Alpha, omega-acrylate terminated macromonomer compounds

Abstract: A α,ω-methacrylate terminated epoxide-carboxylic acid macromonomer compound formed by reaction of at least one diepoxide, at least one dicarboxylic acid and at least one unsaturated mono-carboxylic acid and having the general formula I: wherein R is an aromatic moiety formed from a diepoxide R' is a substituted or unsubstituted aliphatic, araliphatic, cycloaliphatic or aromatic moiety formed from a dicarboxylic acid, R'' is hydrogen, a substituted or unsubstituted aliphatic, araliphatic, aromatic or cycloaliphatic moiety formed from a mono-carboxylic acid, and n is an integer from 1 to 20.

Description: The invention relates to compounds having repetitive units of α,ω-acrylate terminated macromonomer epoxide-carboxylic acid. Synthesis of such compounds is carried out by a two-step reaction or by simultaneous polymerization of diepoxides, dicarboxylic acids and unsaturated monocarboxylic acids. These compounds are useful as dental adhesives, dental cements, dental restoratives and dental luting materials. α,ω-(meth)acrylate terminated epoxide-amine macromonomers recently described in patent application (DD 279667) are not comparable to the α,ω-methacrylate epoxide-carboxylic acid macromonomers of the present invention. Nor is the synthesis of the α,ω-methacrylate terminated epoxide carboxylic acid macromonomers of the present invention comparable to the synthesis of amine-macromonomers, because carboxylic acids react at higher temperatures with epoxides than do amines (see Houben-Weyl Bd 14/2, S. 499ff). At such high reaction temperatures there is concern that the polymerization of the unsaturated monocarboxylic acid may occur. M.Fedkte et al, in Plaste und Kautschuk 31 (1984) 405; K. Dusek, L. Matejka, Amer. Chem. Soc. 1984, 15, disclose reaction of epoxide-carboxylic acid to form insoluble network polymers caused by side reactions of epoxides and hydroxylic groups wherein R is an aromatic diepoxide moiety. The synthesis of α,ω-methacrylate terminated epoxide carboxylic acid macromonomers in accordance with the present invention is surprising. EP-A-0 104 491 describes α,ω-terminated monoepoxide-ester macromonomers. As used herein "(Meth)acrylic acid" is understood to mean acrylic and methacrylic acids. Brief Summary of the Invention The invention provides α,ω-acrylate terminated epoxide-carboxylic acid macromonomer compounds formed by reaction of at least one diepoxide, at least one dicarboxylic acid and at least one unsaturated mono-carboxylic acid and having the general formula I: wherein R is on aromatic moiety formed from a diepoxide, R' is a substituted or unsubstituted aliphatic, araliphatic, cycloaliphatic or aromatic moiety formed from a dicarboxylic acid, R'' is hydrogen, a substituted or unsubstituted aliphatic, araliphatic, aromatic or cycloaliphatic moiety formed from a mono-carboxylic acid, and n an integer from 1 to 20. Detailed description of the invention The invention provides α,ω-acrylate terminated epoxide-carboxylic acid macromonomer compounds within the scope of general formula (I): wherein R is a residue arisen from a diepoxide, such as R' is a difunctional substituted or unsubstituted aliphatic, araliphatic, cycloaliphatic or aromatic residue, such as -CH 2 CH 2 -, -CH 2 CH 2 CH 2 CH 2 -, -CH 2 -,-(CH 2 ) 3 -, -C 6 H 4 -, or -C 6 H 10 -, R'' is hydrogen or a monofunctional substituted or unsubstitued aliphatic, araliphatic, aromatic or cycloaliphatic moiety, but preferably CH 3 , and n is an integer from 1 to 20. Compounds within the scope of general formula I are prepared by reaction of diepoxides, dicarboxylic acids and unsaturated monocarboxylic acids. Preferably this reaction is carried out in the presence of catalysts and/or accelerators near or in solvents such as tetrahydrofuran, toluene, or triethyleneglycoldimethacrylate at temperatures between 60 to 150°C. In accordance with the invention are provided compositions which include at least one compound within the scope of general formula I and at least one polymerizable low molecular weight oligomer having a moiety formed from at least one diepoxide and at least one monocarboxylic acid. Methacrylic acid is a preferred monocarboxylic acid used for the synthesis of α,ω-methacrylate terminated epoxide-carboxylic acid macromonomers of formula 2: wherein R is a residue arisen from a diepoxide, such as R' is a difunctional substituted or unsubstituted aliphatic, araliphatic, cycloaliphatic or aromatic residue, such as -CH 2 CH 2 -, -CH 2 CH 2 CH 2 CH 2 -, -CH 2 -,-(CH 2 ) 3 -, -C 6 H 4 -, or -C 6 H 10 -, n is an integer from 1 to 20, The α,ω-acrylate terminated epoxide-carboxylic acid-macromonomers are preferably prepared in two steps. In the first step a prepolymer is formed by