TUBULAR LAMINATE AND PRODUCTION THEREOF

Abstract: A process for producing a tubular laminate which comprises subjecting the surface of a tubular fluororesin molding to electric discharge treatment in an inert gas atmosphere containing a functional organic compound and coating the resultant surface with a molten resin by extrusion. This process can provide a firm adhesion between the fluororesin molding and the coating resin even without using any adhesive, whereby the step of applying an adhesive can be dispensed with and a tubular laminate can be produced continuously.

Description: TECHNICAL FIELD The present invention relates to a process for producing a tubular laminate of a fluorine-containing resin. BACKGROUND ART A fluorine-containing resin has excellent characteristics such as non-stickiness, stain resistance, heat resistance, chemical resistance, clearness, ultraviolet ray aging resistance, weatherability, and water and oil repelling property, which are not possessed by the other resins. However, the fluorine-containing resin is very difficult to be laminated on the other materials due to its non-sticking characteristic. Therefore, the fluorine-containing resin is not actually widely used in spite of the above-mentioned excellent characteristics. A tubular laminate is not an exception. Effort to conduct lamination on a fluorine-containing resin molded article has been first directed to modification of a surface of the fluorine-containing resin molded article, and various modification methods have been developed. For example, there are known methods in which an electric discharge treatment such as corona discharge is conducted (JP-B-17485/1962, JP-B-51421/1984, JP-B-54848/1990, JP-A-214620/1984, JP-A- 9533/1988, JP-A-218336/1988, JP-A-222838/1988), a method in which a flame treatment or a metallic sodium treatment is conducted (JP-B-10176/1988), a method in which surface roughing treatment is conducted by sand blast, and the like. DE-B-1 290 717 teaches the surface treatment of polymeric materials by electrical discharge in the presence of a polymerizable organic compound, a non-polymerizable organic compound with active hydrogens or a perhalogenated hydrocarbon. In most cases, however, sufficient adhesion may not be obtained only by modifying the surface of the fluorine-containing resin. Therefore, an adhesive is used for lamination. These methods are similarly applied to lamination of a tubular fluorine-containing resin molded article. JP-B-51421/1984 discloses a process for producing a tubular laminate in which after treating an outer surface of an inner layer of the fluorine-containing resin molded article by corona discharge, a rubber-based primer layer is formed on the treated surface, and an unvulcanized rubber sheet is wrapped on the primer layer, then vulcanization is conducted. For forming the primer layer or the adhesive layer, however, more steps are necessary corresponding thereto. Further, various considerations are required for selection of the adhesive. The present invention provides a process for producing a tubular fluorine-containing resin laminate without an adhesive layer (a primer layer) and having a strong adhesion to each other. DISCLOSURE OF THE INVENTION The present invention relates to a process for producing a tubular laminate which comprises, discharge-treating an outer surface of a tubular fluorine-containing resin molded article in an inert gas atmosphere containing an organic compound having a functional group, extruding a molten resin onto the treated surface, and coating the treated surface with the molten resin, wherein the coating resin has a melting point lower than the fluorine-containing resin of the inner layer and a surface tension of not less than 30 dyn/cm. The preferred embodiments of the present invention are explained hereinbelow: The fluorine-containing resin used in the present invention is not restricted, provided that a tubular molded article can be produced from the resin. Examples are polytetrafluoroethylene (PTFE) or a modified compound thereof, tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer (PFA), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), tetrafluoroethylene-ethylene copolymer (ETFE), tetrafluoroethylene-vinylidene fluoride copolymer (TFE/VdF), tetrafluoroethylene-hexafluoropropylene-perfluoroalkyl vinyl ether copolymer (EPA), polychlorotrifluoroethylene (PCTFE), chlorotrifluoroethylene-ethylene copolymer (ECTFE), chlorotrifluoroethylene-vinylidene fluoride copolymer (CTFE/VdF), poly(vinylidene fluoride)(PVdF), poly(vinyl fluoride) (PVF), and the like. Among them, PTFE, PFA, FEP, ETFE, PCTFE and PVdF are particularly preferable. The fluorine-containing resin molded article may be either a tubular article itself or a coated layer formed on other tubular substrates, for example, a metallic pipe made of steel, copper, aluminium or the like, a nonmetallic pipe made of glass, cement, resin or the like. For the surface modification of the fluorine-containing resin molded article, there are adopted discharge treatments such as corona discharge treatment, glow discharge treatment, plasma discharge treatment and sputtering treatment (JP-B-17485/1962, JP-B-12900/1974, US-A-3296011). For example, in the corona discharge treatment, the surface treatment is carried out by exposing a surface to be modified to an atmosphere of an inert gas (for example, nitrogen gas, helium gas, argon gas, or the like) containing an organic compound having a functional group, applying a high frequency voltage between electrodes