Flame retardant compositions

Abstract: A composition comprising: (a) polyethylene having a density equal to or less than 0.925 gram per cubic centimeter, grafted with an unsaturated aliphatic diacid anhydride; and (b) magnesium hydroxide, surface treated with a saturated or unsaturated carboxylic acid or a metal salt thereof in an amount of about 0.1 to about 1 part by weight of acid or salt per 100 parts by weight of magnesium hydroxide.

Description: This invention relates to flame retardant compositions containing an ethylene copolymer and a magnesium hydroxide filler. The compositions are useful in the insulation and jacketing of electrical conductors and communications media such as fiber optics cable. Wire and cable, whether used for the transmission of power or communications, are usually stored outside or in unheated areas before installation. If the insulation or jacketing becomes brittle at low temperatures and cracks, the integrity of the wire or cable is defeated and a short circuit with its attendant problems becomes a real possibility. Consequently, the specifications for the insulating or jacketing layers generally require that these materials pass a low temperature brittleness test. Low temperature performance of minus 50°C or higher is often cited by wire and cable manufacturers as desirable, particularly for installations in, for example, Canada. A typical power cable is constructed of metal conductors insulated with a polymeric material. These elements are generally twisted to form a core and are protected by another polymeric sheath or jacket material. In certain cases, added protection is afforded by inserting a wrap between the core and the sheath. EP-A-490354 discloses flame retardant compositions comprising (1) a homopolymer or copolymer of ethylene having bonded thereto, through an anhydride of an unsaturated diacid, one or more polyamides polyesters and/or polyurethanes; and (2) a metal hydrate flame retardant compound. Flame retardant compositions comprising polyethylene and magnesium hydroxide are useful in wire and cable applications, the polyethylene providing flexibility and the magnesium hydroxide, flame retardance. Unfortunately, these compositions do not come close to meeting the most desirable low temperature performance as far as brittleness is concerned. It is difficult, for example, to achieve a low temperature brittleness of O°C with a linear low density polyethylene flame retardant composition, let alone the desirable minus 50°C. An object of this invention, therefore, is to provide a flame retardant composition, which has outstanding low temperature brittleness resistance, thus being useful in the coldest of climes. Other objects and advantages will become apparent hereinafter. According to the present invention the above object is met by a composition consisting essentially of: (a) polyethylene having a density equal to or less than 0.925 gram per cubic centimeter, grafted with an unsaturated aliphatic diacid anhydride; and (b) magnesium hydroxide, surface treated with a saturated or unsaturated carboxylic acid or a metal salt thereof in an amount of 0.1 to 1 part by weight of acid or salt per 100 parts by weight of magnesium hydroxide. The polyethylene having a density equal to or less than 0.925 gram per cubic centimeter is a copolymer of ethylene and at least one alpha-olefin having 3 to 12 carbon atoms and preferably 3 to 8 carbon atoms. The density of the copolymer is preferably equal to or less than 0.915 gram per cubic centimeter and is preferably no lower than 0.860 gram per cubic centimeter. It can be produced, for example, in the presence of (i) a catalyst containing chromium and titanium, (ii) a catalyst containing magnesium, titanium, a halogen, and an electron donor; or (iii) a catalyst containing vanadium, an electron donor, an alkyl aluminum halide modifier, and a halocarbon promoter. Catalysts and processes for making the copolymer are described in US-A-4 101 445 and 4 302 565 and EP-A- 120 501. The melt index of the polyethylene can be in the range of 0.1 to 50 grams per 10 minutes and is preferably in the range of 0.4 to 10 grams per 10 minutes. The melt index is determined in accordance with ASTM D-1238, Condition E, measured at 190°C. Suitable alpha-olefin comonomers are exemplified by propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, and 1-octene. The portion of the polyethylene attributed to the comonomer(s), other than ethylene, is in the range of 1 to 49 percent by weight based on the weight of the copolymer and is preferably in the range of 15 to 40 percent by weight. Anhydrides of unsaturated aliphatic diacids are commonly grafted to various polyolefins. These anhydrides can have 4 to 20 carbon atoms and preferably have 4 to 10 carbon atoms. Examples of anhydrides, which are useful in this invention, are maleic anhydride, itaconic anhydride, and nadic