METHOD FOR THE TREATMENT OF INCINERATION RESIDUES AND THE USE THEREOF AS ADSORPTION AGENT

Abstract: The invention relates to a method for the treatment of incineration residues which are produced, for example, in the incineration of domestic waste, in which method said residues are treated with gas containing CO2. In the treatment, microorganisms may be used which are already present naturally in the incineration residues or can be added thereto. The invention furthermore relates to the use of incineration residues as absorption material for the removal of CO2 from exhaust gases.

Description: Method for the treatment of incineration residues and the use thereof as adsorption agent The invention relates to a method for the treatment of incineration residues. It is known that slags which are released in the incineration of waste, in particular of domestic waste and waste comparable thereto, are usable as foundation material and embankment material in road construction and as gravel substitute in concrete (C.R.O.W. (1988): Residues are (no longer) waste - IP slags. Publication 15, Stichting C.R.O.W., Ede [1]; Leenders, P. (1984)- Management of Solid Waste Incinerator Residues in The Netherlands. In: K.J. Thome-Kozmiensky (ed.): Recycling International, Vol. 2, p. 1420-1441. EF-Verlag, Berlin [2]). This material, referred to as WIP slags for short, serves to fulfil certain civil-engineering and environmental-hygiene quality requirements, depending on the field of application. The environmental- hygiene quality requirements can be subdivided into requirements relating to the composition and requirements relating to the leachability of the product. As far as the territory of the Netherlands is concerned, these environmental-hygiene quality requirements will be laid down in the so- called Building Materials Order, a General Order in Council (AMVB) within the framework of the Soil Protection Act. In said AMVB, a draft of which has been published, the stress is placed on the quality requirements relating to leaching. Of the civil engineering quality requirements which are imposed on applications as foundation material [1], in particular, the requirements which are imposed on unincinerated and digestible material are relevant within this framework. For applications as gravel substitute in concrete, the pH is also important. In order to meet the requirements of the Building Materials Order, it is necessary to suppress the leaching of heavy metals from WIP slags. Such processes, generally referred to as immobilization processes, are generally known and are subdivided into physico-chemical and thermal processes. The object of physico-chemical processes is to produce a hard, low-porosity and durable matrix by using binders and other aggregates and at the same time fix impurities in the form of sparingly soluble compounds. The formation of a hard matrix according to known methods, in which, for example, use is made of a binder is in general not a problem. According to leaching tests, however, in many cases no chemical binding of the impurities occurs. After reduction of the matrix, the leaching is often again at the level of the starting material. Another weak point of the present physico-chemical immobilization processes is the use of relatively large amounts (typically 10-502 on a weight basis) of expensive aggregates such as cement. The object of thermal processes is to incorporate impurities in a silicate matrix by means of sintering or melting of the material. From tests it is found that the impurities are often fixed well. A disadvantage of the process is that the costs are high as a consequence of the high investment and the considerable energy consumption. A method of the type described in the introduction has now been found which is characterized in that the residues are treated with gas containing 0.1 to 100^ by volume of C0 2 , preferably at a temperature from the ambient temperature up to 200"C under a pressure from atmospheric pressure up to 10 bar. The content of C0 2 is higher than the content in the atmosphere. The method can be carried out at ambient temperature (approximately 0-30°C) and atmospheric pressure (approximately 1 bar). Increasing pressure and temperature results, however, in an acceleration of the reactions. Good results have been obtained with gas having C0 2 contents of at least 1, for example, approximately 5 _ 20, in particular approximately 8% by volume, a temperature of at most 100°C, for example approximately 20-70°C, more particularly approximately 20-50°C and an overpressure of at most 1 atmosphere. The present method has similarities to the known physico- chemical immobilization processes, but differs therefrom in the respect that no hard matrix is formed. Another difference is that use is also made of microbiological reactions. The method is therefore to be described as a chemical immobilization process whose efficiency is increased by microbiological conversions. The existing immobilization processes are characterized by an inadequate fixing of impurities and/or a relatively high cost level, as a result of which treatment of residues produced in bulk amounts is virtually impracticable. The reaction of C0 2 with the basic WIP slag results in the formation of carbonates and a (re)carbonating process is therefore involved. Not only the formation of carbonates, however, is important for the fixing of heavy metals and metalloids, it is also important the pH of the material is modified in such a way that the solubility of the components concerned is minimal. This pH control is, moreover, important for the optimization of microbiological reactions. Most microorganisms (particularly bacteria) cannot