REGENERATING CHELATING TYPE ION EXCHANGE RESINS

Abstract: The use of chelating type cation exchange resins, particularly those with iminodiacetic acid functionality, to remove dissolved multivalent cations such as iron, zinc, and chromium from used autodeposition compositions permits reuse of the autodeposition compositions without the need for added surfactant and without developing any undesirable graininess or other texture in the coatings formed. The cation exchange resins can be efficiently regenerated with 0.5 to 4 % by weight aqueous hydrofluoric acid.

Description: Description REGENERATING CHELATING TYPE ION EXCHANGE RESINS BACKGROUND OF THE INVENTION Field of the Invention This invention relates to processes for separating from autodeposition compositions dissolved and/or dispersed metal ions having a valence of two or higher (this type of metal ions being briefly denoted hereinafter as "multival¬ ent") , particularly iron, chromium, and/or zinc cations. The invention also relates to regenerating to their acid form chelating type cation exchange resins, particularly those containing iminodiacetic acid functional groups, after the cation exchange resins have been at least par¬ tially loaded with multivalent metal cations, particularly with iron, chromium, and/or zinc cations. In one embod¬ iment of particular interest, the invention relates to re- generating such ion exchange resins that have been used to remove iron, chromium, and/or zinc cations from autodeposi¬ tion baths. Statement of Related Art Autodeposition involves the use of an aqueous resinous coating composition of relatively low solids concentration (usually less than about 10 %) to form a coating of rela- tively high solids concentration (usually greater than about 10 %) on a metallic surface immersed therein, with the coating increasing in thickness and areal density (i.e., mass per unit area of coating) the longer the time the metallic surface is immersed in the composition. Auto- deposition is somewhat similar to electrodeposition but does not require the aid of external electrical current to cause the resin particles to deposit on the metal surface. In general, autodepositing compositions are aqueous acid solutions having solid resin particles dispersed therein in very finely divided form. The coating formed while the metal substrate used is immersed in the bath is generally wet and fairly weak, although sufficiently strong to maintain itself against gravity and moderate spraying forces. In this state the coating is described as "un- cured". To make an autodeposition coated object suitable for normal practical use, the uncured coated is dried, usu¬ ally with the aid of heat. The coating is then described as "cured". Basic constituents of an autodepositing composition are water, resin solids dispersed in the aqueous medium of the composition, and activator, that is, an ingredient or ingredients which convert the composition into one which will form on a metallic surface a resinous coating which increases in thickness or areal density as long as the surface is immersed in the composition. Various types of activators or activating systems are known. The activating system generally comprises an acidic oxidizing system, for example: hydrogen peroxide and HF; HN0 3 ; a ferric ion con¬ taining compound and HF; and other combinations of (i) sol- uble metal containing compounds such as, for example, sil¬ ver fluoride, ferrous oxide, cupric sulfate, cobaltous ni¬ trate, silver acetate, ferrous phosphate, chromium fluor- ide, cadmium fluoride, stannous fluoride, lead dioxide, and silver nitrate, in an amount between about 0.025 and about 50 grams per liter (hereinafter often abbreviated as "g/L"), with (ii) one or more acids such as hydrofluoric, sulfuric, hydrochloric, nitric, and phosphoric acids and organic acids such as, for example, acetic, chloroacetic, and trichloroacetic acids. The use of autodeposition to coat metal objects con¬ taining iron, chromium, and/or zinc causes some dissolution of the objects and therefore increases the concentrations of one or more of these ions in the coating bath. Such increased concentrations of these ions, if sufficiently large, causes the baths to produce unsatisfactory coatings or even to coagulate and become unusable. Removal of these accumulating metal ions is therefore necessary to permit prolonged satisfactory use of an autodeposition bath. U. S. Patent 3,839,097 of Oct. 1, 1974 to Hall et al. teaches the stabilization of autodeposition baths by remov¬ ing metal ions therefrom with an ion exchange resin, then regenerating the ion exchange resin by treating it with an aqueous solution of a strong acid. The entire spec¬ ification of this patent, to the extent not inconsistent with any explicit statement herein, is hereby incorporated into this specification by reference. Sulfuric, phos- phoric, hydrochloric, and nitric acids are specifically recommended in this reference, with 20 % by weight sulfuric acid apparently highly preferred, based on its use in all the examples in which regeneration is described. Similar¬ ly, although several types of ion exchange resins are taught by this reference as suitable, only sulfonic acid type resins are used in working examples. This reference teaches that removal of metal cations from an autodeposi¬ tion bath by use of a cation exchange resin should be sup¬ plemented by addition of surfactant to the bath, in order to maintain very long term stability and avoid the devel¬ opment of a grainy or textured appearance of the coatings formed by the bath on metal substrates after the bath has been in contact with a cation exchange resin. The general use of ion exchange resins has been re¬ viewed by R. E. Anderson in Section 1.12, "Ion-Exchange Separations", in P. A. Schweitzer (ed.). Handbook of Sepa- ration Techniques for Chemical Engineers (McGraw-Hill, New York, 1979) . I inodiacetic acid resins in particular are described on pages 1-384 - 1-385 in this reference. A published product Bulletin, Ion Exchange Resins AMBERLITE* IRC-718 (Rohm & Haas Co., Philadelphia, 1988), is believed to be typical of current manufacturers' recom¬ mendations for use and regeneration of commercial iminodi¬ acetic acid functional resins. This shows that, at pH 2, ferric iron ions are the most tightly bound to this resin of all commonly occurring cations and states that, for regeneration, "the amount of acid required is higher than that required for conventional weakly acidic ion exchange resins. A regeneration level of 6 to 10 lbs. HCl/ft 3 may be sufficient for metals with moderate selectivity, but this should be increased slightly for tightly held metals. ... Acid concentration should be 5 to 15 percent, with higher concentrations needed for more tightly bound species." Published Canadian Patent Application 2,017,026 de¬ scribes extraction of iron and other metals from electro¬ deposition baths using iminodiacetic acid type ion exchange resins. This reference teaches (page 5) that the resins may be regenerated with 20 % by weight sulfuric acid solu¬ tion in water, but otherwise devotes little attention to the regeneration step. U. S. Patent 4,303,704 of Dec. 1, 1981 to Courduvelis et al. teaches removing complexed copper or nickel from aqueous solutions by passage through a bed of iminodiacetic acid type ion exchange resin. This teaches that, "Prefer¬ ably, a 0.5 to 20 % solution of sulfuric acid or other strong acid is used as the eluent." Japanese Laid Open Application No. 54-24,283, accord¬ ing to an abstract thereof, teaches regenerating ion ex¬ change resins suitable for removing iron compounds from aqueous solutions, using as regenerant an aqueous solution of an aminopolycarboxylic acid, such as hydroxyethylethyl- ene-diaminetriacetic acid, nitrilotriacetic acid, cyclo- hexanediaminetetraacetic acid, or a water soluble salt of such an acid. DESCRIPTION OF THE INVENTION Except in^the claims and the operating examples, or where otherwise expressly indicated, all numerical quant¬ ities in this