Antiviral composition

Abstract: An antiviral composition comprising: a thiosulfate salt and at least one of thiosulfate complex salt of a metal and a porous particulate carrier; said metal being at least one selected from the group consisting of silver, copper and zinc; said salts being carried on said porous particulate carrier. It is applicable to a wide range of living environment such as medical instruments and appliances, hygienic implements as well as kitchen utensils, and also demonstrates an antibacterial activity in addition to the antiviral activity. The composition releases its salts slowly to the environment and the antiviral and antibacterial activities of said composition lasts for a long period of time. A method for preparing said composition as well as an antiviral disinfection method and a virucidal disinfection fluid using said composition are also disclosed.

Description: FIELD OF THE INVENTION AND RELATED ART STATEMENT 1. FIELD OF THE INVENTION The present invention relates to the use of a composition for the preparation of an antiviral composition, which latter is applicable to a wide range of environments in life such as medical instruments and appliances, hygienic implements as well as kitchen utensils. Said antiviral composition also demonstrates an antibacterial activity in addition to the antiviral activity. 2. DESCRIPTION OF THE RELATED ART Heretofore, there have been disclosed various chemotherapeutic agents such as 1-adamantanamine hydrochloride salts, thiosemicarbazide, arabinocyl nucleotide, 2', 3'-dideoxynucleotides, and derivatives of pyrophosphates, as an antiviral agent. In addition, there have been disclosed hygienic products such as condoms into which have been incorporated a metal or a metal salt of silver or copper as its antibacterial and antiviral agents. Each of the above-mentioned antiviral agents is however effective only to a specified species of viruses and does not have any antibacterial property. Thus, such antiviral agents cannot be utilized for a use different from pharmaceutical products. Further, there has never been described any antiviral agent that can withstand the molding temperature of a resin and could therefore be employed as an antiviral component to be incorporated into molded resin products. In the above-mentioned hygienic products into which have been incorporated antibacterial and antiviral agents, the antibacterial and antiviral agents are directly mixed with the material used in order to form the products. Since these agents are directly incorporated into the products, it is inevitable for these antibacterial and antiviral agents to expose themselves from the surface of the products. And, the thus exposed agents are caused to directly contact a human body and to adversely stimulate his skin. In addition, the antibacterial and antiviral activities of these agents cannot be controlled in a manner that the amount of these agents actually participating in the antibacterial and antiviral action on the surface of these products is properly adjusted by any means. The EP-A 0 488 269 discloses an antibacterial and antifungicidal composition and a method for producing the same, which composition is carried on a porous particle carrier. The composition may be used by being contained in a resin or a similar material. According to preferred embodiments, said antifungicidal composition may comprise a metal complex salt. No antiviral activity is disclosed or contemplated. The reference "Chemical Abstracts 97(21): 174528w, Yu.F. Borisovich et al: "Antiviral and toxic properties of silver thiosulfate complexes" & TR.-VSES. GOS. NAUCHNO-KONTROL'N. INST. VET. PREP. Vol. 29-30, 1980, pp. 127 - 132 discloses the suppression of fowlpox viruses by means of silver thiosulfate solutions, this virus having a structure thus that it can be easily inactivated. OBJECT AND SUMMARY OF THE INVENTION It is therefore a primary object of the present invention to provide the use of a composition for the preparation of an antibacterial and antiviral composition, which latter can be applied to a resin molded product, a rubber molded product, a resinous textile and the like products as well as a pharmaceutical product. It is another object of the present invention to provide the use of a composition for the preparation of an antibacterial and antiviral composition, which latter comprises components having antibacterial and antiviral activities and which does not directly expose itself from the surface of the carrier thereof, and which latter