AROMATIC POLYAMIDE PULP BY MEANS OF CONTINUOUS TRANSFERABLE POLYMERIZATION-ORIENTATION METHOD AND A PROCESS FOR PREPARATION THEREOF

Abstract: A process for the preparation of aromatic polyamide pulp having both excellent physical properties and a high degree of polymerization by continuous polymerization and orientation by using of mixed solutions. The solutions are prepared by reacting diamine with aromatic diacid dichloride in an amide and/or urea-based polymerization solvent containing inorganic salts, or a mixture of inorganic salts and a Lewis acid compound. The process can be practised by polymerization-orientation apparatus located on the continuous transferable polymerization-orientation means comprised of a belt and one or more stirring bars.

Description: AROMATIC POLYAKIDE PULP BY MEANS OF CONTINUOUS TRANSFERABLE POLYMER I ZAT I ON-OR I ENTAT I ON METHOD AND A PROCESS FOR PREPARATION THEREOF TECHNICAL FIELD: The present invention relates to a process for preparing aromatic polyamide pulp. More particulary, the invention relates to a process for the preparation of polyamide pulp having both excellent physical properties and a high degree of polymerization wherein an aromatic diamine is reacted with aromatic diacid dichloride in an amide and/or urea-based polymerization solvent containing inorganic salts, or a mixture of inorganic salts and a Lewis acid compound. BACKGROUND ART: U.S. Patent No. 4,511,623 discloses a process for preparing an aromatic polyamide using solvent mixture of comprising inorganic salts wherein a tertiary amine is added into the amide solvent system. According to this method, polyamide fibers are prepared by adding tertiary amines prior to polymerization and applying a high mechnical shear rate at the moment gelation is achieved, thus rapidly increasing the rate of polymerization and producing a high degree of orientation and a high degree of polymerization. But, because U.S. 4,511,623 adds the amide solvent and excess tertiary amines simultaneously, and adds the diacid dichloride all at once, the viscosity of the reaction mixture suddenly increases whi le polymerization is occurring. Accordingly, polymerization is rapidly termi nated(wi th in 10 seconds) and control of the process becomes very difficult. In fact, it is impossible to continuously produce fibers, particularly fibers having a high degree of polymerization which can take 5 hours. In order to overcome the problems of the prior art the present inventors discovered a process for producing pulp comprising extruding a liquid crystall ine pre-polymer(LCP) through an orientation unit, spraying, and contact with a tertiary amine solvent system(e.g., Korean published patent 90-4911). However, because gelation of polymer solution in this process is initiated by the wall surface of the orientation unit the orientation unit becomes clogged, and control of the process becomes difficult.' USP No. 5,106,560 discloses a process for the preparation of pulp by providing a polymerization solution of diacid dichloride, di¬ amine and inorganic salts in an amide solvent system, followed by pouring the solution on a inclined support to provide orientation by means of gravity-induced shear forces. However, by using natural gravity molecular orientation it is impossible to produce pulp having a high degree of orientation. USP Serial No. 07/87,565 (filed April 28, 1992 by the present inventors) discloses a method wherein an anisotropic polymerizing solution is continuously ejected into container, where it remains to mature. Unfortunately, this method has the same drawback as USP No. 5,106,560 which provides orientation by means of gravity-induced shear forces in that a relatively low degree of orientation is achieved. When an anisotropic polymerization solution having low inherent viscosity is ejected according to USP Serial No. 07/87,565, the pro¬ perties of the final product are poor, and it takes approximately 0.5 ~5 hrs to increase the inherent viscosity and degree of orientation of the polymerizing solution. Similarly, the degree of molecular orientation obtained by means of gravity shear is lower than that obtained by means of stirring, which results in decreased fibril growth in the final pulp and an increase in the time required for growth of fibri ls having acceptable specific surface areas due to the low degree of orientation. Further, the properties of final product (e.g., as friction materials or gaskets) which are made from such a f iπal pulp are poor . Generally, in the case of friction materials containing fibers, the friction effect appl ied to a matrix is increased with an increase in the specific surface area of the fiber whi le the adhesion effect increases as the