anhydride. The preferred anhydride is maleic anhydride. Excess anhydride, if present after grafting, can be removed by devolatilization at temperatures in the range of 200°C to 250°C. The grafting is accomplished by using an organic peroxide catalyst, i.e., a free radical generator, such as dicumyl peroxide; lauroyl peroxide; benzoyl peroxide; tertiary butyl perbenzoate; di(tertiary-butyl) peroxide; cumene hydroperoxide; 2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3; 2,5-dimethyl-2,5-di(t-butylperoxy)hexane; tertiary butyl hydroperoxide; isopropyl percarbonate; and alpha,alpha'-bis(tertiary-butylperoxy)diisopropylbenzene. The organic peroxide catalyst may be added together with the anhydride. Grafting temperatures can be in the range of 100 to 300°C and are preferably in the range of 150 to 200°C. A typical procedure for grafting maleic anhydride onto polyethylene is described in US-A-4 506 056. Grafting can also be accomplished by adding a solution of anhydride, an organic peroxide catalyst, and an organic solvent to polyethylene in particulate form. The organic peroxide catalyst is soluble in the organic solvent. Various organic solvents, which are inert to the reaction, can be used. Examples of useful organic solvents are acetone, methyl ethyl ketone, methyl propyl ketone, 3-pentanone, and other ketones. Other carrier solvents which allow solubilization of peroxide and anhydride, and which strip off well under appropriate devolatilization conditions may be used. Acetone is a preferred solvent because it acts as a stripping agent for residuals such as non-grafted anhydride or anhydride by-products. The anhydride solution can contain 10 to 50 percent by weight anhydride; 0.05 to 5 percent by weight organic peroxide catalyst; and 50 to 90 percent by weight organic solvent based on the total weight of the solution. A preferred solution contains 20 to 40 percent anhydride; 0.1 to 2 percent peroxide; and 60 to 80 percent solvent. The anhydride grafted polyethylene can contain 0.05 to 5 parts by weight of anhydride per 100 parts by weight of polyethylene and preferably contains 0.1 to 2 parts by weight of anhydride per 100 parts by weight of polyethylene. The polyethylene can also be grafted with an unsaturated monomeric silane having one or more hydrolyzable groups in order to make the polyethylene hydrolyzable thus permitting moisture cure. While such grafting can be accomplished simultaneously with the grafting of the unsaturated aliphatic diacid anhydride, the grafting can also be effected before or after the grafting of the anhydride, if desired. The silane grafted copolymer can be prepared by the technique described below. In this copolymer, the portion attributed to the silane is present in an amount of 0.5 percent to 10 percent by weight based on the weight of the copolymer and is preferably incorporated into the copolymer in an amount of 0.5 to 4 percent by weight. Generally speaking, any unsaturated monomeric silane containing at least one hydrolyzable group can be used. The silane used to modify the copolymer can be, among others, an alkenyl alkoxy silane such as a vinyl trialkoxy silane exemplified by vinyl trimethoxy silane, vinyl triethoxy silane, or vinyl isopropoxy silane. If slower water cure or better shelf stability are desired, vinyl triisobutoxy silane or vinyl tris(2-ethyl-hexoxy) silane can be used. The hydrolyzable silane and anhydride grafted polyethylene can be crosslinked with moisture in the presence of a conventional silanol condensation catalyst such as dibutyl tin dilaurate, dioctyl tin maleate, stannous acetate, stannous octoate, lead naphthenate, zinc octoate, iron 2-ethyl hexoate, and other metal carboxylates. Further acceleration of crosslinking can be accomplished by adding a cocatalyst such as tetramethoxy titanate, tetraisopropyl titanate, tetramethyl titanate, or other organo titanates mentioned in US-A-4 446 279. The catalysts can be introduced into the composition in conventional amounts, typically 0.005 to 1 part by weight of primary catalyst per 100 parts by weight of copolymer and 0.25 to 10 parts by weight of cocatalyst per 100 parts by weight of copolymer. A typical procedure for preparing a silane grafted polyethylene follows: 100 parts of ethylene/1-butene copolymer having a density of 0.90, 0.2 part of polymerized 1,3-dihydro-2,2,4-trimethylquinoline (an antioxidant), 0.1 part of dicumyl peroxide, and 4 parts of vinyl tri-2-ethyl-hexoxy silane are mixed in a Brabender mixer at a temperature in the range of 80°C to 115°C, a temperature low enough to keep the dicumyl peroxide below its decomposition temperature. After mixing for five minutes, the temperature is raised to a temperature in the range of 150°C to 220°C. The batch is then mixed for 5 to 10 minutes during which grafting of the silane to the copolymer occurs. The antioxidant is used as a radical trap to control the amount of