Ethylene copolymer composition

Abstract: An ethylene copolymer composition comprising an ethylene/α-olefin copolymer [A-1] which has a density, a melt flow rate (MFR), an amount of a n-decane-soluble portion in the specific ranges and whose melt tension (MT) at 190 °C and MFR satisfy the relation MT>2.2xMFR -0.84 , and one (co)polymer selected from the group consisting of [B-1] a low-density polyethylene obtained by high-pressure radical polymerization, [B-2] a crystalline polyolefin and [B-3] an olefin type elastomer. Also disclosed is an ethylene copolymer composition comprising an ethylene/α-olefin copolymer composition and the low-density polyethylene [B-1] obtained by high-pressure radical polymerization, said ethylene/α-olefin copolymer composition comprising ethylene/α-olefin copolymers [A-2] and [A-3] both having physical properties similar to those of the above ethylene/α-olefin copolymer [A-1] and having intrinsic viscosities different from each other. Further disclosed is an ethylene copolymer composition comprising an ethylene/α-olefin copolymer [A-4] which has a density, a melt flow rate (MFR), a weight of a n-decane-soluble portion in the specific ranges and whose melt tension (MT) at 190 °C and MFR satisfy the relation MT≦2.2XMFR -0.84 , and one (co)polymer selected from the above group consisting of [B-1], [B-2] and [B-3]. Still further disclosed is an ethylene copolymer composition comprising an ethylene/α-olefin copolymer composition and a low-density polyethylene [B-4] obtained by high-pressure radical polymerization, said ethylene/α-olefin copolymer composition comprising ethylene/α-olefin copolymers [A-5] and [A-6] both having physical properties similar to those of the above ethylene/α-olefin copolymer [A-4] and having intrinsic viscosities different from each other. The ethylene copolymer compositions of the invention are excellent in heat stability and moldability, and able to form films of high transparency, high mechanical strength and anti-blocking resistance.

Description: FIELD OF THE INVENTION The present invention relates to ethylene copolymer compositions, more particularly to ethylene copolymer compositions which show higher heat stability and moldability as compared with conventional ethylene copolymers or ethylene copolymer compositions and from which films of high transparency, high mechanical strength and high blocking resistance can be formed. BACKGROUND OF THE INVENTION Ethylene copolymers have heretofore been molded by various molding methods, and used in many fields. The requirement for the characteristics of the ethylene copolymers differs depending on the molding methods and uses. For example, when an inflation film is molded at a high speed, it is necessary to select an ethylene copolymer having a high melt tension compared with its molecular weight in order to stably conduct high speed molding without fluctuation or tearing of bubbles. An ethylene copolymer is required to have similar characteristics in order to prevent sag or tearing in blow molding, or to suppress width shortage to the minimum range in T-die molding. Further, in extrusion molding, it is important to have small stress under high shearing during extrusion in order to improve quality of molded article and reduce electric power consumption at molding. On the other hand, Japanese Patent L-O-P Nos. 90810/1981 and 106806/1985 propose a method for improving moldability by improving the melt tension and blow ratio (die/swell ratio) of ethylene polymers obtained by using Ziegler type catalysts, especially a titanium type catalyst The ethylene polymers obtained by using a titanium catalyst, however, especially the low density ethylene polymers generally have problems such as their broad composition distribution and stickiness of their molded articles such as films. Of the ethylene polymers prepared by using the Ziegler type catalysts, those obtained by using chromium type catalysts are relatively excellent in melt tension but has a defect of poor heat stability. This is thought to be caused by that the chain terminals of the ethylene polymers prepared by using the chromium type catalysts tend to become unsaturated bonds. It is known that the ethylene polymers obtained by using a metallocene catalyst from among the Ziegler type catalysts have merits such as a narrow composition distribution and a low stickiness of their molded articles such as films. However, it is described in, for example Japanese Patent L-O-P. No. 35007/1985, that an ethylene polymer obtained by using a zirconocene compound formed from a cyclopentadienyl derivative contains one terminal unsaturated bond per molecule, and hence this ethylene polymer is presumably poor in heat stability similarly to the above-mentioned ethylene polymer obtained by using the chromium type catalyst. Further, because of its narrow composition distribution, this ethylene polymer might show poor flowability during the extrusion molding. Accordingly, the advent of ethylene polymers having a small stress under the high-shear region, a good heat stability, a high mechanical strength and a narrow composition distribution will industrially be of great value. . The present inventors have earnestly studied in the light of the circumstances as described above. As a result, they have found that the ethylene/α-olefin copolymer obtained by copolymerizing ethylene with an α-olefin of 3 to 20 carbon atoms in the presence of a specific catalyst for olefin polymerization has a density, a melt flow rate (MFR), a temperature (Tm) at which its endothermic curve measured by a differential scanning calorimeter (DSC) shows the maximum peak, a flow index (FI) and an amount of a decane-soluble portion in the specific ranges, and the melt tension (MT) at 190 °C and the melt flow rate (MFR) satisfy the relation MT>2.2xMFR -0.84 . The present inventors have also found that such an ethylene/α-olefin olefin copolymer [A-1] as mentioned above is excellent in melt tension and heat stability and has a narrow composition distribution. However, the ethylene/α-olefin copolymer [A-1] is not always well-balanced between the melt tension and the flowability, so that a problem sometimes occurs when the copolymer is subjected to extrusion molding to form a film. The present inventors have further studied and found that the following ethylene copolymer composition is excellent in heat stability, melt tension and flowability under the high-shear region, and films obtained from these compositions are excellent in transparency, mechanical strength and blocking resistance. An ethylene copolymer composition comprising the aforesaid ethylene/α-olefin copolymer [A-1] and a specific low-density polyethylene [B-1] obtained by high-pressure radical polymerization. Thus, the present inventors have accomplished the invention. OBJECT OF THE INVENTION It is an object of the present invention to provide ethylene copolymer compositions which are excellent in heat stability and melt tension and from which films of high transparency, high mechanical strength and high blocking resistance can be obtained. SUMMARY OF THE INVENTION The ethylene copolymer composition according to the present invention is an ethylene copolymer composition comprising: [A-1] an ethylene/α-olefin copolymer of ethylene with an α-olefin of 3 to 20 carbon atoms having such properties that (i) the density (d) is in the range 0.890 to 0.935 g/cm 3 , (ii) the melt flow rate (MFR) at 190 °C under a load of 2.16 kg is in the range of 0.01 to 200 g/10 min, (iii) the temperature (Tm (°C)) at which the endothermic curve of said copolymer measured by a differential scanning calorimeter (DSC) shows the maximum peak and the density (d) satisfy the relation Tm < 400 × d - 250 , (iv) the melt tension (MT (g)) at 190 °C and the melt flow rate (MFR) satisfy the relation MT > 2.2 × MFR - 0.84 , (v) the flow index (Fl (1/sec)) defined by a shear rate which is given when a shear stress of molten copolymer at 190 °C reaches 2.4 x 10 6 dyne/cm 2 and the melt flow rate (MFR) satisfy the relation FI > 100 × MFR , and (vi) the amount (W (% by weight)) of a decane-soluble portion at 23 °C and the density (d) satisfy the relation, in the case of MFR ≤ 10 g/10 min, W < 40 × exp - 100 ⁢ d - 0.88 + 0.1 in the case of MFR > 10 g/10 min, W < 80 × MFR - 9 0.26 × exp - 100 ⁢ d - 0.88 + 0.1 ; and [B-1] a high-pressure radical polymerization low-density polyethylene having such properties that (i) the melt flow rate (MFR) is in the