OLEFIN SKELETAL ISOMERIZATION PROCESS USING ZSM-35

Abstract: A process is disclosed for the highly selective skeletal isomerization of linear olefin-containing organic feeds wherein linear olefins, e.g., n-butenes, are contacted with catalyst comprising ZSM-35, preferably microcrystalline ZSM-35 having its largest crystal dimension no greater than 0.5 micron, under isomerization conditions to produce iso-olefins of corresponding carbon number, e.g., isobutene.

Description: O EFIN SKELETAL ISOMERIZATION PROCESS USING ZSM-35 This invention relates to a method for the selective conversion of linear olefins to corresponding iso-olefins of the same carbon number. The demand for iso-alkenes has recently increased. For example, relatively large amounts of isobutene are required for reaction with methanol or ethanol over an acidic catalyst to produce methyl tert-butyl ether (MTBE) or ethyl tert-butyl ether (ETBE) which is useful as an octane enhancer for unleaded gasolines. Isoamylenes are required for reaction with methanol over an acidic catalyst to produce tert-amyl methyl ether (TAME) . With passage of the Clean Air Act in the United States mandating increased gasoline oxygenate content, MTBE, ETBE and TAME have taken on new value as a clean-air additive, even for lower octane gasolines. Lead phasedown of gasolines in Western Europe has further increased the demand for such oxygenates. An article by J.D. Chase, et al., Oil and Gas Journal. April 9, 1979, discusses the advantages one can achieve by using such materials to enhance gasoline octane. The blending octane values of MTBE when added to a typical unleaded gasoline base fuel are RON = 118, MON = 101, R+M / 2 = 109. The blending octane values of TAME when added to a typical unleaded gasoline base fuel are RON = 112, MON = 99, R+M / 2 = 106. Isobutene (or isobutylene) is in particularly high demand as it is reacted with methanol to produce MTBE. The addition of shape-selective zeolite additives such as ZSM-5 to cracking catalysts, e.g. those used in fluidized catalytic cracking (FCC) , is beneficial in producing gasoline boiling range product of increased octane rating. However, increased amounts of olefins result, including n-butenes, creating a need for their conversion to higher value products such as isobutene which can be used to produce MTBE. Butene exists in four isomers: butene-1, cis- butene-2, its stereo-isomer trans-butene-2, and isobutene. Conversion between the butenes-2 is known as geometric isomerization, whereas that between butene-1 and the butenes-2 is known as position isomerization, double-bond migration, or hydrogen-shift isomerization. The aforementioned three isomers are not branched and are known collectively as normal or n-butenes. Conversion of the n-butenes to isobutene, which is a branched isomer, is widely known as skeletal isomerization. The reaction of tertiary olefins with alkanol to produce alkyl tertiary alkyl ether is selective with respect to iso-olefins. Linear olefins are unreactive in the acid catalyzed reaction, even to the extent that it is known that the process can be utilized as a method to separate linear and iso-olefins. The typical feedstream of FCC C4 or C4+ crackate used to produce tertiary alkyl ethers in the prior art which contains normal butene and isobutene utilizes only the branched olefin in etherification. This situation presents an exigent challenge to workers in the field to discover a technically and economically practical means to utilize linear olefins, particularly normal butene, in the manufacture of tertiary alkyl ethers. In recent years, a major development within the petroleum industry has been the discovery of the special catalytic capabilities of a family of zeolite catalysts based upon medium pore size shape selective metallosilicates. Discoveries have been made leading to a series of analogous processes drawn from the catalytic capability of zeolites in the restructuring of olefins. European Patent 0026041 discloses a process for the restructuring of olefins in contact with zeolite catalyst to produce iso-olefins, followed by the conversion of iso-olefins to MTBE and TAME. The restructuring conditions comprise temperature between 204oC and 315oC and pressure below 51 kPa. In European Patent 0247802, it is taught that linear olefins can be restructured in contact with zeolite catalyst, including Theta-1 (ZSM-22) and ZSM- 23, to produce branched olefins. The restructuring conditions comprise temperature between 200-550oC, pressure between 100 and 5000 kPa and WHSV between 1 and 100. Selectivities to isobutene up to 91.2% are reported using a calcined Theta-1 tectometallosilicate at 400°C and 30.6% 1-butene conversion. U.S. Patent No. 4,922,048 discloses the use of a wide variety of medium pore size zeolites, e.g. ZSM-5, ZSM-11, ZSM-12, ZSM-22, ZSM-23, ZSM-35 and