Programmable contact structure

Abstract: A programmable semiconductor contact structure and method are provided. A semiconductor substrate has a first patterned conductive layer for forming an interconnect. A first insulating layer overlies the first patterned conductive layer. An opening is formed through the insulating layer to the first patterned conductive layer to form the contact via. A buffer layer overlies portions of the first insulating layer and covers the opening. A third conductive layer overlies the buffer layer. A fourth conductive layer then overlies the integrated circuit. The buffer layer is a material, such as amorphous silicon, which functions as an anti-fuse and can be programmed by application of a relatively high programming voltage.

Description: The present invention relates generally to semiconductor integrated circuits, and more specifically to a programmable contact structure for such circuits. Field programmable gate arrays are a type of integrated circuit made up of multiple, connected gates and are known in the art. Field programmable gate arrays (FPGA) may be used to provide custom functions. These, and other types of field programmable logic devices, are programmed by storing programming information into the devices in a nonvolatile manner. This stored information defines the operation of the device. One-time programmable logic devices can be programmed using either fuses or anti-fuses. Anti-fuses are well known and implement logic functions by providing an open electrical circuit between nodes until the anti-fuse is programmed. The anti-fuse may be programmed by applying a high voltage across the nodes, which then creates an electrical short circuit by electrically connecting the nodes. Anti-fuses have been fabricated by first depositing an interconnect metal layer and then a buffer layer which is typically comprised of amorphous silicon. The sandwiched amorphous silicon will result in high contact resistance and therefore act as an insulator between the interconnect metal layer and an upper metal layer until the anti-fuse is programmed. After a programming voltage is applied, the resistance of the anti-fuse decreased so that larger current can flow through the contact. The difference in these resistances is great enough to be interpreted as logical zeros and ones by the circuity of the device. During formation of an amorphous silicon contact, an interlevel insulating layer is deposited over the amorphous silicon and is etched to form a contact via. This via exposes the underlying amorphous silicon. As is known in the art, process variations typically cause the insulating layer to have an uneven topography, with some areas being much thicker than others. Etch rates and times must be calculated to etch through the thickest areas of the insulating layer in order to ensure that none of the insulating layer is left in the contact via. However, even using highly selective etches, some of the amorphous silicon will necessarily be etched away in the via. In some cases, so much of the amorphous silicon may be etched away that a short is formed between the interconnect metal layer and the overlying metal layer. This would result in a particular location behaving as a programmed via when such was not intended. Perhaps worse, just enough of the amorphous silicon layer may be removed to make that location behave unreliably, allowing a completed device to pass testing only to fail in actual use. US-A-5100827 discloses an integrated circuit having one or more antifuses formed therein. The antifuses have a layer of amorphous silicon underlying a layer of conductive material and are covered by a layer of dielectric material which is etched to form contact vias. It would, therefore, be desirable to provide a programmable contact via method and structure in which the amorphous silicon buffer layer is not damaged during fabrication. It would be further desirable for a process for forming such a structure to be simple, reliable, and compatible with standard processing techniques. According to the present invention there is provided a programmable semiconductor contact structure in an integrated circuit comprising a semiconductor substrate having a first patterned conductive layer, wherein the first patterned conductive layer forms an interconnect, a first insulating layer overlying the first patterned conductive layer, an opening through the first insulating layer to the first patterned conductive layer, a second conductive layer overlying portions of the first insulating layer and extending into the opening to contact the first patterned conductive layer exposed through the opening, a buffer layer consisting of an amorphous silicon layer overlying the second conductive layer, a third conductive layer overlying the buffer layer, insulating sidewalls surrounding the second conductive layer, buffer layer, and third conductive layer said second