Colour cosmetic composition

Abstract: A powdered moulded colour cosmetic composition is provided that includes a talc having average particle size between 2 and 8 microns and a mica with an average particle size between 2 and 8 microns.

Description: The invention relates to a colour cosmetic composition in powder form. Moulded powder colour cosmetics in a major part consist of fillers and extenders. Most often they are of the mineral variety. Illustrative are talc, kaolin, mica and silicon dioxide. In more limited amount, the extenders or fillers may be organic polymers, including nylon and polyethylene. Often one or more of the aforementioned substances are blended together. These blends utilize relative proportions determined from consideration of skinfeel, spreadability, opacifying effect, mouldability and adherence. Typical of this technology are the disclosures found in US Patent 4,882,225 (Fukui et al) and Japanese Patent 62-49427 (Ohno et al). Despite advances in the art, there remains considerable room for improvement in the aesthetic and performance properties of moulded powder colour cosmetics. Accordingly it is an object of the invention to provide a pressed powder colour cosmetic composition which exhibits improved properties of skinfeel, spreadability, creaminess, adhesion to skin and smoothness. A further object of the invention is to provide a pressed powder cosmetic colour composition with good compression in manufacture. A still further object of the invention is to provide a pressed powder cosmetic colour composition that is neither too dusty nor brittle. These and other objects of the invention will become more apparent by consideration of the following summary, detailed description and examples. Thus, according to one aspect of the invention, there is provided a powder colour cosmetic composition suitable for topical application to the human skin, comprising a mixture of 1 to 95% by weight of talc and 1 to 95% by weight of mica, characterised in that: i) the talc has an average particle size of from 2 to 8 microns; and ii) the mica has an average particle size of from 2 to 8 microns. Now it has been found that an improved pressed powder colour cosmetic can be achieved that combines a talc and a mica, each of a particle size ranging from 2 to 8 microns. Good compressibility (hardness) and cushion (softening of the cake) is achieved with the combination. According to the present invention, the talc may have a hydrophobic or hydrophilic surface, the former being achieved through treatment with a silicone such as a methicone. Amounts of the talc in the composition may range anywhere from 1 to 95%, preferably between 30 to 70%, optimally between 40 and 60% by weight. Talc average particle size should range from 2 to 8 microns, optimally between 6 and 8 microns. The second essential component of this invention is a mica which may be selected from muscovite, phlogopite, tiotite, sericite, lepidolite, paragonite and artificial or synthetic mica having a fluorine atom substituted for the hydroxyl group of natural mica, as well as baked or calcined products thereof. These micas may be used alone or in any mixture thereof. Particularly preferred is a hydrophobic mica, wherein the mineral has been coated with a silicone compound such as cyclomethicone or dimethicone. Amounts of the mica may range anywhere from 1 to 95%, preferably between 30 and 70%, optimally between 40 and 60% by weight. Mica average particle size should range from 6 to 8 microns. In addition to the essential two components, there also may be present inorganic pigments, metal oxide and hydroxides, pearling pigments, organic pigments, mineral silicates, porous materials, carbons, metals, biopolymers and combinations thereof. Examples of inorganic pigments are ultramarine blue, Prussian blue, manganese violet and bismuth oxychloride. Examples of metal oxides and hydroxides useful in the present invention are magnesium oxide, magnesium hydroxide, magnesium carbonate, calcium oxide, calcium hydroxides, aluminum oxide, aluminum hydroxide, silica, iron oxides (α-Fe 2 O 3 , y-Fe 2 O 3 ,Fe 3 O 4 , FeO), iron