UV LIGHT STABILIZING, ANTIOXIDANT AND COLORANT COMPOUNDS

Abstract: Monomeric benzotriazole, benzophenone, 3,3-diphenyl-2-cyanoacrylate, 2,2,6,6-tetramethylpiperidine, hindered phenol, and diazo derivatives of 4'-hydroxyacetophenone, 4-hydroxystyrene, 1,1,1-tris(4'-hydroxyphenyl)ethane, 1,3,5-tris(4'-hydroxyphenyl)benzene, and the like are disclosed. When included in polymer formulations as monomeric species or as monomers covalently incorporated into an oligomeric or polymeric structure, or as additives, such derivatives impart color or resistance to free radical, oxidative, or ultraviolet (UV) light-induced degradation.

Description: UV LIGHT STABILIZING, ANTIOXIDANT AND COLORANT COMPOUNDS FIELD OF THE INVENTION The present application relates to novel compositions that are useful as ultraviolet stabilizers, antioxidants and colorants. The compositions are derivatives of 4'- hydroxyacetophenone (4-HAP) , 4-hydroxystyrene (4-HS) , l,l,l-tris(4'-hydroxyphenyl)ethane (THPE) and 1,3,5- tris (4'-hydroxyphenyl)benzene (THPB) . They can be used as additives to the materials to be protected, or optionally be chemically incorporated into polymer backbones.. BACKGROUND OF THE INVENTION Additives to impart ultraviolet stabilizing property or antioxidant property to polymers or to perform as colorants are known. For example, the Uvinul ™ materials (from BASF Corporation, Chemicals Division, Parsippany, New Jersey) and the Tinuvin ™ additives (from Ciba-Geigy Corporation, Additives Department, Hawthorne, New York) are ultraviolet stabilizers that are commercially available for use with polymers. Such additives generally are low molecular weight species, and have several problems including poor compatibility with the polymer formulation, poor dispersion into the polymer formulation, migration within the polymer, losses due to volatility of the additive material during processing or use, and leaching into liquids (e.g., washing of fabrics). Thus, there is a need for better materials which can function as ultraviolet stabilizing agents, antioxidants and colorants that may not have the above problems. The materials must be useful as compatible additives to polymers. They may also have functionalities which allow them to be incorporated into the backbone of polymers. When incorporated into the backbone, the protecting moieties may stay as an integral, compatible part of the product at desired concentrations. Accordingly, it is an object of this invention to provide molecules that carry moieties that possess ultraviolet stabilizing, antioxidant and colorant properties, and that can be used as additives to materials that need to be imparted such properties. It is another object of this invention to provide moieties that possess ultraviolet stabilizing, antioxidant and colorant properties, as well as reactive functionalities so they may be polymerized into homopolymers, or copolymerized with suitable comonomers to make copolymers, or simply be covalently incorporated into the backbone of polymers. These and other objects of the present invention will become apparent to the skilled artisan upon a review of the following description, and claims. SUMMARY OF THE INVENTION The present invention discloses a functionalized aromatic monomeric unit useful as an ultraviolet stabilizer, antioxidant or colorant in a polymeric system, said monomer being derived from 4-hydroxyacetophenone, and including a structural unit selected from the group consisting of: wherein each R is independently selected from the group consisting of hydrogen, alkyl, aroyl, alkanoyl, and a structural unit selected from the group consisting of 3,3,- diaryl-2-cyanoacryloyl and 2,2, 6,6-tetraalkylpiperidinyl, Ri indicates independently a moiety selected from the group consisting of benzotriazole, benzophenone, branched alkyl, aroyl, diazoarene, and 2,2,6,6-tetraalkylpiperidine, and n is an integer from 1 to 5. The present invention also discloses polymers derived from the above-described functionalized aromatic monomeric units. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention includes compositions of matter that are colorants or that carry ultraviolet stabilizing property and/or antioxidant property. In one embodiment, the compositions are based on 4-hydroxyacetophenone moiety (4-HAP) (Formula 1) , wherein R refers to one or more functionalities selected independently from the group consisting of benzotriazoles, 3, 3-diphenyl-2- cyanoacrylates, 2,2,6,6-tetramethylpiperidine hindered amine stabilizer (HALS), hindered phenols, suitable benzophenones and diazobenzenes. The above-described functionalities offer colorant properties, ultraviolet stabilizing or antioxidant properties to the underlying structural unit. For example, benzotriazoles (BZT) , 2- hydroxybenzophenones, HALS and 3,3-diphenyl-2- Formula 1 Formula 