Semiconductor laser having an A1GaInP cladding layer

Abstract: A semiconductor laser includes a GaAs substrate, an active layer made of a semiconductor material having a band gap energy smaller than that of GaAs, and a top clad having an AlGaInP cladding layer. An index antiguiding type semiconductor laser is constituted based on the above structure. A top clad includes a base layer formed on the active layer and a protrusion strip for current injection protruding from the base layer and having an AlGaInP cladding layer. An AlGaInP light diffusion layer with an Al proportion smaller than that of the AlGaInP cladding layer and inclusive of zero, is formed on the base layer adjacent to the protrusion strip. The base layer has such a thickness as allows laser oscillation light to leak out to the light diffusion layer.

Description: BACKGROUND OF THE INVENTION The present invention relates to a semiconductor laser usable for pumping an Er-doped quartz optical fiber amplifier and other purposes. The invention also relates to a stripe-type semiconductor laser having a GaAs substrate. An Er-doped quartz optical fiber amplifier now attracts much attention as one of kernel devices and technologies of next generation optical communication systems. A semiconductor laser having a wavelength of 1.48 µm or 0.98 µm is used as a pumping light source for that optical amplifier. There has been proposed a 0.98-µm semiconductor laser which has a GaInAs quantum well active layer and AlGaAs or GaInP cladding layers. In general, to increase the efficiency of introducing laser output power to an optical fiber by elongating a near-field pattern in the vertical direction, a quantum well active layer and optical confinement layers need to be made thinner. However, the thinning of the quantum well active layer and optical confinement layers deteriorates the optical confinement efficiency. As a result, carriers are confined insufficiently, to deteriorate temperature characteristics. Due to the above phenomena inherent in a semiconductor laser, the above-mentioned 0.98-µm semiconductor laser cannot satisfy both of high output power and superior temperature characteristics required for a pumping light source for the Er-doped quartz optical fiber amplifier. Turning to another subject here, we know a 1-µm-band semiconductor laser which uses a silicon oxide film or a silicon nitride film to confine light and current. While this type of conventional semiconductor laser can be manufactured easily, it has a disadvantage of low heat dissipation. In view of the above, semiconductor lasers are now being developed in which light and current are confined by a structure made of only semiconductors. In the case of semiconductor lasers in which the energy of oscillation light is greater than or equal to the band gap energy of GaAs, light can be substantially confined by forming a mesa portion (protrusion strip) in a clad and filling the side regions of the mesa portion with GaAs, where the side portions serve to absorb guided light. However, since this type of structure cannot be employed in 1-µm-band semiconductor lasers, various attempts have been made in those semiconductor lasers. Among those attempts, a technique of filling the side regions of a clad mesa portion with a material whose effective refractive index is smaller than the clad is now being investigated actively, because this type of structure can be produced relatively easily. We will point out two examples below. In the first one, a clad is made of AlGaAs and the side regions of a meas portion is filled with GaInP whose refractive index is smaller than AlGaAs (Chida et al., The 40th Spring Conference of the Japan Society of Applied Physics, Presentation No. 1a-C-2 (1993)). In the second one, a mesa portion including a high-refractivity GaAs layer is formed in a clad made of GaInP, and the side regions of the GaAs layer is filled with GaInP (Sagawa et al., The 40th Spring Conference of the Japan Society of Applied Physics, Presentation No. 31p-C-11 (1993)). The above two techniques employ the real refractive index waveguide structure, in which the side regions of a mesa portion are filled with a low-refractivity material. On the other hand, a red semiconductor laser of an index antiguiding structure has been proposed in which the side regions of a mesa portion of an AlGaInP clad are filled with AlGaInP of a smaller Al proportion (Kidoguchi et al., The Autumn Conference of the Japan Society of Applied Physics, Presentation No. 18a-V-5 (1992)). Since this index antiguiding structure