Method and apparatus for preparing crystalline thin-films for solid-state lasers

Abstract: The present invention has been achieved by perceiving the fact to the effect that a semiconductor production process-like manner such as CVD method or the like by which materials and film thickness can be controlled in an atomic scale may be utilized in case of preparing thin-film crystal, and employing such semiconductor production process-like manner being quite different from conventional technique. The invention relates to preparation of crystalline thin-films for solid-state lasers wherein a substrate contained in a vessel under a high vacuum condition is heated, materials for forming the laser material are supplied onto the surface of the aforesaid substrate in the form of gas, ion, single metal or metal compound to grow crystal on the surface of the aforesaid substrate, and a material of active ionic species is supplied onto the surface of the aforesaid substrate simultaneously with supply of the aforesaid materials for forming the laser host crystal, thereby controlling valence number of the material of active ionic species so as to be identical with the valence number of the metal ion constituting the crystal of the aforesaid laser host crystal.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a method and an apparatus for preparing crystalline thin-films for solid-state lasers, and more particularly to a method according to the preamble of claim 1 and an apparatus according to the preamble of claim 6 for preparing crystalline thin-films for solid-state lasers by which such crystalline thin-films for solid-state lasers can be prepared which can be used for the development of micro-cavities and the like, and which enable growing of a solid-state laser directly on a semiconductor laser. Description of the Related Art Such a method and apparatus according to the preambles of claims 1 and 6, respectively, are known from the publication "RF Sputtering Crystal..." in JP Journal of Appl. Physics, vol. 23, no. 3, March 84, pages 312-316. DE-A-30 05 536 shows a laser emission element which is formed as a film of monocrystalline tin oxide and comprising lithium therein on a substrate. The laser emission film is formed by melting the respective materials all together in a single crucible, evaporating and depositing the constituents on the substrate. Recently, in order to respond to a variety of needs for shorter laser wavelength, expansion in wavelength band to be oscillated, higher laser output power, higher efficiency and higher beam quality and so on, extensive studies have been made with respect to research for novel solid-state laser materials, and higher quality in the solid-state laser crystals which have been heretofore known. Heretofore, solid-state laser crystals have been prepared by flux method, crystal pulling method or Verneuil's method and the like methods. These methods will be described in brief hereinbelow. [Flux Method] In this method, a crystal is deposited and grown from a molten material at a high temperature, and a molten inorganic salt or an oxide functions as its solvent. [Crystal Pulling Method] In this method, a seed crystal is dipped in molten liquid or saturated solution to be compatible with each other, and then the seed crystal is gradually pulled up to grow a single crystal on the extreme end portion of the seed crystal. [Verneuil's method] In this method, a raw material which has been finely pulverized is blown into a high temperature flame such as an oxyhydrogen flame and the like to heat and melt the raw material, and the molten material is received by a seed crystal so as to grow a single crystal thereon. As described above, in any of conventional methods, first a material to come to be solid-state laser crystal is molten at high temperatures, and then either a crystal is deposited and grown, or a single crystal is allowed to grow on the seed crystal. While the above described flux method, crystal pulling method or Verneuil's method and the like are very effective methods for preparing a large bulk crystal, it has been known that uniform dispersion of the active ionic species giving rise to the emission subject of a laser beam as a result of spatial control in laser host crystal, and prevention of inclusion of ionic species into laser host crystal giving rise to absorption of the laser beam are difficult. More specifically, since a solid-state laser crystal is allowed to grow in a rod-like shape in the prior art, temperatures become different in the central portion of the rod-like solid-state laser crystal from the peripheral portion thereof, and as a result conditions in diffusion of ion in both the portions had been different. Accordingly, it is difficult to effect uniformly doping of the active ionic species being come to be emission subject along the axial and diametrical directions of solid-state laser crystal. For this reason, uniform dispersion of active ionic species in the laser host crystal could not have been attained heretofore. Furthermore, since it is difficult to control the valence number of the ions to be doped as active ion species, there was such a case where the ion which had been doped did not become emission subject of laser beam, but became the ion species to come to be absorption subject of laser beam. For example, in such a case where Al 2 O 3 is used as laser host crystal, and doping is effected by using Ti as active ionic species, when Ti is trivalent, while it became emission subject, when Ti is di- or tetravalent, it became absorption