Polydimethylsiloxanes for modulus reduction and method for their preparation

Abstract: A polydimethylsiloxane which has both low reactivity endgroups and high reactivity endgroups. These polydimethylsiloxanes are useful for making sealants with reduced modulus. An example of these polydimethylsiloxanes is one having low reactivity endgroups of the formula XR₂SiO-, where X is methoxy or methylethylketoximo and R is methyl or vinyl, and high reactivity endgroups having a formula Y b R (3-b) SiO-, in which b is 2 or 3, R is methyl radical and each Y is a hydrolyzable group selected from the group consisting of a ketoximo group and methoxy.

Description: This invention relates to polydimethylsiloxanes which can be used to reduce the modulus of siloxane sealants. Many methods have been proposed for the reduction of the modulus of siloxane sealants. One method of making the polydimethylsiloxanes to reduce or regulate the modulus of siloxane sealants is illustrated by the method described by Dupree in U.S. Patent No. 3,274,145, issued September 20, 1966. Kamis et al in U.S. Patent No. 4,898,910, issued February 6, 1990, teach another method for reducing the modulus of siloxane sealants and show polydimethylsiloxanes which have both vinyl endblocking and alkoxysilethylene endblocking. WO 81/02895 also discloses vulcanizable silicone rubber compositions having a low modulus which comprise a silanol end-stopped diorganopolysiloxane, a di-functional acetamide coupler and as the cross-linker a ketoxime functional silane or an aminoxy functional silane. Our invention relates to a polydimethylsiloxane comprising a polydimethylsiloxane having low reactivity endgroups having a formula X'R 2 SiO- where X' is methoxy or methylethylketoximo, and R is methyl or vinyl and high reactivity endgroups having a formula Y b Me (3-b) SiO- in which b is 2 or 3, Me is methyl radical, and each Y is a hydrolyzable group selected from methoxy and methylethylketoximo. This invention relates to a method of making polydimethylsiloxanes having both low reactivity endgroups and high reactivity endgroups comprising, under conditions to exclude moisture from contacting ingredients, mixing a hydroxyl endblocked polydimethylsiloxane with hydrolyzable silane of the formula Me (4-c) SiY c in which c is 3 or 4, each Y is a hydrolyzable group selected from methoxy and a ketoximo group, preferably methylethylketoximo, and Me is methyl radical, and thereafter adding a hydrolyzable silane of the formula R 2 SiX 2 in which X is N-methylacetamido, and R is methyl or vinyl radical. The polydimethylsiloxane of this invention comprises a mixture of different molecular species. Their viscosity is preferably from 3 to 400 Pa·s (Pascal-seconds). The polydimethylsiloxane is preferably a mixture of molecular species which together has >0% to ≤30% of the endgroups being low reactivity and ≥70% to <100% of the endgroups being high reactivity. In this mixture, some molecules can have both endgroups as either low reactivity or high reactivity, and some molecules can have one endgroup low reactivity and the other endgroup high reactivity, but the average of the mixture will fall in the range as stated above. These mixtures of polydimethylsiloxanes can be made prior to combining with the other ingredients or they can be made in situ. The most preferred polydimethylsiloxane are those which have from 5% to 20% of the endgroups being low reactivity and from 80% to 95% of the endgroups being high reactivity. These preferred polydimethylsiloxanes provide a low modulus sealant which is desirable for sealant joints in building constructions. The polydimethylsiloxanes can be made by reacting polydimethylsiloxane which has hydroxyl groups at both ends with a silane having at least three hydrolyzable groups per molecule and has the formula Formula A Me (4-c) SiY c in which c is 3 or 4, preferably c is 3, Y is ketoximo and methoxy, and Me is methyl. The amount of silane of Formula A is that amount sufficient to react with less than the hydroxyl groups of the polydimethylsiloxane. For highly reactive silanes, this amount can be less than one silane molecule per hydroxyl group of the polydimethylsiloxane. For silanes having lower reactivity, the amount of silane of Formula A may be more than one silane molecule per hydroxyl group of the polydimethylsiloxane. In the later case, the silane of Formula B can be added before the silane of Formula A completely reacts with the hydroxyl groups of the polydimethylsiloxane. After the silane of Formula A reacts with the hydroxyl of the polydimethylsiloxane, a silane having two hydrolyzable groups per molecule is added. These silanes preferably have a fast reaction time with the hydroxyl of the polydimethylsiloxane. The silanes with two hydrolyzable groups per molecule have a formula Formula B R 2 SiX 2 in which R and X are defined above. Such silanes can be