Composite membrane with high selectivity and flux and process for the manufacture thereof

Abstract: Composite membrane comprising a microporous polymer film having a high air permeability as support and a non-porous gas or vapour separating coating which has a thickness of not more than 15 µm and whose separation factor and flux are substantially equal to those of the coating and process for the manufacture of a composite membrane comprising a support and a gas or vapour separating coating by drawing a polymeric film to which the coating material has been applied, the viscosity of the coating being increased during drawing.

Description: The invention relates to a composite membrane comprising a microporous polymer film as support and a non-porous gas or vapour-separating coating present on that film. Such a composite membrane is disclosed in EP-A-181.772. That patent application discloses a method for the depositing of a layer consisting of a solution of polysiloxane in a suitable solvent onto a porous polysulfone film as support. The solvent is subsequently removed and the polysiloxane is crosslinked to form a solid coating. This coating is non-porous, which means that essentially no through-holes are present and no void channels extending from one surface of the coating to the opposite surface, and the composite membrane obtained is suitable as gas separation membrane. However, that process is suited only for depositing non-porous layers onto supports whose surface pores are small, in the aforementioned application preferably smaller than 0.1 µm. That is why in these membranes according to the state of the art the support exhibits a high resistance to the transfer of gas or vapour. The pores in the surface cannot be chosen any larger, however, inasmuch as the deposited solution would enter the pores and the polysiloxane would partially fill the pores. This would cause the effective thickness, as defined hereafter, of the gas separating coating to increase and the attainable gas flux, as defined hereafter, to decrease. From EP-A-174.918 it is known to solve the problem of supports with large pores requiring the application of thick coatings by applying on a porous support first a non-porous intermediate layer with good permeability to gases. A thin, selective coating is subsequently applied to this dense intermediate layer. Although the presence of a suitably chosen intermediate layer need not necessarily reduce the separation factor, as defined hereafter, of the composite membrane to any appreciable extent, it does have a negative effect on the gas permeability and the attainable gas flux of the membrane. The invention aims to provide a composite membrane in which the negative effect of the support on the permeability and the separation factor of the membrane is appreciably smaller than it is in membranes known in the art. The composite membrane according to the invention is characterised in that the support exhibits an air permeability, measured by the Gurley method, of not more than 40 sec/50 ml and that the coating thickness is not more than 15 µm and that the actual separation factor of the membrane is at least 80% of the ideal separation factor of the coating and the effective thickness of the coating is not more than 20% greater than the nominal thickness, as defined hereafter, of that layer. The air permeability is preferably not more than 20 s/50 ml, more preferably not more than 10 s/50 ml and most preferably not more than 5 s/50 ml. The definition of the separation factors will be given later. The membranes of the invention allow gas or vapour separation with a high actual separation factor and a high flux, which is understood to be the amount of gas or vapour that can pass through the membrane per unit time and per unit area at a given pressure difference across the membrane. The effect of the resistance of the support manifests itself in a decrease in the flux through the membrane. This decrease can be expressed as an equivalent increase in the thickness of the coating, i.e. the increase that brings about the same flux decrease, so that the composite membrane may be characterised by an effective thickness of the coating. This effective thickness can be calculated by dividing the flux of the membrane by the flux per unit thickness of the material of the coating. In the case of the membrane of the invention this effective thickness is not more than 20% greater than the nominal thickness of the coating, preferably not more than 15%, more preferably not more than 10% and most preferably not more than 5%. The nominal thickness of the coating is understood to be the average thickness of the coating in the membrane, measured by means of Scanning Electron Microscopy (SEM). The relatively high resistance to gas and vapour transport of the support in the composite membranes known in the art restricts the flux of the membrane as a whole to a value which is substantially