can produce a large difference between thresholds of the fundamental transverse mode and higher order transverse modes, it can readily provide a single transverse mode operation. However, the first conventional technique of Chida et al. has a problem of a small control range of optical confinement, because the clad material is limited to AlGaAs whose refractive index is larger than GaInP as the embedding material. In the second conventional technique of Sagawa et al., the increase of the refractive index difference in the horizontal direction will necessarily be associated with excessive concentration of light in the GaAs layer. Further, while the third conventional technique of Kidoguchi et al. having the index antiguiding structure can readily provide a single transverse mode operation, it requires the AlGaInP light diffusion layer (which buries the mesa portion (protrusion strip)) to have a small Al proportion (Ga/(Al + Ga)) of 0.6. It is difficult to control growth conditions and pre-treatment conditions of the growth of the AlGaInP light diffusion layer. That is, since the quantum well active layer of the semiconductor laser of Kidoguchi et al. is made of GaInP, whose band gap energy is much larger than GaAs, the Al proportion of the clad needs to be increased to effectively confine carriers, necessitating the increase of the Al proportion of the light diffusion layer. IEEE Photonics Technology Letters, vol.4, no.7, July 1992, pages 676-679 discloses a semiconductor laser according to the preamble of claim 1. SUMMARY OF THE INVENTION An object of the present invention is to provide a semiconductor laser having high output power and superior temperature characteristics specifically suitable for use as a pumping light source for an Er-doped optical fiber amplifier. This object is solved by a semiconductor laser having the features of Claim 1. One special embodiment of the invention provides an index antiguiding type semiconductor laser which can confine light and current by a structure made of only semiconductor materials and can easily provide a single transverse mode operation, and which can control optical confinement in both of the vertical and horizontal directions. A carrier (electron) overflow from the active region to the p-type cladding layer is the main factor of a loss occurring in high-current injection. To suppress the carrier overflow, it is effective to increase a barrier height between the quantum well active layer and the cladding layer (i.e., a conduction band discontinuity between GaInAs and AlGaInP). In AlGaInP with an Al proportion of 50%, the conduction band discontinuity is approximately twice that of GaInP. Since AlGaInP (including the case where the Al proportion is zero) of the light diffusion layer has a refractive index larger than that of AlGaInP of the protrusion strip, light tends to diffuse in the horizontal direction. However, because of a gain obtained under the protrusion strip, the light is substantially concentrated in the central region to attain light guidance. Since the degree of light diffusion in the horizontal direction varies with the mode, the transverse mode can be controlled by adjusting the refractive index of the protrusion strip. If the Al proportion (Al/(Al + Ga)) of AlGaInP of the protrusion strip is increased (i.e., the refractive index is decreased) to provide a higher degree of diffusion, the gain becomes insufficient for light guidance. Conversely, if the Al proportion of AlGaInP of the protrusion strip is decreased (i.e., the refractive index is increased) to provide a lower degree of diffusion, higher order transverse modes become likely to occur. A single transverse mode operation is easily established if the Al proportion of the protrusion strip minus that of the light diffusion layer is set in the range of 0.1 to 0.4. Since the light diffusion layer is epitaxially grown from the surface produced by shaping the protrusion strip and is therefore exposed to air, it is difficult to restart growth of AlGaInP. In the invention, since the quantum well active layer is made of a material, for instance, GaInAs, whose band gap energy is smaller than that of GaAs, the Al proportion of AlGaInP of the light diffusion layer can be made sufficiently small. The growth of AlGaInP can be restarted more easily if its Al proportion is smaller. In view of this, it is preferred that the Al proportion of AlGaInP of the light diffusion layer not exceed 0.2. Restarting of the AlGaInP growth of the light diffusion layer is further facilitated by forming, in