Non-aqueous battery

Abstract: A non-aqueous battery has a positive electrode having a composition essentially represented by a formula LixNiOy (0 < x ≦ 1.3 and 1.8 < y < 2.2), a negative electrode having a material which occludes and releases lithium reversibly and a non-aqueous electrolyte. The composition has a ratio of I₁₀₄ to I₀₀₃ ranging from 0.35 to 0.68 when measured by an X-ray powder diffraction method using CuK µ as a target. The I₁₀₄ represents a peak in tensity of reflection of X-rays at an angle about 2ϑ = 44 degrees with respect to the lattice plane (104), and the I₀₀₃ representing another peak intensity of reflection of X-rays at an angle about 2ϑ = 19 degrees with respect to the lattice plane (003).

Description: BACKGROUND OF THE INVENTION 1. Field of the invention This invention relates to a non-aqueous battery using lithium, as an active material, and more particularly to an improvement of a positive electrode material used in a non-aqueous battery. 2. Description of the prior art MoO 3 , V 2 O 5 , lithium-manganese composite oxide, MoS 2 and LiNiO 2 have been suggested as a positive electrode material in a non-aqueous battery, and some have been used in practice. A positive LiNiO 2 electrode generates about 3.7v with a lithium negative electrode and it has a high discharge voltage. This yields a high energy density batteries, and therefore, LiNiO 2 is one of the most useful materials for the positive electrode. To produce LiNiO 2 using conventional methods, the lithium hydroxide (LiOH-H 2 O) and nickel oxide (NiO) are prepared and mixed in equal mole amounts, and the resulting mixture is heat-treated under one atmosphere pressure at 700°C for about 4 hours. U.S. Patent No.4,980,080 describes this method. However, LiNiO 2 obtained by this conventional method generally has a small discharge capacity. Electrochimica Acta, vol. 38, no. 9, pp 1159-1167 (1993), Ohzuku et al., discloses lithium nickel oxides: LiNiO 2 , LiNi 3/4 Co 1/4 O 2 , LiNi 1/2 Co 1/2 O 2 and LiNi 1/4 Co 3/4 O 2 which have respectively the intensity ratio I (003) /I (104) of 1·32, 1·43, 1·69 and 2·11 on the X-ray diffraction pattern. SUMMARY OF THE INVENTION To overcome the small discharge capacity, many kinds of crystal structures of lithium-nickel composite oxide have been researched by an X-ray powder method. The research showed that changes in an intensity ratio for the reflection of X-rays (hereinafter "reflection intensity") at specific peaks can affect the discharge capacity of a positive electrode. Accordingly, a primary object of an embodiment of the present invention is to provide a non-aqueous battery with improved battery characteristics, such as an improved discharge capacity. A non-aqueous battery according to the present invention, comprises a negative electrode having a material which occludes and releases lithium reversibly, a non-aqueous electrolyte and a positive electrode which includes a composition essentially represented by a formula LixNiOy (where 0 < x ≤ 1.3 and 1.8 < y < 2.2) having a ratio of I 104 to I 003 ranging from 0.35 to 0.68 when measured by an X-ray powder diffraction method using CuKa as a target. The I 104 represents the one peak intensity of reflection ratio of X-rays at an angle about 2 = 44 degrees with respect to the lattice plane (104), and the I 003 represents another peak intensity of reflection ratio of X-rays at an angle about 2 = 19 degrees with respect to the lattice plane (003). In a positive electrode for a non-aqueous battery according to the present invention, the positive electrode comprises a lithium-nickel composite oxide essentially represented by a formula LixNioy (where 0 < x ≤ 1.3 and 1.8 < y < 2.2) having a ratio of I 104 to 1 003 ranging from 0.35 to 0.68. The composition, the composite oxide, or the lithium-nickel composite oxide used for the positive electrode may include cobalt, and which may be in the amount of 0.06 mole or less per 1 mole of nickel. The cobalt may be in the composition, the composite oxide, or the lithium-nickel composite oxide, as an impurity or as a composite oxide. Moreover, the composition, the composite oxide, or the lithium-nickel composite oxide may have a specific surface area which ranges from 0.5 m 2 /g to 10.0 m 2 /g when measured by a BET method, and it may have an average granule size ranging from 0.4µm to 10.0µm. The ratios of I 104 to I 003 for the composition, the