Method and plant for continuously recycling waste parts with a coating made of synthetic resin

Abstract: Waste parts with coating made of synthetic resin, for example bumpers, are crushed into chips. The chips are continuously supplied to a cylindrical vessel by the first let-off apparatus. In this vessel, coating is continuously hydrolyzed and decomposed. After the chips with a powdered coating are dried in a dry furnace, the chips are delivered to the second let-off apparatus, and are kneaded into synthetic resin by a kneader. Kneaded chips are extruded from extruding dies and are pelletized. The pelletized synthetic resin is reused as material for new bumpers.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method and plant for recycling waste parts, with a coating made of synthetic resin, especially with a method and plant enabling continuous recycling. 2. Description of the Prior Art Recently, it has become necessary to reuse waste parts made of synthetic resin, for environmental reasons, and it is general to separate waste parts and reuse them as material for new products. It is, furthermore, general to coat products with thermosetting coating to add to the beauty of the products. In the case of liquefying waste parts with a coating, a thermosetting coating is not decomposed. Therefore, material strength is degraded when synthetic resins containing undecomposed coatings are reused. For instance, in a cold district, the material strength of bumpers made of synthetic resins containing undecomposed coatings is lower than that of bumpers made of synthetic resin without the coatings. The degradation of material strength can be avoided if coating is removed, but perfect removal of the coating is too difficult. Although coatings can be mechanically removed by shot blasting etc., it not only takes a long time but is impossible to perfectly remove the coating when parts have complicated shapes. Mechanical removal, therefore, is unsuitable for mass recycling. Although removal of the coating with organic acid has been proposed, it causes environmental pollution. To solve the above-mentioned problem, the present applicant has already proposed a method for recycling synthetic resin parts, that is, the coating thereof is hydrolyzed and kneaded into synthetic resin chips (See EP-A-0 547 249, which belongs to the prior art according to Article 54(3) EPC). To shorten the process time, hydrolysis must be performed under a relatively high temperature atmosphere, but this is unavoidable if the synthetic resin is to liquefy. When hydrolyzed synthetic resin is taken out from the vessel for hydrolyzing after cooling-down, it is impossible to reuse the synthetic resin as raw material without crushing, because it is again solidified. On the other hand, when liquefied synthetic resin is reused as a raw material, it is necessary to keep a flow path of the liquefied synthetic resin at a relatively high temperature, but this requires more energy consumption. SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide a method and plant able to continuously recycle waste parts, with a coating, into raw material for new products without degrading the material strength. According this invention, waste parts made of synthetic resin with a coating are crushed and continuously supplied to a vessel. In this vessel, the coating is continuously hydrolyzed and powdered. Then the powdered coating is kneaded into the synthetic resin, and the kneaded synthetic resin is pelletized as material. BRIEF DESCRIPTION OF THE DRAWINGS Present invention will be more clearly understood from the description set forth below with reference to the accompanying drawings. Fig. 1 is a flow-sheet of continuous regenerating plant for waste parts with coating made of synthetic resin. Fig. 2 is a sectional drawing of a vessel for hydrolyzing. Fig. 3 is a partial enlarged drawing of the vessel for the first embodiment. Fig. 4 is a structural drawing of an isolation wall. Fig. 5 is a sectional drawing of the vessel for the seventh embodiment. Fig. 6 is a sectional drawing of the vessel for the eighth embodiment. Fig. 7 is a sectional drawing of the vessel for the ninth embodiment. Fig. 8 is a sectional drawing of the vessel for the tenth embodiment. Fig. 9 is a sectional drawing of the vessel for the eleventh embodiment. Fig. 10 is a graph showing the result of the Izod impact test. Fig. 11 is a graph showing the result of a low temperature