as that of the luminous porous layer 2 and has a continuous crystal structure at the pn-junction interface 4 to the substrate 1. The second explanatory method of manufacturing the device shown in Fig. 2B is not applied to the step in which a pn-junction is formed by counter-doping after the porous structure layer is formed as shown in Figs. 5A to 5C. The reason is that the phenomenon is utilized, that both the porous structure formation and the porous material structure are largely influenced by the composition of non-porous material, impurity concentration, and other factors. For example, in the porous silicon formation by anodization, the structure strength increases because when a heavy impurity concentration in a silicon substrate lowers a resistance, the residual structure is large and the porous degree lowers, thus suppressing a resistance increase due to porous material. In this case, a non-luminous porous material is formed. In the steps explained with reference to Figs. 8A to 8C, a non-luminous porous material of low resistance is used as the intermediate layer 2' shown in Fig. 2B. First, the non-porous substrate 1 having a desired conductivity type and a resistance is prepared (Fig. 8A). On a surface of the substrate, the layer 20', which has conductivity type different from that of the substrate 1 but has the same mother material and has a continuous crystal structure at the interface 4, is provided. Further the layer 20, which has the same conductivity type as that of layer 20' but has a different impurity concentration and has a continuous crystal structure (Fig. 8B). For example, the impurity concentration of the layer 20' may be set to a higher amount than that of the layer 20. The process used in the step shown in Fig. 4B can be used in the concrete method of manufacturing the layers 20 and 20'. For example, when a formation is effected by epitaxial growth, layer 20 may be deposited after a deposition of the layer 20'. In ion implantation, multiple step ion-implantation with varying implanting energy conditions or ion species, or an ion-implanting profile may be used, whereby the spatial transition between the layers 20 and 20' becomes continuous. Next, by making the layers 20 and 20' porous from the surface to the interface 4 (Fig. 8C), the luminous region 2 comprising a luminous porous material, the layer 20' acting as the intermediate layer 2', is formed. Then the extracting electrodes 5, 5' are formed on the luminous region 2 to form a light emitting device with the structure shown in Fig. 2B. In this case, the crystal structure at the pn-junction interface is continuous. Next, the first explanatory method of manufacturing a device with the structure shown in Fig. 2C is shown in Figs. 9A to 9C. First, the non-porous substrate 1 having a desired conductivity type and a resistance is prepared (Fig. 9A). On a surface of the substrate, the layer 20, which has a conductivity type different from that of the substrate 1 but has the same mother material and has a continuous crystal structure at the interface 4, is provided. Further, the layer 30, which has the same conductivity type as that of the layer 20 and has a different impurity concentration, is provided (Fig. 9B). For example, the impurity concentration of the layer 30 may be higher than that of the layer 20. The process used in the step shown in Fig. 4B can be used as the concrete method of manufacturing the layers 20 and 30. For example, the formation is effected by epitaxial growth, the layer 30 is deposited after a deposition of the layer 20. In ion implantation, multiple step ion-implantation with varying implanting energy conditions or ion species, or an ion-implanting profile may be used, whereby the spatial transition between the layers 20 and 30 becomes continuous. Next, by making the layers 30 and 20 porous from the surface to the interface 4 (Fig. 9C), both the layers become an injection electrode layer 3 of a non-luminous porous material and the luminous layer 2 comprising a luminous porous material. Then the extracting electrodes 5 and 5' are formed on the luminous layer 2 to form a light emitting device with the structure shown in Fig. 2B. In this case, the crystal structure at the pn-junction interface 4 is continuous. The second explanatory method of manufacturing a device with the structure shown in Fig. 2C is shown in Figs. 10A to 10D. First, the non-porous substrate 1 having a desired conductivity type and a resistance is prepared (Fig. 10A). On a surface of the substrate, the layer 20, which has a conductivity type different from that of the substrate 1 but has the same mother material and has a continuous crystal structure at the interface 4, is provided (Fig. 10B). The concrete method of manufacturing the layer 20 is the same as the process described above. Next, the layer 20 is made porous from the surface to the interface 4 to form the luminous layer 2 comprising a luminous porous material (Fig. 10C). The injection electrode layer 3 of a non-porous material is deposited on the surface by epitaxial growth etc. (Fig. 10D). Since the injection electrode layer 3 should be of the same conductivity type as that of the light emitting device 2 and have a low resistance, the impurities are introduced at a deposition or are doped in a later step. By performing both the first and second explanatory methods for forming a device with the structure shown in Fig. 2C, it is possible to form the injection electrode layer 3 of the plural layers shown in