Anisotropic film laminate

Abstract: The anisotropic film laminate comprises a continuous elastomeric core layer (3) and at least one continuous inelastic skin layer (2,4) of a uniaxially oriented thermoplastic film layer. The film laminate is substantially inelastic in a direction of orientation of said at least one skin layer, and said skin layer is unoriented in a direction transverse to said direction of orientation such that the laminate is extensible in said transverse direction.

Description: The invention concerns anisotropic films and more specifically concerns an improved anisotropic laminate. Elastomeric films have for some time been used and discussed in the literature with regard to their applications in disposable products, such as baby diapers and adult incontinent devices. These elastomeric webs or films are used primarily in the body hugging portions of garments. Many of these elastics are temperature-treated to provide for controlled elastic recovery. In diapers, for example, elastomeric bands are typically used in the waistband portions such as discussed in US-A-4,681,580 and US-A-4,710,189. Both of these patents describe the use of elastomeric materials which have a heat stable and a heat unstable form. The heat unstable form is created by stretching the material when heated around its crystalline or second phase transition temperature followed by a rapid quenching to freeze in the heat unstable extended form. The heat unstable elastomeric film can then be applied to the, e.g., diaper and then heated to its heat stable elastomeric form. US-A- 3,694,815, proposed a method for attaching a stretched relaxed elastic ribbon to a garment by stretching conventional elastic ribbons and immediately freezing the elastomeric material at relatively extreme low temperatures (e.g., well below ambient). GB-2190406 A proposed maintaining a conventional elastomer in a stretched condition, while attaching it to the member to be shirred (e.g., a diaper), by a rigidifying member, which would then be removed or destroyed following the attachment procedure. As described, the elastomers are first stretched then applied to the rigidifying member in its stretched form. GB-B-2,160,473, proposes an elastomer which will shrink at an elevated temperature (e.g., at or above 175°F or 79.4°C). The allegedly novel feature of this material, compared to the heat shrink materials discussed above, is that it does not require preheating or cold treatment during the stretching operation but rather could be stretched at ambient temperatures by a differential speed roll process or by "cold rolling". The polymer proposed was a copolymer having alternating segments of polyamidepolyether block polymers, commercially available under the trade name Pebax, particularly Pebax Extrusion grades 2533 and 3533. Problems with these elastomeric films include the difficulties inherent in applying a stretched elastic film to a flexible substrate such as a disposable diaper. For example, these film elastics, after being attached to a flexible substrate, such as by adhesives, will place shear stresses on the attachment areas. This can result in the elastic detaching from the flexible substrate, particularly after repeated elongations. EP-A-500 590 discloses an elastomeric laminate having at least one elastomeric layer and at least one skin layer which addresses some of the above-noted problems in the art. Despite the numerous advantages in the materials of EP-A-500 590 there is room for improvement for some applications. In order to activate the honelastomeric laminate into a state that will allow it to recover and become elastomeric, the laminate must be stretched a substantial amount, for many materials contemplated as useful for the skin and core layers. Further, when the elastic is applied to a garment, equally high stretch ratios are generally required to provide sufficient elastic force to functionally elasticize the garment. This is problematic for applications where low elastic stretch ratios would be desirable, for example, when high levels of gathering of a garment is undesirable or where required by manufacturing needs. There is also a need for elastics that will provide elasticity only in specified areas without requiring the application of separate discrete elastic elements at each area. WO 91/15364 discloses an elastomeric laminate such as disclosed in EP-A-500 590 with specific regions strengthened or weakened so that only certain regions (i.e., those not strengthened or those that are weakened) of the film will elongate when subject to stress. These regions that were elongated will then, recover to form elastic regions thereby forming a film with elastic regions and nonelastic regions. GB-A-2,064,608 discloses a diaper with elastic ribbons attached. The elastic ribbon is selectively heated to "kill" the elastic properties while the ribbon is extended. The elastic ribbon is then applied to the diaper web and the area where the elastic was not heated recovers causing the diaper web to which the ribbon is attached to shirr only in these regions. There is still a need to provide an improved elastomeric film laminate having anisotropic qualities which is well-suited to applications where a film is desired that is strong in one direction yet conformable in the cross direction. The object of the present invention is to provide an improved elastomeric film laminate. The object of the present invention is achieved with the features of the claims. The present invention relates to improved non-tacky, multi-layer anisotropic, film