Non aqueous dispersion ink

Abstract: Ink formulations have been conceived that result in inks having improved shelf life, tack and flow properties so that problems relating to ink plugging with contemporary ink pads are reduced. Another advantage of the inks is that they have improved paper dust resistance. These inks are made of a coloring material having an organic pigment dispersed in a modified rosin ester or dispersed in a modified rosin ester and triazine formaldehyde aryl sulphonamide resin dispersed in an alkyd oil. The solvent system is preferably composed of non drying solvents such as emollients and high molecular weight glycols.

Description: Great demands have been made upon printing systems and materials therefor in light of the need of faster printing, in conjunction with the computer age, and the seeking of lower toxicity to comply with governmental environmental regulations. In high speed printing, a problem has been encountered with paper dust which is generated during paper transport and the impact of a printing element on the paper. This is particularly true of the printing on envelopes which are made of paper with loose fibers. One of the components of the printing system that has required extensive modification is the ink. In most printing applications, a pad or roller made of a porous material is supplied with ink for the purpose of transferring the ink to a printhead. The printing pad may be one which is self contained or it may be one that is periodically supplied with ink from a reservoir. The problems in producing a satisfactory fluorescent ink are compounded because a plurality of dyes and pigments are required for achieving good color, fill in, edge acuity and the other qualities required from an ink. One of the major problems associated with inks is aging which results in printing that has a change in color and intensity with the passing of the time the ink is stored. An ink that overcomes the aging problem and shows low environmental sensitivity (high humidity and low and high temperatures), low tackiness and flow properties, material compatibility and paper dust resistance would be advantageous. Another consideration is that the ink pad must function in an open environment without drying for at least six months; therefore, the ink solvents should be non volatile. An example of a printing ink of the prior art is given in U.S. Patent No. 4079026, which relates to printing inks containing a dispersed phase of coloured resin particles in a continuous phase liquid-film forming vehicle which is a non-solvent for the coloured resin particles. The composition comprises 55 to 75 wt. % of a binder resin system consisting essentially of 15 to 30 wt. % of a drying oil modified alkyd resin, 40 to 70 wt. % of an ester of modified resin and 15 to 30 wt. % of a low molecular weight, carboxylated hydrocarbon resin. We have now found it possible to provide non aqueous dispersion ink formulations which are nontoxic and have flow properties which substantially reduce the tendency of the ink to cause plugging in an inking pad. Ink pad life has a variability caused mainly by the inherent properties of the ink with which it is used. The inking pad may be assembled with two layers of foam, the first layer serving as an ink reservoir layer and the second layer serving as a metering layer which contacts the print head. Because of its high density and smaller pore size, the metering layer can act as a filter as a consequence of the ink concentrating at the interface of the two layers. As a result, plugging tends to occur. Of course, what is meant by plugging is the fact that particles of the ink are captured within the pores of the inking member and thus prevent the tlow of ink. It has been found that the plugging onset can be delayed with the ink formulations of the instant invention because of decreased dissolved resin concentration, thereby decreasing the viscosity, even though the size of the pigments can vary from 0.1µm to 0.5µm. According to a first aspect of the present invention, there is provided a non aqueous dispersion ink composition, comprising: a) 40 to 90 wt. % of a non-aqueous continuous phase solvent comprising: (i) 70-90 wt. % of an emollient selected from stearyl polyoxypropylene ether and polyoxypropylene (10) cetyl ether, and (ii) 10-30 wt. % of polypropylene glycol, b) 0.2-1 wt . % of an organic titanate coupling agent, and c) 1-10 wt. % of an organic pigment dispersed in a rosin ester vehicle, 98% or more of the organic pigment particles having an average particle size of 0.1-0.4 µm. The ink formulation of the instant invention is based on organic pigments dispersed in rosin esters or a combination of organic pigments dispersed in rosin esters and amino formaldehyde resin dispersed in an alkyd resin. The resulting colour of these inks can be red, blue, green or black. It has been found that these ink formulations reduce the effects of paper dust accumulations because the solvents of the instant ink formulations are non drying on the printing elements and maintains printing elements in a wet state. Furthermore, the solvent has emollient properties. This wet state causes the flushing of elements resulting in paper dust being carried away. Lower concentrations of dissolved resin produces a lower tack ink which results in less paper dust attraction in the ink. The ink formulations