SEALED CONDUCTIVE ACTIVE ALLOY FEEDTHROUGHS

Abstract: Disclosed is a method of manufacturing an electrically conductive feedthrough in an article having a ceramic surface comprising the steps of inserting a feedthrough preform into and closely fitting an insertion hole in the article, said preform integrally comprising an outer surface comprising at least in part an active alloy capable of reacting with an inner surface of said insertion hole to wet said inner surface and form a braze and then heating and cooling said article and said feedthrough preform to form a braze sealing said feedthrough to said article. Also disclosed are feedthrough preforms comprising either an active alloy wire or a composite wire having a core and an outer layer of an active alloy. The invention further comprises fixing a non-melting electrical conductor to either feedthrough preform during the brazing step.

Description: SEALED CONDUCTIVE ACTIVE AT/mv FF P HROUGHS This invention relates to feedthroughs and to wires usable for forming such feedthroughs. More particularly, the invention relates to sealed conductive active alloy feedthroughs for use in articles having a ceramic surface. Feedthroughs comprise a conductive path (the feedthrough) passing via a hole (the feedthrough aperture) through a wall in an article. Metallic feedthroughs (e.g., electrodes) are well known in industry and are commonly used to provide electrically conductive paths through ceramic articles while excluding the passage of solids, liquids, and gases. One application for such feedthroughs is in magnetic inductive field flow meters which require a chemically inert electrode hermetically sealed in the wall of an electrical insulating and chemically resistant ceramic cylinder. Feedthroughs are also used to carry electrical power to/from an active device such as a transistor or diode. Various commercial methods have been employed to produce metallic feedthroughs. Typically, with alumina ceramics, the feedthroughs (i.e., metallic conductors) are brazed in place using a multi-step process described in the following with reference to FIG. 1 of the drawings. A ceramic article 1 has an ceramic electrode insertion hole 2 forming a feedthrough aperture which is metallised by coating with a moly- anganese or tungsten paint 3 and sintered at approximately. l,50θ''c in wet hydrogen. The inside diameter of the coated insertion hole 2 is then nickel plated 4 and sintered at approximately. 950 β C (this step is known as metallisation plating). The metallic conductor 5 is inserted in the electrode insertion hole 2 with a brazing alloy preform 6 or a paste positioned on the top side to fill voids at the interface of the conductor 5 and the insertion hole 2 upon brazing. The ceramic article 1 and conductor 5 are then simultaneously heated to effectuate brazing of the conductor 5. A major drawback of this method is that, in most instances, the conductor 5 is placed in a vert al position during brazing to avoid migration of the brazing alloy or paste (disposed on the top side of the conductor 5) from regions of the interface under the influence of gravity. This multi-step operation is also very time consuming and expensive. In U.S. Patent No. 5,095,759 a method is disclosed wherein a core wire (e .g. , platinum) 9, coated with an active alloy paste 7, is inserted into a pre-sintered ceramic insertion hole 8 forming a feedthrough aperture (See FIG 2. of the drawings). The ceramic article 10 and the wire 9 are then simultaneously heated to braze the wire 9 in the hole 8. According to this method, since the paste 7 (a powder in a liquid carrier) only occupies approximately 50% of the space, an additional alloy, in the form of a brazing filler preform 11 is placed on the top side of the ceramic article 10 to fill the void upon brazing. This method also suffers from similar drawbacks as noted above. By active alloy is meant an alloy which contains a constituent that reacts with the surface to be brazed to so as to wet and provide chemical as well as mechanical bonding. A review of such alloys may be found in Ceramics and Glasses', Volume 4, Engineered Materials Handbook pages 502-510 (published by ASM International, 1991). A further review may be found in % Joining in Ceramics', pages 73-92, editor M.G. Nicholas, (published by Chapman & Hall for the Institute of Materials, 1990). In U.S. Patent No. 4,912,838 a method is disclosed wherein an electrode is formed by filling a predetermined hole 12 forming a feedthrough aperture in a sintered ceramic 13 with a conductive metal paste 14 comprising moly-manganese, tungsten, copper, or similar material and subsequently heating the paste 14 to promote adherence to the ceramic (see FIG. 3). This method often produces conductive feedthroughs that fail during vacuum leak testing. This document also discloses use of ceramic cores (32a, 41a) to such feedthroughs and discloses lining feedthrough holes with paste (71b) and filling the