Formation of supersaturated rare earth doped semiconductor layers by CVD

Abstract: A CVD process for producing a rare earth-doped, epitaxial semiconductor layer on a substrate is disclosed. The equipment is a 7.6 cm diameter ultra high vacuum chemical vapor deposition (UHVCVD) reactor wherein pumping and wafer loading are done using the same end of the reactor. This modification allows the installation of a heated precursor reservoir (1) on the opposite end of the reactor. The reservoir is connected to the reactor end flange using a short diameter stainless steel tubing (12). The reactor is heated by external resistive heating (4). The reactor is pumped both before and during deposition by a 150 L/sec turbomolecular pump (8) backed by a two-stage oil pump (9). The load lock chamber is also pumped by a turbomolecular pump (10) to prevent contamination from pump oil.The process utilizes a silane or germane and a rare earth compound in the gas phase. By this method single phase, rare earth-doped semiconductor layers, supersaturated in the rare earth, are produced. The preferred rare earth is erbium and the preferred precursors for depositing erbium by CVD are erbium hexafluoroacetylacetonate, acetylacetonate, tetramethylheptanedionate and flurooctanedionate. The process may be used to produce optoelectronic devices comprising a silicon substrate and an erbium-doped epitaxial silicon film.

Description: The invention relates to a CVD process for producing a rare earth-doped, epitaxial semiconductor layer on a substrate utilizing a silane or germane and a rare earth compound in the gas phase. By this method single phase, rare earth-doped semiconductor layers, supersaturated in the rare earth, are produced. The process may be used to produce optoelectronic devices comprising a silicon substrate and an erbium-doped epitaxial silicon film. In recent years increasing research has been focused on the realization of optoelectronic integrated circuits (OE-ICs) on silicon. Possible applications would be chip-to-chip interconnects, parallel processing and the integration of photonics on silicon chips. While the first two applications require basically a light source and a detector on silicon, operating above 77 K, the last application requires the operation of the light source at a certain wavelength, i.e., about 1.5 µm, which falls in the absorption minimum of optical fibers. In 1983 Ennen et al. [Appl. Phys. Lett. 43, 943 (1983)] pointed out the potential of rare-earth ions in semiconductor materials for the development of light-emitting diodes and lasers. One of the most promising candidates for the preparation of these devices is erbium doping of silicon. The 1.54 µm luminescence of erbium is below the band gap of silicon, thus allowing the construction of optical wave guides within the silicon. This property presents exciting possibilities for creating optical devices in silicon and for integrating electrical and optical devices in circuits fabricated in silicon. The mature manufacturing technology of silicon can be extended into optical communications by this path as the limitation of the silicon indirect band gap is overcome. This wavelength is also becoming extremely important in optical communication because it corresponds to a transmission maximum in optical fibers and is also the output of wavelength of IR-pumped Er-doped silica optical amplifiers. The 1.54 µm luminescence of erbium is the result of an internal 4f transition. The 5s and 5p shells shield the 4f orbitals of the Er 3+ from first-order host lattice effects, and, thus, luminescence is fairly independent of the host materials. The optical transitions occur between the spin-orbit levels, 4 I 13/2 → 4 I 15/2 , of Er 3+ (4f 11 ). Since the influence of the crystal field of the host lattice is weak, erbium as an impurity in silicon is expected to show luminescence at room temperature. Within the past decade, the photo- and electroluminescence, electrical