Solid solution semiconductor laser element material and laser element

Abstract: The present invention relate to a solid solution semiconductor laser element material which can form a laser element which oscillates in an infrared region of wavelength 0.2-8 µm, varies wavelength and is operable in the vicinity of room temperature, particularly a laser element of a lattice-matching double hetero junction or lattice-matching quantum well structure. The disclosed solid state semiconductor is made of a material selected from a material having the general chemical formula Ca 1-x Pb x X where, 0<x<0.5 and X is at least one element selected from S, Se and Te, and a material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X where, 0<x≦0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn, and a material having the general chemical formula Ca 1-x Pb x S 1-z Se z where, 0<x≦0.4 and 0≦z≦1.

Description: The present invention relates to a solid solution semiconductor laser element material consisting of a solid solution semiconductor having the general chemical formulae Ca 1-x Pb x X and Ca 1-x (Pb 1-y Y y ) x X, oscillating within a wide region of wavelenght 0.2-8 µm and being operable in the vicinity of a room temperature and a laser element with the use of this material. The structure of a semiconductor laser element is explained by referring to Fig. 1, Figs. 1(A), 1(B) and 1(C) show a lattice matching type double hereto junction structure laser element, a lattice matching type quantum well structure laser element and its partly enlarged view, respectively, and a laser beam is emitted from an active layer 2 sandwiched by cladding layers 1, 1 in the arrow direction by flowing a current through an electrode 3, 3. In case of the semiconductor laser element, a laser beam is different from the other gas laser and the like and faint, so that there has recently been designed to increase luminous efficiency of laser by a complicated structure dividing an active layer 2 into a barrier layer 4 and a quantum well 5 as shown in Fig. 1(B). As a task required for the above-described semiconductor laser, it is important to increase an operating temperature and to have good junction between a cladding layer 1 and active layer 2. Hitherto, as wavelength variable semiconductor laser element material within a region of wavelength 0.2-8 µm, there have been known Hg 1-x Cd x Te where 0<x≦1 as a II-VI group compound semiconductor and InAs or InSb as a III-V group compound semiconductor and each kind of IV-VI group compound semiconductors. Among them, the IV-VI group compound semiconductor is noted as the most practically usable material from the point of a high operating temperature and large wavelength variation, and Pb 1-x Cd x S 1-y Se y or Pb 1-x Eu x Te 1-y Se y as a quaternary lead salt solid solution semiconductor has hitherto been known. A laser element is usually formed with a double hetero junction structure substantially matching lattice constants of an active layer 2, a charge carrier, and a light beam cladding layer, wherein the cladding layer 1 is made Pb 1-x Cd x S 1-y Se y or Pb 1-x Eu x Se y Te 1-y , and the active layer 2 is made PbS or Pb 1-x' Eu x' Se y' Te 1-y' , respectively. Operating temperatures are 200 K and 270 K, respectively, but only attained by pulse oscillation, and if the pulse oscillation becomes continuous oscillation, operating temperatures are further disadvantageously lowered in the continuous oscillation and cannot practically be used. Generally, in order to increase the operating temperature of the above injection type semiconductor laser, it is desired to form a laser element with a lattice matching type double hetero junction structure or lattice matching type quantum well structure matching each lattice constant of active layer, a charge carrier and beam cladding layer, and it is further greatly desired to make an energy gap of the cladding layer 1 larger than that of the active layer 2 and to make its difference sufficient, but in either one of Pb 1-x Cd x S 1-y Se y or Pb 1-x Eu x Se y Te 1-y , the difference is small, and as a result, an operating temperature is disadvantageously low. In case of forming a laser element with a lattice-matching type double hetero junction structure or lattice-matching type quantum well structure, it is necessary to make an energy gap of the cladding layer 1 larger than that of the active layer 2, to make its difference large and to form a laser element with joining materials which crystalline structures and lattice constants are substantially the same. In Pb 1-x Cd x S 1-y Se y or Pb 1-x Eu x Se y Te 1-y of a quaternary solid solution having a rock salt-type crystalline structure, materials having different energy gaps and substantially equal lattice constants can be obtained by controlling a composition x of Cd or Eu and a composition y of Se, respectively, so that a laser element can be formed by joining them. However, in case of actually manufacturing a laser element, a large solid solution amount of Pb cannot be expected from limitation such as a manufacturing condition and the like, and a quaternary solid solution is manufactured by a small amount of solid solution at present. Materials pulse oscillated at 200 K and 270 K as described above are understood that compositions x of Cd and Eu in the above-described quaternary solid solution are 0.05 and 0.018, respectively, and that a solid solution amount to Pb is small. Therefore, in case of using them as a beam cladding layer 1, energy gap difference between the cladding layer 1 and the