Process for removing carbon dioxide from combustion gases containing oxygen

Abstract: A process for removing CO₂ from a combustion gas which comprises bringing a combustion gas containing oxygen and CO₂ and a CO₂ absorbent solution into contact at the atmospheric pressure, thereby allowing the CO₂ absorbent solution to absorb CO₂ from the combustion gas, and, in the ensuing step, heating the absorbent solution that has absorbed CO₂ to liberate CO₂ and regenerate the CO₂ absorbent solution, and circulating the regenerated solution for reuse. An aqueous hindered amine solution is used as the CO₂ absorbent solution, and carbon steel is used in building the members of the equipment that contact the aqueous hindered amine solution. The absorbent solution may contain cupric carbonate. The invention is advantageously carried into practice on an industrial scale because of low equipment cost owing to little corrosion and a saving of the energy required for the regeneration of the absorbent solution.

Description: FIELD OF THE INVENTION AND RELATED ART STATEMENT This invention relates to a process for removing carbon dioxide (CO 2 ) from combustion gases. More particularly, it relates to a process for removing CO 2 from combustion gases which contain oxygen and CO 2 at atmospheric pressure, using an aqueous solution of a specific hindered amine solution as a CO 2 absorbent solution and also using a specific material for the equipment that contacts the solution. In recent years the greenhouse effect of CO 2 has attracted attention as a factor responsible for the global warming. Counteracting this effect is urgently needed throughout the world to protect the global environment. The source of CO 2 is omnipresent in the whole areas of human activities that involve the combustion of fossil fuels, and the tendency is toward stricter emission control than heretofore. In view of these, energetic studies are under way on the removal and recovery of CO 2 from combustion gases, especially from those emitted by power-generating installations such as steam power plants that burn enormous quantities of fossil fuels, and on the storage of the recovered CO 2 without release to the atmosphere. For example, methods of contacting combustion gases from boilers with alkanolamine solution etc. have been studied. Examples of the alkanolamine are monoethanolamine, diethanolamine, triethanolamine, methyldiethanolamine, diisopropanolamine, and diglycolamine. Usually, monoethanolamine (MEA) is used by preference. A variety of techniques are known for separating acidic gases from various mixed gases by the use of amine compounds. Japanese Patent Application Disclosure No. SHO 53-100180 (DE-A-2 804 418) describes a process for acid gas removal which comprises bringing a normally gaseous mixture into contact with an amine-solvent liquid absorbent composed of (1) an amine mixture consisting of at least 50 mol% of a sterically hindered amine containing at least either one secondary amino group which forms a part of a ring and is bound to a secondary carbon atom or a tertiary carbon atom or one primary amino group bound to a tertiary carbon atom and at least about 10 mol% of a tertiary amino-alcohol and (2) a solvent for the above amine mixture which is a physical absorbent for acid gases. Examples of the sterically hindered amine cited are 2-piperidine ethanol and the like, those of the tertiary amino-alcohol are 3-dimethylamino-1-propanol and the like, and those of the solvent are sulfoxide compounds which may contain up to 25 wt% of water. As an example of the gas to be treated, the printed publication, page 11, upper left column refers to "a normally gaseous mixture containing high concentrations of carbon dioxide and hydrogen sulfide, e.g., 35% CO 2 and 10-12% H 2 S". Working examples of the invention used CO 2 itself. Patent Application Disclosure No. SHO 61-71819 (DE-A-2 628 376) introduces an acid-gas scrubbing composition containing a sterically hindered amine and a nonaqueous solvent such as sulfolane. As a sterically hindered primary monoamino-alcohol, 2-amino-2-methyl-1-propanol (AMP) and the like are given as examples and employed. Working examples of the invention use CO 2 -nitrogen and CO 2 -helium combinations as gases to be treated. Aqueous solutions of amine and potassium carbonate and the like are used as absorbents. The printed publication mentions the use of water too. It further explains the benefit of the sterically hindered amine by means of a reaction