Process for preparing crosslinked methacrylic anhydride copolymers

Abstract: The present invention provides crosslinked, spherical copolymer beads of methacrylic anhydride which are suitable as precursors for weak-acid and other ion exchange resins, affinity chromatography materials and other materials which require spherical polymers having reactive anhydride groups for their preparation. The present invention also provides a process for making such copolymers.

Description: The present invention is concerned with a process for preparing crosslinked, insoluble copolymers, and more particularly to a process for preparing crosslinked copolymers of methacrylic anhydride suitable for use as adsorbents and ion-exchange resin precursors. Ion-exchange resins prepared by copolymerizing acrylic and methacrylic acids with crosslinking monomers are well known, and are useful as weakly acidic cation exchangers. Because the monomers of these acids are hydrophilic, and water soluble to a significant extent, the copolymers are more difficult to prepare by suspension polymerization than resins made from acrylic and methacrylic esters. The esters are relatively insoluble in water and hydrophobic, and as a result polymerize within the droplets of the oil phase, forming relatively clean beads. The acids, however, tend to polymerize partially within the aqueous suspending phase as well, forming undesirable, aqueous-phase polymer that wastes monomer and interferes with formation of clean copolymer beads. Special techniques must be employed to minimize this tendency of the acid monomers to dissolve in the aqueous phase. One such technique is to add inorganic salts to the aqueous phase, "salting out" the monomer, or reducing its solubility in the resulting brine to the point where it is forced into the oil phase where its polymerization is desired. Not only must the salt be recovered, either for re-use or to permit ecologically responsible disposal of the waste aqueous phase, but it tends to cause the oil-phase droplets to distort during polymerization. This promotes formation of non-spherical copolymer beads, which have unpredictable hydraulic properties and pack poorly in ion-exchange columns. Porous resin beads are particularly advantageous for certain uses, for example as adsorbents or as ion exchangers with rapid kinetic properties. Porosity can be introduced into the beads in a number of different ways; the use of a phase-separating agent to form macroreticular beads, as for example disclosed by Meitzner et al., in US-A-4,221,871, is one common way to generate this porosity. Selection of the phase-separating agent offers some control over the total porosity, the pore sizes and the pore-size distribution in the finished beads. Because methacrylic acid in the oil phase dissolves some water from the aqueous phase, the water reduces the solubility of the total monomer solution in the oil phase, and phase separation occurs in the absence of an introduced phase-separating agent. Consequently the preparation of macroreticular resins from methacrylic acid is simpler, but control over the pore parameters is limited. Anhydrides of acids are known to hydrolyze in the presence of strong acids or bases to form the acids themselves. Anhydride polymers, such as polymers of maleic anhydride, introduce into copolymers reactive sites that may be used for subsequent reactions, such as ion-exchange functionalization, as for example disclosed in US-A-2,988,541 to Semon et al . or US-A-3,871,964 to Hüper et al . Methacrylic anhydride has been disclosed, within a broad disclosure of esters, amides and nitriles of methacrylic acid, as a monomer for preparing copolymers that could then be functionalized as a weakly acidic cation exchanger (US-A-2,324,935 to Kautter), and GB-A-894,391 to Bayer suggests methacrylic anhydride as one of a broad range of olefinically unsaturated carboxylic acids, esters and anhydrides from which copolymer having "a sponge structure" might be made, but no practical preparations of such copolymers are shown. Others, as for example Kraemer et al . in US-A-4,070,348, Lehmann et al . in US-A-3,764,477 and Barnes in US-A-2,308,581, made copolymers of methacrylic anhydride by bulk or precipitation polymerization or reverse-phase, suspension polymerization in which the continuous, suspending phase was an organic rather than an aqueous liquid. Lehmann et al . (above) mentions suspension polymerization as a possibility, but without exemplifying a practical preparation. We have now found a process by which beads of crosslinked, methacrylic anhydride copolymer may be prepared with controlled surface area and particle size, and where porous beads are made, the porosity may also be controlled. These beads are useful as adsorbents, affinity-chromatography materials, ion-exchange resins and precursors of these materials. According to the present