Method of removing alkali metal compounds from a polymer

Abstract: A process for separating an alkali metal or alkali metal compound from a polymer comprising a conjugated diene and/or an alkenyl aromatic hydrocarbon monomer wherein a polymer and one or more alkali metal compounds is contacted with a suitable solid adsorbent. Preferably, the solid adsorbent will be selected from the group consisting of alumina, silica-alumina, silica and mixtures thereof.

Description: This invention relates to a process for separating alkali metal compounds from a block copolymer. More particularly, this invention relates to a method for removing alkali metal compounds from a block copolymer comprising a conjugated diene and an alkenyl aromatic hydrocarbon monomer unit. Heretofore, several methods have been proposed for separating certain alkali metal compounds (cf. DE-A-3 520 103 or GB-A-1 218 221), particularly lithium compounds from a polymer, particularly a conjugated diene polymer. In general, these methods involve contacting the polymer and alkali metal-containing composition with water and/or an acid. A principal problem associated with these methods is that each introduces an impurity into the polymer which must be removed before the polymer is suitable for at least most end use applications. These methods, then, add a rather complicated separation step to the processes. While the separation processes may be reasonably successful they frequently result in at least a small amount of impurity remaining in the polymer composition. Also, the separation step is an added, rather complicated, step in preparing the polymer composition for its various end use applications. The need, then, for a process which will separate alkali metal compounds, particularly lithium compounds, from a polymer comprising a conjugated diene and/or an alkenyl aromatic hydrocarbon monomer without introducing impurities thereto and without introducing a rather complicated "clean-up" or purification step is believed to be readily apparent. It has now been discovered that the foregoing and other disadvantages of the prior art processes for separating alkali metal compounds, particularly lithium compounds, from a polymer comprising a conjugated diene and/or an alkenyl aromatic hydrocarbon can be avoided or at least significantly reduced with the method for separating alkali metal compounds, particularly lithium compounds, and an improved process provided thereby. It is, therefore, an object of this invention to provide an improved process for separating alkali metal compounds, particularly lithium compounds, from a polymer comprising a conjugated diene and/or an alkenyl aromatic hydrocarbon monomer. It is another object of this invention to provide such an improved process wherein the alkali metal compounds are separated without introducing an impurity therein. It is another object of this invention to provide such an improved process wherein the alkali metal compounds can be separated with a reduced number or at least simpler processing steps. This invention provides a process for separating certain alkali metal compounds from a block polymer comprising at least one conjugated diene monomer block and at least one alkenyl aromatic hydrocarbon monomer block, said block copolymer being in the liquid form or in solution and containing one or more alkali metal compounds, comprising the steps of: (a) contacting the block copolymer with a solid adsorbent which has a particle size within the range of from 0.15 to 12.0 mm and a pore size within the range of from 30 to 10000 nm, and which is selected from the group consisting of alumina, silica-alumina, silica and mixtures thereof; (b) separating the solid adsorbent from the block copolymer solution when necessary: and (c) recovering the block copolymer containing a reduced amount of alkali metal compounds. The adsorbents will, of course, be solids and can readily be separated from the polymer composition by physical separation means or the alkali metal compound containing composition can be passed over a fixed bed of such solid adsorbents. Such a separation will, of course, separate all the solid compounds and not introduce any therein thereby leaving the polymer composition free of any impurities introduced as a result of the separation process. The improved process for separating certain alkali metal compounds of this invention offers the advantage of producing a polymer free of any impurities introduced as a result of the alkali metal compound separation step and aside from the step required to separate the solid adsorbent, when this technique is used, does not really introduce any additional steps to the process. The certain alkali metal compounds can be removed from the polymer composition by contacting the polymer solution with a suitable solid adsorbent. Suitable solid adsorbents are high surface area adsorbents including alumina, silica alumina and silica. Suitable high surface area solid adsorbents will have a particle size within the range of from 0.15 to 12 mm and a pore size within the range from 30 to 10,000 nm. Solid adsorbents within the ranges heretofore noted will work best when dry at the larger particle size and pore sizes within the ranges set forth and will work best wet when smaller particle