A CELLULAR POLYMER CONTAINING PERFORATED CELL WINDOWS AND A PROCESS FOR THE PREPARATION THEREOF

Abstract: A cellular polymer containing perforated cell windows obtained in the presence of a perforating agent being a substance that has a critical surface free energy of less than 23 mJ/m2 is disclosed. The cellular polymers obtained according to this invention have a fine cell structure and show enhanced dimensional and thermal insulation stability. The invention also relates to rigid polyurethane foam prepared in the presence of, for example, particulate poly(tetrafluoroethylene) or a liquid polyfluoro- or perfluorocarbon, with a boiling point of at least 130 C, as perforating agent.

Description: A CELLULAR POLYMER CONTAINING PERFORATED CELL WINDOWS AND A PROCESS FOR THE PREPARATION THEREOF This invention relates to a cellular polymer containing perforated cell windows, and more particularly a polyurethane polymer and a process for the preparation thereof Cellular polymers such as, for example, polyethylene, polystyrene, or polyurethane are of value in many application areas including notably thermal insulation In this case it is particularly advantageous that such foam exhibits attractive dimensional stability and a relatively stable thermal insulation performance Both of these traits are largely ^ u determined by the cellular structure of the foam and by the composition of the gas(es) within the cell cavity A finer cell structure generally confers better insulation properties to a foam However, as cells become finer, that is of a smaller average diameter, the compressive strength and dimensional stability of the foam frequently becomes inferior Susceptibility to poor dimensional stability is greatest when the cell cavity contains a gas which is likely to condense • -* or alternatively diffuse out of the cell Either phenomenon leads to a loss of partial gas pressure within the cell, resulting in poor dimensional stability of the foam Exemplary of a cell gas noted to diffuse out of a cell cavity, especially of polyurethane, is carbon dioxide The use of carbon dioxide to prepare cellular polymers and especially polyurethane is presently highly favored as a substitute for many of the commonly used physical blowing agents considered 2- harmful to the ozone layer In support of this trend there exists a need to develop an improved process for the preparation of cellular polymers which exhibit attractive dimensional stability and thermal insulation properties Particularly for polyurethane foam, there exists a need for a process which permits the use of, for examDle, water-generated carbon dioxide and yet provides for a 25 foam having a commercially acceptable dimensional stability and thermal insulation performance From the general understanding of foam morphology and the formation of fine celled polymers it is to be appreciated that as the average cell size decreases the closed cell content of the foam becomes significant A cell is comprised of a plurality of struts and corners • ** *u defining a plurality of window regions By "closed cells" it is generally understood that the window regions are completely sealed by a membrane thereby providing an isolated cell cavity A high closed cell content frequently results in poor dimensional stability of the foam A potential solution to the dimensional stability problem is to provide a foam with an open-celled structure That is a structure where one or more of the cell windows are *-* • --> completely open and not sealed by a membrane Such open cells can not suffer from loss of partial pressure and ensuing poor dimensional stability Expanded polymer having an open celled structure may be prepared by crushing the expanded polymer after its preparation to break cell windows. The latter means is only available for elastomeπc polymers since crushing of rigid cellular polymers would lead to permanent deformation and damage. To provide for cell opening in a rigid polymer use of a cell opening agent during the process of its manufacture is required. Typically such cell opening agents are high boiling liquids such as for example high molecular weight poly(oxyalkylene) adducts. However, a disadvantage associated with the use of such cell opening agents is that they generally promote the formation of polymer containing a coarse cell structure and consequently unattractive thermal insulation properties. Thus there exists a need to provide a foam having an "open-cell trait" regarding dimensionally stability but which retains a fine cell structure. To this purpose, the concept of preparing foam with a perforated cell window has been investigated. By "perforated" it is to be understood that the cell windows retain a membrane contacting the struts and corners, but that such membrane has voids within it, that is "pin-holes" or perforations. Thus there exists a need to discover substances which are