METHOD AND APPARATUS FOR SEPARATING AND REMOVING LIQUID PARTICLES FROM MOLTEN METAL

Abstract: Molten metal (11) containing suspended liquid particles is passed preferably generally upwardly through a porous media (24) so constructed and arranged such that the movement of the molten metal (11) therethrough renders the suspended liquid particles gravity separable. The gravity separable liquid particles (34) rise upwardly or settle downwardly so as to be removable from said molten metal for subsequent removal therefrom. An associated apparatus is also provided.

Description: Method and Apparatus for Separating and Removing Liquid Particles from Molte Metal This invention relates to separating 5 and removing suspended liquid particles from molten metal by passing the molten metal containing the suspended liquid particles preferably generally upwardly through a porous media. The porous media is constructed and 10 arranged such that the movement of the molten metal therethrough renders the suspended liquid particles gravity separable. Molten metal, such as aluminum, including alloys containing over 50% aluminum, 15 has been treated to remove impurities therefrom. Some of these treatments, such as in furnace fluxing or in-line treatment, generate liquid particles, such as molten salts. Also, additions of salts are often made to furnaces to 20 reduce melt loss. A portion of these molten salts are carried along with the molten metal and, if not removed from the molten metal, can create "oxide patches" on the surface of the solidifying ingot. These oxide patches not only 25 adversely affect ingot quality but also many times have to be scalped off of the ingot, which results in a reduction of the recovery of metal in the ingot casting operation. Oxide patches can also cause ingots to crack. In some cases, the oxide patches are so prevalent that the entire ingot must be scrapped and remelted. This, of course, adds cost to the ingot casting operation. The liquid particles referred to, such as the molten salts, are in the micron size range, typically from less than 1 micron up to 80 or possibly 100 microns in size. The molten salts are usually MgCl 2 , NaCl, CaCl 2 , KC1, LiCl and mixtures thereof. The molten salts can also contain NaF, AlF j and CaF 2 originating from furnace additives or potroom metal. Most liquid salts are lighter than the molten metal and would be gravity separable but remain entrained or suspended largely because their small size results in an extremely slow rise velocity. Other than for their small size, the buoyant liquid particles would rise to the surface for removal by skimming or similar operations. There have been efforts to remove particles, such as solid and liquid inclusions, from molten metal. United States Patent No. 4,390,364 discloses a removal method comprising moving the molten metal containing suspended particles downwardly through a medium of submerged contacting surfaces such as a packed bed. The contacting medium has a high void fraction and a high specific surface area. The patent states that this results in coalescence or agglomeration of the suspended particles. After this, the molten metal is passed generally downwardly through inclined channels or passages. Buoyant particles and agglomerates collect on the underside of the inclined surfaces and typically move upward in a counter- flow relationship with the metal, where the metal moves laterally and downwardly through the inclined passages. These buoyant particles and agglomerates are removed by skimming or similar operations. United States Patent No. 4,790,873 • discloses a method of removing particles from molten metal by contacting the molten metal with a medium which retains metal-nonwettable inclusions and then passing the molten metal through a filter of metal-wettable material. The metal-wettable material of the filter retains the liquid particles therein. The filter containing the liquid particles is subsequently removed and replaced. Despite these known methods and apparatus, there remains a need for an improved method for separation and removal of liquid particles from molten metal. The invention has met the above- described need. In accordance with the invention, molten metal containing liquid particles suspended therein can be treated by passing the same through a porous media so constructed and arranged such that the movement of the molten metal therethrough renders the suspended liquid particles gravity separable. Preferably, the molten metal is passed generally upwardly through the porous media. In this way, the gravity separable liquid particles rise upwardly so as to be removable from the molten metal. In one aspect of the invention, the porous media is so constructed and arranged to facilitate coalescence of the suspended liquid particles on the porous media. The coalesced liquid particles are carried out of the porous media by sufficient molten metal velocity and by creating coalesced liquid particles having increased buoyancy over the original smaller suspended liquid particles. The porous media may also filter out some solid particles. In an embodiment of the invention, the porous media is made of a porous ceramic material which has preferably 10 to 60 pores per inch and more preferably 20 to 40 pores per inch. In another embodiment the porous media can have an upper portion and a lower portion, the lower portion having more pores per inch than the upper portion. In this