Plastic flexible grinding stone

Abstract: A plastic flexible grinding stone comprising a plastic flexible material having with a powder synthetic detergent and an abrasive composed of grains from 3 to 50 µm in diameter, said abrasive being at least one of silica sand, calcium carbonate, alumina, ceramics, and Green Carborundum. The grinding stone is capable of removing simultaneously minute protrusions and strains from coated surfaces of, for example, rolling stock and machines.

Description: The present invention relates to a plastic flexible grinding stone for use in removing, by polishing, small protrusions which are generated on the coated surfaces of rolling stock and industrial machines, as well as in removing stains and oil films from the surface of window glass . When rolling stock is placed in parking lots near to railways and iron works, or in places close to construction sites where coating operations are conducted, iron powder and paint mist contact the coated surfaces of the rolling stock and adhere thereto to form minute protrusions. Such unfavorable protrusions were conventionally removed by polishing the surface using a compound or sand paper. However, when a compound or sand paper is applied to the surface to remove the protrusions, not only the protrusions but also the coated surface are brought into contact with the abrasive thus forming scratches or flaws on the coated surface. As illustrated schematically in FIG. 3(a), it can be seen that this type of polishing suffers very poor operability, because the abrasive force is fully (100%) exerted on the coated surface if the abrasive force is fully applied to the protrusions. With a view to ameliorating the poor operatability of the conventional method, the present inventors have previously proposed in JP-B-4-11335 (the term "JP-B-" as referred herein signifies "an examined published Japanese patent application"), a plastic flexible grinding stone comprising a plastic flexible material having mixed therewith fine abrasive composed of grains from 3 to 50 µm in diameter, such as silica sand and calcium carbonate. When polishing is conducted using the proposed grinding stone, however, as shown in Fig.3(b) no (0%) polishing force is exerted on the coated surface when the polishing force is fully(100%) applied to the protrusions. Accordingly, it can be seen that favorable operability is realized for the protrusions, but that stains cannot be removed from the coated surface. Conventional grinding stones include plastic flexible grinding stones comprising a plastic flexible material having incorporated therein silica sand and calcium carbonate. The protrusions formed by adhesion of minute granules or droplets to the coated surface can be removed completely using those grinding stones, however, stains were left to be removed by other means. An object of the present invention is to obtain a smooth and plain coated surface by polishing, and yet removing stain from the smooth and plane surface. Accordingly, the present invention comprises controlling both the polishing force being exerted on the protrusions and the polishing force being applied to the planar surface. The object of the present invention is accomplished by a plastic flexible grinding stone comprising a plastic flexible material having mixed therewith a powder of a synthetic detergent and at least one type of fine abrasive composed of grains from 3 to 50 µm in diameter and selected from a group consisting of silica sand, calcium carbonate, alumina, ceramics, and Green Carborundum (silicon carbide abrasive). The powder of the synthetic detergent is preferably composed of grains from 30 to 1,500 µm in diameter. The powder of the synthetic detergent is conveniently mixed in an amount of from 0.5 to 20 parts by weight with respect to 100 parts by weight of the flexible material. The size of the grains of the synthetic detergent is preferably confined to the range above, because grains too large in size cause the grains to protrude from the polishing surface, whereas grains too small in size make it difficult to achieve a homogeneously mixed state in the flexible material. The addition of the synthetic detergent is preferably limited to the range above. If the addition is too small, the stain is insufficiently removed from the surface; if the addition is too large, on the other hand, fine abrasives tend to appear excessively on the surface so as to impair the polished surface. The invention will now be illustrated with the aid of the accompanying drawings in which: FIG. 1 is an explanatory figure showing a plastic flexible grinding stone according to the present invention in use; FIG. 2 is a cross sectional view of a plastic flexible grinding stone with the abrasive thereof forming protrusions against the polishing surface; and FIG. 3 is a schematic figure provided as an explanatory means to show the exertion of polishing force against the protrusions and stain. The present invention is illustrated in greater detail referring to a non-limiting example below. It should be understood, however, that the present invention is not to be construed as being limited thereto. EXAMPLE A plastic flexible grinding stone was produced by mixing 100 parts by weight of a petroleum resin (polybutene in the present example) as a plastic flexible material with 65 parts by weight of fine silica sand and calcium carbonate grains from 20 to 30 µm in diameter, and 5 parts by weight of a powder synthetic detergent composed of grains 500 µm in diameter. The powder synthetic detergent may be a soap or any type having a cleaning power. Referring to FIG. 1, the flexible grinding stone 1 above was used to remove a small protrusion 2 (0.5 mm in height and 1 mm in width) from the coated surface. The flexible grinding stone was pressed against a planar coated surface A to form a flat plane on the flexible