Process for improving adhesive attachment

Abstract: The invention relates to a process for treating a machined glass surface for improving the adhesive attachment of an optical fiber to this surface, characterized in that machined surface is attacked by an aqueous solution of hydrofluoric acid, then the attacked surface is treated with a bifunctional hydrolyzable silane adhesion promoter or the product of its hydrolysis and partial condensation.

Description: Background of the Invention The invention relates to a process for improving the attachment with an adhesive of optical fibers to a glass substrate, and also to an integrated optical component treated by this process. US-A-3 341 399 discloses a method of bonding together glass surfaces with a polyvinyl butyral film, which method involves, after a step of cleaning the surfaces to be bonded, the steps of treating said surfaces with an aqueous solution of a triethoxysilane, then pressing the surfaces together while heating at a temperature approximating the flow point of polyvinyl butyral. I.V. PISHCH et al., in CERAMIC ABSTRACTS, Vol. 54, No. 9/10, October 9, 1975, discuss the effect of NH₄F on the polishing of cut glass using different concentrations of HE and H₂SO₄ solutions. Integrated optical components such as couplers to which optical fibers are glued, are known (for example in FR-A-2 612 301 or in the application for the French patent 92 07490 filed on June 19, 1992). Most of the time optical fibers must be glued to a surface of the component which has been produced by mechanical or other machining (sawing) of a slice or small sheet of glass. It turned out that the adhesive attachment between the fibers and the machined surface on which they are glued is very often defective. The Applicant, who caried out extensive research to solve this problem, has found that the defective attachment which was observed could be the result of one or more of the following causes : fragility of the glass surface resulting from the machining process (porosity, fissures, loosely fixed fragments) ; the presence of organic or other stains on the machined surface; the existence of an elevated degree of unstabilized ions of alkali metals in the surface layer of the machined glass, which could result from a previous ion-exchange process, optionally under the action of an electric field; the use of a glass with a relatively low silica content (<55% in weight), which can be altered by humidity. Therefore, there is a need for a treatment of a machined glass surface which improves the adhesive attachment of optical fibers to this surface. The invention precisely aims to provide such a treatment. The invention relates to a process for treating a machined glass surface, for improving the attachment of an optical fiber to this surface with an adhesive, characterized in that the machined surface is attacked by an aqueous solution of hydrofluoric acid; then the attacked surface is treated with a bifunctional hydrolyzable silane adhesion promoter or the product of its hydrolysis and partial condensation. We surprisingly found that the inventive treatment improved the adhesive bond to a much greater extent than could be expected from the improvements obtained with separate treatments -- that is by a solution of hydrofluoric acid alone or by a silane treatment alone. The invention is especially useful for treating glasses with a SiO₂ content below 55% in weight which are particularly sensitive to the effects of humidity at a moderately elevated temperature (60-65°C). As an aqueous solution of hydrofluoric acid, a diluted solution as well as a concentrated solution can be used. The speed of the attack will simply be increased according to the concentration of the solution, and therefore the duration of the attack will have to be adjusted accordingly. Also, the attack will be more rapid if the temperature is elevated. Finally, an ultrasonic stirring of the attack bath will increase even more the speed of attack. We have found that the attack conditions (concentration, stirring, duration, temperature) leading to the removal of a layer of glass of 3 to 5 µm are usually satisfactory. After such an attack, one usually observes the disappearance, on the machined surface, of the scratches and roughness due to mechanical sawing, and the formation of a surface with a globular and more polished aspect. However, a more significant attack can be carried out without drawback provided that it is taken into account in the component dimensions. Nevertheless, such a significant attack