METHOD FOR THE FABRICATION OF MULTIPOLE MAGNETS

Abstract: A method for the fabrication of multipole magnets, which method comprises the steps of (i) screen or stencil printing an ink comprising a mixture of particles of a magnet material and a carrier material onto a backing sheet in a predetermined pattern; (ii) curing or drying the patterned sheet and magnetising the areas forming the predetermined pattern in step (i) using a magnetic field perpendicular to the plane of the backing sheet to produce North poles on one side of the sheet and South poles on the other side of the sheet; (iii) screen or stencil printing an ink comprising a mixture of a magnet material and a carrier material onto a backing sheet in a pattern which is complementary to the pattern in step (i), the ink being printed in those areas where no ink was printed in step (i); (iv) curing or drying the patterned sheet and magnetising the areas forming the complementary pattern in step (iii) using a magnetic field perpendicular to the plane of the backing sheet to produce North poles on one side of the sheet and South poles on the other side of the sheet; (v) turning over the sheet from step (iv); and (vi) bringing the sheet from step (ii) and the reversed sheet from step (v) together form a laminate, thereby forming a multiple magnet.

Description: METHOD FOR THE FABRICATION OF MULTIPOLE MAGNETS The present invention relates to a method for the fabrication of multipole magnets and, in particular, to a method for the fabrication of multipole magnets comprising a crystalline phase of an alloy of Fe, B and R, where R is a rare earth element. Magnetic materials and permanent magnets are important materials which are used in many applications, including electrical appliances and electronic devices. In view of the increasing requirement for miniaturization and the greater demands placed on electrical appliances and electronic devices there has been an increasing demand for improved magnetic materials and permanent magnets. EP-A-0101552 describes magnetic materials based on alloys of the type Fe-B-R containing at least one stable compound of the ternary Fe-B-R type, where R is a rare earth element including yttrium, which compound can be magnetised to become a permanent magnet. The amount of rare earth R is generally in the range of from 8 to 30 atomic percent. EP-A-0108474 describes a magnetically hard alloy composition comprising at least 10 atomic percent of one or more rare earth elements, 0.5 to 10 atomic percent of boron; and iron or mixtures of iron with a transition metal element, the alloy containing a major portion of magnetically hard, fine crystallites having an average diameter of less than 400 nanometres. With the development of the rare-earth magnets, one of the major benefits is the high coercivity, or resistance to demagnetisation. This means that a high applied magnetic field is required before any permanent damage to the magnet can occur. This is particularly relevant to magnets which are very thin (in the direction of magnetism) , and already have a significant internally generated demagnetising field due to the aspect ratio. Many applications now demand (or would benefit from) magnetic components that are very thin, due to constraints of size and weight, and can only be addressed by utilising the high coercivity of these types of magnet. Problems arise in respect of the magnetisation of these materials as their inherently high magnetic stability means that very high external fields must be applied to achieve a high percentage of the available magnetic strength (saturation) . For isotropic materials such as certain melt spun NdFeB alloys the situation is even worse because the magnetisation process is attempting to magnetise the majority of grains in the material in a direction which is not a preferred or "easy" direction. Thus, in order to achieve a magnetisation which is within a few percent of the saturation value, external fields of three to four times the intrinsic coercivity are required. The normal method of magnetising these high coercivity materials is to dicharge a very large current, from a bank of capacitors, through a copper coil or arrangement of copper wires. The cross sectional area of the copper wire obviously has to be large enough to prevent melting of the copper by resistance heating. It is not unusual for currents in excess of 10,000 amps to be required in order to generate sufficiently high magnetising fields. Apart from the fact that these materials are difficult to magnetise, the types of application for which they are required are becoming more demanding. For example, one of the major markets for these materials is in the permanent magnet components for motors. Depending on the design of the system these may be a number of separately magnetised components that are assembled in a circular arrangement or a number of magnetised "poles" may be imprinted around the circumference of a continuous ring sample. The latter is becoming the favoured route as this reduces the difficulty and costs of assembly. As motors become smaller, (i.e. smaller rings) and the number of poles required increases, the difficulty of imprinting the required pattern increases, due to the physical volume of the copper windings required to generate the high fields. The combination of materials which are difficult to magnetise, small diameter components and more complex magnetisation patterns (i.e. larger numbers of poles) all