One component epoxy resin compositions containing modified epoxy-amine adducts as curing agents

Abstract: A one component epoxy resin composition comprising, in addition to the epoxy resin, (1) an epoxy adduct obtainable by reacting an epoxy compound having one, two or more epoxy groups per molecule with a nitrogen-containing heterocyclic compound, an aliphatic amine or an aromatic amine, and (2) a boron compound of formula (I) B(OR₁)(OR₂(OR₃) (I) wherein R₁ to R₃ are the same or different and each is hydrogen, straight-chained, branched or cyclic alkyl or aryl, which composition optionally further comprises (3) a phenolic compound and/or (4) other epoxy curing agents. The composition is storage stable and cures quickly upon heating.

Description: Background of the Invention (Field of the Invention) The present invention relates to a one-liquid type epoxy resin composition which can be stored for extended periods of time at ordinary temperature and cures quickly upon heating. (Prior Art) Epoxy resins of the two-liquid type have heretofore been used being comprised of an epoxy resin and a curing agent. The epoxy resin composition of the two-liquid type, however, require such operations as weighing, stirring and mixing at a time when they are used on the site. These operations involve such problems as a decreased operation efficiency, erroneous weighing, or disposal of excess amounts of the epoxy resin composition. At present, therefore, study has been extensively conducted in an effort to developing one-liquid type epoxy resin compositions that permit highly efficient workability on the site and can be stored for extended periods of time to substitute for the two-liquid type ones. Development of a latent epoxy curing agent is a prerequisite for preparing the one-liquid type epoxy resin compositions. Known examples of the latent epoxy curing agent include dicyandiamide, carboxylic acid hydrazide, guanamine compounds, imidazole compounds. However, these latent curing agents cure the composition by heating at relatively high temperatures for extended periods of time. It has therefore been urged to provide a curing agent that activates at a low temperature and exhibits an excellent latent property. As latent curing agents for curing epoxy resins at relatively low temperatures, there is known an adduct of an alkylamine and an epoxy resin, and an adduct of an imidazole compound and an epoxy resin (U.S. Patent No. 4,066,625). These adducts however, are insufficient alone to obtain satisfactory latency. Therefore, additional modifications have been reported in which the surfaces thereof are coated with various compounds. For instance, there has been reported a method of encapsulation with an isocyanate compound (Japanese Laid-Open Patent Publication No. 268723/1986) and a method of surface treatment using an acidic substance (Japanese Patent Publication No. 18326/1990, Japanese Laid-Open Patent Publication No. 223027/1988). However, a satisfactory degree of latency has not been reliably achieved by the above-mentioned attempts to import latency by surface treatment. For instance, the capsule film of the isocyanate compound is easily destroyed by mechanical impact but is not sufficiently regenerated. In addition, surface treatment with an acidic compound such as an organic acid, an inorganic acid, a resin acid or an aluminum compound does not help obtain stabilised latency. EP-A-0,458,502 discloses latent catalysts for curing epoxy resin compositions which comprise a curing agent such as an amine which reacts with polyepoxide and a cure inhibitor comprising boric acid or maleic acid. JP-A-3/234727 discloses latent curing agent for epoxy resin produced by reaction under heat of a polyepoxy compound, an imidazole and at least two members selected from among boric acid, pyrogallol and gallic acid. JP-A-63/178125 discloses a latent curing agent for epoxy resin comprising a finely powdered epoxy-resin curing agent reacted at its surface with a sultone. Summary of the Invention The present invention seeks to develop an epoxy resin-curing agent which is effective as a low-temperature curing agent for an epoxy resin, and to develop a one-liquid type epoxy composition that can be stored for extended periods of time by utilizing the above curing agent. The present invention provides an epoxy resin composition comprising, in