Rapid plasma hydrogenation process for polysilicon MOSFET's

Abstract: A method for rapid plasma hydrogenation of semiconductor devices is provided in which the hydrogenation is conducted in two steps, the first step being conducted at a hydrogenation temperature that is higher than the out-diffusion temperature at which a substantial amount of hydrogen diffuses out of said semiconductor device; and in the second step, the semiconductor device is cooled to a temperature at which out-diffusion is substantially avoided while the hydrogenation plasma is maintained.

Description: BACKGROUND OF THE INVENTION This invention relates to a method of manufacturing a semiconductor device in which a layer of polysilicon is deposited and patterned on a major surface of a body, after which an insulating layer is formed at said polysilicon and a hydrogen plasma and heating treatment is performed to passivate polysilicon grain boundaries and interface traps. Such methods are particularly important for the manufacture of devices such as charge-transfer devices and insulated gate field-effect transistor circuits in which electrodes are formed on the insulating layer and serve to control the passage of charge carriers in the underlying portion of the polysilicon by capacitance coupling across the insulating layer. Liquid crystal display devices are now widely used. The performance of such display devices is influenced by the characteristics of thin film transistor ("TFT") components making up the display. It is known that the characteristics of the TFT may be greatly improved by the hydrogenation of polycrystalline silicon which is used to make the TFT. Plasma hydrogenation is the critical fabrication step in fabricating high performance polysilicon MOSFETs or TFTs. Such devices as shown in Figure 1 are treated by plasma hydrogenation to improve device characteristics as illustrated in Figure 2. However, normal plasma hydrogenation is a slow process which adds to the expense of and generates greater inefficiency in the manufacturing process. For example, typically the hydrogenation time is inversely proportional to the hydrogenation temperature, i.e. the higher the temperature at which hydrogenation is conducted, the shorter the hydrogenation time. However, this time temperature relationship can only be utilized to a limited extent because at a certain elevated temperature the device starts to lose hydrogen through out-diffusion and the performance characteristics of the device are degraded. As a result, the process has been limited to temperatures below the out-diffusion temperature and this leads to long hydrogenation times. SUMMARY OF THE INVENTION An object of this invention is to provide a method mentioned before in which the hydrogenation time is substantially shortened. Another object of the invention is to provide a process for the manufacture of polysilicon thin film transistors (MOSFETs) in which the hydrogenation time is substantially shortened and the efficiency of the manufacturing process is markedly improved. These and other objects are attained, according to the present invention, by a method in which said hydrogen plasma and heating treatment is carried out in two steps, whereby in the first step in-diffusion of atomic hydrogen from the plasma into the polysilicon is effected at a temperature in the range of 435°C to 800°C at which also a substantial out-diffusion of hydrogen from the polysilicon takes place and whereby in the second step while maintaining said hydrogen plasma the body is cooled to a temperature within the range of 25°C to 375°C at which out-diffusion of hydrogen from the polysilicon is substantially avoided. More specifically, we have found a new method for plasma hydrogenation that consists of two steps (referred to as the "Hi/Lo Process") and by which the process time may be substantially shortened when compared to the conventional continuous process. In its specific embodiments, employing the equipment presently available, in the first step for example, the plasma hydrogenation may be effected at a temperature within the range of 400°C to 800°C, preferably at temperatures of about 435°C or higher for a period of about 30 minutes or less depending on the temperature. Thereafter, the semiconductor body, while still in the presence of the hydrogen plasma may be permitted to cool or is cooled to a temperature within the range of about 25°C to 375°C over a period of time that may vary as desired but is preferably 30 minutes or less. It has been found that the high temperature step increases the diffusion of atomic hydrogen into the polysilicon and leads to rapid hydrogenation of the device. There is no dehydrogenation due to the presence of the hydrogen plasma. During the second step with the hydrogen plasma still on, the temperature is lowered or cools to a level (for example, to 325°C) at which no dehydrogenation can occur even after the hydrogen plasma is shut off or removed. It has been found that dehydrogenation starts at some point between about 350°C and about 375°C in both nitrogen and hydrogen ambients degrading device performance. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a diagrammatical, sectional view showing a TFT of the invention; Fig. 2 is a graph showing the drain current (in log scale) vs. gate voltage of an unhydrogenated and hydrogenated polysilicon TFT; Fig. 3 is a graph showing a variation of drain current for a TFT obtained by two-step process of the invention compared to a TFT obtained by a single step process at different temperatures; Fig. 4 is a graph showing the same device as in Fig. 3 except that the variation in drain current is in linear scale. Fig. 5 is another graph showing a variation of drain current for a TFT obtained by the two-step process of the invention compared to a TFT obtained by a single step process at different temperatures; Fig. 6 illustrates the same device as in Fig. 5 except that the variation in drain current is in linear scale; Fig. 7 is another graph showing a variation of drain current versus gate voltage for a device hydrogenated with the two-step process of the invention compared to a TFT obtained by a single step process; Fig. 8 is another graph showing a variation in the drain current versus gate voltage for a device hydrogenated with the two-step process of the invention and the same device after an anneal in a nitrogen atmosphere; Fig. 9 shows the same device as illustrated in Fig. 8 except that this variation in drain current is in linear scale; Fig. 10 is another graph showing the drain current versus gate voltage for a device comprising a back light shield and hydrogenated with the two-step process of the invention; Fig. 11 is a graph showing the drain current versus gate voltage for a device comprising a back light shield and hydrogenated in a one-step continuous process; Fig. 12 is a graph illustrating the effect of hydrogenation time in a continuous process on device characteristics of 32µm/32µm TFTs with 500A° channel polysilicon; Fig. 13 is a comparison of device characteristics for TFTs with 500A° and 1000A° polysilicon after 1 hour of plasma hydrogenation in a continuous process; Fig. 14 is a comparison of the device characteristics of the device of Fig. 13 for TFTs with 500A° and 1000A° polysilicon after 5 hours of continuous plasma hydrogenation; Fig. 15 is a graph of the effect of device size after 1 hour of hydrogenation in a continuous process on the characteristics of TFTs with channel polysilicon thickness of 1000A° and device sizes of 12µm/12µm, 32µm/32µm, and 50µm/50µm; Fig. 16 is a graph of the effect of the device size after 5 hours of hydrogenation in a continuous process on the characteristics of TFTs with channel polysilicon thickness of 1000A° and device sizes of 12µm/12µm, 32µm/32µm, and 50µm/50µm; Fig. 17 is an illustration of the possible paths for hydrogen transport to channel polysilicon; Fig. 18 is a comparison of device characteristics of 32µm/32µm TFT fabricated on nitride coated quartz substrate to that fabricated on quartz with no nitride coating. Both TFTs had 1000A° channel polysilicon; Fig. 19 illustrates results of experiments with quartz layers on top of TFTs. Fig. 20 illustrates the relationship between subthreshold slope and hydrogenation time for 32um/32um devices, hydrogenated in a one-step process at 275°C and having thickness of channel polysilicon of 1000A°. Fig. 21 is a graph of the variation of drain current (in log scale) with Gate Voltage for the 2-step hydrogenation process of the invention (435°C Hi/Lo, 30 minutes at 435°C followed by 30 minutes with temperature lowered from 435°C to 325°C) vs different single step hydrogenation processes done at different temperatures (250°C, 325°C, 375C°, 400°C, and 435°C) and in which the total hydrogenation time in all cases was 60 minutes; and Fig. 22 is the same as Fig. 21 except that the variation in the Drain Current is in linear scale. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS With reference to the drawings, in Fig. 1, there is illustrated according to the invention a polysilicon MOSFET or TFT 10 provided by methods well known in the art. Polysilicon TFTs were fabricated on a quartz substrate 1. The basic steps for fabricating the TFTs were (1) deposition and patterning of the channel polysilicon 2; (2) gate oxidation of the polysilicon at 1050°C in dry oxygen to form the gate oxide 3; (3) deposition and doping of 5000A° polysilicon for the polygate 4, followed by patterning of this layer; (4) ion implantation of the source 5 and drain 6 regions to form self-aligned gates, (5) deposition and densification of CVD oxide to form the crossover dielectric 7, (6) opening of the contact holes 8 to the source and drain; and (7) deposition and patterning of metal, for example aluminum 9 for interconnection to the source and drain. Fig. 1 shows a cross section of the TFT. After fabrication, the TFTs were subjected to a hydrogen plasma. Fig. 2 illustrates the improved characteristics of a device processed according to the invention when compared to an unhydrogenated device. Most of the hydrogenations discussed herein were conducted in a parallel plate reactor commercially available as Plasma Therm PT-73 although any suitable plasma system may be used. Most, if not all, of the hydrogenations described herein to determine the mechanism of the hydrogenation were conducted in a Plasma Therm 730. As discussed hereinabove, in order to circumvent the problem of the lengthy prior art process, we have invented a new method for plasma hydrogenation. This new