Process for preparing carbon/carbon composite preform and carbon/carbon composite

Abstract: A carbon/carbon composite is prepared without using any expensive carbon fiber fabric and without performing any complicated molding step prior to a densifying step. A pitch-based infusiblized fiber alone, or optionally in the form of a mixture thereof with a pitch-based carbonized fiber, is subjected to carbonization and molding under uniaxial pressing to obtain a carbon/carbon composite preform. The preform is then densified using a carbonaceous matrix.

Description: Background of the Invention The present invention relates to a process for preparing a carbon/carbon composite preform and a carbon/carbon composite. A carbon/carbon composite is a material having unique properties, for example, maintaining high strength and high elastic modulus even at such high temperatures as higher than 1,000°C and exhibiting only a small thermal expansion coefficient. Its utilization as parts of aeronautic and space machinery and devices, brakes, furnace materials, etc. is expected. As to the shape of an aggregate of carbon fibers which is used in the preparation of such carbon/carbon composite, two-dimensional fabrics are mainly used, and three-dimensional fabrics are also used as the case may be. Although the use of these fabrics affords carbon/carbon composites of high strength, the structure of the fabrics and the method for preparing them are complicated and the production thereof is therefore expensive. On the other hand, if carbon fibers in the form of short fibers, such as chopped strands are used, a satisfactory reinforcing effect is not usually obtained. Further, in the case of performing a densifying process for preparing a carbon/carbon composite using any of such fabrics or short fiber-like fibers, it is necessary to provide a separate process for fixing carbon fibers to each other using pitch or a thermosetting resin (binder). This process is one cause of reductions in the productivity of carbon/carbon composite preparing processes. EP-A-0297695 describes a process for fabricating a carbon/carbon fiber composite in which one or more kinds of fibers are woven, laminated or mix-pulverized together with a pitch-based carbon fiber and carbonized under the application of pressure or under pressing. It is the object of the present invention to provide a process for preparing a carbon/carbon composite without using expensive carbon fiber fabrics. Summary of the Invention The present invention resides in a process for preparing a carbon/carbon composite preform, characterized by charging a continuous pitch-based infusibilized fiber by being forced or allowed to fall freely into a vessel and subjecting it, optionally together with a pitch-based carbonized fiber, to carbonization and molding under uniaxial pressing, to obtain a carbon/carbon composite preform having a void volume of 15 - 70 vol. % and a bulk density of 0.10 - 1.70 g/cm 2 . The carbonized fiber may also be charged to the vessel and may be used in an amount of 5 to 1,000 parts per 100 parts by weight of the infusibilized fiber. The carbonization and molding are preferably preformed using a hot press at a pressure of 0.01 to 95 kg/cm 2 and at a temperature of 300°C to 2000°C. The present invention also resides in a process for preparing a carbon/carbon composite, characterized in that the preform obtained above is densified using a carbonaceous matrix. The carbonaceous matrix is preferably a carbonaceous matrix obtained by a chemical vapor deposition of a hydrocarbon gas or is a pitch-based carbonaceous matrix. The chemical vapor deposition may be carried out by heating the hydrocarbon gas, optionally together with a diluting gas, to a temperature of 700°C to 3,000°C in the presence of a primary molded product, allowing carbon formed by thermal decomposition to be deposited within the preform. The densifying using the pitch-based carbonaceous matrix is preferably carried out by heating the preform and a carbonaceous pitch to a temperature above a softening point of the pitch and below a decomposition start temperature thereof under a reduced pressure, allowing the pitch to be impregnated into the preform, and subsequently heating to a temperature of 400°C to 2,000°C under pressure or under pressing. The pitch preferably has an optically anisotropic phase content of 60% to 100%. The carbonaceous matrix may be obtained by any suitable means. In particular, it may be obtained by chemical vapor deposition or by starting from a carbonaceous pitch. In one embodiment of the present invention the preform is densified using both a carbonaceous matrix obtained by vapor deposition and a pitch-based carbonaceous matrix. The present invention, in a further embodiment thereof, resides in a process for preparing a carbon/carbon composite, characterized by subjecting a mixture containing 100 parts by weight of a pitch-based infusibilized fiber and 5-1,000 parts by weight of a pitch-based carbonized fiber to carbonization and molding under uniaxial pressing. The present invention, in a still further embodiment thereof, resides in a process for preparing a carbon/carbon composite, characterized by subjecting a mixture containing 100 parts by weight of a pitch-based, infusibilized fiber and 5-1,000 parts by weight of a carbon fiber to carbonization and molding under uniaxial pressing to obtain a primary molded product having a void volume of 15-70 vol.