ZSM-48, in low temperature (232-385°C) olefin interconversion of C2-C6 olefins to products including tertiary C4-C5 olefins and olefinic gasoline. U.S. Patent No. 4,886,925 discloses low pressure high temperature conversion of light olefins to produce higher olefins rich in isoalkenes. The process converts C2+ n-alkenes to a product comprising C4-C6 alkenes rich in iso-alkenes, C7+ olefinic gasoline boiling range hydrocarbons, and unconverted hydrocarbons over ZSM-5. The reference teaches further treatment of the alkene effluent with methanol in the presence of medium pore size zeolites such as ZSM-5, ZSM-11, ZSM-12, ZSM-35, and ZSM-48. U.S. Patent No. 4,996,386 discloses concurrent isomerization and disproportionation of olefins using a ferrierite/Mo/W/Al203 catalyst. The catalyst exemplified produces fewer branched olefins than a comparable material free of ferrierite and the reference teaches that ferrierite-containing catalysts exhibit improved selectivity to linear olefins than conventionally prepared disproportionation catalysts. Despite the efforts exemplified in the above references, the skeletal isomerization of olefins e.g., to produce isobutene, has been hampered by relatively low selectivity to isobutene perhaps owing to the lability of these olefins. It is further known that skeletal isomerization becomes more difficult as hydrocarbons of lower molecular weight are used, requiring more severe operating conditions, e.g. higher temperatures and lower linear olefin partial pressures. Generally, the conversion of n-butenes to iso- butene is conducted at selectivities below 90%. In order to obtain higher selectivities, operation at high temperatures (>500°C) and with high nitrogen feed dilution (butene partial pressure, typically less than 5 psia (34.5 kPa) ) is generally required. Selectivities of greater than 90%, 95% or even 99% are highly advantageous in commercial conversion of n-butenes to isobutene in order to avoid the need to separate out materials other than n-butene from the product stream. Such high selectivities will permit direct introduction (cascading) or indirect introduction of the isomerizer effluent to an etherification zone where isobutene is reacted with alkanol to produce alkyl tert-butyl ether, e.g. MTBE. Unconverted n-butenes in the isomerizer effluent can be withdrawn either before the etherifica- tion zone or preferably, from the etherification zone effluent insofar as the etherification reaction utilizes only the isobutene component of the isomerizer stream. Unreacted n-butenes from the etherification zone effluent can be recycled to the isomerizer where they are converted to isobutene at high selectivity. If the recycle stream contains not only unconverted linear olefins, e.g. n-butenes, but also by-product such as other olefins (e.g. propylene) or paraffins, they have to be removed from the recycle stream, such as by distillation or by taking a slip stream. These removal steps are expensive and can lead to considerable loss of not only the by-products but butenes as well. These losses are larger when the by-products formed are present in higher concentration. Thus, even small improvements in the isobutene selectivity during n-butene isomerization have a major effect on the commercial viability of the process. However, high selectivities in skeletal isomerization processes have generally required low linear olefin partial pressures and high temperatures which place substantial limitations on such processes. It would, therefore, be advantageous to provide a skeletal isomerization catalyst capable of maintaining relatively high selectivity at low temperatures and high linear olefin partial pressures. Further enhancement of total yield of iso-olefin can be effected by enhancing overall conversion of the n-olefin-containing feedstream. With this object in mind, it would be advantageous to provide a skeletal isomerization catalyst capable of maintaining a high level of conversion as well as high iso-olefin selectivity, even at relatively low temperatures, e.g., no greater than 450°C and high n-olefin space velocities, e.g., no less than 5, e.g., no less than 70. Moreover, as with any catalytic process, it is desirable to provide a catalyst which has a long cycle life. Accordingly, the present invention provides a method for highly selective conversion of linear olefins to corresponding iso-olefins of the same carbon number, e.g. n-butenes to isobutene, which comprises contacting a linear olefin-containing organic feedstock with a catalyst comprising ZSM-35 . Preferably, the catalyst comprises microcrystal- line ZSM-35, by which is meant that the zeolite has a crystal morphology whose largest dimension is no greater than 0.5 micron, and whose ratio of its second largest dimension to said largest dimension ranges from about 0.5 to 1. Preferably, the ZSM-35 is