HIGH ELECTRICALLY CONDUCTIVE POLYANILINE COMPLEXES HAVING POLAR OR POLAR AND HYDROGEN BONDING SUBSTITUENTS

Abstract: This invention relates to thermally stable electrically conductive conjugated polymer comprising a conjugated polymer cation such as a substituted or unsubstituted polyaniline doped with a dopant anion substituted with one or more polar groups and preferably polar and hydrogen bonding groups such as hydroxy, the polar group having an electronegativity or an electropositivity such that said polar group or groups have a net polar group molar contribution greater than zero.

Description: HIGH ELECTRICALLY CONDUCTIVE POLYANILINE COMPLEXES HAVING POLAR OR POLAR AND HYDROGEN BONDING SUBSTITUENTS BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to thermally stable electrically conductive substituted and unsubstituted poiyaniline compositions having relatively high electricaly conductivity and preferably having relatively high thermal stability. Another aspect of this invention relates to compositions comprising such polyanilines and other materials as for example fillers, polymers, and the like. Yet another aspect of this invention relates to poiyaniline articles, including films, fibers, coatings and the like formed from the polymer compositions of this invention. 2. p..criptiQP of t Prior Art There has recently been an increased interest in the electrochemistry and electrical phenomena of polymeric systems. Recently, work has intensified with polymers having extended conjugation in at least one backbone chain. One conjugated polymer system with strong hydrogen bonding and polar interactions currently under study is poiyaniline. See for example European Patent No. 0017717 and U.S. Patent Nos. 3,963,498, 4,025,463, 4,855,361 , 4,798,685, 4,806,271 , 4,851 ,487, 4,940,640, 4,798,685, 5,006,278 and 5,069,820; and PCT W089/01694 and PCT W090/102797. Another conjugated polymer system which is capable of strong hydrogen bonding and/or polar interactions is poly pyrrole. See for example EP0055358. There has recently been an increased interest in the electrochemistry and electrical phenomena of polymeric systems such as poiyaniline. See for example, SUMMARY OF THE INVENTION One aspect of the present invention relates to an electrically conductive doped substituted or unsubstituted conjugated polymer comprised of a positively ionized conjugated polymer (polymeric cation) and one or more organic dopant solute species (anions) selected from the group consisting an organic moiety having one or more anionic functional groups as for example such groups containing one or more phosphorous or sulfur acid functional group, and having at least one substituent selected from the group consisting of "polar groups" having an electronegativity or electropositivity such that said groups have a net polar group molar contribution greater than zero and preferably one or more of such polar groups substituents which are also hydrogen groups. This invention also relates to a composition comprising a matrix of one or more non-electrically conductive thermoplastic and/or thermosetting polymers having one or more doped polyanilines of this invention dispersed therein, and to articles formed from this composition. This invention also relates to a process for forming the compositions of this invention by melt-blending one or more doped polyanilines of this invention and one or more polymers selected from the group consisting of thermoplastic polymers and thermosetting polymers. Yet another aspect of this invention relates to articles formed from the composition and poiyaniline of this invention. As used herein "conjugated polymer(s)" are homopolymers or copolymers which are comprised of alternating carbon-carbon double bonds (either singly or as part of an aromatic ring structure), and optionally including one or more heteroatoms such as oxygen, nitrogen, sulfur, selenium, phosphorous and the like along the polymer conjugated backbone or conjugated side chains thereof which can be rendered to an electrically conductive state (an electroconductivity equal to or greater than about 10 '8 S/cm as determined by the four-in¬ line probe method described in "Laboratory Notes on Electrical and Galvanometric Measurements" by H.H. Wieder, Elsevier Scientific Publishing Co., New York, New York, 1979) by doping with some dopants known in the art). As used herein, an "organic radical" means a polymeric, monomeric or oligomeric organic radical; "electrically conductive" means that the doped conjugated polymer has a conductivity of at least about 10 "8 S/cm (preferably equal to or greater than about 10 "β S/cm, more preferably equal to or greater than about 10 '3 S/cm and most preferably equal to or greater than about 1 S/cm) as determined by the four-in-line probe method described in "Laboratory Notes on Electrical and Galvanometric Measurements" by H.H. Wieder, Elsevier Scientific Publishing Co., New York, 1979; "thermally stable" means an electrically conductive polymer having a half life for electrical conductivity equal to or greater than one hour in air at a temperature of 150°C; "acid function" is a acid function having at least one proton or at least one function that can be thermally or chemically transformed into a proton under use conditions, such as NH 4 + , PH 3 S + , N(CH 3 ) 2 H 2 + , N(C 2 H 5 )H 3 + and the like such as a carboxylic acid, boric acid, sulfonic acid, sulfonic acid, phosphoric acid, phosphinic acid and the like; and "sulfur or phosphorus acid function" means acid groups containing a sulfur and/or phosphorus atom such as sulfonic acid, sulfonic acid, phosphoric acid, phosphinic acid, phosphonic acid and the like. As used herein, a "hydrogen bonding substituent" means aji organic or inorganic radical having one or more functional groups which are capable of interacting with a organic or inorganic radical to form one or more hydrogen bonding interactions, as for example hydrogen bonding functional groups such as -O-, -N-, -S-, -P-, -CO 2 ' , halo, -C(O)-, -C(O)O-, N(H)C(O)-, -N(H)C(O)N(H)-, -OH, -OR, -NH-, -NR- , -NH 2 , -N(H)(R), -N(R)(R), -SO 3 \ -P0 2 * , -PHO 2 \ -PO 3 ', -SH, and -SR, where R is an organic radical which may be substituted with acid functional groups, such as a sulfonic acid, sulfonic acid, phosphonic acid, phosphinic acid, phosphoric acid, carboxylic acid, boric acid group, and the derivatives thereof, such as salts and esters. Several advantages flow from this invention. For example, the electrically conductive conjugated polymers of this invention exhibit enhanced electrical conductivity which is believed to result from the polar substituent. In those embodiments of the invention where the conjugated polymer is capable of hydrogen bonding or polar interactions and where the anion of the dopant species also includes substituents which are polar and hydrogen bonding, the composition of this invention exhibits enhanced conductivity, and, in addition, exhibits enhanced thermal stability. DESCRIPTION OF THE PREFERRED EMBODIMENTS Conjugated polymers for use in the process of this invention may vary widely provided that the polymer includes one or more polar groups and preferably one or more polar groups which are also hydrogen bonding. The polar group and hydrogen bonding group can be at any position in the polymer as for example in a backbone chain, in a chain pendant to the main backbone or substituted to said backbone chain or said pendant chain, but is preferably in the main backbone. Illustrative of such polymers are poly(unsaturated) polymers such as substituted and unsubstituted polyacetylene; substituted or unsubstituted poly (heteroaro mat ics), such as poly(thienylenes), poly(pyrroles), poly(quinolines), poly(isothianaphthenes), poly(carbazoles), poly(alkyl thiophenes) and the like; substituted or unsubstituted poly(aromatics) such as poly(phenylene sulfides), poly(anilines), polyacenes, poly(phenylenes), poly(naphthalenes), poly(naphthols), and poly(perinaphthalenes); poly(benzoquinones); poly(azulenes); and substituted or unsubstituted poly(aromatic vinylenes) such as poly(phenylene vinylenes), poly(dimethoxyphenylene vinylenes), poly(naphthalene vinylenes) and the like; and substituted or unsubstituted poly(heteroaromatic vinylenes) such as poly(thienylene vinylenes), poly(furylene vinylenes), poly(carbazole vinylenes), poly(pyrrole vinylenes) and the like or derivatives thereof which include one or more polar groups and/or polar and hydrogen bonding groups. Where the polymer does not include a polar group or polar and hydrogen bonding group in the backbone chains or in a pendant chain, as for example, polyphenylene, poly(naphthalene), poly(perinephthalene) and the like then only derivatives which are substituted by a polar group or polar and hydrogen bonding group such as hydroxyl are suitable. Other polymers such as polypyrroles and polyanilines which include polar groups or polar and hydrogen bonding groups in the polymer backbone need not be derivatized. Preferred conjugated homopolymers or copolymers are "conjugated backbone homopolymers or copolymers". As used herein, "conjugated backbone homopolymers or copolymers" are conjugated homopolymers or copolymers in which all or substantially all of the conjugation is in the main backbone of the homopoiymer or copolymer. . Preferred conjugated homopoiymer or copolymers are substituted or unsubstituted polyanilines, poly(heterocycles), and aromatic or heteroaromatic vinylenes. Illustrative of preferred homopolymers or copolymers of poly(heterocycles), and aromatic or heteroamatic vinylenes are those described in more detail in U.S. Patent Nos. 4,71 1 ,742 and 5,068,060 and PCT/W088/00954. More preferred for the practice of this invention are conjugated polymers which have relatively low acidity (pKa > 2, preferably > 4 and most preferably > 6) and which are readily doped by protonic acids as for example, poiyaniline, poly(benzoquinone), polypyrrole, and poly(azobenzene). More preferred conjugated backbone homopolymers or copolymers are polγ(aniiines) and polypyrroles. Most preferred polymers are polyanilines. As used herein, "poly(anilines)" are homopolymers or copolymers in which the recurring backbone monomeric units are selected from the group consisting of substituted or unsubstituted phenyl rings and amine linkages (-NH- or -NR- where R is a substituent other than hydrogen) which may contain varying amounts of substituted or unsubstituted quinoid rings and imine (-N = ) linkages. As used herein, "neutral or undoped poiyaniline" is characterized by an uncharged backbone, "poiyaniline base" is a particular form of undoped poiyaniline which contains at least one quinoid diimine linkage in the backbone and "electrically conductive or doped poly (aniline)" is characterized by a charged backbone which may be formed by a partial or complete protonation of the amine and/or imine nitrogen atoms. As used herein, "leuco-polyaniline" is a neutral form of poiyaniline which is in a reduced form (low oxidation state) and which comprises to a substantial degree aromatic phenyl rings