Method for the treatment of mechanical pulps

Abstract: This invention relates to a method for the recovery of organic substances dissolved or brought into a colloid form during the manufacture of a mechanical pulp where said mechanical pulp has not been subject to previous alkaline bleaching or other previous process carried out under alkaline conditions. The method is characterized in the deacetylation of the galactoglucomannans having been brought into dissolved or colloidal form during the pulping process, and subsequent deposition of said deacetylated glucomannans onto a solid phase, such as pulp fibres or organic or inorganic additives. The deacetylation is performed either by alkali or enzymatically. The method diminishes the organic substance loading on recycling waters and effluents, and improves the yield and strength properties of the pulp.

Description: This invention relates to a novel method for the treatment of mechanical pulps which have not previously undergone alkaline treatment e.g. in connection with peroxide bleaching. The method results in improved yield and quality of said pulps. The method further gives rise to a decrease in dissolved and colloidal substances (DCS) in the backwater. The most important mechanical pulp qualities are thermomechanical pulp (TMP), groundwood (SGW), pressurized groundwood (PGW), refiner mechanical pulp (RMP), pressurized refiner mechanical pulp (PRMP) and chemithermomechanical pulp (CTMP). The mechanical pulps are mostly perpared from softwood. The mechanical pulps distinguish from chemical pulps mainly with respect to the high yield which is achieved as a result of the lignin and carbohydrate-saving pulping method. Chemical pulps, from which substantial amounts of the lignin and hemicellulose components have been removed, have a high percentage of cellulose compared to that of mechanical pulps, and have therefore strength qualities superior to those of mechanical pulps. The main use of mechanical pulps is cheaper paper qualities of relatively short-term usage, particularly newsprint. Traditionally newsprint has been made of approximately 80% groundwood and 20% chemical pulp. More recently, the introduction of mechanical pulp qualities of improved strength properties such as TMP, PRMP and PGW have made it possible to considerably decrease the amount of chemical pulp in newsprint. These mechanical pulps are also of great importance in various kinds of other printing papers such as journal paper grades. Most of the mechanical pulps for printing papers are either used as unbleached or are bleached under very mild conditions in order to save as much of the pulp substance as possible. A usual bleaching method for mechanical pulps is the dithionite method, a process carried out at about pH 5 to 6. Another usual process for bleaching mechanical pulps is the bisulphite method, which is carried out at a pH of about 4. Peroxide bleaching, although classified as a wood saving method, causes a higher loss of yield than the dithionite and bisulphite methods, but on the other hand it gives higher brightness. Peroxide bleaching of TMP has been subject to extensive research work and it has also to some extent replaced the above mentioned bleaching methods for TMP because this pulp has partially replaced chemical pulp in many paper grades. Peroxide bleaching is, contrary to the afore mentioned methods, carried out in alkaline conditions, pH 10,5 to 11. However, the main part of mechanical pulps today are either used unbleached or are bleached under methods of slightly acidic conditions. Softwoods contain about 20-25 % mannans consisting of a glucomannan backbone to which acetyl groups and galactose residues are attached. These polyoses are called O-acetylgalactoglucomannans and a partial structure of such a polyose is illustrated as follows: Deacetylation of glucomannans, has been observed in connection with the alkaline conditions during studies with peroxide bleaching of mechanical pulp, particularly TMP. Such results have been reported by J Thornton et al "Effects on peroxide bleaching on spruce TMP on dissolved and colloidal organic substances" presented at the 6th Int. Symp. of Pulping and Wood Chem., Melbourne, Australia, May 7th, 1991. An article by B Holmbom et al, "Chemical Changes in Peroxide Bleaching of Mechanical Pulps", Das Papier, 45. Jahrgang, Heft 10A, 1991, pp 16 - 22 also reported a deacetylation of glucomannans after the alkaline peroxide bleaching process. The same reference disclose that the deacetylation of galactoglucomannans dissolved in the pulp suspension leads to their adsorption onto the pulp fibers and thus to a recovery in pulp yield of about 1 %. Previous studies (Laffend K and Swenson H, Tappi 51(3)118-123(1968) and Hansson, J-Å, Holzforschung 24 (1970) H.3, pp 77-83) have reported the adsorption of hemicelluloses onto cellulose fibres, and the improvement of adsorption due to deacetylation of the glucomannan. Lindström T et al, Svensk Papperstidn. 80(11):341-345, 1977, reported on improvements of strength in pulps to which hemicelluloses and fines have been added. To sum up, from peroxide bleaching of mechanical pulp under alkaline conditions it is known that such alkaline conditions cause deacetylation of dissolved and colloidal galactoglucomannans derived from the pulping process, and that such deacetylated galactoglucomannans adsorb onto the fibres resulting in an improved yield. This invention is based on the idea to utilize this phenomenon, the deacetylation of the galactoglucomannans, to recover organic dissolved or colloidal substances originating from the mechanical pulping process where the mechanical pulp has not been subject to any previous alkaline treatment such as peroxide bleaching. No such use of the deacetylation of galactoglucomannans has been suggested before although there exists a great need to improve pulp yields and to diminish the organic substance loading on recycling waters and effluents. This invention is applicable to the main part of all mechanical pulps manufactured, because as said above, the main part of these pulps has been subject to only mild bleaching under acidic conditions or no bleaching at all, and accordingly, not undergone any alkaline treatment. The invention is not intended for use with mechanical pulps that are bleached with e.g. peroxide under alkaline conditions, because deacetylation takes place automatically during the alkaline bleaching process. The object of the present invention is a method for the recovery of organic substances dissolved or brought into a colloid form during the manufacture of a mechanical pulp where said mechanical pulp has not been subject to previous alkaline bleaching or other previous process carried out under alkaline conditions. A characteristic feature of the method is the deacetylation of the galactoglucomannans having been brought into dissolved or colloidal form during the pulping process and subsequent deposition of said deacetylated glucomannans onto a solid phase. The deposition of the deacetylated glucomannans can take place on any solid component in the system, e.g. on a fibre from the same mechanical pulp; another mechanical, semichemical or chemical pulp fibre; or an organic or inorganic additive. The fibres can be virgin or recycled. The deacetylation of the galactoglucomannans can be carried out directly on the pulp suspension. However, according to a preferred embodiment, the backwater is separated from the pulp suspension first. Then the deacetylation is performed on the galactoglucomannans in the backwater. After the deacetylation of the glucomannans the backwater is returned to a mixture comprising pulp of one or more grades and optionally organic or inorganic additives. In case the backwater is returned to the same mechanical pulp from which the the dissolvbed or collidal glucomannans originated, the deposition of the deacetylated glucomannans on the pulp fibres will lead to increased strength of that pulp grade. The treatment of the backwater instead of the whole pulp suspension leads to more uniform process conditions, and moreover, the deacetylation chemicals are prevented from acting adversively on the pulp fibres. The deacetylation can be performed by using an enzyme or enzyme mixture deacetylating the glucomannans. Suitable enzyms to be used are esterases or enzyme mixtures containing esterase activity, specifically acetyl esterase activity. Most preferable are those having acetyl-glucomannan esterase activity. The process can be carried out in the pH range 3 to 8, but the most preferable pH range is 5 to 6. The temperature can vary within the range 20 to 90°C, preferably 50 to 70°C. The dose ranges from 0.01 to 100 000 µg esterase/mg DCS glucomannans. The invention is presented in more detail in the examples below. In these studies, a method of selectively deacetylating dissolved and/or colloidal glucomannans were investigated. In the example was used an enzyme that had glucomannan deacetylating esterase activity, see Journal of Biotechnology, 18 (1991), 69-84. The method was successful in lowering the amount of dissolved and colloidal organic substances. Example 1 describe the experiment. Example 1 A 1% suspension of TMP from Norway spruce was made according to the standard method disclosed in the article by J. Thornton et al "Effects on peroxide bleaching on spruce TMP on dissolved and colloidal organic substances" presented at the 6th Int. Symp. of Pulping and Wood Chem., Melbourne, Australia, May 7th, 1991. A 20 ml aliquot of this suspension was put in a test tube. 200 µl of the acetyl esterase glucomannan deacetylating enzyme was added to the 20 ml suspension and the tube was capped, thoroughly shaken, and placed in a 40°C water bath. Constant mild shaking was used to keep the tube contents thoroughly mixed throughout the 16 h reaction time. The contents of the tube were then centrifuged. Standard analyses were then made on the resulting fiber and fines-free supernatant. A blank analysis was performed with no enzyme added as a comparison. The results obtained are presented below in Table 1. Results from enzymatic deacetylation experiment Non-treated Enzyme-treated Percent change TOC, mg/l 229.0 186.0 -19% Carbohydrates, mg/l 190.9 138.8 -27% Although not as favorable as the alkaline treatment, this clearly shows that enzymatic deacetylation is a possible method to use for this invention. The decreased carbohydrates were galactoglucomannans. The calculated yield increase was about 0.9%. Still a very significant yield increase. The benefits of this treatment are that no corrosive salts are formed as in the alkaline-deacetylation method. Further research will lead to improved enzyme preparations that will work more effectively at mill conditions.