lower than that of the coating. Thinner coatings by their nature exhibit a lower transport resistance than thicker ones so that the relative effect of the resistance of the support becomes more predominant with decreasing thickness of the coating. Consequently, the advantages of the membrane according to the invention manifest themselves especially in thin coatings, particularly in coatings of not more than 15 µm, more particularly of not more than 10 µm and even of not more than 5 and even of 2 µm. Furthermore, it has been found that a high resistance to gas and vapour transport usually also has a negative effect on the separation factor when a gas or vapour mixture is separated into its individual components. Surprisingly, the actual separation factor of the membrane fabricated according to the invention is virtually equal to the ideal separation factor of the coating proper, which is defined hereafter, and amounts to at least 80% and more preferably at least 90 and even 95% thereof. The supporting film used in the composite membrane according to the invention should consist of a continuous material fabricated by, for instance, extrusion or casting onto a band or roll from a melt or solution of the polymer or compressing the polymer material in a fluid state into a continuous structure at elevated pressure and temperature. Outside the scope of the invention are discrete fibres or threads made up of long polymeric objects such as those obtained by weaving, knitting or other known, analogous techniques such as those by which non-woven structures are fabricated. The invention also relates to a process for fabricating a composite membrane comprising a non-porous coating on a microporous polymeric support, comprising drawing a polymeric film which on drawing becomes more porous, to which film an initial layer has been applied containing the material of the non-porous coating or a precursor thereof, the initial layer being present in the liquid state when drawing is commenced, the viscosity of the initial layer being increased during drawing. Such a process is known from US-A-4.919.856, in which a solution of, for instance, polysiloxane is applied to a non-porous hollow polyethylene fibre. The solvent is evaporated, whereupon the fibre, being covered with polysiloxane in non-liquid, for example solid or semi-solid, state, is drawn. In this process, the support becomes microporous whilst the coating remains non-porous. Finally, the polysiloxane is thermally crosslinked. A disadvantage to this known process is that only draw ratios of up to about 2 can be applied because otherwise pores and holes develop in the polysiloxane layer. No higher draw ratio's are possible in the known process because if the initial layer is present in the solid state, it can withstand only slight drawing without tearing and if this layer is present in the liquid state, drawing must be limited so as to prevent the pores from becoming too large, allowing the material of the layer to sink in them. At said low draw ratios the support material becomes only slightly porous and only small pores of maximum 0.5 µm are formed. As a consequence, the support offers considerable resistance to gas and vapour transport and when the composite membrane is applied for, for instance, gas or vapour separation, the porous support restricts the discharge of the gas or vapour selectively diffusing through the non-porous layer. The invention aims to provide a process allowing composite membranes to be fabricated, in which the support offers less resistance to gas and vapour transport than the membranes known in the art. This objective is achieved by the invention in that the polymeric film is produced from a solution and in that the drawing comprises an uniaxial drawing with a draw ratio of at least 6 or a biaxial drawing with a draw ratio of at least 3*3. A support is started from which either is not yet porous or whose surface pores still are so small that the initial layer deposited on the surface cannot sink into them. This method has been found to allow higher draw ratios so that supports with a higher porosity and a greater mean flow pore size can be obtained and both the coating and the support may be substantially thinner than in the method known in the art, and this is favourable with respect to the flux. Drawing increases the porosity and particularly the permeability to gases of the support. At the same time, however, the viscosity of the initial layer must be increased, as is the greatest pore size that the increasingly viscous initial layer can span without collapsing under its own weight, so that the initial layer is prevented from sinking into the pores at all times. In this way, a composite membrane can ultimately be obtained in which the mean flow pore size of the support can be substantially more than 0.5 µm and which is provided with a very thin coating. The method according to the invention has even been