High-flux hollow-fiber membrane with enhanced transport capability and process for making same

Abstract: Semipermeable membranes are disclosed for purifying aqueous biological fluids. The membranes are particularly suitable for purifying extracorporeal blood via hemodialysis. The membranes, preferably configured as hollow fibers, are made from a hydrophilic polymeric material, preferably cellulose acetate. Features of the membranes include an ultrafiltration coefficient (K uF ) of about 15 to about 55 mL/hr/mmHg/m² (thus termed "high-flux" type membranes), a urea mass transfer coefficient (K oV (urea)) of at least 38x10⁻³ cm/min, and a ratio of K oV (urea)/K uF of at least 2.5x10⁻³. Hollow fibers of such membranes suitable for hemodialysis have a lumen diameter of about 175 to about 210 µm and a wall thickness of about 10 to about 35 µm. According to disclosed methods for making the membranes, a melt comprising about 32 to about 40% w/w cellulose acetate, about 5 to about 10% w/w glycerine, and about 50 to about 67% w/w polyethylene glycol is extruded to make hollow fibers; the fibers are cooled, cold-stretched, water-leached, and replasticized using a glycerine solution.

Description: Background of the Invention While semipermeable membranes that are useful for purifying aqueous biological fluids and made according to the prior art have features that are advantageous for certain applications, they nonetheless have certain limitations. Such a semipermeable membrane is for example disclosed in US-A-4 276 173. The present invention seeks to overcome certain drawbacks of prior-art membranes and to provide new features not heretofore available. A discussion of the features and advantages of the present invention is deferred to the following detailed description, which proceeds with reference to the accompanying drawings. Brief Description of the Drawings FIG. 1 is a profile of maltodextrin sieving and rejection behavior of a prior-art low-flux cellulose-acetate membrane, as discussed in Example 4. FIG. 2 shows maltodextrin sieving profiles for two prior-art hemodialysis membranes, as discussed in Example 4. FIG. 3 is a comparative plot of the maltodextrin sieving profile of a prior-art "Polyflux 130" membrane, compared to a membrane according to the present invention, as discussed in Example 4. FIG. 4 shows sieving data for a prior-art "Polyflux 130" membrane as well as a plot of values of the corresponding rejection statistic for the prior-art membrane, as discussed in Example 4. FIG. 5 shows plots of sieving and rejection statistics (for maltodextrin) for the prior-art "F80" membrane, as discussed in Example 4. Detailed Description The present invention provides a semipermeable hollow-fiber membrane according to claim 1 having a novel combination of hydraulic (i.e., water) permeability and diffusive (i.e., solute) permeability. With respect to diffusive permeability, the membranes according to the present invention are permeable to solutes normally present in aqueous biological fluids (such as blood) having molecular weights up to 30,000 daltons and higher. Thus, the membranes provide optimum operating characteristics when used in separation processes or blood purification applications. This invention also encompasses a process for making cellulose acetate fibers having the above-specified characteristics. The invention furthermore provides an extracorporeal blood-treatment device comprising membranes according to the present invention. The fibers according to the present invention comprise hydrophilic cellulose acetate. For use in processing biological fluids, the hydrophilic cellulose acetate also is resistant to thrombogenesis, and is non-toxic. It has been found that cellulosic polymers are particularly well-adapted for such use. In order to form membranes with the requisite hydraulic and diffusive permeability characteristics, the cellulose acetate hydrophilic is liquified (i.e., melted) and combined with a water-miscible solvent for the hydrophilic cellulose acetate and a water-miscible non-solvent for the cellulose acetate hydrophilic. Of course, the solvent and the non-solvent must be liquids at the melt temperature of the hydrophilic cellulose acetate. Also, the solvent and the non-solvent are preferably non-toxic and resistant to thrombogenesis. The resulting mixture is mixed to homogeneity and "melt-spun" (i.e., extruded in a molten condition) through an annular extrusion die. As discussed below, the mixture can be melt-spun twice, once using a die suitable for making solid fibers, then again using an annular die to produce hollow fibers. Spinning twice allows superior control over the composition and characteristics of the hollow fibers. After extrusion, the resulting hollow fibers are