Polymer precursor for silicon carbide/aluminum nitride ceramics

Abstract: A block copolymer is prepared by reacting an aluminum-nitrogen polymer and a silazane polymer at a temperature not greater than 400°C. Block copolymers containing alkenyl or alkynyl groups can be crosslinked by supplying energy to generate free radicals. An AlN/SiC-containing ceramic is formed by pyrolyzing the crosslinked block copolymer in a nonoxidizing atmosphere.

Description: This invention relates to polymer precursors for silicon carbide ceramics containing aluminum nitride. Ceramic materials are of critical importance for a number of high temperature, high performance applications. These applications require a unique combination of properties such as high specific strength, high temperature mechanical property retention, low thermal and electrical conductivity, hardness and wear resistance, and chemical inertness. Silicon carbide is an extremely hard ceramic that exhibits short-term high strength at elevated temperatures. It oxidizes slowly in air and is serviceable to about 1500°C. Silicon carbide possesses high corrosion resistance, low bulk density, and excellent creep and wear resistance. Nevertheless, microstructural instability during heating often limits the use of SiC in many such applications for extended periods of time. The morphology of SiC formed at low temperatures is cubic (beta-SiC, 3C). Alpha-SiC, which can have either hexagonal (alpha-SiC, 2H, 4H, 6H) or rhombohedral (alpha-SiC, 15R, 21R) morphologies, forms at higher temperatures. Also, beta-SiC transforms to alpha-SiC at higher temperatures. These various polytypes can undergo one or more phase transformations between 1400°C and 2200°C, often resulting in exaggerated grain growth. Such grain growth can result in brittle failure of the ceramic under structural loading. It is known that the presence of >1% AlN in hot-pressed SiC samples results in sintered parts having reduced grain size and improved microstructural uniformity. These phenomena have been attributed to the formation of solid solutions of the AlN in the SiC ceramic. The formation of dense bodies of SiC/AlN solid solutions from a mixture of SiC and AlN powder requires not only powder consolidation (sintering), but also thorough solid-state diffusion of the AlN into the SiC microstructure. Therefore, the high melting points and low solid state diffusivities of both AlN and SiC have limited the use of solid solution SiC/AlN ceramics. As a result, consolidated samples having representative properties have, for the most part, been prepared by pressure-assisted densification methods (e.g., hot-pressing) at relatively high temperatures (2100°C). Such techniques are energy-inefficient and severely limit the complexity of the part that can be fabricated. Polymer precursors have also been used to prepare SiC/AlN ceramics, including solid solutions. For example, U.S. Patent 4,730,026 discloses crosslinked polysilazanes in which the silazane units are linked together by at least one bridge of the formula -MR' n - attached to the nitrogen atoms of silazane repeat units, where M is a metal selected from Groups IIIA, IIB, IVB and IIA of the Periodic Table. W. R. Schmidt et al. disclose preparing a single component precursor to SiC/AlN by treating 1,3,5-trivinylcyclotrisilazane with triethylaluminum. The silazane units are bridged by one -Al(C 2 H 5 )-unit (The Second International Ceramic Science and Technology Congress, Nov. 12-15, 1990, Orlando, FL). None of these polymeric AlN/SiC ceramic precursors are block copolymers in which blocks of repeat units alternate with or are bridged by repeat units where x > 1 and y > 1, and none offer the ability to cure from a liquid to an infusible solid in a controlled fashion at low temperatures. The block copolymers of this invention comprise a multiplicity of blocks of units having the formula: and a multiplicity of blocks of units having the formula: or wherein x > 1 