Surface hardened biocompatible metallic medical implants

Abstract: This invention provides surface hardened, abrasion resistant high strength, biocompatible metal medical implants, in particular, titanium alloy implants which do not include any elements which have been shown or suggested as having short term or long term potential adverse effect from a standpoint of biocompatibility. Further, the invention provides methods of strengthening and hardening the surfaces of other titanium, zirconium, and cobalt-based alloy implants with small concentrations of a metal solute such as zirconium, yttrium, tantalum, aluminum, silicon, chromium, or thorium via internal oxidation or nitridation. Alternatively, nitrogen, oxygen, or carbon can be diffused directly into the surface of the implants by interstitial hardening to further increase the surface abrasion resistance of these internally oxidized or internally nitridized implant metal or metal alloys.

Description: This invention relates to surface hardening of biocompatible metals and alloys, suitable for use as material for a medical implant, including in particular, niobium, titanium, and zirconium based alloys which do not include any elements which have been shown or suggested as having short term or long term potential adverse biological effects. More specifically, this invention relates to medical implants made of these surface-hardened alloys with improved resistance to micro-fretting wear and surface abrasion. The most common materials used for load-bearing medical implants such as orthopedic or cardiovascular implants, are metallic alloys, ceramics, and composites formed from biocompatible polymers and various reinforcing materials. Metals and metal alloys such as stainless steel, Co-Cr-Mo alloy, titanium, and titanium alloys have been used successfully for many years as implant materials, particularly for orthopaedic applications. These materials have the requisite strength characteristics needed for such implants but are susceptible to fretting, wear, and corrosion in the body unless treated to reduce these effects. Particulates produced by joint articulation processes or micromotion between assembled devices tend to cause accelerated wear of prosthetic joints and trauma devices. Further, concern has been raised about potential abrasion between implant metals and adjacent bone and bone cement. This abrasion creates particulates which are associated with adverse cellular response, including bone cell death and eventual loosening of the implant and subsequent revision. To prevent micro-fretting of the implant surface, the surface may be coated with an amorphous diamond-like carbon coating or a ceramic-like coating, such as titanium nitride or titanium carbide, using chemical or plasma vapour deposition techniques to provide a hard, impervious, smooth surface coating. These coatings are especially useful if the prosthesis is subjected to conditions of wear, such as, for instance, in the case of bearing surfaces of knee or hip prostheses, or between screws and bone plates or modular implants. For the case of orthopaedic implant bearing sufaces, bone cement fragments can abrade these relatively thin (up to about 5 microns) surface coatings with time and create hard, abrasion products from these coatings which in turn further accelerate abrasion and wear of the softer underlying metal substrate. Methods for providing amorphous diamond-like carbon coatings are known in the art and are disclosed in, for example, European Patent Application No.302,717 to Ion tech and Chemical Abstract 43655P, Vol.101 describing Japan Kokai 59/851 to Sumitomo Electric, all of which are incorporated by reference herein as though fully set forth. For example, Rowcliffe et al. (Oxide Dispersion Strengthening, Ansell et al., ed., Gordon and Breach, NY, "Strengthening of Niobium- Zirconium Alloys by Internal Oxidation," 1968) have shown that the yield and ultimate tensile strength of Nb-1Zr alloy can double by internal oxidation. Their research was, however, aimed at improving high temperature creep resistance of the alloy and there is no teaching or suggestion of the use of such a method to produce a surface-hardened medical implant for improved wear and abrasion resistance. With orthopaedic and cardiovascular implants being implanted in younger people and remaining in the human body for longer period of time, there is a need for an implant material with requisite strength and high abrasion resistance which minimizes the production of abrasive particles from surface abrasion effects. The present invention aims to provide novel hardened metallic implants with high abrasion resistance and methods for increasing implant abrasion resistance without the use of a hard deposited overlay ceramic-like coating. In one embodiment of the invention the internal oxidation or nitridation of a metal implant is used to harden the implant's surface. While a minimal external surface oxide or nitride scale may form on these hardened implants, surface strengthening is primarily due to dispersion strengthening by