LAYERED CHIP STRUCTURE

Abstract: A method for making a substrate for use in a multilayered integrated circuit or multichip module which includes coating a conductive material (14) on a surface of a support sheet (10) to form a conductive circuit (12) and then drying the sheet. Next, a coating of a layer of dielectric layer (18) is placed on the support surface in the areas where the conductive material is not cast. After which the coated sheet is densified to form a densified conductive circuit embedded dielectric layer. A second coating of a dielectric (28) is placed over the first densified conductive circuit embedded dielectric layer such that the second layer is characterized by vias (30) therein which are in register with at least a portion of the conductive circuit (12). The vias in the second dielectric layer are filled to form electrically conductive vias and then densified to form the substrate (44).

Description: TITLE Layered Chip Structure CROSS REFERENCE TO RELATED APPLICATIONS This application is a continuation-in-part of U.S. Serial No. 07/504,330 filed April 3, 1990 now U.S. Patent No. 5,101,319 issued March 31, 1992. BACKGROUND OF THE INVENTION 1. Field of the invention The present invention relates to a composite multilayer substrate that is used in the manufacture of multilayered IC's or multichip modules. 2. Description of the prior art It is well known in the prior art to utilize a thin film structure that can be formed from multilayers of either high or low temperature pre-fired or co-fireable ceramic green tape with power and ground connections between the multilayers. The so-called co-fireable ceramic tape is a flexible substrate in the green (unfired) state before heating and is manufactured by various companies including DuPont who sells its product under the trademark Greentape. The thin and flexible material becomes rigid after it is subjected to heat as by - firing in an oven. Typically this greentape is commercially available for use with high density packages of IC's. In some cases, a high temperature plastic material, such as polyimides, are used as a substrate for co-fireable structures. Electrically conductive circuits are screen printed or otherwise deposited on the dielectric substrate. Connections between layers of the substrate that are aligned and stacked are made by forming vias and filling with a conductive material. The substrates are typically machined or formed; fired if necessary and drilled using mechanical tools, lasers or chemical etching. Both active and passive components are attached individually onto the substrates, which substrates have suitable dielectric thermal and physical properties, and are connected electrically to the circuit by proper placement and soldering by using conductive cements. Often the circuits, including printed resistors and layered capacitors, are fired before other components are attached to each substrate and the substrates aligned, stacked, packaged and tested. Current ultilayered ICs or multichip modules have low manufacturing yields and premature field failures due to substrate cracks, conduit electrical shorts and poor component adhesion to the substrate. These problems increase the number of layers required and increase component density. Often the vias will crack as a result of material expansion mismatch, residual stress in the substrate and poor via filling. SUMMARY OF THE INVENTION The present invention uses a densified dielectric with an embedded conductive circuit which allows the use of stronger, thinner and flatter layers. The invention improves alignment between layers andvias, reduces layer manufacturing costs and allows use of a wider variety of substrate materials. Gravure printing of the vias improves line resolution, lowers print costs for high volume runs and improves print-to-print duplication accuracy. The process of the invention reduces the number of steps in forming a substrate resulting in a stronger but more compact substrate which has better line resolution, produces smaller vias with improved contact, lowers residual stress levels in the layers and reduces the cost of manufacturing. Broadly the invention comprises a process for producing a substrate and the substrate produced by the process. A conductive circuit is formed on a support surface, such as a polyester, polyethylene, polyimide, film etc. Subsequently, a dielectric having the same thickness as the conductive circuit is placed on the support surface covering the areas of the support surface that are not covered by the conductive circuit thereby forming a first conductive circuit surrounded on three sides by a dielectric layer. The first dielectric layer is densified as taught in the parent application. The thickness of the first dielect-ric layer may be between 50 to 500 m inches after densification. The conductive circuit may include printed electrodes for capacitors or resistors. These conductive circuits may be printed by screen printing, ink jet, gravure roll or vapor deposition. The dielectric may be applied by screen printing, ink jet or gravure roll. Subsequently, a second dielectric layer is formed over the first dielectric layer, which second layer is characterized by properly positioned voids, termed vias. These vias are preferably circular but may have other geometric shapes. They range in size from 50 to 1,000 m inches in diameter. These vias are formed where it is desired to ultimately have an electrical connection between the circuit and a component to be attached to the substrate. The second dielectric layer may range from 0.3 to 10 mils in thickness. Subsequently, a conductive material, such as a conductive ink, which is compatible with the electrical characteristics of the circuit is deposited into and fills the vias in the second dielectric layer forming the conductive paths. Separate depositions of the same conductive materials into the vias in the second dielectric layer, separate depositions of different conductive materials into different vias in the second dielectric layer and/or the formation of additional second dielectric layers with the same and/or different conductive materials in the vias with single or multiple depositions are within the scope of the invention. Preferably, for forming the second dielectric layer and depositing the ink, gravure rolls are used. However, other depositing, casting or coating techniques can be used. Subsequently, the ink-filled second dielectric layer is then