NOVEL FINISHING PROCESS FOR HYDROXY-FUNCTIONAL POLYETHERS

Abstract: A method of preparing a hydroxy-functional polyether comprising contacting (a) a hydroxy-functional polyether containing less than or equal to 200 ppm of a Group IA or Group IIA metal ion, and (b) an acid. Preferably the contact is carried out under reaction conditions such that a salt, which is not suitable to significantly promote trimerization reactions if the hydroxy-functional polyether is reacted with an isocyanate compound, is formed. The amount of acid is sufficient to essentially neutralize residual basic catalyst without requiring additional solids removal steps prior to use of the hydroxy-functional polyether in various applications, such as production of polyurethanes and related products, in which enhanced trimerization may not be desirable. Additional acid may also be added to convert propenyl ether units present in the polyether's backbone to propionaldehyde and the corresponding diol.

Description: NOVEL FINISHING PROCESS FOR HYDROXY-FUNCTIONAL POLYETHERS The present invention relates to the field of polyol finishing processes, particularly to a polyol finishing process having reduced amounts of solid or liquid wastes. Methods for preparing and finishing polyols are numerous in the art. Commonly a catalyst is used in the polyol preparation process, and such catalyst is typically a basic catalyst such as KOH or another alkali metal hydroxide. In this case it is desirable to remove the catalyst or neutralize it with an acid before using the polyol for a final purpose, since the basicity in the polyol may adversely affect the reaction or reactivity which is sought. Such is especially true when a polyol isto be used to prepare a poiyurethane, related product, since the presence of unneutralized catalyst may result in over-catalysis of the reaction desired, for example, a polyurethane-forming reaction. Weak acids and dilute acids can be used for the neutralization and the resultant salts left in the polyol in some cases, but the salts tend to act as catalysts when the polyol is used in certain reactions such as for poiyurethane formation, and enhance the rate of reaction to an undesirable or unacceptable extent. To counter the undesirable effects of leaving the resultant salts in the polyols, various means of their removal have been developed. For example, processes combining crystallization and filtration allow for removal of the salts. Other known means of removing salts include extraction, for example, washing, and adsorption using various adsorbants including, for example, ion exchange media However, the means of removal have some significant disadvantages One disadvantage is that they require one, or more, separate removal steps following the neutralization, which involves in many cases additional time, equipment expense, and/or solvent expense. The waste salt generally must be disposed of in some manner, necessitating additional cost and, in some cases, causing environmental concerns. Finally, the basic catalyst, for example, KOH, which has been converted to the salt (which may be a solid or dissol ed salt) cannot generally be recycled without expensive techniques. It would therefore be desirable in the art to have a means of "finishing" a polyol that would preferably reduce processing steps, reduce waste products that must be removed, and allow easier recycle of at least a portion of the basic catalyst. Accordingly, the present invention provides a method of preparing a hydroxy- functional polyether comprising contacting (a) a hydroxy-functional polyether containing less than or equal to 200 ppm of a Group IA or Group IIA metal ion, and (b) an acid. Preferably suc contact is carried out under reaction conditions sufficient to form a salt in an amount that it is not suitable to significantly promote trimerization reactions if the hydroxy-functionai polyether is reacted with an isocyanate compound. The first requirement of the present invention is a hydroxy-functional polyether, which in one embodiment of the present invention is preferably a crude polyol stream. Such polyol or crude polyol stream may be of a wide range of commonly and conventionally known hydroxy-functional polyethers. These include, for example, polyalkylene polyethers having at least one hydroxyl group, preferably, polyalkylene polyether polyols. These polyethers include the polymerization products of oxiranes or other oxygen-containing heterocyclic compounds, such as tetramethylene oxide prepared in the presence of a catalyst and/or initiated by water, and polyhydric alcohols having from two to eight hydroxyl groups, amine groups, or other active hydrogen sites. Preferably, the polyethers have at least some oxypropyiene units 1 o produced from propylene oxide. As is known to those skilled in the art, the propylene oxide can be homopolymerized or copolymerized with one or more other oxiranes or other oxygen- containing heterocyclic compounds. The oxygen-containing heterocyclic compounds are preferably alkylene oxides. The oxygen-containing heterocyclic compounds, hereinafter exemplified by but ■ 5 not limited to alkylene oxides, are suitably reacted either in mixture or sequentially. When more than one alkylene oxide is used, resulting polyethers can contain random, block, or random-and-block distributions of monomers Mixtures of alkylene oxides most often produce randomly distributed alkylene oxide units. Sequential addition of different alkylene oxides most often produces blocks of the alkylene oxide segments in a polyether chain. 