Additive composition for oil well cementing formulations

Abstract: An oil and gas well cementing composition has styrene/butadiene latex and a combination of nonionic surfactants for improved physical properties, especially fluid loss. The composition has no anionic surfactants.

Description: FIELD OF THE INVENTION The present invention relates to an improved oil and gas well cementing composition having a synergistic combination of nonionic surfactants which in particular improves the fluid loss, free water and rheological properties and provides good compressive strength of the resulting cementing composition. The invention also relates to the use of certain nonionic surfactants as additives for improving oil and gas well cementing compositions. BACKGROUND OF THE INVENTION The initial step in the recovery of hydrocarbons and gases from underground formations is the placement of the cement slurry, usually including cement, water and other additives, in the annular space between the porous formation and the steel casing. The main purpose of the cement in this annular space is to support the casing and also restrict fluid movement between formations. This process is referred to as primary cementing. The most important requirements to insure a satisfactory cementing job are that a highly homogenous cement is present in the annulus and that strong bonds develop between the rock formation, cement and steel casing. In order for this to happen, one must insure that the composition of the cement slurry pumped downhole does not change greatly during the whole cementing process. Therefore, contamination of the cement slurry by the drilling mud used in the previous operation or excessive loss of water to the formation must be carefully avoided. A well-formulated cement slurry will, therefore, exhibit low fluidloss to the formation, give either zero or very low free-water, have a viscosity low enough to be pumpable, set to a hardened mass within the desired time interval and provide adequate compressive strength to support the casing. The free water of a slurry is simply the supernatent fluid formed on top of the slurry column which provides an indication of the amount of settling of the cement particles during slurry placement. Excessive free water on top of the cement column will result in an incompetent zone close to the top of the liner which will have to be remedied with an expensive squeeze job. The viscosity of the slurry describes the rheological behavior of the slurry, which is determined by measuring the plastic viscosity (pv) and the yield point (yp) of the slurry. The cement slurry should be fluid and pumpable until it is in place, then it should start to set as soon as possible after placement. Any delay in the development of compressive strength will increase the "waiting on cement" time (WOC) necessary before proceeding with the next operation. The thickening time (TT) is used to describe the point at which the gelation of the cement has proceeded to such an extent so as to affect the pumping rates. Neat cement slurries have a fluidloss which varies from 700 to 2500 mL over a thirty minute period. This rate of loss will result in rapid dehydration and incorrect placement of the slurry and consequently will lead to failure of the whole cementing job. In order to attempt the control of fluid loss from the cement slurry to the surrounding rock formation, the permeability of the cement matrix must be reduced. This is achieved by addition of additives which provide excellent fluid loss control but at the same time do not adversely affect other properties of the slurry, such as free water, rheology, thickening times and compressive strength. Commercial fluid loss additives based on cellulosic polymers such as hydroxyethylcellulose (HEC) provide fairly good fluid loss control but there are some obvious drawbacks associated with cellulosic polymers. Typical loadings of these polymers to achieve good fluid loss control are in the range of 0.5 to 1% by weight of cement. Such high loadings results in a dramatic increase in the plastic viscosity and the yield point of the slurry, which translates to an increase in the energy needed to pump the slurry downhole. This means that every improvement in the fluidloss brought about by an increase in the level of the cellulosic polymer has to be paid for with high pumping pressures. Other drawbacks of cellulosic polymers include retardation in the thickening times of slurries and also the instability of these polymers at high temperatures, which limits their usefulness as a fluid loss additive to wells cooler than 93°C (200 degrees F). Synthetic polymers based on acrylamide and polyvinylpyrrolidone have been considered by the industry as additives for fluid loss control in cement compositions, but they have not come into wide spread use because of certain inherent drawbacks. Both acrylamide and polyvinyl pyrrolidone are prone to hydrolysis in the alkaline environment of