Bloom-inhibiting fat blends

Abstract: Blends of triglyceride compositions A, and B and/or C, wherein A is a triglyceride composition of the (H 2 M + M 2 H)-type, H = saturated fatty acid ≥ C 16 , M = saturated fatty acid C 8 -C 14 , while preferably the B = triglyceride composition relatively high in (U 3 + U 2 S) triglycerides U = unsaturated fatty acid, S = saturated fatty acid and C = vegetable fat with an N 20 (not stab.) > 15, containing preferably high amounts of SUS triglycerides. are novel and display excellent anti-bloom behaviour at ambient temperatures.

Description: As set out in EP-A-0 530 864 (filed July 3, 1991), chocolate compositions containing the conventional ingredients, such as cocoa powder, cocoa butter, cocoa-butter equivalents, sugar and emulsifiers, need to be tempered because of the presence of polymorphic fats, such as POP, POSt and/or StOSt (P = palmitic acid; St = stearic acid and O = oleic acid). According to the above-mentioned patent application an improvement in bloom formation is obtained by adding a minimum amount of a hardstock fat to the chocolate composition. The hardstock fats used are of the (H 2 M + M2H)-type, wherein H = saturated fatty acid having at least 16 C-atoms and M = saturated fatty acid having C 8 -C 14 atoms, preferably C 12 -C 14 atoms. Very useful are hardstock fats obtainable by interesterification of mixtures of vegetable oils high in triglycerides with fatty acid residues having at least 16 C-atoms, and triglycerides rich in lauric and/or myristic acid residues, e.g. as disclosed in our Australian Patent Application 12346/85 (Serial Number 549,465). In EP 521 549 (published Jan 7 ,1993) encapsulated fillings are disclosed wherein either the filling or the coating for the filling contains H2M + M2H type fats as anti blooming agent. However no indication is given about the use of specific fractions of this H2M + M2H fat. According to EP 322 027 (published June 28, 1989) reduced calorie fats are made and applied in foods which fats comprise triglycerides selected from the group consisting of MML; MLM; LLM; and LML fats and mixtures thereof. However nothing is disclosed about anti blooming properties nor about the use of specific fractions of H2M + M2H fats. Although the results obtained according to the above-mentioned European Patent Application are, in general, very satisfactory, in particular upon storage above ambient temperature, we found that bloom formation still occurred upon storage at ambient temperature when these hardstock fats were applied at relatively high levels, i.e. above 1.5 wt.% on product, in particular in dark chocolate compositions. It has, however, been found that the prevention of bloom at high temperatures is most effective when more of the additive is applied. Therefore, we have conducted a study in order to find out how this problem could be overcome. As a result, we have found a new blend of triglycerides which upon application in in baked bakery products, provided with a chocolate layer or a chocolate-like layer, or in chocolate encapsulated filling led to an improvement of the anti-bloom behaviour of the chocolate compositions. So our invention concerns in the first instance novel triglyceride compositions, comprising triglycerides from the types A and B and C, wherein A is a triglyceride composition of the (H 2 M + M 2 H)-type, as defined above; B is a soft triglyceride composition, having a relatively high level of (U 3 + U 2 S) - triglycerides and C is a vegetable fat or a fraction thereof with an N 20 (not stab.) of more than 15. Depending on the typical use of the triglyceride compositions we can define different triglyceride compositions, each of which is specifically adapted for its typical use. The (H 2 M + M 2 H)-type composition A is preferably obtained from interesterification of vegetable oil high in triglycerides with fatty acid residues having at least 16 C-atoms (in particular hardened palm oil, such as PO-58) and triglycerides rich in lauric and/or myristic acid residues (in particular hardened palm kernel oil, such as PK-39). We found that problems related with the occurence of bloom