PREPARATION OF REFRACTORY MATERIALS FROM ASBESTOS TAILINGS

Abstract: A process for producing especially high temperature refractory materials from asbestos tailings, or from calcined products produced from asbestos tailings. The process comprises grinding the asbestos tailings, or the calcined product, to a suitable particle size, mixing the ground particles with magnesium oxide or a magnesium oxide precursor, and heating the mixture to a temperature of at least 1200 DEG C for a suitable length of time to form a large proportion of forsterite in the resulting product. The amount of magnesium oxide or precursor should preferably be such that the MgO:SiO2 ratio in the starting materials is at least 1.2, which usually requires an amount in the range of 10 to 25 % by weight, based on the weight of the asbestos tailings. Moreover, the particle size of the asbestos tailings or calcined product should preferably be in the range of -1.7 mm +/- 0.1 mm. The resulting refractory product has a fusion point above about 1660 DEG C and can be used in contact with molten steel or the like, particularly when mixed with a bridging agent such as graphite.

Description: PREPARATION OF REFRACTORY MATERIALS FROM ASBESTOS TAILINGS TECHNICAL FIELD This invention relates to refractory materials produced from tailings from asbestos mines. More specifically, this invention yields such refractory materials which are suitable for heat intensive metallurgical applications, such as for example in the taphole nozzles of sliding gate systems in steel mill ladles. BACKGROUND ART Asbestos deposits normally occur in certain types of silicate rock which contain only about 5 to 10% by volume of asbestos fibres. Consequently, separation of the fibres from asbestos ore leaves large quantities of unwanted tailings which accumulate at or near extraction or processing sites. There is therefore a need to find novel commercial applications for these by-products of asbestos mining and refining operations. Chrysotile asbestos tailings normally contain a substantial proportion of hydrated magnesium silicates referred to as serpentine. Other components which occur with serpentine rock are brucite Mg(0H) 2 and hematite- magnetite (Fe 2 0 3 -Fe 3 0 4 ) . Deposits of nickel may also occur in the rock. Known potential uses for asbestos tailings include the use of the tailings as a source of nickel extracted by magnetic separation of nickel- and iron-rich magnetic components; the transformation of the tailings into mineral wool by melting with carbon and forming fibers by blowing air through the resulting molten silicate; and the use of the tailings as a source of magnesium and/or magnesium compounds obtained by acid leaching and crystallisation. It is also known to calcine serpentine in order to produce sintered angular shaped granules useful as sandblasting or heat accumulating material, or to produce granular products useful as foundry mold sands. However, conventional calcination methods give rise to a number of drawbacks. For example, the conventional process of calcining serpentine results in the production of a synthetic harzburgite rich in a pyroxene of the silicate group and commonly referred to as enstatite. Enstatite is further subdivided into protoenstatite and clinoenstatite depending on its resulting crystallographic structure. However, these products have relatively low melting or softening points (less than 1,600°C), and are therefore not useful as refractory materials for particularly high temperature operations, e.g. in the production of steel which involves exposure to temperature in the region of 1,700°C for several hours. The known methods of serpentine calcination normally involve heating the serpentine to a temperature of about 1,300°C, whereby the following chemical reactions are said to take place: (i) dehydration encountered at 600 to 780°C to form an anhydrous magnesium silicate: Mg 3 (Si 2 0 5 ) (0H 4 ) > 3Mg0.2Si0 2 + 2H 2 0 (serpentine) (anhydrous magnesium silicate) (ii) conversion of the anhydrous magnesium silicate into forsterite (Mg 2 Si0 4 ) and free silica (Si0 2 ) , which starts to occur at approximately 800 to 900°C: 2 (3 Mg0.2Si0 2 ) > 3Mg 2 Si0 4 + Si0 2 (forsterite) (free silica) (iii) reaction of forsterite with free silica above 1,000°C thereby forming enstatite (MgSi0 3 ) : Mg 2 Si0 4 + Siθ 2 > Mg 2 Si0 6 (or 2 MgSi0 3 ) (enstatite) As previously stated, such enstatite-rich products can find application as, for example, foundry mold sands or backing sand mixes. However, the product is unsuitable for higher temperature applications in which the product is required to have superior refractory properties, for example, in steel or other high temperature smelting operations. More specifically, enstatite rich-products are unsuitable as ladle and ladle nozzle sands currently utilized, for example, in steel mills and foundries because the product is unable to withstand the necessary temperatures and holding times involved. Sands currently used in steel mill ladles are mostly silica, zircon and chromite based. Although such products have good granulometry, packing density and purity, they are expensive to produce. Moreover, many of these products have various degrees of toxicity. Indeed, the manipulation and use of many of such products causes the liberation of silicious dusts which are known to engender among workers the serious medical condition known as silicosis. To produce a synthetic olivine from asbestos tailings suitable for extremely high temperature