A quantum effect device and a method of producing the same

Abstract: A quantum device including a plate-like conductor part having a necking portion and a method of producing the same are disclosed. The method includes the steps of forming a first mask layer having a first strip portion on a conductor substrate; forming a second mask layer having a second strip portion on the conductor substrate; etching a region of the conductor substrate which is not covered with the first and second mask layers, by using the first and second mask layers as an etching mask, to form a plurality of first recess portions on a surface of the conductor substrate; selectively covering side faces of the plurality of first recess portions, and side faces of the first and second mask layers with a side wall film; selectively removing only the second mask layer, the first mask layer and the side wall film being left unremoved; etching another region of the conductor substrate which is not covered with the first mask layer and the side wall film, by using the first mask layer and the side wall film as an etching mask, to form a plurality of second recess portions on the surface of the conductor substrate; selectively removing part of another region of the surface of the conductor substrate which is not covered with the first mask layer and the side wall film; and removing the first mask layer and the side wall film, to form the plate-like conductor part having the necking portion at the conductor substrate.

Description: The present invention relates to a method of producing a device for which a quantum effect is utilized as defined in claims 1 and 7. Owing to the recent progress of the semiconductor technique, high integration of devices and miniaturization of device size have been progressing. Due to the miniaturization, it is necessary to develop a new device which has a structure different from that of the conventional transistor. For such a new device, a device for which a quantum effect is utilized has been studied (see THE JOURNAL OF THE INSTITUTE OF ELECTRONICS, INFORMATION AND COMMUNICATION ENGINEERS, Vol. 72, No. 12, pp. 1387-1391, December 1989). In order to cause the quantum effect, developments of a technique for forming dots or strip wires each having a size of the order of an electron wavelength, and a technique for constituting a circuit by coupling the dots and the strip wires are required. For a quantum device whose operation is based on the quantum effect, various devices are now being developed. Especially, a device for controlling the electron transfer by utilizing the resonant tunneling effect has been developed. The quantum device for which the resonant tunneling effect is utilized includes a minute conductor region in which the energy states which can be taken by electrons are quantized, and a pair of conductor regions (electrodes) adjacent to the minute conductor region via a thin barrier film through which electrons can tunnel. Such a quantum device is disclosed, for example, in U.S. Patent No. 4,912,531 (Reed et al.). In order to realize the above quantum device, a technique for forming a microstructure with good reproducibility is required. A conventional quantum device is produced by laminating a plurality of different kinds of thin compound semiconductor films on a semiconductor substrate. As a result, in the quantum device, electrons move freely in a direction parallel to the main plane of the substrate, and electrons are confined in the quantized region in another direction perpendicular to the main plane of the substrate. The prior art document EP-A-0 464 834 discloses a quantum effect device comprising a substrate and a plate-like conductor part. The plate-like conductor part has two parallel side faces perpendicular to the main face of the substrate including a necking portion. In this necking portion a one-dimensional quantum effect occurs which leads to a quantized energy state in a direction perpendicular to the respective two side faces of this known quantum effect device. However, the quantum effect area is dimensioned in an exaggerated manner so that a quantum effect can only occur if an additional necking field is applied to the quantum effect area. The prior art document M.S. Reed et al.: Physical Review Letters, vol. 60, no. 6, 1988, pages 535-537, shows various GaAs nanostructures containing quantum dots. These quantum dots should provide zero-dimensional semiconductor nanostructures which in vertical direction include a quantum well. This quantum well and the accompanying layers to this quantum well layer are fabricated by means of a chemical vapor deposition technique. From the prior art document K. Tsubaki et al.: Electronics Letters, vol. 25, no. 11, 1989, pages 728-739, a quantum effect device with a plate-like semiconductor part is known. This semiconductor part has two parallel side faces perpendicular to the main surface. The side faces include a necking portion which has a width of less than 16 nm. According to this small width a quantum effect occurs. The prior art document K. Shimizu et al.: Japanese Journal of Applied Physics, vol. 30, no 3A, 1991, pages L415-L417, concerns the fabrication of MOS nanostructures by employing electron beam lithography and anisotropic wet etching of silicon. According to this document a nanostructure with a width of less than 20 nm is fabricated