Resin composition having excellent paint coatability

Abstract: A resin composition having excellent paint coatability containing (a) 50-80 weight % of a multi-stage polymerized propylene-ethylene block copolymer consisting essentially of (i) a propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion, (b) 20-40 weight % of an ethylene-α-olefin copolymer elastomer, and (c) 20 weight % or less of an inorganic filler, components in the components (a) and (b), which are soluble in p-xylene at a room temperature, having a number-average molecular weight of 4 x 10⁴ or more and a weight-average molecular weight of 20 x 10⁴ or more.

Description: BACKGROUND OF THE INVENTION The present invention relates to a resin composition for exterior automotive parts, and more particularly to a resin composition having excellent paint coatability and moldability, a good balance of impact resistance, ductility, mechanical strength, thermal deformation resistance, brittle temperature, hardness, etc., small molding shrinkage and linear expansion coefficient, and a high paint coating peeling resistance in high-temperature, high-pressure washing. Since polypropylene is light and has excellent mechanical strength, it is used in various applications. However, since it is poor in impact resistance, its copolymers such as propylene-ethylene block copolymers are used. Also, proposals have been made to provide a resin composition comprising a propylene-ethylene block copolymer, an ethylene-α-olefin copolymer elastomer and an inorganic filler such as talc. Japanese Patent Laid-Open No. 61-12742 discloses a resin composition comprising (a) 62-57 weight % of a propylene-ethylene block copolymer having an ethylene content of 2-3 weight % and a melt flow rate of 40-45 g/10 minutes, (b) 26-28 weight % of an ethylene-propylene copolymer elastomer having an ethylene content of 70-80 weight % and a Mooney viscosity ML 1+4 (100°C) of 55-58, (c) 2-3 weight % of a high-density polyethylene having a density of 0.955-0.960 g/cm 3 and a melt flow rate of 18-22 g/10 minutes, and (d) 10-12 weight % of talc having an average size of 1.8-2.2 µm and a specific surface area of 36000-42000 cm 2 /g, the resin composition having a melt flow rate of 13-18 g/10 minutes, a density of 0.950-0.980 g/cm 3 , a flexural modulus of 11500-14000 kg/cm 2 , a linear expansion coefficient of 7 x 10 -5 - 10 x 10 -5 cm/cm/°C in a temperature range between 20°C and 80°C, and a surface gloss (measured by a 60° -60° method according to JIS Z8741) of 55% or more. Japanese Patent Laid-Open No. 1-149845 discloses a resin composition comprising (a) 59-74 weight % of a propylene-ethylene block copolymer containing 5-12 weight % of a boiling p-xylene-soluble component having an ethylene content of 20-60 weight %, and having an ethylene content of 1-7 weight % and a melt flow rate of 15-50 g/10 minutes, (b) 35-20 weight % of an ethylene-propylene copolymer elastomer having a propylene content of 20-60 weight % and a Mooney viscosity ML 1+4 (100°C) of 100-150, and (c) 3-6 weight % of talc having a specific surface area of 30000 cm 2 /g or more and an average size of 0.5-2.0 µm. However, both resin compositions of Japanese Patent Laid-Open Nos. 61-12742 and 1-149845 are susceptible to thermal deformation, and bumpers made of such resin compositions would be easily deformed due to the difference in a linear expansion coefficient between the resin compositions and the automotive body parts in a high-temperature environment, resulting in the deterioration of automotive body appearance. Also, since beautiful coatings are recently formed on bumpers, etc., the resin compositions for bumpers, etc. should have good paint coatability in order to provide the automotive bodies with good appearance. In the above-described resin compositions comprising the propylene-ethylene block copolymer, the ethylene-propylene copolymer elastomer (or high-density polyethylene) and talc, their flowability is controlled for various applications by adjusting ethylene/propylene ratios and molecular weights, etc. in the propylene-ethylene block copolymer and the ethylene-propylene copolymer elastomer. However, the control of such parameters fails to provide resin compositions having well balanced properties such as paint coatability, moldability, rigidity, ductility, thermal deformation resistance, brittle temperature, hardness, etc. on levels suitable for exterior automotive parts. As a polypropylene