20 Exemplary oxiranes suitable for preparation of polyethers include ethylene oxide, propylene oxide, butylene oxide, amylene oxide, glycidyl ethers such as t-butyl glycidyl ether, and phenyl glycidyl ether. Other suitable oxiranes include 1,2-butylene oxide, 1 ,2-hexylene oxide, 1,2-decene oxide, 2-methoxy propylene oxide, methoxy ethylene oxide, 2,3-butyIene oxide, 2,3-hexylene oxide, 3,4-decene oxide, and 1,1,1-trifluoromethyl-2,3-epoxyoctane. The 25 polyethers are also prepared from starting materials such as tetrahydrof uran copolymerized with alkylene oxide; epihalohydrins such as epichlorohydrin, epiiodohydrin, epibromohydrin, 3,3-dichloropropylene oxide, 3-chloro-l,2-epoxypropane, 3-chloro-1,2-epoxybutane, 3,4- dichioro- 1,2-epoxybutane, and 3,3,3-trichloropropylene oxide; and arylalkylene oxides such as styrene oxide. Preferably, the polyethers are prepared from alkylene oxides having from two 30 to six carbon atoms such as ethylene oxide, propylene oxide, and butylene oxide. More preferably, the polyethers are prepared from at least 10, more preferably at least 50, and even more preferably at least 80 percent of an alkylene oxide selected from the group consisting of propylene oxide, 1,2-butylene oxide, 2,3-butylene oxide and mixtures thereof. Most preferably, propylene oxide is selected Homopoiymers of propylene oxide, or 35 copolyethers of propylene oxide with ethylene oxide, butylene oxide and mixtures thereof, are most preferred for use in the practice of the invention Illustrative alcohols suitable for initiating formation of a polyalkylene polyether include glycerine, ethylene glycol, 1 ,3-propylene glycol, dipropylene glycol, 1 ,2-propylene glycol, 1 ,4-butylene glycol, 1 ,3-butylene glycol, 1 ,2-butylene glycol, 1 ,5-pentane diol, 1 ,7- heptane diol, 1 ,1 ,1-trimethylolpropane, 1 ,1 ,1-trimethylolethane, hexane-1 ,2,6-triol, alpha- methyl glucoside, pentaerythritol, erythritol and sorbitol, as well as pentols and hexols. Sugars such as glucose, sucrose, fructose, and maltose, and compounds derived from phenols such as (4,4'-hydroxyphenyl)2,2-propane, bisphenols, alkylphenols such as dodecylphenol, octylphenol, decylphenol and mixtures thereof, are also suitable for forming polyether polyols useful in the practice of the invention. Mono-alcohols, preferably mono-alcohols having from 1 to 18 . carbon atoms and alkoxy-substituted mono-alcohols, including methanol, ethanol, isomers of propyl alcohol, isomers of butyl alcohol, and ethers thereof, are also suitable for forming the hydroxy-functional polyethers. Amines suitable for reaction with oxiranes to form polyethers include aliphatic and aromatic mono- and polyamines, optionally having substituents such as alkyl, carboxyl, or carboalkoxy groups. Exemplary aromatic amines include aniline, o-chloroaniline, p-phenylene diamine, 1 ,5-diaminonaphthalene, methylene dianiline, the condensation products of aniline and formaldehyde, 2,4-diamino toluene, ethylene diamine, and toluene diamine. Exemplary aliphatic amines include methylamine, triisopropanolamine, isopropanolamine, diethanolamine, triethanolamine, ethylenediamine, 1 ,3-propylenediamine, 1 ,2-propylenediamine, 1 ,4-butylenediamine, and mixtures thereof. Amine based polyols are disclosed in further detail in, for example, U.S. Patent 4,358,547. The polyethers preferably have an average of from 1 to 8, preferably from 2 to 4, hydroxyl groups per molecule. The polyethers also are preferably of relatively high molecular weight, having molecular weights ranging from 88 to 50,000, preferably from 1 ,000 to 7,500. The term "relatively high molecular weight" as used herein refers to molecular weights in the 1 ,000 to 7,500 range. The polyethers may also preferably be capped, for example, with ethylene oxide used to cap propylene oxide, as is well-known to those skilled in the art. The polyethers used in the present invention can be prepared by processes known to those skilled in the art, and are further discussed in, for example, Encyclopedia of Chemical Technology, Vol. 7, pp. 257-262, Interscience Publishers (1951); M. J. Schick, Nonionic Surfactants, Marcel Dekker, New York (1967); British Patent 898,306; and U S Patents 1 ,922,459; 2,871 ,219; 2,891 ,073; and 3,058,921. One or more catalysts are advantageously used in the preparation of the hydroxy functional polyether. Conventional catalysts include, for example, alkali or alkaline earth metals or their