Stabilised magnesium hydroxide slurries

Abstract: A stabilized aqueous slurry of magnesium hydroxide and a method for preparing the same are provided. The method involves an aqueous magnesium hydroxide slurry prepared with a combination of (a) one or more polymeric dispersants and (b) one or more water-soluble alkali metal salts. Slurries prepared according to the invention are less susceptible to increases in viscosity upon standing and remain flowable after several days.

Description: This invention relates to stabilised aqueous magnesium hydroxide slurries. Magnesium hydroxide is used in large quantities in various applications including toothpaste additives and as an acid neutralizer. Magnesium hydroxide [Mg(OH) 2 ] is also the precursor in the manufacture of magnesium oxide (MgO) which is used in antacid formulations and as a pigment in the paper industry. It is desirable to be able to ship and store magnesium hydroxide as a high solids aqueous slurry. However, such slurries are fairly unstable and form either gels or hard-pack sediment upon standing, thereby rendering the slurries difficult to use and potentially damaging to piping, pumps, and other slurry handling mechanical equipment. Magnesium hydroxide and magnesium oxide slurry stability has been the subject of extensive research and has been a long standing problem for the magnesium hydroxide industry. The art has addressed the problem by focusing on methods of reducing the viscosity of high solids magnesium hydroxide slurries. US 4,230,610 teaches a method of reducing the viscosity of magnesium oxide slurries by using 0.1 to 5.0 percent by weight of poly(acrylic acid) neutralized to a pH of from about 8.0 to about 12.0. US 4,375,526 teaches a method of reducing the viscosity and enhancing the stability of magnesium hydroxide slurries by using anionic polymers and copolymers. US 4,430,248 teaches a method of reducing the viscosity of magnesium hydroxide slurries by using cationic polymers and copolymers. In EP-A-0 061 354 an aqueous composition is disclosed for conditioning an aqueous system, for example a sewage slurry, comprising an alkali earth metal hydroxide, e.g. lime, and an anionic oligomeric polyelectrolyte, e.g. a salt of polyacrylic acid. Other components may include a weightening agent, e.g. calcium carbonate, a cationic flocculand, e.g. a polyacrylamide, and a base such as sodium hydroxide. Those approaches are somewhat effective in reducing the viscosity of magnesium oxide and magnesium hydroxide slurries but are not generally satisfactory for maintaining the stability of the slurries over an extended period of time. It is an object of this invention to provide aqueous slurries of magnesium hydroxide having such enhanced stability. Accordingly the present invention as claimed in claim 1 provides a stabilized aqueous magnesium hydroxide slurry containing from 30 to 70% by weight, based on the weight of the slurry, of magnesium hydroxide and, as a stabilizer for the slurry, from 0.2 to 20% by weight, based on the weight of the magnesium hydroxide, of a polymeric anionic dispersant having a weight average molecular weight, as determined by aqueous gel permeation chromatography of from 1000 to 50000, or salt thereof characterized in that the slurry also contains from 0.2 to 20% by weight, based on the weight of the magnesium hydroxide, of at least one water-soluble salt of an alkali metal, which salt is selected from alkali metal carbonates and alkali metal citrates, and farther characterized in that the slurry has an initial viscosity of from 100 to 4000 cps (0.1 to 4 Pa.s). Preferred embodiments are claimed in the dependent claims. The one or more polymeric dispersants which are suitable for the present invention are anionic polymeric dispersants which are effective at dispersing aqueous slurries of magnesium hydroxide. Anionic polymers include, for example, homopolymers, copolymers and terpolymers having carboxylic acid, sulphonic acid or phosphonic acid functionalities. Monomers which impart acid functionality include, for example, acrylic acid, methacrylic acid, crotonic acid, maleic acid, maleic anhydride, itaconic acid, mesaconic acid, fumaric acid, citraconic acid, vinylacetic acid, acryloxypropionic acid, vinylsulfonic acid, styrenesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, allylsulfonic acid, allylphosphonic