remaining void space with brazing alloy (71a). All of the above mentioned methods in which pastes are used are complex and time consuming in that ensuring that alloy paste fills or completely lines the feedthrough aperture is difficult. In Japanese Patent (Laid-open) No. 58-501552 (equivalent to U.S. Patent No. 4,507,975), another method is disclosed wherein a high melting point but ductile metal pin is inserted into an electrode insertion hole forming a feedthrough aperture in a cylindrical moulded body made of a non-sintered ceramic material (e.g., oxide ceramic). In this state, the moulded body is sintered at a predetermined temperature and at the same time the electrode is integrally fixed to the electrode insertion hole by sintering. That is, since a ceramic material contracts (approximately. 17 to 20% in the case of A1 2 0 3 ) by sintering, the electrode and the moulded body are integrally formed, and a liquid-tight seal of the electrode insertion hole is obtained. A noble metal such as platinum or a platinum alloy is used as the electrode material. In this method, however, in order to reliably seal the electrode insertion hole, the dimensional tolerance between the electrode and the insertion hole, and the mating surface finishes must be strictly controlled. Further, since the non-sintered electrode insertion hole is weak, it is difficult to machine without damage, resulting in a large number of manufacturing steps, and subject to additional damage when the electrode is inserted into the non-sintered electrode insertion hole. Finally, variations in the contraction rate of the ceramic material upon sintering, due to differing ceramic batches or manufacturing time, generally result in a defective liquid seal or undesirable residual stresses which could damage the ceramic article upon sintering. U.S. Patent No. 3,929,426 discloses a method of retaining a lead in a ceramic body by forming a lead having a core and a coating comprising a ductile metal plating of lower melting temperature than the core, inserting the lead in an aperture in an article, and firing the lead and article to a temperature such that the coating melts and on cooling forms a casting mechanically keyed into the ceramic. The applicants have found that by providing a wire having a surface comprised of active brazing alloy a one-step brazing of feedthroughs into articles having a ceramic surface may be effected providing a hermetic seal with chemical bonding. The sealed conductive feedthroughs of the present invention substantially reduce or eliminate the disadvantages and shortcomings associated with prior art feedthroughs. The invention specifically discloses a method of manufacturing an electrically conductive feedthrough in an article having a ceramic surface comprising the steps of: i) inserting a feedthrough preform member into and closely fitting a predetermined insertion hole forming a feedthrough aperture in the article, said preform member integrally comprising an outer surface comprising at least in part an active alloy capable of reacting with an inner surface of said insertion hole to wet said inner surface and form a braze ii) heating said article and said feedthrough preform member for a predetermined time and at a predetermined temperature to achieve a brazing reaction at the interface between said inner surface of said insertion hole of said article and said outer surface of said feedthrough preform member iii) cooling said article and said feedthrough preform to form a braze sealing said feedthrough member to said article to form a feedthrough. The feedthrough preforms of the invention may comprise an active alloy wire having a sufficiently active element to chemically react with the ceramic surface of the article or a composite wire having a core and an outer layer of an active alloy which would similarly have a sufficiently reactive element to chemically react with both the ceramic surface of the article and the core material. The invention further comprises fixing a non-melting electrical conductor (e.g., connector pin) to either feedthrough preform during the above mentioned heating step. Further features and advantages will become apparent from the following and more particular description of the preferred embodiment of the invention, as illustrated in the accompanying drawings, in which like referenced characters generally refer to the same parts or elements throughout the views, and in which: FIG.s 1-3 are sectional views of prior art feedthroughs (i.e. metallic conductors); FIG. 4 is a sectional view of a feedthrough according to the invention; FIG. 5 is a sectional view of another embodiment of the feedthrough according to the invention; and FIG. 6 is a sectional view of yet another embodiment of the feedthrough according to the invention. In accordance with the present invention, as illustrated in FIG. 4, the first step in manufacturing a sealed conductive feedthrough is to insert the feedthrough preform 