HIGH WATER SOLUBILITY POTASSIUM SULFATE AND METHOD OF PRODUCING SAME

Abstract: Improved potassium sulfate salt products in both solid particulate and liquid form are provided which exhibit enhanced salt solubility in water. The products include potassium sulfate, in combination with a surfactant and mixed together in water. The aqueous mixture is heated to a maximum reaction temperature in the range of about 100-210 DEG F, and will retain enhanced water solubility in either a heated or cooled condition. In preferred forms, potassiums sulfate may be treated with at least 0.1 % by weight of disulfonate surfactant and heated in water to 100-140 DEG F to give K>2<SO>4< solutions of at least 8 % by weight solubility taken as K>2<O.

Description: HIGH WATER SOLUBILITY POTASSIUM SULFATE AND METHOD OF PRODUCING SAME Background of the Invention 1. Field of the Invention The present invention is broadly concerned with improved potassium sulfate salt products having enhanced water solubility permitting them to be used with greater efficiency as liquid, spray-on fertilizer products. More particularly, it is concerned with such improved potassium products, as well as a method of producing the same, wherein potassium sulfate is mixed with water and an appropriate surfactant and optional defoamer and subjected to heating to a temperature of from about 100-210°F; the solution, when cooled, exhibits a significantly increased potassium sulfate solubility as compared with untreated potassium sulfate solutions. 2 . Description of the Prior Art Potassium sulfate, potassium chloride and potassium nitrate are all used as fertilizer products to a greater or lesser degree. Potassium chloride is the most widely used potassium salt, but is inapplicable for chloride and/or salt-sensitive crops such as tobacco, fruits, vegetables and turfs. However, KC1 has a signif¬ icant water solubility on the order of 14-16% as K 2 0, and therefore this salt is often applied as a liquid. Potassium sulfate (commonly referred to in the trade as sulfate of potash or SOP) is a premium fertilizer product. Certain grades of SOP, particularly those manufactured from the brine of the Great Salt Lake, are especially valuable products because they are essentially free of chlorides. Therefore, such products are admirably suited for use on chloride and/or salt-sensitive crops and the like. A drawback of SOP, however, is that in its natural state it is significantly less soluble in water than KCl, having an ambient temperature solubility of about 4-6% by weight as K 2 0. This relatively low water solubility has inhibited the use of K 2 S0 4 as a liquid fertilizer product, despite its otherwise significant advantages. Potassium nitrate is more soluble than SOP, normally about 9-11% by weight as K 2 0, but is a very expensive product as compared with KCl or K 2 S0 4 . Neverthe- less, it has achieved some commercial utility as a liquid fertilizer source, owing at least in part to its low salt index. It will of course be appreciated that enhance¬ ment of the solubility of potassium sulfate salts would represent a significant advance. Such an improvement would mean that more concentrated solutions could be prepared and applied, thereby lessening preparation, storage and transportation costs associated with the liquids. Summary of the Invention The present invention overcomes the problems outlined above, and provides improved potassium sulfate products (both solids and liquids) which exhibit material- ly improved water solubilities. Broadly, the potassium sulfate products of the invention are supplemented with an appropriate surfactant and optional defoamer. In prepar¬ ative procedures, the potassium sulfate and surfactant are present in a water solution, and the mixture is heated to a temperature in the range of from about 100-210°F. In one aspect of the invention, a particulate potassium sulfate product is provided which includes potassium sulfate, with a surfactant and optional defoamer applied onto the surface thereof for increasing the solubility of the resultant product in water. This surfactant is present at a level of at least about 0.1% by weight, more preferably at least 0.25% by