Compositions and agents for vulcanishing rubber

Abstract: A vulcanisable composition comprises sulphur-vulcanisable rubber, sulphur or a sulphur-donor, a zinc compound, and a sulphur-containing amine of the formula R¹-S n -R-NR²R³ wherein R is a divalent radical comprising a chain of at least 2 C atoms, R¹ is an organic radical, and R² and R³ are each H or an organic radical, provided that NR²R³ is not NH(C₁₋₆ alkyl), and n is an integer, or a salt thereof, provided that the amine is not 3-(methylthio)propylamine. The amine is preferably cystamine.

Description: Field of the Invention This invention relates to vulcanisable compositions and to agents for vulcanising rubber. Background of the Invention In recent years, environmental and legislative pressures have made it necessary to replace many of the active agents that have been widely used in rubber technology. One particular area of concern has been the use of compounds, usually based on secondary amines, that are extremely effective accelerators but which can react to give toxic nitrosamines. Various compounds have been proposed, to avoid this problem. For example, the use of dialkyldithiocarbamates and xanthates is described in EP-A-0184301, tetrabenzylthiuram sulphides in EP-A-0283552, EP-A-0284649 and EP-A-0284650, and the combination in EP-A-0413504. Although these compounds are effective, the degree of cure that they provide is usually lower than that provided by conventional secondary amine accelerators. One such accelerator is 2-mercaptoimidazoline (also known as ethylene thiourea) that is both nitrosatable and carcinogenic. Chem. Abs. 80 (1974) 16145p discloses that diaminodisulphides, e.g. cystamine, provide increased scorch times when used in halogen-containing polymer rubbers. The particular example of a composition of this type comprises 100 parts polyepichlorohydrin rubber, 5 parts Pb 3 O 4 , 50 parts carbon black, 1.5 parts 2-mercaptoimidazoline and 1 part 2,2'-diaminodiphenyldisulphide. Summary of the Invention It has now been found that diaminoalkyldisulphides such as cystamine, and other compounds having both an amine group and 2 to 4 sulphur atoms, are useful primary and, more especially, secondary accelerators in sulphur-vulcanisable systems. As amines, such compounds do increase the rate of cure of rubber, but the surprising discovery behind the present invention is that the cured rubber is stable, i.e. it does not suffer either reversion or post-vulcanisation once the cure has reached its plateau. According to the present invention, therefore, a vulcanising agent for a sulphur-vulcanisable rubber (i.e. not a halogen-containing polymer rubber) comprises sulphur, zinc oxide or another zinc compound, and a sulphur-containing amine of the formula R 1 -S n -R-NR 2 R 3 wherein R is a divalent radical comprising a chain of at least 2 C atoms, R 1 is an organic radical, and R 2 and R 3 are each H or an organic radical, provided that NR 2 R 3 is not NH(C 1-6 alkyl), and n is 2 to 4, or a salt thereof. Description of the Invention The sulphur-containing amine used in the present invention apparently has both stabilising/anti-oxidant properties as well as acting as an accelerator. Especially stable compounds of this type are those in which R 1 is a long-chain alkyl group, e.g. of up to 20 C atoms. Thus, for example, the amine may be 2-(decylthio)ethylamine. In order to obtain the accelerating effect associated with the amine group, it is often preferred that R 1 should include another NR 2 R 3 group. Preferred diamines of this type have the formula S n (RNR 2 R 3 ) 2 . While the amount of the amine that is used in the present invention may be 0.1 to 2, and preferably 0.2 to 1, parts by weight by 100 parts rubber, these ranges are particulary suitable for diamines; monoamines may be used in correspondingly larger amounts. The divalent group R is preferably a straight-chain alkylene radical, e.g. C 2-8 alkylene, and preferably -CH 2 CH 2 -. R may also be aromatic; compounds such as 2,2'-diaminophenyldisulphide have good anti-oxidant properties. While n may be 2 to 4, it is preferably 2. Accordingly, preferred compounds for use in the invention are diaminoalkyldisulphides, of which cystamine is the simplest example. The amines used in the invention may be secondary amines, with the given proviso. An example of a suitable secondary amine is di[2-(N-(2-benzthiazyl)amino)ethyl]-disulphide. When R 2 is H, R may be, for example, -CSSM (M = Na or ½ Zn), -SHet (Het = 2-benzthiazyl or 2-thiazolinyl), or benzyl. It is also possible to use tertiary amines, i.e. in which R 2 and R 3 are each organic radicals, e.g. C 1-8 alkyl. One such compound is tetramethylcystamine, of which a given amount may be less effective than cystamine, but which has the advantage over cystamine of being more compatible with rubber. As for cystamine, it is generally preferred that R 2 and R 3 are each H, i.e. the amine is a primary amine. Further examples of amines that can be used in the invention are 3,3'-dithiobispropylamine and also salts of the amines. Suitable salts are those formed with stearic or lauric acid or carbon dioxide. Cystamine itself is a liquid at ambient temperatures. It may be used as such, especially with latex rubber, but, for ease of handling, it may be encapsulated. Advantages associated with the use of cystamine in particular are that it gives no objectionable odours and provides few problems during mill mixing. It acts as an effective post-vulcanisation stabiliser in addition to accelerators, giving high rates and states of cure of vulcanisates, without reversion, and hence good rheological and physical properties. Further, since cystamine is a primary amine, its use does not produce stable nitrosamines. If the given amine, e.g. cystamine is used, in accordance with the invention, in order to boost the effect of a primary accelerator, that accelerator can be relatively non-toxic. In particular, primary accelerators can be used that do not react to give toxic nitrosamines. The cystamine or other sulphur-containing amine is effective in a wide range of elastomers, except chloroprene and other halogen-containing polymer rubbers. Examples of rubbers in which it can be used are natural, nitrile, butyl, Hypalon, SBR and EPDM rubbers. The rubber may be in dry or latex form. Nitrile rubbers exemplify rubbers that are generally resistant to reversion; here and in other cases, reversion resistance may not be a primary object of the present invention, but advantages are then still associated with, for example, reduced toxicity. The sulphur-containing amine functions as a secondary accelerator for a variety of primary accelerators such as dithiocarbamates, thiurams, thiazoles and sulphenamides. Thus, for example, compounds such as tetrabenzylthiuram disulphide or tetrasulphide, which have been proposed for use in low-nitrosamine curing systems but which are only moderate accelerators, can be boosted so that cures are achieved which match those obtained using accelerators based on amines which can give rise to nitrosamines and are therefore listed as dangerous. The general formulae and specific examples of other such accelerators whose performance can be boosted in accordance with the invention are given in EP-A-0184301, EP-A-0413504 and EP-A-0 588 559. As indicated above, the vulcanising agent should include a zinc compound. This may be zinc oxide or a zinc complex such as diammine-diisocyanatozinc. Alternatively, or in addition, zinc may be provided as a zinc compound that can act as a primary accelerator. In particular, zinc-containing accelerators such as the zinc salt of 2-mercaptobenzthiazole, zinc dibenzyldithiocarbamate or zinc diisononyldithiocarbamate, or an analogue thereof, may be used; another such compound is zinc dibutyldithiophosphate, although it is an advantage of the present invention that, if desired, the