Rare-earth metal-nickel hydrogen occlusive alloy ingot and method for production thereof

Abstract: A rare earth metal-nickel hydrogen occlusive alloy ingot contains 90 vol% or more of crystals having a crystal grain size of 1 to 50 µm as measured along a short axis of the crystal and 1 to 100 µm as measured along a long axis of the crystal. A method for producing the rare earth metal-nickel hydrogen occlusive alloy ingot involves melting (1) a rare earth metal-nickel alloy and uniformly solidifying (4,5) the alloy melt to have a thickness of 0.1 to 20 mm under cooling conditions of a cooling rate of 10 to 1000°C/sec and a sub-cooling degree of 10 to 500°C.

Description: BACKGROUND OF THE INVENTION This invention relates to a rare earth metal-nickel hydrogen occlusive alloy ingot having crystalline structures excellent in hydrogen storage and a method for producing same. Up to now, a hydrogen occlusive alloy ingot is prepared by a metal mold casting method of casting a molten alloy into a metal mold. On the other hand, a variety of additive elements such as cobalt, manganese or aluminum are usually added to the alloy for improving its characteristics such as hydrogen occluding characteristics. The document Journal of Alloys and Compounds, volume 180, March 25, 1992, Lausanne, CH, pages 37-54, T. Sakai et al. Rechargeable hydrogen batteries using rare-earth-based hydrogen storage alloys" discloses the examination of elecrochemical properties of low cost MmNi 5 -based hydrogen storage alloys. The used composition of e. g. MmNi 3.5 Co 0.7 Al 0.8 are produced with a columnar structure in the outer region and equiaxial structure in the inner region by using a water-cooled mold or by a melt spinning method. The document Data Base WPI, week 9042, Derwent Publications Ltd, London, GB, AN 90-318095/42 & JP-A-2 228 434 discloses hydrogen-occluding alloy production involving a varying ratio of metal exothermal occluding hydrogen to metal endothermally occluding hydrogen. The ribbon of Mm-Ni alloy revealed therein is produced by spraying the alloy melt through a nozzle with a diameter of 1.0 mm onto a Cu-roller rotating at 200 r.p.m. However, if the molten alloy is to be solidified by the metal mold casting method, the heat conduction through the casting mold determines the rate of heat removal during an initial stage of a heat removal process of the molten alloy. As solidification proceeds, the heat conduction between the casting mold and the solidifying phase or in the solidifying phase determines the rate of heat conduction. Even though the cooling capacity of the metal mold is increased, the inner portions of the ingot and those portions thereof in the vicinity of the casting mold are subjected to different cooling conditions. Such phenomenon is the more pronounced, the thicker the ingot thickness. The result is that in the case of a larger difference between the cooling conditions in the inner portions of the ingot and those in the vicinity of the ingot surface, microscopic segregation of additive elements, above all, is likely to occur. Besides, a homogenizing heat treatment process needs to be carried out for a prolonged period of time for homogenizing the crystal composition. On the other hand, the ingot is usually pulverized to a size of an order of tens of microns during the pulverization step in the course of the process for preparation of hydrogen occlusive alloy powders. However, the ingot produced by the metal mold casting method contains a phase rich in additive elements having a larger particle size and hence presenting difficulties in pulverization. Consequently, the particle size of the powders from the pulverization process becomes non-uniform to adversely affect hydrogen occlusive characteristics, thus rendering it impossible to obtain unobjectionable hydrogen occlusive characteristics of the ultimate hydrogen occlusive alloy powders. SUMMARY OF THE INVENTION It is an object of the present invention to provide a hydrogen occlusive alloy ingot having a crystalline structure favorably influencing the characteristics of hydrogen occlusive alloy powders prepared therefrom and which is particularly useful as a material for an electrode of a nickel hydrogen secondary cell, and a method for producing such alloy ingot. According to the present invention, there is provided a rare earth metal-nickel hydrogen occlusive alloy ingot comprising 90 vol% or more of crystals having a crystal grain size of 1 to 50 µm as measured along a short axis of the crystal and 1 to 100 µm as measured along a long axis of the crystal. According to the present invention, there is also provided a method for producing the aforementioned rare earth metal-nickel hydrogen occlusive alloy ingot comprising melting a rare earth metal-nickel alloy and uniformly solidifying the alloy melt to have a thickness of 0.1 to 0.5 mm under cooling conditions of a cooling rate of 500 to 1000°C/sec and a sub-cooling degree of 100 to 500°C. BRIEF DESCRIPTION OF THE DRAWINGS Fig.1 is a schematic view illustrating the manufacture of a hydrogen occlusive alloy ingot by a strip casting method employed in Example 1. Fig.2 is a graph showing the results of measurement of the hydrogen occlusive characteristics of the hydrogen occlusive alloys prepared in Example 1 and Comparative Example 1. Fig.3 is a graph showing the results of measurement of electrode characteristics of the hydrogen occlusive alloys prepared in Example 1 and Comparative Example 1. Fig.4 is a graph showing the results of measurement of cell characteristics of the hydrogen occlusive alloys prepared in Example 1 and Comparative Example 1. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be explained further in detail hereinbelow. The hydrogen occlusive alloy ingot according to the present invention is a rare earth metal-nickel alloy ingot containing 90 vol.% or more and preferably 95 vol% or more of crystals having a crystal grain size as measured along the short axis of 1 to 50 µm and a crystal grain size as measured along the long axis of 1 to 100 µm. It is particularly required that segregation of constituent elements in main phase crystal grains be less than 5 wt% and the distance between regions of cellular segregation based on dendritic crystal growth be 1 to 40 µm. If the content of the crystals having the above-specified crystal grain size is less than 90 vol%, it is not possible to give superior hydrogen occlusive characteristics to the produced alloy ingot. On the other hand, if the crystal grain size is outside the above-specified range, the grain size distribution becomes non-uniform. If the amount of the segregation of constituent elements exceeds 5 wt% or if the distance between the regions of cellular segregation based on dendritic crystal growth exceeds 40 µm, the particle size distribution may become undesirably non-uniform at the time of pulverization during the process of preparation of the hydrogen occlusive alloy powders. The thickness of the hydrogen occlusive alloy ingot is 0.1 to 0.5 mm. A thickness in excess of 20 mm is not desirable in that difficulties are incurred in the method of preparation of the alloy ingot, as later described, for producing the desired crystal structure. There is no particular limitation to the components of a starting material for preparation of the hydrogen occlusive alloy ingot of the present invention, provided that the starting material is a rare earth metal-nickel based material. Examples of the rare earth metals include scandium, yttrium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, ytterbium, or mixtures thereof. The starting material may also contain other components such as Mn, Co, Al, etc. The proportion of the rare earth metals to nickel is preferably 35 : 65 to 30 : 70 by weight. The aforementioned other components may be contained in an amount of 1 to 45 parts by weight to 100 parts by weight of the rare earth metal and nickel added together. The method for preparing the alloy ingot according to the present invention is produced by homogeneously solidifying the rare earth-nickel based alloy melt under cooling conditions of a cooling rate of 500 to 1000°C/sec and a sub-cooling degree of 100 to 500°C. The sub-cooling degree herein means a value of (melting point of the alloy) - (actual temperature of the alloy melt) which is correlated with the cooling rate. If the cooling rate and the sub-cooling degree are outside the above-mentioned ranges, the alloy ingot having the desired structure cannot be produced. Specifically, according to the present invention, the hydrogen occlusive alloy ingot having the desired crystalline structure is produced by a strip casting method consisting in melting a rare earth metal-nickel based alloy in an inert gas atmosphere, preferably using a crucible, by e.g. a vacuum melting method or a high frequency melting method, and solidifying the resulting molten alloy on e.g. a single roll, a twin roll or a disc, preferably continuously under the aforementioned conditions. The casting temperature and the rate of alloy melt injection are suitably selected within the above-specified ranges so that the ultimate thickness of the alloy ingot is in a range of 0.1 to 0.5 mm. The hydrogen occlusive alloy ingot of the present invention may be processed into hydrogen occlusive alloy powders by the steps of ordinary crushing, heat treatment and pulverization. The hydrogen occlusive alloy ingot of the rare earth metal-nickel of the present invention, containing the specified amounts of crystals having a crystal size as measured along the short crystal axis of 1 to 50 µm and a crystal size as measure along the long crystal axis of 1 to 100 µm, in a uniformly and finely dispersed state, is superior in heat treatment characteristics and pulverizability, and may be advantageously employed as a starting material for a hydrogen occlusive alloy powder having excellent hydrogen occlusive characteristics, above all, as a material for an electrode of a nickel-hydrogen secondary cell. Besides, the cell produced from the material for a cell electrode has superior characteristics as a cell such as high initial charging rate, a longer cell life or a larger electrical capacity. In addition, it is possible with the method of the present invention to produce a hydrogen occlusive alloy ingot having highly uniform composition and structure using the specified cooling rate and the specified sub-cooling degree. EXAMPLES OF THE INVENTION