and y > 1; the blocks x and y are bonded through Si-N-Al linkages; R 1 and R 2 are the same or different and are selected from the group consisting of hydrogen, substituted or unsubstituted 1-12 carbon alkyl, 3-12 carbon cycloalkyl, 2-12 carbon alkenyl, 3-12 carbon cycloalkenyl, and aryl groups; R 3 , R 4 and R 5 are the same or different and are selected from the group consisting of hydrogen, substituted or unsubstituted 1-6 carbon alkyl, 3-6 carbon cycloalkyl, 3-6 carbon cycloalkenyl, aryl, 2-6 carbon alkenyl and 2-6 carbon alkynyl groups, provided that R 1 , R 2 , R 3 , R 4 and R 5 are not all hydrogen and A is O or S. In a preferred embodiment, the silazane units are derived from a (thio)urea-modified silazane. Also according to the invention, these block copolymers are prepared by reacting an aluminum-nitrogen polymer containing Al-C or Al-H bonds with a silazane or a (thio)ureasilazane polymer containing N-H bonds with concomitant formation of C-H or H-H bonds to form hydrocarbon or hydrogen as a by-product. Block copolymers containing alkenyl or alkynyl groups can be cured in the presence of a free radical generator. Pyrolysis of the cured block copolymer in a nonoxidizing atmosphere yields a dense SiC/AlN ceramic. A wide range of ceramic compositions containing SiC and AlN can be prepared from such polymeric ceramic precursors by adjusting the ratio of silazane or (thio)ureasilazane polymer to aluminum-nitrogen polymer during preparation of the block copolymer. Since these polymeric liquids can often be processed using such conventional plastics forming techniques as coating, extrusion, and fiber spinning, a variety of intricately shaped refractory articles can be fabricated. After processing, block copolymers containing unsaturated organic groups can be conveniently cured to a solid that does not lose its dimensional integrity upon pyrolysis. Another advantage of the use of such polymers is their chemical reactivity during pyrolysis. The stoichiometry of Si to C to Al to N desired in the ceramic product is determined at the molecular level in the synthesis step. Therefore such compositions do not require extended treatment at high temperatures after pyrolysis to promote the solid state diffusion often required to form solid solution SiC/AlN ceramics from powder mixtures. The block copolymers of this invention are prepared by heating a mixture of an aluminum-nitrogen polymer containing Al-C or Al-H bonds and a silazane or (thio)ureasilazane polymer containing N-H bonds at a temperature not greater than 400°C, preferably from 90°C to 220°C. Organic groups attached to the Al and N of the Al-N polymer or to the Si atom of the silazane or (thio)ureasilazane polymer can be free of unsaturation or some of them can be unsaturated. Polysilazanes are well known in the art, for example, as described in U.S. Patents 3,853,567; 4,482,669; 4,612,383; 4,675,424; 4,689,252 and 4,722,988. Addition polymers of polysilazanes that are prepared by treating a polysilazane with an isocyanate, isothiocyanate, ketene, thioketene, carbodiimide or carbon disulfide can also be used. Preparation of these addition polymers is described in U.S. Patent 4,929,704. When a polysilazane is reacted with an aluminum-nitrogen polymer containing Al-C or Al-H bonds, the resulting block copolymer comprises a multiplicity of blocks of units having the formula: and a multiplicity of blocks of units having the formula: where x, y, R 1 , R 2 , R 3 and R 4 are defined below. A preferred polymer is obtained by treating a polysilazane containing N-H bonds with an iso(thio)cyanate to form a poly(thio)ureasilazane. The notation "(thio)ureasilazane" indicates that either a ureasilazane or a thioureasilazane can be used. When the resulting (thio)ureasilazane polymer is reacted with an aluminum-nitrogen polymer containing Al-C or Al-H bonds, the resulting block copolymer comprises a multiplicity of blocks of units having the formula: and a multiplicity