Unsaturated polyester resin compositions, molding materials, and molded products

Abstract: Resin compositions containing (a) unsaturated polyester, (b) polymerizable monomer, (c) thermoplastic resin, (d) a polymerization initiator, and (e) hollow glass microspheres with a true density of 0.5 to 1.3 g/cm³ and an elution alkalinity of 0.05 meq/g or less; molding materials obtained by impregnating glass fibers with such resin compositions; and molded products obtained by curing such molding materials. The molding materials have a superior workability and are useful for the production of parts to be coated, such as automotive external body panels. The molded products are light in weight and are highly resistant to water. Defective adhesion of coating or blisters does not occur.

Description: Background of the Invention This invention relates to unsaturated polyester resin compositions and sheet-like and bulk-like molding compounds obtained by impregnating glass fibers with such resin compositions, and molded products obtained therefrom which have superior paintability and hence are useful for coating automotive exterior body panels and other exterior parts. Fiber-reinforced plastics (FRP) using unsaturated polyester resins have superior mechanical strength and resistance against heat, water and chemicals and hence have been extensively used, for example, in bathtubs, water tank panels and bathroom sinks. Since sheet molding compounds (SMC) and bulk molding compounds (BMC) using unsaturated polyester resins are easy to mold and have high production efficiency, they are being commonly used as FRP molding materials. In response to the increased demand for light-weight SMC and BMC, many attempts are being made recently to reduce the density of SMC and BMC. Although the most frequently used methods are by the addition of hollow glass microsphere to a resin composition, the water-resistance is significantly affected by the addition of such hollow glass microsphere in the case of automotive exterior body panels and other exterior parts (such as engine hoods, roofs, trunk lids, spoilers, air intakes and rocker panels), which are usually coated. If a molded product, thus coated, is soaked in warm water, for example, defective adhesion of the coating and blisters will occur, rendering the product unusable as a practical molded product. Moreover, although metallic oxides are frequently used with SMC and BMC as thickeners for resins in order to improve their workability, the addition of hollow glass microspheres has a significant inhibitive effect on the increase in viscosity, and it has been difficult to obtain a molding material which can be easily handled, or worked with. It is for this reason that there have been strong demands for the development of molding materials which are light in weight and have superior paintability and workability. Although a BMC containing hollow glass microspheres having an effective density of 0.3-0.4 g/cm³ and treated with acid at least once, has been proposed (Japanese Patent Publication Tokkai 1-234434) as such a molding material, yet paintability and workability are not sufficiently improved even if this material is used. The inventors have accomplished the present invention as a result of their diligent studies into molding materials having all of these characteristics. Summary of the Invention The inventors have conducted researches to determine what kind of molding materials have all of three desirable qualities, namely, lightweight, superior paintability, and capability of being handled easily. As a result, it has been found that the three qualities are possessed by a molding material comprising a resin composition which contains an unsaturated polyester, a polymerizable monomer, a thermoplastic resin, a polymerization initiator, and a hollow glass microsphere. In particular, a molding material comprising glass fibers impregnated with such a resin composition is very light in weight and can be handled very easily. Also, such a molding material can be used to mold a product light in weight and having superior paintability. Detailed Description of the Invention The present invention relates to (i) a resin composition containing (a) an unsaturated polyester, (b) a polymerizable monomer (c) a thermoplastic resin, (d) a polymerization initiator, and (e) a hollow glass microsphere with true density 0.5-1.3 g/cm³ and elution alkalinity 0.05 meq/g or less; (ii) a molding material obtained by impregnating glass fibers with such a resin composition, and (iii) a molded product obtained by curing such a molding material. The foregoing