Polypropylene composition

Abstract: A polypropylene composition comprising 95 - 55 parts by weight of polypropylene (A) and 5 - 45 parts by weight of an ethylene/1-butene random copolymer (B-1) which contains constituent units derived from 1-butene in an amount of 15 to 25 % by mol; and a polypropylene composition comprising 95 - 55 parts by weight of polypropylene (A) and 5 - 45 parts by weight of an ethylene/1-octene random copolymer (B-2) which contains constituent units derived from 1-octene in an amount of 8 to 20 % by mol. Each of the random copolymers (B-1) and (B-2) has an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin, a glass transition temperature (Tg) of not higher than -50°C, a crystallinity of less than 20 % as measured by X-ray diffractometry, a randomness parameter (B value) of 1.0 to 1.4 as measured by ¹³C-NMR spectroscopy. With respect to a melting point as measured by a differential scanning calorimeter (DSC) as the main peak, the copolymer (B-1) has a value of not higher than 60 °C, while the copolymer (B-2) has a value of not higher than 80 °C.

Description: The present invention relates to polypropylene compositions having excellent rigidity, heat resistance and impact resistance, particularly low-temperature impact resistance. Articles molded from polypropylene have, for example, excellent rigidity, heat resistance and surface glossiness. Hence they have been widely applied in various uses. However, polypropylene is generally crystalline and the impact resistance, particularly low-temperature impact resistance is poor. Therefore application thereof is limited to certain uses. Conventional methods for increasing the impact resistance of polypropylene are the method of adding polyethylene to polypropylene and the method of adding thereto rubber-like materials such as polyisobutylene, polybutadiene and a non-crystalline ethylene/propylene copolymer. In particular, a method of adding a non-crystalline or low-crystalline ethylene/propylene random copolymer has been used in many cases. However, the present inventors have studied polypropylene compositions comprising the non-crystalline or low-crystalline ethylene/propylene random copolymer and polypropylene, and found that the non-crystalline or low-crystalline ethylene/propylene random copolymer cannot improve the impact resistance very much. Hence the ethylene/propylene random copolymer must be contained in the polypropylene composition in a large amount to obtain a satisfactory impact resistance. When a large amount of the ethylene/propylene random copolymer is contained in the polypropylene composition, the composition can have improved impact resistance but also have seriously lowered rigidity, heat resistance and surface hardness. On the other hand, if the ethylene/propylene random copolymer is contained in the polypropylene composition in a small amount to retain the rigidity, heat resistance and surface hardness, the low-temperature impact resistance of the polypropylene composition cannot be sufficiently improved. In place of using such non-crystalline or low-crystalline ethylene/propylene random copolymer, trials in which other ethylene/α-olefin copolymers are added to polypropylene to obtain a polypropylene composition having a high impact resistance have been carried out. For example, Japanese Patent Publications Nos. 25693/1983 and 38459/1983 disclose a composition comprising crystalline polypropylene and an ethylene/1-butene copolymer which contains constituent units derived from 1-butene in an amount of not more than 15 % by mol. In addition, Japanese Patent Laid Open No. 243842/1986 discloses a polypropylene composition comprising crystalline polypropylene and an ethylene/1-butene copolymer which is obtained using a titanium heterogeneous type catalyst. The polypropylene compositions disclosed in these publications have improved impact resistance and rigidity, but much more improvement in the low-temperature impact resistance is desired. Japanese Patent Publication No. 42929/1988 discloses a polypropylene composition comprising crystalline polypropylene and an ethylene/1-butene copolymer which contains constituent units derived from 1-butene in an amount of 25 to 10 % by weight and has an intrinsic viscosity [η] of not more than 1.5 dl/g. This polypropylene composition has insufficient impact resistance. Japanese Patent Laid-Open No. 250040/1991 describes the use of an ethylene/1-butene block copolymer containing constituent units derived from 1-butene in an amount of 10 to 90% by weight to increase the impact resistance of polypropylene. However, this ethylene/1-butene block copolymer does not have good compatibility with polypropylene and there is an insufficient improvement in the impact resistance. There is now eagerly desired a polypropylene composition having excellent impact resistance, particularly low-temperature impact resistance, as well as excellent rigidity and heat resistance. As a result of earnest studies by the present inventors to solve the problems associated with the prior art, they have found that a polypropylene composition comprising polypropylene and a specific ethylene/α-olefin copolymer has excellent rigidity, heat resistance and impact resistance, particularly low-temperature heat resistance. EP-A-52557 discloses a polypropylene composition containing 40 to 98 wt% isotactic polypropylene and 2 to 60 wt% polyethylene having a density of less than or equal to 0.935, obtained by the copolymerization of 85 to 96 wt% ethylene and 4 to 15 wt% of one or more higher α-olefins , the