Catalyst compositions and process for preparing Polyolefins

Abstract: Catalyst compositions comprising metallocene complexes having polymerisable groups may be used for the preparation of polyolefins. The catalyst compositions may be in the form of polymers comprising the metallocene complex and may be suitably supported on inorganic supports. Polymers having a broad range of density and melt indices as well as low hexane extractables and excellent powder morphology and flowability may be obtained by use of the catalyst compositions. Preferred metallocene complexes are zirconium complexes in which the polymerisable group is vinyl.

Description: The present invention relates to novel catalyst compositions comprising metallocene complexes and their use in the polymerisation of olefins. Metallocene complexes of Group IVA metals such as (cyclopentadienyl) 2 ZrCl 2 are known as homogeneous polyolefin catalysts in the presence of a suitable co-catalyst. Such catalyst systems have proven to be highly active towards ethylene and alpha olefins forming narrow molecular weight distributions of polyolefins. It would be highly desirable to provide catalysts which may be used, particularly in the gas phase, to prepare polymers which show good performance and processability. We have now discovered that catalyst compositions comprising metallocene complexes having a polymerisable group may advantageously be used in the polymerisation of olefins. Accordingly, the present invention provides a catalyst composition comprising a polymer of an olefin and at least one metallocene complex of general formula I or II M[XR n ] x Y p wherein R is a univalent or divalent 1-20C hydrocarbyl, or a 1-20C hydrocarbyl containing substituent oxygen, silicon, phosphorous, nitrogen or boron atoms with the proviso that at least one R group contains a polymerisable olefin group and contains at least three carbon atoms, and when there are two R groups present they may be the same or different, and when R is divalent it is directly attached to M, and replaces a Y ligand, wherein X is an organic group containing a cyclopentadienyl nucleus, M is a Group IVA metal, Y is a univalent anionic ligand, and for formula I, n is an integer of 1 to 10 x is either 1 or 2, and when x = 1, p = 0 - 3, that is, when all R are univalent, p = 3; when one R is divalent, p = 2, when two Rs are divalent, p = 1 and when three Rs are divalent, p = 0, when x = 2, p = 0-2, that is, when all R are univalent, p = 2; when one R is divalent, p = 1 and when two Rs are divalent, p = 0, and for formula II, n, m and l are integers or 0 such that n + m + l ≥ 1 , p = 0-2, that is, when all R are univalent, p = 2; when one R is divalent, p = 1 and when two Rs are divalent, p = 0, and Z is a C 1 to C 4 alkylene radical or a dialkyl germanium or silicon or an alkyl phosphine or amine radical or bis-dialkylsilyl or bis-dialkylgermanyl containing hydrocarbyl groups having 1 to 4 carbon atoms bridging the cyclopentadienyl nuclei, supported on an inorganic support. The metallocene complex of the present invention is a Group IVA metallocene complex of general formula I or II wherein M is suitably hafnium, zirconium or titanium. Preferably, M is zirconium. In the metallocene complex of general formula I or II, X comprises a cyclopentadienyl nucleus. Suitably X represents a single ring cyclopentadienyl nucleus or a fused ring one such as indenyl or tetrahydroindenyl or fluorenyl nucleus. Preferably X is a single ring cyclopentadienyl nucleus. In the metallocene complex of general formula I or II when there are two or more R groups present these may be the same or may be different. At least one of R contains the polymerisable, olefinic group. For the purposes of the present invention, a polymerisable group may be defined as a group which can be incorporated into a growing polymer chain. The polymerisable group of which R consists or comprises is an olefinic group. Preferably, the olefinic group consists of or comprises a vinyl group. R is an alkenyl group of 3 to 20, preferably 3-8 carbon atoms. The alkenyl may suitably be linear or branched, for example, an alkenyl group such as but-3-enyl or oct-7-en-yl; or an alkenyl aryl, alkenyl cycloalkyl or alkenyl aralkyl group, each having 8 to 20 carbon atoms, especially p-vinyl phenyl or p-vinyl benzyl. The olefinic group preferably has terminal ethylenic unsaturation. Additionally, one of the groups R may be a silyl group such as trimethyl silyl, triethyl silyl, ethyl dimethyl silyl, methyldiethyl silyl, phenyldimethyl silyl, methyldiphenyl silyl or triphenyl silyl R may also represent an organic hydrocarbyl group such as an alkyl group of 1 to 10 carbon atoms such as methyl, ethyl, propyl hydrocarbyl groups or a cycloalkyl group containing 5 to 7 carbon atoms, for example, cyclohexyl or an aromatic