Soluble anionic polymerization initiators and products therefrom

Abstract: An acyclic alkane soluble anionic polymerization initiator includes a mixture of from about 90 to about 10 parts by weight of a lithio amine having the general formula A₁Li and from about 10 to about 90 parts by weight of at least one other lithio amine having the general formula A₂Li. A₁ and A₂ are selected from the dialkyl, alkyl, cycloalkyl and dicycloalkyl amine radicals and cyclic amine radicals. There is also provided a method of forming a mixture of anionic polymerization initiators, a functionalized polymer and a method of forming a functionalized polymer.

Description: The subject invention relates to anionic polymerization resulting in diene homo- and copolymer elastomers. More particularly, the present invention relates to polymerization employing soluble lithio amine initiators. Specifically, the invention relates to an initiator which is a mixture of at least two different lithio amines, wherein their mixture confers solubility. The initiator is soluble in acyclic alkane solvents, and reproducibly polymerizes monomers in a controllable manner to products with a narrow molecular weight distribution range and other desirable properties. When conducting polymerizations on a commercial basis, it is important to utilize process conditions and components which will allow the molecular weight of the end products to be narrowly and reproducibly defined. The characteristics of a given polymer and its usefulness are dependent, among other things, upon its molecular weight. Hence, it is desirable to be able to predict with some certainty the molecular weight of the end product of the polymerization. When the molecular weight is not narrowly definable, or is not reproducible on a systematic basis, the process may not be commercially viable. In the art, it is desirable to produce elastomeric compounds exhibiting reduced hysteresis characteristics. Such elastomers, when compounded to form articles such as tires and power belts, will show an increase in rebound, a decrease in rolling resistance and will have less heat build-up when subjected to mechanical stresses. A major source of hysteretic power loss has been established to be due to the section of the polymer chain from the last cross link of the vulcanizate to an end of the polymer chain. This free end cannot be involved in an efficient elastically recoverable process, and as a result, any energy transmitted to this section of the cured sample is lost as heat. It is known in the art that this type of heat loss can be reduced by preparing higher molecular weight polymers which necessarily have fewer end groups per given weight. However, this procedure is not always useful because processability of the rubber with compounding ingredients and during shaping operations decreases rapidly with increasing molecular weight. U.S. 5,149,457 describes the use of mixtures of certain lithio amines to confer solubility in aromatic solvents. However, the use of aromatic solvents is often undesirable for anionic polymerizations. Moreover, the lithium amides or lihio amines described in that patent are either unsuitable or undesirable as anionic polymerization initiators, or will not give products with reduced hysteresis characteristics. It is difficult to obtain consistent properties, such as a reduction in hysteresis characteristics, if the polymer cannot be controllably reproduced in a narrow molecular weight distribution range. See, for example, U.S. 4,935,471, in which some polymers are prepared with a heterogeneous mixture of certain secondary amines, including lithium pyrrolidide. Polymers made in this manner have widely varying molecular weights, broad polydispersities, and their functional terminations tend to be erratic, giving rise to poorly reproducible hysteresis reduction results. A major drawback with many of these known anionic lithio amine initiators, is that they are not soluble in acyclic alkanes, such as hexane. Polar solvents have heretofore been employed including the polar organic compounds, especially ethers such as dimethyl or diethyl ether, as well as tetrahydrofuran, diethylene glycol methyl ether (diglyme). The present invention provides novel, acyclic alkane soluble initiators, useful to initiate an anionic polymerization. The invention provides for the incorporation of two separate functionalities from the initiator at two or more ends of separate polymer chains. The invention also provides for efficient, controllable and reproducible polymerizations, with the preparation of well defined end-products of a relatively narrow molecular weight distribution range and having desired hysteretic properties. EP-A-0 423 087 describes a method of preparing lithium amides in a greater concentration, which comprises the step of reacting in a suitable solvent an alkyl lithium and a mixture of amines. It is an object of the present invention to provide anionic polymerization initiators which are soluble in acyclic alkanes. It is a further object of the present invention to provide a method of forming a functionalized polymer from such an anionic polymerization initiator. It is still a further object of the invention to provide an initiator which