resin composition for automotive bumpers having an improved paint coatability, Japanese Patent Laid-Open No. 57-55952 discloses a polypropylene resin composition comprising 55-65 weight % of a crystalline propylene-ethylene block copolymer containing 5-10 weight % of ethylene, a propylene component, 97 weight % or more of which is insoluble is boiling n-heptane, and a component soluble in p-xylene at a room temperature having an intrinsic viscosity (in decalin at 135°C) of 3-4 and a melt flow rate of 2-10; 30-35 weight % of an amorphous ethylene-propylene copolymer elastomer having an intrinsic viscosity (in decalin at 135°C) of 2.0-3.5 and a Mooney viscosity ML 1+4 (100°C) of 40-100; and 5-15 weight % of talc having an average size of 0.5-5 µm. This resin composition shows an improved resistance to peeling of coatings formed thereon, but it fails to show a sufficient peeling resistance of the coatings in washing under severe conditions such as high temperature and/or high pressure. OBJECT AND SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a resin composition for exterior automotive parts having excellent paint coatability and moldability, and well balanced impact resistance, ductility, mechanical strength, thermal deformation resistance, brittle temperature and hardness while showing small molding shrinkage and linear expansion coefficient. Another object of the present invention is to provide a resin composition for exterior automotive parts further having good peeling resistance of coatings under severe conditions such as high-temperature, high-pressure washing. As a result of intense research in view of the above objects, the inventors have found that by blending a propylene-ethylene block copolymer produced by a multi-stage polymerization, an ethylene-α-olefin copolymer elastomer and an inorganic filler, and by controlling the content of propylene-ethylene random copolymer portion in the resulting resin composition and various parameters of the components, the resulting resin composition shows well balanced impact resistance, ductility, mechanical strength, thermal deformation resistance, brittle temperature and hardness. With respect to the peeling resistance of a coating formed on a resin molding substrate under severe conditions such as high-temperature, high-pressure washing, the inventors have also found that the peeling resistance is usually determined by a Young's modulus of the coating, the strength of a substrate and an adhesion strength between the coating and the substrate, and that if the adhesion strength between the coating and the substrate is large enough, the peeling resistance is not affected by the adhesion strength, but largely affected by the strength of the substrate itself. However, if it is tried to increase the strength of the resin substrate, the resin substrate is likely to show decreased impact resistance. In order to increase the strength of the resin substrate while preventing a decrease in the impact resistance, the inventors have found that it can effectively be achieved by increasing the strength of elastomer components in the resin composition, specifically a propylene-ethylene random copolymer portion in the propylene-ethylene block copolymer and an ethylene-α-olefin copolymer elastomer. The present invention has been completed based on these findings. The invention provides a resin composition having excellent paint coatability comprising: (a) 50-80 weight % of a propylene-ethylene block copolymer produced by a multi-stage polymerization including a polymerization stage of propylene to provide a crystalline propylene homopolymer and a subsequent random copolymerization stage of said propylene homopolymer with ethylene + propylene, (b) 20-40 weight % of an ethylene-α-olefin copolymer elastomer, and (c) up to 20 weight % of an inorganic filler, components in said components (a) and (b), which are soluble in p-xylene at a room temperature, are characterized by (i) a number-average molecular weight of 4 X 10 4 or more and a weight-average molecular weight of 20 X 10 4 or more; and optionally at least one of the following requirements consisting of: (ii) a crystallinity of 20-30%; and (iii) a melting point of 50°C or higher. Said propylene-ethylene block copolymer may consist essentially of 80-95 weight % of a propylene homopolymer portion, 5-20 weight % of a propylene-ethylene random copolymer portion, and 10 weight % or less of an ethylene homopolymer