Ultraviolet absorbing green tinted glass

Abstract: A green tinted, ultraviolet absorbing glass is disclosed having a standard soda-lime-silica base glass composition and a colorant portion consisting essentially of on a weight basis: less than 2.0% TiO₂ and greater than 0.6% total iron (expressed as Fe₂O₃) with the ratio of FeO/total iron less than 0.35. The glass exhibits an ultraviolet transmittance no greater than 38 percent (300 to 400 nanometers) and a luminous transmittance (illuminant A) of at least 70 percent at thicknesses ranging from 0.154 to 0.189 inches.

Description: This application is a continuation-in-part application of U.S. Serial No. 07/857,903, filed March 26, 1992, which is a continuation-in-part of U.S. Serial No. 07/559,915, filed July 30, 1990. BACKGROUND OF THE INVENTION This invention relates to soda-lime-silica glass particularly suitable for controlling transmittance of solar radiation in window glazing applications. The glass may be generally described as being green tinted, and is designed to have low heat transmittance and particularly enhanced absorption in the ultraviolet wavelength range. This is desirable for the sake of reducing the rate at which the sun's rays deteriorate plastics and fabrics in applications such as automobiles. A particular objective of the invention is to permit glass of this type to be made at a lower cost by reducing the amount of costly ingredients required. Soda-lime-silica flat glass may be essentially characterized by the following composition on a weight percentage basis of the total glass: SiO 2 66 - 75% Na 2 O 10 - 20 CaO 5 - 15 MgO 0 - 5 Al 2 O 3 0 - 5 K 2 O 0 - 5 Other minor ingredients, including melting and refining aids such as SO 3 , may also appear in the glass composition. Small amounts of K 2 O, BaO or B 2 O 3 and other minor constituents have also sometimes been included in flat glass and may be considered optional. To this base glass are added the coloring constituents that produce the transmittance properties of the glass. The primary colorant in the category of glasses relevant to the present invention is iron, which is usually present in both the Fe 2 O 3 and FeO forms. As is conventional, the total amount of iron present in a glass is expressed herein as Fe 2 O 3 , regardless of the form actually present. A typical green tinted automotive glass has about 0.5 percent by weight total iron, with the ratio of FeO to total iron being about 0.25. Recently, it has become important to maximize the solar performance of automotive glazing. The use of larger glass areas and the elimination of CFC air conditioning coolants places a greater burden on the car interior and air conditioning systems. A goal has been established to limit ultraviolet transmittance to no more than 38 percent in some automotive glass. At the same time, it is a requirement that glass in vision areas of automobiles have an luminious transmittance of at least 70 percent. Two approaches have been followed to improve the solar performance of the glass and meet these goals. In the first approach, high iron levels are used in the glass. The colorant composition and transmittance properties for examples of two commercial annealed products of this high iron, dark green tinted type along with an example of the conventional, light green tinted glass described above are set forth below: Light Green Example A Dark Green Example B Dark Green Example C Total Iron (wt.%) 0.521 0.803 0.728 FeO/Tot. Iron 0.268 0.284 0.291 LT A (%) 80.45 71.1 72.44 TSUV (%) 54.82 38.8 42.28 TSIR (%) 37.38 22.4 24.62 TSET (%) 57.85 44.5 46.92 Although Examples B and C show a reduction in ultraviolet transmittance, the percentage still exceeds the desired goal. Merely increasing the amount of total iron to reduce the ultraviolet transmittance is not desirable because it would impermissibly lower the luminous (visible light) transmittance. Furthermore, the use of very high levels of iron can create problems in manufacturing the glass, such as shorter campaigns or the use of expensive electric boosting. The second approach uses cerium oxide or cerium oxide plus titanium oxide in glass to reduce ultraviolet transmittance as disclosed in U.S. Patent Nos. 2,860,059 and 5,077,133, and the following example is of a commercial product that takes this latter approach: Example D CeO 2 (wt.