Cross-linkable polymeric composition

Abstract: A cross-linkable polymeric casting composition including a fluorene diacrylate or dimethacrylate monomer; and a comonomer including a polymerisable double bond.

Description: The present invention relates to the manufacture of plastic optical articles such as video discs and ophthalmic lenses. The most widely used plastic ophthalmic lens material is polymerised diethylene glycol bis (allyl carbonate). This polymer has proved a satisfactory material for the manufacture of ophthalmic lenses because of a combination of features, including excellent transmission, resistance to discolouration, high strength and high impact resistance. The material has a reasonable abrasion resistance and can be coated to improve that resistance. Fluorene acrylates and methacrylates are specialty resins used in electronic applications. In Australian Patent 601,779, applicant describes a cross-linkable casting composition including at least polyoxyalkylene glycol diacrylate or dimethacrylate and at least one poly functional unsaturated cross-linking agent. Whilst the lenses produced from the prior art compositions provide advances in the art, difficulties may be encountered in certain applications. For example, difficulties may be encountered in some patients in fitting lenses made from such compositions. Eye discomfort, including eye fatigue problems, may be encountered. Moreover, such lenses have been found to be cosmetically unattractive. Further in Australian Patent Application 75160/91, applicant describes a polyoxy alkylene glycol diacrylate or dimethacrylate; a monomer including a recurring unit derived from at least one radical-polymerisable bisphenol monomer capable of forming a homopolymer having a high refractive index of more than 1.55; and a urethane monomer having 2 to 6 terminal groups selected from a group comprising acrylic and methacrylic groups. Japanese Patent Application 244680 of 1989 to NEC Corporation discloses a resin composition including a fluorene epoxy acrylate prepolymer which may be used in the formation of electronic and optical parts. EP-A-0421086 discloses photosensitive epoxy acrylate resins for use in the manufacture of printed circuit boards. JP-A-4325508 discloses a plastic lens material which comprises a copolymer of radically polymerisable monomers and which has a refractive index of at least 1.60. To achieve a refractive index of at least 1.60, JP-A-4325508 teaches the use of fluorene dimethacrylate or acrylate as the main component, for example 75 wt%, in the material. Whilst particular polyoxyalkylene glycol diacrylates and dimethacrylates are taught to be useful comonomer units to increase the impact resistance of the resultant plastic lens, these are taught to be present as a minor ingredient, if at all. JP-A-3106918 discloses a UV-curable resin composition for lenses containing a copolymer of (meth)acrylic acid and di(hydroxy)-phenyl fluorene, (meth)acrylate ester and a photocurable agent. JP-A-4345608 discloses a material for protecting LCD colour filter containing polyfunctional ethylenically unsaturated compounds, photopolymerisation initiators and bis: (meth)acrylate fluorene compounds. Whilst optical articles formed from such compositions exhibit improved refractive index, certain high refractive index monomers used may exhibit unacceptable smell, toxicity, brittleness or low softening temperatures. Accordingly, it is an aim of the present invention to overcome, or at least alleviate, one or more of the difficulties related to the prior art. Accordingly, the present invention provides a cross-linkable polymeric casting composition suitable for use in the formation of an optical article having a refractive index in the range of 1.51 to 1.60 including 5 to 30% by