Borazine derivatized hydridopolysilazane polymers

Abstract: There is described herein a method of preparing borazine modified hydridopolysilazane polymers. The method comprises reacting a hydridopolysilazane polymer with a material comprising at least one borazine ring for a time sufficient to produce the desired polymer. This invention also relates to the novel polymers produced by this method.

Description: The present invention relates to a method of preparing borazine modified hydridopolysilazane polymers. The method comprises reacting a hydridopolysilazane polymer with a material comprising at least one borazine ring for a time sufficient to produce the desired polymer. This invention also relates to the polymers produced by this method. A variety of polysilazane oligomer, cyclics, resins and linear polymers are known in the art. Generally, such polymers are characterized by having backbones with alternating silicon and nitrogen atoms. U.S. Patent No. 4,540,803, describes silazane polymers (hydridopolysilazanes) having a three-dimensional structure formed by the presence of HSi(NH-) 3 and R 3 SiNH- groups. This unique structure afforded such polymers with physical properties which are desirable in the formation of various ceramic materials. U.S. Patent No. 5,030,744 discloses the formation of boron-compound-modified polysilazanes by reacting a polysilazane having repeating units comprising: with a boron compound (including a borazine). The polysilazanes described in this document, however, differ from those claimed in the present invention in that they are primarily linear or cyclic. In contrast, polysilazanes of our present invention are highly branched, three-dimensional polymers. Likewise, European Patent No. 0 364 323, U.S. Patent No. 4,910,173 and Seyferth et al., J. Am. Ceram. Soc. 73, 2131-2133 (1990), all reveal various other methods of forming boron-compound-modified polysilazane polymers. U.S. Patent No. 5,169,908 also claims a method of preparing boron-compound-modified hydridopolysilazane polymer by reacting borane with a hydridopolysilazane polymer. The present invention provides a method of forming borazine modified hydridopolysilazane polymers. The method comprises reacting a material comprising at least one borazine ring having a hydrogen atom attached to at least one nitrogen or boron atom thereof, with a three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH- and HSi(NH-) 3 units at a temperature below 300°C, for a time sufficient to form the borazine modified hydridopolysilazane polymer, wherein R 3 are independently selected from hydrogen atoms, phenyl radicals, vinyl radicals and alkyl radicals containing 1 to 3 carbon atoms and wherein said hydridopolysilazane polymer is prepared by contacting a trichlorosilane with a disilazane wherein the amount of disilazane used is at least equimolar to the trichlorosilane based on the number Si-N bonds of the disilazane and the chlorine content of the trichlorosilane such that a highly branched, three-dimensional cage structure forms. The present invention also relates to the novel polymers produced by this process. The present invention is based on our finding that borazines can be used to modify the hydridopolysilazane polymers claimed herein to form borazine modified derivatives. Four separate mechanisms by which the borazine modification occur are proposed and are described as follows: This modification reaction was unexpected since it was not known whether the highly branched polymers of the starting materials of this invention could be caused to react in the above manner (due to issues such as steric hindrance) without further polymerizing the hydridopolysilazane. Moreover, it was unexpected that this reaction would result in a decrease in molecular weight of the polymer. This result indicates that the hydridopolysilazane polymer is cleaved during the reaction as described in reaction mechanisms [III] and [IV]. The hydridopolysilazane polymers useful herein are those described in U.S. Patent No. 4,540,803. These polymers comprise a series of repeating units of the formula -Si-NH-Si- as described above in reaction mechanisms [I], [II], [III] and [IV]. The structure of these polymers comprises highly three-dimensional cages formed by cross-linking. These polymers are prepared by a method which comprises contacting and reacting in an inert essentially anhydrous atmosphere, trichlorosilane with a disilazane at a temperature in the range of 25 to 300°C. while distilling volatile byproducts. The trichlorosilane is treated with