weight, and most preferably from about 0.30-0.50% by weight, based upon the weight of the nominally dry potassium sulfate. It will be appreciated in this respect that a substantial excess of surfactant could be employed without detracting from the water solubility of the potassium sulfate; however, this is disfavored from an economic standpoint. The preferred surfactants for use in the inven- tion are selected from the group consisting of the disul¬ fonate and oxyalkylated alcohol-carboxylic acid adduct surfactants. In the former class, the alkyl diphenyl ether disulfonates are preferred, wherein the alkyl group contains from about 8-22 carbon atoms, and more particu- larly from about 10-18 carbon atoms. Moreover, the alkyl group of the disulfonate is preferably linear. The second class of preferred surfactants are those selected from the group consisting of surfactants having the general formula R-0-(CH-CH-0) n H X wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. Particularly preferred are the succinic acid derivatives wherein the hydrophobe has a carbon number of from about 9-16. In a related aspect of the invention, aqueous potassium sulfate solutions are provided which comprise water, dissolved potassium sulfate and a surfactant of the type and in the amounts described previously; a defoamer may also optionally be used. The method of increasing solubility of the invention comprises the steps of mixing together water, one or more of the recited potassium sulfate, and a surfactant and optional defoamer of the types and amounts specified in connection with the particulate products. The mixture is then heated to an elevated reaction temper¬ ature of from about 100-210°F, preferably with agitation or stirring. In this respect, it has been found that increasing the reaction temperature has a positive effect upon solubility. However, for overall reasons of ease of processing and handling, and fuel economy, it is believed that a K 2 S0 4 solution having > 8% solubility as K 2 0 is commercially feasible. These types of solutions can readily be produced using a maximum reaction temperature on the order of 100-140°F. After the maximum reaction temperature is achieved, it may be held at this maximum temperature for a short time (e.g., 5 minutes) whereupon the solution is allowed to cool, again with at least occasional agitation or stirring, to approximately room temperature (i.e., 68- 75°F) . It has been discovered that potassium sulfate particulates (preferably having a size range of Tyler mesh 48-150) can be sprayed with one or more of the preferred surfactants (and optionally a defoamer) at the indicated levels without extended drying, and that this product can be appropriately stored and shipped to a remote location in proximity to a point of use. Thereupon, the postassium sulfate/surfactant product can be dissolved in hot water, or placed in cold water and heated to a minimum reaction temperature and cooled to about ambient. This liquid is then eminently suited for spray application onto a crop or turf grass, or direct application to the soil. The dissolved salt content as K 2 0 will not significantly decrease over time, and no salting out or precipitation should occur. To give one specific example, a 100 pound sample of K 2 S0 4 can be sprayed with 0.4% by weight of a preferred disulfonate surfactant, which will adequately adhere to the K 2 S0 4 without drying or other steps. This amount of SOP can then be dissolved in 66 gallons of water and heated to a temperature of 110-120°F. The product will then have a minimum of 8% solubility as K 2 0, with a surfactant content on the order of 615 ppm. Brief Description of the Drawings Figure 1 is a graphical representation illus¬ trating comparative tests with K 2 S0 4 , and showing the effect of treating the potassium sulfate with surfactant in water, followed by heating. Detailed Description of the Preferred Embodiments As indicated above, one preferred class of surfactants for use in the present invention is the disulfonates, and particularly the alkyl diphenyl ether disulfonates. Two particular products which have been found to be useful are the Poly-Tergent 2A1-L anionic surfactant