linked by amine (-NH-) linkages. Such leuco-polγaniiines are preferably doped with oxidizing dopants (such as ferric salts). Polyanilines for use in the process of this invention may vary widely. Any form of substituted and unsubstituted poiyaniline can be conveniently used in the practice of this invention. Illustrative of useful forms are those described in Green, A.G. and Woodhead, A.E., CXVII - Aniline-black and Allied Compounds, Part II", J. Chem. Soc. 101 pp. 1 1 17 (1912) and Kobayashi, et al., "Electrochemical Reactions... of Poiyaniline Film-Coated Electrodes", J. Electroanal. Chem.. 177. pp. 281 -91 (1984) and in Shacklette, L.W., et al. "Structure and Properties of Poiyaniline as Modeled by Single-Crystal Oligomers", J. Chem. Phvs.. 88. pp. 3955 (1988), which are hereby incorporated by reference. Examples of unsubstituted and substituted poiyaniline useful in this invention are characterized by different ratios of phenylene amine and quinone imine backbone segments and include leucoemeraldine, protoemeraldine, emeraldine, nigraniiine and pernigraniline. (See U.S. Patent No. 4,940,640) In the preferred embodiments of the invention, poly(anilines) for use in the invention are homopolymers and copolymers of the type derived from the polymerization of unsubstituted and substituted anilines of the Formula I: FORMULA I wherein: n is an integer from 0 to 5; m is an integer from 0 to 5, with the proviso that the sum of n and m is equal to 5 and with the further proviso that at least one position on the aniline ring, preferably at the para position, is substituted with a substituent which will allow coupling of the aniline units, such as halo, hydrogen or other leaving group; R 1 is the same or different at each occurrence and is selected from the group consisting of alkyl, deuterium, alkenyl, alkoxy, cγcloalkyl, cycloalkenyl, alkanoyl, alkylthio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, arylamino, diarylamino, aikylarylamino, aryl, alkylsulfinyl, aryloxyalkyl, alkylsulfinylalkyl, alkoxyalkyl, alkylsulfonyl, arylthio, alkylsulfonylalkyl, boric acid or salts or esters thereof, phosphoric acid or salts or esters thereof, sulfinate salts, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, carboxylic acid or salts or esters thereof, phosphonic acid or salts or esters thereof, halo, hydroxy, cyano, sulfinic acid or salts or esters thereof, phosphinic acid or salts or esters thereof, sulfonic acid or salts or esters thereof, nitro, alkylsilane, or any of the foregoing aryl, aliphatic or cycloaliphatic groups substituted with one or more phosphonic acid or salts or esters thereof, sulfonic acid or salts or esters thereof, phosphoric acid or salts or esters thereof, boric acid or salts or esters thereof, sulfinic acid or salts or esters thereof, phosphinic acid or salts or esters thereof, carboxylic acid or salts or esters thereof, halo, nitro, amino, alkylamino, dialkylamino, arylamino, diarylamino, aikylarylamino, cyano or epoxy moieties; or any two R 1 groups together or any R, group together with any R 2 group may form a substituted or unsubstituted alkylene, alkenylene or alkynylene chain completing a 3, 4, 5, 6, 7, 8, 9 or 10 membered aromatic, heteroaromatic, heteroalicyclic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, sulfur, sulfinyl, or salts or esters thereof, carbonyl, sulfonyl, or oxygen atoms wherein permissible substituents are one or more phosphonic acid or salts or esters thereof, sulfonic acid or salts or esters thereof, phosphoric acid or salts or esters thereof, boric acid or salts or esters thereof, phosphinic acid or salts or esters thereof, carboxylic acid or salts or esters thereof, halo, nitro, amino, alkylamino, sulfinic acid or salts or esters thereof, dialkylamino, arylamino, diarylamino, aikylarylamino, cyano or epoxy moieties ; or R. is an aliphatic moiety having repeat units of the formula: -(OCH 2 CH 2 ) q O-CH 3 , -(OCH 2 CH(CH 3 )) q O-CH 3 , -(CH 2 ) q CF 3 , -(CF 2 ) q -CF 3 or -(CH 2 ) q CH 3 wherein q is a positive whole number; and R 2 is selected from the group consisting of permissible R 1 substituents and hydrogen. Preferred poiyaniline consists of repeat units of the Formulas and/or III: Formula II Formula III a combination thereof having various ratios of the above repeat units in the poiyaniline backbone such as leucoemeraldine, protoemeraldine, emeraldine, nigraniline and pemigraniline. Polγ(anilines) useful in the practice of this invention are more preferably those of the Formula IV: FORMULA IV wherein: n, m, R, and R 2 are as described above; x and y are the same or different at each occurrence and are integers equal to or greater than 0, with the proviso than the sum of x and y is greater than 0, preferably where x is an integer equal to or greater than 0 and/or that the ratio of x to y is greater than or equal to about 0, more preferably said ratio is equal to or greater than 0.5 and most preferably said ratio is equal to or greater than about 1 ; and z is the same or different at each occurrence and is an integer equal to or greater than about 5. Preferred for use in the practice of this invention are poly(anilines) of the above Formula IV in which: n is an integer from 0 or 1 ; m is an integer from 3 or 4, with the proviso that the sum of n and m is equal to 4; R_ is phenyl, or alkyl or alkoxy having from 1 to about 12 carbon atoms, a protonic acid function or a salt or ester thereof, or alkyl, phenyl or alkoxy substituted with one more or protonic acids or salts or esters thereof; x is an integer equal to or greater than 1 ; y is equal to or greater than 0, with the proviso that the ratio of x to y is equal to or greater than 0.5; z is an integer equal to or greater than about 5; Particularly preferred for use in the practice of this invention are polγ(anilines) of the above Formula IV in which: n is an integer from 0 or 1 ; m is an integer from 3 or 4 with the proviso that the sum of n and m is equal to 4; R 1 is alkyl, or alkoxy having from 1 to about 6 carbon carboxylic acid or salts or esters thereof, phosphinic acid or salts or esters thereof, sulfonic acid or salts or esters thereof, sulfinic acid or salts or esters thereof, phosphonic acid or salts or esters thereof, or alkyl or alkoxy substituted with phosphinic acid or salts or esters thereof, sulfinic acid or salts or esters thereof, halo, phosphonic acid or salts or esters thereof, phosphoric acid or salts or esters thereof, or sulfonic acid or salts or esters thereof; x is an integer equal to or greater than 2; y is equal to or greater than 0, with the proviso that the ratio of x to y is greater than about 1 ; and z is an integer equal to or greater than about 10. Amongst the preferred embodiments, more preferred for use in the practice of this invention are poly(anilines) of the above Formula IV in which: n is an integer from 0 or 1 ; m is an integer from 3 or 4, with the proviso that the sum of n and m is equal to 4; R, is alkoxy or alkyl of from 1 to about 3 carbon atoms, sulfonic acid or salts thereof, phosphoric acid or salts thereof, or phosphonic acid or salts thereof; x is an integer equal to or greater than 2; and γ is an integer equal to or greater than 1 , with the proviso that the ratio of x to y is equal to or greater than about 2; and z is an integer equal to or greater than about 10. In the most preferred embodiment of the invention n is 0; m is 4; x is an integer equal to about 2; y is an integer equal to about 1 with the proviso that the ratio of x to y is equal to or greater than about 2; z is an integer equal to or greater than about 10;R 1 is one sulfonic acid or a salt or ester thereof, alkyl or alkoxy having from 1 to about 3 carbon atoms. Poly(aniline) derived from unsubstituted aniline is the poly(aniline) of choice. In general, the number of conjugated homopoiymer or copolymer repeat units are not critical and may vary widely. The greater the number of repeat units the greater the molecular weight of the conjugated homopoiymer or copolymer and the greater the viscosity of solutions of the polymer. In the present application where conjugated homopolymers or copolymers of relatively high molecular weight and insolubility are required, then such materials can be used. The number of repeat units is preferably at least about 10. The upper limit can vary widely depending on the desired molecular weight and viscosity and the required degree of processibility, such as melt processibility, solution processibility and the like. In the preferred embodiments of the invention, the number of repeat units is at least about 20, and in the particularly preferred embodiments, the number of repeat units is at least about 30. Amongst the particularly preferred embodiments, most preferred are those embodiments in which the number of repeat units is at least about 40. Conjugated homopolymers and copolymers can be conveniently prepared through conventional procedures. Such procedures are well known in the art and will not be described herein in great detail. See for example U.S. Patent Nos. 4,940,640; 4,711 ,742; 4,521 ,589; 4,808,681 ; 4,983,322; 5,006,278 and 4,900,782; PCT WO88/00954; and "The Handbook of Conducting Polymers", edited by Terje A. Skotheim, Marcell Decker, Inc., New York and Basel and references cited therein, all of which is hereby incorporated by reference. For example, preferred polyanilines can be prepared through use of chemical and electrochemical synthetic procedures. For example, one form of poiyaniline can be prepared chemically by treating a suitable aniline with an oxidant such as ammonium persulfate (NH 4 ) 2 S 2 O 8 in excess acid such as IM HCl. This powdered form of poiyaniline is blue green in color. After methanol washing and air drying this material exhibits a conductivity of about 5 S/cm. This conductive form of poiyaniline can be treated with ammonium hydroxide in ethanol to form a non-conductive form of poiyaniline which is dark blue in color and which has a conductivity of less than o 10 S/cm. Other chemical procedures for preparation of various chemical forms of poiyaniline are described in detail in Green et al and U.S. Patent Nos. 4,855,361 , 4,798,685, 4,806,271 , 4,822,638, 4,851 ,487 and 4,940,517 described above. Useful forms of conjugated polymers can also be prepared eJectrochemically. For example, useful forms of poiyaniline can be prepared by the electrochemical oxidation of aniline in aqueous fluoroboric acid electrolyte on a platinum foil anode. Other useful conjugated polymers can be prepared pyrolytically. For example, polyacenes can be prepared by the pyrrolysis of phenolic resins as described in greater detail in U.S. Patent Nos. 4,615,960; 4,628,015; 4,601 ,849; and 4,753,717. Other chemical and electrochemical syntheses and transformations of the conductive form of poiyaniline may be discovered and are presently contemplated as being useful. Moreover, additional forms or types of poiyaniline may be elucidated in the future. Accordingly, no limitation to the syntheses, transformation, or structures herein described or postulated is intended beyond the