Novel copolymer, method for production thereof, and coloring-discoloring material using the polymer

Abstract: Disclosed is a copolymer represented by the following general formula (1): wherein R₁ represents a group based on a polymer or a copolymer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced, R₂ and R₃ represent independently a hydrogen atom or an alkyl group having 1 to 1,000 carbon atoms, A represents a group possessing polarity and exhibiting affinity for ions, and L and M are independently an integer of at least 1, providing that the total degree of polymerization is an integer in the range of 10 to 12,000. The copolymer may be a block copolymer or a random copolymer. This copolymer exhibits electrochromism and, therefore, is useful as a coloring-discoloring material which induces coloration or discoloration on being oxidized or reduced, particularly as an electrochromic substance used in an electrochromic display device.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention: This invention relates to novel copolymers exhibiting electrochromism and methods for the production thereof. This invention further relates to a coloring-discoloring material resorting to electrochromism, which is particularly usable in an electrochromic display device. 2. Description of the Prior Art: The term "electrochromism" refers to the phenomenon of a reversible change in color or the transmittance of light caused by the oxidation-reduction reaction occurring on the surface or in the neighborhood of an electrode in response to the application of voltage thereto, for example. Various materials have been reported as electrochromic substances which exhibit this phenomenon of electrochromism. The heretofore known coloring materials capable of inducing electrochromism include those which use metal oxides like tungsten oxide as disclosed in Japanese Patent Publication No. SHO 52-46098, those which use organic low-molecular weight compounds like viologen in the form of a solution as disclosed in published Japanese Patent Application, KOKAI (Early Publication) No. SHO 51-146253, and those which use electroconductive macromolecular compounds having conjugated double bonds in the main chain thereof as disclosed in published Japanese Patent Application, KOKAI No. SHO 56-67881, for example. Of the conventional coloring materials resorting to electrochromism, the metal oxides are produced by a vacuum process such as sputtering as disclosed in published Japanese Patent Application, KOKAI No. SHO 54-41756 and, therefore, have a problem of difficulty encountered in coating a large surface area with the metal oxide. In the case of the organic low-molecular weight compounds, the production of an electrochromic display device with such an organic low-molecular weight compound, as disclosed in published Japanese Patent Application, KOKAI No. SHO 51-146253, needs interposition of a diaphragm made of a semipermeable membrane between an electrode plate and a transparent electrode plate and further presence of a solution containing an organic low-molecular weight compound like viologen and a supporting electrolyte between the transparent electrode plate and the diaphragm and, therefore, is handicapped by the inevitable complication of the electrochromic display device in construction. Then, in the case of the electroconductive macromolecular compounds having conjugated double bonds in the main chain thereof, the polymerization of such a compound is effected directly on the surface of an electrode by the electrolytic polymerization technique, for example, as disclosed in published Japanese Patent Application, KOKAI No. SHO 60-188931. Thus, it is difficult to coat inexpensively the electrode of a large surface area with the polymer. Further, of the electroconductive macromolecular compounds having conjugated double bonds in the main chain thereof, those which are soluble in a solvent are generally non-polar and, therefore, are deficient in adhesion to an electrode which by nature has a polar surface. These electroconductive macromolecular compounds, therefore, fail to produce fast adhesion to the electrode and still suffer from a problem of layer separation. Particularly when the production of a solid type electrochromic display device by the use of an electroconductive macromolecular compound having conjugated double bonds in the main chain thereof and a macromolecular solid electrolyte is contemplated, the adhesiveness of the macromolecular compound to the macromolecular solid electrolyte poses a problem. In the produced device, the portions of inferior adhesion inhibit ionic conduction and form defective sites in the process of coloration and discoloration. In case where the adhesion is insufficient, the produced device after protracted use develops layer separation in consequence of repetition of the cycle of generation and extinction of color, change in temperature, or the like and the portions affected by the layer separation constitute themselves defective sites in the process of coloration and discoloration. As respects the copolymerization of the kind contemplated and disclosed by the present invention, a polymer having a thiophene oligomer in the side chain thereof is disclosed in published Japanese Patent Application, KOKAI No. HEI 4-108784. Though this polymer is notably improved