capable of providing a perforated cell membrane and yet which do not particularly provide an open-cell structure. From a theoretical consideration, it is necessary to discover substances which are capable of promoting a localized perturbation leading to "pin-hole" formation within the cell membrane Again from a theoretical consideration, substances mostly likely to promote a localized perturbation are those substances which have little or no interaction, physical or chemical, with the cellular polymer Substances noted for having little or no interaction with their environment include, for example, poly(tetrafluoroethylene) often identified as "PTFE". EP-224.945-A discloses a polyurethane foam prepared in the presence of from 25 to 60 parts by weight per 100 parts of polyol of particulate PTFE having a particle diameter of 25 microns or less. U.S. Patent 3,753,933 discloses a polyurethane foaming process in the presence of as little as 9 parts/100 parts polyol of a larger sized PTFE particle. However it is to be noted that use of large sized particles or high loadings in a polyurethane foaming process are not easily processed due to viscosity constraints or and provide foam with an undesirably course, open-celled structure. In a first aspect, this invention relates to a cellular polymer containing perforated cell windows wherein the polymer is prepared in the presence of perforating agent characterized in that the perforating agent, present in from 0.01 to 1.0 percent based on total weight of polymer, is a substance that has a critical surface free energy of less than 23 mJ/m 2 and which when a solid has an average particle size of 20 microns or less, or when a liquid has a boiling point greater than the maximum temperature encountered in the process of preparing the polymer In a second aspect, this invention relates to a Dolyurethane precursor composition comprising a polyurethane precursor, being a polyisocyanate or a substance containing isocyanate-reactive hydrogen atoms, and a perforating agent characterized in that the perforating agent is present in from 0 01 to 2 0 percent based on total weight of precursor and perforating agent present, and in that said perforating agent is a substance that has a critical surface free energy of less 23 mJ/m 2 which when a solid has an average particle size of 20 microns or less, or when a liquid has a boiling point at greater than 130°C In a third aspect, this invention relates to a process for preparing a cellular polyurethane polymer containing perforated cell windows by reacting an organic polyisocyanate with a substance containing one or more isocyanate-reactive hydrogen atoms/molecule in the presence of a blowing agent and a perforating agent characterized in that a) the blowing agent comprises water in an amount to provide for at least 50 mole percent of the total blowing requirement to provide a polymer having a density of from 10 to 150 kg/m3, and b) the perforating agent, present in from 0 01 to 1 0 percent based on total weight of organic polyisocyanate and substance containing one or more isocyanate-reactive hydrogen atoms/molecule, is a substance that has a critical surface free energy of less than 23 mJ/m 2 and which when a solid has an average particle size of 20 microns or less, or when a liquid has a boiling point at atmospheric pressure of at least 130°C In accordance with this invention, a cellular polymer having perforated cell windows is obtained by a process which employs a selected perforating agent that can be a particulate solid or a liquid The oolymer can be a thermoplastic or thermoset polymer including, for example, a polyethylene, a polystyrene, a polyester, a polyether, a polyamide, a phenol-formaldehyde resin or especially a polyurethane polymer In the case of polyurethane polymer, this invention is particularly of value when preparing cellular thermoset polyurethanes that can be flexible, semi-rigid or, preferably, rigid polyurethane foams The perforating agent is a substance which is chemically inert under the conditions of preparing the cellular polymer and which has a critical surface free energy of less than 23, preferably less than 20, and more preferably less than 18 5 mJ/m 2 Use of a substance with a higher critical surface free energy generally will not provide a perforated cell window An explanation of critical surface free energy is provided on page 425 and following pages of the 1983 publication, "CRC Handbook of Solubility Parameters and other Cohesion Parameters" by A F M Barton published by CRC Press Inc , ISBN 0-8493-3295-8 In the case of liquid perforating agents it is to be appreciated that the critical free surface energy is temperature dependent, as the temperature increases generally the critical free surface energy decreases Accordingly, suitable liquid pertorating agents for use in this invention are those which on exposure to