of blocks of units having the formula: wherein x > 1 and y > 1; the blocks x and y are bonded through Si-N-Al linkages; R 1 and R 2 are the same or different and are selected from the group consisting of hydrogen, substituted or unsubstituted 1-12 carbon alkyl, 3-12 carbon cycloalkyl, 2-12 carbon alkenyl, 3-12 carbon cycloalkenyl, and aryl groups; R 3 , R 4 and R 5 are the same or different and are selected from the group consisting of hydrogen, substituted or unsubstituted 1-6 carbon alkyl, 3-6 carbon cycloalkyl, 3-6 carbon cycloalkenyl, aryl, 2-6 carbon alkenyl, and 2-6 carbon alkynyl groups, provided that R 1 , R 2 , R 3 , R 4 and R 5 are not all hydrogen, and A is O or S. Most preferred is a polyureasilazane prepared by reacting a vinyl-substituted polysilazane containing N-H bonds and phenylisocyanate as described in Example C. The aluminum-nitrogen polymers employed in the practice of this invention can be soluble or insoluble solids, or liquids of various viscosities, and have a backbone comprising alternating aluminum- and nitrogen-containing groups. Suitable polymers include aluminum amide polymers, aluminum imide polymers, aluminum imine polymers and polyaminoalanes. Polymers containing an aluminum-nitrogen bond suitable for purposes of the present invention have a general formula selected from the group consisting of: a polymer comprising structural units of the general formula: where n ≥ 2 and R, R', R'' and R''' are selected from the group consisting of alkyl, cycloalkyl, alkenyl, aryl, and hydrogen; a polymer comprising structural units of the general formula: where n ≥ 2 and R'' is an imine group, and R and R' are selected from the group consisting of alkyl, cycloalkyl, alkenyl, aryl and hydrogen; and a polymer comprising structural units of the general formula: where n ≥ 2 and R and R' are selected from the group consisting of alkyl, cycloalkyl, alkenyl, aryl and hydrogen. Preferred aluminum-nitrogen polymers are prepared by heating the reaction product of a dialkylaluminum hydride and an organic nitrile. Most preferred is an aluminum-nitrogen polymer prepared from acetonitrile and diisobutylaluminum hydride as described in Example A. Block copolymers containing at least one site of organounsaturation can be crosslinked, i.e., cured, by supplying energy to generate free radicals. Block copolymers containing alkenyl or alkynyl groups on silicon can also be crosslinked by heating in the presence of a free radical generator. For example, the block copolymer of Example 1 can be heated in the presence of from 0.1 wt. % to 8 wt. % of a radical source such as a peroxide or an azo compound. The cured block copolymers are infusible solids that retain their shape upon pyrolysis and are insoluble in common organic solvents. Suitable peroxides include for example, diaroyl peroxides such as dibenzoyl peroxide, di-p-chlorobenzoyl peroxide and bis-2,4-dichlorobenzoyl peroxide; dialkyl peroxides such as 2,5-dimethyl-2,5-di(t-butylperoxy)hexane and di-t-butyl peroxide; diaralkyl peroxides such as dicumyl peroxide; alkyl aralkyl peroxides such as t-butyl cumyl peroxide and 1,4-bis(t-butyl-peroxyisopropyl)benzene; alkylaroyl peroxides; and alkylacyl peroxides such as t-butyl perbenzoate, t-butyl peracetate and t-butyl peroctoate. Dicumyl peroxide is preferred. Suitable azo compounds include, for example, symmetrical or unsymmetrical azo compounds such as, for example, 2,2'-azobis(2-methylpropionitrile); 2,2'-azodimethyl-4-methoxyvaleronitrile); 1-cyano-1-(t-butylazo)cyclohexane; and 2-(t-butylazo)-isobutyronitrile. These compounds are well known and are described, for example, in U.S. Patents 2,492,763 and 2,515,628. The block copolymers of the present invention containing sites of organounsaturation can also be cured by exposing the polymer to UV light or electron beam radiation. Suitable UV curing agents-such as alpha, alpha-dimethoxyalpha-phenylacetophenone (DMPAP) enhance UV curing. The block copolymers can