Polylactide compounds as sensitivity enhancers for radiation sensitive mixtures

Abstract: A radiation-sensitive composition comprises an admixture in a solvent of: at least one alkali-soluble binder resin, at least one photoactive compound and an effective sensitivity enhancing amount of at least one polylactide compound; the amount of said binder resin being about 60 to 95% by weight, the amount of said photoactive component being about 5% to about 40% by weight, based on the total solids content of said radiation-sensitive compostion.

Description: The present invention relates to radiation sensitive mixtures (e.g., those particularly useful as positive-working resist compositions) containing the admixture of an alkali-soluble binder resin, a photoactive compound and an effective sensitivity enhancing amount of at least one polylactide compound all dissolved in a solvent. Furthermore, the present invention also relates to substrates coated with these radiation sensitive mixtures as well as the process of coating, imaging and developing these radiation sensitive mixtures on these substrates. Photoresist compositions are used in microlithographic processes for making miniaturized electronic components such as in the fabrication of integrated circuits and printed wiring board circuitry. In these processes, a thin coating or film of a photoresist composition is generally first applied to a substrate material, such as silicon wafers used for making integrated circuits or aluminum or copper plates of printed wiring boards. The preferred method of applying this film is spin coating. By this method, much of the solvent in the photoresist formulation is removed by the spinning operation. The coated substrate is then baked to evaporate any remaining solvent in the photoresist composition and to fir the coating onto the substrate. The baked coated surface of the substrate is next subjected to an image-wise exposure of radiation. This radiation exposure causes a chemical transformation in the exposed areas of the coated surface. Visible light, ultraviolet (UV) light, electron beam, ion beam, and X-ray radiant energy are radiation types commonly used today in microlithographic processes. After this image-wise exposure, the coated substrate is treated with a developer solution to dissolve and remove either the radiation-exposed or the unexposed areas of the coated surface of the substrate. In some processes, it is desirable to bake the imaged resist coating before this developing step. This intermediate step is sometimes called post-exposure bake or PEB. There are two types of photoresist compositions--negative-working and positive-working. When negative-working photoresist compositions are exposed image-wise to radiation, the areas of the resist composition exposed to the radiation become less soluble to a developer solution (e.g., a cross-linking reaction occurs) while the unexposed areas of the photoresist coating remain relatively soluble to a developing solution. Thus, treatment of an exposed negative-working resist with a developer solution causes removal of the nonexposed areas of the resist coating and the creation of a negative image in the photoresist coating, and thereby uncovering a desired portion of the underlying substrate surface on which the photoresist composition was deposited but not exposed to the radiation. On the other hand, when positive-working photoresist compositions are exposed image-wise to radiation, those areas of the resist composition exposed to the radiation become more soluble to the developer solution (e.g., the Wolff rearrangement reaction of the photoactive compound occurs) while those areas not exposed remain relatively insoluble to the developer solution. Thus, treatment of an exposed positive-working resist with the developer solution causes removal of the exposed areas of the resist coating and the creation of a positive image in the photoresist coating. The desired portion of the underlying substrate surface is uncovered where the photoresist was exposed to the radiation. Positive-working photoresist compositions are currently favored over negative-working resists because the former generally have better resolution capabilities and pattern transfer characteristics. After this development operation, the now partially unprotected substrate may be treated with a substrate-etchant solution or plasma gases and the like. This etchant solution or plasma gases etch the portion of the substrate where the photoresist coating was removed during development. The areas of the substrate are protected where the photoresist coating still remains and, thus, an