Process for the production of an alkali-metal citrate

Abstract: A process for obtaining an alkali metal citrate from an aqueous solution eg., a fermentation broth, comprises adjusting the pH to more than 5.4, preferably to about 8.5, contacting the solution with a polymeric adsorbent eg. a weakly basic anion exchange resin, eluting the charged adsorbent with a solution of an alkali metal hydroxide or salt and recovering the aqueous solution of the alkali metal citrate.

Description: The present invention relates to a process for the production of an alkali-metal citrate, particularly to the production of an alkali-metal citrate from an aqueous solution, such as a broth containing citric acid obtained by a fermentation process. Citric acid is produced commercially by the fermentation of a suitable carbohydrate feedstock such as dextrose by a citric acid forming microorganism. The crude product of the fermentation process is an aqueous solution of citric acid together with other organic acids, residual carbohydrate, proteins, amino acids and a range of inorganic salts including cations such as potassium, sodium, calcium, magnesium and iron and anions such as sulphate, chloride, phosphate and nitrate. Various methods have been proposed for the recovery of pure citric acid from a fermentation broth including precipitation as the calcium salt or adsorption on a suitable adsorbent. Adsorption methods of separation have received considerable attention in recent years and it is to this type of separation that the present invention relates. A typical method of adsorption separation is described in EP 324 210 A in which an aqueous fermentation product is contacted with a polymeric adsorbent which may be a neutral, cross-linked polystyrene polymer, a nonionic hydrophobic polyacrylic ester polymer, a weakly basic anion exchange resin possessing tertiary amine or pyridine functional groups, or a strongly basic anion exchange resin possessing quaternary amine functional groups. The citric acid is adsorbed on the polymeric adsorbent and is then subsequently desorbed. One strong preference expressed in EP 324 210 A is to conduct the adsorption process at a pH of the aqueous fermentation product which is less than the first ionisation constant of citric acid ie at a pH effectively less than 3.13. At a pH below this figure all the citric acid will be unionised and will be adsorbed as citric acid and not as a citric acid salt. Above pH 3.13 increasing amounts of citric acid salts will be present giving rise to an increased overall process tune because of the longer time required to desorb a mixture of citric acid and citrates rather than citric acid alone. An alternative adsorption process for recovering citric acid from a fermentation broth is described in Japanese Patent Publication No. 58-164541. In this process the citric acid is separated as its alkali metal salt eg. as tri-sodium citrate by adsorption on an anion exchange resin of the salt type followed by desorption by means of a mineral acid solution. Example 2 of the Japanese patent publication describes the separation of sodium citrate and glucose using the SO 4 -- form of an anion exchange resin and eluting with 1 N sulphuric acid to produce citric acid. Citric acid is well known for its applications in the food industry but increasingly it is in demand as its tri-sodium salt in the formulation of detergents where the salt acts as a builder and can thus be used to replace phosphate. Tri-sodium citrate also has some food uses, eg. as a buffering agent, and pharmaceutical applications. In this respect therefore there is an incentive to produce tri-sodium citrate directly as a marketable commodity rather than by converting pure citric acid to the sodium salt. The invention of the present application has therefore the aim of producing citrates, especially tri-sodium citrate from a fermentation broth containing citric acid without the intermediate step of isolating pure citric acid. According to the invention a process for obtaining an alkali metal citrate is characterised by, (a) adjusting the pH of an aqueous solution containing citric acid to a value greater than 5.4, (b) contacting the aqueous solution with a polymeric adsorbent, (c) eluting the charged polymeric adsorbent with an eluant comprising an aqueous solution of a soluble alkali metal hydroxide or alkali metal salt in which the alkali metal corresponds to the alkali metal of the alkali metal citrate it is the intention to produce and (d) recovering an aqueous solution of the alkali metal citrate. Preferably the alkali metal is sodium. The process of the invention is of greatest utility in enabling an alkali metal citrate to be obtained from the crude aqueous product of a process for citric acid production by fermentation. This crude aqueous product may contain residual carbohydrate feedstock such as dextrose, various salts and protein impurities as well as citric acid in various stages of ionisation depending on the pH and the temperature of the fermentation substrate. The pH of the aqueous product is first adjusted to more than 5.4, preferably to about 8.5, suitably by the addition of an alkali eg sodium hydroxide. At this pH the citric acid is in the form of mono-, di- and/or tri-alkali metal citrate(s). The polymeric adsorbent which is used in the process of the invention may be a neutral polymer but is preferably an anion exchange resin particularly a weakly basic anion exchange resin. The polymeric adsorbent is eluted with an aqueous solution of a salt which comprises an alkali metal cation corresponding to that which is to form the alkali metal citrate. The anion component of the eluant salt is less significant but, in the case where the polymeric adsorbent is an anion exchange resin, the anion will become associated with the regenerated resin after removal of the alkali metal citrate therefrom. Suitable anions are sulphate, chloride or hydroxide. The concentration of the alkali metal salt in the eluant is suitably 0.0001 to 7 molar preferably 0.01 to 5 molar. The solution eluted from the polymeric adsorbent is an aqueous solution of the tri-alkali metal citrate. The tri-alkali metal citrate may be recovered in solid form from the aqueous solution by known means eg. by crystallisation or evaporation. The adsorption/desorption stages of the process according to the invention may be carried out at temperatures in the range 20 to 100°C, preferably 20 to 40°C and at pressures from atmospheric to 20x10 5 Pas. The process according to the invention may be carried out batchwise or in a continuous or semi-continuous manner. Preferably, the process is carried out as a countercurrent moving bed or a simulated moving bed countercurrent flow system. The invention will now be further illustrated with reference to the following Example. Example The apparatus used was a double jacket chromatography column of height 100 cm and diameter 2.2 cm filled with 343 mls of an anion exchange resin, the sulphate form of AMBERLITE IRA 68 (AMBERLITE is a trade mark). A pulse test was carried out at 20°C and atmospheric pressure using a feedstock comprising 25 g tri-sodium citrate and 25 g D(+)glucose mono-hydrate in 200 mls of water. The pH of this solution was about 8.5. At a total flowrate of 0.3 BV ("bed volume") per hour, 0.02 BV of the feed mixture was injected and subsequently eluted with 3N sodium sulphate solution. During the desorption stage, fractions of 0.032 BV were collected. The eluted fractions were analysed by HPLC chromatography, the tri-sodium citrate and glucose contents being as follows:- Sample No Time (mins) Tri-sodium citrate content (mg/l) Dextrose content (mg/l) 1 95.0 0.9 2 103.0 3.7 3 111.0 7.9 4 119.0 11.9 5 127.0 15.8 6 135.0 18.2 7 143.0 17.1 8 151.0 13.7 9 159.0 9.5 10 167.0 1.1 6.5 11 175.0 1.6 3.9 12 183.0 2.2 2.3 13 191.0 3.2 1.3 14 199.0 4.2 0.7 15 207.0 5.3 0.4 16 215.0 6.4 17 223.0 6.9 18 231.0 7.8 19 239.0 7.3 20 247.0 8.1 21 255.0 7.9 22 263.0 6.9 23 271.0 6.3 24 279.0 5.5 25 287.0 4.7 26 295.0 4.1 27 303.0 3.3 28 311.0 3.1 29 319.0 2.5 30 327.0 2.1 31 335.0 1.9 32 343.0 1.6

