Hydrosilylative compositions and hydrosilylation reaction processes

Abstract: A blend of (A) an acrylic, polyester or epoxy resin having at least two alkenyl or alkynyl groups in a molecule, (B) an organic silicon compound having at least two hydrogen atoms each directly attached to a silicon atom in a molecule, and (C) a hydrosilylaion catalyst is blended with (D) an organic iron or aluminum compound to form a hydrosilylative composition. Component (D) scavenges a catalyst poison, permitting components (A) and (B) to undergo hydrosilylation reaction with the aid of catalyst (C).

Description: This invention relates to a hydrosilylative composition comprising an acrylic, polyester or epoxy resin having an aliphatic unsaturated bond, a compound having a silylidyne radical and a hydrosilylation catalyst such as platinum and a hydrosilylation reaction process of subjecting the former two compounds to hydrosilylation reaction in the presence of the catalyst. More particularly, it relates to a hydrosilylative composition and process which permit hydrosilylation reaction to readily proceed even in a system which contains or contacts with catalyst poisons. It is well known that acrylic, polyester or epoxy resins having an aliphatic unsaturated bond and compounds having a silylidyne (≡ SiH) radical undergo hydrosilylation reaction in the presence of hydrosilylation catalysts such as platinum or rhodium series catalysts whereby curing takes place through addition of the silylidyne radical to the unsaturated bond. A variety of curable resin compositions which cure through such hydrosilylation reaction are known. Since the hydrosilylation reaction is high in reactivity, curing of resin compositions through hydrosilylation reaction has the advantage that the compositions cure uniformly both at the surface and the interior and with a minimal volume loss. Another advantage is that an overall process from mixing of components to form a composition to the end of curing is energy saving. Owing to these advantages, coupled with availability in liquid form and ease of handling without a need for special equipment or techniques, such curable resin compositions now find widespread use in a variety of fields. For example, they are used for electrical insulation, mold patterning, junction coating, optical fibers, LIMS molding, silicone gel, release paper, and tackifiers. However, the hydrosilylation reaction is sensitive to catalyst poisons. More particularly, if such elements as N, P, S, Sn and As, even in trace amounts, are present in the compositions, or if such elements are present in substrates on which the compositions are coated and cured, then these elements act as catalyst poisons and considerably inhibit hydrosilylation reaction. Retarded hydrosilylation reaction can result in short curing. It is accordingly common practice to carry out hydrosilylation reaction while utilizing suitable catalyst poison scavenging means. That is, catalyst poisons can be removed from the composition itself or from the substrate on which the composition is coated and cured, for example, by pretreating the components of the composition with activated carbon or by heat cleaning the substrate to pyrolytically decompose off the catalyst poisons. It is also possible to carry out hydrosilylation reaction by raising the reaction temperature to enhance the activity of the hydrosilylation catalyst or by increasing the amount of hydrosilylation catalyst added. These approaches, however, are disadvantageous both in process and economy. It would be desirable to ensure that the hydrosilylation reaction can proceed even in the presence of trace amounts of catalyst poisons. We proposed (in Japanese Patent Application Nos. 277645/1991 and 276965/1991) to subject a composition based on an aliphatic unsaturated group-containing resin to hydrosilylation reaction with organohydrogenpolysiloxane for crosslinking. This composition tends to experience short curing when contacted with crosslinked melamine or urethane coatings. There is a desire for improvement in this respect. In the coating field, there are some known examples of resin compositions crosslinking through hydrosilylation reaction in a system containing such elements as N, P, S, Sn and As or a system in contact with a material containing such an element. Such known solutions include (a) curing systems in which hydrosilylation reaction is combined with another distinct curing system, and (b) coating by laying two coats in a single baking step. In the composite curing system (a), the other curing system distinct from hydrosilylation reaction is, for example, a curing system based on addition reaction of a hydroxyl-containing resin and a polyisocyanate or a block thereof, or a curing system based on addition reaction of a carboxyl-containing resin with an epoxy-containing resin. In these systems, alkyl ether melamine resins, polyisocyanate and amine compounds (e.g., tributylammonium bromide) used as a catalyst for reaction between carboxyl and epoxy groups form nitrogenous components. Also phosphates, sulfonates (e.g., para - toluenesulfonate), and tin compounds (e.g., dibutyltin dilaurate) used as a reaction catalyst for the curing system form components containing P, S or Sn. These systems do not drive hydrosilylation reaction