addition to the epoxy resin, (1) an epoxy adduct obtainable by reacting an epoxy compound having one, two or more epoxy groups per molecule with a nitrogen-containing heterocyclic compound, an aliphatic amine or an aromatic amine, that is surface treated with (2) a boron compound of formula (I): B(OR 1 ) (OR 2 ) (OR 3 ) wherein R 1 to R 3 are the same or different and each is hydrogen, straight-chain, branched or cyclic alkyl or aryl, and with (3) a phenolic compound. The invention further provides a latent epoxy curing agent or a cure accelerating agent comprising a fine granular epoxy adduct obtainable by reacting an epoxy compound having one, two or more epoxy groups per molecule with a nitrogen-containing heterocyclic compound, an aliphatic amine or aromatic amine, the surfaces of the fine granular epoxy adduct being coated with a boron compound of formula (I) B(OR 1 )(OR 2 )(OR 3 ) wherein R 1 to R 3 are the same or different and each is hydrogen, straight-chain, branched or cyclic alkyl or aryl, which composition further comprises (3) a phenolic compound. The invention also provides the use as a surface-treating agent for an epoxy adduct, of a boron compound of formula (I) B(OR 1 ) (OR 2 ) (OR 3 ) wherein R 1 to R 3 are the same or different and each is hydrogen, straight-chain, branched or cyclic alkyl or aryl, and a phenolic compound. The invention yet further provides a process for producing an epoxy resin composition of the invention comprising the step of kneading an epoxy resin with the other components of the composition. Specifically, the process of the invention may comprise: (A) adding the epoxy adduct, the boron compound and the phenol compound separately in any order to the epoxy resin; (B) mixing the boron compound and the phenolic compound to form a mixture and adding the mixture and the epoxy adduct separately in any order to the epoxy resin; (C) surface-treating the epoxy adduct with the boron compound then adding the surface treated adduct and the phenolic compound separately in any order to the epoxy resin; or (D) reacting the boron compound and the phenolic compound to form a product, surface-treating the epoxy adduct with the product and mixing the surface-treated epoxy adduct with the epoxy resin. The invention yet further provides the use of an epoxy resin of the invention, latent epoxy curing or curing accelerating agent of the invention or surface-treated adduct produced by the use of the boron and phenolic compounds according to the invention in the production of a cured epoxy resin product. Detailed Description of the Invention The boric acid compounds used in the present invention not only include boric acids and boric acid esters but also include the case where boric acid reacts with an alcohol to form a boric acid ester as well as the case where the boric acid ester is, on the other hand, changed into boric acid through hydrolysis. The boric acid compound used in the present invention further includes the case where there exists a so-called partial ester of boric acid. It has in practice been confirmed that when the surfaces of the adduct powder are coated with trimethyl borate, boric acid adheres on the surfaces of the epoxy adduct as confirmed by infrared absorption analysis. When the surfaces of the very finely granular epoxy adduct are treated with a boric acid ester compound only, the boric acid ester is required in an increased amount and the epoxy-curing property is almost lost. In addition, the surface-treated adduct in an epoxy resin composition aggregates conspicuously during curing, causing the resin to be poorly cured. In the acid anhydride-curing system, furthermore, satisfactory storage stability is still not obtained by a single treatment with boric acid compounds. In order to solve such problems, the present inventors have used an epoxy adduct, a boric acid compound, and a phenolic resin present in an epoxy resin composition. It has been found that when the surfaces of the epoxy adduct are coated with the boric acid compound and the phenolic compound, the epoxy resin composition can be stably preserved. The inventors have further discovered that even when the epoxy adduct is used as a curing agent or as a cure promoting agent for the acid anhydride-type curing agents, the treated epoxy adduct composition can be stably stored and exhibit excellent curing