Supported encapsulated-lens retroreflective sheeting

Abstract: Encapsulated-lens retroreflective sheeting comprising (1) a layer of binder material having a layer of retroreflective elements partially embedded in its top surface; (2) a transparent cover sheet disposed in spaced relation from the layer of retroreflective elements; (3) a network of narrow intersecting bonds comprising binder material embossed from the layer of binder material into contact with the cover sheet so as to adhere the layer of binder material and cover sheet together and form a plurality of cells within which retroreflective elements are hermetically sealed; the embossing of the layer of binder material leaving the bottom surface of the layer of binder material with an embossed configuration; and (4) a support sheet (e.g. fabric, web) lastingly and directly adhered to said bottom surface of the layer of binder material and embossed with the layer of binder material so as to follow the embossed configuration of said bottom surface.

Description: The present invention is directed to encapsulated-lens sheeting (as originally described in US-A-3,190,178) and especially forms of such sheeting that incorporate a support sheet or fabric which allow the sheeting to be incorporated into a garment to be worn by pedestrians. Encapsulated-lens retroreflective sheeting offers bright retroreflection and maintains that reflection even when wet with water. Such sheeting has been provided in flexible fabric supported forms for application to garments to make pedestrians wearing the garments more visible at night to drivers of approaching vehicles. Because the sheeting incorporates a supporting fabric it can be easily sewn or adhered or otherwise incorporated into a garment. However, existing forms of fabric-supported encapsulated-lens sheeting have a number of disadvantages. Addition of a supporting fabric, typically accomplished by use of pressure-sensitive adhesive to adhere the fabric to the bottom surface of the sheeting, has produced a rather thick product which protrudes too far from the surface of a garment to which it is added, and unduly stiffens the garment. Also the steps of coating a pressure-sensitive adhesive and lamination of a fabric into the sheeting by means of the adhesive add to the cost of manufacture. Further, especially under the pressures that develop when the sheeting is wound into a storage roll, the adhesive can ooze through the fabric so as to cause adhesion between adjacent windings in the storage roll and cause contamination of the exterior surface of the sheeting. EP-A-291205 discloses an article and a method according to the preamble of the independent claims. The present invention provides a new supported encapsulated lens retroreflective sheeting that alleviates the noted problems, and the invention also provides a new process for preparing such sheeting. Briefly, the new process comprises (1) preparing a layer of binder material having a layer of retroreflective elements disposed over and partially embedded in its top surface ("top" refers to the exterior surface of the sheeting through which light is received for reflection, or, with respect to the underlying components of the sheeting, the surface that faces in the same direction as the top exterior surface; "bottom" refers to the surface opposite from the top surface); (2) applying a support sheet to the bottom surface of the layer of binder material; (3) disposing a transparent cover sheet over the protruding surfaces of the layer of retroreflective elements; and (4) applying a network-like pattern of heat and pressure against the bottom surface of the support sheet so as to emboss the support sheet and further emboss binder material from the layer of binder material into contact with the cover sheet. The embossing step forms a unified article in which the layer of binder material and cover sheet are adhered together and a plurality of cells is formed within which retroreflective elements are hermetically sealed. The layer of binder material develops an embossed configuration and the support sheet follows that embossed configuration. The support sheet is applied to the bottom surface of the layer of binder material prior to the application of embossing heat and pressure. The support sheet comprises a fabric, and the binder material from the layer of binder material penetrates into interstices of the fabric during the lamination step. By the described process a new sheeting is prepared which in brief summary comprises (1) a layer of binder material having a layer of retroreflective elements disposed over and partially embedded in its top surface; (2) a transparent cover sheet disposed in spaced relation from the layer of retroreflective elements; (3) a network of narrow intersecting bonds comprising binder material embossed from the layer of binder material into contact with the cover sheet so as to adhere the