will reproducibly polymerize a monomer or monomers within a narrow, predictable molecular weight range. It is an additional object of the invention to provide such an initiator which will allow for the incorporation of two separate functional groups onto separate ends of the resulting polymers. It is another object of the present invention to provide elastomers formed with such a polymerization initiator. It is also an object of certain embodiments of the present invention to provide diene polymers having reduced hysteresis characteristics. It is a further object of the present invention to provide vulcanizable elastomeric compounds. Still another object of the present invention is to provide an improved tire formed at least in part, from an elastomer as above. In general, there is provided according to the invention, an acyclic alkane-soluble anionic polymerization initiator. The initiator consists essentially of a mixture comprising from 90 to 10 parts by weight of a lithio amine having the general formula A 1 Li and from 10 to 90 parts by weight of at least one other lithio amine having the general formula A 2 Li. The anionic radicals A 1 and A 2 are different and each is selected from cyclic amine radicals having the general formula wherein R 1 is selected from the group consisting of an alkylene, oxy- or amino-alkylene groups having from 3 to 12 methylene groups and wherein R 1 may be bicyclic, such that two methylene groups therein are bridged to form a bicycloalkane. In a preferred anionic polymerization initiator R 1 includes at least six methylene groups, two of which are bridged to form a bicycloalkane radical. In a further preferred anionic polymerization initiator A is selected from the group consisting of hexamethyleneimine; 1,3,3-trimethyl-6-azabicyclo [3.2.1] octane; pyrrolidine; piperidine; piperazine; 1-azacyclooctane; and derivatives thereof. In a further preferred anionic polymerization initiator said pyrrolidine derivative is perhydroindole. There is also provided according to the invention, a method of forming a functionalized polymer. The method comprises the steps of forming a solution of one or more anionically polymerizable monomers in an acyclic alkane solvent; and, polymerizing the monomers in the presence of an initiator which is soluble in the acyclic alkane solvent. The initiator consits essentially of a mixture comprising from 90 to 10 parts by weight of a lithio amine having the general formula A 1 Li and from 10 to 90 parts by weight of at least one other lithio amine having the general formula A 2 Li. A 1 and A 2 are described hereinabove. A functionalized polymer according to the invention comprises a polymer having a functional group derived from a polymerization initiator consisting essentially of a mixture comprising from 90 to 10 parts by weight of a lithio amine having the general formula A 1 Li and from 10 to 90 parts by weight of at least one other lithio amine having the general formula A 2 Li. A 1 and A 2 are as described hereinabove. There is also provided a method of preparing an acyclic alkane soluble anionic polymerization initiator, which comprises the steps of froming a solution of A 1 H and A 2 H in an anhydrous, aprotic solvent, where A 1 and A 2 are as described hereinabove; adding an organolithium compound to the solution and allowing the organolithium compound to react with A 1 and A 2 H. The organolithium compound has the general formula RLi where R is selected from the group consisting of alkyls, cycloalkyls, alkenyls, aryls and aralkyls having from 1 to 20 carbon atoms and short chain length low molecular weight polymers from diolefin and vinyl aryl monomers having up to 25 units. As will become apparent from the description which follows, the present invention provides novel polymerization initiators which are mixtures soluble in acyclic alkanes such as hexane, pentane, heptane, octane, their alkylated derivatives, mixtures thereof and the like. A initiator is considered to be soluble herein if it is soluble up to about 1 molar concentration at room temperature, as demonstrated by a lack of observable precipitate. Some useful initiators according to the invention are soluble at lower and some at higher concentrations. It has also been discovered herein that certain vulcanizable elastomeric compounds and articles thereof based upon functionalized polymers formed using such an initiator mixture, exhibit useful properties, such as for example, reproducible relatively narrow molecular weight ranges. Furthermore, each of the resulting polymers contains a functionality from one of the components of the initiators, which functionality is useful for example, in improving hysteresis properties, that is, reducing hysteretic loss. While the initiators of the present invention are soluble in acyclic alkane solvents, it will be appreciated that the use of the initiators in other solvent systems is also within the scope of the invention, as will be further described hereinbelow. The initiator according to the invention preferably consists essentially of a metal amide which may or may not be soluble in an acyclic alkane solvent, and one or more other metal amides which also may or may not be soluble in an acyclic alkane