Fluorescent lamps with high color-rendering and high brightness

Abstract: A fluorescent lamp having a plurality of lamp phosphors for converting ultraviolet radiation to visible illumination, in which the lamp phosphor comprises a plurality of metameric blends. The metameric blends of lamp phosphors having substantially identical color coordinates. Cheaper phosphor blends may then be used in conjunction with more expensive fluorescent coatings of the same color coordinate to produce a cheaper fluorescent lamp of the same color coordinates.

Description: This invention relates to fluorescent lamps and fluorescent-lamp phosphors. and specifically to improvements in cost/performance of fluorescent lamps as a result of utilizing appropriate combinations of phosphors. Electrical discharges in a low-pressure noble gas containing mercury generate UV radiation (mainly at 254nm) with high efficiency. This UV radiation from the mercury/noble-gas plasma can be converted into visible light by appropriate materials (phosphors). The combination of this low-pressure plasma plus the phosphor constitutes a fluorescent lamp. For a given low-pressure plasma, the fluorescent-lamp output depends on the phosphor (or phosphor combination) utilized. In the industry the fluorescent-lamp output is specified radiometrically by its S pectral P ower D istribution (SPD). namely by the radiant power per wavelength interval over a spectral region (typically from 375nm to 760nm) that spans not only the visible region, but also a portion of the near UV spectrum and of the near-infrared spectrum. Regardless of the phosphor(s) used, the SPD from a fluorescent source is intrinsically different from that of a black-body radiator, such as the sun or an incandescent lamp. The basic reason for this is that the output from a fluorescent lamp will always contain the sharp emission lines produced in the visible by the plasma-excited mercury atoms, and these emission lines are absent in incandescent lamps or in natural (sun) light. With the introduction of the fluorescent lamps, the need arose in the industry to correlate and compare the output properties of these non-blackbody radiators with those of known white emitters, such as incandescent lamps. The basis of this correlation is the lamp SPD. In effect, by mathematically convoluting the SPD with three spectral-response functions (color-matching functions) associated with the human visual perception, one can mathematically extract from the SPD two quantities (x and y) defined as the "chromaticity coordinates" of the fluorescent lamp. Each pair of chromaticity coordinates defines a point in the so-called color plane. In particular, the SPD's from blackbody radiators (incandescent sources) define in the color plane a line called the "planckian locus". All commercial sources for general-illumination purposes are located on, or in the vicinity of. the planckian locus. A representative spectral convolution involving the SPD will be of the form: with R(λ) one of the spectral-response functions, and with the integration limits being typically a=380nm and b=760nm. Similarly, a convolution of the SPD with one of the aforementioned response functions, the luminous-efficiency function V λ , gives the lumen content of the lamp output, which is a measure of the intensity of the visual stimulus produced by the source in a (typical) human observer. These mathematical transformations have been detailed in various publications of the CIE (Commission Internationale de l'Eclairage). Two sources, such as a fluorescent lamp and an incandescent lamp, can have different SPD's but the same color coordinates; when viewed directly they produce the same visual perception. In such a case the observer visual response is spectrally averaged over the entire SPD of the source, and this averaging is equivalent to the mathematical convolution that produced the color (or chromaticity) coordinates in the first place. Sources with the same color coordinates, but different SPD are defined as being "metameric". Problems arise when objects are being observed under illumination by metameric SPD's. In such a case the observer perception is no longer produced by a spectral average over the entire SPD, but only over the source SPD as reflected from the object being viewed. In general, the color (and hence the color coordinates) of a given object will appear different, when viewed under illumination by one or the other of the metameric sources (the fluorescent source and the corresponding incandescent source). Mathematical procedures were prescribed by the CIE in an attempt to quantify these color differences. The procedures again involve operations on the source SPD, which is now convoluted with the reflectance spectra of eight objects. chosen as representative standards of the range of colors normally encountered. Both the fluorescent-lamp SPD and the SPD of a "temperature correlated" blackbody (incandescent) source are convoluted with the eight reflectance spectra of the standards. In general, the eight quantities derived from the convolution with the fluorescent-source SPD will differ from the corresponding set of eight values obtained with the blackbody SPD. These differences lead to a distortion in color perception, or color rendering, associated with the fluorescent source. The CIE prescribes further mathematical processing of these differences, to arrive at a final set of eight color-rendering indices R a (with a=1,2,..8). In practice the industry relies on an single, overall figure-of-merit for the color rendering, namely the general color-rendering index or CRI , which results from a weighed average of the individual R a . By definition, CRI=100 for a black-body (incandescent) source. Since the SPD of an incandescent source varies smoothly over the visible spectral region, while that of a fluorescent lamp has sharp discontinuities at the spectral location of the Hg lines, in order to maximize the CRI of a fluorescent source one can state, as a rule-of-thumb, that the output from the fluorescent source must by distributed over the visible spectral region in a fairly uniform fashion. Then the spectral averages over various sections of the visible spectrum will not markedly differ from the analogous spectral averages for an incandescent source. But there are no specific rules on how to perform this optimization of the CRI. In any case the CRI of the fluorescent source will be a very sensitivity function of the spectral profile of the SPD. In summary, the output from a fluorescent lamp is fully characterized by its SPD. From the latter one can mathematically derive: its color coordinates, which are roughly speaking a measure of the source "whiteness"; the lumen output (brightness); and the source CRI, namely its ability to faithfully reproduce colors. For a fluorescent source with a given color-point, ideally one would like to simultaneously maximize brightness and CRI, but this is intrinsically impossible. In practice, one strives, by the choice of appropriate phosphor combinations (blends), to produce lamps whose output provides simultaneously high values of the CRI and of the lumen output. In the choice of phosphor-blend components considerations