% and a bulk density of 0.10-1.70 g/cm 2 , and densifying the primary molded product using a carbonaceous material. Brief Description of the Drawings Fig. 1 is a schematic view of an apparatus used in the below-mentioned examples, in which the numeral 1 denotes infusibilized fiber, 2 a hot pressing die, 3 a pulley, 4 a moving direction of the infusibilized fiber and 5 a moving direction of the die. DETAILED DESCRIPTION OF THE INVENTION The following description is now provided about how to prepare a carbon/carbon composite preform and a carbon/carbon composite according to the present invention. The "pitch-based infusibilized fiber" as referred to herein indicates a fiber obtained by making a pitch fiber infusible. The "pitch fiber" indicates a fiber prepared by melt-spinning a carbonaceous pitch in a known manner and having an average diameter of usually 5 to 100 µm, preferably 7 to 30 µm. The kind of the carbonaceous pitch is not specially limited. There may be used any known carbonaceous pitch. Particularly, it is desirable to use a coal or petroleum pitch having a softening point of usually 100° to 400°C, preferably 150° to 350°C. Both optically isotropic and anisotropic carbonaceous pitches are employable, but particularly preferred is an optically anisotropic pitch having an optically anisotropic phase content of 60% to 100%. The infusibilizing treatment can be performed at a temperature of usually 50° to 400°C, preferably 100° to 350°C, in an oxidizing gas atmosphere. Suitable oxidizing gases include air, oxygen, nitrogen oxide, sulfur oxide, halogen, or a mixture thereof. The treatment time is sufficient that the fiber no longer exhibits a fusion-bonding property, and usually it is 10 minutes to 20 hours, preferably 30 minutes to 10 hours. In the present invention, the infusibilized fiber is subjected to carbonization and molding under uniaxial pressing to obtain a preform (i.e. primary molded product) having a void volume of 15-70 vol.% and a bulk density of 0.10-1.70 g/cm 2 . Preferably, the infusibilized fiber is dropped forcibly or naturally into a vessel and is deposited forcibly or naturally in the vessel. In this case, the infusibilized fiber is laminated or deposited in the form of continuous fibers. Suitable methods for charging continuous fibers into a vessel or the like, include a method in which, using a container such as a basket, infusibilized fibers are allowed to fall into a vessel for uniaxial pressing, a method in which infusibilized fibers are fed to a pulley and thereby fed uniformly into a vessel for uniaxial pressing, and a method in which infusibilized fibers are charged into a vessel forcibly through an air ejector. In all of the above filling methods, it is desirable that uniform filling be attained. To this end, it is preferable to move a filling device, a filling vessel, or a filling device and a filling vessel so as to shift a falling position or a filling position during the filing operation. As the vessel for uniaxial pressing it is desirable to use a uniaxial pressing die because the use thereof permits simplification of the process. In the present invention it is desirable that the infusibilized fiber be used alone. If desired, however, it may be used in the form of a mixture with a pitch-based carbonized fiber. The "carbonized fiber" as referred to herein indicates a fiber obtained by subjecting the infusibilized fiber to a known carbonization treatment. The carbonization treatment is performed in a non-oxidizing treatment, preferably in an inert gas, usually at a temperature of 350° to 1,000°C, preferably 350° to 850°C, more preferably 400° to 700°C, for 10 minutes to 5 hours. It is preferable that the carbonized fiber thus obtained has a hydrogen/carbon element ratio of not higher than 0.41, more preferably in the range of 0.01 to 0.35. If the hydrogen/carbon element ratio exceeds this range, fusion-bonding of fibers in the subsequent step may occur. Thus it will be difficult to attain the desired reinforcing effect. Also, a hydrogen/carbon element ratio below the above range is not desirable because the moldability may be deteriorated. The use of the carbonized fiber in combination with the infusibilized fiber exhibits a technical effect in the case where the infusibilized fiber has an adhesive property and there is a fear of adhesion of its constituent fibers to each other or in the case where the resulting molded product exhibits a brittle property. The carbonized fiber is used usually in an amount of 5 to 1,000 parts by weight, preferably 5 to 100 parts by weight, for 100 parts by weight of the infusibilized