Decomposable composite material

Abstract: A composite material consisting of aluminum and a resin composition primarily comprising a lactic acid base polymer, is disclosed. The composite material is excellent in mechanical and gas barrier properties and has characteristic of disappearing with ease by decomposing under alkaline conditions.

Description: BACKGROUND OF THE INVENTION AND RELATED ART 1. Field of the Invention The present invention relates to a decomposable composite material, and more particularly, relates to a readily decomposable composite material having excellent gas-barrier properties and consisting of aluminum and a thermoplastic polymer which primarily comprises a lactic acid polymer. 2. Related Art of the Invention For packaging material, polyethylene, polyethylene terephthalate, polyvinyl chloride, polypropylene, paper, aluminium and composite materials of these materials have conventionally been used. Although some of these packaging material prepared from these plastics are excellent in gas-barrier properties, these materials have a very slow rate of degradation and thus remain semipermanently when discarded as refuse and buried under the ground. Disposal of these plastics in the ocean causes damage of the view or destruction of the living environment of marine organisms. Paper is degradable in the natural environment while lacking gas-barrier properties and thus suffers from the disadvantage that packed content cannot be stored for a long period. On the other hand, an aluminum foil has high gas-barrier properties and low mechanical strength and thus suffers from the defect that the package is broken in the course of transport and the content cannot be protected. On the other hand, polylactic acids and copolymers of lactic acid and other hydroxycarboxylic acids (generic name of the polylactic acid and the copolymer will hereinafter be referred to simply as a lactic acid base polymer) have been known as thermoplastic polymers having degradability. These polymers can be completely biodegraded within a few months to an year in the animal body. When the polymers are placed in soil or sea water, they start to decompose within a few weeks in a moist environment and disappear within several years. Further, final degradation products of these polymers are lactic acid, carbon dioxide and water which are nontoxic to human body. Polymers of lactic add are usually prepared from a cyclic dimer of lactic acid which is called lactide. US-A-1,995,970,2,362,511, and 2,683,136 disclose a polymerization process of lactide. US-A-3,636,956 and 3,797,499 disclose a process for copolymerizing lactic acid and glycolic acid. In the copolymerization of lactic acid and other hydroxy carboxylic acids to produce a copolymer, lactide and a cyclic ester intermediate, for example glycolide, i.e., a dimer of glycolic acid, are used for polymerization. EP-A-0 514 137 (a document under Art. 54(3)EPC) relates to a laminated material comprising a layer of polylactic acid or a copolymer of lactic acid with a hydroxy carboxylic acid and a layer of regenerated cellulose, paper, leather, cloth or fibers and optionally another film layer, e.g. of aluminum foil. WO-A-90/01521 discloses the use of plasticised polymers of L-lactide, D-lactide, D,L-lactide and mixtures thereof, optionally in combination with fibrous mats or fibers, such as cellulose, nylon, cellulose acetate etc. for packaging materials. These polymers may comprise known filler materials, among others aluminum powder. The above lactic acid base polymer is degradable, but has relatively high gas permeability and leads to problems when the polymer is used in the fields where gas-barrier properties are required. Consequently, the delopment of composite materials which can be decomposed with ease and are excellent in gas-barrier properties has been strongly desired. SUMMARY OF THE INVENTION An object of the invention is to provide a composite material which can be decomposed with ease and is excellent in gas-barrier properties. In the course of an intensive research on the degradable polymers, the present inventors have focused attention on the above lactic acid base polymer and found that a composite material consisting of aluminum and a resin composition which primarily comprises a lactic acid base polymer is excellent in mechanical strength and gas barrier properties and can be disposed by decomposing with ease in an alkaline condition. Thus the invention has been completed. The present invention is directed to a decomposable composite material consisting of a layer of aluminum and a laver of a thermoplastic polymer composition. wherein said thermoplastic polymer composition primarily comprises polylactic acid or a copolymer of lactic acid and another hydroxy carboxylic acid the polylactic acid or the copolymer of lactic acid and another hydroxy carboxylic acid having a weight average molecular weight of 70,000 or more, and wherein said layers are in the form of a foil or a shaped body. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS The lactic acid base polymer used for the invention is polylactic add or a copolymer of lactic acid and hydroxycarboxylic acids other than lactic acid. Hydroxycarboxylic acids which can be used include, for example, glycolic acid, 3-hydroxybutyric acid, 4-hydroxybutyric acid, 4-hydroxyvaleric acid, 5-hydroxyvaleric acid and 6-hydroxycaproic acid. The lactic acid used as a raw material of the present invention is L-lactic acid. D-lactic acid or a mixture thereof. The lactic acid base polymer can be obtained by a direct dehydrating polycondensation process of lactic acid, a direct dehydrating copolycondensation process of lactic acid and the other hydroxycarboxylic acid than lactic acid or a ring-opening polymerization process of a cyclic dimer such as lactide, the cyclic dimer of lactic acid, glycolide (GLD), the cyclic dimer of glycolic acid, ε-caprolactone (CL), the cyclic ester of 6-hydroxycaproic acid and other monomers which are copolymerizable with these raw materials. When the lactic acid base polymer is prepared by direct dehydration condensation, lactic acid or a mixture of lactic acid with other hydroxycarboxylic acid is subjected to azeotropic dehydration condensation preferably in the presence of an organic solvent, diphenyl ether based solvent in particular. The condensation is more preferably progressed by returning a substantially anhydrous solvent to the reaction system after removing water from an azeotropically distilled solvent. High molecular weight polylactic acid having sufficient strength for use in the invention can be obtained by such a method. The polymer thus obtained, a copolymer of L-lactic acid and D-lactic acid or a copolymer of lactic acid and glycolic acid in particular, differs in physical properties from the polymer obtained by usual ring-opening polymerization. A composite material prepared from the polymer thus-obtained also differs in properties for practical use such as heat sealability. The thermoplastic polymer composition is prepared by adding usual known thermoplastic polymers, plasticizers and other various additives to the lactic acid base polymer. The known thermoplastic polymers preferably include degradable polymers such as polyglycolic acid and poly-ε-caprolactone. The preferred proportion of the lactic acid base polymer in the thermoplastic polymer composition depends upon the desired decomposability and is generally 50 % or more. The thermoplastic polymer composition can be prepared by application of any known techniques and is used in the form of pellets, rods and powder. The decomposable composite material consisting of aluminum and the thermoplastic polymer composition of the invention can be prepared by coating a thermoplastic polymer on an aluminum foil or a shaped form of aluminum or by vacuum depositing aluminum on a film or a molded form of the thermoplastic polymer. Coating methods include for example, a method of dissolving the thermoplastic resin in a solvent, coating the solution on an aluminum foil or shaped form and drying the coated aluminum; a method of melting the thermoplastic resin and coating the molten resin on aluminum; and a method of adhering a thermoplastic polymer film to an aluminum foil or shaped form by hot-pressing or with an adhesive. Exemplary adhesives which can be used include gelatin, starch paste and low molecular weight polylactic acid. EXAMPLES The present invention will hereinafter be illustrated in detail by way of examples and comparative examples. In the examples and comparative examples, the weight average molecular weight of the polymer was measured by gel permeation chromatography under the following conditions using polystyrene as a reference. Equipment Shimadzu LC-10 AD Detector Shimadzu RID-6A Column Hitachi Kasei GL-S350DT-5, GL-S370DT-5 Solvent Chloroform Concentration 1 % Amount of sample 20 µℓ Flow rate 1.0 ml/min Preparation Example 1 Into a thick-walled cylindrical stainless steel polymerizer equipped with a stirrer, 216g (1.5 mol) of L-lactide, 0.01 % by weight of stannous octoate and 0.03 % by weight of dodecyl alcohol were charged. The mixture was deaerated for 2 hours under vacuum and heated in a nitrogen atmosphere with stirring at 200 °C for 3 hours. Then the polymerizer was gradually deaerated through a gas outlet tube and glass receiver with a vacuum pump to a reduced pressure of 0.4 kPa (3 mmHg) while maintaining the same temperature. After reacting for an hour from the start of deaeration, distillation of monomer and low molecular weight volatiles ceased. The interior of the polymerizer was replaced by nitrogen. Poly-L-lactic acid obtained was discharged from the bottom of the polymerizer in the form of a strand and cut into pellets. The pelletized polymer had an average molecular weight of 100,000. Preparation Example 2 Polylactic add pellets were prepared by carrying out the same procedures as described in Preparation Example 1 except that 216 g of L-lactide was replaced by 172 g of L-lactide and 44 g of DL-lactide. The polymer obtained had an average molecular weight of 100, 000. Preparation Example 3 L-lactide-glycolide copolymer pellets were prepared by carrying out the same procedures as described in Preparation Example 1 except that 216 g of L-lactide was replaced by 108 g of L-lactide and 108 g of glycolide. The copolymer obtained had an average molecular weight of 100,000. Preparation Example 4 L-lactide-ε-caprolactone copolymer pellets were prepared by carrying out the same procedures as described in Preparation Example 1 except that 216 g of L-lactide was