Gear product

Abstract: A novel gear product (M₁) includes plural gear members (13, 14) of different tooth profiles and configurations, which are manufactured integrally through a forging process. The forged gear product is compact, and strong, and includes a clutch spline member with clutch spline teeth (13) and a helical gear member with spiral teeth (14), which are integrally forged and continuously arranged in the axial direction to be adjacent to each other, preferably without any clearance therebetween.

Description: The present invention relates to a gear product including a set of coaxial gear members which have different tooth profiles and configurations and are formed continuously without any clearance therebetween. An example of such gear product includes a gear component having synchronous clutch spline teeth used for a transmission mechanism. Such gear product is typically manufactured according to either of the following two methods: (1) combining or joining separately forged plural gear members; and (2) forging gear material into an integral body consisting of plural gear members. In either method, tooth arrangements on the gear members are generally formed and finished by machining although part of the teeth may be formed through forging process. Especially, the spiral tooth profile of a helical gear cannot be formed by forging and should always be formed by machining. The gear product manufactured by the above method (1) has several drawbacks: (a) Manufacturing processes are rather complicated; (b) The yield is unfavorably low; and (c) It is substantially impossible to make the gear product compact and light in weight since each gear member is manufactured to have a required strength. When teeth on the gear member are formed through machining, the proper fiber or micro-structure of the material is undesirably cut off at the machined part to decrease the strength thereof. Machining the gear member requires a sufficient clearance on either side of its tooth arrangement to receive a machining tool and complete the machining, thus preventing the whole gear product from being made compact and light in weight. Teeth formed through machining further requires a chamfering process. There has, accordingly, been a strong demand for a gear product including plural gear members manufactured integrally by forging. Such demand has, however, not been realized due to some technological difficulties. In other words, conventional forged gear products including plural gear members are not of practical use. JP-A-2 052 139 discloses an integrally forged gear according to the preamble of claim 1. One object of the invention is to provide a novel gear product including plural gear members of different tooth profiles and configurations, which are forged integrally by a stamping process. Another object of the invention is to provide a novel forged gear product which can be made compact and light in weight. A further object of the invention is to provide a novel forged gear product including plural gear members which are adjacent to each other via a flange and which attain adequate strength. According to the invention, there is provided a gear product (M) comprising a plurality of gear members, having different tooth profiles around a periphery thereof, and an externally-extending flange (15), which are coaxially arranged and are integrally forged by a stamping process, the gear members and flange (15) being in intimate contact with one another and being free of clearance therebetween, characterised in that the flange is formed in between a pair of said gear members. The set of gear members may include a helical gear member with a spiral tooth profile and a clutch spline member with a straight tooth profile. In the gear product of the invention, plural gear members are integrally forged and continuously arranged without any clearance therebetween to be adjacent to each other via the flange. This forged gear product of the invention does not require any clearance on either side of each tooth arrangement, which is essential for conventional machined gear members, thus allowing the axial length thereof to be favourably shortened. The fiber structure of the gear material is not undesirably cut off by machining but runs continuously to ensure adequate strength. The plural gear members adjacent to each other via the flange reinforce the whole gear product to further improve the strength thereof. The gear product of the invention can thus be made compact and light in weight. Even a chamfered part can be formed without machining by previously setting in a forging die. The above and other objects, features, aspects, and advantages of the present invention will become more apparent from the following detailed description. The invention will now be described by way of example in the following non-limitive description with reference to the accompanying drawings, in which: Fig. 1 is a perspective view illustrating a gear product not embodying the invention; Fig. 2 is a perspective view illustrating a gear product not embodying the invention; Fig. 3 shows a flow of a fiber structure in a tooth profile of the present invention; Fig. 4 is a perspective view illustrating a gear product not according to the invention; Fig. 5 is a side view illustrating a gear product according to the present invention; Fig. 6 is a perspective view illustrating a gear product not embodying the invention; Fig. 7 is a schematic cross-sectional view showing a forging die used for producing the gear product of Fig. 1; Fig. 8 shows a forging process for producing the gear product of Fig. 1; Fig. 9 shows a forging process for producing the gear product of Fig. 1; Fig. 10 shows a forging process for producing the gear product of Fig. 1; Fig. 11 shows a forging process for producing the gear product of Fig. 2; Fig. 12 shows a forging process for producing the gear product of Fig. 4; Fig. 13 shows examples of gears according to the invention; and Fig. 14 shows examples of a gear product modified to have a