subject. As described above, it was extremely difficult to control such valence number in the prior art. Moreover, as described above, while the prior art is preferable to prepare large bulk crystal, it is difficult to prepare thin-film crystal. Accordingly, it was difficult to control film thickness in an atomic scale. Besides, in the above described prior art, solid-state laser crystal is prepared by the manner quite different from semiconductor production process. Thus, it could not be allowed to grow solid-state laser crystal on a semiconductor substrate in a high-vacuum vessel containing the semiconductor substrate which is used for semiconductor production process. For this reason, solid-state laser crystals could not heretofore be produced in combination with semiconductors and semiconductor lasers. OBJECTS AND SUMMARY OF THE INVENTION In view of the various problems involved in the prior art, the present invention has been made by perceiving the fact to the effect that a semiconductor production process-like manner such as CVD (Chemical Vapor Deposition) method: (a material in gaseous form is used, and the gas is thermally decomposed on a substrate, whereby the material is deposited on the substrate.) by which the material and the film thickness can be controlled in an atomic scale, or the like method can be used in preparation of thin-film crystal. An object of the present invention is to provide a method and an apparatus for preparing crystalline thin-films for solid-state lasers in which a semiconductor production process-like manner quite different from the prior art is utilized and by which the above described problems involved in the prior art can be overcome. More specifically, an object of the present invention is to provide a method and an apparatus for preparing crystalline thin-films for solid-state lasers by which an active ionic species can be uniformly distributed into its laser host crystal. Furthermore, another object of the present invention is to provide a method and an apparatus for preparing crystalline thin-films for solid-state lasers by which valence number of active ionic species can be controlled. Still further, another object of the present invention is to provide a method and an apparatus for preparing crystalline thin-films for solid-state lasers by which film thickness can be controlled in an atomic scale. Yet further, another object of the present invention is to provide a method and an apparatus for preparing crystalline thin-films for solid-state lasers which can produce solid-state laser crystal in combination with semiconductor or semiconductor laser. It is to be noted that the semiconductor production process-like manner involves the above described CVD method used for growth of gallium arsenide and the like, MBE (Molecular Beam Epitaxy) method, ALE (Atomic Layer Epitaxy) method, Ablation Deposition Method and the like, and such manners wherein crystal is allowed to grow on a heated substrate as a result of supplying a material gas, or gaseous or beam-like molecule or ion onto the substrate are named generically as "semiconductor production process-like manner". The above objects are solved with a method, as claimed in claim 1, for preparing crystalline thin-films for solid-state lasers comprising the steps of: heating a substrate in a vessel under a high vacuum condition, supplying materials for forming the laser host crystal onto the surface of said substrate in the form of gas, ion, single metal or metal compound crystal growth on the surface of said substrate, and supplying a material of active ionic species onto the surface of said substrate simultaneously with supply of said materials for forming the laser host crystal, characterized in that said material of active ionic species is supplied separately and independent with respect to said supplying of said materials for forming the laser host crystal thereby allowing to control the valence number of the material of active ionic species so as to be identical with the valence number of a metal ion constituting said laser host crystal. The objects are further solved with an apparatus, as claimed in claim 6, for preparing crystalline thin-films for solid-state lasers comprising a vessel, the inside of which has been highly evacuated and is adapted for containing a substrate, the surface of which is subjected to crystal growth of crystalline thin-films for solid-state lasers, a heating device for heating said substrate, a laser host crystal supplying device for supplying materials for forming the laser host crystal onto the surface of said substrate contained inside said vessel in the form of gas, ion, single metal or metal compound, characterized in that a separate material of active ionic species supplying device is provided inside said vessel for supplying a material of active ionic species onto the surface of said substrate contained inside said vessel separately, independently, and simultaneously with said supply of said materials for forming the laser host crystal. According to the above described invention, a substrate is heated in a vessel under a high vacuum condition, and materials for forming laser host crystal are supplied in the form of gas, ion, single metal or metal compound onto the surface of the aforesaid substrate to grow crystal thereon. Accordingly, solid-state laser crystal can be grown on even a semiconductor substrate such as Si and the like other than seed crystal as in the case of a semiconductor production process-like manner. Moreover, since a material of active ionic