3 cyanoacrylates offer ultraviolet- stabilizing property; the hindered phenols offer antioxidant property, and the diazoarene linkage offers colorant property. If more than one of the above-described moieties are present in the same compound, the benefits could be synergistic. The invention also includes other novel compositions derived from 4-HAP. Such compositions have the 4- hydroxystyrene (4-HS) structural unit (Formula 2), the 1,1,1-tris (4'-hydroxyphenyl)ethane (THPE) unit (Formula 3), and the 1,3,5-tris (4'-hydroxyphenyl)benzene (THPB) unit (Formula 4) , such units being substituted with the R- functionalities described above for 4-HAP, for similar applications. Structural units represented by Formulas 1-4 may additionally contain other substituents so long as they do not interfere with the utility of the compositions for intended applications. The present invention also includes processes for preparing such novel compositions. Several of the compositions described by Formulas 1-4 may be advantageously prepared from suitable 4-substituted acetophenones such as, for example, 4-HAP. As an illustration, synthesis of THPE-BZT (Formula 3, where R is a benzotriazole moiety) from 4-HAP is schematically represented in Scheme 1 and further specifically described in the EXAMPLES section in Examples 1-4. THPEΕZT 2fijifiπi--i Some of the inventive compositions of Formulas 1-4 may contain other functionalities such as, for example, hydroxyl groups, that enable them to be covalently linked to polymer backbones. A diphenolic substituted material may also be useful as a monomer; it may be homopolymerized, or copolymerized with suitable comonomers, to provide polymers containing colorant, ultraviolet stabilizing, and antioxidant moieties in their repeat units. Some suitable polymers that the functionalities of the. invention can be linked to are derived from vinyl monomers such as styrenes, olefins, acrylates and the like. Suitable monomers include styrene, 4-methylstyrene, 4-chlorostyrene, 4-acetoxystyrene, 2-acetoxystyrene, 4-hydroxystyrene, 2- hydroxystyrene, 3,5-dibromo-4-hydroxystyrene, 3-bromo-4- hydroxy-5-methylstyrene, 3,5-dimethyl-4-hydroxystyrene, 3 , 5-dibromo-4-acetoxystyrene, 3-bromo-4-acetoxy-5- methylstyrene, 3,5-dimethyl-4-acetoxystyrene, ethylene, propylene, butadiene, isoprene, chloroprene, maleic anhydride, dimethyl maleate, diethyl maleate, maleic acid, acrylic acid, methyl acrylate, ethyl acrylate, methacrylic acid, methyl methacrylate, ethyl methacrylate, acrylonitrile, acrylamide, vinyl acetate, vinyl chloride, vinyl fluoride, 1,1-fluoroethylene, tetrafluoroethylene, and the like. Copolymers of one or more of the inventive styrene derivatives with one or more of the aforementioned vinyl monomers may be produced by substitution of the inventive styrene derivative for a portion of the known vinyl monomer or monomers in known methods for production of homopolymers or copolymers of the vinyl monomer or monomers, e.g., by free radical polymerization. Suitable difunctional derivatives of the invention may be homopolymerized or copolymerized ■ via condensation polymerization also. By employing condensation polymerization, polymers such as polysulfones, polyesters, polycarbonates, polyurethanes, polyethers, and the like may be produced. Suitable comonomers for condensation polymerization include 1,4-dihydroxybenzene, 1,3- dihydroxybenzene, 2, 6-dihydroxynaphthalene, 1,5- dihydroxynaphthalene, 4,4'-dihydroxybiphenyl, 2,2-di(4'- hydroxyphenyl)propane (bisphenol A), 2,2-di(4'- hydroxyphenyl) -1, 1, 1, 3 , 3 , 3-hexafluoropropane (hexafluorobisphenol A), 1,1-di (4'-hydroxyphenyl)ethane, di(4'-hydroxyphenyl)methane, and the like. Other comonomers such as, for example, ethylene glycol, 1,2-propylene glycol, 1,3-propanediol, neopentylglycol, 1,4-butanediol, and the like, may also be used. Suitable carboxyl comonomers for condensation polymerization include phosgene, dimethyl carbonate, diethyl carbonate, thionyl chloride, sulfuryl chloride, dimethyl sulfate, diethyl sulfate, terephthalic acid, terephthaloyl dichloride, dimethyl terephthalate, diethyl terephthalate, isophthalic acid, isophthaloyl dichloride, dimethyl isophthalate, diethyl isophthalate, 4,4'- biphenyldicarboxylic acid, 4,4'-biphenyldicarboxylic acid dichloride, dimethyl 4 , 4 ' -bipheny1dicarboxy1ate , diethyl 4,4 '- biphenyldicarboxylate, 1,3-benzenedisulfonyl dichloride, dimethyl 1, 3-benzenedisulfonate, diethyl 1,3-' benzenedisulfonate, 4,4'-biphenyldisulfonyl dichloride, dimethyl 4,4'-biphenyldisulfonate, diethyl 4,4'- biphenyldisulfonate, 6,2-naphthalenedicarboxylic acid, 6,2- naphthalenedicarboxylic acid dichloride, dimethyl 6,2- naphthalenedicarboxylate, diethyl 6 , 2- naphthalenedicarboxylate, 1, 5-naphthalenedicarboxylicacid, 1,5-naphthalenedicarboxylic acid dichloride, dimethyl 