Vibration-absorbing elastomeric composite, process for making the same, and vibration damper comprising the same

Abstract: Vibration-absorbing elastomeric composites, having improved vibration-damping properties with improved woldability and resin properties suitable for molded products, are obtained by reacting, insitu in a melted thermoplastic resin such as olefin-diene copolymer, a polyisocyanate with a polyol to for a polyurethane having a nitrogen atom content of at least 3 % and having a solubility parameter which is higher by at least 2.5 than that of said thermoplastic resin.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention : This invention relates to vibration-absorbing elastomeric composites, having improved vibration-damping properties, particularly, those used for the purpose of accelerating damping of vibration and decreasing amplitude in various apparatuses, equipments or devices, vehicles and so on. 2. Description of the Prior Art : Heretofore, as vibration dampers (or vibration insulators), there have been known those comprising polymers, such as natural rubber, butadiene rubber, isoprene rubber, butyl rubber, ethylene-vinyl acetate copolymer, epoxy resin, vinyl chloride resin, or blend of these (for instance JPN Patent Lay-open Nos.227452/1990, 283738/1990 and 759/1991), and those comprising these polymers containing dispersed therein inorganic particles, such as graphite, calcium carbonate, iron oxides, carbon black, mica and the like (for example JPN Patent Lay-open No.227452/1990). These vibration dampers, however, have drawbacks, such that vibration-damping properties are not satisfied because of insufficient damping capacity, effective temperature range remote from room temperature, or narrow effective temperature range; and that their uses are restricted because of poor moldability, or insufficient rigidity and poor shape retention, when they are molded into rubber components to be assembled to structures or machines. FR-A-2299350 provides a process for preparing rapid setting polyurethanes by reacting a polyol with an organic polyisocyanate in the presence of a modifier and a non-amine catalyst. The modifier is a polymer in the form of a liquid or grease. DE-A-2051392 discloses a process for producing a material consisting of rubber granules bound with polyurethane characterised in that the rubber granulate is mixed with at least one polyurethane component, preferably isocyanate, under heating and optionally under pressure such that the granules soften and bind each other. FR-A-2022928 describes a mixture of polyhydroxyl-terminated polymer and a diisocyanate and particles of an incompatible thermoplastic resin. This is formed into a matrix without bringing the incompatible resin to its melting point by treating said mixture at a temperature below the melting point of the incompatible resin. GB-A-2246356 teaches that resin compositions said to have improved dispersibility and mechanical properties can be obtained by polymerizing a polymerizable compound in-situ in a melted thermoplastic resin, in the presence of a dispersant which is reactive or compatible with at least one of the resin and polymerizate of the said polymerizable compound. EP-A-0347794 discloses thermoplastic resinous compositions comprising a polyolefin, a thermoplastic polyurethane and a compatibilizing amount of at least one modified polyolefin. The resulting compositions are said to be soft and flexible and to have high tensile and tear strengths. SUMMARY OF THE INVENTION It is an object of the present invention to provide a vibration-absorbing elastomeric composite having improved damping properties. It is another object of this invention to provide a vibration-absorbing elastomeric composite effective over a wide temperature range including room temperature. It is still another object of the invention to provide a vibration-absorbing elastomeric composite having improved moldability and enough rigidity to be formed into molded products. It is yet another object of the