Fig. 11. In this case, the non-porous injection electrode layer 32 may be deposited by epitaxial growth etc. on the non-luminous porous injection electrode layer 31 formed according to the first method. In the third explanatory method for manufacturing a device shown in Fig. 2C, the order of the layer manufacturing steps described above is reversed. The third process will be explained below with reference to Figs. 12A to 12D. First, the non-porous substrate 0 having a desired conductivity type and a resistance is prepared (Fig. 12A). The substrate 0 is made porous to a desired depth from the surface thereof to form the luminous layer 2 comprising a luminous porous material (Fig. 12B). The injection electrode layer 1 is deposited by epitaxial growth etc. on the surface of the substrate 0 (Fig. 12C). In this case, the injection electrode layer 1 should be of a non-porous material with a low resistance. The interface 4 between the injection electrode layer 1 and the luminous layer 2 should be a continuous crystal structure and the substrate 0 should be different from the luminous layer 2 in a conductivity type. Therefore, it is required that impurities are introduced at a deposition or are doped in a later step. Putting the substrate upside down makes the structure shown in Fig. 12D. The pn-junction interface 4 is formed between the injection electrode layer 1 finally deposited and the luminous layer 2. The injection electrode layer 3 which has the same conductivity as that of the luminous layer 2 in the substrate 0 left without being made porous is formed on the luminous layer 2. The extracting electrodes 5 and 5' are formed to obtain a device shown in Fig. 2C. The device shown in Fig. 2D can be formed by combining the method of manufacturing the device shown in Fig. 2B and the method of manufacturing the device shown in Fig. 2C. For example, referring to Fig. 2A, after a layer which is of the same conductivity type as that of the substrate 0 and has a high impurity concentration is formed on the surface of the non-porous substrate 0, the process goes to the steps shown in Fig. 12B. Thus the high impurity concentration layer is converted to the intermediate layer 2' of non-luminous porous material so that the structure shown in Fig. 13 is obtained and the device shown in Fig. 2D can be formed. The explanatory method of manufacturing the device group shown in Figs. 3A to 3D is the same as that shown in Figs. 2A to 2D except that a non-porous film on the insulating surface of a substrate is made porous. An explanation will be made as for some typical forming steps with reference to the device structure in Fig. 3D as an example. Figs. 14A to 14F show the first explanatory method of manufacturing the device in Fig. 3D. First, a substrate on which a non-porous film 20 is formed on the insulation surface of the substrate 0 is provided (Fig. 14A). Next, using a photolithography process and a local doping process such as a focused ion beam technique which are conventionally used in the semiconductor integrated circuit fabrication, the region 10 having a conductivity type different from that of the non-porous film 20 is formed in the non-porous film 20 and the region 30 having the same conductivity type as that of the non-porous film 20 and having a high impurity concentration and a high resistance is formed (Fig. 14B). The take-out electrodes 5 and 5' in contact with the regions 10 and 30, respectively, are formed using the patterning technique (Fig. 14C). Furthermore, a protective layer 6 is formed over the electrodes 5 and 5' (Fig. 14D). Since the protective layer 6 protects the structure underneath it in the following step when the region 20 of the remaining non-porous film is subjected to a porous structure forming process, it must sufficiently withstand against the porous structure forming process. The protective film 6 on the left end of the opening is offset from the boundary between the regions 10 and 20 as shown in the drawing. Next, the region 20 is converted into a porous layer. In the case where an anodizing process is used as a concrete porous structure forming process, the entire substrate is immersed in an electrolytic solution. Current is conducted between the take-out electrode 5' and the counter electrode 7 (Fig. 14E). In the case of a photo formation, the porous structure forming process is carried out merely by illuminating uniform rays. In the above steps, of the region 20, the region underneath the opening in the protective film 6 is converted into the luminous region 2 including a luminous porous material, the offset part is converted into the intermediate layer 2', and the regions 10 and 30 respectively converted into the injection electrode regions 1 and 3. The device shown in Fig. 3D having a pn-junction at the interface 4 with a continuous crystal structure is formed (Fig. 14F). If the offset of the protective film 6 at the opening is omitted, the device shown in Fig. 3C is formed. If formation of the region 30 is omitted, the device shown in Fig. 3B is formed. If the offset at the opening in the protective film 6 and formation of the region 30 are omitted, the device shown in Fig. 3A is formed. Next, the second explanatory method of forming the devices shown in Fig. 3D will be explained with reference to Figs. 15A to 15D. First, a substrate, comprising the non-porous film 20 formed on the substrate 0 having an insulation surface is provided (Fig. 15A). The entire substrate is immersed in an electrolytic