Production of alkyl tertiary-alkyl ether

Abstract: An improvement in a method for cogeneration of isobutylene and MTBE by etherification of tBA/MeOH over an ion-exchange resin which allows for more complete conversion of the remaining tBA fraction and comprises a second step consisting essentially of the MTBE from the primary fractionator as an overhead fraction and etherifying the bottoms from the primary fractionator over an inorganic acid catalyst comprising a crystalline aluminosilicate faujasite-type Y-zeolite modified with a fluoride-containing compound.

Description: The present invention relates to the preparation of alkyl tertiary alkyl ethers from primary alcohol and tertiary alcohol. More particularly, this invention concerns the cogeneration of isobutylene and MTBE from crude t-butanol/methanol feedstocks. It concerns improved conversions of t-butanol to methyl tertiary butyl ether in a method comprising removing the bottoms from a primary fractionator of a unit for making MTBE and further reacting them over an acidic, fluoride-treated Y-zeolite at temperatures greater than 120°C. Coreactants in the crude feedstock may comprise water, t-butanol, methanol and isopropanol. Reaction over preferred fluoride treated Y-zeolites brings the total t-butanol conversion up to >90% in a continuous unit. In addition, product phase separation is observed at 160°C-220°C into an isobutylene/MTBE product-rich phase and an aqueous methanol heavier phase. The process may be used to prepare other alkyl tertiary-alkyl ethers, such as methyl tertiary amyl ether and ethyl t-butyl ether. The alkyl tertiary-alkyl ethers are useful as a blending component in high octane gasoline. It is known to those skilled in the art that ethers, including unsymmetrical ethers, may be prepared by reacting an alcohol with another alcohol to form the desired product. The reaction mixture, containing catalyst and/or condensing agent may be separated and further treated to permit attainment of the desired product. Such further treatment commonly includes one or more distillation operations. Methyl tert-butyl ether is finding increasing use as a blending component in high octane gasoline as the current gasoline additives based on lead and manganese are phased out. Currently most commercial processes for the manufacture of methyl tert-butyl ether are based upon the liquid-phase reaction of isobutylene and methanol (Eq. 1), catalyzed by a cationic ionexchange resin (see, for example: Hydrocarbon Processing, Oct. 1984, p. 63; Oil and Gas J., Jan. 1, 1979, p. 76; Chem. Economics Handbook-SRI, Sept. 1986, p. 543-7051P). The cationic ion-exchange resins used in MTBE synthesis normally have the sulphonic acid functionality (see: J. Tejero, J. Mol. Catal., 42 (1987) 257; C. Subramamam et al., Can. J. Chem. Eng., 65 (1987) 613). With the expanding use of MTBE as an acceptable gasoline additive, a growing problem is the availability of raw materials. Historically, the critical raw material has been isobutylene (Oil and Gas J., June 8, 1987, p. 55), however, recently, US-A-5,099,072, 5,162,592 and 5,081,318, inter alia, assigned to Texaco Chemical, disclose a one-step method for producing methyl tert-butyl ether (MTBE) from t-butanol (tBA) over various catalysts. It would be advantageous to obtain additional conversion of the t-butanol in the crude feedstock without having to recycle unconverted tertiary butanol. The preparation of methyl tert-butyl ether from methyl and tert-butyl alcohols is discussed in S. V. Rozhkov et al., Prevrashch Uglevodorodov, Kislotno-Osnovn. Geterogennykh Katal. Tezisy Dokl. Vses Konf., 1977, 150 (C. A. 92:58165y). Here the tBA and methanol undergo etherification over KU-2 strongly acidic sulfopolystyrene cation-exchangers under mild conditions. This reference contains data on basic parameters of such a process. It is also noted that, although a plant for etherification over cation exchangers does not present any major problems, considerations include the fact that recycling large amounts of tert-butyl alcohol and methanol, as well as isobutylene, causes the