ALIGNMENT OF INTEGRATED OPTICAL COMPONENTS

Abstract: A method for connecting two components (10, 11) with functional parts (12, 19) thereof in a predetermined alignment such as a semiconductor laser (11) and motherboard (10), comprising forming the laser (11) by processing in which the radiation outlet (19) and alignment means (21) are provided in a predetermined position with respect to each other, similarly forming on the motherboard (10), a waveguide (12) and alignment means (16, 14), mounting the laser (11) on the motherboard (10) in a generally aligned position, providing solder (26) between metal pads (18, 22) on the laser (11) and motherboard (10), and utilizing the surface tension of the molten metal (26) extending between the pads (18, 22) to move the laser (11) into an accurately aligned position on the motherboard (10).

Description: ALIGNMENT OF INTEGRATED OPTICAL COMPONENTS This invention relates to the alignment of components such as integrated optical components- Difficulties are commonly experienced in mounting together integrated optical components (such as a semiconductor laser with optical fibres or planar waveguides, detectors, fibre amplifiers and the like), with sufficient accuracy. One of the most demanding situations is the provision of accurate alignment between a laser and waveguides. As an example of this requirement, the case of a semiconductor laser coupling to an AsG waveguide has been considered. For maximum power transfer, the laser and guide should exactly butt together. The coupling efficiency is limited by the mismatch in the mode sizes of the two components. For the structures of current interest, this results in an efficiency of 45% or a loss of 3.5dB. In practice, it is not possible to achieve exact butt coupling and it is therefore necessary to determine the optimum separation between the laser and the guide where axial alignment sensitivity is at its lowest. For signalling type applications, a coupling efficiency between the laser and waveguide of 10% or a loss of 10dB is seen as the minimum acceptable value. Taking this figure as a target spec fication, the maximum horizontal and vertical misalignment allowable has been calculated as a function of separation between the laser and the waveguide. For the current case, it was found that a separation of 6μm gave the lowest sensitivity to axial misalignment (1.7μm or 1.9μm in the vertical or horizontal directions before loss in excess of the target value was obtained). These calculations do not take into account any angular deviation between the laser and the waveguide and so should be viewed as a "best case" estimate. As a result, the alignment tolerance sought in a motherboard process was taken as less than 1 μm in both the horizontal and vertical directions. If higher coupling efficiencies than 10% are required, (eg in the case of laser pumping for optical amplifiers), it would be necessary to match the mode sizes of the two components by use of, for example, a lensed laser assembly. It has been known to join two- integrated circuit or chips by a so called "flip-chip" solder bonding technique. The faces of the two integrated circuits which are to be joined each contain a corresponding pattern of metal pads, and one of the integrated circuits is provided with a solder bump on each metal pad, the two integrated circuits are approximately aligned, the solder is melted, and the solder, by surface tension, moves the two integrated circuits into alignment so that the corresponding metal pads on each integrated circuits are exactly aligned. The alignment is determined by the metal pads themselves.. Whilst this provides a fairly accurate way of aligning two components, in particular in a case with flip-chips where the two integrated circuits are to be interconnected electrically, as determined above, greater accuracy of alignment is required in aligning integrated optical components. The present invention provides, according to one aspect, a method for connecting two components together with functional parts thereof in a predetermined alignment, comprising:- processing said first component to form a first functional part and a first alignment means in a predetermined position with respect to said first funct ional part , providing a pad in a predetermined position on the surface of said first component, processing said second component to form a second functional part and a second alignment means in a predetermined position with respect to said second funct ional part , providing a pad in a predetermined position on the surface of said second component, providing a meltable solid on one of said pads the meltable solid being of a material which preferentially adheres to the pad, generally aligning the two components, melting the meltable solid so that it interconnects adjacent pads on the two components, the disposition of the first and second alignment means and metal pads being such that the surface tension of the molten solid in contact with adjacent pads on the two components urges the two components into a relative position so that the first and second alignment means accurately align and the first and second functional parts are thus in a predetermined alignment. Preferably, said pads are disposed so that when said two components are aligned, the surface tension of said molten solid continues to provide a component of force which urges the alignment means into contact with each other. Preferably, in respect of one or both components, the functional parts are also defined