use of phosphorus-containing compounds can be avoided. Without wishing to be bound by theory, the present invention may depend on the interaction of the sulphur-containing amine and sulphur. A complex or reaction product of the two may be used, as may a complex of the amine and the zinc compound. Alternatively, the amine may be complexed with any other component of the composition, as in the case of a 2-mercaptobenzthiazole:cystamine complex. The sulphur may be provided as elemental sulphur or in an available form, i.e. in a sulphur donor such as a thiuram or dithiodimorpholine. The following Examples 1-5, 7, 10, 12, 14, 16, 21, 24-26, 28, 30 and 32 illustrate compositions of the invention and their use. Examples 6, 8, 9, 11, 13, 15, 17-20, 22, 23, 27, 29 and 31 are given for the purposes of comparison. In all formulations, amounts are given in parts by weight (unless otherwise specified). The vulcanisation temperature was 160°C (unless otherwise specified). The following abbreviations apply: ZBeD = zinc dibenzyldithiocarbamate ZDNC = zinc diisononyldithiocarbamate MBT = 2-mercaptobenzthiazole DPG = 1,3-diphenylguanidine P25 = dipentamethylenethiuram tetrasulphide PPD = piperidinium pentamethylene dithiocarbamate DDZ = diaminediisocyanatozinc SMR = standard Malaysian rubber SBR = styrene-butadiene rubber NR = natural rubber NR05 = 100 parts NR, 5 parts ZnO, 1 part stearic acid, 1 part antioxidant WSP, 50 parts precipitated coated calcium carbonate, 5 parts SRF black Results are expressed in terms of RH (cure rate), MH (maximum torque) and reversion. Rheometer curves give RH (%) as that part of the rheometer trace where the graph is climbing; MH indicates the maximum cure (kg.cm). Reversion (%) is calculated from (1 - MH 1 /MH 2 ) x 100, where MH 1 and MH 2 are respectively the initial and final maximum torque values. Examples 1 to 23 The formulations and results of these Examples are given in Tables 1 to 3. Table 1 (Examples 1 to 5) shows the effect of cystamine as a primary accelerator. In this case only cystamine and sulphur are used to cure rubber, to different extents depending on the level of sulphur at a constant level of cystamine. Table 1 (Examples 6 to 8) shows that cystamine needs ZnO for vulcanisation in the presence of sulphur. Although it has also been shown that stearic acid is not essential for the vulcanisation of rubber with cystamine in the presence of sulphur, Example 8 shows that cystamine does not act as a vulcanising agent, i.e. it is not capable of curing rubber in the absence of sulphur. Table 2 shows that cystamine and its carbamate act as effective secondary accelerators in combination with dithiocarbamates and thiurams. Table 3 (which repeats results for Examples 11 and 12 given in Table 2) compares the effectiveness of cystamine with other activators/boosters. Cystamine shows faster rates and high states of cure, with minimum reversion. Further comparison of Examples 11, 12 and 17 to 23 shows the superior physical and heat-ageing properties obtained with vulcanisates containing cystamine compared to those using DDZ or DPG. Example 24 The behaviour of cystamine (Example 12, see above) and N,N,N',N'-tetramethylcystamine (Example 24) as primary and secondary accelerators respectively was compared. In both cases, N,N,N',N'-tetramethylcystamine shows lower activity than cystamine. However, processing safety with N,N,N',N'-tetramethylcystamine is somewhat higher. Examples 25 and 26 Formulations of 162 parts NRO5, 0.5 part S and 0.5 part cystamine or 3-(aminopropyl)disulphide (respectively Examples 25 and 26) showed similar curing rates and states. Examples 27 and 28 Hypalon (100 parts) was formulated with 2.67 parts nickel dibutyldithiocarbamate and 2.05 parts P25 (Example 27). This conventional formulation had somewhat lower rate and state of cure than when the Hypalon was formulated with 2.67 parts nickel diisononyldithiocarbamate, 2.91 parts TBzTD, 0.5 part cystamine, 