hydroxides, titanium dioxide, titanium lower oxides, zirconium oxides, chromium oxides, chromium hydroxides, manganese oxides, cobalt oxides, nickel oxides and zinc oxides. These oxides and hydroxides may be used alone or in any mixture thereof. Furthermore, composite oxides and composite hydroxides such as iron titanate, cobalt titanate and cobalt aluminate can also be used in the present invention. Composite materials comprising metal oxides or hydroxides coated on the core materials (e.g. titanium oxides and iron oxides coated nylon) also can be used in the present invention. Examples of organic pigments suitable for the present invention are C.I. 15850, C.I. 15850:1, C.I. 15585:1, C.I. 15630, C.I. 15880:1, C.I. 73360, C.I. 12085, C.I. 15865:2, C.I. 12075, C.I. 21110, C.I. 21095, and C.I. 11680, C.I. 74160 and zirconium, barium or aluminum lakes of C.I. 45430, C.I. 45410, C.I. 45100, C.I. 17200, C.I. 45380, C.I. 45190, C.I. 14700, C.I. 15510, C.I. 19140, C.I. 15985, C.I. 45350, C.I. 47005, C.I. 42053 and C.I. 42090. The surfaces of these organic pigments may be treated with, for examples, resins. These organic pigments may be used alone or in any mixture thereof. Examples of pearling pigments (or nacreaous pigments) are bismuth oxychloride, guanine and titanium composite materials containing, as a titanium component, titanium dioxide, titanium lower oxides or titanium oxynitride. The titanium composite materials may be mixed with coloured pigments such as iron oxides, Prussian blue, chromium oxide, carbon black and carmine. These pearling pigments may be used alone, or in any mixture thereof. Examples of mineral silicates suitable for use in the present invention are phyllosilicates and tectosilicates such as pyrophyllite, chlorite, chrysotile, antigorite, lizardite. kaolinite, dickite, nacrite, halloysite, montmorillonite, nontronite, saponite, sauconite, and bentonite; natrolites such as natrolite, mesolite, scolecite, and thomsonite; heulandites such as heulandite, stilbite, epistibite; and zeolites such as analcite, harmotone, phillipsite, chabazite and gmelinite. These silicate minerals may be used alone or in combination thereof. The phyllosilicates may have organic cations at the interface of the layers thereof, or may be substituted with alkali metal or alkaline earth metal ions. The tectosilicates may include metallic ions in the fine pores thereof. Examples of porous materials suitable for use in the present invention are the above-mentioned silicate minerals; the above-mentioned metal oxides; KAl 2 (Al Si 3 )O 10 F 2 , KMg(Al, Si 3 )O 10 F 2 , and K(Mg, Fe 3 ) (Al, Si 3 )O 10 F 2 ; carbonate minerals such as CaCO 3 , MgCO 3 , FeCO 3 , MnCO 3 , ZnCO 3 , CaMg(CO 3 ) 2 , Cu(OH) 2 CO 3 , and Cu 3 (OH) 2 (CO 3 ) 2 ; sulfate minerals such as BaSO 4 , PbSO 4 , CaSO 4 , CaSO 4 ·2H 2 O, CaSO 4 ·5(H 2 O), Cu 4 SO 4 (OH) 6 , KAl 3 (OH) 6 (SO 4 ) 2 , and KFe 3 (OH) 6 (SO 4 ); phosphate minerals such as YPO 4 , (CeLa)PO 4 , Fe 3 (PO 4 ) 2 ·8H 2 O, Ca 5 (PO 4 ) 3 OH and Ca 5 (PO 4 CO 3 OH) 3 F,OH); and metal nitrides such as titanium nitride and chromium nitride. These materials may be used alone, or in any mixture thereof. Examples of metals suitable for the present invention are iron, cobalt, nickel, copper, zinc, aluminum, chromium, titanium, zirconium, molybdenum, silver, indium, tin, antimony, tungsten, platinum and gold, and the alloys thereof. Powdery biopolymer materials are also suitable for the present invention, especially by virtue of their high safety factor. Examples of biopolymer materials suitable for the present invention are keratin (hair, fur, feather, down, horn, hoof, etc.), fibroin (silk), collagen (skin, hide, leather, tendon, bond, etc.), cellulose, hemicellulose, pectin, chitin, chondroitin, peptide-glucan, nucleic acid (DNA, RNA) and the like. A variety of boron nitrides may also be employed. Average particle size for such material may range from about 0.1 to about 30 microns, preferably between about 3 and 7 microns. Amounts of the boron nitride may range from about 0.001 to about 30%, optimally between about 1 to 10% by weight. Any conventional cosmetic adjunct ingredients