illustrated by methylvinylbis(N-methylacetamido)silane, dimethyldimethoxysilane, and dimethylbis(ethylmethylketoximo)silane. The amount of silane of Formula A and the amount of silane of Formula B used can be varied to obtain a desired modulus. Decreasing the amount of the silane of Formula A and increasing the amount of the silane of Formula B decreases the modulus of the resulting cured elastomeric polyorganosiloxane, i.e. the sealant. Some silanes readily react with the silicon-bonded hydroxyl group (siloxanol) of the polydimethylsiloxane at room temperature without a catalyst whereas others may require either heating, the presence of a catalyst for the reaction or both. Those silanes which readily react with the siloxanols without a catalyst are preferably used to make the polydimethylsiloxane by this method. A preferred method of making polydimethylsiloxanes is to mix hydroxyl endblocked polydimethylsiloxane with hydrolyzable silane (B) of the formula R (4-c) SiY c in which c is 3 or 4, some Y are ketoximo groups and some Y are methoxy groups, and R is methyl radical, and thereafter add a hydrolyzable silane of the formula R 2 SiX 2 in which X is N-methylacetamido, and R is methyl or vinyl radical. These mixtures can react merely by mixing at room temperature in an environment which protects them from contacting moisture and produce polydimethylsiloxanes of (A) in which the low reactivity endgroups have a formula X'R 2 SiO- where X' is methoxy or methylethylketoximo and R is methyl or vinyl. The high reactivity endgroups have a formula Y b R (3-b) SiO- in which b is 2 or 3, R is methyl radical, and some Y are ketoximo groups and some Y are methoxy groups. The polydimethylsiloxanes of this invention have both low reactivity endgroups and high reactivity endgroups. The ratio of low reactivity endgroups to high reactivity endgroups has a direct influence on the modulus of a sealant prepared using the polydimethylsiloxane. Other factors being equal, increasing the concentration of low reactivity endgroups in the polydimethylsiloxane used to make a sealant, decreases the modulus of the cured sealant. The polydimethylsiloxane of this invention provides less unreacted siloxane species in the sealant composition while providing a low modulus sealant. Some preferred polyorganosiloxane elastomeric sealants using the polydimethylsiloxanes of this invention include those which have a siloxaphobic surface layer at the interface between air and the cured sealant. A siloxaphobic surface layer is both siloxaphobic and hydrophilic and is a relatively thin layer at the air-sealant interface which hinders the migration of siloxane species which are unreacted into the cured sealant matrix and migrate out of the sealant matrix to the air-sealant interface. The siloxaphobic surface layer does not readily allow siloxanes to penetrate out of the sealant matrix onto the sealant surface and onto adjacent substrates, such as building materials. A siloxaphobic surface layer also hinders the formation of dirt build-up or staining of the surface of the cured sealant. Additionally, a siloxaphobic surface layer can be one to which paint will adhere. Such sealants are obtained by curing room temperature vulcanizable polyorganosiloxane compositions which produce a siloxaphobic surface layer. A fluorocarbon compound which contains at least one perfluoralkyl group having at least six carbon atoms and a drying oil in a room temperature vulcanizable polyorganosiloxane composition produces, when the composition is cured, a siloxaphobic surface layer at the air-sealant interface which comprises the fluorocarbon compound and a drying oil oxidation product. The drying oil oxidation product enhances the siloxaphobic properties of the siloxaphobic surface layer and also provides a surface which can be painted with either oil based paints or latex based paints. The preferred fluorocarbon compounds are fluorocarbon alcohols or fluorocarbon alcohol derivatives. The drying oils can be an ester compound derived from unsaturated fatty acids having at least ten carbon atoms and alcohols. The unsaturated fatty acids include oleic, linoleic, linolenic, eleostearic, licanic, ricinoleic, and arachidonic acids. The ester compounds include mixtures which preferably contain at least 80 weight percent of the ester compounds made from unsaturated fatty acids having at least 10 carbon atoms. Many of the unsaturated fatty acid esters can be found in natural drying oils obtained from plant and animal sources, such as illustrated by linseed oil, tung oil, soybean oil, caster oil, fish oil, hempseed oil, cottonseed oil, oiticica oil, and rapeseed oil. The drying oil oxidation product is the material obtained when a drying oil reacts (polymerizes) through reaction with oxygen, such as air. A preferred polyorganosiloxane elastomeric sealant is one in which the siloxaphobic surface layer comprises