Carbon composite electrode material

Abstract: A method for manufacturing a carbon composite electrode material which comprises coating the surface of core carbon particles with high crystallinity with a film containing a element of Group VIII metal and depositing and/or covering the surface of resulting coated carbon particles with a carbon material to be formed upon pyrolysis of a hydrocarbon or its derivative.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention The present invention relates to a carbon composite material, a method for manufacturing a carbon composite electrode material, and its use as a negative electrode active material in lithium secondary batteries. 2. Description of the Related Art It was reported that when a certain type of carbon material, of carbon composite electrode materials, is used as a negative electrode active material in lithium secondary batteries, the charge-discharge cycle characteristic and safety of the secondary batteries is excellent (for example, Japanese Patent Unexamined Publication Nos. Sho 63-24555 and Hei 1-311565). This carbon material is manufactured, for example, by chemical vapor deposition (CVD) of a hydrocarbon. The present inventors found out and disclosed the fact that outstandingly excellent as the negative electrode active material in lithium secondary batteries was particularly a carbon material of a structure such that its internal layer had high crystallinity and that its surface layer was coated with a carbon having a turbulent layer structure (Japanese Patent Application No. Hei 3-144547). As manufacturing methods of carbon composite electrode materials, there is available a method of forming and depositing a carbon material through chemical vapor deposition of any hydrocarbon or its derivatives on the surface of such a carbon material as graphite used as its core material. In this instance, the deposited carbon material shows a turbulent layer structure. The system needs to be held at about 1000 °C for a long period of time so as to deposit the carbon material having such a turbulent layer structure. Under such conditions, this method is not practically useful, because a large amount of a tarry product is generated by side reactions. SUMMARY OF THE INVENTION The present invention is defined by the claims. In one aspect the present invention provides a method for manufacturing a carbon composite electrode material which comprises coating the surface of core carbon particles having high crystallinity with a film containing an element of Group VIII metal and depositing on the surface of the resulting coated carbon particles a carbon material formed by pyrolysis of a hydrocarbon or its derivatives. Desirable carbon material should be formed by pyrolysis in vapor phase or aerosol state of any hydrocarbon or its derivatives. The crystal structure of the carbon particles may consist of a mean interlayer spacing of approximately 0.335 - 0.340 nm in the C-axis direction and a ratio of peak intensity of lower than about 0.4 at 1360 cm⁻¹ to that at 1580 cm⁻¹ in the argon laser Raman spectra method. Further, the element of Group VIII metal should desirably be nickel, cobalt or iron or their alloys and the thickness of the film containing the element 0.1 - 2.0 µm. In another aspect, the present invention provides use of the carbon composite electrode material manufactured by the above method, as a negative electrode active material in a lithium secondary battery. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic diagram of a carbon material pyrolysis and depositing apparatus used in an embodiment of this invention; FIG. 2 is a diagrammatic representation of discharging curves for the test electrode A in an embodiment and a comparative electrode; and FIG. 3 is a diagrammatic representation of discharging curves for other test electrodes B, C, D, E, F, G and H in embodiments of this invention. DETAILED DESCRIPTION OF THE EMBODIMENTS The present invention provides a method for manufacturing carbon composite electrode material in which the surface of core carbon particles having high crystallinity is coated by carbon material, at a relatively low temperature, in a short time, and such as to increase the specific surface area of the carbon composite. The core carbon particles having high crystallinity are suitably natural graphite, kish graphite, or carbons obtained by heat-treating at such a high temperature as above 2000 °C such a well-known carbon material as petroleum coke or coal pitch coke or the like graphitizing carbons. Their mean particle size should desirably be not larger than 100 µm, particularly about 1 - 20 µm. If the particle size falls in this range, the utilization rate as an active material is high and the filling density of the negative electrode active material may be made high. The mean particle size is given by measuring and averaging the particle sizes distributed per unit volume. The particle form may include any of spherical, flaky crystal or fibrous or their pulverulences, but the spherical or flaky crystal form is preferable. Further, the desirable crystal structure should have a mean interlayer spacing of 0.335 - 0.340 nm, as determined by the X-ray wide angle diffraction method, and lower than about 0.4 as a ratio of the peak intensity at 1360 cm⁻¹ to that at 1580 cm⁻¹ in the