in solubility, it lacks polarity and still suffers from a problem of inferior adhesion. JP-A-02 110 107 discloses electrochromic materials represented by the following general formula: wherein: R 1 is selected from the group consisting of H, lower alkoxy, NO 2 , NH 2 and lower alkylamino; R 2 , R 3 represent a lower alkyl group; R 4 is selected from the group consisting of H, halogen, lower alkyl, NO 2 , CN, lower alkoxy, lower alkanoyl, halogenated lower alkyl and lower alkanesulfonyl; A is selected from the group consisting of O, S and NR 5 (R 5 = lower alkyl); Q is selected from the group consisting of HC : CR 6 , HC : CH CH : CR 6 (R 6 = H) and lower alkyl; and m : n = 99.9 - 0.1 : 0.1 - 99.9 SUMMARY OF THE INVENTION The present invention, therefore, has an object of providing an electrochromic macromolecular substance exhibiting solubility in a solvent, possessing polarity, excelling in adhesiveness to an electrode and to a macromolecular solid electrolyte, and permitting effective formation of a coating on a large surface. Another object of the present invention is to provide a method for the production of the electrochromic macromolecular substance mentioned above. A further object of the present invention is to provide inexpensively a coloring-discoloring material using the electrochromic macromolecular substance mentioned above, which is free from such drawbacks as layer separation and consequent deficiency in coloration and discoloration and therefore particularly usable in an electrochromic display device. To accomplish the objects described above, in accordance with the present invention, there is provided a novel electrochromic copolymer as specified in claim 1. The copolymer mentioned above may be a block copolymer or a random copolymer and is produced by methods as specified in claims 12 and 13. The block copolymer is obtained by first polymerizing a chromophoric group-containing monomer represented by the general formula (2) in claims 12 and 13, adding a compatible group-containing monomer represented by the general formula (3) in claims 12 and 13 to the resultant reaction system, and further polymerizing the resultant mixture. The random copolymer is obtained by mixing a chromophoric group-containing monomer represented by the general formula (2) in claims 12 and 13 with a compatible group-containing monomer represented by the general formula (3) in claims 12 and 13 and polymerizing the resultant mixture. In accordance with the present invention, there are further provided a coloring-discoloring (or color extinction) material which contains a novel copolymer as specified in claim 1 and induces coloration or discoloration (or color extinction) by the oxidation or reduction of the copolymer and an electrochromic display device using the coloring-discoloring material. BRIEF DESCRIPTION OF THE DRAWINGS Other objects, features, and advantages of the invention will become apparent from the following description taken together with the drawings, in which: Fig. 1 is a graph showing a change in the absorption spectrum of an electrochromic copolymer film produced in Example 1 which will be cited hereinafter before and after immersion of the film in concentrated sulfuric acid; and Fig. 2 is a graph showing a change in the absorption spectrum of an electrochromic copolymer film produced in Example 3 which will be cited hereinafter before and after immersion of the film in concentrated sulfuric acid. DETAILED DESCRIPTION OF THE INVENTION The electrochromic substance according to the present invention is the copolymer of a chromophoric group-containing monomer having a chemical structure represented by the aforementioned general formula (2) containing a group based on an oligomer or a cooligomer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced and an unsaturated compound comprising a group possessing polarity and exhibiting affinity for ions (hereinafter referred to as "a compatible group-containing monomer") having a chemical structure represented by the aforementioned general formula (3). Since the novel copolymer which is obtained by the present invention is a copolymer of a compatible group-containing monomer of high polarity and a chromophoric group-containing monomer capable of functioning as a coloring material, it possesses high adhesiveness to a polar surface and exhibits strong adhesiveness. It further enjoys high affinity for an ion-conducting macromolecular substance and excels in adhesiveness to a macromolecular solid electrolyte. It is, therefore, free from such drawbacks as layer separation and consequent deficiency in coloration and discoloration which are entailed by the conventional coloring-discoloring materials. In addition, the copolymer itself possesses ionic conductivity. The group which is contained in the chromophoric group-containing monomer and based on an oligomer or a cooligomer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced is caused to produce inherent coloration or discoloration by an electrochemical oxidation-reduction. The electrochemical oxidation-reduction necessitates transfer of ions and causes coloration (or generation of color) and discoloration (or extinction of color) depending on the ion concentration. Since the novel copolymer according to the present invention possesses ionic conductivity and contains a