Method for recovering ammonia adsorbent

Abstract: A method for recovering an ammonia adsorbent which comprises streaming an NO X -containing gas at 300-600°C through an ammonia adsorbent layer which adsorbs ammonia and which is saturated with ammonia.

Description: FIELD OF THE INVENTION AND RELATED ART STATEMENT The present invention relates to a method for recovering an ammonia adsorbent. In particularly, the present invention relates to a method for recovering an ammonia adsorbent disposed on the downstream side of a dry exhaust gas denitrating device using ammonia as a reducing agent. This ammonia adsorbent is preferably disposed in a temperature region of 200°C or less on the above-mentioned downstream side. In the present invention, this adsorbent is recovered, when the ammonia adsorbent adsorbs remaining ammonia in the above-mentioned dry exhaust gas denitrating device and it is saturated with ammonia. Ammonia remaining in the exhaust gas from the dry exhaust gas denitrating device utilizing ammonia as a reducing agent is adsorbed by the adsorbent, but the amount of adsorbed ammonia is limited and therefore in order to use the adsorbent repeatedly, a suitable adsorbent recovery treatment is necessary. As an adsorbent recovery means, there have been known a method in which temperature is elevated for desorbing ammonia, and another method in which pressure is lowered to a level in the vicinity of vacuum so that ammonia can be desorbed. However, for the sake of the adsorbent recovery by heat, a high-temperature gas or a heating device is necessary, and for the sake of the adsorbent recovery by vacuum, it is necessary to decrease the pressure by vacuum suction. Both methods have the drawback that a large amount of energy is consumed. In addition, a long period of time is required for the recovery. Since an adsorption process is not carried out during the recovery period, a capacity of the apparatus must be increased so as to overcome such an inconvenience. Particularly for the desorption of adsorbed components present in trace amounts, a degree of vacuum must be increased, so that a great deal of energy and a heating device or a vacuum pump are required, which makes the system more complicated. Therefore, a technique for securely recovering the adsorbent in a short period of time under a low energy consumption has been desired. If this technique is attained, the dry exhaust gas denitrating device in which the adsorption technique can be utilized using the ammonia adsorbent can be applied to many fields, and the energy saving of the whole apparatus can be expected. OBJECT AND SUMMARY OF THE INVENTION In view of the above-mentioned technical level, an object of the present invention is to provide a method for recovering an ammonia adsorbent in response to the above-mentioned technical demand. The gist of the present invention resides in a method for recovering an ammonia adsorbent which comprises the steps of adsorbing remaining ammonia in an exhaust gas by an ammonia adsorbent layer disposed on the downstream side of a dry exhaust gas denitrating device into which ammonia is injected as a reducing agent, to saturate the adsorbent layer with ammonia, and then introducing and streaming an NO x -containing exhaust gas at 300-600°C drawn from an upstream side of the dry exhaust gas denitrating device. In the present invention, an NO x -containing exhaust gas at 300-600°C or an NO x -containing hot air at 300-600°C is used as a heat source required for the recovery of the ammonia adsorbent. In the case that the heat source does not include NO x , the desorption of ammonia from the ammonia adsorbent is carried out only by the effect of an elevated temperature, and therefore a long time is taken to achieve desorption and recovery. However, when NO x is added, NO x itself reacts rapidly with adsorbed ammonia as shown by the following formula, whereby the ammonia adsorbent can be promptly recovered: 4NO + 4NH 3 + O 2 → 4N 2 + 6H 2 O Thus, in the present invention, the removal of ammonia by the reaction of NO x and ammonia and the desorption of ammonia by the effect of high temperature are simultaneously carried out to remove ammonia promptly and efficiently from the ammonia adsorbent, whereby the ammonia adsorbent can be recovered. At a temperature of 300°C or less, the exhaust gas or air containing NO x does not react with ammonia adsorbed by