invention there is provided a polymerization process, which comprises: (a). suspending, in an aqueous suspending medium, droplets of a monomer mixture comprising (i) methacrylic anhydride in an amount that is at least 50% by weight of the monomers, (ii) one or more crosslinking monomer, and (iii) monomer-soluble, free-radical polymerization initiator; (b). heating the droplets above the decomposition temperature of the polymerization initiator until the monomer mixture has polymerized to form crosslinked, spherical copolymer beads having a particle size of from 10 micrometers to 2 millimeters comprising at least 50% by weight of units formed from methacrylic anhydride and wherein more than 80% of the anhydride groups from the methacrylic anhydride monomer remain unhydrolyzed during the polkymerization; and (c). optionally, separating the copolymer beads from the suspending medium. The beads are preferably polymerized from a mixture comprising at least 50 weight percent methacrylic anhydride and from 0.1 to 50 weight percent polyethylenically unsaturated crosslinking monomer, the percentages being based on the total weight of the monomers. Although other monomers are copolymerized with the methacrylic anhydride to make the copolymer beads of the present invention, the copolymer predominantly comprises units formed from methacrylic anhydride. As used herein, the term, "predominantly" means that the polymer contains at least 50 weight percent of polymerized units formed from the indicated monomer, in this case, methacrylic anhydride. The monomers which are copolymerized with methacrylic anhydride to form the copolymer beads of the present invention comprise at least one polyethylenically unsaturated crosslinking monomer which is preferably present at levels from 0.1 to 50 weight percent of the total monomers. The crosslinking monomer or monomers may be aliphatic, for example acrylic crosslinkers such as ethylene glycol dimethacrylate, ethylene glycol diacrylate, trimethylolpropane di- and triacrylates, trimethylolpropane di- and trimethacrylates, divinylketone, allyl acrylate, diallyl maleate, diallyl fumarate, diallyl succinate, diallyl carbonate, diallyl malonate, diallyl oxalate, diallyl adipate, diallyl sebacate, divinylsebacate, N,N'-methylene diacrylamide, N,N'-methylene dimethacrylamide, and polyvinyl or polyallyl ethers of glycol, of glycerol, of pentaerythritol, of mono- or dithio- derivatives of glycols or resorcinol, or they may be aromatic, for example styrenic crosslinkers such as divinylbenzene, trivinylbenzene, divinyltoluenes, divinylnaphthalenes, diallyl phthalate, divinylxylene, or divinylethylbenzene, or they may be heterocyclic crosslinkers such as divinylpyridine. Such crosslinking monomers are well known to those skilled in the art. In one embodiment of the present invention the crosslinking monomer(s) comprise one or more aliphatic crosslinking monomer selected from ethylene glycol dimethacrylate, ethylene glycol diacrylate, trimethylolpropane diacrylate, trimethylolpropane triacrylate, trimethylolpropane dimethacrylate, trirnethylolpropane trimethacrylate, divinylketone, allyl acrylate, diallyl maleate, diallyl fumarate, diallyl succinate, diallyl carbonate, diallyl malonate, diallyl oxalate, diallyl adipate, diallyl sebacate, divinylsebacate, N,N'-methylene diacrylamide, and N,N'-methylene dimethacrylamide. One or more other monomers may be copolymerized with the methacrylic anhydride. Such other monomers include: other acrylic monomers, such as acrylic and methacrylic acids and their esters, including their esters of C 1 -C 18 alkyl, cycloalkyl, aryl, aralkyl and alkaryl alcohols; other aliphatic monomers such as acrylonitrile and methacrylonitrile, vinyl chloride, vinyl formate, vinyl alkyl ethers such as methylvinyl ether, acrylamide, and methacrylamide; and aromatic monomers such as ethylvinylbenzene, styrene, α-methylstyrene, vinyltoluene, and vinylnaphthalene. Methacrylic anhydride is present at levels of at least 50 weight percent in all monomer mixtures useful for preparing the copolymer beads of the present invention. The copolymer beads of the present invention are prepared by suspension polymerization of a mixture of the monomers which contains at least 50 weight percent methacrylic anhydride. In suspension polymerization the monomer mixture is suspended as droplets in an aqueous suspending medium which optionally contains stabilizing agents and other additives to promote stable, uniformly sized droplets. The reaction is initiated by the generation of free radicals in the monomer mixture. The free radical polymerization of the monomers to produce the copolymers of the present invention may result from thermal decomposition of free-radical-generating initiators such as peroxides, peracid salts, and azo initiators in the presence of the monomers, but may also result from redox initiators such