composite oxide, or the lithium-nickel composite oxide may range from 0.40 to 0.60. BRIEF DESCRIPTION OF THE DRAWINGS These and other objects, advantages and features of the invention will become apparent from the following description thereof taken in conjunction with the accompanying drawings which illustrate specific embodiments of the invention. In the drawings: FIG.1 is a graph showing the X-ray diffraction pattern of an embodiment of the present invention, FIG.2 is a cross-sectional view of a non-aqueous battery in accordance with an embodiment of the present invention, FIG.3 is a graph showing the relationship between the ratio of reflection intensity and discharge capacity of an embodiment of the present invention, FIG.4 is a graph showing the relationship between specific surface area and discharge capacity of an embodiment of the present invention, and FIG.5 is a graph showing the relationship between an average granule size and discharge capacity of an embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The following detailed description is believed to be of the best presently contemplated mode of carrying out the invention. This description is not to be taken in a limiting sense, but is made merely for the purpose of illustrating general principles and embodiments of the invention. The scope of the invention is defined by the appended claims. In the present invention, a positive electrode has a composition essentially represented by the formula LixNiOy (where 0 < x ≤ 1.3 and 1.8 < y < 2.2). The composition of the electrode is measured by an X-ray powder diffraction method using CuK α target, where peak intensities of reflection of X-rays are determined both at about 2 = 19 degrees with respect to the lattice plane (003) and at about 2 = 44 degrees with respect to the lattice plane (104). Then the results of this measurement are represented as I 003 and I 104 , respectively, and a ratio of I 104 to I 003 (I 104 /I 003 ) is calculated, compositions having a ratio ranging from 0.35 to 0.68 are used for as a positive electrode in a battery. Consequently, the discharge capacity of the battery according to the present invention is increased. In preferred embodiments, the composition having a ratio ranging from 0.40 to 0.60 may be used for a larger discharge capacity. However, it should be noted that the above ratio ranges from 0.35 to 0.68 may affect a difference in crystal structure of the composition. It should also be noted that a composition represented by the formula LiNiO 2 and prepared by a conventional method has a ratio of I 104 to I 003 greater than 0.7. Further, the composition of LiNiO 2 disclosed in aforementioned U.P. patent 4,980,080 has a ratio of 0.73. In another embodiment of the present invention, the composition for the positive electrode may include cobalt (Co). Further, the cobalt may be included in the composition as an impurity or as a composite oxide. The amount of the cobalt should be less than 0.06 mole per 1 mole nickel (Ni) in the composition, since an amount of cobalt greater than 0.06 mole causes a reduction in the discharge capacity of the battery. It will be noted that an improvement of the battery discharge capacity may also be caused by the composition having a specific surface area ranging from about 0.5 m 2 /g to about 10.0 m 2 /g by the BET method or having an average granule size ranging from about 0.4µm to about 10.0µm. In an embodiment of the present invention, the composition may be lithium-nickel composite oxide, which is prepared as follows. A lithium compound, such as lithium salt represented as lithium carbonate, lithium oxide or lithium hydroxide, is mixed with a nickel compound, such as a nickel salt represented as nickel carbonate, nickel oxide or nickel hydroxide. Then, the mixture is heat-treated at a temperature ranging from about 600°C to about 1000°C, and in preferred embodiments ranging about 700°C to about 800°C. In the heat-treatment, duration time, atmosphere and partial pressure of oxygen for the heat-treatment, not to mention the heat-treatment temperature, are to be regulated. Additionally, the composition should be heat-treated under a dry air atmosphere having a partial pressure of oxygen not less than about 50.7 kPa (0.5 atm). Next, the treated composition represented by lithium-nickel composite oxide is mixed with a conductive agent, such as acetylene black or carbon black, and a