the ammonia adsorbent, and at a temperature of 600°C or more, the ammonia adsorbent deteriorates. Therefore, the temperature of the exhaust gas or air containing NO x should be in the range of from 300 to 600°C. One example of the ammonia adsorbent which can be used in the present invention is an adsorbent comprising 75% of titania, 5% of vanadium pentoxide and a molding auxiliary agent which will be described in the undermentioned embodiment, and other usable examples of the ammonia adsorbent include alumina, zeolite, silica·alumina, molecular sieve and titania. In the present invention, a gas released from an ammonia adsorbent layer at the time of the recovery of the ammonia adsorbent is preferably circulated through a position on the upstream side in the exhaust gas flow of the dry exhaust gas denitrating device and on the downstream side of a dividing/drawing portion of the NO x -containing exhaust gas for the recovery. In the present invention, it is preferable that a plurality of systems of the ammonia adsorbent layers are formed and the adsorption of ammonia and the recovery of the ammonia adsorbent are mutually alternated on each ammonia adsorbent layer. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic view illustrating an embodiment of a method for recovering an ammonia adsorbent regarding the present invention. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS One embodiment of the present invention will be described in reference to, for example, a denitration system of an exhaust gas from a gas turbine 1 equipped with an exhaust gas boiler 2 shown in Fig. 1. This exhaust gas boiler 2 is provided with an ammonia injector 3 and a denitrating device 4 in addition to a heat exchanger (not shown). A gas duct 7 extending from the downstream side of the denitrating device 4 is divided into a duct 10 extending to an ammonia adsorbing tower 5 and a duct 11 extending to another ammonia adsorbing tower 6, and the exhaust gases coming from the ammonia adsorbing towers 5, 6 join into the gas duct 7 again and the joined gas is then discharged into the atmosphere through a chimney 9. Furthermore, the system of the present invention is provided with an NO x -containing gas duct 12 and a recovery gas duct 13. This NO x -containing gas duct 12 divides and draws the exhaust gas on the upstream side of the ammonia injector 3 of the exhaust gas boiler 2 and then introduces this NO x -containing exhaust gas into the ammonia adsorbing towers 5, 6. On the other hand, the above-mentioned recovery gas duct 13 introduces the recovery gases coming from the ammonia adsorbing towers 5, 6 into a position on the upstream side of the denitrating device 4 of the exhaust gas boiler 2 and on the downstream side of the above-mentioned exhaust gas dividing/drawing position. The exhaust gas of the thus constituted gas turbine 1 is heat-exchanged in the exhaust gas boiler 2, so that the temperature of the exhaust gas lowers, and ammonia is injected through the ammonia injector 3 and the exhaust gas is then denitrated by the denitrating device 4. However, in the thus treated exhaust gas, ammonia is kept remaining. This exhaust gas containing ammonia is introduced into the ammonia adsorbing tower 6, in which ammonia is adsorbed, and the exhaust gas is introduced into the gas duct 7 again and then discharged through the chimney 9. At this time, dampers D 1 , D 2 of the duct 11 are opened. On the other hand, dampers D 3 , D 4 of the duct 10 extending to the ammonia adsorbing tower 5 in another system are closed, but-the NO x -containing exhaust gas at a high temperature (300-600°C) forwarded through NO x -containing gas duct 12 is introduced into the ammonia adsorbing tower 5 via a damper D 5 . In this ammonia adsorbing tower 5, ammonia adsorbed by the ammonia adsorbent is desorbed and then returned to an upstream side of the denitrating device 4 of the exhaust gas boiler 2 through the recovery gas duct 13. The dampers D 1 to D 6 are switched suitably in accordance with the adsorbing state of ammonia or when a certain time has passed, so that these ammonia adsorbing towers 5, 6 are alternated to adsorb or desorb ammonia. Comparative Example (Example 1) An ammonia adsorbent comprising 75% of titania, 5% of vanadium pentoxide and a molding auxiliary agent was molded into pellets having a diameter of 3 mm, and a combustion exhaust gas containing 20 ppm of ammonia