Magnetic particles for magnetic recording medium and process for producing the same

Abstract: Magnetic particles suitable for magnetic recording which comprise acicular or plate-like magnetic particles and not less than 0.01 wt% (calculated as Al, SiO₂ or Al and SiO₂ based on the acicular or plate-like magnetic particles) of an oxide or hydroxide containing Al, Si or both Al and Si adhered to the surfaces of the acicular or plate-like magnetic particles, and which have a value of the molecular-weight-dependent parameter α of not less than 0.50, wherein α is defined by formula (I) : As = K₁ · M α wherein: M is the number-average molecular weight of a binder; As is the saturation adsorption of the binder; and K₁ is a constant dependent on the binder and the solvent used for measuring As.

Description: The present invention relates to magnetic particles suitable for magnetic recording, a process for producing the magnetic particles and a magnetic recording medium incorporating the magnetic particles. With the recent development of miniaturized and light-weight magnetic recording and reproducing apparatuses, recording media such as magnetic tape, magnetic disks, magnetic cards and the like have increasingly been required to have a higher performance and a higher recording density. In order to improve the performance and the recording density of a magnetic recording medium, it is necessary to improve the residual magnetic flux density Br of the magnetic recording medium. The residual magnetic flux density Br of the magnetic recording medium largely depends upon the dispersibility of the magnetic particles in the vehicle and the orientation property and the packing property of the magnetic particles in the coating film. Various attempts have been made to improve the dispersibility of magnetic particles. For example, a method of modifying the surfaces of the magnetic particles by coating with an Si compound or an Al compound, is described in JP-A-55-83207 (1980), JP-A-57-56904 (1982), JP-A-58-60506 (1983), JP-A-58-161725 (1983), JP-A-59-23505 (1984), JP-A-60-217529 (1985), JP-A-61-63921 (1986) and JP-A-62-89226 (1987). For example, JP-A-58-161725 (1983) discloses a method of producing magnetic iron powder comprising neutralizing an alkaline suspension containing iron powder, silicate and aluminate with an acid such as carbon dioxide gas so as to form a film of silicic acid and aluminum oxide on the particle surfaces of the iron powder. JP-A-57-56904 (1982) discloses a magnetic powder for magnetic recording, comprising fine hexagonal ferrite particles having an average particle diameter of 0.01 to 0.3 µm which are obtained by depositing SiO2 to the particle surfaces. JP-A-62-89226 (1987) discloses a magnetic powder produced by forming a layer of an aluminum compound on the surface of magnetic iron oxide powder containing cobalt having a BET specific surface area of not less than 40 m 2 /g, and a process for producing a magnetic powder comprising reacting the magnetic iron oxide powder in an aqueous solution containing a cobalt salt, a ferrous salt and an alkali, thereby forming an iron oxide layer containing cobalt on the particle surfaces of a magnetic iron oxide powder, and adding an aqueous solution of an aluminum salt in the reaction solution so as to neutralize the reaction solution, thereby forming a layer of an aluminum compound on the iron oxide layer containing cobalt. A method of producing magnetic particles by coating the surfaces of magnetic particles with a film of an Si compound, forming a film of an Al compound thereon, and further forming a film of an Si compound on the film of the Al compound is also known, as described in, for example, JP-A-63-161522 (1988). Methods of coating the surfaces of magnetic particles with a compound other than an Si compound and an Al compound are disclosed in, for example, JP-A-62-50889 (1987) which discloses a method of coating the particle surfaces with Mg, Ca, Sr, Ba, Zn, Cd, Al, Ga, Y, Pb or the like; JP-A-59-103310 (1984) discloses a method of coating the particle surfaces with Cu, Al, Ti, Zr, Sn, V, Nb, Sb, Cr, Mo, W, Ni or the like; JP-A-63-303817 (1986) discloses a method of coating the particle surfaces with Si, Al, Ca, Ti, V, Mn, Ni, Zn, P or the like; and JP-A-2-70003 (1990) discloses a method of coating the particle surfaces with P and Zn, Co, Ni, Cr, Cu, Fe, Al or the like. JP-A-59-103310 (1984) discloses a method of producing magnetic iron oxide containing cobalt by coating at least one of the oxide or hydroxides of Cu, Al, Ti, Zr, Sn, V, Nb, Sb, Cr, Mo, W, and Ni to the particle surfaces of magnetic iron oxide containing cobalt and then treating the iron oxide containing cobalt with steam, or treating the iron oxide containing cobalt with steam before coating step of the oxide or hydroxide to the particle surfaces. JP-A-270003 (1990) discloses a method of treating a ferromagnetic iron powder by oxidizing in an atmosphere containing oxygen the surface of the ferromagnetic iron powder containing iron as the main ingredient and produced by a dry-reduction process, suspending the ferromagnetic iron powder in water, and adding a phosphoric acid compound and a metal salt of at least one of Zn, Co, Ni, Cr, Cu, Fe, and Al to the thus-obtained suspension so as to deposit phosphoric acid and a compound of the metal to the ferromagnetic iron powder. Furthermore, JP-A-58-60506 (1983) discloses a magnetic powder having improved dispersibility which contains at least one of the oxide or hydroxides of Cu, Ag, Al, Ti, Zr, Sn, V, Nb, Ta, Sb, Cr, Mo, W and Ni on the surface thereof. Although magnetic particles having an excellent dispersibility are now in strong demand, the particles obtained by any of the above-described methods cannot be said to have excellent dispersibility. The reason why particles having an excellent dispersibility are not obtained by any known method is that magnetic particles agglomerate due to the interaction caused by the magnetism, as described at p. 16 of Magnetic Paint Seen from a Standpoint of a Researcher of Magnetic Recording Material pp. 14 to 16 of PROCEEDING OF SEVENTH SUMMER FERRITE SEMINER (1977), published by the Society of Powder and Powder Metallurgy, ".... It is generally considerably difficult to obtain a high degree of dispersion even in an ordinary non-magnetic pigment. It is much more difficult in the case of a magnetic powder due to a magnetic interaction...", and the surface of each agglomerate is coated. Especially, in the case of hexagonal ferrite particles which have an easy magnetization axis perpendicular to the plane, the particles so firmly agglomerate due to the interaction caused by the magnetism that it is difficult to separate the agglomerates into discrete particles merely by a mechanical treatment. The dispersibility of magnetic particles means to what degree the magnetic particles disperse in a polymer, as described at p. 505 of Explication and Applied technique of Dispersion and Agglomeration (1992), published by K.K. Technosystem, ".... A magnetic coating is prepared by stably dispersing a magnetic powder in a system containing, as the main ingredient, a high-molecular resin-solvent as a binding dispersant. A substrate is uniformly coated with the magnetic coating. The performance of the thus-obtained recording medium is therefore largely dependent upon the dispersion stability of the magnetic particles...." For this reason, many studies have been undertaken as to the improvement of the dispersibility of magnetic particles. The evaluation of the dispersibility is represented by a molecular-weight-dependent parameter a (hereinunder referred to merely "parameter α"), as described at pp. 94 to 96 of the above-described Explication and Applied technique of Dispersion and Agglomeration , ".... Many natural and synthetic polymers are adsorbed onto the surface of colloidal particles and form a thick adsorption layer, which exerts a great influence on the stability of the dispersion system. The following relationship generally holds between the molecular weight (M) and the saturation adsorption (As) of a polymer: As = K 1 . M α wherein K 1 is a constant characteristic of the system, and α is called a molecular-weight-dependent parameter, which is also characteristic of the system and changes between 0 and 1 depending upon the structure of the adsorption layer.... When α = 1, the polymer is adsorbed at the end of a molecule. The saturation adsorption (As) is proportional to the molecular weight (M). In this system, since the molecules of the polymer stand close together in the form of deep adsorption layers on the particle surfaces, a strong solid repulsion effect is produced and effectively contributes to the stability of the dispersion system...." The parameter α of the magnetic particles obtained by coating the particle surfaces with an Si compound or an Al compound in accordance with the known methods described in JP-A-55-83207 (1980), JP-A-57-56904 (1982), JP-A-58-60506 (1983), JP-A-58-161725 (1982), JP-A-59-23505 (1984), JP-A-60-217529 (1985), JP-A-61-63921 (1986) and JP-A-62-89226 (1987), was about 0.40 to 0.45, while the parameter α of the particles which were not subjected to such a surface-treatment was about 0.28 to 0.34. The parameters α of the magnetic particles obtained by the methods described in JP-A-63-161522 (1988), JP-A-58-60506 (1983), JP-A-59-103310 (1984), JP-A-63-303817 (1988) and JP-A-2-280301 (1990) was about 0.40 to 0.45. On the other hand, when a magnetic tape is produced from such magnetic particles, the following problems are sometimes caused. Firstly, the strength of the coating film is sometimes lowered. This fact is described, for example, at p. 170 of Causes for Friction and Abrasion between Magnetic Tape and Magnetic Head and Countermeasure for Troubles (1987), published by the publication department of Technological Information Center, ".... The binder of a magnetic recording layer is softened so much as to be adhered to the adjacent layer, or the coating film is so