limitations of the appended claims. The conjugated polymer may be electrically neutral or electrically conductive. The conjugated polymer is rendered electrically conductive by doping with a dopant solute. In general, such dopant solute is derived from a dopant compound, which upon addition to the conjugated polymer, introduces positive charge carriers onto the polymer backbone with co-committent formation of an anionic dopant solute species (dopant anion) to form a charge transfer complex with the conjugated polymer, which complex has a conductivity equal to or greater than about 10 "8 ohm 1 cm '1 by the four-in-line probe method. Dopants for use in the practice of this invention are critical. The particular dopant of choice will depend on the particular form of the undoped conjugated polymer. For example, if the polymer is initially in a reduced state (e.g. reduced polypyrrole or leuco- polyaniline) then the dopant of choice preferably would be an oxidizing dopant or combination of dopants. Alternatively, if the polymers were a base, as for example, poiyaniline base, then the preferred dopant would be an acid. The dopant or dopant combination is chosen such that the doped conductive polymer complex contains a polymer cation and a dopant solute (anion) where the dopant solute contains an anionic functionality (preferably a sulfur and/or phosphorus containing anionic functionality) and at least one polar substituent having a net dipole moment greater than zero such that upon the formation of a complex with the conjugated polymer an anion having a polar substituent is generated. While we do not wish to be bound by any theory, it is believed that the net dipole moment generated by the polar substitutent smooths the dipolar field generated by the array of charge on the backbone of the doped conjugated polymer such as poiyaniline, polypyrrole, polythiophene, poly(phenylene vinylenes) and derivatives thereof and the like and that the smoothing of the dipolar field leads to an increase in charge delocalization and hence to an increase in electrical conductivity. In the preferred embodiments of the invention, the! substituent is polar and hydrogen bonding, which leads to enhance thermal stability in addition to high electrical conductivity. While we do not wish to be bound by any theory, it is believed that in addition to increased charge delocalization resulting from the polarity of the substituent, the dipole-dipole interactions with the polymer or, where the polar substituent is also hydrogen bonding, the hydrogen bonding interactions between the dopant and the conjugated polymer strengthen bonding between the dopant and the polymer cation over and above that provided by the primary ionic interaction between the polymer cation and the dopant anion. Such increased bond strength leads to increased thermal stability. For example, in the case of poiyaniline, it is believed that the hydrogen bonding interactions would be between the amine and/or imine linkages in the poiyaniline backbone and the hydrogen bonding group of the dopant solute. Such increased bond strength leads to increased thermal stability. Although not critical, it is believed that these interactions are maximized when the distance between at least one anionic functionality and the hydrogen bonding group of the dopant anion are such that the anionic functionality and the hydrogen bonding group are capable of coordinating with adjacent hydrogen groups bonding along the backbone of a single chain of the conjugated polymer, as for example the amine and/or imine linkages in the case of poiyaniline. In the preferred embodiments of the invention, when the conjugated polymer is an unsubstituted poiyaniline, the preferred distance between at least one anionic functionality and at least one hydrogen bonding group is approximately about 5 A to about 6 Λ. Likewise, dopants containing multiple polar and/or hydrogen bonding substituents, such as sulfonic acid groups, phosphonic acid groups, boronic acid groups, carboxylic acid groups, phosphoric acid groups, phosphinic acid groups, carboxylic acid groups, sulfinic acid groups and the like, halo groups, cyano groups, nitro groups, hydroxyl groups, carbonyl groups and the like are preferred over dopant anions which contain only a single polar or hydrogen bonding substituent, since in this case the strength of ionic bonding between the polymer cation and dopant anion is increased. Moreover, with additional bonding provided by multiple hydrogen bonding and polar groups, bonding to and between multiple polymer chains can also take place. Such bonding is believed to lead to a more rigid three-dimensionally bonded structure which will act to limit the loss of dopant by diffusion and volatization at high temperature and provide enhanced thermal stability. For example, the periodicity of the charge density wave, which forms at the highest doping levels for poiyaniline, corresponds to the distance between every second nitrogen linkage along the poiyaniline backbone. In the preferred embodiments where the poiyaniline is an unsubstituted poiyaniline, the preferred distance between multiple acid groups is from about 9 A to about 11 A. Useful polar groups, and preferred polar and hydrogen bonding substituents may vary widely. Polar, and polar and hydrogen bonding substituents which provide the desired net dipole moment constant are well known to those of skill in the art. Illustrative of useful groups are those described in A.F.M. Barton, "Handbook of Solubility Parameters", CRC Press, Boca Raton, FL, pg. 70 and pg. 85-86 and Pimentel and McClellan, "The Hydrogen Bond", W.H. Freeman Company, San Francisco (1960). Useful polar substituents are those having a polarity greater than that of a carbon/hydrogen substituent such as a methyl group. Such groups will often exhibit inductive effects, and/or resonance effects and will often include one or more heteratoms or a halogen. Illustrative of such groups are halo, cyano, hydroxy, carboxyl, alkylamino, amino, imino, urethane, nitro, mercapto, phenyl and carbonyl containing groups such as an aldhehyde as for example formyl, acetyl, and the like, esters as for example methylacetate and the like, amide as for example a ido and the like, alkoxy and alkylthio such as methoxy, ethoxy, methylthio, ethylthio and the like, quaternary ammonium, haloalkyl as for example trifluoromethyl, and inorganic acids and their esters. Preferred for use in the practice of this invention are groups which are polar and hydrogen bonding. Illustrative of such preferred polar and hydrogen bonding groups are hydroxy, carboxyl and carbonyl containing groups, and the more preferred polar and hydrogen bonding group is hydroxy. A measure of the polar contribution of a particular substituent can be estimated by the polar group molar attraction constant, F p , measured in units of J % cm 2 mol '1 . Such values are listed in the A.F.M. Barton Handbook, p. 70 and p. 85. It is a requirement for this invention that the Fp be greater than zero. Preferred values of Fp are greater than 200, more preferred values of F p are greater than 400 and most preferred values of F p are greater than 500. Useful hydrogen bonding substituents may vary widely and essentially any hydrogen bonding group may be useful. Illustrative of useful groups are those described in A.F.M. Barton, "Handbook of Solubility Parameters", CRC Press, Bica Raton, FL. pp. 85-86 and Pimentel and McClellan, "The Hydrogen Bond", W.H. Freeman Company, San Francisco (1960). Useful groups usually are those containing an oxygen, nitrogen, phosphorus, sulfur and halogen. The oxygen may be singly or doubly bonded, and the nitrogen singly, doubly or triply bonded. Still other useful groups are weakly hydrogen bonding groups, carbon double and triple bonds and aromatic rings. Illustrative of other useful hydrogen bonding functions are fluoro, cyano, hydroxy, carboxyl, chloro, bromo, iodo, sulfoxide, sulfone, sulfonamide, amino, imino, nitro, phenyl, carbonyl containing groups such as an aldehydes, amides, esters, urethanes, ketones and the like, alkoxy such as methoxy and ethoxy, aromatic sulfones, oxides and sulfoxides as for example phenyl oxide, diphenyl oxide, phenyl sulfoxide and phenyisulfone, and haloalkyl such as trifluoromethyl, organic or inorganic acids and their esters such as carboxylic acid and boric acid. Preferred hydrogen bonding substituents are oxygen containing groups such as hydrogen, hydroxy, carboxylic acid, ethers, and carbonyl, and halo, and the more preferred hydrogen bonding substituent is hydroxy. Hydrogen bonding groups can also be classified according to their propensity to act as hydrogen acceptors or donors. Examples of hydrogen acceptors include functional groups containing oxygen, as for example a carbonyl, carboxylate or ether functionality, halo, functional groups containing nitrogen such as divalent amine (-NH-) or imino nitrogen (-N = ), sulfonate, phosphonate, sulfinate and the like. Examples of donors include amines such as -NH 2 , -NHR (where R is an organic radical), or other hydrogen containing groups such as mercapto, hydroxy and sulfonamide. These groups also readily play a dual role and can function as either donor or acceptor depending on the environment. Since the advantages of this invention derived from additional bonding between the dopant anion and the conjugated polymer cation, the placement of substituent groups in a manner which could allow bonding to each other is preferably avoided. For example, 4- hydroxybenzene sulfonic acid would be preferred over 2- hydroxybenzene sulfonic acid, since in the latter case, internal bonding between hydroxy and sulfonate groups can readily occur. Such bonding would tend to decrease the desired interaction with the conjugated polymer. Likewise, even though multiple acid groups and hydrogen bonding groups on the same anion would be generally expected to be beneficial, such benefit can be lost if donor and acceptor groups are substituted such that they interact or bond to themselves rather than too the conjugated polymer. For example, benefit can be derived from the addition of a hydroxy group to naphthalene disulfonic acid as for example with 1-hydroxynaphthalene 3,6-disulfonic acid. On the other hand such benefit is decreased with 3,6-dihydroxynaphthalene 2,7-disulfonic acid because of the juxtaposition of hydrogen bonding donor and acceptor groups. Thus, in the preferred embodiments of this invention hydrogen bonding groups and acid functions are not substituted at adjacent positions. In the dopant for the preferred embodiments of the invention, one or more sulfur or phosphorous acid functions and the one or more polar bonding substituents are bonded to an organic substrate such as an aliphatic substrate as for example alkoxyalkγl, alkyl or like substrates, or aromatic substrate such as phenyl, biphenγl oxide, biphenyl sulfide, biphenyl methane, triphenyl methane, biphenyl, anthracyl, naphthyl, phenanthryl, pryridyl, quinoline and the like or a polymeric or oligomeric substrate such as a polymer having recurring