applications, it is theorized that a high proportion of forsterite (Mg 2 Si0 4 ) should be produced in the final product. This is because of the favorable refractory properties of forsterite compared to enstatite and because the fusion point of forsterite is much higher than that of enstatite. Aϊtcin, in Am. Ceramic Society Bull.. Vol. 61, No.8 (1982) pp. 857 to 860, teaches calcining and sintering non-magnetic portions of asbestos tailings to produce a refractory product. A process is described whereby fine asbestos tailings are fired at 1,550°C. However, the resulting refractory product is rich in enstatite. The forsterite content of the refractory product will be a function of the basicity index (Mg0:Si0 2 ) of the asbestos tailings. Hence the forsterite content of the final product is limited by the basicity index of the raw material. For example, a typical fusion product of calcined asbestos tailings consists of 33% by volume of forsterite and 54% by volume of enstatite, the remainder being essentially hematite (Fe 2 0 3 ) . Accordingly, there remains a need to realize an efficient method of producing a synthetic olivine composition from asbestos tailings for applications such as, for example, high temperature ladle nozzle sands, which method will overcome the drawbacks of the prior art. A first object of the present invention is to provide a process of treating asbestos tailings in order to convert such tailings into a commercially useful product. A second object of the invention is to provide a process of producing, from asbestos tailings or other ores of similar composition, synthetic olivine sands having good refractory characteristics at very high temperatures, such as those encountered during the manufacture and treatment of steel in steel mill foundries. Another object of the invention is to produce a forsterite-rich product from a serpentine mineral or from a previously-calcined serpentine mineral containing enstatite. Another object of the invention is to provide a novel refractory material suitable for use at very high temperatures. Yet another object of this invention is to provide a novel non-toxic sand exhibiting higher refractoriness, greater density and a lower coefficient of thermal expansion than many conventional high temperature foundry sands. DISCLOSURE OF INVENTION According to one aspect of the present invention, there is provided a process of producing refractory material of high forsterite content, which comprises: heating serpentine-containing asbestos tailings, or an enstatite- containing product produced by calcining serpentine- containing asbestos tailings, with magnesium oxide or a magnesium oxide precursor at a temperature of about 1,200°C or above for a time sufficient to form said forsterite-rich product. The invention also relates to the novel refractory materials produced by the process above and to uses of such materials. It will be noted that the present invention can be used to produce a high-melting refractory material either from asbestos tailings containing serpentine or from a previously calcined product from such tailings which contains enstatite and has a relatively low melting point (fusion temperature) of about 1600"C or lower. The product of the present invention is a synthetic olivine which preferably contains at least 40% by volume of forsterite, more preferably at least 60% by volume of forsterite, and which optimally consists almost entirely of forsterite with very little or no enstatite (preferably less than 10% by volume) . The product preferably has a melting (fusion) point of about 1660°C or higher, and preferably above about 1700°C. A special advantage of the synthetic olivine of the invention is that it is readily useful in a variety of applications where other refractory sands cannot withstand the required operating temperatures, mechanical stresses or holding times. The synthetic olivine of this invention is also free of asbestos fibers, and is essentially non-toxic. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic representation of apparatus used in accordance with this invention; Figure 2 is an example of a rotary kiln which can be used to carry out the present invention; Figure 3 is a graphical representation of analyses and basicity indices of the synthetic olivine sands obtained in tests carried out in accordance with this invention; Figure 4 is a graphical representation of the effect of particle sizes on the fusion points of the synthetic olivine sands obtained in accordance with this invention; Figure 5 is a graphical representation of the effect of the basicity indices on the fusion points of synthetic olivine sands obtained in accordance with this invention; Figure 6 is a schematic cross-section of one possible application of the synthetic olivine sands of this invention in an industrial setting; Figure 7 is a schematic example of a cross-section of the synthetic olivine sands of Figure 6 during a smelting process. BEST MODES FOR CARRYING OUT THE INVENTION In the present invention, a magnesium compound is used during the calcination of asbestos mine tailings, or during the heating of a synthetic enstatite-containing product previously produced by calcining such tailings, at a temperature of about 1,200°C or higher, in order to produce a synthetic olivine compound which is rich in forsterite (Mg 2 Si0 4 ) rather than enstatite (MgSi0 3 ) . Preferably, as noted above, this synthetic olivine compound will contain more than 60% by volume of forsterite and less than 10% by volume of