densified, again in accordance with the teachings of the parent application to form an unfired substrate. The densification, in addition to flattening and compacting the layers, also insures that the vias have flush contact with the circuit and are flush with the top or outer surface of the second dielectric layer. Additionally, a final thick layer 1 to 10 mils of dielectric base may be deposited. Lastly, the substrate is co-fired. BRIEF DESCRIPTION OF THE DRAWINGS Figures 1 is a schematic illustration of the steps of a process embodying the invention; Figure 2 is a plan view of the substrate formed in accordance with the process of Figure 1; and Figure 3 is a side view of the product. DESCRIPTION OF THE PREFERRED EMBODIMENT(S) The invention will be described in reference to the formation of a substrate which can be used as a component in the manufacture of multilayered ICs or multichip modules. Referring to Figure 1, a support sheet 10, such as a polyimide film of 2 mils thickness, has at 14 a conductive ink printed -thereon, such as by a gravure roll, to form a conductive circuit 12. The printed sheet then passes under a dryer 16 at a temperature of between 120 to 220oF. Subsequently, a first dielectric layer 18 is deposited at 20 on the sheet 12, such as by a gravure roll, where the dielectric 18 is coated on the non electrode coated areas of the sheet. The dielectric 18 is then dried at 22 at a temperature of between 120 to 220oF forming a first circuit surrounded on three sides by a dielectric layer. Subsequently, the first layer is calendered (densified) at 24 by passing through calender rolls 24a and 24b at a nip pressure of 600 psi and room temperature. A variety of calendering temperatures ranging from OoC to 200oC and calendering pressures ranging from 10 psi to 4,000 psi may be used to impart specific enhancements to the resulting first dielectric layer. This step densities and enhances the uniformity and flatness of the layer. The layer is reduced in thickness approximately 10 to 15%. In this step, the bumps or roughness inherently found in inks and dielectrics are substantially eliminated and the thickness of the layer does not vary more than 5 to 10% from an average thickness resulting again in a superior 'flat' layer. The densified first dielectric layer can be between 50 to 500 m inches. At 26 a second dielectric layer 28 is applied, such as by a gravure roll which gravure roll has projections thereon which result in vias 30 being formed in the second dielectric layer 28. The film is then dried by a dryer 31 at a temperature of between 120 to 220oF. At 34 ink 32 is deposited in the vias 30, such as by a gravure roll. The ink-filled second dielectric layer is then dried at 36 at a temperature of between 120 to 220oF. Subsequently, the first and second layers are calendered at 38 by calender rolls 38a and 38b at a nip pressure of 600 psi to form an unfired substrate 40. This second dielectric layer is reduced in thickness 5 to 25% and can have a thickness ranging between 0.3 to 10 mils. Again, a variety of calendering temperatures ranging from OoC to 200oC and calendering pressures ranging from 10 psi to 4,000 psi may be used to impart specific enhancements to the resulting second dielectric layer. This step densities and enhances the uniformity and flatness of the layer. In this step, the bumps or roughness inherently found in inks and dielectrics are substantially eliminated and the thickness of the layer does not vary more than 5 to 10% from an average thickness resulting again in a superior 'flat' layer. The densified second dielectric layer can be between 1 to 10 mils. The substrate 40 is co-fired at 42 in an oven to form the fired substrate 44. Typically, the foregoing process is carried out using multitrack or in-line series head coaters with multiple drying and calendering stages. These units maintain registration from print to overlay print by use of mechanical, optical or laser alignment devices. The preferred embodiment has been described with reference to a particular range of processing conditions. Obviously, depending upon the dielectric material used, relative thickness, conductive materials, such as gold, conductive glass, conductive inks, etc., the process conditions will vary. A dielectric such as described in the parent application is suitable for purposes of the preferred embodiment of the invention. Other comparable commercially available dielectrics are also suitable for purposes of the invention as well as various combinations of the conductive materials. Aparticularlypreferred conductive material would be a blend of 85% Ag and 15% palladium. The foregoing description has been limited to a specific embodiment of the invention. It will be apparent, however, that variations and modifications can be made to the invention, with the attainment of some or all of the advantages of the invention. Therefore, it is the object of the appended claims to cover all such variations and modifications as come within the true spirit and scope of the invention. Having described my invention, what I now claim is:

Claims: Claim 1. A method for making a substrate for use in a multilayered integrated circuit or multichip module which includes: coating a conductive circuit on a support surface; coating a dielectric on the support surface in the areas where the conductive circuit is not cast; densifying to form a first conductive circuit embedded dielectric layer; coating a second dielectric layer over the first electrode embedded dielectric layer, said second layer characterized by vias therein which are in register with at least a portion of the conductive circuit; filling the openings in the second dielectric layer to form electrically conductive vias; and densifying the second conductive layer to form the substrate. Claim 2. A substrate for use in a multilayered integrated circuit or multichip module which comprises: a densified first dielectric layer having a conductive circuit embedded therein the outer surfaces of the circuit and dielectric being substantially coplanar; a second densified dielectric layer formed integrally with the first layer, the second layer having vias with conductive material deposited therein, the material in electrical communication with the circuit.

Inventors: RAINWATER JEWEL G, RAINWATER, JEWEL, G.
Applicants: VISTATECH CORP, VISTATECH CORPORATION
Application year: 1993
Main classification: B05D5
IPC codes: B05D5, H01L21, H01L23, H05K3