fiber. If the amount thereof is smaller than 5 parts by weight, there will be little effect of the combination, and if it is larger than 1,000 parts by weight, the moldability may deteriorate. The method of charging a mixture of both such fibers into a vessel or the like is the same as in the foregoing charging method for the infusibilized fiber. It is desirable that both fibers be mixed at the time of filling. Suitable methods for mixing both fibers in a predetermined mixing ratio at the time of charging them as continuous fibers into a vessel, include a method in which, before filling, the number of monofilaments contained in each fiber bundle is set at a predetermined ratio, and a method in which there is provided a pulley or ejection (hereinafter referred to as "filling device") for the infusibilized fiber and a filling device for the carbonized fiber and adjustment is made with respect to the filling speed of each component or the number of filling devices for each component. By using these methods it is possible to mix the components at accurate respective proportions and intimately. Suitable methods for charging both fibers as short fibers into a vessel or the like include a method in which both infusibilized fiber and carbonized fiber, which have been made into short fibers, are deposited by free falling into the vessel, and a method in which both fibers are fed as continuous fibers to above the vessel, then cut with a cutter or the like and thereby allowed to fall. In all of the above filling methods it is desired that the filing be effect uniformly. To this end, it is desirable to move the filing device, the filling vessel, or the filling device and the filling vessel so as to shift the falling position or the filling position during the filling operating. As the vessel, the use of a die or the like for uniaxial pressing is preferred because the process is simplified. After such filling operation and before or after the carbonization and molding under uniaxial pressing, a needle punch processing may be performed in a direction perpendicular to the fiber lamination plane direction. The carbonization and molding under uniaxial pressing are carried out using a hot press, usually at a pressure of 0.01 to 95 kg/cm 2 , preferably 0.05 to 50 kg/cm 2 , more preferably 1 to 20 kg/cm 2 at a temperature of usually 300° to 2,000°C, preferably 300° to 1,000°C, more preferably 400° to 750°C for usually 10 minutes to 10 hours, preferably 30 minutes to 4 hours. It is preferred that this step be conducted in a non-oxidizing atmosphere of, for example, nitrogen, helium, neon, argon, xenon or radon or in a vacuum. Even an oxidizing atmosphere may be used provided that the temperature is held at a relatively low level, for example, in the range of 300° to 600°C, and the treatment time is short. In this way, a carbon/carbon composite is obtained. In the present invention, the carbon/carbon composite is made into a preform, which then may be subjected to a densifying step to obtain a densified carbon/carbon composite ("densified composite" hereinafter). The void volume of the carbon/carbon composite preform is usually in the range of 15 to 70 vol.%, preferably 15 to 60 vol.%, more preferably 15 to 50 vol.%. If the void volume exceeds this range, the shape retaining property of the carbon/carbon composite may deteriorate and in the subsequent step there may occur chipping or deformation of the preform. And if the void volume is below the above range, the densified composite will under a brittle fracture and exhibit a behavior like a monolithic material, thus not exhibiting its inherent characteristics. The bulk density of the carbon/carbon composite preform is usually in the range of 0.10 to 1.70 g/cm 2 , preferably 0.20 to 1.60 g/cm 2 , more preferably 0.50 to 1.30 g/cm 3 . A bulk density thereof below this range is not desirable because it may result in deterioration in the shape retaining property of the carbon/carbon composite and chipping or deformation of the preform may occur in the subsequent step. A bulk density thereof exceeding the above range is not desirable either because the densified composite may undergo brittle fracture and exhibit a behavior like a monolithic material, thus making it impossible to utilize the features inherent in the composite material. Prior to the densifying treatment there may be performed carbonization or graphitization under atmospheric pressure for the preform. In this case, the carbonization or graphitization is conducted in a non-oxidizing atmosphere usually at a temperature of 400° to 3,000°C, preferably 500° to 2,500°C. How to perform the densifying treatment is not specially limited if only it produces a carbonaceous matrix. Any known method may be adopted. Particularly preferred is a method using a matrix obtained by chemical vapor deposition, a matrix starting from pitch or both a matrix obtained by chemical vapor deposition and a matrix starting from pitch. In the case where the densifying treatment is performed by chemical vapor