range of 0.1 to 50 g/10 min, and (ii) the molecular weight distribution (Mw/Mn, Mw = weight-average molecular weight, Mn = number-average molecular weight) measured by GPC and the melt flow rate (MFR) satisfy the relation Mw / Mn ≥ 7.5 × log MFR - 1.2 ; a weight ratio ([A-1]:[B-1]) between said ethylene/α-olefin copolymer [A-1] and said high-pressure radical polymerization low-density polyethylene [B-1] being in the range of 99:1 to 60:40, other than Comparative Example 5 of EP 0 598 626 A2. DETAILED DESCRIPTION OF THE INVENTION The ethylene copolymer composition according to the present invention is described in detail hereinafter. In this specification, the term "polymerization" is used to mean not only homopolymerization but also copolymerization, and the term "polymer" is used to mean not only a homopolymer but also a copolymer. [Ethylene copolymer composition] The ethylene copolymer composition according to the present invention is formed from an ethylene/α-olefin copolymer [A-1] and a high-pressure radical polymerization low-density polyethylene [B-1]. [Ethylene/α-olefin copolymer [A-1]] The ethylene/α-olefin copolymer [A-1] used in the invention is a random copolymer of ethylene with an α-olefin of 3 to 20 carbon atoms. Examples of the α-olefin of 3 to 20 carbon atoms employable for copolymerization with ethylene include propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene and 1-eicosene. In the ethylene/α-olefin copolymer [A-1], it is desired that constituent units derived from ethylene are present in an amount of 55 to 99 % by weight, preferably 65 to 98 % by weight, more preferably 70 to 96 % by weight, and constituent units derived from an α-olefin of 3 to 20 carbon atoms are present in an amount of 1 to 45 % by weight, preferably 2 to 35 % by weight, more preferably 4 to 30 % by weight. In the invention, the composition of an ethylene/α-olefin copolymer is determined by 13 C-NMR spectrum analysis of a sample prepared by uniformly dissolving about 200 mg of the copolymer in 1 ml of hexachlorobutadiene in a sample tube usually having a diameter of 10 mm⌀ under the conditions of a measuring temperature of 120 °C, a measuring frequency of 25.05 MHz, a spectrum width of 1,500 Hz, a pulse repetition period of 4.2 sec and a pulse width of 6 µsec. The ethylene/α-olefin copolymer [A-1] used in the invention has the following properties (i) to (vi). (i) The density (d) is usually in the range of 0.890 to 0.935 g/cm 3 , preferably 0.905 to 0.930 g/cm 3 . In the invention, the density (d) of an ethylene/α-olefin copolymer is determined by means of a density gradient tube using a strand, which has been obtained at the time of a melt flow rate (MFR) measurement described below and which is treated by heating at 120 °C for 1 hour and slowly cooling to room temperature over 1 hour. (ii) The melt flow rate (MFR) is usually in the range of 0.01 to 200 g/10 min, preferably 0.05 to 50 g/10 min, more preferably 0.1 to 10 g/10 min. In the invention, the melt flow rate (MFR) of an ethylene/α-olefin copolymer is determined in accordance with ASTM D1238-65T under the conditions of a temperature of 190 °C and a load of 2.16 kg. (iii) The temperature (Tm (°C)) at which the endothermic curve of the copolymer measured by a differential scanning calorimeter (DSC) shows the maximum peak and the density (d) satisfy the relation: Tm < 400 × d - 250 , preferably Tm < 450 × d - 297 , more preferably Tm < 500 × d - 344 , particularly preferably Tm < 550 × d - 391. In the invention, the temperature (Tm (°C)) at which the endothermic curve of an ethylene/α-olefin copolymer measured by a differential scanning calorimeter (DSC) shows the maximum peak is sought from an endothermic curve obtained by filling about 5 mg of a sample in an aluminum pan, heating to 200 °C at a rate of 10 °C/min, holding the sample at 200 °C for 5 minutes, lowering the temperature to room temperature at a rate of 20 °C/min, and then heating at a rate of 10 °C/min. This measurement is carried out using a DSC-7 type apparatus produced by Perkin Elmer Co. (iv) The melt tension (MT (g)) and the melt flow rate (MFR) satisfy the relation: MT > 2.2 × MFR - 0.84 . The ethylene/α-olefin copolymer [A-1] employable for the invention is excellent in melt tension (MT) and has good moldability. In the invention, the melt tension (MT (g)) of an ethylene/α-olefin copolymer is determined by measuring a stress given when a molten copolymer was stretched at a constant rate. That is, a powdery polymer was melted in a conventional manner, and the molten polymer was pelletized to give a measuring sample. Then, the MT of the sample was measured under the conditions of a resin temperature of 190 °C, an extrusion rate of 15 mm/min and a take-up rate of 10 to 20 m/min using a MT measuring apparatus (produced by Toyo Seiki Seisakusho K.K.) having a nozzle diameter of 2.09 mmø and a nozzle length of 8 mm. During the pelletization, to the ethylene/α-olefin copolymer [A-1] were added tri(2,4-di-t-butylphenyl) phosphate as a secondary antioxidant in an amount of 0.05 % by weight, n-octadecyl-3-(4'-hydroxy-3',5'-di-t-butylphenyl)propionate as a heat stabilizer in an amount of 0.1 % by weight and calcium stearate as a hydrochloric acid absorbent in an amount of 0.05 % by weight. (v) The flow index (FI (I/sec)) defined by a shear rate which is given when a shear stress of a molten copolymer at 190 °C reaches 2.4 x 10 6 dyne/cm 2 and the melt flow rate (MFR) satisfy the relation: FI > 100 × MFR , preferably FI > 120 × MFR . The ethylene/α-olefin copolymer [A-1] whose Fl and MFR satisfy the above-mentioned relation shows a small processing torque because a low stress can be kept even at a high-shear rate, and has good moldability. In the invention, the flow index (FI) of an ethylene/α-olefin copolymer is defined by a shear rate which is given when a shear stress reaches 2.4 x 10 6 dyne/cm 2 at 190 °C. The flow index (FI) is determined by extruding a resin from a capillary while changing a shear rate and measuring the shear rate given when the shear stress reaches the above-mentioned value. In this measurement, the same sample as described in the above-mentioned MT measurement is used, and the FI is measured under the conditions of a resin temperature of 190 °C and a shear stress of about 5 x 10 4 to 3 x 10 6 dyne/cm 2 using a capillary type flow property tester produced by Toyo Seiki Seisakusho K K. In the measurement, a diameter of the nozzle (capillary) is changed as follows depending on the MFR (g/10 min) of the resin to be measured: in the case of MFR > 20 : 0.5 mm in the case of 20 ≥ MFR > 3 : 1.0 mm in the case of 3 ≥ MFR > 0.8 : 2.0 mm, and in the case of 0.8 ≥ MFR : 3.0 mm. (vi) The quantity fraction (W (% by weight)) of a n-decane-soluble component at 23 °C and the density (d) satisfy the relation: in the case of MFR ≤ 10 g/10 min, W < 40 × exp - 100 ⁢ d - 0.88 + 0.1 , in the case of MFR > 10 g/10 min, W < 80 × MFR - 9 0.26 × exp - 100 ⁢ d - 0.88 + 0.1. In the invention, the measurement of the n-decane-soluble component quantity of an ethylene/α-olefin copolymer (polymer having a smaller soluble component quantity has a narrower composition distribution) is carried out by adding about 3 g of the copolymer to 450 ml of n-decane, dissolving the copolymer at 145 °C, cooling the resulting solution to 23 °C, removing a n-decane-insolubte portion by filtering, and recovering a n-decane-soluble portion from the filtrate. It may be concluded that the ethylene/α-olefin copolymer [A-1] which satisfies the above mentioned relation between the temperature (Tm) at which the endothermic curve measured by a differential scanning calorimeter (DSC) shows the maximum peak and the density (d), and the relation between the quantity fraction (W) of a n-decane-soluble component and the density (d), has a narrow composition distribution. Further, the number of unsaturated bond present in the molecule of the ethylene/α-olefin copolymer [A-1] desirably is not more than 0.5 per 1,000 carbon atoms and less than 1 per one molecule of the copolymer. In the invention, the number of unsaturated bond of an ethylenela-olefin copolymer is determined by means of 13 C-NMR, that is, an area intensity of signals assigned to bond other than double bond, i.e., signals within the range of 10 to 50 ppm, and an area intensity of signals assigned to double bond, i.e., signals within the range of 105 to 150 ppm, are sought from the integral curve, and the number of the