copolymerization being carried out at a pressure of less than 4 x 10 6 Pa and in the absence of liquid hydrocarbons. The present invention provides the use of a polypropylene composition for automotive interior or exterior trim, wherein said composition comprises : (A) a propylene homopolymer; and (B-1) an ethylene/1-butene random copolymer having a content of 1-butene derived units from 15 to 25 % by mol, an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin at 135°C, a melting point of not higher than 60°C as measured by a differential scanning calorimeter (DSC) as the main peak, a glass transition temperature (Tg) of not higher than -50°C, a crystallinity of less than 20% as measured by X-ray diffractometry, and a randomness parameter (B value) of 1.0 to 1.4 as measured by 13 C-NMR spectroscopy wherein B= P BE 2P B ·P E wherein P E and P B are the molar fraction of the ethylene component and the molar fraction of the 1-butene component, respectively, and P BE is the molar fraction of the 1-butene/ethylene chain in all the dyad chains; the weight ratio of (A):(B-1) being from 95:5 to 55:45. Further the present invention provides a polypropylene composition comprising: (A) a polypropylene; (B-1) an ethylene/1-butene random copolymer having a content of 1-butene derived units from 15 to 25% by mol, an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin at 135 °C, a melting point of not higher than 60 °C as measured by a differential scanning calorimeter (DSC) as the main peak, a glass transition temperature (Tg) of not higher than -50 °C, a crystallinity of less than 20% as measured by X-ray diffractometry, and a randomness parameter (B value) of 1.0 to 1.4 as measured by 13 C-NMR spectroscopy wherein B= P BE 2P B ·P E wherein P E and P B are the molar fraction of the ethylene component and the molar fraction of the 1-butene component, respectively, and P BE is the molar fraction of the 1-butene/ethylene chain in all the dyad chains; the weight ratio of (A):(B-1) being from 95:5 to 55:45; and (C) a propylene/ethylene copolymer in an amount of not more than 15% by weight of the combined weight of polypropylene (A) and ethylene/1-butene random copolymer (B-1), the propylene/ethylene copolymer having a content of ethylene derived units from 35 to 60% by mol and an intrinsic viscosity [η] of 2 to 12 dl/g as measured in decalin at 135 °C. The present invention also provides a polypropylene composition comprising: (A) a polypropylene; and (B-2) an ethylene/1-octene random copolymer having a content of 1-octene derived units from 8 to 20% by mol, an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin at 135°C, a melting point of not higher than 80°C as measured by a differential scanning calorimeter (DSC) as the main peak, a glass transition temperature (Tg) of not higher than -50°C, a crystallinity of less than 20% as measured by X-ray diffractometry, and a randomness parameter (B value) of 1.0 to 1.4 as measured by 13 C-NMR spectroscopy wherein B= P OE 2P O ·P E wherein P E and P O are the molar fraction of the ethylene component and the molar fraction or the 1-octene component, respectively, and P OE is the molar fraction of the 1-octene/ethylene chain in all the dyad chains; the weight ratio of (A):(B-2) being from 95:5 to 55:45. The above-mentioned polypropylene compositions may further comprise: (C) a propylene/ethylene copolymer in an amount of not more than 15 % by weight, preferably 5 to 15 % by weight, of the combined weight of polypropylene (A) and ethylene/α-olefin random copolymer (B), the propylene/ethylene copolymer having a content of ethylene derived units from 30 to 60 % by mol and an intrinsic viscosity [η] of 2 to 12 dl/g as measured in decalin at 135°C. The polypropylene composition according to the present invention will now be described in more detail. The polypropylene composition of the invention comprises (A) a polypropylene and (B-1) a specific ethylene/1-butene copolymer, or comprises (A) a polypropylene and (B-2) a specific ethylene/1-octene copolymer. (A) Polypropylene The polypropylene (A) includes a homopolymer of propylene and a propylene/α-olefin copolymer containing constituent units derived from an olefin other than propylene in an amount of not more than 10 % by mol. Examples of α-olefins which may be included in the propylene/α-olefin copolymer include ethylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene, 1-dodecene, 1-hexadodecene, 4-methyl-1-pentene, 2-methyl-1-butene, 3-methyl-1-butene, 3,3-dimethyl-1-butene, diethyl-1-butene, trimethyl-1-butene, 3-methyl-1-pentene, ethyl-1-pentene, propyl-1-pentene, dimethyl-1-pentene, methylethyl-1-pentene, diethyl-1-hexene, trimethyl-1-pentene, 3-methyl-1-hexene, dimethyl-1-hexene, 3,5,5-trimethyl-1-hexene, methylethyl-1-heptene, trimethyl-1-heptene, dimethyloctene, ethyl-1-octene, methyl-1-nonene, vinylcyclopentene, vinylcyclohexane and vinylnorbornene. The copolymer of propylene with these olefins may be either a random copolymer or a block copolymer. Further, the propylene/α-olefin copolymer may be a copolymer obtained by prepolymerizing a homopolymer or copolymer of 3-methyl-1-butene, 3,3-dimethyl-1-butene, 3-methyl-1-pentene, 3-methyl-1-hexene, 3,5,5-trimethyl-1-hexene, vinylcylopentene, vinylcyclohexane or vinylnorbornene to a catalyst and then polymerizing propylene using the resultant prepolymerized catalyst. In the present invention, a propylene homopolymer is preferred as the polypropylene (A). The polypropylene (A) used for the invention generally has a melt flow rate (MFR), as measured at 