Silver halide photographic light sensitive material

Abstract: A silver halide photographic light-sensitive material is disclosed, which comprises a support and a silver halide photographic emulsion layer and a protective layer provided in that order on a first side of the support, and a backing layer and a protective backing layer provided in that order on a second side of the support opposite to the silver halide photographic emulsion layer, an outermost layer of the material containing a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant and an outermost layer on the second side of the support containing a compound represented by the Following formula (A) or (B): Formula (A) RCOOM Formula (B) R₁-CO-O-X-O-CO-R₂

Description: This invention relates to a silver halide photographic light sensitive material and particularly to a silver halide photographic light sensitive material improved in finger-print smudge resistance, pressure-fog production resistance in a high temperature and a high humidity and adhesion resistance. In recent years, attempts have been made to improve silver halide photographic light sensitive materials in their image-sharpness and to increase the sensitivity by thinning the layer thickness of the non-light-sensitive protective layers, and the miniaturization of readily portable cameras has become an essential problem. When reducing the volume of a film cartridge for miniaturizing a camera, it was found that the pullout load of a roll type light sensitive material becomes heavy and in particular becomes heavier under high temperature and high humidity conditions. As a result, the drivability of the film is deteriorated in a photographing or projecting apparatus and the pullout load or tension seriously increases. It was, therefore, found that high-speed silver halide photographic light sensitive materials are liable to produce a pressure fog. There have been various proposals for improving the pressure fogs. For example, a known method for increasing the binder content of a silver halide emulsion layer, in which a silver halide/binder ratio is lowered. However, this method has a defect that the sharpness is deteriorated and the effect of thinning a non-light-sensitive protective layer is offset against the merits of this method. Japanese Patent Publication Open to Public Inspection (hereinafter referred to as JP OPI Publication) No. 50-56227/1975 describes a method of adding a polymer latex to an emulsion layer, JP OPI Publication Nos. 53-13923/1978 and 53-85421/1978 describe a method of adding a high boiling organic solvent to an emulsion layer and JP OPI Publication Nos. 50-116025/1975 and 51-107129/1976 describe a method of adding an iridium or thallium salt when preparing silver halide emulsion grains. Methods of applying an improvement in a non-light-sensitive layer are known, for example, a method of adding fine particles of silica, titanium dioxide, polystyrene or the like to an outermost layer of non-light-sensitive layers, another method of adding paraffin and polyvinyl pyrrolidone into a non-light-sensitive layer as described in JP OPI Publication No. 59-72439/1984, and a further method of adding oil-drops and fine particle powder into a non-light-sensitive layer comprising two layers as described in JP OPI Publication No. 58-197734/1983. A still further another method of making use of roundish, monodispersive silver halide grains is described in JP OPI Publication No. 59-149349/1984. Even making use of any of the above-given methods, satisfactory improvement of pressure fogs could not be obtained when a high-speed light sensitive material is loaded in a miniature camera or a miniature cartridge. The outermost layer of a silver halide photographic light sensitive material is a hydrophilic protective layer containing a binder mainly comprising gelatin. It is, therefore, liable to produce a dust adhesion or a finger-print smudge. Particularly with the recent increase of the so-called "Mini-Lab"s, i.e., in shops which process light sensitive materials on the premises dust adhesion and finger-print smudge are liable to occur on light sensitive materials and, sometimes, photoprints may be so affected as to spoil their commercial value. It was, therefore, found that some action for improvements is necessary. There have been some proposals for preventing the above-mentioned adhesions. For example, U.S. Patent No. 4,426,431 proposes polymerizable epoxy and cationic polymerization initiators for epoxy use, polymerizable acryl and radical polymerization initiators of haloacrylated aromatic ketones and polymerizable organofunctional silane-containing radiation hardenable compositions, each described in U.S. Patent No. 4,426,431; terminal epoxy silane, aliphatic polyepoxy, monomers capable of being polymerized with epoxysilane and compositions comprising the reaction products of UV absorbents, each described in U.S. Patent No. 4,136,046; and compositions containing cross-linked polymers each described in U.S. Patent No. 4,262,072. Even these compositions have many defects such as that reaction control may be difficult and the reactivity may be varied in preservation so that the coating operations are difficult to carry out or certain specific characteristics may not be difficult to obtain or a compound may be available with difficulty, because it is of the cationic polymerization type. As for the other example, there are the examples disclosed in JP OPI Publication Nos. 3-240039/1991 and 1-260436/1989 in which a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant are each used at the same time. In these examples, however, finger-print smudge production cannot be improved. JP OPI Publication No. 62-264043/1987 describes a method in which a protective coating layer is formed by coating with a polymer having a group reactive with gelatin and then by hardening the coated polymer by irradiating with radioactive rays. Further, JP OPI Publication No. 3-212640/1991 describes a method in which an ionic polyester is used. As described above, various attempts were tried to form protective coated layers. However, they were not satisfactory in preventing finger-print smudge and raised the problems of lowering sharpness, producing devitrification and so forth. Therefore, the above problems have not yet been solved. To counter the above-mentioned problems, an object of the invention is to provide a silver halide photographic light sensitive material improved in finger-print smudge resistance, pressure fog produced at a high temperature and high humidity and adhesion resistance. The above-mentioned object of the invention can be achieved with a silver halide photographic light sensitive material comprising a support having at least one silver halide emulsion layer, an emulsion layer and a backing layer and a protective layer each arranged on both sides with the emulsion layer and the support between, wherein at least one outermost layer of the silver halide photographic light sensitive material contains