corresponding hydroxides and alkoxides, Lewis acids, protonic acids, and coordination compounds. Thus, such catalysts preferably contain a Group IA or Group IIA metal ion. One skilled in the art can readily determine suitable amounts of alkylene oxides, initiators, catalysts and adjuvants as well as suitable processing conditions for polymerizing th alkylene oxides. Additional sources of detail regarding polymerization of alkylene oxides include, for example, .A. Newton, "Propylene Oxide and Higher 1 ,2-Epoxide Polymers" in Encyclopedia of Chemical Technology, 3rd ed., Vol. 10, R. Kirk and D.F. Othmer, John Wiley & Sons, New York (1982,) p.633; D. J. Sparrow and D. Thorpe, "Polyols for Poiyurethane Production" in Telechelic Polymers: Synthesis and Application, E.J. Goethals, CRC Press, Inc., Boca Raton, Florida (1989), p. 181 ; J. Furukawa and T. Saegusa, Polymerization of Aldehydes and Oxides, Intersάence, New York (1963), pp. 125-208; G Odian, Principles of Polymerization, John Wiley & Sons, New York (2nd ed. 1970) pp.512-521 ; J. McGrath, ed., Ring-Opening Polymerization, Kinetics Mechanisms, and Synthesis, American Chemical Society, Washington, D.C- 0985) pp.9-21, 137-147 and 204-217; and U S. Patents 2,716,137; 3,317,508; 3,359,217; 3,730,922; 4,118,426; 4,228,310; 4,239,907; 4,282,387; 4,326,047; 4,446,313; 4,453,022; 4,483,941; and 4,540,828. Preferred catalysts herein are basic catalysts, more preferably hydroxides and alkoxides of alkali and alkaline earth metals, particularly cesium, sodium, potassium, barium, strontium and lithium- Potassium hydroxide is more preferred. When alkoxides are used as catalysts, the alkoxy groups advantageously contain from one to 36 carbon atoms. Exemplary of such alkoxides are alkoxides having anions of propylene glycol, glycerine, dipropylene glycol, and propoxylated propylene or ethylene glycols. Preferably the crude hydroxy-functional polyether is pre-treated to remove excess catalyst. Removal of excess base catalyst is typically desirable because residual catalyst concentrations in the unfinished polyether are generally high, that is, more than 500 ppm, since such concentrations are needed to provide the desired rate of alkoxylation in preparing the hydroxy-functional polyether. To simply neutralize such a high level of catalyst may result in formation of a turbid solid/liquid solution, which may in some cases necessitate processing to remove the large amounts of salts produced thereby, particularly when such is necessary to meet solids content specifications. Therefore, it is commercially preferred to use means other than neutralization to remove the large amount of catalyst prior to finishing the polyether according to the present invention. Typically such means employed include, for example extraction, or the use of ion exchange resins, as are known to and practiced by those skilled in the art. In a preferred embodiment, the excess catalyst is removed to a level of less than or equal to 200 ppm, more preferably less than or equal to 50 ppm, and most preferably less than or equal to 10 ppm. Following removal of excess catalyst, if desired, the hydroxy-functional polyether is then ready for use in the practice of the present invention, in which the hydroxy-functional polyether is contacted with an acid. This acid is preferably any acid that forms a salt with a Group IA or Group IIA metal containing catalyst. The salt resulting from neutralization with the acid is preferably one that does not significantly promote trimerization reactions if or when the polyether is reacted with an isocyanate compound, such as when the reaction is carried out to make a poiyurethane or polyurea material. This means that the degree of trimerization is not great enough to cause deleterious effects that make it desirable to perform additional processing to remove the salt. The resulting salt preferably, therefore, has an anion of a Bronsted acid having a pKa of less than 1. For this purpose Lewis acids, protonic acids and many other acids known to those skilled in the art are suitable. Among the acids suitable for use are, for example, hydrochloric, dodecylbenzenesulfonic, naphthalene sulfonic, trichloroacetic, sulfuric, perchloric, nitric, benzene sulfonic, toluene sulfonic, methane sulfonic, hydrofluoric, phosphoric, formic, acetic, lactic, carbonic, hexanoic and hypophosphorous acid, and mixtures thereof. Monoprotic (basic) acids can be added at stoichiometries relative to the metal ion of preferably less than but approaching 1.0. For diprotic or triprotic acids, it is desirable to use an acid level which results in a pH in the polyol of as close to neutral as possible. Thus, neutral is defined herein as the pH at which there is no excess acid, base or salt. To achieve this level, it is preferred that, for diprotic acids the stoichiometry is from 0.55 to 0.9, and for triprotic acids, from 0.7 to 0.95 moles acid to moles base. It is important that the acid selected be either soluble in the hydroxy-functional