laminates which are extensible or elastic in one direction and in elastic in a second direction, which two directions are transverse. Laminates can be prepared by coextrusion of the selected polymers for the skin and core layers or by application of one or more elastomer layer(s) onto one or more already formed skin layer(s). The laminate is obtained by stretching the laminate past the elastic limit of the skin layers and, while the laminate is stretched, selectively deactivating the elasticity of the laminate. The stretched end deactivated direction is high-strength. The recovered elastic film laminate can be microtextured or have detached skin layers. Fig. 1 is a schematic representation of a process and apparatus used to coextrude the laminates of the invention. Fig. 2 is the cross-sectional segment of a laminate with microstructuring caused by uniaxially stretching a film of the invention. The present invention is an anisotropic laminate film that will be non-elastic on a first axis and elastic or extensible on an axis orthogonal to the first axis. The multi-layer elastomeric laminates comprise at least one elastomeric core layer and at least one non-elastomeric skin layer. The laminate film non-elastic axis is provided by stretching an elastic laminate, then subjecting the entire stretched laminate to a deactivating heat treatment rather than merely a localized deactivating heat treatment. The skin layer will then be oriented and strengthened in the direction or axis of stretch and substantially non-extensible on this axis. However, the film in the orthogonal or cross direction will be readily extensible or elastic, if subsequently stretched and allowed to recover. This anisotropic quality renders this film particularly well suited to applications where a film is desired that is strong in one direction yet conformable in the cross direction. For example, a sealing pressure-sensitive adhesive tape to be applied to an uneven surface such as a pipe fitting or screw threads is advantageously conformable in the cross direction to sealingly engage all surfaces, despite their variation in diameter, yet strong in the longitudinal direction. The elastomer of the elastomer core layer can broadly include any material which is capable of being formed into a thin film layer and exhibits elastomeric properties at ambient conditions. Elastomeric means that the material will substantially resume its original shape after being stretched and allowed to relax. Further, preferably, the elastomer will sustain only small permanent set following deformation and relaxation, which set is preferably less than 20 percent and more preferably less than 10 percent of the original length at moderate elongation; e.g., about 400-500%. Generally, any elastomer is acceptable which is capable of being stretched to a degree that causes relatively consistent permanent deformation in a relatively inelastic skin layer. This can be as low as 50% elongation. Preferably, however, the elastomer is capable of undergoing up to 300 to 1200% elongation at room temperature, and most preferably up to 600 to 800% elongation at room temperature. The elastomer can be both pure elastomers and blends with an elastomeric phase or content that will still exhibit substantial elastomeric properties at room temperature. Heat-shrink elastomers are contemplated for use in the present invention, however, non-heat-shrinkable elastomers can be used while retaining the advantages of heat shrinkability in selected embodiments. Non-heat-shrinkable means that the elastomer, when stretched, will substantially recover, sustaining only a small permanent set as discussed above. Non-heat-shrinkable polymers include block copolymers such as those known to those skilled in the art as A-B or A-B-A block copolymers. These block copolymers are described, for example, in U.S. Patent Nos. 3,265,765; 3,562,356; 3,700,633; 4,116,917 and 4,156,673, the substance of which are incorporated herein by reference. Styrene/isoprene, butadiene or ethylene-butylene/styrene (SIS, SBS or SEES) block copolymers are particularly useful. Other useful elastomeric compositions can include elastomeric polyurethanes, ethylene copolymers such as ethylene vinyl acetates, ethylene/propylene copolymer elastomers or ethylene/propylene/diene terpolymer elastomers. Blends of these elastomers with each other or with modifying non-elastomers are also contemplated. Viscosity reducing polymers and plasticizers can also be blended with the elastomers such as low molecular weight polyethylene and polypropylene polymers and copolymers, or tackifying resins such as Wingtack™, aliphatic hydrocarbon tackifiers available from Goodyear Chemical Company. Tackifiers can also be used to increase the adhesiveness of an elastomeric layer to a skin layer. Examples of tackifiers include aliphatic or aromatic hydrocarbon liquid tackifiers, polyterpene resin tackifiers, and hydrogenated tackifying resins. Aliphatic hydrocarbon resins are preferred. Additives such as dyes, pigments, antioxidants, antistatic agents, bonding aids, antiblocking agents, slip agents, heat stabilizers, photostabilizers, foaming agents, glass bubbles, reinforcing fiber, starch and metal salts for degradability or microfibers can also be used in the elastomeric core layer(s). The skin layer can be formed of any semicrystalline or amorphous polymer that is less elastic than the core layer(s) and will undergo permanent deformation at the stretch percentage that the elastomeric laminate will undergo. Therefore, slightly elastomeric compounds, such as some