composited with a silica-containing matrix so that the catalyst composite has a total pore volume of at least 0.6 cc/g or 300+ angstroms pore volume of at least 0.1 cc/g. The high selectivity of ZSM-35 in the present invention results in large part from isomerization occurring without significant conversion to lighter and heavier molecules. This phenomenon, it is believed, is a consequence of the pore structure of ZSM-35 which promotes isomerization at a much faster rate than the reaction by which, e.g. butene, is converted to lighter (mostly propylene) and heavier olefins (olefin interconversion reaction) . Moreover, such isomeriza¬ tion takes place without significant cracking of the feed or hydrogenation or dehydrogenation effects resulting in the formation of, say, n-butane or butadiene. The present invention can be used to effect conversion of linear olefins to iso-olefins while resulting in less than 30%, 10%, 5% or even less than 1% by weight of converted product having lower or higher average carbon number. The use of microcrystalline ZSM-35 allows the highly selective olefin isomerization of the present invention to be conducted at higher conversion levels. In addition, it is found that the use of a highly porous, silica-bound catalyst composite reduces catalyst aging. The skeletal isomerization reaction of the present invention is carried out at temperatures of from 100 to 750°C, weight hourly space velocity based on linear olefin in the feed of from 0.1 to 500 and linear olefin partial pressures of from 2 to 2000 kPa. The preferred conditions are a temperature of 150 to 600°C, most preferably 200 to 550°C; weight hourly space velocity based on linear olefin in the feed of 0.5 to 400, most preferably 1 to 100; and a linear olefin partial pressure of 10 to 500 kPa, most preferably 20 to 200 kPa. Under these conditions the conversion of linear olefin, e.g., n-butene, can be at least 10%, preferably at least 35% and more preferably at least 45%. The selectivity to iso-olefin, e.g., isobutene, is at least 75%, preferably at least 85%, 90%, or even 95%. Preferred feedstreams include C4 or C4+ hydrocarbon feedstreams. Linear olefins suited for use in the present invention may be derived from a fresh feedstream, preferably comprising n-butenes and/or n- pentenes, or from the effluent of an iso-olefin etherification reactor which employs alkanol and C4 or C4+ hydrocarbon feedstock. Typical hydrocarbon feedstock materials for isomerization reactions according to the present invention include olefinic streams, such as cracking process light gas containing butene isomers in mixture with substantial amounts of paraffins including n-butane and isobutane. The C4 components usually contain a major amount of un- saturated compounds, such as 10-40% isobutene, 20-55% linear butenes, and small amounts of butadiene. Also, C4+ heavier olefinic hydrocarbon streams may be used, e.g C4 to CIO, preferably C4 to C6 olefinic hydrocarbon streams. The process of the invention employs a catalyst comprising the zeolite ZSM-35. ZSM-35 is more particularly described in U.S. Patent No. 4,016,245. For present purposes, "ZSM-35" is considered equivalent to its isotypes, which include ferrierite (P.A. Vaughan, Acta Cryst. 21, 983 (1966)); FU-9 (D. Seddon and T. V. Whittam, European Patent B-55,529, 1985) ; ISI-6 (N. Morimoto, K. Takatsu and M. Sugimoto, U.S. Patent 4,578,259, 1986); monoclinic ferrierite (R. Gramlich-Meier, V. Gramlich and W. M. Meier, Am. Mineral. 20, 619 (1985)); NU-23 (T. V. Whittam, European Patent A-103,981, 1984); and Sr-D (R. M. Barrer and D. J. Marshall, J. Chem. Soc. 1964, 2296 (1964)). An example of a piperidine-derived ferrierite is more particularly described in U.S. Patent No. 4,343,692. Other synthetic ferrierite preparations are described in U.S. Patent Nos. 3,933,974; 3,966,883; 4,000,248; 4,017,590; and 4,251,499. Further descriptions of ferrierite are found in Bibby et al, "Composition and Catalytic Properties of Synthetic Ferrierite," Journal of Catalysis, 35, pages 256-272 (1974) . Preferably, the ZSM-35 used in the process of the invention is in a microcrystalline form in that it has a morphology whose largest dimension is no greater than 0.5 micron, preferably no greater than 0.25 micron and more preferably no greater than 0.15 micron, and whose ratio of its second largest dimension to its largest dimension is 0.5 to 1.0. Most preferably the ZSM-35 crystals can be described as falling within the range of 0.03 to 0.08 micron by 0.03 to 0.08 micron by < 0.05 micron. Microcrystalline ZSM-35 is made by control of the synthesis formulation and synthesis temperature, with lower temperature favoring smaller crystals. The zeolite catalyst used is preferably at least partly in the hydrogen form, e.g., HZSM-35, but other cations, e.g., rare earth cations, may also be present. When the