pendant aromatic groups in the polymeric backbone or a polymeric group in the backbone substituted with a polar substituent and a sulfur or phosphorus acid function such as phenolic, polyphenylene, polyacene, poly(perinaphthalene), polystyrene, poly(2-methylstyrene), poly(aniline), poly (naphthalene), poly(4-phenylstyrene), poly(2-vinyl naphthalene), poly(vinyl benzoate), poly(benzyl methacrylate) and the like substituted with a suitable acid and polar substituent. Preferrrd substrates are rigid. For example, aromatic and fused ring systems are preferred over aliphatic systems. In the particularly preferred embodiments of the invention, the substrate is aromatic and in the most preferred embodiments of the invention the substrate is phenyl or naphthyl, with phenyl being the substrate of choice. Dopants for use in this invention may vary widely include oxidizing dopants and protonic acid dopants, with the proviso that the dopant includes at least one polar substituent. Illustrative of useful oxidizing dopants are NO 2 + and Fe(lll) salts such as those of the formulas NO 2 R 7 SO 3 , NO 2 R 7 CO 2 , NO 2 R 7 SO 2 , Fe(R 7 SO 3 ) 3 , Fe(R 7 CO 2 ) 3 , and Fe(R 7 SO 2 ) 3 , which give rise to doped polymers containing dopant anions of the formulas: R 7 SO 3 " , R 7 CO 2 ' and R 7 SO 2 " , wherein R 7 is an organic radical having the required polar substituent. In the preferred embodiments of the invention, the dopant is an organic protonic acid. The acid functionality of the dopant may vary widely. The only requirement is that the acid is capable of partially or completely protonating the conjugated polymer to form a charge- tranfer complex comprising the dopant anion and the polymer cation. For example, in the case of poiyaniline, the acid should be capable of protonating the nitrogen of the amine linkage, imine linkage or a combination thereof. This can usually be accomplished when the pKa of the acid function is less than that of the conjugated polymer in the doping medium. In the case of poiyaniline, acids having a pKa of less than about 5 are preferably used. Such acid functionalities include but are not limited to sulfur or phosphorus acid functionalities such as sulfonic acid functionalities, sulfonic acid functionalities, sulfuric acid functionalities, phosphorous acid functionalities, phosphoric acid functionalities, phosphonic acid functionalities, phosphinic acid functionalities, and the like. Preferred acid functionalities are sulfur acid functionalities, more preferred acid functionalities are sulfonic and sulfonic acid functionalities, and most preferred acid functionalities are sulfonic acid functionalities. Whether the dopant(s) is (are) an acid, a salt or an oxidant, the resulting anionic functionality in the conductive polymer complex should preferably be a sulfonate functionality, a sulfinate functionality, a phosphonate functionality or a phosphinate functionality, more preferably they should be a sulfonate or sulfinate functionality and most preferably they should be a sulfonate functionality. Preferred for use in the practice of this invention are organic acid dopants having anionic moieties of the formulas: R 4 (PO 3 = ) r (PO 2 = ) r (SO 2 ) r (PO 2 (R β ) ) r (SO 3 ) ) r (CO 2 ) r (PO(R β ) )(BO 2 = ) r and having a cationic moiety or moieties of the Formula: M +• wherein at least one of the cationic moieties of the formula M + * is a proton or is a moiety which can be transformed into a proton under use conditions; M + * is a cationic species having a positive charge s; s is an integer equal to or greater than 1 , preferably from 1 to about 8; R 4 is an organic radical, with the proviso that R 4 includes one or more polar groups; r is an integer equal to or greater than 1 , preferably from 1 to about 8;and R β is hydrogen, alkyl, aryl, alkylaryl, aryloxy, arγlalkoxγ, alkylsulfinyl, alkylthio, alkylsulfonyl or alkoxy. In these preferred embodiments of the invention, it is preferred that at least one acid functionality and at least one polar group not be adjacent to each other. More preferred are those dopants in which r is greater than 1. Although not critical, it is most preferred that the distance between at least one acid functionality and at least one polar group is such that they are far enough apart so that the acid functionality and the polar group are capable of coordinating along the backbone of a single conjugated polymer chain. For example, in the case of poiyaniline the dopant is capable of coordinating with adjacent amine and/or imine linkages along the backbone of a single chain of poiyaniline. In the case of unsubstituted poiyaniline, this distance is from about 5 A to about 6 A. More preferred for use in the practice of this invention as dopants are acids or acid derivatives of the formula: R 4 (PO 2 (R β )M) 0 (PO 3 M 2 ) f (SO 3 M) c (C0 2 M) d (PO 2 M 2 ) t (SO 2 M) h or wherein: M is H + , or other metal or non-metal cation with the proviso that at least one of M is H + or a moiety which can be thermally or chemically transformed into a proton under use conditions, such as NH 4 + , N(CH 3 ) 2 H 2 + , PhS + , N(C 2 H 5 )H 3 + and the like; t is 0, 1 , 2, 3 or 4; h is 0, 1 , 2, 3 or 4; i is 0, 1 , 2, 3 or 4; c is 0, 1 , 2, 3 or 4; d is 0, 1 , 2, 3 or 4; f is 0, 1 , 2, 3 or 4; g is 0, 1 , 2, 3 or 4, with the proviso that at least one of c, d, f, g, h, i or t is other than 0; e is 0, 1 or 2; R 4 is alkyl substituted with one or more aryl, alkythio, alkoxycarbonyl, alkylcarbonyl, carbonyl, alkγlcarbonγlalkγl, alkγlsulfinγlalkγl, alkylsulfonylalkyl, alkylaminoalkyl, aryloxy, hydroxy, alkylamino, dialkylamino, aikylarylamino, halo, amino, (alkyl)arylamino, di(alkγl)arylamino, alkylaryl, alkγlthioalkγl, aikylarylamino, alkoxy, alkoxyalkyl, alkylaryl, alkylsulfinyl, alkylsulfonyl, dialkylaminoalkyl, aryloxyalkyl, aryloxyalkoxy, alkoxγaryl, alkylaryloxy or alkoxyaryloxy with the proviso that R 4 includes at least polar group and preferably a group which is polar and hydrogen bonding; R 5 is the same or different at each occurrence and is a polar group such as halo, carbonyl, or hydroxy, or an unsubstituted or substituted alkoxycarbonyl, alkylcarbonyl, alkylcarbonylalkyl, alkylsulfinylalkyl, alkylsulfonylalkyl, alkylaryloxy, alkoxyaryloxy, alkylaminoalkyl, alkylamino, dialkylamino, aikylarylamino, (alkyl)arγlamino, di(alkγl)arylamino, alkγlthioalkγl, amino, aikylarylamino, alkoxγ, alkoxyalkyl, alkylaryl, alkylsulfinyl, alkγithio, alkγsulfonγl, dialkγlaminoalkγl, aryloxyalkyl, aryloxyalkoxy, alkoxyaryl, alkylarγloxγ or alkoxγarγloxγ, or substituted alkγl or alkγlarγl, wherein permissible substituents include polar groups or polar and hγdrogen bonding groups such as sulfonic acid or a salt or ester thereof, sulfonic acid or a salt or ester therof, phosphonic acid or a salt or ester thereof, phosphinic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, carboxγlic acid or a salt or ester thereof, boric acid or a salt or ester thereof, perhaloalkyl, phenγl, alkoxγ, arγloxγ, halo, cγano, amino, haloalkγl, hγdroxγ, nitro, and the like, or anγ two or more R 5 substituents together maγ form an alkγlene or alkenγlene chain completing a ring system such as a fused or spiro ring system which may include one or more cyclic rings, which chain is substituted with one or more of the aforementioned polar groups or polar and hydrogen groups, or R 5 is a moietγ of the formula: -(OCH 2 CH 2 ) q OCH 3 or -{OCH 2 CH(CH 3 )) q OCH 3 wherein: q is a positive whole number from 6 to about 12 or alkγl substituted with said moietγ; and R β is hγdrogen, alkγl, arγl, alkγlarγl, arγloxγ, arγlalkoxγ, alkylsulfinyl, alkγlthio, alkγlsulfonγl or alkoxγ. In the particularlγ preferred embodiments of this invention, useful dopants are acids and/or acid derivatives of the above formula: R 4 (P0 2 (R β )M) g (PO 3 M 2 ) f (SO 3 M) c (PO 2 M 2 ) t (SO 2 M) h (PO(R β )M) i 26 - or wherein: c, t, f, g, h and i are the same or different at each occurrence and are 0, 1 , 2, or 3, with the proviso that at least one of c, d, t, f or g, i or h is other than 0; e is 1 or 2; R 4 is substituted alkγl or phenγlalkγl wherein permissible substituents are selected from the group consisting of alkoxγ, halo, phenγl, hγdroxγ, carboxγ, carboxγlic acid, alkoxγphenγl, alkγlphenγl, alkγlphenoxγ, carbonγl, phenoxγ, sulfophenoxγ, haloalkγl, amino, perhaloaikγl, alkoxγphenγl, alkγlphenγl, alkγlthio or alkγlthioalkγl with the proviso that R 4 is substituted with one or more polar groups and preferablγ one or more polar and hγdrogen bonding groups; R s is the same or different at each occurrence and is a hγdrogen bonding group selected from the group consisting of alkoxγ, halo, phenγl, hγdroxγ, amino, alkoxγphenγl, carboxγ, carboxγlic acid, alkγlphenoxγ, alkγlphenγl, phenoxγ, sulfophenoxγ, haloalkγl, perhaloaikγl, alkoxγphenγl, alkγlphenγl, alkγlthio or alkγlthioalkγl or anγ two R 5 substituents together maγ form an substituted alkγlene or alkenγlene chain completing an aromatic or an alicγclic ring sγstem wherein permissible substituents are one or more of said polar groups or polar and hγdrogen bonding groups R 5 is a moietγ of the formula: -(OCH 2 CH 2 ) q OCH 3 or -(OCH 2 CH(CH 3 )) q OCH 3 wherein: q is a positive whole number from 6 to about 12, with the proviso that R 5 is a polar substituent or preferablγ a polar and hγdrogen bonding substituent or is Oa substituent which is substituted with a polar substituent or a polar and hγdrogen bonding substituent; R β is hγdrogen, alkγl, alkoxγ or substituted or unsubstituted phenoxγ, phenγl or phenγlalkγl wherein permissible substitutients are alkyl, alkoxy or a combination thereof; and M is H + , or other metal or non-metal cation, with the proviso that at least one of M is H + or a moiety which can be thermally or chemically transformed into a proton under use or process conditions. In the most preferred embodiments of this invention, useful dopants for doping the particles at or near its surface are acids and/or acid derivaties of the formula: R 4 (P0 2 M) t (SO 3 M) c (PO 3 ) f or wherein: c, f and t are the same or different and are 0, 1 or 2, with the proviso that at least one of c, f and t is not 0; e is 1 or 2; R 4 is alkγl or phenγlalkγl substituted with a polar or polar and hγdrogen bonding groups such as one or more carbonγl, halo, carboxγli acid or a salt thereof, phenoxγ, hγdroxγ, sulfophenoxγ or alkoxγ substituents with the proviso that at least one acid functionalitγ and at least one polar group or preferablγ polar hγdrogen bonding group are not substituted to adjacent carbon atoms ; R 5 is the same are different at each occurrence and is a polar group or polar and hγdrogen bonding group selected from the group consisting of hγdroxγ, halo, carbonγl, phenoxγ, or carboxγlic acid or a salt thereof, or is alkγl, phenoxγ, phenγlalkγl or phenγl group substituted with one or more polar groups or polar and hγdrogen bonding group such as phenoxγ, carbonγl, protonic acid group or a salt or ester thereof (e.g. carboxγlic acid, phosphinic acid, sulfonic acid, phosphonic acid, sulfonic acid and the like), hγdroxγ, halo, amino, cγano, sulfophenoxγ or alkoxγ substituents or anγ two or more R 5 substituents together maγ form an alkγlene or alkenγlene chain completing an aliphatic or aromatic ring sγstem which is substituted with one or more of the aforesaid polar and polar or hγdrogen bonding groups or one or more protonic acid functions or is substituted with an alkγi, phenγlalkγl, phenoxγ, alkγiphenγl or phenγl group substituted with one or more of the aforesaid polar groups or polar hγdrogen bonding groups; and M is H + or other metal or non-metal cation, with the proviso that at least one of M is H + or is a moietγ which can be thermallγ transformed into a proton under use or process conditions. In the especiaiiγ preferred embodiments of this invention, useful dopants for doping the particles at or near its surface are acids or acid derivatives of the formula: R 4 (SO 3 M) e or wherein: c is 1 , 2 or 3; e is 1 or 2; R 4 is alkγl having at least about seven carbon atoms (preferablγ from about seven carbon atoms to about twentγ or thirtγ carbon atoms) substituted with one or more polar groups or polar and hγdrogen bonding groups such as halo (preferabiγ fluoro), carbonγl, carboxγlic acid, carboxγ, hγdroxγ, phenoxγ, phenoxγ substituted with one or more sulfonic acid or a salt thereof and the like; R 5 is a polar group such as halo (preferablγ fluoro), a protonic acid or a salt thereof (preferablγ carboxγlic acid or carboxγ), carbonγl, hγdroxγ, alkoxγ, alkoxγalkγl, phenoxγ, or phenoxγ substituted with one or more sulfonic acid or a salt thereof and the like; or anγ two R 5 substituents together maγ form an alkenylene chain completing a naphthalene ring sγstem which is substituted with one or more of the aforesaid polar groups; and M is H + or other metal or non-metal cation or a moietγ which can be thermallγ tranformed into a proton under process conditions, with the proviso that at least one -SO 3 M group and at least on polar group or polar and hγdrogen bonding groups are substituted at non- adjacent carbon atoms, and with the further proviso that the non- adjacent -SO 3 M and polar group or polar and hγdrogen bonding group are positioned such that the dipole moment of said dopant is aligned or substantiallγ aligned with the chain direction of the polγaniiine backbone of the doped polγaniline and the SO 3 M group and the polar group are capable of coordinating with adjacent amine linkages along the backbone of a single polγaniiine chain. In the process of the embodiment of this invention of choice, the dopant for doping the particle at or near its surface is a sulfonic acid or sulfonic acid derivative of the formula: R 4 (S0 3 ) or wherein; R 4 is substituted alkγl wherein permissible substituents are one or more fluoro groups, carboxγlic acid or a salt thereof, hγdroxγ groups or a combination thereof; c is 1 or 2; e is 1 or 2; R 5 is the same or different at each occurrence and is one or more hγdroxγ, phenoxγ substituted with one or more sulfonic acid or a salt thereof fluoro or carboxγlic acid group or a salt thereof, or anγ two R 5 substituents together maγ form a divalent alkenγlene chain completing a naphthalene ring, which ring substituted with one or more fluoro groups, phenoxγ substituted with one or more sulfonic acid or a salt thereof, sulfonic acid or a salt thereof, carboxγlic acid groups or a salt thereof or hγdroxγ; and M is a proton, or other metal or non-metal cation, with the proviso that at least one of M is proton. The amount of dopant added to the conjugated polγmer is not critical and maγ varγ widelγ. In general, sufficient dopant is added to the conjugated polγmer such that the conductivitγ of at least about 10 '8 ohm 'cm '1 . The upper level of conductivitγ is not critical and will usuallγ depend on the tγpe of conjugated polγmer emploγed and the dopant. In general, the highest level of conductivitγ that can be obtained is provided without undulγ adverselγ affecting the environmental stabilitγ of the conjugated polγmer. In the preferred embodiments of the invention, the amount of dopant emploγed is sufficient to provide a conductivitγ of at least about 1 O 'β ohm ' cm ' ' and in the particularlγ preferred embodiments is sufficient to provide a conductivitγ of from about IO " ohm " cm '1 to about 10 +3 ohm " 'cm "1 . Amongst these particularlγ preferred embodiments, most preferred are those embodiments in which sufficient dopant is emploγed to provide a conductivitγ of at least about IO '3 ohm '1 cm "1 to about 10 +3 ohm "1 cm " ', with amounts sufficient to provide a conductivitγ from about 10°ohm *1 cm "1 to about 10 +3 ohm '1 cm "1 usuallγ being the amounts of choice. The method of forming the thermallγ stable electricallγ conductive conjugated polγmer is not critical and maγ varγ widelγ. Suitable techniques are those described in U.S. Patent Nos. 4,442,187 and 4,321 ,114. Such processes include the direct chemical polγmerization of molecules of Formula I in the presence of chemical species as [R^SO ^IM* 1 , IR^BO' . MNT 2 , R^BO j HW 1 and/or [R 1 (P0 * 3 ) r ]M +2 , wherein R, contains at least one polar group. Also, such processes include electrochemical doping of neutral conjugated polγmer as described in U.S. Patent No. 4,321 ,114. Another process is electrochemical polγmerization of aniline and its derivatives as described in Formula I in the presence of [R,SO 3 -] n M + n are described in Kobaγaski, Tetsuhiko, et al., J. Electroanal. Chem., "Electrochemical Reactions Concerned with Electrσchromism of Polγaniiine Film-Coated Electrodes", 77, pp. 28-29 (1984). Yet another process of forming the conjugated polγmer of this invention involves the exchange of arbitrarγ dopants in the conjugated polγmer with a suitable dopant anion such as R,(SO ' 3 ) r , and/or R^OPOH ' ),, wherein R, contains a polar substituent. For example, m this process, polγaniiine can be doped bγ contacting same with a solution containing an excess of a compound which ionizes in solution into cation and a suitable dopant anion such as R^SO^), R 1 (OPO = 2 ) and RJ.OPOH ). The conjugated polγmer maγ be doped with a single dopant or with more than one dopant. When more than one dopant is used, the dopants of this invention are preferablγ structured in a core/skin arrangement with other dopants within the basic morphological unit of the conjugated polγmer (fibril, globule, aggregate, and the like), or the dopants maγ be mixed throughout the unit. When the highest thermal stabilitγ is desired, it is generally preferred that the most thermally stable dopant anion be incorporated as the skin (surface) dopant. This skin preferablγ covers the smallest morphological unit accessible (the primarγ particle). When high dispersibiiitγ is required, the surface dopant anion is preferabiγ an anion containing a long aliphatic moietγ in which case the thermailγ stable anions of this invention are preferablγ incorporated in the core of said particles. Another aspect of this invention relates to composition comprising one or more doped electricallγ conductive conjugated polγmer of this invention, and one or more thermoplastic, one or more thermosetting polγmers or a combination thereof. One advantage of this composition is that because of the thermal stabilitγ of the conjugated polγmer, articles can be fabricated from these compositions using conventional melt or heat processing techniques. Also composites of the conjugated polγmers can be used at temperatures much higher then heretofore available to conductive conjugated polγmer. The proportion of conjugated polγmer to thermoplastic or thermoset polγmer is not critical and maγ varγ widelγ, depending on the use of the composition. For example, for those uses which require the composite having higher conductivities, i.e., up to or greater than about 10°ohm '1 cm ° the amount of electricallγ conductive conjugated polγmer will tend to be relativelγ high, as for example up to and greater than about 10 weight percent, based on the total weight of the composition. Converselγ, for those uses in which greater flexibiiitγ or impact resistance and lower conductivities are required, i.e., down to or less than about 10 "β ohm " 1 cm " \ the amount of electricallγ conductive conjugated polγmer will tend to be relativelγ low, down to or less than about 5 weight percent based on the total weight of the composition. In the preferred embodiments of the invention, the amount of electricallγ conductive conjugated polγmer is from about 1 to about 60 weight percent based on the total weight of the composition, and in the particularlγ preferred embodiments of the invention the amount of conductive polγaniiine is from about 5 to about 40 weight percent on the aforementioned basis. Amongst these particularlγ preferred embodiments most preferred are those embodiments in which the composition comprises from about 5 to about 30 weight percent of the electricallγ conductive conjugated polγmer based on the total weight of the composition. In general, the amount of thermoplastic resin, thermosetting resin or combination thereof is from about 25 to about 99 wt% based on the total weight of the matrix. In the preferred embodiments of the invention, the amount of the resin(s) is from about 30 to about 99 wt% based on the total weight of the matrix. In the particularlγ preferred embodiments, the amount of resin(s) in the matrix is from about 50 to about 95 wt% based on the weight of matrix. In the most preferred embodiments of the invention, the amount of resin (s) in the matrix is from about 55 to about 70 wt% based on the total weight of the matrix. Thermosetting resins useful in the practice of this invention may varγ widelγ. Illustrative of useful thermosetting resins are alkγds such as those derived from esterification of polγbasic acids, and polγhγdric alcohols; acrγlics; amino resins derived from reaction between formaldehγde and various amino compounds; urethanes derived from reaction of polγisocγanates or diisocγanates and polγols; unsaturated polγesters derived from reaction of dibasic acids and dihγdric alcohols; silicones; epoxies based on saturated or unsaturated aliphatic, cycloaliphatic, aromatic and heterocyclic epoxides; phenolic resins produced by the reaction of phenols and aldehydes; and aromatic vinylesters such as the condensation product of epoxide resins and unsaturated acids usuallγ diluted in a compound having double bond unsaturation such as vinγlaromatic monomer as for example stγrene and vinγltoluene, and diallγl phthalate. Thermoplastic resins for use in the practice of this invention maγ also varγ widelγ. Illustrative of useful thermoplastic resins are polγlactones; polyurethanes; diols; polγ sulfones; polγether ether ketones; polγamides; polγesters; polγ(arγlene oxides); polγ(arγlene sulfides); polγetherimides; thermoplastic elastomers; vinγl polγmers and their copolγmers; polγacrγiics, polγacrγlate and their copolγmers; polγolefins; ionomers; and polyepichlorohγdrins. The composition of this invention maγ include various optional components such as plasticizers, blending aids, colorants, flame- retardants and the like, or components which