scheme to be somewhat more expensive. Also, the progress of the reaction over cation exchangers is usually complicated by various adsorption and diffusion factors, by swelling phenomena, and by the variable distribution of the components between the solution and ion-exchanger phase. Furthermore, said acidic cation-exchangers with an organic (polystyrene or polymethacrylate) backbone generally have a very limited stability range with regard to operating temperatures, with temperatures above 120°C normally leading to irreversible destruction of the resin and loss of catalytic activity. "Preparation of Methyl Tert-Butyl Ether (MTBE) Over Zeolite Catalysts" is an article by Pochen Chu and Günther H. Kühl, Ind. Eng. Chem. Res., 26 , 365, 1987. Chu et al. disclose work which identifies ZSM-5 and ZSM-11 to be selective for the preparation of MTBE. Compared to the conventional Amberlyst® 15 resin, the zeolites are thermally stable, and give no acid effluent; they provide high selectivity to MTBE with little or no diisobutene yield, are less sensitive to the CH 3 OH/i-C 4 H 8 ratio and exhibit good selectivity even at ratios approaching unity. They provide high MTBE output, despite the unfavorable thermodynamic equilibrium, since the process utilizing these zeolites can be operated at high temperature and high space velocity. In addition, deactivation is not observed in the present short catalytic tests and reactivation is not required. The excellent selectivity of these two zeolites is believed to be effected by the size of their pore structure, which provides easy access to methanol and restricted access to isobutene. Zeolite beta was also tested, giving the poorest results and small pore zeolites were inactive. As expected, large pore zeolites do not exhibit shape selectivity. An extensive body of knowledge of zeolite properties and catalytic potential has developed in recent years. A variety of different types of zeolites is known in the art, including natural and synthetic zeolites (see Table A). Research has opened up a spectrum of new opportunities in the field of molecular shape selective catalysis, where the intracrystalline space accessible to molecules has dimensions near those of the molecules themselves. This field is discussed in an article titled "Molecular Shape Selective Catalysis", P.B. Weisz, New Horizons in Catalysis, Part A, 1980. For example, it is possible to catalyze the dehydration of n-butanol over a Linde 5Å zeolite without reacting isobutanol which may be present. COMMERCIALLY AVAILABLE ZEOLITES Zeolite Pore Size/nm Composition Sorportion Capacity (wt%) Si/Al Cation H 2 O nC 6 H 14 C 6 H 12 Faujasite X 0.74 1-1.5 Na 28 14.5 16.6 Y 0.74 1.5-3 Na 26 18.1 19.5 US-Y 0.74 >3 H 11 15.8 18.3 A 0.3 1.0 K,Na 22 0 0 A 0.4 1.0 Na 23 0 0 A 0.45 1.0 Ca,Na 23 12.5 0 Chabazite 0.4 4 * 15 6.7 1 Clinoptilite 0.4x0.5 5.5 * 10 1.8 0 Erionite 0.38 4 * 9 2.4 0 Ferrierite 0.55x0.48 5-10 H 10 2.1 1.3 L-type 0.6 3-3.5 K 12 8 7.4 Mazzite 0.58 3.4 Na,H 11 4.3 4.1 Mordenite 0.6x0.7 5.5 * 6 2.1 2.1 Mordenite 0.6x0.7 5-6 Na 14 4.0 4.5 Mordenite 0.6x0.7 5-10 H 12 4.2 7.5 Offretite 0.58 4 K,H 13 5.7 2.0 Phillipsite 0.3 2 * 15 1.3 0 Silicalite 0.55 ** H 1 10.1 0 ZSM-5 0.55 10-500 H 4 12.4 5.9 *Denotes a mineral zeolite: cations variable, but usually Na, K, Ca, Mg **Very large Si:Al A concise and informative review of zeolite applications in organic synthesis is titled "Zeolite Catalysts Face Strong Industrial Future" in European Chemical News, 10, July 1989, p. 23. Points worth noting are that the major success of zeolite catalysis is in catalytic cracking with about 300,000 tons per year being used worldwide. Typically these are zeolite-Y (12-ring window) but oftentimes a medium-pore, such as H-ZSM-5, is added to increase aromatic content. The ZSM-5 consists of two pore systems (5-6Å in diameter) which intersect to give spatial regions of around 9Å diameter at the intersections. Early work emphasized the role of medium-pore zeolites for aromatics substitution, but more recently, there has been extensive work describing the role of zeolites in the synthesis