weight based on the total weight of the casting composition of a fluorene diacrylate or dimethacrylate monomer selected from monomers of the general formula wherein R 1 = H or alkyl, R 2 = H or alkyl, X = H or OH m and n are integers provided that the sum of m and n is from 0 to 4; 5 to 60% by weight of a polyoxyalkylene glycol diacrylate or dimethacrylate; and at least one comonomer selected from the group consisting of 2.5% to 25% by weight of a urethane monomer having 2 to 6 terminal acrylic and/or methacrylic groups; 5 to 45% by weight of a polyfunctional unsaturated cross-linking agent selected from the group consisting of tri- and tetrafunctional vinyls, and acrylic and methacrylic monomers; 10 to 60% by weight of a bisphenol monomer selected from the group consisting of dimethacrylate and diacrylate esters of bisphenol A, dimethacrylate and diacrylate esters of 4,4'bishydroxy-ethoxy-bisphenol A and mixtures thereof; and 5 to 40% by weight of a thiodiacrylate or thiodimethacrylate; or mixtures thereof. The crosslinkable polymeric casting composition according to the present invention may be utilised in the preparation of an optical article. The presence of the fluorene structure provides high refractive index plus good all round properties such as heat stability, abrasion resistance and impact strength. This may be achieved without the usual negative features of high index monomers such as smell, toxicity, brittleness or low softening temperatures. By the term "high refractive index", as used herein, we mean a polymer having a refractive index of at least approximately 1.55, preferably 1.57 more preferably 1.60 or higher. The fluorene diacrylate or dimethacrylate is of the general formula wherein R 1 = H or alkyl, preferably CH 3 R 2 = H or alkyl, preferably CH 3 X = H or OH m and n are integers provided that the sum of m and n is from 0 to 4 The fluorene monomer may be selected from a bisphenol fluorene dihydroxyacrylate (BFHA) or a bisphenol fluorene dimethacrylate (BFMA) or mixtures thereof. The fluorene diacrylate or dimethacrylate monomer may be present in an amount suitable to provide a casting composition having a viscosity of not greater than approximately 300 mPas (300 cps) at 25°C. The fluorene diacrylate or dimethacrylate monomer is present in amounts of from 5 to 30% by weight, based on the total weight of the casting composition. The polymerisable comonomer may be selected to improve the properties and/or processability of the cross-linkable polymeric casting composition. The thiodiacrylate or dimethacrylates may be selected from bis(4-methacryloylthioethyl)sulfide (BMTES) and bis(4-methacryloylthiophenyl)sulfide (BMTS or TS). When present, the thiodiacrylate is present in amounts of from approximately 5 to 40% by weight, preferably 20 to 40% by weight. The polyoxy alkylene glycol diacrylate or dimethacrylate compound according to the present invention may include ethylene oxide or propylene oxide repeating units in its backbone. A polyethylene glycol dimethacrylate is preferred. One suitable material is that sold under the trade name NKESTER 9G (RTM) by Shin Nakamura. Alternatively, an NK Ester (RTM) 6G, 4G or 14G may be used. The polyoxy alkylene glycol diacrylate or dimethacrylate component is present in amounts of from approximately 5% by weight to 60% by weight based on the total weight of the casting composition. The diacrylate or dimethacrylate component is preferably present in amounts of approximately 15% by weight to 55% by weight, more preferably 20 to 45% by weight. When present, the high index bisphenol monomer component in the cross-linkable casting composition is selected from: dimethacrylate and diacrylate esters of bisphenol A; dimethacrylate and diacrylate esters of 4,4'bishydroxyethoxy-bisphenol A and