CATALYST AND PROCESS FOR A ZIEGLER POLYMERISATION

Abstract: The invention relates to a catalyst that is suitable for the preparation, via a Ziegler polymerisation, of an olefine polymer, comprising an organometallic compound and a transition metal-imidoaryl complex, characterised in that the complex contains at least one amido group bound to the transition metal, the aryl group in the complex being an o,o-disubstituted phenyl group.

Description: CATALYST AND PROCESS FOR A ZIEGLER POLYMERISATION The invention relates to a catalyst that is suitable for the preparation, via a Ziegler polymerisation, of an olefine polymer, comprising an organometaliic compound and a transition metal-imidoaryl complex. Such a catalyst is known from US-A-5,086,023, which describes a catalyst for the preparation of an ethylene-propylene-diene polymer, the transition metal being vanadium. The catalyst used therein contains a vanadium trichloride-imido-para-toluyl complex. A drawback of such a catalyst for use in a Ziegler polyme isation of an olefine is that the activity is low (approx. a factor of 3 lower relative to the catalyst according to the known relevant state of the art (as also appears from the results of such a catalyst presented in US-A-5,086,023) ) . According to the invention, with a new catalyst, to be described below, a substantially increased yield of polymer is obtained (relative to the amount of transition metal used) . The catalyst according to the invention is characterised in that the transition metal-imidoaryl complex contains at least one amido group bound to the transition metal, the aryl group in the complex being an o,o-disubstituted phenyl group. An amido group is here understood to be a group that is originating from an amine via separation of a hydrogen atom; in the context of the present invention the amido group is a nitrogen containing group, in which the nitrogen atom is formally single bonded to the transition metal. Surprisingly it has been found that because of the combination of an amido group bound to the transition metal and an imido, o,o-disubstituted phenyl group a unique catalyst is obtained which presents both a high activity and a good stability; i.e. not only is the initial activity high, the activity profile is also much more constant. The activity profile changes from a 'decay type' to 'active for a long time'. Because of the presence of such specific groups, which are not mentioned in the prior state of the art, a catalyst is obtained that shows catalytic behaviour that differs substantially from that of the transition-metal compounds that have commonly been used in Ziegler chemistry until now. This is apparent from for example different yields (per unit of transition metal), different polymer configurations and different incorporation percentages when more defines are used, so that it must be concluded that there is a different catalytic centre. The high activity described above is not obtained if, instead of the amido group, alkoxide or halogen groups are bound to the transition metal in the complex. The stability of the catalyst described above is not obtained if the aryl group of the imidoaryl complex is different from the group according to the invention, namely an o,o-disubstituted phenyl group. In particular this applies in the case of the use of the trichloro- vanadium-imido-para-toluyl complex as practised in the aforementioned US-A-5,086,023. More in particular the amido group in the complex has the formula -NR^, where R x and R 2 , independently of one another, are an alkyl group, an alkenyl group, an aryl group or a silicon-containing hydrocarbyl group, each containing generally from 1-20 C-atoms. Here and hereafter such a transition metal- imidoaryl complex is understood to be a group of compounds having the following general formula: R-N=M-X π Y m ( NR 1 R 2 ) p ( 1 ) where : R: stands for an o, o-disubstituted phenyl group; M: stands for a transition metal of groups 3-6; X: stands for a halogen group; Y: stands for an alkoxy group, an aryloxy group, an amide group or a silicon containing hydrocarbyl group or a different ligand group to be described below; R x and/or R 2 : stand for an alkyl group, an alkenyl group, an aryl group or a silicon-containing hydrocarbyl group; n: 0-2; (this being dependent on the valency of m: 0-2; the R-N=M group, i.e. n+m+p = valency of p: 1-3. M-2) (R-N=: stands for the imidoaryl ligand). The individual groups in the complex will be discussed below. The aryl group in the complex (R in formula 1) consists of an o, o-disubstituted phenyl group, which optionally may