etched pattern is created in the substrate material which corresponds to the photo-mask used for the image-wise exposure of the radiation. Later, the remaining areas of the photoresist coating may be removed during a stripping operation, leaving a clean etched substrate surface. In some instances, it is desirable to heat treat the remaining resist layer after the development step and before the etching step to increase its adhesion to the underlying substrate and its resistance to etching solutions. End users of photoresists are demanding photoresist formulations possess better lithographic properties for the fabrication of smaller microelectronic circuits. The lithographic properties which are critical to positive-working photoresist end-users include the following: (1) good resolution capabilities in both the micron and submicron ranges without incomplete development in the exposed areas (i.e. scumming); (2) higher thermal image deformation temperatures (e.g., above 120°C); (3) relatively fast photospeeds; (4) good adhesion to substrate; (5) good developer dissolution rates; (6) good process latitude; (7) near to absolute vertical profiles (or good contrast) between exposed and unexposed photoresist areas after development; (8) good resistance to etching solutions and plasma etching techniques; (9) reduced tendency to form insoluble particulates; and (10) mask linearity. Generally in the past, efforts to improve one of these lithographic properties have caused significant decreases in one or more of the other lithographic properties of the photoresist. Accordingly, there is a need for improved photoresist formulations which possess all of these desired properties without making significant tradeoffs. The present invention is believed to be an answer to that need. For example, it is well known to add sensitivity enhancers (also known as photospeed enhancers or speed enhancers) to resist formulation to increase the solubility of the resist coating in both the exposed and unexposed areas when the speed of development is an overriding processing consideration. However, some degree of contrast may be sacrificed with the addition of such sensitivity enhancers, (e.g. in positive-working resists, while the exposed areas of the resist coating will be more quickly developed, the sensitivity enhancers will also cause a larger loss of the resist coating from the unexposed areas). Thus, if too much resist coating is removed from the unexposed areas of positive-working resins, film defects such as pinholes may be introduced into the coating or subsequent plasma etching steps may cause unwanted breakthroughs in the unexposed areas. Accordingly, sensitivity enhancers should provide the desired increased speed of development without too much more film loss in the unexposed areas. Numerous compounds have been proposed as sensitivity enhancers in resist compounds. See U.S. Patent Nos. 3,661,582; 4,009,033; 4,036,644; 4,115,128; 4,275,139; 4,365,019; 4,650,745; and 4,738,915 for examples of known sensitivity enhancers. While their known sensitivity enhancers may be suitable for some resist formulation or for some particular end uses, there is a need for new sensitivity enhancers which have better sensitivity enhancement without significant film loss in other resist formulations or in other end uses, or are suitable in a certain combination of resist formulations or a combination of end uses to which the previously known sensitivity enhancers are not suitable. The present invention is believed to be an answer to this need. Separately, ethyl lactate [CH 3 CH(OH)COO 2 C 2 H 5 ] is a known solvent for positive-working photoresists. In the presence of acidic substances, it forms polylactides [defined as wherein n is from 2 to 10] by the following reaction sequence: It has been found that if positive-working resists are treated with cation exchange resin, a portion of the ethyl lactate solvent in the photoresist formulation may be converted into a polylactide. It has been found that polylactides act as speed enhancers or sensitivity enhancers in positive-working photoresist compositions. Accordingly, the present invention is directed to a radiation sensitive composition useful as a positive-working resist comprising an admixture in a solvent of: (a) at least one photoactive compound; (b) at least one alkali-soluble binder resin; and (c) an effective sensitivity enhancing amount of at least one polylactide compound; the amount of said photoactive compound or compounds being about 5% to about 40% by weight and the amount of said binder resin or resins being about 60 to 95% by weight, based on the