sufficient disilazane to react with all of the chlorine in the trichlorosilane. The amount of disilazane used is at least equimolar to the trichlorosilane, based on the number of Si-N bonds of the disilazane and the chlorine content of the trichlorosilane, i.e., at least 1.5 moles of disilazane per mole of trichlorosilane. The preferred ratio is between 2.5 to 3 moles of disilazane per mole of trichlorosilane. The disilazane of U.S. Patent No. 4,540,803 has the formula (R 3 3 Si) 2 NH, where R 3 is independently selected from hydrogen atoms, phenyl radicals, vinyl radicals and alkyl radicals containing 1 to 3 carbon atoms. Thus, each R 3 can be, for example, hydrogen, methyl, ethyl, propyl, vinyl or phenyl. Examples of suitable disilazanes include [(CH 3 ) 3 Si] 2 NH, [C 6 H 5 (CH 3 ) 2 Si] 2 NH, [(C 6 H 5 ) 2 CH 3 Si] 2 NH, [CH 2 =CH(CH 3 ) 2 Si] 2 NH, [CH 2 =CH(CH 3 )C 6 H 5 Si] 2 NH and [CH 2 =CH(C 6 H 5 )C 2 H 5 Si] 2 NH. An especially preferred embodiment of U.S. Patent No. 4,540,803, involves the reaction of trichlorosilane with hexamethyldisilazane. The polymer produced thereby, trimethylsilyl hydridopolysilazane, has been shown to have valuable preceramic properties. The above reactants are brought together in an inert essentially anhydrous atmosphere. By inert, it is meant that the reaction is carried out under a blanket of inert gas such as argon, nitrogen or helium. What is meant by essentially anhydrous is that the reaction is preferably carried out in an absolutely anhydrous atmosphere but minute amounts of moisture can be tolerated. When the reactants are contacted with each other an intermediate amino compound is formed. It is preferred that the reactants are brought together in such a manner to keep the initial reaction exotherm to a minimum. Upon continued heating, additional amino compound is formed and, with further heating, R 3 SiCl is distilled from the reaction mixture and the silazane polymer formed. For best results, the rate of heating should be controlled at a rate of less than 1°C./min. A heating rate of 0.5°C./min or less is preferred. As the temperature of reaction is raised, more condensation takes place and branching occurs with residual R 3 3 Si- that is not distilled from the mixture acting as a chain stopper. This control allows one to stop the reaction at any point to obtain almost any desired viscosity. The desired temperature range for the reaction is 25 to 300°C. with a temperature in the range of 125 to 275°C. being preferred. The length of time that the reaction requires depends on the temperature employed and the polymer viscosity one wishes to achieve. After the above polymer is formed, it is reacted with a material comprising at least one borazine ring to produce the desired borazine modified hydridopolysilazane polymer. The material useful herein comprises at least one borazine ring having a hydrogen atom attached to at least one nitrogen or boron atom thereof. Any material known in the art comprising at least one such borazine ring can be used in the present invention. As shown in proposed reaction mechanisms [I], [II], [III] and [IV], a preferred embodiment of the invention comprises reacting the hydridopolysilazane with a material comprising at least one borazine ring of the general formula (BR 1 -NR 2 ) 3 wherein at least one R 1 or R 2 is a hydrogen atom. The remaining R 1 and R 2 in said borazine ring are independently selected from hydrogen atoms, hydrocarbon radicals containing 1 to 20 carbon atoms, borazine substituted hydrocarbon radicals and radicals containing boron and nitrogen. The hydrocarbon radicals can be linear or cyclic groups. Thus, R 1 and R 2 can be, for example, alkyl radicals such as methyl, ethyl, propyl, isopropyl, hexyl or octadecyl; alkenyl radicals such as vinyl, allyl or hexenyl; cycloaliphatic radicals such as cyclopentyl, cyclohexyl or cyclohexenyl; aromatic hydrocarbon radicals such as phenyl or tolyl. R 1 and R 2 can also be any polyvalent hydrocarbon radical such as methylene, dimethylene, trimethylene or octadecamethylene. Thus, materials comprising borazine ring useful herein can be monomers such as, for example, (BH-NH) 3 , mono-B-methyl borazine, di-B-methyl borazine, mono-N-ethyl borazine, di-N-methyl borazine, tri-N-propyl borazine, mono-N-di-B-methyl borazine, mono-B-vinyl borazine or mono-N-phenyl-di-N-methyl borazine and borazanaphthalene. Materials comprising borazine ring useful herein can also be polymers such as, for example, polyborazylene, polyvinyl borazine and organic copolymers of polyvinyl borazine. As shown in