way, the lower portion can facilitate coalescence of the liquid particles while the upper portion facilitates carrying away of the coalesced liquid particles out of the porous media. In yet another embodiment of the method, a filter can be provided downstream of the porous media to further capture remaining liquid and solid particles in the molten metal flowing through the filter. An associated apparatus is also provided which comprises a molten metal passageway having mounted generally horizontally therein a porous media arranged such that the molten metal passes generally upwardly through the porous media. The porous media is so constructed and arranged such that movement of the molten metal therethrough renders the suspended liquid particles gravity separable, whereby the gravity separable liquid particles rise upwardly to the upper surface of the molten metal. The molten metal passageway has an inlet portion upstream of the porous media and a settling zone downstream of the inlet portion. The settling zone has sufficient length in relation to molten metal velocity and depth of molten metal to allow the gravity separable liquid particles to float to the top surface of the molten metal in the settling zon<?. It is an object of the invention to remove liquid particles from molten metal before casting of the molten metal into ingots. It is a further object of the invention to provide a method and apparatus which creates gravity settlable liquid particles from liquid particles suspended in the molten metal. It is yet another object of the invention to provide a porous media which is constructed and arranged so as to facilitate coalescence of liquid particles therein for subsequent carrying out by the molten metal and ultimate removal from the molten metal surface by skimming or a like operation. It is still another object of the invention to provide a liquid particle removal method and apparatus that will result in increasing the useful lifetime of the bed filter and/or other filtration systems used in the casting process. These and other objects of the invention will be more fully understood from the following description of the invention with reference to the drawings appended hereto. Figure 1 is a top plan view depicting the operation of the improved system showing one arrangement suitable for practicing the invention. Figure 2 is a cross-sectional view taken along line 2-2 of Figure 1. Figures 3-6 are enlarged cross- sectional views of the porous media, in a time lapse sequence, showing the coalescing and subsequent release from the media of the liquid particles. Figure 7 is a schematic drawing showing a porous media * with an upper portion and a lower portion having different pore sizes. Figure 8 is a schematic view of two liquid inclusions, showing the difference between a wetting and a non-wetting surface. Figure 9 is a graph showing the terminal rise velocity as a function of the particle diameter. Figure 10 is a photomicrograph (lOOx) of an inclusion sample taken upstream of the porous media for the first example. Figure 11 is a photomicrograph (lOOx) of an inclusion sample taken downstream of the porous media for the first example. Figure 12 is a photomicrograph (lOOx) of an inclusion sample taken upstream of the porous media for the second example. Figure 13 is a photomicrograph (10Ox) of an inclusion sample taken downstream of the porous media for the second sample. The method and apparatus of the invention operates in association with the process of casting molten metal, such as aluminum and aluminum alloys, into ingots. As is well known to those skilled in the art, a source of aluminum is provided and melted in a furnace and then transferred to a holding furnace. The molten metal is then often subjected to a fluxing and/or filtering treatment. The filtering treatment removes entrained solid particles such as aluminum oxide particles and the fluxing treatment is used to remove dissolved hydrogen as well as lowering the content of metals such as sodium, calcium and magnesium. However, when chlorine or chlorine-containing reactants are used, the fluxing treatment can form liquid particles, such as molten salts e.g. MgCl 2 . A fraction of the molten salt in the melt can remain as a very finely divided suspension and can be difficult to remove or separate from the molten aluminum by flotation or gravity separation. That is, even though the molten salt may have a lower density than the aluminum, some remains entrained therein and can pass through the filtering system with the resulting imperfections in the cast aluminum ingot. Referring now to Figures 1 and 2, the improved liquid particle removal system includes a containment vessel 12 constructed or lined with a suitable refractory material in which the molten metal 11 is contained. The containment vessel 12 includes two sidewalls 13, 14 (Figure 1) as well as a floor 15 (Figure 2) . A lid (not shown) can be provided to cover the containment vessel 12. An inlet baffle 18 establishes an inlet leg 20 for the flow of molten metal (shown by the arrows in Figure 1 and 2) . A rigid porous ceramic media 24 is mounted generally horizontally in the containment vessel 12 such that the molten metal entering the inlet leg 20 is passed generally upwardly therethrough, as seen best in Figure 2. The containment vessel 12 further includes an outlet baffle 28 which establishes an outlet leg 30. The inlet baffle 18 and outlet baffle 28 define