resin compositions (i) are light in weight and have superior paintability and workability. In addition, they have the characteristics of FRP, that is, superior mechanical strength and resistance against heat and chemicals. Sheet-like and bulk-like molding materials (ii), obtained by impregnating glass fibers (such as those with a length of 1/4 to 2 inches) with such resin compositions (i) at a ratio of 10-60 weight per cent with respect to the entire composition, have improved workability and are useful as a molding material for the production of parts to be coated such as automotive exterior body panels. Molded products (iii) obtained by curing molding materials (ii) of the present invention are light in weight and have superior resistance against water after coating and no defective adhesion of coating or blisters result. Unsaturated polyesters (a) to be used according to the present invention are of a kind which has hitherto been used commonly and can be synthesized by condensing an α ,β olefinically unsaturated dicarboxylic acid and a divalent alcohol. These polyesters can also be synthsized by using saturated dicarboxylic acids, aromatic dicarboxylic acids, or dicyclopentadiene which reacts with carboxylic acids. Examples of the α ,β -olefinically unsaturated dicarboxylic acid include maleic acid, fumaric acid, itaconic acid, citraconic acid, and anhydrides of these dicarboxylic acids. Examples of dicarboxylic acid which may be used together with such an α ,β olefinic unsaturated dicarboxylic acid include adipic acid, sebacic acid, succinic acid, gluconic acid, phthalic anhydride, isophthalic acid, terephthalic acid, tetrahydrophthalic anhydride, and chlorendic anhydride. Examples of divalent alcohol include alkanediols, oxaalkanediols, and diols obtained by adding alkylene oxide such as ethylene oxide and propylene oxide to bisphenol-A or hydrogenated bisphenol-A. Monovalent monools and trivalent triols may also be used. Examples of alkanediol include ethyleneglycol, 1,2-propyleneglycol, 1,3-propyleneglycol, 1,3-butanediol, 1,4 butanediol, neopentylglycol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, cyclohexanediol and hydrogenated bisphenol-A. Examples of oxaalkanedimethanol include dioxyethyleneglycol, trioxyethyleneglycol, dioxypropyleneglycol and trioxypropyleneglycol. Examples of monovalent or trivalent alcohol which may be used together with such divalent alcohols include octyl alcohol, oleyl alcohol and trimethylolpropane and so on. Synthesis of unsaturated polyester is usually carried out with heating while produced water is removed. Unsaturated polyesters with an average molecular weight of 800-4000 and an acid value of 20-60 are generally used according to the invention. Examples of polymerizable monomers (b) which can be used for the invention are monovinyl monomers including aromatic monovinyl monomers such as styrene, p-chlorostyrene and vinyl toluene and acrylic monovinyl monomers such as acrylic acid, ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, methacrylic acid, methyl methacrylate, isobutyl methacrylate, 2-hydroxyethyl methacrylate and acrylonitrile. Among them styrene is particularly desirable. This component (b) is usually added to the components (a) and (c) as their diluent. The component (c) to be used according to the present invention is the kind of the thermoplastic resins which have commonly been used as low profile agents for unsaturated polyester resins. Examples of such resins include polybutadienes and their hydrogenated products, polyisoprenes and their hydrogenated products, aromatic vinyl-conjugated diene block copolymers and their hydrogenated products, polystyrenes, styrene-vinyl acetate block copolymers, polyvinyl acetates and polymethyl methacrylates. Additionally, saturated polyesters (with a molecular weight of 300 to 100,000), urethane derivatives of such saturated polyesters (with a molecular weight of 2,000 to 100,000), or polyethers may also be used. The foregoing aromatic vinyl-conjugated diene block copolymers are themselves well-known polymers and can be synthesized by a known block copolymerization between aromatic vinyl monomers such as styrene, chlorostyrene, vinyl toluene or the like and conjugated diene monomers such as butadiene, isoprene or the like. Examples of such block copolymers include styrene-isoprene block copolymers, styrene-butadiene block copolymers and hydrogenated products thereof. Preferable examples of copolymers for the invention are those with molar ratio of aromatic vinyl monomer to conjugated diene monomer in the range of about 50:50-5:95 and average