aged that the strength is lowered, which is likely to lead to the peel-off of the coating film or dropouts...." The activity of the surfaces of magnetic particles is generally high, so that in a magnetic coating produced from the magnetic particles and a binder resin, the condensation or association of molecules of the solvent which come into contact with the surfaces of the magnetic particles is caused, thereby raising the boiling point of the solvent in the magnetic coating and making the vaporization of solvent in the magnetic coating difficult. The lowering of the strength of the coating film is caused by a large amount of residual solvent in the magnetic film. Even after the magnetic coating is oriented and dried during the production of a magnetic tape, the solvent which cannot evaporate remains in the magnetic coating film, so that the magnetic layer is plasticized and softened, which influences the physical properties of the coating film. The amount of residual solvent on the surface of magnetic particles was not less than 2.0 % (calculated as C), when the surfaces of the magnetic particles were not coated with any of the above-described compounds in accordance with the known methods. Secondly, in a magnetic tape produced from magnetic particles, the mechanical strength is sometimes lowered or the increase of the friction coefficient sometimes causes a trouble. This fact is described, for example, at p. 169 of Causes for Friction and Abrasion between Magnetic Tape and Magnetic Head and Countermeasure for Troubles (1987), published by the publication department of Technologic Information Center, ".... The higher the surface strength (the scratch resistance) of the magnetic layer, the smaller the increase of dropouts with respect to the frequency of use....", and ".... In a magnetic recording system, the magnetic tape runs in contact with the head and the fixed guides. The friction coefficient of the magnetic tape and the contacting portion of the recording machine directly influences the running property of the magnetic tape...." In order to improve the durability and running property of a magnetic tape, abrasives and lubricants are generally added during the production of the magnetic tape. Although the appropriate addition of abrasives and lubricants improves the durability and running property of a magnetic tape, if the amount is too much, such an additive sometimes deteriorates the signal recording property (electromagnetic conversion property) of the magnetic tape or even lowers the durability. The amount of abrasives and lubricants used therefore has its limitation. The present inventors have made an attempt to improve the durability of a magnetic tape while reducing the amount of abrasives and lubricants used by modifying the surfaces of the magnetic particles. Thirdly, the surface resistance of the magnetic tape produced from magnetic materials and a binder resin sometimes increases, causing trouble. This fact is described, for example, at p. 171 of Causes for Friction and Abrasion between Magnetic Tape and Magnetic Head and Countermeasure for Troubles (1987), published by the publication department of Technologic Information Center, ".... When a magnetic tape slides in a recording machine and causes charging, the load drawn from half of the tape is increased, the tape absorbs dust, thereby causing dropouts. Also the tape adheres to the drum in a helical scan system, or the discharge noise (white noise) is caused by discharging. In order to prevent charging, an antistatic agent is added or a material which lowers the surface resistance is selected...." For example, in order to prevent a magnetic tape from charging and to lower the surface resistance, carbon black or the like is generally added during the production of the magnetic tape. Although the addition of an appropriate amount of carbon black or another antistatic agent is effective in preventing charging and the lowering of the surface resistance, too much addition thereof sometimes deteriorates the magnetic properties of the magnetic tape such as the saturation magnetization and the residual magnetization. The amount of antistatic agent added therefore has its limitation. The present inventors have also made an attempt to reduce the surface resistance of a magnetic tape while reducing the amount of used carbon black or another antistatic agent by modifying the surfaces of the magnetic particles. Accordingly, the technical problems to be solved of the present invention are to provide magnetic particles, (A) which have excellent dispersibility and a large parameter a, or (B) which have excellent dispersibility and a large parameter α and (i) which can improve the strength of the coating film of a magnetic recording medium produced therefrom, (ii) which can provide a magnetic recording medium produced therefrom with a high durability by improving the mechanical strength and reducing the friction coefficient, or (iii) which can lower the surface resistance of a magnetic recording medium produced therefrom without impairing the saturation magnetization and the residual magnetization. It is an object of the present invention to provide magnetic particles which have excellent dispersibility and which have a molecular-weight-dependent parameter α of not less than 0.50. It is another object of the present invention to provide magnetic particles which have excellent dispersibility, which have a molecular-weight-dependent parameter α of not less than 0.50 and in which the strength of the coating film of a magnetic recording medium (tape) produced therefrom is improved. It is another object of the present invention to provide magnetic particles which have excellent dispersibility, which have a molecular-weight-dependent parameter α of not less than 0.50 and in which the magnetic recording medium produced therefrom shows a high durability due to improved mechanical strength and reduced friction coefficient. It is another object of the present invention to provide magnetic particles which have excellent dispersibility, which have a molecular-weight-dependent parameter α of not less than 0.50 and in which the surface resistance of the magnetic recording medium produced therefrom is small. Accordingly, the present invention provides magnetic particles suitable for magnetic recording which comprise acicular or plate-like magnetic particles and not less than 0.01 wt% (calculated as Al, SiO 2 or Al and SiO 2 based on the acicular or plate-like magnetic particles) of an oxide or hydroxide of A1 and/or Si adhered to the surfaces of the acicular or plate-like magnetic particles, and which have a value of the molecular-weight-dependent dispersibility parameter α of not less than 0.50, wherein α is defined by formula (I): As = K 1 · M α wherein: M is the number-average molecular weight of a urethane resin binder used in determining the value of α ; As is the saturation adsorption amount of the said binder on the magnetic particles; and K 1 is a constant dependent on the said binder and the mixed solvent of methyl ethyl ketone, toluene and cyclohexane used for measuring As in the determination of the value of α. The present invention also provides a magnetic medium comprising a substrate and a magnetic coating containing magnetic particles according to the invention. Typically the magnetic medium of the invention may have a running durability of 14 to 60 minutes. Typically the magnetic medium may have a surface resistance of not more than 5 x 10 9 Ω/sq. Thus the present invention provides a magnetic medium comprising a substrate and a magnetic coating containing magnetic particles according to the invention, which are applied to said substrate. The present invention additionally provides a process for producing magnetic particles according to the invention which comprises: adding an aqueous alkali solution to an aqueous suspension containing acicular or plate-like magnetic particles to obtain a suspension having a pH of not less than 10; adding an aqueous solution containing A1 or an aqueous solution containing Si, or a mixture thereof to said suspension; adjusting the pH of said suspension to approximately neutrality with stirring to deposit or precipitate an oxide or hydroxide of Al and/or Si on the surface or periphery of the acicular or plate-like magnetic particles; filtering out said acicular or plate-like magnetic particles together with said oxide or hydroxide; washing and drying the obtained solid substance; and compacting and pulverizing said solid substance by an edge runner mill so as to adhere the oxide or hydroxide to the surfaces of said acicular or plate-like magnetic particles. Optionally the steps taken from said step of adding an aqueous alkali solution to said step of compacting and pulverising said solid substance are repeated at least twice. The obtained particles from this process can be subjected to further treatment. Thus the invention also provides a process wherein the obtained particles comprise not less than 0.01 wt% (calculated as Al or SiO 2 or Al and SiO 2 and based on the acicular or plate-like magnetic particles) of the oxide or hydroxide of Al and/or Si adhered to the surfaces of the acicular or plate-like magnetic particles, and have a value of α of not less than 0.50; which process further comprises: adding an aqueous solution to an aqueous suspension containing the magnetic particles to obtain a suspension having a pH of not less than 10: adding an aqueous alkali solution containing at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe to said suspension; adjusting the pH of said suspension to approximately neutrality with stirring to deposit or precipitate an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe on the surface or periphery of the acicular or plate-like magnetic particles; filtering out said acicular or plate-like magnetic particles together with said further oxide or hydroxide; washing and drying the obtained solid substance; and compacting and pulverising said solid substance by an