the cement composition and therefore cause excessive retardation in the development of cement compressive strength. Furthermore polyvinylpyrrolidone is expensive and has a strong flocculating behavior which makes it an unattractive candidate as an additive in cement compositions. The synthetic polymers used as fluid loss additives are typically high molecular weight polymers which are quite expensive and this limits the amount of polymeric additive that can be added to the cement composition. Even if the cost factor is overlooked, high loadings of synthetic polymers may give improved fluid loss properties but often lead to viscous slurries which require increased pumping energy. The art is replete with copolymers which function as additives in cement compositions, but the inherent drawbacks associated in the form of undesirable side effects in the case of cellulosic and some synthetic polymers, coupled with the high cost of synthetic polymers have severely curtailed their widespread use in the industry. As heretofore noted, slurry compositions for oil and gas well cementing typically require that the slurry be fluid enough to be pumpable. This means that the plastic viscosity of the slurry should be less than 0.1 Pa s (100 centipoises (cps)), and more preferably less than 50 cps. In addition, the yield point of the slurry should be less than 9.6 Pa (20 lbs/100 ft 2 ), the fluid loss be less than 50 mL/30 minutes and the freewater be less than or equal to 3 mL over a two hour standing period. Cementing compositions meeting these requirements can be extremely difficult to design, and often times do not meet all of these requirements. Certain cementing compositions which contain anti-gas channeling additives have been described in the art. For example, Parcevaux et al., U.S. Patent No. 4,537,918, describes a cement composition which contains styrene-butadiene latex, as well as a stabilizer. The stabilizer is described as an anionic component of the cement composition which is selected from the group of lignosulfonates and their partly desulfonated derivative, sulfonic acid or sulfite modified melamine-formaldehyde resins, formaldehyde/sulfonate naphthalene resins, and condensation products of bi-nuclear sulfonated phenols and of formaldehyde. Each compound in this recited class of stabilizers is thus required to be anionic and to include a compound which contains sulphur in its molecule. In Parcevaux et al., U.S. Patent No. 4,721,160, there is also described a cement slurry composition which contains a styrene butadiene latex and a stabilizer. However, the patentees limit their additive for use with a resulting cement composition having a specific gravity within the range of 1.2 to 1.6, i.e. a lightweight cement slurry composition. In addition, U.S. Patent No. RE 28,722 reissued to Sanders, U.S. Patent No. 3,043,790, describes a cement mortar composition which includes a styrene butadiene additive system having three necessary additives. These include a nonionic surfactant, an ionic surfactant and a polyorganosiloxane fluid surfactant. The preferred nonionic surfactants include condensation products of ethylene oxide with phenols, naphthols, and alkyl phenols, for example octyphenoxy- nonaoxyethyleneethanol. There appears to be no mention made of the use of this particular composition in oil and gas well cementing applications. There presently exists a need in the art for an additive system which is relatively inexpensive, and provides superior fluid loss control via a synergistic combination of only nonionic surfactants, without adversely affecting other critical properties of the cement slurry for oil and gas well cementing. OBJECTS OF THE INVENTION It is therefore an object of the present invention to provide a cementing composition for use in oil and gas wells which comprises a synergistic combination of nonionic surfactants which improves several of the physical properties of the cement composition. It is also an object of the invention to provide for the use of nonionic surfactants as additives to improve cementing compositions used in the drilling industry. Another object of the present invention is to utilize only nonionic surfactants in combination with styrene-butadiene latex and cement which gives a readily mixable cement slurry for use in oil and gas wells. A further object of the invention is to provide a cement composition having nonionic surfactant additives to achieve a set of rheological properties which makes it readily pumpable. Another object of the present invention is to have an oil well cementing composition with excellent physical properties without the addition of anionic surfactants as additives. Still another object of the invention is to have an oil and gas well cementing composition which gives very low fluid loss over a thirty minute interval. Another object is to have a cementing composition which provides low free water values. A further object is to have a cement slurry