IMPROVED BACK-SIDE HYDROGENATION TECHNIQUE FOR DEFECT PASSIVATION IN SILICON SOLAR CELLS

Abstract: A two step back-side hydrogenation process includes the steps of first bombarding the back side (24) of the silicon substrate (12) with hydrogen ions (30) with intensities and for a time sufficient to implant enough hydrogen atoms into the silicon substrate (12) to potentially passivate substantially all the defects and impurities in the silicon substrate (12), and then illuminating the silicon substrate (12) with electromagnetic radiation to activate the implanted hydrogen, so that it can passivate the defects and impurities in the substrate. The illumination step also annihilates the hydrogen-induced defects. The illumination step is carried out according to a two stage illumination schedule (34), the first or low power stage (38) of which subjects the substrate (12) to electromagnetic radiation having sufficient intensity to activate the implanted hydrogen, yet not drive the hydrogen from the substrate (12). The second or high power illumination stage (40) subjects the substrate (12) to higher intensity electromagnetic radiation which is sufficient to annihilate the hydrogen-induced defects and sinter/alloy the metal contacts (28).

Description: Description Improved Back-Side Hydrogenation Technique for Defect Passivation in Silicon Solar Cells The United States Government has rights in this invention under Contract No. DE- AC02-83CH10093 between the U.S. Department of Energy and the National Renewable Energy Laboratory, a Division of Midwest Research Institute. Technical Field The present invention relates to hydrogenation of silicon substrates in general and in particular to an improved hydrogenation method for passivating defects in silicon solar cells. Background Art A typical silicon solar cell comprises a p-type and an n-type conductivity region in a silicon substrate and generates electricity when impinging radiation creates electron-hole pairs which migrate to the respective p-type and n-type conductivity regions. Unfortunately, certain impurities in the silicon substrate, as well as defects in the crystal lattice itself, can reduce the efficiency of the solar cell over what otherwise could be achieved if the silicon substrate were perfect and defect free. Consequently, researchers have searched for ways to minimize the effects of such defects and impurities, thus increase the overall efficiency of the cell. One method to minimize the effects of the defects and impurities is to hydrogenate the cell by implanting hydrogen into the silicon substrate. While the exact effect that hydrogen has on the substrate is not yet fully understood, it is known that the hydrogen minimizes or "passivates" the defects and impurities in the substrate. For example, many of the unit cells in the crystal lattice may be missing one or more silicon atoms, creating voids or areas where silicon atoms should be, but are not. Hydrogenating the substrate allows hydrogen atoms to fill those voids in the unit cells, thereby reducing the deleterious effects of those voids or defects. In fact, it is now well established that the performance of solar cells, as well as many other electronic devices that are fabricated on p and n doped silicon substrates, such as integrated circuits, can be improved by such hydrogen passivation. With regard to solar cells, hydrogen passivation improves cell efficiency by reducing minority carrier recombination losses at grain boundaries, dislocations, and other defects in the crystal lattice. Unfortunately, while the improved performance resulting from hydrogen passivation has been demonstrated in the laboratory, it has been difficult to apply hydrogen passivation techniques commercially, because the precise effects of hydrogenation on the silicon substrate still are not well understood. In the past, solar cells have been hydrogenated by introducing hydrogen into silicon substrate from the junction or front side of the cell by using an RF plasma or by ion implantation. However, front side hydrogenation is not without its disadvantages. For example, all of the cell processes that require temperatures in excess of 300" C must be carried out prior to hydrogenation, since temperatures above about 300 * C will drive the previously implanted hydrogen out of the substrate. Moreover, because hydrogen ions do not readily pass through the anti-reflective (AR) coatings usually placed on the front side of the cell, front side hydrogenation also must be performed prior to the deposition of the anti-reflective (AR) coating. Therefore, the subsequent AR coating process must be carried out at a temperature below 300° C, which, unfortunately, requires the use of more expensive coatings and processes. Also, such