combine to limit the capability of the existing capacitor discharge technology. A further limitation is the precision of the transition between the imprinted poles. For devices such as stepper motors, which rely greatly on the accuracy of the imprinted pattern and the width of the transition for precision movement, there is a need to control all aspects of the magnetisation pattern; something which is exceedingly difficult to do with conventional magnetisation techniques. The need for high definition of poles in all motor systems becomes more important as the efficiency of designs improves. . We have now developed a method for the production of multipole magnets which avoids the disadvantages of the prior art method discussed above. Accordingly, the present invention provides a method for the fabrication of multipole magnets, which method comprises the steps of i) screen or stencil printing an ink comprising a mixture of particles of a magnet material and a carrier material onto a backing sheet in a predetermined pattern; ii) curing or drying the patterned sheet and magnetising the areas forming the predetermined pattern in step (i) using a magnetic field perpendicular to the plane of the backing sheet to produce North poles on one side of the sheet and South poles on the other side of the sheet; iii) screen or stencil printing an ink comprising a mixture of a magnet material and a carrier material onto a backing sheet in a pattern which is complementary to the pattern in step (i) , the ink being printed in those areas where no ink was printed in step (i) iv) curing or drying the patterned sheet and magnetising the areas forming the complementary pattern in step (iii) using a magnetic field perpendicular to the plane of the backing sheet to produce North poles on one side of the sheet and South poles on the other side of the sheet; v) turning over the sheet from step (iv) ; and vi) bringing the sheet from step (ii) and the reversed sheet from step (v) together form a laminate, thereby forming a multipole magnet. The backing sheet which is used in the method of the present invention may be paper or a film material. Optionally, the paper or film material may be coated with a release agent. The screen or stencil printing may be carried out according to well known techniques, using conventional screen or stencil printing equipment, using either a screen, where the mesh size is large enough to avoid clogging by the magnet particles, or more preferably (especially for relatively thick printed layers) a simple metal stencil typically of the order of 0.1 to 2 mm thick. The screen and stencil designs are produced by conventional methods. Whilst the magnet material may be any permanent magnetic material, it is preferred that it is an alloy of the type Fe-B-R, where R is a rare earth metal, preferably neodymiu . The magnet material will generally be in the form of fine particles of a magnet powder, preferably the powder having a particle size of less than 100 micrometres. The carrier material is preferably a low viscosity carrier material, typically having a viscosity in the range of from 10 to 1000 centipoise. The carrier material may be, for example, an epoxy resin, either as a liquid resin or dissolved in suitable solvents, an air activated or chemically activated silicone rubber, a cyanoacrylate, polyvinyl alcohol, a thermosetting or thermoplastic polymer, or a low melting point metal. Epoxy resin based carrier materials are generally preferred for use in the invention. The magnet powder is generally contained in the magnet ink in an amount of from 10 to 60% by volume of the ink composition. Preferably the magnet ink is screen printed onto the backing sheets in steps (i) and (iii) of the method of the invention and, accordingly, the ink should have a suitable viscosity for appropriate printing. After the backing sheets have been printed in steps (i) and (iii) the patterned sheets are cured or dried prior to the magnetisation step. For example, if an epoxy resin is used as the carrier material then it can be cured to give a semi-rigid structure. The magnetisation which is carried out in steps (ii) and (iv) may be carried out using a simple magnetisation field perpendicular to the plane of the backing sheet, to produce North poles on one side of the sheet and South poles on the other side of the sheet. No complicated equipment is required to effect such magnetisation. As previously indicated, the pattern which is produced in step (iii) of the method of the invention is complementary to the pattern produced in step (i) so that when the pattern sheet from step (iv) is turned over, it will match with the pattern produced in step (ii) to form a multipole magnet. One or both of the sheets produced in steps (ii) and (iv) may be coated with an adhesive prior to the lamination in step (vi) of the method of the invention. The lamination will generally be carried out under heat and/or pressure in order to produce a stable structure. The backing sheet upon which the patterns are printed may be retained on either side of the laminate to provide physical support and protection, or if the backing sheets are coated with a suitable release agent they may be removed, thereby minimising air gaps in the finished assembly. Using the method of the present invention a strip of multipole magnets is produced which may then be wound around a circular former to produce a rotor assembly. Alternatively, the multipole magnet