an elevated process temperature have a critical surface free energy of less than 23 mJ/m 2 at the elevated temperature and preferably those which have a critical surface free energy of less than 23 mJ/m 2 at room temperature When a solid, the perforating agent has a particle size commensurate with the thickness of the membranes occupying the window regions of the cell Typically the average particle size is less than 20, preferably less than 15, more preferably less than 10, and most preferably less than 3 microns. With an average particle size of 10 microns, advantageously the distribution is such that at least 90 percent of the particles are of 10 micron or less; and with an average particle size of 3 microns or less then at least 90% of the particles are of less than 6 microns and at least 10% of the particles are less than 1 micron. Such particle sizes and distribution can be determined by conventional laser, non shear, techniques using equipment such as the Malvern Laser Diffraction Analyzer. It is further advantageous if the particle has a 0 specific surface area of at least 3, preferably at least 4 5 and more preferably at least 6.5 m /g as determined by krypton absorption. Exemplary of suitable solid, particulate perforating agents include fluoπnated polymers comprising poly(tπfluoroethylene) with a critical surface energy of 22 mJ/m 2 * poly(hexafluoropropylene), 16.2 mJ/m 2 - poly(1 ,1-dιhydro-perfluorooctyl methacrylate), 10.6 mJ/m 2 * and especially poly(tetrafluoroethylene), 18.5 mJ/m 2 . Particulate 5 PTFE suitable for use in this invention is available commercially and includes products designated by the trademark FLUOROGLIDE available from ICI such as FL1710 and FL1200, and products available from Dupont under the trademark TEFLON including TEFLON MP 1 100, TEFLON MP 1200, MP 1300 and MP 1500. When a liquid, the perforating agent advantageously has a boiling point at o atmospheric pressure which is greater than the maximum process temperature encountered during the preparation of the cellular polymer. If the liquid perforating agent has a boiling point significantly less than the maximum process temperature, it will function not as a perforating agent but as blowing agent. By "significantly less" it is understood a boiling point which is at least 10°C below the maximum process temperature. Preferably the boiling point is 5 at least 20°C below the maximum process temperature Typical process temperatures can be, for an extrusion process of a thermoplastic polymer, at least 100 C C or higher. Alternatively, such a process may be a reactive molding process such as employed in the preparation of thermoset polymer, notably polyurethane. Accordingly, suitable liquid perforating agents include those substances which advantageously have an atmospheric boiling point of at least 0 100°C, preferably at least 130°C and more preferably at least 150°C and most preferably at least 175°C and which are insoluble or only sparingly soluble in the polymer or precursors thereof. Suitable liquid perforating agents include organic polyfluoro- and especially perfluorocarbon compounds which advantageously have an average molecular weight of at least 350 and preferably at least 400. Exemplary of suitable liquid perforating agents include the fluoπnated 5 organic compounds marketed by 3M under the trademark FLUORINERT including substances identified as FC-104, FC-75, FC-40, FC-43, FC-70, FC-5312 and FC-71 , and substances marketed by Rhone-Poulenc under the trademark FLUTEC including substances identified as PP3, PP6, PP7, PP10, PP1 1 PP24 and PP25 Such liquid perforating agents typically have a critical free surface energy of from 9 to 16 mJ/m 2 at room temperature When the perforating agent is a solid, it preferably is present in from 0 05 to 0 75, and more preferably in from 0 05 to 0 5 percent based on total weight of cellular polymer When the perforating agent is a liquid, preferably it is present in from 0 01 to 0 6, more preferably from 0 01 to 0 5 and most preferably in from 0 01 to 0 2 percent In the present invention, use of a liquid perforating agent is preferred over a solid perforating agent as it is easier to introduce into the process when preparing a cellular polymer Additionally, the liquid perforating agent can be employed in smaller quantities than a solid agent to obtain the same technical effect Combinations of solid and liquid perforating agents may also be used In a preferred embodiment, this invention relates to cellular polyurethane polymers Cellular polyurethane polymers are generally obtainable by contacting under reaction conditions, in presence of said perforating agent and advantageously a blowing agent, polyurethane precursor materials including a polyisocyanate and a substance containing one or more isocyanate-reactive hydrogen atoms Substances containing isocyanate-reactive hydrogen atoms include