zeolites are prepared in the presence of organic cations, they may be quite inactive possibly because the intracrystalline free space is occupied by the organic cations from the forming solution. The zeolite may be activated by heating in an inert atmosphere to remove the organic cations e.g., by heating at over 500°C for 1 hour or more. The hydrogen form can then be obtained by base exchange with ammonium salts followed by calcination e.g., at 500°C in air. Other cations, e.g., metal cations, can be introduced by conventional base exchange or impregnation techniques. In order to obtain the desired linear olefin skeletal isomerization activity/selectivity, the ZSM-35 should have an alpha value of at least 5, preferably at least 50 when used in the catalyst of the present invention. Alpha value, or alpha number, of a zeolite is a measure of zeolite acidic functionality and is more fully described together with details of its measurement in U.S. Patent No. 4,016,218, J. Catalysis. 6_, pp. 278-287 (1966) and J. Catalysis. 61. pp. 390-396 (1980) . The ZSM-35 may be incorporated in another material usually referred to as a matrix or binder. Such matrix materials include synthetic or naturally occurring substances as well as inorganic materials such as clay, silica and/or metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates or " gels including mixtures of silica and metal oxides. Naturally occurring clays which can be composited with the zeolite include those of the montmorillonite and kaolin families, which families include the subbentonites and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, the zeolites employed herein may be composited with a porous matrix material, such as silica, alumina, zirconia, titania, silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel. A mixture of these components could also be used. The relative proportions of finely divided ZSM-35 and inorganic oxide gel matrix may vary widely with the zeolite content ranging from 1 to 90 percent by weight and more usually in the range of 30 to 80 percent by weight of the composite. Of all the foregoing materials, silica is preferred as the matrix material owing to its relative inertness for catalytic cracking reactions which are preferably minimized in the instant isomerization processes. Alternatively, silica-containing matrix containing a minor amount of aluminum may be employed. It is believed that using a silica binder and controlling extrusion conditions by means such as moisture control to ensure increased pore volume results in a catalyst which ages more slowly under skeletal isomerization conditions, resulting in increased cycle length. Such conditions increase total pore volume to greater than 0.6 g/cc, or 300 angstroms pore volume to greater than 0.1 cc/g. These increased pore volumes can be obtained by increasing moisture content of the extrudate. The resulting catalyst composite is of particular utility insofar as its use can result in increased cycle length without any significant loss of iso-olefin selectivity. The regeneration of spent zeolite catalyst used in the isomerization reaction is carried out oxidatively or hydrogenatively employing procedures known in the art. The catalyst of the present invention can be readily reactivated without significantly reducing selectivity for isobutene by exposing it to hydrogen for a suitable period, e.g. overnight. The invention will now be more particularly described with reference to the Examples and the accompanying drawings, in which: Figure 1 depicts the respective conversions and products obtained for ZSM-22, ZSM-23 and ZSM-35 in skeletal isomerization of 1-butene at 550°C. Figure 2 depicts the respective conversions and products obtained for ZSM-22, ZSM-23 and ZSM-35 in skeletal isomerization of 1-butene at 400 β C. Figure 3 is a selectivity/conversion plot comparing the performance of ZSM-23 and ZSM-35. Figure 4 depicts the conversions and products obtained for ZSM-35 in skeletal isomerization of 1- butene at high WHSV, low temperatures and high butene partial pressures. Figure 5 is a transmission electron microscopy (TEM) micrograph of a microcrystalline ZSM-35 sample prepared in accordance with the procedure set out in Example 1. Figure 6 is a transmission electron microscopy (TEM) micrograph of large crystal ZSM-35 of Example 12. Figure 7 is a transmission electron microscopy (TEM) micrograph of large crystal synthetic ferrierite of Example 13. Figure 8 depicts 1-butene conversion and iso-butene selectivity over temperature at 165 WHSV from Example 14. Figure 9 depicts 1-butene conversion and iso-butene selectivity over temperature at 2 WHSV from Example 15. Figure 10 depicts the low aging rate of microcrystalline ZSM-35 compared to large crystal synthetic ferrierite where n-butene conversion is plotted as a function of cumulative 1-butene