olefinic elastomers, e.g. ethylene-propylene elastomers or ethylene-propylene-diene terpolymer elastomers or ethylenic copolymers, e.g., ethylene vinyl acetate, can be used as skin layers, either alone or in blends. However, the skin layer is generally a polyolefin such as polyethylene, polypropylene, polybutylene or a polyethylene-polypropylene copolymer, but may also be wholly or partly polyamide such as nylon, polyester such as polyethylene terephthalate, polyvinylidene fluoride, polyacrylate such as poly(methyl methacrylate)(only in blends) and the like, and blends thereof. The skin layer material can be influenced by the type of elastomer selected. Skin-to-core layer contact in the Fig. 3 embodiment has been found to follow three modes; first, full contact between the elastomeric core layer and microtextured skin layer; second, full contact with cohesive failure of the core under the microtextured skin folds; and third, adhesive failure of the skin to the core under the microtexture folds with intermittent skin/core contact at the fold valleys. The skin layer, preferably inelastic, used in conjunction with an elastomeric core layer will form at least one outer layer of the laminate. Used as either an outer or inner layer, the skin layer will modify the elastic properties of the elastomeric laminate when in contact with the elastomeric layer by any of the three above-described modes. Additives useful in the skin layer include, but are not limited to, mineral oil extenders, antistatic agents, pigments, dyes, antiblocking agents, provided in amounts less than about 15%, starch and metal salts for degradability and stabilizers such as those described for the elastomeric core layer. Other layers may be added between the core layer and the outer layers, such as interlayers to either increase or decrease the banding of the skin and core layers. Tie layers can be formed of, or compounded with, typical compounds for this use including maleic anhydride modified elastomers, ethyl vinyl acetates and olefins, polyacrylic imides, butyl acrylates, peroxides such as peroxypolymers, e.g., peroxyolefins, silanes, e.g., epoxysilanes, reactive polystyrenes, chlorinated polyethylene, acrylic acid modified polyolefins and ethyl vinyl acetates with acetate and anhydride functional groups and the like, which can also be used in blends or as compatibilizers or delamination-promoting additives in one or more of the skin or core layers. The laminate can elastically recover in the cross-direction after stretching depending on the conditions of film formation, the nature of the elastomeric layer(s), the nature of the skin layer(s), the manner in which the laminate film is stretched and the relative thicknesses of the elastomeric and skin layer(s). By controlling these variables, the laminate film can be designed to instantaneously recover, recover over time or recover upon heat activation. Generally, the core-to-single skin layer ratio will be at least 3, preferably, at least 5 and less than about 100 and most at least 5 to about 75. The overall laminate thickness will be at least 25.4 µm (1 mil), preferably at least 50.8 µm (2 mils), although preferably less than 254 µm (10 mils) for cost and performance considerations. At core-to-skin layer ratios less than 3, the laminate has a tendency to not recover when stretched. A stretched and selectively deactivated laminate capable of instantaneous shrink is one in which the stretched, non-deactivated areas of the elastomeric laminate will. recover more than 15% in 1 sec. A laminate capable of time shrink is one where the 15% recovery point takes place more than 1 sec., preferably more than 5 sec., most preferably more than 20 sec. after stretch, and a laminate capable of heat shrink is where less than 15% shrink recovery occurs to the laminate in the first 20 seconds after stretch and will remain capable of heat shrink for weeks after it is stretched. Percent recovery is the percent that the amount of shrinkage is of the stretched length minus the original length of the activated area. For heat-shrink laminates there will be an activation temperature which will initiate significant heat-activated recovery. The activation temperature used for a heat-shrink laminate will generally be the temperature that will yield 50% of the total possible recovery (T a-50 ) and preferably this temperature is defined as the temperature which will yield 90% (T a-90 ) of the total possible recovery. Total possible recovery includes the amount of preactivation shrinkage. Generally, where the skin layer is relatively thin, the streched laminate will tend to contract or recover immediately in the non-deactivated areas. When the skin thickness is increased sufficiently the streched laminate can become heat shrinkable in the non-deactivated regions or areas. This phenomenon can occur even when the elastomeric layer is formed from a non-heat shrinkable material. By careful selection of the thicknesses of the elastomeric layer and the skin layer(s), the temperature at which the laminate recovers by a set amount can be controlled. This is termed skin controlled recovery, where generally by altering the thickness or composition of the skin, one can raise the elastic recovery activation temperature of an elastomeric core by a significant degree, generally more than at least 10°F (5.6°C) and preferably by 15°F (8.3°C) and more. Although any skin thickness which is effective can be employed, too thick a skin will cause the laminate to remain permanently set when stretched. Generally, where a single skin is less