coatings and processes make it more difficult to achieve good AR coatings over large areas. Another significant disadvantage associated with the front side hydrogenation process is that it creates a damaged surface layer on the front side of the substrate. While the actual thickness of the damaged surface layer is relatively small compared to the total thickness of the substrate, the damaged surface layer nevertheless reduces cell performance. Recognizing the disadvantages associated with front surface hydrogenation, researchers have developed various processes to hydrogenate the substrate from the back side. A primary advantage of back side hydrogenation is that the damaged surface layer is created on, and confined to, the back side of the substrate, away from the junction side of the cell, thus minimizing its adverse effect on cell performance. Another advantage associated with back side hydrogenation is that it can be performed after the deposition of the front side AR coating, since the hydrogen ions are implanted from the back side of the cell. Unfortunately, however, back side hydrogenation is not without its drawbacks. For example, back side hydrogenation requires either a fully open or a partially open back contact, so the hydrogen can be implanted into the substrate. Another disadvantage is that it is still necessary to ensure that the subsequent processing steps, such as annealing or alloying, are carried out at temperatures below 300° C to prevent the hydrogen from escaping from the substrate. One way around the temperature limitation described above is to coat the back side of the cell with a hydrogen-encapsulating material to prevent the escape of the implanted hydrogen during subsequent high temperature processing. In my paper entitled A Backside Hydrogenation Technique for Defect Passivation in Silicon Solar Cells, J. Appl. Phys. 64, 15 November 1988, pp. 5264-5266, 1 described a process to confine the hydrogen in the silicon substrate during the subsequent back side contact alloying process. Essentially, that process required the deposition of a layer of aluminum about 2000 A thick on the back side of the cell to prevent the hydrogen from escaping during subsequent high temperature processing. While the foregoing process attempted to maximize the then-recognized benefits of substrate hydrogenation, the aluminum coating process represented an additional step that did not directly add to cell efficiency. Also, at that time it was not generally recognized that the hydrogenation process, while effectively reducing the minority carrier recombination losses, introduced its own performance degrading effects on the solar cell, which defects should be minimized to maximize cell efficiency. Therefore, there is a need for an improved hydrogen passivation process that maximizes the passivation effect on defects and impurities in the silicon substrate, while at the same time minimizing the deleterious effects associated with hydrogenation itself. Ideally, such a process should be able to be performed on completed solar cells and with a minimum number of steps to minimize cell production costs. Until this invention, no such process existed. Disclosure of the Invention Accordingly, it is a general object of this invention to provide an improved hydrogenation process that maximizes the passivation of defects and impurities in the silicon substrate and minimizes the deleterious effects introduced by the hydrogenation process itself. It is another object of this invention to provide an improved hydrogenation process that does not require the deposition of a hydrogen-encapsulating coating. It is a further object of this invention to provide an improved hydrogenation process that can be performed on a completed solar cell. It is yet a further object of this invention to provide an improved back side hydrogenation process that can produce epitaxial regrowth of the damaged surface layer. It is still yet another object of this invention to reverse deactivation of boron within the bulk of the substrate. Additional objects, advantages, and novel features of this invention shall be set forth in part in the description that follows, and in part will become apparent to those skilled in the art upon examination of the following or may be learned by the practice of the invention. The objects and the advantages of the invention may be realized and attained by means of the instrumentalities and in combinations particularly pointed out in the appended claims. To achieve the foregoing and other objects and in accordance with the purposes of the present invention, as embodied and broadly described herein, the improved back-side hydrogenation process according to this invention may comprise the steps of first