Method for preparation of polycrystalline silicon carbide fibers

Abstract: This invention relates to the preparation of polycrystalline silicon carbide fibers from ceramic fiber. The process involves heating the ceramic fiber in an environment containing a volatile sintering aid to a temperature sufficient to convert the ceramic fiber to polycrystalline silicon carbide fiber.

Description: The present invention relates to a method for the aftertreatment of ceramic fibers to provide thermally stable, polycrystalline silicon carbide fibers. The method comprises heating a ceramic fiber containing silicon and carbon in an environment comprising a volatile sintering aid at a temperature sufficient to convert the ceramic fiber to polycrystalline silicon carbide fiber. The resultant fibers exhibit excellent mechanical strength at high temperatures and are useful as reinforcements for plastic, ceramic or metal matrices or for the formation of products, such as high temperature insulation, belting, gaskets and curtains. Several methods for the production of silicon carbide fibers have been developed. For instance, it is known that organosilicon polymers may be spun into fibers, infusibilized (cured) to prevent melting and ceramified at elevated temperatures. Such a process is used commercially to produce NICALON™ SiCO fibers and TYRANNO™ SiCOTi fibers from polycarbosilane and titanium-modified polycarbosilane, respectively. That method, however, does not produce high density polycrystalline fibers and it has been found to introduce substantial amounts of oxygen into the fiber. When such fibers are heated to temperatures above 1300°C., the oxygen volatilises as CO and/or SiO causing weight loss, porosity and decreased tensile strength. Methods for the preparation of thermally stable, polycrystalline silicon carbide fibers are also known in the art. For instance, U.S. Patent No. 5,071,600 describes a process for forming such fibers in which polycarbosilane resin is spun into a green fiber, treated with boron, infusibilized and pyrolyzed at a temperature in excess of 1600°C under an inert atmosphere. The process of this patent is clearly different from that of the present invention in that the boron is incorporated at an early stage of the fiber formation process (eg., before or during the cure) whereas the present invention describes heating a ceramic fiber in the presence of a volatile sintering aid during conversion of the ceramic fiber to a polycrystalline silicon carbide fiber. Smoak in U.S. Patent No. 4,237,085 teaches the preparation of silicon carbide bodies by a process which comprises molding SiC powder and elemental carbon into the desired shape and heating the molded body in an atmosphere containing boron. The method and products of this latter patent, however, are clearly different than those taught herein. EP A 435065 relates to a process for the preparation of substantially polycrystalline silicon carbide fibers from a preceramic polymeric precursor comprising phenyl-containing polyorganosiloxane resins which are infusibilized and pyrolyzed. Boron is incorporated either prior to or during formation of the fibers or during the infusibilizing or pyrolyzing steps. EP A 435065 teaches that incorporation of boron becomes increasingly difficult at temperatures above about 400°C. The present invention is based on the unexpected finding that ceramic fibers can be converted to polycrystalline silicon carbide fibers which retain their strength at elevated temperatures (eg., in excess of 1400°C.) by heating the ceramic fibers in an atmosphere comprising a volatile sintering aid. This was particularly unexpected since the prior art teaches that heating ceramic fibers to elevated temperatures causes degradation of the fiber and loss of strength. It was also particularly unexpected since the prior art does not teach that volatile sintering aids can be incorporated in a fiber which has undergone ceramification. The present inventors have now discovered that a volatile sintering aid such as boron can be incorporated into such ceramic fibers and that the boron is effective in limiting fiber grain growth and aiding in densification of the fiber. The fibers resulting from the process of this invention are characterized as having at least 75% crystallinity, a density of at least 2.9 gm/cc and a very low residual oxygen and/or nitrogen content. The fibers also have