Silver halide photographic elements containing furan or pyrrole substituted dye compounds

Abstract: Spectral sensitizing dyes, and silver halide photographic elements incorporating them, which dyes have the formula: wherein: X1 and X2 each independently represent the atoms necessary to complete a 5- or 6-membered heterocyclic nucleus (preferably benzo-condensed), and X1 may be further substituted and X2 substituted or unsubstituted; n is a positive integer from 1 to 4, p and q each independently represents 0 or l, each L independently represents a substituted or unsubstituted methine group, R1 and R2 each independently represents substituted or unsubstituted aryl or substituted or unsubstituted alkyl, Z1 represents a substituted or unsubstituted pyrrole or furan containing group; W1 is a counterion as needed to balance the charge of the molecule.

Description: Field of the Invention This invention relates to dyes and silver halide photographic elements containing such dyes as sensitizing dyes. Background of the Invention Silver halide photography usually involves the exposure of a silver halide photographic element with light in order to form a latent image that is developed during photographic processing to form a visible image. Silver halide is intrinsically sensitive only to light in the blue region of the spectrum. In order to sensitize the silver halide to other than the blue region, sensitizing dyes are used in the silver halide emulsion. Sensitizing dyes are chromophoric compounds (usually cyanine dye compounds). Their usual function is to adsorb to the silver halide and to absorb light (usually other than blue light) and transfer that energy via an electron to the silver halide grain thus rendering the silver halide sensitive to radiation of a wavelength other than the blue intrinsic sensitivity. However, sensitizing dyes can also be used to augment the sensitivity of silver halide in the blue region of the spectrum. Generally a sensitizing dye should wash out of the film or paper during processing. Any retained dye contributes to Dmin and this is often referred to as sensitizing dye stain. Dye stain, which adversely affects the image recorded in the photographic material, has been a source of concern for many years. The problem of retained sensitizing dye stain has been aggravated by the advent of new emulsions, such as tabular grains, which have more surface area and use higher dye levels and accordingly tend to give higher levels of dye stain. Additionally, the use of high chloride emulsions makes preferable the use of sensitizing dyes having enhanced adsorption to silver halide since sensitizing dyes tend to be inherently less well adsorbed to silver chloride emulsions. This can also lead to higher levels of dye stain. Such high chloride emulsions are also often subjected to rapid processing, which can further aggravate dye stain problems. In order to reduce dye stain, stain-reducing agents, such as bis-triazine stilbene compounds, also known as optical brighteners, have been used to reduce dye stain. These compounds, however, are expensive and can be difficult to incorporate in the hydrophilic layers of photographic materials. Another method for reducing dye stain in some cases, is to incorporate certain substituents into the dye molecule to reduce dye stain. For example, dyes containing N,N'-2-hydroxy-3-sulfopropyl nitrogen substituents (J. Gotze, et al., U.S. patent number 3,424,586) are generally less retained than the corresponding dyes with 3-sulfopropyl groups. Other stain-reducing nitrogen substituents have also been disclosed such as the 2-sulfoethylcarbamoylmethyl groups disclosed in U.S. patent number 5,091,298 to Parton et al. Although the foregoing dye structure modifications can be effective at reducing dye stain they have not eliminated the problem. New substituents are always desirable which will result in dyes with low dye stain. In addition, there is an important class of green sensitizers for which it is not possible