Organic electroluminescence device

Abstract: An organic electroluminescence device comprises an organic emitting layer 3 and a hole transport layer 4 laminated with each other and arranged between a cathode 1 and an anode 2, is characterised in that the hole transport layer is made of tris-phenothiazinyltriphenylamine or tris-phenoxazinyl-triphenylamine derivative. The hole transport layer has high heat-resistance and high conductivity to improve the durability and emits light at a high luminance and a high efficiency upon application of a low voltage.

Description: The present invention relates to an electroluminescence (EL) device having an emitting layer made of an emitting substance, which utilizes an electroluminescence phenomenon that the emitting substance emits light by applying an electric current to the emitting layer. More particularly, it is concerned with an organic EL device in which the emitting layer is made of an organic emitting substance. As prior art organic EL devices, there have been known an device of two-layer structure having two layers of organic compounds as shown in Fig. 1, in which an organic fluorescent thin film 3 (hereinafter referred as "emitting layer") and an organic hole transport layer 4 are laminated with each other and are arranged between a metal cathode 1 and a transparent anode 2. There have been also known an device of tree-layer structure having three layers of organic compounds as shown in Fig. 2, in which an organic electron transport layer 5, an emitting layer and an organic hole transport layer 4 are laminated in sequence and are sandwiched as a whole between a metal cathode 1 and a transparent anode 2. The hole transport layer 4 facilitates the infusion of the holes from the anode and blocks electrons. The electron transport layer 5 facilitates the infusion of electrons from the cathode. In these organic EL devices, a glass substrate 6 is furnished outside the transparent anode 2. The recombination of electrons infused from the metal cathode 1 and the holes infused from the transparent anode 2 to the emitting layer 3 generates excitons. The excitons emit light when they are deactivated through radiation. This light radiates toward outside through the transparent anode 2 and the glass substrate 6. The conventional organic EL devices constructed as indicated above generally emit light even at a low voltage. However, when the EL device with a simple matrix structure is continuously driven by a DC current, its luminance deterioration probably occurs and then the EL device easily becomes destructible. The heat resistance of such a device is also low. An object of the present invention is to provide an organic EL device with a high heat resistance capable of stably emitting light at a high luminance and a high efficiency for a long time to overcome the above mentioned problem. An organic EL device according to the present invention comprises a cathode, an emitting layer of organic compound, a hole transport layer of organic compound and an anode which are laminated in sequence, wherein said hole transport layer is made of a tris-phenoxazinyl-triphenylamine derivative represented by the following chemical formula (2) where R each independently represents a hydrogen atom, an alkyl group of from 1 to 6 carbon atoms, a halogen group, a cyano group, a nitro group, a primary, secondary or tertiary amino group, an aryl group of from 6 to 14 carbon atoms, an aralkyl group or an alkoxy group. According to the present invention, there is obtained an organic EL device with a high heat resistance capable of stably emitting light at a high luminance and a high efficiency with the durability. Fig. 1 is a schematic diagram showing an organic EL device with two-layer structure; Fig. 2 is a schematic diagram showing an organic EL device with tree-layer structure; and Fig. 3 is a schematic diagram showing an organic EL device shown in Examples 3 and 4 in accordance with the present invention. The embodiments according to the present invention will be described in more detail with reference to the accompanying drawings. The EL device in accordance with the present invention is similar to the organic EL device of the structure shown in Fig. 1 or 2. Such an EL device may have the two-layer structure formed by layering a fluorescent emission layer 3 and a positive-hole transport layer 4 between a pair of a metal cathode 1 and a transparent anode 2 as shown Fig. 1. The EL device also may have the three-layer structure formed by layering an organic electron transport layer 5, the organic fluorescent film 3 and the organic positive-hole transport layer 4 in sequence between a pair of the metal cathode 1 and the transparent anode 2. In the both structures of the EL device, at least one of the electrodes 1 and 2 may be transparent. The cathode 1 is formed of a metal with a lower work function such as