argon laser Raman scattering method. The core carbon particles having high crystallinity of the present invention are coated with a film containing a Group VIII metal. The elements of Group VIII metal of the present invention include iron, nickel, cobalt, ruthenium, rhodium, palladium, osmium, iridium and platinum and their alloys. Among them, iron, nickel and cobalt are preferable. The coating methods include electroless plating process or a vapor deposition process of evaporating by heating the aforementioned Group VIII metal held under a highly reduced pressure, and sputtering process to form a metal film by the ion impact, and so on. The electroplating process or the electroless plating process is preferable in views of economy and productivity. In the electroless nickel plating process, a plating bath is prepared with approx. 20 of NiSO₄·7H₂O and approx. 25 of NaH₂PO₂ in ratio by weight with its pH adjusted to approx. 5.0 and the core carbon particles are dipped into this plating bath. Then by adding such a reducing agent as phosphate or sodium hydrogen boride to this plating bath, while holding it at about 90°C, a metal film is formed on the surface of the carbon particles with high crystallinity. For these plating baths and the reducing agents, those prepared and available commercially may be utilized (for example, TMP Kagaku nickel: mfd. by Okuno Seiyaku Kogyo K.K.). The average thickness of the coated film containing a Group VIII metal should preferably be 0.01 - 2.0 µm. If it is thinner than 0.01 µm, its effect as a catalyst is slight, but if thicker than 2.0 µm, the rates of intercalation and deintercalation into and from the internal carbon material are slow. As the film containing a Group VIII metal, a carbon material is formed, deposited and/or covered through pyrolysis of a hydrocarbon or its derivatives in vapor phase or in the state of aerosol. The hydrocarbons and their derivatives include aliphatic or aromatic or alicyclic hydrocarbons and their partial substituents (halogen atoms, hydroxyl, sulfo, nitro, amino and carboxyl groups, etc.). Their actual examples include: methane, ethane, propane, butane, pentane, hexane, cyclohexane, naphthalene, anthracene, pyrene, benzene, toluene, pyridine, allyl benzene, hexamethyl benzene, aniline, phenol, 1,2-dichloroethylene, 1,2-dibromoethylene, 2-butene, acetylene, biphenyl, diphenyl acetylene, styrene, acrylonitrile, pyrrole and thiophene and their derivatives. Of these compounds, methane, ethane and propane are preferable, because they are not expensive, their waste gases are readily treatable and they are not liable to corrode the pyrolysis furnace. Any of the aforementioned hydrocarbons or its derivatives in gas phase or in aerosol state is (are) fed to a carbon pyrolysis and depositing apparatus, to be carried onto a film containing a Group VIII metal which is placed on a holder for depositing carbon material. As the reaction conditions at that time, the feed rate of the gas phase material or the aerosol is 0.03 - 20 mols/hr and its flow rate 5 - 100 cm/min. This pyrolysis is performed at a temperature of approx. 300 - 1300°C, preferably approx. 500 - 1100°C in a noncombustible atmosphere, for example, under reduced pressure or in an inert gas. In this way, a carbon composite electrode material with a particle size of approx. 15 - 50 µm is obtained. In this carbon,composite electrode material, core carbon particles having high crystallinity are coated with a film containing a Group VIII metal and on their film surface, there is further formed a carbon material through pyrolysis and deposition of a hydrocarbon or its derivatives in gas phase or in aerosol state. Accordingly, it has the undermentioned characteristic features. First, since the Group VIII metal acts as a catalyst for the pyrolysis reaction of the hydrocarbon or its derivatives in gas phase or in aerosol state, the carbon material can be relatively formed and deposited at a low temperature and in a short time. Secondly, a part or all of the film of the Group VIII metal diffuses into the carbon material formed, deposited and/or covered thereon during the aforementioned pyrolysis, and the core carbon particles having high crystallinity are directly covered with the carbon material formed and deposited through pyrolysis. Thirdly, the carbon material of the surface layer of the carbon composite electrode material is a carbon material formed and deposited through pyrolysis of a hydrocarbon. Therefore, it is a carbon material of the so-called turbulent layer structure which permits easy intercalation and deintercalation of lithium ion, etc. The carbon material with turbulent layer structure refers to a material having a crystal structure which gives a mean lattice width of 0.377 nm or larger in its C-axis direction and which gives a ratio of 0.4 or higher of the peak intensity at 1360 cm⁻¹ to that at 1580 cm⁻¹ of the argon laser Raman spectra. EXAMPLES Example 1 As core carbon particles having high crystallinity, 5.014 g of a powder (mean particle size 18.0 µm, average lattice width of 0.3358 nm in the C-axis direction and the peak at 1360 cm⁻¹ in its argon laser Raman spectra not observed) of graphite (KS-75, mfd. by Lonza Co.) were taken and coated with nickel by the electroless nickel plating process. In forming the nickel film, the powder was subjected to a sensitization treatment as a pretreatment, using MAC-100 (mfd. by Okuno Seiyaku Kogyo K.K.), thoroughly water-rinsed, then subjected to an activation treatment with MAC-200 (mfd. by Okuno Seiyaku Kogyo K.K.), followed by thorough water-rinsing, and thereafter underwent the plating process. The film was formed using TMP Kagaku nickel (mfd. by Okuno Seiyaku Kogyo K.K.) as the plating bath at approx. 