composition which is not subject to excessive retardation, and which has good compressive strength. SUMMARY OF THE INVENTION These and other objects of the invention are achieved by providing an oil and gas well cementing composition which is made up of cement, and a styrene/butadiene latex in an amount of from 5% to 30% by weight of the dry cement, that is, without water. The ratio of styrene to butadiene in the latex is typically about 2:1. As part of the composition there is also from 0.05% to 2%, more preferably from 0.08% to 0.7% of the nonionic surfactant alkylphenol ethoxylate having a molecular weight of from 1000 to 3000 and having in most cases from about 25 to about 50 moles of ethylene oxide (EO) (n equals in most cases about 25 to about 50). The alkylphenol ethoxylate has the following formula: R - C 6 H 4 - O - [CH 2 - CH 2 - O] n - H where R is a butyl, pentyl, hexyl, heptyl, octyl, nonyl or decyl group. In a preferred embodiment of the invention, the alkylphenol ethoxylate has a molecular weight range of from 1300 to 2500, and even more preferably from 1500 to 2200. The moles of ethylene oxide (value of n) are preferably from about 28 to about 45, and even more desirably from about 30 to about 40. In an especially preferred embodiment, the molecular weight is about 1730 and the moles of EO are about 35. It is in this embodiment that the alkylphenol ethoxylate is octylphenolethoxylate. In combination with the heretofore alkylphenol ethoxylate, there is also from 0.05% to 2% of one or more nonionic surfactants from the group consisting of tetra-functional ethylene oxide/propylene oxide ethylenediamine block copolymers of the following formula: having molecular weights of from 3000 to 30,000 and the values of all the x's and y's are such that the surfactant has an ethylene oxide (EO) content of from 10 to 90% by weight of the polymer; and the nonionic surfactant of the formula: having a molecular weight of from 1300 to 12,000, more preferably having a molecular weight of about 11,400, and the values of x, y, and xl are such that the surfactant has an ethylene oxide content of from 10 to 90% based upon the weight of the polymer. Also in a preferred embodiment of the invention, one or more of the heretofore ethylenediamine block copolymers is selected from the group of copolymers having molecular weights of about 3600, about 5500, about 6700 and about 25,000. Water makes up the remainder of the cement composition in an amount such that the total quantity of water is from 30% to 60% by weight of the dry cement. Unless otherwise specified, all quantities of individual components of the cement composition are expressed in terms of weight percentage based on the weight of the dry cement. All molecular weights are expressed as weight average molecular weight or M W . Further provided as part of the invention is the use of the heretofore described alkylphenol ethoxylates in combination with at least one of the heretofore described nonionic surfactant additives as stabilizer additives in oil and gas well cementing compositions. Also provided is a method of improving the rheological properties of cementing compositions which comprises adding the heretofore nonionic surfactant stabiiizer additives in the quantities set forth. It has now been discovered that the synergistic combination of alkylphenol ethoxylate with one or more of the heretofore other nonionic surfactants provides measurable improvements in the plastic viscosity, yield point, fluid loss, and freewater values, as well as other physical properties of cement compositions used in drilling oil and gas wells. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The cement utilized as part of the composition according to the invention is any of the known cements available to those skilled in the art of oil and gas well cementing. Of these, American Petroleum Institute (API) Class H is preferred. Particularly preferred is Texis Lehigh Class H cement available from the Texis Lehigh Company of Buda, Texas. The styrene/butadiene latex is added to the cement in an amount of from 5% to 30% based on the weight of the cement. In a preferred embodiment, the latex comprises from 8% to 25%, most desirably, about 15%, by weight of the cement. The ratio of styrene to butadiene in the latex is typically about 2:1, although a somewhat higher or lower ratio is certainly within the scope of the invention. In most instances, a dispersion of about 50% of the active polymer styrene/butadiene is formed with about 50% water, and this dispersion in turn is added to the cement. Styrene/butadiene latexes are considered to be very compatible with cement. These latexes are typically manufactured via an emulsion polymerization process to yield a dispersion with an average of about 50% latex polymer content, the remainder being water. Since these dispersions have a relatively high percentage of active polymer, it is possible to utilize a high loading in cement compositions in order