layer of binder material and cover sheet together and form a plurality of cells within which retroreflective elements are hermetically sealed; and (4) a support sheet lastingly and directly adhered to the bottom surface of the layer of binder material and embossed with the layer of binder material so as to follow the embossed configuration of the bottom surface of the layer of binder material. The support sheet comprises a fabric, and binder material from the layer of binder material penetrates into interstices of the fabric to enhance the adhesion of the fabric to the layer of binder material. Figure 1 is a top view of a portion of sheeting of the invention; Figure 2 is a greatly enlarged cross-section of an intermediate assembly occurring during preparation of sheeting of the invention; and Figure 3 is a greatly enlarged cross-section of sheeting of the invention together with parts of apparatus used during manufacture of the sheeting. An exemplary finished sheeting of the invention 10 is pictured in top view in Figure 1 of the drawings and in greatly enlarged cross-section in Figure 3 (along the lines 3-3 in Figure 1). As pictured, the exemplary sheeting 10 comprises a base layer of binder material 11; a layer of transparent microspheres 12 partially embedded in the top surface of the layer of binder material 11 and covered over their embedded or bottom surfaces with vapor-deposited specularly reflective material 13 (the specularly reflective material is typically a metal such as aluminum or silver or a dielectric material such as described in Bingham, U.S. Pat. 3,700,305 vapor-deposited onto the microspheres; in combination the microspheres and specularly reflective material form a retroreflective element supported in the binder material); a transparent cover or top sheet or film 14 disposed over the protruding or non-embedded surfaces of the microspheres 12 and bonded to the layer of binder material by a network of narrow bonds 15 comprising binder material embossed from the layer 11 through the microspheres 12 into adhering connection with the cover film 14; a support sheet 16 laminated to the bottom surface of the layer 11 of binder material and following the embossed configuration of the layer of binder material; and a protective film 17 which may be optionally included as explained below. In preparing sheeting of the invention the microspheres 12 are typically first removably and partially embedded in a carrier sheet such as polyethylene-coated paper (see US-A-3,190,178). The surfaces of the microspheres protruding from the carrier sheet are covered with the specularly reflective material 13 by vapor-deposition. A representative carrier sheet 18 is pictured in Figure 2 of the drawings and includes a paper sheet 18a and polyethylene layer 18b. The intermediate product of microspheres embedded in the carrier sheet and covered with specularly reflective material is labeled as 19 in Figure 2. Binder material is then applied over the specularly reflective material as by coating the binder material from solution or a melt or by pressing a preformed layer of the binder material against the microspheres (see US-A-5,064,272, column 5, line 61, through column 6, line 17; the latter refers to the preferred practice of pressing the layer of binder material against the microspheres only to an extent that the binder material does not contact the portion of the coated specularly reflective material deposited onto the carrier sheet between the microspheres; thus when the carrier sheet is later separated from the layer of binder material, the specularly reflective material between the microspheres stays with the carrier sheet and does not cover the surface of the binder material between the microspheres, thereby minimizing coloration of the product by metallic specularly reflective material). Upon drying or cooling of the binder material, the layer 11 is formed with the microspheres partially embedded in the layer 11 and also partially embedded in the carrier sheet. The result is the construction labeled 20 in Figure 2. In a preferred practice of the invention the support sheet 16 is then laminated to the free surface of the layer of binder material. Such a lamination could occur later, for example, after removal of the temporary carrier sheet 18; but the assembly is better supported when lamination is performed with the carrier sheet in place. Lamination preferably is achieved by pressing the support sheet 16 against the binder material 11 and heating the assembly as by passing the assembly under pressure between a pair of rollers, represented in Figure 2 by the parts marked 21 and 22, at least one of which is heated. The support sheet 16 is a fabric, and during the lamination operation portions of the binder material 11 penetrate into interstices of the fabric thereby firmly bonding the fabric to the binder material. To prevent the penetrated binder material from