METHOD FOR DISPERSION SPINNING OF SHEATHED ROD-IN-TUBE SUPERCONDUCTING COMPOSITES

Abstract: Methods of forming composite articles of superconducting materials and metal are disclosed. The composite articles are formed by applying a mixture of metal and binder to a ceramic oxide preform. The coated preform is heat treated to provide composite articles of superconducting ceramic and metal.

Description: HIL METHOD FOR DISPERSION SPINNING OF SHEATHED ROD-IN-TUBE SUPERCONDUCTING COMPOSITES FTE D OF THE INVENTION This invention is generally directed to manufacture of composite materials. More particularly, this invention is directed to manufacture of superconducting wires. BACKGROUND OF THE INVENTION High temperature superconductors, that is, superconductors that have a critical temperature on the order of 90°K, are disclosed by u et al., Phys. Rev. Lett. 58, 908-910 (1987). These high temperature superconductors are based on the Y-Ba-Cu-0 system. U.S. Patent 4,929,594 discloses a superconducting composition comprised of a crystalline phase of the formula Tl 2 B 2 CuOg +x , wherein x is from 0 to about 0.5, that has a temperature above 90°K. Subramanian et al.. Science 239, 1015-1017 (1988), disclose materials of the formula Bi2Sr3-_ x Ca_-.Cu2θ8-y which show a resistivity drop at about 116 β K and apparent zero resistivity at 91 β K. A wide variety of applications for superconducting materials has developed. These applications include power transmission and high-speed computer electronics. Superconductor materials have been used primarily in the form of sintered articles since elongated articles such as wire are difficult to form and have non-uniform properties. Known technologies of forming superconducting wire, ' as shown in U.S. Patent 4,980,964, employ powder-in-tube technology. This technology entails filling a metal tube with a powder of superconductive material, sealing the tube, and cold drawing the sealed metal tube until a predetermined wire size is achieved. The drawn wire is heat treated to assure crystallinity in the superconductor material. This technology, however, produces wire of short lengths and nonuniform properties. An improvement over powder-in-tube technology is described in European Patent Application publication number 0292 385. This publication describes manufacturing an elongated superconducting composite by kneading a mixture of powder of superconducting oxide with a binder while shaping the ' resulting kneaded paste into an elongated pre-form by an extruder or other device. The pre-form is heated continuously to remove the binder. The pre-form then is wrapped with a metallic sheet and sintered at elevated temperatures. While this method results in longer and somewhat more uniform superconducting wire, this method can change the phase content of the resulting sintered ceramic and thus sacrifice superconducting properties. European Patent Application 306,034 shows a method of forming superconducting ceramics which have a metal cladding thereon. In an embodiment, preforms of plastic compositions of polymer, plasticizer, and ceramic material are bonded prior to firing with a blend of meta.1, polymer and plasticizer to yield a metal clad sintered ceramic article upon firing. This method, however, is susceptible to undesirable leaching of materials between superconducting material and the metal coating. A need therefore exists for processes for manufacturing elongated superconducting ceramic, metal clad articles useful for wire application which provides increased lengths and uniformity, but which avoids the deficiencies of the prior art methods. SUMMARY OF THE INVENTION This invention provides a continuous process for forming elongated, superconducting composite articles ' that include superconducting materials in a metallic sheath. The method entails forming an elongated shaped article from a mixture of ceramic powder and organic binder solution. The elongated article is coated with a mixture of metallic powder and an organic binder solution that is different from the binder solution employed with the ceramic powder. The metal coated article is heated to burn off the organic binder and to crystallize the ceramic powder to form an elongated metal coated, superconducting composite article. DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic drawing of a spin cell employed to form ceramic fibers for subsequent coating with metal. Figure 2 is a schematic drawing of an apparatus for producing metal coated superconducting ceramic wire. Figure 3 is a schematic cross sectional view of a superconducting wire in accordance with this invention. DETAILED DESCRIPTION OF THE INVENTION Superconducting materials useful in the practice of this invention include ceramic materials that have a critical temperature (T c ) , that is, the temperature at which resistivity drops to substantially zero, of preferably more than about 77°K. Such materials are described, for example, in Song et al., J. Mater. Res., Vol. 5, No. 1, 27-32 (1990) and in Pierre et al., J. of Appl. Phys., £3., 2296-2303 (1990). Ceramic materials that have a T c >77°K include ceramic oxides from the Y-Ba-Cu-0 system including YιBa 2 Cu 3 θ; the Tl-Ba-Cu-O system such as Tl 2 Ba 2 CuOβ +x wherein x = 0 to 0.5; from the Bi-Sr-Ca-Cu-0 system such as Bi 2 Sr 3 _ x Ca x Cu 2 θ 8 - y where x = 0.4 to 0.9 and 0 < y < 1; and from the Bi-Pb-Sr-Ca-Cu-O system such as Biι.6Pbo.4Srι. 6 Ca2.oCu2.8θ9.2+x and Biι.8Pbo.4Sr2-oCa2.2Cu3.oOιo-3+x where x = 0.1 to 0.5. Generally, the superconducting wire material provided by the invention can be made by mixing a solution of organic binder with the superconducting ceramic material. The resulting mixture of superconducting ceramic and binder is shaped into preforms which are coated with a mixture of metal and a solution of binder to provide a superconducting ceramic- metal composite. The solvent employed in binder solutions of the mixture of metal and binder is distinct from the solvent employed in the binder used for the ceramic. Typically, either solution or vapor deposition methods may be employed to apply the metal coating to the ceramic metal composite. The metal coated ceramic is heat treated to remove organic binders to yield an elongated metal coated superconducting product. Generally, commercially available organic binders or mixtures thereof may be employed with both the ceramic and the metallic materials. Preferably, however, the organic binders employed burn off without yielding any residue. Organic binders useful to form superconducting ceramic, metal clad articles in accordance with this invention may include cellulose acetate, cellulose acetate butyrate, poly(vinyl alcohol), poly(ethylene oxide), poly(vinyl butyral) , pol (methyl methacrylic acid), pol (methyl methacrylate) , methyl cellulose, poly(isobutylene) , and poly(propylene carbonate), preferably polyethylene oxide; most preferably poly(propylene carbonate). Preferably, substantially the same organic binders are employed with both the ceramic.oxide and the metal powders. Different binders, however,, may be employed between the ceramic powder and the metal coating provided that the binders dissolve in different solvents. The amount of binder in the mixture of ceramic and binder, based on the total volume of the binder and ceramic material, but excluding any solvent, may vary from 20% to 80%. Preferably, the amount of binder can vary from 30% to 45% by volume. Similarly, the amount of binder in the mixture of binder and metal may vary from 20% to 80% by volume. Preferably, the volume percent of binder in the mixture of binder and metal may vary from 30% to 45%. In order to provide an intimate mixture of organic binder either with the ceramic or metal powder, the binder is mixed with an organic solvent that is at least a partial solvent for the binder. Solvents useful in this invention include both polar and nonpolar solvents. Useful solvents, therefore, include ethylene glycol, methyl ethyl ketone, cyclohexanone, acetone, ethyl acetate, methanol, glycerol and water, preferably, methyl ethyl ketone. Solvents employed for the organic binder that is admixed with the metal powder, however, are not solvents for the organic binder employed with the ceramic oxide. The solvent chosen should at least partially dissolve the binder, e.g., polar solvents should be employed for polar binders. Generally, surfactants may be incorporated with the mixture of solvent and binder which are employed with the ceramic and metal powders. Surfactants which may be employed in this invention include long chain organic acids, such as oleic acid, and polyacrylic acid, fatty