characteristics, and structural properties of Er-doped silicon have been studied. For instance in the article : Optical activation of Er 3+ implanted in silicon by oxygen impurities (Japanese Journal of Applied physics, Vol. 29, N° 4, April 1990, ppL 524-526) and in US-A-5119460 which describes a structure including a silica-based, erbium-doped active core. The active core has an erbium-to-silicon atomic ratio of at least about 0.01, an absolute erbium concentration of at least about 1.4x10 20 atoms/m 3 . However, prior to the present invention, all Er-doped silicon layers had to be prepared by ion implantation of bulk silicon or by low energy ion implantation of MBE grown silicon. After implantation, samples were annealed to both remove ion damage and to "activate" the implanted erbium. (Activate in the sense of possibly forming an Er-impurity complex which acts as the optical center in these materials.) The best results were obtained at annealing temperatures of 900°C. Unfortunately, erbium possesses a solubility limit in Si of about 1.3 x 10 18 atom/cm 3 at 900°C, and annealing results in the formation of platelets of ErSi 2 which precipitate out within the silicon phase if the concentration of Er is higher than 1.3 x 10 18 . Since higher levels of incorporation of rare earth into epitaxial silicon layers would provide more efficient and powerful devices, there is a need for a process which would produce levels of incorporation above the present limit of solubility at 900°C. We have found that by avoiding the requirement for high temperature annealing and taking advantage of the non-equilibrium nature of chemical vapor deposition (CVD), it is possible to exceed the equilibrium concentration of dopants to produce metastable, highly doped materials. Thus, ultra high vacuum chemical vapor deposition (UHVCVD) is used to deposit erbium-doped silicon with an erbium doping level of about 2 x 10 19 atoms/cm 3 , an order of magnitude above the equilibrium solid solubility of erbium in silicon. It is an object of the present invention to provide a process for producing high levels of incorporation of rare earths, particularly erbium, into epitaxial silicon layers. It is a further object to provide a process for producing germanium layers containing high levels of erbium. It is a further object to provide optoelectronic devices having improved output and efficiency. These and other objects and features are realized in the present invention which relates to a process for creating an erbium-doped semiconductor layer on a substrate comprising introducing into a UHVCVD chamber a mixture of a first component chosen from germanes, silanes or mixtures thereof in the gas phase and a second component consisting of an erbium compound in the gas phase and heating the substrate, whereby a deposition film is formed on the substrate. The erbium compound has a vapor pressure greater than 133.3 10 -6 Pa at 500°C. In a preferred process a source of oxygen atoms, which may be external (such as NO) or may be the rare earth ligand itself, is provided whereby the resulting silicon or germanium layer comprises erbium and oxygen, in addition to the semiconductor. When the precursor is chosen to include the source of oxygen, preferred precursors are tris(1,1,1,5,5,5-hexafluoro-2,4-pentanedionato-0,0') erbium, tris(2,4-pentanedionato-O,O')erbium, tris (1,1,1-trifluoropentanedionato-O,O')erbium, tris(1,1,1-trifluoro-5,5-dimethyl-2,4-hexanedionato-O,O')erbium, tris(5,5-dimethyl-2,4-hexanedionato-0,0')erbium, tris(1-cyclopropyl-4,4,4-trifluoro-1,3-butanedionato-0,0')erbium, tris(2,2,6-trimethyl-3,5-heptanedionato-0,0')erbium, tris(2,2,6,6-tetramethyl-3,5-heptanedionato-0,0')erbium, tris(1,1,1,5,5,6,6,7,7,7-decafluoro-2,4-heptanedionato-0,0')erbium, 2,2-dimethyl-6,6,7,7,8,8,8-heptafluoro-3,5-octanedionato)erbium and tris[(2-phenyliminomethyl)phenolato-O,N]erbium. When the source of oxygen atoms is external, such as nitrous oxide, preferred precursors are