found capable of producing composite membranes in which the mean flow pore size of the support is 1 µm or more and even 2 µm or more. Consequently, the overall resistance to gas or vapour transport of such a membrane is substantially less than that of a membrane produced according to the state of the art. As polymeric film which can be drawn to serve as the desired microporous support use may in principle be made of any film whose surface pores are so small that the initial layer cannot sink into them or can sink into them only to a very limited extent or which is even non-porous but whose volume porosity and particularly the size of the surface pores increases on drawing. Suitable starting films are for instance films of polytetrafluoroethylene, high and low-density polyethylene, polypropylene, polyetherimide, polyvinylidene fluoride, polyoxymethylene, polyphenylene sulphide , poly-4-methyl pentene and other polymers from which films can be formed whose porosity increases on drawing under suitable conditions. The presence of inorganic fillers in the polymer often has a favourable effect on the increase in porosity on drawing. The undrawn films may be produced from a melt or a solution of the polymer by processes known per se in this branch of engineering for the production of such films. Films produced from a solution generally exhibit high drawability and this is of advantage in the process according to the invention. Particularly suitable are films obtained through gelation of a polyethylene solution, preferably polyethylene with an Intrinsic Viscosity, measured in Decalin at 135°C, of at least 4 dl/g, in an organic solvent, for instance Decalin or xylene, followed by removal of the solvent. Such films combine a relatively low initial volume porosity and an initially small surface pore size with high drawability and can be drawn to form supports having excellent mechanical properties, high volume porosity, a large mean flow pore size, relatively large surface pores and high surface porosity. Examples of these are to be found in EP-A-378.279, EP-A-500.173 and EP-A-504.954. Another advantage of membranes in which such films obtained through gelation are applied is the high pressure resistance of the coating, even in the case of very thin coatings and a large pore diameter. Consequently, the problem known from EP-A-174.918 of the coating cracking at the pores arises at much higher pressure differences across the membrane than in the case of the membranes known in the art. The cause of this is not known but a possible explanation may be sought in the fibrillic structure of the drawn film, as a result of which the pores that are perpendicular to the surface are only shallow. If the undrawn film has surface pores, they are preferably smaller than 0.2 µm. The film thickness is chosen depending on the desired and attainable draw ratio and the desired thickness of the composite membrane and may be between for instance 100 and 1000 µm. An initial layer is applied to the film, which layer contains the material of the non-porous layer or a precursor thereof. The advantages of the process manifest themselves especially when initial layers having a low viscosity are applied, such as liquid layers which in the process known in the art readily sink into the pores of a porous film. The initial layer may be applied by casting, spread coating, spraying or any other suitable technique of applying a layer of the desired uniform thickness onto the polymeric film. The coating usually consists of a polymer, in particular a silicone rubber or other rubber displaying appreciably higher permeability to at least one gas or vapour than to other gases and vapours. Many such polymers are liquid but become solid through crosslinking. Such polymers may suitably be applied in pure form to serve as liquid initial layer. If a liquid precursor, in the form of a monomer, precursor monomer or oligomer of the material of the first coating is available, which can be made solid, such a precursor may be applied as initial layer. A solution of the coating material or of a precursor may also be applied as initial layer. This is preferable for obtaining very thin coatings. An extensive list of materials which because of their selective permeability to various gases or vapours may be applied as coating in a composite membrane for gas separation which also includes pervaporation is to be found in US-A-4.919.856. A condition for applicability is that the material, when dissolved or in the molten state, can be drawn under those conditions under which the porosity of the support increases on drawing and under which the viscosity of the coating can be increased by taking appropriate measures, as disclosed hereafter. The thickness with which the initial layer is applied is chosen to match the desired thickness of the non-porous coating and the extent to which the polymeric film and the material of the initial layer can be