Organosiloxane compositions exhibiting improved bonding to substrates during curing

Abstract: Organosiloxane compositions curable by a platinum-catalyzed hydrosilation reaction contain a characterizing ingredient of a silane comprising an silicon-bonded alkenyl radical containing at least five carbon atoms and at least one alkoxy group. The silane, or a hydrolysis-condensation product thereof, is optionally used in combination with a catalyst that will promote reaction of the silane with groups present on the surface of the substrate to which bonding is desired.

Description: This invention relates to curable organosiloxane compositions that cure by a platinum-catalyzed hydrosilation reaction and develop strong cohesive bonds to various substrates, particularly aluminum, steel and glass, with which the compositions are in contact with during curing. Organosiloxane compositions that cure by a hydrosilation reaction between alkenyl radicals and silicon-bonded hydrogen atoms are well known. The curing reaction is typically catalyzed by a metal from the platinum group of the periodic table or a compound of one of these metals. The consistency of the cured materials range from gels to elastomers to resins. The ability of these compositions to cure at temperatures from ambient to 200°C. without evolution of undesirable by-products make them suitable for a wide range of applications. A disadvantage to wider acceptance of organosiloxane compositions as coating materials is their relatively poor adhesion to organic and metal substrates. Attempts have been made to improve the adhesion of organosiloxane compositions by the use of primer compositions or adhesion promoters. Organosilicon compounds have been widely used as both primers and adhesion promoters for these compositions. Typical silanes used for these purposes have the formula ASi(OR) 3 , where R represents a lower alkyl radical and A represents a substrate reactive group. Examples of A include ethylenically unsaturated groups such as vinyl radicals and 3-(meth)acryloxypropyl groups, epoxy-containing groups such as gamma-glycidoxypropyl, aminoalkyl, mercaptoalkyl, isocyanato and alkoxy groups. Organosiloxanes containing at least one of these reactive groups per molecule have also been used for these purposes. Adhesion promoting organosiloxanes with one epoxy group and one or more types of reactive groups per molecule are described in U.S. Patent No. 4,912,188, Japanese Laid Open Application No. 3/234,768; and in U.S. Patent No. 4,732,932. Primer compositions and adhesion promoters comprising mixtures or reaction products of two or more organosilicon compounds with at least one reactive group are also known from U.S. Patent No. 4,087,585; U.S. Patent No. 4,737,562; and Japanese Laid Open Application No. 47/36,255. US-A-4,329,273 describes a self-bonding silicone rubber composition comprising (A) 100 parts by weight of a base polymer of the formula, where R is selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, and x is such that the viscosity of the base polymer varies from 100 to 200,000,000 centipoise at 25°C; (B) from 0.5 to 50 parts by weight of a hydride siloxane cross-linking agent; (C) from 1 to 500 parts per million of platinum catalyst; and (D) from 0.1 to 5 parts by weight of a self-bonding additive which is the partial hydrolysis product of a compound of the formula, R a 1 Si(OR 3 ) 4-a wherein R 1 is an aliphatic unsaturated radical selected from the class consisting of alkenyl radicals and alkynyl radicals of 2 to 8 carbon atoms, R 3 is selected from the class consisting of alkyl radicals and cycloalkyl radicals of 1 to 8 carbon atoms and a is 1 and wherein the partial hydrolysis product is such that on the average 16 to 49 mole percent of the hydrocarbonoxy groups of said silane are hydrolyzed. A variety of catalysts have been suggested in these prior proposals to promote a hydrolysis-condensation reaction between the alkoxy and/or hydroxyl groups on the adhesion promoter and the substrate surface. Suitable catalysts include tetraalkyl titanates and chelates such as acetylacetonates derived from metals including aluminum, copper and titanium. A drawback to the use of alkoxysilanes or organosiloxanes with vinyl or allyl reactive groups as adhesion promoters and primer compositions is the inhibiting effect of these groups. This inhibition is particularly evident at curing temperatures below 120°C. An objective of this invention is to provide such alkoxysilane and organosiloxane compositions as adhesion promoters and primer compositions for curable organosiloxane compositions which will not substantially inhibit the cure rate of temperatures below 