Solid golf ball

Abstract: The present invention provides a one-piece solid golf ball or a two or more piece solid golf ball which comprises an inner core and a cover covering the inner core. The one-piece solid golf ball is formed from a rubber composition which comprises; a base rubber, vulcanized rubber powder, and a vulcanizing agent. The two or more piece solid golf ball comprises an inner core and a cover covering the inner core, the inner core being composed of either one uniform rubber materlal or a combination of a center and one or more outer layers disposed over the center, wherein one or more rubber portions of the inner core are formed from a rubber composition comprising: a base rubber, vulcanized rubber powder, and a vulcanizing agent.

Description: The present lnvention relate to a one-piece solid golf ball or a two or more piece solid golf ball which compries an inner core and a cover covering the inner core. One-piece solid golf balls and two or more piece solid golf balls golf balls are commercially available. One-piece solid golf balls are formed by molding and vulcanizing a rubber composition. Two or more piece solid golf balls are composed of an inner core and a cover covering the inner core, the inner core being composed of either one uniform rubber material or a combination of a center and one or more outer layers disposed over the center. At least one portion of the inner core is formed by molding and vulcanizing a rubber composition. The rubber composition for the solid golf ball generally comprises a polybutadiene rubber having at least 40% of cis-1,4 structure as a base rubber, a metal salt of an α,β-ethylenically unsaturated carboxylic acid (e.g. methacrylic acid, acrylic acid, etc.) as a co-crosslinking agent and a vulcanizing agent (e.g. organic peroxides). One-piece solid golf balls are mainly use in driving ranges. The most important requirement for golf ball used in the driving ranges is a high durability (i.e. the golf balls must be hard to break). However, the conventionally used one-piece solid golf balls do not have sufficient durability and there is therefore a desire to improve the durability. Two or more piece solid golf balls are generally used as high quality golf balls, but it is further required to improve the shot feel. It is considered that the poor shot feel occurs due to the difference in hardness between the cover and the inner core. In order to improve the shot feel of these golf balls, it has been proposed to provide an inner core in which the surface portion is harder than the central portion. The larger the hardness difference between the surface and center of the inner core, the better the shot feel. However, as the difference is larger, the durability is liable to become inferior. Sometimes, there are golf balls which break by hitting with a golf club (e.g. No.1 to No. 3 wood clubs, etc.) 10 to 15 times. GB-A-2 163 437 relates to homogeneous blends of thermoplastics and cured elastomeric materials for use in the manufacture of golf balls. GB-A-2 237 809 relates to a golf ball comprising a core composed of a relatively hard rubber matrix and multiplicity of relatively soft rubber particles. We have now found that, when vulcanized rubber powder is formulated into a rubber composition for the golf balls, the durability can be improved without any deterioration of the shot feel. The main object of the present invention is to provide a golf ball having an excellent durability and shot feel. The present invention provides a one-piece solid golf ball of a rubber composition comprising a vulcanized mixture of: a base rubber, vulcanized rubber powder, and a vulcanizing agent. The present invention also provides a two or more piece solid golf ball comprising an inner core and a cover covering the inner core, the inner core consisting of a centre only or comprising a centre with one or more outer layers disposed over the centre, wherein the centre of the inner core is obtainable by forming a mixture of: a base rubber, a powder of a vulcanized rubber which has a JIS C hardness of from 40 to 95, and a vulcanizing agent, and vulcanizing the said mixture to form the centre of the inner core, wherein the centre of inner core so produced has a JIS C hardness of from 50 to 90. In the present invention, the reason why the durability of the golf balls can be improved by incorporating