ION-CONDUCTIVE POLYMER AND ELECTROLYTE ADDITIVES

Abstract: Compounds are provided for use in an electrolyte comprising repeating unit selected from the group consisting of cyclic and heteorcyclic species having y carbon atoms and z heteroatoms, X, and where y is 4, 5 or 6 and z is 0, 1 or 2. The heteroatom is selected from the group consisting of O, S and N. The repeating unit is further substituted by four to six pendant groups having the formula (CHR1)mO(CHR1CHR1O)nY, where the majority of pendant groups comprises at least two O and further, in which m is 0 or 1; in which n is in the range of 0 to 25, in which each R1 is the same or different and R1 is selected from the group consisting of H, alkyl, allylic and alkenyl radicals having 1 to 18 carbon atoms and Y, and in which each Y is the same or different and Y is a functional group selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species. Electrolytes, plasticizers and macro-ions prepared from these compounds are described.

Description: Ion-Conductive Polymer and Electrolyte Additives Background of the Invention This invention relates to electrolyte solvent and/or electrolyte additives for electrolytic cells and electrochemical devices, such as batteries, capacitors, fuel cells and displays, prepared therefrom. It further relates to novel electrolyte compositions for electrolytic cells. Success of an alkali metal-based electrochemical devices requires the use of aprotic solvent-based electrolytes. These electrolytes must be electrochemically stable towards both cathode and anode materials. In devices such as batteries, these electrolytes must be highly conductive in order to allow useful current to be drained during use. Current liquid aprotic electrolytes are characterized by low ionic conductivity and poor electrochemical stability. The latter leads to decomposition of the electrolyte. Decomposition products then lead to the formation of highly resistive layers at the surface of the electrodes (high interfacial impedance), which further limits the current density and useful cycle life of the device. This represents a major obstacle to the development of an alkali metal-based electrochemical device technology. In order to overcome the difficulties inherent in liquid electrolytes, solid polymer electrolyte (SPE) materials have been developed in which ion mobility is possible through coordination of an electrolyte ion with suitable sites on the polymeric chain. Prior art polymer electrolytes have used high molecular weight polyethers (PEO) as solvents. However, PEO is crystalline at ambient temperature (20 °C) with an adverse effect on the conductivity. Gel-polymers, in which plasticizers, such as dimethoxy ethane, propylene and ethylene carbonate and acetonitrile, are added to the polymer, have also been used as solvents. The lower molecular weight plasticizers are of lower viscosity and allow greater segmental motion in the polymer, thereby enhancing ion mobility in solution. Addition of plasticizer increases conductivity to a value approaching that of the plasticizer-alone conductivity and also decreases the temperature dependence of conductivity. However, most of the prior art plasticizers are unsuitable for use in alkali metal-based batteries because they have SUBSTITUTE SHEET higher vapor pressures and/or are unstable with respect to alkali metals. In these respects, gel polymers are similar to aprotic liquid electrolyte systems. Another problem which arises in current solid polymer electrolyte technology is anionic polarization in the electrolyte layer. The anions migrate during use, thereby forming a charge gradient in the electrolyte. The anions migrate only very slowly back to their original position resulting in prolonged polarization of the cell. Therefore, attempts have been made to prepare a single- ionic mobility solid polymer electrolyte in which only the cations are mobile, while the anions are fixed to the polymeric chain. In U.S. Patent No. 5,098,589 to Motogami et al, a solid polymer for use in an electrolyte is disclosed which is formed by cross-linking an organic compound derived from glycerol and having an average molecular weight of 1,000 to 20,000. The compound contains block co-polymer alkoxy pendant groups with substituent alkoxy groups extending therefrom. The pendant groups terminate in an active hydrogen or a polymerizable functional group. Cross-linking or polymerization of the organic compound takes place either at the polymerizable functional group or at the active hydrogen site. Conductivity at room temperature was in the range of 2.9-3.8 x 10 "5 S/cm. In U.S. Patent No. 4,357,401 to Andre et al , a solid polymer electrolyte, a so-called "linear star polymer", based on diaminoethylene and containing block co-polymer ethylene and propylene oxide pendant groups is disclosed. Cross- linking occurs through active hydrogen sites at the pendant termini to provide a polymeric material with a conductivity in the range of 1-40 x 10 "5 S/cm at 100°C. U.S. Patent No. 5,059,443, discloses alkoxylated glucose derivatives containing fatty acid functional end groups for use as a fat substitute. The electrolytic properties of these derivatives were not investigated. Thus far, none of the existing polymer electrolyte materials provide high ionic conductivity, high electrochemical stability and good mechanical properties at useful temperatures (preferably ambient). In addition, prior art liquid and solid polymer electrolytes do not allow for the promotion of the mobility of the ionic species of interest. This lack of control over these critical parameters greatly limits the performance, safety and cycle life of the existing alkali metal SUBSTITUTE SHEET electrochemical device technologies. The present invention overcomes the above- stated limitations of the prior art. It is the object of the present invention therefore, to provide a solid polymer electrolyte with improved conductivity and electrochemical stability and, optionally, with self-plasticizing capability. It is a further object of the present invention to provide improved plasticizers with low vapor pressure, high conductivity and electrochemical stability and compatibility with a variety of electrolytes and cathode and anode materials. It is yet a further object of the invention to provide an electrolytic species having high cationic mobility (high cationic transport number) and low anionic mobility. Summary of the Invention In one aspect of the invention, a compound is provided for use in an electrolyte. The compound includes a cyclic or polycyclic backbone consisting of 1 to 10 repeating unit, C y X z , where the repeating unit is selected from the group consisting of cyclic and heterocyclic species having y carbon atoms and z heteroatoms, X, and where y is 4 , 5 or 6 and z is 0, 1 or 2. The heteroatom is selected from the group consisting of O, S and N. The repeating unit, C y K z , is further substituted by four to six pendant groups having the formula, where the majority of pendant groups comprises at least two O and further, in which m is 0 or 1 , in which n is in the range of 0 to 25, in which each Ri is the same or different and R, is selected from the group consisting of H, alkyl, allylic and alkenyl radicals having 1 to 18 carbon atoms and Y, and in which each Y is the same or different and Y is a functional group selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species. The ionic species contains a cation from the alkali SUBSTITUTE SHEET metal or alkaline earth elements. Unless otherwise stated, the number of each n is an average. Furthermore, to obtain superior electrolytic properties, the morphology of the above and subsequently disclosed compounds should be characterized by a compact backbone and extended pendant groups that is, a "star compound". By "star compound", as that term is used herein, it is