150°C. This objective is achieved by using a silane with a silicon-bonded alkenyl radical having at least five carbon atoms. This silane also has at least one alkoxy group. In the presence of incidental water and an optional catalyst, this silane, or a hydrolysis-condensation product thereof, reacts with groups present on the surface of the substrate to which bonding is desired. This invention provides a curable organosiloxane composition comprising: A. a polyorganosiloxane containing at least two alkenyl radicals per molecule; B. an organohydrogensiloxane containing an average of at least three silicon-bonded hydrogen atoms per molecule and the silicon-bonded hydrogen atoms in component B being present in a stoichiometric excess relative to the alkenyl radicals in component A; C. a platinum-containing hydrosilation catalyst present in said composition in an amount within the range equivalent to a range of from 1 to 50 parts of platinum per 1 million parts of said curable organosiloxane composition; D. an adhesion promoter selected from silanes represented by the general formula R 2 SiR 3 n (OR 1 ) 3-n , where R 1 and R 3 represent identical or different alkyl radicals, R 2 represents an alkenyl radical having at least 5 carbon atoms and n is 0 or 1, in a concentration of from 0.01 to 10 weight percent based on the total weight of the curable composition. The molar ratio of said silicon-bonded hydrogen atoms in said component B to said alkenyl radicals in said component A is, preferably, in the range of from 2:1 to 4:1, more preferably, in the range of from 2.5:1 to 2.8:1. Preferably, said adhesion promoter (D) is present in said composition in a concentration of from 0.1 to 5 weight percent based on the total weight of the curable composition. In a preferred composition, in said adhesion promoter (D), n is 0, R 2 is CH 2 =CH(CH 2 ) p - and p is an integer with a value of at least 3, and the silicon-bonded organic groups present in said polyorganosiloxane (A) and said organohydrogensiloxane (B) are monovalent unsubstituted or substituted hydrocarbon radicals containing from 1 to 20 carbon atoms. Preferably, in said adhesion promoter (B), R 1 contains from 1 to 4 carbon atoms, and said monovalent hydrocarbon radicals in said polyorganosiloxane (A) and said organohydrogensiloxane (B) are C 1-4 alkyl, phenyl or 3,3,3-trifluoropropyl. In a more preferred composition, at least a portion of said silicon-bonded organic groups are methyl and any remainder are phenyl or 3,3,3-trifluoropropyl. In another preferred composition, said component (B) is a resinous organosiloxane copolymer containing triorganosiloxy and SiO 4/2 units, where the silicon-bonded organic groups are monovalent hydrocarbon radicals. A further preferred composition contains an hydrolysis-condensation catalyst in a concentration of from 0.1 to 1 weight percent based on the weight of said curable organosiloxane composition. More preferably, said hydrolysis-condensation catalyst is selected from tetraalkyl titanates and chelated compounds of aluminum, copper and titanium. The characterizing feature of the present invention is the presence of ingredient D. This organosilicon compound is selected from silanes represented by the general formula R 2 SiR 3 n (OR 1 ) 3-n and partial condensation products of said silanes, where R 1 and R 3 represent identical or different alkyl radicals, R 2 represents an alkenyl radical having at least 5 carbon atoms and n is 0 or 1. Preferably, R 2 is a linear, terminally unsaturated hydrocarbon radical having from 5 to 8 carbon atoms, n is 0 and R 1 is lower alkyl having from 1 to 4 carbon atoms. These preferences are based on the availability of the reactants used to prepare the silane and the efficacy of the silanes as adhesion promoters. The curable composition of this invention can also contain partial condensation products of such a silane which result from the hydrolysis of at least one alkoxy group present on the silane and the subsequent reaction of the resultant compound with at least one adjacent silane molecule to form a siloxane (Si-O-Si) bond. The ability of the condensation product to effectively function as an adhesion promoter or primer composition is adversely affected when the average number of silicon atoms present in the condensation product exceeds about 4. The minimum concentration of ingredient D is a function of a number of variables including the particular adhesion promoter, type of substrate, curing conditions and the other ingredients present in the curable organosiloxane composition. The concentration will typically be from 0.01 to 10 weight percent, preferably from 0.1 to 5 weight percent, based on the