Flame retardant compositions

Abstract: A composition comprising: (a) polyethylene having a density equal to or less than 0.915 gram per cubic centimeter grafted with an unsaturated aliphatic diacid anhydride; and (b) magnesium hydroxide, the surface of which is untreated.

Description: This invention relates to flame retardant compositions containing an ethylene copolymer and a magnesium hydroxide filler. The compositions are useful in the insulation and jacketing of electrical conductors and communications media such as fiber optics cable. Wire and cable, whether used for the transmission of power or communications, are usually stored outside or in unheated areas before installation. If the insulation or jacketing becomes brittle at low temperatures and cracks, the integrity of the wire or cable is defeated and a short circuit with its attendant problems becomes a real possibility. Consequently, the specifications for the insulating or jacketing layers generally require that these materials pass a low temperature brittleness test. Low temperature performance of minus 50°C or higher is often cited by wire and cable manufacturers as desirable, particularly for installations in, for example, Canada. A typical power cable is constructed of metal conductors insulated with a polymeric material. These elements are generally twisted to form a core and are protected by another polymeric sheath or jacket material. In certain cases, added protection is afforded by inserting a wrap between the core and the sheath. Flame retardant compositions comprising polyethylene and magnesium hydroxide are useful in wire and cable applications, the polyethylene providing flexibility and the magnesium hydroxide, flame retardance. Unfortunately, these compositions do not come close to meeting the most desirable low temperature performance as far as brittleness is concerned. It is difficult, for example, to achieve a low temperature brittleness of O°C with a linear low density polyethylene flame retardant composition, let alone the desirable minus 50°C. An object of this invention, therefore, is to provide a flame retardant composition, which has outstanding low temperature brittleness resistance, thus being useful in the coldest of climes. Other objects and advantages will become apparent hereinafter. According to the present invention the above object is met by a composition comprising: (a) polyethylene having a density equal to or less than 0.915 gram per cubic centimeter grafted with an unsaturated aliphatic diacid anhydride; and (b) magnesium hydroxide, the surface of which is untreated. The polyethylene is a very low density polyethylene (VLDPE). The VLDPE is a copolymer of ethylene and at least one alpha-olefin having 3 to 12 carbon atoms and preferably 3 to 8 carbon atoms. The density of the copolymer is equal to or less than 0.915 gram per cubic centimeter and is preferably no lower than 0.860 gram per cubic centimeter. It can be produced, for example, in the presence of (i) a catalyst containing chromium and titanium, (ii) a catalyst containing magnesium, titanium, a halogen, and an electron donor; or (iii) a catalyst containing vanadium, an electron donor, an alkyl aluminum halide modifier, and a halocarbon promoter. The catalysts and the processes for making the VLDPE are described, respectively, in United States patents 4,101,445 and 4,302,565 and European patent application 0 120 501 published on October 3, 1984. EP-A-0 370 517 relates to a composition comprising a thermoplastic resin, an inorganic flame retardant, a copolymer of ethylene and either 1-hexene or 1-octene, wherein said copolymer has been modified with an unsaturated organic compound containing at least one carboxylate group and, optionally, a copolymer of ethylene and one or more alpha-olefins having a crystallinity of less than about 40 percent by weight. DE-38 13 200 relates to a thermoplastically processable plastic composition on the basis of modified polyethylenes for electrical cables and wires consisting of a polyethylene having a specific density of below 0.91 g/cm 3 (VLDPE) and fillers in larger amounts. JP-A-62 280 242 relates to a polyethylene resin composition comprising 20 to 70% by wt. of a LLDPE having ethylene and 6C alpha-olefin units and 80 to 30% by wt. Mg(OH) 2 with a mean particle diameter of 2.2-8.0 µm. The composition has a good flame retardancy, good mechanical properties and low temperature brittleness and does not generate toxic gases