solution. Then a photo-formation is carried out by illuminating a locally focused light 6 onto the non-porous film 20 to form the luminous region 20 including a luminous porous material (Fig. 15B). Sequentially, using a local doping technique, the region 10 having a conductivity type different from that of the non-porous film 20 and the region 30 having the same conductivity type as that of the non-porous film 20 and having a high impurity concentration and a low resistance are formed (Fig. 15C). According to the above steps, the structure shown in Fig. 3D, which includes the regions 10 and 30 respectively converted into the injection electrode regions 1 and 3 as well as the region remaining between the region 10 and the luminous region 2 converted into the intermediate layer 2', is formed (Fig. 15D). The devices shown in Figs. 3A to 3C can be formed by changing the spatial position of the region 10, or omitting some steps. [Examples] A detailed explanation will be made below as for the examples of a light emitting device and a light emitting device manufacturing method according to the present invention with reference to examples using a silicon crystalline material. (Comparative Example 1) The comparative example of a light emitting device having the structure shown in Fig. 2A shown with the forming steps in Figs. 4A to 4C will be explained below. First, a phosphorus-doped n-type silicon monocrystalline wafer which has a face orientation of <100> and a resistivity of 0.02 Ω·cm is prepared. On the surface of the wafer, a p-type monocrystalline silicon layer of a thickness of about 1 µm was epitaxially grown using a CVD process simultaneously using dichlorosilane gas and diborane gas. Aluminum of a film thickness of 200 nm (2000Å) was vapor-deposited on the back surface of the wafer to ensure perfect ohmic contact. Next, only the wafer surface was contacted with a hydrofluoric acid·ethanol solution of 20 wt% so as to face a platinum plane electrode. While the wafer surface was illuminated with a 1 kW halogen lamp, a DC voltage was applied between the wafer acting as an anode electrode and the platinum electrode. An anodization was performed for two minutes while maintaining the current density on the wafer surface to 10 mA·cm -2 . When the cross section of a sample particularly prepared to confirm the porous structure formation was observed under an electron microscope with a high resolving power, it was confirmed that the anodization advanced just to a depth of 1 µm from the wafer surface to form a porous layer and the residual structure of the porous layer was perfectly continued to the crystal structure of the substrate. This means that the entire p-type epitaxially grown Si layer was converted into a porous layer. Illuminating the surface of the porous layer with a 5 watt ultraviolet lamp gave a red PL. Since the luminous porous layer had a very fine and brittle structure, only the surface of the residual structure was oxidized by a RTO (Rapid Thermal Oxidation) process to stabilize it. By this process, the PL emission peak was somewhat blue-shifted and the strength was increased about five times. After it was confirmed that the porous layer oxidized and having an increased PL efficiency was sufficiently in a stable state, an SiO 2 film of a thickness of 200 nm (2000Å) was again deposited on the wafer surface by using the CVD process. Then some 2 mm square openings were formed in the oxide film by the conventional photolithography process. In forming the openings, the oxide film on the top surface of the oxidized porous layer as the underlying layer must also be removed. Before a re-formation of a natural oxide film in the opening, a semi-transparent gold thin film of a film thickness of 10 nm (100Å) was deposited thereto. Moreover, an Al extracting electrode was wired from the opening. When a DC current was conducted between the contacts on the front and the back surfaces of the wafer of the device prepared by the above process, a rectification characteristic was indicated where the current direction with the front surface contact side being the positive electrode is the forward direction, and a visible area luminescence of nearly orange color occurred from the openings in the oxide film at a threshold voltage of about 3 volts. It is assumed that this luminescence is an electroluminescence due to a current injection into the porous silicon layer with an ultra-fine structure via the junction interface between the n-type monocrystalline layer of the substrate and the p-type porous layer just thereon. It is assumed that the reason for the luminous threshold voltage is practically and sufficiently low is that the continuous crystal structure in the pn-junction interface provides good rectification characteristic whereby the current injection efficiency is higher than that of a conventional structure. (Example 1) An explanation will be made as for an example of a light emitting device of the present invention with the structure shown in Fig. 2B manufactured in the forming steps shown in Fig. 6. A device was prepared by repeating the device preparation steps of Comparative Example 1 with the exception that the anodization time in was reduced by 1.5 seconds. When the cross section of a sample particularly prepared to confirm the porous structure formation was observed under an electron microscope with a high resolving power, it was confirmed that the anodization advances from the wafer surface up to about 0.9 µm depth to form a porous