Hydrogen-absorbing alloy for negative electrode

Abstract: A hydrogen-absorbing alloy electrode having a hydrogen-absorbing alloy in a single crystal system and composed of at least three elements which are coated on a conductive substrate. One of the at least three elements has a density distribution profile with at least two adjacent high density peaks and a lowest density point between the at least two adjacent high density peaks. A density difference between one of the at least two adjacent high density peaks and the lowest density point is not less than about 3.0 wt% and a distance between the two adjacent high density peaks is not less than about 20 µm. The hydrogen-absorbing alloy has a volume of 2µm³ and may include an additive selected from a group consisting of Manganese (Mn), Boron (B), Tungsten (W) and Cobalt (Co).

Description: BACKGROUND OF THE INVENTION 1. Field of the invention This invention relates to a hydrogen-absorbing alloy for use as a negative electrode in an alkaline storage battery. 2. Description of the prior art Currently, research is being carried out to develop for hydrogen-absorbing alloys for use in a battery, and which are capable of absorbing and desorbing hydrogen reversibly. Also being developed are metal hydride storage batteries which use such hydrogen-absorbing alloys for their negative electrode. Metal hydride storage batteries, when compared to conventional Ni-Cd batteries or lead acid batteries, can be lighter and have a larger capacity. Proposed hydrogen-absorbing alloys for the negative electrode in the battery, include LaNi 5 , LaNi 4 Co and LaNi 4 Cu such as described in Japanese patent publication 59-49671, hydrogen-absorbing alloys of an Mm-Ni type (where the "Mm", a so-called "Misch Metal", is a mixture of rare earth elements, such as La, Ce, Nd, Pr, etc.) are also being developed. These alloys produce batteries that can obtain a high capacity. The above alloys are obtained by conventional methods, which typically produce alloys with homogeneous texture. This reduces cracking within the alloy. Therefore, when using these alloys for a negative electrode in a battery, the surface area does not increase, and there is a reduced reaction area. As a result, discharge characteristics of hydrogen descrbtion for the alloys at low temperatures deteriorate. Further, the oxygen absorbing capability of these alloys is inferior, thus, making rapid charging of the battery problematic. In typical conventional process for manufacturing the hydrogen-absorbing alloys, each component of the alloy is measured and mixed, melted in an arc furnace in an inert argon atmosphere, and cooled. Next, the alloys are held in a vacuum furnace and heat-treated at a high temperature (approximately 1000 °C) for a fixed period of time. This is an "annealing" heat treatment which causes homogenization of the hydrogen-absorbing alloys. To complete the electrode, the hydrogen-absorbing alloys are mechanically pulverized into granules. The granules are mixed into a paste with a conductive agent and a binder, such as powered polytetrafluoroethylene (PTFE). A coating of the paste is provided on a conductive substrate, such as a current collector comprising a punched metal plate. The current collector is then pressed to form the hydrogen-absorbing alloy electrode. SUMMARY OF THE INVENTION Accordingly, it is a primary object of an embodiment of the present invention to provide a hydrogen-absorbing alloy electrode with improved electrode characteristics, such as improved discharge characteristics in low temperatures. Another object of an embodiment of the present invention is to provide a hydrogen-absorbing alloy electrode with improved electrode characteristics, such as improved high-rate charge characteristics in the low temperatures. Still another object of an embodiment of the present invention is to provide a hydrogen-absorbing alloy electrode with a large discharge capacity. According to the present invention there is provided a hydrogen-absorbing alloy electrode comprising a conductive substrate on which is provided a hydrogen-absorbing alloy in a single phase crystal system and composed of at Icast three elements; wherein one of said at least three elements has a density distribution profile as provided with measurement by EPMA which for a 2 µm 3 sample of the alloy has at least two adjacent high density peaks and a lowest density point between said at least two adjacent high density peaks, and wherein a density difference between one of said at least two adjacent high density peaks