Lining of a structure for inhibiting deposit of organisms

Abstract: The invention provides a method for the lining of an organism deposit-inhibition structure, which enables that structure to be easily lined to an application surface, excel in the capability to inhibit deposition of organisms and durability, dispense with maintenance work, and offer no toxicity problem. A resin layer (2) made up of an electrical insulating material is bonded to the inner wall periphery of a cylindrical pipe (1) member. A metal gauze (5) of a copper alloy is applied onto the surface of the resin layer (2). The metal gauze (5) is either unfolded and drawn out or rolled over with the inner side turned outwards for its application to the surface of the resin layer (2). The copper alloy has a Be content of 0.2 to 2.8% by weight, and is selected from, e.g, Be-Cu, Be-Co-Cu, Be-Co-Si-Cu and Be-Ni-Cu alloys.

Description: BACKGROUND OF THE INVENTION The present invention relates to the lining of a metal pipe member with a structure , said structure being adapted to inhibit deposition of marine organisms such as barnacles, blue mussel, and seaweed - hereinafter called the organism deposit-inhibition structure. Offshore or marine structures in contact with seawater are always exposed to contamination by marine organisms, resulting in appearance damage or malfunction. For instance, ships suffer a driving force drop when many forms of oceanic organisms are deposited onto their bottoms, etc., and thermoelectric power plants are forced to stop operation when various forms of oceanic organisms are built up on their seawater intake pits, because a serious problem arises in connection with the circulation of a seawater serving as a cooling medium. Among scores of techniques for inhibiting marine deposits studied so far in the art, there is typically now available a method for protecting an offshore structure against contamination, in which the surface of that structure in contact with seawater is coated with a coating material containing cuprous oxide or organotin. Another method is disclosed in JP-A-60-209505 that is directed to an adhesive member for inhibiting marine deposits, which comprises a sheet of copper or a copper alloy, a primer layer provided on one surface thereof, and an adhesive material layer formed on the primer layer. A grave problem with the method using a coating material, however, is that the coating material has a service life of as short as one year, since even when applied in a thick layer, it is likely to peel away; there is needed troublesome maintenance work in which the coating material must be renewed per year. The marine organism deposit-inhibiting member disclosed in JP-A-60-209505, on the other hand, is found to be less than satisfactory in terms of corrosion resistance and antifouling effect, because of the use copper of a copper-nickel (Cu-Ni) alloy. Our years of study have now revealed that the application of a beryllium-copper alloy to an offshore structure achieves a much-more excellent antifouling effect. The reason would be that beryllium and copper ions interact synergistically, producing a great effect on inhibiting oceanic organisms from having access to the offshore structure and preventing their propagation. In other words, we have now found that the beryllium-copper alloy has a combined effect both on inhibiting marine deposits and on the continued liberation of copper ions. A main object of the invention is to provide a method for the lining of a metal pipe member with an organism deposit-inhibition structure, which enables that structure to be easily lined to the metal pipe , excel in the capability to inhibit deposition of organisms and durability, dispense with maintenance work, and offer no toxicity problem. SUMMARY OF THE INVENTION According to the invention, the object mentioned above is achieved by the provision of a method for the lining of a metal pipe member with an organism deposit-inhibition structure , which involves forming an insulator layer on the inner wall surface of said metal pipe member, and bonding a metal gauze made up of a copper alloy to the surface of the insulator layer by drawing out or rolling over the metal gauze. Preferably, the copper alloy has a Be content of 0.2 to 2.8% by weight, and is an alloy selected from the group consisting of Be-Cu, Be-Co-Cu, Be-Co-Si-Cu and Be-Ni-Cu alloys. In a preferred embodiment of the present invention the method for the lining of a metal pipe member with an organism deposit-inhibition structure, involves forming said insulator layer on the inner wall surface of said metal pipe member by a roll-over technique. Preferably, the copper alloy has a Be content of 0.2 to 2.8% by weight, and is an alloy selected from the group consisting of Be-Cu, Be-Co-Cu, Be-Co-Si-Cu and Be-Ni-Cu alloys. BRIEF DESCRIPTION OF THE DRAWINGS The invention will now be explained, more specifically but not exclusively, with reference to the accompanying drawings, in which: Figure 1 is a schematic view of the first embodiment of the lining method according to the invention, Figure 2 is a schematic view showing the second embodiment of the lining method according to the invention, Figure 3 is a schematic representation of what state an oxide film of the beryllium-copper