POLYMERIC COMPOSITION FOR SOFT POLYPROPYLENE FIBERS

Abstract: A polymeric composition particularly suitable for obtaining heat sealable soft polypropylene fibers comprises a propylene homopolymer modified with a propylene homopolymer having an isotacticity index higher than 80, an ethylene-propylene copolymer insoluble in xylene at 23 DEG C and a propylene copolymer soluble in xylene at 23 DEG C.

Description: POLYMERIC COMPOSITION FOR SOFT POLYPROPYLENE FIBERS The present invention relates to a new polymeric composition, fibers and articles. More particularly, it relates to a polymeric composition for manufacturing heat sealable polypropylene fibers, the fibers obtained from this composition, as well as the manuf ctured articles derived from these fibers . Polypropylene fibers have a wide application in the manufacture of non-woven fabrics (TNT) . The process for the production of these non-woven fabrics is based on the heat sealing capacity of the polypropylene fibers within a temperature range lower than the melting point of polypropylene. In the technology used at the present, the heat sealable fibers go through a carding machine, in which they are partially made parallel to the machine direction and give the so-called card web. The card web is subsequently treated in a calender heated at a temperature comprised between 120 and 150°C. In the calender the fibers subjected to a contemporaneous thermic and pressure treatment, melt partially and weld each other, thus giving the non-woven fabric. In order to avoid an excessive stiffness or a paper appearance of this last, a "spotted" heat seal is obtained owing to the use of an embossed cylinder of the calender (embossed cylinder) , in such a way that the surface of said cylinder useful for the weld is comprised between 10 and 30% of the total surface of the cylinder. The usual applications of the non-woven fabric from polypropylene fibers require a high flexibility and softness; they are in fact sanitary products, such as napkins, sanitary towels, table napkins, bandages, which come in direct contact with the skin. Other applications also, such as the protective packing of soft and precious objects, require a high softness. Obviously, the high softness does not involve an excessive reduction of the toughness (ultimate strength) of the non-woven fabric in the two directions at right angle between them (machine direction M.D. and cross direction CD.) . In order to satisfy the request of a higher softness, it is possible to resort to a reduced draw of the heat sealable fiber which reduce the elastic modulus ("partially drawn" fibers); by this expedient the toughness degree of the non-woven fabric obtained from these fibers is seriously penalized. Patent J 2139469 describes the use of bicomponent fibers, in which the external rind is polyethylene, whereas the inside is polypropylene. By these fibers it is possible to combine a good softness and a good toughness, but the cost of the fiber, because of the complexity of the process and of the apparatus for the manufacture, results very high and equal to about the double as an usual heat sealable polypropylene fiber. It has been also foreseen the use of bicomponent fibers wherein the polypropylene is mixed with polyethylene. EP 260974 describes the use of an amount comprised between 20 and 45% by weight of low density linear polyethylene mixed with polypropylene. In the description of said patent it is stated that with amounts of polyethylene lower than 20% the toughness does not increase and problems arise as to the dimensional stability of the fibres. It has been found by the applicant that a particular type of modifying polymer allows, notwithstanding its low concentration in the basic polypropylene, to obtain very good results as to softness and toughness of the non-woven fabric obtained from the fibers. The compositions of the fibers according to the invention comprises a homopolymer polypropylene of the type used for producing heat sealable fibers and a modifying heterophase polymeric composition comprising: A) from 10 to 60% by weight of a propylene polymer (homopolymer or copolymer) with isotacticity index (percentage by weight of insoluble fraction in hot n- heptane) higher than 80, B) from 3 to 25% by weight of an ethylene- propylene copolymer insoluble in xylene at 23°C, and C) from 15 to 87% by weight of a propylene copolymer soluble in xylene at 23°C, said modifying polymeric composition having a concentration lower than 20% by weight on the total. Owing to the particular composition of the fibers, the softness of these last is remarkably higher in comparison with that of the usual heat sealable fibers from propylene homopolymer. The fibers according to the invention maintain