tris(cyclopentadienyl)erbium, tris(pentamethylcyclopentadienyl)erbium, tris(methylcyclopentadienyl)erbium, tris(isopropylcyclopentadienyl)erbium, bis(cyclopentadienyl)erbium halides, and bis(cyclopentadienyl)erbium alkyls. In a particularly preferred process the silane or germane is SiH 4 , the erbium compound is tris(1,1,1,5,5,5-hexafluoro-2,4-pentanedionato-0,0') erbium[Er(HFAC) 3 ], and the erbium-doped semiconductor layer contains more than 10 19 atoms/cm 3 of erbium and additionally at least 10 18 atoms/cm 3 of oxygen. The substrate is heated at 450°C to 800°C, preferably at about 650°C and the pressure is maintained at from 1333 to 133.3 10 -9 Pa. The silane is provided at a flow rate of 1 to 100 sccm, preferably at about 4 sccm when the temperature is 650°C. There is also disclosed an optically active epitaxial film comprising silicon and from about 8 x 10 18 to about 8 x 10 19 atoms/cm 3 of erbium, preferably including from 10 17 to 10 19 atoms/cm 3 of oxygen, said film being substantially free of erbium silicide precipitates. There is also disclosed an optoelectronic device comprising a silicon substrate and an epitaxial silicon film adherent thereon, said film containing from about 8 x 10 18 to about 8 x 10 19 atoms cm 3 of erbium and said epitaxial film being substantially free of erbium silicide precipitates. In yet a further aspect the invention relates to a chemical vapor deposition process for creating a rare earth-doped silicon layer on a substrate comprising depositing said layer by the thermal decomposition of a gaseous precursor mixture of a silane and a rare earth compound. According to the process the rare earth-doped silicon layer may contain the rare earth element in substantially a single phase at a concentration which is higher than the equilibrium concentration for a single phase of that rare earth in silicon. Preferably the gaseous precursor mixture additionally comprises a source of oxygen atoms, which can be the rare earth compound itself. The rare earth compound is preferably chosen from the group consisting of hexafluorocetylacetonates, acetylacetonates, tetramethylheptanedionates and fluorooctanedionates, and the rare earth is chosen from the group consisting of erbium, terbium and europium. FIG. 1 is a schematic representation of an ultra high vacuum CVD apparatus useful in the practice of the invention. FIG. 2 is an IR spectrum of the photoluminescent output of a device formed by the process of the invention. A 7.6 cm diameter ultra high vacuum chemical vapor deposition (UHVCVD) reactor useful for the preparation of films of the invention is depicted in FIG. 1. The reactor differs in design from the original UHVCVD reactor described by Meyerson et al. in the article : Low temperature Si and Si: Ge epitaxy by UHVCVD, published in the IBM Journal of R&D, Vol. 34, N° 6, Nov. 1990, pp 006-015; in that pumping and wafer loading are done using the same end of the reactor. This modification allows the installation of a heated precursor reservoir 1 on the opposite end of the reactor. The reservoir is connected to the reactor end flange using a short length of 12.7mm diameter stainless steel tubing 12. The reactor is constructed of quartz glass and stainless steel, using flanges, valves and seals common to the construction of high vacuum apparatus. The reactor is heated by external resistive heating (tube furnace 4). The reactor is pumped both before and during deposition by a 150 L/sec turbomolecular pump 8 backed by a two-stage oil pump 9. The load lock chamber is also pumped by a turbomolecular pump 10 to prevent contamination from pump oil. The base pressure of the reactor is below 133.3 10 -9 Pa and the load lock is capable of producing pressures below 133.3 10 -6 Pa from atmospheric pressure in less than 10 minutes. According to the process of the invention the precursor reservoir 1 is charged with an appropriate amount of the rare earth compound and evacuated. In a preferred