property. The powdery epoxy adduct that is used for putting the present invention into practice has an average grain size of from about 0.1 to about 100 µm, and is obtained by pulverizing a product that is obtained by addition-reacting an epoxy compound with alkylamines, aromatic amines or nitrogen-containing heterocyclic compounds according to a conventional method. The boric acid compound used in Examples of the present invention is represented by the following general formula, B(OR 1 )(OR 2 )(OR 3 ) wherein R 1 to R 3 are hydrogen atoms, alkyl groups or aryl groups. Representative examples thereof include boric acid, trimethyl borate, triethyl borate, tripropyl borate, tributyl borate, trioctyl borate, triphenyl borate and tricresyl borate, as well as esters formed by the partial alcohol-exchange reaction. Representative examples of the nitrogen-containing heterocyclic compound used in Examples of the present invention include imidazole compounds such as imidazole, 2-ethyl-4-methylimidazole, 2-methylimidazole, 2-phenylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-phenyl-4-methyl-5-hydroxymethylimidazole and 2-phenyl-4,5-dihydroxymethylimidazole, as well as mercaptobenzothiazoles, melamine derivatives and the like. It is further allowable to use nitrogen-containing heterocyclic compounds having a 2-hydroxyethyl group on the nitrogen atom such as 1-(2-hydroxyethyl)-2-methylimidazole, 1-(2-hydroxyethyl)-2-phenylimidazole and diethanolamine, since they exhibit actions similar to those of the adduct. Moreover, representative examples of the aliphatic amine compound and aromatic amine compound used in Examples of the present invention include a diethylenetriamine, a triethylenetetramine, a tetraethylenepentamine, an iminobispropylamine, a bis(hexamethylene)triamine, a diaminodiphenylmethane, a metaphenylenediamine and a 3,9-bis(3-aminopropyl)-2,4,8,10-tetroxaspiro[5,5] undecane. Representative examples of the phenolic compound used for the epoxy resin composition of the present invention include compounds such as catechol, a 4-t-butyl catechol, pyrogallol, resorcin, hydroquinone, phloroglucinol, bisphenol A, bisphenol F, dihydroxybiphenyl, dihydroxynaphthalene, a 1,1,1-tris(4-hydroxyphenyl) ethane and a bis(4-hydroxyphenyl) sulfone, a novolac-type or a resol-type phenol resin, and phenol-type polymers such as a poly(vinyl phenol). Examples of the epoxy resin used for preparing the epoxy adduct or is blended to the epoxy resin composition of the present invention include a bisphenol A-type epoxy resin, a bisphenol F-type resin, a cyclic aliphatic epoxy resin, a glycidyl ester-type epoxy resin, a glycidylamine-type epoxy resin, a hydantointype epoxy resin, a triglycidylisocyanurate, a phenylglycidylether and a butylglycidylether which may be used in one kind or in a combination of two or more kinds. When putting the present invention into practice, a number of methods may be used for preparing an epoxy resin composition using an epoxy adduct, a boric acid compound and a phenolic compound as essential components. The methods include (A) a method in which the epoxy adduct, the boric acid compound and the phenolic compound are separately added to the epoxy resin, and are kneaded using a planetary mixer or a roll mill, (B) a method in which a mixture product of the boric acid compound and the phenolic compound is prepared in advance, and the thus prepared product and the epoxy adduct are kneaded together with the epoxy resin, (C) a method in which the surfaces of the epoxy adduct are treated with the boric acid compound only, which is then kneaded together with the phenolic compound and the epoxy resin, and (D) a method in which the boric acid compound and the phenolic compound are reacted with each other, and the obtained reaction product is applied onto the epoxy adduct using a spray drier or the like, which is then kneaded together with the epoxy resin. The surfaces of the epoxy adduct can be coated by using any method of preparing the epoxy resin composition. In preparing the epoxy resin composition of the resent invention, the boric acid or the boric acid ester compound should be blended in an amount of 0.01 to 200 parts by weight and, preferably, in an amount of 0.5 to 40 parts by weight per 100 parts by weight of the epoxy adduct. When the amount of addition is smaller than 0.01 parts by weight, the latency