conductive layer, buffer layer and third conductive layer being coextensive, and a fourth conductive layer overlying the integrated circuit, characterised in that the second and third conductive layers each comprise titanium nitride, whereby the third conductive layer protects the buffer layer from damage. The novel features believed characteristic of the invention are set forth in the appended claims. The invention itself however, as well as a preferred mode of use, and further objects and advantages thereof, will best be understood by reference to the following detailed description of an illustrative embodiment when read in conjunction with the accompanying drawings, wherein: Figures 1 - 4 are sectional views of an integrated circuit illustrating a method for forming the programmable contact structures of the invention; and Figure 5 illustrates an alternative structure for a programmable structure not forming part of the invention. The process steps and structures described below do not form a complete process flow for manufacturing integrated circuits. The structure of the present invention can be fabricated in conjunction with integrated circuit fabrication techniques currently used in the art, and only so much of the commonly practiced process steps are included as are necessary for an understanding of the present invention. The figures representing cross-sections of portions of an integrated circuit during fabrication are not drawn to scale, but instead are drawn so as to illustrate the important features of the invention. Referring to Figure 1 , a contact is to be formed on a semiconductor substrate 10 . Semiconductor substrate 10 may be simply the substrate on which an integrated circuit is formed, or it may represent multiple lower layers which have already been fabricated. The details of any such multiple lower layers are not important to the present invention. Contact vias in field programmable gate arrays may use amorphous silicon as a buffer between a lower level interconnect metal layer and upper metal layers. Amorphous silicon has a high resistance, thus providing insulation between the metal layers, until the contact is programmed. After programming occurs, by applying a relatively high programming voltage across the contact, the resistance of the amorphous silicon will decrease and it will become a conductor. A first conductive layer 12 is defined and patterned on the semiconductor substrate 10 . In a preferred embodiment, first conductive layer 12 is a first metal level interconnect layer and is comprised of aluminum. A first insulating layer 14 overlies first conductive layer 12 . First insulating layer 14 is preferably an oxide layer, undoped or lightly doped as known in the art. First insulating layer 14 is typically deposited using chemical vapor deposition (CVD) or low pressure chemical vapor deposition (LPCVD). Now referring to Figures 1 and 2, a photoresist mask 16 is used, as known in the art, for patterning and etching an opening or contact via 18. Contact via 18 provides an opening through first insulating layer 14 and exposes a portion of first conductive layer 12. A second conductive layer 20 is formed over first insulating layer 14 and extends into contact via 18. Conductive layer 20 overlies that portion of first conductive layer 12 which is exposed through the opening. In this manner second conductive layer 20, formed from titanium nitride, makes an electrical contact with first conductive layer 12. Next, a buffer layer 22 is formed over second conductive layer 20, and a third conductive layer 24 is formed over buffer layer 22. the invented structure, Buffer layer 22 is amorphous silicon and third conductive layer 24 is titanium nitride. Typically, buffer layer 22 will have a thickness of approximately 1000 angstroms, and second conductive layer 20 and third conductive layer 24 will each have a thickness of approximately 500 angstroms. Third conductive layer 24 acts to shield buffer layer 22 from damage during later processing steps. Therefore, after later etching and processing steps are complete, buffer layer 22 will remain intact and will retain its original thickness. Referring now to Figure 3, second conductive layer 20, buffer layer 22, and third conductive layer 24 are patterned and etched as known in the art. These layers 20, 22, 24 are removed from all portions of the chip except those locations where programmable contacts are desired. Insulating sidewalls 26 are formed using an oxide layer deposition followed by an anisotropic etch back to surround the sides of second conductive layer 20 , buffer layer 22 , and third conductive layer 24 . Insulating sidewalls 26 are used to insulate second conductive layer 20 from upper metal layers to be formed so that no conductive path is formed between interconnect 12 and later formed conductive layers through conductive layer 20 . With reference now to Figure 4 , a fourth