clearance as conventional products. The invention is described in detail with reference to a plurality of embodiments, each including two gear members having different tooth profiles and configurations. A forging die for producing a gear product is shown in Fig. 7. The forging die includes a lower die member 1 and a vertically movable upper die member 2. The lower die member 1 further includes: a base 1a; an outer cylinder 1b rotatable relative to the base 1a; a vertically movable inner cylinder 1c fitted in and arranged coaxially with the outer cylinder 1b, and a punch 3 disposed on the center of the inner cylinder 1c. The base la and the outer cylinder 1b are coupled with each other via bearings 4. A knock-out pin 5 is disposed below the punch 3 while a pair of tubular knock-outs 6 are arranged below the inner cylinder 1c. The inner surface of the upper end of the outer cylinder 1b is provided with a series of grooves 7 for producing spiral teeth (hereinafter referred to as helical grooves 7). The inner surface of the upper end of the inner cylinder lc is provided with a series of grooves 9 for producing synchronous clutch spline teeth (hereinafter referred to as clutch spline grooves 9). The upper die member 2 includes: a punch 10 disposed on the center thereof to be movable downward, and a protrusion ring 11 surrounding the punch 10. A gear material 12 is placed in between the upper die member 2 and the lower die member 1 as clearly seen in Fig. 7. While the upper die member 2 is moved downward, the gear material 12 is pressed into a cavity 8 defined by the outer cylinder 1b and the inner cylinder 1c. The gear material 12 includes a larger diametral section 12a, a smaller diametral section 12b, and a smallest-diametral boss section 12c continuously formed in this order. When the gear material 12 is pressed into the cavity 8, clutch spline teeth 13 are formed on the circumference of the smaller diametral section 12b by the clutch spline grooves 9. The gear material 12 is further pressed against the punches 3 and 10 and the protrusion ring 11 to expand radially, and spiral teeth 14 are formed on the circumference of the larger diametral section 12a by the helical grooves 7 as shown in Fig. 8. Recesses formed in the gear material 12 by the punches 3 and 10 are subsequently worked into a shaft hole. A recess formed by the protrusion ring 11 contributes to weight reduction of a final gear product M. Since the tooth profiles and configurations of the clutch spline teeth 13 and the spiral teeth 14 are freely determined by changing the shape and arrangement of the helical grooves 7 and the clutch spline grooves 9, chamfering or other post-work can be omitted by previously setting required work in the grooves 7 and 9. In this forging process, guide chamfers 20 are simultaneously formed on free ends of the clutch spline teeth 13. In this forging process, the cavity 8 is completely blocked by the lower die member 1 and the upper die member 2, and the shape and size of the gear material 12 is previously determined corresponding to those of a desirable final gear product. Fig. 1 shows a final gear product M1 (not according to the invention) produced through only one step with the forging die described above. The gear product M1 includes the clutch spline teeth 13 and the spiral teeth 14, which are coaxially arranged without any clearance therebetween. Both the teeth 13 and 14 have fiber structure or texture continuously running without any cut as shown in Fig. 3, thus yielding adequate strength. A stopper can be formed on the circumferential end of the spiral or helical teeth to ensure secure engagement and prevent accidental fall-out. In such a case, a gear product M with a stopper is produced with another forging die, in which a cavity 8 is not completely blocked by a lower die member 1 and an upper die member 2, as shown in Fig. 11. The gear product M has a fin 15' formed between the lower die member 1 and the upper die member 2. Fig. 2 shows a gear product M2, (not according to the invention) having a stopper flange 15, which is integrally formed and arranged coaxially with the spiral teeth 14 without any clearance. In the gear product M2, the flange 15 formed integrally with the spiral teeth 14 further improves the strength of the spiral teeth 14. Such improvement of the strength as well as continuous flow of the fiber structure shown in Fig. 3 drastically enhances the durability of the gear product M2. The spiral teeth 14 of the gear product M1 can be formed by machining although the strength thereof is not sufficiently high. The spiral teeth 14 with the stopper flange 15 as in the case of the gear product M2 cannot, however, be produced by a conventional machining process. After forging the gear material 12 into the gear product M, the upper die member 2 is moved upward and separated from the lower die member 1 as seen in Fig. 9. The pair of tubular knock-outs 6 are pressed upward as shown by the arrows of Fig. 9 to move the inner cylinder 1c with the gear product M upward. Here the gear product M is taken out of the outer cylinder 1b while the outer cylinder 1b rotates relative to the base la by an amount corresponding to a tilt angle of the spiral teeth 14. The gear product M is thus taken out in the vertical direction without any rotation. Since the gear product M is lifted vertically, the bearings 4 disposed between the base 1a and the outer cylinder 1b are preferably arranged in a substantially horizontal plane as clearly seen in Fig. 7. This horizontal arrangement reduces a load applied onto the bearings 4 under the pressing conditions. The knock-out pin 5 is then pressed upward as shown in Fig. 10, and the gear product M supported by the upper end of the punch 3 is taken out of the cavity 8. In the gear product M1 or M2 described above the spiral teeth 14 and the clutch spline teeth 13 do not overlap each other in the axial direction. Modification of the forging die, however, allows manufacture of another gear product including spiral teeth and