edge runner mill so as to adhere the further oxide or hydroxide to the particles. or Alternatively the aqueous solution containing Al or Si or Al and Si may further comprise at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe; and an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe is precipitated or deposited, filtered out, washed and dried and adhered with the oxide or hydroxide of Al and/or Si. Another alternative is that the acicular or plate-like magnetic particles used as the starting material have been obtained by: adding an aqueous alkali solution to an aqueous suspension containing acicular or plate-like magnetic particles to obtain a suspension having a pH of not less than 10; adding an aqueous solution containing at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe to said suspension; adjusting the pH of said suspension to approximately neutrality with stirring to precipitate an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe on the surface or periphery of the acicular or plate-like magnetic particles; filtering out said acicular or plate-like magnetic particles together with said oxide or hydroxide; washing and drying the obtained solid substance; and compacting and pulverising said solid substance by an edge runner mill so as to adhere the oxide or hydroxide to the particles; thereby obtaining particles which comprise not less than 0.01 wt% (calculated as Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe and based on the acicular or plate-like magnetic particles) of the oxide or hydroxide adhered to the surfaces of the acicular or plate-like magnetic particles. As Examples of magnetic particles which can be used as a raw material in the present invention are acicular magnetic iron oxide particles such as acicular maghemite particles, acicular magnetite particles, acicular berthollide compound particles which are an intermediate oxide between maghemite particles and magnetite particles; acicular particles in which a metal such as Co, etc. other than Fe is contained the above-mentioned acicular magnetic iron oxide particles; acicular particles in which Co is coated on the surface of the above-mentioned acicular magnetic iron oxide particles; acicular magnetic metal particles containing iron as the main ingredient; and fine hexagonal ferrite particles such as fine plate-like Ba ferrite particles, fine plate-like Sr ferrite particles and fine plate-like Ba-Sr ferrite particles. The hexagonal ferrite particles having an average particle diameter (average face size) of 0.01 to 1 µm, preferably 0.01 to 0.3, more preferably 0.05 to 0.2 µm and a plate ratio (average particle diameter/lamellar thickness) of 2 to 20, preferably 3 to 10, more preferably 3 to 7, and the acicular magnetic iron oxide particles having an average major axial diameter of 0.05 to 0.35 µm, preferably 0.1 to 0.25 µm and an aspect ratio (average major axial diameter/average minor axial diameter) of 3 to 20, preferably 5 to 10 are preferred as a raw material. In the present invention, after the pH of an aqueous suspension containing magnetic particles is adjusted to not less than 10 by adding an aqueous alkali solution thereto, an aqueous solution of an Al compound, an aqueous solution of an Si compound or a mixture thereof to the resultant suspension. This is because it is possible to uniformly mix the above-described compound added with the magnetic particles by dispersing the magnetic particles in the suspension without precipitating the compound as a hydroxide. For adjusting the pH of the suspension to not less than 10, aqueous solutions of sodium hydroxide, potassium hydroxide, ammonia and the like are usable. As the aqueous solution containing Al, an aqueous solution of an alkali aluminate such as sodium aluminate and potassium aluminate, and an aqueous solution of an aluminum salt such as aluminum sulfate, aluminum chloride and aluminum nitrate are usable. The amount of Al compound added is not less than 0.01 wt%, preferably 0.01 to 5.0 wt% (calculated as Al) based on the magnetic particles as a raw material. If the amount is less than 0.01 wt%, the advantages aimed at in the present invention are not obtained. Although these advantages are obtained even if the amount exceeds 5.0 wt%, the increase in the amount of oxide or hydroxide containing Al, which does not contribute to the magnetism, sometimes lowers the saturation magnetization. With due consideration for the dispersibility and the saturation magnetization of the magnetic particles, the amount of Al compound added is more preferably 0.05 to 3.0 wt%. As the aqueous solution containing Si, aqueous solutions of sodium silicate, potassium silicate, colloidal silica, water glass No. 3 and the like are usable. The amount of Si compound added is not less than 0.01 wt%, preferably 0.01 to 5.0 wt% (calculated as SiO 2 ) based on the magnetic particles as a raw material. If the amount is less than 0.01 wt%, the advantages aimed at in the present invention are not obtained. Although these advantages are obtained even if the amount exceeds 5.0 wt%, the increase in the amount of oxide or hydroxide of Si which does not contribute to the magnetism, sometimes lowers the saturation magnetization. With due consideration for the dispersibility and the saturation magnetization of the magnetic particles, the amount of Si compound added is more preferably 0.1 to 2.0 wt%. When a mixture of an aqueous solution containing Al and an aqueous solution containing Si is added to the suspension in the present invention, the amount of Al and/or Si in the mixed solution added is not less than 0.01 wt%, preferably 0.01 to 5.0 wt%, more preferably 0.1 to 3.0 wt% (calculated as the total amount of Al and SiO 2 ) based on the magnetic particles as a raw material. If the process of adhering an oxide or hydroxide of Al and/or Si to the surfaces of the material magnetic particles is repeated not less than twice, that is, the steps taken from the step of adding an aqueous alkali solution to an aqueous suspension containing acicular or plate-like magnetic particles to obtain a suspension having a pH of not less than 10 to the step of the compaction and pulverization by an edge runner mill are repeated at least twice, preferably two to five times, the amount of Al compound added each time is 0.01 to 5.0 wt%, preferably 0.05 to 3.0 wt% (calculated as Al) based on the magnetic particles as a raw material, the amount of Si compound added each time is 0.01 wt% to 5.0 wt%, preferably 0.1 to 2.0 wt% (calculated as SiO 2 ) based on the magnetic particles as a raw material, and the amount of Al compound and Si compound added each time is not less than 0.01 to 5.0 wt%, preferably 0.05 to 3.0 wt% (calculated as the total amount of Al and SiO 2 ) based on the magnetic particles as a raw material. In this case, the total amount of Al compound and Si compound added in the whole process is 0.01 to 10.0 wt%, preferably 0.05 to 5.0 wt% (calculated as the total amount of Al and SiO 2 ) based on the magnetic particles as a raw material. In the present invention, it is possible to add an aqueous solution at least one compound of an element selected from Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe. As such a compound, a water-soluble salt of each element such as a sulfate, a chloride, a nitrate and an acetate thereof-is usable. The amount of such compound added is 0.01 to 5.0 wt% (calculated as each element) based on the magnetic particles. If the amount is less than 0.01 wt%, it is difficult to obtain the advantages aimed at in the present invention. Although these advantages are obtained even if the amount exceeds 5.0 wt%, the increase in the amount of oxide or hydroxide, which does not contribute to the magnetism, sometimes lowers the saturation magnetization. With due consideration for the dispersibility and the saturation magnetization of the magnetic particles, the amount of such compound added is preferably 0.05 to 3.0 wt%. In order to adequately and uniformly mix the compound in the suspension of the magnetic particles having a pH of not less than 10, the above-described compound is added in the form of an aqueous solution. It is also possible to adequately dissolve and mix each compound into the suspension by adding in the form of a crystal salt. In the present invention, an aqueous solution of the above-described compound is added to the suspension of the magnetic particles having a pH of not less than 10, and the pH of the suspension is rapidly adjusted to approximately neutrality (pH of 6.5 to 8.5) under stirring so as to quickly precipitate substantially the total amount of Al, Si, Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd or Fe as an oxide or hydroxide thereof and produce a substance composed of the magnetic particles and the oxide or hydroxide thereof. The time for adjusting the pH of the suspension and for precipitating an oxide or hydroxide containing each element in the suspension is in the range of not more than 10 minutes, preferably 1 to 10 minutes, more preferably 1 to 9 minutes, still more preferably 1 to 8 minutes. If the time exceeds 10 minutes, the oxide or hydroxide containing each element is sometimes precipitated on the surfaces of the magnetic particles in layers. After the precipitation of the oxide or hydroxide thereof, the thus-obtained solid substance composed of the magnetic particles as a raw material and the oxide or hydroxide thereof is filtered out under the normal conditions by an ordinary method. As the acid for adjusting the pH of the suspension, sulfuric acid, hydrochloric acid, acetic acid, nitric acid, carbon dioxide gas, etc. are usable. Among the above-described elements, Ca, Sr and Ba sometimes elute when substantially the total amount of precipitated oxide or hydroxides thereof are washed. To prevent this, they are preferably subjected to the following treatments. When a Ca compound is used and the suspension containing the Ca compound is neutralized with any of the above-described acids other than carbon dioxide gas, after