a settling zone 32 where the gravity separable liquid particles, shown in Figure 2 as coalesced liquid particle globules 34, are collected on the upper surface 35 of the molten metal 11. The settling zone 32 includes a floor 36 supported by walls 37 and 38 (Figure 2) mounted to the floor 15 of the containment vessel 12. A porous ceramic filter 40 is mounted generally horizontally in the floor 36 such that the molten metal in the settling zone area 32 passes generally downwardly therethrough. Referring more particularly to Figure 2, in operation, liquid particles 50, typically salt particles less than one micron to possibly fifty microns, are entrained in the molten metal 11 flowing in the inlet leg 20 upstream of the rigid porous ceramic media 24. As used herein, the term "liquid particles" also includes slurries of liquid particles and solids, the solids being less than about fifteen volume percent of the liquid particles. More generally, the term liquid particles means particles which are deformable to the shear forces experienced in conventional trough and filter arrangements. The liquid particles are typically lighter than the molten metal, but are not gravity separable and remain entrained or suspended largely because of the very low rise velocity caused by their small size. The liquid particles can include molten salts such as MgCl 2 , NaCl, CaCl 2 , KCl, LiCl and mixtures thereof. The molten salts can also contain fine solids, such as NaF, A1F 3 and CaF 2 originating from furnace additives or potroom metal. The fluorides, in addition to being solids, can also be dissolved in the molten salt. Furthermore, the liquid particles can be liquid metal phases insoluble in aluminum, such as Pb. As can be seen by the arrows in Figures 1 and 2, the molten metal 11 containing the liquid particles 50 passes generally upwardly through the rigid porous ceramic media 24. As will be explained in greater detail with respect to Figures ? to 6 below, as the liquid particles pass generally upwardly through the rigid porous ceramic media 24, the rigid porous ceramic media 24 renders the liquid particles gravity separable with the gravity separable liquid particles subsequently being released from the media 24. Once released, the liquid particle globules 34, due to their greater buoyancy and the generally upward molten metal flow velocity, float to the top surface 35 of the molten metal 11 in the settling zone 32 as shown in Figure 2. The liquid particle globules 34 are typically over 50 or 60 microns and as large as 1,000 microns or larger. From there, floating liquid particle globules 34 can be periodically collected and removed from the containment vessel 12 by skimming or other like operations. As can be seen in Figure 2, a small percentage of the liquid particles 62 may remain entrained in the molten metal 11 after it is passed through rigid porous ceramic media 24. This can be caused by the fact that some liquid particles may not be coalesced in the rigid porous ceramic media 24 and because, as will be discussed with respect to Figure 6, as the large coalesced particles are released from the rigid porous ceramic media 24, some smaller diameter droplets of liquid particles can be generated. This happens because in the release process, the film of the liquid particles is ruptured. In order to further remove these liquid particles 62, the molten metal containing these liquid particles optionally can be passed through the porous ceramic filter 40. Liquid particles 62 that remain trapped in the porous ceramic filter 40 can be removed when the filter 40 is replaced, which usually occurs after each casting of molten metai (one casting typically ranging from approximately 40,000 to 250,000 pounds of metal) . The porous ceramic filter 40 ■ can also capture remaining solid particles in the molten metal. Filter 40 can be similar to porous media 24. However, preferably, filter 40 has a greater number of pores per inch (see discussion hereinafter for the meaning of pores per inch) than media 24 to capture the smaller liquid particles that remain entrained in the molten metal 11 after the molten metal 11 is passed through media 24. As porous media 24 effects removal of substantially most of the liquid particles in the molten metal 11, filter 40 is usually not loaded by the liquid particles (as will be explained and shown with respect to Figures 4-6) and thus does not create globules of liquid particles that are released therefrom. Filter 40, thus, is used to capture liquid particles which remain entrained in the molten metal 11 after passing generally upwardly through porous media 24. The invention contemplates using the rigid porous ceramic media 24, which will render gravity separable substantially most of the liquid particles 50 entrained in the molten metal 11 while omitting the use of porous ceramic filter 40. It will be further appreciated that the containment vessel 12 could be configured such that the molten metal will also flow generally upwardly through the porous ceramic filter 40; however, this is not as preferred because this would mean that the settling zone 32 would be shorter (for the same containment vessel length) or the containment vessel size would have to be increased ( or the same settling zone length) . The rigid porous ceramic media 24 can be made of several types of materials such as, for example, ceramic foams, bonded ceramic particulate, porous carbon and glasses. The ceramic