THERMALLY INSULATING MULTIPANE GLAZING STRUCTURE

Abstract: Multipane, insulating glazing structures having exceptional thermal insulation performance are provided. The multipane structures comprise two substantially parallel rigid glazing sheets (12, 18) spaced apart by an interior spacer (20) which includes a physically stable body (22) of low thermal conductivity, closed cell, foamed polymer.

Description: THERMALLY INSULATING MULTIPANE GLAZING STRUCTURE Technical Field The present invention relates generally to multipane glazing structures, and more particularly relates to the use of thermally insulative spacers in novel multipane glazing structures which have exceptional thermal insulation performance. The invention also relates to the interpane spacers. Background Multipane glazing structures have been in use for some time as thermally insulating windows, in residential, commercial and industrial contexts. Examples of such structures may be found in U.S. Patent Nos. 3,499,697, 3,523,847 and 3,630,809 to Edwards, 4,242,386 to Weinlich, 4,520,611 to Shingu et al. , and 4,639,069 to Yatabe et al. While each of these patents relates to laminated glazing structures which provide better insulation performance than single-pane windows, increasing energy costs as well as demand for a superior product have given rise to a need for windows of even higher thermal insulation ability. A number of different kinds of approaches have been taken to increase the thermal insulation performance of windows. Additional panes have been incorporated into a laminated structure, as disclosed in several of the above-cited patents; typically, incorporation of additional panes will increase the R-value of the structure from R-l for a single-pane window to R-2 for a double laminate, to R-3 for a structure which includes 3 or more panes (with "R-values" defined according to the insulation resistance test set forth by the American Society for Testing and Materials in the Annual Book of ASTM Standards) . Southwall Technologies Inc., the assignee of the present invention, has promoted such a triple-glazing structure which employs two glass panes containing an intermediate plastic film. Such products are described, for example, in U.S. Patent No. 4,335,166 to Lizardo et al. In multiplane structures two or more glazing panes are positioned in a spaced parallel relationship to one another by reason of spacers located at the periphery of the glazing panes. An effective spacer should have structural integrity and a substantial level of crush strength so as to allow a dimensionally stable window unit to be formed. Spacers used heretofore have ranged from solid or open metal or plastic constructs to hollow metal, plastic, or composite tubes of circular, rectangular or irregular cross-sections, with continuous or discontinuous peripheries. Hollow spacers are often filled with desiccant to minimize interpane water content and condensation problems in the inner surface of the panes. Examples of spacers in the art include U.S. Patent Nos. 3,935,351 to Franz, 4,120,999 to Chenel et al., 4,431,691 to Greenlee, 4,468,905 to Cribben, 4,479,988 to Dawson and 4,536,424 to Laurent relate to spacers for use in multipane window units. In this application's commonly assigned parent, United States Patent Application Serial No. 389,231, filed 2 August 1989, it is disclosed that a closed-cell polymer foam spacer can be employed to an advantage as a spacer in multipane windows and especially in high performance, gas-filled quadruple-pane glazing structures. References to spacers made from other types of foams include U.S. Patent Nos. 4,563,843 to Grether et al. and 4,831,799 to Glover et al. * As higher and higher R values are demanded from multipane window units, there is an increasing need to minimize or at least reduce the conduction of heat through the edge spaces whenever possible. This invention addresses this need. Despite the increasing complexity in the design of insulating window structures, total window R-values have not surpassed 4 or 5. While not wishing to be bound by theory, the inventors herein postulate several reasons for the limited insulating performance of prior art window structures: (1) thermal conductance across interpane spacers as discussed above present at the window edge; (2) thermal conductance within and across the edge sealant; and (3) the impracticality, due to considerations of window weight and thickness, of having a large number of panes in a single glazing structure. The present invention addresses each of the aforementioned problems and thus provides a novel multipane window structure of exceptionally high thermal insulating performance. In addition to insulating performance, the following characteristics are extremely desirable in a window structure and are provided by the present invention as well: -durability under extremes of temperature; -resistance of internal metallized films to yellowing; -resistance to condensation, even at very low temperatures; -low ultraviolet transmission; and -good acoustical