1,5- naphthalenedicarboxylate, diethyl 1 / 5- naphthalenedicarboxylate, 1, 5-naphthalenedisulfonic acid dichloride, dimethyl 1,5-naphthalenedisulfonate, diethyl 1,5-naphthalenedisulfonate, 2, 6-naphthalenedisulfonic.acid dichloride, dimethyl 2, 6-naphthalenedisulfonate, diethyl 2,6-naphthalenedisulfonate, oxalic acid, oxalyl dichloride, dimethyl oxalate, diethyl oxalate, malonic acid, malonyl dichloride, dimethyl malonate, diethyl malonate, succinic acid, succinic anhydride, succinyl dichloride, dimethyl succinate, diethyl succinate, maleic acid, maleic anhydride, dimethyl maleate, diethyl maleate, and the like. The following Examples describe suitable processes to synthesize some representative compositions of the present invention. Thus, for example, while some of the Examples may illustrate the synthesis of 4-HAP derivatives, it is to be understood that where appropriate, similar derivatives with Formulas 2-4 as the underlying unit may also be prepared by following similar procedures. The Examples are provided in order to further illustrate the present invention; however, the invention is in no way limited thereby. EXAMPLES Example 1. Preparation of 2-nitrobeiizeneaia-.on.iuir. chloride from 2-nitroaniline; An aqueous solution of 2- nitrobenzenediazonium chloride was prepared from 2- nitroaniline under a nitrogen atmosphere as follows. A mixture of 2-nitroaniline, concentrated aqueous HCl (2.125 moles per mole of the aniline) , and water (0.219 ml per ml of cone. aq. HCl) was stirred overnight at room temperature to produce a finely dispersed emulsion. After addition of ice (5.714 g per ml of cone. aq. HCl) and water (2.857 ml per ml of cone. aq. HCl), the resulting emulsion was stirred at 5°C while a solution of NaN0 2 (1.098 moles per mole of the aniline) in water (1.429 ml per ml of cone. aq. HCl) was added slowly over 30 minutes. Stirring of the reaction mixture was continued at 5°C for 30 minutes. Excess nitrite was then destroyed by adding small quantities of sulfamic acid. The resulting golden yellow solution was filtered cold. The filtrate contained 2- nitrobenzenediazonium chloride, and was stored at 0-5°C until used. Example 2. Preparation of 3- (2'-nitrophenylazo)-4- hvdroxyacetophenone (4-HAP containing a diazoarene unit) : An aqueous solution containing 2.5 wt% sodium hydroxide and 4.7 wt% sodium carbonate was prepared. 4- Hydroxyacetophenone (4-HAP) was added to this aqueous solution containing the quantity of sodium hydroxide that was stoichiometrically equivalent to desired incorporation of phenylazo functionality. The resulting mixture was stirred at room temperature under nitrogen until as much of the acetophenone as possible is dissolved as a phenoxide salt. To the resulting aqueous mixture of phenoxide salt stirred at 5-15°C under nitrogen was added over one hour the stoichiometric requirement of 2-nitrobenzenediazonium chloride from Example 1 above as the aqueous solution prepared. The aqueous solution of the benzenediazonium chloride was maintained at 5°C during the addition. After the addition was complete, the reaction mixture was stirred at 5-15°C under nitrogen for an additional 2.0 hours. The product of this diazo coupling, 3- (2 '-nitrophenylazo)-4- hydroxyacetophenone, precipitated from the reaction mixture and was recovered by filtration and washed with 0-5°C water. The crude solid was purified by recrystallization from boiling methylene chloride solution with addition of diethyl ether. The above Example 2 utilizes basic reaction conditions to effect the desired coupling. Such coupling may also be done under acidic or neutral conditions as is known to those skilled in the art. Example 3. Reductive Cvclization of the nitrophenylazo compound of Example 2 to 3-fbenzotriazol-2'-yl)-4- hvdroxyacetophenone (4-HAP-BZT) . A methanol solution of 5.50% by weight sodium hydroxide was prepared. 3-(2- nitrophenylazo)-4-hydroxyacetophenone from Example 2 above was added to the amount of this methanol solution containing a molar quantity of sodium hydroxide equal to 14.9 times the moles of 2-nitrophenylazo groups in the acetophenone. A solution of water (52.7 wt %) , methanol (41.7 wt %) , sodium dithionite (Na 2 S 2 0 4 , 4.26 wt %) , and sodium hydroxide (1.28 wt %) was prepared. To the mixture- of the nitrophenylazo compound kept stirring at 75°C under nitrogen was added over 15 minutes the amount of the aqueous methanol solution containing a molar quantity of sodium dithionite equal to 2.00 times the moles of 2- nitrophenylazo groups in the starting acetophenone. The reaction mixture was then stirred at 75°C under nitrogen for five hours prior to filtration. The filtrate was diluted with a volume of water equal to the volume of methanol in the sodium hydroxide solution to which the starting acetophenone was added. On acidification with aqueous HCl to pH 