Degassing agents for powder coating compositions based on polyester

Abstract: A thermosetting powder coating composition containing a solid saturated thermosetting polyester having an acid value of at least 25 and a glass transition temperature (Tg) of at least 45°C and a curing agent such as a hydroxyalkyl amide capable of reacting with carboxylic acid groups of the polyester additionally contains, as an anti-popping agent, a thermoplastic polymer which i) is solid, ii) has a Tg of 30-100°C, iii) comprises, at least mainly, units derived from at least one alkyl acrylate or alkacrylate and iv) has an acid value of no more than 10.

Description: This invention relates to thermosetting resin based powder coating compositions, which after application to a substrate can be melted, fused and cured by heat to form a hard resilient film. As a means of surface coating, powder technology offers significant advantages. Normally a single application is sufficient to form the final coating, waste or excess powder can be recycled, and the total application weight is less than with liquid systems where a significant proportion of the composition is volatilised in the cure process creating the risk of environmental contamination. EP-A-0517535, acknowledged under Art 54(3) EPC, discloses a powder coating composition containing a base resin, for example, a polyester, a hardener, for example, a glycidyl bearing epoxy compound or isocyanate and an acrylic resin containing from 40 to 100% by weight of t-butyl acrylate and/or methacrylate. Acid functional polyester based powder coatings cured with diglycidyl ether bisphenol A type materials have poor weather resistance. Exterior grade coatings may be made from hydroxy-terminated polyester which is cured with (expensive) blocked isocyanate, but the preferred method has been to use a carboxy-functional polyester cured by a cycloaliphatic epoxy resin. Of the cycloaliphatic epoxies, triglycidyl isocyanurate (TGIC) is the most commonly used, but it is both an irritant and toxic. More recently Rohm and Haas have developed the less toxic hydroxy alkylamide (HAA) range of curing agents for use with carboxy-terminated polyesters. Polycondensation reactions between the hydroxyl groups of the HAA and the carboxylic groups of the polyester at temperatures of 140 - 200°C produce the cured film, at the same time splitting off water. If water vapour is unable to escape freely, popping occurs which leaves the film surface pin holed and cratered. It is known to employ a so-called "antipopping" or "degassing" agent; see, for example, EP-A-0471409, which discloses the use of a crystalline wax as a degassing agent in a thermosetting powder composition based on an acid functional polyester and a hydroxyalkylamide curing agent. It is believed that such agents have a surface tension effect to "hold the film open" during cure to allow the vapour to escape. It is added typically in amounts of between 5 and 50 parts by weight as a component of a 1000 part powder coating formulation hereinafter referred to as a "paint". As illustrated in EP-A-0516375, published after the priority date of this application, benzoin is conventionally used for this purpose. However, benzoin with either heat or ageing tends to cause a degree of yellowing in the paint film. Thus, although HAAs present an advance in polyester powder coating crosslinking technology and benzoin is an answer to popping, the combination of these two materials in the same formulation leads to a new problem. At cure temperature, the compounds at least partially react to form coloured compounds which cause a darkening of the paint. This is sufficiently noticeable to prevent the attainment of a true brilliant white coating. The problem also creates difficulties in formulating pale or pastel shades. The present invention has identified a range of solid thermoplastic polymers that function as anti-popping agents. They can be used as direct replacements for benzoin, when formulated with HAAs, without causing discolouration. Hence true brilliant white, polyester based, HAA cured powder coatings are at last made possible. Incidentally, direct benzoin replacement, as an anti-popping agent, by such a solid thermoplastic polymer may also be made in powder coating formulations which do not contain the HAA curing agent. Differences in colour are noted with curing agents other than HAA, but for such curing agents discolouration is not such a significant problem. However other benefits may be thought useful. The replacement of a low molecular weight, water extractable, compound (benzoin) by a much higher molecular weight water insoluble polymer will certainly improve the durability of the powder paint coatings in terms of weathering; at least marginal improvements may also be expected in terms of toughness and flexibility. The present invention provides a thermosetting powder coating composition comprising:- a) a solid saturated