the pH of the suspension is adjusted, a slight amount of carbon dioxide gas is further blown into the suspension so as to bubble it. By this treatment, Ca ions are combined with carbon dioxide gas as CaCO 3 , so that Ca is unlikely to elute. The same treatment may be adopted when an Sr compound is used so that Sr ions are combined with carbon dioxide gas as SrCO 3 and Sr is unlikely to elute. When a Ba compound is used, the suspension containing the Ba compound is preferably neutralized with sulfuric acid. When an acid other than sulfuric acid is used as the neutralizer, it is preferable to add sulfuric acid after the adjustment of the pH so as to combine Ba ions therewith as BaSO 4 , whereby Ba ions are unlikely to elute. The thus-obtained solid substance composed of the magnetic particles and the oxide or hydroxide is washed and dried by an ordinary method. As the edge runner mill used for the compaction and pulverization of the solid obtained substance in the present invention, "Sand Mill" manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho and "Mix Muller" manufactured by Shinto Industry Co., Ltd., etc. are usable. The line load of the edge runner mill is 15 to 80 kg/cm, preferably 30 to 60 kg/cm. If the line load is less than 15 kg/cm, since the shearing force during grinding is too weak, it is impossible to exert the mechanochemical effect. On the other hand, if the line load exceeds 80 kg/cm, there is a fear of the particles themselves being broken. The treating time is 15 to 120 minutes, preferably 30 to 60 minutes. In the present invention, the steps taken from the step of adding an aqueous alkali solution to an aqueous suspension containing acicular or plate-like magnetic particles to obtain a suspension having a pH of not less than 10 to the step of the compaction and pulverization of the solid substance composed of the magnetic particles and the oxide or hydroxide by an edge runner mill may be repeated not less than twice, preferably two to five times. Although the advantages aimed at in the present invention are obtained even if they are repeated more than five times, the advantages are approximately fully achieved the repeating treatment of not less than 6 times is not industrial. As regards the magnetic particles of the present invention, preferably 0.01 to 10 wt%, more preferably 0.05 to 5.0 wt% and still more preferably 0.1 to 3.0 wt% (calculated as Al, SiO 2 or Al and SiO 2 based on the acicular or plate-like magnetic particles) of the oxide or hydroxide of Al and/or Si is adhered to the surfaces of the acicular or plate-like magnetic particles. The molecular-weight-dependent parameter α has a value of not less than 0.5, preferably not less than 0.53, more preferably not less than 0.55. Typically the said plate-like magnetic particles are hexagonal ferrite particles. Typically the said acicular or plate-like magnetic particles are Co-coated magnetic particles. The said acicular or plate-like magnetic particles can further comprise an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe adhered to the surfaces of said particles. The amount of said further oxide or hydroxide is generally not less than 0.01 wt% (calculated as each element) based on said acicular or plate-like magnetic particles. The further oxide or hydroxide may be an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba and P and the amount of residual solvent in said magnetic particles is less than 2.0 wt% (calculated as C). In that event, generally not less than 0.01 wt% (calculated as Zn, Ni, Mg, Ca, Sr, Ba and P based on the acicular or plate-like magnetic particles), preferably 0.01 to 5.0 wt% and more preferably 0.05 to 3.0 wt%, of the oxide or hydroxide containing at least one of Zn, Ni, Mg, Ca, Sr, Ba and P is adhered to the surfaces of the thus-obtained magnetic particles. The invention includes magnetic particles wherein the further oxide or hydroxide is an oxide or hydroxide of at least one of Zr, Ti, Hf and Mo. Typically, not less than 0.01 wt% (calculated as Zr, Ti, Hf and Mo based on the acicular or plate-like magnetic particles), preferably 0.01 to 5.0 wt% and more preferably 0.05 to 3.0 wt%, of the oxide or hydroxide containing at least one of Zr, Ti, Hf and Mo is adhered to the surfaces of the magnetic particles. The invention includes magnetic particles wherein the further oxide or hydroxide is an oxide or hydroxide of at least one of Sn, Sb, Pd and Fe. Not less than 0.01 wt% (calculated as Sn, Sb, Pd and Fe based on the acicular or plate-like magnetic particles), preferably 0.01 to 5.0 wt% and more preferably 0.1 to 3.0 wt% of the oxide or hydroxide containing at least one of Sn, Sb, Pd and Fe can then be adhered to the surfaces of the magnetic particles. The "hydroxide" used in the present invention means hydrated hydroxide, hydrated oxide, and an intermediate of the hydrated hydroxide and the hydrated oxide, such as hydrated oxyhydroxide and the like. In the present invention, magnetic particles having about 0.50 to 0.80 of the parameter α, produced from hexagonal ferrite particles; magnetic particles having about 0.50 to 0.80 of the parameter α, produced from Co-coated magnetic iron oxide particles; and magnetic particles having about 0.50 to 0.80 of the parameter α, produced from magnetic iron oxide particles such as maghemite particles, magnetite particles, or berthollide compound particles which are an intermediate oxide between maghemite particles and magnetite particles can be obtained. The parameter α of the magnetic particles coated with an Si compound and/or an Al compound by the method described in, for example, JP-A-55-83207 (1980), JP-A-57-56904 (1982), JP-A-58-161725 (1983), JP-A-59-23505 (1984), JP-A-60-217529 (1985), JP-A-61-63921 (1986), JP-A-62-89226 (1987) and JP-A-63-161522 (1988) is as low as about 0.40 to 0.45. It has been considered by the present inventors that this is because the surfaces of magnetic iron oxide particles are uniformly coated with an oxide or hydroxide of Al and/or Si which is precipitated in a comparatively long time, so that when these particles are dispersed in a polymer, the number of polymer adsorption sites on the surfaces of the magnetic particles is small. The parameter α of the magnetic particles coated with an Si compound and an Al compound, or a compound containing at least one of Cu, Ag, Ti, Zr, Sn, V, Nb, Ta, Sb, Cr, W, Ni and Mo by the method described in, for example, JP-A-58-60506 (1983), JP-A-59-103310 (1984), JP-A-63-303817 (1988) and JP-A-2-280301 (1990) is as low as about 0.40 to 0.45. It has been considered by the present inventors that this is because the surfaces of magnetic iron oxide particles are uniformly coated with a hydroxide containing at least one Cu, Ag, Ti, Zr, Sn, V, Nb, Ta, Sb, Cr, W, Ni and Mo which is precipitated in a comparatively long time, so that when these particles are dispersed in a polymer, the number of polymer adsorption sites on the surfaces of the magnetic particles is small. For this reason, a method of increasing the polymer adsorption sites on the surfaces of magnetic particles as much as possible so as to increase the thickness of the polymer adsorption layer was investigated. It has been considered by the present inventors that it was necessary to chemically and firmly adsorb the ultrafine particles of an oxide or hydroxide of Al, and/or Si and/or a compound of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe to the surfaces of the magnetic particles as much as possible. When the ultrafine particles of (i) an oxide or hydroxide of Al, and/or Si, (ii) an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba and P, (iii) an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Zr, Ti, Hf and Mo, or (iv) an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Sn, Sb, Pd and Fe were uniformly deposited and/or precipitated in a suspension containing magnetic particles, uniformly mixed with the magnetic particles and the obtained solid substance was compacted and pulverized, the ultrafine particles composed of (i) an oxide or hydroxide of Al and/or Si, (ii) an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba and P, (iii) an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Zr, Ti, Hf and Mo, or (iv) an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Sn, Sb, Pd and Fe were respectively adhered to the surfaces of the magnetic particles due to the mechanochemical effect, so that the parameter α of the magnetic particles was as large as not less than 0.50. This is considered to be because the number of polymer adsorption sites on the surfaces of the magnetic particles was increased. This effect was further improved by repeating the steps of the precipitation of the oxide or hydroxide (i), (ii), (iii) or (iv), and the compaction and pulverization of the solid substance composed of the oxide or hydroxide and the magnetic particles as a raw material at least twice. This is considered to be because the repetition makes the adherence of the ultrafine particles of the oxide or hydroxide to the surfaces of the magnetic particles more firm and secure, and increases the number of polymer adsorption sites on the surfaces of the magnetic particles, so that a larger parameter α is obtained. The magnetic recording medium according to the present invention is obtained by applying a coating composition containing a binder resin and the magnetic particles of the present invention to a substrate by a conventional method to form a magnetic recording layer on the substrate. The amount of magnetic particles in the magnetic recording layer is 60 to 90 wt%, preferably 65 to 85 wt%. The amount of binder in the magnetic recording layer is 10 to 40 wt%, preferably 15 to 35 wt% and the amount of additives therein is not more than 30 wt%. The coating composition may contain additives which are usually used, such as lubricants, abrasives and antistatic agent. As the binder resin in the present invention, the resins which are ordinarily used in the production of a magnetic recording medium are used, for