portion. Said ethylene-α-olefin copolymer elastomer may be selected from the group consisting of an ethylene-propylene copolymer elastomer, an ethylene-propylene-diene copolymer elastomer and an ethylene-butene copolymer elastomer. DETAILED DESCRIPTION OF THE INVENTION [A] Components of resin composition [1] First resin composition The first resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-α-olefin copolymer elastomer, and (c) an inorganic filler. (a) Multi-stage polymerized propylene-ethylene block copolymer The propylene-ethylene block copolymer usable in the present invention are those produced by a so-called multi-stage polymerization method. In the multi-stage polymerization, propylene is first polymerized in the presence of a catalyst such as a Ziegler catalyst to form a crystalline propylene homopolymer portion which may contain a small proportion of a comonomer, and then ethylene + propylene are supplied to a reactor to form a propylene-ethylene random copolymer portion. The propylene-ethylene block copolymer produced by the multi-stage polymerization consists essentially of (i) a crystalline propylene homopolymer portion, (ii) a propylene-ethylene random copolymer portion, and (iii) an ethylene homopolymer portion. These polymer components may exist as separately or in an unseparably combined state. Though each portion of the propylene-ethylene block copolymer consists essentially of propylene and/or ethylene, other α-olefins and dienes, etc. may be contained in small amounts. The propylene-ethylene random copolymer portion has a low crystallinity, and preferably contains 30-70 weight % of ethylene. If the ethylene content is lower than 30 weight %, or if it exceeds 70 weight %, the resulting resin composition would show undesirably poor ductility. The weight-average molecular weight of the propylene-ethylene random copolymer portion (ii) is preferably 20 x 10 4 or more, more preferably 20 x 10 4 - 80 x 10 4 , most preferably 50 x 10 4 - 80 x 10 4 . Also, the number-average molecular weight of the propylene-ethylene random copolymer portion is preferably 4 x 10 4 or more, more preferably 4 x 10 4 - 10 x 10 4 , most preferably 7 x 10 4 - 10 x 10 4 . The ethylene content in the entire propylene-ethylene block copolymer is preferably 2-10 weight %. Also, On the basis of the total amount (100 weight %) of the components (i) - (iii), the propylene homopolymer portion (i) is preferably 80-95 weight %, the propylene-ethylene random copolymer portion (ii) is preferably 5-20 weight %, and the ethylene homopolymer portion (iii) is preferably 10 weight % or less. Outside the above ranges, the resin composition would not show good properties. The multi-stage polymerized propylene-ethylene block copolymer preferably shows a melt flow rate (MFR, 230°C, 2.16 kg load) of 15-120 g/10 minutes. If the MFR is lower than 15 g/10 minutes, the resulting resin composition would have poor moldability, particularly injection-moldability. On the other hand, if the MFR is higher than 120 g/10 minutes, the resin composition would be likely to exhibit poor mechanical strength. (b) Ethylene-α-olefin copolymer elastomer The ethylene-α-olefin copolymer elastomer is a copolymer elastomer composed of ethylene and at least one other α-olefin. For instance, an ethylene-propylene copolymer elastomer (EPR), an ethylene-propylene-diene copolymer elastomer (EPDM), an ethylene-butene copolymer elastomer (EBR), etc. are used as the ethylene-α-olefin copolymer elastomer. Specifically, in the case of the ethylene-propylene copolymer elastomer (EPR) and the ethylene-propylene-diene copolymer elastomer (EPDM), the preferred ethylene content is 50-90 mol % and the preferred propylene content is 50-10 mol %. More preferably, the ethylene content is 70-80 mol % and the propylene content is 30-20 mol %. In the case of the ethylene-propylene-diene copolymer elastomer (EPDM), the preferred diene monomers are ethylidene norbornene, dicyclopentadiene, 1,4-hexadiene, etc. The diene content is preferably 1-10 mol %. The ethylene-propylene copolymer elastomer (EPR) and the ethylene-propylene-diene copolymer elastomer (EPDM) may preferably have a melt flow rate (MFR, 230°C, 2.16 kg load) of 0.5-20 g/10 minutes, and more preferably 0.5-10 g/10 minutes. The ethylene-butene copolymer elastomer (EBR) preferably has an ethylene content of 70-85 mol %, and a butene-1 content of 30-15 mol %. More preferably, the ethylene content is 75-85 