formula. Chemical Engineering Science , vol. 41, No. 4, pp. 997-1003, discloses the behavior of the aqueous solution of AMP as a hindered amine in the absorption of carbonic acid gas. The gases used for the absorption experiment were CO 2 and a CO 2 -nitrogen mixture at the atmospheric pressure. Chemical Engineering Science , vol. 41, No. 2, pp. 405-408, reports the CO 2 and H 2 S absorption rates of aqueous solutions of a hindered amine such as AMP and a straight-chain amine such as MEA at about the ordinary temperature. According to the report, the two aqueous solutions do not differ appreciably in the absorbent concentration range of 0.1-0.3 M when the partial pressure of CO 2 is 1 atm. However, when aqueous solutions at a concentration of 0.1 M was used and the CO 2 partial pressure was reduced from 1 atm. to 0.5 and 0.05 atm., the absorption rate of AMP decreased substantially below that of MEA at 0.05 atm. U.S. Patent No. 3,622,267 teaches a technique of purifying a synthetic gas containing CO 2 at a high partial pressure, e.g., 30% CO 2 at 40 atm., such as the gas synthesized by partial oxidation of crude oil, using an aqueous mixture containing methyl diethanolamine and monoethyl monoethanolamine. German Patent Disclosure No. 1,542,415 reveals a technique of adding monoalkylalkanolamines and the like to physical or chemical absorbents so as to enhance the rates of absorption of CO 2 , H 2 S, and COS. Likewise, German Patent Disclosure No. 1,904,428 teaches the addition of monomethylethanolamine for the improvement of the absorption rate of methyldiethanolamine. U.S. Patent No. 4,336,233 discloses a technique by which an aqueous solution of piperazine at a concentration of 0.81-1.3 mol/ℓ or an aqueous solution of piperazine and a solvent such as methyldiethanolamine, triethanolamine, diethanolamine, or monomethylethanolamine is used as a scrubbing solution for the purification of natural, synthetic, or gasified coal gas. Similarly, Japanese Patent Application Disclosure No. SHO 52-63171 (DE-A-2 551 717) sets forth CO 2 absorbents prepared by adding piperazine or a piperazine derivative such as hydroxyethylpiperazine as an accelerator to a tertiary alkanolamine, monoalkylalkanolamine or the like. The aqueous MEA solution, used in continuous removal of CO 2 by absorption through gas-liquid contact with high-temperature combustion gas that contains oxygen and CO 2 , would cause a corrosion problem. The CO 2 absorption column in which the combustion gas containing CO 2 and oxygen comes in contact with the absorbent solution, the regeneration column that heats the absorbent solution to liberate CO 2 and thereby regenerate the solution, and pipings, heat exchangers, pumps, and all other metallic components located between and around those two columns can be corrosively attacked. Equipment designs using the conventional materials for chemical plants might be implemented in laboratories but would never be feasible for industrial-scale processes because of a too short service life. A proposal has been made in U.S. Patent Specification No. 4,440,731 to overcome the corrosion of the equipment where CO 2 is taken up from combustion gases containing oxygen and CO 2 by the use of a CO 2 absorbent solution which consists of an aqueous solution of MEA or other similar compound. According to the proposal, at least 50 ppm of bivalent copper ion is added to such an absorbent solution, with or without the further addition of dihydroxyethylglycine, a carbonate of an alkali metal, a permanganate of an alkali metal or ammonium, a thiocyanate of an alkali metal carbonate or ammonium, an oxide of nickel or bismuth, or the like. The method is claimed to inhibit the decomposition of the absorbent MEA or the like even during the treatment of combustion gases containing a high concentration of oxygen. Working examples of this U.S. patent actually describe tests with only an aqueous solution of MEA as a sole amine compound. To be more exact, 13.6 kg (30 lbs.) of CO 2 and 6.8 kg (15 lbs.) of oxygen were supplied to an aqueous solution of 30% MEA being refluxed, and corrosion promotion tests were conducted with mild steel coupons in the presence of various corrosion inhibitors at 130°C. It is reported that the addition of 200 ppm cupric carbonate [CuCO 3 ·Cu(OH) 2 ·H 2 O, CuCO 3 accounting for 56% of the total amount] inhibited the corrosion to 23-30 µm/year (0.9-1.2 mil/y (mpy)) whereas the corrosion in the absence of such an inhibitor was 1-1,3 mm/year (40-52 