example, vinyl chloride-vinyl acetate copolymer, polyurethane, vinyl chloride-vinyl acetate-maleic acid urethane elastomer, butadieneacrylonitrile copolymer, polyvinyl butyral, cellulose derivatives such as nitrocellulose, polyester, synthetic rubber resins such as polybutadiene, epoxy resins and acrylic urethane resins, and mixtures thereof. As the substrate, the materials which are ordinarily used in the production of a magnetic recording medium are usable, for example, the films of synthetic resins such as polyethylene terephthalate, polyethylenes, polyproplylenes, plycarbonates, polyethylene naphthalates, polyamides, polyamide-imides, polyimides and polysulfones, the foils or the plates of metals such as aluminum and stainless steel, and various kinds of paper. The thickness of the magnetic recording layer of the present invention is 0.1 to 20 µm, preferably 0.1 to 7 µm, more preferably 0.5 to 7 µm. When a magnetic recording medium is produced by coating a non-magnetic substrate with a coating composition composed of the magnetic particles obtained by adhering the ultrafine particles of an oxide or hydroxide of Al and/or Si and an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba and P and a binder resin, and drying the coated material, not only do the magnetic particles have a high affinity for the binder resin and improved dispersibility but also the surface activity of the magnetic particles is improved in the coating film formed by applying the coating composition to the substrate and curing the applied composition, so that the amount of solvent modified on the surfaces of the magnetic particles is so small and, hence, the amount of solvent remaining on the surfaces of the magnetic particles or in the coating film after the coating film is dried is so small that the coating film is unlikely to be plasticized, whereby the strength and the durability of the magnetic recording medium are improved. However, it has been found from many experiments made by the present inventors over a long time that while the amount of residual solvent in the magnetic particles in the present invention produced by adhering the ultrafine particles of an oxide or hydroxide of Al and/or Si and an oxide or hydroxide at least one of Sn, Ni, Mg, Ca, Sr, Ba, and P is as small as less than 2.0 % calculated as C, the amount of residual solvent of magnetic particles without any addition of the above-described compound is not less than 2.0 %. When a magnetic recording medium is produced by coating a non-magnetic substrate with a coating composition composed of the magnetic particles obtained by adhering the ultrafine particles of an oxide or hydroxide of Al, and/or Si and an oxide or hydroxide of at least one of Zr, Ti, Hf and Mo and a binder resin, and drying the coated material, the magnetic particles do not only have a high affinity for the binder resin and improved dispersibility but are also capable of enhancing the mechanical strength (scratch resistance) of the coating film and reducing the friction coefficient thereof. As a result, the magnetic recording medium is excellent in running durability. This means that it is possible to produce a highly practical magnetic recording medium from the magnetic particles of the present invention. This is a result of the attempt of the present inventors to improve the durability of a magnetic tape while reducing the amount of abrasives and lubricants used by modifying the surfaces of the magnetic particles, as described above. The relationship between magnetic particles and the durability of the magnetic tape produced therefrom has been investigated, and it was found that the properties of the surfaces of the magnetic particles greatly influence the durability of the magnetic tape produced therefrom. Since the properties of the surfaces of the magnetic particles exposed on the surface of the outermost layer of a magnetic tape influence the scratch resistance and the wear characteristics of the magnetic tape, it is considered that the existence of an oxide or hydroxide of Al, and/or Si and an oxide or hydroxide of at least one of Zr, Ti, Hf and Mo on the surfaces of the magnetic particles of the present invention improves the scratch resistance of the magnetic tape with respect to a magnetic head, and such an oxide or hydroxide also functions as a solid lubricant, which lowers the friction coefficient of the magnetic tape, so that excellent running durability is obtained. When a magnetic recording medium is produced by coating a non-magnetic substrate with a coating composition composed of the magnetic particles obtained by adhering the ultrafine particles of an oxide or hydroxide of Al, and/or Si and an oxide or hydroxide of at least one of Sn, Sb, Pd and Fe and a binder resin, and drying the coated material, the magnetic particles not only have a high affinity for the binder resin and improved dispersibility but are also capable of lowering the surface resistance without impairing the saturation magnetization and the residual magnetization. This is a result of the attempt of the present inventors to reduce the surface resistance of a magnetic tape without impairing the saturation magnetization and the residual magnetization, while reducing the amount of carbon black or another antistatic agent used by modifying the surfaces of the magnetic particles, as described above. The relationship between magnetic particles and the surface resistance of the magnetic tape produced therefrom has been investigated and it has been found that the surfaces of the magnetic particles greatly influence the surface resistance of the magnetic tape produced therefrom. Since the properties of the surfaces of the magnetic particles exposed on the surface of the outermost layer of a magnetic tape influence the surface resistance and the charging property of the magnetic tape, it is considered that the existence of an oxide or hydroxide of Al, and/or Si and an oxide or hydroxide of at least one of Sn, Sb, Pd and Fe on the surfaces of the magnetic particles of the present invention reduces the surface resistance of the magnetic tape to not more than 5 x 10 9 Ω/sq. and improves the charging property of the magnetic tape and the sliding portions of a recording machine. The solid substance is composed of the magnetic particles used as a raw material and the oxide or hydroxide on their surface. The particles and oxide or hydroxide are bound so that the filtration, washing, and drying of the solid substance are carried out by an ordinary method without particularly deteriorating the operability. However, the effect of the present invention is not attained by a method of adding a dispersant to a slurry of magnetic iron oxide particles and mechanically shearing the particles, as shown in JP-A-55-157216 (1980) or by a method of adding a silane coupling agent to magnetic particles and mixing in a dry process, as shown in JP-A-2-188429 (1990). The magnetic recording medium of the present invention has a surface gloss of 150 to 200 %, preferably 152 to 200 %; a surface roughness of 3 to 9.2 nm, preferably 3 to 9.0 nm; Young's modulus (relative value) of 95 to 130, preferably 100 to 130 (in plate-like particles); Young's modulus (relative value) of 125 to 150, preferably 130 to 150 (in acicular particles); a friction coefficient of 0.20 to 0.35, preferably 0.20 to 0.30 (in plate-like particles); a friction coefficient of 0.15 to 0.25 (in acicular particles); a running durability of 14 to 60 minutes, preferably 16 to 60 minutes; a surface resistance of 2x10 8 to 5 x 10 9 Ω/sq; and an amount of residual solvent of 0.1 to 1.8 wt%, preferably 0.1 to 1.6 wt%. The magnetic particles of the present invention are excellent in dispersibility, so that they are suitable as magnetic particles for high-density recording. When a magnetic recording medium is produced from the magnetic particles of the present invention, since the surface activity of magnetic particles is improved, the amount of solvent remaining in the magnetic particles contained in the coating film after the coating film is dried is small, thereby improving the strength and the durability of the magnetic recording medium. In addition, since the mechanical strength (scratch resistance) is improved and the friction coefficient is reduced, the running durability of the magnetic recording medium is excellent. Furthermore, since the magnetic particles have a high affinity for the binder resin and excellent dispersibility , the surface smoothness of the magnetic recording medium is excellent. Since it is possible to reduce the surface resistance of the magnetic recording medium, the charging property is so excellent so as to reduce the number of dropouts and suppress the sticking of the magnetic recording medium to a recording machine. In this way, the magnetic recording medium is excellent. Examples The present invention will now be described in more detail with reference to the following examples, but the present invention is not restricted to those examples and various modifications are possible within the scope of the invention. The properties in the examples were measured by the following methods. (1) Dispersibility The dispersibility was evaluated by the molecular-weight-dependent parameter α in the formula (I): As = K 1 · M α The closer the parameter α to 1, the more excellent the dispersibility. In the present invention, it is necessary that α ≥ 0.5. Binder solutions of not less than three kinds, preferably 5 to 6 kinds having different resin concentrations within the range of 0.01 to 5 % were obtained by adding and dissolving resin binders having different molecular weight, that is, (i) a urethane resin having a number-average molecular weight of 15,000, (ii) a urethane resin having a number-average molecular weight of 28,000 and (iii) a urethane resin having a number-average molecular weight of 42,000 into a mixed solvent of methyl ethyl ketone, toluene and cyclohexane (weight ratio: 5:3:2), respectively. The resin concentration of each binder