internal oxidation or nitridization just below the implant's surface. Thus, there is no significant hard external scale formed which may spall off or produce abrasion products to damage the implant surface or cause undesirable biological effects. Thus according to the invention we provide a surface hardened metal medical implant having an implant body, said implant body comprising a metal selected from the group consisting of Ti-6Al-4V, Ti-Mo, Ti-Al-Nb, Ti-Fe, Ti-V, Zr, Zr-Nb, Ti-Nb, Ti-Nb-Zr, Co-Cr-Mo and Fe-Cr-Ni-Mo, and less than 2% w/w of a more readily oxidisable or nitridable metal solute selected from the group consisting of tantalum, yttrium, hafnium, thorium, zirconium, chromium, niobium, aluminium and silicon alloyed with said metal metal; wherein a substantial proportion of the more oxidisable or nitridable solute at the surface of the implant body is oxidised or nitrided to strengthen and harden the surface of the implant to a hardness greater than about 40 Rockwell C for increased resistance to wear and abrasion in vivo . In another embodiment, the invention also provides for the additional hardening of the implant surface with interstitial diffusion of oxygen, nitrogen, or carbon. This latter method is used on implants which have previously been treated with an internal oxidation or nitridization treatment. A lower diffusion hardening temperature can be utilized which will not affect the previously internally oxidized or nitrided benefits. The invention oxidizing or nitriding method of surface hardening implant metals provides a fine oxide or nitride dispersion within the metal surface without a significant surface scale so that the implant essentially retains its metallic appearance. Standard nitriding, oxidizing, and carbonizing treatments for metals are available and known to persons skilled in the art. These methods use plasma, fluidized beds, molten salts, or nitrogen, oxygen, or carbon-containing gaseous environments at elevated temperatures to perform surface treatments. In these methods, diffusion of nitrogen, carbon, and oxygen into the metallic implant and the subsurface nucleation of nitrides, carbides, or oxides increases hardness and strengthens the metal to depths of 50 microns or more depending on gas concentration, time, temperature, and alloy composition. However, the formation of nitrides or carbides in chromium-containing metals occurs via formation with the chromium. Thus, local depletion of chromium can occur in the matrix adjacent to the nitride or carbide particle and reduce corrosion resistance. Oxygen diffusion hardening of titanium alloys promotes an undesirabe, weaker alpha case on the surface. Internal oxidation or nitridization avoids introducing these limitations of corrosion resistance and loss of strength. While surface hardening by conventional oxygen, nitrogen, or carbon diffusion forms no significant external nitride or carbide scale, if done at sufficiently low partial pressures of these diffusing species, the metallic implant's surface hardness can exceed 50 Rockwell C in the case of certain titanium alloys, significantly higher than for the untreated alloy, which can vary up to about 40 Rockwell C depending on the metal and the heat-treated condition of the metal. Further, conventional diffusion hardening surface treatments can significantly improve surface abrasion and fretting resistance for titanium alloys and stainless steels. Surface hardening by diffusion may be more effective with some metals than others, depending on the rate of diffusion in the particular metal, and the stability of the microstructure at the diffusion hardening temperature. Further, diffusing species such as nitrogen or carbon may react with chromium in cobalt alloys or stainless steel, rendering them less corrosion resistant. The internal oxidation or nitridization process is applicable to almost any metallic implant. To produce the invention hardened implant, a low concentration of a more readily oxidizable or nitridable metal solute is added to the metallic implant's alloy composition, so that the internal oxidation or nitridization process strengthens and hardens the surface via reaction of this specific solute with diffusing oxygen or nitrogen. This is in contrast to conventional diffusion hardening methods described above. Selection of a suitable metal solute for internal oxidation or nitridization is based upon the thermodynamics of the process. Specifically, the more negative the value is for the free energy of formation (ie. ΔG°) for a particular metal oxide (eg. Ta 2 O 5 ), the greater the tendency (ie. thermodynamic driving force) to form the oxide at a given temperature within the metal or alloy. For internal oxidation surface hardening and strengthening, the depth of the internally oxidized zone, the oxide particle size, and the strength of the alloy depend on the oxidizable solute's concentration, the concentration of oxygen in the oxidizing environment, the oxidation temperature, and the oxidation time. Because the strength of the surface is increased, the implant's fatigue