a fluorocarbon alcohol and the drying oil oxidation product is tung oil oxidation product. Polyorganosiloxane elastomeric sealants which have, after 7 days exposure to an air atmosphere of 50% relative humidity at 25°C. an elongation at break of greater than 500%, a tensile strength at break of greater than 600 kPa (kilo-Pascals), and a modulus at 100% elongation of less than 800 kPa where these values are measured by ASTM D-412 procedure are preferred. These sealants also have less than 15% extractable materials using the procedure of ASTM D 3971-69 in which toluene was used as the solvent, the time period was 24 hours, and the sealant was cut into pieces of 3.175 mm (millimeters) by 3.175 mm by 2.54 mm. Polyorganosiloxane elastomeric sealant compositions which cure to give sealants with these properties and the siloxaphobic surface layer are preferred. They provide the unique long term clean sealant surface and equally long term clean substrates adjacent to the cured sealant. At the same time, they maintain these properties making them advantageous to form seals where expansions and contractions occur from heating and cooling of substrates, such as in buildings. The elastomeric polydimethylsiloxane compositions can be packaged in one or two packages. Such packaging is well known in the art. It is believed that the siloxaphobic surface layer is a closely packed surface layer at the air-sealant interface and this layer has a significantly low dispersive force contributing to the surface energy and the unreacted silicone species do not easily migrate through or across this surface layer. The siloxaphobic surface layers have surface energies which have a dispersive force component and a polar force component where the dispersive force component is less than or equal to 15x10 -5 N/cm 2 (15 dynes/cm 2 ) and the polar force component is greater than 0 N/cm 2 (0 dynes/cm 2 ). The siloxaphobic surface layer forms at the air-sealant interface and does not appear to form at the substrate-sealant interface, such as the interface between the sealant and substrates such as glass, aluminum and concrete. The siloxaphobic surface interface is thus unique in that the adhesion of the sealant to the substrate is not substantially changed. The polyorganosiloxane compositions which cure to elastomers at room temperature when exposed to moisture, but remain uncured when protected from moisture are made from the polydimethylsiloxanes having both low reactivity endgroups and high reactivity endgroups, a hydrolyzable silane, a siloxaphobic agent which is a fluorocarbon alcohol or which is a mixture of a fluorocarbon alcohol and a reaction product of the fluorocarbon alcohol and the hydrolyzable silane, and a filler. The hydrolyzable silanes have the formula R* (4-c) SiY * / c in which R* is a monovalent hydrocarbon radical, Y* is a hydrolyzable group containing at least one carbon atom, and c has an average value of from 2 to 4. These hydrolyzable silanes preferably have 3 or 4 Y* groups. Y* can be ketoximo, alkoxy, acyloxy, alkenyloxy, and amido. Ketoximo can be -O-N=X" where X" is R"2= or in which R" is an alkyl of 1 to 5 carbon atoms, phenyl or vinyl, R‴ is a divalent hydrocarbon radical. Examples of hydrolyzable silanes in which Y* is a ketoximo include MeSi(O-N=CMeEt) 3 , ViSi(O-N=CMeEt) 3 , Si(O-N=CMeEt) 4 and PhSi(O-N=CMeEt) 3 . These and other ketoximo silanes can be found in U.S. Patent No. 3,184,427, issued May 18, 1965, to Russell et al; and U.S. Patent No. 3,189,576, issued June 15, 1965, to Sweet. The ketoximosilanes are preferred because of their neutral properties, reactivity, and cured properties. Y* can be alkoxy as illustrated by methoxy, ethoxy, propoxy, isopropoxy, and methoxyethoxy. Examples of hydrolyzable silanes in which Y* is alkoxy include methyltrimethoxysilane, vinyltrimethoxysilane, phenyltrimethoxysilane, vinyltriethoxysilane, tetraethyl orthosilicate, tetramethyl orthosilicate, ethyltrimethoxysilane, propyltrimethoxysilane, methyltriethoxysilane, phenyltriethoxysilane, butyltripropoxysilane, pentyltriisopropoxysilane, methyldimethoxyethoxysilane, and methyldiethoxymethoxysilane. Y* can be acyloxy as illustrated by acetoxy and octanoyloxy. Examples of hydrolyzable silanes in which Y* is acyloxy include methyltriacetoxysilane, ethyltriacetoxysilane, vinyltriacetoxysilane, methyltrioctanoyloxysilane, propyltriacetoxysilane, phenyltriacetoxysilane, and ethyltrioctanoyloxysilane. Y* can be alkenoxy as illustrated by propenoxy, isopropenoxy and butenoxy. Examples of hydrolyzable silanes in which Y* is alkenoxy include methyltripropenoxysilane, ethyltripropenoxysilane and vinyltripropenoxysilane. Y* can be amido as illustrated by N-methylacetamido, N-ethylpropionamido, N-ethylbenzamido, N-phenylacetamido and N-propylpropionamido. Examples of hydrolyzable silanes in which Y* is amido include methyltri(N-methylacetamido)silane