An olefinic thermoplastic elastomer composition

Abstract: An olefinic thermoplastic elastomer composition having an improved property to prevent blooming comprises an olefinic thermoplastic elastomer containing additives and one or more compounds selected from the group consisting of esters of polyhydric alcohols, alkylalkanolamines, alkylalkanolamides, fatty acid amides, higher alcohols, aliphatic amines, fatty acids and adducts of alkylene oxides to these compounds which are compounded into the olefinic thermoplastic elastomer. The olefinic thermoplastic elastomer composition can maintain beautiful appearance of the molded products made from the composition because the additives in the composition do not bloom on the surface of the molded products unlike conventional products. The composition can be advantageously used as interior materials of automobiles and materials for electronic instruments.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention The present invention relates to a novel olefinic thermoplastic elastomer composition. More particularly, it relates to an olefinic thermoplastic elastomer composition having excellent property to prevent blooming of various kinds of additives on the surface of molded products and useful in the fields of automobiles and light electrical appliances. 2. Description of the prior art Prior art documents US-4,925,898, US-A-3,988,227, JP-A-62072740 and JP-A- 56010536 address the problem of the inhibition of blooming in standard elastomer compositions, without considering the problem of blooming in olefinic thermoplastic elastomers. Olefinic thermoplastic elastomers are composite materials made by blending of rubbers comprising the hard segment of a polyolefinic plastic, such as polyethylene, polypropylene and the like, and the soft segment of an ethylenic elastomer, such as EPDM and EPM, as the main components or by partial crosslinking of these rubbers in the process of the blending. The olefinic thermoplastic elastomers have been urged to bring them to practical applications as the material to replace polyvinyl chloride resins because they have advantages of no environmental problems, lower specific gravity and better property for recycling. Particularly when the olefinic thermoplastic elastomers are used as interior materials of automobiles, processes after the T-die extrusion and the calendering can be made much simpler than the processes using polyvinyl chloride resins. Olefinic thermoplastic elastomers are very often adopted as the materials of instrument panels, doors and ceilings because of this reason. In the olefinic thermoplastic elastomers, relatively large amounts of various additives, such as a process stabilizer, a lubricant, an antioxidant, a light stabilizer, a light absorbent and the like, are compounded for the purpose of enhancing workability and durability of the molded products. Because large amounts of additives are compounded into the olefinic thermoplastic elastomers, the additives frequently bloom out with passage of time after films and sheets prepared from the olefinic thermoplastic elastomers and formed into final products. In the olefinic thermoplastic elastomers, additives are compounded in considerably larger amounts than in conventional polypropylene resins and the like for improvement of workability and properties in applications. A large amount of an amorphous component, such as EPM and EPDM, and a mineral oil plasticizer are also compounded in the elastomer in addition to polypropylene. The phenomenon of blooming is caused by these reasons. The blooming of the additives leads to undesirable phenomena, such as unsightly appearance of the products, inferior printing in a later process, poor adhesion and the like, and troubles occur in the subsequent processing from these phenomena. SUMMARY OF THE INVENTION The present invention accordingly has an object to provide an olefinic thermoplastic elastomer composition having the improved property to prevent blooming even when various additives are compounded in it. Extensive investigations undertaken by the present inventors with the object described above led to a discovery that an olefinic thermoplastic elastomer composition comprising esters of polyhydric alcohols compounded in it has the excellent property of preventing blooming after the elastomer is formed into molded products. The present invention has been completed on the basis of the discovery. Thus, the present invention provides an olefinic thermoplastic elastomer composition having an improved property to prevent blooming comprising an olefinic thermoplastic elastomer containing additives and one or more compounds selected from the group consisting of esters of polyhydric alcohols; which are compounded into the olefinic thermoplastic elastomer. Other and further objects, features and advantages of the invention will appear more fully from the following description. DETAILED DESCRIPTION OF THE INVENTION Examples of the olefinic thermoplastic elastomer comprised in the composition of the invention are graft copolymers of polyethylene and butyl rubber, ethylene-propylene copolymer rubbers, ethylene-propylene-polyene copolymer rubbers, thermoplastic resin compositions obtained by dynamic heat treatment of blends of polyolefin resins and ethylene-α-olefin copolymer rubbers (for example, Japanese Patent Publication 1978-34210 and Laid Open Japanese Patent Applications 1978-149240 and 1978-149241), thermoplastic compositions obtained by blending polyolefin resins to thermoplastic resin compositions obtained by dynamic heat treatment of blends of polyolefin resins and ethylene-a-olefin copolymer rubbers (for example, Laid Open Japanese Patent Applications 1978-145857 and 1979-16554) and thermoplastic compositions obtained by dynamic heat treatment of blends of polyolefin resins which are not crosslinked with peroxides and ethylene-α-olefin copolymer rubbers (for