bombarding the back side of the silicon substrate with hydrogen ions with intensities and for a time sufficient to implant enough hydrogen atoms into the silicon substrate to potentially passivate substantially all of the defects and impurities in the silicon substrate, and then illuminating the silicon substrate with electromagnetic radiation to activate the implanted hydrogen, so that it can passivate the defects and impurities in the substrate. The illumination step also annihilates the hydrogen-induced defects. Significantly, the illumination step is carried out according to a two stage illumination schedule. The first or low power illumination stage subjects the substrate to electromagnetic radiation having sufficient intensity to activate the implanted hydrogen, yet not drive the hydrogen from the substrate. The second or high power illumination stage subjects the substrate to higher intensity electromagnetic radiation which is sufficient to annihilate the hydrogen-induced defects and sinter/alloy the metal contacts. Brief Description of Drawings The accompanying drawings, which are incorporated herein and form a part of the specification, illustrate the preferred embodiment of the present invention and together with the description, serve to explain the principles of the invention. In the drawings: Figure 1 is a side view in elevation of a typical solar cell being hydrogenated by the process according to the present invention; Figure 2 is a side view in elevation of the hydrogenated solar cell being illuminated according to the illumination schedule of the present invention; and Figure 3 is a graph showing the two stage illumination schedule according to the present invention as a function of optical power per unit area vs. time. Detailed Description of the Invention The improved back side hydrogenation process according to the present invention is best seen in Figures 1 and 2 as it is used to hydrogenate a prefabricated polycrystalline photovoltaic solar cell 10 of the type well known in the art. The hydrogenation process according to the present invention is a two-step process. The first step in the process implants hydrogen atoms into the substrate 12 of cell 10 by exposing the back side 24 to a hydrogen ion beam 30 generated by a conventional Kaufman ion source (not shown). The implanted hydrogen atoms then rapidly diffuse throughout the substrate 12 by a mechanism that will be explained in more detail below. After the hydrogen has been implanted, the front side 16 of cell 10 is then illuminated by a light beam 26 in accordance with a two stage illumination schedule 34 (Figure 3). Essentially, the two stage illumination schedule 34 exposes the hydrogenated cell to light radiation having specific wavelength bands and specific intensity variations over time. Briefly, the first or low power stage 38 of the illumination schedule 34 activates the implanted hydrogen atoms so that they are free to move about the lattice and passivate the defects and impurities in the substrate. The second or high power stage 40 of the illumination schedule 34 annihilates the hydrogen induced defects and allows for the simultaneous sintering/alloying of the metallic coatings, if applicable, all while preventing the implanted hydrogen from being driven from the substrate. A significant advantage associated with the improved hydrogenation process according to the present invention is that it can be performed on completed cells and does not require the deposition of a separate, hydrogen-encapsulating coating. The hydrogenation process thereby maximizes cell performance and efficiency while minimizing the extra expense and processing steps typically associated with prior art hydrogenation methods. More importantly, because the hydrogenation process can be performed on finished cells, it does not restrict the materials or the kinds of processing steps that can be used to manufacture the cells. Another significant advantage of the hydrogenation process is that, not only does it provide for increased cell efficiency due to the passivation effect of the hydrogen, but that increase in cell efficiency is not compromised by the additional defects typically introduced by hydrogenation, such as the creation of defects deep within the substrate or the creation of a damaged surface layer. The second or high power stage 40 of the illumination schedule 34 not only annihilates the hydrogen induced defects, but also produces an epitaxial regrowth of the damaged back surface layer, thus further increasing cell efficiency. As an added advantage, the illumination process also reverses boron deactivation within the substrate. Referring now to Figure 1, the improved back side hydrogenation process according to the present invention