binder, such as polytetrafluoroethylene (PTFE) or polyvinylidenfluoride (PVdF) to obtain a mixture for a positive electrode. In an embodiment of the present invention, a material for a negative electrode which occludes and releases lithium reversibly may be formed with lithium metal, lithium alloy, coke, graphite or glassy carbon. These carbon compositions have a porous structure, and therefore they may be used independently, or two or more of them may be mixed together. The negative electrode material is mixed with a binder, such as polytetrafluoroethylene (PTFE) or polyvinylidenfluoride (PVdF) to obtain a mixture for a negative electrode. In accordance with an embodiment of the present invention, an electrolyte may include an organic solvent or a mixture of organic solvents, such as a mixture of propylene carbonate and 1,2-dimethoxy-ethane dissolved lithium perchlorate (LiClO 4 ). The electrolyte may also be a solid electrolyte, such as lithium iodide (LiI). Using solid electrolytes instead of a separator provides a reliable and a high energy density battery which is also maintenance free because leakage of the electrolyte is prevented. However, if a separator is used, it may be selected from polyethylene films having a high ion conductivity, such as polypropylene micro porous film which is used in an ordinary non- aqueous battery. EXPERIMENT 1 FIRST EMBODIMENT A method of preparing a positive electrode in accordance with a first embodiment of the present invention is described below. Lithium hydroxide (LiOH) is mixed with nickel hydroxide (Ni(OH) 2 ) in a mole ratio of 1:1 in a mortar to obtain a mixture. In the above, the nickel hydroxide has a nickel purity of 99%. Next, the mixture is heat-treated at 750°C for 20 hours under a dry air atmosphere having a partial pressure of oxygen 75.8 kPa (0.75 atm). This produces a lithium-nickel composite oxide represented by the chemical formula LiNiO 2 . After heat-treatment, the composite oxide is pulverized by a grinding mixer for 60 minutes. Next the peak intensities of both reflection of X-rays at an angle about 2 = 19 degrees with respect to the lattice plane (003) and that of at about 2 = 44 degrees with respect to the lattice plane (104) for the composite oxide of LiNiO 2 are determined. Conditions for the X-ray determination are set as follows: Target; CUK α Wavelength of characteristic X-rays; 1.5406Å Slit; Divergence slit = 1 degree ; Scattering slit = 1 degree ; Receiving slit = 0.3mm Goniometer radius; 180mm Graphite monochromater FIG.1 shows an X-ray diffraction pattern for the composite oxide produced by the above method. The vertical axis represents reflection intensity of the X-rays, the horizontal axis represents angles (2 degree) of diffraction. The "a" represents an X-ray peak at about 2 = 19 degree with respect to the lattice plane (003) and the "b" means the peak of X-ray at about 20 = 44 degree with respect to the lattice plane (104), respectively. The peak intensity at an angle about 2 = 19 degrees with respect to the lattice plane (003) is defined as I 003 and the peak intensity at an angle about 2 = 44 degrees with respect to the lattice plane (104) is defined as I 104 . In the results shown in FIG.1, the ratio of I 104 to I 003 (I 104 / I 003 ) is about 0.50. The specific surface area for the composite oxide is measured at about 2.0m 2 /g by the BET method and the average size of the composite oxide granules is about 3µm. The composite oxide powder produced by the above-described method is next mixed with acetylene black as a conductive agent and polytetrafluoroethylene (PTFE) powder as a binder, in a weight ratio of 90:6:4 to obtain a mixture material. This mixture material is then pressed at a pressure of 2000kg/cm 2 and formed into a disc having a 20mm diameter. After the disc is formed, it is heat-treated at 250 °C for 2 hours to obtain a positive electrode plate. A negative electrode according to an embodiment of the present invention is prepared in a condition as described below. A lithium rolled plate is prepared, and stamped out to have a coin shaped disc with a 20mm diameter. The resulting coin-shaped lithium disc is used as a negative electrode. Following this step, propylene carbonate and 1,2-dimethoxyethane are mixed to form an organic solvent mixture in accordance with an embodiment of the present invention. A lithium salt (LiClO 4 ) is then dissolved into the solvent mixture