replaced by 108 g of L-lactide and 108 g of ε-caprolactone. The copolymer obtained had an average molecular weight of 70,000. Preparation Example 5 In a reaction vessel, 10.0 kg of 90 % L-lactic acid was heated with stirring at 150 °C for 3 hours under reduced pressure of 6.7 kPa (50 mmHg) while distilling out water. Thereafter 6.2 g of tin powder was added and further reacted with stirring at 150 °C for 2 hours under reduced pressure of 4 kPa (30 mmHg) to obtain an oligomer. To the oligomer, 28.8 g tin powder and 21.1 kg of diphenyl ether were added, and an azeotropic dehydration reaction was carried out at 150 °C under reduced pressure of 4.7 kPa (35 mmHg). Distilled water was separated from the solvent in a water separator and the solvent alone was returned to the reaction vessel. After reacting for 2 hours, a returning pass of the solvent was changed to pass through a column packed with 4.6 kg of molecular sieve 3A before returning to the reaction vessel. Successively, the reaction was continued at 150°C for 40 hours under reduced pressure of 4.7 kPa (35 mmHg) to obtain a polylactic acid solution having an average molecular weight of 110,000. The solution obtained was mixed with 44 kg of dehydrated diphenyl ether and cooled to 40 °C. Precipitated crystals were filtered, washed three times with 10 kg of n-hexane and dried at 60 °C under reduced pressure of 6.7 kPa (50 mmHg). The powder thus obtained was mixed with 12 kg of 0.5 N hydrochloric acid and 12.0 kg of ethanol, stirred at 35 °C for an hour, filtered and dried at 60°C under reduced pressure of 6.7 kPa (50 mmHg) to obtain 6.1 kg of polylactic acid powder (85 % yield). The powder was pelletized with a pelletizer and used for measuring properties. The polymer obtained had an average molecular weight of 110,000. The polymers obtained in Preparation Examples 1-5 were individually dissolved in chloroform in a concentration of 10-20 %, cast respectively on a glass plate and dried at 60 °C under reduced pressure. Films thus prepared had a thickness of 25-30 µm and were used in the following examples. In any of the above examples and comparative examples, gas permeability and moisture permeability were measured by the following methods on each composite material obtained. (1) O 2 and CO 2 gas permeability: In accordance with JIS K-7126 Method A (Pressure difference method) which corresponds to ASTM D-1434. (2) Moisture permeability: In accordance with JIS K-0208. Results are illustrated in Table . EXAMPLE 1 A 30 % aqueous gelatin solution was coated as an adhesive on an aluminum foil having dimensions of 150 mm in length, 150 mm in width and 7 µm in thickness. The coated surface was superimposed on a film which was obtained from the polymer of Preparation Example 1 and had thickness of 30 µm. The overlapped film was pressed overnight under pressure of 0.1 MPa (1 kg/cm 2 ). Adhesion between the aluminum foil and the polymer film was good. A composite film thus obtained had good surface glass, high transparency in a resin layer and high strength. The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. EXAMPLE 2 The same polylactic acid film as used in Example 1 was superimposed on an aluminum foil having dimensions of 150 mm × 150 mm × 7 µm and hot-pressed at 175 °C for 5 minutes under the pressure of 3 MPa (30 kg/cm 2 ). Adhesion between the aluminum foil and the polymer film was good. The composite film thus obtained had good surface gloss, high transparency of a resin layer and high strength. Two composite films were overlapped so as to bring the polymer sides into contact with each other and hot-pressed at 105 °C for 0.5 second under the pressure of 0.05 MPa (0.5 kg/cm 2 ). These films, however, could not be adhered. Press temperature of 118 °C was required in order to adhere by pressing for 0.5 second under the pressure of 0.05 MPa (0.5 kg/cm 2 ). The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. EXAMPLE 3 A composite film was prepared by the same procedures as described in Example 2 except that the film obtained from the polymer of Preparation Example 1 was replaced by the film which was obtained from the polymer of Preparation Example 2 and had a thickness of 25 µm. Adhesion between aluminum foil and the polymer film was good. The composite film obtained had good surface gloss, high transparency of a resin layer and high strength. The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. EXAMPLE 4 A composite film was prepared by the same procedures as described in Example 2 except that the film obtained from the polymer of Preparation Example 1 was replaced by the film which was obtained from the polymer of Preparation Example 3 and had a thickness of 25 µm. Adhesion between the aluminum foil and the polymer film was good. The composite film obtained had good surface gloss, high transparency of a resin layer and high strength. The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. EXAMPLE 5 A composite film was prepared by the same procedures as described in Example 2 except that the film obtained from the polymer of Preparation Example 1 was replaced by the film which was obtained from the polymer of Preparation Example 4 and had a thickness of 25 µm. Adhesion between aluminum foil and the polymer film was good. The composite film obtained had good surface gloss, high