rapidly cooled to solidify their constituent materials and leached in heated water to remove the solvent and the non-solvent. In the melt, molecules of the solvent and non-solvent constituents are homogeneously interspersed with molecules of the hydrophilic cellulose acetate. During extrusion and subsequent cooling, the molecules of the hydrophilic cellulose acetate undergo a degree of thermodynamic ordering of themselves relative to the solvent and non-solvent constituents. (This process is termed a "thermally-induced phase separation process," abbreviated "TIPS.") As a result, the molecules of the hydrophilic cellulose acetate become associated with each other during spinning to form a labyrinthine network that, after the solvent and non-solvents are removed by water leaching, is characterized by an extensive and dense network of convoluted voids having an extremely fine mean pore size. These voids extend through the walls of the hollow fibers and provide the routes by which water and solutes pass through the walls. The molecules of the solvent and non-solvent, which originally occupied the voids, are removed by the water-leach step because they are miscible in water and because they do not become covalently bonded to the molecules of the hydrophilic cellulose acetate. For example, and not intended to be limiting, a cellulose acetate hollow fiber according to the present invention is made from a composition comprising a mixture of three constituents. A first constituent is the cellulose acetate polymer which provides the structural aspect of the membrane. A second constituent is glycerine, a non-solvent for cellulose at ambient temperature. A third constituent is polyethylene glycol, a solvent for cellulose at ambient temperature. A preferred mixture for making cellulose acetate membranes consists essentially of about 32 to about 40 percent (w/w) cellulose acetate, about 5 to about 10 percent (w/w) glycerin, and the balance polyethylene glycol having a molecular weight in a range of about 150 to about 600 daltons. A process for making cellulose acetate membranes according to the present invention typically includes a "compounding" step in which the three compounds are mixed to homogeneity at a temperature appropriate to melt cellulose acetate (about 165 to about 180°C). The resulting first "melt" is then extruded through a die to form solid strands. The strands are cooled and pelletized using conventional methods. The composition of the pellets is substantially the same as the composition of the first melt. Fabrication of hollow-fiber membranes from the pellets is performed by first heating the pellets sufficiently to form a second "melt" which is extruded through an annular spinneret. The resulting hollow fibers are immediately cooled by air and leached in a water bath at a temperature of about 80 to about 95°C. The temperature of the second melt while being extruded through the annular spinneret is a key parameter affecting the hydraulic permeability of the resulting membrane. For example, with respect to cellulose acetate, each one degree Celsius increase in spin temperature causes a corresponding decrease in the hydraulic permeability of the hollow fiber by about 17x10 -3 cm 3 /(s.kPa) (2 mL/min/mmHg/m 2 ). Thus, it is possible to "customize" the hydraulic permeability of the hollow fibers by simply controlling the spin temperature. It is also important that the conditions under which the hollow fibers are cooled upon exiting the annular spinneret be maintained substantially constant to ensure uniform fiber characteristics over the length of the fiber produced by the spinneret. These conditions include, but are not necessarily limited to, the temperature of the air used to cool the fiber, the velocity of air movement past the fiber exiting the spinneret, the longitudinal tension applied to the fiber as it exits the spinneret, the rate at which the fiber is cooled relative to the longitudinal velocity of the fiber as it exits the spinneret, and the humidity of the air used to cool the fiber. The longitudinal tension should be sufficient to longitudinally stretch the fiber by no greater than twenty percent. In the water bath, the glycerin and polyethylene glycol constituents of the hollow fibers are leached from the polymeric constituent. After leaching, the hollow fibers are taken up in a wet condition on reels. The wet fibers possess excellent hydraulic and diffusive permeability characteristics with high solute clearances for middle and high molecular weight substances while still exhibiting a manageable ultrafiltration rate for use in hemodialyzers and the like. In the "pores" of the wet fibers water molecules essentially replace the molecules of solvent and non-solvent leached away by