than 30% of the laminate this will not occur. For most heat or time shrink materials, the stretched non-deactivated regions of the elastomeric laminate must be cooled so that the energy released during stretching does not cause immediate heat activated elastic recovery. Fine tuning of the shrink recovery mechanism can be accomplished by the degree that the activated regions are stretched. A preferred mechanism for forming the film laminate by extrusion is shown in Fig. 1 where D, D' and D" are feedblocks or manifolds. D, D' and D" can be separate or combined, or a part of die E. E is a conventional multiple layer die or a combining adapter and die such as disclosed in U.S. Patent Nos. 4,152,387 or 4,197,069 (Cloeren). As shown, feedblocks or manifolds can be used to feed into each layer passageway of the multiple layer die E or to only a single passageway of such a die (e.g., with a combining adaptor in the feedblock region). AA, BB, and CC are extruders. AA', BB' and CC' are streams of thermoplastic material being extruded into the feedblocks or manifold die. E is the 3 or more layer (e.g., 5-layer) die, F is a heated casting roll, and G and H are rolls to facilitate take-off and roll-up of the laminate. Nip rollers can also be provided. The die and feedblock used are typically heated to facilitate polymer flow and layer adhesion. The temperature of the die depends upon the polymers employed and the subsequent heat treatment steps. Generally the temperature of the die is not critical but temperatures are generally in the range of 350 to 550°F (176.7 to 287.8°C) with the polymers exemplified. Whether the laminate is prepared by coating, lamination, sequential extrusion, coextrusion or a combination thereof, the laminate formed and its layers will preferably have substantially uniform thicknesses across the laminate. Laminates prepared in this manner have generally uniform properties with a minimum of edge effects such as curl, modulus change, fraying and the like. After formation, the laminate is stretched past the elastic limit of the skin layer(s), which deform. The stretched laminate is then subjected to heat treatment to relax or deactivate the elastic. The localized heat treatment must be long enough to release stresses in the deformed unstable elastic. The now heat treated laminate can be stretched in the cross direction and recovered, as discussed above. Fig. 2 is a schematic diagram of the common dimensions which are variable for cross direction stretched and recovered laminates in the activated or recovered microtextured regions. The general texture is a series of regular repeating folds. These variables are the total height A-A', the peak to peak distance B-B' and the peak to valley distance C-C'. These variables were measured for a series of polyolefin/styrene-isoprene-styrene/polyolefin laminates. General ranges for A-A', B-B' and C-C' were noted. For total height (A-A'), the range measured was from 0.79 to 32 mils(0.02 to 0.81 mm). For peak-to-peak distance (B-B'), or the fold period, the measured range was from 0.79 to 11.8 mils(0.02 to 0.30 mm). For peak-to-valley distance (C-C'), the measured range was from 0.04 to 19.7 mils(0.001 to 0.5 mm). For those constructions prone to delamination, a brief relaxing or annealing following activation may be used to counteract this tendency, if desired. This brief annealing step will release residual unstable orientation at the elastomeric layer and skin layer interface, particularly for elastic between folds of the microstructured skin layer. The annealing would generally be above the glass transition point temperature (T g ) of the elastomer, above the B bock T g for ABA block copolymers, but below the skin polymer melting point. A lower annealing temperature is generally sufficient. The annealing will generally be for longer than 0.1 seconds, depending on the annealing temperature, followed by cooling to room temperature in the relaxed annealed state. With commercial ABA block copolymers (e.g., Kraton™ 1107), an annealing or relaxing temperature of about 75°C is found to be sufficient.

Claims: An anisotropic film laminate comprising a continuous elastomeric core layer and at least one continuous inelastic skin layer of a thermoplastic film layer oriented in a first direction, characterized in that the film laminate is substantially inelastic in the direction of orientation of said at least one skin layer, such that the laminate is elastic or extensible in a direction transverse to the direction of orientation of the skin layer. The film laminate of any one of claims 1 , wherein the at least one skin layer is a polyolefin film layer. The film laminate of any one of claims 1 or 2, wherein the at least one elastomeric layer is a block copolymer elastomer having elastomeric blocks of polyisoprene. The film laminate of claims 3, wherein the elastomeric layer further comprises 0 to 20 percent of a polystyrene polymer. The film laminate of any of claims 1 to 4, further characterized by a pressure-sensitive adhesive layer.

Inventors: FOX HERBERT J, HELMER PAMELA E, KRUEGER DENNIS L, LOCKRIDGE ROCHELLE L, SWENSON DOUGLAS A, FOX, HERBERT J., HELMER, PAMELA E., KRUEGER, DENNIS L., LOCKRIDGE, ROCHELLE L., SWENSON, DOUGLAS A., Fox, Herbert J., c/o M. M. and M. Co., Helmer, Pamela E., c/o M. M. and M. Co., Krueger, Dennis L., c/o M. M. and M. Co., Lockridge, Rochelle L., c/o M. M. and M. Co., Swenson, Douglas A., c/o M. M. and M. Co.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1993
Main classification: B32B25
IPC codes: B32B7, A61F13, B29C61, B29C55