Improved coatings for laser detector etalons

Abstract: This invention provides embodiments of etalons (10, 14, 18, 22) that eliminate or minimize a falloff of relative radiation modulation as a function of wavelength or FOV. A first embodiment employs a dispersive coating, such as a rugate (12a, 12b, 16), to correct for the phase shift across an etalon step. A second embodiment employs a dispersive coating, such as a rugate (20a, 20b, 24), that provides a stepless etalon in which the phase shifts are generated by the coating. It is shown that in a rugate the phase shift on reflection is directly related to the phase of a sinusoidal index of refraction profile within the rugate, while the frequency of the sinusoidal index of refraction profile determines the wavelength at which the phase shift occurs. By changing the phase of the sinusoidal index of refraction variation as the period of the sinusoidal index of refraction variation is changed, a phase shift of incident radiation is produced that is a function of the wavelength of the incident radiation.

Description: CROSS REFERENCE TO RELATED PATENT APPLICATIONS: This patent application is related to commonly assigned US-A-5 293 548, entitled "Dispersive Rugate Coatings", by E.T. Siebert and to commonly assigned US-A-5 291 332, entitled "Etalons with Dispersive Coatings", by E.T. Siebert. FIELD OF THE INVENTION: This invention relates generally to optical devices and, in particular, to optical coatings for etalons. BACKGROUND OF THE INVENTION: The use of etalons for analyzers and/or detectors of coherent radiation is known in the art. As an example, U.S. Patent No. 4,536,089, entitled "Analyzer for Coherent Radiation", (8/20/85) to E. T. Siebert, shows in Fig. 4, a multi-stepped etalon for use with a plurality of radiation detectors coupled to a plurality of detector channels. Reference is also made, by example, to U.S. Patent No. 4,170,416, entitled "Apparatus for Analyzing Coherent Radiation", (10/9/79) to C. R. Fencil. This patent shows a Fabry-Perot interferometer or etalon that comprises a flat glass spacer having partially reflecting, stepped surfaces. U.S. Patent 3,824,018, (7/16/74) to Robert Crane Jr., entitled "Coherent Light Source Detector" is also of interest. As employed herein, the term "etalon" is intended to encompass an optical device or element having two partially reflecting surfaces that are parallel to each other to optical tolerances. The space between the two reflecting coatings can be air or an optical material, and can be thick or thin. The thicker the spacer, the higher the resolution of the etalon. Fig. 1a shows a "solid" etalon where the spacer is a thick optical material. When the spacer is solid and thin, the etalon assumes the form of an interference filter. Referring to Fig. la, known etalon laser detectors employ an etalon 1 having physical steps (a-d) to generate a phase shift for radiation passing through the etalon. The phase shift across a particular step is given by: β = 2ks; k = 2πn cos '/λ , where s = step height; n,' = index, internal angle; and λ = wavelength. At midband, β is nominally π/2 or 90°, which is an optimum value. However, as the wavelength (or angle) changes, the phase moves off of optimum and the modulation (or signal across a step), going as sin β , decreases. The same is true of the quadrature phase shift. If this falloff becomes significantly large, proper identification of coherent sources ceases and detection "holes" appear at the bandedges or the field-of-view (FOV) edges. Known conventional coated laser detection etalons exhibit this undesirable degradation at the bandedges. The degradation is a result of (a) phase changes across the etalon steps, (b) phase changes between in-phase and quadrature channels, which is also due to phase changes across an etalon step, and (c) phase changes due to the FOV. For conventional coatings the typical falloff of modulation with wavelength/FOV is shown in Fig. 1b. This falloff is a significant contributor to the generation of (a) detection holes in the field of view, (b) limited spectral coverage, (c) and a requirement for additional detector channels, which adds cost and complexity to the laser detection system. It is thus one object of the invention to provide improved coatings for laser detection etalons that eliminate or minimize the undesirable degradation at the band edges due to the aforementioned phase changes at the etalon steps. In accordance with the present invention there is provided an etalon for modulating a radiation signal as specified in claims 1 and 5 hereinafter. Also in accordance with the present invention there is provided an apparatus for detecting coherent radiation as specified in claims 8 and 9 hereinafter. The foregoing and other problems are overcome and the object of the invention is realized by embodiments of etalons that