molecular weight in the range of about 30,000-200,000. With regard to the thermoplastic resins for the invention, styrene-butadiene block copolymers, polyvinyl acetates, saturated polyesters or urethane derivatives of saturated polyester are preferably used as such. Thermoplastic resins to be used in the invention may be obtained by carboxylic modification of polymers described above. Polymers with carboxylic groups introduced thereinto can improve not only compatibility with unsaturated polyesters but also thickening of the compound with magnesium oxide when SMC and BMC are prepared. The resin compositions according to the invention contain 20-40 weight parts, preferably 25-35 weight parts, of the component (a), 30-70 weight parts, preferably 40-60 weight parts, of component (b), and 5-30 weight parts, preferably 10-25 weight parts, of component (c) such that their total will be 100 weight parts. As a polymerization initiator (d) for the present invention, at least one organic peroxide is selected, according to the desired curing speed, from tertiary butyl peroxybenzoate (TBPB), tertiary butyl peroxyoctoate (TBPO), 2,5-dimethyl-2,5-di(benzoyl peroxy)hexane (DDBPH), tertiary amyl peroxyoctoate (TAPO), tertiary butyl isopropyl carbonate (TBIPC), 1,1-bis(t-butyl peroxy)-3,3,5-trimethyl cyclohexane, 1,1-bis(t-butyl peroxy)cyclohexane, 1,1-bis(t-amyl peroxy)-3,3,5-trimethyl cyclohexane and 1,1-bis(t-amyl peroxy)cyclohexane. These initiators (d) are used at a ratio of 0.5-5 weight parts, preferably 1.0-3.0 weight parts, to the total of 100 weight parts of the components (a)-(c). In addition to the polymerization initiators mentioned above, a curing accelerator may be used together according to the present invention. Examples of curing accelerator include organometallic compounds with metals such as cobalt, copper and manganese, as well as their octoates, naphthenates and acetylacetonates. They may be used either singly or in combination. These organometallic compounds are used at the rate of 10-1000 ppm as metal with respect to 100 weight parts for the total of components (a)-(c). Component (e) to be used according to the present invention is hollow glass microspheres with a true density of 0.5-1.3 g/cm³, preferably 0.8-1.2 g/cm³, and with an elution alkalinity of 0.05 meq/g or less, preferably 0.03 meq/g or less. The true density can be measured, for example, according to ASTM D2841 procedure or the nitrogen replacement method. The elution alkalinity can be measured according to ASTM D3100-78 procedure. Although hollow glass microspheres normally contain metal oxides such as Na₂O and has an elution alkalinity of about 0.10 meq/g, use is usually made of those with elution alkalinity reduced to less than 0.05 meq/g by washing them in a solution of an acid such as hydrochloric acid or sulfuric acid and/or by using a coupling agent to carry out a surface treatment. Hollow glass microspheres with 10%-breakage pressure greater than 120 kgf/cm², particularly greater than 240 kgf/cm² are desirable. Those with average particle diameter 5-100µ m, and in particular 5-50 µ m, are preferable. Although the amount of component (e) to be added depends on the true density of the hollow glass microspheres and the density of a product to be molded, yet it is usually 5-100 weight parts, particularly 10-80 weight parts, more particularly 20-60 weight parts, against 100 weight parts for the total of components (a)-(c). Alkanepolyol polymethacrylates or alkanepolyol polyacrylates may be added to the resin composition of the invention to improve the surface quality. Examples of such substances include dimethacrylates or diacrylates of alkanepolyols having 2-12 carbon atoms such as ethyleneglycol dimethacrylate, diethyleneglycol dimethacrylate, triethyleneglycol dimethacrylate, propyleneglycol dimethacrylate, dipropyleneglycol dimethacrylate, 1,4-butanediol dimethacrylate, neopentylglycol dimethacrylate, 1,6-hexanediol dimethacrylate, ethyleneglycol diacrylate, diethyleneglycol diacrylate, triethyleneglycol diacrylate, propyleneglycol diacrylate, 1,4-butanediol diacrylate, neopentylglycol diacrylate, 1,6-hexanediol diacrylate, trimethylolpropane dimethacrylate, glycerine dimethacrylate, pentaerythritol dimethacrylate, trimethylolpropane diacrylate, glycerine diacrylate, and pentaerythritol diacrylate. Further examples include polymethacrylates and polyacrylates of alkanepolyols having 3-12 carbon atoms such as trimethylolpropane trimethacrylate, glycerine trimethacrylate, pentaerythritol trimethacrylate, glycerine triacrylate, pentaerythritol triacrylate, pentaerythritol