%) 0.60 TiO 2 (wt.%) 0.22 Total Iron (wt.%) 0.783 FeO/Tot. Iron 0.266 LT A (%) 72.5 TSUV (%) 31.8 TSIR (%) 23.7 TSET (%) 45.7 This glass exhibits the desired combination of low ultraviolet transmittance and high luminous transmittance, but the high cost of cerium sources substantially increases the cost of making this glass. It would be desirable if these objectives could be met without incurring such high raw material costs. It has also been found that glasses made according to these two approaches darkens upon tempering and exposure to solar ultraviolet radiation. This in turn lowers luminious transmittance. It is therefore necessary to reduce the heat absorbing component (Fe 2 O 3 ) to ensure the glass has at least a 70% luminious transmittance after use. For these reasons, it would be desirable to produce glasses with enhanced spectral properties but at lower cost and with reduced solarization. The transmittance data provided above and throughout this disclosure, except where noted, is based on a glass thickness of 3.9 millimeters (0.154 inch). Luminous transmittance (LT A ) is measured using C.I.E. standard illuminant "A" over the wavelength range 380 to 770 nanometers at 10 nanometer intervals. Total solar ultraviolet transmittance (TSUV) is measured over the wavelength range 300 to 400 nanometers at 10 nanometer intervals. Total solar infrared transmittance (TSIR) is measured over the wavelength range 800 to 2100 nanometers at 50 nanometer intervals. Total solar energy transmittance (TSET) represents a computed value based on measured transmittances from 300 to 2100 nanometers at 50 nanometer intervals. To determine this transmittance data, the transmittance values are integrated over the wavelength range [a,b]. This range is divided into n equal subintervals of length h by points {X o , X 1 , ..., X n } where X i = a + (i x h) . Generally, either the Rectangular Rule or the Trapezoidal Rule is used to compute the transmittance data. For each method, a different interpolating function is used to approximate the integrand ƒ in each subinterval. The sum of integrals of these interpolating functions provides an approximation of the integral: I = a b ƒ(X)dX In the case of the Rectangular Rule, the constant value ƒ(X i ) is used as an approximation of ƒ(X) on [X i-1 ,X i ]. This yields a step-function approximation of ƒ(X) on [a,b], and the numerical integration formula: I = i=1 n ƒ(X i ) x h For the Trapezoidal Rule, ƒ(X) is approximated on [X i-1 ,X i ] by a straight line passing through the graph of ƒ at the end points. Thus, the interpolating function for ƒ(X) is piecewise linear on [a,b] and the integration formula becomes: I = [ƒ(X o )+2 i=1 n-1 ƒ(X i ) + ƒ(X n )] x (h/2) The transmittance data presented throughout this disclosure is based on the Trapezodial Rule. SUMMARY OF THE INVENTION The present invention provides a green tinted, ultraviolet absorbing, soda lime silica glass that has luminous transmittance of at least 70 percent and ultraviolet transmittance of no more than 38 percent at thicknesses ranging from 0.154 to 0.189 inches (3.9 to 4.9 mm). These properties are achieved in the present invention by using a colorant that is less than 2.0 percent by weight TiO 2 of the total glass composition, preferably 0.05 to 0.60 weight percent TiO 2 , greater than 0.60 percent by weight total iron (expressed as Fe 2 O 3 ), preferably 0.6 to 0.95 weight percent total iron, and a ratio of FeO/total iron (ferrous iron expressed as FeO divided by the total iron expressed as Fe 2 O 3 ) of less than 0.350, preferably 0.24 to 0.29. The combination of iron and titanium oxide can actually increase the luminious transmittance, thereby allowing the maximum level of heat absorbing agent to be used and improve the overall solar performance of the glass. The present invention also provides a method of producing green tinted, ultraviolet absorbing glass exhibiting ultraviolet transmittance no greater than 38 percent (300 to 400 nanometers) and luminous transmittance (illuminant A) of at least 70 percent at thicknesses ranging from 0.154 to 0.189.The method includes the steps of melting