A diazo based imaging element having improved storage stability

Abstract: According to the present invention the storage stability of a diazo based imaging element can be improved by controlling the amount of free water in the imaging element. Thus the present invention provides an imaging element comprising on a support a hydrophilic layer containing a hydrophilic (co)polymer or (co)polymer mixture and having been hardened with a hydrolysed tetraalkyl orthosilicate and a light sensitive layer containing a diazo resin or a diazonium salt characterized in that the total amount of free water in said imaging element satisfies the following formula (I): FW (g/m²) ≦ 0.0043 * WS (g/m²) + 0.46 (g/m²) (I) wherein FW represents the amount of free water and WS represents the weight of the support of the imaging element.

Description: 1. Field of the invention. The present invention relates to a diazo sensitized imaging element which is developable by plain water to a lithographic printing plate. 2. Background of the invention. Lithography is the process of printing from specially prepared surfaces, some areas of which are capable of accepting lithographic ink, whereas other areas, when moistened with water, will not accept the ink. The areas which accept ink form the printing image areas and the ink-rejecting areas form the background areas. In the art of photolithography, a photographic material is made imagewise receptive to oily or greasy inks in the photo-exposed (negative-working) or in the non-exposed areas (positive-working) on a hydrophilic background. In the production of common lithographic printing plates, also called surface litho plates or planographic printing plates, a support that has affinity to water or obtains such affinity by chemical treatment is coated with a thin layer of a photosensitive composition. Coatings for that purpose include light-sensitive polymer layers containing diazo compounds, dichromate-sensitized hydrophilic colloids and a large variety of synthetic photopolymers. Particularly diazo-sensitized systems are widely used. These systems have been extensively reviewed by Kosar J. in "Light-Sensitive Systems", Wiley, New York, 1965, Chapter 7. A generally used negative-working diazo-sensitized system is based on the capability of diazo compounds to harden a polymer when exposed to ultraviolet and blue radiation. Diazo compounds which have been used for the preparation of lithographic printing plates based on their hardening properties are e.g. diazonium salts whose photolysis products can harden polymers (natural colloids or synthetic resins) directly and diazonium polymers. Although polymers containing diazonium groups have a large structure they remain water soluble owing to the presence of the ionic diazonium groups. When these groups are destroyed by exposure to light an insoluble resin is formed. Particularly useful diazonium polymers are the condensation products of a carbonyl compound, e.g. an aldehyde, such as formaldehyde, with a diazonium salt of e.g. a p-aminodiphenylamine. These condensation products are usually designated diazo resins. In these systems a polymeric binder is optionally added to the diazo resin coating. Several types of supports can be used for the manufacturing of a diazo-sensitized lithographic printing plate. Common supports are metal supports like Al or Zn, polyester film supports and paper bases. These supports, if not sufficient hydrophilic by themselves, are first coated with a hydrophilic layer to form the hydrophilic background of the printing plate and a top layer containing the diazo compound is then applied (see for example DE-P-1900469, DE-P-2030634 and US-P-3971660). It is known to use as hydrophilic layer in these systems a layer containing polyvinyl alcohol and hydrolyzed tetraethyl orthosilicate and preferably also silicium dioxide and/or titanium dioxide as described in e.g. GB-1064100, GB-P-1419512, FR-P-2300354, US-P-3971660 and 4284705. This hydrophilic layer is overcoated with a light-sensitive layer containing a diazonium salt or a diazo resin in a polymeric binder. Upon image-wise exposure of the light-sensitive layer the exposed image areas become water insoluble and the unexposed areas remain water soluble. The plate is then developed with water to remove the diazonium salt or diazo resin in the unexposed areas. Such development may take place by means of plain water as disclosed in e.g. EP-A-132379 EP-A-450199 and EP92203835.1. It has however been found that the lithographic properties of a lithographic printing plate obtained from diazo based imaging elements as disclosed in e.g. EP-A-450199, EP92203835.1 and US-P-3971660 decrease upon storage of the imaging element. DE-4109563 discloses that a silver salt diffusion transfer based printing plate having less than 15% of water has an improved storage stability. 