Thermoplastic compositions and processes for cross-linking

Abstract: The invention concerns a thermoplastic composition including (a) a main polymer component derived from ethylene and optionally at least one higher alpha-olefin having MI of from 1 to 5; (b) from 1 to 45 % by weight of (a) + (b) of an auxiliary polymer component which is cocrystallisable with (a) derived of ethylene and at least one olefinically unsaturated comonomer, said component (b) having an MI which is from 0.5 to 4.5 MI units below that of (a) which responds rapidly to crosslinking.

Description: Field of invention The invention relates to thermoplastic compositions and processes for cross-linking them for use especially in cable coating end-uses. Background of invention Different methods have been proposed for grafting a silane onto a backbone of an ethylenic polymer so that the resultant composition can be cross-linked by exposure to moisture. The grafting is performed by introducing a free-radical generating compound such as a peroxide. Processability of the composition depends on the polymers present in the composition. The presence of lower molecular weight materials can aid extrusion speeds (see WO 9108262). Other disclosures of compositions of ethylenic or olefinic polymers include GB 2098999; GB 2181437; FR 2315513 (US 4618654 corresponds); BE 9065048 and FR 2374344 (US 4228255 corresponds). GB 125-581; GB 1037687; GB 1031869; GB 1002453 and EP 57238-A1. EP-0A-0 507 075 discloses compositions containing mixtures of propylene polymers and ethylene polymers and an organosilicon compound. The ethylene polymer component may be a mixture of ethylene copolymers of different melt flow indices but compositions in which the ethylene polymer components are the major part of the composition are not disclosed. The moisture induced cross-linking is promoted generally by a silanol condensation catalyst present in the blend. The cross-linking is generally a separate, time-consuming step. It is the object of the invention to provide a polymer composition which responds rapidly to a cross-linking process. Summary of the invention The invention provides a thermoplastic composition including: a) a main polymer component derived from ethylene and optionally at least one higher alpha-olefin having Ml of from 0.5 to 15, preferably from 0.8 to 10; b) from 1 to 45% by weight of a) + b) of an auxiliary polymer component which is cocrystallisable with a), derived of ethylene and at least one olefinically unsaturated comonomer, said component b) having an Ml which is at least 0.3 units below that of a) (the Ml values being measured according to ASTM-1238, condition E; 2.16 kg : 190°C, and c) moisture cross-linking additives including a silane; a silanol condensation catalyst and a free radical initiator, wherein components a) and b) together comprise from 65% to 98% by weight of the composition. Preferably component b) has an Ml of from 0.5 to 12 units below that of a), especially from 1 to 10 units. Relatively small amounts of a lower melt index, i.e. higher molecular weight component, speed up the response of the blend in the silane cross-linking process. Thus, the moisture curing step subsequent to extrusion of an electrical cable can be shortened. Processability can be preserved as relatively small amounts only are used. The lower the Ml of the auxiliary component the smaller the amount needed for achieving faster moisture curing. Typically the Ml range is from 0.5 upwards for the auxiliary component. The selection of the main and the auxiliary component is fairly wide but care should be taken to ensure that they are mutually compatible to an extent sufficient for their co-crystallinisation. Co-crystallisation can be observed by absence of phase separation in microscopic observation or a significant change in melting behaviour of the blend as compared to the individual components. The requirement of co-crystallibility may also provide preferred ranges for blending the main and auxiliary component. Thus for different combination of main and auxiliary components, different MI and blending ranges may be optimal. It may be possible, if the main polymer component has an MI of 15, for the auxiliary component to have an MI of 1 if the components have good compatibility. If the MI difference is too high for certain combinations of components, conventional blending may become difficult but higher MI differences could be achieved by producing the components in a single polymerisation process e.g. by series reactors, i.e. without a physical blending process. The component b) may have an MI of 4.5 below that of a). It is believed that the high molecular weight fraction helps to make the effect of the cross-linking of a low molecular weight component apparent and detectable. The main component may be an ethylene homopolymer (LDPE) or a copolymer. Preferred polymers are LLDPE, LDPE and VLDPE. Table A below characterises distinguishing features of these polymers. POLYMER DENSITY COMONOMERS Mw/Mn HDPE > 0.94 LDPE 0.91 1-butene < 5 0.94 1-hexene preferably preferably 4-methyl-1-pentene < 3 0.915 to 0.925 1-octene 3.5 VLDPE 0.89-0.91 1-butene 1-hexene < 5 1-octene LDPE 0.91 to 0.93 < 5 The auxiliary