Highly mechanical and corrosion resistant stainless steel and relevant treatment process

Abstract: A stainless steel, suitable for the manufacture of seamless pipes for use in sour-well environment, and consisting of, (in wt.%) C ≦ 0.03, Cr 24.5 - 27, Ni 6.5 - 9, Mo 3.5 - 4.5, W 0.7 - 2.5, Cu 1.5 - 2.5, N 0.25 - 0.30, Mn ≦ 1, P ≦ 0.03, S ≦ 0.005, Si ≦ 1, balance iron and trace impurities. The manufacturing process consists of: 1) preparing an ingot of the above-mentioned composition 2) first hot working: forging or rolling 3) heating the intermediate product to a temperature of 1100⁰ to 1260⁰C 4) hot working by extrusion to final shape and size 5) quenching in water from a temperature of min. 950⁰C 6) annealing at a temperature between 1050⁰ and 1200⁰C for 1 to 30 minutes 7) quenching in water An excellent corrosion resistance is obtained, and tensile strength at room temperature is exceeding 90 ksi.

Description: FIELD OF THE INVENTION The present invention refers to a highly mechanical and corrosion resistant stainless steel and the relevant treatment process. The invention also refers to the manufactures made of the aforesaid stainless steel. PRIOR ART Stainless steels have extensive application in the oil wells drill pipes sector, which requires steel types with adequate mechanical and corrosion resistance. However, the growing exploitation of hydrocarbon fields of acid - or sour - type, named so being high in hydrogen sulphide and/or carbon dioxide and often also in chloride, makes the choice of suitable materials extremely hard. Therefore, in an attempt to prevent any possible accident, such as deep pipe piercing, oil companies fixed very stringent standards for said materials. The most suited steels for use in the aforementioned sour fields are biphasic type, e.g. superduplex type. The on-grade composition (% by wt.) of some of them is reported below: UNS S32750: C ≤ 0.03, Cr 24-26, Ni 6-8, Mo 3-5, N 0.24-0.32, Mn ≤ 1.2, P ≤ 0.035, S ≤ 0.02, Si ≤ 0.8; UNS S32550: C ≤ 0.04, Cr 24-27, Ni 4.5-6.5, Mo 2-4, Cu 1.5-2.5, N 0.1-0.25, Mn ≤ 1.5, P ≤ 0.04, S ≤ 0.03, Si ≤ 1; UNS S32760: C ≤ 0.03, Cr 24-26, Ni 6-8, Mo 3-4, W 0.5-1, Cu 0.5-1, N < 0.3, Mn ≤ 1, P ≤ 0.03, S ≤ 0.01, Si ≤1 Notwithstanding the apparent similarity of compositions, the properties of the above steels are different, e.g.: UNS S32750: due to its high nitrogen content, it shows an increased pitting resistance and an increased mechanical resistance by solid solution hardening; UNS S32760: due to its lower nitrogen content, it is less subject to vulnerability caused by the formation of chromium nitrides. The lower nitrogen contribution to the pitting resistance is compensated by the presence of tungsten in the alloy; UNS S32550 has a nitrogen content similar to that of UNS S32760 and does not contain tungsten. However, the presence of copper increases its corrosion resistance in reducing acid media. The aforementioned steels show minimum guaranteed unit tensile yield strength values of approx. 65-80 ksi max. (445.25 - 548 MPa), which values make them inadequate to use in the fast expanding sour-type deep wells. Better mechanical properties can be obtained only by cold-rolling; this treatment, however, causes a considerable increase in the costs of the material and a decrease in its resistance to corrosion and stress corrosion. EP-A-0 566 814, published after the filing of the present application, describes a superduplex alloy having the following composition (% by weight): C0.025max, Mn 0.80max, Si 0.80max, Cr 24-26, Ni 6.5-8.0, Mo 3.0-4.0, S 0.002max, P 0.025max, Cu 1.2-2.0, W 0.8-1.2, N 0.23-0.33, the balance being iron, with Pitting Index = Cr+3.3Mo+16N>42. Further thermomechanical treatments are not specifically disclosed. Only a hint is made to the presence of a ferrite percentage of 40-60 in the product annealed at 1070-1100°C. EP-A-0 545 753, published after the filing of the present application, describes a superduplex alloy having the following composition (% by weight): C 0.03 or lower, Mn 1.5 or lower, 5 0.008 or lower, Ni 5.0-9.0, Mo 2.0-4.0, Si 1.0 or lower, P 0.040 or lower, solubilized Al 0.040 or lower, Cr 23.0-27, N 0.24-0.32, W higher than 1.5 and 5.0max, at least an element selected among Cu 0-2.0° and V 0-1.5, at least an element selected among Ca 0-0.02, Mg 0-0.02, B 0-0.02, and one or more rare heart elements 0-0.02 in tot., the balance being iron and trace impurities; the following conditions have to be also verified: PREW=%Cr+3.3(%Mo+0.5%W)+16%N at least 40, PSI (Phase Stability Index) =%Cr+3.3%Mo+3%Si≤40. A hint is made in the example to a solubilisation treatment at 1100°C for 30min. EP-A-0 534 864, published between the date of priority claimed and the filing of the present application, describes