length of pulp increases; these behaviors are considered to be mutually compromising factors, and lead to the use of powders which have high friction efficiencies due to a high surface area but provide low material reinforcement. Therefore, when the degree of orientation of the molecular chain is high, the specific surface area can be increased by the formation of fibri ls, and the pulp has enough its length to reveal high adhesion effect. But if the degree of orientation is low, the length of pulp is not sufficient to increase the adhesion effect for final materials, whi le the specific surface area is increased due to the powder form. DISCLOSURE OF INVENTION It is an object of the present invention to provide an aromatic polyamide pulp wherein the aforesaid problems of prior art are avoided . It is also an object of the present invention to provide aromatic polyamide pulp by an easy, stable and cheap process without using expensive tertiary amines and which avoids process line solidification problems due to gelation. Another object of the invention is to continuously provide a high molecular weight aromatic polyamide pulp having excellent microfibril growth and sufficient length to be utilized as reinforcement materials. To achieve the aforesaid objects, the present invention provides a process for the preparation of aromatic polyamide pulps having repeating units represented by the following formula (A). H H O O I I II II N -R . -N -C -R . - C ( A ) wherein R , , R 2 are selected from the group consisting of the following aromatic groups, O X is H, Cl, Br, -C-NH 2 , or alkyl or alkoxy group of from 1 to 4 O O C H carbon atoms, Y is -CH z -, -C— , - S — , - O - , or -C- II I O C H 3 Other and further objects, features and advantages of the invention will appear more fully in the following description. BRIEF DESCRIPTION OF DRAWINGS Fig. 1 illustrates d iagrammat ica I ly a preferred process in accordance with the present invention. Fig. 2(A) is a front view of Fig. 1 Fig. 2(B) is a plan view of the apparatus of Fig. 1 Fig. 3 is a front view of the belt part of Fig. 1 Fig. 4 and Fig. 5 represent depictions of ejector of raw material into mixer and a step of the first and second feeding. (A) air layer (B) aromatic diamine solution (C) The first aromatic diacid solution (D) The first mixed solution' (E) The second aromatic diacid solution BEST MODE FOR CARRING OUT THE INVENTIONS In the present invention, aromatic polyamide pulp is prepared by the following process; (a) providing a polymerization solvent by adding one or more inorganic salts into amide-based or urea-based organic solvent system or into a mixture of amide-based and urea-based organic solvent system; (b) preparing a first solution by dissolving one or more aromatic diamines in said polymerization solvent, and then adding 20~ 50 wtK of a total 100 wtX amount of one or more aromatic diacid dichlorides which will react with the one or more aromatic diamines in equivalent moles; (c) adding said first solution and the remainder 50~80 wtX of the one or more aromatic diacid dichloride to a continuous mixer simultaneously with mixing, and then ejecting said mixed solution onto a means for continuous transferable polymerization-orientation; (d) polymerizing and orienting said mixed solution obtained in step (c) by polymerization orientation means located on the continuous transferable polymerization-orientation means; (e) maintaining and maturing the polymerized and oriented mixed solution obtained in (d) at a predetermined temperature for a predeter¬ mined tine in the continuous transferable polymerization-orientation system; (f) precipitating the material obtained in (e) above into a pre¬ cipitating solution, and then pulverizing and drying the precipitated material in a pulping means. The present invention is explained in more detail as follows: 1) Preparation of the polymerization solvent In the present invention, amide-based or an urea-based organic solvent system, or mixture thereof, are used as the polymerization solvent. Any wt% mixture may be used. Preferred amide-based or urea-based organic solvents used in the invention include, for example, N-methyl-2-pyrrol idinone(NMP) , N,N- dimethyl aceta ide(DMAc) , hexamethyI phosphoamide(HMPA) , N,N-d i ethy I- formamide(DMF) , N,N,N ' ,N ' -tetramethylurea (TMU) or combinations thereof. One or more inorganic salts may be added to the above organic solvent system in order to increase the solubility of the eventual polymer. Preferred inorganic salts include metal halides or alkal i earth metal halide salts such as CaCI t , LiCI, NaCI , KCI, LiBr, KBr. A single salt or a mixture of inorganic salts may be added. The amount of inorganic salts added to