be mixed with metal or ceramic fillers. Suitable fillers include, for example, SiC, AlN, Si 3 N 4 , SiO 2 , BN, Al 2 O 3 , TiN, TiC, Si, Ti, Zr, Al, ZrC, ZrO 2 , B 4 C, TiB 2 , HfC and Y 2 O 3 , which can be in the form of powders, whiskers or platelets. A powder, whisker or platelet which comprises a solid solution of SiC and AlN can also be used as a filler. SiC and AlN are the preferred fillers and can be present in an amount of from about 5% to about 98% by weight, based on the total weight of the polymer/SiC mixture. SiC is most preferred. Alpha-SiC, beta-SiC and mixtures thereof can be used. Mixtures of the filler with the block copolymers can be prepared using standard ceramic mixing equipment, which includes, for example, ball mills, double planetary mixers, three roll mills, sigma blade mixers, ribbon blenders, extruders and other apparatus known to those skilled in the art. Mixtures of the block copolymer binder and fillers can be molded by processes including, for example, dry pressing, tape casting, isostatic pressing, extrusion and injection molding. Pyrolysis of the cured or uncured block copolymers at 600° to 2200°C, preferably 1000° to 2000°C, in a nonoxidizing atmosphere yields silicon carbide/aluminum nitride-containing ceramic materials. The non-oxidizing atmosphere can be one that does not contain nitrogen, e.g., argon or helium, or one that does contain nitrogen, e.g., treatment with NH 3 followed by treatment with N 2 at a higher temperature. If the atmosphere contains nitrogen, silicon nitride will also be present in the ceramic product. Temperatures in excess of 2000°C are typically used for densification. The amounts of SiC and AlN formed during pyrolysis depend upon the original ratio of Si introduced in the silazane component of the block copolymer and the Al introduced in the alazane component of the block copolymer. X-ray powder diffraction and energy dispersive X-ray analysis confirm the presence of both SiC and AlN phases. These phases can be in the form of an AlN/SiC solid solution or an AlN/SiC microcomposite. By microcomposite is meant a composite wherein discrete particulate domains of AlN and SiC are homogeneously interdispersed at the micron to submicron level. The polymeric ceramic precursors of this invention can be used for forming fibers, films, coatings and monoliths, in the infiltration of a preform structure, as an adhesive or sealant, and as a binder for ceramic or metal powders. Example A An aluminum-nitrogen polymer was prepared as follows. A 250 ml Schlenk round bottom flask was fitted with a pressure-equalized dropping addition funnel and purged. Acetonitrile (50 ml, 946 mmol) was added to the flask. The funnel was charged with diisobutylaluminum hydride (100 ml, 1.0 M in toluene, 100 mmol) and the flask was cooled to 0°C. The diisobutylaluminum hydride was added dropwise over 30 minutes and stirred at 0°C for an additional hour. The flask was warmed to room temperature and the colorless solution was stirred overnight. The solvent was removed under vacuum leaving 18 g of a yellow liquid. This liquid was heated under nitrogen to 300°C over a period of 2 hours and held at 300°C for 6 hours to form Upon cooling, 10.6 g of a solid polymer were obtained. Example B A polysilazane was prepared as follows. A 5 liter, three-necked flask was equipped with an overhead mechanical stirrer, a dry ice/acetone condenser (-78°C), an ammonia/nitrogen inlet tube and a thermometer. The apparatus was sparged with nitrogen and then charged with hexane (1760 ml, dried over 4A molecular sieves), methyldichlorosilane (209 ml, 230.9 g, 2.0 mol) and vinylmethyldichlorosilane (64 ml, 69.6 g, 0.5 mol). The ammonia was added at a rate of 3.5 l/min (9.37 mol) for one hour. During the addition, the temperature of the reaction rose from 25°C to 69°C. After one hour, the ammonia flow was stopped and the reaction mixture cooled to room temperature. The reaction mixture was filtered on a glass-fritted