a small average crystallite size (eg., less than about 1 micrometer), useful tensile strengths and high elastic modulus even after aging at elevated temperature (eg., in excess of 1600°C.). Thus, the present invention provides a process for the aftertreatment of a ceramic fiber containing silicon and carbon which comprises converting the ceramic fiber to a polycrystalline silicon carbide fiber which has at least 75% crystallinity and a density of at least 2.9 gm/cc by heating the ceramic fiber to a temperature of at least 1500°C characterised in that the said heating of the ceramic fiber is effected in an atmosphere comprising a volatile sintering aid for a time sufficient to allow incorporation of at least 0.1% by weight of the sintering aid into the fiber. The ceramic fibers used in this process are not critical and nearly any amorphous or microcrystalline fiber that contains the silicon and carbon necessary to form stoichiometric or carbon-rich silicon carbide fibers can be used. The ceramic fibers used in the invention, therefore, contain silicon and carbon. In a preferred embodiment of the invention, the silicon and carbon are present in near stoichiometric or moderately carbon rich amounts. Other elements, however, can also be present. These include, for example, oxygen, nitrogen, titanium, zirconium, chlorine and any other elements which can either be volatilized out of the fiber during pyrolysis or remain in the fiber without affecting the integrity of the resultant fiber. Oxygen is commonly found in many ceramic fibers in varying amounts (eg., 0.1 wt% up to 25 wt%). If present, said oxygen generally volatilizes out of the fiber upon heating to temperatures above about 1300°C. in the form of either SiO or CO. The inventors herein have also found that when the ceramic fiber is silicon-rich (i.e., greater than a stoichiometric amount of silicon compared to carbon) the oxygen tends to leave as SiO so as to drive the fiber towards stoichiometric SiC. Similarly, when the ceramic fiber is carbon-rich (i.e., greater than a stoichiometric amount of carbon compared to silicon) the oxygen tends to leave as CO so as to drive the fiber towards stoichiometric SiC. Therefore, the fibers can be either silicon or carbon rich provided that there is sufficient oxygen present to cause the desired stoichiometry. Notwithstanding this, however, the silicon content generally should not significantly exceed the sum of the carbon and oxygen contents on an atomic basis. If this occurs, the product may contain a substantial amount of excess silicon which can lead to excessive grain growth and also cause loss of strength. Similarly, oxygen contents above 25-30% should generally be avoided since the resultant product may have low char yields and high porosity. If the ceramic fiber contains nitrogen, most of said nitrogen generally volatilizes out of the fiber upon heating to temperatures above 1400°C. in the form of N 2 . Thus, nitrogen does little to affect the Si-C stoichiometry of the fiber and it may be incorporated into the fibers of the invention as long as the above SiC stoichiometry can be maintained. It should be noted that some nitrogen may remain in the fiber as the nitride of the sintering aid (eg., BN). The inventors herein postulate that this nitride may interfere with complete densification of the fiber. Preferred fibers of the invention, therefore, contain at least silicon and carbon in near stoichiometric amounts or, alternatively, if oxygen is present the carbon content is approximately equal to the sum of the silicon and oxygen contents on an atomic percent basis. More carbon can be present if a product containing some excess carbon in addition to silicon carbide is desired. This can help stabilize the microstructure by inhibiting crystallite growth and it may improve densification. However, elastic modulus generally drops as the excess carbon level rises and, as such, excess carbon levels above 10-15% are generally not used. Examples of fibers useful herein, therefore, include those containing silicon, carbon and, optionally, oxygen, nitrogen, titanium, zirconium and other volatile or non-volatile elements which do not affect the resultant fibers. Such fibers include SiC, SiCO, SiCN, SiCON, SiCOTi and the like. Many of these fibers are known in the art and several are commercially available. These include silicon oxycarbide fibers with a diameter in