and said lowest density point is not less then 3.0 wt% and a distance between said two adjacent high density peaks is not less than 20 µm. The alloy preferably has the formula ANi a Co b Mn c X d , in which A is a Misch Metal or mixture of rare earth elements include Lanthanum, the ranges of "a", "b", "c" and "d" are respectively defined by 2.5 ≦ a ≦ 3.5, 0 ≦ b ≦ 1.5, 0 ≦ c ≦ 1 and 0 ≦ d ≦ 0.3, the value of a+b+c+d is 3.85 to 5, and X is one of the elements iron (Fe), Copper (Cu), Molybdenum (Mo), Tungsten (W), Boron (B), Aluminium (Al), Silicon (Si) and Tin (Sn). The single phase crystal system may be a hexagonal crystal system. The present invention also provides a hydrogen-absorbing alloy for a negative electrode, the alloy having a single phase crystal system of the formula ANi a Co b Mn c X d , in which A is a Misch Metal or mixture of rare earth elements including Lanthanum, the ranges of "a", "b", "c" and "d" are respectively defined by 2.5 ≦ a ≦ 3.5, 0 ≦ b≦1.5, 0≦c≦1 and 0 ≦ d ≦ 0.3, the value of a+b+c+d is 3.85 to 5, and X is one of the elements iron (Fe), Copper (Cu), Molybdenum (Mo), Tungsten (W), Boron (B), Aluminium (Al), Silicon (Si) and Tin (Sn); wherein one of said at least three elements has a density distribution profile which for a 2 µm 3 sample of the alloy has at least two adjacent high density peaks and a lowest density point between said at least two adjacent high density peaks, and wherein a density difference between one of said at least two adjacent high density peaks and said lowest density point is not less then 3.0 wt% and a distance between said two adjacent high density peaks is not less than 20 µm. The present invention further provides a method of manufacturing a hydrogen-absorbing alloy by cooling a melted mixture of the alloy at a first cooling speed until a nucleus formation temperature is reached and then by quenching at a second cooling speed faster than said first cooling speed, wherein said nucleus fonnation temperature ranges from about 1200 °C to about 1300 °C, and said second cooling speed is greater than 300 °C/min. The second cooling speed may be greater than 500°C/min. A method of manufacturing a hydrogen-absorbing alloy electrode is also provided, the method comprising manufacturing a hydrogen-absorbing alloy as described above and placing said alloy on a conductive substrate. BRIEF DESCRIPTION OF THE DRAWINGS These and other objects, advantages and features of the invention will become apparent from the following description thereof taken in conjunction with the accompanying drawings which illustrate specific embodiments of the invention. In the drawings: FIG. 1 is a cross-sectional illustration of a battery in accordance with an embodiment of the present invention; FIG. 2 is a graph showing a part of the density distribution profile for a hydrogen-absorbing alloy in accordance with a first embodiment of the present invention; FIG. 3 is a graph showing the relationship between temperature and the discharge capacity of a battery in accordance with a first embodiment of the present invention; FIG. 4 is a graph showing the relationship between the charging time and an internal pressure of a battery in accordance with a first embodiment of the present invention; FIG. 5 is a graph showing the relationship between the distance between two adjacent high density peaks and a discharge capacity of a battery in accordance with a first embodiment of the present invention; FIG. 6 is a graph showing the relationship between the distance between the two adjacent high density peaks and internal pressure of a battery in accordance with a first embodiment of the present invention; FIG. 7 is a graph showing the relationship between temperature of a battery and the discharge capacity in accordance with a further embodiment of the present invention; FIG. 8 is a graph showing the relationship between the charging time and internal pressure of a battery in accordance with a further embodiment of the present invention; FIG. 9 is a graph showing the relationship between the discharge between the two adjacent high density peaks and a discharge capacity of a battery in accordance with said further embodiment of the present invention. The following detailed description is of the best presently contemplated mode of carrying out the invention by the inventors. This description should not to be taken in a limiting sense, but is made merely for the purpose of illustrating general principles of embodiments of the invention. The scope of the invention is best defined by the appended