brittleness test. DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 is a flow-sheet of continuous regenerating plant for waste parts with coating made of synthetic resin. A waste part made of synthetic resin is, for example, a bumper 100 made of polypropylene (hereinafter referred to as PP) with a polyester melamine or an acrylic melamine coating on its surface. Note, the synthetic resin is not limited to PP, and it may be allowable that synthetic resin is one kind of thermoplastic resin such as denaturation polypropylene, polyethylene, ABS resin, AS resin, polyamide resin, polyester resin, polycarbonate resin, polyacetal resin, polyphenylene oxide and denaturation polyphenylene oxide. And it may also be allowable that coating is one kind of coating which can be hydrolyzed and decomposed to low molecular weight compound, such as a urethane type or an amino resin type. A crusher 100 consists of a coarse crusher 111 and a fine crusher 112. At first, a bumper 100 with a paint film is crushed to specific sized strips, for example 30 cm length × 5 mm width × 5 mm thick, by the coarse crusher 111, and is further crushed to chips, for example 5 mm × 5 mm × 5 mm cubes, by the fine crusher 112. Chips are supplied to the first quantitative let-off apparatus 120. This consists of a suction fan 12a, a transport pipe 12b, a cyclone 12c, a rotary feeder 12d, a stock bin 12e, a transport screw 12f and a measuring screw 12g. Namely, chips are transported to the cyclone 12c though the transport pipe 12b by suction force of the suction fan 12a. Note, a belt conveyer can be used instead of the transport pipe 12b. Chips stored in the cyclone 12c are transported to the stock bin 12e by the rotary feeder 12d arranged at the bottom of the cyclone 12c. Chips transported to the stock bin 12e are gathered to one side by the transport screw 12f arranged at the bottom of the stock bin 12e, and delivered to an apparatus for hydrolyzing by the measuring screw 12g. This apparatus for hydrolyzing 130 consists of an upstream rotary feeder 131, a vessel 132 and downstream rotary feeder 133. The upstream rotary feeder 131 and the downstream rotary feeder 133 have same construction, and transport chips quantitatively. Namely, a quantity of chips which are supplied from the upstream rotary feeder 131 to the vessel 132, or that which are delivered from the vessel 132 to the downstream rotary feeder 133 can be adjusted by the rotational speed of a rotor. The vessel 132 is used for continuous hydrolyzing of the coating on the chips in steam while the chips are transported from an inlet to an outlet by a screw. The steam conditions for hydrolyzing are not specified, but it is desirable to keep the temperature as high as possible so long as the chips are not liquefied in order to reduce the time for hydrolyzing and to promote easy handling after hydrolyzing, because it is impossible to transport liquefied chips with a screw. Note, it is suitable that chips are hydrolyzed for 0.5 - 2 hours in steam at 160°C, if the synthetic resin is PP. An accelerator for hydrolyzing, such as an acid or, an alkali may be added. After hydrolyzing, each chip has a hydrolyzed and powdered coating around it. Chips transported to an outlet are delivered by concavities 13d of the downstream rotary feeder 133, and supplied to a dryer apparatus 140. The dryer apparatus 140 consists of a dry furnace 141, a rotary feeder 142, a bag filter 143 and suction fan 144. In the dry furnace 141, the moisture contained in the hydrolyzed chips is reduced to below about 0.1% by a hot blast generated from a hot blast furnace (not shown). Wet air is sucked by the suction fan 144, and released to the outside air. Note, the hydrolyzed and powdered coating is caught in the bag filter before being released to the air. Superheated steam may be used to dry the chips instead of the hot blast. In this case, an energy-saving can be accomplished by supplying steam which is released from relief valves arranged on the vessel, dehumidified and superheated, by a dehumidifier and superheater 180, and not using the hot blast furnace. Chips from the bottom of the dry furnace 141 are delivered by the rotary feeder 142, and supplied to the second quantitative let-off apparatus 150. The second quantitative let-off apparatus 150 consists of a suction fan 15a, a transport pipe 15b, a cyclone 15c, a rotary feeder 15d, a stock bin 15e, a transport screw 15f and a measuring screw 15g similar to