advance, at least one of a GaAs and GaAsP thin layers which include only one group III element. It is preferred that these layers have a total thickness less than about 50 Å, because if they are too thick the optical confinement in the horizontal direction is deteriorated. Where GaInP is used (that is, the Al proportion of AlGaInP is zero) for the light diffusion layer, it can be grown more easily. The light distribution in the vertical direction can be controlled by changing the composition and thickness of AlGaInP of the base layer of the top clad which AlGaInP has an Al proportion larger than that of the protrusion strip. Further, if the longitudinal ends of the protrusion strip are spaced from the laser facets and the light diffusion layer is extended to fill the regions in between, the light expands in the facet portions to reduce the light density there and, therefore, the deterioration of the laser facets can be suppressed. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-section showing a vertical structure of a semiconductor laser which is not an embodiment of the present invention; Fig. 2 is a cross-section showing an epitaxial wafer used for producing a semiconductor laser according to a first embodiment of the invention; Fig. 3 is a cross-section showing a structure obtained by mesa-etching the epitaxial wafer of Fig. 2; Fig. 4 is a cross-section showing a structure obtained after a light diffusion layer has been formed on the structure of Fig. 3; Fig. 5 is a cross-section showing a structure obtained after a p-type GaAs film has been formed on the structure of Fig. 4; Fig. 6 is a top view showing an arrangement of a protrusion strip; Fig. 7 is a cross-section showing an epitaxial wafer used for producing a semiconductor laser according to a second embodiment of the invention; Fig. 8 is a cross-section showing a structure obtained by mesa-etching the structure of Fig. 7; Fig. 9 is a cross-section showing a structure obtained after a light diffusion layer has been formed on the structure of Fig. 8; Fig. 10 is a cross-section showing a structure obtained after a p-type GaAs film has been formed on the structure of Fig. 9; Fig. 11 is a cross-section showing an epitaxial wafer used for producing a semiconductor laser according to a third embodiment of the invention; Fig. 12 is a cross-section showing an epitaxial wafer used for producing a semiconductor laser according to a fourth embodiment of the invention; and Fig. 13 is a cross-section showing an epitaxial wafer used for producing a semiconductor laser according to a fifth embodiment of the invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS Fig. 1 schematically shows a vertical structure of a semiconductor laser which is not an embodiment of the present invention. Respective epitaxial layers 2-16 are formed on an n-type GaAs substrate 1 by a known metal organic vapor phase epitaxy (MOVPE). Materials and thicknesses of the respective epitaxial layers 2-16 are as follows. Reference numerals 17 and 18 denote a p-side electrode and an n-side electrode, respectively. 1st layer ... n-type GaAs buffer layer 2 of 0.2 µm in thickness 2nd layer ... Si-doped AlGaInP cladding layer 3 (x = Al/(Al + Ga) = 0.7, n = 2 × 10 18 cm -3 ) of 1.5 µm in thickness 3rd layer ... Undoped AlGaInP cladding layer 4 (x = 0.1) of 100 Å (1nm=10Å) in thickness 4th layer ... Undoped GaInAsP optical confinement layer 5 (Eg ≃ 1.7 eV) of 100 Å in thickness 5th layer ... Undoped GaAs layer 6 of 100 Å in thickness 6th layer ... Undoped GaInAs quantum well active layer 7 of 40 Å in thickness 7th layer ... Undoped GaAs layer 8 of 100 Å in thickness 8th layer ... Undoped GaInAsP optical confinement layer 9 (Eg = 1.7 eV) of 100 Å in thickness 9th layer ... Undoped AlGaInP cladding layer 10 (x = 0.1) of 100 Å in thickness 10th layer ... Zn-doped AlGaInP cladding layer 11 (x = 0.7, p = 5 × 10 17 cm -3 ) of 0.4 µm in thickness 11th layer ... Zn-doped GaAs etching stopper layer 12 of 100 Å in thickness 12th layer ... Zn-doped AlGaInP cladding layer 13 (x = 0.7, p = 5 × 10 17 cm -3 ) of 1.1 µm in thickness 13th layer ... Zn-doped AlGaInP buffer layer 14 (x = 0.1) of 200 Å in thickness 14th layer ... Zn-doped GaAs contact layer 15 (p = 1 × 10 19 cm -3 ) of 0.5 µm in thickness As mentioned above, the values x of the AlGaInP layers 3, 4, 10, 11, 13 and 14 are composition ratios of Al to (Al + Ga). In this embodiment, AlGaInP of the respective layers is substantially lattice-matched with GaAs. We will describe several points to be considered in conducting the epitaxial growth. To obtain