PARTICULATE CaF2 AGENT FOR IMPROVING THE MACHINABILITY OF SINTERED IRON-BASED POWDER

Abstract: The invention relates to an additive for improving the machinability of iron-based powder compositions. The additive contains calcium fluoride particles which are included in an amount of 0.1-0.6 % by weight in the powder composition. The invention further relates to powder compositions containing the additives indicated, as well as sintered products produced from the powder compositions.

Description: Par t iculate CaF2 agent for improving the machinabi1 ity of sintered iron-based powder. The present invention relates to a machinability- improving powder to be added to an iron-based powder composition for use in powder-metallurgical manufacture of components. Powder-metallurgical manufacture of components often involves the following process steps. A base powder, gene¬ rally an iron or steel powder, is admixed with alloying elements, such as nickel, copper, molybdenum and carbon, in the form of a powder, and a lubricant. The powder mix¬ ture is thereafter compacted in a press tool yielding what is known as a green body of almost final geometry. After compacting, the compact is sintered so as to obtain its final strength, hardness, elongation etc. One of the major advantages of powder-metallurgical manufacture of components is that it becomes possible, by compacting and sintering, to produce blanks of final or very close to final shape. There are however instances where subsequent machining is required. For example, this may be necessary because of high tolerance demands or because the final component has such a shape that it can¬ not be pressed directly but requires machining after sin¬ tering. More specifically, geometries such as holes trans- verse to the compacting direction, undercuts and threads, call for subsequent machining. By continuously developing new sintered steels of higher strength and thus also higher hardness, machining has become one of the major problems in powder-metallur- gical manufacture of components. It is often a limiting factor when assessing whether powder-metallurgical manu¬ facture is the most cost-effective method for manufactur¬ ing a component. Hence, there is a great need for new and more effective additives to improve the machinability of sintered steels. It then is important that this additive does not appreciably affect the mechanical properties, such as tensile strength and elongation, of the sintered material. Today, there are a number of known substances which are added to iron-based powder mixtures to facilitate the machining of components after sintering. The commonest powder additive is MnS, which is men¬ tioned e.g. in EP 0 183 666, describing how the machin- ability of a sintered steel is improved by the admixture of such powder. Materials which are difficult to machine, in this context materials having a hardness above about 180 HV, cannot however be machined properly by adding MnS. Moreover, the addition of MnS often entails an unaccept¬ able reduction of the strength of the material after sin¬ tering. US 4,927,461 describes the addition of hexagonal BN (boron nitride) to iron-based powder mixtures to improve machinability after sintering. By agglomerating very fine BN powder (0.05-1.0 μm), it is possible to achieve a simi¬ lar improvement of the machinability of iron-based powder mixtures after sintering as by the addition of MnS. How¬ ever, the sintered strength is affected to a lesser extent if a correct amount of BN powder is added, than when add¬ ing MnS. As in the case of MnS, BN additions do however not make it possible in industrial production to machine materials having a hardness above 200 HV. WO 91/14526 describes how small amounts of Te and/or Se together with MnS are used to improve the machinability about twice in powder-metallurgical materials that are difficult to machine. The addition of Te and/or Se is already conflicting with environmetal considerations, in that the hygienic limit values for these additives are very low and there is a tendency towards ever more strin¬ gent environmental regulations. One object of the present invention is to provide a powder to be added to an iron- or steel-based powder com¬ position which after sintering gives improved machinabi¬ lity in the resulting components. In particular, the invention provides an agent improving the machinability of materials which are difficult to machine, in this con¬ text materials having a hardness above about 180 HV and a strength above about 700 MPa, and being essentially free from hard phase material. Another object of the invention is to provide a machinability-improving agent which but to a small extent, or not at all, affects the mechanical properties, such as strength and dimensional change during sintering, of the