a vulcanized rubber powder into the rubber composition is not clear at present, but it is considered that the vulcanized rubber powder improves the dispersibility of the rubber composition and inhibits the runaway reaction based on the metal salt of α,β-ethylenically unsaturated carboxylic acid when vulcanizing. The base rubber used in the present invention can generally be used for golf balls, for example natural rubber, butadiene rubber, isoprene rubber or a mixture thereof. Butadiene rubber comprising at least 40 cis-1,4 butadiene is preferred. The vulcanizing agent formulated into the rubber composition of the present invention is one that is generally used for golf balls, including organic peroxides, such as dicumyl peroxide and benzoyl peroxide. The preferred vulcanizing agent is dicumyl peroxide. The rubber composition for the golf balls may further contain a co-crosslinking agent, a filler or other additives. The co-crosslinking agent may be a metal salt of an α,β-ethylenically unsaturated carboxylic acid. Exampls of the α,β-ethylenically unsaturated carboxylic acid are acrylic acid and methacrylic acid. The metal atoms used for forming the metal salt are not limited, but generally divalent metal atoms, such as zinc, manganese and calcium may be used. The metal salts of α,β-ethylenically unsaturated carboxylic acid may be prepared in the rubber composition by separately incorporating therein a metal oxide (e.g. zinc oxide, or manganese oxide) and an α,β-ethylenically unsaturated carboxylic acid. The fillers are those used for golf balls, for example zinc oxide or barium sulfate. The additives are those used for golf balls, for example an antioxidant (e.g. 2,5-di-t-butylhydroquinone) and a vulcanization conditioner. In the present invention, it is an important feature that the vulcanized rubber powder is formulated into the rubber composition for the golf balls. Regarding the rubber physical properties (before pulverizing) of the vulcanized rubber powder, the hardness is preferably 40 to 95, more preferably 55 to 80. If the hardness is outside the above range, the resulting ball has a poor durability. The hardness is measured using a hardness tester (JIS-C type). The impact resilience is preferably not less than 50%, more preferably not less than 60%, and the tensile strength is preferably not less than 70 kg/cm 2 , more preferably not less than 100 kg/cm 2 . The rubber formulated with the vulcanized rubber has a hardness of 50 to 90. If the hardness is more than 90 the resulting golf ball has a poor shot feel and if it is less than 50, the golf ball has a poor durability. The vulcanized rubber powder may be formed from either reclaimed rubber (particularly, waste rubber from one-layer golf balls or the inner core from two or more layer golf balls) or a rubber which is newly vulcanized and then pulverized. It is preferred that the rubber component of the vulcanized rubber powder is a butadiene rubber having a cis-1,4 content of at least 40%. The total rubber component may be constituted by polybutadiene rubber, or other rubbers (e.g. natural rubber, styrene-butadiene rubber, isoprene rubber, chloroprene rubber, butyl rubber, ethylene propylene rubber or acrylonitrile rubber) may be blended in the above polybutadiene rubber in an amount of not more than 45 parts by weight, based on 100 parts by weight of the rubber component. When the vulcanized rubber powder is made from a newly produced vulcanized rubber, the vulcanizing agent used is one that is normally used, for example, an organic peroxide (e.g. dicumyl peroxide or 1,1-bis-(t-butylperoxy)-3,3,5-trimethyl-cyclohexane), sulfur or N,N'phenylenebismaleimide. The vulcanizing agent may be contained in an amount of from 0.1 to 6 parts by weight, preferably from 0.5 to 3 parts by weight, based on 100 parts by weight of the rubber component. The rubber composition of the vulcanized rubber powder may contain a co-crosslinking agent, such as products obtained by reacting an α,β-ethylenically unsaturated carboxylic acid with a metal oxide (e.g. zinc oxide, etc.) in the rubber composition, powdered metal salts (e.g. normal salt, basic salt, etc.) of an α,β-ethylenically unsaturated carboxylic acid or polyfunctional monomers. Particularly, the metal salts (particularly, zinc salt) of an α,β-ethylenically unsaturated carboxylic acid are preferred. In order to