or aralkyl group of 6 to 20 or 7 to 20 carbon atoms respectively, for example, phenyl or benzyl. m and/or n is at least 1 and not greater than 10, eg 1-5, the maximum value depending on the number of possible substituent positions available in the X nucleus. Where for example X is cyclopentadienyl, the maximum for n is 5 whilst the maximum of n is 8 for the indenyl nucleus. Y is a univalent anionic ligand. Suitably the ligand is selected from hydride, halides, for example, chloride and bromide, substituted hydrocarbyls, unsubstituted hydrocarbyls, alkoxides, amides or phosphides, for example, a dialkylamide or a dialkyl or alkyl aryl phosphide group with 1 to 10 carbon atoms in each alkoxide or alkyl group and 6 to 20 carbons in the aryl group. The preferred metallocene complex of general formula I is when: M is zirconium R is C 3 to C 10 hydrocarbyl having a vinyl group X is a cyclopentadienyl group Y is chloride, n is 1 or 5 x is 2, and p is 2. The preferred metallocene complex of general formula II is when: M is zirconium R is C 3 to C 10 hydrocarbyl with a vinyl group X is an indenyl group Y is chloride n = m = 1 l = 0, and Z is a C 1 to C 4 alkylene or a bis dimethylsilyl containing C 1 to C 4 hydrocarbyl group. Examples of suitable metallocene complexes of general formula I and general formula II are illustrated in the attached Figures 1 and 2 respectively. Metallocenes complexes of general formula I, where x = 2, and general formula II may suitably be prepared by reacting a suitable group IVA metal salt of the general formula MYYCl 2 with a compound with a polymerisable group containing a cyclopentadienyl anion of the general formula [(R) n X]M' or [R n X-ZR l -XR m ]M' 2 . Suitably the M' is an alkaline metal. It is preferred that the Group IV metal salt is a tetra halide salt, most preferably a tetrachloride salt. It is preferred that the preparation of the metallocene complex is carried out in the presence of an anhydrous organic solvent such as an aliphatic ether such as diethyl ether or an aromatic hydrocarbon such as toluene or a cyclic ether such as tetrahydrofuran and under an inert atmosphere. The preferred conditions are in the presence of dry tetrahydrofuran and under dry nitrogen. If a metallocene complex is to be prepared in which the R groups are different then for formula (I) where x = 2 two different [(R) n X]M' compounds are used and for formula II, the appropriate mixed compound is used. The salt of general formula [(R) n X]M' (III) may be prepared by any suitable method from the corresponding compound of formula (R) n XH (IV) by reaction with a suitable metal. Suitably, the metal is an alkaline metal selected from lithium, sodium or potassium. The metal may also be an organo hydrocarbyl alkali metal compound such as an alkyl or phenyl sodium, lithium or potassium compound. Preferably, the metal is lithium. The compound (R) n XH may itself be formed by reaction of a compound of general formula XM'' (V) where M'' is an alkali metal. Suitably XM'' is sodium cyclopentadiene. XM'' may be reacted with a compound R-R'' where R is as defined above and R'' is a suitable leaving group. Alternatively, XM'' and X'M'' may be reacted with Z(R) l R'' 2 . R'' may suitably be a nucleophilic leaving group. Preferably, R'' is a halide selected from chloride, bromide or iodide; an ester group, especially a sulphonate ester such as alkane sulphonate or aryl sulphonate. Suitably, the aforementioned reactions are carried out in the presence of an anhydrous organic solvent and under an inert atmosphere. Where it is desired to prepare the metallocene complex of general formula I wherein x is 1, the complex may suitably be prepared using procedures well known in the field. For example, the cyclopentadiene compound X(R) n H could be reacted with a metallating agent where the metal (M'') is a Group I alkali metal to provide X(R) n M''. Metallating agents include n-BuLi or MeLi. Suitably X(R) n M'' is then reacted with trimethylsilyl chloride in an appropriate solvent to provide (Me 3 Si)X(R) n . Further reaction with a Group IV metal halide will suitably provide a metallocene complex of general formula M[X(R) n ]Y 3 . This synthesis is particularly preferred for the preparation of the titanium metallocene, although variations of the synthesis can be used to prepare analogous zirconium and hafnium complexes. In another example, if X(R) n contains one or more functional groups with a protonated heteroatom, additional equivalents of the metallating reagent will deprotonate both the cyclopentadiene nucleus and one or more of the heteroatoms. Reaction of the metallated polyanion with a Group IV metal halide will suitably provide a metallocene complex of general formula M[X(R) n ]Yt, where Y is halide and t = 0 - 2. In this case, (3 - t) R groups will bridge the