the water. Thus, the water molecules contribute a substantial degree of structural integrity to the fibers which would otherwise collapse and thereby lose their desired hydraulic and diffusive permeability characteristics. However, it is impractical to maintain the fibers in such a wet condition for extended periods or to incorporate "wet" fibers into such appliances as hemodialyzers using available methods. Therefore, it is necessary to ultimately replace a substantial portion of the water with a stabilizing substance that is resistant to evaporation under ambient conditions but does not interfere with downstream steps necessary to incorporate the fibers into a useful appliance. Such a water-replacement step is termed "replasticization." For example, wet cellulose acetate fibers are preferably replasticized using a solution of glycerin and water. The wet fibers are unreeled and submerged at about 25°C in an aqueous glycerin solution having a glycerin concentration of about 30 to about 40% w/w. The fibers are subsequently dried using air heated to about 70 to about 80°C. After drying, the cellulose acetate fibers can remain stable for extended periods of time because the "plasticizer" (i.e., glycerin and some water) is in equilibrium with the atmosphere at ambient temperature and humidity. At equilibrium, the concentration of glycerin in the cellulose acetate membrane is about 45 to about 50% w/w and the water content is about 15 to about 18% w/w. Hollow cellulose acetate fibers according to the present invention can be made into hollow-fiber hemodialyzers using methods known in the art. When made into hemodialyzers, such fibers have been shown to have the following specifications: Fiber internal diameter: about 175 to about 210 µm Fiber wall thickness: about 10 to about 35 µm Ultrafiltration coefficient (K UF ) 3.13x10 -2 cm 3 /(s.kPa) to about 1.15x10 -1 cm 3 /(s.kPa) (about 15 to about 55 mL/hr/mmHg/m 2 ) Mass-transfer coefficient for urea (K oV (urea)) 6.33x10 -4 cm/s (about 38x10 -3 cm/min) or higher Ratio of [K oV (urea)]/K UF at least 2.5x10 -3 Example 1 This Example is an investigation of the effects of cellulose acetate concentration and hot water-bath leach temperature on diffusive (K oV ) and hydraulic (K UF ) permeability values of hollow-fiber membranes according to the present invention. Results are shown in Table 1. [Cellulose Acetate] (% w/w) 65°C Leach K oV (Urea) cm/s (cm/min) Bath K UF 75°C Leach K oV (Urea) cm/s (cm/min) Bath K UF 42.8 5.88x10 -4 (35.3x10 -3 ) 0.51 (7.6) 6.28x10 4 (37.7x10 -3 ) 0.68 (10.2) 40.3 5.65x10 -4 (33.9x10 -3 ) 0.60 (9.0) - - 38.3 6.22x10 -4 (37.3x10 -3 ) 0.89 (13.3) 6.93x10 -4 (41.6x10 -3 ) 1.32 (19.8) 38.3 6.13x10 -4 (36.8x10 -3 ) 0.89 (13.3) 7.23x10 -3 (43.4x10 -3 ) 1.23 (18.4) 36.7 6.37x10 -4 (38.2x10 -3 ) 1.21 (18.2) 7.50x10 -4 (45.0x10 -3 ) 1.71 (25.6) 34.6 6.83x10 -4 (41.0x10 -3 ) 1.62 (24.4) 7.82x10 -4 (46.9x10 -3 ) 2.07 (31.1) 32.9 7.11x10 -4 (42.7x10 -3 ) 1.82 (27.4) 7.98x10 -4 (47.9x10 -3 ) 2.41 (36.1) Example 2 This Example illustrates the effect of leach-bath temperature on the diffusive permeability (K oV ) and hydraulic permeability (K UF ) of cellulose acetate hollow fibers having a preferred cellulose acetate content of 34.5% w/w. Result are shown in Table 2. Bath Temp °C K oV (Urea) cm/s (cm/min) K UF cm 3 /s.kPa (mL/hr/mmHg/m 2 ) 75 8.68x10 -4 (52.1x10 -3 ) 1.85 (27.8) 80 8.33x10 -4 (50.0x10 -3 ) 1.96 (29.4) 85 8.27x10 -4 (49.6x10 -3 ) 2.43 (36.4) Example 3 This Example illustrates the effects of compounding temperature and hollow-fiber melt-spin temperature on the diffusive and hydraulic permeability values of hollow fibers comprising 34.5% w/w cellulose acetate after passing through an 85°C leach bath. Results are shown in Table 3. Compounding Temp (°C) Fiber Spin Temp (°C) K oV (Na) cm/s (cm/min) K UF cm 3 /s.kPa (mL/hr/mmHg/m 2 ) 165.6 172.2 7.62x10 -4 (45.7x10 -3 ) 3.74 (56.1) 168.3 175 7.01x10 -4 (45.7x10 -3 ) 3.48 (52.2) 171.1 175 0.85x10 -4 (51x10 -3 ) 2.16 (32.4) 173.8 175 8.27x10 -4 (49.6x10 -3 ) 2.43 (36.5) 176.7 177.2 7.41x10 -4 (44.5x10 -3 ) 1.95 (29.2) Example 4 This Example is an investigation of sieving behavior of hollow-fiber membranes according to the present invention compared with prior-art hollow-fiber membranes. The sieving statistics were determined using maltodextrin solutions. See generally , Feldhoff et al., "Effect of Plasma Proteins on the Sieving Spectra of Hemofilters," Artif. Organs 8 : 186-192 (1984). Cellulose acetate hollow fibers made according to the present invention were bundled and made into hollow-fiber hemodialyzers using conventional procedures. The lumens of the hollow fibers (i.e., the "blood" side of the semi-permeable membrane represented by the fibers) received either a human plasma