layer, and that the lattice image was perfectly in a continuous state but a monocrystalline intermediate layer about 0.1 µm thick was formed between a contrast producing surface which appeared to be an epitaxial interface and a porous layer. When a DC voltage was applied between the contacts on the front and back surfaces of a wafer, the device showed a rectification ratio which is higher by nearly one order than that of the device of Comparative Example 1. The threshold voltage increased slightly to about 3.5 volts but a luminous efficiency was obtained which was several times stronger than that of the device of Comparative Example 1. It is presumed that the improved rectification characteristic results from that the front and back portions of the pn-junction are formed of a perfect monocrystal. This improves the efficiency of current injection into the luminous porous layer, thus increasing the luminous efficiency. (Example 2) An explanation will be made as for an embodiment of a light emitting device according to the present invention having the structure shown in Fig. 2B manufactured in the steps shown in Figs. 8A to 8C. A device was prepared by repeating the device preparation steps of Comparative Example 1 with the exception that the step of growing a p-type epitaxial layer on an n-type monocrystalline substrate was divided into two steps. The two steps for forming a p-type layer comprised depositing a heavily doped layer about 0.2 µm thick with the partial pressure of diborane gas increased ten times and then reducing the diborane gas partial pressure to the original pressure to grow a lightly doped layer about 0.2 µm thick. The observation of the cross section of a sample found that the anodization proceeds from the wafer surface to about 1 µm depth to form a porous layer. However, according to a further detail observation, it was confirmed that a porous material having ultra-fine pores was formed to a depth of about 0.8 µm from the wafer surface and the layer of a thickness of about 0.2 µm under the ultra-fine porous material was formed of a porous material of large pores having an average structure larger by about two figures in structure. Conducting a DC current between the electrodes on the front and back surfaces of the wafer found that the device had the intermediate characteristic between the devices according to Comparative Example 1 and Example 1 in items including the rectification characteristics, luminous threshold voltage and luminous efficiency. In this case, it is presumed that the porous layer with large pores functions as an intermediate layer. (Comparative Example 2) An explanation will be made as for a Comparative example of a light emitting device having the structure shown in Fig. 2A manufactured in the steps in Figs. 5A to 5C. First, a boron-doped p-type silicon monocrystalline wafer having a face orientation of <100> and a resistivity of 10 Ω·cm was prepared. Boron ions were accelerated at 50 keV to be implanted into the back surface of the wafer with a dose of 5 x 10 14 cm -2 . Then the wafer was subjected to a thermal annealing at 950°C for 30 minutes in nitrogen atmosphere to be activated. Next, the substrate was arranged between a pair of parallel platinum plane electrodes and immersed in a hydrofluoric acid·ethanol solution of a concentration of 25 wt%. Anodization was performed by applying a DC voltage between one platinum electrode acting as an anode electrode facing the back surface of the wafer and the other platinum electrode for one minute, with the region other than the wafer surface being electrically insulated, while the current density on the wafer surface was controlled to 10 mA·cm -2 . Then, the wafer was left for 10 minutes under a lighting in a room, with the active circuit electrically shortcircuited. When the cross section of an observation sample prepared particularly to check the porous forming process was observed under a high resolution electron microscope, it was confirmed that the anodization advanced from the surface of the wafer just to 0.5 µm deep to form a porous layer. When the surface of the porous layer were irradiated with a 5-watt ultraviolet ray lamp, a PL in red occurs. Next, hydrogen ions accelerated at 30 keV were implanted into the surface of the wafer with a dose of 1 x 10 15 cm -2 and subjected to RTO to effect activation and porous structure stabilization. The PL luminous peak was somewhat blue-shifted and increased in intensity. After it had been confirmed that the porous layer oxidized to have the increased PL efficiency is in a sufficiently stabilized state, the oxide film on the top surface of the porous layer was removed with a dilute aqueous hydrofluoric acid solution. Before re-formation of a natural oxide film, ITO was vapor-deposited to a thickness of 150 nm (1500Å) and then patterned in 5 mm square in the fashion of islands. An AlSi film was deposited on the entire back surface of the wafer by sputtering. When a DC current was conducted between the electrodes on the front and the back surfaces of the wafer of the device produced by the above steps, a rectification characteristic was indicated, where the current with the front surface electrode being the positive electrode is the forward direction, and a visible area luminescence of nearly orange color occurred from the ITO island portions at a threshold voltage of about 5 volts. It is considered that the light emission is an electroluminescence due to a current injection to the porous silicon layer