invention to provide a vibration damper or vibration insulator and a vibration-deadened component or member, having improved damping properties. Briefly, these and other objects of the present in vention as hereinafter will become more readily apparent have been attained broadly by a vibration-absorbing elastomeric composite, which comprises (A) 10-60% by weight of at least one thermoplastic resin selected from the group consisting of olefinic polymers, ethylene-unsaturated ester copolymers and natural rubber, said resin (A) having a weight average molecular weight of 10,000 to 3,000,000, and (B) 90-40% by weight of a polyurethane resin, prepared by reacting a polyisocyanate with a polyol in situ in a melted thermoplastic resin (A); said composite having a modulus of 10 7 -10 9 dyne/cm 2 at 20°C and/or a Tan δ of 0.1-1.5 at 20°C and/or a Shore A hardness of at least 20 at 20°C; wherein said polyurethane (B) has a nitrogen atom content, from the isocyanate groups of the polyisocyanate, of at least 3%, and has a solubility parameter which is higher by at least 2.5 (cal/cm 3 ) ½ than that of said thermoplastic resin, and the polyol comprising a high molecular weight polyol having OH equivalent of 250-4,000. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS (A) Thermoplastic resin Suitable examples of the thermoplastic resin (A) include olefinic polymers, ethylene-unsaturated ester copolymers and natural rubbers. Suitable olefinic polymers include (co)polymers (polymers and copolymers; similar expressions are used hereinafter) of monoethylenically Unsaturated hydrocarbon and/or diene, for example, olefins containing 2 to 30 carbon atoms (such as ethylene, propylene, butene-1, isobutene, and C5-30 α-olefins written in US Patent 4,931,483), styrene and homologues thereof (such as C1-18 alkyl-substituted styrenes), and dienes (such as butadiene and isoprene). Illustrative of olefinic polymers are (co)polymers of monoethylenically unsaturated hydrocarbon(s), for example, ethylene-α-olefin (C3-30) copolymers (such as ethylene-propylene copolymer and ethylene-butene-1 copolymer) and polyisobutylene, (co)polymers of diene(s), such as polyisoprene and polybutadiene, and (co)polymers of monoethylenically unsaturated hydrocarbon with diene, such as isobutylene-isoprene copolymer, EPDM (ethylene-propylene-diene terpolymers) and styrene-diene copolymers. Suitable ethylene-unsaturated ester copolymers ethylene-unsaturated acid copolymers include, for example, copolymers of ethylene with vinyl esters (such as vinyl acetate, vinyl propionate and vinyl butyrate), unsaturated carboxylic acids [such as (meth)acrylic, ethacrylic, crotonic, sorbic, maleic, fumaric, itaconic and sinnamic acids], and/or esters (such as C1-18 alkyl esters) of these unsaturated acids [such as methyl, ethyl, n- and i- propyl and butyl, n-octyl, 2-ethylhexyl, lauryl and stearyl (meth)acrylates]. Suitable natural rubbers include those obtained from latex of Hevea brasiliensis . Among these thermoplastic resins (A), preferred are isobutylene-isoprene copolymer and ethylene-propylene copolymer, particularly isobutylene-isoprene rubber and ethylene-propylene rubber (EP rubber). Weight average molecular weight of these thermoplastic resins (A) is usually about 10,000 to about 3,000,000, preferably about 10,000 to about 1,000,000. (B) Polyurethane Resin Polyurethane resin (B) can be prepared by reacting a polyisocyanate (B1) with a high molecular weight polyol (B2) and a chain extender (B3) insitu in a melted thermoplastic resin (A) as mentioned above. In producing said polyurethane resin (B), there may be used any of organic polyisocyanates, conventionally employed for production of polyurethanes. Suitable polyisocyanates (B1) include, for example, aromatic polyisocyanates containing 6-20 carbon atoms [except carbon atoms in NCO groups], such as 1,3- and 1,4-phenylenediisocyanates, 2,4- and 2,6-tolylenediiso-cyanates [TDI], diphenylmethane-2,4'-and 4,4'-diisocyanates [MDI], naphthalene-1,5-diisocyanate, triphenylmethane-4,4',4'-triisocyanate, polymethylenepolyphenylenepolyisocyanates [PAPI] obtainable by phosgenation of aniline-formldehyde condensation products, and m- and p-isocyanatophenylsulfonylisocyanate; aliphatic polyisocyanates containing 2-18 carbon atoms, such as ethylenediisocyanate, tetramethylenediisocyanate, hexamethylenediisocyanate, dodecamethylenediisocyanate, 1,6,11-undecanediisocyanate, 2,2,4-trimethylhexanediisocyanate, lysine diisocyanate, 2,6-diisocyanatomethyl caproate, bis(2-isocyanatoethyl fumarate, bis(2-isocyanatoethyl) carbonate and 2-isocyanatoethyl-2,6-diisocyanato-hexanoate; alicyclic polyisocyanates containing 4-15 carbon atoms, such as isophorone diisocyanate, dicyclohexylmethane diisocyanates, cyclohexylene diisocyanates, methylcyclohexylene diisocyanates and bis(2-isocyanatoethyl) 4-cyclohexene-1,2-dicarboxylate; araliphatic polyisocyanates containing 8-15 carbon atoms, such as xylylene diisocyanates and diethylbenzene diisocyanates; and modified polyisocyanates of these polyisocyanates, containing urethane, carbodiimide, allophanate, urea, biuret, urethdione, urethimine, isocyanurate and/or oxazolidone groups, such as urethane-modified TDI, carbodiimide-modified MDI, urethane-modified MDI; as well as mixtures of two or more of them. Among these polyisocyanates, preferred are aromatic diisocyanates, particularly TDI [including 2,4- and 2,6-isomers, mixtures of them and crude TDI] and MDI [including 4,4'- and 2,4'-isomers, mixtures of them and crude MDI], and modified polyisocyanates containing urethane, carbodiimide, allophanate, urea, biuret and/or isocyanurate groups, derived from TDI and/or MDI. Suitable high molecular weight polyols (B2) employed for producing polyurethanes include, for example, polyether polyols, polyester polyols, polyolefin polyols, and mixtures of two or more of them. Suitable polyether polyols include alkylene oxide (hereinafter referred to as A0) adducts of compounds containing at least two active hydrogen atoms, such as polyhydric alcohols, polyhydric phenols, amines, polycarboxylic acids and phosphrous acids. Suitable examples of polyhydric alcohols include diols, such as ethylene glycol, propylene glycol, 1,3- and 1,4-butane diols, 1,6-hexane diol, neopentyl glycol, diethylene glycol, bis(hydroxymethyl)cyclohexane and bis(hydroxyethyl)benzene; and polyols having 3 - 8 or more hydroxyl groups, such as glycerol, trimethylol propane, trimethylol ethane, hexane triol, pentaerythritol, diglycerol, alphamethylglucoside, sorbitol, xylitol, mannitol, glucose, fructose and sucrose. Exemplary of suitable polyhydric phenols are mono- and poly-nuclear phenols, such as hydroquinone, catechol, resorcin, pyrogallol, and bisphenols [bisphenol A, bisphenol F, bisphenol sulfon and the like], as well as phenol-formaldehyde condensation products. Suitable amines are inclusive of ammonia; alkanol amines, such as mono-, di- and tri- ethanol amines and isopropanol amines; aliphatic, aromatic, araliphatic and alicyclic monoamines, such as C 1 -C 20 alkyl amines [methyl, ethyl, isopropyl, butyl, octyl and lauryl amines, aniline, toluidine, naphthyl amines, benzyl amine and cyclohexyl amine; aliphatic, aromatic, araliphatic and alicyclic polyamines, such as C 2 -C 6 alkylene diamines [ethylene diamine, tetramethylene diamine and hexamethylene diamine], diethylene triamine, tolylene diamines, phenylene diamines, benzidine, methylenedianilines, diphenylether diamines, xylylene diamines, tetramethylxylylene diamines, isophorone diamine, 1,4-diaminocyclohexane and 4,4'-diaminodicyclohexylmethane; and heterocyclic polyamines, such as piperazine, N-aminoethylpiperazine, and other heterocyclic polyamines, written in JPN Patent Publication No.21044/1980. Suitable A0, employed for producing polyether polyols, include, for example, ethylene oxide (hereinafter referred to as E0), propylene oxide (herein-after referred to as P0), 1,2-, 2,3-, 1,3- and 1,4-butylene oxides, styrene oxide and epichlorohydrin, as well as combinations of two or more of them. Among these, preferred