5, the filtrate precipitated solid product, 4-HAP-BZT. This solid was recovered by filtration and washed with 0-5°C water. The crude solid was purified by recrystallization from diethyl ether. The reductive cyclization of Example 3 utilizes sodium dithionite as the reducing agent. Suitable other reducing agents may be used in place of the dithionite. Alternately, catalytic hydrogenation may be employed for the same purpose. Example 4. Condensation of 4-HAP-BZT with phenol to prepare THPE-BZT; A mixture of phenol (7.38 moles), 4-HAP- BZT from Example 3 above (1.00 moles), 3-mercaptopropionic acid (0.95 moles), and methanesulfonic acid (1.01 moles) was stirred under nitrogen at 48°C for 24 hours. The crude reaction mixture was then diluted with 2.77 times, its weight of methanol, and sodium bicarbonate (6.31 moles) was added. The resulting mixture was filtered, and the filtrate was diluted with about 0.75 times its weight of water. The diluted filtrate was refrigerated overnight at 5°C to precipitate solid THPE-BZT, which was then recovered by filtration. The crude product was purified by recrystallization from aqueous methanol. Purification can also be achieved by recrystallization from other solvents or by HPLC. The yield was 59.5% based on 3 '- (benzotriazol- 2"-yl)-4 , -hydroxyacetophenone (4-HAP-BZT) . Example 5. Rinσ Benzoylation of 4-HAP to prepare benzophenones; Anhydrous A1C1, (10.25 mmoles) is weighed and transferred under nitrogen to a flask fitted with a mechanical stirrer, a nitrogen inlet, and an exit bubbler.. To the AICI 3 is added 30.5 mmoles of 1,2-dichloroethane and 3.85 mmoles moles of benzotrichloride. The resulting mixture is stirred on an ice bath at 0°C for 10 minutes before addition of 4-HAP (3.32 mmoles), in portions, at 0°C with immediate evolution of HCl fumes. The reaction mixture is stirred at 0°C for an additional 15 minutes before being poured over about 4.0 times its weight of ice-water. The resulting aqueous mixture is stirred and heated at 70°C for 30 minutes and then extracted with 1,2-dichloroethane. Vacuum rotary evaporation of the 1,2-dichloroethane extract provides crude 3 '-benzoyl-4'-hydroxyacetophenone, which can be purified by distillation, recrystallization, or HPLC (60.1% yield) . Example 5 describes monobenzoylation of the ring of 4- HAP. The reaction may be modified suitably to substitute the ring with more than one benzoyl group also. Alternately, ring benzoylation reaction described by M. Newman et al. J. Orσ. Chem.. Vol. 19, 992 (1954) may also be used. An alternative method of making the benzophenones would be to first make the benzoate of 4-HAP from 4-HAP and then subject it to Fries rearrangement, as exemplified in Examples 6 and 7. Example 6. Preparation of the benzoate of 4-HAP; An aqueous solution containing about 6.0% by weight of potassium hydroxide is prepared. 4-HAP is added, under nitrogen, so that the base is in about 15% molar excess based on the phenolic functionality. The reaction is stirred at 23°C until 4-HAP is completely dissolved. Benzoyl chloride (in 58% stoichiometric excess) is charged, dropwise, over about 20 minutes at 5°C. The reaction is stirred for at least one hour at 5°C. The benzoate that is formed is filtered, washed with water and may be reerystallized from acetone or other suitable solvent. In a similar manner, 1 , 1 , 1-tris (4 ' - hydroxyphenyl) ethane was converted to its tribenzoate derivative, 1,1,1-tris(4'benzoyloxyphenyl)ethane in an yield of 55.7% (based on 1, 1, 1-tri ' s (4 ' - hydroxyphenyl)ethane) after recrystallization from acetone. Other types of esters such as the acetate ester may also prepared by similar processes. Example 7♦ Fries rearrangement of benzoate esters to benzophenones; The benzoate ester (for example, the benzoate ester from Example 6 above) is added to a stirred autoclave. The reactor is evacuated and then chilled to about -30°C. Anhydrous HF (about 12 times the weight of the benzoate) is now added via suction to about half-fill the reactor. The contents of the vessel are- heated at about 55°C for about 5 hours. The reactor contents are vented (via a dip tube) onto about 8 times their weight of wet ice and neutralized with potassium hydroxide to a pH of about 6.5. The crude solid benzophenone product is filtered on a Buchner funnel and may be reerystallized from acetone, chloroform or other suitable solvent. Thus; from the benzoate of 4-HAP, 3 '-benzoyl-4'-hydroxyacetophenone may be obtained. Example 8. Preparation g_f 2-1-butvl-4-hvdroxv- acetophenone from 4-HAP (rinσ allviation) ; Isobutylene (1 mole) is added to a mixture of 4-HAP (1 mole) and sulfuric acid (4 m) stirred at 0°C in an autoclave. The resulting mixture is stirred and heated to 65°C for 45 minutes, cooled to about 25°C, and then added slowly to twice its weight of water maintained at 