unsaturated bond is determined as a ratio thereof. The ethylene/α-olefin copolymer [A-1] having the properties as mentioned above can be prepared by copolymerizing ethylene with an α-olefin of 3 to 20 carbon atoms in the presence of an olefin polymerization catalyst (1) or a prepolymerization catalyst (1) formed from (a-1) a transition metal compound catalyst component, (b) an organoaluminum oxy-compound catalyst component, (c) a carrier, and if necessary, (d) an organoaluminum compound catalyst component, all components being described later, in such a manner that the resulting copolymer would have a density of 0.880 to 0.960 g/cm 3 . First, the transition metal compound catalyst component (a-1) is explained below. The transition metal compound catalyst component (a-1) (sometimes referred to as "component (a-1)" hereinafter) is a compound of a transition metal in Group IVB of the periodic table which has a bidentate ligand formed by bonding two groups selected from specific indenyl or substituted indenyl groups through a lower alkylene group, or a compound of a transition metal in Group IVB of the periodic table which has as a ligand a cyclopentadienyl group having 2 - 5 substituent groups selected from methyl groups and ethyl groups. Concretely, the component (a-1) is a transition metal compound represented by the following formula [I] or [II] MKL 1 X-2 [I] In the formula [I], M is a transition metal atom selected from Group IVB of the periodic table, K and L 1 are each a ligand coordinating to the transition metal atom. The ligand K is a bidentate ligand formed by bonding the same or different indenyl groups, substituted indenyl groups or their partially hydrogenated products through a lower alkylene group, and the ligand L 1 is a hydrocarbon group of 1 to 12 carbon atoms, an alkoxy group, an aryloxy group, a halogen atom, a trialkylsilyl group or a hydrogen atom. X is a valance of the transition metal atom M. ML 2 X [II] In the formula [II], M is a transition metal atom selected from Group IVB of the periodic table, L 2 is a ligand coordinating to the transition metal atom, at least two of L 2 are substituted cyclopentadienyl groups having 2 - 5 substituent groups selected from methyl group and ethyl group, and L 2 other than the substituted cyclopentadienyl group is a hydrocarbon group of 1 to 12 carbon atoms, an alkoxy group, an aryloxy group, a halogen atom, a trialkylsilyl group or a hydrogen atom. X is a valance of the transition metal atom M. In the above formula [I], M is a transition metal atom selected from Group IVB of the periodic table, and it is concretely zirconium, titanium or hafnium, preferably zirconium. K is a ligand coordinating to the transition metal atom, and is a bidentate ligand formed by bonding the same or different indenyl groups, substituted indenyl groups or partially hydrogenated products of the indenyl or substituted indenyl groups through a lower alkylene group. Concrete examples thereof include ethylenebisindenyl group, ethylenebis(4,5,6,7-tetrahydro-l-indenyl) group, ethylenebis(4-methyl-1-indenyl) group, ethylenebis(5-methyl-1-indenyl) group, ethylenebis (6-methyl-1-irxienyl) group and ethylenebis(7-methyl-1-indenyl) group. L 1 is a hydrocarbon group of 1 to 12 carbon atoms, an alkoxy group, an aryloxy group, a halogen atom, a trialkylsilyl group or a hydrogen atom. Examples of the hydrocarbon group of 1 to 12 carbon atoms include alkyl group, cycloalkyl group, aryl group and aralkyl group. Concrete examples thereof include alkyl group such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, t-butyl group, pentyl group, hexyl group, octyl group, 2-etirylhexyl group and decyl group; cycloalkyl group such as cyclopentyl group and cyclohexyl group; aryl group such as phenyl group and tolyl group; and aralkyl group such as benzyl group and neophyl group. Examples of the alkoxy group include methoxy group, ethoxy group, n-propoxy group, isopropoxy group, n-butoxy group, isobutoxy group, sec-butoxy group, t-butoxy group, pentoxy group, hexoxy group and octoxy group. Examples of the aryloxy group include phenoxy group. Examples of the halogen atom include fluorine, chlorine, bromine and iodine. Examples of the trialkylsilyl group include trimethylsilyl group, triethylsilyl group and triphenylsilyl group. Listed below are examples of the transition metal compound represented by the formula [I]. Ethylenebis(indenyl)zirconium dichloride, Ethylenebis(4-methyl-1-indenyl)zirconium dichloride, Ethylenebis(4,5,6,7-tetrahydro-1-indenyl)zirconium dichloride, Ethylenebis(5-methyl-1-indenyl)zirconium dichloride, Ethylenebis(6-methyl-1-indenyl)zirconium dichloride, Ethylenebis(7-methyl-1-indenyl)zirconium dichloride, Ethylenebis(4-methyl-1-indenyl)zirconium dibromide, Ethylenebis(4-methyl-1-indenyl)zirconium methoxychloride, Ethylenebis(4-methyl-1-indenyl)zirconium ethoxychloride, Ethylenebis(4-methyl-1-indenyl)zirconium butoxychloride, Ethylenebis(4-methyl-1-indenyl)zirconium dimethoxide, Ethylenebis(4-methyl-1-indenyl)zirconium methylchloride Ethylenebis(4-methyl-1-indenyl)dimethylzirconium, Ethylenebis(4-methyl-1-indenyl)zirconium benzylchloride, Ethylenebis(4-methyl-1-indenyl)dibenzylzirconium, Ethylenebis(4-methyl-1-indenyl)zirconium phenylchloride, and Ethylenebis(4-methyl-1-indenyl)zirconium hydride chloride. Also employable in the invention are transition metal compounds obtained by substituting titanium metal or hafnium metal for the zirconium metal in the above-exemplified zirconium compounds. Of the above-exemplified transition metal compounds represented by the formula [I], particularly preferred are ethylenebis(indenyl)zirconium dichloride, ethylenebis(4-methyl-1-indenyl)zirconium dichloride and ethylenebis(4,5,6,7-tetrahydro-1-indenyl)zirconium dichloride. In the above-mentioned formula [II], M is a transition metal selected from Group IVB of the periodic table, and concrete preferable examples of M include zirconium, titanium and hafnium. Of these, particularly preferred is zirconium. L 2 is a ligand coordinated to the transition metal, and at least two of them are substituted cyclopentadienyl groups having 2 - 5 of substituents selected from methyl group and ethyl group. Each of ligand may be the same or different The substituted cyclopentadienyl groups are the substituted cyclopentadienyl groups having 2 or more of substituents, preferably the substituted cyclopentadienyl groups having 2 or 3 of substituents, more preferably the substituted cyclopentadienyl groups having two substituents, particularly the 1,3-substituted cyclopentadienyl groups. Each of substituent may be the same or different. In the above-mentioned formula [II], ligand L 2 other than the substituted cyclopentadienyl group is a hydrocarbon group of 1 to 12 carbon atoms, an alkoxy group, an aryloxy group, halogen, trialkylsilyl group or hydrogen as similar to the ligand L 1 in the above-mentioned formula [I]. The transition metal compound represented by the general formula [II] include, for example, Bis(dimethylcyclopentadienyl)zirconium dichloride, Bis(diethylcyclopentadienyl)zirconium dichloride, Bis(methylethylcyclopentadienyl)zirconium dichloride, Bis(dimethylethylcyclopentatienyl)zirconium dichloride, Bis(dimethylcyclopentadienyl)zirconium dibromide. Bis(dimethylcyclopentadienyl)zirconium methoxychloride, Bis(dimethylcyclopentadienyl)zirconium ethoxychloride, Bis(dimethylcyclopentadienyl)zirconium butoxychloride, Bis(dimethylcyclopentadienyl)zirconium diethoxide, Bis(dimethylcyclopentadienyl)zirconium methylchloride, Bis(dimethylcyclopentadienyl)zirconium dimethyl, Bis(dimethylcyclopentadienyl)zirconium benzylchloride, Bis(dimethylcyclopentadienyl)zirconium dibenzyl, Bis(dimethylcyclopentadienyl)zirconium phenylchloride, and Bis(dimethylcyclopentadienyl)zirconium hydridechloride. In the above exemplified compounds, di-substituted cyclopentadienyl include 1,2- and 1,3-substituted, and tri-substituted include 1,2,3- and 1,2,4-substituted. There may also be used transition metal compounds obtained by substituting titanium or hafnium for zirconium in the above-exemplified zirconium compounds. In the above-mentioned transition metal compounds represented by the general formula [II], particularly preferred is Bis(1,3-dimethylcyclopentadienyl)zirconium dichloride, Bis(1,3-diethylcyclopentadienyl)zirconium dichloride, or Bis(1-methyl-3-ethylcyclopentadienyl)zirconium dichloride. Next, the organoaluminum oxy-compound (b) [hereinafter sometimes referred to as component (b)] is explained below. The organoaluminum oxy-compound (b) may be a known benzene-soluble aluminoxane or the benzene-insoluble organoaluminum oxy-compound having been disclosed in Japanese Patent L-O-P No. 276807/1990. The above-mentioned aluminoxane may be prepared, for example, by the following procedures: (1) a procedure for recovering an aluminoxane as its hydrocarbon solution which comprises adding an organoaluminum compound such as trialkylaluminum to a suspension in a hydrocarbon medium of a compound containing adsorbed water, or a saft containing water of crystallization such as magnesium chloride hydrate, copper sulfate hydrate, aluminum sulfate hydrate, nickel sulfate hydrate and cerium chloride hydrate, and reacting the organoaluminum compound: and (2) a procedure for recovering an aluminoxane as its hydrocarbon solution which comprises reacting water, ice or steam directly with an organoaluminum compound such as trialkylaluminum in a solvent such as benzene, toluene, ethyl ether and tetrahydrofuran. (3) a procedure for recovering an aluminoxane which comprises reacting an organotinoxide such as dimethyltinoxide and dibutyltinoxide with an organoaluminum compound such as trialkylaluminum in a solvent such as decane, benzene or toluene. Moreover, the aluminoxane may contain a small amount of an organometal component. Furthermore, the solvent or unreacted organoaluminum compound may be removed from the above-mentioned recovered aluminoxane-containing solution, by distillation, and the aluminoxane may be redissolved in a solvent. Concrete examples of the organoaluminum compound used for the preparation of the aluminoxane include trialkylaluminum such as trimethylaluminum, triethylaluminum, tripropylaluminum, triisopropylaluminum, tri-n-butylaluminum, triisobutylaluminum, tri-sec-butylaluminum, tri-tert-butylaluminum, tripentylaluminum, trihexylaluminum, trioctylaluminum and tridecylaluminum; tricycloalkylaluminums such as tricyclohexylaluminum and tricyclooctylaluminum; dialkylaluminum halides such as dimethylaluminum chloride, diethylaluminum chloride, diethylaluminum bromide and diisobutylalumunum chloride; dialkylaluminum hydrides such as diethylaluminum hydride and diisobutylaluminum hydride; dialkylaluminum alkoxides such as dimethylaluminum methoxide and diethylaluminum ethoxide; and dialkylaluminum aryloxides such as diethylaluminum phenoxide. Of these compounds, trialkylaluminum is particularly preferable. Furthermore, there may also be used as the organoaluminum compound isoprenylaluminum represented by the general formula (i-C 4 H 9 ) x Al y (C 5 H 10 ) z wherein x, y and z are each a positive number, and z ≥ 2x. The organoaluminum compounds mentioned above may be used either singly or in combination. Solvents used for the solutions of the aluminoxane include aromatic hydrocarbons such as benzene, toluene, xylene, cumene and cymene; aliphatic hydrocarbons such as pentane, hexane, heptane, octane, decane, dodecane, hexadecane and octadecane; alicyclic hydrocarbons such as cyclopentane, cyclohexane, cyclooctane and methylcyclopentane; petroleum fractions such as gasoline, kerosene and gas oil; and halogenated compounds derived from the above-mentioned aromatic hydrocarbons, aliphatic hydrocarbons and alicyclic hydrocarbons, especially chlorinated and brominated hydrocarbons. In addition, there may also be used ethers such as ethyl ether and tetrahydrofuran. Of these solvents as exemplified above, aromatic hydrocarbons are particularly preferred. The benzene-insoluble organoaluminum oxy-compounds used as component (b) contain an Al component soluble in benzene at 60°C in an amount of not greater than 10%, preferably not greater than 5%, particularly preferably not greater than 2% in terms of Al atom, and they are insoluble or sparingly soluble in benzene. Solubility in benzene of such organoaluminum oxy-compounds as mentioned above is obtained by suspending in 100 ml of benzene the organoaluminum oxy-compound in an amount corresponding to 100 mg atoms in terms of Al, mixing the resulting suspension at 60°C for 6 hours with stirring, filtering the resulting mixture with a G-5 glass filter equipped with a jacket kept at 60°C, washing 4 times the solid portion separated on the filter with 50 ml of benzene at 60°C, and measuring the amount (x mmole) of Al atoms present in the whole filtrate. Next, the carrier (c) is explained below. The carrier (c) [hereinafter sometimes referred to as component (c)] is a solid inorganic or organic compound in granules or fine particles having a particle size of 10 to 300 µm, preferably 20 to 200 µm. Of these carriers, porous oxides are preferable as inorganic carriers. Concrete examples of the oxide carriers include SiO 2 , Al 2 O 3 , MgO, ZrO 2 , TiO 2 , B 2 O 3 , CaO, ZnO, BaO, ThO 2 , or a mixture of these compounds such as SiO 2 -MgO, SiO 2 -Al 2 O 3 , SiO 2 -TiO 2 , SiO 2 -V 2 O 5 , SiO 2 -Cr 2 O 3 and SiO 2 -TiO 2 -MgO. Of these carriers, preferred are those comprising at least one compound selected from the group consisting of SiO 2 and Al 2 O 3 as a major component Furthermore, the above-mentioned inorganic oxide or oxides may also contain a small amount of a carbonate, a sulfate, a nitrate and an oxide such as Na 2 CO 3 , K 2 CO 3 , CaGO 3 , MgCO 3 , Na 2 SO 4 , Al 2 (SO 4 ) 3 , BaSO 4 , KNO 3 , Mg(NO 3 ) 2 , Al(NO 3 ) 3 , Na 2 O, K 2 O and LiO 2 . Though the porous inorganic carriers have different properties among them depending on the types and preparation methods thereof, the carriers preferably used in the invention have a specific surface area of 50 to 1000 m 2 /g, preferably 100 to 700 m 2 /g, a pore volume of desirably 0.3 to 2.5 cm 2 /g. The carriers are prepared if necessary by firing at a temperature of 100 to 1000°C, preferably 150 to 700°C. Moreover, there can be mentioned organic compounds in solid granules or fine solid particles each having a particle size of 10 to 300 µm as carriers which can be used as the component (c). Examples of these organic compounds include (co)polymers containing as the main component constituent units derived from an α-olefin of 2 to 14 carbon atoms, such as ethylene, propylene, 1-butene and 4-methyl-1-pentene, or polymers or copolymers containing as the main component constituent units derived from vinylcyclohexane or styrene. Next, the optionally used organoaluminum compound catalyst component (d) is explained below. Examples of the organoaluminum compound (d) [hereinafter sometimes referred to as component (d)] include an organoaluminum compound represented by the following formula [III]. R 1 n AlX 3-n [III] wherein R 1 is a hydrocarbon group of 1 to 12 carbon atoms, X is halogen or hydrogen, and n is 1 to 3. In the above formula [III], R 1 is a hydrocarbon group of 1 to 12 carbon atoms, for example, an alkyl group, a cycloalkyl group or an aryl group. Concrete examples of R 1 include methyl, ethyl, n-propyl, isopropyl, isobutyl, pentyl, hexyl, octyl, cyclopentyl, cyclohexyl, phenyl and tolyl. Concrete examples of such organoaluminum compounds (d) include trialkylaluminum such as trimethylaluminum, triethylaluminum, triisopropylaluminum, triisobutylaluminum, trioctylaluminum and tri-2-ethylhexylaluminum; alkenylaluminum such as isoprenylaluminum; dialkylaluminum halides such as dimethylaluminum chloride, diethylaluminum chloride, diisopropylaluminum chloride, diisobutylaluminum chloride and dimethylaluminum bromide; alkylaluminum sesquihalides such as methylaluminum sesquichloride, ethylaluminum sesquichloride, isopropylaluminum sesquichloride, butylaluminum sesquichloride and ethylaluminum sesquibromide; alkylaluminum dihalides such as methylaluminum dichloride, ethylaluminum dichloride, isopropylaluminum dichloride and ethylaluminum dibromide; and alkylaluminum hydrides such as diethylaluminum hydride and diisobutylaluminum hydride. Furthermore, there may also be used other organoaluminum compounds represented by the following formula [IV] as the organoaluminum compound catalyst component (d); R 1 n AlY 3-n [IV] wherein R 1 is as defined previously, Y is -OR 2 , -OSiR 3 3 , -OAIR 4 2 , -NR 5 2 , -SiR 6 3 or -N(R 7 )AlR 8 2 , n is 1 to 2, R 2 , R 3 , R 4 and R 8 are each methyl, ethyl, isopropyl, isobutyl, cyclohexyl or phenyl, R 5 is hydrogen, methyl, ethyl, isopropyl, phenyl or trimethylsilyl, R 6 and R 7 are each methyl or ethyl. The organoaluminum compounds as mentioned above include, in concrete, such compounds as enumerated below. (1) Compounds of