with a ultra-fine structure via the junction interface between the p-type monocrystalline layer of the substrate and the porous layer as provided just on the p-type layer and changed to n-type by activation of hydrogen ions. It is presumed that the luminous threshold voltage being sufficiently low for practical use results from that the continuous crystal structure in the pn-junction interface provides good rectification characteristic and the current injection efficiency is higher than the conventional one. (Example 3) An explanation will be made as for an example of a light emitting device having the structure shown in Fig. 2B manufactured in the explanatory process shown in Fig. 7. A device was prepared by following the procedure of Comparative Example 2 with the exception that the accelerating energy for the hydrogen ion implantation was boosted to 45 keV and the dose amount was doubled. Although it is difficult to clearly determine by a cross section observation, it is presumed that the n-type region extends to the inside of the monocrystalline substrate through the porous layer. When a DC current was conducted between the electrodes on the front and back surfaces of the wafer, the device indicated a rectification ratio being higher by nearly one order than the device of Comparative Example 2. The threshold voltage increased slightly to about 6 volts, but the luminous efficiency as obtained was several times stronger than that in Comparative Example 2. It is presumed that the improved rectification characteristic results from that the front and back regions of the pn-junction interface is formed of a perfect monocrystal and that this improves the efficiency of current injection into the luminous porous layer, thus increasing the luminous efficiency. (Comparative Example 3) An explanation will be made as for a Comparative example of a light emitting device having the structure shown in Fig. 2C manufactured in the step shown in Figs. 9A to 9C. A device was prepared by following the procedure of Comparative Example 1 with the exception that after a p-type epitaxial layer had been grown on an n-type monocrystalline substrate, boron ions were implanted into the surface thereof at an accelerating voltage of 20 keV with a dose of 5 x 10 14 cm -2 and the substrate was subjected to thermal annealing in a nitrogen atmosphere at 950 °C for 30 minutes to be activated. An observation of the cross section of a sample found that the anodization advances from the wafer surface up to about 1 µm depth to form a porous layer. In further detail observation, it was recognized that the surface was of a porous layer having large pores and a thickness of about 0.05 µm and the underlying lower porous layer was almost of a ultra-fine porous layer. When a DC current was conducted between the front and the back surfaces of the wafer, both the rectification characteristic and the luminous threshold voltage were substantially the same as those in Comparative Example 1 and the luminous efficiency was improved several times that in Comparative Example 1. In this case, it is considered that since the porous layer with large pore structure on the outer surface acts as the injection electrode layer 3 shown in Fig. 2C, the contact resistance with the extracting electrode is reduced so that the luminous efficiency is improved. (Comparative Example 4) An explanation will be made as for a light emitting device with the structure shown in Fig. 2C manufactured in the steps in Figs. 10A to 10D. A device was prepared by following the procedure of Comparative Example 1 with the exception that the following step was added between the RTO treatment to the porous layer and the CVD-SiO 2 layer deposition step. The added step includes removing the oxide film on the top surface of the porous layer with the oxidized surface of the residual structure, and then epitaxially growing a p-type silicon layer of 30 nm (300 Å) thickness by using a bias sputtering method in which a heavily doped p-type silicon target is used. In an observation of the cross section of a sample, innumerable defects including twins and dislocations were observed in the epitaxial silicon layer. However, it was confirmed that the crystal structure of the underlying porous layer was succeeded as an average structure. On conducting a DC current between the front and the back surfaces of the wafer, it was indicated that the rectification characteristic and luminous threshold voltage of the device was substantially the same as those in Comparative Example 1 and the luminous efficiency was improved several times that in Comparative Example 1. In this case, it is considered that since the epitaxial silicon layer on the surface acts as the injection electrode layer 3 shown in Fig. 2C the contact resistance with the extracting electrode is reduced so that the luminous efficiency is improved. (Comparative Example 5) An explanation will be made below as for a light emitting device with the structure shown in Fig. 2C formed in the steps shown in Fig. 11. A device was prepared by following the procedure of Comparative Example 3 with the exception that the following step was added after the porous layer forming step and the RTO treating step. The added step is a step of, after an oxide film had been removed, epitaxially growing, a p-type silicon layer of about 15 nm (150 Å) thick by using a bias sputtering method where a p-type silicon with a high concentration was used as a target. In an observation of the cross