a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant and the outermost layer on the backing layer side comprises at least one compound chosen from a first compound which is one of compounds C-1 to C-14, C-53, C-56, C-60, C-65 and C-66 below and compounds of the following Formula (A), (B) or (B'): Formula (A) RCOOM wherein R represents an aliphatic hydrocarbon group and M represents a cationic group, Formula (B) R 1 -(COO)-X-(OOC)R 2 Formula (B') R 1 -(OOC)-X-(COO)-R 2 wherein R 1 and R 2 each represent an aliphatic hydrocarbon group and X represents a divalent bonding group. The invention will be detailed below. The fluorine-containing anionic surfactant preferably applicable to the invention includes a compound represented by the following Formula (FA); Formula (FA) (Cf)Y wherein Cf represents a group having at least three fluorine atoms and at least two carbon atoms; and Y represents -COOM, -SO 3 M, -OSO 3 M or -P(=O)(OM) 2 in which M represents a hydrogen atom or a cation such as an alkali metal or a quaternary ammonium group. The anionic surfactant more preferably applicable thereto includes a compound represented by the following Formula (FA'); Formula (FA') (Rf)D-Y wherein Rf represents a fluorine-containing alkyl group having from 3 to 30 carbon atoms or a fluorinated aryl group having from 6 to 30 carbon atoms; D represents a divalent bonding group having from 1 to 12 carbon atoms and containing at least one linking group chosen from -O-, -COO-, -CON(R 1 ) - and -SO 2 N(R 1 )-, in which R 1 represents an alkyl group having from 1 to 5 carbon atoms; and Y represents -COOM, -SO 3 M, -OSO 3 M or -P(=0)(OM) 2 in which M represents a hydrogen atom or a cation such as an alkali metal or a quaternary ammonium group. Next, the typical examples of the compounds will be given below. However, the invention shall not be limited thereto. FA-1 CF 3 (CF 2 ) 6 COONH 4 FA-28 CF 3 (CF 2 ) 11 -CH 2 -O-SO 3 Na FA-43 C 9 F 17 OCH 2 CH 2 OSO 3 Na FA-47 HCF 2 (CF 2 ) 6 OCH 2 CH 2 CH 2 SO 3 Na It is particularly desirable to use a fluorine-containing anionic surfactant containing at least one linking group -SO 2 N(R 1 )-. The fluorine-containing cationic surfactants applicable to the invention are the compounds represented by the following Formula (FK); Formula (FK) Rh-T-X + Z - wherein Rh represents a hydrocarbon group having from 1 to 20 carbon atoms preferably from 3 to 20 carbon atoms, in which at least one hydrogen atom is substituted with a fluorine atom; T represents a chemical bond or a divalent group; X represents a cationic group; and Z represents a counter anion. Examples of Rh may be given as follows; -CnF 2n+1 , (n=1-20, preferably 3-12), HCmF 2 m-, -CmF 2 m -1 and -C 3 mF 6 m- 1 , (m=2-20, preferably 3-12). Examples of T may be given as follows; -CONR'- (CH 2 )p-, -O-A'-SO 2 NR'-(CH 2 )p-, (A': alkylene, arylene), -O-A'CONR'- (CH 2 )p-, -O-A'-O-(CH 2 ) p-, -O-A'-(CH 2 ) p-, -O-(CH 2 CH 2 O)q-(CH 2 )p-, (q=1-20), -O-(CH 2 )p-, -NR'-(CH 2 ) p-, -CONR'-(CH 2 )p-O-, and -(CH 2 ) p (CHOH) s (CH 2 ) r -, (s=0-6) Examples of X may be given as follows; -N + (R') 3 , -N + (CH 2 CH 2 OCH 3 ) 3 , and Examples of Z may be given as follows; I - , Cl - , Br - , CH 3 SO 3 - , and CH 3 COO - . Typical examples of the fluorine-containing cationic surfactants desirably applicable to the invention will be given below. In the invention, it is further desirable to use a hardly soluble sulfonamide type fluorine-containing cationic surfactant. The expression, "hardly soluble", herein means the case where a precipitate is produced or a suspended matter is observed after adding 2 g of the surfactant in 100 cc of H 2 O kept at 23°C, stirring the mixture for one hour and then allowing it to stand for 24 hours at 23°C. For example, FK-1, FK-8, FK-15, FK-16 and so forth may be corresponded to the fluorine-containing cationic surfactants. However, they shall not be limitative, but they may be selected in the foregoing tests. The fluorine-containing anionic surfactants relating to the invention or the fluorine-containing cationic surfactants relating to the invention can be synthesized according to the processes described in, for example, U.S. Patent Nos. 2,559,751, 2,567,011, 2,732,398, 2,764,602, 2,806,866, 2,809,998, 2,915,376, 2,915,528, 2,934,450, 2,937,098, 2,957,031, 3,472,894, 3,555,089 and 2,918,501; British Patent Nos. 1,143,927 and 1,130,822; JP Examined Publication No. 45-37304/1970; JP OPI Publication Nos. 47-9613/1972, 50-121243/1975, 50-117705/1975, 49-134614/1974, 50-117727/1975, 52-41182/1977 and 51-12392/1976; Journal of British Chemical Society, 1950, p.2789; ibid, 1957, pp.2574 & 1640; Journal of American Chemical Society, vol.79, p.2549, 1957; Journal of Japan Oil Chemists Society, vol.12, p.653; Journal of Organic Chemistry, vol.30, p.3524, 1965; and so forth. Among the fluorine-containing surfactants relating to the invention, some of them are available on the market under the commercial brand names including, for example, Megafac F manufactured by Dai Nippon Chemical Industrial Co., Ltd., Fluorad FC, by Minnesota Mining and Manufacturing Co., Monflor, by Imperial Chemical Industry Co., Zonyls, by E.I. DuPont, Licowet VPF, by Hoechst A.G., respectively. The fluorine-containing cationic surfactant and the fluorine-containing anionic surfactant may be used in a total amount within the range of, desirably, from 0.1 to 1000mg, more desirably from 0.5 to 300mg and, further desirably, from 1.0 to 150mg, per sq.meter of the photographic material of the invention. When making use of the fluorine-containing cationic surfactants and the fluorine-containing anionic surfactants in combination, two or more kinds of each of them may be used. Alternatively, a combination of a fluorine-containing nonionic surfactant, a fluorine-containing betaine surfactant and a hydrocarbon-containing surfactant may be used. The proportion of the fluorine-containing anionic surfactant and fluorine-containing cationic surfactant added may be, desirably from 1:10 to 10:1 and, more desirably within the range of from 3:7 to 7:3, each in mol ratios. The fluorine-containing anionic surfactant and fluorine-containing cationic surfactant of the invention are added to a surface protective layer, the surface layer on a backing layer side or the surface layer of an intermediate product. It is also allowed to overcoat a compound relating to the invention over the surface layer of the above-mentioned light sensitive material or surface layer on the backing layer side thereof. For displaying the effects of the invention most remarkably, it is desired to add the compounds of the invention to the surface layer, to the surface layer on the backing layer side or to the overcoated layer. In the higher aliphatic acids (or the salts thereof) or the aliphatic hydrocarbon group-containing esters, which are applied in the invention to the outermost layer of a backing layer and represented by the foregoing Formula (A), (B) or (B'), it is desired to contain therein an aliphatic ester in which the aliphatic