230 °C under a load of 2,160 g in accordance with ASTM-D1238, of 0.1 to 200 g/10 min, preferably 0.3 to 100 g/10 min. A polypropylene composition containing the polypropylene (A) having such an MFR as described above has high flowability and can be readily molded into a large-sized article. A polypropylene composition containing polypropylene having a melt flow rate higher than the above-mentioned value has deteriorated impact resistance. The polypropylene (A) can be prepared by various processes. Generally, it is prepared using a conventionally known stereoregular catalyst. For example, the polypropylene is obtainable by polymerisation using a catalyst formed from a solid titanium catalyst component, for example supported on a support material, an organometallic catalyst component and, if desired, an electron donor such as dicyclopentyldimethoxysilane. The solid titanium catalyst component used in this process includes a titanium catalyst component in which titanium trichloride or a titanium trichloride composition is supported on a support material having a specific surface area of not less than 100 m 2 /g, and a titanium catalyst component which contains magnesium, halogen, an electron donor (preferably an aromatic carboxylate or ether containing alkyl group) and titanium as its essential components and in which the essential components are supported on a support material having a specific surface area of not less than 100 m 2 /g. Of these, the latter support type catalyst component is particularly preferably used to prepare the polypropylene. The organometallic catalyst component used in the above process is preferably an organoaluminium compound. Examples of the organoaluminium compound include trialkylaluminium, dialkylaluminium halide, alkylaluminium sesquihalide and alkylaluminium dihalide. Choice of the proper organoaluminium compound can be made in conformity with the kind of titanium catalyst component used. Useful electron donors are organic compounds containing a nitrogen atom, a phosphorus atom, a sulfur atom, a silicon atom or a boron atom. Preferred are silicon compounds, ester compounds or ether compounds containing these atoms. The preferred silicon compound has the formula (i): R a n -Si-(OR b ) 4-n wherein n is 1, 2 or 3; when n is 1, R a is a secondary or tertiary hydrocarbon group; when n is 2 or 3, at least one of R a is a secondary or tertiary hydrocarbon group, and each R a may be the same or different; and R b is a hydrocarbon group of 1 to 4 carbon atoms; and when 4-n is 2 or 3, R b may be the same or different. In the silicon compound of formula (i), the secondary or tertiary hydrocarbon group includes unsubstituted or substituted cyclopentyl, cyclopentenyl and cyclopentadienyl groups, and hydrocarbon groups in which the carbon adjacent to Si is secondary or tertiary. More concretely, the substituted cyclopentyl group includes a cyclopentyl group having an alkyl group such as 2-methylcyclopentyl, 3-methylcyclopentyl, 2-ethylcyclopentyl, 2-n-butylcyclopentyl, 2,3-dimethylcyclopentyl, 2,4-dimethylcyclopentyl, 2,5-dimethylcyclopentyl, 2,3-diethylcyclopentyl, 2,3,4-trimethylcyclopentyl, 2,3,5-trimethylcyclopentyl, 2,3,4-triethylcyclopentyl, tetramethylcyclopentyl and tetraethylcyclopentyl; the substituted cyclopentenyl group includes a cyclopentenyl group having an alkyl group such as 2-methylcyclopentenyl, 3-methylcyclopentenyl, 2-ethylcyclopentenyl, 2-n-butylcyclopentenyl, 2,3-dimethylcyclopentenyl, 2,4-dimethylcyclopentenyl, 2,5-dimethylcyclopentenyl, 2,3,4-trimethylcyclopentenyl, 2,3,5-trimethylcyclopentenyl, 2,3,4-triethylcyclopentenyl, tetramethylcyclopentenyl and tetraethylcyclopentenyl; the substituted cyclopentadienyl group includes a cyclopentadienyl group having an alkyl group such as 2-methylcyclopentadienyl, 3-methylcyclopentadienyl, 2-ethylcyclopentadienyl, 2-n-butylcyclopentadienyl, 2,3-dimethylcyclopentadienyl, 2,4-dimethylcyclopentadienyl, 2,5-dimethylcyclopentadienyl, 2,3-diethylcyclopentadienyl, 2,3,4-trimethylcyclopentadienyl, 2,3,5-trimethylcyclopentadienyl, 2,3,4-triethylcyclopentadienyl, 2,3,4,5-tetramethylcyclopentadienyl, 2,3,4,5-tetraethylcyclopentadienyl, 1,2,3,4,5-pentamethylcyclopentadienyl and 1,2,3,4,5-pentaethylcyclopentadienyl. The hydrocarbon group in which the carbon adjacent to Si is secondary includes i-propyl, s-butyl, s-amyl and α-benzyl; and the hydrocarbon group in which the carbon adjacent to Si is tertiary includes t-butyl, t-amyl, α,α'-diemethylbenzyl and admantyl. When n is 1, the silicon compound of formula (i) includes trialkoxysilanes such as cyclopentyltrimethoxysilane, 2-methylcyclopentyltrimethoxysilane, 2,3-dimethylcyclopentyltrimethoxysilane, cyclopentyltriethoxysilane, iso-butyltriethoxysilane, t-butyltriethoxysilane, cyclohexyltrimethoxysilane, cyclohexyltriethoxysilane, 2-norbornanetrimethoxysilane, and 2-norbornanetriethoxysilane; when n is 2, the silicon compound of formula (i) includes dialkoxysilanes such as dicyclopentyldiethoxysilane, t-butylmethyldimethoxysilane, t-butylmethyldiethoxysilane, t-amylmethyldiethoxysilane, dicyclohexyldimethoxysilane, cyclohexylmethyldimethoxysilane, cyclohexylmethyldiethoxysilane, and 2-norbornanemethyldimethoxysilane. When n is 2, the silicon compound of formula (i) is preferably a dimethoxy compound of formula (ii): wherein R a and R c are each independently a cyclopentyl group, a substituted cyclopentyl group, a cyclopentenyl group, a substituted cyclopentenyl group, cyclopentadienyl group, a substituted cyclopentadienyl group or a hydrocarbon group whose carbon adjacent to