forward. One known example of the latter system, that is, coating using two coats/one bake is a metallic base coating/clear coating system. The clear coating has a system of curing by hydrosilylation reaction and the base coating has a different curing system. However, hydrosilylation reaction is inhibited if the base coating contains a catalyst poison. There is a desire to have a coating technique capable of driving hydrosilylation reaction even in the presence of or contact with such catalyst poisons. A general aim herein is to provide novel hydrosilylation compositions and methods of using and preparing them, preferably compositions and processes which permit hydrosilylation reaction to proceed without inhibition even in the presence of trace amounts of catalyst poisons including such elements as N, P, S, Sn and As. Regarding the hydrosilylation reaction between an acrylic, polyester or epoxy resin having at least two alkenyl or alkynyl groups in a molecule and an organic silicon compound having at least two hydrogen atoms each directly attached to a silicon atom in a molecule in the presence of a hydrosilylation catalyst, the inventors have found that the poisoning of a catalyst poison component containing N, P, S, Sn or As is inhibited if organic iron compounds such as iron octylate, iron naphthenate and iron acetylacetate or organic aluminum compounds, for example, aluminum alkoxides such as aluminum butoxide, aluminum isobutoxide, and aluminum isopropoxide and aluminum chelates such as acetylacetonatoaluminum and ethylacetoacetonatoaluminum are present in the reaction system. Then even when such a catalyst poison component is contained in a composition or a substrate with which the composition comes in contact, hydrosilylation reaction can take place relatively freely. The compositions obtained maintained good properties, e.g. a minimal volume loss on curing, and advantages including acid resistance, weathering resistance, solvent resistance, overcoating capability, and mechanical strength. Thus, broadly the invention provides the use of such iron and/or aluminium compounds to inhibit catalyst poisoning in this context. A first aspect provides a hydrosilylative composition as defined in claim 1, comprising (A) an acrylic, polyester or epoxy resin having at least two alkenyl or alkynyl groups in a molecule, (B) an organic silicon compound having at least two hydrogen atoms each directly attached to a silicon atom in a molecule, (C) a hydrosilylation catalyst, and (D) at least one of an organic iron compound and an organic aluminum compound. In a second aspect, as defined in claim 7, the present invention provides a hydrosilylation reaction process comprising the step of subjecting (A) an acrylic, polyester or epoxy resin having at least two alkenyl or alkynyl groups in a molecule and (B) an organic silicon compound having at least two hydrogen atoms each directly attached to a silicon atom in a molecule to hydrosilylation reaction in the presence of (C) a hydrosilylation catalyst, while using (D) at least one of an organic iron compound and an organic aluminum compound in the reaction system. It is not well understood why the addition of an organic iron or aluminium compound permits hydrosilylation reaction to take place even in the presence of a catalyst poison component containing N, P, S, Sn or As. Though not bound by theory, we hypothesise as follows. If a catalyst poison is present, a Group VIII transition metal catalyst acting as hydrosilylation catalyst coordinates with the catalyst poison so that the hydrosilylation reaction is stopped. However, if the hydrosilylation reaction is effected in a system where a Group VIII transition metal catalyst coexists with an organic iron or aluminium compound, the organic iron or aluminium compound preferentially coordinates with the catalyst poison so that the Group VIII transition metal may remain active. Then even in the presence of a catalyst poison, hydrosilylation reaction can proceed in the same manner as does a catalyst poison-free system. The hydrosilylative composition according to the first aspect of the present invention can be prepared as a curable resin composition and includes (A) an acrylic, polyester or epoxy resin having at least two alkenyl or alkynyl groups in a molecule, (B) an organic silicon compound having at least two silylidyne (≡SiH) radicals in a molecule, and (C) a hydrosilylation catalyst. Component (A) is an acrylic, polyester or epoxy resin which is not particularly limited provided that it has at least two alkenyl or alkynyl groups in a molecule. Exemplary alkenyl groups include aliphatic unsaturated hydrocarbon groups such as vinyl, allyl, methylvinyl, propenyl, butenyl, isobutenyl, isophenyl, pentenyl and hexenyl groups, and cyclic unsaturated hydrocarbon groups such as cyclopropenyl, cyclobutenyl, cyclopentenyl and cyclohexenyl groups. Exemplary alkynyl groups include ethynyl, propargyl and α , α-dimethylpropargyl groups. Alkenyl-containing acrylic resins can be prepared by copolymerizing alkenyl-containing (meth)acrylates with other radically polymerizable monomers. Examples of the alkenyl-containing (meth)acrylate include alkenyl-containing acrylic monomers such as allyl (meth)acrylate, 3-methyl-3-butenyl (meth)acrylate, 2-butenyl (meth)acrylate, cyclohexenylmethyl (meth)acrylate, 3-methyl-2-butenyl (meth)acrylate, etc. Examples of the radically polymerizable monomer include methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, i-butyl (meth)acrylate, t-butyl (meth)acrylate, 2 - ethylhexyl (meth)acrylate, lauryl (meth)acrylate, phenyl (meth)acrylate, benzyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 4 - hydroxybutyl (meth)acrylate, 2 - hydroxyethyl (meth)acrylate and ε-caprolacetone adducts, glycidyl (meth)acrylate, 3 - trimethoxysilylpropyl (meth)acrylate, 3-triethoxypropyl (meth)acrylate, (meth)acrylic 2-acrylamide, (meth)acrylamide, (meth)acryloyl isocyanate, 2 - isocyanatoethyl (meth)acrylate, vinyl acetate, allyl acetate, styrene, α-methylstyrene, vinyltrimethoxysilane, vinyltriethoxysilane, maleic acid, itaconic acid, vinylmethyldimethoxysilane, and vinylmethyldiethoxysilane. Also useful are alkenyl-containing acrylic resins which are obtainable by addition reaction between hydroxyl-containing acrylic resins and alkenyl isocyanate compounds and/or alkenyl - containing carboxylic anhydrides, addition reaction between isocyanato-containing acrylic resins and alkenyl alcohols, addition reaction between carboxyl-containing acrylic resins and alkenyl-containing epoxy compounds, and addition reaction between epoxy-containing acrylic resins and alkenyl-containing carboxylic acids. Alternatively, alkenyl-containing acrylic resins may be obtainable by copolymerizing a hydroxyl-containing acrylic monomer such as hydroxybutyl (meth)acrylate and adducts of 2-hydroxyethyl (meth)acrylate and ε-caprolactone (e.g., Praccell FM series commercially available from Daicell Chemical Industry K.K.) with another one of the above-mentioned acrylic monomers and less than 50% by weight of an α , β-unsaturated vinyl monomer or by polymerizing hydroxyl-containing acrylic monomers singly (homopolymers). Among the above-mentioned components, examples of the alkenyl isocyanate compound include allyl isocyanate, (meth)acryloyl isocyanate, and 2-isocyanatoethyl (meth)acrylate. Exemplary alkenyl-containing carboxylic anhydrides are itaconic anhydride and maleic anhydride. Examples of the isocyanato-containing acrylic resin include those resins obtainable by copolymerizing an isocynato-containing acrylic monomer such as (meth)acryloyl isocyanate and 2-isocyanatoethyl (meth)acrylate with another one of the above-mentioned acrylic monomers and less than 50% by weight of an α , β-unsaturated vinyl monomer or by polymerizing an isocyanato-containing acrylic monomer singly (homo-polymers). Exemplary alkenyl alcohols are allyl alcohol, vinyl alcohol, 3-buten-1-ol, and 2-(allyloxy)ethanol. Examples of the carboxyl-containing acrylic resin include those resins obtainable by copolymerizing a carboxyl-containing acrylic monomer such as (meth)acrylic acid with less than 50% by weight of a carboxyl-containing α , β-unsaturated vinyl monomer such as itaconic acid and maleic acid or by polymerizing a carboxyl-containing acrylic monomer singly (homopolymers). Allyl glycidyl ether is an exemplary alkenyl-containing epoxy compound. Examples of the epoxy-containing acrylic resin include those resins obtainable by copolymerizing an epoxy-containing acrylic monomer such as glycidyl (meth)acrylate with another one of the above-mentioned acrylic monomers and less than 50% by weight of an α,β-unsaturated vinyl monomer or by polymerizing an epoxy-containing acrylic monomer singly (homopolymers). Exemplary alkenyl - containing carboxylic acids are allyl acetate, (meth)acrylic acid, 2-butenoic acid, and 3-butenoic acid. Secondly, a polyester resin having at least two alkenyl groups in a molecule may be selected from those obtained by polycondensation of the above-mentioned alkenyl alcohols and polyhydric alcohols with polybasic acids. Examples of the polyhydric alcohol include ethylene glycol, propylene glycol, 1,6-hexane diol, diethylene glycol, neopentyl glycol, hydroxypivalic acid neopentyl glycol ester, trimethylol propane, and both-end alcoholic hydroxyl - terminated dimethylsiloxane. Examples of the polybasic acid include phthalic anhydride, isophthalic acid, terephthalic acid, adipic acid, azelaic acid, and trimellitic acid. If desired, a monohydric alcohol or monobasic acid may be partially used. Also useful are alkenyl-containing polyester resins which are obtainable by subjecting a carboxyl group of polyester resins resulting from polycondensation of the above-mentioned polyhydric alcohols and polybasic acids to addition reaction with the above-mentioned alkenyl-containing epoxy compounds or by subjecting a hydroxyl group of polyester resins resulting from polycondensation of the above-mentioned polyhydric alcohols and polybasic acids to addition reaction with the above-mentioned alkenyl isocyanate and/or alkenyl-containing carboxylic anhydrides. Thirdly, epoxy resins having at least two alkenyl groups in a molecule may be selected from those obtainable by addition reaction of the above-mentioned epoxy-containing acrylic resins or bisphenol-A diglycidyl ether, for example, to the above-mentioned alkenyl-containing carboxylic acids or by addition reaction of a hydroxyl group in epi-bis type epoxy resins to the above-mentioned alkenyl isocyanates and/or alkenyl-containing carboxylic anhydrides. Next, the alkynyl