grow at the strongly basic pH value which the untreated WIP slags may have. A decrease in the pH to slightly basic values, for example 7-8.5 increases not only the usability of the slags as aggregates for concrete and the like, but also the possibilities for the growth of microorganisms to a considerable extent. Additionally, the activity of microorganisms can be improved by adding nutrients and inoculation with microorganisms (such as bacterial and mould cultures) . The favourable action of the microorganisms is based on the degradation of unincinerated organic material and nitrogen, for example materials containing ammonium groups. Apart from the contribution of these substances as such to the leaching, they also play a role in the leaching of metals. Both organic substances (acids, humic materials and the like) and ammonium groups may form metal complexes. An important effect of the treatment is that the civil- engineering quality of the slag is also appreciably improved. By lowering the pH, the risk of destructive expansion, such as the conversion of pieces of metallic aluminium to aluminium hydroxide, becomes appreciably lower. Furthermore, the material becomes much more suitable for use as a gravel substitute in concrete. No particular requirements are imposed on the C0 2 to be used and the gas mixture containing the C0 2 , except that the gas mixture preferably contains oxygen and is saturated with water. The oxygen is necessary for the microbiological reactions to proceed. Use of water vapour serves to prevent the slag from drying out. The microorganisms may be inhibited or even die owing to lack of water. The C0 2 can be obtained from a supplier and diluted with air. A (purified) flue gas or off-gas from a biological process is, however, also suitable as C0 2 source. A requirement which has to be imposed on these gas mixtures is that the impurity which may be present in the gas must not be such that the quality of the slag decreases significantly by means of adsorption processes. If off-gases are used as C0 2 source, the treatment makes a direct contribution to the reduction of the C0 2 emission. In this variant, the method is therefore to be regarded as a C0 2 removal process. The WIP slags may in this case be regarded as an adsorbent, which is a new application for this material. The time for which the slags have to be treated with C0 2 -rich gas is dependent on the process conditions which are applied (pressure, temperature, C0 2 content). This time varies from one hour (at increased pressure and temperature) to approximately 8 weeks. Under a pressure of approximately 1 atmosphere and at a temperature of approximately 20°C, a dwell time of two to four weeks will in general be adequate. As stated, the pressure varies in general between atmospheric pressure and 10 bar overpressure. In a typical embodiment of the process in which microorganisms are used, an overpressure of 0.01-0.1 bar is employed. A possible device in which the method according to the invention can be carried out is shown diagrammatically in Figure 1. In this figure: 1 is the feed line for a C0 2 -rich gas mixture; 2 are perforated tubes; 3 is a layer of gravel and coarse sand or comparable material in which the perforated tubes are imbedded; 4 is a perforated floor suitable for vehicles; 5 is a layer of WIP slags having a thickness of 0.5-5 π; 6 is a concrete tank which can be sealed at the top with, for example, canvas. The C0 2 -rich gas flows upwards through the slag layer via the distribution system formed by 2 and 3- I escapes at the top of the slag layer and, depending on the composition, it will then be recirculated, discharged directly, discharged via a filter or used as incineration air for a furnace. Depending on the extent of the slag stream to be treated, the concrete tank should be divided into sections. For semicontinuous operation, a minimum of two sections should always be present and alternately, material is being treated in one section or the section is being emptied, while the other section is being filled. During the filling of the sections and during the treatment, inoculation material and nutrients can be added if desired. A continuous operation is possible as a result of making use of horizontally arranged drums with which the slag is conveyed with the aid of a rotating movement. The C0 2 -rich gas is blown through the drum. An alternative is to use a vertically arranged silo which is filled at the top and is emptied at the bottom. The C0 2 -rich gas is blown upwards through the silo. Since the use of large volumes of C0 2 -rich gas is characteristic of the process, usable gas flows are considered in greater detail in Figures 2 and 3- An adequately purified flue gas, for example a flue gas which meets the requirements of the Dutch "1989 incineration directive" can be used as C0 2 source. In Figure 2, this gas flow is indicated by ~ . In Figure 2, the reference numerals furthermore denote: 8 - a compressor; 9 - a heat exchanger (optional, only necessary if the temperature of the flue gas is too high) ; 10 - the slag treatment unit (in accordance with Figure 1); 11 - a recirculation flow; 12 - the return flow of the used flue gas; 13 - an alternative for 12, in which the used flue gas is fed as incineration air to furnace 14; 15 - a kettle; 16 - a flue gas purification system; 16a - a chimney. The relative merit of removal of the gas via 12 or 13 is primarily a technical/economic question and may vary for each installation. If impermissible amounts of volatile impurities were to be released from the slags, removal via 13 would be necessary. In both case, the gas flow of the slag treatment unit can be completely