Method for making rare earth superconductive composite

Abstract: A method for making a rare earth superconductive composite including a matrix of REBa₂ CU₃ O 7-x grains and, uniformly dispersed therein, fine particles of RE₂BaCuO₅, wherein RE is at least one element selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu, and x ranges from 0 to 1, includes the steps of: (1) forming a compacted mass by application of pressure out of a powder material including REBa₂ Cu₃ O 7-x and RE₂BaCuO₅ in a powder form wherein powder particles of REBa₂ CU₃ O 7-x have an average diameter up to 6 µm and a maximum diameter up to 2⊘ µm, and powder particles of RE₂BaCuO₅ have an average diameter up to 6 µm and a maximum diameter up to 2⊘ µm; (2) heating the compacted mass to a temperature which is higher than an incongruent melting temperature of REBa₂ CU₃ O 7-x and which is lower than an incongruent melting temperature of RE₂BaCuO₅ so as to partially melt and decompose the REBa₂ CU₃ O 7-x in the mass into a melt and RE₂BaCuO₅ in a solid state; (3) gradually cooling the mass so as to recrystallizes REBa₂Cu₃ O 7-x from the melt wherein fine particles of RE₂BaCuO₅ are dispersed in grains of REBa₂ CU₃ O 7-x ; and (4) annealing the mass in an atmosphere containing oxygen for a time sufficient for the requisite amount of oxygen to diffuse into the mass. Fine particles of RE₂BaCuO₅ in the composite have a diameter up to 2⊘ µm, and and work as pinning centers. The small powder particles of REBa₂ Cu₃ O 7-x and RE₂BaCuO₅ in the compacted mass makes RE₂BaCuO₅ particles dispersed in the resulting composite smaller thereby improving critical current density of the composite.

Description: Background of the Invention The present invention relates to a method for making a rare earth superconductive composite. A superconductive material loses electrical resistance at temperatures at or below a critical temperature. Recently, a new class of rare earth-alkaline earth-copper oxide was discovered to be a superconductive material having a critical temperature above 77K, which is a boiling point of liquid nitrogen. This type of compounds has an approximate unit formula of YBa 2 Cu 3 O 7-x , where x is typically about close to ⊘, and x represents oxygen deficiency. Crystalline structure of this type of rare earth oxide superconductors have a perovskite structure with the oxygen deficiency. Any superconductor can be classified into either type I superconductor or type II superconductor. When the type I superconductor is exposed to a magnetic field below the critical magnetic field, the superconductor shows complete diamagnetism due to the Meissner effect, and magnetic flux can not penetrate inside the superconductor. A supercurrent flows at the surface of the superconductor so as to cancel the external magnetic field. At the critical magnetic field the superconductor undergoes a transition from a superconductive phase to a non-superconductive phase, and magnetic flux begins to penetrate the inside the superconductor. The type II superconductor exposed to magnetic field below the first magnetic field behaves like the type I superconductor, and magnetic flux can not penetrate inside the superconductor due to the Meissner effect. At the first critical magnetic field the superconductor undergoes a transition from a superconductive phase to a mixed phase, and magnetic flux begins to penetrate the inside the superconductor while maintaining superconductivity. At the second critical magnetic field the type II superconductor undergoes a phase transition from this mixed state to a non-superconductive state. The oxide superconductor belongs to type II superconductor. When an electric current is applied to the type II superconductor in the mixed state, magnetic flux moves due to Lorenz force thereby showing electrical resistance. However, when pinning centers, which include, for example, diamagnetic particles, are dispersed in the superconductor, the magnetic flux penetrates though the pinning centers so that magnetic flux is prevented from moving. Recently, active studies have been reported to obtain a rare earth oxide superconductor having fine particles dispersed therein acting as pinning centers. Japanese Patent Application Laid-Open No. 4-224111 discloses a use of a platinum group element with a partial melt process so as to disperse fine particles of RE 2 BaCuO 5 (RE is Y, Gd, Dy, Ho, Er or Yb) in superconductive grains of REBa 2 Cu 3 O 7-x . The fine particles of RE 2 BaCuO 5 work as pinning centers to prevent magnetic flux from moving in the resulting superconductive composite. The process includes the steps of: heating a green compact including REBa 2 Cu 3 O 7-x and at least one element of Rh, Pt, Pd, Ru, Os, and Sc to a temperature higher than an incongruent melting temperature of REBa 2 Cu 3 O 7-x to partially melt REBa 2 Cu 3 O 