PROCESS FOR PRODUCING DIFLUOROMETHANE

Abstract: A process for producing difluoromethane (CF₂H₂, HFC-32) at high conversion and selectivity by the reaction of dichlorodifluoromethane (CF₂Cl₂, CFC-12) and/or monochlorodifluoromethane (CF₂ClH, HCFC-22) with hydrogen in the presence of a palladium-base catalyst.

Description: The present invention relates to a method for preparing difluoromethane (CF 2 H 2 ) which is used as a refrigerant and the like and is a substitute for a fluorinated gas. Related Art A method for preparing CF 2 H 2 (hereinafter referred to as HFC-32) includes a process of reducing CF 2 Cl 2 (hereinafter referred to as CFC-12), as described in UK Patent No. 732269; and a process of fluorinating CH 2 Cl 2 (dichloromethane), as described in Japanese Patent Kokoku Publication No. 3004/1967 (corresponding to US Patent No. 226447), and Japanese Patent Kokai Publication Nos. 225131/1984, 231029/1984 and 231030/1984. Among them, the former process is to conduct the reduction with hydrogen at a temperature of 400 to 1,000°C in the presence of a Pt, Pt alloy, Cu, Ag or Co catalyst. In the latter process, a used catalyst includes dichromium trioxide, chromium fluoride, aluminum fluoride and a mixture thereof. HFC-32 draws attention as a substitute for CFC-12 (CF 2 Cl 2 , dichlorodifluoromethane) and HCFC-22 (CF 2 ClH, monochlorodifluoromethane). Accordingly, if HFC-32 can be prepared from the CFC-12 or HCFC-22 raw material, the existing apparatus can be effectively used. In this case, a reaction for reducing the raw material is necessary. However, a hitherto known reduction method has a high reaction temperature of at least 400°C and gives an excess reduction in the case that each of HCFC-22 and CFC-12 is used as the raw material, whereby resulting in a large amount of evolved methane so that a selectivity of HFC-32 is low. For example, in the case of the reaction at the temperature of 720°C, a conversion of CFC-12 is 66 % and a selectivity of HCFC-32 is only 13.2 % (cf. UK Patent No. 732269). EP 508 660 describes the production of difluoromethane by reacting a compound of the formulae XYCF 2 wherein X and Y are each H, Cl or Br, but at least one of X and Y is an atom other than hydrogen, and in particular chlorodifluoromethane with hydrogen at an elevated temperature in the presence of a hydrogenation catalyst comprising palladium, optionally together with ruthenium, rhodium, nickel, silver or chromium supported on an active carbon carrier. JP-A-1 242536 discloses a process for the production of tetratluoroethane by reacting a haloethane of the general formula CF 2 XCFYZ, wherein X, Y and Z are Cl, F or H, and wherein 4-5 F atoms are present in the molecule, with hydrogen in the presence of a hydrogenation catalyst comprising a platinum group element and at least one element or compound selected from Zr, Hf, Ti, Nb and Tr supported on a carrier such as active carbon or alumina. In this reaction the use of a catalyst comprising a platinum group element together with another catalytically active compound does not give rise to an improvement with regard to the product selectivity and/or the conversion rate in comparison to the use of a catalyst comprising only a platinum group element as active component. SUMMARY OF THE INVENTION An object of the present invention is to provide a method for preparing HFC-32 from a CFC-12 or HCFC-22 raw material so as to give both of a high conversion and a high HFC-32 selectivity. The present invention provides a method for preparing difluoromethane (CF 2 H 2 , HFC-32) comprising reacting dichlorodifluoromethane (CF 2 Cl 2 , CFC-12) and/or monochlorodifluoromethane (CF 2 ClH, HCFC-22) with hydrogen in the presence of a palladium-based catalyst. DETAILED DESCRIPTION OF THE INVENTION The palladium-based catalyst is a catalyst in which at least one metal selected from the group consisting of vanadium (V), Zirconium (Zr), calcium (Ca), magnesium (Mg), niobium (Nb) and tantalum (Ta) is added to palladium. The above reaction (hydrogenation reaction) in the present invention is preferably conducted at a temperature of 120 to 400°C. The