active layer 2 is at most 0.18 (eV) at 300 K and 0.094 (eV) at 241 K, and a laser element having a high operating temperature could not be obtained. From physical review B, volume 26, no. 10, November 1982, pages 5617-5622, a solid solution semiconductor laser element material having the formular Ca 1-x Pb x S, wherein 0.1<x<0.25 is known. From Journal of Vacuum Science and Technology, part B, volume 4, no. 2, March/April 1986, pages 578-580, it is known that the alkaline earth elements (Mg, Ca, Sr, Ba) are a possible source of high-band gap alloys with PbTe. The demand for high-performance laser elements has recently been increased more and more, particularly the development of solid solution semiconductor laser element material operable in the vicinity of a room temperature is important. That is, in order to increase the operating temperature of a semiconductor laser, it is an urgent task to obtain a novel solid solution semiconductor having larger energy gap of the cladding layer than that of the active layer and sufficiently large different therebetween. The present invention is to obviate said shortcoming and to be made by taking the above into consideration. An object of the invention is to provide a laser element oscillating within a region of wavelength 0.2-8 µm, varying wavelength and being operable in the vicinity of a room temperature, particularly a solid solution semiconductor laser element material which can form a laser element having a lattice matching type double hetero junction structure or lattice matching type quantum well structure. The present inventors have studied variously and discovered that these problems can be solved by solid solving lead (Pb) into calcium (Ca). The characteristics of the present invention are as follows. According to the invention there is provided a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X, where 0<x<0.5 and X is at least one element selected from Se and Te, or where X = S and 0<x≤0,1 or 0,25≤x<0,5. Furthermore, according to the invention there is provided a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X, where, 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn. Furthermore, according to the invention there is provided a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z, where 0<x≤0.4 and 0<z≤1. Furthermore, according to the invention there is provided a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S, where, 0<x≤0.5 and 0<y<1. Furthermore, according to the invention there is provided a laser element, wherein a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X , where O<x<0.5 and X is at least one element selected from S, Se and Te; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X ,where 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z ,where 0<x≤0.4 and 0≤z≤1; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S, where 0<x≤0.5 and 0<y<1 is used as a cladding layer and/or active layer. Furthermore, according to the invention there is provided a double hetero junction laser element, wherein a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X, where 0<x<0.5 and X is at least one element selected from S, Se and Te; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X, where 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z , where 0<x≤0.4 and 0<z≤1; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S, where 0<x≤0.5 and 0<y<1 is used as a cladding layer and/or active layer. Furthermore, according to the invention there is provided a quantum well structure laser element, wherein a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X, where 0<x<0.5 and X is at least one element selected from S, Se and Te; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X, where 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z , where 0<x≤0.4 and 0<z≤1; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S, where 0<x≤0.5 and 0<y<1 is used as a cladding layer and/or active layer. For a better understanding of the invention, reference is made to the accompanying drawing, in which: Fig. 1(A) is a laser element having a lattice-matching type double hetero junction structure. Fig. 1(B) is a laser element having a lattIce-matching quantum well struture. Fig. 1(C) is a partly enlarged view of the element. Fig. 2 is a diagram showing the relation between compositions x and z of Ca 1-x Pb x S 1-z Se z and the energy gap at room temperature. Fig. 3 is a diagram showing the relation between compositions x and z of Ca 1-x Pb x S 1-z Se z and the lattice constant at room temperature. Fig. 4 is a diagram showing the relation between compositions x and y of Ca 1-x (Pb 1-y Mn y ) x S and the energy gap at room temperature. Fig. 5 is a diagram showing the relation between compositions x and y of Ca 1-x (Pb 1-y Mn y ) x S and the lattice constant at room temperature. A method of manufacturing a solid solution semiconductor according to the present invention is explained in detail. Each element is weighed at a desired composition ratio, and sealed in a suitable vessel, such as a quartz vessel, in vacuo or a suitable gas atmosphere. The vessel is inserted in a suitable heating furnace, such as an electric furnace, homogeneously heated and molten, and thereafter water quenched. The sample is ground for further homogenization, and thereafter again sealed in a suitable vessel, such as a quartz vessel, in vacuo or a suitable gas atmosphere, heated at a high temperature for suitable hours, and water quenched, thereby obtaining a homogeneous solid-solved material. The thus obtained material is formed into a single crystal by a