Thermoplastic resin composition

Abstract: A thermoplastic resin composition comprising (A) an ethylenic copolymer containing at least one of acrylamide derivative units and methacrylamide derivative units and (B) other thermoplastic resin and a laminate containing at least one layer prepared from the thermoplastic resin composition.

Description: The present invention relates to a thermoplastic resin composition, and more particularly to a thermoplastic resin composition, useful as a raw material for moldings having distinguished characteristics such as mechanical strength, impact strength, elasticity, gas barrier property, adhesiveness, antistaticability, low temperature heat sealability, transparency, coatability, miscibility, moldability, radiation resistance. Thermoplastics have been widely used in fields of industrial materials, structural materials, medical instrument materials, packaging materials for food, medicines, cosmetics, industrial articles, laminated steel plates, automobile materials, on the basis of their characteristics. However, they still have problems due to recent increasing demands for higher quality. Polyolefins have been used in various fields owing to their low cost, high mechanical strength, good sanitation, and good moldability. However, polyolefins have poor oil resistance and gas barrier property, and when they are used as containers for food such as mayonnaise, soy sauce, it is impossible to preserve these kinds of food for a long time. When they are used as gasoline containers, there are such drawbacks as a large amount of gasoline leakage and swelling of containers leading to container deformation. To overcome the drawbacks, it has been so far proposed to laminate the polyolefins with polyester (which may be hereinafter referred to as PET), polyamide (which may be hereinafter referred to as PA), a saponification product of ethylene-vinyl acetate copolymer (which may be hereinafter referred to as EVOH), aluminum foils, glass or the like through an adhesive layer, or to vapor-deposit a gas barrier material of metal, metal oxide onto the polyolefins. For example, it is known to conduct lamination by applying a dry lamination adhesive such as a polyurethane-based adhesive, a polyacrylic adhesive or a polyester-based adhesive, or to conduct co-extrusion laminating polyolefins graft-polymerized or copolymerized with an unsaturated carboxylic acid or its anhydride as an adhesive resin for lamination. Furthermore, it is known to use olefins graft-polymerized with an acrylic resin derivative as an adhesive resin for the polyolefin and EVOH (JP-A 60-165242), to use a mixture of the graft-polymerized polyolefins with carboxy-modified olefinic polymers or copolymers (JP-A 60-187550), or to use a mixture of olefinic polymers or copolymers with the grafted polyolefins (JP-A 60-184839). However, delamination of the laminates obtained even by these processes has been often observed owing to unsufficient adhesion strength. Polypropylene is generally cheap and is used in various fields on the basis of its distinguished characteristics such as distinguished transparency, mechanical strength, heat resistance, gloss, chemical resistance, oil resistance, rigidity, flex fatigue resistance. Among polypropylene (which may be hereinafter referred to as PP), homo PP has a high glass transition temperature and thus has such drawbacks as high brittleness at a low temperature, easy breakage, poor transparency. PP has such drawbacks as a poor coatability, a high susceptibility considerable deterioration of physical properties when subjected to irradiation of radiation, or a poor heat sealability at a low temperature. In attempts to overcome these drawbacks, for example, in attempts to improve the transparency, it is known to add a dibenzylidene sorbitol derivative as a nucleating agent to PP and obtain the transparency due to the effect of the nucleating agent, as disclosed in Polymer Digest, July issue (1984), page 116 and Polymer Digest, June issue (1985) page 43. However, these procedures still have such problems as decomposition of the nucleus-making agent during the molding, emission of disagreeable odor, decrease in the impact resistance due to the effect of the nucleus-making agent. Furthermore, it is known to use special molding procedures, for example, to add hydrogenated terpene resin and a nucleating agent to PP, followed by molding and quenching, thereby to obtain a transparent sheet (JP-A 1-171833 and JP-A 1-171834) or to add an ethylene/a-olefin copolymer to PP, followed by molding and quenching below 60°C (JP-A 1-299851). However, these procedures require a special molding machine, because it is difficult to readily obtain a molding of high transparency by ordinary molding machines. In attempts to improve the impact resistance, it is known to add 5 to 20% of polyisobutene to PP (JP-B 35-10640), to add 5 to 20% of ethylene/propylene copolymer (JP-B 35-7088), to add a lower pressure process polyethylene of high molecular weight to PP (JP-B 37-6975), or to add polyethylene (which may be hereinafter referred to as PE) and ethylene/propylene rubber to PP, thereby making the so called propylene/ ethylene block copolymer [Kuroda: Kobunshi (Polymer), Vol. 28, No. 10, page 714 (1979)]. However, these procedures still have such problems as poor luster and poor transparency. Furthermore, it has been proposed to add an ethylene-vinyl ester copolymer and/or ethylene-acrylate copolymer to PP (JP-A 51-145553), or to add a modified specific ethylene-propylene copolymer obtained by graft polymerization with an unsaturated dicarboxylic acid or its anhydride to PP (JP-A 61-89239). These procedures still have such problems as a poor effect on the improvement of coatability and a poor compatibility. Among polyolefins, PP has an excellent flexing characteristic (hinge characteristic), but the flex crease turns white, or when a tension is applied to PP, the site on which the tension has been applied turns white. That is, a phenomenon of local whitening, so called stress whitening, appears. To prevent the