3. Summary of the invention. It is an object of the present invention to provide a diazo based imaging element for producing a lithographic printing plate having an improved storage stability. Other objects will become apparent from the description hereinafter. According to the present invention an imaging element is provided as set out in the claims. According to the present invention there is provided a method for obtaining a lithographic printing plate comprising the steps of image-wise exposing an imaging element as defined above and subsequently removing the light sensitive layer in the non-exposed or insufficiently exposed areas of said imaging element by means of rinsing or washing said imaging element preferably with plain water. 4. Detailed description By controlling the amount of free water in the imaging element in accordance with the present invention the lithographic properties such as printing endurance, ink acceptance by the printing areas and ink repellance by the non-printing areas remain much more stable upon storage of the imaging element before imaging. By the amount of free water in connection with the present invention is meant the amount of water taken up by an imaging element at equilibrium with its environment relative to the amount of water in said imaging element when equilibrated at 35°C and 10% relative humidity (RH). By the weight of the support (WS) is understood the theoretical weight as derived from its density. The amount of free water in an imaging element in accordance with the present invention can be controlled by conditioning the imaging element at a temperature and relative humidity such that the amount of water taken up by the imaging element does not exceed formula (I). A suitable temperature and relative humidity for conditioning the imaging element can be determined by routine experimentation. A suitable conditioning in connection with the present invention is for example a temperature of 25°C and a relative humidity between 30% and 45%. The amount of water in the imaging element can be measured by the generally known methods such as e.g. bv means of an Infrared rays moisture meter, an electroconductivity method, Karl Fisher method etc... Subsequent to the conditioning the imaging element is packaged in a sealed package that is impermeable to water or minimizes the amount of water that can penetrate into the package. Examples of suitable packaging materials are e.g. aluminium foils and laminates thereof, high density polyethylen packaging material, laminates of uniaxial oriented polyethylen films with the orientation perpendicular to each other etc.... The light sensitive layer of an imaging element in connection with the present invention preferably contains a diazonium salt or diazo resin and a hydrophilic binder. A suitable hydrophilic binder is for example pullulan. Pullulan is a polysacharide that is produced by micro-organisms of the Aureobasidium pullulans type (Pullularia pullulans) and that contains maltotriose repeating units connected by a α-1,6 glycosidic bond. Pullulan is generally produced on industrial scale by fermentation of partially hydrolysed starch or by bacterial fermentation of sucrose. Pullulan is commmercially available from e.g. Shodex, Pharmacosmos. Alternatively the light sensitive layer may contain polyvinylacetate hydrolysed to an extent of at least 95% by weight as a binder. Preferably the light sensitive layer further includes a cationic fluor containing surfactant, preferably a perfluorinated surfactant and more preferably a perfluorinated ammonium surfactant. Typical examples of perfluorinated ammonium surfactants are: n.C 8 F 17 SO 2 NH-(CH 2 ) 3 N + (CH 3 ) 3 I - (Fluorad FC 135 from 3M) n.C 9 F 19 SO 2 NH-(CH 2 ) 4 N + (CH 3 ) 3 Br - n.C 7 F 15 CONH-(CH 2 ) 3 N + (CH 3 ) 3 I - (n.C 8 F 17 COO-(CH 2 ) 4 ) 2 N + (CH 3 ) 2 I - Examples of low-molecular weight diazonium salt for use in the present invention include: benzidine tetrazoniumchloride, 3,3'-dimethylbenzidine tetrazoniumchloride, 3,3'-dimethoxybenzidine tetrazoniumchloride, 4,4'-diaminodiphenylamine tetrazoniumchloride, 3,3'-diethylbenzidine tetrazoniumsulfate, 4-aminodiphenylamine diazoniumsulfate, 4-aminodiphenylamine diazoniumchloride, 4-piperidino aniline diazoniumsulfate, 4-diethylamino aniline diazoniumsulfate and oligomeric condensation