Si is a secondary or tertiary carbon. The silicon compound of formula (ii) includes, for example, dicyclopentyldimethoxysilane, dicyclopentenyldimethoxyxilane, dicyclopentadienyldimethoxyxilane, di-t-butyldimethoxysilane, di-(2-methylcyclopentyl)dimethoxysilane, di-(3-methylcyclopentyl)dimethoxysilane, di-(2-ethylcyclopentyl)dimethoxysilane, di-(2,3-dimethylcyclopentyl)dimethoxysilane, di-(2,4-dimethylcyclopentyl)dimethoxysilane, di-(2,5-dimethylcyclopentyl)dimethoxysilane, di-(2,3-diethylcyclopentyl)dimethoxysilane, di-(2,3,4-trimethylcyclopentyl )dimethoxysilane, di-(2,3,5-trimethylcyclopentyl)dimethoxysilane, di-(2,3,4-triethylcyclopentyl)dimethoxysilane, di-(tetramethylcyclopentyl)dimethoxysilane, di-(tetraethylcyclopentyl)dimethoxysilane, di-(2-methylcyclopentenyl)dimethoxysilane, di-(3-methylcyclopentenyl)dimethoxysilane, di-(2-ethylcyclopentenyl)dimethoxysilane, di-(2-n-butylcyclopentenyl)dimethoxysilane, di-(2,3-dimethylcyclopentenyl)dimethoxysilane, di-(2,4-dimethylcyclopentenyl)dimethoxysilane, di-(2,5-dimethylcyclopentenyl)dimethoxysilane, di-(2,3,4-trimethylcyclopentenyl)dimethoxysilane, di-(2,3,5-trimethylcyclopentenyl)dimethoxysilane, di-(2,3,4-triethylcyclopentenyl)dimethoxysilane, di-(tetramethylcyclopentenyl)dimethoxysilane, di-(tetraethylcyclopentenyl)dimethoxysilane, di-(2-methylcyclopentadienyl)dimethoxysilane, di-(3-methylcyclopentadienyl)dimethoxysilane, di-(2-ethylcyclopentadienyl)dimethoxysilane, di-(2-n-butylcyclopentadienyl)dimethoxysilane, di-(2,3-dimethylcyclopentadienyl)dimethoxysilane, di-(2,4-dimethylcyclopentadienyl)dimethoxysilane, di-(2,5-dimethylcyclopentadienyl)dimethoxysilane, di-(2,3-diethylcyclopentadienyl)dimethoxysilane, di-(2,3,4-trimethylcyclopentadienyl)dimethoxysilane, di-(2,3,5-trimethylcyclopentadienyl)dimethoxysilane, di-(2,3,4-triethylcyclopentadienyl)dimethoxysilane, di-(2,3,4,5-tetramethylcyclopentadienyl)dimethoxysilane, di-(2,3,4,5-tetraethylcyclopentadienyl)dimethoxysilane, di-(1,2,3,4,5-pentamethylcyclopentadienyl)dimethoxysilane, di-(1,2,3,4,5-pentaethylcyclopentadienyl)dimethoxysilane, di-t-amyl-dimethoxysilane, di-(α,α'-dimethylbenzyl)dimethoxysilane, di-(admantyl)dimethoxysilane, admantyl-t-butyldimethoxysilane, cyclopentyl-t-butyldimethoxysilane, di-isopropyldimethoxysilane, di-s-butyldimethoxysilane, di-s-amyldimethoxysilane, and isopropyl-s-butyldimethoxysilane. When n is 3, the silicon compound of formula (i) includes monoalkoxysilanes such as tricyclopentylmethoxysilane, tricyclopentylethoxysilane, dicyclopentylmethylmethoxysilane, dicyclopentylethylmethoxysilane, dicyclopentylmethylethoxysilane, dicyclopentyldimethylmethoxysilane, cyclopentyldiethylmethoxysilane, and cyclopentyldimethylethoxysilane. Of these, dimethoxysilanes are preferred, in particular dicyclopentyldimethoxysilane, di-t-butyldimethoxysilane, di-(2-methylcyclopentyl)dimethoxysilane, di-(3-methylcyclopentyl)dimethoxysilane or di-t-amyldimethoxysilane. The catalyst used in the above process may be activated by copulverization or other means. Further, the catalyst may be prepolymerized with an olefin as described before. In preparing the polypropylene, an olefin prepolymerized solid titanium catalyst component is preferably used. The olefin for preparing the prepolymerized solid titanium catalyst component includes olefins having a branched structure such as 3-methyl-1-butene, 3-methyl-1-pentene, 3-ethyl-1-pentene, 4-methyl-1-pentene, 4-methyl-1-hexene, 4,4-dimethyl-1-hexene, 4,4-dimethyl-1-pentene, 4-ethyl-1-hexene, 3-ethyl-1-hexene, allylnaphthalene, allylnorbornene, stylene, dimethylstylenes, vinylnaphthalene, allyltoluenes, allylbenzene, vinylcyclohexane, vinylcyclopentane, vinylcycloheptane and allyltrialkylsilanes. Of these, preferred are 3-methyl-1-butene, 3-methyl-1-pentene, 3-ethyl-1-hexene, vinylcylcohexane, allyltrimethylsilane and dimethylstylene, more preferred are 3-methyl-1-butene, vinylcyclohexane and allyltrimethylsilane, and particularly preferred is 3-methyl-1-butene. Furthermore, linear chain olefins such as ethylene, propylene, 1-butene, 1-octene, 1-hexadecene and 1-eicocene may be used in combination with the above-mentioned branched olefins. Details of the process for preparing polypropylene using the support type catalyst component are described in, for example, Japanese Patent Laid-Open Nos. 108385/1975, 126590/1975, 20297/1976, 28189/1976 and 151691/1977. Further, details of the process for preparing a propylene block copolymer are described in, for example, Japanese Patent Laid-Open No. 98045/1977 and Japanese Patent No. 26613/1982. The techniques described in these publications can be applied to the present invention. (B-1) Ethylene/1-butene random copolymer The ethylene/1-butene random copolymer (B-1) contains 1-butene derived units in an amount of 15 to 25 % by mol, preferably 18 to 20 % by mol. The ethylene/1-butene random copolymer (B-1) containing units derived from 1-butene in such an amount as described above has a glass transition temperature of not higher than -50 °C, preferably not higher than -60 °C, and a melting point of not higher than 60 °C, preferably not higher than 50 °C. This melting point is measured as the main peak by a differential scanning calorimeter (DSC). The intrinsic viscosity [η] of the ethylene/1-butene random copolymer (B-1), as measured in decalin at 135 °C, is 1.5 to 3.5 dl/g, preferably 2.0 to 3.0 dl/g. The crystallinity thereof, as measured by X-ray diffractometry, is less than 20 %, preferably not more than 10 %. Further, in the ethylene/1-butene random copolymer (B-1), a parameter (B value) which