throughput. Figure 11 compares the aging rates of alumina-bound ZSM-35 catalyst from Example 16 and silica-bound ZSM-35 catalyst of enhanced pore volume from Example 17. Figure 12 compares selectivity versus conversion in n-butene conversion for the alumina-bound catalyst of Example 16 and the silica-bound catalyst of enhanced pore volume from Example 17. Figure 13 compares the effects of binder pore size on ZSM-35 aging in butene skeletal isomerization for the small pore silica-bound catalyst of Example 4, versus the large-pore silica-bound catalyst of Example 17. Figure 14 compares selectivity versus conversion for the small pore silica-bound catalyst of Example 4, compared with the large-pore silica-bound catalyst of Example 17. EXAMPLE 1 Preparation of Microcrystalline ZSM-35 1.18 parts of aluminum sulfate (17.2% A1203) were added to a solution containing 9.42 parts H20 and 1.38 parts of 50% NaOH solution in an autoclave. 0.03 parts of ZSM-35 seeds and 3.20 parts of Hi-Sil precipitated silica were added with agitation, followed by 1.0 part of pyrrolidine. The reaction mixture had the following composition, in mole ratios: Si02/A1203 21.5 OH-/Si02 0.11 H20/A1203 13.5 R/A1203 6.45 where R = pyrrolidine. The mixture was crystallized at 105°C for 74 hours with stirring. The ZSM-35 product was filtered, washed with deionized water, and dried at 120°C. The chemical composition of the product was, in weight percent: Si02 76.7 A1203 6.4 Na 0.84 C 7.26 N 2.03 Ash @ 1000 β C 85.5 with a silica/alumina ratio for the product, in moles, of 20.3/1. Scanning electron microscopy and transmission electron microscopy indicate the ZSM-35 crystals have platelet morphology with a broad distribution of crystal sizes having the largest dimension of up to 0.05 to 0.1 micron. Figure 5 is a TEM micrograph of the ZSM-35 thus prepared. EXAMPLE 2 Preparation of HZSM-35/Si02 Mix The as-synthesized ZSM-35 of Example 1 was calcined in nitrogen for 3 hours at 538°C, then exchanged two times at room temperature with 1 N NH4N03 solution to convert it to the ammonium form, dried at 120°C, and calcined in air for 6 hours at 538°C to convert it to the hydrogen form. The zeolite was dry mixed with a precipitated silica, in proportion to give 65% ZSM-35 / 35% silica after calcination, formed into pellets, and calcined in air for 3 hours at 538°C. EXAMPLE 3 Preparation of Silica-Bound HZSM-35 A catalyst was prepared by dry mixing the as- synthesized ZSM-35 of Example 1 with precipitated silica, in proportion to give, after calcination, 65% ZSM-35 / 35% silica in the catalyst. A solution containing 2% NaOH (based on solids) was added to the mix to create an extrudable mull, the mix was extruded to 1/16 inch (1.6 mm) diameter and dried at 120°C. The extrudate was exchanged two times with IN NH4N03 solution at room temperature, rinsed with deionized water, dried at 120°C and calcined in nitrogen for 3 hours at 538 β C. It was again exchanged with IN NH4N03 solution two times at room temperature, dried at 120°C, and calcined in air for 9 hours at 538"C. EXAMPLE 4 Preparation of Silica-Bound HZSM-35 A catalyst was prepared by dry mixing the as- synthesized ZSM-35 of Example 1 with precipitated silica. Colloidal silica, in proportion to give 65% ZSM-35 / 35% silica after calcination, and water were added to the dry mix to obtain an extrudable mull. The mull was extruded to 1/16 inch (1.6 mm) diameter, dried at 120 β C, calcined in nitrogen for three hours at 538°C, and then in air for 6 hours at 538°C. The extrudate was exchanged two times with IN NH4N03 solution at room temperature, dried at 120"C and calcined in nitrogen for 3 hours at 538°C. The total pore volume of this catalyst was 0.55 cc/g and 300 angstrom pore volume was 0.04 cc/g. EXAMPLE 5 Isomerization of 1-Butene with ZSM-22, ZSM-23 and ZSM-35 at 550°C ZSM-22 was prepared by charging 48.2 parts water to an autoclave followed by 5.0 parts KOH solution (45% by weight), 1.0 part aluminum sulfate (17.2% A1203) and 0.45 parts seeds. After mixing thoroughly, 8.2 parts of Ultrasil VN3 precipitated silica (Nasilco), then 3.6 parts of ethylpyridinium bromide (50% by weight) were added and mixed thoroughly. After aging the reaction mixture for 16 hours at 93°C while stirring, the temperature was increased to 160"C and maintained until crystallization was complete. The product was identified as ZSM-22 by X-ray diffraction. The slurry was filtered, washed and dried. A portion of the zeolite was calcined in flowing nitrogen for 3 hours at 538°C and 3 hours in air at the same temperature. The cooled zeolite was exchanged with 1 N NH4N03 (5 cc/g zeolite) at room temperature for one hour then washed with water. The exchange procedure was repeated and the catalyst dried at 120°C. The zeolite was then calcined in flowing air for 3 hours at 538 β C, then blended 65 parts zeolite and 35 