Claims: A process for obtaining an alkali metal citrate characterised by, (a) adjusting the pH of a solution containing citric acid to a value greater than 5.4, preferably to about 8.5, (b) contacting the aqueous solution with a polymeric adsorbent, (c) eluting the charged polymeric adsorbent with an eluant comprising an aqueous solution of a soluble alkali metal hydroxide or alkali metal salt in which the alkali metal corresponds to the alkali metal of the alkali metal citrate it is intended to produce and (d) recovering an aqueous solution of the alkali metal citrate. A process according to claim 1 characterised in that the alkali metal citrate is tri-sodium citrate. A process according to claim 1 or claim 2 characterised in that the solution containing citric acid is the crude aqueous product of a process for the production of citric acid by fermentation. A process according to any one of the preceding claims characterised in that the polymeric adsorbent is an anion exchange resin, particularly a weakly basic anion exchange resin. A process according to claim 4 characterised in that the anion exchange resin is in the sulphate form. A process according to any one of the preceding claims characterised in that the eluant is an aqueous solution of sodium sulphate. A process according to any one of the preceding claims characterised in that the concentration of the alkali metal salt in the eluant is 0.0001 to 7 molar. A process according to any one of the preceding claims characterised in the adsorption/desorption stages of the process are conducted at temperatures in the range 20°C to 100°C. A process according to any one of the preceding claims characterised in that the adsorption/desorption stages of the process are conducted at pressures in the range atmospheric to 20x10 5 Pas. A process according to any one of the preceding claims characterised in that it is carried out as a countercurrent moving bed or a simulated moving bed countercurrent flow system.

Inventors: DEREZ FRANK GEORGES HENDRIK, VANDERVONDELEN PATRICK LOUIS J, DEREZ, FRANK GEORGES HENDRIK, VANDERVONDELEN, PATRICK LOUIS JEAN
Applicants: CERESTAR HOLDING BV
Application year: 1993
Main classification: C07C59
IPC codes: C07C51, C07C59