aluminum, magnesium, indium, silver or alloys of the individual metals thereof in the thickness range of from about 100 to 5000 angstroms. The transparent anode 2 is formed of an electric conductive material with a higher work function such as indium-tin oxide (ITO) in the thickness range of from about 1000 to 3000 angstroms. Alternatively, the transparent anode 2 may be formed of gold with the thickness of from about 800 to 1500 angstroms. The electrode of gold thin film is semitransparent. The hole transport layer 4 is made of a tris-phenoxazinyl-triphenylamine derivative represented the above mentioned chemical formula (2). Preferred examples of the tris-phenoxazinyl-triphenylamine derivative includes 4, 4', 4" -tri(N-phenoxazinyl) triphenylamine (hereinafter referred as "TPOTA") denoted by the following formula (4): Inventors have produced so-called star-burst molecules which have a stellar structure, e.g. 4, 4', 4" -tris[N-(3-methylphenyl)-N-phenylamino] triphenylamine (hereinafter referred as "MTDATA") and 4, 4', 4" -tris(N,N-diphenylamino) triphenylamine (hereinafter referred as "TDATA") in order to obtain an amorphous molecular material having a photoelectric function. Inventors have studied the morphological changes, electric properties and photoelectric characteristics with respect to these star-burst molecules. Inventors have further synthesized TPOTA by using phenoxazine which is a pi electron conjugate molecules, and studied its various properties and then revealed that this star-burst molecule has a high glass transition point and a high molecular stiffness. TPOTA was synthesized from 4, 4', 4" -triiodo-triphenylamine and phenoxazine through the Ullmann reaction and measured in a differential scanning calorimeter (DSC). In the DSC curve of TPOTA, the glass transition temperature of 145°C from the glass phase to the supercooled phase, the exothermic peak of 176 °C due to the crystallization thereof and the endothermic peak of 341 °C due to melting were measured. Table 1 shows the glass transition temperatures of TDATA, MTDATA and TPOTA. TPOTA has a higher glass transition temperature than TDATA and MTDATA. Samples TDATA MTDATA TPOTA Glass transition temperature Tg(°C ) 83 75 145 It is assumed that the high glass transition points of TPOTA is obtained due to the increase of molecular stiffness of this star-burst molecule caused by linking the outside phenyl groups with chalcogen atoms. This result shows that the glass transition point of the star-burst molecule can be controlled by the change of molecular stiffness thereof. The tris-phenoxazinyl-triphenylamine derivative such as TPOTA has heat-resistant properties of high melting point and glass transition point in the amorphous states respectively. Also, tris-phenoxazinyl-triphenylamine derivative has a twisted molecular structure and three dimensional framework. Thus, these triphenylamine derivatives of star-burst molecule are hardly crystallized and have excellent shielding properties against a surface of another substance. Even when a thin film made of one of such triphenylamine derivatives is left at the temperature lower than room temperature for several months, it is not crystallized. Therefore each triphenylamine derivative film in an amorphous maintains its excellent thin film forming property. These derivatives are capable of being used as the transport layer materials desirable for forming emitting layer 3 thereon. Another preferable example of tris-phenoxazinyl-triphenylamine derivative is 4, 4', 4" -tris(3-methyl-N-phenoxazinyl) triphenylamine denoted by the following formula: The present invention is not restricted to these examples mentioned above. The emitting layer 3 of the organic EL device comprises the organic fluorescent compound. Preferred examples of the compound are Aluminum oxine chelate (hereinafter referred as "Al q3 ) denoted by the following formula 4 and, tetraphenylbutadiene (TPB) derivatives respectively represented by the following chemical formulas 5 to 7, which may include another fluorescent compound as a guest material. The thickness of the emitting layer 3 is within 1 micron meter or less. In addition, other preferred examples used for the emitting layer 3 are represented by the following formulas 8 to 12: In case that the organic EL device has the three-layer structure, the electron transport layer 5 is preferably made of Bu-PBD [2-(4'-tert-butylphenyl)-5-(biphenyl)-1,3,4-oxadiazole] represented by the following chemical formula 13. Examples of suitable organic compounds which may be employed as the electron transport layer 5 are represented by the following chemical formulas 14 to 20. (Example 1) A glass substrate on which an anode of ITO had been formed at 2000Å thick, was prepared. First, TPOTA of formula 2 was deposited on the ITO anode with the thickness of 500 Å as a hole transport layer at the vacuum deposition rate of 4 Å /sec. Next, Al