the first quantitative let-off apparatus 120. This apparatus supplies chips to a kneader 160. The kneader 160 consists of a biaxial kneader 161 and an extruding die 162. The biaxial kneader 161 kneads the hydrolyzed coating, the size thereof being less than twenty or thirty µm, into chips. Kneaded chips are extruded from the extruding die 162 which has holes each thereof, for example 3 mm in diameter, and supplied to a pelletizing apparatus 170. The pelletizing apparatus 170 consists of a water tank for cooling 171 and a cutter 172. The extruded synthetic resin is cooled in the water tank 171 to solidify and the extruded synthetic resin is cut by the cutter 172 into pellets. Fig. 2 shows the cross sectional drawing of the first embodiment of the hydrolysis apparatus 130. Chips supplied from an inlet arranged at the top of the casing 13a of the upstream rotary feeder 131, are quantitatively transported to an outlet arranged at its bottom of it by concavity 13b made on the rotor driven by a motor. The rotor 13b is arranged so as to touch the casing 13a, and it does not allow high-temperature and high-pressure steam to leak from the hydrolyzing vessel 132 to the first quantitative let-off apparatus 120 arranged at the upstream side of the hydrolyzing vessel. The vessel 132 has a hollow shaft 13d along the axis the cylindrical casing 13c. Around the hollow shaft 13d, a screw 13e is arranged so as to transport chips from the inlet 13f and the outlet 13g when the hollow shaft 13d is driven by a motor (not shown). Further, around the hollow shaft 13d, plural exhaust nozzles are arranged. As steam supplied from a steam inlet 13h through the hollow shaft 13d is delivered therefrom, coating on the chips is continuously hydrolyzed and decomposed while chips are transported from the chip inlet 13f to the chip outlet 13g. Temperature and pressure of steam in the vessel 132 is controlled by the relief valve 13j connected to the steam outlet 13i. Further, steam cavities connected to the hollow shaft 13d are arranged at the both side of the vessel 132. Therefore, pressure in two cavities are equal and do not generate a thrust force, to make the thrust bearings simple. Fig. 3 shows an enlarged view of a part (a) in Fig. 2 to explain the second to the sixth embodiments. In the second embodiment, an isolation wall 13m is arranged around the hollow shaft 13d, and a steam chest is constituted between the isolation wall 13m and the hollow shaft 13d uniformly to distribute steam exhausted from the nozzles 13k. To keep the distance from the hollow shaft 13d to the isolation wall 13m, plural cylindrical supporters 13p are arranged at the side of the screw 13e. Further, plural screw supporters 13q for the isolation wall 13m are arranged around the exhaust nozzles 13k. Note, steam flow paths are drilled in these screw supporters 13q. As shown in Fig. 4 in the third embodiment, the isolation wall 13m practically used has a laminated structure which consists of two sheets of punched metal having rather larger nozzle areas m1 and m2, and a sheet of 200 - 600 mesh wire screen m3 put between the two sheets of punched metal. That is, the two sheets of punched metal m1 and m2 support the weight of the chips, and the wire screen m3 protects exhaust nozzles from being plugged by powdered coating which falls into the steam chest. In the fourth embodiment, shaking bars 13n are screwed in the supporters 13q to improve mixing of chips and steam. In the fifth embodiment, areas of the exhaust nozzles on the hollow shaft 13d are proportionally decreased to the downstream of the vessel 132. Hydrolysis, therefore, is accelerated, as more steam is supplied at the upstream side of the vessel 132 than at the downstream side. In the sixth embodiment, areas of the exhaust nozzles are equal, but areas of the steam paths drilled in the screw supporters 13q are proportionally decreased to the downstream. The amount of steam exhausted from the steam paths can be trimmed by replacing the screw supporters 13q. Fig. 5 shows a sectional drawing of the seventh embodiment, and additional steam outlets, for example three outlets i1, i2 and i3, except a main steam outlet 13i at the end of the vessel 13c are arranged. Each additional steam output is connected to an outlet steam header 13r, and three flow control valves s1, s2 and s3 are installed between each additional steam outlet and the outlet steam header 13r. According to the seventh embodiment, more