does not seem to provide additional advantage. Besides the hydrofluoric acid, the attacking solution may contain an auxiliary acid such as sulfuric or acetic acid. The effect of such an acid is to accelerate the attack. A buffer agent, such as NH₄F, could also be present in the solution, if desired. The hydrofluoric attack must be preceded by a careful cleaning of the surface to be attacked, for example by an ultrasonic wash with a diluted detergent solution, by an ultrasonic wash with an organic solvent such as acetone, and by an alcohol rinse with intermediate and final nitrogen blowing. The careful cleaning of the surface to be attacked may include an ultrasonic wash using a detergent solution of M9 powder, in concentration of 15-25 grams/liter, and M9 additive in concentration of 15-25 ml/l, at a temperature of 60°C for three (3) minutes, followed by three (3) rinses with water at 8MΩ to 10MΩ resistivity (i.e., high purity grade water) with and without ultrasonic vibration. M9 powder is a phosphate detergent with pH buffered at 8.6 to prevent glass from corrosion in alkaline media. M9 additive is a non-ionic surface active agent. Both M9 powder and M9 additive were purchased from FISA, ZAC des Gâtines, 4 avenue du Garigliano, 91601 Saviguy sur Orge Cedex, France. After the hydrofluoric attack, the surface is carefully rinsed with water for example, using a process similar to the rinses incorporated in the careful cleaning, and dried, for example, by heating at 105°C for approximately 60 minutes followed by cooling at room temperature for about 10 minutes, and then it is subjected to a silane treatment. This treatment is carried out with a solution of bifunctional hydrolyzable adhesion promoter or the product of its hydrolysis and partial condensation. The glass adhesion promoters are well known. The most common ones are glycidoxyalkyltrialcoxysilanes, such as glycidoxypropyltrimethoxysilane, or aminoalkyltrialcoxysilanes, such as gamma aminopropyltriethoxysilane. These agents are usually used in the form of a diluted alcoholic aqueous solution containing from 0.1 to 10% in weight of silane --preferably from 0.5 to 2% in weight, though these proportions are not critical--. The following non-limiting examples are given in order to illustrate the invention. Example 1 Four glass couplers having a machined surface for the gluing of optical fibers, formed of a glass composed, in weight % of 47.8% SiO₂, 17.4% B₂O₃, 14.6% Al₂O₃, 12.4% K₂O, 2.2% Na₂O and 5.6% F have been carefully washed, then plunged for 4 seconds at 20°C, without any stirring, into a bath of 23M hydrofluoric acid solution (commercial solution at 40%), and then rinsed with demineralized water in two successive baths, and finally dried with nitrogen blowing. The resulting dry couplers have been treated in a silane bath, composed in weight % of 1% of A187 silane (glycidoxypropyltrimethoxysilane) sold by UNION CARBIDE, 1 wt.% water and 98 wt.% ethanol, that has been previously aged under stirring for 24 hours in order to produce the silane hydrolysis and partial condensation. The duration of the immersion of the couplers in the bath, without stirring, lasted 2 minutes. Then, the couplers have been dried with nitrogen, and placed in an oven at 105°C for 1 hour to complete the silane condensation. Eight optical fibers have been glued to each of the ultimately obtained couplers with a photopolymerisable acrylate adhesive Luxtrak (R) LCR 050V from the ICI Corporation. The couplers with the glued optical fibers have been subjected to a humidity resistance test. This test consisted of maintaining the samples at 60°C and 93% relative humidity for 18 days, then at 65°C and 93% relative humidity for 8 days. At the end of the test, the fiber attachment areas have been observed through a microscope, and the fibers under which the onset of detachment between glass and adhesive (presence of an air strip) was visible have been counted. For comparison purposes, the following samples have also been prepared : 4 samples with no preliminary treatment (except the initial cleaning), 4 samples treated only with hydrofluoric solution, 4 samples treated only with silane. The obtained results are summarized in the following table: Without HF Treatment With HF Treatment Treatment Without Silane With Silane Without Silane With Silane # of Detachments /32 20 15 24 0 % of Detachment 63 47 75 0 These results show, surprisingly, that: 1) without HF treatment, an attachment to a silanised glass has a better humidity resistance than an attachment to a non-silanised