Process for producing alpha-hydroxyisobutyramide

Abstract: There is disclosed a process for producing α-hydroxyisobutyramide by hydration reaction of acetone cyanohydrin in the presence of a catalyst consisting essentially of manganese dioxide which process comprises pretreating the catalyst with a reducing agent. The above process is capable of eliminating the catalyst clogging trouble due to the deposition of the by-produced oxamide and thus proceeding with long-term reaction with the stabilized catalyst performance.

Description: 1.Field of the Invention The present invention relates to a process for industrially producing α-hydroxyisobutyramide by the hydration reaction of acetone cyanohydrin. α-Hydroxyisobutyramide is an industrially useful substance which serves as an intermediate starting material for methacrylamide and methyl methacrylate. 2.Description of the Related Arts It is publicly known that manganese dioxide is used as a solid catalyst in the hydration reaction of acetone cyanohydrin. According to any of the conventional processes, α-hydroxyisobutyramide is obtained by the reaction of acetone cyanohydrin with water as shown by the following reaction equation at a temperature of 40 to 100°C in the presence of manganese-based catalyst and preferably acetone-based solvent in a yield of 60 to 95%. CH 3 C(CH 3 )(OH)CN + H 2 O → CH 3 C(CH 3 )(OH)CONH 2 However, actual result of the hydration reaction thereof by the use of the publicly known manganese-based catalyst involves serious problems from the viewpoint of stable operation in an industrial scale due to the disadvantages that the product α-hydroxyisobutyramide is obtained in low yield with unsatisfactory reaction achievement and catalyst activity deteriorates with the elapse of time even in the case of high performance in the initial stage of the reaction, thereby lowering the yield of the product. The present inventors have already found that the catalyst comprising, as the essential component, manganese dioxide prepared under specific conditions (hereinafter referred to as "modified manganese catalyst") is effective and such catalyst has been disclosed in Japanese Patent Application Laid-Open No.93761/1991. Although the modified manganese catalyst prepared under the specific conditions has an extremely high activity and a long service life, it has been proved that the use thereof as a fixed-bed catalyst in a solid-liquid contact reaction process causes white crystal to deposit at the inlet and on the downstream side of catalyst packing section from the start of the reaction to the relatively initial stage thereof depending upon the reaction condition, thus raising the trouble of clogging the catalyst bed. SUMMARY OF THE INVENTION It is an object of the present invention to provide a method of solving such trouble of clogging in the catalyst bed when the modified manganese catalyst is used in the bed. Under such circumstances, intensive research and investigation were made by the present inventors in order to solve the clogging trouble in the aforesaid catalyst bed. As a result, it has been found by the present inventors that the white crystal which was deposited in the beginning of the synthetic reaction of acetone cyanohydrin with water into α-hydroxyisobutyramide in the presence of the modified manganese catalyst was sparingly soluble in water and organic solvents and that it was oxamide. It was thought that the oxamide was formed through the steps wherein acetone cyanohydrin is decomposed to form hydrogen cyanide, which is oxidized into dicyanides, followed by further hydration. As a result of further investigation continued by the present inventors on the basis of the above-mentioned finding and information, it has been discovered that the by-production of the white crystal can be suppressed and thus the clogging trouble can be eliminated by adopting a method which comprises pretreating the modified manganese catalyst with a reducing liquid prior to the start of the reaction, thereby weakening only the oxidation capability of the catalyst, while preserving the hydration capacity thereof as it is. The above-mentioned discovery led to success in accomplishing the present invention. Specifically the present invention relates to a process for producing α-hydroxyisobutyramide by hydration reaction of acetone cyanohydrin in the presence of a catalyst consisting essentially of manganese dioxide which process comprises treating said catalyst in advance