mixtures thereof. A preferred high index bisphenol compound is a bisphenol A ethoxylated dimethacrylate. A bisphenol A ethoxylated dimethacrylate sold under the trade designation ATM20 (RTM) by Ancomer or Bis GMA (RTM) by Freeman Chemicals have been found to be suitable. Halogenated high index bisphenol compounds which may be used include those sold under the trade designation and NK Ester 534M (RTM) by Shin Nakamura. When present, the high index bisphenol monomer is present in amounts of from approximately 10 to 60% by weight, preferably 20 to 55% by weight, based on the total weight of the casting composition. As stated above, the cross-linkable polymeric casting composition may include a urethane monomer having 2 to 6 terminal acrylic and/or methacrylic groups. Suitable materials falling within this definition include materials supplied under the trade names U-4H, U-4HA and U-6HA (RTMs) by Shin Nakamura, NF-201 and NF-202 (RTMs) by Mitsubishi Rayon. These monomers are included to improve physical toughness without causing the lens material to become too brittle. Impact resistance is improved without adversely affecting abrasion resistance. The urethane monomer may be present in any suitable amount to provide a desired level of hardness. When present, the urethane monomer is present in amounts of from 2.5% to 25% by weight, preferably 5% to 20% by weight, based on the total weight of the casting composition. The cross-linkable polymeric coating composition may include at least one poly-functional unsaturated cross-linking agent. The poly-functional unsaturated cross-linking agent according to the present invention is selected from the group consisting of tri-or-tetra- function vinyls, and acrylic or methacrylic monomers. The cross-linking agent may be a short chain monomer for example trimethylol propane trimethacrylate, pentaerythritol triacrylate or tetracrylate. Other polyfunctional cross-linking agents which may be used include NK Ester TMPT, NK Ester A-TMPT, NK Ester A-TMM-3, NK Ester A-TMMT (RTMs) ditrimethylol propane tetracrylate, trimethylolpropane triacrylate, pentaerythritrol tetramethacrylate, dipentaerythritol monohydroxypenta acrylate, pentaerythritol triacrylate, ethoxylated trimethylolpropane triacrylate, ethoxylated trimethylol- propane trimethacrylate. A material sold under the trade name SR-454 which is an ethoxylated trimethylol propane triacrylate has been found to be suitable. When present, the polyfunctional unsaturated cross-linking agent is present in amounts of from 5 to 45% by weight, preferably 30 to 40% by weight based on the total weight of the casting composition. The cross-linkable casting composition may further include a coreactant including a polythiol. The polythiol may be selected from the group consisting of (a) Pentaerythritol Tetrakis (3-mercapto-propionate) [PTMP] (b) Trimethylolpropane Tris (3-mercaptopropionate) [TTMP] (c) 4-mercaptomethyl-3,6-dithia-1,8-octanedithiol [MDO] (d) Pentaerythritol Tetrakis (3-mercaptoacetate) [PTMA] (e) Trimethylolpropane Tris (3-mercaptoacetate) [TTMA] (f) 4-t-butyl-1,2-benzenedithiol (g) 2-mercaptoethylsulfide HSCH 2 CH 2 SCH 2 CH 2 SH (h) 4,4'-thiodibenzenethiol (i) benzenedithiol (j) Glycol Dimercaptoacetate (k) Glycol Dimercaptopropionate Ethylene bis(3-Mercaptopropionate) (l) Polyethylene Glycol Dimercaptoacetates (m) Polyethylene Glycol Di(3-Mercaptopropionates) The thiol compound may be present in amounts from 0 to approximately 50% by weight. The cross-linkable casting composition according to the present invention may further include an initiator. The initiator may be a heat and/or ultraviolet (U.V.) initiator. The compositions are preferably cured by a combination of UV radiation and heat. The combination of UV radiation and heat may reduce the