size and smaller pore sizes within the ranges set forth are used. When the suitable solid adsorbent is used wet from about 10 to 100% of its pore volume will be occupied by water. The higher water contents within this range are most suitable for the smallest pore sizes and smallest particle sizes within the range heretofore recited. In general, during separation of the certain alkali metal compounds, the polymer may be present in a suitable solvent at a concentration within the range from 1 to 30 weight percent, based on total solution, and the certain alkali metal compounds may be present at a concentration within the range from 0.005 to 5 wt% based on polymer. In general, the contacting will be accomplished at a temperature within the range from 5 to 100 °C, a pressure within the range from 1 to 42 bar (0 to 600 psig) and at a nominal holding time within the range from 10 to 100 minutes. It will, of course, be appreciated that low molecular weight, liquid, polymers could be used in the process of this invention without a solvent (i.e. 100% solids content). In general, the method of this invention can be used to separate certain alkali metal compounds from any block copolymer comprising a conjugated diene block and an alkenyl aromatic hydrocarbon monomer block which is prepared with an alkali metal or an alkali metal compound catalyst or initiator. Such block copolymers will copolymerize using alkali metal or alkali metal compound catalysts or initiators. In general, the conjugated diene will contain from 4 to 12 carbon atoms. Examples of suitable conjugated dienes are 1,3-butadiene, isoprene, piperylene, methylpentadiene, phenylbutadiene, 3,4-dimethyl-1,3-hexadiene, 4,5-diethyl-1,3-octadiene and the like. The alkenyl aromatic hydrocarbon monomer generally will contain from 8 to 14 carbon atoms. Examples are styrene, various alkyl substituted styrenes such as alpha-methyl styrene, and ethyl styrene, alkoxystyrenes such as paramethoxystyrene, and ethoxystyrene, vinylnaphthalene, and vinyltoluene. The block copolymer may be hydrogenated or neat during the alkali metal compound separation step although, generally, it is desirable to separate the lithium compounds prior to hydrogenation. As indicated above, the block copolymer will generally be in solution when the alkali compounds are removed but as indicated previously, this is not necessary with liquid polymers. Preferably, the polymer will be in the same solvent as it was prepared but, as a practical matter, essentially any suitable hydrocarbon solvent could be used to place the polymer in solution. Suitable solvents include, but are not necessarily limited to, hydrocarbons such as paraffins, cycloparaffins, alkyl substituted cycloparaffins, aromatics and alkyl substituted aromatics, all containing from 6 to 10 carbon atoms per molecule. Specific suitable solvents include benzene, toluene, cyclohexane, cyclopentane, methylcyclohexane, n-butane, n-hexane, and n-heptane. Ethers, such as diethyl ether, and tetrahydrofuran, can also be used. As is well known, the polymer can be prepared in any one or more of these solvents or the solvent used for preparation can be separated using suitable means and the polymer dissolved, when necessary, in a different solvent. As indicated previously, the alkali metal compound will be separated by contacting with a suitable solid adsorbent. In general, the solid adsorbent will be used at a concentration within the range from 1 to 50 weight percent based on polymer. It will, of course, be appreciated that higher solid adsorbent concentrations will be most effective and would, generally, lead to the use of shorter contacting times. The alkali metal compounds may be in solution or suspended prior to and at least initially during the separation process. As indicated previously, the polymer solution may be passed over a bed of suitable solid adsorbent or the solid adsorbent may be combined with suitable mixing with the polymer solution and then separated using physical separation means. Suitable physical separation means include centrifugal means, filtration means or settling means. Useful centrifugal means include centrifuges and cyclones. Suitable filtration means include rotary and fixed bed filtration apparatus and the like. Decantation or sedimentation in parallel plate separators may also be used to separate the suitable solid adsorbent from the polymer solution. Passing of the polymer solution over a fixed bed of the suitable solid adsorbent is preferred since this method reduces the number of steps required to produce a polymer for any end use. In general, any alkali metal compound commonly found in a polymer solution when an alkali metal compound is used as the catalyst or initiator can be separated from the polymer with the method of this invention as can any alkali metal compound produced as a result of coupling an alkali metal compound polymerized polymer. Alkali metal compounds most commonly separated, however, will be the compounds normally produced when an alkali metal catalyst or initiator is deactivated. These include alkali metal hydrides, alkali metal alkoxides, alkali metal hydroxides or compounds produced as the result of coupling. In this regard, when the polymer is coupled, any coupling agent known in the prior art