Sealant and adhesive with damping properties

Abstract: Compositions for use as sealants, adhesives and/or coatings containing 3,4-polyisoprene and blends of liquid and/or solid rubbers and/or finely divided polymer powders and optionally plasticizers, fillers and other conventional raw materials exhibit superior vibration damping properties compared to conventional compositions not containing 3.4-polyisoprene. The compositions may be cured similar to the conventional sealant/adhesive and/or coating compositions.

Description: This invention relates to novel compositions for adhesives sealants and/or coatings containing 3,4-polyisoprenes. More particularly this invention involves curable and non-curable compositions for adhesives sealants and/or coatings containing conventional polymeric components and in addition 3,4-polyisoprenes. A preferred field of application for these compositions is the vehicle industry, especially the automotive industry. In the manufacture and assembly of automobiles, adhesives sealants and coatings are used for a variety of different purposes. Sealants and adhesives are selected mainly on the base of the following properties: strength, i.e. shear strength, peel strength elongation, flexibility durability ease of application. For coatings, especially underbody coatings, abrasion resistance is an additional criterion. In view of reducing the complexity of car manufacturing and thus reducing manufacturing costs, there is a need for "multifunctional" products, i.e. sealants, adhesives and/or coatings which solve additional problems in addition to their prime function. Contemporary design of vehicles, machines and appliances involves almost exclusively the use of thin gauge sheet metal. Moving parts and running engines cause vibration of these thin metal structures, which in turn create noise. Numerous methods for noise abatement are known, however, most of these methods require additional manufacturing steps and/or components which have only the function of vibration damping. A prime example of the conventional products for vibration damping are highly filled bitumen pads. These pads have to be extruded, die-cut and shaped in separate steps. Prior to application they frequently have to be heat formed to fit them to non flat structures and then glued to the car body, machine or appliance. Numerous attempts have been made to replace this costly manual procedure by products which can be easily applied by robots. Plastisol formulations serving the dual function of underbody coating (protection against abrasion) and acoustic damping have been described in EP-A-358598, or DE-A-3444863. DE-A-4013318 discloses a two layer underbody coating which performs the dual functions of protecting against abrasion and absorbing noise resulting from impact (stones, gravel, water). Whereas these products/processes are quite useful for combining the functions of underbody coating and noise abatement, there still remains a need to combine the function of an adhesive and/or sealant with noise reduction. This is particularly desirable for those parts of a car, machine or appliance that do not require a specific coating for protection against abrasion such as trunk and hood lids, doors or fire walls of a car. Adhesives and sealants for these parts are normally applied early on in production, in the so-called "body shop". Hence, they are applied to the bare, uncleaned metal which is frequently covered with an oil for rust protection. Although plastisols, PVC-plastisols in particular, are used in the body shop, those disclosed in EP-A-358598 or DE-A-3444863 are not suitable as adhesives/sealants for bare metal substrates. The plastisol formulations which are especially designed for bare metal application have poor to no vibration damping properties. Another class of adhesives/sealants suitable for body shop application are based on rubbers especially vulcanizing compositions based on 1,3-polybutadienes and/or 1,3-polyisoprenes. These preferably contain liquid, low molecular weight polydienes, sulfur and optionally accelerators for sulfur vulcanization. In addition, these formulations may contain solid high molecular weight rubbers, whereby the liquid polydiene(s) and/or the solid rubber may contain functional groups such as hydroxyl groups, carboxylic groups, anhydride groups or epoxy groups. This class of rubber based adhesives/sealants has been the subject of various patent applications, e.g. EP-A-97394, EP-A-309903, DE-A-3834818, DE-A-4120502, DE-A-4122849, EP-A-181441 and EP-A-356715. Although DE-A-4122849 and EP-A-181441 mention a potential use of these compositions for vibration