group-containing resins are described. The alkynyl-containing acrylic resins used herein can be prepared by copolymerizing alkynyl-containing acrylic monomers such as propargyl (meth)acrylate, propargyl (meth)acryloylcarbamate, and 2-propargyloxy-carbonyloxyethyl (meth)acrylate with other polymerizable monomers. The alkynyl-containing acrylic monomers may be selected from those obtained by dehydrochlorination reaction between methacrylic chloride and propargyl alcohols or acetylene alcohols, ester exchange reaction between lower esters of (meth)acrylic acid and propargyl alcohols or acetylene alcohols, addition reaction between isocyanato-containing acrylic monomers and propargyl alcohols or acetylene alcohols, and reaction between propargyl chloroformate and 2-hydroxyethyl (meth)acrylate. The other polymerizable monomers are preferably acrylic monomers. Examples of the acrylic monomer include methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, i-butyl (meth)acrylate, t-butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, phenyl (meth)acrylate, benzyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, adducts of 2-hydroxyethyl (meth)acrylate and ε-caprolactone (e.g., trade name Praccell FMI commercially available from Daicell Chemical Industry K.K.), glycidyl (meth)acrylate, 3-trimethoxysilyl-propyl (meth)acrylate, 3-triethoxysilylpropyl (meth)acrylate, 3-dimethoxymethylsilylpropyl (meth)acrylate, (meth)acrylate, (meth)acrylic 2-acrylamido-2-methylpropanesulfonate, acid phosphoxypropyl methacrylate, tributyltin (meth)acrylate, (meth)acrylamide, (meth)acryloyl isocyanate, and 2-isocyanatoethyl (meth)acrylate. Monomers other than the acrylic monomers, for example, styrene, α-methyl-styrene, itaconic acid, maleic acid, vinyl acetate, allyl acetate, vinyltrimethoxysilane, vinyltriethoxysilane, vinylmethyldimethoxy-silane, and vinylmethyldiethoxysilane may also be used for polymerization as the other polymerizable monomers. However, these monomers should preferably be used in amounts of less than 50% by weight. Also, alkynyl-containing acrylic resins may be prepared by reaction between hydroxyl-containing acrylic resins and alkynyl - containing chloroformate or alkynyl-containing carboxylic acids, addition reaction between isocynato-containing acrylic resins and propargyl alcohols or acetylene alcohols, addition reaction between carboxyl-containing acrylic resins and alkynyl-containing epoxy compounds, and addition reaction between epoxy-containing acrylic resins and alkynyl-containing carboxylic acids. Hydroxyl-containing acrylic resins usable herein may be obtained by copolymerizing a hydroxyl-containing acrylic monomer such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 4 - hydroxybutyl (meth)acrylate, and adducts of 2-hydroxyethyl (meth)acrylate and ε - caprolactone (e.g., Praccell FM series commercially available from Daicell Chemical Industry K.K.) with another one of the above-mentioned acrylic monomers and less than 50% by weight of a non-acrylic monomer or by polymerizing a hydroxyl-containing acrylic monomer singly. Propargylic acid is typical of the alkynyl-containing carboxylic acid. Isocyanato-containing acrylic resins usable herein may be obtained by copolymerizing an isocyanato-containing acrylic monomer such as (meth)acryloyl isocyanate and 2-isocyanatoethyl (meth)acrylate with another one of the above-mentioned acrylic monomers and less than 50% by weight of a non-acrylic monomer or by polymerizing an isocyanato-containing acrylic monomer singly (homopolymers). Carboxyl-containing acrylic resins usable herein may be obtained by copolymerizing a carboxyl-containing acrylic monomer such as (meth)acrylic acid and/or less than 50% by weight of a carboxyl-containing non-acrylic monomer such as itaconic acid and maleic acid with another one of the above-mentioned acrylic monomers and/or less than 50% by weight of a non-acrylic monomer or by polymerizing a carboxyl-containing acrylic monomer singly (homopolymers). Propargyl glycidyl ether is typical of the alkynyl-containing epoxy compound. Epoxy-containing acrylic resins usable herein may be obtained by copolymerizing an epoxy-containing acrylic monomer such as glycidyl (meth)acrylate with another one of the above-mentioned acrylic monomers and less than 50% by weight of a non-acrylic monomer or by polymerizing an epoxy-containing monomer singly (homopolymers). Propargylic acid is typical of the alkynyl-containing carboxylic acid. Secondly, polyester resins having at least two alkynyl groups in a molecule may be selected from those obtainable by polycondensation of the above-mentioned alkynyl alcohols and polyhydric alcohols with polybasic acids. Examples of the polyhydric alcohol include ethylene glycol, propylene glycol, 1,6-hexane diol, diethylene glycol, neopentyl glycol, hydroxypivalic acid neopentyl glycol ester, trimethylol propane, and both end alcoholic hydroxyl - terminated dimethylsiloxane. Examples of the polybasic acid include phthalic anhydride, isophthalic acid, terephthalic acid, adipic acid, azelaic acid, and trimellitic acid. If desired, a monohydric alcohol or monobasic acid may be partially used. Also useful are alkynyl-containing polyester resins which are obtainable by addition reaction of a carboxyl group of polyester resins resulting from