total weight of the curable composition. While not willing to be bound by any theory, it is believed that ingredient D should be at least partially incompatible with the other organosilicon compounds present in the curable organosiloxane composition. This partial incompatibility will cause a major portion of the adhesion promoter to migrate to the interface between the uncured organosiloxane composition and the substrate where it can most effectively function to bond the organosiloxane composition to the substrate. The compositions of this invention optionally contain a catalyst to promote the hydrolysis/condensation reaction of ingredient D as well as a reaction between the alkoxy or other groups present on this ingredient with the hydroxyl or other reactive groups present on the surface of the substrate during the curing reaction. Catalysts that are useful for this purpose are tetraalkyl titanates such as tetra-n-butyl titanate and chelated metal compounds, including the beta-diketonates of metals such as aluminum, copper and titanium. The catalyst concentration is typically from 0.1 to 1 weight percent, based on the weight of the curable organosiloxane composition. In addition to ingredient D and the optional hydrolysis/condensation catalyst, the curable compositions of this invention comprise a polyorganosiloxane containing an average of at least two alkenyl radicals per molecule, ingredient A, an organohydrogensiloxane containing an average of at least three silicon-bonded hydrogen atoms per molecule, ingredient B, and a hydrosilation catalyst, ingredient C. Depending upon the type of cured material desired, the composition may also contain at least one reinforcing or non-reinforcing filler. Ingredient A of the present composition is a polyorganosiloxane containing an average of at least two ethylenically unsaturated hydrocarbon radicals per molecule. The viscosity of this ingredient can range from a liquid to a high viscosity gum that will flow only under pressure. Two of the ethylenically unsaturated hydrocarbon radicals present in ingredient A are preferably located at the terminal positions of the molecule in the form of dimethylvinylsiloxy, methylphenylvinylsiloxy or dimethyl-5-hexenylsiloxy groups. If the curable composition is a liquid or pasty material, the viscosity of ingredient A is preferably from 1 to 500 Pa·s and this ingredient is preferably a polydiorganosiloxane. In addition to diorganosiloxane and terminal triorganosiloxy groups. ingredient A can contain one or more monoorganosiloxane units per molecule, resulting in branching of the polymer molecule. Polymers of this type are described in U.S. Patent No. 3,284,406. Alternatively, ingredient A can be a semi-solid polydiorganosiloxane, known in the art as a gum, exhibiting a viscosity of up to 1000 Pa·s at 25°C. Curable compositions containing this type of polydiorganosiloxane are typically prepared by blending the ingredients under high shear using a two- or three-roll rubber mill or dough-type mixer. The silicon-bonded organic groups of ingredient A and the organohydrogensiloxane referred to as ingredient B are monovalent unsubstituted or substituted hydrocarbon radicals containing from 1 to 20 carbon atoms. Halogen atoms are preferred substituents. Preferably, these hydrocarbon radicals are C 1-4 alkyl, phenyl or a perfluoroalkylethyl radical such as 3,3,3-trifluoropropyl, this preference being based on the commercial availability of the intermediates used to prepare ingredients A and B. Most preferably, at least a portion of the repeating units of ingredients A and B contain silicon-bonded methyl radicals. Ingredient A is cured by a hydrosilation reaction between the ethylenically unsaturated hydrocarbon radicals of this ingredient and silicon-bonded hydrogen atoms of the organohydrogensiloxane, ingredient B. In a typical curable composition of this invention, one or more polydiorganosiloxanes containing an average of at least two ethylenically unsaturated hydrocarbon radicals per molecule react with a relatively low molecular weight, liquid organohydrogensiloxane containing an average of at least three silicon-bonded hydrogen atoms per molecule. Ingredient B can contain from 4 to 20 silicon atoms per molecule and, preferably, exhibits a viscosity of up to 10 Pa·s at 25°C. Ingredient B contains repeating units of the formulae HSiO 1.5 , RHSiO and/or R 2 HSiO 0.5 . The molecules of this ingredient may also include one or more monoorganosiloxane, diorganosiloxane, triorganosiloxy and SiO 4/2 units that do not contain silicon-bonded hydrogen atoms. In these formulae R is an unsubstituted or substituted monovalent hydrocarbon radical selected from