Process for recovering oxygen from gaseous mixtures containing water or carbon dioxide which process employs ion transport membranes

Abstract: The invention is a process for recovering oxygen from an oxygen-containing gaseous mixture containing one or more components selected from water, carbon dioxide or a volatile hydrocarbon which process utilizes ion transport membranes comprising a multicomponent metallic oxide containing strontium, calcium or magnesium. The process utilizes a temperature regime which overcomes problems associated with degradation of strontium-, calcium- and magnesium-containing multicomponent oxides caused by carbon dioxide.

Description: FIELD OF THE INVENTION This invention relates to a process which utilizes membrane separation to recover substantially pure oxygen from oxygen-containing gaseous mixtures containing components such as water, carbon dioxide and volatile hydrocarbons. The process utilizes a class of ion transport membranes formed from multicomponent metallic oxides containing strontium, calcium or magnesium which are not deleteriously affected by such components. Therefore, the process eliminates the necessity to remove these components from the oxygen-containing gaseous mixture prior to conducting the membrane separation. BACKGROUND OF THE INVENTION Cryogenic distillation is currently the preferred process for producing high purity oxygen (>95% ) in large scale plants (50 - 2000 ton/day). However, contaminants in the compressed air feed, ie., water, carbon dioxide and trace hydrocarbons, must be removed before conducting the distillation process in order to prevent blocking of heat exchangers or distillation equipment and buildup of hazardous concentrations of hydrocarbons in the distillation column sump. Reversing heat exchangers are commonly employed to remove contaminants in the front end of the cryogenic plant wherein such contaminants are condensed in the exchanger passages and then removed with a waste gas stream. Alternately, adsorbent beds containing zeolites or alumina which require periodic regeneration are used to adsorb such contaminants. In addition, hydrocarbons must often be removed from the liquid oxygen sump by using an adsorbent such as silica gel. These methods lead to increased capital costs and inefficiencies in the overall separation processes. Alternate methods for recovering oxygen from an oxygen-containing gaseous mixture include vacuum swing adsorption (VSA) and pressure swing adsorption (PSA) processes which employ selective adsorption of various components instead of conventional cryogenic steps to separate the mixture. As in the case of cryogenic processes, one or more of carbon dioxide, water and hydrocarbons must be separated from the feedstock prior to running the process to avoid deleterious interaction with the adsorbents. Typical processes for removing carbon dioxide and water from oxygen-containing gaseous mixtures employ an adsorbent or desiccant and are capable of removing water vapor to very low levels, often to a dew point of less than -45.5°C (-50°F). These processes possess a drawback in that the adsorbent bed must be regenerated, usually by purging the adsorbent bed with a low pressure dry waste gas or by using some portion of the product stream if a suitable waste gas stream is not available. Consequently, these systems are operated in a cyclic manner requiring duplication of equipment, operation of automated, timed switching valves and separate heater devices. An unavoidable loss of the gaseous feed often occurs during regeneration of the adsorbent. US-A-5,108,465 discloses a process for separating oxygen from an oxygen-containing gaseous mare which comprises contacting the oxygen-containing gaseous mixture with a membrane which is impermeable to gas yet which is capable of conducting electrons and oxygen ions. The membranes are formed from a ceramic material selected from the group consisting of BaFe 0.5 Co 0.5 YO 3 ; yellow lead oxide; ThO 2 ; Sm 2 O 3 -doped ThO 2 ; MoO 3 -doped Bi 2 O 3 ; Er 2 O 3 -doped Bi 2 O 3 ; Gd 2 Zr 2 O 7 ; CaTi 1-x M x O 3-α wherein M is Fe, Co or Ni, x is 0 - 0.5 and α is 0 - 0.5; SrCeO 3 ; YBa 2 Cu 3 O 7-β wherein β is 0 - 1 and (VO) 2 P 2 O 7 . The ceramic materials disclosed in US-A-5,108,465 comprise ionically conductive materials, which are commonly used in fabricating solid oxide fuel cell components, and superconducting materials. For example, YBa 2 Cu 3 O 7-β is an ionically conductive superconducting material. However, barium-containing ceramic materials are well known to be adversely affected by the presence of carbon dioxide. For example, literature references teach that water and carbon dioxide will irreversibly degrade YBa 2 Cu 3 O 7 destroying superconductivity