to use these types of stain-reducing nitrogen substituents. In particular, benzoxazole dyes (an example is given in Formula A below) are commonly used to afford green sensitization in many photographic products such as color negative and reversal films, and color paper. In many instances, benzoxazole dyes also produce undesirable post-process stain. However, it has not been possible to incorporate the aforementioned stain-reducing nitrogen substituents on these dyes because the benzoxazole nucleus is too reactive. For instance, attempts to place a 2-hydroxy-3-sulfopropyl substituent, a 2-sulfoethylcarbamoylmethyl or similar group on the benzoxazole nucleus result in ring-opening of the benzoxazole. Thus, alternative stain reducing substituents are especially needed for dyes containing the benzoxazole nucleus. FR-A-1 480 882 and DE-B-1 063 028 disclose photographic elements comprising a sensitizing cyanine dye. EP-A-0 451 816 discloses such elements wherein the dyes are said to provide low stain. It is thus an object of this invention to provide new dye compounds useful as sensitizing dyes for silver halide photographic elements, which dyes have relatively low dye stain. It is a further object of this invention to provide new benzoxazole sensitizers which exhibit relatively low dye stain. Summary of Invention The present invention provides silver halide sensitizing dyes, and photographic elements containing such dyes, which have the structure: wherein: the benzene rings are unsubstituted except by Z 1 and Z 2 , Z 1 represents a substituted or unsubstituted pyrrole or furan containing group; and the pyrrole or furan ring of Z 1 is directly appended to the benzene ring; R 1 and R 2 represent lower alkyl, at least one of R 1 and R 2 is substituted with an acid or acid salt group (for example, a sulfo group or -CH 2 -CO-NH-SO 2 -CH 3 ); R 9 is a lower alkyl; Z 2 is H, substituted or unsubstituted lower alkyl, substituted or unsubstituted alkenyl, halogen, or alkoxy; W3 is a counterion as needed to balance the charge of the molecule; the photographic material additionally comprising a dispersion of a water-immiscible solvent. Embodiments of the Invention In the present application, the term "aromatic" refers to aromatic rings as described in J. March, Advanced Organic Chemistry, Chapter 2 (1985, publisher John Wiley & Sons, New York, NY). Further, the term "lower alkyl" refers to an alkyl group containing from 1 to 6 carbon atoms. Z1 is a substituted or unsubstituted pyrrole or furan, the ring of which is directly appended to the benzene ring of the benzoxazole nucleus. Any substituents on Z1 should preferably maintain the relatively planar shape of the Z1-benzoxazole group. Examples of Z1 include: where R3 is hydrogen, substituted or unsubstituted alkyl (such as methyl or ethyl or 2-hydroxyethyl), or substituted or unsubstituted aryl (such as phenyl or 4-hydroxyphenyl). The above heterocyclic rings for Z1 are unsubstituted (that is, they are as shown). In another embodiment though, the above examples of Z1 may be substituted, for example with a 1 to 8 carbon alkyl (particularly methyl, ethyl, or propyl) or with a halogen (for example, F or Cl). Examples of W3 include sodium, potassium, triethylammonium. R 1 and R 2 represent lower alkyl at least one of which is substituted with an acid or acid salt group. Examples of lower alkyl include methyl, ethyl and propyl, and substituted lower alkyl groups such as a hydroxyalkyl group (for example, 2-hydroxyethyl), or a sulfoalkyl group, (for example, 4-sulfobutyl, 3-sulfopropyl). The alkyl group may be substituted by one or more of the substituents. In particular, R1 and R2 may be 2-sulfoethyl. When Z2 or any substituent other than Z1, is an aromatic substituent that is placed on sensitizing dyes, or Z2 is an unsubstituted furan or pyrrole nucleus, it is preferred that R1 and R2 both be an acid or acid salt substituted alkyl, in particular, 2-sulfoethyl. Preparation of a diazonium salt from an amino-substituted