Cyclopentadienyl group chromium alpha-olefin polymerization catalysts and process for polymerizing alpha-olefins

Abstract: Disclosed is a selected catalyst system for the homopolymerization and copolymerization of alpha-olefins having 2-8 carbon atoms, said catalyst system comprising a cyclopentadienyl Group 6b metal hydrocarbyl compound in which the metal has an oxidation state of +3, said Group 6b metal compound being supported on an inorganic support. The catalyst system may also contain a Group 2 or Group 3 metal alkyl compound.

Description: The present invention relates to selected catalyst systems for polymerizing alpha-olefins and processes for polymerizing alpha-olefins using such catalysts. Chromium based catalysts are used in the commercial polymerization of small alpha-olefins such as ethylene and propylene. One such catalyst is prepared by depositing chromocene (bis (cyclopentadienyl) chromium (II)) on an inorganic metal oxide support, as disclosed in British Patent No. 1,253,063 to Karapinka. U.S. Patent No. 4,015,059, issued March 29, 1977 to Karol, describes the use of bis(indenyl)- and bis(flourenyl)-chromium (II) compounds supported on activated inorganic oxide supports as catalysts for the polymerization of ethylene. Recently, new synthetic methods have been described for preparing Cr +3 organometallic compounds. Theopold, J. Am. Chem. Soc. (1988), 110 , 5902 entitled "Cationic Chromium (III) Alkyls as Olefin Polymerization Catalysts", Theopold, Acc. Chem. Res. (1990), 23 , 263 entitled "Organochromium (III) Chemistry: A Neglected Oxidation State" and Thomas et al., J. Amer. Chem. Soc. , 113 (1991), p. 893 et seq. disclose that certain pentamethylcyclopentadienyl chromium (III) alkyls can be prepared, and that they can be used for making polyethylene homogeneously in CH 2 Cl 2 . However, these homogeneous Cr (III) polymerization catalysts have several deficiencies. These include low polymer productivity, rapid deactivation, and the need to use polar, non-coordinating solvents. Additionally, since they are homogeneous catalysts, they are unsuitable for gas phase olefin polymerizations. U.S. Patent No. 4,530,914, issued July 23, 1985 to Ewen et al., discloses a catalyst system for the polymerization of alpha-olefins which comprises two or more metallocenes, each having different propagation and termination rate constants, and aluminoxane. The metallocenes are cyclopentadienyl derivatives of a transition metal of Group 4b, 5b, and 6b metals of the Periodic Table. They are described by the formulas (C 5 R' m ) p R'' s (C 5 R' m )MeQ 3-p and R'' s (C 5 R' m ) 2 MeQ' where (C 5 R' m ) is a cyclopentadienyl or substituted cyclopentadienyl, each R' is hydrogen or a hydrocarbyl radical, R'' is an alkylene radical, a dialkyl germanium or silicon or an alkyl phosphine or amine radical bridging two (C 5 R' m ) rings, Q is a hydrocarbon radical, Me is a Group 4b, 5b, or 6b metal, s is 0 or 1, p is 0, 1, or 2; when p=0, s=0; m is 4 when s is 1 and m is 5 when s is 0. U.S. Patent No. 4,939,217, issued July 3, 1990 to Stricklen, also discloses a process for polymerizing olefins where the polymerization is conducted in the presence of hydrogen, and a catalyst system is used which contains aluminoxane and at least two metallocenes, each having different olefin polymerization termination rate constants. The metallocenes disclosed are similar to those described in aforementioned U.S. Patent No. 4,530,914. U.S. Patent No. 4,975,403, issued December 4, 1990 to Ewen, discloses a catalyst system for use in the polymerization of olefins. The catalyst system includes at least two different chiral, stereo-rigid metallocene catalysts of the formula R''(C 5 (R') 4 ) 2 MeQ p (where Me is a Group 4b, 5b or 6b metal and (C 5 (R') 4 ) is a cyclopentadienyl or substituted cyclopentadienyl ring) and an aluminum compound. Canadian Patent Application No. 2,000,567, published April 13, 1990, discloses a process for producing polyethylene using a composite catalyst made up of a solid catalyst component typified by a selected chromium compound, a modified aluminum compound typified by a trialkylaluminum, and an alkylaluminum alkoxide compound. The chromium compound may be chromium oxide, and the modified aluminum compound may be the reaction product of an organoaluminum compound and water. EP-0509294A and corresponding CA-A-2 063 090 disclose a catalyst system for the polymerization of alpha-olefins which comprises a cyclopentadienyl chromium hydrocarbyl compound in which the chromium has an oxidation state of +3 and which is supported on an inorganic support. Specific cyclopentadienyl chromium hydrocarbyl compounds are disclosed, including: Cp*Cr(BZyl) 2 (Pyr), Cp*Cr(CH 3 ) 2 (Pyr) and Cp*Cr(TMSM) 2 (Pyr), where Bzyl is benzyl and Pyr is pyridine. The activity of the supported Group 6b metal compounds is stated to increase when they are employed in conjunction with a co-catalyst which is a Group 2 or Group 3 metal alkyl compound. Therefore it is an object of the present invention to provide selected homogenous Group 6b metal catalyst systems for the homopolymerization and copolymerization of alpha-olefins having 2-8 carbon atoms including high polymer productivity, low deactivation, and no need to use polar, non-coordinating solvents, said catalysts should be suitable for slurry or gas phase olefin polymerization especially for polyethylene polymerization. These objects are solved by the catalyst system according to claim 1 or the process according to claim 13 respectively. The subclaims contain special embodiments of the invention. It has now been surprisingly found, that, when the hydrocarbyl compounds according to claim 1 or 3 in which the chromium is in an oxidation state of +3, are supported on inorganic metal oxide or inorganic metal phosphate supports, high pro-ductivity alpha-olefin polymerization catalysts are produced, and that the use of a co-catalyst improves the productivity of many of these compounds. In accordance with a first aspect of the present invention, there is provided a catalyst system for the homopolymerization and copolymerization of alpha-olefins having 2-8 carbon atoms, said catalyst system comprising a cyclopentadienyl chromium hydrocarbyl compound selected from: (C 5 (R') 5 ) a CrX b (L) or [(C 5 (R') 5 ) a CrX b (L) m ] + [A] - wherein (C 5 (R') 5 ) is a cyclopentadienyl or substituted cyclopentadienyl ring; R' is at each independent occurence hydrogen, a hydrocarbyl radical having 1 to 20 carbon atoms, or adjacent R' groups may together form one or more rings; X is a hydrocarbyl radical having 1-20 carbon atoms; L is N,N-dimethylaminopyridine or dimethylphenylphospine; a = 1 or 2, b = 1 or 2, where a+b = 3; m = 1 to 2 inclusive; and A is an anion, in which the Group 6b metal has an oxidation state of +3, said compound being supported on an inorganic support, which is an inorganic metal oxide support, an inorganic metal phosphate support or a silica support, said catalyst system having additionally a co-catalyst which is a group 2 or 3 metal alkyl compound. The cyclopentadienyl chromium hydrocarbyl compound is preferably selected from chromium compounds of the formula: Cp*Cr(CH 3 ) 2 (DMAP) Cp*Cr(CH 3 ) 2 (PMe 2 Ph) CpCr(CH 3 ) 2 (PMe 2 Ph) CpCr(CH 3 ) 2 (DMAP) Further provided in accordance with the present invention is a process for the homopolymerization or copolymerization of alpha-olefins having 2-8 carbon atoms comprising polymerizing said alpha-olefin, or copolymerizing two or more alpha-olefins in the presence of a catalyst system in accordance with the first aspect of the present invention. The present invention also provides a process for the homopolymerization or copolymerization of alpha-olefins comprising polymerizing said alpha-olefin, or copolymerizing two or more alpha-olefins in the presence of a catalyst system in accordance with the first aspect of the present invention. Further provided in accordance with the present invention is a process for the homopolymerization or copolymerization of alpha-olefins having 2-8 carbon atoms comprising polymerizing said alpha-olefin, or copolymerizing two or more alpha olefins in the presence of a catalyst system comprising a cyclopentadienyl chromium hydrocarbyl compound selected from Cp*Cr(CH 3 ) 2 (DMAP); Cp*Cr(CH 3 ) 2 (PMe 2 Ph); CpCr(CH 3 )(PMe 2 Ph); and CpCr(CH 3 ) 2 (DMAP), in which the chromium has an oxidation state of +3, said chromium compound being supported on an inorganic support, which is an inorganic metal oxide support, an inorganic metal phosphate support or a silica support, said catalyst system having additionally a co-catalyst which is a group 2 or 3 metal alkyl compound. In the above catalyst systems and processes, silica, aluminum phosphate and alumina aluminum phosphate are preferred supports, and aluminoxanes and trialkylaluminum compounds are preferred Group 2 or 3 metal alkyl compounds. Figures 1, 2 and 3 each show scanning electron micrographs of polyethylene samples which do not illustrate the claimed invention. The present invention provides catalyst systems for use in the polymerization (either homopolymerization or copolymerization) of alpha-olefins, including ethylene, propylene, 1-butene, 1-hexene and 4-methyl-1-pentene. It has quite surprisingly been found that, even though the productivity of many cyclopentadienyl Chromium hydrocarbyl compounds is quite low when employed as catalyst in the homogeneous polymerization of alpha-olefins, when the compounds used in claim 1 are supported on an inorganic metal oxide or inorganic phosphate solid support, their productivity increases dramatically, especially when co-catalysts are used. While the catalyst systems of the present invention can be used to polymerize a variety of alpha-olefins, they are especially useful in the polymerization of ethylene. These catalysts produce polyethylene in high yield, and the polymers produced have remarkably uniform particle size and highly desirable morphology (i.e., substantially spherical) that is suitable for gas phase polymerizations. The catalysts of the present invention allow the use of hydrogen during polymerization of polyethylene to reduce the molecular weight and to broaden the molecular weight distribution. In addition, the catalyst systems of this invention produce polyethylene with a variety of molecular weight distributions, depending on the support used. Referring now to the Figures, Figure 1 shows a scanning electron micrograph (SEM) at X10 magnification of a polyethylene sample produced by homogeneous polymerization using [Cp*Cr(THF) 2 CH 3 ] + [BPh 4 ] - (where Cp* represents pentamethylcyclopentadienyl, THF is tetrahydrofuran, and Ph is phenyl). As can be seen, this sample is characterized by very small, irregularly shaped particles. These particles are typically less than 20-50 µm (microns) in diameter. Figure 2 shows an SEM at X10 magnification of a polyethylene sample produced by the method of the present invention using Cp*Cr(CH 3 ) 2 (THF) on a silica support. As can be seen, this sample has particles of much larger size (about 1 mm in diameter) than those in Figure 1. The particle size is quite suitable for gas phase polymerization applications. Figure 3 shows a SEM of a polyethylene sample produced by the method of this invention using Cp*Cr(CH 3 ) 2 (THF) on a Al 2 O 3 ·2AlPO 4 support. As can be seen, the particles are quite uniform in size, and primarily spherical in nature. Again, the particle size and spherical nature of the polymer makes this system attractive for gas phase polymerization applications. Activities for the catalyst systems of the present invention are greater than 3,000 grams of polymer per gram of chromium metal per hour ("g/g Cr/hr"), preferably greater than 30,000 g/g Cr/hr, and more preferably greater than 200,000 g/g Cr/hr. The term molecular weight distribution ("MWD"), as used herein, is the weight average molecular weight ("M w ") divided by the number average molecular weight ("M n "), i.e., M w /M n . The polymers produced in accordance with the present invention using silica supported catalysts have a MWD greater than 10, preferably greater than 15, and more preferably greater than 20. These polymers, which have high MWD's, have improved ease of processing, better melt behavior, and other desirable properties such as impact resistance and environmental stress crack resistance. Large blow molded products are superior when made with high MWD polymers. Additionally, film is more puncture resistant when made from polymer with a high MWD. The polymers made in accordance with this invention using alumina aluminum