Process for fabricating a phase shift photomask or phase shift photomask blank

Abstract: The invention relates to a phase shift photomask in which the peripheral region portion of a phase shift layer is removed by a relatively simple procedure and which has no or little defect and is inexpensive, a blank therefor, and a process for fabricating them. The process includes the steps of forming phase shift layer (23) all over the surface of one side of transparent substrate (21), and immersing only the peripheral region of substrate (21) in etching solution (25) to etch away the peripheral region of phase shift layer (23), whereby phase shift layer (27) is confined within an area smaller than that of substrate (21).

Description: The present invention relates to a photomask used for the production of high-density integrated circuits such as LSIs, VLSIs, etc., and more particularly to a process for fabricating a phase shift photomask itself or a blank therefor. Semiconductor integrated circuits such as ICs, LSIs and VLSIs are now fabricated by repeating the so-called lithography process wherein a resist is coated on the substrate to be processed, like a silicon wafer, and exposed to a desired pattern through a stepper, etc., followed by development, etching, doping, CVD, etc. A photomask used for such a lithography process and called a reticle is now increasingly required to have much higher accuracy in association with the high performance and high integration of semiconductor integrated circuits. Referring to a typical LSI, i.e., a DRAM by way of example, a 5x reticle for a 1 megabit DRAM, i.e., a reticle of size five times as large as that of an exposure pattern should be very small in terms of dimensional variation; the accuracy demanded is as small as 0.15 µm even at the mean value ± 3σ (σ is the standard deviation). Likewise, a dimensional accuracy of 0.1 to 0.15 µm is demanded for 5x reticles for 4 megabit DRAMs; and a dimensional accuracy of 0.05 to 0.1 µm for 5x reticles for 16 megabit DRAMS. In addition, the line widths of device patterns formed with the use of these reticles are now becoming finer; for instance, they must be 1.2 µm for 1 megabit DRAMS, 0.8 µm for 4 megabit DRAMS, and 0.6 µm for 16 megabit DRAMS. To meet such demands, various photolithography technologies are now under investigation. In the case of the next generation device patterns of the 64 megabit DRAM class for instance, however, the use of stepper photolithography technologies using conventional reticles will place some limit on resolving the resist patterns. To exceed this limit, a reticle known as a phase shift mask and designed on the basis of a new technological paradigm has been proposed in the art, as set forth in JP-A-58-173744, JP-B-62-59296, etc. Phase lithography making use of this phase shift photomask is a technology that enables the resolving power of a projected image to be enhanced by manipulation of the phase of light transmitting through the reticle. Phase shift lithography will now be explained briefly with reference to FIGS. 1 and 2. FIG. 1 is a schematic of the principle of the phase shift technique, and FIG. 2 is a schematic of a conventional process. FIGS. 1(a) and 2(a) are sectional views of the reticles used, FIGS. 1(b) and 2(b) represent the amplitude of light transmitting through the reticles, FIGS. 1(c) and 2(c) illustrate the amplitude of light on the wafers, and FIGS. 1(d) and 2(d) show the intensity of light on the wafers. Reference numeral 1 is a substrate, 2p a light-blocking pattern, 3p a phase shifter, and L stands for light. In the conventional arrangement, the substrate 1 made up of glass is simply provided with the light-blocking pattern 2p for the purpose of defining a light transmitting portion according to a given pattern, as shown in FIG. 2(a). In the phase shift lithography arrangement, however, the phase shifter 3p made up of a transmitting film is provided on either one of a pair of light transmitting portions of the reticle for phase reversal, as shown in FIG. 1. In the conventional process, therefore, the amplitude of light on the reticle is in the same phase, as shown in FIG. 2(b), and so is the amplitude of light on the wafer, as shown in FIG. 2(c). Consequently, it is impossible to resolve the pattern on the wafer, as can be soon from FIG. 2(d). In phase shift lithography, in contrast, the light passing through the phase shifter 3p is in the opposite phase between adjacent patterns, so that the intensity of light can be reduced to zero