2,2'-Dimethyl-5,5'-diaminodiphenyl sulfone

Abstract: The present invention relates to 2,2'-dimethyl-5,5'-diaminodiphenyl sulfone, useful as a hardener for epoxy resins and as a starting material for other polymeric applications.

Description: The invention relates to 2,2'-Dimethyl-5,5'-diaminodiphenyl sulfone and a resin system comprising the said sulfone as a hardener. US-Patent No. 4,500,582 discloses a resinous hardener system comprising an adduct of an epoxy resin with a diamino diphenylsulfones of the formula wherein R 1 , R 2 , R 3 and R 4 are independently hydrogen, straight and branched chain alkyl of 1 to 12 carbon atoms, preferably 1 to 4 carbon atoms or halogen. It is the primary object of this invention to provide a modified hardener system for epoxy resins. It is a further object to provide such a hardener system which improves upon the performance of diamino diphenylsulfone hardeners. It is another object to utilize such hardener systems with a wide variety of epoxy resins to provide prepreg or laminating resins of improved performance characteristics. Various other objects and advantages of this invention will become apparent from the following descriptive material and illustrative examples. Applicants have surprisingly found that resin systems comprising epoxy resins and 2,2'-dimethyl-5,5'-diamino diphenyl sulfone, as a hardener, exhibits improved processing characteristics. 2,2'-dimethyl-5,5'-diamino diphenyl sulfone is prepared from 2,2'-dimethyl-5,5'-dinitrodiphenyl sulfone by conventional reduction. The hardener of the present invention lends itself for use in primary composite structures. The resin system of the present invention is useful in a wide area of applications such as coatings, molded castings, adhesives and filament wound structures. Resin systems according to the present invention comprise an epoxy resin and said sulfone. The sulfone is present in an amount ranging from about 0.5 to about 1.0, preferably about 0.8 to about 1.0 equivalents of aminohydrogen per equivalent of epoxy. Suitable epoxy resins include epoxide resins based on polyhydric phenols such as those based on bisphenol A, F, and S, epoxidation products of cresol novolacs, and epoxidation products of phenol novolacs; hydantoin epoxide resins; polyglycidyl esters; glycidylated aromatic amines; glycidylated aminophenols; and certain cycloaliphatic epoxy resins. Tetraglycidylated methylene dianiline is preferred for purposes of the instant invention. In addition, in adhesive, coating and filament winding applications, resin based on the diglycidyl ether of bisphenol A is widely used. Techniques for preparing prepregs are well known to those skilled in the art. In terms of honeycomb skins, graphite, glass, Kevlar reinforced skins as well as others, can be readily prepared from the instant systems. Correspondingly, techniques for preparing laminates are well known. Such laminates may be prepared by compression or autoclave molding and may comprise a broad range of thicknesses. Apart from the above areas of utility, the sulfone of this invention is useful as a curing agent for a wide variety of epoxy resins in various heat cured applications. When combined with di- and polyepoxides, at generally stoichiometric amounts, and cured at elevated temperatures, a network of high crosslink density occurs. Accordingly, the expression "cure" as used herein, denotes the conversion of the above sulfone and epoxide material into insoluble and infusible crosslinked products, with simultaneous shaping to give shaped articles such as castings, pressings or laminates, or to give two-dimensional structures such as coatings, enamels or adhesive bonds. The sulfone of the present invention is particularly advantageous for the formation of coatings because of the improved compatibility with resins and the improved toughness of the resulting cured coatings. The compositions of the present invention can furthermore be mixed, at any stage before cure, with usual modifiers such as extenders, fillers and