drawn. The thickness of the polymeric film, too, is chosen to match these. In this context it should be borne in mind that the porosity of the support increases on drawing, which means that its thickness decreases less than proportionally. A certain minimum draw ratio is generally needed for obtaining a microporous film having the desired porosity properties and gas or vapour permeability. On the basis of the desired properties of the composite membrane and the specifications of the starting materials, one skilled in the art will be able choose the correct thicknesses and the draw ratio so that they match one another. A lower limit on the support thickness is dictated by the required mechanical strength of the membrane. Preferably, the support in the membrane is at least 10 µm and more preferably at least 20 µm thick. Although the thickness of the support is not bound by any physical constraints, the thickness is preferably not greater than 100 µm, more preferably not greater than 50 µm and most preferably not greater than 30 µm if a high permeability and flux are to be obtained. The process according to the invention has been found to be capable of producing composite membranes with such thin supports. The invention therefore also relates to composite membranes in which the thickness of the support is not more than 100, preferably not more than 50 and most preferably not more than 30 µm. The film with the initial layer applied to it is drawn. Drawing may be effected uniaxially, (i.e. in one direction in the plane of the film), but is preferably effected biaxially, (i.e. in two directions that are at a right angle to each other in the plane of the film). If drawing is uniaxial, the film dimension that is perpendicular to the direction of drawing is preferably kept constant to ensure that in that case, too, drawing leads to a maximum decrease in thickness of the film and of the initial layer. On the other hand, the porosity increase during drawing can be somewhat lessened by allowing a minor decrease in the film dimension that is perpendicular to the direction of drawing. If drawing is biaxial, the drawing in the two directions may be conducted simultaneously or subsequently. In the latter case the initial layer can be applied before the first drawing step or after the first but before the second drawing step. The drawing conditions, such as the temperature and the draw ratio, should be so chosen that both the film and the initial layer can withstand them without breaking. The optimum drawing conditions and the corresponding maximum draw ratio are either known per se for virtually all polymers, for instance from the aforementioned references concerning the manufacture of films that may be drawn to form a suitable, porous support, or may be established through routine experiments. It is known of high molecular weight polyethylene, for instance, that a film produced from a melt can be drawn about 30-40 times uniaxially or biaxially 6 x 6 times at a temperature below the melting point whilst a film produced from a solution of the same polymer can be drawn no less than 15 x 15 times under the same conditions. The materials of the initial layer and of the support are preferably so chosen that the support can be drawn to the desired ratio at a temperature above the glass transition temperature of the material of the coating. If this condition cannot be fulfilled, or if it can be fulfilled only with difficulty, the initial layer is preferably applied in the form of a solution. The volume porosity of the support as defined hereafter and which substantially determines the gas and vapour permeability, is preferably at least 70%, more preferably at least 80%, and the mean flow pore size (MFP) measured by a Coulter porometer is preferably greater than 0.5 µm and more preferably at least 1.0 µm. In any case, the porosity and the mean flow pore size should be such that the air permeability of the film that has been drawn to form a microporous support, measured by the Gurley method, hereafter referred to as the Gurley value, is not more than 40 s/50 ml, preferably not more than 20 s/50 ml, more preferably not more than 10 s/50 ml and most preferably 5 s/50 ml. The non-porous layer is formed from the initial layer during and by drawing. The thickness of the initial layer decreases to the desired thickness as a result of drawing. The viscosity of the initial layer is increased during drawing, as described hereafter. This prevents the initial layer from sinking into the surface pores, which become larger as a result of drawing. The increase in viscosity should impart sufficient strength to the initial layer in order for it to be able to span the expanding pores. A variety of techniques may be applied for increasing the viscosity, depending on the composition of the initial layer. If the initial layer already consists of the material from which the non-porous layer will ultimately also consist