also be substituted at the meta- or para- position. The substituents present at the o(ortho-)- positions of the phenyl group are alkyl groups, whether or not substituted, having 1-20 C-atoms. Preferred are substituents having 1-8 C-atoms, such as methyl, ethyl, isopropyl and isobutyl. More preferably the ortho- substituent is a methyl or isopropyl group. Suitable substituents at the meta- and para-positions of the R group may be: alkyl, aralkyl , alkoxide, aryloxide, halogen, amino, nitro, thiol and carboxyl. Such and other substituents are known to a person skilled in the art and their suitability can be tested in a simple manner. The transition metal in the complex (M in formula 1) is chosen from groups 3-6 of the Periodic System of the Elements (using the new IUPAC list as shown on the inside page of the Handbook of Chemistry, 70th Edt., 1989-90). Preferably the transition metal is chosen from the group comprising Ti, Zr, V, Nb, Cr and Mo. More preferably the transition metal is Ti or V. For the preparation of amorphous copolymers it is most preferable to use V as the transition metal. The amido group in the catalyst and in particular the -N ^ group is at least singly present (p=l in the general formula 1), but several amido groups are also suitable. Both the Ε. group and the R 2 group in the amido group are, independently of one another, an alkyl group, an alkenyl group, an aryl group or a silicon- containing hydrocarbyl group, whether or not substituted, each containing 1-20 C-atoms. Preferably, an alkyl- or alkenyl group contains 1-8 C-atoms; an arylgroup preferably 6-15 C-atoms. Methyl, ethyl, propyl, isopropyl and higher homologues can for example be mentioned as the alkyl group. Vinyl, 1-propenyl, allyl and 1,3-butadienyl can for example be mentioned as the alkenyl group. Tolyl, phenyl and naphthalyl can for example be mentioned as the aryl group. Preferably use is made of a phenyl group. Trimethylsilyl, triethylsilyl, dimethylethylsilyl and analogous groups can be mentioned as the silicon- containing hydrocarbyl group. The alkyl, alkenyl, aryl or silicon-containing hydrocarbyl groups may also contain substituents such as an aryl or alkyl group, an alkoxide, aryloxide, halogen, amino, nitro, thiol or carboxyl group. Preferably R x and R 2 are an aryl group and more preferably R x and R 2 are a phenyl group. The amido group may also be a heterocyclic system, such as an imidazole group, a carbazole group or a piperidine group. One or two halogen atoms may also be bound to the transition metal (X in the general formula 1), in which case a choice can be made from the group comprising F, Cl, Br and I. Preferably the complex contains at least 1 halogen group, more preferably at least 1 chlorine group, which is bound to the transition metal (i.e. n > . 1). Mixtures of the aforementioned halogens are also suitable. In the above general formula 1, Y can be chosen from the group comprising alkoxide, aryloxide, amine, amide, an S or a P compound, a cyclopentadienyl or a silicon-containing hydrocarbyl group, mixtures being possible too. Transition metal-imidoaryl complexes, notably in the form of vanadium-imidoaryl complexes, are known as such; the reader can be referred to the publication by D.D. Devore et al. in J.Am.Chem-Soc. Vol. 109 (24) , pp. 7408-16 (1987). This article also indicates how complexes containing vanadium as the transition metal can be prepared. The reaction of V0C1 3 with para-substituted arylisocyanates can be mentioned here as an example. For the preparation of complexes based on the other transition metals specific preparation methods are known in the literature. Reference can be made to the article by .A. Nugent and B.L. Haymore in Coord. Chem. Rev. 31 (1990) pp. 123-175. The amido complexes of the invention can be prepared in several ways. The following routes can for example be used: a) the amido group is obtained through a salt- exchange reaction between a transition metal- imidoarylhalide and an alkali metal amide (Me- N iR 2 , where Me is for example Li, Na or K) , b) the amido group is obtained via a reaction of a transition metal-imidoarylhalide with an amine in the presence of a halogen catcher (e.g. a Lewis base such as triethylamine) , c) similar to what has been said above, via the reaction of a substituted amine, the substituent being a good leaving group, such as trimethylsilicon. Several routes for the synthesis are hence available and known to a person skilled in the art. The catalyst also contains an organometaliic compound of group 1, 2, 12 or 13 as a cocatalyst (again according to the new IUPAC