eliminate or minimize a falloff of relative modulation as a function of wavelength or FOV. A first embodiment employs a dispersive coating to correct for the phase shift across an etalon step. A second embodiment employs a dispersive coating that provides a stepless etalon in which the phase shifts are generated by the coating. In addition, the invention teaches two methods of designing the etalon coatings. A first method employs a rugate coating technology in which the phase of the rugate is controlled to provide the desired result. A second method employs an iterative coating design technique in which a coating having the desired properties is generated by successive approximations using a nominal starting point and standard coating optimization routines. The invention extends the use of a rugate coating to provide a change in phase with wavelength. That is, the phase is made dispersive. An important factor in designing such a dispersive rugate coating is shown to be a realization that in a rugate the phase shift on reflection is directly related to the phase of a sinusoidal index of refraction profile within the rugate coating, while the frequency of the sinusoidal index of refraction profile determines the wavelength at which the phase shift occurs. Thus, by changing the phase of the sinusoidal index of refraction variation as the period of the sinusoidal index of refraction variation is changed, a phase shift of reflected incident radiation is produced that is a function of the wavelength of the incident radiation. BRIEF DESCRIPTION OF THE DRAWING The above set forth and other features of the invention are made more apparent in the ensuing Detailed Description of the Invention when read in conjunction with the attached Drawing, wherein: Fig. 1a illustrates in cross-section a conventional stepped etalon and the midband and bandedge transmission characteristics thereof; Fig. 1b is a graph illustrating a fall-off in relative modulation as a function of wavelength or FOV for the conventional etalon of Fig. la; Fig. 2a shows a first embodiment of a stepped etalon; Fig. 2b shows a second embodiment of a stepped etalon; Fig. 3a shows a first embodiment of a stepless etalon; Fig. 3b shows a second embodiment of a stepless etalon; Fig. 4 is a graph illustrating an improvement in transmission characteristics for etalons of Figs. 2 and 3; and Fig. 5a illustrates a rugate for use with a single wavelength; Fig. 5b illustrates a rugate for use with a band of wavelengths; Fig. 5c illustrates a rugate truncated at nulls of an envelope; and Fig. 5d is a graph illustrating an index of refraction profile for a rugate as a function of thickness; DETAILED DESCRIPTION OF THE INVENTION Reference is made to an article entitled "Spectral Response Calculations of Rugate Filters Using Coupled-wave Theory", by W.H. Southwell, Journal of the Optical Society of America, Vol. 5(9), 1558-1564(1988). This article discusses gradient-index interference filter coatings having an index of refraction that varies in a sinusoidal fashion in a direction normal to a substrate. A narrow bandwidth reflector is shown to be achieved with a rugate coating, the bandwidth being proportional to the fractional index change. In Fig. 5d there is shown an exemplary rugate index of refraction profile. In Fig.5c, the substrate is on the right, light is incident from the left, n s is the index of refraction of the substrate, n A is the index of refraction of the incident medium, typically air, n o is the average index of refraction through the rugate, and n 1 is the peak index of refraction variation, which is typically small compared with n o . Phi () is the starting or initial phase of the index of refraction variation. The word rugate, when used as a noun, is herein intended to define a gradient-index interference filter whose index of refraction profile is a sine wave. When used as an adjective, the word rugate is herein taken to describe the sine-wave index of refraction profile of a coating. The invention extends the use of a rugate coating to provide a change in phase with wavelength. That is, the phase is made dispersive. An important factor in designing such a dispersive rugate coating is a realization that in a rugate the phase shift on reflection is directly related to the phase of a sinusoidal index of refraction profile within the rugate coating, while the frequency of the sinusoidal index of refraction profile determines the wavelength at which the phase shift occurs. Thus, by changing the phase of the sinusoidal index of refraction variation as the period of the sinusoidal index of refraction variation is changed, a phase shift of reflected incident radiation is produced that is a function of the wavelength of the incident radiation. That is, the phase shift is made dispersive. For a single wavelength and normal incidence a rugate has an index