base followed by decomposition in the presence of furan results in formation of the furan-2-yl substituted base. Dyes of the present invention can be prepared from the above dye precursers according to techniques that are well-known in the art, such as described in Hamer, Cyanine Dyes and Related Compounds , 1964 (publisher John Wiley & Sons, New York, NY) and James, The Theory of the Photographic Process 4th edition, 1977 (Easkman Kodak Company, Rochester, NY). The amount of sensitizing dye that is useful in the invention is preferably in the range of 0.1 to 4.0 millimoles per mole of silver halide and more preferably from 0.2 to 2.2 millimoles per mole of silver halide. Optimum dye concentrations can be determined by methods known in the art. The silver halide used in the photographic elements of the present invention may be silver bromoiodide, silver bromide, silver chloride or silver chlorobromide. The silver halide used in the like. the photographic elements of the present invention preferably contains at least 90% silver chloride or more (for example, at least 95%, 98%, 99% or 100% silver chloride). In particular, the possibility is also contemplated that the silver chloride could be treated with a bromide solution to increase its sensitivity, although the bulk concentration of bromide in the resulting emulsion will typically be no more than about 2 to 2.5% and preferably between about 0.6 to 1.2% (the remainder being silver chloride). The foregoing % figures are mole %. The photographic elements of the present invention may particularly use the sensitizing dye with tabular grain emulsions. Tabular silver halide grains are grains having two substantially parallel crystal faces that are larger than any other surface on the grain. Tabular grain emulsions are those in which greater than 50 percent of the total projected area of the emulsion grains are accounted for by tabular grains having a thickness of less than 0.3 µm (0.5 µm for blue sensitive emulsion) and an average tabularity (T) of greater than 25 (preferably greater than 100), where the term "tabularity" is employed in its art recognized usage as T = ECD/t 2 where ECD is the average equivalent circular diameter of the tabular grains in µm and t is the average thickness in µm of the tabular grains. The grain size of the silver halide may have any distribution known to be useful in photographic compositions, and may be ether polydipersed or monodispersed. The silver halide grains to be used in the invention may be prepared according to methods known in the art, such as those described in Research Disclosure , (Kenneth Mason Publications Ltd, Emsworth, England) Item 308119, December, 1989 (hereinafter referred to as Research Disclosure I ) and James, The Theory of the Photographic Process . The photographic elements of the present invention, as is typical, provide the silver halide in the form of an emulsion. Photographic emulsions generally include a vehicle for coating the emulsion as a layer of a photographic element. The emulsion can also include any of the addenda known to be useful in photographic emulsions. The silver halide may be sensitized by dyes of the present invention by any method known in the art, such as described in Research Disclosure I . The dye may be added to an emulsion of the silver halide grains in a suitable vehicle (for example, gelatin) at any time prior to (for exmple, during or after chemical sensitization) or simultaneous with the coating of the emulsion on a photographic element. The dye/silver halide emulsion may be mixed with a dispersion of color image-forming coupler immediately before coating or in advance of coating (for example, 2 hours). Essentially any type of emulsion (for example, negative-working emulsions such as surface-sensitive emulsions of unfogged internal latent image-forming emulsions, direct-positive emulsions such as surface fogged emulsions, or others described in, for example, Research Disclosure I ) may be used. The above-described