may be used in its linear form in a sensor or actuator. The patterns which are produced in steps (i) and (iii) of the present invention may be simple patterns of a bar type format, or may be more complex patterns which are impossible to produce by conventional magnetisation methods. Furthermore, several different magnetisation patterns can be combined into a single component, if desired. For example offset patterns may be produced, such patterns being of use in stepper motors. Alternatively graduated spacing may be provided for position sensors, or herringbone patterns produced for photocopier rollers. The definition between the poles of the multipole magnet is high using the technique of the present invention and the spacing between the poles is limited only by the resolution of the printing technique. Furthermore, the size of the component is limited only by the size of the printing equipment. Using the method of the present invention very thin ulitpole magnets, of the order of 0.2mm in thickness, can be produced. The present invention will be further described with reference to the accompanying drawings, in which; Figure 1 is a diagram of a typical multipole motor ring; Figures 2a and 2b are a plan view and side elevation, respectively, of a backing sheet printed with a predetermined magnetic pattern, after magnetisation; Figure 3 illustrates two components printed with predetermined patterns, after magnetisation, ready for lamination; and Figure 4 illustrates the two components of Figure 3 laminated together; Figure 5 illustrates an offset pattern printed on one component, for proportional control in stepper motors; and Figure 6 illustrates a herringbone pattern printed on one component, for use in photocopier rollers. Referring to the drawings, Figure 1 illustrates a typical multiple motor ring comprising a plurality of magnetic sections 1. Each magnetic section 1 comprises either a South pole at the exterior surface of the ring or a North pole at the exterior surface of the ring, the North and South poles alternating around the ring. Each segment then presents the opposite pole to the inner surface of the ring, i.e. a segment which has a South pole facing outwards will have a North pole facing inwards. Referring to Figures 2a and 2b, a backing sheet 2 has a plurality of segments 3 of a magnet ink printed thereon. The printed segments 3 are arranged in a predetermined pattern and are magnetised, by means of a magnetic field, to produce a plurality of North poles facing upwardly as viewed in Figure 2b and a plurality of South poles facing downwardly. Referring to Figure 3, a backing sheet 2 with its predetermined pattern of printed segments 3 has postioned thereabove a complementary sheet 4 with segments 5 printed in a predetermined pattern thereon. The printed segments 5 on backing sheet 4 are magnetised so that the North poles of the magnets face downwards and the South poles of the magnets face upwards, as viewed in section in Figure 3. Thus, the printed pattern on backing sheet 4 is complementary to that on backing sheet 2. Figure 4 illustrates the laminate produced by laminating backing sheets 2 and 4 together. It will be noted that in the finished tape, segments 3 alternate with segments 5 along the length of the tape. The backing sheets 2 and 4, if coated with a release material, may be removed from the laminated assembly, if desired. If adhesion of the two components during the lamination process is not effected by further curing of the binder, then prior to the lamination of sheet 4 to sheet 2, one or both of the sheets is sprayed with a suitable adhesive and the lamination is then effected using heat and/or pressure. The laminated assembly illustrated in Figure 4 may be used to form a multiple rotor as shown in Figure 1. Figure 5 illustrates one component of a laminate in which an offset pattern is printed to provide proportional control in stepper motors. The areas 7 and 8 are printed with a magnet ink in a regular pattern, but with a different pitch. The two components are then laminated in the same way as described above. The spacings between the patterned areas 7 and 8 are adapted to receive a complementary pattern printed on a second component (not shown) to form a laminate. Figure 6 illustrates one component of a laminate in which a herringbone pattern is printed as areas 9. The spacings between the areas 9 are adapted to receive a complementary pattern printed on a second component (not shown) to form a laminate. The present invention will be further described with reference to the following Example. EXAMPLE 1 Printed magnet patterns were produced by screen printing a magnetic paste through a stencil mask consisting of a series of slots; 1mm wide, 5 mm long, and spaced evenly 1.5 mm apart, cut into 0.25 mm thickness stainless steel, to produce the print pattern as shown in Figure 7. The magnetic paste was prepared from a 50 volume % loading of Magnequench MQP-D NdFeB powder, <63 μ, in size, dispersed in a slow curing, low viscosity liquid epoxy resin system. The paste was stencil printed by hand onto a 0.1 mm thick polyster sheet substrate and the printed sheets were then cured at 100 C for 30-60 minutes before magnetisation. The printed magnet patterns were magnetised by placing the printed substrate between the closely spaced poles (approx. 