of the instant invention have low environmental sensitivity due to small variation of the viscosity in the operating temperature range of 5 to 45°C and the low hygroscopicity of the solvents. Use of an emollient in the ink formulation solvent has been found to be compatible with the pigments used to produce the ink, provides low toxicity, ease of fabrication of the ink, is inert to materials in the inking system and provides a non-drying ink. Another advantage to the inclusion of an emollient solvent is that it is non-volatile and consequently results in the inking pad not drying. According to a further aspects, the present invention provides a non-aqueous dispersion ink composition comprising: a) 40-90 wt. % of a non-aqueous phase solvent comprising: (i) 70-90 wt. % of an emollient selected from stearyl polyoxypropylene ether and polyoxypropylene (10) cetyl ether, and (ii) 10-30 wt. % polypropylene glycol, b) 1-10 wt. % of an organic pigment dispersed in a rosin ester vehicle, 98% or more of the organic pigment particles having an average particle size of 0.1-0.4 µm, c) up to 10 wt. % of an organic pigment flushed in a non-ionic surfactant, d) 5 to 20 wt. % of a triazine aryl sulphonamide paraformaldehyde resin dispersed in alkyd linseed oil resin, and e) up to 0.5 wt. % of an organic titanate coupling agent. The formulations of the instant invention provide inks with improved print quality, are inert to materials used in a printer such as inker foams and rubber, low tack, good shelf life stability, and good flow through porous foam materials. It has been found that the inks of the instant invention have an acceptable shelf life. The aged samples show no settling after two weeks of accelerated testing. The aging of the inks by temperature shock shows no settling for the inks during two weeks of accelerated testing that simulated one year of aging by varying the temperature between 70°C to -20°C, every four hours of the working day. The dual inker foam described above that is used in high speed flat bed systems is made of a polychloroprene foam bottom layer. The top layer is made of polyethylene sintered foam. The rubber used in the printing elements is made of polybutadiene acrylonitrile rubber, which is plasticized with dibutyl phthalate. The solvents used in the instant ink formulations are inert to all these materials. The print head should be usable for ten million prints, or ten years, and the pad materials should be compatible with the inks for six months. The pigment dispersion used in the ink formulation is stabilized by using easily dispersible pigments predispersed in a rosin ester vehicle. The rosin ester dispersants are used because of the wide range of compatibility with solvents and resins. It is preferred that the ink composition further comprises up to 10 wt. % of an organic pigment flushed in an non-ionic surfactant. It is further preferred that the ink composition should further comprise 5 to 20 wt. % of a triazine aryl sulphonamide paraformaldehyde resin dispersed in linseed oil alkyd resin. In a further preferred embodiment, the non-aqueous continuous phase further includes trace to 1 wt. % of fumed silica grafted with polysiloxane groups which acts as a surface tension modifier. It is further preferred that the non-aqueous continuous phase of the ink composition should further include up to 5 wt. % of nonyl phenoxy polyoxyethylene ethanol. It is also preferred that the non-aqueous phase should further include up to 10 wt. % of an alkyd linseed oil resin. The solvent system is of the emollient solvent type. The solvent system is composed of a mixture of 10 to 30% of low molecular weight polypropylene glycol and 70 to 90% of polyoxypropylene stearyl ether or polyoxypropylene (1C) cetyl ether (the emollient solvent). Nonyl phenoxy polyoxyethylene ethanol may be present in an amount up to 5%. All percentages in this disclosure and the accompanying claims are in weight percent. Other solvents that can be present in the non-aqueous continuous phase solvent are castor oil, soya bean oil and oleic acid. The condition for use of these other emollient solvents is that the viscosity is in the range of 20 to 300 mPa.s. The pigment dispersion can be further stabilized with a neoalkoxy titanate coupling agent and emulsifiers such as nonyl phenoxy polyethoxylated alcohols, which emulsifiers have an HLB (hydrophylic lipophylic balance) value from 2 to 15. The solvent system is inert to the materials used in the printer, such as ink foams, print elements, pumps, tubing, print pads, and the like. The formulation of the instant invention involves unique color combinations based on mixtures of organic pigments such as the phthalocyanines and results in strong colors with high purity. Other organic pigments that can be used are given in the General Composition table hereinafter. The selection of the phthalocyanines for the blue ink is based on their dichroic properties. They reflect highly in the red region of the spectrum where the transmitted color is much greener. The organic pigments such as the phthalocyanines can be used in different forms such as powder or chips or predispersed pigments in rosin esters and organic pigments flushed with non-ionic surfactants such as oleyl alcohol ethoxylates. The average particle size of the organic pigments is between 0.1 and 0.4 µm for at least 98% of the particles. Another component that may be included as an additive to the ink formulations is fumed silica with grafted polysiloxane groups. This additive controls the thixotrophy of the ink, reduces surface tension and flattens the variation of the viscosity at different temperatures. At the same time, it reduces the hygroscopicity of the ink. The present invention provides a new class of inks that are compatible with the polymeric materials used in contemporary printers. Examples of such inks are as follows: General Composition Ingredients Weight % 1. Organic pigments (≈ 33%) predispersed in a rosin ester (≈67%) 1-10% a. C.I. Pigment Blue 15.1 or Blue 15.3 b. RED LAKE C (Pigment Red 53:1) c. Pigment Red C.I.