description indicating amounts of material or conditions of reaction and/or use are to be understood as modified by the word "about" in describing the broadest scope of the invention. Practice within the exact numeri¬ cal limits stated is generally preferred. Objects of the Invention One object of this invention is to provide an improved means for separating multivalent metal cations, particular¬ ly iron, zinc, and/or chromium cations, from autodeposition baths (an alternative term for autodeposition compositions) that have been used to coat active metal objects that in- troduce such metal cations into the baths, in order to per¬ mit prolonged use of the autodeposition baths by replacing their content of resin and other components that are actu¬ ally incorporated into the autodeposited coatings formed by the baths or are consumed by the chemical reactions that accompany formation of the autodeposited coatings. Another object of the invention is to provide a more economical method of regenerating cation exchange resins, especially chelating type cation exchange resins, more particularly those with iminodiacetic acid functional groups, after the cation exchange resins have been loaded with metal ions of one or more of the types strongly bound by the resins. Still another object is to provide a method of regenerating cation exchange resins that will substantially reduce or eliminate the introduction of unwanted chemical species into autodeposition baths that are subsequently contacted with the regenerated cation exchange resins. Other objects will become apparent from the description below. Summary of the Invention It has surprisingly been discovered that when chelat- ing type cation exchange resins are used to remove iron, chromium, and/or zinc cations from used autodeposition baths, especially those in which hydrofluoric acid is the principal source of acidity, there is no need for addition of surfactant to prevent the development of a grainy and/or textured appearance of the objects subsequently coated with the reused baths. More specifically, one preferred embod- iment of the invention is a process comprising steps of: (I) contacting a metal surface selected from the group consisting of ferriferous and zinciferous metal sur¬ faces with an autodeposition composition comprising water and: (A) from 5 to 550, more preferably from 30 to 300, still more preferably from 40 to 120, and most preferably from 40 to 80, g/L of a stably dis¬ persed organic coating resin; (B) from about 0.4 to about 5, more preferably from 0.5 to 4.0, still more preferably from 1.0 to 3.0, g/L of fluoride ions; (C) an amount sufficient to provide from about 0.010 to about 0.20, more preferably from 0.011 to 0.09, still more preferably from 0.012 to 0.045, oxidizing equivalents per liter of an oxidizing agent selected from the group consisting of di- chro ate, hydrogen peroxide, ferric ions, and mixtures thereof; and (D) a source of hydrogen ions in an amount sufficient to impart to the autodeposition composition a pH in the range from 1.6 to 3.8, more preferably from 1.7 to 3.0, still more preferably from 1.8 to 2.5, said contacting being continued for a sufficient time that the metal surface contacted is covered with a film containing the organic coating resin, said film being sufficiently adherent to the metal surface to resist flowing off under the inf]uence of gravity when the coated metal surface is removed from contact with the autodeposition composition and forming a smooth coating on the metal surface after drying thereon; (II) contacting at least 30 %, more preferably at least 55 %, still more preferably at least 90 %, of the total volume of the autodeposition bath from the end of step (I)iwith a sufficient amount of an acid form chelating cation exchange resin to transfer from the autodeposi- tion bath to the ion exchange resin at least part of the total content of dissolved iron, chromium, and zinc cations in the autodeposition bath and substitute an amount equivalent thereto of dissolved hydrogen ions in the autodeposition bath; and (III) contacting the autodeposition bath from the end of step (II) ^without adding additional surfactant there¬ to,^with additional metal surface selected from the group consisting of ferriferous and zinciferous metal surfaces, so as to form on the additional metal sur- faces a coating that is smooth after drying. Also surprisingly, it has been discovered that at least zinc and iron cations can be more efficiently removed from cation exchange resins by relatively dilute sulfuric acid, hydrochloric acid and, most preferably, hydrofluoric acid regenerants, than by more concentrated and/or stronger acid regenerants, when efficiency is measured by the ratio of equivalents of multivalent ions displaced from the load¬ ed ion exchange resin to the equivalents of hydrogen ions present in the volume of regenerant used. More specifically, a second preferred embodiment of the invention is a process comprising steps of: (I) providing a wet bed of iminodiacetic acid cation ex¬ change resin containing between 0.10 and 0.30 milli- moles per milliliter of wet resin bed volume of a to- tal of iron, chromium, and zinc cations bound thereon by exchange from a solution earlier contacted with the cation exchange resin predominantly in its acid form. SUBSTITUTE SHEET ^ ISA/EP the volume being measured when the bed of resin in it* sodium form has settled to its equilibrium volume under the influence of natural gravity and mild mechanical agitation, in the absence of any flow of liquid through the bed; and the liquid with which the bed is wet being formed by washing the bed with from 0.5 to 4, more preferably with from 1 to 3, total bed volumes of deionized water after the passage of any other liquid through the bed; and adding to the top of the wet bed provided in step (I) a volume of an aqueous acidic regenerant liquid con¬ sisting essentially of water and an acid component selected from the group consisting of sulfuric acid, hydrofluoric acid, hydrochloric acid, and mixtures thereof, so as to cause a volume of eluted liquid equal to the volume of regenerant liquid added to flow from the bottom of the wet bed, the volume and compo¬ sition of the regenerant liquid being selected so as to satisfy at least one of the following two sets of conditions: (A) the total volume of eluted liquid contains at least 0.080 millimoles per milliliter of wet resin bed volume of a total of iron, chromium, and zinc cations dissolved therein and the total moles of iron, chromium, and zinc cations displaced from binding to the cation exchange resin into the total volume of eluted liquid is at least equal to 0.070 times the number of equivalents of acid in the total volume of regen- erant liquid added to the wet bed; (B) the total volume of eluted liquid contains at least 0.016 millimoles per milliliter of wet resin bed volume of a total of iron, chromium, and zinc cations dissolved therein and the total moles of iron and zinc cations displaced from binding to the cation exchange resin into the total volume of eluted liquid is at least equal to 0.025 times the number of equivalents of acid in the total volume of regenerant liquid added to the wet bed. The description immediately above, and other detailed descriptions below, of the processes of using and regener¬ ating a bed of ion exchange resin are based on an assump¬ tion that traditional methods of causing liquid to flow through such a bed in one direction only, except for occas¬ ional backflushing, would be used. However, it is recog- nized that some more modern practice involves flowing the liquid of major interest to be exchanged, the autodeposi¬ tion bath in this instance, in one direction through the bed and the regenerant liquid in the opposite direction - a method often denoted by the word "countercurrent". Operation in this manner is also within the intended scope of the invention, and the above detailed description, with changes in detail having been made in a manner known to those skilled in