mol % and the butene-1 content is 25-15 mol %. The ethylene-butene copolymer elastomer (EBR) preferably has a melt index (MI, 190°C, 2.16 kg load) of 1-30 g/10 minutes, and more preferably 1-20 g/10 minutes. The ethylene-α-olefin copolymer elastomer preferably has a number-average molecular weight of 2 x 10 4 - 8 x 10 4 , more preferably 3 x 10 4 - 6 x 10 4 , and a weight-average molecular weight of 7 x 10 4 - 20 x 10 4 , more preferably 10 x 10 4 -20 x 10 4 . The above-described species of the ethylene-α-olefin copolymer elastomer may be used alone or in combination. (c) Inorganic filler The inorganic fillers are generally used as reinforcing fillers for resins. The inorganic fillers are, for instance, talc, mica, fibrous crystalline calcium silicate, calcium carbonate. Among them, talc is preferable. The inorganic filler preferably has an average size of 15 µm or less. In the case of needle-shaped or fibrous inorganic filler, its diameter is preferably 1-100 µm, and its aspect ratio is preferably 3-30. (d) P-xylene-soluble component A component soluble in p-xylene at a room temperature in the components (a) and (b) is an elastomeric component consisting essentially of the propylene-ethylene random copolymer portion (ii) in the component (a), and the ethylene-α-olefin copolymer elastomer (b). This p-xylene-soluble component has a number-average molecular weight of 4 x 10 4 or more, preferably 4 x 10 4 - 7 x 10 4 , and a weight-average molecular weight of 20 x 10 4 or more, preferably 20 x 10 4 - 30 x 10 4 . If the p-xylene-soluble component has a number-average molecular weight lower than 4 x 10 4 or a weight-average molecular weight lower than 20 x 10 4 , the resulting resin composition would have poor mechanical strength, resulting in insufficient improvement in peeling resistance of coatings formed thereon. Incidentally, the above elastomeric component may be obtained by dissolving the resin composition in boiling p-xylene to separate out the inorganic filler, and cooling it to separate out the propylene homopolymer portion (i) and the ethylene homopolymer portion (iii) as insoluble components, leaving the elastomeric component (ii) in a solution in p-xylene. (e) Proportions of components in first resin composition The proportions of the above components (a)-(c) in the first resin composition are such that the propylene-ethylene block copolymer is 50-80 weight %, preferably 55-75 weight %, the ethylene-α-olefin copolymer elastomer is 20-40 weight %, preferably 20-30 weight %, and the inorganic filler is 20 weight % or less, preferably 5-15 weight %. If the amount of the propylene-ethylene block copolymer is less than 50 weight %, the resulting resin composition would fail to show improved elongation. On the other hand, if the amount of the propylene-ethylene block copolymer is larger than 80 weight %, the resulting resin composition would fail to show improved impact resistance. If the amount of the ethylene-α-olefin copolymer elastomer is less than 20 weight %, the resulting resin composition would fail to show improved tensile properties such as tensile elongation at break. On the other hand, If the amount of the ethylene-α-olefin copolymer elastomer is larger than 40 weight %, the resulting resin composition would fail to show improved mechanical strength such as flexural modulus. If the amount of the inorganic filler is larger than 20 weight %, the resulting resin composition would fail to show improved impact resistance and tensile elongation. Although there is no particular lower limit in the inorganic filler content, 5 weight % or more of the inorganic filler is preferable to achieve sufficient effects. [2] Second resin composition The second resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-α-olefin copolymer elastomer, and (c) an inorganic filler like the first resin composition. (a) Multi-stage polymerized propylene-ethylene block copolymer The multi-stage polymerized propylene-ethylene block copolymer in the second resin composition may be the same as in the first resin composition. Incidentally, in this resin composition, the number-average molecular weight and weight-average molecular weight of the propylene-ethylene block copolymer may not be particularly restricted. (b) Ethylene-α-olefin copolymer elastomer The ethylene-α-olefin copolymer elastomer in the second resin composition may be the same as in the first resin composition, but it is preferable that the ethylene-α-olefin