the same group as those defined for ingredient A of the present compositions. Alternatively, ingredient B can be a cyclic compound containing at least 4 organohydrogensiloxane units of the formula RHSiO or a compound of the formula HR 2 SiO[(HRSiO) a SiR 2 H, where a is at least 1. Most preferably, R is methyl and ingredient B is a linear trimethylsiloxy-terminated polymethylhydrogensiloxane or a dimethylsiloxane/methylhydrogensiloxane copolymer containing an average of from 5 to 50 repeating units per molecule of which from 30 to 100 percent are methylhydrogensiloxane units. The molecular weights of ingredients A and B, together with the number and distribution of the silicon-bonded hydrogen atoms and ethylenically unsaturated hydrocarbon radicals within these ingredients, will determine the location of crosslinks in the cured product and can range from a glass-like resin to an elastomer to a gel. To obtain a crosslinked material the sum of the average number of alkenyl radicals per molecule of ingredient A and the average number of silicon-bonded hydrogen atoms in ingredient B must be greater than 2. The concentration of crosslinks per unit volume of cured organosiloxane composition is often referred to as the "crosslink density" and determines certain physical properties of the cured elastomer, particularly hardness, tensile strength and elongation. The particular combinations of polydiorganosiloxane(s) and curing agent(s) yielding the desired combination of physical properties can readily be determined by routine experimentation with a knowledge of this invention. The molar ratio of silicon-bonded hydrogen atoms in the organohydrogensiloxane to the vinyl or other ethylenically unsaturated hydrocarbon radicals present in ingredient A is a major factor in determining the properties of the elastomer or other cured material obtained from the composition. Because of the difficulty often experienced in achieving a complete reaction between all of the silicon-bonded hydrogen atoms and all of the vinyl or other ethylenically unsaturated hydrocarbon radicals present in the reaction mixture, it is necessary to have a stoichiometric excess of the silicon-bonded hydrogen atoms in a curable composition. The presence in the curable organosiloxane composition of a polyorganosiloxane containing a preferred hexenyl radical has been found to slightly inhibit curing of the composition. This inhibition can be compensated for by increasing the molar ratio of silicon-bonded hydrogen atoms to alkenyl radicals to a minimum of 2, preferably 2.5. A ratio of 2.8 silicon-bonded hydrogen atoms per vinyl or other ethylenically unsaturated hydrocarbon radical has been found to yield optimum combinations of physical properties and completeness of curing for the curable compositions described in the accompanying examples. The preferred ratio for a given composition will be determined at least in part by the average molecular weight of ingredient A and the type of curing agent. The upper limit for the ratio is 4. Hydrosilation reactions are typically conducted in the presence of a catalyst that is a metal from the platinum group of the periodic table or a compound of such a metal. Platinum, rhodium and compounds of these metals have been shown to effectively catalyze hydrosilation reactions. Platinum compounds such as hexachloroplatinic acid, and particularly complexes of these compounds with relatively low molecular weight vinyl-containing organosiloxane compounds, are preferred catalysts because of their high activity and compatibility with the organosiloxane reactants. These complexes are described in U.S. Patent No. 3,419,593. Complexes with low molecular weight organosiloxanes wherein the silicon-bonded hydrocarbon radicals are vinyl and either methyl or 3,3,3-trifluoropropyl are particularly preferred because of their ability to catalyze a rapid curing of the elastomer at temperatures of at least 70°C. The platinum-containing hydrosilation catalyst can be present in an amount equivalent to as little as one part by weight of platinum per one million parts (ppm) of curable composition. Catalyst concentrations equivalent to from 5 to 50 parts of platinum per million of curable composition are preferred to achieve a practical curing rate. Higher concentrations of platinum provide only marginal improvements in curing rate, and are therefore economically unattractive, particularly when the preferred catalysts are used. Mixtures of the aforementioned ingredients A, B and C may begin to cure at ambient temperature. To obtain a longer working time or "pot life", the activity of the catalyst under ambient conditions can be retarded or suppressed by