at the boundary of the patterns and hence the adjacent patterns can be distinctly resolved, as can be seen from FIG. 1(d). In phase shift lithography, therefore, it is possible to resolve patterns which have been incapable of being resolved in the prior art, resulting in some considerable improvement in resolution. A typical process of fabricating conventional phase shift photomask blanks will then be explained with reference to FIG. 3. FIG. 3 is a conceptual sectional schematic showing the process for fabricating a phase shift photomask, wherein 1 is a substrate, 4 an electrically conductive layer, 3 a phase shift layer, S sputtering, and 2 a light-blocking layer. The optically polished substrate 1 is first provided thereon with the conductive layer 4 (that is made up of NESA film and serves as an etching stopper layer for an ionizing radiation resist layer at the later step). On the layer 4 there is then applied and spin-coated a phase shifter material showing a good-enough transmittance with respect to exposure light, e.g., spin-on glass (hereinafter SOG for short). At this time, the four side regions of the rectangular substrate are thicker than the rest, as can be seen from FIG. 3(b). Finally, a light-blocking material such as Cr is formed as film on the phase shifter material, whereby a phase shift photomask blank having the light-blocking layer 2 is completed. Then, a typical process of fabricating a conventional shifter overlying type of phase shift photomask will be explained with reference to FIG. 4 that is a conceptual sectional schematic showing the process of fabricating the phase shift photomask in which 1 is a substrate, 4 an electrically conductive layer, 2p a light-blocking (chromium) pattern, 3 a phase shift layer, IR ionizing radiation, 5p a resist pattern, EP etching gas plasma, 3p a phase shifter pattern, and OP oxygen plasma. As shown in FIG. 4(a), the substrate with the light-blocking (chromium) pattern 2p on it is inspected and repaired, if required, and washed. Then, as shown in FIG. 4(b), the phase shift layer 3 made up of SiO 2 or the like is spin-coated on the light-blocking pattern 2p. At this time, the four side regions of the rectangular substrate are thicker than the rest. Subsequently, as shown in FIG. 4(c), the ionizing radiation resist layer 5 made up of chloromethylated polystyrene or the like is formed on the phase shift layer 3. After alignment done as in the prior art, as shown in FIG. 4(d), a given pattern is written on the ionizing radiation resist layer 5 by the ionizing radiation IR emanating from a radiation exposure system, developed and rinsed to form the resist pattern 5p, as shown in FIG. 4(e). Then, heat and descumming treatments are carried out, if required. Following this, as shown in FIG. 4(f), the portions of the phase shift layer 3 under the openings in the resist pattern 5p is dry etched by etching gas plasma EP to form the phase shifter 3p. It is noted that the phase shifter 3p may also be formed by using wet etching in place of drying etching for which etching gas plasma EP is used. Finally, the remaining resist is incinerated away by oxygen plasma OP, as shown in FIG. 4(g). Through the steps mentioned above, a phase shift photomask having the phase shifter 3p such as one shown in FIG. 4(h) is completed. As can be appreciated from the foregoing explanation, the prior art phase shift photomasks and phase shift photomask blanks pose many problems, e.g., the frequent occurrence of defects, a rise in fabrication cost, and an increase in fabrication time. The reason is that when the phase shift layers represented by spin-on glass (SOG) are spin-coated, the phase shift layers become thicker on the peripheral regions of the rectangular substrates than on the rest, giving rise to cracking and dusting. JP-A-4 153 683 relates to the production of a photomask having a phase shift layer. According to this method, an outer peripheral part of a transparent film used for forming phase shifters can be removed by wet etching after formation of this film during the production process. DE-A-33 14 156 relates to a method of forming a photoresist layer on a semiconductor wafer. Once formed, the photoresist layer is removed from the peripheral region of the wafer. This removal may be effected using a solution to dissolve the photoresist layer, or by means of a laser beam to evaporate the photoresist material, or by means of photolithographic methods. DE-A-41 15 510 discloses an apparatus for removing a layer from the peripheral