alloy according to the invention is in, Figure 4 is a schematic representation of what state an oxide film of a cupronickel, provided for comparative purposes, is in, Figure 5 is a partly cut-away, perspective view showing the first embodiment of the second aspect of the invention, Figure 6 is a schematic view of the third embodiment of the lining method according to the invention, and Figure 7 is a schematic view showing the pipe member lined with the organism deposit-inhibition structure according to the third embodiment of the invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS The copper alloy used in the invention has a beryllium content ranging from 0.2% by weight to 2.8% by weight, and may be selected from the group consisting of Be-Cu, Be-Co-Cu, Be-Co-Si-Cu and Be-Ni-Cu alloys. Typical compositions of the copper alloy used in the invention are: (1) 0.2 to 1.0% by weight of beryllium, 2.4 to 2.7% by weight of cobalt and the balance being copper and inevitable impurities, (2) 0.2 to 1.0% by weight of beryllium, 1.4 to 2.2% by weight of nickel and the balance being copper and inevitable impurities, (3) 1.0 to 2.0% by weight of beryllium, 0.2 to 0.6% by weight of cobalt and the balance being copper and inevitable impurities, and (4) 1.6 to 2.8% by weight of beryllium, 0.4 to 1.0% by weight of cobalt, 0.2 to 0.35% by weight of silicon and the balance being copper and inevitable impurities. Preferably, the contents of beryllium (Be), cobalt (Co), nickel (Ni) and silicon (Si) selectively incorporated in the copper alloy lie in the respective ranges: Beryllium - 0.2 to 2.8% by weight Cobalt - 0.2 to 2.7% by weight Nickel - 1.4 to 2.2% by weight Silicon - 0.2 to 0.35% by weight Set out below are what purpose the above elements are added for and why the upper and lower limits thereof are set at the above values. Beryllium: 0.2-2.8% by weight Beryllium is used to (1) protect the structure, when immersed in seawater, against contamination by liberating beryllium ions, (2) improve the strength and properties, e.g., corrosion resistance, of the copper alloy, (3) enhance the productivity of the copper alloy as by heat treatment and grain size regulation, and (4) improve the processability and castability of the copper alloy. At below 0.2% by weight the above-described effects (1)-(4) are unachievable. At higher than 2.8% by weight, not only is there some metalleability drop but a cost-effective problem arises as well. Cobalt: 0.2 to 2.7% by weight Cobalt is used to form a fine CoBe compound and disperse it throughout the alloy matrix, thereby improving the mechanical properties and productivity of the copper alloy. At less than 0.2% by weight this effect is not well achievable. At higher than 2.7% by weight, not only is there some material flowability drop but there is little or no improvement in the above-described effect as well. In addition, a cost-effective problem arises. Nickel: 1.4-2.2% by weight Nickel is used to form a fine NiBe compound and disperse it throughout the alloy matrix, thereby improving the mechanical properties and productivity of the copper alloy. At less than 1.4% by weight this effect is not well achievable. At higher than 2.2% by weight, not only is there some material flowability drop but there is little or no improvement in the above-described effect as well. In addition, a cost-effective problem arises. Silicon: 0.2-0.35% by weight Silicon is used to improve the material flowability of the copper alloy. At less than 0.2% by weight this effect is not well achievable. At higher than 0.35% by weight the resulting alloy becomes brittle with a toughness drop. As a result of out years of experimentation and research, it has turned out that the beryllium-copper alloy has a combined effect both on preventing contamination and on the continued liberation of copper ions. Detailed explanation will now be made to the antifouling effect and the continued action on liberating copper ions. (1) Antifouling Effect As well known from literature, the order of ionization tendency among beryllium, copper and nickel is expressed by Be>Ni>Cu In other words, beryllium ions are more likely to be liberated than copper ions, and copper ions are more likely to be liberated than nickel ions. In the case of a beryllium-copper combination, beryllium is first ionized to form a local cell, which has an effect on preventing deposition of oceanic life contaminants due to its current effect, while beryllium ions take on the form of internal oxidation. By this internal oxidation, a BeO film is first formed, as typically shown in FIGURE 3. This BeO film, because of being porous, allows copper ions to be liberated, forming Cu 2 O+BeO on the surface. This liberation of copper ions into seawater produces an antifouling effect. (2) Continued Action on Liberating Copper Ions The above-mentioned effect (1) on preventing contamination makes another contribution to providing a continued liberation of copper ions; that is, the beryllium-copper combination enables the antifouling function to be maintained ceaselessly. While in contact with seawater, the beryllium-copper combination forms on its surface an intimate surface oxide (Cu 2 O), just below which a porous oxide film of BeO is formed, as can be seen from FIGURE 