Reticulated bacterial cellulose reinforcement for elastomers

Abstract: Reinforced elastomeric articles, such as tires, wherein the reinforcement is reticulated bacterial cellulose are provided. Reticulated bacterial cellulose has an average diameter of about 0.1 micron and a substantially infinite aspect ratio. The reinforced article comprises about 2 phr to 10 phr of the cellulose reinforcement.

Description: Background of the Invention The invention relates to reinforced elastomeric articles, especially tires, wherein the reinforcement comprises reticulated bacterial cellulose. It is well known in the art that fiber reinforced elastomer composites have a higher modulus and better cut and tear growth properties than the corresponding reinforcement free elastomer. Although a higher modulus and better cut and tear growth properties are desirable properties, a short fiber reinforced elastomer often has reduced tensile properties and reduced elongation properties. It is often the case that the amount of fiber loading in a reinforced elastomer is a trade off between the modulus, cut growth and tear growth properties desired, and the reduction in tensile properties and elongation that can be tolerated. Tires having members reinforced with short fibers and unregenerated cellulose fibers are known from US-A- 3 802 478. The use of microbial cellulose to make composites is known from WO-A- 8 911 783. It is an object of the present invention to provide an elastomeric article that has improved modulus, tear growth and cut growth properties while having substantially undiminished tensile and elongation properties. The invention provides a reinforced elastomeric article, a pneumatic tire containing a fiber reinforced elastomer component and a method of reinforcing an elatomeric article, such as recited in the appended claims. Brief Description of the Drawings Fig. 1 illustrates reticulated bacterial cellulose fiber. Fig. 2 illustrates a cellulose fiber reinforced pneumatic tire. Fig. 2a illustrates cellulose fibers dispersed in an SBR elastomer matrix. Fig. 3 illustrates the storage modulus of the reinforced composite of the invention as compared with unreinforced elastomer and a prior art composite. Fig. 4 illustrates the tan delta for the same composites compared in Fig. 3. Detailed Description of the Invention For good short fiber reinforcement of elastomers, two important criteria are good adhesion between the fiber and the elastomer and a high fiber aspect ratio. To achieve a high aspect ratio, one can either increase the length of the fiber or reduce the diameter of the fiber. It is well known in the art that cellulose fibers exhibit excellent adhesion to elastomers. With reference now to Fig. 1, an illustrated reticulated bacterial cellulose fiber is produced by Acetobacter bacteria in an aerated, agitated culture. Such a fiber known by the trade name Cellulon® is available from Weyerhauser. The illustrated fiber has an average diameter of about 0.1 micron, and the fiber is interconnected and networked such that the aspect ratio is incalculable and, for purposes of this description, is considered to be substantially infinite. The Cellulon® fiber submicron diameter is about 1/100 the diameter of conventional cellulose fibers such as cotton. Cellulon® fiber is supplied in an aqueous medium containing about 15% to 30% solids by weight. It has been found that the fibers can most efficiently be incorporated in an elastomer by introducing the fiber containing medium into a latex or an elastomer cement. If a latex is used, the latex may be coagulated as is conventional in the art. If desired, the resulting fiber containing elastomer can be used as a masterbatch and mixed with natural rubber or other elastomer suitable for its intended purpose. With reference now to Fig. 2, it is believed that the reticulated bacterial cellulose fiber can be used in practically any tire component, alone or together with other reinforcement (including other fibrous reinforcement), where tire properties can be improved by fiber reinforcement. The reticulated bacterial cellulose fiber may comprise 2 phr to 15 phr, preferably 2 phr to 10 phr of the elastomer composite. phr represents parts by weight per one hundred parts by weight rubber. In the tread 12 of tire 10 for example, the reticulated bacterial cellulose fiber reinforcement is believed to provide a greater tread modulus (which improves tread wear and rolling resistance) while the tensile properties (and the traction) remain undiminished. Similarly, in the sidewall 14 the fibers provide better penetration resistance and crack growth properties while the flexibility of the sidewall is not diminished as compared to the sidewall compound without fiber reinforcement. Fig. 2a illustrates an SBR/Cellulon® composite. SBR (styrene butadiene rubber), with specific modifications, can be used in the tread of a tire or in a tire sidewall. Similar results are believed possible in apex 16, treadbase 18, and toe guard 20. Other uses of fiber reinforcement in a tire will be apparent to those skilled in the art. The invention is further illustrated with reference to the following examples. Example 1 Cellulon® fiber is supplied in an aqueous system containing about 15-30% solids (by weight). The fibers can be dispersed either in elastomer cement or latex during elastomer production. 