Multilayer molded articles and process for producing the same

Abstract: A multilayer molded article comprising a skin and a substrate consisting of a polypropylene resin composition having a crystallization rate of 45 second or less, said skin being integrally adhered to the substrate. Said multilayer molded article can be produced by feeding a skin material and a molten polypropylene resin composition having a crystallization rate of 45 second or less between a pair of upper and lower molds, molding the molten polypropylene resin composition in the molds with simultaneous adhering of the skin material to the surface of the molded resin composition and then cooling the molten resin composition to solidify the same. Said multilayer molded article has a small deformation degree without the soft feeling of the skin material being impaired.

Description: This invention relates to a multilayer molded article comprising a skin and a substrate consisting of a polypropylene resin composition having a specific crystallization rate. Multilayer molded articles comprising a skin and a substrate consisting of a resin such as polypropylene or the like have been much used in a wide field such as automobile interior parts, household electric appliances and the like from the viewpoint of economy, light weight, and good moldability. Such multilayer molded articles are produced, as described in, for example, US-A-5 154 872, by feeding a molten thermoplastic resin between a pair of male and female molds in which a skin material has already been placed, clamping the two molds to mold the molten resin in the molds and simultaneously adhere the skin material to the surface of the molded resin, and then cooling the molten resin to solidify the same. JP-A-2080218 discloses a polypropylene resin product laid-up and formed concurrently with a skin layer and a core layer comprising a polypropylene having a melt flow index of 80-1500g/10 minutes. However, when molded articles are produced by known processes, the resulting multilayer molded articles are sometimes deformed, and this deformation not only makes appearance bad but also causes troubles in the course of production of a final article from the multilayer molded articles, whereby the production efficiency is remarkably affected. In order to prevent such deformation from being caused, it is effective to apply a sufficient pressure during the clamping of the molds in the molding process and then sufficiently cool the molten resin; however, this process has such problems that it requires a long molding cycle and hence is inferior in productivity, or the soft feeling of the skin material is lost in the resulting molded article. Thus, the above process is not practical. Thus, it is the object of the present invention to provide a multilayer molded article, the deformation of which is small, without adversely affecting the productivity and appearance of the product. This object has been achieved by the features of the claims i.e. by using as a substrate resin a polypropylene resin composition having a crystallization rate not greater than a certain value. Figs. 1A to 1C show an outline of a press-molding apparatus which is an embodiment of producing the present multilayer molded article and also show the successive steps of the present molding process. Fig. 2 is a partial view of a multilayer molded article in which d shows a deformation degree. The thermoplastic resin used as a substrate material in this invention is a polypropylene resin composition obtained by adding an appropriate amount of a crystallization rate-controlling agent (referred to hereinafter as a nucleating agent) to a polypropylene resin such as a conventional propylene homopolymer or copolymer or a resin composition consisting of the polypropylene resin, a stabilizer and other compounding agents such as inorganic filler and the like to control the crystallization rate of the polypropylene resin composition to 45 second or less, preferably 35 second or less. In this invention, it is very important to use a polypropylene resin composition having a crystallization rate adjusted to 45 second or less, preferably 35 second or less. When a polypropylene resin composition having a crystallization rate of more than 45 second is used, the deformation degree of the molded article obtained is great and the purpose of this invention cannot be achieved. The nucleating agent used for controlling the crystallization rate includes, for example, metal salts of organic acids such as aluminum p-t-butylbenzoate and sodium bis(4-t-phenyl)phosphate, and sorbitol compounds such as dibenzylidenesorbitol, 1,3,2,4-di-p-methylbenzylidenesorbitol and 1,3,2,4-di-p-ethylbenzylidenesorbitol. However, any nucleating agent can be used as far as it can adjust the crystallization rate to 45 second or less. The crystallization rate may be varied depending upon the kind of nucleating agent, the polypropylene resin composition used and the like, and hence, the amount of the nucleating agent is appropriately determined depending upon the various conditions. Thus, the amount of the nucleating agent is not critical. For example, when aluminum p-t-butylbenzoate is used as the nucleating agent, it is added so that the proportion of this compound becomes 0.05-0.3% by weight based on the weight of the polypropylene resin composition. The term "crystallization rate" used herein means a value obtained by melting the polypropylene resin composition, subjecting the same to isothermal crystallization at 130°C and measuring the time required for crystallization of 1/2 of the total amount of the resin to be crystallized by means of a differential scanning calorimeter (DSC). The polypropylene resin composition used in this invention is required to have a crystallization rate of 45 second or less, and moreover, it is suitable that the polypropylene resin composition has a melt index (MI) of 20 or more, preferably 30 