are PO and combination of PO/EO [Weight ratio: usually 30/70 - 100/0, preferably 70/30 - 95/5]. Addition of AO to active hydrogen atom-containing compounds can be carried out in the usuall way, with or without catalysts [such as alkaline catalysts, amine catalysts and acidic catalysts], under normal or elevated pressure, in a single step or multi-stages. Addition of different A0's [P0 and E0] may be performed by random-addition, block-addition or combination of them [for instance, random-addition followed by block-addition]. Illustrative of such polyether polyols are polyethylene glycol, polypropylene glycol, polyethylene /propylene(block or random) glycol, polyethylene/ tetramethylene(block or random) glycol, polytetramethylene-ether glycol and polyhexamethyleneether glycol. Suitable polyester polyols are inclusive of condensation products of low molecular weight polyols [dihydric alcohols (such as ethylene glycol, propylene glycol, 1,3- and 1,4-butane diols, 1,6-hexane diol, 3-methyl-1,5-pentane diol, neopentyl glycol, 1,4-dihydroxy-methylcyclohexane and diethylene glycol) and/or trihydric alcohols (such as glycerol and trimethylolpropane)] and/or polyether polyols [such as those described above] with dicarboxylic acids [aliphatic dicarboxylic acids (such as succinic, adipic, sebacic, glutaric, azelaic, fumaric and maleic acids) and/or aromatic dicarboxylic acids (such as phthalic, iso-phthalic and terephthalic acids] or ester-forming derivatives thereof [anhydrides and lower alkyl esters, such as maleic and phthalic anhydrides, dimethyl terephthalate, for example, polyethylene adipate, polybutylene adipate, polyhexamethylene adipate, polyneopentyl adipate, polyethylene/butylene adipate, poly-3-methyl-1,5-pentane adipate and polybutylene iso-phthalate; ring-opening polymerization products of lactones [such as ε-caprolactone, 3-methyl-valerolactone], for instance, polycaprolactone diol and triol, and poly-3-methyl-valerolactone diol; and polycarbonate polyols, such as polyhexamethylene carbonate diol. Illustrative of polyolefin polyols are polydiene polyols (such as polybutadiene glycol and polyisoprene glycol) and hydrogenated products of them. Among these high molecular weight polyols, preferred are polyether polyols. Preferable polyether polyols are ones obtainable by P0/E0 [Weight ratio: preferably 70/30 - 95/5], particularly polyethylene/propylene (random or block) glycol. These high molecular weight polyols have usually 2 - 8 hydroxyl groups, preferably 2 - 4 hydroxyl groups, and have OH equivalent weight of usually 250 - 4,000, preferably 400 -3,000. Suitable chain extenders (B3) include low molecular weight compounds containing at least two [preferably 2-5] active hydrogen atom-containing groups (such as Hydroxyl group and/or amino groups) and having an equivalent weight [molecular weight per active hydrogen atom-containing group] of at least 30 and less than 250, for example, low molecular weight polyols, polyamines and amino alcohols. Illustrative of suitable low molecular weight polyols are dihydric and trihydric alcohols as mentioned above as raw materials for polyether polyols (such as ethylene glycol, diethylene glycol,propylene glycols, 1,3- and 1,4-butane diols, 1,6-hexane diol, glycerol and trimethylolpropane), and low mole A0 adducts of these polyols and/or amines, as well as mixtures two or more of them. Examples of suitable polyamines include aliphatic, aromatic, araliphatic and alicyclic polyamines as mentioned above as raw materials for polyether polyols (such as ethylene diamine, tetramethylene diamine, hexamethylene diamine, diethylene triamine, tolylene diamines, phenylene diamines, benzidine, methylene dianilines, xylylene diamines, tetramethylxylylene diamines, isophorone diamine, 1,4-diaminocyclohexane and 4,4'-diaminodicyclohexylmethane), as well as mixtures two or more of them. Amino alcohols, include, for instance, alkanol amines as mentioned above (such as ethanol amine), and low mole A0 adducts of the above-mentioned diamines (such as