the range of 10-20 micrometers manufactured by Nippon Carbon and sold under the trade name "Nicalon" (Eg., Ceramic Grade (CG), High Volume Resistivity (HVR), etc.) and silicon oxycarbide fibers containing titanium with a diameter in the range of 8-12 micrometers manufactured by Ube Industries and sold under the tradename "Tyranno". Experimental fibers such as silicon oxycarbonitride fibers with a diameter in the range of about 6-10 micrometers produced by Textron and silicon oxycarbonitride fibers with a diameter in the range of about 10-15 micrometers produced by Dow Corning designated "MPDZ" are also known and are useful herein. Commercial fibers often contain a sizing to prevent their bonding together. Although not necessary for the process of this invention, it may be desirable to remove this sizing prior to heat treatment. This can be accomplished, for instance, by chemically dissolving the sizing or by merely heating the fiber to a temperature sufficient to remove the sizing. Methods for manufacturing the above fibers are well known in the art. The most common approach generally comprises spinning organosilicon polymers (with or without ceramic powder additives) followed by infusibilization and pyrolysis. Alternative approaches, however, such as various sol-gel processing techniques, chemical vapor deposition techniques and the like are also contemplated herein. These methods are described in numerous texts and literature references. Fibers to be used in this process may be nearly any length and may be in nearly any form desired. Generally, the fibers are essentially continuous and are used as either single strands (of 1 or many filaments (tows)) or are aligned unidirectionally (eg., tapes), woven as a 2-dimensional fabric or shaped as a 3-dimensional preform. As noted above, most of the oxygen and/or nitrogen originally present in the fibers is generally volatilized when they are heated at temperatures above 1400°C. in standard environments (eg., inert atmospheres). This generally results in the fibers weakening. The inventors herein, however, have discovered that when these fibers are heated to similar temperatures in an environment comprising volatile sintering aids, they maintain their strength and undergo a densification process which also decreases porosity. The sintering aids which are useful herein are those which have a significant vapor pressure at and above the temperature where diffusion into the substrate proceeds at a useful rate - generally the temperature at which the substrate fiber begins to decompose or densify. For example, for SiCO ceramic fibers, this can be as low as 1200°C. for slow temperature heating (ramp) rates (eg., <1°C./min) or 1400 - 1500°C. for heating rates of several degrees per minute or more. It is advantageous to have the volatile sintering aid present during the entire heat treatment subsequent to onset of substrate fiber decomposition or densification. However, it is also possible to hold the substrate fiber at a temperature at or above its decomposition or densification point in a sintering aid-containing atmosphere for a time sufficient to allow incorporation of sintering aid into the substrate fiber. The fiber may then be heated further in the absence of sintering aid vapor to complete the densification process. Examples of sintering aids include compounds of iron, magnesium, lithium, beryllium, boron, aluminum, thorium, yttrium, lanthanum, cerium and various other metals. Many of these sintering aids are described in Negita, "Effective Sintering Aids for Silicon Carbide Ceramics: Reactivities of Silicon Carbide with Various Additives," 69 J. Am. Ceram. Soc. C-308 (1986). Other metal-containing sintering aids suggested by Negita might also be effective in the practice of this invention. Preferred sintering aids are selected from boron, boron-containing compounds, aluminum and aluminum-containing compounds. Boron and boron-containing compounds are generally more preferred with boron oxides such as B 2 O 3 being most preferred. Mixtures of sintering aids may also be used. The sintering aid is generally used by merely introducing it into the environment for pyrolysis in its volatile state. This can be accomplished, for example, by placing solid or liquid sintering aids in the furnace and allowing them to volatilize under the heat of the furnace. Alternatively, the sintering aid could be volatilized outside