7-x ; slowly cooling the resulting material to recrystallize REBa 2 Cu 3 O 7-x from the melt. The presence of a platinum group element, such as platinum and rhodium, in the melt is associated with a mechanism to disperse fine particles of RE 2 BaCuO 5 in the slowly cooling step. Ogawa, Yoshida and Hirabayashi in ISTEC Journal, Vol. 4, No. 3, 1991, p. 3⊘, describes a generally similar concept of a partial melting process in which a green compact includes a small amount of a platinum group element to make a rare earth superconductive composite in which fine particles of Y 2 BaCuO 5 , acting as pinning centers, are dispersed in superconductive grains of REBa 2 Cu 3 O 7-x . Summary of the Invention An object of the present invention is to improve a critical current density of a superconductive composite in which fine particles of RE 2 BaCuO 5 , which work as pinning centers, are dispersed in a matrix of superconductive REBa 2 Cu 3 O 7-x grains. In the present invention, small powder particles are used for both REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 in a compacted mass for the partial melt process, thereby making RE 2 BaCuO 5 particles dispersed in the resulting composite smaller and increasing a number of the RE 2 BaCuO 5 particles in a unit volume of the resulting composite. Smaller pinning centers and fine dispersion of pinning centers improve critical current density of the superconductive composite. The present invention provides a method for making a rare earth superconductive composite induding a matrix of REBa 2 Cu 3 O 7-x grains and, uniformly dispersed therein, fine particles of RE 2 BaCuO 5 , wherein RE is at least one element selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu, and x ranges from ⊘ to 1, which comprises the steps of: (1) forming a compacted mass by application of pressure out of a powder material including REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 in a powder form wherein powder particles of REBa 2 Cu 3 O 7-x have an average diameter up to 6 µm and a maximum diameter up to 2⊘ µm, and powder particles of RE 2 BaCuO 5 have an average diameter up to 6 µm and a maximum diameter up to 2⊘ µm; (2) heating the compacted mass to a temperature which is higher than the incongruent melting temperature of REBa 2 Cu 3 O 7-x and which is lower than the incongruent melting temperature of RE 2 BaCuO 5 so as to partially melt and decompose the REBa 2 Cu 3 O 7-x in the mass into a melt and RE 2 BaCuO 5 in the solid state; (3) gradually cooling the mass so as to recrystallize REBa 2 Cu 3 O 7-x from the melt wherein fine particles of RE 2 BaCuO 5 are dispersed in grains of REBa 2 Cu 3 O 7-x ; and (4) annealing the mass in an atmosphere containing oxygen for a time sufficient for the requisite amount of oxygen to diffuse into the mass. Gradually cooling the melt in step (3) gives rise to a peritectic reaction of RE 2 BaCuO 5 in a solid state with the melt to give a crystal growth of REBa 2 Cu 3 O 7-x at an interface of RE 2 BaCuO 5 partides and the melt so that fine particles of RE 2 BaCuO 5 are dispersed in grains of REBa 2 Cu 3 O 7-x . Fine particles of RE 2 BaCuO 5 in the composite have a diameter up to 2⊘ µm, and most of the fine particles are less than 5 µm. RE 2 BaCuO 5 particles in the composite work as pinning centers. Preferably the powder particles of REBa 2 Cu 3 O 7-x have an average diameter up to 4 µm and a maximum diameter up to 15 µm, and the powder particles of RE 2 BaCuO 5 have an average diameter up to 4 µm and a maximum diameter up to 15 µm. The powder material in step (1) may include an amount of RE 2 BaCuO 5 ranging from 1⊘% to 8⊘% by mole of an amount of REBa 2 Cu 3 O 7-x . The fine particles of RE 2 BaCuO 5 have diameters up to 2⊘ µm, and most of the fine particles may have diameters up to 1⊘ µm. Diameters of most of the fine particles typically distribute around about 2 to about 4 µm. The melt in step (3) further includes an effective amount of a species so as to disperse the fine particles of RE 2 BaCuO 5 in step (3). The powder material in step (1) further includes the species so as to disperse the fine particles of RE 2 BaCuO 5 in step (3), and the species includes at least one element selected from the group consisting of Pt, Rh, Pd, Ru, Os, Sc, and Ce so that the fine particles of RE 2 BaCuO 5 in step (3) have a maximum diameter up to 2⊘ µm. An amount of the one element ranges from ⊘.