species is supplied onto the surface of a substrate simultaneously with supply of materials for forming the laser host crystal, it is possible to control the valence number of the material of the active ionic species so as to be identical with the valence number of the metal ion constituting the crystal of the laser host crystal. Thus, a little defective solid-state laser crystal in which no absorption subject or a controlled small amount of absorption subject exists can be prepared. In addition to the above, it is easy to control film thickness in an atomic scale, and a material of active ionic species can uniformly be injected from a spatial point of view. BRIEF DESCRIPTION OF THE DRAWINGS The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus not limiting of the present invention, and wherein: Fig. 1 is an explanatory view, in sectional construction, illustrating the apparatus for preparing crystalline thin-films for solid-state lasers according to an embodiment of the present invention; Fig. 2 is a timing chart indicating the timing of supplying gas pulses onto the surface of a substrate; Fig. 3 is a graphical representation indicating dependency of number in gas supplying cycles for growth of Al 2 O 3 ; Fig. 4 is a graphical representation indicating a relationship between changes in temperature of a substrate and its growth rate; Fig. 5 is a graphical representation indicating a relationship between changes in temperature of a substrate and refractive indices at 632.8 nm; Fig. 6 is a table showing an example of a possible combination among materials of the laser host crystal, materials of the active ionic species and materials of the substrate in the case where Al 2 O 3 is formed as the laser host crystal; Fig. 7 is a table showing an example of a possible combination among materials of the laser host crystal, materials of the active ionic species and materials of the substrate in the case where Y 3 Al 5 O 12 is formed as the laser host crystal; Fig. 8 is a table showing an example of a possible combination among materials of the laser host crystal, materials of the active ionic species and materials of the substrate in the case where LiYF 4 is formed as the laser host crystal; and Fig. 9 is an explanatory view, in sectional construction, illustrating the apparatus for preparing crystalline thin-films for solid-state lasers according to another embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the method and apparatus for crystalline thin-films for solid-state lasers according to the present invention will be described in detail hereinbelow by referring to the accompanying drawings. Fig. 1 illustrates an example of the apparatus for crystalline thin-films for solid-state lasers according to the present invention and which comprises a cylindrical vessel 10 made of stainless steel, a connecting tube 12 which is connected with the vessel 10 and for supplying a metal material forming a laser host crystal into the vessel 10, a connecting tube 14 which is connected with the vessel 10 and for supplying an oxidizing agent or halogenating agent forming the laser host crystal into the vessel 10, a connecting tube 16 which is connected with the vessel 10 and for supplying a material of active ionic species into the vessel 10, an electromagnetic valve means 18 for opening and closing the connecting tube 12, an electromagnetic valve means 20 for opening and closing the connecting tube 14, an -electromagnetic valve means 22 for opening and closing the connecting tube 16, a quartz rod 24 disposed vertically in the vessel 10 in such that one end 24a of which is positioned outside the vessel 10, and a halogen lamp 26 for emitting infrared rays into the end 24a to heat a substrate 100 rest on the other end 24b of the quartz rod 24. Furthermore, the interior of the vessel 10 is in high vacuum condition as a result of evacuation of an order of 1.33 x 10 -5 Pa (10 -7 Torr) by means of a turbo-molecular pump (not shown). In the above described construction, such a case where titanium-sapphire (laser host crystal: Al 2 O 3 , active ionic species: Ti) thin films are prepared as crystalline thin-films for solid-state lasers on the substrate 100 being Si (100) substrate by the use of a material gas alternately supplying type CVD method as a semiconductor production process-like manner will be described. It is to be noted that a material such as Si (100), α-Al 2 O 3 or the like lattice constant of which matches with that of the laser host crystal may be used as the substrate 100. For example, in the case where α-Al 2 O 3 is used as the substrate 100, there is no trouble because α-Al 2 O 3 is the same material with that of the laser host crystal. While Si (100) is a material being different from that of the laser host crystal, both the lattice constants of these materials match with each other so that Si (100) can be used as the substrate 100. In this connection, since the present embodiment is one in which Al 2 O 3 is formed as the laser host crystal and Ti is used as the active ionic species, it is to be arranged in such that to the vessel 10 are delivered trimethylaluminum (TMA) as a metallic material for forming the laser host crystal through the connecting tube 12 by opening and closing the electromagnetic valve 18 means, N 2 O as an oxidizing agent for forming the laser host crystal through the connecting tube 14 by opening and closing the electromagnetic valve means 20, and Ti gas as the material of active ionic species through the connecting tube 16 by opening and closing the electromagnetic valve