component may be selected from amongst the same polymers as in Table A but with appropriate different melt indices. In all these cases the melt index of the auxiliary component is preferably 30 % especially 80 % below that of the main component. Thus if the main component has a melt index of 4, the auxiliary component may have a melt index of less than 0.8 (80 % of 4 = 3.2; 4 - 3.2 = 0.8). Preferably, the composition may further include a polymeric processing aid in the form of a fluorinated polymer and/or a polymer derived from ethylene and optionally at least one olefinically unsaturated comonomer having a MI which is at least 5 MI above that of (a) to aid extrusion. The compositions may be produced by blending, optionally together with other components of the silane cross-linking package. The composition of the invention may also be produced as a reactor blend for example in a series reactor arrangement for polymerisation. In the blends of the present invention, silane groups capable of crosslinking are introduced and provided on the polymer. Silane groups capable of crosslinking include any alkoxy silane- or chlorosilane- containing group which is capable of forming an -SiOH group on hydrolysis. The silane groups are preferably vinyl silane groups. They may be introduced into the polyolefin by grafting a silane, e.g., a vinyl silane, preferably a vinyl trialkoxy silane such as vinyl trimethoxy silane, onto the polyolefin backbone using known methods, for example employing a peroxide initiator. The polymers may be blended together using known techniques e.g., by melt mixing or extrusion blending. If the blending is carried out before or during silane grafting, then more than one of the polymer components will possess crosslinkable silane groups. Alternatively, the polymers may be separately silane grafted and then blended; or only the main component (a) may possess grafted silane groups such that it is the only polymer in the blend which is crosslinkable. Preferably, the blend has a silane group content of 0.5 to 1.5 wt % based on the total weight of the blend of components (a) and (b). The silane group-containing blend of the present invention may be cured using moisture, typically water at 60 to 90°C, preferably about 80°C, in the presence of a catalyst such as a dibutyl tin dilaurate. Industrially, such curing may be performed for example in a hot sauna or a steam environment; alternatively the blend may simply be left for an extended period of time in moist air. The blends of the present invention may contain additives which are typically used in coating compositions for cables e.g., fillers such as aluminium trihydrate, calcium carbonate, carbon black; colourants; and other additives such as anti-oxidants. They are generally incorporated at the polymer blending stage. The blends may be extruded using known methods e.g., a single screw extruder to produce a crosslinkable coating in the necessary dimensions. The extruded coating is then exposed to moisture to crosslink it. Accordingly, the present invention provides a polymeric composition comprising a blend as described above which is crosslinked through the silane groups; and a process for producing such a composition comprising performing a crosslinking reaction by hydrolysing and condensing the silane groups of the above described blends. The present invention also provides a shaped coating formed from such a composition; a cable when coated with such a composition; and the use of the above-described blends in cable coating applications. Table B sets out typical overall contents of all blends components. The invention is illustrated by the Examples. Examples 1-5 The resins listed in Table A were blended as shown in the later Tables 1 to 5 LIST OF POLYETHYLENE USED RESIN MI DENSITY MWD COMONOMER VLDPE 1 9.3 0.8815 1.98 1-BUTENE VLDPE 2 1.25 0.8857 1.88 1-BUTENE VLDPE 3 7.3 0.883 1.93 1-BUTENE VLDPE 4 1.1 0.9 2 1-BUTENE VLDPE 5 5.8 0.882 2 1-BUTENE VLDPE 6 1.4 0.883 1.86 1-BUTENE LLDPE 1 9 0.895 2 1-BUTENE LLDPE 2 0.8 0.886 2.06 1-BUTENE LLDPE 3 2.8 0.918 3.5 1-BUTENE LLDPE 4 0.5 0.918 - 1-BUTENE The samples were pre-dried at 70°C for 12 hours. The samples were tumble blended with 0.1 wt % of dicumyl peroxide, 1.2 wt % vinyl trimethoxy silane (VTMOS) and 0.05 wt % dibutyl tin dilaurate catalyst for a few minutes and left to soak for 12 hours. The resulting blends extruded and grafted using a Haake single screw extruder (25 L/D), L/D being the length/diameter ratio, a channel depth ratio of 3:1 giving a high compression using a 19 mm wide slit die for a flat strip having a thickness of 1 mm. The temperature profile was 160-180-200-185°C and the screw was turned at 40 rpm. The extruded tapes were put in a vacuum at a constant temperature then moisture crosslinked in water at 80°C for different periods of time. After the moisture curing, the specimen is immediately subjected to a hot-set test to measure the % elongation of the sample by subjecting it to a load of 2.0 kg/cm 2 for 15 minutes within an oven set at 200°C. The % elongation is measured where possible. It is inversely proportional to the state of the crosslink network (i.e. high % elongation indicate poor crosslink network