sintered component, and which is essentially harmless to the environment. It has been found that these objects can be achieved by admixing to an iron-based powder composition an agent containing calcium fluoride particles. According to the invention, these particles are essentially free (i.e. not attached to graphi e particles, see below) and have an average particle size of less than 100 μm. Preferably, the average particle size ranges between 20 μm and 70 μm. If the particle size becomes too large, the strength of the sintered component will be adversely affected and the machinability-improving effect becomes unsatisfactory. Also when the powder additive is too fine, the machinabi¬ lity-improving effect becomes insufficient. The calcium fluoride particles may be of synthetic or natural origin. An especially preferred starting material is fine-grade fluorspar. The purity of the calcium fluoride also affects the machinability-improving effect, and it has been found that the content of impurities in the starting material used, such as fluorspar, should not exceed 3% by weight, preferably not 2% by weight. According to the invention, the machinability-improving calcium-fluoride-containing powder is added to an iron or a steel powder in an amount of about 0.1-0.6%, preferably 0.15-0.6% and most prefer¬ ably 0.2-0.5% by weight of the powder composition. For contents below 0.1% by weight of CaF ? , the machinability- improving effect becomes insufficient, whereas for con- tents above 0.6% by weight, CaF 2 will have an adverse effect on strength and dimensional change. One field of use of systems with fluorine compounds based on CaF_ involves solid lubricants for reducing the friction between surfaces which are loaded at room tem¬ perature and at elevated temperatures. This is reported in "Some Improvements in Solid Lubricants Coatings for High Temperature Operations", ASLE Transaction, Vol. 16/1, pp. 42-49. The use of calcium fluoride as a lubricant in powder-metallurgical materials with the primary aim of improving wear-resistance in sintered products, such as valve seats containing hard phase material, is also dis¬ closed e.g. in US-A-4,274,876, US-A-4, 836, 848, JP-A-53- 123314, SU 885-319, SU 1114-70, SU 1481-262, JP 63-42348 and EP 277 239. SU 1585-069 teaches that additions of CaF ? and S can be used for improving the machinability of powder-metal¬ lurgical materials, but the addition of CaF- is then very high (2-3%). Otherwise, S is well known for improving the machinability of both conventional and powder-metallurgi¬ cal materials. This publication cannot thus be considered to be of any major guidance to anyone skilled in the art who intends to improve the machinability of powder-metal¬ lurgical materials, since S would then first have to be eliminated before essentially reducing the added amount of CaF ? . Even if the additive according to the present invention can be combined with other conventional machin¬ ability-improving additives, such as MnS, it preferably is essentially free from elementary sulphur which, in addi- tion to being environmentally undesirable, has a marked effect on the dimensional change. JP 63-137137 discloses the addition of CaF 2 to iron- based powder mixtures with a view to improving the machin¬ ability of the components obtained after sintering, i.e. the object is the same as in the present invention. According to this Japanese patent application, however, the calcium fluoride is not in free form when added to the iron or steel composition, but it must be completely or partly attached to graphite. The purpose of using fluoride attached to graphite is to prevent the graphite from com¬ pletely dissolving in the iron matrix. The undissolved graphite then acts by forming a lubricating film between the tool and the material during machining. Furthermore, the Japanese application stipulates that relatively coarse carbon particles be added, which adversely affects the strength of the final component. Thus, the Japanese appli- cation does not in any way indicate that free calcium fluoride particles would give improved machinability. The advantages of the present invention over the invention according to the Japanese application is that, in the pre¬ sent invention, the step of fluoride absorbtion on carbon is dispensed with, since carbon need not be used at all in the invention, and if it is desirable to add carbon, finer carbon particles can be used, which entails comparatively improved strength. In addition to the additives as such, the present invention also encompasses iron- or steel-based powder compositions containing the additives, as well as the sin¬ tered products produced from these compositions. It is preferred that these powder compositions are essentially free from hard phase material, since preliminary tests