containing maltodextrin or a saline rinse. The maltodextrin used in this study had a continuous distribution of molecular weights from about 350 daltons (maltose) to greater than 120,000 daltons. Normal dialysate at 37°C as used in hemodialysis was used in the "dialysate" side. Three liters of human plasma recovered from whole blood were heated to 60°C for 30 minutes to destroy dextrinases. Any cryoprecipitate and coagulated proteins produced by heating the plasma in this matter were removed by centrifuging the plasma at 10,000 x g for 30 minutes. Maltodextrin was then added to a concentration of 6% w/w. The temperature of the plasma-maltodextrin solution was maintained at 37°C with slow stirring using a water bath. For saline rinses of the fiber lumens, one liter of normal saline was prepared and likewise maintained at 37°C. Delivery of plasma or normal saline through the lumens, and delivery of dialysate, were accomplished using conventional peristaltic pumps, with tubing lengths from the respective reservoirs to the dialyzer and back being less than one meter each way. The "plasma" pump was adjusted to deliver plasma or saline to the arterial blood port of the dialyzer at 200 mL/min with a slight back pressure on the venous blood port. The "dialysate" pump was coupled to the dialysate port of the dialyzer with the downstream dialysate port plugged. The dialysate pump was run at 30 mL/min. Pressure transducers were connected by tubing and "T" connections to the arterial blood port, the venous blood port, and the upstream dialysate port. All pressure-monitoring components were positioned at the same hydrostatic elevation to avoid pressure differentials. Before being connected as described above, the dialyzers were rinsed, by "cross-membrane" flow, with one liter of normal saline under a hydrostatic pressure of one meter to wash out glycerine and other solutes from the hollow fibers. After connection as previously described, the dialyzers were rinsed with 0.5 L normal saline withdrawn from the 37°C reservoir. After passing through the fibers, the 0.5 L saline was discharged to a drain. The dialyzers were then rinsed for 1,200 seconds with the 0.5 L normal saline remaining in the 37°C reservoir, with the saline being returned to the reservoir after passing through the fibers. The dialyzers were then drained of any saline on the dialysate side to present excessive dilution of the plasma/maltodextrin solution. Flow of the plasma/maltodextrin solution was then started through the fibers, with any liquid appearing at the venous blood port discharged to the drain until the plasma solution appeared at the port. Then, the plasma solution was recirculated to the 37°C reservoir during continuous passage of the solution through the fibers. Such recirculation was continued for 60 minutes. Samples of the plasma and of filtrate through the fibers were taken at 20 minutes and 60 minutes, and analyzed using high-pressure liquid chromatography (HPLC) to determine the concentrations of various molecular-weight species of maltodextrin therein. After 60 minutes, the experiment was stopped and all plasma solution was flushed from the dialyzers. The dialysate sides were emptied to the reservoir to prevent loss of low molecular-weight maltodextrin molecules. Selected results of these experiments are shown in FIGS. 1-5. FIG. 1 is a profile of the maltodextrin sieving and rejection behavior of a "CDAK 4000" dialyzer incorporating a prior-art low-flux cellulose-acetate-based membrane made by Althin CD Medical, Inc., Miami Lakes, Florida. In FIG. 1, the square-shaped points correspond to the ability of the membrane to reject (i.e., prevent passage therethrough of) maltodextrin molecules having particular molecular weights. The diamond-shaped points correspond to the ability of the membrane to sieve (i.e., pass therethrough) maltodextrin molecules. As is known in the art, performance of hemofiltration membranes is typically described in terms of their ultrafiltration rates (mL/min/mmHg/m 2 ) and their sieving properties. A suitable sieving statistic is determined by measuring the concentration of a solute (here, maltodextrin) in liquid on the "blood" side and on the "dialysate" side. The sieving statistic plotted in FIG. 1 is defined by C d /(C b + C d ) , wherein C d = solute concentration on the dialysate side and C b = solute concentration on the blood side. The rejection statistic plotted in FIG. 1 is defined by C b /(C b + C d ) . FIG. 2 shows maltodextrin sieving profiles for two prior-art hemodialysis membranes. The "sieving coefficient" axis (ordinate) represents values of the sieving statistic described above. In FIG. 2, the "polyflux 130" membrane is a hydrophilic polyamide-based high-flux membrane manufactured by