cylopentadienyl nucleus and the metal atom by means of a bond between the metal atom and a deprotonated heteroatom. If desired the complexes of formula I or II wherein Y is halide may be converted into the complexes of formula I or II wherein Y is the other specified groups by reaction of the halide with an appropriate nuclceophile eg alkoxide. The metallocene complex of general formula I or II may be used in the presence of a suitable co-catalyst. Suitably the co-catalyst is an organometallic compound having a metal of Group IA, IIA, IIB or IIIB of the periodic table. Preferably, the metals are selected from the group including lithium, aluminium, magnesium, zinc and boron. Such co-catalysts are known for their use in polymerisation reactions, especially the polymerisation of olefins, and include organo aluminium compounds such as trialkyl, alkyl hydrido, alkylhalo and alkyl alkoxy aluminium compounds. Suitably each alkyl or alkoxy group contains 1 to 16 carbons. Examples of such compounds include trimethylaluminium, triethylaluminium, diethyl aluminium hydride, triisobutyl aluminium, tridecyl aluminium, tridodecyl aluminium, diethyl aluminium methoxide, diethyl aluminium ethoxide, diethyl aluminium phenoxide, diethyl aluminium chloride, ethyl aluminium dichloride, methyl diethoxy aluminium and methyl aluminoxane. The preferred compounds are alkyl aluminoxanes, the alkyl group having 1 to 10 carbon atoms, especially methyl aluminoxane. Where Y in the general formula I or II is independently hydrogen or hydrocarbyl, suitable co-catalysts also include Bronsted or Lewis acids. The co-catalyst may be added to the polymerisation medium along with the metallocene-containing Polymer. Suitably, the amount of co-catalyst mixed with metallocene complex may be such as to provide an atom ratio of M from the metallocene to the metal in the co-catalyst of 1-10,000: 10,000-1 for aluminoxanes and 1-100: 100-1 otherwise. One or more metallocene complexes of general formula I or II, in the presence of a co-catalyst, are used to produce polymers containing one or more metals M. The metallocene containing polymer usually contains a high group IVA metal content and is usually a low yield polyolefin, comprising one or more metallocene complexes of general formula I and/or II with one or more olefins. Thus, according to the present invention there is provided a catalyst composition suitable for use in the polymerisation of olefins comprising a polymer containing a metallocene complex of general formula I or II as described above, preferably as a copolymer with at least one alpha-olefin and/or ethylene. The metallocene containing polymer may suitably be prepared by heating one or more metallocene complexes of general formula I and/or II, optionally supported, usually in the presence of an inert solvent and/or suitable co-catalysts as described above and preferably in the presence of one or more alpha-olefins or ethylene, so that the metallocene complex is co-polymerised. Suitably the alpha-olefin may be a C3 to C10 olefin. The conditions of formation of the metallocene containing polymer are substantially similar to those for the polymerisation of olefins described hereafter, but with a lower degree of polymerisation, eg for a shorter time. The metallocene containing polymer may suitably be impregnated onto the support material under anhydrous conditions and under an inert atmosphere. The impregnation can be conducted using an inert solvent, in which case the solvent may then be evaporated under reduced pressure. The impregnated support may then be heated to remove any remaining solvent. Preferably, the metallocene containing polymer is dissolved in the inert solvent. Suitable inert solvents include aromatic hydrocarbons, such as toluene. Any suitable inorganic support may be used for example, inorganic oxides such as silica, alumina. Equally suitable inorganic halides may be used. Suitable halides include Group IIA halides eg magnesium chloride. It is a particular advantage of this aspect of the present invention that an active catalyst composition comprising a metallocene containing polymer may be supported on an inorganic oxide or metal halide support without using cocatalysts such as aluminoxanes as the means of support. Aluminoxanes are expensive and difficult to handle and it is desirable to minimise their use. Conventionally, they are used as both a means of binding metallocenes to inorganic supports and as cocatalysts. The current invention obviates the need for aluminoxanes as a means of binding. This allows their use as cocatalysts only or not at all by selecting alternative cocatalysts, eg. Bronsted or Lewis acids. A further advantage of this aspect of the current invention is that it provides a support method which prevents desorption of metallocene complexes from a supported