of refraction (index) profile of: n(x) = n o +n 1 sin(Kx + ), K = 4πn o /λ, where n o is an average index, n 1 is a peak index variation, K determines a wavelength λ for which maximum reflection occurs,  is a starting phase of the index variation, and x is a thickness within a range of (0 ≤ x ≤ L). The amplitude reflectivity (r) produced by this profile is: r = tanh (u/4) exp (i ), R = r 2 = Intensity Reflectivity, u = KLn 1 /n o = 2πNn 1 /n 0 , where Δλ/λ = n 1 /n 0 is a fractional bandwidth, where N is a number of cycles in the coating, normally half integer, and L is the physical thickness of the coating. It can be seen that the maximum reflectivity at λ is determined by u which is the product of the fractional index variation times the number of cycles, while the phase shift on reflection is given by the phase shift of the index profile, . The foregoing analysis provides a basis for a rugate design for use with a single wavelength, as depicted in Fig. 5a. For multiple wavelengths which are widely separated (λ i - λ j >>Δλ), a rugate may be obtained for each wavelength by summing the index profiles: n(x) = n o + Σn i sin(K i x +  i )H((n i K(x-x o ))/(n o u i )) as is shown in Fig. 5b. For a Southwell analysis, H(t) = 1 if 0 ≤ x ≤ 1, otherwise H = 0. However, more generally H is an apodizing function chosen to minimize the reflection sidebands and also to have finite extent (the coating thickness). Possible forms of H are square waves (Southwell truncation), Fourier transform windowing functions (Hanning, Kaiser-Bessel, etc.) or other apodizing functions (e.g., truncated Gaussian or prolate spheroidal functions). It is within the scope of this invention to use these various apodizing functions for H. To design a rugate over a continuous wavelength band, the sum of Eq. (4) is replaced by an integral: n(x)=n o [1+∫H(n i K(x-x o )/n o u(K))sin(Kx + (K))dK/K], where no is equal to the average index of refraction, K - 4πn o /λ, Θ' is the internal angle in the coating and λ is the wavelength, where u(K) = 4tanh -1 [R(K)] 1/2 is a number of cycles in the coating to achieve a desired reflectivity R(K), n 1 is the peak deviation of the index from n o for a single wavelength, where (K) is the phase of reflected light as a function of K, where x is a distance into the coating, and where H is an envelope or apodizing function located at x o whose extent defines the region of index variation at the wavelength λ. In going to the integral, we have multiplied equation (4) by dK/ΔK, where ΔK = n i K/n o is the width of the reflection band. When N is constant and  is constant or linear in K (that is, same reflectivity at all wavelengths and no dispersion), when ΔK is small compared to the average K, and when H=1, the integral gives: n(x)=n o +n 1 (Δ K /K 1 )sin( K x+  )sinc[(x+')(ΔK/2)] where ' is the derivative of  with respect to K (assumed to be constant or zero), and K ,  are the average values of K, . This is similar to the aforedescribed case for a single wavelength, except that the sine wave is multiplied by an envelope (the sinc function) which nominally limits the large index extent to Δx ≈ 2π/ΔK = λ 2 /(2(n o )Δλ). As the spectral bandwidth increases, the region wherein the index varies significantly becomes smaller. It is possible to truncate this envelope, which is technically larger than L, after N cycles as seen in Fig. 5c. Even when  is slightly dispersive, Eq. (6) remains approximately valid with  replaced by (K), so that the same conclusions hold. It is seen that the peak deviation of the index from n o occurs at sin( K x +  )=1. If H=1 and sinc=1 (its maximum), then n p =n 1 ΔK/K 1 = n o ΔK/K. As the fractional bandwidth ΔK/K becomes large, then the peak index can become sufficiently large that it exceeds physical realizability. In this event, the sinc function must be kept less than unity. This can be accomplished by adding a prescribed dispersion to all the coatings. The actual coating phases are immaterial for laser detection etalons so long as their differences are controlled (Fig. 5), so equal phase dispersions can be added to each step. The phase dispersion can be chosen to either move the peak of the sinc function out of the coating (through ') or to change the sinc function into another function having a smaller peak (e.g., a quadratic phase gives the differences of Si functions). Also,  should be slowly varying enough, or n 1 should be chosen small enough, so that n 1 K(d/dK) << πn o . A smaller n 1 increases the N required for a given reflectivity and the fabrication tolerances. It is within the scope of the invention to employ coatings with a phase dispersion chosen to limit the peak index required to a predetermined realizable value. Based upon the foregoing, a technique for specifying a dispersive rugate coating over an extended spectral region is now provided. Using the desired dispersion