5-25°C with cooling. The resulting aqueous mixture is stirred and neutralized to pH 8 by addition 25 weight % NaOH solution, and is then extracted with diethyl ether. The ether extracts re evaporated to leave a residue, from which the t-butyl product may be isolated by recrystallization, distillation, or HPLC. Instead of employing an olefin and sulfuric acid in the above reaction, the t-butyl derivative may also be prepared from 4-HAP by using t-butyl chloride and A1C1 3 . Example 9. Preparation of 3.3-diphenyl-2-cvanoacrylate derivative of 4-HAP; 1 mole of ethyl 2-cyano-3,3- diphenylacrylate and 1 mole of 4-HAP are dissolved in approximately 1 liter of sulfolane. A catalytic quantity of toluenesulfonic acid (0.05 moles) is added, and the mixture heated to 80°C, with removal of product ethanol via distillation. When ethanol evolution has ceased, the reaction mixture is cooled, mixed with 3 liters of water, and neutralized with sodium bicarbonate. The precipitated 3,3-diphenyl-2-cyanoacrylate derivative of 4-HAP is isolated by filtration, and may be purified by crystallization or chromatography. Example 10. Preparation of 2.2.6.6-tetramethyl- pjperldlne derivative of 4-HAP; A mixture of 4-hydroxy- 2,2, 6, 6-tetramethylpiperidine (1.0 mole) and succinic anhydride (1.0 mole) is stirred and heated to 100°C for one hour to form the corresponding monoester of succinic acid. Slow addition of thionyl chloride to this monoester followed by heating to 65°C for one hour converts the carboxylic acid function to an acid chloride function. Reaction of the resulting monoester acid chloride with 4- HAP (1.0 mole) produces the 2,2, 6, 6-tetramethylpiperidine derivative of 4-HAP, which may be isolated and purified by HPLC. The above 2,2, 6, 6-tetramethylpiperidine derivative, which belongs to the class of hindered amine light stabilizers (HALS) , may also be prepared by other methods, e.g. by using catalyst such as, for example, A1C1 3 and HCl. Example 11. Preparation of the etal derivative of 4- HAP; 4-HAP is first converted to its methyl ether, 4- methoxyacetophenone. 4-Methoxyacetophenone (0.9 moles) trimethylorthoformate (2.4 moles), methanol (300 ml) and p- ' toluenesulfonic acid (0.009 moles) are stirred at reflux (57°C) for 1 hour. The reaction mixture is changed from clear liquid to a dark brown color. Unreacted trimethylorthoformate and methanol are removed under reducedpressure on a rotary evaporator. The crude dimethyl ketal derivative is purified via distillation under reduced pressure to afford a clear colorless liquid (yield: 0.8 moles). In a similar manner, other ketals such as the one- with ethylene glycol may also be prepared. Ketal groups have the advantage that they may be easily hydrolyzed, if so desired to the starting acetophenone, for example with a mixture of methanol, water and an acid, as is known to those skilled in the art. Example 12. Preparation of THPB bv condensation trimerlzatlon of 4-HAP; A 250 ml round bottom flask equipped with a magnetic stirrer, a Dean-Stark trap and a condenser is charged with 4-HAP (0.05 m) , aniline (0.2 moles) , and toluene (100 ml) . The reaction mixture is heated at reflux under nitrogen atmosphere for 17- hours. Aniline hydrochloride (0.0038 moles) is then added, and toluene is removed via distillation. After being heated at 190-200°C for 3 hours, the reaction mixture is cooled to 120°C. Toluene (100 ml) is added to the cooled reaction mixture to separate an oil. After the supernate liquid is decanted, hexanes (100 ml) are added to the oily residue to precipitate 1,3,5-tris (4'-hydroxyphenyl)benzene (THPB) , which is recovered by filtration ' and which can be purified by recrystallization or HPLC. (yield: 79%) . In Example 12, if part of 4-HAP is replaced by a different phenolic compound, then a substituted THPB may be formed. Also, the trimerization reaction in Example 12 uses aniline as the condensation reagent. Instead, an acid- catalyzed trimerization using, for example, HCl and triethyl orthoformate, may be employed. Example 13. Reduction of 4-HAP to the corresponding benzyl alcohol; Approximately 0.85 moles of 4-HAP is added to a 500 ml autoclave equipped with a mechanical stirrer, inlets and outlets for N2 and H2, and suitable means for heating and cooling. An optional cosolvent (alkane, alcohol, ether, or other solvents deemed suitable to those skilled in the art) may be added to dissolve 4-HAP if it is not naturally liquid at anticipated reaction temperatures. A suitable Raney nickel catalyst for the hydrogenation of 4-HAP to 1- (4-hydroxyphenyl)ethanol (typically a commercially available molybdenum promoted variety, shipped in water/caustic) is prepared for the reaction via the following procedure. The caustic/water is decanted or filtered from the nickel catalyst, then the catalyst is washed with approximately 10 