zone of the substrate. The apparatus comprises a spraying device which jets a solution to the layer to dissolve. EP-A-0 362 838 describes a method of fabricating semiconductor devices. According to this method, multiple layers are formed on a semiconductor wafer. During these deposition steps, an abnormal protrusion is produced on the wafer edge. Next, a two micrometer thick positive photoresist film may be coated as a protection layer upon the surface where the IC elements are to be formed according to a spin-coat method. Thereafter, the multiple layers deposited on the peripheral portion of the wafer are removed by the use of a grinding wheel so as to expose the entire periphery of the underlying silicon wafer. In an additional etching step, using an etchant of a mixture of hydrofluoric acid and nitric acid, a mirror finish of the wafer edge is achieved. The photoresist used as a protective film for the grinding step is also resistant to this etchant and functions as a mask for the etching step. EP-A-0 489 540 relates to a phase-shifting lithographic mask with improved resolution. This mask comprises a quartz substrate, a layer which is chemically vapour deposited, silicon dioxide or a spun-on glass layer and a chromium layer which is deposited thereon. By means of photolithographic process steps, a structure is formed wherein a part of layer is removed so as to expose a free area on the substrate and wherein the chromium layer is removed around this opening in the layer. EP-A-0 370 511 describes a method of fabricating a photoplate. A mask blank, having a glass substrate and an electrically conductive opaque film coating over an upper surface of the glass substrate, is coated with a resist to form a resist film over the opaque film to produce a photoplate. Before applying the resin to the opaque film a zone of an upper surface of the opaque film is deteriorated in wettability to the resist so that the resist does not adhere to the deteriorated wettability zone. The deteriorated wettability zone is distant from a pattern forming area of the opaque film. Then, the resist is applied to the upper surface of the opaque film to form the resist film, whereby the wettability deteriorated zone of the opaque film is exposed for earthing the opaque film without being covered with a resist. According to an embodiment, two zones are formed on one side of the marginal area of a photoplate. In order to achieve the exposed zones, the chromium film is contaminated by a wettability deteriorating material such as a material including fluorine. Then, the electron beam resist is applied to the whole upper surface of the chromium film to form the resist film so that the exposed zones are formed because of the deteriorated wettability thereof. In view of such situations as mentioned above, an object of the invention is to provide a process for fabricating a phase shift photomask which can be fabricated at low cost with no or little defect by removing the peripheral region of a phase shift layer in a relatively simple manner or a blank therefor. This object is achieved with a process according to the claims. The phase shift layer used may be composed of material such as silicon oxide or spin-on glass (hereinafter often abbreviated as SOG). Here, if the phase shift layer has a thickness, d, given by d = λ/{2(n-1)} where n is the index of refraction of the phase shift layer at an exposure wavelength λ, a portion having the phase shift layer shows a phase lag of 180° with respect to a portion having no phase shift layer. FIG. 5 is a schematic of the steps of fabricating the phase shift photomask blank according to the prior art. In FIG. 5, reference numeral 1 represents a substrate, 4 an electrically conductive layer, 6 a layer that repels the overlying phase shift layer 3, and 3k the phase shift layer. As shown in FIG. 5(a), the electrically conductive layer 4 is provided on the substrate 1, and the layer 6 capable of repelling the overlying phase shift layer is patterned on the layer 4, as shown in FIG. 5(b). Then, as shown in FIG. 5(c), the phase shifter layer 3, if the phase shifter material is SOG, is formed by spin coating, whereby the edge portions of the overlying phase shift layer are repelled. The thus prepared phase shift photomask blank is washed and inspected as to whether or not there is any undesired defective region. In this manner, the phase shift layer of the phase shift photomask blank having the defect-free phase shift layer 3k is completed. This process can be applied