acid esters, and fatty acid alkoxylates, preferably fatty acid alkoxylates. The metal powder employed to coat the ceramic preform may include ductile conducting metals. Suitable metals include silver, gold, platinum, copper, or mixtures thereof, preferably, silver. Composite articles of superconducting ceramic powder and organic binder which are coated with metal prior to heat treating readily can be formed by known techniques for manufacturing continuous ceramic fibers. See, for example, Weddell, J. Text * Inst., 1990, 81 No. 4, pp. 333-359. Preferably, the composite articles are manufactured in accordance with the method of Figure 1. Referring to Figure 1, a mixture 10 of ceramic powder and organic binder is placed into spin cell 20. Mixture 10 is pressed by piston 30 for extrusion through nozzle 40 to provide continuous elongated strip 50. Strip 50 can be collected by winding onto a spool or otherwise deposited in an elongated container (not shown) . Figure 2 illustrates an apparatus for performing " the process of the invention in a continuous manner. As shown in Figure 2, the ceramic organic binder mixture 10 is placed into spin cell 20 and extruded through nozzle 40 by piston 30 to provide at least one ceramic fiber 62. Fiber 62 is passed to coating unit 64 to apply a coating " of a mixture of metal and organic binder to fiber 62. Coating unit 64 can be any commercially available coating unit such as an electric wire coater or a fiber reinforced plastic tow prepreger made by Cincinnati Milicron. Generally, the coating of metal and organic binder may be applied to ceramic fiber 62 in a wide range of thicknesses provided that all the ceramic fibers 62 are coated. The thickness of metal coating may vary from 20 x 10~ 6 m to 2 x lO" 3 m, preferably, 2 x 10 -4 m. After the metal coating has been applied to fiber 62, the coated fiber is passed through oven 80 to burn off the organic binders, crystallize the ceramic, and to densify the metal coating. Generally, the heat treatment employed in oven 80 will vary with the specific ' composition of binder, ceramic material, and metal. Specific heat treatment temperatures, atmospheres, and times can readily be determined in accordance with well known procedures to provide the desired superconducting phase of the ceramic oxide material. The resultant, metal clad, superconducting ceramic fibers may be employed directly in applications such as magnets, powerlines, etc. Alternatively, the metal clad, superconducting fibers, may be passed through press rolls, plates, or dies 90 to further densify the fiber. In that event, the densified fibers then again are passed through a second oven 82 where they are further heat treated to enhance the current carrying capability of the fiber. The resulting fibers then may be collected by a collecting means such as spool 85 or a similar device. The metal coated, superconducting ceramic fibers of the invention can be formed into a variety of configurations where either a single fiber or a plurality of fibers of superconducting ceramic fibers are embedded in or are coated by metal. Fibers 62 can be round, elliptical or rectangular. Figure 3 shows a cross-sectional view of an article 100 wherein a plurality of ceramic fibers 62 are combined into a bundle that is coated by metal 68. The following non-limiting example illustrates the invention. EXAMPLE 1 PREPARATION OF MIXTURES OF CERAMICS AND BINDERS A mixture of ceramic oxide and binder is prepared as follows: In a first container, a dispersion of oxide powder is prepared by mixing 10 g of Bi1.6Pb0-4S 1.6Ca 2 . 0 Cu 2 . 8 0 powder in 50 ml of methyl ethyl ketone. Two drops of a commercially available surfactant. Sotex CW (Marton Chemical) is thoroughly mixed with the dispersion. In a second container, a solution of 1.4 g of poly(propylene carbonate) binder in 20 ml of methyl ethyl ketone is made. This solution is mixed with the dispersion of the oxide powder. The methyl ethyl ketone is partially evaporated by heating until the mixture forms a gummy paste. FORMING ELONGATED FIBERS The gummy paste formed above is inserted into a conventional stainless steel spin cell that has an inside diameter of 1/2 inch, as schematically shown in Figure 1. A piston is inserted into the spin cell to extrude the paste, and the spin cell is placed into a