N-hydroxyethylethylene diamine). Among these chain extenders (B3), preferred are low molecular weight polyols, particularly diols. In the present invention, polyisocyanate (B1), high molecular weight polyol (B2) and chain extender (B3) are reacted in such a ratio to give said polyurethane resin (B) having a content of nitrogen atoms (contained in the urethane groups) of at least 3 %, preferably at least 5 %, more preferably 6-10 % by weight. Use of polyurethane resin having a nitrogen atom content of less than 3% results in poor vibration-damping properties. In producing said polyurethane resin (B), the amount of chain extender (B3) is generally not more than 60%, preferably 4-50%, based on the total weight of high molecular weight polyol (B2) and chain extender (B3). The average molecular weight of high molecular weight polyol (B2) and chain extender (B3) is usually not more than 600, preferably not more than 500 and at least 100. In general, polyisocyanate (B1) is used in such an amount providing NCO-index of 80-120, preferably 90-110. Polyurethane resins can be produced in known manners, including one-shot process, semi-prepolymer process and prepolymer process. It is essential that said polyurethane resin (B) has a solubility parameter (hereinafter referred to as SP) which is higher by at least 2.5 (cal/cm 3 ) ½ than that of said thermoplastic resin (A). The difference between SP of polyurethane resin (B) and SP of thermoplastic resin (A) is usually 2.5-5.0, (cal/cm 3 ) ½ , preferably 3.0-4.5. SP of thermoplastic resin (A) are usually 7.0-9.0, (Cal/cm 3 ) ½ , preferably 7.5-8.5. In the above, SP can be determined according to Robert F. Fadors, Polymer Engineering & Science, Vol. 14, p. 151, and is represented by a square root of quotient of cohesive energy density divided by molecular volume: SP= ΔE N wherein Δ E is cohesive energy density and V is molecular volume. (C) Compatiblilizer or Dispersant In producing said polyurethane resin (B) by reacting a polyisocyanate (B1) with a high molecular weight polyol (B2) and a chain extender (B3) insitu in a melted thermoplastic resin (A), the reaction may be carried out in the presence of a compatibilizer or dispersant (C). Suitable compatibilizers or dispersants (C) include, for example, those disclosed in GB Patent Application No.9115301.5. Such dispersants include those having a moiety substantially same SP as said thermoplastic resin (A) or said polyurethane resins (B) and at least one reactive group (such as carboxylic, carboxylic anhydride, amino, hydroxyl, isocyanate and epoxy groups), and those having a moiety substantially same SP as said thermoplastic resin (A) and a moiety substantially same SP as said polyurethane resins (B). In the above, substantially same SP means that the difference in SP between the moiety and the resin is not more than 0.5. Illustrative of (C) are maleic (anhydride)-modified polypropylene, maleic (anhydride)-modified polyethylene, amino-modified low molecular weight polypropylene, amino-modified low molecular weight polyethylene, hydroxyl-terminated hydrogenated maleic-modified polypropylene, hydroxyl-terminated hydrogenated maleic-modified polyethylene, and mixtures of 2 or more of them. Among these, preferred are maleic (anhydride)-modified polypropylene and maleic (anhydride)-modified polyethylene. These compatibilizers or dispersants (C) have a number-average molecular weight of usually about 800 - about 3,000,000, preferably about 1,000 - about 1,000,000 Composite In the elastomeric composite of the present invention, the content of thermoplastic resin (A) is usually 10-60 %, preferably 20-40 %, the content of polyurethane resin (B) is 90-40 %, preferably 80-60 %, and the content of compatibilizer or dispersants (C) is generally 0-20 %, preferably 2 - 10 %. In the above and hereinafter, % represents % by weight. The elastomeric composite of this invention may be produced by reacting a polyisocyanate (B1) with a high molecular weight polyol (B2) and a chain extender (B3) insitu in a melted