as t -butyl hydroperoxide with sodium formaldehyde hydrosulfite. Preferred for initiating the polymerization is inclusion of a monomer-soluble, thermally unstable initiator in the reaction mixture, and heating, to a temperature above the thermal decomposition point of the initiator, the suspending medium in which the monomer droplets are suspended. Examples of such monomer-soluble, thermally unstable initiators include peroxides and hydroperoxides and related initiators such as benzoyl peroxide, t -butyl hydroperoxide, cumene peroxide, α-cumyl peroxyneodecanoate, tetralin peroxide, acetyl peroxide, caproyl peroxide, t -butyl perbenzoate, t -butyl diperphthalate, di(4- t -butylcyclohexyl)peroxydicarbonate, and methyl ethyl ketone peroxide. Also useful are azo initiators such as azodiisobutyronitrile, azodiisobutyramide, azobis(α,α-dimethylvaleronitrile), azobis(α-methylbutyronitrile) and dimethyl, diethyl or dibutyl azobis(methylvalerate). The peroxide and hydroperoxide initiators are preferably used at a level of from 0.01% to 3% by weight, based on the total weight of the monomer(s), and the azo initiators are preferably used at a level from 0.01% to 2% by weight, based on the total weight of the monomer(s). The preferred initiators are those having a relatively low decomposition point, that is, below 60°C, such as α-cumyl peroxyneodecanoate and di(4- t -butylcyclohexyl)peroxydicarbonate, as these permit polymerization at relatively low temperatures at which the anhydride functionality is less likely to hydrolyze or react with other components present in the reaction. The copolymer beads of the present invention may be gel or macroporous. Preferably, the copolymer beads are macroporous, and preferably contain pores having a diameter from about 5 to 10,000 nm, the pores contributing an internal pore volume to the bead which is at least 5% of the volume of the bead itself (5% pore volume). As a consequence of the porosity, the surface area of the macroporous beads is significantly greater than for gel polymer beads (those which do not contain macroporosity). One method of introducing this macroporosity is disclosed in US-A-4,221,871, to Meitzner et al ., which is mentioned above and which involves introducing to the polymerization reaction mixture a porogen, also known as a precipitant, phase extender and phase-separating agent. The porogen is a good solvent for the monomer but a poor solvent for the polymer, and preferred porogens do not react with the monomer or polymer. Particularly preferred porogens useful in preparing the copolymer beads of the present invention include iso-octane, methyl isobutyl ketone, methyl isobutyl carbinol, xylene, toluene, and di- n -butyl ether. Especially preferred are the more hydrophobic porogens, such as iso-octane and xylene, as they are less likely to promote hydrolysis of the anhydride groups during polymerization. The pore size and surface area of the macroporous polymer beads may be controlled by techniques readily apparent to those skilled in the art, those techniques including the varying of porogen type and concentration, crosslinker type and concentration, initiator type and concentration, polymerization temperature and the like. Other methods of introducing macroporosity into the copolymer beads, which are known to those skilled in the art, may also be used. In one embodiemnt of the process of the present invention, which tends to produce beads having uniform diameter, the monomer mixture is introduced into the suspending medium by jetting it at a controlled rate through one or more orifices of uniform diameter into a moving stream of the suspending medium. The monomer droplets thus formed have a uniform diameter. When the monomer droplets are polymerized, using a free radical initator, by being heated in the suspending medium to a temperature above the decomposition point of the initiator, the resulting copolymer beads retain the particle-size uniformity. These beads may be used as formed, or they may serve as seed beads for growing seed beads to a larger, controlled size. In this alternative process, the introduction of macroporosity to the beads, as described above, remains a preferred embodiment. The size of the beads produced by any of the processes mentioned above may be controlled over the range from 10 µm to 2 mm, more preferably from 50 µm to 1 mm. The adjustment of particle size in suspension polymerization is readily apparent to those skilled in the art, and includes such techniques as varying the interfacial tension at the oil-water interface, varying the viscosity of either or both phases, and varying the speed of agitation. A particular advantage of the present invention is elimination of the need to include in the aqueous suspension medium any inorganic salts or other water-soluble components, for example the aqueous phase inhibitors used to reduce aqueous polymer