claims. The hydrogen-absorbing alloys according to embodiments of the present invention composed of at least three elements. However, the crystal structure of the alloys are mainly in a single phase crystal system. One of the at least three elements is partially condensed in an alloy mixture, and high density portions may be obtained. One of the three elements is measured with EPMA (Electron Probe Micro Analysis), which provides a density distribution profile with at least two adjacent high density peaks and a lowest density point between the at least two adjacent high density peaks. One of the three elements has a density difference between one of the at least two adjacent high density peaks and the lowest density point of not less than about 3.0 wt%. Further, the distance between the two adjacent high density peaks is not less than about 20 µm. This distance is defined by a real length between the two adjacent high density peaks measured by the EPMA method. This distance in embodiments of the present invention has the same meaning as a density pitch which is defined in this specification. For the avoidance of doubt, EPMA is an analysis performed by emitting an electron beam towards a small portion of a sample, in response to which an element of the sample will emit a characteristic X-ray. The wavelength, energy and intensity of this characteristic X-ray may then be analysed to identify both the type of element and its density (i.e. its quantity per unit volume). The so-called density profile of the element is obtained by linearly moving the irradiating electron beam across the sample. One skilled in the art of EPMA would appreciate that the term "density distribution profile", used in the present application, refers to the result of a linear analysis by EPMA. One example of such a density distribution profile is shown in figure 2 of the present application. Referring to figure 2, the horizontal axis represents the physical position of the sample and the vertical axis represents the existing concentration (or density) of the analysed element in the sample. The existing concentration may be designated as either a percent (%) or as a weight percent (wt%), and may be defined according to the following formula: Wt% = (a/b) . 100 Wherein, "a" represents the intensity of the characteristic X-ray of the sample, and "b" represents the intensity of the characteristic X-ray of a standard element. The term "high density peak" is a standard term referring to the point at which the differential value of the density (measured as a function of distance) changes from positive to negative. Two such high density peaks are shown, for example, in figure 2 of the present application. The term "density pitch", which is also a standard term, refers to the distance between two adjacent high density peaks. That is, the term "density pitch" as used in the present application refers to the pitch "or distance" between adjacent peaks of high densities. The above hydrogen-absorbing alloy may be in a single phase crystal system. However, components of portions of the alloy are different. Accordingly, equilibrium-pressure difference from absorbing hydrogen between two portions of the alloy may be created. Further, portions having a low equilibrium-pressure can more easily absorb hydrogen. Therefore, cracks are easily created in the alloy, and the surface area of the hydrogen-absorbing alloys are increased. As a result, the reaction area is also increased. FIRST EMBODIMENT First Example In a first embodiment of the present invention, hydrogen-absorbing alloys are prepared and used to form batteries. FIG. 1 is a cross-sectional illustration of a battery according to a first embodiment of the present invention. In FIG. 1, the battery has a positive electrode 1 of a sintered type nickel hydroxide electrode, a negative electrode 2 of hydrogen-absorbing alloy and a separator 3. The separator 3 is impregnated with an alkaline electrolyte, and spirally wound to insulate the positive electrode 1 from the negative electrode 2. This forms an electrode body 4. The electrode body 4 is set in an outer case 6, which acts as a negative terminal for the battery. The outer case 6 and the negative electrode 2 are electrically connected together by a negative conductive lead 5. An opening in the outer case 6 is closed off by a cap 8 and a packing 7. Inside part of the cap 8, a coiled spring 9 is arranged. Once internal pressure in the battery increases, and the coiled spring is pressed in the direction "A". Thus, internal gas may be released into