catalyst under certain polymerisation process conditions, eg slurry. Conventional metallocene support methods where the metallocene complex is simply adsorbed onto the support surface, with or without the use of cocatalysts such as aluminoxanes, may undergo some metallocene complex desorption under polymerisation process conditions. The resulting metallocene containing polymer may be reacted with an olefin to produce a polyolefin as described below. The polymer may be supported on an inorganic support as described above and may suitably be mixed with a co-catalyst. The present invention also provides a process for the production of polyolefins, in particular homopolymers of ethylene and copolymers of ethylene with minor amounts of at least one C3 to C10, preferably C3 to C8 alpha-olefin. The process comprises contacting the monomer or monomers, optionally in the presence of hydrogen, with a catalyst composition comprising at least one metallocene complex of formula I or II in an olefin polymerisation catalyst composition according to the above aspects of the present invention at a temperature and pressure sufficient to initiate the polymerisation reaction. The catalyst composition is in the form of a metallocene containing polymer of the metallocene complex as described above. Suitably the alpha olefin may be propylene, butene-1, hexene-1, 4-methyl pentene-1 and octene-1 and may be present with the ethylene in amounts of 0.001-80% by weight (of the total monomers). The polymers or copolymers of ethylene thus obtained can have densities, in the case of homopolymers of about 950 to 960 or 965 or in the case of copolymers, as low as 915 kg/m3 or even lower eg less than 900 kg/m3. The C3 to C8 alpha-olefin content in the copolymers of ethylene can be about from 0.01% to 10% by weight or more. The olefin polymerisation catalyst compositions according to the present invention may be used to produce polymers using solution polymerisation, slurry polymerisation or gas phase polymerisation techniques. Methods and apparatus for effecting such polymerisation reactions are well known and described in, for example, Encyclopaedia of Polymer Science and Engineering published by John Wiley and Sons, 1987, Volume 7, pages 480 to 488 and 1988, Volume 12, pages 504 to 541. The catalyst according to the present invention can be used in similar amounts and under similar conditions to known olefin polymerisation catalysts. The polymerisation may optionally be carried out in the presence of hydrogen. Hydrogen or other suitable chain transfer agents may be employed in the polymerisation to control the molecular weight of the produced polyolefin. The amount of hydrogen may be such that the percentage of the partial pressure of hydrogen to that of olefin(s) is from 0.01-200%, preferably from 0.05-10%. Typically, the temperature is from 30 to 110°C for the slurry or "particle form" process or for the gas phase process. For the solution process the temperature is typically from 100 to 250°C. The pressure used can be selected from a relatively wide range of suitable pressures, e.g. from subatmospheric to about 350 MPa. Suitably, the pressure is from atmospheric to about 6.9 MPa, or may be from 0.05-10, especially 0.14 to 5.5 MPa. In the slurry or particle form process the process is suitably performed with a liquid inert diluent such as a saturated aliphatic hydrocarbon. Suitably the hydrocarbon is a C4 to C10 hydrocarbon, e.g. isobutane or an aromatic hydrocarbon liquid such as benzene, toluene or xylene. The polymer is recovered directly from the gas phase process or by filtration or evaporation from the slurry process or evaporation from the solution process. By using the catalyst compositions according to the present invention polymers having both good mechanical properties and good processability may be obtained. For example both cast and blown type films which exhibit very high impact strength combined with excellent processability may be obtained. For catalyst compositions containing one metallocene complex, polymers of unimodal molecular weight distribution may be obtained. In the case where two or more metallocene complexes are present the resulting polymers may have bimodal or multimodal molecular weight distributions and, in the case of copolymerisation, have non-uniform branch distributions within the molecular weight distribution. The metallocene-containing polymer catalyst compositions of the present invention may also be used to prepare polyolefins having much lower melt indexes compared to those prepared using other metallocene catalysts. Melt Index Measurement The Melt Index (MI) of the polymers produced was determined according to ASTM D1238 Condition E, 2.16 kg at 190°C while the High Load Melt Index (HLMI) was according to ASTM D1238 condition F, 21.6 kg at 190°C. Method