of phosphor cost cannot be ignored, since classes of fluorescent-lamp phosphors currently in use incorporate rare-earth elements, which are very expensive. Since the lamp output-characteristics are completely described by the lamp SPD, the process of optimizing the lumen output/CRI combination by means of phosphor blending can be carried out theoretically at first, without actually having to build lamps, as long as we have available a mathematical technique to construct SPD's that meet some specific performance objectives. The building blocks ("component" SPD's) for this process are here conveniently chosen as the SPD's of lamps containing a single phosphor. US-A-4,891,550 discloses a fluorescent lamp which comprises two blends of preferably metameric lamp phosphors. The first blend of relatively cheap phosphors produces a full spectrum whilst the second blend of more expensive rare earth phosphors produces a spectrum of narrow emission bands. The document discusses how the brighter second group of phosphors can be used to improve the brightness and lamp maintenance of the first group of lamp phosphors at the expense of a decrease in the CRI. In accordance with the present invention, there is provided a fluorescent lamp having a plurality of lamp phosphors for converting ultraviolet radiation to visible illumination, the lamp phosphors comprising a plurality of metameric blends, characterised in that the Color Rendering Index (CRI) of the fluorescent lamp is greater than the CRI values exhibited by the individual metameric blends. The present specification describes a subset of the SPD-optimization process, in the sense of concentrating on the search of total (lamp) SPD's exhibiting high levels of lumen output and high CRI values, in the neighbourhood of eighty, for 40 watt-T12 fluorescent sources with color coordinates of x=0.387; y=0.391 Such sources approximate the output of an incandescent source at about 4,000K (more exactly at about 3,950K), and are produced by GTE Products Corp. under the trade name of "Lite-White Deluxe" (LWX) lamps. The methodology to be discussed is applicable in all generality to sources whose color point falls on the planckian locus, or in its vicinity, but here only the results for about 4,000K sources will be reported. Embodiments of the present invention will now be described by way of example only, and with reference to the accompanying drawings, in which: FIG. 1 is perspective view partially broken away of a low pressure mercury discharge fluorescent lamp construction utilizing a dual layer phosphor coating. FIG. S1 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #2194. FIG. S2 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #2288. FIG. S3 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #2293. FIG. S4 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #2345. FIG.-S5 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #246. FIG. S6 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #290. FIG. S7 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #4300. FIG. S8 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #4381. FIG. S9 shows the SPD after 100 hours of operation for a 40Watt-T12 lamp containing Sylvania phosphor type #4459. FIG. S10 shows the SPD associated with the Gd pentaborate:Ce;Mn phosphor, after 100 hours of operation in a 40Watt-T12. FIG. hb1 shows the SPD for the halo blend at the LWX color point (x=0.387; y=0.391), with the composition and output properties indicated in the body of the Figure. FIG. i0 shows lumen and CRI characteristics of quad blend containing phosphor types #246, #2194, #2293, and #2345 as a function of the fractional content in the #2194 phosphor. Blends for the LWX color point (x=0.387; y=0.391). FIG. i1 shows the SPD for a quad blend for the LWX color point and containing phosphors #246, #2194, #2293, and #2345. Mixing coefficients and output characteristics are also indicated. No halo addition. FIG. i2 shows the effect of metameric mixing on the CRI and lumen output for a tri-blend for the LWX color point, and based on phosphors #246, #2293, and #2345, according to the c i mixing coefficients listed in the Figure. FIG. i3 shows the increased CRI resulting from metameric mixing for a specific LWX quad-blend based on phosphors #246, #2194, #2293, and #2345, according to the c i mixing coefficients listed in the Figure. FIG. i4 shows the increase in CRI and lumen output resulting from metameric mixing for a specific LWX quad-blend based on phosphors #246, #2194, #2293, and #2345, according to the c i mixing coefficients listed in the Figure. The CRI reaches the value of 90 at 30% halo admixing. FIG. iil shows the increased CRI resulting from metameric mixing for a specific LWX quad-blend based on phosphors #246, #2194, #2288, and #2345, according to the c i mixing coefficients listed in the Figure. FIG. ii2 shows the increase in CRI and lumen output resulting from metameric mixing for a specific LWX tri-blend based on phosphors #246, #2194, and #2345, according to the c i mixing coefficients listed in the Figure. The CRI exceeds 90 at 45% halo admixing. FIG. iii1 shows the increased CRI resulting from metameric mixing for a specific LWX quad-blend based on phosphors #246, #2288, #2345, and #290, according to the c i mixing coefficients listed in the Figure. FIG. f11 shows the lumen and CRI characteristics of quad blend containing phosphor types #246, #2194, #2288, and L93S as a function of the fractional content in the #2194 phosphor. Blends for the LWX color point (x=0.387; y=0.391). FIG. f12 shows the increase in CRI and lumen output resulting from metameric mixing for a specific LWX tri-blend based on phosphors #246, #2194, #2284, and L93S, according to the c i mixing coefficients listed in the Figure. The CRI exceeds 90 for halo fractions ranging from 0.25 to 0.40. FIG. dr1 shows the SPD of a LWX metameric mix based on a tri-blend containing phosphors #246, #2194, and #2345. Mix of 0.45 halo blend and 0.55 quad blend. CRI at 90.4 and about 3045 lumens. FIG. le1 shows the SPD of the experimental lamp with the tri-blend containing phosphor types #246, #2194, and #2345. FIG. le2 shows the SPD of the experimental lamp with the halophosphate blends. FIG. le3 shows the SPD of the experimental lamp containing the metameric mix of 45% halophosphate phosphor, as per Figure le2, and 55% of the triblend of Figure le1. FIG. b11 shows a portion of the planckian locus and location of the color points of the test lamps. Legend: halo, halophosphate-containing lamp of Figure le2; tri is the tri-blend of Figure le1; MM is the lamp with the metameric mix of Figure le3. The remaining color points are for sources at 3000K, 2500K and 2000K. Referring to FIG. 1, there is shown a fluorescent lamp 24 containing a phosphor excitable to fluorescence. The lamp 24 comprises a tubular, hermetically sealed, glass envelope 25. Electrodes 26 and 27 are sealed in the ends of envelope 25. Suitable terminals 28 and 29 are connected to the electrodes 26 and 27 and project from envelope 25. The electrodes 26 and 27 extend through glass presses in mount stems to the terminals 28 and 29. The interior of the tube is filled with an inert gas such as argon or a