the art, will also describe such counter- current operation of a process according to the invention. In autodeposition baths to be used for coating ferrif¬ erous and/or zinciferous surfaces, it is preferred, with increasing preference in the order given that the baths contain a total of no more than 1, 0.3, 0.1, 0.05, 0.009, or 0.004 g/L of anions other than fluoride and surfactant anions. If any acid other than hydrofluoric acid, or any regenerant composition that contains any substantial amount of anions other than fluoride, is used to regenerate a cation exchange resin used to separate multivalent cations from such autodeposition baths, there is danger of contamination of the bath. Accordingly, a third preferred embodiment of the invention is a process comprising steps of: (I) contacting a metal surface selected from the group consisting of ferriferous and zinciferous metal sur- faces with an autodeposition composition comprising not more than 1 g/L in total of anions other than fluoride and surfactant anions, said contacting being continued for a su ficient time that the metal surface or surfaces contacted are covered with a film contain¬ ing the organic coating resin, said film being suf¬ ficiently adherent to the metal surface to resist flowing off under the influence of gravity when the coated metal surface is removed from contact with the autodeposition composition and forming a smooth coat¬ ing on the metal surface after drying thereon; (II) contacting at least 30 %, more preferably at least 55 %, still more preferably at least 90 %, of the total volume of the autodeposition bath from the end of step (I) with a sufficient amount of an acid form cation exchange resin to transfer from the autodeposition bath to the cation exchange resin at least part of the total content of dissolved iron, chromium, and zinc cations ' in the autodeposition bath and substitute an amount equivalent thereto of dissolved hydrogen ions in the autodeposition bath; (III) separating the cation exchange resin used in step (II) from the autodeposition bath contacted with said cation exchange resin in step (II) ; (IV) contacting the separated cation exchange resin from step (III) with an aqueous acidic liquid consisting essentially of water and hydrofluoric acid in suf- ficient quantity for a sufficient time to displace at least a part of the multivalent metal ions therefrom and thereby regenerate the exchange capacity of the cation exchange resin; and (V) contacting an autodeposition bath comprising cations selected from the group consisting of iron, chromium, and zinc cations and not more than 1 g/L in total of anions other than fluoride and surfactant anions with the regenerated acid form cation exchange resin from step (V) for a sufficient time to transfer from the autodeposition bath to the ion exchange resin at least part of the content of dissolved iron, chromium, and zinc cations in the autodeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodeposition bath; and, optionally, (VI) contacting the autodeposition bath from the end of step (V) with a metal surface selected from the group consisting of ferriferous and zinciferous metal surfaces for a sufficient time that the metal surface contacted is covered with a film containing the organic coating resin, said film being sufficiently adherent to the metal surface to resist flowing off under the influence of gravity when the coated metal surface is removed from contact with the autodeposition composition and forming a smooth coating on the metal surface after drying thereon. The combination of these discoveries permits a very efficient and economical recycling of the autodeposition baths. Brief Description of the Drawings Figures 1 - 3 are all graphs illustrating some import¬ ant characteristics of some specific cation exchange resin regeneration processes according to the invention and other specific regeneration processes according to prior art. Description of Preferred Embodiments The preferred type of ion exchange resin for use with this invention is one having iminodiacetic acid functional groups. Suitable commercial examples include AMBERLITE* IRC-718, described by its supplier as having a "macroretic- ular" structure; LEWATIT™ TP-207, described by its supplier, Mobay Corp, as "macroporous"; and PUROLITE™ S- 930, also described as "macroporous" by its supplier, Purolite Company. It is expected that other products of the same type would be equally satisfactory. Cation exchange resins such as those described above are commonly supplied commercially in the sodium form. Be¬ fore using them in a process according to this invention for extracting multivalent metal ions from autodeposition baths, it is highly preferred to convert them into the acid form, in order to avoid the generally undesired introduc- tion of sodium ions into the baths. This conversion to the acid form may be accomplished by means known per se in the art, for example by treatment with any adequately strong acid. After conversion to the acid form, it is preferred to rinse the acid form resin with water, preferably deionized, distilled, or otherwise purified water, before using it for extracting multivalent metal ions from an autodeposition bath, even if the acid used to put the ion exchange resin into the acid form is the same as the one used in the auto¬ deposition composition to be treated with the bath. The reason for this preference is that experience has shown that the amount of acid remaining in contact with a wet bed Of acid form ion exchange resin, when practical concentra- tions of aqueous acid are used to put the ion exchange resin into acid form, is usually in excess of the amount needed to regenerate the autodeposition composition to be contacted with the acid form ion exchange resin for removal of multivalent metal ions. Therefore, if there is no rinsing before using the acid form ion exchange resin, more acid than is needed will be introduced into the autodeposition composition, so that it will eventually become unsuitable for use for that reason.. It is also preferred to use the same acid(s) as used in the autodeposition composition to be treated for con¬ verting the ion exchange resin to acid form, or for regen¬ erating it after use, in order to avoid introduction into the autodeposition bath of any substantial amounts of an¬ ions other than those originally present in the autodepo- sition bath. As with other uses of ion exchange resins, it is generally preferred with this invention to use the ion exchange resins in the form of a bed formed by settling of the beads or particles of resin as supplied by the manu- facturer into a container with sidewalls impervious to liquids but a bottom at least partially pervious to liquids. Gentle tapping or vibration of the container is generally used to help the formation of a desirably compact bed of the ion exchange resin. Liquids, such as the auto¬ deposition composition, that contain cations to be removed are passed through such beds until some desired fraction of the capacity of the resin for the ions to be removed is reached. A regenerant acid liquid is then passed through the bed, and after enough of the multivalent metal cations have been displaced, the ion exchange resin bed is ready for use again to remove multivalent metal ions. Ordinarily it is preferred to rinse the bed of ion exchange resin with water, preferably with deionized, distilled, or other puri¬ fied water, between each of these stages of use of the bed. The rinses and eluates from the various stages may advan¬ tageously be at least partially recycled for use in a manner known per se, and some cases it may be possible to eliminate some of the intermediate rinses by control of the concentrations of regenerants and other liquid compositions used, for example, so that the amount of acid remaining in equilibrium with the ion exchange resin after regenerating the resin corresponds sufficiently closely to the amount needed to replenish the autodeposition bath. The total volume of cation exchange