and the Poly-Tergent 3B2 anionic surfactant, both of which are commercialized by Olin Chemicals of Stamford, CT. The 2A1-L surfactant is a linear dodecyl di¬ phenyl ether sodium disulfonate, having a freezing point of 32°F, a boiling of 212°F, a specific gravity of 1.16, a bulk density of 9.15 lb/gal., a pH at 25°C of greater than 9, and a vapor pressure at 25°C of 23.7 mm Hg. This product is further defined in an Olin Product Data Sheet entitled "Poly-Tergent 2A1 Acid and Poly-Tergent 2A1 Anionic Surfactant", and the associated Material Safety Data Sheets, all of which are incorporated by reference herein. The Poly-Tergent 3B2 anionic surfactant is a decyl diphenyl ether sodium disulfonate having essentially the same physical properties as the 2A1-L surfactant. The 3B2 surfactant is described in an Olin Product Data Sheet entitled "Poly-Tergent 3B2 Acid and Poly-Tergent 3B2 Anionic Surfactant", and the associated Material Safety Data Sheets; these publications are incorporated by reference herein. Another disulfonate of interest is the Poly- Tergent 4C3 anionic surfactant commercialized by Olin Chemical. This is the sodium salt of hexadecyl diphenyl ether disulfonic acid. Its physical data vary slightly as compared with the 2A1-L and 3B2 surfactants. This product is described in an Olin Product Data Sheet entitled "Poly- Tergent 4C3 Anionic Surfactant" and the related Material Safety Data Sheets, and these materials are incorporated by reference herein. One type of the oxyalkylated alcohol-carboxylic acid adduct surfactants preferred for use in the invention is the Poly-Tergent C-series surfactants commercialized by Olin Chemical. This series is a family of 9 polycarboxyl- ated surfactants having the formula described previously. Particularly preferred members of this class are the succinic acid derivative products, with hydrophobes having an average carbon length ranging from C 9 -C 16 . This class of surfactants is described in an Olin Product Data Sheet entitled "Poly-Tergent C-Series Polycarboxylated Multi¬ functional Surfactants", and the related Material Safety Data Sheets, all of which are incorporated by reference herein. In some instances, it may be advisable to add a very minor amount of a defoamer to the potassium sulfate salt products of the invention, in order to minimize foaming during heating and stirring. One suitable de- foamer is a product commercialized under the name "Foam Ban Co" by Ultra Additives, Inc. of Patterson, NJ. This proprietary product contains polyalkylene glycol as well as an oxyalkylene polymer, and is known to be useful as an anti-foam/defoa er agent. The potassium sulfate of the invention can be derived from virtually any commercial source. However, use of the Soluble Fine grade of potassium sulfate sold by Great Salt Lake Minerals Corporation is particularly preferred. This material is in itself a premium product, which is free of KCl. Therefore, this K 2 S0 4 is especially suited for applications where significant chloride ion cannot be tolerated. The following examples are illustrative of the present invention. It should be understood, however, that these examples are to be taken by way of illustration only, and nothing therein should be considered as a limitation upon the overall scope of the invention. Example 1 In this series of tests, samples of reagent grade K 2 S0 4 were treated with surfactant alone and in the presence of certain additional salts, in order to deter¬ mine the resulting enhancement in K 2 S0 4 solubility. In each test, a quantity of water was mixed with 1.2 g of the previously described Poly-Tergent 2A1-L surfactant along with an appropriate amount of K 2 S0 4 , and in certain cases MgS0 4 , MgCl 2 -6H 2 0, Na 2 S0 4 , NaCl and KCl. The ingredients were then mixed and heated to a maximum temperature and held for 5 minutes. The mixture was then allowed to cool with stirring to approximately 70-72°F, whereupon the mixture was filtered and the liquor was analyzed for salt and ingredient content. The respective liquors were then cooled in a refrigerator over a weekend to a temperature of about 35-37°F, stirred several times and then filtered. The secondary filtrates were then