total solids content of said radiation sensitive mixture. Furthermore, the present invention also encompasses the process of coating substrates with these radiation sensitive mixtures and their exposing and developing these coated substrates. Also further, the present invention encompasses said coated substrates (both before and after imaging) as novel articles of manufacture. As mentioned above, the radiation-sensitive compositions of the present invention have three critical ingredients; at least one alkali-soluble binder resin; at least one photoactive compound; and at least one polylactide compound. Any or all binder resins commonly employed in photoresist compositions may be used herein. The preferred class of binder resins is alkali-soluble resin or resins which are useful in positive-working photoresist compositions. The term "alkali-soluble binder resin" is used herein to mean a resin which will dissolve completely in an aqueous alkaline developing solution conventionally used with positive-working photoresist compositions. Suitable alkali-soluble resins include phenolic novolaks such as phenol-formaldehyde novolak resins, cresol-formaldehyde novolak resins, or polyvinyl phenol resins, preferably those having an average molecular weight of about 500 to about 40,000, and more preferably from about 800 to 20,000. The novolak resins are preferably prepared by the condensation reaction of phenol or cresols with formaldehyde and are characterized by being light-stable, water-insoluble, alkali-soluble, and film-forming. The most preferred class of novolak resins is formed by the condensation reaction between a mixture of meta- and para-cresols with formaldehyde. Any and all photoactive compounds which make radiation-sensitive mixtures useful as photoresists may be employed herein. The preferred class of photoactive compounds (sometimes called "sensitizers") is o-quinonediazide compounds, particularly esters derived from polyhydric phenols, alkyl-polyhydroxyphenones, aryl-polyhydroryphenones, and can contain up to six or more sites for esterification. The most preferred o-quinonediazide esters are derived from 3-diazo-3,4-dihydro-4-oxo-naphthalene-1-sulfonic acid chloride (also know as 1,2-naphthoquinonediazide-4-sulfonyl chloride) and 6-diazo-5,6-dihydro-5-oxo-naphthalene-1-sulfonic acid chloride (also known as 1,2-naphthoquinonediazide-5-sulfonyl chloride). Specific examples include resorcinol 1,2-naphthoquinonediazide-4-sulfonic acid esters; pyrogallol 1,2-naphthoquinonediazide-5-sulfonic acid esters, 1,2-quinonediazidesulfonic acid esters of (poly)hydroxyphenyl alkyl ketones or (poly)hydroxyphenyl aryl ketones such as 2,4-dihydroxyphenyl propyl ketone 1,2-benzoquinonediazide-4-sulfonic acid esters, 2,4,dihydroxyphenyl hexyl ketone 1,2-naphthoquinonediazide-4-sulfonic acid esters, 2,4-dihydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid esters, 2,3,4-trihydroxyphenyl hexyl ketone, 1,2-naphthoquinonediazide-4-sulfonic acid esters, 2,3,4-trihydroxybenzophenone 1,2-naphthoquinonediazide-4-sulfonic acid esters, 2,3,4-trihydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid esters, 2,4,6-trihydroxybenzophenone 1,2-naphthoquinonediazide-4-sulfonic acid esters, 2,4,6-trihydroxybenzophenone 1,2-naphthoquinone-diazide-5-sulfonic acid esters, 2,2',4,4'-tetrahydroxy-benzophenone 1,2-naphthoquinonediazide-5-sulfonic acid esters, 2,3,4,4'-tetrahydroxy-benzophenone, 1,2-naphthoquinonediazide-5-sulfonic acid esters, 2,3,4,4'-tetrahydroxybenzophenone 1,2-naphthoquinone-diazide-4-sulfonic acid esters, 2,2',3,4',6'-pentahydroxybenzophenone 1,2-naphthoquinone-diazide-5-sulfonic acid esters, and 2,3,3',4,4',5'-hexahydroxy-benzophenone 1,2-naphthoquinonediazide-5-sulfonic acid esters; 1,2-quinonediazidesulfonic acid esters of bis[(poly)hydroxyphenyl]alkanes such as bis( p -hydroxyphenyl)methane 1,2-naphthoquinonediazide-4-sulfonic acid esters, bis(2,4-dihydroxyphenyl)methane 1,2-naphthoquinonediazide-5-sulfonic acid esters, bis(2,3,4-trihydroxyphenyl)methane 1,2-naphthoquinonediazide-5-sulfonic acid esters, 2,2-bis( p -hydroxyphenyl)propane 1,2-naphthoquinonediazide-4-sulfonic acid esters, 2,2-bis(2,4-dihydroxyphenyl)propane 1,2-naphthoquinonediazide-5-sulfonic acid esters and 2,2-bis(2,3,4-trihydroxyphenyl)propane 1,2-naphthoquinonediazide-5-sulfonic acid esters. Besides the 1,2-quinonediazide compounds exemplified above, there can also be used the 1,2-quinonediazide compounds described in J. Kosar, "Light-Sensitive Systems", 339-352 (1965), John Wiley & Sons (New York) or in S. DeForest, "Photoresist", 50, (1975), MacGraw-Hill, Inc. (New York). In addition, these materials may be