copolymer elastomer has a crystallinity of 20-30%. With respect to the number-average molecular weight and the weight-average molecular weight, the ethylene-α-olefin copolymer elastomer may not be restricted. In order to have the above crystallinity, it is preferable to use both an ethylene-propylene copolymer elastomer (EPR) and an ethylene-butene copolymer elastomer (EBR). Specifically, it is preferable to use an ethylene-propylene copolymer elastomer (EPR) containing 70-80 mol % of ethylene and 20-30 mol % of propylene and having a crystallinity of 10-20%, and an ethylene-butene copolymer elastomer (EBR) containing 70-85 mol % of ethylene and 15-30 mol % of butene-1 and having a crystallinity of 20-30%. By combining 25-75 weight %, preferably 30-70 weight %, of the ethylene-propylene copolymer elastomer (EPR) and 75-25 weight %, preferably 70-30 weight %, of the ethylene-butene copolymer elastomer (EBR), it is possible to provide the ethylene-α-olefin copolymer elastomer with the desired crystallinity of 20-30%. Also, the crystallinity of the ethylene-α-olefin copolymer elastomer can be increased by adding polyethylene such as linear low-density polyethylene, low-density polyethylene, ultra low-density polyethylene, etc. to the ethylene-α-olefin copolymer elastomer in such a range that elastomeric properties of the ethylene-α-olefin copolymer elastomer are not deteriorated. Specifically, the polyethylene may be added in an amount of about 20 weight % or less per 100 weight % of the entire resin (including the polyethylene). (c) Inorganic filler The inorganic filler in the second resin composition may be the same as in the first resin composition. (d) P-xylene-soluble component The p-xylene-soluble component (elastomeric component) contained in the overall resin composition preferably has a crystallinity of 20-30%. If the crystallinity of the elastomeric component is lower than 20%, the elastomeric component does not have sufficient mechanical strength. On the other hand, if the crystallinity of the elastomeric component is higher than 30%, the resin composition would show poor impact resistance. (e) Proportions of components in second resin composition The proportions of the above components (a)-(c) in the second resin composition may be the same as in the first resin composition. [3] Third resin composition The third resin composition of the present invention comprises (a) a multi-stage polymerized propylene-ethylene block copolymer, (b) an ethylene-α-olefin copolymer elastomer, and (c) an inorganic filler like the first resin composition. (a) Multi-stage polymerized propylene-ethylene block copolymer The multi-stage polymerized propylene-ethylene block copolymer in the third resin composition may be the same as in the first resin composition. Incidentally, in the third resin composition, the number-average molecular weight, weight-average molecular weight and crystallinity of the elastomeric components (propylene-ethylene random copolymer portion (ii) and ethylene-α-olefin copolymer elastomer (b)) may not be particularly restricted. (b) Ethylene-α-olefln copolymer elastomer The ethylene-α-olefin copolymer elastomer in the third resin composition may be the same as in the first resin composition, but it is preferable that the ethylene-α-olefin copolymer elastomer has a melting point of 50-70°C. With respect to the number-average molecular weight, the weight-average molecular weight and the crystallinity, the ethylene-α-olefin copolymer elastomer may not be restricted. Since the ethylene-propylene copolymer elastomer (EPR) including the ethylene-propylene-diene copolymer elastomer (EPDM) has a melting point of 10-50°C, particularly 30-50°C, and since the ethylene-butene copolymer elastomer (EBR) has a melting point of 60-90°C, particularly 70-90°C, it is preferable to combine the ethylene-propylene copolymer elastomer (EPR) and the ethylene-butene copolymer elastomer (EBR) in order to achieve the above crystallinity. Specifically, by combining 25-75 weight %, preferably 30-70 weight %, of the ethylene-propylene copolymer elastomer (EPR) and 75-25 weight %, preferably 70-30 weight %, of the ethylene-butene copolymer elastomer (EBR), it is possible to provide the ethylene-α-olefin copolymer elastomer with the desired melting point of 50-70°C. (c) Inorganic filler The inorganic filler in the third resin composition may be the same as in the first resin composition. (d) P-xylene-soluble