when burned. The melt index of the VLDPE can be in the range of 0.1 to 50 grams per 10 minutes and is preferably in the range of 0.4 to 10 grams per 10 minutes. The melt index is determined in accordance with ASTM D-1238, Condition E, measured at 190°C. Suitable alpha-olefin comonomers are exemplified by propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, and 1-octene. The portion of the VLDPE attributed to the comonomer(s), other than ethylene, is in the range of 1 to 49 percent by weight based on the weight of the copolymer and is preferably in the range of 10 to 40 percent by weight. Anhydrides of unsaturated aliphatic diacids are commonly grafted to various polyolefins. These anhydrides can have 4 to 20 carbon atoms and preferably have 4 to 10 carbon atoms. Examples of anhydrides, which are useful in this invention, are maleic anhydride, itaconic anhydride, and nadic anhydride. The preferred anhydride is maleic anhydride. Excess anhydride, if present after grafting, can be removed by devolatilization at temperatures in the range of 200°C to 250°C. The grafting is accomplished by using an organic peroxide catalyst, i.e., a free radical generator, such as dicumyl peroxide; lauroyl peroxide; benzoyl peroxide; tertiary butyl perbenzoate; di(tertiary-butyl) peroxide; cumene hydroperoxide; 2,5-dimethyl-2,5-di(t-butyl- peroxy)hexyne-3; 2,5-dimethyl-2,5-di(t-butyl-peroxy)hexane; tertiary butyl hydroperoxide; isopropyl percarbonate; and alpha,alpha'-bis(tertiary-butylperoxy)diisopropylbenzene. The organic peroxide catalyst may be added together with the anhydride. Grafting temperatures can be in the range of 100 to 300°C and are preferably in the range of 150 to 200°C. A typical procedure for grafting maleic anhydride onto polyethylene is described in United States patent 4,506,056. Grafting can also be accomplished by adding a solution of anhydride, an organic peroxide catalyst, and an organic solvent to polyethylene in particulate form. The organic peroxide catalyst is soluble in the organic solvent. Various organic solvents, which are inert to the reaction, can be used. Examples of useful organic solvents are acetone, methyl ethyl ketone, methyl propyl ketone, 3-pentanone, and other ketones. Other carrier solvents which allow solubilization of peroxide and anhydride, and which strip off well under appropriate devolatilization conditions may be used. Acetone is a preferred solvent because it acts as a stripping agent for residuals such as non-grafted anhydride or anhydride by-products. The anhydride solution can contain 10 to 50 percent by weight anhydride; 0.05 to 5 percent by weight organic peroxide catalyst; and 50 to 90 percent by weight organic solvent based on the total weight of the solution. A preferred solution contains 20 to 40 percent anhydride; 0.1 to 2 percent peroxide; and 60 to 80 percent solvent. The anhydride grafted polyethylene can contain 0.05 to 5 parts by weight of anhydride per 100 parts by weight of polyethylene and preferably contains 0.1 to 2 parts by weight of anhydride per 100 parts by weight of polyethylene. The VLDPE can also be grafted with an unsaturated monomeric silane having one or more hydrolyzable groups in order to make the polymer hydrolyzable thus permitting moisture cure. While such grafting can be accomplished simultaneously with the grafting of the unsaturated aliphatic diacid anhydride, the grafting can also be effected before or after the grafting of the anhydride, if desired. The silane grafted copolymer can be prepared by the technique described below. In this copolymer, the portion attributed to the silane is present in an amount of 0.5 percent to 10 percent by weight based on the weight of the copolymer and is preferably incorporated into the copolymer in an amount of 0.5 to 4 percent by weight. Generally speaking, any unsaturated monomeric silane containing at least one hydrolyzable group can be used. The silane used to modify the copolymer can be, among others, an alkenyl alkoxy silane such as a vinyl trialkoxy silane exemplified by vinyl trimethoxy silane, vinyl triethoxy silane, or vinyl isopropoxy silane. If slower water cure or better shelf stability are desired, vinyl triisobutoxy silane or vinyl tris(2-ethyl-hexoxy) silane can be used. The hydrolyzable silane and anhydride grafted polymer can be crosslinked with moisture in the presence of a conventional silanol condensation catalyst such as dibutyl tin dilaurate, dioctyl tin maleate, stannous acetate, stannous