and if that material is capable of being cross-linked, the viscosity can be increased by cross-linking, preferably by thermal means, of the initial layer applied in the liquid state. If a precursor of the coating material is applied, the viscosity can often be increased by effecting the conversion of the substances mentioned to the material. If the initial layer consists of a solution of the coating material, the viscosity can be increased by removing the solvent. The solvent used is preferably not a solvent to the polymer of the support. The measures mentioned may optionally be taken in combination. The initial layer may in all cases contain suitable additives such as accelerators, activators, catalysts and the like. The drawing rate and the rate at which the viscosity is increased in the aforementioned or in other suitable manners must always be so matched as to prevent the initial layer from sinking into the pores and to ensure it retains sufficient drawability. By adjusting the drawing rate, for instance, the residence time in the drawing oven, which usually operates at elevated temperature, can be suitably chosen. In this way, both evaporation of the solvent and thermal cross-linking can be effected. The film may also be irradiated during drawing so as to effect cross-linking. It is only required that during the drawing process the viscosity of the initial layer is increased to such an extent that sinking into the pores is prevented. If required e.g. the cross-linking process or the solvent removal treatment can be finished after the drawing step. The process is particularly suitable for producing membranes to be applied for gas separation and pervaporation. In that case, the non-porous layer will consist of a material possessing a better permeability to at least one gas or vapour than to other gases or vapours. In that application, polysiloxanes are highly suitable materials for the non-porous layer. The invention will be elucidated with reference to the following examples. The quantities mentioned in the examples are determined as follows. The ideal separation factor α 0 of the coating material for separation of two gases is calculated as the ratio of the permeability coefficients of the material for the gases concerned. The permeability coefficient is determined in a cell consisting of two parts separated by the membrane to be tested. The effective membrane area is 11.34 cm 2 . The cell is evacuated and subsequently to the part of the cell at one side of the membrane, denoted by the feed side, gas is offered at constant pressure. Under the driving force of the vacuum on the other side, denoted as the permeation side, and the pressure at the feed side sorption and diffusion of the gas in the membrane occurs due to which the pressure at the permeate side increases. The increase of the pressure at the permeate side, denoted by dp/dt, is recorded. The recorded curve shows an initial curved part, the diffusion region, which shades off in a straight line. The slope of this straight part gives the value of dp/dt to be used for the calulation of the permeability coefficient P according to the following formula: P = {(273/T x 1.013x 10-3) x Vp x dp/dt x l}/(A x p), wherein P is expressed in 10 -10 cm 3 .cm/cm 2 .s.cmHg (this unit will be further denoted as "Barrer"); T is the temperature in Kelvin; V p is the volume of the cell part at the permate side in cm 3 ; dp/dt is the increase of pressure at the permeate side in mbar/s; l is the thickness of the separating layer of the membrane; A is the effective membrane area; and p is the pressure over the membrane. In case a mixture of gases a and b is used the permeability coefficients of both gases can be determined by applying the partial pressures over the membrane in the given formula. The composition of the gas at the permeate side is determined by gas chromatography. The actual separation factor, α, of a composite membrane for gas separation is calculated in an analogous manner from the permeability coefficients of the membrane for the gases concerned. The separation properties of the coating material in pervaporation are determined from measurements on a CELFA P28 Laboranlage® pervaporation set-up. A 10-% solution of ethanol in water at a temperature of 55°C and a pressure of 2 bar is present on the feed side. The pressure on the permeate side is 20 mbar. The ideal separation factor of the coating material for the separation of two components 1 and 2 from a mixture of liquids in pervaporation is then calculated as follows: α 0 = (X1/X2)/(Y1/Y2) where X1 and X2 represent the percentage concentrations of the components 1 and 2 on the permeate side and Y1 and Y2 represent the concentrations on the feed side of the membrane. The actual separation factor, α, of a composite membrane in pervaporation is calculated in the same way from the concentrations mentioned, measured in the set-up referred to with the composite membrane as