properties of the material upon contact with carbon dioxide at temperatures greater than about 400°C. This phenomena is discussed in numerous articles including those by E. A. Cooper et al., J. Mater. Res. 6 (1991) 1393 and Y. Gao et al., J. Mater. Res. 5 (1990) 1363. Like barium, other Group II metal oxides will react with carbon dioxide and water to form hydroxy carbonates. One of ordinary skill in the art would be lead to believe that use of membranes containing strontium, calcium or magnesium would be restricted to the separation of oxygen from oxygen-containing gaseous mixtures which are substantially free of carbon dioxide, water or hydrocarbons. Considerable effort is being expended in developing an oxygen recovery process wherein the feedstock does not have to be pretreated to remove carbon dioxide, water or volatile hydrocarbons prior to conducting the separation. Moreover, improved processes are being sought to develop Group II-containing ceramics membranes which are capable of separating oxygen from oxygen-containing gaseous mixtures containing water or carbon dioxide. SUMMARY OF THE INVENTION The present invention relates to a process for recovering oxygen from an oxygen-containing gaseous mixture containing one or more components selected from water, carbon dioxide or a volatile hydrocarbon which process utilizes ion transport membranes comprising a multicomponent metallic oxide containing strontium, calcium or magnesium, or mixtures thereof. The process provides numerous advantages over prior art process in that the oxygen-containing gaseous mixture to be separated into its respective components does not have to be pretreated to remove contaminants such as water, carbon dioxide or volatile hydrocarbons prior to effecting the separation. The instant process which employs membranes formed from strontium-, calcium- or magnesium-containing multicomponent metallic oxides utilizes a temperature regime which overcomes prior art problems associated with degradation of strontium, calcium or magnesium-containing multicomponent oxides caused by carbon dioxide at elevated temperatures above about 400°C. Unexpectedly, Applicants have discovered that oxygen permeance of ion transport membranes formed from the enumerated class of strontium-, calcium- and magnesium-containing multicomponent metallic oxides is not degraded by presence of carbon dioxide, water or volatile hydrocarbons if the process is conducted at temperatures in excess of predefined critical temperatures, typically in excess of 700°C. The instant process for recovering oxygen from an oxygen-containing gaseous mixture containing one or more components selected from water, carbon dioxide or a volatile hydrocarbon comprises (a) delivering the oxygen-containing gaseous mixture into a first gas compartment which is separated from a second gas compartment by an ion transport membrane comprising a multicomponent metallic oxide containing strontium, calcium or magnesium; (b) establishing a positive oxygen partial pressure difference between the first and second gas compartments by producing an excess oxygen partial pressure in the first gas compartment and/or by producing a reduced oxygen partial pressure in the second gas compartment; (c) contacting the oxygen-containing gaseous mixture with the ion transport membrane at a temperature greater than about 810°C to separate the compressed oxygen-containing gaseous mixture into an oxygen permeate stream and an oxygen-depleted gaseous stream; and (d) recovering an oxygen permeate stream containing more than 95 vol% O 2 . The ion transport membranes suitable for practicing the claimed process comprise a multicomponent metallic oxide formed of at least two different metals or a mixture of at least two metal oxides wherein one of the metals is strontium, calcium or magnesium. Preferred multicomponent oxides of the present invention demonstrate both electron conductivity as well as oxygen ion conductivity at elevated temperatures. Preferred multicomponent metallic oxide compositions are represented by A x A' x' A'' x'' B y B' y' B'' y'' O 3-z , where A and A'' are chosen from the group comprising Groups 1, 2 and 3 and the F block lanthanides; A' is selected from the group consisting of strontium, calcium and magnesium and B, B' and B'' are chosen from the D block transition metals according to the Periodic Table of the Elements adopted by the IUPAC wherein 0≤x''≤1, 0<x'≤1, 0≤x≤1, 0<y≤1, 0≤y'≤1, 0≤y''≤1, x+x'+x''=1 , y+y'+y''=1 and z is a number which renders the composition charge neutral. BRIEF DESCRIPTION OF THE DRAWINGS FIGURE 1 is a plot of oxygen flux versus time observed during separation of oxygen from an oxygen-containing mixture using an ion transport membrane comprising