buildup, in order to reduce the solubility of the monomer in water. As described above, monomer solubility is a particular problem when weak-acid cation-exchange resins are made from methacrylic acid monomer. Because the methacrylic anhydride monomer is relatively insoluble in water, such salts and other water-soluble components need not be present, although their presence does not exclude a process from the present invention as it is most broadly contemplated. Once formed, the copolymer beads of the present invention may be reacted to introduce ion-exchange or chelating functional groups, specific affinity ligands, or any of a wide assortment of hydrophilic or hydrophobic moieties, or combinations of these, to the beads. For example, the copolymer may be functionalized with carboxylic acid functional groups, ammonium salt functional groups, or amine salt functional groups. The anhydride functionality from the methacrylic anhydride monomer is present in the copolymer, is particularly reactive, and provides convenient reaction sites for the attachment of other functional groups. Hydrolysis of the anhydride to weak-acid carboxylic groups is also a route to form cation-exchange functional groups on the copolymer. It should be noted that below 20%, and frequently below about 15%, of the total anhydride groups which theoretically would be present in the copolymer are hydrolyzed to form carboxylic acid groups during the polymerization. Further hydrolysis with acid to form weak-acid carboxylic groups in the hydrogen form, or with an alkali-metal hydroxide to form weak-add carboxylic groups in the alkali-metal form, may be used to increase the weak-acid functionalization. Other examples of the reactions that may be used to create functional groups on the beads, and the resulting functional groups, include reaction with ammonia to form ammonium salts of the carboxylic acid group, and reaction with amines, including primary, secondary and tertiary amines and polyethyleneamines, to form amine salts. Other suitable derivatives of the anhydride polymers include the alkyl or other esters and amides, preferably the C 1 - C 8 alkyl esters and amides, and alkylamides, dialkylamides, arylamides, alkarylamides and alkylamides having amine substitution, prepared by reacting carboxyl groups on the polymer with the appropriate amines or alkyl or phenylalkyl alcohol, as well as amino esters, amino amides, hydroxy amides and hydroxy esters, where the functional groups are separated by alkylene, phenyl, alkyleneamine, alkylene oxide, phenylalkyl, phenylalkylphenyl or alkylphenylalkyl or other aryl groups. Substituents bearing amines or amine salts including quaternary amine salt groups are conveniently formed by reacting the carboxyl groups on the polymer with polyfunctional amines such as dimethylaminoethanol, to form an amide linkage with the polymer, or in certain cases when higher temperatures are employed, to form an imide linkage with a vicinal carboxyl, or reacting the anhydride groups on the polymer with the same polyfunctional amines to form ester linkages with the polymer. Sulfur-containing derivatives may similarly be made by reacting the anhydride group with thiols and thioalcohols. The manner in which such functionalizations of the copolymer beads may be carried out will readily be apparent to those skilled in the art, as will additional functionalities which may be incorporated into the copolymer beads. Hybrid resins may be produced by filling the pores of the macroporous copolymer beads or functionalized resin beads of the present invention with monomer, which may be the same as or different from the monomer used to produce the macroporous beads, polymerizing the monomer, and then functionalizing the newly formed polymer in the pores with a different functionality from that on the beads to produce beads with a dual functionality. Alternatively, the surface of macroporous copolymer beads or functionalized resin beads from the prior art may be coated with, or the pores filled with, the methacrylic anhydride monomer of the present invention, which may then be polymerized to form either a hybrid resin having dual functionality, or a macroreticular bead having a coating of the methacrylic anhydride polymer of the present invention. Advantages offered by this latter structure include control of swelling and diffusion kinetics by choice of the base macroporous polymer, improved chemical stability of the coated beads, and a reduced potential for bead fouling. The present invention further provides an adsorption, ion exchange or affinity chromatography process, which comprises contacting a fluid with crosslinked, spherical copolymer beads prepared by a process according to the present invention, and wherein said crosslinked, spherical copolymer beads have, optionally, been functionalized with functional groups. The present invention still