⊘1 to 1⊘ % by weight of the sum of RE 2 BaCuO 5 and REBa 2 Cu 3 O 7-x in the powder material. Preferably step (2) further includes a step of maintaining the mass at a steady temperature ranging from 95⊘°C to 125⊘°C for a sufficient time to partially melt REBa 2 Cu 3 O 7-x . In step (3) the mass may be gradually cooled from a temperature ranging from 1⊘5⊘°C to 98⊘°C to a temperature ranging from 94⊘°C to 85⊘°C at a rate ranging from ⊘.1°C to 2°C per hour. Preferably after step (2) and prior to step (3), the mass may be rapidly cooled to an initial temperature of the mass at step (3) at a rate ranging from 5⊘°C to 4⊘⊘°C per hour. In step (3) an initial temperature from which the mass is gradually cooled may be a temperature higher by 5°C to 2⊘ °C than the incongruent melting temperature of REBa 2 Cu 3 O 7-x , and an ending temperature to which the mass is gradually cooled is a temperature lower by at least 3⊘°C than the incongruent melting temperature of REBa 2 Cu 3 O 7-x . Detailed Description of the Invention The superconductive composite obtained by the method of the present invention indudes a matrix composed of grains represented by a formula REBa 2 Cu 3 O 7-x . In the formula, RE is at least one element selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu. REBa 2 Cu 3 O 7-x has a multi-layered perovskite structure with oxygen deficiency shown by x. In the formula x is a number ranging from ⊘ to 1, and an oxygen content in REBa 2 Cu 3 O 7-x is non-stoichiometric. A value of x has a direct influence on the superconductivity of the grains. An example of the formula includes YBa 2 Cu 3 O 7-x . The rare earth element represented by RE is not restricted to one element and may be a mixture of two or more elements selected from the group. An example of such mixed rare earth elements is that RE is shown as Y y Yb 1-y where y ranges from ⊘ to 1. A starting material for powder of REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 includes, for example, an oxide of RE, including Y, Gd, Dy, Ho, Er, and Yb; a carbonate, oxide or peroxide of Ba; and an oxide of Cu. To form powder of REBa 2 Cu 3 O 7-x , a mixture including RE, Ba, and Cu in a molar ratio of 1:2:3 is sintered at a temperature ranging from 65⊘°C to 1,⊘⊘⊘°C, which is lower than the incongruent melting temperature of REBa 2 Cu 3 O 7-x , in an ambient atmosphere, and the sintered material is pulverized. Alternatively, the mixture may be heated to a temperature higher than the incongruent melting temperature to partially melt REBa 2 Cu 3 O 7-x and then to cool the mass to solidify the melt. To form powder of RE 2 BaCuO 5 , a mixture including RE, Ba, and Cu in a molar ratio of 2:1:1 is fired at a temperature ranging from 8⊘⊘°C to 1,2⊘⊘°C in an ambient atmosphere, and the fired material is pulverized, for example with a mill. An average partide size can be adjusted by a period of time for pulverizing the fired material. Large particles may be eliminated by a sedimentation method using an appropriate solvent such as ethanol, and a sieving method. In the sedimentation method, powder partides are dispersed in a solvent, and larger partides fall quicker than smaller particles, thereby removing larger particles. Powder particles having an average diameter of not more than about 3 µm may be obtained by a coprecipitation method using oxalates, a sol-gel method, or a spray-pyrolysis method. In the sol-gel method, nitrates or acetates of a rare earth metal, barium, and copper are dissolved in an organic solvent such as alcohol. Ethyleneglycol may be used as a solvent. An organic acid, for example, citric acid, tartaric acid, lactic acid, etc. is added to the starting solution to form metallic salts of the organic acid. Then the solvent is removed from the solution at a temperature ranging from about 7⊘°C to about 9⊘°C for a sufficient time, for example, over a period of scores of hours so as to change a sol to a gel to solidify. The solid obtained is pulverized, and then fired at about 8⊘⊘°C for one to six hours to give fine powder. A molar ratio of RE:Ba:Cu in the starting solution is adjusted for a desired ratio such as 1:2:3 and 2:2:1. In the spray pyrolysis method, a solution containing a rare earth metal, barium, and copper in a desired ratio is sprayed into a furnace which is heated to high temperatures in advance so as to pyrolyze the compound in the sprayed solution to give a composite oxide. This method is disclosed in "Advances in Superconductivity II" p873-876 by Springer-Verlag, 199⊘. A compacted mass is obtained by application of pressure out of a powder material including REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 in a powder form. The powder material may consist essentially of 1⊘⊘ molar parts of REBa 2 Cu 3 O 7-x and 1⊘ to 8⊘ molar parts of RE 2 BaCuO 5 , and further preferably 1⊘⊘ molar parts of REBa 2 Cu 3 O 7-x and 2⊘ to 5⊘ molar parts of RE 2 BaCuO 5 . The ratio of the two starting materials is suitable for dispersing fine particles of RE 2 BaCuO 5 in the resulting composite. The powder material contains at least one element selected from the group consisting of Pt, Rh, Pd, Ru, Os, Sc, and Ce, and an amount the at least one element is ⊘.