means 22, respectively. In this case, TMA, N 2 O and Ti gas are supplied into the vessel 10 as gas pulses in accordance with the following manner. Namely, TMA and N 2 O material gases are alternately jetted in every two seconds onto the substrate 100 placed on the vessel 10 for a gas jetting period of one second. More specifically, the TMA gas (or N 2 O gas) is supplied to the interior of the vessel 10 for one second to raise pressure of the TMA gas (or N 2 O gas), thereafter supply of the TMA gas and N 2 O gas is stopped for a period of two seconds, and the interior of the vessel 10 is evacuated by a turbo-molecular pump. Then, N 2 O gas (or TMA gas) is supplied for one second to elevate pressure of N 2 O gas (or TMA), thereafter supply of the TMA gas and N 2 O gas is stopped for a period of two seconds, and the interior of the vessel 10 is evacuated by the turbo-molecular pump. The treatment described herein is utilized as one cycle, and a prescribed number of times of this cycle is repeated. In this connection, one cycle requires six seconds. Furthermore, Ti gas being the active ionic species is supplied synchronously with the TMA gas. In addition, the substrate 100 is placed on the end 24b of the quartz rod 24, and is heated from the back thereof with infrared rays irradiated from the halogen lamp 26. In this case, a base pressure is in an order of 1.33·10 -5 Pa (1 x 10 -7 Torr) and the pressure in the vessel 10 at the time of introducing the gas was set at 2.7 x 10 -2 Pa (2 x 10 -4 Torr). Fig. 3 is a graphical representation indicating the dependency of the growth of the Al 2 O 3 film on Si (100) as the substrate 100 on the number of gas supplying cycles (thickness (a thickness of the thin film: nm) is plotted as ordinate and number of cycles as abscissa). As described above, both the pressures of TMA and N 2 O in the vessel 10 were set at 2.7·10 -2 Pa (2 x 10 -4 Torr) (pressure ratio is "TMA/N 2 O = 1"), and the temperature of substrate was 360°C (T sub = 360°C). It is understood from Fig. 3 that the Al 2 O 3 film thickness grows linearly at a rate of about 0.4 nm/cycle. More specifically, a thickness of the Al 2 O 3 film was proportional to the number of gas supplying cycles, and the growth rate was 0.4 nm/cycle. Furthermore, it was also found that as a result of XPS (X-ray photoelectron spectroscopy), a composition of the thin film had been stoichiometrically 2 : 3. Next, both the pressures of TMA and N 2 O in the vessel 10 were set at 2.7·10 -2 Pa (2 x 10 -4 Torr) as in the case described above, respectively, and a temperature of the substrate (T sub ) was changed. The results in this case were measured by a spectroscopic ellipsometer with respect to the thin films and refractive indices. Fig. 4 is a graphical representation indicating a relationship between growth rate of the thin film and temperature changes in the substrate in which the growth rate (speed of growth: nm/cycles) obtained by dividing film thickness with number of cycle is plotted as ordinate and changes in temperatures (°C) of the substrate (T sub ) as abscissa. Furthermore, Fig. 5 is a graphical representation indicating a relationship between refractive indices of the thin film and changes in temperatures of substrate in which refractive indices (n) at 632.8 nm are plotted as ordinate and changes in temperature (°C) of the substrate (T sub ) as abscissa. It is found from Fig. 4 that the growth rate is as low as 0.02 nm/cycle before the temperature reaches 320°C. In this case, the refractive indices were 1.6 - 1.7 which correspond to equal to or higher than the refractive index of amorphous Al 2 O 3 . At the higher substrate temperature of 360°C, the growth rate was 0.4 nm/cycle and the refractive index was 1.77, respectively. Moreover, timing at the doping of an active ionic species synchronizes with timing of the supply of TMA as shown in Fig. 2. According to this arrangement, trivalent Al is replaced by Ti so that the Ti to be doped may be made only trivalent or substantially trivalent. Figs. 6 through 8, inclusive, illustrate each example of possible combinations of materials for the laser host crystal, materials for the active ionic species, and materials for the substrate wherein Fig. 6 shows a case of forming Al 2 O 3 as the laser host crystal, Fig. 7 shows a case of forming Y 3 Al 5 O 12 as the laser host crystal, and Fig. 8 shows a case of forming LiYF 4 as the laser host crystal, respectively. In addition, Fig. 9 illustrates another embodiment of the apparatus for preparing crystalline thin-films for solid-state lasers according to the present invention wherein the corresponding component parts to those of Fig. 1 are represented by the same reference characters as those in Fig. 1, and explanation for the detailed construction and function thereof will be omitted. In the case where a single metal or a metal compound being the metallic material for forming laser host crystal as well as a material of active ionic species are in solid state at normal temperature, the apparatus for preparing crystalline thin-films for solid-state lasers as shown in Fig. 9 may be used for the sake of effecting evaporation by heating, or sputtering by means of laser, electron beam, and ion beam. In the apparatus for preparing crystalline thin-films for solid-state lasers shown in Fig. 9, the vessel 10 is provided with a window section 30 for introducing laser, whereby it is possible to irradiate the laser into the vessel 10 from the outside. Furthermore, the apparatus is constructed such that a holder 23 for supporting a single