cannot be maintained to a sufficient degree and when the amount of addition is greater than 200 parts by weight, on the other hand, the curing property becomes poor. The surface-treated epoxy adduct should be blended in an amount of 0.5 to 50 parts by weight and, preferably, in an amount of 1 to 25 parts by weight per 100 parts by weight of the epoxy resin. In this case, suitable curing rate and latent curing property are maintained. The phenolic compound is blended in an amount of 0.001 to 50 parts by weight and, preferably, in an amount of 0.05 to 10 parts by weight per 100 parts by weight of the epoxy resin. The optimum amount of addition varies depending upon the amount of boric acid or boric acid ester compound that is used at the same time. It is desired that the equivalent ratio of phenolic hydroxyl group to boric acid or boric acid ester is 1:0.2 to 1:5. According to the present invention, furthermore, an epoxy resin composition that can be stably preserved is obtained even in a curing system in which other epoxy curing agents such as acid anhydrides are added to the above-mentioned epoxy resin composition. Representative examples of the curing agent used here includes acid anhydrides such as maleic anhydride, phthalic anhydride, trimellitic anhydride, pyromellitic anhydride, succinic anhydride, methylnadic anhydride and chlorendic anhydride, as well as dicyandiamide, acid hydrazides, diaminomaleonitrile, diallylmelamine and amineimides. In preparing the epoxy resin composition, it is allowable to use, as required, an antioxidizing agent, granular and fibrous fillers of various kinds, and additives such as a plasticizer, a reactive diluent, a coloring agent, a viscosity-adjusting agent and like agents, in addition to the curing agent or the cure accelerating agent. Contents of the present invention will now be concretely described by way of Examples. it needs not be pointed out that in the present invention, the epoxy resins, amine compounds, nitrogen-containing heterocyclic compounds, phenolic compounds and silica used as starting materials are in no way limited to those described in Examples and Comparative Examples only. In Examples of the present invention, furthermore, the epoxy adducts are prepared in compliance with a widely known method, and the components constituting the epoxy adducts that are used are described in parenthesis. (1) Epoxy resin Trade name: Epikote No. 828, produced by Yuka Shell Co. Trade name: Epikote No. 152, produced by Yuka Shell Co. Trade name: DER-438, produced by Dow Chemical Japan Co. Trade name: DER-331J, produced by Dow Chemical Japan Co. Trade name: ERL-4221, produced by Union Carbide Japan Co. (2) Nitrogen-containing heterocyclic compound Trade name: Curezol 2E4MZ, produced by Shikoku Kasei Kogyo Co. (2-ethyl-4-methylimidazole) Trade name: Curezoi 2PZ, produced by Shikoku Kasei Kogyo Co. (2-phenylimidazole) Trade name: Curezol C17Z, produced by Shikoku Kasei Kogyo Co. (2-heptadecylimidazole) Trade name: Curezol C11Z, produced by Shikoku Kasei Kogyo Co. (2-undecylimidazole) (3) Phenolic compound Trade name: Resitop PSM-4261, produced by Gun-ei Kagaku Kogyo Co. Trade name: Resin X, produced by Mitsubishi Yuka Co. Trade name: Resin M, produced by Maruzen Sekiyu Kagaku Co. (4) Silica Trade name: Aerosil No. 380PE, produced by Japan Aerosil Co. The surfaces were treated in compliance with the above-mentioned methods (A) to (D). The storage stability of the epoxy resin composition was evaluated in terms of a gelation time at 40°C and the curing property of the epoxy resin was evaluated in terms of a gelation time at 150°C. The gelation time was found by a stroke-cure method on a heated steel plate maintained at a temperature of 40°C or 150°C. (Example 1) About 280 g of Curezol 2MZ was dissolved in 5 liters of methyl ethyl ketone with heating followed by the addition of a solution obtained by diluting about 690 g of epoxy resin DER-331J in 500 ml of methyl ethyl ketone. The mixture was refluxed and reacted for two hours. Then, the solvent was removed and the reaction product was finely pulverized to prepare about 950 g of an epoxy adduct. On the other hand, 2.5 g of Resitop which is a phenolic compound used as a surface-treating agent was dissolved in 25 g of an epoxy resin. 