and forming soda lime silica glass having a colorant portion consisting essentially of, on a weight percent basis, less than 2.0% TiO 2 , preferably 0.05 to 0.60 weight percent TiO 2 , and greater than 0.6% iron (expressed as Fe 2 O 3 ), preferably 0.6 to 0.95 weight percent total iron, and a ratio of FeO/total iron (ferrous iron expressed as FeO divided by the total iron expressed as Fe 2 O 3 ) of less than 0.350, preferably 0.24 to 0.29, and tempering the glass to increase its luminous transmittance to a value greater than 70 percent. DETAILED DESCRIPTION The base glass composition is not critical to the present invention and may consist of any conventional soda-lime-silica flat glass composition, which may be characterized by the ranges set forth above. Preferably, the base glass is one known by those of skill in the art to be producible in a continuous melting furnace and formed into a flat sheet by the float process. A specific example of a base glass of the present invention can be seen in the following example which is Example A discussed earlier. Base Glass Example A Composition SiO 2 72.67 percent by weight Na 2 O 13.76 CaO 8.71 MgO 3.84 Al 2 O 3 0.14 K 2 O 0.05 SO 3 0.214 Fe 2 O 3 (total) 0.521 Additionally, traces of impurities may be present without significant effect on the glass. Melting and fining aids such as SO 3 are useful during production of the glass, but their residual amounts in the glass can vary and have no significant effect on the properties of the glass product. K 2 O is present in this example as an impurity, and its presence is not required, although it serves a function in the glass essentially equivalent to that of Na 2 O. The batch mixture of raw materials from which the glass of Example 1 was melted was as follows: Sand 1000 parts by weight Soda ash 329 Limestone 71 Dolomite 242 Gypsum 19.65 Rouge 6.4 It is important to control the ratio of ferrous to total iron in order to get the required spectral properties. One of the ways to control this ratio of ferrous to total iron is by selecting an amount of coal or other reducing agent to be included in the batch mixture. Instead of coal, various other sources of carbon are known to serve as reducing agents during melting of glass. Another means of control is by way of the ratio of air to fuel in the melting furnace. A higher air to fuel ratio produces conditions in the melting furnace that are more oxidizing, which, in turn, leads to a lower ferrous to total iron ratio. Specifying the oxidizing control measures depends upon the particular operating characteristics of a particular melting furnace. In some cases, as with the base glass in Example A, it may be desirable to include no coal or other reducing agent in order to attain the proper glass redox conditions required for the present invention. It has been found that the spectral characteristics of soda lime silica glass change as a result of its subsequent use and processing. More specifically, the glass tends to darken upon exposure to ultraviolet radiation, which in turn lowers LT A , TSUV and TSET. This effect, referred to as solarization, is particularly significant in high iron (Fe 2 O 3 > 0.6 wt.%) and cerium containing glass. In addition, it has been found that tempering also changes the glass's spectral characteristics. As used herein, tempering means heating the glass to above its annealing point temperature, typically about 1000 to 1040°F. (530 to 560°C.) for soda lime silica glass, and quickly cooling it to rapidly drop the glass temperature through the annealing range to the glass annealing point temperature, which is typically about 925 to 970°F. (496 to 521°C.). This operation induces compressive stresses in the outer layers of the glass and tensile stresses in the center. Referring to Table 1, Examples 1 through 3 are modifications of the base glass described in Example A which illustrates the benefits of using titanium oxide in the glass batch to lower ultraviolet transmittance as well as improve luminous transmittance. Table 1 illustrates the base glass modifications and the average spectral properties of the annealed glass based on six samples for each composition. Table 2 shows the change in the percentages of the spectral