adjust the specific gravity and improve the strength of the vulcanized rubber powder, one or more types of inorganic fillers (e.g. barium sulfate or calcium carbonate) may be included. Further, softening agents and liquid rubbers may also be included in order to control the hardness of the vulcanized rubber powder, and antioxidants may also be appropriately included in order to improve the resistance to ageing. The rubber composition thus obtained may then be subjected to press vulcanization at 140 to 200°C for 8 to 60 minutes, preferably 150 to 175°C for 10 to 40 minutes, or subjected to radiation crosslinking using γ rays to provide a vulcanized rubber which is then pulverized to obtain the vulcanized rubber powder. The shape of the vulcanized rubber before pulverizing is not specifically limited, but it may have a size and shape suitable to be processed by a normal pulverizer. The size of the particles of the vulcanized rubber powder after pulverizing is not specifically limited, but they are preferably not more than 1000 µm. The lower limit of the particle size of the vulcanized rubber powder is not specified and it may be as low as 0.1 µm. Any method may be used to pulverize the vulcanized rubber. Preferably, the vulcanized rubber is formed into tips of about 1 to 3 mm at normal temperature, and then the tips are frozen (e.g, cooled using liquid nitrogen or dry ice) and then pulverized to obtain an extremely fine vulcanized rubber powder, whereby the dispersibility on kneading is improved. The vulcanized rubber powder thus obtained is formulated in the rubber composition for making the golf ball of the present invention, which is kneaded with a roll, a kneader, a Banbury mixer, etc. Then, the resulting blend is charged in a die and vulcanized to form a one-piece solid golf ball or an inner core of a two or more piece solid golf ball. Regarding the two or more piece solid golf ball, the inner core is covered with a cover which is mainly composed of an ionomer. The amount of the vulcanized rubber powder is preferably from 1 to 35 parts by weight, particularly 5 to 20 parts by weight, based on 100 parts by weight of the base rubber. When the amount of the vulcanized rubber powder is less than the above range, the effect for improving durability is insufficient. On the contrary, when the amount is greater than the above range, workability on mixing is inferior. The vulcanized rubber powder may be formulated together with other materials for preparing the rubber composition for making the golf ball, and then kneaded to form a rubber composition containing the vulcanized rubber powder. Alternatively, the rubber composition for the golf ball may prepared be as a preliminary, and then the vulcanized rubber powder is incorporated therein. The former method is normally used. The rubber composition in which the vulcanized rubber powder has been included may be vulcanized under the same condition as that of the prior art, for example, it is conducted at 140 to 200°C for 8 to 40 minutes, preferably 150 to 18°C for 10 to 25 minutes. EXAMPLES The following Examples and Comparative Examples further illustrate the present invention in detail but are not to be construed to limit the scope thereof. Examples 1 to 3 and Comparative Example 1 In order to obtain a vulcanized rubber powder used for preparing golf balls of the Examples, a rubber composition shown in Table 1 was firstly prepared. Component Amount (parts by weight) Polybutadiene rubber 100 Zinc oxide 22 Methacrylic acid 20 Antioxidant 0.2 Calcium carbonate 5 Vulcanization agent 1.6 The above rubber components were kneaded by a 10 liter kneader and then sheeted by an open roll. It was then press-vulcanized at 165°C for 18 minutes to make a vulcanized rubber sheet. Physical properties of the resulting vulcanized rubber are shown in Table 2. Physical properties Measured value Hardness (JIS-C) 70 Impact resilience (%) 74 Tensile strength (kgf/cm 2 ) 150 Then, the above vulcanized rubber sheet was pulverized roughly into tips of 1 to 3 mm by a pulverizer and cooled, and then pulverized into powders having a particle size of not more than 800 µm. The resulting vulcanized rubber powder was formulated in the rubber components shown in Table 3 to prepare a rubber composition. It was then charged in a mold and vulcanized at 165°C for 20 minutes to make a one-piece solid golf ball