solvent. The initiator has the general formula xA 1 Li·yA 2 Li, where x + y = 1 and both x and y range from 0.1 to 0.9, and preferably from 0.3 to 0.7. That is, in the broad embodiment, the initiator contains from 90 to 10 parts by weight of A 1 Li and from 10 to 90 parts by weight of A 2 Li. The A 1 and A 2 components in each of the amines of the initiator, represent an amine functionality to be incorporated into the resulting polymer. A 1 and A 2 may be selected from cyclic amine radicals having the general formula wherein R 1 is selected from the group consisting of an alkylene, oxy- or amino-alkylene groups having from 3 to 12 methylene groups and wherein R 1 may be bicyclic, such that two methylene groups therein are bridged to form a bicycloalkane. Exemplary R 1 groups include tetramethylene, hexamethylene, oxydiethylene and N-alkylazadiethylene. R 1 may be bicyclic, such that two methylene groups therein are bridged to form a bicycloalkane, such as 1,3,3-trimethyl-6-azabicyclo [3.2.1] octane. By "bridged" it is understood to mean that two non-adjacent methylene groups in a larger ring are connected, either by bonding directly or through an alkylene group having one or more methylene groups, thus forming a bicyclic structure of smaller rings. The resulting polymerizations are slow, presumably due to hindrance around the nitrogen at the initiation site, if, in a preferred embodiment of the invention, the carbon atoms in R 1 bonded directly to the nitrogen in the amine radical, are also bonded to at total of at least three hydrogen atoms. For example, as long as A 1 and A 2 are different they may each be a derivative of pyrrolidine; piperidine; piperazine; perhydroazepine, also known as hexamethyleneimine (HMI); 3,3,5-trimethyltetrahydroazepine, also known as trimethylhexamethyleneimine (THMI); and, 1-azacyclooctane including bicyclics such as perhydroisoquinoline and perhydroindolene. Pyrrolidine, perhydroazepine and 1-azacyclooctane are preferred for forming the metal amides in the mixture. Preferred A 1 and A 2 components for the amine precursor of the metal amides include hexamethyleneimine, 1,3,3-trimethyl-6-azabicyclo [3.2.1] octane, pyrrolidine, 1-azacyclooctane, 3,3,5-trimethyltetrahydroazepine. As stated hereinabove, some of the metal amides may not each be themselves soluble (as the term is used herein) in acyclic alkanes. For example, lithium pyrrolidide, lithium hexamethyleneimine and lithium azacyclooctane are not soluble in hexane. One of the unexpected results of the invention, is that such otherwise non-soluble metal amides are rendered soluble when mixed with other metal amides, as will be exemplified hereinbelow. The initiator according to the present invention can be formed by preparing a mixture of the amine components A 1 H and A 2 H, in an anhydrous, aprotic solvent, such as the hexane. To this solution is then added an organolithium reagent in the same or a similar solvent. That is, an acyclic alkane soluble mixture of anionic polymerization initiators is prepared, according to one aspect of the invention, by forming a solution of a first functionalizing agent and at least one other functionalizing agent in an anhydrous, aprotic solvent, and adding an organolithium reagent to the solution. The organolithium reagent has the general formula RLi where R is selected from the group consisting of alkyls, cycloalkyls, alkenyls, aryls and aralkyls having from 1 to 20 carbon atoms and short chain length low molecular weight polymers from diolefin and vinyl aryl monomers having up to 25 units. Typical alkyls include n-butyl, s-butyl, methyl, ethyl and isopropyl. The cycloalkyls include cyclohexyl and menthyl. The alkenyls include allyl and vinyl. The aryl and aralkyl groups include phenyl, benzyl and oligo(styryl). Exemplary short chain length polymers, also known as "oligomers", include the oligo(butadienyls), oligo(isoprenyls) and oligo(styryls). The solution of the mixture of amines and the organolithium reagent is allowed to react for from several minutes to 1 to 2 hours or more at ambient temperature (25° to 30° C), or elevated temperatures up to about 100°C, preferably at less than 50°C, and more preferably at less than 38°C, following which the soluble catalyst is ready for use. Reaction times of about one hour are normally sufficient. The two amide initiators are mixed in amounts of from 90 to 10 parts by weight of the first amide component with from 10 to 90 parts by weight of the second amide component. It is preferred that the two amides be mixed at a ratio of from 30:70 to 70:30 parts by weight, and more preferably at 50:50 parts by weight. The amide components are mixed in an excess of an acyclic alkane or hydrocarbon solvent. If more than one second amide component is used, the ratios may be adjusted accordingly. The final concentration of mixed lithium amides may range from very dilute to as high as 1 or 2 molar, depending on the combination of amides used. As stated above, the initiator mixture thus formed may be employed as to prepare many anionically-polymerized elastomers, e.g., polybutadiene and polyisoprene and copolymers thereof with monovinyl aromatics such as styrene and alpha methyl styrene or trienes such as myrcene. Thus, the