list). At least one hydrocarbon group is bound directly to the metal atom via a carbon atom. The compounds of sodium, lithium, zinc and magnesium and in particular aluminium can be mentioned as compounds of such metals in which at least one hydrocarbon group is bound directly to the metal ion via a carbon atom. The hydrocarbon group bound to the metal atom in these compounds preferably contains between 1 and 30 carbon atoms, more in particular 1-10 carbon atoms. Examples of suitable compounds are amylsodium, butyllithium, diethylzinc, butylmagnesium chloride and dibutylmagnesium. Aluminium compounds, in particular trialkylaluminium compounds (such as triethylaluminium), alkylaluminium hydrides (such as diisobutylalumium hydride), alkylalkoxyaluminium compounds and halogen- containing aluminium compounds (such as diethylaluminium chloride, diisobutylaluminium chloride, monoethylaluminium chloride and ethylaluminium sesquichloride) , are preferred. Mixtures of such compounds can also be used. The molar ratio of the organometaliic compound and the transition-metal complex can be varied within a wide range. In general this ratio will lie between 1:1 and 1500:1. Preferably it is chosen to be between 2:1 and 300:1, more in particular between 3:1 and 50:1. The catalyst can be added to a polymerisation reactor both in dissolved condition (in which case a solvent or dispersing agent that is also used in the corresponding liquid-phase polymerisation is preferably chosen) and in a form with which at least one of the components is applied to a carrier. Several techniques for achieving the latter option, which are known per se, are known to a person skilled in the art. Silica, alumina, zeolite, MgCl 2 , etc. can for example serve as the carrier. This so-called heterogenisation of the catalyst makes it possible to carry out the polymerisation in a slurry or as a gas-phase process. The catalyst can be modified in several ways to make it more suitable for the preparation, via a Ziegler polymerisation, of an olefine polymer. For example the catalyst may also contain a promoter, that is a compound that improves a catalyst's polymerisation yield. Halogenated compounds are particularly suitable promoters. Preference is given to the use of specific compounds with a low halogen content as promoters in the preparation of copolymers of ethylene so as to avoid too high a halogen concentration in the polymer to be prepared. Substantially and preferably, said compounds contain at most 2 halogen atoms per molecule, for example alkyl or alkoxyalkyl esters of phenyl mono- or dihalogen acetic acid. Reference can be made to US-A-4,435,552 for these and other suitable promoters. The catalyst of the invention may also contain a Lewis acid. Such an acid is also capable of increasing the activity of the catalyst according to the invention. Examples of suitable Lewis acids include, but are not limited to: A1C1 3 , AlBr 3 , GaCl 3 , GaBr 3 , BC1 3 or SiCl 4 . Another possibility is that the catalyst of the present invention contains a Lewis base. Like a Lewis acid, such a compound is capable of intensifying the catalytic effect. Examples of Lewis bases include, but are not limited to esters, ethers, ketones, alcohols, amines and the like. Another possibility of influencing the catalytic activity is to (partially) replace the halogen group (or groups) X of the transition metal-imidoaryl complex by a different ligand (that is, the Y group of general formula 1). Examples of such ligands include, but are not limited to: - alkoxygroup, - aryloxygroup, - amine group or amide group, - S compound (such as e.g. sulphide, sulphite, sulphate, thiol, sulphinate), - P compound (such as e.g. phosphine, phosphite, phosphate ) , - cyclopentadienyl, whether or not substituted, - a silicon-containing hydrocarbyl compound. The above modifications can be applied to the catalyst itself or they can be carried out during the polymerisation using methods known in the art. The present invention also relates to a process with which a catalyst according to the invention is used in the preparation, via a Ziegler polymerisation, of an olefine polymer, in particular a polymer based on an olefine chosen from the group comprising cx-olefines, non¬ terminal olefines or diolefines. Mixtures hereof may also be used. In particular the invention relates to a process for polymerising α-olefines. The α-olefines are preferably chosen from the group comprising ethylene, propylene, butylene, pentene, heptene and octene; mixtures hereof may also be used. More preferably ethylene and/or propylene is used as the