grinding stone. Fine abrasive 3 and powder synthetic detergent 4 are distributed within a flexible material 5 as shown in FIG. 2. By reciprocating the planar surface of the flexible grinding stone 1 on the coated surface having the protrusion 2 thereon, the small protrusion 2 was removed completely from the coated surface in about 30 seconds. The stain on the coated surface was removed at the same time. A coated surface as plain and smooth as the surface before polishing was obtained free from scratches and flaws by the polishing operation. Referring again to FIG. 2, a pore 4a can be seen to open on the surface in contact with the coated planar surface A, due to the dissolution of the powder synthetic detergent 4. The open pore 4a facilitates the fine abrasive to stick against the polishing surface. In this manner, the polishing speed of the plane surface is accelerated. Hard fine grains such as those of alumina, ceramics, and Green Carborundum may be incorporated in the flexible material as the fine abrasive 3 in the place of the aforementioned grains of silica sand and calcium carbonate. Those fine grains may be used either alone or as a mixture of two or more selected therefrom. The fine abrasive grains in the example were confined to a diameter in the range of 20 to 30 µm, but the size may be freely selected within a range of from 3 to 50 µm depending on the object of polishing. The addition of the fine abrasive such as the fine grains of silica sand and calcium carbonate may be varied within a range of from 60 to 80 parts by weight with respect to 100 parts weight of the flexible material. In removing small protrusions from the coated surface using the plastic flexible grinding stone according to the present invention, the flexible grinding stone is pressed against a flat and hard plane to form a flat surface on the grinding stone. At this stage, the fine abrasives are buried inside the flat surface of the grinding stone to leave no edges thereof sticking out from the flat surface of the flexible grinding stone. When the flat surface of the flexible grinding stone is placed over the small protrusion on the coated surface, the small protrusion bores a small hole on the flat surface of the flexible grinding stone and accommodates itself therein. This stage is illustrated in FIG. 1. When the flexible grinding stone is repeatedly reciprocated on the coated surface along the direction indicated with the arrows shown in FIG. 1, the flat surface of the flexible grinding stone moves with its surface being cut with the small protrusion. Since the fine abrasives are not pressed uniformly by the small protrusion in this stage, the edges of the fine abrasive stick out from the flexible material. Accordingly, the fine abrasive sticking out from the flexible material are brought forcibly into contact with the small protrusion to conduct polishing. The flat surface having formed on the flexible grinding stone is also brought into contact with the coated surface in this case, however, the coated surface suffer no scratches nor flaws because the edges of the fine abrasive do not stick out from the flat surface of the flexible material. Water may be sprayed onto the region on which the flexible grinding stone is moved or onto the flexible grinding stone. By this means, the powder detergent incorporated into the flexible grinding stone dissolves into the water to allow the fine abrasive to be exposed on the surface. The amount of the exposed fine abrasive can be controlled by the amount of the powder detergent being incorporated into the flexible grinding stone. The fine abrasive grains sticking out from the polishing surface immediately slip into the flexible material upon detection of a resistance on the polishing surface. In this manner, the polishing force against a flat surface is exerted at about 1/80 to 1/100 of the force applied to a protrusion (in a case 5% by weight of a powder synthetic detergent is added to the grinding stone). This signifies that a significant force is applied to both the protrusion and the surface stain in conducting polishing as shown in FIG. 3(c); specifically, 0.5 to 3% of the polishing force is applied to the stain with respect to 100% of the force applied to the protrusion. The polishing ability against a flat surface may be controlled in the range of from 1/30 to 1/200 by varying the content of the powder synthetic detergent depending on the object of polishing. The polished state and the removal of the stain were evaluated while changing the addition of the powder synthetic detergent 4 with respect to 100 parts by weight of the flexible material 5 . The results are summarized in Table 1. In the evaluation, the polishing speed signifies the time consumed for removing a protrusion 0.5 mm in height and 1 mm in width, and the speed for removing the stain refers to the time necessary for removing the stain around the protrusion. The frictional force in this case was evaluated from the degree the force applied by the operator on the grinding stone. A flexible grinding stone comprising 65 parts by weight of fine abrasive grains 25 µm in average diameter was used. A conventional flexible grinding stone containing the same fine abrasive but no powder synthetic detergent was also evaluated for comparison. The results are summarized in Table 1. Content of Detergent (pts. wt.) Speed of Polishing (sec) Speed of Stain removal (sec) Frictional Force Evaluation 0 30 Unable to remove Large Poor 0.5 26 48 Medium Fair 3 25 38 Medium Fair 10 20 20 Small Good 20 19 20 Small Good 25 31 22 Small Poor to Fair Table 1 shows that the stain can be rapidly removed by adding 0.5 parts by weight or more of a powder synthetic detergent, but that the polishing speed for a protrusion is lowered by adding the detergent in excess of 20 parts by weight. Furthermore, it can be seen that the polishing