foam media can be produced by using a polyurethane precursor which is immersed in a ceramic slurry and then fired at a high temperature. During firing, the polymer precursor vaporizes leaving a sintered or fused ceramic media. The bonded ceramic particulate media consists of tabular ceramic media held together by a ceramic binder or by bonds formed by sintering without a binder. Rigid porous ceramic media is commercially available from various manufacturers such as Hi-Tech Ceramics, Inc. of Alfred, New York sold under the trade name Alucel™. These media are generally composed of mixtures of oxides such as alumina, zirconia and silica. The alumina filters, in particular, can be sintered or phosphate bonded. As is known to those skilled in the art, a standard measurement of pore size of a porous ceramic media is described by the number of pores per linear inch or PPI. The PPI of a specific media is determined, for foam media, from the original pore si∑c of the polyurethane foam used as the precursor. Although a variation in pore size can occur, an average PPI can usually be determined and since the pores are nearly spherical in shape, their size can be represented by an effective diameter. The pores sizes for the media used in the present invention are preferred to be in the range of about 10 to 60 PPI with 20 to 40 PPI being more highly preferred. Referring now to Figures 3 to 6, a detailed view of the operation of the rigid porous ceramic media 24 is shown. The molten metal 11 containing liquid particles 50 is passed generally upwardly through the media 24 (as indicated by the flow direction arrows) , and because the media 24 is wettable by the liquid particles 50, they can wet the media 24 as is shown by the stippled areas 70 on the media 24 in Figure 3. This wetting will continue until most of the media 24 is wetted as shown in Figure 4. Once this occurs, the liquid particles will start to move upwardly as a viscous liquid flow by virtue of the molten metal flow and will eventually gather on the upper surface of the media 24 as shown in Figure 5 by the retained coalesced liquid particles 75. This will continue until the surface effects of the coalescing liquid particles cause the coalesced particles to become buoyant and start to lose contact with the media 24 as shown by coalesced liquid particle globules 34 shown in Figure 6 and in Figures 1 and 2. The size of these coalesced liquid particle globules 34 is on the order of about 100 to 10,000 microns, with most being greater than 500 microns. At this size, the coalesced liquid particle globules 34 are gravity separable and then rise through the molten metal 11 in the settling zone 32. It can also be seen from Figure 6 that some smaller liquid particles, such as particles 62 (see also Figure 2) , can be released when the larger liquid particle globules 34 are released. This is believed to be because in the release process, the film of the liquid particles is ruptured which creates these smaller liquid particles 62. Nonetheless, the amount of such smaller liquid particles 62 is drastically reduced over the amount of smaller liquid particles 50 carried by the molten metal entering the system. Referring now to Figure 7, in another embodiment, the ceramic media can consist of an upper portion 90 and a lower portion 92, the upper portion having less average PPI (such as 10 to 20 PPI) than the lower portion (such as 30 to 40 PPI) . In this way, the liquid particles are captured more easily on the lower portion 92 for coalescence and subsequently the coalesced particles can pass more easily through the upper portion 90. As was mentioned above, the ceramic media is wettable by the liquid particles sought to be removed. One narrow test for determining whether a media is wettable or not involves heating the media to about 600-700°C. and pouring a heated liquid salt on the media. If the liquid salt beads on the media, the media is non-wettable. If the liquid salt does not bead, the media is wettable. In a narrower test, if the heated liquid salt is poured on a heated media and passes through or spreads (but does not bead) the media is also wettable. A more broad test involves measuring wettability as a function of the interfacial tensions (measured in dynes per centimeter) between the ceramic media, the molten salt and the molten aluminum. Figure 8 illustrates partially schematically the concept of wettability and non-wettability. The molten salt-solid substrate (in this case the ceramic media) interfacial tension is indicated by the variable γsl, the molten salt-molten aluminum interfacial tension is indicated by the variable γsv and the molten aluminum-solid substrate interfacial tension is indicated by γlv. If γsl is greater than γsv, then the angle θ, which is determined by the Young-Dupre equation cosθ = vsv - γsl γlv will be greater than 90° and the molten salt will be non-wetting toward the substrate. In this case, the molten salt will have no tendency to spread on the ceramic media surface but instead the molten aluminum will spread over the ceramic media in preference to the molten salt. If γsl is less than γsv, then θ will be less than 90° and the molten salt will be wetting toward the substrate and the molten salt, as opposed to the molten aluminum, will tend to spread over the ceramic media surface. The minimum length of the settling zone 32 (Figures 1 and 2) is determined to accommodate gravity settling of the liquid