strength in tension bending will also increase, as well as its surface hardness and subsequent abrasion resistance. While the invention surface hardened implants possess a relatively high strength, the usefulness of these hardening processes is not limited to treating implants in load-bearing applications. Because of its abrasion resistance, enhanced fatigue strength, and tension bending strength, the hardened implants can be used in many types of implants including, but not limited to, hip joints, knee joints, compression hip screws, tooth implants, skull plates, fracture plates, intramedullary rods, staples, bone screws and other implants. According to the invention we provide a surface hardened metal medical implant as hereinbefore described comprising less than about 2% w/w, eg. 1 - 3% w/w, such as 2% w/w of a more readily oxidisable metal solute selected from the group consisting of tantalum, yttrium, hafnium, thorium, zirconium, chromium, niobium and aluminium and alloyed thereto. We further provide a surface hardened metal medical implant as hereinbefore described comprising less than about 2% w/w, eg. 1 - 3% w/w, such as 2% w/w of a more nitridable metal solute selected from the group consisting of silicon, thorium, zirconium, tantalum and aluminium and alloyed thereto. The invention provides surface hardened, abrasion resistant medical implants. The hardening methods may be applied to all currently used implant metals include AISI 316L stainless steel (ie. Fe-Cr-Ni-Mo), Co-Cr-Mo (F75 or F799) and Ti-6A1-4V, and those alloys that may be contemplated as useful. While the methods for producing the invention abrasion resistant metallic implants may be applied to almost any metal or alloy used to fabricate implants, the Co-Cr-Mo and titanium alloys are preferred in the present invention. Consequently, much of the description will discuss titanium alloy implants, it being understood that other alloys may also be similarly processed by the invention methods to produce the invention surface hardened implants. Examples of preferred titanium alloys include Ti-6Al-4V, beta titanium alloys, Ti-Mo, Ti-Al-Nb, TiV and Ti-Fe. Newer, more biocompatible titanium alloy compositions with lower elastic moduli such as Ti-Zr, Ti-Nb-Zr and Ti-Nb, are also capable of internal oxidation, as are zirconium and niobium based alloys. Examples of such compositions may be found in US Patent No.5169597. Other metals and metal alloys that may be employed include, but are not limited to, zirconium and zirconium alloys such as Zr-Nb, for example, and stainless steels, such as, for example, stainless steel 316L (Fe-Cr-Ni-Mo). Preferred alloys include those containing titanium and niobium and the oxidisable metal solute is selected from the group consisting of tantalum, yttrium, zirconium, hafnium, chrominum and aluminium; those containing titanium, niobium and zirconium and the oxidisable metal solute is selected from the group consisting of hafnium, chrominum, tantalum, yttrium and aluminium; those containing titanium, aluminium and vanadium and oxidisable metal solute is tantalum and those containing Co-Cr-Mo and the oxidisable metal solute is selected from the group consisting of tantalum, aluminium and yttrium. The most preferred biocompatible, low-modulus titanium alloy implants may be produced by combining, as commercially pure components, titanium, niobium, and zirconium in the appropriate proportions. The titanium alloys (depending on the alloying constituents) may further contain concentrations of another metal (typically less that 2% w/w), such as tantalum, yttrium, thorium, chromium, aluminium, and the like, for purposes of internal oxidation. Ti-Nb alloys may contain zirconium, aluminium, yttrium, hafnium, or tantalum in concentrations less than about 2% w/w for the same purpose. Zirconium or zirconium alloys may contain less than about 2% w/w tantalum, yttrium, thorium, or aluminium for this purpose. Cobalt alloys and stainless steels may contain less then about 2% w/w tantalum, aluminium, and yttrium for this purpose. One preferred alloy contains titanium as the major component comprising 73 - 75% eg. 74% w/w of the alloy in combination with 12 - 14% eg. 13% w/w of w/w zirconium and 13% w/w niobium. Less than 1 - 3% eg. 2% of another metal such as tantalum or aluminium is added to replace the same amount of titanium, or zirconium, or to a lesser degree, niobium (since niobium concentration is important to establish a low modulus). The other group of preferred alloys also contains titanium as the major component, comprising about 84 to 87% w/w of the metal, in combination with about 13-17% w/w niobium, and less than about 1 - 3% eg. 2% w/w tantalum, yttrium, hafnium, thorium, aluminium, or chromium. The additional metal added preferably replaces the same amount of titanium or to a lesser degree niobium. The most preferred biocompatible low modulus alloys include Ti-13Nb-13Zr and 1% Ta; and, Ti-15Nb with 1% Ta. Preferred embodiments of a hardened metal medical implant as hereinbefore described comprising a nitridable metal solute include; those