a superduplex alloy having the following composition (% by weight): C 0.03 or lower, Mn 2.0 or lower, Ni 5.0-9.0, N 0.10-0.35, Si 0.4 or lower, Cr 26.0-30.0, Mo 3.0-4.5, Al 0.01-0.04, Cu and/or W in a total amount of 0-3.0, at least an element selected among Ca, B and Ce in a total amount of 0-0.01, the balance being iron and trace impurities (P 0.03 or lower, S 0.004 or lower, 0 0.015 or lower being considered as impurities) and the following condition having to be further verified: -1.5 ≤ PBI ≤ 1.5 In addition Cu+W have to be comprised between 0.05 and 3.0. The articles manufactured with the above composition are obtained starting from powders and are subjected to a thermal solubilisation treatment at 1000-1200°C, followed by water quenching. EP-A-0 220 141 and EP-A-0 360 143 both describe a duplex alloy with low amounts of W and Cu. Nothing is said about specific thermal treatments. US-A-4 604 887 describes a duplex alloy without W and in which Al (0.01-0.1% by wt.) and Ca and/or B are present. Such alloy is used to produce seamless tubes with a plug mill process, according to a specific thermal treatment, strictly related to specific reducing steps. GB-A- 2160221 discloses a two phase (austenitic -ferretic) stainless steel containing soluble aluminum in amounts less than 0.02 wt. % and having improved impact characteristics, many other elements could be added, among others : Cu, W, V, Ti, NB, ZR, CA, B, MG, however none alloy composition is expressly disclosed. To conclude, no superduplex stainless steel known so far is capable of meeting the mechanical resistance requirements deeper wells and the corrosion and stress corrosion resistance requirements involved by the use in ever more aggressive media. It has now been found an alloy consisting of conveniently selected and well balanced elements capable of solving the problems mentioned above. The alloy complies with oil companies' stringent and exacting regulations governing steel compositions. SUMMARY It is an object of the present invention to obtain a steel alloy. A further object of the present invention is the use of said alloy for producing highly mechanical, corrosion and stress corrosion resistant manufactures in the solubilized hot-extruded or rolled form. It is a further object of the present invention to provide manufactures constructed of said alloy, preferably pipes, and more preferably seamless pipes. A further object of the present invention is the heat treatment, i.e. annealing and quenching, the said manufactures are subjected to to reach minimum guaranteed unit tensile yield strength values of about 90 ksi (616.5 MPa) or higher. Further objects of the present invention will become apparent from the detailed description thereof. DETAILED DESCRIPTION OF THE INVENTION The alloy according to the present invention is characterized by the composition as defined in the appended claims. Preferable composition ranges are disclosed in the dependent claims. The alloy according to the invention is characterized by the presence of W and Cu in the amounts and ranges as defined above and by the combination of same with Cr, Ni, Mo, and N. Adequate alloying and heat treatment give highly mechanical and corrosion resistant products well suited to use in sour-type deep wells. It is therefore possible to obtain superduplex stainless steel manufactures, in particular seamless pipes, which in the solubilized hot-worked form show high mechanical, corrosion and stress corrosion resistance properties. The claimed procedure consists of the concurrent combination of the steps of: preparing an ingot having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1 balance iron and trace impurities; first hot-working of same by traditional techniques, such as forging or rolling, to obtain a semimanufactured product; heating of the semimanufactured product to a temperature of 1100°C to 1260°C and further hot-working of same by extrusion to obtain a manufacture, e.g. seamless pipes, in the desired final shape and size, which is quenched in water from a temperature higher than 950°C; annealing the product at a temperature between 1050°C and 1200°C for 1 to 30 minutes, and quenching in water to obtain and stabilize a biphasic ferrite and austenite structure with ferrite fraction of 0.4 to 0.6 by vol. The following work conditions are preferred: casting into ingots, forging into rods 130-250 mm in diameter, followed by annealing at a temperature of 1180°C to 1240°C, hot-working by extrusion or by rolling and quenching in water from a temperature of 1050°C to 1150°C, final annealing at a temperature of 1090°C to 1190°C, for 5 to 25 minutes, and quenching in water from a temperature of 1050°C min. The various steps of the claimed procedure are