35°C, while stirring the bath with a stirrer. Since the weight of graphite, after being coated with the film, was 10.128 g, the mean nickel film thickness was calculated to be 0.79 µm from the increment of its weight and its mean particle size. The graphite coated with nickel film obtained in this way was mounted on a holder of a carbon pyrolysis and depositing apparatus. Then using the carbon pyrolysis and depositing apparatus shown in FIG. 1, the formation, deposition and/or covering of the carbon material through pyrolysis of any hydrocarbon was carried out by the undermentioned procedure. Through an argon feeding line I and a propane feeding line 2, argon and propane gases were respectively fed into this apparatus. By operating needle valves 3 and 4, the concentration of propane was adjusted to 10 mol%. The current velocity of both gases was preset to 12.7 cm/min and propane was fed at a rate of 0.05 mol/hr. On the other hand, on the sample holder 6 inside the reactor tube 5, the graphite coated with the nickel film was mounted and a furnace 7 was installed on the outer circumference of the reactor tube 5. By this furnace 7, the sample holder 6 and the graphite coated with the nickel film were held at a temperature of 750°C, for pyrolysis with the propane fed through a pipe 3 made of Pyrex glass, thereby forming and depositing the carbon material on the surface of the nickel film coating the graphite, yielding particles of a carbon composite electrode material. The reaction time at this time was set at approx. 30 min. The mean particle size of the carbon composite electrode material obtained at this time was approx. 25.1 µm, as determined by laser diffraction particle analyzer. However, there is a possibility that the observed particles consisted of the mixture of those cohered with each other and those not so cohered, since the particles were deposited and cohered with each other through the reaction. It should be noted that the gas remaining in the reactor tube after the pyrolysis reaction was removed by exhausting through an exhaust facility 9. With regard to the crystalline structure of the carbon composite electrode material obtained in this way, results of measurements of its X-ray diffraction and argon laser Raman spectra gave the following data: d=0.3373 nm and R=0.48. In this case, X-ray by CuKα line was employed for the X-ray diffraction and d represents a mean interlayer spacing. R denotes the ratio of the peak intensity at 1360 cm⁻¹ to that at 1580 cm⁻¹ of the argon laser Raman spectra. About 30 mg of this carbon composite electrode material was mixed with 5% by weight of a polyolefin as a binder. It was then hot-pressed on a nickel mesh at about 120°C and under about 400 kg/cm², yielding a pellet with an approx. 15 mm dia. This pellet was named test electrode A. Comparative Example 1 Using the powder of the graphite (KS-75, mfd. by Lonza Co.) of Example 1 as the core carbon particles having high crystallinity, the carbon composite electrode material was prepared under the similar conditions, except that they were not coated with the nickel film. When the measurements were taken of the characteristics of the crystal structure obtained in this way under the similar conditions as in Example 1, the results gave the following data: d=0.3360 and R=0.15. The aforementioned interlayer spacing was found to be nearly equal to that of graphite, attesting to the fact that under such conditions as in Example 1, noncrystalline carbon material is hardly formed on the graphite surface. Measurement results of the specific surface area by the BET method suggested that the carbon composite electrode material of Example 1 has 12 times as large a specific surface area as that of the carbon composite electrode material of Comparative Example 1. Further, from about 30 mg of this carbon composite electrode material, a pellet with an approx. 15 mm dia. was obtained by the similar method as in Example 1. This pellet was named comparative electrode, referenced "COMP" in FIG. 2. Example 2 A powder of the graphite (KS-75, mfd. by Lonza Co.) of Example 1 used as the core carbon particles having high crystallinity was coated with cobalt by electroless cobalt plating process. The powder was dipped in a cobalt plating bath, after subjecting it to the pretreatment and the activation treatment under the similar conditions as in Example 1. The plating bath was prepared by mixing 0.13 mol/l of CoCl₃·6H₂O and 0.05 mol/l of sodium hypophosphite and with this bath, the cobalt was plated on the powder at a temperature of 80°C. The plated cobalt film thickness, as measured by the similar method as in Example 1, was approx. 