chromophoric group capable of inducing inherent coloration or discoloration by the electrochemical oxidation-reduction, it functions as an ion-conducting chromophoric material and exhibits an outstanding chromophoric property. As concrete examples of the group R 1 which is based on an oligomer or a cooligomer possessing electroconductivity and inducing coloration or discoloration in consequence of the oxidation or reduction thereof, conjugated aromatic oligomers such as phenylene oligomer, naphthalene oligomer, anthracene oligomer, and azulene oligomer; conjugated heterocyclic oligomer such as thiophene oligomer, alkylthiophene oligomer, selenophene oligomer, pyrrole oligomer, pyridine oligomer, and furan oligomer; heteroatom-containing conjugated oligomer such as aniline oligomer; oligomer having a π electron conjugated group such as ferrocene and phthalocyanine in the side chain thereof; combinations thereof; modifications thereof obtained by introducing an alkyl group or a similar thereinto as a side chain thereof such as 3-alkyl thiophene oligomer; and modifications thereof obtained by introducing an alkyl group into the terminal thereof may be cited. The introduction of an alkyl group into any position of the nucleus of the oligomer mentioned above excluding the position attached to a vinyl group is effective for improving the solubility of a chromophoric group-containing monomer in a solvent and makes the subsequent treatment thereof easy. These substances are caused to manifest their inherent coloration and discoloration in consequence of the electrochemical oxidation-reduction. As the chromophoric group-containing monomers mentioned above, the chemical structures represented by the following four general formulas may be cited: wherein R 1 represents a group based on an oligomer or a cooligomer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced and B 1 , B 2 , and B 3 represent independently a substituent. Of these chromophoric group-containing monomers, the α,β-2 substituted compounds, i.e. the compounds of the general formulas (C) and (D), are deficient in polymerizability and are polymerized to a desired degree of macromolecularity only with difficulty. The compounds which logically constitute themselves sources of the group R 1 based on an oligomer or a cooligomer possessing electroconductivity and inducing coloration or discoloration by the oxidation or reduction thereof are generally such that their solubility in a solvent decreases in proportion as their degrees of polymerization increase. As a result, the chromophoric group-containing monomer which results from the combination with such a compound manifests low solubility in a solvent and undergoes a polymerization reaction only with difficulty. The influence of this behavior of solubility will be conspicuous particularly in the compounds of the chemical structure of (A). The compounds of the chemical structure of (B) secure solubility by virtue of the substituent B 1 and acquire polymerizability. As the chromophoric group-containing monomer for use in the present invention, therefore, the compounds of the aforementioned chemical formula of (B) are most desirable. The groups which possess polarity and exhibit affinity for ions and, therefore, fit the compatible group-containing monomers mentioned above are selected among hydroxyl group, carboxyl group, thiocarboxyl group, sulfonic group, sulfinic group, sulfenic group, nitrile group, aldehyde group, thioaldehyde group, amino group, imino group, mercapto group, esterified groups thereof, and amidated groups thereof. As the compatible group-containing monomers, similarly to the aforementioned chromophoric group-containing monomers, the chemical structures represented by the following four general formulas may be cited: wherein A represents a group possessing polarity and exhibiting affinity for ions and B 1 , B 2 , and B 3 represent independently a substituent. Of the compounds of the chemical structures cited above, those of the general formulas (G) and (H) produce polymers only with difficulty because they have poor ability to polymerize similarly to the case of the chromophoric group-containing momoners. In the present invention, the compounds of the general formulas (E) and (F) are effectively usable. In the case of compounds of the general formula of (E), since they strongly manifest the quality of the group A possessing polarity and exhibiting affinity for ions, it will be at times difficult to find a solvent which has strong polarity and is capable of simultaneously solving a chromophoric group-containing monomer and a compatible group-containing monomer. In the case of the compounds of the general formula of (F), since their solubility is variable with the particular kind of the substituent B 1 , a solvent capable of simultaneously solving a chromophoric group-containing monomer and a compatible group-containing monomer can be secured. The substituents of a chromophoric group-containing monomer and a compatible group-containing monomer should be saturated alkyl groups so as to preclude the otherwise possible occurrence of cross-linkage in the process of polymerization. The sizes of these saturated alkyl groups are only required to be such that the corresponding monomers are soluble in a solvent. Thus, the alkyl groups are such that their numbers