further provides a process for adsorbing proteins onto a copolymer functionalized with functional groups having an affinity for proteins, which comprises contacting the proteins with the functionalized copolymer, wherein the copolymer is a copolymer prepared by a process according to the present invention, and the proteins are in an aqueous suspension. The proteins adsorbed onto the copolymer may, for example, be subsequently removed from the copolymer into a liquid which is different from the aqueous suspension. Preferably, at least 80 weight percent, more preferably at least 90 weight percent, and most preferably at least 95 weight percent, of the proteins adsorbed onto the copolymer are subsequently removed from the copolymer into a liquid which is different from the aqueous suspension. The following Examples are presented to illustrate certain embodiments of the present invention. All percentages and ratios are by weight unless otherwise specified, and all reagents used are of good commercial quality unless otherwise specified. Example 1 The following Example illustrates a preparation of macroporous resin beads of the present invention from methacrylic anhydride. To a 1-liter, 4-neck, round-bottom flask equipped with a stirrer, liquid-cooled condenser and thermocouple probe was charged 462.45 g deionized water, 27.5 g of 2% aqueous hydroxyethylcellulose solution, 9.0 g of 10% aqueous, 98%-hydrolyzed polyvinyl alcohol having a molecular weight of 11,000 - 31,000, and 0.15 g sodium nitrite. The charge was stirred for one hour at 300 rpm. An organic mixture was prepared separately by mixing 12.5 g o-xylene, 4.7 g of 80% divinylbenzene (the remainder being primarily ethylvinylbenzene), 32.8 g methacrylic anhydride (99.5% purity), 0.5 g of a 75% mineral-spirits solution of α-cumyl peroxyneodecanoate and 0.375 g di(4- t -butylcyclohexyl) peroxydicarbonate, and agitating the mixture until the initiators were fully dissolved in the liquid. At the end of the 1-hour stirring period, stirring of the flask charge was continued while the organic mixture was slowly added to the flask. When addition of the organic mixture was complete, the flask contents were heated, with stirring, at 1 C°/minute to 35°C, and then at 0.2 C°/minute to 75°C. The flask contents were held at 75°C, with stirring, for one hour, and then allowed to cool to room temperature. The resulting beads were drained, washed three times with an amount of acetone equal to the bead volume, then allowed to dry in a Buchner funnel with vacuum. After drying, a 25-g sample of the copolymer beads was treated with 120 g of a 50% (wt/wt) aqueous solution of sodium hydroxide and 300 ml deionized water at a temperature of 80-90°C for approximately three hours, and allowed to cool overnight with agitation, to convert the anhydride groups in the copolymer to weak-acid groups in the sodium form. Following this reaction the beads were washed with deionized water, drained and dried. The properties of these beads and those of Examples 2 through 6, below, are shown in Table 1, below. Example 2 This Example illustrates a preparation of macroporous resin beads of the present invention similar to that of Example 1, using the same organic mixture with different suspending agents and a steeper temperature profile to a lower final polymerization temperature. The procedure of Example 1 was repeated except that the initial charge to the flask was 449.15 g deionized water, 0.75 g carboxymethyl-methylcellulose and 0.05 g sodium lauryl sulfate, and the reaction mixture was heated at 1 C°/minute to 60°C and held at that temperature for five hours before allowing it to cool to room temperature. Example 3 This Example illustrates a preparation of macroporous polymer beads of the present invention similar to that of Example 2 using an acrylic crosslinking agent, trimethylolpropane trimethacrylate, in place of the divinylbenzene, and a different organic solvent, methyl isobutyl ketone, in place of the o -xylene. Using the procedure of Example 1, and the initial charge to the flask and the heating schedule of Example 2, polymer beads were prepared using, as the separately prepared organic mixture, 23.0 g methyl isobutyl ketone, 10.0 g trimethylolpropane trimethacrylate, 27.5 g methacrylic anhydride (99.5% purity), 0.5 g of a 75% mineral spirits solution of α-cumyl peroxyneodecanoate and 0.375 g di(4- t -butylcyclohexyl) peroxydicarbonate. Example 4 This Example illustrates yet another preparation of macroporous resin beads of the present invention, using different conditions and reagents. Using the procedure of Example 1, an aqueous mixture of 750 g deionized water, 1.26 g carboxymethylmethylcellulose and 0.09 g pure, powdered sodium lauryl sulfate was prepared in the reaction flask, and to this was added an organic mixture of 50.0 g methyl isobutyl ketone, 30.0 g trimethylolpropane trimethacrylate, 82.5 g methacrylic anhydride (92% purity), 1.0 g of a 75% mineral spirits solution of α-cumyl peroxyneodecanoate and 0.76 g di(4- t -butylcyclohexyl) peroxydicarbonate. The reaction mixture was heated to 50°C at 1 C°/minute, from 50° to 58°C at 0.5 C°/minute, held at 58°C for 1.5 hours, then allowed to cool to room temperature, and resin beads of the present invention were recovered, dried, and post-treated as described in Example 1. A portion of these beads were functionalized with a polyamine to form an anion-exchange resin according to the following procedure. A 0.677-g sample of the dry copolymer beads was transferred to a 1-liter, round-bottom flask and suspended with agitation in 250 g deionized water. In a 500-ml beaker 3.0 g triethylenetetramine (TETA) was suspended in 250 ml deionized water, and the suspended amine was added, dropwise, to the flask containing the copolymer beads. After addition of the amine, the flask contents were heated to 50°C and held at that temperature for five hours, after which they were cooled, washed with deionized water, and dried. Results of particle-size measurements are for these TETA-functionalized beads. Example 5 This Example illustrates another preparation of macroporous resin beads of the present invention, using a different organic mixture. Using the procedure of Example 1, and the aqueous mixture and temperature profile of Example 4, resin beads were prepared using, as an organic mixture, 50.0 g methyl isobutyl ketone, 15.0 g trimethylolpropane trimethacrylate, 97.5 g methacrylic anhydride (92% purity), 1.0 g of a 75% mineral spirits solution of α-cumyl peroxyneodecanoate and 0.76 g di(4- t -butylcyclohexyl) peroxydicarbonate. The copolymer beads were recovered, dried and post-treated according to the procedure of Example 1. After drying, a sample of the copolymer was converted to the TETA form as described in Example 4, and results of the particle-size measurements are for these TETA-functionalized beads. Example 6 This Example illustrates a preparation of macroporous resin beads of the present invention using a low level of the divinylbenzene crosslinker of Examples 1 and 2 with the methyl isobutyl ketone porogen of Examples 3 through 5. Resin beads were prepared using the procedure of Example 1, the aqueous mixture of Examples 4 and 5, and an organic mixture of 30.645 g methyl isobutyl ketone, 2.563 g divinylbenzene (80% purity), 47.95 g methacrylic anhydride (92% purity), 0.665 g of a 75% mineral spirits solution of α-cumyl peroxyneodecanoate and 0.5 g di(4- t -butylcyclohexyl) peroxydicarbonate. The reaction mixture was heated to 50°C at 1 C°/minute, held at 50°C for four hours, and allowed to cool to room temperature. The copolymer beads were recovered, dried and post-treated according to the procedure of Example 1. Cytochrome-c Capacity and Recovery Determination Each of the resins prepared above was tested for its capacity to adsorb and elute the protein, cytochrome-c. For determining the cytochrome-c capacity (i.e. that amount of cytochrome-c which the resin can adsorb from solution per unit volume of resin) a 20-ml, wet sample of each resin was pre-treated by transferring it to a glass chromatographic column having a 2.5-cm internal diameter and a length of at least 20 cm. Free liquid was forced from the column by applying air pressure of 2 x 10 5 N m -2 (2 bars) to the top of the column. The column was then filled with HPLC grade methanol which was similarly forced through the column at a pressure of 2 x 10 5 N m -2 (2 bars); this was repeated until 200 ml of methanol had been forced through the column. The methanol was then forced from the column and 200 ml of purified, deionized water were similarly forced through the column. The water was forced from the column and 200 ml of 0.05 M acetate buffer solution (3.0 g glacial acetic acid in 1000 ml water, adjusted to pH 5.4 with 50% aqueous sodium hydroxide solution) were similarly forced through the column. The exact volumes of approximately 2-ml samples of the resins pretreated as described above were determined, and the samples were diluted with the acetate buffer to a total volume of 80 ml resin plus buffer. Each sample was transferred to a 250-ml container and 20 ml of a 20 mg/ml solution of cytochrome-c (Sigma C-2506; Sigma Chemical Co., St. Louis, MO) in acetate buffer was rapidly added. The container was closed and shaken for 30 minutes, after which the resin was allowed to settle for 5 minutes. The ultraviolet absorbance of the supernatant liquid was determined at 550 nanometers (nm) and compared to that of standard cytochrome-c solutions to determine its free cytochrome-c concentration. The cytochrome-c capacity of the resin was calculated using Formula 1: Capacity = (400-(100 x C s ))/V r where C s is the cytochrome-c concentration (mg/ml) in the supernatant liquid and V r is the volume of the resin sample (ml). Cytochrome-c recovery (i.e. the amount of cytochrome-c adsorbed onto the resin which could be eluted from it) was determined by transferring all of each 2-ml sample from the capacity determination above to a glass chromatographic column having a 1-cm internal diameter and rinsing it with 4-5 ml of the acetate buffer to remove as much of the remaining cytochrome-c solution as possible. Exactly 100.0 ml of 0.5 M sodium chloride solution in acetate buffer was then passed through each resin sample at a rate of 1 ml/minute, and the ultraviolet absorbance of the collected sodium chloride solution was determined at 550 nm. The free cytochrome-c concentration in the sodium chloride solution was determined as above by comparing it to the standard solutions, and the recovery for the resin was calculated from Formula 2: Recovery (%) = (100 x C r )/(V r x Capacity) where C r is the concentration (mg/ml) of cytochrome-c in the sodium chloride solution, Capacity is the cytochrome-c capacity of the resin as calculated by Formula 1, and Vr is the volume of the resin sample, as described above. The results of both of these determinations for the resins of Examples 1 through 6 are shown below in Table 1. Also shown in Table 1, below, are the results of streptomycin-capacity determinations on the copolymers of Examples 4, 5 and 6; results are given in streptomycin activity units per milliliter of wet resin. Each milligram of streptomycin sulfate is approximately equal to 767 streptomycin activity units. In Table 1, below, comparative results are also shown for two different ground and classified, weak-acid, macroporous, methacrylic acid-divinylbenzene resins of the prior art, one (Comparative Example A) having a particle size distribution in the range of 150 to 300 µm and the other (Comparative Example B) having a particle size distribution in the range of 75 to 105 µm. Example Particle Size (µm) CEC (meq/g) Cyto-C Capacity (mg/ml) Cyto-C Recovery (%) Strep Recovery (StrepUnits) 1 - - 72 91 - 2 277 6.86 144 82 - 3 202 5.48 157 98 - 4 160 6.95-7.72 19 85 305 5 160 8.73-9.17 44 81 251 6 500 6.9 - - 101 A 150-300 11.7 82 100 B 75-150 10.3 11 87 As may be seen from the above Examples 1-6 and the results shown in Table 1, the cation-exchange capacity of the resins of the present invention is satisfactory for many purposes, the capacity and recovery for proteins such as cytochrome-c and streptomycin ranges from good to excellent, and the resins themselves may be prepared without the need for elaborate procedures involving salting-out and the like to eliminate monomer solubility problems. Example 7 This Example illustrates preparation of a gel resin of the present invention using the suspension aids of Example 2, and omitting the porogen. An aqueous phase was prepared by mixing 958.47 g deionized water,1.44 g carboxymethyl-methyl cellulose, and 0.0864 g sodium lauryl sulfate in a 2-liter, round-bottom flask until the solid materials dissolved. A separate organic phase was prepared by mixing 88.87 g commercial divinylbenzene (55% purity), 163.97 g methacrylic anhydride (94% purity), 4.8 g di(4- t -butylcyclohexyl)peroxydicarbonate initiator and 3.2 g α-cumyl peroxyneodecanoate initiator until the initiators dissolved. The organic phase was added to the aqueous phase with stirring, to form a suspension of organic droplets in the aqueous phase. The mixture was heated from 25 to 60°C at 0.5C°/min and held at 60°C for four hours; because of an exotherm, the temperature rose to 65°C for 20 minutes. At the end of the reaction period the flask contents were cooled, the solid material was separated from the liquid in a Buchner funnel, and the solid material was washed with acetone. This solid material was in the form of non-porous, or gel, copolymer beads.

Claims: A polymerization process, which comprises: (a). suspending, in an aqueous suspending medium, droplets of a monomer mixture comprising (i) methacrylic anhydride in an amount that is at least 50% by weight of the monomers, (ii) one or more crosslinking monomer, and (iii) monomer-soluble, free-radical polymerization initiator; (b). heating the droplets above the decomposition temperature of the polymerization initiator until the monomer mixture has polymerized to form crosslinked, spherical copolymer beads having a particle size of from 10 micrometers to 2 millimeters, and wherein the copolymer comprises at least 50% by weight of units formed from methacrylic anhydride and more than 80% of the anhydride groups from the methacrylic anhydride monomer remain unhydrolyzed during the polymerization; and (c). optionally, separating the copolymer beads from the suspending medium. A process as claimed in claim 1, wherein the beads have a diameter of from 50 micrometers to 1 millimeter. A process as claimed in claim 1 or claim 2, wherein the beads are macroporous. A process as claimed in claim 3, wherein