performance, i.e., sound deadening within the multilaminate structure. Citation of Prior Art In addition to the references noted in the preceding section, the following patents and publications relate to one or more aspects of the present invention. Multipaned glazing units: U.K. Patent Application Publication No. 2,011,985A describes a multiple glazed unit containing one or more interior films. The unit may in addition include sound damping materials and a gas filling. U.S. Patent No. 4,687,687 to Terneu et al. describes a structure containing at least one sheet of glazing material coated with a layer of a metallic oxide. U.S. Patent No. 2,838,809 to Zeolla et al. is a background reference which describes multiple glazing structures as windows for refrigerated display cases. U.S. Patent Nos. 4,807,419 to Hodek et al. and 4,815,245 to Gartner also relate to multiple pane window units. Heat-reflective, low-emissivity ("low e") coatings have been incorporated into one or more panes of a window structure, increasing the R-value to 3.5 or higher. Such a heat-reflective coating is described, for example, in U.S. Patent No. 4,337,990 to Fan et al. (which discloses coating of a plastic film with dielectric/metal/dielectric induced transmission filter layers) . Window structures which include heat-reflective coatings are described in U.S. Patent Nos. 3,978,273 to Groth, 4,413,877 to Suzuki et al. , 4,536,998 to Matteucci et al., and 4,579,638 to Scherber. Still another and more recent method which has been developed for increasing the thermal insulation performance of windows is the incorporation, into the window structure, of a low heat transfer gas such as sulfur hexafluoride (as described in U.S. Patent No. 4,369,084 to Lisec) , argon (as described in U.S. Patent Nos. 4,393,105 to Kreisman and 4,756,783 to McShane) , or krypton (also as disclosed in McShane '783). These gas- filled laminated windows are reported to have total window R-values of 4 or 5, with the total window R-value approximating the average of the center-of-glass and edge area R-values (Arasteh, "Superwindows", in Glass Magazine, May 1989, at pages 82-83). U.S. Patent Nos. 4,019,295 and 4,047,351 to Derner et al. disclose a two-pane structure containing a gas filling for acoustic insulation purposes. U.S. Patent No. 4,459,789 to Ford describes a multi-pane, thermally insulating window containing bromotrifluoromethane gas within the interpane spaces. U.S. Patent No. 4,604,840 to Mondon discloses a multipane glazing structure containing a dry gas such as nitrogen in its interpane spaces. U.S. Patent No. 4,815,245 to Gartner, cited above, discloses the use of noble gases to fill interpane spaces. Sealants: U.S. Patent Nos. 3,791,910 to Bowser, 4,334,941 and 4,433,016 to Neely, Jr., and 4,710,411 to Gerace et al. describe various means for sealing multipane window structures. Summary of the Invention It is a primary object of the invention to address the above-noted deficiencies of the prior art and thus to provide a multipane window structure of exceptionally high thermal insulation performance. It is still another object of the invention to provide a novel interior (i.e., interpane) spacer for use in multipane window structures. Additional objects, advantages and novel features of the invention will be set forth in part in the description which follows, and in part will become apparent to those skilled in the art upon examination of the following, or may be learned by practice of the invention. In one aspect of the invention, a multipane glazing structure comprises at least two substantially parallel sheets of glazing held in spaced relationship to each other by a peripheral spacer, said spacer comprised of a closed cell foamed polymer having a thermal conductivity of less than about 0.12 w/(M x °C) which equals 0.8 BTU/(hr x ft 2 x °F/in) , as measured by ASTM Test C518. The closed cell foam element in the spacer provides a thermal break across the spacer. In this aspect, the closed cell foam element can be accompanied by an additional spacer element such as a conventional spacer, for example, a hollow tube, a solid body, an irregularly shaped spacer, or the like. In other aspects of the invention, multipane glazing structures are provided with a foam spacer as above, and further can include a peripheral seal surrounding and enclosing the outside edges of the glazing sheets and the spacers, additional sheets of glazing in parallel orientation, gas filling of the space between the parallel sheets, and the like. The peripheral seal can comprise (a) a layer of curable sealant adhered to the edges of the sheets of glazing and to the outer surface of the spacers, and (b) a continuous gas-impermeable tape adhered to and overlaying the layer of sealant. In a preferred embodiment, the polymeric foam spacer extends beyond the edges of the glazing sheets to the exterior tape so as to provide a thermal break within the sealant. Description of the Figures This invention will be further described with reference being made to the accompanying drawings. In these