the formula R 1 n Al(OR 2 ) 3-n such as dimethylaluminum methoxide, diethylaluminum ethoxide and diisobutylaluminum methoxide. (2) Compounds of the formula R 1 n Al(OSiR 3 3 ) 3-n such as Et 2 Al(OSiMe 3 ), (iSO-Bu) 2 Al(OSiMe 3 ) and (iso-Bu) 2 Al(OSiEt 3 ). (3) Compounds of the formula R 1 n Al(OAlR 4 2 ) 3-n such as Et 2 AlOAlEt 2 and (iso-Bu) 2 AlOAl (iso-Bu) 2 . (4) Compounds of the formula R 1 n Al(NR 5 2 ) 3-n such as Me 2 AlNEt 2 , Et 2 AlNHMe, Me 2 AlNHEt, Et 2 AlN(SiMe 3 ) 2 , (iso-Bu) 2 AlN(SiMe 3 ) 2 . (5) Compounds of the formula R 1 n Al(SiR 6 3 ) 3-n such as (iso-Bu) 2 AlSiMe 3 . (6) Compounds of the formula such as Of the organoaluminum compounds as exemplified above, preferred are those having the formulas R 1 3 Al, R 1 n Al(OR 2 ) 3-n and R 1 n Al(OAIR 4 2 ) 3-n , and particularly preferred are those having the above-mentioned formulas in which R 1 is isoalkyl and n is 2. The ethylene/α-olefin copolymer [A-1] used in the present invention can be prepared by the olefin polymerization catalyst (1) formed by contacting the above-mentioned components (a-1), (b), (c) and if necessary, component (d). Though the mixing of these components (a-1), (b), (c) and (d) may be conducted in arbitrarily selected order, the mixing and contacting is preferably conducted in the order of: mixing and contacting the components (b) and (c), followed by mixing and contacting the component (a-1), and if necessary, mixing and contacting the component (d). The mixing of the above-mentioned components (a-1), (b), (c) and (d) can be carried out in an inert hydrocarbon. As the inert hydrocarbon solvent for preparing the catalyst, there may be mentioned an aliphatic hydrocarbon, such as propane, butane, pentane, hexane, heptane, octane, decane, dodecane and kerosene; an alicyclic hydrocarbon, such as cyclopentane, cyclohexane and methylcyclopentane; an aromatic hydrocarbon, such as benzene, toluene and xylene; a halogenated hydrocarbon, such as ethylene chloride, chlorobenzene and dichloromethane; and a mixture thereof. In contacting and mixing of the components (a-1), (b), (c) and if necessary, component (d), the component (a-1) is used usually in an amount of 5 x 10 -6 to 5 x 10 - 4 mol, preferably 1 x 10 -5 to 2 x 10 -4 mol based on 1 g of the component (c), and the concentration thereof is 1 x 10 -4 to 2 x 10 -2 mol/l, preferably 2 x 10 -4 to 1 x 10 -2 mol/l. The atomic ratio (Al/transition metal) of the aluminum in the component (b) to the transition metal in the component (a-1) is usually 10 to 500, preferably 20 to 200. The atomic ratio (Al-d/Al-b) of the aluminum atoms (Al-d) in the component (d) optionally used to the aluminum atoms (Al-b) in the component (b) is usually 0.02 to 3, preferably 0.05 to 1.5. The components (a-1), (b) and (c), and if necessary, the component (d) are mixed and contacted at a temperature of usually -50 to 150° C, preferably -20 to 120° C, with a contact time of 1 minute to -50 hours, preferably 10 minutes to 25 hours. In the catalyst (1) for olefin polymerization obtained as described above, it is desirable that the transition metal derived from component (a-1) is supported in an amount of 5 x 10 -6 to 5 x 10 -4 g atom, preferably 1 x 10 -5 to 2 x 10 -4 g atom, and aluminum derived from components (b) and (d) is supported in an amount of 10 -3 to 5 x 10 -2 g atom, preferably 2 x 10 -3 to 2 x 10 -2 g atom, all the amounts being based on 1 g of the component (c). Further, the catalyst for preparing the ethylene/α-olefin copolymer [A-1] used in the present invention may be a prepolymerized catalyst (1) obtained by prepolymerization of olefin in the presence of the above-mentioned components (a-1), (b) and (c), and if necessary, (d). The prepolymerized catalyst (1) can be prepared by mixing the component (a-1), the component (b), the component (c), and if necessary, the component (d), introducing olefin to the resulting mixture in the inert hydrocarbon solvent, and carrying out prepolymerization. The olefins which can be prepolymerized include ethylene and α-olefins each having 3 to 20 carbon atoms, for example, propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-octene, 1-decene, 1-dodecene and 1-tetradecene. Of these, particularly preferred is ethylene or the combination of ethylene and α-olefin used in the polymerization. During the prepolymerization, the component (a-1) is used usually in a concentration of is 1 x 10- 6 to 2 x 10 -2 mol/l, preferably 5 x 10 -5 to 1 x 10 -2 mol/l and amount thereof is usually 5 x 10 -6 to 5 x 10 -4 mol, preferably 1 x 10 -5 to 2 x 10 -4 mol based on 1 g of the component (c). The atomic ratio (Al/transition metal) of the aluminum in the component (b) to the transition metal in the component (a-1) is usually 10 to 500, preferably 20 to 200. The atomic ratio (Al-d/Al-b) of the aluminum atoms (Al-d) in the component (d) optionally used to the aluminum atoms (Al-b) in the component (b) is usually 0.02 to 3, preferably 0.05 to 1.5. The prepolymerization is carried out at a temperature of -20 to 80°C, preferably 0 to 60°C, with a time of 0.5 to 100 hours, preferably 1 to 50 hours. The prepolymerized catalyst (1) can be prepared as described below. First, the carrier (component (c)) is suspended in the inert hydrocarbon. To the suspension, the organoaluminum oxy-compound catalyst component (component (b)) is introduced, and reacted for predetermined period. Successively, supernatant is removed, and the resulting solid component is re-suspended in the inert hydrocarbon. Into the system, the transition metal compound catalyst component (component (a-1)) is added and reacted for predetermined period. Then, supernatant is removed to obtain a solid catalyst component. Continuously, the solid catalyst component obtained above is added into inert hydrocarbon containing the organoaluminum compound catalyst component (component (d)), and olefin is introduced therein to obtain the prepolymerized catalyst (1). An amount of prepolymerized polyolefin produced in the prepolymerization is, desirably based on 1 g of the carrier (c), of 0.1 to 500g, preferably 0.2 to 300g, more preferably 0.5 to 200 g. In the prepolymerized catalyst (1), component (a-1) is desirably supported in an amount in terms of transition metal atom, based on 1 g of the carrier (c), of about 5 x 10 -6 to 5 x 10 -4 g atom, preferably 1 x 10- 5 to 2 x 10 -4 g atom. Further, a molecular ratio (AI/M) of aluminum atom (Al) derived from components (b) and (d) to transition metal atom (M) derived from component (a-1) is usually 5 to 200, preferably 10 to 150. The prepolymerization may be carried out either batchwise or continuously, and under reduced pressure, normal pressure or applied pressure. During the prepolymerization, hydrogen may be allowed to be present to obtain a prepolymer desirably having an intrinsic viscosity [η] of 0.2 to 7 dUg, preferably 0.5 to 5 dl/g as measured in decalin at least 135°C. The ethylene/α-olefin copolymers [A-1] used in the present invention are obtained by copolymerizing ethylene with an α-olefin having 3 to 20 carbon atoms such as propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1 -hexadecene, 1-octadecene and 1-eicosene in the presence of the olefin polymerization catalyst (1) or the prepolymerized catalyst (1). Copolymerization of ethylene and α-olefin is carried out in a gas phase or liquid phase, for example, in slurry. In the slurry polymerization, an inactive hydrocarbon or the olefin itself may be used as a solvent. Concrete examples of the inactive hydrocarbon solvent include aliphatic hydrocarbons such as butane, isobutane, pentane, hexane, octane, decane, dodecane, hexadecane and octadecane; alicyclic hydrocarbons such as cyclopentane, methylcyclopentane, cyclohexane and cyclooctane; aromatic hydrocarbons such as benzene, toluene and xylene; and petroleum fractions such as gasoline, kerosene and gas oil. Of these inactive hydrocarbons, preferred are aliphatic hydrocarbons, alicyclic hydrocarbons and petroleum fractions. When the copolymerization is carried out by the slurry method or the gas phase method, the olefin polymerization catalyst (1) or the prepolymerized catalyst (1) is used at such amount that the concentration of the transition metal compound becomes usually 10 -8 to 10 -3 g atom/liter, preferably 10 -7 to 10 -4 g atom/liter in terms of the transition metal in the polymerization reaction system. Furthermore, in the polymerization, an organoaluminum oxy-compound similar to the catalyst component (b) and/or an organoaluminum compound (d) may be added. In this case, the atomic ratio (Al/M) of the aluminum atom (Al) derived from the organoaluminum oxy-compound and the organoaluminum compound to the transition metal atom (M) derived from the transition metal compound catalyst component (a-1) is 5 to 300, preferably 10 to 200, more preferably 15 to 150. When the ethylene/α-olefin copolymer [A-1] is prepared by the slurry polymerization, the polymerization temperature is usually -50 to 100°C, preferably 0 to 90°C. When the ethylene/α-olefin copolymer [A-1] is prepared by the gas phase polymerization, the polymerization temperature is usually 0 to 120°C, preferably 20 to 100°C. The polymerization is carried out usually at a normal pressure to 100 kg/cm 2 , preferably under a pressure condition of 2 to 50 kg/cm 2 . The polymerization can be carried out either batchwise, semicontinuously or continuously. Furthermore, the polymerization may also be carried out in not less than 2 steps having reaction conditions different from each other. [High-pressure radical polymerization low-density polyethylene [B-1]] 11 The high-pressure radical polymerization low-density polyethylene [B-1] used in the invention is a branched polyethylene having a number of long chain branches prepared by so-called high-pressure radical polymerization, and has a melt flow rate (MFR), as determined in accordance with ASTM D1238-65T under the conditions of a temperature of 190 °C and a load of 2.16 kg, of 0.1 to 50 g/10 min, preferably 0.2 to 10 g/10 min, more preferably 0.2 to 8 g/10 min. In the high-pressure radical polymerization low-density polyethylene [B-1] used in the invention, the index of the molecular weight distribution (Mw/Mn, Mw = weight-average molecular weight, Mn = number-average molecular weight) measured by means of gel permeation chromatography (GPC) and the melt flow rate (MFR) satisfy the rotation: Mw / Mn ≥ 7.5 × log MFR - 1.2 , preferably Mw / Mn ≥ 7.5 × log MFR - 0.5 , more preferably Mw / Mn ≥ 7.5 × log MFR . In the invention, the molecular weight distribution (Mw/Mn) of a high-pressure radical polymerization low-density polyethylene is determined as follows using GPC-150C produced by Milipore Co. That is, in a column of TSK-GNH-HT having a diameter of 72 mm and a length of 600 mm, a sample (concentration: 0.1 % by weight, amount: 500 microliters) is moved under the conditions of a moving rate of 1.0 ml/min and a column temperature of 140 °C using o-dichlorobenzene (available from Wako Junyaku Kogyo K.K) as a mobile phase and 0.025 % by weight of BHT (available from Takeda Chemical Industries, Ltd.) as an antioxidant As a detector, a differential refractometer is used. The standard polystyrenes of Mw<1,000 and Mw>4x10 6 are available from Toso Co., Ltd., and those of 1,000<Mw<4x10 6 are available from Pressure Chemical Co. The high-pressure radical polymerization low-density polyethylene [B-1] used in the invention desirably has a density (d) of 0.910 to 0.930 g/cm 3 . In the invention, the density of a low-density polyethylene is determined by means of a density gradient tube using a strand which has been obtained in the above-mentioned melt flow rate (MFR) measurement and which is treated by heating at 120°C for 1 hour and slowly cooling to room temperature over 1 hour. Further, in the high-pressure radical polymerization low-density polyethylene [B-1] used in the invention, a swell ratio indicating a degree of the long chain branch, namely, a ratio (Ds/D) of a diameter (Ds) of a strand to an inner diameter (D) of a nozzle, is desirably not less than 1.3. The strand used herein is a strand extruded from a nozzle having an inner diameter (D) of 2.0 mm and a length of 15 mm at an extrusion rate of 10 mm/min and a temperature of 190 °C using a capillary type flow property tester. The high-pressure radical polymerization low-density polyethylene [B-1] as mentioned above may be a copolymer obtained by copolymerizing ethylene with a polymerizable monomer such as other α-olefin, vinyl acetate or acrylic ester, provided that the object of the invention is not marred. [Ethylene copolymer composition] The ethylene copolymer composition according to the invention comprises the aforementioned ethylene/α-olefin copolymer [A-1] and the high-pressure radical polymerization low-density polyethylene [B-1], and a weight ratio ([A-1]: [B-1]) between the ethylene/α-olefin copolymer [A-1] and the high-pressure radical polymerization low-density polyethylene [B-1] is in the range of 99:1 to 60:40, preferably 98:2 to 70:30, more preferably 98:2 to 80:20. When the amount of the high-pressure radical polymerization low-density polyethylene [B-1] is less than the lower limit of the above range, the resulting composition is sometimes improved insufficiently in the transparency and the melt tension, and when the amount thereof is larger than the upper limit of the above range, the resulting composition is sometimes markedly deteriorated in the tensile strength and the stress crack resistance. The first ethylene copolymer composition according to the invention may contain various additives if desired, for example, weathering stabilizer, heat stabilizer, antistatic agent, anti-slip agent, anti-blocking agent, antifogging agent, lubricant, pigment, dye, nucleating agent, plasticizer, anti-aging agent hydrochloric acid absorbent and antioxidant, provided that the object of the invention is not marred. The first ethylene copolymer composition according to the invention can be prepared by known processes, for example, processes described below. (1) A process of mechanically blending the ethylene/α-olefin copolymer [A-1], the high-pressure radical polymerization low-density polyethylene [B-1], and if necessary, other optional components by the use of an extruder or a kneader. (2) A process comprising dissolving the ethylene/α-olefin copolymer [A-1], the high-pressure radical polymerization low-density polyethylene [B-1], and if necessary, other optional components in an appropriate good solvent (e.g., hydrocarbon solvent such as hexane, heptane, decane, cyclohexane, benzene, toluene and xylene), and then removing the solvent from the resulting solution. (3) A process comprising independently dissolving the ethylene/α-olefin copolymer [A-1], the high-pressure radical polymerization low-density polyethylene [B-1], and if necessary, other optional components in an appropriate good solvent to prepare solutions, then mixing the solutions, and removing the solvent from the resulting mixture. (4) A process of combining the above processes (1) to (3). The ethylene copolymer composition according to the present invention is subjected to ordinary air-cooling inflation molding, two-stage air-cooling inflation molding, high-speed inflation molding, T-die film molding or water-cooling inflation molding, to obtain a film. The film thus obtained is excellent in transparency and mechanical strength, and has properties inherently belonging to general LLDPE, such as heat-sealing properties, hot-tack properties, heat resistance and blocking resistance. Further, the film is free from surface stickiness because the ethylene/α-olefin copolymer [A-1] has a prominently narrow composition distribution. Moreover, because of low stress within the high-shear region, the ethylene copolymer composition can be extruded at a high speed, and consumption of electric power is small, resulting in economical advantage. Films obtained by processing the ethylene copolymer composition of the invention are suitable for, for example, standard bags, heavy bags, wrapping films, materials for laminates, sugar bags, packaging bags for oily goods, packaging bags for moist goods, various packaging films such as those for foods, bags for liquid transportation and agricultural materials. The films may also be used as multi-layer films by laminating the films on various substrates such as a nylon substrate and a polyester substrate. Further, the films may be used for liquid transportation bags obtained by blow molding, bottles obtained by blow molding, tubes and pipes obtained by extrusion molding, pull-off caps, injection molded products such as daily use miscellaneous goods, fibers, and large-sized molded articles obtained by rotational molding. EFFECT OF THE INVENTION The ethylene copolymer composition of the present invention is excellent in heat stability and melt tension, and from this ethylene copolymer composition, a film showing high