reinforcing agents, pigments, dyestuffs, organic solvents, plasticizers, tackifiers, rubbers, accelerators, diluents, and the like. As extenders, reinforcing agents, fillers and pigments which can be employed in the curable mixtures according to the invention there may be mentioned, for example: coal tar, bitumen, glass fibers, boron fibers, carbon fibers, cellulose, polyethylene powder, polypropylene powder, mica, asbestos, quartz powder, gypsum, antimony trioxide, bentones, silica aerogel ("Aerosil"), lithopone, barite, titanium dioxide, carbon black, graphite, iron oxide, or metal powders such as aluminum powder or iron powder. It is also possible to add other usual additives, for example, flameproofing agents, agents for conferring thixotropy, flow control agents such as silicones, cellulose acetate butyrate, polyvinyl butyral, waxes, stearates and the like (which are in part also used as mold release agents) to the curable mixtures. It is also possible in adhesive formulations, for example, to add rubbers such as carbonyl-terminated acrylonitrile-butadiene rubber, modifying resins such as triglycidyl p-aminophenol, accelerators such as boron trifluoride monoethylamine complexes or imidazole complexes, and other additional hardeners such as dicyandiamide. The curable mixtures can be manufactured in the usual manner with the aid of known mixing equipment (stirrers, kneaders, rollers and the like). The following examples will further illustrate the embodiments of the instant invention, but are not intended to limit this invention. Examples 1-3 These examples illustrate the preparation of a curable mixture according to the present invention and the preparation of 2 controls for comparative purposes. The curable mixtures are prepared by heating the resin in a 3 neck flask to a temperature just sufficient to dissolve the hardener in an oil bath. The hardener is then added slowly and the mixture stirred until all solids are dissolved. The resulting prepolymer is then degassed with a mechanical vacuum pump and the prepolymer is then poured into a preheated aluminum mold and cured. A du Pont 9900 Differential Scanning Colorimeter is used to determine reaction temperatures; gel times are determined using a hot plate, system viscosities and pot lives are measuring with a Brookfield viscometer, viscosity isotherms are obtained with a Rheometrics Dynamic Spectrometer (RDA 700) and Dynamic Young's Moduli are measured by Dynamic Mechanical Analysis (du Pont DMA 983). The formulations are presented in Table 1 and the physical properties are presented in Table 2. Formulations (Parts by weight) Component Ex. 1 Ex. 2 Ex. 3 MY 720 (tetraglycidylated methylene dianiline from CIBA-GEIGY Corp.) 100 100 100 HT 976 (4,4'-diamino diphenyl sulfone from CIBA-GEIGY Corp.) - 44 - 2,2'-dimethyl-5,5'-diamino diphenyl sulfone 50 - - 3,3'-diamino diphenyl sulfone - - 44 The following Table 2 shows that the DSC identified exotherm initiation (Ti) and peak (Tpk) temperatures for Example 1 in accordance with the present invention are 20°C and 40°C lower, respectively, than those of control Example 2. At 100°C, the viscosity of Example 1 in accordance with the present invention is almost twice that of both control Examples 2 and 3. Furthermore, the pot-life (time required to double the initial viscosity) at 100°C of Example 1 is significantly shorter (2.0 hours) than that of control Example 2 (> 2.5 hours) and control Example 3 (2.5 hours). The resin system of Example 1 gelled within 5 minutes at 177°C, whereas under the same conditions the resin systems of control Examples 2 and 3 gelled in 17.9 and 7.7 minutes, respectively. Physical Properties DSC Ex. 1 Ex. 2 Ex. 3 Ti, °C 150 170 135 Tpk, °C 207 245 223 ΔH, J/g 557 557 322 VISCOSITY at 100°C (cps) 1080 580 600 POT-LIFE (Time to double initial viscosity). at 100°C (hrs) 2.0 >2.5 2.5 GEL TIME AT 177°C (min.) 4.8 17.9 7.7 Examples 4 and 5 These examples illustrate the preparation of a curable mixture according to the present invention and the preparation