enstatite. Without wishing to be bound to any particular theory, it is believed that, during the heating or calcining step, the presence of the added magnesium compound prevents the forsterite resulting from reaction (ii) above from degrading, via chemical reaction with free silica, into enstatite by reaction (iii) . Alternatively, the free silica produced by reaction (ii) may be made to react with the added magnesium compound instead of reacting with the forsterite according to reaction (iii) . Consequently, a forsterite-rich compound is obtained. In other words, it is believed that a forsterite-rich chemical equilibrium is obtained when the reaction of anhydrous magnesium silicate into enstatite is surpassed by the reaction of free silica with magnesium. This is indicated by reaction (iv) shown below: (iv) reaction of free silica above approximately 1,200 "C with magnesium oxide: Siθ 2 + 2MgO > Mg 2 Si0 4 (forsterite) Alternatively, to achieve similar results, previously calcined asbestos tailings, rich in enstatite, can be heated to a temperature of about 1200°C or higher in the presence of suitable amounts of magnesium oxide or a precursor thereof. It is inferred that some enstatite is reacted back into forsterite, and free silica is reacted with magnesium to form additional forsterite. The precise composition of the product obtained in accordance with the present invention will normally be dependent on the initial index of basicity (Mg0:Si0 2 weight ratio, referred to as "lb") of the batch of serpentine used, the amount of magnesium oxide or precursor, the calcining temperatures, and the granulometry of the reactants. Table 1 below provides typical compositions of tailings from asbestos mines in the Province of Quebec, Canada, and shows the index of bascisity (lb) of these materials. TABLE 1 Typical Chemistries of Tailings from Chrysotile Mines Loss on ignition The amount of magnesium oxide or precursor required in order to ensure a high percentage of forsterite in the product depends on the initial lb ratio, which may range from about 0.8 to 1.2. In theory, lOOg of pure serpentine would produce 10.8g of silica according to reaction (ii) above, which would require the presence of 14.5g of magnesium oxide for complete reaction with the silica according to reaction (iv) . If an excess of magnesium oxide is provided, this is not harmful because it remains unreacted in the product as periclase which itself has a high fusion temperature. In general, therefore, the required amount of Mgo is in the range of 10-25% by weight, and is more preferably at least 15% by weight, based on the amount of asbestos tailings. Another way of expressing the amount of MgO required is to state that the lb of the starting materials (serpentine and MgO or precursor) should preferably be in the range of 1.34 to 1.68. In carrying out the present process, it is not essential to use magnesium oxide as such since any magnesium compound which yields magnesium oxide under the reaction conditions (i.e. a magnesium oxide precursor) can be employed, such as for example magnesium hydroxide, magnesium carbonate, magnesium sulfate, or other chemical equivalents of magnesium oxide. Naturally, when a magnesium oxide precursor is used, its relative amount should be calculated as magnesium oxide. At a given MgO:Si0 2 (lb) ratio, the fusion temperature of the calcined product increases in direct proportion to the fineness of the particles of the serpentine starting material, possibly because of better diffusion of the magnesium oxide into the grains of the serpentine (or forsterite-enstatite, if the reaction is carried out on a previously calcined tailings product) . The preferred size range of the serpentine (or forsterite-enstatite) is -1.68mm, in diameter. If necessary, the serpentine starting material may be subjected to a preliminary grinding step to reduce the particle size as required. The size of the particles of MgO or precursor is not critical, but these particles are desirably of similar size to the serpentine particles in order to assure good distribution and mixing of the two kinds of materials. It is preferable to form granular agglomerates of the particles of tailings and the particles of magnesium oxide (or precursor) by mixing these materials together with water and a binder which remains present at reasonably high temperature in order to form a paste and then to making granules from the paste. The binder prevents disintegration of the granules during the calcination step, which could result in loss of the magnesium oxide dust from the calciner and an uneven ratio of MgO to Si0 2 in the heated granules. The size and strength of the granules can be controlled by the amount and dilution ratio of the binder in the aqueous solution. Usually, about 3 to 10% by weight of the binder solution is required to form suitable granules, and an amount of about 5% is normal, depending on the binder chosen. An example of a suitable binder solution is an aqueous solution of MgS0 4 . The mixture of starting materials employed in the present invention is heated at a temperature of at least 1200°C, and preferably at a temperature in the range of 1200°C to 1500°C, for a length of time necessary for the desired reactions to reach equilibrium. Ideally, the calcination temperature is around 1460°C and the reaction time is usually at least about one hour. The resulting products, particularly those having lb ratios over about 1.2, have suitable characteristics with respect to size distribution, packing