Fluorinated organosilicon compound

Abstract: A novel fluorinated organosilicon compound, exhibiting excellent solvent resistance, chemical resistance and mold release, which is represented by general formula (1): wherein Rf is a divalent group represented by general formula (2): wherein Y is a fluorine atom or CF₃ group; l is an integer of 0-8; k and m are integers of 0-4; j and n are integers of 0 or 1; except when j=k=l=m=n=0.

Description: BACKGROUND OF THE INVENTION The present invention relates to a novel fluorinated organosilicon compound. Fluorinated organosilicon compounds are known to be useful crosslinking agents, or useful starting materials for solvent-resistant or chemical-resistant rubber materials, and those for mold release materials. Document "CA, vol. 106, 1987, abstr. n° 93654M" discloses ClSi(Me) 2 CH 2 CH 2 (CF 2 ) 6 CH 2 CH 2 Si(Me) 2 Cl as a starting compound to make siloxane polymers. SUMMARY OF THE INVENTION It is an object of the present invention to provide a novel fluorinated organosilicon compound which is extremely useful for the above applications. There is provided by the present invention a fluorinated organosilicon compound represented by general formula (1) below: wherein Rf is a divalent perfluoroalkylene group or a divalent perfluoropolyether group represented by general formula (2) below: wherein Y is a fluorine atom or CF 3 group; 1 is an integer of 0-8; k and m are integers of 0-4; j and n are integers of 0 or 1, except when j=k=l=m=n=0. In the fluorinated organosilicon compound of the present invention, there are two silylethylene groups. Since each silylethylene group has a structure that a Si atom is linked, through an ethylene group, to a divalent perfluoroalkylene group or a divalent perfluoropolyether group, the fluorinated organosilicon compound of the present invention exhibits excellent properties, such as solvent resistance, chemical resistance, and mold release, and it permits manufacturing therefrom, materials such as a variety of rubbers, with improvements in their properties. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is an IR spectrum of the fluorinated organosilicon compound of the present invention synthesized in Example 1. Figure 2 is an IR spectrum of the fluorinated organosilicon compound of the present invention synthesized in Example 2. Figure 3 is an IR spectrum of the fluorinated organosilicon compound of the present invention synthesized in Example 3. DETAILED DESCRIPTION OF THE INVENTION The above fluorinated organic group Rf in the present invention is preferably a divalent perfluoropolyether group. Its preferable examples are those illustrated below: -(CF 2 ) 4 -, -(CF 2 ) 6 -, -(CF 2 ) 8 - Thus, the following are typical examples for the fluorinated organosilicon compound of the present invention. The fluorinated organosilicon compound of the present invention may be synthesized by treating, with a reducing agent, a doubly-silyl-terminated perfluoropolyether or a doubly-silyl-terminated perfluoropolyalkylene represented, for example, by general formula (3) below: wherein X represents a halogen atom, F, Cℓ, Br, or I and Rf has the same meaning as previously defined. The reaction of a polyether or polyalkylene of general formula (3) above may be readily carried out by suspending or dissolving a reducing agent in a nonaqueous solvent, and adding dropwise the polyether or polyalkylene of general formula (3) above. Suitable reducing agents to be used are lithium aluminum hydride, sodium borohydride, and the like, usually used in amounts of 1/4 - 3 times, preferably about 1/2 - about equimolar amounts with respect to the terminal group X of the compound or general formula (3) above. Suitable nonaqueous solvents are dehydrated nonaqueous solvents, such as THF, diethylether, 1,3-dimethyl-2-imidazolidinone (DMI), dimethylformamide (DMF), dimethylsulfoxide (DMSO), and the like. If the reaction, which for the most part proceeds rapidly even at room temperature, is slow, it should be heated to a suitable temperature ranging from 40-100°C. The fluorinated organosilicon compounds of the present invention may be used in a variety of applications. For example, treating a double-unsaturation-terminated perfluoropolyether or perfluoropolyalkylene, for example, as represented by the following general formula: CH 2 =CH-Rf-CH=CH 2 (Rf is as previously defined) with a fluorinated organosilicon compound of the present invention in the presence of an addition reaction catalyst will lead to the synthesis of a polymer with a main chain containing perfluoropolyether groups or perfluoropolyalkylene groups. The polymer is useful as a material for highly solvent-resistant and chemical-resistant rubber because the polymer has a high fluorine content, and particularly as a material which may be used as a mold release because the polymer has a low surface energy. EXAMPLES The present invention is illustrated in more detail by reference to the following examples. EXAMPLE 1 To a 100mℓ three-neck flask provided with a stirrer, a thermometer, a Dimroth condenser, and a dropping funnel through which nitrogen gas was introduced at a rate of 50mℓ/min were added 0.38 g of lithium aluminum hydride and 10 g of THF, followed by adding dropwise, while stirring the contents with a stirrer, 10.7g of a doubly-dichlorosilyl-terminated perfluoropolyether represented by the following formula: After completing the addition, the mixture was allowed to stand for 30 minutes at room temperature and after filtering off the unchanged lithium aluminum hydride, it was vacuum distilled to give 8.3 g of a fraction boiling at 117 °C /lmmHg. The distillate fraction was analyzed by elemental analysis, IR, 1 H-NMR, 19 F-NMR, and GC-MASS. The results are given below. GC-MASS: Molecular weight = 1,004 IR: The spectrum is provided in Figure 1: ν Si-H : 2,130cm -1 ν c-F : 1,100-1,300cm -1 1 H-NMR: TMS Standard, ppm 0.13 (d, Si-CH 3 , 12H) 0.83 (m, Si-CH 2 , 4H) 2.20 (m, CF-CH 2 , 4H) 3.93 (m, Si-H, 2H) 19 F-NMR: CF 3 COOH Standard, ppm a: - 3.60 b: - 6.19 c: - 9.36 d: -52.05 e: -67.87 Elemental Analysis: C% H% Si% F% O% Calculated 27.5 2.2 5.5 56.8 8.0 Found 27.8 1.9 5.1 56.7 8.5 The above analytical results show the distillate fraction to be a compound of the following structural formula. EXAMPLE 2 To a 100mℓ three-neck flask provided with a stirrer, a thermometer, a Dimroth condenser, and a dropping funnel through which nitrogen gas was introduced at a rate of 50mℓ/min were added 0.38 g of lithium aluminum hydride and 10 g of THF, followed by adding dropwise, while stirring the contents with a stirrer, 9.lg of a doubly-dichlorosilyl-terminated perfluoropolyether represented by the following formula: After completing the addition, the mixture was allowed to stand for 30 minutes at room temperature and after filtering off the unchanged lithium aluminum hydride, it was vacuum distilled to give 6.9 g of a fraction boiling at 108 °C /lmmHg. The distillate fraction was analyzed in a manner similar to that of Example 1 to give the following results: GC-MASS: Molecular weight = 838 IR: The spectrum is provided in Figure 2: ν Si-H : 2,130cm -1 ν c-F : 1,100-1,300cm -1 1 H-NMR: TMS Standard, ppm 0.14 (d, Si-CH 3 , 12H) 0.85 (m, Si-CH 2 , 4H) 2.21 (m, CF-CH 2 , 4H) 3.95 (m, Si-H, 2H) 19 F-NMR: CF 3 COOH Standard, ppm a: - 3.93 b: - 4.81 c: - 9.35 d: -10.78 e: -43.11 f: -68.07 Elemental Analysis: C% H% Si% F% O% Calculated 28.7 2.6 6.7 54.4 7.6 Found 28.9 2.3 6.7 55.0 7.1 The above analytical results show the distillate fraction to be a compound of the following structural formula. EXAMPLE 3 To a 100mℓ three-neck flask provided with a stirrer, a thermometer, a Dimroth condenser, and a dropping funnel through which nitrogen gas was introduced at a rate of 50mℓ/min were added 0.76 g of lithium aluminum hydride and 10 g of THF, followed by adding dropwise, while stirring the contents with a stirrer, 10.8g of a doubly-dichlorosilyl-terminated perfluoropolyalkylene represented by the following formula: After completing the addition, the mixture was allowed to stand for 30 minutes at room temperature, and after filtering off the unchanged lithium aluminum hydride, it was vacuum distilled to give 7.0 g of a fraction boiling at 121 °C /4mmHg. The distillate fraction was analyzed in a manner similar to that of Example 1 to give the following results. GC-MASS: Molecular weight = 474 IR: A spectrum is provided in Figure 3: ν Si-H : 2,130cm -1 ν c-F : 1,100-1,300cm -1 1 H-NMR: TMS Standard, ppm 0.16 (d, Si-CH 3 , 12H) 0.88 (m, Si-CH 2 4H) 2.22 (m, CF-CH 2 , 4H) 3.96 (m, Si-H, 2H) 19 F-NMR: CF 3 COOH Standard, ppm a: -38.42 b: -44.28 c: -45.80 Elemental Analysis: C% H% Si% F% Calculated 35.4 4.6 11.8 48.2 Found 35.6 4.3 12.1 48.0 The above analytical results show the distillate fraction to be a compound of the following structural formula. Because the novel fluorinated organosilicon compound of the present invention has two silylethylene groups having a structure that a Si atom is linked, through an ethylene group, to a divalent perfluoroalkylene group or a divalent perfluoroether group, they exhibit excellent properties, such as solvent resistance, chemical resistance, and mold release, and materials prepared from these polymers, such as a variety of rubbers, show improvements in these properties.