addition of a suitable inhibitor. Known platinum catalyst inhibitors include the acetylenic compounds disclosed in U.S. Patent No. 3,445,420. Acetylenic alcohols such as 2-methyl-3-butyn-2-ol constitute a preferred class of inhibitors that will suppress the activity of a platinum-containing catalyst at 25°C. Compositions containing these catalysts typically require heating at temperatures in excess of 70°C. to cure at a practical rate. If it desired to increase the pot life of a curable composition under ambient conditions, this can be accomplished using an olefinically substituted siloxane of the type described in U.S. Patent No. 3,989,667. Cyclic methylvinylsiloxanes are preferred. Inhibitor concentrations as low as one mole of inhibitor per mole of platinum will in some instances impart satisfactory storage stability and cure rate. In other instances, inhibitor concentrations of up to 500 or more moles of inhibitor per mole of platinum are required. The optimum concentration for a given inhibitor in a given composition can readily be determined by routine experimentation. Some compositions may begin to cure under ambient conditions even when an inhibitor is present. One way to ensure storage stability is to package the composition in two or more containers and place the hydrosilation catalyst and the organohydrogensiloxane in separate containers. The contents of the containers are combined when it is desired to cure the composition. If it is desired to prepare one-part organosiloxane compositions having virtually indefinite storage stability at temperatures of up to 50°C., this can be achieved by microencapsulating the platinum-containing hydrosilation catalyst in a thermoplastic or thermosetting polymer. Curable organosiloxane compositions containing micro-encapsulated hydrosilation catalysts are described in U.S. Patent No. 4,766,176 and U.S. Patent No. 5,017,654. The consistency of the present compositions can vary from a flowable liquid to a semi-solid paste to a high consistency gum that will flow only under high shear. In addition to the aforementioned ingredients the compositions can also contain other additives including reinforcing and non-reinforcing fillers, treating agents for these fillers, pigments, processing aids, stabilizers and flame retardants. The following examples describe preferred embodiments of the curable compositions. Unless otherwise specified, all parts and percentages in the examples are by weight and all viscosities were measured at 25°C. Example 1 This example demonstrates the ability of the present compositions to develop cohesive bonding to substrates under ambient conditions. A curable composition of this invention was prepared by blending the following ingredients to homogeneity: 76 parts of a dimethylvinylsiloxy terminated polydimethylsiloxane having a viscosity of about 2.1 Pa·s at 25°C.; 24.7 parts of a fume silica having a nominal surface area of 250 m 2 /g that had been treated with 1.9 parts of water and 6.1 parts of hexamethyldisilazane; 1.2 parts of a trimethylsiloxy-terminated polyorganosiloxane copolymer having an average of five methylhydrogensiloxane units and three dimethylsiloxane units per molecule with a silicon-bonded hydrogen atom content in the range of from 0.7 to 0.8 weight percent; 1 part of 5-hexenyltrimethoxysilane (HTMS); 0.9 part of a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane that had been diluted with a liquid dimethylvinylsiloxy terminated polydimethylsiloxane in an amount sufficient to achieve a platinum content of 0.7 weight percent; 0.5 part tetrabutyltitanate (TBT); and 0.2 part of cyclic methylvinylsiloxane. The resultant composition of this invention was coated on an aluminum sheet and allowed to remain for 3 days under ambient conditions. The cured elastomer that formed during this period was cohesively bonded to the aluminum panel. For comparative purposes, a curable organosiloxane composition outside the scope of the present invention was prepared using the same types and amounts of ingredients as the composition described in the preceding section of this example, with the exception that the 5-hexenyltrimethoxysilane was replaced with an equal weight of vinyltrimethoxysilane. A coating of the resultant composition on an aluminum sheet did not cure after 3 days under ambient conditions. Example 2 This example describes a preferred curable composition of this invention and demonstrates its adhesion to aluminum and glass substrates following curing at a range of temperatures from 25 to 137°C. Curable compositions of this invention were prepared by blending the following ingredients to homogeneity: 49 parts of a dimethylvinylsiloxy