the furnace and introduced during heating. The volatile sintering aid could be used neat, it could be diluted in a carrier gas (eg., inert gases such as argon, helium, etc.) or it could be added under a vacuum. Generally, the time for exposure to the volatile sintering aid atmosphere is not critical so long as exposure continues at least until the desired densification is complete or until sufficient sintering aid has been incorporated in the fiber to produce densification during subsequent thermal treatment in the absence of additional volatile sintering aid. The amount of sintering aid used is, likewise, generally not critical as long as crystallite growth and porosity are minimized and, thus, fiber strength remains acceptable. The resultant polycrystalline fibers have at least 0.1% by weight sintering aid incorporated therein. The ceramic fibers are heated in the environment comprising the sintering aid at a temperature sufficient to convert the ceramic fiber to polycrystalline fiber and allow for evolution of any material that is released during decomposition. This temperature is greater than 1500°C., preferably in the range of about 1600-2200°C., and most preferably in the range of 1700-2000°C. It should be noted that this temperature should also be at least equivalent to that expected in any subsequent processing and/or the final utility. The rate at which the fibers are heated and the holding times (holds) at the maximum temperature are also not critical as long as they allow for diffusion of the sintering aid into the fiber and the escape of volatile by-products. Heating rates in the range of 1-50°C./minute with either no hold or holding times up to several hours are generally used. The total thermal exposure of the fiber which is dependant on heating rate, maximum temperature and time at maximum temperature does, however, often affect fiber characteristics such as modulus and grain growth. It should be noted that the above process describes the conversion of preformed ceramic fibers (eg., from a commercial source) to polycrystalline silicon carbide fibers. The ceramic fibers which result from the process of this invention have at least 75% crystallinity and have a density of at least 2.9 gm/cc, which represents at least 90% of the theoretical density of SiC. They generally have tensile strengths greater than about 100 Ksi (0.69 GPa) and often in excess of 200 Ksi (1.38 GPa). The fibers also have a relatively smooth surface structure and generally have an average grain size less than 1 micrometer, often less than 0.5 micrometer and typically less than 0.2 micrometer. The fibers can have a wide variety of diameters depending on the original ceramic fiber with diameters in the range of 5-20 micrometers being the most common. Virtually all of the oxygen and/or nitrogen originally present in, or introduced into, the fibers is removed by the high temperature pyrolysis step, except for any nitrogen which may be converted to the nitride of the sintering aid. The following non-limiting examples are included in order that one skilled in the art may more readily understand the invention. Example 1 (comparative) Several 3 inch (7.6 cm) long tows of Ceramic Grade NICALON™ fiber obtained from Nippon Carbon Company (Si 1 C 1.35 O 0.44 ) were desized by heating at 600°C. for 0.5 hours in air. The fibers were then placed on a sheet of Grafoil™ in a furnace and ramped up at 10°C./minute to 1800°C. with a 0.5 hr hold at 1200°C. and a 1 hour hold at 1800°C., all under 99.998% argon. The fiber lost 29.3% of its weight and was too weak and crumbly for tensile strength measurement. SEM examination showed filaments to have large-grained, porous cross-sections and extremely large grained surfaces. Example 2 Several 3 inch (7.6 cm) long tows of the same Ceramic Grade NICALON TM fiber lot used in Example 1 were desized as in Example 1 and laid on a sheet of Grafoil TM inside a loosely closed graphite crucible which also contained 0.2-0.3 g of boron oxide (B 2 O 3 ) in a small Grafoil TM dish. The fibers and boron oxide were heated in a furnace as in Example 1. The resultant fiber had lost 28.4 percent of its weight, but retained 181 +/- 50 ksi (1.25 +/-0.3 GPa) tensile strength. Fractography showed critical flaws to be small surface pits - sites of localized unusual degradation rather than widespread grain growth and porosity development. Elastic modulus was 59.3 +/- 