Claims: A fluorinated organosilicon compound represented by general formula (1): wherein Rf is a divalent group represented by general formula (2): wherein Y is a fluorine atom or CF 3 group; l is an integer of 0-8; k and m are integers of 0-4; j and n are integers of 0 or 1; except when j=k=l=m=n=0. The organosilicon compound of claim 1, wherein Rf is a divalent perfluoropolyether group. The organosilicon compound of claim 1, wherein Rf is a divalent perfluoroalkylene group. The organosilicon compound of claim 1, wherein Rf is wherein k and m are integers of 0-4; except when k=m=0. The organosilicon compound of claim 1, wherein Rf is The organosilicon compound of claim 1, wherein Rf is wherein k and m are integers of 0-4. The organosilicon compound of claim 1, wherein Rf is wherein k and m are integers of 0-4; and l is an integer of 1-8. The organosilicon compound of claim 1, wherein Rf is wherein k and m are integers of 0-4; and l is an integer of 0-8.

Inventors: MATSUDA TAKASHI, SATO SHINICHI, TAKAGO TOSHIO, TAKANO KOUJI, MATSUDA, TAKASHI, SATO, SHINICHI, TAKAGO, TOSHIO, TAKANO, KOUJI
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1993
Main classification: C07F7
IPC codes: C07F7