used in combinations of two or more. Further, mixtures of substances formed when less than all esterification sites present on a particular polyhydric phenol, alkyl-polyhydroxyphenone, arylpolyhydroxyphenone have combined with o-quinonediazides may be effectively utilized in positive acting photoresists. Of all the 1,2-quinonediazide compounds mentioned above, 1,2-naphthoquinonediazide-5-sulfonic acid di-, tri-, tetra-, penta-, and hera-esters of polyhydroxy compounds having at least 2 hydroxyl groups, i.e., about 2 to 6 hydroxyl groups, are one class of preferred compounds. Among this class of preferred 1,2-naphthoquinonediazide compounds are 2,3,4-trihydroxy-benzophenone 1,2-naphthoquinone-diazide-5-sulfonic acid esters, 2,3,4,4'-tetrahydroxy-benzophenone 1,2-naphthoquinonediazide-5-sulfonic acid esters, and 2,2',4,4'-tetra-hydroxybenzo-phenone 1,2-naphthoquinonediazide-5-sulfonic acid esters. Another preferred 1,2-quinonediazide compound is mixed 1,2-naphthoquinonediazide-5-sulfonic acid esters of 2,2'3,3'-tetrahydro-3,3,3',3'-tetramethyl-1,1-spirobi (1H-indene)-5,5'6,6'7,7'-hexol (C.A.S. Reg. No. 32737-33-0). These 1,2-naphthoquinonediazide compounds may be used alone or in combination of two or more. Another preferred 1,2-naphthoquinone-5-diazide compounds are phenol 1,2-naphthoquinonediazide-5-sulfonic acid ester and bis[4-(2,6-dimethylphenol)]-4-catehol methane 1,2-naphthoquinone-5-diazide sulfonic acid esters. Another preferred class of photoactive o-quinonediazide compounds is prepared by condensing spirobiindane or spirobichroman derivatives with 1,2-naphthoquinonediazido-4-sulfonyl chloride or 1,2-naphtho-quinonediazide-5-sulfonyl chloride or a mixture thereof to make compounds of formula (A) shown below: wherein R 1 to R 8 are independently hydrogen, a hydroxyl group, a halogen atom, an alkyl group, an alkoxy group, an aralkyl group, an aryl group, an amino group, a monoalkylamino group, a dialkylamino group, an acylamino group, an alkylcarbamoyl group, an arylcarbamoyl group, an alkylsulfamoyl group, an arylsulfamoyl group, a carboxyl group, a cyano group, a nitro group, an acyl group, an alkyloxycarbonyl group, an aryloxycarbonyl group, an acyloxy group, (wherein R is hydrogen, or an alkyl group, and D is a 1,2-naphthoquinonediazido-5-sulfonyl group or a 1,2-naphthoquinonediazido-4-sulfonyl group); R 9 to R 12 are independently hydrogen or a lower alkyl group; and Z is oxygen or a single bond (i.e. the latter forms a five-member ring); provided that at least one of R 1 to R 8 is The halogen represented by R 1 to R 8 in the formula (A) is preferably chlorine, bromine or iodine. The alkyl group is preferably an alkyl group having 1 to 4 carbon atoms, such as methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl and tert-butyl. The alkoxy group is preferably an alkoxy group having 1 to 4 carbon atoms, such as methoxy, ethoxy, hydroxyethoxy, propoxy, hydroxypropoxy, isopropoxy, n-butoxy, isobutoxy, sec-butoxy and tert-butoxy. The aralkyl group is preferably a benzyl group, a phenethyl group or a benzhydryl group. The aryl group is preferably phenyl, tolyl, hydroxyphenyl or naphthyl. The monoalkylamino group is preferably a monoalkylamino group having 1 to 4 carbon atoms, such as monomethylamino, monoethylamino, monopropylamino, monoisopropylamino, mono-n-butylamino, monoisobutylamino, mono-sec-butylamino, or mono-tert-butylamino. The dialkylamino group is preferably a dialkylamino group with each akyl substituent having 1 to 4 carbon atoms, such as dimethylamino, diethylamino, dipropylamino, di-isopropylamino, di-n-butylamino, di-iso-butylamino, di-sec-butylamino, or di-tert-butylamino. The acylamino group is preferably an aliphatic group-substituted acylamino group such as acetylamino, propionylamino, butylamino, isobutylamino, isovalerylamino, pivaloylamino or valerylamino, or an aromatic group-substituted acylamino group such as benzoylamino or toluoylamino. The alkylcarbamoyl group is preferably an alkylcarbamoyl group having 2 to 5 carbon atoms, such as methylcarbamoyl, ethylcarbamoyl, propylcarbamoyl, isopropylcarbamoyl, n-butylcarbamoyl, isobutylcarbamoyl, sec-butylcarbamoyl, or tert-butylcarbamoyl. The arylcarbamoyl group is preferably phenylcarbamoyl or tolylcarbamoyl. The alkylsulfamoyl group is preferably an alkylsulfamoyl group having 1 to 4 carbon atoms, such as methylsulfamoyl, ethylsulfamoyl, propylsulfamoyl, isopropylsulfamoyl, n-butylsulfamoyl, sec-butylsulfamoyl, or tert-butylsulfamoyl. The arylsulfamoyl group is preferably phenylsulfamoyl or tolylsulfamoyl. The acyl group is preferably an aliphatic acyl group having 1 to 5 carbon atoms, such