proposed reaction mechanisms [I], [II], [III] and [IV], the proposed reactive sites in the reaction are the B-H and N-H bonds. The reactivity of the material comprising borazine ring increases with the increased number of B-H and N-H bonds. Therefore, the most preferred material comprising borazine ring is (BH-NH) 3 . The minimum amount of the material comprising borazine ring used in the present invention is generally the desired amount of borazine incorporated in the hydridopolysilazane. An excess borazine may be used to prevent a crosslinking reaction of the polymers. The amount of excess borazine used is only limited by the cost effectiveness of the process. Preferred is an amount of the material comprising borazine ring which dissolves the hydridopolysilazane reactant to form a homogenous solution. The reaction of the hydridopolysilazane and material comprising borazine ring is generally conducted by merely mixing the reactants in a suitable reaction vessel. This reaction can also be conducted in the presence of a solvent. The solvents which may be used herein include any which acts as a solvent for the material comprising borazine ring, the hydridopolysilazane polymer and the borazine modified hydridopolysilazane polymer without adversely affecting any of the species. The solvents may be, for example, solvents not containing active N-H bonds such as ethers, alkanes or aromatic hydrocarbons. Most preferred is a reaction conducted without solvents. The above reactants are generally brought together in a essentially anhydrous atmosphere. What is meant by essentially anhydrous is that the reaction is preferably carried out in a absolutely anhydrous atmosphere but minute amounts of moisture can be tolerated. The reaction of the hydridopolysilazane polymer can be conducted in the presence of a catalyst. The catalyst which can be employed in the present reaction is any catalyst used in the art to facilitate the dehydrogenation reaction between the borazine ring and the hydridopolysilazane polymer. The dehydrogenation catalyst can be, for example, platinum dibromide. The dehydrogenation catalyst can also be, for example, osmium (II), rhodium (II) or ruthenium (II) metals, each containing ligands comprising phosphines and/or carbonyls. The reaction of the hydridopolysilazane polymer is generally conducted in a reaction environment wherefrom the hydrogen byproduct is periodically removed. For example, the reaction can be conducted in a static vacuum reaction environment with a hydrogen headspace wherefrom the hydrogen byproduct is periodically removed from the reaction vessel. In addition, the reaction can be conducted under reflux in an inert atmosphere wherefrom the hydrogen gas is periodically purged from the system with an inert gas. By inert atmosphere, it is meant that the reaction is carried out under a blanket of inert gas such as argon, nitrogen or helium. Removal of hydrogen byproduct drives the derivatization reaction forward. Thus, the frequency of hydrogen byproduct removal affects the equilibrium of the derivatization reaction. Alternatively, the reaction can be conducted in a pressure vessel as shown in Examples 1 and 2 below. Since the increase in pressure (e.g. up to 5 bar (atm)) drives the reaction forward, removal of the hydrogen byproduct may not be necessary. The reactants can be reacted at any temperature below the boiling point of the material comprising borazine ring, unless elevated pressures are employed. Under atmospheric pressure, the reactants can be reacted at room temperature, but preferred is a slightly elevated temperature to induce the reaction. More preferred is reaction temperature below 300°C. Even more preferred is a reaction temperature below 100°C. The most preferred reaction temperature is between 60 and 80°C. The length of time that the reaction requires depends on the temperature employed and the degree of derivatization polymer one wishes to achieve. Under increased pressure, the reaction can run to completion in less time. The amount of borazine incorporated into the hydridopolysilazane polymer can also be readily controlled by the reaction time, temperature and pressure. After the reaction is completed, the unreacted material comprising borazine ring can be removed from the reaction vessel by any means of liquid removal well known in the art. The removal can be preformed by, for example, vacuum evaporation or distillation. The unreacted material comprising borazine ring can then recycled. The borazine modified hydridopolysilazane polymer produced by the above