⊘1-1⊘% by weight in proportion to the sum of REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 . When at least one of Pt, Rh, Pd, Ru, and Os is used, an amount of the metal may preferably range from ⊘.1 to 5% by weight in proportion to the sum of REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 . When Sc is used, an amount of scandium may range ⊘.1 to 3% by weight in the sum of REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 . Powder particles of these elements in the powder material may have an average diameter up to 6 µm, and a maximum diameter up to 2⊘ µm. These elements may be pure substance, binary oxides including, for example, PtO 2 and Rh 2 O 3 , or oxides which contain barium and a noble metal, including, for example, Ba 4 PtO 6 , Ba 4 CuPt 2 O 9 , Y 2 Ba 2 CuPtO 8 , Y 2 Ba 3 Cu 2 PtO 1⊘ , Ba 4 CuRh 2 O 9 , etc. The oxide containing barium and a noble metal are obtained by heating a powder material including barium oxide, the noble metal, and the other oxides of constituent metals in a desired stoichiometry in an ambient atmosphere. For example, to form Ba 4 CuPt 2 O 9 in a powder form, a powder mixture composed of BaO, CuO, and PtO 2 in a molar ratio of 4:1:2 is sintered at about 95⊘°C for five hours in an ambient atmosphere, and the sintered material is pulverized. To form Y 2 Ba 3 Cu 2 PtO 1⊘ powder, a powder mixture composed of Y 2 O 3 , BaO, CuO, and PtO 2 so as to have a molar ratio of Y:Ba:Cu:Pt being 2:3:2:1 is sintered at about 1⊘5⊘°C for five hours in an ambient atmosphere, and the sintered material is pulverized. Alternatively, these elements may be added to the melt in the heated compact mass prior to the step of gradually cooling the mass. The presence of the elements in the melt of the partially melt process is related to disperse fine particles of RE 2 BaCuO 5 uniformly dispersed in grains. These fine particles act as pinning centers, and their presence is preferable. These elements are dispersed uniformly in a form of particles in the REBa 2 Cu 3 O 7-x grains of the resulting composite. REBa 2 Cu 3 O 7-x powder, RE 2 BaCuO 5 powder, and optionally powder of a compound including at least one element of Pt, Rh, Pd, Ru, Os, Sc, and Ce are thoroughly mixed in wet or dry. Alternatively a solution of the compound may be mixed with REBa 2 Cu 3 O 7-x powder and RE 2 BaCuO 5 powder, and the mixture is dried, and then pulverized to give a powder material. Pressure is applied to the powder material to give a compacted mass. The powder material may be subjected to a known molding method, such as press molding, injection molding, cast molding, isotropic press molding, etc. to form a desired shape. The compacted mass has any shape, including a disk, a cylinder, a prism; a parallelepiped; a rectangular parallelepiped; a cone; a pyramid; a spheroid; a sphere; a shape obtained by subjecting any of the above shapes to plastic deformation in any desired direction; a shape obtained by cutting any of the above shapes in any direction so as to give a flat or curved surface; and a shape obtained by making at least one hole in any of the above shapes, such as a cylindrical tube. As disclosed in EP-A-0 564 279, the compacted mass to be heated may include a small amount of silver so that the resulting composite includes particles containing silver thereby ensuring resilience to crack formation in REBa 2 Cu 3 O 7-x grains. As further disclosed in EP-A-0 564 279, the compacted mass may include a small amount of a silver compound having a gradation in its concentration through the mass so as to decrease the solidifying point of the mass so that in the gradual cooling step the melt may crystallize from the portion of the compact having the highest solidifying point to a direction of the portions of the compact having lower solidifying points thereby ensuring high orientation of grains in a composite. The compacted mass is heated to a temperature which is higher than an incongruent melting temperature of REBa 2 Cu 3 O 7-x so as to partially melt the REBa 2 Cu 3 O 7-x in the mass and to decompose the REBa 2 Cu 3 O 7-x into a melt and RE 2 BaCuO 5 in the solid state. However, this temperature is lower than an incongruent melting temperature of RE 2 BaCuO 5 at which RE 2 BaCuO 5 decomposes into a melt and RE 2 O 3 in the solid state. During this heating step RE 2 BaCuO 5 powder in the compacted mass is believed to remain as it is in the solid state. The compacted mass may be placed into a furnace, and then heated at a rate of 1⊘⊘°C to 4⊘⊘°C per hour, and, further preferably 2⊘⊘°C to 3⊘⊘°C per hour. Alternatively, the compacted mass may be placed Into a furnace which was heated in advance to a desired temperature. Preferably the atmosphere during the heating step is an ambient atmosphere thereby facilitating the heating operation. Preferably the mass is maintained at a steady temperature ranging from 95⊘°C to 125⊘°C for a sufficient time to partially melt the REBa 2 Cu 3 O 7-x in the mass. The