Buried heterostructure lasers using MOCVD growth over patterned substrates

Abstract: This invention pertains to buried heterostructure lasers which have been fabricated using a single step MOCVD growth of an MQW laser structure over a pattern etched GaAs substrate. The wet chemical etching of grooves having a dovetailed cross-section and being parallel to the [0 11 ] direction in GaAs substrates produced reentrant mesas which resulted in isolated laser active regions (17-2) buried by the AlGaAs cladding layer (18). The 250 µm long uncoated lasers emit at about 1 µm. Lasers with coated facets have threshold currents of 20 mA and emit >100 mW per facet under room temperature operation. The external differential quantum efficiency for currents of from 30 mA to about 50 mA is found to be nearly independent of temperature in the range of 10°C to 90°C suggesting a low temperature dependence of leakage current.

Description: Technical Field This invention pertains to buried heterostructure lasers with MOCVD growth over patterned substrates. Background of the Invention Semiconductor lasers fabricated from strained layer quantum well material have attracted considerable interest as pump lasers for erbium doped glass fiber amplifiers. However, ridge waveguide lasers with planar multi-quantum well (MQW) In 0.2 Ga 0.8 As/GaAs heterostructures grown by molecular beam epitaxy (MBE) and metal organic chemical vapor deposition (MOCVD) growth techniques are weakly index-guided, and their mode stability is not expected to be as good as that for a strongly index-guided buried heterostructure lasers. For example, see N. K. Dutta et al. "Temperature Dependence of Threshold of Strained Quantum Well Lasers", Appl. Phys. Lett. 58 (11), 18 March 1991, pages 1125-1127. The latter include several types of InGaAs/GaAs buried heterostructure lasers fabricated using multistep growths. An improvement in the lateral optical confinement in quantum well stripes resulted in lasers with GaAs/AlGaAs heterostructures fabricated using a single step growth on nonplanar GaAs substrates. One example of such a single growth structure is disclosed in an article by D. E. Ackley and G. Hom entitled "Twin-Channel Substrate-Mesa Guide Injection Lasers Fabricated by Organometallic Vapor Phase Epitaxy", Applied Physics Letters , Vol. 42, No. 8, April 1983, pages 653-655. Ackley and Hom disclose a high-power index-guided laser fabricated by a one-step organometallic vapor phase epitaxy on photolithographically patterned and etched substrates. A narrow mesa is defined by a twin-channel v-groove structure. The twin channel structure provides for an improved control over the width of the lateral waveguide relative to a single groove configuration, which allows well-controlled zero order mode operation. However, the growth of the active layer is continuous over the side walls of the v-grooves of the twin-channel defined mesa structure. This would lead to the spreading of carriers across the whole of the width of the active layer, not just across its portion on the mesa. Lateral electrical confinement was achieved by ion implantation after the growth of the semiconductor structure. Since ion-implantation requires subsequent heating of the device, this adds to the complexity of the process, negating the advantages of the single-step growth processing. Therefore, it is desirable to produce a buried heterostructure laser in a more simplified manner. A laser as set out in the preamble of claim 1 is disclosed in Patent Abstracts of Japan vol. 12, no. 304 (E-646) [3151], 18th August 1988 (JP-A-63 073 691). Summary of the Invention According to the invention there is provided a laser and a fabrication method as set out in the independent claims hereof. Each of said bottom and top confining layers may be of Al x Ga 1-x As₁, with x being from 0.1 to 0.4, and said active layer may be GaAs. Each of the confining layers may comprise Al 0.4 Ga 0.6 As, and may further comprise a thin Al 0.15 Ga 0.85 As layer positioned between the active layer and the Al 0.4 Ga 0.6 As layer. The active layer may comprise In y Ga 1-y As wells and GaAs barriers with y being within a range of from 0.05 to 0.25, and preferably three In 0.2 Ga 0.8 As wells and four GaAs barriers. The top electrode may comprise AuBe, and the overlay electrode may comprise TiAu. Preferably, said grooves are etched with a mixture of H₂SO₄:H₂O₂:H₂O in ratio of 1:1:1. The dielectric layer may comprise SiO₂. Each of the layers of the semiconductor structure may be deposited by MOCVD. In this process a single-step metal organic chemical vapor deposition (MOCVD) growth has been used to fabricate a buried heterostructure InGaAs/GaAs multi-quantum well laser over a patterned GaAs substrate. The pattern is a reentrant mesa defined by two dovetailed grooves formed by wet chemical etching oriented along [0 11 ] direction. Growth over the mesa results in isolated