hydrocarbon groups have at least 24 carbon atoms in total. Formula (A) RCOOM wherein R represents an aliphatic hydrocarbon group; and M represents, a hydrogen atom, a metal such as Na, K, Li, Mg, Ca, Sr and Ba, or HN(R 2 ) 3 , or N(R 2 ) 4 (in which R 2 represents an alkyl group or a substituted alkyl group each having from 1 to 18 carbon atoms). In the invention, however, it is preferred that the cations represented by M are other than hydrogen atoms. Formula (B) R 1 -(COO)-X-(OOC)-R 2 Formula (B') R 1 -(OOC)-X-(COO)-R 2 wherein R 1 and R 2 each represent an aliphatic hydrocarbon group. It is desirable that each of them has from 12 to 70 carbon atoms and the total carbon atoms of R 1 and R 2 is preferably within the range of from 24 to 140. It is more desirable that at least one of R 1 and R2 represents a branched aliphatic hydrocarbon group having 12 carbon atoms and the total carbon atoms of R 1 and R 2 is within the range of from 32 to 140. X represents a divalent bonding group. Examples of a first compound referred to above or of Formula (A), (B) or (B'), each desirably applicable to the invention, will be given below. However, the invention shall not be limited thereto. Exemplified compounds C C-1 (n)C 21 H 43 COOC 17 H 35 (iso), C-2 (n)C 21 H 43 COOC 15 H 31 (iso), C-3 (n)C 21 H 43 COOC 18 H 37 (iso), C-4 (n)C 21 H 43 COOC 24 H 49 (iso), C-5 (iso)C 17 H 35 COOC 32 H 65 ∼ C 36 H 73 (iso), C-6 (n)C 27 H 55 COOC 18 H 37 (iso), C-7 (n)C 17 H 35 COOC 32 H 65 ∼ C 36 H 73 (iso), C-8 (n)C 21 H 43 COOC 16 H 33 (iso), C-9 (n)C 21 H 43 COOC 20 H 41 (iso), C-10 (n)C 23 H 47 COOC 24 H 49 (iso), C-11 (iso)C 17 H 35 COOC 50 H 101 (n), C-12 (iso)C 23 H 47 COOC 24 H 49 (iso), C-13 (iso)C 31 H 63 ∼ C 36 H 71 COOC 18 H 37 (iso), C-14 (n)C 27 H 55 COOC 24 H 49 (iso), C-32 (iso)C 17 H 35 COO(CH 2 ) 14 OOCC 17 H 35 (iso) C-33 (iso)C 17 H 35 COO(CH 2 ) 20 OOCC 17 H 35 (iso) C-37 (iso)C 17 H 35 COOCH 2 CH 2 SCH 2 OOCC 27 H 53 (n) C-40 (iso)C 23 H 47 COO(CH 2 ) 2 OOCC 23 H 47 (iso) C-41 (iso)C 15 H 31 COO(CH 2 ) 6 OOCC 21 H 43 (n) C-42 (iso)C 31 H 53 ∼ C 35 H 71 COO(CH 2 ) 4 OOCC 31 H 63 ∼ C 35 H 71 (iso) C-53 (n)C 25 H 51 COOC 18 H 37 (iso) C-56 (n)C 27 H 35 COOC 18 H 37 (iso) C-60 (n)C 21 H 43 COOC 24 H 49 (iso) C-65 (n)C 15 H 31 COOC 16 H 33 (n) C-66 (n)C 17 H 35 COOC 18 H 37 (n) C-73 (n)C 17 H 35 COONa C-74 (n)C 21 H 43 COOH C-75 (n)C 21 H 43 COONa C-76 (n)C 21 H 43 COOHN(C 2 H 5 ) 3 C-77 (n)C 21 H 43 COON(C 2 H 5 ) 4 C-78 (n)C 27 H 55 COOK C-79 (iso)C 23 H 47 COOH C-80 (n)C 15 H 31 COOHN(C 8 H 17 ) 3 C-81 (n)C 17 H 35 COOH C-82 (iso)C 17 H 35 COO½Ca C-83 C 21 H 43 COOK C-84 C 21 H 43 COOHN(C 2 H 4 OH) 3 C-85 C 17 H 35 COO½Ba C-88 (n)C 17 H 35 COO(CH 2 ) 2 OOCC 17 H 35 (n) C-89 (n)C 21 H 43 COO(CH 2 CH 2 O) 2 OCC 21 H 43 (n) C-90 (n)C 15 H 31 COO(CH 2 ) 4 OOCC 15 H 31 (n) The above-mentioned compounds can be used upon dissolving them in a solvent including, for example, alcohols such as methanol and ethanol; ketones such as acetone and methylethyl ketone; ethers such as diethylether and dioxane; and aromatic hydrocarbons such as benzene and toluene. The above-mentioned compounds may be used independently or in combination with a binder. The binders capable of being used in combination include, for example, the polymers or copolymers of polystyrene, polymethyl methacrylate, vinylidene polychloride, polyacrylonitrile and vinyl acetate; cellulose derivatives such as cellulose diacetate, cellulose nitrate; and acetals such as polyvinyl formal, polyvinyl acetal and polyvinyl benzal. The compounds shall not be limited thereto, provided, they have a coat-forming capability and are soluble to any solvents. The compounds represented by Formula (A), (B) or (B') may be used in an amount within the range of, desirably from 1 to 500 mg and, more desirably from 5 to 100 mg, each per sq.meter of a light sensitive material used. The hydrophilic colloids applicable to the invention include, besides gelatin, for example, a gelatin derivative, a colloidal albumin, agar, gum arabic, alginic acid, a cellulose derivative such as cellulose acetate hydrolyzed to have about from 19 to 26% acetyl content, acrylamide, imidized polyacrylamide, casein, a vinyl alcohol polymer containing a urethane carboxylic acid group or a cyanoacetyl group such as vinyl alcohol and a vinyl cyanoacetate copolymer, polyvinyl alcohol, polyvinyl pyrrolidone, hydrolyzed polyvinyl acetate and a polymer prepared by polymerizing protein or saturated acylated protein and a monomer having a vinyl group. In the invention and with the purpose of improving the physical properties of a coated layer comprising the above-mentioned hydrophilic colloids, it is desired if required to use various kinds of layer physical property improving agents such as a layer hardener. When adding a layer hardener, for example, not only can synergistic effects on scratch prevention be seen, but also the mechanical strength of layers and the solubility resistance to solutions can be improved, so that a light sensitive material having remarkably excellent layer physical properties can be obtained. When using gelatin as a hydrophilic colloid, concrete examples of typical layer hardeners may include those of the aldehyde type, epoxy type, ethyleneimine type, carbodiimide type, mucochloric acid type and acryloyl type. These gelatin hardeners applicable to the invention are described in, for example, U.S. Patent Nos. 3,539,644, 3,642,486, 2,726,162, 2,816,125 and 3,047,394; West German Patent No. 1,085,663; British Patent No. 1,033,518; JP Examined Publication No. 48-3549/1973; PB Report No. 19921; U.S. Patent Nos. 2,950,197, 2,964,404, 2,983,611, 3,271,175, 2,938,892, 3,640,720, 3,058,827 and 2,994,611; British Patent Nos. 822,061, 1,042,083, 1,2052,052 and 1,230,354; West German Patent No. 872,153; JP Examined Publication Nos. 44-29622/1969, 47-25373/1972, 47-8736/1972 and 46-38715/1971; JP OPI Publication Nos. 49-73122/1974, 49-24435/1974, 48-43319/1973 and 49-116154/1974; and JP Application Nos. 48-112325/1973, 48-110996/1973 and 49-15096/1974. The layer hardeners may be used in any amount, to provide the effects of the invention and so as to meet the kinds of subject gelatin layers, the physical properties required, and the photographic characteristics. However, it is desired that they are contained in an amount of not less than 0.01 wt% and, desirably, not less than 1 wt% of the dried amount of gelatin contained in the outermost layer and other hydrophilic colloidal layers of a light sensitive material of the invention. The hydrophilic colloidal layers of the light sensitive materials of the invention may contain any other photographic additives than the above-mentioned layer hardeners, if required. The photographic additives include, for example, a gelatin plasticizer, a surfactant, a UV absorbent, an antistaining agent, a pH controller, an antioxidizer, an antistatic agent, a thickener, a graininess improver, a dye, a mordant, a whitening agent, a development speed controller and a matting agent. These additives may be used