mpy). OBJECT AND SUMMARY OF THE INVENTION In resisting the corrosive attack of an absorbent solution, stainless steel is naturally superior to carbon steel. This apparently favors the use of stainless steel as the equipment material. However, an equipment of stainless steel costs several times more than that of carbon steel. It is for this reason that a CO 2 absorbent having the least possible corrosive action on carbon steel is desired. The afore-described techniques of the prior art for separating acidic gases from various mixed gases by the use of an amine compound teach nothing as to the CO 2 absorption from combustion gases that contain oxygen and CO 2 at the atmospheric pressure by an equipment built of carbon steel members, while preventing the corrosion of the equipment. The method of the above-mentioned U.S. Patent Specification No. 4,440,731 that absorbs CO 2 from combustion gases using one of the specific absorbents while avoiding the corrosion is fairly effective. There is room, nevertheless, for further improvement in corrosion resistance to extend the life span of the equipment. A CO 2 absorbent with the least possible corrosive action on carbon steel is desired, of course, to exhibit high CO 2 absorption performance at a low CO 2 partial pressure such as of combustion gas, i.e., a high CO 2 absorption rate per given amount of an aqueous absorbent solution at a given concentration, a high CO 2 absorption rate per unit absorbent mole of an aqueous absorbent solution at a given concentration, a high CO 2 absorption velocity at a given concentration, and a small energy requirement for the regeneration of the aqueous absorbent solution that has absorbed CO 2 . In view of these problems of the prior art, the present inventors have intensively searched for a CO 2 absorbent which is little corrosive to carbon steel and yet performs CO 2 absorption excellently. It has now been found that, under the conditions for CO 2 absorption from oxygen-containing combustion gases, an aqueous hindered amine solution has an extremely weak corroding action on carbon steel and is superior in absorption performance to the ordinary aqueous MEA solution. This finding has just led to the perfection of the present invention. It has also been found that the addition of the cupric carbonate used in the U.S. Patent No. 4,440,731 to the aqueous hindered amine solution lessens the already limited corroding action of the solution on carbon steel. Thus, the present invention provides a process for removing carbon dioxide from a combustion gas by bringing a combustion gas containing oxygen and carbon dioxide into contact with a carbon dioxide absorption solution at atmospheric pressure, thereby allowing the carbon dioxide absorbent solution to absorb carbon dioxide from the combustion gas, after absorption of the carbon dioxide, heating the absorbent solution that has absorbed carbon dioxide, to liberate carbon dioxide and regenerate the carbon dioxide absorbent solution, and circulating the regenerated solution for reuse, said carbon dioxide absorbent solution being aqueous and containing a hindered amine, which process comprises using members of equipment that contact the absorbent solution built of carbon steel, wherein said hindered amine is an amine compound selected from the classes, excluding the compounds having two or more amino groups, consisting of (A) compounds having in the molecule an alcoholic hydroxyl group and a primary amino group, said primary amino group being bound to a tertiary carbon atom having two unsubstituted alkyl groups, (B) compounds having in the molecule an alcoholic hydroxyl group and a secondary amino group, said secondary amino group having an N atom bound to a group which has a chain of two or more carbon atoms including the binding carbon atom and an unsubstituted alkyl group which contains three or fewer carbon atoms, and (C) compounds having in the molecule an alcoholic hydroxyl group and a tertiary amino group, at least two groups bound to the tertiary amino group each having a chain of two or more carbon atoms including the binding carbon atom, two of the groups bound to the tertiary amino group being unsubstituted alkyl groups. In the present invention it is especially desirable that the carbon dioxide absorbent solution contain cupric carbonate to improve the corrosion resistance of the equipment. The hindered amine to be used in the invention desirably is one containing an alcoholic hydroxyl group in the molecule. Particularly