polyether or of such low concentration as to form a stable suspension above the solubility level. The solubility of the salt formed by reaction of the acid and the metal ion in part determines the concentration of salt which will remain in solution and provide a consistent and non-turbid solution. Typically, a salt will remain suspended at concentrations of up to about 400 ppm above their solubility limit. The stability of such supersaturating salts is also related to crystal size. Therefore, even though a salt may have minimal impact on performance of the polyether in a given application at supersaturated concentrations, it is desirable that such concentration be less than that at which the salt readily falls out of solution. Thus it is preferred that the product polyether has a stable salt content which results in negligible impact on performance in applications where trimerization is undesirable. It is an advantage of the present invention that the acid can be used for two purposes. First, an amount of acid can be added that is sufficient to neutralize the basic catalyst. Second, a relatively small proportion of excess acid can be concurrently added. The excess acid advantageously serves to catalyze the conversion of propenyl polyether units, present in the hydroxy-functional polyether backbone, to propionaldehyde and the corresponding diol. Since propenyl polyether units may contribute to discoloration of flexible poiyurethane foams prepared using high temperature processing therefrom, or cause other difficulties in other types of processing for which the polyol is to be used, this conversion is in many cases desirable. Such is discussed further in copending U.S. Patent 5,095,061 , issued March 10, 1992, incorporated herein by reference in its entirety. Preferably the excess amount is less than 30 ppm, preferably less than 25 ppm, that is, 0 03 to 5 5 milliequivalents of acid per kilogram of hydroxy-functional polyether (meq acid/kg polyether), more preferably from 0.1 to 1.5 meq acid/kg polyether, and most preferably from 0.3 to 0.5 meq acid/kg polyether, wherein the acid has an aqueous pKa value of less than 2.13. In general the amount of acid to be used is determined in part by the acid's pKa, since the amount of propenyl polyether hydrolyzed is inversely proportional to the pKa of the acid catalyst selected, that is, lower pKa acids tend to produce high levels of hydrolysis, while higher pKa acids show reduced hydrolytic activity and therefore higher amounts of propenyl polyethers remaining in the final product. While it is possible to use a different acid for the conversion of the propenyl ether units present in the polymer backbone to propionaldehyde and the corresponding diol, for convenience it is, o obviously, desirable to simply add a small excess of the same acid used for the neutralization and salt formation. Thus, preferably the acid selected for conversion has the same aqueous pKa value of less than 1. If a different acid is used for the secondary propenyl ether conversion step, acids are preferably selected of pKa's less than 5, preferably less than 2, still more preferably less than 1.5, and most preferably less than 1. 5 Following addition of the acid catalyst the hydroxy-functional polyether/acid catalyst mixture is allowed to react for a time sufficient to allow the conversion of any propenyl polyethers present therein to propionaldehyde. Preferably the mixture is allowed to react from 5 to 120 minutes- Those skilled in the art will balance reaction time with other reaction variables to achieve desired results, and will know to determine the degree of conversion to 0 propionaldehyde by analyzing the product for either propionaldehyde or propenyl polyether content. The rate constant for this reaction is on the order of 1 ,000 liters per mole-minute at 85°C. The contact time is preferably balanced with temperature to avoid degradation of the hydroxy-functional polyether- Degradation can result in discoloration of the product and/or a reduction in the product's reactivity to isocyanate in poiyurethane manufacture. As is known 5 to those skilled in the art, the volatility of the acid should be taken into account in selecting the pressure- A wide range of pressures can therefore be used, and can be easily ascertained by the skilled routineer. The reaction of the acid and the hydroxy-functional polyether is also preferably carried out at an elevated temperature. This temperature is preferably determined by the acid 0 concentration and residence time in the reaction vessel. For most purposes the temperature is preferably in a range of from 25°Cto 200°C, more preferably from 50°Cto 150°C, and most preferably from 90°Cto 120°C. Another advantage of the present invention is that, since excess acid beyond the amount required to achieve neutrality as defined can be added to reduce the propenyl ether 5 content, it is not necessary to control the acid addition for the neutrality as precisely as with some other