Polyolefin polymerization process, method of producing catalyst, and catalyst

Abstract: A process for preparing a polymerization catalyst useful for the polymerization of olefins is provided comprising contacting a metal dihalide compound wherein the metal is selected from Group 2 and Group 12 of the Periodic Table and a transition metal compound which is a hydrocarbyloxide of a transition metal selected from Group 4 and Group 5 to form a first catalyst component; contacting the first catalyst component with at least one organoaluminum precipitating agent, wherein at least at the commencement of this step, the temperature at which such contacting is carried out is greater than about 70°C to about 150°C to form a solid product, and contacting the solid product with an activating agent to form a catalyst. Other aspects of the invention provide a catalyst prepared by the above described method and a polymerization process employing the thus prepared catalyst.

Description: BACKGROUND OF THE INVENTION This invention relates to methods for the production and use of transition metal catalysts for the polymerization of 4-methyl-1-pentene. A process for preparing catalysts for the polymerization of olefins is described in EP-A 0 370 864. However, the process requires the use of a titanium compound comprising chlorine. A further process for preparing such polymerization catalyst is known from EP-A 0 430 154. The process comprises the steps of (a) forming a first component by reactants comprising a magnesium dihalide, a phenol, an alkylbenzoate, and a titanium tetrahydrocarbyloxide, (b) reacting said first component with an organoaluminum halide to produce a solid product, and contacting said solid product with an activating liquid under a pressure of at least 485 kPa. The temperature during step (b) is not significantly above 50 °C. Similarly, the process known from EP-A 0 164 596 is known to comprise a contacting step (b) at temperatures not above 70 °C. In the production of polyolefins, such as for example polyethylene, polypropylene, ethylene-butene copolymers, and polymethylpentene, an important aspect of the various processes and catalysts used to produce such polymers is the productivity. By productivity is meant the amount or yield of solid polymer that is obtained by employing a given quantity of catalyst. If the productivity is high enough, then the amount of catalyst residues contained in the polymer is low enough that the presence of the catalyst residues does not significantly affect the properties of the polymer and the polymer does not require additional processing to remove the catalyst residues. As those skilled in the art are aware, removal of catalyst residues from polymer is an expensive process and it is very desirable to employ a catalyst which provides sufficient productivity so that catalyst residue removal is not necessary. High productivities are also desirable in order to minimize catalyst costs. In the polymerization of propylene and higher olefins, it is desirable to produce isotactic polymer. Atactic polymer and low molecular weight polymer are soluble in the olefin monomer. High levels of the undesirable soluble polymer make operation of the polymerization reactor difficult if not impossible, especially for a continuous operation. Therefore, control of the amount of soluble polymer produced during polymerization is essential to a commercially viable process. Soluble polymer production in high productivity catalysts is a function of both catalyst preparation and polymerization conditions. The changes in polymerization conditions, to decrease soluble polymer formation, include either the addition of external modifiers to the polymerization cocatalyst system, or the reduction of polymerization temperature. Reducing the polymerization temperature has the adverse effect of reducing catalyst productivity. However, it would be desirable to develop new and improved catalysts and polymerization processes which provide relatively high catalyst productivities and lower soluble polymer levels. SUMMARY OF THE INVENTION An object of the present invention is to provide a process to produce olefin polymerization catalysts having high productivity. Another object of the present invention is to provide improved olefin polymerization catalysts that produce polymers of 4-methyl-1-pentene with reduced soluble polymer content. Another object is to provide an improved olefin polymerization process for producing isotactic polymeric 4-methyl-1-pentene. In accordance with one aspect of the present invention, a process preparing a catalyst is provided, which comprises contacting a magnesium dihalide, a titanium tetrahydrocarbyloxide, and a phenol to form a first catalyst component, contacting the first catalyst component with at least one organoaluminum precipitating agent to form a solid product, wherein, at least at the commencement of this step, the temperature at which such contacting is carried out is in the range of 85 to 145°C; and contacting the solid product with an activating agent to form a catalyst. The precipitating and activating agents are as defined in claim 1. In accordance with other aspects of the invention, a catalyst produced by the above described process and the use of such catalyst for the polymerization of 4-methyl-1-pentene are provided. The use of the catalyst in the polymerization process can optionally also employ a cocatalyst. DETAILED DESCRIPTION OF THE INVENTION As used herein, by the term "Periodic Table" is meant the Periodic Table of the Elements shown as the new IUPAC form on the inside front cover of Handbook of Chemistry and Physics , 70th Edition, CRC Press, Inc. (1990). Some suitable magnesium dihalide compounds include, for example, magnesium dichloride, magnesium dibromide, and magnesium diiodide. Magnesium dichloride is most preferred, because it is readily available and relatively inexpensive and has provided excellent results. The titanium tetrahydrocarbyloxides are used, because they produce excellent results and