in any amounts, provided, the effects of the invention cannot be spoiled. Among these various additives, those desirably applicable to the invention include in particular the following additives. For example, the thickeners or plasticizers include the substances given in U.S. Patent No. 2,960,404, JP Examined Publication No. 43-4939/1968, West German Patent No. 1,904,604, JP OPI Publication No. 48-63715/1973, JP Examined Publication No. 45-15462/1969, Belgian Patent No. 762,833, U.S. Patent No. 3,767,410 and Belgian Patent No. 588,143 and, particularly, a styrene-sodium maleate copolymer and dextran sulfate; the UV absorbents include the compounds given in JP Examined Publication No. 48-31255/1973, U.S. Patent No. 3,253,921, British Patent No. 1,309,349, JP Examined Publication No. 48-31255/1973, U.S. Patent No. 3,253,921 and British Patent No. 1,309,349 and, particularly, 2-(2'-hydroxy-5'-tert-butylphenyl)benzotriazole, 2-(2'-hydroxy-3', 5'-di-tert-butylphenyl)benzotriazole, 2-(2'-hydroxy-3'-tert-butyl-5'-butylphenyl)-5-chlorobenzotriazole, 2-(2'-hydroxy-3',5-di-tert-butylphenyl)-5-chlorobenzene triazole; the surfactants include the compounds given in British Patent Nos. 548,532 and 1,216,389, U.S. Patent Nos. 3,026,202 and 3,514,293, JP Examined Publication Nos. 44-26580/1969, 43-17922/1968, 43-17926/1968, 43-13166/1968 and 48-20785/1973, French Patent No. 202,585 and Belgian Patent No. 773,459 and, particularly, sodium-di-2-ethylhexyl sulfosuccinate, sodium-amyl-decyl sulfosuccinate, sodium dodecylbenzene sulfonate and sodium triisopropylnaphthalene sulfonate; the antistaining agents include the compounds given in U.S. Patent Nos. 2,360,210, 2,728,659, 2,732,300 and 3,700,453 and, particularly, 2-methyl-5-hexadecyl-hydroquinone, 2-methyl-5-sec-octadecyl-hydroquinone and 2,5-di-tert-octyl hydroquinone; the antistatic agents include the compounds given in JP Examined Publication No. 46-24159/1971, JP OPI Publication No. 48-89979/1972, U.S. Patent Nos. 2,882,157 and 2,972,535, JP OPI Publication Nos. 48-20785/1973, 48-43130/1973 and 48-90391/1973, JP Examined Publication Nos. 46-39312/1971, 48-43809/1973, 49-4853/1974, 49-64/1974 and 47-8742/1972 and JP OPI Publication No. 47-33627/1972; and the matting agents include the compounds given in U.S. Patent Nos. 1,221,980, 2,992,101 and 2,956,884 and, particularly, silica gel having a particle size within the range of from 0.5 to 20µm and a polymethyl methacrylate polymer having a particle size within the range of from 0.5 to 20µm. The compounds represented by the first compound as defined above or by a compound of Formula (A), (B) or (B') are contained in the outermost layer of backing layers. The material may also contain, if required, a matting agent, a surfactant, a dye and so forth in the outermost layer of the backing layers. As for the matting agents, fine particles of silicon dioxide having an average particle size within the range of from 0.01 to 10µm may desirably be used. There is no special limitation to the various kinds of the above-mentioned additives and the preparation processes thereof. For example, the additives and the preparation processes thereof may be as referred to in Research Disclosure, vol.176, pp.22∼31, Dec., 1978. The methods applicable thereto for coating a layer containing the compounds represented by Formula (A), (B) or (B') include, for example, any known methods such as a curtain-coating method, a reverse-roll coating method, a fountain-coating method, an air-doctor coating method, a slide-hopper coating method, an extrusion-coating method and a dip-coating method. The silver halide emulsions applicable to the invention can be chemically sensitized in any ordinary methods. The chemical sensitization thereof can be performed with gold compounds, noble metal salts such as those of platinum, palladium, rhodium and iridium and, besides, stannous salts and amines. The silver halide emulsions applicable to the invention can be added with a stabilizer or an antifoggant, which include various compounds such as many kinds of heterocyclic compounds, mercury-containing compounds, mercapto compounds and metal salts, as well as 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene and 3-methyl-benzothiazole, 1-phenyl-5-mercaptotetrazole. The silver halide emulsions applicable to the invention can also be added with various spectrally sensitizing dyes so as to meet the objects. These spectrally sensitizing dyes include, for example, melocyanine dyes, carbocyanine dyes and cyanine dyes. In the invention, the color couplers applicable thereto include, for example, 4-equivalent type methylene-containing yellow couplers, 2-equivalent type diketomethyl-containing yellow couplers, 4- or 2-equivalent type pyrazolone-containing magenta couplers, indazolone-containing magenta couplers, α-naphthol-containing cyan couplers and phenol-containing cyan couplers. Besides the above, the so-called DIR couplers may also be used therein. The photographic component layers of the light sensitive materials of the invention can contain a dye, a UV absorbent and the layer hardeners and the surfactants such as those described before. The supports applicable to the light sensitive materials of the invention include, for example, film supports each made of polyolefin (such as polyethylene), a cellulose derivative (such as polystyrene and cellulose triacetate) or a polyester (such as polyethylene terephthalate), or supports each made of a sheet of baryta paper, synthetic paper or paper coated on both sides with the above-mentioned polymer films and the analogues thereof. The photographic component layers of the light sensitive materials of the invention can be coated one layer after another or multilayer-coated at the same time, in various methods such as a dip-coating method, an air-knife coating method, a curtain-coating method and an extrusion-coating method. Various kinds of the additives, vehicles, supports, coating methods and so forth each applicable to the invention can be as referred to in Product Licensing Index, vol.92, pp.107-110, Dec., 1971. There is no special limitation to the exposure light sources for the light sensitive materials of the invention. Therefore, those having a low illuminance up to a high illuminance can be used. The exposure time may be within the range of the order of some tens of seconds to 10 -6 seconds. The light sensitive materials of the invention are applicable to any one of black-and-white photographic light sensitive materials, color photographic light sensitive materials and those for general use, printing use, X-ray use and radiation use. To be more concrete, they are applicable to every silver halide photographic light sensitive material including, for example, black-and-white negative type film, paper and reflection type photographic light sensitive materials; color negative type film, paper and for reversal use; and the so-called coupler-in-developer type color photographic light sensitive materials containing color developing agents in processing