can be used together with the powder materials. Typical examples of such ingredients include various hydrocarbons such as squalane, liquid paraffin, and microcrystalline wax; emollient acids and alcohols such as caprylic acid, myristic acid, palmitic acid, stearic acid, oleic acid, isostearic acid, cetyl alcohol, hexadecyl alcohol and oleyl alcohol; emollient esters such as caprylate esters, cetyl-2-ethylhexanoate, ethylhexyl palmitate, 2-octyldodecyl myristate, 2-octyldodecyl gum ester, neopentyl glycol-2-ethylhexanoate, isooctyl triglyceride, 2-octyldodecyl oleate, isopropyl myristate, isostearic acid triglycerides, coconut oil fatty acid triglyceride, olive oil, avocado oil, beeswax, myristyl myristate, mink oil, lanolin and dimethyl polysiloxane; resins such as alkyd resins and urea resins; plasticizers such as camphor and acetyl tributyl citrate; UV absorbers; antioxidants; preservatives; surfactants; humectants; perfumes; water; alcohols and thickening agents. Among the preservatives useful for the present invention are phenoxyethanol, ethyl paraben, isobutyl paraben, n-butyl paraben, methyl paraben, propyl paraben, sodium dehydroacetate and combinations thereof. The amount of preservative may range from about 0.01 to about 5%, preferably between about 0.10 and 2%, optimally between about 0.4 and 1% by weight. Various herbal extracts may also be employed. Examples of these extracts are rosemary, althea, sambucus, matricaria and combinations thereof. Levels of the extract may range from 0.0001 to about 10%, preferably about 0.1 to about 2% by weight. Compositions of the present invention advantageously will have all components of a similar average particle size, preferably between about 1 and about 8 microns, optimally between 2 and 7 microns. Uniformity of particle size may either be achieved by separately combining components of the proper size or by shear mixing the total composition down to the desired particle size range. A jet mill is particularly useful for purposes of shearing the total composition. The following Examples will more fully illustrate the embodiments of the present invention. All parts, percentages and proportions referred to herein and in the appended claims are by weight unless otherwise indicated. Example 1 An eye shadow formula according to the present invention which has been jet milled is outlined under Table I. Chemical or CTFA Name Weight % Hydrophobic Talc 40 Hydrophobic Mica 40 Silica Beads 3.8-5 Zinc Stearate 0-6 Nylon 12 2-4 Boron Nitride 5.00 Methyl Paraben 0.20 Propyl Paraben 0.10 Sodium Dehydroacetate 0.20 Bismuth Oxychloride 0-10 Matricaria Extract 0-1 Rosemary Extract 0-1 Althea Extract 0-1 Sambucus Extract 0-1 Octyl palmitate 0-5 Pentaerythritol tetra(2-ethyl hexanoate) 0-5 Dimethicone 0-5 Colorants 1-30 Colorants listed below will vary in percentages due to shade. The colorant can range from 1 to 30% depending upon the shade. Carmine C.I. 75470 Chromium Oxide, Hydrous Green C.I. 77289 Chromium Oxide, Anhydrous Green C.I. 77288 Ultramarine Rose C.I. 77007 Brown Iron Oxide C.I. 77491, 2, 9 Red Iron Oxide C.I. 77491 Russet Iron Oxide C.I. 77491 Yellow Iron Oxide C.I. 77492 Black Iron Oxide C.I. 77499 Manganese Violet C.I. 77742 Ultramarine Blue C.I. 7707 Titanium Dioxide C.I. 77891 Prussian Blue C.I. 77510 Pearl Substrate: Mica and/or TiO 2 ; Carmine; Iron Oxides; Ferric Ferrocyanide; Ultramarine Rose; Manganese Violet; Chromium Oxide Hydrous/Anhydrous Green; Ferrocyanide; Bismuth Oxychloride. Example 2 A blush formula according to the present invention which has been jet milled is outlined under Table II. Chemical or CTFA Name Weight % Talc BC 36 Mica 36 Mica & Silicon Dioxide 4.00 Bismuth Oxychloride 2.00 Magnesium Myristate 2.00 Boron nitride 5.00 Methyl paraben 0.20 Propyl paraben 0.10 Sodium Dehydroacetate 0.20 Dimethicone 1.25-2.25 Pentaerythritol tetra(2-ethyl hexanoate) 1.25-2.25 Octyl palmitate 1.25-2.25 Colorants 8-10 Colorants listed below will vary in percentages due to shade. The colorant can range from 1 to 10% depending upon the shade. Total pigment level of blusher is approximately 8 to 10%. D&C Red 7 C.I. 15850:1 D&C Yellow 5 C.I. 