resin used in a process according to this invention is measured when, needed by allowing the resin particles in their sodium form, wet with a suitable liquid, to settle into a bed in a container under the influence of natural gravity and gentle tapping or vibration of the container, and then discontinuing any net flow of liquid through the bed. The minimum bulk con¬ tainer volume required to contain the amount of ion ex- change resin used under such conditions is taken as the volume of the ion exchange resin for purposes of any quantitative descriptions of the volume of ion exchange resin herein. The conditions and compositions used for coating metal substrates by autodeposition in a process according to this invention are generally those already known in the art. Specific preferred conditions are described below. One preferred type of coating resin for use in forming autodeposited coatings in a process according to the pres¬ ent invention comprise internally stabilized vinylidene chloride copolymers or externally stabilized vinylidene chloride copolymers containing in excess of 50 percent by weight (hereinafter "w/o") , or more preferably at least 80 w/o, of residues from polymerizing vinylidene chloride. Most preferably, the vinylidene chloride copolymer is crys¬ talline in nature. Exemplary crystalline resins are de- scribed in U.S. Patents 3,922,451 and 3,617,368. Generally speaking, crystalline poly{vinylidene chloride) containing resins comprise a relatively high proportion of residues from vinylidene chloride, for example, at least about 80 % by weight thereof. A preferred working autodepositing bath containing a commercially available poly(vinylidene chloride} resin has ' the following composition, designated Bath Composition I: Amount (in Grams, 100% Ingredient Active Ingredients Basis) Vinylidene chloride-acrylonitrile- butyl acrylate copolymer latex 50.00 Dodecyl diphenyloxide disulfonate surfactant 0.14 Colloidal carbon black pigment 1.88 Ferric fluoride 3.00 Hydrofluoric acid 1.40 Deionized water - balance to make one liter of bath. Examples of latexes for suitable use in the composition are commercially available and include the SERFENE* latexes available from Morton Chemical, DARAN* 112 and DARAN* SL 143 available from . R. Grace, 76 RES 5517 available from Unocal and the HALOFLEX* latexes such as, for example, HALOFLEX* 202 available from Imperial Chemicals Industries. Examples of colloidal carbon black pigment dispersions for suitable use in the composition include RAVEN BLACK* 1035 available from Columbian Chemicals Co. , T-2166A available from ABCO Enterprises, Inc., AQUABLACK* 255 and AQUABLACK* 115A available from Borden Chemical Co. A second preferred type of resin for use in autodepo¬ sition coating in connection with this invention is the acrylic type, particularly copolymers of acrylonitrile. A preferred working autodepositing bath containing a commer- cially available acrylic resin has the following composi¬ tion, designated Bath Composition II: Amount (in Grams, 100% Ingredient Active Ingredients Basis) Acrylic resin latex 58.00 Dodecyl diphenyloxide disulfonate surfactant 0.14 TEXANOL™ 12.20 Colloidal carbon black pigment 1.88 Ferric fluoride 3.00 Hydrofluoric acid 1.40 Deionized water - balance to make one liter of bath. Examples of commercially available latexes for suitable use in the composition include NACRYL C« 78-6334 and NACRYLIC* 78-6408 from National Starch Cc. : NEOACRYL* A-640 from Imperial Chemicals Industries; RHOPLEX* L-91 and RHOPLEX* B-85 from Rohm and Haas Co.; 76 RES 1018 from Unocal. Examples of colloidal carbon black are the same as those listed above. TEXANOL™ is available from Eastman Chemical Products, Inc. and is reported by its supplier to consist substantially of 2,2,4-trimethyl-l,3-pentanediol monoiso- butyrate. Preferably the concentration of dissolved iron, which is usually in the ferric form in autodeposition composi¬ tions of the preferred type, should not be allowed to be- come greater than 4, or more preferably not greater than 2.0 g/L during the operation of a process according to this invention; the concentration of dissolved zinc cations should not be allowed to become greater than 3, or more preferably not greater than 1.0, g/L during the operation of a process according to this invention; and the concen¬ tration of dissolved chromium cations should not be allowed to become greater than 2, or more preferably not greater than 0.5, g/L during the operation of a process according to this invention. Maintenance of dissolved multivalent cation levels below their desired limits can be assured by contacting the entire autodeposition composition, or usual¬ ly more conveniently a part of it within a given time in- terval, with an acid form cation exchange resin and then returning the thus "purified" autodeposition composition for use in coating additional metal surfaces. Means of ac¬ complishing such purification processes batchwise or con¬ tinuously are generally known in the art and will not be considered in detail here. Instead, the focus will be on the major point of novelty of the present processes, the use and regeneration of cation ion exchange resins, prefer¬ ably those of the chelating type, particularly the highly preferred iminodiacetic acid type. When any fixed volume of a cation exchange resin is contacted with increasing volumes of a specified liquid composition containing exchangeable cations, the volume of cation exchange resin will eventually become saturated with the exchangeable ions and will no longer remove any such ions from any additional volume of the specified liquid composition until the ion exchange resin is regenerated by contact with a regenerant liquid containing ions of a dif¬ ferent type from those exchanged with the first specified liquid composition. The amount of cations per unit volume of resin present after such saturation of the ion exchange resin is generally known in the art as the "saturation ca¬ pacity" of the resin, in contrast to a "working capacity" that depends on how an actual process is operated. The saturation capacity is often assumed, particularly when dealing with relatively simple solutions such as natural waters to be softened or otherwise purified, to be inde¬ pendent of the composition used to load the resin. In fact, however, the saturation capacity of an ion exchange resin for a particular type or mixture of types of cations often depends on the liquid composition used to load it with these cations. In connection with this process, it is particularly important to note that the capacity values specified below must be defined in connection with the autodeposition composition used with the exchange resin, as it has been found that the actual capacities of the ion exchange resins for iron and zinc in particular can be substantially lower than the nominal values given by manufacturers of the exchange resins, these manufacturers' values being normally based on sodium exchange, when the capacity is determined with actual used or simulated used autodeposition compositions. The saturation capacity of iminodiacetic acid resins in particular is very sensitive to pH of the solutions used to load the resins with multi¬ valent ions. When the ion exchange resin used in a process accord¬ ing to this invention has been loaded to a point within the range of from 50 - 99, more preferably from 75 - 95, or still more preferably from 75 to 90, percent of its saturation capacity for the ions that are desired to be removed from the autodeposition compositions used in the same process according to the invention, the ion exchange resin is ready for the regeneration step of the process. Alternatively, when compositions and other operating parameters have been sufficiently reliably established by experience with particular autodeposition compositions and loads of substrate surfaces to be coated, and the ion exchange resin is used in a bed as described above, regeneration can be based on the number of bed volumes of used autodeposition