in a concentration of 1 mole/liter to produce a non-aqueous electrolyte. In preferred embodiments the electrolyte, a volume ratio of propylene carbonate to 1,2-dimethoxyethane is preferably set at 1:1. As shown in FIG.2, the battery "BA1" in accordance with the first embodiment of the present invention has a positive electrode 1 and a negative electrode 2. The electrodes 1 and 2 are separated by a separator 3 which is impregnated with a non-aqueous electrolyte. The separator 3 is typically formed from a porous thin film such as polypropylene. The positive electrode 1, the separator 3 and the negative electrode 2 are stacked and placed in an outer case 4 as shown in FIG.2. The positive electrode 1 is connected to the outer case 4 through a current collector 6 consisting of ferritic stainless steel such as SUS430. The negative electrode 2 is connected to a cap 5 through a current collector 7 consisting of ferritic stainless steel, such as SUS430. The battery "BA1" typically has a coin shape; however other shapes may be used. In a preferred embodiment, the diameter and the height of the battery "BA1" are 24 mm and 3.0 mm, respectively. SECOND EMBODIMENT In a second embodiment in accordance with the present invention, the mixture of the first embodiment is heat-treated under a dry air atmosphere having a partial pressure of oxygen at 50.7 kPa (0.50 atm), to produce a lithium-nickel composite oxide. The resulting oxide is then formed in the same way as in the first embodiment. The composite oxide of the second embodiment shows a ratio of I 104 /I 003 of 0.60. Using this composite oxide produces a non-aqueous battery "BA2" in accordance with the second embodiment of the present invention. THIRD EMBODIMENT In a third embodiment in accordance with the present invention, a mixture is heat-treated under a dry air atmosphere having a partial pressure of oxygen at 101.3 kPa (1.00 atm), to produce a lithium-nickel composite oxide. The resulting oxide is then formed in the same way as in the first embodiment. The composite oxide of the third embodiment shows a ratio of I 104 /I 003 of 0.45. Using this composite oxide produces a non-aqueous battery "BA3" in accordance with the third embodiment of the present invention. FOURTH EMBODIMENT In a fourth embodiment in accordance with the present invention, the mixture of the first embodiment is heat-treated at 800°C under a dry air atmosphere having a partial pressure of oxygen at 202.6 kPa (2.00 atm), to produce a lithium-nickel composite oxide. The resulting oxide is then formed in the same way as in the first embodiment. The composite oxide of the fourth embodiment shows a ratio of I 104 /I 003 of 0.35. Using this composite oxide produces a non-aqueous battery "BA4" in accordance with the fourth embodiment of the present invention. FIFTH EMBODIMENT In a fifth embodiment in accordance with the present invention, the mixture of the first embodiment is heat-treated at 700°C under a dry air atmosphere having a partial pressure of oxygen at 50.7 kPa (0.50 atm), to produce a lithium-nickel composite oxide. The resulting oxide is then formed in the same way as in the first embodiment. The composite oxide of the fifth embodiment shows a ratio of I 104 /I 003 of 0.68. Using this composite oxide produces a non-aqueous battery "BA5" in accordance with a fifth embodiment of the present invention. COMPARATIVE EXAMPLE 1 In a comparative example 1, the mixture of the first embodiment is heat-treated at 850°C for 40 hours under a dry air atmosphere having a partial pressure of oxygen at 50.7 kPa (0.50 atm), to produce a lithium-nickel comparative composite oxide. The resulting comparative composite oxide is then formed in the same way as in the first embodiment. The comparative composite oxide shows a ratio of I 104 /I 003 of 0.10. Using this comparative composite oxide produces a comparative non-aqueous battery "BC1" of the comparative example. COMPARATIVE EXAMPLE 2 In a comparative example 2, the mixture of the first embodiment is heat-treated at 850°C under a dry air atmosphere having a partial pressure of oxygen at 50.7 kPa (0.50 atm), to produce a lithium-nickel comparative composite oxide. The resulting comparative oxide is then formed in the same way as in the first embodiment. The comparative composite oxide shows a ratio of I 104 /I 003 of 0.20. Using this comparative composite oxide produces a comparative non-aqueous battery "BC2" of the comparative example. COMPARATIVE EXAMPLE 3 In a comparative example 3, the mixture of the first embodiment is heat-treated at 800°C under a dry air atmosphere having a partial pressure of oxygen at 50.7 kPa (0.50 atm), to produce a lithium- nickel comparative composite oxide. The resulting comparative oxide is then formed in the same way as in the first embodiment. The comparative composite oxide shows a ratio of I 104 /I 003 of 0.30. Using this comparative composite oxide produces a comparative non-aqueous battery "BC3" of the comparative example. COMPARATIVE EXAMPLE 4 In a comparative example 4, the mixture of the first embodiment is heat-treated under a dry air atmosphere having a partial pressure of oxygen at 20.2 kPa (0.20 atm), to produce a lithium-nickel comparative composite oxide. The resulting comparative oxide is then formed in the same way as in the first embodiment. The comparative composite oxide shows a ratio of I 104 /I 003 of 0.70. Using this comparative composite oxide produces a comparative non-aqueous battery "BC4" of the comparative example. COMPARATIVE EXAMPLE 5 In a comparative example 5, lithium hydroxide (LiOH) is mixed with nickel carbonate (NiCO 3 ) in a mole ratio of 1:1 in a mortar to obtain a mixture. In the above, the nickel carbonate has a cobalt impurity of no more than 0.06 mole per nickel 1 mole. Next, the mixture is heat-treated at 750°C for 20 hours under a dry air atmosphere having a partial pressure of oxygen at 75.8 kPa (0.75 atm), to produce a lithium-nickel comparative composite oxide. After heat-treatment, the comparative composite oxide is pulverized by a grinding mixer for 60 minutes. The resulting comparative composite oxide shows a ratio of I 104 /I 003 of 0.80. Using this comparative composite oxide, a comparative non- aqueous battery "BC5" of the comparative example is produced. COMPARATIVE EXAMPLE 6 In a comparative example 6, lithium hydroxide (LiOH) is mixed with nickel oxide (NiO) in a mole ratio of 1:1 in a mortar to obtain a mixture. In the above, the nickel oxide has a nickel purity of 99.9%. Next, the mixture is heat-treated at 700°C for 20 hours under a dry air atmosphere having a partial pressure of oxygen at 75.8 kPa (0.75 atm), to produce a lithium-nickel comparative composite oxide. After heat-treatment, the comparative composite oxide is pulverized by a grinding mixer for 60 minutes. The resulting comparative composite oxide shows a ratio of I 104 /I 003 of 1.00. Using this comparative composite oxide produces a comparative non-aqueous battery "BC6" of the comparative example. COMPARATIVE EXAMPLE 7 In comparative example 7, the mixture of the first embodiment is heat-treated at 700°C under a dry air atmosphere having a partial pressure of oxygen at 20.2 kPa (0.20 atm), to produce a lithium-nickel comparative composite oxide. The resulting comparative oxide is then formed in the same way as in the first embodiment. The comparative composite oxide shows a ratio of I 104 /I 003 of 1.20. Using this comparative composite oxide produces a comparative non-aqueous battery "BC7" of the comparative example. COMPARATIVE EXAMPLE 8 In a comparative example 8, lithium carbonate (Li 2 CO 3 ) is mixed with nickel carbonate (NiCO 3 ) in a mole ratio of 1:2 in a mortar to obtain a mixture. In the above, the nickel carbonate is the same as used in the comparative example 5. Next, the mixture is heat-treated at 750°C for 20 hours under a dry air atmosphere having a partial pressure of oxygen at 20.2 kPa (0.20 atm), to produce lithium-nickel comparative composite oxide. After heat-treatment, the comparative composite oxide is pulverized by a grinding mixer for 60 minutes. The resulting comparative composite oxide shows a ratio of I 104 /I 003 of 1.25. Using this comparative composite oxide produces a comparative non-aqueous battery "BC8" of the comparative example. COMPARATIVE EXAMPLE 9 In a comparative example 9, lithium carbonate (Li 2 CO 3 ) is mixed with nickel hydroxide (Ni(OH) 2 ) in a mole ratio of 1:2 in a mortar to obtain a mixture. Next, the mixture is heat-treated at 700°C for 20 hours under a dry air atmosphere having a partial pressure of oxygen at 20.2 kPa (0.20 atm), to produce lithium-nickel comparative composite oxide. After heat-treatment the comparative composite oxide is pulverized by a grinding mixer for 60 minutes. The resulting comparative composite oxide shows a ratio of I 