meant that the compound possesses a dense core for supporting pendant groups. The core may be cyclic or linear or a combination of cyclic and linear repeating units. The pendant groups extend outward and away from the core, so as to impart to the compound a star- like appearance. The morphology of the compound plays an important role in its performance as an electrolyte constituent. The extended branched arrangement of the pendant groups increases chain mobility and thereby reduces the tendency of the compound to crystallize (decreases T g ). By "plasticizing agent", as that term is used herein, it is meant any non- reactive, electrochemically stable functional group that does not contribute to the crystallinity of the compound. By "alkali metal" as that term is used herein, it is meant the Group la metals of the Periodic Table of the Elements, including lithium, sodium, potassium, rubidium and cesium. By "alkaline earth metal", as that term is used herein, it is meant the Group Ila metals of the Periodic Table of the Elements, including beryllium, magnesium, calcium, strontium and barium. The compound is used in an electrolyte with an electrolytic salt. The cation of the electrolytic salt is solvated by the oxygen of the pendant groups. It has been observed that at least two oxygen per pendant group are required for most of the pendant groups to effect the solubilization of the cation. In another aspect of the invention, a functionalized alkoxylated carbohydrate, such as monosaccharides and oligosaccharides, is provided for use in an electrolyte. The saccharide moiety is selected from the group consisting of pentoses and hexoses and typically has one to five hydroxyl groups. The hydroxyl groups are substituted with a total of between 4 and 150, and preferably a total of between 4 and 60, alkoxy groups attached through ether linkages. The alkoxy groups terminate in a hydroxyl group. Each terminal hydroxyl group of the SUBSTITUTE SHEET carbohydrate is then functionalized with a functional group, Y, selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species. By "carbohydrate", as that term is used herein, it is meant a compound comprised of sugars, sugar alcohols or dehydrated sugar alcohols. "Sugar alcohol" is used in the conventional sense as the reduction product of sugars, wherein the aldehyde or ketone group is reduced to an alcohol. By "oligosaccharide", as that term is used herein, it is meant polysaccharides that yield from two to ten monosaccharide units upon hydrolysis. In another aspect of the invention, a solid polymer electrolyte is provided which contains a solvated cation and a polymer constituted from a compound comprising a linear backbone having 1 to 20 repeating units, C C,*, where the repeating unit is selected from the group consisting of saturated and unsaturated alkyl and alkenyl species containing i carbon atoms and / heteroatoms, X, where is in the range of 1 to 6 andj is in the range of 0 to 3. The heteroatom, X, is selected from the group consisting of O, S, and N. The repeating unit, C / X,, further is substituted by one to six pendant groups having the formula, (CHR 1 ) m Q(CHR 1 CHR 1 Q) n Y. The pendant group is selected such that a majority of the pendant groups contains at least two Q and further, in which m is 0 or 1 , in which n is in the range of 0 to 25, in which Q is a Group la or Group Ila cation-solvating species selected from the group consisting of O, S and NR,, in which each Rj is the same or different and Rj is selected from the group consisting of H, alkyl, allylic and alkenyl radicals having 1 to 18 carbon atoms and Y, and in which each Y is the same or different and Y is a functional group selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species, wherein at least one Y is a polymerizable functionality and at least one Y is a functionality other than a polymerizable functionality. Unless otherwise stated, the number of each n is an average. SUBSTITUTE SHEET The cation may be a monovalent or divalent cation selected from the Group la and Group Ila elements. The cation should be capable of solvation by "Q" of the pendant group, which is oxygen, nitrogen or sulfur. As stated above, most pendant groups should have at least two Q to effect solvation of the cation. In another aspect of the invention, a solid polymer electrolyte is provided which contains a solvated cation and a polymer constituted from a compound comprising a backbone having 1 to 10 repeating units, C^ , where the repeating unit is selected from the group consisting of saturated and unsaturated cyclic and heterocyclic species and saturated and unsaturated alkyl and alkenyl species containing a carbon atoms and b heteroatoms, X, where a is in the range of 1 to 8 and b is in the range of 0 to 10. The heteroatom is selected from the group consisting of O, S, and N. At least one repeating unit comprises a cyclic species. The repeating unit, C^, further is substituted by one to six pendant groups having the formula, (CHR^ CHR.CHR^^Y. The pendant group is selected such that a majority of the pendant groups comprises at least two Q and further, in which m is 0 or 1, in which n is in the range of 0 to 25, in which Q is a Group la or Group Ila cation-solvating species selected from the group consisting of O, S and NR*, in which each R^ is the same or different and R λ is selected from the group consisting of H, alkyl, allylic and alkenyl radicals having 1 to 18 carbon atoms and Y, and in which each Y is the same or different and Y is a functional group selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species, wherein at least one Y is a polymerizable functionality. Unless otherwise stated, the number of each n is an average. The cation may be a monovalent or divalent cation selected from the Group la and Group Ila elements. The selection of a particular functional group for Y imparts specific desirable properties to an electrolyte comprising the above compounds. As used herein, when the compound contains polymerizable functional groups, the SUBSTITUTE SHEET compound is referred to as a "monomer" . When the compound contains no polymerizable functionalities, the compound is referred to as an "electrolyte additive". Electrolyte additives include plasticizers and electrolyte salts. The pendant group may be functionalized with a polymerizable functionality to provide a monomer capable of cross-linking or polymerizing to form a high molecular weight polymer of high ionic conductivity. At least one Y of the compound must be a polymerizable functionality to form a solid polymer electrolyte. A polymerizable functionality may be an epoxide, an isocyanate, an acrylate or an alkenyl group. The polymerizable functionality is not intended to include an active hydrogen for enhanced safety in alkali metal-based electrochemical devices. The pendant group may be functionalized with a plasticizing agent. If a monomer additionally contains a plasticizing agent, it is designated a "self- plasticizing" monomer. By "self-plasticizing", as that term is used herein, it is meant that the polymer contains pendant groups which impart to the polymer desirable properties, such as improved mechanical properties and reduced crystallinity at room temperature, through increased segmental motion. If a compound contains only plasticizing agents as Y groups, it functions as a plasticizer. A plasticizer of the present invention is a good ionic solvent, typically a liquid, that is non- volatile and non-reactive. A plasticizing agent may be a trialklysilyl, an alkyl, a phosphate ester, phosphinate ester or a saturated ester group. The pendant group may be functionalized with an ionic species. An ionic species provides cation of the Group la or Ila elements for use as an electrolytic species. A compound containing at least one and ranging up to only ionic species results in a macro-ion. Because