INTUMESCENT ONE-COMPONENT SEALANT

Abstract: The invention relates to an intumescent one-component sealant based on polyurethane and containing an intumescent agent and a vitreous fusible filler. The intumescent agent and the vitreous filler have been pretreated by reaction with an isocyanate having a functionality of at least 2. The sealant is stable in storage and is an effective fire barrier in the event of fire.

Description: INTUMESCENT ONE-COMPONENT SEALANT. The invention relates to an intumescent one-component sealant comprising a polyurethane binder, an intumescent agent and, if required, conventional additives, to a process for preparing such a sealant, and to the use thereof for sealing openings or joints in construction parts. One- and two-component sealants based on polyurethane are often used as high-performance sealing materials in the construction industry, for example for the elastic sealing of settlement joints between prefabricated concrete elements. In the event of fire, the sealing material is generally not capable of preventing, as fire barrier, passage of the flames through the joint for more than 20 minutes. Specially formulated sealants are therefore necessary to keep the joints closed for hours even in the event of fire. It is already known, namely by EP-A-420302, that a composition of a polyurethane binder, an intumescent substance and glass frits as glass-like melting filler provides an intumescent material ; this document however does not provide an indication about a preparation of the glass-like filler by means of an isocyanate. In DE-A-3421086 it is described the reaction of an aqueous alcaline silicate solution with a polyisocyanate and a polyol. The reaction product however is a tridimensional crosslinked organomineral without the property of intumescence. From DE-A- 11 18966 it is known a flame -resistant sealant composition which comprises a crosslinked polyurethane and a silicic acid filler which before crosslinking of the binder was dissolved, at least in colloidal state, in a fluid ad duct of a component comprising OH- groups and an isocyanate. This composition however is not intumescent and the silicic acid was not prepared with an isocyanate alone. JP-A-52/ 102395 describes a fire-resistant sealing composition made from a foamable polyurethane and an aqueous sodium silicate solution. However in this document can be found no mention of the addition of a glass-like melting filler prepared from an isocyanate to intumescent polyurethane sealing composition. The purpose of the present invention is to provide intumescent one-component sealants which are in particular stable on storage and are an effective fire barrier in openings and joints of construction parts in the event of fire. A second objective of the present invention is to indicate a process for preparing a sealant of this kind. The present invention therefore relates to an intumescent one-component sealant comprising a polyurethane binder and an intumescent agent and, if required, conventional additives, characterised in that it further contains a vitreous fusible filler and in that the intumescent agent and the vitreous filler have been subjected to a pretreatment by reaction with an isocyanate having a functionality of at least 2. The polyurethane binder used in the sealant according to the invention is, for example, a polyurethane prepolymer. The starting components for preparing such polyurethane prepolymers, such as polyols, isocyanates and catalysts, are very well known in polyurethane chemistry. The sealants according to the invention are moisture-curing. In order to prevent premature curing before application, the sealants are therefore stored in impermeable containers, for example in aluminium or plastics cartridges, with the exclusion of moisture. The vitreous filler used according to the invention preferably has a wide melting range of approximately 300 to 900°C and serves to improve the properties of the sealant as a fire barrier in the event of fire. Glass frit materials are especially suitable for this purpose, a glass frit material having a melting range of about 350 to 700°C being especially preferred. Such vitreous fillers having a wide melting range are available commercially, for example under the tradename "Ceepree" for a glass frit material having a melting range of 350- 700°C, which devitrifies above 800°C and