Ferroelectric-ferromagnetic composite materials

Abstract: A material which possesses both capacitive and inductive properties for suppressing electromagnetic interference is provided, wherein the material is a composite of a ferroelectric material and a ferromagnetic material. The ferroelectric-ferromagnetic composite material is formulated and processed so as to retain the distinct electrical properties of the individual constituents according to the relative quantities of the constituents present in the ferroelectric-ferromagnetic composite material. As a unitary composite element, the ferroelectric-ferromagnetic composite material is readily formable to provide a compact electrical filter whose filtering capability is highly suitable for suppressing electromagnetic interference from sources internal and external to an automotive environment.

Description: The present invention generally relates to filtering elements used in conjunction with electrical connectors to suppress electromagnetic interference. More particularly, this invention relates to improved materials for such filtering elements, wherein the improvement pertains to a composite ferroelectric-ferromagnetic filter element which exhibits both capacitive and inductive filtering capabilities. In an automotive environment, electromagnetic interference (EMI) is often present in the form of stray radio frequency noise, cross-talk between electrical devices, and noise created by such things as the making and breaking of circuits, spark discharges, poor or intermittent metallic contact between metal bonds and components, and atmospheric interference. It is well known that such EMI sources pose a serious threat to the electrical integrity of electrical circuitry and to the function of electrical components. As the dependence on electrical circuitry by modern automobiles increases, there is an increased need for effective electrical filters to reduce electromagnetic interference between individual electrical components and circuits. The difficulty of reducing such extraneous noise is further complicated by the desire to produce automobile electronic devices in smaller modules. In addition, low-level signals associated with on-board sensors and computer systems require better EMI filtering as switching electronic devices operate at higher voltages. Currently, the predominant method of EMI filtering is to install capacitors on an electronic circuit board using conventional manufacturing technology. At times, an inductor is added to provide "LC-type" filtering, such as when a block inductor is placed in series with one or more discrete capacitors. The use of LC-type filtering is often necessary in that a capacitor will exhibit inductance at high frequencies, producing resonance which can seriously impair the effectiveness of an electronic device. However, as electronic devices become more compact, these types of filters take up increasingly valuable space on the circuit board. Furthermore, these filters do not always provide a sufficient level of protection in that they are extremely sensitive to frequency and thus are application-dependent. As a result, it is often necessary to narrowly tailor the capabilities of such filters to perform well for very specific applications. It is also known to locate EMI filters, such as feed-through filters, at electrical interconnections to suppress cross-talk and other extraneous noise at the connector pins. Simple forms of such filters include a dielectric material, and, more preferably, a ferroelectric ceramic tube plated on its interior and exterior surfaces with metallic coatings that serve as electrodes. The interior electrode is in electrical contact with a connector pin whilst the exterior electrode is in electrical contact with a ground potential. The capacitance of the filter depends upon the surface area and thickness of the tube and the dielectric constant, or permittivity, of the ceramic material used. Whilst such filters are adequate for many applications, they are prone to exhibit the aforementioned resonance at very high frequencies. It is known to form the ceramic tube from a ferromagnetic material such as a ferrite, and then to sinter a ferroelectric material, such as barium titanate, to the exterior surface of the tube. The ferromagnetic material, characterised by having high permeability, provides inductance whilst the ferroelectric material, characterised by having high permittivity, provides capacitance between the ferromagnetic material and ground potential. As a result, the ferromagnetic and ferroelectric materials act together to provide an LC-type filter, wherein the inductive capability provided by the ferromagnetic material attenuates the resonance which otherwise occurs with the capacitive element at the higher frequencies. Examples of these types of EMI filters include U.S. Patent No. 3,035,237 to Schlicke, U.S. Patent No. 3,243,738 to Schlicke et al., U.S. Patent No. 3,789,263 to Fritz et al., and U.S. Patent No. Re. 29,258 to Fritz. Whilst the above EMI filters have advantageous features in terms of electromagnetic interference attenuation, they are not altogether economical to manufacture for purposes of the quantities typically required in automotive applications. Furthermore, single versus multi-component connectors are simpler to assemble and are believed to be less expensive to manufacture and store. Materials are known which exhibit both ferroelectric and ferromagnetic, or