ADDITION POLYMERIZATION CATALYSTS COMPRISING REDUCED OXIDATION STATE METAL COMPLEXES

Abstract: Addition polymerization catalysts comprising a metal complex containing a Group 4 metal in the +3 oxidation state, a delocalized pi -bonding moiety, and at least one stabilizing ligand, optionally in combination with an activating cocatalyst.

Description: ADDITION POLYMERIZATION CATALYSTS COMPRISING REDUCED OXIDATION STATE METAL COMPLEXES This invention relates to addition polymerization catalysts comprising certain stabilized, reduced metal complexes. In one embodiment such catalysts additionally employ an activating cocatalyst. In another embodiment such catalysts may be employed with or without an activating cocatalyst. Finally the invention relates to an improved method for preparing the stabilized reduced metal complexes. The compositions are especially useful as catalysts for the polymerization of olefins such as ethylene for the preparation of polymers having utility as molding resins and in the formation of foamed products having cushioning and insulating applications and films that are useful as protective wrappings. In U.S. Serial No. 545,403, filed July 3, 1990 (equivalent to EP-A-0416,845) there are disclosed and claimed certain monocyclopentadienyl metal complexes having utility as homogeneous olefin polymerization catalysts. In US-A-5,064,802 (equivalent to EP-A-0418,044), cation ic monocyclopentadienyl metal complexes with salts of Bronsted acids containing a non-coordinating compatible anion are disclosed and claimed. In U.S. Serial No. 547,718, also filed on July 3, 1990 (EP-A-0468,651), an oxidative activation technique for preparing such cationic catalysts is disclosed and claimed. In US-A-4,057,565 there are disclosed Ti, Zr, or Hf derivatives of 2-dialkylamino- benzyl or 2-dialkylaminomethylphenyl all in the + 4 oxidation state which are useful as components of catalysts for olefin polymerization. In J. Am. Chem. Soc. 100, 8068-8073 (1978) there is mentioned the synthesis and characterization of Ti( + 3) complexes containing cyclopentadienyi groups and 2-dialkylami no- benzyl or 2-dialkylaminomethylphenyl groups. No mention of utility as addition polymerization catalysts is given. In US patent 4,870,042, catalysts for olefin polymerizations comprising a pyrazolyl borate complex of titanium or zirconium compounds including titanium trichloride (Example 4) are disclosed. In Orqanometallics, 10, 3227-3237 (1991) certain titanium + 3 complexes containing cyclopentadienyi groups and alkyl groups are mentioned. On page 3236, the reference states: "So far no well-defined neutral titanium-based molecular system with established activity for catalytic olefin polymerization has been described... Apparently, the tervalent Cp * 2 Ti system cannot induce sufficient positive charge atthe β-carbon atom of an incoming ethylene molecule to reach the polar transition state for migratory insertion." In Journal of Orqanometallic Chemistry, 334 ( 1987) C1-C4, η 3 -allyl(bis-η 5 - cyclopentadienyl)titanium (III) activated with dimethylaluminum chloride was found to create a coordinated species Cp 2 Ti (allyl) - (CH 3 ) 2 AICI which was found to polymerize ethylene to a small extent. Use of stronger Lewis acids so as to cause ligand abstraction thereby destroying the requisite carbon-titanium bond was to be avoided according to the reference. Figure 1 is an electron spin resonance spectrogram of the product obtained in preparation ii) of Examples 1-58. Figure 2 is an electron spin resonance spectrogram of the product obtained in Example 59. Figure 3 is an electron spin resonance spectrogram of the product obtained in Example 60. According to the present invention in its most generic description, there is provided an addition polymerization catalyst comprising: (i) a metal complex corresponding to the formula: Cp a (ZY)bML c , wherein: a is 1 or 2; b is O oM ; cis 1 or 2; the sum of a, b and c is 3; Cp independently each occurrence is a cyclopentadienyi group π-bound to M, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbylmetalloid or halohydrocarbylmetalloid substituted derivative of said cyclopentadienyi group, said Cp containing up to 50 nonhydrogen atoms, and, when a is 2, optionally both Cp groups may be joined together by a bridging group; L independently each occurrence is hydride, halo, ora monovalentanionic ligand selected from covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, and sulfido groups optionally being further substituted with amine, phosphine, ether, and thioether; mixtures thereof; said ligand having up to 50 nonhydrogen atoms, with the proviso that in at least one occurrence L is a stabilizing ligand comprising an amine, phosphine, ether or thioether functionality able to form a coord inate-cova lent bond or chelating bond with M, or except when a is 1, comprising an ethylenic unsaturation able to form an η3 bond with M; M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation ^a 1 --; Y is a linking group comprising nitrogen, phosphorus, oxygen or sulfur covalently bonded to M and Z through said nitrogen, phosphorus, oxygen or sulfur atom; Z is a divalent moiety comprising oxygen, nitrogen, phosphorous, boron, or a member of Group 14 of the Periodic Table of the Elements, said moiety having up to 30 nonhydrogen atoms; the ligand moiety consisting of -Cp-Z-Y- being dianionic and having the ionic charges residing formally on Cp and Y; and, when b is 0 and optional ly when b is 1 , (ii) an activating cocatalyst. In accordance with one embodiment of the above generic description of the invention there is provided an addition polymerization catalyst comprising in combination: (i) a metal complex, Ai, corresponding to the formula: (la) Cp' 2 ML', wherein: Cp' independently each occurrence is a cyclopentadienyi group π-bound to M, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbyimetalloid or halohydrocarbylmetalloid substituted derivative of said cyclopentadienyi group, said Cp' containing up to 50 nonhydrogen atoms, and optionally both Cp groups may be joined together by a bridging group; M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation state; L' is a monovalent anionic stabilizing ligand selected from the group consisting of: covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, sulfido groups and mixtures thereof, said group being further substituted with an amine, phosphine, ether, or thioether containing substituent able to form a coordinate-covalent bond or chelating bond with M; said ligand having up to 50 nonhydrogen atoms; and (ii) an activating cocatalyst. Preferably in accordance with the present invention the ratio of metal complex to