drawings, common numbering for common elements will be used from figure to figure. In the drawings, Figure 1 is a schematic cross- sectional representation of one multipane glazing structure of this invention. Figures 2-9 each are schematic cross-sectional views of additional embodiments of the multipane glazing structure of this invention. Figure 10 is a perspective end view of a foam- containing spacer of this invention. Figures 11-13 each are schematic cross- sectional views of additional typical foam-containing spacers of this invention. Detailed Description of the Invention The glazing structures of the invention include two substantially parallel rigid sheets of glazing spaced apart from each other by a peripheral polymeric spacer. Turning now to Figure 1, a multipane window structure according to the invention is shown generally as 101. The multipane structure 101 contains three distinct, substantially parallel glazing sheets 12, 16 and 18 spaced apart from one another by spacers 20, 22 and 24. Spacer 22 is a closed cell polymeric foam spacer having a thermal conductivity of less than 0.12 w/(M x °C) that is 0.8 BTU/ (hr x ft 2 x °F/in) . The first and third glazing sheets 12 and 18, which represent the exterior panes of the structure, can be of a rigid plastic material such as a rigid acrylic or polycarbonate, but more commonly these sheets are glass. Depending on architectural preference, one or both of these exterior panes can be coated, tinted or pigmented. This can be done to enhance appearance, to alter light- transmission properties, to promote heat rejection, to control ultraviolet transmission, or to reduce sound trans ission. Bronze, copper or grey tints are often applied to the outer of the two glass panels. The outer glazing sheets 12 and 18 can also be of a special nature, e.g., laminated, tempered, etc. Typically, the thickness of these outer sheets will be in the range of about 0.15cm (1/16") to about 0.3cm (1/4"). Interior glazing sheet 16 is shown as a flexible plastic sheet, although, like the outer glazing sheets, it can also be comprised of glass or coated glass. If plastic, the material should be selected so as to have good light stability so that it will withstand the rigors of prolonged sun exposure. This plastic should also be selected so as not to be substantially susceptible to outgassing, which could lead to deposits on the inner surfaces of the glass layers and interfere with optical clarity. Polycarbonate materials and the like can be used, but there is a preference for the polyesters, such as polyethylene terephthalate (PET) . These interior plastic films are relatively thin as compared with other typical window-film materials. Thicknesses above about 0.002cm (1 mil or 0.001") are generally used, with thicknesses in the range of about 2 mil to about 25 mil being preferred and thicknesses in the range of about 2 mil to 10 mil being more preferred. It is preferred that the interior glazing sheet 16 be provided with one or more apertures 15 to enable equalization of pressure between the interpane gas spaces. Such apertures also allow desiccant present in the interior of spacers 26 and 28 to absorb vapor from space 38 as well as from space 42. In embodiment 101, the interior glazing sheet 16 is coated on one of its sides with heat-reflective layers as known in the art (element 16a, in Figure 1) and as exemplified in U.S. Patent No. 4,337,990 to Fan et al., cited hereinabove. Two or more such heat reflective layers may be used but commonly only one such coating is present. Such coatings can be designed to transmit from about 40% to about 90% of the visual light impacting them. It is preferred to use as such coatings a dielectric/metal/dielectric multilayer induced transmission filter as described in commonly assigned U.S. Patent No. 4,799,745, issued January 24, 1989. These layers can be laid down by magnetron sputtering techniques which are known to the art. Southwall markets a range of induced transmission heat reflective film products under its HEAT MIRROR trademark. These materials have various thicknesses of metal (often silver) sandwiched between layers of dielectric and are designed to give substantial heat reflection and typically transmit from about 10 to 90% of total visible light. Reflector 16a can be on either or both sides of film 16. It may be eliminated if desired. Spacers 20 and 24 may be selected from a wide variety of commercially available materials. These spacers are typically metallic, plastic, or composite (i.e., plastic plus fiberglass, plastic plus metal) or the like, as is well known in the art. Spacers 20 and 24 are generally fabricated so as to have hollow interiors 26 and 28 containing desiccant in order to prevent build- up of moisture between the layers. The desiccant may or may not be present within the interior spacers 26 and 28. The spacer structures 20 and 24 of Figure l are merely representational; generally rectangular or square cross- sections will be employed. The exact shape of the spacers 20 and 21 can vary substantially. In addition to