such as divinylbenzene, and silicon halides can be used. Interestingly, alcohol can, in some cases, be used to enhance the separation of this process. Alcohol will, generally, enhance separation effected with larger particle size larger pore size solid adsorbents. When an alcohol such as methanol is used, alkali metal compounds produced when deactivating an alkali metal catalyst or initiator, such as alkali metal hydride and alkali metal hydroxide, will be converted to the corresponding alkali metal alkoxide. This conversion also apparently occurs when an alkali metal halide is separated and an alcohol is used. This, then, has an added advantage of converting harder to separate alkali metal compounds to the more readily separated alkali metal alkoxides. When an alcohol is used it will, generally, be used at a concentration within the range from 0.1 to 10 moles alcohol per mole of alkali metal compound. In a preferred embodiment of the present invention, alumina will be used to separate a lithium halide and/or a lithium methoxide from a block copolymer comprising at least one conjugated diene monomer block and at least one aromatic hydrocarbon monomer block. In a most preferred embodiment, the conjugated diene will be either isoprene or butadiene and the alkenyl aromatic hydrocarbon monomer will be styrene. In the preferred embodiment, the polymer solution will be diluted to a polymer concentration within the range from 5 to 25 weight percent polymer based on total solution. In the preferred embodiment of this invention, contacting between the alumina and the lithium compound-containing polymer will be accomplished at a temperature within the range from 15 to 60 °C, a total pressure within the range from 2.7 to 15 bar (25 to 200 psig) and at a nominal holding time within the range from 20 to 100 minutes. The alumina will be used at a concentration within the range from 5 to 25 weight percent based on polymer. Having thus broadly described the present invention and a preferred and most preferred embodiment thereof, it is believed that the invention will become even more apparent by reference to the following examples. It will be appreciated, however, that the examples are presented solely for purposes of illustration and should not be construed as limiting the invention. Example 1 In this example, silica having a particle size of about 1.6 mm and a pore size of 600 nm was used to separate lithium bromide from an SBS block copolymer comprising a butadiene polymer block having a number average molecular weight of 60,000 and styrene polymer blocks, each having a number average molecular weight of 10,000. The polymer and lithium bromide were contained in a solvent comprising 75 weight percent cyclohexane and 25 weight percent isopentane at a concentration of 35 weight percent. During the separation, the polymer concentration was reduced to 17.8 weight percent by adding additional cyclohexane. The polymer solution contained 385 ppm lithium bromide. The contacting between the silica and the lithium bromide containing polymer solution was effected at a temperature of 25 °C, at ambient pressure and at a holding time of 72 hours. Three different runs were completed in this example. In the first run, the silica was used dry, in the second run the silica was used with 50 volume percent of its pores filled with water and, in the third run, the silica was used with 100% of its pore volume filled with water. After 72 hours, the polymer was decanted, diluted with tetrahydrofuran and analyzed for bromide content. 27.4% of the bromide was removed with the dry adsorbent, 79.1% of the bromide was removed with the 50% wet adsorbent and 87.9 weight percent of the bromide was removed with the 100% wet silica sample. The separation was accomplished, in each case by introducing three ounces of the polymer cement with the adsorbent into a bottle and then allowing the bottle to roll at a medium speed for 72 hours. Example 2 In this example, alumina having a particle size of about 1.6 mm and a pore size of primarily 30 to 10,000 nm was used to separate lithium bromide from a block copolymer comprising a butadiene block having a number average molecular weight of 60,000 and styrene polymer blocks of number average molecular weight of 10,000. Again, the polymer was contained, initially, in a solvent comprising 75% cyclohexane and 25% isopentene and the polymer was diluted from a concentration of 35 weight percent to 17.8 weight percent based on total solution. The polymer feedstock contained 385 parts per million lithium bromide. The contacting between the alumina and the lithium bromide containing polymer solution was effected at a temperature of 25 °C, ambient pressure and at a holding time of 72 hours. Three different runs were again completed in this example. In the first run, the alumina was used dry, in the second run, the alumina was used with 50% of its pore volume filled with water and in the third run the alumina had 100% of its pore volume filled with water. After completion of each run the polymer cements were decanted, diluted with tetrahydrofuran and analyzed for bromide concentration. In the three runs, the amount of bromide actually separated was 24.0 weight percent when the alumina was dry, 57.3 weight percent when the alumina