reaction of diepoxides with dicarboxylic acids. Then these prepolymers are terminated by reaction with an unsaturated monocarboxylic acid. The reactions in these steps may preferably occur simultaneously. Preferably tetrahydrofuran, dioxane, and/or toluene, are used as solvents for these reactants. Polymerizable diluents such as triethyleneglycolbismethacrylate, diethyleneglycolbismethacrylate, dioxolanbismethacrylate, vinyl-, vinylene- or vinylidene-compounds, acrylate or methacrylate substituted spiroorthoesters, ethoxylated Bis-GMA, are preferably used as solvents for the synthesis of macromonomers in accordance with the invention. Thus polymerizable diluents preferably became part of a macromonomer containing solution to provide a useful function such as reduced viscosity desirable to compound dental composites for restorative dentistry. The α,ω-acrylate terminated epoxide-carboxylic acid macromonomers within the scope of general formulas 1 and 2 of the invention are preferably polymerized using photochemical, radical initiated, and other methods of polymerization, including methods known in the art to accelerate the polymerization of methacrylate monomers. The polymers show good mechanical properties, good adhesion to metals, glass and ceramics. Furthermore they show a relatively low water absorption and especially low shrinkage during the polymerization. Compounds within the scope of general formula I are useful as dental adhesives, and are preferably used in dental compositions which include a self cure catalyst such as benzoyl peroxide. Polymerizable dental composite compositions in accordance with the invention preferably include at least one compound within the scope of general formula I and a filler, such as organic polymer particles and/or inorganic particles. Example 1 6.808 g (20.00 mmol) bisphenol-A diglycidyl ether, 1.462 g (10.00 mmol) adipic acid and 0.091 g triethylbenzylammoniumchloride are dissolved in one another and stirred and heated quickly to 150°C (2-5 minutes) and reacted for 1 hour at 90°C to form a reaction mixture. Then 0.009 g hydroquinone and 1.722 g (20.00 mmol) methacrylic acid are added to the reaction mixture, stirred and reacted for four hours at 90°C. The methacrylate terminated macromonomer obtained is soluble in organic solvents including chloroform, DMF and THF, and has M n (vpo) of 1050 g/mol, T g of 13.9°C the formula (C 56 H 70 O 16 ) 999.17 g/mol with a calculated C of 67.32 and H of 7.06 and a found C of 67.37 and H of 7.34. Example 2 6.808 g (20.00 mmol) bisphenol-A diglycidyl ether, 2.023 g (10.00 mmol) sebacic acid and 0.091 g triethylbenzylammoniumchloride were stirred while heating to 150°C (2-5 minutes) and allowed to react for 1 hour at 90°C to form a reaction mixture. Then 0.009 g hydroquinone and 1.722 g (20.00 mmol) methacrylic acid are added to the reaction mixture, dissolved with stirring and reacted for four hours at 90°C. The methacrylate terminated macromonomer obtained is soluble in organic solvents including chloroform, DMF and THF. It has M n (vpo) of 1130 g/mol, T g of 6.9°C and formula (C 60 H 78 O 16 ) 1055.27 g/mol. Example 3 6.808 g (20.00 mmol) bisphenol-A diglycidyl ether, 2.222 g (10.00 mmol) 3,6,9-trioxaundecane dicarboxylic acid and 0.091 g triethylbenzylammonium chloride are stirred while heating to 150°C (2-5 minutes) and reacted for 1 hour at 90°C to form a reaction mixture. Then 0.009 g hydroquinone and 1.722 g (20.00 mmol) methacrylic acid are added to the reaction mixture stirred and reacted for further four hours at 90°C. The methacrylate terminated macromonomer obtained is soluble in organic solvents including chloroform, DMF and THF. It has M n (vpo) of 1090 g/mol, T g of 14.4°C and the formula (C 58 H 74 O 19 ) 1075.21 g/mol. Example 4 13.616 g (40.00 mmol) bisphenol-A diglycidyl ether, 2.924 g (20.00 mmol) adipic acid, 3.444 g (40.00 mmol) methacrylic acid, 5.052 g triethyleneglycoldimethacrylate, 0.182 g triethylbenzylammoniumchloride and 0.040 g 2,6-di-tert-butyl-p-cresol are reacted for four hours at 90°C. The methacrylate terminated macromonomer obtained is soluble in organic solvents including chloroform, DMF and THF. Its IR-spectrum has absorption at 1720 cm -1 indicating ester groups and no absorption of epoxide groups at 915 and 3050 cm -1 . Example 5 13.616 g (40.00 mmol) bisphenol-A diglycidyl ether, 3.323 g (20.00 mmol) isophthalic acid, 3.444 g (40.00 mmol) methacrylic acid, 5.052 g triethyleneglycoldimethacrylate 0.182 g triethylbenzylammoniumchloride and 0.040 g 2,6-di-tert-p-cresol are reacted for four hours at 90°C. The methacrylate terminated macromonomer obtained in soluble in organic solvents including chloroform, DMF and THF. Its IR-spectrum has absorption at 1720 cm -1 indicating ester groups and no absorption of epoxide groups at 915 and 3050 cm -1 . Example 6 20.425 g (60.00) mmol) bisphenol-A diglycidyl ether, 5.848 g (40.00 mmol) adipic acid, 3.444 g (40.00 mmol) methacrylic acid, 7.430 triethyleneglycoldimethacrylate, 0.246 g triethylbenzylammoniumchloride and 0.060 g 2,6-di-tert.