composition furthermore has a small skin stimulation even if the resin molded product incorporating the latter composition is made to be in contact with the human body. It is a further object of the present invention to provide the use of a composition for the preparation of an antibacterial and antiviral composition having a slow releasing property, and thus maintaining its antibacterial and antiviral activities to be effective for a long period of time. According to the present invention, there is provided the use of a composition comprising: a thiosulfate salt and at least one thiosulfate complex salt of a metal, and a porous particulate carrier; said metal being at least one selected from the group consisting of silver, copper and zinc; said salts being carried on said porous particulate carrier; and at least a part of said porous particulate carrier which carries said thiosulfate salt and said thiosulfate complex salt being optionally coated with a layer of a coating material; for the preparation of a composition exhibiting both antiviral and antibacterial effects being maintained for a long period of time. A preferred antibacterial and antiviral composition according to the use of the present invention comprises: silver thiosulfate salt and silver thiosulfate complex salt which are carried on a porous particulate carrier. In the above-mentioned antibacterial and antiviral composition according to the use of the present invention, said porous particulate carrier includes particles of an inorganic oxide such as silica gel, alumina, zeolite, zirconia, montmorillonite, and the like, but the most preferred of these oxides is silica gel. In compliance with the covering area, thickness, porosity and the like of said layer of the above-mentioned coating material, the degree and rate of releasing of the salt carried on said carrier are properly controlled. A preferred material for said coating material layer is silicon dioxide, and as a method in order to form said silicon dioxide layer, there is exemplified a sol-gel method of hydrolyzing an alcoholic solution of an alkoxysilane by adding water to the solution. A preferred alkoxysilane and alcohol each has an alkyl group having 1 - 4 carbon atoms in their molecules. By forming said coating material layer, the above-mentioned antibacterial and antiviral composition according to the use of the present invention becomes to have a preferred slow releasing property. Therefore, it has a scarce detrimental effect for contaminating the environment. In addition, by the provision of the coating material layer, the heat stability of the metal salt, particularly of the silver salt which has been carried on the carrier is improved. Although the above-mentioned thiosulfate metal salt and thiosulfate complex salt can hardly be obtained as a simple substance in a solid state, it is possible to prepare them as water-soluble compounds, in order to carry said compounds on a porous particulate carrier such as silica gel by impregnating the carrier with an aqueous solution of said compounds and to immobilize them subsequently by drying to the state of being carried on the carrier. The above-mentioned thiosulfate metal salt and thiosulfate complex salt can be obtained first by adding a salt selected from the group consisting of sulfite salt and hydrogen sulfate salt to an aqueous solution of a salt of said metals, and then by adding a thiosulfate salt to said aqueous solution. The proportions of said salts, to be added to said aqueous solution of the metal salt suitable for preparing said thiosulfate metal salt and thiosulfate metal complex salt, are approximately 2 - 4 moles of said sulfite salt and/or hydrogen sulfate salt and 2 - 6 moles of said thiosulfate salt for one mole of the metal salt. If the amounts of the sulfite salt and/or hydrogen sulfate salt and the thiosulfate salt are too small, the formation of the complex salt is not sufficient, but too large amounts cause a discoloration of the obtained salt and complex salt. Furthermore, it is preferable to use approximately 1 - 10, and more preferably 3 -5 parts by weight of the total amount of the thiosulfate metal salt and the thiosulfate metal complex salt to be carried on the porous particulate carrier, for 100 parts by weight of the carrier. If the total amount is too large, the carried carrier becomes to be liable to discoloration. Each of said sulfite salt, hydrogen sulfate salt and thiosulfate salt is preferably a sodium salt, and more preferably a potassium salt. The thiosulfate complex