indicates randomness of a copolymerized monomer chain distribution as measured by 13 C-NMR spectroscopy is from 1.0 to 1.4. The B value of the ethylene/1-butene random copolymer (B-1) is an index of composition distribution of constituent units derived from each monomer in the copolymer chain, and can be determined by dividing the molar fraction of the ethylene/1-butene alternating chain in all the dyad chains of the copolymer by a number twice as much as the product of the ethylene content (molar fraction) by the 1-butene content (molar fraction). That is, the B value can be calculated from the following formula: B= P BE 2P B ·P E wherein P E and P B are the molar fraction of the ethylene component and the molar fraction of the 1-butene component, respectively, contained in the ethylene/1-butene copolymer; and P BE is the molar fraction of the 1-butene/ethylene chain in all the dyad chains. The values for P E , P B and P BE can be obtained in the following manner. In a sample tube having a diameter of 10 mm, about 200 mg of ethylene/1-butene copolymer is homogeneously dissolved in 1 ml of hexachlorobutadiene to give a sample, and the 13 C-NMR spectrum of the sample is measured under the following conditions. Measuring temperature: 120 °C Measuring frequency: 25.05 MHz Spectrum width: 1,500 Hz Filter width: 1,500 Hz Pulse repetition period: 4.2 sec Pulse width: 7 µsec Integration times: 2,000 - 5,000 From the 13 C-NMR spectrum obtained as above, the P E , P B and P BE values can be concretely defined in accordance with the reports by, for example, G.J. Ray (Macromolecules, 10 , 773, 1977), J.C. Randall (Macromolecules, 15 , 353, 1982, J. Polymer Science, Polymer-Physics Ed., 11 , 275, 1973), and K. Kimura (Polymer, 25 , 441, 1984). The B value is 2 when the ethylene/1-butene random copolymer is a perfectly alternating copolymer, while the B value is 0 when the copolymer is a perfectly block copolymer. A polypropylene composition containing an ethylene/1-butene random copolymer (B-1) having a B value of less than 1.0 tends to have lowered impact resistance. The ethylene/1-butene random copolymer (B-1) as described above has good compatibility with polypropylene, and a polypropylene composition containing such a copolymer has excellent flowability as well as rigidity and impact resistance. Hence, such a polypropylene composition can be molded into articles having a good appearance. The ethylene/1-butene random copolymer (B-1) can be prepared using a conventionally known vanadium or metallocene catalyst. (B-2) Ethylene/1-octene random copolymer The ethylene/1-octene random copolymer (B-2) contains 1-octene derived units in an amount of 8 to 20 % by mol, preferably 10 to 15 % by mol. The ethylene/1-octene random copolymer (B-2) containing units derived from 1-octene in such an amount as described above has a glass transition temperature of not higher than -50 °C, preferably not higher than -60 °C, and a melting point of not higher than 80 °C, preferably not higher than 70 °C. This melting point is measured as the main peak by a differential scanning calorimeter (DSC). The intrinsic viscosity [η] of the ethylene/1-octene random copolymer (B-2), as measured in decalin at 135 °C, is 1.5 to 3.5 dl/g, preferably 2.0 to 3.0 dl/g. The crystallinity thereof, as measured by X-ray diffractometry, is less than 20 %, preferably not more than 10 %. Further, in the ethylene/1-octene random copolymer (B-2), a parameter (B value) which indicates randomness of a copolymerized monomer chain distribution as measured by 13 C-NMR spectroscopy is from 1.0 to 1.4. The B value of the ethylene/1-octene random copolymer (B-2) can be determined in a manner similar to that for the B value of the aforementioned ethylene/1-butene random copolymer. That is, the B value of the ethylene/1-octene random copolymer (B-2) can be calculated from the following formula: B= P OE 2P O ·P E wherein P E and P O are the molar fraction of the ethylene component and the molar fraction of the 1-octene component, respectively, contained in the ethylene/1-octene copolymer; and P OE is the molar fraction of the 1-octene/ethylene chain in all the dyad chains. A polypropylene composition containing an ethylene/1-octene random copolymer (B-2) having a B value of less than 1.0 tends to have lowered impact resistance. The ethylene/1-octene random copolymer (B-2) as described above has good compatibility with polypropylene, and a polypropylene composition containing such a copolymer has excellent flowability as well as rigidity and impact resistance. Hence, such a polypropylene composition can be molded into articles having a good appearance. The ethylene/1-octene random copolymer (B-2) can be prepared using a conventionally known vanadium or metallocene catalyst. Polypropylene composition The first polypropylene composition according to the present invention contains the polypropylene (A) in an amount of 95 to 55 parts by weight, preferably 85 to 65 parts by weight, and the ethylene/1-butene random copolymer (B-1) in an amount of 5 to 45 parts by weight, preferably 15 to 35 parts by weight (provided that (A)+(B-1) is 100 parts by weight). The second polypropylene composition according to the present invention contains the polypropylene (A) in an amount of 95 to 55 parts by weight, preferably 85 to 65 parts by weight, and the ethylene/1-octene random copolymer (B-2) in an amount of 5 to 45 parts by weight, preferably 15 to 35 parts by weight (provided that (A)+(B-2) is 100 parts by weight). These polypropylene compositions of the present invention have