whitening of PP, it has been so far proposed to add a lubricant or a plasticizer to PP, followed by kneading. However, this procedure has such problems as appearance of bleeding and blooming and deterioration of transparency. Furthermore, in the field of medical packaging, PP moldings are usually irradiated with gamma ray of cobalt 60 or electron beams as a sterilizing means. However, such a sterilization treatment of PP deteriorates PP, that is, lowers the physical properties such as impact resistance, stretching elongation, etc. To solve the problems, various procedures including modification of PP have been proposed (JP-A 60-215047 and JP-A 61-73711). However, all these procedures have such drawbacks as insufficient transparency, and insufficient effect of control on decreases in physical properties such as impact resistance and stretching elongation after the irradiation with radiation beams. Furthermore, it has been proposed to improve the heat sealability of PP at a low temperature by adding polybutene-1, or an ethylene/propylene elastomer, or an ethylene/propylene/butene-1 copolymer to PP (JP-A 54-28351 and JP-A 54-603498). However, these procedures still have such a drawback as insufficient heat sealability at a low temperature. Since polyvinyl alcohol (which may be hereinafter referred to as PVA) has a very close melting temperature and a heat decomposition temperature very close to each other, it has been impossible to conduct melt-extrusion molding of PVA. The PVA film is soft and tough under a high humidity, but loses the flexibility under a low humidity to become brittle and thus readily breakable. It has been proposed to solve these problems, for example, by adding EVOH to PVA (JP-A 49-33945) or by adding other polymers than polyolefins to modified PVA (JP-A 49-117536) or by other means (JP-A 50-123151). However, all these procedures still have insufficient melt moldability and a poor gas barrier property. Generally, PA is tough, but an impact resistance as one of indicators of toughness is considerably increased by moisture adsorption. The impact resistance of PA right after the molding or in the dry state during the winter season or at a low temperature is not always satisfactory. That is, cracks are often generated on the PA moldings. In attempts to improve the impact resistance of PA, it is known to add a copolymer resin of polyolefin and α,β-unsaturated carboxylic acid or its ester, graft-modified polyolefin resin with an α,β-unsaturated carboxylic acid represented by maleic anhydride, ionomer copolymer resin of ethylene and methacrylic acid or its ester ionized by Na, Zn, Mg, or graft-modified ethylene/propylene/diene copolymer rubber with maleic anhydride to PA (JP-A 51-70254, JP-B 44-29262, US Patent No. 3,845,163 and JP-B 54-44108). However, these procedures still have such problems as (1) poor compatibility with PVA, (2) local generation of gel by an organic peroxide during the graft modification, (3) generation of much gel by reaction with PA, when the polymer contains unreacted monomers, resulting in yellow discoloring, and (4) decrease in the gas barrier property by blending, which follows the addition. EVOH is used as packaging materials for food, cosmetic or medicines, which require a gas barrier property particularly to oxygen. However, EVOH is hard, very brittle and readily breakable. Since EVOH has hydroxyl groups in the molecule, it can readily absorb moisture such as water and water vapors, and its gas barrier property is much more deteriorated by moisture absorption. To overcome these drawbacks, EVOH is used as a multilayer laminate by laminating EVOH with one or more thermoplastic resins, such as polyolefins (for example, PE, PP, etc.), PET, polystyrene, polyvinyl chloride. The lamination procedure includes co-extrusion molding process or extrusion lamination molding process for extruding a thermoplastic resin such as polyolefins, EVOH and resin for bonding these polymers, thereby making a laminate, a dry lamination molding process for individual molding of these polymers, followed by lamination, a solution coating molding process, where the resulting laminate is in the form of sheets, films or bottles. The laminate sheets are used to serve as container packages, and thus the raw sheets of multilayer laminates are subjected to a secondary heat molding processing including high temperature stretching such as vacuum molding or compressed air molding. In the secondary processing, the molding conditions mostly depend on the polymer resin having an intermediate melting point among the constituent materials for the multilayer laminates. That is, the secondary heat molding processing is carried out under these molding conditions. Thus, EVOH, which usually belongs to the material species having a high melting point, is often subjected to the secondary processing under in appropriate molding conditions, and thus fine spaces (so called voids) or cracks are liable to form in the layers. Furthermore, such voids, cracks or local unevenness in the thickness are liable to form due to higher crystallization rate of EVOH. The laminate films undergo flexing movements in the pouch-making step, packaging step, distribution steps, resulting in occurrence of pinholes or cracks in the EVOH layer. Thus, the gas barrier property of EVOH is often deteriorated considerably. In attempts to solve these problems, a method for blending EVOH with PA (JP-A 59-20345), a method for mixing EVOH with glycerin (JP-A 53-88067), a method for blending EVOH with lithium chloride (JP-A 61-281147), have been proposed. However, the blending of EVOH with PA has a problem that PA reacts with EVOH during the melt molding, resulting in formation of gel or fish-eyes. The blending with a plasticizer such as glycerin has a problem that the plasticizers have a poor compatibility with EVOH and thus bleeding of these compounds takes place with time, i.e. the plasticizers move towards the boundary surface to the adhesive resin layer and the bonding strength to the layer is lowered with time. Furthermore, the blending of