polycondensation of the above-mentioned polyhydric alcohols and polybasic acids to the above-mentioned alkynyl-containing epoxy compounds or by addition reaction of a hydroxyl group of polyester resins resulting from polycondensation of the above-mentioned polyhydric alcohols and polybasic acids to the above-mentioned alkynyl-containing carboxylic acids. Thirdly, epoxy resins having at least two alkynyl groups in a molecule may be selected from those obtainable by addition reaction of the above - mentioned epoxy - containing acrylic resins or bisphenol-A diglycidyl ether, for example, to the above - mentioned alkynyl-containing carboxylic acids or by addition reaction of a hydroxyl group in epi-bis type epoxy resins to the above-mentioned alkynyl chloroformates and/or acetylene alcohols of alkynyl - containing carboxylic acids. The acrylic, polyester and epoxy resins having alkenyl or alkynyl groups should have a molecular weight of from 500 to 100,000, especially from 2,000 to 50,000. Resins with a molecular weight of less than 500 tend to be low in film forming ability or provide insufficient film strength whereas resins with a molecular weight of more than 100,000 are usually too viscous to work with and then inadequate as high-solids resin compositions. Component (B) is an organic silicon compound which is not particularly limited insofar as it has at least two hydrogen atoms each directly attached to a silicon atom in a molecule. Exemplary are organohydrogensilanes and organohydrogensiloxanes. The organohydrogensiloxanes may be linear, cyclic or network and include from oligomers to polymers although tetrasiloxane and higher ones having a viscosity of up to 10Pa.s (10,000 centipoise) at room temperature are especially preferred when the flexibility of cured coatings and workability are taken into account. Typical structural formulae for component (B) are as follows. R is a monovalent hydrocarbon group, preferably an alkyl, cycloalkyl, aralkyl or aryl group having 1 to 8 carbon atoms. R may be substituted, provided that the substitution does not spoil the curability of the compositions, or other conventionally-desired property. Unsubstituted phenyl or methyl groups are preferable. k and j are integers; k ≧ 2 and j ≧ 0. R and j are as defined above, and m is an integer of m ≧ 0. R and k are as defined above, and n is an integer of n ≧ 1. R p SiH q O (4-p-q)/2 R is as defined above, and p and q are numbers to satisfy 0 < p + q < 2, 0 < p < 2, and 0 < q < 2. Illustrative, non-limiting examples of component (B) are shown below. Components (A) and (B) are blended such that the molar ratio of alkenyl/ alkynyl group in component (A) to hydrogen atom attached to silicon atom in component (B) is in the range from 1:0.5 to 1:50, especially from 1:1 to 1:10. On this basis, if the proportion of component (B) is less than 0.5, crosslinking may be short. If the proportion of component (B) is more than 50, unreacted component (B) may bleed on a coating. Component (C) is a hydrosilylation catalyst which is generally selected from transition metals of Group VIII in the Periodic Table and their compounds. Exemplary Group VIII transition metal compounds are complexes of platinum, palladium, rhodium and ruthenium, for example, such as PtCl 4 , H 2 PtCl 6 ·6H 2 O, Pt-ether complexes, Pt-olefin complexes, PdCl 2 (PPh 3 ) 2 , PdCl 2 (PhCN) 2 , RhCl 2 (PPh 3 ) 3 wherein Ph is phenyl. Other known hydrosilylation catalysts and mixtures of such catalysts are also useful. If desired, these catalysts may be used by diluting with solvents such as alcohol, aromatic, hydrocarbon, ketone and basic solvents. Component (C) is blended in an amount to give 0.1 to 10,000 parts by weight of metal per million parts by weight of component (B). Catalysis may be insufficient with less than 0.1 ppm of component (C) whereas more than 10,000 ppm of component (C) may cause the cured coating to be colored due to the catalyst's own color and is economically disadvantageous since the Group VIII metals are expensive. Catalyst poison controlling component (D) in the form of an organic iron or aluminium compound is used with, e.g. added to a blend of, components (A), (B) and (C). The organic iron and aluminum compounds as component (D) are not particularly limited insofar as they are soluble in components (A) and (B). Exemplary organic iron compounds include ferric organosalts e.g. ferric octylate, ferric acetate, ferric propionate and ferric naphthenate, and acetyl-acetonatoiron. Exemplary organic aluminium compounds are aluminum alkoxides and chelates as shown below. In the formulae, acac is acetylacetonato, Pr is propyl, and Bu is butyl. Component (D) may be included in an amount corresponding to the content of catalyst poison envisaged. Since even trace amounts of catalyst poison can affect hydrosilylation reaction or catalyst component (C), component (D) is preferably used in a weight of 10 to 10,000 times the weight of the metal of component (C) in order to prohibit any such influence. Less than 10 times the metal weight of component (D) may provide insufficient guard against the catalyst poison whereas more than 10,000 times the metal weight of component (D) may cause the cured coating to be cracked or colored with iron. In addition to the essential components (A) to (D), the composition