particles to the top surface of the molten metal 11 so that the coalesced liquid particle globules 34 can be skimmed or otherwise removed from the top surface of the molten metal. As can be seen on the graph shown in Figure 9, the larger the liquid particle globule diameter, the faster the rise velocity. Therefore, for larger particles the settling zone 32 (assuming constant width, depth and metal flow velocity) can be shorter in order for the liquid particle globules to rise to the top surface of the molten metal. Referring in more detail to Figure 9, the relationship between the particle diameter (measured in microns) plotted on he x-axis and the rise velocity of the particle (measured in cm/sec) plotted on thfc y-axis is shown. The values on this graph are calculated using Stokes Law, with the viscosity (n) of aluminum being equal to 1.2 cp and the density difference (pm- ps) between the aluminum and the liquid particle being 0.05 g/cπr . Figure 9 clearly shows that rise velocity increases substantially as the particle diameter becomes larger. As an example, assuming a coalesced liquid particle size of 1,000 μm, from Figure 9, the rise velocity will be 2.3 cm/sec. As the rise velocity increases, the coalesced liquid particles will need less distance in the molten metal flow direction to rise to the surface of the molten metal in the settling zone 32 (Figure 1) . While the foregoing description has emphasized the improvement as applied to treating molten aluminum, such is not necessarily intended to limit the scope of the improvement herein described which applies to the light metal magnesium and to other metals. While considerable emphasis has further been placed on passing the molten metal generally upwardly through the porous media and the liquid particles rising upwardly to the surface of the molten metal, the invention also encompasses passing the molten metal generally downwardly or generally laterally through the porous media and also encompasses the liquid particles being rendered gravity separable by sinking downwardly for subsequent removal from the molten metal passageway where the density of the particle phase is greater than the molten metal. EXAMPLES To demonstrate the concept, a test was rur with aluminum alloy 5182. A quantity of 10,000 lb of alloy was ' melted in a gas-fired furnace. Phosphate-bonded alumina foam media (30 PPI, 12"L x 12"W x 2"D) were used in both the upstream and downstream positions of a unit similar to Figure 1. The alumina foam media had 30 PPI. The metal in the furnace was heated to approximately 1350°F. At some given time, the plug was removed from the furnace taphole and metal flowed from the furnace into a connecting trough and then into the unit. As soon as metal flow was begun, molten salt of composition 70% MgCl -30% NaCl was semi-continuously poured onto the metal surface and stirred in for dispersal with a graphite stirrer, the additions being made immediately upstream of the unit. Initially, no liquid salt particles were observed on the metal surface in the unit or downstream of the unit. After twenty-eight minutes of operation, large releases of liquid salt particles floated to the metal surface above the upstream media. Regular releases of liquid salt particles occurred throughout the remainder of the test. These liquid salt particles could be skimmed off the metal surface at this point. The test continued for approximately 1 hour at a flowrate of 7,000 lb/hr. This test demonstrated that the salt added and dispersed upstream of the invention was coalesced in the first media, was released from the media in a coalesced state and then floated to the surface of the molten metal in the settling zone. The salt was not carried downstream of the first media, so it did not end up in the final product. Inclusions samples were taken both upstream of the first media 24 and downstream of the second media 40, to demonstrate its ability to remove salt. The procedure to take an inclusion sample was to pull molten aluminum, by a vacuum of approximately 25 in. of mercury, through a porous carbon disk. After approximately 0.5 to 1 kg of aluminum was passed through the porous carbon, the cartridge containing the porous carbon was removed from the metal being supplied and allowed to solidify. The porous carbon disk was then sectioned and examined metallographically. Any solid or liquid inclusion present in the metal were collected on the surface of the porous carbon disk. Figure 10 shows a photomicrograph of an inclusion sample taken upstream of the first media. The existence of round holes 101 in the metallic portion 100 of the sample, grey staining of the metal 102, and round rings 103 are the results of salt present in the sample. A portion of the carbon 104 from the inclusion sample cartridge can also be seen. The grey staining of the sample is the result of atmospheric moisture because of the hygroscopic nature of the salt present in the sample. Figure 11 shows a photomicrograph of an inclusion sample taken downstream of the second media. The metallic portion 110 is relatively clean with little, if any, salt 111 present. The voids 112 in the sample are solidification, shrinkage cavities and, in addition, some constituent phase 113 can also be seen. The carbon 114 from the inclusion sample cartridge is also present in Figure 11. No grey staining of the sample occurred, and round voids indicative of salt were not present. This metallographic analysis