separating element. The air permeability is determined in s/50 ml as the Gurley value in accordance with ASTM Standard D726-58 with a measuring area of 6.45 cm 2 (1 sq. inch) under a weight of 567 grams. The thickness of the support is measured either with a Millitron Feinprüf meter, the probe of which has a radius of curvature of 12 mm, or by Scanning Electron Microscopy (SEM). The coating thickness is also determined by SEM. The density of the support is determined by weighing a piece of film of known volume. The volume porosity is determined from the measured density ρ and the density of the polyolefinic bulk material ρ 0 as: volume porosity = ρ 0 - ρ ρ 0 X 100%. The pore size distribution and, based on this, the mean flow pore (MFP) size are determined with the aid of a Coulter porometer. The intrinsic viscosity (IV) of polyethylene is determined in Decal in at 135°C. Example I A polyethylene film having an IV of 16 dl/g, a thickness of 450 µm, a volume porosity of 30% and a Gurley value of 133 s/50 ml is spread coated with a mixture of 12 parts by weight of polydimethylsiloxane (PDMS; RTV 615A of GE Silicones), a liquid silicone rubber, to which a cross-linking agent (RTV 615 B of GE Silicones) has been added. The viscosity of this initial layer is about 4 Pa.s, the thickness of the layer is 130 µm. A square section of 8 x 8 cm is cut from this and is simultaneously biaxially drawn in an Iwamoto drawing frame at a rate of 5 mm/s at 120°C. During drawing, the PDMS is cross-linked almost completely. On cooling to room temperature, the drawn film is removed from the frame. Its thickness, porosity and permeability are determined. The Gurley value of the membrane is infinite, which means that the coating is completely impermeable and free of holes. The properties of the drawn support are measured on the support after removal of the PDMS layer. The properties measured on a support drawn without a coating but for the rest under the same conditions are found not to differ therefrom to any appreciable extent. The results are given in Table 1. Draw ratio 4x4 5x5 6x6 8x8 Membrane: Support thickness (µm) 100 70 55 32 Coating thickness (µm) 14 11 6 1.5 Gurley value (S/50 ml) ∞ ∞ ∞ ∞ Support: Porosity (%) 87 87 85 84 Gurley value (s/50 ml) 0.5 0.6 0.3 0.3 Max. pore size (µm) 7.6 7.8 9.9 10.7 Min. pore size (µm) 3.7 3.3 3.7 4.2 Mean pore size (µm) 4.4 4.9 4.8 6.0 Example II A polyethylene film having an IV of 4 dl/g, a thickness of 450µm, a volume porosity of 35% and a Gurley value of 1200 s/50 ml is spread coated, with the aid of a doctor blade, with a 400-µ thick layer of a 30-% solution of high molecular weight (400,000 g/mol), atactic polymethyl methacrylate (PMMA) in acetone. A square section of 8 x 8 cm cut from this film is biaxially drawn in an Iwamoto drawing frame at a rate of 5 mm/s at 120°C. The solvent evaporates during drawing. The properties of the membrane and the support are determined on the analogy of Example 1. The results are given in Table 2. Draw ratio 4x4 5x5 6x6 Membrane: Support thickness (µm) 128 115 85 Coating thickness (µm) 10 8 4.5 Gurley value (S/50ml) ∞ ∞ ∞ Support: Porosity (%) 84 83 85 Gurley value (s/50 ml) 15.6 11.3 8.1 Max. pore size (µm) 0.87 0.71 0.91 Min. pore size (µm) 0.24 0.25 0.34 Mean pore size (µm) 0.54 0.57 0.62 Example III A polyethylene film having an IV of 4 dl/g, a thickness of 600 µm, a volume porosity of 30% and an MFP of less than 0.07 µm is spread coated with the polydimethylsiloxane - cross-linking agent mixture of Example I. The viscosity of this initial layer is about 4 Pa.s. A square section of 8 x 8 cm cut from this film is biaxially drawn 5 x 5 times in an Iwamoto drawing frame at a rate of 5 mm/s at 120°C. During drawing, the PDMS is cross-linked almost completely. On cooling to room temperature, the drawn film is removed from the drawing frame and tested with respect to its properties as a composite membrane. In the pervaporation test, the ethanol concentration on the permeate side after 6 hours is 45%. The actual separation factor of the membrane for ethanol/water is calculated herefrom to be 7.4. The ideal separation factor, measured on a self-supporting 100-µm thick PDMS layer, is 7.8. The flux of the composite membrane standardized with respect to the coating thickness is 3.0 kg/m 2 .h.µm. The flux of pure PDMS is 3.2 kg/m 2 .h.µm. This means that the presence of the support reduces the separation factor by only 5% relative to the ideal separation factor and has no greater effect on the flux than that of an increase in the thickness of the gas separating coating of only 0.6 µm, which is equivalent to 6.7%. The data of the membrane and of the support are given in Table 3. Draw ratio 5x5 Membrane: Support thickness (µm) 90 Coating thickness (µm) 9 Gurley value (S/50 ml) ∞ Standardized flux (kg/m 2 .h.