tested for salt and ingredient content. In Run #1, the surfactant was mixed with 830 g of water and 300 g K 2 S0 4 . This mixture was heated to 192°F and held for 5 minutes, whereupon it was first-stage cooled with stirring to 71°F, filtered and analyzed. The recovered liquor was then second-stage cooled (refrigerat¬ ed) as described previously to 35°F, stirred, refiltered and again analyzed. A 30 ml portion of the final refil- tered liquor was diluted with 200 ml of water and the pH was measured. All of the succeeding runs were carried out as described, with the following changes in ingredients and processing parameters. Run #2: 861 g water, 200 g K 2 S0 4 , and 70 g MgS0 4 ; maximum heating temperature was 192°F and first-stage cooling was carried out to a temperature of 72°F, and second-stage cooling to 35°F. Run #3: 813 g water, 200 g K 2 S0 4 , 118 g MgCl 2 -6H 2 0; maximum heating temperature was 194°F; first- stage cooling to 72°F, and second-stage cooling to 35°F. Run #4: 848 g water, 200 g K 2 S0 4 , 83 g Na 2 S0 4 ; maximum heating temperature was 200°F; first-stage cooling to 72°F, and second-stage cooling to 35°F. Run #5: 863 g water, 200 g K 2 S0 4 , 68 g NaCl; maximum heating temperature was 200°F; first-stage cooling to 71°F, and second-stage cooling to 35°F. Run #6: 844 g water, 200 g K 2 S0 4 , 87 g KCl; maximum heating temperature was 200°F; first-stage cooling to 72°F, and second-stage cooling to 35°F. Run #7: 931 g water, 200 g K 2 S0 4 ; maximum heating temperature was 206°F; first-stage cooling to 71°F, and second-stage cooling to 35°F. The following table sets forth the results of these test runs after the first-stage cooling analysis, where all percentages are on a weight basis: Table 1 'Theoretical K 2 S0 4 refers to the percentage of untreated K 2 S0 4 in water solution at the selected cooling temperature of analysis. 2 Actual K 2 S0 4 refers to the percentage of treated K 2 S0 4 actually in solution at the cooling temperature of analy¬ sis. 3 K 2 0 is a calculated value determined by the equation K 2 0 = (%K) x (1.2046). Table 2 gives the test results after second- stage cooling. Table 2 The foregoing data demonstrates the significant increases in K 2 S0 4 solubility derived from the addition of surfactant and heating in accordance with the present invention. The advantageous results are particularly evident at the higher room temperatures (70-72°F) of Table 1. Example 2 In this test, a number of runs were carried out at different maximum heating temperatures, in order to determine the maximum temperature level needed to produce the highest K 2 S0 4 solubility. In each test, identical amounts of water. Soluble Fine Potash (Great Salt Lake Minerals Corp.) and 1090 ppm Poly-Tergent 2A1-L were mixed and heated to various maximum temperatures, whereupon the mixtures were first-stage cooled with occasional stirring to 70°F, filtered and the filtrate was analyzed to deter¬ mine %K 2 0; thereafter, the solutions were second-stage cooled for 3 days in a refrigerator to 35°F, refiltered and reanalyzed for %K 2 0 in the filtrate. These results are set forth below: Table 3 As can be seen, the best solubility results in this series of tests were obtained using a maximum heating and reaction temperature in the range of from about 130- 210°F. Example 3 In this example, a number of other commercially available surfactants were tested to ascertain their utility in the context of the invention. In each test run, 400 g water was mixed with an amount of a surfactant and 90 g K 2 S0 4 . Each mixture was then heated with stirring to 200°F, and thereupon cooled with stirring to 72°F. The respective samples were then filtered and analyzed to determine %K 2 0. These results are set forth below, and should be compared with a theoretical %K 2 0 for untreated K 2 S0 4 at 72°F of 5.6%. Table 4 The surfactants of Runs #1-5 were several years old, whereas the reagents of Runs #6-8 were fresh. The surfactants of Table 4 are further identified as follows: Astrowet 075: Sodium dioctyl sulfosuccinate (CAS #577-11-7); Alco Chemical Corp., Chattanooga, TN; Alcosperse 149: Sodium polyacrylate (CAS #9003- 04-7); Alco Chemical Corp., Chattanooga, TN; Dowfax 