excellent rigidity, heat resistance and impact resistance, particularly low-temperature impact resistance. These polypropylene compositions may further comprise a propylene/ethylene random copolymer (C) in an amount of not more than 15 parts by weight, preferably 5 to 15 parts by weight, more preferably 5 to 10 parts by weight, based on 100 parts by weight of the above-mentioned polypropylene composition. The propylene/ethylene random copolymer (C) used for the invention contains constituent units derived from ethylene in an amount of 30 to 60 % by mol, preferably 35 to 45 % by mol. The propylene/ethylene random copolymer (C) has an intrinsic viscosity [η], as measured in decalin at 135 °C, of 2 to 12 dl/g, preferably 3 to 6 dl/g. A polypropylene composition containing the propylene/ethylene random copolymer (C) has excellent impact resistance, rigidity and flowability. In the polypropylene composition of the invention, the polypropylene (A) and the propylene/ethylene random copolymer (C) may be contained in the form of a block copolymer of polypropylene and a propylene/ethylene random copolymer. The polypropylene (A) and the propylene/ethylene random copolymer (C) may be prepared in the same reactor. The polypropylene composition according to the present invention may contain an inorganic filler if desired. The inorganic filler is preferably contained in the composition in an amount of 5 to 20 % by weight. Examples of the inorganic filler include finely powered talc, calcium carbonate, basic magnesium sulfate whiskers, calcium titanate whiskers and aluminium borate whiskers. The polypropylene composition of the present invention may further contain various additives, for example, polyethylene (PE), heat stabilizer, aluminium salts of aromatic carboxylic acids, esters or salts of aromatic phosphoric acids, nucleating agent such as dibenzylidene sorbitol, ultraviolet light absorber, lubricant, antistatic agent, flame retardant, pigment, dye, other polymers, organic filler and an ethylene/propylene random copolymer (EPR) other than the above-described one, with the proviso that the object of the present invention is not marred. The polypropylene composition of the present invention can be obtained by kneading the above-mentioned components all together or one after another by means of, for example, a Henschel mixer, a twin-cylinder blender, a tumbling blender or a ribbon blender, and then melt-kneading the resultant kneadate by means of, for example, a single screw extruder, a multiple screw extruder, a kneader or a Banbury mixer. Of these kneading devices, those showing high kneading performance such as a multiple screw extruder, a kneader and a Banbury mixer are preferably used, because a polypropylene composition of high quality wherein each component is homogeneously dispersed can be obtained by using them. The polypropylene composition of the present invention has excellent rigidity, heat resistance and impact resistance, particularly low-temperature impact resistance. The polypropylene composition of the invention having such excellent properties can be favorably applied to various uses, for example, to automotive interiors or exterior trims such as a bumpers. EXAMPLES The present invention will be further described below in more detail in the Examples. In the Examples, physical properties were measured in the following manner: (1) Melt flow rate (MFR) The melt flow rate (MFR) was measured in accordance with ASTM-D1238 under the conditions of a temperature of 230 °C and a load of 2.16 kg. (2) Flexural modulus (FM) The flexural modulus (FM) was measured in accordance with ASTM-D790 under the following conditions. Size of a specimen: 12.7 mm (width) × 6.4 mm (thickness) × 127 mm (length) Span: 100 mm Flexural rate: 2 mm/min (3) Izod impact strength (IZ) The izod impact strength (IZ) was measured in accordance with ASTM-D256 under the following conditions. Temperature: 23 °C Size of a specimen: 12.7 mm (width) × 6.4 mm (thickness) × 64 mm (length) Notch: A notch is provided by a mechanical process. Examples 1 - 8 Polypropylene compositions set forth in Table 2 were molded into specimens for ASTM tests in an injection molding machine under the conditions of a resin temperature of 200 °C and a mold temperature of 40 °C. The specimens were measured for the above-mentioned physical properties. The results are set forth in Table 2. The components used for preparing the polypropylene compositions are set forth in Table 1, wherein the physical properties of each components are also set forth. The abbreviations for each component in Table 1 and Table 2 have the following meanings: (A) Polypropylene (1) PP-A: polypropylene (trade name: HYPOL J800) available from Mitsui Petrochemical Industries, Ltd. (2) PP-B: high-crystalline homopolypropylene prepared by the following process [Preparation of catalyst] 95.2 g of magnesium chloride anhydride, 442 ml of decane and 390.6 g of 2-ethylhexyl alcohol were heated together at 130 °C for 2 hours to give a homogeneous solution. To the solution was added 21.3 g of phthalic anhydride, and the mixture was stirred at 130 °C for 1 hour to dissolve the phthalic anhydride in the solution to give a homogeneous solution. The homogeneous solution thus obtained was cooled to room temperature, and 75 ml of this solution was then dropwise added to 200 ml of titanium tetrachloride kept at -20 °C over a period of 1 hour. After the addition was completed, the resultant mixture was heated to 110 °C over a period of 4 hours. When the temperature of the mixture reached 110 °C, 