of carbon atoms are in the range of 1 to 1,000. If the molecular weight of the pendant alkyl group of the monomer is too high, however, the reactivity thereof will be degraded and the time required for the coloration or discoloration of the resultant electrochromic substance will be prolonged. Thus, the pendant alkyl group (R 2 or R 3 ) of each of the chromophoric group-containing monomer and the compatible group-containing monomer is desired to have 1 to 50 carbon atoms. To secure the sufficient solubility in a solvent and the suitable time required for the coloration or discoloration of the electrochromic substance as required in commercial use, the pendant alkyl group is particularly desired to have 1 to 25 carbon atoms. When the group possessing polarity and exhibiting affinity for ions happens to have so strong polarity as to inhibit a polymerization reaction, when no existing solvent is capable of simultaneously solving a chromophoric group-containing monomer and a compatible group-containing monomer, or when the relevant monomers are not stable, for example, the group possessing polarity and exhibiting affinity for ions is enabled to secure reactivity, solubility, and stability as required by having this group esterified or amidated in advance of polymerization. The ester or amide can be decomposed by hydrolysis after the polymerization. The chromophoric group-containing monomer and the compatible group-containing monomer described above can be easily polymerized in a suitable solvent by the use of a polymerization initiator, for example, peroxides such as benzoyl peroxide and azo compounds such as azobisisobutyronitrile. In the production of a block copolymer, a block copolymer having a chromophoric group-containing monomer and a compatible group-containing monomer severally polymerized in the form of a block is obtained by first polymerizing the chromophoric group-containing monomer alone, then adding the compatible group-containing monomer to the produced polymer, and further effecting polymerization of the resultant mixture. In the production of a random copolymer, a random copolymer whose configuration is determined by the reactivity and selectivity of each of the two monomers involved is obtained by first mixing the chomophoric group-containing monomer with the compatible group-containing monomer and then subjecting the resultant mixture to polymerization. The proportion of the chromophoric group-containing monomer to the copolymer falls in the range of 0.1 to 30% by molar ratio. That is, the molar ratio of the chromophoric group-containing monomer to the compatible group-containing monomer is within the range of 0.1 : 99.9 to 30 : 70. When the copolymer has an unduly high content of the chromophoric group-containing monomer, it is at a disadvantage in sacrificing adhesiveness and film strength to a great extent. This disadvantage will increase particularly when the group based on a polymer or a copolymer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced assumes an unduly large proportion. To secure the electroconductivity, however, the proportion of the chromophoric group-containing monomer to the copolymer is desired to be as high as possible. When the copolymer has a low content of the chromophoric group-containing monomer, a long period is required for the coloration of the electrochromic substance. As for the solubility of the copolymer in a solvent, it is desired that the copolymer has a high content of the compatible group-containing monomer. Particularly, when the copolymer contains vinyl acetate, it may dissolve in various solvents. Thus, the proportion of the chromophoric group-containing monomer to the copolymer is within the range of 20 to 30% by molar ratio. The total degree of polymerization of the copolymer is in the range of 10 to 12,000 in consideration of ease of reaction, solubility in a solvent, and strength of the film to be formed of the copolymer. If the degree of polymerization is too high, the polymer solution will be applied to a substrate only with difficulty because the solubility of the copolymer in a solvent is lowered and the viscosity of the resultant solution inevitably increases. To obtain the copolymer excelling in solubility and application properties and secure the sufficient strength of the film to be formed of the copolymer as the electrochromic material, the degree of polymerization is desired to be in the range of 20 to 1,500, preferably 20 to 250. In general, the chromophoric group-containing monomer is soluble in a non-polar solvent and, therefore, may be polymerized in the non-polar solvent such as toluene, benzene, and tetrahydrofuran. As for the compatible group-containing monomer, vinyl acetate, methyl methacrylate, etc. are soluble in toluene, benzene, tetrahydrofuran, and the like. In the polymerization of the copolymer according to the present invention, the solvent capable of dissolving both the chromophoric group-containing monomer and the compatible group-containing monomer therein may be used. The produced copolymer is soluble in these solvents. In case the compatible group (A) of the copolymer is hydroxyl group or carboxyl group, the copolymer is soluble in a polar solvent such as dimethyl formamide and dimethyl sulfoxide. Further, the copolymer containing vinyl acetate exhibits solubility in