damping and/or sound damping, no reference is made to the efficacy of these compositions for vibration damping, because to the best of applicant's knowledge these materials have not been used for their combined adhesive/sealant and vibration damping properties. The use of 3,4-polyisoprenes for sealants, adhesives and coatings has thus far not been described. FR-A-2255313 (DE-A-2459357) discloses materials with a high coefficient of vibration damping containing predominantly polyisoprene with at least 60% 1,2- and 3,4-structures. These materials are vulcanized to polyisoprene sheets. The cured sheet is then bonded to a substrate or substrates using a solvent born adhesive (Chemosil 220). FR-A-2255313 is silent about curable compositions based on 3,4-polyisoprene to be applied in an uncured state to a metal substrate followed by curing. Moreover, applications as curable adhesives, sealants or coatings are not disclosed. US-A-4808657 discloses a rubbery adhesive cement comprising 70% to 95% of volatile solvents containing a vulcanizable rubbery polymer(s) tackifying resins, vulcanizing agents and fillers whereby the rubbery polymer(s) may contain 3,4-polyisoprenes. These adhesive cements are used in tire building applications for cementing the mating ends of extruded tire treads. Other applications for forming rubber to rubber bonds are also disclosed. US-A-4808657 does not disclose curable solventfree damping adhesives, sealants or coatings. In accordance with the present invention, it has been found that 3,4-polyisoprene can be combined with other curable or non-curable liquid and/or solid rubbers or liquid polyolefins to provide adhesive and sealant formulations with superior vibration damping properties. Surprisingly, the incorporation of 3,4-polyisoprenes into sealant/adhesive formulations does not have a detrimental effect on other desired properties of the formulations, i.e. applicability, curing speed, adhesion, strength and/or elasticity. In addition to 3,4-polyisoprene and at least one curative, sealant/adhesive formulations according to the present invention contain at least one of the following items: one or more liquid or solid rubber(s) or elastomers finely divided polymer powders fillers tackifiers and/or adhesion promoters plasticizers/liquid extenders curatives, accelerators, catalysts stabilizers, antioxidants rheology improvers. 3,4-polyisoprenes according to this invention are polyisoprenes with a significant content of at least 30%, and preferably 55% to 70% of 3,4-polyisoprene, as determined by NMR-spectroscopy. Although the preferred 3,4-polyisoprenes are high molecular weight (MW) polymers, i.e. MW 200000 and above, it can be advantageous for some formulations to use low molecular weight liquid 3,4-polyisoprenes as additives to conventional plastisols, for example. The compositions according to this invention contain 5 to 40% by weight of 3,4-polyisoprene, preferably 5 to 20% by weight of 3,4-polyisoprene, and more preferably 5% to 15% by weight of 3,4-polyisoprene. Acoustical damping characteristics can be varied according to the amount of 3,4-polyisoprene added, as evidenced by corresponding changes in the loss factor. To a lesser extent, the effective useful temperature range over which the loss factor is increased also appears to be somewhat dependent upon the amount of 3,4-polyisoprene added. Suitable additional liquid rubbers or elastomers can be selected from among the following homo- and/or copolymers: polybutadienes, especially the 1,3- and 1,2-polybutadienes which may have terminal and/or pendant functional groups such as hydroxy-, carboxylic acid-, carboxylic anhydride-, or epoxy groups, polybutenes, polyisobutylenes, 1,4-polyisoprenes, styrene-butadiene-copolymers, butadiene acrylonitrile copolymers, polyurethanes and polyepoxides. The MW of the liquid rubbers is typically below 20000, preferably between 2000 and 10000. The amount of liquid rubbers in the composition depends upon the desired rheology of the uncured formulation and the desired mechanical properties and acoustic damping properties of the cured formulation. In general, the amount of liquid rubbers or elastomers varies from 5 to 50 percent by weight. Suitable solid rubbers, which usually have a significantly higher MW than the liquid rubbers (100000 or higher), include polybutadiene (preferably with high cis-1,4-content), styrene butadiene rubber, butadiene acrylonitrile rubber, isoprene rubber, butyl rubber and polyurethane rubber. Examples of thermoplastic polymers are polypropylene, polyethylene, thermoplastic polyurethanes, methacrylate copolymers, styrene copolymers and PVC. Fillers