16 into a predetermined insertion hole 17 in an article 18 to form an assembly of preform 16 and article 18 whereby the active alloy outer surface of the preform 16 is disposed in contact with the inner surface of the insertion hole 17. The article 18 may comprise ceramics, metals, or mixtures of metals and ceramics. Metal articles may have a ceramic coating or be heavily oxidised such that the surface has a composition and wetting behaviour approximating a ceramic. The feedthrough preform 16 has an outer surface approximately conforming with the inner surface of the insertion hole 17 and comprises at least in part an active alloy having sufficient active element to chemically react with the inner surface of the insertion hole 17 of the article 18 and, thereby, enhance the wetting and adherence of the active alloy to the ceramic surface of article 18. In the preferred embodiment of the invention, the feedthrough preform 16 comprises an active alloy wire. As will be recognised by one skilled in the art, a key feature of the invention is the use of an active alloy (i.e., active brazing alloy) to achieve a sufficiently bonded and, hence, hermetically sealed conductive feedthrough 16. By the term "hermetically sealed", is meant an effective gas and, hence, liquid and solid seal exhibiting an acceptable leak rate for the particular application intended. In most instances, this will be preferably less than 10 cc/second of helium on a conventional helium mass spectrograph. It is generally recognised that metals will not bond chemically to ceramics because the metallic electronic structure is not compatible with the ionic-covalent electronic structure of ceramic materials. A different phase is thus necessary at the interface as a compatible transition between the metal and the ceramic. With oxide ceramics, the compatible phase (i.e., chemical bond) is one of the oxides of the metal. The oxide maintains a continuous electronic structure across the interface, and a transition in bond type and bond energies between the metal and the ceramic. A balance of bond energies and a continuous electronic structure across an interface is generally indicative of a chemical bond, whether the bonding is ionic, covalent, or metallic. These factors do, however, influence the bond microstructure. For example, when the two reacting materials or phases (ceramic/ceramic or metal/metal) have no changes in valence, then the reaction is the formation of a solid solution alloy or compound by inter-diffusion. When the two reacting materials (ceramic/metal) have changes in valence, then a reduction-oxidation (redox) reaction occurs. The driving force for a redox reaction is a favourable negative standard free energy ΔG° R . In order to realise a favourable ~A G °R» ^ t * s necessary to employ materials (i.e., metals) having sufficiently high oxygen potentials to reduce the cation (i.e., ceramic) with a lower oxidation potential. Such metals are commonly referred to as active elements and include, but are not limited to, titanium, zirconium, chromium and vanadium. Thus, according to the invention, the feedthrough preform 16 comprises at least in part an active alloy having sufficient active element to chemically react with the ceramic surface of an article 18, particularly a ceramic article. The feedthrough preform 16 may for example comprise an active alloy wire having a composition substantially comprised of, in weight percent: 58-60% Ag, 26.25-28.25% Cu, 12-13% In, 1-1.5% Ti (Incusil ABA(™) ) . In further embodiments of the invention, the active alloy wire 16 may substantially comprise, in weight percent: 62-64% Ag, 33.25-35.25% Cu, 0.75-1.25% Sn, 1.5-2.0% Ti (Cusin-1 ABA(TM) ) ; 62-64% Ag, 34.25-36.25% Cu, 1.5-2.0% Ti (Cusil ABA( M)) ; 92.25-93.25% Ag, 4.5-5.5% Cu, 0.75-1.25% Al, 1-1.5% Ti (Silver ABA(™)); 92.25- 93.25% Cu, 1.75-2.25% Al, 2.75-3.25% Si, 2-2.5% Ti (Copper ABA(n ); 95.9-96.9% Au, 2.5-3.5% Ni, 0.5-0.7% Ti (Gold ABA(TM)); and 81-83% Au, 14.5-16.5% Ni, 0.5-1.0% Mo, 1.5-2.0% V (Nioro ABA(TM)). Other materials which may be used include:- 5-25% Pd, 5-25% Cu, 20-85% Ag, and from about 0.25- 4% of a metal selected from the group consisting of Ti, V and Zr (Palcusil 10 ABA(™)); 75-98% Au, 0.5-20% Ni, 0.5-6% V; 75- 98% Au, 0.5-20% Ni, 0.5-6% V, 0.25-4% Mo; 75-98% Au, 0.5-20% Ni, 0.5-6% V, 0.3-5% Cr; and 75-98% Au, 0.5-20% Ni, 0.5-6% V, 0.3-5% Cr, 0.25-4% Mo. These active alloys are commercially available under the aforementioned trademarks from Wesgo, Inc., a division of The Morgan Crucible Company, pic. According to the method of the invention, the second step comprises heating the assembly of the article 18 and feedthrough preform 16 for a sufficient predetermined time and temperature to achieve a brazing reaction at the interface between the inner surface of the insertion hole 17 of the article 18 and the outer surface of the feedthrough 16 to produce a hermetically sealed feedthrough 16. Preferably, the heating time and