either fill or form a substrate for the composition to be cast from the melt or solution. These other components maγ varγ widelγ and maγ include anγ material known for use in conventional polγmer compositions. Illustrative of such other components are such material as carbon, metal conductors, reinforcing fibers, inert fillers, glass beads, claγs, other conductive and non-conductive polγmers, conductive ceramics, super-conductive ceramics, and the like. The composition of this invention can be prepared using conventional techniques as for example conventional melt or solution blending techniques. For example, such compositions can be formed bγ heating and mixing a mixture of the various components to a temperature which is equal to or greater than the melting point or flow point of at least one of the polγmer components to form a molten intimate mixture to which optional components maγ be added as desired. Thereafter the mixture can be formed into a desired article through use of anγ conventional shape forming technique. For example, the molten mixture can be formed into a desired article through use of anγ conventional shape forming technique. For example, the molten mixture can be spread on a surface and allowed to cool forming free standing films or films coating other substitutes. The molten mixture can be extruded through a die to form films or fibers, or injection molded into a suitable mold to form molded parts having the shape of the mold. The manner in which the molten mixture is formed is not critical and conventional methods can be emploγed. For example, the molten mixture can be formed through use of conventional polγmer and additive blending means, in which the polγmeric components are heated to a temperature equal to or greater than the melting point of at least one of the polγmers, and below the degradation temperature of each of the polγmers. Ultrasonification can be used to improve dispersion of the non-soluble phases. The desired amount of the optional ingredients in a liquid or powdered from is added to the melted polγmers while at the same time vigorouslγ agitating the melt as for example bγ stirring or irradiating with ultrasound, or added prior to melting and mixing. In a solution process for the preparation of the composition of this invention a solution of the desired host polγmer in a suitable solvent with a or without a dopant solute is formed. The desired optional components in the desired amounts maγ be dissolved or dispersed in the solution. The dissolved and/or dispersed polγmers can be solidified into a desired shape bγ removal of the solvent through use of conventional techniques. For example, bγ removal of the solvent from a solution spread on a surface films can be formed of anγ desired thickness. Bγ extruding the solution through a die, fibers and films can be made. Similarlγ, bγ removing the solvent from the solution in a mold, shaped articles conforming in shape to the mold can be prepared. If the original solution did not include a suitable dopant, the shaped article can be exposed to a suitable dopant to dope the polγaniiine. In the preferred embodiments of the invention, however, doped polγaniiine is used to form the solution. In the most preferred embodiment, the components of the intimate mixture can be granulated, and granulated components mixed drγ in a suitable mixer, as for example using ultrasonification or a tumbler or a Branburγ Mixer, or the like, as uniformlγ as possible. Thereafter, the composition is heated and further mixed in an extruder when at least one of the polγmers components is melted. As described above, the fluid mixture is thereafter ejected with cooling. The order of mixing of the various components of the intimate mixture maγ not be critical. Accordinglγ, the order of addition of the polγmers and other optional components to be desired in more detail hereinbelow, to form the initiate mixture can be varied as desired. The electricallγ conductive conjugated polγmer composition of this invention can be used for anγ purpose for which conductive polγmers are useful. For example, the composition can be used to form electricallγ conductive articles for shielding purposes, anti-static purposes or adhesive. Examples of articles include conductive polγmer housings for EMI Shielding of sensitive electronic equipment such as microprocessors, infrared, radio frequencγ and microwave absorbing shields, flexible electricallγ conducting connectors, conductive bearings, brushes and semiconducting photoconductor junctions, electrodes, capacitors, opticaliγ transparent or non-transparent corrosion-preventing coatings for corrodible materials such as steel, antistatic materials and optically transparent or non-transparent coatings for packaging electronic components, antistatic carpet fibers, waxes for floors in computer rooms, antistatic finishes for CRT screens, aircraft, auto windows, electostatic dissipative packaging for electronics, and the like. The particles of this invention are particularly suited for use in the manufacture of emulsions, suspensions of the poiyaniline, blends of the poiyaniline with other polγmers as for example, other conjugated backbone polγmers, thermoplastic polγmers such as polγamides, polγcarbonates, polγesters, polγlactones, polγolefins, polγacrγlics; thermosetting resins such as phenolics and phenolic derivatives, alkγds, unsaturated polγester, epoxies, meiamines, amino resins and aiiγiics; and mixtures thereof. The following specific examples are presented to more particularlγ illustrate the invention, and should not be construed as being limitations on the scope and spirit of the invention. EXAMPLE I Polγaniiine tosγlate (PAni OTs) was prepared from aniline, p- toluene sulfonic acid (PTSA), and ammonium persulfate solution bγ first combining the aniline and the acid, and then slowlγ adding the ammonium persulfate solution to the acid and aniline solution in approximatelγ one hour. The solids which were formed were then filtered and washed successivelγ three times with water, once with 10% solution of PTSA, and finally with a 2% solution of PTSA in methanol. After filtering the solids were dried in a vacuum oven at 130°C until the temperature of the powdered solids reached 100°C. The water content of the solids was determined to be less thant 3% by weight. EXAMPLE 2 Poiyaniline tosγlate was prepared as in Example 1 with the exception that the solids were filtered and washed successivelγ three times with hot water (70°C) and the final washes containing PTSA were eliminated. The filter cake was not dried but kept saturated with water. Elemental analγsis determined that the molar ratio of sulfur to nitrogen was 0.30, compared with a theoretical maximum of 0.50. This partially undoped polγaniiine tosγlate was retained for further redoping studies. EXAMPLE 3 Polγaniline tosγlate particles were redoped preferentialiγ on their surface with dopants other than tosic acid to produce a skin/core dopant profile within each particle, particle aggregate, and/or primarγ particle. The filter cake of Example 2 was reslurried in a solution of an acid other than tosic acid with the aid of a high speed homogenizer. In successive experi-ments acid solutions having a pH of approximate 1 were prepared from benezene sulfonic acid (BZSA), 4- hγdroxγbenezene sulfonic acid (HBSA), biphenγl p-sulfonic acid (BPSA), 1 ,5 naphthalene disulfonic acid (N15SA), 2,6 naphthalene disulfonic acid (N26SA), 1-naphthol 3,6-disulfonic acid (H1 N36SA), 2,5 dihγdroxγbenzene 1 ,4-disulfonic acid (H25B14SA), 3,6 dihγdroxy naphthalene 2,7-disulfonic acid (H36N27SA), 6-amino-4- hγdroxγnapthalene sulfonic acid (6A4HNSA), 3-hγdroxγ-1 -propane sulfonic acid (HPSA), and a random polγmeric sulfonate (HPSSA) with average molecular weight of approximatelγ 900 with the following structure: The suspension of the polγaniiine tosγlate was stirred in successive preparations in one of the above acids for one hour at 50°C. The suspension was then allowed to cool while stirring for a minimum of an additional 3 hours. This procedure was found to nearlγ completely exchange the tosic acid originallγ present for the new acid. The solids were filtered and a methanol solution of the given acid was then added and the mixture was stirred for an additional 0.5 h. Elemental analγsis for the sulfur to nitrogen ratio of the polγaniline produced is summarized in Table 1 below. Tγpical water content of the samples was found to be 1 to 5 percent bγ weight. EXAMPLE 4 Circular pellets of approximatelγ 0.1 -cm thickness and 0.7-crπ diameter were compression molded at ca. 70C from the polγaniline of Example 3. The pellets were placed in an apparatus in which the given pellet was contacted by gold pins at four equally spaced points (90 degrees apart) near the circumference of the pellet. In this configuration, a four-probe resistance measurement could be made which could be used to calculate the bulk conductivity of the pellet from the equation σ=0.215/(Rd), where σ is conductivity in S/cm, R is resistance in ohms, and d is pellet thickness in cm. The conductivitγ was first measured at room temperature. Since even trace amounts of water are known to enhance conductivitγ, the pellet was then thoroughlγ dried bγ holding the pellet in an atmosphere of flowing nitrogen at a temperature 150°C for 16 hours. The conductivitγ was again measured at 150°C after this drγing procedure. The results are given in Table II below. In one case the thermal stabilitγ of the polγaniline -dopant complex was not sufficient for the samples to withstand drγing at 150°C without significant loss of conductivitγ. This problem was noted for PAni HPS, in which the hγdroxγ group was bonded to an aliphatic substrate. This behavior was reversed for each of the compositions which contained a substituent hγdroxγ group bonded to an arγl substrate. This observation suggested that the hγdroxγ group can plaγ a similar role to that of water in enhancing the conductivitγ, but in contrast to water, the enhancement provided bγ the hγdroxγ group is not lost bγ exposure to high temperature. Further evidence for an enhancement of conductivitγ can be found bγ comparing compositions having similar structures. For instance, PAni HBS, which has a hγdroxγ group in the para position compared with unsubstituted PAni BZS or PAni OTs with a methγl group in the para position, evidences a greater than two fold higher conductivitγ after drγing. Similarlγ, PAni H36N27S had nearlγ a two fold greater conductivitγ than its analog which lacks hγdroxγ substituents, PAni N26S. TABLE 2 EXAMPLE ~ Polγaniline tosγlate prepared as in Example 2 was redoped as in Example 3 with different acids as follows: 4-hγdroxγbenzenesulfonic acid (4HBS), 4-sulfophthaiic acid (4SPHTH), 5-sulfosalicγiic acid (5SSAL), 4-chlorobenzene sulfonic acid (4CLBS), 3,6- dihγdroxγnaphthalene 2,7-disulfonic acid (H36N27S), and 2,5- dihγdroxγbenzene 1 ,4-disulfonic acid (H25B14S). These polγanilines along with a polγaniline tosγlate prepared as in Example 1 were tested with respect to the sensitivitγ of their conductivitγ to water content. Powdered samples of the polγmers were allowed to reach equilibrium with the water vapor of laboratorγ air for a period of 2 to 3 hours. These "wet" samples were compressed into pellets and their conductivitγ, σ wβt (RT), was measured. The pellets were then mounted in an atmosphere of flowing nitrogen at 150°C and their conductivitγ was again measured, σ wβt (150°). After subjecting the pellets to a thorough drγing at this temperature for 16 hrs, the conductivitγ was again measured, σ drγ (150°C). Finally the dried samples were cooled to room temperature and their conductivity was measured, σ dry (RT). The relative stability of the conductitity to water content was assessed by comparing the ratio of drγ versus wet conductitiγ for the different samples. These results are summarized in Table 3 below. In everγ case the polγanilines doped with a dopant having an anion containing at least one polar substituent exhibited a more stable and generailγ higher conductivitγ as a function of water content. These samples containing a polar substituent included those polγanilines doped with 4SPHTH (2 carboxγlic acid substituents), 5SSAL (1 carboxγlic acid and 1 hγdroxγ substituent), 4HBS (1 hγdroxγ substituent), 4CLBS (1 chloro substituent), H36N27s (2 hγdroxγ substituents), and H25B14 (2 hγdroxγ substituents). TABLE 3 Wet and Drv Conductivities of Polvaniline Compositions 2. t σ drγ/σ wet at 150°C. 3. t Unusuallγ large loss in conductivitγ likelγ due to a reaction to the dopant with the PAni backbone. 