a commonly used solvent such as acetone, too. The copolymer of the present invention which is obtained as described above allows production of a film by any of the conventional methods. When the group possessing polarity and exhibiting affinity for ions happens to be a hydroxyl group, for example, in the same manner as the preparation of the film of polyvinyl alcohol, the copolymer allows production of this film by a method which comprises dissolving this copolymer in a suitable solvent thereby preparing a solution, for example, a dimethyl sulfoxide solution containing the copolymer at a concentration in the range of 0.1 to 5%, casting the solution on a glass plate, and drying the resultant layer of the solution at a temperature in the neighborhood of 70°C under a reduced pressure for about 10 hours. As mentioned above, since the novel copolymer according to the present invention is excellent in the ability of coloration-discoloration and in the adhesive strength manifested to an electrode and a macromolecular solid electrolyte and, at the same time, soluble in a solvent, it allows manufacture of a film on a large surface as by the casting technique. It, therefore, constitutes itself a highly practical and advantageous material for electrochromic display devices. It is well known in the art that the electrochromic display device essentially comprises a transparent electrode, a counter electrode, and an electrochromic substance and an electrolyte solution or solid electrolyte both interposed between the transparent electrode and the counter electrode. ITO (indium tin oxide) may be advantageously used as the transparent electrode and as the counter electrode. When the transparency is not required for the counter electrode, such an electrode as metal or carbon electrode which is commonly used in electrochemical devices may be used as the counter electrode. As a supporting electrolyte for accelerating coloration and discoloration of the electrochromic substance, ionizing salts which exhibit good solubility in a solution or solid electrolyte to be used as a carrier thereof and contain an anion exhibiting the electron releasing property to such an extent that the coloration of the chromophoric group is secured may be used. Examples of supporting electrolytes which are usable in the present invention include, but are not limited to: LiClO 4 , KClO 4 , NaClO 4 , LiBF 4 , KBF 4 , NaBF 4 , LiAsF 6 , KAsF 6 , and NaAsF 6 . Examples of solid electrolytes which are usable in the present invention include, but are not limited to: polyethylene oxide, macromolecular polyethylene glycol, polyvinyl alcohol, and gel of propylene carbonate. Now, the present invention will be described specifically below with reference to working examples. Example 1: A vinyl monomer having a trimer of thiophene as a chromophoric group thereof was synthesized in accordance with the method disclosed in published Japanese Patent Application, KOKAI No. HEI 4-108784. In 5 ml of benzene, 0.15 g of the resultant vinyl monomer and 0.01 g of azobisisobutyronitrile were stirred at 60°C for 24 hours and the resultant mixture and 4.5 g of vinyl acetate monomer added thereto were together subjected to polymerization for 24 hours. Benzene was removed from the polymerization product under reduced pressure. The block copolymer thus deprived of the solvent was dissolved in methanol and the solution was cast on a glass plate to form a film. The film consequently obtained assumed a light yellow color and exhibited good adhesiveness to glass. When the film as held fast on the glass plate was immersed in concentrated sulfuric acid, the color of the film changed to a red color. The change in a visible ultraviolet spectrum of the produced copolymer film before and after immersion in the concentrated sulfuric acid is shown in Fig. 1. Example 2: A vinyl monomer having a trimer of thiophene as a chromophoric group thereof was synthesized in accordance with the method disclosed in published Japanese Patent Application, KOKAI No. HEI 4-108784. In 5 ml of benzene, 0.15 g of the resultant vinyl monomer, 4.5 g of vinyl acetate monomer, and 0.01 g of azobisisobutyronitrile were stirred for polymerization at 60°C for 48 hours. Benzene was removed from the polymerization product under reduced pressure. The copolymer deprived of the solvent was dissolved in 250 ml of methanol. The resultant solution was saponified by being stirred at room temperature for 24 hours in conjunction with 6.3 ml of an aqueous 40% sodium hydroxide solution. The obtained saponification product was found by the infrared spectrum thereof to have a saponification ratio of about 100%. The copolymer thus produced was dissolved in dimethyl sulfoxide and the solution was cast on an ITO (indium tin oxide) glass plate to form a film. The produced film assumed a light yellow color and showed good adhesiveness to the ITO glass. When the ITO glass (transparent electrode) having the polymer film deposited thereon was subjected to a doping treatment by being opposed to a counter electrode made of platinum in an electrolytic solution (containing lithium perchlorate/propylene carbonate in a concentration of 0.1 mol per liter) and exposed to a potential of +2 V, the polymer film assumed a red color. When the polymer was dedoped by inverting the potential to -2 V, it resumed the