clutch spline teeth which overlap each other and are continuously arranged without any clearance in the axial direction. In a second embodiment, a forging die as shown in Fig. 12 is used, in which die members 1 and 2 respectively have grooves at similar positions in the radial direction. In the forging die of Fig. 12, for example, the lower die member 1 has clutch spline grooves 9 while the upper die member 2 has helical grooves 7. The clutch spline grooves 9 and the helical grooves 7 are disposed to have similar radii from the axial center. The upper die member 2 with the helical grooves 7 is rotatable relative to the lower die member 1. Fig. 4 shows a final gear product M3, not according to the invention, produced with the forging die of Fig. 12. The gear product M3 of Fig. 4 has spiral teeth 14 continuously overlapping with clutch spline teeth 13, thus having an extremely high strength. Gear products having such features could not have been mass-produced by any means hitherto. When the forging die is modified in the same manner as the first arrangement, a fin may be formed between two types of teeth. Fig. 5 shows a final gear product M4 having features according to the present invention, that is in which a stopper flange 15 is integrally formed in between spiral teeth 14 and clutch spline teeth 13. An example of other modifications is shown in Fig. 6. A gear product M5 of Fig. 6 has clutch spline teeth 13 on a larger diametral section and spiral teeth 14 on a smaller diametral section. A stopper flange may also be formed between the teeth 13 and 14 in this case. The invention may be changed, varied, or modified in many forms and ways other than those mentioned above without departing from the scope of the appended claims. The most essential feature of the gear product of the invention is that gear members with different types of teeth are integrally forged and continuously arranged without any clearance therebetween to be adjacent to each other and, according to the present invention, via a flange. Typical examples of gear products of the invention are schematically shown in Fig. 13. These gear products are compact and light in weight and have sufficient strength can be mass-produced at a relatively low cost. Although all the gear products of the above embodiments have gear members with two different types of tooth profiles, that is, a helical tooth profile and a straight tooth profile, the gear product may have plural helical tooth profiles or plural straight tooth profiles. The gear product may also have three or more gear members with teeth as long as a smaller diametral member is not placed between larger diametral members. The position of the flange as well as the number, diameter, thickness and module of teeth may be changed as occasion demands. Typically, there is no clearance between gear members or between a gear member and a flange in the gear product of the invention. However, the gear product of the invention may have a clearance 16 between plural gear members as shown in Fig. 14 as occasion demands. Fig. 14 shows example M12 of such a modification. Such a modified gear product is favorably applicable to a device which has been used with a conventional gear product having a clearance.

Claims: A gear product (M) comprising a plurality of gear members (13, 14), having different tooth profiles around a periphery thereof, and an externally-extending flange (15), which are coaxially arranged and are integrally forged by a stamping process, the gear members and flange (15) being in intimate contact with one another and being free of clearance therebetween, characterised in that the flange (15) is formed in between a pair of said gear members (13, 14). A gear product in accordance with claim 1, in which said gear members comprise (A) a helical gear member (14) with a spiral tooth profile and (B) a clutch spline member (13) with a straight tooth profile. A gear product in accordance with claim 2, in which said clutch spline member (13) has teeth having guide chamfer means on one end thereof. A gear product according to claim 1, 2 or 3, comprising: a smallest diametral boss element (12c); a smaller diametral element (12b) with clutch spline teeth (13); a larger diametral element (12a) with spiral or helical teeth (14); and a flange (15); wherein said smallest-diametral boss element, said smaller diametral element, said flange and said larger diametral element are in axial succession and in intimate contact with one another, and being free of any clearance therebetween. A gear product according to claim 1, comprising: a first portion (12b) of a first diameter having clutch spline teeth (13); a flange (15); and a second portion (12c) of a second diameter similar to said first diameter having spiral or helical teeth (14); wherein said first portion, said flange and said second portion are arranged in axial succession and in intimate contact with each other, and being free of any clearance therebetween. A gear product according to claim 1 comprising: a smallest-diametral boss portion (12c); a smaller diametral portion (12b) with helical or spiral teeth (14); a flange (15); and a larger diametral portion (12a) with clutch spline teeth (13); wherein said smallest-diametral boss portion, said smaller diametral portion, said flange and said larger diametral portion are arranged in axial succession and in intimate contact with one another, and being free of any clearance therebetween. A gear product according to claim 6, wherein each of said clutch spline teeth (13) has guide chamfer means on one end thereof. A gear product according to claim 2, wherein the flange (15) is integrally formed with the helical gear member (14). A gear product according to claim 8, wherein the flange (15) is interposed between the helical gear member (14) and the clutch spline member (13).

Inventors: HOGUCHI TETSUYA, HOGUCHI, TETSUYA
Applicants: O OKA FORGE CO LTD, O-OKA FORGE CO., LTD.
Application year: 1993
Main classification: F16H55
IPC codes: B21K1, F16D23, F16H55, F16D11