elastomers include diene homopolymers and copolymers thereof with monovinyl aromatic polymers. Suitable monomers include conjugated dienes having from 4 to 12 carbon atoms and monovinyl aromatic monomers having 8 to 18 carbon atoms and trienes. Examples of conjugated diene monomers and the like useful in the present invention include 1,3-butadiene, isoprene, 1,3-pentadiene, 2,3-dimethyl-1,3-butadieneand 1,3-hexadiene, and aromatic vinyl monomers include styrene, a-methylstyrene, p-methylstyrene, vinyltoluene and vinylnaphtalene. The conjugated diene monomer and aromatic vinyl monomer are normally used at the weight ratios of 95-50:5-50, preferably 95-65:5-35. Polymerization is conducted in an acyclic alkane or hydrocarbon solvent, such as the various pentanes, hexanes, heptanes, octanes, their alkylated derivatives, and mixtures thereof. Other solvents may also be used, including cyclohexane and benzene. In order to promote randomization in copolymerization and to control vinyl content, a polar coordinator may be added to the polymerization ingredients. Amounts range between 0 and 90 or more equivalents per equivalent of lithium. The amount depends on the amount of vinyl desired, the level of styrene employed and the temperature of the polymerization, as well as the nature of the specific polar coordinator (modifier) employed. Compounds useful as polar coordinators are organic and include tetrahydrofuran, linear and cyclic oligomeric oxolanyl alkanes such as 2-2'-di(tetrahydrofuryl) propane, di-piperidyl ethane, hexamethylphosphoramide, N-N'-dimethylpiperazine, diazabicyclooctane, dimethyl ether, diethyl ether and tributylamine. The linear and cyclic oligomeric oxolanyl alkane modifiers are described in U.S. 4,429,091, Compounds useful as polar coordinators include those having an oxygen or nitrogen hetero-atom and a non-bonded pair of electrons. Other examples include dialkyl ethers of mono and oligo alkylene glycols; "crown" ethers; tertiary amines such as tetramethylethylene diamine (TMEDA); linear THF oligomers. A batch polymerization is prepared by conventional techniques, and may be begun by charging a blend of monomer(s) and acyclic alkane solvent or other appropriate solvents, to a suitable reaction vessel, followed by the addition of the polar coordinator (if employed) and the mixture of initiator compounds previously described. The reactants are heated to a temperature of from 20 to 200°C, and the polymerization is allowed to proceed for from 0.1 to 24 hours. A functional amine group is derived from each of the initiator compounds and bonds at the initiation site of one of the growing polymers. Thus, substantially every resulting polymer chain has the general formula A 1 YLi or A 2 YLi where A 1 and A 2 are as described above, and Y is a divalent polymer radical which is derived from any of the foregoing diene homopolymers, monovinyl aromatic polymers, diene/monovinyl aromatic random copolymers and block copolymers. The monomer addition at the lithium end causes the molecular weight of the polymer to increase as the polymerization continues. To terminate the polymerization, and thus further control polymer molecular weight, a polymer modifying agent such as a terminating, coupling or linking agent may be employed. Useful modifying agents include active hydrogen compounds such as water or alcohol, or compounds providing multifunctionality such as, for example, carbon dioxide; tetramethyldiaminobenzophenone; dialkyl- and dicycloalkyl-carbodiimides having from 5 to 20 carbon atoms; (R 3 ) a ZX b ; and, where Z is tin or silicon. It is preferred that Z is tin. R 3 is an alkyl having from 1 to 20 carbon atoms; a cycloalkyl having from 3 to 20 carbon atoms; an aryl having from 6 to 20 carbon atoms; or, an aralkyl having from 7 to 20 carbon atoms. For example, R 3 may include methyl, ethyl, n-butyl, neophyl, phenyl or cyclohexyl. X is chlorine, bromine or iodine, "a" is from 0 to 3, and "b" is from 1 to 4; where a + b = 4. Each R 4 is the same or different and is an alkyl, cycloalkyl or aryl, having from 1 to 12 carbon atoms. For example, R 4 may include methyl, ethyl, nonyl, t-butyl or phenyl. R 5 is an alkyl, phenyl, alkylphenyl or dialkylaminophenyl, having from 1 to 20 carbon atoms. For example, R 5 may include t-butyl, 2-methyl-4-pentene-2-yl, phenyl, p-tolyl, p-butylphenyl, p-dodecylphenyl, p-diethyl-aminophenyl and p-(pyrrolidino)phenyl. Each R 6 is the same or different, and is an alkyl or cycloalkyl having from 1 to 12 carbon atoms. Two of the R 6 groups may together form a cyclic group. For example, R 6 may include methyl, ethyl, octyl, tetramethylene, pentamethylene or cyclohexyl. R 7 is alkyl, phenyl, alkylphenyl or dialkylaminophenyl, having from 1 to 20 carbon atoms. For example, R 7 may include methyl, butyl, phenyl, p-butylphenyl, p-nonylphenyl, p-dimethylaminophenyl, p-diethylaminophenyl or p-(piperidino)phenyl. Other examples of useful modifying agents include SnCl 4 , (R 1 ) 3 SnCl, (R 1 ) 2 SnCl 2, R 1 SnCl 3, SiCl 4, (R 1 ) 3 SiCl, (R 1 ) 2 SiCl 2 , R 1 SiCl 3 , carbodiimides, N-methylpyrrolidine, cyclic amides, cyclic ureas, isocyanates, Schiff bases and 4,4'-bis(diethylamino) benzophenone, where R 1 is as described hereinabove. The modifying agent is added to the reaction vessel, and the vessel is agitated for 1 to 1000 minutes. As a result, an elastomer is produced having an even greater affinity for compounding materials such as carbon black, and hence, even further reduced hysteresis. Additional examples of modifying agents include those found in U.S. . 