EVOH with lithium chloride, etc. has a problem that the distribution is often poor at the blending, or more cracks or pinholes are generated due to voids formed when the added compounds are subjected to heat stretching treatment. As described above, pinholes, cracks, unevenness in thickness are very liable to appear when a multilayered laminate of EVOH is formed or processed into containers, and consequently the gas barrier property is largely deteriorated. Furthermore, the multilayered laminate has another problem of effective utilization of scraps. For example, when a multilayered laminate film is processed into containers, burrs are formed up to about 40%. As a process for recovering such scraps, it has been attempted to reuse a regrind obtained by grinding the foregoing scraps. For example, there are suggested a process for providing a regrind layer composed of the regrind on the multilayer laminate or a process for mixing the regrind in the outermost polyolefin layer. However, since polyolefin and gas barrier resin generally have a poor miscibility between both, and polyolefin and gas barrier resin in the regrind form an unhomogenous mixture, the following troubles during mold-processing at the time of recovery occur. That is, when a regrind layer is provided, adhesion between the regrind layer and gas barrier layer is inferior, so that peeling readily takes place, or the part of gas barrier resin in regrind is readily peeled off as fine fibrous pieces, or foreign matters readily result from uneven interlayer separation. Such foreign matters increase in a prolonged operation, resulting in formation of projections or granular structures on the ultimate products, when observed from the outermost layer side of multilayered laminate, and thus the projections or granular structures considerably deteriorate the appearance of the multilayered laminate, or in the worst case these projections or granular structures break through the resin layers at the outer side or lower the mechanical strength. In the coextrusion molding, a known adhesive resin is generally used as a miscibility agent for the regrind component. However, such use of the known resin is not satisfactory yet, because of poor miscibility with EVOH or PA, and unreacted monomers, if present in the adhesive resin, readily react with EVOH or PA, resulting in much formation of gels and yellow discoloring as problems. Multilayered laminates using a hygroscopic gas barrier of EVOH, PA, PVA have such characteristics that permeation of a gas such as oxygen can be sufficiently suppressed at a low humidity to prevent oxidation of contents in containers, and the quality of the contents can be stabilized for a prolonged time. However, when the multilayered laminates are used in boiling water at 90° to 135°C as in the form of retort food packages, water permeates into the multilayered laminates from the outermost layer and is absorbed into the gas barrier layer. As a result, the gas permeation resistance of the gas barrier layer is abruptly lowered. That is, the multilayered laminates cannot be used in the pouch food application. For example, when a multilayered laminate consisting of a PP layer, an adhesive resin layer and an EVOH layer and having a total thickness of about 100 µm is subjected to a retort treatment in boiling water at least at 120°C, water absorption of the EVOH layer amounts to 7% by weight or more, and the oxygen permeation increases to 1,000 times as much as that before the retort treatment in some cases. In attempts to overcome these problems, it is proposed, for example, to add a drying agent comprising an inorganic metal salt to the adhesive layer that bounds the gas barrier layer to the outer layer so that the adhesive layer can capture the permeated water, thereby preventing the deterioration of the gas barrier property (European Patent No. 59274, US Patents Nos. 4,407,897 and 4,464,443; JP-A 57-170748). However, even in this proposed procedure, the interlayer bonding strength is decreased between the adhesive layer and the gas barrier layer, or the use is inevitably limited due to the presence of the inorganic metal salt as foreign matters. Furthermore, a method for adding a phenol compound to improve the water resistance (US Patents Nos. 4,347,337 and 4,289,830), and a method for forming the outermost layer of polycarbonate resin having a good water vapor permeability or PA or its mixture in close proximity to the EVOH layer (JP-A 1-253442; JP-A 1-308626; European Patent No. 322891) are known. However, these methods may be effective for thin products such as films, but not for thick product such as sheets and bottles and they are costly. In case of polycarbonate resin, it is difficult to conduct multilayered extrusion and thus a special extruder is required. On the other hand, in multilayered laminates containing an EVOH layer, attempts have been made to provide an EVOH layer at the outer side to accelerate restoration of the gas barrier property after the retort treatment [Paper, Film & Foil Converter, October issue, page 54 (1985); Food Package, November issue, page 82 (1985); ibid, December issue, page 67 (1985); COEX '89, page 267 (1989), held by Scotland Business Research, Inc. (USA)]. However, in these attempts, the resulting laminates take an asymmetrical multilayer structure in the thickness direction, and thus requires an additional extruder in the molding, in contrast to the coextrusion molding for producing a symmetrical multilayer structure in the thickness direction, which requires only one extruder for the outer layer resin. Thus, the molding is costly and the restoration of the gas barrier property is not satisfactory yet. Recently, an attempt has been made to use EVOH having a high content of ethylene units and set the EVOH layer to a large thickness in advance in anticipation of a deterioration of the gas barrier property due to the retort treatment [Future-Pak '90, page 125 (1990), Ryder Associates, Inc. (USA)]. However, the attempt has such a disadvantage as an inevitable high cost. Still furthermore, a method