phosphate supported catalysts possess high molecular weight and a more narrow MWD, making them useful in such applications as injection molding. Typically, the MWD for polymers made with alumina aluminum phosphate supported catalysts is less than 3. The catalyst systems of the present invention comprise at least one cyclopentadienyl chromium hydrocarbyl compound in which the chromium is in an oxidation state of +3, and which is catalytically active when deposited on an inorganic metal oxide or inorganic metal phosphate or silica support. As used herein, the term "cyclopentadienyl" refers to unsubstituted cyclopentadienyl as well as substituted derivatives of cyclopentadienyl in which the cyclopentadienyl ring contains one or more substituents which do not interfere with the chromium compound's ability to function as an alpha-olefin polymerization catalyst. Examples of substituted cyclopentadienyl include pentamethylcyclopentadienyl, methylcyclopentadienyl, t-butylcyclopentadienyl, and pentaphenylcyclopentadienyl, as well as compounds where the substituent forms a multi-cyclic ring with the cyclopentadienyl ring. Examples of these multi-cyclic rings include indenyl and fluorenyl rings. For the sake of simplicity, the abbreviation "Cp" will be used herein to refer to unsubstituted cyclopentadienyl, and the abbreviation "Cp*" will be used to refer to pentamethylcyclopentadienyl. Cp* is a preferred cyclopentadienyl group as it stabilizes the organometallic compound of this invention. These chromium compounds have, in addition to one cyclopentadienyl group, at least one hydrocarbyl group bonded to the metal atom. As used herein, the term "hydrocarbyl" refers to alkyl, alkenyl, aryl, aralkyl and alkaryl radicals and the like. Exemplary hydrocarbyl radicals include, but are not limited to, methyl, ethyl, propyl, butyl, amyl, isoamyl, hexyl, neopentyl, isobutyl, heptyl, octyl, nonyl, decyl, cetyl, phenyl, benzyl and other similar groups. Additionally, organosilyl groups, such as trimethylsilyl methyl, i.e., (CH 3 ) 3 SiCH 2 -, and the like can be used. If more than one hydrocarbyl group is bonded to the metal atom, they can be independent or linked, i.e., they can form a 3-, 4-, 5-, 6-, or 7-membered metallocycle. Preferably, the hydrocarbyl group is sigma bonded to the chromium. In addition to the cyclopentadienyl and hydrocarbyl groups, the chromium compounds of the present invention may also contain one or more sigma donor stabilizing ligands. These ligands contain an atom, such as oxygen, nitrogen, phosphorous or sulfur, which has a nonbonded electron pair. Examples of these ligands include, ethers, amines, phosphines and thioethers. The chromium compound used in this invention is selected from compounds having the following general formulas: (C 5 (R') 5 ) a MX b L or [(C 5 (R') 5 ) a MX b (L) m ] + [A] - wherein M is chromium; (C 5 (R') 5 ) is a cyclopentadienyl or substituted cyclopentadienyl ring; R' is at each independent occurrence hydrogen, a hydrocarbyl radical having 1-20 carbon atoms, or adjacent R' groups may together form one or more rings; X is a hydrocarbyl radical having 1-20 carbon atoms (for example, a monovalent saturated aliphatic or alicyclic radical or a monovalent aromatic radical, or combinations thereof); a = 1 or 2, b = 1 or 2 where a+b = 3; L is N,N-dimethylaminopyridine or dimethylphenylphosphine; m = 1 to 2 inclusive; and A is an anion. Examples of compunds having Formula (I) above include Cp*Cr(CH 3 ) 2 (DMAP), Cp*Cr(CH 3 ) 2 (PMe 2 Ph), and CpCr(CH 3 ) 2 (DMAP), where DMAP is N,N-dimethylaminopyridine, and PMe 2 Ph is dimethylphenylphosphine. An especially preferred compound is Cp*Cr(CH 3 ) 2 (PMe 2 Ph). Theopold, J. Am. Chem. Soc. (1988), 110 , 5902 entitled "Cationic Chromium (III) Alkyls as Olefin Polymerization Catalysts", Theopold, Acc. Chem. Res. (1990), 23 , 263 entitled "Organochromium (III) Chemistry: A Neglected Oxidation State", and Thomas et al., J. Amer. Chem. Soc. , 113 (1991), p. 893 et seq. describe syntheses useful in making some of the Group 6b metal compounds of this invention. Similar procedures can be used to make related compounds. In the catalyst systems of the present invention, the chromium compound is deposited on an inorganic support selected from inorganic metal oxide, inorganic metal phosphate and silica supports. Suitable inorganic metal oxide supports include alumina, silica-alumina mixtures, thoria, zirconia, magnesium oxide and similar oxides. Suitable inorganic metal phosphates include aluminum phosphate, zirconium phosphate, magnesium-containing alumina phosphate and alumina aluminum phosphate. Silicas, aluminum phosphates and alumina aluminum phosphates are preferred. Suitable silica supports include Davison 952, Davison 955, Crosfield EP-10 and Crosfield EP17MS. Further examples of useful supports are the following: alumina aluminum phosphates with aluminum to phosphorus ratios of about 5:1 to 1:1 as disclosed in U.S. Patents Nos. 4,080,311 and 4,219,444; magnesia-alumina-aluminum phosphates as described in U.S. Patent No. 4,210,560; zinc oxide-cadmium oxide-alumina-aluminum phosphates such as those disclosed in U.S. Patent No. 4,367,067; and the calcium, barium, and/or strontium oxide-alumina-aluminum phosphates described in U.S. Patent Nos. 4,382,877 and 4,382,878. The acidity of these supports can be adjusted by judicious inclusion of basic metals such as alkali and alkaline earth metals (Ca, Be, Mg, K, Li) to counteract excessive acidity. Other useful supports include magnesium halides, particularly magnesium chloride, such as those described in "Transition Metals and Organometallics as Catalysts for Olefin Polymerization" (1988, Springer-Verlag) edited by W. Kaminsky and H. Sinn and "Transition Metal Catalyzed Polymerizations-Ziegler-Natta and Metathesis Polymerizations" (1988, Cambridge University Press) edited by R. Quirk. The supports useful in this invention should have a high surface area. In general, these supports should have the characteristics listed in the following table: Property Broad Range Preferred Range Surface area 25-600 m 2 /g 100-370 m 2 /g Pore volume 0.25-4 cm 3 /g 0.7-3 cm 3 /g Mean particle diameter 30-200 microns 60-140 microns Preferably, the pore size distribution is broad, with a significant percentage of the pores in the macropore