as formyl, acetyl, propionyl, butyryl, isobutyryl, valeryl, isovaleryl or pivaloyl, or an aromatic acyl group, such as benzoyl, toluoyl, salicyloyl, or naphthoyl. The alkyloxycarbonyl group is preferably an alkyloxycarbonyl group having 2 to 5 carbon atoms, such as methoxycarbonyl, ethoxycarbonyl, propoxycarbonyl, isopropoxycarbonyl, n-butoxycarbonyl, isobutoxycarbonyl, sec-butoxycarbonyl, or tert-butoxycarbonyl. The aryloxycarbonyl group is preferably phenoxycarbonyl. The acyloxy group is preferably an aliphatic acyloxy group having 2 to 5 carbon atoms, such as acetoxy, propionyloxy, butyryloxy, isobutyryloxy, valeryloxy, isovaleryloxy or pivaloyloxy, or an aromatic acyloxy group such as benzoyloxy, toluoyloxy, or naphthoyloxy. The lower alkyl group represented by R 9 to R 12 in the formula (A) is preferably an alkyl group having 1 to 4 carbon atoms, such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, or tert-butyl. In the formula (A) above, R 1 to R 8 are preferably a hydrogen atom, a hydroxy group or an -OD group wherein D is as defined above, and R 9 to R 12 are preferably a hydrogen atom or a methyl group. R is preferably an alkyl group having 1 to 4 carbon atoms, such as a methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, or t-butyl group. The proportion of the photoactive compound in the radiation-sensitive mixture may range from 5% to 40%, more preferably from 10% to 25% by weight of the nonvolatile (e.g., nonsolvent) content of the radiation-sensitive mixture. The proportion of total binder resin of this present invention in the radiation-sensitive mixture may range from 60% to 95%, preferably, from 75% to 90% by weight, of the nonvolatile (e.g., excluding solvents) content of the radiation-sensitive mixture. The third critical ingredient of the radiation-sensitive composition of the present invention is the polylactide compound or mixture of such compounds. The preferred proportion of the polylactide compound or compounds in the radiation-sensitive mixture may range from 0.5% to 10%, preferably 2% to 4% by weight of the nonvolatile (e.g., excluding solvents) content of the radiation-sensitive mixture. These radiation-sensitive mixtures may also contain, besides the resin, photoactive compound and polylactide compound, conventional photoresist composition ingredients such as other resins, solvents, actinic and contrast dyes, anti-striation agents, plasticizers, and other sensitivity enhancers. These additional ingredients may be added to the binder resin, photoactive compound and polylactide compound solution before the solution is coated onto the substrate. The binder resin, photoactive compound or sensitizer, and polylactide compound may be dissolved in a solvent or solvents to facilitate their application to the substrate. Examples of suitable solvents include methoxyacetoxy propane, diglyme, toluene, ethyl cellosolve acetate, n-butyl acetate, ethyl lactate, propylene glycol alkyl ether acetates, or mixtures thereof. Cosolvents such as xylene, n-butylacetate, or ethyl ethoxy propionate may also be used. The most preferred solvent is ethyl lactate alone or in combination with another solvent (e.g., ethyl 3-ethoxy propionate). The preferred amount of solvent may be from 50% to 500%, or higher, by weight, more preferably, from 100% to 400% by weight, based on combined resin, sensitizer, and polylactide compound weight. Actinic dyes help provide increased resolution on highly reflective surfaces by inhibiting back scattering of light off the substrate. This back scattering causes the undesirable effect of optical notching, especially on a substrate topography. Examples of actinic dyes include those that absorb light energy at approximately 400-460 nm [e.g., Fat Brown B (C.I. No. 12010); Fat Brown RR (C.I. No. 11285); 2-hydroxy-1,4-naphthoquinone (C.I. No. 75480) and Quinoline Yellow A (C.I. No. 47000) and Macrolex Fluoroyellow 10GN (C. I. No. Solvent Yellow 16:1)] and those that absorb light energy at approximately 300-340 nm [e.g. 2,5-diphenyloxazole (PPO-Chem. Abs. Reg. No. 92-71-7) and 2-(4-biphenyl)-6-phenyl-benzoxazole (PBBO-Chem. Abs. Reg. No. 17064-47-0)]. The amount of actinic dyes may be up to 10% weight levels, based on the combined weight of resin and sensitizer. Contrast dyes enhance the visibility of the developed images and facilitate pattern alignment during manufacturing. Examples of contrast dye additives that may be used together with the radiation-sensitive mixtures of the present invention include Solvent Red 24 (C.I. No. 26105), Basic Fuchsin (C.I. 42514), Oil Blue N (C.I. No. 61555) and Calco Red A (C.I. No. 26125) up to 10% weight