palladium-based catalyst used in the present invention comprises a carrier and an active metal component. The active metal component is a combination of a palladium metal with at least one additional metal selected from the group consisting of vanadium, zirconium, calcium, magnesium, niobium and tantalum. An amount of palladium supported in the catalyst is preferably from 0.5 to 5 % by weight. A molar ratio of the additional metal to Pd is usually from 0.01 to 4, preferably from 0.1 to 2. Since the large molar ratio does not give a significant effect on a selectivity and gives a decrease of reaction conversion, the molar ratio is preferably at most 4. A size of the catalyst is not limited and is usually from 1 to 6 mm. A powdery catalyst may be used. The additional metal may be in the form of a salt. A nitrate salt, a metal oxide salt, an oxide and a chloride salt can be used. The carrier may be one usually used in conventional catalysts, such as active carbon and alumina. Since HF may evolve in the method of the present invention, it is undesirable to use a catalyst which has no resistance to HF. One example of procedure for supporting the additional metal on the carrier is explained hereinafter. However, the present invention is not limited to this example. A salt of an additional metal is dissolved in water. Formalin and a powdery catalyst having Pd supported on active carbon are added to water and aged. The additional metal is dissolved in such amount that the desired molar ratio of the additional metal to palladium is achieved. Then, after water is evaporated, the catalyst is dried in air. Before the method of the present invention, the catalyst may be pretreated at 300-500°C for 0.1-10 hours in a hydrogen stream. In the reaction of the present invention, a molar ratio of hydrogen to CFC-12 or HCFC-22 is usually from 1 to 10. When the molar ratio is from 1 to 10, the selectivity is not adversely affected and the reaction seldom gives an excessively hydrogenated paraffin compound. The W/F (W: weight of catalyst (g), F: total flow rate of raw material and hydrogen (ml/sec at STP)) corresponding to a contact time is preferably from 0.01 to 10. When the W/F is up to about 10, the W/F gives an effect only on the reaction conversion with a slight change of the selectivity. The method of the present invention is usually conducted in a gas phase. A reaction temperature is usually from 120 to 400°C, preferably from 200 to 300°C. A reaction pressure is usually from 1 to 10 atm, preferably from 1 to 5 atm. According to the present invention, when the reaction temperature is from 200 to 300°C, the reaction gives the result that a conversion from CFC-12 is 91 % and a selectivity to HFC-32 is 81 %. In the reaction of the present invention, a raw material is either CFC-12 or HCFC-22; or combination thereof. According to the method of the present invention, the reaction of CFC-12 and/or HCFC-22 with hydrogen in the presence of the palladium-based catalyst at the temperature of at most 400°C gives a higher conversion and a higher HFC-32 selectivity. PREFERRED EMBODIMENT OF THE INVENTION The present invention will be illustrated by the following Examples. Example 1 An additional metal (namely, Zr) was supported on a catalyst material in which 5 % by weight of Pd is supported on active carbon (a commercially available catalyst manufactured by N. E. CHEMICAL CATALYST) to prepare a catalyst. A molar ratio of Zr/Pd in the resultant catalyst was 0.5. 0.083 g of zirconyl chloride was dissolved in 30 ml of water. 