La 0.2 Sr 0.8 Co 0.8 Fe 0.2 O 2.6 at 707°C. FIGURE 2 is a plot of oxygen flux versus time observed during separation of oxygen from an oxygen-containing mixture using an ion transport membrane comprising La 0.2 Sr 0.8 Co 0.8 Fe 0.2 O 2.6 at 835°C. DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a process for recovering oxygen from an oxygen-containing gaseous mixture containing one or more components selected from water, carbon dioxide or a volatile hydrocarbon which process utilizes ion transport membranes comprising a multicomponent metallic oxide containing a Group II metallic oxide. Applicants' process for recovering oxygen from an oxygen-containing gaseous mixture does not require removing contaminants such as water, carbon dioxide or volatile hydrocarbons prior to effecting the separation processes. The instant process for recovering oxygen from an oxygen-containing gaseous mixture containing one or more components selected from water, carbon dioxide or a volatile hydrocarbon comprises: (a) delivering the oxygen-containing gaseous mixture into a first gas compartment which is separated from a second gas compartment by an ion transport membrane comprising a multicomponent metallic oxide containing stontium, calcium or magnesium; (b) establishing a positive oxygen partial pressure difference between the first and second gas compartments by producing an excess oxygen partial pressure in the first gas compartment and/or by producing a reduced oxygen partial pressure in the second gas compartment; (c) contacting the oxygen-containing gaseous mixture with the ion transport membrane at a temperature greater than about 700°C to separate the compressed oxygen-containing gaseous mixture into an oxygen permeate stream and an oxygen-depleted gaseous stream; and (d) recovering an oxygen permeate stream containing more than 95 vol% O 2 . Applicants' process which employs membranes formed from strontium-, calcium- or magnesium-containing multicomponent metallic oxides utilizes a temperature regime which overcomes prior art problems associated with degradation of Group II-containing multicomponent oxides caused by carbon dioxide and water at elevated temperatures. Unexpectedly, Applicants have discovered that oxygen permeance of ion transport membranes formed from the enumerated class multicomponent metallic oxides is not degraded by presence of carbon dioxide, water or volatile hydrocarbons in the oxygen-containing gaseous mixture to be separated if the process is conducted at a critical temperature in excess of about 700°C. The critical temperatures for strontium-, calcium-and magnesium-containing multicomponent metallic oxides is 700°C, 600°C and 500°C, respectively. Applicants' discovery that membranes comprising the enumerated multicomponent metallic oxides are not degraded by carbon dioxide when operated under the claimed temperature regime represents a significant breakthrough. For example, barium-containing ceramic materials are well known to be adversely affected by the presence of carbon dioxide and/or water. For example, literature references teach that carbon dioxide will irreversibly degrade YBa 2 Cu 3 O 7-β destroying superconductivity properties of the material upon contact with carbon dioxide at temperatures greater than about 400°C. This phenomena is discussed in numerous articles including those by E. A. Cooper et al., J. Mater. Res. 6 (1991) 1393 and Y. Gao et al., J. Mater. Res. 5 (1990) 1363. The first step of Applicants' process comprises delivering an oxygen-containing gaseous mixture into contact with an ion transport membrane formed from a multicomponent metallic oxide containing strontium, calcium or magnesium wherein the membrane separates a first gas compartment and a second gas compartment. Any conventional apparatus can be utilized to house the ion transport membranes of the present invention whereby the membrane forms a partition between the first and second gas compartments. A representative apparatus is disclosed in US-A-5,035,727, issued to Air Products and Chemicals, Allentown, PA. The ion transport membrane provides a gas-tight partition between the first and second gas compartments wherein the membrane is impervious to the components of the oxygen-containing gaseous mixture at ambient temperature. The ion transport membranes of the present invention comprise a multicomponent metallic oxide formed of at least two different metals or a mixture of at least two metal oxides wherein one of the metals is strontium, calcium or magnesium. Preferred multicomponent metallic oxides demonstrate both electron conductivity as well as oxide ion conductivity at elevated temperatures and are referred to as mixed conductors. Preferred multicomponent metallic oxides are