products of diazodiphenylamine and formaldehyde. Examples of diazo resins useful in the present invention include condensation products of an aromatic diazonium salt as the light-sensitive substance. Such condensation products are known and are described, for example, in German Pat. no. 1214086. They are in general prepared by condensation of a polynuclear aromatic diazonium compound, preferably of substituted or unsubstituted diphenylamine-4-diazonium salts, with active carbonyl compounds, preferably formaldehyde, in a strongly acid medium. The light sensitive layer according to the present invention preferably also contains dispersed water-insoluble polymers. Said aqueous dispersion of water insoluble polymer is preferably cationic or nonionic either e.g. as a result of an emulsifier or by having the cationic or nonionic group linked to the polymer. The water insoluble polymer is preferably a solid particulate having a size in the range of about 100 Angstroms to 1 micron in diameter and does not form a film below 30 °C. In general, any polymer which carries a cationic or nonionic group or which can be formulated into an emulsion using a cationic or nonionic emulsifier can be employed in the present invention. Suitable polymers include homopolymers and copolymers of styrene, methylacrylate, ethylacrylate, butylacrylate, methylmethacrylate, ethylmethacrylate, butyl methacrylate, vinyl acetate, vinyl chloride, vinylidene chloride, butadiene, methyl styrene, vinyl toluene, dimethylaminoethyl acrylate, acrylic acid, methacrylic acid, isoprene, chloroprene, malei anhydride, ethylene glycol acrylates such as polyethylene glycol acrylate, halogenated vinyl aromatics such as chlorostyrene and bromostyrene, methylvinyl ether, vinyl pyrrolidone, polyurethane and the like. Among the cationic and nonionic emulsifiers which can be used in the present invention are: ammonium salts of substituted amines containing alkyl and/or aryl groups attached to the nitrogen, alkyl or aryl sulfonium salts, alkyl and alkyl-aryl polyethers, cationic or nonionic fluorosurfactants and polyoles. The thickness of the light-sensitive layer in the material of this invention may vary in the range of 0.1 to 10 um and is preferably between 0.5 and 2.5 um. Suitable supports that can be used in an imaging element in accordance with the present invention are substrated polyethylene terephthalate film, cellulose acetate film, plastics having a metal layer or deposit thereon, and polyolefin (e.g. polyethylene) coated paper, the polyolefin surface of which may have been subjected to a corona discharge to improve the adherence of a hydrophilic layer. As hydrophilic (co)polymers in the hydrophilic layer of an imaging element in connection with the present invention one may use, for example, homopolymers and copolymers of vinyl alcohol, acrylamide, methylol acrylamide, methylol methacrylamide, acrylic acid, methacrylic acid, hydroxyethyl acrylate, hydroxyethyl methacrylate or maleic anhydride/vinylmethylether copolymers. The hydrophilicity of the (co)polymer or (co)polymer mixture used is the same as or higher than the hydrophilicity of polyvinyl acetate hydrolyzed to at least an extent of 60 percent by weight, preferably 80 percent by weight. Examples of hydrolyzed tetraalkyl orthosilicate crosslinking agents are hydrolyzed tetraethyl orthosilicate and hydrolyzed tetramethyl orthosilicate. The amount of tetraalkyl orthosilicate crosslinking agent is preferably at least 0.2 parts by weight per part by weight of hydrophilic (co)polymer, more preferably between 0.5 and 5 parts by weight, most preferably between 1.0 parts by weight and 3 parts by weight. Said hydrophilic layer in an imaging element used in accordance with the present invention preferably also contains substances that increase the mechanical strength and the porosity of the layer. For this purpose colloidal silica may be used. The colloidal silica employed may be in the form of any commercially available water-dispersion of colloidal silica for example having an average particle size up to 40 nm, e.g. 20 nm. In addition inert particles of larger size than the colloidal silica can be added e.g. silica prepared according to Stöber as described in J. Colloid and Interface Sci., Vol. 26, 1968, pages 62 to 69 or alumina particles or particles having an average diameter of at least 100 nm which are particles of titanium dioxide or other heavy metal oxides. By incorporating these particles the surface of the layer is given a uniform rough texture consisting of microscopic hills and valleys, which serve as storage places