this higher softness also after they have been transformed into non-woven fabric without undergoing particular reductions of the toughness characteristics. The propylene polymer (A) can be either a propylene homopolymer or a copolymer of propylene with another olefin, and it is preferably a homopolymer polypropylene or a propylene-ethylene crystalline copolymer with a content of propylene higher than 85% by w. or a crystalline terpolymer of propylene with ethylene and another alpha-olefin having from 4 to 10 carbon atoms, or mixtures thereof . The copolymer (C) consists of propylene and another olefin, and it is preferably a propylene- ethylene copolymer with an ethylene content comprised between 20 and 60% by weight, or a terpolymer of propylene with ethylene and a diene having an ethylene content comprised between 20 and 60% by weight and a diene content comprised between 0.1 and 10% by weight, or a terpolymer of propylene with ethylene and an alpha-olefin having from 4 to 10 carbon atoms, or a terpolymer of propylene with an alpha-olefin having from 4 to 10 carbon atoms and a diene, or mixtures thereof . The propylene polymer (A) defined as above is present in the heterophasic polymeric composition in a concentration preferably comprised between 20 and 50% by weight (on the total of the modifying polymeric composition) . In the case that the propylene polymer consists of homopolymer polypropylene, the isotacticity index of this last is preferably comprised between 90 and 98. The ethylene-propylene copolymer (B) shows a propylene content preferably comprised between 0.5 and 5% by weight. The propylene copolymer (C) as above defined is present in the modifying polymeric composition in a concentration preferably comprised between 30 and 75% by weight (on the total of the modifying polymeric composition) . Components (A) , (B) and (C) of the modifying polymeric composition added to the homopolymer of propylene usually used for the preparation of heat sealable fibers are preferably prepared by sequential polymerization in two or more steps, using catalysts of the Ziegler-Natta type. The modifying polymeric composition can be also prepared by mechanical mixing of the three components (A) , (B) and (C) , provided that the apparatus used for said mixing has a high homogenizing power. It is also possible to obtain by sequential polymerization a mixture of two of the above mentioned components, and subsequently mechanically mix it with the third component. The Melt Index value of the heterophasic polymeric composition (A)+ (B) + (C) is preferably as much as possible near to that of the propylene homopolymer generally used for the production of fibers. The range of the possible change of the Melt Index is preferably comprised between 5 and 25 g/10' (at 230° Lth a 2.16 kg load) . The optimum weight ratio between the propylene homopolymer generally used in spinning and the modifying polymeric composition consisting of the polymers (A) , (B) and (C) is preferably comprised between 95:5 and 80:20. The polymeric composition for fibers according to the invention allows to not modify in any way the traditional spinning process which uses as raw material a propylene homopolymer. In the process for the formation of the non-woven fabric also, it is not necessary to cause any change in the carding step; in the calender step it is preferable to lower the temperature of 5-10°C. Furthermore it has been surprisingly found that the fibers according to the present invention can be coupled with polyolefinic films with results better than those obtainable with fibers from propylene homopolymer. The manufactured articles consisting of non-woven fabric from polyolefinic fibers coupled with one or more polyolefinic films are widely applied for example as napkins, overalls, protective garments etc. The coupling between the film and the non-woven fabric is performed by means of adhesives, bonding agents or hot melts, with complications as to the process and remarkable cost burden. The heat seal between the non- woven fabric and the polyolefinic film has shown until now problems relating to poor adhesion. It has been observed that the polypropylene fibers according to the present invention, as well as the non-woven fabrics produced from them, are very easily coupled with a polyolefinic film by simple thermic treatment in a calender at temperatures comprised between 100 and 150°C, with a coupling pressure comprised between 20 and 100 kg/linear cm between the two cylinders of the calender (smooth and embossed cylinder) . The best coupling results have been obtained with a polyolefinic film having a substantially identical composition as that of the heterophasic polymeric composition used as modifier of the