q3 of formula 4 was deposited on the TPOTA layer as an emitting layer with the thickness of 500 Å at the vacuum deposition rate of 5 Å /sec. Then, magnesium and aluminum were vacuum co-deposited on the emitting layer of Al q3 with the thickness of 1500 Å at the atomic ratio of Mg:Ag=10:1 as a cathode. Each of these thin films was formed by a vacuum deposition method at vacuum conditions equal to or less than 1.33 × 10 -3 Pa (1.0 × 10 -5 Torr). When the resultant EL device was operated with the application of the DC voltage 8V at the constant current density of 6.3 mA/cm 2 , the emission of this EL device was luminance of 152 cd/m 2 . Upon application of the DC voltage at the constant current density of 11 mA/cm 2 , the half-life of the initial luminance of this EL device was 370 hours under a vacuum state. There was hardly changed in the current and luminance property before and after the heat-resistance test in which the EL device of example 2 was stored at the temperature of 90°C for 72 hours under a vacuum state. (Example 2) An EL device shown in Fig. 3 was assembled by the same procedure as in the Example 1, except that a second transport layer 4a made of MTDATA at a thickness 500Å was formed between the ITO anode and the TPOTA transport layer whose thickness was 250Å layer. When the resultant EL device was operated with the application of the DC voltage 9V at the constant current density of 6.3 mA/cm 2 , the emission of this EL device was luminance of 218 cd/m 2 . Upon application of the DC voltage at the constant current density of 8.5 mA/cm 2 , the half-life of the initial luminance of this EL device was 530 hours under a vacuum state. In this way, this example EL device having a multilayer of the second transport layer of MTDATA and the TPOTA transport layer has a luminance efficiency higher than that of the example 1 and a long-life luminance. (Comparative example) An EL device was assembled by the same procedure as in the Example 1, except that the transport layer was made of N, N' -diphenyl-N-N'-bis(3-methylphenyl)-1,1'-biphenyl-4,4'-diamine (so-called "TPD") represented by the following chemical formula (21) instead of TPOTA used in the Example 1. When the resultant EL device was operated with the application of the DC voltage 6V at the constant current density of 6.3 mA/cm 2 , the emission of this EL device was luminance of 258 cd/m 2 . Upon application of the DC voltage at the constant current density of 7.5 mA/cm 2 , the half-life of the initial luminance of this EL device was 131 hours under a vacuum state. The current and luminance property largely changed between before and after the same heat-resistance test of example 1, the deterioration of luminance of the EL device was rapid in comparison with Examples mentioned above. As described above, the organic EL device according to the present invention comprises the organic emitting layer and the first organic hole transport layer laminated with each other and arranged between the cathode and the anode, in characterized in that the hole transport layer made of tris-phenoxazinyl-triphenylamine derivative. The hole transport layer has the high heart-resistant property. Thus, the hole transport layer reduces the undesirable influence thereon caused by the heat generated from application of electric current. In this way, it is possible according to the present invention to improve the durability of the organic EL device which emits light at a high luminance and a high efficiency upon application of a low voltage.

Claims: An organic electroluminescence device comprising a cathode, an emitting layer of organic compound, a hole transport layer of organic compound and an anode which are laminated in sequence, wherein said hole transport layer comprises a tris-phenoxazinyl-triphenylamine derivative represented by the following chemical formula where R each independently represents a hydrogen atom, an alkyl group of from 1 to 6 carbon atoms, a halogen group, a cyano group, a nitro group, a primary, secondary or tertiary amino group, an aryl group of from 6 to 14 carbon atoms, an aralkyl group or an alkoxy group. An organic electroluminescence device according to Claim 1, wherein an organic electron transport layer is provided between said cathode and said emitting layer.

Inventors: IMAI KUNIO, INADA HIROSHI, KOBATA TOMOKAZU, SHIROTA YASUHIKO, WAKIMOTO TAKEO, IMAI, KUNIO, INADA, HIROSHI, KOBATA, TOMOKAZU, SHIROTA, YASUHIKO, WAKIMOTO, TAKEO, Imai, Kunio, c/o Corporate R&amp;D Lab., Inada, Hiroshi, c/o Bando Chemical Ind. Ltd., Kobata, Tomokazu, c/o Bando Chemical Ind. Ltd., Wakimoto, Takeo, c/o Corporate R&amp;D Lab.
Applicants: BANDO CHEMICAL IND, PIONEER ELECTRONIC CORP, SHIROTA YASUHIKO, BANDO CHEMICAL INDUSTRIES, LIMITED, PIONEER ELECTRONIC CORPORATION, SHIROTA, YASUHIKO
Application year: 1993
Main classification: H05B33
IPC codes: H05B33, H01L51, C09K11, C07D265, C07D279