Thermoplastic olefin elastomers and process for their preparation

Abstract: Disclosed are thermoplastic elastomeric compositions comprising: A) from 10 to 80% by weight of one or more crystalline polymer of propylene containing from 0.05 to 15% in moles of ethylene unsaturations, or a mixture of the above polymer with a saturated thermoplastic olefin polymer in quantities lower than or equal to 80% by weight; B) from 20 to 90% by weight of an unsaturated elastomeric olefin polymer; said compositions having been dynamically cross-linked with a cross-linking agent comprising a free radical generator.

Description: The present invention relates to thermoplastic elastomeric compositions obtained by mixing and dynamically cross-linking a thermoplastic olefin polymer, which comprises an unsaturated polyolefin, and an unsaturated elastomeric olefin polymer. Thermoplastic elastomeric compositions obtained by mixing in the molten state a thermoplastic olefin polymer with an unsaturated elastomeric olefin polymer (such as an ethylene-propylene-diene rubber, known as EPDM) and dynamic cross-linking, such as the ones described in published European patent application 213 285 in the name of the Applicant, are known in the art. By dynamic cross-linking one means that the cross-linking agent is added to the polymers described above before or during mixing, and said mixing is continued in the molten state during the cross-linking stage. The practical interest of compositions thus obtained is due to the fact that, although they can be processed and molded with apparatus and processes typical of thermoplastic polymers, they supply products which have elastomeric characteristics that, without being high, are in fact satisfactory for many application sectors, such as the construction, automotive and appliance industries. Thermoplastic resin compositions having a good balance between mouldability and elastic properties are disclosed in European Patent Applications 390 451 and 486 293. These compositions are obtained by crosslinking a mixture of an unsaturated thermoplastic olefin polymer with an unsaturated elastomeric olefin polymer. Useful unsaturated thermoplastic olefin polymers, however, are only those based on the copolymerization of propylene with particular non-conjugated diene monomers. Now the Applicant has unexpectedly found that the thermoplastic elastomeric olefin compositions of this type possess improved elastic properties, as can be seen by the particularly low compression set values, if the unsaturated thermoplastic polymer used in the preparation thereof derives from the copolymerization of propylene with a conjugated diene monomer. Therefore, the present invention provides thermoplastic elastomeric compositions comprising: A) from 10 to 80% by weight, preferably from 20 to 60%, of one or more crystalline, isotactic polymers of propylene containing from 0.05 to 15% in moles, preferably from 0.1 to 10%, of ethylene unsaturations deriving from the copolymerisation with a conjugated C 4 -C 10 diene (unsaturated polymer), or a mixture of the above polymer with a saturated thermoplastic olefin polymer in quantities lower than or equal to 80% by weight; B) from 20 to 90% by weight, preferably from 40 to 80%, of an unsaturated elastomeric olefin polymer; said compositions having been dynamically cross-linked with a cross-linking agent comprising a free radical generator. The unsaturated polymers used as component (A) are isotactic, or mostly isotactic, propylene polymers, preferably having an isotactic index in xylene at 20°C greater than 70%, and comprise copolymers of propylene with ethylene and/or C 4 -C 10 α-olefins. The ethylene and/or C 4 -C 10 α-olefin content in the copolymers is preferably from 1 to 30% by weight, more preferably from 1 to 20%. Examples of C 4 -C 10 α-olefins are: 1-butene, 1-hexene, 1-octene, 4-methyl-1-pentene and 6,6-dimethyl-1-pentene. The ethylene unsaturations in the above polymers can be introduced directly in synthesis, copolymerizing minor quantities of a conjugated