parts Ultrasil VN3 and pelleted. The pellets were sized 14/24 mesh and recalcined at 538°C in flowing air for 3 hours. ZSM-23 was prepared by charging 85.5 parts water to an autoclave followed by 2.64 parts KOH solution (45% by weight), 1.0 part aluminum sulfate (17.2% A1203) and 0.5 parts ZSM-23 seeds (100% basis). After mixing thoroughly, 14.5 parts of Ultrasil VN3 precipitated silica (Nasilco), then 5.1 parts of pyrrolidine were added and mixed thoroughly. The autoclave was heated to 160"C with stirring and maintained at these conditions until crystallization was complete. The product was identified as ZSM-23 by X-ray diffraction. After flashing the pyrrolidine, the slurry was cooled, washed, filtered and dried. Eight parts of the dried ZSM-23 were combined with 1 part Ultrasil VN3 and 1 part Ludox colloidal silica (DuPont) , mulled and extruded to form 1/16 inch pellets which were dried at 120"C. The pellets were then calcined in flowing nitrogen for 2 hours at 538°C and 3 hours in air at the same temperature. The cooled catalyst was exchanged with 1 N NH4N03 (5 cc/g catalyst) at room temperature for one hour then washed with water. The exchange procedure was repeated and the catalyst dried at 120°C. The exchanged extrudate was then calcined at 538°C in flowing air for 3 hours. The above-prepared ZSM-22 and ZSM-23, and ZSM-35 prepared in accordance with Example 3 above were used in butene skeletal isomerization reactions. The approximate experimental conditions were: Temperature 550°C Pressure 177 kPa 1-Butene WHSV 65 hr-1 N2/Butene in feed 3 vol/vol Figure 1 graphically depicts the respective conversions and products obtained for ZSM-22, ZSM-23 and ZSM-35. Under these conditions selectivities of 83.5%, 88.2% and 95%, respectively, were obtained. EXAMPLE 6 Isomerization of 1-Butene with ZSM-22, ZSM-23 and ZSM-35 at 400 β C ZSM-22 and ZSM-23 prepared in accordance with Example 5, and ZSM-35 prepared in accordance with Example 3 above were used in butene skeletal isomerization reactions. The approximate experimental conditions were: Temperature 400°C Pressure 177 kPa 1-Butene WHSV 65 hr-1 N2/Butene in feed 3 vol/vol Figure 2 graphically depicts the respective conversions and products obtained for ZSM-22, ZSM-23 and ZSM-35. Under these conditions selectivities of 54.3%, 51.1% and 93.2%, respectively, were obtained. ZSM-35 maintains selectivity above 90% even at temperatures which significantly reduce selectivities for ZSM-22 and ZSM-23. EXAMPLE 7 Isomerization of Butene with ZSM-23 and ZSM-35 at 400°C ZSM-22 and ZSM-23 prepared in accordance with Example 5, and ZSM-35 prepared in accordance with Example 3 above were used in 1-butene skeletal isomerization reactions at 400°C and varying n-butene conversions over a wide range of process conditions. Figure 3 is a selectivity/conversion plot comparing the performance of the two catalysts. At 30 to 40% conver¬ sion, selectivity of ZSM-23 ranges of from 30 and 80%. In contrast, selectivity of ZSM-35 ranges from 90 to 99%. Indeed, selectivity of ZSM-35 remains relatively flat at greater than 85% all the way from about 2 to 40% conversion. EXAMPLE 8 Isomerization of 1-Butene with HZSM-35/Si02 Mix The ZSM-35-containing catalyst of Example 2 was used to process a 1-butene feed under four sets of skeletal isomerization conditions comprising two temperatures and two relatively low 1-butene partial pressures. The conditions and compositions of the product streams from Runs 1 to 4 are set out in Table 1 below. Selectivity for isobutene ranged from 93.2 to 99%. Table 1 Butene Skeletal Isomerization Using ZSM-35/SJQ2 Mix Catalyst: ZSM-35/Silica Mixed (65/35), Siiica/Alumina * =20, Catalyst Alpha=96 Feed: 1-Butene/Nitrogen EXAMPLE 9 Isomerization of 1-Butene with Silica-Bound ZSM-35 The ZSM-35-containing catalyst of Example 3 was used to process a 1-butene feed under four sets of skeletal isomerization conditions comprising two temperatures and two relatively low 1-butene partial pressures. The conditions and compositions of the product streams from Runs 1 to 4 are set out in Table 2 below. A comparison of Tables 1 and 2 shows that silica binding has no significant deleterious effect on performance between silica-bound ZSM-35 and ZSM-35/Si02 mix catalysts. Table 2 Butene Skeletal Isomerization Using Silica-Bound ZSM-35 Feed: 1-Butene/Nitrogen Run Number: Feed 1-Butene WHSV: Feed Nitrogen/1-Butene (vol/vol) Temperature (°C) Pressure (kPa) Hours On Stream Composition of the Prod Normal Butenes Isobutene Propene Pentenes Other C5- C6+ n-Butene Conversion (%) Isobutene Selectivity(%) EXAMPLE 10 1-Butene Conversion at Low Temperature, High Pressure Conditions 1-Butene was converted over the HZSM-35 catalyst of Example 4 under the following conditions: Temperature 400°C Pressure 200 kPa 1-Butene WHSV 20 to 65 Total WHSV 40 to 130 N2/Butene 1 (vol/vol) The results