are readily available. Suitable titanium tetrahydrocarbyloxide compounds include those expressed by the general formula Ti(OR) 4 wherein each R is individually selected from an alkyl, cycloalkyl, aryl, alkaryl, and aralkyl hydrocarbon radical containing from 1 to 20 carbon atoms per radical and each R can be the same or different. Titanium tetrahydrocarbyloxides in which the hydrocarbyl radical contains from 1 to 10 carbon atoms per radical are most often employed, because they are more readily available. Suitable titanium tetrahydrocarbyloxides include, for example, titanium tetramethoxide, titanium dimethoxydiethoxide, titanium tetraethoxide, titanium tetra-n-butoxide, titanium tetrahexyloxide, titanium tetradecyloxide, titanium tetraeicosyloxide, titanium tetracyclohexyloxide, titanium tetrabenzyloxide, titanium tetra-p-tolyloxide, and titanium tetraphenoxide. Of the titanium tetrahydrocarbyloxides, titanium tetraalkoxides are preferred and titanium tetra-n-butoxide is particularly preferred because of the excellent results obtained employing this material. Titanium tetra-n-butoxide is also generally available at a reasonable cost. The molar ratio of the transition metal compound to the metal dihalide compounds can be selected over a relatively broad range. Generally the molar ratio is within the range of 0.1:1 to 10:1, preferably from 0.2:1 to 2:1. As a third starting material, a phenol is also employed in preparing the first catalyst component. Such a phenol includes substituted as well as unsubstituted phenolic compounds. Typical examples include phenol, o-methylphenol, m-methylphenol, p-methylphenol, 4-phenylphenol, o-fluorophenol, m-fluorophenol, p-fluorophenol, p-sec-butylphenol, p-ethylphenol, p-methoxyphenol, and mixtures thereof. The preferred phenols have 6 to 12 carbon atoms per molecule. Of those phenols, 4-phenylphenol is the most preferred. The molar ratio of the phenol employed relative to the transition metal compound can vary over a relatively broad range. Generally, the molar ratio is within a range of from 0.1:1 to 10:1 and preferably from 0.2:1 to 5:1. The magnesium dihalide compounds, the titanium compounds, and the phenol as above described, can be reacted in the presence of a liquid diluent or solvent, or when at least one of the reagents is in the liquid state during the reaction, the use of diluent can be omitted. The Mg-dihalide compound, the titanium tetrahydrocarbyloxy compound, and the phenol employed in the present invention are normally mixed together in a suitable dry (essential absence of water) diluent or solvent, which is essentially inert to these components and the product produced. By the term "inert" is meant that the diluent does not chemically react with the dissolved components such as to interfere with the formation of the product or the stability of the product once it is formed. Such diluents include, for example, n-pentane, n-hexane, n-heptane, methylcyclohexane, toluene, and xylenes. Aromatic solvents are preferred, because the solubility of the Mg- dihalide compound and of the titanium compounds is higher in aromatic solvents as compared to aliphatic solvents, particularly at low temperatures. Xylenes are most preferred. Generally, the amount of solvent or diluent employed can be selected over a broad range. Usually the amount of solvent or diluent is within the range of 1 to 100 ml per gram of Mg- dihalide compound, preferably from 20 to 100 ml per gram. Temperatures for contacting the magnesium dihalide compound, the phenol, and the titanium compound are generally within the range of from 0°C to 150°C and preferably from 10°C to 150°C. The contacting temperatures employed could be higher, if the pressure employed is above atmospheric pressure. The pressure employed during contacting of the magnesium dihalide, the phenol and the titanium compound does not appear to be a significant parameter and can vary broadly. Generally the pressure is within the range of 6900 to 6.900.000 Pa, preferably 6900 to 690.000 Pa (1 psi to 1000 psi, preferably 1 psi to 100 psi). Generally, the time required for contacting the magnesium dihalide, the phenol and the titanium compound is within the range of 5 minutes to 10 hours, although in most instances a time within the range of 15 minutes to 3 hours is sufficient. Following the contacting operation, the resulting solution can be filtered to remove any undissolved material or extraneous solid, if desired. In a preferred embodiment, water is employed in preparing the first catalyst component. Generally, 0.5 to 1.5 moles of water per mole of Mg- dihalide are employed. The organoaluminum precipitating agent contains a halogen radical and at least one hydrocarbyl radical, wherein the hydrocarbyl radical is selected from hydrocarbyl radicals selected from alkyl, cycloalkyl, aryl, alkaryl, and aralkyl hydrocarbon radicals containing 1 to 20 carbon atoms per radical. Typical examples include methylaluminum dibromide, ethylaluminum diiodide, dimethylaluminum chloride, diethylaluminum chloride, diisopropylaluminum chloride, diisobutylaluminum chloride, dodecylaluminum dibromide, dimethylaluminum bromide, methyl-p-propylaluminum bromide, di-n-octylaluminum bromide, dicyclohexylaluminum bromide, di-n-decylaluminum chloride, ethylisobutylaluminum chloride, diphenylaluminum chloride, dieicosylaluminum chloride, di-n-propylaluminum chloride, methylaluminum sesquibromide, ethylaluminum sesquiiodide, ethylaluminum sesquichloride, and mixtures thereof. Of these compounds, dialkylaluminum chlorides are preferred. Diethylaluminum chloride and ethylaluminum sesquichloride are readily available and have been employed with good results, and are especially preferred. It has been found that the type of organoaluminum precipitating agent employed in catalyst preparation can affect the production of undesirable soluble polymer during polymerization. Diethylaluminum chloride is especially preferred for reducing soluble polymer levels. The molar ratio of the titanium compound to the organoaluminum