and vinyltri(N-methylacetamido)silane. The amido silanes are shown by Toporcer et al in U.S. Patent No. 3,776,933, issued December 4, 1973. The hydrolyzable silanes can be those in which the Y* groups are different in the same silane. For example, silanes (B) can be those in which some Y* are ketoximo and some Y* are alkoxy. Such silanes are described by Klosowski et al in U.S. Patent No. 4,657,967, issued April 14, 1987, and by Haugsby et al in U.S. Patent No. 4,973,623, issued November 27, 1990, which show silanes which contain both ethoxy-ketoximo silanes and methods of their preparation. The amount of hydrolyzable silane is that amount necessary to crosslink the polydimethylsiloxane and to protect the elastomeric polydimethylsiloxane composition from the ingress of moisture when packaged in a container. This amount is preferably at least one molecule of silane per siloxanol. Such amounts are usually from 1 to 10 weight percent silane based on the weight of the composition. The siloxaphobic agent is one of the materials which provides the siloxaphobic surface layer of the cured elastomeric polyorganosiloxane composition. This siloxaphobic agent is a fluorocarbon alcohol, a reaction product of a fluorocarbon alcohol and a hydrolyzable silane, or a mixture of the fluorocarbon alcohol and the reaction product of the fluorocarbon alcohol and the hydrolyzable silane. The fluorocarbon alcohol contains at least one fluorocarbon group of the formula C x F( 2x+1 )- group where x has an average value of at least 6. Fluorocarbon alcohols which have fluorocarbon groups where x was less than 6 did not prevent the migration of siloxane species to the surface of the sealant. Preferably, the fluorocarbon alcohols are those with fluorocarbon groups in which x has an average value of from 6 to 20. The fluorocarbon alcohols are commercially available and are illustrated by the following formulae where g has a value of from 6 to 20. Commercial mixtures are sold in which g has an average of 7.5 and contain species in which g ranges from 4 to 8 inclusive. Such a mixture is FC-10 which is sold by Minnesota Mining and Manufacturing Company (3M), Minneapolis, Minnesota. Other commercial mixtures sold by 3M are FC-170C which is a fluorocarbon alcohol and has the following average formula and FC-171 which is a fluorocarbon alcohol and has the following average formula Other commercially available fluorocarbon alcohols include C x F (2x+1) CH 2 CH 2 OH, and C x F (2x+1) CH 2 CH 2 O(CH 2 CH 2 O) f H where x is from 4 to 20 and f is a positive integer. The siloxaphobic agent is preferably a reaction product of a fluorocarbon alcohol and a hydrolyzable silane. These siloxaphobic agents are siloxaphobic reaction product mixtures which are made by mixing at least 0.01 mole of the fluorocarbon alcohol with one mole of the hydrolyzable silane under conditions which exclude moisture from contacting the ingredients, preferably 0.1 mole of fluorocarbon alcohol per one mole of hydrolyzable silane. Fluorocarbon alcohols can be used by themselves but some are solid at room temperature and handling and mixing with the other ingredients is not fully acceptable. The resulting mixture is heated until some of the fluorocarbon alcohol reacts with the hydrolyzable silane and forms a C-O-Si bond. The resulting reaction mixture is unreacted hydrolyzable silane, unreacted fluorocarbon alcohol, and a reaction product of fluorocarbon alcohol and the hydrolyzable silane in which at least one Y group is replaced by the fluorocarbon alcohol, as illustrated by the following equation The siloxaphobic reaction product mixtures contain from >0% to 100% reaction product of fluorocarbon alcohol and silane. These reaction product mixtures provide the preferred siloxaphobic agents, especially when the reaction product of the fluorocarbon alcohol and silane is <50% of the siloxaphobic reaction mixture. A preferred siloxaphobic reaction mixture is one in which the fluorocarbon alcohol has the following formula wherein x has an average value of at least 6, the hydrolyzable silane has the formula and the reaction product of the fluorocarbon alcohol and the hydrolyzable silane comprises a compound of the formula wherein x has an average value of at least 6. The siloxaphobic reaction mixture is preferred because the siloxaphobic surface layer is rapidly formed during the curing of the elastomeric polyorganosiloxane composition and the surface resists the accumulation of dirt and/or stain when the sealant is very vulnerable to dirt pick-up. The siloxaphobic reaction mixture through some unknown mechanism more readily forms the siloxaphobic surface layer than the use of unreacted fluorocarbon alcohol, i.e. the fluorocarbon alcohol is merely mixed with the other elastomeric polydimethylsiloxane composition ingredients. The siloxaphobic surface layer is regenerated over the useful life of the