solution prepared was measured by a weight method and was assumed to be an initial resin concentration Ci. To 56 g of each binder resin prepared, 20 g of magnetic particles were added and resultant solution was uniformly dispersed to form a magnetic coating composition until the adsorbed resin concentration on the surface of the magnetic particles and a resin concentration in the binder solution reached equilibrium. The obtained magnetic coating composition was subjected to centrifugal separation at a rate of 10,000 rpm for 25 minutes by using a centrifugal separator (manufactured by Kokusan Enshinki Kabushiki Kaisha). After attaining equilibrium between a supernatant liquid and a precipitated substance, the precipitated substance was removed therefrom and the equilibrated binder concentration C of the obtained supernatant liquid was determined by a weight method. The difference obtained by subtracting the binder concentration C of the supernatant liquid from the initial resin concentration Ci is assumed to be an apparent resin-adsorption A of the magnetic particles. The binder concentration C and the apparent resin-adsorption A of each binder solution having different concentration was measured by the same method described above. The obtained values were plotted on a graph, the ordinate being the ratio (C/A) of the binder concentration C to the apparent resin adsorption A and the abscissa being the binder concentration C, thereby obtaining a linear relationship therebetween. The inclination of the obtained straight-line in the graph corresponds to 1/As in the following Langmuir induction formula. C/A = (1/As) x C + (1/As·K 2 ) C: Equilibrated binder concentration of the supernatant liquid A: Apparent resin-adsorption As: Saturation adsorption K 2 : Constant Accordingly, the saturation adsorption As was obtained from the above-mentioned Langmuir induction formula. The saturation adsorption As and the molecular weight M of the binder were plotted in a log-log table so as to obtain the linear relationship between As and M. The molecular weight-dependent parameter α was obtained from the inclination of the straight line. (2) Amount of coating element The amount of element of the Al, Si, Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd or Fe compound with which the magnetic particles were coated, was measured by fluorescent X-ray analysis. (3) Magnetic properties The magnetic properties of the magnetic particles were measured by using "Vibration Sample Magnetometer VSM-3S-15", manufactured by Toei Kogyo Kabushiki Kaisha and applying an external magnetic field of 10 kOe (5 kOe when magnetic iron oxide particles were used). The magnetic properties of the magnetic recording medium were measured by applying an external magnetic field of 10 kOe (5 kOe when Co-coated magnetic iron oxide particles or magnetic iron oxide particles were used). (4) Amount of residual solvent After a sample was adequately immersed in cyclohexanone, it was dried at a temperature of 60°C for 24 hours. The carbon content C in the sample was obtained by quantitative analysis by "Carbon/Sulfur Analyzer EMIA-2200" (manufactured by Kabushiki Kaisha Horiba Seisakysho). A smaller carbon content C, corresponds to a smaller amount of residual solvent which is preferable because the interaction between the sample and the solvent is less strong. (5) Surface Gloss The surface gloss of the coating film was measured by "UGV-5D" (manufactured by Suga Testing Machine Kabushiki Kaisha) at an incident angle of 45°. The value was expressed as a percentage assuming that the standard plate glossiness was 86.3%. (6) Surface roughness The surface roughness Ra was expressed by the center line-average roughness of the coating film measured by "Surfcom-575A" (manufactured by Tokyo Seimitsu Co., Ltd.) (7) Strength of coating film The strength of the coating film was expressed by the Young's modulus obtained by using "Autograph" (manufactured by Shimazu Seisakusho Ltd.) The Young's modulus was expressed by the ratio of the Young's modulus of the coating film to that of a commercially available video tape "AV T-120 (manufactured by JVC Corp.). The higher the relative value, the more favorable. (8) Friction coefficient of coating film The friction coefficient of the coating film was expressed by the friction coefficient between the coating surface and the base film (substrate) obtained from the relationship between the tensile stress and the load. The lower the friction coefficient, the more slippery the coating film is. (9) Running durability The running durability was evaluated by the operating time under the conditions that the load was 200 gw and the relative speed of the head and the tape was 16 m/s by using "Media Durability Tester MDT-3000" (manufactured by Steinberg Associates Corp.). The longer the operating time, the higher the running durability. (10) Scratch resistance The surface of the magnetic tape after running was observed and the degree of scratching was visually judged. Evaluation was divided into the following four ranks. A: No scratch B: A few scratches C: Many scratches D: Great many scratches In the present invention, the evaluation is required to be A or B. (11) Surface resistance After the coating film was exposed to an atmosphere of 25°C and 60% RH for not less than 12 hours, it was slit into a width of 6 mm. The test piece was placed on metal electrodes of 6.5 mm wide. A weight of 170 g was attached to both ends of the test piece so as to be brought into close contact with the electrodes. A DC voltage of 500 V was applied between the electrodes to measure the surface resistance of the coating film. <Surface treatment of magnetic particles> Examples 1 to 7 Example 1 6 kg of plate-like Co- and Ti-substituted Ba ferrite particles having an average particle diameter of 0.05 µm, a plate ratio (average particle diameter/lamellar thickness) of 5.0 and a coercive force of 736 Oe was mixed with water, and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture until a pH of the mixed suspension came into 11.4. After the mixed suspension was stirred, 2220 ml (equivalent to 0.5 wt% of the magnetic particles (calculated as Al)) of an aqueous sodium aluminate of 0.5 mol/l was added to the resultant suspension, and the mixed suspension was stirred. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.0. The time taken for the adjustment was 8 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 5 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 60 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio was 5.0, the coercive force was 736 Oe, and the parameter α was 0.59. Examples 2 to 7 Magnetic particles were produced in the same procedure as in Example 1 except for varying the kind of magnetic particles as a raw material, the kind and the amount of compound added, the time taken to add the compound, the stirring time and the line load and the time for the compaction and pulverization. The main producing conditions and various properties of the product in each example are shown in Tables 1 and 2. <Production of magnetic tape> Examples 8 to 14 Example 8 The magnetic particles obtained in Example 1 were first mixed with a binder resin and a solvent so that the solid content was 76 wt%, and the mixture was kneaded for 30 minutes by a PLASTI-CORDER (manufactured by Brabender Corp.). Thereafter, a predetermined amount of kneaded product was taken out and charged into a glass bottle together with abrasive carbon black, glass beads and a solvent. The mixture was mixed and dispersed for 6 hours by a paint conditioner. Lubricants and a hardening agent were further added to the mixture, and the resultant mixture was mixed and dispersed for 15 minutes. The final composition of the magnetic paint obtained was as follows: Magnetic particles 100 parts by weight Vinyl chloride-vinyl acetate copolymer resin having a sodium sulfonate group 10 parts by weight Polyurethane resin having a sodium sulfonate group 10 parts by weight Abrasives 10 parts by weight Carbon black 3 parts by weight Lubricants 2.5 parts by weight Hardening agent 5 parts by weight Cyclohexanone 52.5 parts by weight Methyl ethyl ketone 130.5 parts by weight Toluene 78.3 parts by weight The magnetic paint obtained was applied to a polyethylene terephthalate film having a thickness of 14 µm to a thickness of 40 µm by using an applicator, and dried to obtain a sheet-like sample. The sheet-like sample was calendered, and hardened at 60 °C for 24 hours. The sample was then slit to a width of 0.5 inch to produce a magnetic tape. The coercive force Hc of the magnetic tape produced was 780 Oe, the squareness was 0.83, the gloss was 186 %, and the surface roughness Ra was 6.0 nm. Examples 9 to 14 Magnetic tapes were produced in the same procedure as in Example 8 except for using the magnetic particles obtained in Examples 2 to 7. Various properties of the products are shown in Table 3. Example 15 6 kg of plate-like Co- and Ti-substituted Ba ferrite particles having an average particle diameter of 0.05 µm, a plate ratio (average particle diameter/lamellar thickness) of 5.0 and a coercive force of 736 Oe was mixed with water and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l mixture was added to the mixture until a pH of the mixed suspension came into 11.4. After the mixed suspension was stirred, 2220 ml (equivalent to 0.5 wt% of the magnetic particles (calculated as Al)) of an aqueous sodium aluminate of 0.5 mol/l was added to the suspension and the mixed suspension was stirred. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.0. The time taken for the adjustment was 8 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 5 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2 " (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho) and compacted and pulverized for 60 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 736 Oe, and the parameter α was 0.59. 