alcohols, polyester polyols, polyether polyols, and primary or secondary amine-terminated polyethers, or mixtures thereof The perforating agent may be added independently to the reacting mixture or preblended with a polyurethane precursor When preblended with a polyurethane precursor, the amount of perforating agent present is such to provide, after dilution by other reactants, a cellular polymer containing the already mentioned amount of perforating agent Typically, the amount of perforating agent present with a polyurethane precursor will be from 0 01 to 2, preferably from 0 01 to 1 5, and more preferably from 0 01 to 1 0 percent based on total weight of polyurethane precursor and perforating agent present Suitable polyisocyanates include aromatic, aliphatic and cycloaliphatic polyisocyanates and combinations thereof A crude polyisocyanate may also be used in the practice of this invention, such as the crude toluene dnsocyanate obtained by the phosgenation of a mixture of toluene diamines or the crude diphenylmethane dnsocyanate obtained by the phosgenation of crude methylene diphenylamine The preferred polyisocyanates are disclosed in U S Patent 3,215,652 Especially preferred are methylene-bπdged polyphenyl polyisocyanates and mixtures thereof with crude diphenylmethane dnsocyanate, due to their ability to cross-link the polyurethane The amount of polyisocyanate present when preparing the polyurethane foam is such to provide from 0 6 to 3 0 isocyanate groups per isocyanate reactive atom present in the polyol(s) and any water as may be present Preferably the amount of isocyanate is such to provide from 0 7, more preferably from 0 8, and preferably up to 2, more preferably up to 1 6 isocyanate groups per isocyanate reactive atom Suitable polyols include those as are conventionally used in the preparation of rigid polyurethane foam and which typically have an average hydroxyl equivalent weight of from 50 to 700, preferably from 70 to 500, more preferably from 70 to 300 AdditionaMy, such polyols will generally contain from 2 to 8, preferably from 3 to 8, and more preferably from 3 to 6 hydroxyl groups per molecule Examples of suitable polyols are polyetner polyols as described more fully in U S Patent 4,394,491 Exemplary of such Dolyether polyols include those commercially available under the trademark, VORANOL and include VORANOL 202, VORANOL 360, VORANOL 370, VORANOL 446, VORANOL 490, VORANOL 575, VORANOL 640, VORANOL 800 all sold by The Dow Chemical Company Other preferred polyols include alkylene oxide derivatives of Mannich condensate as taught in, for example, U S Patents 3,297,597, 4, 137,265 and 4,383,102, and amino-alkylpiperazine-initiated polyether polyols as described in U S Patents 4,704,410 and 4,704,41 1 A group of polyester oolyols suitable for use in this invention when a foaming process displaying thixotropic properties is required include those whicn are essentially a solid at room temperature Advantageously, the polyester polyol has a melting point within the range of from 50°C to 115°C, and preferably from 55° to 100°C Typically such polyester polyol has an average molecular weight of from 2000 to 6000, preferably from 2500, and more preferably from 3000 and preferably up to 5000, more preferably up to 4500 Exemplary of such a polyester polyol is Dynacoll ™ 7360, a poly-hexamethylene-adipate polyol, of molecular weight 3500 and melting point 60°C, available from Huls AG Advantageously, when preparing a cellular polymer according to this invention there is present a blowing agent The blowing agent is present m an amount to provide the cellular polymer with an overall density of typically from 10 to 150, preferably from 10 to 100, and more preferably from 15 to 80 kg/m3 Suitable blowing agents include, for example, alkanes such as (cyclo)pentane, (cyclo)hexane or a halogen-containing substances such as (per)fluorocarbons and the hydrogen-containing chlorofluorocarbon compounds exemplary of which include Refrigerant 21 , Refrigerant 22, Refrigerant 123, Refrigerant 123a, Refrigerant 124, Refrigerant 124a, Refrigerant 133 (all isomers), Refrigerant 134, Refrigerant 141 b, Refrigerant 142, Refrigerant 151 Among these, Refrigerant 123 (all isomers), Refrigerant 141 b and Refrigerant 142 (all isomers) are most preferred, as these are commercially available in addition to being recognized as having low ozone depletion potentials Other suitable blowing agents also include the amine/carbon dioxide complexes such as taught in U S Patents 4,735,970 and 4,500,656 When preparing polyurethane foam advantageously the blowing agent comprises water Water reacts with the polyisocyanate leading to the in situ generation of nascent carbon dioxide causing the reacting mass to exoand and acquire a reduced density Typically, water is present in an amount to provide for at least 50, preferably at least 75, and up to 100 >nole percent