possibility of incomplete curing for example due to the phenomenon known as "radical trapping". The composition, with the addition of approximately 0.2 to 2.0% by weight of cross-linking initiator may be exposed to UV radiation for between 0.5 and 10 seconds. Any commercially viable UV curing system may be used. We have used a Fusion System with microwave driven lamps. A number of fusion bulbs with different output Spectra may be considered. Presently we prefer the "D" bulb and the "V" bulb. One source we have found satisfactory is a 25cm, 120 watt/cm [10 inch, 300 watt/inch] mercury lamp. The mould assembly is then heated to 100°C for one hour or the lens may be removed from the assembly and heated in air for about one hour at 100°C. This means that fully cured lenses can be manufactured, if desired, in about one hour. Heat curing can also be used without any use of U.V. radiation. Typically 2 - 4 passes under the UV lamps plus an hour of heat treatment at 100°C completes the cure. Any suitable UV initiator may be used. An initiator available under the trade designation Irgacure 184 has been found to be satisfactory. More than one curing agent may be present. It has been possible to operate with a relatively low level of initiator of between approximately 0.05 and 0.25% by weight. A range of photoinitiators available commercially can be used, depending on sample thickness, type of UV lamp used and the absorption wavelength of the monomer mix. The following photoinitiators (which are sold under the given RTMs) have been found to be suitable. Alcolac Vicure 10 - isobutyl benzoin ether Alcolac Vicure 30 - isopropyl benzoin ether Alcolac Vicure 55 (V55) - methyl phenyl glyoxylate Cyracure UV1-6974 (cationic photoinitiator) Triaryl sulfonium hexafluoroantimonate Lucirin TPO (radical photoinitiator) 2,4,6-Trimethylbenzoyldiphenylphosphine oxide Vicure 55 (radical photoinitiator) methyl phenylglyoxylate benzoic acid Initiator may be a single component or combination of initiator components. Additionally, combination of photoiniator mixtures or photoinitiator mixtures with a heat induced free radical initiator such as peroxides, peroxypercarbonates or an azo compound may also be employed. As an alternative to photo curing a heat curing initiator may be used, for example 1,1 di-tert butyl peroxy -3,3,5- trimethylcyclohexane or secondary isopropyl percarbonate. Other additives may be present which are conventionally used in casting compositions such as inhibitors, dyes, UV stabilisers and materials capable of modifying refractive index. Mould release agents can be added but they are in general not required with the compositions used in the method of the present invention. Such additives (which were sold udner the given RTMs) UV Absorbers including Ciba Geigy Tinuvin P - 2(2'-hydroxy-5'methyl phenyl) benzotriazole Cyanamid Cyasorb UV 531 -2-hydroxy-4-n-octoxybenzophenone Cyanamid Cyasorb UV5411-2(2-hydroxy-5-t-octylphenyl)-benzotriazole Cyanamid UV 2098 - 2-hydroxy-4-(2-acryloyloxyethoxy) benzophenone National Starch and Chemicals Permasorb MA - 2 hydroxy-4-(2 - hydroxy-3- methacryloxy)propoxy benzophenone Cyanamid UV24 - 2,2'-dihydroxy-4-methoxybenzophenone BASF UVINUL 400 - 2,4 dihydroxy-benzophenone BASF UVINUL D-49 - 2,2'-dihydroxy-4,4' dimethoxybenzophenone BASF UVINUL D-50 - 2,2', 4,4' tetrahydroxy benzophenone BASF UVINUL D-35-ethyl-2-cyano-3,3-diphenyl acrylate BASF UNINYL N-539-2-ethexyl-2-cyano-3,3-diphenyl acrylate Ciba Geigy Tinuvin 213 Hindered amine light stabilizers (HALS), including Ciba Geigy Tinuvin 765/292 - bis (1,2,2,6,6-pentamethyl-4-piperidyl)sebacate Ciba Geigy 770 - bis (2,2,6,6-tetramethyl-4-piperidinyl) sebacate Antioxidants including Ciba Geigy Irganox 245 - triethylene glycol-bis-3-(3-tertbutyl-4-hydroxy-5-methyl phenyl)propionate