the irregularly shaped but hollow structure shown in Figure 1, other structures such as a U-shaped or double- U-shaped cross-section material can be employed, as well as other spacers known in the art. As noted above, spacer 22 is comprised of a closed cell foam polymer having a thermal conductivity of less than about 0.12 w/ (M x °C) that is 0.8 BTU/ (hr x ft 2 x °F/in) , preferably less than about 0.08 w/ (M x °C) that is 0.5 BTU/(hr x ft 2 x °F/in) , most preferably less than about 0.03 w/(M x °C) that is 0.2 BTU/ (hr x ft 2 x °F/in) . The closed cell foam material should be firm with a compressive strength of at least about 100 psi; to this end, the material preferably has a density of at least about 3.0 lb/ft 3 , typically in the range of about 3.0 to about 6.0 or 7.0 lb/ft 3 and could range from 3.0 to 25 lb/ft 3 . The material should not be such that it outgasses significantly, and should, in general, be chemically and physically stable. Exemplary materials for use as interior spacer 22 include foamed polyurethanes, foamed polycarbonate, foamed polyvinyl chloride (PVC) modified so as to prevent outgassing (e.g., using a steam process as known in the art), or synthetic thermoplastic poly(phenylene oxide) resins manufactured by the General Electric Corporation. Closed cell PVC materials which make excellent spacers are available commercially, as well. In the embodiment 101, in Figure 1, closed cell foam spacer 22 extends all the way to the outer periphery of the glazing unit, thus providing a thermal break across the edge seal. Commonly, the thickness of the spacer materials is controlled; for example, in Figure 1 the overall thickness of the glazing unit should commonly be kept to below about 5 cm (2 inches) , preferably below about 4 cm (1.5 inches), and more preferably at about 2.5 cm (1 inch) or below. Thus, the space between glazing elements 16 and 12 should range from about 4 cm (1.5 inches) to about 1 cm (3/8 inch) . In this spacing, the thickness of foam layer 22 should be at least about 0.3 cm (1/8 inch) , but not the entire distance between a pair of glazing surfaces. As illustrated in Figure 1 and Figure 9 and Figure 10, foam spacer 22 can occupy from about 10% of the space between a pair of glazing layers up to and including as much as 75 or 80% or more. In commonly owned United States Patent No. 5,156,894, additional embodiments are shown where a foam spacer spans the entire distance between a pair of glazing sheets. Typical thicknesses, measured in the glazing sheet-to- glazing sheet direction for the foam spacer 22 range from about 0.1 cm (1/16 inch) to about 2 cm (3/4 inch), and especially from about 0.2 cm (1/8 inch) to about 1.2 cm (1/2 inch) . As shown in Figure 10, it is preferred that the exposed surfaces of the foam 60 of spacer 22 be covered by metal foil or metallized film 62 to ensure that gas loss through the spacer is minimized and to protect the spacer from ultraviolet rays. Film 62 is typically comprised of aluminum, silver, copper or gold deposited on a polyester or other polymeric substrate. Generally, metallized film 62 will have a thickness in the range of 0.5 to 3 mil. Other coatings which achieve these advantages can be used as well. Interpane voids 38, 40 and 42 which result from the spacing apart of the three glazing sheets are filled with a gas selected to reduce heat conductance across the window structure. Virtually any inert, low heat transfer gas may be used, including krypton, argon, sulfur hexafluoride, carbon dioxide, or the like, at essentially the atmospheric pressure prevailing at the location of use of the window unit. It is particularly preferred that the gas filling have a high krypton content, of at least about 10%, more preferably at least about 25%, most preferably at least about 50%, depending on the thickness of the window structure (thicker windows with thicker voids would not typically employ as high a krypton content as a thinner window) . It is also preferred that the filling gas contain some appreciable amount of oxygen (preferably in the range of about 1% to 10% by volume, more preferably in the range of about 2% to 5% by volume) . Incorporation of oxygen into the filling gas tends to prevent or minimize yellowing of the interior plastic glazing sheet 16. Sealant 44 is present between glazing sheets 12 and 18 at their edges. This sealant should be a curable, high-modulus, low-creep, low-moisture- vapor-transmitting sealant. It should have good adhesion to all of the materials of construction (i.e., metal or plastic, glass, metallized interior films, and the like) . Polyurethane adhesives, such as the two-component polyurethanes marketed by Bostik, are very suitable. These adhesives are merely representative, and the invention is not limited to the use of these adhesives, particularly in constructions where no film glazing, such as 16 in Figure 1, is employed. The peripheral seal of window structure 101 is formed both by sealant 44 and by continuous layer 46 of a gas-impermeable tape which adheres to and overlays the sealant. The tape is