glass, but the resulting advantage is insufficient to be satisfactory from an industrial standpoint; 2) the HF treatment alone doesn't improve the humidity resistance of the attachment rather the treatment deteriorates the resistance in comparison with the absence of any treatment; 3) the HF treatment followed by the silane treatment produces a synergistic effect that results in an exceptional humidity resistance for the attachment. Examples 2 to 4 The highly concentrated solution used in the example #1 presents the following drawback: the glass is attacked so quickly that the attack duration must be controlled with precision, a 1 or 2 seconds error being capable of making the attack depth vary 1 µm or more. As the optical fibers must be very precisely positioned on the coupler, it may be difficult to control the use of such a concentrated solution on an industrial scale. Therefore, attack bath compositions and attack conditions producing a slower attack while allowing a 3 to 5 micrometers glass elimination in 1 to 2 minutes are suggested below. Example HF, mole/l H₂SO₄ mole/l °C stirring 2 0.6 - 20 none 3 0.46 0.23 25 none 4 0.46 - 25 none Example 5 This example illustrates the effect of the temperature on the attack speed. The composition of the attack bath used is the one of example 3, and 3 sample-couplers have been subjected to an attack of 2 minutes in this bath, without any stirring, and at temperatures of 20, 25 and 30°C, respectively. The thickness of eliminated glass on the machined part of each couplers was, respectively, 1.7, 2.8 and 3.7 µm. This example shows that the temperature plays an important role, and that it must be precisely controlled to obtain reproducible results. Example 6 This example illustrates the effect of ultrasonic vibration on the speed of the attack. The composition of the attack bath used is the one of example 3, and sample-couplers have been subjected to an attack in this bath at 25°C for 2 min, with and without ultrasonic agitation. The attack depths on the machined surface of the couplers have been 4.9 and 2.8 µm respectively. Thus, ultrasonic vibration increases the attack speed to a great extent. Needless to say, the described embodiments are merely examples, they can be modified -- in particular by substituting technical equivalents -- without thereby departing from the scope of the invention.

Claims: A process for treating a machined glass surface, to improve the adhesive attachment of an optical fiber to this surface, wherein said machined surface is attacked by an aqueous solution of hydrofluoric acid, then the attacked surface is treated with a silane adhesion promoter. The process of claim 1, characterized in that the hydrofluoric acid solution also contains an auxiliary acid. The process of claim 2, characterized in that the auxiliary acid is sulfuric acid. The process of claim 1, characterized in that said silane adhesion promoter is a bifunctional hydrolyzable silane adhesion promoter or the product of its hydrolysis and partial condensation. The process of claim 1, 2, 3 or 4, characterized in that the attack is continued until the thickness of eliminated glass is 3 to 5 µm. The process of claim 1, characterized in that the silane adhesion promoter is chosen from among the glycidoxyalkyltrialcoxysilanes and the aminoalkytrialcoxysilanes. The process of claim 6, characterized in that the adhesion promoter is the glycidoxypropyltrimethoxysilane. The process of any of claims 1 to 7, characterized in that the process is carried out on the machined surface of a glass with a SiO₂ content below 55 weight %. The process of any one of claims 1 to 8, characterized in that the process is carried out on a coupler. The process of any one of claims 1-9, characterized in that the attack is preceded by a cleaning step. The process of claim 10, characterized in that said cleaning step comprises washing in a detergent solution under ultrasonic agitation followed by rinsing with water. An integrated optical component comprising a glass body having at least one machined surface to which at least one optical fiber has been attached by means of an adhesive, wherein said surface has been treated by a process such as defined in any one of claims 1 to 11.

Inventors: FLORENT FREDERIC HENRI FRANCOI, PEGOURET JEAN MARIE MARCEL GEO, FLORENT, FREDERIC HENRI FRANCOIS JEAN-MARIE, PEGOURET, JEAN MARIE MARCEL GEORGES
Applicants: CORNING INC, CORNING INCORPORATED
Application year: 1993
Main classification: C03C27
IPC codes: C03C27, C03C17, G02B6, C03B37, C07F7, C03C15, C09J5