polyester having an acid value of at least 25 and a glass transition temperature (Tg) of at least 45°C; b) a curing agent capable of reaction with carboxylic acid groups of the saturated polyester (a) and preferably comprising a hydroxyalkyl amide (HAA); and c) a thermoplastic polymer which , in combination, i) is solid; ii) has a Tg of from 30°C to 100°C inclusive; iii) comprises units, at least 80% of which are derived from at least one alkyl acrylate or alkacrylate; iv) has an acid value of no more than 10, preferably no more than 5; and v) is present in an amount of from 2 to 6% by weight of the total weight of the compound. According to another aspect, the invention provides the use, as an antipopping agent in a thermosetting powder coating composition containing a solid saturated polyester having carboxylic acid groups and curable by a curing agent capable of reacting with the carboxylic acid groups of the solid saturated polyester, of the thermoplastic polymer [c]. The polyester [a] may be any such thermosetting polyester having free carboxylic groups capable of a crosslinking reaction with the curing agent. The solid saturated polyester is one which is free from ethylenic (alkene) or acetylenic (alkyne) unsaturation. It can be made by reacting one or more polyols, especially glycols, with one or more saturated poly, especially, di, carboxylic acids, the dimethyl esters thereof or their anhydrides. In an alternative reaction by which the saturated polyester can be made, one or more (typically two) glycols are reacted with one or more (typically two) saturated dicarboxylic acids or reactive derivatives thereof such as their dimethyl ester(s) or their anhydride(s). The required acid value of at least 25 may be obtained either by adjusting the relative proportions of polycarboxylic acid and polyol components or, for example, preparing a hydroxyl-terminated prepolymer and reacting this with a polycarboxylic acid. Typically, the polyol component is derived from at least one of ethylene glycol, propylene glycol, 1,4-butanediol, 1,6-hexanediol, neopentyl glycol, diethylene glycol, 1,4-cyclohexanedimethanol and trimethylolpropane. Typically, the acid component is derived from at least one of adipic acid, succinic acid, azelaic acid, sebacic acid, trimellitic acid, terephthalic acid, isophthalic acid and reactive derivatives thereof. Preferably at least one of the acid and glycol components is derived from two acids or glycols respectively. The curing agent may be an epoxy resin, for example, a cycloaliphatic epoxy resin such as triglycidyl isocyanurate. However, as mentioned above, particular benefits of the invention are realised when the curing agent comprises a hydroxyalkyl amide (HAA) but nevertheless a brilliant white coating (previously unattainable with such coatings when an antipopping agent was also present) is desired. A β-hydroxyalkyl amide curing agent which may be used has, according to EP-A-0516375, the formula wherein R 1 is H or C 1-5 alkyl R 2 is H, C 1-5 alkyl or R is a bond, or a mono- or polyvalent organic radical derived from a saturated, unsaturated or aromatic hydrocarbon which is optionally substituted and contains 2-20 carbon atoms, for example an alkylene radical where x is 2-12, e.g. 4-10, m is 1 or 2 n is 0 or 2 and m + n is at least 2, e.g. 2-4. Such a curing agent (b) is available commercially as Primid ™ XL-552 (Rohm and Haas) which, according to the manufacturers, has the formula: Preferably, the respective amounts of HAA curing agent (b) and solid saturated polyester (a) should be such as to provide a hydroxy equivalent of the HAA (b) to a carboxyl equivalent of the polyester (a) of about 0.6:1 to 1.6:1, especially 0.8:1 to 1.3:1. The solid thermoplastic polymer (c), present as antipopping agent, has a glass transition temperature (Tg) of from 30°C to 100°C, preferably within the range 30 to 70°C inclusive, more preferably within the range 35 to 60°C inclusive. It should have a low or medium molecular weight and have a degree of compatibility, preferably a partial compatibility, with molten polyester powder coating resins when above its Tg. Thus, the preferred peak molecular weight range is from 500 to 1 million, more preferably 1,000 to 500,000, especially 3,000 to 130,000. It has an acid value of no more than 10 so that it does not undergo any significant reaction with the hydroxyl groups on either or both of the solid saturated polyester (a) or curing agent (b). It is believed also that the absence of a significant number of carboxyl groups from the solid thermoplastic polymer will provide a certain degree of incompatibility between the solid saturated polyester (a) and the solid thermoplastic polymer (c) which is thought may be necessary. The polymer should be active as an anti-popping agent at the cure temperature of the powder coating composition which may be within the range of 140 - 220°C, preferably within the range 140 - 200°C. Suitable