precipitating agent can be selected over a relatively broad range. Generally, the molar ratio is within a range of from 0.1:1 to 10:1 and preferably within a range of 0.1:1 to 3:1. A molar ratio within the latter range usually produces a catalyst which can be employed as an especially active 4-methyl-1-pentene polymerization catalyst. The contacting of the first catalyst component and the organoaluminum precipitating agent can be carried out either in the presence of a liquid diluent, or when at least one of the reagents is in the liquid state, in the absence of such diluent. Preferably, a liquid solution of the magnesium dihalide, the phenol and the titanium compound is contacted with a hydrocarbon solution of the organoaluminum precipitating agent. Diluents or solvents which can be employed in preparing the first catalyst component, as described above, are also suitable for contacting the first catalyst component and the organoaluminum precipitating agent. It has been found that maintaining a dispersion of inert gas, such as nitrogen or argon, most preferably nitrogen, improves mixing while contacting the first catalyst component and the precipitating agent. The dispersion also has the effect of reducing the amount soluble polymer formed during polymerization of olefins such as 4-methyl-1-pentene. The dispersion system is affixed to the feedstock inlet. The dispersion system comprises two concentric tubes which allow the organoaluminum feed to enter the reactor through one tube, while inert gas enters the reactor through the other tube. The dispersion system is located above the level of the liquid in the reactor. The flow of inert gas causes a turbulent region at the end of the tube which disperses the feed entering the reactor into small droplets. The flow rate of the inert gas can vary broadly. Generally the flow rate is in the range of 0.1 to 20 liters/minute, preferably in the range of 1 to 15 liters/minute, and most preferably in the range of 2 to 10 liters/minute. The temperature employed while contacting the first catalyst component and the organoaluminum precipitating agent is, at least at the commencement of this contacting step and most preferably maintained for the time indicated below, within the range of 85°C to 145°C. It has been found that when the catalyst is used in the polymerization of olefins such as 4-methyl-1-pentene, the temperature employed during the precipitation step of catalyst preparation can affect the amount of soluble polymer produced. The temperature employed is high enough to reduce the amount of soluble polymer produced, and has the additional effect of producing a fibrous catalyst as opposed to discrete particles. Heat is evolved when the first catalyst component and the organoaluminum precipitating agent are contacted and the contacting rate can be adjusted as required to preferably maintain the desired temperature. Additional cooling can also be employed in order to maintain a relatively constant temperature. It is noted that the order of addition is not important and either component can be added to the other. The pressure employed while contacting the first catalyst component and the organoaluminum precipitating agent can be selected over a broad range. Generally, the pressure is within the range of 6900 to 6.900.00 Pa, preferably 6900 to 690.000 Pa (1 psi to 1000 psi, preferably 1 psi to 100 psi). The first catalyst component is contacted with the organoaluminum precipitating agent for a sufficient time at the above mentioned temperature, generally within a range of 5 minutes to 10 hours, preferably from 15 minutes to 3 hours, to insure that contacting of the components is complete. Precipitation of the solid product produces a slurry. The slurry can be stirred or agitated during precipitation. It has been found that the precipitation efficiency can be improved, i.e. the amount of solid product is increased, by contacting the slurry containing the solid product with a hydrocarbon before contacting with the activating agent. Generally the hydrocarbon is an aliphatic compound containing from 4 to 12 carbon atoms such as for example, n-pentane, n-hexane, n-heptane, cyclohexane, octane, and decane. The preferred hydrocarbons are n-hexane and n-heptane. The conditions, i.e. temperature, pressure, and time, suitable for contacting the hydrocarbon and the slurry containing the solid product are the same as those suitable for contacting the first catalyst component and the organoaluminum precipitating agent. The amount of hydrocarbon employed can be selected over a broad range. Generally the amount of hydrocarbon is within the range of 1 to 100 g per g of organoaluminum precipitating agent, preferably from 5 to 80 g per g, and most preferably from 10 to 60 g per g. Thereafter the solid product can be recovered from the slurry by filtration or decantation. The solid product can then be washed with a suitable material, such as a hydrocarbon, to remove any soluble material which may be present. If the solid product is decanted, the slurry can be stored under dry nitrogen or the solid product can be dried and then stored under nitrogen. An ester can optionally be contacted with the first catalyst component or with the solid product after precipitation of such solid product. Esters that can be used include alkyl or aromatic esters of linear or cyclic carboxylic acids having from 2 to 20 carbon atoms. Examples of suitable esters include methyl formate, ethyl formate, methyl acetate, ethyl acetate, n-propyl acetate, n-butyl acetate, ethyl octanoate, n-butyl-eicosanoate, methyl anisate, methyl benzoate, ethyl benzoate, ethyl p-methoxybenzoate, methyl p-toluate, diethyl carbonate, dimethyl maleate, methyl ethyl carbonate, di-(3-methylbutyl)carbonate, diphenyl carbonate, ethyl toluate, ethyl p-butoxybenzoate, ethyl p-methoxybenzoate, butylbenzoate, ethyl o-chlorobenzoate, ethyl naphthenate, ethyl cyclohexanoate, ethyl pivalate, and mixtures thereof. The preferred esters are those having 8 to 12 carbon atoms per molecule. Ethyl