with a reducing liquid. DESCRIPTION OF PREFERRED EMBODIMENT In the following, the specific embodiment to carry out the present invention will be described. As the reaction method in the present invention, there is applied continuous flow reaction method using fixed-bed catalyst which is well suited to industrial mass production. The modified manganese catalyst to be used as the fixed-bed catalyst is applied in lump or in the form of molding by tabletting or extrusion. The pretreatment of the modified manganese catalyst by means of a reducing liquid according to the present invention can be put into practice separately prior to its packing in a reactor, but is preferably carried out after its packing in the reactor and prior to feeding a starting raw liquid from the industrial standpoint. As the reducing liquid, that is, the pretreating agent in the present invention, there is effectively usable a reductive substance exemplified by an alcohol such as methanol, ethanol and propanol; an aldehyde such as formaldehyde, acetaldehyde and propionaldehyde; a ketone such as acetone and methyl ethyl ketone; formic acid; and hydrogen peroxide. The above-exemplified reducing liquid can be employed alone or in combination with at least one other reducing liquid. The reducing liquid can be employed in the form of aqueous solution, if necessary. The pretreating temperature with the reducing liquid according to the present invention is usually in the range of room temperature to 80°C but should be determined in accordance with the kind and concentration of the reducing liquid to be employed. The pretreating time with the reducing liquid is not specifically limited but is preferably in the range of 0.1 to 48 hours from the viewpoint of industrial practice. The hydration reaction temperature of acetone cyanohydrin according to the present invention is in the range of 30 to 100°C, preferably 40 to 80°C. A reaction temperature lower than 30°C undesirably lowers the rate of the reaction, whereas that higher than 100°C unfavorably increases the by-products due to the decomposition of the acetone cyanohydrin. The reaction pressure is preferably selected so as to maintain the reaction system in liquid phase usually in the range of atmospheric pressure to not higher than 2 kg/cm 2 G, taking into consideration the hydration reaction being liquid-phase reaction. The hydration reaction according to the present invention is put into practice in the reaction system containing usually an excess of water. The content of acetone cyanohydrin in the starting raw liquid is 10 to 60%, preferably 20 to 50% by weight. The presence of acetone in the starting raw liquid in an amount of 5 to 30% by weight is effective in that the decomposition of the acetone cyanohydrin as the side reaction is suppressed thereby, resulting in an increase in the yield of the α-hydroxyisobutyramide as the objective product. The process according to the present invention can suppress the byproduction of oxamide and thereby eliminate the clogging in the catalyst bed by pretreating the catalyst consisting essentially of manganese dioxide in advance with the reducing agent in the synthetic reaction of acetone cyanohydrin with water into the objective α-hydroxyisobutyramide in the presence of the catalyst, thus rendering itself extremely significant from the industrial standpoint. In the following, the present invention will be described in more detail with reference to examples and a comparative example, which however, are not to be construed to limit the invention thereto. Example 1 1)Preparation of catalyst : To a solution of 66.4g of potassium permanganate in 580g of water was promptly added at 70°C, a mixture of 138.7g of aqueous solution of manganese sulfate containing 14% by weight of Mn, 2.91g of stannous sulfate, 23.9g of conc. sulfuric acid and 20g of water. The resultant precipitate was aged at 90°C for 3 hours and then filtered. The resultant cake was washed with one (1) liter of water four times and was dried overnight at 110°C to provide 68.2g of modified manganese dioxide. 2)Pretreatment : A jacketed pyrex-made tubular reactor having 10mm inside diameter and 20cm length was packed with 4g of the catalyst consisting of the modified manganese dioxide which had been obtained in the preceding item 1) and arranged to 30 to 60 mesh by crushing, and warm water at 50°C was allowed to pass through the jacket. Subsequently 20% by weight of aqueous solution of acetone was fed to the catalyst thus packed at a rate of 4g/hour for 12 hours. 