activating cocatalyst is from 1 :0.01 to 1 : 10 6 . In a further embodiment there is provided an addition polymerization catalyst comprising in combination: (i) a metal complex, A 2 , corresponding to the formula (lb) Cp"ML" 2 , wherein: Cp" is a cyclopentadienyi group π-bonded to M, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbyimetalloid, or halohydrocarbylmetalloid substituted derivative thereof, said Cp" containing up to 50 nonhydrogen atoms; M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation state; L" independently each occurrence is hydride, halo, or a monovalent anionic ligand selected from the group consisting of covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, and sulfido groups; mixtures thereof; and amine, phosphine, ether, and thioether derivatives of the foregoing, said ligand having up to 50 nonhydrogen atoms, with the proviso that in at least one occurrence L" is a stabilizing ligand comprising an amine, phosphine, ether or thioether functionality able to form a coordinate-covalent bond or chelating bond with M, or comprising an ethylenic unsaturation able to form an η3 bond with M; and (ii) an activating cocatalyst. Preferably the activating cocatalyst is present in an amount to provide a ratio of metal complex to activating cocatalyst from 1 :0.01 to 1 :10 6 . In a still further embodiment of the present invention there is provided a metal complex, A 3 , corresponding to the formula: do) Cp • • • _ vX L 1 ' ' wherein: M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation state; Cp'" is a cyclopentadienyi group, or a hydrocarbyl, silyl, halo, halohydrocarbyl, or hydrocarbyimetalloid substituted derivative thereof, said Cp'" containing upto 50 nonhydrogen atoms; Z is a divalent moiety comprising oxygen, nitrogen, phosphorous, boron, or a member of Group 1 of the Periodic Table of the Elements said moiety having up to 30 nonhydrogen atoms; Y is a linking group comprising nitrogen, phosphorus, oxygen or sulfur covalently bonded to M and Z through said nitrogen, phosphorus, oxygen or sulfur atom, the ligand moiety consisting of -Cp'"-Z-Y- being dianionic and having the ionic charges residing formally on Cp'" and Y; and L'" is a monovalent stabilizing ligand selected from the group consisting of L' and C3- 1 5 hydrocarbyl groups comprising an ethylenic unsaturation able to form an ~ 3 bond with M. The above complexes, A3, are suitable for use in polymerization of addition polymerizable monomers alone or optionally in the presence of an activating cocatalyst. In the latter event there is provided an addition polymerization catalyst comprising: (i) the complex, A3, and (ii) an activating cocatalyst. The activating cocatalyst is preferably used in an amount to provide a ratio of metal complex to activating cocatalyst from 1 :0.01 to 1 : 10 6 . It is believed, without agreeing to be bound by such belief, that the metal complexes Ai, A 2 , and A3 when combined with the activating cocatalyst are converted into cationic metal complexes wherein the metal is in the + 3 oxidation state. Evidence for this belief is established by electron spin resonance spectroscopy (ESR) and by the fact that solutions of the metal complexes in combination with the activating cocatalyst, especially tris(perfluorophenyl)boron are conductive in cyclic voltammetry analysis without added supporting electrolyte, whereas the complex alone is not conductive under the same conditions. The presence of the above identified stabilizing ligand in the complexes of the invention results in improved complex stability and greatly improved usefulness in the formation of catalysts. The catalysts formed from these complexes by combination with the activating cocatalyst additionally possess higher activity and are more efficient addition polymerization catalysts than catalysts formed from corresponding complexes lacking such stabilizing ligand group. The metal complexes, Ai, may be prepared by a process comprising contacting a Group 4 metal complex corresponding to the formula: (lla) Cp' 2 M * XL' wherein Cp' and L' are as previously defined, and M* is a metal of Group 4 of the Periodic Table of the Elements in the + 4 oxidation state; and X is halide or C._ 10 hydrocarbyloxide, with a reducing agent under reducing conditions to form the Group 4 metal complex. The metal complexes, A 2 , may be prepared by a process comprising contacting a Group 4 metal complex corresponding to the formula: (lib) Cp"M*XL" 2 wherein Cp" and L" are as previously defined, and M * is a metal of Group 4 of the Periodic Table of the Elements in the * 4 oxidation state; and X is halide or C 1 10 hydrocarbyloxide, with a reducing agent under reducing conditions to form the Group 4 metal complex. Finally, the metal complexes, A3, may be prepared by a process comprising contacting a Group 4 metal complex corresponding to the formula: He Cp ' "_- M * / L - ' ' wherein Cp'", Z, Y, M * , X and L'" are as previously defined, with a reducing agent under reducing conditions to form the Group 4 metal complex. There are also provided polymerization processes comprising contacting an addition polymerizable monomer or monomers with the foregoing catalysts under polymerization conditions and recovering the resulting polymer. All reference to the Periodic Table of the Elements herein shall refertothe Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 1989. Also, any reference to a Group or Groups shall be to the Group or Groups as reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. By the term "stabilizing ligand" is meantthatthe ligand group stabilizes the metal complexthrough either: 1) a nitrogen, phosphorus, oxygen or sulfur chelating bond, or 2) an η3 bond with a resonant, delocalized ir-electronic structure. Examples of stabilizing ligands of group 1) for use according to the present invention include alkyl, cycloalkyl, aryl, silyl, amido or phosphido ligands substituted with one or more aliphatic or aromatic ether-, thioether-, amine- or phosphine- functional groups, especially such amine or phosphine groups that are tertiary substituted, said stabilizing ligand having from 3 to 30 nonhydrogen atoms. Most preferred group 1) stabilizing ligands are 2-dϊalkyiammobenzyl or 2-(dialkylaminomethyl)phenyi groups containing from 1 to 4 carbons in the alkyl groups. Examples of stabilizing ligands of group 2) for use according to the present invention, include linear C3-- 5 hydrocarbyl groups containing ethylenic unsaturation, such as allyl, 1-methylallyl, 2-methylallyl, 1J-dimethyIallyl, 1,2,3-trimethylallyl. 