benzoate is especially preferred for preparing a catalyst having high productivity and selectivity for the more desirable insoluble polymer product. The molar ratio of ester employed relative to the titanium tetrahydrocarbyloxide can vary from 0.1:1 to 5:1, preferably from 0.2:1 to 3:1. The activating agent comprises at least one halogen-containing compound of an element selected from Groups 4, 5, 14, and 15 of the Periodic Table capable of adding halogen to the catalyst. The activating agent compounds preferably comprise chlorine-containing compounds of silicon and titanium. The currently preferred activating agent comprises titanium tetrachloride and trichlorosilane. The ratio of the titanium tetrachloride to the trichlorosilane can vary over a wide range. It is currently preferred that the weight of titanium tetrachloride is greater than that of the trichlorosilane. In a currently most preferred embodiment, the activating agent is a mixture of titanium tetrachloride, trichlorosilane, and silicon tetrachloride. Here again, the relative amounts of the various components of the activating agent can vary, however, it is generally preferred that the trichlorosilane be employed in a greater weight basis than the silicon tetrachloride and that titanium tetrachloride be employed in a greater weight basis than the trichlorosilane. Typical values for the weight ratio of the titanium tetrachloride:trichlorosilane:silicon tetrachloride would be in the range of 3:2:1 to 5:4:1. While the weight ratio of the activating agent to the solid product can be selected over a relatively broad range, the weight ratio of the activating agent to the solid product is generally within a range of 0.1:1 to 100:1 and preferably from 0.5:1 to 60:1. Following the treatment of the solid product with the activating agent, the surplus activating agent can be removed by washing the solid catalyst with a dry (essential absence of water) liquid such as a hydrocarbon of the type previously discussed, n-hexane, or xylene for example. The thus activated catalyst can be stored under an inert atmosphere such as dry nitrogen. Generally the reaction of the solid product and the activating agent can be carried out neat or in a liquid medium in which the activating agent is soluble. Any suitable diluent can be employed. Examples include normally liquid hydrocarbons such as n-pentane, n-hexane, n-heptane, cyclohexane, benzene, and xylene. The temperature employed in contacting the solid product and the activating agent can be selected over a relatively broad range, generally in the range of 0°C to 150°C, preferably 20°C to 120°C. In a preferred embodiment, the activation is carried out at a pressure of at least 480 kPa (70 psi). A particularly effective pressure range would be 480 to 655 kPa (about 70 psi to about 95 psi), or more preferably 585 to 655 kPa (85 psi to 95 psi). The contacting time of the solid product and the activating agent can be selected over a broad range and generally is within the range of 10 minutes to 10 hours, preferably from 15 minutes to 3 hours. It is noted that the order of addition is not important and either component can be added to the other. If desired, the catalyst can be admixed with a particulate diluent such as, for example, silica, silica-alumina, silica-titania, magnesium dichloride, magnesium oxide, polyethylene, polypropylene, or poly(phenylene sulfide), prior to using the catalyst in a polymerization process. While the weight ratio of the particulate diluent to catalyst can be selected over a relatively wide range, the weight ratio of particulate diluent to catalyst generally is within the range of 100:1 to 1:100. More often, the weight ratio of particulate diluent to catalyst is within the range of 20:1 to 2:1 and use of a particulate diluent can facilitate charging of the catalyst to the reactor. The present catalysts are particularly useful for the polymerization of 4-methyl-1-pentene and are especially well suited for producing isotactic polymethylpentene, providing high productivity as well as low soluble polymer formation. While it may not be necessary in all instances to employ a cocatalyst with the catalyst of the present invention, the use of cocatalysts is recommended for best results. The cocatalysts suitable for use in accordance with the invention can be selected from among the hydrides and organometallic compounds of metals of Groups 1, 2, 12, and 13 of the Periodic Table. Some typical examples include lithium alkyls, Grignard reagents, dialkyl magnesium compounds, dialkyl zinc compounds, and organoaluminum compounds. Of the organometallic cocatalysts, organoaluminum compounds are preferred, with the most preferred organoaluminum cocatalysts being compounds of the formula R' 3 Al, wherein each R' is individually selected from hydrocarbyl radicals containing 1 to 20 carbon atoms per radical. Typical examples include, trimethylaluminum, triethylaluminum, triisopropylaluminum, tridecylaluminum, trieicosylaluminum, tricyclohexylaluminum, triphenylaluminum, and 2-methylpentyldiethylaluminum. Triethylaluminum is preferred since this compound has produced excellent results. The molar ratio of the organometallic compound of the cocatalyst to the titanium compound of the first catalyst component is not particularly critical and can be selected over a relatively broad range. Generally, it is within a range of 1500:1 to 1:100, preferably from 200:1 to 1:10. For catalyst systems wherein the cocatalyst comprises at least one organoaluminum compound, typically there is employed 0.25 to 15 mg of the titanium-containing catalyst per millimole of organoaluminum cocatalyst. In some cases it may be desirable to use a multi-component cocatalyst system comprising triethylaluminum and either aromatic esters such as ethylanisate, ethylbenzoate and methyl-p-toluate; or silanes such as diphenyl dimethoxysilane, triphenyl ethoxysilane, and methyl triethoxysilane. In general, the catalyst of this invention can be used with the same types of cocatalyst systems and in