the solvent is preferably less than 12 wt% based on the total weight of polymerization solvent. When the amσunt of inorganic salts is more than 12 wtX, it is not economical becuase further desired effects are not achieved. A small amount of one or more Lewis acids may be added to the polymerization solvents in addition to the inorganic salt(s) in order to further increase the solubility of the polymer. Preferred Lewis acid compounds are selected from the group consisting of compounds of halogen atoms and transition metals, and compounds of halogen atoms and Group IA, IVA, VA, and VIA atoms of the periodic table, including BF , , BCI 3 , AICI , , MgCI , , FeCI 2 , FeCI , , ZnCI , , SbCI , and HgCI t . The amount of Lewis acid added is preferably from o.1 to 5 wtX on the basis of the total weight of polymerization solvent. When the amount of Lewis acid is less than 0.1 wtS, the increase in the solubility of the final polymer and its molecular weight is no more than that obtained with the simple addition of inorganic salts. When the amount of Lewis acid is more than 5X, while the solubility and molecular weight is increased, it is not economical. According to the present invention, when mixtures of inorganic salts are used with Lewis acids, the inherent viscosity of the solu¬ tion is increased due to an increase in solubility as compared with the case of using only inorganic salt(s). 2) Preparation of the first solution. After an aromatic diamine solution is prepared by dissolving one or more aromatic diamines in the above-described polymerization solvent, the aromatic diamine solution is transferred to a mixer set at a predetermined temperature using a quantitative pump and tem- perature controller, and simultaneously 20 to 50 wtX of a total 100wtS of one or more aromatic diamine in equivalent moles, is added thereto mixed, and reacted. The process of adding the aromatic diacid dichloride(s) is -preferably carried out at a temperature of from 0 to 30°c The above first mixed soI ut ion(solvent , polyamide and some diacid dichloride) and remainder 50 to 80 wtK of aromatic diacid dich lor ide(s) are then simultaneously added to a continuous mixer using a pump and a temperature control ler and mixed to provide a second mixed solution, and then the mixture is ejected onto means for continuous transferable polymerization-orientation, where it is stirrred and polymerized. In the above process, it is possible to add all the aromatic diacid dichloride at once, but because mixing is not achieved uni¬ formly due to an abrupt reaction and because side reactions have an effect on the properties of the final product, it is preferable to add it in two stages as above in order to obtain a uniform mixture. In order to obtain a uniform mixture in a short time, it is preferable to add the reactants together in same direction (paral lel direction) by using an ejector l ike that represented in Fig. 4 and Fig. 5 when the first mixed solution and the remainder of aromatic diacid dichloride are added together and/or to the continuous mixer. General ly it takes approximately 1~30 sec to mix the above reactants in a continuous mixer. Therefore, the present invention does not require a special polymerization reactor as prior art methods do to make possible the production of large quantities. 3) Polymerization, orientation and maturing of the mixed sol ut ion The second mixed solution is ejected onto means for continuous transferable polymerization-orientation at a predetermined temperature, and the solution is stirred, optional ly continuously, using polymeri¬ zation-orientation means to increase the degree of polymerization and provide orientation (in the rotating direction) . The average shear rate of the polymerization-orientation means is preferably more than 10/sec. Referring now to the drawings, a continuous transferable polymeri¬ zation-orientation system in accordance with the present invention is il lustrated in Fig. 1 to Fig. 3. The polymerization-orientation apparatus (circled) of the con¬ tinuous transferable polymerization-orientation system of Fig. 1 can be moved from front to rear, and the rpm of all driving motors (1) can be controlled variably. The polymerization-orientation apparatus is fixed at a predetermined place on the system while belt (4) is moving at low speed to polymerize and provide orientation. A guide (8) may be attached to both edges (6) of the belt to prevent the polymer solution from flowing to the side (5) of the belt and guide (7) may be located on the back edge of the belt to prevent the ejected polymer solution from flowing in the opposite direction of the belt progress direction. Polymerization and orientation by stirring in the continuous transferable