conventional spin unit. A spinneret is added to the spin cell to enable formation of fibers. The speed of the spin unit is adjusted to provide fibers from the spinneret. When spinnerets with openings of less than 1/8-inch diameter are employed, the extruded fibers are collected onto a 6-inch diameter bobbin. When larger hole size spinnerets are used, the extruded fibers may be collected onto a tray. In either case, the collected fibers are dried at room temperature. PREPARATION OF METAL COATED CERAMICS A silver paste for coating the ceramic fibers formed above is prepared by mixing 2.0 g of commercially available silver powder, 0.24 g of poly(ethylene oxide) of an average molecular weight of about 600,000, and 5 ml of methanol. The extruded ceramic fibers prepared above are uniformly coated with the silver paste by dipping the ceramic fibers in the silver paste and evaporating the solvent. HEAT TREATMENT ftNp FORMATION 0? METAL-COATED, COMPOSITE SUPERCONDUCTING WIRE The metal coated ceramic fibers prepared above are heated in air to remove the organic binder: starting at "25°C, the temperature is increased at the rate of 3°C per minute to 520°C, whereupon the temperature is raised to 580°C over 5 hours. The temperature then is lowered to 520°C over 5 hours and further reduced at 3°C per minute to 120°C. The heat treated material then is pressed between two metal plates to form a metal coated, composite superconducting ceramic wire. The heat treated and pressed wire then is recoated by dipping in a silver paste to seal any possible openings in the first silver coating. The recoated fiber again is heat treated in air under the low temperature cycle initially used to remove the organic binders. The resulting metal coated ceramic wire is again pressed as above. The resulting wire then is heated to drive off any remaining organic binder from the oxide powder and silver paste to form a silver coated superconducting ceramic of Bi1.6Pb0.4S 1.6Ca2.0Cu2.8O. The heat treatment is performed in an atmosphere of 7% oxygen and 93% nitrogen by increasing the temperature from 25° to 842°C at a rate of 3°C per minute and holding at 842°C for 25 hours. The temperature then is lowered to 120°C at 3°C per minute.

Claims: CLAIMS What is claimed is: 1. A method of manufacture of composite articles of ceramic bearing a metal coating comprising, forming a first mixture of ceramic powder and a first solution of organic binder into an elongated ceramic preform, coating said preform with a second mixture of metal and a second solution of organic binder that employs a solvent other than a solvent for the binder employed in said first solution of organic binder to provide a coated ceramic preform, and firing said coated ceramic preform to yield a composite article of ceramic bearing a uniform metal coating thereon. 2. The method of Claim 1 wherein said ceramic is a superconducting ceramic oxide selected from the group Biι.6Pbo.4Srι.6Ca2.oCu2.8θ9.2+x and Biι.8Pbo.4S 2.oCa2.2C 3.oOιo.3+ x , where x = 0.1 to 0.5, and said metal is selected from the group silver, gold, platinum, copper, or mixtures thereof. 3. The method of any one of Claims 1 or 2 wherein said organic binders are selected from the group cellulose acetate, cellulose acetate butyrate, pol (vinyl alcohol), poly(ethylene oxide), poly(vinyl butyral), poly(methyl methacrylic acid), poly(methyl methacrylate), methyl cellulose, poly(isobutylene) , and poly(propylene carbonate) . 4. The method of any one of Claims 1 or 2 wherein said firing is at a temperature of less than 850°C. 5. The method of Claim 3 wherein said ceramic is Bi .6P o.4Srι.6Ca2.oCu2.8θ9.2+χ where x = 0.1 to 0.5, and said metal is silver. 6. The method of Claim 3 wherein said ceramic is Biι.8Pbo.4Sr2.oCa2.2Cu3.oOιo.3+ where x = 0.1-0.5. 7. The method of Claim 5 wherein said composite article includes at least one ceramic preform. 8. The method of any one of Claims 1 or 2 wherein said organic binder is at least 10% by volume in each of said first and second mixtures. 9. The method of either Claim 5 or 6 wherein said metal is silver and said binder is poly(propylene carbonate) .

Inventors: ZAHR GEORGE ELIAS, ZAHR, GEORGE, ELIAS
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1993
Main classification: C04B35
IPC codes: C04B35, D01D5, D01F9, D06M11, D06M101, H01B13, H01L39