for blending a polymer reticular structure such as a reticular structure of vinyl alcohol-acrylate copolymer into any one of the oxygen barrier layer, the outer layer and the adhesive layer (JP-A 62-182030; JP-A 62-208344), and a method for blending an inorganic powder such as mica powder or sericite powder into the outer layer and the EVOH layer (JP-A 2-47139) have been proposed. However, the former has a problem in the molding due to poor melt moldability and heat stability of the polymer reticular structure, whereas the latter has problems due to the hardness and the resulting brittleness caused by the blending of inorganic powder. EP-A-490 562 discloses a polymeric blend and discloses that most commercial copolymers of ethylene and vinyl alcohol, having a relatively low mol% of vinyl alcohol content and diminished barrier properties, are unsuitable for the purpose of the invention of EP-A-490 562; however, copolymers of from about 5 to about 25 mol% ethylene, preferably from about 5 to about 15 mol%, may be melt-processed when blended with the copolymers of lower alkyl (meth)acrylates disclosed in EP-A-490 562. The object of the present invention is to provide a thermoplastic resin composition useful as a raw material for moldings having distinguished characteristics such as mechanical strength, impact strength, elasticity, gas barrier property, adhesiveness, antistatic properties low temperature heat sealability, transparency, printability, compatibility, moldability, radiation resistance. The object of the present invention is achieved by providing a thermoplastic resin composition which comprises: (A) 90 to 1% by weight of a copolymer consisting of ethylene units, 0.01 to 50 % by weight of N-alkyl or N,N-dialkyl acrylamide units and/or N-alkyl or N,N-dialkyl methacrylamide units, and optionally, not more than 40% by weight of units of other polymerizable monomers, and (B) 10 to 99% by weight of a saponification product of an ethylene vinyl acetate copolymer containing 29 to 60 mol% of ethylene units. Ethylenic copolymers containing at least one of acrylamide derivative units and methacrylamide derivative units for use as component (A) in the thermoplastic resin composition of the present invention can be prepared according to the ordinary procedures disclosed in Kobunshi Ronbunshu (Polymer Articles), Vol. 35, No. 12, page 795 (1978); US Patent No. 3,629,209; JP-B 43-21655; JP-B 44-19537; JP-B 43-23766; JP-B 43-9063; JP-A 63-304010. The procedures include bulk polymerization, solution polymerization, suspension polymerization and emulsion polymerization. Bulk copolymerization is the most popular procedure, where the ethylenic copolymer is prepared by radical polymerization at a temperature of 100 to 300°C and a pressure of 700 to 3,000 atmospheres. A preferable pressure range is 1,000 to 2,500 atmospheres and a preferable temperature range is 150 to 270°C as an average temperature in the reactor. Melt flow rate (which will be hereinafter referred to as MFR) at 190°C of the ethylenic copolymers for use in the present invention is preferably less than 300 g/10 minutes. To improve the bendability with other thermoplastic resin, a portion of the thermoplastic resin can be used as blended therewith in advance, and in that case basically it is not objectionable that MFR exceeds 300 g/10 minutes. Acrylamide derivatives and methacrylamide derivatives that constitute the ethylenic copolymers means N-alkyl derivatives and N,N-dialkyl derivatives, and specifically include, for example, N-methylacrylamide, N-ethylacrylamide, N-n-propylacrylamide, N-isopropylacrylamide, N-n-butylacrylamide, N-isobutylacrylamide, N-t-butylacrylamide, N,N-dimethylacrylamide, N,N-diethylacrylamide, N-ethylmethacrylamide, N-n-propylmethacrylamide, N-t-butylmethacrylamide, N,N-dimethylmethacrylamide and N,N-diethylmethacrylamide which can be used alone or in mixture. Above all, N-ethylacrylamide, N-isopropylacrylamide, N-t-butylacrylamide, N,N-dimethylacrylamide, N,N-diethylacrylamide, N-n-propylacrylamide, and N-t-butylmethacrylamide are preferable. Content of acrylamide derivative units and methacrylamide units in the ethylenic copolymer is within a range of 0.01 to 50% by weight, preferably 1 to 45% by weight. The ethylenic copolymer for use in the present invention contains ethylene units, 0.01 to 50% by weight of N-alkyl or N,N-diakylacrylamide units and/or N-alkyl or N,N-dialkylmethacrylamide units, and optionally not more than 40% by weight of other polymerizable monomers. The other polymerizable monomers include, for example, ester compounds, acid compounds, ether compounds, hydrocarbon compounds, each having an unsaturated bond. Ester compounds having an unsaturated bond include, for example, vinyl acetate, methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, hexyl acrylate, octyl acrylate, lauryl acrylate, benzyl acrylate, N,N-dimethylaminoethyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, hexyl methacrylate, octyl methacrylate, lauryl methacrylate, N,N-dimethylaminoethyl methacrylate, methyl fumarate, ethyl fumarate, propyl fumarate, butyl fumarate, dimethyl fumarate, diethyl fumarate, dipropyl fumarate, dibutyl fumarate, methyl maleate, ethyl maleate, propyl maleate, butyl maleate, dimethyl maleate, diethyl maleate, dipropyl maleate and dibutyl maleate. Acid compounds having an unsaturated bond include, for example, acrylic acid, methacrylic acid, maleic acid and fumaric acid. Ether compounds having an unsaturated bond include, for example, methylvinyl ether, ethylvinyl ether, propylvinyl ether, butylvinyl ether, octadecylvinyl ether and phenylvinyl ether. Hydrocarbon compounds having an unsaturated bond include, for example, styrene, norborene, butadiene, and further acrylonitrile, methacrylonitrile, acrolein, crotonaldehyde, trimethoxyvinylsilane, vinyl chloride and vinylidene chloride. Basically it is preferable that the polymerizable monomer will not react with the amide groups of acrylamide derivatives and methacrylamide derivatives, but when its amount is selected in view of the stoichiometric