range(>50nm) (>500 Angstroms). Preferably, at least 50% of the pores are macropores. It is also desirable that the support be substantially anhydrous before the chromium compound is deposited on it. Thus, it is desirable to calcine the support prior to deposition of the chromium compound. The supported catalysts of this invention are readily prepared by techniques well known in the art. For example, a solution of the chromium compound in aliphatic, aromatic or cycloaliphatic hydrocarbons, or ethers such as diethyl ether or tetrahydrofuran can be stirred with the support until the chromium compound is adsorbed on or reacted with the support. The amount of chromium compound relative to the amount of support will vary considerably depending upon such factors as the particle size of the support, its pore size and surface area, the solubility of the chromium compound in the solvent employed, and the amount of chromium compound which is to be deposited on the support. However, in general the amount of chromium compound used is adjusted so that the final metal content (calculated as the element), relative to the support, is in the range of from 0.01 to 10 weight percent. In most cases, the most desirable level is in the range of 0.1 to 5 weight percent. It has been found that the activity of many of the supported chromium compounds of this invention is significantly increased when they are employed in conjunction with a co-catalyst. The co-catalysts useful in the practice of the present invention are Group 2 and Group 3 metal alkyls. As used herein, the term "Group 2 and Group 3 metal alkyls" refers to compounds containing a metal from Group 2 or Group 3 of the Periodic Table (such as Mg, Zn, B, or Al) to which is bonded at least one alkyl group, preferably a C 1 to C 8 alkyl group. Suitable Group 2 and Group 3 metal alkyls include dialkyl magnesium, dialkyl zinc, trialkylboranes, and aluminum alkyls. Suitable aluminum alkyls include trialkylaluminums (such as trimethylaluminum, triethylaluminum, triisobutylaluminum and trioctylaluminum). Trialkylaluminums with alkyl groups of four carbons or greater are preferred. Other aluminum alkyls useful in the practice of the present invention include alkylaluminum alkoxides (such as diethylaluminum ethoxide and ethylaluminum diethoxide), and alkylaluminum halides (such as diethylaluminum chloride, diethylaluminum bromide, diethylaluminum iodide, diethylaluminum fluoride, ethyl aluminum dichloride, ethyl aluminum dibromide, ethyl aluminum diiodide, ethyl aluminum difluoride, and ethyl aluminum sesquichloride). Other suitable aluminum alkyls are aluminoxanes, including those represented by the general formula (R-Al-O) n for the cyclic form and R(R-Al-O) n -AlR 2 for the linear form. In these formulas, R is, at each independent occurrence, an alkyl group (such as methyl, butyl, isobutyl and the like) preferably with more than two carbon atoms, more preferably with 3-5 carbon atoms, and n is an integer, preferably from 1 to 20. Most preferably, R is an isobutyl group. Mixtures of linear and cyclic aluminoxanes may also be used. Examples of aluminoxanes useful in this invention include, but are not limited to, ethyl aluminoxane, isobutyl aluminoxane, and methyl aluminoxane. Aluminoxanes (also known as "alumoxanes") suitable for use in this invention are described in Pasynkiewicz, "Alumoxanes: Synthesis, Structure, Complexes and Reactions," Polyhedron 9, p. 429 (1990). The preferred Group 2 and Group 3 metal alkyls are the aluminoxanes and the trialkylaluminums. The Group 2 and Group 3 metal alkyls are used in a Group 2 or 3 metal alkyl to chromium compound mole ratio of from 1:1 to 1000:1. The preferred mole ratio is from 10:1 to 200:1. The catalyst systems of the present invention may be used in either slurry or gas phase polymerization processes. After the catalysts have been formed, the polymerization reaction is conducted by contacting the monomer charge with a catalytic amount of the catalyst at a temperature and at a pressure sufficient to initiate the polymerization reaction. If desired, an organic solvent may be used as a diluent and to facilitate materials handling. The polymerization reaction is carried out at temperatures of from 30°C or less up to 200°C or more, depending to a great extent on the operating pressure, the pressure of the entire monomer charge, the particular catalyst being used, and its concentration. Preferably, the temperature is from 30°C to 125°C. The pressure can be any pressure sufficient to initiate the polymerization of the monomer charge, and can be from atmospheric pressure up to 6.9x10 6 Pa (1000 psig As a general rule, a pressure of 1.38x10 5 to 5.5x10 6 Pa (20 to 800 psig) is preferred. When the catalyst is used in a slurry-type process, an inert solvent medium is used. The solvent should be one which is inert to all other components and products of the reaction system, and be stable at the reaction conditions being used. It is not necessary, however, that the inert organic solvent medium also serve as a solvent for the polymer produced. The inert organic solvents which may be used include saturated aliphatic hydrocarbons (such as hexane, heptane, pentane, isopentane, isooctane, purified kerosene and the like), saturated cycloaliphatic hydrocarbons (such as cyclohexane, cyclopentane, dimethylcyclopentane, methylcyclopentane and the like), aromatic hydrocarbons (such as benzene, toluene, xylene and the like), and chlorinated hydrocarbons (such as chlorobenzene, tetrachloroethylene, o-dichlorobenzene and the like). Particularly preferred solvents are cyclohexane, pentane, isopentane, hexane and heptane. When the catalyst is used in a gas phase process, it is suspended in a fluidized bed with, e.g., ethylene. Temperature, pressure and ethylene flow rates are adjusted so that to maintain acceptable fluidization of the catalyst particles and resultant polymer particles. Further descriptions of such a fluidized bed may be found in British Patent No. 1,253,063, to Karapinka. The following examples are intended to further illustrate the present invention. EXAMPLES Examples 1 to 17, 22 and 23 are not in accordance with the invention and are provided by way of example and reference only. EXAMPLE 1 SUPPORTS Silica supports were purchased from W. R. Grace & Co., and included