will now be described in detail as it is applied to a conventional solar cell 10 having a p-type polycrystalline silicon substrate 12. In accordance with standard practice, an n-type conductivity region 14 is created on the front side 16 of substrate 12 and is separated from the p- type substrate 12 by a junction 18. A plurality of front surface metallic contacts 20 are disposed on the front surface 16 and both the front surface 16 and metallic contacts 20 are covered by an anti- reflective (AR) coating 22. Similarly, a plurality of back surface contacts 28 are disposed on the back side 24 of substrate 12. Back surface contacts 28 may be already sintered or alloyed to the back surface 24 of substrate 12, although it is not necessary. The back surface metallic contacts 2 may be sintered or alloyed during the illumination process, as will be described in more detail below. The first step in the improved hydrogenation process is to implant hydrogen atoms in the substrate 12, so that they can eventually passivate the defects and impurities in the silicon crystal lattice and reduce minority carrier losses at grain boundaries, dislocations, and other defects in the substrate. The hydrogen atoms are implanted into the substrate 12 by exposing the back sid 24 to a relatively low energy hydrogen ion beam 30 produced by a conventional Kaufman ion source (not shown). For effective implantation, the hydrogen ions 30 should have energies in the range of 500 eV to 2 keV and the substrate should be maintained at a temperature below about 300°C. In the preferred embodiment, the hydrogen is implanted at 1.5 keV with a beam current of about 0.5 mA/cm 2 for 15 minutes and the substrate is maintained at a temperature of about 250° C. Of course, lower beam current densities can be used if the exposure time is correspondingly increased. For example, if the beam current density is reduced to about 0.2 mA/cm 2 , the exposure time should be increased to about 30 minutes. As is well known, the hydrogen ion beam 30 will create a damaged surface layer 32. While the exact nature of the damaged surface layer created by the implantation of hy rogen ions i not known, it is believed to be a damaged area wherein the crystal structure has been somewhat disrupted by the incident hydrogen ions. At any rate, it is known that the damaged surface layer impairs the performance of the solar cell, particularly when it is located on the junction or front sid 16 of the cell 10. Back side hydrogenation, therefore, allows the damaged surface to be kept away from the junction side to reduce the performance degrading effect that it has on the cell. Until recently, it was thought that the damaged surface layer 32 was the only area damaged by the implanted hydrogen. However, it has since been discovered that the defects introduced by the hydrogenation process are not limited to the damaged surface layer, but extend deep within the substrate itself. While even less is known about the exact nature of the deep hydrogen defects than about the nature of the damaged surface layer, it is known that those defects partia-Jy offset the gains achieved by hydrogen passivation. Accordingly, the optical processing step of the present invention includes a two stage illumination schedule that annihilates a substantial percentage of the deep hydrogen-induced defects. The optical processing step and its associated illumination schedule 34 are best seen by referring simultaneously to Figures 2 and 3. As mentioned above, the illumination schedule 34 is significant in that it is responsible for many of the improvements associated with the process of the present invention. However, it will be easier to understand and apply the illumination schedule 34 shown in Figure 3 after first briefly describing the mechanism thought to control the hydrogen diffusion and passivation process. Since solar cells are minority carrier devices, the implanted hydrogen should be diffused throughout the entire substrate, typically about 300 μm thick, for effective passivation. While little is known about the diffusivity of hydrogen in silicon and its dependence on material parameters, or the impurity/defect passivation mechanism itself, I have developed a model for the hydrogen diffusion process that is in good agreement with experimental results derived thus far. According to that model, the implanted hydrogen ions combine with vacancies in the substrate to form hydrogen-vacancy (H-V) complexes that are nearly as mobile as the individual vacancies themselves , TT i ese hydrogen-vacancy (H-V) complexes rapidly cany the hydrogen atoms throughout the entire substrate, resulting in much higher diffusivities than observed in Czochralski and Float Zone wafer,, heretofore thought to pennit the