Corrosion inhibition with Cu-BTA

Abstract: A corrosion protecting film layer is formed on a non-passivating non-noble metal, such as cobalt, by placing the metal in a dilutesolution of Cu⁺² ions and benzotriazole (1 H-BTA). Exposure of the metal to a solution containing Cu⁺² and 1 H-BTA results in a spontaneous interaction of Cu⁺² and the metal to produce a film layer of Cu(I)BTA on the metal surface to create a permanent corrosion protection for the metal. A borate buffer, such as boric acid and a borate, can be added to the solution to adjust the pH of the solution to be in the range between 8 and 9.

Description: The present invention relates to corrosion inhibition and particularly to the formation of a thin film of Cu(I)-BTA for inhibiting corrosion of non-passivating, non-noble metals. Corrosion is a spontaneous process and a ubiquitous problem for all but a few noble metals. Cobalt is particularly susceptible to corrosion. While cobalt forms a marginally protective passive layer in alkaline solutions, nevertheless corrosion occurs at a rate of 0.2 µm/day in DI water with no evidence of passivation. Moreover, cobalt is a non-noble metal and is thus very susceptible to galvanic attack when in contact with other, more noble, metals. Cobalt and its alloys are widely used in magnetic applications due to its exceptional magnetic properties. For example, thin film magnetic disks and thin film inductive magnetic recording heads may be fabricated from cobalt alloys. These products are particularly intolerant of any corrosion loss, both in fabrication and in use. While there are various known passivation techniques, few are effective at reducing the corrosion rate of cobalt by significant amounts. An important consideration is that any protection technique have no adverse effect upon the magnetic properties of the material. For example, alloying the non-noble metal with an element such as chromium, thermal oxidation methods or the application of conversion layers are all possible methods of passivating non-noble metals. However, each of these methods has undesirable limitations. It is also possible to control unwanted metallic dissolution in fabrication steps where cobalt or its alloys are in contact with process solutions by the use of corrosion inhibitors. However, many corrosion inhibitors offer only a limited protection of a cobalt workpiece in situ, and even less protection after the workpiece is removed from the environment containing the corrosion inhibitor. Copper, for example, is a more noble metal than cobalt but has an oxide that is an equally marginal surface passivator. Copper is a viable engineering material, largely as a result of the very effective corrosion inhibiting effect provided by benzotriazole (1 H-BTA) and its derivatives. The 1 H-BTA compound reacts with a metallic Cu surface to form a Cu-BTA film. Depending upon the details of the preparation, the film can be as thin as 2nm thick. Even such a thin film provides effective corrosion inhibiting effect. Once formed, the thin film reduces the corrosion rate of copper in water (with or without the addition of a corrosion inhibitor) by more than two orders of magnitude. In M. Bakszt, "Providing Solderability Retention by Means of Chemical Inhibitors", Metal Finishing, vol. 83, no. 1, p. 35 (1989) there is disclosed an aqueous solution comprising 0.003 g/L of benzotriazole and varying amounts of copper in the form of copper sulfate. This solution is used as an organic coating on base copper boards to achieve good solderability protection. There is no comparably effective inhibitor known in the art for use with cobalt workpieces. In aqueous solutions, benzotriazole chemisorbs on the surface of the cobalt and reduces the corrosion rate by only one order of magnitude. However, when the cobalt workpiece is then placed in a solution devoid of 1 H-BTA, the corrosion rate is reduced to only 3 to 5 times less than that of a cobalt workpiece not previously exposed to 1 H-BTA. In order to overcome these limitations and provide a much improved corrosion inhibiting effect, a thin film containing Cu-BTA is formed on the cobalt containing workpiece. While the protection afforded by a thin film layer of Cu-BTA on a copper containing workpiece is well known to those skilled in the art, the present invention concerns the formation of such a Cu(I)-BTA film on a non-copper containing, non-passivating, non-noble workpiece by the utilization of a treatment bath containing cupric ions and benzotriazole. The symbol Cu(I) indicates that the copper combining with the benzotriazole is in the +1 oxidation state. In accordance with the teachings of the present invention, the protective film is formed by exposing the