to obtain a uniform well-dispersed cement matrix. It is this cement matrix that effectively controls the loss of fluid from the cement composition. Since the styrene-butadiene polymer is dispersed in the aqueous medium, it is possible to use high loadings of the polymer without imparting high viscosity to the cement slurry. As part of the invention, there is also included a nonionic alkylphenol ethoxylate surfactant additive as a stabilizer. It is especially desirable that this surfactant be octylphenol ethoxylate with a molecular weight in the range of from 1500 to 2200, and having from about 30 to about 41 moles of ethylene oxide (EO). Especially preferred is octylphenol ethoxylate having a molecular weight of about 1730 and about 35 moles of EO. Octylphenol ethoxylate is octylphenol to which ethylene oxide is added. The octylphenol ethoxylate has the following formula: CH 3 (CH 2 ) 7 - C 6 H 4 - O -[CH 2 -CH 2 -O] n - H wherein n has a value of from about 30 to about 41. This component is added in an amount of from 0.05% to 2% based on the weight of the cement. In a preferred embodiment, the octylphenol ethoxylate is added in an amount of from 0.08% to 0.7%, even more preferably from 0.1% to 0.5%. Particularly preferred for use with the composition according to the invention is the octylphenol ethoxylate available from BASF Corporation and marketed under the tradename ICONOL OP 30 or 40. This product may also be known under the name TRITON X 405, which is available from Union Carbide. In combination with octylphenol ethoxylate is added 0.05% to 2% of one or more nonionic surfactants from the group consisting of tetra-functional ethylene oxide/propylene oxide ethylenediamine block copolymers having the following formula: having molecular weights of from 3,000 to 30,000, more preferably having molecular weights of about 3600, about 5500, about 6700 and about 25,000; and the nonionic surfactant additive of the formula: having a molecular weight of from 1300 to 12,000, more preferably having a molecular weight of about 11,400. In a preferred embodiment of the invention, one or more of these surfactants is added in an amount of from 0.08% to 0.7%, even more preferably from 0.15% to 0.5%. The heretofore ethylenediamine nonionic surfactant having a molecular weight of about 3600 is available from BASF Corporation under the trademark TETRONIC ® 701. The surfactant having a molecular weight of about 5500 is also available from BASF Corp. under the trademark TETRONIC ® 704. The surfactant having a molecular weight of about 6700 is available from BASF Corp. under the trademark TETRONIC ® 904, and the surfactant with the molecular weight of about 25,000 is also available from BASF under the trademark TETRONIC ® 908. The nonionic surfactant having a molecular weight of about 11,400 is available from BASF under the trademark PLURONIC ® F-88. Water is also added to the cement composition in amounts of from 30% to 60%, preferably from 36% to 42%, and more preferably about 38% by weight of the cement. One or more defoamers may also be added to the various embodiments of the cement composition as part of the invention. These are added for their deairentrainment properties imparted to the resulting cementing composition. Any one of a number of defoamers available to those skilled in the art may be utilized. Preferred for use is the defoamer available from BASF Corporation under the trademark PLURACOL ® 4010. This is a polypropylene glycol with an average molecular weight of about 3300. The defoamer is typically added to the composition in an amount of from 0.01% to 0.1% based on the weight of the cement. In some instances certain other additives kncwn as retarders or accelerators may be added to the cement composition to adjust the thickening time of the cement slurry for the drilling operation. Because "Waiting on Cement" (WOC) is very expensive these additives are often added in quantities of from 0.5 to 1.5%. U.S. Patent No. 4,527,918 describes many of the known accelerators and retarders available to those in the art, and the salient portions thereof are incorporated herein by reference. Sometimes in addition to these additives, silica flour is added in amounts of from 30% to 35% by weight of the cement if the temperature of the oil well is greater than 104°C (220 degrees F). Since Portland cement experiences strength retrogression at high temperatures, silica flour can be added to increase the compressive strength of cement. The physical properties of the cement slurry compositions according to the various embodiments of the invention should be as follows: the fluidloss should be less than about 55 mL/30 minutes, preferably less than about 50 mL/30minutes, and more preferably less than about 40 mL/30 minutes. The plastic viscosity cf the composition should be less than about 0.1 Pa s (100 cp), and more preferably less than about 0.05 Pa s (50 cp). Additionally, the yield point should be less than about 9.6 Pa (20 