to the fabrication of an phase shifter overlying type of phase shift photomask in exactly the same manner as mentioned above, provided that it is necessary to form a material capable of repelling off the overlying phase shift layer on any desired region where the phase shift layer is to be removed prior to the formation of the phase shifter layer. According to the invention, there is provided a process for fabricating a phase shift photomask blank and a phase shift photomask, which involves the steps of providing the peripheral region of a substrate with a layer of material capable of lifting off an overlying phase shift layer, providing the phase shift layer on the substrate, and lifting off the phase shift layer. Here, too, it is understood that the invention encompasses a phase shift photomask blank prepared by this lift-off process and a phase shift photomask obtained by processing this blank as well. The layer of material capable of lifting off the overlying phase shift layer is melted by heating. In this case, the lifting-off is achieved by melting by heating. Furthermore, the invention provides a process for fabricating a phase shift mask blank and a phase shift mask, characterized in that the layer of material capable of lifting off the overlying phase shift layer is a material that is a solid at normal temperature (25°C), has a melting point of 150°C or lower, and is melted by heating at a suitable temperature. FIG. 6 is a schematic showing the steps of fabricating a phase shift photomask blank according to the invention. In FIG. 6, 1 is a substrate, 4 an electrically conductive layer, 7 a layer of material capable of lifting off the overlying phase shift layer, 3 a phase shift layer, H a heat treatment, and 3k is a phase shift layer after lifting-off. As shown in FIG. 6(a), the conductive layer 4 is formed on the substrate 1. Then, as shown in FIG. 6(b), the layer 7 of material capable of lifting off the overlying phase shift layer is patterned on the peripheral region of the substrate (that may include the four corners in triangular forms). Subsequently, as shown in FIG. 6(c), the phase shifter layer 3, if the shifter material is SOG, is formed by spin coating. Thereafter, as shown in FIG. 6(d), the heat treatment H is done to lift off the layer 7 of material capable of lifting off the overlying phase shift layer, as shown in FIG. 6(e). The thus prepared phase shift photomask blank is washed and inspected as to whether or not there is any undesired defective region. In this manner, the phase shift layer of the phase shift photomask blank having the defect-free phase shift layer 3k after lifting-off is completed. This lift-off process can be applied to the fabrication of an phase shifter overlying type of phase shift photomask in exactly the same manner as mentioned above. That is, the invention provides a phase shift photomask blank having at least a phase shift layer on a transparent substrate and a phase shift photomask obtained therefrom, characterized in that the peripheral region of the phase shift layer on the substrate is removed so as to confine the phase shift layer within an area smaller than that of the substrate. In this case, the phase shift layer may be made up of spin-on glass. According to the invention, there is thus provided a process for fabricating a phase shift photomask blank and a phase shift photomask, characterized by including the steps of providing the peripheral region of a transparent substrate with a layer of material capable of lifting off an overlying phase shift layer, providing the phase shift layer on the substrate, and lifting off the phase shift layer. In this case, the lifting-off may be done by heating and the layer of material capable of lifting off the overlying phase shift layer may be made up of a material that is solid at normal temperature (25°C), has a melting point of 150°C or lower, and is melted by heating at a suitable temperature. It is possible to fabricate phase shift photomask blanks and phase shift photomasks within a short fabrication period of time and at lower cost, but with neither frequent occurrence of defects nor dusting. Still other objects and advantages of the invention will in part be obvious and will in part be apparent from the specification. The invention accordingly comprises the features of construction, combinations of elements, and arrangement of parts which will be exemplified in the construction hereinafter set forth, and the scope of the invention will be indicated in the claims. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic showing phase shift techniques. FIG. 2 is a schematic illustrating a conventional technique. FIG. 3 is a conceptual sectional illustration of the process of fabricating a conventional phase shift photomask blank. FIG. 4 is a conceptual sectional illustration of the process of fabricating a conventional phase shift photomask. FIG. 5 is a conceptual sectional illustration of a prior art process for fabricating a phase shift photomask blank. FIG. 6 is a conceptual sectional illustration of the process for fabricating a phase shift photomask blank according to the invention. FIG. 7 is a sectional illustration of a phase shift photomask blank. FIG. 8 is sectional illustration of one embodiment of a prior art process for fabricating the blank of FIG. 7. FIG. 9 is a sectional illustration of a phase shift photomask blank. FIG. 10 is a sectional illustration of one embodiment of the process for fabricating the blank of FIG. 9. FIG. 11 is a sectional illustration of a phase shift photomask prepared by processing the blank of FIG. 7. FIG. 12 is a sectional illustration of the process for fabricating the photomask of FIG. 11. FIG. 13 is a sectional illustration of a halftone type of phase shift photomask. FIG. 14 is a sectional illustration of a halftone type of phase shift photomask. FIG. 15 is a sectional illustration of an edge-enhanced type of phase shift photomask. In what follows, the present invention will be explained, more specifically but not exclusively, with reference to some examples of the phase shift photomask blank, the process for fabricating the blank, and the phase shift photomask obtained from the blank. Examples 1 to 8 are only illustrative examples, whereas Examples 9 and 10 refer to the claimed invention. Example 1 FIG. 7 is a sectional view of the phase shift photomask of the first example, and FIG. 8 is a sectional schematic for illustrating one example of the process for fabricating it. As shown in FIG. 8(a), a high-purity quartz glass substrate 21 of 5 to 6 square inches in size and 0.09 to 0.25 inches in thickness is first provided thereon with an etching stop layer 22 having a thickness of about 10 to 110 nm and composed mainly of NESA glass (tin oxide·strontium oxide), tin oxide, aluminum oxide, or the like, by means of ordinarily available vapor deposition, ion plating, sputtering or other known techniques. The etching stop layer 22 is further spin-coated thereon with commercially available spin-on glass (SOG, e.g., USG-50S or Accuglass 311S made by Allied Signal Corp.). After this, baking is done at a temperature of 200 to 350°C to form a phase shift layer 23 of 400 to 440 nm in thickness that is used for in-line exposure (at a wavelength of 365 nm). Then, as shown in FIG. 8(b), a substrate 24 formed, as shown in FIG. 8(a), is immersed, while remaining upright, in an etching tank 26 charged with an etching solution 25, so that one side thereof can be immersed by a depth of 2 to 10 mm in the etching solution 25 for a constant period of time, and then pulled out, just after which it is washed with water. After this procedure is repeated for each of the remaining three sides, drying is done to form on the etching stop layer 22 the phase shift layer 27, all the four side portions of which have been removed, as shown in FIG. 8(c). Here a buffered aqueous solution of hydrofluoric acid consisting of a 50% aqueous solution of hydrofluoric acid and a 40% aqueous solution of ammonium fluoride at about 1 : 7 to 30 proportions may be used as the etching solution. It is noted, however, that when organic SOG (commercial SOG, e.g., Accuglass 311S) is used, use may be made of an alkaline aqueous solution containing about 10 to 40% of sodium hydroxide, potassium hydroxide, or the like. While SOG has been described as being etched after baking, it is understood that SOG may be etched prior to baking. Finally, a single- or multi-layer form of light-blocking film 28 composed mainly of chromium, chromium nitride, chromium oxide or the like is formed on the phase shift layer 27 in conventional manners such as sputtering. In this manner, a phase shift photomask blank according to one example, such as one shown at 29 in FIG. 7, is completed. Here it goes without saying that the light-blocking layer 28 may be larger in area that the phase shift layer 27, as shown in FIG. 7, or may be identical or smaller in area with or than it. It is noted that the transmittance of the light-blocking layer 28 with respect to