and the resulting structures are very subtle and straight. By means of this structure it is possible to generate a quantum effect. However, in the above prior art, it is difficult to form a region which has a very small thickness which is measured along a direction parallel to the main plane of the substrate. Therefore, it is an object of the present invention to provide such a method. This object is solved by a method including the features one of claim 1 or 7. Advantageous embodiments are defined by the features in the subclaims. The method of producing a quantum device including a plate-like conductor part having a necking portion of this invention, includes the steps of: (a) forming a first mask layer having a first strip portion on a semiconductor substrate; (b) forming a second mask layer having a second strip portion which crosses the first strip portion on the semiconductor substrate; (c) etching a region of the semiconductor substrate, by using said first and second mask layers as an etching mask to form a plurality of first recess portions on a surface of said semiconductor substrate, said region not being covered with said first and second mask layers, thereby at least partially a plate-like semiconductor part is formed; (d) selectively covering side faces of said plurality of first recess portions and side faces of said first and second mask layers with a side wall film; (e) selectively removing only said second mask layer, said first mask layer and said side wall film being left unremoved; (f) etching another region of said semiconductor substrate by using said first mask layer and said side wall film as an etching mask to form a plurality of second recess portions on said surface of said semiconductor substrate, said region not being covered with said first mask layer and said side wall film; (g) selectively reducing a width of a portion of said plate-like semiconductor part, said portion being not covered with said wall film, thereby forming said necking portion; and (h) removing said first mask layer and said side wall film to form said plate-like semiconductor part having said necking portion at said semiconductor substrate. In one variation, the step (g) includes: a step of selectively oxidizing another region of the surface of the conductor substrate, the region being not covered with the first mask layer and the side wall film, to form an oxide film; and a step of removing the oxide film. In one variation, the step (g) includes: a step of selectively nitriding another region of the surface of the conductor substrate, the region being not covered with the first mask layer and the side wall film, to form a nitride film; and a step of removing the nitride film. In one variation of the method according to the invention, the step (g) includes a step of selectively etching another region of the surface of the conductor substrate, the region being not covered with the first mask and the side wall film. In one variation, the method further includes the steps of: forming a pair of tunnel insulation films at least on side faces of the necking portion; and forming a pair of conductive members which sandwich the necking portion via the pair of tunnel insulation films. In one variation, the method further includes the steps of: forming a gate insulation film at least on an upper face of the necking portion; and forming a gate electrode on the gate insulation film. In another aspect of the invention, a method of producing a quantum device including a plate-like conductor part having a necking portion is provided. The method includes the steps of: (a) forming an insulation film on a semiconductor substrate; (b) forming a multilayer film having a conductive layer as a bottom layer on the insulation film; (c) patterning the multilayer film, to form a first mask layer having a first strip portion on the insulation film; (d) forming a first side wall film on side faces of the first strip portion; (e) forming a second mask layer having a second strip portion which crosses the first strip portion on the insulation film; (f) etching a region of the insulation film and the semiconductor substrate, by using said first and second mask layers and the first side wall film as an etching mask to form a plurality of first recess portions on a surface of said semiconductor substrate, said region not being covered with said first and second mask layers and said first side wall film; (g) selectively covering at least side faces of said plurality of first recess portions with a second side wall film; (h) selectively removing only said second mask layer, said first mask layer and said first and second side wall films being left unremoved; (i) etching another region of said semiconductor substrate by using said first mask layer and said first and second side wall films as an etching mask to form a plurality of second recess portions on said surface of said semiconductor substrate, said region not being covered with said first mask layer and said first and second side wall films, thereby forming at least partially said plate-like semiconductor part; (j) selectively reducing a width of a portion of said plate-like semiconductor part, said portion not being covered with said first and second side wall films, thereby forming said necking-portion; and (k) removing said first and second side wall films to form said