sealant. The siloxaphobic reaction mixture acts as a reservoir and continually renews the siloxaphobic surface layer as it becomes depleted with age. The siloxaphobic surface layer also provides a sealant which exhibits retardation of color formation of the sealant surface and the surrounding areas adjacent to the sealant which may be the result of exposure to weather. The siloxaphobic surface layer keeps the properties of the sealant from changing with age because siloxane ingredients are not readily lost by migration or evaporation, but are maintained within the sealant matrix. The siloxaphobic reaction mixture does not adversely effect the curing properties of the elastomeric polydimethylsiloxane composition, and the adhesion to various substrates, particularly those used in building construction, does not appear to be altered by addition of the siloxaphobic reaction mixture to the composition. The siloxaphobic reaction mixture can be used in small amounts and yet provide its useful properties over long periods of time. The amounts are such that the fluorocarbon group is present in the composition in amounts of from 0.1 to 7 inclusive weight percent based on the weight of the composition, preferably from 1 to 3 weight percent. The polydimethylsiloxane compositions which cures to elastomers can also contain a filler. These fillers can be those generally used in formulating silicone sealants, and include both reinforcing fillers such as fumed silica, hydrophobicized fumed silica, hydrophobicized precipitated silica, and carbon black and non-reinforcing fillers such as calcium carbonate, stearic acid treated calcium carbonate, precipitated calcium carbonate, finely pulverized quartz, diatomaceous earth, titanium dioxide, alumina, iron oxide, magnesium oxide, and zinc oxide. The calcium carbonate fillers are preferred because they appear to act as a reservoir for the fluorocarbon alcohol, which extend the useful life of the siloxaphobic agent. The polydimethylsiloxane compositions which cure to elastomers and have a siloxaphobic agent present have enhanced siloxaphobic properties by the addition of at least 0.5 weight percent of a drying oil based on the weight of the composition. These drying oils are described above and increase the siloxaphobic characteristics of the cured sealant. They also provide a surface which is paintable with both oil based paints and latex paints wherein paints are materials used to enhance the aesthetics of a substrate as well as protect it from the environment and are pigmented to various colors. The drying oil which is preferred is tung oil. When a drying oil, such as tung oil, is used it may be added just before use or it may be mixed with the other ingredients into what is known as a one package sealant. In the latter case, it is required that the package be an airless package because drying oils react with atmospheric oxygen and therefore, compositions which contain a drying oil need to be protected from air until it is desirable to cure them. Some drying oils may require the use of accelerators to achieve their properties. Accelerators can be used as long as they do not interfere with the other properties of the sealant, its storage, its cure, or its manufacture. These accelerators are known in the paint art as driers. Also, the use of photoinitiators with the drying oils may be useful in these compositions. The polydimethylsiloxane compositions which cure to elastomers may find a catalyst for curing useful to develop the sealant properties within an acceptable period of time. With some hydrolyzable silanes of catalysts are generally required. For example, alkoxysilanes require a catalyst for cure in satisfactory time periods and such catalyst can include tin catalysts such as dibutyltin dicarboxylates such as dibutyltin dilaurate, dibutyltin diacetate, dibutyltin dioctoate, stannous octoate, and stannous 2-ethylhexoate; and titanium catalyst such as tetrabutyltitanate. tetraisopropyltitanate, bis-(acetylacetonyl)diisopropyltitanate, and 2,5-diisopropoxy-bis-ethylacetoacetate titanium. These catalysts are well known in the art of silicone sealants. Compositions which are made by using ketoximosilanes for the hydrolyzable silane preferably contain a mixture of tin catalyst and titanium catalyst. The preferred catalysts are dibutyltin dilaurate and 2,5-diisopropoxy-bis-ethylacetoacetate titanium. The preferred amounts are from 0.05 to 0.2 part by weight of the tin catalyst based on 100 parts by weight of polydimethylsiloxane and 0.1 to 2 parts by weight of the titanium catalyst based on 100 parts by weight of polydimethylsiloxane. The polydimethylsiloxane compositions which cure to elastomers preferably contain a silane adhesion promoter. The breadth of substrates to which the sealants can be adhered can be increased as well as the consistency of the adhesion can be maintained by the addition of