of its large size, the anion is effectively anchored in place, so that primarily the cation is mobile. The ionic species may be an alkali metal or alkaline earth salt of an alkoxide or an alkyl or haloalkyl carboxylate or sulfonate. The present invention provides the capability of tailoring the individual compounds to thereby impart unique properties to the electrolyte. In particular, the compounds of the present invention may contain only one type of functional group or any combination of functional groups. For example, monomers having both polymerizable and plasticizing functionalities can be polymerized with compounds having both polymerizable and ionic functionalities, thereby providing a polymer having all three functionalities. The overall composition of the polymer can be easily adjusted by changing the relative proportions of the variously functionalized monomers. Mixtures of monomer and electrolyte additives can be used to further tailor the electrolyte composition. Upon polymerization, the monomers participate in the polymerization reaction to form a polymer, while electrolyte additives without polymerizable functionalities do not. The result is an intimately mixed composite material of polymer and electrolyte additive. The electrolyte additive can be a plasticizer to help improve the conductivity and mechanical properties of the electrolyte. The electrolyte additive can be a macro-ion to provide a soluble cation and a macroanion for the electrolyte. Compounds of the present invention can also be used as electrolyte additives, such as plasticizers and macro-ions, in conventional electrolyte systems, such as primary and rechargeable liquid electrolyte lithium batteries. They also can be used in the preparation of composite electrodes. The above-described electrolytes can be used with negative and positive electrodes in an electrochemical device, such as a battery, capacitor, fuel cell or display. Brief Description of the Drawing In the Drawing: Figure 1 is a cyclic voltammogram of an electrochemical cell using an electrolyte of the invention over a range of 0 to 5N. Detailed Description of the Invention The present invention has recognized that certain classes of materials, as described herein, exhibit excellent ionic conductivity and thermal and electrochemical stability when used in an electrolyte. SUBSTITUTE SHEET The compounds of the present invention have the following features in common: a compact backbone, extended pendant groups containing cation- solvating species and functionalizing groups which impart desirable properties to the electrolyte. The compounds of the present invention are highly versatile in that the nature and relative proportions of the functionalizing groups can be readily altered. These compounds are useful as monomers in preparing solid polymer electrolytes and as electrolyte additives, such as plasticizers and macro-ions. The compact backbone of the compounds used in the invention may have a repeating structure of the general formula, X,*, selected from the group consisting of linear saturated and unsaturated alkyl and alkenyl species containing i carbon atoms andy heteroatoms, where is in the range of 1 to 6, where j is in the range of 0 to 3. The heteroatom, X, is selected from the group consisting of O, S, and N. In particular, the repeating structure may be alkylene imine, diaminoalkyl, alkoxy groups, such as ethoxy or propoxy and the like, or their thio-derivatives. Alternately, the compact backbone may have a repeating structure of the general formula, CJζ. b , selected from the group consisting of saturated and unsaturated cyclic and heterocyclic species and linear alkyl and alkenyl species containing a carbon atoms and b heteroatoms, where a is in the range of 1 to 8 and b is in the range of 0 to 4. The heteroatom is selected from the group consisting of O, S, and N. At least one repeating structure comprises a cyclic or heterocyclic species. In particular, the repeating structure may be cyclic alkyl groups, such as cyclohexyl and cyclopentyl and the like, cyclic ethers and their thio-derivatives, such as furanyl, tetrahydrofuranyl, thiophenyl, pyranyl, tetrahydropyranyl, dioxanyl, trioxanyl and the like, and cyclic amino groups such as pyrolidinyl and piperidinyl and die like. The repeating structure may also include alkylene imine, diaminoalkyl, and alkoxy 1 groups, such as ethoxy or propoxy and the like, and their thio-derivatives. A particularly preferred compound has a repeating structure of the general formula, C^X., selected from the group consisting of cyclic and heterocyclic species consisting of y carbon atoms and z heteroatoms, X, where y is 4, 5 or 6 and z is 0, 1 or 2. The heteroatom is selected from the group consisting of O, S and N. The repeating structure, C ζ y , may be a group such as cyclic alkyl SUBSTITUTE SHEET groups, such as cyclohexyl and cyclopentyl and the like, cyclic ethers and their thio-derivatives, such as furanyl, tetrahydrofuranyl, thiophenyl, pyranyl, tetrahydropyranyl, dioxanyl, trioxanyl and the like, and cyclic amino groups such as pyrolidinyl and piperidinyl and the like. Certain classes of preferred compounds for use in the electrolyte of the present invention may be conveniently prepared from carbohydrates in their cyclic form. The carbohydrate possesses a plurality of pendant hydroxyl groups that can be readily converted into the extended pendant chains of the present invention. A functionalized alkoxylated carbohydrate for use in an electrolyte includes monosaccharide moieties selected from the group consisting of pentoses and hexoses and having one to five hydroxyl groups, wherein a total of between 4 and 150 and preferably between 4 and 60 alkoxy groups are attached through ether linkages to the hydroxyl group of each monosaccharide moiety and wherein each alkoxide-substituted hydroxyl group of the monosaccharide moiety is functionalized with a functional group, Y, selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species. Oligosaccharides comprising monosaccharide moieties described above are also contemplated. Suitable carbohydrates include monosaccharides and oligosaccharides which provide a variety of templates for derivatization. Five- or six-membered cyclic monosaccharaides, such as glucose, fructose, sorbose, mannose, ribose, xylose and the like; disaccharides, such as sucrose, maltose, lactose and the like; and trisaccharides, such as raffinose, are particularly preferred templates. The pendant groups of the compounds of the invention contain elements, such as oxygen, sulfur or nitrogen, which are capable of solvating cations of the Group la and Ila elements. The pendant group can be an alkoxy group, such as ethoxy, propoxy and the like or its thio derivatives; or an alkylene imine. The pendant group provides a branching side chain which can solvate the electrolyte cation or help form a network polymer upon polymerization. The chain length of the extended pendant group also contributes to the formation of a macroanion by helping to anchor the macroanion in the electrolyte. SUBSTITUTE SHEET Among the polymerizable functionalities, there are included alkenyl groups, isocyanates, epoxides and unsaturated carboxyl groups. Such polymerizable functionalities, include but are in no way limited to, alkenyl groups such as vinyl and allyl; unsaturated carboxyl compounds such as aery late, methacrylate, cinnamate, fiimarate, maleate and the like; isocyanates such as methylisocyanate and the like; and halosilyl groups, such as dimethyl chlorosilyl and die like. In particular, the polymerizable functionality can include -CH 2 CH ° CH 2 , -CH 2 NCO, -SiCl(CH 3 ) 2 , -C(=O)CH=CH 2 , -C(=O)C(CH 3 )=CH 2) -CH 2 CH=CH 2 and -CH=CH 2 . Unless otherwise stated, cross-linking functionalities can be used as polymerizable functionalities, in that, they both perform the