the atmosphere. The cap 8 and the positive electrode 1 are electrically connected together by a positive conductive lead 10. The above cylindrical type metal hydrogen battery may be produced in accordance with the process described below. To prepare the hydrogen-absorbing alloy, Mm (so-called Misch Metal), Nickel (Ni), Cobalt (Co), Aluminum (Al) and Manganese (Mn) are measured in an element ratio of 1:3.2:1:0.2:0.6. These elements are then melted in a high frequency melting furnace in an argon atmosphere (or other inert atmosphere) to form a melted mixture. Next, the melted mixture is slowly cooled at less than a 50 °C/min cooling speed to reach a nucleus formation temperature (ranging from about 1200 °C to about 1300 °C). Once the mixture temperature reaches less than the nucleus formation temperature, the mixture is quenched at a quenching speed ranging from 300 °C/min to 500 °C/min. This produces a hydrogen-absorbing alloy bulk with a composition represented by the formula MmNi 3.2 Co 1.0 Al 0.2 Mn 0.6 . The above produced alloy is called "a1". The hydrogen-absorbing alloy "a1" is then mechanically pulverized into granules with an average size of 50 µm. Next, the granules are kneaded with polyethyleneoxide (PEO), water-soluble binder, to obtain a paste. The paste is applied to a punched metal conductive substrate, on both sides, and then dried to produce a negative electrode 2. The negative electrode 2 and the positive electrode 1, with the separator 3 interposed between them, are wound to produce the electrode body 4. The electrode body 4 is then inserted into the outer case 6, and a 30 wt% KOH electrolyte solution is poured into the outer case 6. Then, the outer case 6 is closed off by the cap 8 and packing 7. This produces a battery called battery "A". Second Example A second example is similar to the above described first example, however the quenching speed is altered. The quenching speed is set higher than 500 °C/min. This produces a hydrogen-absorbing alloy bulk having the same elements as described in the first example. This alloy is called "a2". The hydrogen-absorbing alloy "a2" is used to produce a negative electrode, and then a battery "A2" using the negative electrode is prepared by the same method used in the above first example. Comparative example A comparative example is produced for comparison with the above first and second examples. To produce the comparative example, the cooling speed of both the slow-cooling and the quenching is altered. These cooling speeds are set at less than 300 °C/min. This also produces a hydrogen-absorbing alloy bulk having the same elements as described in the first example. This alloy is called "x". The hydrogen-absorbing alloy "x" is used to produce a negative electrode and then a battery "X" is prepared by the same method used in the above first example. Experiments Several experiments were performed on the above battery examples. The purpose was to determine the battery characteristics and to compare the battery example. Below is a description of the experiments performed. Experiment 1-1 In experiment 1-1, a relationship between a Manganese (Mn) density difference and a density pitch in the alloy was tested, and the results are shown in table 1. The density pitch is the distance between two adjacent high density peaks. In the experiment 1-1, a distance between portions of two adjacent segregated elements in the hydrogen-absorbing alloy is measured in a 2 µm 3 volume by linear analysis methods. FIG. 2 graphically illustrates the relationship between the density difference and the density pitch (distance). In FIG. 2 a horizontal line represents the density pitch (the distance between the two adjacent high density peaks) and a vertical line represents a density difference for one of the elements. Therefore, a height for one of the density peaks defines the density differences. As shown in table 1, the alloys "a1" and "a2" of the present invention have enlarged Manganese (Mn) density differences and exhibit density pitches, which are spread out. In the alloys "a1" and "a2", the density differences are not less than about 3.0 wt% and the density pitches are not less than about 20 µm, respectively. Alloy Density difference (wt%) Density pitch (µm) a1 3.0 20 a2 5.7 63 x 1.1 less than 15 Experiment 1-2 Experiment 1-2 test the discharge capacities of batteries "A1", "A2" and "X". The batteries used the corresponding alloys "a1", "a2" and "x" for the negative electrode and the experiment 1-2 results are shown in table 2. The discharge capacity of the