methods. Rather, an acid scavenger can be used following the hydrolysis step to remove any excess acid present. Preferably, this acid scavenger is an epoxy compound which substantially scavenges the excess. As used herein, the term "substantially" means that at least 85 percent of the acid, by weight, is preferably scavenged, more preferably at least 90 percent, and most preferably at least 95 percent. The epoxy compound can preferably be selected from the group consisting of monoepoxide and polyepoxide compounds including alkylene oxides such as butylene oxide (all isomers), propylene oxide, ethylene oxide, and styrene oxide, as well as glycidyl ethers such as cresyl glycidyl ethers, and phenylglycidyl ether; epoxy resins, including those formed from epichlorohydrin and bisphenols, such as bisphenol A and bisphenol F, as well as aliphatic and cycloaliphatic epoxy resins such as epoxycyclohexyl methyl epoxycyclohexyl carboxylates; epoxidized soybean oils; cresol resins; Novolac resins; and mixtures thereof. The epoxy compounds preferably have structures represented by Formula 1 : H \ C C / \ R' R Formula 1 wherein R and R' (referred to hereinafter as R groups) are independently hydrogen or inert groups or R and R' together form an inert cyclic structure. Inert groups are groups which do not significantly reduce polyether stability under conditions suitable for scavenging the acid. Suitable inert groups include, for instance, additional epoxy groups, halogens, ester, alkyl, aryl, aralkyl, cycloalkyl, alkoxy, and aryloxy, aralkoxy and cycloalkoxy groups, which groups are unsubstituted or substituted by inert groups. Suitable halogens are chlorine, bromine, fluorine and iodine. Preferably R and R' together have fewer than 60 carbon atoms. When R and R' together form an inert cyclic structure, that structure is preferably a cyclohexyl ring having inert groups as substituents. Preferably, the weight percent of oxirane oxygen in the epoxy compound is from 3 to 30, more preferably from 6 to 12 percent. Epoxy compounds having more than one epoxy group preferably have molecular weights of from 100 to 1,000. Preferred epoxy com pounds are epoxy com pounds other than the alkylene oxides used in preparation of the polyether, such as ethylene oxide, propylene oxides and butylene oxides, and include other monoepoxy compounds and epoxy resins. Epoxy resins, that is, molecules which have at least two glycidyl groups and which cure readily with amines, are particularly preferred. Preferably, the epoxy compound is added in an amount sufficient to scavenge the acid catalyst, preferably from 1 to 300 epoxy equivalents (eq) per 1 acid catalyst eq, more preferably from 5 to 100 epoxy eq per acid catalyst eq, and most preferably from 10 to 50 epoxy eq per acid catalyst equivalent. The term "epoxy equivalent" as used herein means that amount of epoxy compound which contains an average of one epoxy group. The term "acid catalyst equivalent" as used herein means that amount of acid catalyst which contributes an average of one hydrogen ion in aqueous solution. An advantage of the present invention is that proportionately very little soluble acid catalyst is needed to convert virtually all of the propenyl polyether to propionaldehyde, and therefore very little epoxy compound is needed to scavenge the acid. Thus, contamination of the end product hydroxy-functional polyether is reduced or eliminated. Contact of the epoxy compound and acid in the hydroxy-functional polyether preferably occurs at a temperature that is sufficient for reaction of the epoxy compound to reduce acidity, but insufficient to result in undesirable degradation of the polyether. A sufficient temperature is preselected such that the acidity is reduced within a time acceptable for a specific application. Preferably, the temperature is from 0°C, more preferably from 50°C, and most preferably from 110°, to 150°C, more preferably 135°C, and more preferably 130°C, These temperatures are suitably maintained for a time sufficient for the epoxy compound to react with the acid, preferably for at ieast 1 minute, more preferably for from 20 to 120 minutes. As is known to those skilled in the art, temperature and residence time are preferably balanced to achieve the desired degree of removal of the acid catalyst. Conditions suitable for reaction of the hydroxy-functional polyether with the epoxy compound are preferably avoided. For instance, materials known to catalyze the reaction of epoxy compounds with hydroxy-functional polyethers are preferably substantially absent or, at most, present in insufficient quantities to result in significant reaction. It is also preferred that the conditions of temperature and pressure to which the polyether is exposed are not sufficient to interfere undesirably with acidity reduction or to measurably alter the physical properties of the polyether. According to the present invention, the epoxy compound and polyether are contacted or admixed using conventionally known mixing