fouling the laminating rollers, a film 17 may be removably applied over the bottom surface of the support fabric. One useful film is a two-layer film which has a heat-softenable layer 17a such as polyethylene and a nonsoftening layer 17b such as polyethylene terephthalate, and which can be heat-laminated to the support fabric. The film 17 becomes bonded to the support fabric, and can either remain as part of the final product or be stripped away prior to inclusion of the fabric in a garment or other use of the product. Next, in the illustrated preferred process the carrier sheet 18 is stripped away, uncovering microspheres protruding from the layer 11 of binder material. A cover film 14 is laid against the protruding surfaces of the microspheres and the resulting assembly is subjected to an embossing operation as represented in Figure 3. The whole assembly, comprising cover film 14, layer of binder material 11, support sheet 16 and protective sheet 17, is inserted between a pair of heated platens or rollers 24 and 25. One platen or roller (25) is an embossing platen having a pattern of raised ridges 26. The ridges 26 on the embossing platen press against the bottom of the protective sheet 17 to deform the protective sheet, support sheet 16, and binder layer 11 into the configuration shown in Figure 3. The layer 11 of binder material is heated and pressed sufficiently so that it floods the microspheres in the area pressed and contacts the cover film 14 to develop a bond 15. The pattern of ridges on the embossing platen is such as to form the network of narrow bonds 15 illustrated in Figure 1. The bonds intersect so as to define cells 27 within which microspheres are hermetically sealed. A variety of patterns can be used; for example the square cells of Figure 1 can instead have a hexagonal pattern. Useful cover films for inclusion in encapsulated-lens sheeting are well known. For sheeting of the invention polyolefin films, which have good flexibility even in low-temperature environments are especially desirable; examples are polyethylene, polypropylene and ethylene-acrylic acid copolymers. Ultraviolet absorbers are desirably included, especially in the polyolefin films to avoid deterioration of the film and underlying elements during outdoor weathering. Because the described polyolefin films are softer and may not exhibit a desired resistance to penetration by microspheres during the embossing operation represented in Figure 3 of the drawings, the cover sheet desirably has a layer or coating (not pictured) of a harder, higher softening material as described in U.S. Pat. 5,066,098 (incorporated herein by reference). Polyurethanes are especially useful as the harder material, e.g., layers formed from aqueous colloidal urethane dispersion; or acrylic emulsions can also be used. Suitable commercial materials are sold under the tradenames of Neo Rez (polyurethanes) or Neo Cryl (acrylics) by Polyvinyl Chemical Industries. Besides providing the noted resistance to penetration, such layers can enhance adhesion between the cover film and the binder material embossed into contact with the cover film. Also, the layers can be colored, as by inclusion of a dye. Highly plasticized polyvinyl chloride films may also be used as the cover film. In general, binder materials to be used in sheeting of the invention should have low glass transition temperatures (T g ), e.g., -20°C or lower, to maintain good low temperature performance. A thermoplastic polyurethane polymer is especially useful as the binder material 11 and provides good durability and flexibility, including flexibility at low temperatures. Although aromatic polyurethanes discolor in sunlight, addition of a hiding type pigment such as titanium dioxide avoids any discoloration of the product. A white coloration is typically desired to minimize the gray or metallic color caused by a metal coating on the microspheres. Ethylene-acrylic acid copolymers are another useful polymer in the binder material, though it is difficult to add a pigment to such a material. If an ethylene-acrylic acid polymeric cover film is used with an ethylene-acrylic acid polymeric binder material, there is no need for a polyurethane hard layer on the cover film to achieve a good bond to the cover film. The binder material can comprise a mixture of polymeric materials as well as other ingredients. For example, a vinyl chloride/acetate copolymer is desirably mixed with a polyurethane polymer to provide flexibility. Heat-stabilizers and antioxidants can also be added to improve weatherability. Fluorescent dyes are also useful to provide brightly visible colors. Fabrics are especially useful as the support sheet because they are durable, with high tensile strength; the binder material can penetrate the fabric to achieve a good bond; and fabrics avoid the plasticizers often included in polymeric films for flexibility, which can weaken adhesion and cause