adequately combined to obtain an alloy having the desired characteristics. The mechanical properties were probably improved by a synergistic effect produced by solid solution hardening caused by copper and tungsten, and enhanced by the particular thermomechanical cycle adopted. The heat treatment, i.e. solubilization and balancing of phases, at 1050°C to 1190°C for 1 to 30 min. allows to obtain a structure containing a ferrite and an austenite fraction, each being 0.4 to 0.6 by vol. The manufactures produced according to the claimed procedure, after solubilization annealing, showed a unit tensile yield strength at room temperature of 90 ksi (616.5 MPa) min., preferably of 90 to 110 ksi (616.5-753.5Mpa), which value decreases by 15% at 130°C. The manufactures as per the present invention show a much higher stress corrosion resistance than the traditional stainless steels meant for the same applications: therefore, the claimed manufactures, and in particular seamless pipes, can be used in highly aggressive media. The material produced was subjected to slow strength rate test (SSRT) in an aggressive medium and proved to be free from stress corrosion and pitting at high temperatures. In particular, corrosion phenomena did not occur at 80°C in 100 g/l sodium chloride solutions in the presence of a gas phase containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide at a partial pressure of 0.30 bar max.; at 110°C in media containing hydrogen sulphide at a partial pressure of 0.35 bar max., carbon dioxide at a partial pressure of about 40 bar min., and sodium chloride of about 50 g/l; at 180°C, i.e. at the characteristic temperature of very deep wells, in media containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide at 0.30 bar max., in the presence of sodium chloride at a concentration of 200 g/l max. The following example illustrates the claimed invention. The example is illustrative only and is not to be regarded as limiting the scope of the invention. EXAMPLE Steels having the following composition (% by wt.) were prepared: Ref 1: C 0.017, Cr 25.59, Ni 7.30, Mo 3.88, W 1.00, Cu 1.72, N 0.272, Mn 0.53, P 0.021, S 0.001, Si 0.54. Ref 2: C 0.025, Cr 26.86, Ni 7.05, Mo 4.23, W 1.18, Cu 1.55, N 0.258, Mn 0.61, P 0.021, S 0.0016, Si 0.88 Ref 3: C 0.020, Cr 25.07, Ni 7.63, Mo 4.02, W 0.87, Cu 1.85, N 0.288, Mn 0.55, P 0.024, S 0.002, Si 0.70 and treated as follows: casting into ingots, forging into rods 180 mm in diameter, followed by heating to 1190°C and extrusion to form a pipe 88.9 mm in diameter and 6.45 mm in thickness, quenching in water from a temperature of 1060°C, final solubilization annealing at 1160°C for 12 minutes, and quenching in water from a temperature of 1050°C. The steel under Ref 2 underwent, by way of comparison, a different treatment, characterized by different solubilization annealing conditions (1240°C for 5 minutes), followed by quenching in water from a temperature of 900°C; said steel will be referred to as Ref 2a. The manufactures obtained were subjected to tests according to API standards, 5CT, sect. 5.2 and 5.3 for mechanical properties checking and to SSRT in an aggressive medium consisting of a 200 g/l NaCl aqueous solution at 80°C, saturated with H 2 S at a partial pressure of 100 mbar. Tests comparison gave some parameters, the most significant being the ductility ratio (ELR), i.e. the ratio of the elongation at break in an aggressive medium to the elongation at break in an inert medium (oil). At ELR of 0.90 min., the material is considered free from stress corrosion. The presence, if any, of secondary cracks (SCC) was also checked at the end of the test. Likewise, tests were conducted on known steels of the aforesaid types in accordance with UNS code, having the following compositions (% by wt.): 750: C 0.022, Cr 25.48, Ni 7.04, Mo 3.58, Cu 0.12, N 0.257, Mn 0.84, P 0.024, S 0.001, Si 0.45 550: C 0.020, Cr 25.20, Ni 6.48, Mo 3.46, Cu 1.64, N 0.240, Mn 1.26, P 0.020, S 0.001, Si 0.66 760: C 0.016, Cr 25.22, Ni 7.36, Mo 3.17, W 0.70, Cu 0.62, N 0.220, Mn 0.70, P 0.023, S 0.002, Si 0.47. The results obtained are shown in the following table: Rp 0.2 ksi (MPa) ELR SCC Ref 1 96 (661) 0.99 no Ref 2 97 (668) 0.97 no Ref 2a 88 (606) 0.74 yes Ref 3 94 (647) 0.97 no UNS 750 82 (565) 0.97 no UNS 550 82 (565) 0.92 no UNS 760 78 (537) 0.93 no As may be seen, a particular alloy composition combined with an adequate thermomechanical cycle, according to the present invention, give products showing tensile yield strengths higher by at least 14.6% than the corresponding values of known products as well as excellent stress corrosion resistance values. As proved by Ref 2a, the same results cannot be obtained if the heat treatment differed from the claimed one.