have shown that the agent according to the present inven¬ tion does not exhibit any marked machinability-improving effect when hard phase material is included in the iron or steel compositions. As used herein, "hard phase material" relates to materials of non-metal having a hardness which essentially exceeds the hardness of alloyed metal, or exceeds 800 microvickers. Examples of hard phase materials are carbides, nitrides, oxides and borides. The powder compositions according to the invention may, in addition to iron and additive, comprise other sub- stances, such as C, P, Cr, Mn, Cu, Ni and/or Mo, which are traditionally included in this type of powder compo¬ sitions. Preferably, these substances are included in the powder compositions in the following contents: 0.1-2% by weight C, 0-0.6% by weight P, 0-25% by weight Cr, 0-10% by weight Mn, 0-5% by weight Cu, 0-8% by weight Ni, and 0-2% by weight Mo, the additive mentioned above being included in an amount of 0.1-0.6% by weight, preferably 0.15-0.6 and most preferably 0.2-0.5% by weight. According to a particular aspect of the invention, CaF„ is used in such known iron and steel compositions which, before the conception of the present invention, were admixed with sulphur for improved machinability. However, since sulphur causes swelling during sintering, whereas CaF- substantially does not affect the dimensions during this step, these known compositions can be admixed with another substance which, like sulphur, causes swell- ing during sintering. An example of such a swelling substance is MoS^, which may make up 0.05-0.5% by weight, preferably 0.1-0.3% by weight of the iron-based composition. The powder-metallurgical manufacture of components by means of the additive according to the invention is per¬ formed in conventional manner, i.e. most often by the fol¬ lowing process steps: The base powder, i.e. the iron or steel powder, is admixed with desired alloying elements, such as nickel, copper, molybdenum and optionally carbon as well as the additive according to the invention in pow¬ der form. This powder mixture is admixed with a conven¬ tional lubricant prior to compacting, for instance zinc stearate, which disappears during the subsequent sinter¬ ing. Mixing is done to distribute the alloying elements homogeneously in the material. The powder mixture is thereafter compacted in a press tool yielding what is known as a green body of close to final geometry. Compact¬ ing generally takes place at a pressure of 400-800 MPa. Higher compacting pressures only give an insignificant increase of the density but essentially increased tool wear. Lower compacting pressures entail densities which are too low to be useful in most structural details. After compacting, the compact is sintered and is given its final strength, hardness, elongation, etc. Sintering must take place at a temperature above 1083°C to make it possible to use Cu as alloying element. In view of the rate of diffu- sion in the material and the minimising of the sintering time, a maximum temperature is preferred. However, most of the production furnaces can only cope with temperatures up to 1150°C. Today, the commonest sintering temperature is 1120°C. At this temperature, desirable properties are generally achieved after sintering for 30 min. The present invention will be illustrated hereinafter in a few non-limitative Examples. All the materials used in these Examples are commer¬ cially available from Hόganas AB, Sweden, except for CaF„ which is a high-purity (99% CaF_) fine-grade fluorspar supplied by Indesko AB, Sweden. The materials in the fol¬ lowing Examples have all been compacted at 600 MPa to standardised tensile test bars according to ISO 2740-1973 and to discs having a diameter of 50 mm and a height of 12 mm. The materials were sintered in a laboratory mesh belt furnace at 1120°C for 30 min in endothermic atmos¬ phere with a carbon potential corresponding to 0.5%. The test bars were used to determine tensile strength accord¬ ing to EN 10002-1, hardness according to ISO 6507/1-1992 and dimensional change. The discs were used in drill tests to determine the machinability index. This index is defined as the average number of holes which six identical drills can make through six discs before the drills are worn out. Drilling was performed with high-speed steel drills at a constant speed and a constant feed without any coolant. Example 1 Six different materials with compositions described in Table 1 were mixed with additions of either MnS or CaF^ in order to evaluate the effects of the additives on the mechanical properties and machinability. The MnS used was a commercially available grade normally used for machin- ability-enhancing purposes. The CaF_ was sieved on a 63 μm sieve, and the fine fraction was used. The materials were