can be selected from a wide variety of materials including chalk, calciumcarbonate (natural ground or precipitated), silicates, barytes and carbon black. Also, flake type fillers such as vermiculite, mica, talc or similar layered silicates are suitable. In some formulations such flake type fillers have shown improved vibrational damping efficacy. The total amount of fillers can vary between 10 to 70 percent by weight, with the preferred range from 25 to 60 percent by weight. Tackifiers and/or adhesion promoters may include hydrocarbon resins, phenolic resins, terpene phenolic resins, modified or unmodified rosin acids and esters, polyamines, polyaminoamides, polyepoxy resins and anhydrides and anhydride-containing copolymers. The type and amount of tackifier(s) depends upon the polymer composition of the sealant/adhesive, the strength of the cured composition, and the substrate to which the sealant/ adhesive is applied. Typical tackifier resins such as the terpene phenolic resins or rosin derivatives are generally used in concentrations of 5 to 20 percent by weight, and preferably between 7 and 15 percent by weight. Typical adhesion promoters such as polyamines or polyaminoamides are normally used in the range from 0.5 to 10 percent by weight. A great number of products are suitable for use as plasticizers or extenders, including C 4 - to C 14 -dialkylesters of phthalic acid and C 4 - to C 14 -dialkylesters of C 3 - to C 8 -dicarboxylic acids, as exemplified by dioctyladipate, aliphatic, aromatic or naphthenic oils, low molecular weight polybutenes or polyisobutylenes, high boiling hydrocarbon fluids and mixtures thereof. The rheology of the uncured formulation and the mechanical properties including the vibration damping can be influenced to a certain extent by the amount of plasticizer and/or extender. Generally, plasticizer(s)/extender(s) are used in the range of 5 to 40 percent by weight. Appropriate curatives, accelerators or catalysts depend upon the reactive and/or functional groups of the polymers selected. The curatives may be selected from the group consisting of dicyanodiamide, carboxylic acid anhydrides, polyurethane catalysts and vulcanizing agents consisting of sulfur and/or an organic accelerator or accelerators. For curing the olefinic double bonds of liquid or solid rubbers, including 3,4-polyisoprene, a sulfur vulcanizing system is used. A variety of organic and inorganic accelerators can be used alone, or in combination with sulfur powder. Examples of these accelerators are mercaptobenzothiazoles, dithiocarbamates, sulfenamides, disulfides such as dibenzothiazole disulfide and/or thiuram disulfides, aldehyde amine accelerators, guanidines and metal oxides such as zinc oxide. In addition, other typical rubber vulcanizing agents such as fatty acids (e.g. stearic acid) may be present in the formulation. The amount of sulfur can vary widely from zero (in unvulcanized systems) to 15 percent by weight, preferably to 10 percent. Similarly, the amount of accelerator(s) can vary between zero and about 10 percent. The amount of metal oxides is in the range of zero to about 10 percent. Stabilizers may be used for protection against thermal, thermooxidative or ozone degradation. They can be selected from among conventional stabilizers such as sterically hindered phenols or amines. The amount of stabilizer used is usually in the range of 0.1 to 5 percent by weight. Although rheology is normally adjusted by the appropriate type and amount of fillers, conventional rheology improvers such as fumed silicas or bentonites can be present in the range of 0.1 to 7 percent by weight. In addition, other conventional additives may be present in the formulations. The acoustical damping efficacy of the compositions according to the present invention can be tailored to the specific needs of the application with respect to the maximum loss factor and the temperature range of the effective loss factor. The governing parameters are the vulcanizing system (amount of sulfur, amount of accelerator) and the rubbers incorporated. To a lesser extent, the fillers also influence the maximum loss factor and the corresponding temperature. In addition, the thickness of the applied material influences the damping factor, whereby foamed materials exhibit a higher damping factor, although this may not be applicable in cases where a high tensile strength is required for the adhesive. In most cases, it is desirable that the peak value of the loss factor should occur approximately at room temperature (about 20°C) and that a sufficiently high loss factor be achieved over a broad temperature range. The