sufficient time depends on the size of the mass and the steady temperature, and it may be at least 1⊘ minutes for a mass having a disk shape with a diameter of 2⊘ mm and a height of less than 5 mm. The incongruent melting temperature of the compacted mass depends upon the kind of rare earth element, the kind and amount of the noble metal compound in the compact. In general a larger amount of a noble metal compound decreases the incongruent melting temperature of REBa 2 Cu 3 O 7-x . The steady temperature to keep the compacted mass may be, for example, in the range from about 1,⊘⊘⊘°C to 1,2⊘⊘°C for YBa 2 Cu 3 O 7-x , from about 1,⊘4⊘°C to 1,23⊘°C for SmBa 2 Cu 3 O 7-x , from about 1,⊘3⊘°C to 1,2⊘⊘°C for EuBa 2 Cu 3 O 7-x . from about 1⊘8⊘°C to 1,23⊘°C for GdBa 2 Cu 3 O 7-x , from about 1⊘3⊘°C to 1,21⊘°C for DyBa 2 Cu 3 O 7-x , from about 1⊘4⊘°C to 1,19⊘°C for HoBa 2 Cu 3 O 7-x , from about 1⊘2⊘°C to 1,17⊘°C for ErBa 2 Cu 3 O 7-x , and from about 95⊘°C to 1,15⊘°C for YbBa 2 Cu 3 O 7-x . Then the mass may be rapidly cooled at a rate ranging from 5⊘°C to 4⊘⊘°C per hour to an initial temperature from which a gradually cooling starts. The initial temperature may be a temperature higher by 5°C to 2⊘ °C than the incongruent melting temperature of REBa 2 Cu 3 O 7-x . Subsequently, the mass is gradually cooled so as to recrystallizes REBa 2 Cu 3 O 7-x from the melt. Gradually cooling the melt in the mass gives rise to a peritectic reaction of RE 2 BaCuO 5 in the solid state with the melt to give crystal growth of REBa 2 Cu 3 O 7-x at an interface of RE 2 BaCuO 5 particles and the melt. The melt includes the RE 2 BaCuO 5 in the solid state due to the decomposition of REBa 2 Cu 3 O 7-x and the RE 2 BaCuO 5 particles from the starting material. The presence of a noble metal prevents RE 2 BaCuO 5 particles from growing to more than 2⊘ µm. In the present invention, the RE 2 BaCuO 5 particles from the starting material are small from the beginning. The RE 2 BaCuO 5 in a solid state due to the decomposition of REBa 2 Cu 3 O 7-x are believed to be small because initial REBa 2 Cu 3 O 7-x particles are small. These small particles of RE 2 BaCuO 5 in the melt are related to the dispersion of small RE 2 BaCuO 5 particles in a matrix composed of REBa 2 Cu 3 O 7-x grains in the resulting composite. The initial temperature from which the mass is gradually cooled may be a temperature higher by 5°C to 2⊘ °C than the incongruent melting temperature of REBa 2 Cu 3 O 7-x . The ending temperature at which the gradually cooling ends may be lower than the incongruent melting temperature by about 3⊘ °C to 7⊘°C. The rate of the gradual cooling may range from ⊘.1°C to 2°C per hour, and preferably from ⊘.2°C to 1.5°C per hour. For example, a mass including YBa 2 Cu 3 O 7-x may be gradually cooled from a temperature ranging from 1⊘5⊘°C to 98⊘°C to a temperature ranging from 94⊘°C to 85⊘°C As disclosed in EP-A-0 564 279, during the gradual cooling step, a seed crystal, which is a small piece of a single crystal of, for example, REBa 2 Cu 3 O 7-x , may be placed onto the mass so as to provide nucleation sites for REBa 2 Cu 3 O 7-x grains. The seed crystal may be single crystals of SrTiO 3 , MgO, LaAlO 3 , LaGaO 3 , NdGaO 3 , PrGaO 3 and the like which have the lattice constants of the (1⊘⊘) surface in their single crystals close to the lattice constant of the ab surface of REBa 2 Cu 3 O 7-x . The rare earth superconductive composite after gradual cooling is heat-treated in an oxygen atmosphere at a given temperature in the same manner as in a known melting process, whereby the REBa 2 Cu 3 O 7-x grains in the superconductive composite absorb a sufficient amount of oxygen for adjusting the value of x to a positive real number up to ⊘.2 thereby ensuring superconductivity. The heat treatment in an oxygen atmosphere may be conducted at 6⊘⊘° C for 5-1⊘ hours, at 5⊘⊘° C for 1⊘-2⊘ hours or at 4⊘⊘° C for 2⊘-5⊘ hours. In the method of the present invention small powder particles of REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 are used in a compacted mass in the partial melt process thereby increasing a critical current density of a resultant superconductive composite into more than 1⊘,⊘⊘⊘ ampere per square centimeter. The composite obtained by the method of the present invention may be applied to various areas, for example, superconductive wires, a flying wheel, a structure for magnetic screening, etc. Examples 1-5 Y 2 O 3 powder, BaCO 3 powder and CuO powder were thoroughly mixed so as to have a molar ratio of Y:Ba:Cu to be 1:2:3 using a dry type pot mill for 6 hours. The mixture was spread on a silver plate in an ambient atmosphere, and calcined at 9⊘⊘°C for 1⊘ hours. The calcined material was pulverized in a rotary mill using zirconia balls, for a sufficient time to obtain calcined powders of YBa 2 Cu 3 O 7-x having an average