by the same etching step as the alignment means. There are very considerable advantages in the method of the invention. Thus the alignment means will be reproducibly accurately aligned with the functional part of the component as they are made by the same process. Thus for example, where one of the components is a semiconductor laser, the radiation output of the laser (which is the functional part), is defined in an etching process step which may also be used to provide the alignment means. Similarly, if the component is a silicon motherboard, the input of a waveguide (which for this purpose is the functional part) is defined in our etching step which is also used to define the alignment means. The method is compatible with conventional silicon processing, that is wet and dry etching and photolithography requirements. In accordance with conventional techniques, the etching may be carried out after a resist layer has been laid on the surface by photolithography. In a preferred arrangement, each component may include two alignment means, to operate in orthogonal directions. The alignment means may comprise a protrusion, an edge, or a slot. In a preferred arrangement, one of the components may comprise a substrate of crystalline material which contains intersecting planes which can be delineated by etching, the etching of the alignment means forming the alignment means. The present invention also provides in combination, two components mounted together, each component comprising a functional part and an alignment means in a predetermined position with respect of said functional part, each component including a pad in a predetermined position on its surface, said two components being interconnected by a molten solid extending between adjacent pads on the two components, said combination being formed in accordance with a method as claimed in any of claims 1 to 9. The invention will now be described by way of example only and with reference to the accompanying drawings in which:- Figure 1 is a diagrammatic plan view of part of a motherboard with semiconductor laser mounted thereon in accordance with a method of the invention, Figure 2 is a section of Figure 1 on line Y-Y, and, Figure 3 is a section of Figure 1 on line X-X. Referring to Figure 1 there is shown a silicon motherboard 10 on top of which is to be mounted a semiconductor laser 11. In the process of the invention, various components are formed on the silicon of the motherboard 10, for example, a waveguide 12. The optical waveguide 12 is defined on a silicon motherboard by a l thographically patterned AsG core surrounded by an undoped silicon dioxide cladding. This combination of glasses can be processed conveniently at low temperatures, and owing to their large index difference, allow the fabrication of low loss, small radius bends which permit a high component density on the motherboard. The process sequence includes initially forming the recess 13 by a micromachining or wet etch process. The waveguide 12 is produced by a wet etch process using a KOH chemically etched recess (typically 7μm deep) which is partially filled with a PECVD undoped silicon oxide for the low cladding or buffer layer. The waveguide core is formed by a 2μm thick AsG layer which is dry (plasma) etched and reflowed in an oxidising atmosphere at temperatures between 950t and 1000°^. This plasma dry etching process also defines a mask for subsequently forming the slot 14 to be referred to later. The end of the waveguide which needs to be accurate is formed by plasma etching. A 4 to 6μm undoped oxide is deposited to surround the waveguide core. Potential difficulties arising from cavities between the core and cladding may be minimised by using planarising techniques. Micro achining or wet etching is then used through the defined mask to form the V groove 14 which is thereby accurately aligned with the waveguide 12. The recess 13 and V groove 14 are both formed by micromachining by an anisotropic etching process using an etchant such as KOH or ethylene diamine pyrocatechol and water (EDP). With such etchants, some crystal planes in silicon etch much more slowly than others. Consequently when a masking window is aligned correctly along the intersections of two such planes with the surface of the silicon, etching terminates at these planes and a V shaped groove results. Since these planes are related directly to the crystal lographic structure of the silicon, the angle and direction of the recess 13 or V groove 14 are very tightly controlled. The width of the V groove can therefore be controlled very accurately, typically to a tolerance of 0.25 to 0.5 μm. As the mask window for the V groove 14 is etched in the same step as the waveguide 12 is etched, the position of the V groove 14, and in particular the sides of tJie V groove 14 can be accurately predetermined with respect to the position of the waveguide 12, by utilising photolithography. It will be seen from Figure 1 that the V groove 14 is straight (as would be expected as it is along a crystal plane) and of a suitable depth as will be determined. There is also provided on the top surface of the motherboard 10 a pair of polysilicon stops 16 which are formed by providing a layer of polysilicon and etching away (before the wet etching of the "V groove 14 and just before the plasma etch of the end surface of the waveguide) the remainder of the layer to provide the polysilicon stops. Once again, because the polysilicon stops are provided by means of an etching process through a mask, the