crosslinking. The foregoing technique can be repeated, for example, with 3 parts of vinyltriisobutyoxysilane and 0.1 part of the antioxidant, tetrakis[methylene(3-5-di-tert-butyl-4-hydroxyhydro-cinnamate)]methane; initial mixing is in the range of 110°C to 120°C; grafting is for five minutes at 185°C. Various processes for preparing silane grafted polyethylene and numerous unsaturated silanes suitable for use in preparing these polymers and bearing hydrolyzable groups such as alkoxy, oxyaryl, oxyaliphatic, and halogen are mentioned in US-A-3 075 948; 3 225 018; 4 412 042; 4 413 066; 4 574 133; and 4 593 071. It will be noted that the same organic peroxide catalyst is used in silane grafting as in anhydride grafting. The magnesium hydroxide is one conventionally used in wire and cable applications. A preferred magnesium hydroxide has the following characteristics: (a) a strain in the <101> direction of no more than 3.0 x 10 -3 ; (b) a crystallite size in the <101> direction of more than 80 nm (800 Å); and (c) a surface area, determined by the BET method, of less than 20 square meters per gram. The preferred magnesium hydroxide and a method for its preparation are disclosed in US-A-4 098 762. A preferred characteristic of the magnesium hydroxide is that the surface area, as determined by the BET method, is less than 10 square meters per gram. The amount of magnesium hydroxide used in the composition can be in the range of about 100 to about 180 parts by weight of magnesium hydroxide per one hundred parts by weight of anhydride grafted polyethylene and is preferably in the range of 120 to 160 parts by weight of magnesium hydroxide per one hundred parts by weight of anhydride grafted polyethylene. The magnesium hydroxide is surface treated with a saturated or unsaturated carboxylic acid, which can have 8 to 24 carbon atoms and preferably has 12 to 18 carbon atoms, or a metal salt thereof. Mixtures of these acids and/or salts can be used, if desired. Examples of suitable carboxylic acids are oleic, stearic, palmitic, isostearic, and lauric; of metals which can be used to form the salts of these acids are zinc, aluminum, calcium, magnesium, and barium; and of the salts themselves are magnesium stearate, zinc oleate, calcium palmitate, magnesium oleate, and aluminum stearate. The amount of acid or salt can be in the range of 0.1 to 1 part by weight of acid or salt per one hundred parts by weight of magnesium hydroxide and preferably is 0.15 to 0.50 part by weight per one hundred parts by weight of magnesium hydroxide. Various conventional additives can be added in conventional amounts to the composition of the invention. Typical additives are antioxidants, ultraviolet absorbers, antistatic agents, pigments, dyes, other fillers including carbon black and aluminum silicate, slip agents, fire retardants, stabilizers, crosslinking agents, halogen scavengers, smoke inhibitors, crosslinking boosters, processing aids, e.g., metal carboxylates, lubricants, plasticizers, and viscosity control agents. The electrical conductor can be comprised of metal such as copper or carbon, and the communications medium of glass or plastic filaments used, for example, in fiber optics applications. Patents and other publications mentioned in this specification are incorporated by reference herein. The invention is illustrated by the following examples. EXAMPLES 1 to 12 Polyethylene I is an unmodified linear low density polyethylene, which is a copolymer of ethylene and 1-hexene having a density of 0.917 gram per cubic centimeter and a melt index of 3.4 grams per 10 minutes. Polyethylene II is a maleinized copolymer of ethylene and 1-butene having a density of 0.900 gram per cubic centimeter and a melt index of 0.4 grams per 10 minutes. The polyethylene is grafted with 0.3 part by weight maleic anhydride per 100 parts by weight of polyethylene according to the procedure mentioned above. All of the magnesium hydroxides used in the examples fall within the definition of the preferred magnesium hydroxide mentioned above and are the same except for their surface treatment. Magnesium hydroxide I is surface treated with 3 parts by weight of stearic acid per 100 parts by weight of magnesium hydroxide. Magnesium hydroxide II is surface treated with 3 parts by weight of oleic acid per 100 parts by weight of magnesium hydroxide. The magnesium hydroxide is granular. Magnesium hydroxide III is surface treated with 0.25 part by weight of oleic acid per 100 parts by weight of magnesium hydroxide. The magnesium hydroxide is granular. The antioxidant is tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)]methane. Sixteen compositions are processed into test specimens as required by the test procedure for low temperature brittleness (LTB), i.e. ASTM D-746-73 and the test procedure is carried out. LTB is reported in degrees Centigrade. Variables and results are reported in the Table.