of the present invention may further include an agent for controlling hydrosilylation reaction for the purpose of adjusting ease of operation. Such control agents include acetylene alcohols, siloxane-modified acetylene alcohols, methyl-vinylcyclotetrasiloxane, and hydroperoxides. Their illustrative examples are given below. HC ≡ CCH 2 OH, Such agents are known. These control agents may be added in any desired amount in accordance with desired operating conditions, typically in an amount of 1 to 1,000% of the metal weight of component (C). Also if desired, reinforcing fillers may be used in the compositions. Exemplary fillers are reinforcing silica, ground quartz, iron oxide, alumina and vinyl-containing silicone resins. Various other additives may be used in accordance with the intended use of the composition. Examples include heat resistance modifiers such as oxides and hydroxides of cerium and iron; coloring agents such as organic pigments or dyes and inorganic pigments (e.g., TiO 2 , Fe 2 O 3 , and C); tackifiers such as carbon functional silanes and siloxanes; mold release agents such as silicone fluid, raw rubber and metal fatty acid salts; flame retardants such as zinc carbonate and calcium carbonate; leveling agents; flow control agents; and anti-settling agents. Depending on operating conditions, the composition of the invention may be used without solvent. Where component (A) or (B) is highly viscous or component (A) is solid, it may be dissolved in an organic solvent. The organic solvent used herein is not particularly limited insofar as components (A) to (D) are soluble herein. Exemplary solvents are aromatic hydrocarbons such as benzene, toluene and xylene; aliphatic hydrocarbons such as hexane, heptane and octane; ketones such as acetone, methyl ethyl ketone, cyclohexanone, and methyl isobutyl ketone; esters such as ethyl acetate, butyl acetate and isobutyl acetate; and haloalkanes such as 1,1,1-trichloroethane, trichloroethylene and methylene chloride. Toluene and xylene are preferred for industrial purposes. The procedure of preparing the composition of the invention is not limitative. For example, components (A), (C) and (D) are first dissolved in an organic solvent and the solution is then mixed with component (B). Hydrosilylation reaction will take place in the composition of the invention under conventional conditions, typically by heating at a temperature of 50 to 150°C. EXAMPLE Examples of the invention are given below by way of illustration and not by way of limitation. All parts are by weight. Prior to Examples and Comparative Examples, preparation examples of metallic paint and synthesis examples of various resin solutions are first described. Preparation Example 1 A reactor equipped with a stirrer, thermometer, reflux condenser, nitrogen gas inlet tube and dropping funnel was charged with 220 parts of high-boiling aromatic petroleum naphtha (Solvesso #100, Esso Standard Petroleum) and heated to 150°C while passing nitrogen gas. Thereafter, a mixture (a) shown below was added dropwise to the reactor through the dropping funnel at a constant rate over 3 hours. Mixture (a) Parts by weight Ethyl acrylate 307 Ethyl methacrylate 292 2-hydroxyethyl methacrylate 116 1:1 adduct of 2-hydroxyethyl methacrylate and ε-caprolactone (Paracell FM-1, Daicell K.K.) 217 Methacrylic acid 18 n-dodecylmercaptan 50 t-butylperoxy-2-ethylhexanoate 80 After the completion of addition of mixture (a), the reactor was maintained at the temperature for 30 minutes. Then a mixture of 10 parts of t-butylperoxy-2-ethylhexanoate and 30 parts of Solvesso #100 was added dropwise at a constant rate over 30 minutes. After the completion of addition, the reaction solution was ripened a 150°C for 3 hours and then cooled down, obtaining a resin solution A. The resin had a number average molecule weight of 1,800. The resin solution has a non-volatile content of 69.8% by weight and a Gardner viscosity of Z4. A metallic paint was prepared by mixing 531 parts of resin solution A, 425 parts of methylated melamine (Cymel, Mitsui Toatsu Chemical K.K.), 10 parts of p-toluenesulfonic acid, 240 parts of aluminum paste (Almipaste 7160N, Toyo Alumi K.K.), 10 parts of UV absorber (SEESORB, Shiraishi Calcium K.K.), and 5 parts of 8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazospiro(4,5)decane-2,4-dione (Sanol LS-770, Ciba Geigy) in a conventional manner. The metallic paint was diluted with a solvent mixture (toluene/n-butanol/ethoxyethyl acetate = 3/1/1) to a viscosity of 15 sec./20°C as measured in Ford cup #4, obtaining a metallic paint dilution I . Preparation Example 2 A reactor as used in Preparation Example 1 was charged with 500 parts of ethoxypropanol and heated to 105°C while passing nitrogen gas. Thereafter, a mixture (b) shown below was added dropwise to the reactor through the dropping funnel at a constant rate over 3 hours. Mixture (b) Parts by weight 2-hydroxyethyl methacrylate 140 n-butyl acrylate 165 Methacrylic acid 50 2-ethylhexyl methacrylate 260 Methyl methacrylate 305 Styrene 85 Ethoxypropanol 500 t-butylperoxy-2-ethylhexanoate 60 After the completion of addition of mixture (b), the reactor was maintained at the temperature for 30 minutes. Then a mixture of 3 parts of t-butylperoxy-2-ethylhexanoate and 25 parts of ethoxypropanol was added