section of a sample, an ultra-thin layer of about 0.05 µm in depth in the top surface side of the porous layer was converted to a porous structure with coarse pores. It may be said that the epitaxial layer on the porous layer is nearly a monocrystal because a defect or the like was not found therein. It is considered that the improved crystallinity of the epitaxial layer results from that the epitaxial growth surface is a porous with coarse pores, compared with that in Comparative Example 4. On conducting a direct current between the front and back surfaces of the wafer of the above device, the rectification characteristics of the device was substantially the same as those in Comparative Example 3. The luminous threshold voltage was slightly increased, whereby the luminous efficiency was improved by about 50%. In this case, since the epitaxial layer on the top surface as well as the underlying porous layer with a coarse structure act as the injection electrode layer 3 shown in Fig. 2C, it is considered that the contact resistance of the take-out electrode is reduced so that the luminous efficiency is improved. (Comparative Example 6) The Comparative example of the light emitting device with the structure shown in Fig. 2C formed in the steps shown in Figs. 12A to 12D will be explained below. The same steps as in Comparative Example 2 were carried out except that after the hydrogen ion implanting step, the porous layer was subjected to a RTO treatment. After the oxide film on the top surface of the porous layer had been removed, an n-type silicon layer of about 20 nm (200 Å) was epitaxially grown by using a bias sputtering method in which a n-type silicon with a high concentration was used as a target. In an observation of the cross section of an observation sample, some defects including dislocations and twins in the epitaxial silicon layer were found. However, it was confirmed that the crystal structure was continued from the underlying porous layer as a whole. After it had been confirmed that the porous layer oxidized and with an increased PL efficiency is sufficiently stabilized, an about 200 nm (2000Å) thick SiO 2 film was again deposited on the surface of the wafer by using a CVD process. Using a conventional photolithography process, some openings of 2 x 2 mm 2 were formed in the oxide film. Moreover, a semi-transparent gold film of a thickness of 10 nm (100Å) was vapor-deposited in the openings to wire the take-out electrodes A1 derived from the openings. When a direct current was conducted between the electrodes on the back surface of the above wafer, the device produced by the above steps indicated a rectification characteristic in which a forward current flows to the surface electrode acting as a cathode electrode. An area light emission of nearly orange visible rays was emitted from the openings in the oxide film at a threshold voltage of about 2 volts. It is considered that this light emission is due to an electroluminescence based on a current injection to the porous silicon layer with the ultra-fine structure via the junction interface between the n-type epitaxial crystal layer and the underlying p-type porous layer. It is presumed that the sufficiently low luminous threshold voltage for practical use results from that the pn-junction interface has a continuous crystal structure and a good rectification characteristics and therefore the current injection efficiency is very high. (Example 4) An explanation will be made as for an example of a light emitting device having the structure shown in Fig. 2D produced in the forming steps shown in Fig. 13. The device was prepared by a method not according to the invention in the same manner as in the Comparative Example 6 except that before converting the surface of a p-type monocrystalline substrate into a porous structure, boron ions with a dose of 5 x 10 14 cm -2 were implanted to the surface thereof at an accelerating voltage of 20 keV. Then the implanted surface was activated by annealing in a nitrogen atmosphere at 950°C for 30 minutes. An observation of the cross section of a sample found that the ultra-thin layer of about 0.05 pm in the top surface side of the porous layer was in a porous state with bulky structure and that the epitaxial layer thereon included nearly no defects, and it can be stated that it is nearly a monocrystal. It is considered that the epitaxial layer having a crystallinity better than that in the Comparative Example 4 results from the epitaxially grown surface with bulky porous structure. On conducting a direct current between the electrodes on the front and back surfaces of the wafer, the rectification characteristics and luminous threshold voltage of the device were substantially the same as those in the Comparative Example 6 and the luminous efficiency was improved several times, compared with that in the Comparative Example 6. In this case, it is considered that the crystallinity of the n-type epitaxial silicon layer in the top surface reduced the contact resistance of the interface so that the luminous efficiency was improved. (Example 5) An explanation will be made as for an Example of a light emitting device having the structure shown in Fig. 3D explained in the forming steps of Figs. 14A to 14F, which are not in accordance with the method of the present invention. First, a SOI substrate having a boron-doped p-type silicon monocrystalline thin film with a face orientation of <100> and a thickness of 0.5 µm formed on a transparent quartz