terminated polydimethylsiloxane having a viscosity of about 2.1 Pa·s at 25°C., 46.5 parts of finely divided quartz, 3 parts of a trimethylsiloxy-terminated polydiorganosiloxane containing an average of five methylhydrogensiloxane units and three dimethylsiloxane units per molecule with a silicon-bonded hydrogen atom content in the range from about 0.7 to 0.8 weight percent, 0.1 part of a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane that had been diluted with a liquid dimethylvinylsiloxy terminated polydimethylsiloxane in an amount sufficient to achieve a platinum content of 0.7 weight percent, 0.06 part of cyclic methylvinylsiloxanes as a platinum catalyst inhibitor, 0.45 part of zinc oxide, 0.25 part of carbon black, 0 or 1.0 part of HTMS, and 0 or 0.5 part of TBT. The molar ratio of silicon-bonded hydrogen atoms to vinyl radicals was 2.77. The resultant compositions were coated as a 0.25 to 1.5 mm thick layer on aluminum and glass panels. The following conditions were used to cure the compositions: 16 hours at 25°C., 1 hour at 50°C., 15 minutes at 80°C. or 15 minutes at 137°C. Following curing, the coated substrates were allowed to remain at 25°C. for 7 days. The adhesion of the cured composition to the substrate was then determined by lifting a section of the composition from the substrate using a knife blade, manually grasping the lifted section and pulling the remainder of the coating away from the substrate. If more than half of the area of the substrate had cured composition still adhering to it, the failure was rated as "cohesive" (C). Otherwise it was rated "adhesive" (A). Table 1 contains a ranking of these samples. The rankings for cohesive failure are based on the percentage of the substrate covered with cured material following removal of the coating. Samples exhibiting adhesive failure are not listed unless all of the samples exhibited this type of failure. Glass Sample HTMS TBT Cure Temp(°C.) Failure 1 Yes No 25 C 2c No No C Ranking: 1 > 2c 3 Yes No 50 C 4 Yes No 80 C 5c No No C Ranking: 4 > 5c 6 Yes No 137 C 7 Yes Yes C 8c No No C Ranking: 6 > 7 > 8c Aluminum Sample HTMS TBT Cure Temp(°C.) 9 Yes No 25 A 10 Yes Yes A 11c No No A 12c No Yes A Ranking: 9, 11c > 10, 12c All samples exhibited adhesive failure 50 13 Yes No 80 A 14 Yes Yes A 15c No No A 16c No Yes A Ranking: 13 > 14 > 15c, 16c 17 Yes No 137 C 18 Yes Yes C Ranking: 17 > 18 Example 4 This example demonstrates the ability of ingredient D of this invention to be used in combination with other adhesion promoters or primer compositions without cure inhibition being a problem. A two-part curable composition of this invention was prepared by blending the following ingredients to homogeneity: Part A 52 parts of a dimethylvinylsiloxy-terminated polydimethylsiloxane having a viscosity of 0.4 Pa·s at 25°C.; 46 parts of finely divided quartz exhibiting an average particle size of 5 micrometers; 2 parts 3-glycidoxypropyltrimethoxysilane; 1 part of HTMS; 0.9 part of zinc oxide; 0.5 part of carbon black; and 0.2 part of a reaction product of hexachloroplatinic acid and sym-tetramethyldivinyldisiloxane that had been diluted with a liquid dimethylvinylsiloxy terminated polydimethylsiloxane in an amount sufficient to achieve a platinum content of 0.7 weight percent. Part B 4.7 parts of the finely divided quartz present in part A; 4.6 parts of the dimethylvinylsiloxy-terminated polydimethylsiloxane present in part A; 0.6 part of a trimethylsiloxy-terminated organosiloxane copolymer containing an average of five methylhydrogensiloxane units and three dimethylsiloxane units with a silicon-bonded hydrogen atom content in the range from 0.7 to 0.8 weight percent; 0.01 part of cyclic methylvinylsiloxanes; and 0.01 part of aluminum acetylacetonate. For purposes of comparison a two-part composition outside the scope of the present invention was prepared using the same types and amounts of ingredients described in the preceding section of this example, with the exception that the hexenyltrimethoxysilane was replaced with an equal weight of vinyltrimethoxysilane. Parts A and B of both compositions were aged for 15 days at 60°C. Two curable compositions were prepared by combining the two parts of each composition and blending the resultant mixture to homogeneity. The compositions were then coated on sheets of a polysulfone resin and the coated substrates were heated at 150°C. for 15 minutes. The composition of this invention cured to an elastomer that exhibited cohesive failure when sufficient force was applied to pull the elastomer away from the substrate. The comparative composition containing the vinyltrimethoxysilane did not cure during the heating cycle.