temperature is sufficient to achieve the brazing reaction while avoiding substantial migration of the active alloy from regions of the interface under the influence of gravity. By the term "brazing reaction", it is meant to mean the occurrence of the requisite reduction-oxidation (redox) reaction at the interface of the active alloy and the ceramic surface of an article whereby a chemical bond is achieved at the interface. As will be recognised by one skilled in the art, the brazing temperature will, in most instances, be at or near the liquidus temperature for the active alloy. It has been found that by maintaining the brazing reaction temperature for a predetermined time, in addition to achieving the requisite redox reaction at the interface of the feedthrough preform 16 and the article 18, the active alloy will wet to and generally flow into the capillary gaps in the article 18, notwithstanding the orientation (i.e., vertical, horizontal, etc. ) of the feedthrough preform 16. In addition, when the feedthrough preform (i.e., active alloy wire) 16 is melted in the insertion hole 17, the feedthrough 16 will generally fill any imperfections in the hole 17. These factors significantly enhance the hermetic sealing of the feedthrough 16 in the insertion hole 17. Thus, as will be recognised by one skilled in the art, various compatible ceramic/active alloy systems within the scope of this invention may be employed to meet the requirements of a particular application. The general requirement of a compatible system is, of course, that the active alloy have a melting point less than the article providing the feedthrough aperture. In a further embodiment of the invention, as illustrated in FIG. 5, the feedthrough preform 19 comprises a composite wire having a core 20 and at least an outer layer 21 of an active alloy having sufficient active element to chemically react with the ceramic surface of an article 22. The core 20 generally comprises an electrically conductive material which has a higher melting point than the active alloy outer layer 21. Preferably, the core 20 comprises a material selected from the group consisting of Kovar(™) , gold, copper, nickel, platinum, silver, palladium, molybdenum, niobium, titanium, zirconium, iron and alloys thereof. The active alloy outer layer 21 of the composite wire preform 19 may comprise any of the alloys listed above for feedthrough preform 16. As will be recognised by one skilled in the art, various compatible materials within the scope of this invention may be employed to produce the composite wire feedthrough preform 19. It has, however, been found that certain requirements of compatibility should be adhered " to realise the full benefits of the invention. First, the core material must not readily alloy with the active alloy outer layer. For example, a silver active brazing alloy outer layer with a copper core could form an undesirable lower melting point silver-copper eutectic alloy. Second, the annealing temperature range for both the core and active alloy outer layer should be similar. It has also been found that the thickness of the active alloy outer layer 21 should be maintained in the range of approximately 0.001 to 0.010 inches [0.0254 to 0.254mm] to realise optimum wetting and adherence of the composite wire feedthrough 19 to the article 22 (or host) . In the preferred embodiment, the active alloy outer layer 21 would comprise a cladding disposed immediately adjacent to, and completely surrounding, the core 20. The cladding is generally of solid form such as an active brazing alloy sleeve. The active alloy clad wire 19 may also be mechanically reduced to a predetermined size and shape. For example, the clad wire 19 may be drawn to achieve the desired cladding thickness or upset (i.e., flattened) on one end to form a flat tab for electrical attachment or to form a flat (i.e., nail head) bonding face. The flattened end or tab may also be employed as a mechanical stop to position and anchor the wire 19 in place during the heating step, thus eliminating the need for gaging or pastes. The clad wire 19 may also be upset at mid-length with electrical leads disposed on each end. A further advantage of the composite wire feedthrough 19 is that the extra active alloy cladding 21, which is available from the wire being slightly extended from the insertion hole 23, will be drawn toward the ceramic surface and generally fill any voids in the hole 23. Thus, active alloy pastes or preforms 11, as illustrated in FIG. 2, are not required. As will be recognised by one skilled in the art, an additional advantage of the composite wire feedthrough 19 is that the feedthrough may be employed for use in relatively large (i.e., > .020" [0.508mm] diameter) insertion holes 23. The maximum diameter of the active alloy wire feedthrough would be dictated by several variables including, among other factors, the surface tension at the interface, brazing temperature, and alloy