steam may be supplied, because used low energy steam is quickly exhausted. To shorten hydrolyzing time, the temperature of steam supplied to the vessel may be increased but, in this case, the treatment becomes difficult because hydrolyzed chips will tend to solidify as one block. To solve above-mentioned problem, it can be arranged that a part of the casing is constructed as a sink for storing hot water so that hydrolysis is accelerated by increasing the rate of reaction between the paint film and water molecules and then solidification by dead-weight can be avoided because the chips float on hot water. Fig. 6 shows a partial sectional drawing of the eighth embodiment, the vessel 132 is installed on a frame 134 so as the level of the chip inlet side 131 is lower than that of the chip outlet side 133. Hot water 135 can be stored at the chip inlet side 131 of the vessel 132. Fig. 7 shows the sectional drawing of the ninth embodiment where the diameter of the center part of the vessel 13x is formed larger than that of both ends of the vessel 13y and 13z. Hot water, therefore, can be stored in the center part of the vessel 13x. Hydrolysis can be accelerated by installing at least one microwave generator on the casing of the vessel. Fig. 8 shows the sectional drawing of the tenth embodiment with microwave generators 13z1, 13z2 ... 13zn. The paint film on the surface of the synthetic resin chips increases in temperature by absorbing microwaves generated by the microwave generators 13z1, 13z2 ... 13zn, and the hydrolysis of the coating can be accelerated. On the other hand, the synthetic resin chips can not absorb microwaves, so the temperature of the chips does not rise. The temperature in the vessel, therefore, can be maintained rather low while speed of hydrolysis is accelerated . In order to hydrolyze a large amount of chips, it is necessary that volume of the vessel, that is its length and/or diameter, is increased. In this case, however, the following problems must be solved. Increasing of the diameter of the vessel requires increasing the diameter of the screw, but does not cause increasing of an effective volume for hydrolysis. Increasing of the length causes thermal distortion of the vessel and the hollow shaft. Fig. 9 shows the sectional drawing of the eleventh embodiment to solve above-mentioned problem, and this consists of an upstream rotary feeder 131, a hopper 136, a quantitative feeder 137, a main vessel for hydrolysis 132 and a downstream rotary feeder 133. In the eleventh embodiment, the hopper 136 is used as the vessel for preliminary hydrolyzing and the quantitative feeder 137 is arranged upstream of the main vessel 132 to keep the length and/or diameter of the main vessel 132 within reasonable limits. The hollow shaft 13d is commonly used for the quantitative feeder 137 and the main vessel 132, and has plural exhaust nozzles. Steam supplied from a steam inlet 13h and exhausted form nozzles p1, is led to the hopper 136 arranged on the quantitative feeder 137, and coating on the chips stored in the hopper 132 is preliminarily hydrolyzed. In the hopper 136, a level sensor 13m, for example a rotary level sensor, is installed. When the hopper 136 is filled with chips, and the moving of the rotary level sensor 13m is locked by the chips, the rotational speed of the upstream rotary feeder 131 is decreased so that amount stored in the hopper does not increased. Chips in the hopper 132 fall to the quantitative feeder 137 and are transported to the main vessel 132 by a screw e1 driven by a motor (not shown). Note, the diameter of the hollow shaft 13d is proportionally increased to the downstream of the quantitative feeder 133. Diameter of the casing of the main vessel 132 for hydrolyzing is larger than that of the quantitative feeder 137, so that a volume of the chest arranged between the casing 13c and the hollow shaft 13d is increased so that chips are blown by steam. Pelletized synthetic resin made by above-mentioned process can be recycled, for example, as raw material to make bumpers. To understand the characteristics of this pelletized synthetic resin as raw material, Izod impact test and a test for evaluating cold brittleness for test pieces was performed based on Japan Industrial Standards. Note, condition for hydrolysis is following. Temperature 160°C Pressure 5.5 kg/cm 2 Hydrolyzing time 1 Hour Fig. 10 is a graph showing the result of Izod impact test. Abscissa denotes