α-olefine. The use of such olefines leads to the formation of both high-density and low-density crystalline polyethylene homopolymers and copolymers (HDPE, LDPE, LLDPE, etc.) and polypropylene homopolymers and copolymers (PP and EMPP). The monomers required for such products and the processes to be used are known to a person skilled in the art. The process according to the invention is also pre-eminently suitable for the preparation of amorphous or rubbery copolymers based on ethylene and a different α- olefine. Preferably propylene is used as the different α- olefine, which results in the formation of EPM rubber. It is also possible to use a diene in addition to ethylene and the other α-olefine, which results in the formation of a so-called EADM rubber, in particular EPDM (ethylene- propylene-diene rubber). An amorphous copolymer is here and hereinafter understood to be a copolymer which at room temperature and higher temperatures has a crystallinity of at most 5%, measured with the aid of DSC (differential scanning calorimetry) . Preferably the amorphous copolymer has a crystallinity of at most 1%. The olefine can be polymerised in a known manner, both in the gas phase and in a liquid reaction medium. Both solution and suspension polymerisation are suitable for the latter option. The process according to the invention will be elucidated below with reference to the preparation of EP(D)M, which is known per se. For the preparation of other polymers based on an olefine reference is emphatically made to the many publications on this subject. α-Olefines that are suitable for use as the monomer in addition to ethylene in the preparation of an EA(D)M polymer are: propylene, butylene-1, pentene-1, hexene-1, octene-1 or the branched isomers hereof, such as 4-methylpentene-l, and furthermore styrene, α-methyl- styrene. Mixtures of these alkenes can also be used, in which case propylene and/or butylene-1 is preferred. A polyunsaturated compound that is able to introduce unsaturation into the polymer is to be used as the diene in such an amorphous copolymer; this compound contains at least two C=C bonds and may be aliphatic or alicyclic. Aliphatic polyunsaturated compounds generally contain between 3 and 20 carbon atoms; the double bonds may be both conjugated and, preferably, non-conjugated. Examples thereof include: 1,3-butadiene, isoprene, 2,3- dimethylbutadiene-1,3, 2-ethylbutadiene-l,3, piperylene, myrcene, allene, 1,2-butadiene, 1,4,9-decatrienes, 1,4- hexadiene, 1,5-hexadiene and 4-methyl-hexadiene-l,4. Alicyclic polyunsaturated compounds, which may or may not contain a bridging group, may be monocyclic or polycyclic. Examples of such compounds include, but are not limited to norbornadiene and its alkyl derivatives; the alkylidene- norbornenes, in particular the 5-alkylidenenorbornenes-2, in which the alkylidene group contains between 1 and 20, preferably between 1 and 8 carbon atoms; the alkenyl- norbornenes, in particular the 5-alkenylnorbornenes-2, in which the alkenyl group contains between 2 and 20, preferably between 2 and 10, carbon atoms, for example vinyl-norbornene, 5-(2 '-methyl-2 'butenyl)-norbornene-2 and 5-(3 '-methyl-2 'butenyl)-norbornene-2; dicyclopentadiene and the polyunsaturated compounds of bicyclo-(2,2,1)- heptane, bicyclo-(2,2,2)-octane, bicyclo-(3,2,l)-octane and bicyclo-(3,2,2)-nonane, where at least one of the rings is unsaturated. In addition, use can be made of compounds like 4,7,8,9-tetrahydroindene and isopropylidenetetrahydroindene. In particular use is made of dicyclo-pentadiene, 5-methylene- or 5-ethylidene- norbornene-2, or hexadiene-1,4. Mixtures of the compounds described above can also be used. The diene can be present in the copolymer in amounts up to 30 wt.%, preferably however up to at most 10-15 wt.%. In addition to or instead of the diene an unsaturated compound having one or more functional groups, such as halogen atoms, OH-, OR-, C00H-, COOR- or NH 2 groups, may optionally be incorporated in the copolymer in an amount up to 20 wt.