thermoplastic resin (A), optionally in the presence of a compatibilizer or dispersant (C), within any known mixing machine. Suitable mixing machines include, for example, extruders (such as twin-screw extruder), kneaders, Banbury mixers and planetary mixers. The reaction can be carried out at a temperature of generally 10-350°C, preferably 100-300°C, under a normal pressure or under pressure of upto 20 atm., preferably upto 10 atm. It is preferred for inhibiting thermal degradation to carry out the reaction within a period of time as short as possible, for instance, 0.8 - 60 minutes, preferably 1 - 30 minutes. In producing composites according to this invention, there may be used, if necessary, any known materials, such as catalysts [for example, organo-matal compounds (particularly organo-tin compounds, such as dibutyltin dilaurate, dioctyltin dilaurate and stannous octoate) and/ or amine compounds (such as triethyl amine, triethylene diamine and diazabicycloundecene); mold-release agents (such as hydrocarbon waxes and silicone compounds), lubricants, plasticizers, colorants (pigments and dyes), blowing agents [halogenated hydrocarbons (such as methylene chloride, chloroform, ethylidene dichloride, vinylidene chloride, trichlorofluoromethane, dichlorofluoromethane) and/or water], stabilizers (weathering stabilizers and thermal stabilizers, such as age antioxidants and resistors), flame-retardants (such as phosphorus compounds, halogen compounds and Sb 2 O 3 ), surfactants (such as silicone surfactants), coupling agents, germicides, fillers (such as carbon black, titanium dioxide, diatomaceus earth, glass fiber, shattered glass fiber, talc, mica, silica, sand, aluminum powder, graphite and asbestos) and other auxiliaries, usually employed in producing polyurethanes. Composites of the invention may be molded according to any known method, for example, by injection molding, extrusion molding and compression molding. Injection molding is preferred in view of workability and productivity. Composites according to the present invention show high vibration-damping properties (such as Tan δ of 0.1 or more) over a wide temperature range (such as -20°C to 60° C). Besides, these composites have, over such a wide temperature range, high resin strengths, such as modulus of 10 7 -10 9 dyne/cm 2 and Shore A hardness of at least 20. Accordingly, composites of this invention are useful as vibration dampers or vibration insulators in various applications, for example, as vibration-deadened components or members, in transports, including vehicles, such as automobiles and railway rolling stocks, aircrafts and water craft; members, requiring damping properties, in various industrial machines, various electrical, electronical or other apparatuses or appliances (such as computers, printers, air-conditioners, washing machines, cleaners, acoustic or audio systems, pianos, organs and so on; noize-reducing members in various noise sources in factories and residences; innersoles for sports shoes. Having generally described the invention, a more complete understanding can be obtained by reference to certain specific examples, which are included for purposes of illustration only and are not intended to be limiting unless otherwise specified. In the following examples, parts represents parts by weight, and raw materials and measuring methods used therein are as follows: (1)Raw materials IIR : isobutylene-isoprene rubber (JSR Butyl 065, produced by Japan Synthetic Rubber K.K.). EPR : ethylene-propylene rubber (propylene content:30%, number-average molecular weight:70,000). PEPG : EO adduct of polypropylene glycol (MW:900, EO content: 10%). EG : ethylene glycol. BG : 1,4-butane diol. MDI : 4,4'-diphenylmethane diisocyamate PP-MA : maleic anhydride-modified polypropylene (combined maleic anhydride:10%, number-average molecular weight 5,000: U-Mex 1010, produced by Sanyo Chemical Industries, Ltd.). PEA : polyethylene adipate diol (number-average molecular weight: 2,000). (2) Tan δ and modulus : measured with use of