cobalt workpiece to a solution containing CUSO₄5H₂O and benzotriazole (1 H-BTA). As a result of spontaneous interaction of the Cu²⁺ and Co, Cu(I)BTA is formed at the Co surface to form a permanent corrosion protection for the cobalt. In an alternative method, a borate buffer, that is a solution of boric acid with a borate, such as sodium borate, is added to the Cu²⁺ ions and 1 H-BTA aqueous solution to adjust the pH to be in the range between 8 and 9. The addition of the borate buffer to a BTA + Cu²⁺ + H₂O solution results in a reduction of the corrosion rate of the workpiece during treatment in the cupric ion and 1 H-BTA solution while a Cu(I)-BTA protective film is being formed on the workpiece surface. The present invention provides for the formation of a corrosion inhibiting film layer on non-passivating, non-noble metals by a simple chemical treatment. The protective film layers includes a Cu(I)-BTA complex. A principal object of the present invention is, therefore, the provision of a method for forming a corrosion inhibiting layer on non-passivating non-noble metals by a simple chemical treatment. Another object of the invention is the provision of a method for forming a corrosion inhibiting film layer on a non-passivating, non-noble metal where the film layer includes Cu(I)-BTA. A further object of the invention is the provision of a solution for depositing a corrosion inhibiting film on a non-passivating, non-noble metal where the bath contains CUSO₄5H₂O, 1 H-BTA and a borate buffer for controlling the pH of the bath. A still further object of the invention is the provision of non-passivating non-noble metal workpiece coated with a thin film corrosion inhibiting layer containing Cu(I)-BTA. Further and still other objects of the present invention will become more clearly apparent when reading the following description. The present invention concerns the use of a two, and preferably three component system. Specifically, a dilute solution of CUSO₄5H₂O and benzotriazole (1 H-BTA), and preferably including a borate buffer, is used to generate a protective film on metals such as cobalt or iron which are normally marginally protected by 1 H-BTA alone. By exposing the metal, such as cobalt, to a solution containing CUSO₄5 H2 O and 1 H-BTA, a spontaneous interaction of Cu²⁺ and the metal produces a film of Cu(I)BTA at the metal surface to form a permanent corrosion protection for the metal. The following example describes a bath solution for providing a corrosion inhibiting film layer on a cobalt or cobalt alloy workpiece, where the film layer comprises Cu(I)-BTA. The cobalt or cobalt alloy workpiece is exposed to an aqueous solution (of distilled or de-ionized water) containing 0.01M 1 H-BTA and low concentrations of cupric ions. The solution contained a range of 1 x 10⁻⁵ M to 6 x 10⁻⁵ M CUSO₄5H₂O. The open circuit potential of Co in water is normally approximately 400 mV below the reversible potential for Cu oxidation. Thus, cupric ions will tend to undergo reduction on a Co surface. The rate of reduction will be diffusion limited for a dilute solution. The first step of Cu⁺⁺ reduction in a non-complexing solution is the formation of Cu⁺. The second step would be the formation of metallic Cu from Cu⁺. This is one mechanism for the electrodeposition of Cu. In the present invention, the second step is prevented by the presence of BTA⁻ in the solution and therefore at the Co surface. The BTA quickly reacts with the Cu⁺ ions to form a thin film layer of Cu(I)-BTA on the workpiece surface. It is important to keep the concentration of the Cu ions low so that the rate of cupric ion reduction stays well below the rate of oxygen reduction which controls the dissolution of Co. The Cu(I)-BTA film thickness, as evaluated by in-situ ellipsometry, depends upon the CUSO₄ concentration, the pH of the solution, the stirring rate and immersion time. For example, in a solution of water with benzotriazole and 6 x 10⁻⁵ M CuSO₄, stirred by O₂ bubbling, the film thickness grows at a parabolic rate, reaching a thickness of approximately 12 nm in 10 minutes. Electrochemical data show that the film formed in the described manner is protective of a cobalt workpiece, both in the solution containing benzotriazole and during subsequent exposure to a solution devoid of benzotriazole. The corrosion rate in water is reduced to 4% of the original value as shown in the following Table I. Corrosion Potential and Rate Measured in a Droplet of Triple Distilled Water Workpiece Corrosion Potential V,MSE Corrosion Rate A/cm² Co -0.66 1 x 10⁻⁶ Co w/Cu(I)-BTA film -0.82 4 x 10⁻⁸ The fact that the corrosion potential of a cobalt workpiece with a Cu(I)-BTA film layer is lower than the corrosion