process consists of 2 steps. In the first step, the plasma hydrogenation is done at a high temperature (preferably 435°C or higher). In the second step, the temperature is lowered from the high temperature to a lower temperature (preferably to 325°C) without shutting off the hydrogen plasma. The high temperature step increases the diffusion of the hydrogen into the polysilicon 2 and leads to rapid hydrogenation of the entire device. There is no dehydrogenation due to the presence of the hydrogen plasma. During the second step with the hydrogen plasma still on, the temperature is lowered to a level (for example to 325°C) at which no dehydrogenation can occur even after the hydrogen plasma is shut off. This 2-step Hi/Lo process was run in a Plasma Therm PT-73 parallel plate reactor using the following parameters: 500 watts @ 13.56 MHz 110 mTorr of pressure 45 sccm hydrogen 435°C for 30 minutes followed by 30 minutes being cooled to 325°C Total time = 60 minutes This process is compared with the single step (one temperature) continuous process with all process parameters identical other than temperature. The parameters of the invention were tested in a series of experiments in which a semiconductor device having the structure illustrated in Fig. 1 was produced, hydrogenated as indicated, and its characteristics tested and plotted as illustrated in the figures. Hydrogenation experiments were performed with both P and N channel TFTs. For the sake of consistency only p-channel devices were used for most of the results reported below. However experiments with n-channel devices showed that their behavior is similar. Additionally, as suitable plasma, instead of pure hydrogen, mixtures of hydrogen in nitrogen and/or argon may also be employed. For the experiments illustrated in the figures, in the experiments illustrated in Figs. 3 and 4, TFT devices were hydrogenated in a 2-step hydrogenation process (435°C Hi/Lo, 30 minutes at 435°C followed by 30 minutes with temperature lowered from 435C to 325°C) versus different continuous single step hydrogenation processes done at different temperatures (250°C, 325°C, 375°C, 400°C, and 435°C). Total hydrogenation time in all cases was 60 minutes. It will be seen that the 2-step hydrogenation process results in superior device characteristics when compared to any of the single step hydrogenation processes. In Figs. 5 and 6, TFT devices were hydrogenated in the 2-step hydrogenation process (435°C Hi/Lo, 15 minutes at 435°C to 325°C) versus different single step, (continuous) hydrogenation processes done at different temperatures (250°C, 325°C, 375°C, 400°C, and 435°C). Total hydrogenation time in all cases was 30 minutes. It will be seen that the 2-step hydrogenation process results in superior device characteristics when compared to any of the single step hydrogenation processes. In Fig. 7, a device was hydrogenated with the 2-step hydrogenation process (435°C Hi/Lo, total time = 60 minutes) and compared with a single step hydrogenation process (325°C cont., 5 hours). This shows that the shorter time 2-step hydrogenation process produces devices with characteristics that are equivalent to those devices produced by the long hydrogenation time with the single step process. In Fig. 8, a device was hydrogenated with the 2-step hydrogenation process (435°C Hi/Lo, 60 minutes) and the same device measured after N 2 anneal at 435°C for 15 minutes. In this step, the plasma is shut off and the device is allowed to sit in the reactor for the designated period of time at the indicated temperature. It will be seen that the nitrogen anneal results in a loss of hydrogen and degrades the device. From the experimental results illustrated in Figures 3 to 6, it can be clearly seen that for a fixed hydrogenation time, decidedly better results are obtained with the 2-step hydrogenation process of the invention. The results illustrated in Fig. 7 show that a short (60 minute) 2-step hydrogenation process of the invention produces devices with characteristics that are equivalent to devices produced by a long hydrogenation time (5 hours) with the single step, continuous process conducted at 325°C. The results illustrated in Figures 8 and 9 show that the devices are degraded due to the loss of hydrogen on anneal at 435°C in a nitrogen ambient. This shows that the second step of the 2-step hydrogenation process (temperature lowered, hydrogen plasma still on) is needed to prevent dehydrogenation. To fully evaluate the mechanism and kinetics of the two-step plasma hydrogenation process of the invention, several experiments were conducted as a continuous process and the results plotted and presented in the Figures. Effect of hydrogenation time Fig. 12 is a plot of the variation of the drain current with gate voltage for 32µm/32µm devices with 500A° channel polysilicon which were hydrogenated for various times at constant power, pressure, temperature, gas flow and frequency. These devices were tested at a drain voltage of -5V and were hydrogenated at a continuous temperature of 275°C, at a power setting of 500W, flow of 150 sccm hydrogen at 13.5 MHz and 100m Torr. The data indicates that the device characteristics ("off" current, subthreshold slope and "on" current) rapidly improve during the first 60 minutes of