solutions. EXAMPLES The illustrations of the effects of the invention will now be cited below. In all the following examples, the amounts of the materials added to the silver halide photographic light sensitive materials shall be indicated by the numbers of grams per sq.meter, unless otherwise expressly stated. The amounts of silver halides and colloidal silver shall be indicated by converting them into the silver contents. Example 1 A subbing process was applied to one side (of the surfaces) of a triacetyl cellulose film support and then the backing layers having the following compositions were each prepared, in order from the support side, on the surface (i.e., on a backing layer) opposite to the subbed surface with interposing the support between. Backing layer 1 This layer was prepared by coating the following backing layer 1 coating solution in a proportion of 20 ml/m 2 and was then dried at 80°C for 5 minutes. Alumina sol AS-100 (manufactured by Nissan Chemical Industries Co., Ltd.) 40 g Acetone 500 ml Methanol 400 ml Dimethyl formamide 100 ml Backing layer 2 On the resulting backing layer 1, the following backing layer 2 coating solution was so coated as to be 20 ml/m 2 and was then dried up at 80°C for 5 minutes. Diacetyl cellulose 1 g SiO 2 fine particles (having an average particle size of 3.0µm) 0.02 g Acetone 500 ml Ethyl acetate 500 ml Backing layer 3 On the resulting backing layer 2, the following backing layer 3 coating solution was so coated as to be 20 ml/m 2 and was then dried up at 90°C for 5 minutes. Toluene 700 ml Methylethyl ketone 300 ml Compound contained in the backing layer (See Table 1) 1 g Next, a multilayered color photographic light sensitive material was prepared by forming each of the layers having the following compositions, in order from the support side, on the surface side (i.e., on the emulsion layer side) of the support opposite to the backing layer. Layer 1 : Antihalation layer (HC) Black colloidal silver 0.15 UV absorbent (UV-1) 0.20 Colored cyan coupler (CC-1) 0.02 High boiling solvent (Oil-1) 0.20 High boiling solvent (Oil-2) 0.20 Gelatin 1.6 Layer 2 : Intermediate layer (IL-1) Gelatin 1.3 Layer 3 : Low-speed red-sensitive emulsion layer (R-L) Silver iodobromide emulsion, (having an average grain size of 0.3µm and an average iodine content of 2.0 mol%) 0.4 Silver iodobromide emulsion, (having an average grain size of 0.4µm and an average iodine content of 8.0 mol%) 0.3 Sensitizing dye (S-1) 3.2x10 -4 (mols/mol of Ag) Sensitizing dye (S-2) 3.2x10 -4 (mols/mol of Ag) Sensitizing dye (S-3) 0.2x10 -4 (mols/mol of Ag) Cyan coupler (C-1) 0.50 Cyan coupler (C-2) 0.13 Colored cyan coupler (CC-1) 0.07 DIR compound (D-1) 0.006 DIR compound (D-2) 0.01 High boiling solvent (Oil-1) 0.55 Additive (SC-1) 0.003 Gelatin 1.0 Layer 4 : High-speed red-sensitive emulsion layer (R-H) Silver iodobromide emulsion, (having an average grain size of 0.7µm and an average iodine content of 7.5 mol%) 0.9 Sensitizing dye (S-1) 1.7x10 -4 (mols/mol of Ag) Sensitizing dye (S-2) 1.6x10 -4 (mols/mol of Ag) Sensitizing dye (S-3) 0.1x10 -4 (mols/mol of Ag) Cyan coupler (C-2) 0.23 Colored cyan coupler (CC-1) 0.03 DIR compound (D-2) 0.02 High boiling solvent (Oil-1) 0.25 Additive (SC-1) 0.003 Gelatin 1.0 Layer 5 : Intermediate layer (IL-2) Gelatin 0.8 Layer 6 : Low-speed green-sensitive emulsion layer (G-L) Silver iodobromide emulsion, (having an average grain size of 0.4µm and an average iodine content of 8.0 mol%) 0.6 Silver iodobromide emulsion, (having an average grain size of 0.3µm and an average iodine content of 2.0 mol%) 0.2 Sensitizing dye (S-4) 6.7x10 -4 (mols/mol of Ag) Sensitizing dye (S-5) 0.8x10 -4 (mols/mol of Ag) Magenta coupler (M-1) 0.17 Magenta coupler (M-2) 0.43 Colored magenta coupler (CM-1) 0.10 DIR compound (D-3) 0.02 High boiling solvent (Oil-2) 0.70 Additive (SC-1) 0.003 Gelatin 1.0 Layer 7 : High-speed green-sensitive emulsion layer (G-H) Silver iodobromide emulsion, (having an average grain size of 0.7µm and an average iodine content of 7.5 mol%) 0.9 Sensitizing dye (S-6) 1.1x10 -4 (mols/mol of Ag) Sensitizing dye (S-7) 2.0x10 -4 (mols/mol of Ag) Sensitizing dye (S-8) 0.3x10 -4 (mols/mol of Ag) Magenta coupler (M-1) 0.03 Magenta coupler (M-2) 0.13 Colored magenta coupler (CM-1) 0.04 DIR compound (D-3) 0.004 High boiling solvent (Oil-2) 0.35 Gelatin 1.0 Layer 8 : Yellow filter layer (YC) Yellow colloidal silver 0.1 Additive (HS-1) 0.07 Additive (HS-2) 0.07 High boiling solvent (Oil-2) 0.15 Gelatin 1.0 Layer 9 : Low-speed blue-sensitive emulsion layer (B-L) Silver iodobromide emulsion, (having an average grain size of 0.3µm and an average iodine content of 2.0 mol%) 0.25 Silver iodobromide emulsion, (having an average grain size of 0.4µm and an average iodine content of 8.0 mol%) 0.25 Sensitizing dye (S-9) 5.8x10 -4 (mols/mol of Ag) Yellow coupler (Y-1) 0.60 Yellow coupler (Y-2) 0.32 DIR compound (D-1) 0.003 DIR compound (D-2) 0.006 High boiling solvent (Oil-2) 0.18 Gelatin 1.3 Layer 10 : High-speed blue-sensitive emulsion layer (B-H) Silver iodobromide emulsion, (having an average grain size of 0.8µm and an average iodine content of 8.5 mol%) 0.5 Sensitizing dye (S-10) 3.0x10 -4 (mols/mol of Ag) Sensitizing dye (S-11) 1.2x10 -4 (mols/mol of Ag) Yellow coupler (Y-1) 0.18 Yellow coupler (Y-2) 0.10 High boiling solvent (Oil-2) 0.05 Gelatin 1.0 Layer 11 : Protective layer 1 (PRO-1) Silver iodobromide, (having an average grain size of 0.08µm and an average iodine content of 1.0 mol%) 0.3 UV absorbent (UV-1) 0.07 UV absorbent (UV-2) 0.1 Additive (HS-1) 0.2 Additive (HS-2) 0.1 High boiling solvent (Oil-1) 0.07 High boiling solvent (Oil-3) 0.07 Gelatin 0.8 Layer 12 : Protective layer 2 (PRO-2) Compound contained in the protective layer (See Table 1) Total (mol ratio 1:1) 0.01 Polymethyl methacrylate, (having an average particle size of 3µm) 0.02 Copolymer of methyl methacrylate: ethyl methacrylate: methacrylic acid = 3:3:4 (in wt ratio), (having an average particle size of 3µm) 0.13 Gelatin 0.5 The silver iodobromide emulsion used in Layer 10 was prepared in the following process. The silver iodobromide emulsion was prepared, in a double-jet process, by making use of the monodisperse type silver iodobromide grains having an average grain size of 0.33µm (and having a silver iodide content of 2 mol%) as the seed grains. While keeping solution <G-1%> to be a temperature of 70°C, a pAg of 7.8 and a pH of 7.0 and stirring, it was added with a seed emulsion equivalent to 0.34 mols. (Formation of an internal high iodine phase -a core phase-) After then, with keeping the flow rate of <H-1> to <S-1> to be 1:1, the resulting mixture was added by taking 86 minutes at an accelerated flow rate (i.e., the final flow rate was 3.6 times as fast as the initial flow rate.) (Formation of an external low iodine phase -a shell phase-) Successively, with keeping the pAg and pH at 10.1 and 6.0, respectively, <H-2> and <S-2> were added by taking 65 minutes at the flow rates accelerated by the flow rate of 1:1 (i.e., the final flow rate