of this conversion are depicted in Figure 4 and show that ZSM-35, unlike ZSM-22 and ZSM- 23, performs well, particularly respecting selectivity, even at high WHSV, low temperatures and high butene partial pressures. EXAMPLE 11 1-Pentene Conversion over ZSM-35 1-Pentene was converted over the ZSM-35/Si02 catalyst of Example 3 under the following conditions: Temperature 400"C Pressure 200 kPa 1-Pentene WHSV 123 hr-1 Hours On Stream 10. This conversion yielded the following product distribution (wt%) : Total C4- 1.7 2-methyl-l-butene 19.4 2-methyl-2-butene 51.5 3-methyl-l-butene 0.1 1-pentene 2.2 trans-2-pentene 14.9 cis-2-pentene 9.6 Total C6+ 0.7 IC5=/NC5= in product 2.66. The above results indicate that linear pentene is converted to branched pentenes (to near equilibrium) over ZSM-35 with excellent selectivity. EXAMPLE 12 Preparation of Large Crystal ZSM-35 0.14 parts of aluminum sulfate (17.2% A1_0_) were added to a solution containing 6.5 parts water and 0.43 parts of 50% NaOH solution in a third autoclave. 0.74 parts of PPG Hi-Sil 233 TM preci.pi.tated si.li.ca were added with 1.0 part of pyrrolidine. The mixture was crystallized at 175"C for twenty four hours with stirring. The zeolite was recovered by filtration and washing, then calcined with nitrogen at 540"C to decompose the organic, exchanged with 1 N NH.NO_ solution to remove sodium and finally calcined in air to remove residual organic. Scanning electron microscopy and transmission electron microscopy indicate the ZSM-35 crystals have platelet morphology with a broad distribution of crystal sizes having the largest dimension of up to 1 to 2 microns. Figure 6 is a TEM micrograph of the large crystal ZSM-35 thus prepared. EXAMPLE 13 Large Crystal Synthetic Ferrierite A synthetic ferrierite obtained from Tosoh had a silica to alumina molar ratio of 16.8/1, an alpha value of 81, and a surface area of 219 m 2/g. Scanning electron microscopy and transmission electron microscopy indicate the synthetic ferrierite crystals have platelet morphology with a broad distribution of crystal sizes having the largest dimension of up to 1 to 2 microns. Figure 7 is a TEM micrograph of the large crystal synthetic ferrierite thus prepared. The synthetic ferrierite was dry mixed with precipitated silica in a ratio to achieve 65% ferrierite/35% silica after processing. Water and sodium hydroxide (2 parts NaOH/35 parts silica) was added to obtain an extrudable mixture. The mix was extruded to 1/16 inch (1.6 mm) diameter pellets and dried at 100°C. The dried extrudate was treated twice with 1 N NH.NO for 1 hour at room temperature and washed with water. After drying at 100°C, the extrudate was calcined in nitrogen at 538°C for 3 hours. Following cooling, the calcined material was exchanged twice with 1 N NH.NO for 1 hour and dried. The catalyst was then calcined for 6 hours at 538°C in air. EXAMPLE 14 Isomerization of 1-Butene with Microcrystalline ZSM-35 and Large Crystal ZSM-35 The microcrystalline ZSM-35 of Example 4 and the large crystal ZSM-35 of Example 12 were used in 1-butene skeletal isomerization reactions carried out at 300, 400, 500 and 550"C, and at 165 WHSV, 30 psia. 1-Butene conversion and iso-butene selectivity over temperature are depicted in Figure 8. Significantly higher n-butene conversions occur with microcrystalline ZSM-35 with no loss of isobutene selectivity. EXAMPLE 15 Isomerization of 1-Butene with Large Crystal Synthetic Ferrierite The synthetic ferrierite of Example 13 was used in 1-butene skeletal isomerization reactions carried out at 400 to 500°C, 66 WHSV, 24 psia, using a nitrogen/1-butene feed. The conditions of each run and the product composition is set out below in Table 3. At 400°C, conversion was near zero (0.34%). Conversion did not increase even when temperature was raised to 550"C and WHSV reduced to 33. Conversion did increase to 50-60% when WHSV was cut to 2 as depicted in Figure 9. However, selectivity was low (60-70%) and the cata¬ lyst aged rapidly. The rapid aging of the synthetic ferrierite becomes dramatically clear when n-butene conversion for this catalyst and small crystal ZSM-35 are plotted as a function of cumulative 1-butene throughput as in Figure 10. Microcrystalline ZSM-35 ages approximately three orders of magnitude more slowly. Table 3 EXAMPLE 16 Preparation of Alumina-Bound ZSM-35 A catalyst was prepared by dry mixing the as-synthesized ZSM-35 of Example 1 with alumina (LaRoche Versal 250) such that the final product contained 65 parts ZSM-35 and 35 parts alumina. Sufficient water was added to obtain a mixture which was extruded to 1/16 inch (1.6 mm) diameter pellets then dried at 100°C. The extrudate was calcined in nitrogen at 538°C for three hours, then exchanged twice with a 1 N NH.N0_ solution at room temperature, dried at 100°C and calcined in air for 6 hours. The product had a pore