funnel to remove the precipitated ammonium chloride. The hexane was removed from the filtrate under reduced pressure (28 mm Hg, 60°C) to give [(CH 3 SiHNH) 0.8 (CH 3 SiCH=CH 2 NH) 0.2 ] x as a clear oil (150.76 g, 2.34 mol, 95% yield). The oil had a viscosity of 43 cp at 25°C. Example C A polyureasilazane was prepared as described in U.S. Patent 4,929,704 by treating 1451.8 g of the polysilazane, [(CH 3 SiHNH) 0.8 (CH 3 SiCH=CH 2 NH) 0.2 ] x , prepared as described in Example B, with 6.62 ml phenylisocyanate and heating the mixture to 70°C for 1 hour. Example 1 A block copolymer was prepared by combining 10.0 g of the polysilazane, [(CH 3 SiHNH) 0.8 (CH 3 Si(CH=CH 2 )NH) 0.2 ] x , prepared as described in Example B, and 7.2 g of the aluminum-nitrogen polymer, prepared as described in Example A, and heating under nitrogen to 110°C for 5 hours. Isobutane was formed as a by-product of the reaction. The resulting block copolymer is an orange liquid. Example 2 A 6.0 g sample of the block copolymer of Example 1 was combined with 0.1 g dicumyl peroxide in a vial under nitrogen. The sample was heated to 150°C for 15 minutes to form a cured infusible solid. Example 3 A 1.0 g sample of the liquid block copolymer of Example 1 was combined with 0.02 g of azo(bis)isobutyronitrile (AIBN) in a vial under nitrogen. The sample was heated to 145°C for 30 minutes. The sample cured to a rigid solid. Example 4 A 1.13 g sample of the cured block copolymer of Example 2 was fired in a graphite boat from room temperature to 1600°C at 10°C/min in an argon atmosphere with a two hour hold at 1600°C. The resulting ceramic, 0.64 g, was shown by X-ray powder diffraction to be crystalline α-SiC/AlN. 2H α-SiC was the only SiC polytype detected. Example 5 A 1.0 g sample of the cured block copolymer of Example 2 was fired in an alumina boat in a mullite tube furnace from room temperature to 1000°C in ammonia and held for 2 hours at 1000°C. The atmosphere was then switched to nitrogen and the temperature was ramped to 1600°C at 10°C/min. The sample was held at 1600°C for 2 hours. The resulting ceramic was shown by X-ray diffraction to contain Si 3 N 4 , AlN and SiC. Example 6 A 1 g sample of the liquid block copolymer of Example 1 was filled with silicon carbide powder (0.5 g). Dicumyl peroxide (0.02 g, 2 wt. % based on polymer) was added and the mixture heated at 160°C under nitrogen for 5 minutes to form a rigid, cured solid piece. Example 7 A 0.5 g sample of the block copolymer of Example 1 was transferred under nitrogen to a quartz flask and mixed with 0.02 g of the UV curing agent alpha, alpha-dimethoxy-alpha-phenylacetophenone sold by Ciba-Geigy under the trade name IRGACURE 651. The flask was exposed to UV under a low pressure mercury lamp for 4 hours. A solid cured polymer formed. Example 8 A block copolymer was prepared by combining 10.0 g of the isocyanate-modified polysilazane prepared as in Example C, and 7.2 g of the alazane polymer, prepared as in Example A, and heating under nitrogen to 110°C for 4 hours. Isobutane is formed as a by-product of the reaction. The resulting block copolymer was an orange liquid. Example 9 A 2.1 g sample of the block copolymer of Example 8 was combined with 0.04 g (2 wt. %) dicumyl peroxide in a vial under nitrogen. The sample was heated to 150°C for 15 minutes to form a cured, infusible solid. Example 10 A 2.1 g sample of the liquid block copolymer of Example 8 was combined with 0.04 g of AIBN (azo(bis)isobutyronitrile) in a vial under a flow of nitrogen. The sample was heated to 150°C for 30 minutes. The sample cured to a rigid solid. Example 11 A 0.5 g sample of the block copolymer of Example 8 was transferred under nitrogen to a quartz flask and mixed with 0.02 g of the UV curing agent alpha, alpha-dimethoxy-alpha-phenylacetophenone sold by Ciba-Geigy under the trade name IRGACURE 651. The flask was exposed to UV under a low pressure mercury lamp for 4 hours. A solid cured polymer was