acid, vinylphosphonic acid, and vinylsulfonic acid. Anionic polymeric dispersants may also be formed, in part, from monomers which do not contribute to the carboxylic, sulphonic or phosphonic acid, functionality of the polymer. Monomers which do not contribute to the carboxylic, sulphonic or phosphonic acid functionality of the polymer include, for example: alkyl esters of acrylic and methacrylic acid such as methyl, ethyl and butyl acrylate and methyl, butyl and isobutyl methacrylate; hydroxyalkyl esters of acrylic and methacrylic acids, such as hydroxyethyl and hydroxypropyl acrylate and methacrylate; acrylamide; methacrylamide; N-tertiarybutylacrylamide; N-methylacrylamide; N,N-dimethylacrylamide; dimethylaminoethyl acrylate; dimethylaminoethyl methacrylate; N-vinylpyrrolidone; N-vinylformamide; phosphoethyl methacrylate; allyl and methallyl alcohols, esters and ethers; acrylonitrile; vinyl acetate; and styrene. Monomers which do not contribute to the carboxylic, sulphonic or phosphonic acid functionality of the polymer may be present in the polymer at levels up to the point where the polymer is no longer water-soluble. Generally, monomers which do not contribute to the carboxylic, sulphonic or phosphonic acid functionality of the polymer will be present in the polymers at a level of below 50 percent by weight, preferably below 30 percent by weight. Anionic polymeric dispersants can be used in their acid forms, or they can be used in a partially or fully neutralized form. The anionic polymeric dispersants can be neutralized with my suitable base, such as alkali metal or ammonium hydroxides. Preferably, the anionic polymeric dispersant is fully neutralized with sodium hydroxide. The polymeric dispersants have a weight average molecular weight (M w ) of from 1,000 to 50,000 as measured by aqueous gel permeation chromatography (gpc). Where "M w " appears, it refers to the M w as measured by aqueous gpc. The method of preparing anionic polymeric dispersants is well known to those skilled in the art. The anionic polymers can be prepared by solvent, aqueous, or solvent-free processes. The art of preparing anionic polymeric dispersants has also employed various methods of controlling the molecular weight of polymers to produce polymers having M w below about 50,000. These methods include the use of chain transfer agents, metal activators and increased levels of initiators. In one embodiment of the present invention, it has been found to be beneficial to use as the one or more anionic polymeric dispersants, homopolymers or copolymers, including terpolymers, made using hypophosphites (such as sodium hypophosphite or ammonium hypophosphite) as a chain transfer agent. Suitable polymeric dispersants prepared using sodium hypophosphite as a chain transfer agent are taught, for example, in US 4,046,707 and 4,681,686. Particularly preferred polymeric dispersants prepared using sodium hypophosphite as a chain transfer agent are, for example, homopolymers of acrylic acid and salts thereof and copolymers of acrylic acid and maleic anhydride or maleic acid and salts thereof. The water-soluble alkali metal salts used in the present invention are alkali metal carbonates and alkali metal citrates. Preferred inorganic alkali metal salts are sodium carbonate and potassium carbonate. A preferred organic alkali metal salt is sodium citrate. The addition of the water-soluble alkali metal salt to the magnesium hydroxide slurry may affect the viscosity of the slurry. It is desirable to add the water-soluble alkali metal salts to provide an initial slurry viscosity of from 100 to 4,000 cps (0.1 to 4 Pa.s), preferably from 300 to 3,000 cps (0.3 to 3 Pa.s). It is also preferable that the alkali metal salt is added to the magnesium hydroxide slurry to a level which provides a weight ratio of alkali metal salt to polymeric dispersant of from 10:1 to 1:10, and most preferably from 2:1 to 1:2. The anionic polymeric dispersant is preferably added to the magnesium hydroxide slurry to a level which is within about 0.1 percent by weight (based on the weight of magnesium hydroxide) of the minimum viscosity dispersant dosage ("MVDD"). The minimum viscosity dispersant dosage is the level of dispersant beyond which there is no appreciable decrease in slurry viscosity. The actual MVDD will vary depending upon the type of polymeric