preferably comprised of a multilayer plastic packaging material which acts as a retaining barrier for the gas filling in the window structure. The tape is of a material selected so as to be hydrolytically stable, resistant to creep, and, most importantly, highly resistant to vapor transmission. Exemplary materials useful as tape 46 include metal- backed tapes in general as well as butyl mastic tapes, mylar-backed tapes, and the like. It is particularly preferred that the adhesive component of the tape be a butyl adhesive. The thickness of the sealing tape is preferably in the range of about 5 to 30 mils, more preferably in the range of about 10 to 20 mils. The peripheral seal formed by the curable sealant/gas-impermeable tape system ensures that there is virtually no gas leakage from the window, on the order of 1% per year or less. This is in contrast to prior art methods of sealing gas-filled glazing structure, which can result in gas leakage as high as 20% to 60% per year. As may be deduced from Figure 1, thermal conductivity across the window structure may occur in three regions: across the central portion 32 of the window; across the metallic edge spacers, identified as region 34 in the Figure; or through the very edge of the structure, across the sealant (identified as region 36 in the Figure) . The use of multiple panes, reflective coatings and gas fill reduces the conductivity in the 32 region and the closed cell foam spacer of the present invention reduces the thermal conductivity in all regions 34 and 36, and thus improves insulation performance while significantly reducing the problem of condensation. With respect to region 34, conductivity across the exterior metallic spacers is significantly reduced by the presence of foam spacer 22 which has, as noted above, very low conductivity. With respect to region 36, conductivity across sealant 44 is significantly reduced by foam spacer 22, which, as shown, extends to the very edge of the glazing structure so that its "end" extends beyond the edges of the interior glazing sheets and is aligned with the edges of exterior sheets 12 and 18. Extension of interior spacer 22 in this way provides virtually complete thermal break at the edge of the glazing structure so as to substantially reduce thermal conductivity across and through the sealant 44. This aspect of the invention can significantly improve insulation performance and resistance to condensation. Alternative structures for the foam spacer containing windows of this invention are illustrated in Figures 2-9. In all of these structures, and in the structure depicted in Figure 1, either of the panes 12 and 18 may face outward into the environment with the other facing inward, into the room. In Figure 2, glazing structure 102 is shown. It is similar to structure 101 just described but employs a foam spacer 22 which does not extend all the way through seal 44 to the outside edge of the structure. This configuration may be somewhat less efficient than that of structure 101 but may offer manufacturing advantages. Structure 103, shown in Figure 3, is similar to structure 101 and 102 but it lacks the exterior sealant film 46. This can be done when the window structure is not gas filled so that there is no concern about gas leakage from the unit. It also can be used if a gas- impermeable seal 44 is employed. Structure 104, shown in Figure 4 shows an additional simplification structure 103 in which the interim film 16 is omitted. Removing interim film 16, particularly with its heat reflective layer 16a, does decrease the thermal performance of the overall window unit but it does not reduce the effectiveness of the foam spacer 22 of the invention. Structure 106, shown in Figure 5 is a variation in structure 104 in that it includes foam spacer 22 but also optionally includes outer seal 46 which, as already discussed, facilitates the use of gas filling in the unit by sealing the unit and preventing gas leakage. Structure 107 in Figure 6 illustrates another way to achieve a gas tight seal using the closed cell foam spacer in a window. In structure 107 a gas impermeable sealant such as polyisobutylene is applied as layers 50, 52 and 54 at each of the points at which gas could enter or leave the unit around or through the spacer. This use of seal 50, 52 and 54 eliminates outer seal 46 and is quite durable since the seals are shielded from possible tearing or the like. As illustrated by structure 110 shown in Figure 7, foam spacer 22 need not be "centered" in the glazing unit but may be located "off center." Structure 110 is equivalent to structure 101. Figures 8 and 9 show structures 111 and 112, respectively, each of which are simplified applications of the closed cell foam spacer in window units. In structures 111 and 112, the interior film has been eliminated as in structures 104-107. In structures 111 and 112, the closed cell foam is paired with a single rigid spacer 20. The thickness of the closed cell foam 22 and the spacer 20 can be varied, as shown in Figures 8 and 9, to achieve the overall void thickness