The present invention will be explained in detail with reference to an Example and a Comparative Example. It is noted that these Examples are given for the sake of illustration only and are not intended for limiting the invention. Example 1 1 kg of an alloy represented by the following formula I Mm 1 (Ni 0.7 - Mn 0.06 - Co 0.14 - Al 0.1 ) 5 was melted by the high frequency melting method in an argon atmosphere, using an alumina crucible to produce a molten alloy. After the produced molten alloy was maintained at a temperature of 1400°C, it was processed by a device shown in Fig.1 in accordance with the following method to produce a hydrogen occlusive alloy ingot. The results of analysis of the structure of the produced alloy ingot are shown in Table 1. Fig.1 schematically shows a device for preparing a hydrogen occlusive alloy ingot by the strip casting method using a single roll. An alloy melt 2 obtained by the high frequency melting method was contained in a crucible 1. The alloy melt 2 maintained at 1400°C was continuously injected onto a tundish 3 and allowed to be quenched and solidified on a roll 4 rotated at a rate of approximately 1 m/sec under the cooing conditions of the cooling rate of 500°C/sec and the sub-cooling degree of 200°C. The melted mass was caused to descend continuously in the rotating direction of the roll 4, as it was being solidified, to produce an alloy ingot 5 having a thickness of 0.5 mm. The produced hydrogen occlusive alloy ingot was pulverized to have a particle size of not more than 500 µm, using a planetary ball mill to produce hydrogen occlusive alloy powders. The hydrogen occlusive characteristics of the produced powders at 40°C were measured using a PCT measuring device based on Sievelt's method. The results are shown in Table 2 and Fig.2. The above powders were further pulverized to have a particle size of 80 µm, using a planetary ball mill. 10 g of the resulting powders, 1 g of an electrically conductive agent (copper powders) and 0.3 g of powders of an ethylene tetrafluoride-propylene hexafluoride copolymer (FEP powders) were mixed together to produce a pellet electrode having a diameter of 20 mm. A cell was produced by the above electrode dipped in a 6N KOH solution and a reference electrode of mercury oxide, and electrode characteristics were measured using a potentio-galvanostat. The results are shown in Table 3 and Fig.3. On the other hand, a negative electrode of a hydrogen occlusive alloy was prepared using 10 g of the above powders pulverized to have a particle size of 80 µm and 0.3 g of a polytetrafluoroethylene as a binder. The negative electrode thus prepared was dipped in a 6N KOH solution in combination with a positive nickel hydroxide electrode for constituting a cell in conjunction with a mercury oxide reference electrode. Cell characteristics were measured using a potentio-galvanostat. The results are shown in Table 4 and Fig.4. Comparative Example 1 The alloy melt prepared in Example 1 was pulverized in the same way as in Example 1 except using a hydrogen occlusive alloy ingot, 30 mm in thickness, produced by the metal mold casting method at a cooling rate of 5°C/sec and a sub-cooling degree of 20°C. The various characteristics as measured of the produced powders are shown in Tables 1 to 4 and in Figs.2 to 4. It is seen from Fig.2 that, with the hydrogen occlusive alloy ingot of the present invention, the amount of hydrogen absorped is increased, while a plateau area is broader and an equilibrium pressure is lowered as compared to that of the conventional product. It is also seen from Figs.3 and 4 that the discharge capacity and deterioration are lowered and hence the electrode has superior electrode characteristics and cell characteristics.

Claims: A rare earth metal-nickel hydrogen occlusive alloy ingot prepared by strip casting comprising one or more rare earth metal including scandium and yttrium, nickel, and one or more member selected from manganese, cobalt, or aluminium, characterized in that said ingot including 90 vol. % or more of crystals having a crystal grain size of 1 to 50 µm as measured along a short axis of said crystal and 1 to 100 µm as measured along a long axis of said crystal, wherein degree of segregation of a member selected from said rare earth metal including scandium and yttrium, nickel, manganese, cobalt, or aluminium in main phase crystal grains of said alloy ingot is less than 5 wt% of total weight of the main phase crystal grains, and a distance between regions of cellular segregation based on dendritic crystal growth is 1 to 40 µm. A method for producing the rare earth metal-nickel hydrogen occlusive alloy ingot as claimed in claim 1 comprising melting a rare earth metal-nickel alloy and uniformly solidifying the alloy melt to have a thickness of 0.1 to 0.5 mm under cooling conditions of a cooling rate of 500 to 1000 °C/sec and a sub-cooling degree of 100 to 500 °C.

Inventors: KITAZUME NOBUYUKI, MIYAKE YUICHI, OKADA CHIKARA, YAMAMOTO KAZUHIKO, KITAZUME, NOBUYUKI, MIYAKE, YUICHI, OKADA, CHIKARA, YAMAMOTO, KAZUHIKO
Applicants: SANTOKU METAL IND, SANTOKU METAL INDUSTRY CO., LTD.
Application year: 1993
Main classification: C01B3
IPC codes: C22C1, C01B3, H01M4, C22C19, B22D11