5.22 g of diisobutyl phthalate (DIBP) was added to the mixture, which was then stirred for 2 hours at the same temperature. After completion of the 2-hour reaction, a solid portion produced by the reaction was collected by hot filtration. The solid portion was suspended again in 275 ml of titanium tetrachloride, and the resultant suspension was heated at 110 °C for 2 hours to perform a reaction. After the reaction was completed, a solid portion produced by the reaction was again collected by hot filtration, and the solid portion was washed well with decane and hexane at 110 °C until no titanium compound was detected in the washing liquid. The solid titanium catalyst component [A] obtained by the above process was stored as a decane slurry. [Polymerization] Into a 17-liter autoclave was introduced 4 kg of propylene and 45 liters of hydrogen at room temperature in a propylene atmosphere, and the temperature of the autoclave was elevated to 60 °C. Then, to the autoclave were added 5.0 mmol of triethylaluminum, 5.0 mmol of dicyclopentyldimethoxysilane (DCPMS) and 0.05 mmol (in terms of Ti atom) of the above-obtained solid titanium catalyst component [A], and the temperature of the autoclave was further elevated to 70 °C to perform polymerization reaction at the same temperature for 40 minutes. Immediately after the reaction was completed, a small amount of ethanol was added to the reaction system to decompose the catalyst, and the unreacted propylene and hydrogen were removed from the system. Thus, 1,515 g of polypropylene was obtained as a powdery white solid. The polypropylene thus obtained had an MFR of 15 g/10 min. (3) PP-C: high-crystalline homopolypropylene prepared using a prepolymerized catalyst described below [Preparation of prepolymerized catalyst] A pressure-resistant 2-liter autoclave was charged with 1 liter of purified hexane, 100 mmol of triethylaluminium, 100 mmol of trimethylmethoxysilane (TMMS) and 10 mmol (in terms of titanium atoms) of the above-mentioned solid titanium catalyst component [A] at 20 °C in a nitrogen atmosphere, and the content of the autoclave was stirred. Then, to the mixture in the autoclave was added 115 g of 3-methyl-1-butene to perform a prepolymerization reaction at 20 °C for 2 hours with stirring. After the reaction was completed, the supernatant liquid was removed, and the residue was washed twice with purified hexane and suspended in purified decane. The whole amount of the resultant suspension was transferred into a catalyst bottle. Thus, a prepolymerized catalyst was obtained. [Polymerization] Using the above-obtained prepolymerized catalyst, homopolymerization of propylene was carried out in a manner similar to that for preparing the PP-B (polypropylene-B). The polypropylene thus obtained had an MFR of 15.5 g/10 min. (4) PP-D: block polypropylene prepared by the following process A 17-liter autoclave was thoroughly purged with propylene. Into the autoclave were introduced 4 kg of propylene and 60 liters of hydrogen, and the temperature of the autoclave was elevated to 60 °C. Then, to the autoclave were added 5.0 mmol of triethylaluminium, 5.0 mmol of dicyclopentyldimethoxysilane (DCPMS) and 0.05 mmol (in terms of Ti atom) of the above-mentioned solid titanium catalyst component [A], to perform polymerization at 80 °C for 1 hour. Liquid propylene was removed from the reaction system, and 100 liters of ethylene and 150 liters of propylene were added to the reaction system over 150 minutes. Then, the unreacted mixed gas was removed from the system to obtain 2.1 kg of block polypropylene as a powdery white solid. The block polypropylene thus obtained had an MFR of 22 g/10 min, contained constituent units derived from ethylene in an amount of 8.0 % by weight, contained an n-decane-soluble portion in an amount of 11.1 % by weight at room temperature, and had an intrinsic viscosity [η] of the soluble portion of 3.0 dl/g. (B-1) Ethylene/1-butene random copolymer EBR-1: Constituent units derived from 1-butene : 19 % by mol Intrinsic viscosity [η] : 2.5 dl/g (B-2) Ethylene/1-octene random copolymer EOR: Constituent units derived from 1-octene : 13 % by mol Intrinsic viscosity [η] : 2.3 dl/g ( C) Propylene/ethylene random copolymer PER-1: Constituent units derived from ethylene : 40 % by mol Intrinsic viscosity [η] : 3.0 dl/g Others EBR-2: Constituent units derived from 1-butene : 11 % by mol Intrinsic viscosity [η] : 1.8 dl/g EPR (Ethylene/propylene random copolymer): Constituent units derived from ethylene : 80 % by mol Intrinsic viscosity [η] : 2.6 dl/g PE (Polyethylene): Hizex 1300J (trade name) available from Mitsui Petrochemical Industries, Ltd. Talc: Mean particle diameter : 2.5 µm Content of particles having a diameter of not less than 5 µm : 3 % by weight Comparative Examples 1 - 5 Polypropylene compositions set forth in Table 2 were molded into specimens in the same manner as described above. The specimens were measured for the aforementioned physical properties. The results are set forth in Table 2. The physical properties of each component of the polypropylene compositions are set forth in Table 1. Examples 9 - 11 The polypropylene compositions set forth in Table 2 were molded into specimens for ASTM tests by an injection molding machine under the conditions of a resin temperature of 200 °C and a mold temperature of 40 °C. The specimens were measured for the aforementioned physical properties. The results are set forth in Table 2. The physical properties of each component used for preparing the polypropylene compositions are set forth in Table 1.