to generate corona discharge, thereby producing active species on the surface, subsequentry introducing the functional group of the organic compound or graft-polymerizing a polymerizable organic compound. Conditions of the corona discharge may be properly selected according to a dielectric constant of the fluorine-containing resin molded article. The feature of the present invention is that the organic compound having a functional group exists in the atmosphere on the discharge-treatment. The surface of the fluorine-containing resin modified by the discharge treatment has an increased surface activity, and an extremely enhanced reactivity. A surface tension after the modification is preferably not less than approximately 30 dyn/cm, particularly not less than approximately 40 dyn/cm. Examples of the functional group are, for instance, hydroxyl group, epoxy group, carboxyl group, ester group, carbonyl group, isocyanate group, nitrile group, amino group, ether bond, polymerizable double bond, and the like. However, the functional group is not restricted to them. The compound having the functional group may be either a polymerizable compound or a non-polymerizable compound. Non-restricted examples are listed below. (a) Compounds having hydroxyl group Polymerizable organic compounds: Polyhydric alcohols such as ethylene glycol and gricerol; and the like. Non-polymerizable organic compounds: Monohydric alcohols such as methanol, ethanol and phenol; and the like. (b) Compounds having epoxy group Polymerizable organic compounds: Epoxydized compounds such as glycidyl methacrylate and epichlorohydrin; and the like. Non-polymerizable organic compounds: Glycidyl ethers, epoxy alkanes; and the like. (c) Compounds having carboxyl group Polymerizable organic compounds: Dicarboxylic acids such as phtalic acid and maleic acid; acrylic acids such as acrylic acid and methacrylic acid; and the like. Non-polymerizable organic compounds: Carboxylic acids such as formic acid and acetic acid; and the like. (d) Compounds having ester group Polymerizable organic compounds: Esters such as methyl acrylate, methyl methacrylate, ethyl acrylate, glycidyl methacrylate and diallyl phthalate; and the like. Non-polymerizable organic compounds: Esters such as ethyl formate and ethyl acetate; and the like. (e) Compounds having carbonyl group Polymerizable organic compounds: The carbonyl group in the carboxylic acids or the esters of (c) and (d). Non-polymerizable organic compounds: Ketones such as acetone (carbonyl group in monofunctional carboxylic acids and esters). (f) Compounds having isocyanate group Isocyanates such as tolylenediisocyanate and its derivatives. (g) Compounds having nitrile group Polymerizable organic compounds: Acrylonitriles such as acrylonitrile and methacrylonitrile; cyanoacrylates; and the like. Non-polymerizable organic compounds: Nitriles such as acetonitrile and propionitrile; and the like. (h) Compounds having amino group Polymerizable organic compounds: Melamines; diamines; acrylamides; and the like. Non-polymerizable organic compounds: Various amines and ammonium salts; and the like. (i) Compounds having ether bond Polymerizable organic compounds: Vinyl ethers such as vinyl methyl ether and vinyl ethyl ether; and the like. Non-polymerizable organic compounds: Various ethers such as diethyl ether and glycidyl methyl ether; or the like. (j) Compounds having polymerizable double bond Olefines such as ethylene and propylene; vinyl carboxylates such as vinyl acetate; perhalogenated olefins such as chlorotrifluoroethylene, tetrafluoroethylene and hexafluoropropylene; or the like. The organic compound is required to be present in gaseous (steam) state in the inert gas atmosphere. The concentration varies with kinds of the organic compound, and is usually 0.1 to 10.0 % by mole, preferably 0.5 to 7.0 % by mole. Therefore, the organic compound necessarily has a vapor pressure of at least not less than 1 mmHg at the discharge treatment temperature (usually from 20° to 100°C). In case of the polymerizable organic compound, it is particularly preferable to combine with a coating resin comprising a polymer obtained by polymerization or copolymerization of the polymerizable organic compound. In case of the non-polymerizable organic compound, it is required to have at least one active hydrogen or to be a compound having a bond dissociation energy of not more than 100 kcal, since the non-polymerizable organic compound has to be activated by the discharge treatment. In the present invention, the coating layer is formed by melt-extruding the coating resin directly on the thus surface-modified tubular fluorine-containing resin molded article. The coating resin has a lower melting temperature than that of the fluorine-containing resin of the inner resin, preferably an excellent wettability with the surface treated fluorine-containing resin molded article, and a surface tension of not less than 30 dyn/cm. When the surface tension is less than that, since the wettability is worse, adhesion is not good. The preferable coating resins are, for example, polyamides such as nylon 12, nylon 11, nylon 6 and nylon 66; polyolefins such as polyvinylchloride (PVC); poly(vinyl acetate), poly(methyl methacrylate), polyacrylonitrile, polyethyleneterephthalate, polyurethane, and the like. Among them, particularly preferable is a polymer obtained by polymerization or copolymerization of a monomer which has the same functional group as or a functional group having an affinity with the functional group of the organic compound