was 5.2 times as fast as the initial flow rate.) The pAg and pH in the course of forming grains were controlled with an aqueous potassium bromide solution and an aqueous 56% acetic acid solution. After completing the grains, they were washed in an ordinary flocculation method and were then redispersed by adding gelatin, so that the pAg and pH were adjusted to be 8.06 and 5.8 at 40°C, respectively. The resulting emulsion was proved to be a monodisperse type emulsion containing octahedral silver iodobromide grains having an average grain size of 0.80µm, a distribution range of 12.4% and a silver iodide content of 8.0 mol%. <G-1> Osein gelatin 100.0 g A 10 wt% methanol solution containing compound-[I] 25.0 ml An aqueous 28% ammoniacal solution 440.0 ml An aqueous 56% acetic acid solution 660.0 ml Add water to make 5000.0 ml <H-1> Osein gelatin 82.4 g Potassium bromide 151.6 g Potassium iodide 90.0 g Add water to make 1030.5 ml <S-1> Silver nitrate 309.2 g An aqueous 28% ammoniacal solution An equivalent amount Add water to make 1030.5 ml <H-2> Osein gelatin 302.1 g Potassium bromide 770.0 g Potassium iodide 33.2 g Add water to make 3776.8 ml <S-2> Silver nitrate 1130.0 g An aqueous 28% ammoniacal solution An equivalent amount Add water to make 3776.8 ml The average grain size of the seed grains, the temperature, the pAg and pH, the flow rate, the adding time and the halide compositions of the seed grains were each varied in the same manner as above, so that emulsions having different average grain sizes and silver iodide contents could be prepared. Each of the resulting emulsions was a core/shell type monodispersed emulsion having a distribution range of not wider than 20%. Each of the emulsions was subjected to the optimum chemical sensitization in the presence of sodium thiosulfate, chloroauric acid and ammonium thiocyanate and was then added with sensitizing dyes and 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene-1-phenyl-5-mercaptotetrazole. Further, the resulting light sensitive material samples each contained compounds Su-1 and Su-2, a viscosity controller, layer hardeners H-1 and H-2, stabilizer ST-1, antifoggants AF-1 and AF-2 (having weight average molecular weights of 10000 and 1100000, respectively), dyes AI-1 and AI-2 and compound DI-1 (in an amount of 9.4/m 2 ). (Method for measuring a pressure fog) The sample was prepared in a dark room and then cut into a size of 35mm x 111mm. The cut piece of the sample was loaded in a cartridge (of a current type) having an inner diameter of 22mm. In the state where the sample-loaded cartridge was loaded in Konica Camera FT-1 (manufactured by Konica Corp.), a forced aging test was carried out (at 23°C and 80%RH for one day). After then, the whole light sensitive material sample was wound up. Next, the light sensitive material sample was developed in the following processing steps and the resulting pressure fog was evaluated. The yellow density of the resulting spot-like fog and the unfogged portions on the leading edge side of the sample were measured by a microdensitometer. From the measurement results, the density difference ΔD was obtained and was then evaluated in the following criteria. ○: 0∼0.06, Δ: 0.07∼0.12, ×: 0.12∼0.19, ××: 0.20 or more The samples prepared in the above-described manner were exposed wedgewise to white light and were then developed. Processing step A Processing time Processing temperature Amount replenished Color developing 3min.15sec 38°C 780 ml Bleaching 45sec 38°C 150 ml Fixing 1min.30sec 38°C 830 ml Stabilizing 60sec 38°C 830 ml Drying 1min. 55°C ― (The amounts replenished were indicated by the values per sq.meter of the subject light sensitive materials.) The stabilizing step was carried out in a three-tank-cascade system. Color developer Water 800 ml Potassium carbonate 30 g Sodium hydrogen carbonate 2.5 g Potassium sulfite 3.0 g Sodium bromide 1.3 g Potassium iodide 1.2 mg Hydroxylamine sulfate 2.5 g Sodium chloride 0.6 g 4-amino-3-methyl-N-ethyl-N-(β-hydroxylethyl) aniline sulfate 4.5 g Diethylenediamine pentaacetate 3.0 g Potassium hydroxide 1.2 g Add water to make 1 liter Adjust pH with potassium hydroxide or a 20% sulfuric acid solution to be pH10.06 Color developer replenisher Water 800 ml Potassium carbonate 35 g Sodium hydrogen carbonate 3 g Potassium sulfite 5 g Sodium bromide 0.4 g Hydroxylamine sulfate 3.1 g 4-amino-3-methyl-N-ethyl-N-(β-hydroxylethyl) aniline sulfate 6.3 g Potassium hydroxide 2 g Diethylenediamine pentaacetate 3 g Add water to make 1 liter Adjust pH with potassium hydroxide or a 20% sulfuric acid solution to be pH10.18 Bleacher Water 700 ml Ferric ammonium 1,3-diaminopropane tetraacetate 175 g Disodium ethylenediamine tetraacetate 2 g Sodium nitrate 50 g Ammonium bromide 150 g Glacial acetic acid 40 g Add water to make 1 liter Adjust pH suitably with aqueous ammonia or glacial acetic acid to be pH4.4 Bleacher replenisher Water 700 ml Ferric ammonium 1,3-diaminopropane tetraacetate 180 g Disodium ethylenediamine tetraacetate 2 g Sodium nitrate 50 g Ammonium bromide 200 g Glacial acetic acid 56 g Adjust pH with aqueous ammonia or glacial acetic acid to be pH4.0 Add water to make 1 liter Fixer Water 800 ml Ammonium thiosulfate 150 g Ammonium thiocyanate 120 g Sodium sulfite 15 g Disodium ethylenediamine tetraacetate 2 g Adjust pH with acetic acid and aqueous ammonia to be pH6.2 Add water to make 1 liter Fixer replenisher Water 800 ml Ammonium thiosulfate 180 g Ammonium thiocyanate 150 g Sodium sulfite 20 g Disodium ethylenediamine tetraacetate 2 g Adjust pH with acetic acid and aqueous ammonia to be pH6.5 Add water to make 1 liter Finger-print smudge resistance The evaluation method is as follows: Each of the samples was cut into a film strip (a 24-exposure film) measuring 35 × 117 mm which was put in a cartridge having an inner diameter of 22 mm after being wound around a spool having an outer diameter of 11 mm. Each sample was subjected to moisture treatment for 5 hours under the conditions of 25°C in temperature and 70%RH in relative humidity. A tester, on the other hand, washed his hands well with a neutral detergent (10% aqueous solution), rinsed with water, and dried with a dryer. After that, he put on cotton gloves and kept them on for 1 hour. Then, the took off the gloves and put his hand on the sample naturally as far as possible and applied a load of 1 kg on his hand for 30 seconds to mark a fingerprint on the sample. After 20 minutes, the marked fingerprint was tried to be wiped off with a cloth. Then, a remaining fingerprint on each of the samples was observed and evaluated by three evaluators as follows: o ○ Finger-print was wiped off completely, ○ Finger-print was almost wiped off, but remained faintly, Δ Finger-print remained a half or more, × Finger-print could not be wiped off at all, (with scratches) Kinetic friction coefficient measurement method The kinetic friction coefficient to the velvet of the backing outermost layer of a subject sample was measured by making use of a Nylon-made 1-cm 2 -sized