containing titanium and niobium and the metal solute is selected from the group consisting of silicon and thorium, especially preferred are those containing 84 -86% w/w, eg. 85% w/w titanium and 14 - 16% w/w, eg. 15% w/w niobium; those containing titanium, niobium, and zirconium and the metal solute is thorium, especially preferred are those containing 72 - 74% w/w, eg. 73% w/w titanium, 12 - 14% w/w, eg. 13% w/w niobium and 12 - 14% w/w, eg. 13% zirconium; those containing Co-Cr-Mo and the metal solute is selected from the group consisting of silicon, tantalum, thorium, zirconium, titanium and aluminium; those containing titanium, aluminium and vanadium and the metal solute is selected from the group consisting of silicon and thorium, especially those containing 89 - 91% w/w, eg. 90% w/w titanium, 5 - 7% w/w, eg. 6% aluminium and 3 - 5% w/w, eg. 4% vanadium. The methods of making and using implants of titanium, niobium (and optionally tantalum as a substitute for niobium) and optionally zirconium or zirconium alloy (and optionally tantalum, yttrium, or aluminium as a substitute for zirconium) are described US Patent No.5169597. The machining, casting or forging of the alloys into the desired implant shape may be carried out by any of conventional methods used for titanium or zirconium alloys. Implants fabricated from the titanium alloys may be supplied with a sintered porous bead or wire or plasma-sprayed coating of titanium alloy of the same or different composition, or even pure titanium, to allow stabilization of the implant in the skeletal structure of the patient after implantation by bone ingrowth into the porous structure. Similarly, zirconium or zirconium alloys may be supplied with the similar porous coatings of zirconium or zirconium alloy. Such porous structures are occasionally attached to the implant surface by sintering. Similarly, cobalt alloys may be supplied with a porous metal coating. Because sintering of porous coating is preferred at temperatures above 1000°C, the mechanical properties of titanium alloys can change significantly due to substantial grain growth, phase changes, and other metallurgical factors arising from the sintering process. Thus, for example, after sintering to attach the porous coating, additional heat treatments are desired to restore mechanical properties. To avoid these potential restrictions, the implant metal or alloy may be porous coated using plasma spray methods in which minimal heating occurs to the base material. While the preferred titanium alloys themselves provide a non-toxic material suitable for orthopedic, cardiovascular, or other medical implants, it is desirable, for other reasons, such as micro-fretting against bone or polyethylene bearing surfaces, or microfretting, to harden the surface of an implant fabricated from these alloys, such as the stainless steels or cobalt alloys, surface hardening may be desirable for both increasing fatigue strength and the reduction of micro-fretting or abrasive wear. The invention provides methods to strengthen and harden an alloy's surface and includes (1) an internal oxidation process which includes adding a low concentration of a more readily oxidizable solute such as yttrium, niobium, tantalum, zirconium, thorium, hafnium, chromium, or aluminium to the alloy, and oxidizing a portion of the solute that is found immediately beneath the metal surface; (2) an internal nitridization process which includes adding low levels of a relatively more nitridable solute such as zirconium, silicon or thorium to the alloy and nitriding a portion of this solute that is found just below the metal surface; and (3) an additional interstitial diffusion strengthening process using nitrogen, oxygen, or carbon. For the internal oxidation and nitridization processes, the particular oxidizable or nitridable solute selected will vary, depending upon the particular metal or metal alloy composition of the implant. Each of these three methods will be discussed in turn. In the internal oxidation process, a small quantity of a "more readily oxidizable solute" is added to the alloy from which the implant is to be fabricated. By more readily oxidizable solute, we mean one that oxidizes more readily than the other constituent metals of the alloy with which the solute is admixed or alloyed. During controlled oxidation, oxygen diffuses into the implant's surface leading to the formation of a fine dispersion of solute oxide particles on and immediately below the alloy surface. The depth of this internally oxidized zone, the oxide particle size, and hardening and substrate strengthening of the surface depends on the solute concentration, the concentration of oxygen in the oxidizing environment, the oxidation temperature, and the oxidation time. Because both the hardness and strength at the surface is increased, the fatigue strength will also increase. In the case of titanium or Ti-Nb alloys, tantalum may be added as a solute, because tantalum is more reactive with oxygen (lower free energy of formation) than either titanium or niobium. Thus, it is