sensitizing dyes can be used alone, or may be used in combination with other sensitizing dyes, e.g. to also provide the silver halide with sensitivity to wavelengths of light outside the green region or to supersensitize the silver halide. Other addenda which may be in the emulsion and other photographic layers are well-known in the art and are disclosed in Research Disclosure I and the references cited therein. Photographic elements of the present invention may have dye-forming couplers dissolved in a water-immiscible solvent dispersed in the element (such as a color coupler solvent). The emulsion may also include brighteners, such as stilbene brighteners. Such brighteners are well-known in the art and are used to counteract dye stain, although the dyes of the present invention generally have low dye stain even if no brightener is used. The emulsion layer containing silver halide sensitized with a dye of the present invention can be coated simultaneously or sequentially with other emulsion layers, subbing layers, filter dye layers, interlayers, or overcoat layers, all of which may contain various addenda known to be included in photographic elements. Photographic elements of the present invention can be black and white but are preferably color. A color photographic element generally contains three silver emulsion layers or sets of layers (each set of layers often consisting of emulsions of the same spectral sensitivity but different speed): a blue-sensitive layer having a yellow dye-forming color coupler associated therewith; a green-sensitive layer having a magenta dye-forming color coupler associated therewith; and a red-sensitive layer having a cyan dye-forming color coupler associated therewith. Photographic elements comprising the composition of the invention can be processed in any of a number of well-known photographic processes utilizing any of a number of well-known processing compositions, described, for example, in Research Disclosure I , or in James, The Theory of the Photographic Process 4th, 1977. Such processing further includes rapid processing of the type described in, for example, U.S. Patent Number 4,892,804. The invention is further described in the following Examples. Synthesis Example 1 - Synthesis of Dye I-1. Intermediate A: 5-(pyrrol-1-yl)-2-methylbenzoxazole: 5-Amino-2-methylbenzoxazole (30.0 g, 0.203 mol) and 2,5-dimethoxytetrahydrofuran (30.0 g, 0.227 mol) were combined with 90 mL of acetic acid and the solution was heated at reflux for 1 hr. The mixture was evaporated to a red slurry and mixed with hexane to give a dark solid. The solid was dissolved in methylene chloride and extracted with basic water. The organic phase was removed, dried, and evaporated to a brown solid. Recrystallization from hexane/heptane afforded 18 g (45 % yield) of product, m.p. 115 -121 °C. Anal. Calcd for C 12 H 10 N 2 O: C, 72.72; H, 5.08; N, 14.13. Found: C, 72.51; H, 4.97; N, 14.03. Intermediate B: Anhydro-5-(pyrrol-1-yl)-2-methyl-3-(3-sulfopropyl)benzoxazolium hydroxide: 5-(Pyrrol-1-yl)-2-methylbenzoxazole (2.0 g, 0.01 mol) was combined with 1,3-propanesultone (1.81 g, 0.015 mol) and 1.5 mL of valeronitrile and heated at 138 °C for 2 hrs. The solid formed was collected and washed with acetone and dried (3.0 g, 94% yield). Anal. Calcd for C 15 H 16 N 2 SO 4 : C, 54.65; H, 5.16; N, 8.50. Found: C, 54.93; H, 4.81; N, 8.46. Preparation of Anhydro-5-chloro-9-ethyl-5'-(pyrrol-1-yl)-3,3'-di(3-sulfopropyl)oxacarbocyanine hydroxide potassium salt (Dye I-1): Anhydro-5-(pyrrol-1-yl)-2-methyl-3-(3-sulfopropyl)benzoxazolium hydroxide (3.2 g, 10 mmol) was combined with anhydro-5-chloro-2-(2-ethoxybutenyl)-3-(3-sulfopropyl)benzoxazolium hydroxide (3.8 g, 10 mmol), 10 mL of m -cresol and triethylamine (5 mL) and heated at 95 °C for 30 min. The mixture was removed from the heat, chilled in an ice-bath, and diluted with ether. The orange oil that formed was dissolved in 400 mL of methanol and potassium acetate (5.0 g) was added. The product precipitated