C 4 -C 10 diene. Examples of the above dienes are: 1,3-butadiene, isoprene and 1,3-pentadiene. The synthesis of the polymers containing the unsaturations is carried out by known polymerization techniques with coordination catalysts, operating in liquid phase, or gas phase, or a liquid-gas phase. The catalysts used are coordination catalysts known in the art, preferably high yield and high stereospecificity ones, comprising a titanium compound supported on a magnesium halide, in particular MgCl 2 . In order to obtain the molar quantities of ethylene unsaturations mentioned above, one copolymerizes the same molar quantities of the above mentioned dienes. Examples of the above mentioned polymerization processes are described in published European patent application n. 171 025, in the name of the Applicant. As explained in said European patent application, the conjugated dienes can be bonded to the polymer chains in position 1,2 or 1,4, so that the ethylene unsaturations are present along the chain (position 1,4) or in branched groups (position 1,2). By using the coordination catalysts mentioned above, one generally obtains introductions of the conjugated diene both in 1,2 position and 1,4 position. Also included within the definition of the present invention are the thermoplastic elastomeric compositions wherein part of the unsaturated polymer constituting component (A) is substituted by a saturated thermoplastic olefin polymer. This way one obtains a mixture of a saturated and an unsaturated polymer. Examples of the above mentioned saturated polymers are the ethylene homopolymers, and the crystalline copolymers of ethylene with α-olefins, such as HDPE, LLDPE, LDPE, or with other nonhydrocarbon monomers, such as vinyl acetate, acrylic acid, methacrylic acid, acrylic and methacrylic esters, maleic anhydride, or homopolymers and copolymers of the types previously defined for component (A), where no ethylene unsaturations are introduced. In order to obtain the best elastic properties in the final compositions, it is best if the saturated polymers do not constitute over 50% by weight of component (A) in the formulations defined above. Examples of elastomeric olefin polymers that can be used as component (B) are the mainly amorphous terpolymers of ethylene, containing from 20 to 80% by weight of propylene and/or C 4 -C 10 α-olefins, and from 0.5 to 15% by weight of a conjugated or nonconjugated C 4 -C 10 diene. Examples of α-olefins and C 4 -C 10 dienes are those already given for component (A). Particularly preferred elastomeric polymers are the ethylene/propylene/2-ethylidene-5-norbornene terpolymers containing from 25 to 70% by weight of propylene, and from 4 to 10% by weight of 2-ethylidene-5-norbornene. The compositions of the present invention are prepared by a process comprising a dynamic cross-linking step consisting of subjecting components (A) and (B) to mixing at a temperature higher than or equal to their softening or melting point, in the presence of the cross-linking agent comprising a free radical generator, that can be added before, during or after the first mixing step, continuing said mixing throughout the cross-linking step. During the mixing step one obtains a fine dispersion of component (B) in component (A). Preferably, component (B) is dispersed in the form of particles having a diameter ranging from 0.5 to 1 micrometer. The cross-linking agent can be added before, during, or after the above mentioned mixing stage. The mixing can occur in an internal mixer, in an extruder, or in a system comprising an internal mixer and an extruder. The operation can also take place by using a number of machines placed in series, where the intimate mixing and homogenization of the compositions occurs in the first machine, and the cross-linking occurs in the others, always under mixing conditions. Mineral fillers, carbon black, dyes, plastifiers, stabilizing agents, extender oils, and other conventional additives which are typically used in unsaturated elastomeric olefin polymer compositions, can