levels, based on the combined weight of resin and sensitizer. Anti-striation agents level out the photoresist coating or film to a uniform thickness. Anti-striation agents may be used up to five percent by weight levels, based on the combined weight of resin and sensitizer. One suitable class of anti-striation agents is nonionic silicon-modified polymers. Nonionic surfactants may also be used for this purpose, including, for example, nonylphenoxy poly. The photoresist coatings produced by the above described procedure are particularly suitable for application to silicon/silicon dioxide-coated or polysilicon or silicon nitride wafers such as are utilized in the production of microprocessors and other miniaturized integrated circuit components. An aluminum/aluminum oxide wafer can be used as well. The substrate may also comprise various polymeric resins especially transparent polymers such as polyesters and polyolefins. After the resist solution is coated onto the substrate, the coated substrate may be preferably baked at approximately 70° to 125°C until substantially all the solvent has evaporated and only a uniform radiation-sensitive coating remains on the substrate. The coated substrate can then be exposed to radiation, in any desired exposure pattern, produced by use of suitable masks, negatives, stencils, or templates. Conventional imaging process or apparatus currently used in processing photoresist-coated substrates may be employed with the present invention. While ultraviolet (UV) light and electron beam radiations are the preferred sources of radiation, other sources such as visible light, ion beam, and X-ray radiant energy may be instead used. In some instances, a post-exposure bake at a temperature of 10°C higher than the soft bake temperature for 30-300 seconds is used to enhance image quality and resolution. The exposed resist-coated substrates are next developed in an aqueous alkaline developing solution. This solution is preferably agitated, for example, by nitrogen gas agitation. Examples of aqueous alkaline developers include aqueous solutions of tetramethylammonium hydroxide, sodium hydroxide, potassium hydroxide, ethanolamine, choline, sodium phosphates, sodium carbonate, and sodium metasilicate. The preferred developers for this invention are aqueous solutions of either alkali metal hydroxides, phosphates or silicates, or mixtures thereof, or tetramethylammonium hydroxide. Alternative development techniques such as spray development or puddle development, or combinations thereof, may also be used. The substrates are allowed to remain in the developer until all of the resist coating has dissolved from the exposed areas. Normally, development times from about 10 seconds to about 3 minutes are employed. After selective dissolution of the coated wafers in the developing solution, they are preferably subjected to a deionized water rinse to fully remove the developer or any remaining undesired portions of the coating and to stop further development. This rinsing operation (which is part of the development process) may be followed by blow drying with filtered air to remove excess water. A post-development heat treatment or bake may then be employed to increase the coating's adhesion and chemical resistance to etching solutions and other substances. The post-development heat treatment can comprise the baking of the coating and substrate below the coating's thermal deformation temperature. In the manufacture of microcircuitry units, the developed substrates may then be treated with a plasma gas etch employing conventional plasma processing parameters (e.g., pressure and gas flow rates) and conventional plasma equipment. Later, the remaining areas of the photoresist coating may be removed from the etched substrate surface by conventional photoresist stripping operations. The present invention is further described in detail by means of the following Examples. All parts and percentages are by weight unless explicitly stated otherwise. EXAMPLES 1-7 Polylactide Formation Testing One gram of ethyl lactate was added to each of seven aluminum dishes. A different resin (0.5 grams in dried form) was added to sir of these dishes. The seventh dish had nothing added to it. The six different resins added to the ethyl lactate were as follows: AMBERLYST A-15 styrene sulfonic acid-divinyl (benzene copolymer cation exchange resin available from Rohm & Haas of Philadelphia, PA. MITSUBISHI RCP-22H styrene sulfonic acid-divinyl benzene copolymer cation resin which is a highly porous cross-linked particulate resin available from Mitsubishi Kasei of Tokyo, Japan. TORAY TIN 100 a