or more, from the viewpoint of effecting the molding of the molten resin to form a multilayer molded article at a relatively low pressure. The upper limit of the melt index is not critical in relation to deformation; however, it is usually 200, preferably 150 from the viewpoint of physical properties. The term "MI" used herein means a value obtained by measurement according to JIS K7210 (230°C, 2.16 kg). The skin material used in this invention is not critical, and various materials can be used. It includes, for example, woven, knit and non-woven fabrics composed of various starting materials, and sheets and films of thermoplastic resins and thermoplastic elastomers. These may be embossed. The skin material also includes foams of various resins such as polyolefins, polyvinyl chloride, polystyrene and polyurethane, and rubber foams of e.g. cis-1,4-butadiene polymers or ethylene-propylene copolymers. The above-mentioned materials may be used alone or in the form of a laminate of two or more. In the use of such a skin material, pre-heating or pre-forming may be previously applied thereto in order to adjust the tensile stress, elongation and the like. As far as a polypropylene resin composition having a crystallization rate of 45 second or less is used as a substrate material, the multilayer molded article of this invention can be produced by a known, general molding method for a thermoplastic resin which comprises feeding a skin material and a molten thermoplastic resin between a pair of molds, molding the resin in the molds with simultaneous adhering of the skin material to the surface of the molded resin, and then cooling the molten resin to solidify the same, thereby forming a multilayer molded article consisting of a skin and a substrate consisting of the thermoplastic resin, such as a press molding method or injection molding method. The molding method is not critical, however, the press molding method is preferred because substantially no strain or the like is caused. An example of producing the multilayer molded article of this invention is explained below referring to Figs. 1A to 1C. The press molding apparatus in this example consists of a pair of upper mold (1) and lower mold (2), as shown in Figs. 1A to 1C, and a clamper (3) which can be moved upward and downward by means of hydraulic pressure, pneumatic pressure, spring or the like is arranged about the outer periphery of the lower mold (2) for putting the skin material (6) on the clamper. The clamper (3) may be provided at its upper end with pins (not shown) for controlling the elongation of the skin material (6), and the control and adjustment of elongation of the skin material are effected with these pins or by adjusting the power of fastening the skin material sandwiched in between the upper surface of the clamper (3) and the lower surface of the peripheral portion of the upper mold (1). The mold surface of the lower mold (2) is provided with an opening (4) for feeding the molten polypropylene resin composition sent through a resin path (7). Incidentally, either one or both of the molds may be provided, if necessary, with a piping for cooling. An explanation is made below of a specific production method using the above-mentioned apparatus. In the state that the lower mold (2) and the upper mold (1) are opened, the skin material (6) is put on the upper surface of the clamper (3) (see Fig. 1A), and the upper mold (1) is allowed to fall down to an appropriate position as shown in Fig. 1B, after which the molten polypropylene resin composition (5) is fed between the skin material (6) and the lower mold (2) from the resin-feeding opening (4) (see Fig. 1B). While the molten resin is fed, or after the feeding of the desired amount of the molten resin has been completed, the upper mold (1) is further allowed to fall down to clamp the molds, whereby the molten polypropylene resin composition (5) is spread in the cavity formed by the molds and molded and simultaneously adhered to the skin material (see Fig. 1C). After cooling, the molds are opened and the molded article is taken out. By the above method, there can be obtained a multilayer molded article (9) in which the skin material (6) has been integrally and firmly adhered to the surface of the substrate resin (8) consisting of the polypropylene resin composition. The above-mentioned apparatus and the above-mentioned production method using the apparatus are merely an embodiment, and the present invention is not limited thereto. In the following Examples, % and parts are by weight unless otherwise specified. Example 1 Preparation of polypropylene resin composition Polypropylene block copolymer (ethylene content=8.2%, MI=35) 81.9% Talc (Micronwhite 5000S' manufactured by Hayashi Kasei K.K.) 18.0% Aluminum p-t-butylbenzoate 0.1% To 100 parts by weight of a mixture of the these components were added as stabilizers 0.1 part of Irganox 1010 (phenol type stabilizer manufactured by Geigy) and 0.15 part of Ultranox 626 (phosphite type antioxidant manufactured by General Electric). The resulting resin mixture was kneaded in a twin-screw kneader and pelletized to form polypropylene resin composition pellets. Incidentally, a small amount of 2,5-dimethyl-2,5-di(t-butylperoxy)hexane was added during the kneading to adjust the MI to 40. The crystallization rate of the polypropylene resin composition was 30.4 second. Preparation of multilayer molded article Using the press-molding apparatus shown in Figs. 1A to 1C, a multilayer molded article consisting of a skin and a substrate consisting of a polypropylene resin composition was prepared by the following press-molding method: On the clamper (3) was put a skin material (a laminate consisting of a polypropylene elastomer sheet having a thickness of 0.5 mm and a polypropylene foam sheet having a thickness of 3 mm and a foaming magnification of 15) so that the foam sheet faced the clamper, and thereafter, the upper mode (1) was allowed to fall down. The polypropylene resin composition (5) was previously melted, and the molten polypropylene resin composition (5) was fed between the skin material (6) and the lower mold (2) from the resin-feeding opening (4) through the resin path (7). After the desired amount of the resin had been fed, the upper mold (1) was further allowed to fall down to clamp the molds, and thereafter, the molded resin was cooled. The molds were opened to obtain a box-shaped multilayer molded article (9) having a length of 2300 mm, a width of 750 mm, a depth of 100 mm and a resin layer thickness of 3 mm. The molding conditions were as follows: Molten resin temperature: 200°C Mold temperature: upper mold, 30°C; lower mold, 35°C Cooling time under pressure: 40 second The pressing pressure required for the molding was 60 bar of unit area of the molded article obtained. The deformation degree d of the molded article obtained was 4 mm. Incidentally, the deformation degree d was evaluated by the difference of the end of the deformed horizontal wall from its position before the deformation (see d in Fig. 2) in the cross-section at about the center portion of the molded article obtained. The smaller the d value, the smaller the deformation degree. Example 2 The same procedure as in Example 1 was repeated, except that the MI was adjusted to 20 during the kneading, to obtain a multilayer molded article. The deformation degree d of the molded article obtained was 4 mm and the pressing pressure required for the molding was 100 bar of unit area of the molded article. Example 3 Polypropylene block copolymer (PD 7035 manufactured by Exson) 81.8% Talc (MP 1250 manufactured by Pfizer) 18.0% Aluminum p-t-butylbenzoate 0.2% To 100 parts by weight of a mixture of these components were added as stabilizers 0.1 part of Irganox (phenol type stabilizer manufactured by Geigy) and 0.15 part of Ultranox 626 (phosphite type antioxidant manufactured by General Electric), and a small amount of 2,5-dimethyl-2,2-di(t-butylperoxy)hexane was added to the mixture to adjust the MI to 40. The resulting mixture was kneaded in a twin-screw kneader and then pelletized to obtain polypropylene resin composition pellets. The crystallization rate of the polypropylene resin composition was 25.8 second. In the same manner as in Example 1, the polypropylene resin composition pellets thus obtained were subjected to molding treatment to obtain a multilayer molded article. The deformation degree d of the molded article was 3 mm and the pressing pressure required for the molding was 60 bar of unit area of the molded article obtained. Example 4 The same procedure as in Example 1 was repeated, except that a polypropylene block copolymer having an ethylene content of 4.5% and an MI of 50 was substituted for the polypropylene resin, to obtain a polypropylene resin composition having an MI of 40. The crystallization rate of the polypropylene resin composition obtained was 25.8 second. In the same manner as in Example 1, the polypropylene resin composition was subjected to molding treatment to obtain a multilayer molded article. The deformation degree d of the multilayer molded article obtained was 2.5 mm, and the pressing pressure required for the molding was 60 bar of unit area of the molded article obtained. Comparative Example 1 Polypropylene block copolymer (PD 7035 manufactured by Exson) 82% Talc (Micronwhite 5000S' manufactured by Hayashi Kasei K.K.) 18% To 100 parts by weight of a mixture of these components were added as stabilizers 0.1 part of Irganox 1010 (phenol type antioxidant manufactured by Geigy) and 0.15 part of Ultranox 626 manufactured by General Electric), and a small amount of 2,5-dimethyl-2,5-di(t-butyl-peroxy)hexane was added to the mixture to adjust the MI of the mixture to 40. The resulting mixture was kneaded in a twin-screw kneader and then pelletized to obtain polypropylene resin composition pellets. The crystallization rate of the polypropylene resin composition was 57.6 second. In the same manner as in Example 1, the polypropylene resin composition pellets were subjected to molding treatment to obtain a multilayer molded article. The deformation degree d of the multilayer molded article was 7 mm and the pressing pressure required for the molding was 60 bar of unit area of the molded article obtained. Comparative Example 2 Polypropylene block copolymer (PD 7035 manufactured by Exson) 78% Talc (MP 1250 manufactured by Pfizer) 22% To 100 parts by weight of a mixture of these components were added as stabilizers 0.1 part of Irganox (phenol type stabilizer manufactured by Geigy) and 0.15 part of Ultranox 626 (phosphite type antioxidant manufactured by General Electric), and a small amount of 2,5-dimethyl-2,5-di(t-butylperoxy)hexane was added to the mixture to adjust the MI to 40. The resulting mixture was kneaded in a twin-screw kneader and then pelletized to obtain polypropylene resin composition pellets. The crystallization rate of the polypropylene resin composition was 58.8 second. In the same manner as in Example 1, the polypropylene resin composition pellets were subjected to molding treatment to obtain a multilayer molded article. The deformation degree d of the multilayer molded article obtained was 8 mm and the pressing pressure required for the molding was 60 bar of unit area of the molded article obtained. According to the present invention, a polypropylene resin composition having a specific crystallization rate is used as the substrate resin, and this enables one to obtain a multilayer molded article having a small deformation degree without impairing the soft feeling of the skin material by the known molding method without any special modification being applied thereto. Since the deformation degree of the molded article thus obtained is small, the appearance is good, and final products can be easily obtained using the multilayer molded article as the starting material.