light yellow color. As the result of the determination of a visible ultraviolet spectrum of the produced polymer, it was found to exhibit a similar spectrum to that of Fig. 1. Example 3: 0.405 g of magnesium and 5.00 g of 4-bromo-4'-n-pentyl biphenyl were introduced into a flask containing 20 ml of tetrahydrofuran and the mixture was stirred until magnesium disappeared. The resultant solution kept at 0°C was gradually added dropwise to a solution obtained by stirring and dispersing 2.51 g of 4-chloro-alpha-methyl styrene and 0.072 g of dichloro-1,3-bis (diphenylphosphinopropane) nickel (II) in 15 ml of tetrahydrofuran. The mixture was stirred at 35°C for two and a half hours and at room temperature for 13 hours. Thereafter, 400 ml of 1N hydrochloric acid was added dropwise to the mixture and the mixture was further stirred for one hour to continue the reaction. At the termination of the reaction the mixture was washed with water and subjected to a filtration and subsequent extraction with diethyl ether to separate the object; a vinyl monomer having a trimer of phenylene as a chromophoric group. In 4 ml of toluene, 0.5 g of the resultant vinyl monomer, 2.5 g of vinyl acetate monomer, and 0.058 g of azobisisobutyronitrile were stirred at 90°C for 35 hours to effect polymerization. The polymerization product was purified by reprecipitation from hexane to obtain a random copolymer. The purified random copolymer was dissolved in toluene and the solution was cast on a glass plate to form a film. The produced film assumed a yellowish white color and exhibited good adhesiveness to glass. When the film as held fast on the glass plate was immersed in concentrated sulfuric acid, the color of the film changed to a red color. The change in color of the film was reversible. When the film was immersed in ammonia water, its color was reverted to the original color. The change in a visible ultraviolet spectrum of the produced copolymer film before and after immersion in the concentrated sulfuric acid is shown in Fig. 2. Example 4: A vinyl monomer having a trimer of phenylene as a chromophoric group was prepared in the same manner as in Example 3. In 4 ml of toluene, 0.5 g of the resultant vinyl monomer and 0.058 g of azobisisobutyronitrile were stirred at 90°C for 20 hours and the resultant mixture and 2.5 g of vinyl acetate monomer added thereto were together subjected to further polymerization for 15 hours. The polymerization product was purified by reprecipitation from hexane to obtain a block copolymer. The obtained block copolymer was dissolved in 250 ml of methanol, 0.5 ml of aqueous 20% sodium hydroxide solution was added thereto, and the mixture was stirred at room temperature for one hour. The mixture and an equal weight of hydrochloric acid added thereto were together added dropwise to ice-water and the precipitate was washed with water. The obtained copolymer was dissolved in methanol and the solution was cast on a glass plate to form a film. The produced film assumed a yellowish white color and exhibited good adhesiveness to glass. When the film as held fast on the glass plate was immersed in concentrated sulfuric acid, the color of the film changed to a red color. The change in color of the film was reversible. When the film was immersed in ammonia water, its color was reverted to the original color. The change in a visible ultraviolet spectrum of the produced copolymer film before and after immersion in the concentrated sulfuric acid was same as that of Fig. 2. Example 5: A vinyl monomer having a trimer of phenylene as a chromophoric group was prepared in the same manner as in Example 3. In 4 ml of toluene, 0.5 g of the resultant vinyl monomer and 0.058 g of azobisisobutyronitrile were stirred at 90°C for 20 hours and the resultant mixture and 2.5 g of vinyl acetate monomer added thereto were together subjected to further polymerization for 15 hours. The polymerization product was purified by reprecipitation from hexane to obtain a block copolymer. The obtained block copolymer was dissolved in 250 ml of methanol, 6 ml of aqueous 40% sodium hydroxide solution was added thereto, and the mixture was stirred at room temperature for 24 hours. The mixture and an equal weight of hydrochloric acid added thereto were together added dropwise to ice-water and the precipitate was washed with water. The obtained copolymer was dissolved in methanol and the solution was cast on a glass plate to form a film. The produced film assumed a yellowish white color and exhibited good adhesiveness to glass. When the film as held fast on the glass plate was immersed in concentrated sulfuric acid, the color of the film changed to a red color. The change in color of the film was reversible. When the film was immersed in ammonia water, its color was reverted to the original color. The change in a visible ultraviolet spectrum of the produced copolymer film before and after immersion in the concentrated sulfuric acid was same as that of Fig. 2. While certain specific working examples have been disclosed herein, the invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The described examples are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by foregoing description and all changes which come within the meaning and range of equivalency of the claims are, therefore, intended to be embraced therein.