possible to internally oxidize the alloy without oxidizing niobium or titanium if the concentration of oxygen (partial pressure of oxygen) is less than that required to form niobium or titanium oxides. Similarly, for Ti-Nb-Zr or Zr-Nb alloys with tantalum added as a solute, the concentration of oxygen is less than that required to form titanium, niobium, or zirconium oxides. Additionally, when tantalum is added as a solute, to Co-Cr-Mo alloys, then the more oxidizable tantalum causes internal oxidation of the alloy. Table l is a list of published standard free energies of formulation (ΔG°) for various titanium, niobium, zirconium, tantalum, aluminium, yttrium, and other oxides. The more negative the ΔG° value, the greater the tendency (ie. thermodynamic driving force) to form the oxide at a given temperature, T(°K). Thus, those skilled in the art can appreciate that the low-modulus titanium-niobium and titanium-niobium-zirconium alloys described in US Patent No. 5169597 and other titanium, cobalt, and zirconium alloys described above can be internally oxidized by the presence of small quantities of relatively more oxidizable solutes such as yttrium, chromium, aluminium, hafnium, and tantalum. Tantalum and aluminium can be used for internally oxidizing Ti-Nb-Zr alloys as their ΔG° is more negative than even that of zirconium or niobium. However, based on biological factors, aluminium is not preferred over tantalum. These biological factors are partially mitigated because the aluminium near the surface of the implant converts to inert aluminium oxide so that the presence of aluminium will not be as potentially detrimental as if aluminium metal were present in the bulk alloy. The alloys that may be internally oxidized via the presence in the alloy of small amounts (in parentheses) of zirconium, tantalum, or aluminium include, but are not limited to, Ti-Nb-Zr-(Ta), Ti-Nb-(Zr), Ti-Nb-(Ta), and Ti-Nb-(Cr), Ti-A1-V-(Ta), Co-Cr-Mo-(Ta), and 316L stainless steel (Ta). Other combinations are also possible based on relative differences in ΔG° between the preferred solute and other alloy constituents. In the internal oxidation process, the depth of internal oxidation (flat plate surface) from the surface (X) for a given period of time (t) is represented by the following equation. X=[2N 0 (s) D 0 t/vN b (0) ] 1/2 where: No (s) is the concentration of oxygen at the surface (less than that required to oxidize either the titanium or niobium base alloy, for example if tantalum is added as the solute); D o is the rate of diffusion of oxygen into the surface; v is the stoichiometric value (ratio) of oxidizing solute species to oxygen (ie. v=2 for ZrO 2 ); and N b (0) is the concentration of the solute which is being internally oxidized (ie. chromium, aluminium, yttrium, or tantalum, and the like). For internal oxidation, the depth increases with decreasing concentration of solute. The value N o (s) is related, by a reaction rate constant, to the square root of the partial pressure of oxygen. To optimize the strengthening effect of the internal oxidation process, the advancing front of diffusing oxygen should progress rapidly. This results in more nucleation and less growth of internal oxide particles, and therefore smaller, more effective particles. Relatively lower oxidation temperatures are also preferred to minimize particle growth, but presents a trade-off with the rate of oxygen diffusion. Thus, the partial pressure of oxygen and the solute concentration should be maximised (preferably less than about 2% w/w). Various times and temperatures are possible and can be optimized experimentally. To internally oxidize a particular alloy implant containing a more readily oxidizable added solute such as tantalum, yttrium, aluminium, or zirconium, the alloy implant is packed in a mixture of a metal and its oxide whereby the metal selected for the packing mixture is the next most readily oxidizable solute compared to the added metal solute (eg. tantalum and zirconium). Oxygen is evacuated from the implant's environment and residual oxygen is scavenged by, for example, resistance heating a zirconium or tantalum wire in the evacuated environment. [This is called "getting" the oxygen to a sufficiently initial low level]. Upon heating the alloy implant, the metal oxide in the packing and the metal in the packing attain an equilibrium which produces the required low level of oxygen concnetration (partial pressure) in the system, sufficient to react primarily with the low concentration of more readily oxidizable metal solute present in the implant and to thereby internally oxidize the metal implant's surface. For example, to internally oxidize a Ti-6Al-4V implant with a tantalum solute, the implant is evacuated in a packed mixture of aluminium and aluminium oxide, since aluminium is the most readily oxidizable metal next to tantalum. Any remaining oxygen in the evacuated system is reduced by resistance heating a zirconium or tantalum wire in the evacuated environment. Upon heating to about 500°C-1200°C for up to about 100 hours (depending upon the desired