lbs/100 ft 2 ). The freewater value should be less than or equal to about 3 mL for a two hour standing period, preferably less than about 2 mL, and more preferably less than about 1 mL. The following example will illustrate how to make the composition according to one embodiment of the invention. This example should not be construed as limiting the scope of the invention. EXAMPLE 1 To a Waring blender, approximately 327 mL of water is added. Next, about 0.35 grams of defoaming agent and 1.3 grams of the surfactant TRITON X 405 are added and this mixture is allowed to stir at low speed (1000 rpm). If the second nonionic surfactant stabilizer is liquid, approximately 1.3 grams is also added along with the TRITON X 405 at this point. Next, approximately 131 grams of styrene/butadiene latex is added. If the second stabilizer is a solid it is first blended with about 860 grams of dry cement and the resulting mixture is added to the solution within 10 seconds with the stirring maintained at 4000 rpm. Soon after the cement mixture is added, stirring is increased to 12,000 rpm and the mixture is allowed to stir for 35 seconds after which stirring is stopped. Rheology measurements are made at room temperature after which the slurry is homogenized in an atmospheric consistometer for twenty minutes at the desired operating temperature. The pourability of the slurry is determined at this point. If after twenty minutes of stirring the resulting slurry is so thick that it does not pour out of the consistometer, then the slurry is discarded and no further tests are performed. If the slurry is homogenous and pourable then routine cement testing is then performed. EXAMPLE 2 The following API Tests at the indicated temperatures were performed with the composition according to various embodiments of the invention. The compositions performed extremely well based upon several measurable parameters. These tests further highlight the use of the nonionic surfactant stabilizer additives as part of the cement compositions according to the invention. Measurements were based on the following: Fluidloss : Thirty minute fluidloss values were measured under static conditions using a high temperature, high pressure filter press made by Bariod. All tests were conducted at 69 bar (1000 psi) using nitrogen as the pressurizing gas. Freewater : The amount of freewater was determined by measuring the amount of water present on top of a 250 mL graduated cylinder filled with cement slurry, after a two hour standing period at room temperature. Rheology : Rheological properties were measured using Chan 35 Viscometer equipped with a R1 rotor sleeve and a B1 bob. All measurements were made at room temperature on freshly prepared slurries. Thickening Time : Pressurized thickening times were measured with a high temperature, high pressure consistometer using the appropriate API schedules. The reported value indicates the length of time taken by the slurry to achieve a consistency of 70 Bc. Compressive Strength : The slurries were cured in a pressurized curing chamber and the compressive strength of the cured cement was tested by crushing the 2 inch by 2 inch cement cubes with a Soiltest hydraulic press with a gage measuring up to 1380 bar (20,000 psi). Latex Loadings : 15.3% BWOC(= 1.73 gallons/sack)(BWOC = Based on Weight of Cement) 10.2% BWOC(= 1.15 gallons/sack) 8.1% BWOC(= 0.92 gallons/sack) Those skilled in the art may find that the loading of latex may vary somewhat depending upon individual oil well conditions. API Test at 82°C (180 degrees F) (with TETRONIC ® 908 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): Texas Lehigh Class H Cement 860 grams Styrene/Butadiene Latex 15.3% Defoamer 0.04% Water 38% TRITON X405 0.153% TETRONIC ® 908 0.153% API Fluidloss at 30 minutes 38 mL Freewater 3 mL Plastic Viscosity (Pa s) 0.048 (48 cps) Yield Point (Pa) 9.2 (19.1 lbs/100 ft 2 ) Pressurized Thickening Time 81 minutes (Cement Casing Schedule 6g-7, 10,000 ft.) Compressive Strength 216 bar (3132 psi) API Test at 82°C (180 degrees F) (with TETRONIC ® 908 additive) In this test, Styrene/Butadiene Latex was subjected to four Freeze/Thaw Cycles before use. In each cycle the temperature was lowered to -20 degrees C and the dispersion was allowed to stabilize at this temperature for two hours. The dispersion was then allowed to warm to room temperature. No coagulum was observed at the end of each cycle. Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): The above test demonstrates that the use of latex subjected to successive freeze/thaw cycles imparts no reduction in performance to the resulting cement composition. API Test at 60°C (140 degrees F) (with TETRONIC ® 908 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): Texas Lehigh Class H Cement 860 grams Styrene/Butadiene Latex 10.2% Defoamer 0.04% Water 38% TRITON X405 0.102% TETRONIC ® 908 0.102% API Fluidloss at 30 minutes 38 mL Freewater 3 mL Plastic Viscosity (Pa s) 0.0315 (31.5 cps) Yield Point (Pa) 13.5 (28.2 lbs/100 ft 2 ) Pressurized Thickening Time 91 minutes (Cement Casing Schedule 5g-6 8000 ft.) Compressive Strength 203 bar (2944 psi) API Test at 27°C (80 F) (with TETRONIC ® 908 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): API Test at 82°C (180 F) (with TETRONIC ® 904 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): Texas Lehigh Class H Cement 860 grams Styrene/Butadiene Latex 15.3% Defoamer 0.04% Water 38% TRITON X405 0.153% TETRONIC ® 904 0.153% API Fluidloss at 30 minutes 43 mL Freewater 2 mL Plastic Viscosity (Pa s) 0.03 (30 cps) Yield Point (Pa) 8.7 (18.1 lbs/100 ft 2 ) Pressurized Thickening Time 146 minutes (Cement Casing Schedule 6g-7 2000 ft.) Compressive Strength 189 bar (2733 psi) API Test at 82°C (180 F) (with TETRONIC ® 701 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): Texas Lehigh Class H Cement 860 grams Styrene/Butadiene Latex 15.3% Defoamer 0.04% Water 38% TRITON X405 0.153% TETRONIC ® 701 0.153% API Fluidloss at 30 minutes 31 mL Freewater 1 mL Plastic Viscosity (Pa s) 0.03 (30 cps) Yield Point (Pa) 8.7 (18.1 lbs/100 ft 2 ) Pressurized Thickening Time 147 minutes (Cement Casing Schedule 6g-7 2000 ft.) Compressive Strength 211 bar (3062 psi) API Test at 82°C (180 F) (with TETRONIC ® 704 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): Texas Lehigh Class H Cement 860 grams Styrene/Butadiene Latex 15.3% Defoamer 0.04% Water 38% TRITON X405 0.153% TETRONIC ® 704 0.153% API Fluidloss at 30 minutes 53 mL Freewater 0.5 mL Plastic Viscosity (Pa s) 0.028 (28 cps) Yield Point (Pa) 7.9 (16.5 lbs/100 ft 2 ) Pressurized Thickening Time 141 minutes (Cement Casing Schedule 6g-7 2000 ft.) Compressive Strength 192 bar (2784 psi) API Test at 82°C (180 F) (with PLURONIC ® F-88 additive) Cement Slurry Composition (%'s Based on Weight of Cement, or BWOC): Texas Lehigh Class H Cement 860 grams Styrene/Butadiene Latex 15.3% Defoamer 0.04% Water 38% TRITON X405 0.153% PLURONIC ® F-88 0.153% API Fluidloss at 30 minutes 45 mL Freewater 1 mL Plastic Viscosity (Pa s) 0.033 (33 cps) Yield Point (Pa) 6.6 (13.8 lbs/100 ft 2 ) Pressurized Thickening Time 143 minutes (Cement Casing Schedule 6g-7 2000 ft.) Compressive Strength 168 bar (2430 psi) These results demonstrate that typical fluidloss values are lower than 50 mL for a latex loading between 10.2 and 15.3% BWOC in the temperature range of 27°C (80 F) to 82°C (180 F), the freewater values are lower than 3 mL in the latex loading range and the temperature range set forth above. Plastic viscosity values are lower than 0.05 Pa s (50 cps), and the yield point and plastic viscosity values decrease with increased latex loadings. A good set of compressive strength properties was observed with Class H cement in the temperature range of 27°C (80 F) to 82°C (180 F). Additional dispersants, notably anionic surfactants, were not required to achieve these sets of properties. EXAMPLE 3 In order to fully assess the efficacy of the cement composition according to the invention, comparative tests were done utilizing: 1) no surfactant stabilizer additive 2) formaldehyde/sulfonate naphthalene resin alone (anionic surfactant disclosed in U.S. Patent No. 4,537,918) 3) TRITON X 405 nonionic surfactant alone 4) TRITON X 405 nonionic surfactant with 2) above 5) TETRONIC ® 701 nonionic surfactant alone 6) TETRONIC ® 704 nonionic surfactant alone 7) TETRONIC ® 904 nonionic surfactant alone 8) TETRONIC ® 908 nonionic surfactant alone 9) PLURONIC ® F-88 nonionic surfactant alone In each test, 860 grams of Texis Lehigh Class H Cement was utilized. 15% of styrene/butadiene latex, 0.04% of defoamer, and 38% of water was also utilized (all %'s BWOC). The fluid loss values were as follows at 82°C (180 degrees F): API Fluid Loss at 30 minutes: 1) no surfactant stabilizer additive - fluid loss could not be measured as cement slurry could not be poured. 2) 0.153% sodium naphthalene sulfonic acid condensate with formaldehyde alone (anionic surfactant disclosed in U.S. Patent No. 4,537,918) - fluid loss was 138 mL. 3) 0.153% TRITON X 405 nonionic surfactant alone - fluid loss was 130 mL. 4) 0.153% TRITON X 405 nonionic surfactant with 1% 2) above - fluid loss was 112 mL. 5) TETRONIC ® 701 nonionic surfactant alone - fluid loss was 137 mL. 6) TETRONIC ® 704 nonionic surfactant alone - fluid loss was 139 mL. 7) TETRONIC ® 904 nonionic surfactant alone - fluid loss was 126 mL. 8) TETRONIC ® 908 nonionic surfactant alone - fluid loss was 135 mL. 9) PLURONIC ® F-88 nonionic surfactant alone - fluid loss was 108 mL. Examples 2 and 3 demonstrate the synergism between the nonionic surfactants as part of the claimed invention according to the various embodiments thereof. While the invention has been described in each of its embodiments, it is expected that certain modifications thereto may be made by those skilled in the art without departing from the true spirit and scope of the invention, as set forth in the specification and the accompanying claims.