exposure light may be less than 1% as usual, while the transmittance of the light-blocking layer for a halftone type of phase shift photomask may lie in the range of about 1 to 50%. In the case of a halftone type of phase shift photomask blank, however, it is desired that the total of the phase shift of exposure light passing through the two layers, i.e., the light-blocking and phase shift layers 28 and 27 amount to 160° to 200°. Example 2 FIGS. 9 and 10 are a sectional view of another example of the phase shift photomask blank and a sectional view of another example of the process for fabricating it, respectively. As shown in FIG. 10, a high-purity quartz substrate 41 is first provided thereon with an etching stop layer 42, on which a light-blocking layer 43 composed chiefly of chromium or the like is sputtered or otherwise formed in conventional manners. Following this, a phase shift layer 44 is formed. In this connection, it is noted that when the layer 44 is made up of silicon oxide, it may be formed by ordinary vapor deposition, CVD, sputtering or other known techniques, and that when the layer 44 is made up of SOG, it may be formed by spin coating. Further, all the peripheral region of the phase shift layer 44 is removed by a simple etching procedure that does not use any etching mask as in Example 1. In this way, a phase shift photomask blank 46 having a phase shift layer 45 is obtained, all the peripheral region of which has been removed, as shown in FIG. 9. Example 3 FIGS. 11 and 12 are a sectional view of one example of the phase shift photomask, which is obtained by processing the phase shift photomask bland 29 shown in FIG. 7, and a sectional schematic of the process for fabricating it, respectively. As shown in FIG. 12(a), a desired resist pattern 30 is first formed on a light-blocking layer 28 in conventional manners. Then, the unpatterned portions of the light-blocking layer 28 are wet or dry etched away, and the remaining resist pattern 30 is incinerated away by oxygen plasma, thereby making a light-blocking pattern 31, as shown in FIG. 12(b). Then, as shown in FIG. 12(c), a desired resist pattern 32 is aligned with a given position on the light-blocking pattern 31 and formed thereon in conventional manners. Following this, the unpatterned portions of the phase shift layer 27 are dry etched away with gas such as CF 4 to form a phase shift pattern 33. Then, the remaining resist is incinerated away or otherwise removed to make such a phase shift photomask as shown in FIG. 11 complete. Example 4 This is directed to another example of the phase shift photomask, which is obtained by using the phase shift photomask blank 29 shown in FIG. 7. In this example, a halftone type of phase shift photomask is obtained, in which, as illustrated in FIG. 13, the area of the phase shift pattern 33 is coincident with that of the overlying light-blocking pattern 31, and the transmittance of the light-blocking layer 31 with respect to exposure light is 1 to 50%. Example 5 This is directed to one example of the phase shift photomask, which is obtained by using the phase shift photomask blank 46 shown in FIG. 9. In this example, a halftone type of phase shift photomask is obtained, in which, as shown in FIG. 14, the area of the halftone light-blocking pattern 49 is coincident with that of the overlying phase shift pattern 48. Example 6 This is directed to another example of the phase shift photomask, which is obtained by using the same phase shift photomask blank 46. In this example, a so-called edge-enhanced type of phase shift photomask is obtained, in which, as shown in FIG. 15, the area of the phase shift pattern 48 is substantially coincident with, but is slightly smaller than, that of the underlying light-blocking pattern 49 composed of an ordinary light-blocking layer with a transmittance of less than 1% with respect to exposure light. Example 7 This is directed to another example, In this example, a quartz substrate with an electrically conductive NESA film on it was provided with a fluorocarbon resin pattern capable of repelling liquid SOG on only the region thereof, from which the phase shift layer was to be removed, i.e., on the four side and corner portions. The SOG was then spin-coated. Following this, chromium was sputtered to form a light-blocking layer. The thus obtained phase shift photomask blank is found to show no peeling of SOG and be of good quality and high accuracy. Example 8 This is directed to another example. In this example, a substrate with a