reaction is then merely recovered from solution. Methods such as recrystallization or simple evaporation of the solvent under heat and/or vacuum are known in the art and useful herein. Modification of the polymers has been confirmed by 11 B NMR data which show a fairly clean derivatization and by IR data which show the presence of B-H, B-N and N-H stretches that were not present in the hydridopolysilazane starting material. The process of this invention may produce polymers having number average molecular weights higher than, equivalent to or less than those of the starting polymers. The expected products of the above process represented by reaction mechanisms [I] and [II] above have about the same number average molecular weights as their hydridopolysilazane starting materials. The expected products of the above process represented by proposed reaction mechanisms [III] and [IV] have about the same or lower molecular weights than the starting materials. Resultant polymers formed by reaction mechanism [III], however, theoretically dominate over those produced by reaction mechanism [IV], since the latter is observed to require more vigorous conditions. Experimental results are consistent with the reaction involving all of these competing mechanisms. Even though the modification reaction results in a decrease or no change in number average molecular weights, the derivatized polymers have higher ceramic yield than that of the unmodified polymer and the ceramic yield of the derivatized polymers increases with increased incorporation of boron. Furthermore, the nitrogen levels in the ceramic chars (of the derivatized polymer) are higher because of B-N bond formation. Finally, X-ray diffraction analysis (XRD) show that borazine retards crystallization of hydridopolysilazanes up to pyrolysis temperatures of 1700°C., while crystallization of the SiC and Si 3 N 4 ceramic phases occurs in the unmodified polymer at pyrolysis temperatures of 1500°C. The derivatized polymers of this invention are especially valuable since they are meltable and easily curable at elevated temperatures. Such curability is critical in applications such as ceramic fibers, as coatings on ceramic and carbon-carbon composites, as ceramic monoliths and as ceramic matrix composites. The following examples are provided so that one skilled in the art may more readily understand the invention. In the following examples, hydridopolysilazane samples of the general formula (HSi) 0.33 (Me 3 Si) 0.17 (NH) 0.33 N 0.17 were obtained from Dow Corning Corp. (Midland, MI). Borazine of the formula (BH-NH) 3 , was purchased from Callery Chemical Co. and was purified by refraction through -45°, -78° and -196° trap series, with only the material collected at -78° used. Elemental analyses of carbon, hydrogen and nitrogen for both the polymers and the ceramics were performed on a Control Equipment Corporation 240-XA Elemental Analyzer. Oxygen analyses were done on a Leco Oxygen Analyzer equipped with an Oxygen Determinator 316 (Model 783700) and an Electrode Furnace EF100. Silicon and boron compositions were determined by a fusion technique which consisted of converting the material to soluble forms of silicon and boron followed by analyzing the solute for total silicon or boron by atomic absorption spectrometry. XRD characterization was performed on a Norelco Philips vertical goniometer (Type 42271/0) fitted with a closed sample chamber, sample spinner, graphite monochromator, scintillation counter and a long fine focus copper target tube. Gel permeation chromatography (GPC) data (i.e. molecular weight distribution averages) were obtained on a GPC (Waters Inc.) equipped with a model 600E systems controller, model 490 ultraviolet absorbance (UV) and model 410 differential refractometer detectors interfaced to a Digital Professional 380 computer employing EXPERT software (Waters Inc.). All values were relative to polystyrene standards. Diffuse-reflectance IR spectra were obtained on a Perkin-Elmer 7770 Fourier transform spectrophotometer equipped with the appropriate diffuse-reflectance attachment. 