Catalytic system and process for copolymerizing carbon monoxide with one or more olefins

Abstract: A catalyst active in the preparation of alternating olefin/carbon monoxide (CO) copolymers is constituted by: (a) at least one salt of a metal of Group IB of the Periodic System, (b) a mono or bidentate ligand base containing one or two nitrogen or phosphorus atoms capable of linking to the metal atom by means of dative bonds, (c) a mineral or organic oxidizer agent. Also disclosed are the preparation of the catalyst and the use of said catalyst in alternated copolymerization of ethylene (C2) and/or other olefins with carbon monoxide (CO).

Description: The present invention relates to a homogeneous, Cu-based catalyst, to its preparation and to its use in the copolymerization of ethylene (C2) and/or other olefins with carbon monoxide (CO) in order to produce alternated copolymers with regular morphology. From the prior art, catalytic systems capable of yielding alternating C2/CO polymers are known and widely described. Most of them are catalytic systems based on metals belonging to Group VIII of the Periodic System. So, for example, U.S. patent 3,984,388 discloses the use of nickel cyanide as polymerization catalyst for C2/CO mixtures. Other non-patent references [Makromol. Chem., 161 , 1741 (1968)] disclose the possible use of cobalt carbonyls. A large number of patents disclose, on the contrary, the use of catalytic system based on Pd salts, or salts of other metals belonging to Group VIII of the Periodic System and containing a bidentate ligands capable of binding to the metal atom through dative bonds; such catalytic systems are capable of copolymerizing ethylene (C2) and/or other compounds containing unsaturations of olefinic type with carbon monoxide (CO), yielding alternating copolymers, either in solution or in suspension, and in the presence of a mineral and/or organic acid. So, for example, in U.K. Patent No. 1,081,304 there is disclosed the solution polymerization of monomeric mixtures of C2 and CO in order to yield alternating copolymers by means of the use of an alkyl phosphinic complex of a Pd salt, and U.S. Patent No. 3,689,460 claims a catalyst based on a tetrakis-phosphinic palladium complex. Analogous catalytic systems are disclosed in U.S. Patent No. 3,694,412. Other catalytic systems known from the prior art, capable of yielding alternating C2-CO copolymers, are constituted by: (1) a palladium, nickel or cobalt salt of a preferably carboxy acid, (2) a bidentate base, generally constituted by an alkyl or cycloalkyl hydrocarbon symmetrically substituted with two dialkyl-or diphenyl phosphinic moieties or with two moieties containing at least one nitrogen atom, and (3) an anion of an acid, preferably an organic acid, with a pKa value of approximately 2. Such catalytic systems are disclosed, e.g., in EP Patent Nos. 0 121 965, 0 222 454, 0 257 663, 0 305 012 and make it possible alternating C2/CO polymers to be obtained with good yields. Some modifications of the above approach consist in adding to the catalytic systems a fourth component selected from compounds belonging to the groups of quinones, organic oxidizers and aromatic nitrocompounds, according to as claimed, e.g., in European Patents EP No. 239 145 and EP No. 245 893, and so forth, or in the use of bidentate bases with both heteroatoms constituted by nitrogen, or mixed heteroatoms P and S, such as disclosed, e.g., in European Patents EP No. 245 893 and EP No. 343 734. The present Applicant has now unexpectedly found that alternating copolymers of carbon monoxide with an olefin or a mixture of olefins, such as ethylene (C2), propylene, butene and/or higher omologues, can be prepared in the presence of a salt of a metal belonging to Group IB of the Periodic System; such a Group comprises copper, silver and gold. In accordance therewith and according to a first aspect, the present invention relates to a homogeneous catalytic system active in the preparation of alternating copolymers of olefins with carbon monoxide (CO), constituted by: (a) at least one salt of a metal of Group IB of the Periodic System, (b) a bidentate chelating base containing two phosphorus or nitrogen atoms, capable of binding to Cu, Ag or Au atom through dative bonds, (c) an organic or inorganic oxidizer. The present invention relates also, and this is a second aspect of the invention, to the use of such a catalytic system in the alternating copolymerization of ethylene (C2) and/or other olefins with carbon monoxide (CO). The copper, silver or gold salts which can be used as the component (a) of the catalytic system of the present invention generally are inorganic, organic or organometallic salts which are soluble in such common organic salts as, e.g., methanol, toluene and dimethoxyethane; the solvents are better detailed in the following. Examples of Cu, Ag or Au salts for the purposes of the present invention are trifluoromethane sulfonate, trifluoroacetate, acetate, tosylate, sulfate, chloride, diethyl carbamate and hexafluorophosphate. The bidentate chelating bases suitable as the component (b) of the catalytic system of the present invention are compounds which contain two heteroatoms, such as two phosphorus or nitrogen atoms capable of linking to the Cu, Ag or Au atom through dative bonds and correspond to the general formula (I) R 1 R 2 -M-R-M-R 3 R 4 in which: M represents a phosphorus or nitrogen atom, R stands for a polymethylene radical containing from 2 to 4 carbon atoms, a cycloalkylidene radical containing from 2 to 10 carbon atoms, an orthophenylene radical, R 1 , R 2 , R 3 , and R 4 , which are the same or may be different from each other, represent an alkyl radical of from 1 to 6 carbon atoms, a cycloalkyl radical of from 3 to 6 carbon atoms, an aromatic radical of from 6 to 12 carbon atoms, possibly with substituents. Inasmuch as, the bidentate chelating agent can form a complex with the metal atom through its two heteroatoms, the total number of atoms which constitute the complex ring should preferably be not higher than 7, that means that the total number of carbon atoms in the polymethylene radical R should preferably not exceed 4; if, on the contrary, R is constituted by a cycloalkylidene radical, the latter will preferably carry both its chelating atoms bound to two adjacent atoms in the ring. Basing on the above, examples of bidentate chelating bases containing two phosphorus atoms are: 1,3-bis(diphenylphosphino)propane, 1,4-bis(dicyclohexylphosphino)butane and 1,2-bis(diphenylphosphino)cyclohexane; other bidentate bases containing two nitrogen atoms, which do not belong to the group of chelating compounds which can be represented by the general formula (I), but which can be used in order to form the catalytic systems of the present invention are 1,10-phenanthroline, 3-methyl-1,10-phenanthroline, 2,2'-bipyridyl and 4,4'-dimethyl-2,2'-bipyridyl. The component (c) of the catalytic system of the present invention is, as said above, an inorganic oxidizer agent, such as, e.g., nitrosonium tetrafluoroborate (NOBF 4 ), or an organic oxidizer agent, such as, e.g., parabenzoquinone. The end catalytic system is obtained by adding to a solution of the component (a) in a suitable solvent, the other two components of the catalytic system, i.e., respectively, the component (b), i.e., the bidentate base, and the component (c), i.e., the organic or inorganic oxidizer agent; the addition is carried out at room temperature and under an inert atmosphere. The resulting solution is then ready for use in the synthesis of the alternating polymers. The homogeneous catalyst is preferably obtained by adding to a solution of Cu(CH 3 COO) 2 in methanol a bidentate ligand containing two phosphorus atoms, for example, 1,3-bis(diphenylphosphino)propane (DPPP), and then an oxidizer agent, such as nitrosonium fluoroborate (NOBF 4 ) or p-benzoquinone. An also preferred embodiment of the present invention is the homogeneous catalyst which is obtained by adding to a solution of silver trifluoromethanesulfonate (CF 3 SO 3 Ag) in methanol a bidentate ligand containing two phosphorus atoms, e.g., 1,3-bis(diphenylphosphino)propane, and then an oxidizer agent, such as nitrosonium fluoroborate or p-benzoquinone. The molecular ratio of the copper or silver or gold salt to the bidentate ligand to be added to the reaction media may vary within a wide range, even if the preferred ratio is rather close to the stoichiometric values; in the preferred case when the component (b) is constituted by a bis(diphenylphosphino)alkane, such as, e.g., 1,3-bis(diphenylphosphino)propane, such a ratio is generally comprised within the range of from of 1 : 1 to 1 : 4 mols of salt : mol of bidentate base; a ratio of 1 : 1 is anyway preferred. The component (c) constituted, as said above, by an organic or inorganic oxidizer agent, is added to the reaction media in such an amount that its molar ratio to the copper salt is comprised within the range of from 2 to 40 mols of oxidizer agent per mol of salt. As the solvents in the reaction of formation of the catalytic complex of the present invention, there may be used aliphatic and aromatic hydrocarbons, the blends of mixed aromatic-aliphatic solvents, hydroxylated solvents, such as alcohols and glycols, linear or cyclic ethers, such as, e.g., diethyl ether, dimethoxyethane and tetrahydrofuran; the selection of the most suitable solvent is carried out from time to time by taking into consideration the solubility of the Cu, Ag or Au salt and of the bidentate compound with no prejudice for the activity of the end catalytic system. An objective advantage of the present invention resides in that the catalytic system is characterized by a considerable flexibility and requires materials which are easily available from the market and/or can be easily prepared, with a considerable simplification of the production process; in fact, both the copper and silver salts, which constitute the component (a) of the catalytic system according to the present invention, and the bidentate base (b), as well as the oxidizer agent (c), are relatively cheap, commercially available and easily synthetized products. Furthermore, preparing the catalytic system of the invention only requires, as said above, simply mixing the components in the selected solvent and adding the mixture to the polymerization reaction. As an alternative, the preparation of the catalytic system according to the above reported modalities can be directly carried out inside the polymerization reactor and before charging the monomers. By carrying out the copolymerization of CO with one or more monomers containing olefinic unsaturations and in the presence of the homogeneous catalyst according to the present invention, alternating CO/olefin copolymers are obtained with high yields, as reported in the following examples. The exact alternation of the copolymer obtained according to the present invention was verified by using a spectroscopic system described in the literature and precisely in "Application of Polymer Spectroscopy" published by Academic Press (1978), at page 19. The reaction of polymerization of the monomers, i.e., the olefinic component, or the