potential measured on a Co sample without the film layer indicates that the film layer is free of metallic Cu and that it is a stronger barrier for oxygen reduction than normally provided by native oxide. In a modification of the above described system, the corrosion rate of cobalt during the treatment is even more greatly reduced if a borate buffer, such as boric acid and a borate such as sodium borate, is added to the treatment solution to adjust the pH to be in the range between 8 and 9. Treatment of a cobalt workpiece in an aqueous solution of 1 H-BTA and a borate buffer does not provide corrosion protection when the workpiece is removed from the solution. Treatment of a cobalt workpiece in an aqueous solution of CUSO₄ + 1 H-BTA provides lasting protection, but the corrosion rate of the workpiece during treatment may be excessively high for certain applications, such as the treatment of small magnetic devices. Treatment of a cobalt workpiece in an aqueous solution of CUSO₄ + 1 H-BTA + a boric buffer results in the formation of a lasting protective film layer and a corrosion rate of the workpiece during treatment which is very low. In an experiment 0.09M boric acid and 0.005M sodium borate was added to an aqueous solution of Cu²⁺ + 1 H-BTA resulting in a solution having a pH of 8.2. In alkaline solutions such as boric acid/borate buffer and pH of 8.2 or in dilute ammonia and pH in the range of 8.8 to 9, 1 H-BTA alone behaves as an effective corrosion inhibitor for cobalt. Boric acid/borate solution alone does not show a measurable corrosion inhibition of cobalt. However, in the presence of 1 H-BTA, the boric acid/borate buffer appeared to aid in the corrosion inhibition process. Measurements performed using a cobalt workpiece in a 10⁻⁵ M CUSO₄ in water with benzotriazole both indicated a reduced Co corrosion rate by a factor of 2X in one minute which increased to a factor of 10X in five minutes. However, in a bath containing 10⁻⁵ M CUSO₄ and 10⁻² M BTA from an alkaline solution with boric acid/borate resulted in a practically instantaneous reduction of Co dissolution by a factor of about 100X. The newly formed protective film layer, CuBTA, was very thin, reaching a thickness of 3.2nm in 10 minutes. Once formed, the film layer provides a better permanent protection than that observed with benzotriazole treatment alone. A solution with CUSO₄ and 1 H-BTA in a borate buffer consumes very small amounts of Co and therefore higher concentrations of CUSO₄, such as 10⁻³ M, can be used to produce thicker CuBTA film layers of up to 10nm and yield even higher factors of permanent corrosion protection of up to two orders of magnitude. While the above description refers primarily to cobalt and cobalt alloy workpieces, the invention is also applicable to use with other metals and alloys which have a lower open circuit potential than copper. Such metals include, but are not limited to, aluminum, magnesium, iron, manganese, tungsten and zinc, and alloys thereof. Furthermore, the invention is also applicable for use with other benzotriazole derivatives, for example, 5 CH₃-BTA and 5 Cl-BTA.

Claims: An aqueous solution for forming a corrosion inhibiting film on a non-passivating, non-noble metal or alloy thereof comprising Cu²⁺ ions and benzotriazole or derivatives thereof, characterized in that said solution comprises approximately 0.01M of 1 H-BTA and CUSO₄ 5H₂O in a concentration in the range between 1 x 10⁻⁵ and 6 x 10⁻⁵ M. An aqueous solution according to claim 1 further comprising a borate buffer in sufficient quantity to adjust the pH of the solution to be in the range between 8 and 9. An aqueous solution as set forth in claim 2 wherein said borate buffer comprises boric acid and a borate, preferably sodium borate. A method of forming a corrosion inhibiting film on a non-passivating non-noble metal comprising the steps of placing the metal in a solution according to any one of the preceding claims for forming a thin film layer of Cu(I)-BTA on the metal. A method as set forth in claim 4, wherein said metal is selected from the group consisting of cobalt, aluminum, magnesium, iron, manganese, tungsten and zinc and alloys thereof, preferably cobalt and alloys thereof. A method of corrosion inhibiting an inductive magnetic recording head comprising the step of placing the head in an aqueous solution according to any one of claims 1 to 3.

Inventors: BRUSIC VLASTA A, FRANKEL GERALD SIMON, PETERSEN TINA ALEXEANDRIA, RUSH BENJAMIN MARK, SCHROTT ALEJANDRO G, BRUSIC, VLASTA A., FRANKEL, GERALD SIMON, PETERSEN, TINA ALEXEANDRIA, RUSH, BENJAMIN MARK, SCHROTT, ALEJANDRO G.
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1993
Main classification: C23F11
IPC codes: C23F11, G11B5