of organic intermediates containing oxygen and nitrogen, Ibid , p. 24. In US-A-4,214,307 (C D Chang et al) (July 22, 1980), it is shown that hydration of C 2 to C 4 olefins to alcohols can be carried out over ZSM-5 below about 240°C and 10 to 20 atmospheres of pressure without forming ethers or other hydrocarbons, however, above 240°C propene and butenes undergo other olefinic reactions, forming higher molecular weight hydrocarbon products. US-A-4,058,576 (Chang et al) teaches the use of (pentasil-type) aluminosilicate zeolites, such as ZSM-5, having a pore size greater than 5 angstrom units and a silica-to-alumina ratio of at least 12, to convert lower alcohols to a mixture of ethers and olefins. In US-A-4,943,545 (Chang et al) there is suggested modification of Y-zeolites having Si:Al ratio of at least 4 with a very dilute (0.001 → 0.1N) solution of HF in a cracking catalyst as a means of reactivation. US-A-4,605,787 discloses a process for the preparation of methyl tert-butyl ether which comprises reacting methanol and isobutylene in vapor phase in the presence of ZSM-5 or ZSM-11 acidic zeolite catalyst. US-A-5,099,072; 5,162,592 and 5,081,318, (Texaco Chemical Co) relate to various zeolite catalysts used in the one-step synthesis of methyl t-butyl ether from t-butanol. In EP-A-0,528,626, there is disclosed a catalyst for synthesis of MTBE from t-BuOH comprising hydrogen fluoride modified zeolites. In European Application No. 93305745.7, there is disclosed a catalyst for MTBE synthesis comprising fluorophosphoric acid-modified zeolites. In the art, where the feedstock for producing MTBE is t-butanol, the conversions are not as high as would be desirable. There does not seem to be any disclosure of a second-stage etherification, wherein bottoms from the primary reactor are reacted in a secondary etherification unit to obtain higher overall conversions. This would allow more complete conversion of t-butanol without the necessity of recycling. The second stage of such a two-step process would require a catalyst which can withstand very high temperatures. It would be a substantial advance in the art if crude t-butanol/methanol feedstocks could be used and still obtain higher tBA conversions (>90%) and total MTBE + isobutylene selectivity as high as 99%. According to the process of the present invention, there is provided a process for preparing alkyl tert-alkyl ether from tertiary alcohol and primary alcohol. More particularly there is a primary etherification step using crude tBA/MeOH to generate methyl tertiary butyl ether (MTBE) over an acidic catalyst. In order to achieve more complete conversion of t-butanol without recycle, the instant invention provides for a second step for etherifying remaining t-butanol over an acidic, fluoride-treated Y-zeolite catalyst. The effluent from the primary reactor is fed to the methyl tertiary butyl ether recovery distillation tower which recovers MTBE, isobutylene and some methanol overhead while water, tBA and methanol are removed in the bottoms. The bottoms from the primary fractionator, comprising water, t-butanol, methanol and isopropanol are fed into a second etherification unit and reacted over an acidic fluoride-treated Y-zeolite for cogeneration of isobutylene and MTBE. The preferred fluoride-treated Y-zeolites achieve >90% conversion and they are stable at high temperatures. More particularly the instant process involves: 1) The etherification of tBA/MeOH feed to MTBE over an ion-exchange resin at temperatures of <120°C; 2) Recovery of the MTBE in the primary fractionator as an overhead fraction; 3) Etherification of the bottoms from the primary fractionator comprising crude t-butanol/methanol feedstock over an acidic type Y-zeolite modified with a fluorine - containing compound at a temperature of 120°C to 250°C, e.g. 140°-240°C, most preferably 180°C to 220°C to complete the conversion of the remaining tBA fraction to MTBE plus isobutylene. The t-butanol/methanol feedstock comprises four principal components, -water, t-butanol, methanol and isopropanol. The etherification reaction can be