of the blowing requirement to obtain a Dolyurethane foam of said density In a highly preferred embodiment of this invention, the polyurethane blowing agent consists essentially of water Typically for this purpose, the amount of water present is from 0 5 to 15 preferably from 2 0, more preferably from 3 0, and preferably up to 10, more preferably up to 8 parts per 100 parts by weight of polyol Optionally other ingredients may be present when preparing the polyurethane foam Among these other ingredients are catalysts, surfactants, colorants, antioxidants, reinforcing agents, fillers, antistatic agents and flame retardants Suitable flame retardants include phosphorus containing substances such as trιs(chloroalkyl)phosDhate and tπsalkylphosphates, for example tπethyl phosphate; and nitrogen containing substances such as melamine One or more catalysts for the reaction of the active hydrogen-containing compound with the polyisocyanate are advantageously present Suitable catalysts include tertiary amine compounds and organometal c compounds Exemplary tertiary amine catalysts include tπethylenediamine, N-methylmorpho ne, pentamethyldiethylenetπamine, tetramethylethylenediamine, 1-methyl-4-dιmethylamιnoethylpιperazιne, 3-methoxy-N- -dimethylpropylamine, N-ethylmorpholme, diethylethanolamine, N-cocomorpholine, N,N-dιmethyl-N',N'-dιmethyl isopropylpropylenediamine, N,N-dιethyl- -3-dιethylamιnopropylamιne and dimethylbenzylamine Exemplary organometalhc catalysts include organomercury, organolead, organoferπc and organotin catalysts, with organotm catalysts being preferred among these Suitable tin catalysts include stannous chloride, tin salts of carboxylic acids such as dibutyltin dι-2-ethyl hexanoate, as well as other organometal c compounds such as are disclosed in U S Patent 2,846,408 A catalyst for the trimenzation of polyisocyanates and formation of polyisocyanurate polymers, such as an alkali metal alkoxide, alkali metal carboxylate, or quaternary amine compound, may also optionally be employed herein When employed, the quantity of catalyst used is sufficient to increase the rate of polymeπzation reaction Precise quantities must be determined experimentally, but generally will range from 0 01 to 3 0 parts by weight per 100 parts polyol depending on the type and activity of the catalyst It is generally highly preferred to employ a minor amount of a surfactant to stabilize the foaming reaction mixture until it cures Such surfactants advantageously comprise a iiαuid or solid organosi cone surfactant Other, less preferred surfactants, include polyethylene glycol ethers of long chain alcohols, tertiary amine or alkanolamine salts of long chain alkyl acid sulfate esters, alkyl sulfonate esters and alkyl arylsulfonic acids Such surfactants are employed in amounts sufficient to stabilize the foaming reaction mixture against collapse and the formation of large, uneven cells Typically, from 0 1 to 5 parts of the surfactant per 100 parts by weight polyol are sufficient for this purpose The optimum amount of surfactant required needs to be established by experimentation However, it is to be noted that as the amount of surfactant increases tne operating efficiency of the perforating agent may decline The foam obtained according to the disclosed process exhibits attractive dimensional and thermal insulation stability The dimensional stability properties of the foam results from it having a perrorated cell window content sufficient to minimize or overcome the tendency to shrink Presently, Applicants are not aware of a convenient means of 5 quantitatively measuring the perforated cell window content other than by observation using optical microscope techniαues Conventional air flow techniques, as used to determine the open-cell content of a foam, for example test procedure ASTM D 2856, do not provide a reliable means of measurement Attractive thermal insulation properties are accorded to the foam by its fine cell structure Advantageously the foam has an average cell size of less than 1 o 400, preferably less than 350, and more preferably less than 300 microns The polyurethane foam of this invention is of value for the construction industry where insulation board stock with both attractive dimensional stability and thermal insulation is highly desirable The invention may also be used to provide polyurethane foam for semi¬ rigid applications such as for example sealant foam applications 15 The invention is illustrated by way of the examples given hereinbelow, which are not to be considered as limiting the scope of the invention Unless otherwise indicated all amounts given are parts by weight Example 1 Foams 1 to 4 and Comparative Foam A are prepared according to the formulation 20 given in Table 1 Where reported the foam physical properties are measured in accordance with the mentioned test procedures Compressive Strength - DIN 53421 , Dimensional Stability - DIN 53431 , and Thermal Conductivity - ASTM C 518 Polyol A contains (parts by weight) 41 3 parts NIAX APP 315, a polyester polyol available from Union Carbide Corporation, 25 25 8 parts IXOL B251 , a halogen-containing polyether polyol available from Solvay Cie, 6 2 parts VORANOL RN 482, a sorbitol initiated polyether polyol available from The Dow Chemical Company, 5 2 parts VORANOL RA 640 an ethylenediamine initiated polyether polyol available from The Dow Chemical Company, 30 2 1 parts glycerine, 15 4 Darts tπethylphosphate (TEP), 5 0 parts melamme, average particle size 10 microns, available from DSM, 4 0 parts sihcone-based surfactant blend, a 1 3 weight ratio of surfactant DC 193 available from Dow Corning and surfactant Tegostab B-8418 available from Th 35 Goloschmidt AG, 4 7 parts catalyst mixture containing a 17 5 5 1 weight ratio of a proprietary amine compound VORANOL C-52 available from The Dow Chemical Company, dιmethylamιnocyclohexane(DMCHA), and a proprietary amine compound NIAX A1 available from Union Carbide Corooration, 2 1 parts water, 3 0 parts FLUTEC PP1 available from Rhone-Poulenc and understood to be perfluorohexane; 1 1 8 parts isopentane Perforating Agents TEFLON* MP 1 100 particulate PTFE, average particle size 3 microns, ≥ 90% of the particles have an average diameter of less 6 microns and at least 10% of the particles have an average diameter of less ≤ 1 micron, ano average surface area 8 m 2 /g TEFLON* MP 1200 particulate PTFE, average particle size 3 microns, average surface area 3 m 2 /g TEFLON* MP 1300 particulate PTFE, average particle size 15 microns, average surface area 3 m 2 /g TEFLON* MP 1500 particulate PTFE, average particle size 20 microns, average surface area 3 m 2 /g Polyol A is reacted with a crude polyphenyl polymethylene polyisocyanate VORANATE M220 available from The Dow Chemical Company The polyisocyanate is present in an amount to provide for an isocyanate reaction index of 1 6 The reactivity of the system is observed by measuring its cream time (C T ), gel time (G T ) and tack-free time (T F T ) Foams 1 to 4 show improved low temperature dimensional stability compared to Comparative Foam A which contains no perforating agent Foams 1 to 4 also show the desirability of preparing foam in the presence of a perforating agent which has a smaller average particle size Example 2 (Foam 5) The method of Example 1 is repeated with the following exceptions TEFLON 30- N, an aqueous dispersion of particulate poly(tetrafluoroethylene) understood to contain 60 weight percent solids having an average particle size of 20 microns is employed as the perforating agent Polyol A is replaced by a blend of Polyol B, polyester polyol NIAX APP 315 and Polyol C, a phenol-formaldehyde initiated polyoxyalkylene polyol having a hydroxyl equivalent weight of 300 Polyols B and C are selected to orovide a foam particularly susceptible to shrinkage in normal circumstances Physical properties of the foam is reported in Table 2 The results presented in Table 2 demonstrate that the solid perforating agent can oe conveniently introduced into the foaming process as an aqueous dispersion Example 3 (Foams 6 to 9. and Comparative Foam B) The method of Example 2 is repeated, only in this case the Derforating agents are (1 )TEFL0N MP 1500, and (2)TEFLON MP 1 100 Comparative Foam B is prepared in the presence of particulate starch understood to have a particle size of 10 microns ana a critical surface free energy of 39 mJ/m 2 Physical properties of the foams are reported in Table 3 The results presented in Table 3 demonstrate the difference in dimensional stability to be obtained with different perforating agents employed in various amounts Comparative Foam B demonstrates that particulate starch can not confer the same degree of dimensional stability to a foam, even when used in superior amounts Example 4 The method of Example 2 is repeated, only in this case the perforating agent is FLUORINERT L-9901 available from 3M and understood to be a mixture of G 5-C 1 8 perfluoπnated compounds having a boiling point of 215°C Comparative Foams C and D, are prepared in the presence of FLUORINERT FC 104, available from 3M, and understood to be perf I uorocarbon compound which has a boiling point of 101 °C and a critical surface free energy of 10 mJ/m 2 The boiling point of FLUORINERT FC 104 is less than the observed maximum process temperature of 160°C Physical properties of the foams 10, 1 1 and Comparative Foams C and D are reported in Table 4 The results in Table 4 demonstrate that a substance with a critical surface free energy of less than 23 mJ/m 2 and with a boiling point of substantially less than the maximum process temperature is unable to confer similar dimensionally stability to a foam prepared in the presence of a perforating agent according to this invention Table 2. 7942 Table 3. 7942 Taole4.