depth and hardening), the aluminium metal and aluminium oxide establish an oxygen partial pressure (or No (s) sufficient to produce oxidation of the tantalum solute by diffusion of oxygen into the alloy surface, but without causing the titanium, aluminium, or vanadium in the alloy to form a significant external oxide scale. For this case, it is more desirable to establish the partial pressure of oxygen close to 10 -6 torr because levels near 10 -5 torr tend to produce aluminium monoxide (Al0) near the surface. At oxygen pressures less than 10 -6 torr, the strengthening effect is less pronounced (ie. more growth vs. nucleation of the internal oxide particles) due to lower levels of oxygen and slower penetration (diffusion) rates of oxygen into the surface. Oxidation depth should preferably be less than about 150 angstroms), processing time, and temperature, and to optimize hardness and strength. The preferred internal surface strengthened metallic implants having excellent biocompatibility include those produced by the internal oxidation of shaped Ti-Nb alloys using small concentrations of zirconium, yttrium, or tantalum (ie. Ti-Nb-Zr, Ti-Nb-Y, or Ti-Nb-Ta), or internal oxidation of Ti-Nb-Zr implants or zirconium or zirconium implants using small concentrations (less than about 2% w/w) of tantalum (ie. Ti-Nb-Zr-Ta or Zr-Ta) or yttrium. Additionally, aluminium solute levels less than about 2% w/w would be effective for internally oxidizing these implants. As an alternative to internal oxidation, internal nitridization can be performed by adding low levels (less than about 2% w/w) of a solute more nitridable than the base alloy constituents. By a "more nitridable solute", we mean one that nitrides more readily than the other constituent metals of the alloy with which it is admixed or alloyed. In the case of the titanium alloys, solutes such as zirconium, silicon, or thorium may be added. The titanium alloys (with solutes for internal nitridization in parentheses) suitable for internal nitridization via the presence of small amounts (ie. less than 2% w/w) of silicon, thorium, or zirconium include, but are not limited to, Ti-Nb-(Si), Ti-Nb-(Th), and Ti-Nb-(Zr). Zirconium alloys should contain less that about 2% w/w of silicon or thorium, and cobalt alloys and 316L stainless steel should contain less than about 2% w/w of thorium, tantalum, aluminium, silicon or zirconium. It should be noted that for both internal nitridation and oxidation, a substantial portion of the respective solute added that occurs at the implant's surface will undergo nitridization or oxidation. Solute concentrations are preferably less than about 2% w/w. While more solute may be added, surface hardening will not be as effective therefore such addition is not preferred. Another method which may be used to improve the surface abrasion resistance of metallic implants, especially the preferred titanium implants such as Ti-Nb-Zr, Ti-Nb, Ti-Nb-Zr-Ta, Ti-Nb-Ta and zirconium and zirconium alloys, is "interstitial diffusion" strengthening of the surface with oxygen, nitrogen, or carbon. Treatments for interstitial diffusion strengthening of metals generally use gaseous or liquid nitrogen or carbon-containing environments or gaseous environments, including fluidized beds, or similar oxygen-containing environments, at elevated temperatures, and are known to those skilled in the art. Diffusion strengthening to depths of less than 100 microns are usually sufficient. In the interstitial diffusion strengthening process, oxygen, nitrogen, and carbon concentrations are kept sufficiently low so that there is no significant formation of an external oxide nitride or carbide scale so that an essentially metallic-type appearance remains on the surface. The surface hardness of a typical 33 Rockwell C hardness titanium alloy when so treated can exceed 60 Rockwell C hardness and can also significantly improve surface abrasion and fretting resistance. While the general interstitial diffusion hardening process using oxygen, nitrogen, and carbon is used commercially and is well known to those of skill in the art, its application to Ti-Nb, Ti-Nb-Zr, zirconium, Ti-6Al-4V, Co-Cr-Mo, and other medical implant metals capable of internal oxidation or internal nitridization is novel. This diffusion hardening process can be applied to the preferred titanium alloy, zirconium alloy, cobalt alloy, and stainless steel compositions, whether or not these alloy compositions have received a previous internal oxidation or internal nitridization treatment, to achieve additional benefits. It should be noted that the internal oxidation and interstitial diffusion hardening methods can be controlled to minimize or eliminate the formation of an external scale-type coating. Therefore, the hardened implant's surface may, with little or no additional surface treatment, be coated with, for example, amorphous diamond-like carbon, pyrolytic carbon, TiN, TiC, and oxide coatings and the like, which are physical or chemical vapor deposited, for further improved abrasion resistance, if desired. The hardening