1-phenyl-3-benzylallyl or 1J-diphenyI-3-(diphenylmethyl)aIlyl groups. Preferred substituents of the groups Cp, Cp" and Cp'" are hydrocarbyl (including hydrocarbylene) and halosubstituted hydrocarbyl groups, said groups having from 1 to 30 carbons, and C._ 30 hydrocarbyl or halohydrocarbyl substituted metalloid radicals wherein the metalloid is an element from Group 14 of the Periodic Table of the Elements. Exemplary hydrocarbyl radicals include straightand branched alkyl radicals, cyclic aliphatic hydrocarbon radicals, alkyl-substituted cyclic aliphatic hydrocarbon radicals, aromatic radicals and alkyl-substituted aromatic radicals. Preferred are methyl, ethyl, butyl and phenyl radicals. Exemplary organometailoid radicals include straightand branched chain silyl radicals, alkyl-substituted silyl radicals, germyl radicals and divalent derivatives of the foregoing. Preferred are trimethylsilyl, triethylsilyl, ethyl dimethyl silyl, methyldiethylsilyl, dimethyl-t- butylsilyl, triphenylsilyi, triphenytgermyl, and trimethyf germyl radicals. More particularly, suitable cyclopentadienyi or substituted cyclopentadienyi groups in complexes A, are illustrated by the formula: wherein: R' is hydrogen, or a group selected from silyl, hydrocarbyl, and combinations thereof having up to 30 carbon or silicon atoms, or two R' groups together form a divalent derivative of such group. Preferably, R' independently each occurrence is hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, (including where appropriate all isomers), cyclopentyl, cyclohexyl, norbornyl, benzyl, or phenyl or two R' groups are linked togetherthereby forming an indenyl, tetrahydroindenyl, fluorenyl, tetrahydrofluorenyl, or octahydrofluorenyl group in place of the cyclopentadienyi group. Exemplary metal complexes of formula A^ are: biscyclopentadienyl 2-(N,N- dimethylamino)benzyl titanium, bis(methylcyclopentadienyl) 2-(N,N-dimethylamino)benzyl titanium, bis(t-butylcyclopentadienyl) 2-((N,N-dimethylamino)methyl)phenyl titanium, bis(pentamethylcyclopentadienyl) 2-(N,N-dimethylamino)benzyl titanium, bis(indenyl)( 2-N,N- dimethyiamino)benzyl titanium, bis(fluorenyl) (2-N,N-dimethylamino)benzyl titanium, and corresponding zirconium and hafnium derivatives. Additional bis-cyclopentadienyl compounds of formula A. include those containing a bridging group linking the cyclopentadienyi groups. Preferred bridging groups are those corresponding to the formula (ER" 2 ) χ wherein E is silicon or carbon, R", independently each occurrence is hydrogen or a group selected from silyl, hydrocarbyl and combinations thereof, said R" having up to 30 carbon or silicon atoms, and x is 1 to 8. Preferably R" independently each occurrence is methyl, benzyl, tert-butyl, or phenyl. Examples of the foregoing bridged cyclopentadienyi group containing complexes are compounds corresponding to the formula: wherein: M, L' f E, R' R" and x are as previously defined. Such bridged structures are especially suited for the preparation of polymers having stereoregular molecular structure. In such capacity it is preferred that the complex be nonsymmetrical or possess a chiral, stereorigid structure. Examples of the first type are compounds possessing different delocalized π-bonded systems, such as one cyclopentadienyi group and one indenyl group. Similar systems based on Ti(IV) or Zr(IV) were disclosed for preparation of syndiotactic olefin polymers in Ewen, et al., J.Am. Chem. Soc. 1 10, 6255-6256 (1980). Examples of chiral structures include bis-indenyl complexes. Similar systems based on Ti(IV) orZr(IV) were disclosed for preparation of isotactic olefin polymers in Wild eta!., J. Orqanomet. Chem.232, 233-47, (1982). Exemplary bridged cyclopentadienyi complexes of formula la are: (dimethylsilyl- bis-cyclopentadienyl) titanium 2-(N,N-dimethylamino)benzyl, (dimethylsilyl-bis- cyclopentadϊenyl) titanium 2-((N,N-dimethylamino)methyI)phenyl r (dimethylsiyl-bis-t- butylcyciopentadienyl) titanium 2-(N,N-dimethylamino)benzyl, (dimethylsiiyl-bis- tetramethylcyclopentadienyl) titanium 2-(N,N-dimethylamino)benzyl, (dimethylsilyl-bis- indenyl) titanium 2-(N,N-dimethylamino)benzyl, (isopropylidene-cyclopentadienyl-f luorenyl) titanium 2-(N,N-dimethyiamino)benzylJ2,2'-biphenyldiylbis(3,4-dimethyl-1 - cycIopentadienyl)]titanium 2-(N,N-dϊmethylamino)benzyl, [6,6-dimethyl-2,2'biphenylbϊs(3,4- dimethyl-1-cyclopentadienyl)] titanium 2-(N,N-dimethylamino)benzyl, and corresponding zirconium and hafnium complexes. Exemplary complexes of formula A 2 include cyclopentadienyi titanium allyl chloride, t-butylcyclopentadienyl titanium allyl chloride, pentamethylcyclopentadienyl titanium allyl chloride, pentamethylcy iopentadienyl titanium allyl methoxide, n-butylcyclopentadienyl titanium allyl is ropoxide, pentamethylcyclopentadienyl titanium allyl phenoxide, cyclopentadienyi titanium (2-methyl allyl) chloride, ethylcyciopentadienyl titanium (2-methylallyl) ethoxide, cyclopentadienyi titanium 2-(N,N-dimethylamino)benzyl chloride, pentamethylcyclopentadienyl titanium 2-(N,N-dimethylamino)benzyl bromide, cyclopentadienyi titanium 2-(N,N-dimethylamino)benzyl methoxide, n-butylcyclopentadienyl titanium 2-((N,N-dimethyiamino)methyl)phenyl isopropoxide, cyclopentadienyi titanium allyl dimethylamide, n-butyicyclopentadienyl titanium allyl dimethylamide, t-butyicyclopentadienyl titanium allyl diethylamide, cyclopentadienyi titanium diallyl, cyclopentadienyi titanium 2-(methylallyl) dimethylamide, cyclopentadienyi titanium (2-methylallyl) (di-t-butylamide), cyclopentadienyi titanium 2-(N,N-dimethylamino)benzyl dimethylamide, pentamethyl¬ cyclopentadienyl titanium 2-(N,N-dimethylamino)benzyl dimethylamide, methylcyclopentadienyl titanium methyl 2-(N,N-dimethylaminobenzyl), methylcyclopentadienyl titanium benzyl 2-(N,N-dimethylamino)benzyl, methylcyclopentadienyl titanium trimethylsilyl methyl 2-(N,N-dimethylamino)benzyl, pentamethylcyclopentadienyl titanium methyl 2-(N,N-dimethylaminobenzyi, pentamethyl¬ cyclopentadienyl titanium trimethylsilylmethyl 2-(N,N-dimethylamino)benzyl, and corresponding zirconium and hafnium complexes. Illustrative cyclic complexes, A 3 , that may be employed in the practice of the present invention include: (tert-butylamido)dimethyl(tetramethyl-η5- C ydopentadienyl)silane 2-(N,N-dimethylamino)benzyl titanium, (phenylamido)dimethyl(tetramethyl-η 5 -cyclo- pentadienyl)silane 2-(N,N-dimethylamino)benzyl titanium, (tert-butylamido)(tetramethyl-η5. cyclopentadienyl)-1,2-ethanediyl allyl titanium, (tert-butylamido)(tetramethyl-η 5 - cyciopentadienyl)-1 ,2-ethanediyl 2-(dimethylamino)benzyltitanium, (methylamido)(tetra- methyl-η5-cyclopentadienyl)-1,2-ethanediyi allyl titanium, (tert-butylamido)dibenzyl- (tetramethyl-η5-cyclopentadienyl)silane 2-(N,N-dimethylamino)benzyl titanium, (benzyl- amido)dimethyl(η . 