dispersant and the solids level of the slurry. The minimum viscosity dispersant dosage for a given slurry can readily be determined by monitoring the viscosity of the slurry as the level of dispersant is increased. Determination of MVDD for a 50 Percent By Weight Slurry of Mg(OH) 2 The MVDD of the sodium salt of a polymer of 95 percent by weight acrylic acid and 5 percent by weight ethyl acrylate having M w 2,800 made using sodium metabisulfite as a chain transfer agent (referred to hereinafter as "Polymer A") was determined in a 50 percent by weight aqueous slurry of magnesium hydroxide in the following manner: To 500.0 grams of deionized water was added 225.0 grams of dried magnesium hydroxide. This mixture was stirred with a spatula for one minute. The pH of the mixture was 9.7. The polymeric dispersant was added as an aqueous solution of 45 percent by weight polymer solids to the aqueous mixture. This mixture was stirred with a spatula until it was completely mixed. The viscosity of the slurry was then measured at 23°C using a Brookfield viscometer, model RVT, spindle #2 at 20 revolutions per minute (rpm). Additional polymeric dispersant was added to the mixture and the viscosity was measured in the same manner as before. The data appear in Table I, below. The polymer level reported in Table I is the weight percent of PolymerA solids based on the weight of magnesium hydroxide. MVDD of Polymer A in a 50 Percent By Weight Slurry of Mg(OH) 2 Polymer A Level Viscosity (centipoises) 0.44 1450 0.49 665 0.54 264 0.57 120 0.59 60 0.62 42 0.64 30 0.67 30 0.70 30 The data in Table I show that the minimum viscosity dispersant dosage for the 50 percent by weight magnesium hydroxide slurry using the polymeric dispersant described above is 0.64 percent by weight based on the weight of magnesium hydroxide; at dispersant levels beyond 0.64 percent by weight, no decrease in viscosity was observed. Stability Test of Anionic Polymeric Dispersant Magnesium hydroxide slurries, to which only a polymeric dispersant has been added, were tested for stability over time. This is shown in Table II, below. Two magnesium hydroxide slurries were prepared with a polymeric anionic dispersant and the viscosity was measured as a function of time. The magnesium hydroxide slurries were made in the following way: the anionic polymeric dispersant was added to deionized water and diluted with additional deionized water to 225g. The anionic polymeric dispersant, designated Polymer B in the Tables below, was a 42 percent by weight aqueous solution of the sodium salt of a 3,500 M w poly(acrylic acid) made using sodium hypophosphite as a chain transfer agent. This mixture was stirred with a spatula until it was completely mixed. Then, 225.0g of dried magnesium hydroxide was added to the mixture and the mixture was stirred at high speed on a Waring blender for five minutes. The viscosity of the slurry was then measured at 23°C using a Brookfield viscometer, model RVT, spindle #2 at 20 rpm. The polymer level in Table II is the weight percent of polymer solids based on the weight of magnesium hydroxide. Polymer B Level Time (minutes) Viscosity (centispoises) 0.65 0 380 4 940 110 9,040 0.70 0 60 4 268 The data in Table II show that the magnesium hydroxide slurries to which only a polymeric dispersant has been added, are not stable over time. Dispersants do act to lower the viscosity of the magnesium hydroxide slurry, but the lower viscosity is not maintained. Stability Test of Anionic Polymeric Dispersant and Alkali Metal Salt By contrast, magnesium hydroxide slurries prepared in accordance with the present invention exhibit stability of viscosity over time. The magnesium hydroxide slurry appearing in Table III, below, was made in the same manner as the slurries appearing in Table II, above, except that 0.6 percent by weight based on the weight of magnesium hydroxide of Na 2 CO 3 was additionally added. PolymerB Level Na 2 CO 3 Level Time (minutes) Viscosity (centpoises) 0.6 0.6 0 1600 4 1119 110 970 The data appearing in Table III show that the magnesium hydroxide slurry made with a combination of an anionic polymeric dispersant and a water-soluble alkali metal salt is stable over time. The slurry viscosity did not increase in the course of 110 minutes. The slurry appearing in Table III was allowed to stand for four days. After four