other problems. Spun-bond polyester fabrics are especially useful; they often comprise a bicomponent fiber with a polyethylene terephthalate core and a polyethylene or polyester outer layer that softens at a lower temperature than the polyethylene terephthalate core. Woven cloths are also useful. Polymeric films offer an alternative to fabric for some purposes. Although removable liners such as the liner 17 are preferred in sheeting of the invention, they can be avoided, for example, by coating the bottom surface of the fabric (opposite surface from that bonded to the layer of binder material) with a suitable repellent material. However, materials should be chosen that maintain adhesion to the binder material. In fact, corona treatments are preferred with the described polyethylene-containing spun-bonded fabrics to enhance adhesion. A finished product of the invention is thin, light weight and flexible, which preferably extends to low temperatures such as -20°C. Preferably the complete product, without protective film 17, is 325 micrometers or less thick and is sufficiently flexible so that it can be readily wrapped around a 3 millimeter-diameter (0.125 inch) mandrel at room temperature, and preferably at -20°C. The support sheet follows the embossed configuration of the bottom surface of the layer of binder material and therefore there are no voids for collection of moisture. Besides being incorporated into a garment, sheeting of the invention can be used by itself, e.g., as a sign that can be unwound from a storage roll and mounted where needed, as on the rear of a vehicle. The invention will be further illustrated with the following example. A solution of binder material prepared from the ingredients listed below was coated over a sheet 19 comprising a carrier sheet 18 in which microspheres 12 averaging 65 micrometers in diameter were embedded to about 30% of their diameter and coated with vapor - deposited aluminum. Parts by weight Thermoplastic polyurethane resin 16.99 Vinyl chloride/acetate copolymer 6.73 Titanium dioxide 7.00 Antioxidant 0.48 Stearic acid 0.48 Methyl ethyl ketone 49.49 Cyclohexanone 17.88 The coated solution was dried at an elevated temperature of 120°C (80-120°C is a useful range) to a thickness of about 50 micrometers. Thereupon a polyester textile fabric (Toray textile fabric No. 501) was laminated to the dried exposed surface of the layer of binder material; a temperature of 100°C and 5 kg f /cm 2 pressure was used (ranges of 70-100°C and 3-5 kg f /cm 2 are useful). A two-layer protective film 17 comprising a polyethylene top layer and polyethylene terephthalate bottom layer had been previously laminated to the bottom surface of the fabric. In an alternative example, a nonwoven spun-bond fabric comprising bicomponent fibers having a polyethylene layer on a polyethylene terephthalate core (Unitika nonwoven fabric S1003WDO) was laminated to the layer of binder material instead of the polyester fabric. The lamination temperature and pressure were 100°C and 5 kg f /cm 2 , respectively. In this example, protective film 17 was not used. In both examples the carrier sheet 18 was then stripped away, and a 75 micrometer-thick cover film 14 of extruded ethylene/acrylic acid copolymer (Primacor 3440 supplied by Dow Chemical) containing an ultraviolet light absorber laid into contact with the exposed surfaces of the microspheres. This assembly was then subjected to embossing pressure using a smooth-surfaced rubber-covered top pressure roll heated to 160°C and a bottom metal roll heated to 80°C and carrying a network of embossing ridges that intersect in a hexagonal pattern. The rolls were pressed together to develop a pressure of 3-5 kg f /cm 2 and the assembly was pulled between the rolls at a rate of 3 meters per minute. The protective film 17 was removed after the embossing operation. The resulting supported retroreflective sheeting was then subjected to a series of tests as shown in the following Table 1. Test Item Test Method Result Backing edge Knife Cutting OK Adhesive bleeding 40 kg/100 cm 2 /65°C/336 hrs. OK Reflectivity 0.2°/-4°, 30°, 40° 325, 346, 320 CPL Gloss 60° gloss OK Water resistance 40°C/120 hrs. OK Hot water resistance 80°C/60 mins. OK Heat resistance 120°C/60 mins. OK Heat cycle 8 cycles OK Head humidity 65°C/95%RH/192 hrs. OK Impact resistance -20°C/80Pl OK Flexibility -20°C/0.125 inch Mandrel OK Weathering Sunshine Weatherometer 750 hrs. OK QUV 750 hrs. OK In still another example, a woven polyester fabric (a 100 percent polyester 85.5 X 60 construction weighing 3.1 ounces/yard 2 using textured polyester yarns, 1/150/34 warp and fill supplied by Milliken) was used as the support sheet. In this example, lamination of the fabric to the bottom layer of binder material and embossing of the assembly to the cover film were performed simultaneously. The top pressure roll was unheated and the bottom metal roll was heated to 215°C.