treatment of any of the methods described in this specification would improve the attachment strength of these coatings. According to the invention we also provide the use of a metal selected from the group consisting of Ti-6Al-4V, Ti-Mo, Ti-A1-Nb, Ti-Fe, Ti-V, Zr, Zr-Nb, Ti-Nb, Ti-Nb-Zr, Co-Cr-Mo and Fe-Cr-Ni-Mo; and less than 2% w/w of a more readily oxidisable or nitridable metal solute selected from the group consisting of tantalum, yttrium, hafnium, thorium, zirconium, chromium, niobium, aluminium and silicon alloyed with said metal; wherein a substantial proportion of the more oxidisable or nitridable solute at the surface of the implant body is oxidised or nitrided to strengthen and harden the surface of the implant to a hardness greater than about 40 Rockwell C for increased resistance to wear and abrasion in vivo in the manufacture of a surface hardened metal medical implant body. Figure 1 is a surface hardness vs. depth curve (from the surface) for a Co-Cr-Mo alloy coupon alloyed with 1% w/w tantalum which has been surface hardened by internal oxidation at a temperature of 500°C for 20 hours. Figure 2 is a surface hardness vs. depth curve for a Ti-13Nb-13Zr alloy coupon alloyed with 1% w/w tantalum which has been surface hardened by internal oxidation at a temperature of 700°C for 20 hours. Figure 3 is a surface hardness vs. depth curve for a Ti-6Al-4V alloy coupon alloyed with 1% w/w tantalum which has been surface hardened by internal oxidation at a temperature of 800°C for 20 hours. The following examples are intended to illustrate the invention as described above and claimed hereafter and are not intended to limit the scope of the invention in any way. Example 1 A coupon formed of Co-Cr-Mo alloyed with about 1% w/w of tantalum was placed in a tube and packed with chromium and chromium oxide. The tube was evacuated to remove essentially all oxygen and sealed. The tube was then placed in a furnace and heated to a temperature in the range 500 to 800°C for a certain time period as indicated in table 2 below. The tube was then allowed to cool to room temperature. This procedure was also applied to a Ti-13Nb-13Zr alloy (packed with zirconium and ZrO 2 ) and a Ti-6Al-4V alloy (packed with aluminium and Al 2 O 3 ), each containing about 1% w/w tantalum, both of which were heated to the temperatures and for the time periods indicated in table 2 below. The bulk hardness, surface hardness, and hardness gradient depths for each of the three alloys after internal oxidation at the indicated conditions are shown in table 2. Material Internal Oxidation Parameters Bulk Hardness (Knoop) Surface Hardness (Knoop) Hardness Gradient Depth (Micron) Temp (C°) Time (Hrs.) Co-Cr-Mo (F-75) w/1 wt. % Ta 500 1 300 350 50 500 6 340 550 150 500° 20 340 550 150 600 1 310 650 200 600 6 300 500 250 600 20 310 650 300 700 1 300 600 200 700 20 340 600 250 800 1 280 450 100 800 6 350 500 200 Ti-13Nb-13Zr w/1 wt. % Ta 700° 20 225 400 150 700 100 225 425 200 800 1 215 300 250 800 6 240 350 >300 Ti-6Al-4V w/1 wt. % Ta 800 1 275 375 100 800° 20 280 375 150 Figures 1 - 3 represent the surface hardness vs. depth curves for the alloy materials marked with asterisks as shown in Table 2. Specifically, Figure 1 is the surface hardness vs. depth curve for a Co-Cr-Mo alloy containing 1% w/w Ta which has been heated to 700°C for 20 hours. Figure 2 represents the surface hardness vs. depth curve for a Ti-13Nb-13Zr alloy containing 1% w/w Ta which has been heated to 700°C for 20 hours. Figure 3 represents the surface hardness vs. depth curve for a Ti-6Al-4V alloy containing 1% w/w Ta which has been heated to 800°C for 20 hours. The peak hardness values given in Table 2 are not necessarily as great as that produced by the curves shown in Figures 1-3. Extrapolation of these curves suggest a still higher hardness at the immediate surface. While it is clear that a chemical element of the Periodic Table that is a metal is a pure metal, alloys of metallic elements are also referred to as "metals", in the sense that they are metallic rather than ceramic organic, etc. Therefore, in the specification and claims when reference is made to a "metal implant", this includes an implant fabricated from a metal alloy as opposed to a ceramic or polymer or composite. Further, in the specification and claims when an alloy is combined with a metal solute, it forms a "solute-containing alloy". Thus, when an alloy of a given composition, commercially available or specially made, is specified, its composition does not include the metal solute, unless so specified. Therefore, in the claims the metal implant's composition is specified in terms of (1) a metal composition and (b) the metal solute subsequently added to then make the solute-containing alloy from which the implant body is fabricated. The invention has been described with reference to its preferred embodiments. After studying this disclosure, a person of skill in the art may appreciate changes and modifications that are within the spirit of the invention as disclosed above and within the scope of the claims herebelow.