%. The molar ratio of the monomers used in the present invention is dependent on the desired composition of the polymer. Because the polymerisation rates of the monomers differ substantially no generally applicable ranges of molar ratios can be given. In the case of the copolymerisation of ethylene and propylene molar ratios of between 1 : 1 and 1 : 5 will however generally be chosen. If a polyunsaturated compound is copolymerised, its molar ratio relative to ethylene will usually be between 0.0001 : 1 and 1 : 1. The polymerisation reaction is generally carried out at a temperature between -40 and 200°C, preferably between 10 and 80°C. The pressure will usually be 0.1-5 MPa, but higher or lower pressures can also be used. Preferably the process is carried out in continuous mode, but it can also be carried out in semi-continuous mode or batchwise. The residence time of the polymerisation reaction used may vary from a few seconds to several hours. A residence time of between a few minutes and an hour is usually preferred. The polymerisation may take place in a liquid that is inert relative to the catalyst, for example one or more saturated aliphatic hydrocarbons (such as butane, pentane, hexane, heptane, pentamethylheptane or petroleum fractions); aromatic hydrocarbons (for example benzene or toluene) or halogenated aliphatic or aromatic hydro¬ carbons (for example tetrachloroethylene) . The temperature and pressure used can be such that one or more of the monomers used, in particular the α-olefine, for example propylene, is liquid and is present in such a large amount that it serves as a dispersing agent. There is then no need for a different dispersing agent. The process according to the invention can be carried out both in a polymerisation reactor filled with gas and liquid and in a reactor filled entirely with liquid. Use of a heterogenised catalyst of the present invention makes it possible to carry out the polymerisation process in suspension or in the gas phase. The molecular weight can be set via techniques known to a person skilled in the art. In particular it can be done by using chain-length regulators, such as diethylzinc and preferably hydrogen. Very small amounts of hydrogen already have sufficient effect on the molecular weight. In the case of liquid-phase processes, the catalyst of the present invention is suitable for use at room temperature or even higher temperatures, so that the heat of reaction can be discharged in a more efficient manner. As is known, this can be done via strong cooling of the feed to the reactors or via evaporation of a portion of the reaction medium. After polymerisation the polymer can be worked up in different manners. Both evaporation of the solvent and steam-coagulation are suitable in the case of liquid-phase processes. Amorphous copolymers obtained using the process of the present invention generally contain between 25 and 85 wt.% ethylene. Products with an ethylene content of between 40 and 75 wt.% are preferred. Such copolymers are suitable for a variety of applications, for example for the manufacture of hoses, conveyor belts and pre-formed seals. Optionally, the copolymers can be vulcanised according to the standard methods known in the art, using free radical supplying substances such as peroxides or using sulphur. In order to make the product processable as a rubber the copolymer can be mixed with oil. This is preferably done during the polymerisation. Adding agents to the copolymer to obtain a so-called friable bale is known. This can be done for example by adding for example talc or by using a system such as that described in EP-A- 427,339. The composition described therein, comprising an inorganic partitioning agent, a thickener and an anionic dispersant, is very suitable for use with the products of the present invention. The invention will be described below with reference to the following examples and comparative experiments, without being limitative hereto. Cat. 1 = V0C1 3 Cat. 2 = ArN=VCl 2 N(Et) 2 where Ar = o,o diiso- Cat. 3 = ArN=VCl 2 N(Et) (Ph) propylphenyl Cat. 4 = ArN=VCl 2 N(Ph) 2 Ph = phenyl Cat. 5 = ArN=VCl 2 -carbazilido Et = ethyl Cat. 6 = ArN=VCl 2 -(N-ethyl) 2,4 dichloroanilido DCPAE = dichlorophenylacetic ethyl ester SEAC = ethylaluminium sesquichloride C 3 cont.= weight content of propylene units in the polymer Yield = either the yield in grams of polymer (g) or in kilograms per gram of transition metal (kg/g of M). Comparative Experiment A A 1-litre glass autoclave was filled with 400 ml of petrol and 0.1 mmole of SEAC. The reactor was brought to a pressure of 8 bar with the aid of purified monomers and was conditioned so that the propylene : ethylene ratio in the gas cap was 2:1. The temperature of the reactor was 30°C. Then 0.006 mmole of cat. 1, immediately followed by 0.025 mmole of DCPAE, was added to the contents of the reactor. During the polymerisation the concentrations of the monomers were kept constant as much as possible by supplying propylene (200 nl/hr) and ethylene (100 nl/hr) to the reactor. After 10 minutes' polymerisation no reaction was observed any more and the reactor was depressurized, the solution was