metal salt and the thiosulfate metal salt according to the composition for the use of the present invention can be modified in respect of their antibacterial and antiviral activity providing a wider spectrum by employing them together with various chemotherapeutic agents. Such chemotherapeutic agents can be exemplified as, for instance, 1-adamantamine hydrochloride, thiosemicarbazide, arabinocyl nucleotide and 2', 3'- deoxynucleotide. As a method for employing the salts for the composition according to the use of the present invention with these chemotherapeutic agents, there is a method of causing an aqueous solution of these agents to be carried on the porous particulate carrier together with the thiosulfate metal salt and the thiosulfate metal complex salt, or a method of mixing these agents with the porous particulate carrier which has already carried the thiosulfate metal salt and the thiosulfate metal complex salt thereon. The antibacterial and antiviral composition according to the use of the present invention can provide the antibacterial and antiviral activities for various resin products, rubber products, resinous textile products and the like by mixing the composition with the material for forming the products. For instance, the silicone rubber which will be described later in Example 5 may be employed as a material for a contraceptive condom, and the water-absorbing powder which will be described later in Example 6 may be employed as a material for a menstrual blood absorber. In addition, by mixing the composition in an ointment base such as vaseline, an antiviral ointment may be obtained. While the novel features of the present invention are set fourth particularly in the appended claims, the invention, both as to organization and content, will be better understood and appreciated, along with other objects and features thereof, from the following detailed description taken in conjunction with the attached drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIG.1 is an X-ray diffraction pattern of the antiviral composition according to the use of the present invention prepared in accordance with one embodiment of the present invention. FIG.2 is an X-ray diffraction pattern of the antiviral composition shown in FIG.1 which has been heated at 240°C for 10 minutes. FIG.3 is an X-ray diffraction pattern of the antiviral composition shown in FIG.1 which has been heated at 240°C for 30 minutes. FIG.4 is an X-ray diffraction pattern of the antiviral composition shown in FIG.1 which has been heated at 500°C for 5 minutes. FIG.5 is an X-ray diffraction pattern of the antiviral composition according to the use of the present invention prepared in accordance with another embodiment of the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENT In the following paragraphs, preferred embodiments according to the use of the present invention will be described with reference to the attached drawings. Property The antibacterial and antiviral composition according to the use of the present invention comprises: a porous particulate carrier and a thiosulfate salt and a thiosulfate complex salt of silver, copper or zinc, carried on said carrier. The most preferred thiosulfate complex salt and thiosulfate salt are those of silver. A preferred carrier is silica gel having a mean particle diameter of 1 - 10 µm, and particularly is Type B silica gel particle defined in Japanese Industrial Standard JIS Z 0701. Particularly preferred silica gel is one that has a moisture absorption rate of 20% or below under a low humidity environment (relative humidity: 50% or below, 25°C) and a moisture absorption rate of 50% under a high humidity environment (relative humidity: 90% or above, 25°C). The silica gel does thus scarcely release moisture under the low humidity environment, but releases moisture in a large quantity under the high humidity environment. The antibacterial and antiviral agents carried on such silica gel are hardly volatile and are stable to heat and therefore they exhibit their antibacterial and antiviral activities for a long period of time. Further, silica gel is generally transparent and its refractive index is similar to that of any synthetic resin. Therefore, when the silica gel carrying the antibacterial and antiviral agents is incorporated into the synthetic resin and the like, it does not change the color of the resin. Preparation A preferred antiviral composition according to the use of the present invention is prepared, for instance, in the following procedure. First, an