magnetoelectric, properties. One class of such materials consist of compounds having a single crystalline phase. However, the permeability and permittivity of this group of materials are generally inadequate for technical applications because the optimum magnetoelectric properties of these compounds exist only at temperatures well below room temperature. A more recently discovered group of magnetoelectric materials are formed from composites of fine-grain powders of ferrite and lead zirconate titanate (PZT) which have been sintered together for evaluating magneto-strictive and electro-strictive effects - i.e., the contraction or expansion of a material when subjected to a magnetic or electrical field. However, lead is reactive with the ferrite, yielding a composite material having greatly diminished permeability and permittivity as compared to its individual constituent materials. Such losses in constituent properties are well known to those skilled in the art. Thus, it would be desirable to provide a material which has both high permittivity and high permeability, such that a single element is able to exhibit both capacitive and inductive filtering capabilities for suppressing electromagnetic interference in an automotive environment. Furthermore, it would be desirable that such a material should be capable of use as an electrical component that is economical to produce for mass-production applications. JP-A-02232915 discloses a composite ceramic material containing a ferrite of metal oxide MFe 3 O 4 , having the metal element M containing one or more element selected from Mn, Ni, Mg, Co, Zn, Fe and containing a dielectric compound consisting of one or more groups of barium titanate and strontium titanate. It is an object of this invention to provide a material which is suitable as an electrical filter for suppressing electromagnetic interference in electrical components. It is a further object of this invention that such a material should have both a large permeability and a large permittivity so as to have both capacitive and inductive filtering capabilities. Lastly, it is still a further object of this invention that such a material should be economically formable as compact elements which can be used to suppress electromagnetic interference in electrical interconnections. In accordance with a preferred embodiment of this invention, these and other objects and advantages are accomplished as follows. According to the present invention as defined in claim 1, there is provided a material which is a composite of a high permittivity ferroelectric material and a high permeability ferromagnetic material. As such, the ferroelectric-ferromagnetic composite material can be formed as a compact unitary element which singularly exhibits both inductive and capacitive properties so as to act as an LC-type electrical filter. The compactness, formability and filtering capability of such an element is therefore highly suitable for suppressing electromagnetic interference from sources internal and external to an automotive environment. The ferroelectric-ferromagnetic composite includes a ferroelectric material and a ferromagnetic material which are combined and consolidated to form a solid composite material which is capable of suppressing electromagnetic interference at an electrical component or device. In the preferred embodiment, the ferroelectric material is barium titanate and the ferromagnetic material is a ferrite material, and more preferably based upon a copper zinc ferrite. The solid composite material is combined and consolidated in a manner that ensures that the microstructure of the solid ferroelectric-ferromagnetic composite is characterised by grains which are large enough to maintain their respective ferroelectric or ferromagnetic properties. As such, detrimental interaction between the ferroelectric and ferromagnetic materials is substantially absent, as determined by x-ray diffraction, so as to permit the materials to retain their permittivity and permeability properties, respectively. The method by which the ferroelectric-ferromagnetic composite is formed entails combining ferroelectric and ferromagnetic materials in granular form. The quantity of each material used is chosen to effect the final properties of the ferroelectric-ferromagnetic composite material. The preferred ratio of the two materials may vary widely, depending on the desired application. Once sufficiently mixed, the mixture is pressed at a pressure and temperature which are sufficient to minimise porosity in the resulting solid composite pre-form, and ultimately to maximise the effective permittivity and permeability of the composite material. In addition, the solid composite pre-form should exhibit sufficient strength and toughness to resist chipping and cracking, as well as to permit pre-shaping. The composite solid pre-form is then heated at a temperature and for a duration which is sufficient to sinter the ferroelectric and ferromagnetic materials together to form the ferroelectric-ferromagnetic composite material without causing the individual constituents to react together. Final shaping of the ferroelectric-ferromagnetic composite material can use routine procedures known for ceramic materials. Using the above processing method, the ferroelectric and ferromagnetic materials are able to retain their permittivity and permeability, respectively, such that the ferroelectric-ferromagnetic composite material can possess both