hydrogenation time, after which there is little further improvement. Experiments were also done to see if annealing in molecular hydrogen (no plasma) at 275°C had any effect. In the absence of a plasma there was no effect on the device characteristics, indicating that active hydrogen atoms were needed to passivate the polysilicon. Effect of Polysilicon thickness Experiments were performed using TFTs with 500A° thick channel polysilicon (after fabrication) as well as those with 1000A° polysilicon. Process conditions were the same as that given for Fig. 12. Fig. 13 is a plot of the variation of the drain current versus gate voltage for devices with 500A° and 1000A° channel polysilicon which were hydrogenated for 1 hour. The characteristics of the 500A° thick polysilicon TFT appears to be much better than that with 1000A° polysilicon. Fig. 14 shows the results after 5 hours of hydrogenation. Here the characteristics of the TFTs with 500A° and 1000A° thick polysilicon are comparable. Therefore, from Figs. 13 and 14 it can be seen that TFTs with thinner polysilicon channels hydrogenate faster than those with thicker polysilicon. Effect of Device Size In the preceding experiments, all the experiments were performed with large (32µm/32µm) devices. In these experiments, the effect of device dimensions on the degree of hydrogenation and consequent device characteristics is examined. Process parameters were the same as that given for Fig. 12. Fig. 15 compares the device characteristics of TFTs with varying width/channel length (12µm/12µm, 32µm/32µm and 50µm/50µm) which were hydrogenated for 60 minutes. All the TFTs were fabricated with 1000A° polysilicon. From the figure it can be seen that the smallest device possesses much better characteristics although all three devices have a width to length ratio of one. However, when the devices are hydrogenated for 5 hours (Fig. 16), the TFT characteristics, except leakage current, are almost independent of device dimensions. Leakage current scales with width and is independent of channel length. From Figs. 15 and 16 it may be concluded that smaller devices hydrogenate faster than larger devices. TFTs fabricated with thinner (500A°) polysilicon, also show a similar effect, with smaller devices hydrogenating faster than larger ones. Mechanism of hydrogen transport to the channel polysilicon The data presented earlier was examined to trace the mechanism of hydrogen transport to the channel polysilicon. Fig. 17 indicates the possible paths. While not intending to be bound by any theory, it is believed that since smaller devices hydrogenate faster than larger devices, path A (through the polysilicon gate) may be ruled out. A wide range of values has been reported in the literature for the diffusion of atomic hydrogen through single crystal silicon (10 -6 cm 2 /s to 10 -12 cm 2 /s at 350°C). See for example, S.J. Pearson et al, "Hydrogen in Crystalline Semiconductor," Appl. Phys. A, Vol. 43, 1987, p. 153. In polycrystalline silicon the diffusivity is expected to be higher; however polysilicon absorbs considerable amounts of hydrogen, so it is not surprising that hydrogen cannot go through the thick polysilicon gate. Thus the hydrogen goes around the polysilicon gate - either through the channel polysilicon (path B) or through the quartz substrate (path C) or through the gate oxide (path D). However, since thinner devices hydrogenate faster than thicker devices, path B may also be eliminated as a possible diffusion path since the area of path B through which the hydrogen can enter is proportional to the polysilicon thickness, which compensates for the increased polysilicon volume (again proportional to thickness) which has to be hydrogenated. In addition since hydrogen cannot go through 0.5µm polysilicon gate (path A), it is unlikely that it will go through several microns of channel polysilicon (path B). Thus it appears that the hydrogen can only follow paths C and/or D. It should be noted that in path C, the hydrogen does not necessarily have to go through the thin polysilicon in the source or drain regions, it can go by the side of the source or drain polysilicon into the quartz. Since the gate oxide and the quartz substrate are essentially the same material (silicon dioxide) the diffusivity of hydrogen should be the same in both. However, the cross sectional area through which the flux of hydrogen atoms may enter the gate oxide is limited by the oxide thickness - only 1000A°, compared with a length of several microns through which the hydrogen has to diffuse. The quartz substrate, however, is thick in comparison (550µm), so its thickness should pose no limitation to hydrogen diffusion. Thus path C appears to be the most likely path (or the path of least resistance) for the diffusion of hydrogen. According to the above hypothesis diffusion of hydrogen atoms through the quartz controls the hydrogenation of the polysilicon. To test this theory, 1000A° of silicon nitride followed by 2000A° of LPCVD oxide was deposited on the quartz surface prior to TFT fabrication. Silicon nitride is well known for its properties as a diffusion barrier so it should prevent hydrogen diffusion into the quartz. The 2000A° of LTO on top of the nitride was used as an etch stop so that the nitride beneath would not be