aqueous solution of the silver thiosulfate and the silver thiosulfate complex salt is prepared by adding sodium sulfite and sodium thiosulfate to an aqueous solution of silver acetate. Then, a porous particulate carrier such as silica gel is impregnated with the thus obtained aqueous solution and is then dried, in order to immobilize the contained agents in the carried state. Although it is not apparent in which state the above-mentioned silver salts are actually being carried on the carrier, it is possible to identify the silver salts on the carrier by means of X-ray diffraction using the Kα-line of Cu. FIG.1 shows the X-ray diffraction pattern, and there are recognized the diffraction lines of Ag 2 O (marked by ), as well as power diffractions at 10.3°, 11.2°, 11.9° and 12.3° having the diffraction angle 2 (hereinafter, these value of 2 are referred to as P 1 , P 2 , P 3 and P 4 , respectively) which are not recognized in the JCPDS (Joint Committee on Power Diffraction Standards) card. In this pattern, the marks o show the diffraction lines of sodium sulfate (Na 2 SO 4 ). In the above-mentioned step of causing the silver salts to be carried on the carrier, if the drying temperature is raised, the X-ray power diffractions peculiar to the silver salts are made to disappear. FIG.1 shows the X-ray diffraction pattern of the antiviral composition obtained by a drying temperature at 100°C or below. FIG.2, FIG.3 and FIG.4 show the X-ray diffraction patterns of the antiviral composition obtained under the drying conditions at 240°C for 10 min., at 240°C for 30 min. and at 500°C for 5 min., respectively. When the drying temperature exceeds 200°C, the peaks of the diffraction lines of Ag 2 O and the power diffractions at P 1 - P 4 gradually become smaller. The antiviral composition which has been subjected to a heat treatment at a temperature of 500°C demonstrates no power diffraction signals with the exception of those of Na 2 SO 4 , because the silver compounds have presumably been sublimated out of the composition. The composition that has an antibacterial and an antiviral activity as will be described later is, characterized in having small, but distinct power diffractions at P 1 - P 4 in the X-ray diffraction pattern as shown in FIG.2, wherein all of the peaks of the power diffractions are approximately equal with one another, in addition to those having the X-ray diffraction pattern as shown in FIG.1. The compositions having the X-ray diffractions patterns as shown in FIG.3 and FIG.4 have no antibacterial and antiviral activity. Although sodium salts such as sodium sulfite, hydrogen sulfate and thiosulfate are used in the above-mentioned preparation of silver thiosulfate complex salt and silver thiosulfate salt, a potassium salt may also be used in the preparation and the X-ray diffraction pattern of the composition obtained with the potassium salt is shown in FIG.5. In this diffraction pattern, there are recognized peculiar power diffractions at 8.7°, 9.4°, 9.8° and 11.2° having the diffraction angle 2, which are not recognized in the JCPDS card. As compared with that of FIG.1, the diffraction pattern of FIG.5 demonstrates that the diffraction angles representing the characteristic power diffractions are shifted to smaller angles. In this pattern, although diffraction lines of silver oxide (Ag 2 0) are not clearly recognized, however the diffraction lines representing potassium sulfate (K 2 SO 4 ) and another potassium compound (K 2 S 4 O 6 ) are recognized. As previously described, the silver thiosulfate complex salt and silver thiosulfate salt for being carried on the porous particulate carrier can be obtained by adding at least one salt selected from the group consisting of a sulfite salt and a hydrogen sulfate salt as well as a thiosulfate salt to an aqueous solution of a water-soluble silver salt such as silver acetate and silver nitrate. It is preferable to use from 2 moles to 4 moles of the sulfite salt and/or hydrogen sulfate salt and from 2 moles to 6 moles of thiosulfate salt, for one mole of the silver salt. In the thus obtained aqueous solution silver thiosulfate complex ions represented by [Ag (S 2 O 3 )] 3- , [Ag 2 (S 2 O 3 )] 2- , and the like, are existing together, in addition to thiosulfate ions and silver ions. In view of the fact that the aqueous solution does not produce any remarkable white turbidity even when it is brought into contact with tap water containing chlorine, it is presumed that most of the silver ions are in the form of the respective