represented by: The dehydration reaction can be represented by: Generally the crude t-butanol/methanol and isopropanol coreactants may be mixed in any proportion in order to generate the desired methyl t-butyl ether. In the initial etherification, the molar ratio of crude methanol feedstock to t-butanol feedstock in the mixture should be between 10:1 and 1:10 if the yield of desired MTBE is to be maximized. The most preferred methanol-to-tertiary butanol molar ratio is from 1:1 to 5:1. In the instant etherification the proportions of coreactants are about 2:1. However, in order to achieve maximum selectivity to MTBE, and optimum conversion per pass, an excess of methanol in the liquid feed is desirable. The syntheses of Equations 2 and 3 can also be conducted where the t-butanol and methanol reactants are mixed with certain other components including water, alcohols such as isopropanol, ketones such as acetone, peroxides and hydroperoxides such as di-t-butyl peroxide and allyl t-butyl peroxide, as well as esters such as t-butyl formate. Typically each of said classes of components makes up less than 30% of the total feed mixture. The same process may also be applied to the preparation of other alkyl tertiary alkyl ethers. For example, said process may be applied to the reaction of a C 1 -C 6 primary alcohol such as methanol, ethanol, n-propanol and n-hexanol with a C 4 -C 10 tertiary alcohol such as, for example, tertiary butanol and tertiary amyl alcohol. Reaction of methanol with tertiary amyl alcohol (2-methyl-2-butanol) would then yield methyl tertiary amyl ether (TAME) while reaction of ethanol with t-butanol would yield ethyl t-butyl ether (ETBE). Alternatively a mixture of alcohols, e.g., a mixture of C 1 -C 5 alcohols, could be reacted to give a mixture of alkyl tert-alkyl ethers. Good results were realized using certain acidic, fluoride-treated Y-zeolites as catalysts for the reactions represented in Equations 2 and 3, particularly the isostructural group of faujasite zeolites that include the synthetic Y-zeolites. The preferred Y-zeolites are the ammonium exchanged and rare earth exchanged Y-zeolites. The unit cells of zeolites X and Y are cubic, a o ≈ 2.5 nm, and each contains 192 silicon- or aluminum-centered oxygen tetrahedra which are linked through shared oxygen atoms. Because of the net negative charge on each of the aluminum-centered tetrahedra, each unit cell contains an equivalent number of charge-balancing cations. These are exclusively sodium ions in zeolites in their synthesized form. Typical cell contents for the Y-zeolites in the hydrated form are: Na 56 [(A10 2 ) 56 (SiO 2 ) 136 ] . 250 H 2 O Y-zeolites are distinguished on the basis of the relative concentration of silicon and aluminum atoms and the consequent effects on detailed structure and related chemical and physical properties. The aluminum atoms in the unit cell of Y-zeolite vary from 76 to 48 giving a Si:Al ratio between 1.5 and 3.0. Both the cation concentration and charge density on the aluminosilicate structure are lower for Y-zeolites than for X-zeolites, where the aluminum atoms in the unit cell vary from 96 to 77. The feature which determines the difference between faujasites and other zeolites built up from sodalite units is the double 6-membered ring or hexagonal prism, by which the units are linked. The sodalite unit, or β-cage, can be represented by a truncated octahedron, with the 24 silicon or aluminum atoms (designated T atoms) taking positions at the vertices. The 36 oxygen atoms are displaced from the midpoints of the edges joining the vertices in order to attain tetrahedral configuration around the T atoms. The free diameter of the void within the β-cage is 0.66 nm, but only the smallest molecules can enter through the 0.22 nm diameter opening in the distorted ring of six oxygen atoms associated with each hexagonal face. Each sodalite unit is linked tetrahedrally across hexagonal faces by six bridging oxygens to four other sodalite units. The larger void spaces enclosed by sodalite units and hexagonal prisms are termed α-cages, or supercages. The