properties of Examples 1, 2 and 3 due to solarization and tempering. The results for Examples 1 and 2 are based on actual production glass while Example 3 results are based on laboratory melts. (0.154 inch reference thichness) Example 1 Example 2 Example 3 Fe 2 O 3 (wt. %) 0.917 0.523 0.824 Redox 0.262 0.268 0.267 TiO 2 0.017 0.325 0.40 LT A (%) 70.3 79.6 71.3 TSUV (%) 37.0 48.3 36.6 TSIR (%) 19.8 37.9 21.7 TSET (%) 42.7 57.2 43.7 (change in spectral property percentage) Example 1 LT A TSUV TSIR TSET Tempering -0.4 -2.2 0 -0.3 Solarization -0.7 -0.8 0.4 -0.2 Total -1.1% -3.0% 0.4% -0.5% Example 2 LT A TSUV TSIR TSET Tempering -0.2 -1.5 0.2 0 Solarization -0.4 -0.8 0.5 0.1 Total -0.6% -2.3% 0.7% 0.1% Example 3 LT A TSUV TSIR TSET Tempering 0.6 -3.4 0.4 0.6 Solarization -0.4 -0.5 0.5 0 Total 0.2% -3.9% 0.9% 0.6% Referring to Table 1, although all three examples include TiO 2 , the 0.017 wt. % amount in Example 1 is merely a trace amount of titanium oxide resulting from impurities in the glass batch materials. With respect to Examples 2 and 3, it can be seen that the addition of titanium oxide to both a typical soda lime silica glass (Example 2) and a high iron glass (Example 3) reduces the ultraviolet transmittance by 12% and 33%, respectively when compared to the base glass composition (Example A). From this it is clear that titanium oxide or titanium oxide with additional iron (Fe 2 O 3 ) at levels disclosed herein may be used as an ultraviolet radiation absorber to reduce ultraviolet transmittance without the need of other additives. Referring to Table 2, of particular significance is the effect the titanium oxide has on LT A after solarization and tempering. In Example 1, the LT A dropped a total amount of 1.1%. This means it would be expected that the LT A of 70.3% for the annealed glass would eventually drop to about 69.2% after tempering and exposure to ultraviolet radiation. It is noted that this LT A value is below the 70% level required under federal law. In Example 2, the LT A dropped 0.6% which is about half of the drop found in Example 1. In Example 3, the LT A actually increased 0.2%. In comparing the individual effects of solarization and tempering on LT A , solarization reduced the LT A in Example 1 by 0.7% while the reduction in Examples 2 and 3 was only 0.4%. Tempering reduced the LT A in Example 1 by 0.4% while the reduction in Example 2 was only 0.2%. In Example 3, tempering actually increased the LT A by 0.6% rather than decrease it as shown in Example 1. This reduced effect of solarization and tempering on LT A in Example 3 and the unexpected increase in luminous transmittance is particularly significant when compared to Example 1 because, since both compositions have nearly the same high amount of total iron and comparable redox, this effect may be attributed mainly to the presence of titanium oxide. As a result, it is clear that the combination of iron and titanium oxide can actually increase the LT A , thereby allowing the maximum amount of iron to be used and improve the overall solar performance of the glass. Table 2 also indicates that the drop in TSUV for Example 3 is greater than Example 1, with a 50% increase in the contribution due to tempering while the drop due to solarization is reduced. This reduction in TSUV is favorable since TSUV is a spectral property that the glass compositions are attempting to reduce. Again, since the iron content and redox for Examples 1 and 3 are comparable, the advantageous reduction in TSUV is principally attributable to the presence of titanium oxide in the glass. In the present invention, titanium oxide is used to enhance the spectral properties of glass. More particularly, not only is it added to reduce TSUV in annealed glass but also to further reduce the TSUV as a result of tempering and solarization and improve the ultraviolet transmittance performance. In addition, the titanium oxide reduces the drop in LT A by inhibiting solarization and tempering and in some instances, actually improves the LT A . As a result, glass compositions may be formulated with titanium oxide to provide spectral properties, and in particular LT A and TSUV, that are borderline with respect to or do not meet desired specifications, with the