forms a fireproof barrier layer. Suitable intumescent agents are the substances conventionally used, for example, ammonium polyphosphate, expandable graphite, dicvandiamide, melamine and its derivatives, such as melamine phosphate, melamine resins or melamine cyanurate, guanidine salts and cyanuric acid derivatives. Especially advantageous results are obtained with ammonium polyphosphates. These are compounds of the general formula (NH 4 PO 3 ) n where n = 20-1000 and molecular weights of approximately 2000 to 100,000. Such compounds are also available commercially, for example under the name Phos-chek. The intumescent agents are suitably used in a quantity of approximately 2 to 10 % by weight and the vitreous filler in a quantity of approximately 5 to 15 % by weight, in each case based on the total weight of the sealant. Surprisingly, it is possible according to the present invention to obtain a storage-stable one-component sealant based on polyurethane if the intumescent agent and the vitreous fusible filler are subjected to a pretreatment by reaction with an isocyanate having a functionality of at least 2 before being mixed with the polyurethane binder. It is assumed that the reactive surfaces of the intumescent agent and the filler are blocked or desactivated by this pretreatment. The term "isocyanate having a functionality of at least 2" here is taken to mean isocyanates having 2 or more isocyanate groups per molecule. Suitable isocyanates for this reaction are conventional diisocyanates and low molecular-weight polyisocyanates, aromatic diisocyanates such as diphenylmethane 4,4'-diisocyanate (MDI), toluylene diisocyanate (TDI) and derivatives thereof being especially preferred. The invention likewise relates to a process for preparing a one-component sealant of this type, which is characterised in that an intumescent agent and a vitreous fusible filler are reacted with an isocyanate having a functionality of at least 2 and the components thus pretreated are mixed with a polyurethane binder and, if required, conventional additives. Conventional additives which can be added to the sealant according to the invention are, for example, thickening agents, such as bentonite or silicic acid, pigments, such as titanium dioxide, flame retardants, such as antimony trioxide, fillers such as chalk or silicates and the like. The one-component sealant according to the invention is a very effective fire barrier in openings and joints in construction parts. Furthermore it has the advantages of a moisture-curing one- component sealant, such as simple application, outstanding mechanical properties, such as low modulus, high extensibility and elastic recovery, good adhesion to many substrates and good weather resistance. The invention is explained in greater detail in the following examples, where all parts are indicated by weight. Comparative Example 1 The following basic formulation is used : 1. Titanium dioxide 8.0 2. Diisodecyl phtalate 21.0 3. Chalk (ground ; dried for 24 hours at 130°C) 30.0 4. PVC powder/emulsion polymer 10.0 5. Prepolymer (45.73 % polyether diol* 43.45 % polyether triol** and 10.8 % TDI, free NCO = 440 mVal/kg 30.0 6. Tosyl isocyanate 0.5 7. Adhesion promoter (Union Carbide Silane A 187) 0.4 8. Dibutyltin dilaurate 0.1 * Molecular weight approximately 2000, based on polypropylene glycol. * * Molecular weight approximately 4000, based on polypropylene glycol. Components Nos. 1 to 5 are homogeneously mixed with stripper in a vacuum dissolver, then component No. 6 is added and mixed for a further 15 minutes. Finally components Nos. 7 and 8 are added and the mixture is mixed under vacuum for 10 minutes and degassed. Comparative Example 2 Components Nos. 1 to 5 from Comparative Example 1 are mixed together with 5.0 parts of ammonium polyphosphate, the rest of the procedure being as in Comparative Example 1. Comparative Example 3 To components Nos. 1 to 5 from Comparative Example 1 are added 5.0 parts of ammonium polyphosphate and 10.0 parts of a commercial glass frit material (melting range 350-700°C, dried for 24 hours at 130°C) , the rest of the procedure being as in Comparative Example 1. Example 1 To components Nos. 1 and 2 from Comparative Example 1 are added : 5.0 parts of ammonium polyphosphate, 10.0 parts of a commercial glass frit material (melting range 350-700°C, dried for 24 hours at 130°C), 1.0 part of a commercial