composition. According to the method of the invention, a further step may be employed whereby an electrical conductor 25 is placed on at least one end of the feedthrough 26 during the heating and melting of the active alloy (i.e., wire or outer layer), whereby the electrical conductor 25 is effectively fixed to the feedthrough 26 upon cooling (see FIG. 6). the electrical conductor may, for example, be a connector pin or conductive end piece used to facilitate electrical connection and, hence, transfer of electrical energy and/or signals to and from a body. In this instance, the electrical conductor 25 may be employed to transfer signals to/from the feedthrough 26 or as an electrode surface (i.e., contact point). Various conventional positioning methods may be employed to position and anchor the electrical conductor 25 in place during the melting of the active alloy 26. For example, the electrical conductor 25 may be self-centring or self- positioning, i.e., designed to be positioned by the insertion hole itself and anchored therein by the frictional forces between the electrical conductor 25 and the insertion hole (e.g., slight press fit) or designed and configured to engage the outside diameter or configuration of the ceramic body 22 proximate the insertion hole (e.g., ribbon clip) (see FIG. 6). Various alloy pastes may also be employed to position and anchor the electrical conductor 25 in place during melting of the active alloy 26. * In the preferred embodiment of the invention, the electrical conductor 25 would comprise a conductive material. Preferably, the electrical conductor 25 would comprise a material selected from the group consisting of Kαvar(τn) , copper, platinum, nickel, gold, silver, molybdenum, niobium, zirconium, titanium, palladium, iron and alloys thereof. As will be recognised by those skilled in the art, the electrical conductor 25 may have a wide variety of shape characteristics including variable cross-sectional dimensions (e.g. round or flat ribbon) . The electrical conductor 25 can also be tailored to the particular application on either side of the feedthrough 26 as may be required. For example, two electrical conductors may be employed with different cross- sections and/or different compositions (i.e., copper on one side and platinum on the other side) . To enhance the sealing of the feedthrough 26 and the mechanical bond of the electrical conductor 25 to the feedthrough 26, an active brazing alloy paste 27 may be placed around the electrical conductor 25 prior to heating of the feedthrough 26 and, hence, melting of the active alloy. Suitable active brazing alloy paste 27 could have a composition substantially comprised of, in weight percent 59.0% Ag, 27.25% Cu, 12.5% In, 1.25% Ti. In further embodiments of the invention, the active alloy paste 27 may have a composition substantially comprised of, in weight percent: 63.0% Ag, 34.25% Cu, 1.0% Sn, 1.75% Ti; 63.0% Ag, 35.25% Cu, 1.75% Ti; and 92.75% Ag, 5.0% Cu, 1.0% Al, 1.75% Ti. Indeed any of the active alloys mentioned as suitable for forming the feedthrough preform 16 or outer layer 21 may, in paste form, be used for this purpose. The examples which follow illustrate the methods of manufacturing the conductive feedthroughs of the present invention. The examples are for illustrative purposes only and are not meant to limit the scope of the claims in any way. Exapple 1 A 0.011" [0.2794mm] diameter Cusin-1 ABA (63.0% Ag, 34.25% Cu, 1.0% Sn, 1.75% Ti) active braze alloy wire was inserted into a 0.012" [0.3048mm] diameter hole in an alumina ceramic body (0.064" [1.6256mm] wall thickness). The wire preform was cut to leave zero to 1/8" [3.175mm] overhang on each end of the hole. The assembly was placed in a vacuum furnace and heated to 825 β C under 10~ 5 torr vacuum. The active alloy feedthrough was then tested with a helium mass spectrograph. The feedthrough was found to be hermetically sealed having a leak rate of less than 10~ 9 cc/second. Example 2 An active alloy covered composite alloy wire was produced by inserting a 0.588" [14.9352mm] outer diameter Kovar rod into a 0.592" [15.0368mm] inner diameter 0.750" [19.05mm] outer diameter alloy tube with a composition of 63% Ag, 34.25% Cu, 1% Sn, 1.75 Ti. The assembly was reduced to a wire 0.0185" [0.4699mm] diameter by conventional wire drawing. Approximately 0.25" [6.35mm] length of one end of the wire was flattened and cut to a length of 0.550" [13.97mm], The 0.0185" [0.4699mm] diameter wire was inserted into a sintered alumina 0.050" [1.27mm] thick with a 0.020" [0.508mm] hole, leaving 0.25" [6.35mm] protruding at each end. The assembly was placed in a vacuum furnace and heated to 830°C under 10~ 5 torr vacuum. The brazed assembly, after cooling, demonstrated that the brazing alloy from each protruding end flowed toward the alumina to fill the hole and leave a fillet at each face of the alumina feedthrough. The brazed seal was tested with a helium mass spectrograph and exhibited