volume of 0.86 cc/g and a 300 angstrom pore volume of 0.46 cc/g. EXAMPLE 17 Preparation of Large-Pore Silica-Bound ZSM-35 A catalyst was prepared by dry mixing the as-synthesized ZSM-35 of Example 1 with precipitated silica (Ultrasi .lTM VNSP3 from Degussa) . Colloidal silica, in proportion to give 65% ZSM-35 / 35% silica after calcination, and water were added to the dry mix to obtain an extrudable mixture. The mix was extruded to 1/16 inch (1.6 mm) diameter pellets, and dried at 100"C. The extrudate was calcined in nitrogen at 538°C for three hours, then exchanged twice with a 1 N NH.NO solution at room temperature, dried at 100°C and calcined in air for 7 hours. The product had a pore volume of 0.86 cc/g and a 300 angstrom pore volume of 0.37 cc/g. EXAMPLE 18 Skeletal Isomerization of 1-Butene with Catalyst Compositions of Examples 16, 4 and 17 1-Butene was subjected to skeletal isomerization conditions in the presence of alumina-bound ZSM-35 (Example 16) , silica bound ZSM-35 of lower pore volume (Example 4) , and silica bound ZSM-35 of enhanced pore volume (Example 17) . The conditions comprised 33 1-butene WHSV on zeolite, 1/1 v/v butene/nitrogen feed, 207 kPa (30 psia) , and 400°C using catalysts comprising 65 wt% ZSM-35 sized to 14/24 mesh. Figure 11 compares the effects of aging on n-butene conversion for the alumina-bound catalyst of Example 16, versus the silica-bound catalyst of Example 17, showing a reduction in activity from 46% to 23% n-butene conversion over about 7 days compared with a reduction in activity from 47% to 30% n-butene conversion over about 18 days, respectively. Figure 12 compares the effects of n-butene conversion on isobutene selectivity for n-butene conversion for the alumina-bound catalyst of Example 16, versus the silica-bound catalyst of Example 17. The results show little variation in isobutene selectivity over a range of about 23 to 50% n-butene conversion between the two catalyst types. Figure 13 compares the effects of aging for the silica-bound catalyst of Example 4, versus the silica-bound catalyst of Example 17, showing a reduction in activity from 48% to 28% n-butene conversion over about 12 days compared with a reduction in activity from 47% to 30% n-butene conversion over about 18 days, respectively. Figure 14 compares the effects of reduced n-butene conversion (aging) on isobutene selectivity on n-butene conversion for the silica-bound catalyst of Example 4, versus the silica-bound catalyst of Example 17. The results show little variation in isobutene selectivity over a range of about 28 to 50% n-butene conversion between the two catalyst types.

Claims: CIAIMS : 1. A method for the conversion of linear olefins to corresponding iso-olefins of the same carbon number which comprises contacting an organic feedstock comprising linear olefins with a catalyst comprising ZSM-35. 2. The method of claim 1 wherein the ZSM-35 has a crystal size of whose largest dimension is no greater than 0.5 micron. 3. The method of claim 2 wherein the ratio of the second largest dimension to the largest dimension of the ZSM-35 is 0.5 to 1.0. 4. The method of claim 2 wherein said crystal size has the dimensions of 0.03 to 0.08 micron by 0.03 to 0.08 micron by < 0.05 micron. 5. The method of claim 1 wherein said catalyst comprises a binder and has a total pore volume greater than 0.6cc/g. 6. The method of claim 5 wherein said catalyst comprises a silica binder. 7. The method of claim 1 wherein said catalyst ccoommpprriisseess aa bbiinnddeerr aanndd hhaass aa 330000 angstroms pore volume of greater than 0.1 cc/g. 8. The method of claim 7 wherein said catalyst comprises a silica binder. 9. The method of claim 1 wherein said conversion is carried out at a temperature of 100 to 750°C, a weight hourly space velocity (WHSV) based on linear olefin in said feedstock of 0.1 and 500 WHSV, and a linear olefin partial pressure of 2 to 2000 kPa. 10. The method of claim 1 wherein said conversion is carried out at a temperature of 150 to 600"C, a weight hourly space velocity (WHSV) based on linear olefin in said feedstock of 0.5 and 400 WHSV, and a linear olefin partial pressure of 10 to 500 kPa. 11. The method of claim 1 wherein said conversion is carried out at a temperature of 200 to 550°C, a weight hourly space velocity (WHSV) based on linear olefin in said feedstock of 1 and 100 WHSV, and a linear olefin partial pressure of 20 to 200 kPa. 12. The method of claim 1 wherein said feedstock comprises C. to C 1Q linear olefins.

Inventors: HAAG WERNER OTTO, HUSS ALBIN JR, KLOCKE DONALD JOSEPH, LISSY DARIA NOWAKIWSKA, RAHMIM IRAJ ISAAC, HAAG, WERNER, OTTO, HUSS, ALBIN, JR., KLOCKE, DONALD, JOSEPH, LISSY, DARIA, NOWAKIWSKA, RAHMIM, IRAJ, ISAAC
Applicants: MOBIL OIL CORP, MOBIL OIL CORPORATION
Application year: 1993
Main classification: C07C1
IPC codes: B01J29, C07B61, C07C5, C07C11