for water in background areas. The thickness of a hydrophilic layer in a material according to this invention may vary in the range of 0.2 to 25 um and is preferably 1 to 10 um. According to a preferred embodiment in connection with the present invention there is provided an intermediate layer of an organic compound having cationic groups between the hydrophilic and light sensitive layer. As a consequence the development by plain water of such a diazo based imaging element is improved. Organic compounds having cationic groups for use in an intermediate layer are preferably hydrophilic and may be low moleculair weight compounds but are preferably polymers. Preferred compounds are those having one or more ammonium groups or amino groups that can be converted to ammonium groups in an acidic medium. An especially preferred type of cationic compounds are polysacharides modified with one or more groups containing an ammonium or amino group. Most preferred organic compounds having cationic groups are dextrans or pullulan wherein at least some of the hydroxy groups of the dextran or pullulan has been modified into one or more of the following groups: -O-R 1 -O-CO-R 2 wherein R 1 represents an organic residue containing an amino or ammonium group, e.g. an amine substituted alkyl, an amine substituted alkylaryl etc.. R 2 has one of the significances given for R 1 or stands for -OR 3 or -N(R 4 )R 5 , wherein R 3 has one of the significances given for R 1 and each of R 4 and R 5 which may be the same or different have one of the significances given for R 1 . Examples of dextrans or pullulan that can be used in accordance with the present invention are dextrans or pullulan wherein some of the hydroxyl groups have been modified in one of the groups shown in table 1. no. modified group 1 -O-CH 2 -CH 2 -NH 2 2 -O-CO-NH-CH 2 -CH 2 -NH 2 3 -O-CO-NH-CH 2 -CH 2 -N(CH 2 -CH 2 -NH 2 ) 2 4 -O-CH 2 -CH 2 -NH-CH 2 -CH 2 -NH 2 5 -O-CH 2 -CH 2 -NH-CH 2 -CHOH-CH 2 -N + (CH 3 ) 3 Cl - 6 -O-(CH 2 -CH 2 -O) n -CH 2 -CH 2 -NH 2 wherein n represents an integer from 1 to 50 7 -O-CO-NH-CH 2 -CH 2 -NH-CH 2 -CHOH-CH 2 -N + (CH 3 ) 3 Cl - 8 -O-CH 2 -CH 2 -N(CH 2 -CH 3 ) 2 .HCl 9 -O-CH 2 -CH 2 -N(CH 2 -CH 2 -NH 2 ) 2 10 -O-CONH-CH 2 -CH 2 -N(CH 2 -CH 2 -NH 2 ) 2 11 -O-CONH-(CH 2 -CH 2 -O) n -CH 2 -CH 2 -NH 2 The modified dextrans or pullulan can be prepared by a reaction of a dextran with e.g. alkylating agents, chloroformates, acid halides, carboxylic acids etc... An intermediate layer containing the organic compound having one or more cationic groups is preferably provided in an amount of 5 to 500mg/m 2 and more preferably in an amount of 10 to 200mg/m 2 . The imaging element in connection with the present invention advantageously contains water-soluble dyes such as rhodamines, sudan blue, methylen blue, eosin or trifenylmethane dyes such as crystal violet, victoria pure blue, malachite green, methylviolet and fuchsin or dye pigments. These colorants may be incorporated in the light sensitive layer and/or hardened hydrophilic layer. To obtain a lithographic printing plate from an imaging element according to the invention said imaging element is image-wise exposed and subsequently rinsed or washed with plain water to remove diazo resin or diazonium salts in the non-exposed or insufficiently exposed parts of the imaging element. The exposure of the imaging element used in the present invention advantageously proceeds with ultraviolet light optionally in combination with blue light in the wavelength range of 250 to 500 nm. Useful exposure sources are high or medium pressure halogen mercury vapour lamps, e.g. of 1000 W. Since most lithography is done by the offset process, the imaging element is preferably exposed in such a way that the image obtained thereon is right reading. The exposure may be an exposure using optics or a contact exposure. The diazo resin or diazonium salts are converted upon exposure from water soluble to water insoluble (due to the destruction of the diazonium groups) and additionally the photolysis products of the diazo may induce an advancement in the level of crosslinking of the polymeric binder or diazo resin, thereby selectively converting the surface, in an image pattern, from water soluble to water insoluble. The unexposed areas remain unchanged, i.e. water soluble. The following examples illustrate the present invention without being limited thereto. The percentages given are by weight unless otherwise stated. EXAMPLE Preparation of a lithographic base To 440 g of a dispersion contg. 