highest hydrogen diffusivities. While the high hydrogen diffusivity resulting from the H-V complexes is advantageous in distributing the available hydrogen atoms throughout the lattice, the hydrogen atoms must be separated from the H-V complexes before they can migrate to and passivate the large scale defects in the lattice. The optical processing step of the present invention optically and electrically activates the inactive hydrogen atoms and separates them from the H-V complexes. Referring now to Figure 2, the optical processing step is caπied out by iUuminating the front surface 16 of the solar cell with high intensity radiation 26 according to the two stage illumination schedule 34 shown in Figure 3. The first or low power stage 38 breaks apart the H-V complexes, while the second or high power stage 40 annihilates the hydrogen-induced defects and sinters/alloys the metal contacts to the cell. The high power stage 40 also promotes epitaxial regrowth of the previously damaged surface layer 32. While the two stage illumination schedule 34 exposes the cell to approximately the same maximum power per unit area as the conventional illumination schedule 36 typically associated with conventional back side hydrogenation techniques, the existence of the lower power stage 38 allows the optical processing step to achieve results that were not possible with the prior art illumination schedules. Advantageously, the first or low power stage 38 breaks-up or dissociates the H-V complexes, freeing the hydrogen to passivate large scale defects and impurities, without driving the hydrogen from the substrate. Then, the optical power is increased to the second or high power stage 40 to anneal the hydrogen-induced defects by optical and thermal dissociation. The second power stage 40 also transfers sufficient energy to the cell to sinter/alloy the metal contacts 28 to the back surface 24 of substrate 12, if such sintering/alloying was not already performed on the finished solar cell 10. The electromagnetic radiation used in the illumination step according to this invention should have wavelengths in the range of about 4000 A to 15,000 A The intensity of the low power stage 38 should be in the range of about 1.5 to 3 Watts/cm 2 and the intensity of the high power stage 40 in the range of about 2 to 4 Watts/cm 2 . The durations of both the low and high power stages should be in the range of 10 to 20 seconds, yielding a total exposure time in the range of about 30 to 60 seconds. In the preferred embodiment, the optical power (illumination intensity), is linearly increased or "ramped up" over a period of about 15 seconds to the first or low power level 38, which is maintained at an intensity of about 1.5 Watts/cm 2 for about 10 seconds. The illumination intensity is then increased over the period of about 5 seconds to the second or high power level 40, which is maintained at an intensity of about 2 Watts/cm 2 also for about 10 seconds. The illumination intensity is then linearly decreased to zero over a period of about 5 seconds, yielding a total exposure time of about 45 seconds. It should be noted that the "ramp up" or steady increase in the optical power described in the foregoing example is not a requirement of the illumination schedule 34, but rather is imposed by the particular optical apparatus used to expose the cell. The only requirement of the illumination schedule 34 according to this invention is that it include a low power stage 38 to dissociate the H-V complexes without driving the hydrogen from the substrate, and a second, higher power stage 40 to anneal the hydrogen-imposed defects. Also, while the particular illumination schedule 34 shown and described herein is effective for passivating low cost polycrystalline solar cells, other illumination schedules are possible depending on the characteristics of the particular substrate sought to be passivated, as well as on the degree of passivation desired. Since such alternate illumination schedules would be obvious to persons having ordinary skill in the art after having become familiar with the details of the present invention as well as with the purposes to be accomplished by the illumination step, the present invention should not be regarded as limited to the particular illumination schedule 34 shown and described herein. The foregoing is considered illustrative only of the principles of the invention. Further, since numerous modifications and changes will readily occur to those skilled in the art, it is not desired to limit the invention to the exact construction and operation shown and described, and accordingly, all suitable modifications and equivalents may be resorted to as falling within the scope of the invention as defined by the claims which follow.