ability, thermal resistance and sintering properties for utilization as ladle sand or for similar refractory uses. It is especially desirable to mix the refractory product of the invention with graphite (or other suitable so-called bridging agent) prior to use of the material in refractory applications. The graphite helps the refractory material to form a low thermal conductivity protective sintered crust when exposed to high temperatures. The amount of graphite or other bridging agent is usually in the range of 5 to 15% by weight of the resulting mixture, and more usually 5 to 10% by weight. The major properties required for ladle sands applications are refractoriness, size distribution, high degree of packing, low thermal expansion, and ability to form a suitable crust in the upper nozzle. The most common conventional sands used as nozzle materials are silica, natural olivine and zircon with fusion points ranging from 1,430°C to 1,760°C, 1,540°C to 1,760°C and 2,040°C to 2,220°C, respectively. The olivines produced by calcining serpentine with MgO according to the present invention have fusion points ranging upwardly from 1,610°C to more than 1,680°C depending on the nature of the composition, and particularly on the MgO:Siθ 2 (lb) ratio. Preferably, the fusion points are above 1,660°C. The high thermal resistance of the synthetic olivine produced according to the present invention in the presence of liquid steel makes it suitable also for other applications in steelmaking, namely, in castables, plastic and fire bricks, and gunning and ramming materials resisting to temperatures over 1650°C. The process of the invention may be carried out continuously in an apparatus of the type shown in schematic form in Figure 1. In this apparatus, asbestos tailings (previously ground to a desired particle size) are fed from a hopper 10 through flow control valve 11 to a conveyor belt 12. The belt then conveys the serpentine particles beneath a stream of magnesium oxide or precursor particles from hopper 14. The resulting powder mixture is then conveyed beneath a stream of an aqueous solution of an inorganic binder from tank 15. The resulting paste-like mixture is deposited in a mixer (granulator) 16 and the emerging granules are fed into the entrance of a downwardly inclined rotary kiln 17 in which the required calcination takes place. The kiln 17 is shown in greater detail in Figure 2. The granules from mixer 16 are fed to input funnel 21, into feeding zone 22 and proceed to a pre-heating zone 23. Dehydration of the serpentine begins in the pre-heating zone 23. The pre-heated material then proceeds to a static furnace calcining and sintering zone 24 where it reaches a desired temperature in the range of 1,200 to 1,500°C. The calcined material then reaches a cooling zone 25, from which the final product is collected. The material has a residence time in the kiln 17 of about one hour. The invention is illustrated by the following Examples but should not be construed as limited thereto. EXAMPLE 1 A test was carried out to determine the effect of the size of raw serpentine particles and of the amount of MgO added to the serpentine on the fusion point of the calcined products. Heat treatments of various starting materials were carried out in a rotary kiln of the type shown in Figure 2 , subjecting the starting materials to an increasing temperature from ambient to 800°C in a first step, and then heating was pursued up to 1350"C in a static furnace. The total retention time was 2 hours. In each test, granulation of the serpentine-MgO mixture was employed to prevent kiln loss during the calcination stage. The pellet size and strength were controlled by the amount and dilution ratio of a magnesium sulfate binder in the aqueous solution. Table 2 shows the composition of the serpentine-MgO mixtures tested, as well as the chemical analyses of the corresponding calcined products and their fusion temperature (T f ) . Calcining temperatures reached approximately 1,350°C in the static furnace except as otherwise indicated in Table 2. The temperatures of fusion were measured with a heating microscope calibrated to a maximum reading of 1,680°C. The MgO:Si0 2 (lb) ratio was calculated before and after the heat treatment. The ratio values are plotted in the graph shown in Figure 3 along with comparative analytical results. Table 2 Composition of the Feed and Products of Calcination * Calculated from the head analyses of the mixed serpentine and magnesium oxide. ** These two products started to soften at 1,680°C. *** Calcining temperature reaching 1,425°C. **** Calcining temperature reaching 1,460°C. Figure 4 shows the relationship between the serpentine particle size and the fusion temperature of the resulting products. The graph shows that, at a given MgO:Si0 2 ratio (1.2 in this case), the fusion temperature of the calcined product increases with the fineness of the raw serpentine. Since pure forsterite has an MgO:Si0 2 ratio of 1.34 with a fusion temperature of 1890°C, it is significant that any compositions having a higher MgO:Si0 2 ratio have resulting fusion temperatures greater than 1680°C (which was the highest detectable limit of the heating microscope used in this Example) . The effect of the amounts of MgO additions on the fusion temperatures of the products is graphically illustrated in Figure 5. EXAMPLE 2 This Example shows the testing of forsterite-rich synthetic olivine produced according to the present invention as ladle sand for a steel slide-gate system. Three