11 B NMR spectra at 64.2 MHz were obtained on a Bruker AF-200 spectrometer equipped with the appropriate decoupling accessories. All 11 B shifts were referenced to BF 3 -O(C 2 H 5 ) 2 (0.0 ppm) with a negative sign indicating an upfield shift. All synthetic manipulations were carried out by using standard high vacuum or inert-atmosphere techniques. Examples 1 and 2 . A sample of hydridopolysilazane was charged into a 88 mL Fisher pressure reaction vessel and the vessel was evacuated. The purified borazine was vacuum distilled into the reactor vessel, which was sealed and brought to room temperature. The amounts of hydridopolysilazane (HPZ (g)) and borazine (borazine (g)) used for each example are detailed in Table 1. The hydridopolysilazane gradually dissolved to form a clear solution. The mixture was then heated in an oil bath and maintained at 73°C. As shown in Table 1 (time (h)), the reactant mixture which produced borazine modified polymer (1) was heated in excess borazine for 7.0 hours, while the mixture which produced borazine modified polymer (2) was heated for 17.5 hours. The borazine modified polymers were isolated as white solids after vacuum evaporation of excess borazine from the reaction vessel. The product yield for each example is listed in Table 1 (Yield(g)). Elemental analyses were performed on the precursor polymer (HPZ) and the borazine modified polymers (1) and (2). As shown in Table 1, more borazine is incorporated into the hydridopolysilazane polymer when the reaction time is increased at a constant temperature. GPC data (i.e.: molecular weight distribution averages) of the starting polymer (HPZ) and modified polymer (1) and polymer (2) were also obtained. IR spectra for polymers (1) and (2) show absorptions characteristic of the brazinyl BH (2510 cm -1 ) and NH (3450 cm -1 ), polymer NH (3380 cm -1 ), SiH at (2160 cm -1 ) and saturated CH (2900-3000 cm -1 ) with the relative intensities of these absorptions changing according to the polymer composition. With increasing borazine content, the backbone NH, SiH and CH absorptions decrease, while the borazine BH and NH absorptions increase. The 11 B decoupled proton NMR spectra of both reactant and product samples show broad resonances centered at 5.10 ppm (NH), 4.60 ppm (BH) and a very strong resonance at 0.2 ppm (saturated C-H attached to Si) with the relative intensities characteristic of their borazine and silazane compositions. 11 B NMR spectrum for polymer (1) is composed of a singlet at 25.8 ppm and a doublet at 31.0 ppm (J BH =112Hz) in a 1:2 integrated ratio, indicating the borazine unit is connected to the hydridopolysilazane through one of the three boron atoms in the borazine ring. The chemical shifts are characteristic of those observed for substituted borazines suggesting no ring-opening reaction has occurred. The 11 B NMR spectra for modified polymer (2) contained similar features as polymer (1). However, the resonances in the higher borazine content polymer (2) were broadened. Other characterizations of the polymers are summarized in Table 2. Summary of Reaction Conditions and Modified Polymer Yield and Compositions Polymer HPZ(g) Borazine(g) T(°C) time(h) Yield(g) Polymer Composition HPZ --- --- --- --- --- Si 1.0 N 1.04 C 1.16 H 4.69 (1) 1.52 3.24 73 7.0 1.56 Si 1.0 B 0.32 N 1.22 C 1.02 H 4.67 (2) 1.51 3.15 73 17.5 2.28 Si 1.0 B 1.68 N 2.61 C 1.04 H 6.25 Characterization of the Hydridopolysilazane Precursor and Borazine Modified Products elemental analyses (wt %) GPC polymer %C %H %N %Si %B Mn Mw HPZ 21.84 7.42 23.06 44.3 --- 2214 11,438 (1) 18.69 7.12 25.97 42.7 5.3 1483 6,729 (2) 11.96 6.00 35.15 26.9 17.42 783 4,322 Example 3 26 g of hydridopolysilazane were charged into a 500 mL round bottom flask fitted with a vacuum stopcock and the flask was evacuated. 21.68 g of purified borazine were vacuum distilled into the reactor vessel, which was sealed and brought to room temperature. The polysilazane gradually dissolved to form a clear solution. The mixture was then heated in an oil bath and maintained at 73°C. The mixture which produced borazine modified polymer was heated in excess borazine for 2.2 hours. The vessel was degassed every hour. 26.8 g of borazine modified polymers were isolated as white solids after vacuum evaporation of excess borazine from the reaction vessel. Elemental analyses were performed on the precursor polymer (HPZ) and the borazine modified polymer (3). GPC data (i.e.: molecular weight distribution averages) of polymer (3) were obtained. IR spectra for modified polymer (3) showed similar absorpotion characteristics as modified polymers (1) and (2). The 11 B NMR spectra for modified polymer (3) contained similar features as modified polymers (1) and (2); however, the resonances in the higher borazine content polymers (1) and (2) were broader than those of polymer (3). Characterization of the Polysilazane Precursor and the Boron Modified Polymer Product after 2.2 hours of reaction at 73°C. elemental analyses (wt%) GPC polymer %C %H %N %Si %B formulation Mn Mw HPZ 