for Measuring the Molecular Weight Distribution The molecular weight distribution of a (co)polymer is calculated according to the ratio of the weight-average molecular weight, Mw, to the number-average molecular weight distribution curve obtained by means of a "WATERS" (trademark) model "150 C" gel permeation chromatograph (High Temperature Size Exclusion Chromatograph), the operating conditions being the following: solvent: 1,2,4-trichlorobenzene; solvent flow rate: 1.0 ml/minute; three "SHODEX" (trademark) model "AT 80 MS" columns of 25 cm length are employed; temperature: 145°C; sample concentration: 0.1% by weight; injection volume: 500 microlitres; Universal standardisation using monodisperse polystyrene fractions. The present invention will now be further illustrated with reference to the following examples: All of the reactions and purifications detailed below involving organometallic species were carried out under a dry nitrogen atmosphere using standard vacuum-line techniques. Tetrahydrofuran and diethyl ether were dried over sodium benzophenone ketyl and distilled. Toluene was dried over sodium-potassium and distilled. Dichloromethane was dried over 4Å molecular sieves. All other reagents were used as received. Impact Measurement The impact measurement of polymer films was determined according to ASTM D1709-85. The test method determines the energy required to cause a polyethylene film to fail under specified conditions of impact of a free falling dart. The energy is expressed in terms of the weight. Perforation Energy The energy required to cause polyethylene film to perforate under specified conditions was determined according to ASTM D781 using an Adamel-Lhomargy puncture tester. The present invention will be further illustrated with reference to the following examples. Preparation Example 1: Preparation of Bis (3-butenyl-cyclopentadienyl) Zirconium Dichloride Step (a) Preparation of 3-buten-1-tosylate To a solution of 100 g (525 mmol) p-toluenesulphonyl chloride in 200 ml of dry pyridine cooled to 0°C was added 21.1 g (29.3 mmol) 3-buten-1-ol. The reaction solution was thoroughly mixed and allowed to stand in a refrigerator at -5°C overnight. The reaction mixture was then poured with stirring into 200g of ice/water. The oily tosylate product was extracted from the aqueous mixture with 3 x 300 ml aliquots of ether. The combined ethereal fractions were washed twice with 300 ml of cold aqueous hydrochloric acid (conc HCl:water 1:1 w/w) to remove pyridine and then with 300 ml water, dried over potassium carbonate and sodium sulphate and decolourised with activated carbon. The suspension was filtered and the ether evaporated from the filtrate under reduced pressure to leave a pale yellow oil. The oil was then washed with cold pentane to remove impurities and induce crystallisation. 51.0 g of spectroscopically pure product ('H NMR) as a microcrystalline white solid were isolated (225 mmol, 76.7%). Step (b) Preparation of 3-butenyl cyclopentadiene To a solution of 25.0 g (110 mmol) 3-buten-1-tosylate prepared according to step (a) above in 200 ml THF cooled to 0°C was added 68.9 ml of 2.0 M (138 mmol) sodium cyclopentadienylide in THF. The reaction mixture was allowed to warm to room temperature and was stirred for 16 h. 100 ml concentrated aqueous saline solution was added and the product extracted with ether (3 x 75 ml). The combined organic fractions were dried over magnesium sulphate for 2 hours, filtered and the solvents removed under reduced pressure using a rotary evaporator to yield a dark brown oil. The crude product was distilled under reduced pressure (b.p. 50-51°C @ 15 mm Hg) to give 5.71 g of a colourless oil (47.6 mmol, 43.3%). Step (c) Preparation of Bis (3-butenyl cyclopentadienyl) zirconium dichloride 19 ml of 2.5 M (47.5 mmol) butyllithium in mixed C 6 alkane solvent was slowly added to 5.7 g (47.5 mmol) 3-butenylcyclopentadiene prepared according to step (b) above in 50 ml THF cooled to 0°C and stirred for 1 hour. The lithium 3-butenyl cyclopentadienylide solution produced was added to 4.43 g (19.0 mmol) zirconium tetrachloride in 50 ml THF cooled to 0°C and stirred for 65 hours. The volatiles were removed under vacuum and the residue extracted with ether and filtered. The product was precipitated as a microcrystalline white solid upon slow cooling of the solution to -50°C. Recrystallisation from cold ether (-12°C) yielded 1.54 g of spectroscopically pure product ( 1 H NMR) as colourless needles (3.85 mmol, 20.2%). Preparation Example 2: Preparation of Bis(3-propenylcyclopentadienyl)zirconium Dichloride Step (a) Preparation of 3-Propenylcyclopentadiene To a rapidly stirred solution of allylbromide (42.73g; 0.35mol) dissolved in dry THF (200ml) at 0°C was added a solution of sodium cyclopentadiene (220ml, 2.0M; 0.44mol) in THF. The