of inclusion samples indicates that the invention effectively remove salt particles from the stream of molten aluminum. In a second example, conditions were the same as the first example except mullite- bonded alumina media (1.5 in. thick) were used and the metal flowrate through the unit was 11,000 lb/hr. Releases of molten salt above the upstream media element were observed 19 minutes after salt additions upstream of the entire unit were begun. Figure 12 is a photomicrograph of an inclusion sample taken upstream of the unit. The metallic portion 140 contains evidence of salt due to the condensed droplets of water 141 and the grey staining 142. Constituent metallic phase 143 and shrinkage cavities 144 are also present as well as the carbon 145 from the inclusion sample cartridge. Figure 15 shows a photomicrograph of an inclusion sample taken downstream of the second media. Once again, there is little or no evidence of the presence of salt in the metallic portion 150. Constituent metallic phase 151 and shrinkage cavities 152 as well as the carbon 153 from the inclusion sample is shown. The photomicrographs in Figures 10-13 show that the apparatus and the method of the invention are effective for removing molten salts from molten aluminum. While it will be appreciated that the examples have shown removal of molten salts from molten aluminum, the invention is not limited to molten aluminum and can be used with other light molten metals such as magnesium. While the invention has been described in terms of preferred embodiments, the claims appended hereto are intended to encompass all embodiments which fall within the spirit of the invention.

Claims: C L A I M S 1. A method of treating molten metal containing suspended liquid particles, said method comprising: passing said molten metal containing said liquid particles through a porous media so constructed and arranged such that said movement of said molten metal therethrough renders said suspended liquid particles gravity separable, whereby said gravity separable liquid particles rise upwardly or settle downwardly so as to be removable from said molten metal. 2. The method of claim 1, wherein said porous media is wettable by said suspended liquid particles. 3. The method of claim 1, wherein said porous media is made of materials selected from the group of oxides of alumina, zirconia and silica. 4. The method of claim 1, wherein said porous media contains phosphate bonded alumina. 5. The method of claim 1, wherein said porous media contains sintered alumina. 6. The method of claim 1, wherein said porous media has an average of between about 10 to 60 pores per inch. 7. The method of claim 6, wherein said porous media has an average of between about 20 to 40 pores per inch. 8. The method of claim 1, wherein said porous media has an upper portion and a lower portion, said upper portion having less average pores per inch than the average pores per inch of said lower portion. 9. The method of claim 8, wherein said upper portion has about 10 to 20 pores per inch and said lower portion has about 30 to 40 pores per inch. 10. The method of claim 1, wherein said molten metal is contained in a molten metal passageway having an inlet portion upstream of said porous media and a settling zone downstream of said inlet portion; and said settling zone having sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to the top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 11. The method of claim 10, including after passing said molten metal through said porous media, passing said molten metal through a filter media to capture suspended liquid particles remaining in said molten metal. 12. The method of claim 1, including after passing said molten metal through said porous media, passing said molten metal through a filter media to capture suspended liquid particles remaining in said molten metal. 13. A method of treating molten metal containing suspended liquid particles, said method comprising: passing said molten metal containing said liquid particles generally upwardly through a porous media so constructed and arranged such that said movement of said molten metal therethrough renders said suspended liquid particles gravity separable, whereby said gravity separable liquid particles rise upwardly so as to be removable from said molten metal. 14. The method of claim 13, wherein said porous media is wettable by said suspended liquid particles. 15. The method of claim 13, wherein said porous media is made of materials selected from the group of oxides of alumina, zirconia and silica. 16. The method of claim 13, wherein said porous media contains phosphate bonded alumina. 17. The method of claim 13, wherein said porous media contains sintered alumina. 18. The method of claim 13, wherein said porous media has an average of between about 10 to 60 pores per inch. 19. The method of claim 18, wherein said porous media has an average of between about 20 to 40 pores per inch. 20. The method of claim 13, wherein said porous media has an upper portion and a lower portion, said upper portion having less average pores per inch than the average pores per inch of said lower portion. 