6.25g of Cellulon® product (17 wt% fiber) was blended with 250 g of (21% SBR) Plioflex 1502 latex in a Waring Blender for 2 minutes. Plioflex 1502 comprises a styrene butadiene co-polymer containing 23.5% styrene. The mixture was coagulated with a typical coagulating agent (900 g of water, 30 g of NaCl, 1.8 g of Conc. H 2 S0 4 , and 7.5 g of a liquid cationic amine) at 70° C. The coagulated elastomer fiber mixture was washed twice with 2000 cc of water. The prepared sample contained 2 phr fiber. The resulting sample, designated 1b, was mixed into a testing compound having the following formulation. The compound was subsequently cured and tested. In the examples herein, the material specific to an example is designated 1b in the following formula. Unless otherwise specified, all the examples are the same except for the different 1b materials specified. Ingredient Type Amount in phr 1.(a) cis,1,4-polyisoprene elastomer 25 (b) material in examples elastomer 75 2. carbon black,general purpose tread filler 45 3. petroleum process oil plasticizer 9 4. N-phenyl-N'-(1,3 dimethyl/butyl) N-phenyl-P-phenylenediamine antidegradant 2 5. mixed diaryl-P-phenylene diamine antidegradant 1 6. paraffinic/micro crystalline wax processing aid 1 7. stearic acid activator 3 Brabender Mixer Compounding. The Cellulon® fibers were on top of the 100 parts of elastomer as described in the ingredients. A Brabender mix at 70 rpm using a 120°C oil bath, was used for non productives (ingredients 1-7). Mix time was 5 minutes, and the drop temperature was approximately 270°F (132°C). The non-productive mixes were used for further compounding by reloading the non-productives in the mixer and adding the following ingredients: 8. Sulfur curative 1.6 9. N, N' diphenyl guanidine accelerator 0.4 10. 2 (morpholino-thio) benzenethiazole accelerator 0.8 11. Zinc oxide accelerator 3 Productive mixes (non-productive plus the accelerators and vulcanizing agents, (ingredients 8-11) were carried out without external heating at 50 rpm for 3 minutes. The compounded elastomers were cured at 150°C. The vulcanizate physical properties of the reinforced elastomer were compared to that of a control compound comprising the above formulation prepared without the addition of a fiber reinforcement Example 2 The procedure of Example 1 was repeated using 12.5g Cellulon® fibers in material 1 (b), and the resultant sample had a fiber content of 2.9 phr. Example 3 The procedure of Example 1 was repeated using 25g Cellulon® product (17 wt% fiber) in material 1(b), and the resultant sample contained 5.6 phr fiber reinforcement. Example 4 90 g of 62 wt% of natural rubber latex was mixed with 100 g of water and 14 g of 16 wt% Cellulon® product in a Waring blender for 2 minutes. The mixture was coagulated in 800 g of isopropanol and dried. 75 phr of the natural rubber fiber composite, material 1(b), was used in the formulation described in Example 1. The resultant sample had a fiber content of 2.9 phr. The comparative results of tensile properties are listed below. Control 1 is a rubber sample of the formula illustrated in Example 1 (polyisoprene/SBR) without fiber reinforcement. Control 2 is a blend of 75 phr natural rubber and 25 phr cis 1, 4 polyisoprene. Sample Moduli (psi) (MPa) Tensile PSI (MPa) Elongation % T90 (min) @50% 100% 300% Control 1 131 0,90 184 1,27 301 2,08 3318 22,88 1143 23.5 Example 1 207 1,43 279 1,92 416 2,87 3293 22,70 1150 22.5 Example 2 294 2,03 390 2,69 555 3,83 3193 22,01 1074 21.0 Example 3 357 2,46 474 3,27 679 4,68 2906 20,04 940 21.5 Control 2 147 1,01 238 1,64 825 5,69 3446 23,76 837 9.7 Example 4 286 1,97 496 3,42 1300 8,96 3580 24,68 741 9.7 Autovibron was run with a frequency of 11 Hz. The data shows that the modulus increases with increased fiber loading while the tensile properties and elongation properties are relatively stable. The cure rheometer data (Table 1) showed Cellulon® fiber does not alter the curing characteristics of SBR. T90 values of samples containing various amounts of Cellulon® fiber are similar to the SBR control. Tensile values show that the modulus value is proportional to the concentration of Cellulon® fiber in Plioflex 1502. There is very little reduction in breaking tensile and elongation at a Cellulon® fiber concentration below four percent by weight. Tensile values in Table 1 also show the effectiveness of Cellulon® in natural rubber latex. At 2.9 phr loading there are 94% and 108% improvements of moduli at 50% and 100% elongation respectively. There is no loss in ultimate tensile strength. The properties of the composite of this invention are compared with composites made with other types of fibers in Table 2. COMPARISON OF ELASTOMER REINFORCED WITH VARIOUS FIBERS (3.3PHR FIBER) Sample Plioflex 1502 Control Kevlar® PULP