a silane adhesion promoter. The silanes which act as adhesion promoters are preferably aminoorganotrialkoxysilanes and glycidoxyorganotrialkoxysilane. Aminoorganotrialkoxysilanes are illustrated by gamma-aminopropyltriethoxysilane and N-beta-aminoethyl-gamma-aminopropyltrimethoxysilane. Glycidoxyorganotrialkoxysilanes are illustrated by gamma-(glycidoxy)propyltrimethoxysilane. In addition to providing adhesion to substrates, these silanes also increase the cure rate of the sealant, especially elastomeric polydimethylsiloxane compositions which contain as ingredient (B) ketoximosilanes. The amounts of such silane adhesion promoters is small, usually less than one weight percent of the composition, preferably less than 0.5 weight percent. The preferred silane adhesion promoters are mixtures of aminoorganotrialkoxysilane and glycidoxyorganotrialkoxysilane. The preferred polydimethylsiloxane compositions which cure to elastomers contain a non-reinforcing thixotropic agent which can be illustrated by a polymer of 2,5-furandione with 1,3-butadiene. These non-reinforcing thixotropic agents increase the oleophobic character of the sealant and enhances the siloxaphobic surface layer properties of the sealant. Thixotropy is best enhanced when the non-reinforcing thixotropic agents are used with compositions containing calcium carbonate. The following examples are for illustrative purposes and should not be construed as limiting the invention which is properly delineated in the claims. In the following examples, viscosities are at 25°C., "part" or "parts" are by weight, Me represent methyl radical, Vi represents vinyl radical. A siloxaphobic reaction mixture was prepared by mixing in a closed vessel, 29 parts of a fluorocarbon alcohol, FC-10 manufactured by 3M, which has the average formula where g has an average value of 7.5 and contains species having g values of 4, 5, 6, 7, and 8, and 71 parts of a ketoximosilane mixture which was approximately 70 weight percent methyltri(methylethylketoximo)silane, 24 weight percent methyldi(methylethylketoximo)methoxysilane, 0.5 weight percent methyldimethoxy(methylethylketoximo)silane, and 5.5 weight percent impurities. The resulting mixture was heated at 50°C for 30 minutes under a nitrogen purge. The resulting siloxaphobic reaction mixture was 19.7 weight percent unreacted fluorocarbon alcohol, 59.9 weight percent unreacted ketoximosilane, and 12.3 weight percent reaction product of the formula and 8.1 weight percent impurities. This siloxaphobic reaction mixture was used as obtained and for these examples is designated Siloxaphobic Agent A. Siloxaphobic Agent B was made in the same manner as Siloxaphobic Agent A, except 33 parts of FC-10 and 67 parts of the ketoximosilane mixture were used and a nitrogen purge was not used. Siloxaphobic Agent C was made in the same manner as Siloxaphobic Agent A, except 23 parts of FC-10 and 77 parts of the ketoximosilane mixture were used and a nitrogen purge was not used. Siloxaphobic Agent D was made in the same manner as Siloxaphobic Agent A, except 45.5 parts of FC-10 and 54.5 parts of the ketoximosilane mixture were used and a nitrogen purge was not used. EXAMPLE 1 Polydimethylsiloxane compositions which were cured to elastomers were prepared by using the following ingredients: Polymer A = a hydroxyl endblocked polydimethylsiloxane having a viscosity of 50 Pa·s. Polymer B = a hydroxyl endblocked polydimethylsiloxane having a viscosity of 200 Pa·s. Polymer C = a hydroxyl endblocked polydimethylsiloxane having a viscosity of 4 Pa·s. Silane A = a ketoximosilane mixture of approximately 70 weight percent methyltri(methylethylketoximo)silane, 24 weight percent methyldi(methylethylketoximo)methoxysilane, 0.5 weight percent methyldimethoxy(methylethylketoximo)silane, and 5.5 weight percent impurities. Silane B = methylvinyldi(N-methylacetamido)silane. Filler A = stearic acid treated precipitated calcium carbonate. Filler B = stearic acid treated ground calcium carbonate. Thixotropic Agent = a polymer of 2,5-furandione with 1,3-butadiene. Adhesion Promoter A = gamma-aminopropyltriethoxysilane. Adhesion Promoter B = gamma-(glycidoxy)propyltrimethoxysilane. Adhesion Promoter C = N-beta-aminoethyl-gamma-aminopropyltrimethoxysilane. Catalyst A = dibutyltin dilaurate. Catalyst B = diisopropoxy-bis-(ethylacetoacetate) titanium. Polydimethylsiloxane compositions which cured to elastomers of Formulations 1-8 were prepared by mixing Polymer A, Polymer B, and Polymer C with Silane A in the amounts as shown in Table I, which also shows the amounts of the other ingredients used to make the compositions. To the resulting mixture, Siloxaphobic Agent B, C, or D, Filler A, Filler B, Thixotropic Agent, Adhesion Promoter A, Adhesion Promoter B, Catalyst A, and Catalyst B were in the amounts as shown in Table 1. The polydimethylsiloxane compositions which cured to elastomers of