was 50% wet and 76.6 weight percent when the alumina was 100% wet. Example 3 In this example, the three runs of Example 2 were repeated except that an alumina having a particle size of about 4.0 mm and a pore size of primarily 30 to 10,000 nm was substituted for the alumina used in Example 2. After the runs were completed, the polymer was analyzed for bromide content and the amount of bromide removed was 59.9% when the alumina was used dry, 47.7 weight percent when the alumina was used 50% wet and 91.0 weight percent when the alumina was used 100% wet. Example 4 In this example, the runs of Example 2 were repeated except that an alumina having a particle size of about 0.8 mm and a pore size of about 90 nm was substituted from the alumina used in Example 2. After the runs were completed, the polymer was analyzed and the amount of bromide actually removed determined. In this example, the amount of bromide actually removed was 37.0 weight percent when the alumina was used dry, 72.6% when the alumina was used 50% wet and 87.3 weight percent when the alumina was used 100% wet. Example 5 In this example, the three runs of Example 2 were repeated except that an alumina having a particle size of about 1.3 mm and a pore size of about 90 nm was substituted for the alumina used in Example 2. In this example, the amount of lithium removed was 39.3 weight percent when the alumina was dry, 77.7 weight percent when the alumina was 50% wet and 54.8 weight percent when the alumina was 100% wet. Example 6 In this example, the runs of Example 2 were repeated except that an alumina having a particle size of about 0.2 mm and a pore size of primarily 30 to 10,000 nm was substituted for the alumina used in Example 2. After the runs were completed, it was determined that 71.8 weight percent of the lithium was removed when the alumina was used dry, 96.9 weight percent of the lithium was removed when the alumina was used 50% wet and 95.8 weight percent of the lithium was removed when the alumina was used 100% wet. Example 7 In this example, the runs of Example 6 were repeated except that an alumina having a particle size of about 0.6 mm was used. After the runs were completed, it was determined that 60.2 weight percent of the lithium was removed when the alumina was used dry, 92.4% weight percent of the lithium was removed when the alumina was used 50% wet and 89.8 weight percent of the lithium was removed when the alumina was used 100% wet. Example 8 In this example, the three runs of Example 6 were again repeated except that an alumina having a particle size of about 1.8 mm was used. After the runs were completed it was determined that 53.1 weight percent of the lithium was removed when the alumina was used dry, 60.2 weight percent of the lithium was removed when the alumina was used 50% wet and 88.1 weight percent of the lithium was removed when the alumina was used 100% wet. Example 9 In this example, silica having a particle size of 1.6 mm and a pore size of 600 nm was used to separate lithium bromide from an SBS block copolymer comprising a butadiene polymer block having a number average molecular weight of 60,000 and styrene polymer blocks of number average molecular weight of 10,000. Again, the polymer was contained, initially, in a solvent comprising 75% cyclohexane and 25% isopentane. Initially, the polymer was at 35 weight percent in solution but it was diluted to 19 weight percent, based on total solution, before the lithium was removed. The polymer feedstock solution contained 442 ppm lithium bromide. The contacting between the silica and the lithium bromide containing polymer solution was effected at a temperature of 25 °C, ambient pressure and at a holding time of 72 hours. Three different runs were completed in this example. In the first run, the silica was used dry, in the second run the silica was used with 50% of its pore volume filled with water and in the third run the silica had 100% of its pore volume filled with water. The polymer was contacted with the silica by placing three ounces of polymer solution with the requisite amount of silica in a jar and allowing the jar to roll at medium speed. Methanol was added to the polymer solution prior to mixing with the silica at a concentration of 5.5 moles methanol per mole of lithium in the polymer. In the three runs completed in this example, the amount of lithium removed was 82.1 weight percent when the alumina was dry, 97.3 weight percent when the alumina was 50% wet and 96.8% when the silica was 100% wet. Example 10 In this example, the three runs of Example 9 were repeated except that an alumina having a particle size of about 1.6 mm and a pore size of primarily 30 to 10,000 nm was substituted for the silica. The amount of lithium removed in the three runs was 76.4 weight percent when the alumina was dry, 75.7 weight percent when the alumina was 50% wet and 91.2 weight percent when the alumina was 100% wet. Example 11 In this example, the runs of Example 9 were repeated except that an alumina having a particle size of about 4.0 mm and a pore size of primarily 30 to 10,000 nm was substituted for the silica. After the runs were completed, it was determined that 83.1 weight percent of the lithium was separated when the alumina was dry, 46.7 weight percent of the lithium was