4.5 kg of the thus-obtained magnetic particles were mixed with water again, and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture until a pH of a mixed suspension came into 10.8. After the mixed suspension was stirred, 77.9 g (equivalent to 0.5 wt% of the magnetic particles (calculated as SiO 2 )) of water glass No. 3 was added to the suspension, and the mixed suspension was stirred. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 6.5. The time taken for the adjustment was 6 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 4 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 60 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 742 Oe, and the parameter α was 0.65. Examples 16 to 21 Magnetic particles were produced in the same procedure as in Example 15 except for varying the kind of magnetic particles as a raw material, the kind and the amount of compound added, the time taken to add the compound, the stirring time, the line load and the time for the compaction and pulverization and the number of cycles of treatments. As the material magnetic particles, the particles used in Examples 2 to 7 shown in Table 1 were used in Examples 16 to 21, respectively. The main producing conditions and various properties of the product in each example are shown in Tables 4 to 6. Examples 22 to 28 Magnetic tapes were produced in the same procedure as in Example 8 except for using the magnetic particles obtained in Examples 15 to 21. Various properties of the products are shown in Table 7. Example 29 6 kg of plate-like Co- and Ti-substituted Ba ferrite particles having an average particle diameter of 0.05 µm, a plate ratio (average particle diameter/lamellar thickness) of 5.0 and a coercive force of 736 Oe was mixed with water, and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture until a pH of a mixed suspension came into 11.4. After the mixed suspension was stirred, 4440 ml (equivalent to 1.0 wt% of the magnetic particles calculated as Al) of an aqueous sodium aluminate of 0.5 mol/l was added to the suspension and the mixed suspension was stirred. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.5. The time taken for the adjustment was 6 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 5 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 60 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, and coercive force was 740 Oe, and the parameter α was 0.60. After 4.5 kg of the thus-obtained magnetic particles were mixed with water again and the mixture was stirred, an aqueous solution of NaOH of 0.1 mol/litre was added to the mixture until a pH of a mixed suspension came into 11.0. Thereafter, 1380 ml (equivalent to 1.0 wt% of the magnetic particles (calculated as Zn)) of an aqueous solution of zinc sulfide of 0.5 mol/l was added to the mixture to obtain a suspension. While stirring the suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.5. The time taken for the adjustment was 4 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 4 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha. Matsumoto Chuzo Tekkosho), and compacted and pulverized for 60 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 753 Oe, the parameter α was 0.63, and the amount of residual solvent was 1.11 wt%. Examples 30 to 36 Magnetic particles were produced in the same procedure as in Example 29 except for varying the kind of magnetic particles as a raw material, the kind and the amount of compound added, the time taken to add the compound, the stirring time, the line load and the time for the compaction and pulverization and the number of cycles of treatments. The main producing conditions and various properties of the product in each example are shown in Tables 8 to 10. Examples 37 to 44 Magnetic tapes were produced in the same procedure as in Example 8 except for using the magnetic particles obtained in Examples 29 to 36. Various properties of the products are shown in Table 11. Example 45 6 kg of plate-like Co- and Ti-substituted Ba ferrite particles having an average particle diameter of 0.05 µm, a plate ratio (average particle diameter/lamellar thickness) of 5.0 and a coercive force of 736 Oe was mixed with water and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture until the pH of the suspension became 11.4. After the mixed suspension was stirred, 2220 me (equivalent to 0.5 wt% of the magnetic particles (calculated as Al)) of an aqueous sodium aluminate of 0.5 mol/l was added to the suspension, and the mixed suspension was stirred. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.0. The time taken for the adjustment was 5 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 5 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 60 minutes at a line load of 30 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 738 Oe, and the parameter α was 0.57. 4.5 kg of the thus-obtained magnetic particles were mixed with water again, and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture to adjust the pH to 10.5. 2470 ml (equivalent to 2.50 wt% of the magnetic particles (calculated as Zr)) of an aqueous solution of zirconium sulfate was then added to the mixture and stirred to obtain a mixed suspension. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.0. The time taken for the adjustment was 5 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 4 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 60 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 748 Oe, and the parameter α was 0.64. Examples 46 to 52 Magnetic particles were produced in the same procedure as in Example 45 except for varying the kind of magnetic particles as a raw material, the kind and the amount of compound added, the time taken to add the compound, the stirring time, the line load and the time for the compaction and pulverization and the number of cycles of treatments. As the material magnetic particles, the particles used in Examples 29 to 36 shown in Table 8 were used in Examples 46 to 52, respectively. The main producing conditions and various properties of the product in each example are shown in Tables 12 and 13. Examples 53 to 60 Magnetic tapes were produced in the same procedure as in Example 8 except for using the magnetic particles obtained in Examples 45 to 52. Various properties of the products are shown in Table 14. Example 61 6 kg of plate-like Co- and Ti-substituted Ba ferrite particles having an average particle diameter of 0.05 µm, a plate ratio (average particle diameter/lamellar thickness) of 5.0 and a coercive force of 736 Oc was mixed with water, and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture until the pH of the suspension became 12.0. After the mixed suspension was stirred, 889 ml (equivalent to 0.2 wt% of the magnetic particles (calculated as Al)) of an aqueous sodium aluminate of 0.5 mol/l was added to the suspension and the mixed suspension was stirred. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.5. The time taken for the adjustment was 3 minutes. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 5 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 30 minutes at a line load of 6 0 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 740 Oe, and the parameter α was 0.55. 4.5 kg of the thus-obtained magnetic particles were mixed with water again and the mixture was stirred. Thereafter, an aqueous solution of NaOH of 0.1 mol/l was added to the mixture to adjust the pH to 10.3. 1516 ml (equivalent to 2.00 wt% of the magnetic particles calculated as Sn) of an aqueous solution of sodium stannate was then added to the mixture and stirred to obtain a mixed suspension. While stirring the mixed suspension, an aqueous solution of HCl of 0.1 mol/l was added so as to adjust the pH to 7.1. The time taken for the adjustment was 7 minutes'. The precipitate was immediately filtered out, washed with water and dried by an ordinary method to obtain a solid substance. 4 kg of the thus-obtained solid substance were charged into an edge runner mill "MPUV-Model 2" (manufactured by Kabushiki Kaisha Matsumoto Chuzo Tekkosho), and compacted and pulverized for 30 minutes at a line load of 60 kg/cm. The average particle diameter of the magnetic particles obtained was 0.05 µm, the plate ratio (average particle diameter/lamellar thickness) was 5.0, the coercive force was 746 Oe, and the parameter α was 0.60. Examples 62 to 68 Magnetic particles were produced in the same procedure as in Example 61 except for varying the kind of magnetic particles as a raw material, the kind and the amount of compound added, the time taken to add the compound, the stirring time, the line load and the time for the compaction and pulverization and the number of cycles of treatments. As the material magnetic particles, the particles used in Examples 29 to 36 shown in Table 8 were used in Examples 62 to 68, respectively. The main producing conditions and various properties of the product in each example are shown in Tables 15 and 17. Examples 69 to 76 Magnetic tapes were produced in the same procedure as in Example 8 except for using the magnetic particles obtained in Examples 61 to 68. Various properties of the products are shown in Table 18. Comparative Examples 1 to 6 Magnetic particles were produced in the same procedure as in Example 1 except for varying the kind of magnetic particles, the kind and the amount of compound added, the time taken to add the compound, the stirring time, the line load and the time for the compaction and pulverization and the number of cycles of treatments. The main producing conditions and various properties of the product in each comparative example are shown in Tables 19 and 20. Comparative Examples 7 to 12 Magnetic tapes were produced in the same procedure as in Example 8 except for using the magnetic particles obtained in Comparative Examples 1 to 6. Various properties of the products are shown in Table 21. Examples Magnetic particles as raw material Kind Average particle diameter (µm) Plate ratio or aspect ratio (-) Coercive force Hc (Oe) Saturation magnetization σs (emu/g) Example 1 Plate-like Co- and Ti-containing Ba ferrite particles 0.05 5.0 736 59.0 Example 