present in the atmosphere for modification, because the polymer has an improved adhesion. A polymer which has a good excellent wettability with the modified surface provides a sufficient adhesion. Into the coating resin, there may be blended usual additives, for example, curing agents, ultraviolet ray absorbents, fillers, pigments, antistatic agents, plasticizers, and the like. As an extrusion-coating method, there may be employed a method similar to a usual electric cable coating method. For example, there is a method which comprises, discharge-treating an outer surface of a tubular fluorine-containing resin molded article laminated on a mandrel made of resin or metal in an inert gas atmosphere which contains the organic compound having a functional group, subsequently extruding a coating resin continuously through a crosshead of an extruder, and then coating the outer surface with the resin. The extrusion-coating method is not limited to this method. According to the present invention, there can be continuosly produced a tubular laminate made of different kinds of resins with strong adhesion therebetween without using an adhesive. BEST MODE FOR CARRYING OUT THE INVENTION The present invention is explained by means of the following Examples. The present invention is not limited only to the Examples. Example 1 A tubular molded article (outer diameter 6.0 mm, thickness 0.2 mm) made of ETFE (melting temperature 260°C) was discharge-treated in a nitrogen gas atmosphere containing 7 % by mole of vinyl acetate vapor under a charge density of 3 W/cm 2 to obtain a tubular molded article of which outer surface was modified with vinyl acetate (surface tension after modification 45 dyn/cm). Onto the surface modified tubular fluorine-containing resin molded article was extruded a molten nylon 12 (melting temperature 180°C, surface tension 36 dyn/cm) heated at 220°C to form a coating layer having a thickness of 1.0 mm. When peel strength of the resulting laminate was measured according to the following method, the peel strength was 3.0 kgf/inch. (Peel strength) A universal tension meter (Tensiron available from Orientech Kabushiki Kaisha) was used to carry out 180° peel. Stretching rate was 100 mm/min. Examples 2 to 6 Tubular fluorine-containing resin molded articles were discharge-treated under the conditions shown in Table 1 according to the method of Example 1 to modify their surfaces. The coating resins shown in Table 1 were melt-extruded to obtain tubular laminates, and the peel strengths were measured. The results are shown in Table 1. Comparative Example 1 A molten resin (nylon 12) is extruded to obtain a tubular laminate coated herewith in the same manner as in Example 1 except that the surface treatment was not carried out. The peel strength was not more than 0.1 kgf/inch. Comparative Example 2 The surface modification was carried out and a molten resin (nylon 12) was extruded to obtain a tubular laminate coated therewith in the same manner as in Example 1 except that the discharge treatment was conducted in the absence of vinyl acetate. The peel strength was 0.5 kgf/inch. Comparative Example 3 A coating resin was extruded to obtain a tubular laminate coated therewith in the same manner as in Example 1 except that polypropylene was used instead of nylon 12 as the coating resin. The peel strength was 0.2 kgf/inch. Each abbreviation used in Tables 1 to 3 has the following meaning. (Fluorine-containng resin) FEP: Tetrafluoroethylene-hexafluoropropylene copolymer. ETFE: Tetrafluoroethylene-ehtylene copolymer PFA: Tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer (Organic compound) VAc: Vinyl acetate GMA: Glycidyl methacrylate (Coating resin) PU: Polyurethane elastomer PE: Polyethylene PP: Polypropylene INDUSTRIAL APPLICABILITY According to the present invention, there can be obtained a strong adhesion between the tubular fluorine-containing resin molded article and the coating resin without using an adhesive. Therefore, an applying step of the adhesive can be omitted as well as the tubular laminate can be produced continuosly.

Claims: A process for producing a tubular laminate which comprises, discharge-treating an outer surface of a tubular fluorine-containing resin molded article in an inert gas atmosphere containing an organic compound having a functional group, extruding a molten resin onto the treated surface, and coating the treated surface with the molten resin wherein the coating resin has a melting point lower than the fluorine-containing resin of the inner layer and a surface tension of not less than 30 dyn/cm. The process of Claim 1, wherein the functional group of the organic compound is hydroxyl group, epoxy group, carboxyl group, ester group, carbonyl group, isocyanate group, nitrile group, amino group, ether bond or polymerizable double bond. The process of Claim 1, wherein the fluorine-containing resin is polytetrafluoroethylene, tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, tetrafluoroethylene-hexafluoropropylene copolymer, tetrafluoroethylene-ethylene copolymer, polychlorotrifluoroethylene or poly (vinylidene fluoride).

Inventors: IDEMORI KENJIRO, NAKATA YUTAKA, SHIMADA KAZUHIKO, IDEMORI, KENJIRO, NAKATA, YUTAKA, SHIMADA, KAZUHIKO, IDEMORI, Kenjiro, Yodogawa-seisakusho, NAKATA, Yutaka, Yodogawa-seisakusho, SHIMADA, Kazuhiko, Yodogawa-seisakusho
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LIMITED
Application year: 1993
Main classification: B29C47
IPC codes: C08J5, B32B1, B29C47, B29C59, C08J7, B32B27, B29D23, F16L9, B29K27, F16L11, B29L9, B29L23