21.5% TiO 2 (average particle size 0.3 to 0.5 um) and 2.5% polyvinyl alcohol in deionized water were subsequently added, while stirring, 250 g of a 5% polyvinyl alcohol solution in water, 105 g of a hydrolyzed 22% tetramethylorthosilicate emulsion in water and 12 g of a 10% solution of a wetting agent. To this mixture was added 193 g of deionized water and the pH was adjusted to pH=4. The obtained dispersion was coated on a polyethyleneterephthalate film support having a thickness of 275µm (382g/m 2 ) (coated with a hydrophilic adhesion layer) to a wet coating thickness of 50 g/m 2 , dried at 30 °C. and subsequently hardened by subjecting it to a temperature of 57 °C for 1 week. To this base was further provided an aqueous solution of (pH=5) of Dormacid (a dextran modified with a diethylaminoehtylgroup available from Pfeifer & Langen) and a cationic wetting agent to a dry coating thickness of 30 mg Dormacid per m 2 . The obtained element was then heated for 1 week at 57 °C. Preparation of the imaging elements An imaging element according to the invention was produced by preparing the following light sensitive composition and coating it to the above described lithographic base in an amount of 35g/m 2 (wet coating amount) and drying it at 30°C. Preparation of the light sensitive coating: To 63g of a 20% dispersion of polymethylmethacrylate (particle diameter of 40nm) stabilized with cetyltrimethylammoniumbromide in deionized water was subsequently added, while stirring, 120 g of a 5% solution of a 98% hydrolised polyvinyl acetate (POLYVIOL W48/20 available from Wacker) in water and 15 g of a 10% dispersion of heligen blue (BASF) in water. 66 g of a 15% solution of the condensationproduct of diphenylamine diazonium salt and formaldehyde in water was then slowly added. Finally 30 g of a 1.6% solution of cationic fluor containing surfactant (Fluorad FC135 available from 3M) in water, and 726 ml of water were added. The obtained imaging elements were conditioned at 25°C at various relative humidity conditions (see table 2) and under these conditions packaged in a closed aluminium bag being impermeable for water. The packages were then stored for 3 days at 57°C. The imaging elements were then each exposed to a high pressure halogen mercury vapour lamp of 1000W at a distance of 70cm for 90 seconds. Subsequently the imaging elements were developed by rinsing with plain water and used to print on an offset press running with a commonly employed ink and fountain solution. The obtained results are shown in table 2. Relative humidity free water (g/m 2 ) Printing results 30% 1.60 Excellent 40% 1.90 Excellent 45% 2.10 Excellent 50% 2.25 no printing possible 60% 2.55 no printing possible (*) The maximum amount of free water according to formula (I) was 2.1g/m 2

Claims: An imaging element comprising on substrated polyethylene terephthalate film, cellulose acetate film, plastics having a metal layer or deposit thereon, or polyolefin coated paper a hydrophilic layer containing a hydrophilic (co)polymer or (co)polymer mixture and having been hardened with a hydrolysed tetraalkyl orthosilicate and a light sensitive layer containing a diazo resin or a diazonium salt characterized in that the total amount of free water in said imaging element satisfies the following formula (I): FW (g/m 2 ) ≤ 0.0043 * WS (g/m 2 ) + 0.46 (g/m 2 ) wherein FW represents the amount of free water and WS represents the weight of the support of the imaging element. An imaging element according to claim 1 wherein said support is a polyester film support. An imaging element according to claim 1 or 2 wherein there is provided an intermediate layer containing an organic compound having cationic groups between said hydrophilic layer and said light sensitive layer. An imaging element according to any of the above claims wherein said light sensitive layer contains a polyvinylacetate hydrolysed to an extent of at least 95% by weight as a hydrophilic binder and further a cationic fluor containing surfactant. A method for making a lithographic printing plate comprising the steps of image-wise exposing an imaging element as defined in any of the above claims and subsequently developing a thus obtained image-wise exposed imaging element by means of rinsing with plain water.

Inventors: HAUQUIER GUIDO, VERMEERSCH JOAN, VERSCHUEREN ERIC, HAUQUIER, GUIDO, VERMEERSCH, JOAN, VERSCHUEREN, ERIC, HAUQUIER, GUIDO, C/O AGFA-GEVAERT N.V., DIE 3800, VERMEERSCH, JOAN, C/O AGFA-GEVAERT N.V., DIE 3800, VERSCHUEREN, ERIC, C/O AGFA-GEVAERT N.V., DIE 3800
Applicants: AGFA GEVAERT NV, AGFA-GEVAERT N.V.
Application year: 1993
Main classification: G03F7
IPC codes: G03F7