the same manner as disclosed in U.S. Pat. Nos. 4,588,703, 4,394,291, and 4,477,588. The use of the catalyst prepared polymerisation according to the present invention in the polymerization can be in a solution phase process, in the presence or absence of an inert hydrocarbon diluent, in a particle form process, or in a gas phase process. The polymerization process employing the catalysts and cocatalysts as above described can be performed either batchwise or continuously. In a batch process, for example, a stirred autoclave is prepared for use by first purging with an inert gas such as nitrogen and then with a suitable compound, such as isobutane for example. When the catalyst and cocatalyst are employed, either can be charged to the reactor first or they can be charged simultaneously through an entry port under an isobutane purge. After closing the entry port, hydrogen, if used, is added, and then a diluent, if used, is added to the reactor. The reactor is heated to the desired reaction temperature, which for polymerizing 4-methyl-1-pentene is generally within a range of 20°C to 120°C and the monomer is then admitted and maintained at a partial pressure within a range of 135 to 5105 kPa (about 5 psig to about 725 psig) for best results. At the end of the designated reaction period, the polymerization reaction is terminated and the unreacted olefin and diluent can be vented. The polymer can then be collected as a free-flowing white solid and dried to obtain the product. In a continuous process, for example, a suitable reactor such as a loop reactor can be continuously charged with suitable quantities of solvent or diluent, catalyst, cocatalyst, polymerizable compounds and hydrogen, if any, and in any desirable order. The reactor product can be continuously withdrawn and the polymer recovered as appropriate, generally by flashing the diluent (solvent) and unreacted monomers and drying the resulting polymer. The olefin polymers made with the catalysts of this invention are useful in preparing articles by conventional polyolefin processing techniques such as injection molding, rotational molding, and extrusion of film. The following examples will serve to show the present invention in detail by way of illustration and not by way of limitation. Examples The first example compares the effect of precipitation temperature on the soluble polymer produced during polymerization. It was found that increasing the temperature during precipitation reduces the amount of soluble polymer produced during polymerization. The soluble polymer is the atactic and low molecular weight polymer soluble in the monomer. The second example compares the relative effectiveness of various organoaluminum precipitating agents employed in catalysts prepared at temperatures in accordance with the invention. Good productivity and lower soluble polymer levels were attained with diethylaluminum chloride. The third example demonstrates the improvement attained by employing an inert gas (nitrogen) dispersion during precipitation in accordance with the invention. Catalysts were prepared with a 379 l (100 gallon) reactor, a 37,9 l (10 gallon) reactor, or on a bench scale level in glass bottles, as indicated in each example. The 379 and 37.9 l (100 gallon and 10 gallon) reactor were Pfaudler reactors each equipped with a retreat curve agitator. Each reactor was also equipped with a nitrogen dispersion system on the feedstock inlet. The dispersion system consists of 2 concentric tubes which allowed the feed to enter the reactor through the outer tube while nitrogen entered the reactor through the inner tube. The nitrogen creates a turbulent region at the end of the tube which disperses the feed entering the reactor. A typical batch of the catalyst was prepared with the 379 l (100 gallon) reactor as follows. To the reactor, 136 l (36 gallons) of xylene and 5610 g anhydrous MgCl 2 were added, followed by 1324 ml of water added over a period of about 30 minutes. The resulting mixture was then heated to a temperature in the range of 40°C to 50°C, stirred for about 80 minutes, and allowed to cool to about 30°C. 7560 g 4-phenylphenol were added, followed by the addition of 10 kg (23 pounds) of titanium tetra-n-butoxide. The reactor and its contents were then heated to 90°C to 100°C and stirred for 15 minutes. 2.2 kg (4.8 pounds) of ethylbenzoate were added and the temperature was maintained at 90°C to 100°C for about 45 minutes. Nitrogen dispersion was then begun by passing nitrogen into the reactor through the nitrogen dispersion system at a flow rate of 4.9 liters/minute. The precipitating agent, 28.5 kg (63 lbs) ethylaluminum sesquichloride, was added over a period of 1 hour and 3 minutes at the temperature ("precipitation temperature") designated in the examples. The nitrogen dispersion was turned off and the resulting slurry was stirred for 30 minutes. Then 57 l (15 gallons) of hexane were added to the slurry. The slurry was cooled to about 30°C, the solids were allowed to settle, and the liquid was decanted. The solids were subjected to four washings, each using 170 l (45 gallons) hexane. The wash step involved contacting the solids and the hexane and then decanting the hexane. The solids were then divided and stored 19 l (in 5 gallon)Carboys for later use. The solids were then activated with an activating agent to produce the catalyst. A large batch of activating agent was prepared and used in activating all catalysts described. In a large cylinder, 27 kg (59 lbs) trichlorosilane, 11 kg (24 lbs) silicon tetrachloride, and 49 kg (109 lbs) titanium tetrachloride were combined to produce the activating agent. The solids were activated in a 37.9 l (10 gallon) Pfaudler reactor. The reactor was purged two times with nitrogen. The solids were charged and mixed for 10 minutes. To the solids, 9 kg (20 lbs) of activating agent were added and the reactants were heated to about 100°C for 1 hour at a pressure of 685 to 755 kPa (85-95 psig). The mixture was cooled to 30°C and the liquid decanted. The thus