Claims: Claims The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows: 1. A method of hydrogenating a silicon substrate, wherein said silicon substrate has a front side and a back side and includes a plurality of defects and impurities, comprising the steps of: bombarding the back side of the silicon substrate with hydrogen ions having intensities and for a time sufficient to implant an amount of hydrogen atoms into the silicon substrate sufficient to potentially passivate substantially all of the defects and impurities in the silicon substrate; and illuminating the silicon substrate with electromagnetic radiation having an intensity and for a time sufficient to activate the hydrogen atoms in the substrate and passivate substantially all of the defects and impurities in the substrate, but not drive the hydrogen atoms out of the substrate. 2. The method of hydrogenating the silicon substrate of claim 1, wherein the intensity of the electromagnetic radiation includes a low power stage having a low power intensity sufficient to activate the hydrogen atoms in the substrate followed by a higher power stage having a higher power intensity sufficient to annihilate substantially all hydrogen-induced defects. 3. The method of hydrogenating the silicon substrate of claim 2, wherein said low power intensity is in the range of about 1.5 to 3 Watts/cm 2 and said higher power intensity is in the range of about 2 to 4 Watts/cm 2 . 4. The method of hydrogenating the silicon substrate of claim 3, wherein the electromagnetic radiation remains in said lower power stage for a time in the range of about 10 to 20 seconds and wherein the electromagnetic radiation remains in said higher power stage for a time in the range of about 10 to 20 seconds. 5. The method of hydrogenating the silicon substrate of claim 4, wherein the electromagnetic radiation has wavelengths in the range of 4,000 A to 15,000 A 6. The method of hydrogenating the silicon substrate of claim 5, wherein the substrate is illuminated for a total time in the range of about 30 to 60 seconds. 7. The method of hydrogenating the silicon substrate of claim 6, wherein the implanted hydrogen ions have energies in the range of about 500 eV to about 2 keV. 8. The method of hydrogenating the silicon substrate of claim 7, wherein the hydrogenation implant step is performed when the substrate is at a temperature in the range of about 100° C to 300° C. AMENDED CLAIMS [received by the International Bureau on 20 January 1994 (20.01.94); original claim 2 cancelled; original claims 1,3 and 8 amended; claims 3-8 renumbered as claims 2-7 (1 page)] 1. A method of hydrogenating a silicon substrate, wherein said silicon substrate has a front side and a back side and includes a plurality of defects and impurities, comprising the steps of: bombarding the backside of the silicon substrate with hydrogen ions with sufficient intensity and for a sufficient time to implant an amount of hydrogen atoms into the silicon substrate sufficient to potentially passivate substantially all of the defects and impurities in the silicon substrate; and illuminating the silicon substrate in a low-power stage with electromagnetic radiation having a low-power intensity for a sufficient time to activate the hydrogen atoms in the substrate and passivate substantially all of the defects and impurities in the substrate, but not drive the hydrogen atoms out of the substrate, and then illuminating the silicon substrate in a high-power stage having a higher power intensity sufficient to annihilate substantially all hydrogen-induced defects. 2. The method of hydrogenating the silicon substrate of claim 1 , wherein said low power intensity is in the range of about 1.5 to 3 Watts \cm 2 and said higher power intensity is in the range of about 2 to 4 Watts\cm 2 . 3. The method of hydrogenating the silicon substrate of claim 2, wherein the electromagnetic radiation remains in said lower power stage for a time in the range of about 10 to 20 seconds and wherein the electromagnetic radiation remains in said high power stage for a time in the range of about 10 to 20 seconds. 4. The method of hydrogenating the silicon substrate of claim 3, wherein the electromagnetic radiation has wavelengths in the range of 4,000 A to 15,000 A. 5. The method of hydrogenating the silicon substrate of claim 4, wherein the substrate is illuminated for a total time in the range of about 30 to 60 seconds. 6. The method of hydrogenating the silicon substrate of claim 5, wherein the implanted hydrogen ions have energies in the range of about 500 eV to about 2 keV. 7. The method of hydrogenating the silicon substrate of claim 6, wherein the hydrogenation implant step is performed when the substrate is at a temperature in the range of about 100°C to 300°C. STATEMENT UNDER ARTICLE 19 The Amendments made to claims 1, 3 and 8 as specifically described in the accompanying Letter Describing Differences Between Replaced Sheets and Replacement Sheets submitted concurrently herewith, are made to more clearly describe the invention.

Inventors: SOPORI BHUSHAN L, SOPORI, BHUSHAN, L.
Applicants: MIDWEST RESEARCH INST, SOPORI BHUSHAN L, MIDWEST RESEARCH INSTITUTE
Application year: 1993
Main classification: H01L21
IPC codes: H01L21, H01L31