5-cyclopentadienyl)silane 2-((N,N-dimethylamino)methyl)phenyl titanium, (phenylphosphido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane 2-(dimethylamino)benzyl titanium, (tert-butylamido)-dimethyl(tetramethyl-η5-cyclopentadienyl)silane allyl titanium, (methylamido)cyclotetramethylene(- 5 -octahydrofluorenyl)silane 2-(N,N- dimethylamino)benzyl titaniumJmethyiamido)cyclotetramethyiene(η5-octa- hydrofluorenyl)siiane 2-(N,N-dimethylamino)benzyl titanium, and corresponding zirconium or hafnium complexes. Preferred cyclic complexes, A 3 , are amidosiiane- or amidoalkanediyl- compounds corresponding to the formula: wherein: M, L"', E, R', and R" are as previously defined; Y' is nitrogen; R'" is a group selected from silyl, hydrocarbyl and combinations thereof, said group or combination having up to 30 carbon or silicon atoms; and m is 1 or 2. Preferably R'" is methyl, ethyl, propyl, butyl, pentyl, hexyl, (including where appropriate all isomers), cyclopentyl, cyclohexyl, norbornyl, benzyl, or phenyl. In the most preferred embodiment -(ER" 2 ) m Y'R'"- is an amidosilane or amidoalkane group of u to 30 nonhydrogen atoms, especially, (tert-butyl- amido)(dϊmethyIsilyl), (methylamido)(dimethylsilyl),or (tert-butylamido)-1-ethane-2-yl. Other complexes which are useful in the catalyst compositions of this invention will be apparentto those skilled in the art. Highly preferably in complexes A^ M is titanium and L' is 2-dimethylaminobenzyl. Highly preferably in complexes A 2 , M is titanium and L" is 2-dimethylaminobenzyl or allyl. Highly preferably in complexes A3, M is titanium and L'" is 2-dimethyiaminobenzyI or allyl. By the term "reducing agent" herein is meant a metal or compound which, under reducing conditions causes M to be reduced from the + 4 oxidation state to the + 3 oxidation stare. Examples of suitable metal reducing agents are alkali metals, alkaline earth metals, lead and zinc, alloys of alkali metals or alkaline earth metals such as sodium/mercury amalgam and sodium/potassium alloy. Examples of suitable reducing agent compounds are sodium naphthalenide, potassium graphite, and Grignard reagents. Most preferred reducing agents are the alkali metals or alkaline earth metals, especially magnesium. Bythe term "reducing conditions" is meant the use of diluents and temperatures that allow the desired reduction to take place. Preferred temperatures are from 0°C to 200°C, more preferably from 5°Cto 120°C and most preferably from 10°Cto 50°C. Preferred diluents are polar solvents, more preferably C,_ 5 aliphatic ethers, most preferably tetrahydrofuran, 1,2-dimethoxyethane or diethyl ether. The term "activating cocatalyst" as used herein refers to a secondary component that renders the metal complex catalytically effective or improves the catalytic effectiveness of the metal complex as an addition polymerization catalyst. Examples of the activating cocatalysts for use herein include aluminum compounds containing an Al-O bond such as the alkylalumoxanes, especially methylalumoxane and isobutyl modified methylalumoxane; aluminum alkyls; aluminum halides; alkylaluminum halides; Lewis acids other than any of the foregoing list; and mixtures of the foregoing. Preferred Lewis acids are those compounds corresponding to the formula: R"" 3 B, wherein R"" independently each occurrence is selected from hydrogen, silyl, hydrocarbyl, halohydrocarbyl, alkoxide, aryloxide, amide or combinations thereof, said R"" having up to 30 nonhydrogen atoms. It is to be appreciated by those skilled in the art, that the above formula for the preferred Lewis acids represents an empirical formula, and that many Lewis acids exist as dinners or higher oligomers in solution or in the solid state. Other Lewis acids which are useful in the catalyst compositions of this invention will be apparent to those skilled in the art. Preferred activating cocatalysts include trimethylaluminum, triisobutylaluminum, methylalumoxane, ethylalumoxane, chlorodiethylaluminum, dichloroethylaiuminum, triethylboron, trimethylboron, triphenylboron and halogenated, especially fluorinated, tri phenyl boron compounds. Most highly preferred activating cocatalysts include triethylaluminum, methylalumoxane, and fluoro-substituted triaryl borons such astris(4-fluorophenyl)boron, tris(2,4-difluorophenylboron), tris(3,5-bis(trifluoromethyl)phenyl)boron, tris(penta- fluorophenyl)boron, pentafluorophenyldiphenylboron, and bis(pentafluoro- phenyl)phenylboron. Such fluoro- substituted triaryl boranes may be readily synthesized according to techniques such as those disclosed in Marks, et al. J. Am. Chem. Soc, 1 13, 3623- 3625 (1991). A neutral Lewis base may additionally be present in combination with the complexes and catalysts of the invention. Suitable neutral Lewis bases include, for example, organic compounds containing oxygen, nitrogen, phosphorus or sulfur, or olefins. More specifically, examples of suitable electron donating compounds include organic amines, amides, ketones, nitriles, phosphines, phosphorylamides, esters, ethers (including cyclic ethers such as furans), thioethers and thioesters. Preferred are such compounds containing up to 20 nonhydrogen atoms. A highly preferred electron donating agent istetrahydrofuran (THF). It has been previously reported that Lewis bases such as THF have a severe degrading effect on the catalytic activity of cyclopentadienyi complexes of Group 4 metals in the + 4 oxidation state. Jordan, et al,. J. Am. Chem. Soc, 108, 7410-741 1 (1986) at 7410, reported that "Addition of THF or other donor ligands slows the polymerization rate dramatically and in THF or CH 3 CN solvents no activity is observed" . Similarly, Bochmann et al., Polyhedron, 8 (13-14), 1838-1843 (1989) reported that bis(pentamethylcyclopentadienyl)titan- ium(IV) methyl tetraphenylborate prepared in THF solvent was inactive for ethylene polymerization. Surprisingly, the presence of a neutral Lewis base does not necessarily adversely affect the catalytic activity of the metal complexes of the present invention, particularly the complexes of formula A3. The catalyst can be formed by combining the activating cocatalyst (where required) with the complex, with orwithouta neutral Lewis base, optionally in the presence of a diluent. Complexes that need no activating cocatalyst may be used to polymerize addition polymerizable monomers without further additives or in combination with the above neutral Lewis base and optionally in the presence of a diluent. The preparation may be conducted in the presence of one or more addition polymerizable monomers, if desired. Preferably, the catalysts are prepared at a temperature within the range from -100°C to 300°C, preferably 0 G