desirable one is chosen from among the amine compounds (excluding those having two or more amino groups) of the classes (A), (B), and (C) above. It is beneficial that such an amine compound has one alcoholic hydroxyl group in the molecule. Out of the hindered amines that can be used for the present invention, (A) the compounds having in the molecule an alcoholic hydroxyl group and a primary amino group, said primary amino group being bound to a tertiary carbon atom having two unsubstituted alkyl groups are such that the unsubstituted alkyl groups may be the same or different. Those groups may be methyl, ethyl, propyl or other group each, preferably the both being methyl groups. The compounds that fall under the category (A) are, e.g., 2-amino-2-methyl-1-propanol, 3-amino-3-methyl-2-pentanol, 2,3-dimethyl-3-amino-1-butanol, 2-amino-2-ethyl-1-butanol, 2-amino-2-methyl-3-pentanol, 2-amino-2-methyl-1-butanol, 3-amino-3-methyl-1-butanol, 3-amino-3-methyl-2-butanol, 2-amino-2,3-dimethyl-3-butanol, 2-amino-2,3-dimethyl-1-butanol, and 2-amino-2-methyl-1-pentanol. Among these, 2-amino-2-methyl-1-propanol (AMP) is preferable. The compounds (B) for use in the invention have in the molecule an alcoholic hydroxyl group and a secondary amino group, said secondary amino group having an N atom bound to a group which has a chain of two or more carbon atoms including the binding carbon atom and an unsubstituted alkyl group which contains 3 or fewer carbon atoms. The chain of two or more carbon atoms including the binding carbon atom is, e.g., a hydroxyl group-substituted alkyl group usually having 2-5 carbon atoms, preferably 2-3 carbon atoms. The compounds belonging to this class (B) are, e.g., 2-(ethylamino)-ethanol, 2-(methylamino)-ethanol, 2-(propylamino)-ethanol, 2-(isopropylamino)-ethanol, 1-(ethylamino)-ethanol, 1-(methylamino)-ethanol, 1-(propylamino)-ethanol, and 1-(isopropylamino)-ethanol. Especially, 2-(ethylamino)-ethanol (EAE) and 2-(methylamino)-ethanol (MAE) are preferred. Of the hindered amines for use in this invention, the compounds (C) have in the molecule an alcoholic hydroxyl group and a tertiary amino group, at least two groups bound to the tertiary amino group each having a chain of two or more carbon atoms including the binding carbon atom, two of the groups bound to the tertiary amino group being unsubstituted alkyl groups. The two unsubstituted alkyl groups may be the same or different, e.g., methyl, ethyl, propyl, isopropyl, or/and other similar groups. Examples of these compounds are 2-(dimethylamino)-ethanol, 2-(diethylamino)-ethanol, 2-(ethylmethylamino)-ethanol, 1-(dimethylamino)-ethanol, 1-(diethylamino)-ethanol, 1-(ethylmethylamino)-ethanol, 2-(diisopropylamino)-ethanol, 1-(diethylamino)-2-propanol, and 3-(diethylamino)-1-propanol. Particularly desirable is 2-(diethylamino)-ethanol (DEAE). The hindered amine or amines chosen from among these classes may be used singly or as a mixture. The concentration of the aqueous hindered amine solution to be used as a CO 2 absorbent solution usually ranges from 25 to 65 wt% depending on the type of the hindered amine or amines used. The present invention is characterized by the use of carbon steel in the equipment members that contact an aqueous hindered amine solution. The carbon steel for use in the invention is a steel with a carbon content of 0.33 wt% or less, preferably 0.20 wt% or less. To a hindered amine according to the invention is preferably added cupric carbonate [CuCO 3 ·Cu(OH) 2 ·H 2 O]. Cupric carbonate, also known as basic copper carbonate, is added in an amount, in terms of bivalent copper ion, of preferably at least 50 ppm or more, more preferably in the range of 100-300 ppm. When necessary, a deterioration-retarding agent (stabilizer) may be added to an aqueous hindered amine solution. In reality, the process of the invention causes such scarce deterioration of the hindered amine that the addition is not considered essential. The temperature of the aqueous hindered amine solution in contact with combustion gas is usually in the range of 30-70°C. The aqueous hindered amine solution that has absorbed CO 2 is heated at the regeneration step. The heating temperature is usually 80-130°C. For the purposes of the invention the term "atmospheric pressure" used here encompasses the pressures in the neighborhood of the atmospheric that permit the operation of a blower or the like to feed a combustion gases to the system. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow diagram of a process into which the present invention can be incorporated; and FIG. 2 is a graph showing the relationship between the absorption rates of absorbent solutions (Nm 3 CO 2 /m 3 absorbent solution as ordinate) and temperature (°C as abscissa). The process to which the present invention for the CO 2 removal from combustion gases can be incorporated is not specially limited. A typical process will now be described with reference to FIG. 1. FIG. 1 shows only major component units, omitting ancillary equipment. Referring to FIG. 1, the numeral 1 indicates a CO 2 -removal column; 2, a lower packed bed; 3, an upper packed bed or trays; 4, a CO 2 -removal column combustion gas inlet; 5, a CO 2 -free combustion gas outlet; 6, an absorbent solution feed inlet; 7, a nozzle; 8, a combustion gas cooler, which is provided when necessary; 9, a nozzle; 10, a packed bed; 11, a humidifying-cooling water circulating pump; 12, a makeup water line; 13, a CO 2 -containing absorbent solution discharging pump; 14, a heat exchanger; 15, an absorbent solution regeneration ("regeneration" for short) column; 16, a nozzle; 17, a lower packed bed; 18, a regenerative heater (reboiler); 19, an upper packed bed; 20, a refluxing water pump; 21, a CO 2 separator; 22, a recovered CO 2 discharge line; 23, a regeneration column reflux condenser; 24, a nozzle; 25, a regeneration column absorbent solution reflux line; 26, a combustion gas feed blower; 27, a cooler; and 28, a regeneration column refluxing water inlet. In FIG. 1, a combustion gas is forced by the combustion gas feed blower 26 into the combustion gas cooler 8. In the cooler the gas is humidified and cooled through contact with humidifying-cooling water from the nozzle 9 and the packed bed 10. It is then led through the CO 2 -removal column combustion gas inlet 4 into the CO 2 -removal column 1. The humidifying-cooling water that has contacted the combustion gas collects at the bottom of the combustion gas cooler 8 and is recycled to the nozzle 9 by the pump 11. Since the humidifying-cooling water is gradually lost by the humidification and cooling of the combustion gas, it is replenished by the makeup feed line 12. When the combustion gas in the humidified and cooled state is to be further cooled, a heat exchanger may be installed between the humidifying-cooling water circulating pump 11 and the nozzle 9 to cool the humidifying-cooling water before it is supplied to the combustion gas cooler 8. The combustion gas forced into the CO 2 -removal column 1 is brought into countercurrent contact in the lower packed bed 2 with the absorbent solution at a given concentration being supplied by the nozzle 7. Thus CO 2 is absorbed away from the combustion gas by the absorbent solution, and the CO 2 -free combustion gas flows upward into the upper packed bed 3. The absorbent solution supplied to the CO 2 -removal column 1 absorbs CO 2 and, because of the heat of reaction due to absorption, it attains a higher temperature than when it is usually is at the feed inlet 6. The CO 2 -containing absorbent solution is sent by the absorbent solution discharging pump 13 to the heat exchanger 14, where it is heated and then transferred to the absorbent solution regeneration column 15. The adjustment of temperature of the regenerated absorbent solution may be done either by the heat exchanger 14 or, according to the necessity, by a cooler 27 provided between the heat exchanger 14 and the absorbent solution feed inlet 6. In the regeneration column 15, the absorbent solution is regenerated in the lower packed bed 17 by the heat from the regenerative heater 18. It is then cooled by the heat exchanger 14 and returned to the CO 2 -removal column 1. In the upper part of the absorbent solution regeneration column 15, the CO 2 separated from the absorbent solution comes in contact with the refluxing water from the nozzle 24 in the upper packed bed 19. Then CO 2 is cooled by the regeneration column reflux condenser 23 and is flown into the CO 2 separator 21, where it is separated from the refluxing water that results from the condensation of water vapor it entrained. By way of the recovered CO 2 discharge line 22 it is conducted to a CO 2 recovery step. Part of the refluxing water is returned to the regeneration column 15 by the refluxing water pump 20. Another part is fed through the regeneration column refluxing water supply line 25 to the regeneration column refluxing water inlet 28 of the CO 2 -removal column 1. This