polymerization-orientation system is achieved within the turning radius of the rotating plate (2) of polymerization orientation apparatus. More than one polymerization-orientation stirring bar (3) can be used, and is assembled so that attachment and detachment is easy. Further, it is possible to use two or more polymerization- orientation apparatuses to polymerize and orient. The obtained polymer, which is polymerized and oriented by stirring, is maintained on the continuous transferable polymerization- orientation system (e.g., on the belt) and matured at a temperature of from 25 to 100°c , for preferably 10 to 60 mins to increase the in¬ herent viscosity and the degree of orientation of the polymer. When the maturing temperature is less than 25°c, the time required for maturing is extended and when it is more than 100°C, the inherent vis ¬ cosity of the final pulp is decreased. The concentration of polymer is preferably about 3 to 15K by weight of the polymerizing solvent. When the concentration of polymer is less than 3X by weight, it is not economical due to the low concentration although it is possible to produce a pulp having high inherent viscosity, and when the concentration of polymer exceeds 15K by weight, solubility is decreased and it is difficult to prepare a pulp having a high inherent viscosity. 4) Preparation of the pulp ' Matured polymer is precipitated into a precipitating solution and then added to pulping means (10), pulverized and dried to prepare polyamide pulp. The precipitating solution of the present invention is preferably water or a basic aqueous solution, or a mixture of one of the above precipitating solutions and the polymerization solvent. A basic aqueous solution is used in order to remove the HCI gas generated in the polymerization reaction and to neutralize the system to prevent the inherent viscosity of polymer from decreasing due to the presence of acid and to prevent the apparatus from corroding. The object of using the mixture of precipitating solution and polymerization solvent is to control the extraction rate of polymerization solvent to reduce the time required for pulping and to promote microfibrii growth. Preferred basic aqueous solutions are aqueous solutions selected from the group consisting of NaOH, KOH, Na z CO , ,K 2 CO , , NaHCO , ,Ca(0H) 2 , and CaO. The concentration of these aqueous solutions is preferred to be from 0.1 to 20K by weight in order to obtain neutralization and increased viscosity. When using a mixed precipitating solution, the amount of the polymerization solvent is preferably less than 50K by weight of the total precipitating solvent. When the amount of the polymerization solvent is more than 50K by weight, the extraction rate of the solvent is decreased and provides a bad pulp shape. Any conventional pulping machine can be used as the pulping means of the present invention. According to the above method, an aromatic polyamide pulp having repeating units represented by formula (A) can be prepared : H H O O I I II II N-R , -N -C-R z - C - ( A ) wherein R, , and R 2 are selected from the group consisting of the following aromatic groups. O II X is H, Cl, Br, -C-NH 2 , I or alkyl or alkoxy group of from 1 to 4 O O C H 3 II I! i carbon atoms, Y is -CH 2 -, -C— , -S— , - O - , or -C- and II I O C H 3 where R , is the aromatic group of the aromatic diamine, and R 2 is the aromatic group of the aromatic diacid dichloride. The inherent viscosity (I .V.) of the pulp prepared by the presnet invention is preferably more than 3.0 g/ M and the Canadian Standard Freeness is preferably within the range of 650 to 400m£, and the length distribution as measured by BAUER-McNETT classifier is preferably 14 mesh or more is less than 30K, 28 mesh or more is more than 30K, 48 mesh or more is more than 60K, 100 mesh or more is more than 70K, 150 mesh or less is less than 25%, where the screen mesh sizes are of the Tyler series and where the Canadian Standard Freeness and length distribution were measured by TAPPI T227 om-85 and TAPPI 233 om-82, respectively. One of the main effects of the present invention is to increase the degree of polymerization and orientation in a short amount of time by utilization of a polymerization-orientation apparatus in a con¬ tinuous transferable polymerization-orientation system without using expensive and harmful tertiary amines. In conventional methods, it is impossible to orient continuoulsy a high viscosity polymer solution because gelation occurs due to abrupt reaction in the reactor, and the orientation apparatus is clogged by gelation. The present invention solves the problem of gelation on a process line because polymerization and orientation is carried out in open