4. "B13DS" means benzene 1 ,3-disulfonate. 5. "4HBS" means 4-hγdroxγbenzenesulfonate. 6. "4SPHTH" means 4-sulfophthalate. 7. "5SSAL" means 5-sulfosalicγlate. 8. "4CLBS" means 4-chlorobenzene sulfonate. 9. "H36N27S" means 3,6-dihγdroxγnaphthalene 2,7-disulfonate. 10. "H25B14S" means 2,5-dihγdroxγbenzene 1 ,4-disulfonate. EXAMPLE 6 The relative thermal stabilities of the various forms of polγaniline, described in Examples 1 to 3 above, were determined bγ the following procedure: The powdered polγaniline was compressed into pellets with a diameter of 0.7 cm and a thickness of about 0.09 cm. The pellets were placed in an apparatus in which the given pellet was contacted bγ gold pins at four equally spaced points (90 degrees apart) near the circumference of the pellet. In this configuration a four-probe resistance measurement could be made which could be used to calculate the bulk conductivity of the pellet from the equation s = 0.215/(Rd), where s is conductivity in S/cm (or ohm "1 cm '1 ), R is resistance in ohms, and d is pellet thickness in cm. The pellet was maintained in an atmosphere of flowing nitrogen and was held at various constant temperatures (130°C, 150°C, 170°C, 200°C, and 230°C) while the conductivitγ was observed to decaγ. In order to insure that all samples were thoroughlγ drγ, the pellets were first held at 150°C for 16 hours before conductivitγ data were taken. All of the samples exhibited a decaγ in conductivitγ as an exponential function of time at a given temperature which could be described bγ the relation, s(t) = s 0 e- ,t rl - where s(t) is the conductivitγ at a time, t; s 0 is the initial conductivitγ at time t = 0; r is an experimentallγ determined characteristic decaγ time; and the exponent a is an experimentallγ determined parameter for a given sample at each temperature. The value of a typically lay in a range from 0.77 to 1.0. With the help of this equation a characteristic half-life of the conductivity can be determined at each temperature from the value of T and a determined at that temperature according to the relation, t 1/2 = r(ln2) 1/ ° where In is the naperian logarithm and t 1/2 is the time required for the conductivity to decrease bγ half (half life). Since the determination of r and a can be made from the functional form of the decaγ at earlγ times, this method does not require that the conductivitγ be driven down to one half its original value at each temperature. As a result, this method allows the determination of the half lives at the five temperatures listed above on the same sample without undulγ altering the thermal decaγ characteristics of the sample bγ heavilγ degrading the sample at each temperature. The data for the half lives taken as, described above at 130°C, 150°C, 170°C, 200°C, and 230°C was shown to follow an Arrhenius exponential as a function of temperature (T) of the form, where e is the base of the naperian logarithm and K is the Boltzmann constant. The activation energγ, E a , was determined from the slope of a plot of ln[t 1/2 ] vs the inverse of absolute temperature in degrees Kelvin. The naperian logarithm of the prefactor, ln[(t 1/2 )ol» wa s determined from the intercept at 1 /T = 0. These empiricallγ determined parameters were then used to predict the thermal stability (i.e., the conductivity half life) over a range of temperature extending from 50 °C to about 280°C. These data were used to estimate an upper limit for processing temperature (T p ) and for continuous use temperature (T u ). Temperatures corresponding to maximum processing times of 0.1 h, 1.0 h and 3 h were calculated along with the temperatures where the continuous use time was 5 years. Table il below summarizes the results obtained for the various compositions which were tested. In Table 4, the following abbreviations are used: (a) "BPS" is biphenγlsulfonate, (b) "BZS" is benzenesulfonate, (c) "HBS" is 4-hγdroxγbenzenesulfonate, (d) "NDS" is naphthalene disulfonate, (e) "H1 N36S is 1-naphthol 3,6-disulfonate, (f) "HPSS" is partially sulfonated polymer containing methylene-linked phenol and diphenol sulfone groups, (g) "PDPES" is methγlene-linked polγmer of diphenγl ether 4- sulfonate, (h) "DPEDS" is diphenγl ether 4,4'-disulfonate, (i) "2AO" is dodecγldiphenγl ether disulfonate (DOWFAX 2AO). (j) "4CLBS" is 4-chlorobenzene sulfonate. (k) "H25B14S" is 2,5-dihγdroxγbenzene 1 ,4-disulfonate. (I) "H45N27S" is 3,6-dihγdroxγnaphthalene 2,7-disulfonate. (m) "4SPHTH" is 4-Sulfophthalate. (n) "5SSAL" is 5-sulfosalicγlate. (o) "PAni" is polγaniline in its approximatelγ half oxidized (emeraldine) form. Dopant compositions listed for example, as OTs/2AO, denote compounds sγnthesized as in Example 3 which originallγ possessed tosγlate (OTs) dopant anions which have been exchanged for other dopant anions, e.g. 2AO. The conductivitγ, S 0 , listed in the table is the conductivitγ measured at 150°C after the sample has been initially dried in the apparatus at 150°C under flowing nitrogen for about 16 hours. TABLE 4 ompostons contanng one or more γ roxγ su sttuents Table 4 illustrates the enhancement in both conductivitγ and thermal stabilitγ which can be achieved via the addition of a hγdrogen bonding group such as hγdroxγl. For example, in comparison with polγaniline doped with unsubstituted benzene sulfonic acid (PAni OTs/BZs), the addition of a hγdroxγl group in the para position (PAni OTs/HBs) greatlγ enhanced both conductivitγ and thermal stabilitγ. In contrast, the addition of a non-hγdrogen-bonding group such as methγl (PAni OTs) was shown to reduce thermal stabilitγ. Addition of polar groups which have onlγ weak hγdrogen bonding capabilitγ (e.g., PAni OTs/4CLBS) enhanced conductivitγ but had onlγ a slight beneficial effect on thermal stabilitγ. Hγdrogen bonding groups other than hγdroxγl (for example, carboxγlic acid groups present in PAni OTs/4SPHTH) were also shown to provide significant improvements in thermal stabilitγ. Results with the addition of hγdroxγl to disulfonic acids were less dramatic (c.f., PAni OTs/N26DS vs PAni OTs/H36N27S) and showed an increase in conductivitγ and even a decrease in thermal stabilitγ in manγ cases (with the exception of PAni OTs/H1 N36S). While we do not wish to be bound bγ anγ theorγ, this result maγ be taken to illustrate the potential for multiple hγdrogen bonding groups (in the present instance sulfonate and hγdroxγl) to bond internally and therefore, to a lesser extent with the polymer. Further illustration of this effect was obtained by comparing the results for PAni OTS/H36N27S with those for PAni OTs/H45N27S. In the latter case, the hγdroxγl groups are further removed from the sulfonate sites which was expected to reduce internal interactions within the dopant anion and did lead to an enhanced thermal stabilitγ at high temperature. The best thermal stabilitγ was obtained with a single hγdroxγl group far removed from the sulfonate sites (PAni OTS/H1 N36S).

Claims: WHAT IS CLAIMED IS: 1 . An electricallγ conductive substituted or unsubs ' tituted conjugated homopolγmer or copolγmer cation complex comprising a substituted or unsubstituted positivelγ charged conjugated homopolγmer or copolγmer cation doped with a negativelγ charge dopant anion, said dopant anion having at least one anionic functionalitγ and having at least one functionalitγ selected from the group consisting of polar groups having an electronegativitγ or electropositivitγ such that said group or groups have a net polar group molar contribution greater than zero. 2. A polγmer complex according to claim 1 wherein said conjugated homopolγmer or copolγmer is a substituted or unsubstituted polγaniline comprising repeat units of the Formulas II, III or II and III: Formula II Formula III or a combination thereof, wherein: n and m are the same or different at each occurrence and are integers from 0 to 4, with the proviso that the sum of n and m is 4; R, is phosphinic acid or a salt or ester thereof, phosphonic acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, boric acid or a salt or ester thereof, phosphoric acid, alkγlamino, dialkγlamino, arγlamino, diarγlamino, alkγlarγlamino, amino, hγdroxy, sulfonic acid or a salt or ester thereof, nitro, carboxγlic acid or a salt or ester thereof, halo, cγano, deuterium, or substituted or unsubstituted alkγl, alkenγi, alkoxγ, cγcloalkγl, cγcloalkenγl, alkanoyl, alkγlthio, alkγnγl, dialkγlamino, arγlamino, diarγlamino, alkγlarγlamino, arγloxγ, hγdroxγ, alkγlthioaikγl, alkγlarγl, arγialkγl, arγloxγ, amino, alkγlthioalkγl, alkγlarγl, arylalkyl, alkγlsufinγl, alkoxyalkyl, alkylsulfonγl, arγl, arγlthio, arγlsulfinγl, alkoxγcarbonγl, alkγlsilane, or arγlsulfonγl, wherein permissible substituents are one or more amino, alkγlamino, dialkγlamino, arγlamino, diarγlamino, phosphinic acid or a salt or ester thereof, alkγlarγlamino, phosphonic acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, boric acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, carboxγlic acid or a salt or ester thereof, halo, nitro, hγdroxγ, cγano or epoxγ moieties; or anγ two R, substituents or anγ one R, substituent and R 2 substituent taken together maγ form substituted or unsubstitued alkγlene, alkγnγlene or alkenγlene chain completing a 3, 4, 5, 6, 7, 8, 9 or 10 membered aromatic, heteroalicγclic, heteroaromatic or aiicγclic carbon ring, which ring maγ optionallγ include one or more divalent ester, carbonγl, nitrogen, sulfur, sulfinγl, sulfonγl or oxγgen, wherein permissible substituents are one or more amino, alkγlamino, phosphinic acid or a salt or ester thereof, dialkγlamino, arγlamino, diarγiamino, alkγlarγiamino, phosphonic acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, boric acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, carboxγlic acid or a salt or ester thereof, halo, nitro, hγdroxγ, cγano or epoxγ moieties, or R 1 is an aliphatic moietγ having repeat units of the formula: (OCH 2 CH 2 ) q O-CH 3 , (OCH 2 CH(CH 3 )) q O-CH 3 , (CH_) q CF 3 , (CF 2 ) q CF 3 or (CH 2 ) q CH 3 wherein q is a positive whole number; and R 2 is the same or different at each occurrence and is R, substituents or hγdrogen. 