µm) 3.0 Support: Porosity (%) 84 Gurley value (s/50 ml) 0.7 Max. pore size (µm) 5.7 Min. pore size (µm) 2.0 Mean pore size (µm) 2.7 Example IV A polyethylene film having an IV of 4 dl/g, a thickness of 450 µm, a volume porosity of 35% and a Gurley value of 1200 s/50 ml is spread coated, with the aid of a doctor blade, with a 60 µm thick layer of a 21 wt% solution of medium molecular weight (100,000 g/mol), atactic polymethyl methacrylate (PMMA) in acetone. A square section of 8 x 8 cm cut from this film is sequentially biaxially drawn in an Iwamoto drawing frame at a rate of 5 mm/s at 120°C. The solvent evaporates during drawing. The gas separation properties of the obtained membrane for a 50/50 vol.% mixture of CO 2 and CH 4 are determined as described above. The results are given in Table 4. Draw ratio 3x3 5x5 Support thickness (µm) 135 100 Coating thickness (µm) 4.2 1.8 Gurley value (S/50ml) ∞ ∞ CO 2 -permeability (Barrer) 0.27 0.20 CO 2 -flux (cm 3 /cm 2 .s) 7 x 10 -6 1.5 x 10 -5 α CO2/CH4 30 43 For comparison it is noted that for pure PMMA the CO 2 permeabilty is about 0.34 Barrer and the α CO2/CH4 about 50. Example V A roll of polyethylene film having an IV of 4 dl/g, a thickness of 450 µm, a volume porosity of 35%, a Gurley value of 1200 s/50ml and a width of 24 cm is drawn on a Cellier drawing line first at 125°C in the direction of its length (Machine Direction, MD) by a drawing factor of 3.8. Subsequently to the drawn film an initial layer of 60 µm consisting of a mixture of PDMS (RTV615A of GE Silicones) and 10 wt% of the total mixture of a cross linking agent (RTV615B of GE Silicones)is applied using a doctor blade. The coated film was transported with a speed of 13 mm/min through a drawing oven during which it is drawn to 6 x its original width at a temperature increasing from 135 to 140°C. At the exit of the oven the PDMS was completely cross-linked. The gas separation properties of the membrane was determined as described above for a 50:50 vol.% mixture of CO 2 and CH 4 and for a 20:80 vol.% mixture of O 2 and N 2 . The results are given in Table 5. Membrane: Support thickness (µm) 100 Coating thickness (µm) 10 Gurley value (S/50 ml) ∞ CO 2 -permeability (Barrer) 1734 α CO2/CH4 2.38 O 2 -permeability (Barrer) 340 α O2/N2 1.64 Support: Porosity (%) 85 Gurley value (s/50 ml) 2.4 Max. pore size (µm) 2.1 Min. pore size (µm) 1.0 Mean pore size (µm) 1.2

Claims: Composite membrane comprising a microporous polymeric film as support and a non-porous gas or vapour-separating coating present on that film, characterized in that the air permeability of the film, measured by the Gurley method, is not more than 40 s/50 ml and the coating thickness is not more than 15 µm and in that the actual separation factor of the membrane is at least 80% of the ideal separation factor of the coating and the effective thickness of the coating is not more than 20% greater than the nominal thickness of that layer. Composite membrane according to Claim 1, characterized in that the polymeric film is polyethylene having an Intrinsic Viscosity, measured in Decalin at 135°C, of at least 4 dl/g. Process for the manufacture of a composite membrane comprising a non-porous coating on a microporous polymeric support, comprising drawing a polymeric film, which on drawing becomes more porous, to which an initial layer has been applied containing the material of the non-porous coating or a precursor thereof, the initial layer being present in the liquid state when drawing is commenced, the viscosity of the initial layer being increased during drawing, characterized in that the polymeric film is produced from a solution and in that the drawing comprises a uniaxial drawing with a draw ratio of at least 6 or a biaxial drawing with a draw ratio of at least 3*3. Process according to claim 3 characterized in that the polymeric film is obtained through gelation of a polyethylene solution in an organic solvent, followed by removal of the solvent, the polyethylene having an Intrinsic Viscosity, measured in Decalin at 135°C, of at least 4 dl/g. Process according to either Claim 3 or Claim 4, characterized in that the initial layer comprises a solution of the material or the precursor in a solvent and in that the viscosity is increased by removing at least a portion of the solvent during drawing. Process according to anyone of Claims 3-5, characterized in that the viscosity is increased by cross-linking the material or the precursor during drawing. Process according to any one of claims 3-6, characterized in that the non-porous layer is more permeable to at least one gas than to other gases. Process according to any one of Claims 3-7, characterized in that the polymeric film is drawn until, as a support, it exhibits an air permeability, measured by the Gurley method, of not more than 20 sec/50 ml.

Inventors: FORTUIN HENRICUS MATHEUS, STOKMAN PETRUS HENRICUS MARIA, FORTUIN, HENRICUS MATHEUS, STOKMAN, PETRUS HENRICUS MARIA
Applicants: DSM NV, DSM N.V.
Application year: 1993
Main classification: B01D69
IPC codes: B01D67, B29C55, B01D69