19140:1 D&C Red 30 C.I. 73360 D&C Red 6 C.I. 15850 D&C Orange 4 C.I. 15510 Carmine C.I. 75470 Chromium Oxide, Hydrous Green C.I. 77289 Chromium Oxide, Anhydrous Green C.I. 77288 Ultramarine Rose C.I. 77007 Brown Iron Oxide C.I. 77491, 2, 9 Red Iron Oxide C.I. 77491 Russet Iron Oxide C.I. 77491 Yellow Iron Oxide C.I. 77492 Black Iron Oxide C.I. 77499 Manganese Violet C.I. 77742 Ultramarine Blue C.I. 7707 Titanium Dioxide C.I. 77891 Prussian Blue C.I. 77510 Pearl Substrate: Mica and/or TiO 2 ; Carmine; Iron Oxides; Ferric Ferrocyanide; Ultramarine Rose; Manganese Violet; Chromium Oxide Hydrous/Anhydrous Green; Ferrocyanide; Bismuth Oxychloride. Example 3 A set of experiments were conducted to demonstrate criticality of particle size with respect to the talc and mica. Table III lists the formulation components. The binder is an approximately equal weight mixture of octyl palmitate, pentaerythritol tetra(2-ethyl hexanoate) and dimethicone. Component A B C D E F Talc (2-8 micron) 47.5 95.0 - - 47.5 47.5 Talc (10-15 micron) - - - 47.5 - 47.5 Mica (2-8 micron) 47.5 - 95.0 - - 47.5 Mica (15-30 micron) - - - 47.5 47.5 - Binder 3.0 3.0 3.0 3.0 3.0 3.0 Red Iron Oxide (50%) 2.0 2.0 2.0 2.0 2.0 2.0 Samples A-F were filled into respective pans. These were compressed at 56.25 kg/cm 2 (800 psi) down to a set fill line. Each pan had thus a uniform volume and ranged in weight from 2.4 to 3.4 grams. The resultant cakes were measured by a penetrometer. Three penetrometer determinations were conducted on each sample and the values averaged. Ordinarily, the penetrometer values will be acceptable when ranging from 7 to 15. Values less than 7 indicate an unacceptable brick-like cake. Values greater than 15 indicate cakes that are too soft and provide too much payoff when rubbed with a brush. The Drop Test was utilized as measure of the brittleness of each sample. Pass or fail indications were given for each. Performance Properties A B C D E F Penetrometer (mm) 11.2 4.2 17.7 27.5 17.8 14.3 Drop Test Passed Passed Failed Failed Failed Failed Samples C, D and E had penetrometer values outside the acceptable range. Each of these also failed the Drop Test. Although Sample F was just within the acceptable penetrometer values, this Sample also failed the Drop Test. Sample B had an unacceptable penetrometer value of 4.2. Only Sample A of the Series tested had both an acceptable penetrometer value and passed the Drop Test. These results indicate that a combination of ultrafine talc and ultrafine mica provide a much better cosmetic cake than either material alone or any combination not having an ultrafine particle size. The foregoing description and examples illustrate selected embodiments of the present invention.

Claims: A powder colour cosmetic composition suitable for topical application to the human skin, comprising a mixture of 1 to 95% by weight of talc and 1 to 95% by weight of mica, characterised in that i) the talc has an average particle size of from 2 to 8 microns; and ii) the mica has an average particle size of from 6 to 8 microns. A composition according to claim 1 wherein the talc has an average particle size of from 6 to 8 microns. A composition according to any of the preceding claims, wherein the mica is muscovite, phlogopite, tiotite, sericite, lepidolite, paragonite, artificial or synthetic mica having a fluorine atom substituted for the hydroxyl group of natural mica, baked or calcined products of the aforementioned micas, or mixtures thereof. A composition according to any of the preceding claims wherein the mica is a hydrophobic mica. A composition according to claim 4 wherein the mica has been coated with a silicone. A method of making a powder colour cosmetic composition, comprising compressing a mixture comprising from 1-95% by weight of a talc having an average particle size of from 2 to 8 microns and from 1-95% by weight of a mica having an average particle size of from 6 to 8 microns, in an appropriate container.

Inventors: HECCHAVARIA CARIDAD, HECCHAVARIA, CARIDAD
Applicants: UNILEVER NV, UNILEVER PLC, UNILEVER N.V.
Application year: 1993
Main classification: A61K7
IPC codes: A61Q1, A61K8