can be conducted with a small frictional force by adding 0.5 parts by weight or more of a powder synthetic detergent. In removing both the protrusion and the stain from a coated surface, it is preferred that the protrusion and the stain are removed within a same duration of time, or the protrusion is removed faster than the stain. It is not favorable that the stain be removed faster than the protrusion, because the polishing marks of the protrusion may remain on the coated surface. Accordingly, by using a flexible grinding stone having added therein a powder synthetic detergent at an amount of from 0.5 to 20 parts by weight, the stain can be removed completely upon finishing the removal of the protrusion to yield a favorable operability. Furthermore, in the comparative example above, scratches were found to be formed around the protrusion. However, the examples according to the present invention suffered no scratches or flaws and yielded a flat and smooth surface around the polished area because of the lubricity imparted to the grinding stone. Then, grinding stones containing powder synthetic detergent 4 with varying grain diameter were produced to evaluate the polishing state and the removal of the stain. The results are summarized in Table 2 below. The evaluation was carried out in the same manner in the previous evaluation whose results are summarized in Table 1. A flexible grinding stone comprising 65 parts by weight of fine abrasive grains 25 µm in average diameter was used, and the powder synthetic detergent was added in an amount of 10 parts by weight. Diameter of Detergent (µm) Speed of Polishing (sec) Speed of Stain removal (sec) Frictional Force Evaluation 15 28 40 Medium Poor to Fair 30 24 32 Medium Fair 100 20 28 Small Good 500 20 26 Small Good 1000 23 23 Small Good 1500 24 25 Small Good 2000 30 25 Small Poor to Fair Table 2 shows that the polishing of the small protrusions and the stain removal take a longer time when a grinding stone containing powder synthetic detergent 30 µm or less in diameter is used. Similarly, the removal of small protrusions as well as stain is retarded if grinding stones containing powder detergents exceeding 1,500 µm in grain diameter are used. It is understood also that the grain diameter of the powder synthetic detergent has no influence on the frictional force. In removing both the protrusions and the stains from a coated surface, it is preferred that the protrusions and the stains are removed within the same duration of time, or the protrusion is removed faster than the stain. It is not favorable that the stain be removed faster than the protrusion, because the polishing marks of the protrusion may remain on the coated surface. Accordingly, it can be seen from Tables 1 and 2 that a preferred range of grain diameter for the powder synthetic detergent is from 30 to 1,500 µm, and that the amount of addition thereof is in the range of from 0.5 to 20 parts by weight with respect to 100 parts by weight of the flexible material. By controlling the addition and the grain size of the detergent within these ranges, the protrusion can be polished faster than removing the stain. This signifies that the stain is removed upon completion of the removal of the protrusions, thereby yielding good operability. The plastic flexible grinding stone according to the present invention comprises a flexible material having mixed therewith fine abrasive and powder synthetic detergent. Accordingly, the flexible grinding stone according to the present invention is capable of removing small protrusions and stain from the surface without impairing flat or curved planes such as of coated planes by maintaining a uniform surface against the area to be polished. Furthermore, the grinding stone according to the present invention facilitates rapid operation because it can be worked with a small frictional force. The grinding stone according to the present invention is such that the protrusion can be removed more rapidly than the stain. This not only ameliorates the operability, but also prevents the surface flatness from being impaired by the reciprocal movement of the grinding stone after the protrusion is removed. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the scope thereof which is defined in the appended claims.

Claims: A plastic flexible grinding stone which comprises a plastic flexible material having mixed therewith a powder synthetic detergent and an abrasive composed of grains from 3 to 50 µm in diameter, said abrasive being at least one of silica sand, calcium carbonate, alumina, ceramics, and Green Carborundum. A plastic flexible grinding stone as claimed in claim 1, wherein said power synthetic detergent is composed of grains from 30 to 1,500 µm in diameter. A plastic flexible grinding stone as claimed in claim 1 or claim 2, wherein said powder synthetic detergent is present in an amount of from 0.5 to 20 parts by weight with respect to 100 parts by weight of said plastic flexible material. A plastic flexible grinding stone as claimed in any one of the preceding claims, wherein said abrasive is present in 60 to 80 parts by weight with respect to 100 parts by weight of said plastic flexible material. A plastic flexible grinding stone as claimed in any one of the preceding claims, wherein said abrasive comprises silica sand and calcium carbonate. A method of removing small protrusions and stains from a coated surface, said method comprising rubbing said surface with a plastic flexible grinding stone as claimed in any one of the preceding claims. A method as claimed in claim 6, which includes the step of spraying water onto said coated surface or onto said plastic flexible grinding stone.

Inventors: KODATE TADAO, KODATE, TADAO
Applicants: KODATE TADAO, KODATE, TADAO
Application year: 1993
Main classification: B24D11
IPC codes: B24D15, B24D13, B24D11, B24D3