velvet to which a 100 g load was applied under the conditions of a speed at 10cm/minute, (provided, however, the temperature was 23°C and the humidity was 55%.) The results thereof will be shown in Table 1. Adhesion resistance evaluation method A sample was cut into two pieces each having a size of 5cm 2 . The cut pieces were stored for one day in an atmosphere at 23°C and 80%RH so as not to come into contact with each other. The protective layers of the two pieces of one and the same sample were brought into contact with each other and were then applied with a load of 800 g. They were stored for three days in an atmosphere at 40°C and 80%RH. After that, the sample was peeled off and the area of the adhered portion was measured, so that the adhesion resistance thereof was measured. The evaluation criteria were as follows. Rank Adhesion area A 0 to less than 10% B 10 to less than 20% C 20 to less than 40% D 40 to less than 60% E 60% or more High humidity slidability measurement method The high humidity slidability of the outermost layer on the emulsion side of a sample was evaluated in terms of a kinetic friction coefficient to the outermost backing layer of Sample (I-1) cut into a 1 cm 2 size. The above-mentioned measurement was carried out in the conditions that a load of 50 g was applied and a speed was at a rate of 10 cm/minute. (provided, the temperature was 23°C and the humidity was 92%RH.) Scratch resistance measurement A 35mm x 117cm sized film (for 24ex.) was stored in a cartridge having an inner diameter of 22mm, wound around a spool having an outer diameter of 11mm and was then forcibly aged (at 55°C for one day). After that, some suitably amount of sand were sprinkled over the backing layer side of the film in the velvet portion of the cartridge and the film was then pulled out at a speed of 20 cm/second. The scratches resulted on the backing layer surface of the film were evaluated according to the following criteria. Criteria for evaluating scratch resistance: O: No scratch was found at all, Δ: Few scratches were found, X: Serious scratches were found. Antistaticity measurement Antistaticity was graded by measuring the static mark productions. The static mark production test was tried in the method that the surface of the emulsion layer side of an unexposed light sensitive material subject to the test was put downward on a rubber sheet and they were contacted with pressure by a rubber roller. After that, they were peeled off from each other so that static marks could be produced. The test was tried in an atmosphere at 25°C and 25%RH. The rehumidification of the test pieces was carried out for 24 hours in the foregoing conditions. The evaluation was made in accordance with the following 5 ranks. A: No static mark production was found, B: Little static mark production was found, C: Considerable static mark production was found, D: Serious static mark production was found, E: Static mark production was found on the whole surface. The results of the above-mentioned various evaluation will be shown in Table 1. As is obvious from Table 1, it was proved that the finger-print adhesion, the pressure fog produced at a high humidity and, particularly, in a high humidity and high temperature atmosphere, the adhesion resistance, the antistaticity and so forth can remarkably be improved when making combination use of a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant in the outermost layer and, at the same time, when making use of a higher aliphatic acid (or the salt thereof) or an aliphatic hydrocarbon group-containing ester in the outermost layer of the backing layers. Example 2 Samples were each prepared in the same manner as in Example 1. The amounts added and mixing ratios of the fluorine-containing anionic surfactant and fluorine-containing cationic surfactant, and the amounts added of the higher aliphatic acid (or the salt thereof) or the aliphatic hydrocarbon group-containing ester were as follows: Table 2 shows the results of the kinetic friction coefficients, scratch resistance, antistaticity, adhesion resistance, finger-print adhesion on high humidity slidability and pressure fog. As is obvious from Table 2, when a sample was applied with a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant each in a desirable mixing ratio and in a desirable amount added to the outermost layer and also applied with a higher aliphatic acid (or the salt thereof) or an aliphatic hydrocarbon group-containing ester in a desirable amount, the resulting sample can remarkably be improved in finger-print adhesion, pressure fog production at a high humidity and, particularly, in a high temperature and high humidity atmosphere, adhesion resistance, antistaticity and so forth. Example 3 The emulsion side of a sample was prepared in the same manner as in Example 1 and the backing layer side thereof was prepared in the following manner. Backing layer 1 The following backing layer 1 coating solution was coated in a proportion of 20 ml/m 2 and was then dried at 80°C for 5 minutes. (Backing layer 1 coating solution) Gelatin 10 g Alumina sol, AS-100 (manufactured by Nissan Chemical Industrial Co., Ltd.) 30 g Acetone 500 ml Methanol 400 ml Dimethyl formamide 100 ml Backing layer 2 The following backing layer 2 coating solution was coated over the backing layer 1 so as to be 20 ml/m 2 and was then dried at 80°C for 5 minutes. (Backing layer 2 coating solution) Gelatin 10 g Diacetyl cellulose 1 g SiO 2 fine particles (having an average particle size of 3.0µm) 0.020 g Acetone 500 ml Ethyl acetate 500 ml Backing layer 3 The following backing layer 3 coating solution was coated on the film coated with the backing layer 2 thereon, so as to be 20 ml/m 2 and was then dried at 90°C for 5 minutes. (Backing layer 3 coating solution) Gelatin 10 g Toluene 700 ml Methylethyl ketone 300 ml Polymethyl methacrylate (having an average particle size of 2.5µm) 0.03 g Poly(methyl methacrylate/methacrylic acid : 60/40 in mol ratio) (having an average particle size of 2.1 µm) 0.02 g Higher aliphatic acid (or the salt thereof) or higher aliphatic acid ester (See Table 3) 1 g Fluorine-containing surfactant, (those of the anionic and cationic type) (See Table 3) (in a mol ratio of 1:1) Total 0.5 g Table 3 shows the results of the kinetic friction coefficients, scratch resistance, antistaticity, adhesion resistance, high humidity slidability, finger-print adhesion resistance and pressure fog production resistance. As is obvious from Table 3, it was proved that, when a sample was applied with a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant each to the outermost layer and also applied with a higher aliphatic acid (or the salt thereof) or an aliphatic hydrocarbon group-containing ester to the outermost layer of the backing layers, the resulting sample can remarkably be improved in finger-print adhesion, pressure fog production at a high humidity and, particularly, in a high temperature and high humidity atmosphere, adhesion resistance, antistaticity and so forth.