3. Thus, the liberation of copper ions into seawater is maintained, while this film increases in volume by the oxidation. When the volume increase reaches a certain level, the surface oxide film peels away from the porous oxide or BeO layer. This would enable electrochemical action and the liberation of copper ions to be maintained over an extended period of time. The continued action of the beryllium copper on the liberation of copper ions will now be explained with reference to FIGURE 5 that is a graphic representation showing the results of comparison of beryllium copper with cupronickel. When the corrosion (oxidation) product reaches a certain thickness, it peels away from the beryllium copper (BeCu), as can be best seen from FIGURE 5. Then, the beryllium-copper alloy is again exposed on the surface to seawater, and corroded or oxidized for oxide film growth. When this film grows to a certain thickness level, it peels away from the beryllium copper. This process is repeated over and over. The liberation of copper ions, on the other hand, is likely to be reduced with an increase in the thickness of the oxidation product. As the oxidation product peels away, however, the beryllium-copper alloy is again exposed on the surface to seawater, so that there can be an increase in the amount of the copper ions liberated. Thus, the increase and decrease in the amount of the copper ions liberated occur alternately. The beryllium-copper alloy used in the invention enables copper ions to be continuously liberated by the peeling-off of the oxide film. As a result, the amount of contaminants deposited onto the surface of the beryllium copper is little, if any. This is in contrast to the comparative cupronickel (CuNi), as can be seen from FIGURE 4. With the passing of some years, an intimate nickel oxide (NiO 2 ) or copper oxide (CuO 2 ) layer is formed on the surface of the cupronickel, reducing the liberation of copper ions, as can be seen from FIGURE 5. According to the order of ionization tendency (Be>Ni>Cu), this would be due to the fact the nickel (Ni) is preferentially ionized to form a local cell and so an intimate oxide is formed on the surface of the cupronickel, as can be seen from FIGURE 5. As can be seen from FIGURE 6, the thickness of the corrosion product on the cupronickel increases with time in an early stage, but its growth rate decreases as time goes by. With this, there is a decrease in the amount of the copper ions liberated. In addition, the corrosion product is less likely to peel away from the cupronickel that from the beryllium copper. Thus, the quantity of the copper ions liberated remains low, making the antifouling effect slender. It is to be noted that the facts that a beryllium-copper alloy has a remarkable antifouling effect and provides a continued liberation of copper ions have been discovered by us for the first time. Insofar as we are concerned, never until now have such facts been referred to or indicated in literature. It has also been confirmed that not only does a beryllium alloy pose no toxicity problem at all, but its service life in seawater is as long as that of aluminum bronze or white copper. For practical beryllium alloys, various alloys inclusive of JIS 11 ALLOY having a beryllium content of 0.2 to 0.6% by weight and JIS 25 ALLOY having a beryllium content of 1.8 to 2.0% by weight are now available in the art. In view of the antifouling effect, however a beryllium content of at least 1.60% by weight is preferable. At a beryllium content higher than 2.8% by weight, beryllium does no longer form any further solid solution with copper. In other words, the resulting alloy excels in the antifouling effect but undergoes a gradual decrease in metalleability. Referring now to FIGURE 1, there is shown the first embodiment of the invention. This embodies the application of the invention to a seawater-circulation pipe used in a power plant cooling system. As disclosed in FIGURE 1, a resin layer 2 made up of an electrical insulating material is formed on the inner peripheral wall of a cylindrical iron pipe 1 buried in the ground. Then, a metal gauze 5 comprising a copper alloy, for instance, a beryllium-copper alloy is applied on the surface of the resin layer 2. The metal gauze 5 of beryllium copper, that is pre-contracted in a cylindrical form, is extended out on the ground, and then inserted through the underground iron pipe 1, wherein it is spread over the surface of the resin layer 2. It is here noted that the resin layer 2 is pre-coated thereon with an adhesive agent. After this, the metal gauze 5 is drawn out in the direction shown by an arrow in FIGURE 1. Illustrated in FIGURE 2 is the second embodiment of the invention. This embodies the bonding of a metal gauze 6 made up of a beryllium-copper alloy to the inner wall of a pipe member 1 by the roll-over technique. Water is supplied into the pipe member 1 by way of a water-supply vehicle, so that the metal gauze 6 can be gradually inserted through the pipe 1 by the resulting water pressure with the inner side turned outwards. In the instant embodiment, a resin layer 2 is formed on the inner wall surface la of the pipe 1. After the drying of the resin layer 2, the metal gauze 6 is bonded thereto. To this end, preference is given to coating