reaction was stirred for 2hrs during which time it was allowed to warm to room temperature. Iced water (1500ml) was added and the organic product extracted with diethylether (3x400ml). The combined organic fractions were dried over magnesium sulphate overnight, filtered and the solvents removed under reduced pressure using a rotary evaporator to yield a pale brown oil. The crude product was distilled under reduced pressure (b.p. 35-45 °C @ 17 mm Hg) to give 11.17g of a colourless oil (0.105mol, 33.3%). Step (b) Preparation of bis (3-propenylcylopentadienyl)zirconium Dichloride Methyllithium solution (75.25ml, 1.4M; 0.105mol) in diethylether was slowly added to a rapidly stirred solution of propenylcyclopentadiene (11.17g, 0.105mol) in dry diethylether at 0°C. The reaction was warmed to room temperature and stirring continued until gas evolution had ceased. The precipitated lithium propenylcyclopentadienylide was isolated by filtration, washed with diethylether (2x100ml) and pumped to dryness to give 10.65g (0.095mol) of fine white powder. To a rapidly stirred THF solution (100ml) of the lithium propenylcyclopentadienylide at 0°C was added zirconium tetrachloride (11.09g, 47.5mmol) dissolved in dry THF (100ml). The reaction mixture was allowed to warm to room temperature and was stirred for 16 hrs. The volatiles were removed under vacuum and the residue extracted with diethylether (4x100ml) and filtered. The product was obtained as a microcrystalline white solid upon slow cooling of the solution to -78°C. Recrystallisation from cold ether yielded 13.33g of spectroscopically pure product (1H NMR) as colourless needles (35.8 mmol, 75.4%). Preparation Example 3: Preparation of Supported Catalyst 15 mol of MAO (10% solution in toluene, WITCO) and 100 mmol bis(propenylcyclopentadienyl)zirconium dichloride (Example 2) in 1.5 litres toluene were maintained at room temperature with stirring for 15 min. 2 kg of silica (GRACE SD 3217.50 dried at 800°C for 5 hrs) was added to the mixture to form a suspension. The resultant mixture was stirred for 1 hr at room temperature, the suspension transferred to a drier and the solvent removed at 120°C to provide a free-flowing spherical powder. Preparation Examples 4-5 The procedure in Example 3 was repeated using bis(3-butenylcyclopentadienyl)zirconium dichloride (prepared as in Example 1) and Crosfield ES70 silica in Example 4 and Grace SD 3217.50 silica in Example 5. Example 6 - Ethylene homopolymerisation 400g sodium chloride were introduced under nitrogen into a 2.5 litre stainless steel autoclave equipped with a stirrer. The temperature was increased to 80°C and the autoclave charged with supported catalyst obtained in Example 3 (0.02 mmol Zr). Ethylene pressure was increased to 0.8 MPa. After 2 hrs the sodium chloride was removed by washing with water to yield 245g polyethylene of very good morphology having a melt index of 0.8g/10 min measured at 190°C under a load of 2.16 kg (ASTM-D-1238-condition E), bulk density 0.42g/cm3, an average particle diameter measured by laser diffraction of 545 µm and 0.6% of fine powder less than 125 µm. Preparation Example 7 - Ethylene/l-butene copolymerisation The procedure of Example 6 was repeated using supported catalyst (0.025 mmol Zr), an ethylene pressure of 0.9 MPa and the introduction of l-butene into the autoclave to produce a polymer of density of 0.920g/cm3 non annealed. After 70 min. the sodium chloride was removed by washing with water to yield 575g of copolymer of very good morphology containing 4.8 wt% of butene, having a melt index of 3g/10 min. measured at 190°C under a load of 2.16 kg, 0.6% Kumagawa C6-extractables and bulk density 0.43g/cm3. Preparation Example 8 - Ethylene/l-butene copolymerisation The procedure in Example 7 was repeated using supported catalyst as described in Example 4 (0.1 mmol Zr) and an ethylene pressure of 0.25 MPa. l-Butene was introduced to give a polymer of density of 0.916g/cm3 non annealed. After 2 hrs the sodium chloride was removed to yield 530g of copolymer of very good morphology having a melt index of 7.8g/10 min measured at 190°C under a load of 2.16 kg, 2% Kumagawa C6 extractables and a bulk density of 0.44g/cm3. Preparation Example 9 - Ethylene homopolymerisation The procedure was carried out in a fluidised bed reactor having a diameter of 15cm, height of 1m and operating with the aid of a fluidisation gas propelled at an upward velocity of 25 cm/s. Ethylene pressure was maintained at 1 MPa, hydrogen maintained during 2 hrs 35 min. at a ratio of PH2/PC2 = 0.004 and the temperature maintained at 90°C. 1000g of anhydrous homopolyethylene was introduced as a charge powder followed by catalyst of Example 5 (0.18 mmol Zr). 