thermoplastic polymers have been found to be acrylate polymers such as homo and copolymers of alkyl, preferably C 1-4 alkyl, acrylates, or alkacrylates, preferably (C 1-2 alk) acrylates, especially methacrylates, mixtures thereof and copolymers of any of these with styrene, especially styrene/(meth)acrylate copolymers. A copolymer contains at least 80% of the alkyl acrylate or alkacrylate. The thermoplastic polymer is present in an amount of 2-6%, especially 2.5-5%, by weight of the total weight of the composition. According to another aspect, the invention provides a method of preparing the above thermosetting powder coating composition comprising components (a), (b) and (c), which method comprises maintaining the solid saturated polyester (a) at a temperature above its melting point, blending into the polyester the thermoplastic polymer (c), allowing the mixture to cool, granulating the resulting solid, adding the curing agent (b) and optionally any other additive, extruding the resultant composition through an extruder and grinding the resultant mass to form the said powder coating composition. Such blending of the antipopping agent and the polyester may be carried out by the resin manufacturer in the reactor prior to running out the hot molten completed polyester base resin. If the thermoplastic polymer is added and stirred into the resin at or above 180° C it will form an intimate blend with the polyester. When the composition has been cooled and granulated, the paint manufacturer may then blend in the curing agent and any other ingredient such as pigment, filler etc. by extrusion. According to an alternative method in accordance with the invention for preparing the above thermosetting powder coating composition comprising components (a), (b) and (c), each of components (a), (b) and (c) is merely admixed, together with any other additive optionally present, to form a mixture which is extruded at normal powder coating temperatures usually at a minimum temperature of 50°C, preferably at a temperature of at least 80°C, to form a mass, which is allowed to cool and then ground into a powder. Such blending of the solid thermoplastic polymer with the polyester may be carried out by the paint manufacturer, in which case the full powder paint formulation is mixed and extruded. When passing the composition through the extruder at typically 100 - 120°C, the polymer of Tg ≦ 100°C will be sufficiently dispersed or miscible to be effective with the polyester. In addition to its serving as an anti-popping agent, the solid thermoplastic polymer may additionally improve other properties of the coating composition such as the flexibility of powder coating films produced from it. Flow modifiers or flow control agents, especially polymeric flow control agents, may also be added to polyester powder coating formulations. These may be polymers of low molecular weight and may even be acrylic in nature. However they are all liquids or semi-liquids at ambient temperature (Tg ≤ 30°C), although sometimes they may give the appearance of powders when they are absorbed into silica particles for ease of handling. Such polymers function so as to prevent the formation of "orange peel", ripples or waves on the paint surface during cure, but they do not alleviate popping even when added in excess of normal levels. They are present in amounts ≤1% by weight of the total weight of the paint composition. The powder coating composition may be coated onto a substrate by any of the conventional methods, for example spraying, and thereafter melted, fused and cured by heat to form a hard resilient film of a thickness which is preferably 50-250µm, more preferably 60-100µm, especially 60-80µm. Embodiments of the invention will now be described in more detail with reference to the following Examples. Example 1 Preparation of Polyester A polyester was prepared from the following composition so as to provide hydroxyl termination. pbw Terephthalic acid 440.3 Adipic acid 42.1 Neopentyl glycol 343.7 Trimethylolpropane 14.1 Dibutyl tin oxide 2.9 Water 3.1 The hydroxy-terminated polyester was then reacted with the following composition at high temperature to provide a carboxyl-terminated polyester capable of reaction with an HAA curing agent. Isophthalic acid 105.7 Dibutyl tin oxide 2.4 Examples 2-3 Paint Formulation - Method 1 These Examples describe a first paint formulation method embodying the invention in which the solid thermoplastic polymer (c) is first blended with molten saturated polyester (a) to form a polymer blend, granules of which are thereafter blended into a paint formulation. Example 2 - Blending of Anti-popping Agent While the carboxyl terminated polyester prepared above was still molten, the following anti-popping agent was blended with it. Acronal ™ 260F 19.7 parts. Acronal 260F is an acrylic/styrene copolymer commercially available from BASF, in the form of fine white beads. It has a softening point (DIN 