Claims: A curable organosiloxane composition comprising: A. a polyorganosiloxane containing at least two alkenyl radicals per molecule; B. an organohydrogensiloxane containing an average of at least three silicon-bonded hydrogen atoms per molecule and the silicon-bonded hydrogen atoms in component B being present in a stoichiometric excess relative to the alkenyl radicals in component A; C. a platinum-containing hydrosilation catalyst present in said composition in an amount within the range equivalent to a range of from 1 to 50 parts of platinum per 1 million parts of said curable organosiloxane composition; D. an adhesion promoter selected from silanes represented by the general formula R 2 SiR 3 n (OR 1 ) 3-n , where R 1 and R 3 represent identical or different alkyl radicals, R 2 represents an alkenyl radical having at least 5 carbon atoms and n is 0 or 1, in a concentration of from 0.01 to 10 weight percent based on the total weight of the curable composition. A composition according to claim 1, wherein the molar ratio of said silicon-bonded hydrogen atoms in said component B to said alkenyl radicals in said component A is in the range of from 2:1 to 4:1. A composition according to claim 2, wherein said molar ratio of said silicon-bonded hydrogen atoms in said component B to said alkenyl radicals in said component A is in the range of from 2.5:1 to 2.8:1. A composition according to any of claims 1 to 3, wherein said adhesion promoter (D) is present in said composition in a concentration of from 0.1 to 5 weight percent based on the total weight of the curable composition. A composition according to any of claims 1-4, wherein, in said adhesion promoter (D), n is 0, R 2 is CH 2 =CH(CH 2 ) p -, and p is an integer with a value of at least 3, and the silicon-bonded organic groups present in said polyorganosiloxane (A) and said organohydrogensiloxane (B) are monovalent unsubstituted or substituted hydrocarbon radicals containing from 1 to 20 carbon atoms. A composition according to claim 5, wherein, in said adhesion promoter (B), R 1 contains from 1 to 4 carbon atoms, and said monovalent hydrocarbon radicals in said polyorganosiloxane (A) and said organohydrogensiloxane (B) are C 1-4 alkyl, phenyl or 3,3,3-trifluoropropyl. A composition according to claim 6, wherein at least a portion of said silicon-bonded organic groups are methyl and any remainder are phenyl or 3,3,3-trifluoropropyl. A composition according to to any of claims 1-7, wherein said component (B) is a resinous organosiloxane copolymer containing triorganosiloxy and SiO 4/2 units, where the silicon-bonded organic groups are monovalent hydrocarbon radicals. A composition according to to any of claims 1-8, wherein said composition contains an hydrolysis-condensation catalyst in a concentration of from 0.1 to 1 weight percent based on the weight of said curable organosiloxane composition. A composition according to claim 9, wherein said hydrolysis-condensation catalyst is selected from tetraalkyl titanates and chelated compounds of aluminum, copper and titanium.

Inventors: LARSON KENT ROBERT, LARSON, KENT ROBERT
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1993
Main classification: C08L83
IPC codes: C09D183, C08L83, C08K5