mixing rate of synthetic resin with hydrolyzed coating, and ordinate denotes rate of impact strength of synthetic resin with hydrolyzed coating against that of synthetic resin without hydrolyzed coating. Note, solid line shows the result of Izod impact test at 23°C ambient temperature, and dotted line shows at -30°C. As shown in this graph, impact strength is almost constant regardless of mixing rate of synthetic resin with hydrolyzed coating, and when the bumper is made only from synthetic resin with hydrolyzed coating, its impact strength is not lowered. Fig. 11 is a graph showing the result of test for evaluating cold brittleness. Abscissa denotes mixing rate in the test piece of synthetic resin with hydrolyzed coating, and ordinate denotes rate of brittle temperature of synthetic resin with hydrolyzed coating against that of synthetic resin without hydrolyzed coating. As shown in this graph, brittle temperature is almost constant regardless of mixing rate of synthetic resin with hydrolyzed coating, and when the bumper is made only from synthetic resin with hydrolyzed coating, its brittle temperature is not lowered. Note, rupture elongation, tension strength, flexural strength, modulus of flexural rigidity, hardness and MI value of synthetic resin with hydrolyzed coating are also same as these of synthetic resin without hydrolyzed coating. Moreover, to understand effect of radiation by microwaves, the following test was performed. Synthetic resin PP Temperature 160°C Pressure 5.5 kg/cm 2 Hydrolyzing time 0.5 Hour Brittle temperatures of test piece (A) made from chip not radiated by microwave and test piece made from chip (B) radiated by microwave are evaluated. Test result is shown about rate of brittle temperature of test pieces against brittle temperature of synthetic resin without hydrolyzed coating. Brittle temperatures of test piece (A) -25% Brittle temperatures of test piece (B) -2% As mentioned above, brittle temperature is remains the same as that of synthetic resin without hydrolyzed coating. Waste parts with coating made of synthetic resin, for example bumpers, are crushed into chips. The chips are continuously supplied to a cylindrical vessel by the first let-off apparatus. In this vessel, coating is continuously hydrolyzed and decomposed. After the chips with a powdered coating are dried in a dry furnace, the chips are delivered to the second let-off apparatus, and are kneaded into synthetic resin by a kneader. Kneaded chips are extruded from extruding dies and are pelletized. The pelletized synthetic resin is reused as material for new bumpers.

Claims: A method for continuously recycling waste parts made of synthetic resin with a coating, comprising the steps of: crushing waste parts made of synthetic resin with a coating into chips, quantitatively letting-off said chips by a first let-off apparatus (120), delivering said let-off chips from said first let-off apparatus (120) to an apparatus for hydrolyzing (130), continuously hydrolyzing the coating on said chips in steam in said apparatus for hydrolyzing (130) with a screw, drying said chips with hydrolyzed coating in a dry furnace (141), quantitatively letting-off said dried chips by a second let-off apparatus (150), kneading said chips by a kneader (160), and pelletizing said kneaded chips after cooling into pellets by a pelletizing apparatus (170). A plant for continuously recycling waste parts made of synthetic resin with coating, comprising: a crusher (110) for crushing waste parts made of synthetic resin with a coating into chips, a first let-off apparatus (120) for quantitatively letting-off said synthetic resin waste parts crushed into chips by said crusher, a hydrolyzing apparatus (130) with a screw for continuously hydrolyzing in steam the coating on said chips supplied from said first let-off apparatus, a dry furnace (141) for drying said chips with a hydrolyzed coating, a second let-off apparatus (150) for quantitatively letting-off said chips dried by said dry furnace, a kneader (160) for kneading said chips supplied from said second let-off apparatus, and a pelletizing apparatus (170) for pelletizing said chips kneaded by said kneader after cooling, wherein said hydrolyzing apparatus (130) comprises a cylindrical vessel (132) having a chip inlet, a chip outlet, a steam inlet, a steam outlet, and a screw which transports chips from said chip inlet to said chip outlet, an upstream rotary feeder (131) to keep