amount, it is possible to use monomers reactable with these derivatives. One or more of such polymerizable monomers can be used in accordance with desired applications. Content of the polymerizable monomer or monomers is not more than 40% by weight. Above 40% by weight, the characteristic properties of the ethylenic copolymer will be deteriorated. The resin composition contains 10 to 99% by weight of another thermoplastic resin as component (B). The other thermoplastic resin (B) is a saponification product of an ethylene vinyl acetate copolymer (EVOH). In the present invention, EVOH containing 29 to 60% by mole of ethylene component and having a saponification degree of vinyl acetate component of at least 90% is used. Below less than 29% by mole of ethylene component the melt moldability is lowered, and below a saponification degree of vinyl acetate component of 90% the gas barrier property is deteriorated. Preferably a saponification degree of vinyl acetate component of at least 96% is used. EVOH may contain, besides ethylene and vinyl acetate (or vinyl alcohol derived from saponification of vinyl acetate), unsaturated acids such as acrylic acid, methacrylic acid, crotonic acid and maleic acid, or their alkyl esters, or α-olefins such as propylene, butene, α-decene, α-octadecene as comonomers in such a small amount as not to deteriorate the major characteristics of saponification products. As to the mixing ratio of the present thermoplastic resin composition comprising (A) ethylenic copolymer and (B) saponification product, the present thermoplastic resin composition contains (A) 90 to 1% by weight of ethylenic copolymer and (B) 10 to 99% by weight of saponification product. Below 10% by weight of saponification product no gas barrier property will be obtained, whereas above 99% by weight no effects will be obtained on prevention of pinhole and crack development, prevention of uneven thickness, improvement of heat stretchability. Preferably, 20 to 96% by weight of saponification product is used in the present invention. Melt index (MFR under a load of 1.16 kg at 230°C according to JIS-K 6758) of the present thermoplastic resin composition is not particularly limited, and is appropriately in a range of 0.1 to 50 g/10 min. for a resin composition for extrusion molding, though dependent on type of molding procedures. In the present thermoplastic resin composition, better flexibility, impact resistance and gas barrier property can be obtained than those of single EVOH. In the present invention it is desirable that the content of ethylenic copolymer as component (A) is 1 to 40% by weight, preferably 2 to 35% by weight, more preferably 4 to 20% by weight. Below 1% by weight, the thermoplastic resin composition will be non-uniform, whereas above 40% by weight the thermoplastic resin will be soft, causing a trouble in some cases. In an embodiment of the invention a thermoplastic resin composition containing a thermoplastic resin containing 0.01 to 20% by weight of unsaturated dicarboxylic acid or its anhydride as a third component besides the components (A) and (B) is used. The thermoplastic resin is usually used as an adhesive resin for EVOH or PA. The content of the unit derived from unsaturated dicarboxylic acid or its anhydride in the thermoplastic resin of the third component is preferably in a range of 0.01 to 20% by weight. Below 0.01% by weight the mechanical strength of the resin composition will be unsatisfactory, and the compatibility of EVOH or PA with the thermoplastic resin will be decreased, whereas above 20% by weight the reaction with EVOH or PA will excessively proceed, resulting in undesirable coloring or gel formation. Preferable content of the unit derived from unsaturated dicarboxylic acid or its anhydride is in a range of 0.2 to 10% by weight. Unsaturated dicarboxylic anhydride includes, for example, maleic anhydride, itaconic anhydride, endic anhydric and citraconic anhydride. The thermoplastic resin as the third component may further contain a polymerizable monomer unit besides the unsaturated dicarboxylic acid or its anhydride. The polymerizable monomer includes ester compounds, acid compounds, ether compounds, hydrocarbon compounds, each containing an unsaturated bond. Besides the thermoplastic resin containing the unsaturated dicarboxylic acid or its anhydride, other thermoplastic resins such as polyolefins, e.g. PE, PA, copolymers of ethylene with α-olefin having 3 to 12 carbon atoms; polystyrene, polyethylene terephthalate; polyvinyl chloride, polycarbonate can be used as a fourth component thermoplastic resin. The present thermoplastic resin composition can contain various additives and compounding agents, if required. Examples of additives and compounding agents include an antioxidant (heat stabilizer), an ultraviolet absorber (light stabilizer), an antistatic agent, an anti-mist agent, a flame retardant, a lubricating agent (slip agent and antiblocking agent), inorganic and organic fillers, a reinforcing agent, a coloring agent (dye and pigment), a foaming agent, a cross-linking agent, a perfume. Procedure for blending to prepare the present thermoplastic resin composition is not particularly limited, and it is preferable to conduct pelletizing, for example, with a ribbon blender, a higher speed mixer, a kneader, a pelletizer, mixing rolls and then dry the resulting pellets. The respective components of the present thermoplastic resin composition can be directly charged into a molding machine to conduct molding. Additives and compounding agents can be added to the component polymers of the resin composition in the production line for pelletization or to the resin composition when pelletized. The present invention will be explained in detail below, referring to Examples and Comparative Examples, which will not be limitative of the present invention. In the following Examples and Comparative Examples the following testing procedures were employed: Izod impact strength (notched) Measurement was made according to ASTM-D256. Flexural modulus test Measurement was made according to