plate-like semiconductor part having said necking portion at said semiconductor substrate. In one variation, the step (j) includes: a step of selectively oxidizing another region of the surface of the conductor substrate, the region being not covered with the first mask layer and the first and second side wall films, to form an oxide film; and a step of removing the oxide film. In one variation, the step (j) includes: a step of selectively nitriding another region of the surface of the conductor substrate, the region being not covered with the first mask layer and the first and second side wall films, to form a nitride film; and a step of removing the nitride film. In one variation, the step (j) includes a step of selectively etching another region of the surface of the semiconductor substrate, the region being not covered with the first mask and the first and second side wall films. The quantum device fabricated in accordance with the invention includes: a semiconductor substrate having a main face; and a plate-like conductor part having two side faces, the side faces being perpendicular to the main face of the conductor substrate, the side faces being parallel to each other, wherein the plate-like conductor part includes a necking portion having a width smaller than a distance between the two side faces, and energy states of electrons in the necking portion are quantized in a direction perpendicular to the two side faces. The quantum device can further include: a pair of tunnel insulation films formed at least on side faces of the necking portion; and a pair of conductive members which sandwich the necking portion via the pair of tunnel insulation films. The quantum device can further includes: a gate insulation film formed at least on an upper face of the necking portion; and a gate electrode formed on the gate insulation film. The gate electrode of the quantum device can be self-aligned with an upper face of the plate-like conductor part. Thus, the invention described herein makes possible the advantages of (1) providing a device for which a quantum effect is utilized, and (2) providing a method of producing a quantum device including steps capable of forming a necking portion having a very small thickness which is measured along a direction parallel to the main plane of a substrate. These and other advantages of the present invention will become apparent to those skilled in the art upon reading and understanding the following detailed description with reference to the accompanying figures. Figures 1A to 1C are perspective views illustrating a flow for producing a quantum device according to a first example of the invention. Figures 2A to 2F are perspective and cross-sectional views illustrating the flow for producing the quantum device according to the first example of the invention. Figures 3A to 3C are perspective views illustrating a flow for producing a quantum device according to a second example of the invention. Figures 4A to 4C are diagrams showing the operation principle of the quantum device according to the second example of the invention. Figure 4D is a graph schematically illustrating the relationship between the amount of current and the potential difference between a first and a second electrodes. Figures 5A to 5D are perspective views illustrating a flow for producing a quantum device according to a third example of the invention. Figures 6A to 6C are perspective views illustrating a flow for producing a quantum device according to a fourth example of the invention. Figures 7A to 7C are perspective views illustrating the flow for producing the quantum device according to the fourth example of the invention. Figures 8A to 8E are cross-sectional and perspective views illustrating the flow for producing the quantum device according to the fourth example of the invention. Hereinafter, a method of producing a quantum device according to a first example of the invention will be described with reference to the relevant figures. Figures 1A to 1C and Figures 2A to 2F show the method of producing a quantum device according to the first example of the invention. The production flow will be described below. In the step shown in Figure 1A , a nitride film (thickness: 100 nm) 2 like a strip wire (width: 500 nm) is formed on a silicon substrate 1 . An oxide film (thickness: 100 nm) 3 like a strip wire (width: 500 nm) is also formed on the silicon substrate 1 . The nitride film 2 and the oxide film 3 are formed substantially perpendicular to each other. In the step shown in Figure 1B , using the nitride film 2 and the oxide film 3 as a mask, the silicon substrate 1 is etched by a dry etching technique, so as to form a first recess portion (depth: 300 nm) 4 . For the etchant, SF 6 is used. In the step shown in Figure 1C , a nitride film (thickness: 100 nm) is first deposited over the entire surface. Then, the nitride film is etched back by anisotropic etching, so as to form a side wall structure 5 of the nitride film on the side walls of the nitride film 2 , the oxide film 3 , and the first recess portion 4 . Thereafter, the oxide film 3 is removed away by an etching method. In the step shown in Figure 2A , by using the nitride film 2 and the side wall structure 5 as a mask, the exposed portion of the silicon substrate 1 is etched by the dry etching technique, so as to form a second recess portion (depth: 