temperature and pressure of steam in said cylindrical vessel, and a downstream rotary feeder (133) to keep temperature and pressure of steam in said cylindrical vessel. A plant for continuous recycling of waste parts made of synthetic resin with a coating as set forth in claim 2, wherein said dry furnace (140) uses dry steam dehumidified by dehumidifier (180) which dehumidifies steam exhausted from said steam outlet of said cylindrical vessel (132). A plant for continuously, hydrolyzing a coating on waste parts made of synthetic resin, as set forth in claim 2, wherein the vessel (132) comprises a cylindrical casing (13c) and a screw (13e), wherein, a shaft (13d) of said screw (13e) is hollow to distribute steam along an axis of said shaft (13d) in said cylindrical casing (13c) and has plural exhaust nozzles (13k) to exhaust steam. A plant as set forth in claim 4, wherein the vessel (132) comprises an isolation wall (13m) arranged around said shaft (13d) at the specific distance to make a steam chest around said shaft (13d). A plant as set forth in claim 5, wherein the vessel (132) comprises said isolation wall (13m) having a laminated structure which consists of two sheets of punched metal (m1, m2) having rather larger nozzle area which supports the weight of said chips, and one sheet of mesh wire screen (m3) between said two sheets of punched metal (m1, m2) which protects said exhaust nozzles from being plugged by powdered chips. A plant as set forth in claim 4, wherein the vessel (132) comprises plural shaking bars (13n) extending in a radial direction to improve mixing of chips and steam are screwed around said shaft (13d). A plant as set forth in claim 4, wherein the vessel (132) comprises diameters of said plural exhaust nozzles (13k) being proportionally decreased towards the downstream end of said vessel. A plant as set forth in claim 4, wherein the vessel (132) comprises diameters of said plural exhaust nozzles (13k) being equal, and attachments (13s) each of which has a steam path of which diameter is proportionally decreased towards the downstream end of said vessel being screwed into each of said plural exhaust nozzles (13k). A plant as set forth in claim 4, wherein the vessel (132) comprises plural steam outlets (i1, i2,...in) being arranged on the casing of said vessel (132), and steam flow control valves (s1, s2,...sn) to control the flow of steam exhausted from said plural steam outlets being connected to said plural steam outlets. A plant as set forth in claim 4, wherein the vessel (132) comprises a sink for storing hot water being arranged in a part of said vessel. A plant as set forth in claim 11, wherein the vessel (132) comprises said sink being at an inlet side of said vessel, the level thereof being lower than that of the outlet side. A plant as set forth in claim 11, wherein the vessel (132) comprises said sink being a center of said vessel, the diameter thereof being larger than that of both sides. A plant as set forth in claim 4, wherein the vessel (132) comprises at least one microwave generator (13z1, 13z2,...13zn) being arranged along the casing of said vessel (132). A plant for continuous hydrolyzing a paint film on waste parts made of synthetic resin, as set forth in claim 2, wherein the vessel (132) comprises a preliminary hydrolyzing hopper (136) which stores chips, and in which preliminary hydrolysis is performed, a quantitative let-off apparatus (137) which is connected to the bottom of said preliminary hydrolyzing hopper quantitatively to let-off preliminarily hydrolyzed chips, a main vessel, where paint film on chips supplied from said quantitative let-off apparatus (137) is hydrolyzed, wherein, said quantitative let-off apparatus (137) and said main hydrolysis vessel have a common cylindrical casing (13c), and a common screw (13d), volume of a main cavity formed by said common cylindrical casing and said common screw is larger than volume of a quantitative let-off cavity formed by said common cylindrical casing and said common screw.

Inventors: IKEDA SADAO, KITO MAKOTO, TAGUCHI YOSHIO, TANAKA ATSUSHI, IKEDA, SADAO, KITO, MAKOTO, TAGUCHI, YOSHIO, TANAKA, ATSUSHI, Ikeda, Sadao, c/o Toyota Jidosha K.K., Kito, Makoto, c/o Toyota Jidosha K.K., Taguchi, Yoshio, c/o Toyota Jidosha K.K., Tanaka, Atsushi, c/o Toyota Jidosha K.K.
Applicants: TOYOTA MOTOR CO LTD, TOYOTA JIDOSHA KABUSHIKI KAISHA
Application year: 1993
Main classification: B29B17
IPC codes: B29B17, B29B9