capacitive and inductive filtering capabilities. This result is highly unexpected, in that some reduction in the respective properties would be expected when combining materials to form a composite material. However, no significant loss in electrical properties occurs. In the composite material, the individual constituents maintain their high permeability and permittivity, though the effective permeability and effective permittivity of the composite material is lessened as compared to the separate constituents. Furthermore, the capacitive and inductive characteristics of the ferroelectric-ferromagnetic composite materials made according to the present invention exhibit attenuation capabilities which show no signs of levelling off at frequencies as high as 1 GHz. Whilst the geometry of the ferroelectric-ferromagnetic composite material will significantly effect the ultimate capacitive and inductive nature of an electrical filter formed accordingly, the processing parameters of the ferroelectric-ferromagnetic composite material readily facilitate numerous variations which can further enable the particular properties of the device to be tuned to produce suitable attenuation for specific applications and environments. Other objects and advantages of this invention will be better appreciated from the following detailed description taken in conjunction with the accompanying drawings, in which: Figure 1 shows in cross-section a ferroelectric-ferromagnetic composite device in accordance with this invention; Figures 2 to 9 graphically show the attenuation capabilities of the device of Figure 1 formed from pure barium titanate, pure ferrite, and various intermediate proportions thereof; Figure 10 shows in cross-section a second ferroelectric-ferromagnetic composite device in accordance with this invention; Figures 11 and 12 graphically show the attenuation capabilities of the device of Figure 10 formed from a 62.5% barium titanate-37.5% ferrite composite and a 75% barium titanate-25% ferrite composite; and Figures 13 and 14 graphically show attenuation capability vs. volume percent barium titanate for the device of Figure 1 at 200 MHz and 1 GHz. A material which possesses both capacitive and inductive properties for suppressing electromagnetic interference is provided, wherein the material is a composite of a ferroelectric material and a ferromagnetic material. The ferroelectric-ferromagnetic composite material is formulated and processed so that the two materials remain as discrete particles therein without appreciable reaction occurring therebetween. As a result, the ferroelectric and ferromagnetic materials are able to retain their distinct electrical properties according to their relative quantities within the ferroelectric-ferromagnetic composite material. Referring specifically to Figure 1, there is shown a ceramic bead 10 formulated and processed according to the present invention as an electrical filter for an electrical harness interconnection. The ceramic bead 10 includes a tubular-shaped member 16 formed from the ferroelectric-ferromagnetic composite material. Both the exterior and interior cylindrical surfaces of the tubular-shaped member 16 are coated with an electrically-conductive material, such as a silver paste, which is fired to form a pair of electrodes 12 and 14. A connector pin 18 extending through the tubular-shaped member 16 is also shown. The connector pin 18 closely fits the inner periphery of the tubular-shaped member 16 to provide electrical contact therebetween. To complete the electrical filter, a ground wire or cable (not shown) is connected to the outer electrode 12. Whilst this particular configuration was used for testing various composite samples, as will be described in detail below, the ferroelectric-ferromagnetic composite material of this invention could foreseeably be employed in a variety of structures and applications. However, for comparison, substantially identical beads 10 of the type described were tested to eliminate geometrical effects as a factor in the performance of the beads 10 during evaluation. According to the present invention, the ferroelectric-ferromagnetic composite material is prepared from a composition composed of materials which, when combined, contribute properties to the ferroelectric-ferromagnetic composite which are similar to those of the constituent materials. To achieve this aspect, the individual constituent materials must essentially not react with one another in order to preserve their distinct crystalline phases because any interaction would significantly diminish the desired electrical properties, which interaction occurs for all known composite materials formed for numerous other applications. Increasing temperatures and small grain size of the constituents encourage reaction, whilst large grain size and widely separated melting temperatures help to preserve the phase-constituent separation and thus reduces the likelihood of an interaction occurring between the constituents. As such, the processing employed to form a unitary composite element, such as the ceramic bead 10, must begin with suitably sized ferroelectric and ferromagnetic particles. More specifically, the particles must be sufficiently sized so as to maintain their respective ferromagnetic and ferroelectric properties. Generally, the minimum particle diameter can be calculated according to the equation (Dt) 1/2 , where D is the diffusion rate of intermixing the two constituents, and