Compositions of ionically curable elastomeric polymers

Abstract: Ionically curing of VDF-containing fluoroelastomers selected from the ones containing less than 60 moles % of VDF and from the ones containing hydrogenated olefins is improved by using, as accelerators, triazinic compounds of formula: (R = H, C₁-C₄ alkyl; R' = R or benzyl, arylalkyl; X = Cl, Br, I, a bisphenoxy radical or O-CH₂Rf-CH₂R₂; Rf = a perfluorooxyalkylene chain; R₂ = -OH, -O⁻). What is claimed are the fluoroelastomeric compositions containing said accelerators.

Description: The present invention relates to compositions of ionically curable fluoroelastomeric polymers, comprising particular curing accelerators. As is known, fluoroelastomeric polymers are ionically curable by means of a combination of a cross-linking agent, which is a polyhydroxylic compound such as Bisphenol AF, and of a curing accelerator. As curing accelerators there are used, or are suggested in the art, aminophosphonium compounds (US Patent 4,259,463), phosphoranes (US Patent 3,752,787), and the organoonium compounds in general, as are described in US patents 3,655,727, 3,712,877, 3,857,807, 3,686,143, 3,933,732, 3,876,654, 4,233,421 and in European patent applications 182,299, 120,462 and 335,705. Curing of fluoroelastomeric copolymers such as for example the ones composed of vinylidene fluoride (VDF), hexafluoropropene (HFP) and tetrafluoroethylene (TFE), having a low VDF content, is, however, difficult when the abovesaid accelerators are utilized. The same difficulty in the curing with such accelerators is exhibited by the fluoroelastomeric copolymers containing hydrogenated olefins, as are described for example in EP-A-335,705, owing to the particular stability of their polymeric chain to the nucleophilic compounds. However, such fluoroelastomers can be easily cured with peroxides, after suitable peroxide curing sites have been introduced into the macromolecule. It has now been found by the Applicant that fluoroelastomeric copolymers containing monomeric VDF units, selected from the ones containing less than 60 moles % of VDF and free from units deriving from hydrogenated olefins, and from the ones which, irrespectively of the VDF unit amount, contain monomeric units deriving from hydrogenated olefins, can be easily ionically vulcanized by means of conventional hydroxylated cross-linking agents, utilizing, as an accelerator, a triazabicyclo compound having general formula (R = H, C₁-C₄) alkyl) or (R = H, C₁-C₄ alkyl) (R' = H, C₁-C₄ alkyl, benzyl, C₇-C₁₁ arylalkyl); X = Cl, Br, I, or a bisphenoxy radical or a radical of formula O-CH₂-Rf-CH₂-R₂, where: Rf = a perfluoropolyoxyalkylene chain having an average molecular weight ranging from 350 to 2,000, and comprising perfluorooxyalkylene units of formula (-CF₂CF₂O)- and/or R₂ = -OH, O⁻ or X can be a counterion of formula BF 4 - , PF 6 - , ½ ZnCl 4 -- , ½ CdCl 4 -- . Thus, object aof the present invention are the compositions based on fluoroelastomeric copolymers containing VDF units, selected from: a) the copolymers containing less than 60 moles % of VDF, free from monomeric units deriving from hydrogenated olefins, and b) the copolymers containing monomeric units deriving from hydrogenated olefins, which are ionically curable and contain, as curing accelerators, at least a compound comprised in general formulas (I) and/or (II) defined hereinbefore. Such compound can be present in the abovesaid compositions in amounts ranging from 0.2 to 1, but preferably from 0.35 to 0.60 parts by weight on 100 parts by weight of copolymer. The fluoroelastomeric copolyumers having a VDF content lower than 60 moles %, which are therefore curable, are composed of monomeric units deriving from VDF, with at least another monomer such as HFP, hydropentafluoropropene (HFPE), TFE, chlorotrifluoroethylene (CTFE), perfluoroalkylvinylether (PAVE). Esamples of such elastomers are the VDF/HFP/TFE copolymers, such as, for example, a few products marketed under the trade-names Dai-el (Daikin), Fluorel (3M), Tecnoflon (Montedison), Viton (du Pont), the copolymers described in EP-A-525,685, EP-A-525,687 and EP-A-570,762 in the name of the Applicant, containing VDF amounts lower than 60 moles %. The fluoroelastomeric copolymers containing monomeric units deriving from hydrogenated olefins, curable with the abovesaid accelerators, comprise the copolymers having the following molar composition: VDF 4-75% HFP and/or PAVE and/or HFPE and/or CTFE 0-40% 0l(olefin containing 1-4 C) 2-35% TFE 0-60% Advantageously cured are, in particular, the copolymers containing not more than 40 moles % of VDF and hydrogenated olefin in amounts from 5 to 25 moles %, described for example in EP-A-518,073 in the name of the Applicant, or the copolymers containing units of VDF, TFE and propylene cited in EP-A-335,705, containing 30-36 moles % of VDF, 41-45 moles % of TFE and 19-28 moles % of C₃H₆. The following examples are given to illustrate the present invention, but not to limit the scope thereof. EXAMPLES 1-2 These esamples refer to the cure of copolymers, the composition of which is reported in Table 1. In said Table, the characteristics of the curing formulation as well as the ones of the cured products according to the art (a) and according to the invention (b) are indicated too. NOTE: GM 102E is the phosphoranamine of formula TBD = compound of formula phr = per hundred rubber EXAMPLES 3-4 For these examples, a copolymer having the following composition in moles per cent VDF 31.5 HFP 7.5 TFE 26.0 MVE 15.0 E (Ethylene) 20.0 and having a fluorine content equal to 65.3% by weight and a Mooney viscosity ML (1 + 10) at 121°C = 40 was used. The characteristics of the curing compositions and of the cured products according to the prior art (tests (a)) and according to the invention (tests (b)) are reported in Table 2. EXAMPLE 5 For this example, a copolymer having the following molar per cent composition: VDF 22 TFE 46 P (propylene) 32 was used. The characteristics of the curing composition and of the cured products according to the prior art (a) and according to the invention (b) are reported in table 3. EXAMPLES 6-9 These examples refer to the curing of the copolymer utilized in examples 3 and 4 by using, as accelerators, triazinic compounds according to the invention. The characteristics of the curing compositions and of the cured products are reported in Table 4. TBD: formula (I), R = H Modified TBD: formula (II); R = H; R' = benzyl; X⁻=Cl⁻ TBD hydrochloride: formula (II); R = H; R' = H; X⁻ = Cl⁻ TBD/bisphenol AF adduct: formula (II) ; R = H; R' = H; X⁻= bis phenoxy EXAMPLES 11-13 (comparison with conventional guanidines as accelerators) For these examples, the copolymer of examples 3-4 was used. The characteristics of the curing compositions and the results of the curing are reported in Table 5. EXAMPLES 14-17 (comparison with conventional accelerators) For these examples, the copolymer of examples 3-4 was used. The curing formulations and their rheological properties are reported in Table 6.