tetramethacrylate, dipentaerythritol hexamethacrylate, pentaerythritol tetraacrylate and dipentaerythritol hexaacrylate. They are added at the rate of 1-15 weight parts or preferably 3-10 weight parts with respect to 100 weight parts for the total of components (a)-(c). Fillers, pigments, or thickeners may be added to such resin compositions if necessary. Examples of fillers include calcium carbonate, aluminum hydroxide, talc, silica, clay, glass power and so on. Examples of pigment include titanium oxide, carbon black, iron oxide red, phthalocyanine blue, and so on. Molding materials such as SMC and BMC can be obtained from resin compositions containing such additives of many kinds by using known facilities and method to impregnate glass fibers (for example, of diameter about 8-20 microns and length 1/4-2 inches) therewith. Glass fibers are usually used at the rate of 10-60 weight % with respect to the total weight of the molding material. Molding materials of the present invention can be compression-molded with heating in a mold (under a pressure of 20-120 kgf/cm² and at a temperature of 110-180 o C) to produce molded products. The unsaturated polyester resin compositions and the molding materials obtained by impregnating glass fibers with them are light in weight and have a high workability and superior paintability. For this reason, they are extremely useful as molding materials for the production of molded products such as automotive exterior body panels that are to be coated. Examples The invention will now be described in more detail by way of test examples. Test Examples 1-7 and Comparative Examples 1- 5 Sheet molding compounds (SMC) were prepared by using the components of Table 1. In Table 1, the unsaturated polyester resin A is a styrene solution of unsaturated polyester synthesized from propyleneglycol and maleic anhydride, containing 30 weight per cent of styrene and having a viscosity of 820 cps at a temperature of 25 o C and an acid value of 16.5. Unsaturated polyester resin B is a styrene solution of unsaturated polyester synthesized from 1.0 mole of propyleneglycol, 0.2 mole of dicyclopentadiene, and 1.0 mole of maleic anhydride, containing 35 weight % of styrene and having a viscosity of 650 cps at a temperature 25 o C and an acid value of 21. The styrene-butadiene block copolymer solution comprises 30 weight parts of copolymer and 70 weight parts of styrene with a viscosity of 28,000 cps at 25 o C. This copolymer had an average molecular weight of 120,000, comprising 15 weight % of styrene component and 85 weight % of butadiene component, and having 0.5 weight % of carboxyl group. The polyvinyl acetate solution comprises 40 weight parts of vinyl acetate polymer and 60 weight parts of styrene. The average molecular weight of the vinyl acetate polymer was 40,000. Hollow glass microspheres A-C had an average particle diameter of 40 µ m, a true density of 0.50 g/cm³, a 10%-breakage pressure of 240 kgf/cm² and an elution alkalinity as shown in Table 1. Hollow glass microspheres D and E had an average particle diameter of 8 µ m, a true density of 1.10 g/cm³, a 10%-breakage pressure of more than 700 kgf/cm² and an elution alkalinity as shown in Table 1. Comparative Examples 1-5 are cases where hollow glass mirospheres with elution alkalinity outside the range according to the present invention. Viscosity of resin compositions was measured at a temperature of 40 o C by using a viscometer (Model BHT produced by Brookfield Co.) with T-F rotor at 2.5 rpm after magnesium oxide was added to the resin composition as a thickener and it was matured for a specified length of time inside a thermostatic container at 40 o C. Regarding the workability of SMC, those with practically no stickness and good workability are indicated by "A", those which are workable although with some stickiness are indicated by "B", and those which are strongly sticky and difficult to work with are are indicated by "C." Each SMC was compression-molded at a pressure of 80 kgf/cm² and a flow time of 9 seconds to produce flat-panels (300 mm x 300 mm x 2 mm). In melamine coating, melamine alkyd paint was coated, and baked at 140 o C. In urethane coating, a urethane paint was coated, and baked at 80 o C. After each coated SMC panel was soaked in warm water of 40 o C for 10 days, the number of blisters formed on the coated surface was counted, and adhesiveness was evaluated by a crosscut adhesion test. As shown in Table 1, the SMCs according to the invention have superior workability, and the molded products therefrom are light in weight and have extremely superior paintablity.