the monomer mixture further comprises a porogen. A process as claimed in claim 4, wherein the porogen is selected from iso-octane, methyl isobutyl ketone, methyl isobutyl carbinol, xylene, toluene and di- n -butyl ether. A process as claimed in any of claims 3 to 5, wherein the beads contain pores having diameters from 5 to 10,000 nanometers which contribute an internal pore volume to the beads which is at least 5% of the volume of the beads. A process as claimed in claim 1 or claim 2, wherein the beads are gel beads. A process as claimed in any preceding claim, wherein the crosslinking monomer comprises one or more aliphatic, polyethylenically unsaturated monomer. A process as claimed in claim 8, wherein the aliphatic crosslinking monomer(s) is/are selected from ethylene glycol dimethacrylate, ethylene glycol diacrylate, trimethylolpropane diacrylate, trimethylolpropane triacrylate, trimethylolpropane dimethacrylate, trimethylolpropane trimethacrylate, divinylketone, allyl acrylate, diallyl maleate, diallyl fumarate, diallyl succinate, diallyl carbonate, diallyl malonate, diallyl oxalate, diallyl adipate, diallyl sebacate, divinylsebacate, N,N'-methylene diacrylamide, and N,N'-methylene dimethacrylamide. A process as claimed in any of claims 1 to 7, wherein the crosslinking monomer comprises one or more aromatic crosslinking monomer. A process as claimed in claim 10, wherein the aromatic crosslinking monomer(s) is/are selected from divinylbenzene, trivinylbenzene, divinyltoluenes, divinylnaphthalenes, diallyl phthalate, divinylxylene, and divinylethylbenzene. A process as claimed in any preceding claim, wherein the polymerization initiator is a peroxide initiator or a hydroperoxide initiator. A process as claimed in claim 12, wherein the peroxide or hydroperoxide polymerization initiator is selected from benzoyl peroxide, t -butyl hydroperoxide, cumene peroxide, α-cumyl peroxyneodecanoate, tetralin peroxide, acetyl peroxide, caproyl peroxide, t -butyl perbenzoate, t -butyl diperphthalate, di(4- t -butylcyclohexyl)peroxydicarbonate, and methyl ethyl ketone peroxide. A process as claimed in claim 12 or claim 13, wherein the peroxide initiator or hydroperoxide initiator is present at a level of from 0.01 percent to 3 percent, by weight, based on the total weight of the monomers. A process as claimed in any of claims 1 to 11, wherein the polymerization initiator is an azo initiator. A process as claimed in claim 15, wherein the azo polymerization initiator is selected from azodiisobutyronitrile, azodiisobutyramide, azobis(α,α-dimethylvaleronitrile), azobis(α-methylbutyronitrile), dimethyl azobis(methylvalerate), diethyl azobis(methylvalerate), and dibutyl azobis(methylvalerate). A process as claimed in claim 15 or claim 16, wherein the azo polymerization initiator is present at from 0.01 percent to 2 percent, by weight, based on the total weight of the monomers. A process as claimed in any preceding claim, wherein the polymerization initiator has a decomposition point below 60°C. A process as claimed in any preceding claim, wherein the copolymer is functionalized with: (i) carboxylic acid functional groups; (ii) ammonium salt functional groups; or (iii) amine salt functional groups. Use of crosslinked, spherical copolymer beads prepared by a process as claimed in any of claims 1 to 18, and which have optionally been functionalized with functional groups, in an adsorption, ion exchange or affinity chromatography process in which a fluid is contacted with the copolymer beads. Use as claimed in claim 20, wherein the crosslinked copolymer beads have been functionalized with (i) carboxylic acid functional groups, (ii) ammonium salt functional groups, or (iii) amine salt functional groups. Use of crosslinked, spherical copolymer beads prepared by a process as claimed in any of claims 1 to 18, and which have been functionalized wiuth functional groups, for adsorbing proteins, the proteins being in an aqueous suspension and being contacted with the functionalized copolymer beads. Use as claimed in claim 22, wherein the crosslinked copolymer beads have been functionalized with (i) carboxylic acid functional groups, (ii) ammonium salt functional groups, or (iii) amine salt functional groups. Use as claimed in claim 22 or claim 23, wherein proteins adsorbed onto the copolymer are subsequently removed from the copolymer into a liquid which is different from the aqueous suspension. Use as claimed in claim 24, wherein at least 80 weight percent of the proteins adsorbed onto the copolymer are subsequently removed from the copolymer into a liquid which is different from the aqueous suspension.

Inventors: STEFFIER LARRY WAYNE, STEFFIER, LARRY WAYNE
Applicants: ROHM & HAAS, ROHM AND HAAS COMPANY
Application year: 1993
Main classification: C08F220
IPC codes: C08F265, C08F2, B01D15, C08F220, B01J43, B01J20, B01J39, C08F8, C08J3, C08F20, C08J9