obtained. Example 12 A 1.0 g sample of the cured block copolymer of Example 9, was fired in an alumina boat from room temperature to 1500°C at 10°C/min in an argon atmosphere with a two hour hold at 1500°C. The resulting ceramic, 0.23 g, was shown by X-ray powder diffraction to be crystalline α-SiC/AlN. 2H α-SiC was the only SiC polytype detected. Example 13 A 2.0 g sample of the liquid block copolymer of Example 8 was filled with silicon carbide powder (1.0 g). Dicumyl peroxide (0.04 g, 2 wt. % based on polymer) was added and the mixture heated at 160°C under nitrogen for 5 minutes to form a rigid cured solid piece. Example 14 This example demonstrates that a block copolymer is formed by the reaction of a polysilazane and an aluminum-nitrogen polymer. Deuterated polysilazane, with deuterium labels on the nitrogen atoms, was prepared according to the method of Example B by using a 500 ml three-necked flask equipped with a magnetic stir bar, a dry ice/isopropanol condenser (-78°C), an ammonia/nitrogen inlet tube and a thermometer. The apparatus was sparged with nitrogen and then charged with hexane (175 ml, dried over 4A molecular sieves), methyldichlorosilane (5.5 ml, 0.053 mol) and vinylmethyldichlorosilane (1.69 ml, 0.013 mol). The solution was cooled to 0°C in an ice bath and d 3 -ammonia (5 l, 0.20 mol) was added over 30 minutes with stirring. The reaction mixture was filtered on a glass-fritted funnel to remove precipitated ammonium chloride. The hexane was removed under reduced pressure to give [(CH 3 SiHND) 0.8 (CH 3 Si(CH=CH 2 )ND) 0.2 ] x as a clear oil. The alazane (0.72 g), prepared as in Example A, was dissolved in 1.0 g of the deuterated polysilazane [(CH 3 SiHND) 0.8 (CH 3 Si(CH=CH 2 )ND) 0.2 ] x . A 0.5 g sample of this polymer mixture was transferred under argon to an oven-dried vial and sealed with a septum. The sample was heated to 110°C for 3.5 hours, then cooled to room temperature. The gas headspace was analyzed by gas chromatography/Fourier Transform infrared spectroscopy. d 1 -Isobutane was identified by comparison to known GC standards and by the observation of C-D stretching bands at 2160 cm -1 in the infrared spectrum. d 1 -Isobutane can only be obtained by reaction of a silazane Si-N-D group with an alazane Al-C 4 H 9 group, which forms C 4 H 9 D with concomitant Si-N-Al bond formation. Example 15 The liquid polysilazane [CH 3 Si(H)NH] x was prepared according to the method of Example B using methyldichlorosilane and ammonia. (1.4 g), prepared as in Example A, was dissolved in [CH 3 Si(H)NH] x (3.0 g). The polymer solution was heated to 200°C for 4 hours under nitrogen. Isobutane was formed as a by-product of the reaction. At 190°C the solution viscosity began to increase, ultimately resulting in a solid block copolymer that contained no unsaturated organic groups. Example 16 The solid block copolymer of Example 15 (1.0 g) was fired in a mullite tube furnace under an argon atmosphere in an alumina boat from room temperature to 1500°C at 5°C/minute. The sample was held two hours at 1500°C and 0.89 g of fired product was isolated. X-ray powder diffraction of the fired product showed α-SiC and AlN as the only crystalline products. Example 17 A block copolymer was prepared by combining 6.4 g of the polysilazane, [(CH 3 SiHNH) 0.8 (CH 3 Si(CH=CH 2 )NH) 0.2 ] x , prepared as described in Example B and 3.8 g of the aluminum-nitrogen polymer, prepared as described in Example A, and heating under nitrogen to 110°C for 4 hours. Isobutane was formed as a by-product of the reaction. A spin dope was prepared by mixing 0.3 g of the block copolymer with 0.01 g of dicumyl peroxide. Fibers were drawn from the spin dope, heated to 180°C in nitrogen to crosslink the fiber to establish dimensional stability and then fired to 1500°C at 10°C/minute in an argon atmosphere. The fibers retained their shape on firing. X-ray powder diffraction of the fixed fibers showed α-SiC and AlN as the only crystalline phases.