complex ions. Anyway, in the above-mentioned coexisting state of the ions, the composition according to the use of the present invention demonstrates both an antibacterial and an antiviral activity. In view of the "slow releasing and long acting"-property of the composition, it is preferable to select the amount of these silver thiosulfate salts and silver thiosulfate complex salts to be carried on the porous particulate carrier as 1 -- 10 parts by weight, and more preferably as 2 -- 5 parts by weight for 100 parts of the carrier. Example 1 Silver acetate (0.232 g) is dissolved in 30 ml of deionized water, and 0.627 g of potassium sulfite is added thereto and then stirred to dissolve therein. Thereafter, 1.54 g of potassium thiosulfate (K 2 S 2 O 3 ) is added to the mixture and stirred to dissolve. In this manner, an aqueous solution of silver thiosulfate salt and silver thiosulfate complex salt is prepared. As a carrier for carrying the thus obtained aqueous solution, this Example employs a type B silica gel powder described in "JIS Z 0701: Silica Gel for packaging". This type B silica gel has a low moisture absorption rate under a low humidity environment, but it has a high moisture absorption rate under a high humidity environment, and therefore has a high total moisture absorption amount under the high humidity environment. In this Example, one that has a particle diameter of from 2 to 30 µm (average: 8 µm) is employed. This type B silica gel powder is dried at 180°C for 2 hours or longer, and further is dried at 60°C for 24 hours. Then, 100 parts by weight of the above-mentioned silica gel is mixed with the previously described aqueous solution containing its silver components in 2 parts by weight, and the mixture is heated at 60°C under a reduced pressure to remove its water component. Thereafter, the dried particles are pulverized to have a given particle diameter. In this way, the silica gel which carries the silver thiosulfate salt and the silver thiosulfate complex salt is obtained. Next, 100 parts by weight of the above-mentioned silica gel is dispersed in a solution prepared by dissolving 100 parts by weight of tetraethoxysilane in 100 parts by weight of ethanol, and then the tetraethoxysilane in the obtained dispersion is hydrolyzed by adding pure water to cause silicon dioxide film as the hydrolyzed product of the tetraethoxysilane to coat at least a part of the surface of the above-mentioned silica gel. Then, the coated silica gel is dried. Example 2 After dissolving 200 mg of silver acetate in 30 ml of pure water kept at 50 - 60°C, the obtained solution is filtered to remove unsolved residues. To the filtrate, 1 g of potassium sulfite and 1.8 g of potassium thiosulfate are added in this order to be dissolved. To the obtained solution, a type B silica gel powder having a mean particle diameter of about 2.6 µm described in "JIS Z 0701: Silica Gel for packaging" is added to be mixed. Drying of this mixture under a reduced atmosphere gives a silica gel carrying the silver thiosulfate salt and the silver thiosulfate complex salt. Example 3 Cupric acetate (0.272 g) is dissolved in 30 ml of deionized water, and 1.0 g of potassium sulfite is added thereto to be dissolved. Next, 0.66 g of potassium thiosulfate (K 2 S 2 O 3 ·5H 2 O) is added to the obtained mixture to be dissolved and stirred. In this manner, an aqueous solution containing the cupric thiosulfate salt and the cupric thiosulfate complex salt is prepared. Next, in a similar manner to that of Example 1, the cupric thiosulfate salt and the cupric thiosulfate complex salt are caused to be carried on silica gel and a part of the surface of the silica gel is coated with the silicon dioxide film. Example 4 Zinc acetate (0.286 g) is dissolved in 30 ml of deionized water, and 1.0 g of potassium sulfite is added thereto to dissolve. Next, 0.66 g of potassium thiosulfate (K 2 S 2 O 3 ·5H 2 O) is added to the obtained mixture to be dissolved and stirred. In this manner, an aqueous solution of the zinc thiosulfate salt and the zinc thiosulfate complex salt is prepared. Next, in a similar manner to that of Example 1, the zinc thiosulfate salt and the zinc thiosulfate complex salt are caused to be carried on silica gel and a part of the surface of the silica gel is coated with the silicon dioxide film. Example 5 The composition obtained by the procedure of Example 1, namely, the silica gel particles which carry the silver thiosulfate salt and the silver thiosulfate complex salt and whose surfaces are coated with the