function of increasing the molecular weight of the network polymer. Polymerization can be carried out using standard techniques, including photoinitiation and thermal and chemical initiation. Among the plasticizing agents, there are included, but in no way are limited to, trialklysilyl, alkyl, nitrilic, phosphate ester, phosphinate ester and saturated ester groups. In particular, these include, trimethyl- or triethylsilyl; alkyl groups such as methyl, ethyl and die like; phosphate ester groups such as diethyl phosphatyl and diphenyl phosphatyl; diphenyl phosphinatyl; alkylnitrile and saturated alkyl esters such as acetate, isobutyrate and die like. In particular, the plasticizing agent includes -Si(CH 3 ) 3 , -CH 3 and -C(=O)CH 3 . In general, plasticizing agents can include non-reactive, electrochemically stable functional groups that do not contribute to the crystallinity of the compound. In an important aspect of the invention, an electrolyte is prepared using the compounds of die invention and a soluble cation. The cation is introduced as an ionic functional group on the pendant group of the compound. In tiiis instance, the compound functions as a macro-ion. Among the ionic functional groups suitable for use in the macro-ion of the present invention, there are included, but are in no way limited to, alkali metal and alkaline earth salts of alkoxides, alkyl carboxylates and sulfonates and haloalkyl carboxylates and sulfonates. It may also be desirable to introduce some or all of the soluble cation as a soluble electrolyte salt of the prior art. Among the soluble electrolyte salts suitable for use in the electrolyte of the present invention, there are included, but SUBSTITUTE SHET in no way limited to, inorganic ion salts containing a cation selected from the Group of la and Ila elements associated with anions such as ClO 4 ", SCN", BF 4 " , AsF 6 " , CF 3 SO 3 " (triflate), Br\ I " , PF « f, (CF 3 SO 2 ) 2 N- (bis(trifluoromethanesulfonyl)imide or TFSI), (CF 3 SO 2 ) 3 C " (tris(trifluoromethanesulfonyl)methide or TFSM), CF 3 CO 2 " and the like. In particular, lithium ion is the preferred cation. By incorporating plasticizing agent functional groups onto pendant chains that also include polymerizable functional groups, followed by polymerization, the polymer becomes self-plasticizing. This is particularly desirable because the polymer, while exhibiting the properties of a solid polymer electrolyte film retains an amorphous, non-crystalline morphology with a high degree of segmental mobility of the pendant chains at room temperature. As a consequence, the need for a liquid plasticizer of the prior art can be eliminated. Plasticizers and soluble alkaline metal macro-ions of die present invention can be incorporated into conventional electrolyte systems. Such electrolytes include, but are in no way limited to, e ylene carbonate, propylene carbonate, dimethoxy ethane and sulfolane. When the plasticizers and soluble macro-ions of the present invention are incorporated into conventional electrolyte systems, the resultant electrolyte exhibits improved electrochemical properties and reduced anion mobility, respectively. A composite electrode can be prepared containing an electrochemically active compound, carbon as an electronic conductor and monomers of the present invention. Upon polymerization, a solid composite material is obtained containing electrode active materials and an ionically conductive solid polymer of the present invention. Preferred Embodiments of the Invention Odier characteristics and advantages of die invention are illustrated, but in no ways limited to, die following examples. The starting materials for the following examples is an ethoxylated methyl glucoside. CFTA-adopted names for such compounds are methyl glucedι-10 ["MG-10"] and methyl gluceth-20 ["MG-20"], respectively. Propoxylated SUBSTITUTE SHEET derivatives are designated PPG methyl gluceth-10 ["PPG-10"] and PPG methyl gluceth-20 ["PPG-20"], respectively. The material is commercially available as Glucam ® (Amerchol Corp., Talmadge Rd. , Edison, NJ). Glucam ® is offered as derivatives of both ethylene oxide (Glucam ® -E) and propylene oxide (Glucam ® -P) and having an average of 10 or 20 edioxy or propoxy groups per molecule. Other alkoxylated glucosides widi various molecular weights could also be used as a starting material. The desired alkoxylated starting materials can be prepared by reacting 1 mole of mediyl glucoside widi the desired moles of an alkylene oxide, for example, ethylene oxide, to form an emoxylated methyl glucoside, which has 4 primary hydroxyl groups available for reaction. Other alkoxylated saccharides with various molecular weights could also be used as a starting material. The desired alkoxylated starting materials can be prepared by reacting 1 mole of saccharide widi the desired moles of an alkylene oxide, for example, ethylene oxide, to form an ethoxy lated saccharide, the number of primary hydroxyl groups available for reaction is dependent upon the initial degree of hydroxyl group substitution on die backbone. Other backbones with different structures could also be used as a starting material. The desired alkoxylated starting materials can be prepared by reacting 1 mole of a selected backbone containing pendant hydroxyl groups with the desired moles of an alkylene oxide to form an alkoxylated starting material, the number of primary hydroxyl groups available for reaction dependent upon the initial degree of hydroxyl groups substitution by the backbone. Examples 1-4 present a metiiod of preparing plasticizer-functionalized compounds. Example 1. An acetylethoxylated metiiyl glucoside according to the present invention is prepared as follows. A cyclohexane solution of MG-20 (50.0 g, 0.048 mole) and sodium acetate (6.49 g, 0.0791 mole, Fisher Scientific) is heated to the cyclohexane refluxing temperature (80°C). Traces of water are removed from the system as the cyclohexane azeotrope and collected in die receiver. When refluxing removes no additional water, acetic anhydride (19.94 g, 0.196 mole, Fisher Scientific) is slowly added to me stirred and refluxing mixture in the flask over a 1 hr. period, and die flask then cooled to room temperature. About 150 ml SUBSTITUTE SHEET distilled water is added to the flask's contents and dien stirred. Concentrated NaOH solution is added to raise the pH to above 7.0. The cyclohexane organic phase is separated from the aqueous phase. The aqueous phase is ien extracted twice wid two 150 ml portions of chloroform. The product is isolated by concentrating the dried chloroform extract in a rotary flash evaporator at about 55°C until no additional solvent is removed. Yield of acetylethoxylated methyl glucoside (MG-20-ACETYL 4 ) is 46.45 g (80% dieoretical). The nomenclature indicates functionalization with four acetyl groups per glucoside backbone. The product is a clear, pale yellow, viscous fluid widi no odor. Confirmation of the product's identity is made by infrared spectroscopy. Example 2. A trimethylsilylethoxylated methyl glucoside according to die present invention is prepared as follows. MG-20 (1003 g, 0.981 mole), triethylamine (479 g, 4.73 mole, Aldrich Chemical Co.), and tetrahydrofuran (4000 ml, THF) are stirred briefly in a round bottom flask to form a clear, colorless solution, and a slightly positive pressure of argon gas maintained in die reaction flask. Trimethylchlorosilane (513.6 g, 4.73 mole, Aldrich Chemical Co.) is diluted widi THF (780 ml). One-third (500 ml) of me trimethylchlorosilane/THF solution is slowly added to die reaction flask's contents while stirring the reaction mixture. A large volume of white precipitate (triethylamine hydrochloride) forms in the reaction mixture almost immediately. The remaining two-thirds of die trimethylchlorosilane/THF solution is then slowly added to die reaction flask