mixture of argon and krypton at a low pressure, for example 266 Pa (2 torr), and a small quantity of mercury, at least enough to provide a low vapor pressure during operation. An arc generating and sustaining medium such as one or more inert gases and mercury is included within envelope 25 so that ultraviolet radiation is produced in the interior of the glass envelope during lamp operation. A phosphor coating 31 on the interior surface of the glass envelope converts the emitted ultraviolet radiation to visible illumination having a white color. In accordance with the principles of the present invention, an improved phosphor layer of the present invention which is illustrated at 33 comprises a plurality of metameric blends of lamp phosphors for converting ultraviolet radiation to visible illumination. Although dual layers of metameric phosphor blends are shown in FIG. 1, a single layer comprising a mixture of metameric phosphor blends may be utilized as a single coat. When a dual layer is utilized as shown in FIG. 1, the first layer 35 is deposited on the inner glass surface and a second phosphor layer or top layer 33 is deposited on the first phosphor layer 35. The use of a dual phosphor layer permits the weight of phosphor utilized in the second or top coat to be reduced and a less expensive phosphor to be utilized as the first layer 35. The first layer 35 preferably comprises a finely divided metameric blend of fluorescent calcium haloapatite phosphor exhibiting the desired white color point. The second layer or top layer 33 comprises a metameric quad phosphor blend on the inside of the tube so that a substantial portion of the ultraviolet radiation is converted to visible illumination having a white color. The amount of the metameric quad-phosphor blend applied is generally between about 10 percent and 50 percent of the total combined phosphor weight of the total of the metameric quad-blend and the metameric halophosphor. The derivation to be detailed next goes through the following stages. First, various combinations of four primary (component) SPD's are systematically explored to identify total (lamp) SPD's exhibiting a target color-point and the required levels of CRI and lumen output. Second, it is shown how the CRI values can be raised by combining two metameric blend-SPD's with the same target color-point, but individually exhibiting a relatively-low CRI. Third, guidelines for implementation in actual lamps are described. Fourth, examples of reduction to practice are reported. 1. SPD of four-component (quad) blends . The main focus of the present treatment is on the results of combining four SPD's, or equivalently, on blending four phosphors. There is a compelling reason for considering four-component blends. When three component SPD's are combined to obtain a total SPD with a pre-assigned target color-point, namely SPD (tot) =Σ i c i ·(SPD) i with C i =1, 2, 3, and Σ i c i = 1 either no solution is possible, or there is a unique solution for the c 1 , c 2 , and c 3 mixing coefficients. This produces one single value for the CRI and for the lumen output from the blend. The solution exists whenever the target color-point is contained within the triangle formed by the color-points of the three blend components. As a concrete example, suppose a halophosphate blend with the color point of eq. 2, is required. Such a blend can be obtained for instance by combining the SPD's of the halophosphate phosphor types #4381, #4459. and #4300 listed in Tables b1 and b2. The resulting SPD of the LWX halo-blend will be produced by the combination: 0.120·SPD(#4381) +0.796·SPD(#4459) +0.084·SPD(#4300) where by SPD(#4381) we mean the 100hrs-SPD pertaining to a (performance optimized) 40Watt-T12 lamp containing only phosphor #4381, and so forth for SPD(#4459) and SPD(#4300). The c i mixing coefficients of eq. 3 therefore assume the values: 0.120; 0.796; and 0.084, respectively. On the other hand, if four primary SPD's are combined (four-component phosphor blend) an infinity of solutions satisfy eqs (3) and (4), with as many sets of c 1 , c 2 , c 3 , and c 4 mixing coefficients. To each solution there will correspond a pair of values for the CRI and the lumens, and so an infinite set of CRI and lumen values is accessible for selection. The detailed composition of this infinite set of four-component (quad) blends can be sampled by a process of mathematical induction, starting from the mixing of binary blends with ternary blends. Proprietary computer software was developed to systematically explore the range of existing solutions (c i mixing coefficients) and to sequentially derive the lumen content and CRI of the various SPD (tot) of eq. 3. In this application we are not mainly concerned with the details of the mathematical derivation, but rather with the actual SPD's obtained, on the basis of the "primary" or "component" SPD's of lamps containing the phosphors listed in Table b1. A summary listing of the relevant phosphor emission-color, powder weight in lamps, and output characteristics at 100 hours of operation is given in Table b2 for 40Watt-T12 lamps containing a single phosphor. The actual SPD's are shown in detail in Figures s1 to s10. In turn, the SPD of the LWX halo-blend as derived from eq. 5 is given in Figure hb1. Approximate chemical composition of Sylvania phosphors considered in the present application Phosphor type (Sylvania™) Composition #2194 BaMgAluminate:Eu;Mn #2288 Zinc ortho-silicate:Mn #2293 (Ce,Tb)Mg Hexa-aluminate #2345 Yttrium Oxide:Eu # 246 BaMg Aluminate:Eu #290 Ca Silicate:Pb;Mn #4300 Ca apatite:Sb;Mn (halo-phosphate) #4381 Ca fluoroapatite:Sb;Mn (halo-phosphate) # 4459 Ca apatite:Sb;Mn (halo-phosphate) (L93S) Gd pentaborate:Ce;Mn Composition, powder weight, and output characteristics (at 100 hours of operation) of single-component W40-T12 lamps utilized in the derivation Phos. type (Sylvania) Emiss. color Rare-earth weight (grams) lumen at 100hrs color coordinates x y #246 blue yes 5.2 1,006 0.151 0.088 #2194 green yes 5.9 3,467 0.162 0.560 #2288 green no 6.0 4,900 0.247 0.635 #2293 green yes 6.6 4,732 0.315 0.554 #290 red no 3.1 1,900 0.589 0.331 #2345 red yes 6.1 2.750 0.506 0.377 #4300 white no 7.6 3,260 0.440 0.406 #4381 yellow no 6.3 3,410 0.406 0.430 #4459 white no 6.3 3,100 0.379 0.384 (L93S) red yes n/a 1,795 0.526 0.309 Although quad blends can be obtained by taking all possible combination of existing lamp phosphors, only five such combinations of four phosphors will be described here. namely: 1. The addition of phosphor #2194 (see Tables b1 and b2) to a typical "tri-color" blend (i.e., phosphors #246, #2293, #2345) currently used in the industry for high-CRI, high-efficacy fluorescent lamps. 2. Same as above, but with #2293 replaced by #2288 (see Tables b1 and b2). 3. Phosphors #246 and #2288, plus the two red-emitting phosphors #2345 (line emitter) and #290 (band emitter). See Tables bi and b2. 4. Phosphor #246, the two green-emitting phosphors #2194 and #2288, and red-emitting Gd pentaborate: Ce;Mn (see Tables b1 and b2). 