embodiment, the rare earth is erbium, although other rare earths, particularly terbium and europium may also be used. The rare earths include elements 57 to 71. The rare earth compounds are restricted in that they must be able to provide a vapor for the CVD process at the temperatures and pressures at which CVD can be run. In a practical sense this means that the rare earth compound should exhibit a vapor pressure of at least about 133.3 10 -6 Pa at 500°C. Exemplary compounds fall into two broad categories: (a) coordination compounds, where the rare earth is bound to oxygen, nitrogen, sulfur or phosphorus, and (b) organometallic compounds, where the rare earth is bound to carbon atoms. Suitable ligands for the coordination compounds include: acetylacetonate (2,4-pentanedionate) and derivatives of acetylacetonate including hexafluorocetylacetonate (HFAC, 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate) and trifluoroacetylacetonate (TFAC, 1,1,1-trifluoro-2,4-pentanedionate); 2,4-hexanedionate and derivatives of 2,4-hexanedionate; 2,4- and 3,5-heptanedionate and derivatives including 2,2,6,6-tetramethyl 3,5-heptanedionate (THD) , 2,2,6-trimethyl 3,5-heptanedionate, and 1,1,1,5,5,6,6, 7,7,7-decafluoro 2,4 heptanedionate; 2,2-dimethyl-6,6,7,7,8,8,8-heptafluoro-3,5-octanedionate(FOD); and Schiff base type complexes such as the condensation product of aniline and 2-hydroxybenzaldehyde, which give a bidentate ligand binding through nitrogen and oxygen. Examples of organometallic compounds include tris-cyclopentadienyl erbium (III) and organic derivatives of the cyclopentadienyl ring including the tris-pentamethylcyclopentadienyl ligand, the methylcyclopentadienyl ligand, and the isopropylcyclopentadienyl ligand, bis(cyclopentadienyl)erbium halides, and bis-(cyclopentadienyl)erbium alkyls, wherein alkyl is defined as a linear or branched hydrocarbon radical of one to six carbon atoms. Preferred ligands include acetylacetonate, HFAC, THD and FOD. From the literature it appears that the inclusion of oxygen (and perhaps carbon, nitrogen and fluorine as well) along with erbium gives rise to enhanced photoluminescence. For this reason it is desirable to provide a source of oxygen for the CVD film. This can be achieved either by introducing a gaseous source of oxygen, such as nitrous oxide, or by using a precursor compound that contains oxygen, such as the ligands discussed above. In either case, when the precursor is thermally decomposed on the substrate, a film containing both rare earth atoms and oxygen (or other impurity" atoms) will be deposited. The substrate is loaded onto the quartz wafer boat 3, placed in the load-lock chamber 2 and evacuated to a suitable pressure, preferably less than 133.3 10 -5 Pa. The substrate can be any material that is compatible with the CVD conditions; single-crystal silicon wafers are preferred. In general, a better film is produced when the substrate wafer has been previously cleaned in the usual manner. A precursor gas for the semiconductor film is introduced into the reactor. The precursor can be any silane or germane or mixture of the two that is volatile under the conditions of CVD; silane (SiH 4 ), disilane (Si 2 H 6 ), germane (GeH 4 ) and digermane (Ge 2 H 6 ) are preferred. Group III dopant precursors, such as diborane, or group V dopant precursors, such as phosphine, may be introduced to alter the electrical properties of the films. The semiconductor precursor gases are introduced via gas inlet 11 into the reactor. The temperature of the reactor is maintained at 450°C to 800°C. Below 450°C epitaxial growth of Si, Ge, or Si/Ge is not observed; as 900°C is approached, erbium begins to segregate. The pressure in the load- lock chamber 2 before introducing the substrate into the reactor is preferably below 133.3 10 -5 Pa. After the substrate is moved through the gate valve 5 into the reactor chamber 13 by the magnetically coupled manipulator 6, the rare earth precursor is vaporized