activated solids were washed four times with 19 l (5 gallons) of hexane to produce the catalyst. A typical batch of the catalyst was prepared with the 37.9 l (10 gallon) reactor as follows. To the reactor, 9.5 l (2.5 gallons) of xylene and 561 g anhydrous MgCl 2 were added, followed by addition of 132 ml of water over a period of about 30 minutes. The resulting mixture was then heated to a temperature in the range of 40°C to 50°C, stirred at that temperature for about 80 minutes and allowed to cool to about 30°C. 76 g 4-phenylphenol were then added, followed by the addition of 1 kg (2.5 pounds) of titanium tetra-n-butoxide. The reactor and its contents were then heated to 90°C to 100°C, stirred for about 15 minutes, and then 225 g (0.5 pounds) of ethylbenzoate were added. The resulting mixture was maintained at 90°C to 100°C for about 45-60 minutes. Nitrogen dispersion was begun by passing nitrogen into the reactor through the nitrogen dispersion system at a flow rate of 4.9 liters/minute. The precipitating agent, 2.8 kg (6.3 lbs) ethylaluminum sesquichloride, or the organoaluminum compound indicated, was added through the nitrogen dispersion system over a period of 1 hour and 3 minutes at a temperature of 100°C. The nitrogen dispersion was stopped and the resulting slurry was stirred for 30 minutes. Approximately 7.6 to 19 l (2 to 5 gallons) of hexane were added to the slurry. The slurry was cooled to about 30°C, the solids were allowed to settle and the liquid was decanted. The solids were subjected to four washings, each using 19 l (about 5 gallons) of hexane. To the washed solids, 9 kg (20 lbs) of activating agent described above, were added. The solids and activating agent were heated to 100°C and the pressure was maintained at 685 kPa (85 psig) for 60 minutes. The thus activated solids were cooled to about 30°C and washed 4 times with hexane to produce the catalyst. Bench scale catalysts were produced in glass bottles. Raw materials were transferred to the bottle via syringes or nitrogen pressure through needles. The catalysts were washed by allowing the catalyst to settle and decanting the supernatant liquid through a needle. Heating was accomplished in a controlled temperature oil bath. Thermocouples were inserted through the bottle septum to directly measure the temperature of the contents of the bottle. The solvent charged during precipitations was preheated to the same temperature as the slurry to avoid large changes in the slurry temperature. A typical typical batch of the catalyst was prepared in a glass bottle as follows. To a glass bottle, 153 g xylene and 1.75 g anhydrous MgCl 2 were added, followed by the addition of 0.43 g water over a period of about 30 minutes. The resulting mixture was then heated to a temperature in the range of 40°C to 50°C, stirred at that temperature for about 80 minutes, and allowed to cool to about 30°C. 0.5 g 4-phenylphenol were then added, followed by the addition of 3.28 g titanium tetra-n-butoxide. The bottle and its contents were heated to 90°C to 100°C, and stirred for 15 minutes. 0.53 g ethylbenzoate were added and the temperature was maintained at 90°C to 100°C for 45-60 minutes. The bottle and contents were heated to a temperature of 100°C to 120°C and the precipitating agent, i.e. 9.0 g of the indicated organoaluminum compound was added over a period of 1 hour and 3 minutes. Then 240-260 g diluent (hexane or heptane), heated to a temperature of 100°C to 120°C, were charged to the bottle, and the contents were mixed for 30 minutes at a temperature of 100°C to 120°C. The mixture was cooled to about 30°C. The solids were allowed to settle and the liquid was decanted. The solids were subjected to four washings with hexane. The wash step involved contacting the solids and the hexane and then decanting the hexane. The solids were activated with the above described activating agent. To the solids, approximately 550-700 g activating agent were added. The resulting mixture was heated to approximately 100°C for 1 hour. The thus activated solids were then cooled to about 30°C and washed 4 times with hexane to produce the catalyst. The catalysts were employed in the polymerization of 4-methyl-1-pentene. The polymerizations were carried out in a 3.8 l (one gallon) stirred stainless steel autoclave equipped with automatic temperature control. Monomer was dried over alumina before charging to the reactor. Hydrogen added to the reactor was measured as the pressure drop over a 300 ml vessel. To the clean reactor, purged with nitrogen, at room temperature, approximately 1350 g of liquid 4-methyl-1-pentene (4MP1) was charged to the reactor. The plug on the head of the reactor was removed while the reactor was purging with nitrogen, and 8.4 ml of triethylaluminum cocatalyst (approximately 4.6 mmol/l in toluene) were added, followed by a weighed amount of dried catalyst. The reactor was sealed and the desired amount of hydrogen, approximately 285 kPa (25 psig) pressure drop over a 300 ml vessel, was added. The reactor was stirred for one minute and nitrogen was added to bring the pressure of the reactor to approximately 170 kPa (10 psig). The reaction mixture was then brought to about 50°C and maintained for about 1 hour. The reactor was cooled by venting and using cooling water. The liquid remaining in the reactor was drained from the reactor through a bottom valve into a tared aluminum pan, the monomer was evaporated leaving the soluble polymer i.e. atactic and low molecular weight polymer, and the soluble polymer was weighed. The solid polymer was removed from the reactor, placed in a tared aluminum pan and weighed before and after drying. In the following tables; Precipitation temperature is the temperature at the commencement of the precipitation step in °C. Solubles is the concentration of 4-methyl-1-pentene solubles. This measurement is a function of monomer conversion. Monomer conversion is not the same for every test, and the measurements were adjusted to a monomer conversion level of 10 percent. The adjusted