formation in chocolate or chocolate-like coatings of baked bakery products could be overcome by the application of compositions according to the invention. In these cases we found, that an additional problem had to be solved: while the problems, related with the bloom formation could be overcome by the use of mixtures of A and B, we found that the application of these mixtures did not always provide the highly functional doughs that we aimed for. We found that in those cases higly functional doughs could be obtained by incorporation of a fat component C with a minimum N 20 -value (not stabilized) of 15. The application of such fat components C provided, that we could apply fractions of the fat component A, such as the olein fraction thereof. Baked bakery products, such as biscuits, cookies or cakes, are often provided with a chocolate layer (or a chocolate-like layer based on a cocoa butter equivalent). This layer can completely encapsulate the baked product or can be present as a coating, not completely encapsulating the baked product. As the chocolate or chocolate-like layer is based on polymorphic fats high in SUS-type triglycerides (S = sat. C 16 -C 18 ; U = mainly C 18:1 ), storage of the products often led to bloom formation on the chocolate(-like) layer. In our Australian Patent Application 19,379/92 we already disclosed fat compositions that could be applied to prevent bloom in the chocolate(-like) layers of encapsulated fillings. A possible filling is a biscuit or a cookie, while Example VI of this Australian Patent Application illustrates the preparation of a biscuit which is enrobed by a chocolate composition containing 75 wt.% of palm oil olein and 25 wt.% of a fat having about 70 wt.% of (H 2 M + M 2 H). We have now found new fat compositions that can display an effect similar to that disclosed in the above-mentioned Australian Patent Application, even if the baked product is not encapsulated in a chocolate(-like) layer but is provided with a coating of chocolate(-like) material that does not completely encapsulate the baked product. The (H 2 M + M 2 H) fat present in the fat phase of the dough from which the baked product is made migrates to the chocolate(-like) layer and acts there as an anti-bloom agent. It is, however, also possible to add the fat composition immediately to the chocolate composition from which the chocolate(-like) layer is made. Therefore, the invention concerns a fat composition suitable for the preparation of non-blooming chocolate-coated, baked bakery dough products comprising fats A, B and/or C, wherein: fat A = fat rich in (H 2 M + M 2 H) triglycerides, H = saturated fatty acid having ≥ C 16 , preferably C 16 -C 18 , M = saturated fatty acid having C 8 -C 14 , preferably C 12 -C 14 , fat B = fat containing at least 35 wt.% (U 3 + U 2 S), U = mono- or polyunsaturated fatty acid having ≥ C 18 , preferably all cis, S = saturated fatty acid having ≥ C 16 , preferably C 16 -C 22 , fat C = vegetable fat or a fraction thereof, displaying an N 20 (non-stab.) of more than 15, fat A being present in amounts of 5.5-60 wt.%, preferably 30-55 wt.%, fat B being present in amounts of 30-80 wt.%, fat C being present in amounts of 5-40 wt.%, Fat A suitably is the olein fraction of the fractionation of an interesterified mixture of vegetable oil high in triglycerides with fatty acid residues having at least 16 C atoms and vegetable triglycerides rich in lauric and/or myristic acid residues. The olein fraction of the interesterified mixture displays a weight ratio C 42 : C 36 (= triglyceride with 42, respectively, 36 C atoms) of less than 2.0. The perequisite for fat A is that its (H 2 M + M 2 H) content is 20-100 wt.%, preferably 40-85 wt.%. In the fats A rich in (H 2 M + M 2 H) triglycerides, the triglyceride distribution is such that (C 40 -C 46 ) : (C 30 -C 38 ) is between 0.8 and 15, preferably between 1 and 10. Fat B is a liquid oil suitably selected from the group consisting of sunflower oil, rapeseed oil, soybean oil, arachidic oil, palm oil olein, high oleic sunflower oil, high oleic rapeseed oil, with preferably a (U 2 S + U 3 ) content of more than 45 wt.