expectation that solarization and tempering of the glass will increase LT A and reduce TSUV so that the glass meets the specifications. Tables 3, 4, 5 and 6 illustrate examples of other glass compositions which include high iron along with titanium oxide and their spectral properties prior to solarization and tempering. The spectral data for Tables 3 and 4 are based on laboratory melts at reference thicknesses of 0.154 inch (3.9 mm) and 0.189 inch (4.9 mm), respectively. The spectral data in Tables 5 and 6 was generated using a computer model which predicts the spectral properties of the glass based on the glass composition and redox. (at 0.154 inch thickness) Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Fe 2 O 3 (wt.%) 0.807 0.833 0.830 0.837 0.808 Redox 0.260 0.283 0.270 0.28 0.285 TiO 2 (wt.%) 0.42 0.42 0.42 0.42 0.41 LT A (%) 72.3 72.6 71.1 70.9 71.2 TSUV (%) 37.1 36.2 36.6 35.9 36.8 TSIR (%) 24.0 25.2 21.2 21.6 21.6 TSET (%) 45.4 46.1 43.3 43.4 43.6 (at 0.189 inch thickness) Ex. 9 Ex. 10 Ex. 11 Ex. 12 Ex. 13 Fe 2 O 3 (wt.%) 0.729 0.738 0.764 0.749 0.718 Redox 0.255 0.274 0.251 0.254 0.265 TiO 2 (wt.%) 0.41 0.42 0.47 0.52 0.42 LT A (%) 70.5 70.7 69.9 70.3 70.9 TSUV (%) 34.3 35.4 33.1 32.2 35.7 TSIR (%) 21.0 20.6 20.0 21.3 20.3 TSET (%) 42.8 42.7 41.9 42.7 42.7 (at 0.154 inch thickness) Ex. 14 Ex. 15 Ex. 16 Ex. 17 Ex. 18 Fe 2 O 3 (wt.%) 0.910 0.930 0.845 0.925 0.807 Redox 0.268 0.252 0.265 0.255 0.262 TiO 2 (wt.%) 0.05 0.15 0.30 0.30 0.35 LT A (%) 70.5 70.7 71.7 70.6 72.6 TSUV (%) 36.6 34.7 36.4 34.0 37.0 TSIR (%) 20.9 22.0 23.4 21.8 25.2 TSET (%) 43.1 43.7 45.0 43.4 46.3 (at 0.189 inch thickness) Ex. 19 Ex. 20 Ex. 21 Ex. 22 Ex. 23 Fe 2 O 3 (wt.%) 0.700 0.700 0.690 0.700 0.650 Redox 0.268 0.272 0.265 0.265 0.280 TiO 2 (wt.%) 0.05 0.15 0.30 0.35 0.40 LT A (%) 71.5 71.2 71.6 71.3 71.8 TSUV (%) 37.9 37.1 35.9 37.1 36.7 TSIR (%) 22.6 22.1 23.3 22.9 23.4 TSET (%) 44.6 44.1 44.8 44.4 45.0 It is expected solarization and tempering will effect the glass compositions in Examples 4 through 23 in a manner similar to that shown for Example 3. Based on the test results, it is believed that titanium oxide, in an amount up to 2.0 weight percent of the glass batch may be used to reduce ultraviolet transmittance to a desired level, and in particular to a level not to exceed 38%. The ultraviolet transmittance herein has been reported with reference to the wavelength range 300 to 400 nanometers. Others may use the range 300 to 390 nanometers for measuring ultraviolet. The goal of a maximum ultraviolet transmittance of 38 percent for the present invention would be approximately equivalent to 31 percent if the range 300 to 390 nanometers is used. In addition, if the Rectangular Rule is used over the 300 to 390 nanometer range, the goal of the maximum ultraviolet transmittance would be approximately 34 percent. The glass of the present invention has a distinctly green color. The color may be a matter of taste, and the specific color characteristics need not be considered critical to the present invention, but the glasses that have been made in accordance with the invention have been characterized by excitation purity greater than 1 percent, usually from 2 to 4 percent, and dominant wavelength from 495 to 535 nanometers. In the present invention, titanium was included in the glass composition in the form of titanium oxide. It should be appreciated by those skilled in the art that titanium in forms other than TiO 2 , e.g. an elemental form, may be used in the batch composition but it will be converted to this oxide form within the ranges disclosed herein during the batch melting and refining process. The total solar energy transmittance (TSET) of the glass of the present invention is relatively low, thereby significantly reducing the amount of thermal energy that passes through a window glazed with the glass. Although not critical to the invention, the TSET of the glasses of the present invention are generally lower than 45 percent. The invention has been described with reference to specific embodiments, but it should be understood that variations and modifications that are known to those of skill in the art may be resorted to within the scope of the invention as defined by the claims that follow.