propylene homopolymer in the manufacture of fibers. In particular, very good results have been obtained using a soft film obtained from a heterophasic polymeric composition comprising: A) from 10 to 60% by weight of a propylene polymer (homopolymer or copolymer) having isotacticity index (percentage by weight of the fraction insoluble in boiling n-heptane) higher than 80, B) from 3 to 25% by weight of an ethylene- propylene copolymer insoluble in xylene at 23°C, and C) from 15 to 87% by weight of a propylene copolymer soluble in xylene at 23°C. It has been observed that the toughness of the composite manufactured article (film + non-woven fabric) thus obtained is higher than the toughness of a composite manufactured article obtainable from homopolymer polypropylene fibers, contrarily to that one could expect when taking into account the higher toughness of the homopolymer fibers in comparison with that of the fibers according to the present invention. Further advantages and characteristics of the present invention will be clear from the examination of the following examples, which have not to be intended as limitative of the scope of the present invention. EXAMPLE 1 A spinning pilot line for polypropylene has been used to produce staple fiber, in separated production cycles, starting from the following materials: 1) Homopolymer polypropylene, having Melt Index = 12 g/10 minutes and isotactic index (fraction by weight insoluble in boiling n-heptane) equal to 96%- Physical form: powder ("flakes") . 2) Blend of: 95% homopolymer polypropylene as the above described; 5% polymeric composition consisting of: 50% (by weight) propylene isotactic homopolymer, having isotacticity index about 96%; 10% ethylene copolymer with about 2% by weight of propylene, insoluble in xylene at room temperature; 40% of ethylene-propylene copolymer, in weight proportion 60/40, completely amorphous and soluble in xylene at room temperature. Melt Index of the composition: 12 g/10' . 3) ■ Blend of: 90% homopolymer polypropylene as above described 10% polymeric composition consisting of : 50% (by weight) propylene-ethylene random copolymer (97.5/2.5) , having isotacticity index 92; 8% ethylene/propylene copolymer (98/2) , insoluble in xylene at room temperature; 42% ethylene/propylene copolymer (50/50) , completely soluble in xylene at room temperature. Melt Index of the composition: 8.5 g/10' . The spinning and finishing conditions have been the following: Spinneret with 1881 holes Extruder temperature: 295°C Head temperature: 300°C Collecting speed: 750 meters/min. Spinning count: 4.1 dtex Drawing ratio: 2.4 Final titre: 2.2-2.3 dtex Crimping: 10 waves/cm Finish: 0.4-0.45 % Cut: 4 cm In three separate production cycles the following results have been obtained. Toughness (g/dtex) Elongation (%) Elasticity modulus (g/dtex) Sticked fibers (%) The three fibers have been used for preparing non-woven fabrics, by passage in the card and subsequently in the calender (pilot apparatus) . One of two cylinder is smooth, the other is embossed, with an embossed drawing of small lozenges. The surface occupied by the embossed drawing was about 20% of the total surface of the cylinder. The calendering conditions have been the following: Temperature of cylinders: 145°/145°C Pressure of cylinders: 50 kg/linear cm Formation speed of non-woven fabric: 70 m/min - Substance of the produced non- woven fabric: 20 g/m 2 Non-woven fabrics having the following characteristics have been obtained: Fiber 1 Fiber 2 Fiber 3 carried out according to UNI 8639 standard **: Weldability index is the square root of the product of the stiffness according to the "Machine Direction" (M.D.) for the stiffness according to the "Cross Direction" (CD.) . ***: The softness is evaluated as the mean of judgments of a taster panel who have a scale of reference values from 1 (stiff) to 5 (very soft) . EXAMPLE 2 In the process for the production of non-woven fabric, it has been worked in such a way to supply contemporarily to the two calendering cylinders the fiber web coming from the card (card web) with average substance equal to 20 g/m 2 , and a soft polypropylene film having a 15 μm thickness. The polypropylene film had been obtained by blown-bubble technology, using a resin having the following composition: A) 30% of ethylene/propylene copolymer, insoluble in xylene at 23°C, containing 1.6% of ethylene; B) 5% of ethylene/propylene copolymer, insoluble in xylene at 23°C and containing about 0.8% of propylene; c) 65% of propylene/ethylene copolymer, soluble in xylene at 23°C, containing 26% of ethylene; Melt Index of the composition: 0.8 g/10' (ASTM D 1238 condition L- 230°C- load 2.16 kg) . The ploug planing of the film and card web has been carried in such a way to bring the film in direct contact with the smooth cylinder, maintained at the temperature of 105°C and the card web in contact with the embossed cylinder, maintained at 125°C The results obtained using the same film and fibers corresponding to cycles 1 and 3 of the Example 1 have been the following: M.D. Stiffness N/5cm CD. Stiffness N/5cm M.D. Ultimate Strength, % 240 83 77 CD. Ultimate Strength, % >400 76 52 Substance (g/m 2 ) 14 30 33 Softness higher for the coupled Film/Fiber 3 Noise lower for the coupled Film/Fiber 3