buried heterostructures. The 250 µm long lasers emitted near 1 µm. The external differential quantum efficiency in the current range of from 30 mA to about 50 mA is almost independent of temperature in the temperature range of 10°C to 90°C which suggests a minimal temperature dependent leakage current. Lasers with coated facets have threshold currents of 20 mA and emit > 100 mW/facet at room temperature. Brief Description of the Drawings FIG. 1 is a schematic representation of a buried heterostructure InGaAs/GaAs MQW laser; FIG. 2 is a schematic representation of the compound semiconductor substrate with a reentrant mesa bordered by two dovetailed grooves used in the fabrication of the laser of FIG. 1; FIG. 3 is a plot of power in mW versus current in mA for continuous wave operation of the laser of FIG. 1 at room temperature and wavelength of approximately 0.98 µm; Fig. 4 is a plot of light versus current curves for a buried heterostructure laser operated at temperatures ranging from 10°C to 90°C; Fig. 5 is a plot of threshold current versus temperature for a buried heterostructure laser. Detailed Description This invention embodies the fabrication of a buried heterostructure laser using a single-step growth by MOCVD over a reentrant mesa patterned semiconductor substrate. The growth over the reentrant mesa produces a discontinuity in the growth of a bottom confining layer and of an active layer, while the overgrowth of the top confining layer results in a buried heterostructure laser structure. The laser is a structure comprising group III-V or II-VI compound semiconductors, such as GaAs, AlAs, AlGaAs, InP, GaInP, AlInP, GaInAs, GaInPAs, AlGaInAs, and other lattice compatible compound semiconductors based on group III-V or II-VI semiconductors. FIG. 1 is a schematic cross-sectional representation of a laser, 10, according to the invention. Laser 10 includes in an ascending order, a bottom electrode, 11, a patterned substrate, 12, of one conductivity type provided with dovetailed grooves, 13, forming a reentrant mesa, 14, a discontinuous buffer layer, 15, having sections 15-1, 15-2 and 15-3 of said one conductivity type, a discontinuous bottom confining layer, 16, having sections 16-1, 16-2 and 16-3 of said one conductivity type, a discontinuous active layer, 17, having sections 17-1, 17-2 and 17-3, a top confining layer, 18, of another conductivity type opposite to said one conductivity type, a contact layer, 19, of said another conductivity type, a dielectric layer, 20, having a window, 21, a top stripe electrode, 22, within the window, and an overlay electrode, 23. Construction of laser 10 is described below. For clarity reasons, various elements of the laser are not drawn to scale. The invention is described with reference to an Al x Ga 1-x As/GaAs/In y Ga 1-y As system in which x is from 0 to 0.4 and y is from 0 to 0.25. Substrate 12 is a heavily doped n⁺ type GaAs having two dovetailed grooves 13 which form reentrant mesa 14. (FIG. 2). Typically the thickness of the substrate ranges from 100 to 500 µm and the doping concentration of the substrate ranges from 1x10¹⁷ to 1x10¹⁹cm⁻³. In some applications the substrate may be first grown on a master substrate of silicon which is common to a number of devices on the master substrate. Buffer layer 15 is also n-type GaAs deposited in a thickness typically ranging from 0.1µm to 5µm, and with a doping concentration of from 1x10¹⁷ to 1x10¹⁹ cm⁻³. The buffer layer serves the purpose of stopping possible propagation of defects from the substrate. The buffer layer is in the form of independent sections 15-1, 15-2 and 15-3. Sections 15-1 overlay the bottom of each dovetailed groove 13; section 15-2 overlays the top surface of mesa 14; and sections 15-3 overlay each of the remaining portions of the top surface of the substrate. The bottom and the top confining layers 16 and 18 are provided to confine carriers and, thus, the radiation of active layer 17 within the narrow thickness of the active layer. The confining layers are typically deposited in a thickness of up to 3 µm, and with a doping concentration of from 1x10¹⁷ to 1x10¹⁹ cm⁻³. In this embodiment, the confining layers are of Al x Ga 1-x As with x ranging from 0.1 to 0.4. The bottom confining layer is an n-type Al x Ga 1-x As and is in the form of independent sections 16-1, 16-2 and 16-3 which overlay sections 15-1, 15-2 and 15-3, respectively, of the buffer layer. Active layer 17 is in the form of independent sections 17-1, 17-2 and 17-3 which overlay sections 16-1, 16-2 and 16-3, respectively, of the bottom confining layer. The active layer includes at least one quantum well (QW) comprising In y Ga 1-y As well and GaAs barriers, with y being from 0.05 to 0.25. Top confining layer 18 is of a p-type Al x Ga 1-x As with x ranging from 0.1 to 0.4. Layer 18 overlays sections 17-1, 17-2 and 17-3 of the active layer and those portions of sections 