times its weight of isopropanol, at least three times. In some optional cases, the catalyst is further washed with reaction solvent, reactants, or products, in order to remove the isopropanol from the catalyst. Approximately 10 wt % of the Raney Nickel catalyst (relative to the 4-HAP) is added to the hydrogenation reactor described above, the reactor sealed, and purged with N2. The reactor is stirred and heated to reaction temperature (- 60°C) . Hydrogen gas is added to the reactor to give a total reactor pressure of 400 psig, and replenished as necessary to maintain the reactor pressure at 400 psig. When the slowing of H2 gas uptake indicates the reaction is complete, the reaction is terminated by stopping stirring and rapidly cooling the reactor. The catalyst is filtered from the reaction product, and the crude product can be optionally purified by means such as distillation, crystallization, or chromatography. The above procedure was used to reduce 0.843 moles of 4'-acetoxyacetophenone using 10.4% Davison R3100 catalyst, in the absence of a cosolvent, over 280 minutes, to yield 1-(4'-acetoxyphenyl)ethanol in 94% yield. Instead of catalytic hydrogenation, the above reduction to the benzyl alcohol could be carried out with sodium borohydride too. Alternatively, Grignard reaction may be employed to achieve the same, as disclosed by Nir e£ al, J. Polymer Science: Polymer Chemistry Ed. , Vol. 20, 2735-2754 (1982) . Example 14. Dehydration of the benzyl alcohol of Example 13 to the corresponding styrene: This procedure is similar to that of Nir et al. referred to above. An agitated mixture of the crude benzyl alcohol from Example 13 and freshly fused KHS0 4 (1.0 g per 10 grams of the benzyl alcohol) is heated to 165° C in a short-path distillation apparatus under vacuum (0.005 mm HgA) . The resulting vapors are condensed to provide the crude styrene, which may be purified by liquid chromatography. The above dehydration may also be catalyzed by anhydrous CuS0 4 . Alternatively, the dehydration reactionmay be carried out in presence of phosphoric acid as Example 15 illustrates. Example 15. Dehydration of the benzyl alcohol to the styrene in presence of phosphoric acid; A three necked 250 ml round bottom flask was equipped with a magnetic stirrer, a distillation column, a thermometer and a vacuum pump. The flask was heated- to 220-230° C by immersion in an oil bath and maintained at a vacuum of 80 mmHg. l-(4'- acetoxyphenyl)ethanol (1.16 mol) was mixed with acetic anhydride (1.28 moles), phenothiazine (0.1 wt%) , and 85% by weight phosphoric acid (0.32 mol%) . The reaction mixture was fed continuously at a rate of 2.0 g/minute to the hot flask and the distillate was collected overhead. The residue was left in the hot flask and maintained at 180-190° C. After all the reaction mixture has been added to the hot flask, the vacuum was increased to 10 mmHg. A total of 338.7 g of the product was collected overhead. Analysis of the product by gas chromatography revealed that 0.96 moles of 4'-acetoxystyrene were made (83% yield). Example 16. Esterlflcation of the benzyl alcohol; A 3 1 round bottom flask equipped with a reflux condenser, a magnetic. stirrer was charged with l-(4'- acetoxyphenyl)ethanol (from Example 13, 2.8 moles), sodium acetate (0.15 moles) and acetic anhydride (3.6 moles). The reaction mixture was heated to 120° C and stirred for 6 hours. The reaction mixture was then cooled to room temperature and stirred for 16 hours. Acetic acid and unreacted acetic anhydride were removed via distillation under reduced pressure. The product l-(4'- acetoxyphenyl)ethyl acetate (2.1 moles) was distilled at 0.05 mmHg b.p. 132°C. Example 17. Preparation of styrene bv elimination of carboxylic acid from esters; A three necked 250 ml round bottom flask was equipped with a magnetic stirrer, a " distillation column, a thermometer and a vacuum pump. The flask was heated to 220-230°C by immersion in an oil bath and maintained at a vacuum of 80 mmHg. l-(4'- Acetoxyphenyl)ethyl acetate (from Example 16, 0.86 moles) was mixed with acetic anhydride (0.86 mol), phenothiazine (0.1 wt%) , and ammonium bisulfate (0.25 mol%) . The reaction mixture was fed continuously at a rate of 2.0 g/mimite to the hot flask and the distillate was collected overhead. The residue was left in the hot flask and maintained at 180-190°C. After all the reaction mixture has been added to the hot flask, the vacuum was increased to 10 mmHg. A total of 306.9 g of the product was collected overhead. Analysis of the product by gas chromatography revealed that 0.68 moles of 4'-acetoxystyrene were made (7.9% yield). Example 18. Preparation of the styrene derivative from 4-HAP bv wittig reaction; Methyltriphenyl phosphonium bromide (35.7 g, 0.1 moles) is placed under nitrogen atmosphere into a dry three neck 500 ml flask