104 /I 003 of 1.30. Using this comparative composite oxide produces a comparative non-aqueous battery "BC9" of the comparative example. COMPARATIVE EXAMPLE 10 In a comparative example 10, the mixture according to the first embodiment is heat-treated at 600°C under a dry air atmosphere having a partial pressure of oxygen at 20.2 kPa (0.20 atm), to produce a lithium-nickel comparative composite oxide. The resulting comparative oxide is then formed in the same way as in the first embodiment. The resulting comparative composite oxide shows a ratio of I 104 /I 003 of 1.40. Using this comparative composite oxide produces a comparative non-aqueous battery "BC10" of the comparative example. STUDY Table 1 shows conditions under which the above described lithium-nickel composite oxides in batteries "BA1-BA5" in accordance with the described embodiments of the present invention and batteries "BC1-BC10" of the comparative example were obtained. In the table 1, the following conditions and resulting characteristics are displayed in the respective column; battery signs (1*), heat-treatment temperature (°C : 2*), heat-treatment duration (hours : 3*), partial pressure of oxygen (kPa : 4*), a ratio of I 104 /I 003 (5*) and starting materials (6*). 1* 2* 3* 4* 5* 6* BA1 750 20 75.8 0.50 LiOH+Ni (OH) 2 BA2 750 20 50.7 0.60 LiOH+Ni (OH) 2 BA3 750 20 101.3 0.45 LiOH+Ni (OH) 2 BA4 800 20 202.6 0.35 LiOH+Ni (OH) 2 BA5 700 20 50.7 0.68 LiOH+Ni (OH) 2 BC1 850 40 50.7 0.10 LiOH+Ni (OH) 2 BC2 850 20 50.7 0.20 LiOH+Ni (OH) 2 BC3 800 20 50.7 0.30 LiOH+Ni (OH) 2 BC4 750 20 20.2 0.70 LiOH+Ni (OH) 2 BC5 750 20 75.8 0.80 LiOH+NiCO 3 BC6 700 20 75.8 1.00 LiOH+NiO BC7 700 20 20.2 1.20 LiOH+Ni (OH) 2 BC8 750 20 20.2 1.25 Li 2 CO 3 +NiCO 3 BC9 700 20 20.2 1.30 Li 2 CO 3 +Ni (OH) 2 BC10 600 20 20.2 1.40 LiOH+Ni (OH) 2 FIG.3 shows the discharge characteristics of the batteries tested in the study. In FIG.3, the horizontal axis represents a ratio of I 104 /I 003 as to the lithium-nickel composite oxide used in a positive electrode in the batteries and the vertical axis represents battery discharge capacity per 1 gram (mAh/g ) of the composite oxide. In the test, the batteries are first charged to a charge stopping voltage of 4.2 V at a charging current of 1 mA/cm 2 . Next, the batteries are discharged to a discharge stopping voltage of 2.5 V, and then the discharge capacity of the composite oxide is determined. According to the FIG.3, the batteries made in accordance with embodiments of the present invention, "BA1-BA5", are produced with the composite oxide having a ratio of I 104 /I 003 ranging from 0.35 to 0.68 for the positive electrode, have the largest discharge capacity when compared to the batteries of the comparative example "BC1-BC10". The comparative examples do not have a ratio of I 104 /I 003 within the above range from 0.35 to 0.68. Moreover, the batteries of the present invention "BA1- BA3" according to the first three embodiments, are formed with the composite oxide having a ratio of I 104 /I 003 ranging from 0.40 to 0.60 for the positive electrode, and thus have the largest discharge capacities. EXPERIMENT 2 SIXTH-TENTH EMBODIMENTS In the sixth-tenth embodiments in accordance with the present invention, the pulverizing time of the composite oxide is changed from 0 minutes (a sixth embodiment), to 30 minutes (a seventh embodiment), to 90 minutes (a eighth embodiment), to 120 minutes (a ninth embodiment) and to 240 minutes (a tenth embodiment), respectively. All of the other conditions relating to formation are the same as that described above in the first embodiment. The different pulverizing times produced five kinds of lithium-nickel composite oxide, which have different surface areas and varied average sizes of granules. These five composite oxides were used to produce batteries "BA6-BA10" in accordance with the sixth-tenth embodiments of the present invention. Table 2 shows conditions under which the sixth-tenth embodiments were formed and the resulting characteristics are displayed in the respective column: battery signs (7*), pulverizing time (minutes : 8*), surface areas (m 2 /gram : 9*) by the BET method and an average size of granules (µm; 10*). In table 2, the value of the battery "BA1" of the first embodiment in accordance with the present invention is also presented for case of comparison. 