etched during the definition (etch) of the channel polysilicon. The TFT was then hydrogenated along with a control sample (TFT with no nitride layer on top of the quartz). The process conditions were the same as in Fig. 12. Fig. 18 shows the results. It will be seen that the device characteristics of the sample with the nitride layer on top of the quartz shows very little effect of hydrogenation and is considerably poorer than the control sample (no nitride). This confirms our hypothesis that the hydrogen diffusion through quartz is the rate controlling step in the hydrogenation process for polysilicon TFTs on quartz although it is also possible to hydrogenate the devices through the oxide with the metal layer removed. Another experiment was performed under the same conditions to verify that hydrogen diffusion through the quartz was the rate controlling step. In this experiment quartz pieces of varying thickness were placed on top of device wafers and then plasma hydrogenation was done using the same process parameters for all pieces. Fig. 19 shows the results. Clearly the extent of hydrogenation depends on the extent the hydrogen has to diffuse through the quartz. Comparison of Fig. 19 with Fig. 15 (effect of device size on hydrogenation) further strengthens the hypothesis. In other experiments, the standard continuous hydrogenation process was carried out at 325°C, 500 W at 13.56 MHz, 105-110 mTorr and with a flow of 45-50 sccms of hydrogen. It was found that the uniformity of the continuous hydrogenation within a given wafer varied possibly as a result of different gas flow patterns and/or to the non-uniformity of the sputter deposit on the wafer surface generated during hydrogenation. It was found that by rotating the samples 180 degrees at the midpoint of the hydrogenation cycle, the sputter deposit was more even and device characteristics were extremely uniform. Unlike in the continuous processing, Hi/Lo processing according to the invention was found to result in extremely uniform hydrogenated TFTs with or without wafer rotation. Electrical measurements taken on at least 500 transistors were extremely uniform. In another series of experiments, under the same conditions, TFT arrays with polysilicon back light shielding and/or natural or synthetic quartz substrates normally require hydrogenation times of six to nine hours. According to the invention, however, the processing of such difficult to hydrogenate devices may also be improved. This is shown by the results illustrated in Figs. 10 and 11 in which such a device with back light shielding is processed with excellent results in 4.5 hours and 6.5 hours (Figs. 10a and 10b) when using 500W at 13.56 MHz, 110 in Torr, 45 sccm hydrogen, at 435°C followed by cooling to 325°C for 30 minutes. In contrast thereto, comparable results with the same device hydrogenated with the one-step continuous process required 8 hours. Rapid hydrogenation of the devices with back light shielding, i.e. wherein there is a shield substance between the substrate and the polysilicon which normally prevents diffusion through the substrate requiring the hydrogen to diffuse along a path (analogous to that of a pipe) leading into the polysilicon, is particularly significant and lends great flexibility and adaptability to the process making it suitable for use in a variety of applications. While specific time periods and temperatures have been enumerated for purposes of illustration, it will be understood that the invention is not limited to these particular time-temperature relationships since it is expected that even more rapid hydrogenation may be obtained at higher temperatures for shorter time periods primarily depending on the plasma generating equipment that is available.

Claims: Method of manufacturing a semiconductor device in which a layer of polysilicon is deposited and patterned on a major surface of a body, after which an insulating layer is formed at said polysilicon and then a hydrogen plasma and heating treatment, to passivate polysilicon grain boundaries and interface traps, is performed in two steps, whereby in the first step in-diffusion of atomic hydrogen from the plasma is effected and whereby in the second step while maintaining said hydrogen plasma the body is cooled to a temperature within the range of 25°C to 375°C, characterized in that the in-diffusion of atomic hydrogen is effected at a temperature in the range of 435°C to 800°C. Method as claimed in Claim 1, characterised in that the first step is carried out for a period of time sufficient to obtain substantial equilibrium of hydrogen in- and out-diffusion. Method as claimed in Claim 1, characterised in that the first step is carried out at a temperature of about 435°C for a period of time not greater than about 30 minutes and that in the second step the body is cooled to a temperature of about 325°C over a period of time not greater than about 30 minutes. Method as claimed in Claim 1, characterised in that the semiconductor device is a polysilicon thin film transistor.

Inventors: KHAN BABAR, MITRA UDAY, ROSSI BARBARA A, KHAN, BABAR, MITRA, UDAY, ROSSI, BARBARA
Applicants: KONINKL PHILIPS ELECTRONICS NV, KONINKLIJKE PHILIPS ELECTRONICS N.V.
Application year: 1993
Main classification: H01L21
IPC codes: H01L21, H01L29