metal or a metal compound being the metallic material which forms a solid-state laser material at normal temperature as well as a material of active ionic species is located at a position to which is irradiated the laser in the vessel 10, and this holder 32 is rotatably driven by a motor through a magnetic coupling 34. In the above construction, the apparatus is arranged in accordance with the similar manner as that of the embodiment shown in Fig. 1 in such that into the vessel 10 is delivered TMA as a metallic material for forming the laser host crystal through a connecting tube 12 by opening and closing an electromagnetic valve means 18, and N 2 O as an oxidizing agent for forming the laser host crystal through the connecting tube 14 by opening and closing the electromagnetic valve means 20, besides Ti is attached to the holder 32, and the laser introduced from the window section 30 for introducing laser is irradiated to the Ti to heat the same while driving rotatively the holder 32 by means of the motor 36 through the magnetic coupling 34. Thus, the Ti attached to the holder 32 is sputtered off so that titanium-sapphire (laser host crystal: Al 2 O 3 , active ionic species: Ti) thin films can be formed on the substrate 100. Moreover, in also the case where a solid material is used as one for forming the laser host crystal, it may be arranged in such that a similar apparatus as in the above described case of Ti is further provided, and laser irradiation is effected to ablate the solid material. Although not specifically illustrated, electron beam or ion beam may be irradiated in place of the laser in the embodiment shown in Fig. 9, and in this case a source for electron beam or ion beam may be disposed directly on the interior of the vessel 10. While the metallic material for forming laser host crystal and the oxidizing agent or halogenating agent have been alternately supplied in the above described respective embodiments, the invention is not limited thereto, but the metallic material for forming laser host crystal may be supplied simultaneously with the oxidizing agent or halogenating agent without supplying them alternately. Furthermore, heating for the substrate 100 is not limited to heating by means of infrared rays, but resistance heating may be used and in this case, a heating coil may be formed on the substrate 100 to heat electrically the same. Moreover, it may be arranged in such that a laser is irradiated on the substrate 100 from the obliquely upper direction in the vessel 10 to heat the substrate 100. Since the present invention has been constructed as described above, the following advantages are obtained. The method for preparing crystalline thin-films for solid-state lasers according to the present invention is characterized by the steps of heating a substrate in a vessel under a high vacuum condition, supplying materials for forming the laser host crystal onto the surface of said substrate in the form of gas, ion, single metal or metal compound to grow crystal on the surface of said substrate, and separately supplying a material of active ionic species onto the surface of said substrate simultaneously with supply of said materials for forming the laser host crystal, thereby controlling valence number of the material of active ionic species so as to be identical with the valence number of the metal ion constituting the crystal of said laser host crystal in the laser crystal. Furthermore, the apparatus for preparing crystalline thin-films for solid-state lasers according to the present invention is characterized by being provided with a vessel the inside of which has been highly evacuated and adapted for containing a substrate, the surface of which is subjected crystal growth of crystalline thin-films for solid-state lasers, a heating device for heating said substrate, a laser host crystal supplying device for supplying materials for forming the laser host crystal onto the surface of said substrate contained inside said vessel in the form of gas, ion, single metal or metal compound, and a material of active ionic species supplying device for separately supplying a material of active ionic species onto the surface of said substrate contained inside said vessel simultaneously with supply of said materials for forming the laser host crystal. Because of the above described construction of the present invention, it is possible that a substrate is heated in a vessel under a high vacuum condition, materials for forming the laser host crystal are supplied onto the surface of the substrate in the form of gas, ion, single metal or metal compound to effect crystal growth on the surface of the substrate. Thus, it becomes possible to grow solid-state laser crystal on a semiconductor substrate made of Si and the like other than seed crystal as in the case of semiconductor production process-like manner. Furthermore, since a material of active ionic species is supplied onto the surface of the substrate simultaneously with supply of the materials for forming the laser host crystal, valence number of the material of active ionic species can be controlled so as to be identical with valence number of the metal ion constituting crystal of the laser host crystal, whereby a solid-state laser crystal being little defective in which no absorption subject or a controlled small amount of absorption subject exists can be prepared. Still further, it is easy to control a film thickness in atomic level, and a material of active ionic species can also be uniformly injected from spatial point of view.