Claims: A resin composition containing (a) an unsaturated polyester, (b) a polymerizable monomer, (c) a thermoplastic resin, (d) a polymerization initiator, and (e) a hollow glass microsphere with a true density (measured according to ASTM D2841) of 0.5-1.3 g/cm³ and an elution alkalinity (measured according to ASTM D 3100-78) of 0.05 meq/g or less. A resin composition of claim 1 containing 20-40 weight parts of component (a), 30-70 weight parts of component (b), and 5-30 weight parts of component (c) such that their total is 100 weight parts, and also containing 0.1-5.0 weight parts of component (d) and 5-100 weight parts of component (e). A resin composition of claim 1 wherein the unsaturated polyester (a), the polymerizable monomer (b), and the thermoplastic resin (c) are used by 25 to 35 parts by weight, 40 to 60 parts by weight, and 10 to 25 parts by weight, respectively, such that the three components (a) to (c) make up a total of 100 parts by weight, and in addition the polymerization initiator (d) and the hollow glass microspheres (e) are used by 0.1 to 5.0 parts by weight and 5 to 100 parts by weight, respectively. A resin composition in accordance with claim 1 wherein the hollow glass microsphere has a true density of 0.8 to 1.2 g/cm³ and an elution alkalinity of 0.03 meq/g or less. A resin composition in accordance with claim 1 wherein the hollow glass microspheres have an average particle diameter of 5 to 100 µ m. A resin composition in accordance with claim 1 wherein the hollow glass microsphere has a 10%-breakage pressure of 120 kgf/cm² or more. A resin composition in accordance with claim 1 wherein the unsaturated polyester (a), the polymerizable monomer (b), and the thermoplastic resin (c) make up a total of 100 parts by weight while the hollow glass microspheres (e) are used by 10 to 80 parts by weight. A resin composition in accordance with claim 1 wherein the polymerizable monomer is an aromatic monovinyl monomer. A resin composition in accordance with claim 8 wherein said aromatic monovinyl monomer is styrene. A resin composition in accordance with claim 1 wherein the thermoplastic resin is (i) a styrene-butadiene block copolymer, (ii) polyvinyl acetate, (iii) a saturated polyester with a molecular weight of 300 to 100,000, or (vi) a urethane derivative of such a saturated polyester with a molecular weight of 2,000 to 100,000. A resin composition in accordance with claim 1 wherein the unsaturated polyester has an average molecular weight of 800 to 4,000 and an acid value of 20 to 60. A resin composition of claim 1 further containing alkanepolyol polyacrylate or alkanepolyol polymethacrylate. A molding material obtained by impregnating glass fibers with any one of the resin compositions of claims 1 to 12. A molding material in accordance with claim 13 wherein 10 to 60 per cent by weight of the glass fibers, relative to the whole amount of the resin composition, are used. A molded product obtained by curing the molding material of claim 13. A molded product of claim 15 having a density of 1.2 to 1.7 g/cm³.

Inventors: AKIYAMA KOICHI, AOKI SANJI, HATTA KEN, INO TAKASHI, MISHIMA YASUHIRO, MIYASHITA HIROMU, AKIYAMA, KOICHI, AOKI, SANJI, HATTA, KEN, INO, TAKASHI, MISHIMA, YASUHIRO, MIYASHITA, HIROMU
Applicants: TAKEDA CHEMICAL INDUSTRIES LTD, TAKEDA CHEMICAL INDUSTRIES, LTD.
Application year: 1993
Main classification: C08L67
IPC codes: C08L67, C08K7