475 Grams of the epoxy resin, 100 g of the above epoxy adduct, 4.5 g of tributyl borate, and 27.5 g of the above-mentioned epoxy resin in which has been dissolved the Resitop were weighed into a stainless steel pot and were mixed. The mixture was then kneaded at room temperature for about 15 minutes using a three-roll mill to prepare an epoxy resin composition for evaluation. The gelation times of the obtained epoxy resin composition were measured to be 30 days or longer at 40°C and 23 seconds at 150°C. (Examples 2 to 6) By using the epoxy adducts shown in Table 1 obtained by the same method as that of Example 1 and by using the surface-treating agents shown in Table 1, the epoxy resins, epoxy adducts and surface-treating agents were treated at blending ratios shown in Table 1 in the same manner as in Example 1 to prepare epoxy resin compositions. The gelation times of the epoxy resin compositions were measured to be as shown in Table 1. Example 1 2 3 for comparison 4 5 6 Epoxy resin (Epikote =828) 100 100 100 100 100 100 Epoxy adduct (Epikote =828/2MZ) 20 (Epikote =828/2MZ/bisphenol A) 20 (Epikote =828/2PZ) 20 (Epikote =828/2E4MZ) 20 (Epikote =828/C11Z) 20 (DER-438/2E4MZ) 20 (ERL-4221/2E4MZ) Surface-treating agent Trimethyl borate 0.50 0.50 0.50 0.50 Tributyl borate 0.90 0.90 Triphenyl borate 1.10 Resitop 0.50 0.50 0.50 0.50 0.50 0.50 Surface-treating method A A A A A A Gelation time (sec/150°C) 23 72 62 25 95 23 (days/40°C) >30 >30 >30 >30 25 >30 (Examples 7 and 8) By using the epoxy adduct shown in Table 2 obtained by the same method as that of Example 1 and by using the surface-treating agents shown in Table 2, the epoxy resin, epoxy adduct and surface-treating agents were treated at blending ratios shown in Table 2 in the same manner as in Example 1 to prepare epoxy resin compositions. The gelation times of the epoxy resin compositions were measured to be as shown in Table 2. (Example 9) 2.5 Grams of pyrogallol which is a phenolic compound serving as the surface-treating agent and 2.5 g of a trimethyl borate were dissolved in 40 ml of acetone with heating. Then, acetone was moderately removed by evaporation to obtain a mixture surface-treating agent. Next, 460 g of the epoxy resin, 100 g of the epoxy adduct (curing agent) and 5 g of the above mixture surface-treating agent were weighed into a stainless steel pot and were mixed in advance. The mixture was then mixed at room temperature for about 15 minutes using a three-roll mixer to prepare a sample for evaluation. The gelation time of the obtained epoxy resin composition was measured to be 30 days or longer at 40°C and 24 seconds at 150°C. (Examples 10 to 13) By using the epoxy adduct shown in Table 2 obtained by the same method as that of Example 9 and by using the surface-treating agents shown in Table 2, the epoxy resin, epoxy adduct and surface-treating agents were treated at blending ratios shown in Table 2 in the same manner as in Example 9 to prepare epoxy resin compositions. The gelation times of the epoxy resin compositions were measured to be as shown in Table 2. (Example 14) A solution obtained by dissolving 10 g of triethyl borate in 50 ml of acetone was spray-dried on 100 g of a fine powdery epoxy adduct (DER 331J/2E4MZ) by using a spray drier to obtain an epoxy adduct of which the surface has been treated. To 500 g of the epoxy resin were then added 110 g of the above surface-treated epoxy adduct and 2.5 g of catechol. The mixture was kneaded at room temperature for 15 minutes using a three-roll mill to obtain a desired composition. The gelation time of the resin was 30 days or longer at 40°C and was 24 seconds at 150°C. (Example 15) 10 Grams of trimethyl borate and 10 g of Resitop were dissolved in 100 ml of acetone, which was then spray-dried onto 400 g of the adduct to obtain the adduct whose surface has been treated. Then, 110 g of the surface-treated epoxy adduct was added to 500 g of the epoxy resin, and the mixture was kneaded at room temperature for 15 minutes using a three-roll mixer to obtain a desired composition. The gelation time of the resin was 30 days or longer at 40°C and was 26 seconds at 150°C. (Example 16) By using the epoxy adduct shown in Table 2 obtained by the same method as that of Example 15 and by using the surface-treating agents shown in Table 2, the epoxy-resin, epoxy adduct and surface-treating agents were treated at blending ratios shown in Table 2 in the same manner as in Example 15 to prepare