transparency of a resin layer and high strength. The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. EXAMPLE 6 To an aluminum foil having dimensions of 150 mm × 150 mm × 7 µm. 20g of a 15% chloroform solution containing the polymer prepared in Preparation Example 1 was applied and dried overnight at room temperature. The coated film was further dried at 50 °C under reduced pressure. The composite film thus obtained had good surface gloss, high transparency of a resin layer and high strength. The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. EXAMPLE 7 A metallized film was prepared by vapor deposition of aluminum to a thickness of 50 nm (500 Å) on a film which was obtained from the polymer of Preparation Example 1 and had dimensions of 150 mm × 150 mm × 30 µm. The polymer surface of the film obtained had good gloss and the resin layer had high transparency. The film obtained was buried in a soil having a moisture content of 30 % and temperature of 35°C. After a month, the film strength was drastically decreased and the film shape was broken with ease by external force. EXAMPLE 8 A composite film was prepared by the same procedure as described in Example 2 except that the film obtained from the polymer of Preparation Example 1 was replaced by the film which was obtained from the polymer of Preparation Example 5 and had a thickness of 25 µm. Adhesion between aluminum foil and the polymer film was good. The composite film obtained had good surface gloss, high transparency of a resin layer and high strength. Two composite films were overlapped so as to bring their polymer sides into contact and hot-pressed at a hot-plate temperature of 105 °C for 0.5 second under the pressure of 0.05 MPa (0.5 kg/cm 2 ). Good adhesion could be obtained. The film thus obtained was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The film was completely dissolved in the solution. COMPARATIVE EXAMPLE 1 A film having a thickness of 30 µm was prepared from the polymer of Preparation Example 1. The film had a very high permeability for gas and moisture. COMPARATIVE EXAMPLE 2 A composite film was prepared by the same procedures as described in Example 1 except that the polylactic acid film was replaced by a polypropylene film having a thickness of 30 µm. The polymer surface of the composite film had some haze. The composite film was immersed in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The aluminum layer of the composite film was dissolved in the solution, but the polypropylene film maintained the shape. COMPARATIVE EXAMPLE 3 A metallized film was prepared by the same procedures as described in Example 7 except that the polylactic acid film was replaced by a polypropylene film of 30 µm in thickness. The polymer surface of the metallized film had some haze. The metallized film was submerged in an 1 N aqueous sodium hydroxide solution at 60 °C for an hour. The aluminum layer of the metallized film was dissolved in the solution. However, the polypropylene film maintained the shape. COMPARATIVE EXAMPLE 4 A composite film was prepared by the same procedures as described in Example 2 except that the polylactic acid film was replaced by a copolymer film which had an average molecular weight of 190,000, consisted of 3-hydroxybutyric acid and 3-hydroxyvaleric acid in a weight ratio of 75:25, and was 30 µm in thickness. The copolymer surface of the composite film had some haze. The composite film was submerged in an 1 N aqueous sodium hydroxide solution at 60°C for an hour. The aluminum layer was dissolved in the solution. However, the copolymer layer maintained the shape. Gas permeability (cm 3 /m 2 • 24 h • atm) Moisture permeability (g/m 2 • 24 h) O 2 CO 2 Example 1 0 0 0 Example 2 0 0 0 Example 3 0 0 0 Example 4 0 0 0 Example 5 0 0 0 Example 6 0 0 0 Example 7 35 110 14 Example 8 0 0 0 Comp. Ex. 1 380 1200 150 Comp. Ex. 2 0 0 0 Comp. Ex. 3 180 530 2 Comp. Ex. 4 0 0 0 In the Table Comp. Ex. means Comparative Example.

Claims: A decomposable composite material consisting of a layer of aluminum and a layer of a thermoplastic polymer composition, wherein said thermoplastic polymer composition primarily comprises polylactic acid or a copolymer of lactic acid and another hydroxycarboxylic acid, said polylactic acid or copolymer of lactic acid and another hydroxycarboxylic acid having a weight average molecular weight of 70,000 or more, and wherein said layers are in the form of a foil or a shaped body. A decomposable composite material of claim 1 wherein lactic acid is L-lactic acid, D-lactic add or a mixture of these lactic acids. A decomposable composite material of claim 1 or claim 2 wherein the other hydroxycarboxylic acid is glycolic acid or 6-hydroxycaproic acid. A decomposable composite material of any of the claims 1 to 3 obtained by coating a layer of a thermoplastic polymer composition on an aluminum foil. A decomposable composite material of any of the claims 1 to 3 obtained by vapor deposition of aluminum on a shaped body of the thermoplastic polymer composition.

Inventors: AJIOKA MASANOBU, ENOMOTO KATASHI, SUZUKI KAZUHIKO, YAMAGUCHI AKIHIRO, AJIOKA, MASANOBU, ENOMOTO, KATASHI, SUZUKI, KAZUHIKO, YAMAGUCHI, AKIHIRO
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1993
Main classification: B32B15
IPC codes: B32B27, B32B15, C08L67