having an outer diameter of 42.7 mm. The polybutadiene rubber, antioxidant and vulcanization initiator used were the same as those shown in Table 1. Physical properties of the resulting golf ball are shown in Table 4. Example 1 Example 2 Example 3 Comparative Example 1 Polybutadiene rubber 100 100 100 100 Zinc oxide 23 23 23 23 Methacrylic acid 20 20 20 20 Antioxidant 0.5 0.5 0.5 0.5 Vulcanizing agent 1.5 1.5 1.5 1.5 Vulcanized rubber powder 10 20 30 0 Unit: parts by weight Example 1 Example 2 Example 3 Comparative Example 1 Weight (g) 45.6 45.7 45.8 45.5 Compression (PGA) 92 93 93 92 Impact resilience 1.000 1.003 1.002 1.000 Hardness (JIS-C) Center-Surface 63-76 60-76.5 60-76.5 67-75.5 Durability 155 144 141 100 As is apparent from Tables 3 and 4, the golf balls of Examples 1 to 3 wherein the vulcanized rubber powder was formulated showed excellent durability in comparison with the golf ball of Comparative Example 1 wherein no vulcanized rubber powder was formulated. Regarding impact resilience which is one of the evaluation criteria for flying performances, the golf balls of Examples 1 to 3 have the value which is the same as or superior than that of the golf ball of Comparative Example 1. Regarding a hitting test by 10 testers including some professional golfers, it was evaluated that the golf balls of Examples 1 to 3 have excellent hit feeling in comparison with the golf ball of Comparative Example 1. No deterioration of flight performances and hit feeling due to the addition of the vulcanized rubber powder were observed. Examples 4 to 6 and Comparative Example 2 A rubber composition wherein the same vulcanized rubber powder as that used in Examples 1 to 3 was formulated in an amount shown in Table 5 was prepared. The resulting rubber composition was charged in a mold and vulcanized at 160 °C for 25 minutes to make an inner core having an outer diameter of 38.5 mm. Then, a cover was formed by covering the inner core with a mixture containing 100 parts by weight of ionomer resin and 2 parts by weight of titanium oxide to make a two-piece solid golf ball having a diameter of 42.7 mm. The same materials as those of Table 3 were used. The ionomer resin used for forming the cover is a mixture of HI-MILAN 1706 and HI-MILAN 1605 manufactured by Mitsui Du Pont Polychemical Co. (weight ratio: 50/50). Example 4 Example 5 Example 6 Comparative Example 2 Polybutadiene rubber 100 100 100 100 Zinc oxide 20 20 20 20 Zinc acrylate 30 30 30 30 Antioxidant 3 3 3 3 Vulcanizing agent 4 4 4 4 Vulcanized rubber powder 5 10 20 0 Unit: parts by weight The physical properties of the resulting two-piece solid golf balls are shown in Table 6. Regarding impact resilience, the number is expressed as an index when the number of the golf ball of Comparative Example 2 is made 1.000. Regarding durability, the number is expressed as an index when the golf ball of Comparative Example 2 is made 100. Regarding the hardness, the hardness of the center and surface of the inner core is shown, respectively. Example 4 Example 5 Example 6 Comparative Example 2 Weight (g) 45.1 45.0 45.0 45.1 Compression 88 88 89 87 Impact resilience 1.000 1.002 1.002 1.000 Hardness (JIS-C) 59-82 61-82 62.5-83 67-80 Center-Surface Durability 111 123 114 100 As is apparent from Tables 5 and 6, the golf balls of Examples 4 to 6 wherein the vulcanized rubber powder was formulated showed excellent durability in comparison with the golf ball of Comparative Example 2 wherein no vulcanized rubber powder was formulated. Regarding impact resilience which is one of the evaluation criteria, the golf balls of Examples 4 to 6 have the value which is the same as or superior than that of the golf ball of Comparative Example 2. Regarding a hitting test by 10 testers including some professional golfers, it was evaluated that the golf balls of Examples 4 to 6 have excellent hit feeling in comparison with the golf ball of Comparative Example 2. No deterioration of flying performances and hit feeling due to the addition of the vulcanized rubber powder were observed. As is described above, according to the present invention, a golf ball having excellent durability can be provided by formulating a vulcanized rubber powder in the golf ball of one-layer structure or the inner core of the golf ball of at least two-layer structure comprising the outer layer and inner core of at least one layer.