single crystal manufacturing method, such as a Bridgeman method, vapor-phase method and the like. Then, the material is manufactured into a thin film having suitable thickness by using a thin film manufacturing device, such as an MBE method, Hot Wall method and the like. For the better understanding of the present invention, the present invention is explained by referring to the accompanying drawings. Fig. 2 shows the characteristic diagram of the relation between the energy gap in the room temperature and the composition of x and z of Ca 1-x Pb x S 1-z Se z and Fig. 3 shows the characteristic diagram of relation between composition of x and z of Ca 1-x Pb x S 1-z Se z and the lattice constants in the room temperature obtained by an X-ray powder diffraction method with respect to single crystals of Ca 1-x Pb x S 1-z Se z , and Figs. 4 and 5 show those with respect to crystals of Ca 1-x (Pb 1-y Mn y ) x S, respectively. Moreover, both the energy gap and the lattice constant are the value at room temperature. It is possible from these drawings to select a combination of materials which energy gaps are large so as to have large difference, and moreover lattice constants are equal. That is, a combination of materials as a charge carrier, a beam cladding layer and an active layer in a lattice-matching type double hetero junction structure laser element or a lattice matching type quantum well structure laser element. For example, Fig. 1 shows that, in case of a combination of Ca 0.98 Pb 0.02 Se and PbS, lattice constants become equal, and a large different of energy gaps such as 4.4 eV is obtained. Therefore, the present invention can manufacture a lattice matching type double hetero junction structure laser element or a lattice matching type quantum well structure laser element which oscillates within a region of wavelength 0.2-8 µm, can vary wavelength and can be operable at a temperature in the vicinity of a room temperature. Example 1 With respect to a solid solution semiconductor of Ca 1-x Pb x S 1-z Se z (x=0.02-0.04, z=0.2-0.8), raw materials of granular Ca, Pb, S and Se of 99.999% purity were weighed to be gross weight of 2g at a desired composition ratio. The raw materials were vacuum sealed in a quartz vessel of 8 mm in inner diameter and 40 mm in length under vacuum of 1×10 -6 Torr, and a synthetic reaction was preliminarily progressed with a weak oxygen-hydrogen flame. Thereafter, the vessel was inserted into an electric furnace heated to 1127 K, maintained for about 10 minutes, then increased a temperature to 1393 K at a rate of 50 K/hr, maintained at the same temperature for 3 hours, homogeneously molten, and water quenched. The thus obtained material was ground in a mortar, vacuum sealed in a clean vessel of 8 mm in inner diameter and 50 mm in length, and placed at one end. In order to prevent the temperature distribution from disturbance caused by the flow within a furnace, the vessel was further vacuum sealed in a big quartz vessel, and a double sealed structure is formed. This vessel was placed in a furnace (such as horizontal furnace) holding a sample temperature of about 1223 K and a temperature gradient of a temperature difference 4K from a crystal growth portion, left for several days to single crystallize, thereafter water-quenched to form a solid solution semiconductor laser element material. In table 1 are shown energy gaps and lattice constants of each of the thus obtained solid solution semiconductors. These values are well matched with energy gaps and lattice constants shown in Figs. 2 and 3. No. Composition Energy gap (eV) Lattice constant (Å) x z 3 0.02 0.2 5.20 5.697 7 0.04 0.2 5.10 5.699 9 0.02 0.5 5.05 5.692 13 0.02 0.8 4.91 5.689 17 0.04 0.8 4.81 5.681 Example 2 With respect to five kinds of a solid solution semiconductor of Ca 1-x (Pb 1-y Mn y ) x S (x=0.03-0.5, y=0.07-0.62), raw materials of granular Ca, Pb, Mn and S of 99.999% purity were weighed to be gross weight of 2 g at a desired composition ratio. A method of manufacturing a sample is the same as that of Example 1. Energy gaps and lattice constants of each of the thus obtained solid solution semiconductors are as shown in Table 2. These values are well matched with energy gaps and lattice constants shown in Figs. 4 and 5. No. Composition Energy gap (eV) Lattice constant (Å) x z 6 0.03 0.07 5.26 5.700 10 0.05 0.22 5.18 5.700 12 0.03 0.42 5.29 5.695 18 0.05 0.42 5.21 5.695 24 0.03 0.62 5.31 5.690 Table 3 shows various properties when typical solid solution semiconductor laser element materials obtained by the present invention are used for a laser element cladding layer and/or active layer. Lattice constants of the cladding layer and the active layer are well-matched, and their energy gap difference is large. That is, it is understood that the difference is remarkably improved as compared with a comparative example having the highest value of 0.18 (eV) obtained by the prior art. As shown in the above examples, tables and drawings, the solid solution semiconductor laser element material of the present invention is wide in solid solution range and large in energy gap so as to be suitable material for laser elements. That is, it is possible to manufacture a laser element having a high operating temperature and high luminous efficiency by using the material of the present invention as a cladding layer, and suitably selecting a solid solution semiconductor having a smaller energy gap than that of the cladding layer, a large difference thereof, substantially equal lattice constant and well-matching lattice alignment, such