dropwise at a constant rate over 30 minutes. After the completion of addition, the reaction solution was ripened at 105°C for 3 hours and then cooled down. To the solution was added 25 parts of diethylene glycol monobutyl ether. The solvent was distilled off at 100°C under a vacuum of 10 mmHg. To the solution were added 48 parts of diethanolamine and 3750 parts of deionized water, obtaining a resin solution B. The resin had a number average molecule weight of 3,800. The resin solution has a non-volatile content of 20.1% by weight and a viscosity of 80 centipoise. An agitation mixer was charged with 12 parts of aluminum paste (Almipaste 7160, Toyo Alumi K.K.) and 5 parts of butyl cellosolve, which were agitated for one hour to form an aluminum pigment concentrate. A metallic paint was prepared by mixing the aluminum pigment concentrate with 233 parts of resin solution B, 30 parts of methylated melamine (Cymel, Mitsui Toatsu Chemical K.K.), and 2 parts of p-toluenesulfonic acid in a conventional manner. The metallic paint was diluted with a solvent mixture (toluene/n-butanol/ethoxyethyl acetate = 3/1/1) to a viscosity of 15 sec./20°C as measured in Ford cup #4, obtaining a metallic paint dilution II . Synthesis Example 1 A reactor as used in Preparation Example 1 was charged with 500 parts of xylene and heated to 130°C while passing nitrogen gas. Thereafter, a mixture (c) shown below was added dropwise to the reactor over 6 hours. Mixture (c) Parts by weight Allyl methacrylate 40 n-butyl methacrylate 50 2,4-diphenyl-4-methyl-1-pentene 10 t-butylperoxy-2-ethylhexanoate 10 After the completion of addition of mixture (c), the reactor was maintained at the temperature for 30 minutes. Then a mixture of 1 part of t-butylperoxy-2-ethylhexanoate and 10 parts of xylene was added dropwise at a constant rate over 30 minutes. After the completion of addition, the reaction solution was ripened at 130°C for 3 hours and then cooled down. The solvent was distilled off at 60°C under a vacuum of 10 mmHg, obtaining a resin solution C. The resin had a number average molecule weight of 2,200. The resin solution has a non-volatile content of 56.2% by weight and a Gardner viscosity of S - T. Synthesis Example 2 A reactor as used in Preparation Example 1 was charged with 90 parts of Solvesso #100 and heated to 120°C while passing nitrogen gas. Thereafter, a mixture (d) shown below was added dropwise to the reactor over 3 hours. Mixture (d) Parts by weight Styrene 30 n-butyl methacrylate 20 3-methyl-3-butenyl methacrylate 50 2,2'-azobis(2-methylbutyronitrile) 5 After the completion of addition of mixture (d), the reactor was maintained at the temperature for 30 minutes. Then a mixture of 0.5 part of 2,2'-azobis(2-methylbutyronitrile) and 4.5 parts of Solvesso #100 was added dropwise at a constant rate over 30 minutes. After the completion of addition, the reaction solution was ripened at 120°C for 3 hours and then cooled down, obtaining a resin solution D. The resin had a number average molecule weight of 5,000. The resin solution has a non-volatile content of 51.9% by weight and a Gardner viscosity of H. Synthesis Example 3 A resin solution E was prepared by the same procedure as Synthesis Example 2 except that the 3-methyl-3-butenyl methacrylate was replaced by 2-butenyl methacrylate. The resin had a number average molecule weight of 4,700. The resin solution has a non-volatile content of 48.9% by weight and a Gardner viscosity of F. Synthesis Example 4 A resin solution F was prepared by the same procedure as Synthesis Example 2 except that the 3-methyl-3-butenyl methacrylate was replaced by 2-propargyloxycarbonyloxyethyl methacrylate. The resin had a number average molecule weight of 2,500. The resin solution has a non-volatile content of 46.9% by weight and a viscosity of 129 centipoise at 25°C. Synthesis Example 5 A reactor as used in Preparation Example 1 was charged with 90 parts of Solvesso #100 and heated to 130°C while passing nitrogen gas. Thereafter, a mixture (g) shown below was added dropwise to the reactor over 3 hours. Mixture (g) Parts by weight Styrene 30 n - butyl methacrylate 20 Cyclohexenylmethyl methacrylate 50 t - butylperoxy - 2 - ethylhexanoate 7 After the completion of addition of mixture (g), the reactor was maintained at the temperature for 30 minutes. Then a mixture of 0.5 parts of t-butylperoxy-2-ethylhexanoate and 3.6 parts of Solvesso #100 was added dropwise at a constant rate over 30 minutes. After the completion of addition, the reaction solution was ripened at 130°C for 3 hours and then cooled down, obtaining a resin solution G. The resin had a number average molecule weight of 3,600. The resin solution has a non-volatile content of 75.3% by weight and a Gardner viscosity of higher than Z6. Synthesis Example 6 A reactor equipped with a decanter was charged with 42.2 parts of dimethyl terephthalate, 15.1 parts of hydroxypivalic acid neopentyl glycol ester, 6.6 parts of trimethylol propane, 36.9 parts of a silicone compound of the following general formula, and 0.05 parts of dibutyltin oxide. The reactor was heated to 150°C and then heated from 150°C to 220°C over 10 hours for effecting condensation reaction until the removal of methanol reached 10 parts. Thereafter, the reaction temperature was raised to 100°C, 12.5 parts of glycerin