4630g polyethylene was obtained having a melt index of 3.7g/10 min measured at 190°C under a load of 2.16 kg, density of 0.961g/cm3 non annealed and a bulk density of 0.36g/cm3. Preparation Example 10 - Ethylene/l-butene copolymerisation The procedure in Example 9 was repeated using an ethylene pressure of 1.15 MPa while l-butene was maintained for 3 hrs at a ratio of PC4/PC2 = 0.042 at a temperature of 55°C. Supported catalyst of Example 5 (0.07 mmol Zr) was used to yield a copolymer having a melt index of 1.2g/10 min measured at 190°C under a load of 2.16 kg, a density of 0.913g/cm3, a bulk density of 0.41g/cm3 and 0.6% Kumagawa C6 extractables. Preparation Example 11 - Ethylene/n-hexene copolymerisation Ethylene, n-hexene and nitrogen were fed into a continuous fluidised bed reactor of diameter 45 cms maintained at a total pressure of 1.9 MPa. The gas composition was maintained constant at PC6/PC2 = 0.03 and supported catalyst of Example 3 injected into the reactor continuously at a rate of 7g/hr to maintain a constant reaction rate in the reactor. Polymer product was continuously removed from the reactor through a valve as copolymer of non annealed density of 0.916g/cm3 non annealed having 1 ppm of catalyst residues and 560 Pa.s of shear viscosity at 100 radian/s. The reaction conditions were varied to prepare different types of copolymer which all exhibit very high impact strength combined with excellent processability. The results are given in Table 1. Example 12 (Comparative) A mixture of 150 mmol MAO (WITCO) and bis(n-butylcyclopentadienyl)zirconium dichloride in 50 ml of toluene were stirred at room temperature under nitrogen. 20g silica (Grace SD 3217.50, dried at 800°C for 5 hr) were added to the mixture to form a suspension and the mixture stirred for 1 hr at room temperature before raising the temperature to 120°C and the solvent removed to give a free flowing powder. Example 13 (Comparative) 400g of sodium chloride were introduced into a 2.5 litre stainless steel autoclave equipped with a stirrer. The temperature was increased to 80°C and the autoclave charged with the supported catalyst obtained in Example 12 (0.1 mmol Zr). Ethylene pressure was increased to 0.2 MPa and after 5 hrs the sodium chloride removed by washing with water to yield polyethylene having a melt index of 7.7g/10 min measured at 190°C under a load of 2.16 kg (ASTM-D-1238 Condition-E), an average particle diameter measured by laser diffraction of 376 µm and 7.5% of fine powder less than 125 µm. Examples 14 - 16 - Preparation of Metallocene-containing Polymers Preparative details for each polymer, and the zirconium content before and after toluene washing, are given in Table 2. A solution of MAO in toluene was added to the metallocene complex and the solution stirred to dissolve the metallocene. The mixture was heated to 50°C and ethylene introduced at a measured flow rate. After the ethylene flow was stopped the mixture was filtered and the solid prepolymer washed with 5 25ml aliquots of toluene at room temperature. Residual solvent was removed under vacuum. A sample of each metallocene containing polymer (0.5 - 1g) was transferred to a round bottom flask, 100ml toluene added and the mixture stirred while the flask was heated to 100°C for 3 hrs resulting in a clear pale yellow solution. The flask was cooled to room temperature resulting in reprecipitation of the polymer. The solution was filtered and the polymer washed with 5 25ml aliquots of toluene at room temperature. Residual solvent was removed under vacuum. Due to the high solubility of the free metallocene complex in toluene, the zirconium analyses before and after washing indicate that the metallocene complex has been incorporated into the polymer. Example 17 - Preparation of Supported Metallocene-containing Polymer 750 mmol (Al) MAO (WITCO, 10% in toluene), and 5 mmol of bis(n-butenylcyclopentadienyl)zirconium dichloride (Example 1) in 200 ml toluene were added under N2 to 1.3 litres of toluene at 80°C in a stainless steel reactor. Ethylene was introduced into the reactor at a uniform rate of 100g/h for 30 min. and then the reactor cooled to 20°C and the contents washed several times with cold toluene. No Zr was detected in the toluene washings. The toluene was removed under vacuum and 10g of the resultant product extracted under N2 with boiling toluene in the presence of 20g of silica SD 3217.50 in the recovery flask. The content of the flask was transferred to a rotatory drier and the solvent removed to yield the free flowing catalyst. Example 18 - Ethylene homopolymerisation 6.8g of the supported metallocene containing polymer prepared in Example 17 (0.078mmol Zr) was premixed with 36 mmol of Al as MAO (WITCO, 10% in toluene) and the toluene removed under vacuum. 