battery was measured at a low temperature at -20 °C. To conduct the experiment, each battery is charged at room temperature at 1C rate to provide a full-charge. Next, the battery is cooled to -20 °C and the battery is discharged until a 0.8 V battery voltage is measured. In table 2, a discharge capacity at 20 °C (room temperature) is 100 %. Alloy Battery Discharge capacity (%) a1 A1 32 a2 A2 64 x X 5 As shown in table 2, the batteries "A1" and "A2" of the present invention have excellent capacities, compared to the battery "X" from the comparative example. Experiment 1-3 Experiment 1-3 tested a relationship between discharge temperature and discharge capacity for the batteries "A2" and "X". The batteries used the corresponding alloys "a2" and "x" for the negative electrode and the experimental results are shown in FIG. 3. The discharge capacity for each battery was measured by changing the discharge temperature. As shown in FIG. 3, a discharge capacity at 20 °C (room temperature) is 100%. FIG. 3 shows that reducing the discharge temperature has a lesser affect on the discharge capacity for the batteries "A1" and "A2" compared to the battery "X" from the comparative example. Experiment 1-4 Experiment 1-4 tested a relationship between charging time and internal pressure of the batteries "A2" and "X". The batteries used the corresponding alloys "a2" and "x" for the negative electrode and the experimental results are shown in FIG. 4. The charging current for this experiment was set at a 2 C rate. As shown in FIG. 4, the battery "A2" of the present invention has a significantly smaller internal pressure increase from rapid charging as compared to the battery "X". Experiment 1-5 Experiment 1-5 determined a relationship between density pitch and a discharge capacity for the batteries "A1", "A2" and "X". The batteries used the corresponding alloys "a1", "a2" and "x" for the negative electrodes and the experimental results are shown in FIG. 5. The battery discharge is performed at various temperatures which are changed from 0°C, to -10°C and to -20°C. Each discharge capacity is compared to a discharge capacity at 25°C which represents a 100% discharge capacity. FIG. 5 shows that the batteries "A1" and "A2" of the present invention are less susceptible to discharge capacity reduction from low temperature discharging as compared to the battery "X". Experiment 1-6 Experiment 1-6 tested a relationship between density pitch and internal pressure for the batteries "A1", "A2" and "X" and the experimental results are shown in FIG. 6. For this experiment, the batteries are charged at a 1C rate to 200% the normal charging capacity of the battery, and then the internal pressure for each battery is compared. FIG. 6 shows that the batteries "A1" and "A2" of the present invention have a significantly smaller internal pressure increase as compared to the battery "X". The results of above experiments, 1-1 to 1-6, show that a density pitch between two adjacent portions are preferably greater than about 20 µm. SECOND EMBODIMENT First example In a second embodiment of the present invention, the hydrogen-absorbing alloy is prepared with Mm (Misch metal), Nickel (Ni), Cobalt (Co), Aluminum (A1) and Manganese (Mn) being measured in an element ratio of 1:3.2:0.8:0.2:0.8. These elements are mixed and melted in accordance with the same method used in the first embodiment. This produces a hydrogen-absorbing alloy "b1" represented by the formula MmNi 3.2 Co 0.8 Al 0.2 Mn 0.8 . This alloy is used as a negative electrode and to produce a battery "B1". Second example A second example of the second embodiment is similar to the above described first example of the second embodiment, however, the quenching speed is altered. The quenching speed is set higher than 500 °C/min after the slow-cooling to the nucleus formation temperature. This produces a hydrogen-absorbing alloy bulk having a composition represented by the formula MmNi 3.2 Co 0.8 Al 0.2 Mn 0.8 , and which is called "b2". The hydrogen-absorbing alloy "b2" is used to produce a negative electrode and then battery "B2" using the same method used for the first example. Comparative example A comparative example is produced for comparison with the first and second examples. To produce the comparative example, both the slow-cooling speed and quenching speed are set to less than 300 °C/min. This produces a hydrogen-absorbing alloy bulk having the same elements as described in the first example. This alloy is called "y". The hydrogen-absorbing alloy "y" is used to produce a negative