high crystalline quality, it is preferred that the AlGaInP layers 3, 4, 10, 11, 13 and 14 be grown at temperatures about 50°C higher than the GaInP layers. In this embodiment, for example, the n-type AlGaInP layer 3 is grown at 760°C, and the p-type AlGaInP layers 11, 13 and 14 are grown at 740°C. The flow rate of diethylzinc, which is a material gas of Zn as the p-type dopant, is set at the same level as in the case of forming the Zn-doped GaAs contact layer 15. In this semiconductor laser, since GaInAs is used for the quantum well active layer and AlGaInP is used for the cladding layers, a large difference can be obtained between the band gap energies of the quantum well active layer and the cladding layers. As a result, a large electron energy level difference is produced, and electrons are less likely to escape from the quantum well active layer, which means that the electron-hole recombination is effectively performed in the quantum well active layer. Thus, this semiconductor laser can produce a sufficiently high output power suitable for a pumping light source for an Er-doped quartz optical fiber amplifier without deteriorating temperature characteristics. Semiconductor lasers according to a first embodiment of the invention will be described below. In a semiconductor laser according to a special embodiment, an epitaxial wafer 116 having a multilayered structure of Fig. 2 is formed by a reduced pressure MOVPE at about 60 Torr. An n-type GaAs buffer layer 102, an n-type AlGaInP cladding layer 103, an active region 115, a p-type AlGaInP cladding layer 111, a p-type GaInP etching stopper layer 112, a p-type AlGaInP cladding layer 113 and a p-type GaInP cap layer 114 are sequentially formed on a GaAs substrate 101 by epitaxial growth. The active region 115 consists of a GaInP cladding layer 104, a GaInAsP optical confinement layer 105, a GaAs layer 106, a GaInAs quantum well layer 107, a GaAs layer 108, a GaInAsP optical confinement layer 109 and a GaInP cladding layer 110. The p-type AlGaInP cladding layer 111, p-type GaInP etching stopper layer 112, p-type AlGaInP cladding layer 113 and p-type GaInP cap layer constitutes a top clad. The p-type AlGaInP cladding layer 113 is shaped, by subsequent etching, into a protrusion strip that is coextensive and parallel with a current-injecting portion of the quantum well active layer. Thicknesses, kinds and concentrations of dopants of the respective epitaxial layers are indicated in Fig. 2. Also shown in the left part of Fig. 2 is a variation of the temperature during the epitaxial growth. It is desired that AlGaInP for the clads be grown at a higher temperature, and that GaInAs for the quantum well active layer be grown at a lower temperature. In this embodiment, as shown in Fig. 2, the active region 115 is grown at 650°C and the bottom and top clads are grown at 720-740°C. Then, unnecessary portions of the GaInP cap layer 114 and the AlGaInP cladding layer 113 of the thus formed epitaxial wafer 116 are removed by etching. First, a 0.1-µm-thick silicon nitride film is deposited on the entire surface, and patterned by a lithography technique to leave a 4-µm-wide bandlike portion 120. Then, the GaInP cap layer 114 and the AlGaInP cladding layer 113 are etched using the silicon nitride film 120 as a mask (see Fig. 3). More specifically, first, the GaInP cap layer 114 and a very surface portion of the AlGaInP cladding layer 113 are etched out by a mixture at 50°C of sulfuric acid, hydrogen peroxide and water which are mixed at a ratio of 3:1:1. Then, the AlGaInP cladding layer 113 is etched by concentrated sulfuric acid of 60°C until the color of the wafer surface changes, which means exposure of the GaInP etching stopper layer 112. Thus, a protrusion strip 121 of the top clad is formed as shown in Fig. 3. Then, as shown in Fig. 4, a light diffusion layer 132 of n-type GaInP is formed so as to occupy both sides of the protrusion strip 121. A GaAs layer 130 and a GaAsP layer 131 are formed prior to the formation of the light diffusion layer 132. As a result of exposure to air, the wafer surface is rough at the time of restarting growth of the light diffusion layer 132. In particular, where the surface material includes two or more group III elements, the surface condition is bad, i.e., not suitable for the growth of the light-diffusion layer 132. The GaAs layer 130 and the GaAsP layer 131 serve to facilitate the growth of the light diffusion layer 132. The total thickness of the layers 130 and 131 should be less than about 50 Å, because if they are two