Formulations 9-14 were prepared by mixing Polymer A, Polymer B, and Polymer C with Silane A in the amounts shown in Table 2. After the polymer was mixed with Silane A, Silane B was added to provide a polydimethylsiloxane which had both low reactivity endgroups of the formula where X is either methoxy or methylethylketoximo, and high reactivity endgroups of the formula Y 2 MeSiO- in which some Y are methylethylketoximo groups and some Y are methoxy groups. The reaction of Silane B with the unreacted hydroxyl groups of Polymer A, Polymer B, and Polymer C was very fast and was essentially complete after mixing. The remaining ingredients and their amounts were as shown in Table 2. The resulting polydimethylsiloxane compositions (sealant composition) of Formulations 1-14 were prepared under conditions which protected against the ingress of moisture and were stored in packages which protected them from moisture. The staining and dirt pick-up property was evaluated by placing a horizontal bead of about 1.9 cm width and 0.6 cm depth across the top of a panel having a polished ceramic surface with mortar backing (Glassweld panel). The panels were then set outside at a 45 degree angle facing south for four months. After the outside exposure of four months and six months, the panels were evaluated for sealant surface dirt pick-up and staining was evaluated after four months and and given the following rating: 1 = as clean as a panel without a sealant bead; 2 = no streaks, panel and sealant are mainly clean, but not as clean as a panel without a sealant bead; 3 = slight streaks, panel looks slightly hazy from staining, very little dirt pick-up on sealant which cannot be seen from more than 1.5 meters away; 4 = moderate streaks, panel is hazy overall, some dirt pick-up on sealant that is visible at 1.5 meters away; and 5 = heavy/dark streaks, panel has heavy film covering it, and the sealant has turned dark from dirt. The results of the stain and dirt pick-up test were as shown in Table 3. The 100% elongation modulus after allowing the sealant to cure for seven days at room temperature. The modulus was determined by ASTM D-412 and the results are shown in kPa. The percent extractables, after curing for seven days at room temperature, was determined in accordance with ASTM D-3971-69 procedure using toluene as the solvent, a time period of 24 hours, and the cured sealant pieces were 3.175 mm by 3.175 mm by 2.54 mm. The contact angle using trimethylsilyl endblocked polydimethylsiloxane having a viscosity of 0.1 Pa·s was determined and the results were as shown in Table 3. The contact angle determination was done in the same manner as would be used for determining the contact angle of water, except that trimethylsilyl endblocked polydimethylsiloxane was used in place of the water. The surface energy was determined by water contact angle and methylene iodide contact angle for obtaining the dispersive force component and the polar force component using the equation of Owen et al in the Journal of Applied Polymer Science, 1969, vol. 13, beginning at page 1741. EXAMPLE 2 Polydimethylsiloxane compositions which cured to elastomers of Formulations 17, 18, and 19 were prepared as described in Example 1 for Formulations 9-14 using the ingredients as identified in Table 4. Instead of using FC-10, the Siloxaphobic Agent A was used with the amounts shown in Table 4. In Formulations 18 and 19, titanium dioxide pigment was used, and in Formulation 19, tung oil was used. For Formulations 18 and 19, Polymer A by reaction with Silane A and Silane B resulted in a polydimethylsiloxane with low reactivity endgroups and high reactivity endgroups as described in Example 1 for Formulations 9-14. The results of staining and dirt pick-up, 100% modulus after curing at room temperature for 7 days, and the contact angle as described in Example 1 were determined and were as shown in Table 4, except the panels used for exposure to outside atmospheric conditions were reflective glass panels and the sealant beads were applied in a square root shape of 5 cm width and 0.6 cm depth across the top of the panel. The panels were placed in an industrial environment. Ingredients Formulation, In Parts 17 18 19 Polymer A 100 100 100 Silane A 2 1 1 Silane B 2 1 1 Siloxaphobic Agent A 9 10 10 Filler A 40 60 60 Filler B 50 0 0 Thixotropic Agent 0.5 0.5 0.5 Adhesion Promoter A 0.3 0 0 Adhesion Promoter B 0.7 0.1 0.1 Adhesion Promoter C 0 0.3 0.3 Catalyst A 0.16 0.07 0.07 Catalyst B 0.5 1 1 TiO 2 Pigment 0 9 9 Tung Oil 0 1 0 Staining and Dirt Pick-up After: 3 Months 1-2 1 1-2 6 Months 2 --- --- 100% Modulus (kPa) 165 228 255 200 Fluid Contact Angle 28 37 31 Dispersive Force, dynes/cm 2 12.6 9.9 14.3 Polar Force, N/cm 2 (dynes/cm 2 ) 15.3x10 -5 (15.3) 12.7x10 -5 (12.7) 5.9x10 -5 (5.9) Formulation 17 was cured for 7 days at room temperature and also cured for 7 weeks at 50°C. The tensile strength