and was collected. The dye was purified by recrystallization from pyridine / water and then recrystallization from propionic acid, followed by recrystallization from acetic acid. This afforded 300 mg (4% yield) of dye; λ-max = 501 nm (MeOH), ε-Max = 14.3 x 10 4 . Anal Calcd for: C 29 H 29 ClN 3 O 8 S 2 K-2.0 H 2 O: C, 48.18; H, 4.57; N, 5.82. Found: C, 48.36; H, 4.14; N, 5.83. Synthesis Example 2 - Synthesis of Dye I-5 Intermediate C: 5-(Furan-2-yl)-2-methylbenzoxazole: 5-Amino-2-methylbenzoxazole (7.0 g, 0.05 mole), isopentyl nitrite (20 mL), and furan (230 mL) were combined and heated with stirring at 30 o C in a round-bottom flask equipped with a condenser. After heating for 48 hrs, the reaction mixture was removed from the heat, washed with water, and then evaporated to an oil. Distillation afforded the product ( 4.0 g, 43% yield), bp 130 -140 o C (0.6 mm). Recrystallization from ispropyl alchohol (14 mL) afforded 3.0 g of product (32% yield) mp 60 °C. Intermediate D: Anhydro-5-(furan-2-yl)-2-methyl-3-(3-sulfopropyl)benzoxazolium hydroxide : 5-(Furan-2-yl)-2-methylbenzoxazole (40.0 g, 0.2 mol) was combined with 1,3-propanesulfone (25 g, 0.2 mole) and butyronitrile (100 mL) and heated at reflux for 18 hrs. The mixture was cooled to 25 o C and the product was collected and washed with butyronitrile and then ether. This afforded 55 g (86% yield) of D. Preparation of Anhydro-5-chloro-9-ethyl-5'-(furan-2-yl)-3,3'-di(3-sulfopropyl)oxacarbocyanine hydroxide potassium salt (Dye I-5) : Anhydro-5-(furan-2-yl)-2-methyl-3-(3-sulfopropyl)benzoxazolium hydroxide (3.2g, 10 mmol) was combined with anhydro-5-chloro-2-(2-ethoxybutenyl)-3-(3-sulfopropyl)benzoxazolium hydroxide (4.0 g, 11 mmol), 20 mL of acetonitrile, and triethylamine (3 mL) and heated at reflux for 3 min. The mixture was cooled and then diluted with ether to give an orange oil. The ether was decanted; the oil was dissolved in pyridine (20 mL) and potassium acetate (1.0 g) in water (5 mL) was added. After heating to reflux, the mixture was cooled to 25 o C and the solid was collected. Recrystallization from pyridine / water, followed by a second recrystallization from acetic acid afforded the product (0.45 g, 7% yield), λ-max = 503 nm (MeOH), ε-max = 15.71 x 10 4 . Anal Calcd for: C 29 H 28 ClN 2 O 9 S 2 K-2.0 H 2 O: C, 48.16; H, 4.46; N, 3.87. Found: C, 47.93; H, 3.90; N, 3.81. Photographic Evaluation Example 1 : Black and white photographic materials. Black and white photographic materials were prepared by coating a polyester support with a silver halide emulsion layer containing chemically-sensitized 0.2 µm cubic silver bromoiodide (2.6 mol % I) at 10.8 mg Ag/dm 2 , hardened gelatin at 73 mg/dm 2 , and sensitizing dye as identified in the Table III at 0.8 mmole/mole Ag. The elements were given a wedge spectral exposure and processed in RP X-OMAT (a trademark) chemistry (a developer containing hydroquinone and p-methylaminophenol as developing agents). The photographic speed of the dyes is reported (Table III) in terms of a sensitizing ratio (SR), which is defined as the speed at λ-max (in log E units multiplied by 100) minus the intrinsic speed of the dyed emulsion at 400 nm (in log E units multiplied by 100) plus 200. This measurement of speed allows for comparison while using a uniform chemical sensitization that is not optimized for each sensitizing dye. Black and white stain was measured by processing unexposed film and placing the processed film in front of a scanning spectrophotometer. The total transmission was measured between 400 and 900 nm. This data was plotted as absorbance (-log 1/T). The stain was calculated as the maximum absorbance at any wavelength in the range 400 - 900 nm (Table IV). Photographic Evaluation Example 2 : Color photographic materials. Color photographic materials were prepared by coating a polyester support with a silver halide emulsion layer containing chemically-sensitized 0.7 µm (equivalent circular diameter) polymorphic silver bromoiodide (6 mole % I) at 