0.51 µm. The carbon material was formed, deposited and/or covered, to prepare the carbon composite electrode material, similarly as in Example 1, except using the graphite coated with the cobalt film obtained in this way. The mean particle size of the carbon composite electrode material at this time was found to be about 28.3 µm, as determined by laser diffraction particle analyzer. The results of the measurements on the characteristics of this crystal structure, as taken under the similar conditions as in Example 1, gave the following data : d=0.3375 and R=0.51. Further a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode B. Example 3 A powder of the graphite (KS-75, mfd. by Lonza Co.) of Example 1 used as the core carbon particles having high crystallinity was coated with nickel-iron alloy by electroless nickel-iron plating process. The powder was dipped in a nickel-iron alloy plating bath, after subjecting it to the pretreatment and the activation treatment under the similar conditions as in Example 1. The plating bath was prepared by mixing 0.05 mol/l of NiSO₄·6H₂O, 0.05 mol/l of ammonium iron (II) sulfate, 0.16 mol/l of sodium citrate and 0.5 mol/l of ammonium sulfate and with this bath, the powder was plated with nickel-iron at about 90°C. The plated film thickness, as measured by the similar method as in Example 1, was found to be approx. 0.80 µm. The mean particle size of the carbon composite electrode material at this time was found to be about 28.3 µm, as determined by observation by laser diffraction particle analyzer. The carbon material was formed and deposited, to prepare the carbon composite electrode material, similarly as in Example 1, except using the graphite coated with the nickel-iron alloy film obtained in this way. The results of the measurements on the characteristics of this crystal structure, as taken under the similar conditions as in Example 1, gave the following data: d=0.3386 and R=0.49. Further a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode C. Example 4 A powder of the graphite (KS-75, mfd. by Lonza Co.) of Example 1 used as the core carbon particles having high crystallinity was coated with nickel by the nonelectrolytic nickel plating process similarly as in Example 1. The formation and deposition of the carbon material was made through pyrolysis of a hydrocarbon by the similar procedure as in Example 1, using the carbon pyrolysis and depositing apparatus shown in FIG. 1. At this time, in place of propane, benzene was used as the raw material hydrocarbon. The conditions of the pyrolysis were: the current velocity of the gases 25.5 cm/min, its feed rate 0.15 mol/hr, the reaction temperature approx. 650°C and the reaction time approx. 30 min. The mean particle size of the carbon composite electrode material at this time was found to be about 29.3 µm, as determined by laser diffraction particle analyzer. The results of the measurements on the characteristics of the crystal structure of this carbon composite electrode material, as taken under the similar conditions as in Example 1, gave the following data: d=0.3385 and R=0.43. Further, a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode D. Example 5 A powder of the graphite (KS-75, mfd. by Lonza Co.) of Example 1 used as the core carbon particles having high crystallinity was coated with nickel by the electroless nickel plating process similarly as in Example 1. The formation and deposition of the carbon material was made through pyrolysis of a hydrocarbon by the similar procedure as in Example 1, using the carbon pyrolysis and depositing apparatus shown in FIG. 1. At this time, in place of propane, 2-dichloroethylene was used as the raw material hydrocarbon. The conditions of the pyrolysis were: the flow rate of the gases 18.5 cm/min, its feed rate 0.12 mol/hr, the reaction temperature approx. 650°C and the reaction time approx. 30 min. The mean particle size of the carbon composite electrode material at this time was found to be about 34.5 µm, as determined by laser diffraction particle analyzer. The results of the measurements on the characteristics of the crystal structure of this carbon composite electrode material, as taken under the similar conditions as in Example 1, gave the following data: d=0.3412 and R=0.55. Further, a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode E. Example 6 About 5 g of a powder of natural graphite (produced in Madagascar, its mean particle size 6.2 µm, d=0.3363 nm, no peak at 1360 cm⁻¹ in the argon laser Raman spectra observed) used as the core carbon particles having high crystallinity was coated with nickel by the electroless nickel plating process. The pretreatment and the activation treatment for forming the nickel film were similarly performed as in Example 1 and then the powder was submitted to the plating process. A nickel film was formed in the plating bath of a mixture of 30 g/l of NiSO₄·6H₂O, 10 g/l of sodium acetate and 10 g/l of sodium hypophosphite at about 90°C. From the weight of the graphite thus coated, the mean film thickness of the nickel film was calculated to be 0.70 µm. Similarly as in Example 1, a carbon composite electrode material was prepared by forming and depositing a carbon material on the plated particles. The mean particle size of the carbon composite electrode material at this time was approx. 