ASTM-D790. Half-life test of static electricity Measurement was made by Electrostatic Honest Meter, Type S5109 (100 V, 80 VA, 1550 rpm), made by Shishido Denki K.K., Japan. Volume resistibility test Measurement was made by electric resistance meter, Type 16008, made by Yokogawa-Hewlett-Packard, K.K., Japan. Coatability test Measurement was made by cross-cut peeling test according to JIS-K5400. Radiation resistance test Test pieces were irradiated with γ-rays, 3 Mrad, from a cobalt-60 source, and tensile strength, elongation in tension and falling weight impact strength were measured right after the irradiation and after preservation at 50°C for 30 days. Tensile strength test Measurement was made according to JIS-K6758. Falling weight impact test Weight were made to fall onto test pieces from a definite height to measure an energy level (j(kg-cm)) until the test pieces were broken. Haze test Measurement was made by Haze meter, made by Toyo Seiki Seisakusho, K.K., Japan, according to ASTM-D1003. Heat seal peel strength test A film, 40 µm thick, was formed by a 40 mm-in-diameter cast film molding machine, and heat sealed at preset temperatures under head seal pressure of 98 kPa (1kg/cm 2 ) for a heat seal time of 1.0 second by a heat sealing machine having a heat seal bar, 5 mm x 200 mm, and test pieces, 15 mm wide, were prepared from the film. Type T peel strength was determined for every 10 test pieces at a drawing speed of 500 mm/minutes by rounding off the figure in the first place. Oxygen permeation test Measurement was made at a relative humidity of 65% and also of 90% by OXTRAN-10/50A, made by Modern Control Co. according to ASTM-D3985-81 (cc-30 µm/m 2 ·day·atm). Film impact strength test Test films were left standing at 23°C and a relative humidity of 50% for 7 days to conduct state conditioning and subjected to measurement at 23°C and a relative humidity of 50% by a pendulum-type, impact tester (2.54 cm (1-inch) hemisphere) made by Toyo Seiki Seisakusho, K.K., Japan. Film moldability test Melt molded state was observed and evaluation was made by the following marks: Symbol o ○: Good film state without any of formation, eg. of pores, gels, of the film. Symbol ○ : Fair film state, though there is slight formation of fisheyes. Symbol × : Poor film state with complete failure to conduct melt extrusion molding or with formation of pores. Flexural fatigue resistance test Measurement was made by Geboflex tester with a cylinder diameter of 90 mm, a stroke of 178 mm, a twisting angle of 440°, a twisting stroke of 89 mm, a straight stroke of 63.5 mm, and a reciprocating rate of 40 runs/minute, made by Tester Sangyo K.K., Japan where flexing number fill generation of pin holes was determined by increasing the flexing number of Geboflex tester to 5, 10, 50, 100, 200 and then upwards by every increment of 100. [Materials employed] (1) Ethylene copolymer (EAA) Abbreviation Composition (Figures show % by weight) EA - 1 E/DAA 19.2 (MFR 3.5) 2 E/DAA 37 (MFR 3.7) 4 E/DAA 9.1/MMA 6.2 (MFR 5.1) 5 E/DAA 8.2/MAH 3.9 (MFR 7.4) 7 E/DAA 27.0/VAC 6.0 8 E/DAA 20.0/MMA 10.0 9 E/DAA 18.6/MMA 9.6 (MFR 11.6) 10 E/DAA 24.1/VAC 3.4 (MFR 4.4) 11 E/DAA 28.2/VAC 7.8 (MFR 5.2) MFR (g/10 minutes) was determined at 190°C under a load of 2.16 kg according to JIS K 6760. E: Ethylene DAA: N,N-dimethyl acrylamide MMA: Methyl methacrylate MAH: Maleic anhydride VAC: Vinyl acetate (2) Ethylene/unsaturated dicarboxylic anhydride copolymer (EAN) EN - 1 E/MMA 7.6/MAH 2.8 (MFR 8.3) 2 E/EA 6.5/MAH 3.5 (MFR 6.8) EA: Ethyl acrylate (3) Modified polyolefin MP - 1 LDPE/MAH Graft 0.5 (MFR 5) 2 Random PP/MAH Graft 0.9 (MFR 55) (4) Other resins PO- 1 LDPE (ρ=0.923, MFR 3.5) 2 Random PP (MFR 8.4, E 3.2) 3 Homo PP (MFR 8.1) 5 Nucleating agent-added random PP (0.35 wt.% dibenzylidene-sorbitol added) (MFR 20.1, E 7.1) (5) Saponified product of ethylene/vinyl acetate copolymer (EVOH) EV - 1 Soanol D (made by Nihon Gosei Kagaku K.K., Japan (E 29 moles) 2 Soanol A (made by Nihon Gosei Kagaku K.K., Japan (E 44 moles) 3 Soanol DT (made by Nihon Gosei Kagaku K.K., Japan (E 29 moles) 4 Eval EP-F101 (made by Kuraray K.K., Japan) (E 32 moles) Preparation Example 1 Preparation of ethylenic copolymer Polymerization was carried out in an autoclave-type reactor of 4-ℓ net capacity with two separated zones at a temperature of 190 to 230°C under pressure of 182.39 MPa (1,800 atm) to 197.58 MPa (1,950 atm), using t-butylperoxypivalate. N,N-dimethyl acrylamide and acrylamide as acrylamide components, and at least one of other monomers and solvent were injected into the upstream to the second stage compressor, and charged into the first zone of the reactor together with ethylene. The resulting copolymer was separated from the unreacted monomers in a high pressure separator and a low pressure separator, and pelletized through an extruder. In this manner, copolymers having different ethylene contents and MFRs were prepared. Contents of acrylamide derivatives in the respective copolymers were determined by an infrared spectrometer and 13 C-NMR. Preparation Example 2 Preparation of ethylene/unsaturated dicarboxylic anhydride copolymer Polymerization was carried out in an autoclave-type reactor of 4-ℓ net capacity with two separated zone at a temperature of 190 to 230°C under pressure of 182.39 to 197.58 MPa (1,800 to 1,950 atmospheres), using t-butyl peroxypivolate. Unsaturated dicarboxylic anhydride or unsaturated dicarboxylic anhydride and at least one of other monomers and a solvent were injected into the upstream to the second stage compressor and charged into the first zone of the reactor together with ethylene. The resulting copolymer was separated from the unreacted monomers in a high pressure separator and a low pressure separator and pelletized through an extruder. Preparation Example 3 (1) Modified PE (MP-1) Low density polyethylene was molten and graft modified with maleic anhydride through twin screw extruder and then washed with acetone to completely remove the unreacted matters. MFR: 5 (g/10 minutes); density: 0.915; maleic anhydride content: 0.5 wt.