of a control for comparative purposes. The formulations are provided in Table 3 and the physical properties are presented in Table 4. Formulations Component (parts by weight) Ex. 4 Ex. 5 RD 87-160 (Tetra-functional Epoxy from CIBA-GEIGY Corp.) 100 100 HT 976 (4,4'-diamino diphenyl sulfone from CIBA-GEIGY Corp.) - 44 2,2'-dimethyl-5,5'-diaminodiphenyl sulfone 50 - Physical Properties DSC Ex. 4 Ex. 5 Ti, °C 165 170 Tpk, °C 228 254 ΔH, J/g 432 439 VISCOSITY at 100°C (cps) 265 GEL TIME AT 177°C (min.) 11.1 37.2 CURE SCHEDULE Room temperature to 177°C using an increase in temperature of 2°C/min, then 4 hours at 177°C DMA MODULUS, DRY (KSI) 25°C 548 577 150°C 430 (79%) 438 (76%) 200°C 333 (61%) 340 (59%) Tg, °C 220 220 Values in parentheses indicate retention of room temperature modulus. The DSC identified initiation temperature of the resin system of Example 4 is equivalent to control Example 5. However, the peak (Tpk) temperature of the resin system of Example 4 is approximately 30°C lower than that of the control Example 5. At 177°C the resin system of Example 4 gelled three times faster than that of control Example 5 (11.1 minutes as compared with 37.2 minutes, respectively). Thus, the results establish that 2,2'-dimethyl-5,5'-diaminodiphenyl sulfone exhibits a higher melting point, reactivity, and equivalent weight than 3,3'-diaminodiphenyl sulfone and 4,4'-diaminodiphenyl sulfone. The resin system in accordance with the present invention exhibits good thermal-mechanical properties.

Claims: 2,2'-Dimethyl-5,5'-diaminodiphenyl sulfone. A resin system comprising an epoxy resin and 2,2'-dimethyl-5,5'-diaminodiphenyl sulfone. A resin system according to claim 2 wherein said 2,2'-dimethyl-5,5'-diaminodiphenyl sulfone is present in an amount ranging from about 0.5 to about 1.0 equivalents of aminohydrogen per equivalent of epoxy. A resin system according to claim 2 wherein said 2,2'-dimethyl-5,5'-diaminodiphenyl sulfone is present in an amount ranging from about 0.8 to about 1.0 equivalents of aminohydrogen per equivalent of epoxy. A resin system acccording to claim 2 wherein said epoxy resin is selected from the group consisting of epoxide resins based on polyhydric phenols, epoxidation products of cresol novolacs and phenol novolacs, hydantoin epoxide resins, polyglycidyl esters, glycidylated aromatic amines, glycidylated aminophenols, and cycloaliphatic epoxy resins. A resin system according to claim 2 wherein said epoxy resin is tetraglycidylated methylene dianiline. A resin system according to claim 2 wherein said epoxy resin is based on the diglycidyl ether of bisphenol A. A resin system according to claim 2 further comprising modifiers, fillers and reinforcing agents, pigments, dyestuffs, organic solvents, plasticizers, tackifiers, rubbers, accelerators, diluents or combinations thereof. A resin system according to claim 2 further comprising coal tar, bitumen, glass fibers, boron fibers, carbon fibers, cellulose, polyethylene powder, polypropylene powder, mica, asbestos, quartz powder, gypsum, antimony trioxide, bentones, silica aerogel, lithopone, barite, titanium dioxide, carbon black, graphite, iron oxide, metal powders or a combination thereof. A resin system according to claim 2 further comprising flameproofing agents, agents for conferring thixotropy, flow control agents, cellulose acetate butyrate, polyvinyl butyral, waxes, stearates or a combination thereof. A resin system according to claim 2 further comprising rubbers, modifying resins accelerators, additional hardeners and combinations thereof. A resin system according to claim 2 further comprising carbonyl-terminated acrylonitrile-butadiene rubber, triglycidyl p-aminophenol, boron trifluoride monoethylamine complexes or imidazole complexes, dicyandiamide and combinations thereof.

Inventors: FU BERNIE, KING JOHN, LEE BYUNG, FU, BERNIE, KING, JOHN, LEE, BYUNG
Applicants: CIBA GEIGY AG, CIBA SPECIALTY CHEMICALS HOLDING INC.
Application year: 1993
Main classification: C08G59
IPC codes: C08G59, C07C317, C08L63