curing conditions for the adhesive/sealant compositions according to the invention can be tailored to the specific application; usually, the curing takes place at temperatures between 80°C and 240°C in 10 to 35 minutes. An additional enbodiment of the present invention is to provide for a method of joining and/or sealing joints between components by coating at least one surface of the components to be joined with an adhesive/sealant composition as disclosed above assembling the components heating the assembled and optionally clamped components to cure the sealant/adhesive composition. An other embodiment of the present invention is to provide for a method of coating components by spraying or extruding a composition as disclosed above onto the surface of the component and heating said coated component to cure the coating composition. Still an other embodiment of the present invention is a method of sealing and/or joining and/or coating joints and/or surfaces of components by applying a preextruded sheet, ribbon or tape made from compositions as disclosed above and optionally heating said component to cure the composition. The present invention may be further appreciated by reference to the following specific examples. As will be readily apparent to one skilled in the relevant art, these examples are illustrative of various parameters of the present invention except to the extent that any parameters shown in the examples may be incorporated into the appended claims. The damping property (dissipation or loss factor) in these examples was determined according to the Oberst method (DIN 53440) on steel strips which had been coated with a defined layer of the adhesive/sealant composition, followed by curing in a conventional laboratory oven. All parts given in the formulations below are parts by weight unless otherwise stated. Examples 1-5: The following components were thoroughly mixed in a Z-blade kneader: 1 2 3 4 5 3,4-polyisoprene 10 10 10 10 10 chalk 35 31.5 31 31 31 precipitated calciumcarbonate 24 25 25 25 24 terpene phenolic resin 10 10 10 10 10 naphthenic oil 5 5 5 5 5 polyisobutylene 15 15 15 15 15 antioxidant 1 1 1 1 1 calciumoxide 0 1 1 1 1 zinc oxide, active 0 1 1 1 1 sulfur powder 0 0 0.5 0 1.0 Dibenzothiazole disulfide (MBTS) 0 0.5 0.5 1.0 1.0 Lap shear strength (MPa) 0.06 n.a. n.a. n.a. 1.2 Comparative example 1 A PVC plastisol was prepared by mixing the following components: paste grade emulsion PVC 32.0 dioctylphthalate 30.0 natural ground chalk 16.5 precipitated calciumcarbonate 6.0 calciumoxide 3.0 metal oxides (colour pigments) 1.0 carbon black 0.1 stabilizer 1.0 adhesion promoter 2.0 fumed silica 0.4 hydrocarbon extender 8.0 Example 6 and comparative example 2 (Comp.2) The following ingredients were thoroughly mixed in a Z-blade kneader. Comp.2 6 7 solid rubber 2.7 - - 3,4-polyisoprene - 5.0 10.0 liquid polybutadiene 8.9 8.9 7.0 liquid polybutadiene 17.8 15.5 12.0 carboxylated polybutadiene 8.9 8.9 - benzylated polybutadiene - - 8.0 precipitated calciumcarbonate 12.1 12.1 12.1 chalk 12.1 12.1 12.0 talc 18.6 18.6 21.0 calciumoxide 5.6 5.6 5.5 carbon black 0.5 0.5 0.1 antioxidant 0.5 0.5 0.5 zinc oxide, active 4.3 4.3 4.0 sulfur powder 3.0 3.0 2.5 Dibenzothiazole disulfide (MBTS) 5.0 5.0 5.3 Lap shear strength (MPa) 1.4 1.5 1.2/1.8 Acoustic Damping Properties Spring steel strips 240 mm x 10 mm, 1mm thick were coated on a 200 mm long section with a layer of the compositions described in examples 1 to 6 and comparatative examples 1 and 2. The coating thickness is given below. The coated steel strips were cured in a laboratory oven for 30 min at 190°C, unless otherwise stated. The cured strips were subsequently submitted to a bending vibration test according to DIN 53440 (Oberst-Method). As can be seen from figures 1 to 3, the compositions containing 1,4-polyisoprene exhibit a significant damping factor at normal service temperatures (-10°C to 30°C), moreover, examples 2 to 5 demonstrate clearly, that by slightly changing in the vulcanizing system, one can optimize the temperature range of maximum loss factor to the desired region. Example 6 and 7 demonstrate that incorporation of 3.4-polyisoprene into conventional vulcanizing rubber sealant/adhesives (comparatative example 2) improves the damping factor of the cured sealant/adhesive significantly without sacrificing on the shear strength property. Also, example 7 shows clearly that a higher curing temperature increases the shear strength of the cured adhesive although one probably might expect this. But surprisingly, also the vibration damping as measured by the Oberst method is increased, in addition this increased damping