21. The method of claim 20, wherein said upper portion has about 10 to 20 pores per inch and said lower portion has about 30 to 40 pores per inch. 22. The method of claim 13, wherein said molten metal is contained in a molten metal passageway having an inlet portion upstream of said porous media and a settling zone downstream of said inlet portion; and said settling zone having sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to the top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 23. The method of claim 22, including after passing said molten metal through said porous media, passing said molten metal through a filter media to capture suspended liquid particles remaining in said molten metal. 24. The method of claim 13, including after passing said molten metal through said porous media, passing said molten metal through a filter media to capture suspended liquid particles remaining in said molten metal. 25. A method of treating molten metal containing suspended liquid particles, said method comprising: passing said molten metal containing said suspended liquid particles generally upwardly through a porous media so constructed and arranged to facilitate coalescence of said suspended liquid particles on said porous media; and carrying said coalesced liquid particles out of said porous media by sufficient molten metal velocity and ry creating coalesced liquid particles having increased buoyancy over said suspended liquid particles. 26. The method of claim 25, wherein said porous media is wettable by said suspended liquid particles. 27. The method of claim 25, wherein said porous media is made of materials selected from the group of oxides of alumina, zirconia and silica. 28. The method of claim 25, wherein said porous media contains phosphate bonded alumina. 29. The method of claim 25, wherein said porous media contains sintered alumina. 30. The method of claim 25, wherein said porous media has an average of between about 10 to 60 pores per inch. 31. The method of claim 30, wherein said porous media has an avenge of between about 20 to 40 pores per inch. 32. The method of claim 25, wherein said porous media has an upper portion and a lower portion, said upper portion having less average pores per inch than the average pores per inch of said lower portion. 33. The method of claim 32, wherein said upper portion has about 10 to 20 pores per inch and said lower portion has about 30 to 40 pores per inch. 34. The method of claim 25, wherein said molten metal is contained in a molten metal passageway having an inlet portion upstream of said porous media and a settling zone downstream of said inlet portion; and said settling zone having sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to the top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 35. The method of claim 34, including after passing said molten metal through said porous media, passing said molten metal through a filter media to capture suspended liquid particles remaining in said molten metal. 36. The method of claim 25, including after passing said molten metal through said porous media, passing said molten metal through a filter media to capture suspended liquid particles remaining in said molten metal. 37. A method of treating molten metal containing suspended liquid particles, said method comprising: passing said molten metal containing said liquid particles generally upwardly through a porous media having an average of between 10 to 60 pores per inch such that said suspended liquid particles are rendered gravity separable, whereby said gravity separable liquid particles rise upwardly so as to be removable from said molten metal. 38. The method of claim 37, wherein said porous media has an average of between 20 to 40 pores per inch. 39. A method of removing liquid particles suspended in molten metal, said method comprising: passing said molten metal containing said suspended liquid particles generally upwardly through a porous media so constructed and arranged such that movement of said molten metal therethrough renders said suspended liquid particles gravity separable, whereby said gravity separable liquid particles rise upwardly to an upper surface of said molten metal; and periodically collecting and removing said gravity separable liquid particles from said upper surface of said molten metal. 40. The method of claim 39, wherein said removing step includes skimming said molten metal including said gravity separable liquid particles from said upper surface of said molten metal. 41. A method of treating molten metal containing suspended liquid particles comprising: passing said molten metal containing said liquid particles generally upwardly through a porous media so constructed and arranged such that said movement of said molten metal therethrough renders said suspended liquid particles gravity separable so that said gravity separable liquid particles can rise upwardly; moving said molten metal containing said gravity separable liquid particles generally horizontally through a settling zone wherein said gravity separable liquid particles rise to the top surface of said molten metal so as to be removable from said molten metal; and passing said molten metal generally downwardly through a filter media to capture suspended liquid particles that do not rise to the top surface of said molten metal in said settling zone. 42. The method of claim 41, wherein said settling zone has sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to said top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 43. A method of treating molten metal comprising: treating said molten metal with a chlorinaceous substance, said treatment creating liquid salt particles; passing said molten metal containing said liquid salt particles generally upwardly through a porous media so constructed and arranged such that said movement of said molten metal therethrough renders said suspended liquid particles gravity separable so that said gravity separable liquid particles can rise upwardly; moving said molten metal containing said gravity separable liquid particles generally horizontally through a settling zone wherein said gravity separable liquid particles rise to the top surface of said molten metal so as to be removable from said molten metal; and passing said molten metal generally downwardly through a filter media to capture suspended liquid particles that were not made gravity separable by said porous media. 