Davison 952 and Davison 955 silicas. These silicas have the following properties: Property Davison 952 Davison 955 Surface area 340 m 2 /g 300 m 2 /g Pore volume 1.68 cm 3 /g 1.60 cm 3 /g Mean particle diameter 110 µm 40 µm Other silica supports were purchased from Crosfield Catalysts. These included EP-10, EP-11 and EP-12 supports. Some properties of the EP-10 support are: Property Crosfield EP-10 Surface area 320 m 2 /g Pore volume 1.80 cm 3 /g Mean particle diameter 105 µm The AlPO 4 support was purchased from W.R. Grace & Co. The alumina aluminum phosphate supports used in the following examples were prepared by the procedure of Example 1 in U.S. Patent No. 4,080,311, issued March 21, 1978 to Kehl. The product had an Al 2 O 3 to AlPO 4 ratio of 1:2. CATALYST PREPARATIONS In the preparation of the following catalysts, all manipulations were performed under argon using glove box or Schlenk techniques. All solvents were thoroughly dried over Na/benzophenone or calcium hydride and distilled prior to use. EXAMPLE 2 [Cp*Cr(CH 3 ) 2 ] 2 The organochromium compound [CP*Cr(CH 3 ) 2 ] 2 was prepared by the procedure described in Theopold, Acc. Chem. Res., 23 (1990), p. 264. EXAMPLE 3 SUPPORTED [Cp*Cr(CH 3 ) 2 ] 2 The organochromium compound [Cp*Cr(CH 3 ) 2 ] 2 (0.040 g, 9.2 x 10 -5 mole), prepared as described in Example 2, was dissolved in 10 ml of pentane, giving a dark brown solution to which was added Davison 952 silica (1.00 g). The resulting mixture was stirred for 15 minutes, giving a dark brown solid and a clear supernatant. The resulting solid catalyst was washed with pentane, and dried to a free-flowing powder. EXAMPLE 4 SUPPORTED Cp*Cr(CH 3 ) 2 (THF) [Cp*Cr(CH 3 ) 2 ] 2 (0.040 g, 9.2 x 10-5 mole) was added to 20 ml of tetrahydrofuran ("THF") and stirred for 0.5 hour, generating a green colored solution containing Cp*Cr(CH 3 ) 2 (THF). Al 2 O 3 ·2AlPO 4 (1.0 g) solid support was added all at once to this solution, and the resulting mixture was stirred for several minutes. All of the organochromium compound reacted with the solid support yielding a deep purple catalyst and a clear supernatant. The resulting catalyst slurry was filtered and the purple solid was washed twice with 10 ml of THF and dried under vacuum to a free flowing powder. EXAMPLE 5 [Cp*CrCH 3 (THF) 2 ] + [BPh 4 ] - This compound was prepared by the method described in Thomas et al., J. Amer. Chem. Soc. , 113 (1990), p. 900. Preparation No. 13, method B was used to prepare compound number 14 in that paper, i.e., [Cp*CrCH 3 (THF) 2 ] + [BPh 4 ] - . EXAMPLE 6 SUPPORTED [Cp*CrCH 3 (THF) 2 ] + [BPh 4 ] - [Cp*CrCH 3 (THF) 2 ] + [BPh 4 ] - (0.075 g, 1.1 x 10 -4 mole) was dissolved in 20 ml of THF and treated all at once with 1.00 g of Al2O 3 ·2AlPO 4 . The resulting mixture was stirred for 15 minutes resulting in a dark blue solid and a clear supernatant. The solid was washed with THF, and dried to a free-flowing powder. COMPARATIVE EXAMPLE A ETHYLENE POLYMERIZATION USING AN UNSUPPORTED CATALYST 90.1 micromoles of [Cp*CrCH 3 (THF) 2 ] + [BPh 4 ] - was dissolved in 25 ml methylene chloride in a 50 ml Fischer-Porter bottle, and pressured to 50 psig with ethylene. The reactor was stirred at 25°C for 1.0 hour. Initially, the ethylene uptake was rapid, but this rate decreased rapidly over the first half hour. The reaction was stopped by venting the pressure. The polymer produced was washed with isopropanol and then with acetone. The polymer was then dried under vacuum. The results of this polymerization are indicated in Run 1 in Tables I and II. COMPARATIVE EXAMPLE B ETHYLENE POLYMERIZATION USING AN UNSUPPORTED CATALYST AND A CO-CATALYST The procedure of Comparative Example A was repeated, except that 71 molar equivalents of isobutyl aluminoxane (IBAO) was added to the reaction vessel prior to pressurization with ethylene. The results of this polymerization are indicated in Run 2 in Tables I and II. EXAMPLE 7 ETHYLENE POLYMERIZATION Polymerization runs were conducted in 1 or 2 liter autoclave reactors under particle form (slurry) conditions using between 300 and 500 ml heptane as diluent, and a weighed amount of catalyst (typically 0.050 to 0.250 g). Run times of 0.5 to 1.0 hour were normally employed. For example, in a typical run, 0.100 g of the catalyst prepared in Example 4 (Cp*Cr(CH 3 ) 2 (THF) adsorbed on Al 2 O 3 .2AlPO 4 ) was charged to a one-liter autoclave along with 300 ml of heptane. Polyisobutylaluminoxane (0.5 ml of a 1.0M heptane solution, prepared by slow hydrolysis of triisobutylaluminum with 1.0 equivalents of H 2 O as in Example 3 of U.S. Patent No. 4,665,208, issued May 12, 1987 to Welborn et al.) was added to stirred reactor as co-catalyst. The reactor temperature and pressure were adjusted to 85° C. and 3.79x10 6 Pa (550 psi) (with ethylene), respectively. The ethylene was supplied on demand from a pressurized reservoir. After 0.5 hour, the reaction was stopped by rapidly cooling the reactor and venting the pressure. The polymer produced was washed with isopropanol and acetone, and dried under vacuum to yield 82.9 g of white, granular solid. The results of this polymerization are indicated in Run 15 in Tables III and IV. Polymerization runs similar to that described above were conducted using the catalysts and conditions shown in Tables I, III, and V below. Analytical data for the polyethylenes produced in these runs is shown in Tables II, IV and VI below. All molecular weights in these tables were determined by gel permeation chromatography. EXAMPLE 8 GAS PHASE POLYMERIZATION The procedure of Example 7 is repeated in a 2 liter, stirred autoclave using the supported Cr +3 catalysts described above, except that heptane is not added to the autoclave. The reactor temperature and pressure are adjusted to 85°C 3.79x10 6 Pa (550 psi) (with ethylene), respectively. A white granular polymer is produced. POLYMERIZATION DATA FOR [Cp*CrMe(THF) 2 ][BPh 4 ] Run Support µmol Cr Co- catalyst Al:Cr C 2 H 4 , (psig) Temp. °C Activity Activity 1 none 90.1 -- 0 3.45x10 5 Pa (50) 25 510 40 2 none 90.1 IBAO 71:1 3.45x10 5 Pa (50) 25 89 7 3 Davison 952 Silica 28.2 IBAO 71:1 (50) 3.45x10 5 Pa 25 6,690 72 4 Davison 952 Silica 21.6 -- 0 3.8x10 6 Pa (550) 80 0 0 5 Davison 952 Silica 27.0 IBAO 110:1 3.8x10 6 Pa (550) 80 48,400 523 6 Davison 952 Silica 27.0 IBAO 71:1 3.8x10 