days, the slurry formed a loose gel. When this loose gel was disrupted with very slight agitation by a spatula, the slurry flowed from the inverted container without exhibiting hard-pack formation or gellation. The magnesium hydroxide slurries appearing in Table IV, below, were made in the following way: the anionic polymeric dispersant (Polymer B unless indicated otherwise) and the water-soluble alkali metal salt were added to deionized water and diluted with additional deionized water to 225.0g. This mixture was stirred with a spatula until it was completely mixed. Then, 225.0g of dried magnesium hydroxide was added to the mixture and the mixture was stirred at high speed on a Waring blender for five minutes. The viscosity of the slurry was then measured at 23°C using a Brookfield viscometer, model RVT, spindle #2 at 20 rpm. The polymer level reported in Table IV is the weight percent of polymer solids based on the weight of magnesium hydroxide. The salt level reported in Table IV is the weight percent of the alkali metal salt based on the weight of magnesium hydroxide. The viscosity results and observations on the stability of the slurry after standing for three days at room temperature appear in Table IV, below. Polymer Level Salt Level Salt Type Initial Viscosity (centipoises) 3 Day Stability none 0.6 Na 2 CO 3 --- none 0.6 Na 2 CO 3 2,350 none 0.6 sodium citrate --- 0.6 none -- 7,000 0.6 none -- 7,000 0.3 0.3 sodium citrate 9,950 0.4 0.4 sodium citrate 3,820 0.5 0.5 sodium citrate 740 0.6 0.6 sodium citrate 40 0.7 0.6 Na 2 CO 3 1,250 0.6 0.6 Na 2 CO 3 1,600 0.5 0.6 Na 2 CO 3 2,800 0.6 0.7 Na 2 CO 3 2,420 0.6 0.5 Na 2 CO 3 3,270 0.6 0.6 Na 2 CO 3 1,270 0.6 0.6 Na 2 CO 3 2,100 0.6 0.6 Na 2 CO 3 3,250 0.7 0.6 Na 2 CO 3 1,670 The data appearing in Table IV show that magnesium hydroxide slurries made without an anionic polymeric dispersant, or without a water-soluble alkali metal salt, do not flow from an inverted container after three days. The data also show that stable magnesium hydroxide slurries can be prepared according to the present invention with anionic polymeric dispersants having a variety of compositions and molecular weights. The data also show that stable magnesium hydroxide slurries can be prepared according to the present invention with various alkali metal salts. The magnesium hydroxide slurries appearing in Table V, below, were made in the same manner as the slurries appearing in Table IV. The slurries were maintained at a slightly elevated temperature, 27°C. After one hour and after 9 days, the viscosity of the slurry was then measured at 23°C using a Brookfield viscometer, model RVT, spindle #2 at 100 rpm. The polymer level reported in Table V is the weight percent of polymer solids based on the weight of magnesium hydroxide. The salt level reported in Table V is the weight percent of the alkali metal salt based on the weight of magnesium hydroxide. After 14 days at 27°C, the container holding the slurry was inverted. The percent by weight of the slurry which flowed from the container and other observations are reported in Table V in the column entitled "Stability" under the heading "No Mixing." The slurry was then gently stirred (2 to 4 revolutions) with a spatula; the percent by weight of the original slurry which flowed from the container and other observations are reported in Table V in the column entitled "Stability" under the heading "Mild Mixing." The slurry was then vigorously stirred (8 or 10 revolutions) with a spatula; the percent by weight of the original slurry which flowed from the container and other observations are reported in Table V in the column entitled "Stability" under the heading "Strong Mixing." The data reported in Table V as 100% does not include the weight of the residual slurry coating the surface of the container. The data appearing in Table V below shows that magnesium hydroxide slurries made without an anionic polymeric dispersant, or without an alkali metal salt, do not flow from an inverted container after 14 days. The data also show that stable magnesium hydroxide slurries can be prepared according to the present invention with anionic polymeric dispersants having a variety of compositions and molecular weights. The data also show that the viscosity of the slurries prepared according to the present invention are fairly constant after nine days.