substrate was provided. The SOI substrate was subjected to the LOCOS process to form 10 x 10 µm 2 element separation regions. The surfaces of the separated silicon islands were oxidized to about 50 nm (500Å). Then with a stripe of 1.5 µm width being left at the middle portion of the island, boron ions accelerated at 150 keV were implanted with a dose of 2 x 10 15 cm -2 into the right region and phosphorus ions accelerated at 150 keV were implanted with a dose of 3 x 10 15 cm -2 into the left region. The substrate was subjected to a thermal annealing in a nitrogen atmosphere at 950 °C for 30 minutes to activate it. Next, aluminum wirings were formed in contact with the right and left ion implanted regions. Particularly, the wiring from the boron implanted region was wound to the orientation flat of the substrate. Then a conventional photoresist was coated on the surface of the substrate. An opening was formed in the non ion-implanted stripe region left at the middle area of the silicon island at the surface side. The end of the opening at the pn-junction side was offset so as to overlap slightly the inner side of the stripe region from the junction boundary. Then the oxide film on the surface in the opening was removed. The substrate was subjected to an anodizing process by immersing in a hydrofluoric acid-ethanol solution of a concentration of 25 wt·% while a direct current was conducted between a platinum plate electrode acting as a cathode facing the substrate and the aluminum wirings winding to the orientation flat of the substrate. The anodizing process was completed in 30 seconds while the anodizing current density was controlled at a fixed value of about 20 mA·cm -2 at the photoresist opening on the surface of the substrate. Then the photoresist was removed from the substrate. A SiNx film was deposited on the entire surface of the substrate by using a plasma CVD process. An opening was formed at a portion where the aluminum wiring was needed. An observation of the cross section of the device found that the 1.4 µm width stripe region at the middle portion of the silicon island became a porous structure. It seems probable that a predetermined intermediate layer with a width of less than about 0.1 µm is formed at the pn-junction boundary. On conducting a direct current between two electrodes sandwiching the porous region in the device, the device indicated its good rectification characteristics. A luminescence was recognized from a small applied voltage of about 1 volt. (Example 6) An explanation will be made below as for an Example of a light emitting device having the structure shown in Fig. 3D produced in accordance with the steps in Figs. 5A to 5C, which are not in accordance with the method of the present invention. First, an SIMOX substrate having a phosphorus-doped n-type silicon monocrystalline thin film with a face orientation of <100>, a resistivity of 20 Ω·cm, and a thickness of 0.5 µm formed on a buried oxide film of 300 nm (3000 Å) thick was provided. The SIMOX substrate was immersed in a hydrofluoric acid solution of a concentration of 49 wt·%. A photo-formation was carried out by irradiating a He-Ne laser beam focused in a rectangular shape of 2 x 8 µm 2 onto a part of the substrate surface for 30 minutes. Next, the substrate was subjected to the RTO process to stabilize the porous region. According to the same steps as those for manufacturing the device of Example 5, an ion implantation was performed to the two regions sandwiching the porous region to isolate electrically them. The element separation step using the LOCOS process activates the implanted ions. In this case, the phosphorus ion-implanted region was spaced from the porous region by 0.1 µm and the boron ion-implanted region was spaced from the porous region by 0.2 µm. Thus, the horizontal diffusion during an activation annealing was ceased at or just before the boundary of the porous region. An intermediate layer was formed between the boron implanted region and the porous region. Finally, aluminum wirings were derived out of both the ion implanted regions so that a device was completely formed. On conducting a direct current between two electrodes sandwiching the porous region in the device, it was indicated that this device has good rectification characteristics. It was ensured that a light emission occurred at a small applied voltage of about 1.5 volts. (Example 7) An explanation will be made below as for an example of driving a light emitting device drive by an electrical circuit which is, fabricated on the same substrate including the light emitting device shown in the Example 5, with reference to Figs. 16A to 16E and 17A to 17D. First, a SOI substrate having a boron-doped p-type silicon monocrystalline film 200 with a face orientation of <100>, a resistivity of 10 Ω·cm, and a thickness of 0.5 µm formed on an insulation surface of a silicon substrate 0 was provided (Fig. 16A). The substrate was subjected to an element isolation by using the LOCOS process to form island regions 20 each having an area of 10 x 10 µm 2 . A 50 nm (500Å) thick oxide film 7 was formed on the surface of each isolated silicon island by using a thermal oxidizing process (Fig. 16B). Next, a polycrystalline silicon film of 0.5µm thick was deposited on the surface of the oxide film 7 by using the LPCVD process. The polycrystalline silicon film was patterned through a conventional photolithography process so as to leave the 2 µm wide island region 8 (Fig. 16C). Then, with the