CATALYST AND PROCESS FOR PURIFYING DIESEL EXHAUST GASES

Abstract: The invention relates to a catalyst intended for purifying diesel exhaust gases, the catalyst comprising a honeycomb and a support which has been prepared by using titanium dioxide and an inorganic sol, and at least one catalytically active agent.

Description: CATALYST AND PROCESS FOR PURIFYING DIESEL EXHAUST GASES The present invention relates to a catalyst according to the preamble of Claim 1 for purifying diesel gases. The invention also relates to a method for the manufacture of a catalyst and to a method for purifying diesel exhaust gases. The exhaust gases of diesel engines contain nitrogen oxides, carbon monoxide, and hydrocarbons„ In addition, diesel exhaust gas contains small amounts of S0 2 gas, which in the operating conditions of an exhaust gas catalyst tends to form, for ex¬ ample, sulphates, which, when depositing on a surface con¬ taining noble metals, will weaken the efficiency of the exhaust gas catalyst. Other compounds which are detrimental for the functioning of a catalyst are lead compounds and phosphorus compounds. Sulphur dioxide gas in itself does not hamper the functioning of a catalyst. However, in the exhaust gas catalysts in diesel engines, sulphur dioxide gas tends to oxidize, whereby sulphur trioxide is formed, and in a moist environment further sulphate. This, in turn, results in the accumulation of sulphur on the catalyst surface and a weakening of the catalytic action. The accumulation of sulphur on the surface of the cata¬ lyst is a serious problem in diesel exhaust gas catalysts. Patent publication US-5 000 929 discloses a catalyst in which diesel exhaust gases are purified by using the oxides of pal¬ ladium, praseodymium, neodymium and samarium, and as a support inorganic oxides. These inorganic oxides include active alumi¬ num oxide, silica, titanium dioxide, zirconium oxide, etc., mentioned in the patent. The operating conditions of the above- mentioned catalyst are a high temperature and an oxidizing atmosphere„ EPO publication 0 377 290 discloses a catalyst which is silica- based and removes impurities from diesel exhaust gases by oxi¬ dizing carbon monoxide and hydrocarbons into carbon dioxide and water. Both noble metals and promoters are added to the silica support layer. The promoters include gold chloride, silver nitrate, cerium chloride, etc. By means of the invention, the oxidation of S0 2 to S0 3 is decreased to a rather low level. Patent publication WO-90/00439 discloses a method for lowering the light-off temperature of diesel soot. On the surface of the soot filter there is produced a support layer in which,, for example, titanium dioxide is used- The surface of the titanium dioxide is impregnated with a noble metal, which may be Pt r Pd or Rh. The light-off temperature of the soot was lowered by means of such a filter. Patent publication EP-214 085 discloses a method for the pro¬ duction of a catalyst intended for the elimination of NO,; gases. According to the method, the support is prepared by sin¬ tering a mixture of orthotitanic acid and silicic acid. Thereby a Ti0 2 with very small crystals is formed. Instead of silicic acid, or in addition to it, a compound of tungsten or molyb¬ denum may be used in the method. By the use of a catalyst which contains no noble metals and which cannot be used for the puri¬ fication of diesel exhaust gases, N0 X gases can be removed while the oxidation of S0 2 remains insignificant. The state-of-the-art methods for the manufacture of catalysts have the deficiency that they do not enable production of a noble metal catalyst which would have simultaneously both an efficient conversion of CO and HC gases and a low binding of sulphur, i.e. oxidation of S0 2 . The object of the present inventio is to provide a catalyst in which the binding of the sulphur present in diesel exhaust gas to the catalyst is inhibited and which has an effective con- version of CO and HC gases. A further object is a catalytic unit in which the support adheres well to the metal foil. These objects are achieved by means of the catalyst according to the invention, which is mainly characterized in the facts stated in the characterizing clause of Claim 1. According to the invention there is also provided a method for the manufacture of such a catalyst, in which method the carrier forming a honeycomb, for example a metal foil, is coated with a slurry containing titanium dioxide and- an inorganic sol, where¬ after drying and calcination are carried out in order to form a support on the carrier, and thereafter the support is impregnated with at least one catalytically active agent. The invention is based on the surprising observation that, when the support used is a mixture made up of titanium dioxide and an inorganic sol, the light-off temperatures of both CO and HC are brought to a sufficiently low level while the oxidation of S0 2 is prevented, whereupon its accumulation on the surface of the support remains low. The honeycomb may be of metal or a ceramic material, and pref¬ erably it is made of metal foil. The titanium dioxide used may also be modified, i.e. stabil¬ ized, in which case it contains various stabilizers such as compounds of Al, Si, Zr, La, Ba, Y and/or Ce, or mixtures of these compounds. When titanium dioxide in anatase form is the support, the said substances may be added before the kiln treatment in the titanium dioxide production process, in which case they can pass into the crystal lattice of the anatase. This can further be calcined at a higher temperature to rutile. Rutile-form titanium dioxide stabilizes onto the crystal sur¬ face. For additives it is possible to use small amounts of, for example, A1 2 0 3 and/or Si0 2 , which settle on the surface of rutile. An inorganic sol is a suspension made up of finely-divided particles (0.01 - 0.1 μm) and a liquid. The liquid is usually water. The solid may be in the form of an oxide or hydroxide. According to the invention the sol may be, for example., silica sol ("colloidal silica"), aluminum sol, titanium sol, zirconium sol, or a mixture of these. During calcination, the inorganic sol is converted into an oxide and the size of the crystals increases. The purpose of using a sol is, on the one hand, for the sol to function as an "adhesive" between the crystals of the support by crystallizing adjacently located separate crys¬ tals to each other and, on the other hand, to improve the ad¬ hesion of the crystals in the support to the crystals on the surface of the metal foil, the latter crystals having been produced by a thermal treatment of the metal foil. The sol is used at 10 - 80 % by weight, preferably at 40 - 60 % by weight, calculated from the dry weight of the support. During the heating step, the volatile components are removed from the sol of the support layer, and in the end a dry oxide is obtained. By combining, in accordance with the invention, titanium dioxide and the above-mentioned sol, a support is obtained which adheres well to a metal foil and on which sulphur dioxide is not left to a noteworthy degree. The support thus obtained is impregnated by conventional methods with at least one catalytically active agent, in particular a noble metal such as palladium. As the promoter compound, which may be a salt or a solution, it is possible to use compounds which promote catalytic reactions or retard the ageing of the support and/or of the noble metals. Often promoter compounds in themselves are not sufficiently active catalytically, but together with a catalytically active component they improve the properties of the catalyst. Such compounds include the compounds of the lanthanide group and transition metal compounds. The support according to the invention remains well on the surface of a metal honeycomb, and it can be used even for a honeycomb with densely spaced openings. The binding of sulphur to the catalyst remains low in this case. The invention is described below in greater detail, with the help of examples. Example 1. To prepare a support slurry, 240 g of anatase (Ti0 2 ) and 112 g of si.lica sol (Ludox HS-40) , calculated as 40 % Si0 2 , were slurried in water. Both corrugated and flat metal foils were pre-treated and coated with this slurry. Support was used in an amount which was, calculated as dry weight, 40 g/m 2 of metal sheet. The support coating was dried at 105 °C and calcined for 4 h at 550 °C. The obtained coating was impregnated with pal¬ ladium by using a palladium tetra-amminedichloride solution so that the Pd concentration obtained for the catalyst was 0.30 % Pd as calculated from the weight of the catalyst. Finally cal¬ cination for 1 h at 400 °C was performed. For testing the catalyst, a synthetic diesel exhaust gas having the following composition was used. The spaee velocity in the catalyst was 50,000 h: 1 . In the test, the light-off temperatures of the catalyst for carbon monoxide and hydrocarbon were measured. By light-off temperature is meant the temperature at which 50 % of the gas is oxidized. In addition, the conversion percentages of the. gases at 400 °C were measured. The binding or accumulation of sulphur was measured by using a synthetic diesel exhaust gas (100 ppm S0 2 , 5 % 0 2 , space velocity 10 000 h "1 , 30 min) by measuring the S0 2 concentration continuously at 400 °C. The result of the test was Example 2. (reference example) A test otherwise similar to that in Example 1 was performed, but the support was prepared by using a mixture of aluminum oxide and aluminum sol. The result of the test was Example 3. To produce a support slurry, 82.6 g of La-stabilized anatase- form Ti0 2 , 46.7 g of silica sol (Ludox HS-40) and 39.0 g of crystalline La nitrate were slurried in water. The slurry was ground. Thereafter, the same procedures were carried out as in Example 1. According to the analysis, the catalyst obtained had a Pd concentration of 0.36 % and a La concentration of 2.5 %. The result of the experiment was The results show that, when the combination according to the invention is used as a support, i.e. titanium oxide and an inorganic sol together, a significant decrease in the binding of sulphur on the catalyst surface is achieved. The anatase used in Examples 1 and 3 was normal titanium di¬ oxide after the anatase kiln of the titanium dioxide process (sulphate process) .