Claims: A green tinted, ultraviolet absorbing, soda lime silica glass having a colorant portion consisting essentially of, on a weight percent basis less than 2.0% TiO 2 and greater than 0.6% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron less than 0.35, and exhibiting ultraviolet transmittance no greater than 38 percent (300 to 400 nanometers) and luminous transmittance (illuminant A) of at least 70 percent, at thicknesses ranging from 0.154 to 0.189 inches. The glass as in claim 1 wherein said colorant portion is 0.6 to 0.95% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.24 to 0.29 and 0.05 to 0.60% TiO 2 . The glass as in claim 2 wherein said colorant portion is 0.65 to 0.925% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.251 to 0.285 and 0.15 to 0.52% TiO 2 .. The glass as in claim 1 wherein said ultraviolet transmittance is no greater than 38 percent and said luminous transmittance is at least 70 percent at a reference thickness of 0.154 inches. The glass of claim 4 wherein said colorant portion is 0.8 to 0.95% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.24 to 0.29 and 0.05 to 0.50% TiO 2 . The glass of claim 5 wherein said colorant portion is 0.807 to 0.925% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.252 to 0.285 and 0.15 to 0.42% TiO 2 . The glass as in claim 1 wherein said ultraviolet transmittance is no greater than 38 percent and said luminous transmittance is at least 70 percent at a reference thickness of 0.189 inches. The glass of claim 7 wherein said colorant portion is 0.6 to 0.8% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.24 to 0.29 and 0.05 to 0.60% TiO 2 . The glass of claim 8 wherein said colorant portion is 0.65 to 0.764% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.251 to 0.280 and 0.15 to 0.52% TiO 2 . The glass of claim 1 wherein the glass exhibits a dominant wavelength from 495 to 535 nanometers. The glass of claim 1 wherein the glass exhibits a total solar energy transmittance less than 45 percent within said thickness range. A method of producing green tinted, ultraviolet absorbing glass exhibiting ultraviolet transmittance no greater than 38 percent (300 to 400 nanometers) and luminous transmittance (illuminant A) of at least 70 percent at thicknesses ranging from 0.154 to 0.189 inches, comprising: melting and forming soda lime silica glass having a colorant portion consisting essentially of, on a weight percent basis, less than 2.0% TiO 2 and greater than 0.6% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron less than 0.35, said glass having a luminous transmittance less than 70 percent; and tempering said glass to increase said luminous transmittance to a value greater than 70 percent. The method as in claim 12 wherein said melting and forming step produces glass having ultraviolet transmittance greater than 38 percent and said tempering step reduces said ultraviolet transmittance to a value no greater than 38 percent. The method of claim 12 wherein said ultraviolet transmittance is no greater than 38 percent and said luminous transmittance is at least 70 percent at a reference thickness of 0.154 inches and said colorant portion is 0.8 to 0.95% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.24 to 0.29 and 0.05 to 0.05% TiO 2 . The method of claim 14 wherein said colorant portion is 0.807 to 0.925% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.252 to 0.285 and 0.15 to 0.42% TiO 2 . The method of claim 12 wherein said ultraviolet transmittance is no greater than 38 percent and said luminous transmittance is at least 70 percent at a reference thickness of 0.189 inches and said colorant portion is 0.6 to 0.8% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.24 to 0.29 and 0.05 to 0.60% TiO 2 . The method of claim 16 wherein said colorant portion is 0.650 to 0.764% iron (expressed as Fe 2 O 3 ) with the ratio of FeO/total iron between 0.251 to 0.280 and 0.15 to 0.52% TiO 2 .

Inventors: GULOTTA JOSEPH A, KRUMWIEDE JOHN F, SHELESTAK LARRY J, GULOTTA, JOSEPH A., KRUMWIEDE, JOHN F., SHELESTAK, LARRY J.
Applicants: PPG INDUSTRIES INC, PPG INDUSTRIES, INC.
Application year: 1993
Main classification: C03C4
IPC codes: C03C3, C03C4