as PbS, PbSe, PbTe, PbS 1-z Se z and the like as an active layer, or by suitably selecting a solid solution semiconductor having a large energy gap, such as CaSe, CaS and the like as a cladding layer and suitably selecting the material of the present invention having a smaller energy gap than that of the cladding layer, a large difference thereof and well-matching lattice alignment as an active layer. Further, it is possible to manufacture a laser element having a high operating temperature and high luminous efficiency by suitably selecting the material of the present invention having a larger energy gap of the cladding layer than that of the active layer, a large difference thereof, and well-matching lattice alignment as both the cladding layer and the active layer. Therefore, the laser element of the present invention is suitable for not only a light source of a superhigh resolution spectroscope within a region of wavelength 0.2-8 µm or quartz glass fiber optical communication, but also a light source of optical communication with the use of a metal halide polar loss glass fiber having less optical loss now in development. Moreover, when lattices cannot align at an interface of the active layer and the cladding layer of the laser element, crystal defect such as dislocation is introduced into the active layer, luminous efficiency is lowered, and performance of the laser element is deteriorated, so that it is desirable that lattice constants of the cladding layer and the active layer are substantially equal and alignment is good. The reason why the general chemical formulae of the material of the present invention are limited to Ca 1-x Pb x X (where, 0<x<0.5, X: at least one element selected from S, Se and Te) and Ca 1-x (Pb 1-y Y y ) x X (where, 0<x≦0.5, 0<y<1, X: at least one element selected from S, Se and Te, Y: at least one element selected from Zn and Mn) is because if the material deviates from these composition ranges, the manufacture of a laser element becomes difficult, an operating temperature and luminous efficiency are lowered, and it is unsuitable as laser element material. However, if a solid solution semiconductor is obtained even though there is some deviation from the above stoichiometric composition, properties as a laser element material are not spoiled and the material belongs to the category of the present invention. Moreover, an element of Ca of the present material is remarkably effective for widening a solid solution range with Pb and enlarging energy gap, and elements of Zn, Mn, S, Se and Te are largely effective for controlling lattice constant of a solid solution semiconductor. The material of the present invention can easily form a laser element, particularly a lattice matching-type double hetero junction or lattice matching-type quantum well structure laser element which oscillates within a range of wavelength 0.2-8 µm, varies wavelength and is operable in the vicinity of a room temperature, so that it is suitable as material of a laser element having high luminous efficiency and high performance, and this laser element is further suitable as a light source of optical communication system, superhigh resolution spectroscope and other general instruments, and its applicable range is wide.

Claims: A solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X where 0<x<0.5 and X is at least one element selected from Se and Te, or where X = S and 0<x≤0,1 or 0,25≤x<0,5. A solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1 -yY y ) x X, where, 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn. A solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z where 0<x≤0.4 and 0<z≤1. A solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S where, 0<x≤0.5 and 0<y<1. A laser element, wherein a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X where 0<x<0.5 and X is at least one element selected from S, Se and Te; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X where 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z where 0<x≤0.4 and 0<z≤1; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S where 0<x≤0.5 and 0<y<1 is used as a cladding layer and/or active layer. A double hetero junction laser element, wherein a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X where 0<x<0.5 and X is at least one element selected from S, Se and Te; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X where 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z where 0<x≤0.4 and 0<z≤1; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S where 0<x≤0.5 and 0<y<1 is used as a cladding layer and/or active layer. A quantum well structure laser element, wherein a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x X where 0<x<0.5 and X is at least one element selected from S, Se and Te; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Y y ) x X where 0<x≤0.5, 0<y<1, X is at least one element selected from S, Se and Te and Y is at least one element selected from Zn and Mn; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x Pb x S 1-z Se z where 0<x≤0.4 and 0<z≤1; or a solid solution semiconductor laser element material having the general chemical formula Ca 1-x (Pb 1-y Mn y ) x S where 0<x≤0.5 and 0<y<1 is used as a cladding layer and/or active layer.

Inventors: ABE SEISHI, MATSUMOTO KATASHI, MOCHIZUKI KATSUMI, ABE, SEISHI, MATSUMOTO, KATASHI, MOCHIZUKI, KATSUMI
Applicants: ELECT & MAGN ALLOYS RES INST, THE FOUNDATION: THE RESEARCH INSTITUTE OF ELECTRIC AND MAGNETIC ALLOYS
Application year: 1993
Main classification: H01S3
IPC codes: H01L33, H01S5, H01L21