2 ditto 0.05 5.4 825 59.5 Example 3 ditto 0.05 5.4 825 59.5 Example 4 ditto 0.07 5.8 1105 58.9 Example 5 Co-coated γ-Fe 2 O 3 particles 0.18 6.0 765 78.9 Example 6 ditto 0.18 6.0 765 78.9 Example 7 γ-Fe 2 O 3 0.22 7.0 362 73.2 Examples Kind of magnetic Particles as raw material Properties of tape Coercive force (Oe) Residual magnetization Br (Gauss) Squareness (-) Glossiness (%) Surface roughness Ra (nm) Example 8 Example 1 780 1345 0.83 186 6.0 Example 9 Example 2 888 1310 0.83 180 6.0 Example 10 Example 3 890 1286 0.83 182 5.6 Example 11 Example 4 1201 1250 0.81 175 7.6 Example 12 Example 5 821 1421 0.88 171 6.0 Example 13 Example 6 818 1430 0.87 163 8.4 Example 14 Example 7 401 1280 0.88 160 8.8 Examples Magnetic Particles as raw material Properties of tape Coercive force (Oe) Residual magnetization Br (Gauss) Squareness (-) Glossiness (%) Surface roughness Ra (nm) Example 22 Product in Example 15 786 1369 0.85 191 5.6 Example 23 " 16 899 1352 0.86 196 5.4 Example 24 " 17 896 1321 0.84 196 5.4 Example 25 " 18 1212 1296 0.85 185 6.8 Example 26 " 19 823 1440 0.89 176 5.6 Example 27 " 20 816 1462 0.88 169 7.0 Example 28 " 21 396 1315 0.88 165 7.8 Examples Kind of magnetic particles Properties of tape Coercive force Hc (Oe) Residual magnetization Br (Gauss) Squareness (-) Glossiness (%) Surface roughness Ra (nm) Young's modulus (relative value) (-) Ex. 37 Ex. 29 790 1330 0.84 188 6.0 116 Ex. 38 " 30 892 1320 0.85 190 5.6 124 Ex. 39 " 31 899 1302 0.85 186 5.8 109 Ex. 40 " 32 1195 1201 0.82 179 7.0 111 Ex. 41 " 33 819 1446 0.89 171 6.0 132 Ex. 42 " 34 808 1456 0.90 175 5.4 138 Ex. 43 " 35 386 1311 0.87 156 8.8 145 Ex. 44 " 36 872 1340 0.87 153 8.8 142 Examples Magnetic particles as raw material Kind Average particle diameter (µm) Plate ratio or aspect ratio (-) Coercive force Hc (Oe) Saturation magnetization σs (emu/g) Example 61 Plate-like Co- and Ti-containing Ba ferrite particles 0.05 5.0 736 59.0 Example 62 ditto 0.05 5.4 825 59.5 Example 63 Co-coated magnetite particles 0.22 6.5 732 83.2 Example 64 ditto 0.22 6.5 732 83.2 Example 65 Co-coated maghemite particles 0.18 6.0 765 78.9 Example 66 ditto 0.18 6.0 765 78.9 Example 67 maghemite particles 0.22 7.0 362 73.2 Example 68 ditto 0.22 7.0 362 73.2 Examples Kind of magnetic particles Properties of tape Coercive force Hc (Oe) Residual magnetization Br (Gauss) Squareness (-) Glossiness (%) Surface roughness Ra (nm) Surface resistance (Ω/sq.) Ex. 69 Ex. 61 801 1296 0.82 180 6.4 4.2 x 10 9 Ex. 70 " 62 889 1320 0.83 181 6.4 3.0 x 10 9 Ex. 71 " 63 796 1510 0.91 168 6.0 6.5 x 10 8 Ex. 72 " 64 796 1492 0.90 165 6.2 2.8 x 10 8 Ex. 73 " 65 825 1462 0.91 176 5.4 5.6 x 10 8 Ex. 74 " 66 822 1479 0.91 170 5.8 1.0 x 10 9 Ex. 75 " 67 402 1292 0.87 155 8.2 4.6 x 10 9 Ex. 76 " 68 396 1310 0.87 156 8.2 4.3 x 10 9 Examples Magnetic particles as material Kind Average particle diameter (µm) Plate ratio or aspect ratio (-) Coercive force Hc (Oe) Saturation magnetization σs (emu/g) Comp. Example 1 Plate-like Co- and Ti-containing Ba ferrite particles 0.05 5.2 780 58.3 Comp. Example 2 ditto 0.05 5.4 825 59.5 Comp. Example 3 Co-coated maghemite particles 0.18 6.0 765 78.9 Comp. Example 4 ditto 0.18 6.0 765 78.9 Comp. Example 5 ditto 0.18 6.0 765 78.9 Comp. Example 6 ditto 0.18 6.0 765 78.9

Claims: Magnetic particles suitable for magnetic recording which comprise acicular or plate-like magnetic particles and not less than 0.01 wt% (calculated as Al, SiO 2 or Al and SiO 2 based on the acicular or plate-like magnetic particles) of an oxide or hydroxide of A1 and/or Si adhered to the surfaces of the acicular or plate-like magnetic particles, and which have a value of the molecular-weight-dependent dispersibility parameter α of not less than 0.50, wherein α is defined by formula (I): As = K 1 · M α wherein: M is the number-average molecular weight of a urethane resin binder used in determining the value of α; As is the saturation adsorption amount of the said binder on the magnetic particles; and K 1 is a constant dependent on the said binder and the mixed solvent of methyl ethyl ketone, toluene and cyclohexane used for measuring As in the determination of the value of α. Magnetic particles according to claim 1, wherein said plate-like magnetic particles are hexagonal ferrite particles. Magnetic particles according to claim 1 or 2, wherein said acicular or plate-like magnetic particles are Co-coated magnetic particles. Magnetic particles according to any one of the preceding claims, wherein α is not less than 0.53. Magnetic particles according to any one of the preceding claims, wherein said acicular or plate-like magnetic particles further comprise an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe adhered to the surfaces of said particles. Magnetic particles according to claim 5, wherein said further oxide or hydroxide is an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba and P and the amount of residual solvent in said magnetic particles is less than 2.0 wt% (calculated as C). Magnetic particles according to claim 5, wherein said further oxide or hydroxide is an oxide or hydroxide of at least one of Zr, Ti, Hf and Mo. Magnetic particles according to claim 5, wherein said further oxide or hydroxide is an oxide or hydroxide of at least one of Sn, Sb, Pd and Fe. Magnetic particles according to any one of claims 5 to 8, wherein the amount of said further oxide or hydroxide is not less than 0.01 wt% (calculated as each element) based on said acicular or plate-like magnetic particles. A magnetic medium comprising a substrate and a magnetic coating containing magnetic particles as defined in any one of the preceding claims. A magnetic medium according to claim 10, which has a running durability of 14 to 60 minutes. A magnetic medium according to claim 10 or 11, which has a surface resistance of not more than 5 x 10 9 Ω/sq. A process for producing magnetic particles as defined in claim 1 which comprises: adding an aqueous alkali solution to an aqueous suspension containing acicular or plate-like magnetic particles to obtain a suspension having a pH of not less than 10; adding an aqueous solution containing A1 or an aqueous solution containing Si, or a mixture thereof to said suspension; adjusting the pH of said suspension to approximately neutrality with stirring to deposit or precipitate an oxide or hydroxide of Al and/or Si on the surface or periphery of the acicular or plate-like magnetic particles; filtering out said acicular or plate-like magnetic particles together with said oxide or hydroxide; washing and drying the obtained solid substance; and compacting and pulverizing said solid substance by an edge runner mill so as to adhere the oxide or hydroxide to the surfaces of said acicular or plate-like magnetic particles. A process according to claim 13, wherein the steps taken from said step of adding an aqueous alkali solution to said step of compacting and pulverising said solid substance are repeated at least twice. A process according to claim 13 or 14, wherein the aqueous solution containing Al or Si, or Al and Si further comprises at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe; and an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe is precipitated or deposited, filtered out, washed and dried and adhered with the oxide or hydroxide of Al and/or Si. A process according to claim 13 or 14, wherein the obtained particles comprise not less than 0.01 wt% (calculated as Al or SiO 2 or Al and SiO 2 and based on the acicular or plate-like magnetic particles) of the oxide or hydroxide of Al and/or Si adhered to the surfaces of the acicular or plate-like magnetic particles, and have a value of α of not less than 0.50; which process further comprises: adding an aqueous solution to an aqueous suspension containing the magnetic particles to obtain a suspension having a pH of not less than 10: adding an aqueous alkali solution containing at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe to said suspension; adjusting the pH of said suspension to approximately neutrality with stirring to deposit or precipitate an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe on the surface or periphery of the acicular or plate-like magnetic particles; filtering out said acicular or plate-like magnetic particles together with said further oxide or hydroxide; washing and drying the obtained solid substance; and compacting and pulverising said solid substance by an edge runner mill so as to adhere the further oxide or hydroxide to the particles. A process according to claim 13 wherein the acicular or plate-like magnetic particles used as the starting material have been obtained by: adding an aqueous alkali solution to an aqueous suspension containing acicular or plate-like magnetic particles to obtain a suspension having a pH of not less than 10; adding an aqueous solution containing at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe to said suspension; adjusting the pH of said suspension to approximately neutrality with stirring to precipitate an oxide or hydroxide of at least one of Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe on the surface or periphery of the acicular or plate-like magnetic particles; filtering out said acicular or plate-like magnetic particles together with said oxide or hydroxide; washing and drying the obtained solid substance; and compacting and pulverising said solid substance by an edge runner mill so as to adhere the oxide or hydroxide to the particles; thereby obtaining particles which comprise not less than 0.01 wt% (calculated as Zn, Ni, Mg, Ca, Sr, Ba, P, Zr, Ti, Hf, Mo, Sn, Sb, Pd and Fe and based on the acicular or plate-like magnetic particles) of the oxide or hydroxide adhered to the surfaces of the acicular or plate-like magnetic particles.

Inventors: HAYASHI KAZUYUKI, MORII HIROKO, OHSUGI MINORU, SUGITA NORIO, HAYASHI, KAZUYUKI, MORII, HIROKO, OHSUGI, MINORU, SUGITA, NORIO
Applicants: TODA KOGYO CORP, TODA KOGYO CORP.
Application year: 1993
Main classification: G11B5
IPC codes: B22F1, G11B5, C01G49, H01F1