be present in the composition that is subjected to mixing and dynamic cross-linking. The cross-linking step is carried out at temperatures preferably ranging from 170 to 230°C, by way of adding a free radical generator preferably consisting of an organic peroxide. The free radical generator is preferably added in quantities ranging from 0.1% to 10% by weight, more preferably from 1% to 5% by weight with respect to the sum of components (A) and (B). Examples of peroxides that can be used as free radical generators are: 1,1-bis(tert-butylperoxy)3,5,5-trimethyl cyclohexane; tert-butylperbenzoate; 2,2-bis(tert-butylperoxy)butane; dicumyl peroxide; di-tert-amyl peroxide; di-tert-butyl peroxide; 1,3-bis(tert-butylperoxy isopropyl)benzene. The cross-linking action can also be supported by the addition of cross-linking coagents, such as: triallyl cianurate; triallyl isocianurate; maleimides; allyl acrylates; divinylbenzene; polybutadiene, and benzoquinone dioxime. Particularly indicated for this purpose are some unsaturated furfuryl aldehyde condensation products with hydrazine, acrolein; acetone, acrylamide or acrylonitrile, such as: i-difurfuralaldazine; 3(α,furyl)acrolein; 1,5-difurfuryl-1,4-pentadiene-3-one; 3-(α-furyl)acrylamide; 3-(α-furyl)acrylonitrile. The preferred compound is the difurfuralaldazine. Preferably, the cross-linking coagents are added in quantities ranging from 5% to 60% by weight with respect to the free radical generator. The following examples are given in order to illustrate and not limit the present invention. Examples 1-4 The following polymers are introduced in a BRABENDER PLASTI-CORDER® PLD651 internal mixer in the quantities specified in Table 1 as percentages by weight: U-PP 1: propylene/1,3-butadiene copolymer containing 3.9% by weight of butadiene (2% as 1,2 monomeric units, and 1.9% as 1,4 monomeric units) corresponding to 3% in moles of unsaturations, and having an intrinsic viscosity [η]= 2.3 dl/g (measured in tetraline at 135°C), and fraction soluble in xylene at 20°C of 6.9%; U-PP 2: propylene/1,3-butadiene copolymer comprising 4.2% by weight of butadiene (2% as 1,2 monomeric units, and 2.1% as 1,4 monomeric units) corresponding to 3.2% in moles of unsaturations, and having an intrinsic viscosity [η]= 2.3 dl/g measured in tetraline at 135°C), and fraction soluble in xylene at 20°C of 7.0%; DUTRAL® TER 536E2: ethylene/propylene/2-ethylidene-5-norbornene (ENB) terpolymer comprising 29% by weight of propylene and 8% by weight of ENB, extended with 50% by weight of oil and having a Mooney ML (1+4) viscosity at 125°C = 43. The content was stirred for 3 minutes, then the extender oil and zinc oxide were added, and finally the PEROXIMON® F40 [ 1,3-bis(tert-butylperoxyisopropyl)benzene peroxide] and the VP3 difurfuralaldazine cross-linking coagent were added in the quantities shown in Table 1 as percentages by weight. The mixing was allowed to continue for an additional 4 minutes, and the content was then discharged. The following determinations were made on the product thus obtained (as reported in Table 1): PROCESSABILITY. Determined by way of a SOMEF® single screw extruder with an inside diameter of 15 mm, length/diameter ratio (L/D) = 20, die diameter 2.5 mm, operating at 230°C and with a flow rate of 9.5 cm 3 /min. The head pressure is measured in MPa. COMPRESSION SET. Determined by ASTM D-395, measured on specimens maintained at 100°C for 22 hours. 1 2 3 4 U-PP 1 6.50 6.50 6.50 6.50 U-PP 2 6.50 6.50 6.50 6.50 Dutral® TER 537 E2 64.00 64.00 64.00 64.00 Extender oil 8.00 8.00 8.00 8.00 Zinc Oxide 9.00 10.40 9.22 8.07 Peroximon® F40 6.00 4.00 5.00 6.00 VP3 --- 0.60 0.78 0.93 Pressure (MPa) 8.5 16.0 17.5 18.5 Compress.set % 17 15 9 8 Examples 5-8 Using the blending and cross-linking methods described in Examples 1-4, but substituting the U-PP 2 unsaturated polypropylene with MOPLEN® S30G propylene homopolymer (saturated), having an intrinsic viscosity [η] = 2.3 dl/g one obtains the compositions set forth in Table 2 (wherein the quantities are percentages by weight). 