C to 250°C, and most preferably 0°C to 100°C. Suitable solvents include straight and branched- chain hydrocarbons such as isobutane, butane, pentane, hexane, heptane, octane, and mixtures thereof; cyclic and alicydic hydrocarbons such as cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane; perfluorinated hydrocarbons such as perfluorinated -4-10 a "*- anes »" ar| d aromatic and alkyl-substituted aromatic compounds such as benzene, toluene and xylene. Suitable solvents also include liquid olefins which may act as monomers or comonomers including ethylene, propylene, butadiene, cyclopentene, 1-hexene r 3-methyl-1- pentene,4-methyl-1-pentene, 1,4-hexadiene, 1-octene, 1-decene, styrene, dϊvinylbenzene, 4-vinylcyclohexene, allyl benzene and vinyltoluene (including all isomers alone or in admixture). Preferred solvents are aliphatic hydrocarbons especially C 5 -C 10 alkanes or cycloalkanes and mixtures thereof. Such a mixture is available commercially under the trade designation lsopar™E, available from Exxon Chemicals. If no cocatalyst is necessary, the complex itself is contacted with the addition polymerizable monomer. "Addition polymerizable monomers" usefully polymerized according to the present invention include, for example, ethylenicallyunsaturated monomers, cyclic olefins, acetylenic compounds, conjugated or nonconjugated dienes and polyenes. Specific examples include C 2 20 olefins, styrene, halo- or hydrocarbyl substituted styrenes, divinyl benzene, 4-vinylcyclohexene, tetrafIuoroethylene, vinylbenzocyclobutane, butadiene, isoprene, 1,4-hexadiene, cydobutene, cyclopentene, cyclohexene, norbornene, ethyl idene norbornene, acetylene, and mixtures thereof. Preferred monomers include the C2-10 α-olefins especially ethylene, propylene, isobutylene, 1-butene, 1-hexene, 4-methyl-1-pentene, styrene, and 1-octene. In general, the polymerization may be accomplished at conditions well known in the prior art for Ziegler-Natta or Kaminsky-Sinn type polymerization reactions, that is, temperatures from 0 to 250°C and pressures from atmospheric to 1000 atmospheres (100 MPa). Suspension, solution, slurry, gas phase or other process condition may be employed if desired. The catalyst may be supported and such supported catalyst may be employed in the polymerizations of this invention. Preferred supports include alumina and silica. The equivalent ratio of metal complex to activating cocatalyst (where employed) is preferably in a range from 1 :0.5 to 1 : 10 4 , more preferably from 1 :0.75 to 1 : 10 3 , most preferably 1 : 1 to 1 : 10. In most polymerization reactions the equivalent ratio of catalyst: polymerizable compound employed is from 10 "12 : 1 to 10 *1 : 1, more preferably from 10 "9 : 1 to 10- 4 : 1. Having described the invention the following examples are provided as further illustration thereof and are not to be construed as limiting. Unless stated to the contrary all parts and percentages are expressed on a weight basis. Examples 1-58 i) Preparation Of Reduced Metal Complex - (tert-butyl- amido)dimethyl(tetramethyl--5-cyclopentadienyl)si!ane (2-N, N-dimethylamino)benzyl titanium, In a drybox, 1.65 g (4.45 mmol) of TiCI 3 (THF) 3 and 2.29 g (4.46 mmol) of (MgCI) 2 ((CH 3 ) 4 C 5 Si(CH 3 ) 2 -C(CH 3 ) 3 )(THF) 2 were mixed together in a 100 mL flask. Tetrahydrofuran (THF) (50 mL) was added to give a purple solution. After 15 minutes, 0.63 g (4.46 mmol) of o-UCH 2 C 6 H 4 N(CH 3 ) 2 was added. After 30 minutes, the volatile materials were removed under reduced pressure to yield a red-brown solid. Pentane (50 mL) was added, the solution was filtered, and the volume reduced to 40 mL. This concentrated solution was cooled to -30°C. Red crystals were isolated by filtration and dried under reduced pressure. The electron paramagnetic resonance (EPR) spectrum of this material exhibited a single line at room temperature (g = 1.974) and 2 lines at 77 K. The X-ray crystal structure had final cell parameters corresponding to atridinic unit cell. Cell parameters were : a = 9.922(4), b= 14.366(9), c = 9.857(5) (angstroms); α= 104.35(6), β - 1 1 1.69(4), y - 99.61(6); V = 1212(1) (angstroms 3 ). ii) Alternate preparation of (tert-butylamido)dimethyl(tetramethyl-η 5 -cyclo- pentadienyl)siiane 2-(dimethylamino)benzyl titanium - reduction of Ti(IV) complex. TiCl3(THF)3 suspended in THF was contacted with equal molar quantities of solid tetramethylcyclopentadienyldimethyl-t-butylaminosiiane-diGrignard -THF complex ((CH 3 )4C5Si(CH3)2-N-t-Bu Mg2CI 2 (THF)2). To the resulting Ti(lll) complex was added a sufficient amount of a 1.56M solution of methyiene chloride in THF to provide a 0.5: 1 molar ratio of methylene chloride to the metal complex. After one hourthe product, (CH 3 ) 4 C5Si(CH3)2 - - BUTICI2, was recovered by extraction in pentane. In an argon filled glovebox, 0.990 g (2.69 mmol) of the (tert-butylamido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane titanium dichlorϊde and 0.389 g (2.76 mmol) of Li(o-CH 2 (C 6 H 4 )N(CH 3 ) 2 ) were mixed together in a 100 mL flask. Pentane (75 mL) was added and the mixture stirred for 16 hours to provide an orange colored product. The mixture was filtered through a sintered glass frit. The solids were washed with pentane and the filtrates combined. Pentane solvent was removed under reduced pressure leaving a solid residue which was washed with cold pentane. The pentane wash was decanted from the residue and the product dried under reduced pressure giving 0.96 g. of an orange solid. 1 H NMR analysis confirmed the product's identity as (tert-butylamido)dimethyl- (tetramethyl-η5-cyclopentadienyI)siianetitanium 2-(N,N-dimethylamino)benzyl chloride. Yield was 76 percent. The solid product (0.490 g, 1.05 mmole) obtained above was added to 50 ml of tetrahydrofuran. Magnesium powder (30 mg) wasthen added. The mixture was stirred at 25°C After 30 minutesthe orange color of the solution changed to brown. After 4 hours the solvent was removed under reduced pressure. The solid residue was extracted with pentane (3 x 25ml). The pentane extracts were filtered through a sintered glass frit, combined, and the pentane removed under reduced pressure to give 0.452 g (quantitative yield) of rose-purple microcrystalline solid, identified as (tert-butylamido)dimethyl(tetramethyl-η5-cyclo- pentadieny silane 2-(N,N-dimethylamino)benzyl titanium by comparison of its cyclic voltamagram with that of the material obtained in Preparation ϊ. iii) Preparation of Reduced Metal Complex- (tert-butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane allyl titanium (III), «CH 3 ) 4 C 5 Si(CH 3 ) 2 NC(CH 3 ) 3 )Ti(C 3 H 5 ). In a drybox, 0.30 g of TiCI 3 (THF) 3 and 0.42 g of (MgCI) 2 ((CH 3 ) 4 C 5 Si(CH 3 ) 2 N- C(CH 3 ) 3 )(THF) 2 were mixed in a Schlen tube. 20 mL of THF was added to give a purple solution. The Schlenktube was sealed and removed to a Schlenk line, and the solution was cooled to -30°C. 0.81 mLof 1.0 M aliyimagnesium bromide was added by syringe. After 20 minutes, the solution was warmed to 0°C and the volatile materials were removed under reduced pressure to yield a dark solid. While keeping the flask at 0°C pentane (30 mL) was added, and the deep red solution was filtered, concentrated to 5-7 mL, and cooled to -40°C. Red crystals were isolated by filtration and dried in 22 percent yield. The EPR spectrum of this material exhibited a single line at room temperature and 2 lines at 77K. iv) Preparation of Reduced Metal Complex - biscyclopentadienyl 2-(N,N- α ' imethylamino)benzyl titanium (III), Cp 2 Ti(o-CH 2 C 6 H 4 N(CH 3 ) 2 ). This metal complex was prepared according to the procedure of J. Am. Chem. Soc. 100, 8068-8073 (1978) by reaction of stoichiometric amounts of biscyclopentadienyltitanium (III) chloride and 2-dimethylaminobenzyl lithium in diethyl ether. v) Preparation of Reduced Metal Complex- (tert-butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane 1,2,3-trimethylallyl titanium (III). In a glovebo underan inert atmosphere, (tert-butylamido)dimethyl(tetramethyl- η 5 -cydopentadienyl)silanetitanium (IV) dichloride (0.500 g, 0.0014 mol) was dissolved in 30 mL of diethyl ether giving a yellow solution. To this solution was added 3-methyl-1 ,3-pentadiene (0.31 ml, 0.0027 mol) and i-PrMgCI (1.18 ml, 0.0028 mol). Gas evolution was noted and the color became red/purple. After 50 minutes the solvent was removed and the product dried. Extraction with pentane (5 X 10 ml) and drying under reduced pressure gave the desired product as a red solid. Polymerization Several catalyst compositions were prepared by combining the metal complex and a cocatalyst in a stirred polymerization reactor. The cocatalysts used were tris(perfluorophenyl)borane (I), methylalumoxane (1 M in toluene, available from Schering (AG) (II), trimethyl aluminum (III), triisobutylaluminum (IV), isobutyl modified methylalumoxane (1 M in toluene, MMAO, type 3A, available from Texas Alkyls Corp.) (V), triethylaluminum (VI), phenyl bis(perfluorophenyl) borane (VII), and triphenyl borane (VIII). Accordingly, a 2 L stirred reactor was charged with the desired amounts of mixed alkane solvent (Isopar-E™ available from Exxon Chemicals Inc.) and 1-octene comonomer. The reactor was heated to the polymerization temperature, hydrogen was added by differential pressure expansion from a -75 mL addition tank, and the reactor was saturated with ethylene to the desired pressure. Metal complex and cocatalyst (where used) were mixed in a drybox by syringing the desired amount of 0.0050 M metal complex solution (in Isopar-E™ or toluene) into a solution of the cocatalyst (in Isopar-E 1 " ortoluene). This solution was then transferred to a catalyst addition tank and injected into the reactor. The same procedure was employed when no cocatalyst was employed excepting only the complex was added to the reactor. The polymerization was allowed to proceed for the desired time and the solution was removed from the reactor and quenched with isopropanol. A hindered phenol antioxidant (Irganox™ 1010, available from Ciba Geigy Corp.) was added and the polymers (linear low density polyethylenes) were air-dried for 16 hours and then dried in a reduced pressure oven. Results are contained in Table I. TABLE I Com- Amt. Cocat- Amt. Solvent 1-Octene Ethylene H2 Temp Time Polymer Efficiency Ex. plex (μmol) alyst (μmol) (g) ( g ) (MPa) (ΔkPa) (°C) (min) (g) (g poly/g Ti) σ-> 25 1.00 3.0 740 118 170 140 16.3 340,292 TABLE I (continued) Com- Amt. Cocat- Amt. Solvent 1-Octene Ethylene H2 Temp Time Polymer Efficiency Ex, plex (μmol) alyst (μmol) ( g ) ( g ) ( M p a ) (Δ Pa) (°C) (min) (g) (g poly/g Ti) I TABLE I (continued) Com¬ Amt. Cocat¬ Amt. Solvent 1-Octene Ethylene H2 Temp Time Polymer Efficiency Ex. plex (μmol) alyst (μmol) (g) (g) (MPa) (ΔkPa) (°C) (min) (g) (g poly/g Ti) CO I Example 58 (i) Preparation of (phenylamido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane 2- (N,N-dimethylamino)benzyl titanium chloride In an argon filled glove box, 0.55 g (1.29 mmol) of (phenylamido)dimethyl- (tetramethyl-η5-cyclopentadienyl)siiane titanium dichloride (prepared according to Example 89 of EP-A-0416845 and 0J8g (1.3 mmol) of 2-(N,N-dimethylamino)benzyl lithium were slurried in ~75 mL of pentane. The mixture turned from yellow to red after ~ 16 hours. The mixture was filtered and the solids were extracted with diethyl ether. The pentane and ether fractions were devolatilized under reduced pressure. 'H NMR analysis confirmed the product's identity from both fractions as (phenylamido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane titanium 2- (N,N-dimethylamino)benzyl chloride. Total yield was 0.33 g, 53 percent. (ii) Preparation of (phenylamido)dimethyl(tetramethyl-η5-cydopentadienyl)silane-2- (N,N-dimethylamino)benzyl titanium In an argon filled glove box 16 mg of magnesium powder was added to 0.33 g (0.68 mmol) of (phenylamido)dimethyl(tetramethyl-η5-cydopentadienyl)silane 2-(dimethyl- amino)benzyl titanium chloride in —40 mL of tetrahydrofuran (THF). After stirring for 6 hours the THF was removed under reduced pressure. The solid residue was extracted with pentane. The pentane extracts were filtered and combined and the pentane solvent removed under reduced pressure to give 0.29 g (94 percent yield) of (phenylamido)dimethyl(tetramethyl-η5- cydopentadienyl)silane-2-(N,N-dimethylamino)benzyl titanium, characterized by cyclic voltametry. Example 59 A 100 mil round bottom flask was loaded with 0J00 g of (tert-butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane (2-N, N-dimethyiamino)benzyl titanium. 