4,616,069 . Care should be taken to preserve the live C-Li for effective termination, such as by avoiding prolonged exposure to high temperatures or impurities such as protic acids or the like. The polymer may be separated from the solvent by conventional techniques. These include steam or alcohol coagulation, thermal desolventization, or any other suitable method. Additionally, solvent may be removed from the resulting polymer by drum drying, extruder drying or vacuum drying. The elastomers of the present invention comprise a plurality of polymer molecules having a functional group at two or more ends. Compounds of such polymers may result in products exhibiting reduced hysteresis, which means a product having increased rebound, decreased rolling resistance and has less heat build-up when subjected to mechanical stress. Furthermore, one aspect according to the invention elastomer is formed from a plurality of polymer chains as above, and is also multifunctional wherein the polymer also carries a tin-carbon bond, such as may be derived from a modifying agent such as the terminating, coupling or linking agent discussed hereinabove. It has also been found, as will be exemplified hereinbelow, that polymers formed using the initiator mixture of the invention, are repeatably producible in a relatively narrow range of molecular weights, such as that substantially consistently reproducible polymers are possible with a molecular weight range of 20,000 to 250,000. The polymers of the present invention can be used alone or in combination with other elastomers to prepare an elastomer product such as a treadstock compound. A treadstock compound can be formed from a vulcanizable elastomeric composition of the invention polymers. A tire according to the invention may have at least a portion of its tread formed from such a treadstock compound. Compounds to form other tire structural elements, such as sidewalls and carcasses can also be advantageously made from the polymers of the present invention. For example, the polymers according to the invention can be blended with any conventionally employed treadstock rubber which includes natural rubber, synthetic rubber and blends thereof. Such rubbers are well known to those skilled in the art and include synthetic polyisoprene rubber, styrene/butadiene rubber (SBR), polybutadiene, butyl rubber, Neoprene, ethylene/propylene rubber, ethylene/propylene/diene rubber (EPDM), acrylonitrile/butadiene rubber (NBR), silicone rubber, the fluoroelastomers, ethylene acrylic rubber, ethylene vinyl acetate copolymer (EVA), epichlorohydrin rubbers, chlorinated polyethylene rubbers, chlorosulfonated polyethylene rubbers, hydrogenated nitrile rubber and tetrafluoroethylene/propylene rubber. When the polymers of the present invention are blended with such conventional rubbers, the amounts can vary widely such as between 10 and 99 percent by weight. The polymers can be compounded with reinforcing agents such as carbon black in amounts ranging from 5 to 100 parts by weight, per 100 parts of rubber (phr), with 5 to 80 phr being preferred, in order to form a vulcanizable elastomeric composition. Useful carbon blacks may include any of the commonly available, commercially-produced carbon blacks but those having a surface area (EMSA) of at least 20 m 2 /gram and more typically at least 35 m 2 /gram up to 200 m 2 /gram or higher are preferred. Surface area values used in this application are those determined by ASTM test D-1765 using the cetyltrimethyl-ammonium bromide (CTAB) technique. Among the useful carbon blacks are furnace black, channel blacks and lamp blacks. More specifically, examples of the carbon blacks include super abrasion furnace (SAF) blacks, high abrasion furnace (HAF) blacks, fast extrusion furnace (FEF) blacks, fine furnace (FF) blacks, intermediate super abrasion furnace (ISAF) blacks, semi-reinforcing furnace (SRF) blacks, medium processing channel blacks, hard processing channel blacks and conducting channel blacks. Other carbon blacks which may be utilized include acetylene blacks. Mixtures of two or more of the above blacks can be used in preparing the carbon black products of the invention. Typical values for surface areas of usable carbon blacks are summarized in the following TABLE I. CARBON BLACKS ASTM Designation (D-1765-82a) Surface Area (m 2 g) (D-3765) N-110 126 N-220 111 N-339 95 N-330 83 N-550 42 N-660 35 The carbon blacks utilized in the preparation of the rubber compounds of the invention may be in pelletized form or an unpelletized flocculent mass. Preferably, for more uniform mixing, unpelletized carbon black is preferred. The reinforced rubber compounds can be cured in a conventional manner with known vulcanizing agents at 0.5 to 4 phr. For example, sulfur or peroxide-based curing systems may be employed. For a general disclosure of suitable vulcanizing agents one can refer to Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd ed., Wiley Interscience, N.Y. 1982, Vol. 20, pp. 365-468, particularly "Vulcanization Agents and Auxiliary Materials" pp. 390-402. Vulcanizing agents may be used alone or in combination. Vulcanizable elastomeric compositions of the invention can be prepared by compounding or mixing the polymers thereof with carbon black and other conventional rubber additives such as fillers, plasticizers, antioxidants and curing agents using standard rubber mixing equipment and procedures and conventional amounts of such additives. General Experimental In order to demonstrate the preparation and properties of the initiator mixture and elastomers of the present invention, a number of such initiator mixtures and elastomers were prepared. A solution of styrene and butadiene monomers in hexane was prepared and polymerized with the above described mixtures. As noted above, various techniques known in the art for carrying out anionic polymerizations may be employed without departing from the scope of the present invention. Example No. 1 Preparation of Initiator Mixture 3,3,5-trimethyltetrahydroazepine (also known as trimethylhexamethyleneimine or "THMI"), was vacuum distilled from calcium hydride at approximately 75°C at approximately 15 Torr and transferred under nitrogen to a dried, nitrogen-purged bottle. Hexamethyleneimine, "HMI", was distilled from calcium hydride and transferred under nitrogen to a dried, nitrogen-purged bottle. The mixed lithium amides HMI and THMI ("LHMI/LTHMI") were prepared by treating a mixture of 7.5 milli equivalent (meq) of a 1.16 M solution of THMI in hexanes and 7.5 meq of neat HMI with 15.0 meq of a 1.67 M solution of n-butyllithium in hexanes, swirling the mixture at room temperature overnight. The resulting approximately 0.9 M solution was a clear, pale yellow. When either HMI or THMI alone was treated with n-butyllithium in hexanes in the absence of the second amine, cloudiness and/or precipitation occurred immediately. The ("LHMI/LTHMI") solution was stable for at least a month at room temperature. Samples were drawn from it by syringe for use in initiating polymerization. A. Polymerization of Butadiene and Styrene with LHMI/LTHMI: A 0.9 M solution of the above initiator mixture was added to a 80 percent/20 percent by weight blend of butadiene and styrene in hexanes, at a level of 1.0 meq Li/100 g monomer, and N,N,N',N'-tetramethylethylenediamine ("TMEDA") was added at 0.30 TMEDA/Li on a mole/mole basis. The mixture was agitated at 50°C for 2.5 hr, proceeding to approximately 100 percent conversion to polymer. In practicing the invention, there is considerable leeway in the reaction times and temperatures, as well as in the reaction vessels, type of agitation, etc., used. The polymer cements then were quenched by injection with 1.5 ml of i-PrOH, treated with an antioxidant (3 ml of a mixture containing 1.6 wt percent DBPC in hexane), coagulated in i-PrOH, air-dried at room temperature, then drum-dried. Suitable characterizations were performed. The product polymer contained 20.0 percent styrene (1.5 percent block), 37.0 percent vinyl (46.3 percent vinyl if butadiene (or "BD") = 100 percent), Tg -47°C, GPC(THF): M n 103582, molecular weight distribution (Mw/Mn or MWD) 1.31, raw ML/4/100 = 15. B. Polymerization of Butadiene and Styrene with LHMI/LTHMI and End-linking with SnCl 4 : The above procedure was followed exactly, except that after 1.5 hour of polymerization at 50°C, the polymerization mixture was treated with 0.8 equivalent of SnCl 4 per equivalent of Li charged. The product was worked up in the same manner as above. The product polymer contained 19.4 percent styrene (0.8 percent block), 39.5 percent vinyl (49 percent vinyl if BD = 100 percent), Tg -45°C , GPC(THF): M n 165756, MWD 1.72, ca. 54 percent high molecular weight; raw ML/4/100 = 65. Evaluation of Compounded Properties The product polymer was compounded and tested as indicated in the test recipe shown in TABLE II, and cured 20 minutes at 165°C. Results of physical tests are reported in TABLE III hereinbelow: COMPOUNDING RECIPE Ingredient Mix Order Parts per Hundred Parts Rubber Polymer 1 100 Naphthenic oil 2 10 Masterbatch Carbon black, N-351 3 55 145-155°C, 60 RPM ZnO 4 3 Antioxidant 5 1 Wax blend 6 2 Total Masterbatch: 171 Stearic acid 2 Final Sulfur 1.5 77-93°C, 40 RPM Accelerator 1 Total Final: 175.5 PHYSICAL TEST RESULTS, EXAMPLE NO. 1 Example No. ML/4/212 1 Hz Dynastat tan δ 50°C Ring Stress-Strain, R.T. (gum) (cpd) M300 T.S. Percent Eb 1-A 15 65 0.098 2562 3244 410 1-B 65 94 0.088 2673 3167 390 In addition, the carbon-bound rubber content of the uncured, final compounded stocks of 1-A and 1-B were 36 percent and 42 percent respectively. This indicates an enhanced interaction between the polymer and carbon black in these cases, compared to unmodified rubber, which typically exhibits 20-22 percent carbon-bound rubber, and a comparable butyllithium-initiated, Sn-linked rubber, which typically exhibits 31-33 percent carbon-bound rubber. The results of this test provide good evidence for reduced hysteresis in this polymer. The Dynastat tan δ(50°C) = 0.098 is about 50 percent below the value expected for a comparable unmodified polymer of this molecular weight, prepared using