Claims: Claims for the following Contracting States : AT, BE, DE, ES, FR, GB, IT, SE Procedure for the production of steel manufactures characterised by the concurrent combination of the steps of: (i) preparing an ingot having the following composition (% by wt.): 0 ≤0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤1, P ≤0.03, S ≤0.005, Si ≤1, the balance being iron and inevitable impurities; (ii) first hot-working of same to obtain a semimanufactured product; (iii) heating of the semimanufactured product to a temperature of 1100°C to 1260°C and further hot-working of same by extrusion to obtain a manufacture in the desired final shape and size, which is quenched in water from a temperature of 950°C min.; (iv) annealing the product at a temperature between 1050°C and 1200°C for 1 to 30 minutes, and quenching in water to obtain a biphasic ferrite and austenite structure with ferrite fraction of 0.4 to 0.6 by vol. The procedure according to claim 1 wherein the first hot-working is carried out by techniques selected between forging and rolling. Procedure for the production of steel manufactures characterised by the concurrent combination of the steps of: preparing an ingot having the following composition (% by wt.): C ≤0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤1, P ≤0.03, S ≤0.005, Si ≤1, the balance being iron and inevitable impurities; forging into rods 130-250 mm in diameter, followed by annealing at a temperature of 1180°C to 1240°C, hot-working by extrusion or by rolling and quenching in water from a temperature of 1050°C to 1150°C, final annealing at a temperature of 1090°C to 1190°C, for 5 to 25 minutes, and quenching in water from a temperature of 1050°C min. The procedure according to claims 1 to 3 wherein the ingot composition (% by wt.) is in the following range: C ≤0.3, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W >1.2-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤0.03, S ≤0.005, Si ≤ 1. The procedure according to claims 1 to 3 wherein the manufactures are seamless pipes. Metal manufactures having the following composition (% by wt.) C ≤0.03, Cr 24.5-27, Ni6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2 5 N 0.25-0.30, Mn ≤1, P ≤0.03, S ≤0.005 Si ≤1 the balance being iron and inevitable impurities, said manufactures being characterized by a unit tensile strength at room temperature of 90 ksi (616.5 MPa) min and for which slow strength rate tests revealed no corrosion phenomena at 80°C in in 100 g/l sodium chloride solutions in the presence of a gas phase containing carbon dioxide at a partial pressure of 40 bar min and hydrogen sulphide at a partial pressure of 0.30 bar max. The manufactures according to claim 6 characterised by a unit tensile yield strength ranging between 90 ksi (616.5 MPa) and 110 ksi (753.5 MPa) at room temperature and decreasing by 15% at a temperature of 130°C. The manufactures according to claim 6 or 7 wherein slow strength rate tests revealed no corrosion phenomena at 110°C in media containing hydrogen sulphide at a partial pressure of 0.35 bar max., carbon dioxide at a partial pressure in the order of 40 bar min., and sodium chloride in the order of 50 g/l. The manufactures according to claim 6 or 7 wherein slow strength rate tests revealed no corrosion phenomena at 180°C, in media containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide at 0.30 bar max., in the presence of sodium cloride at a concentration of 200 g/l max. Seamless pipes having the following composition (% by wt.): C ≤0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤1, P ≤0.03, S ≤0.005, Si ≤1, the balance being iron and inevitable impurities. Seamless pipes having the following composition (% by wt.): C ≤0.025, Cr 24.5-26, Ni 7-8, Mo 3.8-4.2, W 0.8-1.2, Cu 1.5-2.0, N 0.25-0.30, Mn 0.5-0.7, P ≤0.03, S ≤0.003, Si ≤0.7, the balance being iron and inevitable impurities. The pipes according to claims 10 and 11 wherein the unit tensile yield strength at room temperature is 90 ksi (616.5 MPa) min. The pipes according to claims 10 and 11 wherein the unit tensile yield strength ranges between 90 ksi (616.5 MPa) and 110 ksi (753.5 MPa) and decreases by 15% at a temperature of 130°C. The pipes according to claims 10 and 11 wherein slow strength rate tests revealed no corrosion phenomena at 80°C in 100 g/l sodium chloride solutions in the presence of a gas phase containing carbon dioxide at a partial pressure 40 bar min. and hydrogen sulphide at a partial pressure of 0.30 bar max. The pipes according to claims 10 and 11 wherein slow strength rate tests revealed no corrosion phenomena at 110°C in media containing hydrogen sulphide at a partial pressure of 0.35 bar max., carbon dioxide at a partial pressure in the order of 40 bar min., and sodium chloride in the order of 50 g/l. The pipes according to claims 10 and 11 wherein slow strength rate tests revealed no corrosion phenomena at 180°C, in media containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide at 0.30 bar max., in the presence of sodium chloride at a concentration of 200 g/l max. Alloy having the following composition (% by wt.): C ≤0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W >1.2-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤1, P ≤0.03, S ≤0.005, Si ≤1, the balance being iron and inevitable impurities. Use of an alloy having the following composition (% by wt): C ≤0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W >1.2-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤1, P ≤0.03, S ≤0.005, Si ≤1, the balance being iron and inevitable impurities, for the production of hot-worked manufactures. The use according to claim 18 wherein the manufactures are hot-worked by forging, rolling, extrusion and combinations thereof. The use according to claims 18 to 19 for the production of seamless pipes. Claims for the following Contracting States : CH, LI, DK, GR, IE, LU MC, NL, PT Alloy having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-25; Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1, balance iron and inevitable impurities. Alloy having the following composition (% by wt.): C ≤ 0.025, Cr 24.5-26, Ni 7-8, Mo 3.8-4.2, W 0.8-1.2, Cu 1.5-2.0, N 0.25-0.30, Mn 0.5-0.7, P ≤ 0.03, S ≤ 0.003, Si ≤ 0.7 balance iron and inevitable impurities. Procedure for the production of steel manufactures characterized by the concurrent combination of the steps of: (i) preparing an ingot having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1, the balance being iron and inevitable impurities; (ii) first hot-working of same to obtain a semimanufactured product; (iii) heating of the semimanufactured product to a temperature of 1100°C to 1260°C and further hot-working of same by extrusion to obtain a manufacture in the desired final shape and size, which is quenched in water from a temperature of 950°C min.; (iv) annealing the product at a temperature between 1050°C and 1200°C for 1 to 30 minutes, and quenching in water to obtain a biphasic ferrite and austenite structure with ferrite fraction of 0.4 to 0.6 by vol. The procedure according to claim 3 wherein the first hot-working is carried out by techniques selected between forging and rolling. Procedure for the production of steel manufactures characterized by the concurrent combination of the steps of: preparing an ingot having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1, the balance being iron and inevitable impurities; forging into rods 130-250 mm in diameter, followed by annealing at a temperature of 1180°C to 1240°C, hot-working by extrusion or by rolling and quenching in water from a temperature of 1050°C to 1150°C, final annealing at a temperature of 1090°C to 1190°C, for 5 to 25 minutes, and quenching in water from a temperature of 1050°C min. The procedure according to claims 3 to 5 wherein the ingot composition (% by wt.) is in the following range: C ≤ 0.025, Cr 24.5-26, Ni 7.0-8.0, Mo 3.8-4.2, W 0.8-1.2, Cu 1.5-2.0, N 0.25-0.30, Mn 0.5-0.7, P ≤ 0.03, S ≤ 0.003, Si ≤ 0.7. The procedure according to claims 3 to 6 wherein the manufactures are seamless pipes. Use of an alloy having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5, Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1, the balance