Claims: A multilayer molded article comprising a skin (6) and a substrate consisting of a polypropylene resin composition (5) having a crystallization rate of 45 second or less, said skin (6) being integrally adhered to the surface of the substrate, wherein the crystallization rate is a value obtainable by melting the polypropylene resin composition (5), subjecting the polypropylene resin composition (5) to isothermal crystallization at 130°C and measuring the time required for crystallizing 1/2 of the total amount of resin to be crystallized by means of a differential scanning calorimeter. A multilayer molded article according to Claim 1, wherein the polypropylene resin composition (5) has a melt index of 20 or more. A multilayer molded article according to Claim 1 or 2, wherein the polypropylene resin composition (5) has a crystallization rate of 35 second or less. A process for producing a multilayer molded article comprising a skin and a substrate consisting of a thermoplastic resin, which process comprises feeding a skin material (6) and a molten thermoplastic resin between a pair of upper mold (1) and lower mold (2), molding the molten resin in the molds (1,2) with simultaneous adhering of the skin material (6) to the surface of the molded resin, and then cooling the molten resin to solidify the same, characterized by using a polypropylene resin composition (5) having a crystallization rate of 45 second or less as the thermoplastic resin, wherein the crystallization rate is a value obtainable by melting the polypropylene resin composition (5), subjecting the polypropylene resin composition (5) to isothermal crystallization at 130° and measuring the time required for crystallizing 1/2 of the total amount of resin to be crystallized by means of a differential scanning calorimeter. A process for producing a multilayer molded article comprising a skin and a substrate of a thermoplastic resin, which process comprises feeding a skin material (6) between an unclosed pair of upper and lower molds (1,2), allowing the upper mold (1) to fall down to an appropriate position, feeding a molten thermoplastic resin between the skin material (6) and the lower mold (2), allowing the upper mold (1) to further fall down while feeding the molten thermoplastic resin or after completion of feeding the predetermined amount of the molten thermoplastic resin, thereby clamping the upper and lower molds (1,2) to mold the molten thermoplastic resin in the molds (1,2) and simultaneously adhere the skin material (6) to the surface of the molded resin, and then cooling the molten resin to solidify the same, characterized by using, as the thermoplastic resin, a polypropylene resin composition (5) having a crystallization rate of 45 second or less, wherein the crystallization rate is a value obtainable by melting the polypropylene resin composition (5), subjecting the polypropylene resin compositions (5) to isothermal crystallization at 130° and measuring the time required for crystallizing 1/2 of the total amount of resin to be crystallized by means of a differential scanning calorimeter. A process according to Claim 4 or 5, wherein the polypropylene resin composition (5) has a melt index of 20 or more. A process according to Claim 4, 5 or 6, wherein the polypropylene resin composition (5) has a crystallization rate of 35 second or less.

Inventors: HARADA HIROYUKI, HIGASHI KENICHI, MATSUMOTO MASAHITO, USUI NOBUHIRO, HARADA, HIROYUKI, HIGASHI, KENICHI, MATSUMOTO, MASAHITO, USUI, NOBUHIRO
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY LIMITED
Application year: 1993
Main classification: B29C43
IPC codes: B29C43, B29C70, B29C45, B32B27, B29L9, B29K23