53180) of about 120°C, a low acid value (DIN 53402) of ca 2 mg. KOH/g. The resultant blend, containing both polyester and anti-popping agent, was cooled and granulated. It is referred to below as PPA. Example 3 - Blending of Formulation The following blends were then prepared, each containing a polyester, HAA curing agent, pigment, flow modifier and anti-popping agent, namely Acronal ™ 260F (Example 3A) or benzoin (Example 3B). Example 3A pbw PPA of Example 2 950 (containing Acronal ™ 260F) Primid ™ XL-552 50 Titanium dioxide 500 BYK ™ 360P 10 Ultramarine blue 1 Primid ™XL-552 is a commercially available hydroxyalkyl amide with the following characteristics, provided by the manufacturer: BYK ™ 360P is a commercially available polymeric flow control agent from BYK-Chemie. Example 3B (comparative) pbw Polyester of Example 1 950 Benzoin 10 Primid ™ XL-552 50 Titanium dioxide 500 BYK ™ 360P 10 Ultramarine blue 1 The separate blends of Examples 3A and 3B were extruded at 100 - 120°C then ground to provide powder coating formulations. Example 4 Application of Coating The above powder coating formulations were applied to respective metal sheets by an electrostatic coating procedure and then cured for 15 minutes in an oven at 180°C. The colour of the resulting film was measured using a Minolta colour computer according to ASTM D2244. Example Tristimulus values L a b 3A 94.02 -1.14 -2.59 3B 93.63 -1.45 -0.54 The "b" value gives an indication of yellowness, the more negative the value, the less the apparent yellowness. Hence it can be seen that an excellent white surface is produced by the coating composition embodying the invention, which is far superior to that obtained when using benzoin as an anti-popping agent. Example 5 Paint formulation - Method 2 This describes a second paint formulation method embodying the invention in which the solid thermoplastic polymer (c) is initially cold blended with the solid saturated polyester (a). Nine acrylic polymers were blended in this manner to provide respective paint formulations shown in Table 3 below. In each case, all components of the paint formulation were cold blended in a Z blade mixer for 20 minutes and the resulting blend was then passed through an extruder at a temperature of 100 - 120°C to form a mass which was cooled and then ground to a powder. The respective acrylic polymers used were all commercially available and details are given in Tables 1 and 2, Table 1 giving details of the acid value, Tg and composition and Table 2 the measured peak, number average and weight average molecular weights. The molecular weights were determined by gel permeation chromatography. All molecular weights are given as polystyrene equivalents. Paint formulations were made up with and without flow agent according to the compositions shown in Table 3. I] No Flow Agent pbw Resin of Example 1 950 Primid XL 552 50 Titanium dioxide 500 Acrylic polymer 25 Ultramarine blue 1 II] With Flow Agent pbw Resin of Example 1 950 Primid XL 552 50 Titanium dioxide 500 Acrylic polymer 25 BYK 360P 10 Ultramarine blue 1 Example 6 Application of Coating Powder paint was electrostatically coated onto 4 inch (10.16 cm) by 6 inch (15.24 cm) Type S ground steel, "Q-Panels", which are standardised substrates for testing coatings, adhesives and mist inhibitors and are made from standard cold rolled steel complying with SAE 1010 (low carbon), ASTM-A-366 and QQS-698. The type S panels conform to standard D609, Type 2 of A366, are of ¼ hard temper, roughness 15-25 microinches (381-635 nm), B60-B70 Rockwell Hardness, tensile strength 54,000 psi (372 MPa) and 0.8mm thick. They have a surface which is abrasive ground, completely removing the mill surface and imparting a smooth surface resembling a "brushed" finish. The coated panels were cured for 15 minutes at 180°C, the film thickness being approximately 70 microns. They were then subjected to a visual analysis of colour, pinholing and flow. Further tests were performed: 1] Rhopoint 60 degree gloss reading* 2] Colour measurement using a Minolta colour computer 3] Standard pencil hardness test Minolta (L, a, b) Colour Results (see Example A) Minolta Colour Paint No. L a b P.870 93.90 -1.16 -3.27 P.871 94.05 -1.14 -3.09 P.872 94.12 -1.12 -3.16 P.873 94.15 -1.16 -3.19 P.874 94.10 -1.17 -3.24 P.875 93.94 -1.19 -2.84 P.876 94.16 -1.15 -3.09 P.877 94.15 -1.14 -3.17 P.878 94.31 -1.14 -3.29 It can be seen from the above results that paints containing the higher molecular weight acrylic polymer additives and no flow agent tended to produce films of good gloss and flow. As the molecular weight of the additive decreased, then the degree of cissing increased and the gloss diminished. All films containing flow agent were of excellent whiteness, gloss and flow showing no signs of cissing (pitted appearance) and only extremely minor surface popping. Hence films of good quality and whiteness can be made, cured with HAA and without the use of benzoin.