fibrous polystyrene/polyolefin composite cation resin having sulfonic acid exchange groups introduced onto the polystyrene resin available from Toray Industries Ltd. of Tokyo, Japan. DIANION CR-10 cross-linked styrene-divinyl benzene chelate resin copolymer (acid type) having iminodiacitic acid side chain groups and an average 1.2 micron particle diameter available from Mitsubishi Kasei of Tokyo, Japan. DIANION CR-20 cross-linked styrene-divinyl benzene chelate resin (amino type) having polyamine functional chelating groups in the copolymer and an average 1.2 micron particle diameter and available from Mitsubishi Kasei of Tokyo, Japan. NAFION NRSO 10-35 mesh perfluorinated polyethylene sulfonic acid available from DuPont. After the resin addition, the seven dishes were each heated at 135-145°C for three hours. Various amounts of polymeric residues were formed in these dishes by this heating. These residues were believed to be polylactides formed by the thermal polymerization of ethyl lactate. These residues were separated from the remaining ethyl lactate and the resin material. Each individual separated residue was then weighed. The amount of each residue as a percentage by weight of the original ethyl lactate added to the dish was determined. Those residue weight percentages are given in Table 1 below: Example Resin Residue Weight Percent 1 None 0.12 2 AMBERLYST A-15 10.1 3 MITSUBISHI RLP-22H 4.44 4 TORAY TIN 0.18 5 DIANION CR-10 2.23 6 DIANION CR-20 0.13 7 NAFION 2.78 These tests show the following conclusions. Ethyl lactate is not significantly thermally polymerized by itself. The potential of polylactide formation was in the following order: A-15 > RCP-22H > NAFION > >CR-10 >> TIN > C-20 Thus, ethyl lactate can be polymerized in the presence of an acidic substance but not in the presence of a basic substance. EXAMPLES 8-11 AND COMPARISON 1 Five different photoresist formulations were prepared using HiPR-6512 positive-working photoresist available from OCG Microelectronic Materials, Inc. of West Paterson, NJ, and varying amounts of polylactide. HiPR-6512 contains an alkali-soluble novolak resin and a naphthoquinonediazide sensitizer dissolved in an ethyl lactate:ethyl 3-ethoxy propionate solvent. The different formulations include a control with no polylactide addition (Comparison 1); an 0.5% by weight polylactide formulation (Example 8); a 5% by weight polylactide formulation (Example 9); a 10% by weight polylactide formulation (Example 10); and a 20% by weight polylactide formulation (Example 11). The five photoresist formulations were each processed on a minimum of five 4 inch diameter base silicon wafers. Each wafer was cleaned with HF vapor primed with HMDS and manually coated with one of the five different formulations. The coating track spin speeds were adjusted to achieve a a targeted post softbake thickness of 11,750 ± 50 angstroms (the targeted E max ). When coating the various formulations at constant spin speeds, a dramatic change in resist post soft bake thickness was noticed. Lower post soft baked film thicknesses were afforded as polylactide concentration was increased (see Table 2 below). After the coating operation, each coated wafer was softbaked at 90°C for 60 seconds on a Silicon Valley Group hot plate oven. Each wafer was subjected to a 7 x 14 array exposure matrix with 2 mJ/cm 2 energy increments on a Canon g-line stepper. After this exposure operation, each wafer was subjected to a post exposure bake at 115°C for 60 seconds on a Silicon Valley Group hot plate oven. Each wafer was then developed at 21°C using HPRD-441 positive developer available from OCG Microelectronic Materials, Inc. of West Paterson, NJ. The development process included spraying for 4 seconds at 500 rpm; spraying for 3 seconds at 250 rpm; spraying for 2 seconds at 0 rpm; and puddle develop for 50 seconds. After development, the exposure energy required to clear all resist from an open frame (E o ) was measured for each wafer tested. The measured values of the wafer for each formulation were averaged. The average E o value (within + or - 1 mJ/cm 2 ) for each formulation is given in Table 2 below: C-1 E-8 E-9 E-10 E-11 E max (Krpm) 5.23 5.18 4.52 3.94 3.19 E o (mJ/cm 2 ) 149 136 116 119 106 The results shown in Table 2 indicate two notable effects associated with the formation or introduction of polylactides into HiPR-6512 photoresist. One effect is that the viscosity of the resist is greatly reduced by the presence of polylactides. The second effect is that resist photospeed increases with an increase in polylactides present, even when resist thicknesses were normalized to an E max .