represented by the structure A x A' x ,A'' x'' B y B' y ,B'' y'' O 3-z , where A and A'' are chosen from the group comprising Groups 1, 2 and 3 and the F block lanthanides; A' is selected from the group consisting of strontium, calcium and magnesium and B, B' and B'' are chosen from the D block transition metals according to the Periodic Table of the Elements adopted by the IUPAC wherein 0≤x''≤1, 0<x'≤1, 0≤x≤1, 0<y≤1, 0≤y'≤1, 0≤y''≤1, x+x'+x''=1 , y+y'+y''=1 and z is a number which renders the composition charge neutral. A self-supporting ion transport membrane of this invention can be prepared by compressing a sintered and ground powder of the desired multicomponent metallic oxide containing strontium, calcium or magnesium into the desired shape according to procedures known in the art. Care should be taken to ensure that the membrane is free from cracks and through-porosity which would greatly diminish or destroy the selectivity achieved by the process. The membranes can also be fabricated by slip or tape casting and injection molding processes according to procedures known in the art. In a preferred embodiment, a thin layer of the subject multicomponent metallic oxides is deposited onto a porous support. Use of a porous substrate for receiving the multicomponent metallic oxide greatly improves the mechanical stability of the resulting ion transport membrane. A wide variety of porous substrates are capable of receiving the enumerated multicomponent metallic oxides. Such porous substrates possess a network of pores such that a gas can penetrate through the substrate (i.e., through-porosity). Therefore, the term, porous substrate, does not refer to materials which merely possess surface or closed internal porosity. Suitable porous substrates include metal oxide-stabilized zirconia such as yttria-stabilized zirconia and calcium-stabilized zirconia, alumina, magnesia, silica, titania, a high temperature oxygen compatible metal alloy, and compounds and mixtures thereof. Any combination of porous substrate and the enumerated multicomponent metallic oxides can be utilized so long as their coefficients of thermal expansion are compatible and chemical reactions are minimized between the substrate and multicomponent metallic oxide at operating temperatures of the ion transport membrane. Thin layers of the desired multicomponent metallic oxide having a thickness ranging from 10 to about 0.1 micrometers in thickness can be deposited onto the enumerated porous substrate by known techniques such as chemical vapor deposition and the like. A preferred technique for manufacturing ultrathin inorganic membranes is presented in United States Patent Application Serial No. 07/816,206, filed on January 1, 1992, which is assigned to Air Products and Chemicals, Inc., Allentown, PA. Oxygen-containing gaseous mixtures containing one or more components selected from carbon dioxide, water and a volatile hydrocarbon which are capable of being separated according to the present process typically contain between about 10 vol.% to 50 vol.% oxygen. The preferred oxygen-containing gaseous mixture is atmospheric air. Representative hydrocarbons which will not adversely affect operation of this process include linear and branched alkanes, alkenes and alkynes having from 1 to about 6 carbon atoms and aromatics having from 6 to about 8 carbon atoms. Such hydrocarbons are believed to be converted to carbon dioxide and water under the process operating conditions thereby causing no adverse effect on the separation process. If the multicomponent metallic oxide demonstrates both oxygen ionic and electronic conductivities, the oxide is said to be mixed conducting. Particularly useful for practical purposes are those in which the ionic and electronic conductivities are comparable or balanced. When fabricated in the form of a thin membrane, such oxides can be used to separate oxygen from an oxygen-containing gaseous mixture such as air by maintaining an oxygen partial pressure difference between the feed and permeate sides of the ion transport membrane, i.e., the first and second gas compartments. Examples of such materials are described in US-A-4,330,633 and JP-A-61-21717. In the latter, the mixed conducting perovskite structure oxide La 1-x Sr x Co 1-y Fe y O 3-d is mentioned, where x ranges from 0.1 to 1.0 and y from 0.05 to 1.0. Oxides of this type have an oxygen ionic conductivity of approximately 10 -2 ohm -1 cm -1 and an electronic conductivity of approximately 10 2 ohm -1 cm -1 at a temperature of about 800°C. When an oxygen-containing gaseous mixture at a higher partial pressure is applied to one side (the first gas compartment) of a 1 - 5 mm thick disc of multicomponent metallic oxide, oxygen will adsorb and dissociate