Claims: Supported retroreflective sheeting comprising (a) a layer of binder material (11) having a layer of retroreflective elements (12) disposed over and partially embedded in its top surface; (b) a transparent cover sheet (14) disposed in spaced relation from and on top of the layer of retroreflective elements; (c) a network of narrow intersecting bonds (15) comprising binder material embossed from the layer of binder material into contact with the cover sheet so as to adhere the layer of binder material and cover sheet together and form a plurality of cells within which retroreflective elements are hermetically sealed; the embossing of the layer of binder material leaving the bottom surface of the layer of binder material with an embossed configuration; (d) a support sheet (16) being lastingly and directly adhered to said bottom surface of the layer of binder material and embossed with the layer of binder material so as to follow the embossed configuration of said bottom surface, characterized in that the support sheet (16) comprises a fabric, and in that binder material from the layer of binder material penetrates into interstices of the fabric. Retroreflective sheeting of claim 1 in which the cover sheet comprises a polyolefin. Retroreflective sheeting of claim 2 in which the polyolefin comprises an ethylene-acrylic acid polymer. Retroreflective sheeting of any one of claims 1 to 3 in which the binder material comprises a polyurethane. Retroreflective sheeting of any one of claims 1 to 4, in which the cover sheet comprises a polyolefin and the surface of the cover sheet contacted by the binder material is covered with a polyurethane-based layer. Retroreflective sheeting of any one of claims 1 to 5, in which a protective film (17) covers the bottom surface of the support fabric (16). Retroreflective sheeting of claim 6 in which the protective film (17) comprises a top layer of heat-softenable material and a bottom layer, and the protective film is heat-laminated to the support fabric by means of the heat-softenable layer. Retroreflective sheeting of any one of claims 1 to 7, in which the layer of binder material is between about 25 and 50 micrometers in thickness. A method for preparing a supported retroreflective sheeting comprising (a) preparing a layer of binder material (11) having a layer of retroreflective elements (12) disposed over and partially embedded in its top surface; (b) disposing a transparent cover sheet (14) over the protruding surfaces of the layer of retroreflective elements; and (c) applying a network-like pattern of heat and pressure against the bottom surface of a support sheet (16) so as to emboss the support sheet and further emboss binder material from the layer of binder material into contact with the cover sheet, whereby (d) the support sheet (16) is applied to the bottom surface of the layer of binder material prior to application of the network-like pattern of heat and pressure, whereby a unified article is formed in which the layer of binder material and cover sheet are adhered together and a plurality of cells is formed within which retroreflective elements are hermetically sealed, and the support sheet is lastingly adhered to the bottom surface of the layer of binder material and follows the embossed configuration of said layer of binder material, characterized in that the support sheet (16) comprises a fabric and in that binder material from the layer of binder material penetrates into interstices of the fabric during the lamination step. A method of claim 9 in which the support sheet is laminated to the bottom surface of the layer of binder material by heat and pressure prior to the application of embossing heat and pressure.

Inventors: LIGHTLE VERA L, NAGAOKA YOSHIYUKI, LIGHTLE, VERA L., NAGAOKA, YOSHIYUKI, Lightle, Vera L., c/o Minnesota Mining and, Nagaoka, Yoshiyuki, c/o Minnesota Mining and
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1993
Main classification: G02B5
IPC codes: B32B7, B32B5, G02B5