epoxy resin compositions. The gelation times of the epoxy resin composition were measured to be as shown in Table 2. (Comparison Example 1) The epoxy resin, epoxy adduct and boric acid were mixed together at a blending ratio shown in Table 2 quite in the same manner as that of Example 1 but without using the phenolic compound, in order to prepare an epoxy resin composition. The gelation times of the thus obtained epoxy resin composition were measured to be as shown in Table 2. (Comparison Example 2) The epoxy adduct of which the surfaces have been treated with methyl borate and the epoxy resin were mixed together at a blending ratio shown in Table 2 quite in the same manner as that of Example 14 but without using the phenolic compound, in order to prepare an epoxy resin composition. The gelation times of the thus obtained epoxy resin composition were measured to be as shown in Table 2. (Examples 17 to 19) A variety of surface-treated epoxy adducts were obtained in the same manner as in Example 14. Then, the epoxy resin, phenolic compounds, Aerosil and the epoxy adducts serving as the cure promoting agents were kneaded at blending ratios shown in Table 3 at room temperature for 15 minutes using a three-roll mixer. The kneaded product was then transferred to a planetary mixer followed by the addition of a predetermined amount of methylnadic anhydride which is a curing agent. The mixture was mixed with stirring under a reduced pressure for 30 minutes to obtain epoxy resin compositions. The gelation times of these epoxy resin compositions were measured to be as shown in Table 3. (Examples 20 and 21) A variety of surface-treated epoxy adducts were obtained in the same manner as in Example 14. Then, the epoxy resin, phenolic compounds, Aerosil, dicyandiamide as a curing agent and the epoxy adducts as a cure accelerating agents were kneaded at blending ratios shown in Table 3 at room temperature for 15 minutes using a three-roll mixer in order to prepare epoxy resin compositions. The gelation times of these epoxy resin compositions were measured to be as shown in Table 3. (Examples 22 and 23) By using the epoxy adduct shown in Table 3 obtained by the same method as that of Example 1 and by using the surface-treating agents, the epoxy resin, curing agent, epoxy adduct and surface-treating agents were treated at blending ratios shown in Table 3 in the same manner as in Example 1 to prepare epoxy resin compositions. The elation times of the epoxy resin compositions were measured to be as shown in Table 3. Example 17 18 19 20 21 22 23 Epoxy resin (parts) Epikote #828 100 100 100 100 100 100 DER-331J 100 Curing agent (parts) Methylnadic anhydride 85 85 85 85 85 Dicyandiamide 4 4 Cure promoting agent (parts) (DER-438/2E4MZ) 6 5 5 6 6 (Epikote#152/2E4MZ) 6 (DER-438/2PZ) 6 Surface-treating agent (parts) Trimethyl borate 4 5 5 5 5 4 Pyrogallol 5 5 5 5 Catechol 4 Resitop 2 Aerosil (parts) 3 3 3 2 2 3 3 Surface-treating method C C C C C A A Gelation time (sec/150°C) 330 320 250 96 82 305 320 (days/40°C) >30 >30 >30 >30 >30 5 2 (Comparative Examples 3 and 4) An epoxy adduct of a composition shown in Table 4 serving as a curing agent or an imidazole compound was mixed at a blending ratio as shown in Table 4 to prepare an epoxy resin composition. The gelation times of the epoxy resin composition were measured to be as shown in Table 4. Comparative Example 5) An epoxy resin composition was prepared quite in the same manner as in sample 1 but without adding the boric acid compound. The gelation times of the epoxy resin composition were measured to be as shown in Table 4. Comparative Example 3 4 5 Epoxy resin Epikote #828 100 100 100 Curing agent Adduct ERL-4221 (5.1 parts) 15 C 17 Z (6.1 parts) Pyrogallol (2.0 parts) Boric acid (1.8 parts) Curezol C 17 Z 6.1 Adduct (Epikote#828/2E4MZ) 20 Resitop 1 Gelation time (sec/150°C) >1800 155 23 (days/40°C) >30 >30 1 When an epoxy adduct is used as a curing agent or Is used as a cure accelerating agent with other curing agents, boric acid or a boric acid ester compound and a phenolic compound used together with the epoxy adduct in the epoxy resin composition, provide the epoxy resin composition with favorable storage stability and curing property. The epoxy resin composition of the present invention, therefore, can be used as an adhesive, a sealant, an in, a painting material and the like.