30 ml of pentane were added to form a solution. To this solution was added, via pipet, 0J 19 g of B(C6Fs) 3 in 40 ml of pentane. Within minutes the solution become cloudy and a pink/orange solid precipitated from solution. The reaction mixture was stirred for an additional 15 minutes after which time the solid was collected by filtration and washed with fresh pentane (3x15 ml). Yield of the product (believed to be [(tert-butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silanetitanium(lll)] ((2-N, N- dimethylamino)benzyl)trispentafluorophenylboron), after drying under reduced pressure was 0.205 g. The ESR spectrum of this reaction product showed a single line at room temperature (g = 1.97). The cycle voltamagram (in dimethyl ether (DME) with no supporting electrolyte) of the reaction product showed an irreversible reduction wave at -2.74 volts vs. ferrocene. Under similar conditions, the neutral complex, (tert-butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane (2-N, N-dimethylamino)benzyl titanium, was not conductive and did not give a cyclic voltamagram. The fact that electrochemical measurements could be obtained in the absence of added supporting electrolyte strongly indicates that the activated complex was cationic. Underthe polymerization conditions of Example 54, the above activated complex used as a catalyst gave 28.8 g of ethylene/octene copolymer. Example 60 The reaction conditions of Example 59 were repeated to prepare the pink/orange cationic metal complex which was then redissolved in tetrahydrofuran thereby giving a purple solution. Addition of pentane caused precipitation of a purple solid which was collected by filtration, washed with fresh pentane, and dried. The ESR spectrum of the purple product showed a single line at room temperature (g = 1.97) and the cyclic voltamagram (in DME with no supporting electrolyte) showed an irreversible reduction wave at-2.74 volts vs. ferrocene. Under similar conditions, the neutral complex did not give a cyclic voltamagram thereby indicating thatthe purple solid was an ionicTi + 3 complex. 15 mg of the purple solid was combined with 0.5 mLof methanol and the resulting solution was analyzed by gc/mass spectroscopy. THF was identified in the solution, indicating thatthe purple solid contained the neutral Lewis base, THF. On this basis the purple solid was believed to be [(tert-butylamido)dimethyl(tetramethyl-η.5-cyclopentadienyl)silane titaniumOI tTHFJl ^-N. N-dimethylaminoJbenzylJtrispentafluorophenyl boron). Underthe polymerization conditions of Example 54, the above purple solid used as a catalyst gave 29.2 g of ethylene/octene copolymer. Example 61 (i) Preparation of (t-butylamido)dimethyl(tetramethyl-η.5-cyclopentadienyl)silane (1- phenyI-3-benzylaIlyl) titanium In an argon filled glove box, 0.50 g (1.4 mmol) of (t-butylamido)dimethyl- (tetramethyl-η5-cyclopentadienyl)silane titanium dichloride was dissolved into 30 mL of diethyl ether to give a yellow solution. 0.28 g (1.4 mmol) of 1 ,4-dipheπyl-1 ,3 butadiene and 1J8 mL (2.8 mmole) of isopropyl magnesium chloride were added with stirring. Gas evolution occurred and the mixture darkened to a red/purple color over 50 minutes. The solvent was removed and the product was dried. The solid was extracted with pentane (5x10 mL) and dried under reduced pressure to give the product as a red/purple solid (0.545 g). Underthe polymerization conditions of Example 54, 68.7 g of ethylene/octene copolymer were produced. Catalyst efficiency was 717,000 g/g. Example 62 (i) Preparation of (t-butylamido)dimethyl(tetramethyl--5-cydopentadienyl)silane (1 J-diphenyl-3-(diphenylmethyl)allyl) titanium In an argon filled glove box, 0.50 g (1.4 mmol) of (t-butylamido)dimethyl- (tetramethyl-ηS-cyclopentadienyl)siiane titanium dichloride was dissolved into 30 mL of diethyl ether to give a yellow solution. 0.49 g (1.4 mmol) of 1 J ,4,4-tetraphenyl-1 ,3-butadiene and 1.18 mL (2.8 mmole) of isopropyt magnesium chloride were added with stirring. Gas evolution occurred and the mixture darkened to a red color over 2 hours. The solvent was removed and the product was dried. The solid was extracted with pentane (4x15 mL) and dried under reduced pressure to give the product as a tacky, red solid. Underthe polymerization conditions of Example 54, 32.0 g of ethylene/octene copolymer were produced. Catalyst efficiency was 334,029 g/g.

Claims: CLAIMS 1. An addition polymerization catalyst comprising: (i) a metal complex corresponding to the formula: Cp a (ZY)bML c , wherein: a is 1 or 2; b is 0 or 1 ; c is 1 or 2; the sum of a, b and c is 3; Cp independently each occurrence is a cyclopentadienyi group π-bound to M, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbyimetalloid or halohydrocarbylmetalloid substituted derivative of said cyclopentadienyi group, said Cp containing up to 50 nonhydrogen atoms, and, when a is 2, optionally both Cp groups may be joined together by a bridging group; L independently each occurrence is hydride, halo, or a monovalent anionic ligand selected from covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, and sulfido groups optionally being further substituted with amine, phosphine, ether, and thioether; mixtures thereof; said ligand having up to 50 nonhydrogen atoms, with the proviso that in at least one occurrence L is a stabilizing ligand comprising an amine, phosphine, ether or thioether functionality able to form a coordinate-covalent bond or chelating bond with M, or except when a is 1, comprising an ethylenic unsaturation able to form an η3 bond with M; M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation state; Y is a linking group comprising nitrogen, phosphorus, oxygen or sulfur covalently bonded to M and Z through said nitrogen, phosphorus, oxygen or sulfur atom; Z is a divalent moiety comprising oxygen, nitrogen, phosphorous, boron, or a member of Group 14 of the Periodic Table of the Elements, said moiety having up to 30 nonhydrogen atoms; the ligand moiety consisting of -Cp-Z-Y- being dianionic and having the ionic charges residing formally on Cp and Y; and, when b is 0 and optionally when b is 1 ; and (ii) an activating cocatalyst. 2. An addition polymerization catalyst comprising in combination: (i) a metal complex corresponding to the formula: Cp' 2 ML', wherein: Cp' independently each occurrence is a cyclopentadienyi group π-bouπd to M, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbyimetalloid or halohydrocarbylmetalloid substituted derivative of said cyclopentadienyi group, said Cp' containing up to 50 nonhydrogen atoms, and optionally both Cp groups may be joined together by a bridging group; M is a metal of Group4 of the Periodic Table of the Elements in the + 3 oxidation state; L' is a monovalent anionic stabilizing ligand selected from covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, sulfido groups and mixtures thereof, and being further substituted with an amine, phosphine, ether, or thioether containing substituent able to form a coordinate-covalent bond or chelating bond with M; said ligand having up to 50 nonhydrogen atoms; and (ii) an activating cocatalyst. 