21.8 7.4 23.1 44.3 --- Si 1.0 N 1.04 C 1.16 H 4.09 2,214 11,438 (3) 2.2 7.4 24.1 42.8 2.2 Si 1.0 B 0.13 N 1.13 C 1.17 H 4.84 1,649 9,873 As shown in Table 3, in 2.2 hours, only 2.2 wt% boron was incorporated into polymer (3), drastically less than the amount of boron incorporated in polymer (1) (5.3 wt%) and polymer (2) (17.42 wt%), when the reaction was allowed to proceed for much longer times, 7 and 17.5 hours, respectively. Examples 4 through 6 . Investigation of the ceramic conversions of the modified polymers from Examples 1, 2 and 3 were performed by converting the polymers to ceramic chars. An aliquot of the resin was weighed into a graphite crucible which was then transferred into an Astro graphite furnace equipped with Eurotherm temperature controllers. A type K thermocouple was used to monitor temperatures below 900°C. and an Ircon Modeline Plus optical pyrometer for temperatures above 900°C. The furnace was then evacuated to less than 2.7 kPa (20 torr) and backfilled with argon. Under a purge of argon, the sample was heated to a temperature of 1400°C. at a rate of 10°C. per minute and held at that temperature for one hour. The sample was then cooled to room temperature. The resulting ceramic chars were ground for elemental analysis and XRD characterization, employing a mortar and pestle molded of finely powdered synthetic sapphire. Table 4 summarizes the ceramic yield, the compositions and the XRD results for the ceramics derived from the precursor polymer (HPZ) and the borazine modified polymers (1), (2) and (3). Ceramic Yield, Elemental and XRD Analyses of the Polysilazane Precursor and Borazine Modified Product after pyrolysis to 1400°C. ceramic elemental analysis(wt%) Example# polymer yield %C %N %Si %B XRD ---- HPZ 56.97% 11.1 28.2 59.9 -- beta-SiC and alpha Si 3 N 4 4 (1) 68.31% 9.69 32.66 52.3 4.4 amorphous 5 (2) 76.5% 7.39 41.2 33.6 17.1 amorphous 6 (3) 70% 10.5 29.9 53.4 2.4 amorphous As shown in Table 4 above, the ceramic chars of boron modified polymers (1), (2) and (3) are predominantly amorphous after pyrolysis to 1400°C. Moreover, higher ceramic yield results when boron is incorporated into the hydrdopolysilazane polymer. Examples 7 through 11 Investigations to determine the temperatures to which these borazine modified hydridopolysilazane materials can retain nitrogen and remain amorphous were performed. Aliquots of the precursor polymer (HPZ) and modified polymer (3) were weighed into a graphite crucible and were transferred into an Astro graphite furnace equipped with Eurotherm temperature controllers. A type K thermocouple was used to monitor temperatures below 900°C. and an Ircon Modeline Plus optical pyrometer for temperatures above 900°C. The furnace was then evacuated to less than 2.7 kPa (20 torr) and backfilled with argon. Under a purge of argon, the sample was heated to temperatures of 1400°C. (Ex. 7), 1500°C. (Ex.8), 1600°C. (Ex. 9), 1700°C. (Ex. 10) and 1800°C. (Ex. 11), at a rate of 10°C. per minute. In each example, the sample was held at the respective pyrolysis temperature for one hour. The sample was then cooled to room temperature. The resulting ceramic chars were ground for elemental analysis and XRD characterization, employing a mortar and pestle molded of finely powdered synthetic sapphire. Table 5 below summarizes the percent ceramic yields (%ceramic yield), composition of nitrogen (wt%N) in weight percent and XRD results for the ceramics derived from the precursor polymer (HPZ polymer) and the borazine modified polymer (3). Ceramic Yield, Nitrogen Composition and XRD of Polysilazane Precursor and Borazine Modified Product HPZ polymer modified polymer (3) pyrolysis ceramic ceramic Ex.# temperature yield wt%N XRD yield wt%N XRD 7 1400°C. 62.3% 29.3 major 68.8% 29.9 major amorphous amorphous minor trace alpha-Si 3 N 4 alpha-Si 3 N 4 beta-SiC beta-SiC 8 1500°C. 61.3% 28.9 major 69.9% 28.8 major alpha-Si 3 N 4 amorphous minor minor amorphous alpha-Si 3 N 4 9 1600°C. 55.5% 23.8 major 62.9% 28.6 major beta-SiC amorphous alpha-Si 3 N 4 minor minor alpha-Si 3 N 4 alpha-SiC beta-SiC 10 1700°C. 44.1% 4.11 major 59.1% 25.1 major beta-SiC alpha-Si 3 N 4 beta-SiC trace amorphous 11 1800°C. 42.4% 1.00 100% 51.1% 15.3 major beta-SiC beta-SiC minor beta-Si 3 N 4 , Si Table 5 shows minimal nitrogen loss for the boron containing ceramics throughout the pyrolysis region studied. In addition, while the unmodified hydridopolysilazane achieved crystallization at 1500°C., retardation of crystallization is observed up to 1700°C. in the boron containing ceramics. These results