3.1 Msi (0.41 +/1 0.02 TPa) and density was >3.1 g/cc, both near expected values for polycrystalline SiC and well above those of the initial Nicalon TM fiber (26.3 +/- 0.7 Msi (0.18 +/- 0.005 TPa) and 2.54 g/cc, respectively). SEM examination showed filaments to have fine grained, low porosity cross-sections that appeared uniform from surface to core. X-ray diffraction line broadening measurements showed the fiber to be Beta-SiC with average crystallite size < 0.1 micrometer. Fiber surfaces were smooth having developed only a faint, small-scale texture. Example 3 Approximately 50 feet (15.24 m) of the same Ceramic Grade NICALON TM fiber lot used in Example 1 was desized as in Example 1 and wound onto a collapsible spool made of Grafoil TM . The spool was heated with 0.301 g of boron oxide (B 2 O 3 ) in the same manner as Example 2. This yielded 1.90 g of tow with a uniform shiny grayish appearance. The resultant fibers retained tensile strength of 211 +/- 69 ksi (1.46 +/- 0.5 GPa), elastic modulus of 64.4 +/- 4.1 Msi (0.44 +/- 0.03 TPa) and density >3.1 g/cc. SEM examination showed dense fine grained uniform cross-sections. Tow strength was good, but weak spots at kinks (where laid across sharp edges on the collapsible spool) inhibited rewinding to another spool. The fiber had the following composition: silicon - 68.1 wt.%; carbon - 31.5 wt.%; nitrogen - 0.41 wt.%; oxygen - 0.115 wt.%; and boron - 0.39 +/- 0.05 wt.%. These fibers were thermally aged by heating to 1600°C. under argon for 12 hours. The fibers had a weight loss of 0.61% and retained 83% of their tensile strength (1.21 +/- 0.34 GPa) (176 +/- 49 ksi). The fibers were also thermally aged by heating to 1800°C. under argon for 12 hours. The fibers had a weight loss of 0.3 % and retained 83% of their tensile strength (1.21 +/- 0.47 GPa) (176 +/- 68 ksi). Example 4 A 3.5 inch (8.9 cm) diameter cylinder was created with 29.353 g of HVR NICALON TM cloth consisting of a single sheet of cloth wound 3 times. On this cloth was wound 5.46 g. (22.9 m. or 75 feet) of Ceramic Grade NICALON TM fiber tow. The cloth/fiber was desized as in Example 1 and heated with 0.501 g of boron oxide (B 2 O 3 ) in the same manner as Example 2. The continuous fiber was easily rewound onto a conventional spool in its entirety, although tow strength was not as good as Example 3. SEM examination showed porous large grained cross-sections. The fiber contained an average bulk boron concentration of 0.30 +/- 0.05 wt%. Tows of fiber within the NICALON cloth appeared to have the same strength as the above fiber of this Example. The cloth remained flexible enough to be repeatedly rolled out flat and recoiled. Example 5 Approximately 50 feet (15.24 m) of the Ceramic Grade NICALON™ fiber used in Example 1 was coiled loosely and heated with 0.72 g of boron oxide (B 2 O 3 ) in the same manner as Example 2. The fiber matted together during treatment but was easily wound on a storage spool once separated. The resultant fibers had a dense fine grained cross-section and contained 2.66 wt% boron. They retained a tensile strength of 166 +/- 42 ksi (1.15 +/- 0.29 GPa) and an elastic modulus of 48.7 +/- 5.2 Msi (0.34 +/- 0.04 TPa). Example 6 TYRANNO™ TRN-M1601 fiber (Si 1 C 1.4 O 0.7 Ti 0.02 ) was desized and heated with boron oxide in the same manner as Example 2. The resultant fibers were shiny and nearly black with dense fine-grained cross-section. They retained tensile strength of 251 +/- 51 ksi (1.73 +/- 0.35 GPa) and elastic modulus of 40.1 +/- 1.7 Msi (0.28 +/- 0.01 TPa). Example 7 TYRANNO™ Lox M fiber (Si 1 C 1.4 O 0.4 Ti 0.02 ) was heated with boron oxide in the same manner as Example 2. The resultant fibers were shiny and nearly black with dense fine-grained cross-section. They retained tensile strength of 319 +/- 70 ksi (2.2 +/- 0.48 GPa) and elastic modulus of 58.6 +/- 3.4 Msi (0.4 +/- 0.02 TPa). Example 8 A SiCNO fiber made by the spinning, air curing and pyrolysis of a phenyl vinyl modified methylpolydisilylazane polymer (made by the process of U.S. Patent No. 4,340,619) of the empirical structure (Si 1 C 1.36 N 0.58 O 0.22 ) was heated with boron oxide in the same manner as Example 2. The resultant fiber had smooth exterior surfaces and small grain size, but the interior contained a considerable amount of small scale porosity. The fiber contained 31.8 wt% carbon and 2.41 wt% nitrogen and had a tensile strength of 77 +/- 23 