% (2) Modified PP (MP-2) Ethylene/propylene random copolymer having ar ethylene content of 4.5 wt.% was molten and graft modified with maleic anhydride through a twin screw extruder and then washed with acetone to completely remove the unreacted matters. MFR: 55 (g/10 minutes); maleic anhydride content: 0.9 wt.% (3) Modified homo PP (MP-3) Homopropylene resin was graft modified with maleic anhydride. MFR: 72 (g/10 minutes); maleic anhydride content: 0.7 wt.% (4) Modified ethylene/propylene elastomer (MP-4) Ethylene/propylene elastomer was graft modified with maleic anhydride. Maleic anhydride content: 1.6 wt.% Examples 1-1 to 1-15 and Comparative Examples 1-1 to 1-3 Resin compositions were prepared by melt mixing ethylenic copolymer and PP (P0-2, 3 and 5) shown in Table 5 at 230°C by a vent-type twin screw extruder, type KTX-37, made by Kobe Seiko K.K., Japan. The thus obtained resin compositions were prepared into test pieces for determining Izod impact strength and flexural modulus by Minimat 24.80 g (7/8-ounce) injection molding machine, made by Sumitomo Juko K.K., Japan at an injection temperature of 230°C and a mold temperature of 45°C. The test pieces were left standing in a thermo-hygroset room at 23°C and a relative humidity of 50% for 7 days for state conditioning, and then subjected to determination of Izod impact strength (notched) and flexural modulus at 23°C and a relative humidity of 50%. The results are shown in Table 1. In Examples 1-2, 1-5, 1-8, 1-9, 1-12 and 1-14 and Comparative Examples 1-1 to 1-3, the resin compositions were molded not flat plates, 10 cm × 12 cm and 2 mm in thickness by a 283.5 g (10-ounce) injection molding machine, made by Nisei Jushi Kogyo K.K., Japan at an injection temperature of 230°C and a mold temperature of 45°C. The molded flat plates were subjected to determination of volume resistivity on one hand, and the same flat plates were sprayed with Flexen 101, a product made by Nihon Paint K.K., Japan to conduct a coatability test. The results are shown in Table 5. To observe stress whitening, the flat plates were flexed, and it was found that no whitening phenomena were observed on all the flat plates of Examples, but the flat plates of Comparative Examples were readily whitened. 0.05% by weight of tetrakis [methylene (3.5-di-t-butyl-hydroxyphenyl)propionate] methane, 0.05% by weight of calcium stearate and 0.35% by weight of dibenzylidene-sorbital were added to each of the resin compositions with the mixing ratios given in Table 1, and thoroughly mixed therewith. After the mixing, each of the resulting mixtures was extruded through a twin screw extruder, 40 mm in diameter, at 230°C and pelletized. The pellets were molded into flat plates, 10 cm x 12 cm and 2 mm thickness, through the same injection molding machine under the same molding conditions as above. The resulting flat plates were irradiated with γ-rays from the cobalt-60 source to evaluate irradiation resistance of the flat plates. At the same time, heat seal peel strength and HAZE were measured. The results are shown in Table 2. As is apparent from the foregoing Examples and Comparative Examples, the present thermoplastic resin compositions can give moldings having distinguished characteristics such as distinguished flexibility, impact strength, transparency, low temperature heat sealability, antistatic property, coatability, radiation resistance. Thus, it is expected that the present thermoplastic resin compositions are effectively utilized as various industrial materials, industrial packaging materials, food packing material, medical instrument materials, medicament packaging materials, cosmetic packaging material and polyvinyl chloride substitute materials. Examples 2-1 to 2-12 and Comparative Examples 2-1 to 2-3 Ethylenic copolymer EAA and EVOH, i.e. Soanol D, trademark of a product made by Nihon Gosei Kagaku K.K., Japan (EV-1) or Soanol A, trademark of a product made by Nihon Gosei Kagaku K.K., Japan (EV-2) were melt mixed in mixing ratio shown in Table 3 through a vent-type twin screw extruder, Type KTX-37, made by Kobe Seiko K.K., Japan, at 220°C to obtain thermoplastic resin compositions shown in Table 3. The thus obtained resin compositions were vacuum dried at 60°C for 24 hours and casted into films, 30 µm thickness, through a cast film molding machine, made by Yoshii Tekko K.K., Japan, at 220°C. The films were tested for oxygen permeability and film impact strength, and the results are shown in Table 3. The films of Examples 2-1 to 2-5 and Comparative Example 2-1 were also tested for flexural fatigue resistance, and the results are also shown in Table 3. The resin compositions of Examples 2-1 to 2-3 and Comparative Example 2-1 were molded into test pieces for measuring Izod impact strength and flexural modulus through a Minimat 24.80 g (7/8-ounce) injection molding machine, made by Sumitomo Juko K.K., Japan, at an injection temperature of 230°C and a mold temperature of 45°C. The test pieces were left standing in a thermo hygroset room at 23°C and a relative humidity of 50% for 7 days for state conditioning and tested for Izod impact strength (notched) and flexural modulus at 23°C and a relative humidity of 50%. The results are shown in Table 3. The resin compositions of Examples 2-4 and 2-5 were molded in test pieces in the same manner as above and the test pieces were likewise tested for izod impact strength (notched). It was found that the test pieces were not broken at all. The results are also shown in Table 3. Examples 2-13 to 2-18 and Comparative Examples 2-2 to 2-3 The respective components were melt mixed and pelletized in mixing ratios shown in Table 3 through a vent-type twin screw extruder, Type KTX-37, made by Kobe Seiko K.K., Japan, at 220°C to obtain thermoplastic resin compositions shown in Table 3. The thus obtained resin compositions were vacuum dried at 60°C for 24 hours and then casted into films, 30 µm thickness, through a cast film unit, made by yoshii Tekko K.K., Japan, at 230°C, and the films were tested for oxygen permeability and film impact strength. The results are shown in Table 