α-cage is a 26-hedron with a free diameter of ≈1.3 nm, and it can be entered through four distorted 12-member rings of diameter 0.80-0.90 nm. In this way each α-cage is tetrahedrally joined to four others giving a complex system of void space extending throughout the zeolite structure. The α- and β-cages together give Y-zeolites, along with X-zeolites, the largest void volume of any known zeolites, which is ca. 50 vol% of the dehydrated crystal. From the catalytic viewpoint, the α-cages are by far the most important, since, unlike the β-cages, they permit entry of numerous aliphatic and aromatic compounds. Particularly effective in the subject synthesis of MTBE are the synthetic Y-zeolites. Preferably said zeolites should be in a strongly acidic form whereby some, or all, of the cations (Group I or II, alkali or alkaline earth metal ions such as sodium, potassium, calcium or magnesium) are exchanged by protons either through ammonium exchange followed by thermal stabilization (deammoniation, removal of NH 3 ) at elevated temperatures (e.g. 400-500°C) through mineral acid treatment, etc. Alternatively, said Y-zeolites may be rare-earth exchanged with, for example, a mixture of rare-earth salts, by treatment with lanthanum salts, etc. Said rare-earth exchanged Y-zeolites would then have a Si:A1 ratio of 1.5 to 3. The exchange of the sodium ions of the Y-zeolite by rare earth ions has been reviewed (see, for example, R. Rudham and A. Stockwell, The Chemical Society Specialist Periodical Report - Catalysis, Vol. I, 1977, Chapter 3). The preferred acidic Y-zeolites for the practice of this invention have silica:alumina ratios in the range 100:1 to 1:1. Illustrative of suitable Y-zeolites for the practice of this invention include Linde SK-500, a rare-earth exchanged Y-zeolite, having a Si:Al ratio of 1.5→2, PQ Corporation's CP 304-37, a thermally-stabilized, ammonium-exchanged Y-zeolite having a silica:alumina ratio of ca. 11:1, with a silica-alumina binder, as well as CP 316-26, another ammonium exchanged Y-zeolite, this time having a silica-to-alumina ratio of 46, LZY-82 from UOP having a silica:alumina ratio of 7.8 and a unit cell size of 24.53A, and LZY-85 having a silica:alumina ratio of 9.1 and a unit cell size of 24.49A. It has been discovered that acidic fluoride-treated Y-zeolites have a number of improved properties for the production of MTBE. Most importantly they possess the stability at high temperatures necessary for a second stage process of the type described herein. The acid useful for modifying the zeolites is selected from the group consisting of fluoride-containing compounds such as ammonium fluoride or silicon hexafluoride compounds, hydrogen fluoride, hydrofluoric acid, or fluorosulfonic acid and its congeners such as fluorosulfonic acid, trifluoromethane sulfonic acid (triflic acid), as well as triflic anhydride. These fluorosulfonic acids can be substituted with a variety of alkyl groups, as in the case of trifluoromethanesulfonic acid. Methods of preparing these triflic acid-modified catalysts are illustrated in the accompanying Example 2. The fluoride-modified zeolites may be prepared by treating the Y-zeolite or dealuminized Y-zeolite with hydrogen fluoride, with an aqueous solution of hydrofluoric acid, with ammonium fluoride, or with a solution of HF or NH 4 F in a suitable organic solvent. Preferably the hydrogen fluoride is added to said zeolite as a solution of hydrofluoric acid in distilled water. The method of preparing these HF-modified catalysts is illustrated in the accompanying Example 1. For example, the treatment of the Y-zeolites with fluoride ion is accomplished by adding a solution of from one to about 60% of one N to 30 N fluoride compound such as, for example, hydrogen fluoride, ammonium fluoride, triflic acid, fluorosulfonic acid or triflic anhydride in distilled water or an organic solvent such as a ketone, such as acetone, to 100g of a Y-zeolite or dealuminated Y-zeolite, stirring from 1 hour to at least 24 hours, under nitrogen, filtering and washing the solids with distilled water, then drying in vacuo