Ksi (0.53 +/- 0.16 GPa) and modulus of 23.1 Msi (0.16 TPa). Example 9 (comparative) A SiCNO fiber made by the spinning, curing and pyrolysis of hydridopolysilazane polymer (made by the process of U.S. Patent No. 4,540,803) of the empirical structure (Si 1 C 0.4 N 0.92 O 0.12 ) was heated with boron oxide in the same manner as Example 2. The resultant fiber was fragile and SEM examination showed a very porous, large-grained structure. Proper densification did not occur because the silicon content of the polymer was significantly greater than the sum of the carbon and oxygen contents on an atomic basis. Example 10 Several 3 inch (8.9 cm) long tows of the same Ceramic Grade NICALON™ fiber lot used in Example 1 were desized as in Example 1 and laid on a sheet of Grafoil™ inside a loosely closed graphite crucible which also contained 0.3 g of boron oxide (B 2 O 3 ) in a small Grafoil™ dish. The fibers and boron oxide were then placed in a furnace and ramped up at 10°C./min to 1500°C. with a 0.5 hour hold at 1200°C. and a 2 hour hold at 1500°C., all under 99.998% argon. The resultant fiber had lost 25.9 percent of its weight, but retained 184 +/- 27 ksi (1.27 +/- 0.19 GPa) tensile strength. Elastic modulus was 29.0 ± 1.5 Msi (0.2 +/- 0.001 TPa). The fibers were then laid on a Grafoil TM sheet and placed in a furnace with no additional boron oxide present and ramped up at 10°C./min. to 1800°C. with a 0.5 hour hold at 1200°C. and a 1 hour hold at 1800°C., all under 99.998% argon. A 3.3% weight loss occurred during this process, but the tensile strength of the product fiber was 226 ± 69 Ksi (1.56 +/- 0.48 GPa) and its modulus had risen to 61.3 ± 4.7 Msi (0.43 +/- 0.03 TPa). SEM examination showed a microstructure similar to that obtained with a 1-step treatment as described in Example 2.

Claims: A process for the aftertreatment of a ceramic fiber containing silicon and carbon which comprises converting the ceramic fiber to a polycrystalline silicon carbide fiber which has at least 75% crystallinity and a density of at least 2.9 gm/cc by heating the ceramic fiber to a temperature of at least 1500°C characterised in that the said heating of the ceramic fiber is effected in an atmosphere comprising a volatile sintering aid for a time sufficient to allow incorporation of at least 0.1% by weight of the sintering aid into the fiber. The process of claim 1 wherein the ceramic fiber additionally contains elements selected from oxygen, nitrogen, titanium, zirconium and chlorine. The process of claim 1 wherein the ceramic fiber is selected from SiC, SiCO, SiCN, SiCON and SiCOTi. The process of claim 3 wherein the ceramic fiber comprises silicon, carbon and oxygen. The process of claim 4 wherein the carbon content is approximately equal to or greater than the sum of the silicon and oxygen contents on an atomic percent basis. The process of claim 4 wherein the oxygen content is less than about 30 weight percent. The process of claim 1 wherein the volatile sintering aid has a significant vapor pressure at and above the temperature at which the substrate fiber begins to decompose or densify. The process of claim 1 wherein the volatile sintering aid is selected from compounds of iron, magnesium, lithium, beryllium, boron, aluminum, thorium, yttrium, lanthanum and cerium. The process of claim 1 wherein the maximum temperature for heating is in the range of 1500 to 2200°C. The process of claim 1 wherein the fiber is heated in an environment selected from an inert gas and vacuum. The process of claim 1 wherein the volatile sintering aid is present during the entire period at which the pyrolysis temperature is in excess of the fiber decomposition or densification temperature. The process of claim 1 wherein the fiber is heated at a temperature above its decomposition or densification point in the environment comprising the sintering aid for a time sufficient to allow incorporation of at least 0.1% by weight of the sintering aid into the fiber and then further heated in the absence of additional sintering aid. The process of claim 1 wherein the ceramic fiber additionally contains oxygen and at least one element selected from the group consisting of titanium, zirconium and chlorine.

Inventors: LIPOWITZ JONATHAN, RABE JAMES ALAN, LIPOWITZ, JONATHAN, RABE, JAMES ALAN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1993
Main classification: C04B35
IPC codes: C04B35, D01F9, C01B31