16 mg Ag/dm 2 , hardened gelatin at 63 mg/dm 2 , 4-hydroxy-6-methyl-1,3,3a,7-tetraazaindene antifoggant at 5 mg/dm 2 , N-[4-[2,4-bis (1,1-dimethylpropyl)phenoxy]butyl]-1-hydroxy-2-naphthalenecarboxamide coupler at 14 mg/dm 2 , di-n-butylphthalate (8 mg/dm 2 ) and sensitizing dye as identified in Table III at 0.4 mmole/mole Ag. The elements were given a wedge spectral exposure and coatings were processed in Kodak C-41 processing. The photographic speed of the dyes is reported in terms of a sensitizing ratio (SR) and λmax was determined from absorptance measurements. Color stain was obtained by processing unexposed color coatings for 3.5 minutes at 33 °C in the processing solution described below, followed by 1.5 minutes in a bleach-fix solution, and then a 3.5 minute wash. Stain was measured by placing the processed film in front of a scanning spectrophotometer. The stain was calculated as the maximum absorbance at any wavelength in the range 400 - 900 nm (Table IV). Processing Solution Benzyl alcohol 14.2 mL Potassium carbonate 28 g 45% Potassium sulfite 2.75 mL Triethanolamine 11 mL Hydroxylamine sulfate 3.2 g Potassium bromide 0.58 g Potassium chloride 0.13 Lithium chloride 0.13 Anticalcium agent 0.8 mL Water to make 1.0 L pH adjusted to 10.08 All the dyes effectively sensitized the silver halide emulsions in which they were used. Comparison dyes are shown below. Dye Speed in the B&W and Color Formats. Dye B&W Format Color Format lmax SR lmax SR C-1 547 250 540 225 C-4 550 226 I-1 550 255 550 238 I-5 554 257 560 225 C-2 538 235 543 208 I-2 541 250 540 224 I-7 546 248 550 221 C-3 545 245 C-5 559 253 560 240 Dye Stain in the B&W and Color Formats Dye B&W Format Dye Color Format lmax Stain OD 10 3 lmax Stain OD 10 3 C-1 508 47 C-1 510 42 I-1 510 36 C-4 512 38 I-5 510 39 I-1 510 22 I-6 510 36 I-5 512 35 560 19 I-2 505 30 I-7 510 36 C-2 515 34 I-4 518 38 I-2 510 13 I-7 510 15 C-3 515 56 C-3 512 46 545 73 550 105 C-5 520 49 C-5 550 >100 560 88 Photographic Evaluation Example 3: High silver chloride, color paper materials. The dyes (Table V) were coated at a level of 4.75 x 10 -4 moles / Ag mole on an aurous sulfide sensitized 0.31 µm silver chloride emulsion having the following coverages: silver (280 mg/m 2 ), gelatin (829 mg/m 2 ), 1-(3-acetamidophenyl)-5-mercaptotetrazole (380 mg/ mole Ag), potassium bromide (700 mg/mole Ag), potassium chloride (7.9 g/mole Ag). The magenta coupler dispersion contained 1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-(a-(4-hydroxy -3- tert -butylphenoxy)tetradecanoamide)anilino)-5-pyrazolone coupler (423 mg/m 2 ), di-n-butyl phthalate (220 mg/m 2 ) and gelatin (829 mg/m 2 ). The coupler dispersion was added to the dye/silver chloride emulsion immediately before coating. The elements also included a gelatin overcoat layer (1.08 g/m2) and a gelatin undercoat layer (3.23 g/m2). The layers were hardened with bis(vinylsulfonyl)methyl ether at 1.7% of the total gelatin weight. To evaluate photographic sensitivity, the elements were exposed to a light source designed to simulate a color negative print exposure. The elements were then processed through a Colenta processor. This consists of a color development (45 sec, 35 °C), bleach-fix (45 sec, 35 °C) and stabilization or water wash (90 sec, 35 °C) followed by drying (60 sec, 60 °C). Processing solutions are described below. The speeds at 1.0 density units above Dmin are listed in Table V. Color Developer Lithium salt of sulfonated polystyrene (30% by weight) 0.25 mL Triethanolamine 11.0 mL N,N-diethylhydroxylamine (85% by wt) 6.0 mL Potassium sulfite (45% by wt) 0.5 mL Color developing agent 4 (N-ethyl,N-2-methanesulfonylaminoethyl)-2-methyl phenylenediaminesesquisulfate monhydrate 5.0 g Kodak Ektaprint 2 Stain Reducing Agent (a stilbene material commercially available from Eastman Kodak Co. 2.3 g Lithium sulfate 2.7 g Potassium chloride 2.5 g Potassium bromide 0.025 g Kodak Anti Cal No (an organic phosphorous acid material commercially available from Eastman Kodak