suggest that ceramic fibers made from borazine modified hydridopolysilazane polymers have more thermal stability than those made from the unmodified hydridopolysilazane polymers. Moreover, the thermal stability of the borazine modified hydridopolysilazane polymers correlates directly with their nitrogen level. Comparison Example A control experiment to determine any thermally induced molecular weight changes in the starting hydridopolysilazane polymer was carried out by heating 0.53 g of hydridopolysilazane dissolved in 6.0 g benzene at 70°C. for 30 hours. Molecular weight study of the white solid that was obtained upon solvent evaporation was performed on a GPC. Table 6 shows that there was no decrease and only a modest increase in molecular weight in the heated polymer (heated) when compared to the starting hydridopolysilazane polymer (HPZ). Molecular Weight Distribution Averages of unheated versus heated starting hydridopolysilazane polymer GPC polymer Mn Mw HPZ 2,214 11,438 heated 1,365 12,388

Claims: A method of forming a borazine modified hydridopolysilazane polymer comprising: reacting a material comprising at least one borazine ring having a hydrogen atom attached to at least one nitrogen or boron atom thereof, with a three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH- and HSi(NH-) 3 units at a temperature below 300°C. for a time sufficient to form the borazine modified hydridopolysilazane polymer, wherein R 3 are independently selected from hydrogen atoms, phenyl radicals, vinyl radicals and alkyl radicals containing 1 to 3 carbon atoms and wherein said hydridopolysilazane polymer is prepared by contacting a trichlorosilane with a disilazane wherein the amount of disilazane used is at least equimolar to the trichlorosilane based on the number Si-N bonds of the disilazane and the chlorine content of the trichlorosilane such that a highly branched, three-dimensional cage structure forms. The method of claim 1 wherein the borazine ring has the general formula (BR 1 -NR 2 ) 3 , wherein at least one R 1 or R 2 is a hydrogen atom, the remaining R 1 and R 2 radicals are independently selected from hydrogen atoms, hydrocarbon radicals containing 1 to 20 carbon atoms, borazine substituted hydrocarbon radicals and radicals containing boron and nitrogen. The method of claim 2 wherein the material comprising at least one borazine ring is selected from (BH-NH) 3 , borazanaphthalene, polyborazylene and polyvinyl borazine. The method of claim 1 wherein each R 3 is a methyl radical. The method of claim 1 wherein the reaction temperature is in the range of 60 to 80°C. The method of claim 1 wherein the reaction of the material comprising at least one borazine ring with the three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH-and HSi(NH-) 3 units is conducted in a static vacuum system with a hydrogen headspace from which the byproduct hydrogen gas is periodically removed. The method of claim 1 wherein the reaction of the material comprising at least one borazine ring with the three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH-and HSi(NH-) 3 units isconducted under reflux in an inert atmosphere wherefrom the hydrogen gas is periodically purged with an inert gas. The method of claim 1 wherein the reaction of the material comprising at least one borazine ring with the three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH-and HSi(NH-) 3 units is conducted under elevated pressure. The method of claim 1 wherein the reaction of the material comprising at least one borazine ring with the three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH-and HSi(NH-) 3 units is conducted in the presence of a catalyst. The method of claim 1 wherein the reaction of the material comprising at least one borazine ring with the three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH-and HSi(NH-) 3 units is conducted in an essentially anhydrous atmosphere. The method of claim 1 wherein the reaction of the material comprising at least one borazine ring with the three dimensional hydridopolysilazane polymer having (R 3 ) 3 SiNH-and HSi(NH-) 3 units is conducted in a solvent selected from alkanes, ethers and aromatic hydrocarbons. The borazine modified hydridopolysilazane polymers produced by the process of claim 1.

Inventors: SNEDDON LARRY GEORGE, SU KAI, ZANK GREGG ALAN, SNEDDON, LARRY GEORGE, SU, KAI, ZANK, GREGG ALAN
Applicants: DOW CORNING, UNIV PENNSYLVANIA, DOW CORNING CORPORATION, UNIVERSITY OF PENNSYLVANIA
Application year: 1993
Main classification: C08G77
IPC codes: C08G77, C04B35, C08G79, C07F7