deposition, a thermal decomposition is conducted using as a starting material a hydrocarbon gas such as, for example, methane, ethane, acetylene, propane, benzene or natural gas, or at least one of those gases diluted, for example, with an inert gas or hydrogen, thereby allowing the thermally decomposed carbon to be deposited within the primary molded product. Suitable inert gases include argon, nitrogen and helium. The thermal decomposition temperature is usually in the range of 700° to 3,000°C, preferably 800° to 2,500°C. As to the thermal decomposition pressure, a reduced pressure is preferred although this treatment may be conducted even at atmospheric pressure. Usually the pressure is in the range of 66.7 to 13332.2 Pa (0.5 to 100 Torr), preferably 66.7 to 6666.1 Pa (0.5 to 50 Torr). A diluting gas such as an inert gas or hydrogen may be used for the purpose of controlling the reaction rate. In this case, the diluting gas is used in an amount of 1 to 1,000 times, preferably 1 to 100 times, the volume of the above hydrocarbon gas used. If the proportion of the diluting gas is below the above range, there will not be obtained a satisfactory diluting effect, and if it exceeds the above range, the reaction rate will be decreased to a greater extent than required. Thus, both such proportions are not desirable. In the case where the densifying treatment is carried out by the use of a matrix starting from pitch, there usually is adopted a method in which the preform is impregnated with a carbonaceous pitch and thereafter carbonized. The carbonaceous pitch is not specially limited. There may be used any known one. Particularly preferred is a coal or petroleum pitch having a softening point of usually 100° to 400°C, preferably 150° to 350°C. Both optically isotropic and anisotropic carbonaceous pitches are employable, but an optically anisotropic pitch having an optically anisotropic phase content of 60% to 100% is especially preferred. How to effect the impregnation is not specially limited. Any known method may be adopted. For example, the impregnation may be carried out by sealing the primary molded product and the carbonnaceous pitch into a vacuum vessel and heat-melting them under a reduced pressure, e.g 1 x 10 -2 ∼ 300 Torr. The heating temperature is usually above the softening point of the carbonaceous pitch and below the decomposition start temperature thereof, preferably higher by 30°C or more than the softening point and below the decomposition start temperature, more preferably 100° to 400°C. The carbonization is preferably conducted under pressure or pressing. The carbonization under pressure is performed, for example, by evacuating a vessel containing an impregnated primary molded product, then pressurizing usually to 50-10,000 kg/cm 2 , preferably 100-2,00 kg/cm 2 , using an inert gas such as, for example, nitrogen, argon or helium, followed by heating to 400-2,000°C, preferably 500-1,500°C. The carbonization under pressing is carried out by uniaxial pressing usually to 10-500 kg/cm 2 , preferably 20-200 kg/cm 2 and heating usually to 400-2,000°C, preferably 500-1,500°C. A suitable value of a volumetric content (Vf) of fibers in the carbon/carbon composite may be selected according to purpose, but usually 5% to 70%. According to the present invention it is possible to prepare the carbon/carbon composite in a simple manner without going through any complicated step. The following examples are given to illustrate the present invention more concretely, but it is to be understood that the invention is not limited thereto. (Example 1) An optically anisotropic petroleum pitch having a softening point of 280°C was melt-spun to obtain pitch fibers having an average diameter of 13 µm. A tow of 2,000 such pitch fibers was made infusible in air at 200°C for 1 hour to obtain a tow of infusibilized fibers. This tow of infusibilized fibers was passed as continuous fibers onto a pulley and fed into a hot pressing die continuously from above the die. The die was moved to permit uniform deposition of the infusibilized fibers in the interior of the die (Fig. 1). Thereafter, the infusibilized fibers were carbonized under pressing by means of a hot press at a pressure of 5 kg/cm 2 , at 700°C, for 1 hour, to afford a preform having a void volume of 25% and a bulk density of 1.1 g/cm 3 . When the preform was taken out from the die, no change in shape was observed (Example 2) The preform of Example 1 was then subjected to a densifying treatment by chemical vapor depositing using methane as a starting gas at 1,200°C, at 1.5 Torr, for 120 hours, to obtain a carbon/carbon composite. The composite had a void volume of about 4% and was not cracked. It retained the shape of the preform. (Example 3) An optically anisotropic petroleum pitch having a softening point of 280°C was melt-spun to obtain pitch fibers having an average diameter of 13 µm. A tow of 2,000 such pitch fibers was subjected to an infusibilizing treatment in air at 300°C for 1 hour. This tow of infusibilized fibers was