edges 17 of the polysilicon stop 16 will be accurately aligned with, for example, the input of the waveguide 12. A metal pad 18 of "L" shape is laid down in the recess 13, in a manner well known in semiconductor technology, one leg of the pad extending parallel to the V groove and the other leg extending parallel to the edges 17 of the polysilicon stops 16. Referring now to the semiconductor laser 11, there is provided an active region (viz, output) at which the laser radiation is outρutted adjacent the waveguide 12. The under surface of the semiconductor laser, includes a ridge 21 downwardly depending from its lower surface. The ridge 21 is produced by an etching process, the etching being carried out as described above. As the active region 19 of the laser is also defined by an etching process, the alignment of the active region 19 and the ridge 21 is predetermined by the masks used in the etching process and can therefore be accurately determined. There is also laid down on the under surface of the laser 11 a metal pad 22 which is of similar shape and extent to the metal pad 18, that is, "L" shaped with a first leg parallel to the ridge 21 and a second leg parallel to an edge 23 of the laser, except that the width of the legs of the pad 22 are smaller, typically one third, of the width of the legs of the pad 18. The position, and shape of the metal pads 18 and 22 is defined in the manufacture of the relevant component by photolithography through a suitable mask. Furthermore, the metal pads are made of, or coated with, a metal which is wetted by molten solder. When the motherboard and laser are correctly aligned, as is exaggerated in the view of Figure 1, the metal pad 22 is, in the view of Figure 1, slightly below and to the left of the metal pad 18. -_ Before assembly of the motherboard 10 and the semiconductor laser 11, the metal pad 22 is provided with solder 26 in the form of a solder bump. To assemble the semiconductor laser 11 to the motherboard 10, the laser 11 is laid onto the motherboard in approximate alignment with its final position. In practice, the laser 11 will naturally rest below and to the left of the final position in Figure 1 , because it cannot rest on top of the polysilicon stops 16 and the ridge 21 will naturally rest somewhere towards the middle of the V groove 14. The solder is then melted, and by means of surface tension effects (see solder 26 in Figures 2 and 3), will interconnect the two metal pads 18 and 22, and draw the laser 11 in the direction of the arrow A in the Figures so that the ridge 21 engages against the right side of the V groove 14 as shown in Figure 3 and the edge 23 of the laser abuts the edges 17 of the polysilicon stop 16. In this way the semiconductor laser 11 is accurately aligned with the motherboard 10 so that the active region 19 is accurately aligned with the waveguide 12. In the final aligned position of the laser 11 and motherboard 10, it may be arranged that the two metal pads 18,22 exactly align with one another. Alternatively, it can be arranged that the metal pad 22 may, when viewed in Figure 1, be arranged to be below and to the left of the metal pad 18 (exaggerated in the Figures) whereby even when the laser 11 and motherboard 10 are correctly aligned, there will be some residual slight force caused by the surface tension effects of the molten solder, urging the laser 11 in an direction of arrow A. In some circumstances, it may be that the laser 11 may have a large surface overlapping and laying on the motherboard 10 and there may be frictional forces to be overcome if the laser and motherboard are to be moved relative to one another. In this case, one solution is for the quantity of solder in each solder bump to be greater than otherwise so that when the solder melts, there is sufficient solder to cause the laser 11 to be lifted above the motherboard 10 to thereby eliminate friction. The amount by which the laser is lifted above the motherboard is preferably very small, typically 1 μm and therefore the amount of solder in each solder bump should be carefully calculated to provide that exact clearance between the laser and motherboard. In this way, by eliminating friction particularly to zero, the surface tension effect is sufficient to move the laser with respect to the motherboard exactly into alignment as above described. We have therefore provided a method of connecting external components such as lasers, detectors, and/or other optical integrated circuits to a motherboard. The process is compatible with conventional silicon processing and photol thography. The use of surface tension in molten solder to move the semiconductor laser 11 into correct alignment with the motherboard 10 enables one to use a controlled force to move the laser. Excessive force could cause damage to the alignment means, in particular the ridge 21 which might easily be damaged or broken. In an alternative arrangement, the pad 18 may also be made thinner than the pad 22 in which case their orientations would need to be rotated by 180° in respect of the view in Fi gu re 1 . The invention is not restricted to the details of the foregoing example. The two pads 18 and 22 are shown "L" shaped in the present arranged. However the two pads could be other shapes, for example rectangular but they should have the relative orientation shown in Figure 1, that is the pad 18 is (in the plane of the drawing) further up and to the right with respect to the pad 22. The invention is not restricted to the details of the foregoing example.