5 6 7 8 U-PP 1 6.50 3.90 6.50 3.90 MOPLEN® S 30 G 6.50 9.10 6.50 9.10 Dutral® TER 537 E2 64.00 64.00 64.00 64.00 Extender oil 8.00 8.00 8.00 8.00 Zinc Oxide 9.22 9.22 8.07 8.07 Peroximon® F40 5.00 5.00 6.00 6.00 VP3 0.78 0.78 0.93 0.93 Pressure (MPa) 14.5 12.5 15.0 13.5 Compress.set % 11 14 10 13 Examples 9-12 (comparison) Using the blending and cross-linking methods described in Examples 1-4, but substituting completely the U-PP 1 and U-PP 2 unsaturated polypropylenes with saturated MOPLEN® S30G propylene homopolymer, having an intrinsic viscosity [η] = 2.3 dl/g, one obtained the compositions set forth in Table 3 (wherein the quantities are percentages by weight). The drastic deterioration of the elastic properties expressed in terms of compression set can be seen in this table. 9 10 11 12 MOPLEN® S30G 13.00 13.00 13.00 13.00 Dutral® TER 537 E2 64.00 64.00 64.00 64.00 Extender oil 8.00 8.00 8.00 8.00 Zinc Oxide 9.00 10.40 9.22 8.07 Peroximon® F40 6.00 4.00 5.00 6.00 VP3 --- 0.60 0.78 0.93 Pressure (MPa) 3.5 8.0 8.5 8.5 Compress.set % 31 28 26 25 Example 13-14 (comparison) Operating as in examples 1-4, other types of cross-linking agents were used. In particular, a sulfur/accelerators based formulation was used together with one based on phenolic resin. In Example 13 the vulcanization was carried out at 170°C for 15 minutes; in Example 14 the cross-linking was carried out at 215°C for 6 minutes. From the results reported in Table 4 wherein the quantities are percentages by weight, it can be seen that both cross-linking formulations tested were less effective than the one based on peroxide/VP3, and that the compression set values are considerably worse. 13 14 U-PP 1 6.50 6.50 U-PP 2 6.50 6.50 Dutral® TER 537 E2 64.00 64.00 Extender oil 8.00 8.00 Zinc Oxide 10.00 11.00 Stearic acid 1.00 --- Tetramethylthiuram monosulfide 1.50 --- 2-mercaptobenzothiazole 0.75 --- Sulfur 1.50 --- Titanium dioxide 0.25 --- Schenectady® SP 1045 phenolic resin --- 3.60 p-toluenesulfonic acid --- 0.40 Pressure (MPa) 11.5 11.5 Compression set (%) 29 26

Claims: A thermoplastic elastomeric composition comprising: A) from 10 to 80% by weight of one or more crystalline, isotactic polymers of propylene containing from 0.05 to 15% in moles of ethylene unsaturations deriving from the copolymerization with a conjugated C 4 -C 10 diene, or a mixture of the above polymer with a saturated thermoplastic olefin polymer in quantities lower than or equal to 80% by weight of component (A); B) from 20 to 90% by weight of an unsaturated elastomeric olefin polymer; said composition having been dynamically cross-linked with a cross-linking agent comprising a free radical generator. The thermoplastic elastomeric composition of claim 1, wherein the free radical generator is an organic peroxide. The thermoplastic elastomeric composition of claim 1, wherein the unsaturations present in component (A) are obtained by copolymerization with a diene selected from 1,3-butadiene, isoprene and 1,3-pentadiene. The thermoplastic elastomeric composition of claim 1, wherein, component (B) is an ethylene/propylene/2-ethylidene-5-norbornene terpolymer containing from 25 to 70% by weight of propylene and from 4 to 10% by weight of 2-ethylidene-5-norbornene. The thermoplastic elastomeric composition of claim 1, wherein the saturated thermoplastic olefin polymer is present in quantities lower than or equal to 50% by weight of component (A). A process for the preparation of the thermoplastic elastomeric composition of claim 1, comprising a dynamic cross-linking step consisting of subjecting components (A) and (B) to mixing at a temperature higher than or equal to their softening or melting point, in the presence of a cross-linking agent comprising a free radical generator, continuing said mixing during the cross-linking step.

Inventors: CECCHIN GIULIANO, GARAGNANI ENEA, CECCHIN, GIULIANO, GARAGNANI, ENEA
Applicants: MONTELL NORTH AMERICA INC, MONTELL NORTH AMERICA INC.
Application year: 1993
Main classification: C08L23
IPC codes: C08L23, C08J3, C08K5