component The p-xylene-soluble component, (elastomeric component) contained in the overall resin composition preferably has a melting point of 50°C or higher, more preferably 55-65°C. If the melting point of the elastomeric component is lower than 50°C, the elastomeric component does not have sufficient heat resistance and high-temperature peeling resistance. (e) Proportions of components in third resin composition The proportions of the above components (a)-(c) in the third resin composition are such that the propylene-ethylene block copolymer is 50-80 weight %, preferably 55-75 weight %, the ethylene-α-olefin copolymer elastomer is 20-40 weight %, preferably 20-30 weight %, and the inorganic filler is 20 weight % or less, preferably 5-15 weight %. By satisfying two or more requirements in the above first to third resin compositions, it is possible to provide a resin composition with highly improved paint coatability, peeling resistance of coatings formed thereon, and other properties. [B] Other components in resin composition To improve the properties of the first to third resin compositions, various other additives such as heat stabilizers, antioxidants, photostabilizers, flame retardants, plasticizers, antistatic agents, parting agents, foaming agents, etc. may be added. Typical examples of the preferred combinations of the parameters other than those of the first to third resin compositions will be shown below. (1) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have an Mn of 4 x 10 4 or more, an Mw of 20 x 10 4 or more, and a crystallinity of 20-30%. (2) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have an Mn of 4 x 10 4 or more, an Mw of 20 x 10 4 or more, and a melting point of 50°C or higher. (3) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have a crystallinity of 20-30%, and a melting point of 50°C or higher. (4) Components in the components (a) and (b), which are soluble in p-xylene at a room temperature, have an Mn of 4 x 10 4 or more, an Mw of 20 x 10 4 or more, a crystallinity of 20-30%, and a melting point of 50°C or higher. (5) The propylene-ethylene random copolymer portion has a number of 20 x 10 4 or more and an Mw of 60 x 10 4 or more, and an ethylene content is 60 weight % or more and the ethylene homopolymer portion (iii) is 40 weight % or more based on the total amount of (ii) and (iii). [C] Method of producing resin compositions The first to third resin compositions of the present invention can be produced by blending the components at 150-300°C, preferably 190-250°C in a single-screw extruder or a double-screw extruder. The present invention will be explained in further detail by way of the following Examples without intention of restricting the scope of the present invention. Examples 1-8, Comparative Examples 1 and 2 Starting materials used in these Examples and Comparative Examples are as follows: (a) Multi-stage polymerized propylene-ethylene block copolymer BPP-1: [ethylene content: 4 weight %, melt flow rate (MFR, 230°C, 2.16 kg load): 60 g/10 minutes]. (b1) Ethylene-propylene copolymer elastomer EPR-1: [propylene content: 23 weight %, melt flow rate (MFR, 230°C, 2.16 kg load): 0.8 g/10 minutes, hardness (JIS A): 74, melting point: 43°C, crystallinity: 11%, number-average molecular weight: 5.7 x 10 4 , weight-average molecular weight: 14.2 x 10 4 ]. EPR-2: [propylene content: 22 weight %, melt flow rate (MFR, 230°C, 2.16 kg load): 3.6 g/10 minutes, hardness (JIS A): 73, melting point: 41.3°C, crystallinity: 12%, number-average molecular weight: 4.5 x 10 4 , weight-average molecular weight: 9.9 x 104]. (b2) Ethylene-butene copolymer elastomer EBR-1: [butene-1 content: 20 weight %, melt index (MI, 190°C, 2.16 kg load): 1.3 g/10 minutes, hardness (JIS A): 87, melting point: 78.2°C, crystallinity: 26%, number-average molecular weight: 6.5 x 10 4 , weight-average molecular weight: 12.7 x 10 4 ]. EBR-2: [butene-1 content: 20 weight %, melt index (MI, 190°C, 2.16 kg load): 3.5 g/10 minutes, hardness (JIS A): 85, melting point: 70.8°C, crystallinity: 25%, number-average molecular weight: 3.8 x 10 4 , weight-average molecular weight: 8.3 x 10 4 ]. (c) Inorganic filler Talc: [LMS300 available from Fuji Talc K.K., average size: 1.25 µm] (d) Linear low-density polyethylene LLDPE: [density: 0.930 g/cm 3 , melt index (MI, 190°C, 2.16 kg load): 1.0 g/10 minutes]. A multi-stage polymerized propylene-ethylene block copolymer (BPP-1), an ethylene-propylene copolymer