Claims: A method for preparing crystalline thin-films for solid-state lasers comprising the steps of: heating a substrate in a vessel under a high vacuum condition, supplying materials for forming a laser host crystal onto the surface of said substrate in the form of gas, ion, single metal or metal compound by crystal growth on the surface of said substrate, and supplying a material of active ionic species onto the surface of said substrate simultaneously with supply of said materials for forming the laser host crystal, characterized in that said material of active ionic species is supplied separately and independent with respect to said supplying of said materials for forming the laser host crystal thereby allowing to control the valence number of the material of active ionic species so as to be identical with the valence number of a metal ion being included in said laser host crystal. A method for preparing crystalline thin-films for solid-state lasers as claimed in claim 1 wherein said materials for forming the laser host crystal are composed of a metallic material and an oxidizing agent or a halogenating agent, and said metallic material and said oxidizing or halogenating agent are alternately or simultaneously supplied onto the surface of said substrate. A method for preparing crystalline thin-films for solid-state lasers as claimed in claim 2 wherein said material of active ionic species is supplied onto the surface of said substrate simultaneously with supply of said metallic material. A method for preparing crystalline thin-films for solid-state lasers as claimed in claim 1 wherein a lattice constant of said laser host crystal matches with that of said substrate. A method for preparing crystalline thin-films for solid-state lasers as claimed in any one of claims 1, 2, 3 and 4 wherein in the case where a single metal or a metal compound being the metallic material for forming said laser host crystal as well as said material of active ionic species are in solid-state at normal temperature, these materials are supplied onto the surface of said substrate after evaporation of these materials by heating or sputtering or ablation of the materials by laser, electron beam or ion beam. An apparatus for preparing crystalline thin-films for solid-state lasers comprising a vessel (10), the inside of which has been highly evacuated and is adapted for containing a substrate (100), the surface of which is subjected to crystal growth of crystalline thin-films for solid-state lasers, a heating device (26) for heating said substrate a laser host crystal supplying device (14, 12) for supplying materials for forming the laser host crystal onto the surface of said substrate (100) contained inside said vessel (10) in the form of gas, ion, single metal or metal compound, characterized in that a material of active ionic species supplying device (16; 32) is separately provided inside said vessel for supplying a material of active ionic species onto the surface of said substrate contained inside said vessel separately, independently, and simultaneously with said supply of said materials for forming the laser host crystal. An apparatus for preparing crystalline thin-films for solid-state lasers as claimed in claim 6 wherein said laser host crystal supplying device (12, 14) is provided with a supplying device for supplying a metallic material for forming said laser host crystal and a supplying device for supplying an oxidizing agent or a halogenating agent. An apparatus for preparing crystalline thin-films for solid-state lasers as claimed in claim 7, wherein said material of active ionic species supplying device supplies said material of active ionic species onto the surface of said substrate simultaneously with supply of said metallic material onto the surface of said substrate by means of said supplying device for supplying a metallic material for forming said laser host crystal. An apparatus for preparing crystalline thin-films for solid-state lasers as claimed in claim 6, 7 or 8 further comprising a heating means for evaporating a single metal or a metal compound being the metallic material for forming said laser host crystal and said material of active ion species, both the materials being in solid-state at normal temperature. An apparatus for preparing crystalline thin-films for solid-state lasers as claimed in claim 6, 7 or 8 further comprising a sputtering means for sputtering off a single metal or a metal compound being the metallic material for forming said laser host crystal and said material of active ionic species, both the materials being in solid-state at normal temperature. An apparatus for preparing crystalline thin-films for solid-state lasers as claimed in claim 10 wherein said sputtering means is a means for effecting sputtering or ablation by laser, electronic beam or ion beam.

Inventors: KUMAGAI HIROSHI, TOYODA KOUICHI, KUMAGAI, HIROSHI, TOYODA, KOUICHI
Applicants: RIKAGAKU KENKYUSHO
Application year: 1994
Main classification: C30B25
IPC codes: B01J19, H01S5, H01S3, C30B25, C23C14, C23C16