5. Blue-emitting #246, green-emitting #2194, and the two red-emitters #2345 and #290. In all five cases listed above, after determining the output characteristics of the quad blends, the metameric mixing of the quad blends with the LWX halo-blend of eq. 5 was also explored. Since two metameric SPD's combine to produce a total SPD with the same color point, metameric SPD's can be mixed in any arbitrary proportion, and still maintain some pre-assigned color coordinates. In what follows "metameric mixing" will mean specifically the admixing of a LWX quad-blend with the LWX halo-blend of eq. 5. In view of the low cost of the halophosphate phosphors, economic advantages will always result from this "metameric mixing". Furthermore, in the most favorable cases the CRI, brightness and cost of the final LWX-mix will all be improved by the addition of the halophosphate phosphors. 1. Blends of #246; #2194; #2293, #2345. A representative sampling of the infinite set of possible formulations, with the respective values of lumen output and CRI, are listed in Table p1. The entries in the columns labelled by the phosphor types correspond to the mixing coefficient c i of eqs. 3 and 4. The output characteristics are also plotted in Figure i0 as a function of the fractional content in #2194. From inspection of Table p1 and Figure i0 it can be concluded that the addition of #2194 to the tri-color blend of #246, #2293, and #2345 (first row of Table p1, and leftmost data points in Figure i0) produces a broad increase in the CRI, to a peak value of ∼87.1 for 0,115·SPD(#2194). The SPD of this blend is shown in Figure i1, and is listed in detail in Appendix 1. The CRI of the quad blend exceeds that of the original tri-blend for #2194 fractions ranging from 0 to ∼0.30 (Figure i0 and Table p1). Then the CRI drops as the #2194 content is further raised beyond ∼0.30. Conversely, the quad-blend lumen output drops linearly as the #2194 content increases (Figure i0). Moving next to metameric mixes, quite generally the changes in CRI resulting from the admixing of the LWX halo-blend depend on the specific #2194 content in the quad blend. When the #2194 content is zero (first row in Table p1) the quad blend reduces to a triphosphor blend of the type currently employed in the industry. In this case the effect of metameric mixing with the LWX halo-blend of eq. 5 is summarized in Table p2 and Figure i2. where the LWX halo-blend is added in 5% increments, starting at the 10% level, up to a value of 50%. As the LWX halo-blend is added to the tri-component blend, both the CRI and the lumen output drop monotonically (Figure i2), the latter in a linear fashion, the former in a shallow. parabolic fashion, down to the limiting value of CR1=58.8, which is the CRI for the LWX halo-blend alone (Table p2). The only motivation for adding the LWX halo-blend then would be to capitalize on its lower cost, even if lumens and CRI have to be sacrified, compared to the starting tri-component blend. Quad blends for the LWX color-point (x=0.387 and y=0391), based on phosphors #246, #2194, #2293, and #2345. Composition and predicted output in order of increasing #2194. Quad-blend content as fractional SPD(#XXXX) Lumens CRI #246 #2194 #2293 #2345 0.134 0.000 0.476 0.389 3460.3 83.13 0.125 0.061 0.411 0.401 3392.0 85.74 0.117 0.115 0.355 0.412 3333.1 87.09 0.104 0.201 0.264 0.430 3237.1 86.89 0.101 0.220 0.244 0.433 3216.2 86.11 0.097 0.250 0.213 0.434 3182.7 84.76 0.087 0.313 0.146 0.452 3112.0 81.76 0.085 0.324 0.135 0.455 3100.8 81.22 0.084 0.333 0.125 0.456 3091.0 80.77 0.075 0.390 0.065 0.468 3027.0 77.67 0.074 0.398 0.056 0.470 3017.9 77.21 0.066 0.452 0.000 0.481 2958.3 73.82 Effect of adding the LWX halo-blend to LWX quad-blends. QUAD blend: 0.134 (#246); 0.000 (#2194); 0.476 (#2293); 0.389 (#2345) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 3460.3 83.13 0.10 0.90 3429.4 81.45 0.15 0.85 3413.9 80.47 0.20 0.80 3398.4 79.43 0.25 0.75 3382.9 78.35 0.30 0.70 3367.4 77.24 0.35 0.65 3351.9 76.10 0.40 0.60 3336.5 74.93 0.45 0.55 3321.0 73.74 0.50 0.50 3305.0 72.52 1.00 0.00 3150.6 58.83 A similar trend is observed in the metameric mixing of the quad blend containing 0.061· SPD(#2194), and whose composition is given in the second row of Table p1. The halo addition (Table p3) improves neither the lumen output nor the CRI of the starting quad-blend. As the #2194 content increases, though, the halo addition is definitely beneficial. This is shown in Figure i3 and in Table p4 for a blend containing 0.220·SPD(#2194). A peak CRI value of ∼89 (Table p4) is predicted at a 20% admix of the LWX halo-blend. The lumen loss caused by the halo addition is minimal, only ∼13 lumens, that is about one-third of a percent. It was already mentioned that, as #2194 replaces the more expensive #2293 phosphor, the blend brightness progressively drops (Table p1). When the quad blend reaches a lower brightness than that of the halo-blend, the metameric mixing is instrumental in increasing both brightness and CRI. This is shown in Table p5 and in Figure i4 for the quad blend with 0.313 fractional content in #2194. The lumen output increases linearly with the halo-blend content, while the CRI reaches a peak value of ∼90 at a 30-35% halo admix. The metameric mixing was investigated for all the quad blends of Table p1. For the sake of brevity, rather than reproducing for all the blends of Table p1 the detailed results of the metameric mixing, as shown in detail in Tables p2 to p5, we shall explicitly list in Table p6 only those metameric mixes with maximum values of the CRI. Therefore, Table p6 is to be viewed as an expanded version of Table p1. When the metameric mixing increases the CRI of the corresponding quad blend, the halo fraction that produces the highest CRI value is listed below the corresponding quad blend. Values of the CRI in the neighborhood of 90 at lumen levels exceeding 3,000 lumens are achievable with most of the metameric mixes. This is important in countries where the building codes require CRI values of 90 for office buildings. Effect of adding the LWX halo-blend to LWX quad-blends. QUAD blend: 0.125 (#246); 0.061 (#2194); 0.411 (#2293); 0.401 (#2345) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 3392.0 85.74 0.10 0.90 3367.9 84.98 0.15 0.85 3355.8 84.01 0.20 0.80 3343.7 82.86 0.25 0.75 3331.7 81.63 0.30 0.70 3319.6 80.34 0.35 0.65 3307.5 79.00 0.40 0.60 3295.5 77.62 0.45 0.55 3283.4 76.21 0.50 0.50 3271.3 74.77 1.00 0.00 3150.6 58.83 Effect of adding the LWX halo-blend to LWX quad-blends QUAD blend: 0.101 (#246); 0.220 (#2194); 0.244 (#2293); 0.433 (#2345) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 3216.2 86.11 0.10 0.90 3209.7 88.47 0.15 0.85 3206.4 88.84 0.20 0.80 3203.1 88.92 0.25 0.75 3199.8 88.68 0.30 0.70 3196.6 87.78 0.35 0.65 3193.3 86.28 0.40 0.60 3190.0 84.55 0.45 0.55 3186.7 82.67 0.50 0.50 3183.4 80.69 1.00 0.00 3150.6 58.83 Effect of adding the LWX halo-blend to LWX quad-blends. . QUAD blend: 0.087 (#246); 0.313 (#2194); 0.146 (#2293): 0.452 (#2345) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 3112.6 81.76 0.10 0.90 3116.4 85.23 0.15 0.85 3118.3 86.84 0.20 0.80 3120.2 88.31 0.25 0.75 3122.1 89.37 0.30 0.70 3124.0 89.97 0.35 0.65 3125.9 89.65 0.40 0.60 3127.8 88.20 0.45 0.55 3129.7 86.32 0.50 0.50 3131.6 84.17 1.00 0.00 3150.6 58.83 Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2293, and #2345. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 1. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2293 #2345 0.134 0.000 0.476 0.389 0.00 3460.3 83.13 0.125 0.061 0.411 0.401 0.00 3392.0 85.74 0.117 0.115 0.355 0.412 0.00 3333.1 87.09 0.104 0.201 0.264 0.430 0.00 3237.1 86.89 0.104 0.201 0.264 0.430 0.15 3224.1 88.7 0.101 0.220 0.244 0.433 0.00 3216.2 86.11 0.101 0.220 0.244 0.433 0.20 3203.1 88.9 0.097 0.250 0.213 0.434 0.00 3182.7 84.76 0.097 0.250 0.213 0.434 0.25 3174.7 89.3 0.087 0.313 0.146 0.452 0.00 3112 81.76 0.087 0.313 0.146 0.452 0.30 3124.0 90.0 Maximum CRI obtainable from metameric mixes of quad blends based on #246. #2194, #2293, and #2345. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 2. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2293 #2345 0.085 0.324 0.135 0.455 0.00 3100.8 81.22 0.085 0.324 0.135 0.455 0.30 3115.7 90.0 0.084 0.333 0.125 0.456 0.00 3091.0 80.77 0.084 0.333 0.125 0.456 0.35 3111.9 90.0 0.075 0.309 0.065 0.468 0.00 3027.0 77.67 0.075 0.309 0.065 0.468 0.40 3076.0 90.4 0.074 0.398 0.056 0.470 0.00 3017.9 77.21 0.074 0.398 0.056 0.470 0.40 3071.0 90.5 0.066 0.452 0.000 0.481 0.00 2958.3 73.82 0.066 0.452 0.000 0.481 0.45 30.44.9 90.4 2 Blends of #246; #2194; #2288, #2345. The quad blend considered previously contained the rare-earth-activated, green-emitting phosphor #2293. In the set of blends to be discussed next #2293 is replaced by the #2288 phosphor, which does not contain any rare-earth elements and is therefore cheaper. After the derivation of the output characteristics of such blends, the effect of metameric mixing is considered. A summary listing of the resulting formulations of highest CRI is given in Table s1. The latter is analogous to Table p6, but for the new choice of phosphor types. There are two limiting cases of Table s1, whereby the quad blends degenerate into tri-component blends (tri-blends), namely the target color-point can be reached with no #2194 present (first two rows), or with no #2288 present (last two rows). These two cases deserve an explicit treatment. The pertinent results are summarized in Table s2 and Figure ii1 for the tri-blend based on #246, #2288, and #2345, and in Table s3 and Figure ii2 for the one based on #246, #2194, and #2345. In the case of the tri-blend with #246, #2288, and #2345 (Table s2 and Figure ii1) the halo addition produces an increase in CRI for halo fractions c halo in the range O<c halo ≤0.4, up to a peak value of 87.8 for c halo =0.20. This entails a modest lumen loss of ∼37 lumens, that is ∼1% by comparison with the starting tri-blend. The lumen output of the tri-blend with #246, #2194, and #2345 (∼2,960 lumens) is lower (Table s1, Part 2) than that of the LWX halo-blend. Therefore the metameric mixing produces an increase in brightness. Simultaneously, the CRI rises over a broad range of halo fractions (Table s3 and Figure ii2). The remarkably-high CRI and lumen values (CRI>90; lumens in excess of 3,000) should be noted for the metameric mix with 45% halo (Table s3 and Figure ii2). In view of the high halo content, this type of blend will also be quite inexpensive. Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2288, and #2345. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 1. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2288 #2345 0.140 0.000 0.386 0.473 0.00 3336.2 85.4 0.140 0.000 0.386 0.473 0.20 3299.1 87.8 0.128 0.070 0.326 0.474 0.00 3277.8 84.3 0.128 0.070 0.326 0.474 0.25 3246.0 88.5 0.117 0.140 0.267 0.475 0.00 3219 82.7 0.117 0.140 0.267 0.475 0.25 3202.2 89.0 0.116 0.148 0.260 0.475 0.00 3212.2 82.5 0.104 0.201 0.264 0.430 0.30 3193.8 89.1 0.111 0.177 0.235 0.476 0.00 3188.4 81.8 0.111 0.177 0.235 0.476 0.30 3177.1 89.3 0.101 0.237 0.184 0.477 0.00 3138.4 80.3 0.101 0.237 0.184 0.477 0.35 3142.4 89.7 Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2288, and #2345. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 2 Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2288 #2345 0.100 0.246 0.176 0.477 0.00 3130.6 80.1 0.100 0.246 0.176 0.477 0.35 3137.6 89.8 0.086 0.329 0.104 0.478 0.00 3060.9 77.8 0.086 0.329 0.104 0.478 0.40 3096.8 90.2 0.085 0.337 0.098 0.479 0.00 3054.5 77.6 0.085 0.337 0.098 0.479 0.40 3093.0 90.3 0.083 0.351 0.086 0.479 0.00 3042.5 77.1 0.083 0.351 0.086 0.479 0.40 3085.7 90.3 0.075 0.397 0.047 0.480 0.00 3004.7 75.7 0.075 0.397 0.047 0.480 0.40 3063.1 90.2 0.066 0.452 0.00 0.480 0.00 2958.3 73.8 0.066 0.452 0.00 0.480 0.45 3044.9 90.4 Effect of adding the LWX halo-blend to LWX quad-blends. QUAD blend: 0.140 (#246); 0.000 (#2194); 0.386 (#2288); 0.473 (#2345) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 3336.2 85.44 0.10 0.90 3317.6 87.25 0.15 0.85 3308.3 87.62 0.20 0.80 3299.1 87.81 0.25 0.75 3289.8 87.72 0.30 0.70 3280.5 87.05 0.35 0.65 3271.2 85.78 0.40 0.60 3262.0 84.29 0.45 0.55 3252.7 82.60 0.50 0.50 3243.4 80.76 1.00 0.00 3150.6 58.83 Effect of adding the LWX halo-blend to LWX quad-blends. QUAD blend: 0.066 (#246); 0.452 (#2194); 0.000 (#2288); 0.481 (#2345) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 2958.4 73.82 0.10 0.90 2977.6 78.72 0.15 0.85 2987.2 80.96 0.20 0.80 2996.9 83.09 0.25 0.75 3006.5 85.12 0.30 0.70 3016.1 87.08 0.35 0.65 3025.7 88.68 0.40 0.60 3035.3 89.87 0.45 0.55 3044.9 90.43 0.50 0.50 3054.5 88.82 1.00 0.00 3150.6 58.83 3. Blends of #246; #2288; #2345, #290. Cost considerations require that the content of the expensive #2345 phosphor be minimized in blends. This could be achieved by adding to the combination of phosphors #246, #2288, and #2345 an inexpensive red-emitting material, such as phosphor #290. Accordingly, Table tr1 gives an overview of the predicted performance (lumens and CRI) of quad blends containing #246, #2288, #2345, and #290. As in the previous cases, the metameric mixes with the highest CRI are also indicated, where appropriate. The highest CRI (87.7 at ∼3,180 lumens) is obtained in the presence of #290 when c #290 =0.115, and for a 15% mix with the halo blend (Table tr2 and Figure iii1). For C #290 =0.115, halo admixing up to ∼0.3 increases the blend CRI. The lumen output of the metameric mixes decreases linearly with the halo content. Maximum CRI obtainable from metameric mixes of quad blends based on #246. #2288, #2345 and #290. Comparison with no halo addition. Quad blends listed in order of increasing #290 content. LWX color point. Part 1. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2288 #2345 #290 0.140 0.386 0.473 0.000 0.00 3336.3 85.4 0.140 0.386 0.473 0.000 0.20 3299.2 87.8 0.131 0.354 0.398 0.115 0.00 3186.0 86.6 0.131 0.354 0.398 0.115 0.15 3180.7 87.7 0.122 0.320 0.315 0.242 0.00 3019.1 87.0 0.112 0.283 0.227 0.337 0.00 2841.9 87.0 0.102 0.247 0.142 0.507 0.00 2672.3 86.0 0.100 0.237 0.118 0.544 0.00 2623.7 85.3 Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2288, #2345 and #290. Comparison with no halo addition. Quad blends listed in order of increasing #290 content. LWX color point. Part 2. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2288 #2345 #290 0.095 0.219 0.076 0.609 0.00 2539.2 83.9 0.090 0.201 0.031 0.677 0.00 2450.4 82.2 0.088 0.196 0.018 0.697 0.00 2424.2 81.6 0.086 0.188 0.000 0.725 0.00 2386.9 80.7 Effect of adding the LWX halo-blend to LWX quad-blends. QUAD blend: 0.131 (#246); 0.355 (#2288); 0.398 (#2345); 0.115 (#290) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 3186.0 86.57 0.10 0.90 3182.4 87.49 0.15 0.85 3180.7 87.67 0.20 0.80 3178.9 87.58 0.25 0.75 3177.1 86.93 0.30 0.70 3175.4 85.74 0.35 0.65 3173.6 84.35 0.40 0.60 3171.8 82.78 0.45 0.55 3170.1 81.07 0.50 0.50 3168.3 79.26 1.00 0.00 3150.6 58.83 4. Blends containing Gd pentaborate:Ce;Mn as the red emitter . Compared with the emission from phosphor #290 (Figure s6) the emission from the pentaborate phosphor (L93S) is shifted to longer wavelengths and peaks at ∼630nm (Figure s10). Starting from a tri-blend containing #246, #2288, and the pentaborate, phosphor #2194 is gradually added. This produces a monotonic drop in lumens and CRI, with the latter ultimately slumping down to ∼71.6 from the initial value of 82.5 (Table IsO and Figure fl1). The metameric mixing raises both lumen out and CRI, the latter way above the value of 90. Details on the effect of the metameric mixing are listed in the summary Table Is1, and in Figure fl2 for the end-of-series novel formulation: 0.015•SPD(#246) + 0.343•SPD(#2194) + 0.641•SPD(L93S) Quad blends based on #246, #2194, #2288 and L93S, in order of increasing #2194 content. LWX color point. Quad-blend content as SPD(#XXXX) Lumens CRI #246 #2194 #2288 L93S 0.071 0.000 0.294 0.633 2653.4 82.5 0.063 0.054 0.248 0.634 2606.9 82.0 0.057 0.088 0.218 0.635 2577.2 81.5 0.054 0.104 0.205 0.635 2563.9 81.2 0.042 0.176 0.143 0.637 2501.8 79.2 0.041 0.181 0.138 0.637 2497.3 79.0 0.030 0.248 0.081 0.639 2439.9 76.2 0.029 0.257 0.074 0.639 2432.1 75.8 0.028 0.263 0.068 0.639 2427.0 75.5 0.022 0.300 0.037 0.640 2395.2 73.8 0.015 0.343 0.000 0.641 2358.1 71.6 Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2288 and L93S. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 1. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2288 L93S 0.071 0.000 0.294 0.633 0.00 2653.4 82.5 0.071 0.000 0.294 0.633 0.20 2752.8 87.1 0.063 0.054 0.248 0.634 0.00 2606.9 82.0 0.063 0.054 0.248 0.634 0.20 2715.6 88.1 0.057 0.088 0.218 0.635 0.00 2577.2 81.5 0.057 0.088 0.218 0.635 0.20 2691.9 88.6 0.054 0.104 0.205 0.635 0.00 2563.9 81.2 0.054 0.104 0.205 0.635 0.25 2739.9 88.9 0.042 0.176 0.143 0.637 0.00 2501.8 79.2 0.042 0.176 0.143 0.637 0.25 2664.0 90.0 0.041 0.181 0.138 0.637 0.00 2497.3 79.0 0.041 0.181 0.138 0.637 0.25 2660.6 90.1 Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2288 and L93S. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 2. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2288 L93S 0.030 0.248 0.081 0.639 0.00 2439.9 76.2 0.030 0.248 0.081 0.639 0.30 2653.2 91.0 0.029 0.257 0.074 0.639 0.00 2432.1 75.8 0.029 0.257 0.074 0.639 0.30 2647.1 91.1 0.028 0.263 0.068 0.639 0.00 2427.0 75.5 0.028 0.263 0.068 0.639 0.30 2644.1 91.2 0.022 0.300 0.037 0.640 0.00 2395.2 73.8 0.022 0.300 0.037 0.640 0.30 2621.9 91.5 0.015 0.343 0.000 0.641 0.00 2358.1 71.6 0.015 0.343 0.000 0.641 0.35 2635.5 91.9 Effect of adding the LWX halo-blend to LWX quad-blends. QUAD blend: 0.015 (#246); 0.343 (#2194); 0.000 (#2288); 0.641 (L93S) LWX halo-blend: 0.120 (#4381); 0.796 (#4459); 0.084 (#4300). Halo fraction Quad fraction Lumens CRI 0.00 1.00 2358.1 71.60 0.05 0.95 2397.7 75.84 0.10 0.90 2437.3 79.90 0.15 0.85 2477.0 83.76 0.20 0.80 2516.6 87.04 0.25 0.75 2556.2 89.75 0.30 0.70 2595.9 91.60 0.35 0.65 2635.5 91.85 0.40 0.60 2675.1 90.54 0.45 0.55 2714.7 88.55 0.50 0.50 2754.4 86.13 1.00 0.00 3150.6 58.83 5. Blends of #246; #2194; #2345, and #290. The quad blends considered next contain the two red emitters (#2345 and #290), as in the previous blends, the usual #246 as blue emitter, and #2194 as the green emitter. The results for the quad blends and their metameric mixes are summarized in Table tw1. In the absence of #290 the tri-blend brightness is of ∼2,958 lumens with a CRI of 73.8 (first row of Table tw1). The addition of #290 improves dramatically the CRI, up to 90, but exacts a toll in brightness, mainly because the replacement of #2345 by the relatively low-brightness #290 phosphor. Some of the lumen losses can be recouped by halo addition. In all cases CRI values of 90 and more can be reached. For the particular case of the tri-blend with no #290, a substantial halo addition (45%) produces a CRI of 90.4 at 3045 lumens (row 2 of Table tw1). The pertinent SPD of such a metameric mix is shown in Figure dr1. This is the same tri-blend discussed in connection with the blends of #246, #2194, #2288, and #2345. Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2345 and #290. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 1. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2345 #290 0.066 0.452 0.481 0.000 0.00 2958.4 73.8 0.066 0.452 0.481 0.000 0.45 3044.9 90.4 0.064 0.420 0.415 0.100 0.00 2854.2 76.2 0.064 0.420 0.415 0.100 0.40 2972.8 90.6 0.061 0.382 0.338 0.217 0.00 2732.1 79.2 0.061 0.382 0.338 0.217 0.35 2878.6 90.7 0.059 0.344 0.259 0.337 0.00 2607.2 82.4 0.059 0.344 0.259 0.337 0.30 2770.3 90.8 0.058 0.338 0.246 0.356 0.00 2587.2 83.0 0.058 0.338 0.246 0.356 0.25 2728.1 90.6 0.055 0.284 0.136 0.524 0.00 2412.4 87.6 0.055 0.284 0.136 0.524 0.15 2523.1 90.8 Maximum CRI obtainable from metameric mixes of quad blends based on #246, #2194, #2345 and #290. Comparison with no halo addition. Quad blends listed in order of increasing #2194 content. LWX color point. Part 2. Quad-blend content as fractional SPD(#XXXX) Halo fract. Lumens CRI #246 #2194 #2345 #290 0.052 0.252 0.070 0.624 0.00 2307.9 89.7 0.052 0.252 0.070 0.624 0.10 2392.2 90.4 0.052 0.246 0.057 0.643 0.00 2288.4 89.9 0.052 0.246 0.057 0.643 0.05 2331.5 90.4 0.051 0.232 0.028 0.687 0.00 2242.9 90.1 0.050 0.218 0.000 0.731 0.00 2197.2 89.7 Some guidelines will be now outlined for the implementation of the present results into actual lamps. The basic results of the present application are: 1. The spectral profiles of SPD's that are characterized by a pre-assigned color point, and have associated specific values of lumens and CRI. 2. The way to construct such SPD's starting from the SPD of existing single-component lamps, by means of the mixing coefficients c i introduced in eqs 3 and 4. Up to this point the derivation is rigorous. 