Cellulon® Santoweb® Tensile,psi (MPa) 3669 (25,30) 3012 (20,77) 3663 (25,26) 2988 (20,60) Elg. % 639 521 623 574 Mod. psi @ (MPa) 50% 169 (1,17) 455 (3,14) 297 (2,05) 286 (1,97) 100% 254 (1,75) 658 (4,54) 479 (3,30) 376 (2,59) 300% 1194 (8,23) 1434 (9,89) 1450 (10,00) 1200 (8,27) DeMattia [in/Kc (cm/Kilocycles) 0.0231 (0,059) 0.0511 (0,130) 0.0209 (0,053) 0.0380 (0,067) Kevlar® fiber diameter 20 micron from DuPont Cellulon® fiber diameter 0.1 micron Santoweb® material is ribbon like with two axes=16 & 18 micron. Results in Table 2 indicate a Cellulon® reinforced composite has an excellent modulus modified at low strain. Cellulon® reinforcement is not as effective as Kevlar® pulp, but at high strain the difference diminishes. This may be due to the debonding of Kevlar® from the elastomer. The lower break tensile strength of Plioflex 1502-Kevlar® as compared to the control and Plioflex 1502-Santoweb® and Plioflex 1502/Cellulon® could also be due to debonding of Kevlar®. Both Cellulon® and Santoweb® are cellulose fibers. Santoweb® is a Monsanto product. It is based on unregenerated cellulose fiber with a surface treatment for better adhesion to elastomer. Results in Table 2 showed that Cellulon® fiber is a more effective reinforcement than Santoweb® in terms of tensile strength and tensile modulus. Demattia Flex test results gave some indication that the Plioflex 1502-Cellulon® composite has better cut growth resistance than the control and the other two fiber reinforced composites. This can be attributed to the small diameter and high aspect ratio of Cellulon® fibers. The Kevlar® and Santoweb® reinforced composites did not have good cut growth resistance, perhaps due to the large fiber diameter. Figure 3 shows that the storage modulus of samples containing 4% Cellulon® fiber and Santoweb® are higher than the storage modulus of the control throughout the temperature range (-40° to 120° C). Cellulon® fiber and Santoweb® showed similar effectiveness in improving the storage modulus of the final composite. Tan Deltas of all three samples (Fig. 4) are quite similar in the range between 20° and 80° C. These samples containing fibrous reinforcement have a tan delta slightly higher than the control between 80° and 120° C, but all of them are below 0.12. In Summary, low concentrations of Cellulon® fibers increase the tensile modulus of SBR elastomer composites without sacrificing ultimate tensile and elongation. Cellulon® fibers improve the tensile modulus of natural rubber composites without reducing the tensile at break. Cellulon® fiber reinforced SBR has a similar Tan Delta scan to a composite reinforced with Santoweb®, Figure 4. It has a higher storage modulus than an SBR control in the temperature range (-40° to 120°C). Cellulon® fiber reinforced SBR shows improved cut growth resistance.

Claims: A fiber reinforced elastomeric article in which the elastomer therein has tensile properties and elongation properties equivalent an elastomer used to make the article without fiber reinforcement, characterized in that said reinforced elastomeric article has an elastomeric matrix having distributed therein 2-15 phr reticulated bacterial cellulose fiber having an average diameter of about 0.1 micrometer and has a tensile modulus 25% to 400% greater than said elastomer without reinforcement, wherein said fiber is coated with a latex or an elastomer cement prior to incorporation in said elastomeric article. A pneumatic tire characterized in that one or more of its elastomer components are reinforced with reticulated bacterial cellulose fiber as claimed in claim 1. The pneumatic tire of claim 2 having 2 phr to 10 phr reticulated bacterial cellulose fiber incorporated therein. The pneumatic tire of claim 2 wherein tread rubber is reinforced with reticulated bacterial cellulose. The pneumatic tire of claim 2 wherein sidewall rubber is reinforced with reticulated bacterial cellulose. The pneumatic tire of claim 2 wherein tread base rubber is reinforced with reticulated bacterial cellulose. The pneumatic tire of claim 2 wherein apex rubber is reinforced with reticulated bacterial cellulose. The pneumatic tire of claim 2 wherein toe guard rubber is reinforced with reticulated bacterial cellulose. A method of reinforcing an elastomeric article comprising the steps of: (a) preparing and mixing an elastomer to be used in a reinforced elastomeric article; (b) adding reticulated bacterial cellulose having an average diameter of about 0.1 micrometer to a latex or elastomer cement to provide reticulated bacterial cellulose coated with latex or elastomer cement; and (c) adding 2 to 20 phr reticulated bacterial cellulose fiber coated with latex or elastomer cement to the elastomer mixture of step (a) during mixing.

Inventors: BAUER RICHARD GEORGE, CALLANDER DOUGLAS DAVID, TUNG DEBORAH ANN, TUNG WILIAM CHUNG-TSING, BAUER, RICHARD GEORGE, CALLANDER, DOUGLAS DAVID, TUNG, DEBORAH ANN, TUNG, WILIAM CHUNG-TSING
Applicants: GOODYEAR TIRE & RUBBER, THE GOODYEAR TIRE & RUBBER COMPANY
Application year: 1993
Main classification: B60C1
IPC codes: C08L21, B60C1