Claims: Claims 1. A catalyst for the purification of diesel exhaust gases, the catalyst comprising a honeycomb and a support and at least one catalytically active agent, characterized in that the support is prepared by using titanium dioxide and an inorganic sol. 2. A catalyst according to Claim 1, characterized in that the titanium dioxide is stabilized by using a compound of Al, Si, Zr, La, Ba, Y or Ce. 3. A catalyst according to Claim 1, characterized in tnat the inorganic sol is a silicon sol aluminum sol, titanium sol,, - zirconium sol, or a mixture of these. 4. A catalyst according to Claim 1, characterized in that the support contains at least one component acting as a pro¬ moter, the component being preferably a compound of the lanthanide group or a soluble salt of a transition metal. 5. A catalyst according to Claim 1, characterized in that the honeycomb is made of metal. 6. A method for the manufacture of a catalyst according to Claim 1, characterized in that the carrier forming a honeycomb is coated with a slurry containing titanium dioxide and an inorganic sol, whereafter drying and calcination are carried out in order to form a support on the carrier, and thereafter the support is impregnated with at least one catalytically active agent. 7. A method for purifying diesel exhaust gases, charac¬ terized in that the diesel exhaust gases are directed through a catalyst according to Claim 1.

Inventors: HAERKOENEN MATTI, KIVIOJA MATTI, MAUNULA TEUVO, RAVOLA SOINTU, SLOTTE THOMAS, VIRTA PIRKKO, HAERKOENEN, MATTI, KIVIOJA, MATTI, MAUNULA, TEUVO, RAVOLA, SOINTU, SLOTTE, THOMAS, VIRTA, PIRKKO
Applicants: HAERKOENEN MATTI, KEMIRA OY, KIVIOJA MATTI, MAUNULA TEUVO, RAVOLA SOINTU, SLOTTE THOMAS, VIRTA PIRKKO
Application year: 1993
Main classification: B01J21
IPC codes: B01D53, B01J37, F02B3