1. From SPD fraction to phosphor-weight formulations. From the viewpoint of the lamp technologist the type of photometric information embedded in the c i mixing coefficients has to be translated into fractional weight composition for the individual phosphors in the blend. Let us start with the simple assumption that the blend components represent completely randomized and non-interacting subsystems in the lamp, so that the blend output in lamps is the superposition of the contributions from the individual blend components. In such a case, if the single-lamp powder weights are the same, then the photometric c i coefficients become identical to the fractional weight w i of the individual phosphor-blend components. With reference to Table b2, the phosphor weight in the single-component lamps is in practice not the same. Then the transition from SPD fractions to weight fractions is a simple matter of multiplying the SPD fractions c i by the powder-weight of the corresponding lamp, and of re-normalizing, as shown below. Let c n be the photometric (SPD) fraction for blend component n, and s n the phosphor powder-weight of the s ingle-component lamp for blend component n (see Table b2). Then the blend fractions w n in weight units are given by: w n =(c n •s n ):(Σ n c n •s n ) with n=1,2,3, and 4. An example of this simple transformation will be carried for the entries of Table p1. The ensuing Table i1 is a modified version of Table p1, in the sense that each pair of rows gives the phosphor-blend compositions expressed in c i units (fraction of single-lamp SPD) in the top row, and in fractional-weight units in the bottom row. Quad blends for the LWX color-point (x=0.387 and y=0.391), based on phosphors #246, #2194, #2293, and #2345. Composition, blend weight (in grams) and predicted output in order of increasing #2194. Top row in row pairs: c i mixing coefficients for the SPD's; bottom row: weight percent fraction in blends. Part 1. #246 #2194 #2293 #2345 Blend weight Lumens CRI 0.134 0.000 0.476 0.389 3460.3 83.13 0.112 0.000 0.506 0.382 6.21 3460.3 83.13 0.125 0.061 0.411 0.401 3392.0 85.74 0.105 0.058 0.440 0.396 6.16 3392.0 85.74 0.117 0.115 0.355 0.412 3333.1 87.09 0.099 0.110 0.381 0.409 6.14 3333.1 87.09 0.104 0.201 0.264 0.430 3237.1 86.89 0.088 0.195 0.286 0.431 6.09 3237.1 86.89 0.101 0.220 0.244 0.433 3216.2 86.11 0.086 0.214 0.265 0.435 6.07 3216.2 86.11 Part 2. #246 #2194 #2293 #2345 Blend weight Lumens CRI 0.097 0.250 0.213 0.434 3182.7 84.76 0.084 0.244 0.233 0.439 6.03 3182.7 84.76 0.087 0.313 0.146 0.452 3112.0 81.76 0.075 0.307 0.160 0.458 6.02 3112.0 81.76 0.085 0.324 0.135 0.455 3100.8 81.22 0.073 0.317 0.148 0.461 6.02 3100.8 81.22 0.084 0.333 0.125 0.456 3091.0 80.77 0.073 0.327 0.137 0.463 6.01 3091.0 80.77 0.075 0.390 0.065 0.468 3027.0 77.67 0.065 0.385 0.072 0.478 5.97 3027.0 77.67 0.074 0.398 0.056 0.470 3017.9 77.21 0.064 0.393 0.062 0.480 5.97 3017.9 77.21 0.066 0.452 0.000 0.481 2958.3 73.82 0.058 0.448 0.000 0.493 5.94 2958.3 73.82 2. The linearized blend model of completely randomized, non-interacting blend components may turn out not to be realized in practice for a variety of reasons. Then the weight fractions listed in the previous Table may not exactly result in a lamp with the targeted color-point. In such a case the target SPD (see for instance Figures i1 and dr1) can always be constructed on the basis of the information provided in the present application, namely from the component SPD's of Figures s1 to s10 and the c i coefficients (and halo-mixing fractions in the case of metameric mixes) listed in the preceding Tables. Once the target SPD is thus constructed, it can be used as a bench-mark for the SPD obtained from the experimental lamps, in the sense that the blend composition of the test lamps can be slightly altered by trial-and-error, until the SPD's of the experimental lamps containing the modified blend converge to the bench-mark SPD, and hence to the target color-point. 3. An alternative, more systematic approach, requiring the fabrication and photometric characterization of a single test lamp, is the following. Let S targ (λ 1 ) be the predicted SPD-intensity for the target blend-lamp at the wavelength λ 1 , and S e (λ 1 ) the actual SPD-intensity observed in the test lamp containing a blend of weight-percent composition characterized by the w i coefficients of eq.7. Let us assume that S e (λ 1 )≠S targ (λ 1 ). Then one possible route to bring about the convergence of S e to S targ is the following. At a given wavelength λ m the output S e (λ m ) from the experimental lamp can be viewed as arising from the contribution of the component SPD's, here labelled S c (λ), each blend component contributing according to a factor f c (λ m ). So at the wavelength λ m , one has for the test lamp: Σ c f c (λ m )·S c (λ m )= S e (λ m ) with c=1, 2, 3, and 4. We assume now that f c (λ m )= f c , namely that the f c factors are independent of wavelength, which is normally the case, unless, for instance, one of the phosphors absorbs the visible radiation emitted by another blend component. This means that if we choose four different wavelengths λ m in the S e output, we can set up three more relations such as eq. 8, that constitute together with eq. 8 a system of four linear equations in the four unknown f c (with c=1,2,3 and 4). Such a system of linear equations is easily solved by means of a well-known procedure, Cramer's rule. The f c quantities can be viewed as "effective mixing coefficients", compared to the c i factors of eq. 3, 4 that are derived for the linear model of randomized, non-interacting blend components. After deriving the f c values, we use them to arrive at a modified blend formulation. In the corrected blend the following relation will apply at λ m : Σ c g c S c (λm)= S targ (λ m ) with c i =1, 2, 3, and 4, and where S targ (λ m ) is now the target SPD, rather than the SPD of the test lamp, as in eq. 8. By a repeat of the previous procedure, after selecting three additional wavelengths in the SPD, we can derive again by Cramer's rule the unknown g c factors, since the S c (λ m ) spectral profiles are known experimentally (see Figures s1 to s10), and the S targ 's are derived in the present application. Once the g c factors have been obtained, we are still left with the problem of establishing a connection between these photometric g c factors and a blend description in terms of the component fractional-weights. Such a relation, though, has been established for the f c coefficients, since in the test lamp the f c coefficients are associated with the fractional weights w c of the blend components. In particular the f c coefficient for the case of unit weight (1 gram) of component c is given by: u c = f c w c L e with: u c a power/weight equivalent with dimensions of Watts/(nm·grams); L e the blend weight in grams for the test lamp; and w c the weight fraction for component c. Using eq. 10, the required weight W c of component c that will satisfy eq. 9 will be then given by the expression: g c = f c w c L e •W c = u c •W c and re-arranging eq. 11 : W c = g c u c for the required weight of component c in the blend. Going back to the mixing coefficients c i of eqs. 3 and 4, their associated power/weight equivalent was 1/s i , with s i the powder weight of the single-phosphor lamp containing component s i . The ratio: (1/s c ): u c = (u c • s c ) -1 of the predicted and observed power/weight equivalents is therefore a measure of the deviation from the linearized model of randomly-distributed, non-interacting phosphor blends. The expression (u c • s c ) -1 , which will be either greater or less than unity, can be viewed as a "utilization factor" of phosphor c in the particular phosphor blend under consideration. 