6 Pa (550) 85 50,600 546 7 Davison 952 Silica 27.0 Al(CH 3 ) 3 71:1 3.8x10 6 Pa (550) 85 3,700 40 8 Al 2 O 3 ·2AlPO 4 15.0 IBAO 33:1 3.8x10 6 Pa (550) 85 233,000 2516 ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH [Cp*CrMe(THF) 2 ][BPh 4 ] Run Support T m , °C Density g/cc Mean Particle Diameter, Microns Mw x 10 -3 MMD 1 -- 135.5 -- -- 125 5.8 5 Davison 952 Silica 138.8 -- 830 252 12.8 6 Davison 952 Silica 137.9 0.942 850 258 22.6 7 Davison 952 Silica 136.3 -- -- 236 34.2 8 Al 2 O 3 ·2AlPO 4 138.0 0.927 -- 919 4.41 POLYMERIZATION DATA FOR SUPPORTED Cp*CrMe 2 (THF) Run Support µmol Cr Co-catalyst Al:Cr C 2 H 4 , (psig) Pa Temp. °C Activity Activity 9 Davison 952 Silica 46.0 -- 0 (550) 3.8x10 6 80 0 0 10 Davison 952 Silica 46.0 EAO 44:1 (550) 3.8x10 6 80 15,200 164 11 Davison 952 Silica 46.0 IBAO 44:1 (550) 3.8x10 6 85 33,000 356 12 Davison 955 Silica 46.0 IBAO 44:1 (550) 3.8x10 6 85 51,000 551 13 Davison 955 Silica 18.4 IBAO 54:1 (550) 3.8x10 6 85 55,900 604 14 Al 2 O 3 ·2AlPO 4 46.0 -- 0 (550) 3.8x10 6 85 5,400 58 15 Al 2 O 3 ·2AlPO 4 18.4 IBAO 27:1 (550) 3.8x10 6 85 173,000 1868 16 Al 2 O 3 ·2AlPO 4 18.4 IBAO 54:1 (550) 3.8x10 6 65 272,000 2938 17 Al 2 O 3 ·2AlPO 4 18.4 IBAO 27:1 (550) 3.8x10 6 65 169,000 1825 18 Al 2 O 3 ·2AlPO 4 18.4 IBAO 27:1 (550) 3.8x10 6 85 240,000 2592 ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH SUPPORTED Cp*CrMe 2 (THF) Run Support T m , °C Density g/cc Mw x 10 -3 MWD 10 Davison 952 Silica 138.4 0.941 306 18.2 11 Davison 952 Silica 139.6 -- 293 19.2 12 Davison 955 Silica 138.3 -- 301 20.4 13 Davison 955 Silica 138.3 0.941 270 14.4 14 Al 2 O 3 ·2AlPO 4 135.1 -- 805 2.68 15 Al 2 O 3 ·2AlPO 4 134.7 -- 790 2.63 16 Al 2 O 3 ·2AlPO 4 136.6 0.927 1130 2.75 17 Al 2 O 3 ·2AlPO 4 139.0 0.924 917 4.13 18 Al 2 O 3 ·2AlPO 4 138.1 0.926 1134 5.61 POLYMERIZATION DATA FOR SUPPORTED [Cp*CrMe 2 ] 2 Run Support µmol Cr Co-cat Al:Cr C 2 H 4 , Pa (psig) Temp. °C Activity Activity 19 Davison 952 Silica 76.7 -- 0 (550) 3.8x10 6 85 15,200 164 20 Davison 955 Silica 74.8 -- 0 (550) 3.8x10 6 85 16,000 173 21 Al 2 O 3 ·2AlPO 4 57.5 -- 0 (550) 3.8x10 6 85 2,900 31 ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH SUPPORTED [Cp*CrMe 2 ] 2 Run Support T m , °C Density g/cc Mean Particle Diameter, Microns Mw x 10 -3 MWD 19 Davison 952 Silica 139.3 -- 910 252 23.5 20 Davison 955 Silica 140.6 -- -- 347 14.7 21 Al 2 O 3 ·2AlPO 4 138.3 -- -- -- -- Looking at Tables I and II, it can be seen that the polymerization using the homogeneous cationic Cr +3 compound has low activity (Run 1), and that adding triisobutylaluminoxane does not improve the activity, but rather reduces it (Run 2). These runs were performed at 25°C so as to avoid decomposition of the thermally labile homogeneous catalyst. In contrast, Run 3 shows an approximately ten-fold improvement in activity using a supported catalyst system. Runs 4-8 show the need for a co-catalyst when using this cationic Cr +3 compound. The aluminoxane co-catalyst gives improved activity over the trimethylaluminum co-catalyst. Additionally, higher molecular weights (M w ) and higher molecular weight distributions ( MWD = M w /M n ) are obtained with the catalyst system of the present invention (see Table III). The activity of this catalyst system was highest when the support was an alumina aluminum phosphate support, and the polymer had higher molecular weight as well. Looking at Tables III and IV, a co-catalyst appears to be necessary with the silica support and is advantageous with the alumina aluminum phosphate support. Using the aluminoxane with the longer alkyl groups (isobutyl vs. ethyl) gives higher activities. Also, the Davison 955 silica, which has a substantially smaller average particle size than the Davison 952 silica, gives higher activity (compare Runs 10 and 11 with Runs 12 and 13). Table III also shows that the catalyst systems perform exceptionally well over the temperature range of 65°-85°C. Looking at Tables V and VI, the catalyst system based on [Cp*Cr(CH 3 ) 2 ] 2 dimer is also quite active, and gives polymers with very attractive high molecular weights and broad (high) MWD's. EXAMPLE 9 Cp*Cr(TMSM) 2 1.318 g of CrCl 3 (THF) 3 was placed in a 100 ml Schlenk flask along with a stirring bar and about 50-60 ml of THF. 0.500 g of Cp*Li was added to the resulting slurry producing a blue solution ([Cp*CrCl 2 ] 2 ). This solution was allowed to stir for at least three hours (preferably overnight). To the stirring solution was slowly added 2 equivalents of LiCH 2 Si(CH 3 ) 3 . The solution changed from blue to purple. The THF was then removed by rotoevaporation and the resulting Solid was dissolved in pentane yielding a red brown solution which was filtered to remove LiCl. The pentane was removed by rotoevaporation and the solid was redissolved in a minimum amount of pentane and crystallized at -30°C. Yield 50-60%. It is important to note that this compound is thermally unstable and decomposes at room temperature liberating tetramethylsilane. EXAMPLE 10 SUPPORTED Cp*Cr(TMSM) 2 Cp*Cr(TMSM) 2 (0.075 g) was dissolved in 10 ml of pentane. Al 2 O 3 ·2AlPO 4 (1.00 g) was added all at once to the stirred solution resulting in the formation of a purple solid and clear supernatant after 15 minutes. The solid was collected, washed twice with pentane, and dried in vacuo to a free-flowing powder. EXAMPLE 11 The supported Cp*Cr(TMSM) 2 prepared in Example 10 was used to polymerize ethylene by a procedure similar to that described in Example 7, except that the polymerization was performed at 80°C-85°C and 3.8x10 6 Pa (550 psi) total pressure (ethylene and hydrogen). The results of these polymerization runs are indicated in Table VII below, and analytical data for the polyethylenes produced are indicated in Table VIII below. POLYMERIZATION DATA FOR SUPPORTED Cp*Cr(TMSM) 2 Run µ mol Co Al:Cr H 2 Pa (psi) Temp °C Activity Activity 22 31 None 0 0 (0) 80 2,500 27 23 16 IBAO 16:1 0 (0) 80 250,000 2700 24 16 IBAO 32:1 0 (0) 80 341,000 3680 25 16 IBAO 32:1 0 (0) 80 372,000 4010 26 16 IBAO 19:1 0 (0) 80 248,000 2670 27 16 IBAO 19:1 0 (0) 80 230,000 2480 28 16 IBAO 32:1 6.9x10 3 (10) 80 294,000 3170 29 16 IBAO 32:1 1.72x10 3 (25) 80 340,000 3660 30 16 IBAO 32:1 1.72x10 3 (25) 80 227,000 2450 31 16 IBAO 32:1 3.4x10 5 (50) 80 227,000 2452 32 16 IBAO 32:1 3.4x10 5 (50) 80 249,000 2689 33 16 IBAO 32:1 6.9x10 5 (100) 80 194,000 2091 34 16 IBAO 32:1 1.38x10 6 (200) 80 124,000 1339 35 16 TEB 32:1 (0) 80 ∼0 0 All polymerizations performed at 3.8x10 6 Pa (550 psi) total pressure (ethylene plus hydrogen). ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH SUPPORTED Cp*Cr(TMSM) 2 Run T m , °C MI HLMI Mw x 10 -3 MWD 23 139.1 0 0 1,124 2.02 24 139.4 0 0 891 7.61 25 136.3 - - 1,075 2.72 26 138.1 - - 901 2.71 27 137.6 - - 824 2.42 28 139.9 0 0 -- -- 29 139.9 0 2.27 330 9.29 30 141.9 0 2.03 276 8.52 31 139.7 0 6.50 228 9.62 32 138.8 0 11.9 205.6 9.40 33 138.0 2.12 12.7 116.3 8.37 34 135.0 High High 55.8 10.50 EXAMPLE 12 Cp*Cr(Bzyl) 2 (THF) To a slurry of CrCl 3 (THF) 3 (2.00 g, 5.33 mmoles) in 50 ml of THF was added LiCp* (0.76 g, 5.34 mmoles) slowly with stirring to yield a deep blue solution. This solution was stirred for two hours. Slow addition of benzyl magnesium chloride (5.3 ml of 2.0 M solution) resulted in a deep purple solution after complete addition. Solvent was subsequently removed under vacuum to yield a sticky purple residue. Pentane (200 ml) was added and stirred overnight. The pentane solution slowly became green-brown during this time. The pentane solution was filtered to remove metal halides, concentrated to ca. 75 ml and stored at -40°C overnight. The crystalline material that formed was collected, washed with cold pentane, and dried under vacuum, affording 680 mg (29%) of dark brown material. COMPARATIVE EXAMPLE 13 HOMOGENEOUS POLYMERIZATION WITH Cp*Cr(Bzyl) 2 (THF) Seventy-five milligrams of Cp*Cr(CH 2 Ph) 2 (THF) was dissolved in 50 ml of heptane and placed in a thick-walled glass vessel which was attached to a purified ethylene supply. Ethylene was added to 50 psi at ca. 20°C. A mild exotherm ensued with the generation of 0.70 g of beige polymer after one hour. The catalyst was essentially inactive after one hour as evidenced by the lack of ethylene uptake. EXAMPLE 14 Cp*Cr(Bzyl) 2 (THF) was supported on Al 2 O 3 ·2AlPO 4 (which had been dehydrated at 400°C for 48 hours) and used to polymerize ethylene using the procedure described in Example 11. The results of these polymerization runs are indicated in Tables IX and X below. POLYMERIZATION DATA FOR Cp*Cr(Bzyl) 2 (THF) Run µ mol Cr Co- catalyst Al:Cr C 2 H 4 (psi) Pa Temp (°C) Activity Activity 36 12 IBAO 25:1 3.8x10 6 (550) 80 444,000 3900 37 12 IBAO 25:1 3.8x10 6 (550) 80 235,000 1940 38 12 IBAO 25:1 3.8x10 6 (550) 80 230,000 1900 39 12 IBAO 25:1 3.8x10 6 (550) 80 613,000 5000 40 , 12 IBAO 25:1 2.07x10 6 (300) 80 236,000 1940 41 158 ? 0 3.4x10 5 (50) 80 720 85 ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH Cp*Cr(Bzyl) 2 (THF) Run T m , C Density M w x10 -3 MWD 39 135.7 0.9288 1,243 1.75 40 135.4 0.9325 881 3.13 41 --- --- 22.6 2.34 EXAMPLE 15 Cp*Cr(CH 3 ) 2 (Pyr) This compound was prepared following the general description contained in Noh, S.K.; Sendlinger, S. C.; Janiak, C.; Theopold, K. H. J. Am. Chem Soc. (1989), 111, 9127. Lithium cyclopentadienide (0.380 g, 2.67 mmol) was added slowly to a slurry of 1.00 g (2.67 mmol) of CrCl 3 (THF) 3 in 50 mL of THF. The resulting blue solution was stirred for 2 hours. Pyridine (0.222 g, 2.80 mmol) was added resulting in the deposition of a light blue solid. Stirring was continued for 1 hour after which was added (dropwise) 2.0 equivalents (3.80 mL of 1.4 M solution in Et 2 O) of methyllithium. The dark green-brown solution was stirred an additional 0.5 hr and then taken to dryness under vacuum. The dark solid was extracted into pentane, filtered to remove metal halides, and taken dryness. The remaining solid was reextracted into pentane, filtered, and the solvent was reduced until microcrystals appeared. The dark brown solution was kept at -40°C overnight resulting in the depositon of black crystals. The crystals were collected and dried under vacuum. EXAMPLE 16 Cp*Cr(Bzyl) 2 (Pyr) This compound was prepared as in Example 15 except that two equivalents of benzylmagnesium bromide were substituted for methyllithium. A microcrystalline solid formed and was dried under vacuum. Anal. Calc. for C 29 H 34 NCr: C,77.65; H,7.64; N,3.12. Found: C,77.03; H,7.48; N,2.80. EXAMPLE 17 Cp*Cr(TMSM) 2 (Pyr) This compound was prepared as in Example 15 except that two equivalents of trimethylsilylmethyllithium solution were added in place of methyllithium. Long, black needles formed after cooling to -40 °C overnight. These were collected and dried to yield 1.30 g (55%) of pure material. Anal. Calc. for C 23 H 42 NSi 2 Cr: C, 62.67; H, 9.60; N, 3.17. Found: C, 62.36; H, 9.46; N, 2.84. EXAMPLE 18 (according to the invention) CP*Cr(CH 3 ) 2 (DMAP) This compound was prepared as described in Example 15 except that 1.05 equivalents of N,N-dimethylaminopyridine (DMAP) were added instead of pyridine. Large, dark brown crystals were collected and dried under vacuum (710 mg, 78% yield). Anal. Calc. (Found) for C 19 H 31 N 2 Cr: C, 67.22 (66.69); H, 9.20 (9.01); N, 8.25 (7.73). EXAMPLE 19 (according to the invention) CpCr(CH 3 ) 2 (DMAP) This compound was prepared as described in Example 15 except that 1.0 equivalent of a 1.0 M solution of sodium cyclopentadienide in the THF was added in place of lithium pentamethycyclopentadienide. Dark brown microcrystals were obtained in 67% overall yield (485 mg): Anal. Calc. (Found) for C 14 H 21 N 2 Cr: C, 62.43 (62.12); H, 7.88 (7.87); N, 10.40 (10.42). EXAMPLE 20 (according to the invention) Cp*Cr(CH 3 ) 2 (PMe 2 Ph) This compound was prepared as described in Example 15 except that 1.05 equivalents of dimethylphenylphosphine (PMe 2 Ph) were added instead of pyridine. Large blue/purple crystals were obtained in 56% overall yield (530 mg). Anal. Calc. (Found) for C 20 H 32 PCr: C, 67.58 (67.14); H, 9.07 (8.96); N, 0.0 (0.12) EXAMPLE 21 (according to the invention) CpCr(CH 3 ) 2 (PMe 2 Ph) This material was prepared according to Example 20 except that 1.0 equivalents of sodium cyclopentadienide was added in place of lithium pentamethylcyclpentadienide. Long blue/purple needles were obtained in 59% yield (453 mg). Anal. Calc. (Found) for C 15 H 22 PCr: c, 63.15 (62.33); H, 7.77 (7.59); N, 0.0 (0.0). EXAMPLE 22 Cp*Cr(CH 3 )(3,5-Lutidine) Prepared as in Example 15 above except that 1.05 equivalents of 3,5-lutidine were added in place of pyridine. Dark microcrystals (510 mg, 59%) were