synthetic olivine blended products according to the invention were prepared and tested for their thermal resistance to liquid steel at high temperature for extended periods. These products are identified in Table 3 with the corresponding basicity index and major mineralogical components. Table 3 Blended Products to be Tested as Ladle Sand * Maghemite Of-Fe^), hematite (Fe^), magnesioferrite (MgFe 2 0 4 ) ** Test numbers refer to test numbers in Example 1. Note: No silica (Si0 2 ) was identified in the products. A proper grain size distribution insures high packing. The sand, therefore, should report on several successive screens in order to avoid too many interstices between the grains. Table 4 shows a comparison of the size of the forsteritic olivines of this invention with other types of sands. Table 4 Comparative Screen Tests of Ladle Sands Other physical characteristics of the olivine sands assure good packing qualities. These characteristics are namely, specific gravity, bulk density, and percentage of void volume. Table 5 shows such physical characteristics for each of the synthetic olivines. Table 5 Physical Properties of Synthetic Forsterite-rich Sands Both the relatively high specific gravity and a semi- angular shape of the olivine products have resulted in good free-flowing material. Finally, two other factors making the novel sands suitable for taphole nozzle are a low thermal expansion coefficient (1.09 x 10 "5 ) and high hardness (5.5 on Mohs scale) for all three olivine products. In contact with liquid steel, a satisfactory ladle sand must form a low thermal conductivity layer, known as a crust, at the top of the nozzle. This crust is broken by the static pressure of steel when the sliding gate is opened to tap the furnace. Sintering is obtained either from natural occurrence, such as by the presence of feldspar in silica sands, or by making admixtures to this effect, e.g. via additives like graphite to chromite, silica to zircon, etc. The latter combination produces a glassy bridge at about 1540°C by the melting of free silica and the decomposition of zircon into zirconia and silica. As illustrated in Figure 6, to assess the suitability of the synthetic olivine products as ladle sands, tests were conducted in an electrical induction furnace 60 having no tapping hole at the bottom. A refractory mold 61, filled up with an olivine-graphite mixture 62 (containing 10% graphitic carbon) , was installed at the bottom of the furnace and was surrounded with rammed mullite 63 (to avoid side heat transfer) . The refractory mold 61 had a conical section 64 in its upper section and the sand was heaped into a "flower pot" topping 65 in this conical section. The top surface of the sand was protected by a steel plate 66 over which was placed a 25 kg steel ingot 67. The metal was melted and maintained at pre-selected temperatures, i.e., 1600°C, 1650°C and 1700°C, for periods of time varying from 1 to 2 hours as schematically illustrated in Figure 7. Since the thickness of a crust 70 formed at the top of the refractory bed 62 depended on the temperature of the liquid steel 72 and the contact period between the liquid metal and the ladle sand, the two factors were investigated simultaneously by increasing both the temperature and the length of time as shown in Table 6. Table 6 Conditions of Nozzle Testing with Forsteritic Olivine After the test was completed, the furnace 60 was tilted and the liquid steel 72 poured. The refractory crust 70 formed at the interphase between the olivine-graphite sand 74 and the liquid steel 72 was sufficient to retain the unaltered olivine-graphite sand 74 in the mold, which was pulled out for examination. It was found in every test that the crust 70 was thin enough to be easily broken by a small rod. This indicated that the sintered layer would break under the pressure of the liquid steel in an industrial sliding-gate system. EXAMPLE 3 Five tests were carried out in which serpentine tailings were heated with magnesia precursors MgC0 3 and MgS0 4 . The conditions and results are shown in Tables 7 and 8 below. Table 7 Granulometry, composition, and basicity index of serpentine, additives and resulting mixtures Table 8 Thermal treatment conditions, analysis of olivine product at measurement of control temperatures EXAMPLE 4 Seven samples were produced according to the process of the invention and analyzed for the content of various mineral phases. The results are shown in Tables 9 and 10 below. Table 9 Analyses of the X-ray powder-diffraction patterns gives the following uncorrected compositions (expressed as volumetric percentages) : Correcting these figures for the respective I/I c ratios, and normalizing, gives the following quantitative compositions: Table 10 Phase ICDD# 4. 65 58 66 75 81 52 54 19 14 10 16 20 26 13 11 8 14 27 15 quartz 5-490 SiO, Total 100 100 100 100 100 100 100 lb ratio 1.27 1.39 1.48 1.48 1.48 1.48 1.48 Numerous modifications and variations of the present invention may be made, in light of the above teachings, without departing from the basic spirit of the present invention. Accordingly, it will be appreciated by those skilled in the art that, within the scope of the appended claims, the invention may be practised otherwise than as specifically described herein. INDUSTRIAL APPLICABILITY The process of the invention is easily applied industrially because the starting materials are readily available in large quantities and the procedures are easily carried out using conventional heating equipment.