250 nm) 6 . By this etching step, a silicon stripe S is formed. At the step of Figure 2A , the cross-sectional view taken along line B-B' is shown in Figure 2B , and the cross-sectional view taken along line C-C' is shown in Figure 2C . As is shown in Figure 2B , in the portion where the oxide film 3 has been formed at the step of Figure 1A , the nitride film 2 exists on the silicon stripe S , and nothing exists on the side walls of the silicon stripe S . As is shown in Figure 2C , in the portion where the oxide film 3 has not been formed at the step of Figure 1A , the nitride film 2 exists on the silicon stripe S , and the side wall structure 5 is positioned on the side walls of the silicon stripe S . Thereafter, a thermal oxidation process is performed, so as to form a thermal oxide film (thickness: 220 nm) 7 . The thermal oxidation process is performed in a pyrogenic atmosphere, at a temperature of 1000°C for about 50 minutes. After the thermal oxidation process, the resulting cross-sectional view taken along line B-B' is shown in Figure 2D , and the resulting cross-sectional view taken along line C-C' is shown in Figure 2E . Specifically, since the side wall structure 5 does not exist on the side walls of the silicon stripe S in the B-B' cross section, the oxide film formation progresses from the side wall portions of the silicon stripe S . As a result, an extremely thin width 8 of the silicon stripe S in the B-B' cross section is obtained, as is shown in Figure 2D . In the C-C' cross section, since the side wall structure 5 exists on the side walls of the silicon stripe S , the oxidation progresses from a portion of the silicon stripe S lower than the side wall structure 5 . As a result, a relatively thick width 9 in the C-C' cross section is obtained. Figure 2F shows the resulting silicon surface structure excluding the oxide films and the nitride films. As is shown in Figure 2F , a silicon strip wire 10 having a necking portion (the thickness thereof which is measured along a lateral direction: 60 nm) 11 is obtained. Even in a case where the strip sizes (widths) of the nitride film 2 and the oxide film 3 are those not capable of attaining the quantum effect, a small size capable of attaining the quantum effect can be realized in the necking portion 11 according to this example. In another case where the strip sizes of the nitride film 2 and the oxide film 3 are those capable of attaining the quantum effect, quantum strip wires having various widths can be produced according to this example. As described above, according to this example, a method for easily producing a quantum device having a lateral size capable of attaining the quantum effect can be obtained. In this example, the thermal oxidation is performed so as to form the thermal oxide film 7 for obtaining the extremely thin width 8 in the B-B' cross section. Alternatively, silicon may be etched by wet etching by using a mixture of hydrofluoric acid and nitrate as the etchant so as to reduce the width 8 in the B-B' cross section. In this example, thermal oxidation is performed for forming the thermal oxide film 7 so as to obtain the width 8 in the B-B' cross section. Alternatively, the width 8 may be reduced by the combination of the wet etching and the thermal oxidation. Hereinafter, a method of producing a quantum device according to a second example of the invention will be described with reference to the relevant figures. Figures 3A to 3C illustrate the method of producing a quantum device according to the second example of the invention. Figures 4A to 4D illustrate the principle of the operation of the quantum device in the second example of the invention. The production flow is described below. In the step shown in Figure 3A , a plate-like silicon 60 including a necking portion (thickness: 60 nm) 61 is formed on a silicon substrate 1 by the method described in the above first example. In the step shown in Figure 3B , a thermal oxidation is performed, so as to form a thin thermal oxide film (thickness: 2 nm) 62 around the plate-like silicon 60 and the necking portion 61 , and on the silicon substrate 1 . In the step shown in Figure 3C , a single crystal silicon 63 is formed and then a planarization is performed. The left portion of the single crystal silicon 63 functions as a first electrode 63a . The right portion of the single crystal silicon 63 functions as a second electrode 63b . As seen from Figure 3C , a structure including, along the x direction, the single crystal silicon 63 , the 2-nm tunnel oxide film 62 , the necking portion (substrate 1) 61 , the 2-nm tunnel oxide film 62 , and the single crystal silicon 63 is formed. The energy states of electrons in the necking portion 61 are quantized in the thickness direction x, so that it has a two-dimensional structure. A thickness of 2 nm of the oxide film 62 is sufficient for electrons to tunnel through the oxide film 62 . Figures 4A to 4C are potential diagrams in the cross section along the x direction in the region including the necking portion in Figure 3C . The operation of the quantum device as shown in Figure 3C is described with reference to Figures 4A to 4D . Figure 4A shows a state where the potential difference between the first electrode 63a and the second electrode 63b is 0. Figure 4B shows a state where a first potential difference 108 is applied between the first