composition passed through the bed of ion exchange resin. The practice of the invention may be further appreci- ated from the following working examples. Examples and Comparison Examples Group 1 The following laboratory tests were carried out in an attempt to determine the optimum conditions for regenera¬ tion. A large sample of AMBERLITE* IRC-718 cation exchange resin was saturated with iron by passing through it 10 bed volumes of a simulated used autodeposition composition having the same ingredients as Bath Composition I already given above, except that the amount of ferric fluoride was increased to give a concentration of 2 g/L of iron cations. The resin thus loaded was then rinsed with deionized water until the effluent was free of visible latex. The solution in the wet bed was sampled and found to contain 0.060 g/L of iron. The resin contained 0.13 millimoles of iron per milliliter (hereinafter abbreviated "ml") of resin, as measured by the maximum amount that could be eluted with any of the acids described below. Samples of 60 - 61 ml of this loaded and rinsed resin were then placed in a conventional lab container for ion exchange resins to give a bed depth of 45 centimeters and subjected to successive elution with six successive incre¬ ments, of 20 ml volume per increment, of the nine specified regenerant acid compositions as follows: 0.25, 1.0, and 5.20 N aqueous solutions of each of sulfuric, hydrochloric, and hydrofluoric acids. (In calculating the normalities, sulfuric acid was assumed to ionize both protons completely and hydrofluoric and hydrochloric acids to ionize their protons completely.) The effluents from the columns after each such incre¬ ment were collected and analyzed for iron content by atomic absorption spectroscopy. The amounts of iron found were corrected for the amount present in the liquid in which the ion exchange resin was immersed; the correction factors were determined in a control experiment by measuring the amount of chloride ions eluted from fresh ion exchange resin in the sodium form, immersed in deionized water, in a bed of the same size by 1.0 N aqueous NaCl solution, and calculating therefrom the fraction of the eluate in each increment that was derived from the eluant rather than ' from the solution in contact with the ion exchange resin in the wet bed. The fraction of eluate derived from the eluant was thereby determined to be 0.0 for the first increment, 0.12 for the second increment, 0.92 for the third incre¬ ment, and 1.0 for all subsequent increments. The cumulated amounts of regenerated iron determined as above after each increment of eluant were plotted against the cumulated number of millimoles of acid in the amount of eluant used to produce Figures 1 - 3. Certain features of these Figures are illustrated in Table 1. TABLE 1 Eluant Composition Ratio of Millimoles of Iron Regenerated to Millieguivalents of Acid in Eluant Vol "u"me Used After 1 Millimole of Iron Total Has Been Eluted 5.2 N H 2 S0 4 0. 026 5.2 N HC1 0. 021 5. 2 N HF 0. 021 1. 0 N H 2 S0 4 0. 026 1. 0 N HC1 0. 036 1. 0 N HF 0.036 0.25 N H 2 S0 A < 0. 03* 0.25 N HC1 0. 051 0.25 N HF 0.065 After 5 Millimoles of Iron Total Has Been Eluted 5. 2 N H 2 S0 4 0. 036 5. 2 N HC1 0. 012 5.2 N HF 0.028 1. 0 N H 2 S0 4 0. 062 1. 0 N HC1 0. 086 1.0 N HF 0.079 ♦Value extrapolated from actual data. The Figures and the data in Table 1 show that, con¬ trary to normal expectations, the regeneration is more ef¬ ficient with either 0.25 or 1 N acids than with the same acids at 5.2 N and, also contrary to expectations and the teachings of the most relevant prior art, hydrochloric and hydrofluoric acids can be, and at relatively low concen- trations are, more efficient than sulfuric acid, even though hydrofluoric acid is known not to be nearly as "strong" an acid as sulfuric or hydrochloric because of its lower ionization constant. As already noted above, it is preferred to formulate the autodeposition composition in most cases with hydro¬ fluoric acid as the only acid constituent, and in such cases, it is preferred to use hydrofluoric acid as the regenerant, in a concentration of from 0.5 to 4 w/o, or more preferably from 1 - 2.5 w/o. (For comparison, 1 N HF is very close to 2 % by weight. Examples Group 2 In each of the tests in this group, a bed of 60 - 61 ml of LEWATIT™ TP-207, PUROLITE™ S-940, or AMBERLITE β 2.00 sodium form cation exchange resin was loaded into a 45 centimeter deep bed, and then subjected to the following steps: 1. Convert to acid form with 500 ml of 17 % aqueous sulfuric acid passed through the bed. 2. Rinse with 500 ml of deionized water. 3. Rinse with 200 ml of 5 % aqueous hydrofluoric acid. 4. Rinse with 250 ml of deionized water. 5. Load by flowing through about 900 ml of an autodeposi¬ tion composition that was the same as Bath Composition I described above except that it also contains suffi¬ cient dissolved zinc fluoride to produce a concentra¬ tion of 0.3 g/L of zinc cations, or alternatively with Bath Composition I itself. 6. Rinse with 2 bed volumes of deionized water. 7. Regenerate with 3 bed volumes of 1 % or 10 % aqueous hydrofluoric acid or with 2 or 20 % aqueous sulfuric acid. 8. Rinse with 2 bed volumes of DI water. The effluents from the ion exchange resin bed were analyzed to determine the amounts of iron and zinc retained on the ion exchange resin and subsequently eluted. Some results obtained with the autodepositing composition containing zinc and with 10 % hydrofluoric acid regenerant are shown in Table 2. Notes for Table 2 S-940 Resin has phosphonic acid functional groups; AMBERLITE* 200 has strong (sulfonic acid) functional groups. The data in Table 2 show that sulfonic acid type resins are most efficient in binding both iron and zinc, but are relatively difficult to regenerate with ydro- fluoric acid, especially for zinc. The phosphonic acid resins are very hard to regenerate from bound iron with 10 % hydrofluoric acid. When Bath Composition I (without zinc) was used, along with both dilute and concentrated hydrofluoric and sulfuric acids and the AMBERLITE* 200 sulfonic acid type resin, the results were notably different. With 10 % HF, about 71 % of the bound iron was eluted with 2 bed volumes of acid, while with 20 % sulfuric acid, about 68 % of the bound iron was eluted with the same volume of acid regenerant. With 2 bed volumes of 1 % HF regenerant, over 90 % of the bound iron was eluted, even though this regenerant contained only one-tenth as many protons as the 10 % HF which eluted less. On the other hand, when 2 % H 2 S0 2 was the regenerant, only about 35 % of the bound iron was eluted with 2 bed volumes of regenerant. Thus, with strong acid cation exchangers as well as the chelating weak acid ones, hydrofluoric acid can be more effective than a strong acid such as sulfuric in eluting the bound iron. Examples Group 3 A volume of 19 liters of an autodeposition bath having the same composition as Bath Composition I as defined above, except that the amount of ferric fluoride was in- creased to give an iron cation concentration of 2.2 g/L, was prepared and passed through a bed with a volume of 1.9 liters of AMBERLITE* IRC-718, iminodiacetic acid cation exchange resin, in its acid form, so as to reduce the concentration of iron in the autodeposition bath to 1.7 g/L. The autodeposition composition that had passed through the cation exchange resin was then used to coat several test panels that aggregated to about 1 square meter of total steel surface. The ion exchange resin was rinsed with 0.8 bed volumes of deionized H 2 0, regenerated with 1.5 bed volumes of 10% HF, rinsed with 1.6 bed volumes of deionized H 2 0, and backflushed with deionized H 2 0 at 4.9 eter/hr. for 10 minutes. The above sequence of steps was repeated ten times with the same cation exchange resin, thereby demonstrating that the exchange capacity of the resin did not diminish with this amount of use which amounted to passage of 100 bed volumes of autodeposition bath through the ion exchange bed. After each repetition, the quality of coating produced was evaluated by conventional salt spray and scab corrosion tests, and the surface quality produced was visually evaluated. There was no deterioration in the corrosion test results after any of the ten repetitions, and no development of grainy or textured surface such as reported under similar conditions of iron removal in U. S. Patent 3,839,097. What is claimed is:

Claims: CLAIMS 1. A process comprising steps of: (I) contacting a metal surface selected from the group consisting of ferriferous and zinciferous metal sur- faces with an autodeposition composition comprising water and: (A) from about 5 to about 550 g/L of a stably dis¬ persed organic coating resin; (B) from about 0.4 to about 5 g/L of fluoride ions; (C) an amount sufficient to provide from about 0.01 to about 0.2 oxidizing equivalents per liter of an oxidizing agent selected from the group con¬ sisting of dichromate, hydrogen peroxide, ferric ions, and mixtures thereof; and (C) a source of hydrogen ions in an amount sufficient to impart to the autodeposition composition a pH in the range from about 1.6 to about 3.8, said contacting being continued for a sufficient time that the metal surface contacted is covered with a film containing the organic coating resin, said film being sufficiently adherent to the metal surface to resist flowing off under the influence of gravity when the coated metal surface is removed from contact with the autodeposition composition and forming a smooth coating on the metal surface after drying thereon; (II) contacting at least 30 % of the total volume of the autodeposition bath from the end of step (I) ι with a sufficient amount of an acid form chelating cation exchange resin to transfer from the autodeposition bath to the ion exchange resin at least part of the content of dissolved iron, chromium, and zinc cations in the autodeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodeposition bath; and (III) contacting the autodeposition bath from the end of step (II) ,^without adding additional surfactant there¬ to,^ with additional metal surface selected from the 23 SUBSTITUTE SHEET 1SA/EP group consisting of ferriferous and zinciferous metal surfaces, so as to form on the additional metal sur¬ faces a coating that is smooth after drying. 2. A process according to claim 1, comprising additional s steps of: (IV) separating the cation exchange resin used in step (II) from the autodeposition bath contacted with said cat¬ ion exchange resin in step (II) ; (V) contacting the separated cation exchange resin from o step (IV) with an aqueous acidic liquid in sufficient quantity for a sufficient time to displace at least a part of the multivalent metal ions therefrom and thereby regenerate the exchange capacity of the cation exchange resin; and s (VI) contacting an autodeposition bath containing cations selected from the group consisting of iron, chromium, and zinc cations with the regenerated acid form cation exchange resin from step (V) for a sufficient time to transfer from the autodeposition bath to the ion 0 exchange resin at least part of the content of dis¬ solved iron, chromium, and zinc cations in the auto¬ deposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodepo¬ sition bath. . process accor ng o c a m , w ere n e re a¬ tive amounts of autodeposition composition and of acid form chelating ion exchange resin used in step (II) are such that at the end of step (II) the amount of the total of bound iron, chromium, and zinc cations per unit volume of the ion exchanged resin is at least 75 % of the total amount of bound iron, chromium, and zinc cations per unit volume of the ion exchanged resin that would result from contact between the same amount of the ion exchange resin and any larger volume of the autodeposition composition; (ii) the relative amounts of the acid and of the chelating ion exchange resin used in step (V) are such that at the end of step (V) the amount of the total of bound iron, chromium, and zinc cations per unit volume of the ion exchanged resin is not more than 40 % of the total amount of bound iron, chromium, and zinc cations per unit volume of the ion exchange resin that would result from contact between the same amount of the cation exchange resin and a volume of the autodeposition composition used at the begin- ning of step (II) that is one hundred times larger than the volume of the cation exchange resin; and (iii) in the auto¬ deposition composition, the concentration of stably dis¬ persed organic coating resin is from 40 - 120 g/L, the concentration of fluoride ions is from 0.5 to 3.0 g/L, the concentration of oxidizing equivalents per liter is from 0.011 to 0.09 and is selected from the group consisting of hydrogen peroxide, ferric ions, and mixtures thereof, and the pH is from 1.7 to 3.0. 4. A process according to claim 3, wherein (i) the rela¬ tive amounts of autodeposition composition and of acid form chelating ion exchange resin used in step (II) are such that at the end of step (II) the amount of the total of bound iron, chromium, and zinc cations per unit volume of the ion exchanged resin is at least 90 % of the total amount of bound iron, chromium, and zinc cations per unit volume of the ion exchanged resin that would result from contact between the same amount of the ion exchange resin and any larger volume of the autodeposition composition; (ii) the relative amounts of the acid and of the chelating ion exchange resin used in step (V) are such that at the end of step (V) the amount of the total of bound iron, chromium, and zinc cations per unit volume of the ion ex- change resin is not more than 25 % of the total amount of bound iron, chromium, and zinc cations per unit volume of the ion exchanged resin that would result from contact be¬ tween the same amount of the cation exchange resin and a volume of the autodeposition composition used at the begin- ning of step (II) that is one hundred times larger than the volume of the cation exchange resin; and (iv) in the autodeposition composition, the concentration of stably dispersed organic coating resin is from 40 - 80 g/L, the concentration of fluoride ions is from 1.0 to 3.0 g/L, the concentration of oxidizing equivalents per liter is from 0.012 to 0.045 and is selected from the group consisting of hydrogen peroxide, ferric ions, and mixtures thereof, the pH is from 1.8 to 2.5, and the total concentration of all anions other than fluoride and surfactant anions is not more than 1 g/L. 5. A process according to claim 4, wherein (i) the stably dispersed organic coating resin in the autodeposition com¬ position is selected from the group consisting of (a) poly¬ mers and copolymers of vinylidene chloride that contain at least 80 % by weight of residues from vinylidene chloride and (b) copolymers of acrylonitrile; (ii) the time of contact in step (I) is from 30 to 200 seconds; (iv) the cation exchange resin has iminodiacetic acid functional groups in its acid form; and (v) the aqueous acidic liquid used in step (IV) consists essentially of water and acids selected from the group consisting of hydrofluoric acid, hydrochloric acid, and sulfuric acid in a total amount such that the aqueous acidic liquid is not more concentrated than 1 N in acid. 6. A process according to claim 3, wherein (i) the stably dispersed organic coating resin in the autodeposition com¬ position is selected from the group consisting of (a) poly¬ mers and copolymers of vinylidene chloride that contain at least 80 % by weight of residues from vinylidene chloride and (b) copolymers of acrylonitrile; (ii) the time of contact in step (I) is from 30 to 200 seconds; (iv) the cation exchange resin has iminodiacetic acid functional groups in its acid form; and (v) the aqueous acidic liquid used in step (IV) consists essentially of water and acids selected from the group consisting of hydrofluoric acid, hydrochloric acid, and sulfuric acid in a total amount such that the aqueous acidic liquid is not more concentrated than 1 N in acid. 7. A process according