photoresist acting as a patterned mask, phosphorus ions with a dose of 2 x 10 15 cm -2 accelerated at 180 keV were locally implanted to the polycrystalline silicon film island region 8 as well as the parts 10 and 10' of the silicon monocrystalline film island region 20 at the both sides of the region 8. Moreover, boron ions with a dose of 1 x 10 15 cm -2 accelerated at 100 keV were implanted to a part 30 of the silicon monocrystalline film island region 20 by using the above step (Fig. 16D). The impurities were activated by a thermal process at 900°C for 30 minutes. The oxide films on the surfaces of the regions 30 and 10' were removed, and then aluminum wirings 5 and 5' were taken out of the openings (Fig. 16E). Then the silicon oxide film 9 was deposited on the surface of the resultant substrate and the aluminum wiring 50 was taken out to conduct to the silicon monocrystalline film island region 9 (Fig. 17A). Next, the opening 100 was formed on a part of the upper part of the silicon monocrystalline film island 20 (Fig. 17B). The silicon nitride film 6 was formed so as to leave an opening of 1.5µm wide with a slight offset to the region 10 (Fig. 17C). Finally, the region 2 opened in the same way as that in the Example 11 was converted to a porous layer. A light emitting device which includes the regions 10 and 30 corresponding to the ion-implanted electrode regions 1 and 3 shown in Fig. 14F, the region 2 corresponding to the porous region 2 including a light emitting region, and the offset region corresponding to the intermediate region 2' was formed according to the above steps (Fig. 17D). The ion-implanted electrode region 1 acts as the drain region of a MOS transistor including the region 10' acting as a source part, the region 20 acting as a channel part, and the polycrystalline silicon film island region 9 acting as a gate electrode. With a voltage of 15 volts applied between the wirings 5 and 5', when the gate voltage was increased from 0 via the wiring 50, the MOS transistor was turned on at a threshold voltage 1.1 volts. It was confirmed that the porous region including a light emitting region glowed at 1.5 volts and more. The relationship between the luminous intensity and gate voltage indicated linear characteristics over 2 volts. When a rectangular waveform of 5 volts was applied to the gate of a MOS transistor from a shift register separately formed on the same substrate, the light emitting device can follow even at 20 MHz. The following features can be understood from the above explanations. A light emitting device according to the present invention has a device constitution comprising a non-porous region having a continuous crystal structure adjacent to the luminous region including a porous material and acting as a current injection electrode to the luminous region, whereby the perfect adhesive property between the electrode and the luminous region reduces the contact resistance. By differentiating the conductive types of the non-porous region and the luminous region from each other, a current injection from the junction portion could be injected with high efficiency. As a result, a light emitting device with excellent luminous efficiency and for a practical use can be provided as a whole device. According to the present invention, the light emitting device manufacturing method can provide light emitting devices with good luminous efficiency.

Claims: A light emitting device comprising a luminous region (2) comprising a porous semiconductor having a first conductivity type, a contact region (1) comprising a non-porous semiconductor having a second conductivity type and being electrically connected to the luminous region (2), and an electrode (5) provided at the contact region, the luminous region being light-emitting as a result of a current flowing into the luminous region through the contact region, characterized in that an intermediate region (2') comprising a non-porous semiconductor of a first conductivity type is provided between the luminous region (2) and the contact region (1) and that the current flows into the luminous region through the intermediate region (2'). The light emitting device according to claim 1, wherein the luminous region (2), the intermediate region (2') and the contact region (1) form successive layers. The light emitting device according to claim 1, wherein the luminous region (2), the intermediate region (2') and the contact region (1) are formed on the same substrate and are parallel to a surface of the substrate. The light emitting device according to claim 1, wherein the luminous region (2) and the intermediate region (2') comprise a p-type silicon and the contact region (1) comprises an n-type silicon. A method for manufacturing a light emitting device according to claim 2, comprising the steps of: epitaxially growing a p-type silicon layer (2, 2') on an n-type silicon substrate (1); causing a part of the p-type silicon layer (2) in the thickness direction to be made porous; and providing the n-type silicon substrate (1) and the p-type silicon layer (2) having been made porous with an electrode (5, 5'). The method according to claim 5, wherein the porous structure formation is conducted by anodization.

Inventors: KUMOMI HIDEYA, YONEHARA TAKAO, KUMOMI, HIDEYA, YONEHARA, TAKAO, KUMOMI, HIDEYA, C/O CANON KABUSHIKI KAISHA, YONEHARA, TAKAO, C/O CANON KABUSHIKI KAISHA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 1994
Main classification: H01L33
IPC codes: H05B33, H01L21, H01L33