processed according to the description above, except for the Fe + 0.6% P material, which was sintered in dissociat¬ ed ammonia. As can be seen in Table 1, there is a larger improvement in machinability for the materials containing CaF_ than for the materials containing MnS as compared with the reference. The tensile strength is significantly less affected by the CaF_ addition than the MnS addition, and there is smaller dimensional change for the CaF 2 as compared with the reference. Example 2 A material Fe + 4% Ni + 1.5% Cu + 0.5% Mo + 0.5% C was mixed with different amounts of <63 μm CaF_. The material was processed acccording to the description above, and machinability and tensile strength were mea¬ sured. The material without any addition of CaF« had a tensile strength of 736 MPa, a hardness of 205 HV 10, and a machinability index of 4. The results are presented in Fig. 1. As can be seen in Fig. 1, the machinability is significantly increased when CaF- is added in the amounts falling within the scope of the invention. As can also be seen in Fig. 1, the tensile strength decreases with increasing amounts of CaF_ down to a level which is unacceptable. Example 3 A material Fe + 4% Ni + 1.5% Cu + 0.5% Mo + 0.5% C was mixed with 0.3% CaF» which was sieved to different particle or grain sizes. The maximum grain sizes were ranging from 20 μm to 150 μm. The materials were processed according to the description above, and machinability and tensile strength were measured and are presented in Fig. 2. The material without any addition of CaF_ had a tensile strength of 736 MPa, a hardness of 205 HV 10, and a machinability index of 4. The machinability is highest when the maximum CaF- grain size is between 30 μm and 100 μm. The influence of tensile strength is decreasing with increasing maximum grain size, but it is not until the maximum grain size exceeds 140 μm that the drop in tensile strength becomes unacceptable. The average grain size ranges between half and 2/3 of the maximum grain size.

Claims: CLAIMS 1. An agent for improving the machinability of sin- tered products produced from an iron or steel powder which is essentially free from hard phase material, c h a r ¬ a c t e r i s e d in that it essentially consists of CaF 2 particles which are not attached to graphite particles, optionally in combination with one or more conventional, additional machinability-improving agents which are essentially free from elementary sulphur. 2. An agent as claimed in claim 1, c h a r a c ¬ t e r i s e d in that the powder contains free CaF_ par¬ ticles having an average particle size below 100 μm, pre- ferably between about 20 μm and about 70 μm. 3. An agent as claimed in any one of claims 1-2, c h a r a c t e r i s e d in that the additional machinability-improving agent is MnS in an amount of at most 30% by weight, preferably at most 15% by weight, of the total weight of CaF 2 . 4. An iron-based powder composition essentially free from hard phase material for compacting and sintering into products having enhanced machinability, said composition containing, in addition to iron, at least one of the alloying elements C, P, Cr, Mn, Cu, Ni and Mo, c h a r ¬ a c t e r i s e d in that the iron powder contains 0.1-0.6%, preferably 0.15-0.6% and most preferably 0.2-0.5% by weight of CaF„ powder as claimed in claims 1-3. 5. A powder composition as claimed in claim 4, where¬ in the alloying elements are included in the following contents, based on the weight of the composition: 0.1-1.2% by weight C, 0-0.6% by weight P, 0-25% by weight Cr, 0-10% by weight Mn, 0-5% by weight Cu, 0-8% by weight Ni, and 0-2% by weight Mo. 6. A powder composition as claimed in claim 5, c h a r a c t e r i s e d in that it contains 0.05-0.5%, preferably 0.1-0.3% by weight of MoS 2 . 7. A sintered product having enhanced machinability and being essentially free from hard phase material, said product containing 0.1-1.2% by weight C, 0-0.6% by weight P, 0-25% by weight Cr, 0-10% by weight Mn, 0-5% by weight Cu, 0-8% by weight Ni, and 0-2% by weight Mo, as well as 0.1-0.6% by weight CaF 2 as claimed in claims 1-3. 8. The use of CaF 2 particles which are not attached to graphite particles for improving the machinability of sintered products prepared form an iron or steel powder which is essentially free from hard phase material. 9. A method of improving the machinability of sin- tered products, comprising adding CaF 2 particles, which are not attached to graphite particles, to an iron or steel powder which is essentially free from hard phase material, compacting the iron or steel powder to a green body, and sintering the green body.

Inventors: ANDERSSON OWE, ANDERSSON, OWE
Applicants: ANDERSSON OWE, ANDERSSON, OWE
Application year: 1993
Main classification: B22F1
IPC codes: B22F1, C01F11, C22C33