an acceptable leak rate of less than 10~ 9 cc/second. Example 3 An active alloy coated wire as described in Example 2 was mechanically upset to form a nail head. The wire end was cut to 0.30" [7.62mm] long and inserted into an alumina ceramic 0.050" [1.27mm] thick with a hole 0.020" [0.508mm] in diameter. The assembly was brazed in a vertical position with the nail head on top using similar brazing schedule as in example 2. The brazed assembly had provided a hermetic feedthrough with a slight fillet at each end. The brazed assembly had an acceptable leak rate of less than 10~ 9 cc/sec. Example 4 Seventeen alumina ceramic tubes, having a wall thickness of 0.105" [2.667mm], were produced with four radial through wall holes of 0.012" [0.3048mm] diameter each. Bands of internal metallisation were applied adjacent to some of the holes. Cusin ABA active braze alloy wire (0.011" [0.2794mm] diameter) was inserted into each of the holes with an overhang of 1/16" [1.5875mm] on each end. Cusin ABA paste was applied to the outermost end of the active alloy wire to promote formation of an external bead of alloy after melting. Under high vacuum at 825°C the active braze alloy constituents were melted forming vacuum tight seals and through wall electrical contacts between the outside of the assembly and the inside metallised layers. Example 5 An additional fifteen alumina ceramic tubes were produced as described in Example 4, with the following exceptions. The active alloy wire was cut to terminate 0.025" [0.635mm] inside the ceramic hole on the outside. Inserted into the hole was a 0.010" [0.254mm] thick x 0.060" [l.524mm] wide nickel ribbon with a stamped end to allow insertion into the hole at least 0.025" [0.635mm]. Active braze alloy paste was applied to the nickel ribbon-ceramic interface to promote mechanical adherence. After heating to 825°C in vacuum, all assemblies were vacuum tight and electrically conductive. The nickel ribbon on the outside allowed easy electrical connection to the interior metallised circuitry. Example 6 In this example, both an external nickel ribbon electrical conductor and an internal tungsten alloy wire were connected with the melted feedthrough under similar conditions as described in Examples 4 and 5. Electrically conductive and vacuum tight joints were produced in both cases.

Claims: CLAIMS 1. A method of manufacturing an electrically conductive feedthrough in an article having a ceramic surface comprising the steps of:- i) inserting a feedthrough preform member into and closely fitting a predetermined insertion hole forming a feedthrough aperture in the article, said preform member integrally comprising an outer surface comprising at least in part an active alloy capable of reacting with an inner surface of said insertion hole to wet said inner surface and form a braze; ii) heating said article and said feedthrough preform member for a predetermined time and at a predetermined temperature to achieve a brazing reaction at the interface between said inner surface of said insertion hole of said article and said outer surface of said feedthrough preform member; and, iii) cooling said article and said feedthrough preform member to form a braze sealing said feedthrough preform member to said article to form a feedthrough. 2. A method as claimed in Claim 1 wherein said feedthrough preform member comprises a wire of active alloy. 3. A method as claimed in Claim 1 wherein the feedthrough preform member comprises a composite wire having a core and an outer layer, the outer layer comprising active alloy. 4. A method as claimed in any preceding claim including the step of placing an electrical conductor at an end of said feedthrough preform member prior to heating and cooling whereby subsequent to said heating and cooling said conductor is effectively fixed to said feedthrough. 5. A method as claimed in Claim 4 wherein an active brazing alloy paste is placed around said electrical conductor prior to said heating and cooling to enhance the sealing of said feedthrough and the mechanical bond of said electrical conductor to said feedthrough. SUBSTITUTESHEET 6. A composite active alloy wire comprising an electrically conductive core and an outer layer of active alloy having sufficient active element to chemically react with the surface of an article and thereby enhance the wetting and adherence of said active alloy to the article. 7. A composite active alloy wire as claimed in claim 6 in which the outer layer has a thickness in the range 0.001 to 0.010 inches [0.0254 to 0.254mm]. 8. An article having a ceramic surface and an electrically conductive feedthrough formed by a method as claimed in any of claims 1-5.

Inventors: MIZUHARA HOWARD, SMITH PETER CLARK, MIZUHARA, HOWARD, SMITH, PETER, CLARK
Applicants: MIZUHARA HOWARD, MORGAN CRUCIBLE CO, SMITH PETER CLARK, THE MORGAN CRUCIBLE COMPANY PLC
Application year: 1993
Main classification: H01L21
IPC codes: B23K1, C04B37, H01L21, H05K1, H05K3