integrated in the gas flow through the WIP. If the quality of the flue gas produced by the WIP is inadequate and no other clean, C0 2 -rich off-gas flow is available, a C0 2 - rich gas flow can be created by mixing C0 2 (industrial quality) with air. Possibly, 100% by volume of C0 2 can also be used as gas flow. The C0 2 can be obtained from a gas supplier or separated from the flue gas on site. The alternative in which pure C0 2 is used is shown diagrammatically in Figure 3- Here: 17 is the feedstock vessel containing C0 2 ; 18 is a gas mixing plant in which C0 2 and air are mixed; 19 is the feed line for the C0 2 -rich gas; 10 is the slag treatment unit (according to Figure 1); 13 is the outlet of gas to the furnace 14. This outlet would only be necessary if unacceptable amounts of volatile impurities were to be released from the slag. Otherwise direct discharge of the off-gas (if necessary via a simple biofilter) is possible. In addition to the arrangement shown in Figure 1 for batchwise performance of the process, the method according to the invention can be carried out continuously by bringing the residue to be treated into contact with C0 2 -rich gas in a mixing drum, silo or comparable processing apparatus. From the above description it will clear that the method can be used either with or without added microorganisms. In the typical performance of the process, however, microorganisms are used. It is pointed out that microorganisms may already present naturally in the material to be treated. It is, however, also possible to "inoculate" the material to be treated with material which has already undergone a treatment and which contains microorganisms. These microorganisms generally consume oxygen. Whether or not microorganisms are used or are present is decisive for the conditions to be chosen in the method according to the invention. Thus, the presence of water is essential if microorganisms are used and a gas containing water vapour will preferably be used, preferably gas which contains not only carbon dioxide in the above entioned amounts but is also saturated with water vapour. If microorganisms are used, the temperature will in general not be higher than approximately 70°C. Work will be carried out under the abovementioned slight overpressure of not more than 1 bar. If work is carried out without using microorganisms, the temperature may, however, be 200°C or higher, for example 300°C or θO°C, but the latter are generally rejected for practical reasons. The presence of water vapour may be advantageous, but is not required. It is also true of the pressure that extreme conditions can be used, and a pressure of 3 or 4 bar may be desirable, but pressures of 10, 20 or 50 bars may also, however, be used but at the same time the higher pressures are often undesirable for practical reasons. It is obvious that the incineration residues which can be treated according to the method of the invention are preferably present in finely divided form, for example in the form of particles having a size in the range of 0- cm. As has already been stated above, incineration residues can also be used for the removal of C0 2 from C0 2 -rich off-gases. The invention therefore also relates to the use of incineration residues as absorption material for the removal of C0 2 from C0 2 -rich off-gases, such as flue gases, biogas, disposal-site gas or off-gas from composting plants. It is pointed out that the present invention was based on the discovery that advantageous C0 2 absorption by incineration residues takes place. Both the method described above for the treatment of incineration residues and the use of untreated residues for absorption purposes therefore fulfil the essence of the invention. Within the scope of the above description, incineration residues are understood as meaning solid residues which are formed in the incineration of waste substances in furnaces. In this connection, a distinction is to be made between slags, relatively coarse ingredients which remain behind in the furnace, and fly ashes, fine constituents which escape with the flue gases and are collected in electrostatic filters. After slaking, the slags often undergo a final processing in the form of removal of iron and crushing and/or removal by sieving of coarse constituents. This results in a grading of, for example, 0-4 cm. Example 1 A test arrangement on a laboratory scale was employed. An amount of WIP slags of approximately 1 kg was contained in a column having a height of 0.5 - * *• Air (the reference) or C0 2 -enriched air (approximately 8% by volume) flowed upwards through this column. The gas flow rate was set a ~~ 1/hour, the temperature was approximately 2 ° C and the overpressure approximately 0.1 bar. The treatment was continued for 10 weeks. The leaching of the slag was determined before and after the treatment with the aid of a shaking test. The material was shaken for 23 hours with demineralized water (acidified with nitric acid to a pH of 4), with a liquid/solid (L/S) ratio of 10 (method in accordance with NEN 7343). From Table 1 is becomes clear that the leaching concentrations of the most important heavy metals have fallen under both conditions, but that the effect is appreciably increased by adding C0 2 . Thus, it holds true for copper that the decrease is 842 with an increased C0 2 concentration, compared with ~ Z% when air is passed. The decrease in the molybdenum leaching increases from 572 to 8l#. Without C0 2 being added, the aluminium leaching increases somewhat (+ ' %) but with C0 2 the aluminium leaching falls by 92- The treatment is not efficient for antimony and zinc. The increase in the zinc concentration is, however, not