electrode and then a battery "Y" is prepared by the same method used in the first example. Experiments Several experiments were performed on the above battery examples. The purpose was to determine the battery characteristics and to compare the battery example. Below is a description of the experiments performed. Experiment 2-1 In experiment 2-1, a relationship between a Manganese (Mn) density difference and a density pitch was tested, and the results are shown in table 3. As shown in table 3, the alloys "b1" and "b2" of the present invention have enlarged Manganese (Mn) density differences and define density pitches which are spread out. In the alloys "b1" and "b2", the density differences are not less than about 3.2 wt% and the density pitches are not less than about 42 µm, respectively. Alloy Density difference (wt%) Density pitch (µm) b1 3.2 42 b2 6.0 88 y 1.3 less than 18 Experiment 2-2 Experiment 2-1 tested the discharge capacities of batteries "B1", "B2" and "Y". The batteries used the corresponding alloys "b1", "b2" and "y" for the negative electrode and the experimental results are shown in table 4. The discharge capacity of the batteries is measured at low temperature at -20 °C. Typical conditions for the measurements in this experiment are set to the same conditions as those used in experiment 1-2. Alloy Battery Discharge capacity (%) b1 B1 38 b2 B2 70 Y Y 3 As shown in the table 4, the batteries "B1" and "B2" of the present invention have excellent capacities, compared to the battery "Y" from the comparative example. The produced hydrogen-absorbing alloy has a non-stoichiometric composition ratio. Comparative example A comparative example using the alloy "x" is used to produce a battery "X", in accordance with the comparative example of the first embodiment. Experiments Several experiments were performed on the above battery examples. The purpose was to determine the battery characteristics and to compare the battery example. Below is a description of the experiments performed. Experiment 3-1 In experiment 3-1, a relationship between a Manganese (Mn) density difference and a density pitch was tested and typical results are shown in table 5. The conditions for the measurements in this experiment are the same as the conditions used in experiment 1-1. As shown in table 5, the alloy "c" of the present invention has an enlarged Manganese (Mn) density differences and defines a density pitch, which is spread out. In the alloy "c", the density difference is less than about 10 wt% and the density pitch is not less than about 97 µm, respectively. Alloy Density difference (wt%) Density pitch (µm) c 10 97 x 1.1 less than 15 Experiment 3-2 Experiment 3-2 tested the discharge capacities of the batteries "C" and "X". The batteries used the corresponding alloys "c" and "x" for the negative electrode and experimental results are shown in table 6. The discharge capacities of the battery are measured at a low temperature at -20 °C. Typical conditions for the measurements in this experiment are set to the same conditions as those used in experiment 1-2. Alloy Battery Discharge capacity (%) c C 75 x X 5 As shown in table 6, the battery "C" of the present invention has an excellent capacity, compared to the battery "X" of the comparative example. Experiment 3-3 Experiment 3-3 tested a relationship between discharge temperature and discharge capacities for the batteries "C" and "X". The batteries used the corresponding alloys "c" and "x" for the negative electrode and the experimental results are shown in FIG. 7. Typical conditions for experiment 3-3 are set to the same as those used in experiment 1-3. In FIG. 7 shows that reducing the discharge temperature has a lesser affect on the discharge capacity for the battery "C" compared to the battery "X". Experiment 3-4 Experiment 3-4 tested a relationship between changing time and internal pressure of the batteries "C" and "X". The batteries used the corresponding alloys "c" and "x" for the negative electrode and the experimental results are shown in FIG. 8. Typical conditions for experiment 3-4 are set to the same as those used in experiment 1-4. As shown in FIG. 8, the battery "C" of the present invention has a significantly smaller internal pressure increase from rapid charging as compared to the battery "X" of the comparative example. Experiment 3-5 Experiment 3-5 tested a relationship between density pitch and a discharge capacity of the batteries "C", "B1", "B2" and "X". The batteries used the corresponding alloys "c", b1", "b2" and "x" for the negative