particle diameter of Table 1. For example, the powder was subject to the rotary mill about 15 hours for an average particle diameter of 6 µm. It is noted that the average particle diameter depends on a calcining temperature and a period of time for pulverizing the calcined material in the rotary mill. For example, calcining the mixture at about 95⊘°C and pulverizing the calcined mixture in the rotary mill for 8 hours led to the average particle diameter of about 13 µm. Y 2 O 3 powder, BaCO 3 powder and CuO powder were thoroughly mixed so as to have a molar ratio of Y:Ba:Cu to be 2:1:1 using a dry type pot mill for 6 hours. The mixture was spread on a silver plate in an ambient atmosphere, and calcined at 930°C for 1⊘ hours. The calcined material was pulverized in a rotary mill using zirconia balls, for a sufficient time to obtain calcined powder of Y 2 BaCuO 5 having an average particle diameter of Table 1. For example, the powder was subject to the rotary mill for about 15 hours for an average particle diameter of 6 µm. Alternatively, calcining the mixture at about 95⊘°C and pulverizing the calcined in the rotary mill for 8 hours led to the average particle diameter of about 15 µm. Large powder particles having a diameter larger than 2⊘ µm in both YBa 2 Cu 3 O 7-x powder and Y 2 BaCuO 5 powder were removed by a sieving method. Powder particles having an average diameter of 3 µm of both YBa 2 Cu 3 O 7-x and Y 2 BaCuO 5 were obtained by a coprecipitation method using oxalate. In the coprecipitation method, yttrium nitrate, barium nitrate, and copper nitrate were dissolved in distilled water in a molar ratio of Y:Ba:Cu to 1:2:3, and an aqueous ammonia solution was added to the solution so as to adjust pH of the solution to be in the range of 4.⊘ to 4.6 and, preferably about 4.3. Then, a citrate solution was added to the solution to form oxalate complexes of barium, yttrium, and copper. While the solution was being mixed, ethanol was added to the solution so as to decrease solubility of the oxalate complexes, and the oxalate complexes started to coprecipitate. After filtration, the precipitate was dried and then fired at about 8⊘⊘°C for six hours to give fine powder of YBa 2 Cu 3 O 7-x . After the firing step, pulverization is unnecessary. To obtain fine powder of Y 2 BaCuO 5 , the preparation method is the same as YBa 2 Cu 3 O 7-x except that the molar ratio of Y:Ba:Cu in the starting solution is 2:1:1, and that the firing step requires 9⊘⊘°C for five hours. The powder particles obtained by the coprecipitation method did not include large powder particles having diameters larger than 2⊘ µm. 1 mole part of YBa 2 Cu 3 O 7-x powder was mixed with ⊘.4 mole part of Y 2 BaCuO 5 powder, and to the resultant mixture was added 1% by weight of platinum powder in proportion to the mixture. The platinum powder had an average partide diameter up to 4 µm and a maximum particle diameter up to 1⊘ µm. The mixture was thoroughly mixed in a dry pot mill. The resultant powder material was placed in a mold having a cylindrical shape with an internal diameter of 2⊘ mm, and underwent press molding under a load of 5⊘⊘ kgf to give a green compact having a shape of a disk with a diameter of 2⊘ mm where 1 kgf is equivalent to 9.8⊘665 N. The green compact was heated to 11⊘⊘°C in an electrical furnace in an ambient atmosphere at a rate of 35⊘°C per hour. The green compact was held at 1,1⊘⊘°C for 1 hour so as to partially melt YBa 2 Cu 3 O 7-x and decompose YBa 2 Cu 3 O 7-x into a melt and solid-state phases. The mass was cooled from 1,1⊘⊘°C to 1,⊘⊘⊘°C at a rate of 1⊘⊘ °C per hour. Then, the compact was slowly cooled from 1,⊘⊘⊘°C to 9⊘⊘°C at a rate of 1.⊘ °C per hour to solidify the melt. The mass was cooled in the furnace from 9⊘⊘°C to temperatures below. Then, the atmosphere in the furnace was changed to an oxygen atmosphere and the fired mass was subject to a heat treatment at 65⊘-4⊘⊘°C for 5⊘ hours to obtain a rare earth superconductive composite. The critical current density, which is abbreviated as Jc, of each composite was measured by a magnetization method at 77 K under a magnetic flux density of 1 tesla. The test conditions and the result obtained are shown in Table 1. Ex. average particle diameter (µm) Jc (A/cm 2 ) at 77 K under 1 T YBa 2 Cu 3 O 7-x Y 2 BaCuO 5 1 3 6 18,⊘⊘⊘ 2 6 6 15,⊘⊘⊘ 3 6 3 18,⊘⊘⊘ 4 3 3 19,⊘⊘⊘ 5 5 5 17,⊘⊘⊘ Comparative Examples 1-3 As shown in Table 2, average particle diameters of YBa 2 Cu 3 O 7-x powders and Y 2 BaCuO 5 powders in Comparative Examples 1-3 were changed from Examples 1-5. The other conditions of Comparative Examples 1-3 were the same as those of Examples 1-5. A critical current density of each composite was measured by a magnetization method at 77 K under a magnetic flux density of 1 tesla The test conditions and the result obtained are shown in Table 2. Comp. Ex. average particle