Irganox 1010 -2,2-bis[[3-[3,4-bis(1,1-dimethylethyl)-4-hydroxyphenyl]-1-oxopropoxy]methyl]-1,3-propanediyl 3,5-bis(1,1-dimethyl ethyl)-4-hydroxy benzene propanoate Irganox 1076 - octadecyl 3-(3',5'-di-tert-butyl(-4'-hydroxyphenyl) propionate Anticolouring agents including Triphenyl phosphine 9, 10 dihydro-9-oxa-10-phosphaphenanthrene-1-oxide Cure modifiers including Dodecyl mercaptan Butyl mercaptan Thiophenol Nofmer from Nippon Oils and Fats Q1301 from Waco Other monomeric additives can be present in amounts up to 10% by weight as diluents, and include monomers such as methacrylic acid, vinyl silanes, methyl allyl, hydroxy ethyl, methacrylate. Other monomeric additives may be included to improve processing and/or material properties, these include: methacrylic acid, maleic anhydride, acrylic acid adhesion promoters/modifiers such as Sartomer 9008, Sartomer 9013, Sartomer 9015 etc. dye-enhancing, pH-adjusting monomers like Alcolac SIPOMER 2MIM a charge-reducing cationic monomer to render the material more antistatic, example Sipomer Q5-80 or Q9-75 hydrophobic comonomers: Shin Nakamura NPG, P9-G etc. to reduce the water adsorption of the material viscosity modifiers Accordingly, in a preferred aspect of the present invention the cross-linkable polymeric casting composition may further include at least one aliphatic glycol dimethacrylate or diacrylate. The aliphatic glycol dimethacrylate or diacrylate may function to reduce the viscosity of the composition and thus improve the processing characteristics of the composition. An ethylene, propylene, butylene or pentylene diacrylate or methacrylate may be used. A butylene glycol dimethacrylate is preferred. One suitable material is that sold under the trade designation NK ester BD (RTM) by Shin Nakamura. A neopentyl glycol dimethactylate may be used. One suitable material is that sold under the trade designation NK ester NPG (RTM) by Shin Nakamura. The aliphatic glycol dimethacrylate or diacrylate may be present in amounts of 1 to 10% by weight, preferably 2.5 to 5% by weight based on the total weight of the casting composition. In a further aspect of the present invention there is provided a polymeric article formed from a cross linkable casting composition as described above. The polymeric article may be an optical article. The optical article may provide characteristics equal to or greater than those achievable with articles made from diethylene glycol bis(allyl carbonate) but with a considerably reduced cure time and substantially increased throughput. The optical article may be further characterised by having an increased refractive index without degrading other important lens properties such as density, abrasion, impact, colour, and rigidity (hardness and heat resistance). The overall refractive index may be in the mid to high refractive index range of from approximately 1.51 to 1.59, preferably 1.53 to 1.57. The optical articles prepared by the method of this invention include camera lenses, ophthalmic lenses and video discs. The casting composition may be formed into a suitable article by mixing in a convenient vessel the components making up the material, and then adding the curing catalyst and/or photo-initiator. The mixed material is then degassed or filtered. As the curing time is substantially reduced the casting process may be undertaken on a continuous or semi-continuous basis. The present invention will now be more fully described with reference to the accompanying examples. EXAMPLE 1 A cross-linkable casting composition having the following components was prepared % by weight 9G (polyethylene glycol dimethacrylate) 45% SR-454 (ethoxylated trimethyl propanetriacrylate) 35% U4HA (urethane tetracrylate) 15% BFHA (bisphenolfluorene dihydroxyacrylate) 5% The monomer mix was