Claims: An oil and gas well cementing composition, comprising: a) cement; b) styrene/butadiene latex in an amount of from 5 % to 30 % by weight of said cement; c) from 0.05 % to 2 % by weight of the nonionic surfactant stabilizer additive alkylphenol ethoxylate of the following formula: R-C 6 H 4 -O-[CH 2 -CH 2 -O] n -H wherein R is butyl, pentyl, hexyl, heptyl, octyl, nonyl or decyl, said alkylphenol ethoxylate having a molecular weight of from 1000 to 3000; d) from 0.05 % to 2 % by weight of at least one nonionic surfactant stabilizer additive selected from the group consisting of tetra-functional ethylene oxide/propylene oxide ethylenediamine block copolymers having the following formula: and a molecular weight range of from 3000 to 30,000 and an ethylene oxide content of from 10 to 90 %, and the nonionic surfactant additive of the formula: having a molecular weight of from 1300 to 12,000 and an ethylene oxide content of form 10 to 90 %; and e) water in an amount such that the total quantity of water is from 30 % to 60 % by weight of said cement. The composition as claimed in claim 1, wherein said additive c) is present in an amount of from 0.08 to 0.7 %. The composition as claimed in claim 2, wherein said additive c) is present in an amount of from 0.1 to 0.5 %. The composition as claimed in claim 1, wherein said additive d) is present in an amount of from 0.08 to 0.7 %. The composition as claimed in claim 4, wherein said additive d) is present in an amount of from 0.15 to 0.5 %. The composition as claimed in claim 1, further comprising one or more defoamers in an amount of from 0.01 to 0.1 % based on the weight of said cement. The composition as claimed in claim 1, said composition having a fluid loss of less than or equal to 50 mL/30 minutes. The composition as claimed in claim 1, said composition having a plastic viscosity of less than or equal to 0.1 Pa s (100 centipoises). The composition as claimed in claim 8, said composition having a plastic viscosity of less than or equal to 0.05 Pa s (50 centipoises). The composition as claimed in claim 1, said composition having a freewater value of less than or equal to 3 mL over an approximately 2 hour standing period. The composition as claimed in claim 1, said composition having a yield point value of less than or equal to 9.6 Pa (20 lbs/100 ft 2 ). The composition as claimed in claim 1, wherein said alkylphenol ethoxylate has a molecular weight range of from 1300 to 2500. The composition as claimed in claim 12, wherein said alkylphenol ethoxylate has a molecular weight range of from 1500 to 2200. The composition as claimed in claim 13, wherein said alkylphenol ethoxylate is octylphenol ethoxylate having a molecular weight of about 1730, and n equals about 35. The composition as claimed in claim 13, wherein said ethylene diamine nonionic surfactant is selected form the group consisting of those having a molecular weight of about 3600, about 5500, about 6700 and about 25,000, and wherein said ethylene oxide/ propylene oxide/ ethylene oxide triblock copolymer nonionic surfactant has a molecular weight of about 11,400. The use of a combination of components c) and d) of claim 1 as stabilizer additives in oil and gas well cementing compositions. A method of improving the rheological properties of oil well cementing compositions which comprises adding the stabilizer additives combination of components c) and d) of claim 1.

Inventors: GOPALKRISHNAN SRIDHAR, ROZNOWSKI MICHAEL, GOPALKRISHNAN, SRIDHAR, ROZNOWSKI, MICHAEL
Applicants: BAKER PERFORMANCE CHEM, BAKER PERFORMANCE CHEMICALS INCORPORATED
Application year: 1993
Main classification: E21B33
IPC codes: C04B28, C04B24, C09K8