conductive layer 28 , preferably comprised of aluminum, is formed over the integrated circuit. As described above, fourth conductive layer 28 is insulated from the second conductive layer 20 by insulating sidewalls 26 . The amorphous silicon comprising buffer layer 22 typically has a resistance on the order of 10 6 ohms. Therefore, fourth conductive layer 28 is insulated from first conductive layer 12 by buffer layer 22 , and the contact is effectively an open circuit. However, when contact via 18 is subjected to a programming voltage of approximately 10 - 15 Volts, the resistance of buffer layer 22 falls to below approximately a few hundred ohms. Buffer layer 22 thereby becomes a conductor and creates a contact between fourth conductive layer 28 and first conductive layer 12 . The contact thus acts as an anti-fuse whereby contact via 18 is an open circuit until contact via 18 is programmed by applying a voltage. After contact via 18 is programmed it becomes a closed circuit, allowing current to flow between the conductive layers. Referring now to Figure 5 , an alternate structure not forming part of the invention is shown. This contact differs from that shown in Figures 1-4 only in that the amorphous silicon layer 22 contacts the first conductor 12 directly, and no insulating sidewalls are formed. In this embodiment, insulating sidewalls are not needed because buffer layer 22 insulates first conductive layer 12 from fourth conductive layer 28 . As described above, the contact structure is an anti-fuse whereby an open circuit exists between first conductive layer 12 and fourth conductive layer 28. After a programming voltage is applied, a closed circuit is formed between first conductive layer 12 and fourth conductive layer 28 because of the reduced resistivity of the amorphous silicon comprising buffer layer 22. As will be appreciated by those skilled in the art, the contact structure and method described above provides for isolation of a conductive metal layer from an interconnect metal layer by using an amorphous silicon buffer layer. After a programming voltage is applied, the contact structure provides a closed circuit between the conductive metal layer and an interconnect metal layer by providing an electrical contact between the two metal layers. The electrical contact is formed due to the significantly reduced resistivity of the amorphous silicon buffer layer. The conductive layer 24 serves to protect the buffer layer 22 from damage during later processing steps. Since the via is etched through the insulating layer 14 before the amorphous silicon is deposited, no damage occurs at this stage as occurred using prior art processes. Additionally, during the backsputter typically used to clean the device immediately prior to depositing the upper conductive layer 28, layer 24 protects the amorphous silicon from damage. As a result, the amorphous silicon layer 22 can be relied on to retain its originally deposited thickness. This results in a programmable contact which is much more reliable than provided for in the prior art. This is done without adding significant process complexity.

Claims: A programmable contact structure in an integrated circuit, comprising: a semiconductor substrate (10) having a first patterned conductive layer (12), wherein the first patterned conductive layer forms an interconnect; a first insulating layer (14) overlying the first patterned conductive layer; an opening (18) through the first insulating layer to the first patterned conductive layer (12); a second conductive layer (20) overlying portions of the first insulating layer and extending into the opening to contact the first patterned conductive layer exposed through the opening; a buffer layer (22) consisting of an amorphous silicon layer overlying the second conductive layer; a third conductive layer (24) overlying the buffer layer; insulating sidewalls (26) surrounding the second conductive layer (20), buffer layer (22), and third conductive layer (24) said second conductive layer, buffer layer and third conductive layer being coextensive; and a fourth conductive layer (28) overlying the integrated circuit, characterised in that: the second (20) and third (24) conductive layers each comprise titanium nitride, the third conductive layer protects the buffer layer from damage. The contact structure according to claim 1 wherein the first patterned conductive layer (12) comprises aluminium. The contact structure according to claim 1, wherein the first insulating layer (14) is of oxide. The contact structure according to claim 1, wherein the fourth conductive layer (28) comprises aluminium. The contact structure according to claim 1, wherein the insulating sidewalls (26) are formed from oxide.

Inventors: WEI CHE-CHIA, WEI, CHE-CHIA
Applicants: ST MICROELECTRONICS INC, STMICROELECTRONICS, INC.
Application year: 1993
Main classification: H01L23
IPC codes: H01L29, H01L23, H01L21