solubles were determined using the following formulas. Dissolved polymer is the weight in g of the solids remaining after drying the liquid fraction recovered from the reactor. Dissolved polymer includes atactic and low molecular weight polymer dissolved in the monomer. Wet polymer is the weight in g of the wet polymer as it is recovered from the reactor. Solid polymer is the dry weight in g of the solid polymer. Monomer conversion conv. = (g dissolved polymer) + (g solid polymer) (g 4MP1 added initially to reactor) Concentration of the soluble polymer in the monomer as weight percent P[w] = (g dissolved polymer)100 [(g 4MP1 initially added to reactor)-(g wet polymer)] Adjusted solubles to 10% as weight percent Adj. solubles = P[w] • 10 conv. Productivity in grams polymer/gram catalyst/hour Productivity = (g dissolved polymer) + (g solid polymer) (g solid catalyst) • (time in hours) Decanted catalyst is expressed in weight percent g dry catalyst(100) g decanted slurry Example I A series of catalysts was prepared to determine the effect of conducting the precipitation step at various temperatures. The catalysts in Runs 101-106 were prepared in a 379 l (100 gallon) Pfaudler reactor as described above using precipitation temperatures indicated in Table I. Each batch of the resulting solids was separated into 19 l (5 gallon) portions which were activated in a 38 l (10 gallon) Pfaudler reactor. Run Precipitation Temperature (°C) Adjusted Solubles (wt. %) Productivity (g/g/hr) Decanted Catalyst (wt. %) 101 30 3.52 10,500 36.8 102 40 2.85 13,000 30.8 103 50 1.88 13,600 27.3 104 50 1.61 13,200 24.1 105 70 1.15 11,200 4.4 106 100 0.77 14,200 2.3 Table 1 demonstrates that soluble polymer production was reduced by using higher temperatures at the commencement of the precipitation step in catalyst preparation, Runs 105-106. It was also shown that the productivity remained at a high level. A difference in catalyst structure was observed when the commencement of the precipitation step during catalyst preparation was carried out at higher temperatures. When the catalyst was precipitated at temperatures at or below 50°C, the catalyst's structure appears crystalline and forms discrete particles. At precipitation temperatures at or above 70°C, the catalyst structure was fibrous and fluffy and discrete particles were not apparent when observed under a microscope. Fluffiness increased with increasing temperature of precipitation, as indicated by the decrease in percent decanted catalyst. The percent decanted catalyst depended on the ratio of the weight of dry catalyst to the weight of the slurry. As the catalyst became more fluffy or fibrous, it filled up a larger volume of diluent, or slurry which therefore decreased the ratio of dry solid catalyst to slurry. Example II A series of catalysts was prepared employing various precipitating agents at the precipitation temperature indicated in Table 2. The soluble polymer production and catalyst productivity were compared. The following aluminum compounds were employed as precipitating agents; ethylaluminum dichloride (EADC), triethylaluminum (TEA) (as comparative test), dimethylaluminum chloride (DMAC), ethylisobutylaluminum chloride (EIBAC), di-n-decylaluminum chloride (DNDAC), ethylaluminum sesquichloride (EASC), diethylaluminum chloride (DEAC), di-n-propylaluminum chloride, (DNPAC), and diisobutylaluminum chloride. Catalysts in runs 209-213 were prepared in a 38 l (10-gallon)Pfaudler reactor as described above. With the following exceptions, the catalysts in runs 201-208 were bench scale preparations carried out in glass bottles as described above. Runs 201, 202 and 208 were prepared using hexane as diluent after precipitation. Runs 203-207 were prepared using heptane as diluent after precipitation and the following reagent quantities in the first catalyst component; 74 g xylene, 0.56 g distilled water, 2.4 g anhydrous MgCl 2 , 0.68 g 4-phenylphenol, and 2.96 g titanium tetra-n-butoxide, combined in the manner described for bench scale catalyst preparation. Run Organoaluminum Precipitation Temperature (°C) Productivtiy (g/g/hr) Adjusted Solubles (wt. %) 201 EADC 110 620 3.0 202 TEA 115 2,700 4.3 203 DMAC 120 3,100 5.1 204 DNDAC 120 8,300 4.1 205 EIBAC 120 9,300 1.9 206 DNPAC 120 13,100 2.0 207 DIBAC 120 8,800 1.4 208 DEAC 100 3,600 1.6 209 EASC 100 11,400 2.0 210 DEAC 100 5,200 1.4 211 DEAC 100 5,800 1.5 212 DEAC 100 18,800 1.4 213 DEAC 100 7,200 1.0 Table 2 demonstrates that catalysts precipitated with ethylaluminum sesquichloride, diethylaluminum chloride, ethylisobutylaluminum chloride, di-n-propylaluminum chloride, and diisobutylaluminum chloride produce a catalyst with relatively high productivity and low soluble polymer production. Table 2 also shows that diethylaluminum chloride produced consistently low levels of soluble polymer, even in the absence of ethyl benzoate. Example III Catalysts were prepared to determine the effect of using a nitrogen dispersion during the precipitation step. Soluble polymer production was compared with and without the nitrogen dispersion. All catalysts were precipitated at 100°C during the entire precipitation step. A nitrogen dispersion was employed in Runs 302 and 303. A nitrogen purge, without the benefit of the inventive dispersion system, was employed in Run 300 by bleeding nitrogen into the headspace of the reactor. No nitrogen was admitted to the reactor in run 301. The catalysts in Run 300, 301, and 302 were prepared in 38 l (10 gallon) reactors as described above. The catalyst in Run 303 was prepared in a 38 l (100 gallon)reactor as described above. When employing the nitrogen dispersion, the nitrogen flow rate was 4.9 liters/minute in both reactors. Run Nitrogen Dispersion Precipitation Temperature (°C) Adjusted Solubles (Wt. %) 300 Purge Only 100 4.9 301 None 100 1.5 302 Yes 100 1.0 303 Yes 100 0.7 Table 3 demonstrates that employing a nitrogen dispersion during the precipitation step of catalyst preparation decreased the level of soluble polymer produced during polymerization.