t is the time which the particles will be sintered. In addition, it is preferable that the selected ferroelectric and ferromagnetic materials have melting temperatures that differ significantly from one another. An additional factor in maintaining suitably high permittivity and permeability of the ferroelectric-ferromagnetic composite material is the porosity of the composite material. In particular, porosity has been shown to be extremely deleterious to the electrical properties of both ferroelectric and ferromagnetic materials, even at levels as low as 5 volume percent. Furthermore, porosity is known to contribute other detrimental effects to a ceramic composite material, for example, low yield strength. The effect on manufacturing processes is to lower the yield in production, thereby increasing the average cost per unit. Accordingly, the processing employed to form the ferroelectric-ferromagnetic composite material should also minimise the formation of porosity therein. The ferroelectric material chosen for the ferroelectric-ferromagnetic composite is barium titanate (BaTiO 3 ), although other suitable ferroelectric materials could be used, such as barium strontium titanate, barium strontium niobate, and barium strontium tantalate. However, barium titanate is the preferred material in part because it is a high dielectric material having a large permittivity (κ) of about 2500 at about 1 kHz. Furthermore, the permittivity of barium titanate can be enhanced by the addition of dopants. High purity material and proprietary blends can be purchased commercially, such as through TAM Ceramics Incorporated, of Niagara Falls, New York, U.S.A.. The ferromagnetic material chosen for the ferroelectric-ferromagnetic composite is a ferrite, which is a high-resistance magnetic material consisting principally of ferric oxide (Fe 2 O 3 ) and one or more other metals. More preferably, the ferrite is a copper-based ferrite because of the low melting temperatures associated with such ferrites. Copper zinc magnesium ferrite (Cu 0.2 Mg 0.4 Zn 0.5 Fe 2 O 4 ) is exemplary of such copper-based ferrites, and has been used extensively for tests reported hereinafter. Copper based-ferrites have a permeability (µ) of about 500 at about 100 kHz. In addition, copper-based ferrites advantageously have lower sintering and melting temperatures than barium titanate. Specifically, barium titanate sinters in air to full density at about 1400°C and melts at about 1600°C, whilst copper zinc magnesium ferrite sinters in air to full density at about 1050°C to about 1150°C. As a result, there is a lesser tendency for the barium titanate and the copper zinc magnesium ferrite to react together and diminish their respective electrical properties. The ferroelectric-ferromagnetic composite material was prepared according to two methods. Each method entailed preparing the copper zinc magnesium ferrite by combining cupric oxide (CuO), zinc oxide (ZnO), magnesium oxide (MgO) and ferric oxide (Fe 2 O 3 ) in appropriate amounts, and then ball-milling, drying and calcining the mixture at about 800°C to about 850°C for about one to about three hours. However, the preparation of the barium titanate was varied in order to evaluate the effect of grain size on the electrical properties, and particularly permittivity, of the ferroelectric-ferromagnetic composite material. The first method entailed combining fine-grain barium titanate (particle size of about 1.0 micrometre) and fine-grain copper-based ferrite (particle size of about 1.0 micrometre) using standard ball-milling techniques, though other methods known in the art could also be used with suitable results. The powder mixture was then air-dried at about 100°C, and isostatically pressed into a composite pre-form at a pressure of 310264.2kPa (45,000 psi). The pre-form was then fired in a standard tube furnace at about 1050°C to about 1350°C for about 1 hour in air or flowing oxygen. These parameters assured a minimum porosity and maximum density of the composite material without interaction of the constituents thereof. The second method entailed processing the barium titanate prior to combining the two materials to yield larger grain sizes. Beads of the barium titanate were first formed by isostatically pressing granular (1.0 micrometre particles) barium titanate to about 310264.2kPa (45,000 psi) and then sintering at about 1400 °C for about one hour in air or flowing oxygen (flow rate of about 1 litre/minute). The beads were then fractured and pulverised, and then sieved through a 200 mesh screen. The particles which passed through the sieve were then collected and mixed with granular ferrite having a grain size of about 1 micrometre. Beads of the composite mixture were then prepared by isostatically pressing the mixture at about 310264.2kPa (45,000 psi), and then sintering at about 1050°C to about 1350°C for about one hour in air or flowing oxygen (flow rate of about 1 litre/minute). Each of the above processing methods produced a ferroelectric-ferromagnetic composite material which preserved the granular structure of the individual materials and showed no interaction between the barium titanate and the copper zinc ferrite. Generally, no significant differences were detected in the electrical properties of the ferroelectric-ferromagnetic composite materials formed by either method, indicating that initial grain size of the constituents generally is not a significant factor. As a result, the test