and reflectivities for a given application Eq. (5) is used to determine a nominal coating design. The envelope may be truncated (usually at a zero of the sinc function) or apodized to limit it to a finite region. Coating thickness must be large enough to provide the fractional bandwidth and number of cycles required. The design may be iterated, if necessary, to eliminate truncation and end matching effects. It is also within the scope of the invention to convert the resulting graded index specification into a discrete multilayer embodiment, using standard techniques. Fabrication is essentially unchanged from standard rugate (or multilayer) fabrication. For rugates, the following points should be noted. First, the coating starting point (at the substrate) may not be at n o . However, truncation at a zero of the sinc function, or apodization, returns the starting point to zero. Second, the average frequency is essentially unchanged from the midband. Third, because a significant blocking region is generally desired around the etalon line, the rugate reflection band is relatively wide. This indicates that the rugate coating should be relatively thin, in that the bandwidth of the rugate decreases as the rugate thickness is increased. A relatively thin rugate coating relaxes fabrication control requirements and decreases stress build-up in the coating. Thus, standard coating fabrication techniques are applicable. In accordance with the invention, a first coating approach is to use  to compensate for the variation in β . Fig. 2a shows an etalon 2 that includes a transparent substrate 10 having rugate coatings 12a and 12b that are applied to top and bottom major surfaces, respectively, and step heights of β and 2β, as shown. To compensate for the phase variation β in there is selected: 1' - 2' = 2β' = 2dβ/dk = 4(s+(k/n) (dn/dk). Any combination of s that provides this result is permissible. Thus, one may select 2' = 0 and 1' = 2β' or one may select 2' = - 1' =β'. Similar relationships hold for 3' and 4'. It should be noted that both thickness and index dispersion are compensated for. In equation (7) the terms having a prime are a derivative with respect to k. A plurality of radiation detectors 13 are disposed relative to the etalon 2 for detecting coherent radiation, as in the above referenced U.S. Patent 4,536,039. Fig. 2b shows an etalon 3, having uniform step heights β, that includes a transparent substrate 14 having rugate coatings 16 applied only to a top major surface thereof, the rugate coatings 16 having the characteristics as shown. Figs. 3a and 3b show further embodiments of etalons 4 and 5, comprised of substrates 18 and 22, respectively, having rugate coatings 20a, 20b, and 24, respectively applied to one or more major surfaces thereof. These embodiments eliminate the etalon steps and employ the rugate coatings 20a, 20b, and 24 to generate the phase shifts. In this case, ' is set equal to zero in Eq. (6), and  is employed to determine the coating phase. It can be realized that if  = 0 for the r coating, then  = 180° for the out-of-phase coating (-r), 90° for the quadrature coating, and 270° for the negative quadrature coating. In Fig. 3b the term (i) is equal to the square root of minus one and is used to designate a 90° phase shift. In Figs. 3a and 3b r and -r give the phase shift , and the goal is to provide two coatings with an invariant 180° phase shift. For either of the embodiments of Figs. 2 and 3 radiation may be incident on the top or bottom surfaces and the result is the improved coating modulation characteristic shown in Fig. 4. It is important to note that replacing conventional etalon coatings with the rugate coatings of the invention may be accomplished using current coating technology. In this regard the substrate for the etalons 10 and 12 may be comprised of glass, and the coating material may be comprised of, by example, ThF 4 , ZnSe, Si x O y , and TiO 2 , and of combinations thereof. A presently preferred method of coating deposition employs an evaporative technique wherein the substrate is placed in an evacuated chamber with selected coating source materials, and where the source materials are controllably evaporated and deposited upon a surface of the substrate so as to provide the graded index of refraction variation with depth, or a multi-layered approximation thereof. The etalons of the invention may be employed, by example, as components of coherent radiation analyzers and detectors, of a type disclosed in the U.S. Patents that were to above referenced, to significantly improve the modulation characteristics thereof. While the invention has been particularly shown and described with respect to a preferred embodiment thereof, it will be understood by those skilled in the art that changes in form and details may be made therein without departing from the scope of the invention.