equipped with a magnetic stirrer, a condenser, and a nitrogen bubbler. Anhydrous tert-butyl alcohol (150 ml) is added and the reaction mixture stirred at room temperature. A solution of potassium tert-butyl-butoxide (12.3 g, 0.11 moles) in tert- butyl alcohol (100 ml) is added dropwise to the flask with stirring. After the addition is complete, the reaction mixture is stirred at room temperature for 0.5 hours to complete the preparation of the Wittig reagent CH 2 =P(Phenyl) 3 . To this Wittig reagent, a solution of 4-HAP (0.08 moles) in tert-butyl alcohol (100 ml) is added dropwise over one hour period and the reaction mixture is stirred for an additional three hours at 40°C. The reaction mixture was poured into ice-water (500 ml) and extracted with 3 x 200 ml portions of pentane. The combined pentane extracts are washed with water, dried over anhydrous magnesium sulfate to afford the styrene which may be purified by suitable methods. Preparation of polymers; Example 19. Preparation of Polvsulfones Containing THPE-BZT; Polysulfones are typically prepared from equi olar amounts of dihydric phenols and 4,4'- dichlorodiphenyl sulfone as described in the Encyclopedia of Polymer Science and Engineering. Vol. 13, p. 196-211 (Wiley, 2nd. Edition, 1988) . THPE-BZT prepared in accordance with Example 4 above is substituted for a portion of the stoichiometric amount of dihydric phenol, preferably in an amount of from about 0.05 to about 5 mole percent of the reaction mixture to produce the novel polysulfone polymers of the present invention as follows: Moles 4.4'-dichlorodiphenylsulfone 1 1 1 1 1 Polymerization of the foregoing mixtures is preferably carried out by way of the in-si tu preparation of sodium or potassium salts of the dihydric phenol and reaction with- the dichlorosulfone. Likewise, THPE-BZT may be substituted for diols in condensation polymers such as polyesters and polycarbonates in like molar ratios. Example 20. Preparation of polyesters containing THPE- BZT; Polyesters may be prepared by using THPE-BZT as the diol and a suitable dicarboxylic acid or a dicarboxylic acid derivative such as, for example, terephthaloyl chloride, by following a procedure similar to Example 18. Example 21. Preparation of polycarbonates containing THPE-BZT; Polycarbonates may be prepared by using THPE-BZT as the diol and a suitable carbonyl derivative such as, for example, phosgene, by following a procedure similar to Example 18. Example 22. Preparation of Polyurethanes Containing THPE-BZT; Polyurethanes are prepared incorporating THPE-BZT by substitution of THPE-BZT for other polyols present in a reaction mixture. Examples are described in the Encyclopedia of Polymer Science and Engineering. Vol. 13, p. 243-303 (2nd. Edition, 1988, Wiley). As used herein, the term polyurethane refers to materials that include the carbamate function as well as other functional groups such as ester, ether, amide and urea. Polyurethanes are usually produced by the reaction of a polyfunctional isocyanate with a polyol or other hydroxyl-containing reactant. Since the functionality of the hydroxyl-containing reactant or the isocyanate can be adjusted, a wide variety of branched or cross-linked polymers can be formed. The hydroxyl- containing component may be of a wide variety of molecular weights and types including polyester and polyether polyols. The polyfunctional isocyanates may be aromatic, aliphatic, cycloaliphatic or polycyclic in structure and can be used directly as produced or modified. The flexibility in reactants leads to the wide range of physical properties of available materials. Present invention polymers are prepared by substituting THPE-BZT (from Example 4 above) for a portion of the hydroxyl- containing reactant in a mole ratio of THPE-BZT/hydroxyl from about 0.001: 1 to about 0.1:1 for the polyol in a polyurethane reaction mixture or, in other words, from about 0.05 to about 5 mole percent of the total mixture as described above in connection with polysulfones. Example 23. Preparation of Epoxy Resins Containing THPE-BZT; Epoxy resins may be produced by reactions of epichlorohydrin and a hydroxyl monomer such as bisphenol A [2,2-di (4'-hydroxyphenyl)propane] . Examples are described ' 26 in the Encyclopedia of Polvmer Science and Engineering. Vol. 6., p. 322-382 (2nd. Edition, Wiley, 1988). When a portion of the hydroxyl monomer is replaced by THPE-BZT (from Example 4 above) , such processes yield epoxy resins with covalently bound, non-migratory UN- light stabilizing functionality. The THPE-BZT may be added in any suitable amount, depending upon, the reaction system selected, it being appreciated by those of skill in the art that perhaps the most important intermediate in epoxy resin technology is the liquid reaction product of excess epichlorohydrin and bisphenol A as noted above.