into the reaction chamber from the reservoir 1 by applying heat. In the embodiment shown in FIG. 1 the heat is supplied by an external oven 7 surrounding the reservoir. In the case of Er(HFAC) 3 , the optimal rate of vaporization is obtained when the oven is held at 58° C. Regulation of the precursor reservoir temperature, and hence regulation of the partial pressure of precursor in the reactor, is important to the success of the process. In the case of Er(HFAC) 3 , at temperatures below 55°C, no erbium was incorporated. Above 65°C, the films consisted of a polycrystalline layer 30 to 40 nm thick with a concentration of erbium of 10 to 20%. The thickness of this layer did not increase with longer deposition times, indicating that the growth surface was "poisoned" by the precursor. The likely explanation for this observation is that there is a minimum growth rate above which the erbium and other elements from the precursor may be incorporated and below which the growth surface is poisoned. (The growth rate of pure silicon from silane at 1 mtorr pressure is 4 Å/min at 550°C and 40 nm/min at 650°C.) The selection of the appropriate oven temperature for a given rare earth compound is readily determined empirically as part of the routine adjustment of experimental conditions. Reasonable temperatures can be calculated by comparison of the vapor pressure of the precursor of interest at the pressure of the reservoir with the vapor pressure of Er(HFAC) 3 at 58°/133.3 Pa. Experimental Results The precursor reservoir was charged with 1.0g of anhydrous tris(hexafluoroacetylacetonato-0,0') erbium (III) and evacuated. Four 2.25 inch diameter Si wafers which had previously been cleaned and dipped in 10% hydrofluoric acid until the surface became hydrophobic were immediately placed in the reactor load-lock. The flow of silane (4 sccm) and hydrogen (50 sccm) was started, and the valve to the room-temperature erbium source was opened. After a ten minute pump down in the load-lock the wafers were transferred to the reactor. Three minutes after loading, the flow of hydrogen was stopped and the temperature of the reactor was increased from 500°C to 650°C over a period of one hour. With the reactor at 650°C, the temperature of the oven surrounding the precursor was increased to 58°C, directly subliming Er(HFAC) 3 into the reactor. The pressure during deposition was 200 Pa, giving a calculated system pumping speed of 42 L/sec. The deposition rate under these conditions was approximately 3 nm/min and deposition times varied from 3 to 12 hours. The flow of silane was discontinued, and the wafers were withdrawn to the load-lock chamber to cool. The composition of the films was determined using Rutherford Back Scattering spectroscopy (RBS) to determine the erbium concentration and Secondary Ion Mass Spectroscopy (SIMS) to determine the level of carbon, fluorine and oxygen present in the films. Films produced under the conditions described above (evaporator temperature (T e ) = 58°C, substrate temperature (T s ) = 650°C) had a uniform erbium concentration of 2 x 10 19 atoms/cm 2 with carbon, fluorine and oxygen levels of approximately 4 x 10 19 atoms/cm 3 . The carbon, oxygen, and fluorine levels were equal in the three samples measured, within the uncertainty of the measurement. These "impurities" arise from the decomposition of the precursor. Transmission Electron Microscopy (TEM) was performed on two of the samples. Sample 1 was a 2.7 µm thick film (T e = 60°C, T s = 650°C, Er concentration = 8 x 10 19 atoms/cm 3 ) deposited on Si(100). Electron diffraction indicated that the film was epitaxial but also showed the presence of a second phase readily assignable as ErSi 2 . The corresponding electron image indicated the crystal quality of the layer was extremely poor. Sample 2 was a 2 µm thick film produced by lowering T e by 2°C and growing for longer time (11 h instead of 3 h). The cross sectional TEM of this film does not show any