transparency, high mechanical strength and high blocking resistance can be obtained. [Example] The present invention is further described below with reference to examples, but it should be construed that the present invention is in no way limited to those examples. In this specification, physical properties of films were evaluated in the following manner. Haze The haze was measured in accordance with ASTM-D-1003-61. Gloss The gloss was measured in accordance with JIS Z8741. Film impact The film impact was measured by a pendulum type film impact tester produced by Toyo Seiki Seisakusho K.K. Blocking force Inflation films each having a size of 10 cm (width) x 20 cm were sandwiched between two sheets of typing paper, then further sandwiched between glass plates, and a load of 10 kg was applied to them in an air bath of 50 °C for 24 hours. Then, the films were fitted to an open tool to separate the films at a rate of 200 mm/min. A load at the time when the films are separated is A (g), the blocking force F (g/cm) is determined by the following formula. F = A / width of sample As the F value becomes smaller, blocking of the films come to hardly take place, that is, the film has a higher blocking resistance. Tensile test A specimen was punched using a dumbbell (JIS No. 1) from the film in the machine direction (MD) or the transverse direction (TD) of the film molding direction, and a modulus in tension (YM) and an elongation at break (EL) of the specimen were measured under the conditions of a distance between chucks of 86 mm and a crosshead speed of 200 mm/min. Preparation Example 1 Preparation of an ethylene/α-olefin copolymer [Preparation of a solid catalyst] 7.9 kg of silica having been dried at 250 °C for 10 hours was suspended in 121 liters of toluene, and the resultant suspension was cooled to 0 °C. Thereafter, to the suspension was dropwise added 41 liters of a toluene solution of methylaluminoxane (Al =1.47 mol/l) over 1 hour. During the addition, the temperature of the system was kept at 0°C. Successively, the reaction was carried out at 0 °C for 30 minutes. Then, the temperature of the system was elevated to 95 °C over 1.5 hours, and the reaction was carried out at the same temperature for 4 hours. Thereafter, the temperature of the system was lowered to 60 °C, and the supernatant liquid was removed by decantation. The solid component obtained above was washed twice with toluene, and then again suspended in 125 liters of toluene. To the reaction system was dropwise added 20 liters of a toluene solution of bis(1,3-dimethylcyclopentadienyl)zirconium dichloride (Zr = 28.4 mmol/l) at 30°C over 30 minutes, and the reaction was further carried out at 30 °C for 2 hours. Then, the supernatant liquid was removed, and the residue was washed twice with hexane to obtain a solid catalyst containing 4.6 mg of zirconium based on 1 g of the solid catalyst [Preparation of a prepolymerized catalyst] To 160 liters of hexane containing 16 mol of triisobutylaluminum was added 4.3 kg of the solid catalyst obtained in the above, and the resultant mixture was subjected to prepolymerization with ethylene at 35 °C for 3.5 hours to obtain a prepolymerized catalyst in which polyethylene was present in an amount of 3 g based on 1 g of the solid catalyst This ethylene polymer had an intrinsic viscosity [η] of 1.27 dUg. [Polymerization] In a continuous fluidized bed gas phase reactor, ethylene was copolymerized with 1-hexene at a total pressure of 20 kg/cm 2 -G and a polymerization temperature of 80 °C. To the reactor were continuously fed the prepolymerzied catalyst prepared in the above at a feed rate of 0.048 mmol/hour in terms of zirconium atom and triisobutylaluminum at a feed rate of 10 mmol/hour while continuously feeding ethylene, 1-hexene, hydrogen and nitrogen to maintain a constant gas composition in the reactor (gas composition: 1-hexene/ethylene = 0.030, hydrogen/ethylene = 0.0013, ethylene concentration = 25%). Thus, an ethylene/α-olefin copolymer (A-1-1) was obtained in an amount of 5.3 kg/hour The copolymer had a density of 0.920 g/cm 3 and a melt flow rate (MFR) of 2.0 g/10 min. The temperature at the maximum peak of the DSC endothermic curve (Tm) of the copolymer was 112.2 °C. Further, the copolymer had a melt tension (MT) of 1.8 g at 190 °C and a flow index (FI) of 290 (I/sec). The amount of the decane-soluble portion in the copolymer was 0.47 % by weight at 23 °C. The number of unsaturated bond in the copolymer was 0.091 per 1,000 carbon atoms, and was 0.08 per one molecule of the polymer. Physical properties of the ethytene/α-olefin copolymer (A-1-1) are set forth in Table 1. Example 1 [Preparation of a composition] The ethylene/α-olefin copolymer (A-1-1) obtained in Preparation Example 1 and a high-pressure radical polymerization low-density polyethylene (B-1-1) shown in Table 2 were dry blended in a mixing ratio of 90/10 [(A-1-1)/(B-1-1)]. To the resultant blend were added 0.05 part by weight of tri(2,4-di-t-butylphenyl)phosphate as a secondary antioxidant, 0.1 part by weight of n-octadecyl-3-(4'-hydroxy-3',5'-di-t-butylphenyl)propionate as a heat-resistant stabilizer and 0.05 part by weight of calcium stearate as a hydrochloric acid absorbent, each based on 100 parts by weight of the resin. Then, the resultant mixture was kneaded by a conical-tapered twin-screw extruder (produced by Haake Buchler Instrument Inc.) at a preset temperature of 180 °C, to obtain an ethylene copolymer composition. [Film formation] The ethylene copolymer composition obtained as above was subjected to inflation by the use of a single-screw extruder (20 mmφ • L/D = 26) equipped with a die of 25 mmφ (lip width: 0.7 mm) and a single-slit air ring under the conditions of an air flow rate of 90 l/min, an extrusion rate of 9 g/min, a blow ratio of 1.8, a take-up rate of 2.4 m/min and a processing temperature of 200 °C, to form a film having a thickness of 30 µm. Melt properties of the ethylene copolymer composition and physical properties of the film formed from the composition are set forth in Table 3. As is evident from Table 3, the film obtained from the composition was excellent in optical characteristics, moldability, blocking resistance and strength. Reference Example 1 The procedure of film formation in Example 1 was repeated except for using the ethylene/α-olefin copolymer (A-1-1) obtained in Preparation Example 1, to form a film having a thickness of 30 µm. Melt properties of the ethylene/α-olefin copolymer and physical properties of the film formed from the copolymer are set forth in Table 3. As is evident from Example 1 and Reference Example 1, the ethylene/α-olefin copolymer was improved in moldability and optical characteristics by blending it with a high-pressure radical polymerization low-density polyethylene. Further, the ethylene copolymer composition was hardly reduced in the film impact as compared with the ethylene/α-olefin copolymer (A-1-1), in spite that the composition contained a high-pressure radical polymerization low-density polyethylene having a low film impact Comparative Example 1 [Preparation of an ettrylene/α-olefin copolymer (C-1)] The procedure of copolymerization of ethylene with 1-hexene in Preparation Example 1 was repeated except for replacing the zirconium catalyst system with a titanium type catalyst system described in Japanese Patent Publication No. 63(1988)-54289, to obtain an ethylene/α-olefin copolymer (C-1). Physical properties of the ethylene/α-olefin copolymer (C-1) are set forth in Table 1. [Preparation of an ethylene copolymer composition] The ethylene/α-olefin copolymer (C-1) obtained in the above and a high-pressure radical polymerization low-density polyethylene (B-1-1) shown in Table 2 were used to prepare an ethylene copolymer composition in a manner similar to that of Example 1. [Film formation] From the ethylene copolymer composition obtained in the above, a film having a thickness of 30 µm was formed in a manner similar to that of Example 1. Melt properties of the ethylene copolymer composition and physical properties of the film formed from the composition are set forth in Table 3. The film obtained above had a wide composition distribution and a large amount of sticky component, and hence the film was particularly low in the blocking resistance. Further, as is clear from Comparative Example 1 and Example 1 wherein an ethylene/α-olefin copolymer containing the same comonomers as those of the copolymer in Comparative Example 1 and having MT