octoate, lead naphthenate, zinc octoate, iron 2-ethyl hexoate, and other metal carboxylates. Further acceleration of crosslinking can be accomplished by adding a cocatalyst such as tetramethoxy titanate, tetraisopropyl titanate, tetramethyl titanate, or other organo titanates mentioned in United States patent 4,446,279. The catalysts can be introduced into the composition in conventional amounts, typically 0.005 to 1 part by weight of primary catalyst per 100 parts by weight of copolymer and 0.25 to 10 parts by weight of cocatalyst per 100 parts by weight of copolymer. A typical procedure for preparing a silane grafted polyethylene follows: 100 parts of ethylene/1-butene copolymer having a density of 0.90, 0.2 part of polymerized 1,3-dihydro-2,2,4-trimethyl-quinoline (an antioxidant), 0.1 part of dicumyl peroxide, and 4 parts of vinyl tri-2-ethyl-hexoxy silane are mixed in a Brabender mixer at a temperature in the range of 80°C to 115°C, a temperature low enough to keep the dicumyl peroxide below its decomposition temperature. After mixing for five minutes, the temperature is raised to a temperature in the range of 150°C to 220°C. The batch is then mixed for 5 to 10 minutes during which grafting of the silane to the copolymer occurs. The antioxidant is used as a radical trap to control the amount of crosslinking. The foregoing technique can be repeated, for example, with 3 parts of vinyltriisobutyoxysilane and 0.1 part of the antioxidant, tetrakis[methylene(3-5-di-tert-butyl-4-hydroxyhydrocinnamate)]methane; initial mixing is in the range of 110°C to 120°C; grafting is for five minutes at 185°C. Various processes for preparing silane grafted polymers and numerous unsaturated silanes suitable for use in preparing these polymers and bearing hydrolyzable groups such as alkoxy, oxyaryl, oxyaliphatic, and halogen are mentioned in United States patents 3,075,948; 3,225,018; 4,412,042; 4,413,066; 4,574,133; and 4,593,071. It will be noted that the same organic peroxide catalyst is used in silane grafting as in anhydride grafting. The magnesium hydroxide is one conventionally used in wire and cable applications except that it is not surface treated. This means that the surface of the magnesium hydroxide is not treated or coated with a chemical no matter whether the chemical will react with the surface or not, nor are the usual surface treating agents such as carboxylic acids or salts thereof used in the composition into which the magnesium hydroxide is introduced. It will be understood by those skilled in the art that once the magnesium hydroxide is mixed into the cable composition, it will then be coated with the mixture of resin and other additives. A preferred magnesium hydroxide has the following characteristics: (a) a strain in the <101> direction of no more than 3.0 x 10 -3 ; (b) a crystallite size in the <101> direction of more than 800 angstroms; and (c) a surface area, determined by the BET method, of less than 20 square meters per gram. The preferred magnesium hydroxide and a method for its preparation are disclosed in United States patent 4,098,762. A preferred characteristic of the magnesium hydroxide is that the surface area, as determined by the BET method, is less than 10 square meters per gram. The amount of magnesium hydroxide used in the composition can be in the range of 100 to 1200 parts by weight of magnesium hydroxide per one hundred parts by weight of anhydride grafted polyethylene and is preferably in the range of 100 to 180 parts by weight of magnesium hydroxide per one hundred parts by weight of anhydride grafted polyethylene, 120 to 160 parts being the optimum. Unmodified polyethylenes including VLDPE, linear low density polyethylenes, and other unmodified polyethylenes of varying densities up to 0.965 gram per cubic centimeter can be introduced into the composition of the invention, if desired, with some sacrifice in low temperature brittleness as the amount of unmodified polyethylene increases. Based on 100 parts by weight of modified polyethylene, the unmodified polyethylene can be introduced in a range of 0 to 750 parts by weight, preferably no more than about 325 parts by weight, but the closer to zero unmodified polyethylene, the better. Various conventional additives can be added in conventional amounts to the composition of the invention. Typical additives are antioxidants, ultraviolet absorbers, antistatic agents, pigments, dyes, other fillers including carbon black and aluminum