7* 8* 9* 10* BA6 without pulverization 0.3 20.0 BA7 30 0.5 10.0 BA1 60 2.0 3.0 BA8 90 5.0 1.0 BA9 120 10.0 0.4 BA10 240 20.0 0.2 FIG.4 shows the discharge characteristics of the batteries tested in this experiment. In FIG.4, the horizontal axis represents a surface area (m 2 /g ) of the lithium-nickel composite oxide used in a positive electrode in the batteries and the vertical axis represents battery discharge capacity per 1 gram (mAh/g ) of the composite oxide. In the test, the batteries are first charged to a charge stopping voltage of 4.2 V at a charging current of 1 mA/cm 2 . Next, the batteries are discharged to a discharge stopping voltage of 2.5 V, and then the discharge capacity of the composite oxide is determined. According to the FIG.4, the batteries of the present invention "BA1 and BA6-BA10", are produced with the composite oxide having a surface area ranging from 0.50 m 2 /g to 10.00 m 2 /g for the positive electrode, and have the largest discharge capacity. EXPERIMENT 3 FIG.5 shows the discharge characteristics of the batteries "BA1 and BA6-BA10" tested in this experiment. In FIG.5, the horizontal axis represents an average size of granules (µm) as to the lithium-nickel composite oxide used in a positive electrode in the batteries and the vertical axis represents battery discharge capacity per 1 gram (mAh/g) of the composite oxide. In the test, the batteries are first charged to a charge stopping voltage of 4.2 v at a charging current of 1 mA/cm 2 . Next, the batteries are discharged to a discharge stopping voltage of 2.5 V, and then the discharge capacity of the composite oxide is determined. According to the FIG.5, the batteries of the present invention, "BA1 and BA6-BA10" are produced with the composite oxide having an average size of granules ranging from 0.40µm to 10.00µm for the positive electrode, and have the largest discharge capacity. In the above described embodiments, the batteries have a coin shape. However, it will be understood that a cylindrical shaped battery or a flat shaped battery may also be used. In the above embodiments, the characteristics of secondary batteries have been shown. However, the batteries in accordance with embodiments of the present invention may also be used as non-aqueous primary batteries. While the description above refers to particular embodiments of the present invention, it will be understood that many modifications may be made without departing from the invention. The accompanying claims are intended to cover such modifications. The presently disclosed embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims, rather than the foregoing description, and all changes which come within the meaning of the claims are therefore intended to be embraced therein.

Claims: A non-aqueous battery, comprising: a positive electrode having a composition comprised of a nickel - lithium oxide and cobalt; a negative electrode having a material which occludes and releases lithium reversibly; and a non-aqueous electrolyte; wherein: the nickel-lithium oxide essentially represented by a formula LixNiOy, where O < X ≤ 1.3 and 1.8 < y < 2.2, said formula having a ratio of I 104 to I 003 ranging from 0.35 to 0.68 when measured by an X-ray powder diffraction method using CuK α as a target, said I 104 representing a peak intensity of reflection of X-rays at an angle about 2 = 44 degrees with respect to a lattice plane (104) in the composition, and said I 003 representing another peak intensity of reflection of X-rays at an angle about 2 = 19 degrees with respect to a lattice plane (003) in the composition; and said cobalt is selected from a group consisting of an impurity and a composite oxide and is present in an amount less than 0.06 mole per 1 mole of nickel. A non-aqueous battery according to claim 1, wherein said composition has a specific surface area ranging from 0.5 m 2 /g to 10.0 m 2 /g. when measured by a BET method. A non-aqueous battery according to claim 1, wherein said composition has an average granule size ranging from 0.4µm to 10.0 µm. A non-aqueous battery according to claim 1, wherein said ratio of I 104 to I 003 ranges from 0.40 to 0.60.

Inventors: KUROKAWA HIROSHI, NISHIO KOJI, NOHMA TOSHIYUKI, SAITOH TOSHIHIKO, UEHARA MAYUMI, YAMAMOTO YUUJI, KUROKAWA, HIROSHI, NISHIO, KOJI, NOHMA, TOSHIYUKI, SAITOH, TOSHIHIKO, UEHARA, MAYUMI, YAMAMOTO, YUUJI
Applicants: SANYO ELECTRIC CO, SANYO ELECTRIC CO., LTD.
Application year: 1993
Main classification: H01M4
IPC codes: H01M4, H01M6