apparatus. Local concentrations of epoxy compound are advantageously and conveniently avoided by thorough mixing. The mixing can be carried outbatchwise or continuously in accordance with procedures within the skill of those in the art. Following addition of the epoxy compound to scavenge the acid, it is preferable to remove the propionaldehyde and water. To accomplish this the hydroxy-functional polyether is preferably stripped according to means and methods generally known to those skilled in the art. For example, counter-currentsteam stripping using 2 percent steam with vacuum stripping at 65 mm Hg vacuum and 120°Cis an effective means of substantially removing the propionaldehyde. Counter-current stripping using other inert gases, for example, nitrogen, is also suitable. As used herein, the term "substantially" means that at Ieast 85 percent by weight of the propionaldehyde and water is preferably removed, more preferably at Ieast 90 percent, and most preferably at Ieast 95 percent. Following the acid neutralization of the present invention, which may in some cases be desirably coupled with hydrolysis using excess acid to convert the propenyl ethers to propionaldehyde, the resultant product is a hydroxy-functional polyether generating less waste, particularly solids. This is because the salts formed in neutralizing the basic catalyst by using specific acids, for example, salts that do not promote trimerization reactions, do not require removal before the hydroxy-functional polyether can be used for purposes wherein trimerization is involved or is a potential side reaction, for example, formation of polyurethanes. Thus, the resultant polyether product will not exhibit a catalytic effect, increasing trimerization, that is detrimental to the process in which the product is being employed. Since removal of the resultant salts, which are preferably present in small amount because of the reduction in catalyst level prior to the hydrolysis step, is not necessary, the need to use or build, filters, filter aid pots, pumps, rundown tanks, associated piping, etc., for finishing facilities is eliminated. At the same time solid waste handling is reduced and disposal problems eliminated. Finally, if a substantial amount of residual catalyst is removed priorto reaction with the acids, the catalyst, for example, KOH, is therefore almost fully recyclable. The following examples are given to illustrate the present invention and are not intended to be, nor should they be construed as being, limitative of its scope. All parts and percentages are by weight unless otherwise indicated. Comparative Example 1 A crude, experimental glycerine-initiated, ethylene oxide/propylene oxide heterofed polyether triol (designated Polyol A), having a molecular weight of about 3, 100, was prepared using conventional methods and using potassium hydroxide to initiate the alkoxylation. An extraction was carried out to remove excess potassium hydroxide to a level of about 50 ppm. The polyol was then mixed with an aqueous solution of hydrochloric acid in a static mixer reactor which approaches plug flow behavior for 10 minutes at 120°C. 1 ,200 lb. of crude polyether triol were processed with this static mixer to produce an intermediate product containing about 5,000 ppm water, 35 ppm potassium, and 46 ppm chloride. About 500 ppm of 3,4-epoxy cyclohexyl methyl-3,4-epoxy cylohexylcarboxylate resin was added to the mixture to scavenge the excess acid. It was reacted for 1 minute and then water was stripped from the polyol to reach a level of 500 ppm. Finally, butylated hydroxytoluene (BHT) and 4,4-di(αα-dimethylbenzyl diphenylamine) were added in amounts of 4,500 ppm and 2,000 ppm, respectively, to serve as oxidation inhibitors. The final product had potassium level of 34 ppm. A control polyol, designated Polyol B, was also prepared, starting with the same crude polyol (glycerine-initiated, ethylene oxide/propylene oxide heterofed polyether triol, having a molecular weight of 3,100, prepared using conventional methods and using potassium hydroxide to initiate the alkoxylation), which had been subjected to an extraction t remove the excess potassium hydroxide to a level of about 50 ppm. However, treatment with hydrochloric acid and the epoxy resin was not carried out at this point, but rather, the polyol was processed through a filter using magnesium silicate and perlite filter aid to reduce the potassium to less than 5 ppm. Then 10 ppm HCI acid was added to neutralize the potassium hydroxide such that 8 ppm excess acidity was present. Additional processing, including removal of water and addition of BHT and 4,4-di(α,α-dimethylbeπzyl diphenylamine), were carried out exactly as with the experimental polyol The experimental polyol and the control polyol were then used to prepare poiyurethane foams using the polyol formulation shown in Table 1 below. Table 1 Polyol A is a glycerine-initiated, ethylene oxide/propylene oxide heterofed polyol having a molecular weight of about 