regeneration column refluxing water contains a slight amount of the absorbent solution, which comes in contact with the exhaust gas in the upper packed bed 3 of the CO 2 -removal column 1 and contributes to the removal of a trace amount of CO 2 contained in the gas. The system described above uses carbon steel as the material for the component units that contact the absorbent solution. As has been detailed above, the use of an aqueous hindered amine solution as an absorbent solution in the removal by absorption of CO 2 from combustion gases that contain both oxygen and CO 2 in accordance with the invention reduces the corrosive attack to carbon steel as compared with the attack by an absorbent solution of the prior art prepared by adding cupric carbonate to an aqueous MEA solution. Addition of cupric carbonate to the hindered amine further reduces the corrosion of carbon steel. At the same time, the adoption of a hindered amine as an absorbent solution brings an improvement in CO 2 absorption performance over that of MEA. The present invention makes possible the employment of an apparatus built of carbon steel that is available at lower cost than stainless steel. Moreover, the absorbent solution used requires less energy for regeneration than MEA. These combine to permit the CO 2 absorption from combustion gases to be carried out as an industrial process. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS The present invention is concretely described in connection with the following examples. (Examples 1-8 & Comparative Example 1) Test specimens of carbon steel (SS41) (each having a surface area of about 12 cm 2 (1.87 inch 2 ) and weighing 7.5 g) were polished on a series of three polishing papers Nos. 120, 240, and 400, in the order of mention, in conformity with Japanes Industry Standard JIS R6252 (corresponding to ISO 3366, 3367, 3368 and 3919). They were then washed with acetone, vacuum dried, and weighed. Next, the specimens were transferred into glass testers each filled with 700 mℓ of an aqueous solution containing 30 wt% of a hindered amine saturated with CO 2 beforehand. Each tester was placed in the atmosphere into a two-liter pressure vessel of stainless steel and hermetically sealed. The stainless steel pressure vessel was allowed to stand at 130°C for 48 hours in a high-temperature drier. The specimen was taken out, rinsed, vacuum dried, and weighed. The test was conducted twice for each hindered amine. The results are summarized in Table 1. In the table the expression (contg. cupric carbonate) is used to mean that the absorbent solution contained 200 ppm of cupric carbonate in terms of bivalent copper ion. For comparison purposes similar tests were conducted with an aqueous solution of 30 wt% MEA. The results are also given in Table 1. The corrosion rate µm/year [mpy, standing for mil (1/1000 in.) per year] was calculated from the weight loss due to corrosion and the surface area. Aqueous hindered amine solution Test specimen No. Corrosion rate (mpy) Corrosion rate mm/year Comp.Ex. 1 (MEA) 30 wt% 1 92.95 2.361 aq. sol. 2 76.37 1.940 Ex. 1 AMP 30 wt% 1 4.01 0.102 aq. sol. 2 4.31 0.109 Ex. 2 DEAE 30 wt% 1 2.65 0.0673 aq. sol. 2 2.88 0.0732 Ex. 3 MAE 30 wt% 1 7.04 0.179 aq. sol. 2 6.96 0.177 Ex. 4 EAE 30 wt% 1 3.10 0.0787 aq. sol. 2 3.63 0.0922 Ex. 5 AMP 30 wt% 1 2.80 0.0711 aq. sol. contg. cupric carbonate 2 2.80 0.0711 Ex. 6 MAE 30 wt% 1 3.03 0.0770 aq. sol. contg. cupric carbonate 2 2.35 0.0597 Ex. 7 DEAE 30 wt% 1 1.44 0.0366 aq. sol. contg. cupric carbonate 2 1.89 0.0480 Ex. 8 EAE 30 wt% 1 2.12 0.0538 aq. sol. contg. cupric carbonate 2 2.04 0.0518 (Reference Examples & Reference Comparative Example) Into a glass reactor (flask) placed in a thermostatic chamber was placed 50 mℓ of an aqueous solution containing 30 wt% of a hindered amine. A test gas was passed at a flow rate of 1 ℓ/min at the atmospheric pressure through the aqueous solution while the latter was being stirred at 40°C. The test gas used was a model of combustion gas at 40°C composed of 10 mol% CO 2 , 3 mol% O 2 , and 87 mol% N 2 . The test gas was continuously passed until the CO 2 concentrations at the inlet and outlet became equal. At that point the CO 2 content in the absorbent solution was measured using a CO 2 analyzer (total organic carbon meter) and the CO 2 saturation absorption rate was found. A similar test was repeated at 60°C and 80°C. By way of comparison, similar tests were performed with an aqueous MEA solution. The results are shown in Table 2 (at 40°C) and in FIG. 2. In Table 2, (1) represents Reference Comparative Example and (2)-(5) represent Reference Examples. The vertical axis in FIG. 2 is in the unit of Nm 3 CO 2 /Nm 3 aqueous solution and the horizontal axis is the temperature (°C). From a graph showing the relationship between the CO 2 concentration at the outlet of the flask and the gas passage time, the tangential inclination at the start of gas passage was found, and the initial CO 2 absorption velocity of each absorbent solution was found from its ratio to that of an aqueous MEA solution at the same concentration. The results are also given in Table 2. Test No. Test absorbent sol. (30 wt% aq. sol.) CO 2 saturation absorption rate Initial absorption velocity (aq. MEA sol.=1) CO 2 mol/amine mol Nm 3 CO 2 /Nm 3 abs.sol. (1) MEA 0.56 61.2 1.00 (2) AMP 0.72 54.4 0.69 (3) MAE 0.63 56.0 1.00 (4) EAE 0.68 51.3 0.91 (5) DEAE 0.75 42.2 0.36 As Table 2 indicates, the initial absorption velocities of the aqueous hindered amine solutions (absorbent solutions) used in the present invention (excluding the solution of DEAE) are not so low as expected but are equal to or somewhat lower than that of the MEA solution. There is a possibility of the absorption velocities being improved by the addition of an absorption accelerator. On the other hand, all the CO 2 absorption rates per unit mole of the individual hindered amines are greater than that of MEA. The absorption rates per unit amount of the absorbent solutions vary with the type of the hindered amines used, the rates of the MAE and AMP solutions being somewhat lower than that of the MEA solution. FIG. 2 shows that when a hindered amine such as AMP is used, the decrease in the CO 2 absorption rate with the increase in temperature of the absorbent solution is greater than when MEA is used. This suggests the possibility of saving more thermal energy for the regeneration of the absorbent solution than with MEA.

Claims: A process for removing carbon dioxide from a combustion gas by bringing a combustion gas containing oxygen and carbon dioxide into contact with a carbon dioxide absorption solution at atmospheric pressure, thereby allowing the carbon dioxide absorbent solution to absorb carbon dioxide from the combustion gas, after absorption of the carbon dioxide, heating the absorbent solution that has absorbed carbon dioxide to liberate carbon dioxide and regenerate the carbon dioxide absorbent solution, and circulating the regenerated solution for reuse, said carbon dioxide absorbent solution being aqueous and containing a hindered amine, which process comprises using members of equipment that contact the absorbent solution built of carbon steel, wherein said hindered amine is an amine compound selected from the classes, excluding the compounds having two or more amino groups, consisting of (A) compounds having in the molecule an alcoholic hydroxyl group and a primary amino group, said primary amino group being bound to a tertiary carbon atom having two unsubstituted alkyl groups, (B) compounds having in the molecule an alcoholic hydroxyl group and a secondary amino group, said secondary amino group having an N atom bound to a group which has a chain of two or more carbon atoms including the binding carbon atom and an unsubstituted alkyl group which contains three or fewer carbon atoms, and (C) compounds having in the molecule an alcoholic hydroxyl group and a tertiary amino group, at least two groups bound to the tertiary amino group each having a chain of two or more carbon atoms including the binding carbon atom, two of the groups bound to the tertiary amino group being unsubstituted alkyl groups. The process as claimed in claim 1, wherein further comprising adding cupric carbonate to said carbon dioxide absorbent solution.

Inventors: IIJIMA MASAKI, KARASAKI MUTSUNORI, MIMURA TOMIO, MITSUOKA SHIGEAKI, SHIMOJO SHIGERU, YOSHIDA KUNIHIKO, IIJIMA, MASAKI, KARASAKI, MUTSUNORI, MIMURA, TOMIO, MITSUOKA, SHIGEAKI, SHIMOJO, SHIGERU, YOSHIDA, KUNIHIKO, IIJIMA, MASAKI, MITSUBISHI JUKOGYO K.K., KARASAKI, MUTSUNORI, MITSUBISHI JUKOGYO K.K., Mimura, Tomio, c/o Kansai Elec. Power Co., Inc., Mitsuoka, Shigeaki, c/o Hiroshima Mitsubhishi, Shimojo, Shigeru, c/o Kanasai Elec. Power Co.,Ltd, Yoshida, Kunihiko, c/o Kansai Elec. Power Co.,Inc.
Applicants: KANSAI ELECTRIC POWER CO, MITSUBISHI HEAVY IND LTD, MITSUBISHI JUKOGYO KABUSHIKI KAISHA, THE KANSAI ELECTRIC POWER CO., INC.
Application year: 1993
Main classification: B01D53
IPC codes: B01D53