%. Mixtures thereof can, of course, also be applied. Fat C is either a hardened vegetable fat, a fraction thereof or a fraction of an unhardened vegetable fat. Very suitable fats C are hardened vegetable fats or fractions thereof having a melting point of 25-55°C, such as hardened palm oil olein-37, hardened palm oil-44, hardened soybean-36, a mid-fraction of a hardened mixture of soybean oil and cottonseed oil. However, also fractions of unhardened vegetable oils, which fractions have a SUS content of more than 35 wt.%, preferably more than 60 wt.%, can be successfully applied. A preferred fat C is palm oil stearin. The N 20 value (non-stab., i.e. measured after the following T regime : melt at 80°C; keep at 60°C for 10 minutes, at 0°C for 1 hour and at 20°C for 30 minutes [= measurement temperatures]) of fat C is preferably more than 25, more preferably more than 40. The N line of the total fat composition (so consisting of the blend of fats A, B and/or C) is preferably (not stabilized): N 20 = 15-55, more preferably 20-45, and N 30 = 2-30, more preferably 4-15. Since margarines or spreads are applied in many dough preparations for baked bakery products, the invention is also concerned with water-in-oil emulsions containing 20-85 wt.% of fat and wherein the fat is a fat according to the invention. These emulsions can be made using well-known techniques (cf., e.g., fat-continuous microvotator processing or inversion processing). The baked bakery products, at least partly coated with a chocolate or chocolate-like material, wherein the fat phase of the dough from which the baked product was made at least partly consists of the fat composition according to the invention or of the water-in-oil emulsion according to the invention, are also part of the invention. In another embodiment of the invention we have found that problems, occurring on chocolate-encapsulated fillings can also be overcome by applying the compositions of our invention. In fact we found, that a problem similar to the problem for the dough fats had to be overcome. I.e. to come to a fat composition that displays a high quality performance when applied in fillings and which enables the application of several types of fats A. Chocolate-encapsulated fillings consisting of at least a filling and a chocolate or chocolate-like coating, wherein the filling comprises conventional filling ingredients, such as sugar, skimmed milk powder, salt or emulsifier and at least 25 wt.% of a filling fat, are well-known products. So far, however, these products have displayed a big disadvantage, in particular when the filling is liquid, i.e. fat present in the liquid filling migrates into the coating layer. Because of this migration, blooming of the chocolate occurs. In order to overcome this problem, a solution was sought in the use of an intermediate layer between the liquid filling and the coating. However, such an extra layer complicates the production process and often has a negative influence on the mouthfeel of the product. We have found that it is possible to avoid the necessity of such an extra layer, while the product properties are as good or even better by applying the fat compositions according to the invention. Application of these fat composition leads to a high-quality product performance and enables also the use of a specific type of fat A in our products. From US 2,979,401 stabilizing ingredients for solid chocolate materials or chocolate-coated products are known that are included in the chocolate in amounts of 0.5-5 wt.