Claims: A one-piece solid golf ball obtainable by forming a mixture of: a base rubber, a powder of a vulcanized rubber, and a vulcanizing agent; and vulcanizing the said mixture in order to form the golf ball. A one-piece solid golf ball as claimed in claim 1 wherein the base rubber is a butadiene rubber comprising at least 40% of cis-1,4-butadiene. A one-piece solid golf ball as claimed in claim 1 or claim 2 wherein the vulcanized rubber powder is a powder of a vulcanized rubber having a hardness of from 40 to 95 (JIS-C hardness tester), an impact resilience of 50% or more and a tensile strength of 70 Kg/cm 2 or more. A one-piece solid golf ball as claimed in claim 3 wherein the vulcanized rubber powder is a powder of a rubber composition comprising a butadiene rubber containing at least 40% of cis-1,4-butadiene, a metal salt of an α,β-ethylenically unsaturated carboxylic acid, an organic peroxide vulcanizing agent and a filler. A one-piece solid golf ball as claimed in any one of the preceding claims wherein the vulcanizing agent is dicumyl peroxide. A one-piece solid golf ball as claimed in any one of the preceding claims wherein the mixture further comprises a co-crosslinking agent. A one-piece solid golf ball as claimed in claim 6 wherein the co-crosslinking agent is zinc (meth)acrylate. A one-piece solid golf ball as claimed in any one of the preceding claims wherein the vulcanized rubber powder is contained in the mixture in an amount of from 1 to 35 parts by weight based on 100 parts by weight of the base rubber. A one-piece solid golf ball as claimed in any one of the preceding claims wherein the vulcanizing agent is contained in the mixture in an amount of from 0.1 to 6 parts by weight based on 100 parts by weight of the base rubber. A one-piece solid golf ball as claimed in any one of the preceding claims wherein the co-crosslinklng agent is contained in the mixture in an amount of from 5 to 50 parts by weight based on 100 parts by weight of the base rubber. A two or more piece solid golf ball comprising an inner core and a cover covering the inner core, the inner core consisting of a centre only or comprising a centre with one or more outer layers disposed over the centre, wherein the centre of the inner core is obtainable by forming a mixture of: a base rubber, a powder of a vulcanized rubber which has a JIS C hardness of from 40 to 95, and a vulcanizing agent, and vulcanizing the said mixture to form the centre of the inner core, wherein the centre of inner core so produced has a JIS C hardness of from 50 to 90. A two or more piece solid golf ball as claimed in claim 11 wherein the base rubber is a butadiene rubber comprising at least 40% of cis-1,4-butadiene. A two or more piece solid golf ball as claimed in claim 11 or claim 12 wherein the vulcanized rubber powder is a powder of a vulcanized rubber having an impact resilience of 50% or more and a tensile strength of 70 Kg/cm 2 or more. A two or more piece solid golf ball as claimed in claim 13 wherein said vulcanized rubber powder is a rubber composition comprising a butadiene rubber containing at least 40% of cis-1,4-butadiene, a metal salt of an α,β-ethylenically unsaturated carboxylic acid, an organic peroxide vulcanizing agent and a filler. A two or more piece solid golf ball as claimed in any one of claims 11 to 14 wherein the vulcanizing agent is dicumyl peroxide. A two or more piece solid golf ball as claimed in any one of claims 11 to 15 wherein the mixture further comprises a co-crosslinking agent. A two or more piece solid golf ball as claimed in claim 16 wherein the co-crosslinking agent is zinc (meth)acrylate. A two or more piece solid golf ball as claimed in any one of claims 11 to 17 wherein the vulcanized rubber powder is contained in the mixture in an amount of from 1 to 35 parts by weight based on 100 parts by weight of the base rubber. A two or more piece solid golf ball as claimed in any one of claims 11 to 18 wherein the vulcanizing agent is contained in the mixture in an amount of from 0.1 to 6 parts by weight based on 100 parts by weight of the base rubber. A two or more piece solid golf ball as claimed in any one of claims 11 to 19 wherein the co-crosslinklng agent is contained in the mixture in an amount of from 5 to 50 parts by weight based on 100 parts by weight of the base rubber.

Inventors: HIRAOKA HIDENORI, KOIZUMI YOSHIMASA, HIRAOKA, HIDENORI, KOIZUMI, YOSHIMASA
Applicants: SUMITOMO RUBBER IND, SUMITOMO RUBBER INDUSTRIES, LTD.
Application year: 1993
Main classification: A63B37
IPC codes: C08L9, A63B37