example, Laid Open Japanese Patent Application 1980-71739). The olefinic thermoplastic elastomer contains additives which often cause blooming, such as antioxidants like phenol antioxidants, process stabilizers, lubricants, light stabilizers and the like. The olefinic thermoplastic elastomer occasionally contains linear low density polyethylene (LLDPE), low density polyethylene, high density polyethylene, polypropylene and the like for the purpose of improving surface hardness, tensile strength and texture. Other examples of the additives contained in the olefinic thermoplastic elastomer are conventional pigments, flame retardants, inorganic fillers like talc, clay and calcium carbonate and the like. Examples of the ester of polyhydric alcohol which is compounded into the olefinic thermoplastic elastomer are glycol esters, such as polyethylene glycol monoesters, polyethylene glycol diesters and the like, glycerine esters, such as monoglycerides, diglycerides and triglycerides, sorbitol esters, adducts of alkylene oxides to these compounds and the like other compounds. The aforementioned compounds selected from the group consisting of esters of polyhydric alcohols, which are compounded into the olefinic thermoplastic elastomer are sometimes referred as "the blooming preventing agents" in the following descriptions. The amount of the blooming preventing agent in the composition of the invention is in the range from 0.05 to 5 weight parts per 100 weight parts of the total of the olefinic thermoplastic elastomer in which various kinds of additives including solid additives have already been compounded. When the blooming preventing agent is compounded to the olefinic thermoplastic elastomer in an amount of more than 5 weight parts, further enhancement of the effect to prevent the blooming cannot be expected while cost of the composition is increased. Thus, an amount more than the specified range is not favorable. The olefinic thermoplastic elastomer composition of the invention can be obtained by adding the compounding components of specified amounts and then by kneading them in a kneader, such as a Banbury mixer, a co-kneader, an extruder, a biaxial kneader and the like. For production of molded products from the composition obtained above, a method, such as extrusion molding, injection molding, blow molding, calendering and the like, can be adopted. To summarize the advantages obtained by the invention, the olefinic thermoplastic elastomer composition of the invention can maintain beautiful appearance of the molded products made from the composition because the additives in the composition do not bloom on the surface of the molded products unlike conventional products. Therefore, the olefinic thermoplastic elastomer composition of the invention can be advantageously used as interior materials of automobiles and materials for electronic instruments. The invention will be understood more readily with reference to the following examples; however, these examples are intended to illustrate the invention and are not to be construed to limit the scope of the invention. Examples 1 to 3 and Comparative Examples 1 to 9 An olefinic thermoplastic elastomer and a blooming preventing agent shown in Table 1 were mixed at first by dry blending and then mixed in a biaxial kneader at 180 to 230°C to obtain an olefinic thermoplastic elastomer composition. For evaluation of physical properties of the composition thus obtained, the composition was sheet molded by a 65 m/m bent type T-die extruder to obtain a molded product of 600 mm width and 0.6 mm thickness. For the purpose of easier observation of blooming phenomenon, a carbon black master batch containing 50 weight parts of carbon black per 100 weight parts of low density polyethylene was added to the composition when the composition is molded to the form of sheet. Sample pieces of 200 mm x 200 mm were cut out from the sheet molded in the above and were treated by one of the following two methods: it was left standing for 2 months at the room temperature; or it was treated in a gear oven for 100 hours at 50°C. After the treatment, the surface of the sample sheet was visually observed and the condition of the surface was evaluated according to the following criteria: ○: no change from the original surface was observed. Δ: blooming was very slightly observed. ×: blooming was clearly observed. The results are shown in Table 1. Comparative Examples 10 to 13 Olefinic thermoplastic elastomer compositions were prepared and evaluated by the same method as in Example 1 to 5 by using the components listed in Table 2. The results are shown in Table 2. olefinic thermoplastic elastomer A additive blooming preventing agent condition of the surface (wt. part) kind wt. part kind wt. pt. 2 mon. r.t. gear oven 50°C×100 hr. Comparative Example 10 100 E 0.3 0.5 ○ ○ Comparative Example 11 100 E 0.3 0.5 ○ ○ Comparative Example 12 100 F 0.3 0.5 ○ ○ Comparative Example 13 100 F 0.3 0.5 Δ ○

Claims: An olefinic thermoplastic elastomer composition having an improved property to prevent blooming comprising an olefinic thermoplastic elastomer containing additives and one or more compounds (blooming preventing agents) selected from the group consisting of esters of polyhydric alcohols, which are compounded into the olefinic thermoplastic elastomer. An olefinic thermoplastic elastomer composition having an improved property to prevent blooming as claimed in Claim 1 wherein the amount of the blooming preventing agents is in the range from 0.05 to 5 weight parts per 100 weight parts of the total of the olefinic thermoplastic elastomer containing additives.

Inventors: ITOU JUN-ICHI, NODA MITSUO, SAITO NOBUO, SHIGEMORI YOSHIHIRO, ITOU, JUN-ICHI, NODA, MITSUO, SAITO, NOBUO, SHIGEMORI, YOSHIHIRO
Applicants: DAINICHISEIKA COLOR CHEM, DAINICHISEIKA COLOR& CHEMICALS MFG. CO. LTD.
Application year: 1993
Main classification: C08K5
IPC codes: C08K5, C08L23