thick, they will adversely affect the optical confinement in the horizontal direction. In this embodiment, the GaAs layer 130 is 30-Å thick and the GaAsP layer 131 is 10-Å thick. The composition of the GaAsP layer 130 need not be selected strictly. At 650°C, the mole ratio between arsine and phosphine may be set at about 0.1 and the mole ratio between the group V elements and the group III element may be set at about 70. The temperature should be raised in a phosphine atmosphere. Being of an n-type, the light diffusion layer 132 also serves as a current blocking layer. Next, the silicon nitride film 120 is etched out by a solution of hydrofluoric acid and water (1:1), and a p-type GaAs film 140 is formed to have a thickness of 2 µm. A p-side electrode 141 is evaporated onto the p-type GaAs film 140. After the GaAs substrate 101 is thinned to about 100 µm, an n-side electrode 142 is evaporated onto it. After the electrodes 141 and 142 are alloyed with the adjacent layers by annealing, cleaving and mounting steps are performed to complete a semiconductor laser (see Fig. 5). The optical confinement in both of the vertical and horizontal directions can be controlled by changing the thickness and composition (distribution) of a base layer of the top clad, i.e., the AlGaInP cladding layer 111 in this embodiment. Although in this embodiment the mesa shape of the protrusion strip 121 is an ordinary one (the top is narrower than the bottom), it may be a reversed one, in which case the stripe width can be reduced. Fig. 6 is a top view corresponding to Fig. 5, and shows how the protrusion strip 121 is arranged on a chip as cut out. As shown in Fig. 6, ends 121a and 121b of the protrusion strip 121 are separated from facets 152 and 153. The light diffusion layer also fills the regions between the end 121a and the facet 152 and between the end 121b and the facet 153 in the same manner as in the lateral sides of the protrusion strip 121. It is preferred that distances d between the end 121a and facet 152 and between the end 121b and the facet 153 be about 20 µm. Base layers of the top clad, i.e., the p-type AlGaInP cladding layer 111 and the p-type GaInP etching stopper layer 112 extend to the facets 152 and 153. Since the above facet structure causes light diffusion in the vicinity of the facets, the light density can be reduced there. A sudden failure may occur in semiconductor lasers having a GalnAs quantum well active layer. The sudden failure is caused by fusion of a facet, which is called a catastrophic optical damage (COD) and is considered as originating from an interaction between light and current at a facet portion. If the light density is reduced at the facet portions by using the facet structure of this embodiment, the COD will hardly occur to improve the reliability of the semiconductor laser. In this embodiment, the above structure is employed in both facet portions. Where coatings of different reflectances are applied to the respective facets, the above structure may be employed only for the lower-reflectance-side facet, in which case the protrusion strip 121 is extended to the facet on the higher reflectance side. Fig. 7 shows a multilayered structure of an epitaxial wafer to be used for producing a semiconductor laser according to a second embodiment of the invention. The second embodiment is different from the first embodiment in that the light diffusion layer uses, instead of GaInP, AlGaInP whose refractive index is larger than AlGaInP of the protrusion strip. To this end, as shown in Fig. 7, the AlGaInP cladding layers 103 and 113 of the epitaxial wafer 116 of the first embodiment are replaced by AlGaInP layers 103' and 113' having a large Al proportion to constitute an epitaxial wafer 116'. The procedure of forming the epitaxial wafer 116' is basically the same as in the first embodiment. In the second embodiment, the temperature in forming the top clad is a little higher than in the first embodiment (see Fig. 7). After the formation of the epitaxial wafer 116', a protrusion strip 121' is formed by etching as shown in Fig. 8, and then a light diffusion layer 170 is formed as shown in Fig. 9 which is made of n-type AlGaInP having an Al proportion (Al/(Al + Ga)) of 0.2. Although in this embodiment the light diffusion layer 170 is formed directly on the etching stopper layer 112, to facilitate the epitaxial growth the GaAs layer 130 and the GaAsP layer 131 may be formed in advance as in the case of the first embodiment. Then, as in the case of the first embodiment, the p-type GaAs film 140 and the