Claims: A copolymer which exhibits electrochromism and is represented by the following general formula (1): wherein R 1 represents a group based on an oligomer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced, R 2 and R 3 represent independently a hydrogen atom or an alkyl group having 1 to 1,000 carbon atoms, A represents a group selected from the group consisting of hydroxyl group, carboxyl group, thiocarboxyl group, sulfonic group, sulfinic group, sulfenic group, nitrile group, aldehyde group, thioaldehyde group, amino group, imino group, mercapto group, esterified groups thereof, and amidated groups thereof, and L and M are independently an integer of at least 1, providing that the total degree of polymerization is an integer in the range of 10 to 12,000, wherein the molar ratio (L/(L+M)) of the chromophoric group containing monomer to the compatible group containing monomer is within the range of 0.1:99 to 30:70 in said general formula (1). A copolymer according to claim 1, which is a random copolymer. A copolymer according to claim 1, which is a block copolymer. A copolymer according to any one of claims 1 to 3, wherein said group R 1 of the general formula (1) is a group based on an oligomer selected from the group consisting of conjugated aromatic oligomers, conjugated heterocyclic oligomers, hetero-atom-containing conjugated oligomers, oligomers having a π electron conjugated group in a side chain thereof, cooligomers of the oligomers mentioned above, modifications of said oligomers and cooligomers obtained by introducing an alkyl group thereinto as a side chain thereof, and modifications of said oligomers and cooligomers obtained by introducing an alkyl group into a terminal thereof. A copolymer according to any one of claims 1 to 3, wherein said group R 1 of the general formula (1) is a group based on an oligomer selected from the group consisting of phenylene oligomer, naphthalene oligomer, anthracene oligomer, azulene oligomer, thiophene oligomer, alkylthiophene oligomer, selenophene oligomer, pyrrole oligomer, pyridine oligomer, furan oligomer, aniline oligomer, oligomer having ferrocene in a side chain thereof, oligomer having phthalocyanine in a side chain thereof, modifications of said oligomers obtained by introducing an alkyl group thereinto as a side chain thereof, and modifications of said oligomers obtained by introducing an alkyl group into a terminal thereof. A copolymer according to any one of claims 1 to 3, which is a copolymer of a vinyl monomer having a thiophene oligomer in the side chain thereof and a vinyl acetate monomer. A copolymer according to any one of claims 1 to 3, which is a saponification product of a copolymer of a vinyl monomer having a thiophene oligomer in the side chain thereof and a vinyl acetate monomer. A copolymer according to any one of claims 1 to 3, which is a copolymer of a vinyl monomer having a phenylene oligomer in the side chain thereof and a vinyl acetate monomer. A copolymer according to any one of claims 1 to 3, which is a saponification product of a copolymer of a vinyl monomer having a phenylene oligomer in the side chain thereof and a vinyl acetate monomer. A copolymer according to any one of claims 1 to 9, wherein the total degree of polymerization is within the range of 20 to 1,500. A copolymer according to any one of claims 1 to 10, wherein said groups R 2 and R 3 of the general formula (1) are independently an alkyl group having 1 to 25 carbon atoms. A method of producing a copolymer exhibiting electrochromism, which comprises the steps of: polymerizing a compound represented by the following general formula (2) wherein R 1 represents a group based on an oligomer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced, R 2 represents a hydrogen atom or an alkyl group having 1 to 1,000 carbon atoms, adding to the resultant reaction system a compound represented by the following general formula (3): wherein R 3 represents a hydrogen atom or an alkyl group having 1 to 1,000 carbon atoms and A represents a group possessing polarity and exhibiting affinity for ions selected from the group consisting of hydroxyl group, carboxyl group, thiocarboxyl group, sulfonic group, sulfinic group, sulfenic group, nitrile group, aldehyde group, thioaldehyde group, amino group, imino group, mercapto group, esterified groups thereof, and amidated groups thereof, and further polymerizing the resultant mixture to obtain a block copolymer represented by the following general formula (1): wherein R 1 , R 2 , R 3 and A have the same meanings as defined above, and L and M are independently an integer of at least 1, providing that the total degree of polymerization is an integer in the range of 10 to 12,000 and the molar ratio of the compound represented by the general formula (2) to the compound represented by the general formula (3) is within the range of 0.1 : 99.9 to 30 : 70. A method of producing a copolymer exhibiting electrochromism, which comprises the steps of: mixing a compound represented by the following general formula (2): wherein R 1 represents a group based on an oligomer possessing electroconductivity and inducing coloration or discoloration on being oxidized or reduced, R 2 represents a hydrogen atom or an alkyl group having 1 to 1,000 carbon atoms, with a compound represented by the following general formula (3): wherein R 3 represents a hydrogen atom or an alkyl group having 1 to 1,000 carbon atoms and A represents a group possessing polarity and exhibiting affinity for ions selected from the