3,100. Polyol B is essentially the same as Polyol A, but processed by conventional methods. Amine Catalyst is DABCO-8264*, which is available from Air Products and Chemicals, Inc. Tin Catalyst is T-95 stannous octoate, available from Air Products and Chemicals, Inc. Silicone Surfactant is DC-5160, available from Air Products and Chemicals, Inc. Toluene diisocyanate is an 80/20 blend of 2,4'- and 2,6'-toIuene diisocyanate, respectively. All components of each formulation, each containing either Polyol A or Polyol B, were processed on a VARIMAX* foaming machine, available from Periphlex, Inc., at an isocyanate index of 98 using conventional methods. Processing conditions included a head pressure of 5 psi; trough plate setting of 25.1 ; pivot one plate setting of 13.9; pivot two plate setting of 9.9; pivot three plate setting of 5.3; pivot four plate setting of 0.1 ; converter revolutions per minute (rpm) of 900; mixer rpm of 500; trough size of 24 liters; width of 54 inches; run time of 1 -0 minute; converter speed of 13.0; and total height of 34 inches (86.4 centimeters). Physical property tests were conducted on the resultant box foams, and compared in Table 2. Table 2 • Not an example of the present invention Comparative Example 2 Another crude experimental polyol, designated Polyol C, was prepared. It was a sucrose/glycerine-co-initiated, ethylene oxide/propylene oxide heterofed polyol of 3,500 molecular weight and average functionality of greater than 3. The polyol was prepared using standard alkoxylation with potassium hydroxide as a catalyst. Following reaction to form the polyol, an extraction was carried out to remove excess potassium hydroxide to a level of 50 ppm. The polyol was then mixed with an aqueous solution of hydrochloric acid in a static mixer which approached plug flow behavior for 10 minutes at 120°C. 1 ,200 1b. (545.5 kg) of crude polyether polyol were processed with this static mixer to produce an intermediate product containing 5,000 ppm water, 19 ppm potassium, and 26 ppm chloride. About 500 ppm of 3,4-epoxy cyclohexyl methyl-3,4 epoxy cylohexyl carboxylate resin was added to the mixture to scavenge the excess acid. It was mixed for 1 minute and the water was stripped from the polyol to reach a level of 500 ppm. Finally, butylated hydroxy- toluene (BHT) and 4,4-di(αα-dimethyl benzyl diphenylamine) were added in amounts of 5,000 ppm and 1,500 ppm, respectively, to serve as oxidation inhibitors. The final product had a potassium level of 19 ppm. A control polyol, designated Poiyol D, was also prepared, starting with the same crude polyol (sucrose/gtycerine-co-initiated, ethylene oxide/propylene oxide heterofed polyether triol, having a molecular weight of 2,400, prepared using conventional methods and using potassium hydroxide to initiate the alkoxylation), which had been subjected to an extraction to remove the excess potassium hydroxide to a level of 27 ppm. However, treatment with hydrochloric acid and the epoxy resin was not carried out at this point, but rather, the polyol was processed through a filter using magnesium silicate and perlite filter aid to reduce the potassium hydroxide to 1 ppm. No additional acid was added thereafter. Additional processing, including removal of water and addition of butylated hydroxytoluene (BHT) and 4,4-di(α,α-dimethylbenzyl diphenylamine), were carried out exactly as with the experimental Polyol C The experimental polyol, Polyol C, and the control polyol, Polyol D, were then analyzed to determine certain properties known to affect reactivity in poiyurethane processing- Table 3 shows the results. Table 3 *Notan example of the present invention, "nd" means not detectable. The experimental polyol and the control polyol were then used to prepare poiyurethane foams as described in Comparative Example 3. Comparative Example 3 About 0.5 g amounts of various potassium compounds (identified in Table 6) were added to individual samples (20 ml each) of a polyol identical to Polyol A of Comparative Example 1. This polyol had been treated according to the process of the present invention to neutralize the KOH to a level of 25 ppm, and also contained 2,000 ppm water. Oxidation reduction additives were not used. The individual mixtures were placed in open 100 ml tripours in an oven at 110°C- Color formation was observed and recorded in Table 4. Ultraviolet (uv) light analysis was done using a 0.5 cm sapphire cell, at ambient temperature on certain samples at 340 nanometers (nm) absorbance and recorded in Table 5. Table 4 0 5 Table 5 0 5 *absorbance tested but not detectable. - not measured 30 Comparative Example 4 Three separate portions of a poiyol identical to Polyol C of Comparative Example 2 were prepared, except that the KOH level was 170 ppm, water content was 2,000 ppm, and no oxidation reduction additives were used. The portions were treated as follows: - jr Portion 1 : This sample (about 250 g) was placed on a rotary evaporator for about 30 minutes at full vacuum and 