collected and dried. EXAMPLE 23 CpCr(CH 3 ) 2 (pyr) Prepared as described in Example 15 above except that 1.0 equivalent of sodium cyclopentadienide was added instead of lithium pentamethylcyclopentadienide. EXAMPLE 24 SUPPORTED COMPLEXES Cp*Cr(CH 3 ) 2 (Pyr), Cp*Cr(Bzyl) 2 (Pyr), Cp*Cr(TMSM) 2 (Pyr) Cp*CrMe 2 (3,5-Lutidine), and CpCrMe 2 (Pyr) and Cp*CrMe 2 (DMAP), CpCrMe 2 (DMAP), Cp*CrMe 2 (PMe 2 Ph), CpCrMe 2 (PMe 2 Ph) according to the invention, were individually supported on dehydrated (400 °C) supports as in Example 10 to give catalysts with ca 1.0 wt % chromium. The supports used are listed in the following tables. EXAMPLE 25 The supported catalysts of Example 24 were each in turn used to polymerize ethylene by a procedure similar to that described in Example 11. The results of these polymerization runs are indicated in the following tables. All molecular weight distributions were determined using liquid size exclusion (gel permeation) chromatography. The columns were Polymer Labs Inc. PLgel 20 µm Mixed-a columns. The solvent used was 1,2,4-trichlorobenzene at a temperature of 150°C. All supports were dehydrated prior to use in order to provide increased polymerization activity. Specific dehydration temperatures and conditions are noted in the tables. ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH SUPPORTED Cp*CrMe 2 (pyr) CATALYSTS OF TABLE X Run # T m , °C MI HLMI Density g/cc Mw x10 -3 MWD 42 137.0 0 0 0.9318 1026 2.52 43 138.8 0 0 0.9318 879 2.90 44 139.6 0 0 0.9284 886 2.13 45 139.3 0 0 0.9297 962 2.38 46 136.1 -- -- 0.9306 844 2.33 47 137.0 0 0 0.9297 840 2.73 48 -- 0 3.46 -- 360 6.01 49 -- 0 14.08 -- 274 5.33 50 -- 1.61 High -- 129 7.44 51 -- 0 7.84 0.9552 267 10.76 52 135.9 -- -- -- 676 2.77 53 135.8 -- -- 0.9307 796 2.61 54 137.1 0 0 0.9492 956 4.24 55 136.4 0 0 0.9387 606 39.9 56 136.5 -- -- 0.9362 615 7.20 57 139.6 -- -- 0.9423 722 5.59 58 137.3 -- -- 0.9397 794 3.98 59 136.7 -- -- 0.9398 810 4.24 60 136.9 -- -- 0.9414 830 7.51 ANALYTICAL DATA FOR POLYETHYLENES PREPARED WITH SUPPORTED CATALYSTS OF TABLE XII. Run Tm, °C MI HLMI Density g/cc Mw c x10 -3 MWD 61 139.6 0 0 0.9281 1,013 2.80 63 141.4 -- -- 0.9280 1,414 1.72 64 137.6 0 0 0.9288 1,017 2.90 66 136.8 -- -- 0.9288 921 2.15 67 136.7 -- -- 0.9302 801 2.11 68 135.6 -- -- 0.9290 847 3.04 69 137.2 -- -- -- 850 3.20 70 137.6 -- -- -- 934 3.14 71 135.5 -- -- 0.9315 956 3.76 72 135.8 -- -- 0.9301 882 2.83 73 137.5 -- -- 0.9309 1,002 2.73 74 134.7 -- -- -- 983 3.41 75 137.2 0 0 0.9294 740 2.82

Claims: A catalyst system for the homopolymerization and copolymerization of alpha-olefins having 2-8 carbon atoms, said catalyst system comprising a cyclopentadienyl chromium hydrocarbyl compound selected from: (C 5 (R') 5 ) a CrX b (L) or [(C 5 (R') 5 ) a CrX b (L) m ] + [A] - wherein (C 5 (R') 5 ) is a cyclopentadienyl or substituted cyclopentadienyl ring; R' is at each independent occurrence hydrogen, a hydrocarbyl radical having 1-20 carbon atoms, or adjacent R' groups may together form one or more rings; X is a hydrocarbyl radical having 1-20 carbon atoms, L is N,N-dimethylaminopyridine or dimethylphenylphosphine; a = 1 or 2, b = 1 or 2 where a+b = 3; m = 1 to 2 inclusive; and A is an anion, in which the chromium in the cyclopentadienyl chromium hydrocarbyl compound has an oxidation state of +3, said compound being supported on an inorganic support, which is an inorganic metal oxide support, an inorganic metal phosphate support or a silica support, said catalyst system having additionally a co-catalyst which is a group 2 or 3 metal alkyl compound. The catalyst system of claims 1, wherein the hydrocarbyl is sigma bonded to the cyclopentadienyl hydrocarbyl chromium compound. The catalyst system of Claim 2 wherein the cyclopentadienyl chromium hydrocarbyl compound is selected from chromium compounds of the formula: Cp*Cr(CH 3 ) 2 (DMAP) Cp*Cr(CH 3 ) 2 (PMe 2 Ph) CpCr(CH 3 ) 2 (PMe 2 Ph) CpCr(CH 3 ) 2 (DMAP) where Cp* is pentamethylcyclopentadienyl, DMAP is N,N-dimethylaminopyridine, PMe 2 Ph is dimethylphenylphosphine, and Cp is unsubstituted cyclopentadienyl. The catalyst system of Claim 1, wherein the support is selected from the group consisting of alumina, silica, silica-alumina, aluminum phosphate, zirconium phosphate, and alumina aluminum phosphate. The catalyst system of Claim 1, wherein the support is selected from silica, aluminum phosphate and alumina aluminum phosphate. The catalyst system of Claim 1, wherein the support is alumina aluminum phosphate. The catalyst system of Claim 1, wherein the Group 2 or Group 3 metal alkyl compound is an alkylaluminum compound. The catalyst system of Claim 7, wherein the alkylaluminum compound is selected from the group consisting of trialkylaluminum compounds, alkylaluminum alkoxides, alkylaluminum halides and aluminoxanes. The catalyst system of Claim 8, wherein the alkylaluminum compound is an aluminoxane or trialkylaluminum compound. The catalyst system of Claim 1, wherein the Group VIB metal compound is selected from chromium compounds of the formula: Cp*Cr(CH 3 ) 2 (DMAP) Cp*Cr(CH 3 ) 2 (PMe 2 Ph) CpCr(CH 3 ) 2 (PMe 2 Ph) CpCr(CH 3 ) 2 (DMAP) where Cp* is pentamethylcyclopentadienyl, DMAP is N,N-dimethylaminopyridine, PMe 2 Ph is dimethylphenylphosphine, and Cp is unsubstituted cyclopentadienyl, the support is selected from the group consisting of alumina, silica, silica-alumina, aluminum phosphate, zirconium phosphate, and alumina aluminum phosphate, and the Group 2 or 3 metal alkyl compound is an alkylaluminum compound. The catalyst system of Claim 10, wherein the support is selected from silica or alumina aluminium phosphate, and, the alkylaluminium compound is an aluminoxane or a trialkylaluminium compound. The catalyst system of Claim 11, wherein the support is alumina aluminium phosphate. A process for the homopolymerization or copolymerization of alpha-olefins comprising polymerizing said alpha-olefin, or copolymerizing two or more alpha-olefins in the presence of a catalyst system as claimed in any preceding claim. The process of Claim 13, wherein the alpha-olefins have 2-8 carbon atoms.

Inventors: BEACH DAVID L, CARNEY MICHAEL J, BEACH, DAVID L., CARNEY, MICHAEL J.
Applicants: CHEVRON USA INC, CHEVRON U.S.A. INC.
Application year: 1993
Main classification: C08F10
IPC codes: C08F10, C08F4, C08F110