Vibron produced by Orienteck Co., at frequency of 100 Hz and rate of temperature increase of 2°C/minute. (3) Hardness : Shore A in accordance with JIS K6301. Example 1 Into a twin-screw improver (2D25-S, produced by Toyo-seikiseisakusho, 20mm, L/D=25), 35 parts of IIR, 40 parts of PEPG, 3 parts of EG,parts of and 22 parts of MDI were kneaded under melt at a cylinder temperature of 160°C for 10 minutes to obtain a composite [1]. Examples 2, 3, 4 and 5 Example 1 was repeated in accordance with the formulations written in Table 1 to obtain composites [2], [3], [4] and [5]. Evaluation Each composite was injection molded under conditions of cylinder temperature 170°C and mold temperature of 160°C into a bar of 50mmX 5mmX 2mm, followed by measuring Tan δ (20°C), modulus (10 7 dyne/cm 2 ) and hardness of it. The results were as shown in Table 1. For comparison, the results of each bar of 50mm× 5mm× 2mm of vibration-dampers on the market are also shown in Table 1. Example No. Example Comparative Example 1 2 3 4 5 1 2 3 IIR ,parts 35 35 - 20 35 Vibration-dampers on the market EPR ,parts - - 30 - - PEPG ,parts 40 10 26 - 24 IIR, pressure moled at 160°C SBR, pressure moled at 200°C PU , pressure moled at 180°C PEA ,parts - - - 17 - EG ,parts 3 - 4 - 7 BG ,parts - 9 3 16 - MDI ,parts 22 41 32 47 34 PP-MA,parts - 5 5 - N % of (B) 3.8 7.7 5.5 6.6 5.9 Tan δ 1.2 1.0 1.0 1.1 1.1 0.3 0.1 0.6 Modulus 3.0 4.2 6.5 7.6 7.2 0.5 9.6 0.1 Hardness 42 26 76 85 82 24 78 12 Injection moldability ○ ○ ○ ○ ○ Δ × ×

Claims: A vibration-absorbing elastomeric composite, which comprises (A) 10-60% by weight of at least one thermoplastic resin selected from the group consisting of olefinic polymers, ethylene-unsaturated ester copolymers and natural rubber, said resin (A) having a weight average molecular weight of 10,000 to 3,000,000, and (B) 90-40% by weight of a polyurethane resin, prepared by reacting a polyisocyanate with a polyol in situ in a melted thermoplastic resin (A); said composite having a modulus of 10 7 -10 9 dyne/cm 2 at 20°C and/or a Tan δ of 0.1-1.5 at 20°C and/or a Shore A hardness of at least 20 at 20°C; wherein said polyurethane (B) has a nitrogen atom content, from the isocyanate groups of the polyisocyanate, of at least 3%, and has a solubility parameter which is higher by at least 2.5 (cal/cm 3 ) 1/2 than that of said thermoplastic resin, and the polyol comprising a high molecular weight polyol having OH equivalent of 250-4,000. A composite according to Claim 1, wherein said olefinic polymer is a homopolymer or copolymer of mono-ethylenically unsaturated hydrocarbon and/or diene. A composite according to Claim 1 or Claim 2, wherein said ethylene-unsaturated ester copolymer is selected from ethylene-vinyl acetate copolymer, ethylene-acrylate copolymer and ethylene-methacrylate copolymer. A composite according to any one of Claims 1 to 3, wherein said polyurethane resin is prepared by reacting a polyisocyanate with a polyol component having a number-average molecular weight of 600 or less. A composite according to any one of Claims 1 to 4, wherein said polyol is a polyalkylene ether polyol. A composite according to any one of Claims 1 to 5, which further comprises a compatibilizer. A process for producing a composite according to any one of Claims 1 to 6, which comprises reacting a polyisocyanate with a polyol in situ in a melted thermoplastic resin (A). A vibration damper or vibration insulator, which comprises a composite according to any one of Claims 1 to 6 or a composite prepared according to Claim 7. Use of a composite according to any one of Claims 1 to 6 or a composite prepared according to Claim 7, in a vibration-deadened component or member, particularly that in a vehicle.

Inventors: ANDO TAKAO, GOHDA KATSURA, ICHIHARA EIJI, ITAYAMA HIROSHI, ANDO, TAKAO, GOHDA, KATSURA, ICHIHARA, EIJI, ITAYAMA, HIROSHI
Applicants: SANYO CHEMICAL IND LTD, SANYO CHEMICAL INDUSTRIES, LTD.
Application year: 1993
Main classification: C08L75
IPC codes: C08L87, C08L23, F16F15, C08L71, C08L75, C08G18, F16F7