3)Reaction : A mixed starting raw solution containing 40g of acetone cyanohydrin, 50g of water and 10g of acetone was fed to the reactor at the upper part thereof at a feed rate of 5g/hour. A measurement was made of the concentration of oxamide in the reaction liquid every 0.5 hour. As the result, the concentration reached the maximum value of 500 ppm after two hours from the start of the reaction and thereafter gradually decreased as low as 30 ppm after 5 hours. Deposit of white crystal was not observed in catalyst-packed bed throughout the reaction. In addition, the reaction solution was collected and analyzed after 5 hours from the start of the reation. As the result, the objective α-hydroxyisobutyramide was obtained in 95% yield. Thereafter, long-term stable reaction was possible to continue with stabilized catalyst performance. Comparative Example 1 The procedure in Example 1 was repeated except that the pretreatment by the use of 20% by weight of aqueous solution of acetone was omitted. As a result, white crystal began to deposit in the catalyst-packed part after about one (1) hour from the start of the reaction, the reaction solution was made non-smooth to pass through the reactor after 3 hours and finally the reaction was made impossible to continue after 5 hours. In addition, measurements were made of the solubilities of oxamide in water and the reaction solution, respectively at 50°C. As the result, it was proved that oxamide in a concentration of 1,000 ppm or higher caused its crystal to deposit, thus failing to dissolve completely. Accordingly, it was presumed that oxamide in a concentration of 1,000 ppm or higher had been produced in the procedure of Comparative Example 1. Examples 2 to 5 The procedure of Example 1 was repeated except that the pretreatment was carried out by the use of a reducing liquid other than aqueous solution of acetone. Table 1 gives oxamide concentration in the reaction solution after 2 hours from the start of the reaction as well as the yield of the objective α-hydroxyisobutyramide after 5 hours therefrom. It was possible in any of the examples 2 to 5 to continue long-term stable reaction after 5 hours and thereafter with stabilized catalyst performance.

Claims: A process for producing α-hydroxyisobutyramide by hydration reaction of acetone cyanohydrin in the presence of a catalyst consisting essentially of manganese dioxide which process comprises treating said catalyst in advance with a reducing liquid. The process according to Claim 1 wherein the reducing liquid is at least one member selected from the group consisting of an alcohol, an aldehyde and a ketone. The process according to Claim 1 wherein the reducing liquid is the aqueous solution of at least one member selected from the group consisting of an alcohol, an aldehyde and a ketone. The process according to Claim 1 or 2 wherein the reducing liquid is at least one member selected from the group consisting of methanol, formaldehyde, acetaldehyde and acetone. The process according to Claim 1 wherein the reducing liquid is formic acid or the aqueous solution of formic acid. The process according to Claim 1 wherein the reducing liquid is the aqueous solution of hydrogen peroxide. The process according to Claim 1 wherein said acetone cyanohydrin is contained in an amount of 10 to 60% by weight and acetone is contained in an amount of 5 to 30% by weight in the starting material. The process according to Claim 1 wherein said catalyst is packed in a reactor for the hydration reaction of acetone cyanohydrin and thereafter is pretreated with a reducing liquid. The process according to Claim 1 wherein said catalyst is pretreated with a reducing liquid at a pretreatment temperature in the range of room temperature to 80°C. The process according to Claim 1 wherein said catalyst is pretreated with a reducing liquid for a pretreatment time in the range of 0.1 to 48 hours. The process according to Claim 1 wherein said catalyst is pretreated with a reducing liquid under a pressure which maintains the reaction system in liquid-phase.

Inventors: HIGUCHI HIROFUMI, UCHIYAMA TAKAKO, HIGUCHI, HIROFUMI, UCHIYAMA, TAKAKO, HIGUCHI, HIROFUMI C/O MITSUBISHI GAS CHEMICAL, UCHIYAMA, TAKAKO C/O MITSUBISHI GAS CHEMICAL
Applicants: MITSUBISHI GAS CHEMICAL CO, MITSUBISHI GAS CHEMICAL COMPANY, INC.
Application year: 1993
Main classification: C07C231
IPC codes: C07B61, B01J23, B01J37, C07C231, C07C235