5 mm pole gap) of an electromagnet and applying full power (120V, 12.5A) for 10 seconds. The printed strips were thus magnetised normal to the substrate. All the print patterns were aligned the same way between the magnetising poles such that the printed side gave a nominal "north" for the direction of magnetisation (Figs. 2a, 2b). Pairs of printed pattern, were then laminated together, printed side inwards, to form an alternating pattern of opposite poles on such surface, with the substrate forming the outermost layers, as shown in Figures 3 and 4. In practice, due to the slight "slumping" of the magnetic paste during printing and curing, the separation between printed bars needs to be slightly larger than their width in order that the two layers can interlock. In this example, bars of 1 mm width were printed onto each substrate with 1.5 mm separation between bars. By control of the distance between printed magnets on either of the two substrates the radius of curvature for an interlocked pattern can be controlled, allowing its use on, for example, a cylindrical rotor. Magnetic "profile" measurements were carried out using a three axis (XYZ) table fitted with a high sensitivity Linear Hall Effect sensor (type UGN3503) at the base of the moving arm. Both positioning and magnetic field strength measurements of the sensor were carried out by computer control. The results obtained for an interlocking pattern of 1 mm wide poles, with alternating north and south transitions, give good agreement with a finite element model, and shown a regular sinusoidal magnetisation pattern. The measured results are shown in Figures 8, 9 and 10 for the interlocked arrangement produced above at increasing total effective airgaps (TEAGS) of 0.75, 1.25 and 2.25 mm, respectively. The TEAG is the distance from active element of the sensor and -l i¬ the printed magnet surface. At the substrate surface, corresponding to a TEAG of effective airgap of 0.75 mm (Figure 8) the field varies sinusoidally along the measurement path with peak values of ± 20 mT (± 200 gauss) at the centre of each alternating pole. At larger TEAGS of 1.25 and 2.25 mm (Figures 9 and 10) the measured field levels fall off. The results for Figures 8, 9 and 10 are in good agreement with the calculated values from the finite element model for TEAGS of 0.75, 1.25 and 2.25 mm shown in Figures ii, 12 and 13, respectively.

Claims: CLAIMS : 1. A method for the fabrication of multipole magnets, which method comprises the steps of i) screen or stencil printing an ink comprising a mixture of particles of a magnet material and a carrier material onto a backing sheet in a predetermined pattern; ii) curing or drying the patterned sheet and magnetising the areas forming the predetermined pattern in step (i) using a magnetic field perpendicular to the plane of the backing sheet to produce North poles on one side of the sheet and South poles on the other side of the sheet; iii) screen or stencil printing an ink comprising a mixture of a magnet material and a carrier material onto a backing sheet in a pattern which is complementary to the pattern in step (i), the ink being printed in those areas where no ink was printed in step (i) iv) curing or drying the patterned sheet and magnetising the areas forming the complementary pattern in step (iii) using a magnetic field perpendicular to the plane of the backing sheet to produce North poles on one side of the sheet and South poles on the other side of the sheet; v) turning over the sheet from step (iv) ; and vi) bringing the sheet from step (ii) and the reversed sheet from step (v) together form a laminate, thereby forming a multiple magnet. 2. A method as claimed in claim 1 wherein the backing sheet is paper or a film material. 3. A method as claimed in claim 1 or claim 2 wherein the magnet material is an alloy of the type Fe-B-R, where R is a rare earth metal. 4. A method as claimed in claim 3 wherein the rare earth metal is neodymiu . 5. A method as claimed in any one of the preceding claims wherein the magnet material has a particle size of less than 100 micrometres. 6. A method as claimed in any one of the preceding claims wherein the carrier material is an epoxy resin based carrier material, an air activated or chemically activated silicone rubber, a cyanoacrylate, polyvinylalcohol, a thermosetting or thermoplastic polymer, or a low melting point metal. 7. A method as claimed in any one of the preceding claims wherein one or both of the sheets produced in steps (ii) and (iv) is/are coated with an adhesive prior to the lamination in step (vi) . 8. A method as claimed in any one of the preceding claims wherein the backing sheets are coated with a release agent and are removed after the formation of the laminate in step (vi) . 9. A method as claimed in any one of the preceding claims wherein the ink is printed onto the backing sheets in steps (i) and (iii) using a screen or stencil printing technique. 10. A multipole magnet which has been produced by a method as claimed in any one of the preceding claims. 11. A multipole magnet as claimed in claim 10 which is wound round a circular former to produce a rotor assembly. 12. A multipole magnet as claimed in claim 10 which is used in linear form in a sensor or actuator.

Inventors: BELL JAMES FRASER, CAMPBELL JOHN STEWART, HOLT LYN, JEFFREY STEVEN ROY, BELL, JAMES, FRASER, CAMPBELL, JOHN, STEWART, HOLT, LYN, JEFFREY, STEVEN, ROY
Applicants: BELL JAMES FRASER, CAMPBELL JOHN STEWART, COOKSON GROUP PLC, HOLT LYN, JEFFREY STEVEN ROY
Application year: 1993
Main classification: H01F41
IPC codes: H01F41, H02K15