Claims: CLAIMS : 1. Polymeric composition for the production of polypropylene fibers which comprises polypropylene homopolymer of the type used for the production of heat sealable fibers and a modifying polymeric composition comprising: A) from 10 to 60% by weight of a propylene polymer having isotacticity index (weight percentage of fraction insoluble in boiling n-heptane) higher than 80, B) from 3 to 25% by weight of an ethylene- propylene copolymer insoluble in xylene at 23°C, and C) from 15 to 87% by weight of a propylene copolymer insoluble in xylene at 23°C, said modifying polymeric composition having a concentration lower than 20% by weight of the total. 2. Composition according to claim 1, wherein the propylene polymer (A) is selected from the group consisting of homopolymer polypropylene, propylene- ethylene crystalline copolymer with a propylene content higher than 85% by weight, crystalline terpolymer of propylene with ethylene and with an alpha-olefin having from 4 to 10 carbon atoms or mixtures thereof. 3. Composition according to claim 1 or claim 2, wherein the copolymer (C) is selected from the group consisting of the propylene/ethylene copolymer with an ethylene content comprised between 20 and 60% by weight, terpolymer of propylene with ethylene and with a diene with an ethylene content comprised between 20 and 60% by weight and a diene content comprised between 0.1 and 10% by weight, terpolymer of propylene with ethylene and another alpha-olefin having from 4 to 10 carbon atoms, terpolymer of propylene with an alpha- olefin having 4-10 carbon atoms and with a diene, or mixtures thereof. 4. Composition according to any one of the preceding claims wherein the polypropylene polymer (A) is present in the heterophase polymeric composition in a concentration of 20 to 50% by weight. 5. Composition according to claim 4, wherein the propylene polymer (A) consists of homopolymer polypropylene having an isotacticity index in the range 90 to 98. 6. Composition according to any one of the preceding claims wherein the ethylene-propylene copolymer (B) has a propylene content of 0.5 to 5% by weight. 7. Composition according to any one of the preceding claims wherein the propylene copolymer (C) is present in the heterophase polymeric composition in a concentration of 30 to 75% by weight. 8. Composition according to any one of the preceding claims, wherein the weight ratio between the homopolymer of the type used for the production of heat sealable fibers and the modifying polymeric composition consisting of polymers (A) , (B) and (C) is between 95:5 and 80:20. 9. Polypropylene fibers obtained from a polymeric composition according to any one of the preceding claims. 10. Non-woven fabric based on polypropylene fibers according to claim 9. 11. An article which is coupled non-woven fabric/polyolefinic film, the non-woven fabric comprising polypropylene fibers according to claim 9. 12. Coupled article according to claim 11, wherein the polyolefinic film has a polymeric composition substantially identical with the modifying polymeric composition defined in any one of claims 1 to 9. 13. Coupled article according to claim 11, wherein the polyolefinic film has the following composition: A) from 10 to 60% by weight of a propylene film (homopolymer or copolymer) having isotacticity index (percentage by weight of fraction insoluble in boiling n-heptane) higher than 80, B) from 3 to 25% by weight of an ethylene- propylene copolymer insoluble in xylene at 23°C, and C) from 15 to 87% by weight of a propylene copolymer soluble in xylene at 23°C 14. Polymeric composition, particularly for use as modifier in the production of polypropylene fibers, comprises : A) from 10 to 60% by weight of a propylene polymer having isotacticity index (percentage by weight of fraction insoluble in boiling n-heptane) higher than 80, B) from 3 to 25% by weight of an ethylene- propylene copolymer insoluble in xylene at 23°C, and C) from 15 to 87% by weight of a propylene copolymer insoluble in xylene at 23°C

Inventors: BARSOTTI GIAMPIERO, BARSOTTI, GIAMPIERO
Applicants: MOPLEFAN SPA, MOPLEFAN S.P.A.
Application year: 1993
Main classification: D01F6
IPC codes: B32B27, C08L23, D01F6, D04H1