0.5 part S and 3.0 parts pentaerythritol. Examples 29 and 30 Formulations of 100 parts SBR, 50 parts carbon black, 12 parts processing oil, 5 parts ZnO, 0.4 parts S, 0.7 parts P25 and 1.0 part PPD or cystamine (respectively Examples 29 and 30) showed similar curing rates and states. The vulcanisation temperature was 120°C. The results are shown in Table 4. Examples 31 and 32 A formulation of 100 parts EPDM rubber, 1.2 parts S and 5 parts of a dithiocarbamate/thiazole/sulphenamide blend (Example 31) was compared with the same formulation additionally containing 0.5 part cystamine free base (Example 32). The formulations were cured at 180°C. The results are shown in Table 4; the formulation of Example 32 was a fast-curing, low-nitrosamine cure system, exhibiting little or no reversion. TABLE 1 Example 1 2 3 4 5 6 7 8 SMR 100 100 100 100 100 100 100 100 ZnO 5 5 5 5 5 - 5 5 Cystamine 0.5 0.5 0.5 0.5 0.5 1 1 3 S 2.5 1.2 0.83 0.43 0.21 2.5 2.5 - MBT - - - - - 1 1 - Stearic Acid - - - - - 1 1 1 RH 0.06 0.04 0.04 0.02 0.01 0.06 0.52 no cure MH 46.3 38.8 32.4 21.5 12.9 23.5 71.8 no cure TABLE 2 Example 9 10 11 12 13 12 13 14 NRO5 162 162 162 162 162 162 162 162 ZBeD 0.8 0.8 0.8 0.8 - - - - ZDNC - - - - 0.8 0.8 - - TBzTD - - - - - - 3 3 Cystamine - - - 0.5 - 0.5 - 0.5 Cystamine carbamate - 0.5 - - - - - - S 2.5 2.5 1.5 1.5 1.5 1.5 0.8 0.8 RH 0.55 0.94 0.39 0.73 0.23 0.58 0.15 0.75 MH 35.9 78.2 30.1 71.2 25.5 69.2 43.4 56.7 TABLE 3 Example 11 17 18 12 19 20 21 22 23 NRO5 162 162 162 162 162 162 162 162 162 DPG - 0.5 - - - - - - - ZBeD 0.8 0.8 0.8 0.8 0.8 0.8 0.55 0.55 - DDZ - - 0.5 - - - - 0.5 - S 1.5 1.5 1.5 1.5 1.5 1.5 2.5 2.5 2.5 PEG 4000 - - - - 0.5 - - - - Cystamine - - - 0.5 - - 0.5 - - triethanolamine - - - - - 0.5 - - - 1,6-hexanediamine - - - - - - - - 0.5 RH 0.39 0.78 0.89 0.71 0.34 0.60 0.70 0.55 0.59 MH 30.1 51.2 52.0 71.2 29.6 45.4 78.1 60.8 78.9 Reversion 11.5 24.4 17.8 0.0 12.0 37.8 3.0 14.3 13.2 TABLE 4 Example 29 30 31 32 RH 0.01 0.03 0.53 0.61 MH 45.3 53.8 33.1 42.9

Claims: A vulcanisable composition comprising sulphur-vulcanisable rubber, sulphur or a sulphur-donor, a zinc compound, and a sulphur-containing amine of the formula R 1 -S n -R-NR 2 R 3 wherein R is a divalent radical comprising a chain of at least 2 C atoms, R 1 is an organic radical, and R 2 and R 3 are each H or an organic radical, provided that NR 2 R 3 is not NH(C 1-6 alkyl), and n is 2 to 4 or a salt thereof. A composition according to claim 1, wherein R is C 2-8 alkylene, e.g. -CH 2 CH 2 -. A composition according to claim 1 or claim 2, wherein R 1 includes another NR 2 R 3 group. A composition according to claim 3, wherein the amine has the formula S n (RNR 2 R 3 ) 2 . A composition according to any preceding claim, wherein R 2 and R 3 are each H. A composition according to any preceding claim, wherein n is 2. A composition according to claim 1, wherein the amine is cystamine or a salt thereof. A composition according to any preceding claim, which additionally comprises a non-toxic primary accelerator. A composition according to any preceding claim, wherein the zinc compound is zinc oxide or a zinc dialkyldithiocarbamate. A composition according to any preceding claim, which comprises 0.1 to 2, e.g. 0.2 to 1, parts by weight of the amine per 100 parts rubber. A method for preparing vulcanised rubber, which comprises heating a composition according to any preceding claim. A vulcanising agent comprising sulphur or a sulphur-donor, a zinc compound and an amine as defined in any of claims 1 to 7. A vulcanising agent according to claim 12, which additionally comprises a non-toxic primary accelerator.

Inventors: CHAKRABORTY KHIRUD BEHARI, POYNER WILLIAM RAYMOND RAVENSW, VIRDI RANVIR SINGH, CHAKRABORTY, KHIRUD BEHARI, POYNER, WILLIAM RAYMOND, RAVENSWOOD, VIRDI, RANVIR SINGH
Applicants: ROBINSON BROS LTD, ROBINSON BROTHERS LIMITED
Application year: 1993
Main classification: C08K5
IPC codes: C08K5, C08K3, C08L21