diameter (µm) Jc (A/cm 2 ) at 77 K under 1 T YBa 2 Cu 3 O 7-x Y 2 BaCuO 5 1 8 6 1⊘,⊘⊘⊘ 2 13 6 5,⊘⊘⊘ 3 3 15 6,⊘⊘⊘ Comparing Table 2 with Table 1, as the average particle diameter of YBa 2 Cu 3 O 7-x and Y 2 BaCuO 5 increases, the critical current density of the composite decreases. A cross section of each composite was observed by an electron microscope. In any of the samples taken from Examples 1-5, Y 2 BaCuO 5 particles dispersed in a matrix of YBa 2 Cu 3 O 7-x grains had diameters smaller than 2⊘ µm, and most of the fine particles had diameters less than 3 µm. In contrast, in any of the samples taken from the composites of Comparative Examples 1-3, a small number of Y 2 BaCuO 5 particles dispersed in a matrix of YBa 2 Cu 3 O 7-x grains had diameters larger than 2⊘ µm. Comparative Examples 4-6 As shown in Table 3, average particle diameters of YBa 2 Cu 3 O 7-x powders and Y 2 BaCuO 5 powders in Comparative Examples 4-6 were changed from Examples 1-5, and either YBa 2 Cu 3 O 7-x powder or Y 2 BaCuO 5 powder had a small portion of large particles having particle diameter larger than 2⊘ µm. A content of the large particles in the powder is expressed in percent by weight in proportion to the powder in Table 3. The other conditions of Comparative Examples 4-6 were the same as those of Examples 1-5. The critical current density of each composite was measured by a magnetization method at 77 K under a magnetic flux density of 1 tesla. The test conditions and the result obtained are shown in Table 3. Comp. Ex. YBa 2 Cu 3 O 7-x Y 2 BaCuO 5 Jc (A/cm 2 ) at 77 K under 1 T aver.part. diameter (µm) content of large part. (% by wt.) aver.part. diameter (µm) content of large part. (% by wt.) 4 5 ⊘ 6 1⊘ 1⊘,⊘⊘⊘ 5 6 1⊘ 5 ⊘ 7,⊘⊘⊘ 6 6 15 5 ⊘ 4,⊘⊘⊘ Comparing Table 3 with Table 1, the presence of the large particles having diameters more than 2⊘ µm in either powder decreases the critical current density of the composite. Examples 6-14 In Examples 6-14, average particle diameters of YBa 2 Cu 3 O 7-x powder and Y 2 BaCuO 5 powder were 3µm, and these powders were obtained by a coprecipitation method using oxalates. In Examples 6-14, large powder particles having a diameter larger than 2⊘ µm of both YBa 2 Cu 3 O 7-x powder and Y 2 BaCuO 5 powder were not present. 1 mole part of YBa 2 Cu 3 O 7-x powder was mixed with a specified mole part shown in Table 4 of Y 2 BaCuO 5 powder, and to the resultant mixture was added a specified percent shown in Table 4 by weight of powder of a noble metal compound in proportion to the mixture. The noble-metal-compound powder had an average particle diameter up to 6 µm, and a maximum particle diameter up to 2⊘ µm. This powder material was compacted, fired, and then annealed in the same way as Examples 1-5 to give a composite. A critical current density of each composite was measured by a magnetization method at 77 K under a magnetic flux density of 1 tesla The test conditions and the result obtained are shown in Table 4. Ex. molar ratio of Y 2 BaCuO 5 noble metal compd. Jc (A/cm 2 ) at 77 K under 1 T compd. amount (wt. %) 6 ⊘.1 Pt 1 13,⊘⊘⊘ 7 ⊘.2 Pt ⊘.5 18,⊘⊘⊘ 8 ⊘.4 Pt 1 17,⊘⊘⊘ 9 ⊘.8 Pt 1 12,⊘⊘⊘ 1⊘ ⊘.2 Rh ⊘.5 2⊘,⊘⊘⊘ 11 ⊘.4 Ba 4 CuPt 2 O 9 2 16,⊘⊘⊘ 12 ⊘.4 Ba 4 CuPt 2 O 9 6 17,⊘⊘⊘ 13 ⊘.4 Ba 4 CuRh 2 O 9 2 18,⊘⊘⊘ 14 ⊘.4 Y 2 Ba 3 Cu 2 PtO 1⊘ 2 16,⊘⊘⊘ Comparative Examples 7-13 1 mole part of YBa 2 Cu 3 O 7-x powder was mixed with a specified mole part shown in Table 5 of Y 2 BaCuO 5 powder, and to the resultant mixture was added a specified percent shown in Table 5 by weight of powder of a noble metal compound in proportion to the mixture. The other conditions of Comparative Examples 7-13 were the same as those of Examples 6-14. A critical current density of each composite was measured by a magnetization method at 77 K under a magnetic flux density of 1 tesla. The test conditions and the result obtained are shown in Table 5. Comp. Ex. molar ratio of Y 2 BaCuO 5 noble metal compd. Jc (A/cm 2 ) at 77 K under 1 T compd. amount (wt. %) 7 ⊘ Pt ⊘.5 6,⊘⊘⊘ 8 ⊘.9 Pt 1 1⊘,⊘⊘⊘ 9 ⊘.4 none - 5,⊘⊘⊘ 1⊘ ⊘.4 Pt ⊘.⊘3 6,⊘⊘⊘ 11 ⊘.4 Pt 2⊘ 6,⊘⊘⊘ 12 ⊘.4 Ba 4 CuPt 2 O 9 3⊘ 8,⊘⊘⊘ 13 ⊘.4 Y 2 Ba 3 Cu 2 PtO 1⊘ ⊘.⊘5 6,⊘⊘⊘ Comparing Table 5 with Table 4, it increases a critical current density of a composite that a molar ratio of Y 2 BaCuO 5 to YBa 2 Cu 3 O 7-x ranges from ⊘.1 to ⊘.8, and particularly from ⊘.2 to ⊘.5. It also increases a critical current density of a composite that an amount of a noble metal compound ranges from ⊘.⊘5% to 1⊘%, and particularly ⊘.5 to 6%, by weight in proportion to the sum of the YBa 2 Cu 3 O 7-x powder and the Y 2 BaCuO 5 powder. It is obvious to a person skilled in the art that the different embodiments of the invention may vary within the scope of the invention presented here. The invention in its broader aspects is therefore not limited to the specific examples shown and described.