removed when the alumina was 50% wet and 80.8 weight percent of the lithium was removed when the lithium was 100% wet. Example 12 In this example, the three runs of Example 9 were repeated except that an alumina having a particle size of about 0.8 mm and a pore size of about 90 nm was substituted for the silica. After the runs were completed, it was determined that 75.9 weight percent of the lithium was removed when the alumina was dry, 79.1 weight percent of the lithium was removed when the alumina was 50% wet and 69.5 weight percent of the lithium was removed when the alumina was 100% wet. Example 13 In this example, the three runs of Example 9 were repeated except that an alumina having a particle size of about 1.3 mm and a pore size of about 90 nm was substituted for the silica. After the runs were completed, it was determined that 80.0 weight percent of the lithium was removed when the alumina was dry, 82.8 weight percent of the lithium was removed when the alumina was 50% wet and 66.8 weight percent of the lithium was removed when the alumina was 100% wet. Example 14 In this example, the three runs of Example 9 were repeated except that an alumina having a particle size of about 0.2 mm and a pore size of primarily 30 to 10,000 nm was substituted for the silica. After the runs were completed, it was determined that 87.2 weight percent of the lithium was removed when the alumina was dry, 96.8 weight percent of the lithium was removed when the alumina was 50% wet and 97.3 weight percent of the lithium was removed when the alumina was 100% wet. Example 15 The three runs of Example 14 were repeated with the alumina having a particle size of about 0.6 mm with the following results: 84.5 weight percent of the lithium was removed when the alumina was dry, 93.6 weight percent of the lithium was removed when the alumina was 50% wet and 96.3 weight percent of the lithium was removed when the lithium was 100% wet. Example 16 The three runs of Example 14 were again repeated with an alumina having a particle size of about 1.8 mm with the following results: 90.4 weight percent of the lithium was removed when the alumina was dry, 71.5 weight percent of the lithium was removed when the alumina was 50% wet and 94.4 weight percent of the lithium was removed when the alumina was 100% wet. The results obtained when the alumina was 50% wet in this example are somewhat out of line when compared to the results obtained in Examples 14 and 15 and the reason for this is not known. As will be apparent from reviewing the data set forth in Examples 1-16 and by comparing the results achieved in Examples 9-16 with the results of Examples 1-8 the most effective adsorbent will contain either 50 or 100% water when no alcohol is used and the use of an alcohol, particularly methanol, enhances the separation, particularly when the adsorbent is otherwise dry. 50% water content in the adsorbent seems to be most effective at moderate particle size and pore size while 100% water appears to be most effective at small particle and small pore sizes.

Claims: A process for separating certain alkali metal compounds from a block copolymer comprising at least one conjugated diene monomer block and at least one alkenyl aromatic hydrocarbon monomer block, said block copolymer being in the liquid form or in solution and containing one or more alkali metal compounds, comprising the steps of: (a) contacting the block copolymer with a solid adsorbent which has a particle size within the range of from 0.15 to 12.0 mm and a pore size within the range of from 30 to 10000 nm, and which is selected from the group consisting of alumina, silica-alumina, silica and mixtures thereof; (b) separating the solid adsorbent from the block copolymer solution when necessary; and (c) recovering the block copolymer containing a reduced amount of alkali metal compounds. The process of claim 1 wherein the nominal contacting time in step (a) is within the range from 10 to 180 minutes. The process of claim 1 or 2 wherein said conjugated diene is selected from the group consisting of butadiene and isoprene and said alkenyl aromatic hydrocarbon monomer is styrene. The process of any one of claims 1 to 3 wherein the polymer is contained in a suitable liquid hydrocarbon and the concentration of said polymer is within the range from 1 to 30 weight percent based on total solution. The process of any one of claims 1 to 4 wherein the concentration of the solid adsorbent is within the range from 5 to 25 weight percent. The process of claim 1 wherein step (a) comprises passing said alkali metal compound containing polymer over a fixed bed of the solid adsorbent. The process of any one of claims 1 to 6 wherein an alcohol is used in the absence of water to enhance the separation of the alkali metal compounds, this alcohol being employed in a concentration of 0.1 to 10 moles alcohol per mole of alkali metal compound. The process of claim 7 wherein methanol is used in combination with the solid adsorbent to effect separation of the alkali metal compound.

Inventors: BALAS JAROSLAV GEORGE, LOGAN LORALEE ANN, MASSIE STEPHEN NEIL, BALAS, JAROSLAV GEORGE, LOGAN, LORALEE ANN, MASSIE, STEPHEN NEIL
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1993
Main classification: C08F6
IPC codes: C08C2, C08F6