mixture of a plurality of olefins and respectively carbon monoxide, is carried out inside a sealed reactor, previously purged with nitrogen, by adding the solvent, the components of the catalytic system, or a solution of the previously prepared catalytic system, and the monomers; then the polymerization is carried out at a temperature comprised within the range of from 50 to 120°C, under a pressure comprised within the range of from 40*10 5 to 100*10 5 Pa and for a reaction time comprised within the range of from 3 to 9 hours. The polymerization solvent can be of alcohol, ether, hydrocarbon types, or a mixture of two or more solvents belonging to the above said categories, and the amount of catalyst, expressed as gram-atoms of metal (Cu, Ag or Au) per each litre of solvent, is comprised within the range of from 10 -2 to 10 -5 and the other components of the catalytic system, i.e., the component (b) and (c) respectively, are used in the above mentioned molar ratios. The polymerization reaction is preferably carried out in an alcoholic solvent, containing the catalytic system, with 1 : 1 molar CO/olefin mixtures, under pressures of 50*10 5 -60*10 5 Pa, temperatures comprised within the range of from 70 to 90°C, and for a polymerization time comprised within the range of from 4 to 6 hours. The olefinic monomers, which may be used as single monomers or as mixtures of two or more monomers and together with carbon monoxide, are alpha-olefins, such as ethylene, propylene, butene-1, pentene-1, and so forth, cyclopentene and styrene; the preferred monomer is ethylene (C2), and the preferred mixture is ethylene with propylene. The possibility of being capable of using different olefins, either as a single olefin or simultaneously as olefin blends, in order to produce the copolymers of olefins with carbon monoxide, constitutes a further advantage of the present invention. In such a way, an alternating copolymer can be obtained, the properties of which, such as, e.g., its melting temperature, its glass transition temperature (Tg) and its processability, can be modulated. The general aspects of the instant invention having been disclosed, the following specific examples are supplied now for the only purpose of illustrating some details of the same invention . All the compositions and percent values reported are by weight unless differently specified. Example 1 500 cm 3 of methanol are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Cu (CH 3 COO) 2 , 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 10 mmol of NOBF 4 are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 7 g of copolymer is obtained. Example 2 500 cm 3 of methanol are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Cu(CF 3 COO) 2 , 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 10 mmol of NOBF 4 are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 80°C and with a vacuum of 10 2 Pa. 8 g of copolymer is obtained. Example 3 500 cm 3 of methanol are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Cu(SO 3 CF 3 ) 2 , 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 20 mmol of parabenzoquinone are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 10 g of copolymer is obtained. Example 4 500 cm 3 of methanol are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Cu(CF 3 COO) 2 , 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 20 mmol of para-benzoquinone are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 80°C and with a vacuum of 10 2 Pa. 12 g of copolymer is obtained. Example 5 300 cm 3 of methanol and 200 cm 3 of toluene are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Ag(SO 3 CF 3 ), 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 10 mmol of NOBF 4 are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 4 g of copolymer is obtained. Example 6 500 cm 3 of methanol are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Ag(SO 3 CF 3 ), 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 10 mmol of nitrosonium tetrafluoroborate are added. Then a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 2 g of copolymer is obtained. Example 7 300 cm 3 of methanol and 200 cm 3 of toluene are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Ag(CH 3 COO), 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 10 mmol of nitrosonium tetrafluoroborate are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 4 g of copolymer is obtained. Example 8 300 cm 3 of methanol and 200 cm 3 of toluene are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Ag(SO 3 CF 3 ), 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 20 mmol of benzoquinone are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 6 g of copolymer is obtained. Example 9 500 cm 3 of methanol are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Ag(CH 3 COO), 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 40 mmol of benzoquinone are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 4 g of copolymer is obtained. Example 10 300 cm 3 of methanol and 200 cm 3 of toluene are charged to an autoclave of 2 litres of capacity, previously purged with nitrogen. 0.5 mmol of Ag(CH 3 COO), 0.5 mmol of 1,3-bis(diphenylphosphino)propane (DPPP) and 20 mmol of benzoquinone are added. Then, a mixture of ethylene/CO in the ratio of 1 : 1 by mol is added until a pressure of 56*10 5 Pa is reached. After 5 hours of reaction at 80°C, the autoclave is cooled down to room temperature and the residual pressure is vented. The copolymer is filtered, is washed with methanol, and is dried at a temperature of approximately 60°C and with a vacuum of 10 2 Pa. 4 g of copolymer is obtained.