at 40°C overnight plus 150°C for 4 hours. Said catalysts should have a residual acidity in the range 0.1 to 100 mg KOH/g and they may be in the form of powders, pellets, granules, spheres, shapes and extrudates. The examples described herein demonstrate the advantages of using extrudates. The reaction may be carried out in either a stirred slurry reactor or in a fixed bed continuous flow reactor. The catalyst concentration should be sufficient to provide the desired catalytic effect. Etherification (Eq. 2) and dehydration (Eq. 3) can generally be conducted at temperatures from 20° to 300°C; the preferred range is 120° to 250°C and the most preferred ranqe is 180°C to 220°C. The total operating pressure may be from 0.1 to 7.0 MPa (0 to 1000 psig) or higher. The preferred pressure range is 0.4 to 3.5 MPa (50 to 500 psig). In certain circumstances, it may be particularly desirable that the tBA conversion be high enough (e.g. 80% or greater), such that the crude product mix phase separates into an isobutylene-MTBE product-rich phase and a heavier aqueous methanol phase. Preferably such a product phase separation would be achieved at as low an etherification temperature as possible, but particularly in the range 160-240°C. Typically, MTBE is generated continuously in up to ca. 30 wt% concentration or greater in the crude liquid product at total liquid hourly space velocities (LHSV) of up to 6 or higher and relatively mild conditions, where: LHSV = Volume Of Total Liquid Feed Run Through The Reactor Per Hour Volume of Catalyst In Reactor Conversions of t-butanol (tBA, wt%) are estimated in the following examples using the equation: (Wt% Conc. of tBA in Feed - Wt% Conc. of tBA in Product) Wt% Conc. of tBA in Feed x 100 Selectivities for methyl t-butyl ether (MTBE, mole %) and isobutylene (C 4 H 8 , mole%) are estimated from: Moles of MTBE (or C 4 H 8 ) in Product moles of tBA converted x 100 The results in Tables 1-10 illustrate the additional cosynthesis of isobutylene and MTBE from a crude aqueous t-butanol/methanol feedstock comprising four principal components, viz-water, t-butanol, methanol and isopropanol (2-PrOH) in a second etherification unit, using as catalysts: HF-treated Y-zeolites (Examples 3, 5 and 6); Triflic acid-treated Y-zeolites (Examples 4 and 7); Ammonium fluoride-treated Y-zeolites (Examples 8-11); and Triflic anhydride-treated Y-zeolite (Example 12). By-product identifications in Tables 1-10 are as follows: Diisobutylene (C 8 H 16 ), isopropyl t-butyl ether (IPTBE) and dimethyl ether (DME). The preferred catalysts typically show: a) >90% t-butanol conversion per pass. b) 98% or better molar selectivity to isobutylene plus MTBE. c) Very little cogeneration of diisobutylene or isopropyl t-butyl ether (IPTBE). d) Controlled quantities of dimethyl ether formation. e) Product phase separation into an isobutylene/MTBE product phase and an aqueous methanol heavier phase at operating temperatures of 160°C or above. Extended catalyst life (2000 hours) is illustrated in Tables 11-14 and Examples 13 and 14 for both an ammonium fluoride-treated Y-zeolite (LZY-82) and a hydrofluoric acid treated Y-zeolite (CP316-26). The same, untreated Y-zeolite (CP316-26) shows poor performance with the same feedstock, and under the same conditions, in the comparative Example A and Table 15. Ethyl t-butyl ether (ETBE) production from crude t-butanol plus ethanol using the fluoride-treated Y-zeolite catalyst of Example 1, is illustrated in Example 15. EXAMPLES The examples which follow illustrate the second stage synthesis of MTBE and isobutylene from crude t-butanol/methanol feedstocks using acidic, fluoride-treated Y-type zeolites, particularly in the form of extrudates. The examples are only intended as a means of illustration. EXAMPLE 1 This example illustrates the preparation of a hydrogen fluoride-modified Y-zeolite. To 100g of Y-zeolite (CP316-26, an ammonium-exchanged, thermally-stabilized Y-zeolite having a silica:alumina ratio of 46 and a unit cell size of 24·26A, in 1.6mm diameter extruded form) was added a solution of 48% hydrofluoric acid (50g) in