Claims: Claims : 1 A cellular polymer containing perforated ceil windows wherein the polymer is prepared in the presence of perforating agent characterized in that the perforating agent, present in from 0 01 to 1 0 percent based on total weight of polymer, is a substance that has a critical surface free energy of less than 23 mJ/m 2 and which when a solid has an average particle size of 20 microns or less, or when a liquid has a boiling point greater than the maximum temperature encountered in the process of preparing the polymer 2 A cellular polymer according to Claim 1 which is a polyethylene, polystyrene, polyester, phenol-formaldehyde, polyether, polyamide or polyurethane polymer 0 3 A cellular polymer according to Claim 2 which is a polyurethane with a density of from 10 to 150 kg/m 2 obtainable by contacting, in the presence of said perforating agent, an organic polyisocyanate with a substance containing one or more isocyanate-reactive hydrogen atoms/molecule and further in the presence of a blowing agent that comprises water in an amount to provide for at least 50 mole percent of the blowing requirement to achieve 5 said density 4 A cellular polymer according to Claims 1 to 3 wherein the solid perforating agent is poly(trι luoroethylene), poly(tetrafluoroethylene), poly(hexafluoropropylene) or poly(1 ,1-dιhydro-perfluorooctyl methacrylate) polymer 5 A cellular polymer according to Claim 4 wherein the perforating agent is o poly(tetrafluoroethylene) of average particle size of 10 microns or less, and which is present in from 0 05 to 0 75 percent based on total weight of cellular polymer 6 A cellular polymer according to Claims 1 to 3 wherein the liquid perforating agent has a boiling point at atmospheric pressure of at least 130°C and is an organic polyfluoro- or perfluorocarbon compound which is insoluble or sparingly soluble in the 5 polymer or polymer precursor(s) 7 A polyurethane precursor composition comprising a polyurethane precursor, being a polyisocyanate or a substance containing isocyanate-reactive hydrogen atoms, and a perforating agent characterized in that the perforating agent is present in from 0 01 to 2 0 percent based on total weight of precursor and perforating agent present, and in 0 that said perforating agent is a substance that has a critical surface free energy of less 23 mJ/m 2 which when a solid has an average particle size of 20 microns or less, or when a liquid has a boiling point at greater than 130°C 8 A polyurethane precursor composition according to Claim 7 wherein said solid perforating agent is a particulate poly(tetrafluoroethylene) and wherein said liquid 5 perforating agent is an organic polyfluoro- or perfluorocarbon compound which is insoluble or sparingly soluble in the precursor 94/07942 9 A polyurethane precursor composition according to Claim 7 where the precursor substance containing isocyanate-reactive hydrogen atoms is a polyether polyol, polyester polyol, amine-terminated polyether or mixtures thereof 10 A process for preparing a cellular polyurethane polymer containing 5 perforated cell windows by reacting an organic polyisocyanate with a substance containing one or more isocyanate-reactive hydrogen atoms/molecule in the presence of a blowing agent and a perforating agent characterized in that: a) the blowing agent comprises water in an amount to provide for at least 50 mole percent of the total blowing requirement to provide a polymer having a density of from 10 10 to 150 g/m3, and b) the perforating agent, present in from 0 01 to 1 0 percent based on total weight of organic polyisocyanate and substance containing one or more isocyanate-reactive hydrogen atoms/molecule, is a substance that has a critical surface free energy of less than 23 mJ/m 2 and which when a solid has an average particle size of 20 microns or less, or when a 15 liquid has a boiling point at atmospheric pressure of at least 130°C 0 5 0 5

Inventors: SMITS GUIDE F, THOEN JOHAN A, SMITS, GUIDE, F., THOEN, JOHAN, A.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1993
Main classification: C08J9
IPC codes: C08J9