accompanied by die formation of additional precipitate. The complete addition is made over a period of 3 hr. 15 min. During the addition die temperature of die flask's contents rises from room temperature to about 34°C. Stirring is continued for an additional 2 hr, while the flask cools to room temperature. The triethylamine hydrochloride precipitate is removed by filtration. The crude product solution is concentrated in a rotary flash evaporator at about 35°C and is then diluted widi about 2000 ml hexanes. After stirring, die solution is filtered to remove all traces of triethylamine hydrochloride. The product is isolated by concentrating the hexane solution in a rotary flash evaporator at about 45°C. Yield of trimethylsilylethoxylated methyl glucoside (MG-20-TMS 4 ) is 1246 SUBSTITUTE SHEET g (96.6% theoretical). The nomenclature indicates four trimethylsilyl groups per glucoside backbone. The product is a clear, pale yellow, oily fluid widi no odor. Confirmation of the product's identity is made by infrared spectroscopy. Example 3. A tetrakis(diedιylphosphatyl) ethoxylated me yl glucoside according to the present invention is prepared as follows. MG-20 (50.0g, 0.048 mole) in dry tetrahydrofuran (250 ml) and triethylamine (19.8g, 0.196 mole, Aldrich Chemical Co.) is charged to a 1000 ml 3-neck round bottom flask equipped widi an argon gas purge, a refluxing condenser, a thermometer, an addition funnel, heating mantle, and magnetic stirrer, and die resulting solution is stirred. Diethyl chlorophosphate (33.8 g, 0.196 mole, Aldrich Chemical Co.) in THF (50 ml) is slowly added to the stirred flask over a 1 h. period. A large volume of white precipitate (triethylamine hydrochloride) forms in the reaction mixture almost immediately. During the addition, die temperamre of the flask's contents rises from room temperamre to about 34°C. The flask's contents are heated to the reflux temperature of THF for 4 hs., and ien cooled to room temperature. The flask's contents stored under argon at 5°C overnight. The triethylamine hydrochloride precipitate is removed from the TΗF/product solution by suction filtration. The crude product solution is concentrated in a rotary flash evaporator at about 35 °C until no additional THF is removed and is men diluted widi about 500 ml hexanes/efher. After stirring for about 2 h. die solution is filtered to remove all traces of triethylamine hydrochloride, dried over anhydrous magnesium sulfate and filtered dirough a basic alumina column. The product is isolated by concentrating the solution in a rotary flash evaporator at about 45 °C until no additional solvent is removed. The product is a transparent orange oil. Yield of tetrakis(diedιylphosphatyl) exdioxylated methyl glucoside [MG-20-(PO 3 Et 2 ) 4 ] is 83g (58% dieoretical). Example 4. A tetrakis (diphenylphosphinatyl) ethoxylated memyl glucoside according to die present invention is prepared as follows. Diphenylphosphinic chloride (37.1 g., 0.157 mole, Aldrich Chemical Co.) in dry tetrahydrofuran (100 ml) and triethylamine (18.2g, 0.179 mole, Aldrich SUBSTITUTE SHEET Chemical Co.) is charged to a 500 ml 3-neck round bottom flask equipped with an argon gas purge, a refluxing condenser, an addition funnel, heating mantle, and magnetic stirrer, and die resulting solution stirred. MG-10 (19.3 g., 0.0317 mole) in THF (100 ml), is slowly added to die stirred flask over a 30 min. period. A large volume of white precipitate (triethylamine hydrochloride) forms in the reaction mixture almost immediately. During the addition, die temperature of the flask's contents rises from room temperature to about 34°C, and the mixture increases in viscosity. More THF (100 ml) is added to die flask to reduce die mixture's viscosity. The flask's contents are heated to die reflux temperature of THF for 5 hr. then cooled to room temperamre. The flask's contents stored under argon at 5°C overnight. The triethylamine hydrochloride precipitate is removed from the THF/product solution by suction filtration. The crude product solution is concentrated in a rotary flash evaporator at about 35 °C until no additional THF is removed and dien is diluted widi about 300 ml toluene and 40 ml memylene chloride. The solution is dried over anhydrous magnesium sulfate and filtered. The product is isolated by concentrating die solution in a rotary flash evaporator at about 45°C until no additional solvent is removed. Finally, die product is heated in a vacuum chamber at 105°C for 8 h. to remove residual toluene. The product is a very high viscosity transparent amber oil. Yield of tetrakis (diphenylphoshinatyl) ethoxylated memyl glucoside [MG-10(POPh 2 ) 4 ] is 44.7 g (100% dieoretical). Example 5. This example presents a method of preparing an ionic sulfonate derivative. A sodium sulfopropylethoxylated methyl glucoside salt according to the present invention is prepared as follows. A solution of MG-20 (49.4 g, 0.048 mole), 1,3-propane sultone (27.5 g, 0.225 mole, Aldrich Chemical Co.) and N-methyl pyrolidone (NMP) (50 ml) is prepared. Sodium hydride (5.40 g, 0.225 mole) in 100 ml NMP is charged to a round bottom flask and die MG-20/l,3-propane sultone/NMP solution is introduced tiirough dropwise addition. During the addition, vigorous effervescence of hydrogen gas occurs and die temperamre of the flask's contents rises from room temperamre to about 38°C. SUBSTITUTE SHEET After addition is complete, the reactants are gently warmed widi continuous stirring to about 55 to 70°C for several hours and dien allowed to cool overnight to room temperamre. Gentle heating during die day followed by cooling overnight is repeated for die next 4 days. The reaction mixture is then slowly poured into a rapidly stirred solution of memyl t-butyl ether (MTBE) (300 ml) and medianol (15 ml). The product sulfonate precipitates as a light tan powder. The precipitated product is extracted in a Soxhlet thimble with hot (55°C) MTBE for about 45 min. The product is then held at 60°C and 30 inches Hg vacuum until constant weight is obtained (24 hr). Yield of sodium sulfopropylethoxylated methyl glucoside (MG-20-Na) is 31.0 g (40.2% theoretical). There are four sodium sulfonate groups per glucoside backbone. The product is a tan powder with no odor. It is extremely hygroscopic and will spontaneously form an aqueous solution on exposure to atmosphere. It is insoluble in most organic solvents, slightly soluble in methanol, soluble in NMP, and readily soluble in water. Confirmation of die product's identity is made by infrared spectroscopy and d in layer chromatography. The sodium salt is converted into a lid ium salt using conventional ion exchange mediods. Example 6. This example presents a memod of preparing and polymerizing a polymerizable derivative. An acryloylethoxylated methyl glucoside according to die present invention is prepared as follows. MG-20 (50.0 g, 0.048 mole) is diluted in dry methylene chloride (150 ml). This solution is stirred widi anhydrous sodium carbonate (30 g, Fisher Scientific). Acryloyl chloride (16.1 g, 0.205 mole, Aldrich Chemical Co.) in methylene chloride (25 ml) is added dropwise to die solution over a 1 hr period and widi a slight exodiermic warming of the flask's contents. Stirring is continued overnight. The flask's contents are passed dirough a column of basic activated alumina (Aldrich Chemical Co.) to filter solids and remove acidic material from the product solution. The product is concentrated in a rotary flash evaporator at about 55°C. Yield of acryloylethoxylated me yl glucoside (MG-20- ACR 4 ) is 51 g (79% theoretical). There are four acryloyl groups per glucoside SUBSTITUTE SHEET backbone. The product is a clear, yellow, oily fluid widi a trace acrylic odor. Confirmation of die product's identity is made by infrared spectroscopy. This product is converted to a hard, transparent, solid, polymer film by addition of a