silicon dioxide film, is classified to have a particle diameter of 2 µm or smaller. The classified particles are then mixed with a material for silicone rubber in an amount of 3% by weight, and the obtained mixture is kneaded. The kneaded mixture is then molded into a given shape and thus caused to be crosslinked to obtain a thin film of silicone rubber. Example 6 Each 5 g of methyl acrylate and of vinyl acetate are subjected to a process of suspension polymerization in 10 ml of benzene, and the polymerized product is dispersed in 10 ml of methanol. To this dispersion, 1 g of the silica gel carrying the silver thiosulfate salt and the silver thiosulfate complex salt which has been prepared in Example 2 is added. The thus converted suspension is then saponified with an aqueous solution containing NaOH in an amount of 40% by weight and washed with acetone. The washed suspension is dried to remove its water component, in order to obtain powder of water absorbing property. Example 7 An ointment is prepared by mixing the silica gel carrying the silver thiosulfate salt and the silver thiosulfate complex salt obtained in Example 2 in an amount of 3% by weight with an ointment base of vaseline. Example 8 L-adamantamine hydrochloride (10 mmol) is dissolved in the aqueous solution containing the silver thiosulfate salt and the silver thiosulfate complex salt which has been prepared by the process described in Example 1. The thus obtained aqueous solution is adsorbed on the silica gel particles employed in Example 2, and dried under reduced pressure. Example 9 Ten (10) grams of silica gel carrying the silver thiosulfate salt and the silver thiosulfate complex salt prepared in Example 2 are dispersed in 100 ml of an aqueous ethanol solution containing ethanol in an amount of 50% by weight to obtain a bactericidal disinfection solution. Example 10 Ten (10) grams of silica gel carrying the silver thiosulfate complex salt and the silver thiosulfate salt prepared in Example 4 are dispersed in 100 ml of an aqueous ethanol solution containing ethanol in an amount of 50% by weight to obtain a bactericidal disinfecting solution. Example 11 Another bactericidal disinfecting solution is prepared by storing the solution obtained in Example 9 at room temperature for a week. Comparative example 1 Another coating film of silicone rubber is prepared in a similar manner to that described in Example 5, but with the exception of excluding the incorporation of the silica gel. Comparative example 2 Another bactericidal disinfecting solution is prepared by simply mixing water and ethanol in an amount of 50% by weight. Comparative example 3 Another bactericidal disinfecting solution is prepared by storing the solution obtained in Comparative example 2 at room temperature for a week. Evaluation In the following paragraph, the evaluation process performed on the antibacterial and antiviral activities of the samples prepared in accordance with the above-mentioned Examples and Comparative examples will be described. Samples subjected to the evaluation Each one gram of the products obtained by Examples 1 - 8 and Comparative examples 1 and 3 ml of phosphate buffer solution are combined and stirred for 30 minutes, and salts contained in the product are extracted to give the samples for the evaluation. The disinfecting solutions obtained by Examples 9 - 11 and Comparative example 2 - 3 are used as the samples as they are. Virus used in this evaluation Measles (Nagahata strain), Human immunodeficiency (AIDS) (JMH-1 strain), Helpes simplex (G strain), and Influenza A virus (Okuda strain). Bacteria used in this evaluation Escherichia coli, Staphylococcus aureus, and Methicilline-resistant staphylocuccus aureus. Procedure 1. Antiviral activity: Each one ml of the virus-containing solutions of TCID (Tissue Culture Infective Dose) 50 (/ml): 6.5 - 8.5 is mixed with each one ml of the above-mentioned samples and kept stationary for 30 minutes. Then, the Vero cells derived from Kidney of the African green monkey (guenon), the MT - 4 cells derived from the adult thymocyte leukemia patient and the MDCK cells derived from Kidney of Canien (each: 10 6 cells/ml) are infected with each of the mixtures kept stationary, and the infection activities are evaluated by means of determining the state of the survival of the infected cells after a week, respectively. The results of this evaluation are summarized in Table 1. (antiviral activity) Samples derived from TCID 50 (/ml)[-log] virus B C D E Example 1 2.0 2.5 1.5 2.5 Example 2 2.0 2.5 2.5 2.5 Example 3 3.5 4.0 3.0 3.5 Example 4 3.5 4.0 3.0 3.5 Example 5 2.5 3.0 3.0 3.5 Example 6 2.5 3.0 3.0 3.5 Example 7 2.5 3.0 3.0 3.5 Example 8 1.0 1.0 1.0 1.0 Example 9 0 0 0 0 Example 10 0 0 0 0 Example 11 2.0 2.5 2.5 2.5 Comparative E.1 7.0 6.5 8.5 6.5 Comparative E.2 4.0 3.5 4.0 3.5 Comparative E.3 7.0 6.5 6.5 6.5 B: Measles (Nagahata strain), C: Human immunodeficiency (JMH-1), D: Herpes simplex (G strain), E: Influenza A virus (Okuda strain). 