electrode and the experimental results are shown in FIG. 9. The batteries "B1" and "B2" are prepared in accordance with the above described second embodiment. The battery discharge is performed at various temperatures which are from changed from 0°C, to -10°C and to -20°C. Each discharge capacity is compared to a discharge capacity at 25°C which represents a 100% discharge capacity. FIG. 9 shows that the batteries "C", "B1" and "B2" of the present invention are less susceptible to discharge capacity reduction from such low temperature discharging as compared to the battery "X". Experiment 3-6 Experiment 3-6 tested a relationship between density pitch and internal pressure for the batteries "C", "B1", "B2" and "X". For this experiment, the batteries were charged at a 1C rate to 200% the normal charging capacity of the battery, and then the internal pressure for each battery was compared. The results showed that the batteries "C", "B1" and "B2" of the present invention have a significantly smaller increase in internal pressure as compared to the battery "X". The results of the above experiments, 3-1 to 3-6, show that the density pitch is more preferable more than about 40 µm. FOURTH EMBODIMENT First example In a fourth embodiment of the present invention, the hydrogen-absorbing alloy is prepared with Mm (Misch metal), Nickel (Ni), Cobalt (Co), Aluminum (Al), Manganese (Mn) and an additive of Boron (B) being measured in an element ratio of 1:3.1:0.9:0.2:0.6:0.1. These elements are then melted, and cooled using a cooling speed and a quenching speed less than 300 °C/min in accordance with the same method used by the first embodiment. This produces a hydrogen-absorbing alloy "d1" which is represented by the formula MmNi 3.1 Co 0.9 Al 0.2 Mn 0.6 B 0.1 . This alloy is used as a negative electrode and to produce a battery "D1". Second example In a second example of the fourth embodiment Tungsten (W) is used as an additive which replace the Boron in the first example. This produces a hydrogen-absorbing alloy bulk having a composition represented by the formula MmNi 3.1 Co 0.9 Al 0.2 Mn 0.6 W 0.1 and which is called "d2". The hydrogen-absorbing alloy "d2" is used to produce a negative electrode, and then battery "D2" using the same method used by the first example. Third example In a third example of the fourth embodiment, Molybdenum (Mo) is used as an additive which replaces the Boron in the first example. This produces a hydrogen-absorbing alloy bulk having a composition represented by the formula MmNi 3.1 Co 0.9 Al 0.2 Mn 0.6 Mo 0.1 and which is called "d3". Thy hydrogen-absorbing alloy "d3" is used to produce a negative electrode and then battery "D3" using the same method used by the first example. Comparative example A comparative example using the alloy "x" is used to produce a battery "X" in accordance with the comparative example of the first embodiment. Experiments Several experiments were performed on the above battery examples. The purpose was to determine the battery characteristics and to compare the battery example. Below is a description of the experiments performed. Experiment 4-1 In experiment 4-1, a relationship between a Manganese (Mn) or Cobalt (Co) density difference and a density pitch was tested, typical results are shown in table 7. The conditions for the measurements in this experiment are the same as the conditions used in experiment 1-1. As shown in table 7, the alloys "d1", "d2" and "d3" of the present invention have enlarged Manganese (Mn) or Cobalt (Co) density differences and define density pitches which are spread out. In the alloys "d1", "d2" and "d3", the density difference is not less than about 6.0 wt% and the density pitch is not less than about 50 µm, respectively. Alloy Density difference of Mn (wt%) Density difference of Co (wt%) Density pitch (µm) d1 - 6.0 50 d2 8.6 - 63 d3 7.1 - 64 x 1.1 - 15 Experiment 4-2 Experiment 4-2 determined the discharge capacities of batteries "D1", "D2", "D3" and "X". The batteries used the corresponding alloys "d1", "d2", "d3" and "x" for the negative electrode and the experimental results are shown in table 8. The discharge capacity of the battery is measured at a low temperature at -20 °C. Typical conditions for the measurements in this experiment are set to the same conditions as those used in experiment 1-2. Alloy Battery Discharge capacity (%) d1 D1 69 d2 D2 72 d3 D3 74 x X 5 As shown in table 8, the batteries "D1", D2" and "D3" of the present invention have excellent capacities compared to the battery "X" of the comparative example.