prepared in a beaker together with 0.2% V55 as the U.V. initiator. The casting material was used to fill the space between a pair of glass moulds separated by a plastic gasket at their periphery. The mould was then passed 4 times under a U.V. lamp. This was followed by a 1 hour extended cure at 100°C. EXAMPLES 2 - 13 Example 1 was repeated under similar conditions with monomer mixes as designated in Table 1 below. The results achieved are also given in Table 1. Satisfactory lenses were achieved in Examples 1, 3, 4, 5, 8, 9, 10, 12, 13 and 14. Examples of Using BFHA as a Casting Material Ex. Casting Material S.G. R.I. Impact Y.I. Taber Abrasion Barcol Hard. 1. 9G/S454/ U4HA/BFHA 45/35/15/5 1.23 1.512 Good 1.0 Good 19 2. 9G/S454/U4HA 45/35/20 (Comparative) 1.23 1.507 Good 1.0 Good 17 3. 9G/S454/ U4HA/BFHA 45/35/10/10 1.23 1.517 Good 1.0 Good 20 4. 9G/S454/ U4HA/BFHA 45/35/5/15 1.23 1.522 Good 0.9 Good 17 5. 9G/S454/BFHA 45/35/20 1.23 1.529 Good 1.0 Good 15 6. 9G/U4HA/ATM20 45/5/50 (Comparative) 1.21 1.537 Good 1.0 Good 23 7. 9G/U4HA/ATM20 35/5/60 (Comparative) 1.11 1.543 Poor 1.4 Poor 28 8. 9G/U4HA/ ATM20/BFHA 45/5/40/10 1.22 1.542 Good 1.0 Good 24 9. 9G/U4HA/ ATM20/BFHA 45/5/30/20 1.23 1.549 Good 1.1 Good 25 10. 9G/U4H4/ ATM20/BFHA 45/5/20/30 1.23 1.554 Good 1.1 Good 27 11. 9G/TS/S454/ ATM20 20/30/10/40 (Comparative) 1.24 1.564 Good 2.1 Good 35 12. 9G/TS/S454/ ATM20/BFHA 20/30/10/30/10 1.24 1.570 Good 2.1 Good 38 13. 9G/TS/S454/ ATM20/BFHA 20/30/10/20/20 1.25 1.576 Good 2.1 Good 40 14. 9G/TS/S454/ ATM20/BFHA 20/30/10/10/30 1.25 1.582 Good 2.1 Good 42 DESCRIPTION OF TESTS Taber Apparatus used to assess the abrasion resistance of lens materials. It involves the use of an abrasive wheel rubbed across a lens surface. Degree of abrasion is assessed according to the level of haze induced by wear. Barcol Hardness Measure of the hardness of a lens material. A fixed force is applied to a needle point. The depth of penetration indicates the degree of hardness. Yellowness Index A measure of the degree of yellowness as assessed by the Gardiner Colorimeter Model XL835. Examples 1, 3, 4 and 5 should be compared with Example 2 showing how RI can be improved by using BFHA. Similarly, Examples 8, 9 and 10 should be compared with Example 7, and Examples 12, 13 and 14 should be compared with Example 11. Refractive Index (R.I.) This is measured on the Abbe Refractometer. Specific Gravity (S.G.) This is measured by weighing the material in air and water, and applying Archimede's Principle. Impact Strength This is determined by a drop-ball method according to ANSI standards. Abbreviations 9G polyethylene glycol dimethacrylate SR-454 ethoxylated trimethyl propanetriacrylate U4HA urethane tetracrylate BFHA bisphenolfluorene dihydroxyacrylate ATM20 bisphenol A ethoxylated dimethacrylate TS bis(4-methacryloylthiophenyl)sulfide

Claims: A cross-linkable polymeric casting composition suitable for use in the formation of an optical article having a refractive index in the range of 1.51 to 1.60 including 5 to 30% by weight based on the total weight of the casting composition of a fluorene diacrylate or dimethacrylate monomer selected from monomers of the general formula wherein R 1 = H or alkyl, R 2 = H or alkyl, X = H or OH m and n are integers provided that the sum of m and n is from 0 to 4; 5 to 60% by weight of a polyoxyalkylene glycol diacrylate or dimethacrylate; and at least one comonomer selected from the group consisting of 2.5% to 25% by weight of a urethane monomer having 2 to 6 terminal acrylic and/or methacrylic groups; 5 to 45% by weight of a polyfunctional unsaturated cross-linking agent selected from the group consisting of tri- and tetrafunctional vinyls, and acrylic and methacrylic monomers; 10 to 60% by weight of a bisphenol monomer selected from