means such as on a belt without using a closed system such as a poly¬ merization tank or a polymerization reactor l ike conventional poly¬ merization and orientation apparatuses. Further, the present invention can control the polymerization temperature while reducing the energy consumption which is essential in the prior art to cool the polymerization reactor to low temperature due to the exothermic reaction in conventional methods, and can orient high viscosity solutions easi ly and continuously. One reason the present process is able to orient high viscosity solutions is that it is possible to maintain the effect of molecular orientation by stirring if the stirring is continued unti l the polymer is gelled. If molecular orientation is achieved by shear force, and then the shear force is removed before gelling, molecular orientation is lost and ex- tremely low viscosity is obtained. Because in the present invention, orientation is continued unti l the polymer is gelled, the polymer does not return to the inordered state and obtains maximum orientation. With the present invention, it is possible to reduce the time required for pulping due to the maximum orientation obtained and pro- duce high micro-f ibr i I I ated aromatic polyamide pulp cheaply and cont inuously . This invention is illustrated by the following Examples, but should not construed to be limited thereto. The inherent viscosity (I .V.) of the pulp prepared invention is calculated by following equation. I .V . (g/d β ) = In rβt > c Wherein C is the concentration of polymer solution (0.5g of poly¬ mer is dissolved in lOOmi of 95~98K cone, sulfuric acid), and relative viscosity r) i is the ratio of flowing time measured by cap- iliary viscometer using 95~98% cone, sulfuric acid as solvent. EXAMPLE 1 After the temperature of a reactor in which 700kg N-methyl-2- pyrrol idinone was added was controlled to 70°c, 56 of CaCI 2 was added thereto, stirred and completely dissolved. To the above polymerization solvent was added 29.97kg of p- phenylene diamine, stirred and dissolved to prepare the solution of aromat ic diami ne . The above amine solution was added at the rate of 785.97 g/min using a quantitative pump to a mixer controlled at a temperature of 10°c using a temperature control ler, and, simultaneously, melted terephthaloyI chloride was added thereto at the rate of 19.69 g/min and mixed and reacted to prepare a first mixed solution. To a continuous mixer, the first mixed solution and more melted terephthaloyI chloride was added at rates of 805.66 g/min and 36.57 g/min, respectively. After the resulting solution was stirred in the continuous mixer for 10 sec, the mixed solution was fed into a continuous transferable polymerization-orientation system through an opening at a temperature of 50°c, and stirred and mixed at the shear rate of 20/sec to poly¬ merize and orient until gelation was completed, and then maintained there for 30 mins and matured. After the above sol idified polymer was isolated from the continu¬ ous transferable polymerization-orientation system, it was precipitated into water and fed to a pulping machine, pulverized and dried to prepare a pulp. The inherent viscosity of the pulp was 4.5, and Canadian Standard Freeness was 641 ~£ and the length distribution was, 14 mesh 29K, 28 mesh 22X, 48 mesh 36K, 100 mesh 5K and 150 mesh less than 8X. EXAMPLE 2~9 The same procedure was carried out as described in Example 1 with the amount of components, conditions and properties provided in Table 1. [ TABEL 1 ] ^ NMP : N-methyl-2-pyrol I idone, TPC : Terephtha loy I chloride, to be continued to be cont i nued %, P/0 system polymer izat ion-or ientat ion system polyn . sol , polymerization solvent be cont inued COMPARATIVE EXAMPLE 1 After the temperature of a reactor in which 700 kj; N-methyl-2- pyrrol idinone(NMP) was added was controlled to 70°c, 56 kg of CaCI z was added, stirred and completely dissolved. To the above polymerization solvent was added 29.97kg of p-phenylene diamine, stirred and dissolved to prepare the solution of aromatic diamine. The above amine solution was added at the rate of 785.97 g/min using quantitative pump to the mixer and controlled at the temper ¬ ature of 10°c using temperature control ler, and simultaneously melted terephthaloyI chloride was added thereto at the rate of 19.69 g/min and mixed and reacted to prepare the first mixed solution. To a continuous mixer, the first mixed solution and more melted terephthaloyI chloride was added at the rates of 805.66 g/min and 36.57 g/min, respectively and mixed for 10 sec. The temperature of the polymer inside the continuous mixer was controlled not to exceed 60°c . The above mixed solution was continuously ejected