electrode 63a and the second electrode 63b . Figure 4C shows a state where a second potential difference 109 is applied between the first electrode 63a and the second electrode 63b . In Figure 4A , the first electrode 63a and the second electrode 63b are conductive regions of the single crystal silicon 63 in Figure 3C , and each have a three-dimensional structure, and have a continuous band structure. The Fermi level in the first electrode 63a is defined as a Fermi level 107 in the first electrode 63a . In the necking portion (resonant layer) 61 , the width thereof in the x direction is sufficiently small, so that it is regarded as having a two-dimensional structure on the basis of the quantum theory. The band structure in the necking portions 61 is different from that of the first and second electrodes 63a and 63b . For simplicity, it is presumed herein that values of the Fermi level 107 at which a probability that carriers (electrons) transmit from the first electrode 63a to the second electrode 63b due to the resonant tunneling effect is 1 are represented by quantized levels 106 in the necking portion 61 . In the state shown in Figure 4A , since the Fermi level in the first electrode 63a is not equal to the quantized levels 106 in the necking portion 61 , the resonant tunneling effect does not take place. Thus, the tunneling of the carriers from the first electrode 63a to the second electrode 63b does not occur. Next, in the state of Figure 4B where the first potential difference 108 between the first and the second electrodes 63a and 63b is applied so that the Fermi level 107 in the first electrode 63a is equal to either one of the quantized levels 106 in the necking portion 61 , the tunneling of carriers from the first electrode 63a to the second electrode 63b due to the resonant tunneling effect occurs, thereby causing a current to flow. In the state shown in Figure 4C , the potential difference between the first and the second electrodes 63a and 63b is increased, but has not reached the potential difference between the first and the second electrodes 63a and 63b at which the Fermi level 107 in the first electrode 63a is equal to the other one of the quantized levels 106 in the necking portion 61 . Specifically, when the second potential difference 109 between the first and the second electrodes 63a and 63b is applied as is shown in Figure 4C , the current does not flow. Figure 4D schematically shows the amount of current while the potential difference between the first and the second electrodes 63a and 63b is continuously increased from zero. In Figure 4D , the negative resistance is exhibited. By utilizing the negative resistance, a device having a new function in addition to the conventional ON/OFF function of a MOSFET can be produced. In this example, only the necking portion 61 is sufficiently thin for the quantization in the thickness direction, and the other portions of the plate-like silicon 60 are formed to be sufficiently thick not for the quantization. As a result, as is shown in Figure 3C , even when the single crystal silicon 63 is formed entirely around the plate-like silicon 60 , the region where the resonant tunneling takes place can be limited to the necking portion 61 . Therefore, during the formation of the single crystal silicon 63 , the restrictions for production are reduced. In addition, when a quantum well is produced into a zero dimension in the resonant tunneling effect, the quantum well can be produced only by giving attention to the width in the y direction and the depth in the z direction of the necking portion 61 . As described above, according to this example, a method of producing a quantum device by which a quantum device having a size sufficient for attaining the resonant tunneling effect can readily be produced. Next, a method of producing a quantum device according to a third example of the invention will be described with reference to the relevant figures. Figures 5A to 5D illustrate the method for producing a quantum device in the third example of the invention. The production flow will be described below. In the step shown in Figure 5A , a silicon strip wire 30 having a necking portion (thickness: 60 nm) 31 is formed on a silicon substrate 1 by the method described in the first example of the invention. In the step shown in Figure 5B , an insulator is formed, and patterned to expose the surface of the silicon strip wire 30 . Thus, an insulating film (thickness: 500 nm) 32 is obtained. In the step shown in Figure 5C , a thermal oxidation is performed to form an oxide film (thickness: 10 nm) 33 . In the step shown in Figure 5D , polycrystalline silicon is deposited, and patterned into an electrode shape. Thus, a control electrode 34 is formed. In this example, by controlling the potentials of the control electrode 34 and the silicon substrate 1 which are connected via the silicon strip wire 30 and the oxide film 33 , a depletion region, a reversed region, or a storage region can be formed in the silicon strip wire 30 . Therefore, electrodes are formed at both ends of the strip wire, and a potential is applied, so that a current can be caused to flow. The amount of current can be controlled by changing the electrical potential of the control electrode 34 . As described above, according to this example, a method by which a quantum device can readily be produced