distilled water (100g). The mixture was stirred overnight, under nitrogen, filtered and the solids washed with distilled water, then dried in vacuo at 40°C, overnight, plus 150°C for 4 hours. The recovered white extrudates were found to comprise on analysis: Fluoride, 4.7% Water, 1.9% Acidity, 4.8 mg KOH/g EXAMPLE 2 To 100g of Y-zeolite (CP316-26 that had been dried in vacuo at 175°C for 3 hours and had a water content of 0.54%) was added a solution of trifluoromethane sulfonic acid (40g), in dried acetone, (40cc, dried over 4Å sieve). The mixture was stirred overnight under nitrogen, filtered and the solids washed with dried acetone then dried in vacuo at 40°C overnight, plus at 150°C for 4 hours. The recovered reddish-brown extrudates were found to comprise by analysis: Water, 0.33% Acidity, 29.7 mg KOH/g EXAMPLE 3 This example illustrates the cosynthesis of isobutylene and MTBE from a crude aqueous t-butanol/methanol feedstock using a hydrogen fluoride-modified Y-zeolite. Synthesis was conducted in a tubular reactor (12mm id, 304mm long) constructed of 316 stainless steel, operated upflow and mounted in a furnace controllable to ±1.0°C and fitted with pumps allowing flow control to ±1 cc/hr. The reactor was also fitted with a pressure regulating device and equipment for monitoring temperature, pressure and flow rate. The reactor was charged at the beginning of the experiment with 25cc of hydrogen fluoride-treated Y-zeolite extrudates, prepared by the method of Example 1. A screen of glass wool was placed at the top and bottom of the reactor to ensure the catalyst would remain in the middle portion. The catalyst bed was treated with a crude t-butanol/methanol feed mix also containing sizeable quantities of water and isopropanol components, upflow, at a feed rate of 50 cc/hr, while the reactor was held at 140°C with a total pressure of 2.0MPa (300psi). Samples of effluents were collected periodically on stream and analyzed by glc and gc-ir. Typical analyses data for samples taken under these conditions are summarized in Table 1. Performance at higher temperatures (160°, 180°, 200°C) was determined using the same procedures. These results are also given in Table 1. Operating at 200°C, where the effluent comprises two phases, the t-butanol conversion level and isobutylene/MTBE selectivities are as follows: t-Butanol conversion = 94% Isobutylene selectivity = 91 mole% MTBE selectivity = 7 mole% In Table 1 and subsequent tables, both "t/b" and "t:b" represents the ratio of top phase to bottom phase. EXAMPLE 4 This example illustrates the cosynthesis of isobutylene and MTBE from a crude aqueous t-butanol/methanol feedstock using a triflic acid-modified Y-zeolite. Using the equipment and procedures of Example 3, the reactor was charged with 25cc of triflic acid-treated Y-zeolite extrudates, prepared by the method of Example 2. The catalyst bed was then treated with a crude t-butanol/methanol feedstock also containing sizeable quantities of water and isopropanol at four different operating temperatures (140°, 160°, 180° and 200°C). Typical product analyses data are given in Table 2. Operating at 200°C, where the effluent comprises two phases, the t-butanol conversion level and isobutylene/MTBE selectivities are as follows: t-Butanol conversion = 94% Isobutylene selectivity = 90% MTBE selectivity = 9% EXAMPLES 5-12 These examples also illustrate the cosynthesis of isobutylene and MTBE from crude aqueous t-butanol/methanol feedstocks using various fluoride-treated Y-zeolites. Using the equipment and procedures of Example 3, the following classes of fluoride-treated Y-zeolites were evaluated: a) Hydrofluoric acid-treated Linde SK-500 (Table 3). b) Hydrofluoric acid-treated CP304-37 from PQ Corp. (Table 4). c) Triflic acid-treated Linde SK-500 (Table 5). d) Ammonium fluoride-treated LZY-82 from UOP (Tables 6 and 7). e) Ammonium fluoride-treated LZY-85 from UOP (Tables 8 and 9). f) Triflic anhydride-treated SK-500 (Table 10). High (>90%) t-butanol conversions were achieved with most of these catalysts at the higher operating temperatures. Typical