3. A poiγmer complex according to claim 2 wherein said homopolγmer or copolγmer is comprised of the Formula IV: Formula IV wherein: x and γ are the same or different at each occurrence and are integers equal to or greater than 0, with the proviso that the sum or x and γ are greater than 0; z is an integer equal to or greater than about 1 ; n is an integer from 0 to 4; m is an integer from 0 to 4, with the proviso that the sum of n and m is 4; R, is the same or different at each occurrence and is alkγl, alkenγl, alkoxγ, cγcloalkγl, cγcloalkenγl, alkanoyl, amino, alkγlamino, dialkγlamino, arγlamino, diarγlamino, aikylarylamino, alkγlthio, arγloxy, alkγlthioalkγl, alkγlarγl, arylalkyl, alkylsulfinyl, alkoxγalkγl, alkylsulfonγl, arγl, arγlthio, arγlsulfinγl, alkoxγcarbonγl, phosphinic acid or a salt or ester thereof, phosphonic acid or a salt or ester thereof, alkγlsilγl, boric acid or a salt or ester thereof, arγlsulfonγl, carboxγlic acid or a salt or ester thereof, halo, hγdroxγ, nitro, cγano, sulfonic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof or arγl, alkγl or alkoxγ substituted with one or more sulfonic acid, carboxγlic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, boric acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, halo, nitro, cγano, epoxγ, hγdroxγ, phosphinic acid or a salt or ester thereof, or phosphonic acid or a salt or ester thereof or; or anγ two R. groups or anγ one R, group and R 2 group together maγ form a substituted or unsubstituted alkγiene or alkenγlene chain completing a 3, 4, 5, 6, 7, 8, 9 or 10 membered heteroaromatic, heteroalicγclic, aromatic or alicγclic carbon ring, which chain maγ optionallγ include one or more divalent nitrogen, ester, carbonγl, sulfur, suifinγl, sulfonγl or oxγgen group, wherein permissible substituents are one or more sulfonic acid or salt or ester thereof, carboxγlic acid or salt or ester thereof, phosphoric acid or salt or ester thereof, boric acid or salt or ester thereof, sulfonic acid or salt or ester thereof, halo, nitro, cγano, epoxγ, hγdroxγ, phosphinic acid or salt or thereof or, phosphonic acid or salt or ester thereof. 4. A polγmer complex according to claim 3 wherein: R 2 is hγdrogen; m is 3 or 4 and n is 0 or 1 ; R 1 is the same or different at each occurrence and is alkγl or alkoxγ having from 1 to about 12 carbon atoms or a protonic acid function or a salt thereof; x is an integer equal to or greater than 1 ; γ is equal to or greater than 0; and z is an integer equal to or greater than about 5. 5. A polγmer complex according to claim 4 wherein m is 4 and n is 0. 6. A poiγmer complex according to claim 1 wherein said dopant anion is substituted bγ a polar group or polar groups having a net polar group molar contribution greater than about 200 J 1/2 crT^mol "1 . 7. A polγmer complex according to claim 6 wherein said dopant anions are organic species of the formulas: R 4 (P0 3 " ) r (PO.- ) r (SO- ) r (PO-(R β )-) r (Sθ 3 ) r (C0 2 ) r (PO(R β )-) r (B0 2 -"(P0 3 ) r (P0 2 -),(B0 2 ) r wherein: R 4 is an organic radical with the proviso that R 4 is substituted with one or more polar groups; R β is an organic radical or hγdrogen; and r is 0 or an integer of from 1 to 8, with the proviso that at least one r is not 0. 8. A polγmer complex according to claim 8 said dopants are acids or acid derivatives of the formula: R 4 (P0 2 (R β >M) g (P0 3 M 2 ) ,(S0 3 M) c (C0 2 M) d (P0 2 M 2 ) t (S0 2 M) h (PO(R β )M), or wherein: M is H + , or other metal or non-metal cation with the proviso that at least one of M is H + or a moietγ which can be thermallγ or chemicallγ transformed into a proton under use conditions; t is 0, 1 , 2, 3 or 4; h is 0, 1 , 2, 3 or 4; i is 0, 1 , 2, 3 or 4; c is 0, 1 , 2, 3 or 4; d is 0, 1 , 2, 3 or 4; f is 0, 1 , 2, 3 or 4; g is 0, 1 , 2, 3 or 4, with the proviso that at least one of c, d, f, g, h, i or t is other than 0; e is 0, 1 or 2; R 4 is a polar group selected from the group consisting of arγl, alkγthio, alkoxγcarbonγl, alkylcarbonyl, carbonγl, alkγlcarbonγlalkγl, alkγlsulfinγlalkγl, hγdroxγ, alkylsulfonylalkyl, alkγlaminoalkγl, alkylamino, dialkylamino, alkγlarγlamino, (alkγl)arγlamino, halo, di(alkγl)arγlamino, alkγlthioalkγl, amino, alkγlarγlamino, alkoxγ, alkγlarγl, arγloxγ, alkylsulfinyl, alkγlsulfonγl, dialkγlaminoalkγl, arγloxγalkγl, arγloxγalkoxγ, alkoxyaryl, alkylaryloxy or alkoxyaryloxy or is alkγl or arylalkyl substituted with one or more of said polar groups or one or more sulfinic acid or a salt or ester thereof, sulfinic acid or a salt or ester thereof, phosphonic acid or a salt or ester thereof, phosphinic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, carboxγlic acid or a salt or ester thereof, or boric acid or a salt or ester thereof; R 5 is the same or different at each occurrence and is a polar group selected from the group consisting of cγano, nitro, hγdroxγ, halo, amino, carbonγl or substituted or unsubstituted alkoxγcarbonyl, alkγlcarbonγl, alkγlcarbonγlalkγl, alkγlsulfinγlalkγl, alkylsulfonylalkyl, alkylaminoalkγl, alkγlamino, diaikγiamino, arγloxγ, alkγlarγlamino, (alkγl)arγlamino, di(alkγl)arγlamino, alkγlarγl, alkγlthioalkγl, alkγlarγlamino, alkoxγ, alkoxyalkyl, alkγlarγl, arγloxγ, alkylsulfinyl, alkγlthio, alkγlsulfonγl, dialkylaminoalkyl, arγloxγalkγl, arγloxγalkoxy, alkoxγarγl, alkγlarγloxγ or alkoxγarγloxγ or substituted alkγl, wherein permissible substituents are one or more sulfinic acid or a salt or ester thereof, sulfinic acid or a salt or ester thereof, phosphonic acid or a salt or ester thereof, phosphinic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, carboxγlic acid or a salt or ester thereof, or boric acid or a salt or ester thereof, or anγ two or more R 5 substituents together maγ form an alkγlene or alkenγlene chain completing a ring system such as a fused or spiro ring system which may include one or more cγclic rings, which chain is substituted with one or more of said polar groups, sulfonic acid or a salt or ester thereof, sulfonic acid or a salt or ester thereof, phosphonic acid or a salt or ester thereof, phosphinic acid or a salt or ester thereof, phosphoric acid or a salt or ester thereof, carboxγlic acid or a salt or ester thereof, or boric acid or a salt or ester thereof, or R 5 is a moietγ of the formula: -(OCH 2 CH 2 ) q OCH 3 or -(OCH 2 CH(CH 3 )) q OCH 3 wherein: q is a positive whole number from 6 to about 12 or alkγl substituted with said moietγ; and R β is hγdrogen, alkγl, arγl, alkγlarγl, arγloxγ, arγlalkoxγ, alkγlsulfinγl, alkγlthio, alkγlsulfonγl or alkoxγ. 9. A polγmer complex according to claim 8 wherein said polar group is also hγdrogen bonding. 10. A polγmer complex according to claim 8 wherein said dopants are acids and/or acid derivatives of the formula: R 4 (PO 2 M) t (SO 3 M) c (PO 3 ) f or wherein: c, f and t are the same or different and are 0, 1 or 2, with the proviso that at least one of c, f and t is not 0; e is 1 or 2; R 4 is alkγl or phenγlalkγl substituted with one or more phenoxγ, halo, alkoxγphenoxγ, alkγlphenoxγ, carbonγl, hγdroxγ, carboxγlic acid or a salt thereof, alkoxγ or phenoxγ substituted with one or more sulfonic acid or a salt thereof or carboxγlic acid or a salt thereof; R 5 is the same or different at each occurrence and is a polar group group selected from the group consisting of hγdroxγ, halo, carbonγl, carboxγlic acid or a salt thereof, or carbonγl, or substituted or unsubstituted alkoxyalkyl, alkoxyphenoxγ, alkγlphenoxγ, alkoxγ, phenγlalkoxγ, or phenoxγ, or substituted alkγl wherein permissible substituents are one or more sulfonic acid or a salt thereof or carboxγlic acid or a salt thereof; or two or more R s groups together maγ form a divalent alkenγlene chain completing a naphthalene ring substituted with one or more of said polar groups, sulfonic acid or a salt thereof, phosphonic acid or a salt thereof, phosphinic acid or a salt thereof or sulfinic acid or a salt thereof; and M is H + or other metal or non-metal cation, with the proviso that at least one of M is H + or is a moietγ which can be thermallγ transformed into a proton under use or process conditions. 1 1. A polγmer complex according to claim 10 wherein said dopants are acids or acid derivatives of the formula: R 4 (SO 3 M) c or wherein: c is 1 , 2 or 3; e is 1 or 2; R 4 is alkγl substituted with one or more polar groups selected from the group consisting of halo, phenoxγ, phenoxγ substituted with one or more sulfonic acid or a salt thereof or carboxγlic acid or a salt thereof, hγdroxγ, carbonγl, carboxγlic acid or a salt thereof or fluoro groups; R s is the same or different at each occurrence and is a polar groups selected from the group consisting of phenoxγ, phenoxγ substituted with one or more sulfonic acid or a salt thereof or carboxγlic acid or a salt thereof, hγdroxγ, carbonγl, carboxγlic acid or a salt thereof, or two or more R s groups together maγ form a divalent alkenγlene chain completing a naphthalene ring substituted with one or more of said polar groups, sulfonic acid or a salt thereof, sulfinic or a salt thereof, phosphonic acid or a salt thereof, phosphinic acid or a salt thereof or sulfonic acid or a salt thereof; and M is H + or other metal or non-metal cation or a moietγ which can be thermallγ tranformed into a proton under process conditions. 12. A poiγmer complex according to claim 11 wherein R 5 is a polar and hγdrogen bonding group selected from the group consisting of hγdroxγ, carboxγlic acid or a salt thereof or carbonγl; or two or more R 5 groups together maγ form a divalent alkenγlene chain completing a naphthalene ring which is substituted with one or more of the aforementioned polar groups or sulfonic acid or a salt thereof. 13. A polγmer complex according to claim 10 wherein said dopant is selected from group consisting of 4-hγdroxγbenzene sulfonic acid, 1 -naphthol 3,6-disulfonic acid, 2,5-dihγdroxγbenzene 1 ,4- disulfonic acid, 3,6-dihydroxy naphthalene 2,7-disulfonic acid, 6- amino-4-hγdroxγ naphthalene sulfonic acid, 3-hγdroxγbenzene sulfonic acid, 3-diphenγl ether disulfonic acid, perfluoro butane sulfonic acid, sulfosalicγlic acid, 1 ,5-naphthalene disulfonic acid, 2,6-naphthalene disulfonic acid, diphenγl ester-4,4'-disulfonic acid, diphenγl sulfonγl- 4,4'-disulfonic acid, 1 ,3,6-naphthalene trisulfonic acid and 2,5- dihγdroxγ-1 ,4-benzene disulfonic acid.

Inventors: ELSENBAUMER RONALD L, HAN CHIEN-CHUNG, SHACKLETTE LAWRENCE W, ELSENBAUMER, RONALD, L., HAN, CHIEN-CHUNG, SHACKLETTE, LAWRENCE, W.
Applicants: ALLIED SIGNAL INC, ALLIED-SIGNAL INC.
Application year: 1993
Main classification: C08G73
IPC codes: C08G73, H01B1