photoinitiator (0.1 wt % Darocure ® 1173, EM Industries, Inc.) to die acryloylethoxylated memyl glucoside, casting a 0.005 in film of the product/photoinitiator solution on glass widi an adjustable film casting knife gapped at 0.010 in, and exposing die wet film to high intensity UN light (Fusion Systems H bulb) for about 0.2 sec. Example 7. This example presents a method of preparing and polymerizing doubly-functionalized derivative having polymerizable and plasticizing groups. An acryloylethoxylated trimethylsilyledioxylated methyl glucoside widi an average of about two polymerizable groups per glucoside according to die present invention is prepared as follows. A solution is prepared of MG-20 (250.0 g, 0.245 mole), triethylamine (204.5 ml, Aldrich Chemical Co.), hydroquinone (0.050 g, Anachemia) and dry THF (1500 ml). Acryloyl chloride (38.4 g, 0.489 mole, Aldrich Chemical Co.) in THF (150 ml) is added dropwise to die stirred solution over 1.5 hr. A large volume of white precipitate (triethylamine hydrochloride) forms in me reaction mixture almost immediately. Trimediylchlorosilane (106.2 g, 0.98 mole, Aldrich Chemical Co.) in THF (250 ml) is added dropwise over 3.3 h to the stirring solution accompanied by die formation of additional precipitate. Stirring is continued for an additional 1.5 hr, while the flask cools to room temperamre. The triethylamine hydrochloride precipitate is removed by filtration. The crude product solution is concentrated in a rotary flash evaporator at about 35°C. Some residual triediylamine hydrochloride precipitate forms when the product is concentrated. Crude product is then diluted widi hexanes (750 ml)/emer (500 ml) and stored overnight at 10°C. The product solution is filtered to remove all traces of triethylamine hydrochloride. The product is isolated by concentrating the hexane/edier solution in a rotary flash evaporator at about 30°C. Yield of acryloylethoxylated trimetiiylsilylethoxylated methyl glucoside (MG-20-ACR 2 TMS 2 ) is 295 g (96% theoretical). SUBSTITUTE SHEET The product is a clear, yellow, oily fluid widi a trace acrylic odor. Confirmation of the product's identity is made by infrared spectroscopy and thin layer chromatograph. This product is converted to a transparent, solid, polymer film by addition of a photoinitiator (0.1 wt % Darocure ® 1173, EM Industries, Inc.) to the acryloyletiioxylated trimethylsilylethoxylated methyl glucoside, casting a 0.005 in film of the product/photoinitiator solution on glass widi an adjustable film casting knife gapped at 0.010 in, and exposing die wet film to high intensity UN light (Fusion Systems H bulb) for about 0.2 sec. Example 8. A acryloylemoxylated tris (diphenylphosphatyl) ethoxylated memyl glucoside wid an average of about one polymerizable group per glucoside according to the present invention is prepared and polymerized as follows. MG-10 (250.0g, 0.245 mole), triethylamine (204.5 ml, Aldrich Chemical Co.), hydroquinone (0.050 g, Anachemia) and dry tetrahydrofuran (1500 ml)(THF) are charged to a round bottom flask equipped widi a refluxing condenser capped widi a calcium sulfate drying tube, a mermometer, an addition funnel, and a paddle type stirrer. Diphenyl chlorophosphate (197.5 g, 0.75 mole, Aldrich Chemical Co.) in THF (250 ml) is added dropwise to die stirred solution over a 1.5 h. period widi a slight warming of me flask's contents to 30 °C. A large volume of white precipitate (triethylamine hydrochloride) forms in the reaction mixture almost immediately. The contents of die flask are heated to the reflux temperamre of THF for 3 h. and men cooled to room temperamre. Acryloyl chloride (23.0 g, 0.30 mole, Aldrich Chemical Co.) in THF (150 ml), is added dropwise over a period of 2 h to die stirred solution, accompanied by die formation of additional precipitate. During die addition die temperamre of the stirred solution remains between 30 and 25 °C. Stirring is continued for an additional 6 hr. at room temperamre. The reactor is then stored overnight under dry air atmosphere. The triemylamine hydrochloride precipitate is then removed from the THF/product solution by filtration. The crude product solution is concentrated in a rotary flash evaporator at about 35 °C until no additional THF is removed. Crude product is dien diluted widi memylene chloride, washed widi several small volumes of 0.01N HC1, men dried over anhydrous magnesium sulfate and filtered through a basic alumina column. The product is isolated by concentrating the methylene chloride solution in a rotary flash evaporator at about 30°C until no additional solvent is removed. Yield of acryloyledioxylated tris(diphenylphosphatyl) ethoxylated memyl glucoside [MG-10-ACR(PO 3 Ph-,) 3 ] is 295 g. (69% theoretical). The product is a clear, yellow, oily fluid widi a trace acrylic odor. Confirmation of die product's identity is made by infrared spectroscopy and d in layer chromatography. This product is converted to a transparent, solid, polymer film by addition of a photoinitiator (0.1 wt % Darocure ® 1173, EM Industries, Inc.) to the acryloylethoxylated tris (diphenylphosphatyl) ethoxylated memyl glucoside, casting a 0.005" (0.0127 cm) film of the product/photoinitiator solution on glass widi an adjustable film casting knife gapped at 0.010" (0.0254 cm), and exposing die wet film to high intensity UN light (Fusion Systems H bulb) for about 0.2 sec. Example 9. Ionic conductivity of various alkoxylated compound-based electrolytes is determined. Electrolyte solutions containing an edioxylated glucoside or other alkoxylated compound and a lidiium salt were prepared by dissolving 10% wt of lidiium perchlorate in the compound of interest. The ionic conductivity of d e electrolyte solutions were measured as at room temperamre for various electrolyte compositions and are reported in Table 1. Note diat the ionic conductivity of all diese compounds even at room temperamre is sufficient for most applications. Because of die hydroxyl end groups, non-functionalized alkoxylated compound- based electrolytes are not suitable for use widi alkali metal electrodes, such as lidiium. However, the measured ionic conductivity suggests diat derivatives of these compounds could all be functionalized for use in the present invention. SUBSTITUTE SHEET Table 1. Ionic Conductivity of unfunctionalized alkoxylated compound-based electrolytes. Example 10. Determination of the ionic conductivity of functionalized memyl glucoside-based electrolytes. An electrolyte solution containing trimethylsilylethoxylated methyl glucoside MG-20-TMS 4 , as described in Example 2, and 10% wt of lidiium tris(trifluoromethanesulfonyl)methide (LiTFSM) was prepared. An electrolyte solution containing acetylethoxylated methyl glucoside MG-20-ACETYL 4 , as described in Example 1, and 10% wt of lithium bis(trifluorometiιanesulfonyl)imide (LiTFSI) was prepared. Ionic conductivity were measured as a function of temperamre and are reported in Table 2. The ionic conductivity of diese functionalized edioxylated methyl glucoside-based electrolytes is suitable for most applications even at room temperamre. A threshold ionic conductivity of 10 -5 S/cm is considered necessary for electrochemical devices. Advantageously, die functionalized derivatives, MG-20- TMS 4 and MG-20-ACETYL 4 , can be used in lidiium electrode environments. SUBSTITUTE SHEET Table 2. Ionic conductivity of functionalized ethoxylated methyl glucoside- based electrolytes. Example 11. Electrochemical stability of a MG-20-TMS 4 -based electrolyte is determined. The MG-20-TMS 4 -based electrolyte solution described in Example 10 was used in die following electrochemical cell configuration: Li/MG-20-TMS 4 , LiTFSM (10% wt)/Al. The cell was tested by cyclic voltammetry between 0 and 5 Volt v. lidiium at 10 mN/sec at 100°C to establish the extent of die electrochemical stability window of die electrolyte. As