2A1-L: Benzene 1,1-oxybis tetrapropylene derivatives/sulfonated sodium salts (CAS #119345-04-9) ; Dow Chemical Company, Midland, MI; Desoto Desonate AOS: Now designated Witconate A08; Alkyl (C 14 -Cι 6 ) olefin sulfonate sodium salt (CAS #68439-57-6) ; Witco Organics Division, Houston, TX; Acrysol LMW45NX: Low molecular weight poly- acrylic acid, 20% NaOH neutralized; Rohm & Haas Co. , Philadephia, PA; Cyanamid Aero 845 Promoter: Sulfosuccinate mixture; American Cyanamid Co. , Wayne, NJ; and Sherex 83A: 1,3 propane diamine N-(3-branched tridecyloxypropyl) (CAS #68479-04-9) ; Sherex Chemical Co. , Dublin, OH. The Dowfax 2A1-1 and Cyanamid Aero 845 Promoter products gave results very similar to the surfactants used in Examples 1 and 2, whereas the remaining surfactants were less effective. In order to ascertain the degree of utility of these surfactants, they were further tested by varying the amounts of use thereof. It was determined that a concentration level of about 1000-2000 ppm of these surfactants will achieve maximum results. In another test series, it was determined that the Sherex 83A was less effective than the Cyanamid Aero 845 Promoter, and that the presence of MgS0 4 did increase K 2 S0 4 solubility. This latter series of tests further demonstrated that heating was required in order to achieve increased K 2 S0 4 solubil¬ ity. Example 4 In this test, the solubility effect of Poly- Tergent 2A1-L on reagent grade K 2 S0 4 with and without MgS0 4 was tested; also, the effect of different maximum tempera- tures on the cooled solutions was ascertained. In each K 2 S0 4 -only test, 100 g of reagent grade K 2 S0 4 was mixed in 400 g of water and 1130 ppm of the Poly-Tergent 2A1-L surfactant. In the companion tests, 100 g of reagent grade K 2 S0 4 , and 70 g of MgS0 4 were mixed in 400 g of water with 1130 ppm of the surfactant. The respective test mixtures were then heated to different maximums, and first-stage cooled with stirring to 67-68°F, whereupon they were filtered and the filtrate analyzed to determine %K 2 0. Thereafter, the mixtures were second-stage cooled in a refrigerator to 35-40°F for 3 days, stirred , refiltered and reanalyzed. The test results are set forth in the following tables: Table 5 Reagent Grade K^SO,, Table 6 Reagent Grade K ? SQ 1 With MgSO., The theoretical %K 2 0 values for Table 5 are 5.4% at 67°F and 4.0% at 36°F; for Table 6, they are 5.4% at 67°F and 4.1% at 39°F. Example 5 In this test, a number of samples of reagent grade K 2 S0 4 were tested with varying amounts of the Poly- Tergent 2A1-L surfactant. The respective test procedures are set forth below: Run #1: 0.71 g of the surfactant was mixed with 800 g water, and 200 g reagent grade K 2 S0 4 . The mixture was heated with stirring to 150°F, whereupon it was first- stage cooled with stirring to 73°F, filtered, analyzed, and second-stage cooled to 37°F, refiltered and further analyzed. Run #2: 200 g reagent grade K 2 S0 4 was mixed with 800 g water and heated to 162°F with stirring. After 5 minutes at 162°F, 0.72 g of the Poly-Tergent 2A1-L surfac¬ tant were added, whereupon the mixture was cooled with stirring to 73°F, filtered and analyzed. Run #3: 0.44 g of the 2A1-L surfactant were mixed with 400 g of water and 100 g of reagent grade K 2 S0 4 . The mixture was heated with stirring to 160°F, held for 5 minutes at that temperature and cooled with stirring to 73°F. The mixture was then filtered and the filtrate was analyzed. Run #4: 0.32 g of the 2A1-L surfactant were mixed with 400 water and 100 g of reagent grade K 2 S0 4 . The mixture was heated with stirring to 156°F, held at that temperature for 5 minutes, and cooled overnight with occasional stirring to 73°F. The mixture was then fil¬ tered and the filtrate analyzed. The following table sets forth the results of these tests. Table 7 Example 6 In this study, reaction conditions and surfac¬ tant amounts were optimized for the production of K 2 S0 4 solutions having %K 2 0 values above 8%. In the first aspect of this study, a temperature/solubility profile was completed using a series of samples prepared at a level of 0.5% surfactant based upon the weight of potassium sul¬ fate. Specifically, in each test sample, 45 g of K 2 S0 4 were mixed in 200 ml of water, and sufficient surfactant was added to achieve the 0.5% by weight level, based upon the weight of the K 2 S0 4 . The surfactants used were the Poly-Tergent 3B2 and 2A1-L material described above. The respective solutions were heated with stirring to tempera¬ tures of 68°F and between 80-150°F in increments of 10°F. After the final selected reaction temperature was reached, the solutions were cooled to 68°F in a cold water bath, with stirring. Thereafter, the solutions were filtered and analyzed by atomic absorption spectroscopy. The results of this study are set forth in the following table. Table 8 Both of the test surfactants gave %K 2 0 values greater than 8% at 110°F. In several instances, the 3B2 surfactant appeared to give higher percent solubility as compared with the 2A1-L material at the same temperatures, especially between 80-120°F. Using this data, a reaction temperature of 110°F was selected for continued work, and all solutions were retained to evaluate stability of the soluble potassium sulfate. In another aspect of this study, a second set of samples was analyzed for %K 2 0 using various surfactant concentrations and a maximum reaction temperature of 110°F with subsequent cooling, filtering and analysis at 68°F. Each sample again was made up of 45 g K 2 S0 4 , 200 ml of water and 3B2 and 2A1-L surfactant concentrations ranging from 0.05-.5% by weight, based upon the weight of K 2 S0 4 , in increments of 0.05 weight-percent. It was determined that the 3B2 surfactant gives approximately 8.5% K 2 0 at 0.3-0.5% by weight surfactant, and the 2A1-L material gave approxi- ately the same performance. These samples were also retained for stability studies. In a final aspect of this test, filtrate samples from the temperature/solubility profile and concentration/ solubility profile tests were stored at room temperature (about 68-72°F) . The temperature study samples were all slightly cloudy after filtering the undissolved sulfate. In 24 hours, the turbidity had settled to the bottom of the sample bottles, resembling a thin layer of brown dust, while the samples were clear. Solutions prepared at temperatures up to 120°F were the same after 7 days. Solutions heated to 130°F and higher developed a very small amount of white crystalline precipitate in addition to the brown precipitate. The samples prepared at 100°F and 110°F exhibited good stability with only a very small amount of brown precipitate on the flask bottoms. The concentration study samples were initially similar to the temperature study samples, except for the blank which was clear. A brown precipitate formed after settling overnight as well. Samples containing 0.15% by weight surfactant and lower amounts began to precipitate white crystalline sulfate as well as increasing amounts of brown precipitate after 3 days. After 6 days, all samples at and below 2.5% by weight surfactant had the same precipitate, with the blank showing traces of brown material. The samples at 0.3% and higher surfactant showed some small increases in amounts of brown precipi¬ tate. Based upon this study, it was determined that to obtain a minimum 8% K 2 0 solution, the surfactant should be present at a level of from about 0.3-0.5% by weight, based upon the weight of the K 2 S0 4 . Moreover, the maximum reaction temperature should be on the order of 100-160°F, most preferably about 110°F for reasons of speed and ease of reaction. Fig. 1 illustrates in graphical form the effect of the surfactant/heating treatment of the invention as determined by this series of tests. The untreated/un- heated bar represents the solubility of straight K 2 S0 4 in water, which is about 5.7% taken as K 2 0. The second bar, untreated/heated, illustrates that simply heating a solution of K 2 S0 4 to a reaction temperature in accordance with the invention does not enhance salt solubility. Likewise, treatment of the K 2 S0 4 with surfactant without heating has no appreciable effect. However, the last bar (treated/heated) , demonstrates that the combined effect of surfactant and heating markedly increases K 2 S0 4 solubility in water.