at break, the elongation at break, and the 100% modulus were measured by ASTM D-412. The durometer on the Shore A scale was measured in accordance with ASTM C-661 procedure. The percent extractables was determined in accordance with ASTM D-3971-69 procedure using toluene as the solvent, a time period of 24 hours, and the cured sealant pieces were 3.175 mm by 3.175 mm by 2.54 mm. The results observed were as follows: After Room Temperature Cure After Cure at 50°C. Tensile Strength at break, kPa 1379 1255 Elongation at break, % 915 522 100% Modulus, kPa 165 365 Durometer, Shore A 14 28 Extractables, % 6.7 --- The contact angle and the surface energies were measured after 3 months exposure and after 6 months exposure. The contact angle as determined in Example 1 was 28 degrees after both exposures. The dispersive force component of the surface energy was 13.1x10 -5 N/cm 2 (13.1 dynes/cm 2 ) after 3 months exposure and 12.6x10 -5 N/cm 2 (12.6 dynes/cm 2 ) after 6 months exposure. These low dispersive force components showed that the sealant surface repulsed both siloxane fluid and soot, and that free siloxane materials were not able to migrate out of the sealant onto the sealant surface. The polar force component of the surface energy was 18.5x10 -5 N/cm 2 (18.5 dynes/cm 2 ) after 3 months exposure and 14.7x10 -5 N/cm 2 (14.7 dynes/cm 2 ) after 6 months exposure. The total surface energies were 31.5x10 -5 N/cm 2 (31.5 dynes/cm 2 ) after 3 months exposure and 27.3x10 -5 N/cm 2 (27.3 dynes/cm 2 ) after 6 months exposure. EXAMPLE 3 A polydimethylsiloxane composition which cured to elastomer was prepared as described in Example 1, except the ingredients and their amounts were: 100 parts of Polymer A, 1 part of Silane A, 1 part of Silane B, 10 parts of Siloxaphobic Agent A, 60 parts of Filler A, 0.5 part of Thixotropic Agent, 0.3 part of Adhesion Promoter A, 0.1 part of Adhesion Promoter B, 0.07 part of Catalyst A, and 1 part of Catalyst B. The resulting composition had an extrusion rate of 139 g/min and upon exposure had a skin over time of 170 minutes. The composition was allowed to cure for 7 days at room temperature exposed to the atmosphere, test pieces were made, and using ASTM D-412, the tensile strength at break was 1538 kPa, the elongation at break was 931%, the 100% modulus was 159 kPa, and the tear strength (Die B) was 5.6 kN/m (kilonewtons/meter). The durometer on the Shore A scale as determined by ASTM C-661 was 12 and the amount of extractables as determined in Example 2 was 6%. After allowing the composition to cure for 7 days at room temperature and then for one month at 50°C., the properties were: tensile strength at break = 2089 kPa, elongation at break = 788%, 100% modulus = 324 kPa, durometer on the Shore A scale = 25, the tear strength (Die B) = 5 kN/m, and the amount of extractable = 8%. Tung oil in the amount of one weight percent based on the weight of the composition was added to the above composition and thoroughly mixed. The resulting composition was allowed to cure at room temperature for two weeks after which a portion of the cured surface was painted with a deep blue latex paint and another portion was painted with a red oil based paint. After two days the oil based paint adhered to the cured sealant surface. The latex paint took 17 days to develop partial adhesion to the cured sealant surface and fully adhered after 43 days. The surface of cured sealant without the tung oil would not wet with latex paint and although the oil based paint spread evenly over the surface of the sealant without the tung oil, it did not adhere.

Claims: A method of making polydimethylsiloxanes having both low reactivity endgroups and high reactivity endgroups comprising, under conditions to exclude moisture from contacting ingredients, mixing a hydroxyl endblocked polydimethylsiloxane with hydrolyzable silane of the formula Me (4-c) SiY c in which c is 3 or 4, each Y is a hydrolyzable group selected from a ketoximo group and methoxy group, and Me is methyl radical, and thereafter adding a hydrolyzable silane of the formula R 2 SiX 2 in which X is N-methylactetamido, and R is methyl or vinyl radical. A polydimethylsiloxane preparable according to the method of claim 1 in which the polydimethylsiloxane has low reactivity endgroups having a formula X'R 2 SiO-, where X' is methoxy or methylethylketoximo and R is methyl or vinyl, and high reactivity endgroups having a formula Y b Me (3-b) SiO-, in which b is 2 or 3, Me is methyl radical, and each Y is a hydrolyzable group selected from a ketoximo group and methoxy.

Inventors: ALTES MICHAEL GENE, BERGMAN LOUISE CHRILLA, KLOSOWSKI JEROME MELVIN, O'NEIL VIRGINIA KAY, ALTES, MICHAEL GENE, BERGMAN, LOUISE CHRILLA, KLOSOWSKI, JEROME MELVIN, O'NEIL, VIRGINIA KAY
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1993
Main classification: C08G77
IPC codes: C07F7, C08G77, C08K5, C09K3