Claims: Use of a polypropylene composition for automotive interior or exterior trim, wherein said composition comprises: (A) a propylene homopolymer; and (B-1) an ethylene/1-butene random copolymer having a content of 1-butene derived units from 15 to 25% by mol, an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin at 135 °C, a melting point of not higher than 60 °C as measured by a differential scanning calorimeter (DSC) as the main peak, a glass transition temperature (Tg) of not higher than -50 °C, a crystallinity of less than 20% as measured by X-ray diffractometry, and a randomness parameter (B value) of 1.0 to 1.4 as measured by 13 C-NMR spectroscopy wherein B = P BE 2P B ·P E wherein P E and P B are the molar fraction of the ethylene component and the molar fraction of the 1-butene component, respectively, and P BE is the molar fraction of the 1-butene/ethylene chain in all the dyad chains; the weight ratio of (A):(B-1) being from 95:5 to 55:45. Use according to claim 1, wherein said polypropylene composition further comprises: (C) a propylene/ethylene copolymer in an amount of not more than 15% by weight of the combined weight of propylene homopolymer (A) and ethylene/1-butene random copolymer (B-1), the propylene/ethylene copolymer having a content of ethylene derived units from 30 to 60% by mol and an intrinsic viscosity [η] of 2 to 12 dl/g as measured in decalin at 135 °C. Use according to claim 2, wherein the propylene/ethylene random copolymer (C) is in the form of a block copolymer of polypropylene and a propylene/ethylene random copolymer. Use according to any one of the preceding claims, wherein the polypropylene composition further comprises an inorganic filler in an amount of 5 to 20% by weight. Use according to claim 4, wherein the inorganic filler is talc. Use according to any one of the preceding claims, wherein the propylene homopolymer (A) is obtainable by polymerization using a catalyst formed from a solid titanium catalyst component supported on a support material, an organometallic catalyst component and dicyclopentyldimethoxysilane as an electron donor. Use according to any one of the preceding claims, wherein the propylene homopolymer (A) is obtainable by polymerization using a catalyst obtainable by prepolymerizing 3-methyl-1-butene. A polypropylene composition comprising: (A) a polypropylene; (B-1) an ethylene/1-butene random copolymer having a content of 1-butene derived units from 15 to 25% by mol, an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin at 135 °C, a melting point of not higher than 60 °C as measured by a differential scanning calorimeter (DSC) as the main peak, a glass transition temperature (Tg) of not higher than -50 °C, a crystallinity of less than 20% as measured by X-ray diffractometry, and a randomness parameter (B value) of 1.0 to 1.4 as measured by 13 C-NMR spectroscopy wherein B = P BE 2P B ·P E wherein P E and P B are the molar fraction of the ethylene component and the molar fraction of the 1-butene component, respectively, and P BE is the molar fraction of the 1-butene/ethylene chain in all the dyad chains; the weight ratio of (A):(B-1) being from 95:5 to 55:45; and (C) a propylene/ethylene copolymer in an amount of not more than 15% by weight of the combined weight of polypropylene (A) and ethylene/1-butene random copolymer (B-1), the propylene/ethylene copolymer having a content of ethylene derived units from 35 to 60% by mol and an intrinsic viscosity [η] of 2 to 12 dl/g as measured in decalin at 135 °C. A polypropylene composition comprising: (A) a polypropylene; (B-2) an ethylene/1-octene random copolymer having a content of 1-octene derived units from 8 to 20% by mol, an intrinsic viscosity [η] of 1.5 to 3.5 dl/g as measured in decalin at 135 °C, a melting point of not higher than 80 °C as measured by a differential scanning calorimeter (DSC) as the main peak, a glass transition temperature (Tg) of not higher than -50 °C, a crystallinity of less than 20% as measured by X-ray diffractometry, and a randomness parameter (B value) of 1.0 to 1.4 as measured by 13 C-NMR spectroscopy wherein B = P OE 2P O ·P E wherein P E and P O are the molar fraction of the ethylene component and the molar fraction of the 1-octene component respectively, and P OE is the molar fraction of the 1-octene/ethylene chain in all the dyad chains; the weight ratio of (A):(B-2) being from 95:5 to 55:45. A composition according to claim 9 further comprising: (C) a propylene/ethylene copolymer in an amount of not more than 15% by weight of the combined weight of polypropylene (A) and ethylene/1-octene random copolymer (B-2), the propylene/ethylene copolymer having a content of ethylene derived units from 30 to 60% by mol and an intrinsic viscosity [η] of 2 to 12 dl/g as measured in decalin at 135 °C. A composition according to any one of claims 8 to 10, wherein the polypropylene (A) and the propylene/ethylene random copolymer (C) are in the form of a block copolymer of polypropylene and a propylene/ethylene random copolymer. A composition according to any one of claims 8 to 11, wherein the polypropylene composition further comprises an inorganic filler in an amount of 5 to 20% by weight. A composition according to claim 12, wherein the inorganic filler is talc. A composition according to any one of claims 8 to 13, wherein the polypropylene (A) is obtainable by polymerization using a catalyst formed from a solid titanium catalyst component supported on a support material, an organometallic catalyst component and dicyclopentyldimethoxysilane as an electron donor. A composition according to any one of claims 8 to 14, wherein the polypropylene (A) is obtainable by polymerization using a catalyst obtainable by prepolymerizing 3-methyl-1-butene. A molded article comprising a polypropylene composition as claimed in any one of claims 8 to 15.

Inventors: ISHIMOTO AKIO, SUGI MASAHIRO, WAKUMOTO HIROSHI, YAMAGUCHI MASAYOSHI, ISHIMOTO, AKIO, SUGI, MASAHIRO, WAKUMOTO, HIROSHI, YAMAGUCHI, MASAYOSHI, ISHIMOTO, AKIO, C/O MITSUI PETROCHEMICAL, SUGI, MASAHIRO, C/O MITSUI PETROCHEMICAL, WAKUMOTO, HIROSHI, C/O MITSUI PETROCHEMICAL, YAMAGUCHI, MASAYOSHI, C/O MITSUI PETROCHEMICAL
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1993
Main classification: C08L23
IPC codes: C08L23, C08L53