factor is observed over a broader temperature range compared to the same formulation cured at the lower temperature, see curve 14 vs curve 15 of figure 3. Explanation of Figures 1 to 3 Figures 1 to 3 show graphs of the combined loss factor at 200 Hz of the coated steel strips versus temperature according to DIN 53440 part 3. The test samples were prepared as described above. Most of the samples have been prepared at two different coating thicknesses to compensate for normal thickness deviations between different formulations. Fig. 1 shows the loss factor of a conventional PVC-plastisol from comparative example 1 ( 1,2 ) versus a composition according to example 1 ( 3,4 ). curve formulation coating thickness 1: comp. example 1, 2.27 mm 2: comp. example 1, 4.52 mm 3: example 1, 2.2 mm 4: example 1, 4.5 mm. Fig. 2 illustrates how the factor and the temperature range over which a significant loss factor is observed (loss factor > 0.1) can be varied by slight changes in the composition of the vulcanizing agents. curve formulation coating thickness 5: example 2, 2.0 mm 6: example 2, 2.45 mm 7: example 3, 2.6 mm 8: example 3, 3.5 mm 9: example 4, 2.0 mm 10: example 4, 2.65 mm 11: example 5, 4.8 mm. Fig. 3 shows that the loss factor of a conventional vulcanized rubber composition of comparative example 2 is insignificant at normal service temperatures of a car (-5°C to 30°C) whereas the compositions of the inventive examples 6 and 7 have a significant loss factor at the normal service temperatures: curve formulation coating thickness 12: example 2 3.0 mm 13: example 6 3.1 mm 14: example 7 2.3 mm 15: example 7 2.3 mm 16: example 7 4.4 mm. Note: Samples of curves 15 and 16 were been cured for 30 min at 200°C whereas sample of curve 14 was cured for 30 min at 170°C. All sealant/adhesive formulations of examples 1 to 7 had in addition to their superior damping properties the necessary properties for use as sealant/adhesive for body shop applications in the automotive industry.

Claims: Curable compositions for use as sealants, adhesives or coatings consisting of 5 to 40% by weight of 3,4-polyisoprene, at least one curative and at least one of the following: additional liquid or solid rubber(s) or elastomers, finely divided polymer powders, fillers, curatives, adhesion promoters, plasticizers, liquid extenders, tackifiers, accelerators, catalysts, stabilizers, antioxidants and rheology improvers. Compositions according to claim 1 wherein the liquid and/or solid rubbers are selected from the group consisting of homo- and/or copolymers of polybutadienes, 1,4-polyisoprenes, polyisobutylenes, polybutenes, styrene-butadiene-rubber, polyurethanes and polyepoxides. Compositions according to claim 1 wherein the curatives are selected from the group of vulcanizing agents consisting of sulfur and/or an organic accelerator or accelerators, Dicyanodiamide, carboxylic acid anhydrides and polyurethane catalysts. Compositions according to claim 1 wherein the plasticizers and/or liquid extenders are selected from the group consisting of C 4 - to C 14 -dialkylesters of phthalic acid or C 3 - to C 8 -dicarboxylic acid, aliphatic, aromatic or naphthenic oils, low molecular weight polybutenes or polyisobutylenes and high boiling hydrocarbon fluids. Compositions according to claim 1 wherein the adhesion promoter or adhesion promoters is/are selected from the group consisting of hydrocarbon resins, modified or unmodified rosin acid or rosin esters, phenolic resins, terpene phenolic resins, epoxy resins, polyaminoamides, polyaminoethers or polymeric and monomeric anhydrides of carboxylic acids. A method of joining, and/or sealing joints between components characterized by coating at least one surface of the components to be joined with the adhesive/sealant composition of any of the preceeding claims assembling the components heating the assembled and optionally clamped components to cure the sealant/adhesive composition. A method of coating components by spraying or extruding a coating composition according to at least one of the claims 1 to 5 onto the surface of the component and heating the coated component to cure the coating. A method of sealing and/or joining and/or coating joints and/or surfaces of components by applying a preextruded sheet, ribbon or tape made from compositions according to at least one of the claims 1 to 5 and optionally heating said component to cure the composition.

Inventors: LANOYE THIERRY, LANOYE, THIERRY
Applicants: HENKEL KGAA, HENKEL KOMMANDITGESELLSCHAFT AUF AKTIEN
Application year: 1993
Main classification: C08L9
IPC codes: C09J5, C09J7, C08L21, C09J109, C09D121, C08L9, C09D109