t-butanol conversion levels were as follows: Ex. Catalyst Composition Operation Temp (°C) tBA Conversion (%) 7 Triflic acid/SK-500 200 91 8 NH 4 F/Y-82 200 93 9 NH 4 F/Y-85 200 93 EXAMPLE 13 Following the procedures and using the equipment of Example 3, a sample of ammonium fluoride-treated Y-zeolite (UOP's LZY-82) was treated with a crude t-butanol/methanol feed mix, also containing sizeable quantities of water and isopropanol components, at 200°-220°C for a period of 84 days (ca. 2000 hours). Typical product analyses data are given in Tables 11 and 12 for these two-phase products. Summary t-butanol conversion and isobutylene/MTBE selectivities are as follows: Sample Time On Stream (Days) t-Butanol Conv(%) Molar Selectivities C 4 H 8 MTBE 2R 2 93 89 8.7 6 17 89 81 14 14 52 92 88 12 18 81 82 80 24 EXAMPLE 14 Following the procedures and using the equipment of Example 3, a sample of hydrofluoric acid-treated Y-zeolite (CP316-26), prepared by the method of Example 1, was treated with the crude t-butanol/methanol feed mix of Examples 3 and 13, at 200°-220°C for a period of 85 days (2000+ hours). Typical product analyses data are given in Tables 13 and 14 for these two-phase products. Summary t-butanol conversion and isobutylene/MTBE selectivities are as follows: Sample Time On Stream (Days) t-Butanol Conv(%) Molar Selectivities(%) C 4 H 8 MTBE 1 1 93 60 7.2 4 19 82 85 18 14 85 80 84 16 COMPARATIVE EXAMPLE A Following the procedures and using the equipment of Example 3, a sample of unmodified Y-zeolite (CP316-26) was treated with the crude t-butanol/methanol feed mix of Examples 3 and 14, at 200°-220°C for an extended period. Typical product analyses data are given in Table 15. All product samples were single phase. Summary t-butanol conversion and isobutylene/MTBE selectivities are as follows: Sample Time On Stream(Days) Operating Temp(°C) t-Butanol Conversion(%) 1 3 200 17 3 14 220 43 EXAMPLE 15 Following the procedures and using the equipment of Example 3, a sample of hydrofluoric acid-treated Y-zeolite (CP316-26) prepared by the method of Example 1, was treated with a crude t-butanol/ethanol feed mix at 200°C. Typical product analyses data shown the formation of ethyl t-butyl ether (ETBE) and isobutylene.

Claims: A process for the additional generation of alkyl tertiary-alkyl ether from tertiary alcohol and primary alcohol, comprising etherifying the tertiary alcohol and primary alcohol feed in a primary reactor to alkyl tertiary alkyl ether and recovering said ether as an overhead fraction from a primary fractionator, characterised in that in a second stage the bottoms fraction from said fractionator is etherified in the temperature range from 120°C to 250°C in the presence of a catalyst comprising an acidic type Y-zeolite modified with a fluorine-containing compound. A process as claimed in Claim 1 wherein the alcohol feedstocks are tertiary butanol and methanol which are etherified to form methyl tertiary butyl ether. A process as claimed in Claim 2 wherein the bottoms from the primary fractionator is crude t-butanol/methanol feedstock comprising primarily water, t-butanol, methanol and isopropanol. A process as claimed in any one of Claims 1 to 3 wherein said Y-zeolite has a Si:Al ratio of 1.5-2:1, 8:1 or 46:1. A process as claimed in any one of Claims 1 to 4 wherein the Y-zeolite is modified with hydrogen fluoride, ammonium fluoride, a fluorosulfonic acid or triflic anhydride. A process as claimed in any one of the preceding Claims wherein the temperature in the second stage is from 180°C to 220°C. A process as claimed in any one of the preceding Claims wherein the modified Y-zeolite catalyst has a residual acidity in the range of 0.1 to 100 mg KOH/gm. A method as claimed in any one of Claims 1 and 4 to 7 wherein t-butanol is reacted with ethanol and the major products are ethyl t-butyl ether (ETBE) plus isobutylene.

Inventors: KNIFTON JOHN FREDERICK, KNIFTON, JOHN FREDERICK
Applicants: HUNTSMAN SPEC CHEM CORP, HUNTSMAN SPECIALTY CHEMICALS CORPORATION
Application year: 1993
Main classification: C07C43
IPC codes: C07B61, C07C43, C07C1, C07C41