passed as continuous fibers onto a pulley and fed into a hot pressing die continuously from above the die. The die was moved to permit uniform deposition of the infusibilized fibers in the interior of the die. Thereafter, the infusibilized fibers were carbonized under pressing by means of a hot press at a pressure of 10 kg/cm 2 , at 600°C, for 1 hour, to obtain a preform having void volume of 30% and a bulk density of 1.1 g/cm 3 . The preform (primary molded product) was then calcined in nitrogen at 1,000°C, at atmospheric pressure, to afford a preform having a void volume of 30% and a density of 1.2 g/cm 3 . This preform retained the shape of the as -molded product. (Example 4) The preform of Example 3 was then subjected to a densifying treatment by chemical vapor deposition using methane as a starting gas at 1,100 °C, at 1 Torr, for 120 hours, to obtain a carbon/carbon composite. The composite has a void volume of about 4% and was not cracked. It retained the shape of the primary molded product. (Comparative Example 1) A tow of carbon fibers was passed as continuous fibers onto a pulley and fed into a not pressing die continuously above the die. The die was moved to permit uniform deposition of the carbon fibers in the interior of the die. Thereafter, the carbon fibers were pressed by means of a hot press at a pressure of 10 kg/cm 2 , at 600°C, for 1 hour, and then calcined in nitrogen at 1,000°C, at atmospheric pressure. The resulting calcinate had a large void volume, in which the fibers were not fixed to each other. Subsequently, there was performed a densifying treatment by chemical vapor deposition using methane as a starting gas at 1,100°C, at 1 Torr, for 120 hours. As a result, the molded product was swollen and deformed, and the dispersion of fibers was not uniform. (Example 5) An optically anisotropic petroleum pitch having a softening point of 280°C was melt-spun to obtain pitch fibers having an average diameter of 13 µm. A tow of 2,000 such pitch fibers was made infusible in air to obtain a tow of infusibilized fibers. Subsequent heat treatment at 650°C for 1 hour afforded carbonized fibers having a hydrogen/carbon element ratio of 0.10. Next, ten tows each consisting of 2,000 such infusibilized fibers and one tow of 2,000 carbonized fibers were simultaneously dropped little by little into a die while the die was moved to permit intimate mixing of the two in the interior of the die. Thereafter, the mixed fibers were carbonized under pressing by means of a hot press at a pressure of 5 kg/cm 2 , at 700°C, for 1 hour, to obtain a carbon/carbon composite having a void volume of 16% and a bulk density of 1.35 g/cm 3 . When the composite was taken out from the die, no change in shape was observed. (Example 6) An optically anisotropic petroleum pitch having a softening point of 280°C was melt-spun to obtain pitch fibers having an average diameter of 13 µm. A tow of 2,000 such pitch fibers was rendered infusible in air to obtain infusibilized fibers. Subsequent heat treatment in nitrogen at 650°C for 1 hour afforded carbonized fibers having a hydrogen/carbon element ratio of 0.10. Next, a tow of 2,000 such infusibilized fibers and a tow of 2,000 such carbonized fibers were simultaneously dropped little by little into a die while the die was moved to permit intimate mixing of the two in the interior of the die. Thereafter, the mixed fibers were carbonized under pressing by means of a hot press at a pressure of 5 kg/cm 3 , at 700°C, for 1 hour, to obtain a carbon/carbon composite having a void volume of 30% and a density of 1.1 g/cm 2 . When the composite was taken out from the die, there was no change in shape. The carbon/carbon composite was then subjected to a densifying treatment by chemical vapor deposition using methane as a starting gas at 1,200°C, at 1.5 Torr, for 120 hours, to obtain a densified carbon/carbon composite. The densified composite had a void volume of about 5% and was not cracked. It retained the shape of the carbon/carbon composite obtained initially. (Example 7) Ten tows each consisting of 1,000 infusibilized fibers and one tow of 1,000 carbonized fibers, both fibers obtained in Example 6, were simultaneously dropped little by little into a die while the die was moved to permit intimate mixing of the two in the interior of the die. Thereafter, the mixed fibers were carbonized under pressing by means of a hot press at a pressure of 5 kg/cm 2 , at 700°C, for 1 hour, to obtain a carbon/carbon composite having a void volume of 25% and a bulk density of 1.2 g/cm 2 . When the composite was taken out from the die, there was no change in shape. The carbon/carbon composite was then subjected to a densifying treatment by chemical vapor deposition using methane as a starting gas at 1,200°C, at 1.5 Torr, for 120 hours. The thus-densified carbon/carbon composite had a void volume of about 5% and was not cracked. It retained the shape of the carbon/carbon composite obtained initally. (Example 8) Ten tows each consisting of 500 infusibilized fibers and