15-2 and 15-3 and of sections 16-2 and 16-3 which are laterally exposed, such that section 17-2 of the active layer on the mesa is buried and is separated from sections 17-1 and 17-3 by the top confining layer. Thin contact layer 19 of highly doped p⁺ type GaAs completes the compound semiconductor structure. Typically, the doping concentration of the contact layer ranges from 1x10¹⁹ to 1x10²⁰cm⁻³. Contact layer 19 is provided in a thickness ranging from 0.01 to 0.1 µm to facilitate establishing an ohmic contact between top confining layer 18 and top electrode 22. Dielectric insulating layer 20, having window 21 which is centered over mesa 14, overlays the upper surface of contact layer 19 except for that portion of the surface of contact layer 19 which is exposed in the window, that is for an area immediately overlaying the area of mesa 14 and, thus, of section 17-2 of the discontinuous active layer 17. The dielectric layer insulates the top surface of contact layer 19 and protects it from environmental influences. The dielectric layer may be of a material selected from such insulating materials as SiO₂, SiN x and borosilicate glass (Vycor®). The first two are deposited by plasma CVD, while the latter is deposited by e-beam deposition. Top electrode 22 overlays that portion of the surface of contact layer 19 which is exposed in window 21. Since window 21 is of approximately the same length and width as the mesa, top electrode 22 is also centered over the mesa and over section 17-2 of the active layer which is upon the mesa. Top electrode 22 is of a metal or metal alloy selected from metals or alloys which are inert to or complement the conductivity type of the top confining and contact layers. Overlay electrode 23 is deposited over the insulating layer 19 and in electrical contact with top electrode 22. Overlay electrode 23 covers the whole of the upper surface of dielectric layer 18 and of top electrode 22. Overlay electrode 23, deposited in a thickness of from 0.05 to 1.0 µm, acts as a protective cover, as a surface for establishing an electrical contact to top electrode 22, and as a broad electrical connection area. Bottom electrode 11 is formed on the bottom surface of substrate 12 by depositing a suitable metal or alloy compatible with the conductivity type of the substrate, and alloying the electrode to the substrate. Optionally a layer of gold may be deposited on top of either one or both of overlay electrode 23 and bottom electrode 11. Finally, the bottom side of the laser may be mounted on a copper slab which serves as a heat sink. The preparation of the device begins with forming in the substrate a pattern shown in FIG. 2. Wafer substrates were etched to form "dovetail" grooves on either side of a reentrant mesa. Layers 15-19 forming the laser structure are then grown upon the patterned substrate in succession preferably by such known methods as metal organic vapor phase epitaxy (MOVPE), also known as metal organic chemical vapor deposition (MOCVD). These layers may also be deposited by such other known method as molecular beam epitaxy (MBE) or hydride vapor phase epitaxy (VPE). An important requirement is the deposition of layers 15-17 such that section 17-2 on the mesa is grown apart from other sections, e.g., 17-1 and 17-3 of layer 17. Due to the dovetailed shape of the grooves and of the reentrant shape of the mesas, the MOCVD growth of layers 15, 16 and 17 over the mesas is not continuous with the growth in the grooves and in the field. This results in an isolated layered structure including the MQW active layer 17-2 above the mesas. The top confining layer 18 fills in regions in the grooves, along the side and above the mesas. It is important that the substrate should be so oriented and the etching is so conducted that when the buffer, bottom confining and active layers are deposited, they form discontinuous layers and especially that at least section 17-2 of active layer 17 on the mesa does not have any continuity with sections 17-1 in the grooves. Hence this growth process results in MQW active regions (17-2) on top of the mesa which are buried in higher band gap and lower index layer 18. This assures that the current applied between top electrode 22 and bottom electrode 11 will pass through active layer section 17-2 but carriers will not spread along the whole of the active layer, including sections 17-1. In the preferred embodiment, the laser is an Al x Ga 1-x As/GaAs/In y Ga 1-y As structure comprising, in an ascending sequence, a 0.1 to 0.5µm thick AuGe electrode 11, about 100 µm thick (100) oriented heavily doped (2 x 10¹⁸cm⁻³) n⁺-GaAs substrate 12, a 0.2 to 0.3 µm thick n-type GaAs buffer layer 15 (3 x 10¹⁸cm⁻³), having sections 15-1, 15-2 and 15-3, a 1.5 µm thick n- Al 0.4 Ga 0.6 As bottom confining layer 16 (2 x 10¹⁸cm⁻³), having sections 16-1, 16-2 and 16-3, an MQW active layer 17 having sections 17-1, 17-2 