Claims: Claims : 1. A potassium sulfate salt product having enhanced water solubility and comprising dry postassium sulfate salt having applied onto the surface thereof a surfactant for increasing the solubility of the postassium sulfate in water, said surfactant being present at a level of at least about 0.1% by weight, based upon the weight of said dry potassium sulfate salt. 2. The product of claim 1, said surfactant being present at a level of from about 0.30-0.50% by weight. 3. The product of claim 1, said surfactant being selected from the group consisting of disulfonate and oxyalkylated alcohol-carboxylic acid adduct surfact¬ ants. 4. The product of claim 3, said surfactant comprising a surfactant selected from the group consisting of the alkyl diphenyl ether disulfonates. 5. The product of claim 4, wherein the alkyl group of said disulfonate contains from about 8-22 carbon atoms. 6. The product of claim 5, wherein said alkyl group contains from about 10-18 carbon atoms. 7. The product of claim 5, wherein the alkyl group of said disulfonate is linear. 8. The product of claim 3, said oxyalkylated alcohol-carboxylic acid adduct surfactant being selected from the group consisting of surfactants having the general formula R-0-(CH-CH-0) n H X Y wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. 9. The product of claim 1, further including an amount of MgS0 4 . 10. An aqueous potassium sulfate salt solution comprising water, dissolved potassium sulfate and a surfactant for increasing the solubility of said dissolved sulfate, said surfactant being present at a level of at least about 0.1% by weight, based upon the weight of said potassium sulfate. 11. The product of claim 10, said surfactant being present at a level of from about 0.3-0.5% by weight. 12. The product of claim 10, said surfactant being selected from the group consisting of disulfonate and oxyalkylated alcohol-carboxylic acid adduct surfact- ants. 13. The product of claim 12, said surfactant comprising a surfactant selected from the group consisting of the alkyl diphenyl ether disulfonates. 14. The product of claim 13, wherein the alkyl group of said disulfonate contains from about 8-22 carbon atoms. 15. The product of claim 14, wherein said alkyl group contains from about 10-18 carbon atoms. 16. The product of claim 13, wherein the alkyl group of said disulfonate is linear. 17. The product of claim 13, said oxyalkylated alcohol-carboxylic acid adduct surfactant being selected from the group consisting of surfactants having the general formula R-0-(CH-CH-0) n H X Y wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. 18. The product of claim 10, further including an amount of MgS0 4 . 19. A method of increasing the solubility of potassium sulfate in water, comprising the steps of heating a mixture including water, a quantity of potassium sulfate salt, and at least about 0.1% by weight surfac¬ tant, based upon the weight of said postassium sulfate salt, to a temperature of from about 100-210°F for in¬ creasing the solubility of said potassium sulfate in said water. 20. The method of claim 19, including the step of heating said mixture with agitation. 21. The method of claim 19, including the step of cooling said mixture after said heating thereof to approximately ambient temperature. 22. The method of claim 21, said surfactant being present at a level of from about 0.30-0.50% by weight. 23. The method of claim 19, said surfactant being selected from the group consisting of disulfonate and oxyalkylated alcohol-carboxylic acid adduct surfact¬ ants. 24. The method of claim 23, said surfactant comprising a surfactant selected from the group consisting of the alkyl diphenyl ether disulfonates. 25. The method of claim 24, wherein the alkyl group of said disulfonate contains from about 8-22 carbon atoms. 26. The method of claim 25, wherein said alkyl group contains from about 10-18 carbon atoms. 27. The method of claim 25, wherein the alkyl group of said disulfonate is linear. 28. The method of claim 19, including the step of first mixing together said water, potassium sulfate, and surfactant, and thereafter heating said mixture. 29. The method of claim 24, said oxyalkylated alcohol-carboxylic acid adduct surfactant being selected from the group consisting of surfactants having the general formula R-0-(CH-CH-0) n H X Y wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. 30. The method of claim 19, further including an amount of MgS0 4 . [received by the International Bureau on 11 January 1994 (11.01.94); original claims 1, 10, 19, 30 amended; other claims unchanged (6 pages)] 1. A potassium sulfate salt product having enhanced water solubility and consisting essentially of dry potassium sulfate salt having applied onto the surface thereof a surfactant for increasing the solubility of the potassium sulfate in water, together with a minor amount of a magnesium source selected from the group consisting of sources of magnesium chloride, magnesium sulfate, and mixtures thereof, said surfactant being present at a level of at least about 0.1% by weight, based upon the weight of said dry potassium sulfate salt, said product, when mixed with sufficient water to form a solution and heated, having a potassium sulfate solubility calculated as K 2 0 of at least about 8%. 