elastomer (EPR-1, EPR-2), an ethylene-butene copolymer elastomer (EBR-1, EBR-2), talc and optionally linear low-density polyethylene were dry-blended in proportions shown in Table 1 below by a supermixer and introduced into a double-screw extruder to conduct their blending at 190-250°C and at 200 rpm to produce composition pellets. The resulting composition was dissolved in boiling p-xylene to separate out an inorganic filler (talc) as an insoluble component, and then cooled to separate out a propylene homopolymer portion and an ethylene homopolymer portion as insoluble components. The remaining elastomeric component was measured with respect to a weight-average molecular weight (Mw), a number-average molecular weight (Mn), a crystallinity and a melting point. The results are shown in Table 1. The composition pellets were injection-molded at 210°C to form specimens for measuring their properties (melt flow rate, flexural modulus, Izod impact strength, peeling resistance of coating formed thereon, and resistance to washing). The results are shown in Table 2. As is clear from Table 2, the resin compositions of the present invention are excellent in paint coatability, peeling resistance at high temperature and resistance to high-temperature, high-pressure washing. As described above in detail, since the resin composition of the present invention comprises a multi-stage polymerized propylene-ethylene block copolymer, an ethylene-α-olefin copolymer elastomer and an inorganic filler, and since the elastomeric component (total of a propylene-ethylene random copolymer portion in the propylene-ethylene block copolymer, and an ethylene-α-olefin copolymer elastomer) in the resin composition is designed to have high strength, the resin composition shows excellent paint coatability, peeling resistance of paint Coatings and resistance to high-temperature, high-pressure washing, in addition to welled balanced mechanical properties such as impact resistance, ductility, tensile elongation, thermal deformation resistance, brittle temperature, and hardness. Also, it suffers from only small molding shrinkage and linear expansion coefficient. Such resin compositions of the present invention are usable in various applications, and particularly suitable for exterior automotive parts, etc.

Claims: A resin composition having excellent paint coatability comprising: (a) 50-80 weight % of a propylene-ethylene block copolymer produced by a multi-stage polymerization including a polymerization stage of propylene to provide a crystalline propylene homopolymer and a subsequent random copolymerization stage of said propylene homopolymer with ethylene + propylene, (b) 20-40 weight % of an ethylene-α-olefin copolymer elastomer, and (c) up to 20 weight % of an inorganic filler, components in said components (a) and (b), which are soluble in p-xylene at a room temperature, are characterized by (i) a number-average molecular weight of 4 X 10 4 or more and a weight-average molecular weight of 20 X 10 4 or more; and optionally at least one of the following requirements consisting of: (ii) a crystallinity of 20-30%; and (iii) a melting point of 50°C or higher. The resin composition according to Claim 1, wherein said propylene-ethylene block copolymer consisting ess'entially of 80-95 weight % of a propylene homopolymer portion, 5-20 weight % of a propylene-ethylene random copolymer portion, and 10 weight % or less of an ethylene homopolymer portion. The resin composition according to Claim 1 or 2, wherein said ethylene-α-olefin copolymer elastomer is selected from the group consisting of an ethylene-propylene copolymer elastomer, an ethylene-propylene-diene copolymer elastomer and an ethylene-butene copolymer elastomer.

Inventors: IWAI HISAYUKI, IWANAMI KUNIO, KAWAZU KENJI, KITANO KITSUSHO, MIYAZAKI SHIZUO, NISHIO TAKEYOSHI, NOMURA TAKAO, SAITO YOSHIHARU, SAKAIZAWA MASAO, TASAKA MICHIHISA, IWAI, HISAYUKI, IWANAMI, KUNIO, KAWAZU, KENJI, KITANO, KITSUSHO, MIYAZAKI, SHIZUO, NISHIO, TAKEYOSHI, NOMURA, TAKAO, SAITO, YOSHIHARU, SAKAIZAWA, MASAO, TASAKA, MICHIHISA, Iwanami, Kunio, c/o Tech. Devel. Center of, Kitano, Kitsusho, c/o Tech. Devel. Center of, Saito, Yoshiharu, c/o Tech. Devel. Center of, Sakaizawa, Masao, c/o Tech. Devel. Center of
Applicants: TONEN SEKIYUKAGAKU KK, TOYOTA MOTOR CO LTD, TONEN CHEMICAL CORPORATION, TOYOTA JIDOSHA KABUSHIKI KAISHA
Application year: 1993
Main classification: C08L53
IPC codes: C08L53, C08L23, C08K3