2. Antibacterial Activity: Each one ml of solutions containing the above-mentioned bacteria (10 4 - 10 6 CFU (colony forming units)/ml) is mixed with each one ml of the samples and is stored still for 30 minutes. These thereby prepared mixtures are spread over normal agar media (available from Nissui Pharmaceutical K.K., Japan) with a dilution, respectively. The agar media are incubated for 18 hours, and the numbers of the cells grown on the agar media after the incubation are counted for the evaluation. The results of this evaluation are summarized in Table 2. (antibacterial activity) Samples derived from CFU/ml E.coli S.aureus MRSA Example 1 0 0 0 Example 2 0 0 0 Example 3 0 0 0 Example 4 0 0 0 Example 5 0 0 0 Example 6 0 0 0 Example 7 0 0 0 Example 8 0 0 0 Example 9 0 0 0 Example 10 0 0 0 Example 11 0 0 0 Comparative E.1 1.5×10 5 1.0×10 4 1.0×10 4 Comparative E.2 10 10 10 Comparative E.3 1.0×10 4 1.0×10 4 1.2×10 3 Although the present invention has been described in terms of the presently preferred embodiments, it is to be understood that these disclosures are not to be interpreted as limiting. Various alterations and modifications will undoubtless become apparent to persons skilled in the art to which the present invention pertains, after having read the above disclosure. Accordingly, it is intended that the appended claims are to be interpreted as covering all alterations and modifications as fall within the true spirit and scope of the invention.

Claims: Use of a composition comprising: a thiosulfate salt and at least one thiosulfate complex salt of a metal, and a porous particulate carrier; said metal being at least one selected from the group consisting of silver, copper and zinc; said salts being carried on said porous particulate carrier; and at least a part of said porous particulate carrier which carries said thiosulfate salt and said thiosulfate complex salt being optionally coated with a layer of a coating material; for the preparation of a composition exhibiting both antibacterial effects and antiviral effects being maintained for a long period of time; the latter-mentioned antiviral effects being directed against the following viruses: Measles (Nagahata strain), Human immunodeficiency (AIDS) (JMH-1 strain), Herpes simplex (G strain), Influenza A virus (Okuda strain). Use in accordance with claim 1, wherein said porous particulate carrier is a silica gel. Use in accordance with claim 1 and/or 2, wherein said carrier is an inorganic oxide. Use in accordance with claim 3, wherein said carrier carries said thiosulfate salt and thiosulfate complex salt in 1 - 10 parts by weight for 100 parts by weight of the carrier. Use in accordance with any of the claims 1 to 4, wherein said coating material is silicon dioxide formed by means of hydrolysis of an alkoxysilane. Use in accordance with any of the claims 1 to 5, wherein said metal is silver and the silver salts carried on the carrier are characterized by a diffraction line of Ag 2 O in an X-ray diffraction pattern by means of the K α line of Cu and by power diffractions at 10.3 °, 11.2 °, 11.9 ° and 12.3 ° at the diffraction angle 2. Use in accordance with any of the claims 1 to 5, wherein said metal is silver and the silver salts carried on the carrier are characterized by power diffractions at 8.7 °, 9.4 °, 9.8 ° and 11.2 ° at the diffraction angle 2 in an X-ray diffraction pattern by means of the K α line of Cu. Use in accordance with any of the claims 1 to 7, wherein said metal is silver and the silver salts carried on the carrier have been prepared by impregnating the carrier with an aqueous solution comprising 2 to 4 moles of a sulfite salt, a water soluble silver salt and 2 to 6 moles of a thiosulfate salt for one mole of said water soluble silver salt.

Inventors: HOSHINO KENJI, NISHINO ATSUSHI, OKA HIROAKI, TOMIOKA TOSHIKAZU, TOMITA KATSUMI, UEDA SHIGEHARU, HOSHINO, KENJI, NISHINO, ATSUSHI, OKA, HIROAKI, TOMIOKA, TOSHIKAZU, TOMITA, KATSUMI, UEDA, SHIGEHARU
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1993
Main classification: A01N59
IPC codes: A01N59