onto a moving belt provided at the bottom of opening, and maintained thereon for 50 mins and matured. The above solidified polymer was precipitated into 30X(NMP) solu- tion of polymerization solvent and fed to the same pulping machine used in Examples 1~9, pulverized and dried to prepare a pulp as powder form. The inherent viscosity of the pulp was 1.8. ■ COMPARATIVE EXAMPLE 2 » After the temperature of reactor in which 700kg N-methyl-2- pyrrol idinone was added was controlled at 70°c, 56 g of CaCI t was added, stirred and completely dissolved. To the above polymerization solvent was added 29.97kg of p-phenylene diamine, stirred and dissolved to prepare the solution of aromatic diamine. The above amine solution was added at a rate of 785.97 g/min using a quantitative pump to a mixer and controlled at the temperature of 10°c using temperature control, and simultaneously melted tere- phthaloyl chloride was added thereto at a rate of 19.69 g/min and reacted to prepare a first mixed solution. The first mixed solution and more melted terephtha loyI chloride were added at the rates of 805.66 g/min and 36.57 g/min, respectively on a moving belt, at a temperature of 60°c, and maintained there for 50 mins and matured. The above mixed solution on the belt was not solidified and was precipitated into 30X NMP solution of polymerization solvent and fed to the pulping machine of Example 1, pulverized and dried. The inherent viscosity of the pulp as powder form was 0.3. < COMPARATIVE EXAMPLE 3 » After the temperature of reactor in which 600kg N-methyl-2- pyrrol idi none was added was controlled at 70°c, 50kg of CaCI 2 was added, stirred and completely dissolved. To the above polymerization solvent was added 29.97kg of p-phenylene diamine, stirred and dissolved to prepare the solution of aromatic diamine. The above solution was added at a rate of 679.97 g/min using a quantitative pump to a mixer and controlled at a temperature of 10°c using temperature control , and simultaneously melted terephtha loyI chloride was added thereto at the rate of 14.07 g/min and mixed and reacted to prepare the first mixed solution. To the continuous mixer, the first mixed solution and melted terephthaloyl chloride was added at rates of 694.04 g/min and 42.19 g/min, respectively and mixed for 10 sec. The temperature of the polymer inside the continuous mixer was controlled not to exceed 60°c . The above mixed solution was continuously ejected on a moving belt provided at the bottom of opening, and then maintained there for 50 mins and matured. The above sol idified polymer was precipitated into 30X NMP solution of polymerization solvent and fed to the pulping apparatus of Example 1, pulverized and dried to prepare a pulp as powder form. The inherent viscosity of the pulp was 1.6. Obviously, numerous modifications and variations of the present invention are possible in l ight of the above teachings. It is there¬ fore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifical ly described herein.

Claims: WHAT I S CLA I MED I S ; 1 . A process for the preparation of aromatic polyamide pulp, which process comprises the steps of: (a) preparing a polymerization solvent by providing one or more amide-containing or urea-containing organic solvents, or a mixture of said solvents, optional ly comprising one or more inorganic salts; (b) preparing a first mixture by dissolving one or more aromatic diamines in said polymerization solvent, and mixing therewith 20~50 wtK of one or more aromatic diacid dichlorides, and reacting said one or more diacid dichlorides with said aromatic diamines; (c) adding said first mixture and the remainder 50~80 wtX of aromatic diacid dichloride to a continuous mixer simultaneously with mixing, and then ejecting said mixed solution onto a continuous trans¬ ferable polymerization-orientation means; (d) polymerizing and orienting said mixed solution obtained in (c) by polymerization orientation means located on the continuous transferable polymerization-orientation means; (e) maintaining and maturing said polymerized and oriented mixed solution obtained in (d) in the continuous transferable polymerization- orientation means; (f) precipitating the material obtained in (e) into a precipitat¬ ing solution, and then pulverizing and drying the precipitate in pulping means; (g) obtaining an aromatic polyamide pulp having reapeating units represented by the following for ular (A) : ( A ) wherein R , , R : are selected from the group consisting of the following aromatic groups, X is H, Cl, Br, -C-NH 2 , or alkyl or alkoxy group of from 1 to 4 O O C H , II II I carbon atoms, Y is -CH 2 -, -C— , -S— , — O - , or -C— II I O C H 3 2. The process according to claim 1, wherein said organic solvents are selected from the group consisting of N-methyl-2-pyrrol i- dinone, N,N-dimethylaceta ide, hexamethyIphosphoamide, N,N-dimethyI- forma ide, N,N,N ' ,N ' -tetramethylurea, and mixtures thereof. 