and 17-3 consisting of three In 0.2 Ga 0.8 As wells 80 Å thick each and four GaAs barrier layers 200 Å thick each, 1.5 µm thick, p- Al 0.4 Ga 0.6 As top confining layer 18 (2 x 10¹⁸cm⁻³), and a 200 Å thick heavily doped (1 x 10¹⁹cm⁻³) p⁺ -GaAs contact layer 19. Alternatively, each of the confining layers may be deposited as a composite of 1.5 µm thick Al 0.4 Ga 0.6 As and a 400 Å thick Al 0.15 Ga 0.85 As layers, with the latter being in contact with the active layer. The Al 0.15 G 0.85 As layers are deposited optionally to narrow the far field of the device. The structure further includes an about 3000 Angstrom thick Si0₂ layer 20 having 2 to 4 µm wide window 21, a 0.08 µm thick AuBe top electrode 22 coextensive of window 21 and an 0.1 µm thick TiAu overlay electrode 23. The laser semiconductor structure shown in FIG. 1 was grown on one lateral surface of a n⁺-GaAs (100) substrate wafer which was patterned with grooves to leave mesas parallel to the [0 11 ] direction. Standard photolithographic and wet chemical techniques were used to obtain mesas of ∼4 µm wide. Wet chemical etching of n⁺-GaAs wafers with a mixture of H₂SO₄:H₂O₂:H₂0 in a ratio of 1:1:1 is used to produce in the substrate wafer two dovetailed grooves 13 and the reentrant mesa 14 per device. The etching is conducted at room temperature for a period of from 5 to 15, preferably 10 seconds. The dovetail grooves are from 5 to 3, preferably 4 µm wide and from 3 to 1, preferably 2 µm deep and are spaced each from another a distance of from 4.5 to 3.5 µm defining the reentrant mesa. The following layers were then grown over the etched wafer using the MOCVD growth technique: 0.5 µm thick n⁺ -GaAs buffer layer, followed by a 1.5 µm thick n-Al 0.4 Ga 0.6 As confining layer, the MQW active region consisting of 3 wells of 80Å thick In 0.2 Ga 0.8 As and four 200Å thick GaAs barrier layers, 1.5 µm thick p-Al 0.4 Ga 0.6 As confining layer and a 200Å thick p⁺ -GaAs contacting layer. The dopants used were Zn and Si for the p-type and n-type layers, respectively. After semiconductor layers 15-19 are deposited on the patterned substrate wafer, the fabrication process of the lasers (FIG. 1) is continued by formation of a SiO₂ layer and of AuBe (p-contact) top electrode, wafer thinning, formation of an AuGe (n-contact) bottom electrode, and formation of TiAu metal overlayer on the top of the SiO₂ and AuBe layers. The p-side of the wafer (surface of contact layer 19) is processed by depositing 3000Å SiO₂ and opening 2.5 - 4.5 µm wide windows over the mesas and active regions on the mesas, using photolithography and buffered oxide etchant to pattern the SiO₂. AuBe alloy (p-contact metal) was deposited in a thickness of 0.08 µm using standard photolithographic and lift-off methods resulting in AuBe contacts to contact layer 19 exposed in window 21 in the SiO₂ layer. The AuBe p-contact was then alloyed in a forming gas environment at 420°C for 30 sec. After this the bottom side of the wafer was thinned to 100 µm by chemo-mechanically polishing the substrate side using a 3 percent Bromine-Methanol solution. The bottom electrode 11 (n-contact) was prepared by depositing an AuGe alloy over the bottom surface of the substrate, and rapid thermally alloying at 350°C for 30 sec in forming gas. Deposition of thin layers of Ti and Au in a total thickness of from 0.05 to 1.0 µm by an e-beam evaporation process on top of the SiO₂ layer and of top electrode 22 completed the p-side processing. The wafer was then cleaved to produce chips of 250 µm cavity length. The 250 µm long lasers emitted near 1 µm. Lasers with coated facets were found to have threshold currents of ∼20 mA and were capable of emitting >100 mW per facet at room temperature continuous wave (CW) operation. See FIG. 3. For an example of coating mirror facets on a laser device see U.S. Patent 4,749,255 issued June 7, 1988, to Utpal K. Chakrabarti et al. Light intensities for lasers with uncoated facets in mW versus current characteristics of the laser in mA at different temperatures are shown in FIG. 4. The external differential quantum efficiency is found to be nearly independent of temperature in the range of 10°C to 90°C suggesting a low temperature dependence of leakage current. The lasing threshold was found to increase from 30 mA at room temperature to ∼50 mA at 90°C operation. The nearly parallel slopes of the L-I curves show a small variation of the external quantum efficiency with temperature which suggests a low temperature dependent leakage current. The threshold current plotted as a function of temperature is shown in FIG. 5. The dependence of the threshold current on temperature is represented by the expression: I th = I₀ exp(T/T₀) where I th is the threshold current and T is the temperature while I₀ and T₀ are constants. For the temperature range of 10°C to 90°C, the value of the characteristic temperature, T₀, is determined to be 120K.