desired for thermal break properties. The structures of Figures 8 and 9 can be further varied such as by including an outer sealing tape or internal seals and gas fill, or by varying the width of the foam seal to extend through sealant 44 to the outer edge of the structure. The foam-containing spacers themselves are an aspect of this invention. They can be supplied to the trade in the configuration shown in Figure 10 (with or without film 62) or they can be supplied in combination with one or more non-foam spacer as shown in Figures 11- 14. Figure 11 shows a spacer 114 which includes the closed cell foam spacer 22 adhered to one of the "pane- abutting" surfaces of nonfoam (metal on plastic) spacer 20, shown with interior space 26. In Figure 12 an alternative embodiment 115 is given made up of spacer 20 and 22 and with a second non- foam body 24 adhered to the foam body 22. Spacer 115 additionally depicts a protective layer 62 (film, foil or coating) as shown in Figure 11. It will be noted that in this embodiment layer 62 is on the side of spacers 22, 24 and 26 which typically contacts the outer sealant (44 in Figure 1) . Figure 13 is similar to Figure 12. It shows an embodiment where the protective layer 62 is on the side of spacers 22, 24 and 26 which 5 typically faces "into" the window structure. As these various figures show, the space between a given pair of glazing sheets is spanned by the combination of a closed cell foam element 22 and a nonfoam spacer element 20. As these figures show, the foam element can comprise from a small part of this distance to a substantial part. Manufacturing method: In a typical mode of production, the window structures of the invention are assembled using adhesive, such as double-sided adhesive tape or hot-melt adhesive, to bond the various layers and spacers into their desired configuration. For example, in the case of structures 101-103, the manufacturing method could involve first affixing inner glazing sheet 16 coated with heat-reflecting film 16a to spacer 24 using double-sided adhesive tape. Spacers 20 and 24 are hollow and contain desiccant. Outer glass panes 12 and 18 are joined to their respective outer spacers 20 and 24, again with double-sided tape, to give a glass-spacer- film, and glass-spacer subassemblies. These two subassemblies are then joined using foam spacer 22 and additional adhesive tape, so that the pane edges are aligned. The edge of foam spacer 22 extends out beyond the edges of sheet 16 and is aligned with the edges of the outer panes 12 and 18 as shown in Figure 1. Sealant 44 is introduced at the pane edges and allowed to cure; at this point the window units are subjected to a heat treatment. Typically, temperatures in the range of about 80°C to about 120°C are used. The heating period is generally about 30 minutes, although longer times are required at lower temperatures, and shorter times may be sufficient at higher temperatures. This heat treatment serves to cure the sealant 44 and shrink the internal plastic films 14 and 16 to a taut condition. Interpane gas spaces are then filled. The method of filling the structures with gas should be such that efficiency is maximized and gas loss is minimized. In a particularly preferred method of introducing the filling gas, delivery is carefully controlled, i.e., a timing device is used and the flow rate monitored so that filling will be stopped at a given volume. The gas fill mix is adjusted depending on the thickness of the window structure and on the desired R-value and introduced into the interpane gas structures using the desired method. The structure is re-sealed as above. The selected barrier tape 46 is then applied over the pane edges and sealant as illustrated in Figure 1. Similar production sequences will be used to prepare the other structures having the foam spacers of this invention. In another manufacturing method the several parts of the spacer such as spacer 114, 115 or 116 can be first assembled. This subassembly, which can be sold preassembled is then employed as a unit. It is to be understood that while the invention has been described in conjunction with the preferred specific embodiments thereof, that the foregoing description as well as the example which follows is intended to illustrate and not limit the scope of the invention. Other aspects, advantages and modifications within the scope of the invention will be apparent to those skilled in the art to which the invention pertains. Experimental Edge R-values were measured for several different multipane window structures, approximately 1" thick, fabricated as described in the preceding sections, except that the composition of the interior spacer was varied. A polyvinyl chloride spacer gave an edge R-value of 1.38 BTU/(hr x ft 2 x °F/in) , while a hollow aluminum spacer, an extruded butyl spacer, and a hollow fiberglass spacer gave edge R-values of 0.37, 0.56 and 0.68 BTU/ (hr x ft 2 x °F/in) , respectively. As expected, the foamed polyvinyl chloride spacer, having a much lower thermal conductivity, gave the highest edge R-value.