Claims: A method for the recovery of dissolved or colloidal galactoglucomannan-containing organic substances from mechanical pulp which has not been subject to alkaline conditions which comprises deacetylating the said galactoglucomannans by using an enzyme or mixture of enzymes and subsequently depositing the deacetylated galactoglucomannans on to a solid phase in the pulp. A method according to claim 1 wherein the solid phase is fibre from the same mechanical pulp; another mechanical, semichemical or chemical pulp fibre; or an organic or inorganic additive. A method according to claim 1 or 2 wherein the deacetylation is performed by using an esterase enzyme or an enzyme mixture containing esterase activity. A method according to claim 3 wherein the enzyme or enzyme mixture has acetyl esterase activity. A method according to claim 4 wherein the enzyme or enzyme mixture has acetyl-glucomannan esterase activity. A method according to any one of claims 1 to 5 wherein the deacetylation is performed on galactoglucomannans in the backwater from the pulp and, after the deacetylation, the backwater is returned to a mixture comprising pulp of one or more grades and optionally organic or inorganic additives. A method according to claim 6 wherein the pH of the backwater is adjusted to about 5 to 6 by the addition of an acidifying agent before the backwater is returned to the pulp. A method according to any one of claims 1 to 7 wherein the deacetylated galactoglucomannans are deposited onto fibres from the same mechanical pulp from which the dissolved or colloidal galactoglucomannans originated, whereby the yield and the strength properties of the mechanical pulp are improved.

Inventors: ECKERMAN CHRISTER, EKMAN RAINER, HOLMBOM BJARNE, TENKANEN MIJA, THORNTON JEFFREY, VIIKARI LIISA, ECKERMAN, CHRISTER, EKMAN, RAINER, HOLMBOM, BJARNE, TENKANEN, MIJA, THORNTON, JEFFREY, VIIKARI, LIISA
Applicants: METSAE SERLA OY, METSAE-SERLA OY
Application year: 1993
Main classification: D21C9
IPC codes: D21C9, C12P19, D21C5, C12S3