Claims: Claims 1. A process of producing refractory material in which a particulate starting material comprising serpentine- containing asbestos tailings or an enstatite-containing product produced by calcining serpentine-containing asbestos tailings, is heated to a temperature of at least about 1,200°C, characterized in that said particulate material is mixed with particulate magnesium oxide or magnesium oxide precursor to form a mixture which is subjected to a heating step. 2. A process according to claim 1 characterized in that the amount of said magnesium oxide or precursor is 10 to 25% by weight based on the weight of said starting material. 3. A process according to claim 1 characterized in that the amount of said magnesium oxide or precursor is at least 15% by weight based on the weight of said starting material. 4. A process according to claim 1 characterized in that such an amount of said magnesium oxide or precursor is mixed with said starting material that the ratio of MgO:Si0 2 in said mixture is at least 1.2. 5. A process according to claim 1 characterized in that such an amount of said magnesium oxide or precursor is mixed with said starting material that the ratio of Mg0:Si0 2 in said mixture is in the range of about 1.34 to 1.68. 6. A process according to claim 1, claim 2, claim 3, claim 4 or claim 5, characterized in that said starting material has a particle size in the range of less than 1.68 mm. 7. A process according to claim 1, claim 2, claim 3, claim 4 or claim 5, characterized in that said mixture is heated to a temperature in the range of about 1200°C to 1500°C. 8. A process according to claim 1, claim 2, claim 3, claim 4 or claim 5, characterized in that said mixture is heated to a temperature of about 1460°C. 9. A process according to claim 1, claim 2 , claim 3, claim 4 or claim 5, characterized in that said heating is continued for at least 1 hour. 10. A process according to claim 1, claim 2, claim 3, claim 4 or claim 5, characterized in that said mixture is formed into granules prior to said heating step by adding a solution of a binder in a solvent to form a paste and forming granules from said paste. 11. A synthetic refractory compound having a fusion point of at least 1610°C and containing at least 40% by volume of forsterite, characterized by said compound having been produced by a process according to claim 1, claim 2, claim 3, claim 4 or claim 5. 12. A compound according to claim 11 characterized by having a fusion temperature of at least 1680°C and containing at least 60% by volume of forsterite. 13. A synthetic refractory compound derived from asbestos tailings having a fusion temperature of at least about 1610°C, characterized in that the compound comprises at least 40% by volume of forsterite. 14. A compound according to claim 13 characterized by having a fusion temperature of at least about 1680°C and comprising at least 60% by volume of forsterite. 15. A refractory composition comprising periclase and a refractory synthetic compound derived from asbestos tailings, characterized by having a fusion point of at least 1610°C and containing at least 40% by volume of forsterite. 16. A composition according to claim 15 characterized in that said refractory synthetic compound has a fusion point of at least 1680°C and contains at least 60% by volume of forsterite. 17. A composition according to claim 15 characterized in that said refractory compound is a product produced by a process according to claim 1, claim 2, claim 3, claim 4 or claim 5. 18. A composition according to claim 13 or claim 14 characterized by further comprising particles of graphite. 19. A composition according to claim 15 or claim 16 characterized by further comprising particles of graphite. 20. A refractory mixture suitable for exposure to molten steel comprising a bridging agent and a refractory compound characterized in that said refractory compound has a fusion temperature of at least 1610°C and contains at least 40% by volume of forsterite.

Inventors: AOTA JAY, HUARD YVAN, MATHIEU GILLES, AOTA, JAY, HUARD, YVAN, MATHIEU, GILLES
Applicants: SABLES OLIMAG INC, LES SABLES OLIMAG INC.
Application year: 1993
Main classification: B22C1
IPC codes: B22D41, C04B35