Claims: A thermosetting powder coating composition comprising a) a solid saturated polyester having an acid value of at least 25 and a glass transition temperature (Tg) of at least 45°C; b) a curing agent capable of reaction with carboxylic acid groups of the solid saturated polyester (a); and c) an antipopping agent; characterised in that the antipopping agent is a thermoplastic polymer which, in combination, i) is solid, ii) has a Tg of from 30°C to 100°C inclusive, iii) comprises units, at least 80% of which are derived from at least one alkyl acrylate or alkacrylate; iv) has an acid value of no more than 10; and v) is present in an amount of from 2 to 6% by weight of the total weight of the composition. A composition according to claim 1, wherein the curing agent is a hydroxyalkyl amide. A composition according to claim 2, wherein the respective amounts of hydroxy alkylamide curing agent (b) and solid saturated polyester (a) is such as to provide a hydroxy equivalent of the hydroxy alkylamide (b) to a carboxyl equivalent of the polyester (a) of about 0.6:1 to 1.6:1, especially 0.8:1 to 1.3:1. A composition according to claim 1, 2 or 3, wherein the thermoplastic polymer has an acid value of no more than 5. A composition according to any preceding claim, wherein, in the thermoplastic polymer, the alkyl acrylate or alkacrylate from which the units are derived is a C 1-4 alkyl acrylate or C 1-4 alkyl (C 1-2 alk) acrylate. A composition according to any preceding claim, wherein the thermoplastic polymer is a copolymer having units derived from an alkyl acrylate or alkacrylate and styrene. A composition according to any preceding claim, wherein the thermoplastic polymer has a Tg of from 30 to 70°C inclusive. A composition according to any preceding claim, wherein the thermoplastic polymer has a peak molecular weight of 500 to 1,000,000. A composition according to any preceding claim, which additionally contains d) a flow control agent. A method of preparing a thermosetting powder coating composition according to claim 1, which method comprises maintaining the solid saturated polyester (a) at a temperature above its melting point, blending into the polyester the thermoplastic polymer (c), allowing the mixture to cool, granulating the resulting solid, adding the curing agent (b) and optionally any other additive, extruding the resultant composition through an extruder and grinding the resultant mass to form the said powder coating composition. A method of preparing a thermosetting powder coating composition according to claim 1, which method comprises admixing each of components (a), (b) and (c), and optionally any other additive, extruding the resultant mixture at a temperature of at least 80°C to form a mass, allowing the mass to cool and grinding it into a powder to form the powder coating composition. A method of forming a coating on a substrate comprising applying to the substrate a powder coating composition according to claim 1 and curing the composition at a temperature within the range 140-220°C. Use, as an antipopping agent in a thermosetting powder coating composition containing a solid saturated polyester having carboxylic acid groups and curable by a curing agent capable of reacting with the carboxylic acid groups, of from 2 to 6% by weight of the total weight of the composition of a thermoplastic polymer which i) is solid ii) has a Tg of from 30°C to 100°C inclusive, iii) comprises units, at least 80% of which are derived from at least one alkyl acrylate or alkyl alkacrylate; and iv) has an acid value of no more than 10.

Inventors: PHILLIPS ANTONY, WILKINSON ROY ROWLEY, PHILLIPS, ANTONY, WILKINSON, ROY ROWLEY
Applicants: SCOTT BADER CO, SCOTT BADER COMPANY LIMITED
Application year: 1993
Main classification: C09D167
IPC codes: C09D167, C09D5