diallyl ether was added to the reaction system, which was heated to 220°C over 2 hours, maintained at the temperature for 2 hours and then cooled down. The methanol removed totaled to 13 parts. The reaction solution was combined with 66 parts of xylol, obtaining a resin solution H. The resin had a number average molecule weight of 2,500. The resin solution has a non-volatile content of 57.7% by weight and a Gardner viscosity of J. Examples 1-6 & Comparative Examples 1-2 A series of clear coating compositions, which are hydrosilylative compositions, were prepared by mixing the components as shown in Table 1 to a viscosity of 25 sec./20°C as measured in Ford cup #4. Clear coating composition I was spray coated onto a soft steel strip (which had been degreased and chemically treated with zinc phosphate) to a thickness of 35 µm, allowed to stand at room temperature for 10 minutes, and baked at 140°C for 25 minutes, obtaining a coating (1), which was examined by hardness and rubbing tests. Similarly, clear coating composition II was spray coated onto a similar soft steel strip, allowed to stand, and baked at 180°C for 25 minutes, obtaining a coating (2), which was similarly tested. For clear coating compositions III to VIII, the test procedure is as follows. A test piece was obtained by subjecting a similar soft steel strip to cationic electrodeposition, primer coating and sanding. Metallic coating solution I or II was coated to the test piece to a thickness of 20 µm and set at room temperature for 5 minutes. Directly thereafter in the case of metallic coating solution I and after preheating at 80°C for 5 minutes in the case of metallic coating solution II , each of clear coating compositions III to VIII was coated to the metallic coated test piece to a thickness of 35 µm. Each coating was set at room temperature for 5 minutes and baked at 140°C for 25 minutes, obtaining coatings (3) to (8), which was similarly tested. The results are shown in Table 2. As seen from Table 2, the clear coating compositions within the scope of the invention cured satisfactorily in all situations that they were coated directly to zinc phosphated steel strips (Examples 1 and 2), that they were coated to the metallic coating containing a catalyst poison, and that they themselves contained a catalyst poison. Full curing indicated that hydrosilylation reaction took place to completion. Component (D) permits components (A) and (B) to undergo hydrosilylation reaction with the aid of a hydrosilylation catalyst even in the presence of a catalyst poison. Although some preferred embodiments have been described, many modifications and variations may be made thereto in the light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described.

Claims: A hydrosilylative composition comprising (A) acrylic, polyester or epoxy resin having at least two alkenyl or alkynyl groups per molecule and a molecular weight in the range 500 to 100,000 (B) organic silicon compound having per molecule at least two hydrogen atoms directly attached to silicon atom, and blended in an amount such that the molar ratio of alkenyl/alkynyl groups in component (A) to silicon-attached hydrogen atoms in component (B) is in the range 1:0.5 to 1:50; (C) hydrosilylation catalyst in an amount of 0.1 to 10,000 parts by weight of catalyst metal per million parts by weight of component (B), and (D) organic iron compound and/or organic aluminium compound. A composition according to claim 1 in which component (D) is present at from 10 to 10000 times the weight of metal in the catalyst component (C). A composition according to claim 1 or claim 2 in which component (D) is selected from organic ferric salts, aluminium alkoxides and aluminium chelates. A composition according to claim 3 in which component (D) is selected from iron octylate, iron acetate, iron naphthenate, iron acetylacetonate, aluminium butoxide, aluminium isobutoxide, aluminium isopropoxide, acetylacetonato-aluminium and ethylacetoacetonato-aluminium. A composition according to any one of the preceding claims in which the molecular weight of resin component (A) is in the range 2000 to 50000. A composition according to any one of the preceding claims in which the molar ratio of alkenyl/alkynyl groups in resin compound (A) to silicon-attached hydrogen atoms in component (B) is in the range 1:1 to 1:10. A process comprising effecting hydrosilylation reaction between components (A) and (B) in a composition as defined in any one of claims 1 to 6. A process according to claim 7 in which the hydrosilylation is carried out by heating to a reaction temperature in the range 50 to 150°c. A process according to claim 7 or claim 8 in which the reaction system contains, or is in contact with, a material containing any of N, P, S, Sn and As. Use of the organic iron compound and/or organic aluminium compound (D) to inhibit poisoning of the catalyst (C), in a process as defined in claim 7 or 8.

Inventors: EGUCHI YOSHIO, OHSUGI HIROHARU, TAKARADA MITSUHIRO, YOSHIKAWA YUJI, EGUCHI, YOSHIO, OHSUGI, HIROHARU, TAKARADA, MITSUHIRO, YOSHIKAWA, YUJI
Applicants: NIPPON PAINT CO LTD, SHINETSU CHEMICAL CO, NIPPON PAINT CO., LTD., SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1993
Main classification: C08L101
IPC codes: C08L63, C08L83, C08K5, C08L67, C08L33, C08L101