Claims: A hydrogen-absorbing alloy electrode comprising: a conductive substrate on which is provided a hydrogen-absorbing alloy in a single phase crystal system and composed of at least three elements; wherein one of said at least three elements has a density distribution profile as provided with measurement by EPMA which for a 2 µm 3 sample of the alloy has at least two adjacent high density peaks and a lowest density point between said at least two adjacent high density peaks, and wherein a density difference between one of said at least two adjacent high density peaks and said lowest density point is not less then 3.0 wt% and a distance between said two adjacent high density peaks is not less than 20 µm. A hydrogen-absorbing alloy electrode according to claim 1, wherein said alloy has the formula ANi a Co b Mn c X d , in which A is a Misch Metal or mixture of rare earth elements including Lanthanum in the range selected from 20% to 50%, the ranges of "a", "b", "c" and "d" are respectively defined by 2.5 ≦ a ≦ 3.5, 0 ≦ b ≦ 1.5, 0 ≦c ≦ 1 and 0 ≦ d ≦ 0.3, the value of a+b+c+d is 3.85 to 5, and X is one of the elements iron (Fe), Copper (Cu), Molybdenum (Mo), Tungsten (W), Boron (B), Aluminium (Al), Silicon (Si) and Tin (Sn). A hydrogen-absorbing alloy electrode according to claim 1 or claim 2, wherein said single phase crystal system is a hexagonal crystal system. A hydrogen-absorbing alloy for a negative electrode, the alloy having a single phase crystal system of the formula ANi a Co b Mn c X d , in which A is a Misch Metal or mixture of rare earth elements including Lanthanum in the range selected from 20% to 50%, the ranges of "a", "b", "c" and "d" are respectively defined by 2.5 ≦ a ≦ 3.5, 0 ≦ b ≦ 1.5, 0 ≦ c ≦ 1 and 0 ≦ d ≦ 0.3, the value of a+b+c+d is 3.85 to 5, and X is one of the elements iron (Fe), Copper (Cu), Molybdenum (Mo), Tungsten (W), Boron (B), Aluminium (Al), Silicon (Si) and Tin (Sn); wherein one of said at least three elements has a density distribution profile as provided with measurement by EPMA which for a 2 µm 3 sample of the alloy has at least two adjacent high density peaks and a lowest density point between said at least two adjacent high density peaks, and wherein a density difference between one of said at least two adjacent high density peaks and said lowest density point is not less then 3.0 wt% and a distance between said two adjacent high density peaks is not less than 20 µm. A hydrogen-absorbing alloy according to claim 4, wherein said single phase crystal system is a hexagonal crystal system. A method of manufacturing a hydrogen-absorbing alloy according to any preceding claim, wherein said hydrogen-absorbing alloy is produced by cooling a melted mixture of said hydrogen-absorbing alloy at a first cooling speed until a nucleus formation temperature is reached and then by quenching at a second cooling speed faster than said first cooling speed, wherein said nucleus formation temperature ranges from about 1200 °C to about 1300 °C, and said second cooling speed is greater than 300 °C/min. A method according to claim 6, wherein said second cooling speed is greater than 500°C/min. A method of manufacturing a hydrogen-absorbing alloy electrode, comprising manufacturing a hydrogen-absorbing alloy in accordance with claim 6 or claim 7, and placing said alloy on a conductive substrate.

Inventors: FURUKAWA NOBOHIRO, KIMOTO MAMORU, MASTUURA YOSHINORI, MIZITAKI HUSAGO, NISHIO KOJI, TIKANO YOSHITO, FURUKAWA, NOBOHIRO, KIMOTO, MAMORU, MASTUURA, YOSHINORI, MIZITAKI, HUSAGO, NISHIO, KOJI, TIKANO, YOSHITO, Furukawa, Nobohiro, c/o Sanyo Electric Co. Ltd., Kimoto, Mamoru, c/o Sanyo Electric Co. Ltd., Mastuura, Yoshinori, c/o Sanyo Electric Co. Ltd., Mizitaki, Husago, c/o Sanyo Electric Co. Ltd., NISHIO, KOJI, C/O SANYO ELECTRIC CO. LTD., Tikano, Yoshito, c/o Sanyo Electric Co. Ltd.
Applicants: SANYO ELECTRIC CO, SANYO ELECTRIC CO., LIMITED.
Application year: 1993
Main classification: H01M4
IPC codes: H01M4