%. The stabilizing ingredients consist of triglycerides of lauric, myristic and palmitic acid, preferably in molar ratios of 2.0 : 1.2 : 2.0. Minor amounts of other fatty acids do not change the basic character of the ingredients. The ingredients are used to stabilize the colour of chocolate upon storage. Because of the very strict requirements set to the fatty acid components of the triglycerides that may be used, these products have never been applied commercially. From US 3,491,677 it is further known that bloom formation can be inhibited by utilization of fatty compositions that are mixtures of natural interesterified triglycerides comprising short-chain fatty acids and long-chain fatty acids while the iodine value (= I.V.) of the compounds is 30-55 and the melting point is low. As a consequence of the above-mentioned requirements, only a limited range of triglycerides could be applied while the low melting point may create problems as regards the properties of the chocolate composition. From EP 390,408 triglyceride compositions are known that contain high levels (at least 85%) of combined MLM and MML (M = saturated fatty acid C 8 -C 10 ; L = saturated fatty acid C 20 -C 24 ) and low levels (i.e. at most 10 wt.%) of triglycerides LLM and LML (combined). These fats should always contain C 8 and C 10 fatty acid residues (35-60 wt.%) in a ratio of 1:4 to 4:1, while also 35-60 wt.% of behenic acid should be present. Minor amounts of C 12 -C 18 fatty acids can be present in the fats. The fat phase comprising the above-mentioned triglycerides should contain less than 20 wt.% of cocoa butter (i.e. less than 15 wt.% of SUS; S = saturated C 16 /C 18 ; U = oleic) . The triglycerides are applied in order to reduce the caloric value of compositions normally containing cocoa butter by replacing cocoa butter by these mixed triglycerides. We have now found that the problems associated with the application of the prior art products can be solved by using a specific filling fat for use in the fully or partially encapsulated filling. Therefore, the invention concerns a fat composition suitable for the preparation of non-blooming chocolate-coated, confection products, comprising fats A and C and optionally B, wherein : fat A = an (H 2 M+ M 2 H)- olein with C 42 : C 36 < 2, 0, H = saturated fatty acid having ≥ C 16 , preferably C 16 -C 18 , M = saturated fatty acid having C 8 -C 14 , preferably C 12 -C 14 , fat B = fat containing at least 35 wt.% (U 3 + U 2 S), U = mono- or polyunsaturated fatty acid having ≥ C 18 , preferably all cis, S = saturated fatty acid having C 16 -C 22 , fat C = vegetable fat or a fraction thereof, displaying an N 20 (non-stab.) of more than 15, fat A being present in amounts of 5.5-60 wt.%, preferably 30-55 wt.%, fat B being present in amounts of 30-80 wt.%, fat C being present in amounts of 20-60 wt.%, Fats A, B and C that can be applied are the same fats as described for the application for the preparation of the baked bakery product. The N line of the total fat composition (so consisting of the blend of fats A, B and/or C) is preferably (not stabilized) : N 20 = 10-75 more preferably 20-45, and N 30 = 0-20, more preferably < 18. Although the fat compositions preferably are applied as part of the filling of an encapsulated filling, it is also possible that the fat compositions are applied as part of the fat phase of the encapsulation. EXAMPLE 1 1.1 Biscuits were made according to the following recipe : Zeeuws flour 100% Castor sugar 25% Shortening samples 30% Skimmed milk powder 5% Salt 1% Baking powder 1% Water 22% 1.2 Shortenings were made in a microvotator, using the following fat blends : Fat blend Fat A (M 2 H + MH 2 ) Palm oil olein (= fat B) Hardened palm oil olein (= C) Bl-1 - 70 30 Bl-2 10 70 20 Bl-3 20 70 10 Bl-4 25 70 5 Bl-5 30 70 - In each case, fat A was a stearin fraction of an interesterified mixture of hardened palm oil and hardened palmkernel oil. It displayed a C 42 :C 36 weight ratio of 8.5 and contained 75 wt.% of (H 2 M + M 2 H). The (C 40 -C 46 ) : (C 30 -C 38 ) was 10. The palm oil olein (fat B) contained 75 wt.% of (U 2 S + U 3 ). The hardened palm oil olein had an N 20 = 73 (non-stab.) and an (H 2 M + M 2 H) level of far less than 5%. 1.3 Preparation of the dough and biscuits. The doughs were prepared according to the recipe described above. 500 g dough portions were made, using the procedure: 1. The sugar, margarine, milk powder and salt were fed into a horizontal z-blade high-speed mixer and mixed for 3 minutes. 2. The flour was added and mixed for a further 3 minutes. 3. The baking powder was dissolved in the water and then added to the above-mentioned mixture. The resulting product was stirred for 7 minutes. 