3. An addition polymerization catalyst comprising in combination: (i) a metal complex corresponding to the formula: Cp"ML"2, wherein: Cp" is a cyclopentadienyi group π-bound to M, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbyimetalloid, or halohydrocarbylmetalloid substituted derivative thereof, said Cp" containing up to 50 nonhydrogen atoms; M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation state; L" independently each occurrence is hydride, halo, or a monovalent anionic ligand selected from covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, and sulfido groups; mixtures thereof; and amine, phosphine, ether.and thioether derivatives of the foregoing, said ligand having up to 50 nonhydrogen atoms, with the proviso that in at least one occurrence L" is a stabilizing ligand comprising an amine, phosphine, ether or thioether functionality able to form a coordinate-covalent bond or chelating bond with M, or comprising an ethylenic unsaturation able to form an η3 bond with M; and (ii) an activating cocatalyst. 4. A metal complex corresponding to the formula: L ' " wherein: M is a metal of Group 4 of the Periodic Table of the Elements in the + 3 oxidation state; Cp'" is a cyclopentadienyi group, or a hydrocarbyl, silyl, halo, halohydrocarbyl, hydrocarbyimetalloid, or halohydrocarbylmetalloid substituted derivative thereof, said Cp'" containing up to 50 nonhydrogen atoms; Z is a divalent moiety comprising oxygen, nitrogen, phosphorous, boron, or a member of Group 14 of the Periodic Table of the Elements, said moiety having up to 30 nonhydrogen atoms; Y is a linking group comprising nitrogen, phosphorus, oxygen or sulfur covalently bonded to M and Z through said nitrogen, phosphorus, oxygen or sulfur atom, the ligand moiety consisting of-Cp"'-Z-Y- being dianionic and having the ionic charges residing formally on Cp'" and Y; and L'" is a monovalent anionic stabilizing ligand selected from: a) covalently bonded hydrocarbyl, silyl, amido, phosphido, alkoxy, aryloxy, sulfido groups and mixtures thereof, and being further substituted with an amine, phosphine, ether, orthioether containing substituent able to form a coordinate-covalent bond or chelating bond with M, said ligand having up to 50 nonhydrogen atoms; and b) linear C3-C 1 5 hydrocarbyl groups comprising an ethylenic unsaturation able to form an η3 bond with M. 5. An addition polymerization catalyst comprising a complex as claimed in Claim 4 and an activating cocatalyst. 6. A catalyst or complex as claimed in any one of the preceding claims, wherein M is titanium. 7. A catalyst or complex as daimed in any one of the preceding claims, wherein L, L', L" or L'" is 2-di(C 1 -C 4 -alkyl)amϊnobenzyl or 2-(dϊ(C | -C4-alkyl)aminomethyl)phenyl. 8. A catalyst or complex as claimed in Claim 7, wherein L, L', L" or L"Js 2-(N,N- dimethyiamino)benzyl. 9. A catalyst or complex as claimed in any one of Claims 1, and 3 to 6, wherein L, L" or L"' is linear C3-C15 hydrocarbyl comprising an ethylenic unsaturation . 10. A catalyst or complex as claimed in Claim 9, wherein L, L" or L"' is allyl. 1 1. A catalyst as claimed in any one of Claims 1 , 2, 6, 7 or 8,wherein the metal complex comprises two Cp groups joined bya bridging group of the formula (R" 2 E) X wherein E is silicon or carbon and R" independently each occurrence is hydrogen, silyl, hydrocarbyl or a combination of silyl and hydrocarbyl, said R" having up to 30 silicon or carbon atoms, and is 1 to 8. 12. A catalyst or complex as claimed in Claim 8, wherein the metal complex is biscydopentadienyl 2-(N,N-dimethylamino)benzyl titanium (III). 13. A complex as claimed in Claim 4 selected from (tert-butylamido)- dimethyl(tetramethyl-η5-cyclopentadienyl)silane 2-(N,N-dimethylamino)benzyl titanium (III), (tert-butyl- amido)dimethyl(tetramethyl-~5-cyclopentadienyl)silane allyl titanium (III), (tert- butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane 1,2,3-trimethylallyl titanium (IH)Jtert-butyl- amido)dimethyl(tetramethyl-η5-cyclopentadienyl)silane 1-phenyl-3-benzylallyl titanium (III), and (tert-butyl- amido)dimethyl(tetramethyl-η5-cydopentadienyl)silane 1 J- diphenyl-3-(diphenylmethyl)allyl titanium (III) 14. A catalyst as claimed in Claim 5, wherein the metal complex is selected from (tert-butylamido)-dimethyl(tetramethyl-η5-cyclopentadienyl)-siiane 2-(N,N- dimethyiamino)benzyl titanium (III), (tert-butylamido)dimethyl(tetramethyl-η5- cyclopentadieny silane allyl titanium (III), and (tert-butylamido)dimethyl(tetramethyl-η5- cyclopentadienyDsilane 1,2,3-trimethylallyl titanium (III). 15. An addition polymerization catalyst as claimed in Claim 12 or 14, wherein the cocatalyst istris(pentafluorophenyl)boron. 16. A catalyst as claimed in any one of Claims 1 to 3, 5 to 12, 14or 15, wherein the ratio of metal complex to activating cocatalyst is from 1 :0.01 to 1 : 106. 17. A catalyst as claimed in any one of Claims 1 to 3, 5 to 12 or 14 to 16, wherein the activating cocatalyst is selected from alkylalumoxanes; aluminum alkyls; aluminum halides; alkylaluminum halides; Lewis acids other than any of the foregoing; and mixtures thereof. 18. A catalyst as claimed in Claim 17, wherein the activating cocatalyst is tris(4- fluorophenyl)boron, tris(2,4-difluorophenylboron), tris(3,5-bis(trifluoromethyl)phenyl)boron, tris(pentafiuorophenyl)boron, pentafluorophenyl diphenylboron. triphenyl boron or bis(pentafluorophenyl)phenyl boron. 19. A catalyst as claimed in Claim 18, wherein the activating cocatalyst is tris(pentafluorophenyl)boron. 20. A catalyst or complex as claimed in any one of the preceding claims, additionally comprising a neutral Lewis base. 21. A catalyst or complex as claimed in claim 20, wherein the neutral Lewis base is selected from the group consisting of organic amines, amides, ketones, nϊtriies, phosphines, phosphorylamides, esters, ethers, thioethers and thioesters, said neutral Lewis base containing up to 20 nonhydrogen atoms. 22. A catalyzed addition polymerization process comprising contacting under addition polymerization conditions at least one addition polymerizable monomer with a catalyst or complex according to any one of Claims 1 to 21. 23. A process for preparing a catalystas claimed in Claim 1 , comprising contacting a Group4metal complex corresponding to the formula: Cp a (ZY)bM*L c X, wherein: a, b, c, Cp, L, Y and Z are as defined in Claim 1, M* is a metal of Group 4 ofthe PeriodicTable ofthe Elements in the + 4 oxidation state; and Xis halide or C^ 0 hydrocarbyloxide, with a reducing agent under reducing conditions to form a metal complex corresponding to the formula: Cp a (ZY)bML c , wherein a, b, c, Cp, L, M, Y and Z are as defined in Claim 1, and, when a cocatalyst is present, contacting the so formed complex with the cocatalyst.

Inventors: DEVORE DAVID D, NICKIAS PETER N, ROSEN ROBERT K, STEVENS JAMES C, TIMMERS FRANCIS J, DEVORE, DAVID, D., NICKIAS, PETER, N., ROSEN, ROBERT, K., STEVENS, JAMES, C., TIMMERS, FRANCIS, J.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1993
Main classification: C08F10
IPC codes: C07F17, C08F4, C08F10