and density almost equal to those of the copolymer in Comparative Example 1 was used, the film of Example 1 was very low in reduction of the film impact. Comparative Example 2 From the ethylene/α-olefin copolymer (C-1) obtained in Comparative Example 1, a film having a thickness of 30 µm was formed in a manner similar to that of Example 1. Melt properties of the ethylene/α-olefin copolymer (C-1) and physical properties of the film formed from the copolymer are set forth in Table 3. Preparation Examples 2 and 3 The procedure of Preparation Example 1 was repeated except for varying the kinds of comonomers and the amounts thereof to those set forth in Table 1, to obtain ethylene/α-olefin copolymers (A-1-2), and (A-1-3). Physical properties of the ethylene/α-olefin copolymers (A-1-2), and (A-1-3) are set forth in Table 1. Examples 2 and 3 The procedure for preparing the ethylene copolymer composition in Example 1 was repeated except for varying the ethylene/α-olefin copolymer to those set forth in Table 3, to prepare ethylene copolymer compositions. From the ethylene copolymer compositions thus prepared, films each having a thickness of 30 µm were formed in a manner similar to that of Example 1. Melt properties of the ethylene copolymer compositions and physical properties of the films formed from the compositions are set forth in Table 3. Reference Examples 2 and 3 From the ethylene/α-olefin copolymers (A-1-2), and (A-1-3) obtained in Preparation Examples 2 to 4, films each having a thickness of 30 µm were formed in a manner similar to that of Example 1. Melt properties of the ethylene/α-olefin copolymers (A-1-2) and (A-1-3) and physical properties of the films formed from the copolymers are set forth in Table 3. Preparation Example 4 The procedure of copolymerization of ethylene with 1-hexene in Preparation Example 1 was repeated except for replacing bis(1,3-dimethylcyclopentadienyl)zirconium dichloride with ethylenebis(indenyl)zirconium dichloride and varying the comonomer amount to that set forth in Table 1, to prepare an ethylene/α-olefin copolymer (A-1-5). Physical properties of the ethylene/α-olefin copolymer (A-1-5) are set forth in Table 1. Example 4 The ethylene/α-olefin copolymer (A-1-5) obtained in Preparation Example 4 and a high-pressure radical polymerization low-density polyethylene (B-1-2) shown in Table 2 were used to prepare an ethylene copolymer composition in a manner similar to that of Example 1. From the ethylene copolymer composition thus prepared, a film having a thickness of 30 µm was formed in a manner similar to that of Example 1. Melt properties of the ethylene copolymer composition and physical properties of the film formed from the composition are set forth in Table 3. Reference Example 4 The procedure of film formation in Example 1 was repeated except for using the ethylene/α-olefin copolymer (A-1-5) obtained in Preparation Example 4, to form a film having a thickness of 30 µm. Melt properties of the ethylene/α-olefin copolymer (A-1-5) and physical properties of the film formed from the copolymer are set forth in Table 3. Example 5 The ethytene/α-otefin copolymer (A-1-1) obtained in Preparation Example 1 and a high-pressure radical polymerization low-density polyethylene (B-1-3) shown in Table 2 were used to prepare an ethylene copolymer composition in a manner similar to that of Example 1. From the ethylene copolymer composition thus prepared, a film having a thickness of 30 µm was formed in a manner similar to that of Example 1. Melt properties of the ethylene copolymer composition and physical properties of the film formed from the composition are set forth in Table 3. Comparative Example 3 The ethylenela-olefin copolymer (A-1-1) obtained in Preparation Example 1 and a high-pressure radical polymerization low-density polyethylene (D-1) shown in Table 2 were used to prepare an ethylene copolymer composition in a manner similar to that of Example 1. From the ethylene copolymer composition thus prepared, a film having a thickness of 30 µm was formed in a manner similar to that of Example 1. Melt properties of the ethylene copolymer composition and physical properties of the film formed from the composition are set forth in Table 3. As is evident from Comparative Example 3 and Reference Example 1, even by blending the ethylene/α-olefin copolymer with such a high-pressure radical polymerization low-density polyethylene as used in Comparative Example 3, the resulting composition was not increased in the melt tension. It has been confirmed from the examples, the comparative examples and the reference examples described above that when the ethylene/α-olefin copolymer is blended with a specific high-pressure radical polymerization low-density polyethylene, the resulting composition is improved in the moldability, and the film formed from the composition is improved in the optical characteristics. Further, the ethylene copolymer composition is hardly reduced in the film impact, as compared with the ethylene/α-olefin copolymer only, in spite that the composition contains a high-pressure radical polymerization low-density polyethylene having a low film impact Moreover, it has been also confirmed that a film showing high blocking resistance can be obtained from the ethylene copolymer composition of the invention. Table 2 High-pressure radical plymerization low-density polyethylene Code No. MFR (g/10 min.) Mw/Mn *1 Density (g/cm 3 ) Physical property of film Haze % Gloss % Film impact kg • cm/cm B-1-1 5.2 9.4 4.2 0.919 15.0 14 1,050 B-1-2 0.50 4.4 <0 0.924 7.4 51 1,750 B-1-3 0.32 10.6 <0 0.922 - - - D-1 66 8.9 12.4 0.915 - - - Remark *1 :value obtained by the formula 7.5×log(MFR)-1.2

Claims: An ethylene copolymer composition comprising: [A-1] an ethylene/C 3-20 α-olefin copolymer having the following properties: (i) a density (d) of 0.890 to 0.935 g/cm 3 , (ii) a melt flow rate (MFR) at 190°C under a load of 2.16 kg of 0.01 to 200 g/10 min, (iii) a temperature (Tm (°C)) at which the endothermic curve of the copolymer measured by a differential scanning calorimeter (DSC) shows the maximum peak and a density (d) which satisfy the relation Tm < 400 × d - 250 , (iv) a melt tension (MT (g)) at 190°C and a melt flow rate (MFR) which satisfy the relation MT > 2.2 × MFR - 0.84 , (v) a flow index (Fi (I/sec)) defined by a shear rate which is given when a shear stress of molten copolymer at 190°C reaches 2.4 x 10 6 dyne/cm 2 and a melt flow rate (MFR) which satisfy the relation FI > 100 × MFR , and (vi) an amount (W (% by weight)) of a decane-soluble portion at 23°C and a density (d) which satisfy the relation, in the case of MFR ≤10 g/10 min, W < 40 × exp - 100 ⁢ d - 0.88 + 0.1 in the case of MFR > 10 g/10 min, W < 80 × MFR - 9 0.26 × exp - 100 ⁢ d - 0.88 + 0.1 ; and [B-1] a high pressure radical polymerization low-density polyethylene having the following properties: (i) a melt flow rate (MFR) of 0.1 to 50 g/10 min, and (ii) a molecular weight distribution (Mw/Mn, Mw = weight-average molecular weight, Mn = number-average molecular weight) measured by GPC and a melt flow rate (MFR) which satisfy the relation Mw / Mn ≥ 7.5 × log MFR - 1.2 ; the weight ratio [A-1]:[B-1] being from 99:1 to 60:40, other than Comparative Example 5 of EP 0 598 626 A2. A film formed from a composition according to claim 1. A process for producing a film as defined in claim 2, which process comprises subjecting an ethylene copolymer composition as defined in claim 1 to inflation molding or T-die molding. Use of a film as defined in claim 2 as a wrapping film. A multi-layer film comprising at least one layer of a film according to claim 2. A process for producing a multi-layer film as defined in claim 5, which process comprises laminating a film as defined in claim 2 on a substrate. A process according to claim 6, wherein the substrate is a nylon substrate or a polyester substrate.

Inventors: IKEYAMA SEIICHI, KANESHIGE NORIO, MATSUNAGA SHINYA, TAKAHASHI MAMORU, TODO AKIRA, TSUTSUI TOSHIYUKI, IKEYAMA, SEIICHI, KANESHIGE, NORIO, MATSUNAGA, SHINYA, TAKAHASHI, MAMORU, TODO, AKIRA, TSUTSUI, TOSHIYUKI, IKEYAMA, SEIICHI, C/O MITSUI PETROCHEMICAL, Kaneshige, Norio, c/o Mitsui Petrochemical, Matsunaga, Shinya, c/o Mitsui Petrochemical, TAKAHASHI, MAMORU, C/O MITSUI PETROCHEMICAL, TODO, AKIRA, C/O MITSUI PETROCHEMICAL, TSUTSUI, TOSHIYUKI, C/O MITSUI PETROCHEMICAL
Applicants: MITSUI CHEMICALS INC, MITSUI CHEMICALS, INC.
Application year: 1993
Main classification: C08L23
IPC codes: C08L23