being iron and inevitable impurities, for the production of hot-worked manufactures. Use of an alloy having the following composition (% by wt.) C ≤ 0.025, Cr 24.5-26, Ni 7-8, Mo 3.8-4.2, W 0.8-1.2, Cu 1.5-2.0, N 0.25-0.30, Mn 0.5-0.7, P ≤ 0.03, S ≤ 0.003, Si ≤ 0.7, the balance being iron and inevitable impurities, for the production of hot-worked manufactures. The use according to claims 8 and 9 wherein the manufactures are hot-worked by forging, rolling, extrusion and combinations thereof. The use according to claims 8 to 10 for the production of seamless pipes. Metal manufactures having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9. Mo 3.5-4.5, W 0.7-2.5; Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1, the balance being iron and inevitable impurities. Metal manufactures having the following composition (% by wt.): C ≤ 0.025, Cr 24.5-26, Ni 7-8, Mo 3.8-4.2, W 0.8-1.2, Cu 1.5-2.0, N 0.25-0.30, Mn 0.5-0.7, P ≤ 0.03. S ≤ 0.003, Si ≤ 0.7, the balance being iron and inevitable impurities. The manufactures according to claims 12 and 13 wherein the unit tensile yield strength at room temperature is 90 ksi (616.5 MPa) min. The manufactures according to claims 12 and 13 wherein the unit tensile yield strength ranges between 90 ksi (616.5 MPa) and 110 ksi (753.5 MPa) at room temperature and decreases by 15% at a temperature of 130°C. The manufactures according to claims 12 and 13 wherein slow strength rate tests revealed no corrosion phenomena at 80°C in 100 g/l sodium chloride solutions in the presence of a gas phase containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide a partial pressure of 0.30 bar max. The manufactures according to claims 12 and 13 wherein slow strength rate tests revealed no corrosion phenomena at 110°C in media containing hydrogen sulphide at a partial pressure of 0.35 bar max., carbon dioxide at a partial pressure in the order of 40 bar min., and sodium chloride in the order of 50 g/l. The manufactures according to claims 12 and 13 wherein slow strength rate tests revealed no corrosion phenomena at 180°C, in media containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide at 0.30 bar max., in the presence of sodium chloride at a concentration of 200 g/l max. Seamless pipes having the following composition (% by wt.): C ≤ 0.03, Cr 24.5-27, Ni 6.5-9, Mo 3.5-4.5, W 0.7-2.5; Cu 1.5-2.5, N 0.25-0.30, Mn ≤ 1, P ≤ 0.03, S ≤ 0.005, Si ≤ 1, the balance being iron and inevitable impurities. Seamless pipes having the following composition (% by wt.): C ≤ 0.025, Cr 24.5-26, Ni 7-8. Mo 3.8-4.2, W 0.8-1.2, Cu 1.5-2.0, N 0.25-0.30, Mn 0.5-0.7, P ≤ 0.03, S ≤ 0.003, Si ≤ 0.7, the balance being iron and inevitable impurities. The pipes according to claims 19 and 20 wherein the unit tensile yield strength at room temperature is 90 ksi (616.5 MPa). The pipes according to claims 19 and 20 wherein the unit tensile yield strength ranges between 90 ksi (616.5 Mpa) and 110 ksi (753.5MPa) at room temperature and decreases by 15% at a temperature of 130°C. The pipes according to claims 19 and 20 wherein slow strength rate tests revealed no corrosion phenomena at 80°C in 100 g/l sodium chloride solutions in the presence of a gas phase containing carbon dioxide at a partial pressure 40 bar min. and hydrogen sulphide at a partial pressure of 0.30 bar max. The pipes according to claims 19 and 20 wherein slow strength rate tests revealed no corrosion phenomena at 110°C in media containing hydrogen sulphide at a partial pressure of 0.35 bar max., carbon dioxide at a partial pressure in the order of 40 bar min., and sodium chloride in the order of 50 g/l. The pipes according to claims 19 and 20 wherein slow strength rate tests revealed no corrosion phenomena at 180°C, in media containing carbon dioxide at a partial pressure of 40 bar min. and hydrogen sulphide at 0.30 bar max., in the presence of sodium chloride at a concentration of 200 g/l max.

Inventors: BARTERI MASSIMO, NEMBRINI IVAN, BARTERI, MASSIMO, NEMBRINI, IVAN
Applicants: DALMINE SPA, DALMINE S.P.A.
Application year: 1993
Main classification: C22C38
IPC codes: C21D8, E21B17, C22C38