precipitated ErSi 2 . The erbium concentration of sample 2 was 2 x 10 19 atoms/cm 3 . This level is at least one order of magnitude higher than the highest concentrations reported using implantation techniques. The cross-sectional TEM also shows a high density of threading defects. These defects may be due to stress caused by the introduction of erbium (or erbium complexes) into the film, but it is more likely that these defects are due to contamination from the precursor. At the temperatures used in UHVCVD, the crystal quality is very sensitive to the presence of carbon and oxygen and the SIMS results indicate that these elements are present in relatively high concentrations. One other possible source of contamination is residual carbon and oxygen from the decomposition of the ligand upstream from the deposition zone. The Er(HFAC) 3 complex decomposes in parts of the reactor which are as much as 300°C cooler and may continue to evolve small quantities of organic material which may contaminate the initial growth surface. Support for this hypothesis is given by TEM which shows that the defects occur abruptly and at highest concentration at the initial growth interface. In this respect there may be an advantage to other precursors, particularly of the organometallic type, when used together with controlled levels of oxidant gas. Rare earth compounds can be prepared by methods well known in the art. The Er(HFAC) 3 used in the foregoing experiment was made by a modification of the known process for the synthesis of Al(HFAC) 3 described by Morris et al. in Inorganic Syntheses, Vol. 9, S.Y. Tyree, editor; McGraw Hill, New York, (1967) p. 39. This synthesis is an improvement over the synthesis of Er(HFAC) 3 described by Berg and Acosta [Anal. Chim. Acta, 40, 101, (1968)] in that it is carried out under nonaqueous conditions; it thus avoids the intermediate synthesis of Er(HFAC) 3 monohydrate which must be dehydrated over phosphorus pentoxide under vacuum at elevated temperatures before it can be used in a CVD process. The new synthesis is also considerably faster and easier than the literature preparation, which yields a difficult to handle mixture of crystals and oil requiring several recrystallizations with significant loss of product at each step. All manipulations were carried out under nitrogen using standard Schlenk-line and dry-box techniques. ErCl 3 +3C 5 H 2 F 6 O 2 Er(C 5 HF 6 O 2 ) 3 +3HCl A 200 mL, three-neck flask equipped with a reflux condenser, pressure-equalizing dropping funnel, and gas inlet was charged with 4.11 g (.015 mol) of anhydrous ErCl 3 in 100 mL of a CCl 4 . To the stirred suspension was added 9.57g (0.046 mol) of 1,1,1,5,5,5-hexafluoro-2,4-pentanedione. After several minutes, the solution turned from colorless to faint pink and HCl gas was evolved. Following the addition of the ligand, the solution was refluxed for 1 hour. The hot solution was suction filtered and cooled to -10°C for 6 hours. Pink crystals were observed to form in the flask. The crystals were filtered, washed with cold CCl4 and sublimed twice at 100x C at 133.3 10 -2 Pa. A yield of 7.9 g (67%) of pure Er(HFAC) 3 was obtained. It is contemplated that the foregoing synthesis could be used in similar fashion to prepare other complexes with other rare earths by substituting the appropriate rare earth trichloride for ErCl 3 and the appropriate ligand for HFAC. Photoluminescence measurements were carried out on several of the samples. Measurements were done using an Ar ion laser operating at 514 nm as the excitation source and a Cygnus FTIR to detect the emitted radiation. A representative spectrum of a 2 µm film with an Er concentration of 2 x 10 19 atoms/cm 3 (identical to the sample used for TEM measurements above) is shown in FIG. 2. This spectrum was obtained at 10 K and the luminescence fell sharply as the temperature was raised. At 200 K, the signal intensity was down by a factor of 50 and was not observable at room temperature.