data reported is representative of either process. For purposes of testing, the above methods were employed to form beads such as that shown in Figure 1. The dimensions of the beads 10 included a length of about 10.16 mm (0.4 inch), an outside diameter of about 6.35 mm (0.25 inch), and a bore diameter of about 1.27 mm (0.05 inch). The beads 10 were then coated with the silver electrodes 12 and 14 as shown. Beads 10 having different volume percent proportions of the ferroelectric and ferromagnetic materials were formed to evaluate the effect on electrical properties. As can be seen by reference to Figures 2 to 9, these proportion combinations included pure barium titanate (Figure 2), pure copper zinc magnesium ferrite (Figure 3), and various intermediate proportions thereof (Figures 4 to 9). The ability of the test beads 10 to filter electromagnetic interference was evaluated using a conventional vector network analyser which drove a variable frequency voltage source through the pin 18 into a 50 ohm load. The attenuation provided by each bead 10 can be seen in Figures 2 to 9. The graphs are numerically summarised in Table I below. ATTENUATION IN dB COMPOSITE (VOLUME %) 100 MHz 200 MHz 500 MHz 1 GHz 100% BaTiO 3 -19 dB -21 dB -21 dB -28 dB 100% ferrite - 7 dB - 8 dB - 8 dB - 9 dB 12.5% BaTiO 3 - 4 dB - 5 dB - 8 dB -13 dB 25% BaTiO 3 - 3 dB - 6 dB -14 dB -24 dB 37.5% BaTiO 3 - 5 dB - 9 dB -19 dB -31 dB 50% BaTiO 3 - 8 dB -12 dB -23 dB -37 dB 62.5% BaTiO 3 -11 dB -14 dB -24 dB -38 dB 75% BaTiO 3 -14 dB -15 dB -23 dB -36 dB Figure 2 illustrates that the attenuation of the pure ferroelectric barium titanate bead 10 was quite dramatic, with the attenuation level exceeding about -20 dB at about 200 MHz. However, an intrinsic resonance created a pass-band at about 400 MHz. Conventionally, such a resonance would be eliminated with either placing an inductor in series with the barium titanate bead 10, or by adding a layer of a ferromagnetic material to the bead. In contrast to the performance of the barium titanate bead 10, Figure 3 shows that the electrical filtering properties of the pure ferromagnetic copper zinc magnesium ferrite bead 10 never exceeded -9 dB. Figures 4 to 9 illustrate the advantageous effects of combining barium titanate with copper zinc magnesium ferrite in accordance with the disclosure of this invention. All six ferroelectric-ferromagnetic composite materials exhibited relatively little attenuation capability below about 10 MHz, particularly in comparison to the pure ferroelectric barium titanate and pure ferromagnetic copper zinc magnesium ferrite beads. However, the six ferroelectric-ferromagnetic composites were at least comparable to and more often superior to pure copper zinc magnesium ferrite at frequencies in excess of about 500 MHz, whilst those containing 50% barium titanate by volume were superior to pure copper zinc magnesium ferrite above 100 MHz. Although the ferroelectric-ferromagnetic composite materials did not exhibit attenuation capabilities superior to the pure barium titanate bead at frequencies below about 200 MHz, these composite materials also did not exhibit the resonance noted with the pure barium titanate at about 400 MHz. The absence of resonance in the ferroelectric-ferromagnetic composite beads resulted in better attenuation at frequencies exceeding about 200 MHz. The 62.5% barium titanate composite bead exhibited the maximum attenuation of any of the samples tested, with approximately -38 dB attenuation at about 1 GHz. For comparison, Figures 13 and 14 illustrate attenuation capability vs. volume percent barium titanate for the data gathered at 200 MHz and 1 GHz. For purposes of evaluating the ability to enhance the capacitive and inductive properties of the ferroelectric-ferromagnetic composite material, the previously-described processing methods were employed to form beads 110 such as that shown in Figure 10. The dimensions of the beads 110 were identical to that of the first beads 10 tested, with the exception that the 1.27 mm (0.05 inch) bore was greatly enlarged to about 5.33 mm (0.21 inch) for approximately one half the length of the bead 110. This produced a relatively thick-walled high-inductance region 120 and a relatively thin-walled high-capacitance region 122 in the bead 110. As before, the beads 110 were then coated with the silver electrodes 112 and 114 as shown. As seen by reference to Figures 11 and 12, beads 110 were formed with two different volume percent proportions of the ferroelectric and ferromagnetic materials - a 62.5% barium titanate, 37.5% copper zinc magnesium ferrite composite material (Figure 11), and a 75% barium titanate, 25% copper zinc magnesium ferrite composite material (Figure 12). The beads 110 were tested in the same manner as before, using a conventional vector network analyser. The attenuation provided by each bead 110 can be seen in Figures 11 and 12, whilst the graphs are numerically summarised in Table II below. ATTENUATION IN dB COMPOSITE (VOLUME %) 100 MHz 200 MHz 500 MHz 1 GHz 62.5% BaTiO 3 -26 dB -29 dB -37 dB -50 dB 75% BaTiO 3 -31 dB -34 dB -36 dB -56 dB Figures 11 and 12 illustrate the potential for enhancing the attenuation properties of the ferroelectric-ferromagnetic composite material by using a geometry that optimises the ferroelectric and ferromagnetic properties, exemplified by the geometry of Figure 10. On the average, attenuation was improved by at least an order of magnitude over the same compositions