on the surface, become ionized and diffuse through the solid and deionize, associate and desorb as a separated oxygen gas stream at the lower oxygen partial pressure surface (the second gas compartment). The necessary circuit of electrons to supply this ionization/deionization process is maintained internally in the oxide via its electronic conductivity. This type of separation process is particularly suitable for separating oxygen from a gas stream containing a relatively high partial pressure of oxygen, i.e., greater than or equal to 0.20265 bar (0.2 atm). Multicomponent metallic oxides which demonstrate both oxygen ionic conductivity and electronic conductivity typically demonstrate an oxygen ionic conductivity ranging from 0.01 ohm -1 cm -1 to 100 ohm -1 cm -1 and an electronic conductivity ranging from about 1 ohm -1 cm -1 to 100 ohm -1 cm -1 . Some multicomponent metallic oxides are primarily or solely oxygen ionic conductors at elevated temperatures. An example is (Y 2 O 3 ) 0.1 (Zr 2 O 3 ) 0.9 which has an oxygen ionic conductivity of 10 ohm -1 cm -1 at 1000°C and an ionic transport number (the ratio of the ionic conductivity to the total conductivity) close to 1. A multicomponent oxide of this type can be used to separate oxygen in one of two ways. European Patent Application EP 0399833A1 describes a membrane formed from a composite of this oxide with a separate electronically conducting phase, such as platinum or another noble metal. The electronic conducting phase will provide the return supply of electrons through the structure allowing oxygen to be ionically conducted through the composite membrane under a partial pressure gradient driving force as described previously. Alternatively, porous electrodes can be applied to the surface of the mixed oxide ionic conductor and short circuited externally to complete the electronic circuit for an oxygen partial pressure driven process. Another method, which is particularly useful to separate oxygen from mixtures containing relatively low partial pressures of oxygen, is to apply an external electric potential between the porous electrodes connected to the surface of the oxygen ionically conducting mixed oxide. The externally applied potential supplies and removes electrons from the surface and drives the oxygen ionic current, producing a separated oxygen stream at a higher partial pressure via the Nernst effect. This method is well known and is described in US-E-28,792. Typical oxygen ion conductivities for multicomponent oxides of this type range from 0.01 ohm -1 cm -1 to 100 ohm -1 cm -1 . Another category of multicomponent metallic oxides exhibit primarily or solely electronic conductivity at elevated temperatures and their ionic transport numbers are close to zero. An example is Pr x In y O z which is described in European Patent Application EP 0,399,833 A1. Such materials may be used in a composite membrane with a separate oxygen ionic conducting phase such as a stabilized Zr 2 O 3 . A membrane constructed from a composite of this type may also be used to separate oxygen from an oxygen-containing stream such as air by applying an oxygen partial pressure gradient as the driving force. Typically, the multicomponent oxide electronic conductor is placed in intimate contact with an oxygen ionic conductor. The next steps of the process comprise establishing a positive oxygen partial pressure difference between the first and second gas compartments by producing an excess oxygen partial pressure in the first compartment and/or by producing a reduced oxygen partial pressure in the second gas compartment and contacting the oxygen-containing gaseous mixture with the ion transport membrane at a temperature greater than about 810°C to separate the compressed oxygen-containing gaseous mixture into an oxygen permeate stream and an oxygen-depleted gaseous stream. A difference in oxygen partial pressure between the first and second compartments provides the driving force for effecting the separation when the process temperature is elevated to a sufficient temperature to cause oxygen in the oxygen-containing gaseous mixture residing in the first compartment to adsorb, become ionized via the membrane and to be transported through the membrane in the ionic form. A pure oxygen product is collected in the second gas compartment wherein ionic oxygen is converted into the neutral form by the release of electrons in the second gas compartment which resides at lower oxygen partial pressures than the first gas compartment. A positive oxygen partial pressure difference between the first and second gas compartments can be created by compressing air in the first compartment to a pressure sufficient to recover the oxygen permeate stream at a pressure of