a typical alkyllithium initiator. The carbon-bound rubber content was determined by placing a 0.4 to 0.5 grams sample of the uncured compound into 100 ml of distilled reagent toluene for two days at room temperature and without agitation. After recovering the solids, at constant weight the amount of rubber attached to carbon can be estimated since the amount of other insoluble ingredients in the original sample, (such as the carbon black) are known. Example No. 2 Preparation of Initiator Mixture Hexamethyleneimine, "HMI", was distilled and handled as described above. Pyrrolidine, "PY", was distilled from CaH 2 at atmospheric pressure and handled in the same manner. The mixed N-lithio salts of HMI and PY ("LHMI/LPY") were prepared by treating a mixture of 7.5 meq of a 5.45 M solution of PY in hexanes and 7.5 meq of a 2.24 M solution of HMI in 85:15 cyclohexane: hexanes with 15.0 meq of a 1.67 M solution of n-butyllithium in hexanes, swirling the mixture at room temperature overnight. The resulting ∼ 1.09 M solution was a clear, light-medium yellow. When PY alone was treated with n-butyllithium in hexane or cyclohexane, in the absence of the second amine or other solubilization agent, heavy precipitation occurred almost immediately. The ("LHMI/LPY") solution was stable for at least several days at room temperature. Samples were drawn from it by syringe for use in initiating polymerization. A. Polymerization of Butadiene and Styrene with LHMI/LPY: The 1.09 M solution of the above initiator was added to a 80 percent/20 percent by weight blend of butadiene and styrene in hexanes, at a level of 1.0 meq Li/100 g monomer, and TMEDA was added at 0.30 TMEDA/Li. The mixture was agitated at 50°C for 2.5 hours, proceeding to approximately 100 percent conversion to polymer. The polymer was worked up as described in the previous examples. The product polymer contained 20.2 percent styrene (3.3 percent block), 28.7 percent vinyl (36.0 percent vinyl if BD = 100 percent), Tg -58°C, GPC(THF): M n 103302, MWD 1.60, raw ML/4/100 = 21. B. Polymerization of Butadiene and Styrene with LHMI/LPY and End-linking with SnCl 4 : The above procedure was followed exactly, except that after 1.5 hour of polymerization at 50°C, the polymerization mixture was treated with 0.8 equivalents of SnCl 4 per equivalents of Li charged. The product was worked up in the same manner as above. The product polymer contained 20.1 percent styrene (1.6 percent block), 35.0 percent vinyl (43.8 percent vinyl if BD = 100 percent), Tg -49°C, GPC(THF): M n 145511, MWD 1.90, ca. 52 percent high molecular weight; raw ML/4/100 = 62. Evaluation of Compounded Properties: Product polymer 2-B was compounded and tested as indicated in the test recipe shown in TABLE II hereinabove, and cured 20 minutes at 165°C. Results of physical tests are reported in TABLE IV hereinbelow. PHYSICAL TEST RESULTS, EXAMPLE NO. 2 Example No. ML/4/212 1 Hz Dynastat tan δ 50°C Ring Stress-Strain, R.T. (gum) (cpd) M300 T.S. Percent Eb 2-B 62 98 0.101 2996 3893 411 The results of this test provided good evidence for reduced hysteresis in this polymer. The Dynastat tan δ(50°C) = 0.101 is about 48 percent below the value expected for an unmodified polymer of this molecular weight, prepared using a typical alkyllithium initiator. A preferred method of preparing the initiators for the mixture, according to the invention, is as follows. A glass vessel, such as a small bottle containing a Teflon or glass-clad magnetic stirring bar, is dried, sealed, and purged with nitrogen. The following reagents are added at room temperature by syringe while stirring: 1. 30 mmol total of a mixture of anhydrous secondary amines in hydrocarbon solvent; 2. 30.1 mmol of alkyl lithium in hydrocarbon solvent (added by syringe at once, with stirring, while taking precaution for back-pressures). The solution will heat and develop pressure immediately, but will soon begin to cool back down. When larger amounts of reagent are prepared, e.g. 250-300 mmol in large bottles or 0.5-1.5 mol in reactors, best results are obtained when chilled or cold water cooling is used to keep the peak reaction temperature at about 38°C or below. The normal procedure has been to allow the mixture to stir overnight at room temperature before using. However, the reaction is essentially complete within minutes. The mixture should be clear, straw-yellow, without significant precipitation. Light-to-moderate haziness or cloudiness does not appear to affect activity. Anhydrous conditions are required. Hydrocarbon solvent solutions with less than 30 parts per million (ppm) of water give best results. Some solutions are stable for 3 or more days, and initiator reagents can be stored under positive nitrogen pressures for periods of up to several weeks or more at room temperature (25-27°C). As is clear from the foregoing examples and specification disclosure, that initiator mixtures according to the present invention are useful for the anionic polymerization of diene monomers. Reproducible polymerization of such polymers within a relatively narrow molecular weight range is achieved, and the resulting polymers also exhibit good preservation of live C-Li ends, when compared to the initiators heretofore known in the art.