Claims: Compositions based on fluoroelastomeric copolymers containing vinylidene fluoride (VDF) monomeric units, selected from: a) the copolymers containaing less than 60 moles per cent of vinylidene fluoride (VDF) and free from monomeric units deriving from hydrogenated olefins, and b) the copolymers containing monomeric units deriving from hydrogenated olefins, comprising 4-75 moles % of vinylidene fluoride (VDF); 2-35 moles % of olefin containing 1 to 4 carbon atoms; 0-60 moles% of tetrafluoroethylene (TFE); 0-40 moles% of at least a monomer selected from hexafluoropropene (HFP), hydropentafluoropropene (HFPE), chlorotrifluoroethylene (CTFE), perfluoroalkylvinylether (PAVE); and comprising an organic polyhydroxylic compound as cross-linking agent, which are ionically curable and contain, as curing accelerators, at least a compound comprised in one of the following general formulas: where R = H or an alkyl containing 1 to 4 carbon atoms, where R = H, or an alkyl containing 1 to 4 carbon atoms, R' = H, or an alkyl containing 1 to 4 carbon atoms, a benzyl, an arylalkyl containing 7 to 11 carbon atoms, X = Cl, Br, I or a bisphenoxy radical of formula or -O-CH₂-Rf-CH₂-R₂ wherein: Rf = a perfluoropolyoxyalkylene chain having an average molecular weight ranging from 350 to 2,000, and comprising perfluorooxyalkylene units of formula and/or R₂ = -OH, -O⁻, or X can be a counterion of formula BF 4 - , PF 6 - , ½ ZnCl 4 -- , ½ CdCl 4 -- . The compositions of claim 1, wherein the fluoroelastomeric copolymer is of type (a) and is composed of monomeric units deriving from vinylidene fluoride (VDF) with at least another monomer selected from hexafluoropropene (HFP), hydropentafluoropropene (HFPE), tetrafluoroethylene (TFE), chlorotrifluoroethylene (CTFE), perfluoroalkylvinylether (PAVE). The compositions of claim 1, wherein the fluoroelastomeric copolymer comprises not more than 40 moles % of vinylidene fluoride (VDF) and from 5 to 25 moles % of hydrogenated olefin. The compositions of claim 1, wherein the fluoroelastomeric copolymer comprises 30-36 moles % of vinylidene fluoride (VDF), 41-45 moles % of tetrafluoroethylene (TFE) and 19-28% moles % of propylene. The compositions of claims 1 to 4, wherein the accelerating compound of formula (I) or (II) is contained in amounts ranging from 0.2 to 1% by weight on 100 parts by weight of fluoroelastomeric copolymer.

Inventors: CHIODINI GRAZIELLA, MINUTILLO ANNA, CHIODINI, GRAZIELLA, MINUTILLO, ANNA
Applicants: AUSIMONT SPA, AUSIMONT S.P.A.
Application year: 1993
Main classification: C08L27
IPC codes: C08K5, C08L27