light-blocking film pattern of chromium was provided with a fluorocarbon resin pattern capable of repelling liquid SOG on only the region thereof, from which the phase shift layer was to be removed. Then, SOG was spin-coated on the substrate. As a result, it was found that no SOG was formed on only the upper region with the fluorocarbon resin pattern on it. In this way, the phase shift layer with no unnecessary region was formed. As in the prior art, the resist layer was then formed, followed by the etching of the phase shift layer to form a phase shift pattern (a phase shifter). Finally, the resist pattern was stripped. The thus completed phase shift photomask showed no peeling of SOG. It is found that phase shift photomasks of high accuracy can be obtained at decreased reject rates for a short fabrication period of time. Example 9 This is directed to one example of the invention. In this example, a quartz substrate with an electrically conductive NESA film layer on it was provided with a lift-off pattern (of material capable of lifting off the overlying phase shift layer) made up of phenol (with a melting point of 40.85°C) on only the region thereof, from which the phase shift layer was to be removed. Then, SOG that did not dissolve phenol was spin-coated on the substrate. This substrate was heated to about 60°C to dissolve the lift-off pattern, thereby lifting off the lift-off pattern together with the portion of the phase shift layer (SOG) overlying the lift-off pattern. Following this, chromium was sputtered to form a phase shift mask blank with a light-blocking layer on it. According to the invention, it is thus possible to fabricate at decreased reject rates phase shift mask blanks with no peeling of SOG and having high accuracy. Example 10 This is directed to another example of the invention. In this example, a quartz substrate with an electrically conductive NESA film layer on it was provided with a lift-off pattern (of material capable of lifting off the overlying phase shift layer) made up of phenol (with a melting point of 40.85°C) on only the region thereof, from which the phase shift layer was to be removed. Then, SOG that did not dissolve phenol was spin-coated on the substrate. This substrate was heated to about 60°C to dissolve the lift-off pattern, thereby lifting off the lift-off pattern together with the portion of the phase shift layer (SOG) overlying the lift-off pattern. In this way, the phase shift layer having no defective region was prepared. As in the prior art, the resist layer was then formed, followed by the etching of the phase shift layer to form a phase shift pattern (a phase shifter). Finally, the resist pattern was stripped. The thus completed phase shift photomask showed no peeling of SOG. According to the invention, it is thus found that phase shift photomasks of high accuracy can be obtained at decreased reject rates for a short fabrication period of time. According to the invention wherein the peripheral region of a phase shift layer is removed by lifting off the phase shift layer, as will be appreciated from the foregoing explanation, it is possible to fabricate phase shift photomask blanks and phase shift photomasks within a short fabrication period of time and at lower cost, but with neither frequent occurrence of defects nor dusting.

Claims: A process for fabricating a phase shift mask or phase shift mask blank, comprising the steps of providing a first layer of material capable of lifting off an overlying phase shift layer, providing the overlying phase shift layer, and lifting off the phase shift layer by heating and melting the first layer of material. A process according to Claim 1, wherein the phase shift layer is lifted off from the peripheral region of a transparent substrate. A process according to Claim 1 or 2, wherein the material capable of lifting off the overlying phase shift layer is a material that is solid at normal temperature or 25°C, has a melting point of 150°C or lower, and is melted by heating at a suitable temperature.

Inventors: IIMURA YUKIO, MIKAMI KOICHI, MIYASHITA HIROYUKI, TARUMOTO NORIHIRO, IIMURA, YUKIO, MIKAMI, KOICHI, MIYASHITA, HIROYUKI, TARUMOTO, NORIHIRO, IIMURA, YUKIO, C/O DAI NIPPON PRINTING CO., LTD., Mikami, Koichi, c/o DAI NIPPON PRINTING CO., LTD., MIYASHITA, HIROYUKI, C/O DAI NIPPON PRINT. CO.,LTD, Tarumoto, Norihiro, c/o DAI NIPPON PRINTING CO.LTD
Applicants: DAINIPPON PRINTING CO LTD, DAI NIPPON PRINTING CO., LTD.
Application year: 1993
Main classification: G03F1
IPC codes: G03F1