Gambro, Lund, Sweden; the "F80" membrane is a polysulfone membrane made by Fresenius. FIG. 3 is a comparative plot of the maltodextrin sieving profiles of the prior-art "Polyflux 130" membrane and an "Altrex B" membrane according to the present invention. FIG. 4 shows, for the prior-art "Polyflux 130" membrane, the sieving data shown in FIGS. 2 and 3. FIG. 4 also shows a plot of values of the corresponding rejection statistic for the "Polyflux 130" membrane. FIG. 5 shows, for the prior-art "F80" membrane, plots of the sieving and rejection statistics (for maltodextrin). Example 5 This Example is an investigation of in vivo clearance data of a cellulose acetate membrane according to the present invention. The data, shown in Table 4, were obtained using conventional methods using a hemodialyzer made with the fibers. K UF In Vivo Clearance (cm/min) K UF Uera Creatinie Uric Acid Phosphate 3.33 (50.0) 182 150 155 147 1.13 (16.9) 233 182 195 184 289 220 223 195

Claims: A cellulose acetate hollow fiber semipermeable membrane having a lumen diameter of 175 to 210 µm and a wall thickness of 10 to 35 µm, wherein the membrane exhibits a combination of: an ultrafiltration coefficient K uF of 3.13×10 -2 cm 3 /(s·kPa) to 1.15×10 -1 cm 3 /(s·kPa) (15 to 55 mL/hr/mmHg/m 2 ), a mass-transfer coefficient for urea K oV (urea) of at least 6.33×10 -4 cm/s (38×10 -3 cm/min), and a ratio of [K oV (urea)]/K uF of at least 2.5×10 -3 . The membrane of claim 1, characterized in that the membrane exhibits a sieving statistic, for maltodextrin having a molecular weight of 15,000 to 20,000 daltons, of at least 0.1. The membrane of claim 2, characterized in that the membrane exhibits a sieving statistic, for maltodextrin having a molecular weight of greater than 20,000 daltons, of less than 0.1. The membrane of claim 1, characterized in that the membrane exhibits a ratio: {[K oV (urea)][S(mw)]}/K uF ≥ 0.17×10 -3 for solutes having a molecular weight from 10,000 to 60,000 daltons, wherein S(mw) is a sieving coefficient of the membrane as a function of the solute molecular weight. The membrane of claim 1, characterized in that the membrane is adapted for use in hemodialyzers. A process for making a hollow-fiber semipermeable membrane adapted for purifying aqueous biological liquids, in which process a molten liquid comprising cellulose acetate, a water-miscible non-solvent for cellulose acetate, and a water-miscible solvent for cellulose acetate is extruded through a spinneret to produce a hot hollow fiber that is cooled and contacted with 70 to 85 °C water so as to leach the non-solvent and solvent from the membrane, wherein the molten liquid comprises 32 to 40 % w/w of cellulose acetate, 5 to 10 % w/w of the non-solvent, and 50-63 % w/w of the solvent, and the membrane has an ultrafiltration coefficient (K uF ) of 15 to 55 mL/hr/mmHg/m 2 . The process of claim 6, characterized in that the hot hollow fiber is stretched longitudinally so as to increase its length by no greater than 20 percent. the process of claim 7, characterized in that the fiber, after stretching, has a lumen diameter of 175 to 210 µm and a wall thickness of 10 to 35 µm. The process of claim 6, characterized in that the hollow fiber, after being contacted with the 70 to 85 °C water, is replasticized. The process of claim 9, characterized in that replasticization comprises contacting the hollow fiber with an aqueous glycerin solution. The process of claim 10, characterized in that, after the fiber is replasticized, water is removed from the fiber so as to confer on the fibers a glycerin concentration of 45 to 50 % w/w and a water concentration of 15 to 18 % w/w when the fibers are at equilibrium with the atmosphere. The process of claim 11, characterized in that water is removed from the fibers by drying the fibers in air at 70 to 80 °C. The process of claim 6, characterized in that the molten liquid has a temperature greater than the melting temperature of cellulose acetate. The process of claim 13, characterized in that the molten liquid has a temperature of 165 to 180 °C. The process of claim 6, characterized in that the non-solvent is glycerin and the solvent is polyethylene glycol having a molecular weight of 150 to 600 daltons. An extracorporeal blood-treatment device comprising membranes as claimed in claim 1. The device of claim 16, characterized in that the device is a hemodialyzer.

Inventors: ALTHIN ANDERS, ELSEN RAYMOND, FERNANDEZ BEN, RUZIUS KEES, SILVA LALITH, WASHINGTON GEORGE, ALTHIN, ANDERS, ELSEN, RAYMOND, FERNANDEZ, BEN, RUZIUS, KEES, SILVA, LALITH, WASHINGTON, GEORGE
Applicants: ALTHIN MEDICAL INC, ALTHIN MEDICAL INC.
Application year: 1993
Main classification: B01D69
IPC codes: B01D69, B01D39, B01D63, B01D65, A61M1, B01D67, C08B30, B01D71