electrodes 141 and 142 are formed, and a chip is cut out to complete a semiconductor laser (see Fig. 10). Figs. 11-13 show epitaxial wafers according to third to fifth embodiments, which are alternatives to the epitaxial wafer 116 of Fig. 2. In the third embodiment of Fig. 11, an etching stopper layer of GaAs is employed instead of the etching stopper layer 112 of GaInP of the first embodiment. This change provides larger selection ranges to contribute to stabilization of the manufacturing process. In this embodiment, for instance, a room temperature solution of hydrochloric acid, phosphoric acid and water (22:11:17) may be used as an etchant. In the fourth embodiment of Fig. 12, an n-side (top) clad and a p-side (bottom) clad are made approximately symmetrical. Even in the first embodiment, the light distributions on the n and p sides can be made identical by adjusting the thickness of the AlGaInP cladding layer 111 and other factors. It is apparent that the epitaxial wafer of the fourth embodiment can equalize the n-side and p-side light distributions more easily. In the fifth embodiment of Fig. 13, the Al proportion (Al/(Al + Ga)) of a base layer of the top clad is set the same as that of a protrusion strip, to make the large part of the clad have the same composition. This will facilitate the epitaxial growth. As described above, the semiconductor lasers according to the first to fifth embodiments exhibit good heat dissipation performance because they confine light and current by a structure made of only semiconductor materials. The single transverse mode operation can easily be obtained by virtue of the index antiguiding structure. By changing the thickness and composition of the AlGaInP base layer of the top clad having an Al proportion smaller than that of AlGaInP of the protrusion strip, the optical confinement in both of the vertical and horizontal directions can be controlled.

Claims: A semiconductor laser comprising: a GaAs substrate; an active region (115) comprising a quantum well active layer (7,107) having a band gap smaller than that of GaAs; and a top clad comprising a p-type first cladding layer (111) located on top of said active region (115), and substantially lattice-matched with said GaAs substrate, characterized in that said first cladding layer (111) is made of (Al x Ga 1-x ) 0.5 In 0.5 P (0.5 ≤ x ≤ 1), and said semiconductor laser further comprises a protrusion strip (121) for current injection located over said first cladding layer (111) comprising a second cladding layer (113) of (Al y Ga 1-y ) 0.5 In 0.5 P (0 < y < x) having an Al proportion y smaller than said Al proportion x of said first cladding layer (111), and a light diffusion layer (132) of (Al z Ga 1-z ) 0.5 In 0.5 P (0 ≤ z < y) formed on said first cladding layer (111) adjacent to said protrusion strip (121), said light diffusion layer (132) having an Al proportion z smaller than said Al proportion y of said second cladding layer (113) and including zero, wherein said first cladding layer (111) has such a thickness as to allow laser oscillation light to leak out to the light diffusion layer (132) in order to form an index anti-guiding type semiconductor laser. A semiconductor laser according to claim 1, wherein said Al proportion y of said second cladding layer (113) minus said Al proportion z of said light diffusion layer is in a range of 0.1 to 0.4. A semiconductor laser according to claim 2, wherein said Al proportion z of the light diffusion layer (132) is not more than 0.2. A semiconductor laser according to claim 1, further comprising at least one of GaAs layer (130) and a GaAsP layer (131) between said light diffusion layer (132) and said first cladding layer (111) and between said light diffusion layer (132) and said protrusion strip (121). A semiconductor laser according to claim 1, wherein the longitudinal end surfaces (121a,121b) of the protrusion strip (121), which are parallel to the laser facets (152,153), are spaced from the respective laser facets (152,153), and the light diffusion layer (132) extends to fill regions between the longitudinal end surfaces (121a,121b) of the protrusion strip (121) and the laser facets (152,153).

Inventors: HASHIMOTO JUN-ICHI, KATSUYAMA TSUKURU, YOSHIDA ICHIRO, HASHIMOTO, JUN-ICHI, KATSUYAMA, TSUKURU, YOSHIDA, ICHIRO, HASHIMOTO, JUN-ICHI, C/O YOKOHAMA WORKS OF, KATSUYAMA, TSUKURU, C/O YOKOHAMA WORKS OF, YOSHIDA, ICHIRO, C/O YOKOHAMA WORKS OF
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LIMITED
Application year: 1993
Main classification: H01S3
IPC codes: H01S5