44. The method of claim 43, wherein said settling zone has sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to said top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 45. An apparatus for treating molten metal containing suspended liquid particles comprising: a molten metal passageway; and a porous media mounted generally horizontally in said passageway such that said molten metal passes generally upwardly through said porous media; said ^ porous media so constructed and arranged such that movement of said molten met therethrough renders said suspended liquid particles gravity separable, whereby said gravity separable liquid particles rise upwardly to the upper surface of said molten metal. 46. The apparatus of claim 45, wherein said porous media is wettable by said liquid particles. 47. The apparatus of claim 45, wherein said porous media is made of materials selected from the group of oxides of alumina, zirconia and silica . 48. The apparatus of claim 45, wherein said porous media contains phosphate bonded alumina. 49. The apparatus of claim 45, wherein said porous media contains sintered alumina. 50. The apparatus of claim 45, wherein said porous media has an average of between about 10 to 60 pores per inch. 51. The apparatus of claim 50, wherein said porous ceramic media has an average of between about 20 to 40 pores per inch. 52. The apparatus of claim 45, wherein said porous media has an upper portion and a lower portion, said upper portion has less average pores per inch than the average pores per inch of said lower portion. 53. The apparatus of claim 52, wherein said upper portion has an average of about 10 to 20 pores per inch and said lower portion has an average of about 30 to 40 pores per inch. 54. The apparatus of claim 45, wherein said molten metal passageway has an inlet portion upstream of said porous media and a settling zone downstream of said inlet portion; and said settling zone having sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to the top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 55. The apparatus of claim 54, including a filter media positioned downstream of said porous media to capture suspended liquid particles remaining in said molten metal after said molten metal is passed through said porous media. 56. The apparatus of claim 45, including a filter media positioned downstream of said porous media to capture suspended liquid particles remaining in said molten metal after said molten metal is passed through said porous media. 57. An apparatus for treating molten metal containing suspended liquid particles comprising: a molten metal passageway; and a porous media mounted generally horizontally in said passageway; said porous media constructed and arranged such that said molten metal passes generally upwardly through said porous media; and said porous media having an average of between about 10 to 60 pores per inch. 58. The apparatus of claim 57, wherein said porous media has an average of between about 20 to 40 pores per inch. 59. The apparatus of claim 57, wherein said porous media has an upper portion and a lower portion, said upper portion has less average pores per inch than the average pores per inch of said lower portion. 60. The apparatus of claim 59, wherein said upper portion has an average of about 10 to 20 pores per inch and said lower portion has an average of about 30 to 40 pores per inch. 61. The apparatus of claim 57, wherein said molten metal passageway has an inlet portion upstream of said porous media and a settling zone downstream of said inlet portion; and said settling zone having sufficient length in relation to the velocity of the molten metal in said settling zone and the depth of said settling zone to allow said gravity separable liquid particles to float to the top surface of said molten metal in said settling zone as said molten metal moves through said settling zone. 62. The apparatus of claim 61, including a filter media positioned downstream of said porous media to capture suspended liquid particles remaining in said molten metal after said molten metal is passed through said porous media. 63. The apparatus of claim 57, including a filter media positioned downstream of said porous media to capture suspended liquid particles remaining in said molten metal after said molten metal is passed through said porous media.

Inventors: APELIAN DIRAN, DEYOUNG DAVID H, MUTHARASAN RAJAKKANNU, APELIAN, DIRAN, DEYOUNG, DAVID, H., MUTHARASAN, RAJAKKANNU
Applicants: ALUMINUM CO OF AMERICA, APELIAN DIRAN, DEYOUNG DAVID H, MUTHARASAN RAJAKKANNU, ALUMINUM COMPANY OF AMERICA, APELIAN, DIRAN, DEYOUNG, DAVID, H., MUTHARASAN, RAJAKKANNU
Application year: 1994
Main classification: C22B9
IPC codes: B01D17, C22B9, C22B21