Co.) 0.8 mL Potassium carbonate 25.0 g Water to total 1 liter, pH adjust to 10.12 Bleach-fix Ammonium thiosulfate 58.0 g Sodium sulfite 8.7 g Ethylenediaminetetraacetic acid ferric ammonium salt 40.0 g Acetic acid 9.0 mL Water to total 1 Liter, pH adjusted to 6.2 Stabilizer Sodium citrate 1.0 g Dearside (a biocide produced by Rohm and Haas) 45.0 ppm Water to total 1 liter, pH adjusted to 7.2 For retained dye stain evaluation, identical but unexposed elements prepared as described above were subjected to the processing described below at 35°C. Optical density in the range 400 - 700 nm of the processed coatings was measured by reflectance spectroscopy. Process: 40 sec in developer 5 sec drain 45 sec Kodak Ektaprint2 ® blix 3 min wash dry Developer composition: p-Phenylenediamine developing agent 5.0 g Sulfonated polystyrene 0.25 mL Triethanolamine 11.0 mL Diethylhydroxylamine (85%) 6.0 mL Lithium sulfate 2.7 g Anti-calcium agent 0.8 mL Potassium chloride 1.6 g Potassium bromide 10.0 mg Potassium carbonate 25.0 g Water to make 1.0 L Adjust pH to 10.0 Dye Speed and Stain in the Silver Chloride Paper Format Stain Dye λ max Speed λ max OD x10 3 I-1 550 173 516 04 I-2 541 166 --- 0 I-5 549 191 512 10 I-6 544 181 --- 0 C-1 550 185 509 28 The data presented in Tables III - V indicate that the dyes used according to the invention provided effective sensitization and gave significantly lower post-processing stain than the comparison dyes, particularly in the color format.

Claims: A silver halide photographic element comprising an emulsion of light sensitive silver halide containing a cyanine sensitizing dye characterized in that the dye has the formula: wherein: the benzene rings are unsubstituted except by Z 1 and Z 2 ; Z 1 represents a substituted or unsubstituted pyrrole or furan containing group and the pyrrole or furan ring of Z 1 is directly appended to the benzene ring; R 1 and R 2 represent lower alkyl at least one of which is substituted with an acid or acid salt group; R 9 is a lower alkyl; Z 2 is H, substituted or unsubstituted lower alkyl, substituted or unsubstituted alkenyl, halogen, or alkoxy; W3 is a counterion as needed to balance the charge of the molecule; the photographic element additionally comprising a dispersion of a water-immiscible solvent. A silver halide photographic element according to claim 1, wherein Z 1 is any one of: where R 3 is hydrogen, substituted or unsubstituted alkyl, or substituted or unsubstituted aryl. A silver halide photographic element according to claim 1 or 2, wherein the silver halide emulsion is a tabular grain emulsion wherein at least 50% of the grain population is accounted for by tabular grains that have a thickness of less than 0.5µm and which satisfy the formula ECD/t 2 > 25, wherein ECD represents the average equivalent circular diameter of the tabular grains in micrometers, and t represents the average thickness of the grains in micrometers. A silver halide photographic element according to any preceding claim additionally comprising a water-immiscible dispersion carrying a color coupler. A silver halide photographic element according to any preceding claim, wherein the silver halide emulsion comprises at least 95 mole percent silver chloride. A silver halide photographic element according to any preceding claim, wherein one of R 1 and R 2 is substituted with an acid or acid salt group. A silver halide photographic element according to any preceding claim, wherein any substituents on the dye, other than Z 1 are nonaromatic.

Inventors: FERGUSON PAMELA MCCUE, LINK STEVEN GEORGE, PARTON RICHARD LEE, STEGMAN DAVID ALAN, FERGUSON, PAMELA MCCUE, LINK, STEVEN GEORGE, PARTON, RICHARD LEE, STEGMAN, DAVID ALAN, FERGUSON, PAMELA MCCUE, C/O EASTMAN KODAK CO., LINK, STEVEN GEORGE, C/O EASTMAN KODAK CO., PARTON, RICHARD LEE, C/O EASTMAN KODAK CO., STEGMAN, DAVID ALAN, C/O EASTMAN KODAK CO.
Applicants: EASTMAN KODAK CO, EASTMAN KODAK COMPANY
Application year: 1993
Main classification: G03C1
IPC codes: G03C1, C09B23