2. The product of claim 1, said surfactant being present at a level of from about 0.30-0.50% by weight. 3. The product of claim 1, said surfactant being selected from the group consisting of disulfonate and oxyalkylated alcohol-carboxylic acid adduct surfact¬ ants. 4. The product of claim 3, said surfactant comprising a surfactant selected from the group consisting of the alkyl diphenyl ether disulfonates. 5. The product of claim 4, wherein the alkyl group of said disulfonate contains from about 8-22 carbon atoms. 6. The product of claim 5, wherein said alkyl group contains from about 10-18 carbon atoms. 7. The product of claim 5, wherein the alkyl group of said disulfonate is linear. 8. The product of claim 3, said oxyalkylated alcohol-carboxylic acid adduct surfactant being selected from the group consisting of surfactants having the general formula X Y wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. 9. (Canceled) 10. An aqueous potassium sulfate salt solution comprising water, dissolved potassium sulfate and a surfactant for increasing the solubility of said dissolved sulfate, said surfactant being present at a level of at least about 0.1% by weight, based upon the weight of said potassium sulfate, said water being present in an amount by weight greater than the weight amounts of said potassi¬ um sulfate and surfactant, the potassium salt fraction of said solution consisting essentially of potassium sulfate, said potassium sulfate solution having a potassium sulfate solubility calculated as K 2 0 of at least about 8%. 11. The product of claim 10, said surfactant being present at a level of from about 0.3-0.5% by weight. 12. The product of claim 10, said surfactant being selected from the group consisting of disulfonate and oxyalkylated alcohol-carboxylic acid adduct surfact- ants. 13. The product of claim 12, said surfactant comprising a surfactant selected from the group consisting of the alkyl diphenyl ether disulfonates. 14. The product of claim 13, wherein the alkyl group of said disulfonate contains from about 8-22 carbon atoms. 15. The product of claim 14, wherein said alkyl group contains from about 10-18 carbon atoms. 16. The product of claim 13, wherein the alkyl group of said disulfonate is linear. 17. The product of claim 13, said oxyalkylated alcohol-carboxylic acid adduct surfactant being selected from the group consisting of surfactants having the general formula X wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. 18. The product of claim 10, further including an amount of MgS0 4 . 19. A method of increasing the solubility of potassium sulfate in water, comprising the steps of heating a mixture including water, a quantity of potassium sulfate salt, and at least about 0.1% by weight surfac¬ tant, based upon the weight of said potassium sulfate salt, to a temperature of from about 100-210°F for in¬ creasing the solubility of said potassium sulfate in said water, said water being present in an amount by weight greater than the weight amounts of said potassium sulfate and surfactant, the potassium salt fraction of said mixture consisting essentially of potassium sulfate said potassium sulfate mixture having a potassium solubility calculated as K 2 0 of at least about 8%. 20. The method of claim 19, including the step of heating said mixture with agitation. 21. The method of claim 19, including the step of cooling said mixture after said heating thereof to approximately ambient temperature. 22. The method of claim 21, said surfactant being present at a level of from about 0.30-0.50% by weight. 23. The method of claim 19, said surfactant being selected from the group consisting of disulfonate and oxyalkylated alcohol-carboxylic acid adduct surfact¬ ants. 24. The method of claim 23, said surfactant comprising a surfactant selected from the group consisting of the alkyl diphenyl ether disulfonates. 25. The method of claim 24, wherein the alkyl group of said disulfonate contains from about 8-22 carbon atoms. 26. The method of claim 25, wherein said alkyl group contains from about 10-18 carbon atoms. 27. The method of claim 25, wherein the alkyl group of said disulfonate is linear. 28. The method of claim 19, including the step of first mixing together said water, potassium sulfate, and surfactant, and thereafter heating said mixture. 29. The method of claim 24, said oxyalkylated alcohol-carboxylic acid adduct surfactant being selected from the group consisting of surfactants having the general formula X Y wherein R is a C 8 -C 22 hydrophobe, X and Y are individually selected from the group consisting of H, CH 3 and a succinic acid radical, and n ranges from about 1-8. 30. The method of claim 19, further including the step of adding an amount of a magnesium ion source selected from the group consisting of sources of MgCl 2 , MgS0 and mixtures thereof to said mixture.

Inventors: MCLAUGHLIN J C, NASON DANTON S, PREST JOHN R JR, MCLAUGHLIN, J., C., NASON, DANTON, S., PREST, JOHN, R., JR.
Applicants: GREAT SALT LAKE MINERALS, MCLAUGHLIN J C, NASON DANTON S, PREST JOHN R JR, GREAT SALT LAKE MINERALS CORPORATION
Application year: 1993
Main classification: C01D5
IPC codes: C01D5, C05D1