to claim 3, wherein (i) the stably dispersed organic coating resin in the autodeposition com¬ position is selected from the group consisting of (a) poly¬ mers and copolymers of vinylidene chloride that contain at s least 80 % by weight of residues from vinylidene chloride and (b) copolymers of acrylonitrile; (ii) the time of contact in step (I) is from 30 to 200 seconds; (iv) the cation exchange resin has iminodiacetic acid functional groups in its acid form; and (v) the aqueous acidic liquid o used in step (IV) consists essentially of water and acids selected from the group consisting of hydrofluoric acid, hydrochloric acid, and sulfuric acid in a total amount such that the aqueous acidic liquid is not more concentrated than 1 N in acid. 8. A process according to claim 7, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from 0 said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin¬ cipal container is removed during each hour; (iii) auto- deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 9. A process according to claim 6, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin- cipal container is removed during each hour; (iii) auto¬ deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 10. A process according to claim 5, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin¬ cipal container is removed during each hour; (iii) auto¬ deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 11. A process according to claim 4, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin- cipal container is removed during each hour; (iii) auto¬ deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 12. A process according to claim 3, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin¬ cipal container is removed during each hour; (iii) auto¬ deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 13. A process according to claim 2, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin- cipal container is removed during each hour; (iii) auto¬ deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 14. A process according to claim 1, wherein (i) the con¬ tacting in step (I) is by immersion of the metal surface in a principal container for the autodeposition composition; (ii) a portion of the autodeposition composition in the principal container therefor is continuously removed from said principal container and transported to a separate con¬ tainer wherein step (II) is completed, said portion being sufficiently large that a volume equal to at least 1 % of the total volume of autodeposition composition in the prin¬ cipal container is removed during each hour; (iii) auto¬ deposition composition from the end of step (II) is con¬ tinuously returned to the principal container for the autodeposition composition and mixed therein with the re¬ mainder of the autodeposition composition therein; and (iv) the aqueous acidic liquid regenerant consists essentially of water and from 0.5 - 3.0 % by weight of hydrofluoric acid. 15. A process comprising steps of: (I) contacting a metal surface selected from the group consisting of ferriferous and zinciferous metal sur¬ faces with an autodeposition composition comprising not more than 1 g/L in total of anions other than fluoride and surfactant anions, said contacting being continued for a sufficient time that the metal surface contacted is covered with a film containing the or¬ ganic coating resin, said film being sufficiently adherent to the metal surface to resist flowing off under the influence of gravity when the coated metal surface is removed from contact with the autodeposi¬ tion composition and forming a smooth coating on the metal surface after drying thereon; (II) contacting at least 30 % of the total volume of the autodeposition bath from the end of step (I) with a sufficient amount of an acid form cation exchange resin to transfer from the autodeposition bath to the cation exchange resin at least part of the total con- tent of dissolved iron, chromium, and zinc cations in the autodeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the auto¬ deposition bath; (III) separating the cation exchange resin used in step (II) from the autodeposition bath contacted with said cation exchange resin in step (II) ; (IV) contacting the separated cation exchange resin from step (III) with an aqueous acidic liquid consisting essentially of water and hydrofluoric acid in suffi- cient quantity for a sufficient time to displace at least a part of the multivalent metal ions therefrom and thereby regenerate the exchange capacity of the cation exchange resin; and (V) contacting an autodeposition bath comprising cations selected from the group consisting of iron, chromium, and zinc cations and not moire than 1 g/L in total of anions other than fluoride and surfactant anions with the regenerated acid form cation exchange resin from step (IV) for a sufficient time to transfer from the autodeposition bath to the ion exchange resin at least part of the content of dissolved iron, chromium, and zinc cations in the autodeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodeposition bath. 16. A process according to claim 15, wherein (i) the autodeposition composition in each of steps (I) and (V) comprises a total of no more than 0.3 g/L of anions other than fluoride and surfactant anions and (ii) at least 55 % of the total volume of the autodeposition composition is contacted with acid form cation exchange resin in step (II). 17. A process according to claim 16, wherein (i) the autodeposition composition in each of steps (I) and (V) comprises a total of no more than 0.1 g/L of anions other than fluoride and surfactant anions and (ii) at least 90 % of the total volume of the autodeposition composition is contacted with acid form cation exchange resin in step (II). 18. A process according to claim 17, wherein the time of contact in each of steps (I) and (V) is from 30 - 200 seconds. 19. A process according to claim 15, wherein the time of contact in each of steps (I) and (V) is from 30 - 200 seconds. 20. A process comprising steps of: (I) providing a wet bed of iminodiacetic acid cation ex- change resin containing between 0.10 and 0.30 milli¬ moles per milliliter of wet resin bed volume of a to¬ tal of iron and zinc cations bound thereon by exchange from a solution earlier contacted with the cation ex¬ change resin predominantly in its acid form, the vol- ume being measured when the bed has settled to its equilibrium volume under the influence of natural gravity and mild mechanical agitation in the absence of any flow of liquid through the bed, and the liquid with which the bed is wet being formed by washing the bed with from one half to four total bed volumes of purified water after the passage of any other liquid through the bed; and (II) adding to the top of the wet bed provided in step (I) a volume of an aqueous acidic regenerant liquid con¬ sisting essentially of water and an acid component selected from the group consisting of sulfuric acid, hydrofluoric acid, hydrochloric acid, and mixtures thereof, so as to cause a volume of eluted liquid equal to the volume of regenerant liquid added to flow from the bottom of the wet bed, the volume and compo- sition of the regenerant liquid being selected so as to satisfy at least one of the following two sets of conditions: (A) the volume of eluted liquid contains at least 0.080 millimoles per milliliter of wet resin bed volume of a total of iron and zinc cations dissolved therein and the total moles of iron and zinc cations displaced from binding to the cation exchange resin into the total volume of eluted liquid is at least equal to 0.070 times the number of equivalents of acid in the volume of regenerant liquid added to the wet bed; (B) the volume of eluted liquid contains at least 0.016 millimoles per milliliter of wet resin bed volume of a total of iron and zinc cations dis- solved therein and the total moles of iron and zinc cations displaced from binding to the cation exchange resin into the total volume of eluted liquid is at least equal to 