A method of forming a stabilized vulcanizate of chloro rubbers and said vulcanizate

Abstract: Calcium aluminum hexahydrate is a useful curative-stabilizer for halogenated rubbers such as chloronated polyethylene, chlorosulfonated polyethylene and polychloroprene as it can yield vulcanizates free of leachable lead. Also, these vulcanizates with about 1 to about 30 or more parts with about 3 to about 15 parts calcium aluminum hexahydrate being highly desirable give satisfactory to improved heat ageing properties as well as oil ageing properties.

Description: Field This invention relates to an improved method to vulcanize or cure halogenated rubbers and to the resulting vulcanizates. By this method, the halogenated rubbers are vulcanized with an activator or activators to give a vulcanizate free of poisonous lead and having physical properties essentially equal to lead vulcanizates. More specifically, this invention relates to a vulcanizate of a halogenated rubber containing from 1 to about 30 and higher parts of calcium aluminum hexahydrate. Background of the Invention Halogenated rubbers such as chlorosulfonated polyethylene and chlorinated polyethylene require activators to aid in curing the rubber and to stabilize the cured rubber. In the case of chlorosulfonated polyethylene and chlorinated polyethylene rubbers, metal oxides, and hydroxides of lead, cadmium, magnesium, calcium and barium have been used as activators and stabilizers. Toxicity concerns have decreased the use of barium, cadmium and lead which leaves calcium and magnesium as the most common stabilizer. These are known to be moisture sensitive and cause water absorption and are very unsatisfactory for producing vulcanizates for tank linings. In the case of polychloroprene rubber, oxides of zinc and magnesium and lead are commonly used to activate the cure and stabilize the vulcanizate. Zinc is known to produce moisture sensitivity, resulting in water absorption. In cases where water immersion is needed, lead oxides are preferred in place of zinc oxide and magnesium oxide. Landfill requirements require a limited lead content in acidic leachate tests and lead stabilized polymers are recognized as a disposal problem. Consequently, a need exists for an improved curative-stabilizer for the halogenated rubber vulcanizates other than lead salts. Fig. 1 is a cross-sectional view through the tank 2 of a tank truck showing the Neoprene lining 3 cured with calcium aluminum hexahydrate. The halogen-containing rubbers used in this invention are known and can be properly selected. Examples include halogen-containing olefin rubbers such as chlorinated polyethylene rubber, chlorinated polypropylene rubber, chlorosulfonated polyethylene rubber, chlorinated ethylene/propylene rubber, chlorinated ethylene/propylene/diene rubber, chlorinated ethylene/1-butene rubber, chlorinated ethylene/4-methylpentene rubber, chlorinated butyl rubber, and epihalohydrin rubbers such as polyepichlorohydrin rubber, epichlorohydrin/ethylene oxide copolymer rubber and epichlorohydrin/allyl glycidyl ether copolymer rubber, fluorine rubbers; chlorine-containing and polychloroprene rubbers. We have discovered that the use of calcium aluminum hexahydrate in the curing recipes for halo rubbers yields vulcanizates with improved stabilizing effects in heat ageing, oil ageing and hydraulic fluid ageing relative to the vulcanizates of halo rubbers cured with a recipe containing the industry's best curative, lead oxide. This, indeed, is an important discovery in view of the fact lead oxide vulcanizates present a disposal problem due to the problem of ground water contaminated by extracted lead. Further, these improved properties of the invention vulcanizates make these invention vulcanizates desirable for use in making Freon hose, hydraulic hose as well as gaskets, seals and other industrial products like underground cable coating and tank linings. Synthetic crystalline calcium aluminum hexahydrate produces a high state of cure in polychloroprene rubbers while eliminating the stabilizer lead oxide or magnesium oxide/zinc oxide combination. Hence, if the harmful effects of environmental contamination by lead forces lead's replacement, the instant invention would be preferred for a replacement for lead with advantages in heat ageing, oil ageing and hydraulic fluid ageing. The useful calcium aluminum hexahydrate is also called tri-calcium aluminate hexahydrate with the formula Ca 3 Al 2 (OH) 12 and is available from the Huber Corporation. The calcium oxide and calcium and magnesium salts of the organic acids, for instance, phthalic acids, and specifically terephthalic acid are useable to advantage in curing and producing these vulcanizates with calcium aluminum hexahydrate. The BET specific surface area of the compound of the above formula may be properly chosen, and is preferably 20 to 100 m 2 /g. The particle diameter of the compound of the formula is preferably small to obtain good dispersibility in a rubber material. For example, it has a secondary particle diameter of 0.1 to 10 microns. The curative product of the stabilized formula used in this invention can have specific surface area, for example, 20 to 300 m 2 /g, preferably 20 to 200 m 2 /g, and a particle diameter of 0.1 to 10 microns. The curable rubber composition may contain various compounding agents known in the art such as fillers, reinforcing agents, plasticizers, processing aids, cross-linking agents, antioxidants, pigments and fire retardants. These compounding agents may be used in amounts generally known in the art. For examples, the amounts may be 5 to 200 phr for the fillers, 5 to 150 phr for the reinforcing agents, 1 to 20 phr for the plasticizers, about 1 to 10 phr for the processing aids, 0.1 to 10 phr for the cross-linking agents, 0.1 to 10 phr for the antioxidants, 0.1 to 10 phr for the pigments and 1 to 200 phr for the fire retardants, each based on the weight of the one hundred parts of halogen-containing rubber. Examples of the fillers include carbon black, silicic anhydride, hydrous silicic acid, calcium silicate, aluminum silicate, clay, talc, calcium carbonate, basic magnesium carbonate, alumina hydrate, diatomaceous earth, barium sulfate, mica, alumina sulfate, lithopone, asbestos and graphite. Examples of the reinforcing agents include high-styrene resins, coumarone-indene resin, phenolic resins, modified melamine resins, petroleum resins, lignin, cotton, rayon, nylon, Vinylon, polyesters, glass fibers, carbon fibers and steel cords. Examples of the plasticizers include pine tar, tall oil, rapeseed oil, cottonseed oil, peanut oil, castor oil, palm oil, mineral oil-type softeners, phthalic acid derivatives (e.g., DBP, DHP, DOP, and DIDP), sebacic acid derivatives such as DES and DOS and adipic acid derivatives (such as DOA and DIOA). Examples of the processing aids include Struktol WB212 (a mixture of high-molecular-weight fatty acid esters) and RP-10 (dixylyl disulfide mixture); and rubber hardening agents such as benzidine, p-aminophenol and p-phenylenediamine. Examples of the pigments include titanium white, lithopone, zinc sulfide, cadmium red, cadmium yellow, barium yellow, strontium yellow, chrome yellow, ultramarine, Prussian blue, cobalt blue, chromium oxide, cobalt green, carbon black, Hansa Yellow G, Lake Red C, benzidine orange, phthalocyanine blue, and phthalocyanine green. Examples of the fire retardants include aluminum hydroxide, magnesium hydroxide, antimony trioxide, tetrabromobisphenol A, chlorinated paraffin, tricresyl phosphate, triethyl phosphate, perchloropentacyclodecane and chlorinated polyphenyl. To further illustrate and exemplify the invention, a number of chloronated rubbers were compounded and tested. In a clean cold banbury, the compounding ingredients listed in Tables 1 and 3 below were mixed in the amounts by weight until the mixture in the banbury reach 82°C (180°F) and then mixed an additional minute after the accelerator and the acid scavenger was added and the mixture was dropped from the banbury when the temperature reached 127°C (260°F). The nature of these mixes is shown in Tables 1 and 3 and the properties of their vulcanizates is shown in Tables 2 and 4. The chlorosulfonated polyethylene compositions were cured at 154°C (310°F) for a time equal to the Rheometer T90 plus 10%. The polychloroprene compositions were cured at 149°C (300°F) for a time equal to the Rheometer T90 plus 10%. Table 1 of Recipes Ingredients A B C D Chlorosulfonated polyethylene 100 100 100 100 Carbon black 75 75 75 75 PEG 3 3 3 3 PE wax 3 3 3 3 TOTM 15 15 15 15 Litharge 10 Lime (Ca0) 10 Mg (OH) 2 10 Calcium aluminum hexahydrate 10 Curative 3.5 3.5 3.5 3.5 Totals 209.50 209.50 209.50 209.50 Sp. Gr. 1.382 1.358 1.362 1.363 Recipes of Table 3 Recipe Compounds Ingredients E F G H Polychloroprene 100 100 100 100 Polybutadiene Rubber 5.0 5.0 5.0 5.0 Carbon Black 44.0 44.0 44.0 44.0 Dibutylphthalate 15.0 15.0 15.0 15.0 Octamine 2.0 2.0 2.0 2.0 Stearic Acid .5 .5 .5 .5 MBTS 1.0 1.0 1.0 1.0 Red Lead 15.0 Calcium Aluminum Hexahydrate 15.0 7.5 7.5 Ca(OH) 2 7.5 Magnesium Terephthalate 7.5 Totals 182.10 182.10 182.10 182.10 Sp. Gr. 1.397 1.355 1.352 1.331