greater than or equal to about one atmosphere. Typical pressures range from about 1.03 to 17.24 bar (15 psia to about 250 psia) and the optimum pressure will vary depending upon the amount of oxygen in the oxygen-containing gaseous mixture. Conventional compressors can be utilized to achieved the compression required to practice the present step of the process. Alternately, a positive oxygen partial pressure difference between the first and second gas compartments can be achieved by evacuating the second gas compartment to a pressure sufficient to recover the oxygen permeate. A migration of oxygen ions from the oxygen-rich side to the oxygen-deficient side of the membrane and a migration of electrons in the opposite direction takes place in the ion transport membrane. Thus, the membranes according to the present invention shall be referred to as ion transport membranes. Accordingly, only oxygen selectively permeates electrochemically through the ion transport membrane and oxygen gas having a high purity can be obtained in the second gas compartment which resides at a lower oxygen partial pressure than the first gas compartment. The final step of the process comprises recovering the oxygen-containing gaseous mixture by storing the substantially pure oxygen in a suitable container or transferring the same to another process. The oxygen permeate comprises more than about 95 vol% O 2 and frequently more than 99 vol.% O 2 . The following examples are provided to further illustrate Applicants' claimed process. Such examples are illustrative and are not intended to limit the scope of the appended claims. EXAMPLE 1 PREPARATION OF MULTICOMPONENT METALLIC OXIDE POWDERS CONTAINING STRONTIUM, CALCIUM AND MAGNESIUM The strontium-, calcium- and magnesium-containing multicomponent metallic oxides of the present invention can be conveniently prepared by calcining a mixture of the particular metal salts in air to produce the desired metal-containing multicomponent metallic oxide. The metal salts are hygroscopic and must be weighed in a nitrogen purged glove box. The metal salts used were the nitriates and acetates of the corresponding metals. The stoichiometry of desired final metal oxide compound was determined in order to assess the amounts of metals salts to be used. Each metal salt was individually weighed in a nitrogen purged glove box. Distilled water was then heated in a glass dish on a hot plate and the respective metal salts were added thereto. If the particular multicomponent oxide contained iron nitrate, then the iron nitrate was added last to the water solution with each metal salt being fully dissolved before adding the next salt. Additional water was added as needed. The resulting aqueous mixture of metal salts was stirred with a magnetic stir bar to mix the solution. Alter the salts were dissolved, hot plate temperature was increased until the solution boiled. Boiling was continued under agitation until the solution was nearly dry causing the metal salts to precipitate. The nearly dry solution was removed from hot plate and placed in a 120°C oven to finish drying. The dried mixed salts were removed from the drying dish and ground with a mortar and pestle until a fine powder was obtained. The resulting powder was placed in a zirconia crucible or boat and calcined by ramping at 1°C/min. to 250°C., and holding the temperature for 5 hours. The temperature was then ramped at 5°C/min to 850°C and held for 10 hours followed by cooling to ambient temperature at 5°C/min. Finally, the powders were ground in a mortar and pestle and sieved on a 400 mesh screen. EXAMPLE 2 PREPARATION OF SINTERED PELLET OF MULTICOMPONENT METALLIC OXIDE POWDERS The membranes presented in the specification were prepared in the form of disks, approximately 1.9 cm (3/4 inches) in diameter and less than 2mm thick. Pellets of the multicomponent metallic oxide powders prepared according to Example 1 were pressed with force of 89000 N (20,000 lbs) for 3 to 10 minutes. Dies used were either tool steel or graphite and had a diameter of 2.41 cm (0.95 inches). Binders were occasionally used to hold the green pellet together. Either 600 or 3400 molecular weight polyethylene glycol, in a concentration of 3 - 5 weight percent was mixed with the powder by dissolving the binder in methanol and adding the powder to the binder solution. The resulting slurry was dried in air with occasional stirring. The pressed pellets were placed on setters made of zirconia insulation, chosen for its low thermal mass and high porosity. Sintered pellets of the same composition as the green pellets were placed between the zirconia and the green pellets to prevent possible interaction between the setter and pellets to be sintered. The sintering schedule