0.025 times the number of equivalents of acid in the volume of regenerant liquid added to the wet bed. AMENDED CLAIMS [received by the International Bureau on 18 August 1993 (18.08.93); original claims 1, 15 and 20 amended; other claims unchanged (5 pages)] l. A process comprising steps of: (I) contacting a metal surface selected from the group consisting of ferriferous and zinciferous metal sur- faces with an autodeposition composition comprising water and: (A) from about 5 to about 550 g/L of a stably dis¬ persed organic coating resin; (B) from about 0.4 to about 5 g/L of fluoride ions; (C) an amount sufficient to provide from about 0.01 to about 0.2 oxidizing equivalents per liter of an oxidizing agent selected from the group con¬ sisting of dichromate, hydrogen peroxide, ferric ions, and mixtures thereof; and (C) a source of hydrogen ions in an amount sufficient to impart to the autodeposition composition a pH in the range from about 1.6 to about 3.8, said contacting being continued for a sufficient time that the metal surface contacted is covered with a film containing the organic coating resin, said film being sufficiently adherent to the metal surface to resist flowing off under the influence of gravity when the coated metal surface is removed from contact with the autodeposition composition and forming a smooth coating on the metal surface after drying thereon; (II) contacting at least 30 % of the total volume of the autodeposition bath from the end of step (I) , without adding additional surfactant thereto, with a suffi¬ cient amount of an acid form chelating cation exchange resin to transfer from the autodeposition bath to the ion exchange resin at least part of the content of dissolved iron, chromium, and zinc cations in the aut¬ odeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodeposi- tion bath; and (III) contacting the autodeposition bath from the end of step (II) with additional metal surface selected from the group consisting of ferriferous and zinciferous metal surfaces, so as to form on the additional metal surfaces a coating that is smooth after drying. 2. A process according to claim 1, comprising additional steps of: (IV) separating the cation exchange resin used in step (II) from the autodeposition bath contacted with said cat¬ ion exchange resin in step (II) ; (V) contacting the separated cation exchange resin from step (IV) with an aqueous acidic liquid in sufficient quantity for a sufficient time to displace at least a part of the multivalent metal ions therefrom and thereby regenerate the exchange capacity of the cation exchange resin; and (VI) contacting an autodeposition bath containing cations selepted from the group consisting of iron, chromium, and zinc cations with the regenerated acid form cation exchange resin from step (V) for a sufficient time to transfer from the autodeposition bath to the ion exchange resin at least part of the content of dis¬ solved iron, chromium, and zinc cations in the auto¬ deposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodepo¬ sition bath. 15. A process comprising steps of: (I) contacting a metal surface selected from the group consisting of ferriferous and zinciferous metal sur¬ faces with an autodeposition composition comprising not more than 1 g/L in total of anions other than fluoride and surfactant anions, said contacting being continued for a sufficient time that the metal surface contacted is covered with a film containing the or¬ ganic coating resin, said film being sufficiently adherent to the metal surface to resist flowing off under the influence of gravity when the coated metal surface is removed from contact with the autodeposi¬ tion composition and forming a smooth coating on the metal surface after drying thereon; (II) contacting at least 30 % of the total volume of the autodeposition bath from the end of step (I) , without adding additional surfactant thereto, with a suffi¬ cient amount of an acid form cation exchange resin to transfer from the autodeposition bath to the cation ex- change resin at least part of the total content of dissolved iron, chromium, and zinc cations in the aut¬ odeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodeposi¬ tion bath; (HI) separating the cation exchange resin used in step (II) from the autodeposition bath contacted with said cat¬ ion exchange resin in step (II) ; (IV) contacting the separated cation exchange resin from step (III) with an aqueous acidic liquid consisting essentially of water and hydrofluoric acid in suffi¬ cient quantity for a sufficient time to displace at least a part of the multivalent metal ions therefrom and thereby regenerate the exchange capacity of the cation exchange resin; and (V) contacting an autodeposition bath comprising cations selected from the group consisting of iron, chromium, and zinc cations and not more than 1 g/L in total of anions other than fluoride and surfactant anions with the regenerated acid form cation exchange resin from step (IV) for a sufficient time to transfer from the autodeposition bath to the ion exchange resin at least part of the content of dissolved iron, chromium, and zinc cations in the autodeposition bath and substitute an equivalent amount thereto of dissolved hydrogen ions in the autodeposition bath. 16. A process according to claim 15, wherein (i) the autodeposition composition in each of steps (I) and (V) comprises a total of no more than 0.3 g/L of anions other than fluoride and surfactant anions and (ii) at least 55 % of the total volume of the autodeposition composition is contacted with acid form cation exchange resin in step (II) . 17. A process according to claim 16, wherein (i) the autodeposition composition in each of steps (I) and (V) comprises a total of no more than 0.1 g/L of anions other than fluoride and surfactant anions and (ii) at least 90 % of the total volume of the autodeposition composition is contacted with acid form cation exchange resin in step (II). 18. A process according to claim 17, wherein the time of contact in each of steps (I) and (V) is from 30 - 200 seconds. 19. A process according to claim 15, wherein the time of contact in each of steps (I) and (V) is from 30 - 200 seconds. 20. A process comprising steps of: (I) providing a wet bed of iminodiacetic acid cation ex¬ change resin containing between 0.10 and 0.30 milli¬ moles per milliliter of wet resin bed volume of a to¬ tal of iron and zinc cations bound thereon by exchange from a solution earlier contacted with the cation ex- change resin predominantly in its acid form, the vol¬ ume being measured when the bed has settled to its equilibrium volume under the influence of natural gravity and mild mechanical agitation in the absence of any flow of liquid through the bed, and the liquid with which the bed is wet being formed by washing the bed with from one half to four total bed volumes of purified water after the passage of any other liquid through the bed; and (II) adding to the top of the wet bed provided in step (I) a volume of an aqueous acidic regenerant liquid con- sisting essentially of water and an acid component selected from the group consisting of sulfuric acid, hydrofluoric acid, hydrochloric acid, and mixtures thereof, so as to cause a volume of eluted liquid equal to the volume of regenerant liquid added to flow from the bottom of the wet bed, the volume and compo¬ sition of the regenerant liquid being selected so that the volume of eluted liquid contains at least 0.080 millimoles per milliliter of wet resin bed volume of a total of. iron and zinc cations dissolved therein and the total moles of iron and zinc cations displaced from binding to the cation exchange resin into the total volume of eluted liquid is at least equal to 0.070 times the number of equivalents of acid in the volume of regenerant liquid added to the wet bed.

Inventors: AHMED BASHIR, KOZAK WILLIAM G, AHMED, BASHIR, KOZAK, WILLIAM, G.
Applicants: HENKEL CORP, HENKEL CORPORATION
Application year: 1993
Main classification: B05D7
IPC codes: B01J49, B05D7, C09D5