Claims: Claims : l. A multipane window glazing structure comprising two substantially parallel sheets of glazing held in spaced relationship to each other by a peripheral spacer, said spacer comprised of a body of physically stable closed cell foam polymer spacers having a thermal conductivity of less than about 0.8 BTU/ (hr x ft 2 x °F/in) sized to provide a thermal break across the spacer. 2. The multipane window glazing structure of claim 1, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.5 BTU/(hr x ft 2 x °F/in) . 3. The multipane window glazing structure of claim 1, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.2 BTU/ (hr x ft 2 x °F/in) . 4. The structure of claim 1, wherein the polymer is selected from the group consisting of foamed polycarbonate, polyurethane, polyphenylene oxide and polyvinyl chloride. 5. The structure of claim 4 wherein the polymer has a density of from about 3.0 lb/ft 3 to about 25 lb/ft 3 . 6. A multipane window glazing structure comprising two substantially parallel sheets of glazing held in spaced relationship to each other by a peripheral spacer, said spacer comprised of a body of a physically stable closed cell foam polymer having a thermal conductivity of less than about 0.8 BTU/ (hr x ft 2 x °F/in) adhered to at least one additional spacer element not formed of closed cell foam polymer, said at least one additional spacer element and said closed cell foam body together sized to substantially span the spaced relationship. 7. The multipane window glazing structure of claim l, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.5 BTU/(hr x ft 2 x °F/in) . 8. The multipane window glazing structure of claim 1, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.2 BTU/(hr x ft 2 x °F/in) . 9. The structure of claim 1, wherein the polymer is selected from the group consisting of foamed polycarbonate, polyurethane, polyphenylene oxide and polyvinyl chloride. 10. The structure of claim 4 wherein the polymer has a density of from about 3.0 lb/ft 3 to about 25 lb/ft 3 . 11. The structure of claim 6 wherein the body of nonclosed cell foam material is a spacer having a hollow cross-section tubular structure. 12. The structure of claim 6, wherein the sheets of glazing are rigid sheets of glass or plastic. 13. The structure of claim 1 wherein one of the two sheets of glazing is a flexible plastic film and the other is a rigid sheet of glass or plastic. 14. The structure of claim 7, wherein the flexible plastic film carries a wavelength-selective, reflective coating on one of its surfaces. 15. The structure of claim 7, wherein the flexible plastic film is comprised of polyethylene terephthalate. 16. The structure of claim 8, wherein the plastic film is comprised of polyethylene terephthalate. 17. A multipane glazing structure, having two substantially parallel sheets of rigid glass or plastic glazing held in spaced relationship to one another by peripheral spacers wherein at least one of said spacers comprises a body of physically stable closed cell foam polymer having a thermal conductivity of less than about 0.8 BTU/(hr x ft 2 x °F/in) and at least one hollow cross- section tubular structure, said tubular structure and said body disposed between adjacent sheets and sized to hold the adjacent sheets in said spaced relationship. 18. The multiplane glazing structure of claim 11, additionally comprising a peripheral seal surrounding and enclosing the edges of said sheets and the spacers, said peripheral seal comprising (a) a layer of curable sealant adhered to the edges of the sheets of glazing and to the outer surface of the spacers, and (b) a continuous gas-impermeable tape adhered to and overlaying said layer of sealant. 19. The multipane glazing structure of claim 12, wherein the sealant is a polyurethane. 20. The multipane glazing structure of claim 12, wherein a gas selected to reduce heat transfer is contained and enclosed within said structure. 21. The multipane glazing structure of claim 14, wherein said gas is selected from the group consisting of krypton, argon, sulfur hexafluoride, carbon dioxide, and mixtures thereof. 22. The multipane glazing structure of claim 14, wherein said gas further contains oxygen in an amount of about 1.0 to 10% by volume. 23. The multipane window glazing structure of claim 11, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.5 BTU/(hr x ft 2 x °F/in) . 