Claims: A process for preparing a catalyst suitable for the polymerization of 4-methyl-1-pentene comprising: (1) contacting a magnesium dihalide, a titanium tetrahydrocarbyloxide, and a phenol to form a first catalyst component, (2) contacting said first catalyst component and an organoaluminum precipitating agent, said precipitating agent containing a halogen radical and at least one hydrocarbyl radical containing 1 to 20 carbon atoms, to form a slurry containing a solid product, wherein, at least at the commencement of this step (2), the contacting temperature is within the range of 85 °C to 145 °C; and (3) contacting said solid product and an activating agent comprising at least one halogen-containing compound of an element selected from Groups 4, 5, 14, and 15 of the Periodic Table capable of adding halogen to said catalyst, to form said catalyst. The process of claim 1, wherein said temperature of 85 °C to 145 °C is maintained while said first catalyst component and said organoaluminum precipitating agent are contacted for a time of 5 minutes to 10 hours. The process of claim 1 or 2, further comprising maintaining a dispersion of inert gas, preferably nitrogen, during step (2). The process of any of the preceding claims, further comprising the step of contacting the slurry containing the solid with a hydrocarbon, preferably hexane or heptane, before step (3). The process of any of the preceding claims, wherein said activating agent comprises chlorine-containing compounds of silicon and titanium. The process of any of the preceding claims, wherein said activating agent comprises SiHCl 3 and TiCl 4 , optionally in mixture with SiCl 4 . The process of any of the preceding claims, wherein said contacting in step (1) is carried out at a temperature of 0 to 150 °C for a time of 5 minutes to 10 hours, and said contacting in step (3) is carried out at a temperature of 0 to 150 °C for a time of 10 minutes to 10 hours. The process of any of the preceding claims, wherein the molar ratio of said titanium tetrahydrocarbyloxide to said magnesium dihalide is within the range of 0.1:1 to 10:1, the molar ratio of said titanium tetrahydrocarbyloxide to said organoaluminum precipitating agent is within the range of 0.1:1 to 10:1, and the weight ratio of said activating agent to said solid product is within the range of 0.1:1 to 100:1. The process of any of the preceding claims, wherein in step (1) (i) the magnesium dihalide is magnesium dichloride; (ii) the titanium tetrahydrocarbyloxide is titanium tetra-n-butoxide; (iii) the phenol is 4-phenylphenol; (iv) the contacting is carried out at a temperature of 10 to 150 °C for a time of 15 minutes to 3 hours; wherein in step (2) (v) the precipitating agent is diethylaluminum chloride; (vi) the contacting is carried out for a time of 15 minutes to 3 hours, said temperature being maintained for such time from the commencement of the step; wherein in step (3) (vii) the activating agent comprises SiCl 4 , SiHCl 3 , and TiCl 4 ; (viii) the contacting is carried out at a temperature of 20 to 120 °C for a time of 15 minutes to 3 hours; and wherein (ix) the molar ratio of said titanium tetra-n-butoxide to said magnesium dichloride is within the range of 0.2:1 to 2:1; (x) the molar ratio of said titanium tetra-n-butoxide to said diethylaluminum chloride is within the range of 0.1:1 to 3:1; and (xi) the weight ratio of said activating agent to said catalyst is within the range of 0.5:1 to 60:1. Catalyst obtained by the process of any of claims 1 to 9. Use of the catalyst of claim 10, optionally together with a cocatalyst, for the polymerization or copolymerization of 4-methyl-1-pentene. Use of claim 11, wherein said cocatalyst is selected from hydrides and organometallic compounds of metals of Groups 1, 2, 12, and 13 of the Periodic Table, preferably an aluminum trialkyl, and the molar ratio of said cocatalyst to said transition metal compound is within the range of 1500:1 to 1:100.

Inventors: GODBEHERE DON WAYNE, HAWLEY GIL R, MILLER DAVID CHARLES, MITCHELL KENT EDWARD, GODBEHERE, DON WAYNE, HAWLEY, GIL R., MILLER, DAVID CHARLES, MITCHELL, KENT EDWARD
Applicants: PHILLIPS PETROLEUM CO, PHILLIPS PETROLEUM COMPANY
Application year: 1993
Main classification: C08F10
IPC codes: C08F4, C08F10