group consisting of hydroxyl group, caboxyl group, thiocarboxyl group, sulfonic group, sulfinic group, sulfenic group, nitrile group, aldehyde group, thioaldehyde group, amino group, imino group, mercapto group, esterified groups thereof, and amidated groups thereof, and polymerizing the resultant mixture to obtain a random copolymer represented by the following general formula (1): wherein R 1 , R 2 , R 3 and A have the same meanings as defined above, and L and M are independently an integer of at least 1, providing that the total degree of polymerization is an integer in the range of 10 to 12,000 and the molar ratio of the compound represented by the general formula (2) to the compound represented by the general formula (3) is within the range of 0.1 : 99.9 to 30 : 70. A method according to claim 12 or 13, wherein said compound represented by the general formula (3) has the group A esterified and the ester in the copolymer is hydrolzyed after the completion of polymerization. A method according to claim 12 or 13, wherein said compound represented by the general formula (3) has the group A amidated and the amide in the copolymer is hydrolyzed after the completion of polymerization. A method according to any one of claims 12 to 15, wherein said group R 1 of the compound represented by the general formula (2) is a group based on an oligomer selected from the group consisting of phenylene oligomer, naphthalene oligomer, anthracene oligomer, azulene oligomer, thiophene oligomer, alkylthiophene oligomer, selenophene oligomer, pyrrole oligomer, pyridine oligomer, furan oligomer, aniline oligomer, oligomer having ferrocene in a side chain thereof, oligomer having phthalocyanine in a side chain thereof, modifications of said oligomers obtained by introducing an alkyl group thereinto as a side chain thereof, and modifications of said oligomers obtained by introducing an alkyl group into a terminal thereof. A method according to any one of claims 12 to 16, wherein said compound represented by the general formula (2) is a vinyl monomer having a thiophene oligomer in the side chain thereof, and said compound represented by the general formula (3) is a vinyl acetate monomer. A method according to any one of claims 12 to 16, wherein said compound represented by the general formula (2) is a vinyl monomer having a phenylene oligomer in the side chain thereof, and said compound represented by the general formula (3) is a vinyl acetate monomer. A method according to claims 17 or 18, which further comprises a step of saponification of the resultant copolymer. A method according to any one of claims 12 to 19, wherein said groups R 2 and R 3 of the general formulas (2) and (3) are independently an alkyl group having 1 to 25 carbon atoms. A coloring-discoloring material which comprises in combination: a supporting electrolyte and a copolymer according to claim 1. A material according to claim 21, wherein said group R 1 of the general formula (1) is a group based on an oligomer selected from the group consisting of phenylene oligomer, naphthalene oligomer, anthracene oligomer, azulene oligomer, thiophene oligomer, alkylthiophene oligomer, selenophene oligomer, pryrrole oligomer, pyridine oligomer, furan oligomer, aniline oligomer, oligomer having ferrocene in a side chain thereof, oligomer having phthalocyanine in a side chain thereof, modifications of said oligomers obtained by introducing an alkyl group thereinto as a side chain thereof, and modifications of said oligomers obtained by introducing an alkyl group into a terminal thereof. A material according to claim 21 or 22, wherein said supporting electrolyte is at least one salt selected from the group consisting of LiClO 4 , KClO 4 , NaClO 4 , LiBF 4 , KBF 4 , NaBF 4 , LiAsF 6 , KAsF 6 , and NaAsF 6 . In an electrochromic display device comprising a transparent electrode, a counter electrode, and an electrochromic substance and a supporting electrolyte both interposed between said transparent electrode and said counter electrode, the improvement in which said electrochromic substance is a copolymer according to claim 1. A device according to claim 24, wherein said electrochromic substance is coated on the transparent electrode. A device according to claim 24 or 25, wherein said group R 1 of the general formula (1) is a group based on an oligomer selected from the group consisting of phenylene oligomer, naphthalene oligomer, anthracene oligomer, azulene oligomer, thiophene oligomer, alkylthiophene oligomer, selenophene oligomer, pyrrole oligomer pyridine oligomer, furan oligomer, aniline oligomer, oligomer having ferrocene in a side chain thereof, oligomer having phthalocyanine in a side chain thereof, modifications of said oligomers obtained by introducing an alkyl group thereinto as a side chain thereof, and modifications of said oligomers obtained by introducing an alkyl group into a terminal thereof. A device according to any one of claims 24 to 26, wherein said copolymer has the total degree of polymerization within the range of 20 to 1,500. A device according to any one of claims 24 to 27, wherein said supporting electrolyte is at least one salt selected from the group consisting of LiClO 4 , KClO 4 , NaClO 4 , LiBF 4 , KBF 4 , NaBF 4 , LiAsF6, KAsF 6 , and NaAsF 6 .

Inventors: WAKABAYASHI MASAKI, YAMAMOTO TAKAKAZU, WAKABAYASHI, MASAKI, YAMAMOTO, TAKAKAZU
Applicants: YAMAMOTO TAKAKAZU, YKK CORP, YAMAMOTO, TAKAKAZU, YKK CORPORATION
Application year: 1993
Main classification: C08F246
IPC codes: C08F246, C08F8, C09K9, G02F1