evaluated and discussed under Table I and Figures 8 and 9. It is foreseeable that greater enhancement may be achieved with other bead geometries, and can be tailored for particular applications. From the above, it is apparent that the ferroelectric-ferromagnetic composite material of the present invention is able to suppress high-frequency electromagnetic interference, particularly at frequencies above about 10 MHz. Moreover, electromagnetic interference suppression is attainable up to at least about 1 GHz, and is very likely attainable at frequencies much greater than this. In operation, the inductive capability provided by the ferromagnetic material damps the resonance exhibited by a ferroelectric material alone, providing improved performance at higher noise frequencies. As a particularly important aspect, the ferroelectric and ferromagnetic materials are combined and consolidated to form the composite material in a manner that ensures that the microstructure of the solid ferroelectric-ferromagnetic composite material is characterised by relatively large grains for both the ferroelectric and ferromagnetic materials. As such, interaction between the ferroelectric and ferromagnetic materials is substantially absent, which permits the materials to remain as discrete particles within the ferroelectric-ferromagnetic composite material, so as to retain their respective permittivity and permeability properties. This result is highly unexpected, in that some reaction between the ferroelectric and ferromagnetic materials would be expected. However, substantially no detrimental interaction was discovered by x-ray diffraction. As evident from the data, the relative quantities of the materials can be chosen to effect the final properties of the ferroelectric-ferromagnetic composite and can vary widely, though the final ferroelectric and ferromagnetic properties will also be affected by the geometry of the bead. In addition, the processing used serves to minimise porosity in the composite material so as to maximise the effective permittivity and permeability of the composite material while also optimising its strength and toughness to resist chipping and cracking. Finally, the ferroelectric-ferromagnetic composite material can be formed as a compact unitary element which singularly exhibits both inductive and capacitive properties to act as an LC-type electrical filter. As such, the ferroelectric-ferromagnetic composite material greatly simplifies the manufacturing of various filter shapes which can be adapted to influence the inductive and capacitive properties of the composite material. Shaping of the ferroelectric-ferromagnetic composite material can be done using routine procedures well known for ceramic materials. The compactness, formability and filtering capability of an electrical filter made according to the disclosure of the present invention is therefore highly suitable for suppressing electromagnetic interference from sources internal and external to an automotive environment. Whilst the immediate benefit to such an electrical filter is for electromagnetic interference suppression for electrical components, and particularly automotive electrical harness connectors, it is believed that the use of this invention could also be extended to magneto-strictive, electro-strictive and antennae applications. Therefore, whilst the present invention has been described in terms of a preferred embodiment, it is apparent that other forms could be adopted by one skilled in the art, for example by modifying the processing parameters such as the temperatures or durations employed, or by substituting other appropriate ferroelectric and ferromagnetic materials, or by introducing additional processing steps. Accordingly, the scope of the present invention is to be limited only by the scope of the following claims.

Claims: A composite ferroelectric-ferromagnetic material for use as an electrical filter, said composite ferroelectric-ferromagnetic material comprising: a ferroelectric material and a ferromagnetic material which are combined, intermixed and consolidated to form said composite ferroelectric-ferromagnetic material wherein the ferromagnetic and ferroelectric materials do not react with each other and so that said ferroelectric and ferromagnetic materials substantially retain their respective discrete electromagnetic properties; wherein said composite ferroelectric-ferromagnetic material is suitable for reducing electromagnetic interference; and wherein the ferroelectric material is selected from the group consisting of barium titanate, barium strontium titanate, barium strontium niobate, barium strontium tantalate and mixtures thereof, and the ferromagnetic material comprises principally a copper zinc magnesium ferrite. A composite ferroelectric-ferromagnetic material as recited in claim 1 wherein said ferroelectric material is barium titanate. A composite as set forth in claims 1 or 2 wherein the ferromagnetic material is Cu 0.2 Mg 0.4 Zn 0.5 Fe 2 O 4 . A composite as set forth in claim 1-3 wherein the ferroelectric material is present in about 62.5 volume percent and the ferromagnetic material is present in about 37.5 volume percent.

Inventors: DUNGAN DENNIS FOREST, MANTESE JOSEPH VITO, MICHELI ADOLPH LOUIS, DUNGAN, DENNIS FOREST, MANTESE, JOSEPH VITO, MICHELI, ADOLPH LOUIS
Applicants: GEN MOTORS CORP, GENERAL MOTORS CORPORATION
Application year: 1993
Main classification: H05K9
IPC codes: H03H1, H05K9