Claims: Method for curing a curable rubber composition composed of a halogen containing rubber and a member selected from the group consisting of a vulcanizing agent and a vulcanization accelerator under heat in the presence of an acid acceptor, characterized in that said acid acceptor composition is calcium aluminum hexahydrate of the formula Ca 3 Al 2 (OH) 12 The method of claim 1 wherein the vulcanized halogenated rubber is selected from the class consisting of polychloroprene, chlorosulfonated polyethylene rubber and chlorinated polyethylene rubber. The method of claim 1 wherein the amount of the acid acceptor is present in 1 to 30 parts per hundred of rubber. The method of claim 1 wherein the vulcanizate contains in addition to the acid acceptor, calcium aluminum hexahydrate 1 to 25 parts per hundred of rubber (phr) of a stabilizer selected from the class consisting of MgO, CaO, Ca(OH) 2 , Mg(OH) 2 and calcium or magnesium salt of an organic acid. The method of claim 1 wherein the halogen-contain rubber is cured at 79°C (175°F) to 177°C (350°F). A vulcanized halogenated rubber selected from the group consisting of polychloroprene, chlorosulfonated polyethylene rubber and chlorinated polyethylene characterized by its containing a curative-stabilizer, calcium aluminum hexahydrate. The vulcanized halogenated rubber of claim 6 wherein the curative-stabilizer is present in 1 to 30 parts per hundred of rubber. The vulcanizate of claim 6 wherein the vulcanizate contains in addition to the curative stabilizer, calcium aluminum hexahydrate, 1 to 25 parts per hundred of rubber (phr) of at least one stabilizer selected from the group consisting of Mg0, CaO, Ca(OH) 2 , Mg(OH) 2 and a calcium or magnesium salt of an organic acid.

Inventors: FORSTE CAROL LYNN, PILKINGTON MERVIN VICTOR, FORSTE, CAROL LYNN, PILKINGTON, MERVIN VICTOR
Applicants: GOODYEAR TIRE & RUBBER, THE GOODYEAR TIRE & RUBBER COMPANY
Application year: 1993
Main classification: C08K3
IPC codes: C08K3, C08L23, C08L11