illustrated in Fig. 1, the electrochemical stability window is in excess of 4.5 N, even at elevated temperamre. Example 12. Ionic conductivity of solid polymer electrolyte is determined. A solid polymer electrolyte precursor solution was prepared using 75 % wt of MG-20-TMS 4 (as in example 2) functioning as a plasticizer, 10% wt of MG-20- TMS 2 ACR 2 (as in example 7) functioning as a polymerizable monomer, 5 % wt of polyethylene glycol di-acrylate (PEGDA), and 10% wt of TFSI. A small amount of photoinitiator Darocure ® 1173 was added. The solution was coated on an aluminum foil and exposed to a source of UN radiation. A solid polymer membrane is obtained. The ionic conductivity of diis membrane is 5.5 x 10 '5 S/cm at 25"C and 4.3 x 10 "4 S/cm at 100°C. Example 13. Ionic conductivity of a gel-polymer electrolyte is determined. A gel-polymer electrolyte precursor solution was prepared using 55% wt of MG-20-TMS 4 (as in example 2) functioning as a plasticizer, 10% wt of MG-20- TMS 2 ACR 2 (as in example 7) functioning as a polymerizable monomer, 5%wt of PEGDA, 20% wt of ethylene carbonate (EC), and 10% wt of LiTFSI. A small SUBSTITUTE SHEE amount of photoinitiator Darocure ® 1173 was added. The solution was coated on an aluminum foil and exposed to a source of UV radiation. A solid polymer membrane is obtained. The ionic conductivity of diis membrane is 3.3 x 10 -4 S/cm at 25°C and 2.5 x 10 "3 S/cm at 100°C Example 14. Composite electrode is prepared. A composite electrode, to be used in a lidiium rechargeable battery, was prepared using 18g of LiCoO 2 , 4g of carbon black, and 18g of a solid polymer electrolyte precursor comprising of 4g MG-20-TMS 4 (as in example 2), 9g MG- 20-TMS 2 ACR 2 (as in example 5), 4g of TMPEOTA (trimethyl propane ethoxylate triacrylate), lg of PEO, and a small amount of t-butyl peroctoate (Lucidol). The composite cathode formulation was coated on aluminum foil and cured thermally at 80°C for approximately 2h. Thermal processing is possible because no volatile plasticizer is present. The solid polymer electrolyte composite cathode formed a self supporting membrane having good electrical conductivity and electrochemical performance. Example 15. LiAl anode cycling of a electrochemical cell is performed. An electrolyte as described in example 10 was used to make the following electrochemical cell: Li/MG-20-TMS 4 , LiTFSM (10% wt)/Al-LiAl. The cell was maintained at 95°C and cycled at 50 micro-amperes/cm 2 . The Li cycling efficiency of the LiAl electrode was greater tiian 99% after 50 cycles. Example 16. MG-20-salt ionic conductivity is determined. Electrolyte solutions are prepared by dissolving LiTFSI or MG-20-Na in N-methyl pyrrolidone in various concentrations. Ionic conductivity are reported in die following table. The macro-ion MG-20-Na exhibits comparable conductivity to diat of TFSI, while having die additional advantage of reduced anionic mobility in solution because of die large size of the anion. SUBSTITUTE SHEET Table 3. Comparative ionic conductivities of ionic salt solutions. What is claimed is: SUBSTITUTE SHE

Claims: 1. A compound for use in an electrolyte, comprising: a cyclic or polycyclic backbone of 1 to 10 repeating units, C ζ. z , said repeating unit consisting of y carbon atoms and z heteroatoms, X, where y is 4, 5 or 6 and z is 0, 1 or 2, wherein said heteroatom is selected from the group consisting of O, S and N, said repeating unit, C j X., further substituted by four to six pendant groups having the formula, (CHR 1 ) m O(CHR 1 CHR 1 O)„Y, said pendant group selected such diat the majority of said pendant groups comprises at least two O, and further, in which m is 0 or 1, in which n is in the range of 0 to 25, in which each Rj is the same or different, said R. selected from die group consisting of H, alkyl, allylic and alkenyl radicals having 1 to 18 carbon atoms and Y, and in which each Y is die same or different, said Y selected from die group consisting of polymerizable functionalities, plasticizing agents and ionic species. 2. The compound of claim 1 wherein said polymerizable functionality is selected from the group consisting of epoxides, alkenyl, halosilyl, isocyanates, acrylates, methacrylates, cinnamates, fumarates and maleates. 3. The compound of claim 1, wherein said plasticizing agent is selected from the group consisting of trialkylsilyls, alkyls, alk lnitriles, phosphate esters, phosphinate esters and saturated esters. 4. The compound of claim 1, wherein said heterocyclic backbone is selected from the group consisting of cyclic ediers, cyclic thioethers, dioxanes, trioxanes, ditiiianes and trithianes. 5. The compound of claim 1, wherein said ionic species is selected from die group consisting of alkali metal and alkaline earth alkoxides, alkyl carboxylates and sulfonates and haloalkyl carboxylates and sulfonates. SUBSTITUTE SHEET 6. The compound of claim 1, wherein at least one Y of a pendant group comprises a polymerizable functionality, such mat upon polymerization a solid polymer is formed. 7. The compound of claim 1, wherein said pendant groups are selected such that at least one Y of a first pendant group comprises a polymerizable functionality, at least one Y of a second pendant group comprises a plasticizing agent and at least one Y of a diird pendant group comprises an ionizing species. 8. The compound of claim 1, wherein at least one Y of a pendant group comprises a plasticizing agent, whereby said compound exhibits plasticizing properties. 9. The compound of claim 1, wherein at least one Y of a pendant group comprises an ionic species, whereby said compound functions as a macro- ion. 10. A solid polymer electrolyte, comprising: a cation selected from die group consisting of alkali metal and alkaline earth elements; and a polymer formed by polymerization of the compound of claim 6. 11. A solid polymer electrolyte, comprising: a cation selected from the group consisting of alkali metal and alkaline earth elements; and a polymer formed by polymerization of the compound of claim 7. 12. The electrolyte of claim 10, further comprising: a plasticizer, said plasticizer comprising said compound of claim 1 , wherein each Y of said pendant groups is a plasticizing agent . 13. The electrolyte of claim 11, further comprising: SUBSTITUTE SHEET a plasticizer, said plasticizer comprising said compound of claim 1, wherein each Y of said pendant groups is a plasticizing agent . 14. An electrolyte, comprising: a cation selected from the group consisting of alkali metal and alkaline earth elements; the compound of claim 1 ; and an aprotic solvent or mixtures thereof, said solvent capable of solubilizing said cation. 15. An electrolyte, comprising: a macro-ion, said macro-anion comprising the compound of claim 11 ; and an aprotic solvent or mixtures thereof, said solvent capable of solubilizing said macro-ion. 16. A functionalized alkoxylated carbohydrate for use in an electrolyte, comprising: a carbohydrate selected from the group consisting of monosaccharides and oligosaccharides of pentoses and hexoses and having one to five hydroxyl groups per monosaccharide unit; wherein a total of between 4 and 150 alkoxy groups per monosaccharide unit are attached tiirough ether linkages to said hydroxyl groups; and wherein each the terminal alkoxide-substituted hydroxyl group of said carbohydrate is functionalized widi a functional group, Y, selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species. 17. The carbohydrate of claim 16 wherein said polymerizable functionality is selected from die group consisting of epoxides, alkenyls, isocyanates, halosilyls, acrylates, methacrylates, cinnamates, fumarates and maleates. SUBSTITUTE SHEET 18. The carbohydrate of claim 16, wherein said plasticizing agent is selected from the group consisting of trialkylsilyls, alkyls, alkylnitriles, phosphate esters, phosphinate esters and saturated esters. 