Claims: CLAIMS 1. A method for connecting two components together with functional parts thereof in a predetermined alignment, compris ng:- processing said first component (10) to form a first functional part (12) and a first alignment means (14,16) in a predetermined position with respect to said first functional part (12), providing a pad (18) in a predetermined position on the surface of said first component (10), processing said second component (11) to form a second functional part (19) and a second alignment means (21,23) in a predetermined position with respect to said second functional part (f9), providing a pad (22) in a predetermined position on the surface of said second component (11), providing a meltable solid (26) on one of said pads (18,22) the meltable solid (26) being of a material which preferentially adheres to the pads (18,22), generally aligning the two components (10,11), melting the meltable solid (26) so that it interconnects adjacent pads (18,22) on the two components (10,11), the disposition of the first and second alignment means (14,16,21,23) and metal pads (18,22) being such that the surface tension of the molten solid (26) in contact with adjacent pads (18,22) on the two components (10,11) urges the two components (10,11 ) into a relative position so that the first and second alignment means (14,16,21 ,23) accurately align and the first and second functional parts (12,19) are thus in a predetermined alignment. 2. A method as claimed in claim 1 characterised in that said pads (18,22) are disposed so that when said two components (10,11 ) are aligned, the surface tension of said molten solid (26) continues to provide a component of force which urges the first and second alignment means (14,16,21,23) into contact with each other. 3. A method as claimed in claim 1 or 2 characterised in that said alignment means of at least one of said components (10,11 ) is defined by etching and the functional part (12,19) of said component(s) is also defined by the same etching step. 4. A method as claimed in any of claims 1 to 3 characterised by processing each of said components (10,11 ) to provide two alignment means (14,16,21,23), to operate in orthogonal directions. 5. A method as claimed in any of claims 1 to 4 characterised in that at least one of said alignment means comprises a protrusion (21 ). 6. A method as claimed in any of claims 1 to 4 characterised in that at least one of said alignment means comprises an edge (17,23). 7. A method as claimed in any of claims 1 to 4 characterised in that at least one of said alignment means comprises a slot (14). 8. A method as claimed in any of claims 1 to 7 characterised in that at least one of said components comprises a substrate of crystalline material which contains intersecting planes which can be delineated by etching, the etching of the component forming said alignment means. 9. A method as claimed in any of claims 1 to 8 characterised in that said two components comprise integrated optical components. 10. A method as claimed in any of claims 1 to 9 characterised in that one of said components including a semiconductor laser and the other includes a waveguide. 11. In combination, two components mounted together, each component (10,11) comprising a functional part (12,19) and an alignment means (1 ,16,21,23) in a predetermined position with respect of said functional part, each component (10,11) including a pad (18,22) in a predetermined position on its surface, said two components being nterconnected by a molten solid (26) extending between adjacent pads (18,22) on the two components, said combination being formed in accordance with a method as claimed in any of claims 1 to 10. 12. An integrated optical apparatus comprising two integrated optical components mounted together, a first said component including a semiconductor laser and a second said component including a waveguide, the first component including an output of the semiconductor laser and an alignment means provided in a predetermined position with respect to said laser output means, the second component including a waveguide input and an alignment means provided in a predetermined position with respect to said waveguide input, each component (10,11) including a pad (18,22) in a predetermined position on its surface, said two components being interconnected by a. molten solid (26) extending between adjacent pads (18,22) on the two components, said integrated optical apparatus being formed in accordance with a method as claimed in any of claims 1 to 10 whereby the semiconductor output and the waveguide input are al igned. SUBSTI

Inventors: COOPER KENNETH, WELBOURN ANTHONY DAVID, COOPER, KENNETH, WELBOURN, ANTHONY, DAVID
Applicants: BRITISH TELECOMM, BRITISH TELECOMMUNICATIONS
Application year: 1993
Main classification: G02B6
IPC codes: G02B6