three tows each consisting of 500 carbonized fibers, both fibers obtained in Example 6, were simultaneously dropped little by little into a die while the die was moved to permit intimate mixing of the two in the interior of the die. Thereafter, the mixed fibers were carbonized under pressing by means of a hot press at a pressure of 5 kg/cm 2 , at 700°C, for 1 hour, to obtain a carbon/carbon composite having a void volume of 20% and a bulk density of 1.3 g/cm 3 When the composite was taken out from the die, no change in shape was observed. The carbon/carbon composite was then subjected to a densifying treatment using methane as a starting gas at 1,200°C, at 1.5 Torr, for 120 hours. The thus-densified carbon/carbon composite had a void volume of about 5% and was not cracked. It retained the shape of the carbon/carbon composite obtained initially. (Comparative Example 2) A tow of 2,000 carbon fibers was dropped little by little into a die while granular pitch was also dropped into the die and the die was moved to permit intimate mixing of the two. Subsequently, carbonization was performed under pressing using a hot press at a pressure of 10 kg/cm 2 , at 600°C, for 1 hour, to afford a carbon/carbon composite having a void volume of 30% and a bulk density of 1.1 g/cm 3 . The composite was then calcined in nitrogen at 1,000°C and at atmospheric pressure; as a result, it was cracked at its central part and it was impossible to obtain a densified carbon/carbon composite using such calcinate. (Comparative Example 3) An optically anisotropic petroleum pitch having a softening point of 280°C was melt-spun to obtain pitch fibers having an average diameter of 13 µm. A tow of 2,000 such pitch fibers was made infusible in air at 260°C for 1 hour to obtain a tow of infusibilized fibers. This tow of infusibilized fibers was passed as continuous fibers onto a pulley and fed into a hot pressing die continuously from above the die. The die was moved to permit uniform deposition of the infusibilized fibers in the interior of the die. Thereafter, the infusibilized fibers were carbonized under pressing by means of a hot press at a pressure of 100 kg/cm 2 , at 700°C, for 1 hour, to afford a preform (primary molded product) having a void volume of 4 % and a bulk density of 1.0 g/cm 3 . When the preform was taken out from the die, no change in shape , was observed. (Comparative Example 4) The preform of Comparative Example 3 was then subjected to a densifying treatment by chemical vapor deposition using methane as a starting gras at 1,200°C, at 1.5 Torr, for 120 hours, to obtain a carbon/carbon composite. The composite showed brittle fracture during bending tests.

Claims: A process for preparing a carbon/carbon composite preform, characterized in that a continuous pitch-based infusibilized fiber, optionally together with a pitch-based carbonized fiber, is charged into a vessel by being forced or allowed to fall freely and subjected to carbonization and molding under uniaxial pressing to obtain a carbon/carbon composite preform having a void volume of 15 - 70 vol. % and a bulk density of 0.10 - 1.70 g/cm 3 . A process as set forth in Claim 1 wherein the carbonized fiber is also charged to the vessel and is used in an amount of 5 to 1,000 parts by weight per 100 parts by weight of the infusibilized fiber. A process as set forth in Claim 1 or 2 wherein the carbonization and molding are preformed using a hot press at a pressure of 0.01 to 95 kg/cm 2 and at a temperature of 300 0 C to 2,000 °C. A process for preparing a carbon/carbon composite, characterized in that the carbon/carbon composite preform prepared by the method as set forth in any one of Claims 1 to 3 is densified using a carbonaceous matrix. A process as set forth in Claim 4, wherein the carbonaceous matrix is a carbonaceous matrix obtained by a chemical vapor deposition of a hydrocarbon gas or is a pitch-based carbonaceous matrix. A process as set forth in Claim 5, wherein the chemical vapor deposition is carried out by heating the hydrocarbon gas, optionally together with a diluting gas, to a temperature of 700 °C to 3,000 °C in the presence of a primary molded product, allowing carbon formed by thermal decomposition to be deposited within the preform. A process as set forth in Claim 5, wherein the densifying using the pitch-based carbonaceous matrix is carried out by heating the preform and a carbonaceous pitch to a temperature above a softening point of the pitch and below a decomposition start temperature thereof under a reduced pressure, allowing the pitch to be impregnated into the preform, and subsequently heating to a temperature of 400 °C to 2,000 °C under pressure or under pressing. A process as set forth in Claim 7, wherein the pitch has an optically anisotropic phase content of 60% to 100%.

Inventors: KOHNO TAKEFUMI, SANOKAWA YUTAKA, SOHDA YOSHIO, KOHNO, TAKEFUMI, SANOKAWA, YUTAKA, SOHDA, YOSHIO
Applicants: NIPPON OIL CO LTD, NIPPON OIL CO. LTD.
Application year: 1993
Main classification: C04B35
IPC codes: C04B35, F16D69