#144 d. Permanent Red (Pigment Red 48) e. Little Red (Pigment Red 49:1) f. Pigment Yellow C.I. #110 g. Pigment Brown C.I. #23 h. Pigment Green C.I. #7 i. Pigment Black C.I. #7 2. Organic pigments (same as pigments 1a - 1i above) (≈20%) flushed in a non-ionic surfactant (≈ 80%) (optional) Up to 10% a. Oleyl alcohol ethoxylate b. Fatty acid ester C12 to C14 3. Non-aqueous continuous phase combination of 70-90% of stearyl polyoxypropylene ether or polyoxypropylene (10) cetyl ether with 10-30% polypropylene glycol; and optionally oleic acid, castor oil and soya bean oil. 40-90% 4. Triazine aryl sulphonamide paraformaldehyde resin (50%) dispersed in linseed oil alkyd resin (50%) (optional) 5 to 20% 5. Low polarity emulsifier (optional) nonylphenoxypolyoxyethylene ethanol HLB value 2-4.9 1 - 5% 6. Moderate polarity emulsifier (optional) nonylphenoxypolyoxyethylene ethanol HLB value 11-16 1.0 to 5.0% 7. Surface tension modifier (optional) a) silicon glycol 0.1 to 0.3% b) fumed silica with grafted polysiloxane groups 0.5% trace to 1% 8. Coupling Agent (optional) titanate neoalkoxy 0.2 to 1% 9. Linseed oil alkyd (optional) up to 10% It will be appreciated that the above are given by way of example only and one skilled in the art will recognize that other components having similar properties can be used in the practice of the invention. EXAMPLE I - Red Ink Ingredient Manufacturer wt % Organic pigment Microlith Yellow 2GT (≈ 33% and ≈ 67% rosin ester) CIBA Geigy 2.0 MICROLITH SCARLET R-T 0.5 Pigment Red 52:1 (20%) in Ameroxol OE-5 (80%) Penn Color 7.0 D-500 Colorless triazine/ aryl sulphonamide/formaldehyde resin (50%) in linseed oil (50%) Lawter Int. 14.0 Polypropylene glycol (PLURACOL P-400) BASF 11.9 Nonyl phenoxy polyoxyethylene ethanol ICEPAL CO-210 GAF 2.0 Nonyl phenoxy polyoxyethylene ethanol ICEPAL CO 530 2.0 Titanate Coupling Agent (Lica 38) (titanium IV nesalkanolato, tris (diisooctyl) pyrophosphate) Kenrich .3 Arlamol E (polyoxypropylene stearyl ether) ICI 60.3 The above embodiments have been given by way of illustration only, and other embodiments of the instant invention will be apparent to those skilled in the art from consideration of the detailed description.

Claims: A non-aqueous dispersion ink composition comprising: a) 40 to 90 wt. % of a non-aqueous continuous phase solvent comprising: (i) 70-90 wt. % of an emollient selected from stearyl polyoxypropylene ether and polyoxypropylene (10) cetyl ether, and (ii) 10-30 wt. % of polypropylene glycol, b) 0.2-1 wt. % of an organic titanate coupling agent, and c) 1-10 wt. % of an organic pigment dispersed in a rosin ester vehicle, 98% or more of the organic pigment particles having an average particle size of 0.1-0.4 µm. A non-aqueous dispersion ink composition according to Claim 1, further comprising up to 10 wt. % of an organic pigment flushed in a non-ionic surfactant. A non-aqueous dispersion ink composition according to Claim 1 or Claim 2, further comprising 5 to 20 wt. % of a triazine aryl sulphonamide paraformaldehyde resin dispersed in alkyd linseed oil resin. A non-aqueous dispersion ink composition according to any preceding Claim, wherein said non-aqueous continuous phase further includes trace to 1 wt. % of fumed silica grafted with polysiloxane groups which acts as a surface tension modifier. A non-aqueous dispersion ink composition according to any preceding Claim, wherein said non-aqueous continuous phase further includes up to 5 wt. % of nonyl phenoxy polyoxyethylene ethanol. A non-aqueous dispersion ink composition according to any preceding Claim, wherein said non-aqueous phase further includes up to 10 wt. % of an alkyd linseed oil resin. A non-aqueous dispersion ink composition comprising: a) 40-90 wt. % of a non-aqueous phase solvent comprising: (i) 70-90 wt. % of an emollient selected from stearyl polyoxypropylene ether and polyoxypropylene (10) cetyl ether, and (ii) 10-30 wt. % polypropylene glycol, b) 1-10 wt. % of an organic pigment dispersed in a rosin ester vehicle, 98% or more of the organic pigment particles having an average particle size of 0.1-0.4 µm, c) up to 10 wt. % of an organic pigment flushed in a non-ionic surfactant, d) 5 to 20 wt. % of a triazine aryl sulphonamide paraformaldehyde resin dispersed in alkyd linseed oil resin, and e) up to 0.5 wt. % of an organic titanate coupling agent. The non-aqueous dispersion ink composition according to any preceding Claim, wherein the emollient is stearyl polyoxypropylene ether.

Inventors: AUSLANDER JUDITH D, HOCHWALT NORMAN C, AUSLANDER, JUDITH D., HOCHWALT, NORMAN C.
Applicants: PITNEY BOWES INC, PITNEY BOWES INC.
Application year: 1993
Main classification: C09D11
IPC codes: C09D11