Claims: A polymeric aluminum nitride/silicon carbide ceramic precursor characterized in that it comprises a multiplicity of blocks of units having the formula: and a multiplicity of blocks of units having the formula: or wherein x >1 and y >1; the blocks x and y are bonded through Si-N-Al linkages; and R 1 and R 2 are the same or different and are selected from the group consisting of hydrogen, substituted or unsubstituted 1-12 carbon alkyl, 3-12 carbon cycloalkyl, 2-12 carbon alkenyl, 3-12 carbon cycloalkenyl, and aryl groups; R 3 , R 4 and R 5 are the same or different and are selected from the group consisting of hydrogen, substituted or unsubstituted 1-6 carbon alkyl, 3-6 carbon cycloalkyl, 3-6 carbon cycloalkenyl, 2-6 carbon alkenyl, 2-6 carbon alkynyl, and aryl groups, provided that R 1 , R 2 , R 3 , R 4 and R 5 are not all hydrogen, and A is O or S. A process for preparing the polymeric ceramic precursor of claim 1 characterized by reacting a polymer having a backbone comprising alternating aluminum- and nitrogen-containing groups containing Al-C or Al-H bonds with a silazane or (thio)ureasilazane polymer containing N-H bonds at a temperature not greater than 400°C. The process of claim 2, further characterized in that the temperature is 90°C to 220°C. Use of the polymeric ceramic precursor of claim 1 to prepare a crosslinked block copolymer characterized by supplying energy to generate free radicals to the polymeric ceramic precursor of claim 1, wherein at least one of R 1 , R 2 , R 3 , R 4 and R 5 is an organounsaturated group. The use of claim 4, further characterized in that the organounsaturated group is a vinyl group. The use of claim 4, further characterized in that a free radical generator is also present and the energy that is supplied is heat. The use of claim 6, further characterized in that the free radical generator is a peroxide. The use of claim 6, further characterized in that the free radical generator is an azo compound. The use of claim 4, further characterized in that the energy that is supplied is UV radiation or electron beam radiation. The use of claim 4, further characterized in that the polymeric ceramic precursor is mixed with a filler prior to crosslinking. The use of claim 10, further characterized in that the filler is silicon carbide. The use of claim 10, further characterized in that the filler is aluminum nitride. Use of the crosslinked block copolymer of claims 4 to 12 to prepare an AlN/SiC-containing ceramic characterized by pyrolyzing the copolymer in a nonoxidizing atmosphere. Use of the crosslinked copolymer of claims 4 to 12 to prepare a fiber. The use of claim 14, further characterized by pyrolyzing the fiber to form a ceramic. The use of claim 15, further characterized in that the ceramic comprises SiC and AlN. The use of claim 16, further characterized in that the SiC and AlN are present as a solid solution.

Inventors: JENSEN JAMES ALLEN, JENSEN, JAMES ALLEN
Applicants: LANXIDE TECHNOLOGY CO LTD, LANXIDE TECHNOLOGY COMPANY, LP
Application year: 1993
Main classification: C08G79
IPC codes: C08G77, C04B35, C08L83, C01B31, C08G79, C01B21