the group consisting of dimethacrylate and diacrylate esters of bisphenol A, dimethacrylate and diacrylate esters of 4,4'bishydroxy-ethoxy-bisphenol A and mixtures thereof; and 5 to 40% by weight of a thiodiacrylate or thiodimethacrylate; or mixtures thereof. A casting composition according to claim 1, wherein the polyoxyalkylene glycol diacrylate or dimethacrylate is present in an amount of from 20 to 60% by weight of the casting composition. A casting composition according to claim 1 or claim 2, wherein the composition is suitable for use in the formation of an optical article having a refractive index in the range of 1.55 to 1.60. A casting composition according to any one of claims 1, 2 and 3, wherein the fluorene monomer is selected from a bisphenol fluorene dihydroxyacrylate (BFHA) or a bisphenol fluorene dimethacrylate (BFMA) or mixtures thereof. A casting composition according to any one of the preceding claims, wherein the polyoxyalkylene glycol diacrylate or dimethacrylate compound is a polyethylene glycol dimethacrylate. A casting composition according to any one of the preceding claims wherein the urethane monomer is a tetracrylic urethane monomer. A casting composition according to any one of claims 1 to 5 wherein the cross-linking agent is an ethoxylated trimethylol propane triacrylate. A casting composition according to any one of claims 1 to 5 wherein the bisphenol compound is a bisphenol A ethoxylated dimethacrylate. A casting composition according to any one of claims 1 to 5 wherein the thiodiacrylate or thiodimethacrylate is selected from bis(4-methacryloylthioethyl)sulfide (BMTES) and bis(4-methacryloylthiophenyl)sulfide (BMTS or TS). A casting composition according to any one of the preceding claims further including a coreactant including a polythiol selected from the group consisting of (a) Pentaerythritol Tetrakis (3-mercapto-propionate) [PTMP] (b) Trimethylolpropane Tris (3-mercaptopropionate) [TTMP] (c) 4-mercaptomethyl-3,6-dithia-1,8-octanedithiol [MDO] (d) Pentaerythritol Tetrakis (3-mercaptoacetate) [PTMA] (e) Trimethylolpropane Tris (3-mercaptoacetate) [TTMA] (f) 4-t-butyl-1,2-benzenedithiol (g) 2-mercaptoethylsulfide HSCH 2 CH 2 SCH 2 CH 2 SH (h) 4,4'-thiodibenzenethiol (i) benzenedithiol (j) Glycol Dimercaptoacetate (k) Glycol Dimercaptopropionate Ethylene bis(3-Mercaptopropionate) (l) Polyethylene glycol Dimercaptoacetates (m) Polyethylene Glycol Di(3-Mercaptopropionates) A casting composition according to claim 1 including 5 to 30% by weight, based on the total weight of the casting composition, of the fluorene diacrylate or dimethacrylate monomer; 20 to 45% by weight of a polyethylene glycol dimethacrylate; 5 to 20% by weight of a tetracrylic urethane monomer; and 10 to 40% by weight of an ethoxylated trimethylol propane triacrylate. A casting composition according to claim 1 including 5 to 30% by weight, based on the total weight of the casting composition, of the fluorene diacrylate or dimethacrylate monomer; 20 to 45% by weight of a polyethylene glycol dimethacrylate; 5 to 20% by weight of a tetracrylic urethane monomer; 20 to 55% by weight of a high index bisphenol A ethoxylated dimethacrylate. A casting composition according to claim 12 including 5 to 40% by weight of a thiodimethacrylate selected from bis (4-methacryloyl-thioethyl) sulfide (BMTES) and bis (4-methacryloyl-thiophenyl) sulfide (BMTS or TS). A polymeric optical article formed from a casting composition according to any one of claims 1 to 13 and having a refractive index in the range of 1.51 to 1.60.

Inventors: KOK CHONG MENG, TOH HUAN KIAK, KOK, CHONG MENG, TOH, HUAN KIAK
Applicants: SOLA INT HOLDINGS, SOLA INTERNATIONAL HOLDINGS, LTD.
Application year: 1993
Main classification: G02B1
IPC codes: C08F20, G02B1, C08F290, C08G75, C09D4