4. The dough was then left to stand for 10 minutes, rolled out until 2 mm thick and then pricked. 5. The biscuits were cut from the dough and placed on a perforated plate. The biscuits were baked for 12 minutes at 200°C. 1.4 Preparation of chocolate The dark chocolate (Callebaut) + 2% of cocoa butter (calculated on the product) were melted and tempered in a Kreuter tempering machine. 1.5 Enrobing of the biscuits The biscuits were enrobed at 35°C and cooled in a cooling tunnel, using compartment temperatures of 16°C, 16°C, 16°C; the residence time was 10 minutes. 1.6. Storage conditions After one night on the table, the enrobed biscuits were stored at 13°C, 20°C, 25°C and 30°C. The bloom and gloss of the chocolate coating were evaluated. 1.7 Results Results of Bloom and Gloss Measurements Gloss measurements after 1 week. Dough fat 13°C 20°C 25°C 30°C BL-1 5 5 2 2 BL-2 5 5 3 3 BL-3 5 5 5 4/5 BL-4 5 5 5 4/5 BL-5 5 5 5 4/5 Scale 5 - very good 4 - good 3 - acceptable 2 - poor 1 - very poor Fat bloom measurements after 2 weeks Dough fat 13°C 20°C 25°C 30°C BL-1 5 4/5 2 3 BL-2 5 5 4 4 BL-3 5 5 5 4 BL-4 5 5 5 5 BL-5 5 5 5 5 Scale 5 - no bloom 4 - very slight fat bloom (under microscope) 3 - beginning of fat bloom 2 - serious fat bloom 1 - uniform layer of white fat over the chocolate EXAMPLE 2 2.1 Example 1 was repeated; however, the shortenings were made of the following fat blends : Fat blend Fat A' (M 2 H + MH 2 ) Palm oil olein (= fat B) Hardened palm oil olein (= C) B1-6 - 70 30 B1-7 30 70 - B1-8 60 40 - B1-9 50 20 30 In Bl-7, fat A' was an interesterified mixture of hardened palmkernel and hardened palm oil (weight ratio 70:30). It displayed a C 42 /C 36 ratio = 2.5. In blends 8 and 9, fat A' was the olein fraction of the wet fractionation of the above-mentioned fat A' of blend 7. This olein fraction displayed a C 42 /C 36 ratio = 1.5. Fats B and C are identical with B and C of Example 1. 2.2 Results Gloss measurements after 1 week: Gloss after 3 months: 13°C 20°C 25°C 13°C 20°C 25°C BL-6 4 3/4 1/2 4 1 1 BL-7 4 4 4/5 4 3 4 BL-8 4 3/4 4 4 3 4 BL-9 4/5 5 4 4 3 4 Fat bloom measurements after 1 week 13°C 20°C 25°C BL-6 5 5 3 BL-7 5 5 5 BL-8 5 5 5 BL-9 5 5 5 Fat bloom measurements after 3 months 13°C 20°C 25°C BL-6 5 1 1 BL-7 5 5 4 BL-8 5 4 5 BL-9 5 4 4 Scale : 5 = very good 1 = very poor 2.3 In a comparative example the fat phase consisted of a 60:40 mixture of palm oil olein and hardened palm oil. The results were comparable with these of BL-6. 2.4 It was further found that the dough properties in terms of homogenity and elasticity were improved when fat component C was present (so: blend 9), compared with blends, wherein C was absent (blends 7 and 8).

Claims: Fat composition suitable for the preparation of non-blooming chocolate-coated, baked bakery dough products comprising fats A, B and C, wherein: fat A = an (H 2 M + M 2 H)- olein with C 42 : C 36 < 2.0, H = saturated fatty acid having ≥ C 16 , M = saturated fatty acid having C 8 -C 14 ; fat B = fat containing at least 35 wt.% (U 3 + U 2 S) , U = mono- or polyunsaturated fatty acid having ≥ C 18 , S = saturated fatty acid having C 16 - C 22 , fat C = vegetable fat or a fraction thereof, displaying an N 20 (non-stab.) of more than 15, fat A being present in amounts of 5.5-60 wt.% fat B being present in amounts of 30-80 wt.% fat C being present in amounts of 5-40 wt.% Fat composition according to Claim 1, wherein B is an olein fraction from the fractionation of palm oil. Water-in-oil emulsions containing 20-85 wt.% of fat, wherein the fat is a fat composition according to Claim 1 Baked bakery products, at least partly coated with a chocolate or chocolate-like material, wherein the fat phase of the dough from which the baked product is made at least partly consists of the fat composition according to Claim 1 or of the water-in-oil emulsion according to claim 3.

Inventors: CAIN FREDERICK WILLIAM, HARGREAVES NEIL GRAHAM, HUGHES ADRIAN DAVID, CAIN, FREDERICK WILLIAM, HARGREAVES, NEIL GRAHAM, HUGHES, ADRIAN DAVID
Applicants: UNILEVER NV, UNILEVER PLC, UNILEVER N.V.
Application year: 1993
Main classification: A23D9
IPC codes: A23G1, A21D2, A21D13, A23D7, A23D9, C11B3, A23G3, C11C3