alarming. It is also clear that the pH falls appreciably (to approximately 8), and this is beneficial for the civil-engineering quality. Example 2 At the end of the experiment described in Example 1, the bacterial and mould counts of the material were determined. For this purpose, dilution series were made of the shaking liquid obtained by shaking for 23 hours with L/S 10. These dilutions were applied to PCA plates and maltose-agar plates. The number of colonies on these plates was counted after 2 (PCA) or 3 (maltose-agar) days. From the results (see Table 2) it is evident that a beneficial environment has been produced for bacteria as a result of treatment with C0 2 . Bacteria are not detectable in the reference column. A more diverse microflora is beneficial for the degradation of residual (unincinerated) organic matter. The development of a bacteria population is in agreement with the observed greater decrease in the COD leaching (see Table 1) of the material which has been treated with additional C0 2 . Example ~ * This test has been carried out in accordance with the methods described in Example 1. Because samples were collected from the column every two weeks, a picture was obtained of the variation with time. This variation is shown in Figure 4. From this it is evident that most of the decrease in the copper and molybdenum leaching of the WIP slag is achieved within a treatment time of two weeks. Depending on the initial quality of the slag (type of impurity and concentrations) and the required final quality level, a dwell time of two weeks or possibly shorter is adequate. In some situations, a longer dwell time will be necessary. Example 4 In this experiment slags have been treated for one hour with a C0 2 /air mixture at an increased pressure (3-5 bar) and temperature (150°C). At the beginning of the test, the gas mixture contained approximately 302 by volume of C0 2 . The quality of the slag before and after the experiment has been determined by the leaching test described in Example 1. The results of this experiment are shown in Table 3- From this table it becomes evident that the abovementioned treatment results in an appreciable reduction (an order of magnitude of 502 or more) in the leaching of copper, lead and aluminium. The leaching of the important component molybdenum (in this example) increases. This method of treatment is therefore only suitable for slags whose molybdenum leaching is not of substantial importance. Table 1: Effect of treatment with CO ^ -rich gas on the leaching of WIP slags. Leaching concentrations after 23 hours shaking with de ineralized water, with liquid/solid ratio 10 (method in h Ν Table : Effect of treatment with C0 2 -rich gas at . ~ bar/l c .0 ° C on the leaching of WIP slags. Leaching concentrations after 2 ~ hours shaking with demineralized water, with liquid/solid ratio 10 (method in accordance with ΝEΝ 7343) Starting material C0 2 treatment (1) 10.6 340 23 960 3 830 <6 2000

Claims: CLAIMS 1. Method for the treatment of incineration residues, characterized in that the residues are treated with gas containing 0.1 to 1002 by volume of C0 2 . 2. Method according to Claim 1, characterized in that the treatment is carried out at a temperature from the ambient temperature to 200°C under a pressure from atmospheric pressure to 10 bar overpressure. 3. Method according to Claim 1 or 2, characterized in that the method is carried out with gas containing 5"202 by volume of C0 2 at a temperature of not more than 100°C and an overpressure of not more than 1 atmosphere. 4. Method according to one or more of Claims 1 or 2, characterized in that microorganisms are added during or before the treatment with C0 2 . 5- Method according to one or more of Claims 1-4, characterized in that nutrients are added at the start of or during the treatment with C0 2 to stimulate the growth of microorganisms. 6. Method according to one or more of Claims 1-5, characterized in that the required C0 2 is supplied completely or partly in the form of flue gases or other C0 2 -rich off-gas flows. 7- Method according to Claim 6, characterized in that flue gases originating from the waste incineration plant are used. 8. Method according to one or more of Claims 1-7, characterized in that the required C0 2 is separated from biogas, flue gases or other C0 2 -rich gases and then mixed with air to the required composition. 9- Method according to one or more of Claims 1-8, characterized in that a gas containing water vapour is used. 10. Method according to one or more of Claims 1-9, characterized in that the process is carried out batchwise by passing the C0 2 -rich gas through the residue to be treated in a sealed chamber. 11. Method according to one of more of Claims 1-10, characterized in that the process is carried out continuously by bringing the residue to be treated into contact with the C0 2 -rich gas in a mixing drum, silo or comparable processing apparatus. 12. Method according to one or more of Claims 1-11, characterized in that the pH of the incineration residues is set to 7 _ 8.5 by the treatment with C0 2 -containing gas. 13- Use of incineration residues as absorption material for the removal of C0 2 from C0 2 -rich off-gases, such as flue gases, biogas, disposal-site gas or off-gas of composting plants.

Inventors: STEKETEE JACOB JACOBUS, URLINGS LEONARDUS GERARDUS CAT, STEKETEE, JACOB, JACOBUS, URLINGS, LEONARDUS, GERARDUS, CATHERINA, MATHIAS
Applicants: STEKETEE JACOB JACOBUS, TAUW MILIEU BV, URLINGS LEONARDUS GERARDUS CAT, STEKETEE, JACOB, JACOBUS, TAUW MILIEU B.V., URLINGS, LEONARDUS, GERARDUS, CATHERINA, MATHIAS
Application year: 1993
Main classification: C04B5
IPC codes: B01D53, B09B3, C04B5