can be obtained. Next, a method of producing a quantum device according to a fourth example of the invention will be described with reference to the relevant figures. Figures 6A to 6C , 7A to 7C , and 8A to 8E illustrate the method of producing a quantum device according to the fourth example of the invention. The production flow will be described. In the step shown in Figure 6A , after a gate oxide film (thickness: 10 nm) 12 is formed on a silicon substrate 1 , polycrystalline silicon (thickness: 250 nm) 13 and a nitride film (thickness: 100 nm) 14 are formed and patterned into predetermined shapes. The patterned polycrystalline silicon 13 will serve as a gate electrode. In the step shown in Figure 6B , a nitride film is first deposited over the silicon substrate 1 , and then etched back by anisotropic etching, so as to form a first side wall structure 15 of the nitride film at the side walls of the polycrystalline silicon 13 and the nitride film 14 . In the step shown in Figure 6C , an oxide film is first deposited over the silicon substrate 1 and then patterned by anisotropic etching, so as to form an oxide stripe (thickness: 100 nm) 16 . In the step shown in Figure 7A , the silicon substrate 1 is etched by using the nitride film 14 , the oxide stripe 16 , and the first side wall structure 15 as a mask, so as to form first recess portions 17 . In the step shown in Figure 7B , a nitride film is first deposited and then etched back by anisotropic etching, so as to form a second side wall structure 18 of the nitride film at the side walls of the nitride film 14 , the oxide stripe 16 , the first side wall structure 15 , and the first recess portion 17 . In the step shown in Figure 7C , the oxide stripe 16 is removed, and silicon etching is performed by using the nitride film 14 , the first side wall structure 15 and the second side wall structure 18 as a mask, so as to form second recess portions 19 . Figure 8A shows a cross-sectional view taken along line A-A' in Figure 7C . Figure 8B shows a cross-sectional view taken along line B-B' in Figure 7C . Specifically, in the A-A' cross section, the silicon side wall portions are exposed. In the B-B' cross section, the silicon side wall portions are covered with the second side wall structure 18 . In steps shown in Figures 8C and 8D , a thermal oxidation is performed, so as to form a thermal oxide film (thickness: 220 nm) 20 . Figure 8C shows the A-A' cross section after the thermal oxidation. In the A-A' cross section, the oxidation progresses from the silicon side wall portions, whereby a necking portion 23 having a width 21 is obtained. Figure 8D shows the B-B' cross section after the thermal oxidation. In the B-B' cross section, a silicon strip wire 24 having a width 22 which is larger than the width 21 is obtained. Figure 8E shows the perspective view of the structure after the formation of the thermal oxide film 20 in the steps of Figures 8C and 8D . Note that in Figure 8E , for simplicity, the structure is shown without the nitride films and the thermal oxide film 20 . In this example, the gate electrode (polycrystalline silicon 13 ) is formed in a self-alignment with the necking portion 23 and the silicon strip wire 24 . This means that it is unnecessary to performing any additional step for forming an electrode after the formation steps of the necking portion and the silicon strip wire. Thus, this example is superior to the first example. As described above, according to this example, a method by which a quantum device having a size capable of attaining the quantum effect can easily be produced is obtained. Various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the scope and spirit of this invention. Accordingly, it is not intended that the scope of the claims appended hereto be limited to the description as set forth herein, but rather that the claims be broadly construed.

Claims: A method of producing a quantum effect device including a plate-like semiconductor part (10,30,60) having a necking portion (11,31,61) comprising the steps of: (a) forming a first mask layer (2) having a first strip portion on a semiconductor substrate (1); (b) forming a second mask layer (3) having a second strip portion which crosses said first strip portion on said semiconductor substrate (1); (c) etching a region (4) of said semiconductor substrate (1) by using said first and second mask layers (2,3).as an etching mask to form a plurality of first recess portions (4) on a surface of said semiconductor substrate (1), said region (4) not being covered with said first and second mask layers (2,3), thereby at least partially a plate-like semiconductor part (10,30,60) is formed; (d) selectively covering side faces of said plurality of first recess portions (4) and side faces of said first and second mask layers (2,3) with a side wall film (5); (e) selectively removing only said second mask layer (3), said first mask layer (2) and said side wall film (5) being left unremoved; (f) etching another region (6) of said semiconductor substrate (1) by using said first mask layer (2) and said side wall film (5) as an etching mask to form a plurality of second recess portions (6) on said surface of said semiconductor substrate (1), said region (6) not being covered with said first mask layer (2) and said side wall film (5); (g) selectively reducing a width of a portion (11,31,61) of said plate-like semiconductor part (10,30,60), said portion (11,31,61) being not covered with said side wall film (5), thereby forming said necking portion (11,31,61); and (h) removing said first mask layer (2) and said side wall film (5) to form said plate-like semiconductor part (10,30,60) having said necking portion (11,31,61) at said semiconductor substrate (1). A method according to claim 1, wherein said step (g) includes: a step of selectively oxidizing the portion (11,31,61) of said plate-like semiconductor part (10,30,60) to form an oxide film (7), said portion (11,31,61) being not covered with said side wall film (5); and a step of removing said oxide film (7). A method according to claim 1, wherein said step (g) includes: a step of selectively nitriding the portion (11,31,61) of said plate-like semiconductor part (10,30,60) to form a nitride film (7), said portion (11,31,61) being not covered with said side wall film (5); and a step of removing said nitride film (7). A method according to claim 1, wherein said step (g) includes a step of selectively etching the portion (11,31,61) of said plate-like semiconductor part (10,30,60), said portion (11,31,61) being not covered with said side wall film (5). A method according to claim 1, further comprising the steps of: forming a pair of tunnel insulation films (62) at least on side faces of said necking portion (11,31,61), a thickness of said pair of tunnel insulation films (62) being sufficiently thin for electrons to pass therethrough by the tunneling effect; and forming a pair of conductive members (63a,63b) which sandwich said necking portion (11,31,61) via said pair of tunnel insulation films (62). A method according to claim 1, further comprising the steps of: forming a gate insulation film (33) at least on an upper face of said necking portion (11,31,61); and forming a gate electrode (34) on said gate insulation film (33). A method of producing a quantum effect device including a plate-like semiconductor part (24) having a necking portion (23) comprising the steps of: (a) forming an insulation film (12) on a semiconductor substrate (1); (b) forming a multilayer film (13,14) having a conductive layer (13) as a bottom layer on said insulation film (12); (c) patterning said multilayer film (13,14) to form a first mask layer having a first strip portion on said insulation film (12); (d) forming a first side wall film (15) on side faces of said first strip portion; (e) forming a second mask layer (16) having a second strip portion which crosses said first strip portion on said insulation film (12); (f) etching a region (17) of said insulation film (12) and said semiconductor substrate (1) by using said first and second mask layers (14,16) and the first side wall film (15) as an etching mask to form a plurality of first recess portions (17) on a surface of said semiconductor substrate (1), said region (17) not being covered with said first and second mask layers (14,16) and said first side wall film (15); (g) selectively covering at least side faces of said plurality of first recess portions (17) with a second side wall film (18); (h) selectively removing only said second mask layer (16), said first mask layer (14) and said first and second side wall films (15,18) being left unremoved; (i) etching another region (19) of said semiconductor substrate (1) by using said first mask layer (14) and said first and second side wall films (15,18) as an etching mask to form a plurality of second recess portions (19) on said surface of said semiconductor substrate (1), said region (19) not being covered with said first mask layer (14) and said first and second side wall films (15,18), thereby forming at least partially said plate-like semiconductor part (24); (j) selectively reducing a width of a portion (23) of said plate-like semiconductor part (24), said portion (23) not being covered with said first and second side wall films (15,18), thereby forming said necking-portion (23); and (k) removing said first and second side wall films (15,18) to form said plate-like semiconductor part (24) having said necking portion (23) at said semiconductor substrate (1). A method according to claim 7, wherein said step (j) includes: a step of selectively oxidizing the portion (23) of said plate-like semiconductor part (24) to form an oxide film (20), said portion (23) being not covered with said first and second side wall films (15,18); and a step of removing said oxide film (20). A method according to claim 7, wherein said step (j) includes: a step of selectively nitriding the portion (23) of said plate-like semiconductor part (24) to form a nitride film (20), said portion (23) being not covered with said first and second side wall films (15,18); and a step of removing said nitride film (20). A method according to claim 7, wherein said step (j) includes a step of selectively etching the portion (23) of said plate-like semiconductor part (24), said portion (23) being not covered with said first and second side wall films (15,18).

Inventors: HIRAI YOSHIHIKO, MORIMOTO KIYOSHI, NIWA MASAAKI, OKADA KENJI, UDAGAWA MASAHARU, YASUI JURO, YUKI KOICHIRO, HIRAI, YOSHIHIKO, MORIMOTO, KIYOSHI, NIWA, MASAAKI, OKADA, KENJI, UDAGAWA, MASAHARU, YASUI, JURO, YUKI, KOICHIRO
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1993
Main classification: H01L21
IPC codes: H01L29, H01L21