Claims: A stabilized aqueous magnesium hydroxide slurry containing from 30 to 70% by weight, based on the weight of the slurry, of magnesium hydroxide and, as a stabilizer for the slurry, from 0.2 to 20% by weight, based on the weight of the magnesium hydroxide, of a polymeric anionic dispersant having a weight average molecular weight, as determined by aqueous gel permeation chromatography of from 1000 to 50000, or salt thereof, characterized in that the slurry also contains from 0.2 to 20% by weight, based on the weight of the magnesium hydroxide, of at least one water-soluble salt of an alkali metal, which salt is selected from alkali metal carbonates and alkali metal citrates, and further characterized in that the slurry has an initial viscosity of from 100 to 4000 cps (0.1 to 4 Pa.s). An aqueous magnesium hydroxide slurry according to claim 1 wherein the polymeric anionic dispersant is a homopolymer or copolymer of one or more of acrylic acid, methacrylic acid, crotonic acid, maleic acid, maleic anhydride, itaconic acid, mesaconic acid, furmaric acid, citraconic acid, vinylacetic acid, acryloxypropionic acid, vinylsulfonic acid, styrenesulfonic acid, 2-acrylamido-2- methylpropanesulfonic acid, allylsulfonic acid, allylphosphonic acid, vinylphosphonic acid, or vinylsulfonic acid, or a salt of such a homopolymer or copolymer. An aqueous magnesium hydroxide slurry according to claim 2 wherein the polymeric anionic dispersant is a homopolymer of acrylic acid, a copolymer of acrylic acid and ethyl acrylate, a copolymer of acrylic acid and maleic acid or a salt of such a homopolymer or copolymer. An aqueous magnesium hydroxide slurry according to any one of the preceding claims wherein the polymeric anionic dispersant is added to the slurry as a fully neutralized salt. An aqueous magnesium hydroxide slurry according to any one of the preceding claims wherein the polymeric anionic dispersant is a homopolymer or copolymer which has been obtained using a hypophosphite as a chain transfer agent in the polymerization process. An aqueous magnesium hydroxide slurry according to any one of the preceding claims, which has an initial viscosity of from 300 to 3000 cps (0.3 to 3 Pa.s). An aqueous magnesium hydroxide slurry according to any one of the preceding claims, containing from 40 to 60% by weight, based on the weight of the slurry, of magnesium hydroxide, from 0.3 to 10% by weight, based on the weight of the magnesium hydroxide, of the polymeric anionic dispersant, and from 0.3 to 10% by weight, based on the weight of the magnesium hydroxide, of the alkali metal salt. An aqueous magnesium hydroxide slurry according to any one of the preceding claims, wherein the weight ratio of the alkali metal salt to polymeric anionic dispersant is from 10:1 to 1:10. An aqueous magnesium hydroxide slurry according to claim 8 wherein the weight ratio of the alkali metal salt to polymeric anionic dispersant is from 2:1 to 1:2.

Inventors: MAHAR ROBERT CROUSE, MAHAR, ROBERT CROUSE
Applicants: ROHM & HAAS, ROHM AND HAAS COMPANY
Application year: 1993
Main classification: C01F5
IPC codes: A61K47, A61K8, B28C1, B01J13, A61Q11, C01F5, A61K33