3. The process according to claim 1, wherein said inorganic salts are selected from the group consisting of CaCI 2 ,LiCI, NaCI,KCI, LiBr, KBr, and mixtures thereof. 4. The process according to claim 3, wherein the amount of said inorganic salts is 0.1 to 12X by weight of said polymerization solvent . 5. The process according to claim 1, where one or more Lewis acid compounds is added to said polymerization solvent. 6 . The process according to claim 5, wherein said one or more Lewis acid compounds is selected from the group consisting of BF , , BCI 3 , AICI 3 , MgCI , , FeCI 2 , FeCI 3 , ZnCI t , SbCI 2 , HgCI 2 , and mixture thereof. 7 . The process according to claim 5, wherein the amount of said one or more Lewis acid compounds is 0.5 to 5X by weight of said polymerization solvent. 8. The process according to claim 1, wherein said aromatic diamine/poiymer izat ion solvent solution and said 20~50wtX of said aro¬ matic diacid dichloride in step (b), and said first mixture and said remainder aromatic diacid dichloride of step (c) are mixed in paral lel di rect ion . 9. The process according to claim 8, wherein said mixing is accomplished with the ejector. 1 0 . The process according to claim 1, wherein said continuous transferable polymerization-orientation means comprises a belt and one or more stirring bars. 1 1 . The process according to claim 10, wherein said one or more stirring bars rotate around an axis perpendicular to an upper surface of the belt. 1 2. The process according to claim 10, comprising plural st i rr ing bars . 1 3 . The process according to claim 10, wherein a guide is provided to prevent said solution ejected from flowing in a direction opposite to the progress of the belt. 1 4 . The process according to claim 10, wherein guides are provided at both'edges of said belt to prevent said solution from flowing to the side of said belt. 1 5. The process according to claim 10, wherein said one or more stirring bars are provided at an upper part of said belt. 1 6 . The process according to claim 1, wherein in step (c) said solution is ejected on the continuous transferable polymerization- orientation means by free fall . 1 7 . The process according to claim 1, wherein the concentration of said polymer is 3 to 15K by weight of said total polymerization solut ion . 1 8. The process according to claim 1, wherein polymerization and orientation is carried out unti l the polymer is gelled. 1 9. The process according to claim 1, wherein in step (e) poly¬ mer solution is matured by maintaining said solution at a temperature of 25 to 100°c, for 10 to 60 mins. 2 0. The process acoording to claim 1, wherein said precipita¬ ting solution is selected from the group consisting of water, basic aqueous solution, and mixtures of one water or a basic aqueous solution with said polymerization solvent. 2 1 . The process according to claim 20, wherein said basic aqueous solution is selected from the group consisting of aqueous solutions of NaOH, KOH, Na 2 CO 3 , K 2 CO , , NaHCO 2 , Ca(0H) 2 and CaO . 2 2. The process according to claim 21, wherein the concentra¬ tion of said basic aqueous solution is 0.1 to 20 wtK. 2 3. The process according to claim 20, wherein the amount of polymerization solvent in said mixed precipitation solution is less than 50K by weight of said total precipitating solution. 2 4 . The process according to claim 1, wherein said aromatic polyamide is poly(p-phenylene terephtha lamide) . 2 5 . An aromatic polyamide pulp prepared in accordance with the process of claim 1, which has an inherent viscosity of more than 3.0 g/dtf, a Canadian Standard Freeness of less than 650m£ . 2 6. The aromatic polyamide pulp according to claim 25, having a pulp length distribution at 14 mesh or more of less than 30X, at 28 mesh or more of more than 30X, at 48 mesh or more of more than 60X, at 100 mesh or more of more than 70X, at 150 mesh or less of less than 25X. 2 7. The aromatic polyamide pulp according to claim 25 or claim 26, wherein said aromatic polyamide is poly(p-phenyleneterephtha Imide) ,

Inventors: CHOE WON JUN, JI CHANG SEOP, KIM DU HYUN, PARK YOUNG HWAN, RYU SEOCK CHUL, CHOE, WON, JUN, JI, CHANG, SEOP, KIM, DU, HYUN, PARK, YOUNG, HWAN, RYU, SEOCK, CHUL
Applicants: CHOE WON JUN, JI CHANG SEOP, KIM DU HYUN, KOLON INC, PARK YOUNG HWAN, RYU SEOCK CHUL, CHOE, WON, JUN, JI, CHANG, SEOP, KIM, DU, HYUN, KOLON INDUSTRIES, INC., PARK, YOUNG, HWAN, RYU, SEOCK, CHUL
Application year: 1993
Main classification: C08G69
IPC codes: C08G69, D01F6, D21H13