2 g of the powdery catalyst material in which Pd is supported on active carbon and 0.2 g of formalin were added to water and aged at 50°C for 2-3 hours. Then, water was removed by the use of a rotary evaporator and a solid material was dried at 100°C for 12 hours in air. Before a hydrogenation reaction of CFC-12, the catalyst was treated at 400°C for 2 hours so as to conduct a pretreatment of the catalyst. A SUS-314 reaction tube having an internal diameter of 10 mm was filled with 1 g of catalyst. While keeping the reaction tube at a temperature of 250°C, a combination of 10 Nml/min of CFC-12 and 30 Nml/min of H 2 was passed through the reaction tube. A conversion of CFC-12 was 91 %. A selectivity was 81 % of HFC-32, 14 % of methane, 1 % of ethane and 3 % of HCFC-22. Example 2 The reaction was conducted in the same manner as in Example 1, except that the reaction temperature was 200°C. A conversion of CFC-12 was 75 %. A selectivity was 82 % of HFC-32, 13 % of methane, 1 % of ethane and 4 % of HCFC-22. Example 3 The reaction was conducted in the same manner as in Example 1, except that the flow rates of CFC-12 and H 2 were 4 Nml/min and 9 Nml/min, respectively. A conversion of CFC-12 was 89 %. A selectivity was 70 % of HFC-32, 21 % of methane, 5 % of ethane, 2 % of HCFC-22 and 2 % of HFC-23 (CF 3 H). Example 4 The reaction was conducted in the same manner as in Example 1, except that the molar ratio of Zr/Pd was 0.2. A conversion of CFC-12 was 89 %. A selectivity was 82 % of HFC-32, 12 % of methane, 2 % of ethane and 4 % of HCFC-22. Example 5 The reaction was conducted in the same manner as in Example 1, except that the molar ratio of Zr/Pd was 1. A conversion of CFC-12 was 62 %. A selectivity was 67 % of HFC-32, 20 % of methane, 7 % of ethane and 6 % of HCFC-22. Example 6 The reaction was conducted in the same manner as in Example 1, except that the molar ratio of Zr/Pd was 1.5. A conversion of CFC-12 was 82 %. A selectivity was 76 % of HFC-32, 13 % of methane, 6 % of ethane, 4 % of HCFC-22 and 1 % of HFC-23. Example 7 The reaction was conducted in the same manner as in Example 1, except that ammonium metavanadate was used as the supported metal salt and the molar ratio of V/Pd was 0.2. A conversion of CFC-12 was 74 %. A selectivity was 81 % of HFC-32, 15 % of methane and 4 % of HCFC-22. Example 8 The reaction was conducted in the same manner as in Example 1, except that magnesium chloride was used as the supported metal salt and the molar ratio of Mg/Pd was 1. A conversion of CFC-12 was 40 % and a selectivity of HFC-32 was 81 %. Example 9 The reaction was conducted in the same manner as in Example 1, except that calcium chloride was used as the supported metal salt and the molar ratio of Ca/Pd was 1. A conversion of CFC-12 was 52 % and a selectivity of HFC-32 was 78 %. Example 10 The reaction was conducted in the same manner as in Example 1, except that niobium chloride oxide was used as the supported metal salt and the molar ratio of Nb/Pd was 1. A conversion of CFC-12 was 52 % and a selectivity of HFC-32 was 78 %. Example 11 The reaction was conducted in the same manner as in Example 1, except that tantalum chloride was used as the supported metal salt and the molar ratio of Ta/Pd was 0.5. A conversion of CFC-12 was 46 % and a selectivity of HFC-32 was 82 %. Example 13 The reaction was conducted in the same manner as in Example 7, except that HCFC-22 was used instead of CFC-12, the flow rates of HCFC-22 and H 2 were 10 Nml/min and 20 Nml/min respectively, the reaction temperature was 380°C, and the molar ratio of V/Pd was 1. A conversion of HCFC-22 was 62 %. A selectivity was 76 % of HFC-32, 22 % of methane, 1 % of ethane and 1 % of HCFC-23. Example 14 The reaction was conducted in the same manner as in Example 13, except that the molar ratio of V/Pd was 0.5. A conversion of HCFC-22 was 63 %. A selectivity was 73 % of HFC-32, 24 % of methane and 3 % of HFC-23.

Claims: A method for preparing difluoromethane comprising reacting dichlorodifluoromethane and/or monochlorodifluoromethane with hydrogen in the presence of a palladium-based catalyst, wherein the palladium-based catalyst is a catalyst in which at least one metal selected from the group consisting of vanadium, zirconium, calcium, magnesium, niobium and tantalum is added to palladium. The method according to claim 1, wherein the reaction is conducted at a temperature of 120 to 400°C.

Inventors: ICHIKAWA MASARU, OHNISHI RYUICHIROU, ICHIKAWA, MASARU, OHNISHI, RYUICHIROU, ICHIKAWA, MASARU, HOKKAIDO UNIVERSITY, OHNISHI, RYUICHIROU, HOKKAIDO UNIVERSITY
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LIMITED
Application year: 1993
Main classification: C07C19
IPC codes: C07C17