varied with the composition used and whether or not a binder was used. In the absence of a binder, the pellets were ramped at 20°C/min. to the sintering temperature, held for 5 hours and cooled at 1°C to room temperature. The preferred binder burnout and sintering schedule for La 0.2 Sr 0.8 Co 0.8 Fe 0.2 O 2.6 is summarized as follows: 1. Ramp temperature at 1°C/min. to 125°C. Hold at 125°C for 1 hour; 2. Ramp temperature at 1°C/min from 125°C to 150°C. Hold at 150°C for 1 hour; 3. Ramp temperature at 1°C/min from 150°C to 175°C. Hold at 175°C for 1 hour; 4. Ramp temperature at 1°C/min from 175°C to 200°C. Hold at 200°C for 1 hour; 5. Ramp temperature at 1°C/min from 200°C to 250°C. Hold at 250°C for 1 hour; 6. Ramp temperature at 20°C/min from 250°C to 1100°C. Hold at 1100°C for 5 hours; and 7. Cool to room temperature at rate of 1°C/min. Both calcined powder and sintered pellets were characterized by x-ray diffraction. In addition, some samples were analyzed by ICP to obtain elemental analysis and depth profiled by dynamic SIMS or sputtered XPS depth profiling EXAMPLE 3 SEPARATION OF OXYGEN FROM OXYGEN-CONTAINING GASEOUS MIXTURES USING SINTERED PELLET OF MULTICOMPONENT METALLIC OXIDE POWDERS The pellets prepared according to Example 2 were tested utilizing a conventional testing apparatus typical of those known in the art. The membrane to be tested was sealed onto the end of an alumina tube using a Pyrex brand glass O-ring. One side of the pellet was exposed to a mixture of zero grade air (21% oxygen, 79% nitrogen and <0.5 ppm each of carbon dioxide, water and methane), supplied by Air Products and Chemicals, Inc., Allentown, PA, mixed with controlled amounts of carbon dioxide and water, while the other side of the pellet was exposed to UHP helium or UHP argon. Air or nitrogen flow rates could be varied between 0 and 1000 sccm and argon and helium flow rates could be varied up to 5000 sccm. (ml/m) The oxygen content of the oxygen permeate stream exiting the apparatus was measured with a Teledyne oxygen analyzer and a portion of the oxygen permeate stream was sent to a Spectramass Dataquad mass spectrometer in order to detect and measure the presence of leaks in the membrane. The oxygen-containing gaseous mixture to be separated containing carbon dioxide and water consisted of APCI zero grade air at a flow rate of 930 sccm mixed with either 10,500 ppm CO 2 in N 2 , or 1.5% carbon dioxide in zero grade air. Humidification of the gas was accomplished by bubbling the air through water at room temperature. The measured dew point of the air was 20 - 21°C. Figure 1 illustrates the effect at 787°C of water in the air feed on the oxygen permeation rate through a disc of La 0.2 Sr 0.8 Co 0.8 Fe 0.2 O 3-x . With a dry, carbon dioxide free air feed (zero grade air) the oxygen flux remained constant within experimental error over a period of 19 hours at about 0.5 sccm. After changing to an air feed saturated with 2.5% water vapor at room temperature, the flux declined slightly to 0.48 sccm, which may be due partly to the reduction in oxygen partial pressure in the feed stream, but remained constant at this value over a further 24 hours of continuous operation. The oxygen flux returned to about 0.5 sccm when the dry zero grade air feed was restored. In a further experiment, air with 2.5% water and 430 ppm carbon dioxide was fed to the membrane which resulted in no change in the oxygen flux within experimental error over a 24 hour period. These tests demonstrate that a membrane of this composition is largely unaffected at 787°C by the presence of water and carbon dioxide in the air feed and that the resulting oxygen flux is constant over extended periods of operation. Figure 2 illustrates a similar experiment carried out at 835°C with a disc of La 0.2 Sr 0.8 Co 0.8 Fe 0.2 O 3-x . After an initial equilibration with a feed stream of dry, carbon dioxide free zero grade air, the feed was replaced with air saturated at room temperature with 2.5% water. The oxygen flux was maintained at about 0.68 sccm over a continuous 24 hour period of operation. Zero grade dry air was then fed to the membrane for a further 14 hours with no change in the oxygen flux. The feed was then replaced by dry air with 430 ppm of carbon dioxide for 10 hours and then by air containing 2.5% water and 430 ppm carbon dioxide for an additional 16 hours of continuous operation. In neither case was the oxygen flux altered and the flux remained constant within experimental error over the entire test period of 64 hours. This test demonstrates that a membrane of this composition is unaffected at 835°C by the presence of water and carbon dioxide in the air feed and that the resulting oxygen flux is constant over extended periods of time.