400g of sodium chloride were introduced under N2 into a 2.5 litre stainless steel autoclave, the temperature increased to 80°C and the autoclave charged with the supported catalyst. Ethylene pressure was increased to 0.2 MPa and after 5 hrs the sodium chloride was removed by washing with water to yield 420g of polyethylene having a melt index of 0.7g/10 min measured at 190°C under a load of 2.16 kg (ASTM-D-1238Condition E) and a bulk density of 0.42g/cm3. By using a supported metallocene containing polymer a much lower melt index was achieved when compared with other metallocene catalysts as shown by comparative Example 13. Example 19 - Preparation of Supported Metallocene-containing Polymer Metallocene containing polymer prepared according to Example 14 (0.27g) was dissolved in 15 ml toluene at 80°C and added to 1.73g Crosfield ES70 silica (precalcined in flowing N2 at 500°C for 4 hrs) with stirring. The solvent was removed in vacuum while maintaining the temperature at 80°C to yield a white, free flowing powder having 0.12% w/w Zr. Example 20 - Ethylene polymerization 8.9 mmol of MAO (Shering, 30% in toluene) in 10 ml toluene were added to 1.2g of the catalyst of Example 19 with stirring at 25°C for 90 min. The solvent was removed under vacuum at 25°C to leave a free flowing powder containing 0.084% w/w Zr. 0.55g (5.07 x 10-3 mmol Zr) of the powder was added to a 3 litre stirred gas phase polymerisation reactor. No further addition of MAO cocatalyst was made. Ethylene (0.8 MPa) was introduced at 75°C and the flow allowed to maintain constant reactor pressure. After 2 hrs the pressure was reduced rapidly and the reaction quenched using 2-propanol to yield 30g of polyethylene having Mw of 228,000, Mw/Mn of 2.6 and 370g PE/mmol Zr.h.b.). Preparative Density g/cm 3 MI g/10 min Impact g Perforation Energy (dj) Output/pressure kg/h.b. Thickness (d) µm 0.914 2.9 550 94 0.25 25 0.916 2.3 533 67 0.25 38 0.918 2.8 271 35 0.24 25

Claims: A catalyst composition for use in the polymerization of olefins comprising a polymer of an olefin and at least one metallocene of the general formula II or II M[XR n ] x Y p wherein R is a univalent or divalent 1-20 carbon hydrocarbyl or a 1-20 carbon hydrocarbyl containing substituent oxygen, silicon, nitrogen or boron atoms with the proviso that at least one R group contains a polymerizable olefinic group containing 3-20 carbon atoms and when there are two or more R groups present they may be the same or different, and when R is divalent it is directly attached to M and replaces a Y ligand, and wherein X is an organic group containing a cyclopentadienyl or indenyl group, M is a Group IVA metal, Y is a univalent anionic ligand, and for Formula I n is an integer of 1 to 10, x is either 1 or 2, and when x = 1, p = 0 to 3 when x = 2 p = 0 to 2; and for Formula II, n, m or 1 are integers or 0 such that n + m + 1 ≥ 1 , p = 0-2, and Z is a radical selected from the group consisting of a C 1 to C 4 alkylene, a dialkyl germanium or dialkyl silicon, an alkyl phosphine, an amine, bis-dialkyl silyl, and bis-dialkylgermanyl containing a hydrocarbyl group having 1 to 4 carbon atoms supported on an inorganic support. A catalyst composition according to claim 1 wherein M in general formula I or II is zirconium. A catalyst composition according to claims 1 or 2 wherein the polymerisable olefinic group in a vinyl group A catalyst composition according to claim 1 wherein the inorganic support is selected from silica, alumina and/or a Group IIA metal halide. A catalyst composition according to claim 4 wherein the support is silica. A catalyst composition according to any of the preceding claims further comprising a cocatalyst. A catalyst composition according to claim 6 wherein the cocatalyst is a Group IA, IIA, IIB or IIIB organometallic compound. A catalyst composition according to claim 7 wherein the cocatalyst is an organoaluminium compound. A process for preparing the catalyst composition according to claim 1 characterised in that the polymer of the olefin and metallocene complex is dissolved in an inert solvent and deposited on the inorganic support. A catalyst composition according to claim 1 wherein the metallocene complex is bis(3-butenylcyclopentadienyl) zirconium dichloride. A catalyst composition according to claim 1 wherein the metallocene complex is bis(3-propenylcyclopentadienyl) zirconium dichloride. A process for the polymerisation of olefins comprising contacting at least one olefin monomer with a catalyst composition according to any of the preceding claims. A process according to claim 12 wherein the olefin monomer is ethylene. A process according to claims 12 or 13 wherein the polymerisation is carried out in the gas phase.

Inventors: CHABRAND CHRISTINE JACQULINE, LITTLE IAN RAYMOND, MCNALLY JOHN PAUL, CHABRAND, CHRISTINE JACQULINE, LITTLE, IAN RAYMOND, MCNALLY, JOHN PAUL
Applicants: BP CHEM INT LTD, BP CHEMICALS LIMITED
Application year: 1993
Main classification: C08F4
IPC codes: C08F4, C08F10