silicate, slip agents, fire retardants, stabilizers, crosslinking agents, halogen scavengers, smoke inhibitors, crosslinking boosters, processing aids, lubricants, plasticizers, and viscosity control agents. The invention is illustrated by the following examples. EXAMPLES 1 to 4 Polyethylene I is an unmodified linear low density polyethylene, which is a copolymer of ethylene and 1-hexene having a density of 0.917 gram per cubic centimeter and a melt index of 3.4 grams per 10 minutes for comparison. Polyethylene II is a maleinized VLDPE, which is a copolymer of ethylene and 1-butene having a density of 0.900 gram per cubic centimeter and a melt index of 0.4 grams per 10 minutes. The VLDPE is grafted with 0.3 part by weight maleic anhydride per 100 parts by weight of VLDPE according to the procedure mentioned above. The magnesium hydroxide used in the examples falls within the definition of the preferred magnesium hydroxide mentioned above, and is not surface treated. The antioxidant is tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)]methane. Four compositions are processed into test specimens as required by the test procedure for low temperature brittleness (LTB), i.e. ASTM D-746-73 and the test procedure is carried out. LTB is reported in degrees Centigrade. Variables and results are reported in the Table. EXAMPLE 1 comp. 2 3 4 Formulation (in parts by weight): Polyethylene I 100 88 76 - Polyethylene II - 12 24 100 Magnesium Hydroxide 139.4 139.4 139.4 139.4 Antioxidant 1 1 1 1 Results: LTB (°C) +18 -12.5 -31.5 -45 NOTE TO TABLE: Example 4 in which the resin is 100 percent maleinized VLDPE and the magnesium hydroxide is not surface treated results in an LTB of minus 45°C.

Claims: A composition comprising: (a) polyethylene having a density equal to or less than 0.915 gram per cubic centimeter grafted with an unsaturated aliphatic diacid anhydride; and (b) magnesium hydroxide, the surface of which is untreated. The composition defined in claim 1 wherein the anhydride is maleic anhydride. The composition defined in claim 1 or 2 wherein the polyethylene is additionally grafted with a hydrolyzable unsaturated monomeric silane. The composition defined in any one of claims 1 - 3 wherein the magnesium hydroxide has the following characteristics: (a) a strain in the <101> direction of not more than 3.0 x 10 -3 ; (b) a crystallite size in the <101> direction of more than 800 angstroms; and (c) a surface area, determined by the BET method, of less than 20 square meters per gram. The composition defined in any one of claims 1 - 4 wherein the magnesium hydroxide is present in an amount of 100 to 1200 parts by weight of magnesium hydroxide per 100 parts by weight of anhydride grafted polyethylene. The composition defined in any one of claims 1 - 5 wherein the composition additionally contains polyethylene, which is not grafted with an unsaturated aliphatic diacid anhydride, in an amount of up to 750 parts by weight based on 100 parts by weight of anhydride grafted polyethylene. The composition defined in any one of claims 1 - 6 wherein the anhydride grafted polyethylene contains 0.05 to 5 parts by weight of anhydride per 100 parts by weight of polyethylene. A composition comprising: (a) polyethylene having a density in the range of 0.860 to 0.915 gram per cubic centimeter grafted with maleic anhydride in an amount of 0.1 to 2 parts by weight of maleic anhydride per 100 parts by weight of polyethylene; and (b) 100 to 180 parts by weight of magnesium hydroxide per 100 parts by weight of anhydride grafted polyethylene wherein the magnesium hydroxide has the following characteristics: (i) a strain in the <101> direction of not more than 3.0 x 10 -3 ; (ii) a crystallite size in the <101> direction of more than 800 angstroms; and (iii) a surface area, determined by the BET method, of less than 10 square meters per gram, the surface of which is untreated. An article of manufacture comprising an electrical conductor or communications medium surrounded by one or more layers of the composition defined in any one of claims 1 - 8. The article of manufacture defined in claim 9 wherein one or more glass fibers are surrounded by one or more layers of the composition defined in any one of claims 1 - 8.

Inventors: JOW KINDER, KEOGH MICHAEL JOHN, JOW, KINDER, KEOGH, MICHAEL JOHN
Applicants: UNION CARBIDE CHEM PLASTIC, UNION CARBIDE CHEMICALS & PLASTICS TECHNOLOGY CORPORATION
Application year: 1993
Main classification: C08K3
IPC codes: C08K3