Claims: An epoxy resin composition comprising, in addition to the epoxy resin, (1) an epoxy adduct obtainable by reacting an epoxy compound having one, two or more epoxy groups per molecule with a nitrogen-containing heterocyclic compound, an aliphatic amine or an aromatic amine, that is surface treated with (2) a boron compound of formula (I): B(OR 1 ) (OR 2 ) (OR 3 ) wherein R 1 to R 3 are the same or different and each is hydrogen, straight-chain, branched or cyclic alkyl or aryl, and with (3) a phenolic compound. A latent epoxy curing agent or a cure accelerating agent comprising a fine granular epoxy adduct obtainable by reacting an epoxy compound having one, two or more epoxy groups per molecule with a nitrogen-containing heterocyclic compound, an aliphatic amine or aromatic amine, the surfaces of the fine granular epoxy adduct being coated with a boron compound of formula (I) B(OR 1 ) (OR 2 ) (OR 3 ) wherein R 1 to R 3 are the same or different and each is hydrogen, straight-chain, branched or cyclic alkyl or aryl, which composition further comprises (3) a phenolic compound. The use as a surface-treating agent for an epoxy adduct, of a boron compound of formula (I) B(OR 1 ) (OR 2 ) (OR 3 ) wherein R 1 to R 3 are the same or different and each is hydrogen, straight-chain, branched or cyclic alkyl or aryl, and a phenolic compound. A process for producing an epoxy resin composition according to claim 1 comprising the step of kneading an epoxy resin with the other components of the composition. A process according to claim 4 comprising the adding the epoxy adduct, the boron compound and the phenolic compound separately in any order to the epoxy resin. A process according to claim 4 comprising mixing the boron compound and the phenolic compound to form a mixture and adding the mixture and the epoxy adduct separately in any order to the epoxy resin. A process according to claim 4 comprising surface-treating the epoxy adduct with the boron compound then adding the surface treated adduct and the phenolic compound separately in any order to the epoxy resin. A process according to claim 4 comprising reacting the boron compound and the phenolic compound to form a product, surface-treating the epoxy adduct with the product and mixing the surface-treated epoxy adduct with the epoxy resin. Use of an epoxy resin according to claim 1, a latent epoxy curing or cure accelerating agent according to claim 2 or a surface-treating agent according to claim 3 in production of a cured epoxy resin product.

Inventors: MATSUMOTO AKIKO, NAKATSUKA TAKUO, TANIMOTO MIE, TOYOTA TSUYOSHI, MATSUMOTO, AKIKO, NAKATSUKA, TAKUO, TANIMOTO, MIE, TOYOTA, TSUYOSHI
Applicants: SHIKOKU CHEM, SHIKOKU CHEMICALS CORPORATION
Application year: 1993
Main classification: C08G59
IPC codes: C08G59