Claims: A buried heterostructure laser, which comprises: a compound semiconductor structure and a top (22,23) and a bottom (11) electrode to the said structure, said structure including GaAs and AlGaAs and comprising in an ascending order a substrate (12) of one conductivity type, a buffer layer (15) of said one conductivity type, a bottom confining layer (16) of said one conductivity type, an active layer (17) and a top confining layer (18) of the conductivity type opposite to said one conductivity type, said substrate having two parallel grooves (13) each having a dovetailed cross-section, forming a reentrant mesa (14) between them, said buffer layer, said bottom confining layer and said active layer each having sections arranged in columns on the mesa and in the grooves, each of said sections in one column being laterally discontinuous with respect to the related sections in adjacent columns, CHARACTERIZED IN THAT said structure also includes InGaAs, being an AlGaAs/GaAs/InGaAs system said substrate is of (100) orientation, and said grooves are etched with [0 11 ] orientation, said active layer is a multiquantum well system of InGaAs wells and GaAs barriers, said top confining layer overlies sections of the active layer on top of each column and sloped walls of sections of the buffer layer, bottom confining layer and active layer so as to bury the section of the active layer of the column above the mesa and separate this section from the columns in the grooves, a contact layer (19) of said opposite conductivity type is on top of the top confining layer, a dielectric layer (20) having a window (21) coextensive with the mesa is on top of the contact layer, and said top electrode includes a stripe electrode (22) and an overlay electrode (23), said stripe electrode being in contact with an area of the contact layer exposed in said window, said stripe electrode being in the form of a narrow metal stripe and being coextensive with and in superimposed relation with the mesa and the section of the active layer above the mesa, and said overlay electrode is on the whole of the upper surface of the said stripe electrode and of said dielectric layer. The laser of claim 1, in which said active layer comprises In y Ga 1-y As wells and GaAs barriers, y being in the range 0.05 to 0.25. The laser of claim 2, in which the active layer includes three In 0.2 Ga 0.8 As wells and four GaAs barriers. The laser of any of the preceding claims, in which each of said bottom and top confining layers is of Al x Ga 1-x As, x being in the range 0.1 to 0.4. The laser of claim 4, in which each of said confining layers comprises Al 0.4 Ga 0.6 As. The laser of claim 5, in which each of said confining layers further comprises a thin Al 0.15 Ga 0.85 As layer positioned between the active layer and the Al 0.4 Ga 0.6 As layer. The laser of any of the preceding claims, in which said stripe electrode comprises AuBe. The laser of any of the preceding claims, in which said overlay electrode comprises TiAu. A method of making a buried heterostructure laser as claimed in any of the preceding claims, wherein said buffer layer, bottom confining layer, active layer, top confining layer and contact layer are deposited by MOCVD. The method of claim 10, in which said grooves are etched with a mixture of H₂SO₄:H₂O₂:H₂O in the ratio of 1:1:1.

Inventors: BERGER PAUL RAYMOND, DUTTA NILOY KUMAR, HOBSON WILLIAM SCOTT, LOPATA JOHN, BERGER, PAUL RAYMOND, DUTTA, NILOY KUMAR, HOBSON, WILLIAM SCOTT, LOPATA, JOHN
Applicants: AT & T CORP, AT&T CORP.
Application year: 1993
Main classification: H01S3
IPC codes: H01S5