19. The carbohydrate of claim 16, wherein said ionic species is selected from the group consisting of alkaline metal alkoxides, alkyl carboxylates and sulfonates and haloalkyl carboxylates and sulfonates. 20. The carbohydrate of claim 16, wherein at least one Y of an alkoxide-substimted hydroxyl group comprises a polymerizable functionality, such that upon polymerization a solid polymer is formed. 21. The carbohydrate of claim 16, wherein said alkoxide-substimted hydroxyl groups are functionalized such diat at least one Y of a first alkoxide- substimted hydroxyl group comprises a polymerizable functionality, at least one Y of a second alkoxide-substimted hydroxyl group comprises a plasticizing agent and at least one Y of a third alkoxide-substimted hydroxyl group comprises an ionizing species. 22. The carbohydrate of claim 16, wherein at least one Y of a alkoxy- substituted hydroxyl group comprises a plasticizing agent, whereby said carbohydrate exhibits plasticizing properties. 23. The carbohydrate of claim 16, wherein at least one Y of a alkoxy- substimted hydroxyl group comprises an ionic species, whereby said carbohydrate functions as a macro-ion. 24. A solid polymer electrolyte, comprising: a cation selected from the group consisting of alkali metal and alkaline earth elements; and a polymer constituted from the carbohydrate of claim 20. SUBSTITUTE SHEET 25. A solid polymer electrolyte, comprising: a cation selected from the group consisting of alkali metal and alkaline earth elements; and a polymer constituted from the carbohydrate of claim 21. 26. The electrolyte of claim 24, further comprising: a plasticizer, said plasticizer comprising the carbohydrate of claim 16, wherein each Y of said alkoxy-substimted hydroxyl groups is a plasticizing agent. 27. The electrolyte of claim 25, further comprising: a plasticizer, said plasticizer comprising the carbohydrate of claim 16, wherein each Y of said alkoxy-substimted hydroxyl groups is a plasticizing agent. 28. An electrolyte, comprising: a cation selected from me group consisting of alkali metal and alkaline earth elements; die compound of claim 16; and an aprotic solvent or mixtures thereof , said solvent capable of solubilizing said cation. 29. An electrolyte, comprising: a macro-ion, said macro-anion comprising the compound of claim 23; and an aprotic solvent or mixtures ereof, said solvent capable of solubilizing said macro-ion. 30 . A solid polymer electrolyte, comprising: a cation selected from me group consisting of alkali metal and alkaline earth elements; a polymer constituted from a compound comprising a linear backbone having 1 to 20 repeating units, CJL j , wherein said repeating unit is selected from e group consisting of saturated and unsaturated alkyl and alkenyl species containing i carbon atoms andy heteroatoms, X, where is in die range of 1 to 6 SUB and / is in die range of 0 to 3, and wherein said heteroatom is selected from die group consisting of O, S, and N; said repeating unit, C-X y , further substituted by one to six pendant groups having the formula, (CHR 1 ) m Q(CHRιCHR 1 Q)„Y, said pendant group selected such iat a majority of said pendant groups comprises at least two Q; in which m is 0 or 1 , in which n is in die range of 0 to 25, in which Q is an alkaline metal-solvating species selected from the group consisting of O, S and NRj, in which each R. is the same or different, said R. selected from the group consisting of H, alkyl, allylic and alkenyl radicals having 1 to 16 carbon atoms and Y, and in which each Y is the same or different, said Y being a functional group selected from the group consisting of polymerizable functionalities, plasticizing agents and ionic species, such at at least one Y of a first pendant group is a polymerizable functionality and at least one Y of a second pendant group is a functional group other than a polymerizable functionality. 31. A solid polymer electrolyte, comprising: a cation, selected from the group consisting of alkali metal and alkaline earth elements; a polymer constituted from a compound comprising a backbone, having 1 to 10 repeating units, C^, wherein said repeating unit is selected from me group consisting of samrated and unsamrated cyclic and heterocyclic species and linear samrated and unsamrated alkyl and alkenyl species containing a carbon atoms and b heteroatoms, X, where a is in die range of 1 to 8 and b is in die range of 0 to 4, wherein said heteroatom is selected from the group consisting of O, S, and N, and wherein at least one repeating unit comprises a cyclic species; said repeating unit, C^, further substimted by one to six pendant groups having the formula, (CHRι) m Q(CHR 1 CHR 1 Q)„Y, said pendant group selected such diat a majority of said pendant groups comprises at least two Q; in which m is 0 or 1 , SUBSTITUTE SHEET in which n is in the range of 0 to 25, in which Q is an alkaline metal-solvating species selected from die group consisting of O, S and NR l5 in which each R, is the same or different, said R* selected from the group consisting of H, alkyl, allyl and alkenyl radicals having 1 to 18 carbon atoms and Y, and in which each Y is the same or different, said Y being a functional group selected from die group consisting of polymerizable functionalities, plasticizing agents and ionic species, such mat at least one Y of a pendant group is a polymerizable functionality. 32. The electrolyte of claim 30 or 31 wherein said polymerizable functionality is selected from the group consisting of epoxides, alkenyls, halosilyls, isocyanates, acrylates, methacrylates, cinnamates, fumarates and maleates. 33. The electrolyte of claim 30 or 31, wherein said plasticizing agent is selected from the group consisting of trialkylsilyls, alkyls, alkylnitriles, phosphate esters, phosphinate esters and samrated esters. 34. The electrolyte of claim 30 or 31, wherein said ionic species is selected from the group consisting of alkaline metal alkoxides, alkyl carboxylates and sulfonates and haloalkyl carboxylates and sulfonates. 35. The electrolyte of claim 30 or 31, wherein said compound comprises a plurality of pendant groups, wherein at least one Y of a first pendant group comprises a polymerizable functionality, at least one Y of a second pendant group comprises a plasticizing agent and at least one Y of a tiiird pendant group comprises an ionic species. 36. The electrolyte of claim 10, 11, 14, 24, 25, 28, 30 or 31, wherein said cation is obtained from an alkali metal salt selected from the group consisting SUBSTITUTE SHEET of LiCF 3 SO 3 , LiClO 4 , LiClO 4j LiSCN, LiBF 4 , LiAsF 6 , CF 3 SO 2 Li, LiPF 6 , LiN(CF 3 SO 2 ) 2 , Li C(CF 3 SO 2 ) 3 , CF 3 CO 2 Li and mix res thereof. 37. The electrolyte of claim 10, 11, 14, 24, 25, 28, 30 or 31, wherein said solvated alkaline metal salt comprises said pendant group, wherein Y is selected from me group consisting of ionic species. 38. The electrolyte of claim 30 or 31, further comprising: a plasticizer, said plasticizer comprised of said compound, wherein each Y of said pendant group is a plasticizing agent. 39. An electrochemical device, comprising: a negative electrode; and a positive electrode separated from said negative electrode by means of said electrolyte of any of claims 10, 11, 12, 13, 14, 15, 24, 25, 26, 27, 28, 29, 30 or 31. 40. A composite electrode, comprising: an electrochemically active material; an optional electronically conductive additive; and a compound of any of claims 6, 7, 16 or 21. SUBSTITUTE SHEET

Inventors: FAUTEUX DENIS G, MASSUCCO ARTHUR A, POWELL JOHN R, VAN BUREN MARTIN F, FAUTEUX, DENIS, G., MASSUCCO, ARTHUR, A., POWELL, JOHN, R., VAN BUREN, MARTIN, F.
Applicants: LITTLE INC A, ARTHUR D. LITTLE, INC.
Application year: 1993
Main classification: C07H15
IPC codes: C07H15, C08G59, C08G65, C08L71, C08L101, H01G9, H01M4, H01M6, H01M8, H01M10