the inner wall of the pipe 1 with, e.g., an adhesive agent. The second embodiment of the invention enables the metal gauze 6 to be well bonded to the inner wall of the pipe. As is the case with the first embodiment of the invention, the organism deposit-inhibition structure including the metal gauze 6 is well resistant to a seawater attack, giving rise to an antifouling effect. A further preferred embodiment of the invention will now be explained with reference to FIGURE 6. This embodies the application of the invention to a seawater-circulation pipe used in a power plant cooling system. As disclosed in FIGURE 6, a thermosetting resin layer 22 made up of an electrical insulating material is formed on the inner wall periphery of a cylindrical iron pipe 21 buried in the ground. The electrical insulating resin layer 22 is provided to prevent electrolytic corrosion. The resin layer 22 is formed by the roll-over technique. To be more specific, water is supplied into the liner (resin layer) 22 impregnated with thermosetting resin by way of a water-supply vehicle 26, so that the liner 22 can be gradually inserted through the iron pipe 21 by the resulting water pressure with the outer side turned inwards. Then, a hot water pipe is connected with the trailing end of the liner 22 to supply hot water into the liner 22, so that the resin forming the liner 22 can be heated and set into a completely set, firm pipe member. After the liner 22 is completely solidified, the warm water in the liner 22 is cooled and drained out by means of a pump, not shown. Following the drainage, the hot water hose is removed to give a clear finish to the section of the liner 22. Then, a beryllium-copper alloy layer 25 is formed on the inner wall surface of the liner 22 according to the present invention as described above, to give a metal pipe member as shown in FIGURE 7. The beryllium-copper alloy layer 25, for instance, may be applied to the inner wall surface of the liner 22 in the form of a rectangular or spiral thin sheet form, or may alternatively be applied thereto as by thermal spraying. However, it is to be understood that the beryllium-copper alloy layer 25 may otherwise be formed. The third embodiment of the invention enables the resin layer 22 to be well bonded to the inner wall of the pipe. As is the case with the first embodiment of the invention, the organism deposit-inhibition structure according to the third embodiment is well resistant to a seawater attack, giving rise to some considerable antifouling effect. With the lining methods according to the invention, the metal gauze made up of a copper alloy can be applied to an application surface in a relatively simple manner. The organism deposit-inhibition structure lined according to this method excels in corrosion resistance, can be maintained in less troublesome operation, and can effectively inhibit deposition of marine organisms without offering any toxicity problem. The copper alloy bonded to an application surface by these lining methods, as already mentioned, has some remarkable effect on inhibiting marine organisms from having access to part of offshore or marine structures, and is equivalent in durability to aluminum bronze or white copper. The invention provides a method for the lining of a metal pipe member with an organism deposit-inhibition structure, which enables that structure to be easily lined to the metal pipe member, excel in the capability to inhibit deposition of organisms and durability, dispense with maintenance work, and offer no toxicity problem. A resin layer made up of an electrical insulating material is bonded to the inner wall periphery of a cylindrical pipe member. A metal gauze of a copper alloy is applied onto the surface of the resin layer. The metal gauze is either unfolded and drawn out or rolled over with the inner side turned outwards for its application to the surface of the resin layer. The copper alloy has a Be content of 0.2 to 2.8% by weight, and is selected from, e.g., Be-Cu, Be-Co-Cu, Be-Co-Si-Cu and Be-Ni-Cu alloys.

Claims: A method of lining a metal pipe member with an organism deposit-inhibition structure, which involves forming an insulator layer nn the inner wall surface of a metal pipe member, and bonding a metal gauze made up of a copper alloy to the surface of the insulator layer while the gauze is drawn out. A method of lining a metal pipe member with an organism deposit-inhibition structure, which involves forming an insulator layer on the inner wall surface of a metal pipe member, and bonding a metal gauze made up of a copper alloy to the surface of the insulator layer by a roll-over technique. A method according to claim 1 or 2, wherein said insulator layer on the inner wall surface of a metal member is formed by a roll-over technique. A method according to any of the preceding claims, wherein the copper alloy has a beryllium content of 0.2 to 2.8 % by weight, and is an alloy selected from the group consisting of Be-Cu, Be-Co-Cu, Be-Co-Si-Cu and Be-Ni-Cu alloys. A method according to any of the preceding claims, wherein the insulator layer is made up of a resin.

Inventors: INOUE SHUNJI, INOUE, SHUNJI
Applicants: NGK INSULATORS LTD, NGK INSULATORS, LTD.
Application year: 1993
Main classification: F16L58
IPC codes: F16L58