collected and dried. An amorphous copolymer of ethylene and propylene was obtained. See Table 1 for the results obtained. Example I The same polymerisation setup as in Comparative Experiment A was used. Now a transition metal-imidoaryl complex according to the invention, notably cat. 2, was used as the catalyst component. The reaction conditions were the same as those of Comparative Experiment A. The catalyst remained active with time; after 60 minutes' polymerisation the reactor was depressurized and an amorphous polymer was obtained. Example II Example I was repeated, only now using cat. 3 as the catalyst component. The catalyst showed stable polymerisation behaviour with time; after 50 minutes' polymerisation the reaction was stopped by depressurizing the reactor. Examples III-V Example I was repeated using cats. 4, 5 and 6, respectively, and a polymerisation time of 60 minutes. The results (shown in Table 1) manifestly show that a considerable improvement of the activity and stability is obtained with a catalyst according to the invention. This is clearly apparent from the increase in the yield of polymer per gram of transition metal. In addition, the diarylamido ligand appears to yield a more active catalyst than the dialkylamido ligand or the alkylarylamido ligand. The increase in the activity of the catalyst causes a corresponding and proportionate decrease in the concentration of transition metal in the prepared polymer (a factor of 10 going from Comparative Experiment A to Example III) . Table 1 n.a. = not analyzed

Claims: C L A I S 1. Catalyst suitable for the preparation, via a Ziegler polymerisation, of an olefine polymer, comprising an organometaliic compound and a transition metal- imidoaryl complex, characterised in that the transition metal-imidoaryl complex contains at least one amido group bound to the transition metal, the aryl group in the complex being an o,o-disubstituted phenyl group. 2. Catalyst according to claim 1, characterised in that the amido group has the formula -NR^, where R λ and R 2 , independently of one another, are an alkyl group, an alkenyl group, an aryl group or a silicon- containing hydrocarbyl group. 3. Catalyst according to claim 2, characterised in that x and R 2 are an aryl group. 4. Catalyst according to any one of claims 1-3, characterised in that the aryl group in the complex is an o,o-dimethylphenyl group or an o,o-diisopropyl- phenyl group. 5. Catalyst according to any one of claims 1-4, characterised in that the organometaliic compound contains aluminium. 6. Catalyst according to any one of claims 1-5, characterised in that the transition metal-imidoaryl complex contains vanadium. 7. Catalyst according to any one of claims 1-6, characterised in that a promoter is also present. 8. Catalyst according to claim 7, characterised in that the promoter contains at most two halogen atoms per molecule. 9. Catalyst according to any one of claims 1-8, characterised in that a Lewis acid or a Lewis base is also present. 10. Process for the preparation, via a Ziegler polymerisation, of an olefine polymer, characterised in that the olefine is polymerised in the presence of a catalyst according to any one of claims 1-9. 11. Process according to claim 10, characterised in that the olefine is chosen from the group comprising α-olefine, non-terminal olefine, diolefine or mixtures hereof. 12. Process according to claim 11, characte ised in that the α-olefine is chosen from the group comprising ethylene, propylene, butylene, pentene, heptene, octene or mixtures hereof. 13. Process according to any one of claims 10-12, characterised in that a polymer is prepared on the basis of ethylene and/or propylene. 14. Process according to claim 13, characterised in that a rubbery polymer is prepared on the basis of ethylene, propylene and optionally a diene. 15. Polymer based on an olefine, obtainable through Ziegler polymerisation of the olefine with the aid of a catalyst according to any one of claims 1-9 or using a process according to any one of claims 10-14.

Inventors: KONINGS JEROEN HUBERTINA GERAR, MUSKENS BERNARDUS JOHANNA, PERSAD RADJINDRAKUMAR, RADEMAKERS GERARDUS ARNOLDUS, RENKEMA JACOB, VERWEIJ PETRONELLA DANIELLE, KONINGS, JEROEN, HUBERTINA, GERARDUS, MUSKENS, BERNARDUS, JOHANNA, PERSAD, RADJINDRAKUMAR, RADEMAKERS, GERARDUS, ARNOLDUS, RENKEMA, JACOB, VERWEIJ, PETRONELLA, DANIELLE
Applicants: DSM NV, KONINGS JEROEN HUBERTINA G, RENKEMA JACOB, DSM N.V., KONINGS, JEROEN, HUBERTINA, GERARDUS, RENKEMA, JACOB
Application year: 1993
Main classification: C08F4
IPC codes: B01J31, C08F4, C08F10, C08F36, C08F210