Claims: An etalon for modulating a radiation signal, comprising: a substrate (14, 18, 22) having a first major surface and a second, opposite major surface, the first major surface having at least one step (β) therein and a plurality of first subareas, and the second major surface having a plurality of corresponding second subareas located opposite the first subareas, the step (β) causing radiation propagating through the step to undergo a wavelength dependent step phase shift; and a plurality of dispersive coatings (20a,b) formed upon at least one of said major surfaces of said substrate, each coating being formed on at least one of said first or second subareas, said plurality of dispersive coatings (20a,b) each having a spatially varying index of refraction profile through a depth thereof, the index of refraction profile being the sum of a plurality of sinusoidal functions or an integral of sinusoidal functions and the phases and periods of said sinusoidal functions being selected so that radiation incident on said coatings is provided with a wavelength dependent corrective phase shift, said corrective phase shift combining with the said step phase shift so as to provide a non-wavelength dependent pase shift, thereby reducing a falloff in modulation of said etalon. An etalon as set forth in claim 1 wherein the profile is selected as a function of a height of said at least one step. An etalon as set forth in claim 1 or claim 2 wherein said plurality of dispersive coatings are rugate coatings have a spatially varying index of refraction profile n(x) that varies in accordance with a sinusoidal function, wherein n(x) is given by the expression: n(x)=n o [1+∫H(n i K(x-x o )/n o u(K))sin(Kx + (K))dK/K], where n o is equal to the average index of refraction, K = 4πn o /λ , Θ' is the internal angle in the coating and λ is the wavelength, where u(K) = 4tanh -1 [R(K)] 1/2 is a number of cycles in the coating to achieve a desired reflectivity R(K), n 1 is the peak deviation of the index from n o for a single wavelength, where (K) is the phase of reflected light as a function of K, where x is a distance into the coating, and where H is an envelope or apodizing function located at x o whose extent defines the region of index variation at the wavelength λ. An etalon as set forth in any one of the preceding claims, wherein said plurality of coatings are formed as multi-layered coatings. An etalon for modulating a radiation signal, comprising: a substrate (14, 18, 22) having a first major surface and a second, opposite major surface; and a plurality of dispersive coatings (20a, 20b, 24), each one of which is formed upon a subarea of at least one of said major surfaces of said substrate, said plurality of dispersive coatings each having a spatially varying index of refraction profile through a depth thereof, the index of refraction profile of each dispersive coating being the sum of a plurality of sinusoidal functions or an integral of sinusoidal functions and the phases and periods of said sinusoidal functions being selected so that a predetermined non-wavelength dependent phase shift is induced between radiation emanating from two adjacent coatings. An etalon as set forth in Claim 5 wherein said plurality of dispersive coatings are rugate coatings having a spatially varying index of refraction profile n(x) that varies in accordance with a sinusoidal function, wherein n(x) is given by the expression: n(x)=n o [1+∫H(n i K(x-x o )/n o u(K))sin(Kx + (K))dK/K], where n o is equal to the average index of refraction, K = 4πn o /λ, Θ' is the internal angle in the coating and is the wavelength, where u(K) = 4tanh -1 [R(K)] 1/2 is a number of cycles in the coating to achieve a desired reflectivity R(K), n 1 is the peak deviation of the index from n o for a single wavelength, where (K) is the phase of reflected light as a function of K, where x is a distance into the coating, and where H is an envelope or apodizing function located at x o whose extent defines the region of index variation at the wavelength λ. An etalon as set forth in claim 5 or claim 6 wherein said plurality of dispersive coatings are formed as multi-layered coatings. Apparatus for detecting coherent radiation, comprising: an etalon disposed for receiving coherent radiation, said etalon including a substrate having a first major surface and a second, opposite major surface, the first major surface having at least one step therein and a plurality of first subareas, and the second major surface having a plurality of corresponding second subareas located opposite the first subareas, the step causing radiation propagating through the step to undergo a wavelength dependent step phase shift; and a plurality of dispersive coatings (20a, 20b, 24) formed upon at least one of said major surfaces of said substrate (14, 18, 22), each coating being formed on at least one of said first or second subareas, said plurality of dispersive coatings each having a spatially varying index of refraction profile through a depth thereof, the index of refraction profile being the sum of a plurality of sinusoidal functions or an integral of said sinusoidal functions and the phases and periods of said sinusoidal functions being selected so that radiation incident on said coatings is provided with a wavelength dependent corrective phase shift, said corrective phase shift combining with the said step phase shift so as to provide a non-wavelength dependent phase shift, thereby reducing a falloff in a modulation characteristic of said etalon due to the said step phase shift for coherent radiaiton; and detector means disposed relative to said etalon for detecting a presence of the coherent radiation. Apparatus for detecting coherent radiation, comprising: an etalon (3) disposed for receiving coherent radiation, said etalon including a substrate (14, 18, 22) having a first major surface and a second, opposite major surface; a plurality of dispersive coatings (20a, 20b, 24), each one of which is formed upon a subarea of at least one of said major surfaces of said substrate, said plurality of dispersive coatings each having a spatially varying index of refraction profile through a depth thereof, the index of refraction profile of each dispersive coating being the sum of a plurality of sinusoidal functions or an integral of sinusoidal functions and the phases and periods of said sinusoidal functions being selected so that a predetermined non-wavelength dependent phase shift is induced in the coherent radiation between radiation emanating from two adjacent coatings; and detector means disposed relative to said etalon for detecting a presence of the coherent radiation.

Inventors: SIEBERT EDWARD T, SIEBERT, EDWARD T.
Applicants: HUGHES AIRCRAFT CO, HUGHES AIRCRAFT COMPANY
Application year: 1993
Main classification: G02B5
IPC codes: G01J3, G02B5