Claims: A radiation-sensitive composition comprising an admixture in a solvent of: at least one alkali-soluble binder resin, at least one photoactive compound and an effective sensitivity enhancing amount of at least one polylactide compound; the amount of said binder resin being about 60 to 95% by weight, the amount of said photoactive component being about 5% to about 40% by weight, based on the total solids content of said radiation-sensitive composition. A composition according to claim 1 in which said binder resin is an alkali-soluble phenolic novolak resin. A composition according to claim 1 or claim 2 in which said photoactive compound is an o-quinonediazide compound. A composition according to any one of the preceding claims In which said photoactive compound or compounds are present in the amount of about 10% to about 25% by weight, said binder resin is present in the amount of about 75% to about 90% by weight and said polylactide compound is present in the amount of 0.5% to about 10% by weight, all based on the total solids content of said radiation-sensitive composition. A composition according to any one of the preceding claims further comprising at least one substance selected from solvents, actinic and visual contrast dyes, plasticizers, anti-striation agents, and speed enhancers. The composition of Claim 1 characterized in that said polylactide compound is present in the amount of from about 2% to about 5% by weight, based on the total solids content of said radiation-sensitive composition. The process for forming a pattern on a substrate characterised by: (a) coating said substrate with a radiation-sensitive composition useful as a photoresist, said composition comprising an admixture in a solvent of: at least one alkali-soluble binder resin, at least one photoactive compound and an effective sensitivity enhancing amount of at lease one polylactide compound; the amount of said binder resin being about 60 to 95% by weight, the amount of said photoactive component being about 5% to about 40% by weight, based on the total solids content of said radiation-sensitive composition; (b) subjecting said coating on said substrate to an image-wise exposure of radiant light energy; and (c) subjecting said image-wise exposed coated substrate to a developing solution to form a image-wise pattern in the coating. A coated substrate comprising a substrate coated with a film of a radiation-sensitive composition characterized by an admixture of at least one alkali-soluble binder resin, at least one photoactive compound and an effective sensitivity enhancing amount of at least one polylactide compound; the amount of said binder resin being about 60 to 95% by weight, the amount of photoactive component being about 5% to about 40% by weight, based on the total solids content of said radiation-sensitive composition. A coated substrate according to Claim 8 in which said substrate comprises one or more compounds selected from silicon, doped silicon, aluminium, polymeric resins, silicon dioxide, doped silicon dioxide, silicon resins, gallium arsenide, aluminium gallium arsenide, titanium, tantalum, molybdenum tungsten, titanium silicides, tantalum silicides, molybdenum silicides, tungsten silicides, silicon nitride, copper, polysilicon ceramics, and aluminium/copper mixtures. A coated substrate according to claim 9 in which said substrate is a silicon wafer.

Inventors: FAVIER JAMES G JR, FERREIRA LAWRENCE, MCFARLAND JOHN A JR, FAVIER, JAMES G., JR., FERREIRA, LAWRENCE, MCFARLAND, JOHN A., JR.
Applicants: OCG MICROELECTRONIC MATERIALS, OCG MICROELECTRONIC MATERIALS, INC.
Application year: 1993
Main classification: G03F7
IPC codes: C09D4, G03F7, H01L21