14.1 µm, as determined by laser diffraction particle analyzer. The results of the measurements on the characteristics of the crystal structure, as taken under the similar conditions as in Example 1, gave the following data: d=0.3378 and R=0.51. Further, a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode F. Example 7 About 5 g of mesophase spherules carbonized and further heat-treated at 2800°C (their mean particle size 5.8 µm, d=0.3368 nm and R=0.35) used as the core carbon particles having high crystallinity were coated with nickel by the electroless nickel plating process. Their pretreatment and activation treatment for forming the nickel film were similarly performed as in Example 1 and then the spherules were submitted to the plating process. A nickel film was formed in the plating bath of a mixture of 30 g/l of NiSO₄·6H₂O, 50 g/l of ammonium chloride with 10 g/l of sodium hypophosphite at about 90°C. From the weight of the graphite thus coated, the mean film thickness of the nickel film was calculated to be 0.84 µm. Similarly as in Example 1, a carbon composite electrode material was prepared by forming, depositing and/or covering a carbon material on the plated spherules. The mean particle size of the carbon composite electrode material at this time was approx. 12.6 µm, as determined by laser diffraction particle analyzer. The results of the measurements on the characteristics of the crystal structure, as taken under the similar conditions as in Example 1, gave the following data: d=0.3397 and R=0.62. Further, a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode G. Example 8 A carbon composite electrode material was prepared similarly as in Example 7, except that mesophase spherules which had been carbonized and further heat-treated at 2000 °C (their mean particle size 16.4 µm, d=0.3385 nm, R=0.39) were used as the core carbon particles having high crystallinity. The mean thickness of the nickel film at this time was found to be 1.72 µm and the mean particle size of the carbon composite electrode material was 25.3 µm. The results of the measurements on the characteristics of the crystal structure, as taken under the similar conditions as in Example 1, gave the following data: d=0.3410 and R=0.53. Further, a pellet with an approx. 15 mm dia. was obtained from about 30 mg of this carbon composite electrode material by the similar method as in Example 1. This pellet was named test electrode H. With the test electrodes A through H and the comparative electrode COMP above-mentioned, charge-discharge tests were carried out in the range of 0 - 2.5 V. As the working electrode, the test electrodes and the comparative electrode were used and as the counter electrode and the reference electrode, lithium metal was used. As the electrolyte, propylene carbonate having 1 mol/l of LiClO₄ dissolved therein was used. The charge-discharge test was carried out in a globe box in an argon atmosphere. The discharge curves obtained at that time were depicted in FIGs. 2 and 3. These graphs indicate that, as compared with the comparative electrode COMP, all of the test electrodes A through H gave higher discharge capacity. According to this invention, a carbon material having an inside layer of high crystallinity and an outside layer of turbulent crystal structure can be relatively manufactured at a low temperature and in a short time. In cells using the carbon composite electrode material obtained by this manufacturing method as their negative electrode active substance, the charge-discharge capacity and rate is remarkably improved because of larger surface area of the electrode.

Claims: A method for manufacturing a carbon composite electrode material which comprises coating the surface of core carbon particles having high crystallinity with a film containing an element of Group VIII metal and depositing on the surface of the resulting coated carbon particles a carbon material formed by pyrolysis of a hydrocarbon or its derivatives. The method according to claim 1, wherein the characteristics of the crystal structure of the carbon particles are a mean interlayer spacing of about 0.335 - 0.340 nm in the C-axis direction and a ratio of the peak intensity of lower than about 0.4 at 1360 cm⁻¹ to that at 1580 cm⁻¹ in the argon laser Raman scattering method. The method according to claim 1, wherein the carbon material is formed by pyrolysis of a hydrocarbon or its derivatives in vapor phase or aerosol state. The method according to claim 1, wherein the element of Group VIII metal is nickel, cobalt or iron, or their alloys. The method according to claim 1, wherein the thickness of the film containing said element is in the range from 0.1 to 2.0 µm. A carbon composite electrode material obtainable by the method of any of claims 1 to 5 . A carbon composite material comprising core carbon particles having high crystallinity, said particles coated on the surface by a film containing an element of Group VIII metal, the coated carbon particles further having deposited on the surface thereof a carbon material providing an outside layer of turbulent crystal structure. Use of carbon composite material, as defined by claim 6 or claim 7, or manufactured by the method of any of claims 1 to 5, as a negative electrode active material in a lithium secondary battery.

Inventors: MITATE TAKEHITO, TANAKA HIDEAKI, YAMADA KAZUO, YOSHIKAWA MASAHARU, MITATE, TAKEHITO, TANAKA, HIDEAKI, YAMADA, KAZUO, YOSHIKAWA, MASAHARU
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1993
Main classification: H01M4
IPC codes: D01F9, D01F11, C01B31, H01M4, G01N21