Claims: A composition consisting essentially of: (a) polyethylene having a density equal to or less than 0.925 gram per cubic centimeter, grafted with an unsaturated aliphatic diacid anhydride; and (b) magnesium hydroxide, surface treated with a saturated or unsaturated carboxylic acid or a metal salt thereof in an amount of 0.1 to 1 part by weight of acid or salt per 100 parts by weight of magnesium hydroxide. The composition defined in claim 1 wherein the anhydride is maleic anhydride. The composition defined in claim 1 or 2 wherein the polyethylene is additionally grafted with a hydrolyzable unsaturated monomeric silane. The composition defined in any one of claims 1-3 wherein the magnesium hydroxide has the following characteristics: (a) a strain in the <101> direction of not more than 3.0 x 10 -3 ; (b) a ,crystallite size in the <101> direction of more than 80 nm (800 Å); and (c) a surface area, determined by the BET method, of less than 20 square meters per gram. The composition defined in claim 4 wherein the magnesium hydroxide has a surface area as determined by the BET method, of less than 10 square meters per gram. The composition defined in any one of claims 1-5 wherein the magnesium hydroxide is present in an amount of 100 to 180 parts by weight of magnesium hydroxide per 100 parts by weight of anhydride grafted polyethylene. The composition defined in any one of claims 1-6 wherein the amount of acid or salt is in the range of 0.15 to 0.50 part by weight per 100 parts by weight of magnesium hydroxide. The composition defined in any one of claims 1-7 wherein the anhydride grafted polyethylene contains 0.05 to 5 parts by weight of anhydride per 100 parts by weight of polyethylene. A composition consisting essentially of: (a) polyethylene having a density in the range of 0.860 to 0.915 gram per cubic centimeter, grafted with maleic anhydride in an amount of 0.1 to 2 parts by weight of maleic anhydride per 100 parts by weight of polyethylene; and (b) 100 to 180 parts by weight of magnesium hydroxide per 100 parts by weight of anhydride grafted polyethylene wherein the magnesium hydroxide has the following characteristics: (i) a strain in the <101> direction of not more than 3.0 x 10 -3 ; (ii) a crystallite size in the <101> direction of more than 80 nm (800 Å); and (iii) a surface area, determined by the BET method, of less than 10 square meters per gram, said magnesium hydroxide having been surface treated with an unsaturated carboxylic acid having 8 to 24 carbon atoms in an amount of 0.15 to 0.5 part by weight of acid per 100 parts by weight of magnesium hydroxide. An article of manufacture comprising an electrical conductor or a communications medium surrounded by one or more layers of the composition defined in any one of claims 1-9.

Inventors: JOW JINDER, KEOGH MICHAEL JOHN, JOW, JINDER, KEOGH, MICHAEL JOHN
Applicants: UNION CARBIDE CHEM PLASTIC, UNION CARBIDE CHEMICALS & PLASTICS TECHNOLOGY CORPORATION
Application year: 1993
Main classification: C08K9
IPC codes: C08K9, C03C25