3. Examples 2-19 to 2-21 Ethylenic copolymer EAA, EVOH, i.e. Soanol D (EV-1), and low density polyethylene (PO-1) as other thermoplastic resin were melt mixed in mixing ratios shown in mixing ratios shown in Table 3 through a vent-type twin screw extruder, Type KTX-37, made by Kobe Seiko K.K., Japan, at 220°C to prepare thermoplastic resin compositions shown in Table 3. The thus prepared resin compositions were vacuum dried at 60°C for 24 hours and casted into films, 30 µm thickness, through a cast film unit, made by Yoshii Tekko K.K., Japan, at 220°C, and the film were tested for oxygen permeability and film impact strength. The results are shown also in Table 3. The present thermoplastic resin compositions can give moldings having distinguished flexibility, impact strength and gas barrier property, as compared with the conventional saponification products of olefin-vinyl acetate copolymers, and thus are effective as food packaging materials, medicament packaging materials, cosmetic packaging materials, or compositions applicable to containers required for a good gas barrier property. Examples 3-1 to 3-12 and Comparative Examples 3-1 to 3-6 In Example 3-1, 81 parts by weight of homo PP (PO-3), 4.5 parts by weight of modified PP (MP-2), 9.5 parts by weight of EVOH (EV-4), i.e. Eval EP-F101 (EV-4), trademark of a product made by Kurarey K.K., Japan, and 5 parts by weight of ethylenic copolymer EAA (EA-1) were mixed in a tumbler, pelletized through a twin screw extruder, and then vacuum dried at 60° for 24 hours. Then, the pellets were charged into an extruder with a full-flight screw, L/D = 26 and compression ratio = 3, and molded into a sheet through a flat die, 250 mm wide, at a casting temperature of 170 to 230°C and a die temperature of 230°C. The sheet, 300 µm thickness, was wound onto a take-up roll continuously for 6 hours. The thus obtained sheet was uniform and a good compatibility, and no foreign matters of phase separation due to poor compatibility was observed. In Comparative Example 3-1, 85 parts by weight of homo PP (PO-3), 10 parts by weight of EVOH (EV-4) and 5 parts by weight of modified PP (MP-2) were mixed without EAA (EA-1) of Example 3-1, and a sheet was prepared from the resulting resin composition in the same manner as in Example 3-1. Right after the sheeting of the sheet, many foreign matters of uneven phase separation, not observed in Example 3-1, were found, and at the same time, dark brown molten resin was deposited and accumulated on the die lip increasingly with time. The appearance of the thus obtained sheet was quite poor due to the phase separation of EVOH, which was detected and confirmed by dipping the sheet in an ethanol solution containing 5% Methyl Red as a water-soluble dye. In Examples 3-1 to 3-12 and Comparative Examples 3-2 to 3-6, species of homo PP, EVOH, modified PP and EAA and their mixing ratios were changed from those of Example 3-1, as shown in Table 4, and sheeting was carried out in the same manner as in Example 3-1. Deposition state of the molten resin on the die lip during the molding and the film state of the resulting sheets were inspected. The results are shown in Table 4. Evaluation of the state of the sheets was made according to the following standard: A: Uniform and good compatibility without foreign matters of phase separation. No substantial deposition and accumulation of dark brown molten resins on the die lip during the sheeting. B: Uniform and good compatibility without foreign matter of phase separation. Some deposition and accumulation of dark brown molten resins on the die lip during the sheeting. C: Good compatibility partly with foreign matters of phase separation. A little more deposition and accumulation of dark brown molten resins on the die lip during the sheeting. D: Very poor compatibility with much foreign matters of phase separation. Much deposition and accumulation of dark brown molten resins on the die lip during the sheeting. The resin compositions of Examples 3-2, 3-3, 3-5, 3-7, 3-10 and 3-11, and Comparative Examples 3-2 to 3-6 were molded each into test pieces for measuring izod impact test and flexural modulus test through a Minimat 24.80 g (7/8-ounce), injection molding machine, made by Sumitomo Juko K.K., Japan, at an injection temperature of 230°C and a mold temperature of 45°C. Then, the test pieces were left standing in a thermo hygroset room at 23°C and a relative humidity of 50% for 7 days for state conditioning and then tested for Izod impact strength (notched) and flexural modulus under the same conditions as above. The results are shown in Table 4. As is apparent from the foregoing Examples and Comparative Examples, the present thermoplastic resin compositions have a much improved compatibility between EVOH, the resin containing PA and unsaturated dicarboxylic acid or its anhydride, and other thermoplastic resin.

Claims: A thermoplastic resin composition which comprises: (A) 90 to 1% by weight of a copolymer consisting of ethylene units, 0.01 to 50 % by weight of N-alkyl or N,N-dialkyl acrylamide units and/or N-alkyl or N,N-dialkyl methacrylamide units, and optionally, not more than 40% by weight of units of other polymerizable monomers, and (B) 10 to 99% by weight of a saponification product of an ethylene vinyl acetate copolymer containing 29 to 60 mol% of ethylene units. The thermoplastic resin composition according to claim 1, wherein the acrylamide derivative is one selected from N-alkyl acrylamide N,N-dimethylacrylamide and mixtures thereof. The thermoplastic resin composition according to claim 1 or 2, wherein the other polymerizable monomers are selected from ester compounds, acid compounds, ether compounds and hydrocarbons each having an unsaturated bond.

Inventors: IWASHITA TOSHIYUKI, MIYACHI OSAMU, TSUTSUMI KATSUAKI, WATANABE KAZUYUKI, IWASHITA, TOSHIYUKI, MIYACHI, OSAMU, TSUTSUMI, KATSUAKI, WATANABE, KAZUYUKI
Applicants: SHOWA DENKO KK, SHOWA DENKO KABUSHIKI KAISHA
Application year: 1993
Main classification: C08L101
IPC codes: B32B27, C08L51, C08L101, C08L77, C09J133, C08L33, C08L23, C09J123, C08L53