Claims: An acyclic alkane soluble anionic polymerization initiator consisting essentially of a mixture comprising: from 90 to 10 parts by weight of a lithio amine having the general formula A 1 Li and from 10 to 90 parts by weight of at least one other lithio amine having the general formula A 2 Li; wherein A 1 and A 2 are different and are independently selected from cyclic amine radicals having the general formula wherein R 1 is selected from the group consisting of an alkylene, oxy- or amino-alkylene groups having from 3 to 12 methylene groups and wherein R 1 may be bicyclic, such that two methylene groups therein are bridged to form a bicycloalkane. An anionic polymerization initiator, as set forth in claim 1, wherein the carbon atoms in R 1 which are bonded directly to the nitrogen in the amine radical are also bonded to a total of at least three hydrogen atoms. An anionic polymerization initiator, as set forth in claim 1, wherein R 1 includes at least six methylene groups, two of which are bridged to form a bicycloalkane radical. An anionic polymerization initiator, as set forth in claim 1, wherein A is selected from the group consisting of hexamethyleneimine; 1,3,3-trimethyl-6-azabicyclo [3.2.1] octane; pyrrolidine; piperidine; piperazine; 1-azacyclooctane; and derivatives thereof. An anionic polymerization initiator, as set forth in claim 4, wherein said pyrrolidine derivative is perhydroindole. A method of anionic polymerization resulting in diene homo- and copolymer elastomers comprising the steps of: forming a solution of one or more anionically polymerizable monomers in an acyclic alkane solvent; and polymerizing said monomers in the presence of an initiator which is soluble in said acyclic alkane solvent; said initiator consisting essentially of a mixture comprising: from 90 to 10 parts by weight of a lithio amine having the general formula A 1 Li and from 10 to 90 parts by weight of at least one other lithio amine having the general formula A 2 Li; wherein A 1 and A 2 are different and independently selected from cyclic amine radicals having the general formula as defined in claim 1. A method, as set forth in claim 6, comprising the further step of reacting the polymer with a modifying agent, such that the resulting polymer is multifunctional. A method, as set forth in claim 7, wherein said modifying agent is selected from the group consisting of carbon dioxide; tetramethyldiaminobenzophenone; dialkyl- and dicycloalkyl-carbodiimides having from 5 to 20 carbon atoms; (R 3 ) a ZX b ; and, where Z is tin or silicon; R 3 is selected from the group consisting of alkyls having from 1 to 20 carbon atoms, cycloalkyls having from 3 to 20 carbon atoms, aryls having from 6 to 20 carbon atoms and aralkyls having from 7 to 20 carbon atoms; X is chlorine or bromine; a is an integer of from 0 to 3, and b is an integer of from 1 to 4, where a + b = 4; each R 4 is the same or different and is selected from the group consisting of alkyls, cycloalkyls and aryls, having from 1 to 12 carbon atoms; R 5 is selected from the group consisting of alkyls, phenyls, alkylphenyls and dialkylaminophenyls having from 1 to 20 carbon atoms; each R 6 is the same or different, and is selected from the group consisting of alkyls and cycloalkyls having from 1 to 12 carbon atoms, and R 7 is alkyl, phenyl, alkylphenyl or dialkylaminophenyl having from 1 to 20 carbon atoms. A method, as set forth in claim 8, wherein the two R 6 groups together form a cyclic group. A method, as set forth in claim 6, wherein said one or more anionically polymerizable monomers are selected from the group consisting of conjugated dienes having from 4 to 12 carbon atoms and monovinyl aromatic monomers having 8 to 18 carbon atoms and trienes. A functionalized polymer comprising: a functional group derived from a polymerization initiator system consisting essentially of a mixture comprising from 90 to 10 parts by weight of a lithio amine having the general formula A 1 Li and from 10 to 90 parts by weight of at least one other lithio amine having the general formula A 2 Li; wherein A 1 and A 2 are different and independently selected from cyclic amine radicals having the general formula as defined in claim 1. An elastomer comprising a plurality of polymer chains of the functionalized polymer as set forth in claim 11. An elastomer as set forth in claim 12, wherein a plurality of said polymer chains also carry at least one tin-carbon bond. A vulcanizable elastomeric composition formed from the elastomer of claim 12 and from 5 to 80 parts by weight of carbon black, per 100 parts of the elastomer. A treadstock compound formed from the vulcanizable elastomeric composition of claim 14. A tire having at least one component formed from the vulcanizable elastomeric composition of claim 14. A method of preparing an acyclic alkane soluble, anionic polymerization initiator comprising the steps of: forming a solution of a first amine and at least one other amine in an anhydrous, aprotic solvent; adding an organolithium reagent to the solution and allowing said organolithium reagent to react with said amines; wherein each of said amines are selected from cyclic amine radicals having the general formula as defined in claim 1, wherein said organolithium reagent has the general formula RLi where R is selected from the group consisting of alkyls, cycloalkyls, alkenyls, aryls and aralkyls having from 1 to 20 carbon atoms and short chain length low molecular weight polymers from diolefin and vinyl aryl monomers having up to 25 units. A method as set forth in claim 17, wherein said step of forming a solution includes mixing from 90 to 10 parts by weight of said first amine with from 10 to 90 parts by weight of said at least one other amine.

Inventors: HALL JAMES E, LAWSON DAVID F, OZAWA YOICHI, HALL, JAMES E., LAWSON, DAVID F., OZAWA, YOICHI
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1993
Main classification: C08F36
IPC codes: C08F36, C08F4, C07D295, C08C19, C08F236