24. The multipane window glazing structure of claim 11, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.2 BTU/(hr x ft 2 x °F/in) . 25. The multipane glazing structure of claim 11, wherein the closed cell foam polymer is selected from the group consisting of foamed polycarbonate, polyurethane, polyphenylene oxide, and polyvinyl chloride. 26. The multipane glazing structure of claim 19, wherein the polymer has a density of at least about 3.0 lb/ft 3 . 27. A multiplane glazing structure, said structure having three distinct, substantially parallel glazing sheets, each spaced apart from the others by peripheral spacers, wherein the first and third of said sheets being rigid glass or plastic and representing the exterior faces of said structure, and wherein the second of said sheets is a flexible transparent plastic sheet and is contained on the interior of said structure, said first and second sheets being separated from one of the outer sheets by another by a spacer comprised of a body of physically stable closed cell foamed polymers having a thermal conductivity of less than about 0.8 BTU/ (hr x ft 2 x °F/in) and at least one hollow cross-sectional tubular structure, said tubular structure and said body of foamed polymer together disposed between said first and second sheets to hold the first and second sheets in spaced rela ionship. 28. The multipane glazing structure of claim 21, additionally comprising a gas selected to reduce heat conductance contained between said first and third sheets; and a peripheral seal surrounding and enclosing the edges of the sheets of glazing and the spacers, said seal comprising a layer of curable sealant adhered to the sheets of glazing and the outer surface of the spacers, and a continuous gas-impermeable tape adhered to and overlaying the layer of sealant. 29. The multipane glazing structure of claim 22, wherein the sealant is a polyurethane. 30. The multipane glazing structure of claim 22, wherein said gas is selected from the group consisting of krypton, argon, sulfur hexafluoride, carbon dioxide, and mixtures thereof. 31. The multipane glazing structure of claim 24, wherein said gas further contains oxygen in an amount of about 1.0 to 10% by volume. 32. ~ The multipane window glazing structure of claim 21, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.5 BTU/(hr x ft 2 x °F/in) . 33. The multipane window glazing structure of claim 21, wherein the thermal conductivity of the closed cell foamed polymer is less than about 0.2 BTU/(hr x ft 2 x °F/in) . 34. The multipane glazing structure of claim 21, wherein the closed cell foam polymer is selected from the group consisting of foamed polycarbonate, polyurethane, polyphenylene oxide, and polyvinyl chloride. 35. The multipane glazing structure of claim 28, wherein the polymer has a density of at least about 3.0 lb/ft 3 . 36. A thermal break spacer for use between adjacent sheets of glazing spaced apart from one another a set distance in a multipane window, said spacer comprised of a body of physically stable closed cell foam polymer having a thermal conductivity of less than about 0.8 BTU/ (hr x ft 2 x °F/in) sized to provide a thermal break across the spacer. 37. The spacer of claim 36 wherein the polymer is selected from the group consisting of foamed polycarbonate, polyurethane, polyphenylene oxide and polyvinyl chloride. 38. The spacer of claim 36, said spacer comprised of a body of a physically stable closed cell foam polymer having a thermal conductivity of less than about 0.8 BTU/(hr x ft 2 x °F/in) and adhered thereto at least one additional spacer element not comprised of closed cell foam, said at least one additional spacer element and said closed cell foam body together sized to substantially span the set distance. 39. The spacer of claim 36, wherein said at least one additional spacer element is a hollow cross- section tubular element. 40. The spacer of claim 36 wherein said at least one additional spacer elements is two spacer elements adhered to opposite sides of said closed-cell foam body.

Inventors: HOOD THOMAS G, ILES ROGER F, MILLAR PETER J, HOOD, THOMAS, G., ILES, ROGER, F., MILLAR, PETER, J.
Applicants: HOOD THOMAS G, ILES ROGER F, MILLAR PETER J, SOUTHWALL TECHNOLOGIES INC, SOUTHWALL TECHNOLOGIES, INC.
Application year: 1993
Main classification: E04B1
IPC codes: E04C2, E06B3