-butyl-p-cresol are reacted for four hours at 90°C. The methacrylate terminated macromonomer obtained is soluble in organic solvents such as chloroform, DMF and THF. Its IR-spectrum has absorption at 1720 cm -1 and no absorption of epoxide groups at 915 and 3050 cm-1 was observed. Composite material Example 7 13.616 g (40.00 mmol) bisphenol-A diglycidyl ether, 2.924 g (20.00 mmol) adipic acid, 3.444 g (40.00 mmol) methacrylic acid, 5.052 g triethyleneglycoldimethacrylate, 0.182 g triethylbenzylammoniumchloride and 0.040 g 2,6-di-tert-butyl-p-cresol are reacted for four hours at 90°C to form a macromonomer containing liquid. The methacrylate terminated macromonomer obtained is soluble in organic solvents including chloroform, DMF and THF. Its IR-spectrum has absorption at 1720 cm -1 indicating ester groups and no absorption of epoxide groups at 915 and 3050 cm -1 . 24 g of the macromonomer containing liquid is mixed with 75 g of APH glass, 0.5 g of propamine and 0.5 g of camphorquinone to form a polymerizable dental composite forming material. Visible light is directed onto this dental composite forming material which polymerizes to form a polymeric dental composite having a shrinkage of 1.27 % a compressive strength of 129.8 MPa, a compressive modulus of 1505.0 MPa, a flexural strength of 52.6 MPa, and a diametrial tensile strength of 34.6 MPa Example 8 51.060 g (0.15 mol) bisphenol-A diglycidyl ether, 10.110 g (0.05 mol) sebacic acid, 17.220 g (0.20 mol) methacrylic acid, 0.402 g triethylbenzylammoniumchloride and 0.164 g 2,6-di-tert.-butyl-p-cresol were reacted for four hours at 90°C. The Methacrylate terminated macromonomer obtained is soluble in organic solvents including chloroform, DMF and THF. Its IR-spectrum has absorption at 1720 cm -1 indicating ester groups and no absorption of epoxide groups at 915 and 3050 cm -1 . M n (calc.) = 783.9 g/mol, M n (vpo) = 750 g/mol Dental Restorative Example 9 15.36 g of the macromonomer formed an described in Example 6, 8.64 g of triethyleneglycol methacrylic acid (TEGMA), 75.00 g of AP.H. glass filler, 0.50 g of camphorquinone and 0.50 g of propamine are mixed to form a dental restorative material. Visible light is applied to the dental restorative material to form a polymeric dental restorative having a Compressive strength of 139 (MPa), Flexural strength of 53 (MPa), Diametral tensile strength of 35 (MPa), Barcol hardness (# 934) of 86 and Polymerization shrinkage of 1.3 %. Dental Root Canal filling material Example 10 21.25 g of the macromonomer formed as described in Example 6, 5.32 g of TEGMA, 6.64 g of ethoxylated Bis-GMA, 66.45 g of calcium tungstate, 0.17 g of propamine and 0.17 g of dibenzylperoxide are mixed to form a dental root canal filing material which polymerizes with a setting time at 23°C of 32 minutes setting time at 37°C of 18 minutes, solubility of 0.3 %, Radio-opacity of 9.2 mm Al and Polymerization shrinkage of 1.0 %.

Claims: A dental material comprising: a filler and a α,ω-acrylate-terminated epoxidecarboxylic acid macromonomer compound formed by reaction of at least one diepoxide, at least one dicarboxylic acid and at least one unsaturated mono-carboxylic acid and having the general formula: wherein R is a residue arisen from a diepoxide, R' is a substituted or unsubstituted aliphatic, araliphatic, cycloaliphatic or aromatic moiety formed from a dicarboxylic acid, R'' is hydrogen, a substituted or unsubstituted aliphatic, araliphatic, aromatic or cycloaliphatic moiety formed from a mono-carboxylic acid, and n is an integer from 1 to 20, said material polymerizing with a polymerization shrinkage of not more than 1.3 volume percent. The dental material according to Claim 1 characterized in that it is a dental restorative, dental cement or dental luting material, or a dental root canal filling material or dental adhesive material. The dental material of Claim 1 wherein R is The dental material accoarding to claims 1 to 3 wherein R is an aromatic moiety formed from a diepoxide and R'' is methyl. The dental material of one of claims 1 to 4 wherein R' is -CH 2 CH 2 -, -CH 2 CH 2 CH 2 CH 2 -, -CH 2 -,-(CH 2 ) 3 -, -C 6 H 4 -, or -C 6 H 10 -. The dental mateiral according to one of claims 1 to 5 wherein the filler is an organic filler or an inorganic filler.

Inventors: CLAUBEN FRANK DR, HORHOLD HANS-HEINRICH, KLEE JOACHIM E, CLAUBEN, FRANK, DR., HORHOLD, HANS-HEINRICH, KLEE, JOACHIM E.
Applicants: DENTSPLY GMBH
Application year: 1993
Main classification: C07C69
IPC codes: A61K6, C07C69