Claims: A silver halide photographic light-sensitive material comprising a support and a silver halide photographic emulsion layer and a protective layer provided in that order on a first side of the support, and a backing layer and a protective backing layer provided in that order on the second side of the support opposite to the silver halide photographic emulsion layer, wherein at least one outermost layer of the material comprises a fluorine-containing anionic surfactant and a fluorine-containing cationic surfactant and the outermost layer on the second side of the support comprises at least one of a first, second or third compound wherein the first compound is chosen from C-1 (n)C 21 H 43 COOC 17 H 35 (iso), C-2 (n)C 21 H 43 COOC 15 H 31 (iso), C-3 (n)C 21 H 43 COOC 18 H 37 (iso), C-4 (n)C 21 H 43 COOC 24 H 49 (iso), C-5 (iso)C 17 H 35 COOC 32 H 65 ∼ C 36 H 73 (iso), C-6 (n)C 27 H 55 COOC 18 H 37 (iso), C-7 (n)C 17 H 35 COOC 32 H 65 ∼ C 36 H 73 (iso), C-8 (n)C 21 H 43 COOC 16 H 33 (iso), C-9 (n)C 21 H 43 COOC 20 H 41 (iso), C-10 (n)C 23 H 47 COOC 24 H 49 (iso), C-11 (iso)C 17 H 35 COOC 50 H 101 (n), C-12 (iso)C 23 H 47 COOC 24 H 49 (iso), C-13 (iso)C 31 H 63 ∼ C 36 H 71 COOC 18 H 37 (iso), C-14 (n)C 27 H 55 COOC 24 H 49 (iso), C-53 (n)C 25 H 51 COOC 18 H 37 (iso), C-56 (n)C 27 H 35 COOC 18 H 37 (iso), C-60 (n)C 21 H 43 COOC 24 H 49 (iso), C-65 (n)C 15 H 31 COOC 16 H 33 (n), and C-66 (n)C 17 H 35 COOC 18 H 37 (n), the second compound is a compound of Formula (A) below, and the third compound is a compound of Formulae (B) or (B') below: Formula (A) RCOOM wherein R represents an aliphatic hydrocarbon group and M represents a cationic group, Formula (B) R 1 -(COO)-X-(OOC)-R 2 FORMULA (B') R 1 (OOC)-X-(COO)-R 2 wherein R 1 and R 2 each represent an aliphatic hydrocarbon group and X represents a divalent bonding group. A material according to claim 1, wherein the fluorine-containing anionic surfactant is a compound represented by the following Formula (FA): Formula (FA) (Cf)-Y wherein Cf represents a group having at least three fluorine atoms and at least two carbon atoms; and Y represents -COOM, -SO 3 M, -OSO 3 M, or -P(=O) (OM) 2 wherein M represents a hydrogen atom, an alkali metal or a quaternary ammonium group. A material according to claim 1, wherein the fluorine-containing anionic surfactant is a compound represented by the following Formula (FA'): Formula (FA') (Rf)-D-Y wherein Rf represents a fluorine-containing alkyl group having from 3 to 30 carbon atoms or a fluorinated aryl group having from 6 to 30 carbon atoms; D represents a divalent bonding group having from 1 to 12 carbon atoms and at least one of -O-, -COO-, -CON(R 1 )- and -SO 2 N(R 1 )- wherein R 1 represents an alkyl group having from 1 to 5 carbon atoms; and Y represents -COOM, -SO 3 M, -OSO 3 M or -P(=O) (OM) 2 wherein M represents a hydrogen atom, an alkali metal or a quaternary ammonium group. A material according to any preceding claim, wherein the content of the first, second or third compound is from 1 to 500 mg per square meter of the light-sensitive material. A material according to claim 4, wherein the content of the first, second or third compound is from 5 to 100 mg per square meter of the light-sensitive material. A material according to any preceding claim, wherein the fluorine-containing cationic surfactant is a compound represented by the following Formula (FK) : Formula (FK) Rh-T-X + Z - wherein Rh represents a fluorine-containing hydrocarbon group having from 3 to 20 carbon atoms; T represents a divalent bonding group; X represents a cationic group, and Z represents a counter anion. A material according to any preceding claim, wherein the total content of the fluorine-containing anionic surfactant and the fluorine-containing cationic surfactant is from 0.1 to 1000 mg per square meter of the light-sensitive material. A material according to claim 7, wherein the total content of the fluorine-containing anionic surfactant and the fluorine-containing cationic surfactant is from 1.0 to 150 mg per square meter of the light-sensitive material. A material according to any preceding claim, wherein M in formula (A) represents Na, K, Li, Ca, Sr, Ba, HN(R 2 ) 3 or N(R 2 ) 4 wherein R 2 represents an alkyl group having from 1 to 18 carbon atoms. A material according to any preceding claim, wherein R 1 and R 2 in formula (B) or (B') each independently represent an aliphatic hydrocarbon group having from 12 to 70 carbon atoms. A material according to any preceding claim wherein the third compound is chosen from the following compounds: and or is a compound of the following formula R 1 -CO-O-X-O-CO-R 2 wherein R 1 , R 2 and X are as defined in Claim 1.

Inventors: MOCHIZUKI YOSHIHIRO, UEDA EIICHI, MOCHIZUKI, YOSHIHIRO, UEDA, EIICHI, MOCHIZUKI, YOSHIHIRO, KONICA CORPORATION, UEDA, EIICHI, KONICA CORPORATION
Applicants: KONISHIROKU PHOTO IND, KONICA CORPORATION
Application year: 1993
Main classification: G03C1
IPC codes: G03C1