Claims: A surface hardened metal medical implant having an implant body, said implant body comprising: a metal selected from the group consisting of Ti-6Al-4V, Ti-Mo, Ti-Al-Nb, Ti-Fe, Ti-V, Zr, Zr-Nb, Ti-Nb, Ti-Nb-Zr, Co-Cr-Mo and Fe-Cr-Ni-Mo; and less than 2% w/w of a more readily oxidisable or nitridable metal solute selected from the group consisting of tantalum, yttrium, hafnium, thorium, zirconium, chromium, niobium, aluminium and silicon alloyed with said metal; wherein a substantial proportion of the more oxidisable or nitridable solute at the surface of the implant body is oxidised or nitrided to strengthen and harden the surface of the implant to a hardness greater than 40 Rockwell C for increased resistance to wear and abrasion in vivo . A surface hardened metal medical implant according to claim 1 in which the metal solute is a more readily oxidizable metal solute selected from the group consisting of tantalum, yttrium, hafnium, thorium, zirconium, chromium, niobium and aluminium alloyed with said metal. A surface hardened metal medical implant according to claim 1 in which the metal solute is a more readily nitridable metal solute selected from the group consisting of silicon, thorium, zirconium, tantalum, and aluminium alloyed with said metal. A surface hardened metal medical implant according to claim 1, wherein the implant body has further been interstitially hardened by diffusion of an element selected from the group consisting of nitrogen, oxygen, and carbon into and below the surface of said implant body. A surface hardened metal medical implant according to claim 2 wherein said implant body comprises a metal having a composition comprising titanium and niobium, and the metal solute is selected from the group consisting of tantalum, yttrium, zirconium, hafnium, chromium, and aluminium. A surface hardened metal medical implant according to claim 2 wherein said implant body comprises a metal having a composition comprising titanium, niobium, and zirconium, and the metal solute is selected from the group consisting of hafnium, chromium, tantalum, yttrium and aluminium. A surface hardened metal medical implant according to claim 2 within said implant body comprises a metal of composition comprising titanium, aluminium and vanadium, and the metal solute is tantalum. A surface hardened metal medical implant according to claim 2 wherein said implant body comprises Co-Cr-Mo and the metal solute is selected from the group consisting of tantalum, aluminium, and yttrium. A surface hardened metal medical implant according to claim 3 wherein said implant body comprises a metal of composition comprising titanium and niobium, and the metal solute is selected from the group consisting of silicon and thorium. A surface hardened metal medical implant according to claim 3 wherein said implant body comprises a metal of composition comprising titanium, niobium and zirconium, and the metal solute is thorium. A surface hardened metal medical implant according to claim 3 wherein said implant body comprises Co-Cr-Mo and the metal solute is selected from the group consisting of silicon, tantalum, thorium, zirconium, titanium, and aluminium. A surface hardened metal medical implant of claim 3 wherein said implant body comprises titanium, aluminium, and vanadium, and the metal solute is selected from the group consisting of silicon and thorium. A surface hardened metal medical implant having an implant body, said body comprising Co-Cr-Mo and 1% w/w tantalum as a more readily oxidizable metal solute wherein a substantial proportion of the metal solute at the surface of said implant is oxidized to a depth of less than 200 microns to strengthen and harden the surface of said implant to a hardness of at least 40 Rockwell C. A surface hardened metal medical implant comprising a 90% w/w titanium; 6% w/w aluminum, 4% w/w vanadium, and 1% w/w tantalum as a more readily oxidizable solute wherein a substantial proportion of the tantalum at the surface of said implant is internally oxidized to a depth of less than 200 microns to strengthen and harden the surface of said implant to a hardness of at least 40 Rockwell C. A method of preparation of a surface hardened metal medical implant according to claim 1, which comprises: (1) an internal oxidation process which includes adding a low concentration of a more readily oxidizable solute such as yttrium, niobium, tantalum, zirconium, thorium, hafnium, chromium, or aluminium to the alloy, and oxidizing a portion of the solute that is found immediately beneath the metal suface; or (2) an internal nitridization process which includes adding low levels of a relatively more nitridable solute such as zirconium, silicon or thorium to the alloy and nitriding a portion of this solute that is found just below the metal surface; (3) and optionally an additional interstitial diffusion strengthening process using nitrogen, oxygen, or carbon. The use of a metal selected from the group consisting of Ti-6Al-4V, Ti-Mo, Ti-Al-Nb, Ti-Fe, Ti-V, Zr, Zr-Nb, Ti-Nb, Ti-Nb-Zr, Co-Cr-Mo and Fe-Cr-Ni-Mo; and less than 2% w/w of a more readily oxidisable or nitridable metal solute selected from the group consisting of tantalum, yttrium, hafnium, thorium, zirconium, chromium, niobium, aluminium and silicon alloyed with said metal; wherein a substantial proportion of the more oxidisable or nitridable solute at the surface of the implant body is oxidised or nitrided to strengthen and harden the surface of the implant to a hardness greater than 40 Rockwell C for increased resistance to wear and abrasion in vivo in the manufacture of a surface hardened metal medical implant body.

Inventors: DAVIDSON JAMES A, DAVIDSON, JAMES A.
Applicants: SMITH & NEPHEW INC, SMITH & NEPHEW, INC.
Application year: 1993
Main classification: A61L27
IPC codes: A61F2, A61L27