at a gas temperature of 100°C was then introduced into the pellets to adsorb ammonia sufficiently. Afterward, the feed of the combustion exhaust gas was stopped, and hot air having a gas temperature adjusted to 100°C was introduced thereinto. At this time, an ammonia concentration change with time at the outlet of the ammonia adsorbent was measured. Furthermore, changes with time at air temperatures of 200°C, 300°C and 400°C were measured in the same manner, and the results are shown in Table 1. Gas Temp. (°C) Ammonia Concentrations at Outlet of Adsorbent after 10 min after 20 min after 30 min after 60 min after 120 min 100 2-3 ppm 2-3 ppm 2-3 ppm 2-3 ppm 2-3 ppm 200 3-5 ppm 5-10 ppm 5-10 ppm 5-10 ppm 5-10 ppm 300 60 ppm 100 ppm 100 ppm 50 ppm 10 ppm 400 120 ppm 180 ppm 140 ppm 20 ppm <1 ppm It can be understood from Table 1 that ammonia is rapidly desorbed at a temperature of 300°C or more. Moreover, the ammonia adsorbents after a passage of 120 minutes were ground and then analyzed to inspect ammonia concentrations, and as a result, it was confirmed that in the cases of 100°C and 200°C, ammonia remained at high concentrations in the ammonia adsorbents. In the case of 300°C, it was confirmed that a small amount of ammonia remained in the ammonia adsorbent and most of ammonia was desorbed. Example in accordance with the present invention (Example 2) The same ammonia adsorbents as in Example 1 were used, and ammonia was adsorbed by the same treatment as in Example 1. Afterward, hot air to which NO x was added at a concentration of 30 ppm and which was adjusted to 300°C was introduced, and an ammonia concentration at an outlet was measured. The results are shown in Table 2. Gas Temp. Ammonia Concentrations at Outlet of Adsorbent after 10 min after 20 min after 30 min after 60 min after 120 min 300°C 20 ppm 30 ppm 10 ppm <1 ppm <1 ppm It can be understood from Table 2 that in Example 2 regarding the present invention, the ammonia concentration at the outlet lowers more rapidly as compared with Example 1. In addition, the ammonia adsorbents 60 minutes or 120 minutes had passed were ground and then analyzed to inspect ammonia concentrations in the ammonia adsorbents, and as a result, any ammonia was not detected. In Example 2 described above, the results in the case of using the hot air containing NO x are exhibited, but also with the use of an exhaust gas containing NO x , about the same results have been obtained. As is apparent from the foregoing, according to the present invention, an ammonia adsorbent on which ammonia is adsorbed can be rapidly recovered, and in a dry exhaust gas denitration using ammonia as a reducing agent, the present invention can be advantageously applied to a process in which ammonia remaining in a denitrated exhaust gas is desorbed and removed. In addition, when two or more systems having ammonia adsorbing towers are provided and desorption and adsorption are alternated, ammonia in the exhaust gas can be continuously treated.

Claims: A method for recovering an ammonia adsorbent which comprises the steps of adsorbing remaining ammonia in an exhaust gas by an ammonia adsorbent layer disposed on the downstream side of a dry exhaust gas denitrating device into which ammonia is injected as a reducing agent, to saturate the adsorbent layer with ammonia, and then introducing and streaming an NO x -containing exhaust gas at 300-600°C drawn from an upstream side of the dry exhaust gas denitrating device. The method for recovering an ammonia adsorbent according to Claim 1 wherein a gas released from the ammonia adsorbent layer at the time of the recovery of the ammonia adsorbent is circulated through a position on the upstream side of the dry exhaust gas denitrating device and on the downstream side of a dividing/drawing portion of the NO x -containing exhaust gas for the recovery.

Inventors: IIDA KOUZO, MORII ATSUSHI, NAITO OSAMU, ONISHI TOSHIYUKI, SERIZAWA SATORU, IIDA, KOUZO, MORII, ATSUSHI, NAITO, OSAMU, ONISHI, TOSHIYUKI, SERIZAWA, SATORU, Iida, Kouzo, c/o Hiroshima Res. &amp; Dev. Center, Morii, Atsushi, c/o Nagasaki Shipyard &amp;, Naito, Osamu, c/o Nagasaki Shipyard &amp;, Onishi, Toshiyuki, c/o Nagasaki Shipyard &amp;, Serizawa, Satoru, c/o Nagasaki Shipyard &amp;
Applicants: MITSUBISHI HEAVY IND LTD, MITSUBISHI JUKOGYO KABUSHIKI KAISHA
Application year: 1993
Main classification: C01C1
IPC codes: B01D53, B01J20