aromatic diisocyanate* 0.02 part of dibutyltin dilaurate (* an 80:20 mixture of MDI and the uretonimine derivative of MDI, i.e. the cyclo adduct of MDI to the carbodiimide of the MDI R — N = C — N — R i i R— N — C = O where R = C 6 H 4 - CH 2 - C 6 H 4 NCO). Mixing is continued slowly for one hour at 60 to 70°C in order to complete the reaction. After cooling to 45°C components Nos. 3 to 5 according to Comparative Example 1 are added, the rest of the procedure being as in comparative Example 1. Example 2 To components Nos. 1 and 2 from Comparative Example 1 are added : 3.0 parts of ammonium polyphosphate 10.0 parts of a commercial glass frit material (melting range 350-700°C, dried for 24 hours at 130°C), 0.8 part of MDI (flakes) 0.02 part of dibutyltin dilaurate. The rest of the procedure is as in Example 1. Example 3 To components Nos. 1 and 2 from Comparative Example 1 are added 5.0 parts of melamine cyanurate 10.0 parts of a commercial glass frit material (melting range 350-700°C, dried for 24 hours at 130°C), 1.0 part of a commercial aromatic diisocyanate (as in Example 1) 0.02 part of dibutyltin dilaurate. The rest of the procedure is as in Example 1. Testing the effectiveness as a fire barrier : Test specimens (12 x 12 x 15 mm, between concrete) are prepared from the sealants according to Comparative Examples 1 to 3 and Examples 1 to 3 and stored at room temperature for 4 weeks. A Simmon-Mύller furnace is heated to > 1000°C. The cover of the furnace has a gap of approximately 12 x 50 mm. In each case one test specimen is fixed over this gap so that the sealant closes the gap (test joint). The time for which the gap remains closed, that is to say until the sealant "burns through", is recorded. The results are shown in the table below. Testing the storage stability : The sealants prepared according to Comparative Examples 1 to 3 and Examples 1 to 3 are filled into cartridges. The viscosity is determined 4 hours after preparation (ηl). One further cartridge in each case is stored for 4 weeks at 40°C. After this time the viscosity of the stored specimen is determined again. The ratio η2/ηl serves as a measure of the storage stability. The results are also shown in the table below. Table

Claims: CLAIMS 1. Intumescent one-component sealant comprising a polyurethane binder and an intumescent agent and, if required, conventional additives, characterised in that it further contains a vitreous fusible filler and in that the intumescent agent and the vitreous filler have been subjected to a pretreatment by reaction with an isocyanate having a functionality of at least 2. 2. Sealant according to Claim 1 , characterised in that it contains an ammonium polyphosphate as intumescent agent. 3. Sealant according to Claim 1 or 2, characterised in that the vitreous filler has a melting range of 300 to 900°C. 4. Sealant according to Claim 3, characterised in that the vitreous filler is a glass frit material. 5. Sealant according to one of claims 1 to 4, characterised in that the intumescent agent is present in a quantity of 2 to 10 % by weight, based on the total weight of the sealant. 6. Sealant according to one of claims 1 to 5, characterised in that the vitreous filler is present in a quantity of 5 to 15 % by weight, based on the total weight of the sealant. 7. Sealant according to one of claims 1 to 6, characterised in that the isocyanate is chosen from aromatic isocyanates. 8. Sealant according to Claim 7, characterised in that the aromatic isocyanate is chosen from diphenylmethane 4,4'- diisocyanate, toluylene diisocyanate and derivatives thereof. 9. Process for preparing an intumescent one-component sealant according to Claim 1 , characterised in that an intumescent agent and a vitreous fusible filler are reacted with an isocyanate having a functionality of at least 2 and the components thus pretreated are mixed with a polyurethane binder and, if required, conventional additives. 10. Use of a one-component sealant according to one of Claims 1 to 8 for the effective sealing, in the event of fire, of openings and joints in construction parts.

Inventors: JOACHIMI ROLAND, JOACHIMI, ROLAND
Applicants: BOSTIK AB, BOSTIK AUSTRALIA PTY LTD, BOSTIK INC, BOSTIK LTD, BOSTIK SA, JOACHIMI ROLAND, BOSTIK AUSTRALIA PTY. LTD, BOSTIK INC., BOSTIK LIMITED, BOSTIK S.A.
Application year: 1993
Main classification: C09K21
IPC codes: C08K9, C09K3, C09K21