Claims: Homogeneous catalytic system active in the preparation of alternating copolymers of olefins with carbon monoxide (CO), consisting of: (a) at least one salt of a metal of Group IB of the Periodic System, (b) a bidentate chelating base containing two phosphorus or nitrogen atoms, (c) an inorganic or organic oxidizer agent. Catalytic system according to claim 1, characterized in that the salt of metal of Group IB is selected from trifluoromethanesulfonate, trifluoroacetate, acetate, tosylate, sulfate, chloride, hexafluorophosphate and diethylcarbamate. Catalytic system according to claim 1, characterized in that the bidentate chelating base falls within the group of compounds having the general formula R 1 R 2 -M-R-M-R 3 R 4 in which: M represents a phosphorus or nitrogen atom, R stands for a polymethylene radical containing from 2 to 4 carbon atoms, a cycloalkylidene radical containing from 2 to 10 carbon atoms, a phenylene radical, R 1 , R 2 , R 3 , and R 4 , which are the same or may be different from each other, represent an alkyl radical of from 1 to 6 carbon atoms, a cycloalkyl radical of from 3 to 6 carbon atoms, an aromatic radical of from 6 to 12 carbon atoms. Catalytic system according to claim 1, characterized in that said bidentate chelating base is a compound selected from the group consisting of 1,3-bis(diphenylphosphino)propane, 1,4-bis(dicyclohexylphosphino)butane and 1,2-bis(diphenylphosphino)cyclohexane. Catalytic system according to claim 1, characterized in that said bidentate chelating base is 2,2'-bipyridyl. Catalytic system according to claim 1, characterized in that said bidentate chelating base is 4,4'-dimethyl-2,2'-bipyridyl. Catalytic system according to claim 1, characterized in that said bidentate chelating base selected from the group consisting of 1,10-phenanthroline and 3-methyl-1,10-phenanthroline. Catalytic system according to claim 1, characterized in that the inorganic oxidizer agent is nitrosonium tetrafluoroborate NOBF 4 . Catalytic system according to claim 1, characterized in that the organic oxidizer agent is para-benzoquinone. Process for preparing the catalytic system according to claim 1, characterized in that: (i) the copper, Ag or Au salt is dissolved in a suitable solvent, (ii) the component (b), i.e., the bidentate ligand base, is added to the resulting solution, (iii) the component (c), i.e. the organic or inorganic oxidizer agent is added to the resulting solution. Process according to claim 10, characterized in that such an amount of bidentate ligand base (b) is used that the molar ratio of the salt of Cu, Ag or Au to the ligand base, is within the range of from 1 : 1 to 1 : 4, and preferably is 1. Process according to claim 10, characterized in that the molar ratio of the component (c) to the salt of copper, silver or gold is within the range of from 2 to 40 and preferably is 20. Process for copolymerizing ethylene (C2) and/or other olefinic monomers, either as single monomers or as mixtures of two or more monomers, with carbon monoxide (CO) in order to produce alternating olefin/CO copolymers, characterized in that as the polymerization catalyst, the catalytic system according to claims from 1 to 9 is used. Process according to claim 13, characterized in that said olefinic monomers which can be used either as single monomers or as mixtures of two or more monomers and together with carbon monoxide are alpha-olefins such as ethylene, propylene, butene-1, pentene-1, cyclopentene, styrene. Process according to claim 13, characterized in that the reaction of copolymerization of the monomers, i.e., respectively the olefinic component, or the mixture of a plurality of olefins, and carbon monoxide is carried out in a sealed reactor to which the solvent, the components of the catalytic system and the monomers, are preliminarily charged, at a temperature within the range of from 50 to 120°C, under a pressure within the range of from 40x10 5 Pa to 100x10 5 Pa, and for a polymerization time within the range of from 3 to 9 hours. Process according to claim 8, characterized in that the catalyst amount is such that to the reactor from 10 -2 to 10 -5 gram-atoms of the metal of Group IB of the Periodic System are charged per each solvent litre charged to the same reactor.

Inventors: CALDERAZZO FAUSTO, GARBASSI FABIO, LUGLI GABRIELE, SOMMAZZI ANNA, CALDERAZZO, FAUSTO, GARBASSI, FABIO, LUGLI, GABRIELE, SOMMAZZI, ANNA
Applicants: ENICHEM SPA, ENICHEM S.P.A.
Application year: 1993
Main classification: C08G67
IPC codes: C08G67