Claims: A process for recovering oxygen from an oxygen-containing gaseous mixture containing one or more components selected from water, carbon dioxide or a volatile hydrocarbon, the process which comprises: (a) delivering the oxygen-containing gaseous mixture into a first gas compartment which is separated from a second gas compartment by an ion transport membrane comprising a multicomponent metallic oxide containing strontium, calcium or magnesium; (b) establishing a positive oxygen partial pressure difference between the first and second gas compartments by producing an excess oxygen partial pressure in the first gas compartment and/or by producing a reduced oxygen partial pressure in the second gas compartment; (c) contacting the oxygen-containing gaseous mixture with the ion transport membrane at a temperature greater than about 700°C to separate the compressed oxygen-containing gaseous mixture into an oxygen permeate stream and an oxygen-depleted gaseous stream; and (d) recovering an oxygen permeate stream containing more than 95 vol% O 2 . The process according to Claim 1 wherein the oxygen-containing gaseous mixture is air. The process according to Claim 2 wherein the positive oxygen partial pressure difference is obtained by compressing air in the first gas compartment to a pressure sufficient to recover the oxygen permeate stream at a pressure of greater than or equal to about one atmosphere. The process according to Claim 2 wherein the positive oxygen partial pressure difference is obtained by evacuating the second gas compartment to a pressure sufficient to recover the oxygen permeate stream. The process according to Claim 3 wherein the pressure in the first gas compartment required to recover the oxygen permeate stream ranges from 1.03 to 17.24 bar (15 to 250 psia). The process according to Claim 1 where the multicomponent metallic oxide demonstrates oxygen ionic conductivity and electronic conductivity. The process according to Claim 6 wherein the multicomponent metallic oxide demonstrates an oxygen ionic conductivity ranging from 0.01 ohm -1 cm -1 to 100 ohm -1 cm -1 and an electronic conductivity ranging from about 1 ohm -1 cm -1 to 100 ohm -1 cm -1 . The process according to Claim 1 wherein the ion transport membrane comprises a multicomponent oxide electronic conductor which is placed in intimate contact with an oxygen ionic conductor. The process according to Claim 1 wherein the ion transport membrane comprises a multicomponent metallic oxide oxygen ionic conductor which is placed in intimate contact with an electronic conductor. The process according to Claim 1 where ion transport membranes comprises a multicomponent metallic oxide demonstrating oxygen ionic conductivity wherein external electrodes are attached to the multicomponent oxide and an electrical potential is applied across the electrodes. The process according to Claim 10 wherein the ion transport membrane possesses an ionic conductivity ranging from 0.01 ohm -1 cm -1 to 100 ohm -1 cm -1 . A process according to any preceding claim wherein said ion transport membrane comprises a composition represented by the structure A x A' x' A'' x'' B y B' y' B'' y'' O 3-z , where A and A'' are chosen from the group comprising Groups 1, 2 and 3 and the F block lanthanides; A' is chosen from a metal selected from the group consisting of strontium, calcium and magnesium and B, B' and B'' are chosen from the D block transition metals according to the Periodic Table of the Elements adopted by the IUPAC wherein 0≤x''≤1 0<x'≤1, 0≤x≤1, 0<y≤1, 0≤y'≤1, 0≤y''≤1, x+x'+x''=1 , y+y'+y''=1 and z is a number which renders the compound charge neutral. The process according to Claim 12 wherein the multicomponent metallic oxide is represented by the composition La 0.2 Sr 0.8 Co 0.8 Fe 0.2 O 3-x .

Inventors: CAROLAN MICHAEL FRANCIS, DYER PAUL NIGEL, LABAR JAMES MARLOW SR, THOROGOOD ROBERT MICHAEL, CAROLAN, MICHAEL FRANCIS, DYER, PAUL NIGEL, LABAR, JAMES MARLOW, SR., THOROGOOD, ROBERT MICHAEL
Applicants: AIR PROD & CHEM, AIR PRODUCTS AND CHEMICALS, INC.
Application year: 1993
Main classification: B01D53
IPC codes: C01B13, B01D53, B01D71