Claims: CLAIMS What is claimed is: 1. A functionalized aromatic monomer useful as- an ultraviolet stabilizer, antioxidant or colorant in a polymeric system, said monomer being derived from 4- hydroxyacetophenone, and including a structural unit selected from the group consisting of: wherein each R is independently selected from the group consisting of hydrogen, alkyl, aroyl, alkanoyl, and a structural unit selected from the group consisting of 3,3,- diaryl-2-cyanoacryloyl and 2,2,6,6-tetraalkylpiperidinyl, each X indicates independently a moiety selected from the group consisting of benzotriazole, benzophenone, branched alkyl, aroyl, diazoarene, and 2,2, 6, 6-tetraalkylpiperidine, and n is an integer from 1 to 5. 2. A polymer comprising said functionalized aromatic monomer of claim 1 as a residue. 3. A condensation polymer, comprising said functionalized aromatic monomer of claim 1 as a residue, wherein said condensation polymer is selected from the group consisting of polyester, polycarbonate, polyurethane and polysulfone. 4. A functionalized aromatic compound useful as an ultraviolet stabilizer, antioxidant or colorant in a polymeric system including the structural formula: wherein each R is independently selected from the group consisting of hydrogen, alkyl, aroyl, alkanoyl, and a structural unit selected from the group consisting of 3,3,- diaryl-2-cyanoacryloyl and 2,2,6, 6-tetraalkylpiperidinyl, each X indicates independently a moiety selected from the group consisting of benzotriazole, benzophenone, branched alkyl, aroyl, diazoarene, and 2,2,6,6-tetraalkylpiperidine, and n is an integer from 1 to 5. 5. The functionalized aromatic compound of claim 2, wherein X is benzotriazole. 6. The functionalized aromatic compound of the claim 2, wherein X is benzophenone. 7. A functionalized aromatic compound useful as an ultraviolet stabilizer, antioxidant or colorant in a polymeric system including the structural formula: wherein each R is independently selected from the group consisting of hydrogen, alkyl, aroyl, alkanoyl, and a structural unit selected from the group consisting of 3,3,- diaryl-2-cyanoacryloyl and 2,2, 6, 6-tetraalkylpiperidinyl, each X indicates independently a moiety selected from the group consisting of benzotriazole, benzophenone, branched alkyl, aroyl, diazoarene, and 2,2, 6, 6-tetraalkylpiperidine, and n is an integer from 1 to 5. 8. A functionalized aromatic compound useful as an ultraviolet stabilizer, antioxidant or colorant in a polymeric system including the structural formula: wherein each R is independently selected from the group consisting of hydrogen, alkyl, aroyl, alkanoyl, and a structural unit selected from the group consisting of 3,3,- diaryl-2-cyanoacryloyl and 2,2,6,6-tetraalkylpiperidinyl, each X indicates independently a moiety selected from the group consisting of benzotriazole, benzophenone, branched alkyl, aroyl, diazoarene, and 2,2, 6,6-tetraalkylpiperidine, and n is an integer from 1 to 5. 9. A functionalized aromatic compound useful as an ultraviolet stabilizer in a polymeric system including the structural formula: wherein R indicates hydrogen or one or more alkyl, aryl or hydroxy groups. 10. A condensation polymer, wherein said compound of claim 9 is incorporated as a residue.

Inventors: FRITCH JOHN R, KVAKOVSZKY GEORGE, MURPHY MARK A, FRITCH, JOHN, R., KVAKOVSZKY, GEORGE, MURPHY, MARK, A.
Applicants: HOECHST CELANESE CORP, HOECHST CELANESE CORPORATION
Application year: 1993
Main classification: C07C43
IPC codes: C07C37, C07C39, C07C43, C07C45, C07C49, C07C255, C07D211, C07D249, C07D295, C08G18, C08G59, C08G75, C08K5, C08L101, C09B69, C09K3, C09K15