Claims: A process for creating an erbium-doped semiconductor layer on a substrate comprising introducing into a film-forming UHVCVD chamber, for forming a deposition film on a substrate, a mixture of a first component chosen from the group consisting of germanes, silanes and mixtures thereof in the gas phase and a second component consisting of an erbium compound in the gas phase and heating said substrate, whereby a deposition film is formed on said substrate, said erbium compound having a vapor pressure greater than 133.3x10 -6 Pa at 500° C. A process according to claim 1 additionally comprising introducing a source of oxygen atoms into said UHVCVD film-forming chamber whereby said semiconductor layer comprises said semiconductor, erbium and oxygen. A process according to claim 2 wherein said source of oxygen atoms is said erbium compound. A process according to claim 3 wherein said erbium compound is chosen from the group consisting of tris (1,1,1,5,5,5-hexafluoro-2,4-pentanedionato-0,0')erbium, tris(2,4-pentanedionato-O,O')erbium, tris(1,1,1-trifluoropentanedionato-O,O')erbium, tris(1,1,1-trifluoro-5,5-dimethyl-2,4-hexanedionato-O,O')erbium, tris(5,5-dimethyl-2,4-hexanedionato-0,0')erbium, tris(1-cyclopropyl-4,4,4-trifluoro-1,3-butanedionato-0,0')erbium, tris (2,2,6-trimethyl-3,5-heptanedionato-0,0')erbium, tris(2 ,2,6,6-tetramethyl-3,5-heptanedionato-0,0')erbium, tris (1,1,1,5,5,6,6,7,7,7-decafluoro-2,4-heptanedionato-0,0 ')erbium,2,2-dimethyl-6,6,7,7,8,8,8-eptafluoro-3,5-octanedionato-0,0')erbium and tris [(phenyliminomethyl) phenolato-O,N] erbium. A process according to claim 4 wherein said silane or germane is SiH 4 and said erbium compound is tris 1,1,1,5,5,5-hexafluoro-2,4-pentanedionato-0,0')erbium. A process according to claim 1 wherein said erbium-doped semiconductor layer contains more than 10 19 atoms/cm 3 of erbium. A process according to claim 6 wherein said erbium-doped semiconductor layer additionally contains at least 10 18 atoms/cm 3 of oxygen. A process according to claim 1 wherein said substrate is heated at a temperature between 450° and 800°C. A process according to claim 2 wherein said source of oxygen atoms is a third gaseous component. A process according to claim 9 wherein said third gaseous component is nitrous oxide. A process according to claim 9 wherein said erbium compound is chosen from the group consisting of tris (cyclopentadienyl) erbium, tris(pentamethylcyclopentadienyl)erbium, tris (methylcyclopentadienyl) erbium, tris (isopropylcyclopentadienyl) erbium, bis(cyclopentadienyl)erbium halides, and bis(cyclopentadienyl)erbium alkyls. A process according to claim 4 comprising the steps of: (a) introducing a silicon substrate into a film-forming UHVCVD chamber for forming a deposition film on a substrate; (b) introducing a flow of from 1 to 100 sccm of SiH 4 into said UHVCVD chamber; (c) maintaining said substrate at from 450° to 800°C; (d) maintaining the pressure in said chamber at from 133.3x10 to 133.3x10 -9 Pa; and (e) leading a flow of tris(1,1,1,5,5,5-hexafluoro-2,4-pentanedionato)erbium in the gas phase into said chamber so as to form a deposition film on said substrate. A process according to claim 12 wherein said flow of SiH 4 is 4 sccm, said substrate is maintained at about 650°C, said pressure is maintained at about 200 Pa and said flow of tris(1,1,1,5,5,5-hexafluoro-2,4- pentanedionato)erbium is obtained by heating tris(1,1,1,5,5,5-hexafluoro-2,4-pentanedionato) erbium at a temperature between 55 and 65°C at 200 Pa. A chemical vapor deposition process for creating a rare earth-doped silicon layer on a substrate wherein said rare earth is chosen from the group consisting of erbium, terbium and europium comprising depositing said layer by the thermal decomposition of a gaseous precursor mixture of a silane and a rare earth compound in a UHVCVD chamber. A process according to claim 14 wherein said rare earth-doped silicon layer contains said rare earth element in substantially a single phase at a concentration which is higher than the equilibrium concentration for a single phase of said rare earth in silicon. A process according to claim 14 wherein said gaseous precursor mixture additionally comprises a source of oxygen atoms. A process according to claim 16 wherein said source of oxygen atoms is said rare earth compound. A process according to claim 17 wherein said rare earth compound is chosen from the group consisting of hexafluoroacetylacetonates, acetylacetonates, tetramethylheptanedionates and fluorooctanedionates.

Inventors: BEACH DAVID BRUCE, BEACH, DAVID BRUCE
Applicants: IBM, INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1993
Main classification: H01L21
IPC codes: H01L31, C30B25, H01L21