formation and vice versa). The results of the experiments are shown below. Rapid crosslinking response is demonstrated by a small percentage of elongation. Generally speaking percentage elongation is also inversely proportional to crosslink density. In all cases two measurements are made. Also given is the torque on the screw to maintain 40 rpm and the melt pressure detected in the extruder. Both indicate processability. The MI in Table 1 was determined by ASTM-1238 condition E : 2.16 kg; 190°C. Example 1/Table 1 Crosslinking period (min) VLDPE 1 2 measurements VLDPE1/VLDPE2 (85/15) VLDPE1/VLDPE2 (70/30) VLDPE2 45 180%,180% 135%, 145% 120%, 130% 5 min. 85%/80% 60 145%, 160% 105%, 115% 110%, 105% 10 min 70%/60% 90 125%, 130% 95%, 95% 90%, 85% 30 min 30%/45% 120 90%, 90% 80%, 80% 75%, 70% Torque (NM) 18.4 21.4 26.5 51.2 Melt pressure (bar) 26 34 44 106 Example 2/Table 2 Curing period (min) VLDPE3 VLDPE3/VLDPE4 (85/15) 60 225% 80%, 80% 120 110%, 115% 60%, 55% 180 80%, 75% 35%, 40% Torque (NM) 23.1 26.7 Melt pressure (bar) 33 43 EXAMPLE 3/TABLE 3 Curing period (min) VLDPE5 VLDPE5/VLDPE6 (85/15) VLDPE5/VLDPE6 (70/30) VLDPE6 15 - - - 150%, 145% 30 - - - 90%, 90% 60 * 780", 856" 165%, 170% 120%, 125% 60%, 55% 90 150%, 135% 115%, 105% 85%, 100% 45%, 40% 120 105%, 105% 80%, 90% 60%, 65% - 150 70%, 75% 55%, 60% 50%, 50% - Torque (NM) 23.5 26.5 28.7 46.5 Melt pressure (bar) 32 37 42 82 * Where the sample does not elongate properly but breaks, the value marked " is the time in seconds before it breaks. EXAMPLE 4/TABLE 4 Curing period (min) LLDPE 1 LLDPE1/LLDPE2 (70/30) 30 210%, 200% 110%, 120% 45 155%, 150% 80%, 115% 60 135%, 140% 75%, 95% 120 90%, 85% 40%, 40% Torque (NM) 21.5 30.5 Melt pressure (bar) 32 60 EXAMPLE 5/TABLE 5 Curing period (min) LLDPE 3 LLDPE3/LLDPE4 (95/5) LLDPE3/LLDPE4 (80/20) LLDPE4 5 130%, 115% 95%, 90% 75%, 95% 30%, 25% 10 60%, 65% 45%, 45% 50%, 50% - 15 40%, 40% 30%, 30% 25%, 35% - 30 30%, 35% 20%, 30% 20%, 30% 20%, 15% Torque (NM) 28.4 29.1 31.7 53.1 Melt pressure (bar) 69 74 80 188 Once again the above data indicate that the addition of small amount of lower MI VLDPE to that of the higher MI ones reduce the curing time required to obtain low hot-set elongation % and the addition of higher molecular weight species does not make processing much more difficult as indicated by the torque and melt pressure measurements. The addition of a small amount (e.g. 5 wt %) of a PE wax reduces torque and melt pressure further without unduly extending the curing period.

Claims: Thermoplastic composition including a (a) a main polymer component derived from ethylene and optionally at least one higher alpha-olefin having Ml of from 0.5 to 15, preferably from 0.8 to 10; (b) from 1 to 45 % by weight of (a) + (b) of an auxiliary polymer component which is cocrystallisable with (a) derived of ethylene and at least one olefinically unsaturated comonomer, said component (b) having an Ml which is at least 0.3 units below that of (a) (the Ml values being measured according to ASTM-1238, condition E; 2.16 kg:190°C). and (c) moisture induced cross-linking additives including a silane, a silanol condensation catalyst and a free radical initiator, wherein components (a) and (b) together comprise from 65 % to 98 % by weight of the composition. Composition according to claim 1 including further (d) a polymeric processing aid in the form of a fluorinated polymer and/or a polymer derived from ethylene and optionally at least one olefinically unsaturated comonomer having an Ml which is at least 5 Ml units above that of (a). Composition according to claim 1 or 2 in which (a) is an LLDPE and (b) is an LLDPE, VLDPE or LDPE having an Ml at least 30 %, preferably at least 80 % below that of (a); (b) being preferably present in amounts of from 5 to 45 % especially 10 to 30 wt %. Composition according to claim 1 or claim 2 in which (a) is an LDPE and (b) is an LLDPE, VLDPE or LDPE having an MI at least 30 %, preferably at least 80 % below that of (a), (b) being present in amounts of from 5 to 45 wt % especially 10 to 30 wt %. Composition according to claim 1 or 2 in which (a) is a VLDPE and (b) is an LLDPE, VLDPE or LDPE having an MI at least 30 %, preferably at least 80 % below that of (a), (b) being present in amounts of from 5 to 45 wt %, especially 10 to 30 wt %. Composition according to any of the preceding claims in which there is present from 5 to 70 wt % by weight of (a) + (b) of a filler. Process for making a moisture cross-linkable product including (1) selecting a composition according to any of the preceding claims containing a silane and a silanol condensation catalyst and a free radical initiator; (2) grafting the silane onto the polymer components; (3) shaping the product in molten form; (4) exposing the product to moisture to cross-link the polymers. Process according to claim 7 in which the silane has been introduced in liquid form in an extruder or wherein the silane has been retained on a polymer and blended in solid form into the composition.

Inventors: VARRALL DAVID CYRIL, WONG WAI KEUNG, VARRALL, DAVID CYRIL, WONG, WAI KEUNG
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1993
Main classification: C08L23
IPC codes: C08F255, C08L23, C08L51