120°C. Vacuum was then held over the sample for 15 minutes until the temperature was reduced to below 80°C. About 30 mi of the solution was then placed in a 100 ml tripour and the tripour was placed in an oven at 125°C. Portion 2: This sample (about 238.1 g) was mixed with 0.7226 g of 1.0007 N HCl (about 1.0 stoichiometry). Processing was continued as with Portion 1. Portion 3: This sample (about 271.6 g) was mixed with 0.0949 g of 80 percent by weight phosphoric acid (about 1.0 stoichiometry). Processing was continued as for Portion 1. Ultraviolet (uv) lightanalysiswas done on the portions at 340 nm absorbance and recorded in Table 6. At the time of 1200 minutes the KOH solution had a yellow color, while both neutralized samples were colorless- Table 6 Comparative Example 5 Neutralization of portions of a polyol identical with Polyol C of Comparative Example 2 was carried out according to the process of the present invention. Eight different neutralizing agents were employed (toluene sulfonic acid (TSA), lactic acid, acetic acid, formic acid, dodecyl benzene sulfonic acid (DBSA), methane sulfonic acid (MSA), and hydrochloric acid (HCl), and a control experiment in which no salts were present. Additional testing was done in which KCI was added to the polyol. Two samples were run using hydrochloric acid, with the run designated as "HCl #1 " being performed on polyol which had been first extracted to reduce the catalyst, prior to neutralization, using toluene sulfonic acid. The run designated as "HCl #2" did not receive the prior extraction. In each case the potassium salt of the neutralizing agent was allowed to remain in the polyol at a level of 100 ppm. Each of the six samples was then used in the process described in Example 1 to prepare a foam according to the formulations shown in Table 7, using an isocyanate index of 95. Table 7 1 Polyol C is a sucrose/glycerine-co-initiated, ethylene oxide/propylene oxide heterofed polyol having a molecular weight of about 3,500 and an average functionality greater than about 3 2 Amine Catalyst is DABCO-8264*, which is available from Air Products and Chemicals, Inc. 3 Tin Catalyst is T-9*, stannous octoate, available from * Air Products and Chemicals, Inc. 4 Silicone Surfactant is TEGOSTAB BF-2370*, available from Goldschmidt Chemical Corporation. 5 Toluene diisocyanate is an 80/20 blend of 2,4'- and 2,6'-toluene diisocyanate, respectively. Processing was done to prepare laboratory scale box foam, using a total reactants charge of 600 g for each and foaming in a 15 x 15 x 9 inch lined box. Physical properties were measured and recorded in Table 8. Table 8 ''Not an example of the present invention Comparative Example 6 Two 1 ,000 ml samples of a polyol identical to Polyol A were prepared using the process of the present invention such that the KOH content was reduced to 27 ppm. The polyol samples were kept at a temperature of 100°C. One sample was used as a control. The other sample was placed in a 1 ,000 ml plastic container and 5 g of butylated hydroxytoluene (BHT) was added to it and stirred. After 30 seconds a blue tint was observed in the BHT- containing sample, while the control sample remains clear. After 10 1 f) minutes the color in the BHT-containing sample was lime green. The control sample remained clear. 15 20 25 30

Claims: 1. A method of preparing a hydroxy-functional polyether comprising contacting (a) a hydroxy-functional polyether containing less than or equal to 200 ppm of a Group IA or Group IIA metal ion, and (b) an acid. 2. The method of Claim 1 wherein the contacting is carried out under reaction conditions such that a salt is formed in an amount that is not suitable to significantly promote trimerization reactions if the hydroxy-functional polyether is reacted with an isocyanate compound. 10 3. The method of Claim 1 wherein the hydroxy-functional polyetner is selected from polyethers prepared from alkylene oxides having from 2 to 6 carbon atoms. 4. The method of Claim 1 wherein the Group IA or Group 15 IIA metal ion is selected from potassium, sodium, barium, and mixtures thereof. 5. The method of Claim 1 wherein the acid is selected from hydrochloric, dodecylbenzene sulfonic, naphthalene sulfonic, trichloroacetic, sulfuric, perchloric, nitric, benzene sulfonic, toluene 20 sulfonic, methane sulfonic, hydrofluoric, phosphoric, formic, hexanoic, lactic, acetic, carbonic and hypophosphorous acids, and mixtures thereof. 6. The method of Claim 5 wherein the acid is selected from hydrochloric, dodecylbenzene sulfonic, methane sulfonic, acetic, formic and phosphoric acids, and mixtures thereof. 25 7. The method of Claim 1 wherein the acid has a pKa of less than 5. 8. The method of Claim 1 wherein the acid has a pKa of less than 2. 30 9. The method of Claim 1 wherein the acid has a pKa of less than 1.

Inventors: FRIEDLI HANS R, SUPPES GALEN J, FRIEDLI, HANS, R., SUPPES, GALEN, J.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1993
Main classification: C07C41
IPC codes: C08G65