4. Lamp configurations with two phosphor-layers. We mentioned earlier the high material costs associated with phosphors containing rare-earth elements. As a cost-cutting measure the fluorescent-lamp industry frequently resorts to depositing the phosphors in lamps as two successive layers. The first layer, adjacent to the inner surface of the glass bulb is generally a phosphor, or phosphor blend, consisting of inexpensive halophosphate phosphors. After drying this first phosphor-layer must be insoluble in the suspension used to deposit the subsequent phosphor layer. The second phosphor layer is generally a tri-component blend of rare-earth-containing phosphors, of type #246, #2293 and #2345 in the specific instance of Sylvania lamps. This top layer of premium phosphors efficiently intercepts and absorbs the UV radiation produced by the plasma, and so it can be applied in relatively thin layers. For example, when the top layer represent 20% in weight of the total phosphor content of the lamp, the resulting thin top layer ("skin coat") absorbs approximately 60% of the available UV radiation, the remaining being converted in the underlying halophosphate phosphor-layer. As the thickness of the top layer increases, the fraction of total UV-radiation absorbed in the top layer increases, but so does the phosphor cost. At this stage the economy in phosphor cost has to be balanced against the higher manufacturing costs intrinsic to the two-phosphor-layer fabrication. The results presented here on metameric mixes are applicable also to two-phosphor-layer lamp configurations in the following sense. In the two-phosphor-layer configuration the lamp output is the superposition of the output from the individual phosphor layers. The thickness of the top, or premium, phosphor-layer determines the fraction of available UV radiation to be converted in each individual layer. The two-phosphor-layer configuration can therefore be viewed as an extreme case of the break-down, deliberately induced, of the model of randomized blend components. We have already mentioned that in the "skincoat" configuration 60% of the available UV radiation is converted in the top layer, and 40% in the halophosphate layer. From the viewpoint of lamp output this is exactly equivalent to having a metameric mix of 60% tri- (or quad-) blend and 40% halo blend. As a concrete example, we refer to Table p6. part 2. There are two metameric mixes based on 60% quad-blend containing #246, #2194. #2293. #235, and 40% halo-blend, such mixes providing CRI values of 90.4 and 90.5 respectively, at brightness levels exceeding 3,000 lumens. This type of output can either be achieved in a single-phosphor-layer configuration, or in a double-phosphor-layer configuration. In the latter case the required weight of the quad blend can be reduced to approximately a third, thus realizing a saving in phosphor costs. In the former case the manufacturing process is faster and less expensive. Single-phosphor-layer lamps based on the results of the present application were fabricated at GTE US Lighting by C. Ford, L. Plante, and F. Taubner (Memo of Dec. 21st, 1988). One particular formulation was selected for testing, namely the mix listed as the last row of Table s1. Instead of phosphor #2194, a related phosphor type, #2196, with a slightly different output was used. The fractional weight percent of the phosphor components for the tri-blend are listed in Table te1. Fractional-weight composition for the tri-blend utilized in the lamp tests. #246 #2194 #2345 Calculated (Table I1) 0.058 0.448 0.493 Used in the lamp tests 0.06 0.46 0.48 Three test lamps were built, containing respectively the tri-blend of Figure te1, the halophosphate, and the metameric mix. The SPD of the lamp containing the tri-blend is shown in Figure le1. The lamp CRI was 65.6. The SPD of the halophosphate test-lamp is given in Figure le2. Its CRI was 58.8. The SPD of Figure le2 should be compared with the predictions of Figure hb1. The metameric mix employed in the test lamp consisted of 45% halophosphate and 55% quad-blend. as per the last row of Table s1. The test lamp SPD is displayed in Figure le3. From the SPD one can derive color coordinates of 0.383 and 0.374, and a CRI of 90.4. The output brightness was 3,086 lumens at 0 hrs and 3,011 lumens at 100 hours, with a 0-100 hrs maintenance of 97.6%. The predictions of Table s1 were for 3,045 lumens at 100hrs and a CRI of 90.4. The SPD of the test lamp of Figure le3 should be compared with the calculated SPD of Figure dr1. The agreement is excellent. Minor differences in fine-structure components are due to the different spectral resolution of the detectors used for the measurements of the SPD of Figures s1 to s10, and for the measurement of the SPD of Figure le3. The location of the color points of the three experimental lamps is shown in Figure bl1 relatively to the planckian locus. The color point of the metameric mix, indicated in the Figure as MM, is seen to fall nicely on the Planckian (black-body) locus.

Claims: A fluorescent lamp having a plurality of lamp phosphors for converting ultraviolet radiation to visible illumination, the lamp phosphors comprising a plurality of metameric blends, characterised in that the Color Rendering Index (CRI) of the fluorescent lamp is greater than the CRI values exhibited by the individual metameric blends. A fluorescent lamp as claimed in claim 1, characterised in that one of said metameric blends of lamp phosphors comprise a quad-phosphor blend. A fluorescent lamp as claimed in claim 2, characterised in that said quad-phosphor blend comprises a red color emitting phosphor component having a visible emission spectrum principally in the 590 to 630 nm wavelength range, blue color emitting phosphor component having an emission spectrum principally in the 430 to 490 nm wavelength range, a green color emitting phosphor component having emission spectrum principally in the 500 to 570 nm wavelength range, and an additional phosphor having a visible emission spectrum. A fluorescent lamp as claimed in claim 3, characterised in that said additional phosphor comprises a red or green emitting phosphor component. A fluorescent lamp as claimed in any of claims 2, 3 or 4, characterised in that another one of said blends of lamp phosphors comprises alkaline earth metal halophosphate phosphors. A fluorescent lamp as claimed in claim 5, characterised in that said blend of alkaline earth metal halophosphate phosphors includes a finely divided fluorescent calcium haloapatite phosphor. A fluorescent lamp as claimed in claim 5 or 6, characterised in that a layer of said alkaline earth metal halophosphate phosphors is on the interior surface of the glass envelope and said quad-phosphor blend is a separate layer directly adjacent said layer of alkaline earth metal halophosphate phosphor. A fluorescent lamp as claimed in claim 6 or 7, characterised in that the amount of said halo-phosphor blend is between 10 to 50 weight percent of the total combined phosphor weight of the phosphor layers. A fluorescent lamp as claimed in any preceding claim, characterised in that the CRI of the lamp is greater than 90 and the lumen output is greater than 3000 lumens. A fluorescent lamp as claimed in any preceding claim, characterised in that said visible light has predetermined x and y values of ICI coordinates wherein the x value is in the range of 0.35 to 0.45, and said y value is in the range of 0.375 to 0.425.

Inventors: PAPPALARDO ROMANO G, PAPPALARDO, ROMANO G.
Applicants: FLOWIL INT LIGHTING, FLOWIL INTERNATIONAL LIGHTING (HOLDING) B.V.
Application year: 1993
Main classification: H01J61
IPC codes: C09K11, H01J61