Claims: A method for making a rare earth superconductive composite including a matrix of REBa 2 Cu 3 O 7-x grains and, uniformly dispersed therein, fine particles of RE 2 BaCuO 5 , wherein RE is at least one element selected from the group consisting of Y, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu, and x is in the range from ⊘ to 1, which includes the steps of: (1) forming a compacted mass by application of pressure, from a powder material including REBa 2 Cu 3 O 7-x and RE 2 BaCuO 5 ; (2) heating the compacted mass to a temperature which is higher than the incongruent melting temperature of REBa 2 Cu 3 O 7-x and which is lower than the incongruent melting temperature of RE 2 BaCuO 5 so as to partially melt and decompose the REBa 2 Cu 3 O 7-x in the mass into a melt and RE 2 BaCuO 5 in the solid state; (3) gradually cooling the mass so as to recrystallize REBa 2 Cu 3 O 7-x from the melt wherein fine particles of RE 2 BaCuO 5 are dispersed in REBa 2 Cu 3 O 7-x grains; and (4) annealing the mass in an atmosphere containing oxygen for a time sufficient for the requisite amount of oxygen to diffuse into the mass; characterized in that in the step of forming the compacted mass, powder particles of REBa 2 Cu 3 O 7-x have an average diameter up to 6 µm and a maximum diameter up to 2⊘ µm, and powder particles of RE 2 BaCuO 5 have an average diameter up to 6 µm and a maximum diameter up to 2⊘ µm, and wherein said powder material in step (1) includes at least one element selected from Pt, Rh, Pd, Ru, Os, Sc and Ce so that said fine particles of RE 2 BaCuO 5 in step (3) have a maximum diameter up to 2⊘ µm, and the amount of said at least one element is in the range from ⊘.⊘1 to 1⊘% by weight relative to the sum of RE 2 BaCuO 5 and REBa 2 Cu 3 O 7-x in said powder material. A method according to claim 1, wherein said powder particles of REBa 2 Cu 3 O 7-x have an average diameter up to 4 µm and a maximum diameter up to 15 µm, and said powder particles of RE 2 BaCuO 5 have an average diameter up to 4 µm and a maximum diameter up to 15 µm. A method according to claim 1 or 2, wherein said powder material in step (1) includes an amount of RE 2 BaCuO 5 in the range from 1⊘% to 8⊘% by mole relative to the amount of REBa 2 Cu 3 O 7-x . A method according to any of claims 1 to 3, wherein step (2) further includes a step of maintaining the mass at a steady temperature in the range from 95⊘°C to 125⊘°C for a sufficient time to partially melt REBa 2 Cu 3 O 7-x . A method according to any of claims 1 to 4, wherein in step (3) the mass is gradually cooled from a temperature in the range from 1⊘5⊘°C to 98⊘°C to a temperature in the range from 94⊘°C to 85⊘°C at a rate ranging from ⊘.1 °C to 2°C per hour. A method according to any of claims 1 to 5, after step (2) and prior to step (3), further including a step of rapidly cooling the mass to an initial temperature of the mass at step (3) at a rate in the range 5⊘°C to 4⊘⊘°C per hour. A method according to any of claims 1 to 6, wherein in step (3) an initial temperature from which the mass is gradually cooled is a temperature higher by 5°C to 2⊘ °C than the incongruent melting temperature of REBa 2 Cu 3 O 7-x , and an ending temperature to which the mass is gradually cooled is a temperature lower by at least 3⊘°C than the incongruent melting temperature of REBa 2 Cu 3 O 7-x .

Inventors: HIRABAYASHI IZUMI, YOSHIDA MANABU, HIRABAYASHI, IZUMI, YOSHIDA, MANABU, Hirabayashi, Izumi, c/o Inter. Superconductivity
Applicants: INT SUPERCONDUCTIVITY TECH, NGK INSULATORS LTD, INTERNATIONAL SUPERCONDUCTIVITY TECHNOLOGY CENTER, NGK INSULATORS, LTD.
Application year: 1993
Main classification: C04B35
IPC codes: C04B35, H01L39, H01B12, H01B13, C01G1, C01G3